Abstract:
In a method for manufacturing lamination stacks of controlled height in a tool, starting, material is provided as continuous strip delivered from a coil or as an individual sheet. Laminations are punched from the starting material in several punching steps to a required contour of the laminations. A heat-curing adhesive is applied onto the laminations prior to performing a last punching step. The laminations are combined to a lamination stack. The laminations of the lamination stack are partially or completely heated in a lamination storage. The adhesive is liquefied by heating the lamination stack to build up adhesion and then solidified. Curing the adhesive at the liquefying temperature or solidifying the adhesive in the tool by cooling and subsequently heating the adhesive to a temperature below the liquefying temperature is possible so that the adhesive does not melt but undergoes further curing resulting in higher temperature stability.

Description:
CROSS-REFERENCE TO RELATED APPLICATIONS 
       [0001]    This application is a divisional application of United States application for patent Ser. No. 14/384,713, having a filing date of 12 Sep. 2014, said application Ser. No. 14/384,713 being a national stage filing of international application No. PCT/EP2013/000742 having an international filing date of 13 Mar. 2013 and designating the United States, the international application claiming a priority date of 14 Mar. 2012, based on prior filed German patent application No. 10 2012 005 795.4, the entire contents of the aforesaid United States application; the aforesaid international application, and the aforesaid German patent application being incorporated herein by reference. 
     
    
     BACKGROUND OF THE INVENTION 
       [0002]    The invention relates to a method for manufacturing stacks of laminations with a controlled height in a tool in which laminations are punched, have bonding agent applied to them, and are put together to form the lamination stack. 
         [0003]    Electrical machines often use cores consisting, of stacked laminations, which are fabricated out of cut electric sheets. A punch press is normally employed to cut out the individual laminations. The core or stack can be fabricated in various ways, to include mechanically joining the parts in the press to form cores, and welding, adhesively bonding or mechanically mating the laminations into stacks outside the press. 
         [0004]    DE 24 46 693 provides examples in the field of manufacturing stacks outside of the tool and press. This publication describes how to manufacture stacks of steel that has a thermosetting coating. EP 0 121 173 describes an approach to solving the problem, in which the laminations are provided with elevations and depressions, with which the laminations are pressed together into a stack. This so-called linkage method is associated with several disadvantages:
       a) The linkage technology requires the manufacture of very complex tools, whose parts are very sensitive in terms of material quality, and can be less robust than tools with which the laminations are not linked together. This increases both the costs and the risks associated with the method, which can hamper suitability for use.   b) Very thin steel sheets, e.g., those less than 0.35 mm thick, are very difficult to link, thereby resulting in inefficient methods.   c) Some products require that each lamination be turned by a specific amount. In a stack in which the laminations are not interlinked, the rotational angle is limited by the number of existing linkage locations, i.e., the smallest possible rotational angle is 90° given four existing linkage points.   d) Another disadvantage to the current linkage technology is that materials of varying thickness or characteristics (often distinguished by different quality designations) cannot be joined together.       
 
         [0009]    Other technologies that use externally applied adhesive have also been tried. Examples include DE 35 35 573 and DE 203 18 993, which both describe a method for using an adhesive that is applied to the band surface. An attempt has also been made to use capillary adhesive bonding, i.e., to run an adhesive “seam” down the outside edge of the stack. 
         [0010]    Also known are methods (JP 2005 269 732) in which dots or lines of adhesive are applied to punched laminations. The adhesive is applied with an application head comprised of several nozzles. 
         [0011]    In another method (JP 2001 321 850), the adhesive is sprayed onto the laminations at prescribed positions. The application unit provided for applying the adhesive has a distributor with three nozzles from which the adhesive exits. 
         [0012]    The different existing technologies for applying adhesive to the band surface as an integrated part of core manufacture are associated with various difficulties:
       a) The possible pressing rates are limited by how fast the adhesive is applied. For example, DE 203 18 993 defines speed ranges of up to 200-300 strokes per minute. Cost-effective core production requires that pressing rates measure at least 400 strokes per minute, with typical values in excess of 600 strokes per minute being highly desirable.   b) It is difficult to keep the tool clean. For example, a batch size limit of several thousand strokes is likely for one of the technologies, after which the tool has to be serviced and cleaned. The normal maintenance interval for a carbide tool lies at a minimum of 2,000,000 impacts. Shorter run times tangibly drive up the production costs.   c) Existing systems like those in DE 20 31 899 are known to have problems with component wear.       
 
         [0016]    The difficulties a) through c) all illustrate the fact that applying the adhesive depends on the contact between the application unit and strip. Further difficulties are
       d) The stacks fabricated with some adhesive bonding technologies can exhibit variable/unreliable stack strengths.   e) Tools with integrated application units can cost significantly more than standard tools.   f) The technology underlying the application system integrated into the tool can normally not be used in already existing tools.   g) In another known method (EP 1 833 145 A2), great success has been achieved in the contactless generation of lamination stacks with one application head per partial bond. One constraint on this method is the limited adhesive available for this method. This adhesive forms no long-term bond between the laminations under the thermal conditions for the normal range of application for such a lamination stack. Since the laminations are only partially bonded together with the adhesive, a high strength cannot be guaranteed. In addition, oscillations between the laminations cannot be prevented in some instances.       
 
       SUMMARY OF THE INVENTION 
       [0021]    The makes it possible to fabricate stacks of laminations with the highest strength as an integrated part of the pressing operation at economically competitive speeds. 
         [0022]    In this invention, the incoming material is routed to a compensating sheave, then to a feeder, then to the press, and then to the tool. Although the starting material for the process is usually supplied in the form of coils, cut strips of a specific length can also be used. Each material thickness that can be punched by a press can be joined together when using this technology. In particular thin materials less than 0.5 mm thick benefit from the use of adhesive bonding as the joining technology, because the precision of the tools and machines normally required for these thin materials is diminished. The method can be used to machine materials with varying quality, thickness, characteristics and coatings. It is even possible to join materials with varying quality, thickness, characteristics and coatings in the same stack. 
         [0023]    In this product, use is preferably made of adhesives that, once completely cured, allow a sufficient strength over the long term at temperatures exceeding 80° C., in part even exceeding 180°. 
         [0024]    Use is preferably made of radically curing adhesive systems so as to achieve a rapid curing reaction during manufacture. Methacrylate adhesives are here preferably used, which cure by way of a 2-substance system, wherein one component consists of resin, essentially comprised of ethyl methacrylates and/or methyl methacrylates and/or isobornyl methacrylates, and itself cures somewhat more slowly or not at all, and a curing component, the initiator, essentially comprised of peroxides with a cross-linker, for example consisting of trifunctional ester, and an accelerator, for example consisting of tertiary aniline derivatives. This initiator is only limitedly integrated into the adhesive matrix, and can thus only be present in limited quantities. Contact without any real mixing of both components is most often already enough to achieve a sufficient curing reaction, since individual radicals from the initiator react with the adhesive when the initiator comes into contact with the adhesive, and these reactions under certain conditions trigger an entire chain of additional reactions within the adhesive. The cross-linkers primarily contribute to the higher temperature stability, which preferably measures over 180° C. on a sustained basis. The cross-linkers themselves can be contained in both the initiator and adhesive. 
         [0025]    However, the adhesive can also be an anaerobic system of resin and curing agent, in which the resin dimethacrylic acid ester and the curing agent or initiator contains dissolved metal ions, wherein the resin also cross-links in a radical reaction in combination with the metal ions, to the exclusion of oxygen. 
         [0026]    However, the adhesive can also be a combination of the two resin and curing agent systems mentioned above (9+10), wherein this makes it possible to accelerate the curing reaction and further improve thermal resistance. 
         [0027]    In this process, the initiator is applied partially in flat areas or over the full surface of the upper and/or lower side of the strip without contact via spraying or vapor deposition or with contact via punching, milling, rolling or another flat application process. The quantity and hence layer thickness of the initiator is controlled by the application device, so that the curing reaction can be accelerated and/or the characteristics of the subsequent adhesive bond can be optimally adjusted. 
         [0028]    The adhesive itself is applied without contact as drops in the form of individual drops, or applied partially in flat areas or over the full surface of the upper and/or lower side of the strip without contact via spraying or with contact via punching, milling or rolling. However, the adhesive is preferably applied to the other side of the band material wetted by the initiator, although it can also be applied to the same side. 
         [0029]    If the adhesive is applied over the full surface, it is preferably applied right before the lamination is detached from the material strip so as to minimize contamination of the tool with adhesive, and also, in particular through spatial separation, to avoid contact with the initiator, and thus a curing reaction. 
         [0030]    However, it is also possible to first apply the adhesive, and subsequently apply the initiator to the opposite side, but then to spray it onto the adhesive preferably without contact and/or directly, immediately and a few seconds before joining with the adjacent lamination takes place, and hence before initial reactions in the adhesive system have progressed too far. 
         [0031]    The adhesive can be applied before or after the tool with external equipment or inside the tool itself by means of an integrated system. There are various options in terms of where precisely to apply the adhesive. For example, it is also possible to apply the initiator in the tool, and store the laminations outside of the punch system or directly continue processing them by also wetting, them outside of the punch system and adhesively bonding them in a separate clamping device. 
         [0032]    During the process in the tool, the strip is punched into individual laminations. The stack of laminations is joined together in the matrix. A good bond between the laminations is ensured by the pressure of the punch in the last punching operation and a brake. This high pressure is essential for uniformly curing the adhesive, which in turn imparts a uniform strength to the stack of laminations. 
         [0033]    However, it is also possible to apply an adhesive that cures on its own when exposed to temperature, i.e., does not absolutely need an initiator. Suitable here are acrylate adhesives, for example consisting of methacrylic acid and acrylic acid, or for example epoxy resin adhesives, e.g., essentially consisting of bisphenol A, or also urethane resin adhesives. It is also applied partially or completely over the surface of one or both sides of the lamination. However, it can also be present in dry form on the band material already before the punching process. 
         [0034]    The adhesive can be made up of a resin and curing agent system, which completely cross links only when influenced by temperature. The resin consists of epoxies, for example based on bisphenol A, novolac, etc., and the curing agent consists, for example, of polyaminoamides, polyamides, dicyandiamide, phenol resins, carbonic acid anhydrides, etc., or of a hot-melt adhesive that melts far above the usual service temperature, and thus can adhesively bond during the cooling process, for example hot-melt adhesive based on polyamide. Use can also be made of an adhesive that combines both adhesive bonding processes, for example hot-melt adhesives based on polyester urethane prepolymers with integrated isocyanate groups. 
         [0035]    However, how the adhesive is heated is the crucial factor. Only after the punching process are the laminations preferably heated partially or, if permitted by the lamination design, completely in a lamination storage vessel, and thereby adhesively bonded. Given a partial adhesive bonding, the stack of laminations can be heated and adhesively bonded again later in a separate follow-up process. However, if this can take place completely in the tool, the product is already finished. Complete adhesive bonding becomes possible as a function of the heating technology if the product design does not exceed a distance from the outer contour of at most about 30 mm, since regions of the outer contour would otherwise burn up, and areas of the inner contour would be too cold for adhesive bonding due to the comparatively slow heat input or flow inside the stack of laminations. An induction coil can preferably be used in the tool for heating purposes, which heats the entire stack of laminations. 
         [0036]    While clamping the laminations, it also helps to have a contact pressure that supports the reaction and bonding of the adhesive in addition to the heating process. However, it is also possible to heat the stack of laminations with any other heating systems, for example infrared radiation or heating filaments, which exhibit high resistances as current passes through, become hot as a result, and can release heat to the stack of laminations. 
         [0037]    If the adhesive bonding of the lamination stack does not take place continuously in this hopper, a separating layer very poorly wetted with adhesive can be sprayed onto the top side of the uppermost lamination or on the bottom side of the lowermost lamination, so as to prevent any adhesive bonding from taking place there or subsequently enable an easy separation there. Or a separating film or spacer can also be inserted, which also prevents adhesive bonding at this location. 
         [0038]    However, heating can also take place on the individual finished or partially finished lamination or directly on the material strip because very high energy is able to bring the adhesive to reaction temperature in the shortest time. This preferably takes place with induction coils placed in close proximity to the adhesive surface.  FIG. 1  shows a tunnel  1  through which the strip  2  runs and to which the coils  3  are secured. However, the adhesive  4  can also be rapidly heated in such a tunnel  1  via radiation, such as laser, infrared or some other radiation source, or waves, such as microwaves. If the adhesive is heated over the partial or full surface of the lamination  5  so as to be reactive, this area is joined with the adjacent lamination when separating the lamination out of the strip, and fixed in place under a pressure until such time as the curing reaction has sufficiently run its course. 
         [0039]    In this system, the individual stacks of laminations can also be separated by briefly deactivating the heat source and not heating a lamination enough for the curing reaction. However, the separating processes mentioned in  22  are also conceivable. 
         [0040]    However, it is also conceivable to combine both heating mechanisms, for example by initially heating the adhesive on the individual lamination and having the reaction remain active for even longer by keeping the stack of laminations warm and under pressure even longer in the joined state. 
         [0041]    One option is to control the distribution of adhesive or initiator in such a way as to interrupt it when a new stack is to be initiated. This controller can be linked with a press controller, e.g., so as to prevent the distribution of adhesive drops after a fixed number of punching strokes. This would result in the fabrication of laminations without adhesive, and thus facilitate the initiation of a new stack in the brake. 
         [0042]    A clear advantage to this technology is that it does not depend on physical bonding to join the parts together. For this reason, consecutive laminations can be turned at any angle required for the product. 
         [0043]    The only speed constraints placed on a press when using, this technology are the speed of the adhesive application system and the curing time for the adhesive in the brake. A longer brake permits a longer curing time, if needed. As a result, this technology makes it possible to operate presses with comparable or higher speeds than with other joining technologies. 
     
    
     
       BRIEF DESCRIPTION OF THE DRAWINGS 
         [0044]    The drawings below are intended to provide a better understanding of the description of an exemplary embodiment according to the invention. 
           [0045]      FIG. 1  is a schematic view of an induction channel with a passageway for strips from which laminations are punched. 
           [0046]      FIG. 2  is a schematic view of a punch press with a tool for manufacturing stacks of laminations. 
           [0047]      FIG. 3  is a schematic view of a tool in the punch press. 
           [0048]      FIG. 4  is a schematic view of a controller for an adhesive application unit. 
           [0049]      FIG. 5  is a magnified view of an application head of the adhesive and/or initiator application unit according to  FIG. 4   
           [0050]      FIG. 6  is a schematic view of an application head, with which a large area of an initiator is applied to a lamination. 
           [0051]      FIG. 7  shows several application heads, with which several small areas of initiators are applied to a lamination. 
           [0052]      FIG. 8  is a schematic view depicting the attachment of the adhesive application unit to a tool. 
           [0053]      FIG. 9  is a top view of a strip on which several dots of an initiator are applied in the region above an applicator roll for an adhesive. 
           [0054]      FIG. 10  is a magnified view of a detail on  FIG. 9 . 
           [0055]      FIG. 11  is a view of three rolls used for applying adhesive. 
           [0056]      FIG. 12  is a side view of the applicator roll for the adhesive. 
           [0057]      FIG. 13  is a top view of the applicator roll according to  FIG. 12 . 
           [0058]      FIG. 14  is a schematic view of a hopper in which laminations lying one on top of the other are stacked into a lamination stack. 
           [0059]      FIG. 15  is a schematic view of a strip used to punch laminations, several of which are not provided with an initiator. 
       
    
    
     DESCRIPTION OF PREFERRED EMBODIMENTS 
       [0060]    An exemplary embodiment will be used below to describe this technology in detail. The stacks of laminations are being exemplarily used for rotors and/or stators of electric motors. 
         [0061]      FIG. 2  shows a schematic view of a punch press. The decoiler  8  has a coil  7  of the starting material. As evident, the material is guided through a compensating sheave  9 , and then in a feed device  10  and a press frame  11 ′ of a press  11 . The tool  13  sits on a press table  12 , and consists of two parts, an upper part  13   a  and a lower part  13   b.  An upper beam  14  of the press moves back and forth to punch laminations out of the strip-type material  2 . 
         [0062]    A few more details regarding the arrangement of key elements in the press frame are schematically denoted on  FIG. 3 . In this example, the application unit for the initiator is situated on the front side of the tool  13 , and can be secured either to the upper  13   a  or lower  13   b  part of the tool  13 . The application valve of the application unit operates without contact. 
         [0063]    Prior to entry into the tool  13  or between the upper part  13   a  and lower part  13   b,  the initiator is applied over a partial or full surface of the strip-type starting material  2  in the form of a thin layer of film  15  by spraying. 
         [0064]    The press  11  is hooked up to a controller  16  ( FIG. 4 ), which sends a control signal per press stroke to a controller  17  for actuating the application valves in an adhesive application unit  18 . The signal in the controller  17  sends an electrical current pulse directly to the respective valve  19  of the application unit  18 . The valve  19  for the initiator opens up a short, preset time in which the initiator is sprayed onto the strip surface as uniformly as possible under pressure. This gives rise to the thin layer of film  15  on the strip  2 . The initiator exits a nozzle  21  in the form of drops ( FIG. 5 ). The initiator drops  23  are atomized as they exit the nozzle  21  with the help of sprayed air  22 . The nozzle  21  is part of an application head  20 , which in turn is a constituent of the application unit  18 . In the example, the application head  20  can be spaced apart from the strip surface  24  by about 1 to about 100 mm. The timing of the signal for spraying is very important. Timing is necessary so as to apply the initiator during the correct segment of the press stroke, at precisely the point where the strip material  2  is at rest. This enables a uniform distribution and exact placement of the initiator. If the initiator were to be applied during the forward motion of the band material  2 , the quantity applied would have to depend on the feed rate, since the feed rate is not linear. 
         [0065]    The initiator is stored in containers  25  next to the press  11 . When the containers  25  are exposed to pressure  26 , the initiator is conveyed out of the containers  25  through at least one line  27  to the application heads  20 , with which the initiator is sprayed onto the strips  2  in the manner described. The freshly applied initiator surface(s)  15  ( FIG. 4 ) then lie(s) either on the top side  28   a  or the bottom side  28   b  of the strip  2 , depending on what side the initiator is sprayed. It is preferably sprayed onto the upper side  28   a  of the strip  2 . 
         [0066]    The controller  17  and application unit  18  advantageously constitute an application system. Depending on the distribution required, there is more than one application system to apply the initiator onto the strip  2 . All suitable valve systems are possible as the application units  18 . Whatever valve system is used must ensure that the initiator is applied to the desired locations of the strip  2 . 
         [0067]    The application unit  18  does not have to receive its signals from the press controller  16 ; it can also have its signals supplied by another controller. 
         [0068]    In the case of several application units, it is also possible to adjust and/or control the latter from a joint controller  17 . 
         [0069]    The number of application heads  20  required for a lamination  5  depends on various factors, including the size of the lamination  5 , so that the stability of the lamination stack  6  is uniformly distributed in the entire composite, and its shape, so that the fixing points can be arranged as symmetrically as possible, so as to thereby achieve a sufficient adhesive force ( FIG. 6 ). One application head  20  then suffices. When larger surfaces  29  are to be wetted, for example, distinctly higher forces can be transmitted over this one surface than over smaller surfaces. Smaller surfaces  30  require more joining locations, and hence more application heads  20 , to achieve the same adhesive force ( FIG. 7 ). The application unit  18  essentially consists of the application head  20  and valve  19  ( FIG. 8 ), and is hooked up to the tool  13  via a support device  31 . It remains on the single tool  13 , and is designed to fix the application unit  18  in the right position for this tool. However, the application unit  18  itself can be detached from the support device  31 , and thus used with any other tool  13 . The application unit  18  can also be spaced apart from the tool  13  or situated in the tool  13 . 
         [0070]    As the band material  2  wetted with the initiator passes through, it may come into contact with the tool parts, such as the punch or guiding strips, since the present initiator, which in the exemplary embodiment consists of the derivatives imine and methacrylate ester, and is applied in minimal quantities, has no self-cross-linking effect and consists primarily of volatile substances. This is why contact with the initiator does not cause the band material  2  to get stuck. 
         [0071]    If the initiator is applied in liquid form over the entire surface of the band material before the tool, the initiator acts as a lubricating film on the punch and matrix, and therefore enables a distinctly longer service life for the punching tool, thereby increasing the total output and durability of this tool many times over. 
         [0072]    The lamination  5  is punched in a known manner in several steps with all required contours. In the last step, the lamination  5  is separated from the rest of the strip  2 . The adhesive is applied directly before this last section, in which the lamination  5  is only fixed to the strip  2  by a few narrow connecting webs  32  ( FIG. 9 ). The adhesive can be applied through roller coating, wherein the strip  2  is passed through an upper  33  and a lower  34  roller. The lower roller  34  is rubberized and wetted with adhesive. This wetting takes place according to  FIG. 11  in an adhesive bath  35 , in which the roller  34  dips. A third roller  36  with a minimal distance to the lower roller  34  is adjusted in such a way that the picked up adhesive  35  on the lower roller  34  is partially discharged again, thereby enabling the required layer thickness and a homogeneous distribution of the adhesive during roller coating. The rubberized roller  34  has a circumferential length corresponding to the feeding length of the tool  13 . The rubberized roller  34  has recessed areas  37 ,  37 ′ ( FIGS. 12 and 13 ) that would come into contact with the areas of the connecting webs  32  while rolling off. The recesses  37 ,  37 ′ cause these areas not to be wetted. As evident from  FIG. 9 , the length of the rollers  33 ,  34 ,  36  is greater than the width of the strips  2 , so that the adhesive can be applied to any location needed on the lower side of the laminations  5 . The recesses  37  are exemplarily provided near the two ends of the roller  34  at the same axial height ( FIG. 13 ). Recess  37 ′ lies at half the length of the roller  34 , and is situated diametrically opposite the recesses  37  as viewed in the axial direction of the roller  34  ( FIG. 12 ). The recesses  37 ,  37 ′ designed as depressions have a circular contour in the exemplary embodiment shown, but can also have another suitable contour depending on the type and/or shape of the areas of the lamination  5  not to be wetted with adhesive. 
         [0073]    During the last punching step ( FIG. 14 ), which involves separating the lamination  5  from the band material  2  at the connecting webs  32 , the detached lamination is downwardly pressed by a full-surface punch  38  into a matrix  39 , causing the adhesive  35  on the lower side of the lamination  5  to come into contact with the initiator  15  on the upper side of the previously separated lamination  5 . The contact between the initiator  15  and adhesive  35  triggers the cross-linking reaction, so that the laminations  5  lying on top of each other are rigidly joined together. The laminations  5  lying on top of each other are fixed in place first by the matrix  39  and later by a brake  40  until such time as the adhesive has reached a sufficient initial strength. 
         [0074]    The brake  40  is located in a hopper-like chamber  41 , in which the laminations  5  are put together to form stacks. The brake  40  ensures that the punched laminations do not descend through the hopper  41 . The configuration of the brake is known, and will thus only be briefly explained. For example, the brake can be comprised of partial rings, whose inner diameter is slightly smaller than the outer diameter of the punched laminations  5 . As a result, the laminations  5  are held in the hopper  41  by the brake  40 . After each punching process, the punch  38  presses the next lamination onto the lamination(s) present in the brake  40 . The braking force applied by the brake  40  is large enough to generate a contact pressure while pressing the respective next lamination  5  onto the already formed portion of the lamination stack that ensures a reliable adhesive bonding between the laminations  5  lying one on top of the other. The force exerted by the punch  38  is uniform over the entire lamination  5 . This ensures a balanced contact over all of the laminations, along with a high pressure that facilitates a uniform bond. The time available for curing depends on the number and thickness of the laminations  5 , the distance between the matrix  39  and the end of the brake  40 , and the number of strokes per minute. 
         [0075]    The longer the brake  40  is in the longitudinal direction of the hopper  41 , the longer the time for which the compressed laminations  5  are situated in the brake  40 . This provides more time for curing the adhesive at the same number of strokes per minute. 
         [0076]    When using the described example, there are several methods to ensure the desired length for the stack of laminations in this technology.  FIG. 15  describes one way in which the supply of initiator  15  to the strips  2  can be interrupted in fixed intervals. The laminations  5  provided with initiator are joined together to form a stack  42  in the hopper  41  ( FIG. 14 ). In this case, the supply of initiator  15  to the strip  2  is interrupted in fixed intervals. Laminations  43  whose upper side  28   a  exhibits no initiator  15  are generated in this way. The laminations joined without an initiator do not form adhesive bonds in the hopper  41  fast enough, if at all. As a consequence, the stack can be separated at this location. These laminations  43  not provided with initiator determine the height of the lamination stack  42 . Since every fourth lamination exhibits no initiator in the example, stacks  42  consisting of four laminations  5  situated one on top of the other are formed in the hopper  41 . At the instant the lamination  43  without initiator  15  is pressed onto the uppermost lamination  5  of the partial stack, the packet  42  has the desired height, and is later ejected from the hopper  41  in a known manner and fed to a transport device, which removes this stack. The next lamination stack  42  of four laminations  5  is now formed in the hopper  41 . As soon as the lamination  43  not provided with initiator is pressed onto this partial stack, the stack  42  again has the desired height, and is later ejected. The stack height can be very easily determined in this way. 
         [0077]    The laminations  43  not provided with initiator do not have to be punched out of the strip  2  at regular time intervals. The application of initiator can be controlled in such a way as to interrupt the supply of initiator at various time intervals. Accordingly, the number of laminations  43  in the stack  42  provided with initiator is greater in one case, and smaller in another. This makes it easy to adjust the height of the lamination stack  42 .