A heterophasic polypropylene composition comprising: a. 60.0 to 85.0 wt.-% of a first heterophasic propylene ethylene copolymer (HECO1), having: i. a crystalline fraction determined according to CRYSTEX QC method ISO 6427-B in 1,2,4-trichlorobenzene, present in an amount in the range from 75.0 to 92.0 wt.-%, relative to the total weight of HECO1; ii. a soluble fraction determined according to CRYSTEX QC method ISO 6427-B in 1,2,4-trichlorobenzene, present in an amount in the range from 8.0 to 25.0 wt.-%, relative to the total weight of HECO1; iii. an intrinsic viscosity of the soluble fraction (IV) in the range from 2.00 to 4.00 dl/g; b. 5.0 to 20.0 wt.-% of a second heterophasic propylene ethylene copolymer (HECO2), having i. a soluble fraction determined according to CRYSTEX QC method ISO 6427-B in 1,2,4-trichlorobenzene, in the range from 15.0 to 30.0 wt.-%; ii. an intrinsic viscosity of the soluble fraction (IV) in the range from 2.5 to 5.0 dl/g; and c. 5.0 to 20.0 wt.-% of a polymer of ethylene, being selected from an ethylene-based plastomer and an LDPE, having a density in the range from 895 to 925 kg/m 3; wherein the heterophasic polypropylene composition has a melt flow rate MFR 2, measured according to ISO 1133-1 at 230 °C at a load of 2.16 kg, in the range from 15.0 to 40.0 g/10 min, and a soluble fraction determined according to CRYSTEX QC method ISO 6427-B in 1,2,4-trichlorobenzene, present in an amount in the range from 5.0 to 23.0 wt.-% relative to the total weight of the heterophasic polypropylene composition, wherein the ratio of the melt flow rates MFR 2, measured according to ISO 1133-1 at 230 °C at a load of 2.16 kg, of the first heterophasic propylene ethylene copolymer (HECO1) and the second heterophasic propylene ethylene copolymer (HECO2), MFR 2 (HECO1)/MFR 2 (HECO2), is at least 2.0, and wherein the combined amounts of the first heterophasic propylene ethylene copolymer (HECO1), the second heterophasic propylene ethylene copolymer (HECO2) and the polymer of ethylene are greater than or equal to 95 wt.-%, relative to the total weight of the heterophasic polypropylene composition. a. 60.0 to 85.0 wt.-% of a first heterophasic propylene ethylene copolymer (HECO1), having: i. a crystalline fraction determined according to CRYSTEX QC method ISO 6427-B in 1,2,4-trichlorobenzene, present in an amount in the range from 75.0 to 92.0 wt.-%, relative to the total weight of HECO1; ii. a soluble fraction determined according to CRYSTEX QC method ISO 6427-B in 1,2,4-trichlorobenzene, present in an amount in the range from 8.0 to 25.0 wt.-%, relative to the total weight of HECO1; iii. an intrinsic viscosity of the soluble fraction (IV) in the range from 2.00 to 4.00 dl/g; i. a crystalline fraction determined according to CRYSTEX QC method ISO 6427-B in 1,2,4-trichlorobenzene, present in an amount in the range from 75.0 to 92.0 wt.-%, relative to the total weight of HECO1; ii. a soluble fraction determined according to CRYSTEX QC method ISO 6427-B in 1,2,4-trichlorobenzene, present in an amount in the range from 8.0 to 25.0 wt.-%, relative to the total weight of HECO1; iii. an intrinsic viscosity of the soluble fraction (IV) in the range from 2.00 to 4.00 dl/g; b. 5.0 to 20.0 wt.-% of a second heterophasic propylene ethylene copolymer (HECO2), having i. a soluble fraction determined according to CRYSTEX QC method ISO 6427-B in 1,2,4-trichlorobenzene, in the range from 15.0 to 30.0 wt.-%; ii. an intrinsic viscosity of the soluble fraction (IV) in the range from 2.5 to 5.0 dl/g; and i. a soluble fraction determined according to CRYSTEX QC method ISO 6427-B in 1,2,4-trichlorobenzene, in the range from 15.0 to 30.0 wt.-%; ii. an intrinsic viscosity of the soluble fraction (IV) in the range from 2.5 to 5.0 dl/g; and c. 5.0 to 20.0 wt.-% of a polymer of ethylene, being selected from an ethylene-based plastomer and an LDPE, having a density in the range from 895 to 925 kg/m 3; wherein the heterophasic polypropylene composition has a melt flow rate MFR 2, measured according to ISO 1133-1 at 230 °C at a load of 2.16 kg, in the range from 15.0 to 40.0 g/10 min, and a soluble fraction determined according to CRYSTEX QC method ISO 6427-B in 1,2,4-trichlorobenzene, present in an amount in the range from 5.0 to 23.0 wt.-% relative to the total weight of the heterophasic polypropylene composition, wherein the ratio of the melt flow rates MFR 2, measured according to ISO 1133-1 at 230 °C at a load of 2.16 kg, of the first heterophasic propylene ethylene copolymer (HECO1) and the second heterophasic propylene ethylene copolymer (HECO2), MFR 2 (HECO1)/MFR 2 (HECO2), is at least 2.0, and wherein the combined amounts of the first heterophasic propylene ethylene copolymer (HECO1), the second heterophasic propylene ethylene copolymer (HECO2) and the polymer of ethylene are greater than or equal to 95 wt.-%, relative to the total weight of the heterophasic polypropylene composition.