A laminate having at least a substrate layer, a vapor deposition layer, a barrier coat layer, an adhesive layer, a barrier layer and a sealant layer, in this order, the adhesive layer having oxygen barrier properties, wherein the vapor deposition layer is a vapor deposition film composed of an inorganic material or inorganic oxide, wherein the barrier coat layer is formed by a coated film comprising an alkoxide hydrolysate or alkoxide hydrolytic condensate obtained by polycondensation of an alkoxide and a water-soluble polymer, by a sol-gel method, in the presence of a sol-gel catalyst, an acid, water and an organic solvent, wherein the resin composition that forms the adhesive layer comprises a resin having two or more hydroxyl groups in the molecule as functional groups, an isocyanate compound having two or more isocyanate groups in the molecule as functional groups, a specific phosphoric acid-modified compound selected from the group consisting of phosphoric acid, pyrophosphoric acid, triphosphoric acid, methyl acid phosphate, ethyl acid phosphate, butyl acid phosphate, dibutyl phosphate, 2-ethylhexyl acid phosphate, bis(2-ethylhexyl)phosphate, isododecyl acid phosphate, butoxyethyl acid phosphate, oleyl acid phosphate, tetracosyl acid phosphate, 2-hydroxyethyl methacrylate acid phosphate and polyoxyethylene alkyl ether phosphoric acid, and a lamellar inorganic compound including at least one of a kaolinite-serpentine clay mineral selected from halloysite, kaolinite, endelite, dickite, nacrite, antigorite and chrysotile, and a pyrophyllite-talc mineral selected from pyrophyllite, talc and kerolite, the main backbone containing a polyester, polyester-polyurethane, polyether or polyether-polyurethane, and wherein the barrier layer is a vapor deposition film comprising an inorganic material or inorganic oxide. wherein the vapor deposition layer is a vapor deposition film composed of an inorganic material or inorganic oxide, wherein the barrier coat layer is formed by a coated film comprising an alkoxide hydrolysate or alkoxide hydrolytic condensate obtained by polycondensation of an alkoxide and a water-soluble polymer, by a sol-gel method, in the presence of a sol-gel catalyst, an acid, water and an organic solvent, wherein the resin composition that forms the adhesive layer comprises a resin having two or more hydroxyl groups in the molecule as functional groups, an isocyanate compound having two or more isocyanate groups in the molecule as functional groups, a specific phosphoric acid-modified compound selected from the group consisting of phosphoric acid, pyrophosphoric acid, triphosphoric acid, methyl acid phosphate, ethyl acid phosphate, butyl acid phosphate, dibutyl phosphate, 2-ethylhexyl acid phosphate, bis(2-ethylhexyl)phosphate, isododecyl acid phosphate, butoxyethyl acid phosphate, oleyl acid phosphate, tetracosyl acid phosphate, 2-hydroxyethyl methacrylate acid phosphate and polyoxyethylene alkyl ether phosphoric acid, and a lamellar inorganic compound including at least one of a kaolinite-serpentine clay mineral selected from halloysite, kaolinite, endelite, dickite, nacrite, antigorite and chrysotile, and a pyrophyllite-talc mineral selected from pyrophyllite, talc and kerolite, a resin having two or more hydroxyl groups in the molecule as functional groups, an isocyanate compound having two or more isocyanate groups in the molecule as functional groups, a specific phosphoric acid-modified compound selected from the group consisting of phosphoric acid, pyrophosphoric acid, triphosphoric acid, methyl acid phosphate, ethyl acid phosphate, butyl acid phosphate, dibutyl phosphate, 2-ethylhexyl acid phosphate, bis(2-ethylhexyl)phosphate, isododecyl acid phosphate, butoxyethyl acid phosphate, oleyl acid phosphate, tetracosyl acid phosphate, 2-hydroxyethyl methacrylate acid phosphate and polyoxyethylene alkyl ether phosphoric acid, and a lamellar inorganic compound including at least one of a kaolinite-serpentine clay mineral selected from halloysite, kaolinite, endelite, dickite, nacrite, antigorite and chrysotile, and a pyrophyllite-talc mineral selected from pyrophyllite, talc and kerolite, the main backbone containing a polyester, polyester-polyurethane, polyether or polyether-polyurethane, and wherein the barrier layer is a vapor deposition film comprising an inorganic material or inorganic oxide.