Abstract:
Provided is a cathode material which becomes an alternative material of a cathode material formed of a W—ThO 2  alloy and is formed of a tungsten alloy that does not include thorium which is a radioactive element. When particles of a rare earth oxide and tungsten carbide are finely dispersed in a tungsten cathode material used as a discharge cathode material used in TIG, plasma spraying, plasma cutting, electrical discharge machining, discharge lamps and the like, reduction and diffusion of the rare earth oxide are accelerated, and supply of rare earth elements to a cathode surface is ensured, thereby improving discharge characteristics.

Description:
TECHNICAL FIELD 
       [0001]    The present invention relates to a tungsten material effectively applied to cathode materials used mainly in TIG for low-current operation, plasma spraying, plasma cutting, electrical discharge machining, discharge lamps and the like. 
       BACKGROUND ART 
       [0002]    Tungsten is a metal having a highest melting point and a relatively favorable electrical conductivity, and is thus widely used as electrode materials requiring heat resistance. However, in a case in which tungsten is used as a cathode, a substance having a low work function is frequently added in order to improve thermoelectron emission characteristics. Among the above substances, ThO 2  had a high melting point and a high boiling point, and also had a relatively low work function, and therefore a W—ThO 2  alloy having ThO 2  dispersed in tungsten has been used as an excellent cathode material (refer to Patent Documents 1 to 3). 
         [0003]    Patent Document 1 discloses a tungsten alloy to which oxides of Pr, Nd, Sm and Gd are added. However, data disclosed in Patent Document 1 is a test result of a short period of time of 100 minutes, and it has been impossible to practically obtain an alloy having characteristics stabilized for a long period of time. 
         [0004]    In addition, as described in Patent Document 2, in the case of the W—ThO 2  alloy, acceleration of reduction of Th by providing a char layer on a surface is widely carried out. However, since Th is a radioactive element, there is a tendency of avoiding use of Th, and thus there is an expectation for materials having equal or superior characteristics to the characteristics of the W—ThO 2  alloy of the related art. Even in alloys to which oxides other than ThO 2  are added, certain effects can be obtained by providing a char layer in the same manner, but the effects are not sufficient. 
         [0005]    Meanwhile, there is another example in which a carbide is added to the alloy as described in Patent Document 3; however, in this case, the carbide plays a role of electron emission, and reduction of an oxide is not taken into account. 
       CITATION LIST 
       [0006]    Patent Documents
   Patent Document 1: Japanese Patent Publication Laid-open No. 05-054854   Patent Document 2: Japanese Patent Publication Laid-open No. 04-137349   Patent Document 3: Japanese Patent Publication Laid-open No. 05-067451   
 
       SUMMARY OF INVENTION 
     Technical Problem 
       [0010]    Therefore, the invention is to provide a cathode material which becomes an alternative material of a cathode material formed of a W—ThO 2  alloy and is formed of a tungsten alloy not including thorium which is a radioactive element. 
       Solution to Problem 
       [0011]    It is considered that, in a tungsten cathode material of the related art to which a rare earth oxide was added, since the oxide had a lower boiling point than ThO 2 , the oxide was rapidly evaporated from an electrode surface, not supplied in a timely manner by diffusion, and, consequently, a long service life could not be obtained. As means for accelerating diffusion, conversion of the oxide into a sole metallic atom by reduction can be considered, and it is considered to be more effective to convert the oxide inside the alloy instead of on the electrode surface. Although there are documents describing that the added oxide is reduced by tungsten metal, a free energy change AG of a reaction of, for example, the following formula is positive, and the reaction is not easily caused thermodynamically. 
         [0000]      Nd 2 O 2 +3W=2Nd+3WO 2    
         [0012]    Meanwhile, regarding a reaction of the following formula, it is considered that, when a temperature exceeds approximately 1800° C., ΔG becomes negative, and the reaction easily proceeds. Herein, since the thermodynamic data only includes WC, the carbide is assumed to be WC; however, in an actual tungsten alloy, the carbide forms W 2 C as illustrated in an optical microscopic photograph of  FIG. 1 , and therefore a reaction temperature may include an error, but there is no change in the fundamental idea. 
         [0000]      Nd 2 O 3 +3WC=2Nd+3W+3CO 
         [0013]    When the reaction is rapidly caused in the alloy, Nd is continuously supplied to a surface by diffusion, and discharge characteristics are improved. In order to do so, it is necessary to uniformly and finely disperse a rare earth oxide and a tungsten carbide in the alloy. 
         [0014]    In addition, it is also conceivable to use a carbide of non-tungsten; however, when a carbide having a high melting point, for example, TiC, is used, since an increase in the reaction temperature or an adverse influence of generated Ti should also be considered, tungsten carbide is desirable. 
         [0015]    In addition, regarding impurities other than tungsten, carbon and the rare earth oxide in a sintered compact, characteristics are not influenced as long as a total content of the included impurities, such as Fe, Mo, Al and Si, is 500 ppm or less (mass fraction). In addition, regarding K as well, no influence is observed in an alloy which includes 500 ppm of K (mass fraction). 
         [0016]    An invention according to claim  1  is a cathode material formed of a tungsten alloy which does not include Th and has at least a carbide and a rare earth oxide dispersed therein. Since a rare earth element has a high melting point and a high boiling point, and also has a relatively low work function, the rare earth element is present on a tungsten cathode surface, whereby the cathode material exhibits superior discharge characteristics. In addition, the carbide diffuses carbon in tungsten at a lamp operation temperature, reduces the rare earth oxide, and assists the diffusion of the rare earth element onto the electrode surface. Therefore, excellent discharge characteristics are exhibited by diffusing both the carbide and the rare earth oxide in tungsten. 
         [0017]    An invention according to claim  2  is the cathode material according to claim  1  in which the carbide and the rare earth oxide are dispersed throughout the entire tungsten alloy. The carbide and the rare earth oxide are preferably finely dispersed throughout the entire tungsten alloy. When carbon is diffused only onto, for example, the surface and a vicinity of the surface as described in Patent Document 1, the rare earth oxide is not stably and rapidly supplied to the surface. 
         [0018]    An invention according to claim  3  is the cathode material according to claim  1  or  2  in which an amount of carbon in the tungsten alloy is 10 ppm to 1000 ppm by mass fraction. Carbon is present in the sintered compact in a form of a carbide of tungsten or other components, and an amount thereof is most suitably 10 ppm to 1000 ppm. When the amount is less than 10 ppm, the effect of addition is rarely observed. In addition, a maximum solid solution amount of carbon in tungsten is approximately 1000 ppm, and, when carbon is present in an amount exceeding the maximum solid solution amount, adverse influences, such as dissolution of the tungsten alloy while sintered and while used or an increase in an amount of carbon evaporated from a cathode, are caused. 
         [0019]    An invention according to claim  4  is the cathode material according to any one of claims  1  to  3  in which the carbide in the tungsten alloy includes tungsten carbide. The carbide in tungsten is particularly suitably tungsten carbide. When the carbide is tungsten carbide, tungsten carbide is sufficiently decomposed at an operation temperature of an electrode so as to emit carbon. In addition, since tungsten carbide does not include other metallic elements, an adverse influence on discharge, such as evaporation, is not easily caused. At this time, tungsten carbide refers to WC or W 2 C, but it is confirmed that tungsten carbide forms W 2 C in an equilibrium state. 
         [0020]    An invention according to claim  5  is the electrode material according to any one of claims  1  to  4  in which a total amount of the rare earth oxide with respect to the tungsten alloy is 0.2 mass % to 10 mass %. The rare earth element refers to a lanthanoid element, an actinoid element or yttrium. When a content of the rare earth oxide is less than 0.2 mass %, an effect for significantly improving discharge characteristics is not observed. Theoretically, tungsten alloy may contain a certain amount of the rare earth oxide; however, in actual manufacturing of the cathode material, in a case in which more than 10 mass % of the rare earth oxide is added, cracking occurs in a sintering step, and manufacturing becomes significantly difficult. 
         [0021]    An invention according to claim  6  is the electrode material according to any one of claims  1  to  5  in which half or more of particles of the rare earth oxide by mass are oxides of one or two or more of Sm, Nd, Gd and La. Among oxides of rare earth elements, particularly, the oxides of Sm, Nd, Gd and La have a high melting point, a high boiling point and a low work function, and therefore the oxides are suitable for improving discharge characteristics. 
         [0022]    An invention according to claim  7  is the cathode material according to any one of claims  1  to  6  in which an average particle diameter of the particles of the rare earth oxide is 0.1 μm to 2.5 μm. This is because, when the average particle diameter of the particles of the rare earth oxide is finely dispersed, a surface area of the particles becomes large, and gaps between the particles are narrowed, whereby diffusion of both the carbide and the rare earth oxide becomes easier. It is considered that discharge characteristics are favorable when the particles are fine as described above, and the following examples indicate that the average particle diameter is desirably 2.5 μm or less. When the average particle diameter is small, there is no problem with discharge characteristics; however, when the average particle diameter is below 0.1 μm, manufacturing of powder of the oxide is difficult, and the costs become high while the effects are the same. 
         [0023]    An invention according to claim  8  is a cathode formed of the cathode material according to any one of claims  1  to  7 . When the above material is used, the cathode exhibits favorable characteristics as a cathode used in TIG welding electrodes, plasma spraying electrodes, plasma cutting electrodes, electrical discharge machining electrodes, discharge lamp electrodes and the like. 
       Advantageous Effects of Invention 
       [0024]    According to the invention, with a tungsten alloy used in TIG rods, discharge lamps and other cathodes, it is possible to obtain a cathode material and a cathode which have a sufficiently long service life and favorable characteristics without using Th. 
     
    
     
       BRIEF DESCRIPTION OF DRAWING 
         [0025]      FIG. 1  is an optical microscopic photograph of a tungsten cathode material according to the invention. 
       
    
    
     DESCRIPTION OF EMBODIMENTS 
       [0026]    A cathode material of the invention is obtained in the following order. 
         [0027]    Tungsten powder, a metallic carbide or carbon powder and a compound of a rare earth element are mixed. 
         [0028]    The tungsten powder preferably has a purity of 99.9% or more and an average particle diameter of 0.5 μm to 20 μm. 
         [0029]    The metallic carbide is most suitably tungsten carbide such as WC and W 2 C. Since the tungsten carbide serves as a carbon source, and becomes tungsten after decomposed so as to emit carbon as illustrated in the optical microscopic photograph of  FIG. 1 , the tungsten carbide does not have any adverse influence on discharge characteristics or mechanical characteristics. When a metallic carbide of non-tungsten is selected, the carbide may be selected from carbides of metals having a high melting point which belong to Groups 4a, 5a and 6a, for example, carbides of Mo, Cr, V, Nb, Ta, Ti, Zr and Hf. In addition, regarding the method for adding carbon, carbon is not necessarily added in a form of a metallic carbide, and can also be added in a state of carbon. In a case in which carbon is added in a form of carbon powder, when the carbon has a powder form and a particle diameter of approximately 10 μm or less, the carbon is easily uniformly dispersed in a tungsten alloy. In addition, it is also possible to decompose an organic binder necessary for pressing, such as paraffin or polyethylene glycol, before sintering and to use the decomposed binder as a carbon source. Even in a case in which the carbon powder or the organic binder is used as a carbon source, it is confirmed that almost all the carbon powder or the organic binder becomes a metallic carbide after sintered. In addition, it is also possible to introduce carbon into a sintered compact in a thermal treatment described below instead of adding a carbide or carbon at this stage. The carbide or carbon is added so that an amount becomes 10 ppm to 1000 ppm in the sintered compact. 
         [0030]    In a method for adding the rare earth element, a starting material is not limited to an oxide, and a hydroxide, a nitrate, a carbonate or the like which turns into an oxide by thermal decomposition may be used. 
         [0031]    The above starting materials may be mixed in a dry manner or using a so-called doping method in which the compound of the rare earth element is mixed and dried with components thereof which are soluble in a solvent in a solution state. 
         [0032]    A mixed powder mixture is press-molded into a desired shape at a pressure of 50 MPa to 400 MPa, and a pressed body is sintered in a reduction atmosphere. A CIP method (cold isostatic pressing) or pressing using a mold can be used in the press molding. Regarding the sintering, an electric current sintering in which electrodes are attached to both ends of a compact and an electric current is made to flow may be carried out, and it is also possible to use a method in which a compact is heated and sintered in a geostatic state in an atmosphere furnace. In the latter case, sintering can be carried out at a sintering temperature of 1600° C. to 2200° C. An atmosphere during the sintering is suitably a reduction atmosphere, and particularly suitably an atmosphere in hydrogen since the sintering easily proceeds. 
         [0033]    When it is necessary to make the sintering further proceed, it is also possible to carry out HIP (hot isostatic pressing) at a pressure of 30 MPa to 300 MPa and a temperature of 1700° C. to 2200° C. after the sintering. 
         [0034]    When the compact is made into a rod shape, it is possible to further increase the density by carrying out swaging (hot forging). The density is preferably 98% or more, and more preferably 99% or more in terms of relative density. 
         [0035]    In addition, it is also possible to introduce carbon into the sintered compact obtained as described above at this stage. In order to introduce carbon, the sintered compact is preferably heated to 1500° C. to 2400° C. in an atmosphere in which carbon is present. The atmosphere in which carbon is present refers to an atmosphere in which a carbon source is present in a sintering jig, a furnace body, a heater portion or the like. During the above HIP treatment as well, generally, carbon is present in the atmosphere in an HIP furnace, and therefore it is also possible to introduce carbon from the atmosphere. 
         [0036]    The compact obtained in the above manner is the cathode material of the invention. A cathode can be obtained by carrying out mechanical works and electrical works as necessary on the cathode material into a desired cathode shape. The cathode is preferable for TIG welding, plasma spraying electrodes, plasma cutting electrodes, electrical discharge machining electrodes, discharge lamp electrodes and the like. 
         [0037]    Hereinafter, the invention will be described in more detail using examples. 
       Example 1 
       [0038]    First, predetermined amounts of tungsten powder, powder of a rare earth oxide and WC powder, each of which had an average particle diameter of 1 μm, were mixed in a Henschel mixer. The obtained powder was CIP-molded into a columnar shape at a pressure of 400 MPa, and sintered at 1700° C. in hydrogen. Furthermore, an HIP treatment or swaging was carried out after sintering, and the following tests were carried out on a material a sintered compact of which was made to have a density of 99% or more. Oxide-based materials in which sufficient densities could not be obtained will not be described. In addition, for some samples, carbon was not added to the raw material powder, the raw material powder was put into a carbon container, and a carburization treatment was carried out at 2200° C. for 1 hour in an Ar atmosphere. A high-pressure mercury lamp was produced using the obtained sample, lighted using electric currents of 6 A and 40 A, a UV output at a time of beginning of lighting was set to 100%, and a UV output rate (%) after 500 hours of lighting was measured. 
         [0039]    The amount of carbon in the sintered compact was measured using a glow discharge mass spectrometer (VG-9000 manufactured by V. G. Scientific Co., Ltd.). In addition, a crystal grain diameter (d) of the particles of the rare earth oxide in the sintered compact was computed from an optical microscopic photograph of the polished material taken at a magnification of 1000 times. A case in which the shape is isotropic as described in Patent document 1 can also be considered; however, when a crystal grain diameter is computed from a cross-section cut in the same direction as an electrode surface, there is no practical problem. Mass fractions (f) of particles of the rare earth oxide indicate the amounts of the respective components added to the raw material powder, and since it is confirmed that the results of chemical analyses or optical microscopic photographs of sintered compacts and values computed from theoretical densities of oxides are almost equal, the mass fractions may be measured using any method, which causes no practical problem. 
         [0040]    The results of lamp tests obtained from the above experiments are described in Tables 1 and 2. In addition, Comparison Specimen 1 was a commercially available W-2 mass % ThO 2  alloy; however, except for that, the specimen was manufactured and tested using the above methods. 
         [0041]    Table 1 describes negative electrode materials and the results of 6 A lamp tests. Table 2 describes the negative electrode materials and the results of the 40 A lamp tests. 
         [0000]    
       
         
               
               
               
               
               
               
             
               
               
               
               
               
               
               
               
             
               
               
               
               
               
               
               
               
             
           
               
                 TABLE 1 
               
             
             
               
                   
               
               
                   
                 Oxide 
                 Added 
                 Amount of 
                 UV output 
                   
               
             
          
           
               
                   
                   
                 f 
                 d 
                 substance 
                 carbon 
                 rate 
                 *** 
               
               
                 No. 
                 Type 
                 mass % 
                 μm 
                 mass % 
                 ppm 
                 % 
                 Evaluation 
               
               
                   
               
             
          
           
               
                 Specimen No. 1 
                 Nd 2 O 3   
                 1 
                 1.7 
                 0.01WC 
                 11 
                 85 
                 A 
               
               
                 Specimen No. 2 
                 Nd 2 O 3   
                 1 
                 1.7 
                 0.03WC 
                 23 
                 95 
                 A 
               
               
                 Specimen No. 3 
                 Nd 2 O 3   
                 1 
                 0.1 
                 0.03WC 
                 22 
                 93.5 
                 A 
               
               
                 Specimen No. 4 
                 Nd 2 O 3   
                 1 
                 1.7 
                 0.1WC 
                 67 
                 96 
                 A 
               
               
                 Specimen No. 5 
                 Nd 2 O 3   
                 1 
                 1.7 
                 0.3WC 
                 192 
                 95.5 
                 A 
               
               
                 Specimen No. 6 
                 Nd 2 O 3   
                 1 
                 1.7 
                 0.6WC 
                 370 
                 90.5 
                 A 
               
               
                 Specimen No. 7 
                 Nd 2 O 3   
                 1 
                 1.7 
                 1.6WC 
                 970 
                 86.5 
                 A 
               
               
                 Specimen No. 8 
                 Nd 2 O 3   
                 1 
                 1.7 
                 (Carburization 
                 21 
                 95 
                 A 
               
               
                   
                   
                   
                   
                 treatment) 
                   
                   
                   
               
               
                 Specimen No. 9 
                 Nd 2 O 3   
                 0.2 
                 1.5 
                 0.1WC 
                 70 
                 85.5 
                 A 
               
               
                 Specimen No. 10 
                 Nd 2 O 3   
                 1.5 
                 2.2 
                 0.1WC 
                 68 
                 87.5 
                 A 
               
               
                 Specimen No. 11 
                 Nd 2 0 3   
                 3 
                 2.3 
                 0.1WC 
                 69 
                 84.5 
                 A 
               
               
                 Specimen No. 12 
                 Nd 2 O 3   
                 10 
                 2.5 
                 0.1WC 
                 65 
                 80.5 
                 B 
               
               
                 Specimen No. 13 
                 Sm 2 O 3   
                 0.2 
                 2.4 
                 0.1WC 
                 67 
                 85 
                 A 
               
               
                 Specimen No. 14 
                 Sm 2 O 3   
                 1 
                 2.5 
                 0.1WC 
                 68 
                 93.5 
                 A 
               
               
                 Specimen No. 15 
                 La 2 O 3   
                 0.2 
                 2.3 
                 0.1WC 
                 70 
                 85 
                 A 
               
               
                 Specimen No. 16 
                 La 2 O 3   
                 1 
                 2.4 
                 0.1WC 
                 67 
                 85 
                 A 
               
               
                 Specimen No. 17 
                 Gd 2 O 3   
                 0.2 
                 2 
                 0.1WC 
                 67 
                 86.5 
                 A 
               
               
                 Specimen No. 18 
                 Gd 2 O 3   
                 1 
                 2.2 
                 0.2WC 
                 125 
                 92.5 
                 A 
               
               
                 Specimen No. 19 
                 ** Complex 
                 0.3 
                 1.5 
                 0.1WC 
                 66 
                 90 
                 A 
               
               
                 Specimen No. 20 
                 ** Complex 
                 1 
                 1.6 
                 0.1WC 
                 65 
                 93 
                 A 
               
               
                 Specimen No. 21 
                 ** Complex 
                 2.1 
                 1.8 
                 0.1WC 
                 70 
                 88 
                 A 
               
               
                 Specimen No. 22 
                 Nd 2 O 3   
                 0.1 
                 1.5 
                 0.1WC 
                 66 
                 83 
                 B 
               
               
                 Specimen No. 23 
                 Sm 2 O 3   
                 2.5 
                 2.9 
                 0.1WC 
                 66 
                 83.5 
                 B 
               
               
                 Specimen No. 24 
                 La 2 O 3   
                 0.1 
                 2.2 
                 0.1WC 
                 65 
                 82.5 
                 B 
               
               
                 Specimen No. 25 
                 Gd 2 O 3   
                 2.5 
                 3 
                 0.1WC 
                 66 
                 75.5 
                 B 
               
               
                 Specimen No. 26 
                 ** Complex 
                 0.15 
                 1.4 
                 0.1WC 
                 68 
                 84 
                 B 
               
               
                 Specimen No. 27 
                 CeO 2   
                 1 
                 2.1 
                 0.1WC 
                 68 
                 82.5 
                 B 
               
               
                 Specimen No. 28 
                 Y 2 O 3   
                 1 
                 2.1 
                 0.1WC 
                 69 
                 84 
                 B 
               
               
                 Specimen No. 29 
                 Pr 6 O 11   
                 1 
                 3.2 
                 0.1WC 
                 66 
                 83.5 
                 B 
               
               
                 Specimen No. 30 
                 Dy 2 O 3   
                 1 
                 2 
                 0.1WC 
                 69 
                 84 
                 B 
               
               
                 Specimen No. 31 
                 Nd 2 O 3   
                 1 
                 1.7 
                 0.02Tic 
                 45 
                 82 
                 B 
               
               
                 Specimen No. 32 
                 Nd 2 O 3   
                 1 
                 1.7 
                 0.06Tac 
                 44 
                 83.5 
                 B 
               
               
                 Specimen No. 33 
                 Nd 2 O 3   
                 1 
                 1.7 
                 0.1Mo2C 
                 48 
                 83 
                 B 
               
               
                 Comparative 
                 Th 2 O 
                 2 
                 3.6 
                 — 
                 7 
                 84.5 
                 (Criterion) 
               
               
                 Example 1 
                   
                   
                   
                   
                   
                   
                   
               
               
                 Comparative 
                 — 
                 0 
                 — 
                 0.1WC 
                 69 
                 62 
                 C 
               
               
                 Example 2 
                 — 
                 0 
                 — 
                 0.1WC 
                 69 
                 62 
                 C 
               
               
                 Comparative 
                 ZrO 2   
                 1 
                 1 
                 0.2WC 
                 108 
                 60.9 
                 C 
               
               
                 Example 3 
               
               
                   
               
             
          
         
       
     
         [0042]    Table 2 describes the negative electrode materials and the results of the 40 A lamp tests. 
         [0000]    
       
         
               
               
               
               
               
               
             
               
               
               
               
               
               
               
               
             
               
               
               
               
               
               
               
               
             
           
               
                 TABLE 2 
               
             
             
               
                   
               
               
                   
                 Oxide 
                   
                 Amount of 
                 UV output 
                   
               
             
          
           
               
                   
                   
                 f 
                 d 
                 Added substance 
                 carbon 
                 rate 
                 *** 
               
               
                 No. 
                 Type 
                 mass % 
                 μm 
                 mass % 
                 ppm 
                 % 
                 Evaluation 
               
               
                   
               
             
          
           
               
                 Specimen No. 34 
                 Nd 2 O 3   
                 1 
                 1.7 
                 0.03WC  
                 23 
                 93.5 
                 A 
               
               
                 Specimen No. 35 
                 Nd 2 O 3   
                 2 
                 2.4 
                 0.1WC 
                 69 
                 93 
                 A 
               
               
                 Specimen No. 36 
                 Sm 2 O 3   
                 1 
                 2.5 
                 0.1WC 
                 68 
                 91.5 
                 A 
               
               
                 Specimen No. 37 
                 La 2 O 3   
                 1 
                 2.4 
                 0.1WC 
                 67 
                 80.5 
                 A 
               
               
                 Comparative 
                 Th 2 O 
                 2 
                 3.6 
                 — 
                 7 
                 79.5 
                 (Criterion) 
               
               
                 Example 4 
               
               
                   
               
             
          
         
       
     
         [0043]    Specimens No. 1 to 37 are specimens of the invention. Meanwhile, since Specimen No. 3 is a specimen having the same composition as Specimen No. 2 which has been swaged so as to have a fine diameter, and the particles of the oxide are also deformed to be fine and long, the crystal grain diameter on the cross-section is small. 
         [0044]    In Tables 1 and 2, “complex” refers to a compound obtained by blending equal amounts of Nd 2 O 3 , Sm 2 O 3 , La 2 O 3 , Gd 2 O 3 , Y 2 O 3  and Tm 2 O 3  by mass %. 
         [0045]    In Tables 1 and 2, regarding “evaluation”, “A” indicates being equal or superior to W—ThO 2 , “B” indicates 80% or more after a predetermined period of time elapses, and “C” indicates less than 80% after the predetermined period of time elapses. 
         [0046]    Although not including ThO 2 , in the specimens of the invention described in Tables 1 and 2, the UV outputs slightly decrease. Particularly, a material of claim  2  maintains an equal or superior UV output to W—ThO 2  of Comparison Specimen 4 which is a comparison subject. 
         [0047]    Comparative Example 2 is a comparison specimen to which the rare earth oxide is not added. Among the specimens, the UV output rate decreased most. 
         [0048]    When the rare earth oxide accounts for 0.2 mass % to 10 mass %, half or more of the amount (mass fraction) of dispersed particles of the rare earth oxide are oxides of one or two or more of Sm, Nd, Gd and La, and an average particle diameter of the above oxides is set to 2.5 μm or less, tungsten alloys exhibit equal or superior characteristics to a W—ThO 2  alloy. 
         [0049]    In addition, Comparative Example 3 was an example in which an oxide different from the rare earth oxide was used, and no improvement of discharge characteristics was observed when the rare earth oxide was not included in spite of the amount of carbon being in the range of the invention. 
         [0050]    Regarding the amount of carbon, it was found that, in all the specimens of the invention having an amount of carbon in 10 ppm to 1000 ppm (mass fraction), the UV output rates were not easily decreased. 
         [0051]    In addition, when an oxide other than the oxides of Sm, Nd, Gd and La was solely added, a discharge effect did not become higher than that of ThO 2 , but a certain effect was exhibited due to the addition. In addition, in a case in which the above oxide was added together with the oxides of Sm, Nd, Gd and La as the rare earth oxides, the discharge characteristics became equal or superior to those of the W—ThO 2  alloy as described in Specimens No. 17 to 19 and Specimen No. 24. 
         [0052]    Meanwhile, necessary characteristics such as starting voltage, output efficiency and output fluctuation were investigated, there was no particular problem, and it was determined that, generally, the alloy of the invention has equal or superior characteristics to those of the W—ThO 2  alloy. 
       Example 2 
       [0053]    Swaging and drawing (a processing method in which a specimen is heated using a flame, and made to pass through a die, thereby decreasing an outer diameter) were carried out on the same specimens as Specimens 1, 7 and 19 used in Example 1 until φ1 (mm) is reached. A linear tungsten rod obtained in the above manner was used as a cathode, and 2 mm-thick iron sheets were TIG-welded. No defect was observed in the welded portion, and no abnormality such as deformation was found in the cathodes as well. 
       Example 3 
       [0054]    The same specimens as Specimens 1, 19, 23 and 31 used in Example 1 were mechanically processed into a tiered conical shape after cut, and used as cathodes of plasma spraying electrodes. The specimens were used in spraying of zirconium oxide, and any abnormality was not found in sprayed surface and the cathodes. Meanwhile, in addition to the tiered conical shape, a simply conical shape, a substantially conical shape with an R attached to a front end, and a shape having a certain straight portion which becomes narrower toward the front end can also be applied. 
       Example 4 
       [0055]    The same specimens as Specimens 21, 27, 33 and 34 used in Example 1 were cut into a rod shape, then, mechanically processed, and used as electrodes (corresponding to negative electrodes) for plasma cutting. 500 mm-thick tool steel which was a material to be cut was cut in a plasma cutting machine for which the above negative electrode was used. Argon gas was used as a gas used during the cutting. There was no abnormality during the cutting, the cut surfaces were clean, and no abnormality was found in the electrodes. 
       Example 5 
       [0056]    The same specimens as Specimens 1, 9, 17 and 34 used in Example 1 were cut into a rod shape, and then mechanically processed, thereby obtaining electric discharge machining electrodes matched to a hole shape of cemented carbide which was an article to be processed. The cemented carbide which was an article to be processed was electrical-discharge-machined using the above electrode. There was no abnormality during the machining, the cut surfaces were clean, and no abnormality was found in the electrodes.