A curable adhesive composition comprising a curable (meth)acrylate copolymer having a weight average molecular weight, determined by Gel Permeation Chromatography, in a range of 150,000 to 400,000 Da and an optional photoinitiator, wherein the curable (meth)acrylate copolymer comprises: a) a first monomeric unit of Formula in an amount of at least 50 weight percent based on a total weight of monomeric units in the curable (meth)acrylate copolymer wherein R 1 is hydrogen or methyl; and R 2 is an alkyl, heteroalkyl, aryl, aralkyl, or alkaryl group; b) a second monomeric unit of Formula in an amount in a range of 6 to 10 weight percent based on the total weight of monomeric units in the curable (meth)acrylate copolymer c) a third monomeric unit of Formula in an amount in a range of 0.05 to 5 weight percent based on the total weight of monomeric units of the curable (meth)acrylate copolymer wherein R 3 comprises 1) an aromatic ketone group that causes hydrogen abstraction from a polymeric chain when exposed to ultraviolet radiation or 2) a (meth)acryloyl group that undergoes free radical polymerization in the presence of the photoinitiator when exposed to ultraviolet or visible light radiation; and d) an optional fourth monomeric unit of Formula in an amount in a range of 0 to 20 weight percent based on the total weight of monomeric units of the curable (meth)acrylate copolymer wherein X is -O- or-NH-; R 4 is a hydroxy-substituted alky or hydroxy-substituted heteroalkyl group; and wherein the curable adhesive composition has a creep compliance that is less than 5(10 -4) inverse Pascals at 25°C measured at 287 seconds after application of a constant applied stress of 8000 Pascals; the curable adhesive composition has a creep compliance that is greater than 1(10 -3) inverse Pascals at 70°C measured at 287 seconds after application of a constant applied stress of 8000 Pascals; the curable adhesive composition has a shear storage modulus equal to at least 40 kiloPascals (kPa) when measured at 25°C and at a frequency of 1 radian/second, and wherein the weight average molecular weight, creep compliance, and shear storage modulus are measured according to the methods disclosed in the experimental section of this specification. a) a first monomeric unit of Formula in an amount of at least 50 weight percent based on a total weight of monomeric units in the curable (meth)acrylate copolymer wherein R 1 is hydrogen or methyl; and R 2 is an alkyl, heteroalkyl, aryl, aralkyl, or alkaryl group; R 1 is hydrogen or methyl; and R 2 is an alkyl, heteroalkyl, aryl, aralkyl, or alkaryl group; b) a second monomeric unit of Formula in an amount in a range of 6 to 10 weight percent based on the total weight of monomeric units in the curable (meth)acrylate copolymer c) a third monomeric unit of Formula in an amount in a range of 0.05 to 5 weight percent based on the total weight of monomeric units of the curable (meth)acrylate copolymer wherein R 3 comprises 1) an aromatic ketone group that causes hydrogen abstraction from a polymeric chain when exposed to ultraviolet radiation or 2) a (meth)acryloyl group that undergoes free radical polymerization in the presence of the photoinitiator when exposed to ultraviolet or visible light radiation; and d) an optional fourth monomeric unit of Formula in an amount in a range of 0 to 20 weight percent based on the total weight of monomeric units of the curable (meth)acrylate copolymer wherein X is -O- or-NH-; R 4 is a hydroxy-substituted alky or hydroxy-substituted heteroalkyl group; and X is -O- or-NH-; R 4 is a hydroxy-substituted alky or hydroxy-substituted heteroalkyl group; and