A moulded laminated reinforced composite glass comprising nano composite comprising polyester resin, curing system comprising 2 % (by wt. of the resin) cobalt octoate and 1.5% % (by wt. of the resin) methyl ethyl ketone peroxide, nano particles comprising 0.1 % (by wt. of the resin) carbon nanotubes and 0.3 % (by wt. of the resin) nano clay, and extenders comprising 5 % (by wt. of the resin) epoxy and 3 % (by wt. of the resin) vinyl acetate, the nano composite having a cross section of 20 x 1000 x 1500 mm, wherein the moulded laminated reinforced composite glass further comprises two float glass sheets having equal thickness of 3 mm, wherein said glass sheets are surface treated with amino isopropyl ethoxy silane (AIES); and wherein the moulded laminated reinforced composite glass includes a bidirectional or a unidirectionally pre-stretched fabric with weight selected from one of 80, 120, 180 and 200 grams per square metre wherein: a) the pre-stretched fabric having weight 80 grams per square metre, is selected from bi-directionally pre-tensioned E-glass fabric and bi-directionally pre-tensioned synthetic Basalt fabric; or b) the pre-stretched fabric having weight 120 grams per square metre, is selected from bi-directionally pre-tensioned E-glass fabric and bi-directionally pre-tensioned synthetic Basalt fabric; or c) the pre-stretched fabric having weight 180 grams per square metre, is selected from bi-directionally pre-tensioned synthetic polyester fabric; or d) the pre-stretched fabric having weight 200 grams per square metre, is selected from bi-directionally pre-tensioned E-glass fabric, pre-tensioned synthetic Unidirectional-glass fabric, bi-directionally pre-tensioned synthetic Basalt fabric, and bi-directionally pre-tensioned synthetic polyester fabric. nano composite comprising polyester resin, curing system comprising 2 % (by wt. of the resin) cobalt octoate and 1.5% % (by wt. of the resin) methyl ethyl ketone peroxide, nano particles comprising 0.1 % (by wt. of the resin) carbon nanotubes and 0.3 % (by wt. of the resin) nano clay, and extenders comprising 5 % (by wt. of the resin) epoxy and 3 % (by wt. of the resin) vinyl acetate, the nano composite having a cross section of 20 x 1000 x 1500 mm, wherein the moulded laminated reinforced composite glass further comprises two float glass sheets having equal thickness of 3 mm, wherein said glass sheets are surface treated with amino isopropyl ethoxy silane (AIES); and wherein the moulded laminated reinforced composite glass includes a bidirectional or a unidirectionally pre-stretched fabric with weight selected from one of 80, 120, 180 and 200 grams per square metre wherein: a) the pre-stretched fabric having weight 80 grams per square metre, is selected from bi-directionally pre-tensioned E-glass fabric and bi-directionally pre-tensioned synthetic Basalt fabric; or b) the pre-stretched fabric having weight 120 grams per square metre, is selected from bi-directionally pre-tensioned E-glass fabric and bi-directionally pre-tensioned synthetic Basalt fabric; or c) the pre-stretched fabric having weight 180 grams per square metre, is selected from bi-directionally pre-tensioned synthetic polyester fabric; or d) the pre-stretched fabric having weight 200 grams per square metre, is selected from bi-directionally pre-tensioned E-glass fabric, pre-tensioned synthetic Unidirectional-glass fabric, bi-directionally pre-tensioned synthetic Basalt fabric, and bi-directionally pre-tensioned synthetic polyester fabric. a) the pre-stretched fabric having weight 80 grams per square metre, is selected from bi-directionally pre-tensioned E-glass fabric and bi-directionally pre-tensioned synthetic Basalt fabric; or b) the pre-stretched fabric having weight 120 grams per square metre, is selected from bi-directionally pre-tensioned E-glass fabric and bi-directionally pre-tensioned synthetic Basalt fabric; or c) the pre-stretched fabric having weight 180 grams per square metre, is selected from bi-directionally pre-tensioned synthetic polyester fabric; or d) the pre-stretched fabric having weight 200 grams per square metre, is selected from bi-directionally pre-tensioned E-glass fabric, pre-tensioned synthetic Unidirectional-glass fabric, bi-directionally pre-tensioned synthetic Basalt fabric, and bi-directionally pre-tensioned synthetic polyester fabric.