Abstract:
The invention is a copolymer P, dispersant for dyes and/or pigments in standard plastic substances SK, wherein P exhibits a universal compatibility with standard plastics SK, with the feature that copolymer P is synthesized from monomer units: 
     (m1) methyl methacrylate, 
     (m2) (meth)acrylate of formula I: ##STR1## (m3) (meth)acryl compound of formula II: ##STR2## and optionally (m4) methacrylate of formula III: ##STR3##

Description:
DETAILED DESCRIPTION OF THE INVENTION 
     Monomers (m2), (m3), and (m4) 
     Monomers (m2) are known. Examples include cyclopentyl (meth)acrylate, cyclohexyl (meth)acrylate, and 4-methylcyclohexyl (meth)acrylate. 
     The following are examples of monomers (m3): dialkylaminoalkyl (meth)acrylates, such as N,N-dimethylaminopropyl (meth)acrylate, N,N-dimethylaminobutyl (meth)acrylate, N,N-diethylaminopropyl (meth)acrylate, N,N-diethylaminoethyl (meth)acrylate, or preferably N,N-dimethylaminoethyl (meth)acrylate; dialkylaminoalkyl(meth)acrylamides, such as N,N-diethylaminoethyl(meth)acrylamide, N,N-dimethylaminopropyl(meth)acrylamide, N,N-diethylaminobutyl(meth)acrylamide or preferably N,N-dimethylaminoethyl(meth)acrylamide; alkyl (meth)acrylates, or alkyl(meth)acrylamides with heterocycles as substituents, which have at least a nitrogen and/or oxygen atom in the heterocycle, such as furfuryl (meth)acrylate, tetrahydrohydrofurfuryl (meth)acrylate, 2,2,6,6-tetramethylpiperidinyl (meth)acrylate, 2-N-morpholinoethyl (meth)acrylate, 2-N-pyridinylethyl (meth)acrylate or 2-N-piperazinylethyl (meth)acrylate, and N-(4-morpholinomethyl)(meth)acrylamide, N-(1-piperidinylmethyl)(meth)acrylamide, N-methacryloyl-2-pyrrolidone, N-(methacrylamidomethyl)pyrrolidone, N-(acrylamidomethyl)pyrrolidone, N-(methacrylamidomethyl)caprolactam, N-(acrylamidomethyl)caprolactam, or 2-N-pyridinylethyl(meth)acrylamide, and other heterocyclic compounds, which are listed in EP-A 311,157 and which exhibit a (meth)acrylate or a (methy)acrylamide group; alkoxy (meth)acrylates, such as 2-ethoxyethyl (meth)acrylate, 2-methoxyethyl (meth)acrylate, 2-butoxyethyl (meth)acrylate, or 2-(ethoxyethoxy)ethyl (meth)acrylate. 
     Examples of monomers (m4) are: n-propyl methacrylate, isopropyl methacrylate, isobutyl methacrylate, n-pentyl methacrylate, n-hexyl methacrylate, 2-ethylhexyl methacrylate, n-octyl methacrylate, n-decyl methacrylate, n-dodecyl methacrylate, n-tetradecyl methacrylate, n-hexadecyl methacrylate, n-octadecyl methacrylate, n-eicosyl methacrylate, and preferably n-butyl methacrylate. 
     Preparation of copolymers P 
     Copolymers P are formed, in a known manner, from monomers (m1), (m2), (m3), and optionally (m4) by a radical, anionic, or group-transfer polymerization (see in this regard, for example, H. Rauch-Puntigam, Th. Voker, Acryl- und Methacrylverbindungen [Acrylic and methacrylic compounds], Springer, Heidelberg, 1967; Houben-Weyl, 4th Ed., Volume XIV/1, pp. 1010ff., Thieme, Stuttgart, 1961). The polymerization of copolymers P can be carried out in bulk, suspension, emulsion, or solution. 
     In radical polymerization, peroxide compounds, in particular organic peroxides, such as dibenzoyl peroxide or lauroyl peroxide, azo compounds, such as azodiisobutyronitrile, or redox initiators are preferably used in quantities of 0.01 to 5 wt %, based on the monomer fractions. 
     The radicals triggering the polymerization can also be produced by high-energy radiation. Molecular weight regulators which can be taken into consideration are, for example, traditional sulfur compounds, such as mercapto compounds in quantities of 0.2 to 8 wt %, based on the monomer fractions. In general, the average molecular weights M w  of copolymers P generally lie between 5×10 3  and 5×10 4  daltons, preferably between 10 4  and 3×10 4  daltons. 
     Copolymers P contain the following: methyl methacrylate units, 30 to 94.5 wt %, preferably 45 to 88 wt %, based on the total monomers; monomer units (m2), 5 to 50 wt %, preferably 10 to 45 wt %; and monomer units (m3), 0.5 to 20 wt %, preferably 2 to 15 wt %. In a particularly preferred specific embodiment of the invention, copolymers P also contain 0.5 to 30 wt %, preferably 1 to 25 wt %, of monomer units (m4), which generally influence the melt flow behavior and the compatibility of copolymers P with the standard plastics to be dyed in a favorable way, and thus improve the compoundability of the pigments and the pigment dispersants P or the mixtures. 
     With a large number of standard plastics SK, such as polymethyl methacrylate (PMMA), copolymers of methyl methacrylate and optionally substituted styrenes, polystyrene (PS), poly-α-methylstyrene (P-α-MS), styrene-acrylonitrile copolymers (SAN), acrylonitrile-butadiene-styrene terpolymers, polyolefins, such as polyethylene or polypropylene, polycarbonate (PC), polyester carbonate, polyvinyl chloride (PVC), chlorinated rubber, or polyvinylidene fluoride (PVDF), copolymers P form compatible polymer mixtures PM, whose characterization takes place according to recognized criteria (see in this regard, for example, Kirk-Othmer, Encyclopedia of Chemical Technology, Vol. 18, pp. 457-460, Wiley Interscience, New Work, 1981, J. Brandrup, E. H. Immergut, Polymer Handbook, 2nd Ed., Chapter III, pp. 211ff., Wiley Interscience, New York, 1975). 
     The compatible polymer mixtures PM of amorphous plastics SK and copolymer P has one refractive index and one single glass transition temperature, which lies between the glass transition temperatures of copolymer P and standard plastic SK. As another indication of the compatibility, one can cite the appearance of the LCST (Lower Critical Solution Temperature), whose existence is based on the process that during heating, the transparent mixture, which was clear up to then, is separated into dissimilar phases and becomes optically cloudy, which is clear evidence that the original polymer mixtures consisted of a single phase in thermodynamic equilibrium (see in this regard, for example, D. R. Paul, Polymer Blend &amp; Mixtures, pp. 1ff., Martinus Nijhoff Publishers, Dordrecht, Boston, 1985). 
     Pigments and dyes 
     As pigments in the preparations of the invention, containing pigment and copolymer P, both inorganic and organic pigments can be used. Suitable inorganic pigments are, for example: aluminum oxide hydrate, antimony oxide, barium sulfate, bronze powder, cadmium oxide, cadmium sulfide, calcium carbonate, calcium silicate, lead sulfate, lead chromate, lead oxide, lead chromate molybdate, chromium oxides, chromium antimony titanate, cobalt aluminate, iron oxides, graphite, mercury oxide, mercury sulfide, nickel titanate, silicon dioxide, silicon chromate, strontium chromate, magnesium silicate, titanium dioxide, ultramarine blue, zinc oxide, zinc chromate, zinc sulfide, or zirconium dioxide (see in this regard, for example: Kirk-Othmer, Encyclopedia of Chemical Technology, 3rd., Ed., Vol. 17, pp. 788-838, Wiley Interscience, New York, 1982, Ullmanns Encyclopadie der Technischen Chemie [Ullmann&#39;s Encyclopedia of Technical Chemistry], 4th Ed., Vol. 18, pp. 545-660, Verlag Chemie, Weinheim, 1979). 
     Examples of organic pigments are the following: phthalocyanine blue, phthalocyanine green, Malachite Green, Naphthol Red, toluidine red, pyrazolone red, rhodamine, alizarin, Hansa Yellow, anthraquinone, dianisidine orange (see in this regard: Kirk-Othmer, loc. cit., Vol. 17, pp. 838-871; Ullmanns Encyclopadie der Technischen Chemie, 4th Ed., Vol. 18, pp. 661-695, Verlag Chemie, Weinheim, 1979). 
     The pigments are present in more or less large, occasionally crystal-like agglomerates and are broken up into smaller agglomerates by the pigment dispersants. The dyes are generally dissolved molecularly in the plastic substrate and are to be distinguished from the pigments. However, the solubility of many dyes in standard plastics is poor or the dye intensity of many dyes is too large, so that a direct metering in of the dyes into the plastic melt is not possible. Even in such cases, copolymers P of the invention are excellent as dye dispersants. Examples of such dyes are the following: azo compounds, stilbene compounds, carotinoid dyes, di- and triarylmethane compounds, methine and polymethine compounds or thiazine compounds (see in this regard, Kirk-Othmer, loc. cit., Vol. 8, pp. 159-212, Wiley Interscience, New York, 1979). Such dyes are generally linked by physical interactions, such as hydrogen bonds or dipolar interactions, to copolymer P and/or to the standard plastic SK. The optical properties of such dyes are determined by electron transitions between molecule orbitals, whereas the optical properties of pigments are, moreover, influenced by the structure of the pigment particles. In contrast to the dyes, the pigments retain the primary particle form (crystallites) unchanged during the compounding steps. 
     Mixtures M of pigments and dyes with copolymers P 
     Mixtures M of pigments or dyes with copolymer P, in accordance with the invention, are produced by conventional mixing methods, such as melt-mixing or mixing in a solvent. 
     In general, mixtures MP of pigments and copolymers P contain 0.1 to 95 wt %, preferably 0.2 to 75 wt %, particularly preferably 0.5 to 70 wt %, pigment, with the fraction of copolymer P supplemented to make up 100 wt %. Possible amounts of copolymer P are 99.5-5 wt %, 99.8-25 wt. % and 99.5-30 wt %. 
     Mixtures MF of dyes and copolymers P contain 0.05 to 50 wt %, preferably 0.1 to 25 wt %, particularly preferably 0.2 to 15 wt %, dye, with the fraction of copolymer P supplemented to make up 100 wt %. Possible amounts of copolymer P are 99.95-50 wt %, 99.9-75 wt % and 99.8-85 wt %. For the production of mixtures MP or MF, the generally powdery pigments or dyes are first premixed with copolymers P typically present in granulated form or as material to be ground in slowly running mixing units, such as drum, gyrowheel or double-chamber plough bar mixers. These slowly running mixing units usually produce a mechanical mixing without elimination of the phase boundaries (see, for example, Ullmanns Encyclopadie der Technische Chemie, 4th Ed., Vol. 2, pp. 282-311, Verlag Chemie, Weinheim, New York, 1980). Premixtures produced in such a manner are thermoplastically prepared with homogeneous mixing of the aforementioned mixture components in the melt, using heatable mixing units at suitable temperatures, for example, 150° to 300° C., in kneaders or preferably in extruders, such as in single- or multiple-screw extruders or perhaps in extruders with an oscillating screw and with shear pins (kneaders from the BUSS COMPANY). With these methods, uniform-grain granulated materials with particle sizes of 2 to 5 mm are produced. The granulated materials contain a thermoplastic fraction, synthesized from copolymer P, and the pigments or dyes embedded therein. 
     In another specific embodiment of the invention, copolymer P is dissolved in a suitable solvent, and the pigment is dispersed in the resulting solution (or the dye is dissolved in the solution). This can be carried out, for example, with the aid of shaking devices or a ball mill. The solvent can be removed directly after the mixing process, or mixture M of copolymer P and the pigment or dye can be precipitated from the solution with suitable precipitating agents in order to isolate mixtures M. The preparation of mixtures M with the aid of solvents is taken into consideration, in particular for high pigment or dye concentration, generally above 75 wt %. In these high concentrations, the pigment or dye particles are present separately, coated with copolymer P, and copolymer P no longer forms a cohesive phase. 
     Working of mixtures M into standard plastics SK 
     Standard plastics SK, into which mixture M of pigments or dyes with copolymer P is worked as a universally acting dispersant, form compatible mixtures with copolymer P. This results in mixtures SKMF of transparent standard plastics SK and mixtures MF (mixtures of copolymer P and dyes) also being transparent. 
     Mixtures SKMP of standard plastics SK and pigment-dispersant preparations MP generally contain 0.5 to 80 wt %, preferably 1 to 70 wt %, particularly preferably 2 to 50 wt %, mixture MP of copolymer P and pigment, with the fraction of SK supplemented to make up 100 wt %. Amounts of SK generally fall in the range 99.5-20 wt. %, 99-30 or 98-50 wt. %. For the preparation of mixtures SKMP, generally granulated or powdery mixtures MP are first mixed mechanically in slowly running mechanical mixing units, without eliminating the phase boundaries (as described in the preparation of mixtures MP). The preliminary mixtures are generally mixed in the melt, using heatable mixing units at suitable temperatures for example, between 150° and 350° C., in kneaders or preferably in extruders, such as single-screw or multiple-screw extruders. With this method, mixtures SKMP are generally obtained as uniform-grain granulated materials with particle sizes of 2 to 5 mm. 
     Mixtures SKMF of standard plastic SK and dye-dispersant preparations MF generally contain 0.01 to 40 wt %, preferably 0.05 to 25 wt %, particularly preferably 0.1 to 20 wt %, mixture MF of copolymer P and dye, with the fraction of SK supplemented to make up 100 wt %. Amounts of SK generally fall in the range 99.99-60 wt. %, 99.95-75 wt. %, or 99.9-80 wt %. Generally, mixtures SKMF, such as mixtures SKMP, are preferably prepared by melt-mixing. If the dyes exhibit a high volatility, however, and there is concern-that the migration losses or decomposition of the dye assumes undesired forms, then mixtures SKMF are prepared by dissolving mixture components SK and MF in the common solvent and the subsequent removal of the solvent or precipitation of the mixture. 
     Advantageous effects of the invention 
     Due to the universal compatibility of copolymers P of the invention, with standard plastics SK, pigments and dyes can be worked into many standard plastics SK with the same dispersant P. This makes possible the universal applicability of mixtures MP (dispersant P and pigment) and MF (dispersant P and dye) in very different plastics SK, without having to adapt dispersant P to the plastic. Furthermore, a uniform distribution of dyes in transparent standard plastics SK is possible with the aid of dispersants P, without impairing their transparency. In addition dispersants P can be prepared according to standardized polymerization methods, wherein monomer components of copolymers P are readily accessible. 
     Very different pigments and dyes can be worked into standard plastics SK with dispersants P. With a particular copolymerization composition P, very different mixtures MP and MF can be prepared, which can be worked into standard plastics SK equally well. 
     EXAMPLES 
     Having generally described this invention, a further understanding can be obtained by reference to certain specific examples which are provided herein for purposes of illustration only and are not intended to be limiting unless otherwise specified. 
     Examples 1-8 
     Preparation of various universally compatible pigment binders P 
     For the preparation of 9 or 10 kg polymer P, 5 kg methyl methacrylate, 3.5 kg cyclohexyl methacrylate, 0.5 kg monomer (m3) and optionally 1 kg monomer (m4) are mixed with 4 g tert-butyl perneodecanoate, 15 g tert-butyl peroctoate, and 150 g 2-mercaptoethanol while stirring. The mixture is degassed for 15 min. Subsequently the mixture is poured into a bag made of polyester film, which lies between two halves of an appropriately dimensioned tin container provided with rubber sealing lips, which is then closed. The polymerization takes place in the chamber immersed in a water bath at 50° C. and lasts 20 h. The contents of the bag, which are solid after this polymerization time, are removed from the chamber, and temperature-conditioned at 110° C. in the conditioning cabinet for 12 h for the final polymerization. The resulting polymer P is ground in a mill with a screen size 8 and can be used either as material for grinding or after degassing extrusion at 150° C., as a granulated material. 
     
                       TABLE 1______________________________________                             J values                             according to                             DIN 51562Example  Monomer (m3)   Monomer (m4)                             (ml/g)______________________________________P 1    2-Dimethylamino-                 --          23.3  ethylmethacrylateP 2    2-(4-Morpholine)-                 --          26.4  ethylmethacrylateP 3    2-[2-(2-Ethoxy-                 --          27.4  ethoxy)ethoxy]-  ethylmethacrylateP 4    N-(2-Methacryloyl-                 --          25.8  oxyethyl)ethyleneureaP 5    2-Dimethylamino-                 Butylmeth-  24.0  ethylmethacrylate                 acrylateP 6    2-(4-Morpholine)-                 Butylmeth-  25.4  ethylmethacrylate                 acrylateP 7    2-[2-(2-Ethoxy-                 Butylmeth-  25.9  ethoxy)ethoxy]-                 acrylate  ethylmethacrylateP 8    N-(2-Methacryloyl-                 Butylmeth-  26.2  oxyethyl)ethyleneurea                 acrylate______________________________________ 
    
     Comparative Examples 9-10 
     Preparation of pigment binders P&#39; according to the state of the art. 
     The preparation of polymers takes place according to Examples 1-8: 
     
                       TABLE 2______________________________________                         J value                         according                         to DIN                         51562Example Composition of the polymer                         (ml/g)______________________________________ P&#39;9    95 Parts by weight                Methylmethacrylate                               25.5   5 Parts by weight                2-Dimethylaminoethyl-                methacrylateP&#39;10    95 Parts by weight                Cyclohexylmethacrylate                               25.1   5 Parts by weight                2-Dimethylaminoethyl-                methacrylate______________________________________ 
    
     Examples 11-15 
     Preparation of mixtures MF of pigment binders P and molecularly dissolved dyes 
     In addition to 1 kg pigment binder P or P&#39;, in accordance with Examples 1-10, 10 g soluble dye THERMOPLASTGELB® 104 from BASF AG are weighed and mixed in a tumbling mixer for 5 min. The dry mixture formed is subsequently extruded and strand-granulated on a single-screw laboratory extruder from the STORCK COMPANY at 180° C. 
     
                       TABLE 3______________________________________Example 6  Mixture  Mixture Components______________________________________11         MF 5     P 5 + THERMOPLASTGELB® 10412         MF 6     P 6 + THERMOPLASTGELB® 10413         MF 7     P 7 + THERMOPLASTGELB® 10414         MF 8     P 8 + THERMOPLASTGELB® 10415 (Comparison)      MF &#39;9    P &#39;9 + THERMOPLASTGELB® 10416 (Comparison)      MF &#39;10   P &#39;10 + THERMOPLASTGELB® 104______________________________________ 
    
     Examples 17-22 
     Preparation of mixtures SKMF of thermoplastic standard plastics SK and mixtures MF in accordance with Examples 11-16 
     For the preparation of 1 kg of a dyed standard plastic SKMF, 50 g of mixtures MF in accordance with Examples 11-15 are mixed with 950 g standard plastic SK in a tumbling mixer and extruded in a single-screw extruder at a screw rotational speed of 70 rpm. The extrusion temperatures are dependent on the type of standard plastic SK and listed below. The compatibility was evaluated visually on the extruded strand. Compatibility between mixing components SK and MF exists if the extruded strand is transparent (+); incompatibility, if the extruded strand has an opaque appearance (-). 
     The following standard plastics SK are compounded: 
     
                       TABLE 4______________________________________                          Extrusion                          TemperatureAbbreviation    Origin         (°C.)______________________________________PP (Polypropylene)           VESTOLEN® 7035                          200           from HulsAGPS (Polystyrene)           Polystyrene 158 K                          220           from BASF AGSAN (Styrene-   LURAN® 368 R from                          230acrylonitrile)  BASF AGPMMA (Polymethyl           PLEXIGLAS® Y8N                          240methacrylate)   from Rohm GmbHPC (Polycarbonate)           MAKROLON® 3100                          250           from Bayer AGPVC (Polyvinylchloride)           VESTOLIT® M 6067, Huls AG                          180______________________________________ 
    
     
                       TABLE 5______________________________________          Compatibility Evaluation          (transparent +/nontransparent coating-)Example  Mixture       PP    PS  SAN  PMMA  PC  PVC______________________________________17     SKMF5 = SK + MF5                +     +   +    +     +   +18     SKMF6 = SK + MF6                +     +   +    +     +   +19     SKMF7 = SK + MF7                +     +   +    +     +   +20     SKMF8 = SK + MF8                +     +   +    +     +   +21     SKMF&#39;9 = SK + MF&#39;9                +     -   +    +     -   +22     SKMF&#39;10 = SK +                +     +   -    -     -   +  MF&#39;10______________________________________ 
    
     Examples 23-31 
     Investigation of the compatibility of pigment binders P, in accordance with Examples 1 to 9, with Polystyrene 158K from BASF 
     1 g pigment binder P and 1 g Polystyrene 158 K (PS) are dissolved in 10 g 2-butanone at room temperature. The solution is poured into a Petri dish, and the solvent is completely removed at 70° C. and a vacuum of 20 mbar. The resulting film of the polymer mixture is visually evaluated and is investigated on a Kofler heating bench regarding its demixing temperature LCST (temperature at the transition: clear (thermodynamically compatible mixture)→cloudy (thermodynamically incompatible mixture)). 
     
                       TABLE 6______________________________________                   Film     LCSTExample     Mixture     Evaluation                            (°C.)______________________________________23          PS + P1 = 50/50                   clear    20524          PS + P2 = 50/50                   clear    20525          PS + P3 = 50/50                   clear    21026          PS + P4 = 50/50                   clear    15027          PS + P5 = 50/50                   clear    &gt;24028          PS + P6 = 50/50                   clear    21529          PS + P7 = 50/50                   clear    21030          PS + P8 = 50/50                   clear    16531          PS + P&#39;9 = 50/50                   cloudy   &lt;80(Comparison)______________________________________ 
    
     Obviously, numerous modifications and variations of the present invention are possible in light of the above teachings. It is therefore to be understood that within the scope of the appended claims, the invention may be practiced otherwise than as specifically described herein.