# Annealing Effect of ZnO Seed Layer on Enhancing Photocatalytic Activity of ZnO/TiO2 Nanostructure

Authors: Woo-Young Kim; Soon-Wook Kim; Dae-Hwang Yoo; Eui Jung Kim; Sung Hong Hahn
Journal: International Journal of Photoenergy
 (2013)

---

## Abstract

Zinc oxide (ZnO)/titanium dioxide (TiO2) nanorods have been synthesized via a hydrothermal method for ZnO nanorods and an electron-beam deposition for TiO2 nanorods. This work examined the effect of annealing ZnO seed layer on the photocatalytic activity of the ZnO/TiO2 nanorods which was determined from photodecomposition of methylene blue under UV irradiation. The photocatalytic activity of the ZnO/TiO2 nanorods was improved with increasing annealing temperature of the seed layer from 300°C to 500°C. Annealing the seed layer at 500°C showed the best photocatalytic activity resulting from high UV absorption ability, a large surface area with flower structure and copious oxygen defects which promote separation of electron-hole pairs reducing electron recombination. The prepared nanorods were characterized by field emission-scanning electron microscopy (FE-SEM), X-ray diffraction (XRD), photoluminescence (PL), and UV-visible spectroscopy.


---

## Body

## 1. Introduction

The synthesis of semiconductor nanomaterial is of great worldwide interest. The nanomaterials have enhanced optical and electronic properties, finding their application in various fields such as optoelectronic nanodevices and optical excitations [1–3]. Titanium dioxide (TiO2) is the most promising material for a photocatalyst, because it has good photoactivity, long-term stability, and low cost. Anatase phase, one of TiO2 crystal structures, shows higher photoactivity than rutile [4, 5]. Zinc oxide (ZnO), which has a direct band gap of 3.37 eV and large exciton binding energy of 60 meV, has a high mechanical and a thermal stability [6–8]. In addition, it can be utilized as a source which makes blue/UV optoelectronic devices due to its photochemical properties [9]. It is known that ZnO/TiO2 nanomaterials promote charge separation decreasing electron-hole recombination [10]. Furthermore, they have high chemical and thermal stability and high absorption in the UV region [11]. As a result, the ZnO/TiO2 nanorods show an enhanced photocatalytic activity. The fabrication of one-dimensional (1D) nanostructures has attracted considerable attention due to their great optical and electrical properties [12]. Various 1D of ZnO nanostructures such as nanorods, nanowires, and nanorings have been synthesized by physical and chemical methods including molecular beam epitaxy (MBE) [13], plasma-enhanced chemical vapor deposition (PECVD) [14], thermal evaporation [15], and template based method [16]. The wet chemical processes are a cost-effective low-temperature technique [17–20]. The hydrothermal technique is an effective method to control the 1D ZnO nanostructure [21], which is surface independent [22]. The physical properties of the ZnO/TiO2 nanorods relate to their nanostructure which is dependent on deposition conditions and annealing. Especially, the annealing of the ZnO seed layer improved adhesion on substrate, which contributed to well-aligned ZnO nanorods [23]. The annealing process is important to obtain desirable structural and optical properties. The main contributions of seed layer annealing may come from the improvement of the crystallinity and absorption which could give an significantly effect on the photocatalytic acitivity of ZnO/TiO2 nanorods [24].In this study, we investigate the effect of seed layer annealing of the ZnO/TiO2 nanorods on the photocatalytic activity. The TiO2 nanorods were prepared by electron-beam evaporation. ZnO seed solution was then spin-coated on the TiO2 nanorods, which was followed by annealing at 300°C, 400°C, and 500°C. Subsequently, the ZnO nanorods have been grown by hydrothermal method.


## 2. Experiments

### 2.1. Preparation of TiO2 Nanorods

TiO2 nanorods were obliquely deposited on quartz substrate using electron-beam evaporation. TiO2 tablets with high purity (99.99%) were used as a raw material. After the deposition chamber was evacuated to a base pressure of 6×10-6 torr, the TiO2 films were deposited at a working oxygen gas pressure of 5×10-5 torr. The working current was 200 mA and the electron gun voltage was 7.0 kV. The electron beam was irradiated at an incident angle of 75° to obtain the TiO2 nanorods. The prepared nanorods were annealed at 600°C for 1 hour to form anatase structure.


### 2.2. Growth of ZnO Nanorods

ZnO nanorods were grown on the prepared TiO2 nanorods via a hydrothermal method. ZnO seed solution was prepared by dissolving 5 mM of zinc acetate dihydrate (C4H6O4Zn·2H2O) in 100 mL of methoxy ethanol and then stirring for 24 hours. The ZnO seed solution was spin-coated on the TiO2 nanorods/quartz substrate twice. The ZnO seed coated sample was annealed at 300°C, 400°C, and 500°C, which are referred to as ZT-300, ZT-400, and ZT-500, respectively. The ZnO growth solution was prepared by dissolving 16 mM of zinc nitrate hexahydrate (Zn (NO3)2·6H2O) and 25 mM of hexamethylenetetramine (HMT) into 200 mL of distilled water. The ZnO seed coated sample was immersed into the growth solution at 90°C for 4 hours. The sample was then removed from the solution, washed with distilled water, and annealed at 350°C for 1 hour. For comparison, ZnO nanorods were grown without TiO2, and their seed layers were annealed at 300°C, 400°C, and 500°C, which are labeled as Z-300, Z-400, and Z-500, respectively.


### 2.3. Characterization and Photocatalytic Activity

The surface morphology of the ZnO/TiO2 and TiO2 nanorods was examined by field emission-scanning electron microscopy (FE-SEM, Supra 40, Carl Zeiss, Swiss). The X-ray diffraction (XRD) patterns were measured with a Rint 2000 vertical goniometer using Cu Kα radiation at 40 kV and 100 mA. The photoluminescence (PL) was measured by a SPEX 750 M PL spectrometer with 325 nm He-Cd laser with 4 mW output power at room temperature. UV-vis absorbance spectra were examined to investigate absorption property of the ZnO/TiO2 nanorods. The photocatalytic activities of the ZnO/TiO2 and ZnO nanorods were examined using a UV-visible spectrophotometer (HP 8453) by measuring the photodegradation rate of methylene blue (MB) with an initial concentration of 1×10-5 mol/L. The thin films were immersed in the MB solution in a tubular quartz reactor under four surrounding UV lamps of 20 W (wavelength = 352 nm). After dark adsorption equilibrium for 30 min, photodegradation of the MB was measured by UV-vis spectrophotometer (HP 8453) at λmax=664 nm.


## 2.1. Preparation of TiO2 Nanorods

TiO2 nanorods were obliquely deposited on quartz substrate using electron-beam evaporation. TiO2 tablets with high purity (99.99%) were used as a raw material. After the deposition chamber was evacuated to a base pressure of 6×10-6 torr, the TiO2 films were deposited at a working oxygen gas pressure of 5×10-5 torr. The working current was 200 mA and the electron gun voltage was 7.0 kV. The electron beam was irradiated at an incident angle of 75° to obtain the TiO2 nanorods. The prepared nanorods were annealed at 600°C for 1 hour to form anatase structure.


## 2.2. Growth of ZnO Nanorods

ZnO nanorods were grown on the prepared TiO2 nanorods via a hydrothermal method. ZnO seed solution was prepared by dissolving 5 mM of zinc acetate dihydrate (C4H6O4Zn·2H2O) in 100 mL of methoxy ethanol and then stirring for 24 hours. The ZnO seed solution was spin-coated on the TiO2 nanorods/quartz substrate twice. The ZnO seed coated sample was annealed at 300°C, 400°C, and 500°C, which are referred to as ZT-300, ZT-400, and ZT-500, respectively. The ZnO growth solution was prepared by dissolving 16 mM of zinc nitrate hexahydrate (Zn (NO3)2·6H2O) and 25 mM of hexamethylenetetramine (HMT) into 200 mL of distilled water. The ZnO seed coated sample was immersed into the growth solution at 90°C for 4 hours. The sample was then removed from the solution, washed with distilled water, and annealed at 350°C for 1 hour. For comparison, ZnO nanorods were grown without TiO2, and their seed layers were annealed at 300°C, 400°C, and 500°C, which are labeled as Z-300, Z-400, and Z-500, respectively.


## 2.3. Characterization and Photocatalytic Activity

The surface morphology of the ZnO/TiO2 and TiO2 nanorods was examined by field emission-scanning electron microscopy (FE-SEM, Supra 40, Carl Zeiss, Swiss). The X-ray diffraction (XRD) patterns were measured with a Rint 2000 vertical goniometer using Cu Kα radiation at 40 kV and 100 mA. The photoluminescence (PL) was measured by a SPEX 750 M PL spectrometer with 325 nm He-Cd laser with 4 mW output power at room temperature. UV-vis absorbance spectra were examined to investigate absorption property of the ZnO/TiO2 nanorods. The photocatalytic activities of the ZnO/TiO2 and ZnO nanorods were examined using a UV-visible spectrophotometer (HP 8453) by measuring the photodegradation rate of methylene blue (MB) with an initial concentration of 1×10-5 mol/L. The thin films were immersed in the MB solution in a tubular quartz reactor under four surrounding UV lamps of 20 W (wavelength = 352 nm). After dark adsorption equilibrium for 30 min, photodegradation of the MB was measured by UV-vis spectrophotometer (HP 8453) at λmax=664 nm.


## 3. Results and Discussion

Figure1 shows the SEM images of TiO2 nanorods (as the buffer layer), ZT-300, ZT-400, and ZT-500. The obliquely deposited TiO2 nanorod arrays have a high surface area as shown in Figure 1(a). Figure 1 observed that the size and structure of the ZnO nanorods depend on the annealing temperature of the seed layer. From the SEM results, the sizes of the TiO2 nanorods and ZT-300, ZT-400, and ZT-500 were evaluated to diameter with (a) 21.1 nm, (b) 306.8 nm, (c) 210.2 nm, and (d) 96.6 nm, and length with (e) 60.0 nm, (f) 2.98 μm, (g) 2.48 μm, and (h) 1.91 μm. In the case of ZT-500, a flower-like structure composed of thin nanorods was formed, which relates to the polycrystalline structure of the large-size ZnO seed as shown in Figure 1(c). The big grains are polycrystalline ZnO seeds consisting of plenty of small crystallites [24]. The ZnO nanorods have been grown on the TiO2 nanorod arrays with a porous surface. As a result, the agglomerate of ZnO nanorods with various directions was formed [19].Figure 1
SEM images of the top view of (a) TiO2 nanorods, (b) ZT-300, (c) ZT-400, and (d) ZT-500 and cross-sectional view of (e) TiO2 nanorods, (f) ZT-300, (g) ZT-400, and (h) ZT-500.Figure2 displays the XRD patterns of the Z-300, ZT-300, ZT-400, and ZT-500. In case of the ZnO (JCPDS card no. 79-2205) nanorods, the (100), (002), (101), and (102) peaks appeared. The high intensity (002) peak indicates that the prepared ZnO nanorods have hexagonal wurtzite structure and are grown along the c-axis direction to the substrate surface [25, 26]. With the increase of the seed annealing temperature, the intensity of the (002) peak decreased due to a decrease in the reinforced atomic diffusion between the ZnO and TiO2. When the seed layer of the ZnO/TiO2 nanorods was annealed at high temperature, the atoms can acquire energy enough to move, leading to strengthened interdiffusion motion between the ZnO and TiO2 [27]. The apparent (101) peaks of the TiO2 (JCPDS card no. 84-1286) nanorods indicate anatase TiO2. It is well known that the anatase TiO2 exhibits a better photocatalytic activity than rutile TiO2 [4]. Due to the presence of a ZnO/TiO2 heterojunction, the recombination of electron-hole pairs will be restrained. This improves the availability of the electrons to transfer to the TiO2 surface of the ZnO/TiO2 nanorods and consequently causes a redox reaction [28].Figure 2
XRD patterns of ZT-300, ZT-400, ZT-500, and ZnO.In Figure3, the PL spectra of the ZT-300, ZT-400, and ZT-500 show that the UV emission peak of the ZnO/TiO2 nanorods appeared at 382 nm due to the recombination of free exciton [29, 30]. The peak of the ZT-500 was higher than those of other samples, implying that the crystallinity of the ZnO/TiO2 nanorods was improved with increasing annealing temperature of the seed layers. A visible peak of the ZnO/TiO2 nanorods appeared at 600 nm corresponding to the orange emission. It is related to the levels within band gap caused by defects, and in this case it is associated with oxygen vacancy defects [30]. The orange emission is due to the deep defects and it means that oxygen vacancy defects were deeply inserted in the band gap [31, 32]. The emission intensity of the ZnO/TiO2 nanorods was enhanced with increasing annealing temperature of the seed layers. The inset of Figure 3 shows that the intensities of the visible peaks of the ZT-500 and Z-500 at 600 nm are greatly different. This implies that TiO2 nanorods with ZnO seed layers annealed at 500°C work as supportive materials in the intense increase of orange emission in many ways [29]. The first thing is that they made the radius of ZnO nanorods reduce which is supported from SEM analysis in Figure 1. It leads to the increase of surface area active to the irradiating light and contribute to the increase of PL peak [33]. The second thing is to cause the increase of defects. Atomic diffusion between the ZnO and TiO2 nanorods becomes vigorous at high temperature, resulting in the increase of defects [27]. A difference in the photocatalytic activity is related to the concentration of oxygen defects on the surface layer as well as surface adsorption ability. The oxygen vacancy defects work as an electron acceptor and trap photogenerated electrons decreasing the surface recombination of electron-hole pairs. As described above, the oxygen vacancy and the interstitial oxygen defects promote separation of electron-hole pairs to minimize the electron recombination, leading to higher photocatalytic activity [30, 34, 35].Figure 3
Room temperature PL spectra of ZT-300, ZT-400, and ZT-500. The inset shows visible emission of Z-500, and ZT-500.Figure4 shows the UV-visible absorbance spectra of the ZT-300, ZT-400, and ZT-500. The absorption edge was observed to be located at 371 nm for the crystalline ZnO. The absorbance increased significantly with increasing the annealing temperature of the seed layers. It results from a large surface area of ZT-500 with flower structure composed of thin nanorods as shown in Figure 1. It is that the amorphous phase is reduced with increasing the seed layer annealing temperature since more energy is supplied for crystalline growth, thus resulting in an improvement in crystallinity of the ZT-500. The relationship of the absorption coefficient and the incident photon energy of ZnO and TiO2 nanorods is given by the equation α(hυ)∝(hυ-E0)n, where α is the absorption coefficient, hυ is the energy of the incident photon, n is 0.5 for the semiconductor with direct band gap, and E0 is value of energy gap [36]. According to the above equation, the band gap of the ZnO nanorods was determined as 3.22 eV and that of the TiO2 nanorods as 3.19 eV.Figure 4
UV-vis absorbance spectra of ZT-300, ZT-400, ZT-500, and TiO2.The photocatalytic activities of the ZnO/TiO2 and ZnO nanorods were evaluated by the degradation of the MB under the UV irradiation. Figure 5(a) shows the UV-visible absorption spectra of the MB for the ZT-500 with various UV irradiation times. The MB showed a major absorption band at 665 nm which became transparent after 120 min irradiation, resulting from facile destruction of the chromophoric structure of the MB [37].(a) UV-vis absorbance spectra of MB for the ZT-500. (b) Photodegradation of the MB for ZT-300, ZT-400, ZT-500, and Z-500.
(a)
(b)The photocatalytic activity of the samples can be represented by a plot ofC/Co versus UV irradiation time [38]. Here C is the concentration at irradiation time t and Co is the initial concentration. Figure 5(b) shows the photocatalytic activity of the ZnO/TiO2 and ZnO nanorods by the photodegradation of the MB under the UV irradiation. The MB was decomposed by 76.2%, 83.3%, 87.0%, and 95.5% after 4 h of the UV irradiation for Z-500, ZT-300, ZT-400, and ZT-500, respectively. The samples with a heterojunction of the ZnO/TiO2 nanorods showed an enhanced photocatalytic activity than the ZnO nanorods. Improved photocatalytic activity comes from a high surface area of the TiO2 nanostructure [27], and coupling effect of ZnO and TiO2, which increases interfacial charge transfer and decreases the recombination of the electrons and holes by promoting their separation [39–41]. The ZT-500 showed the best photocatalytic activity, indicating that defects on the ZnO nanorods can act as a dominant factor for enhancing photocatalytic activity. In addition, the ZT-500 has a high surface area leading to high absorption ability compared with those of other samples and a high ability of the generating photoinduced electron-hole pairs [37].Figure6 shows the diagram of the band gap structure of the ZnO/TiO2 nanorods. The photogenerated electrons transfer from the conduction band of ZnO to the conduction band of TiO2. This leads to a decrease in the electron-hole pairs recombination by promoting their separation, and the lifetime of the charge carriers is increased [39, 40]. The charge separation increases the efficiency of the interfacial charge transfer and improves the redox process [40]. Therefore, the ZnO/TiO2 nanorods have a strongly positive effect on the photocatalytic activity.Figure 6
A schematic diagram of the electron and hole transfers for the ZnO/TiO2 nanorods.


## 4. Conclusion

TiO2 nanorod structure was prepared by electron-beam evaporation method through oblique beam incidence. ZnO seed layers were coated on TiO2 and annealed at 300–500°C, which was followed by ZnO nanorod growth to form heterojunction structure of ZnO/TiO2. The annealed ZnO seed layer was found to have a significant influence on the morphology of the ZnO/TiO2 nanorod arrays. With increasing the annealing temperature of the ZnO seed layers, the size of the ZnO nanoparticles was gradually increased, leading to different morphology of ZT-500 composed of the thin nanorods which have a large surface area and a high absorption ability. The heterostructure of ZnO/TiO2 can promote the separation of the electron-hole pairs and decrease their recombination enhancing photocatalytic reaction. When the annealing temperature of the seed layers reaches a relatively high temperature of 500°C, the atomic diffusion between the ZnO and TiO2 nanorods is significantly enhanced, resulting in more interface defects which reduce the electron-hole recombination. As a result, ZnO/TiO2 nanorods with high annealing temperature of the seed layers exhibited excellent photocatalytic activities for the decomposition of the MB.



---

*Source: 130541-2013-05-16.xml*