An aqueous coating composition comprising dispersed polymer particles, wherein (i) the dispersed polymer particles are polyurethane-vinyl polymer hybrid particles obtained by free-radical polymerization of at least one vinyl monomer in the presence of a polyurethane, (ii) the polyurethane and the vinyl polymer in the hybrid particles are present in a weight ratio of polyurethane to vinyl polymer ranging from 1:1 to 20:1, preferably from 2:1 to 16:1, even more preferably from 3:1 to 12:1, even more preferably from 4:1 to 12:1 and even more preferably from 4:1 to 10:1, (iii) the polyurethane is obtained by the reaction of at least the following components: (a) from 5 to 40 wt.%, preferably from 10 to 35 wt.% of at least one organic difunctional isocyanate, (b) from 0.5 to 4 wt.%, preferably from 0.8 to 3.2 wt.% and even more preferably from 1 to 2.5 wt% of an isocyanate-reactive compound containing ionic or potentially ionic water-dispersing groups having a molecular weight of from 100 to 500 g/mol, (c) from 40 to 80 wt.%, preferably from 45 to 75 wt.% and even more preferably from 50 to 70 wt.% of at least one diol having a molecular weight from 500 to 5000, (d) from 0 to 10 wt.%, preferably from 0.5 to 4 wt.% and more preferably from 1 to 3 wt.% of at least one active-hydrogen chain extending compound with a functionality of at least 2 (other than water), (e) from 0 to10 wt.% of at least one diol having a molecular weight below 500 g/mol, where the amounts of (a), (b), (c), (d) and (e) are given relative to the total amount of components used to prepare the polyurethane from which the building blocks from the polyurethane are emanated, and where the isocyanate and hydroxy groups on the components used to prepare the polyurethane are present in a respective mole ratio (NCO to OH) in the range of from 0.8:1 to 5:1, preferably from 1.05:1 to 5:1 and even more preferably from 1.1:1 to 3.5:1. (i) the dispersed polymer particles are polyurethane-vinyl polymer hybrid particles obtained by free-radical polymerization of at least one vinyl monomer in the presence of a polyurethane, (ii) the polyurethane and the vinyl polymer in the hybrid particles are present in a weight ratio of polyurethane to vinyl polymer ranging from 1:1 to 20:1, preferably from 2:1 to 16:1, even more preferably from 3:1 to 12:1, even more preferably from 4:1 to 12:1 and even more preferably from 4:1 to 10:1, (iii) the polyurethane is obtained by the reaction of at least the following components: (a) from 5 to 40 wt.%, preferably from 10 to 35 wt.% of at least one organic difunctional isocyanate, (b) from 0.5 to 4 wt.%, preferably from 0.8 to 3.2 wt.% and even more preferably from 1 to 2.5 wt% of an isocyanate-reactive compound containing ionic or potentially ionic water-dispersing groups having a molecular weight of from 100 to 500 g/mol, (c) from 40 to 80 wt.%, preferably from 45 to 75 wt.% and even more preferably from 50 to 70 wt.% of at least one diol having a molecular weight from 500 to 5000, (d) from 0 to 10 wt.%, preferably from 0.5 to 4 wt.% and more preferably from 1 to 3 wt.% of at least one active-hydrogen chain extending compound with a functionality of at least 2 (other than water), (e) from 0 to10 wt.% of at least one diol having a molecular weight below 500 g/mol, (a) from 5 to 40 wt.%, preferably from 10 to 35 wt.% of at least one organic difunctional isocyanate, (b) from 0.5 to 4 wt.%, preferably from 0.8 to 3.2 wt.% and even more preferably from 1 to 2.5 wt% of an isocyanate-reactive compound containing ionic or potentially ionic water-dispersing groups having a molecular weight of from 100 to 500 g/mol, (c) from 40 to 80 wt.%, preferably from 45 to 75 wt.% and even more preferably from 50 to 70 wt.% of at least one diol having a molecular weight from 500 to 5000, (d) from 0 to 10 wt.%, preferably from 0.5 to 4 wt.% and more preferably from 1 to 3 wt.% of at least one active-hydrogen chain extending compound with a functionality of at least 2 (other than water), (e) from 0 to10 wt.% of at least one diol having a molecular weight below 500 g/mol,