Abstract:
A polyarylene sulfide resin composition comprises (A) 100 parts by weight of a polyarylene sulfide resin and (B) 0.05 to 100 parts by weight of at least one gas-trapping agent selected from zinc carbonate, zinc hydroxide and a complex salt of zinc carbonate and zinc hydroxide. It further comprises up to 400 parts by weight of an inorganic filler other than the gas-trapping agent (B) in way of material, the filler being in the form of fibers, particles and/or plates.

Description:
This application is a continuation of application Ser. No. 522,497, filed Apr. 20, 1990, which is a continuation of Ser. No. 407,654, filed Sep. 15, 1989, both now abandoned. 
    
    
     BACKGROUND OF THE INVENTION 
     The present invention relates to an improved polyarylene sulfide resin composition. More particularly, the present invention is concerned with a polyarylene sulfide resin composition and a molded article thereof having improved properties relative to preventing corrosion and staining of a metal combined with the molded article such as an electric contact. 
     In recent years, thermoplastic resins having a combination of high heat resistance and chemical resistance with flame retardancy have been desired for electrical and electronic equipment component materials, automobile equipment component materials, and chemical equipment component materials. 
     Polyarylene sulfide resins including polyphenylene sulfide are among the resins capable of meeting this desire. The demand for polyarylene sulfide resins has expanded also because polyarylenesulfides have excellent properties for the cost. 
     However, polyarylene sulfide resin has a drawback in that the raw material for production of the resin contains both sulfur and chlorine atoms and as a result by-products containing a large amount of chlorine are formed during synthesis of the resin. Unfortunately, this causes a problem when polyarylene sulfide resin is used as a material for molded components, since metals such as metallic contacts and plated or deposited metallic surfaces in the molded components are corroded and stained. As a result, polyarylene sulfide resin is poor in reliability because metal-polyarylene sulfide composite articles fail to sufficiently exhibit their intended function. 
     Because of the above-described problem, at the present time, polyarylene sulfide resin cannot be effectively for components which are continuously exposed to high temperature and which have a metallic contact, and thus, such problem limits range of applications of the resin. 
     The following expedients are known for solving the above problem. 
     (1) In the manufacturing process of the resin, the amount of inclusion of impurities such as sodium chloride in the resin is reduced by intensively purifying the resin. 
     (2) A trapping agent is positively added to suppress the formation of corrosive impurities. Examples of trapping agents include calcium carbonate, lithium carbonate (cf. Japanese Patent Laid-Open Nos. 162752/1979 and 229949/1985), hydrotalcite (cf. Japanese Patent Laid-Open No. 275353/1986), and zinc oxide (cf. Japanese Patent Laid-Open No. 181408/1984, Japanese Patent Publication No. 45711/1988 and U.S. Pat. Nos. 4,659,761 and 4,740,425). 
     (3) The resin is treated at a temperature as high as 200° C. or above to reduce corrosive gases before use. 
     However, the above methods have respective problems and do not provide any satisfactory solution to the problem. Specifically, it has been found that method (1) wherein the resin is intensively washed can remarkably reduce the, content of sodium chloride but, such method scarcely results in any improvement in preventing corrosion of metallic components contained in the molded articles, e.g., silver, aluminum, or iron. 
     In method (2), it has been found that lithium carbonate reduces generation of chlorinated gas and exhibits the effect of preventing corrosion of some metals such as iron but, exerts no effect on silver and its alloys usually employed in the metallic contact. Further, neither calcium carbonate, hydrotalcite, zinc oxide, etc. prevent corrosion of silver. 
     It has also been found that method (3) causes side effects such as discoloration and deterioration of the resin matrix at high temperature and results in only a slight effect of preventing corrosion of metals such as silver, aluminum, iron, etc., so that this method has not been regarded as practical. 
     In order to improve the prevention of the corrosion and staining of a metal during and after molding without detriment to excellent heat resistance, solvent resistance, flame retardancy, and mechanical properties of a polyarylene sulfide resin composition, particularly a polyphenylene sulfide resin composition, the present inventors have attempted to determine which gases are generated when a polyarylene sulfide resin composition is heated and have searched for an additive for trapping these gases. 
     SUMMARY OF THE INVENTION 
     Although the addition of various trapping agents has been reported in the above-described patent publications, no significant effect in improving the prevention of corrosion and staining of a metal has been observed by the present inventors. Accordingly, considering the reactivity of these trapping agents, the present inventors have selected zinc compounds from the viewpoint that a useful trapping agent particle should be active as much as possible, particularly reactive with a sulfur-containing gas and that the reaction product should be hardly colored. In view of extensive and intensive studies of zinc compounds, it has been found that although zinc oxide barely functions as a trapping agent, zinc carbonate, zinc hydroxide, or a double salt or a mixture thereof remarkably suppresses the corrosion and staining of metals, such as silver, aluminum or iron, caused by a polyarylene sulfide resin composition. 
     In accordance with the present invention, a polyarylene sulfide resin composition is provided which comprises (A) 100 parts by weight of a polyarylene sulfide resin and (B) 0.05 to 100 parts by weight of at least one gas-trapping agent selected from zinc carbonate, zinc hydroxide and a complex salt of zinc carbonate and zinc hydroxide. The composition may further comprise up to 400 parts by weight of an inorganic filler other than the gas-trapping agent (B). The filler may be in the form of fibers, particles and/or plates. 
     The composition preferably comprises as the filler 10 to 250 parts by weight of glass fibers, carbon fibers or particles or plates, alternatively to 400 parts by weight of glass fibers and another filler in the form of particles or plates. 
     The composition of the present invention can be molded into articles such as parts for electric or electronic appliances which may comprise an article molded from the composition as defined above and a connection made from a metal. 
     DESCRIPTION OF THE INVENTION 
     Accordingly, the present invention relates to a polyarylene sulfide resin composition, characterized by comprising: 
     (A) 100 parts by weight of a polyarylene sulfide resin; and, incorporated therein, 
     (B) 0.05 to 100 weight, based on 100 parts by weight of component (A), of at least one member selected from zinc carbonate, zinc hydroxide, and a double salt composed of both; and 
     (C) 0 to 400 parts by weight, based on 100 parts by weight of component (A), of an inorganic filler selected from a fibrous filler, a particulate or flaky filler other than component (B) and a mixture of both. The present invention relates also to a molded article comprising a combination of said polyarylene sulfide resin composition and a metal. 
     The base resin as component (A) of the composition of the present invention is a polyarylene sulfide resin and mainly comprises the following repeating units --(--Ar--S--)--, wherein Ar is an arylene group. 
     Examples of the arylene group (--Ar--) include: ##STR1## wherein R is an alkyl group, preferably a C 1  to C 6  alkyl group or a phenyl group and n is an integer of 1 to 4; ##STR2## 
     It is possible to use a polymer comprising the same repeating units among arylene sulfide groups constituting the above-described arylene groups, i.e., a homopolymer. In some cases, a copolymer containing different kinds of repeating units is preferable from the viewpoint of workability of the composition. 
     The homopolymer is more preferably a substantially linear polymer comprising p-phenylene sulfide groups as the repeating unit wherein a p-phenylene group is used as the arylene group. 
     The copolymer may comprise two or more different kinds of arylene sulfide groups composed of the above-described arylene groups. Among them, combinations including a p-phenylene sulfide group and a m-phenylene sulfide group are particularly preferred. In particular, a substantially linear polymer comprising at least 50% by mole, preferably at least 60% by mole, still preferably at least 70% by mole of p-phenylene sulfide groups is suitable from the viewpoint of properties such as heat resistance, moldability, and mechanical properties. 
     The m-phenylene sulfide groups are contained in an amount of preferably 5 to 50% by mole, particularly preferably 10 to 25% by mole. 
     A copolymer comprising repeating units of the components in the block form (e.g., one described in Japanese Patent Laid-Open No. 14228/1986) is preferably used because it is substantially the same as the copolymer comprising repeating units of the components in the random form in workability but superior in heat resistance and mechanical properties. 
     The polyarylene sulfide resin as component (A) used in the present invention may be a polymer improved in moldability by raising the melt viscosity through curing of the above-described polymer by taking advantage of oxidation cross-linking or thermal crosslinking or may be a polymer having a substantially linear structure and prepared by polycondensation of monomers mainly composed of bifunctional monomers. The latter polymer having a substantially linear structure is usually preferable because the molded article thereof exhibits better properties. 
     Besides the above-described polymers, a blended resin prepared by blending a crosslinked polyarylene sulfide resin capable of exhibiting gelation when melted and prepared through polymerization of a monomer mixture containing a monomer having three or more functional groups as part of the monomer component with the above-described substantially linear polymer may be also used as the base resin of the present invention. 
     Further, besides the polyarylene sulfide resin, it is also possible to use as an auxiliary a small mount of another thermoplastic resin as far as it exerts no adverse effect on the purpose. The another thermoplastic resin used therein may be any thermoplastic resin stable at a high temperature. 
     Examples of the another thermoplastic resin include aromatic polyesters of an aromatic dicarboxylic acid with a diol, such as polyethylene terephthalate or polybutylene terephthalate, and those of a hydroxy carboxylic acid, polyamide, polycarbonate, ABS, polyphenylene oxide, polyalkyl acrylate, polyacetal, polysulfone, polyether sulfone, polyether imide, polyether ketone, fluororesin, etc. These thermoplastic resins may be used also in the form of a mixture of two or more of them. 
     Component (B) used in the present invention is any one of zinc carbonate, zinc hydroxide and a double salt or a mixture thereof. 
     Zinc carbonate and zinc hydroxide are generally prepared by adding a salt of carbonic acid, such as soda ash, or other hydroxide to an aqueous solution of zinc salt, such as zinc sulfate, zinc chloride, zinc nitrate or zinc acetate, to form a precipitate and washing, filtering, and drying the precipitate. The resultant substance is a mixture of zinc carbonate with zinc hydroxide and called &#34;basic zinc carbonate&#34;. This substance is one of the substances preferably used in the present invention. 
     Besides the above substances, zinc orthocarbonate prepared by adding sodium bicarbonate to an aqueous solution of a zinc salt while blowing a carbon dioxide gas into the system is effective in attaining the purpose of the present invention. However, in the case of zinc oxide, the effect intended in the present invention is so small that zinc oxide is not suitable for use in the present invention. 
     Further, other zinc compounds, e.g. zinc chloride, zinc bromide, zinc fluoride, zinc iodide, zinc sulfate, zinc nitrate, zinc sulfite, zinc thiocyanate, zinc formate, zinc acetate, zinc propionate, zinc benzoate, zinc oxalate, zinc lactate, zinc tartrate, zinc oleate, zinc stearate, zinc phosphate, zinc phosphite, zinc hypophosphite, zinc hydrogenphosphite, zinc pyrophosphate, zinc chromate, zinc silicate, and zinc silicofluoride are unsuitable for use in the present invention because they are not difficult to safely and stably knead with the resin from the viewpoint of delinquescene, acidity, thermal resistance, toxicity, etc. but also low in the effect intended in the present invention. 
     Further, metallic zinc powder as well is so low in the effect intended in the present invention that it is unsuitable for use in the present invention. 
     The amount of component (B) used in the present invention is 0.05 to 100 parts by weight, preferably 0.1 to 40 parts by weight per 100 parts by weight of a polyarylene sulfide resin as component (A). When the amount is less than 0.05 part be weight, the effect intended in the present invention is poor, while when the amount is too large, there arises a problem of reduction in the mechanical strengths of the molded article, which is unfavorable. 
     Although the inorganic filler as component (C) used in the present invention is not always necessary, it is preferred to incorporate this component for the purpose of preparing a molded article excellent in performance such as mechanical strengths, thermal resistance, dimensional stability (resistance to deformation and warping), and electrical properties. Any of fibrous, particulate and flaky fillers may be used as the inorganic filler depending upon the purposes. 
     Examples of the fibrous filler include inorganic fibrous substances such as glass fiber, asbestos fiber, carbon fiber, silica fiber, silica-alumina fiber, zirconia fiber, boron nitride fiber, silicon nitride fiber, boron fiber and potassium titanate fiber, and fibrous metals such as stainless steel, aluminum, titanium, copper, and brass. Among them, glass fiber and carbon fiber are representative fibrous fillers. It is also possible to use high-melting organic fibrous materials such as polyamides, fluororesins, and acrylic resins. 
     Examples of the particulate fillers include carbon black, silicates such as silica, quartz powder, glass bead, glass powder, calcium silicate, aluminum silicate, kaolin, talc, clay, diatomaceous earth and wollastonite, metallic oxides such as iron oxide, titanium oxide and alumina, metal salts of carbonic acid such as calcium carbonate and magnesium carbonate, metal salts of sulfuric acid such as calcium sulfate and barium sulfate, and other fillers such as silicon carbide, silicon nitride, boron nitride, and various powdery metals. 
     Examples of the flaky filler include mica, glass flake, and various metal foils. 
     These inorganic fillers may be used alone or in any combination of two or more of them. A combination of a fibrous filler, particularly glass fiber or carbon fiber with a particulate or flaky filler is preferred particularly for the purpose of imparting a combination of mechanical properties with dimensional stability, electrical properties, etc. 
     It is preferred to use a binder or a surface treatment together with the filler according to need. Examples thereof include functional compounds such as epoxy compounds, isocyanate compounds, silane compounds, and titanate compounds. These compounds may be used by previously conducting surface treatment or binding treatment, or alternatively may be added simultaneously in the preparation of the material. 
     The amount of the inorganic filler as component (C) is 0 to 400 parts by weight, preferably 10 to 250 parts by weight per 100 parts by weight of the polyarylene sulfide resin. When the amount is less than 10 parts by weight, the mechanical strengths are poor, while when the amount is too large, not only does it become difficult to conduct molding operation but also there occurs a reduction in the mechanical strengths of the molded article. 
     The composition of the present invention may be mixed with known substances which are added to ordinary thermoplastic and thermosetting resins, i.e., plasticizers, stabilizers such as antioxidants and ultraviolet absorbers, antistatic agents, surface treatments, surfactants, flame retardants, colorants such as dyes and pigments and lubricants for improving the flowability and releasability, lubricating agents, and crystallization accelerators (nucleating agents) depending upon the intended performance in such an amount as will not hinder the purpose of the present invention. 
     The resin composition of the present invention can be prepared by making use of facilities and methods employed in the preparation of ordinary synthetic resin compositions. They include, for example, a method which comprises mixing necessary components, kneading the mixture with a single-screw or twin-screw extruder, and conducting extrusion to prepare pellets for molding; and a method wherein in order to improve the dispersion and mixing of each component, part or the whole of the resin components are pulverized, and mixing and melt extrusion are then conducted. 
     The resin composition thus prepared is molded by injection molding, extrusion molding, vacuum molding, compression molding, etc. and suitable for a molded article combined with a metal or a molded article to be brought into contact with a metal, such as an outsert or an insert, by virtue of less tendency to corrode and stain the metal, particularly useful not only for electrical and electronic components etc. having a metallic contact but also from the general point of view because of less tendency to bring about corrosion and staining of a cylinder mold during fabrication. 
     As is apparent from the foregoing description, the polyarylene sulfide resin composition containing a zinc compound incorporated thereinto according to the present invention exhibits the following effects. 
     (1) Since corrosion and staining of a metal can be greatly reduced when it is used at a high temperature, application to electrical and electronic components having a metallic contact brings about a significant reduction in the trouble of contamination of the contact. Further, the cost of a component can be reduced because it becomes possible to use a polyarylene sulfide resin in preparing a component which could not be prepared without an expensive material hitherto. 
     (2) Excellent thermal resistance, solvent resistance, and flame retardancy characteristic of a polyarylene sulfide resin are maintained. Further, a lowering in the mechanical properties is small. 
     (3) Occurrence of an odor characteristic of a polyarylene sulfide resin composition during kneading and molding is reduced, which contributes to an improvement in the working environment. Further, it is possible to conduct economical and efficient working because corrosion and staining of a cylinder, a mold, etc. hardly occur during molding. 
     (4) Since the additive is inexpensive and has excellent extruding and kneading properties, the resin composition can be produced at a low cost. 
     (5) The additive is non-toxic and safe as opposed to other heavy metals. 
    
    
     EXAMPLES 
     Examples 1 to 14 and Comparative Examples 1 to 7 
     As shown in Table 1, a zinc compound shown in Table 1 was added as component (B) to a substantially linear polyphenylene sulfide resin (trade mark of &#34;Fortron&#34;; a product of Kureha Chemical Industry Co., Ltd.) as component (A) and then mixed therewith by a Henschel mixer for 2 min. 
     Then, an inorganic filler as component (C) was added thereto in an amount shown in Table 1 and mixed by means of a blender for 30 sec. The mixture was kneaded by means of an extruder at a cylinder temperature of 310° C to prepare pellets of a polyphenylene sulfide resin composition. 
     22 g of the pellets were put on the bottom of a test tube having an outer diameter of 30 mm and a height of 150 mm, and a metallic sheet shown in Table 1 was cut into a size of 2 mm×12 mm and suspended with a thread in such a manner that the metallic sheet was positioned at a height of about 60 mm from the uppermost pellets. A stopper was put on the top of the test tube, and the test tube was then placed in a blast dryer to conduct treatment under evaluation test conditions shown in Table 1. The metallic sheet was taken out of the test tube and subjected to visual evaluation of appearance and measurement of electrical resistance of the surface under a contact pressure of 10 g with a milliohmmeter to evaluate corrosive and staining properties of the resin composition. The results are shown in Table 1. 
     The above-described pellets were molded into an ASTM specimen with an injection molding machine at a cylinder temperature of 320° C. and a mold temperature of 150° C., and the specimen was subjected to measurement of the tensile strength and tensile elongation. 
     
                                           TABLE 1__________________________________________________________________________Compositioncomponent (A)polyphenylene component (B) component (C)sulfide resin additive      filler    [pt. wt.] [kind] [pt. wt.]                       [kind]                             [pt. wt.]__________________________________________________________________________Ex. 100       transparent.sup.(a)                0.05   glass.sup.(b)                             701             zinc white    fiberEx. 100       transparent.sup.(a)                0.1    glass.sup.(b)                             702             zinc white    fiberEx. 100       transparent.sup.(a)                1      glass.sup.(b)                             703             zinc white    fiberEx. 100       transparent.sup.(a)                10     glass.sup.(b)                             704             zinc white    fiberEx. 100       transparent.sup.(a)                70     glass.sup.(b)                             705             zinc white    fiberEx. 100       transparent.sup.(a)                1      --    --6             zinc whiteEx. 100       transparent.sup.(a)                1      glass.sup.(b)                             1007             zinc white    fiber                       calcium                             100                       carbonateEx. 100       transparent.sup.(a)                1      glass.sup.(b)                             708             zinc white    fiberEx. 100       transparent.sup.(a)                1      glass.sup.(b)                             709             zinc white    fiberEx. 100       transparent.sup.(a)                1      glass.sup.(b)                             7010            zinc white    fiberEx. 100       zinc ortho-                1      glass.sup.(b)                             7011            carbonate     fiberEx. 100       zinc ortho-                1      glass.sup.(b)                             7012            carbonate     fiberEx. 100       zinc   1      glass.sup.(b)                             7013            hydroxide     fiberEx. 100       zinc   70     glass.sup.(b)                             7014            hydroxide     fiberComp.    100       --     --     glass.sup.(b)                             70Ex. 1                       fiberComp.    100       zinc   1      glass.sup.(b)                             70Ex. 2         oxide.sup.(d) fiberComp.    100       zinc   1      glass.sup.(b)                             70Ex. 3         oxide.sup.(e) fiberComp.    100       --     --     glass.sup.(b)                             100Ex. 4                       fiber                       calcium                             100                       carbonateComp.    100       lithium                1      glass.sup.(b)                             70Ex. 5         carbonate     fiberComp.    100       zinc   1      glass.sup.(b)                             70Ex. 6         sulfate       fiberComp.    100       zinc   1      glass.sup.(b)                             70Ex. 7         chloride      fiber__________________________________________________________________________                       Evaluation of generalEvaluation of corrosion of metal                       properties   evaluation           electrical                evaluation                       tensile                            tensile   test    resistance                of appear-                       strength                            elongation    metal   conditions           [mΩ]                ance   [kgf/cm.sup.2 ]                            [%]__________________________________________________________________________Ex. silver   265° C. × 1 hr           31   small dis-                       1750 1.61                    colorationEx. silver   265° C. × 1 hr           22   slight dis-                       1740 1.62                    colorationEx. silver   265° C. × 1 hr           12   no discolora-                       1650 1.53                    tionEx. silver   265° C. × 1 hr            9   no discolora-                       1400 1.14                    tionEx. silver   265° C. × 1 hr           10   no discolora-                       1320 1.05                    tionEx. silver   265° C. × 1 hr           13   no discolora-                        870 4.06                    tionEx. silver   265° C. × 1 hr            9   no discolora-                       1420 1.07                    tionEx. silver   150° C. × 1 hr           14   no discolora-                       1650 1.58                    tionEx. silver   265° C. × 1 hr           21   slight dis-                       1650 1.59                    colorationEx. alloy.sup.(c)   265° C. × 1 hr           12   no discolora-                       1650 1.510                   tionEx. silver   265° C. × 1 hr            9   no discolora-                       1570 1.411                   tionEx. silver   265° C. × 1 hr           10   no discolora-                       1090 0.912                   tionEx. silver   265° C. × 1 hr           10   no discolora-                       1490 1.313                   tionEx. silver   265° C. × 1 hr            9   no discolora-                       1020 0.914                   tionComp.    silver   265° C. × 1 hr           430  remarkable                       1750 1.6Ex. 1                discolora-                tionComp.    silver   265° C. × 1 hr           175  remarkable                       1720 1.6Ex. 2                discolora-                tionComp.    silver   265° C. × 1 hr           150  remarkable                       1740 1.6Ex. 3                discolora-                tionComp.    silver   265° C. × 1 hr           390  remarkable                       1450 1.0Ex. 4                discolora-                tionComp.    silver   265°  C. × 1 hr           295  remarkable                       1610 1.5Ex. 5                discolora-                tionComp.    silver   265° C. × 1 hr           530  remarkable                       1280 1.0Ex. 6                discolora-                tionComp.    silver   265° C. × 1 hr           815  remarkable                       1350 1.1Ex. 7                discolora-                tion__________________________________________________________________________ Note) .sup.(a) 2ZnCO.sub.3.3Zn(OH).sub.2 .sup.(b) chopped strand having a diameter of 13 μm and a length of 3 m .sup.(c) silverpalladium-copper alloy .sup.(d) zinc white having a ZnO content of 98.5% and a mean particle diameter of 0.65 μm (according to American process) .sup.(e) zinc white having a ZnO content of 99.7% and a mean particle diameter of 0.27 μm (according to French process) 
    
     Example 15 and Comparative Example 8 
     Pellets prepared in Example 3 and Comparative Example 1 were injection molded into components having a brass-nickel-plated lead frame inserted thereinto by an injection molding machine through the use of a mold for a rotary switch housing at a cylinder temperature of 320° C. and a mold temperature of 150° C. 
     Separately, the same pellets were injection molded into rotor components by making use of a mold for a rotor component, and a brass-nickel-plated contact was then jointed thereto by caulking. Further, an O-ring made of silicone rubber was mounted on the rotors. The same pellets were molded into switch lid components by making use of a mold for a switch lid, and the rotors were respectively integrated into the switch lids. Then, the switch lids were inserted into the housings, and the lids were subjected to ultrasonic welding to assemble rotary switches. The rotary switches thus prepared were treated in a blast dryer under test conditions shown in Table 2 and then subjected to functional tests. The results are shown in Table 2. 
     Example 16 and Comparative Example 9 
     Pellets prepared in Example 3 and Comparative Example 1 were injection molded into rotor components by an injection molding machine through the use of a mold for a rotary component at a cylinder temperature of 320° C. and a mold temperature of 150° C. A silver-palladium-copper alloy contact was jointed thereto by caulking to prepare rotor components. 
     These rotor components were assembled through an O-ring to a separately prepared epoxy resin housing having a resistor mounted thereon to prepare a rotary switch (semifixed volume). The molded components thus prepared were treated in a blast dryer under test conditions shown in Table 3 and then subjected to functional tests. The results are shown in Table 3. 
     
                                           TABLE 2__________________________________________________________________________    Composition    component (A)            component (B)                     component (C)    polyphenylene            additive fillerMolded   sulfide resin [pt.     [pt.         Evaluationarticle  [pt. wt.]            [kind]                  wt.]                     [kind]                           wt.]                              Combination metal                                        test conditions                                                results__________________________________________________________________________Ex. rotary    100     trans-                  1  glass.sup.(b)                           70 insert molding of                                        150 × 168                                                excellent current15  switch       parent.sup.(a)                     fiber    brass-nickel-plated                                                value in changeover            zinc white        lead frame        test of switchComp.    rotary    100     --    -- glass.sup.(b)                           70 insert molding of                                        150 × 168                                                abnormal currentEx. switch                fiber    brass-nickel-plated                                                value in changeover8                                  lead frame        test of__________________________________________________________________________                                                switch Note) .sup.(a) 2ZnCO.sub.3.3Zn(OH).sub.2 .sup.(b) chopped strand having a diameter of 13 μm and a length of 3 m 
    
     
                                           TABLE 3__________________________________________________________________________    Composition    component (A)            component (B)                     component (C)    polyphenylene            additive fillerMolded   sulfide resin [pt.     [pt.         Evaluationarticle  [pt. wt.]            [kind]                  wt.]                     [kind]                           wt.]                              Combination metal                                        test conditions                                                results__________________________________________________________________________Ex. semifixed    100     trans-                  1  glass.sup.(b)                           70 integration of                                        265 × 1                                                excellent                                                resistance16  volume       parent.sup.(a)                     fiber    silver-palladium- value in changeover            zinc white        copper alloy frame                                                testComp.    semifixed    100     --    -- glass.sup.(b)                           70 integration of                                        265 × 1                                                abnormal resistanceEx. volume                fiber    silver-palladium- value in changeover9                                  copper alloy frame                                                test__________________________________________________________________________ Note) .sup.(a) 2ZnCO.sub.3.3Zn(OH).sub.2 .sup.(b) chopped strand having a diameter of 13 μm and a length of 3 m 
    
     Examples 17 and Comparative Example 10 
     As shown in Table 4, a zinc compound shown in Table 4 was added as component (B) to a polyphenylene sulfide resin (trade mark of &#34;Fortron KPS&#34;; a product of Kureha Chemical Industry Co., Ltd.) as component (A) and then mixed therewith by a Henschel mixer for 2 min. 
     Then, an inorganic filler (calcium carbonate) as component (C) was added thereto in an amount shown in Table 4 and mixed by means of a blender for 30 sec. The mixture was kneaded by means of an extruder at a cylinder temperature of 310° C. to prepare pellets of a polyphenylene sulfide resin composition. The obtained pellets were molded into an injection molded article with an injection molding machine through the use of a mold for a light reflector plate at a cylinder temperature of 320° C. and a mold temperature of 150° C. This molded article was subjected to ultrasonic cleaning with acetone, and aluminum was vacuum deposited in a thickness of 20 μm on the reflecting surface to prepare a light reflector plate. The reflector plate thus prepared was placed in a blast dryer to conduct treatment under evaluation test conditions shown in Table 4 and then subjected to appearance evaluation. The results are shown in Table 4. 
     
                                           TABLE 4__________________________________________________________________________    Composition    component (A)            component (B)                     component (C)    polyphenylene            additive fillerMolded   sulfide resin [pt.     [pt.         Evaluationarticle  [pt. wt.]            [kind]                  wt.]                     [kind]                           wt.]                              Combination metal                                        test conditions                                                results__________________________________________________________________________Ex. light    100     trans-                  1  calcium                           150                              vacuum deposition                                        200° C. × 3                                                excellent17  reflector    parent.sup.(a)                     carbonate                              of aluminum in    surface    plate        zinc white        a thickness of 20 μmComp.    light    100     --    -- calcium                           150                              vacuum deposition                                        200° C. × 3                                                occurrence ofEx. reflector             carbonate                              of aluminum in    mixture corro-10  plate                          a thickness of 20 μm                                                sion and                                                staining spots                                                on the__________________________________________________________________________                                                surface Note) .sup.(a) 2ZnCO.sub.3.3Zn(OH).sub.2