Abstract:
The present invention discloses a nitrogen-containing luminescent particle, characterized in that a structure of the nitrogen-containing luminescent particle is divided into an oxygen poor zone, a transition zone, and an oxygen rich zone from a core to an outer surface of the particle depending on an increasing oxygen content, the oxygen poor zone being predominantly a nitride luminescent crystal or oxygen-containing solid solution thereof, the transition zone being predominantly a nitroxide material, the oxygen rich zone being predominantly an oxide material or oxynitride material; the nitride luminescent crystal or oxygen-containing solid solution thereof has a chemical formula of M m-m1 A a1 B b1 O o1 N n1 :R m1 , the nitroxide material has a chemical formula of M m-m2 A a2 B b2 O o2 N n2 :R m2 , the oxide material or oxynitride material has a chemical formula of M m-m3 A a3 B b3 O o3 N n3 :R m3 . The nitrogen-containing luminescent particle and the nitrogen-containing illuminant of the present invention have good chemical stability, good aging and light decay resistance, and high luminescent efficiency, and are useful for various luminescent devices. The manufacturing method of the present invention is easy and reliable, and useful for industrial mass production.

Description:
BACKGROUND OF THE INVENTION 
     Field of the Invention 
       [0001]    The present invention relates to LED fluorophors and luminescent devices, and more particularly to a nitrogen-containing luminescent particle capable of being effectively excited with UV light, violet light, or blue light and method for preparing a same, a nitrogen-containing illuminant, and a luminescent device. 
       Description of Related Art 
       [0002]    Nowadays, the semi-conductor lighting electric light source represented by light emitting diodes (LEDs) is touted as the fourth-generation lighting electric light source following incandescent lamps, fluorescent lamps, and energy-saving lamps, and is known as “the green light source in the 21st century”. 
         [0003]    As semi-conductor lighting is used in the field of general lighting, it is pressing to accelerate the development of white LEDs of high color rendering, anti-aging, and low light decay. Current methods of manufacturing a white LED mainly include the following. 1. Application of a yellow fluorescent powder (YAG) on a blue LED chip to effect emission of white light; however, the YAG fluorescent powder has the disadvantages of relatively high color temperature and relatively low color rendering index, which cannot meet the requirements of semi-conductor lighting; although the emission spectrum of the YAG fluorescent powder is very wide, the emission intensity in a red region is very weak, which results in the lack of red light after mixing with the blue LED chip, thereby affecting related color temperature and color rendering index of the white LED. 2. Application of green and red fluorescent powders on a blue LED chip to solve the problem above; however, the red fluorescent powder also has numerous problems such as large light decay and poor chemical stability of CaS:Eu 2+ , narrow excitation range of CaMoO 4 :Eu 2+ , weak absorption and low energy conversion efficiency in a blue region of Y 2 O 3 :Eu 3+  and Y 2 O 2 S:Eu 3+ , and poor light decay resistance of M 2 Si 5 N 8 :Eu 2+ , which all cannot be ideally matched to the LED chip, thus restricting the development of the white LED technology. 3. Introduction of a nitride fluorescent powder of CaAlSiN 3  crystal structure; although the overall performance is superior to the above-mentioned YAG fluorescent powder and common red fluorescent powder, the nitride fluorescent powder has significant drawbacks in that: (1) because diffusion of components, nucleation, and preferential growth orientation as well as primary crystallite size in the fluorescent powder synthesis process have not been fully understood, resulting in relatively low luminescent efficiency of the fluorescent powder, the luminescent efficiency needs to be further improved; and (2) because the fluorescent powder may degrade under a combined action of three factors, high optical density, high temperature, and high moisture, directly resulting in decreased overall light effect, and particularly substantial drifting in color coordinates, the durability of the fluorescent powder still cannot fully meet the requirements of common lighting. 
         [0004]    A fluorophor is disclosed in CN patent 200480040967.7, comprising an inorganic compound having the same crystal structure as CaAlSiN 3 . This solution uses a fluorophor with a nitrogen- and oxygen-containing inorganic compound as a matrix, and it is particularly emphasized that because the luminance brightness decreases with the increase of oxygen added, a small amount of oxygen added is preferred, and that in order to obtain good high-temperature durability, the atom numbers of O and N contained in the inorganic compound should meet 0.5≦N/(N+O)≦1 (see paragraphs 161 and 271 therein). An obvious disadvantage of this solution is that the range of oxygen content is limited in order to maintain the luminance brightness of the fluorescent powder, so that the durability of the fluorophor is reduced. 
         [0005]    The preparation of (Sr,Ca)AlSiN 3  red fluorescent powder using alloy process is proposed in “Synthetic method and luminescence properties of Sr x Ca 1-x AlSiN 3 :Eu 2+  mixed nitride fluorescent powders” published in J. Electrochem. Soc., 2008. Compared to fluorescent powder synthesis using a nitride as a starting material, this method results in lower oxygen content, such that the preparation of (Sr,Ca)AlSiN 3  red fluorescent powder using alloy process has better consistency and phase purity as well as good stability. However, this method still has a significant drawback in that: because it is highlighted for the (Sr,Ca)AlSiN 3  red fluorescent powder prepared by the alloy process to control low oxygen content in order to achieve high consistency and phase purity, the fluorescent powder has significantly reduced durability and thus poor utility, thus limiting its application. 
         [0006]    In “Reduced thermal degradation of the red-emitting Sr 2 Si 5 N 8 :Eu 2+  fluorescent powder via thermal treatment in nitrogen” published in Journal of Materials Chemistry C, 2015, the mechanism of thermal degradation of Sr 2 Si 5 N 8 :Eu 2+  is discussed. It is thought that by forming a layer of protective oxide film on a surface of the fluorescent powder through calcination, the oxidation of Eu 2+  is prevented and the thermal degradation is improved, and thus it is assumed that the applicability of Sr 2 Si 5 N 8 :Eu 2+  in LEDs can be improved, which, however, is not supported by any experimental data. Thus, the long-term aging problem of Sr 2 Si 5 N 8 :Eu 2+  is not fundamentally solved. In fact, in this system, due to poor stability of Sr 2 Si 5 N 8 :Eu 2+  itself, the crystal structure on the surface is destroyed during the calcination, so that the fluorescent powder has significantly decreased luminescent intensity, and thus has no practical application value. 
         [0007]    Taken together, in the prior art, there is a trade-off between the aging and light decay resistance of the nitride fluorescent powder and the luminescent efficiency of the fluorescent powder. That is to say, generally, the aging and light decay resistance of the fluorescent powder is improved at the expense of the luminescent efficiency of the fluorescent powder, or the luminescent efficiency of the fluorescent powder is improved at the expense of the aging and light decay resistance of the fluorescent powder. At present, there is no comprehensive solution that realizes the improvement of the aging and light decay resistance of the fluorescent powder without reducing the luminescent efficiency of the fluorescent powder. Thus, how to overcome the shortcomings in the prior art has become a major problem to be solved in the technical field of LED fluorophors and luminescent devices currently. 
       SUMMARY OF THE INVENTION 
       [0008]    An object of the present invention is to provide a nitrogen-containing luminescent particle and method for preparing a same, a nitrogen-containing illuminant, and a luminescent device, in order to the shortcomings in the prior art. The nitrogen-containing luminescent particle and the nitrogen-containing illuminant of the present invention have the advantages of good chemical stability, good aging and light decay resistance, and high luminescent efficiency, and are useful for various luminescent devices. The manufacturing method of the present invention is easy and reliable, advantageous for improving chemical and physical stabilities of the nitrogen-containing luminescent particle and the nitrogen-containing illuminant, and useful for industrial mass production. 
         [0009]    A nitrogen-containing luminescent particle according to the present invention is characterized in that a structure of the nitrogen-containing luminescent particle is divided into an oxygen poor zone, a transition zone, and an oxygen rich zone from a core to an outer surface of the particle depending on an increasing oxygen content, the oxygen poor zone being predominantly a nitride luminescent crystal or oxygen-containing solid solution thereof, the transition zone being predominantly a nitroxide material, the oxygen rich zone being predominantly an oxide material or oxynitride material; the nitride luminescent crystal or oxygen-containing solid solution thereof has a chemical formula of M m-m1 A a1 B b1 O o1 N n1 :R m1 , the nitroxide material has a chemical formula of M m-m2 A a2 B b2 O o2 N n2 :R m2 , the oxide material or oxynitride material has a chemical formula of M m-m3 A a3 B b3 O o3 N n3 :R m3 ; in the chemical formulas, the M element is at least one of Mg, Ca, Sr, Ba, Zn, Li, Na, K, Y, and Sc, the A element is at least one of B, Al, Ga, and In, the B element is at least one of C, Si, Ge, and Sn, R is at least one of Ce, Pr, Nd, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb, and Lu, wherein 0.5≦m≦1.5, 0.001≦m1≦0.2, 0.5≦a1≦1.5, 0.5≦b1≦1.5, 0≦o1≦0.5, 2.5≦n1≦3.5, 0≦m2≦0.2, 0.5≦a2≦1.5, 0.5≦b2≦1.5, 0.1≦o2≦4, 0.1≦n2≦3, 0≦m3≦0.2, 0.5≦a3≦1.5, 0.5≦b3≦1.5, 3≦o3≦5, 0≦n3≦0.5. 
         [0010]    A nitrogen-containing illuminant according to the present invention is characterized by comprising a mixture of the nitrogen-containing luminescent particle as described above and other crystalline grains or non-crystalline particles, the nitrogen-containing luminescent particle being present in the mixture at a proportion of no less than 50 wt %. 
         [0011]    A method 1 for preparing a nitrogen-containing luminescent particle according to the present invention is characterized by comprising the following basic steps: 
         [0012]    step 1: weighting desired starting materials at a stoichiometric ratio of cations in the composition of a chemical formula M m-m1 A a1 B b1 O o1 N n1 :R m1 , with a nitride, oxide or halide of M, A, B, and R as starting materials; 
         [0013]    step 2: uniformly mixing the starting materials weighted in the step 1 in a nitrogen atmosphere to form a mix; 
         [0014]    step 3: subjecting the mix obtained in the step 2 to high-temperature calcination in a calcination atmosphere, followed by low-temperature calcination at a reduced predetermined temperature in a nitrogen-oxygen mixture or air atmosphere, to give a nitrogen-containing luminescent particle semi-product; and 
         [0015]    step 4: subjecting the nitrogen-containing luminescent particle semi-product obtained in the step 3 to a post-treatment, to give a nitrogen-containing luminescent particle product. 
         [0016]    A method 2 for preparing a nitrogen-containing luminescent particle according to the present invention is characterized by comprising the following basic steps: 
         [0017]    step 1: weighting desired starting materials at a stoichiometric ratio of cations in the composition of a chemical formula M m-m1 A a1 B b1 O o1 N n1 :R m1 , with a nitride, oxide or halide of M, A, B, and R as starting materials; 
         [0018]    step 2: uniformly mixing the starting materials weighted in the step 1 in a nitrogen atmosphere to form a mix; 
         [0019]    step 3: subjecting the mix obtained in the step 2 to high-temperature calcination in a calcination atmosphere, to give a nitrogen-containing luminescent particle semi-product; 
         [0020]    step 4: subjecting the nitrogen-containing luminescent particle semi-product obtained in the step 3 to a post-treatment; and 
         [0021]    step 5: subjecting the nitrogen-containing luminescent particle obtained in the step 4 to low-temperature calcination in a nitrogen-oxygen mixture or air atmosphere, to give a nitrogen-containing luminescent particle product. 
         [0022]    A luminescent device according to the present invention is characterized by at least comprising an LED chip emitting UV light, violet light or blue light, and a fluorescent powder, wherein the fluorescent powder at least uses the nitrogen-containing luminescent particle of the present invention. 
         [0023]    A luminescent device according to the present invention is characterized by at least comprising an LED chip emitting UV light, violet light or blue light, and a fluorescent powder, wherein the fluorescent powder at least uses the nitrogen-containing illuminant of the present invention. 
         [0024]    The present invention is achieved based on the principles that: through the structural design of the nitrogen-containing luminescent particle as described above, the structure of the nitrogen-containing luminescent particle is divided into the oxygen poor zone, the transition zone, and the oxygen rich zone, and these zones are integrally chemically bonded together. Maintaining the original atom composition of the mix in the oxygen poor zone facilitates nucleation of the luminescent crystal of the nitride luminescent particle, thereby ensuring highly efficient luminescence; because a suitable amount of oxygen is present in the nitroxide material of the transition zone and in the oxide material of the oxygen rich zone in the nitrogen-containing luminescent particle, and particularly, the oxygen content is increasing from the core to the outer surface of the particle in the structure of the nitrogen-containing luminescent particle, the negative effect on the highly efficient luminescence formed in the transition zone and the oxygen rich zone can be effectively reduced, thereby ensuring significant improvement of luminescent efficiency of the whole particle; compared to nitrogen ion, oxygen ion has a smaller radius, higher electro-negativity, and stronger interionic binding force, and with the increase of oxygen content from the core to the outer surface of the particle in the structure of the nitrogen-containing luminescent particle, chemical and thermal stabilities of the transition zone and the oxygen rich zone in the nitrogen-containing luminescent particle can be gradually increased, so as to provide effective protection and shielding effect on the oxygen poor zone of the luminescent particle, thereby effectively improving thermal stability and durability of the nitrogen-containing luminescent particle in the LED application environment. 
         [0025]    Compared with the prior art, the present invention has the following significant advantages. 
         [0026]    1. Good chemical stability. In the present invention, a suitable amount of oxygen is introduced respectively in the transition zone and the oxygen rich zone of the nitrogen-containing luminescent particle, which meets the demands of growth of the host crystal of the nitrogen-containing luminescent particle in the process from nucleation to forming and densification, making the crystal structure more compact and stable, and thus improving weatherability of the nitrogen-containing luminescent particle. 
         [0027]    2. Good aging and light decay resistance. In the present invention, the structure of the nitrogen-containing luminescent particle is divided into the oxygen poor zone, the transition zone, and the oxygen rich zone, and the oxygen content is increasing from the core to the outer surface of the particle in the structure of the nitrogen-containing luminescent particle, such that oxygen ion having a smaller radius than that of nitrogen ion can be substituted for more nitrogen ions, so as to enhance the interionic binding force in the structure of the nitrogen-containing luminescent particle, thereby imparting the luminescent particle with very excellent aging and light decay resistance and thus high-temperature durability. In addition, because of the barrier protection effect from the transition zone and the oxygen rich zone, the oxygen poor zone of the nitrogen-containing luminescent particle is less susceptible to the external adverse environment, such that stability of the luminescent center of the nitrogen-containing luminescent particle is significantly improved. 
         [0028]    3. High luminescent efficiency. In the present invention, maintaining the original atom composition of the mix in the oxygen poor zone facilitates nucleation of the luminescent crystal of the nitride luminescent particle, thereby ensuring highly efficient luminescence; because a suitable amount of oxygen is present in the nitroxide material of the transition zone and in the oxide material of the oxygen rich zone in the nitrogen-containing luminescent particle, and particularly, the oxygen content is increasing from the core to the outer surface of the particle in the structure of the nitrogen-containing luminescent particle, the negative effect on the highly efficient luminescence formed in the transition zone and the oxygen rich zone can be effectively reduced, thereby ensuring significant improvement of luminescent efficiency of the whole particle. 
         [0029]    4. Wide applicability. The nitrogen-containing luminescent particle of the present invention is suitable for both nitrogen-containing illuminants and various luminescent devices. 
         [0030]    5. Ease and reliability of the manufacturing method. The manufacturing method of the present invention is advantageous for improving chemical and physical stabilities of the nitrogen-containing luminescent particle and the nitrogen-containing illuminant, and useful for industrial mass production. 
     
    
     
       BRIEF DESCRIPTION OF THE DRAWINGS 
         [0031]      FIG. 1  is a cross-sectional diagram of a structure of a nitrogen-containing luminescent particle of the present invention. 
           [0032]      FIG. 2  is emission spectra of nitrogen-containing luminescent particles from examples 1-4 and a comparative example 1 of the present invention. 
           [0033]      FIG. 3  is excitation spectra of the nitrogen-containing luminescent particles from the examples 1-4 and the comparative example 1 of the present invention. 
           [0034]      FIG. 4  is X-ray diffraction patterns of the nitrogen-containing luminescent particles from the examples 1-4 and the comparative example 1 of the present invention. 
           [0035]      FIG. 5  is an SEM picture of the nitrogen-containing luminescent particle from the example 4 of the present invention. 
           [0036]      FIG. 6  is an SEM picture of the nitrogen-containing luminescent particle from the comparative example 1 of the present invention. 
           [0037]      FIG. 7  is emission spectra of nitrogen-containing luminescent particles from examples 10-13 and a comparative example 3 of the present invention. 
           [0038]      FIG. 8  is thermal quenching spectra of the nitrogen-containing luminescent particles from the examples 10-13 and the comparative example 3 of the present invention. 
           [0039]      FIG. 9  is emission spectra of nitrogen-containing luminescent particles from examples 15-18 and a comparative example 4 of the present invention. 
           [0040]      FIG. 10  is thermal quenching spectra of nitrogen-containing luminescent particles from examples 19-21 and a comparative example 5 of the present invention. 
       
    
    
     DETAILED DESCRIPTION OF THE INVENTION 
       [0041]    A detailed description of the present invention will be further given below in detail with reference to the accompanying drawings and embodiments. 
         [0042]    Referring to  FIG. 1 , a nitrogen-containing luminescent particle of the present invention is shown. A structure of the nitrogen-containing luminescent particle is divided into an oxygen poor zone, a transition zone, and an oxygen rich zone from a core to an outer surface of the particle depending on an increasing oxygen content, the oxygen poor zone being predominantly a nitride luminescent crystal or oxygen-containing solid solution thereof, the transition zone being predominantly a nitroxide material, the oxygen rich zone being predominantly an oxide material or oxynitride material; the nitride luminescent crystal or oxygen-containing solid solution thereof has a chemical formula of M m-m1 A a1 B b1 O o1 N n1 :R m1 , the nitroxide material has a chemical formula of M m-m2 A a2 B b2 O o2 N n2 :R m2 , the oxide material or oxynitride material has a chemical formula of M m-m3 A a3 B b3 O o3 N r3 :R m3 ; in the chemical formulas, the M element is at least one of Mg, Ca, Sr, Ba, Zn, Li, Na, K, Y, and Sc, the A element is at least one of B, Al, Ga, and In, the B element is at least one of C, Si, Ge, and Sn, R is at least one of Ce, Pr, Nd, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb, and Lu, wherein 0.5≦m≦1.5, 0.001≦m1≦0.2, 0.5≦a1≦1.5, 0.5≦b1≦1.5, 0≦o1≦0.5, 2.5≦n1≦3.5, 0≦m2≦0.2, 0.5≦a2≦1.5, 0.5≦b2≦1.5, 0.1≦o2≦4, 0.1≦n2≦3, 0≦m3≦0.2, 0.5≦a3≦1.5, 0.5≦b3≦1.5, 3≦o3≦5, 0≦n3≦0.5. 
         [0043]    Further preferred embodiments of a nitrogen-containing luminescent particle of the present invention include the following. 
         [0044]    The transition zone has a thickness ranging from 50-500 nm, the oxygen rich zone is at the outer side of the transition zone and has a thickness of no more than 50 nm, and the oxygen poor zone is from the inner side of the transition zone to the core of the nitrogen-containing luminescent particle. 
         [0045]    The nitride luminescent crystal or oxygen-containing solid solution thereof in the oxygen poor zone has a content of no less than 90%, the nitroxide material in the transition zone has a content of no less than 60%, and the oxide material or oxynitride material in the oxygen rich zone has a content of no less than 50%. 
         [0046]    The nitride luminescent crystal is at least one of (Sr x Ca 1-x-y1 )AlSiN 3 :y1Eu or an oxygen-containing solid solution thereof, the nitroxide material is (Sr x Ca 1-x-y1 )AlSiN 3-z1 O 1.5z1 :y1Eu, and the oxide material or oxynitride material is (Sr x Ca 1-x-y1 )AlSiO 4.5-z2 N z2 :y1Eu, wherein 0≦x≦0.99, 0.001≦y1≦0.2, 0&lt;z1&lt;3, 0&lt;z2&lt;0.5. 
         [0047]    The oxygen poor zone further comprises a nitroxide luminescent crystal, the transition zone further comprises a nitride material, and the oxygen rich zone further comprises a nitroxide material. 
         [0048]    The material of the structure of the nitrogen-containing luminescent particle is a compound or a mixture. 
         [0049]    Any of the nitrogen-containing luminescent particles of the present invention as described above is excited at an excitation wavelength ranging from 300-500 nm to emit red light having a peak wavelength at 600-670 nm. 
         [0050]    A nitrogen-containing illuminant according to the present invention comprises a mixture of any of the nitrogen-containing luminescent particles of the present invention as described above and other crystalline grains or non-crystalline particles, the nitrogen-containing luminescent particle being present in the mixture at a proportion of no less than 50 wt %. 
         [0051]    A method 1 for preparing a nitrogen-containing luminescent particle and preferred embodiments thereof according to the present invention comprises the following specific steps: 
         [0052]    step 1: weighting desired starting materials at a stoichiometric ratio of cations in the composition of a chemical formula M m-m1 A a1 B b1 O o1 N n1 :R m1 , with a nitride, oxide or halide of M, A, B, and R as starting materials; 
         [0053]    step 2: uniformly mixing the starting materials weighted in the step 1 in a nitrogen atmosphere to form a mix; 
         [0054]    step 3: subjecting the mix obtained in the step 2 to high-temperature calcination in a calcination atmosphere, followed by low-temperature calcination at a reduced predetermined temperature in a nitrogen-oxygen mixture or air atmosphere, to give a nitrogen-containing luminescent particle semi-product; 
         [0055]    wherein the high-temperature calcination has a temperature of 1400-2000° C. and a duration of 6-18 h; the atmosphere of the high-temperature calcination is a nitrogen atmosphere, a nitrogen-argon mixture atmosphere, another inert gas atmosphere, a nitrogen-hydrogen mixture atmosphere, or another reducing gas atmosphere; the pressure of the high-temperature calcination is 1-100 atm; the low-temperature calcination has a temperature of 200-450° C. and a duration of 1-24 h; the feeding rate of the nitrogen-oxygen mixture or air in the low-temperature calcination is 0.1-10 L/min; and the volume percent of oxygen in the nitrogen-oxygen mixture atmosphere is no more than 20%; and 
         [0056]    step 4: subjecting the nitrogen-containing luminescent particle semi-product obtained in the step 3 to a post-treatment, to give a nitrogen-containing luminescent particle product; wherein the post-treatment includes grinding, screening, washing, drying, and the washing is performed to obtain the nitrogen-containing luminescent particle product having a conductivity of less than 10 μs/cm. 
         [0057]    A method 2 for preparing a nitrogen-containing luminescent particle and preferred embodiments thereof according to the present invention comprises the following specific steps: 
         [0058]    step 1: weighting desired starting materials at a stoichiometric ratio of cations in the composition of a chemical formula M m-m1 A a1 B b1 O o1 N n1 :R m1 , with a nitride, oxide or halide of M, A, B, and R as starting materials; 
         [0059]    step 2: uniformly mixing the starting materials weighted in the step 1 in a nitrogen atmosphere to form a mix; 
         [0060]    step 3: subjecting the mix obtained in the step 2 to high-temperature calcination in a calcination atmosphere, to give a nitrogen-containing luminescent particle semi-product; 
         [0061]    wherein the high-temperature calcination has a temperature of 1400-2000° C. and a duration of 6-18 h; the atmosphere of the high-temperature calcination is a nitrogen atmosphere, a nitrogen-argon mixture atmosphere, another inert gas atmosphere, a nitrogen-hydrogen mixture atmosphere, or another reducing gas atmosphere; and the pressure of the high-temperature calcination is 1-100 atm; 
         [0062]    step 4: subjecting the nitrogen-containing luminescent particle semi-product obtained in the step 3 to a post-treatment; wherein the post-treatment includes grinding, screening, washing, drying, and the washing is performed to obtain the nitrogen-containing luminescent particle product having a conductivity of less than 10 μs/cm; and 
         [0063]    step 5: subjecting the nitrogen-containing luminescent particle obtained in the step 4 to low-temperature calcination in a nitrogen-oxygen mixture or air atmosphere, to give a nitrogen-containing luminescent particle product; wherein the low-temperature calcination has a temperature of 200-450° C. and a duration of 1-24 h; and the volume percent of oxygen in the nitrogen-oxygen mixture atmosphere is no more than 20%. 
         [0064]    A luminescent device according to the present invention at least comprises an LED chip emitting UV light, violet light or blue light, and a fluorescent powder, wherein the fluorescent powder at least uses any of the nitrogen-containing luminescent particles of the present invention as described above. 
         [0065]    A luminescent device according to the present invention at least comprises an LED chip emitting UV light, violet light or blue light, and a fluorescent powder, wherein the fluorescent powder at least uses the nitrogen-containing illuminant of the present invention as described above. 
         [0066]    Further preferably, a luminescent device according to the present invention further comprises other types of fluorescent powders, so as to meet lighting requirements or applications in high-color-rendering white light LEDs in the backlight, by complementation of luminescent colors. 
         [0067]    Specific examples and comparative examples of a nitrogen-containing luminescent particle and method for preparing a same according to the present invention are further disclosed below, wherein the examples means that a nitrogen-containing luminescent particle product is obtained following a structure of a nitrogen-containing luminescent particle and method for preparing a same of the present invention, and the comparative examples means that a nitrogen-containing luminescent particle product is obtained following a nitrogen-containing luminescent particle and method for preparing a same disclosed in the prior art. The average oxygen atom content and the average nitrogen atom content in the nitrogen-containing luminescent particles are obtained by an oxygen/nitrogen analyzer. 
       Example 1 
       [0068]    0.27 g of Ca 3 N 2 , 9.954 g of Sr 3 N 2 , 4.477 g of AlN, 5.107 g of Si 3 N 4 , and 0.192 g of Eu 2 O 3  were weighted. These starting materials were thoroughly mixed in a nitrogen atmosphere for 3 h and charged into an Mo crucible, which was rapidly transferred to a tubular furnace, and then the temperature was gradually raised to 1700° C. under a nitrogen atmosphere for 12 h; the resulting nitrogen-containing luminescent particle was pulverized and sieved, the sieved nitrogen-containing luminescent particle was placed into deionized water and stirred for 30 min, then suction-filtered, and finally washed to a conductivity of 8.56 μs/cm, and after drying, the temperature was raised to 400° C. in an air atmosphere for calcination for 5 h, to give a nitrogen-containing luminescent particle product. The emission spectrum is shown in  FIG. 2 , the excitation spectrum is shown in  FIG. 3 , and the X-ray diffraction pattern is shown in  FIG. 4 . The chemical composition of the oxygen poor zone of the nitrogen-containing luminescent particle is Ca 0.05 Sr 0.94 AlSiN 3 :0.01Eu, the chemical composition of the transition zone is Ca 0.05 Sr 0.94 AlSiO 1.5 N 2 :0.01Eu, with a thickness of 400 nm, and the chemical composition of the oxygen rich zone is Ca 0.05 Sr 0.94 AlSiO 4.5 :0.01Eu, with a thickness of 30 nm. 
       Example 2 
       [0069]    0.435 g of Ca 3 N 2 , 9.712 g of Sr 3 N 2 , 4.512 g of AlN, 5.147 g of Si 3 N 4 , and 0.194 g of Eu 2 O 3  were weighted. These starting materials were thoroughly mixed in a nitrogen atmosphere for 3 h and charged into an Mo crucible, which was rapidly transferred to a tubular furnace, and then the temperature was gradually raised to 1700° C. under a nitrogen atmosphere for 12 h; the resulting nitrogen-containing luminescent particle was pulverized and sieved, the sieved nitrogen-containing luminescent particle was placed into deionized water and stirred for 30 min, then suction-filtered, and finally washed to a conductivity of 4.42 μs/cm, and after drying, the temperature was raised to 400° C. in an air atmosphere for calcination for 5 h, to give a nitrogen-containing luminescent particle product. The emission spectrum is shown in  FIG. 2 , the excitation spectrum is shown in  FIG. 3 , and the X-ray diffraction pattern is shown in  FIG. 4 . The chemical composition of the oxygen poor zone of the nitrogen-containing luminescent particle is Ca 0.08 Sr 0.91 AlSiN 3 :0.01Eu, the chemical composition of the transition zone is Ca 0.08 Sr 0.91 AlSiO 1.8 N 1.8 :0.01Eu, with a thickness of 380 nm, and the chemical composition of the oxygen rich zone is Ca 0.08 Sr 0.91 AlSi 0.7 O 3.9 :0.01Eu, with a thickness of 25 nm. 
       Example 3 
       [0070]    0.547 g of Ca 3 N 2 , 9.549 g of Sr 3 N 2 , 4.535 g of AlN, 5.174 g of Si 3 N 4 , and 0.195 g of Eu 2 O 3  were weighted. These starting materials were thoroughly mixed in a nitrogen atmosphere for 3 h and charged into an Mo crucible, which was rapidly transferred to a tubular furnace, and then the temperature was gradually raised to 1700° C. under a nitrogen atmosphere for 12 h; the resulting nitrogen-containing luminescent particle was pulverized and sieved, the sieved nitrogen-containing luminescent particle was placed into deionized water and stirred for 30 min, then suction-filtered, and finally washed to a conductivity of 6.25 μs/cm, and after drying, the temperature was raised to 400° C. in an air atmosphere for calcination for 5 h, to give a nitrogen-containing luminescent particle product. The emission spectrum is shown in  FIG. 2 , the excitation spectrum is shown in  FIG. 3 , and the X-ray diffraction pattern is shown in  FIG. 4 . The chemical composition of the oxygen poor zone of the nitrogen-containing luminescent particle is Ca 0.1 Sr 0.89 AlSiN 3 :0.01Eu, the chemical composition of the transition zone is Ca 0.1 Sr 0.89 AlSiO 1.5 N 2 :0.01Eu, with a thickness of 270 nm, and the chemical composition of the oxygen rich zone is Ca 0.1 Sr 0.89 AlSiO 4.5 :0.01Eu, with a thickness of 42 nm. 
       Example 4 
       [0071]    0.66 g of Ca 3 N 2 , 9.383 g of Sr 3 N 2 , 5.56 g of AlN, 5.202 g of Si 3 N 4 , and 0.196 g of Eu 2 O 3  were weighted. These starting materials were thoroughly mixed in a nitrogen atmosphere for 3 h and charged into an Mo crucible, which was rapidly transferred to a tubular furnace, and then the temperature was gradually raised to 1700° C. under a nitrogen atmosphere for 12 h; the resulting nitrogen-containing luminescent particle was pulverized and sieved, the sieved nitrogen-containing luminescent particle was placed into deionized water and stirred for 30 min, then suction-filtered, and finally washed to a conductivity of 7.28 μs/cm, and after drying, the temperature was raised to 400° C. in an air atmosphere for calcination for 5 h, to give a nitrogen-containing luminescent particle product. The emission spectrum is shown in  FIG. 2 , the excitation spectrum is shown in  FIG. 3 , the luminescent intensity is shown in Table 1 and is higher than that in comparative example 1, the X-ray diffraction pattern is shown in  FIG. 4 , and the SEM picture is shown in  FIG. 5 . The chemical composition of the oxygen poor zone of the nitrogen-containing luminescent particle is Ca 0.12 Sr 0.87 AlSiN 3 :0.01Eu, the chemical composition of the transition zone is Ca 0.12 Sr 0.87 AlSiO 1.35 N 2.1 :0.01Eu, with a thickness of 360 nm, and the chemical composition of the oxygen rich zone is Ca 0.12 Sr 0.87 AlSi 1.05 O 4.3 N 0.2 :0.01Eu, with a thickness of 48 nm. 
       Comparative Example 1 
       [0072]    0.66 g of Ca 3 N 2 , 9.383 g of Sr 3 N 2 , 5.56 g of AlN, 5.202 g of Si 3 N 4 , and 0.196 g of Eu 2 O 3  were weighted. These starting materials were thoroughly mixed in a nitrogen atmosphere for 3 h and charged into an Mo crucible, which was rapidly transferred to a tubular furnace, and then the temperature was gradually raised to 1700° C. under a nitrogen atmosphere for 12 h; the resulting nitrogen-containing luminescent particle was pulverized and sieved, the sieved nitrogen-containing luminescent particle was placed into deionized water and stirred for 30 min, then suction-filtered, and finally washed to a conductivity of 5.12 μs/cm, and after drying, a nitrogen-containing luminescent particle product was obtained. The emission spectrum is shown in  FIG. 2 , the excitation spectrum is shown in  FIG. 3 , the X-ray diffraction pattern is shown in  FIG. 4 , and the SEM picture is shown in  FIG. 6 . The chemical composition of the nitrogen-containing luminescent particle is Ca 0.12 Sr 0.87 AlSiN 3 : 0.01Eu. 
         [0073]    The nitrogen-containing luminescent particles in the examples and the comparative example as described above were made into a luminescent device respectively, and the testing results show that the luminescent intensity and the aging properties of the comparative example 1 are lower than those of the examples 1-4, as shown in Table 1. The aging conditions are: SMD 2835 LED Lamp Bead, chip size 10×30 mil, chip band 452.5-455 nm, current 150 mA, power 0.5 W, ambient conditions: normal temperature and moisture. 
         [0000]    
       
         
               
               
               
             
               
               
               
               
               
             
               
               
               
               
               
             
           
               
                 TABLE 1 
               
             
             
               
                   
               
               
                   
                 luminescent  
                 1000 h aging 
               
             
          
           
               
                   
                 intensity  
                 light decay 
                 ΔX 
                 ΔY 
               
               
                   
               
             
          
           
               
                 Example 1 
                 105 
                 2.2% 
                 −0.006 
                 0.005 
               
               
                 Example 2 
                 103 
                 2.3% 
                 −0.007 
                 0.005 
               
               
                 Example 3 
                 103 
                 2.3% 
                 −0.007 
                 0.006 
               
               
                 Example 4 
                 104 
                 2.5% 
                 −0.01 
                 0.008 
               
               
                 Comparative example 1 
                 100 
                 4.1% 
                 −0.022 
                 0.015 
               
               
                   
               
             
          
         
       
     
       Example 5 
       [0074]    0.545 g of Ca 3 N 2 , 9.412 g of Sr 3 N 2 , 4.522 g of AlN, 5.133 g of Si 3 N 4 , and 0.388 g of Eu 2 O 3  were weighted. These starting materials were thoroughly mixed in a nitrogen atmosphere for 2 h and charged into an Mo crucible, which was rapidly transferred to a tubular furnace, and then the temperature was gradually raised to 1800° C. under a nitrogen-argon mixture atmosphere for 10 h, and then the temperature was reduced to 350° C., and the air atmosphere was fed at a rate of 5 L/min for calcination for 6 h; the resulting nitrogen-containing luminescent particle was pulverized and sieved, the sieved nitrogen-containing luminescent particle was placed into deionized water and stirred for 30 min, then suction-filtered, and finally washed to a conductivity of 5.33 μs/cm, and after drying, a nitrogen-containing luminescent particle product was obtained. The chemical composition of the oxygen poor zone of the nitrogen-containing luminescent particle is Ca 0.1 Sr 0.88 AlSi 0.995 O 0.02 N 2.98 : 0.02Eu, the chemical composition of the transition zone is Ca 0.1 Sr 0.88 AlSiO 0.9 N 2.4 :0.02Eu, with a thickness of 450 nm, and the chemical composition of the oxygen rich zone is Ca 0.1 Sr 0.88 AlSiO 4.5 :0.02Eu, with a thickness of 24 nm. 
       Example 6 
       [0075]    0.447 g of Ca 3 N 2 , 11.3 g of Ba 3 N 2 , 3.706 g of AlN, 4.229 g of Si 3 N 4 , and 0.318 g of Eu 2 O 3  were weighted. These starting materials were thoroughly mixed in a nitrogen atmosphere for 2 h and charged into an Mo crucible, which was rapidly transferred to a tubular furnace, and then the temperature was gradually raised to 1800° C. under a nitrogen-argon mixture atmosphere for 10 h, and then the temperature was reduced to 350° C., and the air atmosphere was fed at a rate of 5 L/min for calcination for 6h; the resulting nitrogen-containing luminescent particle was pulverized and sieved, the sieved nitrogen-containing luminescent particle was placed into deionized water and stirred for 30 min, then suction-filtered, and finally washed to a conductivity of 6.89 μs/cm, and after drying, a nitrogen-containing luminescent particle product was obtained. The chemical composition of the oxygen poor zone of the nitrogen-containing luminescent particle is Ca 0.1 Ba 0.88 AlSiN 3 :0.02Eu, the chemical composition of the transition zone is Ca 0.1 Ba 0.88 AlSiO 0.9 N 2.4 :0.02Eu, with a thickness of 200 nm, and the chemical composition of the oxygen rich zone is Ca 0.1 Ba 0.88 AlSi 1.01 O 4.5 , with a thickness of 32 nm. 
       Example 7 
       [0076]    0.547 g of Ca 3 N 2 , 9.442 g of Sr 3 N 2 , 4.309 g of AlN, 0.137 g of BN, 5.175 g of Si 3 N 4 , and 0.389 g of Eu 2 O 3  were weighted. These starting materials were thoroughly mixed in a nitrogen atmosphere for 2 h and charged into an Mo crucible, which was rapidly transferred to a tubular furnace, and then the temperature was gradually raised to 1800° C. under a nitrogen-argon mixture atmosphere for 10 h, and then the temperature was reduced to 350° C., and the air atmosphere was fed at a rate of 5 L/min for calcination for 6h; the resulting nitrogen-containing luminescent particle was pulverized and sieved, the sieved nitrogen-containing luminescent particle was placed into deionized water and stirred for 30 min, then suction-filtered, and finally washed to a conductivity of 7.65 μs/cm, and after drying, a nitrogen-containing luminescent particle product was obtained. The chemical composition of the oxygen poor zone of the nitrogen-containing luminescent particle is Ca 0.1 Sr 0.88 Al 0.95 B 0.05 SiN 3 :0.02Eu, the chemical composition of the transition zone is Ca 0.1 Sr 0.88 Al 0.95 Bi 0.05 SiO 1.2 N 2.2 :0.02Eu, with a thickness of 360 nm, and the chemical composition of the oxygen rich zone is Ca 0.2 Sr 0.78 AlSiO 4.5 :0.02Eu, with a thickness of 50 nm. 
       Example 8 
       [0077]    0.538 g of Ca 3 N 2 , 9.291 g of Sr 3 N 2 , 4.24 g of AlN, 0.456 g of GaN, 5.092 g of Si 3 N 4 , and 0.383 g of Eu 2 O 3  were weighted. These starting materials were thoroughly mixed in a nitrogen atmosphere for 2 h and charged into an Mo crucible, which was rapidly transferred to a tubular furnace, and then the temperature was gradually raised to 1800° C. under a nitrogen-argon mixture atmosphere for 10 h, and then the temperature was reduced to 350° C., and the air atmosphere was fed at a rate of 5 L/min for calcination for 6h; the resulting nitrogen-containing luminescent particle was pulverized and sieved, the sieved nitrogen-containing luminescent particle was placed into deionized water and stirred for 30 min, then suction-filtered, and finally washed to a conductivity of 7.65 μs/cm, and after drying, a nitrogen-containing luminescent particle product was obtained. The chemical composition of the oxygen poor zone of the nitrogen-containing luminescent particle is Ca 0.1 Sr 0.88 Al 0.95 Ga 0.05 SiN 3 :0.02Eu, the chemical composition of the transition zone is Ca 0.1 Sr 0.88 Al 0.95 Ga 0.05 SiO 1.5 N 2 :0.02Eu, with a thickness of 310 nm, and the chemical composition of the oxygen rich zone is Ca 0.1 Sr 0.88 Al 0.95 Ga 0.05 Si 0.76 O 4 , with a thickness of 50 nm. 
       Example 9 
       [0078]    0.556 g of Ca 3 N 2 , 9.05 g of Sr 3 N 2 , 0.131 g of Li 3 N, 4.609 of AlN, 5.259 g of Si 3 N 4 , and 0.396 g of Eu 2 O 3  were weighted. These starting materials were thoroughly mixed in a nitrogen atmosphere for 2 h and charged into an Mo crucible, which was rapidly transferred to a tubular furnace, and then the temperature was gradually raised to 1800° C. under a nitrogen-argon mixture atmosphere for 10 h, and then the temperature was reduced to 350° C., and the air atmosphere was fed at a rate of 5 L/min for calcination for 6h; the resulting nitrogen-containing luminescent particle was pulverized and sieved, the sieved nitrogen-containing luminescent particle was placed into deionized water and stirred for 30 min, then suction-filtered, and finally washed to a conductivity of 9.12 s/cm, and after drying, a nitrogen-containing luminescent particle product was obtained. The chemical composition of the oxygen poor zone of the nitrogen-containing luminescent particle is Ca 0.1 Sr 0.83 Li 0.1 AlSiN 3 :0.02Eu, the chemical composition of the transition zone is Ca 0.1 Sr 0.83 Li 0.1 AlSi 0.7 O 1.2 N 1.8 :0.02Eu, with a thickness of 440 nm, and the chemical composition of the oxygen rich zone is Ca 0.1 Sr 0.83 Li 0.1 AlSi 0.7 O 3.88 , with a thickness of 25 nm. 
       Comparative Example 2 
       [0079]    0.544 g of Ca 3 N 2 , 9.4 g of Sr 3 N 2 , 4.516 g of AlN, 5.152 g of Si 3 N 4 , and 0.388 g of Eu 2 O 3  were weighted. These starting materials were thoroughly mixed in a nitrogen atmosphere for 2 h and charged into an Mo crucible, which was rapidly transferred to a tubular furnace, and then the temperature was gradually raised to 1800° C. under a nitrogen-argon mixture atmosphere for 10 h; the resulting nitrogen-containing luminescent particle was pulverized and sieved, the sieved nitrogen-containing luminescent particle was placed into deionized water and stirred for 30 min, then suction-filtered, and finally washed to a conductivity of 5.77 μs/cm, to give a nitrogen-containing luminescent particle product. The chemical composition of the nitrogen-containing luminescent particle is Ca 0.1 Sr 0.88 AlSiN 3 :0.02Eu. 
         [0080]    The nitrogen-containing luminescent particles in the examples and the comparative example as described above were made into a luminescent device respectively, and the testing results show that the luminescent intensity and the aging properties of the comparative example 2 are lower than those of the examples 5-9, as shown in Table 2. The aging conditions are: SMD 2835 LED Lamp Bead, chip size 10×30 mil, chip band 452.5-455 nm, current 150 mA, power 0.5 W, ambient conditions: normal temperature and moisture. 
         [0000]    
       
         
               
               
               
             
               
               
               
               
               
             
               
               
               
               
               
             
           
               
                 TABLE 2 
               
             
             
               
                   
               
               
                   
                 luminescent  
                 1000 h aging 
               
             
          
           
               
                   
                 intensity 
                 light decay 
                 ΔX 
                 ΔY 
               
               
                   
               
             
          
           
               
                 Example 5 
                 105 
                 2.5% 
                 −0.008 
                 0.006 
               
               
                 Example 6 
                 104 
                 2.6% 
                 −0.009 
                 0.008 
               
               
                 Example 7 
                 105 
                 2.7% 
                 −0.01 
                 0.009 
               
               
                 Example 8 
                 103 
                 2.6% 
                 −0.01 
                 −0.01 
               
               
                 Example 9 
                 105 
                 2.6% 
                 −0.009 
                 −0.009 
               
               
                 comparative example 2 
                 100 
                 4.3% 
                 −0.021 
                 0.015 
               
               
                   
               
             
          
         
       
     
       Example 10 
       [0081]    5.38 g of Ca 3 N 2 , 5.25 g of AlN, 5.989 g of Si 3 N 4 , and 3.381 g of Eu 2 O 3  were weighted. These starting materials were thoroughly mixed in a nitrogen atmosphere for 3 h and charged into an Mo crucible, which was rapidly transferred to a tubular furnace, and then the temperature was gradually raised to 1850° C. under a nitrogen-argon mixture atmosphere for 12 h; the resulting nitrogen-containing luminescent particle was pulverized and sieved, the sieved nitrogen-containing luminescent particle was placed into deionized water and stirred for 30 min, then suction-filtered, and finally washed to a conductivity of 4.18 μs/cm, and after drying, the temperature was raised to 300° C. in a nitrogen-oxygen mixture atmosphere (in which the volume percent of oxygen is 10%) for calcination for 8 h, to give a nitrogen-containing luminescent particle product. The emission spectrum is shown in  FIG. 1 , and the thermal quenching spectrum is shown in  FIG. 8 . The chemical composition of the oxygen poor zone of the nitrogen-containing luminescent particle is Ca 0.85 AlSiN 3 :0.15Eu, the chemical composition of the transition zone is Ca 0.85 AlSiO 1.5 N 2 :0.15Eu, with a thickness of 230 nm, and the chemical composition of the oxygen rich zone is Ca 0.85 AlSiO 4.5 : 0.15Eu, with a thickness of 30 nm. 
       Example 11 
       [0082]    5.432 g of Ca 3 N 2 , 5.301 g of AlN, 6.047 g of Si 3 N 4 , and 3.219 g of EuN were weighted. These starting materials were thoroughly mixed in a nitrogen atmosphere for 3 h and charged into an Mo crucible, which was rapidly transferred to a tubular furnace, and then the temperature was gradually raised to 1850° C. under a nitrogen-argon mixture atmosphere for 12 h; the resulting nitrogen-containing luminescent particle was pulverized and sieved, the sieved nitrogen-containing luminescent particle was placed into deionized water and stirred for 30 min, then suction-filtered, and finally washed to a conductivity of 7.63 μs/cm, and after drying, the temperature was raised to 300° C. in a nitrogen-oxygen mixture atmosphere (in which the volume percent of oxygen is 10%) for calcination for 8 h, to give a nitrogen-containing luminescent particle product. The emission spectrum is shown in  FIG. 1 , and the thermal quenching spectrum is shown in  FIG. 8 . The chemical composition of the oxygen poor zone of the nitrogen-containing luminescent particle is Ca 0.85 AlSiN 3 :0.15Eu, the chemical composition of the transition zone is Ca 0.85 AlSi 0.75 ON 2 :0.15Eu, with a thickness of 290 nm, and the chemical composition of the oxygen rich zone is Ca 0.85 AlSi 0.625 O 3.6 N 0.1 :0.15Eu, with a thickness of 25 nm. 
       Example 12 
       [0083]    5.215 g of Ca 3 N 2 , 5.089 g of AlN, 5.805 g of Si 3 N 4 , and 3.891 g of EuF 3  were weighted. These starting materials were thoroughly mixed in a nitrogen atmosphere for 3 h and charged into an Mo crucible, which was rapidly transferred to a tubular furnace, and then the temperature was gradually raised to 1850° C. under a nitrogen-argon mixture atmosphere for 12 h; the resulting nitrogen-containing luminescent particle was pulverized and sieved, the sieved nitrogen-containing luminescent particle was placed into deionized water and stirred for 30 min, then suction-filtered, and finally washed to a conductivity of 5.44 μs/cm, and after drying, the temperature was raised to 300° C. in a nitrogen-oxygen mixture atmosphere (in which the volume percent of oxygen is 10%) for calcination for 8 h, to give a nitrogen-containing luminescent particle product. The emission spectrum is shown in  FIG. 1 , and the thermal quenching spectrum is shown in  FIG. 8 . The chemical composition of the oxygen poor zone of the nitrogen-containing luminescent particle is Ca 0.85 AlSiN 3 :0.15Eu, the chemical composition of the transition zone is Ca 0.85 Al 0.7 SiO 0.9 N 2.1 :0.15Eu, with a thickness of 275 nm, and the chemical composition of the oxygen rich zone is Ca 0.85 Al 0.8 SiO 4.2 :0.15Eu, with a thickness of 16 nm. 
       Example 13 
       [0084]    4.985 g of Ca 3 N 2 , 4.865 g of AlN, 5.55 g of Si 3 N 4 , and 4.599 g of EuCl 3  were weighted. These starting materials were thoroughly mixed in a nitrogen atmosphere for 3 h and charged into an Mo crucible, which was rapidly transferred to a tubular furnace, and then the temperature was gradually raised to 1850° C. under a nitrogen-argon mixture atmosphere for 12 h; the resulting nitrogen-containing luminescent particle was pulverized and sieved, the sieved nitrogen-containing luminescent particle was placed into deionized water and stirred for 30 min, then suction-filtered, and finally washed to a conductivity of 6.16 μs/cm, and after drying, the temperature was raised to 300° C. in a nitrogen-oxygen mixture atmosphere (in which the volume percent of oxygen is 10%) for calcination for 8 h, to give a nitrogen-containing luminescent particle product. The emission spectrum is shown in  FIG. 7 , and the thermal quenching spectrum is shown in  FIG. 8 . The chemical composition of the oxygen poor zone of the nitrogen-containing luminescent particle is Ca 0.85 AlSiN 3 :0.15Eu, the chemical composition of the transition zone is Ca 0.85 AlSiO 1.2 N 2.2 :0.15Eu, with a thickness of 365 nm, and the chemical composition of the oxygen rich zone is Ca 0.85 AlSiO 4.5 :0.15Eu, with a thickness of 42 nm. 
       Comparative Example 3 
       [0085]    5.38 g of Ca 3 N 2 , 5.25 g of AlN, 5.989 g of Si 3 N 4 , and 3.381 g of Eu 2 O 3  were weighted. These starting materials were thoroughly mixed in a nitrogen atmosphere for 3 h and charged into an Mo crucible, which was rapidly transferred to a tubular furnace, and then the temperature was gradually raised to 1850° C. under a nitrogen-argon mixture atmosphere for 12 h; the resulting nitrogen-containing luminescent particle was pulverized and sieved, the sieved nitrogen-containing luminescent particle was placed into deionized water and stirred for 30 min, then suction-filtered, and finally washed to a conductivity of 6.35 μs/cm, and after drying, a nitrogen-containing luminescent particle product was obtained. The emission spectrum is shown in  FIG. 7 , and the thermal quenching spectrum is shown in  FIG. 8 . The chemical composition of the nitrogen-containing luminescent particle is Ca 0.85 AlSiN 3 : 0.15Eu. 
         [0086]    The nitrogen-containing luminescent particles in the examples and the comparative example as described above were made into a luminescent device respectively, and the testing results show that the luminescent intensity and the aging properties of the comparative example 3 are lower than those of the examples 10-13, as shown in Table 3. The aging conditions are: SMD 2835 LED Lamp Bead, chip size 10×30 mil, chip band 452.5-455 nm, current 150 mA, power 0.5 W, ambient conditions: normal temperature and moisture. 
         [0000]    
       
         
               
               
               
             
               
               
               
               
               
             
               
               
               
               
               
             
           
               
                 TABLE 3 
               
             
             
               
                   
               
               
                   
                 luminescent  
                 1000 h aging 
               
             
          
           
               
                   
                 intensity 
                 light decay 
                 ΔX 
                 ΔY 
               
               
                   
               
             
          
           
               
                 Example 10 
                 103 
                 3.8% 
                 −0.018 
                 0.011 
               
               
                 Example 11 
                 102 
                 3.9% 
                 −0.019 
                 0.011 
               
               
                 Example 12 
                 103 
                 3.8% 
                 −0.016 
                 0.009 
               
               
                 Example 13 
                 104 
                 3.6% 
                 −0.016 
                 0.01 
               
               
                 comparative example 3 
                 100 
                 5.0% 
                 −0.03 
                 0.025 
               
               
                   
               
             
          
         
       
     
       Example 14 
       [0087]    7.191 g of Ca 3 N 2 , 6.812 g of Si 3 N 4 , 5.971 g of AlN, and 0.026 g of Eu 2 O 3  were weighted. These starting materials were thoroughly mixed in a nitrogen atmosphere for 1 h and charged into an Mo crucible, which was rapidly transferred to a tubular furnace, and then the temperature was gradually raised to 1820° C. under a nitrogen atmosphere for 8 h; the resulting nitrogen-containing luminescent particle was pulverized and sieved, the sieved nitrogen-containing luminescent particle was placed into deionized water and stirred for 30 min, then suction-filtered, and finally washed to a conductivity of 3.27 μs/cm, and after drying, the temperature was raised to 200° C. in a nitrogen-oxygen mixture atmosphere (in which the volume percent of oxygen is 5%) for calcination for 15 h, to give a nitrogen-containing luminescent particle product. The chemical composition of the oxygen poor zone of the nitrogen-containing luminescent particle is Ca 0.999 AlSiN 3 :0.001Eu, the chemical composition of the transition zone is Ca 0.999 AlSi 0.75 ON 2 :0.001Eu, with a thickness of 330 nm, and the chemical composition of the oxygen rich zone is Ca 0.999 AlSi 0.75 O 4 :0.001Eu, with a thickness of 42 nm. 
       Example 15 
       [0088]    7.068 g of Ca 3 N 2 , 6.756 g of Si 3 N 4 , 5.922 g of AlN, and 0.254 g of Eu 2 O 3  were weighted. These starting materials were thoroughly mixed in a nitrogen atmosphere for 1 h and charged into an Mo crucible, which was rapidly transferred to a tubular furnace, and then the temperature was gradually raised to 1820° C. under a nitrogen atmosphere for 8 h; the resulting nitrogen-containing luminescent particle was pulverized and sieved, the sieved nitrogen-containing luminescent particle was placed into deionized water and stirred for 30 min, then suction-filtered, and finally washed to a conductivity of 5.61 μs/cm, and after drying, the temperature was raised to 200° C. in a nitrogen-oxygen mixture atmosphere (in which the volume percent of oxygen is 5%) for calcination for 15 h, to give a nitrogen-containing luminescent particle product. The emission spectrum is shown in  FIG. 9 . The chemical composition of the oxygen poor zone of the nitrogen-containing luminescent particle is Ca 0.99 AlSiN 3 :0.01Eu, the chemical composition of the transition zone is Ca 0.99 AlSiO 1.2 N 2.2 :0.01Eu, with a thickness of 385 nm, and the chemical composition of the oxygen rich zone is Ca 0.99 AlSiO 4.5 :0.01Eu, with a thickness of 32 nm. 
       Example 16 
       [0089]    6.543 g of Ca 3 N 2 , 6.517 g of Si 3 N 4 , 5.713 g of AlN, and 1.226 g of Eu 2 O 3  were weighted. These starting materials were thoroughly mixed in a nitrogen atmosphere for 1 h and charged into an Mo crucible, which was rapidly transferred to a tubular furnace, and then the temperature was gradually raised to 1820° C. under a nitrogen atmosphere for 8 h; the resulting nitrogen-containing luminescent particle was pulverized and sieved, the sieved nitrogen-containing luminescent particle was placed into deionized water and stirred for 30 min, then suction-filtered, and finally washed to a conductivity of 6.95 μs/cm, and after drying, the temperature was raised to 200° C. in a nitrogen-oxygen mixture atmosphere (in which the volume percent of oxygen is 5%) for calcination for 15 h, to give a nitrogen-containing luminescent particle product. The emission spectrum is shown in  FIG. 9 . The chemical composition of the oxygen poor zone of the nitrogen-containing luminescent particle is Ca 0.95 AlSiN 3 :0.05Eu, the chemical composition of the transition zone is Ca 0.95 AlSi 0.775 O 0.9 N 2.1 :0.05Eu, with a thickness of 360 nm, and the chemical composition of the oxygen rich zone is Ca 0.95 AlSi 0.725 O 3.9 , with a thickness of 27 nm. 
       Example 17 
       [0090]    5.937 g of Ca 3 N 2 , 6.242 g of Si 3 N 4 , 5.472 g of AlN, and 2.349 g of Eu 2 O 3  were weighted. These starting materials were thoroughly mixed in a nitrogen atmosphere for 1 h and charged into an Mo crucible, which was rapidly transferred to a tubular furnace, and then the temperature was gradually raised to 1820° C. under a nitrogen atmosphere for 8 h; the resulting nitrogen-containing luminescent particle was pulverized and sieved, the sieved nitrogen-containing luminescent particle was placed into deionized water and stirred for 30 min, then suction-filtered, and finally washed to a conductivity of 5.14 μs/cm, and after drying, the temperature was raised to 200° C. in a nitrogen-oxygen mixture atmosphere (in which the volume percent of oxygen is 5%) for calcination for 15 h, to give a nitrogen-containing luminescent particle product. The emission spectrum is shown in  FIG. 9 . The chemical composition of the oxygen poor zone of the nitrogen-containing luminescent particle is Ca 0.9 AlSiN 3 :0.1Eu, the chemical composition of the transition zone is Ca 0.9 AlSiO 1.5 N 2 :0.1Eu, with a thickness of 440 nm, and the chemical composition of the oxygen rich zone is Ca 0.9 AlSiO 4.5 :0.1Eu, with a thickness of 28 nm. 
       Example 18 
       [0091]    4.866 g of Ca 3 N 2 , 5.756 g of Si 3 N 4 , 5.045 g of AlN, and 4.332 g of Eu 2 O 3  were weighted. These starting materials were thoroughly mixed in a nitrogen atmosphere for 1 h and charged into an Mo crucible, which was rapidly transferred to a tubular furnace, and then the temperature was gradually raised to 1820° C. under a nitrogen atmosphere for 8 h; the resulting nitrogen-containing luminescent particle was pulverized and sieved, the sieved nitrogen-containing luminescent particle was placed into deionized water and stirred for 30 min, then suction-filtered, and finally washed to a conductivity of 8.22 μs/cm, and after drying, the temperature was raised to 200° C. in a nitrogen-oxygen mixture atmosphere (in which the volume percent of oxygen is 5%) for calcination for 15 h, to give a nitrogen-containing luminescent particle product. The emission spectrum is shown in  FIG. 9 . The chemical composition of the oxygen poor zone of the nitrogen-containing luminescent particle is Ca 0.8 AlSiN 3 :0.2Eu, the chemical composition of the transition zone is Ca 0.8 AlSi 0.725 O 1.1 N 1.9 :0.2Eu, with a thickness of 345 nm, and the chemical composition of the oxygen rich zone is Ca 0.8 AlSi 1.075 O 4.2 N 0.3 : 0.2Eu, with a thickness of 40 nm. 
       Comparative Example 4 
       [0092]    4.866 g of Ca 3 N 2 , 5.756 g of Si 3 N 4 , 5.045 g of AlN, and 4.332 g of Eu 2 O 3  were weighted. These starting materials were thoroughly mixed in a nitrogen atmosphere for 1 h and charged into an Mo crucible, which was rapidly transferred to a tubular furnace, and then the temperature was gradually raised to 1820° C. under a nitrogen atmosphere for 8 h; the resulting nitrogen-containing luminescent particle was pulverized and sieved, the sieved nitrogen-containing luminescent particle was placed into deionized water and stirred for 30 min, then suction-filtered, and finally washed to a conductivity of 6.11 μs/cm, and after drying, a nitrogen-containing luminescent particle product was obtained. The emission spectrum is shown in  FIG. 9 . The chemical composition of the nitrogen-containing luminescent particle is Ca 0.8 AlSiN 3 :0.2Eu. 
         [0093]    The nitrogen-containing luminescent particles in the examples and the comparative example as described above were made into a luminescent device respectively, and the testing results show that the luminescent intensity and the aging properties of the comparative example 4 are lower than those of the examples 14-18, as shown in Table 4. The aging conditions are: SMD 2835 LED Lamp Bead, chip size 10×30 mil, chip band 452.5-455 nm, current 150 mA, power 0.5 W, ambient conditions: normal temperature and moisture. 
         [0000]    
       
         
               
               
               
             
               
               
               
               
               
             
               
               
               
               
               
             
           
               
                 TABLE 4 
               
             
             
               
                   
               
               
                   
                 luminescent  
                 1000 h aging 
               
             
          
           
               
                   
                 intensity 
                 light decay 
                 ΔX 
                 ΔY 
               
               
                   
               
             
          
           
               
                 Example 14 
                 120 
                 2.1% 
                 −0.01 
                 0.008 
               
               
                 Example 15 
                 128 
                 2.3% 
                 −0.01 
                 0.007 
               
               
                 Example 16 
                 118 
                 2.9% 
                 −0.012 
                 0.01 
               
               
                 Example 17 
                 110 
                 3.3% 
                 −0.015 
                 0.013 
               
               
                 Example 18 
                 102 
                 4.0% 
                 −0.022 
                 0.016 
               
               
                 comparative example 4 
                 100 
                 6.5% 
                 −0.035 
                 0.025 
               
               
                   
               
             
          
         
       
     
       Example 19 
       [0094]    0.803 g of Ca 3 N 2 , 7.98 g of Sr 3 N 2 , 4.439 g of AlN, 5.064 g of Si 3 N 4 , and 1.715 g of Eu 2 O 3  were weighted. These starting materials were thoroughly mixed in a nitrogen atmosphere for 4 h and charged into an Mo crucible, which was rapidly transferred to a tubular furnace, and then the temperature was gradually raised to 1780° C. under a nitrogen-argon mixture atmosphere for 9 h, and then the temperature was reduced to 320° C., and a nitrogen-oxygen mixture atmosphere (in which the volume percent of oxygen is 7%) was fed at a rate of 3 L/min for calcination for 8h; the resulting nitrogen-containing luminescent particle was pulverized and sieved, the sieved nitrogen-containing luminescent particle was placed into deionized water and stirred for 30 min, then suction-filtered, and finally washed to a conductivity of 5.18 μs/cm, and after drying, a nitrogen-containing luminescent particle product was obtained. The thermal quenching spectrum is shown in  FIG. 10 . The oxygen poor zone of the nitrogen-containing luminescent particle is Ca 0.15 Sr 0.76 AlSiN 3 :0.09Eu, the transition zone is Ca 0.15 Sr 0.76 AlSi 0.8 O 0.8 N 2.2 :0.09Eu, with a thickness of 220 nm, and the oxygen rich zone is Ca 0.15 Sr 0.76 AlSi 0.825 O 4 N 0.1 :0.09Eu, with a thickness of 29 nm. 
       Example 20 
       [0095]    0.805 g of Ca 3 N 2 , 8.002 g of Sr 3 N 2 , 4.317 g of AlN, 0.332 g of Al 2 O 3 , 4.824 g of Si 2 N 3 , and 1.72 g of Eu 2 O 3  were weighted. These starting materials were thoroughly mixed in a nitrogen atmosphere for 4 h and charged into an Mo crucible, which was rapidly transferred to a tubular furnace, and then the temperature was gradually raised to 1780° C. under a nitrogen-argon mixture atmosphere for 9 h, and then the temperature was reduced to 320° C., and a nitrogen-oxygen mixture atmosphere (in which the volume percent of oxygen is 7%) was fed at a rate of 3 L/min for calcination for 8h; the resulting nitrogen-containing luminescent particle was pulverized and sieved, the sieved nitrogen-containing luminescent particle was placed into deionized water and stirred for 30 min, then suction-filtered, and finally washed to a conductivity of 6.25 μs/cm, and after drying, a nitrogen-containing luminescent particle product was obtained. The thermal quenching spectrum is shown in  FIG. 10 . The chemical composition of the oxygen poor zone of the nitrogen-containing luminescent particle is Ca 0.15 Sr 0.76 AlSi 0.95 O 0.2 N 2.8 :0.09Eu, the chemical composition of the transition zone is Ca 0.15 Sr 0.76 AlSi 0.85 O 0.6 N 2.4 :0.09Eu, with a thickness of 360 nm, and the chemical composition of the oxygen rich zone is Ca 0.15 Sr 0.76 AlSi 0.81 O 4 N 0.08 :0.09Eu, with a thickness of 49 nm. 
       Example 21 
       [0096]    0.798 g of Ca 3 N 2 , 7.932 g of Sr 3 N 2 , 4.412 g of AlN, 4.858 g of Si 3 N 4 , 0.295 g of SiO 2 , and 1.705 g of Eu 2 O 3  were weighted. These starting materials were thoroughly mixed in a nitrogen atmosphere for 4 h and charged into an Mo crucible, which was rapidly transferred to a tubular furnace, and then the temperature was gradually raised to 1780° C. under a nitrogen-argon mixture atmosphere for 9 h, and then the temperature was reduced to 320° C., and a nitrogen-oxygen mixture atmosphere (in which the volume percent of oxygen is 7%) was fed at a rate of 3 L/min for calcination for 8h; the resulting nitrogen-containing luminescent particle was pulverized and sieved, the sieved nitrogen-containing luminescent particle was placed into deionized water and stirred for 30 min, then suction-filtered, and finally washed to a conductivity of 5.26 μs/cm, and after drying, a nitrogen-containing luminescent particle product was obtained. The thermal quenching spectrum is shown in  FIG. 10 . The chemical composition of the oxygen poor zone of the nitrogen-containing luminescent particle is Ca 0.15 Sr 0.76 AlSi 0.975 O 0.1 N 2.9 :0.09Eu, the chemical composition of the transition zone is Ca 0.15 Sr 0.76 AlSi 0.8 O 0.8 N 2.2 :0.09Eu, with a thickness of 340 nm, and the chemical composition of the oxygen rich zone is Ca 0.15 Sr 0.76 AlSi 0.85 O 4.2 :0.09Eu, with a thickness of 29 nm. 
       Comparative Example 5 
       [0097]    0.803 g of Ca 3 N 2 , 7.98 g of Sr 3 N 2 , 4.439 g of AlN, 5.064 g of Si 3 N 4 , and 1.715 g of Eu 2 O 3  were weighted. These starting materials were thoroughly mixed in a nitrogen atmosphere for 4 h and charged into an Mo crucible, which was rapidly transferred to a tubular furnace, and then the temperature was gradually raised to 1780° C. under a nitrogen-argon mixture atmosphere for 9 h; the resulting nitrogen-containing luminescent particle was pulverized and sieved, the sieved nitrogen-containing luminescent particle was placed into deionized water and stirred for 30 min, then suction-filtered, and finally washed to a conductivity of 6.87 μs/cm, and after drying, a nitrogen-containing luminescent particle product was obtained. The thermal quenching spectrum is shown in  FIG. 10 . The chemical composition of the nitrogen-containing luminescent particle is Ca 0.15 Sr 0.76 AlSiN 3 :0.09Eu. 
         [0098]    The nitrogen-containing luminescent particles in the examples and the comparative example as described above were made into a luminescent device respectively, and the testing results show that the luminescent intensity and the aging properties of the comparative example 5 are lower than those of the examples 19-21, as shown in Table 5. The aging conditions are: SMD 2835 LED Lamp Bead, chip size 10×30 mil, chip band 452.5-455 nm, current 150 mA, power 0.5 W, ambient conditions: normal temperature and moisture. 
         [0000]    
       
         
               
               
               
             
               
               
               
               
               
             
           
               
                 TABLE 5 
               
             
             
               
                   
               
               
                   
                 luminescent  
                 1000 h aging 
               
             
          
           
               
                   
                 intensity  
                 light decay 
                 ΔX 
                 ΔY 
               
               
                   
               
               
                 Example 19 
                 104 
                 3.0% 
                 −0.015 
                 0.012 
               
               
                 Example 20 
                 102 
                 3.2% 
                 −0.014 
                 0.011 
               
               
                 Example 21 
                 103 
                 3.2% 
                 −0.015 
                 0.012 
               
               
                 comparative example 5 
                 100 
                 6.5% 
                 −0.028 
                 0.022 
               
               
                   
               
             
          
         
       
     
       Example 22 
       [0099]    7.025 g of Ca 3 N 2 , 5.903 g of AlN, 6.735 g of Si 3 N 4 , 0.203 g of Eu 2 O 3 , and 0.134 g of Dy 2 O 3  were weighted. These starting materials were thoroughly mixed in a nitrogen atmosphere for 3 h and charged into an Mo crucible, which was rapidly transferred to a tubular furnace, and then the temperature was gradually raised to 1880° C. under a nitrogen atmosphere for 12 h; the resulting nitrogen-containing luminescent particle was pulverized and sieved, the sieved nitrogen-containing luminescent particle was placed into deionized water and stirred for 30 min, then suction-filtered, and finally washed to a conductivity of 4.56 μs/cm, and after drying, the temperature was raised to 280° C. in a nitrogen-oxygen mixture atmosphere (in which the volume percent of oxygen is 8%) for calcination for 10 h, to give a nitrogen-containing luminescent particle product. The chemical composition of the oxygen poor zone of the nitrogen-containing luminescent particle is Ca 0.987 AlSiN 3 :0.008Eu, 0.005Dy, the chemical composition of the transition zone is Ca 0.987 AlSi 0.8 O 0.8 N 2.2 :0.008Eu, 0.005Dy, with a thickness of 390 nm, and the chemical composition of the oxygen rich zone is Ca 0.987 AlSi 0.8 O 4.1 :0.008Eu, 0.005Dy, with a thickness of 28 nm. 
       Example 23 
       [0100]    7.032 g of Ca 3 N 2 , 5.909 g of AlN, 6.741 g of Si 3 N 4 , 0.203 g of Eu 2 O 3 , and 0.115 g of Lu 2 O 3  were weighted. These starting materials were thoroughly mixed in a nitrogen atmosphere for 3 h and charged into an Mo crucible, which was rapidly transferred to a tubular furnace, and then the temperature was gradually raised to 1880° C. under a nitrogen atmosphere for 12 h; the resulting nitrogen-containing luminescent particle was pulverized and sieved, the sieved nitrogen-containing luminescent particle was placed into deionized water and stirred for 30 min, then suction-filtered, and finally washed to a conductivity of 5.66 μs/cm, and after drying, the temperature was raised to 280° C. in a nitrogen-oxygen mixture atmosphere (in which the volume percent of oxygen is 8%) for calcination for 10 h, to give a nitrogen-containing luminescent particle product. The chemical composition of the oxygen poor zone of the nitrogen-containing luminescent particle is Ca 0.988 AlSiN 3 :0.008Eu, 0.004Lu, the chemical composition of the transition zone is Ca 0.988 AlSiO 0.9 N 2.4 :0.008Eu, 0.004Lu, with a thickness of 465 nm, and the chemical composition of the oxygen rich zone is Ca 0.988 AlSiO 4.5 :0.008Eu, 0.004Lu, with a thickness of 38 nm. 
       Example 24 
       [0101]    7.034 g of Ca 3 N 2 , 5.911 g of AlN, 6.743 g of Si 3 N 4 , 0.203 g of Eu 2 O 3 , and 0.109 g of Ho 2 O 3  were weighted. These starting materials were thoroughly mixed in a nitrogen atmosphere for 3 h and charged into an Mo crucible, which was rapidly transferred to a tubular furnace, and then the temperature was gradually raised to 1880° C. under a nitrogen atmosphere for 12 h; the resulting nitrogen-containing luminescent particle was pulverized and sieved, the sieved nitrogen-containing luminescent particle was placed into deionized water and stirred for 30 min, then suction-filtered, and finally washed to a conductivity of 3.87 μs/cm, and after drying, the temperature was raised to 280° C. in a nitrogen-oxygen mixture atmosphere (in which the volume percent of oxygen is 8%) for calcination for 10 h, to give a nitrogen-containing luminescent particle product. The chemical composition of the oxygen poor zone of the nitrogen-containing luminescent particle is Ca 0.988 AlSiN 3 :0.008Eu, 0.004Ho, the chemical composition of the transition zone is Ca 0.988 AlSi 0.875 O 0.5 N 2.5 :0.008Eu, 0.004Ho, with a thickness of 390 nm, and the chemical composition of the oxygen rich zone is Ca 0.988 AlSi 0.65 O 3.8 :0.008Eu, 0.004Ho, with a thickness of 37 nm. 
       Example 25 
       [0102]    7.033 g of Ca 3 N 2 , 5.91 g of AlN, 6.743 g of Si 3 N 4 , 0.203 g of Eu 2 O 3 , and 0.111 g of Ho 2 O 3  were weighted. These starting materials were thoroughly mixed in a nitrogen atmosphere for 3 h and charged into an Mo crucible, which was rapidly transferred to a tubular furnace, and then the temperature was gradually raised to 1880° C. under a nitrogen atmosphere for 12 h; the resulting nitrogen-containing luminescent particle was pulverized and sieved, the sieved nitrogen-containing luminescent particle was placed into deionized water and stirred for 30 min, then suction-filtered, and finally washed to a conductivity of 4.89 μs/cm, and after drying, the temperature was raised to 280° C. in a nitrogen-oxygen mixture atmosphere (in which the volume percent of oxygen is 8%) for calcination for 10 h, to give a nitrogen-containing luminescent particle product. The chemical composition of the oxygen poor zone of the nitrogen-containing luminescent particle is Ca 0.987 AlSiN 3 :0.008Eu, 0.005Ce, the chemical composition of the transition zone is Ca 0.987 AlSiO 1.2 N 2.2 :0.008Eu, 0.005Ce, with a thickness of 350 nm, and the chemical composition of the oxygen rich zone is Ca 0.987 AlSiO 4.5 :0.008Eu, 0.005Ce, with a thickness of 15 nm. 
       Comparative Example 6 
       [0103]    7.095 g of Ca 3 N 2 , 5.933 g of AlN, 6.768 g of Si 3 N 4 , and 0.204 g of Eu 2 O 3  were weighted. These starting materials were thoroughly mixed in a nitrogen atmosphere for 3 h and charged into an Mo crucible, which was rapidly transferred to a tubular furnace, and then the temperature was gradually raised to 1880° C. under a nitrogen atmosphere for 12 h; the resulting nitrogen-containing luminescent particle was pulverized and sieved, the sieved nitrogen-containing luminescent particle was placed into deionized water and stirred for 30 min, then suction-filtered, and finally washed to a conductivity of 5.58 μs/cm, and after drying, a nitrogen-containing luminescent particle product was obtained. The chemical composition of the nitrogen-containing luminescent particle is Ca 0.992 AlSiN 3 :0.008Eu. 
         [0104]    The nitrogen-containing luminescent particles in the examples and the comparative example as described above were made into a luminescent device respectively, and the testing results show that the luminescent intensity and the aging properties of the comparative example 6 are lower than those of the examples 22-25, as shown in Table 6. The aging conditions are: SMD 2835 LED Lamp Bead, chip size 10×30 mil, chip band 452.5-455 nm, current 150 mA, power 0.5 W, ambient conditions: normal temperature and moisture. 
         [0000]    
       
         
               
               
               
             
               
               
               
               
               
             
               
               
               
               
               
             
           
               
                 TABLE 6 
               
             
             
               
                   
               
               
                   
                 luminescent  
                 1000 h aging 
               
             
          
           
               
                   
                 intensity 
                 light decay 
                 ΔX 
                 ΔY 
               
               
                   
               
             
          
           
               
                 Example 22 
                 103 
                 2.3% 
                 −0.009  
                 0.008 
               
               
                 Example 23 
                 101 
                 2.5% 
                 −0.01 
                 0.009 
               
               
                 Example 24 
                 104 
                 2.5% 
                 −0.01 
                 0.008 
               
               
                 Example 25 
                 102 
                 2.4% 
                 −0.008  
                 0.007 
               
               
                 comparative example 6 
                 100 
                 3.8% 
                 −0.02 
                 0.016 
               
               
                   
               
             
          
         
       
     
         [0105]    The contents not specifically described in the specific embodiments of the present invention are known in the art and may be implemented with reference to known techniques. 
         [0106]    The present invention has been verified via repeated tests, and satisfactory test results are achieved. 
         [0107]    The specific embodiments and examples above are provided to support the technical concepts of a nitrogen-containing luminescent particle and method for preparing a same, a nitrogen-containing illuminant, and a luminescent device of the present invention, and are not intended to limit the scope of protection of the present invention. Any equivalent modification or variations made based on the present technical solution following the technical concepts of the present invention, all fall within the scope of protection of the present invention.