# Phase Transformation of Iron Oxide Nanoparticles from Hematite to Maghemite in Presence of Polyethylene Glycol: Application as Corrosion Resistant Nanoparticle Paints

Authors: Pavani Katikaneani; Ajay Kumar Vaddepally; Narender Reddy Tippana; Ramu Banavath; Srivani Kommu
Journal: Journal of Nanoscience
 (2016)

---

## Abstract

This work proposes a simple method for the efficient and rapid synthesis of hematite (α-Fe2O3) nanostructures based on simple heating method under ambient conditions. Polyethylene glycol (PEG) is employed as a structure directing agent in driving the morphology and phase transformation. Typically, Fe2O3 nanoparticles of size below 50 nm were synthesized at temperature around 500°C. The morphology and mechanism of formation of the nanocapsules and then aggregation of nanocapsules to form larger size nanoclusters were studied by scanning electron microscopy and energy dispersive X-ray spectroscopy. Interestingly, this work demonstrates the structural phase transformation of hematite (α-Fe2O3) to maghemite (γ-Fe2O3) upon addition of different amounts of PEG (say 0.066 M, 0.133 M, and 0.2 M) and then heat treating at 500°C. The prepared powders were used in nanoparticle paint preparation and applied as corrosion resistant coatings on iron samples. Polarization studies performed on the paint coatings made out of all the prepared samples showed size-dependent corrosion resistance. As the particle size decreases, the surface area increases and so the corrosion resistance also increases.


---

## Body

## 1. Introduction

From the last few decades, transition metal oxide nanoparticles have attracted tremendous interest due to their promising applications as electrode materials for rechargeable solid-state batteries [1, 2], as efficient catalysts for fuel-cell reactions [3, 4], and as nanoscale magnetic models for understanding nanomagnetism [5, 6]. Amongst these, iron oxide nanoparticles have received much attention due to their massive applications in the fields of information storage disks, ferrofluids, pigments, and medical applications like targeted drug delivery and cancer diagnoses [7–9]. Iron (III) oxide is an inorganic compound with the formula Fe2O3 and it is of one of the three main oxides of iron; the other two are rarely available iron (II) oxide (FeO) and naturally occurring iron (II, III) oxide (Fe3O4). In steel industry, hematite is the main source of the iron for the production of steel and it is paramagnetic, readily attacked by acids, and reddish brown in colour. As hematite is the most stable and n-type semiconductor under ambient conditions, it is widely used as catalysts, gas sensors, and pigments due to its high resistance to corrosion and low cost. It can also be used as a starting material for the synthesis of maghemite (γ-Fe2O3) and magnetite (Fe3O4), which have been intensively pursued for technological applications in the last few decades [10]. However, hematite is also interesting material as it has a band gap of 2.3 eV; the conduction band (CB) is composed of empty d-orbitals of Fe3+ and the valence band (VB) consists of fully occupied 3D crystal field orbitals of Fe3+ with some admixture from the O 2p nonbonding orbitals [11]. Several methods to synthesize iron oxide nanoparticles such as mechanochemical [12, 13], wire electrical explosion [14], and electrochemical [15, 16] methods have been reported. On the other hand, the method employed in the present work is simple heating method in presence of PEG. Iron nitrate nonahydrate was used as a precursor to formulate Fe2O3 nanostructures involving simple heating process with varying amounts of PEG. The prepared samples were characterized by X-ray diffraction, field emission scanning electron microscopy, and energy dispersive X-ray spectroscopy (EDX). Interestingly, powder XRD was found to show phase transformation from α-Fe2O3 to γ-Fe2O3 with the increase in PEG concentration. This type of transformation is commonly observed with the effect of temperature [17, 18]. The prepared nanoparticles were used in paint preparation and were found to show excellent corrosion resistance as coatings.


## 2. Experimental Method

### 2.1. Synthesis

Iron oxide nanoparticles (Fe2O3) are prepared by simple heating method. This process involves preparation of 0.589 M solution of ferric nitrate nonahydrate salt precursor by dissolving 10 g of Fe(NO3)3·9H2O in 42 mL water to precipitate the oxohydrate at higher temperatures (~70°C). To each 10 mL of prepared salt precursor solution, various amount of PEG (0 M, 0.066 M, 0.133 M, 0.2 M) (as shown in Table 1) is added and stirred for one hour at higher temperatures (~100°C) till the homogeneous viscous solution is formed. These viscous materials were heat treated at 500°C for 1 hour to obtain different iron oxide nanopowders.Table 1
Experimental details.
Sample code
Precursor 0.589 M [Fe(NO3)3
⋅9H2O] solution (mL)
Amount of PEG in g
Molar ratio (precursor : PEG)
Fe2O3-0 PEG
10
0
—
Fe2O3-4 PEG
10
4 (0.066 M)
8.9 : 1
Fe2O3-8 PEG
10
8 (0.133 M)
4.4 : 1
Fe2O3-12 PEG
10
12 (0.2 M)
2.9 : 1


### 2.2. Characterization

The crystal structure of the synthesized particles was determined by powder X-ray diffractometer (D8 Discover, Bruker AXS Co., Ltd., Germany) with Cu-Kα radiation, λ = 1.54056 Å. The particle size and morphology were derived from field emission gun scanning electron microscope (Carl Zeiss Co. Ltd., Germany) and the elemental composition was obtained from energy dispersive X-ray spectroscopy attached to FESEM (EDX INCA, Oxford Instruments).


### 2.3. Corrosion Study

#### 2.3.1. Paint Preparation

Paint preparation involves (i) pigment preparation, (ii) binder preparation, and (iii) pigment binder grinding. Pigment preparation is carried out by taking prepared iron oxide nanoparticles of 1 g each (Fe2O3-0 PEG, Fe2O3-4 PEG, Fe2O3-8 PEG, and Fe2O3-12 PEG) onto a glass slab and made into paste using linseed oil. The iron oxide particles were taken onto a glass slab and then a crater is made in the middle of the powder, into the crater 1 mL of linseed oil is poured, and the mixture was mixed thoroughly with pallet knife. Along with this, binder is prepared by the addition of 2% of bee wax in the linseed oil. For this purpose, 0.4 g of bee wax is added to 19.6 mL of linseed oil and the mixture was heated at 60°C along with magnetic stirring, until all the wax gets dissolved in linseed oil and the colour of mixture turns out to be yellowish. This is cooled to room temperature and can be used as binder. Once the binder cools to room temperature, the pigment is taken onto glass slab; few drops of binder are added and ground well using a miller till the pigment gets mixed up with binder and feels like paint. The prepared paint is stored in plastic containers and was coated on thin sheets of iron on one side and tested for polarization curves.


#### 2.3.2. Potentiodynamic Polarization Curve

A characteristic three-electrode electrochemical corrosion cell was used in all the experiments. As a reference, a saturated calomel electrode (SCE) was used. All measured potentials were referred to this electrode. A platinum foil was used as the counter electrode. Then (i) parent iron sample (blank uncoated sample) and iron samples coated with paints prepared out of (ii) Fe2O3-0 PEG, (iii) Fe2O3-4 PEG, (iv) Fe2O3-8 PEG, (v) Fe2O3-12 PEG, and (vi) microsized Fe2O3 powder were used as working electrodes. A potentiostat (IEC 61326, Ivium Technologies, Netherlands), controlled by a personal computer, equipped with a GPIB card and the commercial software, was employed to attain the potentiodynamic polarization curves. Before every experiment, the open circuit potential (OCP) was recorded for at least 30 minutes. Polarization curves were obtained potentiodinamically; the linear potential sweep was performed at a ±248 mV potential window around the measured OCP, from the cathodic to the anodic side, at scan rates of 0.1 and 1 mV s−1.


## 2.1. Synthesis

Iron oxide nanoparticles (Fe2O3) are prepared by simple heating method. This process involves preparation of 0.589 M solution of ferric nitrate nonahydrate salt precursor by dissolving 10 g of Fe(NO3)3·9H2O in 42 mL water to precipitate the oxohydrate at higher temperatures (~70°C). To each 10 mL of prepared salt precursor solution, various amount of PEG (0 M, 0.066 M, 0.133 M, 0.2 M) (as shown in Table 1) is added and stirred for one hour at higher temperatures (~100°C) till the homogeneous viscous solution is formed. These viscous materials were heat treated at 500°C for 1 hour to obtain different iron oxide nanopowders.Table 1
Experimental details.
Sample code
Precursor 0.589 M [Fe(NO3)3
⋅9H2O] solution (mL)
Amount of PEG in g
Molar ratio (precursor : PEG)
Fe2O3-0 PEG
10
0
—
Fe2O3-4 PEG
10
4 (0.066 M)
8.9 : 1
Fe2O3-8 PEG
10
8 (0.133 M)
4.4 : 1
Fe2O3-12 PEG
10
12 (0.2 M)
2.9 : 1


## 2.2. Characterization

The crystal structure of the synthesized particles was determined by powder X-ray diffractometer (D8 Discover, Bruker AXS Co., Ltd., Germany) with Cu-Kα radiation, λ = 1.54056 Å. The particle size and morphology were derived from field emission gun scanning electron microscope (Carl Zeiss Co. Ltd., Germany) and the elemental composition was obtained from energy dispersive X-ray spectroscopy attached to FESEM (EDX INCA, Oxford Instruments).


## 2.3. Corrosion Study

### 2.3.1. Paint Preparation

Paint preparation involves (i) pigment preparation, (ii) binder preparation, and (iii) pigment binder grinding. Pigment preparation is carried out by taking prepared iron oxide nanoparticles of 1 g each (Fe2O3-0 PEG, Fe2O3-4 PEG, Fe2O3-8 PEG, and Fe2O3-12 PEG) onto a glass slab and made into paste using linseed oil. The iron oxide particles were taken onto a glass slab and then a crater is made in the middle of the powder, into the crater 1 mL of linseed oil is poured, and the mixture was mixed thoroughly with pallet knife. Along with this, binder is prepared by the addition of 2% of bee wax in the linseed oil. For this purpose, 0.4 g of bee wax is added to 19.6 mL of linseed oil and the mixture was heated at 60°C along with magnetic stirring, until all the wax gets dissolved in linseed oil and the colour of mixture turns out to be yellowish. This is cooled to room temperature and can be used as binder. Once the binder cools to room temperature, the pigment is taken onto glass slab; few drops of binder are added and ground well using a miller till the pigment gets mixed up with binder and feels like paint. The prepared paint is stored in plastic containers and was coated on thin sheets of iron on one side and tested for polarization curves.


### 2.3.2. Potentiodynamic Polarization Curve

A characteristic three-electrode electrochemical corrosion cell was used in all the experiments. As a reference, a saturated calomel electrode (SCE) was used. All measured potentials were referred to this electrode. A platinum foil was used as the counter electrode. Then (i) parent iron sample (blank uncoated sample) and iron samples coated with paints prepared out of (ii) Fe2O3-0 PEG, (iii) Fe2O3-4 PEG, (iv) Fe2O3-8 PEG, (v) Fe2O3-12 PEG, and (vi) microsized Fe2O3 powder were used as working electrodes. A potentiostat (IEC 61326, Ivium Technologies, Netherlands), controlled by a personal computer, equipped with a GPIB card and the commercial software, was employed to attain the potentiodynamic polarization curves. Before every experiment, the open circuit potential (OCP) was recorded for at least 30 minutes. Polarization curves were obtained potentiodinamically; the linear potential sweep was performed at a ±248 mV potential window around the measured OCP, from the cathodic to the anodic side, at scan rates of 0.1 and 1 mV s−1.


## 2.3.1. Paint Preparation

Paint preparation involves (i) pigment preparation, (ii) binder preparation, and (iii) pigment binder grinding. Pigment preparation is carried out by taking prepared iron oxide nanoparticles of 1 g each (Fe2O3-0 PEG, Fe2O3-4 PEG, Fe2O3-8 PEG, and Fe2O3-12 PEG) onto a glass slab and made into paste using linseed oil. The iron oxide particles were taken onto a glass slab and then a crater is made in the middle of the powder, into the crater 1 mL of linseed oil is poured, and the mixture was mixed thoroughly with pallet knife. Along with this, binder is prepared by the addition of 2% of bee wax in the linseed oil. For this purpose, 0.4 g of bee wax is added to 19.6 mL of linseed oil and the mixture was heated at 60°C along with magnetic stirring, until all the wax gets dissolved in linseed oil and the colour of mixture turns out to be yellowish. This is cooled to room temperature and can be used as binder. Once the binder cools to room temperature, the pigment is taken onto glass slab; few drops of binder are added and ground well using a miller till the pigment gets mixed up with binder and feels like paint. The prepared paint is stored in plastic containers and was coated on thin sheets of iron on one side and tested for polarization curves.


## 2.3.2. Potentiodynamic Polarization Curve

A characteristic three-electrode electrochemical corrosion cell was used in all the experiments. As a reference, a saturated calomel electrode (SCE) was used. All measured potentials were referred to this electrode. A platinum foil was used as the counter electrode. Then (i) parent iron sample (blank uncoated sample) and iron samples coated with paints prepared out of (ii) Fe2O3-0 PEG, (iii) Fe2O3-4 PEG, (iv) Fe2O3-8 PEG, (v) Fe2O3-12 PEG, and (vi) microsized Fe2O3 powder were used as working electrodes. A potentiostat (IEC 61326, Ivium Technologies, Netherlands), controlled by a personal computer, equipped with a GPIB card and the commercial software, was employed to attain the potentiodynamic polarization curves. Before every experiment, the open circuit potential (OCP) was recorded for at least 30 minutes. Polarization curves were obtained potentiodinamically; the linear potential sweep was performed at a ±248 mV potential window around the measured OCP, from the cathodic to the anodic side, at scan rates of 0.1 and 1 mV s−1.


## 3. Results and Discussion

### 3.1. Powder XRD

The powder X-ray diffraction (XRD) was performed to identify the phase composition of nanoparticles. Iron oxides have many phases such as magnetite (Fe3O4) and maghemite (γ-Fe2O3) with cubic crystal structure and hematite (α-Fe2O3) with rhombohedral crystal structure. The magnetite and maghemite have black and light brown colours, respectively [14], due to the similar crystal structure and close lattice parameters (a = 8.396 Å for magnetite and a = 8.351 Å for maghemite); they are similar in their X-ray diffraction patterns [19]. Fe3+ ions in α-Fe2O3 occupy two-thirds of the octahedral sites that are confined by the virtually ideal hexagonal close-packed O lattice. The structure of γ-Fe2O3 is cubic; each unit of maghemite contains 32 O2− ions, 21.3 Fe3+ ions, and 2.3 vacancies. Oxygen anions give rise to a cubic close-packed arrangement, while ferric ions are distributed over tetrahedral sites (eight Fe ions per unit cell) and octahedral sites (the remaining Fe ions and vacancies).Figure1 shows powder XRD patterns of all synthesized iron oxide nanoparticles. As can be observed, the iron oxide prepared in the absence of PEG (Fe2O3-0 PEG) and after heat treatment at 500°C showed pure hematite α-Fe2O3 phase, matching exactly with PDF-01-077-9926. The main peak of hematite at 33.15° is clearly observed. Other peaks at 24.1°, 35.6°, 40.8°, 49.4°, 54.1°, 57.4° (doublet), 62.4°, and 63.9° are found and indexed. However, the iron oxide synthesized in presence of PEG and heat treated at same temperature starts showing a phase transformation as observed from Figure 1; the main peak of hematite at 33.15° decreases in intensity and new peaks corresponding to maghemite (γ-Fe2O3) appear at 30° and nearly 43.5°. Interestingly, the addition of 12 g (0.2 M) of PEG shows major phase of maghemite (γ-Fe2O3) which can be well indexed and matched with PDF-00-039–1346 along with small amount of hematite α-Fe2O3 still remaining. The percentages calculated from Diffrac Eva software show 72.91% of maghemite (γ-Fe2O3) and 27.09% of hematite (α-Fe2O3) (refer to supplementary information in Supplementary Material available online at http://dx.doi.org/10.1155/2016/1328463). Phase transformation as a function of temperature is a common phenomenon [17, 18], but interestingly in the present work the phase transformation from hematite to maghemite phase is occurring on treatment with various amounts of PEG (0 M, 0.066 M, 0.133 M, and 0.2 M). The reason may be attributed to the fact that the phase transformation in iron oxides is often controlled by size-dependent thermodynamic relationships between initial and final product phases. The new phase is not thermodynamically favored until crystallites of the initial phase have assembled to certain critical size. These formed secondary structures underwent phase transformation, in which a new mineral phase begins forming at the interface between two surfaces of the initial phase [20].Figure 1
Powder XRD patterns of Fe2O3 nanoparticles at different concentrations of PEG.


### 3.2. SEM and EDX

The purpose of study was to measure the size and morphology of the prepared nanoparticles from SEM measurements. Figure2 shows the SEM images of samples which were prepared in presence of various amounts of PEG. Interestingly, it was observed that the particles prepared in the absence of PEG showed irregular morphology including spherical particles whose size was larger when compared to other samples, although existing in the nanorange. When prepared with 4 g (0.066 M) and 8 g (0.133 M) of PEG, the morphology of particles is capsule shaped and is uniform in size and shape. With 4 g (0.066 M) of PEG, nanocapsules of length of 62 nm and cylindrical diameter of 24 nm and in presence of 8 g (0.133 M) of PEG, nanocapsules of decreased size with length of 52 nm and cylindrical diameter of 20 nm were obtained. However, in presence of excess amount of PEG (12 g, 0.2 M), the capsules got sewed up to form angular nanostructures which get interconnected to form rhombic nanostructures which get converted into nanocluster with an average length nearly equal to 101 nm and average width of 40 nm as shown in Figure 2(d). The hypothetical mechanism of capsules getting converted into nanocluster is depicted in Figure 3. Although the average particle size is different under various conditions, the nanoparticles formed have an average particle size of less than 100 nm.Figure 2
SEM images of (a) Fe2O3-0 PEG, (b) Fe2O3-4 PE, (c) Fe2O3-8 PEG, and (d) Fe2O3-12 PEG.
(a)
(b)
(c)
(d)Figure 3
Hypothetical mechanism of aggregation of nanocapsules to nanoclusters on increasing the concentration of PEG.EDX analysis was used to identify the elemental composition of the samples and performed on different sites of each sample. The results showed that the samples consist of iron and oxygen, and no sign of impurity was detected and the composition exactly matches with Fe2O3.


### 3.3. Corrosion Inhibitor Coatings

The corrosion rate and corrosion resistance of iron samples coated with prepared paints involving different iron oxide powders (0 M, 0.066 M, 0.133 M, and 0.2 M PEG) were studied. The polarization curves (Figure4) clearly depict that it is the size and not the structure which influences the corrosion resistance behavior. If it would be structure which influences the corrosion resistance behavior, then the sample coated with Fe2O3-12 PEG being a cubic structure with more close-packing should show high corrosion resistance but it is observed that the paint prepared with Fe2O3-8 PEG has high corrosion resistance and low corrosion rate compared to other paints; this is due to the smaller size of particles in Fe2O3-8 PEG. Due to the smaller size, the surface area is high, so Fe2O3-8 PEG exhibit good surface properties and protect the surface from corrosion (Table 2). Figure 4 also shows that the paint which is prepared with Fe2O3-0 PEG has low corrosion resistance and high corrosion rate. Obviously, the reason is large particle size compared to other samples. From Fe2O3-0 PEG paint to Fe2O3-8 PEG paint corrosion resistance increases. However, in the paint prepared out of Fe2O3-12 PEG, corrosion resistance decreases and the reason is aggregation of nanocapsules to form nanoclustered large particles. The polarization curves (Figure 4) depict that as the size increases the corrosion resistance decreases. To explore more, the paints were prepared with microsized α-Fe2O3 readily available in the laboratory and tested for corrosion behavior. Interestingly, the paint prepared out of Fe2O3-0 PEG which showed highest corrosion rate (Table 2) was observed to have lowest corrosion rate compared to blank uncoated sample (parent iron sample) and sample coated with paint prepared from microsized α-Fe2O3 (Figure 5).Table 2
Corrosion rate and corrosion resistance data from polarization curves.
Sample code
Corrosion rate(mm/y)
Corrosion resistance(ohm)
Fe2O3-0 PEG
1.24 × 10−4
9.2 × 105
Fe2O3-4 PEG
1.04 × 10−7
2.66 × 109
Fe2O3-8 PEG
2.59 × 10−8
6.916 × 1011
Fe2O3-12 PEG
9.735 × 10−6
2.541 × 107
Microsized Fe2O3 powder
1.574 × 10−3
4.29 × 104
Blank sample
0.4222
225.8Figure 4
Polarization curves of iron samples coated with paints prepared from (A) Fe2O3-0 PEG, (B) Fe2O3-4 PEG, (C) Fe2O3-8 PEG, and (D) Fe2O3-12 PEG.Figure 5
Polarization curves of iron samples: (A) blank sample, (B) sample coated with paint prepared from microsized Fe2O3 powder, and (C) sample coated with paint prepared from Fe2O3-0 PEG.


## 3.1. Powder XRD

The powder X-ray diffraction (XRD) was performed to identify the phase composition of nanoparticles. Iron oxides have many phases such as magnetite (Fe3O4) and maghemite (γ-Fe2O3) with cubic crystal structure and hematite (α-Fe2O3) with rhombohedral crystal structure. The magnetite and maghemite have black and light brown colours, respectively [14], due to the similar crystal structure and close lattice parameters (a = 8.396 Å for magnetite and a = 8.351 Å for maghemite); they are similar in their X-ray diffraction patterns [19]. Fe3+ ions in α-Fe2O3 occupy two-thirds of the octahedral sites that are confined by the virtually ideal hexagonal close-packed O lattice. The structure of γ-Fe2O3 is cubic; each unit of maghemite contains 32 O2− ions, 21.3 Fe3+ ions, and 2.3 vacancies. Oxygen anions give rise to a cubic close-packed arrangement, while ferric ions are distributed over tetrahedral sites (eight Fe ions per unit cell) and octahedral sites (the remaining Fe ions and vacancies).Figure1 shows powder XRD patterns of all synthesized iron oxide nanoparticles. As can be observed, the iron oxide prepared in the absence of PEG (Fe2O3-0 PEG) and after heat treatment at 500°C showed pure hematite α-Fe2O3 phase, matching exactly with PDF-01-077-9926. The main peak of hematite at 33.15° is clearly observed. Other peaks at 24.1°, 35.6°, 40.8°, 49.4°, 54.1°, 57.4° (doublet), 62.4°, and 63.9° are found and indexed. However, the iron oxide synthesized in presence of PEG and heat treated at same temperature starts showing a phase transformation as observed from Figure 1; the main peak of hematite at 33.15° decreases in intensity and new peaks corresponding to maghemite (γ-Fe2O3) appear at 30° and nearly 43.5°. Interestingly, the addition of 12 g (0.2 M) of PEG shows major phase of maghemite (γ-Fe2O3) which can be well indexed and matched with PDF-00-039–1346 along with small amount of hematite α-Fe2O3 still remaining. The percentages calculated from Diffrac Eva software show 72.91% of maghemite (γ-Fe2O3) and 27.09% of hematite (α-Fe2O3) (refer to supplementary information in Supplementary Material available online at http://dx.doi.org/10.1155/2016/1328463). Phase transformation as a function of temperature is a common phenomenon [17, 18], but interestingly in the present work the phase transformation from hematite to maghemite phase is occurring on treatment with various amounts of PEG (0 M, 0.066 M, 0.133 M, and 0.2 M). The reason may be attributed to the fact that the phase transformation in iron oxides is often controlled by size-dependent thermodynamic relationships between initial and final product phases. The new phase is not thermodynamically favored until crystallites of the initial phase have assembled to certain critical size. These formed secondary structures underwent phase transformation, in which a new mineral phase begins forming at the interface between two surfaces of the initial phase [20].Figure 1
Powder XRD patterns of Fe2O3 nanoparticles at different concentrations of PEG.


## 3.2. SEM and EDX

The purpose of study was to measure the size and morphology of the prepared nanoparticles from SEM measurements. Figure2 shows the SEM images of samples which were prepared in presence of various amounts of PEG. Interestingly, it was observed that the particles prepared in the absence of PEG showed irregular morphology including spherical particles whose size was larger when compared to other samples, although existing in the nanorange. When prepared with 4 g (0.066 M) and 8 g (0.133 M) of PEG, the morphology of particles is capsule shaped and is uniform in size and shape. With 4 g (0.066 M) of PEG, nanocapsules of length of 62 nm and cylindrical diameter of 24 nm and in presence of 8 g (0.133 M) of PEG, nanocapsules of decreased size with length of 52 nm and cylindrical diameter of 20 nm were obtained. However, in presence of excess amount of PEG (12 g, 0.2 M), the capsules got sewed up to form angular nanostructures which get interconnected to form rhombic nanostructures which get converted into nanocluster with an average length nearly equal to 101 nm and average width of 40 nm as shown in Figure 2(d). The hypothetical mechanism of capsules getting converted into nanocluster is depicted in Figure 3. Although the average particle size is different under various conditions, the nanoparticles formed have an average particle size of less than 100 nm.Figure 2
SEM images of (a) Fe2O3-0 PEG, (b) Fe2O3-4 PE, (c) Fe2O3-8 PEG, and (d) Fe2O3-12 PEG.
(a)
(b)
(c)
(d)Figure 3
Hypothetical mechanism of aggregation of nanocapsules to nanoclusters on increasing the concentration of PEG.EDX analysis was used to identify the elemental composition of the samples and performed on different sites of each sample. The results showed that the samples consist of iron and oxygen, and no sign of impurity was detected and the composition exactly matches with Fe2O3.


## 3.3. Corrosion Inhibitor Coatings

The corrosion rate and corrosion resistance of iron samples coated with prepared paints involving different iron oxide powders (0 M, 0.066 M, 0.133 M, and 0.2 M PEG) were studied. The polarization curves (Figure4) clearly depict that it is the size and not the structure which influences the corrosion resistance behavior. If it would be structure which influences the corrosion resistance behavior, then the sample coated with Fe2O3-12 PEG being a cubic structure with more close-packing should show high corrosion resistance but it is observed that the paint prepared with Fe2O3-8 PEG has high corrosion resistance and low corrosion rate compared to other paints; this is due to the smaller size of particles in Fe2O3-8 PEG. Due to the smaller size, the surface area is high, so Fe2O3-8 PEG exhibit good surface properties and protect the surface from corrosion (Table 2). Figure 4 also shows that the paint which is prepared with Fe2O3-0 PEG has low corrosion resistance and high corrosion rate. Obviously, the reason is large particle size compared to other samples. From Fe2O3-0 PEG paint to Fe2O3-8 PEG paint corrosion resistance increases. However, in the paint prepared out of Fe2O3-12 PEG, corrosion resistance decreases and the reason is aggregation of nanocapsules to form nanoclustered large particles. The polarization curves (Figure 4) depict that as the size increases the corrosion resistance decreases. To explore more, the paints were prepared with microsized α-Fe2O3 readily available in the laboratory and tested for corrosion behavior. Interestingly, the paint prepared out of Fe2O3-0 PEG which showed highest corrosion rate (Table 2) was observed to have lowest corrosion rate compared to blank uncoated sample (parent iron sample) and sample coated with paint prepared from microsized α-Fe2O3 (Figure 5).Table 2
Corrosion rate and corrosion resistance data from polarization curves.
Sample code
Corrosion rate(mm/y)
Corrosion resistance(ohm)
Fe2O3-0 PEG
1.24 × 10−4
9.2 × 105
Fe2O3-4 PEG
1.04 × 10−7
2.66 × 109
Fe2O3-8 PEG
2.59 × 10−8
6.916 × 1011
Fe2O3-12 PEG
9.735 × 10−6
2.541 × 107
Microsized Fe2O3 powder
1.574 × 10−3
4.29 × 104
Blank sample
0.4222
225.8Figure 4
Polarization curves of iron samples coated with paints prepared from (A) Fe2O3-0 PEG, (B) Fe2O3-4 PEG, (C) Fe2O3-8 PEG, and (D) Fe2O3-12 PEG.Figure 5
Polarization curves of iron samples: (A) blank sample, (B) sample coated with paint prepared from microsized Fe2O3 powder, and (C) sample coated with paint prepared from Fe2O3-0 PEG.


## 4. Conclusion

This paper outlines the simple method to synthesize nanocrystallineα- and γ-iron oxides by precipitation-calcination method. It was observed that different morphologies of iron oxide were precipitated by varying amounts of PEG, which is acting as a structure directing agent. Interestingly, powder X-ray studies showed a phase transformation from rhombohedral hematite (α-Fe2O3) to cubic maghemite (γ-Fe2O3) when the amount of PEG is increased and calcined at the same temperature (500°C). Scanning electron micrographs clearly shown at low PEG content nanocapsules were formed, which aggregate to form nanocluster on addition of 12 g (0.2 M) of PEG. However, this agglomeration of nanocapsules is also responsible for phase transformation. These prepared iron oxide nanomaterials are further used in paint preparation and were found to be better protective coatings on iron samples when compared to microsized iron oxide particle coatings.



---