A polymeric intraocular lens material, which is polymerization product of a polymerizable composition comprising (a) from 10% to 30% by weight of a hydrophilic monomer relative to the total amount of all polymerizable components, wherein the hydrophilic monomer is hydroxyethylmethacrylate, hydroxyethylacrylate, N-hydroxyethylmethacrylamide, N-hydroxyethylacrylamide, N,N-dimethylacrylamide, N,N-dimethylmethacrylamide, or a combination thereof, (b) from 20% to 85% by weight of one or more poly(phenyl ether)-containing monomers of formula relative to the total amount of all polymerizable components wherein: R 1 is H or CH 3; R a, R b, R c, R d, R e, R f, R g, R h, and R i independent of one another are H, C 1 -C 12 alkyl, or C 1 -C 12 alkoxy; B p is a direct bond, (CH 2) m1, or (OCH 2 CH 2) m2, in which m1 is 2-6 and m2 is 1-10; n1 is an integer from 1 to 9; n2 is an integer from 0 to 6; Y p is a direct bond, O, S, OC(=O)NH, NHC(=O)NH, or NR' in which R' is H, C 1 -C 10 alkyl, C 6 H 5, or CH 2 C 6 H 5, (c) from 0 to 50% by weight of one or more aryl acrylic monomers of formula relative to the total amount of all polymerizable components wherein A 1 is H or CH 3 (preferably H); B 1 is (CH 2) m1 or [O(CH 2) 2] z1 in which m1 is 2-6 and z1 is 1-10; Y 1 is a direct bond, O, S, or NR' in which R' is H, CH 3, C n' H 2n'+1 in which n'=1-10, iso-OC 3 H 7, C 6 H 5, or CH 2 C 6 H 5; W1 is 0-6, provided that m1+w1≤8; and D 1 is H, Cl, Br, C 1 -C 4 alkyl, C 1 -C 4 alkoxy, C 6 H 5, or CH 2 C 6 H 5, and (d) one or more polymerizable crosslinking agents, wherein the listed components and any additional polymerizable components add up to 100% by weight, wherein the intraocular lens material in a fully-hydrated state has: a glass transition temperature of less than 22°C, a refractive index of 1.55 or greater measured at 589 nm and at room temperature (23±2°C), an equilibrium water content of less than 5.0% by weight at a temperature of from 16°C to 45°C, a Young's modulus of less than 80 MPa, an elongation of at least 100%, a 100% secant modulus of less than 6.0 MPa, and a glistening resistance characterized by having no bright field microvacuoles and 10 or less microvacuoles per viewing screen. (a) from 10% to 30% by weight of a hydrophilic monomer relative to the total amount of all polymerizable components, wherein the hydrophilic monomer is hydroxyethylmethacrylate, hydroxyethylacrylate, N-hydroxyethylmethacrylamide, N-hydroxyethylacrylamide, N,N-dimethylacrylamide, N,N-dimethylmethacrylamide, or a combination thereof, (b) from 20% to 85% by weight of one or more poly(phenyl ether)-containing monomers of formula relative to the total amount of all polymerizable components wherein: R 1 is H or CH 3; R a, R b, R c, R d, R e, R f, R g, R h, and R i independent of one another are H, C 1 -C 12 alkyl, or C 1 -C 12 alkoxy; B p is a direct bond, (CH 2) m1, or (OCH 2 CH 2) m2, in which m1 is 2-6 and m2 is 1-10; n1 is an integer from 1 to 9; n2 is an integer from 0 to 6; Y p is a direct bond, O, S, OC(=O)NH, NHC(=O)NH, or NR' in which R' is H, C 1 -C 10 alkyl, C 6 H 5, or CH 2 C 6 H 5, R 1 is H or CH 3; R a, R b, R c, R d, R e, R f, R g, R h, and R i independent of one another are H, C 1 -C 12 alkyl, or C 1 -C 12 alkoxy; B p is a direct bond, (CH 2) m1, or (OCH 2 CH 2) m2, in which m1 is 2-6 and m2 is 1-10; n1 is an integer from 1 to 9; n2 is an integer from 0 to 6; Y p is a direct bond, O, S, OC(=O)NH, NHC(=O)NH, or NR' in which R' is H, C 1 -C 10 alkyl, C 6 H 5, or CH 2 C 6 H 5, (c) from 0 to 50% by weight of one or more aryl acrylic monomers of formula relative to the total amount of all polymerizable components wherein A 1 is H or CH 3 (preferably H); B 1 is (CH 2) m1 or [O(CH 2) 2] z1 in which m1 is 2-6 and z1 is 1-10; Y 1 is a direct bond, O, S, or NR' in which R' is H, CH 3, C n' H 2n'+1 in which n'=1-10, iso-OC 3 H 7, C 6 H 5, or CH 2 C 6 H 5; W1 is 0-6, provided that m1+w1≤8; and D 1 is H, Cl, Br, C 1 -C 4 alkyl, C 1 -C 4 alkoxy, C 6 H 5, or CH 2 C 6 H 5, and (d) one or more polymerizable crosslinking agents,