A thermoplastic composition, comprising: 40 to 94 weight percent, preferably 60 to 92 weight percent, more preferably 75 to 91 weight percent of a polycarbonate, a polycarbonate copolymer, or a combination thereof; 5 to 20 weight percent, preferably 5 to 15 weight percent, more preferably 8 to 12 weight percent of a fiber reinforcement; optionally 1 to 20 ppm, preferably 1 to 10 ppm, more preferably 3 to 5 ppm of a phosphorous-containing acid stabilizer; 0.01 to 2 weight percent, preferably 0.02 to 1 weight percent, more preferably 0.03 to 0.5 weight percent of a first colorant consisting of a dye, pigment, or a combination thereof, wherein the first colorant does not comprise titanium dioxide; 0.05 to 0.5 weight percent, preferably 0.1 to 0.4 weight percent, more preferably 0.1 to 0.3 weight percent of an anti-drip agent selected from polytetrafluoroethylene, polytetrafluoroethylene encapsulated in styrene acrylonitrile copolymer, polyphenylene ether, or a combination thereof; and 0.3 to 0.9 weight percent, preferably 0.4 to 0.8 weight percent, more preferably 0.4 to 0.6 weight percent of potassium perfluorobutane sulfonate, wherein the composition does not comprise talc, wherein all weight percent values are based on the total weight of the composition, and wherein the total weight percent is 100 wt%, and wherein an injection molded sample of the composition subjected to molding conditions comprising a residence time of 600 seconds at 340°C has a ΔE value of less than or equal to 3.5, preferably less than or equal to 3, more preferably less than or equal to 2.8, according to the CIE1976 L*a*b* color measurement system as specified by ISO 11664-4:2008 /CIE S 014-4/E:2007, as measured at a thickness of 2.5 mm according to ASTM D2244. 40 to 94 weight percent, preferably 60 to 92 weight percent, more preferably 75 to 91 weight percent of a polycarbonate, a polycarbonate copolymer, or a combination thereof; 5 to 20 weight percent, preferably 5 to 15 weight percent, more preferably 8 to 12 weight percent of a fiber reinforcement; optionally 1 to 20 ppm, preferably 1 to 10 ppm, more preferably 3 to 5 ppm of a phosphorous-containing acid stabilizer; 0.01 to 2 weight percent, preferably 0.02 to 1 weight percent, more preferably 0.03 to 0.5 weight percent of a first colorant consisting of a dye, pigment, or a combination thereof, wherein the first colorant does not comprise titanium dioxide; 0.05 to 0.5 weight percent, preferably 0.1 to 0.4 weight percent, more preferably 0.1 to 0.3 weight percent of an anti-drip agent selected from polytetrafluoroethylene, polytetrafluoroethylene encapsulated in styrene acrylonitrile copolymer, polyphenylene ether, or a combination thereof; and 0.3 to 0.9 weight percent, preferably 0.4 to 0.8 weight percent, more preferably 0.4 to 0.6 weight percent of potassium perfluorobutane sulfonate, wherein the composition does not comprise talc, wherein all weight percent values are based on the total weight of the composition, and wherein the total weight percent is 100 wt%, and wherein an injection molded sample of the composition subjected to molding conditions comprising a residence time of 600 seconds at 340°C has a ΔE value of less than or equal to 3.5, preferably less than or equal to 3, more preferably less than or equal to 2.8, according to the CIE1976 L*a*b* color measurement system as specified by ISO 11664-4:2008 /CIE S 014-4/E:2007, as measured at a thickness of 2.5 mm according to ASTM D2244.