Abstract:
The present invention describes a process for the production of olivine lithium nickel phosphate composite by uniformly mixing oxides of Ni and P with Li 2 CO 3 , converting the mixture to a paste by adding glycerol, calcining the paste continuously to obtain the desired composite.

Description:
FIELD OF THE INVENTION  
         [0001]    The present invention relates to a process for the preparation of olivine lithium nickel phosphate (LiNiPO 4 ) composite, which is very useful for high voltage lithium reversible cells. LiNiPO4 is a reversible cathode material useful for high voltage cells of lithium in non-aqueous media.  
         BACKGROUND OF THE INVENTION  
         [0002]    In all the procedures available in the literature several disadvantages are observed:  
           [0003]    1. Phase impurity  
           [0004]    2. Longer duration of thermal preparation  
           [0005]    3. High temperature of operation  
           [0006]    4. pH control  
           [0007]    5. Several steps of preparation.  
         OBJECTS OF THE INVENTION  
         [0008]    The main object of this invention is to synthesis olivine LiNiPO 4  under suitable solid state reaction method which obviates the defects and draw backs hither to known in other method of preparation of this compound from already known procedures in literatures. 
       
    
    
     BRIEF DESCRIPTION OF THE ACCOMPANYING DRAWINGS  
       [0009]    [0009]FIG. 1 shows the X rays analysis confirming the formation of LiNiPO 4 .  
       SUMMARY OF THE INVENTION  
       [0010]    Accordingly the present invention provides a process for the preparation of olivine lithium nickel phosphate composite said process comprising, uniformly mixing oxides of Ni and P with Li 2 CO 3 , converting the mixture to a paste by adding glycerol, calcining the paste so obtained at 750° C. continuously for 12 hours to obtain the desired composite.  
         [0011]    In one embodiment of the invention, the oxide of phosphorous is P 2 O 5 .  
         [0012]    In a further embodiment of the invention, the nickel oxide is NiO.  
         [0013]    In another embodiment of the invention, the calcination is done in a furnace.  
       DETAILED DESCRIPTION OF THE INVENTION  
       [0014]    The prepared product was subjected to x-ray analysis. The product was found to be in single phase. Olivine lithium nickel phosphate composite is prepared by mixing oxides of nickel, phosphorous with lithium carbonate and heating together all in solid state condition.  
         [0015]    The cathode material is synthesised for a secondary battery, by heating a paste prepared by mixing fine particles of Li 2 CO 3 , P 2 O 4  and NiO in glycerol. This paste was initially heated slowly in a furnace to evaporate off glycerol in order to get a dried mass at 250° C. This dried mass was then continuously heated to 750° C. for 12 hrs. The compound formed was slowly cooled to room temperature and was ground well and then examined for its particle size, colour and XRD exposure. It was found that the prepared sample was purple in colour and was homogenous. X-rays analysis confirmed the formation of LiNiPO 4  according to FIG. 1.  
         [0016]    The following examples give the way of synthesising LiNiPO 4   
     
    
     EXAMPLE—1  
       [0017]    Li 2 CO 3 , NiO and P 2 O 5  in the molar ratio of 1:1:1 (0.74 gm; 1.49 gm and 1.42 gm respectively) were mixed slowly in glycerol binder (2 ml). Flux (urea in an amount of 2.402 gm) was added slowly under heating up to a temperature of 800° C. for a period of upto 10 hours. The mixture was then cooled to room temperature and the residue subjected to XRD exposure. The purple coloured product confirmed the production of olivine lithium nickel phosphate (LiNiPO 4 ) composite. The efficiency of the reaction was 90% and the product was obtained in single phase. Single electrode potential of LiNiPO 4  with respect to Li in 1 M LiClO 4  in propylene carbonate was 2.99 v.  
       EXAMPLE—2  
       [0018]    Li 2 CO 3 , NiO and P 2 O 5  in the molar ratio of 1:1:1: (0.74 gm; 1.49 gm and 1.42 gm respectively) were mixed slowly in glycerol binding (3 ml). Flux (urea in an amount of 2.402 gm) was added slowly under heating up to a temperature of 600° C. for a period of upto 12 hours. The mixture was then cooled to room temperature and the residue subjected to XRD exposure. The purple coloured product confirmed the production of olivine lithium nickel phosphate (LiNiPO 4 ) composite. The efficiency of the reaction was 90% and the product was obtained in single phase. Single electrode potential of LiNiPO 4  with respect to Li in 1 M LiClO 4  in propylene carbonate was 2.99 v.  
         [0019]    The advantages of the invention are  
         [0020]    1. Fine particles of the reactants viz. Li 2 CO 3 , NiO and P 2 O 3  were bound by glycerol and made the mixture into a paste uniform reaction during heating.  
         [0021]    2. Glycerol is used as a binder for the inorganic solid state reactants  
         [0022]    3. The product LiNiPO 4  is obtained in a single phase component free from impurities as evidenced by x-ray analysis.  
         [0023]    4. All the reactants uniformly leaving no unreacted initial reactant components.  
         [0024]    5. Addition of glycerol as a binder has no influence in the formation of the final product.  
         [0025]    6. A uniform homogeneous mixture of oxides of phosphorous (P 2 O 5 ) and nickel with Li 2 CO 3  were made into a paste to get a product of high purity.  
         [0026]    7. Glycerol used as a solvent for binding the oxides viz phosphorous and nickel with Li 2 CO 3  for making a paste of required consistency also enhanced the product of fine particles.  
         [0027]    8. The addition of a flux (urea) and excess addition of glycerol (solvent) as a binding material for oxides does not change the colour or quality of the end product