Method for manufacturing a colored laminated glazing comprising at least a first glass sheet and a second glass sheet, the two sheets being connected to one another by a thermoplastic interlayer, characterized in that it comprises the following steps: - depositing a stack of layers comprising at least one functional layer on at least one face of the first and/or second glass sheet, said functional layers being metal layers based on silver, on an alloy comprising silver, or on a metal selected from niobium, tantalum, molybdenum and/or zirconium, and the thickness of the functional coating being less than 300 nm, - depositing, in liquid form, a polymeric layer comprising an anthraquinone as a coloring agent and (meth)acrylate compounds as polymeric compounds on at least one face of the first and/or second glass sheet, the polymeric compounds used in the polymeric layer being chemically compatible with the thermoplastic interlayer, the polymeric composition comprising at least one urethane-acrylic oligomer, at least one mono-, bi- or trifunctional (meth)acrylate monomer, at least one polymerization initiator and at least one coloring agent which is dissolved in the polymeric composition and represents between 0.01 and 10% by weight with respect to the total weight of the polymeric compounds, - drying and optionally curing the polymeric layer, - assembling the glass sheet coated with the colored polymeric layer with a colorless transparent thermoplastic interlayer, and with the second glass sheet, so that the colored polymeric layer is in direct contact with said interlayer, - degassing, during which the air trapped between the glass sheets and the thermoplastic interlayer is removed, and - performing a heat treatment of the laminated glass under pressure and/or under vacuum at a temperature of between 100 and 200°C, during which the coloring agent present in the polymeric layer migrates toward the thermoplastic interlayer and during which the laminated glazing is assembled, and and in that the thermoplastic interlayer is polyvinyl butyral, polyethylene or ethylene-vinyl acetate. - depositing a stack of layers comprising at least one functional layer on at least one face of the first and/or second glass sheet, said functional layers being metal layers based on silver, on an alloy comprising silver, or on a metal selected from niobium, tantalum, molybdenum and/or zirconium, and the thickness of the functional coating being less than 300 nm, - depositing, in liquid form, a polymeric layer comprising an anthraquinone as a coloring agent and (meth)acrylate compounds as polymeric compounds on at least one face of the first and/or second glass sheet, the polymeric compounds used in the polymeric layer being chemically compatible with the thermoplastic interlayer, the polymeric composition comprising at least one urethane-acrylic oligomer, at least one mono-, bi- or trifunctional (meth)acrylate monomer, at least one polymerization initiator and at least one coloring agent which is dissolved in the polymeric composition and represents between 0.01 and 10% by weight with respect to the total weight of the polymeric compounds, - drying and optionally curing the polymeric layer, - assembling the glass sheet coated with the colored polymeric layer with a colorless transparent thermoplastic interlayer, and with the second glass sheet, so that the colored polymeric layer is in direct contact with said interlayer, - degassing, during which the air trapped between the glass sheets and the thermoplastic interlayer is removed, and - performing a heat treatment of the laminated glass under pressure and/or under vacuum at a temperature of between 100 and 200°C, during which the coloring agent present in the polymeric layer migrates toward the thermoplastic interlayer and during which the laminated glazing is assembled, and