# Introduction of Bifunctional Group onto MWNT by Radiation-Induced Graft Polymerization and Its Use as Biosensor-Supporting Materials

Authors: Yu-Jin Lee; Da-Jung Chung; Sang-Hyub Oh; Seong-Ho Choi
Journal: Journal of Nanomaterials
 (2012)

---

## Abstract

A biosensor comprisingtyrosinase immobilized on bifunctionalized multiwalled carbon nanotube (MWNT) supports was prepared for the detection of phenolic compounds in drinks such as red wine and juices. The MWNT supports were prepared by radiation-induced graft polymerization (RIGP) of epoxy-containing glycidyl methacrylate (GMA), to covalently immobilize the tyrosinase, and vinyl ferrocene (VF), which can act as an electron transfer mediator via redox reactions. The bifunctionalized MWNTs were characterized by X-ray photoelectron spectroscopy (XPS), transmission electron microscopy (TEM), and thermogravimetric analysis (TGA). Electrodes prepared with the MWNTs showed increased current with increasing VF content. A biosensor comprising tyrosinase immobilized on the bifunctionalized MWNTs could detect phenol at 0.1–20 mM. Phenolics in red wine and juices were determined using the biosensor after its calibration.


---

## Body

## 1. Introduction

Amperometric enzymatic biosensors are potentially useful in chemical and biomedical analyses, pollution monitoring, biotechnology, and food and agricultural processing [1–3]. They are suitable for biochemical analysis because of their good selectivity, sensitivity, rapid responses, compactness, and reproducible results [4, 5]. However, the electron transfer efficiency of the redox enzymes is poor in the absence of mediator, because the enzymes’ active sites are deeply embedded in the protein. Biosensors’ sensitivities can be significantly improved by the addition of mediators in the sensors’ matrices.Ferrocene and its derivatives have been reported as electron transfer mediators due to their relatively low molecular mass, reversibility, regeneration at low potential, and generation of stable redox forms [6–9]. There has been much research on of the immobilization of electron transfer mediators on electrodes’ surfaces, because low-molecular-weight, soluble mediators can easily diffuse away from an electrode’s surface into the electrolyte if a biosensor is used continuously, significantly decreasing the electron signal and the performance and lifetime of the biosensor. The covalent immobilization of ferrocene derivatives onto electrode supports can reduce this problem.Radiation-induced graft polymerization can introduce specific characteristics to the surface of a functional polymer’s matrix such as thermal stability, mechanical strength, electronic properties, and crystallinity. Enzymatic biosensors have been prepared by the radiation-induced graft polymerization of vinyl monomers with various functional groups onto MWNTs at room temperature [10–14]. The functional groups of the vinyl monomers can be used as physical interaction sites because they have hydrophilic properties compatible with those of the enzyme, allowing their functional groups to interact easily on the surface of the electrode. MWNTs have been used as supporting materials because of their high chemical stability, high surface area, unique electronic properties, and relatively strong mechanical properties [15].Glycidyl methacrylate (GMA) is a monomer that can be easily modified with various functional groups. As it is polymerized, its epoxy groups become available for the introduction of functional groups, such as amines [16], alcohols [17], phosphoric acid [18], and proteins [19, 20]. The epoxy-modified polymer surface is stable over long storage periods and is relatively resistant to hydrolysis. Biomolecules, such as proteins, can be covalently coupled by opening the epoxide bridges in alkaline media.On the other hand, the biosensors based on MWNT for determination of phenolic compounds have been studied by many researchers [4, 21–23]. However, there are no reports about the preparation of MWNTs supporting with bifunctional group using radiation-induced graft polymerization until now.This work reports MWNT supports with epoxy groups, as covalent sites, and ferrocene groups, as electron mediators, prepared by RIGP with various composition of GMA and VF monomers. The resulting MWNT supports were analyzed by X-ray photoelectron spectroscopy (XPS), transmission electron microscopy (TEM), and thermogravimetric analysis (TGA). Electrodes were prepared by hand casting the MWNT supports onto the surface of GC electrodes. Their currents were measured with respect to the relative composition of the GMA and VF monomers. Atyrosinase-immobilized biosensor was prepared by immobilizing tyrosinase in 0.1 M carbonated buffer solution (1.0 mL, pH 9.5) for the detection of phenolic compounds. Its phenol sensing efficiency was evaluated in a phosphate buffer solution. Optimal operating conditions such as pH, temperature, and phenol detection range were evaluated. Total phenolic concentrations in three red wines and twelve juices were then determined using the tyrosinase-modified biosensor.


## 2. Experiment Details

### 2.1. Reagents

Tyrosinase from mushrooms (EC 1.14.18.1), phenol, p-chresol, catechol, glycidyl methacrylate (GMA), and vinyl ferrocene (VF) were from Aldrich-Sigma Chemical Co., MWNTs (CM-95) were from Hanwha Nanotech Co., Ltd., (Republic of Korea). Solutions were prepared with water from a Milli-Q puls water purification system (Millipore Co., Ltd., final resistance, 18.2 M Ω cm−1) that was degassed prior to each measurement. Other chemicals were of reagent grade.


### 2.2. Preparation of a Biosensor ComprisingTyrosinase Immobilized on Bifunctionalized MWNT Supports

Figure1 outlines the preparation of the tyrosinase-immobilized phenol biosensor. The MWNTs were first purified to remove the catalyst and noncrystallized carbon impurities by treatment with phosphate solution. They were then used as the supporting material for grafting binary vinyl monomers: GMA, with epoxy groups, and VF, which can act as an electron transfer mediator via rodox reactions. 0.2 g MWNT and various compositions of the binary vinyl monomers (Table 1) were mixed in methanol (350 mL). Nitrogen gas was bubbled through the solution for 30 min to remove oxygen. The solution was then irradiated by γ-rays from a 60Co source under atmospheric pressure and ambient temperature. 30 kGy was administered at 1.0 × 104 Gy/h. The prepared MWNT supports were dried in a vacuum oven at 50°C, and 3.0 mg was then dissolved in a mixture of DMF (1.0 mL) and water (1.0 mL) to prepare the coating solution. MWNT electrodes were fabricated by hand casting 6.0 μL coating solution onto GC electrodes (0.2 × 0.2 cm) and drying in a vacuum oven at 50°C for 24 hrs. Tyrosinase was covalently immobilized on the epoxy groups of the most suitable MWNT electrode by immersing the electrode in 0.1 M carbonated buffer solution (1.0 mL, pH = 9.5). 1.0 mL base tyrosinase solution was then added to the MWNT electrode in 0.1 M carbonated buffer solution, and the reaction solution was adjusted to pH 9.0 with 0.1 M NaOH. Tyrosinase was immobilized on the electrode by incubation with shaking at 37°C for 20 h. The tyrosinase-immobilized biosensor was rinsed six times with 0.1 M carbonated buffer (pH 8.0) and then twice with acetic acid buffer solution (pH 4.0). The resulting biosensor was stored in phosphate buffer (pH 7.0).Table 1
Properties of the MWNT supports with bifunctional group prepared by RIGPa.
NoFeedGraft yield (%)bFe content (%)cCV current (mA)GMA (mol-%)VF (mol-%)1100020.0—2.27×10-42802030.00.245.60×10-23604015.00.361.21×10-24406020.00.311.83×10-25208020.00.361.09×10-16010025.00.471.33×10-2aReaction condition: MWNT 0.2 g, solvent 350 mL (MeOH).bDetermined by TGA. cDetermined by XPS.Figure 1
Preparationtyrosinase-immobilized biosensor on MWNT supports for the detection of phenolic compounds.


### 2.3. Determination of Phenolic Compounds in Drinks usingTyrosinase-Modified Biosensor

Total concentration of the phenolic compounds for drinks was determined by comparison of calibration curves (see Figure6). In detail, the drop of drinks (0.04 mL) was added in PBS solution (pH 7.0, 3.96 mL), and then the cyclic voltammograms for phenolic compounds using the prepared biosensor were recorded.


### 2.4. Instrumentation

Cyclic voltammograms were measured with a potentiostat/galvanostat (model 283. Ametek PAR, USA) in a conventional three-electrode system. The working electrode was the GC MWNT electrode, the counterelectrode was platinum wire, and the reference electrode was Ag/AgCl (sat’d KCl). Samples’ surface morphologies were determined by HR-TEM (JEOL, JEM-2010, USA). X-ray photoelectron spectra were measured using on a MultiLab ESCA2000 (Thermo Fisher Scientific). Thermal gravimetric analysis (TGA) was conducted on a Scinco TGA S-1000 (Seoul, Republic of Korea) under N2 flow from 25°C to 700°C at a heating rate of 20°C/min.


## 2.1. Reagents

Tyrosinase from mushrooms (EC 1.14.18.1), phenol, p-chresol, catechol, glycidyl methacrylate (GMA), and vinyl ferrocene (VF) were from Aldrich-Sigma Chemical Co., MWNTs (CM-95) were from Hanwha Nanotech Co., Ltd., (Republic of Korea). Solutions were prepared with water from a Milli-Q puls water purification system (Millipore Co., Ltd., final resistance, 18.2 M Ω cm−1) that was degassed prior to each measurement. Other chemicals were of reagent grade.


## 2.2. Preparation of a Biosensor ComprisingTyrosinase Immobilized on Bifunctionalized MWNT Supports

Figure1 outlines the preparation of the tyrosinase-immobilized phenol biosensor. The MWNTs were first purified to remove the catalyst and noncrystallized carbon impurities by treatment with phosphate solution. They were then used as the supporting material for grafting binary vinyl monomers: GMA, with epoxy groups, and VF, which can act as an electron transfer mediator via rodox reactions. 0.2 g MWNT and various compositions of the binary vinyl monomers (Table 1) were mixed in methanol (350 mL). Nitrogen gas was bubbled through the solution for 30 min to remove oxygen. The solution was then irradiated by γ-rays from a 60Co source under atmospheric pressure and ambient temperature. 30 kGy was administered at 1.0 × 104 Gy/h. The prepared MWNT supports were dried in a vacuum oven at 50°C, and 3.0 mg was then dissolved in a mixture of DMF (1.0 mL) and water (1.0 mL) to prepare the coating solution. MWNT electrodes were fabricated by hand casting 6.0 μL coating solution onto GC electrodes (0.2 × 0.2 cm) and drying in a vacuum oven at 50°C for 24 hrs. Tyrosinase was covalently immobilized on the epoxy groups of the most suitable MWNT electrode by immersing the electrode in 0.1 M carbonated buffer solution (1.0 mL, pH = 9.5). 1.0 mL base tyrosinase solution was then added to the MWNT electrode in 0.1 M carbonated buffer solution, and the reaction solution was adjusted to pH 9.0 with 0.1 M NaOH. Tyrosinase was immobilized on the electrode by incubation with shaking at 37°C for 20 h. The tyrosinase-immobilized biosensor was rinsed six times with 0.1 M carbonated buffer (pH 8.0) and then twice with acetic acid buffer solution (pH 4.0). The resulting biosensor was stored in phosphate buffer (pH 7.0).Table 1
Properties of the MWNT supports with bifunctional group prepared by RIGPa.
NoFeedGraft yield (%)bFe content (%)cCV current (mA)GMA (mol-%)VF (mol-%)1100020.0—2.27×10-42802030.00.245.60×10-23604015.00.361.21×10-24406020.00.311.83×10-25208020.00.361.09×10-16010025.00.471.33×10-2aReaction condition: MWNT 0.2 g, solvent 350 mL (MeOH).bDetermined by TGA. cDetermined by XPS.Figure 1
Preparationtyrosinase-immobilized biosensor on MWNT supports for the detection of phenolic compounds.


## 2.3. Determination of Phenolic Compounds in Drinks usingTyrosinase-Modified Biosensor

Total concentration of the phenolic compounds for drinks was determined by comparison of calibration curves (see Figure6). In detail, the drop of drinks (0.04 mL) was added in PBS solution (pH 7.0, 3.96 mL), and then the cyclic voltammograms for phenolic compounds using the prepared biosensor were recorded.


## 2.4. Instrumentation

Cyclic voltammograms were measured with a potentiostat/galvanostat (model 283. Ametek PAR, USA) in a conventional three-electrode system. The working electrode was the GC MWNT electrode, the counterelectrode was platinum wire, and the reference electrode was Ag/AgCl (sat’d KCl). Samples’ surface morphologies were determined by HR-TEM (JEOL, JEM-2010, USA). X-ray photoelectron spectra were measured using on a MultiLab ESCA2000 (Thermo Fisher Scientific). Thermal gravimetric analysis (TGA) was conducted on a Scinco TGA S-1000 (Seoul, Republic of Korea) under N2 flow from 25°C to 700°C at a heating rate of 20°C/min.


## 3. Results and Discussion

### 3.1. Preparation and Characterization of MWNT Supports with Bifunctional Groups

Various vinyl monomers such as acrylic acid, methacrylic acid, glycidyl methacrylate, maleic anhydride, and vinylphenyl boronic acid have previously been grafted onto MWNT surfaces by radiation-induced graft polymerization in aqueous solutions at room temperature [15]. Vinyl monomers were selected for this work because they possess hydrophobic sites to complement the hydrophilic functional groups attached to them. The vinyl groups interacted with the MWNTs’ surfaces through hydrophobic-hydrophobic interactions, and the functional groups attached to the vinyl monomers interacted with the aqueous solution through their hydrophilic properties. Radical polymerization of the vinyl monomers was performed on the surfaces of the MWNTs during γ-irradiation. This successfully introduced various functional groups to the MWNTs’ surface while maintaining their tubular morphology. Tyrosinase-immobilized biosensors incorporating MWNT supports with anion-exchange [11], hydroxy [12], and carboxylic acid [13] groups for the detection of phenolic compounds have been prepared by the physical adsorption of tyrosinase onto the MWNTs by RIGP. Biosensors prepared by physical adsorption are of limited use as the adsorbed tyrosinase can dissociate into the electrolyte during sensing, greatly reducing sensing efficiency. To overcome enzyme dissociation from the electrode, the tyrosinaseshould be covalently immobilized on the surface of the MWNT electrode. Therefore, GMA was chosen here to form covalent bonds between its epoxy groups and amine groups of the tyrosinase in alkali medium. Vinyl ferrocene, with ferrocene groups, was selected as an electron transfer mediator to increase sensing efficiency via redox reactions for the detection of phenolic compounds.Table1 lists the results of radiation-induced graft polymerization of various compositions of GMA and VF onto the MWNTs in MeOH at room temperature. Grafting yields were found to be 15–30% by TGA. Fe contents increased with increasing VF content. The maximum CV current was displayed by the electrode with a molar ratio of GMA/VF of 80/20 (sample 5 in Table 1).Figure2 shows TEM images of the purified MWNTs, and sample 5 prepared by RIGP. A fine coating on the surfaces of MWNTs that increased their diameter (from 21±0.05 nm to 34±0.05 nm) is observable in sample 5. The increased diameter of the MWNTs indicates the successful attachment of bifunctional groups by the radiation graft polymerization. These MWNT supports can be covalently immobilized with biomolecules such as enzymes, microbial molecules, and proteins through reactions of epoxy group of the functionalized MWNTs and amine groups of the biomolecules in alkali medium.TEM images of (a) purified MWNTs and (b) sample 5 in Table1.
(a)(b)Figure3 shows XPS spectra of the pure and RIGP-functionalized MWNTs. Grafting the monomers significantly affected the XPS data. The characteristic Fe 2ps peak at 713 eV appeared after grafting. Grafting with GMA resulted in an additional peak at 288.7–289.5 eV due to carbonyl groups in the polymer chains. These data support the successful functionalization of the MWNTs by RIGP.Figure 3
XPS spectra of the MWNT supports in Table1.Figure4 shows TGA curves of the purified and functionalized MWNTs prepared by one-step radiation-induced graft polymerization. The first weight loss from 50°C to 250°C for the vinyl polymer-grafted MWNTs was attributable to moisture loss because of the hydrophilic properties of the grafted vinyl polymers. The second weight loss at 250–600°C was due to weight loss through the grafted vinyl polymer. These results show that graft yields were ca. 15.0–30.0% after RIGP of vinyl monomers.Figure 4
TGA curves of (a) purified MWNTs and samples in Table1: (b) 1, (c) 2, (d) 3, (e) 4, (f) 5, and (g) 6.To coat MWNT supports onto GC electrodes, polymer binder is generally used. However, the functionalized MWNT supports prepared here possessed polymer surfaces and could be coated onto the surfaces of GC electrodes using a DMF/water mixture without polymer binder. After hand casting the MWNTs onto GC electrodes’ surfaces, CV data were recorded in PBS at pH 7.0 (Figure5). The current increased with increasing Fe content of the binary monomer mixture (Table 1). The maximum current was detected on the electrode prepared with sample 5 in Table 1, which was therefore expected to have the best sensing efficiency.Figure 5
Cyclic voltammograms in PBS at pH 7.0 of (a) GCE and samples in Table1: (b) 2, (c) 3, (d) 4, and (e) 5.(a) Calibration curve and (b) CV curves of thetyrosinase-immobilized biosensor in PBS at pH 7.0 with 0.1 mM–20 mM phenol at a scan rate 50 mV/s.
(a)(b)Table2 exhibits the comparison of the electrochemical properties to the tyrosinase-modified biosensors. The biosensor prepared in this study has a good stability and sensitivity compared to that of other biosensor because of covalently bonding and presence of electron transfer mediator onto electrode supports, respectively. As results, the radiation-induced copolymerization of two functional monomers was good method for preparation of biosensor-supporting materials.Table 2
Comparison of electrochemical properties to thetyrosinase-modified biosensors.
Type of electrodeSensitivity (Am M−1 cm−2)Sensing rangeDetection limit (nM)StabilityReferencePoly 3,4-ethylenedioxythiophene/tyrosinase electrode608Not reported5Retains activity 30% after 12 days[24]Colloidal gold nanoparticles/graphite-Teflon/tyrosinase407.040.010–8.0 M2039 days[25]Tyrosinase/3-mercaptopropionicacid-modified Au electrodes196.70.2–100 M885 days[26]Organoclay-enzyme film electrodes750.2–15 MNot reportedNot reported[27]Sol-gel immobilizedtyrosinase electrode208.831–60 M200Retains activity 57% of after 2 weeks[28]Nafion/ZnO/tyrosinase films30.30.01–0.4 mM4000Retains activity 81.2% after 20 days[29]Poly(GMA-co-VF)-g-MWNT/DMF/tyrosinase electrode1870.1–20 mM25Retain activity 90% after 30 daysThis work


### 3.2. Determination of Phenolic Compounds in Drinks Using a MWNT-Based Biosensor

Biosensors comprisingtyrosinase immobilized on MWNT supports have been prepared through the physical adsorption of tyrosinase onto electrodes supporting MWNTs with hydrophilic functional groups [11–13]. However, such electrodes are of limited use because the enzyme can desorb into the electrolyte during detection. Therefore, a covalently immobilized tyrosinase-based biosensor was prepared here.Cyclic voltammograms of phenols on the biosensor were recorded in 50 mM phosphate buffer at pH 7.0 as a function of phenol concentration (Figure6). The detection response range for phenol was found to be 0.1–20 mM. The sensitivity of the biosensor was 0.187 A M−1 cm−2.Total phenolics in red wine samples detected in a phosphate buffer using thetyrosinase-immobilized biosensor at room temperature were found to be in the range of 580–913 mg/L as shown in Table 3.Table 3
Determination of the phenolic compound concentration in real sample usingtyrosinase-immobilized biosensor based on MWNT supports with bifunctional group.
NumberBrand nameCurrent (mA)Phenolic compounds (mg/L)1Cambras (France)3.89 × 10−29132Demeter (Australa)4.11 × 10−28803Jinro wine (Korea)7.72 × 10−2580Total phenolic of several juices were also measured in PBS using thetyrosinase-immobilized biosensor at room temperature; they ranged between 490 and 750 mg/L (Tables 4 and 5). These tests demonstrate the effectiveness of the prepared tyrosinase-immobilized biosensor for the determination of phenolic compounds in drinks.Table 4
Determination of the phenolic compounds concentration in real sample usingtyrosinase-immobilized biosensor based on MWNT supports with bifunctional group.
NumberBrand nameCurrent (mA)Phenolic compounds (mg/L)1Haruyachae-Red9.96×10-24902Haruyachae-Purple8.93×10-25273Haruyachae-Yellow5.43×10-27324Haruyachae-A5.99×10-26865Haruyachae-B5.75×10-27056Haruyachae-C5.75×10-2705Table 5
Determination of the phenolic compounds concentration in real sample usingtyrosinase-immobilized biosensor based on MWNT supports with bifunctional group.
NumberBrand nameCurrent (mA)Phenolic compounds (mg/L)7Pulmuone yuki myung il yeok nok Jeub9.37×10-25108Pulmuone yuki keil nok Jeub5.40×10-27359Pulmuone danggeun Jeub6.18×10-267210Namyang at Home orange juice7.81×10-257511Seoulmilk 365 yuki achimtomato6.12×10-267612Nongshim welchs grape juice7.61×10-2585


## 3.1. Preparation and Characterization of MWNT Supports with Bifunctional Groups

Various vinyl monomers such as acrylic acid, methacrylic acid, glycidyl methacrylate, maleic anhydride, and vinylphenyl boronic acid have previously been grafted onto MWNT surfaces by radiation-induced graft polymerization in aqueous solutions at room temperature [15]. Vinyl monomers were selected for this work because they possess hydrophobic sites to complement the hydrophilic functional groups attached to them. The vinyl groups interacted with the MWNTs’ surfaces through hydrophobic-hydrophobic interactions, and the functional groups attached to the vinyl monomers interacted with the aqueous solution through their hydrophilic properties. Radical polymerization of the vinyl monomers was performed on the surfaces of the MWNTs during γ-irradiation. This successfully introduced various functional groups to the MWNTs’ surface while maintaining their tubular morphology. Tyrosinase-immobilized biosensors incorporating MWNT supports with anion-exchange [11], hydroxy [12], and carboxylic acid [13] groups for the detection of phenolic compounds have been prepared by the physical adsorption of tyrosinase onto the MWNTs by RIGP. Biosensors prepared by physical adsorption are of limited use as the adsorbed tyrosinase can dissociate into the electrolyte during sensing, greatly reducing sensing efficiency. To overcome enzyme dissociation from the electrode, the tyrosinaseshould be covalently immobilized on the surface of the MWNT electrode. Therefore, GMA was chosen here to form covalent bonds between its epoxy groups and amine groups of the tyrosinase in alkali medium. Vinyl ferrocene, with ferrocene groups, was selected as an electron transfer mediator to increase sensing efficiency via redox reactions for the detection of phenolic compounds.Table1 lists the results of radiation-induced graft polymerization of various compositions of GMA and VF onto the MWNTs in MeOH at room temperature. Grafting yields were found to be 15–30% by TGA. Fe contents increased with increasing VF content. The maximum CV current was displayed by the electrode with a molar ratio of GMA/VF of 80/20 (sample 5 in Table 1).Figure2 shows TEM images of the purified MWNTs, and sample 5 prepared by RIGP. A fine coating on the surfaces of MWNTs that increased their diameter (from 21±0.05 nm to 34±0.05 nm) is observable in sample 5. The increased diameter of the MWNTs indicates the successful attachment of bifunctional groups by the radiation graft polymerization. These MWNT supports can be covalently immobilized with biomolecules such as enzymes, microbial molecules, and proteins through reactions of epoxy group of the functionalized MWNTs and amine groups of the biomolecules in alkali medium.TEM images of (a) purified MWNTs and (b) sample 5 in Table1.
(a)(b)Figure3 shows XPS spectra of the pure and RIGP-functionalized MWNTs. Grafting the monomers significantly affected the XPS data. The characteristic Fe 2ps peak at 713 eV appeared after grafting. Grafting with GMA resulted in an additional peak at 288.7–289.5 eV due to carbonyl groups in the polymer chains. These data support the successful functionalization of the MWNTs by RIGP.Figure 3
XPS spectra of the MWNT supports in Table1.Figure4 shows TGA curves of the purified and functionalized MWNTs prepared by one-step radiation-induced graft polymerization. The first weight loss from 50°C to 250°C for the vinyl polymer-grafted MWNTs was attributable to moisture loss because of the hydrophilic properties of the grafted vinyl polymers. The second weight loss at 250–600°C was due to weight loss through the grafted vinyl polymer. These results show that graft yields were ca. 15.0–30.0% after RIGP of vinyl monomers.Figure 4
TGA curves of (a) purified MWNTs and samples in Table1: (b) 1, (c) 2, (d) 3, (e) 4, (f) 5, and (g) 6.To coat MWNT supports onto GC electrodes, polymer binder is generally used. However, the functionalized MWNT supports prepared here possessed polymer surfaces and could be coated onto the surfaces of GC electrodes using a DMF/water mixture without polymer binder. After hand casting the MWNTs onto GC electrodes’ surfaces, CV data were recorded in PBS at pH 7.0 (Figure5). The current increased with increasing Fe content of the binary monomer mixture (Table 1). The maximum current was detected on the electrode prepared with sample 5 in Table 1, which was therefore expected to have the best sensing efficiency.Figure 5
Cyclic voltammograms in PBS at pH 7.0 of (a) GCE and samples in Table1: (b) 2, (c) 3, (d) 4, and (e) 5.(a) Calibration curve and (b) CV curves of thetyrosinase-immobilized biosensor in PBS at pH 7.0 with 0.1 mM–20 mM phenol at a scan rate 50 mV/s.
(a)(b)Table2 exhibits the comparison of the electrochemical properties to the tyrosinase-modified biosensors. The biosensor prepared in this study has a good stability and sensitivity compared to that of other biosensor because of covalently bonding and presence of electron transfer mediator onto electrode supports, respectively. As results, the radiation-induced copolymerization of two functional monomers was good method for preparation of biosensor-supporting materials.Table 2
Comparison of electrochemical properties to thetyrosinase-modified biosensors.
Type of electrodeSensitivity (Am M−1 cm−2)Sensing rangeDetection limit (nM)StabilityReferencePoly 3,4-ethylenedioxythiophene/tyrosinase electrode608Not reported5Retains activity 30% after 12 days[24]Colloidal gold nanoparticles/graphite-Teflon/tyrosinase407.040.010–8.0 M2039 days[25]Tyrosinase/3-mercaptopropionicacid-modified Au electrodes196.70.2–100 M885 days[26]Organoclay-enzyme film electrodes750.2–15 MNot reportedNot reported[27]Sol-gel immobilizedtyrosinase electrode208.831–60 M200Retains activity 57% of after 2 weeks[28]Nafion/ZnO/tyrosinase films30.30.01–0.4 mM4000Retains activity 81.2% after 20 days[29]Poly(GMA-co-VF)-g-MWNT/DMF/tyrosinase electrode1870.1–20 mM25Retain activity 90% after 30 daysThis work


## 3.2. Determination of Phenolic Compounds in Drinks Using a MWNT-Based Biosensor

Biosensors comprisingtyrosinase immobilized on MWNT supports have been prepared through the physical adsorption of tyrosinase onto electrodes supporting MWNTs with hydrophilic functional groups [11–13]. However, such electrodes are of limited use because the enzyme can desorb into the electrolyte during detection. Therefore, a covalently immobilized tyrosinase-based biosensor was prepared here.Cyclic voltammograms of phenols on the biosensor were recorded in 50 mM phosphate buffer at pH 7.0 as a function of phenol concentration (Figure6). The detection response range for phenol was found to be 0.1–20 mM. The sensitivity of the biosensor was 0.187 A M−1 cm−2.Total phenolics in red wine samples detected in a phosphate buffer using thetyrosinase-immobilized biosensor at room temperature were found to be in the range of 580–913 mg/L as shown in Table 3.Table 3
Determination of the phenolic compound concentration in real sample usingtyrosinase-immobilized biosensor based on MWNT supports with bifunctional group.
NumberBrand nameCurrent (mA)Phenolic compounds (mg/L)1Cambras (France)3.89 × 10−29132Demeter (Australa)4.11 × 10−28803Jinro wine (Korea)7.72 × 10−2580Total phenolic of several juices were also measured in PBS using thetyrosinase-immobilized biosensor at room temperature; they ranged between 490 and 750 mg/L (Tables 4 and 5). These tests demonstrate the effectiveness of the prepared tyrosinase-immobilized biosensor for the determination of phenolic compounds in drinks.Table 4
Determination of the phenolic compounds concentration in real sample usingtyrosinase-immobilized biosensor based on MWNT supports with bifunctional group.
NumberBrand nameCurrent (mA)Phenolic compounds (mg/L)1Haruyachae-Red9.96×10-24902Haruyachae-Purple8.93×10-25273Haruyachae-Yellow5.43×10-27324Haruyachae-A5.99×10-26865Haruyachae-B5.75×10-27056Haruyachae-C5.75×10-2705Table 5
Determination of the phenolic compounds concentration in real sample usingtyrosinase-immobilized biosensor based on MWNT supports with bifunctional group.
NumberBrand nameCurrent (mA)Phenolic compounds (mg/L)7Pulmuone yuki myung il yeok nok Jeub9.37×10-25108Pulmuone yuki keil nok Jeub5.40×10-27359Pulmuone danggeun Jeub6.18×10-267210Namyang at Home orange juice7.81×10-257511Seoulmilk 365 yuki achimtomato6.12×10-267612Nongshim welchs grape juice7.61×10-2585


## 4. Conclusion

A covalently immobilizedtyrosinase-based biosensor was fabricated on MWNT supports bifunctionalized by radiation-induced graft polymerization. Its sensing range for phenol was 0.1 mM–20 mM. It was used to determine phenolic compounds in commercial red wines and juices in phosphate buffer solution; it found 580–913 mg/L phenolics in various red wines and 490–750 mg/L phenolics various juices. These results were calculated from a calibration curve of phenols compiled for the sensor. These results show that bifunctionalized MWNT supports can be used in enzyme-immobilized biosensors as good electron transfer materials and as supports for enzyme immobilization.



---

*Source: 127613-2012-05-27.xml*