A process for batchwise or continuous production of single-layer or multilayer lignocellulose materials, comprising the process steps of (Ia) producing a mixture M1 and (Ib) optionally one or more mixture(s) M2, scattering mixture M1 and optionally mixture(s) M2 to give a mat, optionally precompacting the scattered mat and hot pressing, wherein mixture M1 comprises the lignocellulose particles (component LCP-1) and additionally a) 0.005% to 0.5% by weight of organic carboxylic acid, carboxylic anhydride, carbonyl chloride or mixtures thereof (component A) b) 0.05% to 3% by weight of organic isocyanates having at least two isocyanate groups (component B) and c) 5% to 15% by weight of binder selected from the group of the amino resins (component C) d) 0% to 2% by weight of hardener (component D) and e) 0% to 5% by weight of additive (component E), and mixture(s) M2 comprise(s) the lignocellulose particles (component LCP-2) and additionally f) 0% to 0.3% by weight of organic carboxylic acid, carboxylic anhydride, carbonyl chloride or mixtures thereof (component F), g) 1% to 30% by weight of binder selected from the group consisting of amino resin, phenolic resin, protein-based binder and other polymer-based binders or mixtures thereof (component G-1) and 0% to 3% by weight of organic isocyanate having at least two isocyanate groups (component G-2), h) 0% to 2% by weight of hardener (component H) and i) 0% to 5% by weight of additives (component I), with the proviso that the following conditions are fulfilled: a min < a < a max and a min = − 1 / 6000 · T + 65 / 6000, preferably a min = − 1 / 4500 · T + 65 / 4500, more preferably a min = − 1 / 3500 · T + 65 / 3500, and a max = − 1 / 2000 · T + 75 / 2000, preferably a max = − 1 / 2500 · T + 75 / 2500, more preferably a max = − 1 / 3000 · T + 75 / 3000, where T is the temperature of mixture M1 in °C after process step (Ia) and is between 10 and 65°C, preferably 10 and 60°C, more preferably 15 to 58°C, and a is the amount of acid equivalents in component A) in relation to the mass of component C) in mol/100 g. (Ia) producing a mixture M1 and (Ib) optionally one or more mixture(s) M2, scattering mixture M1 and optionally mixture(s) M2 to give a mat, optionally precompacting the scattered mat and hot pressing, wherein mixture M1 comprises the lignocellulose particles (component LCP-1) and additionally a) 0.005% to 0.5% by weight of organic carboxylic acid, carboxylic anhydride, carbonyl chloride or mixtures thereof (component A) b) 0.05% to 3% by weight of organic isocyanates having at least two isocyanate groups (component B) and c) 5% to 15% by weight of binder selected from the group of the amino resins (component C) d) 0% to 2% by weight of hardener (component D) and e) 0% to 5% by weight of additive (component E), and mixture(s) M2 comprise(s) the lignocellulose particles (component LCP-2) and additionally f) 0% to 0.3% by weight of organic carboxylic acid, carboxylic anhydride, carbonyl chloride or mixtures thereof (component F), g) 1% to 30% by weight of binder selected from the group consisting of amino resin, phenolic resin, protein-based binder and other polymer-based binders or mixtures thereof (component G-1) and 0% to 3% by weight of organic isocyanate having at least two isocyanate groups (component G-2), h) 0% to 2% by weight of hardener (component H) and i) 0% to 5% by weight of additives (component I), with the proviso that the following conditions are fulfilled: a min < a < a max and a min = − 1 / 6000 · T + 65 / 6000, preferably a min = − 1 / 4500 · T + 65 / 4500, more preferably a min = − 1 / 3500 · T + 65 / 3500, and a max = − 1 / 2000 · T + 75 / 2000, preferably a max = − 1 / 2500 · T + 75 / 2500, more preferably a max = − 1 / 3000 · T + 75 / 3000, where T is the temperature of mixture M1 in °C after process step (Ia) and is between 10 and 65°C, preferably 10 and 60°C, more preferably 15 to 58°C, and a is the amount of acid equivalents in component A) in relation to the mass of component C) in mol/100 g. a) 0.005% to 0.5% by weight of organic carboxylic acid, carboxylic anhydride, carbonyl chloride or mixtures thereof (component A) b) 0.05% to 3% by weight of organic isocyanates having at least two isocyanate groups (component B) and c) 5% to 15% by weight of binder selected from the group of the amino resins (component C) d) 0% to 2% by weight of hardener (component D) and e) 0% to 5% by weight of additive (component E), and mixture(s) M2 comprise(s) the lignocellulose particles (component LCP-2) and additionally f) 0% to 0.3% by weight of organic carboxylic acid, carboxylic anhydride, carbonyl chloride or mixtures thereof (component F), g) 1% to 30% by weight of binder selected from the group consisting of amino resin, phenolic resin, protein-based binder and other polymer-based binders or mixtures thereof (component G-1) and 0% to 3% by weight of organic isocyanate having at least two isocyanate groups (component G-2), h) 0% to 2% by weight of hardener (component H) and i) 0% to 5% by weight of additives (component I), T is the temperature of mixture M1 in °C after process step (Ia) and is between 10 and 65°C, preferably 10 and 60°C, more preferably 15 to 58°C, and a is the amount of acid equivalents in component A) in relation to the mass of component C) in mol/100 g.