Abstract:
A composite skin ( 11 ) with swept angle and dihedral for an aircraft mid-box lifting surface having a left side ( 5 ), a right side ( 7 ) and a central transition area ( 9 ) where both sides meet, that is designed and manufactured as a single part from left tip to right tip following a common ply structure for the whole part defined in relation to a single orientation rosette ( 25 ). The invention also refers to a composite aircraft mid-box lifting surface including an upper and lower panel with said composite skin ( 11 ).

Description:
FIELD OF THE INVENTION 
       [0001]    The present invention refers to a composite skin for an aircraft mid-box lifting surface made as a single part and to an aircraft mid-box lifting surface comprising said skin in its upper and lower panels. 
       BACKGROUND OF THE INVENTION 
       [0002]    Current lifting surface architectures for jetliners consist of 2 swept torsion boxes (right and left sides) with a central joint at the aircraft centreline. Eventually, a central torsion box is used instead of a central joint depending on the aircraft architecture. 
         [0003]    In classic metallic structures, the skins of such torsion boxes were manufactured with a number of riveted foils. 
         [0004]    In modern aircraft, thanks to the contribution of composites to parts integration, those skins can be single composite parts from the central joint to the tip. In other words, current state-of-art allows having only 4 full-size skins to produce left and right torsion boxes (2 upper skins and 2 lower ones). A central joint (or central torsion box) is still used to fix both sides to the aircraft fuselage or body. 
         [0005]    There are known some proposals of single parts for aircraft lifting surfaces. In this respect US 2003/0098116 A1 discloses a stabilizing element comprising two portions in which the principal directions intersect at a non-singular angle which is manufactured by a continuous lay-up operation on both parts using two lay-up coordinate systems (one for each portion). This proposal seems to be applicable to small sized lifting surfaces (stabilizers for helicopters or sport airplanes for example). 
         [0006]    The aircraft industry demand continuously a higher degree of design optimisation of typical airliners&#39; lifting surface architectures (multi-rib or multi-spar) driving to both cost and weight reduction. 
         [0007]    The present invention is intended to satisfy this demand. 
       SUMMARY OF THE INVENTION 
       [0008]    It is an object of the present invention to provide skins manufactured as single parts from tip to tip (1 upper and 1 lower skins with swept angle and dihedral) for multi-rib or multi-spar mid-boxes as a step beyond in parts integration applied to torsion boxes of aircraft lifting surfaces. 
         [0009]    It is another object of the present invention to provide aircraft lifting surfaces with important savings removing the central joint, while keeping an architecture that could be detached if needed (maintainability, reparability) what is not strange for airliners. In other words, an object of this invention is to provide a single mid-box for both sides (with stringers, spars and/or ribs to be added subsequently) instead of left and right torsion boxes. 
         [0010]    It is another object of the present invention to provide aircraft lifting surfaces easier to manufacture and assemble. 
         [0011]    These and other objects of the present invention are met in one aspect by a composite skin with swept angle and dihedral for an aircraft mid-box lifting surface having a left side, a right side and a central transition area where both sides meet, that is designed and manufactured as a single part from left tip to right tip following a common ply structure for the whole part defined in relation to a single orientation rosette. 
         [0012]    In another aspect, the invention defines a composite lifting surface build-up, even for high swept angle, by a single upper panel and a single lower panel, having continuous composite skins from left tip to right tip. The single panel concept might allow having a detachable structure configuration (sometimes suitable for airliners) both for multi-rib or multi-spar architectures if desired. 
         [0013]    From the manufacturing and assembly side important advantages are encountered. The central transition area will reduce its thickness, as no box joint exists. This, combined with laying both sides as a single panel, optimises lead times and reduces the amount of material needed. On the other side, a massive central joint is reduced, simplifying the assembly of the component. 
         [0014]    Other characteristics and advantages of the present invention will be clear from the following detailed description of embodiments illustrative of its object in connection with the attached figures. 
     
    
     
       DESCRIPTION OF THE DRAWINGS 
         [0015]      FIG. 1  shows a perspective of a single panel upper cover of a horizontal tail plane mid-box (with sweep angle and dihedral). 
           [0016]      FIGS. 2   a  and  2   b  shows 2D top and front views of the same single panel upper cover of a horizontal tail plane mid-box. 
           [0017]      FIG. 3  shows a top-view sketch of a lifting surface mid-box (left and right) represented by its spars with alternative ply orientation rosettes. 
           [0018]      FIG. 4   a  shows a sketch of the single skin with a first ply laid only on the left side. 
           [0019]      FIG. 4   b  shows a sketch of the single skin with a second ply being laid only on the left side over the previous first ply in this case. 
           [0020]      FIG. 4   c  shows a sketch of the single skin with a third ply being laid only on the left side over the previous second ply in this case. 
           [0021]      FIG. 4   d  shows a sketch of the single panel with a fourth ply being laid over the third one on the left side, and being the first one on the right side. This is the first continuous ply in this case. 
       
    
    
     DETAILED DESCRIPTION OF THE INVENTION 
       [0022]    In a preferred embodiment of the invention the upper skin or lower skin of the mid-box is a single part  11  from left tip to right tip in composites with fully integrated design. 
         [0023]    The resulting composite skin  11  could be considered having three different areas: left and right sides  5 ,  7  with its integrated design according to the stress needs and a central transition area  9  where the two sides meet. 
         [0024]    An important amount of plies is shared by left and right sides  5 ,  7 . The remaining plies are dropped-off conveniently at the central transition area  9 . 
         [0025]    In addition to part count reduction and contribution to integration, this concept allows weight savings by removing the need for a massive central joint to fix left and right torsion boxes of classic configurations, while keeping architecture able to be detached if needed. 
         [0026]    In a preferred embodiment carbon fibre composites will be used for manufacturing these skins. 
         [0027]    The main driver of this invention has been to bring into line the individual orientations that are encountered on multi-box designs for skins. 
         [0028]    Typically, in lifting surfaces, the 0° orientation is parallel or close to the main load paths, i.e. the left rear and front spars  13 ,  15  and the right rear and front spars  17 ,  19  or to a direction in-between. Accordingly in the known art the left side  5  of skin  11  would be laid-up according to the orientation rosette  21  represented in a dot line and the right side  7  of skin  11  would be laid-up according to the orientation rosette  23  represented in a broken line. 
         [0029]    Analysing sweep angles of the spars of lifting surfaces currently used for jetliners, a new global orientation reference can be defined in order to lay-up both sides on a single shot while being compatible with main load paths. 
         [0030]    Therefore, both sides  5 ,  7  of skin  11  will have the same rosette  25 . In a preferred embodiment of the invention, the 90° direction of the global orientation reference  25 , in continuous stroke in  FIG. 3 , matches with the flight direction  31 , but this is an arbitrary criteria. Any other reference could also be convenient. 
         [0031]    A proper lay-up design (that changes the traditional aircraft nomenclature of 0°, +45/−45 and 90° for composite components) optimises laminates at both sides (obtaining equivalent properties of the skins to the multi-box concept) while having a transition area (around the centreline) where the two laminates meet. 
         [0032]    In a preferred embodiment of the invention, in order to have proper flight conditions, left and right stacking sequences are symmetrical with regard to the aircraft longitudinal axis  31 . 
         [0033]    The global orientation reference  25  allows having an important amount of plies shared between left and right sides  5 ,  7 . Those that are not common for the two sides  5 ,  7  are dropped-off conveniently for an optimized design in the central transition area  9 . The invention can be applied to uni-directional (UD) or fabric composite pre-impregnated tapes or to any kind of dry textiles. 
         [0034]    In a preferred embodiment of the invention prepreg UD tape will be used as raw material of skin  11 . 
         [0035]    To be understood as a mere illustration,  FIGS. 4   a  to  4   d  define the principle of the invention here described according to a preferred embodiment, where a chosen rosette  25  allows laminating a certain stacking sequence and sharing carbon tape plies between left and right sides  5 ,  7  of skin  11 . 
         [0036]      FIGS. 4   a  to  4   c  show different plies being laid that only belong to the left side  5 .  FIG. 4   a  shows a first ply  41  laid only on the left side  5  (a −45° ply according to orientation rosette  21 ).  FIG. 4   b  shows a second ply  43  being laid only on the left side  5  (a+45° ply according to orientation rosette  21 ) over the previous first ply  41 .  FIG. 4   c  shows a third ply  45  being laid only on the left side  5  (a 90° ply according to the orientation rosette  21 ) over the previous second ply  43 . 
         [0037]      FIG. 4   d  shows a fourth ply  47  being laid over the third one 45 on the left side  5  (a 0° ply according to the orientation rosette  21 ) and being the first one on the right side  7  (a −45° ply according to the orientation rosette  23 ). This is the first continuous ply in this case. 
         [0038]    The central transition area  9  has to be wide enough to ensure proper paths of the lay-up device while laying the plies. Therefore, a smooth transition area is required at the centreline of the skin  11 . Ply drop-offs in the central transition area  9  are performed in a way to optimise the design (in terms of reinforcements for ribs and/or spars attachments and/or for loading reasons). 
         [0039]    Therefore, in a preferred embodiment the lay-up device would lay plies from one side to the other, being able to cut each ply at the desired position and shape whether it takes place at the transition area or at the outline of the skin. 
         [0040]    In another embodiment of the invention, a continuous external ply could be wanted in one surface of the skin (or in both surfaces) to avoid peeling effects. A detailed design would provide the most suitable direction of a UD or fabric composite prepreg tape or a kind of dry textile as continuous external ply. 
         [0041]    In a preferred embodiment of the invention, contoured automated tape lay-up (3D ATL) is the chosen technology for manufacturing the single piece skins from tip to tip. Current 3D ATL machines allow deposition of tape onto a tool with a surface of similar shape of the final skin with the double curvature encountered as the addition of the skin&#39;s camber and the dihedral of the lifting surface. 
         [0042]    A subsequent autoclave cycle would be used to cure the part. Skins can be co-cured, co-bonded, secondary bonded or riveted to stringers and/or spars and/or ribs. 
         [0043]    Other composite processing techniques like resin infusion/injection of dry stacking sequences placed in open or closed moulds or others would also be suitable for the manufacturing of those skins. 
         [0044]    Modifications may be introduced in the preferred embodiment just set forth, which are comprised within the scope defined by the following claims.