A thermoplastic polycarbonate composition comprising, based on the total weight of the thermoplastic polycarbonate composition, (a) 15 to 22 wt.% of talc; (b) less than 5 wt.% of clay; and (c) 78 to 85 wt.% of a polymer component, comprising, based on the weight of the polymer component, 79 to 98.7 wt.% of a polycarbonate comprising units derived from bisphenol A; 0.1 to 2 wt.% of a fluorinated polymer; 1 to 8 wt.% of an phosphorus-containing flame retardant comprising units derived from bisphenol A; 0 to 5 wt.% of a bulk acrylonitrile-butadiene-styrene; 0.1 to 5 wt.% of a silicone oil; and 0.1 to 1 wt.% of an additive composition comprising an antioxidant, a mold release agent, and a stabilizer; wherein a molded sample of the thermoplastic polycarbonate composition has no drips when measured in accordance with NF P 92-505; a smoke density index of less than 10 determined in accordance with the formula: SDI = Ds max / 100 + VOF 4 / 30 wherein SDI is the smoke density index; Ds max is the maximum smoke density; and VOF4 is the average smoke density measured over the first four minutes, and is calculated in accordance with the formula: 1⁄2 Ds 0 + Ds 1 + Ds 2 + Ds 3 + 1⁄2 Ds 4; wherein Ds0 is the smoke density at 0 minutes, Ds1 is the smoke density at 1 minute, Ds2 is the smoke density at 2 minutes, Ds3 is the smoke density at 3 minutes, and Ds4 is the smoke density at 4 minutes; and Ds max, Ds0, Ds1, Ds2, Ds3, and Ds4 are measured in accordance with NF X 10-702 at a thickness of 3 mm; 100% ductility in a multi-axial impact test at 23°C, measured in accordance with ISO 6603; and an M1 rating at a thickness of 4 mm determined according to NF F 16-101. (a) 15 to 22 wt.% of talc; (b) less than 5 wt.% of clay; and (c) 78 to 85 wt.% of a polymer component, comprising, based on the weight of the polymer component, 79 to 98.7 wt.% of a polycarbonate comprising units derived from bisphenol A; 0.1 to 2 wt.% of a fluorinated polymer; 1 to 8 wt.% of an phosphorus-containing flame retardant comprising units derived from bisphenol A; 0 to 5 wt.% of a bulk acrylonitrile-butadiene-styrene; 0.1 to 5 wt.% of a silicone oil; and 0.1 to 1 wt.% of an additive composition comprising an antioxidant, a mold release agent, and a stabilizer; 79 to 98.7 wt.% of a polycarbonate comprising units derived from bisphenol A; 0.1 to 2 wt.% of a fluorinated polymer; 1 to 8 wt.% of an phosphorus-containing flame retardant comprising units derived from bisphenol A; 0 to 5 wt.% of a bulk acrylonitrile-butadiene-styrene; 0.1 to 5 wt.% of a silicone oil; and 0.1 to 1 wt.% of an additive composition comprising an antioxidant, a mold release agent, and a stabilizer; SDI is the smoke density index; Ds max is the maximum smoke density; and VOF4 is the average smoke density measured over the first four minutes, and is calculated in accordance with the formula: 1⁄2 Ds 0 + Ds 1 + Ds 2 + Ds 3 + 1⁄2 Ds 4; Ds0 is the smoke density at 0 minutes, Ds1 is the smoke density at 1 minute, Ds2 is the smoke density at 2 minutes, Ds3 is the smoke density at 3 minutes, and Ds4 is the smoke density at 4 minutes; and Ds max, Ds0, Ds1, Ds2, Ds3, and Ds4 are measured in accordance with NF X 10-702 at a thickness of 3 mm; 100% ductility in a multi-axial impact test at 23°C, measured in accordance with ISO 6603; and an M1 rating at a thickness of 4 mm determined according to NF F 16-101.