A stretched multilayer thermoplastic resin film comprising a layer containing a thermoplastic resin on at least one surface of a layer containing a thermoplastic resin, said stretched multilayer thermoplastic resin film being characterized in that: an intrinsic birefringence of each of the thermoplastic resin and the thermoplastic resin is -0.005 to 0.005; a glass transition temperature of the thermoplastic resin is 110°C or higher; and a saturated water absorption rate of the thermoplastic resin is less than 1.1 wt%, wherein the thermoplastic resin comprises a (meth)acrylic acid ester structural unit (a) represented by general formula below: wherein R1 represents a hydrogen atom or a methyl group, and R2 represents a C 1 -C 16 hydrocarbon group, and an aliphatic vinyl structural unit (b) represented by general formula below: wherein R3 represents a hydrogen atom or a methyl group, and R4 represents a cyclohexyl group or a cyclohexyl group having a C 1 -C 4 hydrocarbon substituent, and wherein the ratio of the sum of the (meth)acrylic acid ester structural unit (a) and the aliphatic vinyl structural unit (b) is 90 to 100 mol% relative to all the structural units in the thermoplastic resin, and wherein the molar ratio between the (meth)acrylic acid ester structural unit (a) and the aliphatic vinyl structural unit (b) is 55:45 to 85:15, wherein the intrinsic birefringence value is calculated according to the description by using the Lorentz-Lorenz equation, the glass transition temperature is obtained by using a differential scanning calorimeter, 10 mg of a sample at a temperature raising rate of 10°C/min and calculation according to a midpoint method with second heating, and the saturated water absorption rate is obtained according to the description by immersion a disk-like molded plate in water at 23°C. an intrinsic birefringence of each of the thermoplastic resin and the thermoplastic resin is -0.005 to 0.005; a glass transition temperature of the thermoplastic resin is 110°C or higher; and a saturated water absorption rate of the thermoplastic resin is less than 1.1 wt%, wherein the thermoplastic resin comprises a (meth)acrylic acid ester structural unit (a) represented by general formula below: wherein R1 represents a hydrogen atom or a methyl group, and R2 represents a C 1 -C 16 hydrocarbon group, and R1 represents a hydrogen atom or a methyl group, and R2 represents a C 1 -C 16 hydrocarbon group, and an aliphatic vinyl structural unit (b) represented by general formula below: wherein R3 represents a hydrogen atom or a methyl group, and R4 represents a cyclohexyl group or a cyclohexyl group having a C 1 -C 4 hydrocarbon substituent, and R3 represents a hydrogen atom or a methyl group, and R4 represents a cyclohexyl group or a cyclohexyl group having a C 1 -C 4 hydrocarbon substituent, and wherein the ratio of the sum of the (meth)acrylic acid ester structural unit (a) and the aliphatic vinyl structural unit (b) is 90 to 100 mol% relative to all the structural units in the thermoplastic resin, and wherein the molar ratio between the (meth)acrylic acid ester structural unit (a) and the aliphatic vinyl structural unit (b) is 55:45 to 85:15, wherein the intrinsic birefringence value is calculated according to the description by using the Lorentz-Lorenz equation, the glass transition temperature is obtained by using a differential scanning calorimeter, 10 mg of a sample at a temperature raising rate of 10°C/min and calculation according to a midpoint method with second heating, and the saturated water absorption rate is obtained according to the description by immersion a disk-like molded plate in water at 23°C.