A polyamide molding compound comprising the following components or consisting of these components: (A) 40 to 95 wt% of a polyamide mixture consisting of the polyamides (A1) and (A2), wherein (A1) 42 to 68 wt% of at least one semi-crystalline polyamide is selected from the group comprising PA 46, PA 66, PA 66/6, PA 610, PA 612, PA 614, PA 615, PA 616, and mixtures thereof; and (A2) 32 - 58 wt% of at least one transparent semi-aromatic polyamide having at least 30 mol% of monomers having aromatic structural units, with respect to the total quantity of diamines and dicarboxylic acids is in the polyamide (A2) that is amorphous or microcrystalline; (B) 5 to 50 wt% of at least one glass filler having a refractive index, measured in accordance with method B of ISO 489 (1999-04) in the range from 1.540 to 1.600; (C) 0 to 10 wt% of at least one additive; wherein the weight proportions of the components (A) to (C) add up to 100% by weight of the component (A) and the weight proportions of the components (A1) and (A2) add up to 100% by weight of component (A); wherein the at least one transparent polyamide (A2) has a transparency, measured in accordance with ASTM D1003 at a molded body (plate with the dimensions 60 × 60 × 2 mm) manufactured from the polyamides (A2) of at least 90% and a haze, measured in accordance with ASTM D1003 at a molded body (plate with the dimensions 60 × 60 × 2 mm) manufactured from the polyamides (A2) of at most 3%. (A) 40 to 95 wt% of a polyamide mixture consisting of the polyamides (A1) and (A2), wherein (A1) 42 to 68 wt% of at least one semi-crystalline polyamide is selected from the group comprising PA 46, PA 66, PA 66/6, PA 610, PA 612, PA 614, PA 615, PA 616, and mixtures thereof; and (A2) 32 - 58 wt% of at least one transparent semi-aromatic polyamide having at least 30 mol% of monomers having aromatic structural units, with respect to the total quantity of diamines and dicarboxylic acids is in the polyamide (A2) that is amorphous or microcrystalline; (A1) 42 to 68 wt% of at least one semi-crystalline polyamide is selected from the group comprising PA 46, PA 66, PA 66/6, PA 610, PA 612, PA 614, PA 615, PA 616, and mixtures thereof; and (A2) 32 - 58 wt% of at least one transparent semi-aromatic polyamide having at least 30 mol% of monomers having aromatic structural units, with respect to the total quantity of diamines and dicarboxylic acids is in the polyamide (A2) that is amorphous or microcrystalline; (B) 5 to 50 wt% of at least one glass filler having a refractive index, measured in accordance with method B of ISO 489 (1999-04) in the range from 1.540 to 1.600; (C) 0 to 10 wt% of at least one additive; wherein the weight proportions of the components (A) to (C) add up to 100% by weight of the component (A) and the weight proportions of the components (A1) and (A2) add up to 100% by weight of component (A); wherein the at least one transparent polyamide (A2) has a transparency, measured in accordance with ASTM D1003 at a molded body (plate with the dimensions 60 × 60 × 2 mm) manufactured from the polyamides (A2) of at least 90% and a haze, measured in accordance with ASTM D1003 at a molded body (plate with the dimensions 60 × 60 × 2 mm) manufactured from the polyamides (A2) of at most 3%. <EOS>