Abstract:
Process of recovering a hydrophobic organic compound(s) by contacting a chemically activated shaped carbon with a hydrophobic organic compound to repeatedly absorb and desorb the compound, thereby recovering the same. The activated carbon is such that it has a bulk density of 0.25 to 0.6 g/cm 3 , a pore volume of 0.65 to 1.2 cm 3  /g, a bulk density×pore volume of 0.25 to 0.4 cm 3  /cm 3 , a surface area of at least 1000 m 2  /g, a mean pore size of 18 to 35 angstroms, a bulk density×surface area of at least 400 m 2  /cm 3 , and which chemically activated carbon effectively adsorbs butane in an amount of 8.0 to 15 g/100 ml. The process is especially suitable for absorbing gasoline vapor in an automobile exhaust and releasing the absorbed gasoline for reuse in the operation of the engine.

Description:
This is a divisional application of U.S. application Ser. No. 07/409,864, filed Sept. 7, 1989, now U.S. Pat. No. 5,039,650. 
    
    
     BACKGROUND OF THE INVENTION 
     1. Field of the Invention 
     The present invention relates to a chemically activated shaped carbon, a process for producing the activated carbon and use thereof. 
     2. Description of the Prior Art 
     It has been conventional practice to recover organic solvents from gases containing the organic solvent as vaporized, by passing the gas through a layer of shaped activated carbon to cause the carbon to adsorb the organic solvent, and thereafter heating the active carbon layer to desorb the adsorbed solvent. 
     When gasoline engines for motor vehicles are stopped during driving, the heat of the engine operating at a high temperature is released to the environment to bring about a so-called hot-soaked state, permitting evaporation of gasoline. An active carbon layer is used for adsorbing the gasoline vapor and releasing the adsorbed gasoline for reuse for the operation of the engine. 
     It is desired that the activated carbon for use in these activated carbon layers be shaped carbon having high working capacity (the amount of effective adsorption) and high durability. 
     However, the conventional activated carbon for such uses is still unsatisfactory in the amount of effective adsorption, physical strength, etc. 
     Examined Japanese Patent Publication SHO 50-39635 discloses shaped activated carbon for adsorbing heavy metal ions, such as chromium ion, contained in waste liquids. The disclosed carbon is one obtained by chemically activating an organic material such as lauan flour with phosphric acid. U.S. Pat. No. 2,508,474 discloses chemically activated granular carbon, which is suitable for use as gas mask adsorbent. However, both references do not disclose specifically the physical properties of the product obtained. Further, both references do not disclose that the activated carbon obtained can be used for the adsorption and desorption cycle of gases. 
     SUMMARY OF THE INVENTION 
     The main object of the present invention is to provide shaped activated carbon suitable for adsorbing and desorbing hydrophobic organic compounds and having high working capacity and high durability, a process for industrially advantageously producing such shaped activated carbon by the chemical activation method, and uses thereof. 
     Accordingly, the present invention provides a chemically activated shaped carbon suitable for adsorbing and desorbing hydrophobic organic compounds and having the properties of 0.25 to 0.6 g/cm 3  in bulk density, 0.5 to 1.2 cm 3  /g in pore volume, 0.25 to 0.4 cm 3  /cm 3  in bulk density×pore volume, at least 1000 m 2  /g in surface area, at least 400 m 2  /cm 3  in bulk density×surface area, 18 to 35 angstroms in mean pore size and 5.0 to 15 g/100 ml in the effective amount of adsorption of butane. The present invention further provides a process for producing a chemically activated shaped carbon which comprises heating and reacting at 100° to 160° C. a mixture of a chemically activatable starting material and 40 to 70% aqueous solution of a chemical in a ratio of 1/0.6 to 1/3.0 by dry weight of their respective solid, shaping the reaction mixture at a temperature of 90°  to 160° C. when a total weight of the reaction mixture has become 90 to 115% of a dry weight of solids in the mixture before heating, and thereafter calcining, washing and drying the shaped product by conventional methods to obtain a shaped activated carbon. 
     According to the present invention, various materials can be made into shaped activated carbons which are great in the amount of effective adsorption per unit volume, outstanding in durability and suitable for adsorbing and desorbing hydrophobic organic compounds. 
     The shaped activated carbon of the present invention is suited to the recovery of hydrophobic organic compounds and is desirable, for example, for use in gasoline evaporation preventing devices (Evaporated Loss Control Device; ELCD) and the like. 
    
    
     BRIEF DESCRIPTION OF THE DRAWINGS 
     FIG. 1 shows the principle of operation of a gasoline evaporation preventing device as an example in which the shaped activated carbon of the invention is used, diagram (a) showing the device during adsorption and diagram (b) showing the same during desorption; and 
     FIG. 2 is a flow chart illustrating the basic feature of a solvent recovery process as another example in which the present shaped activated carbon is used. 
    
    
     DESCRIPTION OF THE PREFERRED EMBODIMENTS 
     The starting carbon material to be used in the present invention is a chemically activatable material. Examples of such materials are cellulosic materials (e.g., wood chips and coconut shells) and starch materials (e.g., cereals including corn, millet, foxtail millet and barnyard millet). Of these, cellulosic materials are desirable. Examples of chemicals useful for the chemical activation method are those generally used for activation, such as phosphoric acid, zinc chloride, calcium chloride and the like, among which zinc chloride and phosphoric acid are desirable. Zinc chloride is more desirable. 
     The term &#34;bulk density&#34; as used herein for the shaped activated carbon of the invention refers to the bulk density of 10- to 28-mesh (according to old JIS abolished in Mar. 1987) shaped activated carbon as determined according to the method of JIS K 1474. The shaped activated carbon of the invention is generally 0.25 to 0.6 g/cm 3 , preferably at least 0.3 g/cm 3 , more preferably at least 0.35 g/cm 3 , in bulk density. 
     The term &#34;pore volume&#34; refers to the amount of N 2  adsorbed as determined by the N 2  adsorption method at a relative pressure of 0.931 and is used for pore volumes of up to 300 angstroms as determined by the Cranston-Inkley method. The shaped activated carbon of the present invention is generally 0.5 to 1.2 cm 3  /g, preferably at least 0.6 cm 3  /g, more preferably at least 0.65 cm 3  /g, in pore volume. The pore volume can be determined using, for example, a device of CARLO ERBA SORPTO MATIC SERIES 1800. 
     The shaped activated carbon of the invention must further fulfill the requirement that the product of the bulk density multiplied by the pore volume should be in the range of 0.25 to 0.4 cm 3  /cm 3 . When the product is in this range, the activated carbon has high adsorptive capacity per unit volume and excellent strength. The product is preferably at least 0.27 cm 3  /cm 3 , more preferably at least 0.29 cm 3  /cm 3 . 
     With the shaped activated carbon of the invention, the surface area thereof is determined by the BET method. The carbon is generally at least 1000 m 2  /g, preferably at least 1100 m 2  /g, more preferably at least 1300 m 2  /g, in surface area. With the activated carbon of the invention, the surface area is further limited in its relationship with the bulk density. More specifically, the product of the bulk density multiplied by the surface area is generally at least 400 m 2  /cm 3 , preferably at least 500 m 2  /cm 3 , more preferably at least 550 m 2  /cm 3 . The surface area can be measured with use of the same device as mentioned above for the determination of the pore volume. 
     The mean pore size of the shaped activated carbon of the invention is a value calculated from the pore volume and the surface area. The present carbon is generally 18 to 35 angstroms, preferably 19 to 30 angstroms, more preferably 20 to 28 angstroms, in mean pore size. 
     Butane working capacity of the carbon of the present invention is a value determined for 100 ml of a sample of the carbon with use of n-butane having a purity of at least 99.9%. The method of determination will be described in detail in Example 1 to be given later. The present activated carbon is generally 5.0 to 15 g/100 ml, preferably 8.0 to 15 g/100 ml, more preferably 9.0 to 15 g/100 ml, in the effective amount of butane adsorbed as determined by this method. 
     In particle size, the shaped activated carbon of the invention is suitably plus 50 mesh (as determined according to JIS using a screen with an opening size of at least 0.3 mm), preferably plus 36 mesh (using a screen with an opening size of at least 0.425 mm), more preferably plus 30 mesh (using a screen with an opening size of at least 0.5 mm). 
     The chemically activated shaped carbon of the present invention is suitable for adsorbing and desorbing hydrophobic organic compounds. The hydrophobic organic compounds to be adsorbed and desorbed are preferably those having solubility in water of up to 10 wt. % at 20° C. and a boiling point of -5° C. to 170° C. Examples of such hydrophobic organic compounds are chain aliphatic saturated or unsaturated hydrocarbons having 4 to 8 carbon atoms (hereinafter expressed as &#34;C 4  -C 8  &#34;), C 5  -C 9  alicyclic hydrocarbons, C 6  -C 9  aromatic hydrocarbons, C 1  -C 6  hydrocarbon halides, C 4  -C 8  ethers, C 5  -C 7  ketones, C 3  -C 8  esters, etc. 
     More specific examples of such C 4  -C 8  chain aliphatic saturated or unsaturated hydrocarbons are n-butane, n-pentane, n-hexane, isohexane, n-heptane, n-octane, isooctane(2,2,4-trimethylpentane), 2,2-dimethylbutane, 2-pentene and the like. 
     Examples of such C 5  -C 9  alicyclic hydrocarbons are cyclohexane, methylcyclohexane and the like. 
     Examples of such C 6  -C 9  aromatic hydrocarbons are benzene, toluene, o-xylene, m-xylene, p-xylene, ethylbenzene, isopropylbenzene and the like. 
     Examples of such C 1  -C 6  hydrocarbon halides are methylene chloride, chloroform, carbon tetrachloride, ethyl chloride, ethylene chloride, ethylidene chloride, 1,1,1-trichloroethane, 1,1,2-trichloroethane, 1,1,1,2-tetrachloroethane, 1,1,2,2-tetrachloroethane, pentachloroethane, vinylidene chloride, 1,2-dichloroethane, trichloroethylene, tetrachloroethylene, 1,2,3-trichloropropane, isopropyl chloride, allyl chloride, 1,2-dichloropropane, butyl chloride, amyl chloride, o-chlorotoluene, p-chlorotoluene and the like. 
     Examples of such C 4  -C 8  ethers are ethyl ether, n-butyl ether, epichlorohydrin, diglycidyl ether, furan and the like. 
     Examples of such C 5  -C 7  ketones are methyl n-propyl ketone, methyl n-butyl ketone, methyl isobutyl ketone, methyl n-amyl ketone, diethyl ketone, ethyl n-butyl ketone, cyclohexanone, o-methylcyclohexanone and the like. 
     Examples of such C 3  -C 8  esters are ethyl formate, propyl formate, n-butyl formate, isobutyl formate, amyl formate, ethyl acetate, n-propyl acetate, isopropyl acetate, n-butyl acetate, isobutyl acetate, sec-butyl acetate, n-amyl acetate, isoamyl acetate, ethyl butyrate and the like. 
     The starting material for preparing activated carbon by the process of the invention is a chemically activatable material, which is preferably a cellulosic material such as coconut shells, wood chips, saw dust or the like. Chemicals useful for activation are those generally used as such and already mentioned, among which zinc chloride and phosphoric acid are preferable, and more preferable is zinc chloride. 
     With the process of the present invention, the activating chemical is used in the form of a 40 to 70 wt. % aqueous solution. Concentrations less than 40 wt. % are not desirable since the reaction then requires a longer period of time. Concentrations over 70 wt. % present difficulty in uniformly mixing the starting carbon material and the activating chemical together, permit the reaction to proceed at a very high velocity and make it difficult to control the reaction. The carbon material and the aqueous chemical solution are mixed together in the ratio generally of 1/0.6 to 1/3.0, preferably 1/0.8 to 1/2.0, by dry solids weight. 
     The mixture of starting carbon material and aqueous solution of activating chemical is heated at 100° to 160° C. for reaction. The term &#34;reaction&#34; as used herein refers to the preparation of a black substance from the starting carbon material by decomposing and dehydrating the material under the action of the activating chemical. 
     The reaction must be conducted at a temperature of at least 100° C. to effect the removal of water. At a higher temperature, the reaction proceeds at a higher velocity, whereas at temperatures exceeding 160° C., the reaction proceeds excessively, making it impossible to shape the resulting reaction mixture. 
     With the process of the invention, the end point of the reaction is critical. One of the features of the present invention is to terminate the reaction at such a stage that the reaction mixture is most suited to shape. We have found it desirable to discontinue the reaction when the weight of the reaction mixture has become 90 to 115% of the dry weight of the starting mixture (dry weight of the starting carbon material+dry weight of the activating chemical). The term the &#34;reaction mixture&#34; refers to all the substances or materials present in the reaction system inclusive of water. Simultaneously when the starting carbon material becomes black, tar is formed which is thought to act as a binder during shaping and during activation through calcining, so that the reaction, if allowed to proceed excessively, eliminates the tar, makes the reaction mixture difficult to shape and fails to give shaped activated carbon retaining hardness and having a compact structure on calcining and activation. On the other hand, if the reaction is terminated too early, the reaction mixture contains a lesser quantity of tar and still retains a large amount of water, permitting the water to remain between the particles during shaping, with the result that the activated carbon obtained on calcining and activation is low in bulk density and in compactness. 
     Next, the reaction mixture is compactly shaped while being deaerated. The mixture is shaped while being heated at 90° to 160° C., whereby the tar resulting from the reaction is melted and allowed to remain between the particles as a binder, consequently giving a compacted shaped product. 
     If the mixture is shaped at a temperature below 90° C., the tar will not melt, failing to diffuse through the clearances between the particles and rendering the mixture difficult to shape. Furthermore, the product obtained upon calcining and activation is liable to disintegrate into particles. When the temperature is above 160° C., the liquid portion (tar and water) of the reaction mixture becomes separated from the solid portion thereof during the shaping step. This renders the mixture difficult to shape. 
     In the shaping step, the reaction mixture is deaerated by applying a pressure thereto with or without evacuation. A tableting machine, press, extruder or the like is used as the shaping device. While the foregoing conditions are employed for the mixture to be press-shaped with respect to the shaping temperature and the reaction end point, it is suitable in the case of extrusion that the shaping temperature be 90° to 130° C. and that the weight of the reaction mixture at the end point of the reaction be 100 to 115% of the dry weight of the starting mixture (dry weight of the starting carbon material+dry weight of the activating chemical). The shaped product can be in the form of tablets, plates, pellets, briquettes or the like, as optionally determined. Crushed type activated carbon can be obtained by crushing shaped activated carbon. 
     The shaped product is calcined for activation and then washed with an acid by methods which are generally employed for producing chemically activated carbon. For example, the product is calcined for carbonization in a rotary kiln at 500° to 700° C. for 10 minutes to 1 hour and is thereby activated, followed by washing and drying, whereby shaped activated carbon can be prepared. 
     The chemically activated shaped carbon obtained by the above process fulfills the foregoing requirements as to the properties such as bulk density, pore volume, surface area, mean pore size and effective amount of adsorption of butane. 
     The active carbon of the present invention can be further activated with a gas and thereby increased in the effective amount of adsorption of butane. The gas activation can be effected in the same manner as in the usual process for producing gas-activated shaped carbon. For example, water vapor or carbon dioxide is used as the activating gas at a gas partial pressure of 30 to 60% for calcining the carbon at 850° to 1000° C. for 10 minutes to 4 hours. 
     The chemically activated shaped carbon of the present invention is suitable for recovering hydrophobic organic compounds, such as those mentioned above, by repeated adsorption and desorption. The activated carbon is therefore usable, for example, for gasoline evaporation preventing devices (FIG. 1) for gasoline engines, solvent recovery processes (FIG. 2), etc. 
     In the FIG. 1, 1 is activated carbon layer, 2 and 3 each are pressure regulating valves, 4 is intake manifold, 5 is gas tank, 6 is exhaust manifold, 7 is air cleaner, 8 is gas flow. In the FIG. 2, 11 is activated carbon layer, 12 is condenser, 13 is separator, 14 is steam, 15 is gas containing solvent, 16 is solvent, 17 is water, 18 is exhaust. 
     EXAMPLES 
     The present invention will be described in greater detail with reference to the following examples, which nevertheless in no way limit the invention. 
     EXAMPLE 1 
     Dry saw dust (1.3 kg) and 2.6 kg of an aqueous zinc chloride solution having a concentration of 50% were heated with stirring. The temperature of the mixture gradually rose to exceed 100° C., whereupon the mixture started to undergo a reaction with the evaporation of water. The reaction was allowed to proceed to prepare a black reaction mixture. Portions of reaction mixture with varying weights were obtained by changing the end point of the reaction. More specifically, reaction mixture portions were obtained which were altered from 82 to 136% stepwise in weight relative to the dry weight (taken as 100%) of the starting mixture of saw dust and zinc chloride solution. 
     With heating at 130° C., the reaction mixture was shaped into disks (30 cm in diameter and about 4 mm in thickness) by a press or shaped into tablets (5 mm in diameter and about 3 mm in thickness). The shaped pieces were placed into a crucible and calcined at 600° C. for 3 hours for activation. 
     The calcined product was washed with hydrochloric acid and then with water for the removal of zinc chloride, and was thereafter dried in the conventional manner. The dried product was crushed to 10 mesh to 28 mesh and checked for properties. Table 1 shows the results. 
     The experimental results (bulk density, crushing yield, shape) indicate that good results can be achieved when the weight at the reaction end point and the reaction temperature are 90 to 115% and up to 160° C., respectively. 
     
                                           TABLE 1__________________________________________________________________________Exper-   End- Max. temp.                Bulk                    Crushingiment    Shaping    point         during density                    yieldNo. method    wt. (%)         reaction (°C.)                (g/l)                    (%)  Shape__________________________________________________________________________1-1 Press     82  170    334 58   No shape retentivity,                         readily became powder1-2 Press     85  165    374 64   Partly became powdery1-3 Press     94  150    401 72   Hard, slightly became                         powdery1-4 Press    102  130    443 73   Very hard, remained in                         shape1-5 Press    111  125    441 73   Very hard, remained in                         shape1-6 Press    118  120    407 71   Slightly brittle, remained                         in shape1-7 Press    130  115    373 72   Brittle, not became powdery1-8 Press    136  115    320 66   No shape retentivity, not                         became powdery1-9 Tableting     82  170    336 62   Readily became powdery 1-10    Tableting     89  160    404 73   Hard, slightly became                         powder__________________________________________________________________________ 
    
     The activated carbons of Exp. Nos. 1-4 and 1-5 were checked for the effective amount of adsorption of n-butane by the method stated below. The results are given below 
     
         ______________________________________(Results)                  Experiment No.                  1-4   1-5______________________________________Amount of n-butane adsorbed (g/100 ml)                    16.1    16.0Amount of remaining n-butane (g/100 ml)                    7.2     7.2Effective amount of adsorption of                    8.9     8.8n-butane (g/100 ml)______________________________________ 
    
     The effective amount of adsorption of n-butane was determined by the following method. 
     1. The sample is dried at 150° C. for 3 hours and then cooled to room temperature in a desiccator. 
     2. The sample is packed in a glass column, 15.4 mm in inside diameter, to a height of 10 cm. 
     3. The column is sealed off, and the weight is measured (A g). 
     4. With the column set in a constant-temperature water bath at 25° C., n-butane (at least 99.9% in purity) is passed through the sample at a flow rate of 250 mg/min for 15 minutes (up flow). 
     5. The column is removed and checked for the weight (B g). 
     6. The column is then set in the device again, and dry air is passed through the sample (down flow) at 190 ml/min at 25° C. (10 BED vol/min) for 20 minutes. 
     7. The column is removed and checked for the weight (C g). 
     8. The above steps 4 to 7 are repeated four times, and the averages for 2 to 4 cycles are calculated. ##EQU1## 
     EXAMPLE 2 
     The same reaction mixture as prepared in Example 1, 102% in weight at the end point of reaction, was shaped into disks by a press at varying temperatures of 50° to 200° C. The same procedure as in Example 1 was thereafter repeated to obtain shaped activated carbon, which was then checked for properties. Table 2 shows the results. 
     
                       TABLE 2______________________________________ Shaping  Bulk    CrushingExp.  temp.    density yieldNo.   (°C.)          (g/l)   (%)    Shape______________________________________2-1    50      *       44     Readily became powdery2-2    70      341     57     Brittle, partly became                         powdery2-3    90      420     71     Hard, remained in shape2-4   110      431     72     Very hard, remained in                         shape2-5   130      443     73     Very hard, remained in                         shape2-6   160      440     71     Very hard, remained in                         shape2-7   170      393     63     Became partly powdery2-8   200      373     60     Readily became powdery______________________________________ Note *Not measureable because the carbon collapsed into powder. 
    
     At 170° C. and 200° C., the liquid portion separated off. The reaction mixture was hardened at the portions thereof close to the press plates but became brittle at its central portion between the press plates. 
     The shaped activated carbons of Exp. Nos. 2-3, 2-4, 2-5 and 2-6 were checked for the effective amount of adsorption of n-butane in the same manner as above. The results are as follows. 
     
         ______________________________________(Results)              Experiment No.              2-3  2-4    2-5    2-6______________________________________Amount of n-butane adsorbed                15.2   15.6   16.1 16.0(g/100 ml)Amount of remaining n-butane                6.9    7.0    7.2  7.2(g/100 ml)Effective amount of adsorption of                8.3    8.6    8.9  8.8n-butane (g/100 ml)______________________________________ 
    
     EXAMPLE 3 
     Dry coconut shell flour and an aqueous solution of zinc chloride were heated at 120° to 130° C. with stirring for reaction. (The proportion of zinc chloride was varied as shown in the table below, Nos. 1 to 8.) The reaction was terminated when the weight of each reaction mixture became 90 to 115% of the dry weight of the starting mixture, and the resulting reaction mixture was shaped into disks (30 cm in diameter and about 4 mm in thickness) at 130° C. by a press, then placed into a crucible and calcined at 600° C. for 3 hours for activation. 
     In the usual manner, each calcined product obtained was washed with hydrochloric acid and then with water for the removal of unreacted zinc chloride, and was thereafter dried. 
     The dried products (shaped activated carbons Nos. 1-8) where crushed to 10 mesh to 28 mesh and checked for properties. Table 3 shows the results. 
     
                                           TABLE 3__________________________________________________________________________Effects of zinc chloridePress-shaping           Shaped activated carbon No.           1  2  3  4   5  6   7   8__________________________________________________________________________Coconut shell flour [g]            1300               1300                  1300                      1300                         1300                             1300                                 800                                     800Zinc chloride [g]             780               1040                  1170                      1300                         1430                             1625                                 1200                                    1600Water [g]         780                780                  1040                      1300                         1040                             1300                                 1200                                    1200Coconut shell flour [part]             100                100                   100                      100                          100                             100                                 100                                     100Zinc chloride [part]             60                80                   90                      100                          110                             125                                 150                                     200Water [part]      60                60                   80                      100                          80                             100                                  150                                     150Endpoint weight [g]            2030               2150                  2415                    2887.3                         2709                           3286.1                               1987.1                                    2390Endpoint weight [%]            97.6               91.9                  97.8                     111.1                         99.2                            112.3                                99.4                                    99.6Bulk density [g/l]             540                479                   452                      441                          440                             377                                 369                                     325Surface area [m.sup.2 /g]            1102               1315                  1354                      1458                         1399                             1473                                 1310                                    1466Pore volume [ml/g]           0.513              0.618                 0.653                     0.717                        0.726                            0.804                                0.879                                   1.066Mean pore size [ Å ]            18.6               18.8                  19.3                     19.7                         20.8                            21.8                                26.8                                    29.1Surface area [m.sup.2 /ml]             595                630                   612                      643                          616                             555                                 483                                     476Pore volume [ml/ml]           0.277              0.296                 0.295                     0.316                        0.319                            0.303                                0.324                                   0.346Amount of n-butane            14.0               15.2                  15.2                     16.0                         16.6                            15.3                                15.5                                    16.5adsorbed [g/100 ml]Amount of remaining            7.9               7.4                  7.1                      7.2                         6.9                             5.6                                 4.6                                    4.2n-butane [g/100 ml]Effective amount of            6.1               7.8                  8.1                      8.8                         9.7                             9.7                                10.9                                    12.3adsorption of n-butane [g/100 ml]__________________________________________________________________________ 
    
     Consequently, as the proportion of zinc chloride increased, the mean pore size increased, the pore volume increased and the bulk density decreased because of the increase in the pore volume. 
     (For reference, common carbon prepared from coconut shells and activated with water vapor is up to 6.0 g/100 ml in the effective amount of adsorption of n-butane, and other activated carbons commercially available and great in the effective amount of adsorption of n-butane are about 8 g/100 ml in this value.) 
     The mean pore size (angstroms) was calculated from [4×pore volume (ml/ml)/surface area (m 2  /ml)]×10 4 . 
     EXAMPLE 4 
     Dry saw dust (10 g) and 20 g of 50% aqueous solution of Zinc chloride were thoroughly mixed together with a spurtle in a 500-c.c. beaker, held in a constant-temperature dryer for 24 hours and then checked for the resulting change in weight (i.e. the weight of the resulting mixture based on the dry weight of the starting mixture of saw dust and zinc chloride, as expressed in percentage) and also for the degree of reaction. This procedure was repeated at varying dryer temperatures of 70° to 200° C. as listed in Table 4, which also shows the results. 
     
                       TABLE 4______________________________________  DryerSam-   temp.     Weight  Degree of reactionple    (°C.)            (%)     (state of mixture)______________________________________A       70       134     No reactionB       80       129     No reactionC       90       128     Slightly became black but no                    progress in reactionD      100       111     Became blackE      110        91     &#34;F      130        83     &#34;G      150        82     &#34;H      200        82     &#34;______________________________________ 
    
     Each mixture was then shaped into tablets (6 mm in diameter and about 3 mm in thickness) with heating at 130° C. as in Example 1. Although samples C, D and E were shapable, samples A, B, F, G and H were not shapable. Samples C, D and E were calcined at 600° C. for 1 hour for activation, whereby samples D and E were each made into shaped activated carbon of high strength, whereas sample C gave a product which was low in strength and brittle. 
     EXAMPLE 5 
     Dry saw dust (1.3 kg) and 2.6 kg of an aqueous zinc chloride solution having a concentration of 50% were heated with stirring. The temperature of the mixture, rising gradually, was controlled by varying the degree of vacuum. The reaction mixture was then shaped with a press in the same manner as in Example 1, calcined in a crucible at 600° C., washed with acid and water, crushed and checked for properties. Table 5 below shows the results, which indicate that reaction temperatures of above 100° C. afford good results. 
     
                                           TABLE 5__________________________________________________________________________Exper-    End- Max. temp.           Bulk               Crushingiment    point    during density               yieldNo. wt. (%)    reaction (°C.)           (g/l)               (%)  Shape__________________________________________________________________________4-1 123   87    --  --   Not shapable4-2 106   89    --  --   &#34;4-3 102   90    --  --   &#34;4-4 104   94    303 45   No shape retentivity,                    readily became powdery4-5 107  102    432 71   Very hard, remained in                    shape4-6 105  106    441 74   Very hard, remained in                    shape4-7 119  113    386 69   Slightly brittle, but not                    became powdery4-8 103  122    441 72   Very hard, remained in                    shape__________________________________________________________________________ 
    
     The activated carbons with Exp. Nos. 4-5, 4-6 and 4-8 given above were checked for the effective amount of adsorption of n-butane by the method already described. The results are as follows. 
     
         ______________________________________(Results)                 Experiment No.                 4-5  4-6    4-8______________________________________Amount of n-butane adsorbed (g/100 ml)                   15.7   16.1   16.0Amount of remaining n-butane (g/100 ml)                   7.0    7.1    7.2Effective amount of adsorption of                   8.7    9.0    8.8n-butane (g/100 ml)______________________________________ 
    
     EXAMPLE 6 
     The active carbon prepared in Example 3 using 110 parts of zinc chloride was further activated with water vapor under the conditions of Table 6 below. Table 6 also shows the properties of the product. The activation with water vapor for 1.5 hours increased the amount of n-butane adsorbed and the effective amount of adsorption of n-butane by about 12%. 
     
                       TABLE 6______________________________________Influence of activation   (ZnCl.sub.2 110 parts)______________________________________Activation temperature (°C.)               950    950    950  950Activation time (hr)               0.0    0.5    1.0  1.5Charge (g)          150.0  150.0  150.0                                  150.0Output (g)          123.8  121.0  95.3 84.2Yield (%)           82.5   80.7   63.5 56.1Yield (heat treatment base, %)               100.0  97.7   77.0 68.0Bulk density (g/l)  463    450    387  363Surface area (m.sup.2 /g)               1273   1363   1620 1758Pore volume (ml/g)  0.653  0.723  0.889                                  0.987Mean pore size (angstroms)               20.5   21.2   22.0 22.5Surface area (m.sup.2 /ml)               589    613    627  638Pore volume (ml/ml) 0.302  0.325  0.344                                  0.358Amount of n-butane adsorbed               17.4   15.7   17.9 18.6(g/100 ml)Amount of remaining n-butane               7.8    7.3    7.7  7.7(g/100 ml)Effective amount of adsorp-               9.6    8.4    10.2 10.9tion of n-butane (g/100 ml)______________________________________ 
    
     EXAMPLE 7 
     Shaped activated carbon No. 8 prepared in Example 3 was tested for equilibrium adsorption of the five kinds of organic solvents listed below. The amount of equilibrium adsorption (wet %) was determined at 25° C. and 100° C. using nitrogen containing 0.1 vol. % of each organic solvent. The condition of 25° C., 0.1 vol. % is typical of usual conditions under which common organic solvents are adsorbed. The condition of 100° C., 0.1 vol. % is typical of usual conditions under which common organic solvents are desorbed. Accordingly, the greater the difference (effective amount of adsorption) in the amount of adsorption between 25° C. and 100° C., the more suitable is the activated carbon for the recovery of organic solvents. 
     For comparison, activated carbon (particulate SHIRASAGI (S 2  ×4/6)) for recovering usual solvents was also similarly tested. Table 7 below shows the results. 
     
                       TABLE 7______________________________________Active carbon       No. 8              ComparativeN.sub.2 containing 0.1       25° C.                100° C.                          25° C.                                 100° C.vol. % of solvent       (wet %)  (wet %)   (wet %)                                 (wet %)______________________________________Cyclohexane 40.5     6.0       25.7   11.7MIBK*       58.8     7.4       37.3   16.4n-Heptane   45.9     8.5       29.1   17.7p-Xylene    59.6     13.4      37.8   28.3Benzene     45.4     6.1       28.8   11.6______________________________________ *MIBK: methyl isobutyl ketone 
    
     The above results reveal that shaped activated carbon No. 8 is greater than the comparative activated carbon in the effective amount of adsorption of any of the organic solvents.