Abstract:
This invention provides a film structure and a method of making it, as well as packages formed therefrom, wherein the sealing properties of a single-site catalyst, SSC or metallocene polymer surface sealing layer are substantially increased as compared with a monolayer film of such a polymer. This invention provides in one embodiment a sealant film having at least two layers comprising a surface sealing layer and an adjacent hot tack strength boosting layer, the surface sealing layer being selected from single-site catalyst (SSC) interpolymers of ethylene and one or more C 4 -C 8  α-olefins having a density in the range of about 0.87 to about 0.915 gm/cc and a melt index of from about 0.2 to about 10 dg/minute, and a CDBI of greater than 30%; and the adjacent hot tack strength boosting layer increases the hot tack strength of the sealing layer by an amount of at least 1.5 times the unboosted hot tack strength value of the sealing layer over a broad sealing temperature range, and the sealing layer is selected from single-site and non-single-site catalyst copolymers, homopolymers and terpolymers of ethylene and blends thereof; wherein the density difference for the sealing layer to the adjacent hot tack strength boosting layer is at least about 0.015 gm/cc.

Description:
RELATED APPLICATIONS  
       [0001]    This application is a continuation-in-part of U.S. application Ser. No. 08/994,401, filed Dec. 19, 1997, which application is pending and which claims the benefit of U.S. Provisional Patent Application No. 60/034,178, filed Dec. 26, 1996 and now expired. 
     
    
     
       FIELD OF THE INVENTION  
         [0002]    Sealing properties of films are key to their effective use in many packaging applications, such as for example fluid containing disposable pouches that may be manufactured on form and fill equipment employing either impulse or thermic sealing techniques; vacuum packages for irregular shaped products and for prepared meats, cheeses and the like; shrink wrapped poultry and skin packaging. While this invention is directed to all forms of packaging, it is of particular value in the area of liquid packaging, namely for the manufacture of liquid containing pouches.  
           [0003]    Packaging machinery is being designed to operate at faster speeds all the time. Such machinery requires lower sealing temperatures and improved hot tack strength in films to be used to make packaging with such machines.  
         BACKGROUND OF THE INVENTION  
         [0004]    Many efforts have been made to improve the sealing properties of films used in the packaging area, particularly with respect to films used to package flowable materials. While the advent of single-site catalyst polymers or metallocene polymers has provided films of improved hot tack strength, there remains an ongoing need to improve further the seals of such packages. This is especially true for fluid containing pouches, e.g. milk pouches.  
           [0005]    Hot tack strength is the ability of a film to seal under stress while still in a molten state. This property is one of the most critical in packaging applications where machines run at high speeds and sealing takes place between molten sealing components of a package, thereby placing the sealing components, and hence the seal under stress when the package is formed, filled and sealed.  
           [0006]    It should be noted that in the case of fluid containing pouches made on form, fill and seal equipment, there appears to be a correlation between seal leaker frequency and hot tack strength. This is supported by data gathered in the dairy industry.  
           [0007]    The development of single-site catalyst (SSC) or metallocene technology has brought about an improved class of polymers ranging from crystalline to elastomeric materials. These polymers have features such as improved impact strength and toughness, better melt characteristics, because of the control over molecular structure, and better clarity. Exxon and Dow have developed ethylene interpolymers made with SSC or metallocene catalysts and each has the benefit of a number of patents relating to these polymers. Exxon is said to use mono- and bis-cyclopentadienyl metallocenes, while Dow&#39;s focus is on titanium cyclopentadienyl metallocenes, which it calls “constrained geometry catalysts”.  
           [0008]    In practice, Exxon produces ethylene-butene and ethylene-hexene interpolymers, while Dow makes ethylene-octene interpolymers of the metallocene or SSC type. Dow claims that its metallocene or SSC polymers are different as they have a low level of long chain branching that improves processability in otherwise linear polymers.  
         BACKGROUND ART  
         [0009]    Examples of the polymers of Exxon which are representative of polymers that may be used to produce films for pouches are found in the following patents and applications, the disclosures of which are incorporated herein by reference: U.S. Pat. No. 5,382,630 issued Jan. 17, 1995 to Stehling et al and WO93/03093 published Feb. 18, 1993 to Meka et al.  
           [0010]    Examples of the polymers of Dow which are representative of polymers that may be used to produce films for pouches are found in the following patents, the disclosures of which are incorporated herein by reference: U.S. Pat. Nos. 5,508,051 issued Apr. 16, 1996 to Falla et al; 5,360,648 issued Nov. 1, 1994 to Falla et al; 5,278,272 issued Jan. 11, 1994 to Lai et al; and 5,272,236 issued Dec. 21, 1993 to Lai et al.  
           [0011]    In DUPONT CANADA INC.&#39;s PCT International Publication WO 95/10566 published Apr. 20, 1995, the disclosure of which is incorporated herein by reference, there are disclosed pouches for flowable materials wherein the sealant film is made from a SSC copolymer of ethylene and at least one C 4 -C 10  α-olefin. Blends of these SSC copolymers with at least one polymer selected from multi site catalyst linear copolymers of ethylene and at least one C 4 -C 10  α-olefin, a high pressure polyethylene and blends thereof.  
           [0012]    In DUPONT CANADA INC.&#39;s PCT International Publication WO 95/21743 published Aug. 17, 1995, the disclosure of which is incorporated herein by reference, there is disclosed an ethylene copolymer film of improved stiffness for use in the manufacture of fluid containing pouches. Typically, the structure comprises an interposed layer of polyethylene having a thickness in the range of 5 to 20 microns and a density of at least 0.93 gm/cc and a melt index of from about 1 to 10 dg/minute, and at least one outer layer being a SSC or metallocene polyethylene/α-olefin film which may have a density in the range of 0.88 to 0.93 gm/cc. The only requirements placed on the stiffening interposed layer are that it be of a particular thickness and density. These are greater in the stiffening layer than in the metallocene or SSC layer(s). This application indicates that the stiffening layer is included in order for the fluid containing pouch to stand up properly so that fluid may be poured from it when the pouch is placed in a supporting container.  
           [0013]    DUPONT CANADA INC.&#39;s U.S. Pat. Nos. 4,503,102(Mollison) and 4,521,437 (Storms), the disclosures of which are incorporated by reference disclose a polyethylene film for use in the manufacture in a form, fill and seal process of a disposable pouch for liquids such as milk. U.S. Pat. No. 4,503,102 discloses pouches made from a blend of a linear copolymer of ethylene and a C 4 -C 10  α-olefin and an ethylene-vinyl acetate polymer copolymerized from ethylene and vinyl acetate. The linear polyethylene copolymer has a density of from 0.916 to 0.930 g/cm 3  and a melt index of from 0.3 to 2.0 g/10 minutes. The ethylene-vinyl acetate polymer has a weight ratio of ethylene to vinyl acetate from 2.2:1 to 24:1 and a melt index of from 0.2 to 10 g/10 minutes. The blend disclosed in Mollison U.S. Pat. No. 4,503,102 has a weight ratio of linear low density polyethylene to ethylene-vinyl acetate polymer of from 1.2:1 to 24:1. U.S. Pat. No. 4,503,102 also discloses multi-layer films having as a sealant film the aforementioned blend.  
           [0014]    U.S. Pat. No. 4,521,437 (Storms) describes pouches made from a sealant film which is from 50 to 100 parts of a linear copolymer of ethylene and octene-1 having a density of from 0.916 to 0.930 g/cm 3  and a melt index of 0.3 to 2.0 g/10 minutes and from 0 to 50 parts by weight of at least one polymer selected from the group consisting of a linear copolymer of ethylene and a C 4 -C 10 -α-olefin having a density of from 0.916 to 0.930 g/cm 3  and a melt index of from 0.3 to 2.0 g/10 minutes, a high-pressure polyethylene having a density of from 0.916 to 0.924 g/cm 3  and a melt index of from 1 to 10 g/l 0 minutes and blends thereof. The sealant film disclosed in U.S. Pat. No. 4,521,437 is selected on the basis of providing (a) pouches with an M-test value substantially smaller, at the same film thickness, than that obtained for pouches made with film of a blend of 85 parts of a linear ethylene/butene-1 copolymer having a density of about 0.919 g/cm 3  and a melt index of about 0.75 g/10 minutes and 15 parts of a high pressure polyethylene having a density of about 0.918 g/cm 3  and a melt index of 8.5 g/10 minutes, or (b) an M(2)-test value of less than about 12%, for pouches having a volume of from greater than 1.3 to 5 liters, or (c) an M(1.3)-test value of less than about 5% for pouches having a volume of from 0.1 to 1.3 liters. The M, M(2) and M(1.3)-tests are defined pouch drop tests for U.S. Pat. No. 4,521,437. The pouches may also be made from composite films in which the sealant film forms at least the inner layer.  
           [0015]    In Falla et al WO 93/02859 published Feb. 18, 1993, the disclosure of which is incorporated herein by reference, there is described the use of a linear ethylene copolymer in the manufacture of films used to make fluid containing pouches. These copolymers are characterised as ultra low density linear polyethylene (“ULDPE”) sold commercially as ATTANE™ by Dow and described as a linear copolymer of ethylene with at least one α-olefin having from 3 to 10 carbon atoms, for example, the ULDPE may be selected from ethylene-1-propylene, ethylene-1-butene, ethylene-1-pentene, ethylene-4-methyl-1-pentene, ethylene-1-hexene, ethylene-1-heptene, ethylene-1-octene and ethylene-1-decene copolymers, preferably ethylene-1-octene copolymer.  
           [0016]    In Meka et al WO 93/03093 published Feb. 18, 1993, the disclosure of which is incorporated herein by reference, there are described metallocene polymers useful for making sealed articles, comprising ethylene interpolymers having a CDBI of at least 50% and a narrow molecular weight distribution or a polymer blend comprising a plurality of said ethylene interpolymers as blend components.  
         SUMMARY OF THE INVENTION  
         [0017]    This invention provides a film structure and a method of making it, as well as packages formed therefrom, wherein the sealing properties of a surface sealing layer are substantially increased as compared with a monolayer film of such a polymer. By “sealing properties” is meant a substantially increased hot tack strength which is observable in such structures and which therefore allows the production of films and packaging products of greatly increased performance characteristics.  
           [0018]    The film structure proposed herein has been found to possess a substantially increased hot tack strength as compared with a monolayer SSC film. This increase is very unexpected since it is at least 1.5 times the values measured for the monolayer film itself across the whole range of sealing jaw temperatures as well as for the peak values. This is of great significance given the importance of this property in sealing. It is also quite unexpected since it is not observable in non-metallocene or non-SSC polymer film structures. For example, SSC polymers took hot tack strength to levels around 600 to 800 gms/3 inches from the 400 gm/3 inches level, but we have measured strengths of about 1200 to 1800 gm/3 inches in the structures of this invention. Clearly there is a synergistic effect in the structure proposed herein.  
           [0019]    This invention provides in one aspect, a sealant film having at least two layers comprising a surface sealing layer and an adjacent hot tack strength boosting layer, the surface sealing layer being selected from single-site catalyst (SSC) interpolymers of ethylene and one or more C 4 -C 8  α-olefins having a density in the range of about 0.87 to about 0.915 gm/cc and a melt index of from about 0.2 to about 5 dg/minute, and a CDBI of greater than 85%; and the adjacent hot tack strength boosting layer increases the hot tack strength of the surface sealing layer by an amount of at least 1.5 times over the unboosted hot tack strength value of the surface sealing layer over a broad sealing temperature range of at least about 30° C., and the adjacent surface sealing layer is selected from single-site and non-single-site catalyst copolymers, homopolymers and terpolymers of ethylene and blends thereof; and wherein the density difference for the sealing layer to the adjacent hot tack strength boosting layer is at least about 0.015 gm/cc.  
           [0020]    Preferably the CDBI is greater than 50%, and most preferably greater than 85%.  
           [0021]    Lai et al. International Application WO 93/08221, published Apr. 29, 1993, there is a discussion of the term CDBI (Composition Distribution Branch Index). This discussion is reproduced hereinafter, and the disclosure of this publication is incorporated herein by reference.  
           [0022]    The SCBDI (Short Chain Branch Distribution Index) or CDBI (Composition Distribution Branch Index) is defined as the weight percent of the polymer molecules having a comonomer content within 50 percent of the median total molar comonomer content. The CDBI of a polymer is readily calculated from data obtained from techniques known in the art, such as, for example, temperature rising elution fractionation (abbreviated herein as “TREF) as described, for example, in Wild et al,  Journal of Polymer Science, Poly. Phys. Ed.,  Vol. 20, p. 441 (1982), or as described in U.S. Pat. No. 4,798,081. The SCBDI or CDBI for the both truly linear olefin polymers and the substantially linear olefin polymers of the present invention is greater than about 85 percent.  
           [0023]    A unique characteristic of the presently claimed polymers is a highly unexpected flow property where the I 10 /I 12  value is essentially independent of polydispersity index (i.e. M w /M n ). This is contrasted with conventional Ziegler polymerized heterogeneous polyethylene resins and with conventional single site catalyst polymerized homogeneous polyethylene resins having rheological properties such that as the polydispersity index increases, the I 10 /I 12  value also increases.  
           [0024]    The density of the ethylene or ethylene/alpha-olefin substantially linear olefin polymers in the present invention is measured in accordance with ASTM D-792.  
           [0025]    The molecular weight of the ethylene or ethylene/alpha-olefin substantially linear olefin polymers in the present invention is conveniently indicated using a melt index measurement according to ASTM D-1238, Condition 190° C./2.16 kg (formally known as “Condition (E)” and also known as 12). Melt index is inversely proportional to the molecular weight of the polymer. Thus, the higher the molecular weight, the lower the melt index, although the relationship is not linear.  
           [0026]    Another measurement useful in characterizing the molecular weight of the substantially linear olefin polymers is conveniently indicated using a melt index measurement according to ASTM D-1238, Condition 190° C./10 kg (formerly known as “Condition (N)” and also known as I 10 ). The ratio of these two melt index terms is the melt flow ratio and is designated as I 10 /I 2 .  
         Molecular Weight Distribution Determination  
         [0027]    The whole interpolymer product samples and the individual interpolymer samples are analyzed by gel permeation chromatography (GPC) on a Waters 150° C. high temperature chromatographic unit equipped with three mixed porosity columns (Polymer Laboratories 10 3 , 10 4 , 10 5 , and 10 6 ), operating at a system temperature of 140° C. The solvent is 1,2,4-trichlorobenzene, from which 0.3 percent by weight solutions of the samples are prepared for injection. The flow rate is 1.0 milliliters/minute and the injection size is 200 microliters.  
           [0028]    The molecular weight determination is deduced by using narrow molecular weight distribution polystyrene standards (from Polymer Laboratories) in conjunction with their elution volumes. The equivalent polyethylene molecular weights are determined by using appropriate Mark-Houwink coefficients for polyethylene and polystyrene (as described by Williams and Word in Journal of Polymer Science. Polymer Letters Vol. 6, (621) 1968) to derive the following equation: 
           Mpolyethylene=a*(Mpolystyrene)b. 
           [0029]    In this equation, a=0.4316 and b=1.0. Weight average molecular weight, Mw, is calculated in the usual manner according to the following formula: Mw=R wi*Mi, where wi and Mi are the weight fraction and molecular weight, respectively, of the ith fraction eluting from the GPC column.  
           [0030]    The molecular weight distribution (M w /M n ) for both the truly linear olefin polymers and the substantially linear olefin polymers of the invention is generally narrow.  
           [0031]    In another preferred form of the present invention, the sealant film has a CDBI which is greater than or equal to 85% and the MI 10 /M 12  is less than 6.0 and the M W /M N  is greater than MI 10 /M 12 −4.63 for the truly linear SSC interpolymer.  
           [0032]    In another preferred form of the present invention, the sealant film has a CDBI which is greater than or equal to 85% and the MI 10 /M 12  is greater than or equal to 6.0 and the M W /M N  is less than or equal to MI 10 /M 12 −4.63 for the substantially linear SSC interpolymers with long chain branching.  
           [0033]    The film may be the principal or a component in a multi-layer structure, on one or both surfaces thereof.  
           [0034]    The above films may be used to make pouches for containing flowable materials. The pouch is in tubular form and has transversely heat sealed ends.  
           [0035]    In yet another aspect, the invention provides a method of enhancing the sealing properties of a single-site catalyst (SSC) resin layer for use as a sealing layer in a packaging film structure wherein the SSC resin layer is adjacent another polymer layer of higher density, and the density difference between the layers is from at least about 0.15 gm/cc. The film structures described above provide the result of this method.  
           [0036]    Finally the invention provides a process for making pouches filled with a flowable material, using a vertical form, fill and seal apparatus, in which process each pouch is made from a flat web of film by forming a tubular film therefrom with a longitudinal seal and subsequently flattening the tubular film at a first position and transversely heat sealing said tubular film at the flattened position, filling the tubular film with a predetermined quantity of flowable material above said first position, flattening the tubular film above the predetermined quantity of flowable material at a second position and transversely heat sealing said tubular film at the second position, the improvement comprising making the pouches from a flat web of film comprising a film as described above.  
           [0037]    As indicated blends of polymers may be used for the boosting layer because of processability and/or economic requirements. Typically a high pressure polyethylene up to about 25% by weight is added as a processing aid. Above 25% the film properties of the blend start to differ from the main polymer on its own. Other linear low density polyethylene polymers, LLDPE can be blended usually for economic reasons. The blends which may be used herein are any of those which are known in the art and which have been described in any and all of the aforementioned patents and applications.  
           [0038]    The density of the boosting layer preferably ranges from 0.900 to about 0.960, unless the layer is made from ethylene vinyl alcohol copolymer in which case the range would be from about 1.10 to about 1.20 gm/cc, more preferably from about 1.17 gm/cc to about 1.19 gm/cc.  
           [0039]    The single-site catalyst interpolymer may preferably be selected from interpolymers comprising ethylene and at least one C 4 -C 8  α-olefin, in particular butene, hexene, octene, n-methyl-pentane and combinations thereof. Commercially available polymers include the following: EXACT™ and EXCEED™ sold by Exxon and AFFINITY™ and ELITE sold by Dow.  
           [0040]    The more preferred density ranges for the SSC interpolymer may be from about 0.88 to about 0.92 gm/cc.  
           [0041]    The boosting layer may be selected, as stated previously from single-site catalyst and non-single-site catalyst homopolymers, copolymers and terpolymers of ethylene. Especially preferred are interpolymers of ethylene and one or more C 3 -C 20  α-olefins, most preferably C 4 -C 10 , most preferably C 4 -C 6 , in particular, butene, hexene, octene and n-methyl-pentane. Non-single-site catalyst polymers are a preferred group.  
           [0042]    Examples of commercially available linear low density polyethylene materials include SCLAIR™ from Novacor and DOWLEX™ from Dow. An example of ultra low density polyethylene material is ATTANE™ from Dow.  
           [0043]    However, a wide range of ethylene polymers may be used as the boosting layer, with the only criteria being that the layer enhances the hot tack strength of the SSC polymer layer and it meets the intended application requirements. Polymers that fall within this family include both single-site catalyst and non-single-site catalyst ethylene polymers and interpolymers, the latter including, for example, Zeigler-Natta catalyst polymers.  
           [0044]    Other examples of these polymers include polyethylene homopolymers made by high pressure processes. Commercial examples include ALATHON™ available from E.I. du Pont de Nemours and ethylene vinyl acetate polymers, examples of which are commercially available from E.I. du Pont de Nemours under the trade-mark ELVAX™.  
           [0045]    In another embodiment, the boosting layer may be ethylene—acid copolymers such as SURLYN™ and NUCREL™ available from E.I. du Pont de Nemours or ethylene vinyl alcohol copolymers such as EVAL™ from Kuraray or SOARNOL™ from Nippon Gohsei. These polymers may not bond directly with polyethylene and may be secured by co-extrudable adhesives such as BYNEL™ (available from E.I. du Pont de Nemours). In such instance the co-extrudable adhesives may act as the boosting layer.  
           [0046]    It is possible to use the film of this invention as a sealant film or as a component in a more complex multi-layer structure. Typical structures are those known in the art and which will suit the packaging application and still allow the benefits of the enhanced sealing properties of the metallocene or SSC layer to be taken advantage of in the structure.  
           [0047]    The previously referenced patents and applications describe the various processes that may be used to manufacture the pouches of this invention. Vertical form, fill and seal apparatus is used to make the pouches envisaged herein. A flat web of film is unwound from a roll and formed into a continuous tube in a tube forming section by sealing the longitudinal edges together by either a lap seal or a fin seal. This tube is pulled vertically towards a filling station and is then collapsed across a transverse cross section of the tube, the position of which section coincides with a sealing device below a filling station. A transverse heat seal is made at the section providing an air and liquid tight seal across the tube.  
           [0048]    The material to be packaged enters the tube above the transverse seal, the tube drops a predetermined distance under the influence of gravity on its load. The sealing device is operated again, and a second transverse seal is made together with a cut through the tube and often through the material placed in the pouch. Thus in this operation, the pouch which has an elongate pillow shape is formed, filled and sealed in a rapid sequence of steps. Many variations of this process are possible and are apparent to those skilled in the art. Examples of typical liquid packaging apparatus used for this type of manufacture are made by Hayssen, Thimonnier and Prepac.  
           [0049]    The term “flowable materials” as used herein encompasses materials which flow under gravity or which may be pumped. Gaseous materials are not included in this definition. The flowable materials include liquids, for example, milk, water, fruit juice, oil; emulsions, for example, ice cream mix, soft margarine, pastes, for example, meat pastes, peanut butter; preservers, for example, jams, pie fillings, marmalade; jellies; doughs; ground meat, for example, sausage meat; powers, for example, gelatine powders, detergents; granular solids, for example, nuts, sugar; and like materials. The pouch of the present invention is particularly useful for liquid foods, for example, milk.  
           [0050]    The resins used to make the film of this invention are preferably coextruded in known ways, although other suitable methods may be used, such as those involving laminates, coatings and the like. All forms of conventional laminating and coating methods may be used to manufacture the present films, including extrusion coating, roll coating, 100% solids lamination, water and solvent based adhesive laminations and the like. When blends are used, these may be made by blending the components prior to or at the time of extrusion just prior to remelting in the extruder. A film extruder may be used and the film made using known techniques. An example of a blown film process is found in Canadian Patent No. 460,963 issued Nov. 8, 1949 to Fuller. Canadian Patent No. 893,216 issued Feb. 15, 1972 to Bunga et al describes a preferred method using an external or internal cooling mandrel in the blown film process.  
           [0051]    Additives, known to those skilled in the art, such as anti-block agents, slip additives, UV stabilisers, pigments and processing aids including high pressure polyethylene may be added to the polymers from which the pouches of the present invention are made. Typically these may comprise up to 50% by weight of total resin components, although as previously indicated, when the additional additives and other components reach this proportion, it is important to be sensitive to the desired hot tack strength enhancement for the structure.  
           [0052]    As stated previously, the film of this invention may be used in packaging applications where sealing properties, particularly hot tack strength is important. Reference may be had to The Wiley Encyclopaedia of Packaging Technology, 1986, John Wiley &amp; Sons, Inc., under the heading Heat Sealing, the disclosures of which are incorporated herein by reference. Descriptions are found herein for all types of heat sealing including bar, band, impulse, wire or knife, ultrasonic, friction, gas, contact, hot melt, pneumatic, dielectric, magnetic, induction, radiant and solvent sealing. Any of these techniques that lend themselves to packaging materials incorporating the film of this invention fall within the scope of this disclosure. Most preferred are packages made by impulse sealing. 
       
    
    
     BRIEF DESCRIPTION OF THE DRAWINGS  
       [0053]    In the accompanying drawings which are used for purposes of illustrating this invention,  
         [0054]    FIGS.  1  to  9  are graphical plots of the effects of a higher density polyethylene layer adjacent a metallocene layer on hot tack strength.  
         [0055]    [0055]FIG. 10 is a graphical plot of hot tack strength curves for two films described in Example 4. 
     
    
     Method for Determining Hot Tack Strength  
       [0056]    The method described herein is one of many that may be used to measure this property. The values set out subsequently in the examples will be generally equivalent to those obtained using other conventional methods. It should be noted that the measurements performed and described in Examples 10 and onwards are conducted according to the presently described method, but the apparatus used was more modern than the machine used in the earlier examples. The new machine is a J &amp; B Hot Tack tester which runs faster than the old machine and therefore allows for sharp and fast testing. The volume of samples is substantially increased and hence the results are more objective.  
       Principle  
       [0057]    A film seal is stressed immediately after the sealing operation has been completed to give an indication of the hot strength of the seal. This method may be used for all polyolefin films and laminates. Many automatic filling operations place a stress on the seal area immediately after the filling operation has been completed. Films having superior hot tack strength are desirable in this application.  
       Test Method  
       [0058]    1. Place the prepared film samples over the rollers and between the jaws of the hot tack gun. Activate the switch on the gun to clamp the film sample securely in the jaws of the gun apparatus.  
         [0059]    2. Place a weight on the stress ring of the apparatus. A typical starting weight is 200 g.  
         [0060]    3. Set the Sentinel™ heat sealer jaw pressure at 20 psi and the dwell time at 1 second. Set the temperature to control at 125° C. (lower for thin films, higher for thick films). The temperature is increased in 5° C. increments as the ultimate seal range is found.  
         [0061]    4. Using the foot switch, open and close the jaws of the “Sentinel” heat sealer four times to equalize the temperature of the jaws.  
         [0062]    5. Place the gun apparatus so that the taped film or equivalent area of a laminated strip, extends between the sealer jaws.  
         [0063]    6. Close the jaws of the Sentinel™ heat sealer by depressing the foot switch.  
         [0064]    7. Release the jaws of the hot tack gun (by activating the switch on the gun) when the elapsed time indicator reaches 0.5 sec.  
         [0065]    8. Remove the sample from the gun apparatus and judge the seal integrity. One millimeter of separation is considered acceptable.  
         [0066]    9. If the seal is good, use a new sample and repeat the above procedure with increased weight on the stress ring.  
         [0067]    More samples can be prepared while waiting for the heater to settle at the new setting.  
       Apparatus  
       [0068]    1. DuPont hot tack gun with weights in 100 gram divisions.  
         [0069]    2. Sentinal™ heat sealer with pressure gauge and temperature controller. A 1 inch (2.54 cm) Teflon™ coated bar is mounted on the upper jaw. The bottom jaw is stationary with a strip of heatproof fabric 1½″ (3.81 cm) wide placed over a rubber paid, ½″ (1.27 cm) thick by 1″ (2.54 cm) wide. A bracket is attached below the bottom jaw to support and align the gun and sample during testing. Only the upper jaw is heated.  
         [0070]    3. 3.0″×9.25″ template.  
         [0071]    4. 3.5″×9.0″ template.  
         [0072]    5. Scotch™ #352 polyester packaging tape.  
         [0073]    6. Hand held roller with hard rubber roll.  
       Procedure  
       [0074]    A. Unsupported Polyolefin Film  
         [0075]    1. Use the 3.5″×9.0″ template to cut samples with the long side parallel to the MD of the film. The film samples should be allowed to condition for 24 hours before running hot tack tests.  
         [0076]    2. Place the #352 tape across both ends of the sample, allowing the tape to overlap the film edge by about ⅛″.  
         [0077]    3. Roll the tape with the roller to ensure an even contact between the tape and the film, eliminating air bubbles.  
         [0078]    4. Using the 1.8″ tape overlaps, tape the sample in a loop.  
         [0079]    5. Using the 3.0″ and 9.25″ template, trim the excess tape and film off the edges to obtain a loop of film 3.0″×9.0″ with a taped safety seal.  
         [0080]    B. Laminates  
         [0081]    The purpose of the polyester tape is to support the polyolefin film and prevent it from sticking to the jaws. Therefore, a lamination with an outer layer of nylon, polyester, cellulose film etc., will not need to be taped, so the following procedure may be used.  
         [0082]    1. Use the 3.0″×9.25″ template to cut samples with the long side parallel to the MD of the film. The film samples should be allowed to condition for 24 hours before running hot tack tests.  
         [0083]    2. Form the sample strip into a loop and make a 1.8″ safety heat seal at the end.  
         [0084]    Allow seal to cool.  
       Calculations  
       [0085]    Plot the seal rating against temperature. A curve is usually drawn through the seal points to indicate seal integrity for any given temperature.  
         [0086]    It should be noted that density measurements are made in accordance with methods known in the art as set out in ASTM Procedure D1505. The melt index may be determined in accordance with known methods and in particular by ASTM Procedure D1238-94a. The melting point may be determined using Differential Scanning Colorimetry (DSC). An initial melting profile of the polymer is obtained. Heat flow in MW is measured as a function of temperature at which the minimum value of heat flow occurs.  
       DETAILED DESCRIPTION OF THE INVENTION  
     Example 1  
       [0087]    The hot tack strength of two monolayer films was compared to the hot tack strength of a coextruded film made with the same two polymers and the results were plotted in FIG. 1 and were made on a blown film process with an internal cooling mandrel at a blow-up ratio of 1.4:1. The thickness of each of the layers in the 76 μm thick coextruded film was approximately 25/25/25 μm. The hot tack strength of the coextrusion exhibited at least 2 times the hot tack strength of the monolayer films at each temperature tested. A 76 μm thick monolayer film made from single-site catalyst ethylene/octene copolymer with a density of 0.902 g/cc and melt index of 1.0 g/10 min. @190° C./2.16 kg (Dow Affinity™ PL1880) exhibited a hot tack that peaked at 700 g/3 in. at 120 and 125° C. (curve #2). A 19 μm thick monolayer film made from multi site catalyst high density linear polyethylene with a density of 0.957 g/cc and melt index of 1.0 (Sclair™ 19C) exhibited a hot tack of only 300 g/3 in. at 155° C. (curve #3). A coextrusion of the two polymers in which the core layer was 0.957 g/cc density high density polyethylene and the outer layers were 0.902 g/cc density metallocene plastomer exhibited a hot tack with peak values from 1100 to 1500 g/3 in. (curve #1). Another way of expressing this is that addition of a core layer of high density polyethylene, to the metallocene plastomer increased its hot tack strength roughly twofold over its entire hot tack temperature range compared to the same monolayer plastomer film. This was completely unexpected.  
       Example 2  
       [0088]    Hot tack strength of three coextrusions made with Affinity™ PL1880 outer layers and core layers of medium to high density polyethylene were compared and results are found in FIG. 2. The densities of the core layers were 0.935 (curve #1), 0.945 (curve #2) and 0.957 g/cc (curve #3), respectively. The hot tack strength of the monolayer Affinity™ PL1880 was shown for comparison (curve #4). The films were all 76 μm thick and were made on a blown film process with an internal cooling mandrel at a blow-up ratio of 1.4:1. The thickness of each of the layers in the coextruded films were approximately 25/25/25 μm, respectively. As can be seen, the hot tack strength of the Affinity™ PL1880 has been at least doubled by the addition of a higher density core layer. The three coextrusions were similar in hot tack performance. The core layers in the coextruded films were made from the following resins:  
         [0089]    Sclair™ 14K—multi site catalyst ethylene/octene copolymer with a density of 0.935 9/cc and melt index of 5.0;  
         [0090]    Sclair™ 16A—multi site catalyst ethylene/butene copolymer with a density of 0.945 g/cc and melt index of 0.28; and  
         [0091]    Sclair™ 19C—multi site catalyst high density linear polyethylene with a density of 0.957 g/cc and melt index of 1.0  
       Example 3  
       [0092]    The hot tack strength of three coextrusions (nominally 76 μm thick) made with outer layers of Exact™ 3132 0.901 g/cc density metallocene plastomer, each with a core layer of polyethylene with a different density: 0.919 g/cc in curve #1, 0.945 g/cc in curve #2 and 0.957 g/cc in curve #3, respectively was tested and plotted in FIG. 3. The hot tack strength of 76 μm thick monolayer Exact™ 3132 film was shown for comparison (curve #4). The films were made using a conventional blown film process. The coextrusions were made at a blow-up ratio of 2.2:1, whereas the monofilm was made at a blow-up ratio of 2.8:1. The thickness of each of the layers in the coextruded films was approximately 15/46/15 mm, respectively. The 0.919 g/cc density core layer was composed of a blend of 85% by weight of Sclair™ 11L4B LLDPE resin and 15% by weight of Nova LF0521A™ (low density ethylene homopolymer). The 0.945 and 0.957 g/cc density core layers were composed of 100% Sclair™ 16A and 19C respectively. Hot tack values for the center parts of the curves represent the limit of the test method rather than the value for the film a that particular temperature. Nevertheless, it can be seen that the coextrusions of the invention significantly outperform the monofilm in both the lower temperature and upper temperature portions of the hot tack curves. The hot tack strength of the coextruded films exceeds a given value over a broader range of temperatures than does the monofilm. It is apparent that inclusion of a higher density core from about 0.920 to about 0.960 g/cc in the metallocene plastomer films gives an unexpected doubling of hot tack strength.  
         [0093]    Exact™ 3132—single-site catalyst ethylene/hexene copolymer with a density of 0.901 g/cc and a melt index of 1.2 Sclair™ 11L4B—multi site catalyst ethylene/octene copolymer with a density of 0.919 g/cc and a melt index of 0.75 Nova LF0521A™—ethylene homopolymer made by the high pressure process with a density of 0.921 g/cc and a melt index of 5.0 Sclair™ 16A—multi site catalyst ethylene/butene copolymer with a density of 0.945 g/cc and melt index of 0.28 Sclair™ 19C—multi site catalyst high density linear polyethylene with a density of 0.957 g/cc and melt index of 1.0.  
       Example 4  
       [0094]    The hot tack strength of two blown film coextrusions, one 76 μm thick (curve #2) and the other 51 μm thick (curve #3), made with outer layers of Affinity™ PL1880 copolymer resin and a core layer of Sclair™ D332-05 medium density resin are compared with the hot tack strength of 76 μm Affinity™ PL1880 monofilm (curve #1) in FIG. 4. It can be seen that the unexpected improvement in hot tack is not limited to films which are 76 μm thick. The 51 μm coextruded film of the invention has higher hot tack strength than the 76 μm monofilm except at the highest portion of the sealing temperature range. The thickness of each of the layers in the coextruded films were approximately 13/50/13 μm, respectively for the 76 μm film and 8.5134/8.5 μm, respectively for the 51 μm film.  
         [0095]    Affinity™ PL1880—single-site ethylene/octene copolymer with a density of 0.902 g/cc and a melt index of 1.0. Sclair™ D332-05—multi site ethylene/octene copolymer with a density of 0.930 g/cc and a melt index of 1.0.  
       Example 5  
       [0096]    The hot tack strength of a 2 layer blown film coextrusion is measured on both sides of the 76 μm film as shown in FIG. 5. One side of the film was Exact™ 3132 metallocene plastomer. The other side was Sclair™ 11L4B linear low density ethylene-octene copolymer resin. The hot tack strength of the film, measured on the metallocene polymer side (curve #1), is surprisingly high over a very broad temperature range whereas the hot tack strength curve #2 measured on the linear low polyethylene side is neither high nor broad. The layer thickness in the coextruded film were approximately:  
         [0097]    15 μm of Exact™ 3132 and 61 μm of SCLAIR™ 11L4B;  
         [0098]    Exact™ 3132—single-site catalyst ethylene/hexene copolymer with a density of 0.901 g/cc and a melt index of 1.2; and  
         [0099]    Sclair™ 11L4B—multi site catalyst ethylene/octene copolymer with a density of 0.919 g/cc and a melt index of 0.75.  
       Example 6  
       [0100]    The hot tack strength of two blown film coextrusions made with Attane™ 4201 0.912 g/cc outer layers and core layers of Dowlex™ XSS84652.38 low (curve #1) and Sclair™ D332-05 medium density polyethylene (curve #2) were compared with monolayer Attane™ 4201 film (curve #3) in FIG. 6. The films were all 76 μm thick. Attane™ 4201 is a linear very low density ethylene-octene copolymer resin made with a conventional rather than a metallocene catalyst. The coextruded films are not ones of the invention and no surprising increases hot tack strength are observed. The coextrusions had layer thickness of approximately 19/38/19 μm.  
         [0101]    Attane™ 4201—multi site catalyst ethylene/octene copolymer with a density of 0.912 g/cc and a melt index of 1.0.  
         [0102]    Dowlex™ XSS84652.38—multi site catalyst ethylene/octene copolymer with a density of 0.920 g/cc and a melt index of 0.85.  
         [0103]    Sclair™ D332-05—multi site catalyst ethylene/octene copolymer with a density of 0.930 g/cc and a melt index of 1.0.  
       Example 7  
       [0104]    The hot tack strength of an 100 μm thick blown film coextrusion with Affinity™ PL1880 outer layers and a core layer of Soarnol™ ET 3803 EVOH was compared with the hot tack strength of a 76 μm Affinity™ PL1880 monofilm. As can be seen in FIG. 7, the inherent hot tack strength of the Affinity™ PL1880 (curve #1) has been at least doubled by the addition of the higher density core layer (curve #2). In the EVOH coextrusion, layers of Bynel™ 4109 coextrudable adhesive resin were included on either side of the EVOH layer to bond it properly to the Affinity™ plastomer outer layers. The thickness of each of the layers in the coextruded film were 41/4/10/5/41 μm, respectively. The hot tack boosting layer can be thought of as including both the Bynel™ 4109 layers and the Soarnol™ ET 3803 core layer.  
         [0105]    Affinity™ PL1880—single-site ethylene/octene copolymer with a density of 0.902 g/cc and a melt index of 1.0.  
         [0106]    Soarnol™ ET 3803—ethylene/vinyl alcohol copolymer with an ethylene content of 38 mole per cent, a density of 1.17 g/cc and a melt index of 3.3 g/10 minutes measured at 210° C./2.16 kg.  
         [0107]    Bynel™ 4109—anhydride &amp; rubber modified linear low density polyethylene adhesive polymer with a density of 0.928 g/cc and a melt index of 3.2.  
       Example 8  
       [0108]    The hot tack strength of two 76 μm thick blown film coextrusions with different density metallocene plastomer outer layers was compared with the hot tack strength of a 76 μm Affinity™ PL1880 monofilm. In curve #2 of FIG. 8, the metallocene plastomer resin used to form the outer layers was Affinity™ PL1880 (0.902 g/cc density), whereas the outer layers were made from Affinity™ PL1840 (0.908 g/cc density) in curve #3. The coextrusions had layers of thickness of approximately 13/50/13 μm, respectively. The film made with Affinity™ PL1880 outer layers had a core layer made from Sclair™ D332-05 medium density polyethylene. The film made with Affinity™ PL1840 outer layers had a core layer made from Sclair™ E431-06 medium density polyethylene. As can be seen, the hot tack strength curves for the coextruded films are both much broader and higher than the curve for the monofilm (curve #1).  
         [0109]    Affinity™ PL1880—single-site catalyst ethylene/octene copolymer with a density of 0.902 g/cc and a melt index of 1.0.  
         [0110]    Affinity™ PL1840—single-site catalyst ethylene/octene copolymer with a density of 0.908 g/cc and a melt index of 1.0.  
         [0111]    Sclair™ D332-05—multi site catalyst ethylene/octene copolymer with a density of 0.930 g/cc and a melt index of 1.0.  
         [0112]    Sclair™ E431-06—multi site catalyst ethylene/octene copolymer with a density of 0.935 g/cc and a melt index of 1.0.  
       Example 9  
       [0113]    The hot tack boosting effect depends on the density difference between the single-site catalyst polymer sealant layer and the backing layer. FIG. 9 compares the hot tack strength of three blown film coextrusions with that of Affinity™ PL1880 monofilm (curve #1). The coextrusions all have outer layers made from Affinity™ PL1880 resin which has a density of 0.902 g/cc. The core layer in curve #2 has a density of 0.930 g/cc whereas the core layer densities for curves #3 and #4 are 0.912 and 0.908 g/cc respectively. All films were 76 μm thick. The coextrusions had layers of thickness of approximately 13/50/13 μm, respectively. The hot tack boost provided by the medium density core layer was the most dramatic, but a performance improvement is still evident even when the density difference between outer and core layer is as small as 0.006 g/cc.  
         [0114]    Affinity™ PL1880—single-site catalyst ethylene/octene copolymer with a density of 0.902 g/cc and a melt index of 1.0.  
         [0115]    Sclair™ D332-05—multi site catalyst ethylene/octene copolymer with a density of 0.930 g/cc and a melt index of 1.0.  
         [0116]    Attane™ 4201—multi site catalyst ethylene/octene copolymer with a density of 0.912 g/cc and a melt index of 1.0.  
         [0117]    Affinity™ PL1840—single-site catalyst ethylene/octene copolymer with a density of 0.908 g/cc and a melt index of 1.0.  
       Quantifying Hot Tack Boost  
       [0118]    Hot Tack Boost is defined as an increase in Hot Tack Strength, as measured by the method described in the patent application, of at least an average of 470 grams per 3 inches over a temperature range of 30° C. which includes temperatures below, at and above the temperature where the peak Hot Tack Strength of the single-site catalyst interpolymer occurs.  
       Example 10  
       [0119]    Film #1, which shows Hot Tack Boost, is the film of Curve #3 in Example 2.  
       Example 11  
       [0120]    SSC Film #4 is a monofilm made from AFFINITY™ PL1880—Single site catalyst ethylene/octene copolymer which has a density of 0.902 g/cc and a melt index of 1. Film #1 has Affinity PLI 880 sealant layers and a core layer which is SCLAIR™ 14K having a density of 0.935 g/cc and a melt index of 5. Thus the density difference between the two layers is 0.033 g/cc.  
                                                               Hot Tack   Hot Tack               Temperature   Strength   Strength of   Hot Tack           of Sealing Jaws   of SSC Film #4   Film #1   Boost           (° C.)   (g/3 in.)   (g/3 in.)   (g/3 in.)                           105    0     0    0           110    0     0    0           115   500   1200   700           120 ←T max     700   1400   700           125 ←T max     700   1300   600           130   600   1300   700           135   500   1000   500           140   400    900   500           145   300    900   600           150   400    900   500                                                          
 
       Example 12  
       [0121]    Film #2 has the core layer which is SCLAIR™ 16A has a density of 0.945 g/cc and a melt index of 0.28. SSC Film #4 is a monofilm made from Affinity™ PL1880—single-site catalyst ethylene/octene copolymer which has a density of 0.902 g/cc and a melt index of 1. Thus the density difference is 0.043  
                                                               Hot Tack   Hot Tack               Temperature   Strength of   Strength of   Hot Tack           of sealing jaws   SSC Film #4   Film #2   Boost           (° C.)   (g/3 in.)   (g/3 in.)   (g/3 in.)                           105    0    300   300           110    0    800   800           115   500   1000   500           120 ←T max     700   1500   800           125 ←T max     700   1500   800           130   600   1500   900           135   500   1000   500           140   400    900   500           145   300    700   400           150   400   —   —                                                          
 
       Example 13  
       [0122]    Film #3 has a core layer which is SCLAIR™ 19C having a density of 0.957 g/cc and a melt index of 1.  
         [0123]    Film #4 is a monofilm made from AFFINITY™ PL1880—single-site catalyst ethylene/octene copolymer which has a density of 0.902 g/cc and a melt index of 1. Thus the density difference between the two layers is 0.055 g/cc.  
                                                                                     Hot Tack   Hot Tack               Temperature of   Strength of   Strength of   Hot Tack           sealing jaws   SSC Film #4   Film #3   Boost           (° C.)   (g/3 in.)   (g/3 in.)   (g/3 in.)                                        105   0   100   100           110   0   500   500           115   500   1100   600           120 ←T max     700   1300   600           125 ←T max     700   1300   600           130   600   1500   900           135   500   1400   900           140   400   1100   700           145   300   900   600           150   400   —   —                                                          
 
       Example 14  
       [0124]    SSC Film #4a is a monofilm of Exact™ 3132—single-site catalyst ethylene/hexene copolymer has a density of 0.901 g/cc and a melt index of 1. Film #1 has Exact™ 3132 sealant layers and a core layer which is Sclair™ 11L4B has a density of 0.919 g/cc and a melt index of 0.75. Thus the density difference between the two layers is 0.018 g/cc.  
                                                               Hot Tack   Hot Tack               Temperature   Strength   Strength of   Hot Tack           of Sealing Jaws   of SSC Film #4a   Film #1   Boost           (° C.)   (g/3 in.)   (g/3 in.)   (g/3 in.)                           100    0    300   300           105    700   1500   800           110   1000   1800   800           115 ←T max     1600   1800   at least 200           120 ←T max     1600   1800   at least 200           125 ←T max     1600   1800   at least 200           130   1100   1800   700           135   1100   1700   600           140    900   1600   700           145    500   1500   1000            150   —   1200   —                                                          
 
       Example 15  
       [0125]    Film #2 has the core layer which is SCLAIR 16A which has a density of 0.945 g/cc and a melt index of 0.28.  
         [0126]    SSC Film #4a is Exact 3132 monofilm with a density of 0.901 g/cc and a melt index of 1. Thus the density difference between the two layers is 0.044 g/cc.  
                                                               Hot Tack   Hot Tack               Temperature   Strength   Strength of   Hot Tack           of Sealing Jaws   of SSC Film #4a   Film #2   Boost           (° C.)   (g/3 in.)   (g/3 in.)   (g/3 in.)                           100     0    700   700           105    700   1500   800           110   1000   1800   800           115 ←T max     1600   1800   at least 200           120 ←T max     1600   1800   at least 200           125 ←T max     1600   1800   at least 200           130   1100   1800   700                      
 
         [0127]    [0127]                                                               Hot Tack   Hot Tack               Temperature   Strength of   Strength of   Hot Tack           of Sealing Jaws   SSC Film #4a   Film #2   Boost           (° C.)   (g/3 in.)   (g/3 in.)   (g/3 in.)                           135   1100    1500   400           140   900   1500   600           145   500   1300   800           150   —   —   —                                                            
       Example 16  
       [0128]    Film #3 has the core layer which is SCLAIR 19C has a density of 0.957 g/cc and a melt index of 5.  
         [0129]    SSC Film #4a is Exact 3132 monofilm with a density of 0.901 g/cc and a melt index of 1. Thus the density difference between the two layers is 0.056 g/cc.  
                                                               Hot Tack   Hot Tack               Temperature   Strength   Strength of   Hot Tack           of Sealing Jaws   of SSC Film #4a   Film #3   Boost           (° C.)   (g/3 in.)   (g/3 in.)   (g/3 in.)                           100     0    300   300           105    700   1500   800           110   1000   1800   800           115 ←T max     1600   1800   at least 200           120 ←T max     1600   1800   at least 200           125 ←T max     1600   1800   at least 200           130   1100   1800   700           135   1100   1800   700           140    900   1500   600           145    500   1100   600           150   —   —   —                                                          
 
         [0130]    It can be seen on the graph for example #4 that the Hot Tack Values in the region of the Hot Tack Strength maximum are truncated. This is because the test operator cannot use a weight heavier than 1800 grams with the Hot Tack Gun Method (a version of ASTM D3706).  
         [0131]    In FIG. 10, Hot Tack Strength curves for two of the films in example 4 have been generated using the more rapid J&amp;B Hot Tack tester. The data verifies that significant Hot Tack Boost is indeed occurring in the region of maximum value.  
       Example 17  
       [0132]    Film #1 (0.919 density core) versus SSC Film #4 (as in example 14)  
                                                               Hot Tack   Hot Tack               Temperature   Strength   Strength of   Hot Tack           of Sealing Jaws   of SSC Film #4   Film #1   Boost           (° C.)   (Newtons)   (Newtons)   (Newtons)                            90   1.009   0.719   —            95   2.323   3.554   1.231           100   3.634   6.652   3.018           105   5.313   8.915   3.602           110   5.811   9.992   4.181           115   6.18    9.946   3.766           120   6.318   9.445   3.127           125 ←T max     6.5    9.813   3.313           130   6.353   9.631   3.278           135   6.055   8.791   2.736                                                          
 
       Example 18  
       [0133]    Film #2 (0.957 core) versus SSC Film #1 (as in example 15)  
                                                               Hot Tack   Hot Tack               Temperature   Strength   Strength of   Hot Tack           of Sealing Jaws   of SSC Film #1   Film #2   Boost           (° C.)   (g/3 in.)   (g/3 in.)   (g/3 in.)                           100    0     0     0           105    0    100    100           110    0    500    500           115    0   1600   1600           120   100   1600   1500           125   200   1500   1300           130   500   1500   1000           135   700   1300    600           140 ←T max     800   1000    200           145   600    900    300           150   400    700    300                                                          
 
       Example 19  
       [0134]    This data shows that there is no Hot Tack Boost unless the sealant layer is an SSC interpolymer.  
         [0135]    Film #1 (0.920 core) versus non-SSC Film #3 (films are as in example 6)  
                                                               Hot Tack   Hot Tack               Temperature   Strength of   Strength of   Hot Tack           of Sealing Jaws   non-SSC Film #3   Film #1   Boost           (° C.)   (g/3 in.)   (g/3 in.)   (g/3 in.)                           120    0    0    0           125    0    0    0           130    0   100   100           135   100   100    0           140   100   300   200           145 ←T max     400   300   −100            150   300   200   −100            155   300   300    0           160   300   300    0                                                                      
 
         [0136]    [0136]                                                               Hot Tack   Hot Tack               Temperature   Strength of   Strength of   Hot Tack           of Sealing Jaws   non-SSC Film #3   Film #2   Boost           (° C.)   (g/3 in.)   (g/3 in.)   (g/3 in.)                           120    0    0    0           125    0   100   100           130    0   100   100           135   100   100    0           140   100   500   400           145 ←T max     400   400    0           150   300   300    0           155   300   300    0           160   300   200   −100                                                             
       Example 20  
       [0137]    Film #2 (EVOH core) versus non-SSC Film #1 (Films from example 7)  
                                                                                     Hot Tack   Hot Tack               Temperature of   Strength of   Strength of   Hot Tack           Sealing Jaws   SSC Film #1   Film #2   Boost           (° C.)   (g/3 in.)   (g/3 in.)   (g/3 in.)                                        115   0   0   0           120   100   700   600           125   200   1400   1200           130   500   1500   1000           135   700   1200   500           140 ←T max     800   1000   200           145   600   800   200           150   400   600   200           155   300   500   200           160   200   200   0                                                          
 
       Example 21  
       [0138]    The Film #2 versus SSC Film #1 comparison has already been dealt with in Example 4.  
         [0139]    There is no PL1840 monofilm data to compare with the Hot Tack strength of Film #3.  
       Example 22  
       [0140]    The Film #2 versus SSC Film #1 comparison has already been dealt with in Example 4.  
         [0141]    Film #3 (density difference of only 0.010 g/cc) versus SSC Film #1 (Films from Example 9)  
                                                                                     Hot Tack   Hot Tack               Temperature of   Strength of   Strength of   Hot Tack           Sealing Jaws   SSC Film #1   Film #3   Boost           (° C.)   (g/3 in.)   (g/3 in.)   (g/3 in.)                                        100   0   0   0           105   0   200   200           110   0   700   700           115   0   1000   1000           120   100   1200   1100           125   200   1000   800           130   500   800   300           135   700   800   100           140 ←T max     800   700   −100           145   600   500   −100           150   400   300   −100                                                          
 
         [0142]    Film #3 is NOT an example of the patent because the Hot Tack Strength is NOT boosted at temperatures at or above the temperature which results in peak Hot Tack Strength of the single-site catalyst interpolymer.  
         [0143]    Film #4 (density difference of only 0.006 g/cc) versus SSC Film #1 (Films from Example 9)  
                                                                                     Hot Tack   Hot Tack               Temperature of   Strength of   Strength of   Hot Tack           Sealing Jaws   SSC Film #1   Film #4   Boost           (° C.)   (g/3 in.)   (g/3 in.)   (g/3 in.)                                        100   0   0   0           105   0   100   100           110   0   500   500           115   0   1000   1000           120   100   1000   900           125   200   1000   800           130   500   1000   500           135   700   800   100           140 ←T max     800   700   −100           145   600   600   0           150   400   500   100                                                          
 
         [0144]    Film #4 is NOT an example of the invention because the Hot Tack Strength is NOT boosted at temperatures at or above the temperature which results in peak Hot Tack Strength of the single-site catalyst interpolymer.  
         [0145]    In the following Tables information about the resins used for the films of the Examples is found as provided by the manufacturer and as measured by us.  
                                             TABLE 1                           BASIC RESIN SUPPLIER DATA                                nominal                               MI                               (g/10                               min.   nominal           resin   resin           @ 2 kg,   density       supplier   code   type   catalyst   comonomer   190 C.)   (g/cc)               Exxon   EXACT   LLDPE   metallocene   hexene   1.5   0.920           2010       Exxon   EXACT   VLDPE   metallocene   butene/   1.2   0.900           3033           hexene       Exxon   EXACT   VLDPE   metallocene   hexene   1.2   0.901           3132       Exxon   EXACT   ULDPE   metallocene   butene   3.0   0.878           4041       Exxon   EXCEED   LLDPE   metallocene   hexene   1.0   0.917           350D60       Dow   AFFINITY   VLDPE   metallocene   octene   1.0   0.902           PL1880       Dow   AFFINITY   VLDPE   metallocene   octene   1.0   0.908           PL1840       Dow   AFFINITY   VLDPE   metallocene   octene   1.0   0.915           FM1570       Dow   ELITE   LLDPE   metallocene/   octene   0.85   0.920           5100       unknown       Novacor   SCLAIR   LLDPE   Zeigler Natta   octene   0.75   0.920           11L4B       Novacor   SCLAIR   VLDPE   Zeigler Natta   octene   0.8   0.911           E032-07       Novacor   LF0521A   HPPE   unknown   homopolymer   5.0   0.921                  
 
         [0146]    [0146]                                                         TABLE 2                           Experimentally Determined Resin Properties                MI 2     MI 10                                         (g/10 min   (g/10 min       I 10 /I 2 -4.63           @ 2 kg,   @ 10 kg,   MI 10 /   (melt flow   branching/       Resin   190 C.)   190 C.)   MI 2     ratio)   1000 C.   M W     M n     M W /M n     CDBI               EXACT   1.57    8.62    5.49   0.86    8 hexene    98289   51256   1.918   89.7       2010       EXACT   1.26    7.01    5.56   0.93   18 hexene &amp;   101908   53747   1.896   97.2       3033                    6 butene       EXACT   1.19    6.71    5.64   1.01   25 hexene   101407   55960   1.812   97.0       3132       EXACT   2.99   17.74    5.93   1.3   42 butene    83630   41054   2.037   96.4       4041       EXCEED   1.05    5.96    5.68   1.05   15 hexene   112231   49858   2.251   69.3       350D60       AFFINITY   1.18   10.91    9.25   4.62   22 octene    88611   48206   1.838   94.8       PL1880       AFFINITY   1.11   11.45   10.32   5.69   17 octene    78260   41455   1.888   92.6       PL1840       AFFINITY   1.04   11.06   10.63   6.0   14 octene    75024   35048   2.141   91.4       FM1570       ELITE   0.91    6.65    7.31   2.68   14 octene    97259   35591   2.733   30.8       5100       SCLAIR   0.75    6.33    8.44   3.81   14 octene   132185   40649   3.252   31.8       11L4B       SCLAIR   0.70    5.98    8.54   3.91   15 octene   120193   30826   3.899   42.4       E032-07       NOVA   5.07   64.95   12.81   8.18   —    50178   16375   3.064   —       LF0521A                    
         [0147]    The invention may be varied in any number of ways as would be apparent to a person skilled in the art and all obvious equivalents and the like are meant to fall within the scope of this description and claims. The description is meant to serve as a guide to interpret the claims and not to limit them unnecessarily.