A curable coating composition comprising: a silicone imine resin which in the presence of sufficient amounts of water forms an amino-functional silicone resin of the fully condensed formula R x SiO (4-x)/2 where (a) x is a number from 1.0 to 2.1; (b) the amino-functional silicone resin is comprised of the Si units R 3 SiO 1/2, R 2 SiO 2/2, RSiO 3/2, and SiO 4/2 in polymerized form, where at least 5 mole percent of the total amount of Si units of the amino-functional silicone resin comprise (i) RSiO 3/2 groups, (ii) SiO 4/2 groups or (iii) mixtures thereof; (c) each R is independently an alkyl group, an aryl group, or an amino-functional hydrocarbyl group, provided that the -NH- equivalent mass of the amino-functional silicone resin is from 50 to 750; and an acrylic copolymer which has, in polymerized form, epoxy functionalized groups having an epoxy equivalent weight in the range of 200-600 as determined in accordance with ASTM D1652, and cure compatibility groups comprising monomer groups, in polymerized form, that contain one or more of alcohol functionality, a phenolic group, a tertiary amine or an acid group that is either pendant to the backbone or attached as an end group; and wherein the coating composition has a molar ratio of amine NH functionality from hydrolyzed imine functionality on the silicone imine resin, to epoxy functionality, in the range of from 0.5 to 1.3, and wherein NH equivalent mass is determined by obtaining a 13 C-NMR spectrum of a known amount of solution of, or neat sample of, the amino-functional silicone resin and quantifying the peaks associated with the amino-functional Si units of the amino-functional silicone resin relative to those associated with a known amount of an internal standard, then adjusting for solvent content present in the sample, if any, as determined by gas chromatography. a silicone imine resin which in the presence of sufficient amounts of water forms an amino-functional silicone resin of the fully condensed formula R x SiO (4-x)/2 where (a) x is a number from 1.0 to 2.1; (b) the amino-functional silicone resin is comprised of the Si units R 3 SiO 1/2, R 2 SiO 2/2, RSiO 3/2, and SiO 4/2 in polymerized form, where at least 5 mole percent of the total amount of Si units of the amino-functional silicone resin comprise (i) RSiO 3/2 groups, (ii) SiO 4/2 groups or (iii) mixtures thereof; (c) each R is independently an alkyl group, an aryl group, or an amino-functional hydrocarbyl group, provided that the -NH- equivalent mass of the amino-functional silicone resin is from 50 to 750; and (a) x is a number from 1.0 to 2.1; (b) the amino-functional silicone resin is comprised of the Si units R 3 SiO 1/2, R 2 SiO 2/2, RSiO 3/2, and SiO 4/2 in polymerized form, where at least 5 mole percent of the total amount of Si units of the amino-functional silicone resin comprise (i) RSiO 3/2 groups, (ii) SiO 4/2 groups or (iii) mixtures thereof; (c) each R is independently an alkyl group, an aryl group, or an amino-functional hydrocarbyl group, provided that the -NH- equivalent mass of the amino-functional silicone resin is from 50 to 750; and an acrylic copolymer which has, in polymerized form, epoxy functionalized groups having an epoxy equivalent weight in the range of 200-600 as determined in accordance with ASTM D1652, and cure compatibility groups comprising monomer groups, in polymerized form, that contain one or more of alcohol functionality, a phenolic group, a tertiary amine or an acid group that is either pendant to the backbone or attached as an end group; and