Abstract:
A method includes treating a CFx material with a base during the formation of a CFx cathode; and assembling the treated CFx material into a cathode electrode and assembling the cathode electrode with a lithium anode electrode and an electrolyte into a cell.

Description:
CLAIM OF PRIORITY 
       [0001]    This application claims the benefit of priority under 35 U.S.C. §119(e) of U.S. Provisional Patent Application Ser. No. 62/021,814, filed on Jul. 8, 2014, which is herein incorporated by reference in its entirety. 
     
    
     BACKGROUND 
       [0002]    A pulse generator (implantable medical device or IMD), such as a cardiac rhythm management device, can include a sealed housing containing various electronic and electro-chemical components. For example, batteries are often needed in implantable devices. 
         [0003]    Some batteries, such as lithium/carbon monoflouride (Li/CFx) batteries, can develop an increase in battery resistance after storage of the battery. This can result in a lower loaded voltage. 
       SUMMARY 
       [0004]    In example 1, this document describes a method comprising treating a CFx material with a base during the formation of a CFx cathode; and assembling the treated CFx material into a cathode electrode and assembling the cathode electrode with a lithium anode electrode and an electrolyte into a cell. 
         [0005]    In example 2, the subject matter of example 1 can optionally include wherein the base can include a LiOH. 
         [0006]    In example 3, the subject matter of any of examples 1 or 2 can optionally include wherein the base includes a KOH. 
         [0007]    In example 4, the subject matter of any of examples 1-3 can optionally include wherein the base includes a polymeric organic base. 
         [0008]    In example 5, the subject matter of example 4 can optionally include wherein the polymeric organic base includes an amine including H 2 N—(CH 2 )n-NH 2 , or H 2 N—[(CH 2 )n-NH—(CH 2 )n]m-NH 2 . 
         [0009]    In example 6, the subject matter of example 4 optionally include wherein the polymeric organic base includes a pyridine or an imidazole. 
         [0010]    In example 7, the subject matter of example 6 can optionally include wherein the polymeric organic base includes poly-4-vinylpyridine or poly-1-vinylimidazole. 
         [0011]    In example 8, the subject matter of any of examples 1-7 can optionally include wherein the base includes an anionic salt. 
         [0012]    In example 9, the subject matter of example 8 can optionally include wherein the anionic salt includes Li 2 SiO 3 , Li 2 B 4 O 7 , Li 2 CO 3 , or Li 3 PO 4 . 
         [0013]    In example 10, the subject matter of any of examples 1-9 can optionally include wherein the base includes a metal oxide. 
         [0014]    In example 11, the subject matter of example 10 can optionally include wherein the metal oxide includes Li 2 O or Al 2 O 3 . 
         [0015]    In example 12, the subject matter of any of examples 1-11 can optionally include wherein treating the CFx material includes mixing the base and the CFx material during a neutralization process. 
         [0016]    In example 13, the subject matter of any of examples 1-12 can optionally include wherein treating the CFx material includes mixing the base and the cathode material during a cathode manufacturing process. 
         [0017]    In example 14, the subject matter of any of examples 1-13 can optionally include wherein treating the CFx material is performed during both a neutralization process and a cathode manufacturing process. 
         [0018]    In example 15, a method includes: treating a CFx material with a base during a neutralization process of forming a cathode; further treating the treated CFx material with a base during a cathode manufacturing process where additives are added to the treated CFx material to form a cathode powder; assembling the cathode powder into a cathode; and forming a battery cell by assembling the cathode and a lithium anode and an electrolyte into a housing. 
     
    
     
       BRIEF DESCRIPTION OF THE FIGURES 
         [0019]    The drawings illustrate generally, by way of an example, but not by a way of limitation, various embodiments discussed in the present document. 
           [0020]      FIG. 1  shows a schematic cross-section of a battery, in accordance with one embodiment. 
           [0021]      FIG. 2  shows an example of a process flow for manufacturing a battery, in accordance with one embodiment. 
       
    
    
     DETAILED DESCRIPTION 
       [0022]      FIG. 1  shows a schematic cross-section of a battery  100 , in accordance with one embodiment. The battery  100  can be used in an implantable medical device or for other uses, for example. In this example, the battery includes a housing  110  that can be formed of a metal, for example. Within the housing  110  are a series of alternating anodes  112 ,  114 ,  116  and cathodes  113 ,  115 . Each adjacent anode and cathode are separated by a separator  117 , such as micro-porous polypropylene, or polyethylene, (or a combination of both), for example. The anodes  112 ,  114 ,  116  are connected together and connected to a terminal  122 . The cathodes  113 ,  115  are connected together and connected to a terminal  124 . Either one of or both of terminals  122 ,  124  can be insulated from the housing  110 . The housing is filled with an electrolyte solvent, such as dimethoxy ethane (DME). 
         [0023]    In some embodiments, the battery  100  is a Li/CFx battery where the anodes  112 ,  114 ,  116  include lithium and the cathodes include CFx (e.g., for example, where x can be between . 5  and  1 . 1 ). In some examples, the CFx is treated with a base at one or more steps of the cathode building process in order to neutralize acidic sites in CFx which can degrade the DME solvent in the electrolyte. Treating the CFx with a base can prevent degradation products from forming the DME, which can lead to a film being formed on the cathode, increasing its resistance. In addition, the degraded DME products can also migrate to the anode where the lithium can reduce the DME degradation products, resulting in higher anode resistance and in an overall increase in cell resistance. 
         [0024]      FIG. 2  shows an example of a process flow for manufacturing a battery  100 , in accordance with some embodiments of the present disclosure. In  FIG. 2  the process is broken down schematically to show five basic steps, a neutralization step  200 , a cathode manufacture step  220 , a vacuum bake cathode powder step  230 , a pelletize step  240 , and a cell assembly step  250 . In some examples, one or more of these steps can be omitted. 
         [0025]    In one example of a process flow, in the neutralization step  200 , the CFx  212  is mixed with a base solution  214 . The base solution  214  can include the base  218  and an isopropyl alcohol (IPA)/dionized (DI) water mixture  216 . In one embodiment, lithium hydroxide (LiOH) is used as the base used for neutralization. 
         [0026]    In such embodiments, a  0 . 5  molar (M) LiOH solution is used to neutralize the acidic sites on the CFx and to have some additional base to neutralize any additional acidic sites that may become present during the discharge of the cell. For example,  100  grams (g) of CFx  212  can be mixed with a 0.5M LiOH solution (500 milliliters (ml), 80% by vol. deionized (DI) water and 20% by vol. Isopropyl alcohol). In one example, the mixture  219  is stirred for 4 to 6 hours. The final pH of the mixture  219  is about 12.5. The CFx mixture  219  is then filtered with a Buchner funnel and a Whatman #1 filter. The resulting CFx cake is then dried at 120° C. in a forced air or vacuum oven. 
         [0027]    In one example, in the cathode manufacturing step  220 , the CFx cathode (83% CFx/10% Acetylene black/7% PTFE, as one example) can be made as follows. The base  202  (for example, LiOH) is mixed with DI water and stirred to dissolve. IPA is added to the mixture and the neutralized CFx from the neutralization step  200  is added. The solution is mixed and dried. Then further base  202  is mixed with DI water and dissolved. Then, the CFx, AB carbon  204 , and base/DI water/IPA solution  201  are mixed together. 
         [0028]    Then PTFE binder  205  can be mixed together with the CFx/AB slurry. The mixture is dried and cooled. The dried cake is broken up, blended, and sieved one or more times until a cathode powder results. The cathode powder is baked and vacuum dried  230 . The cathode powder can be pressed into pellets  240  if desired. The cathode powder or pellets are formed into a cathode by pressing or otherwise combining with a current collector. 
         [0029]    Treating the CFx with a base and having base present in the DI water/IPA solution during the cathode powder process results in a cell that will remain stable, in terms of resistance, during multiple storage periods at elevated temperature, because of the base reacting with the CFx. 
         [0030]    In various examples, depending on the quality of the original CFx material, for example, treating the CFx material with a base can be omitted in either the neutralization step  200  or the cathode manufacturing step  220 , because enough residual base can be present to react with the CFx to prevent further degradation. 
         [0031]    In one example, in the cell assembly step  250 , the cells can be formed having two cathodes formed of the CFx cathode material described herein and three anodes formed including lithium. One example includes two layers of separator in between the anodes and cathodes. The anodes and cathodes can be placed in the housing  252 . An electrolyte can be added to the housing. In some embodiments, the electrolyte can be a 1M LIBF4 in Gammabutyrolactone/DME (50/50 by vol.). 
         [0032]    In one example, the electrolyte can also include an additive such as 3,5-Dimethylisoxazole (DMI), which can scavenge acidic species. For example, the additive can include 1M LiBF4 in Gamma butyrolactone (GBL)/1,2 Dimethoxyethane (DME) (1:1 by vol.) with 0.5% by wt. DMI. 
         [0033]    In addition to the above example, other forms of neutralizers can be used. For example, acids can be neutralized using proton acceptors, also called bases or buffers that take up the proton forming a salt. The use of neutralizers can remove undesirable amounts of acid species in some materials. An example of this process is the use of LiOH or KOH to neutralize residual acid in electrolytically produced manganese dioxide, which can be produced from the CFx reacting with the electrolyte. 
         [0034]    Another example of a neutralization process is the neutralization of hydrofluoric acid (HF), with lithium hydroxide. The process is shown by the following chemical reaction: 
         [0000]      HF+LiOH→LiF+H 2 O
 
         [0035]    As shown, the proton from the acidic HF combines with the hydroxide group in the base LiOH to form the salt LiF and water. 
         [0036]    In other examples, other bases can be used that do not form water as a reaction product. These include organic bases that are soluble in the electrolyte. 
         [0037]    Another alternative is to use insoluble, polymeric organic bases to neutralize the acidic species that exist or are formed. The polymer organic bases can be included in the cathode mixture, for example. The result is a polymeric salt that is already a solid and does not precipitate in a way that will close pores. Examples of polymeric organic bases include, but are not limited to, amines such as H 2 N—(CH 2 )n-NH 2  and H 2 N—[(CH 2 )n-NH—(CH 2 )n]m-NH 2 , pyridines such as poly-4-vinylpyridine, imidazoles such as poly-1-vinylimidazole, and similar compounds that function as proton bases or buffering agents with a relatively high acid dissociation constant, pKa. The polymers can, for example, be single chain, linear or branching, crosslinked or copolymers. 
         [0038]    Another alternative to neutralize acidic species can be to use insoluble, anionic metal salts and metal oxides. Lithium ion is the cation of the anionic metal salts. The result of using insoluble, ionic metal salts and metal oxides is a compound that is already a solid and does not precipitate in a way that will close pores. An example of anionic metal salts includes, but is not limited to, Li 2 SiO 3 , Li 2 B 4 O 7 , Li 2 CO 3 , or Li 3 PO 4 . Some examples of metal oxides include, but are not limited to, Li 2 O Or Al 2 O 3 . 
         [0039]    The metal salts, metal oxides, or combinations of these additives discussed herein can be mixed directly with the cathode material. These additives can be added in quantities that effectively neutralize acid species yet do not significantly affect the performance of the battery. Moreover, it can further help if the binder contains appropriate groups that function as proton bases or buffering agents. This can limit the amounts of materials that are not electrochemically active in the cathode. 
         [0040]    The above detailed description includes references to the accompanying drawings, which form a part of the detailed description. The drawings show, by way of illustration, specific embodiments in which the invention can be practiced. These embodiments are also referred to herein as “examples.” Such examples can include elements in addition to those shown or described. However, the present inventors also contemplate examples in which only those elements shown or described are provided. Moreover, the present inventors also contemplate examples using any combination or permutation of those elements shown or described (or one or more aspects thereof), either with respect to a particular example (or one or more aspects thereof), or with respect to other examples (or one or more aspects thereof) shown or described herein. 
         [0041]    In the event of inconsistent usages between this document and any documents so incorporated by reference, the usage in this document controls. In this document, the terms “a” or “an” are used, as is common in patent documents, to include one or more than one, independent of any other instances or usages of “at least one” or “one or more.” In this document, the term “or” is used to refer to a nonexclusive or, such that “A or B” includes “A but not B,” “B but not A,” and “A and B,” unless otherwise indicated. In this document, the terms “including” and “in which” are used as the plain-English equivalents of the respective terms “comprising” and “wherein.” Also, in the following claims, the terms “including” and “comprising” are open-ended, that is, a system, device, article, composition, formulation, or process that includes elements in addition to those listed after such a term in a claim are still deemed to fall within the scope of that claim. Moreover, in the following claims, the terms “first,” “second,” and “third,” etc. are used merely as labels, and are not intended to impose numerical requirements on their objects. The above description is intended to be illustrative, and not restrictive. The above-described examples (or one or more aspects thereof) may be used in combination with each other. Other embodiments can be used, such as by one of ordinary skill in the art upon reviewing the above description. The Abstract is provided to comply with 37 C.F.R. §1.72(b), to allow the reader to quickly ascertain the nature of the technical disclosure. It is submitted with the understanding that it will not be used to interpret or limit the scope or meaning of the claims. Also, in the above Detailed Description, various features may be grouped together to streamline the disclosure. This should not be interpreted as intending that an unclaimed disclosed feature is essential to any claim. Rather, inventive subject matter may lie in less than all features of a particular disclosed embodiment. Thus, the following claims are hereby incorporated into the Detailed Description as examples or embodiments, with each claim standing on its own as a separate embodiment, and it is contemplated that such embodiments can be combined with each other in various combinations or permutations. The scope of the invention should be determined with reference to the appended claims, along with the full scope of equivalents to which such claims are entitled.