A rubber composition comprising, based on parts by weight per 100 parts by weight elastomer (phr): 100 parts by weight of a combination of conjugated diene-based elastomers comprising: from 10 to 50 phr, alternatively from 10 to 30 phr, of an organic solvent polymerization prepared styrene/butadiene elastomer having a Tg in a range of from -40°C to -30°C with a styrene content in a range of from 30 to 35 percent wherein said Tg S-SBR is extended with from 10 to 38 parts by weight per 100 parts of said styrene/butadiene elastomer of triglyceride vegetable oil; from 10 to 50 phr, alternatively from 20 to 40 phr, of aqueous emulsion polymerization prepared styrene/butadiene elastomer having a Tg in a range of from -65°C to -45°C with a styrene content in a range of from 15 to 30 percent; and from 20 to 60 phr, alternatively from 30 to 50 phr, of cis 1,4-polybutadiene rubber having a cis 1,4-isomeric content of at least 95 percent and having a Tg in a range of from -100°C to -108°C; from 50 to 250 phr, alternatively from 75 to 175 phr, of a filler comprising silica and carbon black; and from 5 to 45 phr, alternatively from 7 to 25 phr, of a resin comprising at least one of terpene, coumarone indene and styrene-alphamethylstyrene resins having a softening point within a range of from 60°C to 150°C. 100 parts by weight of a combination of conjugated diene-based elastomers comprising: from 10 to 50 phr, alternatively from 10 to 30 phr, of an organic solvent polymerization prepared styrene/butadiene elastomer having a Tg in a range of from -40°C to -30°C with a styrene content in a range of from 30 to 35 percent wherein said Tg S-SBR is extended with from 10 to 38 parts by weight per 100 parts of said styrene/butadiene elastomer of triglyceride vegetable oil; from 10 to 50 phr, alternatively from 20 to 40 phr, of aqueous emulsion polymerization prepared styrene/butadiene elastomer having a Tg in a range of from -65°C to -45°C with a styrene content in a range of from 15 to 30 percent; and from 20 to 60 phr, alternatively from 30 to 50 phr, of cis 1,4-polybutadiene rubber having a cis 1,4-isomeric content of at least 95 percent and having a Tg in a range of from -100°C to -108°C; from 10 to 50 phr, alternatively from 10 to 30 phr, of an organic solvent polymerization prepared styrene/butadiene elastomer having a Tg in a range of from -40°C to -30°C with a styrene content in a range of from 30 to 35 percent wherein said Tg S-SBR is extended with from 10 to 38 parts by weight per 100 parts of said styrene/butadiene elastomer of triglyceride vegetable oil; from 10 to 50 phr, alternatively from 20 to 40 phr, of aqueous emulsion polymerization prepared styrene/butadiene elastomer having a Tg in a range of from -65°C to -45°C with a styrene content in a range of from 15 to 30 percent; and from 20 to 60 phr, alternatively from 30 to 50 phr, of cis 1,4-polybutadiene rubber having a cis 1,4-isomeric content of at least 95 percent and having a Tg in a range of from -100°C to -108°C; from 50 to 250 phr, alternatively from 75 to 175 phr, of a filler comprising silica and carbon black; and from 5 to 45 phr, alternatively from 7 to 25 phr, of a resin comprising at least one of terpene, coumarone indene and styrene-alphamethylstyrene resins having a softening point within a range of from 60°C to 150°C.