An adhesive sheet comprising: a rigid resin film having a yield modulus of 10 MPa to 300 MPa and having a thickness of 80 micrometers to 500 micrometers, a transparent resin film having a graphic image printed on a surface of the transparent resin film, and a first pressure sensitive adhesive layer being disposed on or above a surface of the rigid resin film, wherein the first pressure sensitive adhesive layer comprises elastic resin microspheres having a compressive elastic modulus at 20°C of 1 kPa to 100 kPa and having a volume average particle diameter of 110 micrometers or greater and a tacky binder, and the first pressure sensitive adhesive layer has an uneven surface due to the presence of the microspheres, which are contained in the first pressure sensitive adhesive layer in an amount of 5-200 parts by mass, wherein the yield modulus is the modulus of elasticity at the yield point when a test piece is produced by cutting a rigid resin film into a rectangular shape with a width of 15 mm and a length of 100 mm and the elongation properties of the test piece is measured using a tensile tester in accordance with JIS K 7127 under the condition at 20°C, the distance between grips of 50 mm, and the tensile speed of 300 mm/min, wherein the compressive elastic modulus is a measured value at 20°C determined by producing a sample obtained by forming microspheres having a cylindrical shape and performing measurement using a measurement instrument for viscoelasticity under the following conditions: frequency: 1 rad/sec; compression strain mode; measurement temperature range: -80°C to 150°C; rate of temperature increase: 5.0°C/min, and wherein the volume average particle diameter of the microspheres is measured by using a laser diffraction particle size analyzer. a rigid resin film having a yield modulus of 10 MPa to 300 MPa and having a thickness of 80 micrometers to 500 micrometers, a transparent resin film having a graphic image printed on a surface of the transparent resin film, and a first pressure sensitive adhesive layer being disposed on or above a surface of the rigid resin film, wherein the first pressure sensitive adhesive layer comprises elastic resin microspheres having a compressive elastic modulus at 20°C of 1 kPa to 100 kPa and having a volume average particle diameter of 110 micrometers or greater and a tacky binder, and the first pressure sensitive adhesive layer has an uneven surface due to the presence of the microspheres, which are contained in the first pressure sensitive adhesive layer in an amount of 5-200 parts by mass, wherein the yield modulus is the modulus of elasticity at the yield point when a test piece is produced by cutting a rigid resin film into a rectangular shape with a width of 15 mm and a length of 100 mm and the elongation properties of the test piece is measured using a tensile tester in accordance with JIS K 7127 under the condition at 20°C, the distance between grips of 50 mm, and the tensile speed of 300 mm/min, wherein the compressive elastic modulus is a measured value at 20°C determined by producing a sample obtained by forming microspheres having a cylindrical shape and performing measurement using a measurement instrument for viscoelasticity under the following conditions: frequency: 1 rad/sec; compression strain mode; measurement temperature range: -80°C to 150°C; rate of temperature increase: 5.0°C/min, and wherein the volume average particle diameter of the microspheres is measured by using a laser diffraction particle size analyzer. <EOS>