Abstract:
A standardized sample for scatterometry includes four quadrants each including an inner block surrounded by four outer blocks. A pattern of gratings is repeated within each of the blocks using different resolutions and orientations. Each grating within an outer block has a matching grating within the block&#39;s pair. A grating and its matching grating are negative images of each other—the pitch and line-size of a grating are equal, respectively to the line size and pitch of the matching grating. The inner block also includes a series of background patterns positioned behind the gratings. These patterns include repeating patterns of hole and repeating line structures. This series of structures cover a large die area, helping to simulate the conditions faced by real-world scatterometers. The various structures feature a high-degree of alignment, allowing rapid verification using SEM or other techniques.

Description:
PRIORITY CLAIM 
   The present application claims priority to U.S. Provisional Patent Applications Ser. No. 60/329,900, filed Oct. 16, 2001, Ser. No. 60/366,731, filed Mar. 22, 2002, and Ser. No. 60/342785 filed Dec. 21, 2001 all of which are incorporated herein by reference. 

   TECHNICAL FIELD 
   The subject invention relates to standardized samples used during the evaluation of scatterometers, reflectometers, ellipsometers and other optical metrology systems. 
   BACKGROUND OF THE INVENTION 
   As geometries continue to shrink, manufacturers have increasingly turned to optical techniques to perform non-destructive inspection and analysis of semi-conductor wafers. The basis for these techniques is the notion that a subject may be examined by analyzing the reflected energy that results when a probe beam is directed at the subject. Ellipsometry and reflectometry are two examples of commonly used optical techniques. For the specific case of ellipsometry, changes in the polarization state of the probe beam are analyzed. Reflectometry is similar, except that changes in magnitude are analyzed. Ellipsometry and reflectometry are effective methods for measuring a wide range of attributes including information about thickness, crystallinity, composition and refractive index. The structural details of ellipsometers are more fully described in U.S. Pat. Nos. 5,910,842 and 5,798,837 both of which are incorporated in this document by reference. 
   Scatterometry is a related technique that measures the diffraction (optical scattering) that results when a probe beam is directed at a subject. Scatterometry is an effective method for measuring the critical dimension (CD) of structural features (such as the lines and other structures included in integrated circuits). Scatterometry can be used to analyze periodic two-dimensional structures (e.g., line gratings) as well as periodic three-dimensional structures (e.g., patterns of vias or mesas in semiconductors). Scatterometry can also be used to perform overlay registration measurements. Overlay measurements attempt to measure the degree of alignment between successive lithographic mask layers. 
   As shown in  FIG. 1 , a typical scatterometer generates a probe beam using an illumination source. Depending on the type of scatterometer, the illumination source may be mono or polychromatic. The probe beam is directed at a subject to be analyzed. The subject includes a periodic structure such as a grating. The reflected probe beam is received by a detector. Once received, changes in reflectivity or polarization state of the probe beam are measured as a function of angle of incidence or wavelength (or both). These changes are used to analyze the subject. 
   Scatterometry may be used to analyze a wide range of different subjects. As shown in  FIG. 2 , a typical subject includes a periodic structure overlaying a background material. The background material is typically (for the case of semi-conductor wafers) a multilayer dielectric film. The periodic structure may be composed of one or more layers. For a typical analysis, a scatterometer may be used to measure a range of features of the periodic structure including line size, line spacing, line pitch, and line height. Line shape and side wall profiles may also be characterized. 
   The value of scatterometry systems is entirely dependent on their accuracy. Accuracy, in turn, is generally dependent on proper calibration of all involved systems. Unfortunately, proper scatterometer calibration is not entirely straightforward. In practice, calibration is often measured by comparing scatterometry results to the results obtained by an alternate method, such as a scanning electron microscope (SEM). This process is somewhat painstaking—requiring that test subjects be partitioned using a saw or other device to expose their critical features. Comparison to devices such as the SEM is also not without its own errors—there are cases where the scatterometer produces results that exceed the accuracy of the SEM. 
   In some cases, a specially prepared subject, known as a standardized sample is used to perform scatterometer calibration. Standardized samples have known features (often because they have been pre-measured using an atomic force microscope or other device). In theory, this allows scatterometers to be quickly and accurately calibrated by observing the result obtained during inspection of a standardized sample. In practice, this is not always the case. This is true largely because the standardized samples generally fail to provide adequate coverage of the features and conditions that are encountered during actual use of scatterometers in production environments. 
   For example, it is generally the case that the size of semi-conductor wafers continues to increase. Scatterometers and other inspection equipment must be calibrated to produce accurate measurements at all points within these increasingly large objects. This is true even where the optical components of the scatterometer are configured to remain stationary and the subject is moved to inspect different locations. Semi-conductor wafers also include a wide range of different structures at different orientations. A single wafer, for example, will typically include lines having different sizes, pitches and other important aspects. For optimal performance, each different structure must be accounted for during calibration. 
   Semi-conductor wafers (and other subjects) are produced using a wide range of layers, composed of a wide range of materials and arranged in a wide range of thicknesses and permutations. Since the accuracy of the scatterometry process may be influenced by these different configurations, it is important that they be accounted for during the calibration process. In practice, this is a particularly difficult part of the calibration process, since the range of possible configurations is nearly limitless. 
   To some extent, the dielectric properties of semi-conductor wafers tend to change over time. This is especially true for layers fabricated using organic materials. Exposure to light, especially in the UV range, causes chemical changes in the layers. The aging process also affects the standardized samples constructed to calibrate scatterometers and other optical metrology systems. This is problematic because the line/space features included in standardized samples are typically characterized at the time of their manufacture. Over time, the aging process causes the results to change introducing errors into the calibration process. 
   In production environments, calibration must also be accomplished quickly with minimal setup time. Calibration must also be performed under a range of different test conditions (such as varying temperature). 
   All of these factors contribute to the complexity of scatterometer calibration. And while some of them have been at least partially met by existing standardized sample solutions, no current standardized sample provides a comprehensive solution. For at least these reasons, there is a continuing need for better calibration techniques for scatterometers and related optical inspection systems. 
   SUMMARY OF THE INVENTION 
   The present invention includes a standardized sample for evaluation and calibration of scatterometry equipment. For a representative embodiment, the standardized sample has a square or rectangular shape that is conveniently described using X and Y Cartesian coordinates. Typically, the square shape of the standardized sample is subdivided into four quadrants. Each quadrant is further subdivided into five blocks—an inner block and four outer blocks. The four outer blocks are grouped into two pairs: a vertical pair and a horizontal pair. 
   Each outer block includes a series of gratings, each having a different pitch and line size. The gratings within the vertical pair of blocks are aligned vertically—with lines parallel to the y-axis. The gratings within the horizontal pair of blocks are aligned horizontally—with lines parallel to the x-axis. Each grating within an outer block has a matching grating within the block&#39;s pair. A grating and its matching grating are negative images of each other—the pitch and line-size of a grating are equal, respectively to the line size and pitch of the matching grating. 
   The inner block includes an additional series of gratings. The inner block also includes a series of background patterns positioned behind the gratings. These patterns include repeating patterns of hole and repeating line structures. 
   This series of structures cover a large die area, helping to simulate the conditions faced by real-world scatterometers. The various structures feature a high-degree of alignment, allowing rapid verification using SEM or other techniques. 
   The standardized sample is created by etching a multi-layer dielectric film stack. Preferably, the film stack is created to resist age and exposure related changes in dielectric properties. For a typical case, the stabilized film stack is created to mimic the dielectric properties of a production film stack. Effective layers are defined to replace the aging-prone layers of the production film stack. Each effective layer is an age resistant combination of one or more layers that mimics the dielectric response of an aging-prone layer in the production film stack. For organic anti-reflective coatings and organic photo resist materials, equivalent effective layers are often defined using inorganic materials (SiON and SiO 2 , respectively). The stabilized film stack is then created as a combination that includes the effective layers and replicates the age-resistant layers from the production film stack. The age resistant film stack is then etched to create the line/space features. Alternately, it is also possible to forego the etching process and use the age resistant film stack as a stabilized sample for calibration and testing of ellipsometers and reflectometers. 

   
     BRIEF DESCRIPTION OF THE DRAWINGS 
       FIG. 1  is a block diagram of a prior art scatterometer. 
       FIG. 2  is a block diagram of a prior art film stack shown as a generic scatterometry subject. 
       FIG. 3  is a block diagram of an embodiment of the standardized sample of the present invention. 
       FIG. 4  is a block diagram of a quadrant of the standardized sample of  FIG. 3 . 
       FIG. 5  is a block diagram showing the panels included in the quadrant of  FIG. 4 . 
       FIG. 6  is a block diagram showing the test regions included in the panels of  FIG. 5 . 
       FIG. 7  is a block diagram of the foreground pattern used within the test regions shown in  FIG. 6 . 
       FIG. 8  is a block diagram showing the foreground pattern of  FIG. 7  applied to the test regions shown in  FIG. 6 . 
       FIG. 9  is a block diagram showing a first background pattern for use within a subset of the panels shown in  FIG. 5 . 
       FIG. 10  is a block diagram showing a second background pattern for use within a subset of the panels shown in  FIG. 5 . 
       FIG. 11  is a block diagram of a first film stack suitable for creating the standardized sample of the present invention. 
       FIG. 12  is a block diagram of a second film stack suitable for creating the standardized sample of the present invention. 
       FIG. 13  is a block diagram showing the use of an effective medium to compensate for roughness created during the etching of the film stack of  FIG. 12 . 
       FIG. 14  is a block diagram of a third film stack suitable for creating the standardized sample of the present invention. 
       FIG. 15  is a block diagram of a fourth film stack suitable for creating the standardized sample of the present invention. 
       FIG. 16  is a block diagram of a fifth film stack suitable for creating the standardized sample of the present invention. 
       FIGS. 17   a  through  17   e  show simulated spectral responses for the film stack of  FIG. 16 . 
       FIG. 18  is a block diagram of an un-etched version of the film stack of  FIG. 16 . 
       FIGS. 19   a  through  19   d  show simulated spectral responses for the film stack of  FIG. 18 . 
       FIG. 20  is a block diagram of a sixth film stack suitable for creating the standardized sample of the present invention. 
       FIGS. 21   a  through  21   e  show simulated spectral responses for the film stack of  FIG. 20 . 
       FIG. 22  is a block diagram of an un-etched version of the film stack of  FIG. 20 . 
       FIGS. 23   a  through  23   d  show simulated spectral responses for the film stack of  FIG. 22 . 
       FIG. 24  is a block diagram of a seventh film stack suitable for creating the standardized sample of the present invention. 
       FIG. 25  is a block diagram of an un-etched version of the film stack of  FIG. 24 . 
   

   DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS 
   The present invention includes a standardized sample that may be used for evaluation and calibration of scatterometry equipment. As shown in  FIG. 3 , a representative embodiment of the standardized sample 300 has a square or rectangular shape that is conveniently described using X and Y Cartesian coordinates. Standardized sample 300 is typically subdivided into four equal-sized quadrants (labeled  1  through  4  in  FIG. 3 ). Each quadrant is a square 1.24 cm by 1.24 cm making the entire standardized sample 2.5 cm square. Each of these dimensions may be varied to suit the needs of particular applications. 
   Each quadrant is further subdivided into five blocks—an inner block and four outer blocks. In  FIG. 3 , the inner blocks are labeled by their quadrant number followed by the letter E ( 1 E,  2 E,  3 E and  4 E). The outer blocks are labeled with their quadrant number followed by one of the letters A through D (e.g.,  1 A or  3 B). 
   As shown more clearly in  FIG. 4 , the four outer blocks in each quadrant are grouped into two pairs: a vertically oriented pair including blocks A and C and a horizontally oriented pair including blocks B and D. For this particular example, the vertically oriented blocks (A and C) are 0.4 cm long in the X dimension and 0.8 cm long in the Y dimension. The horizontally oriented blocks (B and D) are 0.8 cm long in the X dimension and 0.4 cm long in the Y dimension. The inner block (E) is 0.4 cm by 0.4 cm. 
   Each quadrant is divided into a series of panels as shown in  FIG. 5 . The outer blocks A through D include six panels. The inner block E includes four panels. Each of these panels is further subdivided into a series of test regions. As shown in  FIG. 6 , each of the panels within the outer blocks A through D includes five test areas. This gives each outer block a total of thirty test regions. Each of the panels within the inner block E includes four test regions giving inner block E a total of sixteen test regions. 
   Each test regions includes the foreground pattern  700  shown in  FIG. 7 . The foreground pattern includes is a series of thirteen square gratings  702 . Each grating  702  has a different size. For the particular example shown this includes 25 μm, 30 μm, 35 μm, 40 μm, 45 μm, 50 μm, 55 μm, 60 μm, 70 μm, 80 μm, 100 μm, 120 μm, and 140 μm gratings  702 . The size of each grating is printed to the grating&#39;s left. For the example being described, the printing is 10 μm tall and is spaced 20 μm from the associated grating. The foreground pattern  700  also includes an alignment marker  704 . The alignment marker  704  is a 100 μm by 100 μm box that includes a pair of crossed, perpendicular lines.  FIG. 8  shows a representative implementation of a quadrant  302  with the foreground pattern  700  repeated in each test region. 
   The same pitch is used for each of the thirteen gratings  702  within a given test region. A single pitch is also used for each of the test regions included in a given panel. This means, for example that each of the gratings within the four test regions of the first panel of the inner block has a 1000 nm pitch. The pitches used within each panel (and each included test region and grating) are summarized in the following table: 
   
     
       
             
             
             
             
             
             
             
           
             
             
             
             
             
             
           
             
             
             
             
             
             
             
           
         
             
                 
                 
             
             
                 
               Panel 1 
               Panel 2 
               Panel 3 
               Panel 4 
               Panel 5 
               Panel 6 
             
             
                 
                 
             
           
           
             
                 
             
           
        
         
             
               1E 
               1000 nm 
                800 nm 
                700 nm 
                600 nm 
               N/A 
             
           
        
         
             
               2E 
                500 nm 
                400 nm 
                300 nm 
                200 nm 
                 
                 
             
             
               3E 
                500 nm 
                400 nm 
                300 nm 
                200 nm 
             
             
               4E 
               1000 nm 
                800 nm 
                700 nm 
                600 nm 
             
             
               1A 
               1500 nm 
               1400 nm 
               1200 nm 
               1000 nm 
               900 nm 
               800 nm 
             
             
               . . . 
             
             
               1D 
             
             
               2A 
               1500 nm 
               1400 nm 
               1200 nm 
               1000 nm 
               900 nm 
               800 nm 
             
             
               . . . 
             
             
               2D 
             
             
               3A 
                700 nm 
                600 nm 
                500 nm 
                400 nm 
               300 nm 
               200 nm 
             
             
               . . . 
             
             
               3D 
             
             
               4A 
                700 nm 
                600 nm 
                500 nm 
                400 nm 
               300 nm 
               200 nm 
             
             
               . . . 
             
             
               4D 
             
             
                 
             
           
        
       
     
   
   As shown in this table, a wide range of pitches are included starting at 200 nm and extending to 1500 nm. 
   As discussed, the same pitch is used for each grating within a given panel. The line size and line spacing is not, however, held constant within any panel. Instead, the panels are configured so that each test area has a different line space and line size. For the first panel of the inner block E this means that the test regions have line spaces of 1:1, 1:2, 1:3 and 1:5, respectively. The line spaces and line sizes used within each test region of each panel are summarized in the following table: 
   
     
       
             
             
             
             
             
             
           
             
             
             
             
             
             
           
         
             
                 
                 
             
             
                 
               Test 
               Test 
               Test 
               Test 
               Test 
             
             
                 
               Region 
               Region 
               Region 
               Region 
               Region 
             
             
                 
               1 
               2 
               3 
               4 
               5 
             
             
                 
                 
             
           
           
             
                 
             
           
        
         
             
               1B, 1C, 
               L:S = 1:1  
               L:S = 1:2 
               L:S = 1:3 
               L:S = 1:4  
               L:S = 1:5 
             
             
               2B, 2C 
             
             
               1A, 1D, 
               L:S = 5:1  
               L:S = 4:1 
               L:S = 3:1 
               L:S = 2:1  
               L:S = 1:1 
             
             
               2A, 2D 
             
             
               3B, 3C, 
               L:S = 1:6  
               L:S = 1:7 
               L:S = 1:8 
               L:S = 1:10 
               Film stack 
             
             
               4B, 4C 
             
             
               1A, 1D, 
               L:S = 10:1 
               L:S = 8:1 
               L:S = 7:1 
               L:S = 6:1  
               Film stack 
             
             
               2A, 2D 
             
             
               1E, 2E, 
               L:S = 1:1  
               L:S = 1:2 
               L:S = 1:3 
               L:S = 1:5  
               N/A 
             
             
               3E, 4E 
             
             
                 
             
           
        
       
     
   
   As shown in this table, blocks B and C (in all quadrants) may be described as light fields. In these blocks line sizes are greater than, or equal to line spacings. Blocks A and D (in all quadrants) are dark fields—line spacings are greater than, or equal to line sizes. This subdivision (of blocks into light and dark fields) splits the vertically oriented pair of blocks (A and C) into a conjugate pair including one light and one dark field. Each test region in either of these blocks (A or C) is a negative image of the same test region in the block&#39;s pair (A or C). In this context, negative image is meant to describe the situation where the line spacing a test region matches the line size of a second region (and the line size within the first test region matches the line spacing within the second). The horizontally oriented pair of blocks (B and D) is similarly split into a conjugate pair of one light and one dark field and test regions in either of these blocks (B or D) are negative images of the same test region in the block&#39;s pair (B or D). 
   As described, each test region includes the foreground pattern shown in  FIG. 7 . The panels within inner block E also include a background pattern. As shown in  FIG. 9 , the background pattern for the panels in inner blocks E 1  and E 3  is a 2 μm grid with a line width of 0.4 μm.  FIG. 10  shows the background pattern for inner blocks E 2  and E 4 . That background pattern is a grid of holes spaced at 1 μm. Each hole has a diameter of 0.2 μm. 
   Standardized sample  300  is created by etching the surface of a dielectric film to create foreground patterns  700 . Depending on the particular application, a wide range of different film stacks may be used for this purpose. One of these is labeled A in  FIG. 11 . As shown, film stack A includes a number of layers. The first (lowermost) of these (layer  0 ) is a Silicon substrate. The substrate is followed by a 100A Oxide layer (layer  1 ), a 500A Nitride layer (layer  2 ), and 4000A Oxide layer (layer  3 ). The etching process stops at the bottom of the uppermost layer (layer  3 ). Film stack A is intended to be easily etchable. The nitride layer (layer  2 ) provides a robust stop for the etching process (since it etches slowly). The 100A Oxide layer (layer  1 ) ensures that the Nitride layer (layer  2 ) is not deposited directly on the Silicon substrate (layer  0 ). 
   A second possible film stack is labeled B in  FIG. 12 . As shown, film stack B includes two layers. The first of these (layer  0 ) is a Silicon substrate. The substrate is followed by a 4000 A Oxide (layer  1 ). This combination (Ox/Si) is used to represent a dielectric etch. The etching process stops at the bottom of the uppermost layer (layer  1 ). Film stack B is intended to provide a simplified system for characterizing scatterometer performance. The use of two layers means that unnecessary variables and unknowns are eliminated. 
   In some cases, it is possible that the etching process used to create film stack B will extend beyond the bottom of the uppermost layer (layer  1 ).  FIG. 13  shows a film stack C that exhibits “roughing” of this type. To account for this, the scatterometry model used for film stack C is modified to include an effective medium at the bottom of the trenches formed during the etch process. 
     FIG. 14  shows a film stack D intended to model deep trenches. As shown, film stack D includes two layers. The first of these (layer  0 ) is a Silicon substrate. The substrate is followed by a 15000 A Oxide (layer  1 ). This combination (Ox/Si) is used to represent a dielectric etch. The etching process stops midway through the uppermost layer (layer  1 ). The use of a thick, partially etched layer makes film stack D an effective model for deep trenches. 
     FIG. 15  shows a film stack E that includes three layers. The first of these (layer  0 ) is a Silicon substrate. The substrate is followed by a 100 A Oxide layer (layer  1 ), and a 1500 A Nitride layer (layer  2 ). This combination (Nitride/Ox/Si) is used to represent Nitride/Ox/Si. The etching process stops midway through the substrate layer (layer  0 ). 
   Film stacks A, B, D and E are relatively simple and include a limited number of layers. To accurately model real-world samples, it is often necessary to include more layers. At the same time, it is generally desirable to avoid the tendency of many layer materials to age or change in response to exposure to light.  FIG. 16  shows a film stack F intended to address both of these objectives. Film stack F includes a total of five layers. The first of these (layer  0 ) is a Silicon substrate. The substrate is followed by a 20 A Oxide layer (layer  1 ), a 2000 A Poly-Si layer (layer  2 ), an inorganic ARC (SiOxNy) layer at 193/248 nm (layer  3 ) and a 3000 A oxide layer (layer  4 ). The etching process stops at the bottom of the uppermost layer (layer  4 ). Layer  4  is intended to provide an inorganic substitute for an organic Resist layer. The oxide used in this layer closely models the dielectric response of Resist and is stable over time and exposure to light. Layer  3  is, similarly intended to provide an inorganic and stable substitute for an organic ARC (anti-reflective coating). 
     FIG. 17   a  through  17   e  show simulated spectral response curves for film stack F. The first figure in this series ( FIG. 17   a ) shows the type of response that would be exhibited by film stack F during inspection by a reflectometer. Each of the following figures is similar, except that the responses correspond to inspection by spectral ellipsometer. In particular, these curves correspond to the response curve of a broadband rotating compensator ellipsometer (RCE) of the type disclosed in U.S. Pat. No. 5,877,859, incorporated herein by reference. In the case of  FIG. 17   b,  the DC signal generated by a spectral ellipsometer is shown.  FIGS. 17   c  and  17   d  show the sine of the two and four omega signals, respectively.  FIG. 17   e  shows the cosine of the four omega signal. 
     FIG. 18  shows an un-etched, or pre-etched version of film stack F. Un-etched portions of the film stack can be used to ascertain the dielectric properties of the film stack independently from the diffractive qualities of the gratings within the standardized sample. Un-etched portions (or entirely un-etched film stacks) may also be used for calibration of ellipsometers and reflectometers. 
     FIG. 19   a  through  19   d  show simulated spectral response curves for the un-etched version of film stack F. The first figure in this series ( FIG. 19   a ) shows the type of response that would be exhibited by the un-etched film stack F during inspection by a reflectometer. Each of the following figures is similar, except that the responses correspond to inspection by spectral ellipsometer (RCE). In the case of  FIG. 19   b,  the DC signal generated by an off-axis spectral ellipsometer is shown.  FIGS. 19   c  and  19   d  are calculations of the conventional ellipsometric parameters tan (psi) and cosine (delta) respectively. 
     FIG. 20  shows a second example of a film stack that is both stable and relatively complex. As shown, film stack G includes a total of four layers. The first of these (layer  0 ) is a Silicon substrate. The substrate is followed by a 20 A Oxide layer (layer  1 ), a 2000 A Poly-Si layer (layer  2 ), and an inorganic ARC (SiOxNy) layer at 193/248 nm (layer  3 ). The etching process stops at the bottom of the top two layers (layers  2  and  3 ). As described for film stack F, layer  3  is intended to provide an inorganic and stable substitute for an organic ARC (anti-reflective coating). 
     FIG. 21   a  through  21   e  show simulated spectral response curves for film stack G. The first figure in this series ( FIG. 21   a ) shows the type of response that would be exhibited by film stack G during inspection by a reflectometer. Each of the following figures is similar, except that the responses correspond to inspection by spectral ellipsometer (RCE). In the case of  FIG. 21   b,  the DC signal generated by a spectral ellipsometer is shown.  FIGS. 21   c  and  21   d  show the sine of the two and four omega signals, respectively.  FIG. 21   e  shows the cosine of the four omega signal. 
     FIG. 22  shows an un-etched, or pre-etched version of film stack G. Un-etched portions of the film stack can be used to ascertain the dielectric properties of the film stack independently from the diffractive qualities of the gratings within the standardized sample. Un-etched portions (or entirely un-etched film stacks) may also be used for calibration of ellipsometers and reflectometers. 
     FIG. 23   a  through  23   d  show simulated spectral response curves for the un-etched version of film stack G. The first figure in this series ( FIG. 23   a ) shows the type of response that would be exhibited by the un-etched film stack G during inspection by a reflectometer. Each of the following figures is similar, except that the responses correspond to inspection by spectral ellipsometer (RCE). In the case of  FIG. 23   b,  the DC signal generated by an off-axis spectral ellipsometer is shown.  FIGS. 23   c  and  23   d  show the calculation of tan (psi) and cos(delta) ellipsometric parameters. 
     FIG. 24  shows a third example of a stable film stack. As shown, film stack H includes a total of three layers. The first of these (layer  0 ) is a Silicon substrate. The substrate is followed by a 20 A Oxide layer (layer  1 ), and a 2000 A Poly-Si layer (layer  2 ). This combination (Poly-Si/Ox/Si) is used to represent Poly/Ox/Si. The etching process stops at the bottom of the uppermost layer (layer  2 ). 
     FIG. 25  shows an un-etched, or pre-etched version of film stack H. Un-etched portions of the film stack can be used to ascertain the dielectric properties of the film stack independently from the diffractive qualities of the gratings within the standardized sample. Un-etched portions (or entirely un-etched film stacks) may also be used for calibration of ellipsometers and reflectometers. 
   Film stacks F, G and H are examples of a more generalized method for creating stabilized reference film stacks for use in standardized samples and other test samples. Stabilized reference film stacks mimic the dielectric properties of production film stacks without having the tendency to age or change dielectric response when exposed to optical radiation. To create a stabilized reference film stack, the layers within a production film stack are subdivided into two categories. First category layers are the layers that tend to age or change optical response when exposed to optical radiation (chiefly UV radiation). Typically, organic anti-reflective coatings, and organic photo-resistive layers are sensitive to UV radiation and are placed in the first category. Second category layers are the layers within the production film stack that are relatively impervious to aging. Inorganic layers are commonly included in this category. 
   An effective layer is then defined for each layer included in the first category. Each effective layer is designed to mimic, as closely as possible, the optical response that is exhibited by the corresponding layer in the first category. At the same time, the materials used for the effective layers are selected to be relatively impervious to aging. Each effective layer may include one or more materials in one or more layers. The use of multiple materials and layers is required when the desired combination of optical response and age-resistance is not available or practical using a single material. In general, it should be appreciated that the process of defining effective layers is not perfect and that it is generally not possible to exactly match the dielectric response of the layers in the first category using substitute materials. At the same time it is generally possible to closely approximate the response of first category layers while greatly decreasingly the tendency for the resulting layers to age. 
   In many cases, the effective layers are selected by substituting an inorganic compound for an aging-prone organic compound. This is particularly true for organic anti-reflective coatings and organic photo resist materials. The effective layers defined for organic anti-reflective coatings are typically fabricated using silicon oxide nitride (SiON). The effective layers for organic photo resist layers are typically fabricated using silicon dioxide (SiO 2 ). 
   The following tables list organic photo-resist materials and organic anti-reflective coatings for which replacement by inorganic materials may be appropriate: 
   
     
       
             
             
           
         
             
                 
             
             
               Photo resist materials 
               Manufacturer 
             
             
                 
             
           
           
             
               APEX-E ™ 
               Shipley Company 
             
             
               UVIIHS ™, UVIII ™ 
             
             
               UV ™ 82, UV ™ 86, UV ™ 110, UV ™ 113, 
             
             
               UV ™ 135, UV ™ 210 
             
             
               EPIC ™-S7 
             
             
               ULTRA-I 123 
             
             
               AZ ® EXP 5888, 5690S, 5200P, 5400P 
               AZ Electronic Materia 
             
             
               AZ ® DTF ™ 11 
             
             
               PFR ® IX1060G, PFR ® IX1010G 
               JSR Microelectronics 
             
             
               EIRIS, KRF, ARF series 
             
             
               TDMR, TDQR-IQ, TDUR-P/N series 
               TOKYO OHKA 
             
             
                 
               KOGYO Co., LTD 
             
             
               Sumiresist series 
               Sumitomo Chemical 
             
             
                 
             
           
        
       
     
   
   
     
       
             
             
             
           
         
             
                 
                 
             
             
                 
               Anti-reflective coatings 
               Manufacturer 
             
             
                 
                 
             
           
           
             
                 
               AR ™2, AR ™3, AR ™8 
               Shipley Company 
             
             
                 
               AR ™5, AR ™6, AR ™7, AR ™10 
             
             
                 
               AZ BARLi ® Series 
               AZ Electronic Materia 
             
             
                 
               AZ EXP HERB ™ 
             
             
                 
               AZ KrF 3G, AZ KrF 17B 
             
             
                 
               AZ EXP KrF 17G-2 
             
             
                 
               AZ EXP ArF-1C, ArF-2C, ArF-2P 
             
             
                 
               NFC 540 
               JSR Microelectronics 
             
             
                 
                 
             
           
        
       
     
   
   Once effective layers have been defined, the stabilized film stack may be constructed as a combination that includes the effective layers and replicates the layers from the second category. The overall result mimics the dielectric response of the production film stack without having the tendency to change over time. In general, it should be appreciated that the use of the term “production” is not intended to be limiting. This same method may be used to create stabilized reference film stacks that model the optical response of prototype or proposed film stacks.