Abstract:
The present invention relates to a process for producing a resin useful in plastic lenses, to plastic lenses containing the resin and to a process for producing the lenses.

Description:
BACKGROUND OF THE INVENTION 
     1. Field of the Invention 
     The present invention relates to a resin having a high refractive index that is useful for preparing plastic lenses, lenses comprising the resin and processes for preparing the same. 
     2. Description of the Prior Art 
     Plastic lenses have been rapidly popularized in recent years for use in optical elements such as lenses of eyeglasses and cameras. Plastic lenses are lightweight, less fragile than inorganic lenses and are capable of being dyed with ease. 
     A resin currently widely used for producing lenses for optical elements is a radical polymerization product of diethylene glycol bisallyl carbonate (herein-after abbreviated as DAC). The resin has excellent impact resistance, is lightweight, has prominent dye-affinity and good machinability including cutting ability and polishing ability. 
     However, lenses prepared from the resin have a smaller refractive index (n D  =1.50) than glass lenses (n D  =1.52). In order to obtain equivalent optical properties to glass lenses, it is necessary to increase the center thickness, peripheral thickness and curvature of the lens and hence the lens as a whole becomes very thick. Therefore, resins having a higher refractive index that are useful for making lenses are desired. 
     Resins having higher refractive indices that have been used to produce plastic lenses include polyurethane base resins obtained by reacting isocyanate compounds with hydroxyl compounds such as diethylene glycol (disclosed in Japanese Patent Laid-Open No. 136601/1982, U.S. Pat. No. 4,443,588), with halogen containing hydroxyl compounds such as tetrabromobisphenol-A (Japanese Patent Laid-Open No. 164615/1983) and with diphenyl sulfide linkage containing hydroxyl compounds (Japanese Patent Laid-Open No. 194401/1985). 
     The present inventors have previously invented resins having high refractive indices that are useful for preparing lenses by reacting isocyanate compounds with sulfur containing hydroxyl compounds (Japanese Patent Laid-Open No. 217229/1985, U.S. Pat. No. 4,680,369 and U.S. Pat. No. 4,780,522) or with polythiol compounds (Japanese Patent Laid-Open No. 199016/1985, U.S. Pat. No. 4,689,378, Japanese Patent Laid-Open Nos. 267316/1987 and 46213/1988, and U.S. Pat. No. 4,775,733). The present inventors prepared plastic lenses from their polyurethane base resins. 
     In molding the polyurethane base lens, it is usually difficult to release the polymerized lens from the mold due to adhesion between the polyurethane compounds and the mold. In order to improve the mold releasing property, the present inventors previously proposed a process in which an external mold releasing agent is used (Japanese Patent Laid-Open No. 267316/1987) or a process in which a polyolefin resin mold is used (Japanese Patent Laid-Open No. 236818/1987) to improve the mold release properties in preparing lenses. 
     Although the refractive indices of these lenses are higher than those of lenses prepared from DAC, the maximum refractive index of these lenses is between approximately 1.65 and 1.68. Further improvement of the refractive index is desired. 
     The above methods are still insufficient for improving the mold releasing property in casting polymerization of polyurethane base lenses. 
     In prior art processes in which external mold releasing agents are used, a portion of the agent that is applied to the inner surface of a mold migrates to the surface and interior of the polymerized lens which results in problems such as nonuniformity of the surface of the lens and turbidity of the lens. When a mold is used repeatedly, mold releasing treatment is required in each molding cycle. Such treatment lowers productivity in producing the lens and thus is extremely uneconomical in industrial production. 
     When the polyolefin resin molds are applied, the resin molds are deformed at elevated temperatures which causes large profile irregularities on the molded lens. Thus, the resin molds cannot be applied to articles requiring high accuracy on the molded surface. 
     SUMMARY OF THE INVENTION 
     The present invention overcomes the problems and disadvantages of the prior art by providing a resin having improved properties over prior art resins, a process for producing the same, and a lens containing the resin having superior properties over prior art lenses and a method of producing the same. 
     An object of the present invention is to provide a colorless and transparent resin having a high refractive index and low dispersion of refractive index which is suitable for use in producing a plastic lens which is lightweight, and is excellent in weatherability and impact resistance. 
     Another object of the invention is to provide a lens having high accuracy in the profile of surface and excellent optical properties and a process for producing the same which does not include specific release treatment of the inner mold surface of the mold used to make the lens. 
     Additional objects and advantages of the invention will be set forth in part in the description which follows, and in part will be obvious from the description, or may be learned by practice of the invention. The objects and advantages of the invention will be realized and attained by means of the instrumentalities and combinations, particularly pointed out in the appended claims. 
     To achieve the objects and in accordance with the purpose of the invention, as embodied and broadly described herein, the invention provides a resin and a process for preparing the resin comprising reacting one or more isothiocyanate compounds with one or more active-hydrogen containing compounds selected from the group consisting of polyol compounds, polythiol compounds and mercapto group containing hydroxy compounds. 
     The invention also provides a lens containing the resin and a process for preparing the lens comprising adding an internal mold releasing agent to a mixture of one or more isothiocyanate compounds and one or more active-hydrogen containing compounds and cast polymerizing the mixture to form a lens. 
     The resin of the invention is colorless, transparent, has a high refractive index and low dispersion of refractive index and is particularly suitable for producing lenses. 
     The lenses of the invention are excellent in weatherability, lightweight and exhibits excellent impact resistance. The lens has excellent optical properties and is very accurate in the profile of the surface. 
    
    
     DESCRIPTION OF THE PREFERRED EMBODIMENTS 
     Reference will now be made in detail to the present preferred embodiments of the invention. 
     Exemplary suitable isothiocyanate compounds for use in the process of the present invention include polyisothiocyanate compounds and isothiocyanate compounds containing isocyanate groups. Such isothiocyanate compounds may contain one or more sulfur atoms in addition to the isothiocyanate groups. Exemplary suitable polyisothiocyanate compounds contain two or more -NCS groups per molecule and include, for example, aliphatic polyisothiocyanate compounds such as ethane-1,2-diisothiocyanate, propane-1,3-diisothiocyanate, butane-1,4-diisothiocyanate, hexane-1,6-diisothiocyanate, p-phenylenediisopropylidene diisothiocyanate; alicyclic polyisothiocyanate compounds such as cyclohexane diisothiocyanate; aromatic polyisothiocyanate compounds such as benzene-1,2-diisothiocyanate, benzene-1,3-diisothiocyanate, benzene-1,4-diisothiocyanate, toluene2,4-diisothiocyanate, m-xylene-2,5-diisothiocyanate, 1,1&#39;-biphenyl-4,4&#39;-diisothiocyanate, 1,1&#39;-methylenebis(benzene-4-isothiocyanate), 1,1&#39;-methylenebis(2-methylbenzene-4-benzene-4-isothiocyanate), 1,1&#39;-methylenebis(3-methylbenzene-4-isothiocyanate), 1,1&#39;-(1,2-ethane-diyl)bis(benzene-4-isothiocyanate), benzophenone-4,4&#39;-diisothiocyanate, 3,3&#39;-dimethylbenzophenone-4,4&#39;-diisothiocyanate, benzanilide-3,4&#39;-diisothiocyanate, diphenylether4,4&#39;-diisothiocyanate, and diphenylamine-4,4&#39;-diisothiocyanate; heterocyclic polyisothiocyanate compounds such as 1,3,5-triazine-2,4,6-triisothiocyanate; and carbonyl polyisothiocyanate compounds such as hexanedioyl diisothiocyanate, nonanedioyl diisothiocyanate, carbonic diisothiocyanate, benzene-1,3-dicarbonyl diisothiocyanate, benzene-1,4-dicarbonyl diisothiocyanate and (2,2&#39;-bipyridine)-4,4&#39;-diisothiocyanate. 
     Exemplary suitable polyisothiocyanate compounds containing at least one sulfur atom in addition to the isothiocyanate groups include sulfur containing aliphatic polyisothiocyanates such as thiobis(3-isothiocyanatopropane), thiobis(2-isothiocyanatoethane) and dithiobis(2-isothiocyanatoethane); sulfur containing aromatic polyisothiocyanates such as 1-isothiocyanato4-{(2-isothiocyanato)sulfonyl}benzene, thiobis(4-isothiocyanatobenzene), sulfonylbis(4-isothiocyanatobenzene), sulfinylbis(4-isothiocyanatobenzene), dithiobis(4-isothiocyanatobenzene), 4-isothiocyanato-1-{(4-isothiocyanatophenyl)sulfonyl}-2-methoxybenzene, 4-methyl-3-isothiocyanatobenzenesulfonyl-4&#39;-isothiocyanate phenyl ester and 4-methyl-3-isothiocyanatobenzenesulfonylanilide3&#39;-methyl-4&#39;-isothiocyanate; and sulfur containing heterocyclic compounds such as thiophene-2,5-diisothiocyanate and 1,4-dithian-2,5-diisothiocyanate. 
     Exemplary suitable isocyanate group containing isothiocyanate compounds include aliphatic and alicyclic compounds such as propane-1-isocyanato-3-isothiocyanate, pentane-1-isocyanato-5-isothiocyanate, hexane-1-isocyanato-6-isothiocyanate, isothiocyanatocarbonyl isocyanate and cyclohexane-1-isocyanato-4-isothiocyanate; heterocyclic compounds such as 1,3,5-triazine-2-isocyanato-4,6-diisothiocyanate; and compounds having sulfur atoms in addition to isothiocyanate groups such as 4-isocyanato-4&#39;-isothiocyanatodiphenyl sulfide and 2-isocyanato-2&#39;-isothiocyanatodiethyl disulfide. 
     Exemplary suitable derivatives of the above isothiocyanate compounds for use in the invention include halogenated isothiocyanates such as chlorinated isothiocyanates and brominated isothiocyanates, alkylated isothiocyanates, alkoxylated isothiocyanates, nitrated isothiocyanates, prepolymer type addition products with polyhydric alcohols, carbodiimide modified isothiocyanates, urea modified isothiocyanates, biuret modified isothiocyanates, dimerization products and trimerization products. 
     The isothiocyanate compounds may be used singly or in combination as a mixture. 
     Exemplary active-hydrogen containing compounds suitable for use in the process of the invention are those selected from the group consisting of polyol compounds, polythiol compounds and mercapto group containing hydroxy compounds. 
     Exemplary suitable polyol compounds include aliphatic polyols such as ethylene glycol, diethylene glycol, propylene glycol, dipropylene glycol, butyleneglycol, neopentyl glycol, glycerol, trimethylolethane, trimethylolpropane, butanetriol, 1,2-methylglucoside, pentaerythritol, dipentaerythritol, tripentaerythritol, sorbitol, erythritol, threitol, ribitol, arabinitol, xylitol, allitol, mannitol, duloitol, iditol, glycol, inositol, hexanetriol, triglycerol, diglycerol, triethylene glycol, polyethylene glycol, tris(2-hydroxyethyl)isocyanurate, cyclobutanediol, cyclopentanediol, cyclohexanediol, cycloheptonediol, cyclooctanediol, cyclohexanedimethanol, hydroxypropylcyclohexanol, tricyclo[5,2,1,0 2 .6 ]decanedimethanol, bicyclo[4,3,0]nonanediol, dicyclohexanediol, tricyclo[5,3,1,1]dodecanediol, bicyclo[4,3,0]nonanedimethanol, tricyclo[5,3,1,1]dodecanediethanol, hydroxypropyltricyclo[5,3,1,1]dodecanol, spiro[3,4]octanediol, butylcyclohexanediol, 1,1&#39;-bicyclohexylidenediol, cyclohexanetriol, maltitol, lactitol; aromatic polyols such as dihydroxynaphthalene, trihydroxynaphthalene, tetrahydroxynaphthalene, hydroquinone, resorcinol, catechol, benzenetriol, biphenyltetraol, pyrogallol, (hydroxynaphthyl)pyrogallol, trihydroxyphenanthrene, bisphenol A, bisphenol-F, xylyleneglycol, di(2-hydroxyethoxy)benzene, bisphenol A-bis(2-hydroxyethylether), tetrabromobisphenol-A, tetrabromobisphenol A-bis(2-hydroxyethylether); halogenated polyols such as dibromoneopentylglycol; and high molecular polyols such as epoxy resin. 
     Additional exemplary polyols suitable for use in the process of the invention include condensed products of above mentioned polyol compounds with organic acids such as oxalic acid, glutamic acid, adipic acid, acetic acid, propionic acid, cyclohexanecarboxylic acid, β-hydroxycyclohexanepropionic acid, dimer acid, phthalic acid, isophthalic acid, salicylic acid, 3-bromopropionic acid, 2-bromoglycolic acid, cyclohexanedicarboxylic acid, pyromellitic acid, butanetetracarboxylic acid and bromophthalic acid; addition products of alkylene oxides such as ethylene oxide and propylene oxide to the above polyol compounds and to alkylenepolyamine: and sulfur atom containing polyols such as bis[4-(hydroxyethoxy)phenyl]sulfide, bis[4-(2hydroxypropoxy)phenyl]sulfide, bis[4-(2,3-dihydroxypropoxy)phenyl]sulfide, bis[4-(4-hydroxycyclohexyloxy)phenyl]sulfide, bis[2-methyl-4-(hydroxyethoxy)6-butylphenyl]sulfide, compounds obtained by the addition of ethylene oxide and/or propylene oxide to sulfur containing polyols in an amount of not more than about 3 moles per mole of hydroxyl group of the polyols, di(2-hydroxyethyl) sulfide, 1,2-bis(2-hydroxyethylmercapto)ethane, bis(2-hydroxyethyl)disulfide, 1,4-dithian-2,5-diol, bis(2,3-dihydroxypropyl)sulfide, tetrakis(4-hydroxy-2-thiabutyl)methane, bis(4-hydroxyphenyl) sulfone (Trade Mark; Bisphenol-S), tetramethylbisphenol-S, 4,4&#39;-thiobis(6-tert-butyl-3-methylphenol) and 1,3-bis(2-hydroxyethylthioethyl)cyclohexane. 
     Exemplary suitable polythiols for use in the process of the invention include aliphatic polythiols such as methanedithiol, 1,2-ethanedithiol, 1,1-propanedithiol, 1,2-propanedithiol, 1,3-propanedithiol, 2,2-propanedithiol, 1,6-hexanedithiol, 1,2,3-propanetrithiol, 1,1-cyclohexanedithiol, 1,2-cyclohexanedithiol, 2,2-dimethylpropane-1,3-dithiol, 3,4-dimethoxybutane-1,2-dithiol, 2-methylcyclohexane-2,3-dithiol, bicyclo[2,3,1]hepta-exo-cis-2,3-dithiol, 1,1-bis(mercaptomethyl)cyclohexane, thiomalic acid bis(2-mercaptoethyl ester), 2,3-dimercaptosuccinic acid 2-mercaptoethyl ester, 2,3-dimercapto-1-propanol 2-mercaptoacetate, 2,3-dimercapto-1-propanol 3-mercaptopropionate, diethylene glycol bis(2-mercaptoacetate), diethylene glycol bis(3-mercaptopropionate), 1,2-dimercaptopropyl methyl ether, 2,3-dimercaptopropyl methyl ether, 2,2-bis(mercaptomethyl)-1,3-propanedithiol, bis(2-mercaptoethyl) ether, ethylene glycol bis(2-mercaptoacetate), ethylene glycol bis(3-mercaptopropionate), trimethylolpropane bis(2-mercaptoacetate), trimethylolpropane bis(3-mercaptopropionate), pentaerythritol tetrakis(2-mercaptoacetate) and pentaerythritol tetrakis(3-mercaptopropionate); aromatic polythiols such as 1,2-dimercaptobenzene, 1,3-dimercaptobenzene, 1,4-dimercaptobenzene, 1,2-bis(mercaptomethyl)benzene, 1,3-bis(mercaptomethyl)benzene, 1,4-bis(mercaptomethyl)benzene, 1,2-bis(mercaptoethyl)benzene, 1,3-bis(mercaptoethyl)benzene, 1,4-bis(mercaptoethyl)benzene, 1,2-bis(mercaptomethyleneoxy)benzene, 1,3-bis(mercaptomethyleneoxy)benzene, 1,4-bis(mercaptomethyleneoxy)benzene, 1,2-bis(mercaptoethyleneoxy)benzene, 1,3-bis(mercaptoethylenoxy)benzene, 1,4-bis(mercaptoethyleneoxy)benzene, 1,2,3-trimercaptobenzene, 1,2,4-trimercaptobenzene, 1,3,5-trimercaptobenzene, 1,2,3-tris(mercaptomethyl)benzene, 1,2,4-tris(mercaptomethyl)benzene, 1,3,5-tris(mercaptomethyl)benzene, 1,2,3-tris(mercaptoethyl)benzene, 1,2,4-tris(mercaptoethyl)benzene, 1,3,5-tris(mercaptoethyl)benzene, 1,2,3-tris(mercaptomethyleneoxy)benzene, 1,2,4-tris(mercaptomethyleneoxy)benzene, 1,3,5-tris(mercaptomethyleneoxy)benzene, 1,2,3-tris(mercaptoethyleneoxy)benzene, 1,2,4-tris(mercaptoethyleneoxy)benzene, 1,3,5-tris(mercaptoethyleneoxy)benzene, 1,2,3,4-tetramercaptobenzene, 1,2,3,5-tetramercaptobenzene, 1,2,4,5-tetramercaptobenzene, 1,2,3,4-tetrakis(mercaptomethyl)benzene, 1,2,3,5-tetrakis(mercaptomethyl)benzene, 1,2,4,5-tetrakis(mercaptomethyl)benzene, 1,2,3,4-tetrakis(mercaptoethyl)benzene, 1,2,3,5-tetrakis(mercaptoethyl)benzene, 1,2,4,5-tetrakis(mercaptoethyl)benzene, 1,2,3,4-tetrakis(mercaptomethyleneoxy)benzene, 1,2,3,5-tetrakis(mercaptomethyleneoxy)benzene, 1,2,4,5-tetrakis(mercaptomethyleneoxy)benzene, 1,2,3,4-tetrakis(mercaptoethyleneoxy)benzene, 1,2,3,5-tetrakis(mercaptoethyleneoxy)benzene, 1,2,4,5-tetrakis(mercaptoethyleneoxy)benzene, 2,2&#39;-dimercaptobiphenyl, 4,4&#39;-dimercaptobiphenyl, 2,5-toluenedithiol, 3,4-toluenedithiol, 1,4-naphthalenedithiol, 1,5-naphthalenedithiol, 2,6-naphthalenedithiol, 2,7-naphthalenedithiol, 2,4-dimethylbenzene-1,3-dithiol, 4,5-dimethylbenzene-1,3-dithiol, 9,10-anthracenedimethanethiol, 1,3-di(p-methoxyphenyl)propane-2,2-dithiol, 1,3-diphenylpropane-2,2-dithiol, phenylmethane-1,1-dithiol and 2,4-di(p-mercaptophenyl)pentane; chlorinated and brominated aromatic polythiols such as 2,5-dichlorobenzene-1,3-dithiol, 1,3-(p-chlorophenyl)propane-2,2-dithiol, 3,4,5-tribromo-1,2-dimercaptobenzene and 2,3,4,6-tetrachloro-1,5-bis(mercaptomethyl)benzene; heterocyclic polythiols such as 2-methylamino-3,6-dithiol-sym-triazine, 2-ethylamino-4,6-dithiol-sym-triazine, 2-amino-4,6-dithiol-sym-triazine, 2-morpholino-4,6-dithiol-symtriazine, 2-cyclohexylamino-4,6-dithiol-sym-triazine, 2-methoxy-4,6-dithiol-sym-triazine, 2-phenoxy-4,6-dithiol-sym-triazine, 2-thiobenzeneoxy-4,6-dithiolsym-triazine and 2-thiobutyloxy-4,6-dithiol-sym-triazine; aromatic polythiols containing sulfur atoms in addition to mercapto groups such as 1,2-bis(mercaptomethylthio)benzene, 1,3-bis(mercaptomethylthio)benzene, 1,4-bis(mercaptomethylthio)benzene, 1,2-bis(mercaptoethylthio)benzene, 1,3-bis(mercaptoethylthio)benzene, 1,4-bis(mercaptoethylthio)benzene, 1,2,3-tris(mercaptomethylthio)benzene, 1,2,4-tris(mercaptomethylthio)benzene, 1,3,5tris(mercaptomethylthio)benzene, 1,2,3-tris(mercaptoethylthio)benzene, 1,2,4-tris(mercaptoethylthio)benzene, 1,3,5-tris(mercaptoethylthio)benzene, 1,2,3,4-tetrakis(mercaptomethylthio)benzene, 1,2,3,5-tetrakis(mercaptomethylthio)benzene, 1,2,4,5-tetrakis(mercaptomethylthio)benzene, 1,2,3,4-tetrakis(mercaptoethylthio)benzene, 1,2,3,5-tetrakis(mercaptoethylthio)benzene, 1,2,4,5-tetrakis(mercaptoethylthio)benzene and aromatic ring alkylated derivatives of these polythiols; aliphatic polythiols containing sulfur atoms in addition to mercapto groups such as bis(mercaptomethyl) sulfide, bis(mercaptoethyl) sulfide, bis(mercaptopropyl) sulfide, bis(mercaptomethylthio)methane, bis(2-mercaptoethylthio)methane, bis(3-mercaptopropyl)methane, 1,2-bis(mercaptomethylthio)ethane, 1,2-bis(2-mercaptoethylthio)ethane, 1,2-bis(3-mercaptopropyl)ethane, 1,3-bis(mercaptomethylthio)propane, 1,3-bis(2-mercaptoethylthio)propane, 1,3-bis(3-mercaptopropylthio)propane, 1,2,3-tris(mercaptomethylthio)propane, 1,2,3-tris(2-mercaptoethylthio)propane, 1,2,3-tris(3-mercaptopropylthio)propane, tetrakis(mercaptomethylthiomethyl)methane, tetrakis(2-mercaptoethylthiomethyl)methane, tetrakis(3-mercaptopropylthiomethyl)methane, bis(2,3-dimercaptopropyl) sulfide, 2,5-dimercapto-1,4-dithian, bis(mercaptomethyl) disulfide, bis(mercaptoethyl) disulfide and bis(mercaptopropyl) disulfide; esters of mercaptoacetic acid, mercaptopropionic acid and mercaptobutyric acid with sulfur containing compounds such as hydroxymethyl sulfide bis(2-mercaptoacetate), hydroxymethyl sulfide bis(3-mercaptopropionate), hydroxyethyl sulfide bis(2-mercaptoacetate), hydroxyethyl sulfide bis(3-mercaptopropionate), hydroxypropyl sulfide bis(2-mercaptoacetate), hydroxypropyl sulfide bis(3-mercaptopropionate), hydroxymethyl disulfide bis(2-mercaptoacetate), hydroxymethyl disulfide bis(3-mercaptopropionate), hydroxyethyl disulfide bis(2-mercaptoacetate), hydroxyethyl disulfide bis(3-mercaptopropionate), hydroxypropyl disulfide bis(2-mercaptoacetate), hydroxypropyl disulfide bis(3-mercaptopropionate), 2-mercaptoethyl ether bis(2-mercaptoacetate), 2-mercaptoethyl ether bis(3-mercaptopropionate), 1,4-dithian-2,5-diol bis(2-mercaptoacetate), 1,4-dithian-2,5-diol bis(3-mercaptopropionate), thiodiglycolic acid bis(2-mercaptoethyl ester), thiodipropionic acid bis(2-mercaptoethyl ester), 4,4-thiodibutyric acid bis(2-mercaptoethyl ester), dithiodiglycolic acid bis(2-mercaptoethyl ester), dithiodipropionic acid bis(2-mercaptoethyl ester), 4,4-dithiodibutyric acid bis(2-mercaptoethyl ester), thiodiglycolic acid bis(2,3-dimercaptopropyl ester), thiodipropionic acid bis(2,3-dimercaptopropyl ester), dithiodiglycolic acid bis(2,3-dimercaptopropyl ester) and dithiodipropionic acid bis(2,3-dimercaptopropyl ester); and heterocyclic compounds containing sulfur atoms in addition to mercapto groups such as 3,4-thiophene-dithiol and 2,5dimercapto-1,3,4-thiadiazol. 
     Exemplary suitable mercapto group containing hydroxy compounds for use in the process of this invention include mercaptoalkanols, mercaptocycloalkanols and mercapto phenols such as 2-mercaptoethanol, 3-mercapto1,2-propanediol, glycerol di(mercaptoacetate), 1-hydroxy4-mercaptocyclohexane, 2,4-dimercaptophenol, 2-mercaptohydroquinone, 4-mercaptophenol, 3,4-dimercapto-2-propanol, 1,3-dimercapto-2-propanol, 2,3-dimercapto-1propanol, 1,2-dimercapto-1,3-butanediol, pentaerythritol tris(3-mercaptopropionate), pentaerythritol mono(3-mercaptopropionate), pentaerythritol bis(3-mercaptopropionate), pentaerythritol tris(thioglycolate), pentaerythritol tetrakis(3-mercaptopropionate); and mercapto group and sulfur atom containing alkanols and phenols such as hydroxymethyltris(mercaptoethylthiomethyl)methane, 1-hydroxyethylthio-3-mercaptoethylthiobenzene, 4-hydroxy-4&#39;-mercaptodiphenyl sulfone, 2-(2-mercaptoethylthio)ethanol, dihydroxyethyl sulfide mono(3-mercaptopropionate), dimercaptoethane monosalicylate, and hydroxyethylthiomethyl-tris(mercaptoethylthiomethyl)methane. 
     Halogenated derivatives of these active-hydrogen containing compounds such as chlorinated derivatives and brominated derivatives may also be used. 
     These active-hydrogen containing compounds may be used singly or in combination as a mixture. 
     The isothiocyanate compounds and the active-hydrogen containing compounds are employed in amount of from about 0.5 to about 3.0 moles of total functional isocyanate and isothiocyanate groups per mole of total hydroxyl and mercapto groups, preferably from about 0.5 to about 1.5 moles of sum of functional isocyanate group and isothiocyanate group per mole of sum of hydroxyl group and mercapto group. 
     A portion of the isothiocyanate compounds used in the process of this invention may be replaced by polyisocyanate compounds. 
     Various additives such as chain extending agents, cross linking agents, light stabilizers, ultraviolet absorbers, antioxidants, oil soluble dyestuffs and fillers may be incorporated to achieve particular desired properties. 
     Known catalysts which are used for the preparation of polyurethane may also be used, if necessary, to adjust the reaction rate in the desired range. 
     Exemplary suitable compounds for use as an internal mold releasing agent in the process of the invention include fluorine containing nonionic surface active agents, silicon containing nonionic surface active agents, alkyl quaternary ammonium salts, acid phosphate esters, liquid paraffins, waxes, higher fatty acids and their salts, higher fatty acid esters, higher aliphatic alcohols, bisamides, polysiloxanes, and adducts of ethylene oxide to aliphatic amines. 
     The internal mold releasing agent is suitably selected on the basis of monomer combination, polymerization conditions, economy and readiness in handling. The agent may be used singly or as a mixture of two or more such agents. 
     Exemplary suitable fluorine containing nonionic surface active agents and silicon containing nonionic surface active agents suitable for use in the process of the invention include compounds containing perfluoroalkyl groups or dimethyl polysiloxane groups and hydroxyalkyl groups or phosphate ester groups. Exemplary suitable fluorine containing nonionic surface active agents include Unidain™: DS-401 and DS-403 (Products of Daikin Kogyo Co., Ltd.) and F-Top™; EF-122A, EF-126 and EF-301 (Products of Shin-Akita Chemical Co., Ltd.). An exemplary suitable silicon containing nonionic surface active agent is a trial product Q2-120A of Dow Chemical Co. 
     Exemplary suitable alkyl quaternary ammonium salts for use in the process of the invention include cationic surface active agents such as alkyl quaternary ammonium halogenides, phosphates and sulfates such as trimethylcetyl ammonium chloride, trimethylstearyl ammonium chloride, dimethylethylcetyl ammonium chloride, triethyldodecyl ammonium chloride, trioctylmethyl ammonium chloride, and diethylcyclohexyldodecyl ammonium chloride. 
     Exemplary suitable acid phosphate esters for use in the process of the invention include isopropyl acid phosphate, diisopropyl acid phosphate, butyl acid phosphate, dibutyl acid phosphate, octyl acid phosphate, dioctyl acid phosphate, isodecyl acid phosphate, diisodecyl acid phosphate, tridecanol acid phosphate, and bis(tridecanol acid)phosphate. 
     Exemplary suitable metal salts of higher fatty acid for use in this invention include zinc, calcium, magnesium, nickel and copper salts of stearic acid, oleic acid, octanoic acid, lauric acid, behenic acid and ricinoleic acid such as zinc stearate, zinc oleate, zinc palmitate, zinc laurate, calcium stearate, calcium oleate, calcium palmitate, calcium laurate, magnesium stearate, magnesium oleate, magnesium laurate, magnesium palmitate, nickel stearate, nickel oleate, nickel palmitate, nickel laurate, copper stearate, copper oleate copper laurate, and copper palmitate. 
     Exemplary suitable higher fatty acid esters for use in the process of the invention include esters obtained by the reaction of higher fatty acids such as stearic acid, oleic acid, octanoic acid, lauric acid and ricinoleic acid with alcohols such as ethylene glycol, propylene glycol, butanediol, neopentyl glycol and hexanediol. 
     The internal mold releasing agent may be used singly or in combination. The total amount of the releasing agents used is from about 0.1 to about 10,000 ppm, preferably from about 1 to about 5,000 ppm per sum of the isothiocyanate compounds and active-hydrogen containing compounds. When used in an amount less than 0.1 ppm, demolding ability becomes poor. When used in an amount greater than 10,000 ppm, the molded lens causes haze. The excess amount also results in poor profile accuracy of the lens surface due to premature release of the molded lens from the mold surface during polymerization. 
     The lens of the invention can usually be produced by casting polymerization. One or more isothiocyanate compounds are preferably mixed with one or more active-hydrogen containing compounds and internal mold releasing agents, incorporated with additives, catalysts or the like if necessary, and then poured into a mold to carry out polymerization. In this step, the resultant mixture is usually deaerated prior to pouring to prevent bubbles in the molded lens. 
     Although the temperature and time of polymerization differ depending upon the type of monomer and additives such as mold releasing agent, the polymerization is generally carried out for from about 0.5 to about 72 hours at a temperature of from about -50° C. to about 200° C., preferably from room temperature to about 150° C., more preferably from room temperature to about 120° C. 
     Annealing of the polymerized lens may be conducted when necessary. 
     The polyurethane base lens obtained has a high profile accuracy of the molded surface and excellent optical properties, is lightweight, excellent in impact resistance and suitable for use as eyeglass lenses and camera lenses. 
     The high refraction lens of this invention can be imparted with the following properties: antireflection, surface hardness, abrasion resistance, chemical resistance, fog resistance and fashionability by subjecting the lens to physical or chemical treatment such as surface polishing, antistatic treatment, hard coating, antireflection coating, dyeing and dimming. 
     This invention will hereinafter be illustrated by way of the following examples and comparative examples, which are intended to be purely exemplary of the invention. In testing the properties of the lens resin obtained, refractive index, Abbe&#39;s number, weatherability, mold release property and appearance were measured by the following methods. 
     Refractive index and Abbe&#39;s number: 
     Measured at 20° C. with a Pulfrich refractometer. 
     Mold release property: 
     After completing the polymerization, a Teflon wedge was struck in the interface of the lens and glass mold. The results were divided into the following two classes. 
     ◯. . . Quite readily released. 
     X . . . Release was partly or wholly impossible. 
     Appearance: 
     Evaluation was conducted by visual observation. 
     EXAMPLE-1A 
     A mixture of 13.5 g (0.07 mole) of benzene1,4-diisothiocyanate and 7.7 g (0.07 mole) of hydroquinone was poured into a mold consisting of a glass mold and a gasket. The mold was then gradually heated from room temperature to 120° C., taking 48 hours to complete the polymerization. The lens obtained was colorless and transparent. The lens had a refractive index n D   20  of 1.78. 
     EXAMPLES 2A-43A AND COMPARATIVE EXAMPLES 1A-9A 
     The same procedures as described in Example 1A were carried out for preparing lenses by using the composition illustrated in Table 1. 
     Results of testing physical properties are summarized in Table 1. 
     EXAMPLE 1B 
     A mixture of 13.5 g (0.07 mole) of benzene1,4-diisothiocyanate, 7.7 g (0.07 mole) of hydroquinone and 0.02 g of dodecanol acid phosphate was poured into a mold consisting of a glass mold and a gasket. Then the mold was gradually heated from room temperature to 120° C., taking 24 hours to complete the polymerization. After completing the polymerization, the lens was readily released from the mold. The lens obtained had a good profile accuracy of surface was colorless and transparent, and had a refractive index n D   20  of 1.78. 
     EXAMPLES 2B-59B 
     The same procedures as described in Example 1B were carried out for preparing lenses by using the compositions illustrated in Table 2. Results on the physical property test are illustrated in Table 2. 
     COMPARATIVE EXAMPLES 1B-36B 
     The same procedures as described in Example 1B were carried out for preparing lenses except that molds were used under conditions described below and compositions set forth in Table 3 were used. The results are summarized in Table 3. 
     The descriptions in the mold treatment column in Table 3 also indicates the following conditions. 
     (1) No treatment . . . A glass mold was used without any releasing treatment. 
     (2) External releasing treatment . . . External mold releasing agent YSR-6209™ (product of Toshiba Silicon Co.) was applied and baked on the inner surface of a glass mold. 
     (3) Recycled use . . . The glass mold obtained by the external releasing treatment was once employed for the polymerization and then used again without any further treatment. 
     (4) PP-mold . . . A polypropylene mold was prepared by injection molding and used in place of the glass mold without any surface treatment. 
     
         TABLE 1   Isothiocyanate Active-hydrogen  Refractive No. compound containing compound Appearance index     Example-1A  ##STR1##  0.07 mol  ##STR2##  0.07 mol Trans-parentcolorless 1.78  Example-2A ##STR3##  0.04 mol  ##STR4##  0.06 mol Trans-parentcolorless 1.73  Example-3A SCN(CH.sub.2).sub.6NCS 0.06 mol &#34; 0.06 mol Trans- 1.69      parent      colorless  Example-4A  ##STR5##  0.07 mol HOC.sub.2 H.sub.4 SC.sub.2 H.sub.4  OH 0.07 mol Trans-parentcolorless 1.69  Example-5A ##STR6##  0.05 mol  ##STR7##  0.025 mol Trans- 1.70      parent      colorless  Example-6A ##STR8##  0.05 mol  ##STR9##  0.025 mol Trans-parentcolorless 1.75  Example-7A ##STR10##  0.05 mol  ##STR11##  0.05 mol Trans-parentcolorless 1.80  Example-8A ##STR12##  0.06 mol  ##STR13##  0.03 mol Trans-parentcolorless 1.74  Example-9A ##STR14##  0.08 mol  ##STR15##  0.08 mol Trans-parentcolorless 1.72  Example-10A SCN(CH.sub.2).sub.3 NCS 0.08 mol  ##STR16##  0.08 mol Trans-parentcolorless 1.72  Example-11A ##STR17##  0.04 mol  ##STR18##  0.02 mol Trans-parentcolorless 1.73  Example-12A ##STR19##  0.04 mol  ##STR20##  0.04 mol Trans-parentcolorless 1.74  Example-13A ##STR21##  0.06 mol  ##STR22##  0.04 mol Trans-parentcolorless 1.76  Example-14A ##STR23##  0.06 mol  ##STR24##  0.06 mol Trans-parentcolorless 1.74  Example-15A ##STR25##  0.04 mol  ##STR26##  0.02 mol Trans-parentcolorless 1.77  Example-16A ##STR27##  0.06 mol  ##STR28##  0.04 mol Trans-parentcolorless 1.76  Example-17A ##STR29##  0.06 mol  ##STR30##  0.03 mol Trans-parent colorless 1.80  Example-18A SCN(CH.sub.2).sub.2 S(CH.sub.2).sub.2  NCS 0.06 mol ##STR31##  0.03 mol Trans- 1.73      parent      colorless  Example-19A ##STR32##  0.05 mol  ##STR33##  0.025 mol Trans-parentcolorless 1.76  Example-20A ##STR34##  0.08 mol  ##STR35##  0.08 mol Trans-parentcolorless 1.76  Example-21A ##STR36##  0.08 mol  ##STR37##  0.04 mol Trans-parentcolorless 1.71  Example-22A ##STR38##  0.06 mol  ##STR39##  0.03 mol Trans-parentcolorless 1.72  Example-23A &#34; 0.06 mol ##STR40##  0.03 mol Trans-parentcolorless 1.72  Example-24A &#34; 0.06 mol ##STR41##  0.06 mol Trans-parentcolorless 1.70  Example-25A ##STR42##  0.06 mol  ##STR43##  0.03 mol Trans-parentcolorless 1.71  Example-26A OCNCH.sub.2 CH.sub.2 CH.sub.2  NCS 0.06 mol ##STR44##  0.06 mol Trans-parentcolorless 1.75  Example-27A ##STR45##  0.06 mol  ##STR46##  0.06 mol Trans-parentcolorless 1.74  Example-28A &#34; 0.06 mol ##STR47##  0.03 mol Trans-parentcolorless 1.72  Example-29A ##STR48##  0.06 mol  ##STR49##  0.03 mol Trans-parentcolorless 1.71  Example-30A &#34; 0.06 mol ##STR50##  0.03 mol Trans-parentcolorless 1.72  ##STR51##  0.03 mol  Example-31A OCNCH.sub.2 CH.sub.2 CH.sub.2 NCS 0.06 mol HOCH.sub.2 CH.sub.2 SCH.sub.2 CH.sub.2 OH 0.06 mol Trans- 1.69 parent      colorless  Example-32A OCNCH.sub.2 CH.sub.2 CH.sub.2 NCS 0.06 mol  ##STR52##  0.04 mol Trans-parentcolorless 1.75  Example-33A ##STR53##  0.06 mol  ##STR54##  0.04 mol Trans-parentcolorless 1.72  Example-34A ##STR55##  0.06 mol  ##STR56##  0.03 mol Trans-parentcolorless 1.76  Example-35A SCN(CH.sub.2).sub.6NCS 0.07 mol C(CH.sub.2 SCH.sub.2 CH.sub.2 SH).sub.4 0.04 mol Trans- 1.78   parent      colorless  ##STR57##  0.01 mol  Example-36A ##STR58##  0.01 mol  ##STR59##  0.04 mol Trans-parentcolorless 1.74   OCNCH.sub.2 CH.sub.2 NCS 0.07 mol  Example-37A ##STR60##  0.07 mol  ##STR61##  0.04 mol Trans- 1.73      parent      colorless  ##STR62##  0.01 mol  Example-38A ##STR63##  0.01 mol  ##STR64##  0.04 mol Trans-parentcolorless 1.77   OCNCH.sub.2 CH.sub.2 CH.sub.2 NCS 0.07 mol  Example-39A ##STR65##  0.01 mol  ##STR66##  0.04 mol Trans-parentcolorless 1.74   OCNCH.sub.2 CH.sub.2 CH.sub.2 NCS 0.07 mol  Example-40A ##STR67##  0.08 mol  ##STR68##  0.02 mol Trans-parentcolorless 1.75  ##STR69##  0.03 mol  Example-41A ##STR70##  0.08 mol  ##STR71##  0.01 mol Trans-parentcolorless 1.73  ##STR72##  0.04 mol  Example-42A ##STR73##  0.04 mol  ##STR74##  0.035 mol Trans- 1.72      parent      colorless  ##STR75##  0.04 mol  ##STR76##   0.005 mol  Example-43A ##STR77##  0.01 mol  ##STR78##  0.08 mol Trans-parentcolorless 1.75  ##STR79##  0.07 mol  ComparativeExample-1A OCN(CH.sub.2).sub.6 NCO 0.07 mol HOCH.sub.2 CH.sub.2 CH.sub.2 CH.sub.2 OH 0.07 mol Trans- 1.50 parent      colorless  ComparativeExample-2A ##STR80##  0.08 mol  ##STR81##  0.04 mol Trans-parentcolorless 1.59  ComparativeExample-3A OCN(CH.sub.2).sub.6NCO 0.07 mol  ##STR82##  0.07 mol Trans-parentcolorless 1.62  ComparativeExample-4A ##STR83##  0.05 mol  ##STR84##  0.025 mol Trans- 1.62      parent      colorless  ComparativeExample-5A  ##STR85##  0.08 mol  ##STR86##  0.08 mol Trans-parentcolorless 1.61  ComparativeExample-6A ##STR87##  0.06 mol  ##STR88##  0.06 mol Trans-parentcolorless 1.67  ComparativeExample-7A OCN(CH.sub.2).sub.2 S(CH.sub.2).sub.2 NCO 0.06 mol  ##STR89##  0.03 mol Trans- 1.66      parent      colorless  ComparativeExample-8A  ##STR90##  0.08 mol  ##STR91##  0.04 mol Trans-parentcolorless 1.64  ComparativeExample-9A ##STR92##  0.06 mol  ##STR93##  0.06 mol Trans-parentlightyellow 1.61 
    
     
         TABLE 2  No.    Mold  Refractive Example Isothiocyanate compound Active-hydrogen containing compound Internal releasing agent release Appearance index                                                         1B  ##STR94##  0.07 mol  ##STR95##  0.07 mol Dodecanol acidphosphate 1000 ppm ◯ Good surfaceaccu racyTransparentcolorless 1.78                                      2B  ##STR96##  0.07 mol  ##STR97##  0.07 mol Unidain DS-403(Daikin) 500 ppm ◯ Good surfaceaccura cyTransparentcolorless 1.78                                        3B SCN(CH.sub.2).sub.6 NCS 0.07 mol  ##STR98##  0.07 mol Q2-120A(Dow) 300 ppm ◯ Good surfaceaccuracyTranspar entcolorless 1.69                                                  4B SCN(CH.sub.2).su b.6  NCS 0.07 mol ##STR99##  0.07 mol Trimethyloctylammoniumchloride 500 ppm ◯ Good surfaceaccuracyTransparentcolorless 1.69                           5B SCN(CH.sub.2).sub.6 NCS 0.08 mol C(CH.sub.2 SCH.sub.2 CH.sub.2 SH).sub.4 0.04 mol Unidain DS-403 300 ppm ◯ Good surface 1.70      (Daikin)   accuracy Transparent         colorloess                                      6B SCN(CH.sub.2).sub.6 NCS 0.08 mol C(CH.sub.2 SCH.sub.2 CH.sub.2 SH).sub.4 0.04 mol Unidain DS-401 100 ppm ◯ Good surface 1.70      (Daikin)   accuracy Q2-120A 100 ppm  Transparent      (Dow)   colorless                7B  ##STR100##  0.08 mol C(CH.sub.2 SCH.sub.2 CH.sub.2 SH).sub.4 0.04 mol Diisopropyl acidphosphate 500 ppm ◯ Good surfaceaccuracyTransparentcolorl ess 1.75                                                           8B  ##STR101##  0.08 mol C(CH.sub.2 SCH.sub.2 CH.sub.2                                  a  SH).sub.4 0.04 mol Trimethyloctylmmoniumchloride 500 ppm ◯ Good surfaceaccuracyTransparentcolorless 1.75                      9B  ##STR102##  0.08 mol  ##STR103##  0.04 mol Unidain DS-401(Daikin) 100 ppm ◯ Good surfaceaccura cyTransparentcolorless 1.74                                         10B  ##STR104##  0.08 mol  ##STR105##  0.04 mol Q2-120A(Dow) 100 ppm ◯ Good surfaceaccuracyTranspar entcolorless 1.74                                                   11B  ##STR106##  0.06 mol  ##STR107##  0.06 mol Unidain DS-403(Daikin) 100 ppm ◯ Good surfaceaccura cyTransparentcolorless 1.72                                         12B  ##STR108##  0.06 mol  ##STR109##  0.03 mol Unidain DS-403(Daikin) 100 ppm ◯ Good surfaceaccura cyTransparentcolorless 1.76  ##STR110##  0.03 mol                                                           13B  ##STR111##  0.06 mol  ##STR112##  0.06 mol Q2-120A (Dow) 150 ppm ◯ Good surfaceaccuracyTranspa rentcolorless 1.80                                                  14B SCN(CH.sub.2).s ub.6NCSOCN(CH.sub.2).sub.6NCO 0.04 mol0.02 mol  ##STR113##  0.06 mol Trimethyloctylammoniumchloride 500 ppm ◯ Good surfaceaccuracyTransparentcolorless 1.75                            15B  ##STR114##  0.03 mol0.03 mol C(CH.sub.2 SCH.sub.2 CH.sub.2 SH).sub.4 0.03 mol Unidain DS-401(Daikin) 200 ppm ◯ Good surfaceaccuracyTranspar entcolorless 1.73                                                   16B  ##STR115##  0.04 mol C(CH.sub.2 SCH.sub.2 CH.sub.2 OH).sub.4 0.02 mol Dodecanol     p acidhosphate 1000 ppm ◯ Good surfaceaccuracyTransparentcolorl ess 1.73                                                            17B  ##STR116##  0.04 mol  ##STR117##  0.04 mol Unidain DS-403(Daikin) 500 ppm ◯ Good surfaceaccura cyTransparentcolorless 1.74                                         18B  ##STR118##  0.06 mol  ##STR119##  0.04 mol Q2-120A(Dow) 300 ppm ◯ Good surfaceaccuracyTranspar entcolorless 1.76                                                   19B (SCH.sub.2 CH.sub.2  NCS).sub.2 0.06 mol ##STR120##  0.06 mol Triethyloctylammoniumchloride 500 ppm ◯ Good surfaceaccuracyTransparentcolorless 1.74                            20B  ##STR121##  0.04 mol C(CH.sub.2 SCH.sub.2 CH.sub.2 SH).sub.4 0.02 mol Unidain       ( DS-403Daikin) 300 ppm ◯ Good surfaceaccuracyTransparentcolorl ess 1.77                                                            21B  ##STR122##  0/04 mol C(CH.sub.2 SCH.sub.2 CH.sub.2 SH).sub.4 0.02 mol Unidain       ( DS-401Daikin)Q2-120A(Dow) 100 ppm100 ppm ◯ Good surfaceaccura cyTransparentcolorless 1.77                                         22B  ##STR123##  0.06 mol  ##STR124##  0.04 mol Diisopropyl acidphosphate 500 ppm ◯ Good surfaceacc uracyTransparentcolorless 1.76                                      23B  ##STR125##  0.06 mol C(CH.sub.2 SH).sub.4 0.03 mol Trimethyloctyl ammoniumchloride 500 ppm ◯ Good surfaceaccuracyTransparentcolorless 1.8024B SCN(CH.sub.2).sub.2 S(CH.sub.2).sub.2 NCS 0.06 mol C(CH.sub.2 SCH.sub.2 CH.sub.2 SH).sub.3 0.03 mol Unidain DS-401(Daikin) 100 ppm ◯ Good surfaceaccuracyTransparentcolorless 1.73         25B  ##STR126##  0.05 mol  ##STR127##  0.025 mol Q2-120A(Dow) 100 ppm ◯ Good surfaceaccuracyTranspa rentcolorless 1.76                                                  26B  ##STR128##  0.08 mol  ##STR129##  0.08 mol Unidain DS-403(Daikin) 100 ppm ◯ Good surfaceaccura cyTransparentcolorless 1.76                                         27B  ##STR130##  0.08 mol  ##STR131##  0.03 mol Unidain DS-403(Daikin) 100 ppm ◯ Good surfaceaccura cyTransparentcolorless 1.77     C(CH.sub.2 SH).sub.4 0.025 mol      28B S(CH.sub.2 CH.sub.2  NCS).sub.2 0.08 mol ##STR132##  0.04 mol Q2-120A(Dow) 150 ppm ◯ Good surfaceaccuracyTranspar entcolorless 1.71                                                   29B S(CH.sub.2 CH.sub.2  NCS).sub.2 0.08 mol ##STR133##  0.04 mol Unidain DS-401(Daikin) 150 ppm ◯ Good surfaceaccura cyTransparentcolorless 1.71                                         30B  ##STR134##  0.04 mol C(CH.sub.2 SH).sub.4 0.04 mol Trimethyloctylammoniumchloride 500 ppm ◯ Good surfaceaccuracyTransparentcolorless 1.73  ##STR135##  0.04 mol                                                           31B  ##STR136##  0.08 mol C(CH.sub.2 SCH.sub.2 CH.sub.2 SH).sub.4 0.04 mol Dodecanol     p acidhosphate 1000 ppm ◯ Good surfaceaccuracyTransparentcolorl ess 1.72                                                            32B  ##STR137##  0.08 mol C(CH.sub.2 SCH.sub.2 CH.sub.2 SH).sub.4 0.04 mol Unidain       ( DS-403Daikin) 500 ppm ◯ Good surfaceaccuracyTransparentcolorl ess 1.72                                                            33B  ##STR138##  0.08 mol  ##STR139##  0.08 mol Q2-120A(Dow) 300 ppm ◯ Good surfaceaccuracyTranspar entcolorless 1.72                                                   34B  ##STR140##  0.08 mol  ##STR141##  0.08 mol Trimethyloctylammoniumphosphate 500 ppm ◯ Good surfaceaccuracyTransparentcolorless 1.70                            35B  ##STR142##  0.08 mol  ##STR143##  0.08 mol Unidain DS-403(Daikin) 300 ppm ◯ Good surfaceaccura cyTransparentcolorless 1.71                                         36B  ##STR144##  0.08 mol  ##STR145##  0.08 mol Unidain DS-401(Daikin)Q2-102A(DOW) 100 ppm100 ppm ◯  Good surfaceaccuracyTransparentcolorless 1.71                      37B  ##STR146##  0.06 mol  ##STR147##  0.06 mol Diisopropyl acidphosphate 500 ppm ◯ Good surfaceacc uracyTransparentcolorless 1.74                                      38B OCNCH.sub.2 CH.sub.2 CH.sub.2  NCS 0.06 mol ##STR148##  0.06 mol Trimethyloctylammoniumchloride 500 ppm ◯ Good surfaceaccuracyTransparentcolorless 1.75                            39B  ##STR149##  0.06 mol  ##STR150##  0.03 mol Unidain DS-401(Daikin) 100 ppm ◯ Good surfaceaccura cyTransparentcolorless 1.72                                         40B  ##STR151##  0.08 mol C(CH.sub.2 SCH.sub.2 CH.sub.2 SH).sub.4 0.04 mol Q2-120A(Dow) 100 ppm ◯ Good surfaceaccuracyTransparentcolorless 1.7141B  ##STR152##  0.06 mol  ##STR153##  0.03 mol Q2-120A(Dow) 100 ppm ◯ Good surfaceaccuracyTranspar entcolorless 1.72  ##STR154##  0.03 mol                                                           42B  ##STR155##  0.03 mol  ##STR156##  0.06 mol Dodecanol acidphosphate 500 ppm ◯ Good surfaceaccur acyTransparentcolorless 1.75  ##STR157##  0.03 mol                                                           43B  ##STR158##  0.03 mol  ##STR159##   0.06 mol Trimethyloctylammoniumchloride 500 ppm ◯ Good surfaceaccuracyTransparentcolorless 1.72  ##STR160##  0.03 mol                                                           44B  ##STR161##  0.03 mol C(CH.sub.2 SCH.sub.2 CH.sub.2 SH).sub.4 0.04 mol Unidain       ( DS-401Daikin) 200 ppm ◯ Good surfaceaccuracyTransparentcolorl ess 1.72  ##STR162##  0.05 mol                                                           45B OCNCH.sub.2 CH.sub.2 NCS 0.06 mol HOCH.sub.2 CH.sub.2 SCH.sub.2 CH.sub.2 OH 0.06 mol Diisopropyl acid 500 ppm ◯ Good surface 1.69  phosphate   accuracy         Transparent         colorless         46B OCNCH.sub.2 CH.sub.2 CH.sub.2  NCS 0.06 mol ##STR163##  0.04 mol UnidainSD-403(Daikin) 300 ppm ◯ Good surfaceaccurac yTransparentcolorless 1.75                                          47B  ##STR164##  0.06 mol  ##STR165##  0.04 mol Trimethyloctylammoniumchloride 500 ppm ◯ Good surfaceaccuracyTransparentcolorless 1.72                            48B  ##STR166##  0.06 mol C(CH.sub.2  SH).sub.4 0.03 mol Dodecanol acidphosphateDiisopropyl acidphosphate 100 ppm500 ppm ◯ Good surfaceaccuracyTransparentcolorless 1.76  49B  ##STR167##  0.07 mol0.01 mol C(CH.sub.2 SCH.sub.2 CH.sub.2 SH).sub.4 0.04 mol  Q2-120A(Dow) 100 ppm ◯ Good surfaceaccuracyTransparentcolorl ess 1.78                                                            50B  ##STR168##  0.01 mol0.07 mol  ##STR169##  0.04 mol UnidainDS-401(Daikin) 100 ppm ◯ Good surfaceaccurac yTransparentcolorless 1.74                                          51B  ##STR170##  0.07 mol0.01 mol C(CH.sub.2 SCH.sub.2 CH.sub.2 OH).sub.4 0.04 mol UnidainDS-401(Daikin) 100 ppm ◯ Good surfaceaccuracyTranspare ntcolorless 1.73                                                    52B  ##STR171##  0.01 mol C(CH.sub.2 SH).sub.4 0.04 mol Diisopropyl acidphosphate 500 ppm ◯ Good surfaceaccuracyTransparentcolorless 1.77 OCNCH.sub.2 CH.sub.2 CH.sub.2 NCS 0.07 mol                          53B  ##STR172##  0.01 mol  ##STR173##  0.04 mol Diisopropyl acidphosphate 500 ppm ◯ Good surfaceacc uracyTransparentcolorless 1.74  OCNCH.sub.2 CH.sub.2 CH.sub.2 NCS 0.07 mol                                                                 54B (S CH.sub.2 CH.sub.2  NCS).sub.2 0.08 mol ##STR174##  0.02 mol Diisopropyl acidphosphate 500 ppm ◯ Good surfaceacc uracyTransparentcolorless 1.75    C(CH.sub.2 SCH.sub.2 CH.sub.2  SH).sub.4 0.03 mol                                                 55B  ##STR175##  0.08 mol  ##STR176##  0.01 mol0.04 mol Diisopropyl acidphosphate 500 ppm ◯ Good surfaceaccuracyTransparentcolorless 1.73                            56B SCN(CH.sub.2).sub.6 NCS(SCH.sub.2 CH.sub.2  NCS) 0.04 mol0.04 mol ##STR177##  0.035 mol0.005 mol Diisopropyl acidphosphate 500 ppm ◯ Good surfaceaccuracyTransparentcolorless 1.72                            57B SCN(CH.sub.2).sub.3 NCS 0.08 mol  ##STR178##  0.08 mol Diisopropyl acidphosphate 500 ppm ◯ Good surfaceacc uracyTransparentcolorless 1.72                                      58B  ##STR179##  0.06 mol  ##STR180##  0.06 mol Diisopropyl acidphosphate 500 ppm ◯ Good surfaceacc uracyTransparentcolorless 1.71                                      59B  ##STR181##  0.01 mol  ##STR182##  0.08 mol Diisopropyl acidphosphate 500 ppm ◯ Good surfaceacc uracyTransparentcolorless 1.75  SCN(CH.sub.2).sub.3  NCS 0.07 mol 
    
     
         TABLE 3  No.       Comparative  Active-hydrogen  Mold  Refractive Example Polyisothiocyanate compound Mold treatment release Appearance index                                                          1B  ##STR183##  0.07 mol  ##STR184##  0.07 mol No treatment X -- --                                     2B &#34;  &#34;  External ◯ Non uniformity 1.78      releasing  of surface      treatment  Colorless,    Transparent                                                 3B &#34;  &#34;  Recycled use X -- --      (from Comparat.      Example-2B)                   4B &#34;  &#34;  PP-mold ◯ Poor surface 1.78  accuracy        Colorless,        Transparent                 5B SCN(CH.sub.2).sub.6 NCS 0.08 mol C(CH.sub.2 SCH.sub.2 CH.sub.2 SH).sub.4 0.04 mol No treatment X -- --          6B &#34;  &#34;  External ◯ Non uniformity 1.70 releasing  of surface      treatment  Colorless,        Transparent7B &#34;  &#34;  Recycled use X -- --      (from Comparat.      Example-6B) 8B &#34;  &#34;  PP-mold ◯ Poor surface 1.70        accuracy Colorless,        Transparent                                       9B  ##STR185##  ##STR186##  0.03 mol No treatment X -- --  ##STR187##  0.03 mol                                                           10B &#34;  &#34; External releas- ◯ Poor surface 1.76      ing treatment accuracy        Colorless,        Transparent 11B &#34;  &#34;  Recycled use X -- --      (from Comparat.      Example-10B)    12B &#34;  &#34; PP-mold ◯ Poor surface 1.76        accuracy13B  ##STR188##  0.04 mol C(CH.sub.2 SCH.sub.2 CH.sub.2 OH).sub.4 0.02 mol No treatment X -- --                                                             14B &#34; &#34;  External ◯ Non uniformity 1.73      releasing  of surface treatment  Colorless,        Transparent 15B &#34;  &#34;  Recycled use X -- --      (from Comparat.      Example-14B)    16B &#34;  &#34;  PP-mold ◯ Poor surface 1.73        accuracy    Colorless,        Transparent 17B  ##STR189##  0.06 mol  ##STR190##  0.04 mol No treatment X -- --                                      18B &#34;  &#34;  External .largecircle . Non uniformity 1.76      releasing  of surface      treatment Colorless,        Transparent 19B &#34;  &#34;  Recycled use X -- --      (from Comparat.      Example-18B)   20B  ##STR191##  0.06 mol  ##STR192##  0.04 mol PP-mold ◯ Poor surfaceaccuracy Colorless,Transparen t 1.76                                                              21B  ##STR193##  0.08 mol  ##STR194##  0.03 mol No treatment X -- --    C(CH.sub.2 SH).sub.4 0.025 mol    22B &#34;  &#34;  External ◯ Non uniformity 1.77 releasing  of surface      treatment  Colorless,        Transparent 23B &#34;  &#34;  Recycled use X -- --      (from Comparat.      Example-22B ) 24B &#34;  &#34;  PP-mold ◯ Poor surface 1.77        accuracy Colorless,        Transparent 25B  ##STR195##  0.08 mol  ##STR196##  0.08 mol No treatment X -- --                                      26B &#34; 0.08 mol &#34; 0.08 mol External ◯ Non uniformity 1.72      releasing  of surface   treatment  Colorless,        Transparent 27B &#34; 0.08 mol &#34; 0.08 mol Recycled use X -- --      (from Comparat. Example-26B) 28B &#34; 0.08 mol &#34; 0.08 mol PP-mold ◯ Poor surface 1.72 accuracy        Colorless,        Transparent                       29B  ##STR197##  0.08 mol C(CH.sub.2 SCH.sub.2 CH.sub.2 SH).sub.4 0.04 mol No treatment X -- --                                                             30B &#34; 0.08 mol &#34; 0.04 mol External ◯ Non uniformity 1.71 releasing  of surface      treatment  Colorless,        Transparent 31B &#34; 0.08 mol &#34; 0.04 mol Recycled use X -- --      (from Comparat. Example-30B) 32B &#34; 0.08 mol &#34; 0.04 mol PP-mold ◯ Poor surface 1.71 accuracy        Colorless,        Transparent                       33B  ##STR198##  0.08 mol  ##STR199##  0.04 mol No treatment X -- --  ##STR200##  0.04 mol                                                           34B &#34;  &#34; External ◯ Non uniformity 1.72      releasing  of surface   treatment  Colorless,        Transparent 35B &#34;  &#34;  Recycled use X -- --      (from Comparat.      Example-34B)    36B &#34;  &#34;  PP-mold ◯ Poor surface 1.72        accuracy    Colorless,        Transparent