Abstract:
A process for recovering bitumen from oil-in-water (O/W) emulsions is disclosed wherein water soluble demulsifiers are used. These demulsifiers are polyureas of average molecular weight greater than about 5,000 prepared by the reaction between a polyisocyanate and a polyoxyalkylenediamine. To resolve the bituminous petroleum emulsions, the process is carried out between 25° and 160° C. wherein the demulsifier of the invention is contacted with the bituminous emulsion.

Description:
BACKGROUND OF THE INVENTION 
     1. Field of the Invention 
     This invention is concerned with the breaking or resolution of oil-in-water (O/W) bituminous emulsions by treatment with polyureas. 
     2. Description of the Prior Art 
     A great volume of hydrocarbons exist in known deposits of tar sands. These deposits occur at various places, the Athabasca tar sands in Canada being an example. The petroleum in a tar sand deposit is an asphaltic bitumen of a highly viscous nature ranging from a liquid to a semisolid. These bituminous hydrocarbons are usually characterized by being very viscous or even non-flowable under reservoir conditions by the application of driving fluid pressure. 
     Where surface mining is not feasible, the bitumen must be recovered by rendering the tar material mobile in-situ and producing it through a well penetrating the tar sand deposit. These in-situ methods of recovery include thermal, both steam and in-situ combustion and solvent techniques. Where steam or hot water methods are used, a problem results which aggravates the recovery of the bitumen. The difficulty encountered is emulsions produced by the in-situ operations. These emulsions are highly stable O/W emulsions which are made even more stable by the usual presence of clays. Most liquid petroleum emulsions are water-in-oil (W/O) types. These normal W/O emulsions are broken by methods known in the art. However, the bitumen emulsions which are O/W types present a much different problem, and the same demulsifiers used in W/O emulsions will not resolve the O/W bitumen emulsions. The uniqueness of these O/W bitumen emulsions is described in C. W. W. Gewers, J. Canad. Petrol. Tech., 7(2), 85-90 (1968). (Prior art Reference A.) There is much prior art concerning the resolution of normal W/O emulsions. Some of the art even mistakenly equates bitumen O/W emulsions with these W/O emulsions. The following is a list of several art references. 
     B. British Pat. No. 1,213,392 discloses a polyurethane for breaking W/O emulsions. 
     C. British Pat. No. 1,112,908 discloses the use of polyurethanes to break W/O emulsions. Even in a discussion of prior art, this British Patent discusses hydrophilic polyurethanes and indicates that they are ineffective for breaking emulsions. 
     D. U.S. Pat. No. 3,594,393 is also concerned with breaking W/O emulsions with polyurethanes. 
     E. U.S. Pat. No. 3,640,894 discloses polyurethanes and polyurethanes used in combination with Novolak alkoxylates to break W/O emulsions. 
     F. U.S. application Ser. No. 152,453 filed May 22, 1980, now allowed, claims a process for recovering petroleum from bitumen emulsions by demulsifying the emulsions with the reaction product of a polyisocyanate and diols and triols wherein the resulting polyurethane is greater than about 8,000 molecular weight. 
     It is an object of the present invention to provide a method whereby O/W bitumen emulsions may be broken by treatment with a class of polyureas. 
     SUMMARY OF THE INVENTION 
     The invention is a method for recovering petroleum from O/W bitumen emulsions by resolving or breaking these emulsions by contacting the emulsions at a temperature of from between about 25° and 160° C. with a polyurea prepared by the reaction under appropriate conditions of temperature and catalysis of a polyisocyanate and a diamine or mixture of diamines containing alkyleneoxy units having the general structure ##STR1## where m is from 0 to 30 and n is from 0 to 5 and wherein the polyurea contains at least 70% by weight ethyleneoxy units and wherein the polyurea has an average molecular weight equal to or greater than about 5,000. 
     DESCRIPTION OF THE PREFERRED EMBODIMENTS 
     The process of this invention utilizing the chemical demulsifier as described above utilizes as a chemical demulsifier a particular polyurea. 
     Especially useful and preferred in this process are polyureas prepared by reaction under appropriate conditions of temperature and (optionally) catalysis of the following two components: (a) a polyisocyanate, especially diisocyanate such as TDI or MDI of molecular weight under 500, and (b) a diamine containing alkyleneoxy units having the general structure. ##STR2## wherein m is from 10 to 22 and n is from 0 to 1.5. The polyureas useful in this invention have an average molecular weight equal to or greater than about 5,000. Especially useful as the diamine containing alkyleneoxy component of the polyurea are the JEFFAMINE® ED series polyoxyalkylenepolyamines from Texaco Chemical Company prepared by reductive amination of an appropriate diol. An especially useful JEFFAMINE polyoxyalkylenediamine has a structure as above wherein m is 20.9 and n is 0.75. The relative values of m and n and the weight ratios of the diisocyanate and the diamines must be adjusted so that the final polyurea has a weight percent ethyleneoxy content of about 70% or greater. Mixtures of different polyoxyalkylenediamines may also be used. For example, the hydrophilicity of the demulsifier may be adjusted by one skilled in the art to maximize effectiveness on a particular emulsion. This may be done by adjusting the values of m and n in the product or by blending different products. 
     The produced bitumen emulsions may be treated by the process of our invention in a conventional manner, for example, in a conventional horizontal treater operated, for example, from about 25° to 160° C. and, preferably, from about 50°-150° C. at autogenous pressures. The concentration of the chemical demulsifier described above used in treating the bitumen in water emulsions may range from about 1 to 200 parts per million and, preferably, from about 10 to 100 parts per million with the optional addition of an organic diluent and/or inorganic salt as well as standard flocculants and mechanical or electrical means of demulsification. The following examples describe more fully the present process. However, these examples are given for illustration and are not intended to limit the invention. 
    
    
     The examples which follow describe the preparation of chemical demulsifiers of the invention and the demulsification test results. 
     EXAMPLE I 
     Polyurea Demulsifier 
     A one-liter resin flask was charged with 200 grams of JEFFAMINE® ED-2001 with structure ##STR3## The starting material was dried by stirring at 0.1 mm Hg pressure at 100° C. for one-half hour. To this material was added 400 grams toluene (previously dried over 3 angstrom molecular sieves) and 0.2 grams 2,6-di-t-butyl-p-cresol. 13.5 ml toluene diisocyanate was added with stirring over a five minute period at 50° C. The reaction mixture was then stirred under nitrogen for one hour at 60° C. and two hours at 100° C. The reaction mixture was then vacuum stripped to remove solvent. The product of this reaction was found to contain 0.017 meq/g total amine and was shown to have a molecular weight of 12,600 by liquid chromatographic analysis, using poly(ehtyleneoxy)glycol standards. 
     EXAMPLE II 
     Low Molecular Weight Analog of Product of Example I 
     The general procedure of Example I was repeated using 0.5 moles toluene diisocyanate per mole of JEFFAMINE ED-2001 to obtain a product with an approximate molecular weight of 4,200 and containing 0.41 meq/g total amine. 
     EXAMPLE III 
     Mixed Poly(Urea-Urethane) 
     A one-liter resin flask was charged with 194 grams of 7,500 molecular weight poly(ethyleneoxy)glycol which was dried in vacuum at 100° C. for one-half hour. To this were added 400 grams toluene, 0.2 grams 2,6-di-t-butyl-p-cresol and 0.08 grams dibutyl tin dilaurate. To this mixture was added 6 grams JEFFAMINE® D-230 (230 molecular weight diamine prepared by reductive amination of a poly(propyleneoxy)glycol), followed by addition of 6.7 ml toluene diisocyanate at 50° C. over a six minute period. The reaction mixture was stirred under nitrogen for one hour at 50° and then two hours at 100°. Solvent was removed under reduced pressure, leaving a product of high molecular weight too insoluble in most solvents to obtain adequate analysis. 
     EXAMPLE IV 
     Polyurea from a Mixture of Diamines 
     193 Grams JEFFAMINE ED-2001 was dried as in Example I. To this were then charged 7 grams JEFFAMINE D-230, 0.2 grams 2,6-di-t-butyl-p-cresol and 300 grams dry toluene. 16.0 milliliters toluene diisocyanate was added to 50° C. over eight minutes and the mixture was digested under N 2  for one hour at 50° and two hours at 100°, adding 300 grams additional toluene to reduce solution viscosity. Solvent was removed under reduced pressure and the resulting polymer found to contain 0.01 meq/g total amine and have an average molecular weight of 6,990. 
     EXAMPLE V 
     Low Ethyleneoxy-Content Polyurea 
     Charged one-liter resin flask with 200 grams JEFFAMINE ED-900 having general structure ##STR4## and dried under reduced pressure for one-half hour at 80° C. Added 400 grams toluene and 0.2 grams 2,6-di-t-butyl-p-cresol. At 50° C. added 30.6 ml toluene diisocyanate over five minutes. Cooled reaction mixture after 35 minutes at 69-70° C. and removed solvent under reduced pressure. The product had a weight average molecular weight of 5,689 by liquid chromatographic analysis. 
     EXAMPLE VI 
     Higher Molecular Weight Analog of Product of Example IV 
     Repeated procedure of Example IV using 600 grams toluene, 16 ml toluene diisocyanate and digestion times of one hour at 60-70° C., followed by one hour at 100° C. The stripped product had a molecular weight of 13,400 and contained 0.036 meq/g total amine. 
     EXAMPLE VII 
     Mixed Poly(Urea-Urethane) from Amino Alcohol 
     A one-liter resin flask was charged with 200 grams of a product obtained by incompletely reductively aminating (34.7 mole% conversion) a diol of the general structure ##STR5## This compound was dried at 100° C. for one-half at reduced pressure. To this were charged 0.08 grams dibutyl tin dilaurate, 500 grams dry toluene and 0.2 grams 2,6-di-t-butyl-p-cresol. Then 6.2 ml toluene diisocyanate was added at 50° C. over four minutes and then mixture digested under nitrogen for one hour 50° and two and 1/4 hours at 100°. Solvent was removed under reduced pressure to leave a product containing 0.01 meq/g total amine and having a weight average molecular weight of 30,879. 
     EXAMPLE VIII 
     Demulsifier Testing of Products from Example 1-4 
     The method employed for testing the products of Examples 1-4 is as follows: 
     (a) A 1% solution of each chemical was prepared (in H 2  O or in toluene). 
     (b) 100 ml of fresh, hot bitumen emulsion of known bitumen content obtained by in-situ steam flooding in tar sand pattern located at Ft. McMurray, Alberta, Canada was poured into a sample bottle. 
     (c) 50 parts (volume) of Wizard Lake crude was added as diluent to 100 parts bitumen contained in the emulsion. 
     (d) Chemical was added to the diluted emulsion at the following concentrations: 10, 20, 30, 50, 75 and 100 ppm. 
     (e) Contents of the bottle were mixed and placed in an oven at 180-200° F. for a 24-hour period. 
     (f) BS&amp;W determinations were made on the oil layer. 
     With each emulsion, a blank was also run in which no chemical agent was introduced. Similar results were obtained from all these blanks; namely, the sample consisted of a thin upper layer consisting mainly of diluent (sometimes containing substantial water), a broad middle layer consisting of unbroken emulsion, and a small (sometimes non-existent) dark water layer containing particles or chunks of solid bitumen and clay. 
     Comparison results for no demulsifier and a poly-(ethylene oxide) demulsifier are also included. 
     EXAMPLE IX 
     Demulsifier Testing of Products from Example 5-7 
     The general method employed in testing the products of Examples 5-7 is as follows: 
     (a) A 1 wt.% solution of each chemical was prepared (in water or acetone). 
     (b) A 30 ml PYREX® test tube equipped with screw top was charged with 23 ml emulsion of 11.5 wt.% bitumen content obtained by in-situ steam flooding in tar sand pattern located at Ft. McMurray, Alberta, Canada. 
     (c) 2 ml Wizard Lake crude oil was added as diluent and the contents of the test tube were mixed. 
     (d) The contents of the test tube were equilibrated in a 80° C. oven for 1-2 hours and mixed again. 
     (e) Chemical was added to the hot, dilute emulsion at the following concentrations: 30, 60, 120 ppm. 
     (f) Contents of the test tubes were mixed, re-equilibrated in an oven at 80° C. for 1 hour and mixed again. 
     (g) After 20 hours of standing at 80° C., measurements were made on the volume of top and middle layers, and the appearance of the aqueous phase was noted. Samples of some top layers were carefully removed by pipetting and subjected to Karl Fischer analysis for determination of the water content. 
     
         __________________________________________________________________________DEMULSIFIER TESTING                Treated Emulsion          % Bitumen                % BW &amp; W in OilEx.   Candidate   in Emul-                (ppm chemical8  Demuslifier sion  used)    Middle Phase                                  Water Phase__________________________________________________________________________a  Product of Ex. 2          12-16 13 (100) Wide and unstable                                  Muddyb  Product of Ex. 3          14    6 (50)   Thick    Just translucentc  Product of Ex. 3          14    30 (100) Quite small                                  Just translucentd  POLYOX® WSR-301*          14    31 (50)  Large    Heavily cloudede  None        14    46       Moderate Dark, muddyf  Product of Ex. 1          20    4 (20)   Small    Light, muddyg  Product of Ex. 1          20    2.5 (75) None     Light, muddyh  POLYOX WSR-301*          20    4.5 (20) Moderate Light, muddyi  None        20    18       Very large                                  Brown, muddy                                  with bottom depositj  Product of Ex. 4          20    4.5 (20) Moderate Brown, muddyk  Product of Ex. 4          20    3 (100)  None     Light, muddyl  POLYOX WSR-301*          20    5 (20)   Moderate Heavily cloudedm  None        20    5        Very wide                                  Brown, muddy                                  with large bottom                                  deposit__________________________________________________________________________ *Commercial 4,000,000 molecular weight poly(ethylene Note:) Horizontal lines on left group tests run on same day and on same emulsion 
    
     
         __________________________________________________________________________DEMULSIFIER TESTINGExampleCandidate  Concentration                   Oil Phase Volume                            Emulsion Phase                                        Aqueous9    Demulsifier           ppm     in ml (% H.sub.2 O)                            Volume in ml (% H.sub.2 O)                                        Phase Appearance__________________________________________________________________________a    Product of Example 5           60      7 (59.6) 0           Muddy with solid                                        depositsb    Product of Example 5           120     3.5      3           Muddyc    Product of Example 6           60      7 (8.77) 1.5         Muddyd    Product of Example 7           60      5        3           Muddye    Product of Example 7           120     7 (86)   2           Muddyf    POLYOX WSR-301           60      7.5 (60) 0.5         Yellow, translucentg    None       --      1.5      3.5         Muddy__________________________________________________________________________