Abstract:
A photodiode-FET combination having an optimized layer structure wherein the photodiode and the FET are separated from one another by a separating trench and are separated from the substrate by barrier layers forming a pn-junction in order to avoid tributary currents. A layer sequence is provided formed of an absorption layer grown on in surface-wide fashion, of a photodiode layer that is likewise grown on in surface-wide fashion and which is etched back to the region of light incidence in the region of the photodiode, of a channel layer in the region of the FET, and of a cover layer on the channel layer which forms a gate.

Description:
BACKGROUND OF THE INVENTION 
     Developments in optical data transmission systems involve the use of integrated opto-electronic circuits for the connection between optical and electronic components. The problem of integration of the photodetector and pre-amplifier arises at the receiver side. Good compatibility of the semiconductor layers and manufacturing techniques required for the various components is required. A monolithically integrated, planar module that contains a photodiode and a field effect transistor (FET) on a semiconductor substrate and that takes the different requirements of doping concentration and layer thickness into consideration is recited in H. Albrecht, Ch. Lauterbach, &#34;Monolithically Integrated InGaAs/InP:Fe Photodiode-Junction Field-Effect Transistor Combination&#34;, Siemens Forschungs-und Entwicklungsberichte 17, 195-198 (1988), incorporated herein by reference. 
     For a high external quantum efficiency, an optimized photodiode requires an adequately thick absorption layer of n-InGaAs having low residual doping. This nominally undoped InGaAs layer is a prerequisite for a low capacitance as well as a low dark current and, consequently, good noise properties. A highly doped n-conductive semiconductor layer (for example, InGaAs or InAlAs or InP) on the InP:Fe substrate reduces the series resistance and the transient time effects, i.e. the carrier transient time of the photodiode. 
     For a high transconductance, the FET requires a highly doped n +  --InGaAs layer that must be correspondingly thin for a good cut-off behavior of the FET. The cover layer of n-InP or N-InAlAs forms a hetero barrier vis-a-vis the InGaAs and enables the realization of a blocking metal-to-semiconductor junction as a gate, or enables the manufacture of a barrier layer gate together with a p-diffusion or p-implantation. This layer also has the advantage that, due to the higher band spacing of InP or InAlAs compared to InGaAs, a passivation of the pn-junction at the component surface lengthens the long-term stability and reduces leakage currents. This advantage results both for the photodiode as well as for the FET. 
     SUMMARY OF THE INVENTION 
     It is an object of the present invention to specify a monolithically integrated photodiode-FET combination having a semiconductor layer structure that is optimized both for simple manufacturability and good functionability. 
     This object is achieved with a photodiode-FET combination wherein a grown absorption layer is provided over a substrate; a photodiode layer of second conductivity type is applied on the absorption layer at a region above the absorption layer where the field effect transistor is formed and also at a region above the absorption layer where the photodiode is formed; a second contact is also applied on the absorption layer at the location where the photodiode is formed; a first annular contact is provided on the photodiode layer at the region of the photodiode; a anti-reflection layer is provided on the photodiode layer inside the annular first contact; a channel layer of first conductivity type is applied on the photodiode layer at the region of the field effect transistor; a cover layer is applied on the channel layer; and a separating trench is provided between the photodiode and the field effect transistor. 
     In a further improvement of the invention a first barrier layer of second conductivity type is grown between the substrate and the absorption layer and a second barrier layer of first conductivity type is grown on the side of the first barrier layer that faces away from the substrate. 
     The semiconductor layer structure of the invention has the advantage that all required dopings and layer thicknesses can be manufactured in one work cycle on a planar, semi-insulating InP substrate crystal, and is manufactured in surface-wide fashion with epitaxial processes such as, for example, VPE, MOVPE, MBE or MOMBE. 
     The selective etching properties of the different mixed crystal layers are utilized in the following chip technology in order to selectively expose defined layers and contact them. Given optimized layer sequences for both components, thus no selective doping steps such as, for example, diffusion or ion implantation, are required after the epitaxy of the layers. Thus, high-temperature processes that could deteriorate the properties of epitaxially grown hetero layers and doping profiles are eliminated. 
    
    
     BRIEF DESCRIPTION OF THE DRAWING 
     The photodiode-FET combination of the invention is shown in cross section in the drawing figure. 
    
    
     DESCRIPTION OF THE PREFERRED EMBODIMENTS 
     In an especially advantageous development of the photodiode-FET combination of the invention, a first barrier layer 2 and a second barrier layer 3 are successively grown on a substrate 1 of, for example, semi-insulating indium phosphide. These barrier layers 2, 3 can be each respectively formed of InP, InAlAs, or InGaAlAs. The first barrier layer 2 is p-doped with an acceptor density of N A  =10 15 . . . 10 18  cm -3  ; and the second barrier layer 3 is n-doped and has a donor density of N D  =10 16 . . . 10 18  cm -3 . The first barrier layer has a thickness of about 0.2 to 2 μm; and the second barrier layer 3 has a thickness of approximately 0.2 to 3 μm. These barrier layers 2, 3 form a blocking pn-junction that, together with a separating trench 14 that extends into the substrate 1 and is situated between the photodiode and the FET, reduces leakage currents via the semi-insulating substrate 1. In addition, the second barrier layer 3 reduces the transient time effects and series resistance in the photodiode. 
     An absorption layer 4 is grown surface-wide over this second barrier layer 3. For example, this absorption layer 4 is composed of InGaAs and is nominally undoped (donor density N D  &lt;2*10 15  cm -3 ) and has a thickness of 1 to 3 μkm. This absorption layer 4 is provided as the absorption layer for the photodiode. A photodiode layer 5 of p-doped InP, InAlAs, or InGaAlAs having an acceptor density of N A  =10 16 . . . 10 18  cm -3  and a thickness of 0.2 to 1 μm is grown on the absorption layer 4. This photodiode layer 5 is likewise grown in surface-wide fashion and forms first the p-region of the photodiode and, second, also electrically separates the entire photodiode layers from the following FET layers as a result of its blocking property. The cut-off behavior of the FET, moreover, is additionally beneficially influenced by this underlying photodiode layer 5 as a buffer layer (K. Steiner, U. Seiler, K. Heime, &#34;Influence of p-InP buffer layers on submicron InGaAs/InP junction field-effect transistors&#34;, Appl. Phys. Lett.  53, 2513-2515 (1988) incorporated herein by reference). This photodiode layer 5 is etched back to such an extent in the region of the photodiode 16 that the surface of the absorption layer 4 is exposed to the extent required for the application of a contact on the absorption layer 4. 
     A channel layer 6 of, for example, InGaAs is grown onto the photodiode layer 5 in the region of the FET 15. This channel layer 6 of the FET is n-conductively doped with a donor density of N D  =10 16 . . . 10 18  cm -3  and has a thickness of 0.05 to 2 μm. The transconductance and the cut-off behavior of the FET are defined by the thickness and by the doping of this channel layer 6. 
     A cover layer 7 of InP or InAlAs or InGaAlAs is grown on as the gate of the FET. This cover layer is p-conductively doped with an acceptor density of N A  =10 16  . . . 10 18  cm 31  3 given a thickness of 0.2 to 1 μm. This cover layer 7 forms a hetero gate for the JFET. Alternatively, this layer can be n-conductively doped with a donor density of N D  =10 14 . . . 10 16  cm -3  given a thickness of approximately 0.5 μm. And given selection of a suitable contact material for a gate contact applied onto this cover layer 7, a MISFET can thus be realized. The channel layer 6 and the cover layer 7 are grown on only in the region of the FET 15 or are removed in the region of the photodiode 16 by selective etching. The realization of the gate region of the FET 15 and of the p-region of the photodiode 16, i.e. the parts of the photodiode layer 5 remaining in the region of the photodiode 16, can occur on the basis of a self-aligned technology, for example the T-gate technique (D. Wake, A. W. Livingstone, D. A. Andrews, G. J. Davies, &#34;A Self-aligned InGaAs Junction Field-Effect Transistor Grown by Molecular Beam Epitaxy&#34;, IEEE EDL-5, 285-287 (1984), incorporated herein by reference). In any case, the surface-wide, p-conductively doped layer (photodiode layer 5) is structured. 
     In the photodiode-FET combination of the invention, a first contact 9 that is annularly fashioned is applied on that part of the photodiode layer 5 remaining in the region of the photodiode 16, a second contact 12 is applied in the region of the photodiode 16 on the absorption layer 4, a gate contact 8 is applied on the cover layer 7, a drain contact 10 is applied on the channel layer 6, and a source contact 11 is applied on the channel layer 6 in the region of the drain or of the source. An anti-reflection layer 13 applied inside the annular, first contact 9 of the photodiode 16 increases the efficiency of the photodiode by approximately 30%. The photodiode 16 and the FET 15 are separated by a separating trench 14 that extends through all epitaxial layers 2, 3, 4, 5, 6 down into the substrate 1. 
     Alternatively to the application of the barrier layers 2, 3, a surface-wide p-diffusion or p-implantation into the semi-insulating InP substrate 1 can be realized before the epitaxy in order to improve the insulating property of the substrate 1. 
     When the semi-insulating property of the substrate 1 suffices or when an adequate improvement of the insulating property of the substrate 1 is achieved with the diffusion or implantation, the barrier layers 2, 3 can be omitted without the basic function of the FET 15 being deteriorated. 
     By contrast to the prior art (for example, pinFET structures as disclosed in Y. Akahori, S. Hata et al, &#34;Monolithic InP/GaInAs pinFET Receiver using MOMBE-Grown Crystal&#34;, Electronics Letters 25, 37-38 (1989), incorporated herein by reference), the structure of the photodiode-FET combination of the invention has the advantage that the FET layers having the structures in the micrometer and sub-micrometer range that are difficult to manufacture lie farthest toward the top in the structure of the invention, and thus allow a contact exposure in the photolithography. By contrast, the photodiode structure that lies only slightly deeper can still be manufactured without problems with considerably greater tolerances. Given the standard doping levels, the step between the field effect transistor and the photodiode given the structure of the invention also amounts to only about 0.5 to 0.6 μm, whereas semiconductor steps of 2 to 3 μm are necessary given the structure published in D. A. H. Spear, P. J. G. Dawe, G. R. Antell, W. S. Lee, S. W. Bland, &#34;New Fabrication Technology for Long-Wavelength Receiver OEIC&#39;s&#34;, Electronics Letters 25, 156-157 (1989), incorporated herein by reference. 
     Although various minor changes and modifications might be proposed by those skilled in the art, it will be understood that we wish to include within the claims of the patent warranted hereon all such changes and modifications as reasonably come within our contribution to the art.