Abstract:
A laminated structure comprising at least two nonadhesive layers and at least one white-pigmented adhesive layer, wherein the white-pigmented adhesive layer is made of a composition stabilized against thermal crosslinking and consequent reduction of its melt index, consisting essentially of a uniform dispersion of alumina-coated titanium dioxide pigment in a blend of a matrix polymer which is a dipolymer of ethylene with an ethylenically unsaturated carboxylic acid or a terpolymer of ethylene with an ethylenically unsaturated carboxylic acid and with another ethylenically unsaturated comonomer, or with carbon dioxide or sulfur dioxide, with a stabilizing polymer which is a high melt index copolymer of ethylene with acrylic or methacrylic acid. Such laminated structures include, for example, toothpaste tubes, condiment pouches, traffic road signs, and roadway lane marking tapes.

Description:
CROSS-REFERENCE TO RELATED APPLICATION 
     This is a continuation-in-part of my application Ser. No. 07/436,467 filed Nov. 14, 1989, and now allowed as U.S. Pat. No. 4,992,486. 
     BACKGROUND OF THE INVENTION 
     This invention relates to laminated structures in which at least one adhesive layer is a melt-stable, titanium dioxide-containing composition of one or more copolymers of ethylene with alpha, beta-unsaturated carboxylic acids such as, e.g., toothpaste tubes, where metal foil is laminated to a printable plastic layer on which the name of the product or other similar information is to be printed. Ethylene copolymers with alpha, beta-unsaturated carboxylic acids are known to be very good hot melt adhesives, which are suitable for bonding the outer layer to the metal foil or to another plastic layer. When the outer layer is a clear or at least translucent plastic, it is considered advantageous from the standpoint of aesthetics and commercial appeal that the adhesive layer be white-pigmented, so that the white color may show through. Another typical application for such white-pigments copolymers is in condiment pouches. 
     Traditionally, titanium dioxide has been used as white pigment for plastics and for other purposes. However, commercial titanium dioxide particles normally are coated on their surface with alumina, which improves the pigment&#39;s flowability. When such alumina-coated titanium dioxide is incorporated into an ethylene/alpha, beta-unsaturated carboxylic acid copolymer, and such pigmented copolymer is exposed to high temperatures, such, for example, as are encountered during extrusion, the copolymer appears to be reacting with the alumina coating, as evidenced by a decrease of the polymer&#39;s melt index. Further reduction of melt index occurs on storage. Such lowering of the melt index is undesirable because it leads to nonuniform coating thicknesses and pinholes in the coatings. In addition to the instability of the melt index, a further problem has been the formation of gels in the polymer, resulting in poor quality extrusion coatings. 
     There is, therefore, a great need for a thermally stable titanium dioxide-pigmented ethylene/alpha, beta-unsaturated carboxylic acid copolymer. 
     SUMMARY OF THE INVENTION 
     According to this invention, there is provided a laminate structure comprising at least two nonadhesive layers and at least one white-pigmented adhesive layer, which adhesive layer is made of a composition stabilized against thermal crosslinking and consequent decrease of its melt index consisting essentially of a uniform dispersion of alumina-coated titanium dioxide pigment in a blend of a matrix polymer with a stabilizing polymer, 
     the matrix polymer being a copolymer represented by the formula E/X/Y, where E stands for ethylene; X stands for a C 3  -C 7  alpha, beta-unsaturated carboxylic acid; and Y, which is optional, stands for another copolymerizable comonomer selected from the group consisting of C 3  -C 7  alpha, beta-unsaturated carboxylic acids, C 1  -C 10  alkyl esters of such acids, vinyl esters, vinyl ethers, acrylonitrile, methacrylonitrile, carbon monoxide, and sulfur dioxide; the respective relative weight ratios of the monomers in said E/X/Y copolymer being about 96:4:0 to 40:30:30, and the melt index of said copolymer, determined according to ASTM D1238, Condition E, being about 0.1-100 dg/min; and 
     the stabilizing polymer being a high melt index copolymer of ethylene with an unsaturated carboxylic acid selected from the group consisting of acrylic acid (E/AA copolymer) and methacrylic acid (E/MAA copolymer), said high melt index copolymer having a melt index of at least about 5,000 dg/min, but preferably at least 10,000 dg/min, determined according to ASTM D1238, condition E, and containing at least about 5 weight percent, preferably at least 9 weight percent, of carboxylic acid monomer; 
     the relative weight ratio of matrix polymer to stabilizing polymer being about 95:5 to 80:20, and the amount of titanium dioxide in the blend being about 5 to 20 weight percent. 
     The composition may be further compounded to incorporate minor amounts of conventional additives such as, e.g., stabilizers, antioxidants, and slip improving agents. It can be additionally formulated with further additives such as, for example, plasticizers and unreactive fire retardants such as halogenated hydrocarbons, the total amount of plasticizers, if present, being no more than about 15 weight percent, but preferably 5-15 weight percent of the final composition; and the amount of fire retardants, if any, being about 10 to 30 weight percent of the final composition, depending on the level of fire resistance desired. 
    
    
     BRIEF DESCRIPTION OF THE DRAWING 
     The drawing represents a plot of intitial melt index of representative compositions of the present invention as well as of some compositions outside the scope of the present invention vs. weight percent of high melt index copolymer in those compositions. 
    
    
     DETAILED DESCRIPTION OF THE INVENTION 
     Definition: For the purpose of the present disclosure and claims, the expression &#34;consisting essentially of&#34; means that the recited components are essential, while smaller amounts of other components may be present to the extent that they do not detract from the operability of the present invention. 
     The E/X/Y copolymers suitable in the compositions of the present invention either are available commercially or can be made according to known processes from readily available monomers. Copolymers of ethylene with unsaturated carboxylic acids are described in U.S. Pat. Nos. 4,351,931 to Armitage, 4,252,954 to Chatterjee, 3,264,272 to Rees, 3,520,861 to Thomson et al., 3,884,857 to Ballard et al., and 3,658,741 to Knutson et al. Terpolymers of ethylene with unsaturated carboxylic acids and with alkyl esters of unsaturated carboxylic acids are described in U.S. Pat. No. 3,264,272 to Rees; terpolymers of ethylene with carbon monoxide and unsaturated carboxylic acids are disclosed in U.S. Pat. No. 3,780,140 to Hammer, while terpolymers with sulfur dioxide and unsaturated carboxylic acids are described in U.S. Pat. No. 3,784,140 to Hammer. Various ethylene copolymers with methacrylic acid are sold by E. I. du Pont de Nemours and Company under the trademark NUCREL®. Ethylene copolymers with acrylic acid are sold by Dow Chemical Company under the trademark Primacor®. Carboxylic acids, in addition to acrylic, methacrylic, and higher unsaturated monocarboxylic acids, also include monoesters of alpha, beta-unsaturated dicarboxylic acids such as, e.g., maleic, fumaric, and itaconic acids. Typical alkyl esters of alpha, beta-unsaturated carboxylic acids include methyl, ethyl, butyl, pentyl, hexyl, octyl, and decyl esters, both linear and branched, as well as diesters of dicarboxylic acids. 
     High melt index copolymers of ethylene with acrylic or methacrylic acid normally will be dipolymers, although a minor amount of a third monomer, such as, for example, one of those that can be present in matrix terpolymers, can be tolerated without impairing the operability of this invention. 
     High melt index copolymers of ethylene with acrylic acid are available, for example, from Allied Signal Corporation under the trademark A-C® Copolymers. Such copolymers also can be made according to known methods, as illustrated by means of examples herein. 
     High melt index copolymers of ethylene with methacrylic acid also can be made according to known methods, as illustrated by means of examples herein. 
     Titanium dioxide is available from several sources, including E. I. du Pont de Nemours and Company. 
     Preferred matrix dipolymers are dipolymers of ethylene with methacrylic acid (X is methacrylic acid and Y is absent) and especially those in which the weight proportion of methacrylic acid is about 3-30%, preferably 4-15% by weight. Preferred matrix terpolymers are terpolymers of ethylene in which X is methacrylic acid and Y is vinyl acetate, n-butyl acrylate, or isobutyl acrylate. 
     It is generally preferred to choose the type and amount of the stabilizing polymer such that the resulting initial melt index of the composition is close to the melt index of the matrix polymer itself. As will be seen below, this objective can be met for the preferred compositions with moderate amounts, 15% or less, of stabilizing polymer. 
     Laminates of the present invention comprise a substrate, for example, metal foil, sheet of plastic, or sheet of kraft paper, at least one adhesive layer, and at least one additional layer, wherein a composition of the present invention serves as the bonding agent. Such laminates can be made in a number of ways, all of which are generally known to the art, such as, for example, film casting, multilayer blow molding, compression molding, coextrusion, and extrusion lamination. In making these laminates, the stabilized, titanium dioxide-containing composition (sometimes also identified hereinafter as WPAC, which stands for white pigmented acid copolymer) will normally be provided in one of two forms: either it is first formed into a sheet by blown film extrusion or calendering, and then, in a second step, the sheet is rolled and pressed onto a polymer substrate; or it is supplied in a particulate form such as pellets or the like, which are extruded into a sheet in contact with various substrate layers. 
     Film casting is a continuous process by which a thermoplastic material is extruded through a slot die onto a chill roll, where it is quenched and solidified. The molten film normally exits the extruder vertically through a slot die and tangentially contacts the chill roll that cools the material into a web. Extrusion lamination is an adaptation of this technique, wherein the film is cast onto a substrate such as kraft paper, aluminum foil, polyester film, or low density polyethylene (LDPE) film. Since the WPAC compositions of the present invention normally are used as adhesive or bonding layers in laminate structures, the WPAC film is cast between two substrates. A typical laminate may thus be, for example, aluminum foil//WPAC//clear LDPE or kraft paper//WPAC//clear LDPE. In a multilayer laminate structure, more than one WPAC bonding layers may be present. 
     Another common process for producing films of thermoplastic materials is blown film extrusion. In this process, a molten tube of polymer is simultaneously drawn axially and expanded radially from an annular slit die. The hot tube is cooled by high velocity air from an air ring on the outside and sometimes also on the inside of the tube. Normally, the tube is formed and drawn in a vertical and upward direction. 
     In multilayer blow molding, multilayer laminate structures are formed through coextrusion. A multiplicity of extruders, usually from two to seven, feed individual polymers into a coextrusion head, where a multilayer laminate is extruded. This may be a flat film or sheet laminate or a hollow tube (parison). The parison is captured at regular intervals in vertically positioned molds. Thereafter, the hot plastic material is blown with air to expand it to the configuration of the mold cavity, thus forming the final, usually container, shape. The continually extruded parison is cut during the process. The WPAC compositions of this invention can be used as the adhesive layer in structures such as, for example, ethylene/vinyl alcohol copolymer//WPAC//high density polyethylene or polypropylene. 
     Compression molding is the simplest process for producing laminates. The apparatus, or molding press, consists of two platens that close together. Heat and pressure are applied to form the material into the desired shape. A typical laminate that can be made in such equipment has the following layers: aluminum foil//WPAC//clear polyester. The two outer layers are higher melting than the inner layer, so that under the press conditions only the adhesive inner layer is activated. A typical press temperature is about 200° C. Compression force can reach as much as 1000 tons. 
     Laminates in sheet or film form can be used for making a variety of articles such as, for example, the aforementioned toothpaste tubes, and condiment pouches, where the substrate is either metal foil or a plastic sheet, and the top coat is clear plastic on which appropriate information is printed; traffic road signs, where the substrate is either plastic or metal, and the top coat is clear plastic; and roadway lane marking tapes, in which both the bottom layer and the top layer are made of plastics. Other types of laminated articles, which can be formed directly, for example, by compression molding or by coextrusion and blow molding, comprise containers of various types, including bottles. 
     In the practical operation of the present invention, the high melt index stabilizing polymer and titanium dioxide may first be blended in a suitable equipment above the melt temperature of the polymer to form a masterbatch containing about 50-75 weight percent of TiO 2  uniformly dispersed in the polymer matrix. This masterbatch is then again melt-blended in the desired proportions with the matrix polymer. As an alternative, all three components may be melt-blended in one step. Neither method appears to offer an advantage over the other. 
     This invention is now illustrated by the following examples of certain preferred embodiments thereof, where all parts, proportions, and percentages are by weight unless otherwise indicated. TiO 2  used in all the examples was a commercial product of E. I. du Pont de Nemours and Company sold under the trademark Ti-Pure® R101. It had an average particle size of 0.18 micrometer and was coated on its surface with aluminum oxide. 
     Small quantities of material, about 50 g, were melt-compounded using a Haake System 40 Mixer fitted with roller-blade rotors. Samples were prepared for this mixer by dry blending the various powders and pellets and charging the total slowly to the mixer. Unless otherwise noted, the compounds were mixed in the Haake mixer at the required temperature for 3 minutes at 15 RPM, then for 7 minutes at 50 RPM. 
     Larger quantities of dry blend were compounded on a Werner and Pfleiderer corotating twin screw extruder using either a 28 mm trilobal or a 30 mm bilobal screw configuration. 
     Melt Index (MI) 
     Unless otherwise specified, melt index was determined, according to ASTM D1238, condition E, which requires a temperature of 190° C. and a 2,160 g weight. 
     High MI Copolymers 
     High MI acid copolymers E through M were prepared according to the general disclosure of U.S. Pat. No. 3,264,272 to Rees. Commercial ethylene and acrylic acid (AA) or methacrylic acid (MAA) were fed in a continuous manner to a stirred pressure vessel. Free radical initiator (t-butyl peroxyacetate) was fed by a separate line. The flow of monomers was adjusted to give constant mole ratios, and the feed rate was the same as the rate of discharge of polymer and of unpolymerized monomers from the reactor. A small amount of acetone or methanol, used as a telogen (chain transfer agent), was also introduced into the reactor with the feed monomers to control the molecular weight. 
     Table I represents the state of the art of compounding pigmented compositions containing TiO 2  and gives melt index stability data for representative compositions containing an E/MAA copolymer as the matrix polymer and a commercial dispersion of titanium dioxide in either an ethylene/methyl acrylate copolymer carrier or a low density polyethylene (LDPE) carrier, both supplied by Ampacet Co. of Mount Vernon, Illinois. Samples 1-3 were the matrix polymers, and samples 4 and 5 were the Ampacet TiO 2  concentrates. Samples 6 through 11 were made by extruder-blending 25 parts of Ampacet concentrate with 75 parts of matrix polymer at 170° C. The resulting blends had initial MIs of 11.0 to 5.4, but those dropped considerably after mixing at 280° C. in the Haake Mixer. Samples 13 and 14 were made by directly compounding 30 parts of Ampacet concentrates with 70 parts of matrix polymer in the Haake Mixer. The blends had very low MIs, suggesting a rather high degree of crosslinking. Sample 12 was a control, made by direct blending of matrix polymer with TiO 2 . This sample had a higher MI than samples 13 and 14, which were made via the concentrates. 
     
                                           TABLE I__________________________________________________________________________STATE OF THE ART OF POLYMER/TIO.sub.2 COMPOUNDING    TiO.sub.2      Matrix            % TiO.sub.2                 Extruder                         HaakeSample    Dispers.,      Polymer,            in   Mix     Mix MINo. Polymer, %      %     Blend                 Temp.                      MI Temp.                             Init.                                1 Mo.                                    2 Mo.__________________________________________________________________________1   --     [a],         100            --   --   12.5                         --  -- --  --2   --     [b],         100            --   --   9.1                         --  -- --  --3   --     [c],         100            --   --   7.0                         --  -- --  --4   [d],  100 --    --   --   9.1                         --  -- --  --5   [e],  100 --    --   --   5.1                         --  -- --  --6   [d],  25  [a],         75 12.5 170  11.0                         280 0.4                                0.6 0.57   [d],  25  [b],         75 12.5 170  9.7                         280 2.0                                2.0 2.08   [d],  25  [c],         75 12.5 170  7.1                         280 0.8                                0.8 0.89   [e],  25  [a],         75 12.5 170  9.1                         280 0.7                                0.8 0.610  [e],  25  [b],         75 12.5 170  7.7                         280 2.1                                2.1 2.711  [e],  25  [c],         75 12.5 170  5.4                         280 0.7                                0.8 0.612  --     [a],         85 15.0 --   -- 280 1.2                                1.5 1.413  [e],  30  [a],         70 15.0 --   -- 280 1.0                                0.8 0.714  [d],  30  [a],         70 15.0 --   -- 280 0.4                                0.5 0.5__________________________________________________________________________ [a] E/MAA copolymer, 9% MMA, nominal MI = 10 [b] E/MAA copolymer, 6% MAA, nominal MI = 9 [c] E/MAA copolymer, 4% MAA, nominal MI = 7 [d] &#34;Ampacet&#34; 11892: 50% TiO.sub.2, E/Methyl acrylate carrier, nominal blend MI = 12 [e] &#34;Ampacet&#34;  11171: 50% TiO.sub.2, LDPE carrier, nominal blend MI = 5 
    
     Tables II and III describe the various copolymers used in the course of the experimental work reported herein. 
     Table II lists the matrix copolymers, and Table III lists the high melt index stabilizing E/AA and E/MAA copolymers. The matrix copolymers are identified by Roman numerals I through IV. High melt index stabilizing copolymers are designated by letters A-G. Those designated H and J-P have melt indices below 5,000 dg/min and are outside the scope of the present invention; they are included for comparison purposes only. Gel permeation chromatography data reported in Table III were obtained using Waters HPLC 150, AT-80M/S columns Numbers 7J732 and 7G707, with trichlorobenzene as solvent, at a temperature of 135° C. The intrinsic viscosities were calculated using the Mark-Houwink equation with k=0.0004340 and alpha=0.724. 
     
                       TABLE II______________________________________ETHYLENE/METHACRYLICACID MATRIX COPOLYMERS             I    II______________________________________Acid Content (%)    9.0    4.0Melt Index (dg/min) 10     11______________________________________ 
    
     
                                           TABLE III__________________________________________________________________________HIGH MI COPOLYMERS__________________________________________________________________________     A*   B*   C*   D*   E   F__________________________________________________________________________Acid Type AA   AA   AA   AA   MAA AAAcid Content (%)**     5.0  9.1  15.6 23.8 22.0                             18.1Meq/g     0.69 1.26 2.17 3.31 2.59                             2.51Melt IndexLiterature     &gt;15,000          &gt;15,000               &gt;15,000                    &gt;15,000                         --  --Determined     --   --   --   --   12200                             &gt;10000GPC DataPeak MW   8160 6850 4590 1800 3130                             2740Mw        10400          8820 5670 2860 3720                             3190Mv        9610 8040 5100 2460 3360                             2900Mn        5470 3420 2040 960  1450                             1330Mw/Mn     1.90 2.58 2.78 2.97 2.56                             2.41Intr. Visc.     0.16 0.155               0.115                    0.124                         0.155                             0.139__________________________________________________________________________     G   H  J  K  L   M   N   P__________________________________________________________________________Acid Type AA  AA AA AA MAA MAA MAA MAAAcid Content (%)**     29.7         18.1            24.5               29.5                  22.4                      28.6                          34.6                              11.0Meq/g     4.13         2.51            3.40               4.10                  2.64                      3.36                          4.07                              1.29Melt IndexLiterature     --  -- -- -- --  --  --  100Determined     10000         2400            1750               1200                  1120                      1000                          1100                              -- GPC DataPeak MW   2350         7720            6910               5210                  7850                      6850                          4170                              N/DMw        3120         9800            8210               6420                  9950                      7690                          5660                              N/DMv        2810         8870            7360               5760                  8960                      6940                          5040                              N/DMn        1200         3480            2730               2090                  3570                      2690                          1890                              N/DMw/Mn     2.60         2.82            3.01               3.07                  2.79                      2.86                          2.99                              N/DIntr. Visc.     0.136         0.313            0.274               0.229                  0.315                      0.262                          0.208                              N/D__________________________________________________________________________ *&#34;A-C&#34; resins from AlliedSignal Co. **By titration 
    
     Table IV lists representative pigmented compositions obtained from matrix polymer I by compounding at 280° C. with varying amounts of high MI copolymers. Samples 15-18, 33, and 41 were controls containing no high MI copolymer. Samples 15-32 contained 15% of TiO 2;  samples 33-40 contained 9% of TiO 2  ; and samples 41-42 contained 8% of TiO 2 . Samples 38-40 are outside the scope of the invention. These data show that with increasing level of high MI copolymer the initial MI increased, and MI stability improved. 
     
                                           TABLE IV__________________________________________________________________________PIGMENTED COMPOSITIONS BASED ONMATRIX POLYMER I COMPOUNDED AT 280° C.High MI       Matrix    MISample No. Copolymer, %         Polymer, %                TiO.sub.2                   Initial                       2 Wk.                           1 Mo.                               2 Mo.__________________________________________________________________________15    --      85     15 2.5 2.4 2.7 2.316    --      85     15 1.4 1.5 1.3 1.317    --      85     15 1.4 --  --  --18    --      85     15 1.6 1.8 --  --19    A,  2   83     15 2.2 2.7 2.2 2.220    A,  5   80     15 2.2 2.7 2.6 2.721    A,  10  75     15 4.1 4.4 4.0 3.222    A,  15  70     15 8.2 7.3 7.0 6.723    B,  2   83     15 1.6 1.6 1.6 1.524    B,  5   80     15 2.1 2.2 2.7 1.825    B,  10  75     15 5.1 5.5 4.9 5.226    B,  15  70     15 9.1 10.0                           8.6 9.027    C,  2   83     15 2.2 2.4 2.7 2.428    C,  5   80     15 3.1 3.9 3.4 3.829    C,  7.5 77.5   15 6.0 6.4 6.0 --30    C,  10  75     15 7.6 8.0 7.0 7.731    C,  10  75     15 7.9 8.8 --  --32    C,  15  70     15 16.4                       --  15.4                               15.133    --      91     9  4.1 4.0 3.9 4.134    C,  3   88     9  5.7 6.2 6.2 6.835    C,  5   86     9  6.4 6.9 7.9 8.736    C,  8   83     9  11.5                       11.5                           12.1                               10.837    C,  10  81     9  14.0                       14.9                           15.0                               12.238    P,  5   86     9  4.9 5.2 5.5 5.339    P,  10  81     9  5.8 5.6 6.2 6.640    P,  15  76     9  6.0 6.1 6.5 5.341    --      92     8  3.7 4.1 --  4.242    C,  4   88     8  7.1 7.2 --  7.0__________________________________________________________________________ 
    
     Table V similarly lists representative pigmented compositions obtained from matrix polymer II. Here, samples 43-55 contained 15% of TiO 2  ; samples 56-63 contained 9% of TiO 2  ; and samples 64-69 contained 6% of TiO 2 . Samples 43 and 56 were controls. The same general observation can be made that a higher level of high MI copolymer increased both the MI and the MI stability of the pigmented compositions. 
     The drawing is a plot comparing the effectiveness of representative high MI copolymers in increasing the initial MI of TiO 2  -containing matrix polymer II compositions. It shows the superiority of copolymers B and C, which had MI&#39;s in excess of 15,000, over copolymers H, J, K, L, and M, which had MI&#39;s from 2400 to 1000. The melt indices of the compositions containing copolymers B and C were higher initially and increased dramatically with the level of the copolymers B or C, while they were lower initially for copolymers H through L and either increased to a much lesser degree or not at all with increasing levels of those copolymers. 
     
                                           TABLE V__________________________________________________________________________PIGMENTED COMPOSITIONS CONTAININGMATRIX POLYMER II COMPOUNDED AT 280° C.High MI       Matrix    MISample No. Copolymer, %         Polymer, %                TiO.sub.2                   Initial                       2 Wk.                           1 Mo.                               2 Mo.__________________________________________________________________________43    --      85     15 5.2 4.8 5.3 --44    B   5   80     15 10.3                       9.7 9.3 9.545    B   6   79     15 11  10.5                           10.5                               11.546    B   10  75     15 15.2                       16.3                           16.6                               16.547    B   15  70     15 23.9                       25.7                           25.2                               27.148    C   4.5 80.5   15 11.2                       11.1                           10.9                               11.349    C   5   80     15 12.1                       12.9                           12.1                               --50    C   10  75     15 17.6                       17.6                           16.6                               --51    C   15  70     15 29.5                       29.1                           30.8                               --52    D   2.0 83     15 9.1 --  9.5 9.353    D   4.0 81     15 10.1                       --  10.1                               10.654    D   6.0 79     15 10.7                       --  10.9                               11.355    D   8.0 77     15 12.9                       --  13.3                               14.356    --      91     9  7.3 6.9 7.0 --57    B   5   86     9  10.9                       10.7                           12.6                               11.658    B   5   86     9  11.5                       11.2                           11.6                               12.359    B   10  81     9  19.4                       18.1                           18.1                               18.860    B   15  76     9  27.7                       27.2                           26.3                               26.861    C   3.5 87.5   9  10.7                       11.7                           11.5                               11.862    C   3   88     9  10.5                       11.6                           12.4                               --63    C   8   83     9  15.8                       16.5                           16.2                               --64    B   2   92     6  9.3 10.1                           9.0 9.165    B   4   90     6  10.4                       11.6                           11.2                               10.566    B   6   88     6  13.6                       13.1                           13.3                               13.267    C   2   92     6  8.7 9.5 8.3 9.068    C   4   90     6  11.5                       12.2                           11.9                               11.769    C   6   88     6  13.1                       14.1                           13.4                               14.0__________________________________________________________________________ 
    
     Table VI presents data correlating the melt index of lower MI copolymers, outside the scope of the invention, with the melt index stability of the blends. All the blends were prepared on the Haake System 40 Mixer at 280° C. All the copolymers in this table had MI&#39;s between 1000 and 2400 dg/min but this still was not high enough for optimum effectiveness. It can be seen, for example, that while the MI&#39;s were reasonably stable, increasing the amount of the high MI copolymer did not in most cases significantly increase the MI of the blend. 
     
                                           TABLE VI__________________________________________________________________________STABILIZATION OF MELT INDEX WITH HIGH MI COPOLYMERSHigh MI       Matrix      MISample No. Copolymer, %         Polymer, %                % TiO.sub.2                     Initial                         2 Wk.                             1 Mo.__________________________________________________________________________70    H   6   I  79  15   5.0 5.5 5.871    H   9   I  76  15   5.6 6.3 5.972    H   12  I  73  15   5.7 5.8 6.473    H   4   II 81  15   8.4 9.0 8.574    H   8   II 77  15   8.1 8.3 8.775    H   12  II 73  15   7.9 8.1 8.376    J   3   I  82  15   4.4 4.1 4.677    J   6   I  79  15   5.1 6.0 5.178    J   9   I  76  15   4.9 6.0 5.479    J   12  I  73  15   5.1 5.7 5.380    J   4   II 81  15   8.1 8.3 8.681    J   8   II 77  15   8.2 8.4 8.682    J   12  II 73  15   8.3 8.5 8.883    K   3   I  82  15   5.5 4.3 6.084    K   6   I  79  15   3.7 5.8 6.185    K   9   I  76  15   4.9 4.7 6.386    K   12  I  73  15   4.8 4.2 4.987    K   4   II 81  15   8.0 7.7 7.588    K   8   II 77  15   6.7 7.5 7.189    K   12  II 73  15   9.2 8.3 9.190    L   3   I  82  15   5.7 4.8 5.791    L   6   I  79  15   6.5 7.4 7.492    L   9   I  76  15   7.6 8.7 8.793    L   12  I  73  15   8.4 8.6 9.694    L   4   II 81  15   9.7 9.5 9.995    L   8   II 77  15   10.4                         10.7                             11.296    L   12  II 73  15   14.5                         16.1                             14.397    M   3   I  82  15   4.3 5.0 3.898    M   6   I  79  15   6.2 6.1 7.099    M   9   I  76  15   7.7 7.7 7.5100   M   12  I  73  15   7.7 10.1                             11.8101   M   4   II 81  15   9.1 9.5 10.0102   M   8   II 77  15   10.7                         11.1                             10.8103   M   12  II 73  15   13.9                         14.5                             13.9104   N   3   I  82  15   5.1 5.5 5.7105   N   6   I  79  15   5.9 6.2 7.1106   N   9   I  76  15   7.2 8.3 5.7107   N   12  I  73  15   6.1 8.0 7.0108   N   4   II 81  15   9.5 8.9 8.9109   N   8   II 77  15   10.9                         11.8                             10.5110   N   12  II 73  15   13.9                         12.7                             12.1__________________________________________________________________________ 
    
     Table VII presents similar data as Table VI, except that all the high MI copolymers have MIs of at least 10,000. In this case, both high MIs and high MI stabilities are obtained for the blends; and, further, increase of the level of high MI copolymer considerably increases the MI of the resulting blend. For example, sample 113 in this table was of the same composition as sample 92 in Table VI. Yet, at same level of high MI copolymer, the blend MI in the former case was 10.2, but in the latter case it was only 7.6. 
     
                                           TABLE VII__________________________________________________________________________STABILIZATION OF MELT INDEX WITH HIGH MI COPOLYMERSHigh MI       Matrix      MISample No. Copolymer, %         Polymer, %                % TiO.sub.2                     Init.                        2 Wk.                            1 Mo.                                2 Mo.__________________________________________________________________________111   E   3   I  82  15   3.7                        3.0 2.6 2.9112   E   6   I  79  15   6.4                        7.1 6.4 5.3113   E   9   I  76  15   10.2                        10.8                            8.8 10.2114   E   12  I  73  15   13.5                        14.4                            13.5                                14.4115   E   4   II 81  15   12.1                        12.7                            11.7                                11.2116   E   8   II 77  15   14.6                        14.2                            12.9                                13.7117   E   12  II 73  15   21.0                        21.2                            20.4                                19.9118   F   3   I  82  15   2.3                        3.9 2.6 --119   F   6   I  79  15   5.6                        5.9 7.5 --120   F   9   I  76  15   9.0                        9.1 10.2                                --121   F   12  I  73  15   12.0                        12.4                            12.3                                --122   F   4   II 81  15   11.1                        10.9                            10.2                                --123   F   8   II 77  15   14.0                        13.4                            13.3                                --124   F   12  II 73  15   17.6                        18.0                            18.7                                --125   G   3   I  82  15   3.0                        4.9 5.2 --126   G   6   I  79  15   6.4                        7.8 7.4 --127   G   9   I  76  15   8.4                        9.6 7.6 --128   G   12  I  73  15   11.2                        11.7                            12.4                                --129   G   4   II 81  15   9.7                        10.3                            10.2                                --130   G   8   II 77  15   13.5                        13.2                            14.1                                --131   G   12  II 73  15   16.5                        17.2                            17.3                                --__________________________________________________________________________ 
    
     Table VIII summarizes the preparation of TiO 2  concentrates for the practice of this invention. 
     Samples 132-138 were prepared using the Haake System 40 Mixer. Those compositions were then scaled up on a 30 mm twin screw extruder. Comparison of the initial MIs of samples 132 and 139 and samples 133 and 140 shows good initial MI reproducibility on scale-up. 
     
                                           TABLE VIII__________________________________________________________________________PIGMENTED COMPOSITIONS PREPARED USING CONCENTRATESPART ABlended in the Haake Mixer High MI Matrix      Melt                         InitialSample No. copolymer, %         Polymer, %                TiO.sub.2, %                     Temp.                         Melt Index__________________________________________________________________________Blended in the Haake Mixer132   C   35.0         I  15  50   200 427133   C   21.7         I  48.3                30   170 55134   B   50.0         --     50   170 --135   C   30.0         II 20  50   170 836136   C   11.7         II 58.3                30   170 25137   B   20.0         II 30  50   170 47138   B   16.7         II 53.3                30   170 30Extruded on 30 mm twin screw extruder139   C   35.0         I  15  50   170 650   same as 132140   C   21.7         I  48.3                30   170 57    same as 133141   B   50.0         --     50   170 too liquid                               to be extruded,                               same as 134142   C   16.7         II 33.3                50   170 86    --143   C   11.7         II 58.3                30   170 22    same as 136144   B   20.0         II 30  50   170 27    same as 137145   B   16.7         II 53.3                30   170 30    same as 138__________________________________________________________________________ 
    
     Table IX is a continuation of the experiments reported in Table VIII. All the compositions were compounded using a Haake System 40 Mixer. Table IX demonstrates that the invention can be practiced in two steps, using Ti02 concentrates, to the same extent as by blending individual components in a one-step operation. The concentrates were blended with either Matrix Polymer I or Matrix Polymer II in such amounts that the resulting blends contained either 9% or 15% of TiO 2 . The initial MIs of the final blends were comparable to those of the corresponding single-step preparations, which MIs are given in square brackets. 
     
                                           TABLE IX__________________________________________________________________________PIGMENTED COMPOSITIONS PREPARED USING CONCENTRATESPART BConcentrate   Matrix Melt                    Melt IndexSample No. Sample No., %         Polymer, %                Temp                    Init.* 2 Wk.                               1 Mo.                                   2 Mo__________________________________________________________________________146   132 30  I  70  280 10.3   10.1                               8.8 10.3                    [9.2]Gives 10.5% High MI Copolymer C + 74.5% Matrix Copolymer I + 15%TiO.sub.2147   133 30  I  70  280 8.4    9.5 8.1 9.5                    [8.2]Gives 6.5% High MI Copolymer C + 84.5% Matrix Copolymer I + 9% TiO.sub.2148   134 30  I  70  280 9.8    10.0                               9.0 9.2                    [8.3]Gives 15% High MI Copolymer B + 70% Matrix Copolymer I + 15% TiO.sub.2149   135 30  II 70  280 15.5   17.1                               16.1                                   16.4Gives 9% High MI Copolymer C + 76% Matrix Copolymer II + 15% TiO.sub.2150   136 30  II 70  280 12.4   12.9                               12.5                                   12.5                    [10.7]Gives 3.5% High MI Copolymer C + 87.5% Matrix Copolymer II + 9%TiO.sub.2151   137 30  II 70  280 8.9    9.7 11.0                                   9.8                    [11.0]Gives 6% High MI Copolymer B + 79% Matrix Copolymer II + 15% TiO.sub.2152   138 30  II 70  280 12.5   13.5                               13.5                                   11.9                    [8.1]Gives 5% High MI Copolymer B + 86% Matrix Copolymer II + 9% TiO.sub.2153   139 30  I  70  280 8.0    9.0 --  9.0                    [10.3]Gives 10.5% High MI Copolymer C + 74.5% Matrix Copolymer I + 15%TiO.sub.2154   140,     30  I  70  280 5.8    7.1 --  7.8                    [8.4 for 147]Gives 6.5% High MI Copolymer C&#34; + 84.5% Matrix Copolymer I + 9%TiO.sub.2155   142 30  II 70  280 11.4   12.5                               --  12.3Gives 5% High MI Copolymer C + 80% Matrix Copolymer II + 15% TiO.sub.2156   143 30  II 70  280 10.4   9.6 --  11.2                    [12.4]Gives 3.5% High MI Copolymer C + 87.5% Matrix Copolymer II + 9%TiO.sub.2157   144 30  II 70  280 10.4   11.4                               --  11.1                    [8.9]Gives 6% High MI Copolymer B + 79% Matrix Copolymer II + 15% TiO.sub.2158   145 30  II 70  280 11.9   10.1                               --  12.3                    [12.5]Gives 5% High MI Copolymer B + 86% Matrix Copolymer II + 9%__________________________________________________________________________TiO.sub.2 *Number in square brackets is the MI of the corresponding blend prepared from the same components in one step, without using a concentrate 
    
     LAMINATION EXPERIMENTS 
     In the following experiments, all data obtained in units other than SI have been converted to SI units. 
     Adhesive strength of laminates was determined according to the following test (with indicated variants). 
     A specimen, 2.54 cm wide and 12.7 cm long (in Example 1) or 15 mm wide and 25.4 cm long (in Example 2) was used for the test. About 2.5 cm of the coating was manually peeled from the substrate. The coating was placed in the upper jaw of the Instron Tensile Tester (in Example 1) or of the Zwick Model 1410 testing machine (in Example 2), and the substrate was placed in the lower jaw. The specimen was peeled at a 90° angle either at a crosshead speed of 30.5 cm per minute (in Example 1) or of 10 cm per minute (in Example 2). The load required to peel the coating away from the substrate was measured in units of force (or weight) per unit of width. In each test, triplicate measurements were made, and the average result was reported. 
     EXAMPLE 1 
     Two compositions, designated respectively as Compound 1A and Compound 1B, were compounded as follows: 
     
         ______________________________________Compound 1AE/MAA copolymer II from Table II (matrix)                     81.5%TiO.sub.2 (Ti-Pure ® R101)                     12.5%E/AA copolymer B from Table III (high MI)                     6.0%Compound 1BE/MAA copolymer I from Table II (matrix)                     75.0%TiO.sub.2 (Ti-Pure ® R101)                     15.0%E/AA copolymer C from Table III (high MI)                     10.0%______________________________________ 
    
     These compounds were extruded and laminated onto untreated 51 micrometer thick aluminum foil using an 11.4 cm Egan Laminator Coater®. The extruder was fitted with a two-stage mixing screw having a length-to-diameter (L/D) ratio of 28:1 and a compression ratio of 5:1. The extruder temperature settings were 177-304° C., the polymer melt temperature being 285-305° C. Each compound was extruded through a 122 cm wide ER-WA-PA® coat hanger die with a 508 micrometer opening. The extruded polymer film was laminated to the aluminum foil substrate using a matte finish chill roll. Line speed determined the ultimate coating thickness. The laminates were stored at ambient temperature for either 13 days or 57 days. The adhesive strength of the pigmented material was measured using the 90 peel test. The results are given below in Table X. 
     
                       TABLE X______________________________________  Line     Coating     Adhesive                               AdhesiveCompd. Speed    Thickness   Str., g/cm                               Str., g/cm(Sample)  m/min    micrometers 13 days 57 days______________________________________1A   (1)   40.2     76        189     3511A   (2)   61.0     51        552     4651A   (3)   121.6    25        240     2361B   (4)   40.5     76        193     3111B   (5)   60.6     51        213     4101B   (6)   121.9    25        221     236______________________________________ 
    
     EXAMPLE 2 
     A white-pigmented composition was compounded as follows: 
     
         ______________________________________E/MAA 96:4 copolymer, MI = 7 (matrix)                    84.0%TiO.sub.2 (Ti-Pure ® R101)                    9.0%E/AA copolymer B, Table III (high MI)                    7.0%______________________________________ 
    
     The laminates were prepared using a 9 cm Egan Laminator Coater® (mixing screw of L/D ratio of 30:1) with temperature settings of 170° C., 210° C., 250° C., 270° C., and 290° C. for the barrel and 290° C. for the connecting pipes. The air gap was 15 cm. The die opening was 700 micrometers and the die width 80 cm. Films were cast using a semi-matte finish chill roll. Aluminum foil and clear LDPE films were used as substrates for the laminated structures. In Test 2, below, (with multilayer laminates), two inner adhesive layers were formed by an unpigmented E/AA copolymer (9% AA, MI=10). 
     TEST 1 
     LDPE film//WPAC//E/AA copolymer//aluminum foil. This was the bottom portion of the multilayer laminate of Test 2. 
     TEST 2 
     The laminate from Test 1 was passed through the laminating line for the second time to give the following structure (from bottom to top): LDPE film//WPAC//E/AA copolymer//aluminum foil//E/AA copolymer//WPAC//LDPE film 
     The adhesive strength of 15 mm-wide test strips was determined in the 90° peel test. The average adhesion strength, in N/15 mm, was as follows: 
     
         ______________________________________For LDPE film//WPAC (bottom layer)                    7.4For WPAC//LDPE film (top layer)                    13.6______________________________________