# Effects of Treated Cow Dung Addition on the Strength of Carbon-Bearing Iron Ore Pellets

Authors: Qing-min Meng; Jia-xin Li; Tie-jun Chun; Xiao-feng He; Ru-fei Wei; Ping Wang; Hong-ming Long
Journal: Advances in Materials Science and Engineering
 (2017)

---

## Abstract

It is of particular interest to use biomass as an alternative source of fuel in direct-reduction ironmaking to ease the current reliance on fossil fuel energy. The influence of cow dung addition on the strength of carbon-bearing iron ore pellets composed of cow dung, iron ore, anthracite, and bentonite was investigated, the quality of green and dry pellet was evaluated based on FTIR analysis, and the mechanism of strength variation of the reduced pellets was investigated by analysing the phase composition and microstructure using XRD and SEM. The results show that cow dung addition decreased the green pellet strength due to expansion of the amorphous region of the cellulose in the cow dung; however, the dry pellet strength increased substantially. In the process of reduction roasting, it was found that cow dung addition can promote aggregation of iron crystals and increase the density of the pellets, resulting in increased strength of the reduction roasted pellets, while excessive cow dung addition resulted in lower strength.


---

## Body

## 1. Introduction

With the gradual depletion of raw materials for the blast furnace, such as coke and quality iron ore, direct-reduction and smelting reduction technologies using gas, liquid fuels, and noncoking coal as energy sources were developed as cleaner, more environment friendly alternatives, which have been applied widely around the world [1–3]. However, the fuel sources of noncoking coal iron-making technology have not fundamentally changed, and there is a gap in product quality and energy consumption compared to the blast furnace. The use of biomass as an alternative fuel source, to further reduce the consumption of fossil fuels and emission of carbon in the steel-making industry, has become a hot topic among scholars [4–8]. Sterol [9] investigated the mechanisms of iron ore reduction with biomass wood waste. The results showed that the iron ore was successfully reduced to predominantly metallic iron when up to 30 wt% of biomass was introduced into the mixture and reduction commenced at approximately 943 K and was almost completed at 1473 K. Wei et al. [10] studied the characteristics and kinetics of iron oxide reduction by carbon in biomass composites. The result showed that iron oxide can be reduced by biomass very rapidly, and the degree of metallisation and reduction increased with temperature.Iron oxide reduction by carbon in biomass can be divided into two stages, namely, reduction by volatile matter followed by reduction by nonvolatile carbon. The reduction times of the two stages both decrease with increasing temperature. Liu et al. [11] researched the reduction of carbon-bearing pellets, using the reducing agents prepared from carbonization products of rice husk, peanut shells, and wood chips. The result showed that the carbon-bearing pellets could be reduced rapidly between 1473 K and 1573 K in about 15 to 20 minutes, while the higher carbon content and appropriate volatile content in biological carbon were beneficial to the pellet reduction. Han et al. [12] studied the effect of biomass on the reduction of carbon-bearing pellets using charcoal, bamboo charcoal, and straw as reductant. The results showed that the biomass reductants had little effect on metallisation rate, but certain biomass reductants had a substantial influence on the strength and volumetric shrinkage of the pellets. The compressive strength of pellets with straw was relatively higher, while the strength of pellets with charcoal or bamboo charcoal was low.Biomass includes all animals, plants, and microorganisms, including organic waste residues. Thus, maximising the use of biomass could potentially relieve the global energy crisis. The large amount of animal dung produced as a by-product of the Agricultural Industry is causing an increasingly serious environmental problem [13], with the stock of cow dung topping the list. Researchers have made extensive studies regarding the issue of cow dung utilisation. Cow dung reclamation technology, such as energy, composting, and animal feed, has achieved considerable economic and social benefits [14–17]. Other than this, researchers are also exploring the applications of cow dung in areas such as new preparation methods of biomass carbon materials [18–20] and solid waste disposal [21, 22].Similar to other plant biomass, cellulose, hemicellulose, and lignin are the main chemical constituents of dry cow dung. The similarity of organic components between cow dung and plant biomass makes it feasible to use cow dung as an alternative reducing agent in iron ore reduction, and this has been demonstrated in various studies. Rath et al. [23] used cow dung as a reductant in the reduction roasting of an iron ore slime containing 56.2% Fe. A concentrate of ~64% Fe, with a recovery of ~66 wt%, was obtained from the reduced product after being subjected to low intensity magnetic separation. Under similar conditions, a concentrate of ~66% Fe, with a recovery of only 35 wt%, was obtained after using conventional charcoal as the reductant (93.5% fixed carbon and 1.2% volatile matter), which demonstrated that cow dung was a better reductant.The key purpose of this study is to investigate the effect of cow dung addition on the strength of carbon-bearing iron ore pellets and its mechanism. The influence of cow dung addition on the quality of green and dry pellets is evaluated based on FTIR analysis, and the mechanism of strength variation of reduction roasted pellets was investigated by analysing the phase composition and microstructure using XRD and SEM, to provide a benchmark for further utilisation of cow dung in direct-reduction ironmaking.


## 2. Materials and Methods

### 2.1. Materials

Carbon-bearing iron ore pellets were prepared by pressing a mixture consisting of iron ore, anthracite, bentonite, and different proportions of cow dung. The chemical composition of the iron ore used in this study is shown in Table1, while the proximate analyses of the anthracite and the cow dung used as the reductant in this study are given in Table 2. The cow dung was obtained from the Mengniu Modern Animal Husbandry (Group), Maanshan Co. First, all of the raw materials were dried at 383 K for 24 h, individually ground in a ball mill to a passing size of 74 μm for the iron ore and 200 μm for the reducing agents. Mixtures of the ground materials were prepared according to the experimental plan given in Table 3. A little water was added, and 20 mm diameter pellets (molar ratio of Cfix/Oiron oxide = 1) were prepared by pressing at 10 MPa.Table 1
Chemical composition of iron ore (wt%).
TFe
FeO
SiO2
Al2O3
CaO
MgO
P
S
61.4
23.5
3.3
1.1
1.0
0.2
0.028
0.328Table 2
Proximate analysis of reducing agent (wt%).
Type of reducing agent
Fixed carbon
Ash
Volatile matter
P
S
Anthracite
78.8
13.4
7.9
0.024
0.580
Cow dung
7.7
24.9
67.4
0.001
0.270Table 3
Raw material ratio of the carbon-bearing iron ore pellets.
Sample number
Iron ore
Anthracite
Cow dung
Bentonite
C
fix
/
O
iron oxide
1
82.5%
17.5%
0.0%
1.6%
1.0
2
79.4%
16.5%
4.1%
1.6%
1.0
3
76.7%
15.6%
7.8%
1.6%
1.0
4
74.2%
14.7%
11.1%
1.6%
1.0
5
72.1%
14.0%
14.0%
1.6%
1.0


### 2.2. Characterization Techniques

Characterization studies were undertaken on the raw materials and some reduction roasted products. The FTIR spectra were obtained with a Nicolet 8700 spectrophotometer by adding 32 scans at a resolution of 4 cm−1, using KBr wafers containing about 0.5 g of sample, which had been dried at 393 K for 24 h before spectral analysis. XRD was carried out with a D8 Advance X-ray powder diffractometer using Cu-Kα radiation. The voltage and current of the machine were set at 60 kV and 80 mA, respectively, scanning from 20° to 80° using a step size of 0.02°. A scanning electron microscope (NOVA Nano SEM430, USA) equipped with EDS detector was used for the microstructure studies.


### 2.3. Strength Tests and Reduction Roasting

The compressive strength of green, dry, and reduction roasted pellets was measured with an automatic compressive strength tester, and each sample was tested 20 times under the same conditions and the results were averaged. A schematic of the reduction roasting experimental apparatus is shown in Figure1. The furnace has a working temperature range of 298–1573 K, with ±1 K temperature control accuracy, and produces a 150 mm hot zone. The carbon-bearing pellets were placed in a Ni-Cr alloy basket which was hung over the hot zone, and the pellets were heated to 1523 K at a rate of 20 K/min. High-purity nitrogen gas was supplied at a constant flowrate of 1 l/min in the reaction tube. At the end of the experiment, the basket was quickly moved to the top of the furnace with high-purity nitrogen gas continuing to be supplied until the pellets cooled to room temperature.Figure 1
A schematic of experimental apparatus of reduction roasting.


## 2.1. Materials

Carbon-bearing iron ore pellets were prepared by pressing a mixture consisting of iron ore, anthracite, bentonite, and different proportions of cow dung. The chemical composition of the iron ore used in this study is shown in Table1, while the proximate analyses of the anthracite and the cow dung used as the reductant in this study are given in Table 2. The cow dung was obtained from the Mengniu Modern Animal Husbandry (Group), Maanshan Co. First, all of the raw materials were dried at 383 K for 24 h, individually ground in a ball mill to a passing size of 74 μm for the iron ore and 200 μm for the reducing agents. Mixtures of the ground materials were prepared according to the experimental plan given in Table 3. A little water was added, and 20 mm diameter pellets (molar ratio of Cfix/Oiron oxide = 1) were prepared by pressing at 10 MPa.Table 1
Chemical composition of iron ore (wt%).
TFe
FeO
SiO2
Al2O3
CaO
MgO
P
S
61.4
23.5
3.3
1.1
1.0
0.2
0.028
0.328Table 2
Proximate analysis of reducing agent (wt%).
Type of reducing agent
Fixed carbon
Ash
Volatile matter
P
S
Anthracite
78.8
13.4
7.9
0.024
0.580
Cow dung
7.7
24.9
67.4
0.001
0.270Table 3
Raw material ratio of the carbon-bearing iron ore pellets.
Sample number
Iron ore
Anthracite
Cow dung
Bentonite
C
fix
/
O
iron oxide
1
82.5%
17.5%
0.0%
1.6%
1.0
2
79.4%
16.5%
4.1%
1.6%
1.0
3
76.7%
15.6%
7.8%
1.6%
1.0
4
74.2%
14.7%
11.1%
1.6%
1.0
5
72.1%
14.0%
14.0%
1.6%
1.0


## 2.2. Characterization Techniques

Characterization studies were undertaken on the raw materials and some reduction roasted products. The FTIR spectra were obtained with a Nicolet 8700 spectrophotometer by adding 32 scans at a resolution of 4 cm−1, using KBr wafers containing about 0.5 g of sample, which had been dried at 393 K for 24 h before spectral analysis. XRD was carried out with a D8 Advance X-ray powder diffractometer using Cu-Kα radiation. The voltage and current of the machine were set at 60 kV and 80 mA, respectively, scanning from 20° to 80° using a step size of 0.02°. A scanning electron microscope (NOVA Nano SEM430, USA) equipped with EDS detector was used for the microstructure studies.


## 2.3. Strength Tests and Reduction Roasting

The compressive strength of green, dry, and reduction roasted pellets was measured with an automatic compressive strength tester, and each sample was tested 20 times under the same conditions and the results were averaged. A schematic of the reduction roasting experimental apparatus is shown in Figure1. The furnace has a working temperature range of 298–1573 K, with ±1 K temperature control accuracy, and produces a 150 mm hot zone. The carbon-bearing pellets were placed in a Ni-Cr alloy basket which was hung over the hot zone, and the pellets were heated to 1523 K at a rate of 20 K/min. High-purity nitrogen gas was supplied at a constant flowrate of 1 l/min in the reaction tube. At the end of the experiment, the basket was quickly moved to the top of the furnace with high-purity nitrogen gas continuing to be supplied until the pellets cooled to room temperature.Figure 1
A schematic of experimental apparatus of reduction roasting.


## 3. Results and Discussion

### 3.1. Effects of Treated Cow Dung Addition on the Cold Strength of Carbon-Bearing Pellets

The cold strength test results of green and dry pellets with different proportions of cow dung addition are shown in Figure2. The bar charts show that the strength of green and dry pellets varies with cow dung addition, but there is no clear correlation between the average compressive strength and the ratio of cow dung to anthracite added. The average strength of the green pellets containing cow dung decreased by 8–16% relative to pellets with no dung. For example, the strength of green pellets with no dung was 10.1 N/pellet, while green pellets with a dung-to-anthracite ratio of 1 : 4 (containing 4.1% cow dung) were 8.5 N/Pellet and the strength of green pellets with a dung-to-anthracite ratio of 3 : 4 (containing 11.1% cow dung) was 8.6 N/Pellet. In contrast, the average strength of dry pellets containing cow dung was between 33.5% and 56.6% higher than dry pellets with no cow dung. For example, the average strength of dry pellets with no cow dung was 18.2 N/pellet, while pellets with a dung-to-anthracite ratio of 1 : 4 had an average strength of 27.7 N/pellet.Figure 2
Cold strength of carbon-bearing pellets with different proportions of cow dung. (a) Green pellet; (b) dry pellet.
(a)
(b)The FTIR spectral analyses of different pellet samples are provided in Figure3, which shows that the spectrum of the iron ore-anthracite sample (Figure 3(a)) aligns closely with the spectrum of the iron ore-anthracite-bentonite sample (Figure 3(b)). The main absorption peaks appear at 3413 cm−1 (stretching vibration centre of hydroxy-OH), 1619 cm−1 (antisymmetric vibration peak of carboxyl-COOH) and 1032 cm−1 (Si-O bond stretching vibration of silicate impurities). This demonstrates that bentonite is not chemically adsorbed with the raw materials such as iron ore and anthracite, and it can be assumed that the strength of these green pellets with no cow dung was maintained by alternative strength mechanisms such as capillary and viscous forces.Figure 3
FTIR spectra of carbon-bearing pellets, comparing different raw materials.A SEM backscattered image of a cross-sectioned dry pellet sample with no added cow dung is shown in Figure4(a). The bentonite, iron concentrate, and finely pulverised coal particles have formed a gel, which has surrounded or coated the particles. The gel has a bridging effect and increases the bridge fluid viscosity and surface tension, strengthening the capillary and viscous forces that bind the particles in the green pellets [24]. In the drying process, the bentonite can make the solid particles be further drawn by the gel, the area of particle contact be increased, the intermolecular forces be strengthened, and the strength of the dry pellet be improved [25].Figure 4
SEM back scattered images of different carbon-bearing pellets after drying. (a) Dry pellet sample without cow dung; (b) dry pellet sample with 14.0% cow dung.
(a)
(b)The FTIR spectra of a pellet sample containing anthracite, iron ore, and cow dung are shown in Figure3(c), while a pellet sample containing anthracite, iron ore, cow dung, and bentonite is shown in Figure 3(d). The main absorption peaks in Figure 3(c) appear at 3423 cm−1, 1631 cm−1, 1423 cm−1, and 1032 cm−1, while the main peaks in Figure 3(d) appear at 3420 cm−1, 1633 cm−1, and 1032 cm−1. The stretching vibration peak of hydroxy-OH and antisymmetric peak of carboxyl-COOH have shifted and increased in intensity. Near 1423 cm−1, the lignin double bond or the hydroxy of carboxylic acid has generated an in-plane bending vibration peak, which suggests that chemical adsorption has probably occurred between the cellulose, hemicellulose, and free hydroxy of lignin and iron ore.A SEM backscattered image of a cross-sectioned dry pellet sample containing 14.0% cow dung is shown in Figure4(b). It can be seen in the figure that the bentonite, iron ore, and finely pulverised coal have formed a gel, infilled with or coating, particles, similar to that observed in the sample that did not contain cow dung (Figure 4(a)). The cellulose and hemicellulose in the particles of cow dung have a rope-shaped arrangement that reinforces the structure of the dry pellets and results in greater strength compared with the dry pellets that did not contain any cow dung.


### 3.2. Effects of Treated Cow Dung Addition on the Strength of Carbon-Bearing Pellets after Reduction Roasting

The average strength of pellets that contained different proportions of cow dung after reduction roasting at 1523 K is given in Figure5. The bar chart shows that the strength of the roasted sample with no cow dung was 2473 N/pellet. The pellets that had cow dung additive had a higher strength, but the strength decreased with increasing cow dung addition. The pellets containing 4.1% cow dung had a strength of 3106 N/pellet after reduction roasting, which was the highest strength obtained (an increase of 25.6%).Figure 5
Strength of different carbon-bearing pellets after reduction roasting at 1523 K.The strength of reduction roasted pellets is controlled by the rate of formation of intergrown iron crystals, their abundance, and physical structure, while the bentonite binder will have little effect on pellet strength after roasting [26]. When a mixture of anthracite and cow dung is used as a reducing agent in carbon-bearing pellets, the volatile matter in the cow dung cracks at about 773 K and will produce H2, CO, CO2, CH4, and other gases [27]. Reduction reactions may occur directly between H2, CO, and CH4, while CO (which is a strong reductive agent) will be formed according to the Boudouard reaction between C (originating from the anthracite and cow dung additives) and CO2. Devolatilisation generates pores within the carbon-bearing pellets, which increases their permeability to the reducing gases, promoting the rate of reduction and formation of intergrown iron crystals.The size of the carbon-bearing pellets before and after reduction roasting is compared in Figure6, which shows that the diameter of the sample with no cow dung contracted by 19%, and the sample with 7.8% cow dung contracted by 24%, while the sample containing 14.0% cow dung contracted by 28%. Thus, it can be concluded that the pellet shrinkage increases with increasing cow dung content. The shrinkage of reduction roasted pellets is mainly the result of aggregation of intergrown iron crystals, but porosity and the amount of low melting-point slag present may also influence the extent of pellet shrinkage [28]. However, Figures 5 and 6 show that the pellet shrinkage does not clearly correlate with higher pellet strength.Figure 6
Size of the carbon-bearing pellets before and after reduction roasting.The metallisation degree of carbon-bearing pellets after reduction is shown in Table4. It can be seen that the metal produced of reduction sample gradually decreases with increase of amount of the cow dung. The pellets containing 4.1% cow dung had a degree of metallisation of 88.6% after reduction roasting, which was the highest degree of metallisation obtained.Table 4
Degree of metallization of carbon-bearing pellets after reduction roasting (%).
Sample number
Total Fe
Metal Fe
R
m
1
81.9
71.0
86.7
2
79.6
70.5
88.6
3
78.0
67.6
86.6
4
76.4
62.6
82.0
5
74.9
60.1
80.3


### 3.3. Phase Analysis of Carbon-Bearing Pellets after Reduction Roasting

Figure7 shows the XRD spectra of different pellet samples after reduction roasting at temperatures of 873, 1073, 1273, and 1523 K. It can be seen in Figure 7(a) that, after roasting at 873 K, the sample containing no cow dung additive was mainly composed of magnetite (Fe3O4) and a small amount of hematite (α-Fe2O3) and maghemite (γ-Fe2O3). In comparison, the peak intensity of α-Fe2O3 is smaller, while the peak intensity of Fe3O4 is larger, in the sample that originally contained 7.8% cow dung. When this sample (7.8% cow dung) was reduction roasted at 1073 K, diffraction peaks for wüstite (FeO) appeared, while the diffraction peaks of Fe2O3 were no longer detected (Figure 7(b)). After reduction roasting at 1273 K, diffraction peaks for metallic Fe were present, and their intensity was stronger in the sample with 7.8% cow dung compared to the sample with no cow dung (Figure 7(c)). Following reduction roasting at 1523 K, the XRD spectrum of the sample initially containing 7.8% cow dung consisted mainly of Fe diffraction peaks (Figure 7(d)). The results in Figure 7 demonstrated that cow dung addition and reduction temperature affect the extent of reduction of the iron oxides in the pellets. Taking into account the degree of metallisation in Table 4, it can be concluded that the extent of reduction at 1523 K decreases when the amount of cow dung additive exceeds about 4–8%.Figure 7
XRD of different carbon-bearing pellets after reduction at different temperatures. (a) 873 k; (b) 1073 k; (c) 1273 k; (d) 1523 k.
(a)
(b)
(c)
(d)SEM backscattered images of different carbon-bearing pellet samples reduction roasted at 1273 and 1523 K are shown in Figure8. Figure 8(a) shows that the edges of iron ore particles were blurred and boundaries between some of the ore and reducing agent particles were hard to distinguish in the sample that had no cow dung addition after roasting at 1273 K. There were few small particles of reducing agent observed, and the structure of the pellet was relatively loose. For the sample with 7.8% cow dung (Figure 8(b)), whole iron ore particles were hard to distinguish, while some metallic iron had formed on the surface of some iron ore and reducing agent particles. The microstructure of the roasted samples that contained 7.8% and 14.0% cow dung (Figures 8(b) and 8(c)) was relatively similar. After reduction roasting at 1523 K, the discrete particles of iron ore, reducing agent, and other raw materials disappeared (Figures 8(d)–8(f)), and the reduction product was predominantly metallic iron with a minor amount of iron oxide. In the sample with no added cow dung (Figure 8(d)), the metallic iron phase is connected by a number of fine grains and there are a considerable number of pores or voids in the pellets. The metallic iron in the samples with 7.8% and 14.0% cow dung is flaky, but the sample with 14.0% cow dung has more voids and the amount of solid solution formed by the metallic iron and incompletely reduced iron oxide is more abundant.Figure 8
SEM backscattered images of different carbon-bearing pellets after reduction at 1273 and 1523 K. (a) 1273 k, cow dung 0%; (b) 1273 k, cow dung 7.8%; (c) 1273 k, cow dung 14.0%; (d) 1523 k, cow dung 0%; (e) 1523 k, cow dung 7.8%; (f) 1523 k, cow dung 14.0%.
(a)
(b)
(c)
(d)
(e)
(f)Figures7 and 8 demonstrate the effect of cow dung addition and the influence of temperature on the microstructure and phase composition of reduction roasted pellets. After reduction roasting at 1523 K, the intergrown iron crystals in pellets that contained cow dung are strongly clustered compared with the samples containing no cow dung. The higher ash content of the cow dung compared to the anthracite can improve the quaternary basicity (mass ratio of (CaO+MgO)/(SiO2+Al2O3)) of the carbon-bearing pellets, promoting the reduction of iron oxides and facilitating the aggregation of intergrown iron crystals [29]. The larger amount of low melting-point amorphous slag produced can infill the pores, making the structure of the pellets stronger and more compact after reduction. However, an excessive addition of cow dung (of more than about 4–8%) will lead to more voids caused by hydrocarbon cracking and volatilisation, which will decrease the extent of metallisation during the reduction of iron oxides, resulting in a decrease pore filling by amorphous slag phases as well as decrease roasted pellet strength, compared with pellets that contained about 4% cow dung.


## 3.1. Effects of Treated Cow Dung Addition on the Cold Strength of Carbon-Bearing Pellets

The cold strength test results of green and dry pellets with different proportions of cow dung addition are shown in Figure2. The bar charts show that the strength of green and dry pellets varies with cow dung addition, but there is no clear correlation between the average compressive strength and the ratio of cow dung to anthracite added. The average strength of the green pellets containing cow dung decreased by 8–16% relative to pellets with no dung. For example, the strength of green pellets with no dung was 10.1 N/pellet, while green pellets with a dung-to-anthracite ratio of 1 : 4 (containing 4.1% cow dung) were 8.5 N/Pellet and the strength of green pellets with a dung-to-anthracite ratio of 3 : 4 (containing 11.1% cow dung) was 8.6 N/Pellet. In contrast, the average strength of dry pellets containing cow dung was between 33.5% and 56.6% higher than dry pellets with no cow dung. For example, the average strength of dry pellets with no cow dung was 18.2 N/pellet, while pellets with a dung-to-anthracite ratio of 1 : 4 had an average strength of 27.7 N/pellet.Figure 2
Cold strength of carbon-bearing pellets with different proportions of cow dung. (a) Green pellet; (b) dry pellet.
(a)
(b)The FTIR spectral analyses of different pellet samples are provided in Figure3, which shows that the spectrum of the iron ore-anthracite sample (Figure 3(a)) aligns closely with the spectrum of the iron ore-anthracite-bentonite sample (Figure 3(b)). The main absorption peaks appear at 3413 cm−1 (stretching vibration centre of hydroxy-OH), 1619 cm−1 (antisymmetric vibration peak of carboxyl-COOH) and 1032 cm−1 (Si-O bond stretching vibration of silicate impurities). This demonstrates that bentonite is not chemically adsorbed with the raw materials such as iron ore and anthracite, and it can be assumed that the strength of these green pellets with no cow dung was maintained by alternative strength mechanisms such as capillary and viscous forces.Figure 3
FTIR spectra of carbon-bearing pellets, comparing different raw materials.A SEM backscattered image of a cross-sectioned dry pellet sample with no added cow dung is shown in Figure4(a). The bentonite, iron concentrate, and finely pulverised coal particles have formed a gel, which has surrounded or coated the particles. The gel has a bridging effect and increases the bridge fluid viscosity and surface tension, strengthening the capillary and viscous forces that bind the particles in the green pellets [24]. In the drying process, the bentonite can make the solid particles be further drawn by the gel, the area of particle contact be increased, the intermolecular forces be strengthened, and the strength of the dry pellet be improved [25].Figure 4
SEM back scattered images of different carbon-bearing pellets after drying. (a) Dry pellet sample without cow dung; (b) dry pellet sample with 14.0% cow dung.
(a)
(b)The FTIR spectra of a pellet sample containing anthracite, iron ore, and cow dung are shown in Figure3(c), while a pellet sample containing anthracite, iron ore, cow dung, and bentonite is shown in Figure 3(d). The main absorption peaks in Figure 3(c) appear at 3423 cm−1, 1631 cm−1, 1423 cm−1, and 1032 cm−1, while the main peaks in Figure 3(d) appear at 3420 cm−1, 1633 cm−1, and 1032 cm−1. The stretching vibration peak of hydroxy-OH and antisymmetric peak of carboxyl-COOH have shifted and increased in intensity. Near 1423 cm−1, the lignin double bond or the hydroxy of carboxylic acid has generated an in-plane bending vibration peak, which suggests that chemical adsorption has probably occurred between the cellulose, hemicellulose, and free hydroxy of lignin and iron ore.A SEM backscattered image of a cross-sectioned dry pellet sample containing 14.0% cow dung is shown in Figure4(b). It can be seen in the figure that the bentonite, iron ore, and finely pulverised coal have formed a gel, infilled with or coating, particles, similar to that observed in the sample that did not contain cow dung (Figure 4(a)). The cellulose and hemicellulose in the particles of cow dung have a rope-shaped arrangement that reinforces the structure of the dry pellets and results in greater strength compared with the dry pellets that did not contain any cow dung.


## 3.2. Effects of Treated Cow Dung Addition on the Strength of Carbon-Bearing Pellets after Reduction Roasting

The average strength of pellets that contained different proportions of cow dung after reduction roasting at 1523 K is given in Figure5. The bar chart shows that the strength of the roasted sample with no cow dung was 2473 N/pellet. The pellets that had cow dung additive had a higher strength, but the strength decreased with increasing cow dung addition. The pellets containing 4.1% cow dung had a strength of 3106 N/pellet after reduction roasting, which was the highest strength obtained (an increase of 25.6%).Figure 5
Strength of different carbon-bearing pellets after reduction roasting at 1523 K.The strength of reduction roasted pellets is controlled by the rate of formation of intergrown iron crystals, their abundance, and physical structure, while the bentonite binder will have little effect on pellet strength after roasting [26]. When a mixture of anthracite and cow dung is used as a reducing agent in carbon-bearing pellets, the volatile matter in the cow dung cracks at about 773 K and will produce H2, CO, CO2, CH4, and other gases [27]. Reduction reactions may occur directly between H2, CO, and CH4, while CO (which is a strong reductive agent) will be formed according to the Boudouard reaction between C (originating from the anthracite and cow dung additives) and CO2. Devolatilisation generates pores within the carbon-bearing pellets, which increases their permeability to the reducing gases, promoting the rate of reduction and formation of intergrown iron crystals.The size of the carbon-bearing pellets before and after reduction roasting is compared in Figure6, which shows that the diameter of the sample with no cow dung contracted by 19%, and the sample with 7.8% cow dung contracted by 24%, while the sample containing 14.0% cow dung contracted by 28%. Thus, it can be concluded that the pellet shrinkage increases with increasing cow dung content. The shrinkage of reduction roasted pellets is mainly the result of aggregation of intergrown iron crystals, but porosity and the amount of low melting-point slag present may also influence the extent of pellet shrinkage [28]. However, Figures 5 and 6 show that the pellet shrinkage does not clearly correlate with higher pellet strength.Figure 6
Size of the carbon-bearing pellets before and after reduction roasting.The metallisation degree of carbon-bearing pellets after reduction is shown in Table4. It can be seen that the metal produced of reduction sample gradually decreases with increase of amount of the cow dung. The pellets containing 4.1% cow dung had a degree of metallisation of 88.6% after reduction roasting, which was the highest degree of metallisation obtained.Table 4
Degree of metallization of carbon-bearing pellets after reduction roasting (%).
Sample number
Total Fe
Metal Fe
R
m
1
81.9
71.0
86.7
2
79.6
70.5
88.6
3
78.0
67.6
86.6
4
76.4
62.6
82.0
5
74.9
60.1
80.3


## 3.3. Phase Analysis of Carbon-Bearing Pellets after Reduction Roasting

Figure7 shows the XRD spectra of different pellet samples after reduction roasting at temperatures of 873, 1073, 1273, and 1523 K. It can be seen in Figure 7(a) that, after roasting at 873 K, the sample containing no cow dung additive was mainly composed of magnetite (Fe3O4) and a small amount of hematite (α-Fe2O3) and maghemite (γ-Fe2O3). In comparison, the peak intensity of α-Fe2O3 is smaller, while the peak intensity of Fe3O4 is larger, in the sample that originally contained 7.8% cow dung. When this sample (7.8% cow dung) was reduction roasted at 1073 K, diffraction peaks for wüstite (FeO) appeared, while the diffraction peaks of Fe2O3 were no longer detected (Figure 7(b)). After reduction roasting at 1273 K, diffraction peaks for metallic Fe were present, and their intensity was stronger in the sample with 7.8% cow dung compared to the sample with no cow dung (Figure 7(c)). Following reduction roasting at 1523 K, the XRD spectrum of the sample initially containing 7.8% cow dung consisted mainly of Fe diffraction peaks (Figure 7(d)). The results in Figure 7 demonstrated that cow dung addition and reduction temperature affect the extent of reduction of the iron oxides in the pellets. Taking into account the degree of metallisation in Table 4, it can be concluded that the extent of reduction at 1523 K decreases when the amount of cow dung additive exceeds about 4–8%.Figure 7
XRD of different carbon-bearing pellets after reduction at different temperatures. (a) 873 k; (b) 1073 k; (c) 1273 k; (d) 1523 k.
(a)
(b)
(c)
(d)SEM backscattered images of different carbon-bearing pellet samples reduction roasted at 1273 and 1523 K are shown in Figure8. Figure 8(a) shows that the edges of iron ore particles were blurred and boundaries between some of the ore and reducing agent particles were hard to distinguish in the sample that had no cow dung addition after roasting at 1273 K. There were few small particles of reducing agent observed, and the structure of the pellet was relatively loose. For the sample with 7.8% cow dung (Figure 8(b)), whole iron ore particles were hard to distinguish, while some metallic iron had formed on the surface of some iron ore and reducing agent particles. The microstructure of the roasted samples that contained 7.8% and 14.0% cow dung (Figures 8(b) and 8(c)) was relatively similar. After reduction roasting at 1523 K, the discrete particles of iron ore, reducing agent, and other raw materials disappeared (Figures 8(d)–8(f)), and the reduction product was predominantly metallic iron with a minor amount of iron oxide. In the sample with no added cow dung (Figure 8(d)), the metallic iron phase is connected by a number of fine grains and there are a considerable number of pores or voids in the pellets. The metallic iron in the samples with 7.8% and 14.0% cow dung is flaky, but the sample with 14.0% cow dung has more voids and the amount of solid solution formed by the metallic iron and incompletely reduced iron oxide is more abundant.Figure 8
SEM backscattered images of different carbon-bearing pellets after reduction at 1273 and 1523 K. (a) 1273 k, cow dung 0%; (b) 1273 k, cow dung 7.8%; (c) 1273 k, cow dung 14.0%; (d) 1523 k, cow dung 0%; (e) 1523 k, cow dung 7.8%; (f) 1523 k, cow dung 14.0%.
(a)
(b)
(c)
(d)
(e)
(f)Figures7 and 8 demonstrate the effect of cow dung addition and the influence of temperature on the microstructure and phase composition of reduction roasted pellets. After reduction roasting at 1523 K, the intergrown iron crystals in pellets that contained cow dung are strongly clustered compared with the samples containing no cow dung. The higher ash content of the cow dung compared to the anthracite can improve the quaternary basicity (mass ratio of (CaO+MgO)/(SiO2+Al2O3)) of the carbon-bearing pellets, promoting the reduction of iron oxides and facilitating the aggregation of intergrown iron crystals [29]. The larger amount of low melting-point amorphous slag produced can infill the pores, making the structure of the pellets stronger and more compact after reduction. However, an excessive addition of cow dung (of more than about 4–8%) will lead to more voids caused by hydrocarbon cracking and volatilisation, which will decrease the extent of metallisation during the reduction of iron oxides, resulting in a decrease pore filling by amorphous slag phases as well as decrease roasted pellet strength, compared with pellets that contained about 4% cow dung.


## 4. Conclusions

The following conclusions can be made through this study.(1) The addition of cow dung affects the strength of carbon-bearing pellets. The green pellet strength decreased by about 8–16% and the dry strength increased by about 34–57% after adding cow dung. However, there was no obvious correlation between the quantity of cow dung added and the change in cold pellet strength. Compared with reduction roasted pellets containing no cow dung, roasted pellets containing cow dung had greater strength (ranging from about 16–26% stronger), but the strength decreased as the proportion of cow dung increased.(2) The lower strength of green pellets containing cow dung was found to be due to expansion of the amorphous region of the cellulose contained in the cow dung. The greater strength of dry pellets containing cow dung was found to be the result of chemical adsorption among cellulose, hemicellulose, and free hydroxy in lignin and iron concentrate. The rope arrangement of cellulose and hemicellulose also positively reinforces the pellet structure.(3) In process of reduction roasting of carbon-bearing pellets, cow dung additions is beneficial for aggregation of intergrown iron crystals and may help to increase the density of the physical structure of the pellets; thus the strength of the reduction roasted pellets is also improved. However, excessive addition of more than about 4–8% cow dung will result in lower pellet density and decreased strength compared with pellets containing about 4% cow dung.



---