Abstract:
The invention disclosed herein relates to a method of making a monolayer or multilayer film structure as well as to a method of making a unitized pallet of goods wherein the pallet is stretched wrapped with the film structure. The film structure in each method comprises a polymer blend which contains at least one branched polymer (e.g. low density polyethylene (LDPE) or ethylene/vinyl acetate copolymer (EVA) and at least one linear polyethylene (e.g., LLDPE). The film structure is characterized as having a good overall balance of properties, including high ultimate elongation, excellent load retention and good machine direction tear.

Description:
CROSS-REFERENCE TO RELATED APPLICATION 
     This is a divisional of application Ser. No. 07/962,772 filed Oct. 19, 1992 now U.S. Pat. No. 5,399,426. 
    
    
     FIELD OF THE INVENTION 
     This invention relates to films made from blends of linear low density polyethylene and a minor amount of at least one branched polymer selected from the group consisting of ethylene homopolymers (e.g., high pressure low density polyethylene) and ethylene/vinyl actetate copolymers. The films have high elongation, excellent load retention and good tear resistance. 
     BACKGROUND OF THE INVENTION 
     Thermoplastic stretch wrap films are commonly used to unitize pallet loads of goods during shipment and storage. Optimally, the films should have good stretch performance (high ultimate elongation), low relaxation over time to prevent film sag and loss of goods from the pallet, good cling to hold the film to itself, good optical properties to view the palletized goods through the stretched film (low haze), and good puncture and tear resistance to resist failure on irregularly shaped or sharped-edged loads. 
     These stretch wrap films are commonly manufactured by blown film and cast film processes. The films are often monolayer films comprising linear low density polyethylene, but can also be coextruded film structures having different layers. 
     Coextruded multilayer films are also made which have specific film layers to do specific jobs (e.g., one layer provides cling while another provides stretchability). For example, U.S. Pat. No. 5,019,315 (Wilson), incorporated herein by reference, discloses a coextruded stretch film with two outer layers of LLDPE and a core layer of branched high pressure-type low density polyethylene (LDPE). Other additives are said to be included to help impart tack or cling to the film. Conversely, U.S. Pat. No. 4,339,180 (Briggs et al.) and U.S. Pat. No. 4,418,114 (Briggs et al.), both incorporated herein by reference, describe coextruded stretch wrap films having a core layer of LLDPE and a skin layer of LDPE. 
     Yet another type of cling wrap film is disclosed in U.S. Pat. No. 4,367,256 (Biel), incorporated herein by reference, where a blend of LDPE and a minor amount of LLDPE is used to make the film. Still another type of cling wrap film is disclosed in U.S. Pat. No. 4,518,654 (Eichbauer et al.), incorporated herein by reference, where an A/B stretch wrap film structure has one sided cling. The cling is imparted by using a specific cling additive, such as PIB to one layer of the structure. 
     While there have been various solutions to specific stretch wrap film problems, films having an overall balance of properties, including superior stretch and load retention, along with good tear resistance, are still desired for commercial viability in the marketplace. 
     SUMMARY OF THE INVENTION 
     Monolayer or multilayer film structures made from specific polymer blends have now been discovered which have this balanced set of properties making the structures suitable for use as stretch wrap film structures. The film structures have improved load retention and ultimate stretching capability, and adequate overall physical properties, such as tear resistance. The stretch wrap film structures comprise at least one layer of a polymer blend, wherein the polymer blend comprises: 
     (A) at least one linear polyethylene, and 
     (B) at least one branched polymer selected from the group consisting of ethylene homopolymers and ethylene/vinyl actetate copolymers, wherein the linear polyethylene and the branched polymer in the polymer blend are in a ratio from about 5:1 to about 33:1, as a function of the molecular weight of the branched polymer used. 
     In another aspect, the invention is a method of improving the ultimate elongation and load retention of a unitized pallet of goods by extruding the polymer blends disclosed herein into at least one layer of a film structure and stretch wrapping the pallet with the formed film structure. 
    
    
     BRIEF DESCRIPTION OF THE DRAWING 
     FIG. 1 graphically displays a range of blends of linear low density polyethylene and low density polyethylene compositions disclosed herein having properties suitable for use in stretch wrap film structures. The area of the graph defined and encircled by data points M, N, O, P and Q form a polygon and indicates those compositions having balanced properties as a function of melt index and percentage of the low density polyethylene. 
    
    
     DETAILED DESCRIPTION OF THE INVENTION 
     There are several ways to manufacture both the LLDPE and the branched LDPE for use in this invention. For example, U.S. Pat. No. 4,076,698 (Anderson et al.), incorporated herein by reference, involves the use of coordination catalysts of the &#34;Ziegler&#34; or &#34;Phillips&#34; type and includes variations of the Ziegler type, such as the &#34;Natta&#34; type for making linear polyethylenes. These catalysts may be used at very high pressures, but may also (and generally are) used at very low or intermediate pressures and also include various high pressure or low pressure gas phase processes. Other manufacturing techniques are disclosed variously in U.S. Pat. No. 2,699,457; U.S. Pat. No. 2,846,425; U.S. Pat. No. 2,862,917; U.S. Pat. No. 2,905,645; U.S. Pat. No. 3,058,963; and U.S. Pat. No. 4,668,752. The disclosures of all of these U.S. Patents are incorporated herein by reference. 
     The products made by coordination catalysts are generally known as &#34;linear&#34; polyethylenes because of the substantial absence of branched chains of polymerized monomer units pendant from the main polymer &#34;backbone.&#34; It is these linear polyethylenes to which the present invention primarily pertains. LLDPE and ultra linear low density polyethylene (ULDPE) (ULDPE is sometimes also known as very low density linear low density polyethylene, or VLDPE) typically have a density from about 0.87 grams/cubic centimeter (g/cm 3 ) to about 0.94 g/cm 3 , while linear high density polyethylene (HDPE) has a density from about 0.941 g/cm 3  to about 0.965 g/cm 3  (i.e., ethylene homopolymer). The term &#34;linear polyethylene&#34; used herein means that the linear polyethylene can be either ULDPE or LLDPE, or mixtures of one or more of each of these. 
     The density of the linear polyethylene, as measured by ASTM D-792, is lowered by copolymerizing ethylene with minor amounts of at least one alpha-, beta-ethylenically unsaturated alkene(s) having from 3 to 18 carbons per alkene molecule (e.g., 1-propene, 1butene, 4-methyl-1-pentene, 1-hexene, 1-octene, 1,9-decadiene and 1,7-octadiene), preferably 4-8 carbon atoms (e.g., 1-butene, 4-methyl-1-pentene, 1-hexene and 1-octene) and most preferably 8 carbon atoms (i.e., 1-octene). The density of the linear polyethylene (or blend of linear polyethylenes) for use in the present invention is generally from about 0.9 g/cm 3  to about 0.93 g/cm 3 , preferably from about 0.91 g/cm 3  to about 0.925 g/cm 3 , and especially from about 0.91 g/cm 3  to about 0.922 g/cm 3 . 
     The molecular weight of the linear polyethylene (or blend of linear polyethylenes) for use in the present invention is conveniently indicated using a melt index measurement according to ASTM D-1238, Condition 190° C./2.16 kg (formerly known as &#34;Condition(E)&#34; and also known as I 2 ). Melt index is inversely proportional to the molecular weight of the polymer. Thus, the higher the molecular weight, the lower the melt index, although the relationship is not linear. The melt index for the linear polyethylenes used herein is generally from about 0.5 grams/10 minutes (g/10 min) to about 10 g/10 min, preferably from about 0.7 g/10 min to about 5 g/10 min, and especially from about 2 g/10 min to about 4 g/10 min. 
     The high pressure branched LDPE, one of the branched polymers used herein, can also be made variously as disclosed in The Encyclopedia of Polymer Science and Engineering, Second Edition, Vol. 6, pp. 386-429 (John Wiley &amp; Sons), incorporated herein by reference. High pressure LDPE is usually ethylene homopolymer and is made using a free radical initiator at elevated pressures, frequently from about 15,000 psi to about 50,000 psi at temperature up to about 300° C. in tubular or stirred reactors, causing numerous long chain branches to be formed along the &#34;backbone&#34; of the polymer. The density of the LDPE for use in the present invention is also measured according to ASTM D-792 and is generally from about 0.9 g/cm 3  to about 0.93 g/cm 3 , preferably from about 0.915 g/cm3 to about 0.925 g/cm 3 . 
     The molecular weight of the LDPE (or blends of LDPE) for use in the present invention is also indicated using a melt index measurement according to ASTM D-1238, Condition 190° C./2.16 kg (I 2 ). The melt index is generally from about 0.1 grams/10 minutes (g/10 min) to about 20 g/10 min, preferably from about 0.1 g/10 min to about 10 g/10 min and especially from about 0.5 g/10 min to about 8 g/10 min. 
     Another of the branched polymers useful herein is an ethylene-vinyl actetate copolymer. Ethylene-vinyl acetate copolymers (EVA) can also be made variously. For example, EVA can be made using a high pressure process similar to that used to make LDPE, i.e., a free radical polymerization reaction between ethylene and vinyl acetate. These polymerizations can be performed in conventional stirred autoclave or tubular reactors, and are usually conducted at high pressures (e.g., greater than about 20,000 psi) and at high temperatures (e.g., 200-320° C.). The molecular weight of the EVA copolymers is typically controlled by addition of chain terminators, e.g., propylene or isobutylene. The type and level of branching of EVA copolymers is similar to that observed in LDPE. Typically, from about 5 to about 50 weight percent (based on the total weight of the final EVA copolymer) vinyl actetate is copolymerized with ethylene. For use herein, the EVA copolymers have a vinyl acetate content from about 2 to about 9 percent, based on the total weight of the final EVA copolymer. The molecular weight of the EVA is also indicated by measuring melt index using ASTM D-1238 Condition 190° C./2.16 kg (I 2 ), as described for the LDPE. The melt index range for the EVA copolymers is the same as that described for the LDPE. 
     The amount of the branched polymer added to the linear polyethylene is a minor amount. The proportion of linear polyethylene:branched polymer in the polymer blend is dependent upon the molecular weight of the branched polymer, but is generally from about 5:1 to about 33:1, especially from about 7:1 to about 25:1. For a branched polymer having a melt index from about 0.1 to about 1 grams/10 minutes, the ratio of linear polyethylene:branched polymer in the polymer blend is from about 16:1 to about 33:1. For a branched polymer having a melt index of greater than about 1 gram/10 minutes to about 2 grams/10 minutes, the ratio of linear polyethylene:branched polymer is from about 7:1 to about 24:1, especially from about 7:1 to about 16:1. For a branched polymer having a melt index of greater than about 2 gram/10 minutes to about 20 grams/10 minutes, the ratio of linear polyethylene:branched polymer is from about 4.5:1 to about 16:1, especially from about 4.5:1 to about 7.5:1. 
     Additives such as antioxidants (e.g., Irgafos™ 168 (a phosphite) and Irganox™ 1010 (a hindered phenolic) both made by Ciba-Geigy Corporation), cling additives (e.g., polyisobutylene (PIB), ethylene vinyl acetate (EVA), amorphous polypropylene, polyterpene, sorbitan monooleate, glycerol monooleate, and microcrystalline wax), antiblock additives, pigments, and the like can also be included in the polymer blends, to the extent that they do not interfere with the enhanced film properties discovered by Applicants. 
     The polymer blends are formed by any convenient method, including dry blending the individual components and subsequently melt mixing, either directly in the extruder used to make the film, or by pre-melt mixing in separate extruder before making the film. The polymer blends may also be prepared by dual polymerization techniques, or by melt conveying the desired amount of LDPE directly into a molten stream of LLDPE from a polymerization reactor, prior to pelletization of the polymer blend. The polymer blends can also be made by dry blending discrete polymers having the specified properties in appropriate weight ratios, as demonstrated herein. 
     The films formed from the polymer blends of LDPE and linear polyethylene are made using known film manufacturing techniques, such as blown film equipment or cast film equipment. Specific manufacturing techniques of blown film are discussed, for example, in The Encyclopedia of Chemical Technology, Kirk-Othmer, Third Edition, John Wiley &amp; Sons, New York, 1981, Vol. 16, pp. 416-417 and Vol. 18, pp. 191-192, the disclosures of all of which are incorporated herein by reference. Specific cast film manufacturing techniques are discussed, for example, in The Encyclopedia of Chemical Technology, Kirk-Othmer, Third Edition, John Wiley &amp; Sons, New York, 1981, Vol. 18, pp. 192-199, and in Modern Plastics Encyclopedia, mid-October 1988, Issue Vol. 65, Number 11, pp. 232-234, the disclosures of which are also incorporated herein by reference. No special consideration need be given to process the blends disclosed herein on conventional film forming equipment. 
     The films may be monolayer or multilayer films. However, for coextruded multilayer film structures (e.g., 3 layer film structures), the polymer blend described herein can be used as a core layer or as a skin layer of the structure. Generally, the polymer blend described herein comprises at least 60 percent of the total multilayer film structure. When the polymer blend disclosed herein is used as the core layer, preferably each skin layer can comprise a linear low density polyethylene having a density from about 0.9 g/cm 3  to about 0.925 g/cm 3  and a melt index from about 2 g/10 minutes to about 6 g/10 minutes. 
     The thickness of the films may vary, but is typically from about 0.3 to about 10 mils (7.6 to 254 micrometers). For the three layer film structures described herein, the film thickness is preferably from about 0.4 mils to about 2 mils, and especially from about 0.5 mils to about 1.2 mils. 
     Films comprising the LDPE/LLDPE polymer blends disclosed herein and having a thickness from about 0.5 mils to about 1.2 mils have a balanced set of properties. The film structures comprising the polymer blends disclosed herein preferably have an ultimate elongation of at least 20 percent (absolute) higher than the ultimate elongation obtained using the LLDPE alone in the same film structure. The balanced set of properties is also indicated by a load retention of greater than or equal to about 108 percent of that obtained using the LLDPE alone in the same film structure; and a tear strength of at least 50 percent of that obtained using the LLDPE alone in the same film structure, when tested in the same batch of samples. 
     EXAMPLES 
     The polymers listed in Table 1 are used to make coextruded A/B/A three layer film structures on a cast film line. The percentage of each layer (based on the total thickness of the structure) is 10 percent/80 percent/10 percent. For these examples, the film thickness is about 20 micrometers; thus each A layer is about 2 micrometers thick and the B layer is about 16 micrometers thick. The core polymer (or polymer blend) and the skin polymer is varied in these examples and the coextruded film structures are each tested for ultimate elongation, load force, and machine direction tear. 
     
                       TABLE 1______________________________________                  I.sub.2   DensityPolymer  Description     (g/10 min)                            (g/cm.sup.3)______________________________________I      ethylene/1-octene                  2.3       0.917  LLDPEII     ethylene/1-octene                  3.3       0.916  LLDPEIII    ethylene/vinyl acetate                  2.9       6 percent vinyl  copolymer                 acetateIV     LDPE            0.21      0.92V      LDPE            1.77      0.924VI     LDPE            7.13      0.919VII    LDPE            1.89      0.923VIII   LDPE            0.7       0.923IX     LDPE            1.81      0.922X      LDPE            4.2       0.924______________________________________ 
    
     Various 3-layer coextruded film structures are prepared using a cast film line. 
     The polymer blends are made by dry blending pellets of the specific polymers and feeding the dry blend into the appropriate extruder according to the weight ratios specified in Tables 2 and 7-13. The polymer blends described in each table are converted into film and tested separately from those described in the other tables, to ensure that a recent film sample from the same batch is fairly tested as a comparative. Data obtained from testing the film samples does not vary appreciably throughout a batch of film samples, but does vary somewhat from one testing batch to another, due to load cell changes/calibrations on the pallet testing device. Consequently, the data is evaluated within a given batch of film samples to ensure meaningful results. 
     The resultant multilayer film structures are tested for various physical properties using the following procedures: 
     Tear properties are measured using an Elmendorf tear tester according to ASTM D-1922. 
     Ultimate elongation and load force are measured using a Lantech SHS Film Test Stretch Wrapper. Ultimate elongation is the extent to which a stretch film will elongate prior to failure during the stretch wrapping process. This failure occurs between the rollers of a power pre-stretch unit. The ultimate elongation is measured by increasing the percent prestretch until the film fails between the two prestretch rollers. The percent prestretch at failure is referred to as the ultimate elongation. During this measurement, the force to load (F2) is preset to 10 pounds and the turntable rotates at a constant 9 rpm. 
     Load retention, or load force, reflects the ability of a stretch film to maintain a load of goods during storage or shipment. In this test, load retention is the force exerted by three wraps of film onto a load cell mounted on the face of an angle iron frame (which simulates a loaded pallet). For some of these tests, the stretch wrapper is set to obtain a 200 percent prestretch and 250 percent on-pallet elongation (designated as Load Force 200/250 (in pounds)). This test conforms to ASTM D-4649 A1.2. 
     
                                           TABLE 2__________________________________________________________________________                Branched polymer       LLDPE:branched                melt indexEx.   Core     polymer ratio                (g/10 min)                          Skin__________________________________________________________________________1* 100% Polymer I       NA       NA        100% Polymer II2* 100% Polymer I       NA       NA        100% Polymer III3   94% Polymer I       15.7:1   0.21      100% Polymer II    6% Polymer IV4*  91% Polymer I       10.1:1   0.21      100% Polymer II    9% Polymer IV__________________________________________________________________________ *Comparative Example Only NA = Not Applicable 
    
     
                       TABLE 3______________________________________   Ult.         Load Force                          MD   Elong.       200/250   TearEx.     (%)          (lbs)     (grams)______________________________________1**     325          38        2752**     350          46        2003       400          46        2454**     425          50        110______________________________________ **Comparative Example Only 
    
     Comparing Example 3 with Comparative Example 1, coextruded film made using a polymer blend of LDPE and LLDPE has a better balance of properties than a coextruded film made using the same LLDPE polymer alone as the core layer. The ultimate elongation is improved at least about 75% (absolute) for example 3, as compared with Comparative Example 1, while the load force is at least about 21% higher than, and the tear resistance is at least about 89% of comparative example 1. Comparative Example 4, a blend of LLDPE and LDPE in a ratio of about 10.1:1, has low tear strength and thus is not an example of the invention. 
     For Tables 7-11, three layer film structures are prepared as described in the fabrication conditions outlined in Tables 4-6 below: 
     
                       TABLE 4______________________________________Extruder 1 (skin)Zone       Temperature (°F.)______________________________________1          3502          4503          504-5054          505-506______________________________________ 
    
     
                       TABLE 5______________________________________Extruder 2 (core)Zone       Temperature (°F.)______________________________________1          350-3522          424-4263          482-4864          484-4865          484-4856          484-4867          485-486______________________________________ 
    
     
                       TABLE 6______________________________________Extruder 3 (skin)Zone       Temperature (°F.)______________________________________1          349-3502          424-4263          520-5214          520-521______________________________________ 
    
     Extruder 1 is a 2.5 inch diameter extruder; extruder 2 is a 3.5 inch diameter extruder; and extruder 3 is a 2 inch diameter extruder. Melt temperatures, extruder rpm and back pressure varies according to the polymer blend used to make the film structure and is easily determined and suitably varied by observing the stability of the extrusion melt. 
     For these experiments, the die temperature is held at about 525° F., the die width is about 30 inches, and the die gap is about 20 mils. The chill roll temperature is about 70° F. The line speed is about 800 feet/minute at a throughput of about 385 lbs/hour. The film gauge is about 0.8 mils and the film is trimmed to about 18 inches for these tests. 
     
                                           TABLE 7*__________________________________________________________________________Branched polymer melt index of 0.21 g/10 min       LLDPE:branched                Ult.  Load Force                             MD TearEx.   Core     polymer ratio                Elong. (%)                      200/250 (lbs)                             (gms)__________________________________________________________________________5   97% Polymer I       32.3:1   320   42     175    3% Polymer IV6**    91% Polymer I       10.1:1   345   50      87    9% Polymer IV7**   100% Polymer I       NA       285   38     318__________________________________________________________________________ *The skin for these film structures is 100% Polymer I **Comparative example only NA = Not Applicable 
    
     Comparing example 5 with comparative example 7**, the load force is higher by about 10%, while improving ultimate elongation by about 35% (absolute) and maintaining good tear resistance (about of the tear resistance of comparative example 1). 
     
                                           TABLE 8*__________________________________________________________________________Branched polymer melt index of 0.7 g/10 min        LLDPE:branched                 Ult.  Load Force                              MD TearEx.   Core      polymer ratio                 Elong. (%)                       200/250 (lbs)                              (gms)__________________________________________________________________________8   94% Polymer I        15.7:1   285   45     244    6% Polymer VIII9**    88% Polymer I         7.3:1   320   49      98    12% Polymer VIII10**   100% Polymer I        NA       260   37     275__________________________________________________________________________ *The skin for these film structures is 100% Polymer I **Comparative example only NA = Not Applicable 
    
     Comparing example 8 with comparative example 10**, the load force is higher by about 22%, while increasing ultimate elongation by about 25% (absolute) and maintaining tear resistance (about 89% of the tear resistance of comparative example 1). 
     
                                           TABLE 9*__________________________________________________________________________Branched polymer melt index of about 2 g/10 min        LLDPE:branched                 Ult.  Load Force                              MD TearEx.   Core      polymer ratio                 Elong. (%)                       200/250 (lbs)                              (gms)__________________________________________________________________________ 7**   100% Polymer I        NA       285   38     31811**    97% Polymer I        32.3:1   300   40     238    3% Polymer VII12  94% Polymer I        15.7:1   320   43     212    6% Polymer V13  94% Polymer I        15.7:1   320   42     195    6% Polymer IX__________________________________________________________________________ *The skin for these film structures is 100% Polymer I **Comparative example only 
    
     Comparing examples 12 and 13 with comparative example 7**, the load force is higher by at least about 10%, while ultimate elongation is increased by about 35% (absolute) and tear resistance is maintained (at least about 61% of the tear resistance of comparative example 1 ). 
     
                                           TABLE 10*__________________________________________________________________________Branched polymer melt index of about 2 g/10 min       LLDPE:branched                Ult.  Load Force                             MD TearEx.   Core     polymer ratio                Elong. (%)                      200/250 (lbs)                             (gms)__________________________________________________________________________10**   100% Polymer I       NA       260   37     27514  88% Polymer I       7.3:1    290   41     151    12% Polymer V15**    82% Polymer I       4.6:1    345   51      66    18% Polymer V__________________________________________________________________________ *The skin for these film structures is 100% Polymer I **Comparative example only NA = Not Applicable 
    
     Comparing examples 14 with comparative example 10**, the load force is higher by at least about 11%, while ultimate elongation is increased by about 30% (absolute) and tear resistance is maintained (at least about 55% of the tear resistance of comparative example 10**). 
     
                                           TABLE 11*__________________________________________________________________________Branched polymer melt index of about 4 g/10 min       LLDPE:branched                Ult.  Load Force                             MD TearEx.   Core     polymer ratio                Elong. (%)                      200/250 (lbs)                             (gms)__________________________________________________________________________10**   100% Polymer I       NA       260   37     27516**    97% Polymer I       32.3:1   265   39     266    3% Polymer X17  94% Polymer I       15.7:1   280   40     214    6% Polymer X18  88% Polymer I        7.3:1   315   42     167    12% Polymer X19  82% Polymer I        4.5:1   320   43     144    18% Polymer X20**    76% Polymer I        3.2:1   365   60     108    24% Polymer X__________________________________________________________________________ *The skin for these film structures is 100% Polymer I **Comparative example only 
    
     Comparing examples 18 and 19 with comparative example 10**, the load force is higher by at least about 13%, and ultimate elongation is higher by about 55% (absolute). Tear resistance is maintained at least about 52% of the tear resistance of comparative example 10**. 
     
                                           TABLE 12*__________________________________________________________________________Branched polymer melt index of about 7 g/10 min       LLDPE:branched                Ult.  Load Force                             MD TearEx.   Core     polymer ratio                Elong. (%)                      200/250 (lbs)                             (gms)__________________________________________________________________________ 7**   100% Polymer I       NA       285   38     31821**    97% Polymer I       32.3:1   285   38     254    3% Polymer VI22  94% Polymer I       15.7:1   305   41     170    6% Polymer VI23  91% Polymer I       10.1:1   310   43     208    9% Polymer VI__________________________________________________________________________ *The skin for these film structures is 100% Polymer I **Comparative example only 
    
     Comparing examples 22 and 23 with comparative example 7**, the load force is higher by at least about 8%, while maintaining good ultimate elongation (at least about 20% higher absolute elongation than comparative example 7**) and tear resistance (at least about 53% of the tear resistance of comparative example 7**). 
     
                                           TABLE 13*__________________________________________________________________________Branched polymer melt index of about 7 g/10 min       LLDPE:branched                Ult.  Load Force                             MD TearEx.   Core     polymer ratio                Elong. (%)                      200/250 (lbs)                             (gms)__________________________________________________________________________10**   100% Polymer I       NA       260   37     27524  88% Polymer I       7.3:1    290   44     214    12% Polymer VI25**    82% Polymer I       4.6:1    300   47     95    18% Polymer VI26**    76% Polymer I       3.2:1    305   50     32    24% Polymer VI__________________________________________________________________________ *The skin for these film structures is 100% Polymer I **Comparative example only NA = Not Applicable 
    
     Comparing example 24 with comparative example 10**, the load force is higher by at least about 18%, while having better ultimate elongation (30% higher absolute elongation) and adequate tear resistance (at least about 78% of the tear resistance of comparative example 10**). Example 24 also has a better balance of physical properties than does comparative examples 25** and 26**, notably a higher tear strength. 
     FIG. 1 shows preferred compositions comprising low density polyethylene and linear low density polyethylene disclosed herein which, when formed into film structures as described herein, have a good balance of physical properties. The compositions fall within the area of polygon MNOPQ bounded by the points M (32, 0.02), N (7.3, 2), O (4.5, 4), P (7.3, 7), and Q (10.1, 7) in FIG. 1 and includes compositions described on the lines represented by this polygon (i.e., lines MN, NO, OP, PQ and QM). 
     
                       TABLE 14*______________________________________Branched polymer is Polymer III; ethylene/vinylacetate copolymer                          Ult.  Load Force             LLDPE:branched                          Elong.                                200/200Ex.  Core         polymer ratio                          (%)   (lbs)______________________________________25    85% Polymer I             5.7:1        375   24 15% Polymer III 1** 100% Polymer I             NA           350   21______________________________________ *The skin for these film structures is 100% Polymer II NA = Not Applicable 
    
     Comparing example 25 with comparative example 1**, the ultimate elongation is about 25% (absolute) higher than the ultimate elongation of Comparative example 1** and the load force is higher by at least about 14%.