# Synthesis and Characteristics of Valeric Acid-Zinc Layered Hydroxide Intercalation Material for Insect Pheromone Controlled Release Formulation

Authors: Rozita Ahmad; Mohd Zobir Hussein; Siti Halimah Sarijo; Wan Rasidah Wan Abdul Kadir; Taufiq-Yap Yun Hin
Journal: Journal of Materials
 (2016)

---

## Abstract

A new intercalation compound of insect pheromone, valeric acid (VA), based on zinc layered hydroxide (ZLH) as host release material, was successfully prepared through coprecipitation method. The as-produced organic-inorganic nanolayered material, valerate nanohybrid, VAN, shows the formation of a new peak at lower 2θ angle with basal spacing of 19.8 Å with no ZnO reflections, which indicate that the intercalation of anion between the inorganic ZLH interlamellae was accomplished. The elemental, FTIR, and ATR analyses of the nanohybrid supported the fact that the intercalation with the percentage anion loading was calculated to be 23.0% (w/w). The thermal stability property of the resulting nanohybrid was enhanced compared to the unbound anion. Field emission scanning electron micrograph of the ZnO has a nonuniform granular structure but transforms into flake-like structure with various sizes after the intercalation process. Release kinetics of anion from the interlayer of intercalated compound exhibited a slow release behavior governed by the pseudo-second-order kinetic model at different pHs of aqueous media. The valerate anion was released from VAN with the highest release rate at pH 4. These findings provide the basis to further development of controlled release formulation for insect pheromone based on ZLH intercalation.


---

## Body

## 1. Introduction

Controlled release materials acting as host and delivery system for many active ingredients such as drugs, fertilizers, pesticides, and cosmetic agents have gained high interest due to their multiple functionalities. These include protecting the active agents from degradation, increase stability of the chemical, and prevent loss through leaching or evaporation and prolonged activity duration of an active agent. Furthermore, they prevent an active agent from direct contact with human or surroundings and reduce multiple application which promotes safe environment.The use of pheromone as alternative to chemical insecticide was reported to be one of the potential biopesticides for insect control [1]. However, the environmental factors such as heat, sunlight, and rainfall could affect the pheromone release. Insect pheromone contains volatile compounds and is unstable due to degradation and isomerization at ambient temperature or in the presence of light [2]. Thus, a suitable encapsulated material is required to minimise the environmental related problem.Intense research has been carried out in employing layered metal hydroxide (LMH) as controlled release formulations for various applications such as herbicide [3], flame retardant [4], UV absorbers [5], drug carrier [6], and anticorrosion agent [7] due to anion exchangeable reactions. Layered metal hydroxides compounds can be classified into three groups based on their formula structure. They are layered double hydroxides (LDH), hydroxyl double salts (HDS), and layered hydroxide salt (LHS). LDH is group of compounds comprised of two metal cations, either one monovalent or one divalent and one trivalent cations. LDH can be expressed by the general formula, M2+1-xM3+xOH2x+  Am-x/m·nH2O. HDS contain two types of divalent metal cations and the composition is expressed as M2+1-xMe2+1+xOH31-yAm-(1+3y)/m·nH2O. LHS is also known as layered single-metal hydroxide group which consists of only one type of divalent metal cation and is represented by M2+OH2-xAn-x/n·nH2O, where M2+ denotes the divalent metallic cations such as Mg2+, Zn2+, Ni2+, Cu2+, Mn2+, and Co2+ and M3+ represents the trivalent metallic cations such as Al3+, Fe3+, Co3+, and Cr3+. Am- is interlayer anions that can be organic or inorganic molecules with negative charge and m neutralizes the positive charge of the cations.Zinc layered hydroxide (ZLH) is a type of LHS, comprised of zinc as the metal cation in which only zinc and hydroxyl represent the inorganic layers. ZLH structure is comprised of 2 parts: positively charged brucite-like inorganic layers and exchangeable anions and water molecules in the interlayer. The positively charged inorganic layer is electrically balanced by the negative charged anions and water molecules enable the accommodation of functional anion between the interlayer regions. The stacking layers of ZLH interlaying with anionic layers can form a nanocomposite material with high stability and controllable functionalities [8]. The interlayer anions can be exchanged with various organic and inorganic charged compounds. ZLH is an interesting host nanomaterial due to the fact that its anion exchange ability has led to the formation of various nanocomposite materials in multiple applications such as catalyst host [9], surfactant nanomaterial [10], and sensors and photoelectrical devices [11].Intercalation of anion between the interlayer spacings of ZLH can be achieved using various techniques. There are various methods reported for the preparation of ZLH nanohybrid such as urea hydrolysis [12], pulse laser-ablation technique [10], exfoliation-restacking route method [9], and chemical bath deposition [13]. Coprecipitation technique which is among the simple synthesis methods that employ less chemical with fewer preparation steps has been frequently adopted in the ZLH nanocomposite synthesis [14, 15]. Furthermore, this method uses normal laboratory equipment and no dedicated complex instrumental setup is required. In anion exchange method, the ZLH matrices need to be preprepared into solid form before mixing with the active agent [16]. The coprecipitation methods have been studied in the synthesis of ZLH nanohybrid as carrier for herbicides [17, 18], drugs [19], and UV-absorber [20, 21].To date, research on ZLH as nanocarrier for insect pheromone has not yet been reported elsewhere. Due to this reason and relatively few works reported for nonaromatic or aliphatic carboxylic acid type [22, 23], we have chosen valeric acid (VA), an insect pheromone with low melting point existing in colorless liquid to be intercalated into ZLH, and discuss our investigation here. Valeric acid, a linear carboxylic compound as guest anion, was intercalated into the interlayer region of the ZLH as a host material by coprecipitation method for the formation of a two-dimensional organic-inorganic nanohybrid structure, VAN. Furthermore, to the best of our knowledge no such work on the intercalation of liquid pheromone into any ZLH has been accomplished, and therefore it is worth looking into. In this study, we report the physicochemical properties of the resulting nanohybrid VAN and further investigate the release behavior of valerate anions into the aqueous media at various pHs.


## 2. Experimental

### 2.1. Synthesis of Nanohybrid

All chemicals used in this experiment were obtained from various chemical suppliers and used without any further purification. All solutions were prepared using deionized water. About 0.10 g of ZnO was suspended into 100 mL deionized water and was stirred on a magnetic stirrer for 15 minutes. Valeric acid solution (0.5 M) was prepared by mixing 5.60 mL in 20 mL ethanol and adjusted to 100 mL with deionized water in a volumetric flask. The VA solution was then added dropwise into ZnO suspension with constant stirring, producing a clear mixed solution. pH of the solution was adjusted to 7.9 using 0.5 M NaOH aqueous solution to obtain white precipitate. The slurry solution was vigorously stirred using a magnetic stirrer for 3 h at room temperature and continued for 18 h at 70°C. The as-synthesized product was centrifuged, thoroughly washed with deionized water, and dried in an oven at 70°C. The resulting material was ground into fine powder for further use and characterization.


### 2.2. Characterization

Powder X-ray diffraction patterns of the nanohybrid were obtained at 2–60° on a Shimadzu Diffractometer XRD-6000 using CuKα radiation (λ = 1.5418 Å) and dwell time of 4 degrees per minute. Fourier transform infrared (FTIR) spectra were recorded over the range of 400–4000 cm−1 on a Perkin Elmer 1725X Spectrophotometer using the KBr disc method. Attenuated total reflectance (ATR) method was employed on a Perkin Elmer Spectrum 100 FTIR Spectrometer to determine the functional groups present in valeric acid, since it is liquid in nature. The carbon and hydrogen composition was analysed by a CHNS analyzer, model Thermofinnigan Flash 2000 series. The amount of Zn in the sample was extracted with mineral acids and its concentration was determined by a Varian 725-OES inductive coupled plasma optical emission spectrometer. Thermogravimetry and differential thermogravimetry measurements were recorded using a Mettler Toledo instrument at heating rate of 10°C/minute in the range of 28–1000°C. The surface morphology analysis of the synthesized nanohybrid was captured on a field emission scanning electron microscope, model JEOL JSM-7600.


## 2.1. Synthesis of Nanohybrid

All chemicals used in this experiment were obtained from various chemical suppliers and used without any further purification. All solutions were prepared using deionized water. About 0.10 g of ZnO was suspended into 100 mL deionized water and was stirred on a magnetic stirrer for 15 minutes. Valeric acid solution (0.5 M) was prepared by mixing 5.60 mL in 20 mL ethanol and adjusted to 100 mL with deionized water in a volumetric flask. The VA solution was then added dropwise into ZnO suspension with constant stirring, producing a clear mixed solution. pH of the solution was adjusted to 7.9 using 0.5 M NaOH aqueous solution to obtain white precipitate. The slurry solution was vigorously stirred using a magnetic stirrer for 3 h at room temperature and continued for 18 h at 70°C. The as-synthesized product was centrifuged, thoroughly washed with deionized water, and dried in an oven at 70°C. The resulting material was ground into fine powder for further use and characterization.


## 2.2. Characterization

Powder X-ray diffraction patterns of the nanohybrid were obtained at 2–60° on a Shimadzu Diffractometer XRD-6000 using CuKα radiation (λ = 1.5418 Å) and dwell time of 4 degrees per minute. Fourier transform infrared (FTIR) spectra were recorded over the range of 400–4000 cm−1 on a Perkin Elmer 1725X Spectrophotometer using the KBr disc method. Attenuated total reflectance (ATR) method was employed on a Perkin Elmer Spectrum 100 FTIR Spectrometer to determine the functional groups present in valeric acid, since it is liquid in nature. The carbon and hydrogen composition was analysed by a CHNS analyzer, model Thermofinnigan Flash 2000 series. The amount of Zn in the sample was extracted with mineral acids and its concentration was determined by a Varian 725-OES inductive coupled plasma optical emission spectrometer. Thermogravimetry and differential thermogravimetry measurements were recorded using a Mettler Toledo instrument at heating rate of 10°C/minute in the range of 28–1000°C. The surface morphology analysis of the synthesized nanohybrid was captured on a field emission scanning electron microscope, model JEOL JSM-7600.


## 3. Controlled Release Study

The controlled release study of VA from the nanohybrid into the aqueous media was determined by distilled water at pHs 4, 6.5, and 8. The pH was adjusted by either HCl or NaOH. About 2 mg of the intercalated compound was placed in a cuvette containing 3.5 mL of aqueous solution. The study was carried outin situin which the accumulated amount of VA released is automatically recorded at every 30 seconds at λmax 205 nm using a Perkin Elmer UV-Visible Spectrophotometer, Lamda 35. The analysis was done continuously until the equilibrium stage was achieved. The data of the release was fitted to pseudo-first order, pseudo-second order, and parabolic diffusion kinetics models. All the aqueous media and Zn2+ from ZnO solution have no interference at λmax 205 nm. After the controlled release, the pH 4, 6.5, and 8 solutions were filtered through Whatman filter paper number 2. The filtrate was analysed using ICP-OES to determine Zn2+ content to detect dissolution of ZLH layer from VAN.


## 4. Results and Discussion

### 4.1. Powder X-Ray Diffraction and Surface Morphology

Figure1 shows the PXRD patterns for zinc oxide and VAN. ZnO exhibits a distinctive pattern with five sharp reflections at 2θ = 30–60° region, corresponding to 100, 002, 101, 102, and 110 lattice planes which indicate high crystallinity of the precursor. Previous studies of ZLH intercalated with nitrate ions show sharp diffraction peak with basal spacing of 9.6–9.9 Å recorded around 2θ = 9.3 due to the 200 planes of the monoclinic structure [24, 25]. The basal reflections of VAN are shifted to lower 2θ with d-spacings of 19.8 Å, 9.9 Å, and 6.6 Å. This indicated that intercalation of valerate anion into interlayer space of ZLH has occurred. The evenly d-spacing values of these reflection peaks with ratio of 1, 2, and 3, respectively, indicated a well formation and orderly stacked interlayer of the new nanohybrid VAN. The absence of the intense peaks of ZnO phase suggested that VAN is a pure phase, in which the ZnO phase was completely transformed to ZLH [26] and evident to the successful intercalation of the guest anion, valeric acid has been accomplished. The surface morphologies for ZnO and VAN are presented in Figure 2. Zinc oxide has a nonuniform granular structure without any specific shapes. The formation of VAN resulted in a morphology transformation into nonuniform flaky shapes with no specific structures.Figure 1
PXRD patterns of ZnO and the nanohybrid VAN prepared at 0.5 M VA.Figure 2
FESEM images of (a) ZnO at 50,000, (b) VAN at 10,000, and (c) VAN at 50,000 magnification.
(a) (b) (c)


### 4.2. Spatial Orientation of Guest Anion between ZLH Interlayers

Intercalation of the guest anion between the metal hydroxide layers resulted in an increase of basal spacing due to the dimension and spatial arrangement of the organic moiety in the interlamellae of host material, ZLH. The dimensional size of VA was determined using the Chemoffice Software Ultra, 2008, 11.01. Figure3(a) shows the three-dimensional molecular size of VA with x-, y-, and z-axis to be 7.2, 8.7, and 4.9 Å, respectively. Using the average basal spacing of 19.8 Å for VAN obtained from PXRD study, the interlayer space for anion can be estimated. With the thickness of ZLH layer being 4.8 Å [26] and 2.6 Å for each zinc tetrahedron, the gallery space available is calculated to be 9.8 Å. Therefore, the suggested spatial orientation for the VA anion between the ZLH interlayers as bilayer arrangement is illustrated in Figure 3(b). The gallery space of 9.8 Å permits two VA anions to be positioned superimposed from z-axis and arranged in bilayer stacking. This fitted nicely twice the thickness of VA molecules, 4.9 Å.Figure 3
(a) Three-dimensional molecular structure of VA and (b) spatial orientation of valerate in ZLH inorganic interspacing.
(a) (b)


### 4.3. FTIR and ATR Spectroscopy

FTIR spectra for ZnO and VAN synthesized using 0.5 mol/L VA are shown in Figures4(a) and 4(b), respectively. The absorption bands for valeric acid and its nanohybrid VAN are highlighted in Table 1. FTIR spectra of ZnO in Figure 3(a) showed a single strong band at 376 cm−1 due to the vibration of zinc and oxygen sublattices [27]. ATR spectrum of VA in Figure 4(c) portrayed a sharp band at 1712 cm−1 due to the C=O stretching of the carboxylic group.Table 1
ATR and FTIR absorption bands with functional group assignment for VA and VAN.
Assignments VA VAN ν  (O-H) — 3380 ν (CH2) 2964 2957 ν (C=O) in COOH 1712 — ν a s y m (COO−) — 1545 ν (C-O) in carboxylic group 1362 1370 δ (O-H) 1222 — ν (C-O) in carboxylic group 1093 — Stretching (C-O) in COO− — 1013Figure 4
FTIR spectra of (a) ZnO, (b) VAN, and (c) ATR spectra of VA.Valeric acid also exhibits two other intense peaks recorded at 1362 and 1222 cm−1 which are attributed to C-O of carboxylic bond and OH bending [28], respectively. A weak band observed at 2964 cm−1 can be assigned to CH2 stretching of the methylene group of linear-chain carboxylic acids.The FTIR spectrum of VAN depicted in Figure4(b) showed that most of the vibrations are similar to the free anion VA (Figure 4(c)). However, due to the intercalation process, some of the peaks in VAN are observed to be slightly shifted from the original position of pure VA as a result of the interaction process of VA anion into the ZLH interlayer. This is observed for bands from CH2 stretching and C-O asymmetric stretching which are shifted from 2964 to 2957 cm−1 and 1362 to 1370 cm−1, respectively. The shift is due to the presence of VA anions between the host interspacings. On the other hand, the distinctive peak for C=O stretching vibration associated for COOH functional group [29] at 1712 cm−1 was not found in VAN spectrum. This C=O stretching band in valeric acid disappears after intercalation confirms that the anion was intercalated into ZLH layers which are in the anionic form of valeric acid, that is, valerate [29, 30]. A strong absorption band at 1545 cm−1 assigned for the antisymmetric carboxylate stretching indicates that there is an interaction between valerate anion and ZLH layers [30].The presence of a broadband at 3380 cm−1 designated for OH group with O-H stretching vibration represents the adsorbed interlayer water [29]. ZnO band at the lower frequencies, 376 cm−1, has subsided in VAN spectrum, suggesting that successful intercalation has occurred and all the ZnO has transformed into ZLH, resulting in the formation of VAN. The FTIR results which correspond with the PXRD pattern observed in Figure 1 supported the intercalation process of VA into the interlayer of zinc layered hydroxide.


### 4.4. Thermal Analysis

Figure5 shows the TGA-DTG thermograms for pure ZnO, valeric acid, and VAN. For ZnO, a small weight loss of 0.4% was observed between 243.5 and 257.9°C with no maximum temperature indicating that this precursor is a very stable compound. A single weight loss of 99.3% was observed for valeric acid with maximum temperature occurring at 182.4°C compared to 207.6°C for VAN with weight loss of 15.5%. The decomposition temperature of VA intercalated inside the ZLH inorganic interlayer is higher compared to its counterpart anion. This suggests that the thermal stability of the VA in the nanohybrid is enhanced due to interaction with ZLH host. The intercalation process resulted in the formation of electrostatic reaction between the guest anion and the inorganic ZLH layers [31].Figure 5
TGA-DTG thermograms of (a) ZnO, (b) VA, and (c) VAN.
(a)
ZnO (b)
VA (c)
VANThe thermogram of VAN occurred in four stages of weight loss between 59.4 and 425.6°C. Table2 reports on the maximum temperature and weight loss of VAN. The first two peaks of thermal decomposition were observed at temperature ranging from 59.4°C to 80.4°C and from 108.8°C to 111.2°C with weight loss of 5.5 and 6.4%, respectively. These weight losses are due to elimination of surface-physisorbed water and bonded water molecules [32].Table 2
Maximum temperature and weight loss of VAN from TGA-DTG thermograms.
Peak Maximum temperature (°C) Weight loss (%) 1 37.4 5.5 2 111.8 6.4 3 207.6 15.5 4 399.2 6.4The other stages of weight loss were contributed to the decomposition of organic moiety, VA anion, observed in 171.8–230.8°C region. The maximum temperature was detected at 207.6°C with corresponding weight loss of 15.5% due to the degradation of intercalated VA between the inorganic ZLH layers. The intercalated compound was further degraded to 6.4% at temperature range of 357.3–425.6°C. Further degradation occurs at temperature between 177.8 and 425.6°C with total weight loss of 21.9%. This result is close to the percentage anion loading of VA in VAN determined by CHNS, with a value of 23.0% as shown in Table3. Chemical composition analysis (CHNS) revealed that VAN contained 13.5% carbon (w/w) which gave the percentage valerate anion loading in VAN nanohybrid calculated to be 23.0%. The percentage of valerate anion loading gave an indication of the degree of intercalation of guest anion in the ZLH host [29]. ICP-OES determination detected 38.3% (w/w) of Zn in VAN. Therefore, the formula of VAN was proposed as Zn0.6(OH)1.77(CH3CH2CH2CH2COO−)0.23.0.66H2O.Table 3
Chemical composition of VAN and percentage anion loading.
Sample C (%w/w) Zn (% w/w) Anion loading (% w/w) VAN 13.5 38.3 23.0


### 4.5. Release Behavior of Valerate Anions

The controlled release study was carried out using distilled water at pHs 4, 6.5, and 8 to investigate the effect of different pH on the release behavior of valeric acid from ZLH intergallery. pH 4 and pH 8 were chosen to simulate the pH of acidic and alkaline soil. The release profiles of anion VA from the intergallery VAN into the release media are shown in Figure6. The release rate of VA was found to be faster in the first 300 mins followed by a slower one, thereafter. In the first 300 mins, about 32, 22, and 28% of VA were released into pH 4, 6.5, and 8 aqueous solution, respectively. The fast release could be supported by the “burst effect” mechanism from the high release of adsorbed VA anions on the surface of inorganic layer ZLH [13]. Equilibrium stage was achieved after 1200 mins with maximum amount release recorded of 41, 27, and 33% in the pH 4, 6.5, and 8 aqueous solution, respectively.Figure 6
Release profiles of valeric acid from its nanohybrid, VAN interlayers into distilled water at pHs 4, 6.5, and 8.The release rate of VA into the aqueous media can be arranged in the order of pH 4 > pH 8 > pH 6.5. Low and high pH of aqueous solution cause partial dissolution of ZLH due to the collapse of the inorganic layer structure [16] which resulted in the release of VA into the acidic and basic aqueous media. In this work, the aqueous solution of pH 4 and pH 8 contains 19.91 ppm and 11.32 ppm Zn2+, respectively, as shown in Table 4. This implies that ZLH is not stable in low and high pHs and dissolution of the ZLH matrix affects the composition amount of VA released from the host, ZLH. ZLH which is more stable at pH 6.5 causes the release process of VA to be slower in comparison with the aqueous media at pH 4 and pH 8 aqueous media. The concentration of Zn2+ in the aqueous media at pH 6.5 after the controlled release is 5.15 ppm. It was found that the full release of VA did not happen as the saturated release was only achieved below 45%. This could be due to the strongly held VA anions by the positively charged layered host, resulting in the low release of VA into the aqueous solution [15].Table 4
Concentration of Zn (ppm) in the aqueous media at pH 4, pH 6.5, and pH 8.
Aqueous media pH 4 pH 6.5 pH 8 Content 19.91 5.15 11.32


### 4.6. Release Kinetics of Anions from VAN Intercalation Compound

To determine the release mechanism of VA from the nanohybrid, the controlled release data of VAN were fitted to several kinetic models, namely, pseudo-first order (In(qe-qt)=Inqe-k1t) [30] and pseudo-second order (t/qt=1/k2qe2+t/qe) [33] and parabolic diffusion ((1-Mt/Mo)/t=kt-0.5+b) [32], where qe and qt denote the equilibrium release amount and release amount of anion at any time, t, respectively. k is the apparent release rate constant while Mo and Mt denote the anion remaining in the ZLH at zero time and release time, t, respectively. The corresponding linear correlation coefficient, r2, value closest to 1, was used as a guide to the selection of the best fit kinetic model that describes the kinetic release of anion from VAN.The pseudo-first order which describes the release is dependent on the dissolution of the host material, while the parabolic diffusion emphasizes on the diffusion-controlled process such as intraparticle diffusion or surface diffusion [34, 35]. Figure 7 shows plots of the fitting of valerate anions released from VAN while Table 5 reports on the results of fitting to the various kinetic models. The correlation coefficient, r2, was found to be close to 1 when the data were fitted into pseudo-second-order kinetic model. This suggests that the release of valerate anion from the VAN was best expressed by the pseudo-second-order kinetic model. The release of valerate anion from the interlayer space is due to dissolution of VAN as well as ion exchange between valerate anions and the anions present in the aqueous media. In pH 4 and pH 8 solution, valerate anion was ion exchanged with Cl− and OH− due to the addition of HCL and NaOH, respectively [36]. In pH 6.5 solution, anion exchange between valerate ion and carbonate ion may occur due to the dissolution of carbon dioxide from the atmosphere in distilled water [37]. The highest release rate value, k, of VA released into various pH media solutions is obtained in pH 4 media (2.49 × 10−5mg/min) as shown in Table 5. This is agreeable to the highest saturated release values of 41% VA in pH 4 which suggested that the release of VA from intercalated compound into pH 4 is the fastest compared to pH 6.5 and pH 8. VA release from VAN into pH 6.5 solution has the lowest k rate that releases small amount of VA before equilibrium stage is achieved.Table 5
Parameters derived from the fitting of the data obtained from the release of VA from VAN intercalation compound into various pH solutions using parabolic diffusion, pseudo-first-order, and pseudo-second-order kinetic expression.
pH Saturated release (%) Correlation coefficient,r2 Pseudo-second order Pseudo-first order Pseudo-second order Parabolic diffusion Rate constant,k (mg/min) × 10−5 4 41 0.9921 0.9984 0.9336 2.49 6.5 27 0.9740 0.9989 0.9325 1.48 8 33 0.9871 0.9968 0.9625 1.87Figure 7
Fitting the data of valeric acid released from its intercalation compound into distilled water at different pHs using pseudo-first order and pseudo-second order and parabolic diffusion models at (a–c) pH 4, (d-e) pH 6.5, and (g–i) pH 8.
(a)
(Pseudo-first order) (b)
(Pseudo-second order) (c)
(Parabolic diffusion) (d)
(Pseudo-first order) (e)
(Pseudo-second order) (f)
(Parabolic diffusion) (g)
(Pseudo-first order) (h)
(Pseudo-second order) (i)
(Parabolic diffusion)The release of VA from the intergallery of its organic-inorganic nanohybrid at various pHs was found to behave in a controlled manner governed by the pseudo-second-order kinetic rate expression. However, full release of VA into the release media was not achieved within the observed period, due to the strong electrostatic interaction of valerate anion and the positively charged ZLH interlayer, which affect the release process.


## 4.1. Powder X-Ray Diffraction and Surface Morphology

Figure1 shows the PXRD patterns for zinc oxide and VAN. ZnO exhibits a distinctive pattern with five sharp reflections at 2θ = 30–60° region, corresponding to 100, 002, 101, 102, and 110 lattice planes which indicate high crystallinity of the precursor. Previous studies of ZLH intercalated with nitrate ions show sharp diffraction peak with basal spacing of 9.6–9.9 Å recorded around 2θ = 9.3 due to the 200 planes of the monoclinic structure [24, 25]. The basal reflections of VAN are shifted to lower 2θ with d-spacings of 19.8 Å, 9.9 Å, and 6.6 Å. This indicated that intercalation of valerate anion into interlayer space of ZLH has occurred. The evenly d-spacing values of these reflection peaks with ratio of 1, 2, and 3, respectively, indicated a well formation and orderly stacked interlayer of the new nanohybrid VAN. The absence of the intense peaks of ZnO phase suggested that VAN is a pure phase, in which the ZnO phase was completely transformed to ZLH [26] and evident to the successful intercalation of the guest anion, valeric acid has been accomplished. The surface morphologies for ZnO and VAN are presented in Figure 2. Zinc oxide has a nonuniform granular structure without any specific shapes. The formation of VAN resulted in a morphology transformation into nonuniform flaky shapes with no specific structures.Figure 1
PXRD patterns of ZnO and the nanohybrid VAN prepared at 0.5 M VA.Figure 2
FESEM images of (a) ZnO at 50,000, (b) VAN at 10,000, and (c) VAN at 50,000 magnification.
(a) (b) (c)


## 4.2. Spatial Orientation of Guest Anion between ZLH Interlayers

Intercalation of the guest anion between the metal hydroxide layers resulted in an increase of basal spacing due to the dimension and spatial arrangement of the organic moiety in the interlamellae of host material, ZLH. The dimensional size of VA was determined using the Chemoffice Software Ultra, 2008, 11.01. Figure3(a) shows the three-dimensional molecular size of VA with x-, y-, and z-axis to be 7.2, 8.7, and 4.9 Å, respectively. Using the average basal spacing of 19.8 Å for VAN obtained from PXRD study, the interlayer space for anion can be estimated. With the thickness of ZLH layer being 4.8 Å [26] and 2.6 Å for each zinc tetrahedron, the gallery space available is calculated to be 9.8 Å. Therefore, the suggested spatial orientation for the VA anion between the ZLH interlayers as bilayer arrangement is illustrated in Figure 3(b). The gallery space of 9.8 Å permits two VA anions to be positioned superimposed from z-axis and arranged in bilayer stacking. This fitted nicely twice the thickness of VA molecules, 4.9 Å.Figure 3
(a) Three-dimensional molecular structure of VA and (b) spatial orientation of valerate in ZLH inorganic interspacing.
(a) (b)


## 4.3. FTIR and ATR Spectroscopy

FTIR spectra for ZnO and VAN synthesized using 0.5 mol/L VA are shown in Figures4(a) and 4(b), respectively. The absorption bands for valeric acid and its nanohybrid VAN are highlighted in Table 1. FTIR spectra of ZnO in Figure 3(a) showed a single strong band at 376 cm−1 due to the vibration of zinc and oxygen sublattices [27]. ATR spectrum of VA in Figure 4(c) portrayed a sharp band at 1712 cm−1 due to the C=O stretching of the carboxylic group.Table 1
ATR and FTIR absorption bands with functional group assignment for VA and VAN.
Assignments VA VAN ν  (O-H) — 3380 ν (CH2) 2964 2957 ν (C=O) in COOH 1712 — ν a s y m (COO−) — 1545 ν (C-O) in carboxylic group 1362 1370 δ (O-H) 1222 — ν (C-O) in carboxylic group 1093 — Stretching (C-O) in COO− — 1013Figure 4
FTIR spectra of (a) ZnO, (b) VAN, and (c) ATR spectra of VA.Valeric acid also exhibits two other intense peaks recorded at 1362 and 1222 cm−1 which are attributed to C-O of carboxylic bond and OH bending [28], respectively. A weak band observed at 2964 cm−1 can be assigned to CH2 stretching of the methylene group of linear-chain carboxylic acids.The FTIR spectrum of VAN depicted in Figure4(b) showed that most of the vibrations are similar to the free anion VA (Figure 4(c)). However, due to the intercalation process, some of the peaks in VAN are observed to be slightly shifted from the original position of pure VA as a result of the interaction process of VA anion into the ZLH interlayer. This is observed for bands from CH2 stretching and C-O asymmetric stretching which are shifted from 2964 to 2957 cm−1 and 1362 to 1370 cm−1, respectively. The shift is due to the presence of VA anions between the host interspacings. On the other hand, the distinctive peak for C=O stretching vibration associated for COOH functional group [29] at 1712 cm−1 was not found in VAN spectrum. This C=O stretching band in valeric acid disappears after intercalation confirms that the anion was intercalated into ZLH layers which are in the anionic form of valeric acid, that is, valerate [29, 30]. A strong absorption band at 1545 cm−1 assigned for the antisymmetric carboxylate stretching indicates that there is an interaction between valerate anion and ZLH layers [30].The presence of a broadband at 3380 cm−1 designated for OH group with O-H stretching vibration represents the adsorbed interlayer water [29]. ZnO band at the lower frequencies, 376 cm−1, has subsided in VAN spectrum, suggesting that successful intercalation has occurred and all the ZnO has transformed into ZLH, resulting in the formation of VAN. The FTIR results which correspond with the PXRD pattern observed in Figure 1 supported the intercalation process of VA into the interlayer of zinc layered hydroxide.


## 4.4. Thermal Analysis

Figure5 shows the TGA-DTG thermograms for pure ZnO, valeric acid, and VAN. For ZnO, a small weight loss of 0.4% was observed between 243.5 and 257.9°C with no maximum temperature indicating that this precursor is a very stable compound. A single weight loss of 99.3% was observed for valeric acid with maximum temperature occurring at 182.4°C compared to 207.6°C for VAN with weight loss of 15.5%. The decomposition temperature of VA intercalated inside the ZLH inorganic interlayer is higher compared to its counterpart anion. This suggests that the thermal stability of the VA in the nanohybrid is enhanced due to interaction with ZLH host. The intercalation process resulted in the formation of electrostatic reaction between the guest anion and the inorganic ZLH layers [31].Figure 5
TGA-DTG thermograms of (a) ZnO, (b) VA, and (c) VAN.
(a)
ZnO (b)
VA (c)
VANThe thermogram of VAN occurred in four stages of weight loss between 59.4 and 425.6°C. Table2 reports on the maximum temperature and weight loss of VAN. The first two peaks of thermal decomposition were observed at temperature ranging from 59.4°C to 80.4°C and from 108.8°C to 111.2°C with weight loss of 5.5 and 6.4%, respectively. These weight losses are due to elimination of surface-physisorbed water and bonded water molecules [32].Table 2
Maximum temperature and weight loss of VAN from TGA-DTG thermograms.
Peak Maximum temperature (°C) Weight loss (%) 1 37.4 5.5 2 111.8 6.4 3 207.6 15.5 4 399.2 6.4The other stages of weight loss were contributed to the decomposition of organic moiety, VA anion, observed in 171.8–230.8°C region. The maximum temperature was detected at 207.6°C with corresponding weight loss of 15.5% due to the degradation of intercalated VA between the inorganic ZLH layers. The intercalated compound was further degraded to 6.4% at temperature range of 357.3–425.6°C. Further degradation occurs at temperature between 177.8 and 425.6°C with total weight loss of 21.9%. This result is close to the percentage anion loading of VA in VAN determined by CHNS, with a value of 23.0% as shown in Table3. Chemical composition analysis (CHNS) revealed that VAN contained 13.5% carbon (w/w) which gave the percentage valerate anion loading in VAN nanohybrid calculated to be 23.0%. The percentage of valerate anion loading gave an indication of the degree of intercalation of guest anion in the ZLH host [29]. ICP-OES determination detected 38.3% (w/w) of Zn in VAN. Therefore, the formula of VAN was proposed as Zn0.6(OH)1.77(CH3CH2CH2CH2COO−)0.23.0.66H2O.Table 3
Chemical composition of VAN and percentage anion loading.
Sample C (%w/w) Zn (% w/w) Anion loading (% w/w) VAN 13.5 38.3 23.0


## 4.5. Release Behavior of Valerate Anions

The controlled release study was carried out using distilled water at pHs 4, 6.5, and 8 to investigate the effect of different pH on the release behavior of valeric acid from ZLH intergallery. pH 4 and pH 8 were chosen to simulate the pH of acidic and alkaline soil. The release profiles of anion VA from the intergallery VAN into the release media are shown in Figure6. The release rate of VA was found to be faster in the first 300 mins followed by a slower one, thereafter. In the first 300 mins, about 32, 22, and 28% of VA were released into pH 4, 6.5, and 8 aqueous solution, respectively. The fast release could be supported by the “burst effect” mechanism from the high release of adsorbed VA anions on the surface of inorganic layer ZLH [13]. Equilibrium stage was achieved after 1200 mins with maximum amount release recorded of 41, 27, and 33% in the pH 4, 6.5, and 8 aqueous solution, respectively.Figure 6
Release profiles of valeric acid from its nanohybrid, VAN interlayers into distilled water at pHs 4, 6.5, and 8.The release rate of VA into the aqueous media can be arranged in the order of pH 4 > pH 8 > pH 6.5. Low and high pH of aqueous solution cause partial dissolution of ZLH due to the collapse of the inorganic layer structure [16] which resulted in the release of VA into the acidic and basic aqueous media. In this work, the aqueous solution of pH 4 and pH 8 contains 19.91 ppm and 11.32 ppm Zn2+, respectively, as shown in Table 4. This implies that ZLH is not stable in low and high pHs and dissolution of the ZLH matrix affects the composition amount of VA released from the host, ZLH. ZLH which is more stable at pH 6.5 causes the release process of VA to be slower in comparison with the aqueous media at pH 4 and pH 8 aqueous media. The concentration of Zn2+ in the aqueous media at pH 6.5 after the controlled release is 5.15 ppm. It was found that the full release of VA did not happen as the saturated release was only achieved below 45%. This could be due to the strongly held VA anions by the positively charged layered host, resulting in the low release of VA into the aqueous solution [15].Table 4
Concentration of Zn (ppm) in the aqueous media at pH 4, pH 6.5, and pH 8.
Aqueous media pH 4 pH 6.5 pH 8 Content 19.91 5.15 11.32


## 4.6. Release Kinetics of Anions from VAN Intercalation Compound

To determine the release mechanism of VA from the nanohybrid, the controlled release data of VAN were fitted to several kinetic models, namely, pseudo-first order (In(qe-qt)=Inqe-k1t) [30] and pseudo-second order (t/qt=1/k2qe2+t/qe) [33] and parabolic diffusion ((1-Mt/Mo)/t=kt-0.5+b) [32], where qe and qt denote the equilibrium release amount and release amount of anion at any time, t, respectively. k is the apparent release rate constant while Mo and Mt denote the anion remaining in the ZLH at zero time and release time, t, respectively. The corresponding linear correlation coefficient, r2, value closest to 1, was used as a guide to the selection of the best fit kinetic model that describes the kinetic release of anion from VAN.The pseudo-first order which describes the release is dependent on the dissolution of the host material, while the parabolic diffusion emphasizes on the diffusion-controlled process such as intraparticle diffusion or surface diffusion [34, 35]. Figure 7 shows plots of the fitting of valerate anions released from VAN while Table 5 reports on the results of fitting to the various kinetic models. The correlation coefficient, r2, was found to be close to 1 when the data were fitted into pseudo-second-order kinetic model. This suggests that the release of valerate anion from the VAN was best expressed by the pseudo-second-order kinetic model. The release of valerate anion from the interlayer space is due to dissolution of VAN as well as ion exchange between valerate anions and the anions present in the aqueous media. In pH 4 and pH 8 solution, valerate anion was ion exchanged with Cl− and OH− due to the addition of HCL and NaOH, respectively [36]. In pH 6.5 solution, anion exchange between valerate ion and carbonate ion may occur due to the dissolution of carbon dioxide from the atmosphere in distilled water [37]. The highest release rate value, k, of VA released into various pH media solutions is obtained in pH 4 media (2.49 × 10−5mg/min) as shown in Table 5. This is agreeable to the highest saturated release values of 41% VA in pH 4 which suggested that the release of VA from intercalated compound into pH 4 is the fastest compared to pH 6.5 and pH 8. VA release from VAN into pH 6.5 solution has the lowest k rate that releases small amount of VA before equilibrium stage is achieved.Table 5
Parameters derived from the fitting of the data obtained from the release of VA from VAN intercalation compound into various pH solutions using parabolic diffusion, pseudo-first-order, and pseudo-second-order kinetic expression.
pH Saturated release (%) Correlation coefficient,r2 Pseudo-second order Pseudo-first order Pseudo-second order Parabolic diffusion Rate constant,k (mg/min) × 10−5 4 41 0.9921 0.9984 0.9336 2.49 6.5 27 0.9740 0.9989 0.9325 1.48 8 33 0.9871 0.9968 0.9625 1.87Figure 7
Fitting the data of valeric acid released from its intercalation compound into distilled water at different pHs using pseudo-first order and pseudo-second order and parabolic diffusion models at (a–c) pH 4, (d-e) pH 6.5, and (g–i) pH 8.
(a)
(Pseudo-first order) (b)
(Pseudo-second order) (c)
(Parabolic diffusion) (d)
(Pseudo-first order) (e)
(Pseudo-second order) (f)
(Parabolic diffusion) (g)
(Pseudo-first order) (h)
(Pseudo-second order) (i)
(Parabolic diffusion)The release of VA from the intergallery of its organic-inorganic nanohybrid at various pHs was found to behave in a controlled manner governed by the pseudo-second-order kinetic rate expression. However, full release of VA into the release media was not achieved within the observed period, due to the strong electrostatic interaction of valerate anion and the positively charged ZLH interlayer, which affect the release process.


## 5. Conclusion

A new insect pheromone nanohybrid was successfully synthesized by the intercalation of valeric acid, a linear carboxylic group into ZLH interlayer via coprecipitation technique. The resulting nanohybrid material, VAN, has basal spacing of 19.8 Å without any ZnO peaks and implies full transformation of ZnO into the ZLH with bilayer arrangement of the guest anion between the host lattice spacings. The intercalation of VA into ZLH interlayer was supported by FTIR, ATR, and elemental analyses with percentage anion loading of 23.0% and the thermal stability of VA in the nanohybrid was enhanced compared to its counterpart anion. The release of VA anion from VAN behaved in a slow manner due to strong electrostatic interaction between the anion-host lattices governed by diffusion-anion exchange process. These findings provide the basis towards further development of organic-inorganic nanostructured material based on ZLH as host matrices for insect pheromone controlled release formulation.



---

*Source: 1285721-2016-10-25.xml*