A polyolefin composition comprising a blend of (A) a heterophasic polypropylene composition comprising - a propylene homopolymer or a propylene ethylene random copolymer and - an elastomeric ethylene propylene rubber, and (B) 5.0 to 30.0 wt% of an ethylene homo- or copolymer, based on the weight of the polyolefin composition wherein the heterophasic polypropylene composition is characterized by (a1) 75.0 to 95.0 wt% of a crystalline fraction (CF) having an ethylene content of up to 4.0 wt% and an MFR 2 of 0.1 to 100 g/10 min, wherein MFR 2 is determined according to ISO 1133 at 230 °C under a load of 2.16 kg and, (a2) 5.0 to 25.0 wt% of a soluble fraction (SF) having an ethylene content of 10.0 to 70.0 wt% and an intrinsic viscosity of 1.0 to 4.0 dl/g, wherein the crystalline fraction (CF) and the soluble fraction (SF) are determined in 1,2,4-trichlorobenzene at 40 °C, and wherein the ethylene homo- or copolymer has a density of at least 941 kg/m 3 and a melt flow rate MFR 21 of 1.0 to 7.5 g/10 min, wherein MFR 21 is determined according to ISO 1133 at 190 °C under a load of 21.6 kg. (A) a heterophasic polypropylene composition comprising - a propylene homopolymer or a propylene ethylene random copolymer and - an elastomeric ethylene propylene rubber, and - a propylene homopolymer or a propylene ethylene random copolymer and - an elastomeric ethylene propylene rubber, (B) 5.0 to 30.0 wt% of an ethylene homo- or copolymer, based on the weight of the polyolefin composition wherein the heterophasic polypropylene composition is characterized by (a1) 75.0 to 95.0 wt% of a crystalline fraction (CF) having an ethylene content of up to 4.0 wt% and an MFR 2 of 0.1 to 100 g/10 min, wherein MFR 2 is determined according to ISO 1133 at 230 °C under a load of 2.16 kg and, (a2) 5.0 to 25.0 wt% of a soluble fraction (SF) having an ethylene content of 10.0 to 70.0 wt% and an intrinsic viscosity of 1.0 to 4.0 dl/g, wherein the crystalline fraction (CF) and the soluble fraction (SF) are determined in 1,2,4-trichlorobenzene at 40 °C, and wherein the ethylene homo- or copolymer has a density of at least 941 kg/m 3 and a melt flow rate MFR 21 of 1.0 to 7.5 g/10 min, wherein MFR 21 is determined according to ISO 1133 at 190 °C under a load of 21.6 kg. wherein the heterophasic polypropylene composition is characterized by (a1) 75.0 to 95.0 wt% of a crystalline fraction (CF) having an ethylene content of up to 4.0 wt% and an MFR 2 of 0.1 to 100 g/10 min, wherein MFR 2 is determined according to ISO 1133 at 230 °C under a load of 2.16 kg and, (a2) 5.0 to 25.0 wt% of a soluble fraction (SF) having an ethylene content of 10.0 to 70.0 wt% and an intrinsic viscosity of 1.0 to 4.0 dl/g, wherein the crystalline fraction (CF) and the soluble fraction (SF) are determined in 1,2,4-trichlorobenzene at 40 °C, and (a1) 75.0 to 95.0 wt% of a crystalline fraction (CF) having an ethylene content of up to 4.0 wt% and an MFR 2 of 0.1 to 100 g/10 min, wherein MFR 2 is determined according to ISO 1133 at 230 °C under a load of 2.16 kg and, (a2) 5.0 to 25.0 wt% of a soluble fraction (SF) having an ethylene content of 10.0 to 70.0 wt% and an intrinsic viscosity of 1.0 to 4.0 dl/g, wherein the crystalline fraction (CF) and the soluble fraction (SF) are determined in 1,2,4-trichlorobenzene at 40 °C, and wherein the ethylene homo- or copolymer has a density of at least 941 kg/m 3 and a melt flow rate MFR 21 of 1.0 to 7.5 g/10 min, wherein MFR 21 is determined according to ISO 1133 at 190 °C under a load of 21.6 kg. <EOS>