Abstract:
The invention relates to propylene polymer blends comprising 70-92 wt % of a propylene homopolymer, 5-15 wt % of an elastomeric ethylene-propylene copolymer, 3-15 wt % of a linear low density polyethylene and an a-nucleating agent. The propylene polymer blends have an excellent impact strength/stiffness balance and optical properties. They are especially suitable for thermoforming and extrusion blow moulding.

Description:
REFERENCE TO RELATED APPLICATION 
       [0001]    This is a continuation application of Ser. No. 11/792,690, filed Aug. 15, 2007 which is currently pending. The subject matter of the aforementioned prior application is hereby incorporated herein by reference. 
     
    
     BACKGROUND OF THE INVENTION 
       [0002]    The present invention relates to propylene polymer blends which are suitable for thermoforming and extrusion blow molding applications. The inventive propylene polymer blends are particularly suited for these applications because they have excellent balance of stiffness and impact strength especially at low temperatures, excellent transparency and gloss. 
         [0003]    Polypropylene compositions for technical applications often, suffer from shortcomings in the combination of optical performance (high transparency, low haze), low temperature toughness, stiffness and added properties like gloss. Conventional&#39; modifications are unable to simultaneously achieve these property requirements. 
         [0004]    Especially, optical performance and impact resistance at freezer and refrigerator temperatures are two antagonistic properties:
       In general, a high transparency is achieved by using propylene homopolymers or C 3 /C 2  random copolymers. It can even be further improved by incorporating a-nucleating agents or clarifiers. However, both classes of materials are brittle at temperatures below 0° C., which make them inappropriate for applications which require a certain level of toughness.   Heterophasic propylene copolymers composed of a PP-based matrix and of a dispersed EPR phase have improved low temperature impact strength. This is especially the case when the molecular weight of the EPR is higher than that of the PP-based matrix. These grades are however characterised by low transparency. Lowering the total MFR of the composition would result in sufficient impact strength but poor processability of the composition. Lowering the molecular weight of the EPR fraction to levels below that of the PP-based matrix would improve the transparency but would result in poor impact strength.   Using too high contents of ethylene in the PP-based matrix in heterophasic systems would lower the stiffness to an undesirable level.       
 
         [0008]    EP 714 923 discloses reactor-made propylene block copolymers resulting from a three-step sequential synthesis. The process for producing these propylene block copolymers is however very complicated and inflexible, since each polymerisation step receives the product of the preceeding stage. On the one hand several reactors are required to polymerize the desired components of the final composition, on the other hand it is very complex to run such a plant in a stable mode for a longer period of time. This is however required for a commercially successful operation. If any fluctuations and problems occur in one of the first two polymerization reactors, especially in the first one, it is necessary to run the plant several hours by producing a transition material which is not fulfilling any quality requirements, thereby creating severe losses in terms of commercial profit. 
       SUMMARY OF THE INVENTION 
       [0009]    It is therefore the object of the invention, to provide a propylene polymer composition which is characterised by a combination of excellent optical and mechanical properties. In particular, the inventive propylene polymer compositions shall be characterised by high transparency and gloss, high stiffness and impact strength (e.g. toughness) at ambient, freezer and refrigerator temperatures. Further, the inventive propylene polymer compositions shall be produced in a simple and economic process. 
         [0010]    The new compositions shall be used for thermoforming and extrusion blow moulding applications, therefore the MFR of the compositions is preferred to be from 1-5 g/10 min. Stiffness is considered to be high with moduli according to ISO 527 of ≧1000 MPa. Impact strength, when determined as W tot /mm in the Falling weight test according to ISO 7765/2 shall be at least 5 J/mm at −20° C. and at least 10 J/mm at +23° C. Impact strength, when determined with the Drop Test according to ASTM-D 2463-95 shall be at least 2 m at 0° C. and at least 5 m at 23° C. Haze shall not exceed 20%, when determined on 300 μm sheets and it shall not exceed 50%, when determined on 0.7 mm samples. Gloss must be higher than 100% (when measured on 300 μm sheets). 
         [0011]    The above object was achieved with a propylene polymer blend comprising 
         [0000]    A) 70-92 wt % of a propylene homopolymer having an MFR A  (230° C., 2.16 kg) of 1-5 g/10 min,
 
B)  5 -15 wt % of an elastomeric ethylene-propylene copolymer having an intrinsic viscosity IV of 1.0-2.5 dug and a propylene content of at least 55 wt %,
 
whereby a blend of the propylene homopolymer A and the elastomeric ethylene-propylene copolymer B has an MFR A+B  (230° C., 2.16 kg) of 1-5 g/10 min,
 
where the MFR A+B &gt;MFR C , preferably MFR A+B &gt;1.5×MFR C .
 
C) 3-15 wt % of a linear low density polyethylene, having an ethylene content of at least 85 mol %, preferably from 91-99 mol %, and a density of 0.914-0.924 g/cm 3  and having an MFR C  (190° C., 2.16 kg) of 0.3-5 g/10 min, and
 
D) an α-nucleating agent.
 
         [0012]    The propylene polymer A used for the propylene polymer blend according to the invention is a propylene homopolymer having an MFR A  of from 1-5 g/10 min, preferably of from 1-4 g/10 min. It has been found that for achieving the desired property combination (i.e. total MFR, haze, toughness) it is necessary that the propylene polymer A has an MFR within that interval. 
         [0013]    A further essential component of the present invention is an elastomeric ethylene-propylene copolymer B having an intrinsic viscosity IV of 1.0-2.5 dl/g and a high propylene content of at least 55 wt %. Copolymers B with a lower propylene content do not result in satisfactory optical properties, especially transparency, but also gloss is too low. Copolymers B with a higher intrinsic viscosity do not result in propylene polymer blends having the required transparency. 
         [0014]    The amounts and type of components A and B are selected in order to ensure that a blend consisting of the components A and B has an MFR A+B  of 1-5 g/min. 
         [0015]    A further essential component of the present invention is a linear low density polyethylene C. For achieving the desired combination of good optical properties and mechanical performance at temperatures ≦0° C., it is important for the linear low density polyethylene to have an MFR C  (190° C., 2.16 kg) of from 0.3 to 5 g/10 min. Lower melt indices do not result in a blend having the targeted optical performance and might result in undesirable gloss decrease. When the melt index of the linear low density polyethylene C is too high, i.e. when it is &gt;5 g/10 min the mechanical properties of the compositions, in particular toughness at low temperature, might be not sufficient. It is further essential that the linear low density polyethylene C has a density of from 0.914 to 0.924 g/cm 3 . A density within this interval has been found to be essential for the desired good optical properties. 
         [0016]    All components A, B and C are selected in order to ensure, that MFR A+B ≧MFR C , preferably MFR A+B &gt;1.5×MFR C . 
         [0017]    Finally, the propylene polymer blends of the present invention comprise one or more α-nucleating agents. It is preferred that they contain from 0.01-2 wt % based on the sum of the weight of components A to C of α-nucleating agents. 
         [0018]    Since the propylene polymer blends of the invention are not the result of a multi-stage polymerisation process, as in e.g. EP 714 923, it was possible to avoid the specific problems associated with that prior art, while simultaneously producing propylene polymer blends with superior and unique property combinations. 
         [0019]    The addition of α-nucleating agents to propylene polymers increases their stiffness. α-nucleating agents are therefore added for a high absolute level of stiffness. 
         [0020]    Particularly suitable α-nucleating agents in this invention are sodium-2,2′-methylene-bis(4,6-di-t-butylphenyl)phosphate (NA-11, available from Asahi Denka Kogyo (Japan)), 1,3,2,4-di(3′,4′-dimethylbenzylidene)sorbitol (MILLAD 3988, available from Milliken) and hydroxy bis-(2,4,8,10-tetra-tert butyl-6-hydroxy-12H-dibenzo(d,g)(1.,3,2) dioxaphosphocin 6-oxidato) aluminium (contained in “ADK STAB NA21E” available from Asahi Denka Kogyo (Japan); “NA21” in the examples). 
         [0021]    A further α-nucleation method, herein referred to as “BNT”, is a special reactor technique, where the catalyst is prepolymerised with monomers like vinylcyclohexane (VCH). This method is described in greater detail in e.g. EP 0 316 187 A2. For the purpose of this invention “BNT” is referred to as α-nucleating agent. 
         [0022]    In order to achieve particularly good optical properties of the blends of the invention, it is preferred to use α-nucleating agents, which are also very active as clarifying agents. An example of such α-nucleating/clarifying agents is ADK STAB NA21E from Asahi Denka Kogyo (Japan), which is therefore particularly preferred. Other α-nucleating agents, which are not equally active as clarifying agents, e.g. benzoic acid derivatives, are less preferred in this regard. 
         [0023]    According to a preferred embodiment, the linear low density polyethylene C has a density of 0.915-0.924 g/cm 3 , more preferably of 0.918-0.924 g/cm 3 . 
         [0024]    It is further preferred, that the ethylene-propylene copolymer B has an intrinsic viscosity IV of 1.5-2.5 dl/g. If the intrinsic viscosity is lower than 1.0 dl/g, the end product might be sticky, if the IV is higher than 2.5 dl/g, transparency of the end product will be lowered to an undesirable level. A preferred lower limit of the intrinsic viscosity IV of 1.5 dl/g further ensures that the end product is not sticky. 
         [0025]    According to an embodiment of the present invention, the ethylene-propylene copolymer B has a propylene content of at least 60 wt %. If the propylene content of the ethylene-propylene copolymer B is less than 55 wt %, transparency suffers and it cannot be adjusted to the desired level without adversely affecting other properties, especially gloss. A still higher propylene content of the ethylene-propylene copolymer B, i.e. of at least 60 wt %, is therefore preferred. 
         [0026]    The propylene polymer blends of the present invention are preferably produced by mixing 
         [0000]    A) 70-92 wt % of a propylene homopolymer having an MFR A  (230° C., 2.16 kg) of 1-5 g/10 min,
 
B) 5-15 wt % of an elastomeric ethylene-propylene copolymer having an intrinsic viscosity IV of 1.0-2.5 dl/g and a propylene content of at least 55 wt %,
 
whereby a blend of the propylene homopolymer A and the elastomeric ethylene-propylene copolymer B has an MFR A+B  (230° C., 2.16 kg) of 1-5 g/10 min,
 
C) 3-15 wt % of a linear low density polyethylene, having an ethylene content of at least 85 mol %, preferably from 91-99 mol %, and a density of 0.914-0.924 g/cm 3  and having an MFR C (190° C., 2.16 kg) of 0.3-5 g/10 min,
 
where the MFR A+B ≧MFR C , preferably MFR A+B &gt;1.5×MFR C , and
 
D) an α-nucleating agent,
 
melting and homogenising and
 
cooling and pelletising the mixture
 
         [0027]    The propylene polymer blends of the present invention are preferably produced by combining the propylene polymer A in the form of powder or granules, the elastomeric copolymer B, the linear low density polyethylene C and the α-nucleating agent D in a melt mixing device. 
         [0028]    Melt mixing devices suited for this process are discontinuous and continuous kneaders, twin screw extruders and single screw extruders with special mixing sections and co-kneaders. The residence time must be chosen such that a sufficiently high degree of homogenisation is achieved. 
       Production of Propylene Polymer A 
       [0029]    The propylene polymer may be produced by single- or multistage process polymerisation of propylene or propylene and α-olefin and/or ethylene such as bulk polymerisation, gas phase polymerisation, slurry polymerisation, solution polymerisation or combinations thereof using conventional catalysts. A homo- or copolymer can be made either in loop reactors or in a combination of loop and gas phase reactor. Those processes are well known to one skilled in the art. 
         [0030]    A suitable catalyst for the polymerisation of the propylene polymer is any stereospecific catalyst for propylene polymerisation which is capable of polymerising and copolymerising propylene and comonomers at a temperature of 40 to 110° C. and at a pressure from 10 to 100 bar. Ziegler Natta catalysts as well as metallocene catalysts are suitable catalysts. 
         [0031]    One skilled in the art is aware of the various possibilities to produce propylene homo- and copolymers and will simply find out a suitable procedure to produce suitable polymers which are used in the present invention. 
       Production of Elastomeric Copolymers B 
       [0032]    An ethylene propylene elastomeric copolymer may be produced by known polymerisation processes such as solution, suspension and gas-phase polymerisation using conventional catalysts. Ziegler Natta catalysts as well as metallocene catalysts are suitable catalysts. 
         [0033]    A widely used process is the solution polymerisation. Ethylene, propylene and catalyst systems are polymerised in an excess of hydrocarbon solvent. Stabilisers and oils, if used, are added directly after polymerisation. The solvent and unreacted monomers are then flashed off with hot water or steam, or with mechanical devolatilisation. The polymer, which is in crumb form, is dried with dewatering in screens, mechanical presses or drying ovens. The crumb is formed into wrapped bales or extruded into pellets. 
         [0034]    The suspension polymerisation process is a modification of bulk polymerisation. The monomers and catalyst system are injected into the reactor filled with propylene. The polymerisation takes place immediately, forming crumbs of polymer that are not soluble in the propylene. Flashing off the propylene and comonomer completes the polymerisation process. 
         [0035]    The gas-phase polymerisation technology consists of one or more vertical fluidised beds. Monomers and nitrogen in gas form along with catalyst are fed to the reactor and solid product is removed periodically. Heat of reaction is removed through the use of the circulating gas that also serves to fluidise the polymer bed. Solvents are not used, thereby eliminating the need for solvent stripping, washing and drying. 
         [0036]    The production of ethylene propylene elastomeric copolymers is also described in detail in e.g. U.S. Pat. No. 3,300,459, U.S. Pat. No. 5,919,877, EP 0 060 090 A1 and in a company publication by EniChem “DUTRAL, Ethylene-Propylene Elastomers”, pages 1-4 (1991). 
         [0037]    Alternatively, elastomeric ethylene-propylene copolymers, which are commercially available and which fulfil the indicated requirements, can be used. 
         [0038]    Alternatively, polymers A and B may be produced in a series of reactors, i.e. starting with the production of polymer A in a loop reactor and transferring the product into a gas phase reactor, where copolymer B is polymerised. 
       Production of Linear Low Density Polyethylene C 
       [0039]    It is preferred to use linear low density polyethylene polymers which are commercially available, e.g. FG5190, from Borealis A/S. Alternatively, suitable linear low density polyethylene may be produced according to the following descriptions. 
         [0040]    Linear low density polyethylene is made by the copolymerisation of ethylene and α-olefins. It may be produced in low pressure processes such as gas-phase process (for which the Unipol technology is a typical example), a solution-phase polymerisation process, a slurry process, or combinations thereof like staged gas phase (Union Carbide), staged slurry/gas phase (Borealis) or staged solution phase (Nova). A suitable catalyst for the polymerisation of LLDPE is any stereospecific catalyst which is capable of polymerising and copolymerising ethylene and comononers. Ziegler-Natta as well as metallocene catalysts are suitable catalysts. In the gas-phase process, reactor temperatures are usually below 100° C. with pressures of about 20 bars. In the solution process, reactor temperatures are usually 170-250° C. with pressures of 40-140 bars. In the solution-phase polymerisation process, reactor temperatures are usually 70-110° C. with pressures of 30-50 bars. 
         [0041]    The propylene polymer blends of the present invention are preferably used for thermoforming, e.g. packaging applications for low and subzero temperatures. A further preferred application of the propylene polymer compositions of the present invention are extrusion blow molding applications, e.g. bottles. 
       Measurement Methods 
     MFR 
       [0042]    The melt flow rates were measured with a load of 2.16 kg at 230° C. for polypropylene and at 190° C. for polyethylene. The melt flow rate is that quantity of polymer in grams which the test apparatus standardised to ISO 1133 extrudes within 10 minutes at a temperature of 230° C. or 190° C. respectively, under a load of 2.16 kg. 
         [0043]    Comonomer contents were measured with Fourier transform infrared spectroscopy (FTIR) calibrated with  13 C-NMR. 
       Intrinsic Viscosity 
       [0044]    Intrinsic Viscosity was measured according to DIN ISO 1628-1 (October 1999) in Decalin at 135° C. 
       Falling Weight Test 
       [0045]    Impact strength was determined as thickness normalised energy at break (W tot /mm) with the falling weight test according to ISO7765/2 at +23° C. and −20° C. Test speed was 4.4 m/s. Test specimens were 0.3 mm thick and exhibited a diameter of 80 mm. 
       Stiffness 
       [0046]    Stiffness on films (modulus MD in the examples) was measured according to ISO 527-3 at 1 mm/min on a 170*15*0.3 mm sample where the length represents the machine direction (e.g. the direction parallel to the flow direction) of the film. 
         [0047]    Stiffness on 4 mm thick injection moulded samples was determined at 1 mm/min according to ISO 527 with test specimens described in EN ISO 1873-2 (dog bone shape). 
       Gloss 
       [0048]    Gloss was determined according to ISO 2813 on sheets (thickness 300 μm) at an angle of 20°. 
       Haze 
       [0049]    Haze was determined according to ASTM D 1003-92 on sheets (thickness 300 μm) with 10 independent specimens regarding the thermoforming application and on 30*30*0.7 mm samples taken from bottles with 6 independent specimens cut from three different places of the bottle wall regarding the blow moulding application. 
       Drop Test 
       [0050]    Drop test was performed on bottles at 23° C. and 0° C. according to ASTM-D 2463-95 The height at which 50% of the bottles break, F 50 , in a brittle way was recorded. 
     
    
     DETAILED DESCRIPTION OF THE INVENTION 
     Examples 
     Preparation of Polymers A 
       [0051]    The propylene polymers A used for the present invention were prepared according to the following procedure: 
       Raw Materials: 
       [0052]    Hexane dried over molecular sieve (3/10A)
 
TEAL: 93% from Sigma-Aldrich
 
       Donor: Dicyclopentyldimethoxysilane: ex Wacker Chemie (99%). 
       [0053]    N 2 : supplier AGA, quality 5.0; purification with catalyst BASF R0311, catalyst G132 (CuO/ZNO/C), molecular sieves (3/10A) and P 2 O 5 .
 
Propylene: polymerisation grade
 
Hydrogen: supplier AGA, quality 6.0
 
The catalyst ZN104 is commercially available from Basell.
 
Sandostab P-EPQ is commercially available from Clariant.
 
         [0054]    A 5 I autoclave reactor has been purified by mechanical cleaning, washing with hexane and heating under vacuum/N 2  cycles at 160° C. After testing for leaks with 30 bar N 2  over night reactor has been vacuumed and filled with 1110 g propylene by weighing and 8 nl H 2  by pressure monitoring from a 50 I steel cylinder. 
         [0055]    10 mg of ZN104-catalyst are activated for 10 minutes with a mixture of Triethylaluminium (TEAT; solution in hexane 1 mol/l) and Dicyclopentyldimethoxysilane as donor (0.3 mot/I in hexane)—in a molar ratio of 5 after a contact time of 5 min—and 10 ml hexane in a catalyst feeder. The molar ratio of TEAl and Ti of catalyst is 250. After activation the catalyst is spilled with 300 g propylene into the stirred reactor with a temperature of 23° C. Stirring speed is hold at 250 rpm. After 6 min prepolymerisation at 23° C. temperature is increased to 70° C. in about 14 min. After holding that temperature for 1 hour polymerisation is stopped by flashing propylene and cooling to room temperature. 
         [0056]    After spilling the reactor with N 2  the homopolymer powder is transferred to a steel container and stabilized with 0.1 wt % of Sandostab P-EPQ and 0.2 wt % of lonol in acetone and dried over night in a hood and additionally for 2 hours at 50° C. under vacuum. 
         [0057]    The amount of polymer powder (A3) was 113 g and the MFR (230° C., 2.16 kg) of the powder was 5 g/10 min. 
         [0058]    The homopolymers shown in Table 1 were prepared analogously according to the above procedure: 
         [0000]    
       
         
               
               
               
             
               
               
               
             
           
               
                   
                 TABLE 1 
               
               
                   
                   
               
               
                   
                 polymer 
                 MFR 
               
               
                   
                 No. 
                 [g/10 min] 
               
               
                   
                   
               
             
             
               
                   
               
             
          
           
               
                   
                 A1 
                 2.2 
               
               
                   
                 A2 
                 2.5 
               
               
                   
                 A3 
                 5 
               
               
                   
                 A4 
                 1.8 
               
               
                   
                 A5 
                 0.4 
               
               
                   
                 A6 
                 0.7 
               
               
                   
                   
               
             
          
         
       
     
       Preparation of Elastomeric Copolymers B 
       [0059]    The elastomeric copolymers of the present invention were prepared according to the following procedure: 
         [0060]    A 5 I-reactor (autoclave) filled with about 0.2 barg propylene (polymerisation grade) is pressured up with the required amount of H 2  in order to achieve the targeted intrinsic viscosity of the elastomeric copolymer. Then 300 g of propylene are added. 
         [0061]    5 mg of a ZN101 (supplied by Basell) catalyst is contacted with 0.3 ml white oil for about 16 hours and then activated for 5 minutes with a mixture of Triethylaluminium (TEAl; solution in hexane 1 mol/l) and an alkoxysilane (Dicyclopentyldimethoxysilan in the examples) as donor (0.3 mol/l in hexane)—in a molar ratio of 76 using a contact time of 5 min. The molar ratio of TEAl and Ti of catalyst was 380 and TEAI concentration in TEAl/donor mixture 12.6 mg/ml hexane. After activation the catalyst is transferred to the reactor by spilling in with 500 g propylene. After 12 min pre-polymerisation at 30° C. a specified amount of ethylene is added to the reactor and the temperature is increased to the target polymerisation temperature (55° C. in the examples). During heating up additional ethylene dosing is started to achieve the target total pressure at the target polymerisation temperature. Total pressure is hold constantly via continuously dosing of ethylene during polymerisation. 30 min after end of prepolymerisation the reaction is stopped by flashing of monomers and cooling. 
         [0062]    The polymer is stabilized with 0.1 wt % of Sandostab P-EPQ and 0.2 wt % of lonol in acetone and dried over night in a hood and additionally for 2 hours at 50° C. under vacuum. 
         [0063]    Table 2 with example polymerisation conditions: 
         [0000]    
       
         
               
               
               
               
               
               
               
             
           
               
                   
                 TABLE 2 
               
               
                   
                   
               
               
                   
                   
                   
                   
                 total 
                   
                   
               
               
                   
                 Polymer 
                 H2 
                 C2 
                 pressure 
                 IV 
                 C3 
               
               
                   
                 No. 
                 barg 
                 [g] 
                 [barg] 
                 [dl/g] 
                 [wt %] 
               
               
                   
                   
               
             
             
               
                   
                 B1 
                 2 
                 50 
                 29 
                 2.40 
                 75.0 
               
               
                   
                 B3 
                 4 
                 90 
                 34 
                 1.95 
                 62.5 
               
               
                   
                 B5 
                 3 
                 90 
                 34 
                 2.60 
                 54.0 
               
               
                   
                 B8 
                 3 
                 40 
                 29 
                 2.06 
                 76.0 
               
               
                   
                   
               
             
          
         
       
     
         [0064]    The elastomeric ethylene-propylene copolymers shown in the following table were prepared according to the above procedure(s), except that H 2  and ethylene amounts were varied to achieve different intrinsic viscosities and comonomer concentrations. 
         [0000]    
       
         
               
               
               
               
             
           
               
                   
                 TABLE 3 
               
               
                   
                   
               
               
                   
                 polymer 
                 i.V. 
                 C3 
               
               
                   
                 No. 
                 [dl/g] 
                 [wt %] 
               
               
                   
                   
               
             
             
               
                   
                 B1 
                 2.40 
                 75.0 
               
               
                   
                 B2 
                 1.63 
                 70.0 
               
               
                   
                 B3 
                 1.95 
                 62.5 
               
               
                   
                 B4 
                 3.50 
                 65.0 
               
               
                   
                 B5 
                 2.60 
                 54.0 
               
               
                   
                 B6 
                 3.20 
                 51.0 
               
               
                   
                 B7 
                 2.03 
                 66.0 
               
               
                   
                 B8 
                 2.06 
                 76.0 
               
               
                   
                 B9 
                 3.20 
                 65.0 
               
               
                   
                 B10 
                 3.50 
                 58.0 
               
               
                   
                   
               
             
          
         
       
     
       Linear Low Density Polyethylene C 
       [0065]    The linear low density polyethylene polymers C which are used for the present invention are selected among commercially available LLDPE copolymers. 
         [0066]    The following ethylene homo- and copolymers were used in the examples: 
         [0000]    
       
         
               
               
               
               
               
               
             
           
               
                 TABLE 4 
               
               
                   
               
               
                   
                 commercial 
                   
                 comonomer 
                   
                   
               
               
                 polymer 
                 grade 
                   
                 content 
                 MFR 
                 density 
               
               
                 No. 
                 designation 
                 comonomer 
                 [wt %] 
                 [g/10 min] 
                 [g/cm 3 ] 
               
               
                   
               
             
             
               
                 C1 
                 FG5190 
                 1-butene 
                 6 
                 1.2 
                 0.919 
               
               
                 C2 
                 FT5230 
                 — 
                 — 
                 0.8 
                 0.923 
               
               
                   
               
             
          
         
       
     
         [0067]    The ethylene polymers C1 (LLDPE) and C2 (LDPE) are commercially available from Borealis A/S. 
         [0068]    For the examples, the appropriate amounts of propylene polymers A, elastomeric ethylene-propylene copolymers B, linear low density polyethylene polymers C, conventional additives (0.05 wt % Hydrotalcite (DHT-4A), 0.1 wt % Irgafos 168, 0.1 wt % Irganox 1010, 0.05 wt % Ca-stearate, in each case based on the sum of the weights of components A to C) and nucleating agent (NA21, based in each case on the sum of the weights of components A to C) were mixed in an intensive mixer (Henschel mixer) for 25 seconds. For CE1-CE5, CE1a and E1-E4 0.1 wt % of NA21 were used, for CE6a, E5a and E2a 0.05 wt % of NA21 were used and for CE12-CE15 and E13-E14 0.2 wt % of NA21 were used. The blends were then compounded in a twin screw extruder at a temperature of 250° C. The strands were quenched in cold water and pelletised. 
       Films 
       [0069]    0.3 mm thick films were produced on a cast/film coextrusion line (Barmag 60). 
       Bottles 
       [0070]    1 l bottles (weight 48.5 g) were extrusion blow moulded. Cycle time was 12 s, melt temperature was 195° C., melt pressure was 160 bars, die cap was 99.9%. 
         [0071]    The amounts of each component and the results of the measurements are shown in Tables 5 to 7. 
         [0000]    
       
         
               
               
               
               
               
               
             
               
               
               
               
               
               
               
               
               
               
             
               
               
               
               
               
               
               
               
               
               
             
           
               
                   
                 TABLE 5 
               
             
             
               
                   
                   
               
               
                   
                 Component A 
                 Component B 
                   
                 Component C 
                   
               
             
          
           
               
                   
                   
                 Content 
                   
                 Content 
                 MFR A+B   
                   
                 Content 
                 MFR 
                   
               
               
                   
                 Type 
                 [wt %] 
                 Type 
                 [wt %] 
                 [g/10 min] 
                 Type 
                 [wt %] 
                 [g/10 min] 
                 Influence of 
               
               
                   
                   
               
             
          
           
               
                 CE1 
                 A1 
                 85.7 
                 B1 
                 14.3 
                 2.0 
                 — 
                 — 
                 2.0 
                 (L)LDPE addition 
               
               
                 E1 
                 A1 
                 77.1 
                 B1 
                 12.9 
                 2.0 
                 C1 
                 10 
                 1.8 
               
               
                 CE1a 
                 A1 
                 77.1 
                 B1 
                 12.9 
                 2.0 
                 C2 
                 10 
                 1.8 
               
               
                 E1 
                 A1 
                 77.1 
                 B1 
                 12.9 
                 2.0 
                 C1 
                 10 
                 1.8 
                 type of A and B 
               
               
                 E2 
                 A2 
                 77.8 
                 B2 
                 12.2 
                 3.2 
                 C1 
                 10 
                 3.3 
               
               
                 E3 
                 A2 
                 78.3 
                 B3 
                 11.7 
                 2.8 
                 C1 
                 10 
                 2.5 
               
               
                 CE2 
                 A3 
                 77.1 
                 B4 
                 12.9 
                 3.5 
                 C1 
                 10 
                 3.1 
               
               
                 CE3 
                 A2 
                 78.75 
                 B5 
                 11.25 
                 1.9 
                 C1 
                 10 
                 2.0 
               
               
                 CE4 
                 A3 
                 76.86 
                 B6 
                 13.14 
                 3.3 
                 C1 
                 10 
                 3.1 
               
               
                 E1 
                 A1 
                 77.1 
                 B1 
                 12.9 
                 2.0 
                 C1 
                 10 
                 1.8 
                 amount of B 
               
               
                 E4 
                 A1 
                 81.4 
                 B1 
                 8.6 
                 2 
                 C1 
                 10 
                 2.1 
               
               
                 CE5 
                 A1 
                 86 
                 B1 
                 4 
                 2 
                 C1 
                 10 
                 2 
               
               
                 CE6a 
                 A2 
                 87.8 
                 B2 
                 12.2 
                 3.3 
                 — 
                 — 
                 3.3 
                 amount of C 
               
               
                 E5a 
                 A2 
                 85.2 
                 B2 
                 11.8 
                 3.1 
                 C1 
                  3 
                 3.1 
               
               
                 E2a 
                 A2 
                 79.1 
                 B2 
                 10.9 
                 3.1 
                 C1 
                 10 
                 3.1 
               
               
                 CE12 
                 A4 
                 87.9 
                 B7 
                 12.1 
                 2.0 
                 — 
                 — 
                 2.0 
                 LLDPE addition 
               
               
                 E13 
                 A4 
                 79.1 
                 B7 
                 10.9 
                 2.0 
                 C1 
                 10 
                 2.0 
               
               
                 E13 
                 A4 
                 79.1 
                 B7 
                 10.9 
                 2.0 
                 C1 
                 10 
                 2.0 
                 material 
               
               
                 E14 
                 A4 
                 78 
                 B8 
                 12 
                 2.1 
                 C1 
                 10 
                 2.1 
                 characteristics 
               
               
                 CE13 
                 A2 
                 78.8 
                 B5 
                 11.2 
                 1.8 
                 C1 
                 10 
                 1.8 
               
               
                 CE14 
                 A5 
                 78.3 
                 B9 
                 11.7 
                 0.4 
                 C1 
                 10 
                 0.4 
               
               
                 CE15 
                 A6 
                 75.6 
                 B10 
                 14.4 
                 1.2 
                 C1 
                 10 
                 1.2 
               
               
                   
               
             
          
         
       
     
         [0000]    
       
         
               
               
               
               
               
               
               
               
             
               
               
               
               
               
               
               
               
             
           
               
                   
                 TABLE 6 
               
               
                   
                   
               
               
                   
                   
                 Modulus 
                 Dyn. +23° C. 
                 Dyn. −20° C. 
                   
                   
                   
               
               
                   
                 MFR 
                 MD 
                 Wtot/mm 
                 Wtot/mm 
                 Haze sheet 
                 Gloss 
               
               
                   
                 [g/10] 
                 [MPa] 
                 [J/mm] 
                 [J/mm] 
                 [%] 
                 [%] 
                 Influence of 
               
               
                   
                   
               
             
             
               
                   
               
             
          
           
               
                 CE1 
                 2.0 
                 1324 
                 14.7 
                 4.5 
                 26.5 
                 107 
                 (L)LDPE addition 
               
               
                 E1 
                 1.8 
                 1096 
                 13.4 
                 11.9 
                 13.3 
                 120 
               
               
                 CE1a 
                 1.8 
                 1145 
                 13.9 
                 7.4 
                 15.2 
                 120 
               
               
                 E1 
                 1.8 
                 1096 
                 13.4 
                 11.9 
                 13.3 
                 120 
                 type of A and B 
               
               
                 E2 
                 3.3 
                 1215 
                 14.5 
                 11.5 
                 12.8 
                 125 
               
               
                 E3 
                 2.5 
                 1115 
                 15.0 
                 12.1 
                 17.6 
                 121 
               
               
                 CE2 
                 3.1 
                 1113 
                 14.9 
                 13.2 
                 45.3 
                 46 
               
               
                 CE3 
                 2.0 
                 1193 
                 14.2 
                 13.6 
                 29.4 
                 72 
               
               
                 CE4 
                 3.1 
                 1110 
                 15.9 
                 14.4 
                 54.0 
                 42 
               
               
                 E1 
                 1.8 
                 1096 
                 13.4 
                 11.9 
                 13.3 
                 120 
                 amount of B 
               
               
                 E4 
                 2.1 
                 1171 
                 12 
                 6.4 
                 11.3 
                 121.7 
               
               
                 CE5 
                 2 
                 1320 
                 3.4 
                 1.5 
                 9 
                 124 
               
               
                 CE6a 
                 3.3 
                 1366 
                 10.4 
                 4.2 
                 20.1 
                 117 
                 amount of C 
               
               
                 E5a 
                 3.1 
                 1312 
                 12.1 
                 6.8 
                 17.8 
                 121 
               
               
                 E2a 
                 3.1 
                 1168 
                 11.3 
                 11.2 
                 13.8 
                 122 
               
               
                   
               
             
          
         
       
     
         [0000]    
       
         
               
               
               
               
               
             
               
               
               
               
               
               
               
             
               
               
               
               
               
               
               
             
           
               
                   
                 TABLE 7 
               
             
             
               
                   
                   
               
               
                   
                 Tensile 
                 Haze 
                 Drop test 
                   
               
             
          
           
               
                   
                 MFR 
                 Modulus 
                 bottle 
                 23° C. 
                 0° C. 
                   
               
               
                   
                 [g/10] 
                 [MPa] 
                 [%] 
                 [m] 
                 [m] 
                 Influence of 
               
               
                   
                   
               
             
          
           
               
                 CE12 
                 2.0 
                 1540 
                 54 
                 &lt;0.8 
                 &lt;0.8 
                 LLDPE addition 
               
               
                 E13 
                 2.0 
                 1280 
                 44 
                 &gt;5 
                 3.0 
               
               
                 E13 
                 2.0 
                 1280 
                 44 
                 &gt;5 
                 3.0 
                 material 
               
               
                 E14 
                 2.1 
                 1270 
                 42 
                 &gt;5 
                 3.5 
                 characteristics 
               
               
                 CE13 
                 1.8 
                 1328 
                 59 
                 3.2 
                 0.9 
               
               
                 CE14 
                 0.4 
                 1210 
                 75 
                 &gt;5 
                 3.7 
               
               
                 CE15 
                 1.2 
                 1250 
                 82 
                 4.5 
                 2.8