A method for processing a supply of post consumer scrap linear low density polyethylene film or low density polyethylene film into near-virgin quality blown film product, comprising: removing detected metal from the supply of film; tearing the supply of film in a shredder, wherein surface area of the film is exposed, including delaminating the film; discharging the torn film through a filter screen to a prewash/sink/float tank via a first washing screw; washing the torn film in the prewash/sink/float tank including a surfactant and agitating the film in the bath, wherein contaminates are removed from the delaminated film; wet grinding the film in a wet grinder and washing the ground film using a first rotating friction washer; transferring the ground film from the first rotating friction washer to a first turbo washer using a second washing screw; using the first turbo washer to provide additional cleaning of the ground film; washing the ground film in a second rotating friction washer after the film exits the first turbo washer; using a first turbo dryer to remove moisture from the film exiting the second rotating friction washer; using a second turbo washer to provide additional cleaning of the ground film exiting the first turbo dryer; separating the ground film in a hydrocyclone; washing the ground film in a third rotating friction washer after the film exits the hydrocyclone; drying the ground film in a second turbo dryer and then in a thermal drying apparatus resulting in the ground film containing not more than 10% by weight, water content; and compacting the dry ground film, without addition of water, into granulated objects of near-virgin quality blown film product. removing detected metal from the supply of film; tearing the supply of film in a shredder, wherein surface area of the film is exposed, including delaminating the film; discharging the torn film through a filter screen to a prewash/sink/float tank via a first washing screw; washing the torn film in the prewash/sink/float tank including a surfactant and agitating the film in the bath, wherein contaminates are removed from the delaminated film; wet grinding the film in a wet grinder and washing the ground film using a first rotating friction washer; transferring the ground film from the first rotating friction washer to a first turbo washer using a second washing screw; using the first turbo washer to provide additional cleaning of the ground film; washing the ground film in a second rotating friction washer after the film exits the first turbo washer; using a first turbo dryer to remove moisture from the film exiting the second rotating friction washer; using a second turbo washer to provide additional cleaning of the ground film exiting the first turbo dryer; washing the ground film in a second rotating friction washer after the film exits the first turbo washer; using a first turbo dryer to remove moisture from the film exiting the second rotating friction washer; using a second turbo washer to provide additional cleaning of the ground film exiting the first turbo dryer; separating the ground film in a hydrocyclone; washing the ground film in a third rotating friction washer after the film exits the hydrocyclone; drying the ground film in a second turbo dryer and then in a thermal drying apparatus resulting in the ground film containing not more than 10% by weight, water content; and compacting the dry ground film, without addition of water, into granulated objects of near-virgin quality blown film product.