Abstract:
Methods for manufacturing solid-state thermal neutron detectors with simultaneous high thermal neutron detection efficiency (&gt;50%) and neutron to gamma discrimination (&gt;10 4 ) are provided. A structure is provided that includes a p+ region on a first side of an intrinsic region and an n+ region on a second side of the intrinsic region. The thickness of the intrinsic region is minimized to achieve a desired gamma discrimination factor of at least 1.0E+04. Material is removed from one of the p+ region or the n+ region and into the intrinsic layer to produce pillars with open space between each pillar. The open space is filed with a neutron sensitive material. An electrode is placed in contact with the pillars and another electrode is placed in contact with the side that is opposite of the intrinsic layer with respect to the first electrode.

Description:
CROSS-REFERENCE TO RELATED APPLICATIONS 
       [0001]    This is a Continuation in Part of U.S. patent application Ser. No. 13/014,879, titled “Method To Planarize Three-Dimensional Structures To Enable Conformal Electrodes,” filed Jan. 27, 2011, incorporated by reference. This application claims priority to U.S. provisional No. 61/509,023, filed Jul. 18, 2011, incorporated herein by reference. U.S. application Ser. No. 13/014,879 is a continuation-in-part of U.S. patent application Ser. No. 11/414,288, titled “Semiconductor Materials Matrix for Neutron Detection,” filed Apr. 27, 2006, incorporated herein by reference. U.S. patent application Ser. No. 11/414,288 claims priority to U.S. Provisional Patent Application Ser. No. 60/675,654, titled “Semiconductor Nano-Materials Matrix for Neutron Detection,” filed Apr. 27, 2005, incorporated herein by reference. 
     
    
     STATEMENT REGARDING FEDERALLY SPONSORED RESEARCH OR DEVELOPMENT 
       [0002]    The United States Government has rights in this invention pursuant to Contract No. DE-AC52-07NA27344 between the U.S. Department of Energy and Lawrence Livermore National Security, LLC, for the operation of Lawrence Livermore National Laboratory. 
     
    
     BACKGROUND OF THE INVENTION 
       [0003]    1. Field of the Invention 
         [0004]    The present invention relates to high efficiency solid state thermal neutron detectors, and more specifically, it relates to process design for high thermal neutron efficiency and high gamma rejection. 
         [0005]    2. Description of Related Art 
         [0006]    Solid-state thermal neutron detectors are required for a variety of applications, particularly, nonproliferation of special nuclear material (SNM). The currently used technology involves  3 He tubes, which have a variety of shortcomings when utilized in the field as thermal neutron detectors, including the need for high-voltage operation, sensitivity to microphonics, and large size. Moreover, given that the world&#39;s supply of  3 He is limited, this presents yet another set of critical issues related to strategic and tactical implications, which are of practical importance. 
         [0007]    A variety of solid-state thermal neutron detectors have been proposed, which often involve trade-offs between thermal neutron detection efficiency and gamma discrimination, which are two key performance metrics. As an example, by modifying the detector geometry and composition, one can, in general, increase the neutron detection efficiency. However, improving this metric can result in greater false positives and false negatives. That is, in the present art, increasing the sensitivity of the device to detect thermal neutron events can result in a concomitant increase in the response of the detector to gamma ray events. Since the electrical output signature of the detector for neutron and gamma events is typically similar, neutron events can be misinterpreted as gamma events, and, vice versa. It is desirable to provide sensor designs, as well as different fabrication processes, to realize a robust detector that simultaneously achieves high thermal neutron detection efficiency, with high levels of gamma discrimination. 
       SUMMARY OF THE INVENTION 
       [0008]    One aspect of the invention is a method for manufacturing solid-state thermal neutron detectors with simultaneous high thermal neutron detection efficiency (&gt;50%) and neutron to gamma discrimination (&gt;10 4 ). Another aspect is the detector itself. A structure is provided that includes a p+ region on a first side of an intrinsic region and an n+ region on a second side of the intrinsic region. The thickness of the intrinsic region is chosen to achieve a desired neutron to gamma discrimination. Material is removed from (i) one of the p+ region or the n+ region and (ii) the intrinsic layer to produce pillars with open space between each pillar. The pillars have a pitch within a range from about 0.1 μm to about 10 μm and a height within a range from about 10 μm to about 200 μm. A neutron sensitive material comprising  10 B fills the open space. One electrode is placed in contact with the pillars and another electrode is placed in contact with the opposite side of the intrinsic layer with respect to the first electrode. 
         [0009]    Generally, the intrinsic layer thickness is less than about 120 μm and more specifically, may be about 50 μm. In some embodiments, the structure may be initially formed from a thin wafer having a thickness within a range from about 50 μM to about 200 μm. The intrinsic region, in some embodiments, may be a float zone wafer or an epitaxial grown wafer. Pillar pitch may be within a range from 1 μM to about 3 μm and more specifically, may be about 2 μm, in some embodiments. The pillars may, e.g., comprise an aspect ratio selected from the group consisting of (i) within a range from about 100:1 to about 10:1, (ii) within a range from about 25:1 to about 10:1 and (iii) about 25:1. The p+ region or the n+ region of the pillars may, e.g., comprise a doping density of at least 1E+18 dopants per cm 3 . The structure may, e.g., comprise a handle wafer which may further have a doping density of at least 1E+18 dopants per cm 3  of conductive semiconductor. The handle wafer may, e.g., be an insulating wafer or a wafer with a insulating top layer and may have an etched area to decrease the area under the pillars to increase gamma rejection. The thickness of the intrinsic layer under the pillars may, e.g., be within a range from about 0 μm to about 100 μm. 
     
    
     
       BRIEF DESCRIPTION OF THE DRAWINGS 
         [0010]    The accompanying drawings, which are incorporated into and form a part of the disclosure, illustrate embodiments of the invention and, together with the description, serve to explain the principles of the invention. 
           [0011]      FIG. 1A  depicts a three-dimensional device structure, consisting of a monolithic substrate of one material, with an array of high-aspect ratio pillars with cavity regions etched between the pillars. 
           [0012]      FIG. 1B  depicts a three-dimensional structure with an array of high aspect ratio pillars, whose cavities regions contain a second material, which serves as an active (i.e., functional) region or as a passive (i.e., support) region. 
           [0013]      FIG. 1C  depicts the structure of  FIG. 1B  with conformal electrode coatings on opposing surfaces forming a compact sensor of other electronic device. 
           [0014]      FIG. 2  shows a schematic of a pillar-structured, solid-state thermal neutron detector. 
           [0015]      FIG. 3  shows a Monte Carlo simulation depicting the thermal neutron detection efficiency as a function of pillar height for several different pillar widths and spacings. 
           [0016]      FIG. 4A  shows a schematic of a pillar-structured, solid state thermal neutron detector. 
           [0017]      FIG. 4B  shows the measured gamma discrimination with gamma energy of 662 keV as a function of total thickness of intrinsic layer. 
           [0018]      FIG. 4C  shows simulation of gamma absorption with gamma sources:  241 Am (60 keV),  137 Cs (662 keV), and  60 Co (1.3 MeV) respectively. 
           [0019]      FIG. 4D  shows the effect of substrate doping on gamma counts with incident gamma energy of 1.3 MeV. 
           [0020]      FIG. 5A  shows a first fabrication method to realize a neutron detector with large gamma discrimination using epitaxial growth. 
           [0021]      FIG. 5B  shows the second step of the process, whereby a photoresist pattern is applied to one surface of the wafer to define the pillar regions. 
           [0022]      FIG. 5C  shows the third step of the process, whereby high-aspect ratio cavities are formed via deep reactive ion etching. 
           [0023]      FIG. 5D  shows the fourth step of the process, whereby a neutron converter material is deposited onto the overall structure. 
           [0024]      FIG. 5E  shows the fifth step of the process, whereby the structure is plasma etched. 
           [0025]      FIG. 5F  shows the sixth and final step of the process, whereby conformal electrodes are deposited onto the opposing surfaces of the overall structure. 
           [0026]      FIG. 6A  shows a second fabrication method to realize a neutron detector with large gamma discrimination using a thin substrate approach using ion implantation. 
           [0027]      FIG. 6B  shows the second step of the process, whereby the wafer is doped on opposing surfaces with p-type and n-type materials, respectively; alternately the p+ and n+ regions can be defined by epitaxial growth. 
           [0028]      FIG. 6C  shows the third step of the process, whereby a photoresist pattern is applied to one surface of the wafer to define the pillar regions. 
           [0029]      FIG. 6D  shows the fourth step of the process, whereby high-aspect ratio cavities are formed via deep reactive ion etching. 
           [0030]      FIG. 6E  shows the fifth step of the process, whereby a neutron converter material is deposited onto the overall structure. 
           [0031]      FIG. 6F  shows the sixth step of the process, whereby the structure is plasma etched. 
           [0032]      FIG. 6G  shows the seventh and final step of the process, whereby conformal electrodes are deposited onto the opposing surfaces of the overall structure. 
           [0033]      FIG. 7A  shows a third fabrication method to realize a neutron detector with large gamma discrimination using a high resistivity float zone material and wafer bonded to a low resistivity substrate. 
           [0034]      FIG. 7B  shows the second step of the process, whereby the wafer is doped on the bottom surface with an n+ type material. 
           [0035]      FIG. 7C  shows the third step of the process, whereby the bottom surface of the initial thin wafer is bonded to a thick, n+ type semiconductor handle-wafer. 
           [0036]      FIG. 7D  shows the fourth step of the process, whereby the exposed upper surface of the wafer is lapped to the desired thickness, and, is subsequently doped with a p+ type material. 
           [0037]      FIG. 7E  shows the fifth step of the process, whereby a photoresist pattern is applied to the upper surface of the wafer to define the pillar regions. 
           [0038]      FIG. 7F  shows the sixth step of the process, whereby high-aspect ratio cavities are formed via deep reactive ion etching. 
           [0039]      FIG. 7G  shows the seventh step of the process, whereby a neutron converter material is conformally deposited onto the upper surface of the structure, followed by a plasma back-etch. 
           [0040]      FIG. 7H  shows the eighth step of the process which is optional, whereby the thick n+ semiconductor handle-substrate is selectively wet-etched (or dry etched) in the region directly under the pillar area. 
           [0041]      FIG. 7I  shows the ninth and final step of the process, whereby conformal electrodes are deposited onto the opposing surfaces of the overall structure. 
           [0042]      FIG. 8A  shows a fourth fabrication method to realize a neutron detector with large gamma discrimination using a back-etching approach, applied directly to a single, thick wafer, to selectively remove a region underneath the active pillar area. The first step involves cutting and polishing a thick semiconductor wafer. 
           [0043]      FIG. 8B  shows the second step of the process, whereby the thick semiconductor wafer substrate is selectively back-etched directly under the region that will define the eventual pillar area. 
           [0044]      FIG. 8C  shows the third step of the process, whereby the top surface of the wafer is doped with a p+ type material. 
           [0045]      FIG. 8D  shows the fourth step of the process, whereby the bottom (back-etched) surface of the wafer is doped with an n+ type material. 
           [0046]      FIG. 8E  shows the fifth step of the process, whereby a photoresist pattern is applied to the upper surface of the wafer to define the pillar regions. 
           [0047]      FIG. 8F  shows the sixth step of the process, whereby high-aspect ratio cavities are formed via deep reactive ion etching of the top surface. 
           [0048]      FIG. 8G  shows the seventh step of the process, whereby a neutron converter material is conformally deposited onto the upper surface of the structure, followed by a plasma back-etch. 
           [0049]      FIG. 8H  shows the eighth and final step of the process, whereby conformal electrodes are deposited onto the opposing surfaces of the overall structure. 
           [0050]      FIG. 9A  shows a fifth fabrication method to realize a neutron detector with large gamma discrimination, using an electronically passive and coated handle-wafer approach, to which is bonded the detector wafer and the volume of semiconductor material is etched off early in the process. The first step involves cutting and polishing a thick FZ semiconductor wafer. 
           [0051]      FIG. 9B  shows the second step of the process, whereby the detector wafer is doped on the bottom surface with an n+ type material. 
           [0052]      FIG. 9C  shows the third step of the process, whereby the bottom surface of the detector wafer is bonded to a thick, oxidized handle-wafer. 
           [0053]      FIG. 9D  shows the fourth step of the process, whereby the exposed upper surface of the wafer is lapped to the desired thickness, and, is subsequently doped with a p+ type material. 
           [0054]      FIG. 9E  shows the fifth step of the process, whereby a photoresist pattern is applied to the central region of the upper surface of the wafer to define the pillar regions. 
           [0055]      FIG. 9F  shows the sixth step of the process, whereby high-aspect ratio cavities and thin perimeter layers are formed via deep reactive ion etching. 
           [0056]      FIG. 9G  shows the seventh step of the process, whereby a neutron converter material is conformally deposited onto the central region of the upper surface of the structure, followed by a plasma back-etch over the entire upper surface. 
           [0057]      FIG. 9H  shows the eighth and final step of the process, whereby conformal electrodes are deposited onto the central pedestal and to the thin perimeter region of the upper surface of the overall structure forming a transverse circuit configuration. 
           [0058]      FIG. 10  shows a detector that integrates the basic neutron pillar structure with a monolithic, independent set of one or more gamma-ray detectors for enhanced gamma discrimination and enhanced radiation immunity to potential defect centers. 
       
    
    
     DETAILED DESCRIPTION OF THE INVENTION 
       [0059]    The platform for thermal neutron detection described herein is based on an array of pillar structured p-i-n semiconductor diodes within which a thermal neutron conversion material, such as  10 B, has been interspersed. The salient features of this class of detector are briefly reviewed, followed by embodiments that enhance the detector performance in terms of improved neutron detection sensitivity, concomitant with greater levels of gamma ray discrimination. In the example drawings, the top of the pillar is p+ with n+ as the substrate. The opposite can be done having n+ as the top of the pillar with an p+ substrate. Doping can be done by ion implantation, diffusion or by epitaxial growth. The pillars can be squares, circles, hexagons, etc. While the target design was 50 microns, embodiments of the pillars can be within a broader range, e.g., in the range of 25-100 microns tall. 
         [0060]    A basic pillar-based thermal neutron detector is shown in  FIGS. 1A ,  1 B and  1 C. A schematic drawing of a general three-dimensional neutron detector structure  100  in cross section, is shown in  FIG. 1A . It consists of substrate  110 , etched to form an array of pillars,  115 , with inter-dispersed cavity regions (the gaps between the pillars)  120 , filled with a suitable material, which can differ from that of the substrate material. Typically, the lower surface of structure  100  depicted by cross section A-A in  FIG. 1B , consists of a single material, typically a semiconductor, such as Si, which is a substrate of the overall structure. The upper surface of structure  100 , depicted by cross section B-B in  FIG. 1B , consists of several different materials, whose mechanical and compositional properties can differ in general. Inter-dispersed in the regions between the pillars is a second material  125 , as shown in  FIG. 1B . This second material  125 , in the case of a thermal neutron detector, consists of  10 B. The aspect ratio of the structure, namely, the ratio of the height of the pillars relative to its width can vary from about 1:1 to 1000:1. For thermal neutron detection, the aspect ratio is in the range of 10:1 to 100:1; the pitch as well as the pillar cross section dimension is in the range 1 to 10 μm, and the pillar height is in the range of 10 μm to 100 μm. 
         [0061]    As shown in  FIG. 1C , electrical contact to the detector consists of upper and lower conductive layers,  130  and  140 , respectively, that bound the active region of the sensor. In order to realize functionality and reliability of such three-dimensional structures, it is necessary to deposit a global electrical contact, interconnecting the tops of the pillar-arrayed structure. As an example, the lower surface of the substrate  110  can consist of an n+ layer, whereas the top region of each Si pillar  115 , as shown in  FIG. 1B , can consist of a p+ layer of a p-i-n diode. Preferred processing techniques to circumvent otherwise detrimental non-uniform morphology, including planarization techniques to provide a robust, contiguous and conformal electrode across the upper surface of the pillared structure, are discussed in U.S. patent application Ser. No. 13/014,879, incorporated herein by reference. 
         [0062]    An example of a completed thermal neutron detector,  200  is shown in  FIG. 2 . This figure also depicts an example of a typical neutron event and its interaction with the detector. Owing to the high neutron interaction cross section with  10 B, the neutrons primarily interact in those regions of the detector. The resultant products of this key interaction channel include a  7 Li particle and an alpha particle. The alpha and  7 Li particle subsequently interacts in the neighboring intrinsic Si regions, giving rise to electron-hole pairs, whose resultant current is sensed across electrodes  230  and  240 . An example of an undesirable event (not shown) is the interaction of a gamma ray with the detector, which can also give rise to an electron-hole pair, and, hence, result in a deleterious false alarm. 
         [0063]    The pillar-structured, solid-state thermal neutron detector of  FIG. 2  is a basic detector geometry that enables the optimization of two physical detector mechanisms: (i) a relatively long interaction length (≈50 μm in the longitudinal direction along the length of the  10 B fill material) for the incident thermal neutrons to interact with the  10 B, to optimize the generation of the decay products—an alpha particle and a  7 Li-ion and (ii) a relatively short interaction length (≈2 μm in the lateral direction) for the alpha and  7 Li decay products to interact with the Si pillars, to optimize the generation of electron-hole pairs in the Si p-i-n pillars for detection of the neutron event. 
         [0064]    The choice of the various detector dimensions, aspect ratios, materials and sensor geometry will all have influence on the performance of the detector. As an example, the thermal neutron detection efficiency scales with the pillar height and inversely with pillar width, as shown in  FIG. 3 . In addition to the detection efficiency, neutron detectors have an additional figure-of-merit based on the ability to discriminate between the sensing of desired events relative to that of all other channels. In the present case, a desired event is defined as an output signal resulting from the interaction of a thermal neutron with the detector, whereas, an example of an undesired event is an output signal resulting from the interaction of a gamma ray with the detector, with both normalized to their respective detection probabilities. The present invention optimizes this discrimination metric, so that the false alarm rates (positive and negative) are minimized. 
         [0065]    The Monte Carlo simulation of  FIG. 3  depicts the thermal neutron detection efficiency as a function of pillar height for several different pillar widths and spacings. It shows high thermal neutron detection is possible with 50 μm pillar height and close spaced pillars. The neutron detection efficiency is related to the volume of boron and e/h charged carrier collection. The gamma response is related to the total thickness of semiconducting material between the electrodes and dependent on the doping concentration, n or p type, and electric field. 
         [0066]    The discrimination between (undesirable) gamma events and (desirable) neutron events, henceforth referred to as “gamma discrimination,” is defined as the thermal neutron detection efficiency divided by the gamma detection efficiency. To adequately distinguish between events resulting from thermal neutron events and background gamma events (typical for most practical implementations), the neutron-to-gamma discrimination must be on the order of, or greater than, 1×10 4 . Detectors in the art include  3 He tubes, which possess gamma discriminations of 1×10 8 . Thus, a solid-state thermal neutron detector, as described herein, capable of reaching or exceeding that metric, is highly desirable by the end-user community. 
         [0067]      FIG. 4A  shows a schematic of a pillar-structured, solid state thermal neutron detector. H 1 , H 2 , and H 3  are depicting pillar height, intrinsic layer thickness below pillars and high doped substrate thickness, respectively. For neutron detection, the neutron absorption takes place in neutron conversion material which is defined by pillar size, pitch and height (H 1 ). Pillar height should be sufficiently tall for neutron absorption (50 μm). Generated carriers are swept into n+ and p+ layers by an electric field induced by either built-in voltage or external reverse bias. For gamma detection, the gamma absorption takes place in the whole silicon portion (p+, intrinsic, n+ substrate). Carriers generated in the intrinsic region (H 1  and H 2 ) are collected by carrier drift induced the by electric field, and carriers generated in p+ region and n+ substrate (H 3 ) are collected by carrier diffusion. The portion of collected carriers depends on carrier diffusion length which is determined by doping concentration. 
         [0068]    In general, increasing pillar height (H 1 ) enhances both neutron and gamma absorption. Increasing H 2  increases gamma absorption only since the intrinsic layer below pillars is only sensitive to gamma rays. This layer should be reduced as much as possible in order to obtain high gamma rejection. Increasing H 3  enhances gamma absorption, but the gamma counts will saturate when H 3  is much thicker than the carrier&#39;s diffusion length. 
         [0069]      FIG. 4B  shows the measured gamma discrimination with gamma energy of 662 keV as a function of total thickness of intrinsic layer. The total thickness (H) is the sum of pillar height, H 1  and the thickness of intrinsic layer below pillars (H 2 ). Pillar heights are 25 μm, 50 μm, 50 μm and 50 μm for four samples with total intrinsic layer thickness of 25 μm, 50 μm, 190 μm and 380 μm respectively. The discrimination value is dramatically decreased from 1.3×10 7  down to 44 by increasing the intrinsic layer thickness to 190 μm. To obtain gamma discrimination of 1×10 5 , the total intrinsic thickness should be reduced to less than ˜80 μm. 
         [0000]    
       
         
               
             
               
               
             
               
               
             
           
               
                 TABLE 1 
               
             
             
               
                   
               
               
                 Neutron-to-gamma discrimination per intrinsic layer thickness 
               
             
          
           
               
                 Intrinsic thickness (μm) 
                 Neutron-to-gamma discrimination 
               
               
                   
               
             
          
           
               
                 25 
                 1.30E+07 
               
               
                 50 
                 9.40E+05 
               
               
                 190 
                 44 
               
               
                 380 
                 6 
               
               
                   
               
             
          
         
       
     
         [0070]      FIG. 4C  shows a simulation of gamma absorption with gamma sources:  241 Am (60 keV),  137 Cs (662 keV), and  60 Co (1.3 MeV) respectively. The tendency of substrate thickness dependence remains the same regardless of gamma energies, as shown by the overlapping plots. The gamma counts become saturated (98% of maximum gamma counts) at 30 μm due to the minority carrier (hole) diffusion length. The carriers generated in this region (0-30 μm) can diffuse into the intrinsic layer and contribute gamma counts. That makes this region “sensitive” to gamma rays. The carriers generated in the region (&gt;30 μm) will recombine before they diffuse into the intrinsic layer and will not contribute gamma counts. That makes this region “not sensitive” to gamma rays. Decreasing the thickness of material under the pillars to make it less than the diffusion length is important.  FIG. 4D  shows the effect of substrate doping on gamma counts with incident gamma energy of 1.3 MeV. The gamma counts are the same for both doping concentrations when substrates are thin enough to allow all generated minority carriers diffusion into intrinsic region. As compared to 1 μm substrate thickness 28% more gamma counts is expected for substrate thickness above 30 μm for the doping of 1×10 18  cm −3 . Only 4% more gamma counts are expected for substrate thickness above 5 μm for the doping of 1×10 19  cm −3 . The higher the doping, the shorter the diffusion length. Thus, less gamma “sensitive” region is present with a highly doped substrate. It is therefore important to increase substrate doping. 
         [0000]    
       
         
               
             
               
               
               
               
             
           
               
                 TABLE 2 
               
             
             
               
                   
               
               
                 Properties of minority carrier (hole) in highly doped n-Si substrate 
               
             
          
           
               
                 Doping concentration 
                 Mobility 
                 Lifetime 
                 Diffusion Length 
               
               
                 (cm −3 ) 
                 (cm 2 /Vs) 
                 (μs) 
                 (μm) 
               
               
                   
               
               
                 1 × 10 18   
                 89.2 
                 0.248 
                 7.57 
               
               
                 1 × 10 19   
                 50.7 
                 0.025 
                 1.81 
               
               
                   
               
             
          
         
       
     
         [0071]    Limiting the intrinsic material underneath the pillar and having high substrate doping with the thinnest possible thickness yields high gamma rejection. Accordingly, the present invention provides various process flows to fabricate devices with this ideal high thermal neutron efficiency 50% (but possibilities are between 5-80% with high gamma rejection &gt;1e4). 
         [0072]    The fabrication involves removing a substantial amount of material from a substrate in which the pillarized p-i-n diodes are created, thereby maximizing the gamma discrimination factor. Using this approach, however, results in an array of pillars, which is mechanically weaker than the starting material. Thus, there is a trade-off between the mechanical integrity of the device and its performance, in terms of gamma discrimination. 
         [0073]    The teachings of this invention describe manufacturing processes to fabricate a solid-state detector capable of achieving large gamma discrimination (&gt;1×10 4 ), and, concomitantly, with good mechanical integrity and high fabrication yield. Some embodiment fabrication methods involve techniques to realize a detector with epitaxial growth or a thin substrate, while maintaining its mechanical integrity. Another method involves techniques to enhance the gamma discrimination factor and robustness of thermal neutron detectors in general, regardless of the substrate thickness. This latter method can also augment any of the thin-substrate embodiments to further enhance the gamma discrimination metric of the detector. 
         [0074]    Methods described herein, to enhance the detector performance, include the following: (1) employing a starting substrate that is initially thin (&lt;1.00 μm); (2) bonding of a thin wafer to a thick n+ substrate wafer, with etch-back under the pillar region; (3) selective etching of the substrate under pillar region within a single substrate; (4) bonding of a thin wafer to a thick insulated substrate that is not electrically active but provides mechanical support; and (5) employing auxiliary active or passive layers, monolithically formed above and/or below the native detector, to enhance the gamma discrimination and to radiation-harden the detector. 
         [0075]    U.S. application Ser. No. 13/014,879 describes processing methods to form conformal, large-area electrode contacts across the surfaces of such 3-d, pillarized, high-aspect-ratio detectors, including planarization techniques. One skilled in the art will appreciate which choice of planarization technique, as taught in the parent application, is best suited to implement a conformal, blanket coating or contact for a given detector configuration and its material composition. These fabrication processes are employed in the present invention, as needed. 
         [0000]    Neutron Detector with Large Gamma Discrimination. 
         [0076]      FIG. 5A  shows a first fabrication method to realize a neutron detector with large gamma discrimination using epitaxial growth. The first step involves epitaxial growth of the intrinsic region  400  and p+ region  410  on an n+ substrate  420 .  FIG. 5B  shows the second step of the process, whereby a photoresist pattern  430  is applied to one surface of the wafer to define the pillar regions.  FIG. 5C  shows the third step of the process, whereby high-aspect ratio cavities  440  are formed via deep reactive ion etching.  FIG. 5D  shows the fourth step of the process, whereby a neutron converter material  450  is conformally deposited onto the overall structure.  FIG. 5E  shows the fifth step of the process, whereby the structure is plasma etched.  FIG. 5F  shows the sixth and final step of the process, whereby conformal electrodes  460  and  470  are deposited onto the opposing surfaces of the overall structure. 
       Pillarized Neutron Detectors Using a Thin Substrate, &lt;100 μm in Thickness. 
       [0077]    As discussed above, the gamma discrimination factor can be improved by fabricating a detector with a thin substrate. One employs various processing techniques to reduce the thickness of an initially thick wafer to a value that meets or exceeds the desired gamma discrimination factor. This process, however, can result in a detector whose structure is mechanically compromised, as well as reducing the manufacturing yield. 
         [0078]    In this embodiment, one employs a thin wafer, typically of thickness on the order of 100 μm or less, as a starting material. The wafer thickness is specified to correspond to a desired active region of the final detector. This approach negates the need to reduce the thickness of an otherwise thick wafer, thereby circumventing the possibility of adversely affecting the mechanical integrity of the structure. Moreover, given that the wafer thickness constitutes that of the final detector, and, no additional thinning is required, an intrinsic wafer material can be employed, with each respective surface suitably doped to form the requisite n+ type and p+ type regions of the detector from the onset. 
         [0079]    An example of the processing steps using this approach is shown in  FIGS. 6A through 6G . As shown in  FIG. 6A , a float-zone (FZ) wafer  510  is selected, comprised of a suitable, high-resistivity, intrinsic (undoped) semiconductor material, such as Si. This starting substrate is initially thin, with a thickness on the order of ≈100 μm. The substrate is then heavily doped, as shown in  FIG. 6B , to form p+ and n+ regions,  520  and  530 , respectively, via ion implantation or diffusion processing on the top and bottom of the wafer, respectively. Boron and Arsenic dopants can be employed to form the p+ and n+ regions, respectively. 
         [0080]    The wafer is then coated with photoresist  540  and patterned, with a pitch in the range of 2 to 4 μm, as depicted in  FIG. 6C . In the case of a 3-D neutron detector, the pattern on the surface is in the form of a 2-dimensional grid of squares, as viewed from above the top surface. High-aspect-ratio pillars  550  are then etched into the material using deep reactive ion etching (RIE), to a depth in the range of 10 μm to 50 μm, as shown in  FIG. 6D . 
         [0081]    As depicted in  FIG. 6E , this is followed by the deposition of a conformal neutron converter material  560 , which, in this case, is  10 B. This results in the formation of an array of inlaid pillars  565 , each pillar of which typically measuring 2 μm×2 μm in cross section, with a depth of about 50 μm. The converter material is then etched back to reveal the upper surface  570  of the Si substrate matrix, within which is an array of inlaid  10 B  565 , as shown in  FIG. 6F . 
         [0082]    The resultant surface is then planarized, per the teachings of the parent patent application (e.g., via a plasma etch). The final step in this process is the formation of the sensor electrodes  580 , formed by the deposition of blanket, conformal conductive metalized layers on the top and bottom surfaces of the detector, as shown in  FIG. 6G , resulting in ohmic contacts to the p+ and n+ diffused layers, respectively. 
         [0000]    Pillarized Neutron Detectors Using a Thin or Thick Substrate, Bonded to a Thick Substrate Wafer, with Etch-Back Under the Pillar Region. 
         [0083]    In this embodiment, one employs either a thin or thick intrinsic wafer as the starting substrate material for the detector. The detector substrate is then bonded to a thick handle support wafer. The thick handle support wafer is, in the case of the example of  FIGS. 7A-7I , comprised of a n+ material, and, therefore, forms one end of the n-i-p diode structure. Alternately, the thick handle support may be comprises of a p+ material to form one end of the n-i-p structure. In this embodiment, both wafers are then selectively lapped and planarized to form the overall structure. The net substrate thickness of the resultant detector can therefore be minimized to enhance the gamma discrimination factor, while maintaining the mechanical integrity of the sensor as well as optimizing the manufacturing yield. 
         [0084]    An example of the processing steps using this second approach is shown in  FIGS. 7A through 7I . As shown in  FIG. 7A , a float-zone (FZ) wafer  610  is selected as the detector substrate, comprised of a suitable, high-resistivity, intrinsic (undoped) semiconductor material, such as Si. In this approach, the starting detector substrate can be either thin (on the order of ≈100 μm) or relatively thick. As shown in  FIG. 7B , the detector substrate is subsequently heavily doped (via ion implantation or diffusion processing, as before) on a single surface  615 , which will ultimately form the bottom surface of the resultant detector active region. The dopant can be either n+ or p+ with an example of the former shown in  FIG. 7B , e.g., using Arsenic as the n+ type dopant  630 . 
         [0085]    As shown in  FIG. 7C , the detector substrate  610  is then wafer-bonded to a thick “handle wafer”  690 . The detector substrate wafer is oriented so that its doped (bottom) surface (n+ in this example)  615  forms an interface  695  (dashed line) with the top of the n+ handle wafer. The handle wafer is chosen to be of the same carrier type as that of the doped bottom surface of the detector wafer. In the example shown in  FIG. 7C , the entire handle wafer is chosen to be n+ type, since the bottom surface  615  of the detector wafer is n+ type (the same logic applies in the case of a p+ type interfaced structure). As is known in the art, the method of wafer bonding could be chemically, plasma or heat activated. 
         [0086]    In the next processing step, as shown in  FIG. 7D , the exposed (upper, or, topside) surface of the initially thick wafer  610  is then lapped down to the desired final thickness of the resultant detector substrate region. (This step is not necessary if the starting detector wafer is initially chosen to be of the desired thickness.) The upper (topside) surface of the (now, thin) detector wafer  625  is then heavily doped with the opposite polarity relative to the bottom surface. In the example shown in  FIG. 7D , the exposed surface of the detector wafer is doped as p+ type, using, as an example, Boron as the p+ dopant  620 . In this case, the resultant structure, as viewed downward from above the detector wafer  625 , forms a p-i-n diode or, in the opposite case (viz., a p+ handle wafer), a n-i-p diode. 
         [0087]    Similar steps as described in the above case (Technique 1) above are subsequently performed to form a planar array of converter-material-coated  10 B pillars. Referring to  FIG. 7E , the exposed (top) surface of detector wafer  625  is coated with photoresist  640  and patterned, with a pitch in the range of 2 to 4 μm. In the case of a 3-D neutron detector, the pattern on the surface is in the form of a 2-dimensional grid of e.g., squares (other shapes are within the scope of the invention), as viewed from above the top surface. High-aspect-ratio trenches  650  are then etched into the material using deep reactive ion etching (RIE), to a depth in the range of 10 μm to 50 μm, as shown in FIG. F. 
         [0088]    As depicted in  FIG. 7G , this is followed by the deposition of a conformal neutron converter material  660 , which, in this case, is  10 B. This results in the formation of an array of inlaid pillars, each pillar typically measuring 2 μm×2 μm in cross section, with a depth of about 50 μm. The converter material is then etched back to reveal the upper surface  670  of the substrate matrix, as shown in  FIG. 7G . The resultant surface  670  is then planarized, per the teachings of the parent patent application (e.g., via a plasma etch). 
         [0089]      FIG. 7H  illustrates an optional step wherein the handle wafer  690  is selectively wet etched using a photoresist mask to remove a large fraction of the material directly underneath the active pillar area  697 , as depicted by the cross-hatched area. The remaining thin region of the handle wafer forms the n+ layer of the p-i-n array of Si diodes. The final step in this process, as shown in  FIG. 7I , is the formation of the sensor electrodes  680 , formed by the deposition of blanket, conformal, conductive metalized layers on the top and bottom surfaces of the detector, resulting in ohmic contacts to the p+ and n+ layers, respectively. This technique results in a neutron detector capable of a high gamma discrimination factor, owing to the thin region below the array of  10 B pillars, inlaid within a Si diode array matrix. Moreover, the resultant structure is mechanically stable since the lower part of the detector is comprised of a solid member (the handle wafer). 
         [0000]    Pillarized Neutron Detectors Using a Thick Substrate, with Selective Etching of the Substrate Under Pillar Region. 
         [0090]    In this embodiment, one employs a single, thick intrinsic wafer as the starting substrate material for the detector, with selective etching of the substrate under the pillar region. As opposed to the above embodiment, in which a detector substrate is bonded onto a handle wafer, the present embodiment teaches a single, thick starting substrate. In the context of the above embodiment, the use of a single, thick wafer performs the function of the neutron detector wafer as well as the support handle wafer, in a single, solid member. 
         [0091]    Hence, the entire neutron detector is formed using the single starting wafer. Therefore, no bonding processes are required, resulting in a structure free of internal interfaces, which could otherwise introduce internal defects across such junctions. This approach, therefore, eliminates the possibility of deleterious surface recombination at internal bond interfaces, while still providing for enhanced gamma discrimination and mechanical integrity. 
         [0092]    The processing steps for this embodiment are shown in  FIGS. 8A through 8G . As shown in  FIG. 8A , a thick, float-zone (FZ) wafer  710  is selected as the detector substrate and support structure. The wafer is comprised of a suitable high-resistivity, intrinsic (undoped) semiconductor material, such as Si. As shown in  FIG. 8B , the backside of the wafer under the (soon-to-be-formed) active area is patterned and then selectively wet etched, using a photoresist mask to remove a large fraction of the material directly underneath the active pillar area  797 , as depicted by the cross-hatched area in the figure. 
         [0093]    As shown in  FIG. 8C , the top surface of the structure is subsequently heavily doped (via ion implantation or diffusion processing, as before). In this example, the dopant is Boron, resulting in a p+ type layer,  720 . Next, as shown in  FIG. 8D , the underside surface of the now-thin region of the handle wafer is heavily doped to form an n+ type layer  730 , using, as an example Arsenic as the dopant. Therefore, the structure, as viewed from the upper surface, will form a p-i-n Si diode array. As noted above, the dopants can be interchanged, resulting in a structure of opposite structural polarity (a n-i-p Si diode array). 
         [0094]    Similar steps as described in the above case are subsequently performed to form a planar array of converter-material-coated  10 B pillars. Referring to  FIG. 8E , the exposed (top) surface of detector wafer  710  is then coated with photoresist  740  and patterned, with a pitch in the range of 2 to 4 μm. In the case of a 3-D neutron detector, the pattern on the surface is in the form of a 2-dimensional grid of squares, as viewed from above the top surface. High-aspect-ratio trenches  750  are then etched into the material using deep reactive ion etching (RIE), to a depth in the range of 10 μm to 50 μm, as shown in  FIG. 8F . 
         [0095]    This is followed by the deposition of a conformal neutron converter material  760 , which, in this case, is  10 B, as depicted in  FIG. 7G . This results in the formation of an array of inlaid pillars, each pillar typically measuring 2 μm×2 μm in cross section, with a depth of about 50 μm. The converter material is then etched back to reveal the upper surface  770  of the substrate matrix, as is also shown in  FIG. 8G . The resultant surface  770  is then planarized, per the teachings of the parent patent application (e.g., via a plasma etch). 
         [0096]    The final step in this process, as shown in  FIG. 8H , is the formation of the sensor electrodes  780 , formed by the deposition of blanket, conformal, conductive metalized layers on the top and bottom surfaces of the detector, resulting in ohmic contacts to the p+ and n+ layers, respectively. This overall processing technique results in a neutron detector capable of a high gamma discrimination factor, owing to the thin region below the array of  10 B pillars, inlaid within a Si diode array matrix. Moreover, the resultant structure is mechanically stable since the entire detector is fabricated from a single Si wafer. 
         [0000]    Pillarized Neutron Detectors Using a Thin Substrate, Bonded to a Thick Insulated Substrate that is not Electrically Active but Provides Mechanical Support. 
         [0097]    In this embodiment, one employs either a thin or thick intrinsic float zone processed wafer as the starting substrate material for the detector. The detector substrate is then bonded to, e.g., a thick insulated support wafer or a wafer with a top insulating region. The thick support wafer in the present embodiment is not electrically active (i.e., it is an insulator), yet, provides mechanical support for the neutron detector. In this embodiment, only the detector wafer requires lapping and planarization to form a thin active region. The substrate thickness of the active detector is minimized to enhance the gamma discrimination factor, while the support wafer maintains the mechanical integrity of the sensor, and, furthermore, improves the manufacturing yield. Given that the support wafer is electrically inactive, the pair of electrical contacts to the active diode wafer, in this case, can be formed on a single relative side of the overall module, at two different surfaces or planes. 
         [0098]    An example of the processing steps using this fourth approach is shown in  FIGS. 9A through 9H . As shown in  FIG. 9A , a float-zone (FZ) wafer  810  is selected as the detector substrate, comprised of a suitable, high-resistivity, intrinsic (undoped) semiconductor material, such as Si. In this approach, the starting detector substrate can be either thin (on the order of ≈100 μm) or relatively thick. As shown in  FIG. 8B , the detector substrate is subsequently heavily doped (via ion implantation or diffusion processing, as before) on a single surface  815 , which will ultimately form the bottom surface of the detector active region. The dopant can be either n+ or p+ with an example of the former shown in  FIG. 9B , using Arsenic as the n+ type dopant  830 . 
         [0099]    As shown in  FIG. 9C , the detector substrate  810  is then wafer-bonded to a thick, oxidized “handle wafer”  890 . The detector substrate wafer is oriented so that its doped (bottom) surface (n+ in this example)  815  forms an interface  895  (dashed line) with the oxide layer of the insulating handle wafer. As is known in the art, the method of wafer bonding could be chemically or plasma activated. 
         [0100]    In the next processing step, as shown in  FIG. 9D , the exposed (upper, or, topside) surface of the initially thick wafer  810  is then lapped down to the desired final thickness of the detector substrate. (This step is not necessary if the starting detector wafer is initially chosen to be of the desired thickness.) The upper (topside) surface of the (now, thin) detector wafer  825  is then heavily doped with the opposite polarity relative to the bottom surface. In the example shown in  FIG. 9D , the exposed (top) surface of the detector wafer is doped as p+ type, using, as an example, Boron as the p+ dopant  820 . In this case, the resultant structure, as viewed downward from above the detector wafer  825 , forms a thin p-i-n diode, which, in turn, is bonded to a thick, insulating, electrically inactive substrate  890 . 
         [0101]    Similar processing steps, as described in the above embodiments, are subsequently performed to form a planar array of neutron converter  10 B pillars. Referring to  FIG. 9E , the exposed (top) surface of detector wafer  825  is coated with photoresist  840  and patterned in the form of a 2-dimensional grid of circles, with a pitch in the range of 2 to 4 μm. Note that the photoresist pillar array pattern for this embodiment is confined to the central area of the surface of the wafer  825 . The perimeter region of the wafer that surrounds the central (patterned) area will, after etching, result in a very thin layer of Si, whose doping profile consists of the heavily doped (backside) n+ region. The thin n+ perimeter layer will enable an ohmic contact to be subsequently formed for the bottom wafer surface electrode. 
         [0102]    As shown in  FIG. 9F , high-aspect-ratio pillars  850  are then etched into the detector wafer material using deep reactive ion etching (RIE), to a depth sufficient to reach the heavily doped backside (n+) region, typically in the range of 10 μm to 100 μm. Hence, the base of the trenches, as well as the exposed surface  855  of the (now) thin layer of Si the surrounds the trenches, reveals the heavily n+ doped backside region of the wafer. The resultant detector surface will therefore consist of a central “pedestal” region of trenches, the perimeter of which is surrounded by a thin layer of Si. 
         [0103]    As depicted in  FIG. 9G , this is followed by the deposition of a conformal neutron converter material  860 , which, in this case, is  10 B. The spatial region of the  10 B deposition is confined to coat only the central trench/pillar area of the wafer. Conventional mask alignment techniques, as is known in the art, can be employed to ensure that deposition of the  10 B is, indeed, limited to the central pillar region, and, furthermore, restricted from coating the (thin) Si perimeter region. This processing step results in the formation of an array of inlaid pillars, each pillar typically measuring 2 μm×2 μm in cross section, with a depth in the range of 10 μm to about 100 μm. The converter material is then etched back to reveal the upper surface  870  of the substrate matrix, as shown in  FIG. 9G . The resultant surfaces  870  and  855  are then planarized, per the teachings of the parent patent application (e.g., via a plasma etch). 
         [0104]    Referring again to  FIG. 9G , it is seen that the central pedestal consists of inlaid  10 B pillars within a Si matrix, whose surface is p+ doped. Thus, a Si p-i-n diode array structure is formed, inlaid with  10 B pillars, whose current flows vertically downward from the p+ doped pedestal surface  870  and, subsequently, laterally outward along the n+ doped layer to the perimeter region  855 . 
         [0105]    The final step in this process, as shown in  FIG. 9H , is the formation of electrodes via the deposition of blanket, conformal, conductive metalized layers  880  that bound the detector. One electrode  881  consists of an ohmic contact formed on the top surface of, the pedestal, while the other electrode  882  consists of an ohmic contact formed along the perimeter region that surrounds the central  10 B pillared pedestal. This technique results in a neutron detector capable of a high gamma discrimination factor, owing to the thin region below the array of  10 B pillars, inlaid within a Si diode array matrix. Furthermore, the resultant structure is mechanically stable since the thin detector wafer is bonded to a solid member (the passive, insulating handle wafer). 
         [0000]    Pillarized Neutron Detectors, Augmented with Monolithic Active or Passive Layers to Electronically Gate the Neutron Detector or Absorb Undesirable Gamma Rays or Other Deleterious Radiation Flux. 
         [0106]    This embodiment teaches methods to further enhance the gamma discrimination factor of the neutron detector by augmenting any or all of the above four embodiments with electronic gating techniques to actively discriminate against gamma rays. In addition, an embodiment is described that can extend the functional lifetime of the sensor through the use of a passive sacrificial layer wherein radiation damage (color centers, defects, etc.) of high-energy interactions can occur with minimal effect on the neutron detector. The auxiliary implementations can be monolithically formed onto the neutron detector, resulting in a rugged, robust, self-aligned structure. 
         [0107]    Examples of such auxiliary enhancement techniques are shown in  FIG. 10 , as applied to a basic neutron detector  910 . The neutron detector is bound by a pair of electrodes  920 , whose output current across contacts  950  is detected by amplifier  960 . The amplifier is electronically gated via logic control input  970 , with a resultant output signal  965 . Surrounding the detector are one of more active and/or passive monolithic structures that can enhance the gamma discrimination factor, as well as improve the lifetime and performance of the detector in the presence of deleterious damaging radiation flux. 
         [0108]    In one example, the neutron detector is augmented with one of more auxiliary gamma ray (or, other ionizing particle interaction) sensors. These sensors can consist of a basic solid-state detector, in the form of an ionizing material  930 , which can be a layer of Si, bound by a pair of electrodes  920 . These detectors can be monolithically formed on one or both surfaces (i.e., upstream and/or downstream) of the neutron detector, and, can be arranged as a single or cascaded set of sensors. One skilled in the art will appreciate that the number and arrangement of the sensors, their specific material(s), layer thicknesses and/or dopants will be a function of the environment and application space in which the neutron detector is to be implemented, including, but not limited to, the expected radiation flux and the specific attributes of the deleterious radiation (particles, energy, etc.), as well as the interaction cross sections of the desired events to be detected (i.e., thermal neutrons) relative to the those of the competing radiation and their respective detection efficiencies. 
         [0109]    Returning to  FIG. 10 , an example of an active gamma ray discrimination system is shown in the case of one upstream and two downstream gamma ray detectors. The output  940  of the respective gamma ray detectors are directed to a respective set of amplifiers  941 , with optional threshold control. In this example, the output logic level of each respective amplifier  943  is conditional on the gamma ray signal level exceeding a programmable threshold level. In this example, the logic outputs  943  are directed to a three-way AND module  945 , whose output logic level  947  is HIGH if all three inputs are HIGH (this indicated that detection and temporal coincidence of a gamma event), and LOW otherwise. This logic level is then directed to the gate input port  970  of the neutron signal amplifier  960 . Contingent on the absence or presence, respectively, of a gamma event, the amplifier will or will not, respectively, provide a neutron output signal  965 . One skilled in the art will appreciate that the logic requirements that define the presence or absence of a competing event will determine the logic tree for a given scenario, including the joint probability of the sensors in terms of false alarms and tagging of events, etc. 
         [0110]    Returning to  FIG. 9 , an example of a passive modality is shown that can improve the consistency and reliability of a neutron detector over time. In this example, a passive layer  940  is monolithically deposited on the detector module, upstream of the detector and possible active discrimination sensors. The function of this passive layer is to perform as a sacrificial component of the overall detector. It is well-known that deleterious radiation incident onto a detector can, over time, degrade its performance. An example of such a degradation mechanism results from the formation of color centers was well as crystalline and structural defects due to external radiation. These damage sites can compromise the efficiency, sensitivity and signal-to-noise attributed of a given detector. By placing a passive layer  940  upstream of the detector, the occurrence of damaging radiation in the active detector can be reduced, since, in such cases, there is a finite probability that the damaging radiation effects will be more confined to the sacrificial layer. The number of defects in a passive layer instead of in the active detector will maintain the performance metrics of the detector significantly over time relative to exposing the detector directly to the radiation. One skilled in the art will appreciate the systems tradeoffs of such sacrificial layers in terms of detector lifetime on the one hand, and, sensitivity and efficiency on the other hand. 
         [0111]    The foregoing description of the invention has been presented for purposes of illustration and description and is not intended to be exhaustive or to limit the invention to the precise form disclosed. Many modifications and variations are possible in light of the above teaching. The embodiments disclosed were meant only to explain the principles of the invention and its practical application to thereby enable others skilled in the art to best use the invention in various embodiments and with various modifications suited to the particular use contemplated. The scope of the invention is to be defined by the following claims.