Abstract:
A solar PV panel has an array of primary mirrors that collects and reflects solar radiation toward an array of dichroic secondary elements. The dichroic secondary elements reflect near-visible solar radiation to an array of near-visible radiation sensitive solar cells and simultaneously transmit infrared radiation to an array of infrared sensitive solar cells. The array of near-visible radiation sensitive cells and the array of infrared sensitive cells are wired in series. The optical properties of the dichoic secondary element, near-visible radiation sensitive cell, and IR sensitive cell are chosen for simultaneous maximum power production from the panel.

Description:
This application claims the benefit of U.S. Provisional Application No. 60/775,715 filed Feb. 23, 2006, which is hereby incorporated by reference in its entirety. 
    
    
     BACKGROUND OF THE INVENTION 
     Various types of multijunction solar cells have now been demonstrated with energy conversion efficiencies over 35%. Several prior art configurations are shown in  FIGS. 1 ,  2 ,  3 , and  4 . 
       FIG. 1  shows GaAs light sensitive cells and GaSb IR sensitive cells mechanically-stacked in a triplet circuit in a voltage-matched configuration in a concentrator module with Fresnel lenses focusing the solar energy onto the cells. This is a cell configuration with 2 junctions in 2 different materials. A lens parquet  1  overlays a circuit  7  on a heat spreading back plate, on which top light sensitive cells  3  and bottom IR sensitive cells  5  are placed. 
       FIG. 2  shows a 2-junction monolithic InGaP/GaInAs cell mechanically-stacked on a separate GaSb cell. There are 3 junctions in 3 different materials. No circuit wiring is suggested for this ease. A prismatic cover with double AR coatings  9  cover the InGaP/GaInAs cell and a prismatic cover with single AR coating  15  covers the GaSb cell. Double AR coatings  11  and isolation  13  separate the two cells. 
       FIG. 3  shows a Cassegrain module with voltage-matched InGaP/GaAs  21  and GaSb  19  cells. This Cassegrainian PV module concept uses a dichroic hyperbolic secondary mirror to split the incoming light  17  spectrum into short and long wavelength bands to create two focal points. There are 3 junctions in 3 separate materials. The module is 33% efficient. 
       FIG. 4  shows a very popular InGaP/GaInAs/Ge monolithic 3-junction cell that has been developed for light-weight for satellite power systems with positive contact  23  and negative contact  25 . 
     It is very desirable to integrate these high efficiency multijuction cell concepts with optics where the circuits are simple to fabricate and the resultant solar panels are inexpensive and produce maximum power with maximum energy conversion efficiency. However, problems with the prior art configurations have prevented such a product from being realized. 
     In the mechanically stacked configurations shown in  FIGS. 1 &amp; 2 , the metal grids on the top and the bottom of the top cell produce shading losses for the IR bottom cell. Furthermore the top cell substrate can absorb substantial IR energy before it arrives at the IR cell for conversion. These reflection and absorption losses decrease the energy conversion efficiency. Furthermore, the grid on the back of the top cell adds complexity and cost. 
     Another problem for the configurations shown in  FIGS. 1 and 3  as described in the prior art is a problem with high currents in the voltage-matched configuration. For example if in the  FIG. 1  case, the GaAs cells each produce 10 Amps and the GaSb circuit produces 8 Amps, the voltage matched triplet will produce 38 Amps at 1 Volt. 
     There are also several problems with the InGaP/GaInAs/Ge monolithic cell shown in  FIG. 4  when it is brought down from space for terrestrial applications. While it is light-weight for space, this is not important for terrestrial applications. There are really three problems that relate to the germanium cell. 
     The first problem with the germanium cell is that it produces excess current that can not be used.  FIG. 5  shows the current available from the terrestrial spectrum as a function of the longest wavelength that a given semiconductor can receive. It follows from this curve that the most current available to an InGaP cell lattice matched to germanium will be about 17.5 mA/cm2 with a similar amount of current available to a lattice matched GaInAs cell. Meanwhile, the current available to the germanium cell is much larger at about 28 mA/cm2. Because of the monolithic series connection in this cell, the excess germanium cell current is wasted resulting in a lower than optimal conversion efficiency. 
     The second problem with the germanium cell is a lower than optimal voltage. Given the terrestrial spectrum, the bandgap of germanium is just too low. While it can theoretically absorb out to 1.9 microns, there are just no photons in the terrestrial spectrum beyond about 1.8 microns. 
     The third problem with germanium is that its open circuit voltage in practice is just not as good as it should be theoretically.  FIG. 6  shows the open circuit voltage of materials having a variety of bandgaps, compared to the radiative limit. A Ge cell has a voltage of only 0.2 V whereas a GaSb cell (not shown) can produce 0.5 V. 
     Needs exist for improved simple solar concentrator panels with series connected cells with different compositions with all cells operating at their maximum power such that said panel operates at its maximum efficiency. 
     SUMMARY OF THE INVENTION 
     A new solar PV panel has an array of primary mirrors that collect and reflect solar radiation toward an array of dichroic secondary elements. The dichroic secondary elements reflect near-visible solar radiation to an array of near-visible radiation sensitive solar cells and simultaneously transmit infrared radiation to an array of infrared sensitive solar cells. The array of near-visible radiation sensitive cells and the array of infrared sensitive cells are all wired in series. The optical properties of the dichoic secondary element and the near-visible radiation sensitive cell and the IR sensitive cell ensure simultaneous maximum power production from the panel. 
     In a preferred embodiment, the infrared sensitive cell is a GaSb cell and the near-visible radiation sensitive cell is a GaAs 1-x P x  cell and the dichroic secondary element transition wavelength is chosen to fall at the GaAs 1-x P x  cell bandedge. 
     The phosphorus content, x, in the GaAs 1-x P x  cell falls between 1% and 9%, nominally 5%, and the dichroic filter transition wavelength is at approximately 0.8 microns. 
     In another embodiment, the infrared sensitive cell is a GaSb cell and the near visible radiation sensitive cell is an In 1-z Ga z P/Ga 1-y In y As dual junction cell and the dichroic secondary element transition wavelength is chosen to fall at the Ga 1-y In y As cell band edge. The Indium content, y, in the In 1-z Ga z P/Ga 1-y In y As dual junction cell falls between 5% and 15%, nominally 10%, the gallium content, z, falls between 35% and 45%, nominally 40%, and the dichroic filter transition wavelength is at approximately 1 microns. 
     In a preferred embodiment, a GaSb cell is the infrared sensitive cell and its short circuit current is greater than that for the chosen near-visible light sensitive cell so that as the two cell arrays are series connected, all cells operate simultaneously at their individual maximum power points. 
    
    
     
       BRIEF DESCRIPTION OF THE DRAWINGS 
         FIG. 1  is a diagram of a prior art concentrator module with GaAs light sensitive cells stacked on GaSb IR sensitive cells in triplet voltage matched configuration. 
         FIG. 2  is a diagram of a prior art GaInP/GaInAs—GaSb mechanical stack cell configuration. 
         FIG. 3  is a diagram of a prior art Cassegrain module with voltage-matched InGaP/GaAs—GaSb cells. 
         FIG. 4  is a diagram of a prior art series connected monolithic triple junction cell. 
         FIG. 5  is a graph showing the current available from the terrestrial spectrum as a function of the longest wavelength that a given semiconductor can absorb. 
         FIG. 6  is a graph showing the open circuit voltage of materials having a variety of bandgaps, compared to the radiative limit. 
         FIG. 7  is a diagram of a concentrator panel with series connected IR and light sensitive cell strings. 
         FIG. 8  is a diagram of a Cassegrain PV module and key components. 
         FIG. 9  is a close-up diagram of the cells in the Cassegrain PV module of  FIG. 8 . 
         FIG. 10  is a diagram of a GaSb IR cell formed by diffusion. 
         FIG. 11  is a diagram of a GaSb IR cell formed by epitaxy. 
         FIG. 12  is a diagram of a GaAs light sensitive cell with phosphorus for connecting with a GaSb IR cell. 
         FIG. 13  is a plot of internal quantum efficiency versus wavelength for GaInAs single-junction solar cells with various bandgaps. 
         FIG. 14  is a diagram of a monolithic InGaP/GaInAs dual junction light sensitive cell. 
     
    
    
     DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS 
       FIG. 7  illustrates a Cassegrain concentrator PV panel with series connected IR and light sensitive cell strings. The panel  100  in this invention consists of any number of Cassegrainian modules  101  where all cells  103  in the panel are series connected and the cell compositions are chosen such that all of the different cells operate at their maximum power points. Wire series  27  connects the IR cells, wire series  29  and  31  connect the IR cell string and light sensitive cell string, and wire series  33  connects the light sensitive cells. Wire series  29  and  33  connect to the panel electric power terminals  35 .  FIGS. 8 and 9  show the details of the Cassegrainian modules  101  making up the panel  100 . 
       FIG. 8  shows the key components in a Cassegrainian PV module  101 . Infrared radiation is conveyed to the IR cell  39  by the primary mirror  47  through the dichroic secondary cold mirror  43 , set in glass window  41 . The IR cell is backed by an IR cell heat sink  37 . A homogenizer  45  conveys near-visible light to the near-visible light sensitive cell  49  from the light source and dichroic secondary mirror  43 . The near-visible light sensitive cell is mounted on a back mounting plate  51  and has a heat sink  53 . 
       FIG. 9  highlights the two cells, IR cell  105  and near-visible cell  107 , whose compositions need to be optimized for operation together at their respective maximum power points when connected in series. A key feature of this invention is to specify the cell compositions required for maximum panel efficiency. These required compositions are derived by reference to  FIG. 5 . The resultant compositions are summarized in Table 1 below for two panel embodiments. A first simpler panel embodiment uses 2 junctions in two different materials and a second more efficient panel embodiment uses 3 junctions in three different materials. The table shows cells and performance predictions for series connected 2J and 3J configurations. 
     
       
         
               
               
               
               
               
               
               
               
               
             
               
               
               
               
               
               
               
               
               
             
           
               
                   
               
               
                   
                   
                 AM1.5 1sun 
                 Cut-on 
                   
                   
                 Practical 
                   
                 Practical 
               
               
                 Cell  
                 Current 
                 Theory Jsc 
                 Wavelength 
                 Eg 
                 Voc 
                 Jsc 
                 Practical 
                 Target 
               
               
                 Composition 
                 Partition 
                 (mA/cm2) 
                 (microns) 
                 (eV) 
                 (V) 
                 (mA/cm2) 
                 FF 
                 Efficiency 
               
               
                   
               
             
             
               
                   
               
             
          
           
               
                 Series 2J Panel 
                   
                   
                   
                   
                   
                   
                   
                   
               
               
                 GaAs(0.95)P(0.05) 
                 45% 
                 27.9 
                 0.82 
                 1.5 
                 1.2 
                 23.8 
                 0.85 
                 24.3% 
               
               
                 GaSb 
                 55% 
                 34.1 
                 1.77 
                 0.7 
                 0.5 
                 29.1 
                 0.8 
                 11.5% 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 35.8% 
               
               
                 Series 3J Panel 
                   
                   
                   
                   
                   
                   
                   
                   
               
               
                 In(0.6)Ga(0.4)P 
                 30% 
                 18.6 
                 0.73 
                 1.7 
                 1.4 
                 15.9 
                 0.88 
                 19.6% 
               
               
                 Ga(0.9)In(0.1)As 
                 30% 
                 18.6 
                 0.99 
                 1.25 
                 0.95 
                 15.9 
                 0.85 
                 12.8% 
               
               
                 GaSb 
                 40% 
                 24.8 
                 1.77 
                 0.7 
                 0.5 
                 21.2 
                 0.8 
                 8.5% 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 40.9% 
               
               
                   
               
             
          
         
       
     
     The cell compositions were selected such that all cells operate at their maximum power points when series connected. When different cells are operated in series, they will all operate at the same current. As a first approximation, this means that each cell of each different composition should be operated at its maximum power current. However, variations in humidity will result in variations in the amount of IR arriving at the IR cell. To allow for this, the compositions of the different cells are chosen such that the IR cell operates with a small amount of excess current. 
     A GaSb cell is used as the IR cell because it is simple to make and has a bandgap at the right energy to absorb all of the photons available out to 1.8 microns. Beyond 1.8 microns, water vapor absorption eliminates IR photons leading to the plateau at 62 mA/cm2 in  FIG. 5 . Given the choice of GaSb as the IR material, the cells can be made either by diffusion or by epitaxy. 
       FIGS. 10 and 11  show GaSb IR cell configurations made by diffusion and by epitaxy, respectively. In  FIG. 10 , a top metal grid  59  and AR coating  61  are layered on a GaSb diffused junction cell  63  with a back metal contact  67  on an alumina circuit plate  65 . In  FIG. 11 , a top metal grid  69  and AR coating  71  over an AlGaSb window layer  73  cover GaSb P &amp; N epitaxy layers  75  on a GaSb crystal substrate  77  with a back metal contact  79  mounted on an alumina circuit plate  81 . 
     The simple GaAs cell from  FIG. 1  is not optimal for the top cell in a 2 junction panel as its available 1-sun short circuit current is too high at 34 mA/cm2 leaving only 28 mA/cm2 for the GaSb cell, as can be seen in  FIG. 5 . If GaAs and GaSb cells were wired in series, the GaSb cell would limit the current for the two cells and the resultant circuit would operate at a much lower efficiency than the sum efficiency possible if the two cells were operated independently. The solution to this problem is to add a small amount of phosphorus (P) to the GaAs to form GaAs(1−x)P(x), raising the near-visible light sensitive cell&#39;s′bandgap. The P content is approximately 5% with an x&gt;0 and &lt;10%. 
       FIG. 12  shows the resultant GaAs 1-x P x  cell  111  for connection with a GaSb IR cell. Such a combination yields maximum power and efficiency of operation. A top metal grid  83  and AR coating  85  on AlInP window layer  87  cover GaAs 0.95 P 0.05  P &amp; N epitaxy layers  89  over transition layer  91  on GaAs crystal substrate  93  with back metal contact  95  against alumina circuit plate  97 . 
     As can be seen from Table 1, the GaAs 0.95 P 0.05  cell&#39;s bandgap corresponds to a threshold wavelength for absorption at, approximately 0.82 microns, decreasing its potential short circuit current to approximately 28 mA/cm2. The transition wavelength below which the dichroic filter reflects and above which it transmits is chosen to be at approximately a corresponding 0.82 microns, resulting in the short circuit current available to the GaSb IR cell increasing to approximately 34 mA/cm2. Because the fill factor for a low bandgap cell is always less than for a high bandgap cell and there must be an allowance for a margin in humidity variations, these compositions allow both GaAs 0.95 P 0.05  and GaSb cells to operate simultaneously at near their respective maximum power points, maximizing the power output and efficiency for the panel. The amount of phosphorus addition is sufficient to match cell maximum power points but is small enough to keep crystal lattice constants similar enough to maintain good crystal quality in the GaAs 0.95 P 0.05  cell. 
     As shown in table 1, this combination of cells should allow a combined series-circuit solar energy conversion efficiency of over 35%. 
     A second panel embodiment has 3 different junctions with three different cell materials series connected. The three appropriate cell materials used in the panel of this invention are also described in table 1. An In 1-z Ga z P/Ga 1-y In y As dual junction cell is used as the near visible radiation sensitive cell. 
     For this second panel embodiment, the material compositions must again be adjusted such that all 3 junctions operate simultaneously at their maximum power points when all junctions are series connected. A 62 mA/cm2 current is available out to the band edge of a GaSb cell. Rather than dividing this current by three for the three junctions, 40% is allocated to the GaSb low band gap cell to give it more short circuit current, with 30% to each of the In 1-z Ga z P and Ga 1-y In y As junction materials. Given that the band gap of Ga 1-y In y As can be adjusted downward with more indium content as shown in  FIG. 13 , an appropriate indium content y is selected from the nature of terrestrial sunlight given in  FIG. 5 . Good quality Ga 1-y In y As cells can now be made. 
     As shown in table 1, the indium content, y, is selected to be about 10% or in the range between 5% and 15%. The gallium content, z, in the In 1-z Ga z P is selected to be about 40% or between 35% and 45%, such that the crystal lattices of In 1-z Ga z P and Ga 1-y In y As match. 
       FIG. 14  shows the monolithic dual junction cell to be used in series with GaSb cells in this second embodiment, high efficiency Cassegrain panel. Top metal grid  201  and AR coating  203  on AlInP window layer  205  cover a sandwich of In 0.6 Ga 0.4 P P &amp; N epitaxy layers  207 , Ga 0.9 In 0.1 As P &amp; N epitaxy layers  211 , and GaAs crystal substrate  215  separated by P+ and N+ tunnel junction  209  and transition layers  213  on back metal plate  217  against alumina circuit plate  219 . 
     Referring to Table 1, the dichroic filter transmission to reflection transition wavelength is 0.99 microns (approximately 1 micron) so that wavelengths shorter than 1 micron are reflected to the In 0.6 Ga 0.4 P/Ga 0.9 In 0.1 As cell and wavelengths longer than 1 micron are transmitted to the IR GaSb cell. 
     As table 1 shows, these material choices allow all 3 junctions to be operated simultaneously at their maximum power and efficiency points, yielding a combined practical solar conversion efficiency over 40%. 
     The panel embodiments described in this invention have several advantages over prior art solar panels. Referring specifically to the series connected In 0.6 Ga 0.4 P/Ga 0.9 In 0.1 As—GaSb Cassegrain panel cell group in comparison to the Monolithic In 0.5 Ga 0.5 P/GaAs/Ge series connected cell, the GaSb cell beats the Ge cell with a better voltage by 0.3 V. The theoretical limit efficiency for the InGaP/GaInAs—GaSb combination is 59.5% with a 40% practical module efficiency possible, both values again substantially better than for the prior art. 
     An additional advantage for the InGaP/GaInAs—GaSb combination in the Cassegrainian configuration is the division of the solar radiation heat load into two separate locations with a very manageable heat load at the IR cell location. This will result in lower cell operating temperatures and still higher practical panel efficiency relative to a panel with a monolithic InGaP/GaInAs/Ge cell.