A coated article, comprising: a fibrous substrate; and at least one polymeric coating layer secured to at least a portion of a first surface of the fibrous substrate, the at least one polymeric coating layer having a coat weight of 13 g/m 2 or less, wherein the at least one polymeric coating layer comprises: 1) from 20 wt% to 80 wt% of an ethylene-based polymer having: a) a melt index of from 5 g/10 min to 30 g/10 min; b) a melt elastic modulus G' (G" = 500 Pa) at 170°C below 15 Pa; c) a relaxation time lambda at 170°C below 0.003 s; d) at least two second melt temp peaks between 110°C and 120°C; e) a weight average molecular weight (Mw) of from 10,000 g/mol to 55,000 g/mol; f) a molecular weight distribution (Mw/Mn) of from 2.0 to 5.0; and g) a Mz/Mw ratio of from 1.5 to 2.1; and 2) from 20 wt% to 80 wt% of: (i) a low density polyethylene; (ii) an ethylene acrylic acid copolymer; (iii) an ethyl-methyl acrylate copolymer; (iv) a polymer produced by polymerization at a pressure of 50 MPa-g or more; (v) an ethylene-methacrylic acid copolymer; or (vi) a combination thereof. a fibrous substrate; and at least one polymeric coating layer secured to at least a portion of a first surface of the fibrous substrate, the at least one polymeric coating layer having a coat weight of 13 g/m 2 or less, wherein the at least one polymeric coating layer comprises: 1) from 20 wt% to 80 wt% of an ethylene-based polymer having: a) a melt index of from 5 g/10 min to 30 g/10 min; b) a melt elastic modulus G' (G" = 500 Pa) at 170°C below 15 Pa; c) a relaxation time lambda at 170°C below 0.003 s; d) at least two second melt temp peaks between 110°C and 120°C; e) a weight average molecular weight (Mw) of from 10,000 g/mol to 55,000 g/mol; f) a molecular weight distribution (Mw/Mn) of from 2.0 to 5.0; and g) a Mz/Mw ratio of from 1.5 to 2.1; and 2) from 20 wt% to 80 wt% of: (i) a low density polyethylene; (ii) an ethylene acrylic acid copolymer; (iii) an ethyl-methyl acrylate copolymer; (iv) a polymer produced by polymerization at a pressure of 50 MPa-g or more; (v) an ethylene-methacrylic acid copolymer; or (vi) a combination thereof. 1) from 20 wt% to 80 wt% of an ethylene-based polymer having: a) a melt index of from 5 g/10 min to 30 g/10 min; b) a melt elastic modulus G' (G" = 500 Pa) at 170°C below 15 Pa; c) a relaxation time lambda at 170°C below 0.003 s; d) at least two second melt temp peaks between 110°C and 120°C; e) a weight average molecular weight (Mw) of from 10,000 g/mol to 55,000 g/mol; f) a molecular weight distribution (Mw/Mn) of from 2.0 to 5.0; and g) a Mz/Mw ratio of from 1.5 to 2.1; and a) a melt index of from 5 g/10 min to 30 g/10 min; b) a melt elastic modulus G' (G" = 500 Pa) at 170°C below 15 Pa; c) a relaxation time lambda at 170°C below 0.003 s; d) at least two second melt temp peaks between 110°C and 120°C; e) a weight average molecular weight (Mw) of from 10,000 g/mol to 55,000 g/mol; f) a molecular weight distribution (Mw/Mn) of from 2.0 to 5.0; and g) a Mz/Mw ratio of from 1.5 to 2.1; and 2) from 20 wt% to 80 wt% of: (i) a low density polyethylene; (ii) an ethylene acrylic acid copolymer; (iii) an ethyl-methyl acrylate copolymer; (iv) a polymer produced by polymerization at a pressure of 50 MPa-g or more; (v) an ethylene-methacrylic acid copolymer; or (vi) a combination thereof. <EOS>