# Grafting Carbon Nanotubes on Glass Fiber by Dip Coating Technique to Enhance Tensile and Interfacial Shear Strength

Authors: Bahador Dastorian Jamnani; Soraya Hosseini; Saeed Rahmanian; Suraya Abdul Rashid; Sa'ari b. Mustapha; Sepideh Keshan Balavandy
Journal: Journal of Nanomaterials
 (2015)

---

## Abstract

The effects of noncovalent bonding and mechanical interlocking of carbon nanotubes (CNT) coating on tensile and interfacial strength of glass fiber were investigated. CNT were coated over glass fiber by a simple dip coating method. Acid treated CNT were suspended in isopropanol solution containing Nafion as binding agent. To achieve uniform distribution of CNT over the glass fiber, an optimized dispersion process was developed by two parameters: CNT concentration and soaking time. CNT concentration was varied from 0.4 to 2 mg/mL and soaking time was varied from 1 to 180 min. The provided micrographs demonstrated appropriate coating of CNT on glass fiber by use of CNT-Nafion mixture. The effects of CNT concentration and soaking time on coating layer were studied by performing single fiber tensile test and pull-out test. The obtained results showed that the optimum CNT concentration and soaking time were 1 mg/mL and 60 min, respectively, which led to significant improvement of tensile strength and interfacial shear stress. It was found that, at other concentrations and soaking times, CNT agglomeration or acutely curly tubes appeared over the fiber surface which caused a reduction of nanotubes interaction on the glass fiber.


---

## Body

## 1. Introduction

Carbon nanotubes, both single walled and multiwalled, are widely used and well characterized as nanofillers [1]. These materials composed of graphitic sheets that are rolled into tubes possess unique properties, mainly due to their sp2 bonds [2]. The tensile strength of carbon nanotubes is about one hundred times higher than that of steel, while their specific weight is about six times lower [3]. Thus, CNT have attracted extensive investigations in the field of biomedical materials, biosensors, drug delivery, composite materials, and tissue engineering because of their high chemical stability, good mechanical and thermal properties, electrical property, and biochemical property [4]. CNT are considered as promising nanofillers in composite materials [5] which are being increasingly used in many engineering applications because of their numerous advantages over conventional engineering materials such as metals [6]. High stiffness and strength to weight ratio are among their most appealing advantages [7]. Fiber-reinforced composite (FRC) materials consist of a stiff and strong phase (fibrous filler) and another typically weaker phase (matrix). It is important to understand the drawbacks of conventional FRC materials in terms of their response to different types of mechanical loading and failure mechanisms in order to target specific areas and make progress towards the improvement of the material [8, 9]. Failure can be manifested in many forms such as the breaking of fibers, microcracking of matrix, and separation of fibers from the matrix (debonding) [10].Glass fiber (GF) is widely used as reinforcement in the manufacture of FRC materials with polymeric matrices [11] such as polyester, vinylester, phenolic, and epoxy resins [12]. However the stress transfer from the matrix to the GFs often presents a challenge to exploit the reinforcement role of fibers completely. CNT coating on GF can be suggested as an appropriate method to improve the adhesion of fiber and matrix [13, 14]. Furthermore, the addition of the conductive CNT fiber to the nonconductive GF composite can enhance its multifunction ability for the structural health monitoring of the composite material. In addition, the CNT integration with optical fiber has been reported to improvement the sensitivity of electrochemical sensors [15]. Various researches have been done to coat CNT on carbon fiber by use of chemical vapor deposition (CVD) [16, 17] or electrophoretic methods [18] with much success. But GF cannot be easily used in CVD or electrophoretic deposition because of their thermal instability and nonconductive behavior, respectively [19]. Therefore, solution dip coating method [20] is considered as a suitable alternative method to coat CNT on GF. Indeed different parameters such as solvent media, filler concentration, and coating time are important factors in order to provide effective coverage of nanotubes on GF.In this paper the effects of mechanical interlocking and noncovalent bonding of CNT on the interfacial and tensile strength of GF were investigated. A simple dip coating method is presented to graft CNT on GF by use of a binding agent. CNT suspension containing Nafion was examined with different concentrations and soaking times to find the optimal coating condition. SEM images were used to identify the CNT morphology deposited on the surface of GFs. The effects of nanotubes coverage on mechanical properties of GFs were demonstrated by performing single fiber tensile and pull-out tests. By comparing the SEM images and mechanical properties, a relationship between CNT coating and tensile and interfacial characteristics of GF was interpreted.


## 2. Experimental

### 2.1. Materials

All chemicals used were of analytical reagent grade purchased from Sigma Aldrich. Isopropanol was purchased from Bischem Co. Nafion solution (5%) was obtained from High Tech Company. CNT with a diameter of 20–40 nm were provided by Hangzhou Dayang Chem Co. GF (obtained from Fibreglass Enterprise, China) with a diameter of 20μm was used as received. The thermoset matrix used was a commercially available epoxy resin as known as EpoxAmite purchased from Smooth-On, Inc. The thermoset was fabricated based on two epoxy and hardener components. The optimum weight ratio of epoxy and hardener was suggested by the manufacturer as 100/28.4 by weight. The characteristics of neat epoxy and hardener are summarized in Table 1.Table 1
Characteristics of neat epoxy.
Hardener type
Mix ratio by volume
Mixed viscosity CPS
Ultimate tensile strength (MPa)
Tensile modulus (GPa)
Heat deflection temp. (°C)
4,40 Methylenebis(cyclohexylamine) and polypropylene triamine
3 : 1
650
55
1.75
53


### 2.2. CNT-Solvent Mixture for Coating

CNT were oxidized in order to add oxygen functional groups to the carbon surface using nitric acid and sulfuric acid. 5 g of CNT was fluxed in 250 mL solution containing concentrated HNO3 (63 wt%) and H2SO4 (98%) at 130°C for 2 h to remove impurities. The detailed procedure for the functionalization process can be found in [21]. After acid treatment, the mixture was allowed to cool. The mixture was then filtrated by using glass filter funnels via vacuum filtration. The residual was washed several times with hot distilled water to remove excess acid solution until the pH reached 7 [22]. Then, the acid modified CNT were dried at 100°C for 24 h. The acid modified CNT were denoted as CNT-treated. The treated CNT were added to 24 mL isopropanol (IPA) solvent and 1 mL Nafion solution (5%). Nafion (5%) allows better dispersion of the nanotubes as it facilitates dispersion through the application of ultrasonic forces, high shear mixing, or other dispersion methods. Ultrasonication process was employed for 1 h to provide a homogeneous suspension. Then, the homogeneous suspension was used in order to coat GF. Different amounts of treated CNT (0.01, 0.025, 0.04, and 0.05 g) were used to prepare coating solution. After finding the optimal CNT concentration, the GF was dip-coated on the suspension with soaking times of 1, 30, 60, 120, and 180 min. The samples were dried in a vacuum oven at 70°C for 24 h. The morphology of the composites was examined by scanning electron microscopy (SEM, S-4800, Hitachi).


### 2.3. Single Fiber Tensile Test

The tensile strength of each single GF was evaluated using a Universal Testing Machine (Instron) aiming at determining the influence of the CNT coating on the axial properties. To prepare the sample for the test, single GFs were stuck onto a paper frame with glue for better handling. Then, the fiber and frame were subjected to mechanical loading at a crosshead speed of 0.5 mm/min [20]. The data of force and displacement were measured during the tests and used to calculate the modulus and ultimate tensile strength of specimens. In addition, the fiber diameter was measured individually by use of an optical microscope. The gauge lengths were 25 mm. A minimum of twenty measurements were carried out for each type of coated GF specimen with fixed gauge length.


### 2.4. Single Fiber Pull-Out Test

Single fiber pull-out tests were carried out on a universal testing machine with the apparatus as illustrated in Figure1. First, few drops of epoxy were put on the single fiber to be cured. A GF was pulled out at a crosshead speed of 0.5 μm/s [23] from the drop of cured epoxy. The interfacial shear strength (IFSS) was calculated according to the maximum force applied to pull the GF out of the epoxy drop by the employment of the following equation:(1)τIFSS=Fmax⁡π·df·le,where Fmax is defined as the maximum pullout force, df is the diameter of GF, and le refers to the embedded length of microdroplet. At least 20 specimens were tested for each set of single fibers.Figure 1
Schematic representation of single fiber pull-out test.


## 2.1. Materials

All chemicals used were of analytical reagent grade purchased from Sigma Aldrich. Isopropanol was purchased from Bischem Co. Nafion solution (5%) was obtained from High Tech Company. CNT with a diameter of 20–40 nm were provided by Hangzhou Dayang Chem Co. GF (obtained from Fibreglass Enterprise, China) with a diameter of 20μm was used as received. The thermoset matrix used was a commercially available epoxy resin as known as EpoxAmite purchased from Smooth-On, Inc. The thermoset was fabricated based on two epoxy and hardener components. The optimum weight ratio of epoxy and hardener was suggested by the manufacturer as 100/28.4 by weight. The characteristics of neat epoxy and hardener are summarized in Table 1.Table 1
Characteristics of neat epoxy.
Hardener type
Mix ratio by volume
Mixed viscosity CPS
Ultimate tensile strength (MPa)
Tensile modulus (GPa)
Heat deflection temp. (°C)
4,40 Methylenebis(cyclohexylamine) and polypropylene triamine
3 : 1
650
55
1.75
53


## 2.2. CNT-Solvent Mixture for Coating

CNT were oxidized in order to add oxygen functional groups to the carbon surface using nitric acid and sulfuric acid. 5 g of CNT was fluxed in 250 mL solution containing concentrated HNO3 (63 wt%) and H2SO4 (98%) at 130°C for 2 h to remove impurities. The detailed procedure for the functionalization process can be found in [21]. After acid treatment, the mixture was allowed to cool. The mixture was then filtrated by using glass filter funnels via vacuum filtration. The residual was washed several times with hot distilled water to remove excess acid solution until the pH reached 7 [22]. Then, the acid modified CNT were dried at 100°C for 24 h. The acid modified CNT were denoted as CNT-treated. The treated CNT were added to 24 mL isopropanol (IPA) solvent and 1 mL Nafion solution (5%). Nafion (5%) allows better dispersion of the nanotubes as it facilitates dispersion through the application of ultrasonic forces, high shear mixing, or other dispersion methods. Ultrasonication process was employed for 1 h to provide a homogeneous suspension. Then, the homogeneous suspension was used in order to coat GF. Different amounts of treated CNT (0.01, 0.025, 0.04, and 0.05 g) were used to prepare coating solution. After finding the optimal CNT concentration, the GF was dip-coated on the suspension with soaking times of 1, 30, 60, 120, and 180 min. The samples were dried in a vacuum oven at 70°C for 24 h. The morphology of the composites was examined by scanning electron microscopy (SEM, S-4800, Hitachi).


## 2.3. Single Fiber Tensile Test

The tensile strength of each single GF was evaluated using a Universal Testing Machine (Instron) aiming at determining the influence of the CNT coating on the axial properties. To prepare the sample for the test, single GFs were stuck onto a paper frame with glue for better handling. Then, the fiber and frame were subjected to mechanical loading at a crosshead speed of 0.5 mm/min [20]. The data of force and displacement were measured during the tests and used to calculate the modulus and ultimate tensile strength of specimens. In addition, the fiber diameter was measured individually by use of an optical microscope. The gauge lengths were 25 mm. A minimum of twenty measurements were carried out for each type of coated GF specimen with fixed gauge length.


## 2.4. Single Fiber Pull-Out Test

Single fiber pull-out tests were carried out on a universal testing machine with the apparatus as illustrated in Figure1. First, few drops of epoxy were put on the single fiber to be cured. A GF was pulled out at a crosshead speed of 0.5 μm/s [23] from the drop of cured epoxy. The interfacial shear strength (IFSS) was calculated according to the maximum force applied to pull the GF out of the epoxy drop by the employment of the following equation:(1)τIFSS=Fmax⁡π·df·le,where Fmax is defined as the maximum pullout force, df is the diameter of GF, and le refers to the embedded length of microdroplet. At least 20 specimens were tested for each set of single fibers.Figure 1
Schematic representation of single fiber pull-out test.


## 3. Results and Discussion

Figure2 shows the surface morphology of the as-prepared samples. SEM results were carried out to examine the coated surfaces and monitor the failure mechanism. Figure 2(a) shows an SEM image of the neat GF and Figures 2(b), 2(c), and 2(d) show various concentrations of CNT coated on the GF using a set soaking time of 1 min.Figure 2
(a) Neat GF and CNT coated GF with different concentrations of CNT suspension, (b) 0.4 mg/mL, (c) 1 mg/mL, and (d) 2 mg/mL.The surface of neat GF was smooth in nature while the coating with 0.4 mg/mL CNT concentration showed a thin and nonuniform coating on the GF surface. As shown in Figure2(c), increasing the suspension concentration to 1 mg/mL led to a relatively uniform and denser deposition of nanotubes on the fiber surface. The inset image also provides better view of the CNT configuration at high magnification which shows individual attachment of nanotubes. Figure 2(d) reveals a high density attachment of CNT with agglomerated regions which were formed by soaking fibers in 2 mg/mL suspension concentration. The SEM images shown in Figure 2 qualitatively indicate that 1 mg/mL is the optimal concentration which provides an appropriate amount of CNT coating on GF. Therefore, this concentration was selected to examine the effect of soaking time on coating morphology.The results of soaking time are shown in Figures3(a) and 3(b) with soaking times of 60 and 180 min, respectively. In comparison to 5 min soaking time Figure 2(c) and Figure 3(a) show a homogeneous and complete coverage of nanotubes on the fiber surface, which demonstrate the coating improvement with 60 min soaking time. Soaking the GF for a longer time especially at 180 min resulted in higher absorption of nanotubes to the surface. In this situation, the larger coating thickness of CNT and the interaction among nanotubes separate them in some region from GF. It can be interpreted that the adhesion of CNT to the fiber surface was declined because of stronger interaction between nanotubes and formation of bulk aggregations. By comparing the SEM images of Figures 2 and 3, it can be deduced that both CNT concentration and soaking time are important factors to consider in order to obtain proper grafting of nanotubes on to the fiber surface.Figure 3
CNT coated GF soaked in 1 mg/mL CNT suspension with soaking time of (a) 60 min and (b) 180 min.Single fiber tensile tests were carried out to measure the effect of CNT coating on the modulus and tensile strength of GF. The tensile properties of as-received and coated GF are presented in Figures4(a) and 4(b). Comparing the elastic modulus of coated GF in Figure 4(a) reveals that the CNT coating does not influence elastic modulus significantly. However, the CNT coating affected the ultimate tensile strength of GF under certain treatment conditions. Varying the concentration of CNT suspension revealed that an optimum coating concentration was achieved at 1 mg/mL CNT suspension which yielded an enhancement of tensile strength by 28%. Lower or higher CNT coating concentrations improved the tensile strength of GF only slightly. Interestingly coating the GF with the highest concentration of 2 mg/mL led to a strength similar to the neat GF. This implies that the CNT coating with higher concentration somehow does not interact with the surface of GF effectively. Perhaps a thicker coating led to some debonding of the coating from the surface of the fiber.Figure 4
Ultimate tensile strength of CNT coated GF (a) with different CNT concentrations and (b) with different soaking times.
(a)
(b)After detection of optimum concentration of CNT suspension, the effect of GF soaking time on the tensile strength of the GF was also studied as shown in Figure4(b). The results show that a similar trend was achieved for soaking time whereas an optimum soaking time was observed. The tensile strength increased by 38% as the soaking time was increased to 1 h. However, extending the soaking time for more than 1 hour led to a decrease in the tensile strength. Indeed, higher soaking time resulted in a higher density of coated nanotubes on the GF surface which can explain the change of single fiber strength by debonding process.The IFSS was also studied as shown in Figures5(a) and 5(b). The IFSS increased to 76% compared to neat fiber by increasing the CNT concentration to 1 mg/mL. However, increasing the concentration further led to a decrease in IFSS. As for the effect of soaking time, increasing the soaking time to 1 h led to an improvement by 23% in comparison to 1 min soaking time and by 116% in comparison to neat GF. Extending the soaking time further led to a decrease in IFSS of coated GF.Figure 5
Interfacial shear stress of CNT coated GF (a) with different suspension concentrations and (b) with different soaking times.
(a)
(b)Looking at the obtained mechanical properties hints that CNT coating affects the strength and IFSS of single fiber, which is related to the surface properties of the fibers. Appropriate attachment of nanotubes on the surface of GF can repair the defects on the fiber and bridge the crack or flaw as well as hindering their propagation which led to the increase in fiber strength. This achievement is important since CNT cannot grow easily on GF like carbon fiber. Furthermore, growing CNT on carbon fiber often reduces the strength of carbon fiber because of the catalyst interaction with fiber surface [24, 25]. In the present method, CNT were coated on GF with a simple technique which improved its tensile strength. Considering the magnitude of shear stress between coated GF and epoxy droplet indicates that the improvement of shear stress was achieved with van der Waals bonding [26] as well as mechanical interlocking of nanotubes between the matrix and fiber [27]. In this experiment, chemical treatment was not used in attaching the CNT to the GF. Therefore, it can be inferred that nanotubes can enhance the shear stress of fiber and matrix effectively through mechanical interlocking under optimum coating conditions.Additional inference of the CNT effects on the mechanical properties of GF can be provided by relating the mechanical properties with the SEM images of coated nanotubes. By increasing the concentration of CNT suspension or soaking time, the coverage of nanotubes on fiber surface increased. Consequently, the matrix-fiber interaction was improved which was afforded by the higher surface area of nanotubes, thus improving the mechanical properties of the coated fiber. However, an optimal coating is necessary since higher concentrations of CNT would cause CNT entanglement. When nanotubes entangle and twist each other, an agglomeration of CNT is created which significantly weakens the matrix-fiber interaction and reduces the stress transfer to individual nanotubes. As shown previously in Figures2(d) and 3(b), higher than optimum CNT concentrations caused CNT to entangle and create agglomerations on the GF surface. Such areas adhere weaker to the fiber surface and in some regions are obviously separated from the fiber as shown in Figure 3(b). When nanotubes entangle and twist each other, an agglomeration of CNT is created which decline dramatically the stress transfer to individual nanotubes. Such agglomeration bulks form a smooth surface with low interaction to the surrounded fiber or matrix. These configurations were not effective in shear stress between GF and epoxy as well as fiber strength. Hence, CNT coverage is only effective on mechanical properties in optimum condition of nanotubes coating through dip coating technique.The GF with the optimal coating after pull-out test is shown in Figures6(a) and 6(b). When a fiber is pulled from a polymer matrix, the tensile force is transmitted to the surrounding matrix on the fiber surface through shear stress. SEM images of the interfacial region of fiber and matrix after fracture can be used to evaluate the effect of CNT coating. Figure 6(a) clearly shows the rough surface of GF on the contact zone of fiber and epoxy drop. The high magnification image of the interface region (Figure 6(b)) demonstrates the adhesion of epoxy on the fiber surface with dimensions equal to the CNT coating layer. The coated CNT provide an anchoring mechanism in the interface region, which improves the matrix-fiber interaction. When the GF is pulled, the nanotubes on the interface region undergo both tensile and shear stress followed by being transferred to the epoxy matrix. Therefore, it can be deduced that the morphology of coated fiber indicates that the coating of CNT on GF creates local interlocking between the matrix and fiber which results in the improvement of stress transfer between fiber and matrix.Figure 6
SEM images of CNT coated GF after pull-out test.


## 4. Conclusions

A simple dip coating method was presented to graft CNT on GF. Acid treated CNT were dispersed in isopropanol with the addition of Nafion to enhance dispersion. CNT concentration and soaking time of GF in the CNT suspension were investigated to find the optimum coverage of nanotubes. CNT concentration of 1 mg/mL and 60 min soaking time was found to provide an optimal coating condition for CNT coated GF. SEM images showed that the CNT coating was homogeneous with complete coverage. Single fiber tensile test and interfacial shear stress were employed to study the effect of CNT coating on the mechanical properties of GFs. Whilst the elastic modulus of coated fibers was approximately unchanged with CNT coating morphology, its ultimate tensile strength increased up to 38% under optimal CNT coating condition. The interfacial shear stress of optimal CNT coated GF was measured by pull-out test and demonstrated an improvement of up to 116% compared to neat GF.



---