A method of manufacturing a direct blow-molded container, the container containing 60 to 90% by mass of a polyolefin, 5 to 30% by mass of an acid-modified polyolefin, and 2 to 35% by mass of a metaxylylene group-containing polyamide, the metaxylylene group-containing polyamide being dispersed and layered in the polyolefin, the method being characterized in comprising: using a die provided with a die body having a flow hole in which the melted resin extruded from an extruder flows and a cylindrical hollow having an opening in the lower side and the flow hole in the upper side, the opening and the flow hole opening downward and upward, respectively, a mandrel having a tip in the upper side, the tip pointing to the opening of the tip of the flow hole, and a support part formed in a flow path clearance so that the flow path clearance formed between the hollow of the die body and the mandrel defining a resin flow path, the support part holding the mandrel in the hollow of the die body; setting the temperature of the die to fall within the range between the melt beginning temperature and the melt ending temperature of the metaxylylene group-containing polyamide, the melt beginning temperature and the melt ending temperature being measured with a differential scanning calorimeter; feeding melted resin formed by the extruder to the flow hole; forming the melted resin flowing through the flow hole in a cylindrical shape wrapping around the mandrel by the tip of the mandrel; passing the cylindrical melted resin through the support part in the flow path clearance to divide the cylindrical melted resin immediately before the support part; joining the divided resin immediately after the support part so as to form the joined melted resin in a cylindrical shape again; and extruding the cylindrical melted resin from the opening. using a die provided with a die body having a flow hole in which the melted resin extruded from an extruder flows and a cylindrical hollow having an opening in the lower side and the flow hole in the upper side, the opening and the flow hole opening downward and upward, respectively, a mandrel having a tip in the upper side, the tip pointing to the opening of the tip of the flow hole, and a support part formed in a flow path clearance so that the flow path clearance formed between the hollow of the die body and the mandrel defining a resin flow path, the support part holding the mandrel in the hollow of the die body; a die body having a flow hole in which the melted resin extruded from an extruder flows and a cylindrical hollow having an opening in the lower side and the flow hole in the upper side, the opening and the flow hole opening downward and upward, respectively, a mandrel having a tip in the upper side, the tip pointing to the opening of the tip of the flow hole, and a support part formed in a flow path clearance so that the flow path clearance formed between the hollow of the die body and the mandrel defining a resin flow path, the support part holding the mandrel in the hollow of the die body; setting the temperature of the die to fall within the range between the melt beginning temperature and the melt ending temperature of the metaxylylene group-containing polyamide, the melt beginning temperature and the melt ending temperature being measured with a differential scanning calorimeter; feeding melted resin formed by the extruder to the flow hole; forming the melted resin flowing through the flow hole in a cylindrical shape wrapping around the mandrel by the tip of the mandrel; passing the cylindrical melted resin through the support part in the flow path clearance to divide the cylindrical melted resin immediately before the support part; joining the divided resin immediately after the support part so as to form the joined melted resin in a cylindrical shape again; and extruding the cylindrical melted resin from the opening.