Abstract:
Disclosed is a substantially flat nanosheet with a first side and a second side, the first side having substantially different properties than the second side. The nanosheet may have self-assembly properties under certain anisotropic conditions such as phase separation boundaries, sheer stresses, friction, temperature gradients, viscosity, density, and/or combinations therein.

Description:
[0001]    This application claims the benefit of U.S. Provisional Application No. 61/654089, filed Jun. 1, 2012, which is incorporated herein by reference in its entirety. 
     
    
     BACKGROUND 
       [0002]    The present disclosure is related to the field of nanotechnology and materials science. Nanotechnology may include nanostructures, the chemical compositions of nanostructures, devices that include nanostructures and specific uses of nanostructures which may possess special properties that originate from structure&#39;s physical size. Particularly, the present disclosure is directed towards nanosheets. 
     
    
     
       BRIEF DESCRIPTION OF THE DRAWING 
         [0003]    The detailed description is set forth with reference to the accompanying FIGURE. 
           [0004]    The FIGURE is a perspective view of a nanostructure comprising a first functional surface and a second functional surface. 
       
    
    
     DETAILED DESCRIPTION 
     Overview 
       [0005]    While there are many examples of nanostructures that have original properties based on size alone, this disclosure presents an approach wherein the new properties originate not only from the nanostructure&#39;s size, but also from the shape of the nanostructures and their surface properties. Nanostructures according to this disclosure may possess anisotropic properties that lead to their ability to exhibit self-assembly under conditions such as, but not limited to, phase boundaries, shear stresses, friction, differences in surface tension, and/or temperature gradients. Such self-assembling properties are not typically displayed by bulk materials of the same chemistry. 
         [0006]    This disclosure describes a three-dimensional object with at least a first dimension less than 100 nanometers, and second and third dimensions substantially greater than 100 nanometers. The object may comprise a first surface and a second surface, the first surface having substantially different properties than the second surface. The different surface properties may be the result of different chemical structures or the same chemical structure with different orientations, crystal structures, defects, substitute dopants or other features that may lead to substantial differences in properties. By way of example and not limitation, the surface properties may include, surface termination, surface energy, hydrophilicity, thermal conductivity, coefficients of thermal expansion, reactivity and conductivity. By employing different features on the first surface and the second surface of the object, the particulate matter comprising the object may be configured to have a combination of different surface properties. 
         [0007]    In some embodiments, the object may be built using a top-down approach or, in other embodiments, the object may be built using a bottom-up approach. 
         [0008]    Multiple and varied example implementations and embodiments are described below. However, these examples are merely illustrative, and other implementations and embodiments of a nanostructure with functionally different surfaces may be implemented without departing from the scope of the disclosure. 
         [0000]    Illustrative Nanostructure with Functionally Different Surfaces 
         [0009]    The embodiments shown in the FIGURE is presented by way of example. The components shown in the FIGURE may be combined as desired to create a nanostructure with functionally different surfaces having various configurations. The components shown in the FIGURE may be rearranged, modified, duplicated, and/or omitted in some configurations. 
       Embodiment One 
       [0010]    As illustrated in the FIGURE, some embodiments may use a top-down approach in preparing a nanostructure  100  with different properties on a first side  102  and a second side  104 . A 1:1 layered material, such as a member of the phylosillicates group, may be provided. Phylosillicate group members may include, but are not limited to, kaolinite, serpentinite, and chlorite. The crystalline structure of this 1:1 layered material may comprise structurally different layers. A mechanical grinding technique may be employed to reduce the the particle size of the material. The material may exhibit lamellar dehydration properties. Lamellar dehydration may occur at certain temperatures when alternating layers of a hydrated material dehydrate preferentially while the other layers stay hydrated. After initial particle reduction (e.g., by the mechanical grinding technique), layer separation can be achieved by applying ultrasound, heat treatment, shear stress, electromagnetic field or other methods, either separately or combined. 
         [0011]    In one specific example, serpentine powder of a lizardite variety was dry-ground into a powder with an average particle size of less than 1 micron using a Spex SamplePrep® 8000M High Energy Ball Mill. After grinding, the powder was heated to 400° C. for eight hours to produce lamellar dehydration. The weight of the sample decreased by three to four percent, while full dehydration leads to thirteen percent weight loss. The resulting powder was then dispersed into ethanol and sonicated using a Cole-Parmer® 300W Ultrasonic Processor for one hour. The resulting flakes were observed to have a distorted magnesium oxide structure on one side and a tetrahedral silica structure on the other side. In some embodiments, the side comprising magnesium oxide may attach to a metals&#39; surface, exposing the silica side on the outside. 
       Embodiment Two 
       [0012]    In a second embodiment, nanostructures with two different sides can be synthesized using a bottom-up approach, such as the direct synthesis of layered nanosheets with subsequent modification of one side of the nanostructure. 
         [0013]    In one specific example, finely ground forsterite powder was mixed with sodium metasilicate and subjected to microwave hydrothermal synthesis at 250° C. in a Biotage® Advancer Kilobatch Microwave Pressure Reactor for three hours. The resulting powder was dispersed in ethanol using a 300W ultrasonic processor. Sedimentation was used to separate synthesized nanosheets from larger host particles of forsterite. 
         [0014]    Other methods may be used to generate nanostructures with a first side having substantially different properties than a second side. Some example methods may include lithography, chemical or plasma vapor deposition of a material on one of the first side or the second side of the nanostructure. For example, gold or platinum may be deposited on nanosheets of talc or molybdenum disulphide. 
       CONCLUSION 
       [0015]    Although this disclosure uses language specific to structural features and/or methodological acts, it is to be understood that the scope of the disclosure is not necessarily limited to the specific features or acts described. Rather, the specific features and acts are disclosed as illustrative forms of implementation.