A soft-touch feel polymeric composition comprising a blend of: i. 15 to 50 weight percent of a first polymeric component including a relatively hard thermoplastic; wherein the first polymeric component is a polypropylene selected from the group consisting of a polypropylene homopolymer, an impact polypropylene, a random polypropylene copolymer of ethylene and propylene, and any combination thereof, wherein the polypropylene has a crystallinity of greater than 31 percent, measured by differential scanning calorimetry, a melting temperature greater than about 125 °C, measured by differential scanning calorimetry, and is characterized by a melt flow rate from 20 to 500 g/10 min as measured according to ASTM D-1238 at 230°C / 2.16 kg; ii. greater than 20 weight percent of a second polymeric component, based on the total weight of the first and second polymer components, including a relatively soft thermoplastic as compared with the first polymeric component and a crystallinity of less than 30 percent, measured by differential scanning calorimetry, wherein the relatively soft thermoplastic is a lower-α-olefin/α-olefin interpolymer (LAO/α-olefin interpolymer) which is a multiblock copolymer having at least two hard blocks, and at least two soft blocks that are softer than the hard blocks, wherein the concentration of the soft blocks is 50 to 95 weight percent based on the total weight of the LAO/α-olefin interpolymer, the lower-α-olefin is ethylene, and the LAO/α-olefin interpolymer has a density of 0.850 to 0.895 g/cm 3; and iii. 10 to 40 weight percent glass fibers based on the total weight of the polymeric composition; and iv. a maleic anhydride grafted polypropylene coupling agent; wherein the polymeric composition has a melt flow rate of at least 5 g/10 min as measured according to ASTM D-1238 at 230 °C / 2.16 kg. i. 15 to 50 weight percent of a first polymeric component including a relatively hard thermoplastic; wherein the first polymeric component is a polypropylene selected from the group consisting of a polypropylene homopolymer, an impact polypropylene, a random polypropylene copolymer of ethylene and propylene, and any combination thereof, wherein the polypropylene has a crystallinity of greater than 31 percent, measured by differential scanning calorimetry, a melting temperature greater than about 125 °C, measured by differential scanning calorimetry, and is characterized by a melt flow rate from 20 to 500 g/10 min as measured according to ASTM D-1238 at 230°C / 2.16 kg; ii. greater than 20 weight percent of a second polymeric component, based on the total weight of the first and second polymer components, including a relatively soft thermoplastic as compared with the first polymeric component and a crystallinity of less than 30 percent, measured by differential scanning calorimetry, wherein the relatively soft thermoplastic is a lower-α-olefin/α-olefin interpolymer (LAO/α-olefin interpolymer) which is a multiblock copolymer having at least two hard blocks, and at least two soft blocks that are softer than the hard blocks, wherein the concentration of the soft blocks is 50 to 95 weight percent based on the total weight of the LAO/α-olefin interpolymer, the lower-α-olefin is ethylene, and the LAO/α-olefin interpolymer has a density of 0.850 to 0.895 g/cm 3; and iii. 10 to 40 weight percent glass fibers based on the total weight of the polymeric composition; and iv. a maleic anhydride grafted polypropylene coupling agent;