Abstract:
The instant invention relates to the production of crystal-free, transparent glass articles which emit a strong bluish luminescence when excited by either ultraviolet or cathode rays. Such glass articles are prepared from aluminosilicate compositions which consist essentially, in terms of mole percent on the oxide basis, of about 15-30% Al 2  O 3  and 45-70% SiO 2 , the sum of those two components constituting at least 75 mole percent, but no more than about 95 mole percent, of the total composition, and 0.025-2% europium, expressed as Eu 2  O 3 . The remainder of the composition is generally made up of compatible monovalent, divalent, and/or trivalent modifying oxides. The desired high degree of luminescence is brought about by exposing the glass articles to a reducing atmosphere at a temperature below the softening point of the glass.

Description:
BACKGROUND OF THE INVENTION 
     Europium can exist in two oxidation states when present in glass. The more common trivalent state, Eu +3 , emits a moderately strong reddish photoluminescence, i.e., upon exposure to ultraviolet radiation, particularly where europium is included in high concentrations; but its cathodoluminescence, i.e., its emission when subjected to cathode rays, is quite weak. The divalent state, Eu +2 , can emit a strong bluish luminescence under both forms of excitation, viz., ultraviolet and cathode rays. However, in many conventionally melted, high temperature glasses a mixture of the two valence states will exist such that the luminescence color exhibited under ultraviolet or cathode ray excitation is the result of contributions from both valence states. Hence, luminescence colors can range from violet or violet-blue at low europium concentrations, thereby indicating a predominance of Eu +2  emission, to deep pink or red at high europium concentrations, thereby evidencing a predominance of Eu +3  emission. However, the cathodoluminescent efficiency of such glasses is, in the main, very poor. It has been postulated that the presence of the relatively inefficient Eu +3  ions degrades the efficiency of the Eu +2  ions which are present in the glass. Enhancement of the Eu +2  ion concentration in the glass has been attempted via melting the glass batch under reducing conditions, but such trials have not been uniformly satisfactory and, furthermore, the procedures required are cumbersome and not readily adaptable to commercial glass melting operations. 
     It has long been recognized that crystals commonly luminesce with much higher efficiencies than do glasses of like composition. Nevertheless, the transparency and freedom from light-scattering defects intrinsically present in glass articles have stimulated continued research to develop glass compositions which will luminesce brilliantly when subjected to a beam of high voltage electrons. Such glasses would be particularly suitable for the formation of transparent faceplates or screens for cathode ray tubes or other applications where image contrast or image resolution is of vital importance. 
     Unfortunately, with few exceptions, this research has not been rewarding in that the glasses developed have generally demonstrated poor cathodoluminescence efficiency. For example, the large majority of the glasses produced exhibited efficiencies of less than about 1%. Therefore, a cathodoluminescence efficiency of 1% has been deemed a baseline for certifying an improved glass. 
     OBJECTIVE OF THE INVENTION 
     The primary objective of the instant invention is to provide a transparent, crystal-free glass which will display a strong bluish luminescence when impinged by ultraviolet or cathode rays and which will exhibit a cathodoluminescence efficiency of at least 1%. 
     SUMMARY OF THE INVENTION 
     That objective can be achieved in glass articles which consist essentially, in terms of mole percent on the oxide basis, of about 15-30% Al 2  O 3  and 45-70% SiO 2 , the sum of those two components constituting at least 75 mole percent, but no more than 95 mole percent, of the total composition, and at least 0.025% europium, expressed as Eu 2  O 3 . The remainder of the composition will consist of other compatible metal oxides which can improve the melting and forming characteristics of the glass and/or modify the physical properties thereof. Such would include well-recognized network formers such as B 2  O 3  and P 2  O 5  and network modifiers such as the alkali metals, divalent metal oxides and, in particular, the alkaline earth metals, and trivalent metal oxides, with Y 2  O 3  and La 2  O 3  being especially useful. Such additions will be included in an amount of at least about 3 mole percent. The method of the invention comprehends three general steps. First, a batch of the proper composition is melted and simultaneously cooled and a glass article of a desired geometry shaped therefrom. Second, the glass article is exposed to a reducing environment at an elevated temperature below the softening point of the glass for a period of time sufficient to produce at least a surface layer on the glass article wherein the europium is present as Eu +2  ions. Third, the glass article is cooled to room temperature. 
     The temperature of firing in the reducing environment is dependent upon the composition of the glass. For example, with soft glasses, commonly containing monovalent ions such as the alkali metal ions, temperatures in the vicinity of 600° C. will be operable. In contrast, with harder glasses containing divalent and/or trivalent metal oxides, the firing will be conducted at a temperature in excess of 775° C., but less than about 950° L C., with the preferred temperatures ranging between about 800°-900° C. Hence, incomplete conversion to Eu +2  is encountered at temperatures below about 775° C., whereas some degree of deformation or softening of the glass is commonly experienced at temperatures above about 950° C. In all cases, the maximum firing temperature will be held below the softening point of the particular glass. 
     The time required for the firing step is temperature dependent and the progress of the reaction generally follows the law of diffusion, i.e., where the temperature is maintained constant, the rate of penetration, or the distance within the glass wherein the europium is reduced to Eu +2  ions, is proportional to the square root of time. In general, a firing time of at least about two hours will be required, with 4-16 hours being commonly employed. 
     Various gaseous reducing atmospheres are effective. For example, mixtures of carbon dioxide and carbon monoxide can be operable as can an atmosphere of hydrogen. A preferred embodiment employs forming gas, a gaseous mixture consisting of 92 volume percent N 2  and 8 volume percent H 2 . This combination of gases is relatively inexpensive and avoids the hazards of the hydrogen atmosphere. 
     DISCUSSION OF THE PRIOR ART 
     U.S. Pat. No. 2,049,765 discloses alkali metal borosilicate glasses containing a number of sensitizing agents in particulate form which will luminesce when subjected to ultraviolet or cathode rays. More specifically, the patent describes a colloidally-dispersed, crystalline structure in a glass matrix -- hence, an article having the structure of a two-phase system. Europium compounds were alleged to be suitable as sensitizing agents but no exemplary composition of such was provided. Furthermore, there is no disclosure whatever regarding the firing of the glassy-crystalline articles in a reducing environment. 
     U.S. Pat. No. 3,374,381 describes the fabrication of multi-color photoluminescent glass systems wherein a structure is made up of individual glass elements. These glass elements preferably have the same base components, such that the separate members can be joined together relatively easily, but will be doped with different photoluminescent agents. Hence, when subjected to long wavelength ultraviolet radiation, the different glass elements would luminesce in various colors. The patent mentions the development of glass compositions which will exhibit a bluish photoluminescence and three exemplary compositions are provided, two employing copper and a single example utilizing europium. However, there is no teaching whatever in the patent regarding the firing of glasses in a reducing environment and the sole europium-containing example involved a base glass composition consisting, in mole percent, of 29.8% MgO, 10.6% Al 2  O 3 , and 59.6% SiO 2  (column 6, lines 46-56), therefore outside of the composition area operable in the instant invention. Finally, there is no reference made to cathodoluminescence so, obviously, there is no discussion as to the efficiency displayed by the products of the patented invention. 
     U.S. Pat. No. 3,459,673 describes the preparation, via a hydrolysis technique, of rare earth-doped silica products exhibiting luminescence. Although europium is mentioned as a useful dopant, there is no disclosure of firing the articles in a reducing atmosphere, there is no disclosure regarding a bluish luminescence under either ultraviolet or cathode rays, and the very high silica contents render the glasses far removed from those of the present invention. 
     U.S. Pat. No. 3,522,191 discloses the melting of europium-containing glasses under reducing conditions, the base compositions of which include substantial amounts of B 2  O 3  and/or P 2  O 5 . Such glasses are, self-evidently, outside of the aluminosilicate glasses of the instant invention. Of particular interest, however, is Glass No. 25 in Example III which has the same composition as the sole europium-containing example of U.S. Pat. No. 3,374,381, supra. The comments made by the patentees (who are also the patentees of Patent No. 3,374,381, supra) regarding Glass No. 25 and others indicated a lack of strong luminescence therein and that their B 2  O 3  and/or P 2  O 5  -containing glasses constituted a marked improvement thereover. Those comments also underscored the fact, noted above in the section of the present specification entitled Background of the Invention, that attempts to produce high Eu +2  ion concentrations in glasses through melting under reducing conditions have been less than uniformly satisfactory. Thus, the instant invention is based upon firing the glass in a reducing environment after it has been shaped into an article. 
     DESCRIPTION OF PREFERRED EMBODIMENTS 
     Table I reports a number of approximate glass compositions, expressed in terms of mole percent on the oxide basis, illustrating the operable parameters of the instant invention. (Table IA recites the same glass compositions, but expressed in terms of parts by weight on the oxide basis.) The batch ingredients therefor can comprise any materials, either the oxides or other compounds, which, when melted together, will be converted to the desired oxide in the proper proportions. Some chloride is retained in the glass and, since it is not known with which cation(s) it is combined, it is simply reported in terms of CaCl 2 , the actual batch ingredient employed. 
     The batch ingredients for the individual examples were compounded, ballmilled together to assist in achieving a homogeneous melt, and deposited in platinum crucibles. (Larger scale melts involving pots or continuous melting tanks can, of course, be undertaken.) The crucibles were covered, placed in a furnace operating at about 1650° C., and the melts maintained therewithin for 16 hours with stirring. The melts were then poured into steel molds to yield slabs having dimensions of about 10 inches × 4 inches × 1/4 inch and those slabs were immediately transferred to annealers operating at 700°- 900° C. 
     The slabs were annealed to room temperature to allow observation of glass quality and to permit pieces to be cut therefrom. For example, tests for photoluminescence and cathodoluminescence were conducted on polished glass plates of about 10 × 10 × 1 millimeters. 
     Table I also records the Annealing Point (A.P.) and Strain Point (St.P.) determinations in °C. conducted on several of the glasses in accordance with conventional measuring techniques. 
     
                       TABLE I______________________________________   1      2      3    4    5    6    7    8______________________________________SiO.sub.2   60.3   60.3   60.4 60.3 60.6 60.7 49.8 60.1Al.sub.2 O.sub.3   20.4   20.5   20.5 20.4 20.6 20.6 25.8 20.4CaO     19.2   19.2   18.9 18.7 18.4 18.1 22.0 18.0CaCl.sub.2   --     --     --   --   --   --    1.0  1.2Na.sub.2 O   --     --     --   --   --   --    1.0 --Eu.sub.2 O.sub.3   0.03   0.06    0.2  0.3 0.45  0.6  0.5  0.3A.P.    --     --     --   --   --   --   --   838°St.P.   --     --     --   --   --   --   --   794°   9      10     11   12   13   14   15   16______________________________________SiO.sub.2   59.9   59.6   67.5 50.1 50.3 67.1 67.0 67.1Al.sub.2 O.sub.3   20.4   20.2   17.5 26.0 26.1 17.4 17.4 17.4CaO     17.9   17.8   13.7 22.6 --   --   --   --CaCl.sub.2    1.2    1.2   --   --   --   --   --   --MgO     --     --     --   --   23.1 15.0 --   --SrO     --     --     --   --   --   --   15.0 --BaO     --     --     --   --   --   --   --   15.1Eu.sub.2 O.sub.3    0.6    1.2    1.3  1.3  0.5  0.5  0.5  0.5A.P.    --     --     --   --   802°                                --   863°                                          --St.P.   --     --     --   --   763°                                --   814°                                          --   17     18     19   20   21   22   23______________________________________SiO.sub.2   67.0   66.3   66.9 60.0 82.2 75.5 71.0Al.sub.2 O.sub.3   17.4   23.2   23.4 21.9  1.2 --    1.1ZnO     15.0   --     --   --   --   --   --Y.sub.2 O.sub.3   --     10.0   --   --   --   --   --La.sub.2 O.sub.3   --     --      9.2 --   --   --   --K.sub.2 O   --     --     --    6.0 --   16.5  3.3Na.sub.2 O   --     --     --    6.0  4.1 --    3.3Li.sub.2 O   --     --     --    6.0 --   --    3.3B.sub.2 O.sub.3   --     --     --   --   12.2  7.7 --SrO     --     --     --   --   --   --   17.7Eu.sub.2 O.sub.3    0.5    0.6    0.6  0.2  0.3  0.3  0.3A.P.    768°          877°                 853°                      --   --   --   --St.P.   726°          833°                 809°                      --   --   --   --______________________________________ 
    
     
                       TABLE IA______________________________________   1      2      3    4    5    6    7    8______________________________________SiO.sub.2   53.3   53.2   53.3 52.8 52.5 52.2 41.5 52.0Al.sub.2 O.sub.3   30.7   30.7   30.6 30.4 30.3 30.1 36.6 30.0CaO     15.9   15.8   15.5 15.3 14.9 14.6 17.1 14.6CaCl.sub.2   --     --     --   --   --   --    1.5  1.9Na.sub.2 O   --     --     --   --   --   --    0.8 --Eu.sub.2 O.sub.3   0.16   0.31   0.93  1.5  2.3  3.1  2.4  1.5______________________________________   9      10     11   12   13   14   15   16______________________________________SiO.sub.2   51.2   49.7   57.5 40.8 44.5 61.1 53.4 48.6Al.sub.2 O.sub.3   29.6   28.7   25.4 36.0 39.2 27.0 23.6 21.4CaO     14.3   13.9   10.9 17.2 --   --   --   --CaCl.sub.2    1.9    1.8   --   --   --   --   --   --MgO     --     --     --   --   13.7  9.2 --   --SrO     --     --     --   --   --   --   20.7 --BaO     --     --     --   --   --   --   --   27.9Eu.sub.2 O.sub.3    3.0    5.8    6.3  6.0  2.6  2.7  2.4  2.1   17     18     19   20   21   22   23______________________________________SiO.sub.2   55.9   45.3   40.7 51.1 78.7 67.3 61.5Al.sub.2 O.sub.3   24.7   26.9   24.2 31.8  1.9 --    1.6ZnO     17.0   --     --   --   --   --   --Y.sub.2 O.sub.3   --     25.6   --   --   --   --   --La.sub.2 O.sub.3   --     --     33.1 --   --   --   --K.sub.2 O   --     --     --    8.0 --   23.1  4.5Na.sub.2 O   --     --     --    5.3  4.1 --    3.0Li.sub.2 O   --     --     --    2.5 --   --    1.4B.sub.2 O.sub.3   --     --     --   --   13.6  8.0 --SrO     --     --     --   --   --   --   26.5Eu.sub.2 O.sub.3    2.5    2.2    2.0  1.2  1.7  1.6  1.4______________________________________ 
    
     Table II records several treatments in reducing atmospheres which were applied to the exemplary compositions of Table I. As was explained above, the slabs formed from the crucible melts were annealed to room temperature to enable test samples to be cut therefrom. Table II recites visual observations of photoluminescence of the polished glass plates exposed to sources of ultraviolet radiations having a wavelength of 2537A and 3650A, respectively, and cathodoluminescence resulting from the bombardment of electrons having an energy of 11 kilovolts (kV). It must be recognized that the annealing to room temperature prior to firing in a reducing environment is not mandatory for the successful operation of the invention. Hence, if desired, the glass shape formed from the molten batch max be immediately subjected to the firing step and then cooled to room temperature. Such practice can increase the speed of the overall process while also providing energy savings. 
     Forming gas (92% by volume N 2  -- 8% by volume H 2 ) was utilized as the source of a reducing atmosphere in the firings reported in Table II because of its safety and relative cheapness. The influence of moisture on the action of the reducing environment was studied through the use of &#34;wet&#34; forming gas. That is, the forming gas was passed through a container of distilled water prior to its introduction into the firing chamber. Moisture was thereby picked up from the reservoir of water and carried into the firing chamber. In like manner, the comparison examples of &#34;wet&#34; nitrogen employed the same apparatus. 
     The test glass samples of Table II were placed within a sealed furnace tube with the appropriate gaseous atmosphere flowing at a rate of 100 cc/minute. The furnace tube was purged with the treating gas prior to the actual firing step to insure reproducibility of results. In each case, the glass was heated from room temperature to the recorded temperature at furnace rate which, in the present case, was about 500° C./minute. It will be understood that much slower, or even faster, heatup rates are possible. However, care must be exercised where more rapid heatup rates are employed to avoid thermal breakage. 
     
                                           TABLE II__________________________________________________________________________Example No.  Heat Treatment                2537A     3650A     11 kV Electrons__________________________________________________________________________1      None          Blue-white                          Blue      Violet-blue1      900° C.-16 hrs. forming                Strong blue                          Strong blue                                    Strong blue  gas2      None          Blue-white                          Blue      Blue-violet2      900° C.-16 hrs. forming                Strong blue                          Strong blue                                    Strong blue  gas3      None          Lavender  Blue-white                                    Violet3      900° C.-16 hrs. forming                Bright blue                          Bright blue                                    Bright blue  gas4      None          Light pink                          Light lavender                                    Lavender4      900° C.-16 hrs. forming                Bright blue                          Bright blue                                    Bright blue  gas5      None          Pink      Lavender  Pink5      900° C.-16 hrs. forming                Bright blue                          Bright blue                                    Bright blue  gas6      None          Reddish-pink                          Pink      Deep pink6      900° C.-16 hrs. forming                Bright blue                          Bright blue                                    Bright blue  gas7      None          Orange-pink                          Violet pink                                    Violet pink7      900° C.-16 hrs. forming                Bright blue                          Bright blue                                    Bright blue  gas7      900° C.-16 hrs. wet                Bright blue                          Bright blue                                    Bright blue  forming gas7      925° C.-16 hrs. forming                Bright blue-                          Bright blue-                                    Bright blue-  gas           glass softened                          glass softened                                    glass softened8      None          Lavender  Blue violet                                    Violet pink8      850° C.-16 hrs. Air                Lavender  Blue violet                                    Violet pink8      850° C.-16 hrs. Wet N.sub.2                Lavender  Blue violet                                    Violet pink8      850° C.-16 hrs. forming                Bright blue                          Bright blue                                    Bright blue  gas8      900° C.-16 hrs. forming                Bright blue                          Bright blue                                    Bright blue  gas8      950° C.-16 hrs. forming                Bright blue -                          Bright blue -                                    Bright blue -  gas           glass softened                          glass softened                                    softened9      None          Deep pink Violet-pink                                    Deep pink9      900° C.-16 hrs. Air                Deep pink Violet-pink                                    Deep pink9      900° C.-16 hrs. N.sub.2                Deep pink Violet-pink                                    Deep pink9      900° C.-16 hrs. forming                Bright blue                          Bright blue                                    Bright blue  gas9      900° C.-16 hrs. wet                Bright blue                          Bright blue                                    Bright blue  forming gas10     None          Deep red  Deep red  Deep red10     900° C.-16 hrs. forming                Bright blue                          Bright blue                                    Bright blue  gas10     900° C.-16 hrs. wet                Bright blue                          Bright blue                                    Bright blue  forming gas11     None          Red-orange                          Deep pink Deep pink11     750° C.-16 hrs. forming                Violet-pink                          Violet-blue                                    Violet-blue  gas11     800° C.-16 hrs. forming                Bluish-white                          Bluish-white                                    Bluish-white  gas11     825° C.-16 hrs. forming                Bright blue                          Bright blue                                    Bright blue  gas11     850° C.-4 hrs. forming                Bright blue                          Bright blue                                    Bright blue  gas12     None          Red-orange                          Orange pink                                    Deep pink12     750° C.-16 hrs. forming                Violet-pink                          Violet-blue                                    Violet-pink  gas12     825° C.-16 hrs. forming                Bright blue                          Bright blue                                    Bright blue  gas12     850° C.-4 hrs. forming                Bright blue                          Bright blue                                    Bright blue  gas13     None          Deep blue Lavender  Violet-pink13     800° C.-4 hrs. forming                Bright blue                          Bright blue                                    Bright blue  gas13     825° C.-16 hrs. forming                Bright blue                          Bright blue                                    Bright blue  gas13     900° C.-16 hrs. forming                Bright blue -                          Bright blue -                                    Bright blue -  gas           glass softened                          glass softened                                    glass softened14     None          Pink      Blue-white                                    Deep pink14     825° C.-16 hrs. forming                Bright blue                          Bright blue                                    Bright blue  gas14     850° C.-16 hrs. forming                Bright blue                          Bright blue                                    Bright blue  gas14     950° C.-16 hrs. forming                Bright blue-                          Bright blue-                                    Bright blue -  gas           glass softened                          glass softened                                    glass softened15     None          Pink      Blue-white                                    Deep pink15     825° C.-16 hrs. forming                Bright blue                          Bright blue                                    Bright blue  gas15     950° C.-16 hrs. forming                Bright blue                          Bright blue                                    Bright blue  gas16     None          Pink      White     Deep pink16     825° C.-16 hrs. forming                Bright blue                          Bright blue                                    Bright blue  gas16     850° C.-16 hrs. forming                Bright blue                          Bright blue                                    Bright blue  gas17     None          Orange pink                          Pink      Deep pink17     825° C.-16 hrs. forming                Bright blue                          Bright blue                                    Bright blue  gas17     850° C.-4 hrs. forming                Bright blue                          Bright blue                                    Bright blue  gas17     850° C.-16 hrs. forming                Bright blue-hazy                          Bright blue-hazy                                    Bright blue-hazy  gas           glass-opalized at                          glass-opalized at                                    glass-opalized at                900° C.                          900° C.                                    900° C.18     None          Violet-pink                          Lavender-blue                                    Reddish-pink18     825° C.-16 hrs. forming                Bright blue                          Bright blue                                    Bright blue  gas18     900° C.-16 hrs. forming                Bright blue                          Bright blue                                    Bright blue  gas19     None          Pink      Blue-violet                                    Pink19     825° C.-16 hrs. forming                Bright blue                          Bright blue                                    Bright blue  gas20     None          Pink      Blue      Violet20     800° C.-16 hrs. forming                Bright blue                          Bright blue                                    Bright blue  gas20     850° C.-16 hrs. forming                Bright blue-                          Bright blue-                                    Bright blue-  gas           glass softened                          glass softened                                    glass softened21     None          Pink      Lavender  Pink21     650° C.-5 hrs. forming                Weak blue Weak blue Weak blue  gas21     700° C.-5 hrs. forming                Moderate blue                          Moderate blue                                    Moderate blue  gas21     750° C.-16 hrs. forming                Moderate blue -                          Moderate blue -                                    Moderate blue -  gas           glass softened                          glass softened                                    glass softened22     None          Red       Red       Red22     700° C.-5 hrs. forming                Red       Red       Red  gas22     750° C.-5 hrs. forming                Red - glass                          Red - glass                                    Red- glass  gas           softened  softened  softened23     None          Red-orange                          Red-orange                                    Red-orange23     650° C.-5 hrs. forming                Red-orange                          Red-orange                                    Red-orange  gas23     700° C.-5 hrs. forming                Red-orange - glass                          Red-orange - glass                                    Red-orange -  gas           softened  softened  softened__________________________________________________________________________ 
    
     Several features of interest can be discerned from Table II. For example, the untreated glasses of Examples 1-6 illustrate the tendency for the luminescence to acquire an increasingly reddish character as greater amounts of europium are incorporated in the glass. However, after exposure to reducing conditions, each manifests a considerably brighter luminescene, and of a blue color, under both ultraviolet and cathode rays. Visually, the brightness of the luminescence increases from Example 1 through Example 6. 
     Comparison tests utilizing wet and dry forming gas did not evidence any marked difference in effect therebetween. The use of gaseous atmospheres of nitrogen (a neutral environment) and air (an oxidizing environment) clearly pointed to the need for reducing conditions to secure the presence of Eu +2  ions with the consequent blue luminescence. 
     Treatments at 750° C. of Examples 11 and 12 demonstrated incomplete conversion to Eu +2  ions. A temperature of at least about 800° C. appears to be a preferred lower limit for glasses containing divalent or trivalent modifying oxides, depending upon glass composition, and will be determined for each glass of interest. With the softer, monovalent ion glasses, temperatures of about 600° C. will be operable. The upper temperature limit comprises that temperature at which opalization or softening of the glass occurs. Most of the glasses recorded in Table II displayed some degree of softening at 950° C. Exceptions thereto were Examples 7 and 13, which softened at lower temperatures, and Example 17 which opacified. 
     To prove that the blue surface luminescence was not caused by the development of a transparent surface crystalline phase, Examples 11, 12, and 14, after being exposed to dry forming gas for 16 hours at 950° C., and Example 17, after being fired in dry forming gas for 16 hours at 850° C., were examined by surface X-ray diffraction techniques. Only Example 17, noted as hazy in Table II, exhibited a trace of surface crystallization. The other samples evidenced no trace of crystallization. 
     Examples 21-23 are softer glasses containing little or no alumina. Thus, Examples 22 and 23 represent glasses in which surface reduction does not take place at temperatures below the glass deformation temperature. Example 21 is illustrative of a borderline composition, with respect to the firing step, in that a weak-to-moderate blue luminescence can be secured at temperatures approaching the softening point thereof. Example 20 can exhibit relatively good blue luminescence but its cathodoluminescence is somewhat less than that of Example 3 containing about the same Eu 2  O 3  content on the molar basis. 
     A more detailed examination of the cathodoluminescence behavior of several of the exemplary compositions is set out in Table III. Because these luminescent surfaces are produced by the action of a diffusing gas, viz., hydrogen, the depth and uniformity of the surface layer so produced must be characterized as a function of the penetrating power of impinging electrons to which the surface may be exposed during actual service. Most conventional cathode ray tube phosphors consist of some luminescence activator uniformly distributed within the structure of a host material, customarily a crystalline material. 
     A measurement of cathodoluminescence intensity versus electron accelerating potential, measured at a constant beam current, for such a uniform material will generally yield a straight line. This linearity indicates that over the electron energy range encountered in the conventional cathode ray tube, such as a television receiver tube, the cathodoluminescence efficiency of the phosphor is constant. Since electrons of different energies penetrate the phosphor to different depths, linearity also illustrates that the efficiency of the phosphor is constant throughout the thickness of the phosphor corresponding to the penetration depth of the impinging electrons. A convenient estimate of electron penetration depth is given by the &#34;penetration limit&#34; defined as that depth beyond which negligible power is transmitted to the material. Penetration limits are set out below for the electron energy range, expressed in electron volts (KEV), customarily obtaining in the cathode ray tube and color television industries. The data are derived from Terrill&#39;s Equation recited on page 158 of An Introduction to Luminescence of Solids, Humboldt W. Leverenz, Dover Publications, Inc., New York, 1968. A glass density of 2.5 g/cm 3  is assumed in the calculations. 
     
         ______________________________________Electron Energy in KEV           Penetration Limit in Microns______________________________________ 5              0.2510              1.0015              2.2520              4.0025              6.25______________________________________ 
    
     Hence, to provide constant efficiency for electrons up to 25 KEV in energy, the reducing conditions to which the glass is exposed must be capable of insuring the presence of Eu +2  ions to a depth of about 6 microns. 
     Table III records measurements made on several of the examples from Table I over the range of 6-24 kV acceleration potential (6-24 KEV electron energy). The range of linearity of cathodoluminescence intensity and, therefore, of constant efficiency is given as well as the calculated efficiency. Also, the wavelength of maximum photoluminescent intensity and the C.I.E. color coordinates are reported. Finally, Table III reports a measure of aging resistance (AR) expressed in %. 
     The aging of a cathodoluminescent phosphor is defined as the loss of luminescence intensity under sustained electron bombardment. It is measured during an accelerated aging test in which a sample is exposed to a high current density (30 microamperes/cm 2 ) of high energy electrons (25 kV) for a period of 10 minutes. Aging resistance is defined as the ratio of the intensity of cathodoluminescence after 10  minutes exposure to the test conditions, to the intensity at the commencement of the test. 
     In general, higher-temperature, longer-time, heat treatments in reducing environments give rise to the most desirable combination of linearity, high efficiency over the electron energy range of most interest, and good aging resistance. It will be appreciated, of course, that optimum conditions must be determined for each individual glass. 
     In general, the aging resistance of these surface-activated europium-containing glasses is superior to that of most conventional glasses. It is exceeded only by that exhibited by the manganese-doped RO-Al 2  O 3  -SiO 2  glasses disclosed in U.S. Pat. No. 3,962,117. 
     Although Table III reports visual descriptions of &#34;bright blue&#34; cathodoluminescence, it is apparent from the C.I.E. color coordinates that a range of bluish colors can be obtained, differing principally in saturation. Saturation is that quality of color which differentiates an intense &#34;pure&#34; blue color (saturated) from a pastel blue (relatively unsaturated). Side-by-side comparisons of polished glass plates can be useful in distinguishing such color differences in the respective luminescence emissions. 
     
                                           TABLE III__________________________________________________________________________Example        Linear Efficiency                       Wave Length                                 C.I.E. Coordinates (at 24 kV)No.  Heat Treatment          Range (kV)                 %     A      AR x        y__________________________________________________________________________ 7   900° C. - 16 hrs.          6-24   1.7   4500   50 0.180    0.185forming gas 7   900° C. - 16 hrs.          6-24   1.5   4600   52 0.189    0.212wet forming gas 8   900° C. - 16 hrs.          6-24   2.0   4300   61 0.167    0.121forming gas 9   900° C. - 16 hrs.          6-24   1.9   4450   57 0.172    0.150forming gas 9   900° C. - 16 hrs.          6-24   1.7   4500   56 0.176    0.166wet forming gas10   None      6-24   0.17  6200   -- 0.615    0.31710   900° C. - 16 hrs.          6-24   1.4   4500   49 0.183    0.200forming gas10   900° C. - 16 hrs.          6-24   1.3   4600   40 0.198    0.220wet formng gas11   825° C. - 16 hrs.          6-24   0.3   4400   68 0.189    0.167forming gas11   850° C. - 4 hrs.          6-16   1.7   4500   55 0.178    0.169forming gas12   825° C. - 16 hrs.          6-24   0.5   4400   69 0.181    0.153forming gas12   850° C. - 4 hrs.          6-10   1.1   4700   48 0.248    0.258forming gas13   850° C. - 4 hrs.          6-12   1.5   4450   60 0.178    0.145forming gas14   825° C. - 16 hrs.          6-24   1.7   4500   57 0.184    0.193forming gas14   850° C. - 16 hrs.          6-24   1.7   4500   51 0.184    0.199forming gas15   825° C. - 16 hrs.          6-24   2.1   4500   60 0.176    0.165forming gas15   950° C. - 16 hrs.          6-22   2.2   4500   54 0.172    0.156forming gas16   825° C. - 16 hrs.          6-24   1.9   4400   69 0.162    0.113forming gas16   850° C. - 4 hrs.          6-22   1.8   4500   48 0.183    0.192forming gas17   825°  C. - 16 hrs.          6-20   1.3   4400   69 0.172    0.147forming gas17   800° C. - 4 hrs.          6-22   1.9   4500   52 0.176    0.167forming gas18   825° C. - 16 hrs.          6-16   1.2   4700   43 0.213    0.248forming gas18   900° C. - 16 hrs.          6-20   1.2   4650   46 0.200    0.249forming gas19   825° C. - 16 hrs.          6-24   1.8   4500   47 0.170    0.162forming gas__________________________________________________________________________ 
    
     Table III clearly demonstrates the superior cathodoluminescent properties exhibited by the glasses of the instant invention. Hence, power conversion efficiencies greater than 1% are customarily achieved and, in some instances, can surpass 2%. Also, the values of aging resistance commonly exceed 50% in the above-described test. 
     Table IV reports several examples, expressed in mole percent on the oxide basis, which were produced in accordance with the method outlined above for the exemplary compositions of Table I and Annealing Points (A.P.) and Strain Points (St.P.) where measured. (Table IVA records the compositions in terms of weight percent.) 
     
                                           TABLE IV__________________________________________________________________________24      25 26 27  28  29 30 31 32 33  34 35 36  37__________________________________________________________________________SiO.sub.2    59.6   59.9      59.8         59.9             59.9                 59.9                    59.9                       59.9                          59.9                             59.8                                 59.9                                    59.9                                       59.9                                           59.9Al.sub.2 O.sub.3    10.6   19.9      20.0         20.0             19.9                  9.9                    10.0                       10.0                          20.0                             10.0                                 20.0                                    20.0                                       20.0                                           20.0MgO 29.8   19.0      -- --  --  -- -- -- -- --  -- -- --  --CaO --  -- 19.9         --  --  -- -- -- -- --  16.9                                    16.9                                       --  --SrO --  -- -- --  --  29.9                    -- -- -- --  -- -- --  --BaO --  -- -- --  --  -- 29.9                       -- -- --  -- -- --  --ZnO --  -- -- --  --  -- -- 29.9                          -- --  -- -- --  --CdO --  -- -- 19.9             --  -- -- -- -- --  -- -- --  --PbO --  -- -- --  19.9                 -- -- -- -- --  -- -- --K.sub.2 O    --  -- -- --  --  -- -- -- 19.9                              9.9                                 --  1.0                                       --  --Na.sub.2 O    --  -- -- --  --  -- -- -- --  9.9                                  3.0                                     1.0                                       19.9                                           --Li.sub.2 O    --  -- -- --  --  -- -- -- -- 10.1                                 --  1.0                                       --  19.9Eu.sub.2 O.sub.30.006    0.3      0.25         0.26             0.24                 0.24                    0.24                       0.24                          0.26                             0.24                                 0.25                                    0.25                                       0.25                                           0.25A.P.    --  -- -- 766°             693°                 -- -- -- -- 453°                                 -- -- 764°                                           668°St.P.    --  -- -- 702°             646°                 -- -- -- -- 414°                                 -- -- 707°                                           622°__________________________________________________________________________ 
    
     
                                           TABLE IVA__________________________________________________________________________24     25 26 27 28 29 30 31 32 33 34 35 36 37__________________________________________________________________________SiO.sub.2    61.0  55.1     52.6        43.4           35.4              46.1                 38.7                    50.4                       47.3                          59.8                             52.5                                52.5                                   51.7                                      57.0Al.sub.2 O.sub.3    18.5  31.2     30.0        24.6           20.0              13.0                 11.0                    14.3                       26.8                          15.5                             29.7                                29.7                                   29.3                                      32.2MgO 20.5  12.3     -- -- -- -- -- -- -- -- -- -- -- --CaO -- -- 16.4        -- -- -- -- -- -- -- 13.9                                13.9                                   -- --SrO -- -- -- -- -- 39.8                 -- -- -- -- -- -- -- --BaO -- -- -- -- -- -- 49.4                    -- -- -- -- -- -- --ZnO -- -- -- -- -- -- -- 34.1                       -- -- -- -- -- --CdO -- -- -- 30.9           -- -- -- -- -- -- -- -- -- --PbO -- -- -- -- 43.8              -- -- -- -- -- -- -- -- --K.sub.2 O    -- -- -- -- -- -- -- -- 24.7                          14.3                             -- 0.9                                   -- --Na.sub.2 O    -- -- -- -- -- -- -- -- --  9.4                              2.7                                0.4                                   17.8                                      --Li.sub.2 O    -- -- -- -- -- -- -- -- --  4.6                             -- 1.3                                   --  9.4Eu.sub.2 O.sub.3    0.05   1.4      1.3         1.1            0.9               1.1                  0.9                     1.2                        1.2                           1.3                              1.3                                1.3                                    1.3                                       1.4__________________________________________________________________________ 
    
     Table V sets out several treatments in reducing atmospheres consisting of dry forming gas to which the glass articles of Table IV were subjected. In like manner to Table II above, Table V recites visual observations of photoluminescence of polished glass plates exposed to sources of ultraviolet radiations having a wavelength of 2537A and 3650A, respectively, and cathodoluminescence resulting from the bombardment of electrons having an energy of 11 kilovolts. The treatment in forming gas was carried out similarly to that described in Table II except that in no example was the gas passed through distilled water prior to introduction into the furnace. 
     A comparison of the visual observations with respect to Examples 7, 9, and 10 of Table III indicated that the luminescence produced utilizing a wet reducing atmosphere was slightly less efficient and, perhaps, the color less saturated than when a dry atmosphere was employed. In any event, no significant advantage was observed with the H 2  O-containing environment and the elimination of the water column simplifies the procedure and, hence, the use of a dry atmosphere is more desirable from a practical point of view. 
     
                       Table V______________________________________Ex.  HeatNo.  Treatment   2537A    3650A   11 kV Electrons______________________________________24   None        Weak     Weak blue                             Very weak blue            blue24   900° C.-16 hrs.            Weak     Weak blue                             Very weak blue            blueGlass exhibited a slightly hazy appearance25   None        Violet-  Blue-   Very weak pink            pink     white25   900° C.-16 hrs.            Blue     Blue    Very bright blue26   None        Pink     Blue-   Very weak pink                     white26   900° C.-16 hrs.            Blue     Blue    Very bright blue27   None        Bright   Deep    Very weak pink            orange-  orange-            red      red27   900° C.-16 hrs.            Flat blue                     Dull    Moderate blue                     orange-                     redGlass exhibited a yellow color28   None        Bright   Deep    Very weak pink            orange-  orange-            yellow   red28   850° C.-16 hrs.            Dead     Dead    Very weak blueGlass exhibited a black surface skin29   None        Orange   Yellow- Weak orange pink                     white29   850° C.-16 hrs.             --       --     Moderate blue-                             white30   None        Yellow-  Yellow- Very weak pink            orange   orange30   850° C.-16 hrs.             --       --     Weak pink white31   Glass became opalized upon cooling from melt32   Glass extremely viscous, did not pour33   None        Yellow-  Red     Weak pink orange            white33   850° C.-16 hrs.            Glass flowed and devitrified33   600° C.-5 hrs.            Glass softened and opalized34   None        Pink     Blue-   Very weak pink                     white34   900° C.-16 hrs.            Blue     Blue    Very bright blueforming gas35   None        pink     Blue-   Very weak pink                     white35   900° C.-16 hrs.            Blue     Blue    Very bright blueforming gas36   None        Salmon   Blue-   Weak orange            pink     white36   850° C.-16 hrs.             --       --     Moderate blueforming gas36   700° C.-5 hrs.             --       --     Bright-blueforming gas37   None        Violet   Light   Weak pink-            pink     blue    orange37   850° C.-16 hrs.             --       --     Very bright blueforming gas37   650° C.-5 hrs.             --       --     Bright blueforming gas______________________________________ 
    
     Tables IV and V help to illustrate the compositional parameters that must be observed to achieve the desired properties of the inventive glasses. For example, compositions 24, 29, 30, 31, and 33, falling somewhat outside the prescribed ranges of components, exhibited poor luminescence under both ultraviolet radiation and electron bombardment. Example 27 points up that CdO is not as an effective an addition as are the alkaline earth metal oxides and Example 28 demonstrates an adverse effect resulting from extensive additions of lead. The surface skin was thought to be caused by the reduction of the lead oxide to metallic lead. 
     In summary, glasses consisting solely of Eu 2  O 3 , Al 2  O 3 , and SiO 2  are difficult to melt and form, such that other components, i.e., network formers and/or network modifiers, are included in amounts of at least 3 mole percent. As is evident from Tables I and IV, a wide variety of ingredients can be added which will improve the melting and forming characteristics of the glass and impart greater glass stability. In general, divalent metal oxides, and particularly the alkaline earth metal oxides, comprise the preferred additions. 
     The strength and brilliance of the blue luminescence appear to be enhanced with greater amounts of europium in the glass composition. Therefore, the presence of at least about 0.1 mole percent is preferred. However, the visual appearance does not seem to vary appreciably at concentrations in excess of about 2 mole percent, so that figure is deemed to be a practical maximum.