Abstract:
An adhesive for a rubber compound, comprising a water-in-oil emulsion containing a rubber, carbon black, a zinc compound, a tackifier, an organic solvent, a nonionic surfactant and water.

Description:
FIELD OF THE INVENTION 
     The present invention relates to an adhesive for rubber compounds, and more particularly to an adhesive for rubber goods such as tires, retreaded tires, hoses, belt conveyors and footwear, where the goods manufactured by adhesion processes of adhering unvulcanized rubber compounds, or an unvulcanized rubber compound and a vulcanized rubber compound together and vulcanizing them. 
     The adhesive functions as a pressure sensitive adhesive and vulcanizing adhesive which makes the sticking process easier and adhesion after vulcanization stronger. 
     BACKGROUND OF THE INVENTION 
     Adhesives which are solutions of rubber compounds in organic solvents having a boiling point of at most about 150° C. are used presently in adhesion processes of adhering unvulcanized rubber compounds, or an unvulcanized rubber compound and a vulcanized rubber compound together. 
     Recently, reductions in organic solvent emissions from adhesives have been investigated from the standpoint of industrial hygiene, prevention of disasters and conservation of oil resources. Attempts have been made not to use organic solvents, to decrease the content of organic solvents by using highly concentrated adhesives and to decrease the area of application of adhesives to the surfaces of rubber compounds by improving the formulation of rubber compounds. However, these attempts have been unsatisfactory in achieving low levels of organic solvents emission without adhesion difficulties. Therefore, it is of urgent necessity to achieve a new adhesive having good adhesion strength and with a low organic solvent content. 
     Oligomer type adhesives do not provide sufficient adhesiveness and good adhesion after vulcanization. 
     Latex type adhesives and oil-in-water type adhesives are water-based adhesives, and have such poor wettability to rubber compounds that sufficient tackiness cannot be obtained. Moreover, it is very difficult to remove water of the adhesives from the surface of the rubber compound and the adhesion after vulcanization is deteriorated due to the water present. 
     It is known that water-in-oil type adhesives have low organic solvent content and good wettability to rubber compounds and dispersed water particles of the adhesives so easily cohere due to mechanical stimuli such as supersonic waves that it is easy to remove water of the adhesives from the surface of rubber compounds. 
     European Patent Application No. 83305211.1 (corresponding to U.S. patent application Ser. No. 415,496 filed Sept. 7, 1982, now abandoned) discloses a tire tread adhesive comprising a water-in-oil emulsion with an organic solvent solution of a vulcanizable rubber compound as its oil phase. However, it is difficult to manufacture a stable water-in-oil emulsion because of the necessity to disperse water particles measuring several microns in diameter into the oil phase containing a rubber compound comprising a rubber and carbon black. 
     SUMMARY OF THE INVENTION 
     An object of the present invention is to provide a water-in-oil emulsion type adhesive which has the same tackiness and adhesion fatigue after vulcanization as an organic solvent solution type adhesive, which has a low organic solvent content and where water can be easily removed from the surfaces of rubber compounds. 
     The present invention, thus, provides an adhesive for rubber compounds comprising a water-in-oil emulsion containing 
     (a) 100 parts by weight of a rubber selected from the group consisting of natural rubber, polyisoprene rubber, polybutadiene rubber, styrene-butadiene rubber (e.g., about 5 to 45 wt% styrene, and about 55 to 95 wt% butadiene), isobutylene-isoprene rubber (e.g., about 99 to 96 wt% isobutylene and about 1 to 4 wt% isoprene) and halogenated (e.g., chlorinated or brominated) isobutylene-isoprene rubber, 
     (b) at least about 30 parts by weight of a carbon black having an iodine adsorption value (ASTM D 1510) of at least about 40 mg/g, 
     (c) at least about 0.5 parts by weight, on an elemental zinc basis, of a zinc compound, 
     (d) about 3 to about 30 parts by weight of a tackifier having an average molecular weight of between about 1,000 to about 10,000, 
     (e) at least about 100 parts by weight of an organic solvent having a boiling point of at most about 150° C., 
     (f) at least about 2 parts by weight of a non-ionic surfactant having an HLB value of more than about 2.0 and less than about 8.0 and 
     (g) water at most about three times the volume of said rubber, said carbon black, said zinc compound, said tackifier, said organic solvent and said surfactant. 
    
    
     BRIEF DESCRIPTION OF THE ACCOMPANYING DRAWING 
     The FIGURE is a sectional view of a tire for a passenger car. The dotted lines denote the region where the adhesives tested were applied. 
    
    
     DETAILED DESCRIPTION OF THE INVENTION 
     In the present invention, at least about 30 parts by weight of a carbon black having an iodine adsorption value of between about 40 mg/g to about 150 mg/g is added to the adhesive, based on 100 parts by weight of the rubber component, in order to achieve a good adhesion fatigue property for the adhesive. Examples of commercially available carbon black which have an iodine adsorption value of at least about 40 mg/g are Seast SO (trademark for a FEF made by Tokai Carbon Black Company), Diablack H (trademark for a HAF made by Mitsubishi Chemical Industries), Continex ISAF (trademark for an ISAF made by Mitsui Toatsu Kagaku Co.) and Diablack A (trademark for a SAF made by Mitsubishi Chemical Industries). 
     It is preferred for the carbon black to have an iodine adsorption value of at least about 80 mg/g and for about 40 to about 90 parts by weight of the carbon black to be added to the adhesive composition, based on 100 parts by weight of the rubber component. 
     Zinc compounds are present in an amount of at least about 0.5 parts by weight, on an elemental zinc basis, to complete the vulcanizing reactions in the layer of the adhesive and achieve the good adhesion fatigue property of the adhesion. When one of the rubber compounds which should be adhered is capable of sulfur vulcanization, a certain amount of sulfur, accelerator and stearic acid migrates from the rubber compound to the layer of the adhesive before vulcanization. Therefore, sulfur, accelerators and stearic acid do not need to be added to the adhesive. However, zinc compounds such as zinc white, zinc carbonate, and zinc stearate should be added to the adhesive to complete the vulcanization because they migrate with difficulty. 
     It is preferred that zinc compounds be present in the adhesive in an amount of 1.0 to 2.5 parts by zinc weight based on 100 parts by weight of the rubber component. 
     It is necessary to add a tackifier having an average molecular weight of between about 1,000 to about 10,000 such as Lewisol 29-JA (trade name for an alkylphenol resin made by Hercules Inc.), Tackirol 101 (trade name for an alkylphenol resin made by Sumitomo Chemical Industries Co.), Petorsin (trade name for a petroleum hydrocarbon resin made by Mitsui Petrochemical Co.), and Koresin (trade name for a p-tert-butylphenol-acetylene resin made by Badische Anilin and Soda-Fabrik Co.) to the adhesive in order to improve the tackiness of the adhesive by decreasing the viscosity of the adhesive and increasing the contact area under pressure. Good tackiness is not achieved with use of less than about 3 parts by weight of the tackifier while the mechanical fatigue property of the adhesive after vulcanization is decreased with the use of more than about 30 parts by weight of the tackifier. 
     An organic solvent having a boiling point of at most about 150° C. such as toluene, xylene, n-hexane, n-heptane, cyclohexane and gasolines (for example, LA Gasoline, A Solvent and K Solvent made by Japan Petroleum Co.) is used in order that the organic solvent is evaporated easily from the layer of the adhesive. It is preferred to use about 200 to about 400 parts by weight of the organic solvent. 
     The HLB value of the non-ionic surfactant range from more than about 2.0 to less than about 8.0 and also the amount of the surfactant is at least about 2.0 parts by weight. The tackiness of the adhesive is not sufficient when the HLB value of the non-ionic surfactant is not more than about 2.0, while it is difficult to emulsify the adhesive when the HLB value of the non-ionic surfactant is not less than about 8.0 or the amount of the non-ionic surfactant is less than about 2.0 parts by weight. It is preferred to use about 3.0 to about 7.0 parts by weight of the non-ionic surfactant and for water to be present in an amount of about 2 to about 3 times the volume of the rubber, the carbon black, the zinc compound, the tackifier, the organic solvent and the non-ionic surfactant. The HLB value of the surfactant is evaluated using the Atlas HLB System. 
     Examples of suitable non-ionic surfactants include sorbitan stearate, propyleneglycol monostearate, sorbitan monooleate, diethyleneglycol monostearate, sorbitan monopalmitate, sorbitan tristearate, propyleneglycol monolaurate, sorbitan monostearate, sorbitan sesquioleate, sorbitan tristearate, propyleneglycol monostearate, glycol monostearate, propyleneglycol monolaurate, diethyleneglycol monostearate, glycerol monostearate and diethyleneglycol monolaurate. 
     A larger amount of the bound rubber of the adhesive improves the adhesion fatigue property. Therefore, it is preferred to mix carbon black with a rubber at a temperature above about 120° C. for more than about 30 seconds in the mixing of the rubber compounds and the adhesive. Better results are obtained by using an adhesive having a bound rubber of at least about 20%. 
     The adhesive according to the present invention may also contain vulcanizing agents (such as sulfur, sulfur chloride and alkylphenoldisulfide), accelerating agents (such as dibenzothiazyldisulfide, N,N&#39;-dicyclohexyl-2-benzothiazolysulfenamide, N,-oxydiethylene-2-benzothiazole sulfenamide and diphenylguanidine), activators (such as stearic acid and oleic acid), and the like, as needed or desired. 
     The following examples are given for the purpose of further illustration of the present invention. They are not to be construed, however, as limiting the scope of the present invention. Unless otherwise indicated herein, all parts, percents, ratios and the like are by weight. 
     EXAMPLES 1 TO 7, COMPARATIVE EXAMPLES 1 TO 5 
     Each of twelve different adhesives were prepared as follows: 
     Natural rubber (100 parts by weight) was added to 400 parts by weight of gasoline. After 24 hours, 40 parts by weight of carbon black HAF, 5.0 parts by weight of a tackifier (alkylphenol resin, Tackirol 101 made by Sumitomo Chemical Industries Co.), 2.0 parts by weight of stearic acid, 3.0 parts by weight of zinc white, 2.0 parts by weight of sulfur and 1.0 parts by weight of an accelerating agent (N,-oxydiethylene-2-benzothiazole sulfenamide, Nocceler MSA.F made by Ouchishinko Chemical Co.) were added to the solution of natural rubber in gasoline. Then, the solution was homogenized by stirring at 2,000 rpm and a clearance of 4 mm using a table top homogenizer made by Nippon Seiki Manufacturing Co. for 3 minutes. 
     The homogenized solution was stirred again for 2 minutes after the surfactant was added to the solution. Distilled water (2,000 parts by weight) was added to the solution and the solution was stirred in the condition of 3,000 rpm and a clearance of 2 mm for 20 minutes. The emulsification characteristics were evaluated. The tackiness and the adhesion fatigue of the emulsified adhesive to the rubber compound (a tire tread compound) as shown in Table 1 was evaluated. The results obtained for each and the composition of the 12 adhesives are shown in Table 1 below. 
     
                       TABLE 1______________________________________Component            Parts By Weight______________________________________NR (RSS #4)          70.0SBR 1500             30.0Carbon Black HAF     60.0Cumarone-Indene Resin*                5.0Petroleum Softener (Aromatic Oil)                10.0Zinc White           5.0Stearic Acid         3.0N--Phenyl-N&#39;--isopropyl-p-                1.0phenylenediamineDiphenylguanidine    0.1N,--oxydiethylene-2-Benzothiazolylsulfenamide                0.7Sulfur               1.8______________________________________ *Cumarone CL made by Chisso Petrochemicals Co. 
    
     The test methods used for evaluation were as follows: 
     1. Water-in-Oil Type Emulsibility 
     After an adhesive was stirred and stood for 24 hours, an adhesive with phase separation (oil phase and water phase separated) was evaluated as &#34;No&#34; and an adhesive where phase separation did not occur was evaluated as &#34;Good&#34;. 
     2. Tackiness 
     An adhesive was applied to a 2 mm sheet of the rubber compound as shown in Table 1 above in an amount of 2 g per 100 cm 2   based on the dried adhesive after evaporation of water and solvent in the adhesive, and made visually uniform on the sheet with a spatula. The sample was tested after allowing it to stand for 4-5 hours and evaluated by measuring the tacking force when pressed for 20 seconds at a weight of 500 g with a Picma Type Tackiness Meter made by Toyo Seiki Co. The result was estimated by the arithmetic mean of ten times the values of the measurements. 
     3. Adhesion Fatigue 
     An adhesive was applied to the surfaces of sheets 5.2 mm thick of the rubber compound as shown in Table 1 above in the same manner for measurements of tackiness. After standing, the sheets were adhered together and cured in a mold of 10 mm thick at 150° C. for 40 minutes. The sample, consisting of the two cured sheets, was cut to a size of 25 mm wide, 150 mm long and 10 mm thick. After a center portion, 20 mm long, of the cured sheet was subjected to two repeated extension fatigue tests, which comprise stretching from 20 mm long to 40 mm long (100% elongation), and from 20 mm long to 60 mm long (200% elongation) by 100 times, 1,000 times and 5,000 times at a speed of 500 mm/min. with an Instron Tensile Tester, the adhesion fatigue was evaluated using a peeling test at 180° at a rate of 500 mm/min. When the sample was destroyed at the adhesive layers, the adhesive fatigue property was evaluated as &#34;Bad&#34;. When the sample was destroyed at the rubber compound (the tire tread compound), the adhesive was evaluated as &#34;Good&#34;. 
     
         TABLE 2  Comp.      Comp. Comp. Comp.   Comp. Ex. Ex. Ex. Ex. Ex. Ex. Ex. Ex. Ex. Ex. Ex. Ex. 1 1 2 3 4 5 2 3 4 6 7 5*   NATURAL RUBBER 100 100 100 100 100 100 100 100 100 100 100 100 (RSS #4) GASOLINE 400 400 400 400 400 400 400 400 400 400 400 2400  CARBON BLACK HAF  40  40  40  40  40  40  40  40  40  40  40  40 TACKIROL 101 5.0 5.0 5.0 5.0 5.0 5.0 5.0 5.0 5.0 5.0 5.0 5.0 STEARIC ACID 2.0 2.0 2.0 2.0 2.0 2.0 2.0 2.0 2.0 2.0 2.0 2.0 ZINC WHITE 3.0 3.0 3.0 3.0 3.0 3.0 3.0 3.0 3.0 3.0 3.0 3.0 N,--OXYDIETHYLENE- 1.0 1.0 1.0 1.0 1.0 1.0 1.0 1.0 1.0 1.0 1.0 1.0 2-BENZOTHIAZOLE SULFENAMIDE SULFUR 2.0 2.0 2.0 2.0 2.0 2.0 2.0 2.0 2.0 2.0 2.0 2.0 SORBITAN 5.0 -- -- -- -- -- -- -- -- -- -- -- TETRASTEARATE (1.5)** SORBITAN -- 5.0 -- -- -- -- -- -- -- -- -- -- TRISTEARATE (2.1) PROPYLENEGLYCOL -- -- 5.0 -- -- -- -- -- -- -- -- -- MONOSTEARATE (3.4) SORBITAN -- -- -- 5.0 -- -- -- -- -- -- -- -- MONOSTEARATE (4.3) DIETHYLENEGLYCOL -- -- -- -- 5.0 -- -- 1.0 1.5 20.0 -- -- MONOSTEARATE (4.7) SORBITAN -- -- -- -- -- 5.0 -- -- -- -- -- -- MONOPALMITATE (6.7) SORBITAN -- -- -- -- -- -- 5.0 -- -- -- -- -- MONOLAURATE (8.6) POLYOXYETHYLENE -- -- -- -- -- -- -- 5.0 -- -- -- -- SORBITAN MONOOLEATE (10.0) WATER 2000  2000  2000  2000  2000  2000 2000  2000  2000  2000  2000   0 WATER-IN-OIL GOOD GOOD GOOD GOOD GOOD GOOD NO NO NO GOOD GOOD / TYPE EMULSIBILITY TACKINESS (g) 630 840 790 830 760 890 / / / 850 1100  970 ADHESION 100% ELONG. BAD GOOD GOOD GOOD GOOD GOOD / / / GOOD GOOD GOOD FATIGUE 100 TIMES  100 ELONG. BAD GOOD GOOD GOOD GOOD GOOD / / / GOOD GOOD GOOD  1000 TIMES *A conventional organic solvent solution type adhesive. **HLB value. 
    
     EXAMPLES 8 TO 13 
     Six different adhesives were prepared and the tackiness and the adhesion fatigue properties were evaluated. Their formulation was the same as in Example 6. In these examples, natural rubber was mixed with carbon black HAF in an OOC type Banbury mixer before preparing the adhesives in order to increase the amount of bound rubber present. The elapsed times at above 120° C. in the mixer and the amounts of bound rubber of the adhesives are shown in Table 3. 
     Amount of Bound Rubber 
     An adhesive was applied to a sheet of glass and after water and organic solvent of the adhesive were removed from the adhesive, the adhesive was allowed to stand for 24 hours. About 0.3 g of the dried adhesive was weighed precisely, placed in a small container made of a wire net of 100 mesh and soaked in 200 cc of toluene for 48 hours. After allowing such to stand open in a room for 3 hours to remove the toluene, the sample was dried under vacuum for one hour and then weighed precisely. 
     The amount of bound rubber was obtained using the following formula: ##EQU1## 
     
                                           TABLE 3__________________________________________________________________________           Ex. Ex. Ex. Ex. Ex. Ex.           8   9   10  11  12  13__________________________________________________________________________Adhesive Composition           Same as Example 6Elapsed Time at Above            0   5  20  30  40  60120° C. when RubberMixed with Carbon Black(Seconds)Amount of       12  14  14  20  22  21Bound Rubber (%)Tackiness (g)   920 960 1010                       1080                           980 1040ADHESION  100% Elongation           Good               Good                   Good                       Good                           Good                               Good  1.000 Times  200% Elongation           Bad Bad Bad Good                           Good                               Good  5.000 Times__________________________________________________________________________ 
    
     EXAMPLES 14 TO 23, COMPARATIVE EXAMPLES 6 TO 14 
     Nineteen different adhesives were prepared as shown in Table 4 below. Rubber, carbon black, tackifier, heavy aromatic oil and activator such as stearic acid, zinc white and zinc stearate were mixed together in an OOC type Banbury mixer at above 120° C. for 40 to 60 seconds and then compounds were added to gasoline and the solution was homogenized by stirring sulfur and an accelerator as indicated in Table 4 below. The adhesives were prepared in the same way as described in Examples 1 to 7. 
     The tackiness and the adhesion fatigue were evaluated and the results obtained are shown in Table 4 below. 
     In Table 4, the iodine adsorption values of the carbon blacks were as follows: 
     
         ______________________________________Carbon Black   IA (mg/g)______________________________________GPF            36FEF            42HAF            82______________________________________ 
    
     In Table 4, the average molecular weight of the tackifiers was as follows: 
     
         ______________________________________Tackifier    Average Molecular Weight______________________________________Lewisol 28-JA        3,000Tackirol 101 5,000______________________________________ 
    
     Comparative Example 13 in Table 4 is a conventional organic solvent solution type adhesive. 
     
                                           TABLE 4__________________________________________________________________________                  Comparative                 Comparative       Example    Example    Example          Example                                                     Example       No.        No.        No.              No.    No.       14    15   6     7    16    17   18    8      19__________________________________________________________________________Natural Rubber       100    20  100   100  100   100  100   100    100(RSS #4)SRB 1500    --     80  --    --   --    --   --    --     --Carbon Black GPF       --    --    50   --   --    --   --    --     --Carbon Black FEF       --    --   --     25   30    50  --    --     --Carbon Black HAF        50    50  --    --   --    --    50    50     50Petroleum Softener        10    10   10    10   10    10   40   --     --(Heavy Aromatic Oil)Lewisol 28-JA       --    --   --    --   --    --   --     40     30Tackirol 101        5     5    5     5     5    5    5     5      5Stearic Acid       2.0   2.0  2.0   2.0  2.0   2.0  2.0   2.0    2.0Zinc White  3.0   3.0  3.0   3.0  3.0   3.0  3.0   3.0    3.0Zinc Stearate        0     0    0     0    0     0    0     0      0Amount of Zinc       2.4   2.4  2.4   2.4  2.4   2.4  2.4   2.4    2.4(Elemental)N,--Oxydiethylene-2-       1.0   1.0  1.0   1.0  1.0   1.0  1.0   1.0    1.0benzothiazolesulfenamideSulfur      2.0   2.0  2.0   2.0  2.0   2.0  2.0   2.0    2.0Gasoline    500   500  500   500  500   500  500   500    500Water       2000  2000 2000  2000 2000  2000 2000  2000   2000Sorbitan Monostearate       5.0   5.0  5.0   5.0  5.0   5.0  5.0   5.0    5.0Tackiness (g)       960   640  1120  1030 1010  970  780   more   1340                                              than                                              1500Adhesion100% Elong.       GOOD  GOOD GOOD  GOOD GOOD  GOOD GOOD  BAD    GOODFatigue1000 Times100% Elong.       GOOD  GOOD BAD   BAD  GOOD  GOOD GOOD  --     BAD5000 Times__________________________________________________________________________                 Comparative        Comparative Comparative       Example   Example  Example   Example                                           Example                                                Example       No.       No.      No.       No.    No.  No.       20   21   9   10   22   23   11     24   12   13__________________________________________________________________________Natural Rubber       100  100  100 100  100  100  100    100  100  100(RSS #4)SRB 1500    --   --   --  --   --   --   --     --   --   --Carbon Black GPF       --   --   --  --   --   --   --     --   --   --Carbon Black FEF       --   --   --  --   --   --   --     --   --   --Carbon Black HAF        50   50   50  50   50   50   50     50   50   50Petroleum Softener       --   --   --   10   10   10   10     10   10   10(Heavy Aromatic Oil)Lewisol 28-JA       --   --   --  --   --   --   --     --   --   --Tackirol 101        20   30   40  5    5    5    5      5    5   --Stearic Acid       2.0  2.0  2.0 --   --   --   --     --   --   2.0Zinc White  3.0  3.0  3.0 --   3.0  1.0  0.5    --   --   3.0Zinc Stearate        0    0    0   0    0    0    0     6.0  3.0   0Amount of Zinc       2.4  2.4  2.4  0   2.4  0.8  0.4    0.6  0.3  2.4(Elemental)N,--Oxydiethylene-2-       1.0  1.0  1.0                                 1.0benzothiazolesulfenamideSulfur      2.0  2.0  2.0                                 2.0Gasoline    500  500  500 500  500  500  500    500  500  1500Water       2000 2000 2000                     2000 2000 2000 2000   2000 2000Sorbitan Monostearate       5.0  5.0  5.0 5.0  5.0  5.0  5.0    5.0  5.0Tackiness (g)       1200 more more                     1060 980  1110 1020   1050 990  1040            than than            1500 1500Adhesion100% Elong.       GOOD GOOD BAD GOOD GOOD GOOD GOOD   GOOD GOOD GOODFatigue1000 Times100% Elong.       GOOD GOOD --  BAD  GOOD GOOD BAD    GOOD BAD  GOOD5000 Times__________________________________________________________________________ 
    
     The adhesives, of Comparative Examples 6, 9 and 13 and Examples 17 and 22 in Table 4, were employed as adhesives for test tires for passenger cars (size: 175 SR14), respectively. The amount of the adhesive used was 2 g per 100 cm 2  based on the completely dried adhesive. The adhesives were applied to the splice and superposing portions corresponding to the dotted lines in the FIGURE showing test tires for passenger cars. 
     The durability of the test tires was evaluated by running without a break and with an inner pressure of 1.70 Kg/cm 2  under a load of 675 Kg at a speed of 60 Km/Hr for 500 hours on a drum with an outer diameter of 1.7 m. 
     The results obtained are shown in Table 5 below. The results in Table 5 shows that the adhesives of Examples 17 and 22 in the present invention have the same durability as the conventional organic solution type adhesive of Comparative Example 13. 
     The tires using the adhesives of Comparative Examples 6 and 9 were deformed and destroyed during the running. The tires were checked precisely in the deformed portions and the layers of the adhesive were found to be broken. 
     
                                           TABLE 5__________________________________________________________________________    Tire No.                    3      4      5    1       2       Comparative                           Comparative                                  ComparativeAdhesive Applied    Example 17            Example 22                    Example 6                           Example 9                                  Example 13__________________________________________________________________________Durability of    No breakdown            No breakdown                    Breakdown                           Breakdown                                  No breakdownTire     after lapse            after lapse                    after lapse                           after lapse                                  after lapse    of 500 hours            of 500 hours                    of 380 hours                           of 240 hours                                  of 500 hours__________________________________________________________________________ 
    
     As explained above in the Examples and Comparative Examples, the present invention provides a novel and advantageous adhesive which improves industrial hygiene and conserves oil resources and maintains almost the same tackiness and adhesion fatigue as a conventional organic solvent solution type adhesion. 
     The adhesive of the present invention is useful as an adhesive for, e.g., tires, belt conveyors and other rubber goods. 
     While the invention has been described in detail and with reference to specific embodiments thereof, it will be apparent to one skilled in the art that various changes and modifications can be made without departing from the spirit and scope thereof.