Polyolefin composition comprising (a) a first heterophasic propylene copolymer (HECO1) having (i) a melt flow rate MFR 2 (230 °C) measured according to ISO 1133 in the range of 15.0 to 55.0 g/10min, and (ii) a xylene cold soluble content determined according ISO 16152 (25 °C) in the range of 24 to 38 wt.-%, wherein further (iii) the intrinsic viscosity determined according to DIN ISO 1628/1 (in decalin at 135 °C) of the xylene cold soluble fraction of the heterophasic propylene copolymer (HECO1) is in the range of 2.0 to 3.5 dl/g, and (b) a second heterophasic propylene copolymer (HECO2) comprising a propylene homopolymer (H-PP2) and an elastomeric propylene copolymer, wherein (i) said propylene homopolymer (H-PP2) has a melt flow rate MFR 2 (230°C) measured according to ISO 1133 in the range of above 15 to 400 g/10min; (ii) the xylene cold soluble fraction of the second heterophasic propylene copolymer (HECO2) has an intrinsic viscosity determined according to DIN ISO 1628/1 (in decalin at 135 °C) in the range of more than 3.7 to 9.0 dl/g; and (iii) the comonomer content of the xylene cold soluble fraction of the second heterophasic propylene copolymer (HECO2)is in the range of 10.0 to 40.0 wt.-% wherein (i) the polyolefin composition comprises the first heterophasic propylene copolymer (HECO 1) and the second heterophasic propylene copolymer (HECO2) in a weight ratio [(HECO1):(HECO2)] of 1.2:1 to 15:1, and/or (ii) the two heterophasic propylene copolymers (HECO1) and (HECO2) make up at least 80 wt.-%, of the inventive polyolefin composition. (a) a first heterophasic propylene copolymer (HECO1) having (i) a melt flow rate MFR 2 (230 °C) measured according to ISO 1133 in the range of 15.0 to 55.0 g/10min, and (ii) a xylene cold soluble content determined according ISO 16152 (25 °C) in the range of 24 to 38 wt.-%, wherein further (iii) the intrinsic viscosity determined according to DIN ISO 1628/1 (in decalin at 135 °C) of the xylene cold soluble fraction of the heterophasic propylene copolymer (HECO1) is in the range of 2.0 to 3.5 dl/g, and (i) a melt flow rate MFR 2 (230 °C) measured according to ISO 1133 in the range of 15.0 to 55.0 g/10min, and (ii) a xylene cold soluble content determined according ISO 16152 (25 °C) in the range of 24 to 38 wt.-%, wherein further (iii) the intrinsic viscosity determined according to DIN ISO 1628/1 (in decalin at 135 °C) of the xylene cold soluble fraction of the heterophasic propylene copolymer (HECO1) is in the range of 2.0 to 3.5 dl/g, and (b) a second heterophasic propylene copolymer (HECO2) comprising a propylene homopolymer (H-PP2) and an elastomeric propylene copolymer, wherein (i) said propylene homopolymer (H-PP2) has a melt flow rate MFR 2 (230°C) measured according to ISO 1133 in the range of above 15 to 400 g/10min; (ii) the xylene cold soluble fraction of the second heterophasic propylene copolymer (HECO2) has an intrinsic viscosity determined according to DIN ISO 1628/1 (in decalin at 135 °C) in the range of more than 3.7 to 9.0 dl/g; and (iii) the comonomer content of the xylene cold soluble fraction of the second heterophasic propylene copolymer (HECO2)is in the range of 10.0 to 40.0 wt.-% (i) said propylene homopolymer (H-PP2) has a melt flow rate MFR 2 (230°C) measured according to ISO 1133 in the range of above 15 to 400 g/10min; (ii) the xylene cold soluble fraction of the second heterophasic propylene copolymer (HECO2) has an intrinsic viscosity determined according to DIN ISO 1628/1 (in decalin at 135 °C) in the range of more than 3.7 to 9.0 dl/g; and (iii) the comonomer content of the xylene cold soluble fraction of the second heterophasic propylene copolymer (HECO2)is in the range of 10.0 to 40.0 wt.-% (i) the polyolefin composition comprises the first heterophasic propylene copolymer (HECO 1) and the second heterophasic propylene copolymer (HECO2) in a weight ratio [(HECO1):(HECO2)] of 1.2:1 to 15:1, and/or (ii) the two heterophasic propylene copolymers (HECO1) and (HECO2) make up at least 80 wt.-%, of the inventive polyolefin composition.