Abstract:
A porous, creep-resistant, metal-coated, LiFeO 2  ceramic electrode for fuel cells is disclosed. The electrode is particularly useful for molten carbonate fuel cells (MCFC) although it may have utilities in solid oxide fuel cells (SOFC) as well.

Description:
BACKGROUND OF THE INVENTION 
     This invention was made with Government support under DOE Contract No. DE-AC21-85MC22194 awarded by the Department of Energy, Morgantown Energy Technology Center. The Government has certain rights in this invention. 
    
    
     FIELD: 
     This invention relates to anodes for molten carbonate fuel cells. 
     STATE OF THE ART 
     The use of porous nickel sintered plaques as electrodes in molten carbonate fuel cells has been widespread. In general, these electrodes are high performance electrodes, but suffer from two pivotal problems. First of all, is the high cost of nickel and, secondly, these electrodes continue to sinter with time resulting in a loss of surface area and creep, resulting in altered dimensions, altering of pore size distribution in the plaque and concomitant loss of performance over the 50,000 hour required life of an operating cell. 
     At the anode, hydrogen in the fuel gas reacts with carbonate ions from the electrolyte to form water and carbon dioxide: 
     
         H.sub.2 +CO.sub.3.sup.= =H.sub.2 O+CO.sub.2 +2e.sup.-. 
    
     At the cathode, oxygen and carbon dioxide react to form carbonate via the overall reaction: 
     
         1/2O.sub.2 +CO.sub.2 +2e.sup.- =CO.sub.3.sup.=. 
    
     State-of-the-art molten carbonate fuel cell anodes are porous plaques prepared by sintering a physical mixture of metallic nickel and a variety of stabilizing additives in a reducing atmosphere at about 1000° C. The anode provides reaction sites for electrochemical oxidation of hydrogen in the fuel which is enhanced by increased surface area, good electronic conductivity and sufficient wetting by the carbonate electrolyte. Additional functions of the anode include: reservoir for carbonate storage required to replenish that being lost from the cell package; catalyst for the reforming and water gas shift reaction of the fuel; and as a bubble pressure barrier to prevent intermixing of fuel and oxidant if flaws develop in the electrolyte matrix. For all these functions, the pore structure and the wetting characteristics of the anode are important; and, since the fuel cell is required to endure 40,000 hours of operation, the stability of these properties must be assured. 
     Current Ni+2% to 10% Cr anodes have porosities of 60% to 70% and a mean pore size of 3 to 6 μm. As described earlier, the added chromium is converted during cell operation to LiCrO 2  which consumes carbonate and causes morphological changes in the electrode. These morphological changes of the anode cause shifts in the carbonate inventory of both the electrolyte matrix and the cathode which results in cell performance changes. In addition, this restructuring of the porous anode facilitates unwanted creep of the anode due to the applied holding forces used to maintain good cell contact and adequate gas sealing around the cell perimeter. 
     Metal-coated ceramic anodes for molten carbonate fuel cells have shown superior creep resistance and therefore have great potential for long life, stable, economical anodes. A major problem with the choice of the metal/ceramic substrate compositions is the wetting problem, leaving a weak anode. 
     An electroless metal plating process as described in U.S. Pat. Nos. 4,361,631; 4,404,267 and 4,423,122 of Iacovangelo et al., assigned to General Electric was found to result in non-uniform and incomplete metal coverage, especially on LiAlO 2  substrates. Anodes fabricated from metal coated powders were found to have inadequate strength. The main problems related to the development of metal coated ceramic anodes were shown to be related to dewetting of the metal at elevated temperatures of anode fabrication. Metal coated SrTiO 3  powders were fabricated into anodes by a process identical to that reported in the GE patents. Microstructural examination revealed that the grains of the ceramic had fused together, with the metal having dewetted from the surface of the ceramic. 
     Another problem related to the Cr-stabilized Ni anode is that during cell operation, the Cr undergoes corrosion to form LiCrO 2  through reaction with the Li 2  CO 3  -K 2  CO 3  (62-38 mol ratio) electrolyte. The metal-coated ceramic substrate anodes are expected to offer substantial advantages over the current Ni(Cr) anodes. 
     SUMMARY OF THE INVENTION 
     A creep-resistant, metal-coated, LiFeO 2  ceramic electrode for molten carbonate fuel cells (MCFC) has been developed. 
     A LiFeO 2  powder substrate, when coated with metal, especially nickel and nickel alloys, and sintered to form a porous anode, forms a creep resistant anode which does not exhibit significant dewetting problems. The metal coating adheres well to the ceramic powder and forms a continuous conduction path. The average creep of such anodes is ˜2.5-3%, which is significantly better than state-of-the-art Ni(Cr) anodes. Conceptually, by utilizing a significant volume of a low-cost ceramic substrate, problems related to sintering and morphological changes due to creep can be greatly reduced. Moreover, the absence of Cr as a stabilizer is expected to reduce corrosion/lithiation, thus allowing stable long-term performance. Cu/Ni-coated (50:50 mol ratio, 50 w/o metal loading) LiFeO 2  anodes were optimized to meet MCFC anode specifications. 
     Creep testing of the metal coated ceramic anodes was conducted. From the creep results it was determined that the predominant creep mechanism is due to particle rearrangement. The anode porosity and mean pore size had significant effect on the creep of the anode. Lower porosity and pore size consistent with performance criteria are desired to reduce creep. Lower metal loading with uniformity of coverage will result in lower creep behavior of the anode. Of the substrates evaluated, LiFeO 2  in general exhibited lower creep which was attributed to superior metal adhesion. Such Ni metal coated LiFeO 2  anodes can be also used as anodes for low temperature solid oxide fuel cells (SOFCs). 
     A critical requirement of such anodes is that the metal (Ni or Ni-Cu alloys) form a continuous film over the ceramic powder substrates thus allowing continuous electronic conduction paths. FIG. 1 shows schematically the ideal metal coated ceramic anode morphology. The thin metal layer on the ceramic particles is expected to show substantially increased creep resistance. Further advantages of this approach are that anode morphology can be better controlled by controlling the size of the ceramic (substrate) powder and the metal coating thickness. In addition, substantial cost reductions are also expected by using reduced amounts of metal and low cost ceramic substrates. 
     Suitable anode materials were prepared by coating by electroless deposition techniques 50 Ni/50 Cu on a conductive ceramic (LiFeO 2 ) substrate. 
    
    
     BRIEF DESCRIPTION OF THE DRAWINGS 
     FIG. 1 is a schematic representation of metal coated ceramic particles. 
     FIGS. 2 and 3 are photomicrographs of sintered Cu/Ni on LiFeO 2 . 
     FIGS. 4 and 5 are graphs which show creep behavior of metal. 
     FIG. 6 is a graph which illustrates the effect of temperature on the shrinkage of LiFeO 2  anodes. 
     FIG. 7 is a graph which illustrates the effect of consolidation pressure on porosity of LiFeO 2  anodes. 
     FIGS. 8(A) and 8(B) are photomicrographs of metal coated anodes. 
     FIG. 9 is a diagram of a cell package test stand. 
     FIG. 10 is a graph depicting the creep characteristics of LiFeO 2  material. 
    
    
     DETAILED DESCRIPTION OF THE INVENTION 
     A large batch of LiFeO 2  was synthesized. The powder was determined to be phase pure using XRD, and the particle size distribution and BET surface area were characterized. The powder was milled to get a mean particle size centered around 15 μm. The metal wetting characteristics were found to be favorable as compared to LiAlO 2 . An electroless Ni and Cu plating process was developed and the optimal conditions were determined. The metal coating appeared to be uniform as determined by SEM/EDXS. In a separate study, the phase stability of LiFeO 2  in a molten carbonate melt was determined. 
     Anodes were fabricated from LiFeO 2  particles with Ni, Cu or Ni/Cu alloys. The sintered anodes exhibited good mechanical properties. SEM examination of the microstructure revealed good coating of the particles with well formed necks thus confirming the observed strength of sintered anodes. Typical microstructures are shown in FIG. 2 and 3. After several fabrication trials, it was determined that moderate pressure during sintering improved the strength of the porous anode plaques. The porosity of the sintered plaques was varied by varying the compaction pressure. 
     There was much scatter to the results. Of all the tests, the Ni-Cr electrodes showed the least creep. The creep ranged from a low of 0.65% to a high of 6.18% and were the most consistent. The LiAlO 2  electrodes creep values ranged from a low of 0.96% to a high of 20.23%. The LiFeO 2  electrodes had the most scatter and creep ranged from a low of 1.46% to a high of 33.93. Summarizing the results for metal coated LiFeO 2  powder, with approximately 37% metal loading and 45% porosity an average of 4 samples indicate a creep of 3.6% at 650° C.; 100 psi. This is an improvement over state of the art materials. 
     
         ______________________________________LiFeO.sub.2 at 650° C. and 100 psi  Metal           Poro- %            # ofTest No.  Loading  PPS    sity  Creep Powder Samples______________________________________2.3.lb-10  50.49    9.0    27.63 7.11  LF-18  62.3.lb-05  37.0     6.0    48.7  4.31  LF-10  32.3.lb-05  37.0     6.0    43.42 1.45  LF-10  22.3.lb-06  37.0     6.0    44.10 2.55  LF-10  12.3.lb-06  46.5     6.0    43.8  6.31  LF-9   12.3.lb-11  43.33    N/A    40.97 32.12 LF-19  22.3.lb-11  66.0     N/A    43.07 32.20 LF-l6  5______________________________________ 
    
     The metal wetting characteristics of LiFeO 2  anode are more favorable. Thus, a better bond is to be expected between the metal and the ceramic, thereby reducing the amount of primary creep. FIGS. 4 and 5 show the general trends in the creep behavior of metal-coated LiFeO 2  anodes. Creep is relatively insensitive to both metal loading and anode porosity, indicative that once particle rearrangement occurs secondary creep mechanisms dominate the creep behavior. Creep characteristics are shown for Test #-5. The data show that a magnitude of the primary creep is less than ˜2%. Further creep is as expected for diffusion driven process. Higher anode creep is exhibited for anodes with higher means pore size and porosity. This is consistent with observations for LiAlO 2  anodes. However, the overall creep characteristics are superior for metal coated LiFeO 2  and it exhibits the potential for a viable alternate anode material. 
     Metal-coated LiFeO 2  anodes show great potential as a creep resistant anode. Further improvements in both metal adhesion as well as anode morphology are anticipated which could lead to reduced primary creep and thus enhance creep resistance. These anodes generally meet the functions of the molten carbonate fuel cell anode which are: 
     Provide reaction sites for electrochemical oxidation of the fuel gas 
     Act as fuel reforming catalyst 
     Serve as reservoir for storage of electrolyte for carbonate management of the cell package 
     Act as a bubble pressure barrier when fabricated as a dual porosity structure. 
     To perform these functions, the anode must have: 
     High exchange current density 
     Good electrocatalytic activity 
     Good electrical conductivity 
     Low oxidation potential 
     Good wetting characteristics to hold carbonate 
     High catalytic activity towards fuel reforming reactions 
     Appropriate porosity and pore size distribution 
     Good mechanical strength 
     Sufficient thickness to store the carbonate requirements of life. 
     
                       TABLE 3______________________________________ANODE STRUCTURE TRADEOFFSGoal            Desired Structure______________________________________Strength and Dimensional           1.    Low PorosityStability       2.    Small PoresLow Polarization           1.    Large Pores for Fuel                 Access           2.    Large Surface Area → Small                 ParticlesCarbonate Reservoir           1.    Some Pores Larger than                 Electrolyte Matrix Pores           2.    Thick layer           3.    High Porosity           4.    Large Population of Small                 PoresReforming Catalyst           1.    Large Surface Area______________________________________ 
    
     Clearly, the optimum anode structure with respect to a specified electrolyte and cathode structures must be determined on a &#34;case-by-case&#34; basis for each candidate anode type/structure. The metal coated LiFeO 2  anode materials possess, generally, the desired characteristics for good anode materials. 
     LiFeO 2  Synthesis 
     LiFeO 2  powder was synthesized using the following procedure: Li 2  CO 3  and Fe 3  O 4  were mixed in stoichiometric proportions and ball milled for 12-14 hours in ethanol. The mixture was then dried and calcined in a crucible in air at 1200° C. for 10 hours. The resulting agglomerated powder was ball milled for 2 hours and recalcined at 1200° C. for 10 hours to insure complete reaction and homogeneity. The synthesized powder was characterized by XRD to confirm the LiFeO 2  phase. 
     Among the two large (˜1 kg) batches of LiFeO 2  synthesized the first batch was found to be a mixture of alpha-LiFeO 2  and alpha LiFe 5  O 8  ; the Li deficient phase, alpha-LiFe 5  O 8 , results from a loss of lithia during calcination/reactive-sintering cycles during synthesis. The second batch was synthesized in an effort to achieve a single phase of LiFeO 2 . During the sintering cycles some Li 2  CO 3  was sprinkled on top of the powder to maintain a high Li activity over the powder mass, in order to avoid the loss of lithia. The top layer of the powder was discarded and the rest of the powder was milled to break up agglomerates and then characterized by XRD. This powder was characterized to be single phase alpha-LiFeO 2 . 
     Sintering Trials on Cu/Ni Coated LiFeO 2   
     The past efforts were centered principally on pressureless sintering of metal coating ceramic powders and prepressing at various pressures followed by pressureless sintering. SEM examination of the sintered anodes showed that while the particles were of the approximate size range compatible with achieving the desired anode specifications, the packing of the particles was not optimal. A &#34;honeycomb&#34; type structure was formed due to interparticle necking of the metal deposits. This resulted in large agglomerates with large open pores. 
     Efforts were centered around adding binders to the metal coating ceramic powders and prepressing them to different pressures. In addition to these trialst two more trials were conducted using a magnetic field to align the particles in the graphite die in order to obtain better and more uniform particle packing. The parameters are tabulated in Table I. 
     These samples were analyzed to determine if there was any trend or relationship between fabrication conditions and the resulting density and mean pore size (MPS). A porosity of 50 to 60% with a mean pore size of 35 μm are desired. 
     Variations in the thickness of the plaques of 5-8 mils were observed. Generally, the samples were thinnest at the center and thickest at the edges. The variations in plaque thickness may be a source of density gradients within the samples. 
     
                       TABLE I______________________________________Sintering Variations or Anode Fabrication TrialsSample Code     Sample ID   Sintering Conditions______________________________________31        5NF140      0.2 w/o PVB in acetone; 250                 psi (consolidation                 pressure; 126 g.load;                 gravity sintering.32        5NF140      (LiFeO.sub.2 with 0.5 w/o                 Elvacite) 250 psi                 consolidation pressure; 126                 g.load; &#34;pressureless&#34;                 sintering33        5NF142      vibratory packing in mag.                 field; 100 psi                 consolidation pressure; hot                 press T = 925° C., 1000 psi.34        5NF142      vibratory packing in mag.                 field; 100 psi                 consolidation pressure; 126                 g.load; pressureless                 sintering (T = 925° C.).______________________________________ 
    
     A total of 11 different anode specimens were fabricated and the processing conditions are listed in Table II. 
     Fabrication Characteristics of Metal-coated LiFeO 2  Powders 
     Three anode fabrication trials were conducted to determine the shrinkage and porosity characteristics of metal-coated LiFeO 2  porous compacts. The shrinkage of the LiFeO 2  anodes is considerable as compared to the LiAlO 2  anodes. As shown in FIG. 6, the mean shrinkage upon firing at 925° C. for 1 hr is 36% for a consolidation pressure of about 150 psi. The porosity of these anodes varies from approximately 48 to 54%. For anodes made at different consolidation pressures and fired at 1100° C. for 1 hr, the shrinkage varies from about 32% for a consolidation pressure of about 440 psi to a high of about 38% at 6.6 Kpsi. The porosity variation, shown in FIG. 7, is as expected with the highest porosity being exhibited by the anode fabricated at the lowest consolidation pressure. 
     Fabrication of Metal-coated LiFeO 2  Tape Cast Anodes 
     Several anodes were fabricated by tape casting metal coated LiFeO 2  powder. The resultant tapes were thin and very fragile. Four tapes were pressed together at 10,000 psi. Several anodes 1&#34; in diameter were punched from the plaque. The geometric densities (i.e., sample weight/sample volume) of the anodes were between 3.45 and 3.89 g/cc. A median pore size of 1.24 and a porosity of 46.4% was determined by the porosimetry of one of the anodes. The skeletal density obtained was 8.18 g/cc which may indicate that the powder used was composed primarily of Cu and Ni. 
     For the purpose of conducting the in-cell tests, it was necessary to fabricate the larger 4&#34;×4&#34; anodes for in-cell testing and evaluation. To this end, a large batch of LiFeO 2  powder was synthesized and metal coated. Metal-coated LiAlO 2  powder was used to cast a 8&#34; wide tape. Three large green LiAlO 2  tape blanks were cut and tested in-cell. 
     
                       TABLE II______________________________________Fabrication of Metal Coated LiFeO.sub.2 AnodesSampleNo       Processing Condition______________________________________4-1      10 μm, LiFeO.sub.2, 250 psi consolidation pressure,    126 g.dead load, T = 920° C.; 0.5 w/o binder.4-2      same as above but with ˜ 0.7 w/o binder.4-3      10 μm, LiFeO.sub.2, 100 psi consolidation pressure,    126 g.dead load, T = 920° C.4-4      same as 4-3 but with 250 psi consolidation    pressure.4-5      10 μm, vibratory milled LiFeO.sub.2.4-6      10 μm, ball milled LiFeO.sub.2.4-7      10 μm, ball milled LiFeO.sub.2, coated powder    crushed lightly in a mortar before sintering    to break up necks between particles.4-8      5 μm, ball milled LiFeO.sub.2.4-9      1 μm, vibratory milled LiFeO.sub.2.4-10     sub-1 μm, vibratory milled LiFeO.sub.2.4-11     1 μm, ball milled LiFeO.sub.2, Samples______________________________________ 4-5 thorugh 411 were consolidated at 250 psi and sintered at 920° C. All of the above samples were sintered in a 90% argon10% hydrogen atmosphere. 
    
     In order to span the region of possible temperature and compressive forces that a porous anode could encounter in an operating fuel cell, two temperatures (650° and 700° C.) and three holding forces (25, 50, and 100 psi) were used in earlier tests. 
     All of the tests which were completed are listed in Table III. Porosimetry was used to determine the volume percent porosity, mean pore size, and pore size distribution for each of the anode plaques tested. Initially, the target pore size range was 1-3 μm. The mean pore size of plaques tested initially were typically between 7-15 μm. Mean pore size of plaques were reduced in further experimentation and were mostly in the range of 4-10 μm. The state-of-the-art nickel-10% chrome anodes are about 65 vol. % porosity and an average pore size of 4-6 μm. The majority of the metal coated LiFeO 2  ceramic anodes had 45 to 55 vol. % porosity. In general, the metal coated anodes tested had larger pores and a smaller volume percent porosity than the state of the art nickel-chrome anodes. 
     
                                           TABLE III__________________________________________________________________________                 TestBatch         End  Rig                 Condi-                      Plaque    Pow-                                    Load          Poro-                                                      %No. Test No.    Start         Date No.                 tioning                      No.  Material                                der %  % Ni                                           % Cu                                               PPS                                                  sity                                                      Creep__________________________________________________________________________ 8  CACT-1    10/29/86         11/05/86              3  650 C.                      SNF  LiFeO.sub.2                                SNF 50.00                                       25.00                                           25.00                                               18.20                                                  56.80                                                      26.85                 100 PSI                      138-B     130-B 5  2.3.lb-    07/16/87         07/23/87              1  650 C.                      XXXX LiFeO.sub.2                                LF-18                                    37.00                                       18.50                                           18.50                                               6.00                                                  67.60                                                      7.63    05                100 PSI                      V-1 5  2.3.lb-    07/16/87         07/23/87              1  650 C.                      XXX  LiFeO.sub.2                                LF-18                                    37.00                                       18.50                                           18.50                                               6.00                                                  56.70                                                      2.26    05                100 PSI                      V-2 5  2.3.lb-    07/16/87         07/23/87              1  650 C.                      XXXX LiFeO.sub.2                                LF-18                                    37.00                                       18.50                                           18.50                                               6.00                                                  63.90                                                      8.82    05                100 PSI                      V-4 5  2.3.lb-    07/16/87         07/23/87              2  670 C.                      XXXI-3                           LiFeO.sub.2                                LF-7                                    62.67                                       31.23                                           31.23                                               6.00                                                  67.50    05                100 PSI 5  2.3.lb-    07/16/87         07/23/87              2  650 C.                      XXXI-4                           LiFeO.sub.2                                LF-7                                    62.67                                       31.23                                           31.23                                               6.00                                                  53.60                                                      7.63    05                100 PSI 5  2.3.lb-    07/16/87         07/23/87              3  650 C.                      XXXXI                           LiFeO.sub.2                                LF-10                                    37.00                                       18.50                                           18.50                                               6.00                                                  63.10                                                      2.62    05                100 PSI                      X-1 5  2.3.lb-    07/16/87         07/23/87              3  650 C.                      XXXXI                           LiFeO.sub.2                                LF-10                                    37.00                                       18.50                                           18.50                                               6.00                                                  63.75                                                       .69    05                100 PSI                      X-2 6  2.3.lb-    07/24/87         08/08/87              2  650 C.                      XXXX LiFeO.sub.2                                LF-10                                    37.00                                       18.50                                           18.50                                               6.00                                                  44.10                                                      2.55    06                100 PSI                      VIII-2 6  2.3.lb-    07/26/87         08/08/87              3  650 C.                      XXXIII-                           LiFeO.sub.2                                LF-9                                    46.50                                       23.20                                           23.20                                               6.00                                                  63.80    06                100 PSI                      210  2.3.lb-    11/25/87         12/01/87              1  650 C.                      LXXX LiFeO.sub.2                                LF-18                                    50.49                                       33.00                                           17.49                                               9.00                                                  26.87    10                100 PSI                      XVI-110  2.3.lb-    11/25/87         12/01/87              1  650 C.                      LXXX LiFeO.sub.2                                LF-18                                    50.49                                       33.00                                           17.49                                               9.00                                                  27.37    10                100 PSI                      XVI-210  2.3.lb-    11/25/87         12/01/87              1  650 C.                      LXXX LiFeO.sub.2                                LF-18                                    50.49                                       33.00                                           17.49                                               9.00                                                  27.11    10                100 PSI                      XVI-310  2.3.lb-    11/25/87         12/01/87              2  650 C.                      LXXX LiFeO.sub.2                                LF-18                                    50.49                                       33.00                                           17.49                                               9.00                                                  29.21    10                100 PSI                      XVII-110  2.3.lb-    11/25/87         12/01/87              2  650 C.                      LXXX LiFeO.sub.2                                LF-18                                    50.49                                       33.00                                           17.49                                               9.00                                                  30.12    10                100 PSI                      XVII-210  2.3.lb-    11/25/87         12/01/87              2  650 C.                      LXXX LiFeO.sub.2                                LF-18                                    50.49                                       33.00                                           17.49                                               9.00                                                  27.18    10                100 PSI                      XVII-311  2.3.lb-    03/29/88         04/06/88              1  650 C.                      156-2                           LiFeO.sub.2                                LF-19                                    63.66                                       21.66                                           21.66  41.20    11                100 PSI11  2.3.lb-    03/29/88         04/06/88              1  650 C.                      156-3                           LiFeO.sub.2                                LF-19                                    63.66                                       21.66                                           21.66  40.74    11                100 PSI11  2.3.lb-    03/29/88         04/06/88              2  650 C.                      158-2                           LiFeO.sub.2                                LF-16                                    66.00                                       33.00                                           33.00  42.82    11                100 PSI11  2.3.lb-    03/29/88         04/06/88              2  650 C.                      158-3                           LiFeO.sub.2                                LF-16                                    66.00                                       33.00                                           33.00  42.84    11                100 PSI11  2.3.lb-    03/29/88         04/06/88              3  650 C.                      200-1                           LiFeO.sub.2                                LF-16                                    66.00                                       33.00                                           33.00  44.29    11                100 PSI11  2.3.lb-    03/29/88         04/06/88              3  650 C.                      200-2                           LiFeO.sub.2                                LF-16                                    66.00                                       33.00                                           33.00  41.72    11                100 PSI11  2.3.lb-    03/29/88         04/06/88              3  650 C.                      200-3                           LiFeO.sub.2                                LF-16                                    66.00                                       33.00                                           33.00  38.58    11                100 PSI__________________________________________________________________________ 
    
     Chemical analysis was performed to determine the metal-to-ceramic ratio of the anode materials. The anodes tested were coated with pure nickel or a nickel-copper alloy. The nickel-copper coatings were generally about 50 wt % each metal. The amount of metal in the samples or metal loading varied between 10 and 60 wt % (see Table III). 
     Scanning electron photomicrographs of polished cross-sections of the anode plaques before testing showed the quality of the materials produced was consistently improved. Photomicrographs showing an excellent microstructure are depicted in FIGS. 8(A) and 8(B). 
     IN-CELL TESTING 
     An in-cell test was made using standard boiler-plate hardware, a sintered LiFeO 2  anode, a SOA Ni cathode, stainless steel cathode current collector, and a Ni anode current collector were prepared for assembly. The cell package was assembled and then placed in the bench-scale test stand. A diagram of how the cell package is set up in the test stand is shown in FIG. 9. 
     Three nickel coated LiAlO 2  tapes and one nickel coated LiFeO 2  tape size large enough to test in bench-scale (94 cm 2 ) 54% metal loading were sintered and prepared for creep and bench-scale fuel cell tests. A Ni/LiAlO 2  tape and the Ni/LiFeO 2  tape were sintered in a standard muffle furnace, also purged with cracked ammonia gas. The heating schedule followed was: 
     4 hours ramped to 850° C. 
     1 hour ramp to 950° C. 
     15 minute hold at 950° C. 
     Cool. 
     A LiFeO 2  electrode which had 54% metal loading, a thickness from 0.0233 inch to 0.0064 inch, was tested. The cell package was assembled using a state-of-the-art (SOA) nickel cathode and hot-pressed tile. The test was begun using a normal slow ramp heat-up (room temperature to 350° C. in 3 hours, from 350° C. to 650° C. in 18 hours). The initial cell performance was poor compared to a SOA cell; it would not hold a stable voltage at 140 mA/cm 2  load, and the resistance was somewhat high at 7.68 mΩ. Increases in the cell holding force which was at 10 psi initially were applied at 24 (15 psi), 143 (20 psi), 167 (25 psi), 191 (30 psi), and 239 (35 psi) hours. The reason for increasing the holding force was to attempt to improve the contact of the anode to the tile in case the resistance, and poor performance, were due to poor surface contact between the anode and electrolyte. (The poor contact may have been due to the thickness variation of the electrode.) A table showing the cell performance mV, IR-free mV, and polarization mV is shown in Table IV. 
     
                                           TABLE IV__________________________________________________________________________Cell Test CerLiFe-1 Life DataHours-)0  24 48 72 144               168                  192                     216                        312                           336                              360__________________________________________________________________________mA/cm.sup.2Cell millivolts0(OCV)992   988      986         987            991               990                  989                     994                        989                           989                              987 40  876   877      871         853            811               841                  837                     847                        843                           845                              843 60  812   823      806         790            737               775                  774                     779                        774                           778                              784 80  733   770      744         721            653               698                  688                     708                        694                           704                              703100  660   707      675         644            547               617                  610                     625                        613                           630                              619120  577   645      606         572            455               540                  529                     548                        540                           548                              555140  498   576      531         491            363               463                  454                     475                        467                           483                              483160     510      462         416            273               387                  381                     406                        396                           417                              424180     432      367         330   314                  308                     326                        336                           356                              351200                          266                           284220240resistance7.68   7.85      8.96         10 10.2               10.7                  9.75                     9.9                        7.96                           7.8                              7.89mA/cm.sup.2IR free millivolts 40  907   908      907         893            852               884                  876                     887                        875                           876                              875 60  858   870      860         850            798               839                  833                     838                        822                           825                              831 80  794   833      816         801            735               784                  766                     787                        758                           766                              766100  737   786      765         744            649               724                  708                     724                        693                           708                              698120  669   739      714         692            577               668                  646                     667                        636                           642                              650140  606   686      656         631            506               613                  591                     614                        578                           592                              593160     636      605         576            436               558                  537                     564                        523                           542                              550180     573      528         510   507                  484                     504                        479                           496                              493200                          409                           424220240mA/cm2Polarization millivolts 40   85    80       79          94            139               106                  113                     107                        114                           113                              112 60  134   118      126         137            193               151                  157                     156                        167                           164                              156 80  198   155      170         186            256               206                  223                     207                        231                           223                              221100  255   203      221         243            342               266                  282                     270                        296                           281                              289120  323   249      272         295            414               322                  343                     327                        353                           347                              337140  386   302      330         356            485               377                  399                     380                        411                           397                              394160     352      381         411            555               432                  452                     430                        466                           447                              437180     415      458         477   483                  506                     490                        510                           493                              494200                          580                           565220240__________________________________________________________________________ IR FREE mV = mV at load plus resistance in milliohms times amps at load setting i.e. 7.68 milliohms times (100 cm2 × 160 mA/cm.sup.2 = 1600 mA)/1000 = 122.88 mV Polarization voltage equals OCV millivolts minus IR free millivolts 
    
     The cell was terminated after 360 hours of cell life, since little improvement was observed after the last cell holding force increase. The terminated anode and current collector were measured and compared to the pre-test anode measurements. Allowing for the thickness of the current collector, which was subtracted from the total measurement since it could not be separated from the anode, the change in anode thickness from pre-test to post-test was 2.6 mils. This change, based on the pre-test thickness of 19.7 mils, corresponds to a 13.2% creep value for the anode. 
     
                                           TABLE V__________________________________________________________________________Comparison of IR Loss, IR-Free, and PolarizationCell Test CerLiFe-1Load Voltage, mV      mV at           mV at                IR-Loss                     IR-Free  Polarization      100  160  @ 160                     @ 160                          RES.                              @ 160Date   Hours  OCV mA/cm.sup.2           mA/cm.sup.2                mA   mA   mΩ                              mV/cm.sup.2__________________________________________________________________________19884/12    0  992 660  N/A  123  N/A  7.7 N/A4/13    24 988 707  510  125  635  7.8 3534/14    48 986 675  462  142  604  8.9 3824/15    72 987 644  416  160  576  10.0                              4114/18   144 991 547  273  163  436  10.2                              5554/19   168 990 617  387  171  558  10.7                              4324/20   192 989 610  381  155  536  9.7 4534/21   216 994 625  406  158  564  9.9 4304/22   240 991 621  394  139  533  8.7 4584/25   312 989 613  396  127  523  7.96                              4664/26   336 989 630  417  125  542  7.8 4474/27   360 987 619  424  126  550  7.89                              437Data from a normal SOA fuel cell with Ni + Cr Anode (Cell TestIGT-83-5AC):192    991 847  758   85  843  5.32                              148__________________________________________________________________________ 
    
     As can be seen from Table V, the performance of this cell was inferior to SOA performance. From Table IV it can be seen that the OCV of the cell was acceptable indicating the proper electrochemical potentials each side of the cell (no gas crossover). This was corroborated by measuring the gas crossover during cell life. However, looking at the cell potential at 160 mA/cm 2  and 192 hours, it can be seen that it is about 377 mV (758-381) lower than a SOA cell whose test results are depicted at the bottom of Table V (just the first 360 hours of a 528 hour test are shown for comparison). This 377 mV lower performance is made up from 70 mV higher IR (155-85) and 305 mV higher polarization loss (453-148). That is, most of the observed lower performance is due to polarization losses which are most likely due to the active three phase contact on this metal coated LiFeO 2  anode not being optimized in this first test. This factor is encouraging since the particle size and the electrode morphology can be developed to more closely match that of a SOA electrode. 
     The pre-test sample was analyzed for Ni, Cu, Fe and Li by atomic absorption of a completely dissolved anode solution. The percentages of Fe and Li in the samples were converted to percentages of Fe 2  O 3  and Li 2  O, which may be combined to represent LiFeO 2  or Li x  FeO 2  in case of non-stoichiometry. 
     
                       TABLE VI______________________________________Chemical AnalysisComponents       Pre-test Post-test______________________________________Cu               40.84    35.63Ni               25.60    22.32Li               1.20     1.88Fe               26.61    20.50K                --       2.23CO.sub.2         --       3.40Li.sub.2 O       2.57     3.72Fe.sub.2 O.sub.3 38.04    29.34K.sub.2 CO.sub.3          3.94Li.sub.2 CO.sub.3         0.75Li.sub.2 :Fe.sub.2 O.sub.3 (by mole)            0.36     0.68Cu:Ni (by weight)            1.60     1.60Metal:Fe.sub.2 O.sub.3            1.75     1.98(by weight)______________________________________ 
    
     Results of chemical analysis of pre- and post-test anode are presented in Table VI. The pre-test sample consisted of Cu, Ni and LiFeO 2 . The Li-to-Fe atom ratio was 0.36, indicating a Li-deficient lithium iron oxide compound which can be represented as (Li 2  O) x  Fe 2  O 3  with x=0.36. 
     The post-test anode contained Li 2  CO 3  and K 2  CO 3 . To breakdown the total Li to those tied up to (Li 2  O) x  Fe 2  O 3  and Li 2  OCO 3 , CO 2  analysis was performed. Thus, it was assumed that K was converted to K 2  CO 3  and CO 2  in excess of that tied up to K was combined with Li to form Li 2  CO 3 . Excess Li not tied up with CO 2  was then assumed to be tied up with Fe in the form of (Li 2  O) x  Fe 2  O 3 . The results yield an x=0.68 post-test. Therefore, lithiation of the anode took place during cell operation. This is not surprising since one would expect the stoichiometric Li 2  O.Fe 2  O 3  to be stable phase in the presence of electrolyte. In fact, one should start with a stoichiometric LiFeO 2  material to prevent lithium consumption from the electrolyte. 
     The Cu/Ni ratio was similar for both pre- and post-test samples as expected for a sample coated under controlled conditions. 
     The metal-to-Fe 2  O 3  ratio was 1.75 pre-test and 1.98 post-test suggesting slight non-uniformity in metal loading throughout the sample. 
     The carbonate content of the post-test anode was only 4.69% by weight or 25% filling of the 41% anode porosity. This carbonate content is generally acceptable. 
     An important observation is the obvious improvement in metal coating coverage on LiFeO 2  substrates. This is attributed to the stability of the substrate in the plating bath. It is clear that substrate-bath interactions play an important role, not only in ensuring good unflocculated powder dispersions, but also in ensuring uniformity of surface sensitization and activation procedures. 
     Creep Behavior of Metal-coated LiFeO 2  Anodes 
     In the case of LiFeO 2  anodes, the major difference is that the metal wetting characteristics are more favorable. Thus a better bond is to be expected between the metal and the ceramic, reducing the amount of primary creep. FIG. 10 shows the general trends in the creep behavior of metal-coated LiFeO 2  anodes. Creep is relatively insensitive to both metal loading and anode porosity, indicative that once particle rearrangement occurs secondary creep mechanism dominates the creep behavior. Creep characteristics are shown for Test #2.3.lb-5. The data show that the magnitude of the primary creep is less than ˜2%. Further creep is as expected for diffusion driven process. The data for rig 2 for anodes with higher metal loading are inconsistent with the trend and should be disregarded due to a malfunctioning test rig. The effect of anode morphology is greater, with higher anode creep exhibited for anodes with greater mean pore size and porosity. This is consistent with observations of LiAlO 2  anodes. 
     Conclusions 
     In summary, the following points emerge from the analysis of the microstructure/creep measurements relations. 
     1. For any metal-coated ceramic anodes, the predominant creep mechanism is due to particle rearrangement. This mechanism will dominate creep behavior even if the metal wets the ceramic but does not adhere well. 
     2. The anode porosity must be as low as possible consistent with anode performance criteria such as polarization phenomena associated with mass transport limitations in such porous electrodes. The mean pore size must also be as low as possible, consistent with performance criteria. 
     3. Metal coated anodes will exhibit lower creed at lower metal loadings. In fact, the data suggest that completeness of coverage is not the important criterion. Rather, uniformity of metal deposition is more important. It is conceivable that if the metal deposits adhere well, then in a three dimensional porous structure there can be contiguity of metal contacts leading to anode conductivity, 
     4. The factors affecting metal coating coverage have been mentioned earlier. One consideration is the deposition of metal alloys. In any process which deposits metals sequentially, the driving force for alloy formation will generally exceed the force for wetting (and hence adhesion) on the ceramic. This could also lead to some Kirkendall porosity at the metal/ceramic interface. These factors will weaken the bond and thus lead to poor mechanical properties. Thus there may be advantage in deposition of alloys on the surface.