# Synthesis and Characterization of Carbon Nanofibers Grown on Powdered Activated Carbon

Authors: Yehya M. Ahmed; Abdullah Al-Mamun; Ahmad T. Jameel; Ma’an Fahmi R. AlKhatib; Mutiu K. Amosa; Mohammed A. AlSaadi
Journal: Journal of Nanotechnology
 (2016)

---

## Abstract

Carbon nanofibers (CNFs) were synthesized through nickel ion (Ni2+) impregnation of powdered activated carbon (PAC). Chemical Vapor Deposition (CVD) using acetylene gas, in the presence of hydrogen gas, was employed for the synthesis process. Various percentages (1, 3, 5, and 7 wt. %) of Ni2+ catalysts were used in the impregnation of Ni2+ into PAC. Field Emission Scanning Electron Microscope (FESEM), Fourier Transform Infrared (FTIR) Spectroscopy, Energy Dispersive X-Ray Analyzer (EDX), Transmission Electron Microscopy (TEM), Thermal Gravimetric Analysis (TGA), zeta potential, and Brunauer, Emmett, and Teller (BET) were utilized for the characterization of the novel composite, which possessed micro and nanodimensions. FESEM and TEM images revealed that the carbonaceous structure of the nanomaterials was fibrous instead of tubular with average width varying from 100 to 200 nanometers. The PAC surface area increased from 101 m2/g to 837 m2/g after the growth of CNF. TGA combustion temperature range was within 400°C and 570°C, while the average zeta potential of the nanocomposite materials was −24.9 mV, indicating its moderate dispersive nature in water.


---

## Body

## 1. Introduction

Activated carbon (AC) is an adsorbent used on an enormous scale in gaseous and aqueous purifications, metal extraction, and medicine, amongst other applications [1]. Several studies reported that AC is efficient in the sorption of various types of bioresistant pollutants from the environment [2]. Besides the use of AC for isolation of metals from aquatic environment by adsorption process which is a well-established process [3–5], activated carbons are also employed as catalyst supports for various applications [6, 7].Carbon nanofibers (CNFs) are hydrophobic, generally, without significant functional groups [8], and the CNFs have recently received added attention due to their potential usages in various research and industrial sectors. For instance, chemical industry, material science, and environmental and energy storage specialties [9]. Preparation of polymer composites carried out through the dispersion of CNF into the polymer matrices is also reported [10], while CNF utility in the adsorption of volatile organic compounds (VOC) such as alkanes, aromatics and chloro-hydrocarbons was established in the reports of previous investigations [11]. Factually, CNFs are potential materials for various engineering applications due to their unique chemical, physical, mechanical, and electrical properties [12, 13]. The diameter of a carbon nanofiber ranges between 50 nm and 200 nm and that of the carbon nanotubes is usually less than 100 nm. Studies on the variation in diameter of fibrous graphitic materials are reported by Shaffer and Sandler [14].Several methods have been used in the synthesis of CNF, such as the utility of various catalysts and carbon sources [15–20]. In laser ablation, a graphite target source with little amount of catalysts (usually a transition metal) is exposed to a laser beam which vaporizes the graphite and initiate the growth of CNF just in front of the target [16]. It is pertinent to note that in the CVD method, which is the most common method for bulk production of carbon nanomaterials, different hydrocarbons (carbon sources) are deposited on various metal catalysts (Fe, Co, and Ni) at temperatures between 500 and 1200°C [21].The process parameters that are important for the synthesis of CNF are the ratio of hydrogen to carbon source flow, reaction time, and temperature. The effect of hydrogen gas can be acceleration and suppression. Effect of acceleration on the formation of carbon may be interpreted in two ways. The first theory suggests decomposition of inactive metal carbides by hydrogen to form active metal [22]. The other explanation proposes that hydrogen removes surface carbon and precursors of carbon which leads to active site blocking [5]. The effect of suppressing has also been suggested to occur due to the surface hydrogenation reactions. The effect of hydrogen on the formation of CNF from the decomposition of metal catalyzed by hydrocarbon molecules is thought to convert inactive metal carbides into catalytically active metallic state which prohibits the formation of graphite layers on the surface of the metal particles. Moreover, the diffusion and precipitation rates of carbon atoms are affected by temperature and availability of carbon atoms [23]. The precipitation of carbon on the metal catalysts can be categorized into surface and internal. It is reported that, at low temperatures, carbon atoms can only precipitate on the surface areas of the catalyst particles, while the diffusing and dissolution rates of carbon atoms increase with the temperature, and carbon atoms can get into the internal areas of the catalysts to form CNF [24].The growth time amongst other factors plays a major role in tailoring the morphology of nanomaterials in terms of diameter, dense of growth, and so forth. [25, 26]. Two growth stages are reported in the literature. In the initial stage, a part of the nickel surface is covered by carbon leading to formation of relatively catalyst-rich carbon area. In the next stage dissolved carbon is released to form CNF with the lift-off of the former catalyst-rich carbon particles out of the substrate surface. Lastly, the decomposition of hydrocarbon on the new catalyst initiates new deposition of carbons from the same particle covering the host surface completely by a dense layer of CNF. The role of reaction time was previously studied on the growth of CNF from the decomposition of ethylene over Ni/Y-zeolite [27]. The reaction duration was 60 min while a total time of 3 hr was needed for the synthesis of CNF in the decomposition of ethylene over an unsupported Ni-Cu alloy [28].The main objective of this study was to use oil palm kernel shell based PACs as a solid substrate for the growth of CNF on nickel impregnated PACs by CVD method. Determination of various physicochemical properties of the new nanomicrocomposite carbon material was done as well.


## 2. Experimental

The following materials and equipment were used for the synthesis and characterization processes.


### 2.1. Materials and Reagents

Palm kernel shell based granular activated carbon (GAC) was obtained from Effigen Carbon Sdn. Bhd., Malaysia. The GAC was bought in 20 kg bags and grinded to powdered activated carbon (PAC) of sizes ranging from 100 to 250μm. Nickel (II) nitrate hexahydrate, 99%, was purchased from Acros organics, USA, for the preparation of the nickel catalyst, which was impregnated into the PAC. Acetone QP was obtained from HmbG Chemicals, Germany, for the purpose of dissolving the nickel salt in readiness for the impregnation process. Purified nitrogen gas was purchased from Fuelink Marketing Sdn. Bhd., Selangor, Malaysia, which served as carrier gas for the calcination of the nickel catalyst growth of the CNF on PAC. Purified hydrogen gas was purchased from Malaysian Oxygen Bhd. and utilized for reduction of nickel catalyst. Purified acetylene gas from MOX-Linde Gases Sdn. Bhd. was used as a carbon source for the growth of CNF on PAC surface.


### 2.2. Equipment and Instrumentation

Philips grinder was used to crush the raw granular activated carbon to form PACs. Retsch sieve shakers model AS200 of German product, digit, and Max amplitude of 100 was used to sieve the grinded activated carbon to desired fraction size. A&D four digits weighing balance (HR-202i, Japan) was used for all the weighing measurements. The weighing range of the balance is from 0.001 to 220 g. Ultrasonic bath model (JAC 2010 P) from South Korea was used for the mixing of PAC and nickel solution to impregnate the metal onto the substrate. The bath is equipped with heater (max. 70°C), timer for 99 seconds, and three sonication levels. Lenton, England triple stage horizontal tubular ceramic reactor (diameter, 50 mm; length, 1500 mm), was used for the CVD process for the growth of CNF. The maximum heating temperature for the furnace is 1200°C. At the heating area, the ceramic tube utilized a resistance heating glass wool from Isolite Ceramic Fiber Sdn. Bhd. Malaysia. A drying oven model 600 from Memmert, Germany, of maximum temperature 220°C was used to dehumidify the samples of PAC and CNF-PAC.FESEM model 6700F from JEOL Company (Japan) was used to determine the morphological features of the CNF. Energy Dispersive X-ray Analyzer was attached to the FESEM for the determination of structure of the PAC and CNF. High-resolution TEM model JEM-2010 from JEOL Company (Japan) was used to determine the diameter and length of the CNF. Automated Gas Sorption System (Quantachrome Autosorb) from Quantachrome Company (USA) was used to calculate the surface area of the powdered activated carbon before and after the CNF growth. FTIR model 100 from Perkin Elmer (USA) was used for the classification of the functional groups on the PAC, impregnated PAC, and CNF. Perkin Elmer Instruments Pyris diamond TG/DTA (USA) was used to study the thermogravimetric behavior of PAC and CNF-PAC.


### 2.3. Powdered Activated Carbon Samples Preparation

Palm kernel shell based granular activated carbon (GAC) was grinded and sieved. Powdered activated carbon (PAC) with particle size between 100 and 250μm was collected and kept in sealed plastic bags for production and adsorption studies.


### 2.4. Catalyst Preparation

The incipient wetness impregnation was used to impregnate nickel nitrate salt onto PAC by dissolving the nickel salt in acetone adopting method described elsewhere [25]. Four different weight percent (w/w%) samples of nickel catalyst were prepared and the ratios were calculated based on the Ni to PAC in the sample. Using the ratios, 1, 3, 5, and 7%, preparations were made by mixing the required amount of nickel nitrate hexahydrate Ni (NO3)2·6H2O with small amount of acetone (in universal glass bottle) until all the nickel salt was totally dissolved and homogenously mixed.


### 2.5. PAC Impregnation

The catalyst was mixed with specified amount of PAC. The mixture was then sonicated in the ultrasonic bath for 30 min at room temperature and with high sonication speed. The nickel impregnated PAC was left in the water bath at temperature of 56°C and sonicated for 12 h to ensure complete impregnation process and evaporation of any excess acetone.


### 2.6. CNF Growth

Catalyst substrate was fixed in a ceramic alumina boat in the tubular ceramic reactor (Figure1). Calcination was carried out at 350°C with nitrogen gas flow rate of 200 mL/min for 2 h into the CVD reactor under atmospheric pressure. The solid was then reduced by hydrogen gas at 400°C and 120 mL/min flow rate for 2 hr. The reduced catalysts were, then, cooled down to ambient temperature and weighed to determine the amount of moisture present. The synthesis of CNF was carried out on the reduced catalysts by the CVD reactor at atmospheric pressure and in the presence of a C6H6/H2 mixture (total flow rate, 20 and 100 mL/min) at 650°C [25]. The raw CNF was cooled down to ambient temperature followed by measurement of the product weight. The processes of calcination, reduction, and growth processes of CNF were done for the four different weight percent samples of the catalyst. The best samples in terms of the percentage yield were chosen for further studies. The yield was calculated from the difference between the weight of the sample after calcination and reduction were done (before CNF growth) and its weight after the growth of CNF completed.Figure 1
Schematic diagram of multipurpose triple stage CVD system.


## 2.1. Materials and Reagents

Palm kernel shell based granular activated carbon (GAC) was obtained from Effigen Carbon Sdn. Bhd., Malaysia. The GAC was bought in 20 kg bags and grinded to powdered activated carbon (PAC) of sizes ranging from 100 to 250μm. Nickel (II) nitrate hexahydrate, 99%, was purchased from Acros organics, USA, for the preparation of the nickel catalyst, which was impregnated into the PAC. Acetone QP was obtained from HmbG Chemicals, Germany, for the purpose of dissolving the nickel salt in readiness for the impregnation process. Purified nitrogen gas was purchased from Fuelink Marketing Sdn. Bhd., Selangor, Malaysia, which served as carrier gas for the calcination of the nickel catalyst growth of the CNF on PAC. Purified hydrogen gas was purchased from Malaysian Oxygen Bhd. and utilized for reduction of nickel catalyst. Purified acetylene gas from MOX-Linde Gases Sdn. Bhd. was used as a carbon source for the growth of CNF on PAC surface.


## 2.2. Equipment and Instrumentation

Philips grinder was used to crush the raw granular activated carbon to form PACs. Retsch sieve shakers model AS200 of German product, digit, and Max amplitude of 100 was used to sieve the grinded activated carbon to desired fraction size. A&D four digits weighing balance (HR-202i, Japan) was used for all the weighing measurements. The weighing range of the balance is from 0.001 to 220 g. Ultrasonic bath model (JAC 2010 P) from South Korea was used for the mixing of PAC and nickel solution to impregnate the metal onto the substrate. The bath is equipped with heater (max. 70°C), timer for 99 seconds, and three sonication levels. Lenton, England triple stage horizontal tubular ceramic reactor (diameter, 50 mm; length, 1500 mm), was used for the CVD process for the growth of CNF. The maximum heating temperature for the furnace is 1200°C. At the heating area, the ceramic tube utilized a resistance heating glass wool from Isolite Ceramic Fiber Sdn. Bhd. Malaysia. A drying oven model 600 from Memmert, Germany, of maximum temperature 220°C was used to dehumidify the samples of PAC and CNF-PAC.FESEM model 6700F from JEOL Company (Japan) was used to determine the morphological features of the CNF. Energy Dispersive X-ray Analyzer was attached to the FESEM for the determination of structure of the PAC and CNF. High-resolution TEM model JEM-2010 from JEOL Company (Japan) was used to determine the diameter and length of the CNF. Automated Gas Sorption System (Quantachrome Autosorb) from Quantachrome Company (USA) was used to calculate the surface area of the powdered activated carbon before and after the CNF growth. FTIR model 100 from Perkin Elmer (USA) was used for the classification of the functional groups on the PAC, impregnated PAC, and CNF. Perkin Elmer Instruments Pyris diamond TG/DTA (USA) was used to study the thermogravimetric behavior of PAC and CNF-PAC.


## 2.3. Powdered Activated Carbon Samples Preparation

Palm kernel shell based granular activated carbon (GAC) was grinded and sieved. Powdered activated carbon (PAC) with particle size between 100 and 250μm was collected and kept in sealed plastic bags for production and adsorption studies.


## 2.4. Catalyst Preparation

The incipient wetness impregnation was used to impregnate nickel nitrate salt onto PAC by dissolving the nickel salt in acetone adopting method described elsewhere [25]. Four different weight percent (w/w%) samples of nickel catalyst were prepared and the ratios were calculated based on the Ni to PAC in the sample. Using the ratios, 1, 3, 5, and 7%, preparations were made by mixing the required amount of nickel nitrate hexahydrate Ni (NO3)2·6H2O with small amount of acetone (in universal glass bottle) until all the nickel salt was totally dissolved and homogenously mixed.


## 2.5. PAC Impregnation

The catalyst was mixed with specified amount of PAC. The mixture was then sonicated in the ultrasonic bath for 30 min at room temperature and with high sonication speed. The nickel impregnated PAC was left in the water bath at temperature of 56°C and sonicated for 12 h to ensure complete impregnation process and evaporation of any excess acetone.


## 2.6. CNF Growth

Catalyst substrate was fixed in a ceramic alumina boat in the tubular ceramic reactor (Figure1). Calcination was carried out at 350°C with nitrogen gas flow rate of 200 mL/min for 2 h into the CVD reactor under atmospheric pressure. The solid was then reduced by hydrogen gas at 400°C and 120 mL/min flow rate for 2 hr. The reduced catalysts were, then, cooled down to ambient temperature and weighed to determine the amount of moisture present. The synthesis of CNF was carried out on the reduced catalysts by the CVD reactor at atmospheric pressure and in the presence of a C6H6/H2 mixture (total flow rate, 20 and 100 mL/min) at 650°C [25]. The raw CNF was cooled down to ambient temperature followed by measurement of the product weight. The processes of calcination, reduction, and growth processes of CNF were done for the four different weight percent samples of the catalyst. The best samples in terms of the percentage yield were chosen for further studies. The yield was calculated from the difference between the weight of the sample after calcination and reduction were done (before CNF growth) and its weight after the growth of CNF completed.Figure 1
Schematic diagram of multipurpose triple stage CVD system.


## 3. Results and Discussion

### 3.1. Effect of Ni Catalyst on CNF Yield

After the impregnation, calcination, and reduction of the catalyst and the growth of the CNF, the product was weighed and the yield, %, of the grown CNF was determined by using the formula (1), where w
0 and w
1 were the initial and final weights of the impregnated substrate (PACs). The results are shown in Table 1.(1)
%
Yield
=
w
1
-
w
0
w
0
×
100
.Table 1
Yield percentage of the CNF growth on impregnated PAC.
Catalyst percentage (%)
Weight (g) of sample before CNF growth (w
0)
Weight (g) of sample after CNF growth (w
1)
Yield (%)
1
1.2
1.56
30
3
1.2
2.16
68
5
1.3
2.02
55
7
1.3
1.86
43The yield calculations (%) showed that the highest yield of CNF was achieved from the 3% catalyst and the process condition was used for further production of PAC-CNF samples. A percentage weight catalyst higher than 3% gave less percentage yield, and this is attributable to the agglomeration of Ni, while 1% gave lesser yield when compared with that of 3%. This effect may be attributed to the lesser amount of nickel exposed to the carbon as concluded in previously reported similar investigation [27]. The distribution of the CNF growth on the impregnated PAC is shown in the FESEM images for the various catalyst percentage ratios are shown in Figure 2. The poor growth shown in Figure 2(a) was due to the low weight percentage of nickel catalyst used for the impregnation [29].Figure 2
Field Emission Scanning Electron Microscope image of the CNF for (a) 1% catalyst, (b) 3% catalyst, (c) 5% catalyst, and (d) 7% catalyst.
(a)
(b)
(c)
(d)The FESEM images showed that the catalyst of 3 wt.% gave the best growth of CNF and it matches with the yield calculations showed in Table1. Increase in the catalyst percent weight increased the chance of the growth as reported in earlier investigations [30], while further increase in the catalyst percentage led to the agglomeration of nickel particles and subsequently a decrease in the growth of CNF as depicted in Figure 2. This observation is in conformity with previous reports [31, 32].


### 3.2. FESEM Results

Field Emission Scanning Electron Microscopy (FESEM) technique was used for the analysis of physical morphology of the surface of the prepared samples. Figures3(a), 3(b), and 3(c) showed the images of the raw material (PAC), impregnated PAC, and the prepared PAC-CNF samples with 2000x magnification, respectively. Figure 3(c) showed the whole surface of the substrate covered with the grown CNF, and compared with the images in Figures 3(a) and 3(b), the coverage with the grown CNF led to increase in the original substrate’s adsorption properties. Figure 3(d), which represented the higher magnification of Figure 3(c), showed the diameters of the CNF ranging from the average of 100 to 160 nm with the presence of many white confirmed to be Ni particles by the EDX analysis.Figure 3
Scanning Electron Microscope images: (a) raw PAC, (b) Ni impregnated PAC, and (c) (d) CNF grown on PAC at optimized conditions.
(a)
(b)
(c)
(d)


### 3.3. TEM Results

The Transmission Electron Microscopy (TEM) analysis proved the formation of the as-prepared CNF. Figures4(a) and 4(b) show that the fiber has an average diameter range between 100 and 200 nm as matched with images of FESEM above. Closely related observations were made in the previous TEM studies for the confirmation of CNF dimensions [33–35]. The images also revealed the firmness of the amorphous carbon structure. The high quality image (Figure 5) showed the layers by layers CNF structure as indicated by the white arrows. The image showed that the CNF microstructures possessed defective platelets and more graphitic platelets that was similar to previous reports [36–38].Figure 4
Transmission Electron Microscopy images CNF.
(a)
(b)Figure 5
Transmission Electron Microscopy images of layered structure of CNF.


### 3.4. Surface Area of the PAC-CNF

Using computer-monitoring system, the adsorbed nitrogen gas volume, equilibrium pressures, and BET surface area of the sample were determined. The specific BET surface area of the PAC was found to be 101.1 m2/g. After sonication, the Ni2+ impregnated PAC surface area increased to 131.2 m2/g due to production of additional fine particles during the sonication process. On the other hand, the CNF grown on PAC exhibited 836.7 m2/g, which was more than eight times surface area compared to that of PAC.Plot of volume of nitrogen gas adsorbed on raw PAC and PAC-CNF versusP/P
0 are shown in Figures 6 and 7, respectively. The plot yields a line of slope [(c
-
l)/c
V
m] and intercept [l/c
V
m], where V is the amount of the adsorbate. The values of c, R
2, and V
m (monolayer capacity) were determined from the plots and the results are given in Table 2. As shown in Table 2, the new product, PAC-CNF, exhibited a higher monolayer capacity (V
m) and total pore volume compared with the PAC, and this is in conformity with earlier reports [39, 40]. These results are due to the increase in the surface area after the growth of the CNF on the PAC surface.Table 2
BET isotherm parameters for nitrogen gas adsorption by PAC and PAC-CNF.
Compound
Parameter
Total pore volume (cc/g)
V
m
R
2
PAC
8.8
×
10
-
2
0.029
0.9999
Impregnated PAC
3.26
×
10
-
1
0.029
0.9996
PAC-CNF
6.75
×
10
-
1
0.24
0.9985Figure 6
Adsorption/desorption of nitrogen gas on PAC.Figure 7
Adsorption/desorption of nitrogen gas on PAC-CNF.


### 3.5. Zeta Potential

The zeta potential of the materials was measured for PAC and PAC-CNF in water. Test results showed that the zeta potential for the samples was negative and the peaks shifted towards zero point from PAC value (−30.9) to the PAC-CNF value (−24.9). The negative sign for the zeta potentials was indicative of the hydrophilicity of the composite. The high negative charge is an indication that the adsorbent is more hydrophilic [41]. The values of the zeta potential for the PAC after the growth of the CNF were still in the range of “incipient instability,” a description similar to what was previously reported [42].


### 3.6. Surface Chemistry

The spectrum for the PAC, impregnated PAC, and CNF samples displayed bands with their respective functional groups as shown in Figure8. The intensity of the band in the 3859–2519 cm−1 region contains –OH groups. The width and asymmetry of this band indicated the existence of strong hydrogen bonds, which could be due to adsorbed water on the PAC surfaces. The bands at 1965 and 1746 and 2250–2400 cm−1 were indicative of the presence of carbonyl groups [43, 44]. Those bands at 996 cm−1 contain saturated carbon (methyl group –CH3) which might be from the cracking of acetylene [45].Figure 8
FTIR diagram of PAC, impregnated PAC, and PAC-CNF.The presence of these bands shows the formation of new carbon groups on the surface of PAC which is due to CNF [46]. Absorption peaks at 766 and 702 cm−1 represent NO2 bending vibrations [47]. These results were in agreement with the surface chemistry of other agricultural by-products [45, 48, 49]. Table 3 explains the peaks and functional groups represented by the bands.Table 3
Functional groups detected by FTIR on PAC, impregnated PAC, and PAC-CNF.
Wave number at peak (cm−1)
Functional group
Type of vibration
3859–2519
–OH (un-bonded), –OH (bonded)
No interferences such as OH in lattice, –OH stretch
2400–2250 & 1965, 1746
Aldehyde, ketone, carboxylic acid
C=O, carbonyl group
2343
CO2
1573
C=C aromatic ring
C=C stretch
996
Methyl group
Saturated –CH3
766 & 702
NO2
Bending
739
Hydrogen on an aromatic ring
Adjacent hydrogens on an aromatic ring (Ortho)


### 3.7. Energy Dispersive X-Ray (EDX) Analysis

The EDX imaging analysis revealed the materials’ surface structure and the local elements distribution of PAC, impregnated PAC, and PAC-CNF were examined using the EDX analyzer as depicted in Figure9 [50]. Figures 9(a), 9(b), and 9(c) showed the electron images for the samples; this invariably showed the difference in the surface structure between the four compounds. These observations conformed to the spectrum images shown in Figure 9.Figure 9
EDX spectrums for (a) PAC, (b) Ni impregnated PAC, and (c) PAC-CNF.
(a)
(b)
(c)It was observed in Figure9 that carbon element was present in high percentage in the four mentioned samples followed by oxygen and other elements as impurities (Na, Si, Cl, K, and Ca) with low percentages. The existence of nickel element on the surface of the PAC after impregnation of the element was also established, and this proved the success of the impregnation process. The elements detected by the EDX analyzer with their respective average weight and atomic percentages are presented in Table 4. The table showed that the percentage of the atomic carbon increased from 87% to 94% after the CNF growth on the surface of the substrate which enhances the decomposition of the acetylene to atomic carbon, similar to what was reported previously [51]. The presence of nickel on the surface of PAC was about 6.2%.Table 4
Compositions of elements in PAC, Ni impregnated PAC, and PAC-CNF.
Element
Average weight(%)
Average atomic composition (%)
PAC
Ni-PAC
PAC-CNF
PAC
Ni-PAC
PAC-CNF
C
89.98
78.85
87.37
92.10
86.69
94.05
O
4.88
13.96
3.95
7.20
11.52
6.66
Na
0.18
—
—
0.10
—
—
Si
0.71
0.37
0.69
0.32
0.18
0.32
Cl
0.32
—
—
0.40
—
—
K
0.33
0.36
0.55
0.11
0.12
0.18
Ca
0.43
0.26
0.31
0.13
0.08
0.22
Ni
—
6.16
5.84
—
1.39
1.29


### 3.8. Thermogravimetric Analysis (TGA)

Thermogravimetric analysis (TGA) revealed the temperature effect on the PAC and CNF. The TGA profiles obtained under the inert gas condition are presented in Figure10. The first weight loss occurring around 100°C of temperature was observed for the samples which was caused by thermodesorption of physically adsorbed material such as water vapor (moisture) and hydrocarbons [52] and it showed that the moisture content was around 15–18% for PAC and CNF, respectively.Figure 10
Thermal stability of PAC and PAC-CNF.High temperatures (between 400 and 480°C) for CNF and PAC, respectively, led to the start of combustion. Decrease in weight is commonly considered to be due to the vaporization of volatile organic compounds [53], which was indicated by a significant weight loss of 70% w/w. It was also observed that the weight loss stopped after a higher limit of combustion temperature (570 and 780°C for CNF and PAC, resp.) was reached. Some residual material remained for all samples, and these residues indicated the carbon purity of the samples with PAC having 5% representing the ash content and PAC-CNF exhibiting 8%, which was due to the Ni2+ catalyst impregnated on PAC surface prior to the CNF growth.


## 3.1. Effect of Ni Catalyst on CNF Yield

After the impregnation, calcination, and reduction of the catalyst and the growth of the CNF, the product was weighed and the yield, %, of the grown CNF was determined by using the formula (1), where w
0 and w
1 were the initial and final weights of the impregnated substrate (PACs). The results are shown in Table 1.(1)
%
Yield
=
w
1
-
w
0
w
0
×
100
.Table 1
Yield percentage of the CNF growth on impregnated PAC.
Catalyst percentage (%)
Weight (g) of sample before CNF growth (w
0)
Weight (g) of sample after CNF growth (w
1)
Yield (%)
1
1.2
1.56
30
3
1.2
2.16
68
5
1.3
2.02
55
7
1.3
1.86
43The yield calculations (%) showed that the highest yield of CNF was achieved from the 3% catalyst and the process condition was used for further production of PAC-CNF samples. A percentage weight catalyst higher than 3% gave less percentage yield, and this is attributable to the agglomeration of Ni, while 1% gave lesser yield when compared with that of 3%. This effect may be attributed to the lesser amount of nickel exposed to the carbon as concluded in previously reported similar investigation [27]. The distribution of the CNF growth on the impregnated PAC is shown in the FESEM images for the various catalyst percentage ratios are shown in Figure 2. The poor growth shown in Figure 2(a) was due to the low weight percentage of nickel catalyst used for the impregnation [29].Figure 2
Field Emission Scanning Electron Microscope image of the CNF for (a) 1% catalyst, (b) 3% catalyst, (c) 5% catalyst, and (d) 7% catalyst.
(a)
(b)
(c)
(d)The FESEM images showed that the catalyst of 3 wt.% gave the best growth of CNF and it matches with the yield calculations showed in Table1. Increase in the catalyst percent weight increased the chance of the growth as reported in earlier investigations [30], while further increase in the catalyst percentage led to the agglomeration of nickel particles and subsequently a decrease in the growth of CNF as depicted in Figure 2. This observation is in conformity with previous reports [31, 32].


## 3.2. FESEM Results

Field Emission Scanning Electron Microscopy (FESEM) technique was used for the analysis of physical morphology of the surface of the prepared samples. Figures3(a), 3(b), and 3(c) showed the images of the raw material (PAC), impregnated PAC, and the prepared PAC-CNF samples with 2000x magnification, respectively. Figure 3(c) showed the whole surface of the substrate covered with the grown CNF, and compared with the images in Figures 3(a) and 3(b), the coverage with the grown CNF led to increase in the original substrate’s adsorption properties. Figure 3(d), which represented the higher magnification of Figure 3(c), showed the diameters of the CNF ranging from the average of 100 to 160 nm with the presence of many white confirmed to be Ni particles by the EDX analysis.Figure 3
Scanning Electron Microscope images: (a) raw PAC, (b) Ni impregnated PAC, and (c) (d) CNF grown on PAC at optimized conditions.
(a)
(b)
(c)
(d)


## 3.3. TEM Results

The Transmission Electron Microscopy (TEM) analysis proved the formation of the as-prepared CNF. Figures4(a) and 4(b) show that the fiber has an average diameter range between 100 and 200 nm as matched with images of FESEM above. Closely related observations were made in the previous TEM studies for the confirmation of CNF dimensions [33–35]. The images also revealed the firmness of the amorphous carbon structure. The high quality image (Figure 5) showed the layers by layers CNF structure as indicated by the white arrows. The image showed that the CNF microstructures possessed defective platelets and more graphitic platelets that was similar to previous reports [36–38].Figure 4
Transmission Electron Microscopy images CNF.
(a)
(b)Figure 5
Transmission Electron Microscopy images of layered structure of CNF.


## 3.4. Surface Area of the PAC-CNF

Using computer-monitoring system, the adsorbed nitrogen gas volume, equilibrium pressures, and BET surface area of the sample were determined. The specific BET surface area of the PAC was found to be 101.1 m2/g. After sonication, the Ni2+ impregnated PAC surface area increased to 131.2 m2/g due to production of additional fine particles during the sonication process. On the other hand, the CNF grown on PAC exhibited 836.7 m2/g, which was more than eight times surface area compared to that of PAC.Plot of volume of nitrogen gas adsorbed on raw PAC and PAC-CNF versusP/P
0 are shown in Figures 6 and 7, respectively. The plot yields a line of slope [(c
-
l)/c
V
m] and intercept [l/c
V
m], where V is the amount of the adsorbate. The values of c, R
2, and V
m (monolayer capacity) were determined from the plots and the results are given in Table 2. As shown in Table 2, the new product, PAC-CNF, exhibited a higher monolayer capacity (V
m) and total pore volume compared with the PAC, and this is in conformity with earlier reports [39, 40]. These results are due to the increase in the surface area after the growth of the CNF on the PAC surface.Table 2
BET isotherm parameters for nitrogen gas adsorption by PAC and PAC-CNF.
Compound
Parameter
Total pore volume (cc/g)
V
m
R
2
PAC
8.8
×
10
-
2
0.029
0.9999
Impregnated PAC
3.26
×
10
-
1
0.029
0.9996
PAC-CNF
6.75
×
10
-
1
0.24
0.9985Figure 6
Adsorption/desorption of nitrogen gas on PAC.Figure 7
Adsorption/desorption of nitrogen gas on PAC-CNF.


## 3.5. Zeta Potential

The zeta potential of the materials was measured for PAC and PAC-CNF in water. Test results showed that the zeta potential for the samples was negative and the peaks shifted towards zero point from PAC value (−30.9) to the PAC-CNF value (−24.9). The negative sign for the zeta potentials was indicative of the hydrophilicity of the composite. The high negative charge is an indication that the adsorbent is more hydrophilic [41]. The values of the zeta potential for the PAC after the growth of the CNF were still in the range of “incipient instability,” a description similar to what was previously reported [42].


## 3.6. Surface Chemistry

The spectrum for the PAC, impregnated PAC, and CNF samples displayed bands with their respective functional groups as shown in Figure8. The intensity of the band in the 3859–2519 cm−1 region contains –OH groups. The width and asymmetry of this band indicated the existence of strong hydrogen bonds, which could be due to adsorbed water on the PAC surfaces. The bands at 1965 and 1746 and 2250–2400 cm−1 were indicative of the presence of carbonyl groups [43, 44]. Those bands at 996 cm−1 contain saturated carbon (methyl group –CH3) which might be from the cracking of acetylene [45].Figure 8
FTIR diagram of PAC, impregnated PAC, and PAC-CNF.The presence of these bands shows the formation of new carbon groups on the surface of PAC which is due to CNF [46]. Absorption peaks at 766 and 702 cm−1 represent NO2 bending vibrations [47]. These results were in agreement with the surface chemistry of other agricultural by-products [45, 48, 49]. Table 3 explains the peaks and functional groups represented by the bands.Table 3
Functional groups detected by FTIR on PAC, impregnated PAC, and PAC-CNF.
Wave number at peak (cm−1)
Functional group
Type of vibration
3859–2519
–OH (un-bonded), –OH (bonded)
No interferences such as OH in lattice, –OH stretch
2400–2250 & 1965, 1746
Aldehyde, ketone, carboxylic acid
C=O, carbonyl group
2343
CO2
1573
C=C aromatic ring
C=C stretch
996
Methyl group
Saturated –CH3
766 & 702
NO2
Bending
739
Hydrogen on an aromatic ring
Adjacent hydrogens on an aromatic ring (Ortho)


## 3.7. Energy Dispersive X-Ray (EDX) Analysis

The EDX imaging analysis revealed the materials’ surface structure and the local elements distribution of PAC, impregnated PAC, and PAC-CNF were examined using the EDX analyzer as depicted in Figure9 [50]. Figures 9(a), 9(b), and 9(c) showed the electron images for the samples; this invariably showed the difference in the surface structure between the four compounds. These observations conformed to the spectrum images shown in Figure 9.Figure 9
EDX spectrums for (a) PAC, (b) Ni impregnated PAC, and (c) PAC-CNF.
(a)
(b)
(c)It was observed in Figure9 that carbon element was present in high percentage in the four mentioned samples followed by oxygen and other elements as impurities (Na, Si, Cl, K, and Ca) with low percentages. The existence of nickel element on the surface of the PAC after impregnation of the element was also established, and this proved the success of the impregnation process. The elements detected by the EDX analyzer with their respective average weight and atomic percentages are presented in Table 4. The table showed that the percentage of the atomic carbon increased from 87% to 94% after the CNF growth on the surface of the substrate which enhances the decomposition of the acetylene to atomic carbon, similar to what was reported previously [51]. The presence of nickel on the surface of PAC was about 6.2%.Table 4
Compositions of elements in PAC, Ni impregnated PAC, and PAC-CNF.
Element
Average weight(%)
Average atomic composition (%)
PAC
Ni-PAC
PAC-CNF
PAC
Ni-PAC
PAC-CNF
C
89.98
78.85
87.37
92.10
86.69
94.05
O
4.88
13.96
3.95
7.20
11.52
6.66
Na
0.18
—
—
0.10
—
—
Si
0.71
0.37
0.69
0.32
0.18
0.32
Cl
0.32
—
—
0.40
—
—
K
0.33
0.36
0.55
0.11
0.12
0.18
Ca
0.43
0.26
0.31
0.13
0.08
0.22
Ni
—
6.16
5.84
—
1.39
1.29


## 3.8. Thermogravimetric Analysis (TGA)

Thermogravimetric analysis (TGA) revealed the temperature effect on the PAC and CNF. The TGA profiles obtained under the inert gas condition are presented in Figure10. The first weight loss occurring around 100°C of temperature was observed for the samples which was caused by thermodesorption of physically adsorbed material such as water vapor (moisture) and hydrocarbons [52] and it showed that the moisture content was around 15–18% for PAC and CNF, respectively.Figure 10
Thermal stability of PAC and PAC-CNF.High temperatures (between 400 and 480°C) for CNF and PAC, respectively, led to the start of combustion. Decrease in weight is commonly considered to be due to the vaporization of volatile organic compounds [53], which was indicated by a significant weight loss of 70% w/w. It was also observed that the weight loss stopped after a higher limit of combustion temperature (570 and 780°C for CNF and PAC, resp.) was reached. Some residual material remained for all samples, and these residues indicated the carbon purity of the samples with PAC having 5% representing the ash content and PAC-CNF exhibiting 8%, which was due to the Ni2+ catalyst impregnated on PAC surface prior to the CNF growth.


## 4. Conclusions

The morphological property of the oil palm kernel shell-based PAC was modified through the impregnation of Ni catalyst, followed by the synthesis of CNF with the presence of acetylene as a carbon source. Dispersion of Ni2+ catalyst was successfully carried out with the use of acetone sonication for nickel (II) nitrate hexahydrate to arrive at the successful growth of CNF. Several concentrations of Ni2+ catalysts were tested and the best growth of CNF was achieved at 3% Ni2+ (w/w). The FESEM and TEM showed the graphitic structure of the PAC-CNF, BET surface area 836.7 m2/g, zeta potential −24.9 mV, and TGA combustion temperature range between 400°C and 570°C.



---