A thermoplastic composition comprising: from 10 to 69 wt.% based on the weight of said composition of one or more heterophasic propylene copolymers consisting of i) a propylene-based matrix consisting of a propylene homopolymer and/or a propylene-α-olefin copolymer, said propylene-α-olefin copolymer consisting of at least 70 wt.% of propylene and at most 30 wt.% of α-olefin, based on the total weight of the propylene-α-olefin copolymer, and ii) a dispersed ethylene-α-olefin copolymer comprising ethylene and at least one C3 to C10 α-olefin; at least 30 wt.% based on the weight of said composition of a heterophasic propylene copolymer comprising: * from 70 to 92 wt.% based on the weight of said heterophasic propylene copolymer of a propylene-based matrix consisting of a polypropylene having a melt flow index of at least 150 g/10 min as determined by ISO1133 at 230 °C and 2.16 kg; and wherein the propylene polymer has an intrinsic viscosity IV PP; * from 8 to 30 wt.% based on the weight of said heterophasic propylene copolymer of a dispersed ethylene-α-olefin copolymer having an ethylene content of between 10 and 55 wt.% based on the weight of the ethylene-α-olefin copolymer and wherein the ethylene-α-olefin copolymer has an intrinsic viscosity IV EPR; and wherein the ratio of IV EPR /IV PP is between 3 and 7, wherein IV PP and IV EPR are determined according to ISO-1628-1 and ISO-1628-3 based on the amount of the xylene-soluble matter and xylene-insoluble matter measured according to ISO 16152; C) from 0 - 30 wt.% based on the weight of said composition of an ethylene-α-olefin elastomer comprising ethylene and at least one C3 to C10 α-olefin; D) from 1 - 30 wt.% based on the weight of said composition of a talc; E) from 0 - 10 wt.% based on the weight of said composition of a high-density polyethylene (HDPE); F) from 0 - 5 wt.% based on the weight of said composition of one or more additives. from 10 to 69 wt.% based on the weight of said composition of one or more heterophasic propylene copolymers consisting of i) a propylene-based matrix consisting of a propylene homopolymer and/or a propylene-α-olefin copolymer, said propylene-α-olefin copolymer consisting of at least 70 wt.% of propylene and at most 30 wt.% of α-olefin, based on the total weight of the propylene-α-olefin copolymer, and ii) a dispersed ethylene-α-olefin copolymer comprising ethylene and at least one C3 to C10 α-olefin; i) a propylene-based matrix consisting of a propylene homopolymer and/or a propylene-α-olefin copolymer, said propylene-α-olefin copolymer consisting of at least 70 wt.% of propylene and at most 30 wt.% of α-olefin, based on the total weight of the propylene-α-olefin copolymer, and ii) a dispersed ethylene-α-olefin copolymer comprising ethylene and at least one C3 to C10 α-olefin; at least 30 wt.% based on the weight of said composition of a heterophasic propylene copolymer comprising: * from 70 to 92 wt.% based on the weight of said heterophasic propylene copolymer of a propylene-based matrix consisting of a polypropylene having a melt flow index of at least 150 g/10 min as determined by ISO1133 at 230 °C and 2.16 kg; and wherein the propylene polymer has an intrinsic viscosity IV PP; * from 8 to 30 wt.% based on the weight of said heterophasic propylene copolymer of a dispersed ethylene-α-olefin copolymer having an ethylene content of between 10 and 55 wt.% based on the weight of the ethylene-α-olefin copolymer and wherein the ethylene-α-olefin copolymer has an intrinsic viscosity IV EPR; and wherein the ratio of IV EPR /IV PP is between 3 and 7, wherein IV PP and IV EPR are determined according to ISO-1628-1 and ISO-1628-3 based on the amount of the xylene-soluble matter and xylene-insoluble matter measured according to ISO 16152; * from 70 to 92 wt.% based on the weight of said heterophasic propylene copolymer of a propylene-based matrix consisting of a polypropylene having a melt flow index of at least 150 g/10 min as determined by ISO1133 at 230 °C and 2.16 kg; and wherein the propylene polymer has an intrinsic viscosity IV PP; * from 8 to 30 wt.% based on the weight of said heterophasic propylene copolymer of a dispersed ethylene-α-olefin copolymer having an ethylene content of between 10 and 55 wt.% based on the weight of the ethylene-α-olefin copolymer and wherein the ethylene-α-olefin copolymer has an intrinsic viscosity IV EPR; and C) from 0 - 30 wt.% based on the weight of said composition of an ethylene-α-olefin elastomer comprising ethylene and at least one C3 to C10 α-olefin; D) from 1 - 30 wt.% based on the weight of said composition of a talc; E) from 0 - 10 wt.% based on the weight of said composition of a high-density polyethylene (HDPE); F) from 0 - 5 wt.% based on the weight of said composition of one or more additives.