A spunbonded nonwoven having crimped multicomponent fibers, wherein a first component of the multicomponent fibers consists of a first thermoplastic polymer material comprising a first thermoplastic base polymer and a second component of the multicomponent fibers consists of a second thermoplastic polymer material comprising a second thermoplastic base polymer that is different from the first base polymer; wherein the first base polymer and the second base polymer are polyolefins; wherein the first base polymer and the second base polymer have a melt flow rate of between 15 and 60 g/10min as measured according to ISO 1133 with conditions being 230°C and 2,16 kg; wherein at least one of the first polymer material or the second polymer material is a polymer blend that comprises, further to the respective base polymer, between 1 and 10 weight percent of a high melt flow rate polymer; wherein the high melt flow rate polymer is a polyolefin and has a melt flow rate of between 600 and 3000 g/10min as measured according to ISO 1133 with conditions being 230°C and 2,16 kg; wherein the fibers have a linear mass density of less than 1,5 denier; wherein the average crimp number of the crimped multicomponent fibers is in the range of at least 8 crimps per cm in the fiber, as measured per Japanese standard JIS L-1015-1981 under a pre-tension load of 2 mg/denier; and wherein the nonwoven is obtainable in an apparatus comprising at least two extruders with a spinnerette, a drawing channel and a moving belt, wherein the fibers are spun in a spinnerette, drawn in a drawing channel and laid down on a moving belt, wherein the apparatus comprises a pressurized process air cabin from which process air is directed through the drawing channel to draw fibers, wherein the pressure difference between the ambient pressure and the pressure in the process air cabin is at least 4000 Pascal and/or wherein the maximum air speed in the drawing channel is at least 70 m/s. wherein a first component of the multicomponent fibers consists of a first thermoplastic polymer material comprising a first thermoplastic base polymer and a second component of the multicomponent fibers consists of a second thermoplastic polymer material comprising a second thermoplastic base polymer that is different from the first base polymer; wherein the first base polymer and the second base polymer are polyolefins; wherein the first base polymer and the second base polymer have a melt flow rate of between 15 and 60 g/10min as measured according to ISO 1133 with conditions being 230°C and 2,16 kg; wherein at least one of the first polymer material or the second polymer material is a polymer blend that comprises, further to the respective base polymer, between 1 and 10 weight percent of a high melt flow rate polymer; wherein the high melt flow rate polymer is a polyolefin and has a melt flow rate of between 600 and 3000 g/10min as measured according to ISO 1133 with conditions being 230°C and 2,16 kg; wherein the fibers have a linear mass density of less than 1,5 denier; wherein the average crimp number of the crimped multicomponent fibers is in the range of at least 8 crimps per cm in the fiber, as measured per Japanese standard JIS L-1015-1981 under a pre-tension load of 2 mg/denier; and wherein the nonwoven is obtainable in an apparatus comprising at least two extruders with a spinnerette, a drawing channel and a moving belt, wherein the fibers are spun in a spinnerette, drawn in a drawing channel and laid down on a moving belt, wherein the apparatus comprises a pressurized process air cabin from which process air is directed through the drawing channel to draw fibers, wherein the pressure difference between the ambient pressure and the pressure in the process air cabin is at least 4000 Pascal and/or wherein the maximum air speed in the drawing channel is at least 70 m/s.