A laminate for thermoforming comprising: a thermoplastic resin layer having a monolayer structure or a laminated structure including a (meth)acrylic resin-containing layer; and a cured film laminated on the (meth)acrylic resin-containing layer of the thermoplastic resin layer, wherein the total thickness of the laminate is 75 μm to 5000 μm, wherein the (meth)acrylic resin-containing layer contains 5 to 80% by mass of a methacrylic resin and 95 to 20% by mass of a copolymer containing an aromatic vinyl compound unit and a maleic anhydride unit, wherein the cured film includes a cured product of a curable composition containing one or more curable (meth)acrylates selected from a group of polyfunctional (meth)acrylates and polyfunctional urethane (meth)acrylates, wherein the cured film has a thickness of 10 to 20 μm, has a pencil hardness of a surface of 2H to 4H, and has a composite elastic modulus and a hardness at 23°C satisfying expressions to below: 3.12 ≤ X ≤ 9.43 0.25 ≤ Y ≤ 0.56 5.61 ≤ X + 10 Y ≤ 14.9 wherein X represents the composite elastic modulus (GPa) at 23°C of the cured film, and Y represents the hardness (GPa) at 23°C of the cured film, wherein the pencil hardness is measured in accordance with JIS K5600-5-4 as disclosed in the description, and wherein the composite elastic modulus and the hardness are measured by the nanoindentation method in accordance with ISO14577 as disclosed in the description, wherein the smallest bending radius R is 10 to 75 mm, and wherein the smallest bending radius R is measured according to the method disclosed in the description. a thermoplastic resin layer having a monolayer structure or a laminated structure including a (meth)acrylic resin-containing layer; and a cured film laminated on the (meth)acrylic resin-containing layer of the thermoplastic resin layer, wherein the total thickness of the laminate is 75 μm to 5000 μm, wherein the (meth)acrylic resin-containing layer contains 5 to 80% by mass of a methacrylic resin and 95 to 20% by mass of a copolymer containing an aromatic vinyl compound unit and a maleic anhydride unit, wherein the cured film includes a cured product of a curable composition containing one or more curable (meth)acrylates selected from a group of polyfunctional (meth)acrylates and polyfunctional urethane (meth)acrylates, wherein the cured film has a thickness of 10 to 20 μm, has a pencil hardness of a surface of 2H to 4H, and has a composite elastic modulus and a hardness at 23°C satisfying expressions to below: 3.12 ≤ X ≤ 9.43 0.25 ≤ Y ≤ 0.56 5.61 ≤ X + 10 Y ≤ 14.9 wherein X represents the composite elastic modulus (GPa) at 23°C of the cured film, and Y represents the hardness (GPa) at 23°C of the cured film, has a pencil hardness of a surface of 2H to 4H, and has a composite elastic modulus and a hardness at 23°C satisfying expressions to below: 3.12 ≤ X ≤ 9.43 0.25 ≤ Y ≤ 0.56 5.61 ≤ X + 10 Y ≤ 14.9 wherein X represents the composite elastic modulus (GPa) at 23°C of the cured film, and Y represents the hardness (GPa) at 23°C of the cured film, wherein the pencil hardness is measured in accordance with JIS K5600-5-4 as disclosed in the description, and wherein the composite elastic modulus and the hardness are measured by the nanoindentation method in accordance with ISO14577 as disclosed in the description, wherein the smallest bending radius R is 10 to 75 mm, and wherein the smallest bending radius R is measured according to the method disclosed in the description.