A flame-resistant airbag obtained by forming, on at least one side of an airbag base fabric, a cured film of an addition-curable liquid silicone rubber composition having a coating weight of 5 to 150 g/m 2, which composition comprises: 100 parts by weight of organopolysiloxane which includes at least two silicon-bonded alkenyl groups of 2 to 8 carbon atoms per molecule and is liquid at 25°C; from 5 to 100 parts by weight of three-dimensional network-type organopolysiloxane resin in which from 0.05 to 0.15 mol/100 g of alkenyl groups are bonded solely to difunctional R 1 R 2 SiO 2/2 units (D units; in the formula, R 1 is an alkenyl group of 2 to 8 carbon atoms and R 2 is a group selected from alkyl groups of 1 to 8 carbon atoms, alkenyl groups of 2 to 8 carbon atoms and aryl groups of 6 to 12 carbon atoms), in which the ratio (M units/T and/or Q units) of monofunctional R 3 3 SiO 1/2 units (M units; in the formula, each R 3 is independently a group selected from alkyl groups of 1 to 8 carbon atoms and aryl groups of 6 to 12 carbon atoms) to branched siloxane units which are trifunctional R 3 SiO 3/2 units (T units; in the formula, R 3 is the same as above) and/or tetrafunctional SiO 4/2 units (Q units) is from 0.65 to 1.40, and in which the amount of hydroxyl groups is 0.040 mol/100 g or less, as measured by the method of measuring amount of hydroxyl groups described in the description; from 10 to 30 parts by weight of silica fine powder having a specific surface area according to the BET method of at least 50 m 2 /g; organohydrogenpolysiloxane containing at least two silicon-bonded hydrogen atoms per molecule, in an amount such that the number of silicon-bonded hydrogen atoms included on a molecule of component per silicon-bonded alkenyl group in components and combined is from 1 to 10; an effective amount of a platinum family metal catalyst as a hydrosilylation reaction catalyst; and from 0.1 to 10 parts by weight of organosilicon compound containing an adhesion-promoting functional group, wherein when component contains an alkenyl group and/or a SiH group, it is included in an amount such that the number of silicon-bonded hydrogen atoms on components and per silicon-bonded alkenyl group on components, and is in the range of 1 to 10. 100 parts by weight of organopolysiloxane which includes at least two silicon-bonded alkenyl groups of 2 to 8 carbon atoms per molecule and is liquid at 25°C; from 5 to 100 parts by weight of three-dimensional network-type organopolysiloxane resin in which from 0.05 to 0.15 mol/100 g of alkenyl groups are bonded solely to difunctional R 1 R 2 SiO 2/2 units (D units; in the formula, R 1 is an alkenyl group of 2 to 8 carbon atoms and R 2 is a group selected from alkyl groups of 1 to 8 carbon atoms, alkenyl groups of 2 to 8 carbon atoms and aryl groups of 6 to 12 carbon atoms), in which the ratio (M units/T and/or Q units) of monofunctional R 3 3 SiO 1/2 units (M units; in the formula, each R 3 is independently a group selected from alkyl groups of 1 to 8 carbon atoms and aryl groups of 6 to 12 carbon atoms) to branched siloxane units which are trifunctional R 3 SiO 3/2 units (T units; in the formula, R 3 is the same as above) and/or tetrafunctional SiO 4/2 units (Q units) is from 0.65 to 1.40, and in which the amount of hydroxyl groups is 0.040 mol/100 g or less, as measured by the method of measuring amount of hydroxyl groups described in the description; from 10 to 30 parts by weight of silica fine powder having a specific surface area according to the BET method of at least 50 m 2 /g; organohydrogenpolysiloxane containing at least two silicon-bonded hydrogen atoms per molecule, in an amount such that the number of silicon-bonded hydrogen atoms included on a molecule of component per silicon-bonded alkenyl group in components and combined is from 1 to 10; an effective amount of a platinum family metal catalyst as a hydrosilylation reaction catalyst; and from 0.1 to 10 parts by weight of organosilicon compound containing an adhesion-promoting functional group, wherein when component contains an alkenyl group and/or a SiH group, it is included in an amount such that the number of silicon-bonded hydrogen atoms on components and per silicon-bonded alkenyl group on components, and is in the range of 1 to 10.