Abstract:
There is provided a composition comprising covalently linked segments of for example, polycaprolactone and polyethylene glycol that are linked by a cross-linker. Such a composition foams in the presence of a catalyst and a solution containing an oxygen forming chemical like hydrogen peroxide. The foamed composition retains oxygen for delivery to, for example, a wound, where it aids in healing.

Description:
RELATED APPLICATIONS 
       [0001]    The present application claims priority to U.S. Provisional Application Ser. No. 61/909,039, filed on Nov. 26, 2013, which is incorporated herein in its entirety by reference thereto. 
     
    
     BACKGROUND OF THE INVENTION 
       [0002]    The present disclosure relates to the provision of oxygen for use in wound healing. 
         [0003]    The lack of oxygen, i.e. hypoxia, is commonly experienced by people in their extremities as they get older due to poor blood circulation as well as by those with conditions such as diabetes. Studies have also shown below normal, low oxygen tension in the skins of older people. This often leads to poor skin health and an excessive presence of visible conditions such as wrinkles, dryness and lower skin elasticity. Over the years, cosmetic manufacturers have introduced skin formulations with a large variety of ingredients such as emollients, exfoliators, moisturizers etc., to retard these age related effects and improve and maintain skin health. Attacking the problem of low oxygen directly has not been generally practiced. 
         [0004]    In addition to the normal decrease in oxygen delivery to the skin which can have beneficial results when reversed, oxygen applied to wounds as, for example, a dressing containing oxygen, can speed healing. The delivery of oxygen to the skin and wounds for common use is a technological challenge, since oxygen is quite reactive and unstable. High concentrations of oxygen could not be provided for home use because of this instability. Oxygen can, however, be provided in the form of a peroxide and a peroxide decomposition catalyst per U.S. Patent Application Publication No. 2006/0121101 to Ladizinsky. This publication provides such a treatment for intact skin through the use of a dressing that is applied to an area of the skin. The dressing generally has a rupturable reservoir containing an aqueous hydrogen peroxide composition and a hydrogel layer having a peroxide decomposition catalyst. Unfortunately the catalytic decomposition of hydrogen peroxide to oxygen is quite rapid and so the dressing has a layer that is impermeable to oxygen on the outside so that the oxygen is held against the skin for the maximum time possible. While this dressing is useful for small areas of the skin, it should be clear that it is unworkable for large areas or irregularly shaped areas of skin. 
         [0005]    Alternatively, U.S. Pat. No. 5,736,582 to Devillez proposes the use of hydrogen peroxide in the place of benzoyl peroxide in skin treatment compositions that also contain solvents for hydrogen peroxide. This allows the hydrogen peroxide to stay below a level that will damage the skin and to stay in solution in greater concentrations. A solvent such as dimethyl isosorbide along with water is taught as being effective. No peroxide decomposition catalyst is present. Unfortunately, no data on oxygen concentration or generation are given, nor is the time required for oxygen liberation. While this method appears to be an advance over non-oxygen containing compositions, the lack of data makes it difficult to make objective judgments on the overall effectiveness of this approach. Given the concentrations of peroxide, however, it is doubtful that significant volumes of oxygen were generated. 
         [0006]    There is a need for an easy-to-use way of applying oxygen to wounds to accelerate healing. Such a method and/or product should have relatively few components and be intuitive to use, without the need for special dressings or other awkward requirements. A product that may be used in a manner similar to known products would be most readily accepted by the consumer. 
       SUMMARY 
       [0007]    The problem discussed above has found a solution to a large degree in the present disclosure, which describes the use of a composition of polymeric materials that can foam and contains or generates oxygen. The foam is desirably biodegradable with a weight loss of greater than 10 weight percent in 10 days, desirably without the release of any toxic products from the biodegradation. 
         [0008]    The composition has covalently linked segments of a biodegradable polymer such as but not limited to polycaprolactone, polylactide, polybutylene succinate, polyhydroxy alkanote and mixtures thereof and a polymer hydrogel such as but not limited to polyethylene glycol, polyhydroxylethylmethacrylate, polyacrylamide, polyacrylic acid, carboxylmethyl cellulose, guar gum and mixtures thereof. It is made by the mixing of the two pre-polymers and a cross-linking agent that connects the biodegradable polymer matrix and the hydrogel polymer matrix. One pre-polymer may be an isocyanate terminated polycaprolactone (CAPA) and the second pre-polymer may be a hydroxyl terminated polyethylene glycol (PEG). The cross-linker may be a commercially available aliphatic isocyanate cross-linker. 
         [0009]    The composition forms an oxygen containing foam upon exposure to an oxygen forming chemical, e.g., a solution containing hydrogen peroxide and a catalyst. The catalyst may be chosen from alkali and alkaline earth metals and transition metal oxides. The oxygen containing foam retains oxygen for delivery to, for example, a wound, where it aids in healing. 
     
    
     
       BRIEF DESCRIPTION OF THE DRAWINGS 
         [0010]      FIG. 1  is a representation of the formula of poly(ethylene glycol)-block-poly(8-caprolactone). 
           [0011]      FIG. 2  is a representation of the formula of poly(ethylene glycol)-block-polylactide. 
           [0012]      FIG. 3  is a representation of the formula of poly3-hydroxybutyric acid. 
           [0013]      FIG. 4  is a representation of the formula of poly(D,L-lactide-co-glycolide). 
           [0014]      FIG. 5  is a representation of the formula of poly(sebacic acid). 
           [0015]      FIG. 6  is a representation of the formula of polyphosphazenes. 
           [0016]      FIG. 7  is a representation of the formula of caprolactone diol. 
           [0017]      FIG. 8  is a representation of an idealized structural formula of OH Functional prepolymer. 
           [0018]      FIG. 9  is a representation of the formula of NCO prepolymer. 
           [0019]      FIG. 10  is a representation of the formula of caprolactone Triol cross-linker. 
           [0020]      FIG. 11  is a representation of the formula of poly(lactide diol). 
           [0021]      FIG. 12  is a representation of the formula of poly(ethylene glycol). 
           [0022]      FIG. 13  is a representation of the formula of trimethylene carbonate(1,3-Dioxan-2-one). 
           [0023]      FIG. 14  is a representation of the formula of caprolactone. 
           [0024]      FIG. 15  is a representation of the formula of hydroxybutyric acid glycerol ester. 
       
    
    
     DETAILED DESCRIPTION 
       [0025]    Reference will now be made in detail to one or more embodiments of the invention, examples of the invention, examples of which are illustrated in the drawings. Each example and embodiment is provided by way of explanation of the invention, and is not meant as a limitation of the invention. For example, features illustrated or described as part of one embodiment may be used with another embodiment to yield still a further embodiment. It is intended that the invention include these and other modifications and variations as coming within the scope and spirit of the invention. 
         [0026]    We have synthesized six individual polymer segments and covalently linked them to form the desired polymer matrix. Biodegradation assays confirmed the polyethylene glycol based matrix and the polycaprolactone based matrix each met the biodegradation goal. The oxygen concentration analysis suggested the foam had 25 ppm of oxygen delivered within 24 hours. 
         [0027]    We have made improvements towards foam forming ability to the polymer matrix by adding hydrocolloids which includes but not limited to guar gum and polyvinyl pyrrolidone. The oxygen concentration analysis of the foam obtained from the improved foam forming formulations was also found to contain 25 ppm of oxygen. 
         [0028]    Based on our detailed understanding of the structure-activity relationship reported in the literature, we selected the top biodegradable polymer segments that could possibly meet the biodegradability and biocompatibility criteria for the polymer matrix. These are poly(ethylene glycol)-block-poly(8-caprolactone), with a structure shown in  FIG. 1 ; poly(ethylene glycol)-block-polylactide,  FIG. 2 ; poly3-hydroxybutyric acid,  FIG. 3 ; poly(D,L-lactide-co-glycolide)  FIG. 4 ; poly(sebacic acid),  FIG. 5 ; and polyphosphazenes,  FIG. 6 . 
         [0029]    One of the most important criteria is that the biodegradable polymer matrix should be capable of holding a catalyst and swell in 20 weight percent hydrogen peroxide mixture. The peroxide swollen polymer when exposed to elevated temperature (&gt;60 deg C) should decompose the peroxide and yet retain the oxygen released in the resultant foam. Furthermore, the foam should deliver the oxygen when it is sufficiently moistened. 
         [0030]    In order to meet the requirements, the synthetic biodegradable polymer matrix should contain at least two polymer segments wherein the first polymer segment provides biodegradability and the second polymer segment provides foam forming ability, as well as augmenting biodegradability. Studying and understanding the structure-property relationship led us to conceptualize the potential candidate polymers listed in Table 1. 
         [0000]    
       
         
               
               
               
               
             
           
               
                 TABLE 1 
               
               
                   
               
               
                 Backbone 
                 Polymer 
                 Commercial 
                 Ionomer Choice 
               
               
                 Functionality 
                 Precursor 
                 Availability 
                 (Ionic segments) 
               
               
                   
               
             
             
               
                 Caprolactone 
                 Hydroxyl terminated 
                 Yes. 
                 Carboxyl (e.g. 
               
               
                   
                 poly(caprolactone) 
                 Available in 
                 dimethylol 
               
               
                   
                 diols 
                 different 
                 propionic acid, 
               
               
                   
                   
                 molecular weight 
                 commercially 
               
               
                   
                   
                 and hydroxyl 
                 available) 
               
               
                   
                   
                 number 
               
               
                 Ethylene 
                 Hydroxyl terminated 
                 Yes. Same 
                 Sulfonic acid 
               
               
                 oxide 
                 Poly(ethylene oxide) 
                 as above 
               
               
                 Hydroxy 
                 Formation of ester 
                 No. Two step 
                 Phosphonic acid 
               
               
                 butyric 
                 diol by reacting 
                 process and HBA 
               
               
                 acid (HBA) 
                 HBA and ethylene 
                 has limited 
               
               
                   
                 glycol followed by 
                 supply. 
               
               
                   
                 esterification 
               
               
                   
                 with diacids 
               
               
                 Lactic acid 
                 Same as above 
                 No. Two step 
               
               
                   
                   
                 process. Cheaper 
               
               
                   
                   
                 compared to HBA 
               
               
                 Sebacic Acid 
                 Formation of 
                 No. One step 
               
               
                   
                 Hydroxyl 
                 process 
               
               
                   
                 terminated sebacic 
               
               
                   
                 acid esters 
               
               
                 Aspartic 
                 Poly(aspartic acid) 
                 Yes. Cannot be 
               
               
                 Acid 
                   
                 used as oligomer 
               
               
                   
                   
                 for polymer 
               
               
                   
                   
                 formation but 
               
               
                   
                   
                 could be used to 
               
               
                   
                   
                 form degradable 
               
               
                   
                   
                 crosslinking sites 
               
               
                   
               
             
          
         
       
     
         [0031]    The polymer precursors and the ionomers listed above in Table 1 provide the biodegradability and foam foaming ability to the polymer matrix. They could be covalently linked to form a swellable biodegradable polymer matrix in 20% hydrogen peroxide solution. We have used isocyanate precursors to link the segmented biodegradable polymer for proof of principle demonstration. Details of the test plan are provided as follows: 
       Caprolactone Urethane Work Plan 
       [0032]    A. Category: Thermoplastic or Thermoset 
       Materials: 
       [0033]    Caprolactone diol,  FIG. 7 , e.g., PERSTORP CAPA 2054, PERSTORP CAPA 2205. 
         [0034]    OH Functional prepolymer,  FIG. 8 , idealized structure example. NCO prepolymer,  FIG. 9 . 
         [0035]    Caprolactone Triol cross-linker,  FIG. 10 , e.g. PERSTORP CAPA 3031. 
         [0000]    Variables: 1) Caprolactone Diol molecular weight
       a) CAPA 2054 (550 MW)
           i) 90% of diol wt   ii) 75% of diol wt   iii) 50% of diol wt   
           b) CAPA 2205 (2000 MW)
           i) 90% of diol wt   ii) 75% of diol wt   iii) 50% of diol wt   
           2) Loading of Carboxylic acid functional Urethane diol
           i) 10% of diol wt   ii) 25% of diol wt   iii) 50% of diol wt   
           3) Crosslinker concentration
           a) CAPA 3031 (300 MW)
               i) 5% solids wt   ii) 10% solids wt   iii) 15% solids wt   
               Other options:   b) 1,1,1-Tris hydroxymethyl propane (TMP)   c) Poly(aspartic acid) biodegradable crosslinker   
               
 
       Constants: 1) NCO Prepolymer 
       [0000]    
       
         
           
             2) Isocyanate to hydroxyl ratio 1.1/1 
             3) Solvent NMP 
             4) Curing Temperature and Humidity 
           
         
       
     
       Matrix: 
       [0059]      
         [0000]    
       
         
               
               
               
               
               
             
               
               
               
               
               
             
           
               
                   
               
               
                   
                   
                   
                 Diol 
                   
               
               
                   
                   
                   
                 Carboxylic Acid 
                 Crosslinker 
               
               
                   
                 Diol 
                 Diol 
                 Functional 
                 Triol 
               
               
                 Formulation: 
                 CAPA 2054 
                 CAPA 2205 
                 Urethane Diol 
                 CAPA 3031 
               
               
                   
               
             
             
               
                   
               
             
          
           
               
                 1 
                   
                 90% of diol wt 
                 10% of diol wt 
                 5% solids wt 
               
               
                 2 
                   
                 75% of diol wt 
                 25% of diol wt 
                 5% solids wt 
               
               
                 3 
                   
                 50% of diol wt 
                 50% of diol wt 
                 5% solids wt 
               
               
                 4 
                   
                 90% of diol wt 
                 10% of diol wt 
                 10% solids wt 
               
               
                 5 
                   
                 75% of diol wt 
                 25% of diol wt 
                 10% solids wt 
               
               
                 6 
                   
                 50% of diol wt 
                 50% of diol wt 
                 10% solids wt 
               
               
                 7 
                   
                 90% of diol wt 
                 10% of diol wt 
                 15% solids wt 
               
               
                 8 
                   
                 75% of diol wt 
                 25% of diol wt 
                 15% solids wt 
               
               
                 9 
                   
                 50% of diol wt 
                 50% of diol wt 
                 15% solids wt 
               
               
                 10 
                 90% of diol wt 
                   
                 10% of diol wt 
                 5% solids wt 
               
               
                 11 
                 75% of diol wt 
                   
                 25% of diol wt 
                 5% solids wt 
               
               
                 12 
                 50% of diol wt 
                   
                 50% of diol wt 
                 5% solids wt 
               
               
                 13 
                 90% of diol wt 
                   
                 10% of diol wt 
                 10% solids wt 
               
               
                 14 
                 75% of diol wt 
                   
                 25% of diol wt 
                 10% solids wt 
               
               
                 15 
                 50% of diol wt 
                   
                 50% of diol wt 
                 10% solids wt 
               
               
                 16 
                 90% of diol wt 
                   
                 10% of diol wt 
                 15% solids wt 
               
               
                 17 
                 75% of diol wt 
                   
                 25% of diol wt 
                 15% solids wt 
               
               
                 18 
                 50% of diol wt 
                   
                 50% of diol wt 
                 15% solids wt 
               
               
                   
               
             
          
         
       
     
       Poly(lactic Acid)Diol Urethane Work Plan 
       [0060]    B. Category: Thermoplastic 
       Materials: 
       [0061]    Poly(lactide diol),  FIG. 11 . 
         [0062]    OH Functional prepolymer,  FIG. 8 , idealized structure example. 
         [0063]    NCO prepolymer,  FIG. 9 . 
         [0000]    Variables: 1) Poly(Lactide diol)
       i) 90% of diol wt   ii) 75% of diol wt   iii) 50% of diol wt   2) Loading of Carboxylic acid functional Urethane diol
           i) 10% of diol wt   ii) 25% of diol wt   iii) 50% of diol wt
 
Constants: 1) NCO prepolymer
   
           2) Isocyanate to hydroxyl ratio   3) Solvent NMP   4) Temperature and humidity       
 
       Matrix: 
       [0074]      
         [0000]                                                Diol                   Carboxylic Acid           Diols   Functional   Crosslinker       Formulation:   Poly(lactide diol)   Urethane Diol   CAPA 3031                   1   90% of diol wt   10% of diol wt   5% solids wt       2   75% of diol wt   25% of diol wt   5% solids wt       3   50% of diol wt   50% of diol wt   5% solids wt       4   90% of diol wt   10% of diol wt   10% solids wt       5   75% of diol wt   25% of diol wt   10% solids wt       6   50% of diol wt   50% of diol wt   10% solids wt       7   90% of diol wt   10% of diol wt   15% solids wt       8   75% of diol wt   25% of diol wt   15% solids wt       9   50% of diol wt   50% of diol wt   15% solids wt                    
Poly(ethylene glycol)Urethane Work Plan
 
         [0075]    C. Category: Thermoplastic or Thermoset 
       Materials: 
       [0076]    Poly(ethylene glycol),  FIG. 12 , Aldrich 600 MW, Aldrich 2000, MW. 
         [0077]    OH Functional prepolymer,  FIG. 8 , idealized structure example. 
         [0078]    NCO prepolymer,  FIG. 9 . 
         [0079]    Caprolactone Triol cross-linker,  FIG. 10 , e.g. PERSTORP CAPA 3031. 
         [0000]    Variables: 1) Poly(ethylene glycol) molecular weight
       a) PEG (600 MW)
           i) 90% of diol wt   ii) 75% of diol wt   iii) 50% of diol wt   
           b) PEG (2000 MW)
           i) 90% of diol wt   ii) 75% of diol wt   iii) 50% of diol wt   
           2) Loading of Carboxylic acid functional Urethane diol
           a) 10% of diol wt   b) 25% of diol wt   c) 50% of diol wt   
           3) Crosslinker concentration
           a) CAPA 3031 (300 MW)
               i) 5% solids wt   ii) 10% solids wt   iii) 15% solids wt   
               Other options:   b) 1,1,1-Tris hydroxymethyl propane (TMP)   c) Poly (aspartic acid)   
               
 
       Constants: 1) NCO Prepolymer 
       [0000]    
       
         
           
             2) Isocyanate to hydroxyl ratio 1.1/1 
             3) Solvent NMP 
             4) Curing Temperature and Humidity 
           
         
       
     
       Matrix: 
       [0103]      
         [0000]                                                                              Diol                       Carboxylic Acid           Diol   Diol   Functional   Crosslinker Triol       Formulation:   PEG 600   PEG 2000   Urethane Diol   CAPA 3031                                1       90% of diol wt   10% of diol wt   5% solids wt       2       75% of diol wt   25% of diol wt   5% solids wt       3       50% of diol wt   50% of diol wt   5% solids wt       4       90% of diol wt   10% of diol wt   10% solids wt       5       75% of diol wt   25% of diol wt   10% solids wt       6       50% of diol wt   50% of diol wt   10% solids wt       7       90% of diol wt   10% of diol wt   15% solids wt       8       75% of diol wt   25% of diol wt   15% solids wt       9       50% of diol wt   50% of diol wt   15% solids wt       10   90% of diol wt       10% of diol wt   5% solids wt       11   75% of diol wt       25% of diol wt   5% solids wt       12   50% of diol wt       50% of diol wt   5% solids wt       13   90% of diol wt       10% of diol wt   10% solids wt       14   75% of diol wt       25% of diol wt   10% solids wt       15   50% of diol wt       50% of diol wt   10% solids wt       16   90% of diol wt       10% of diol wt   15% solids wt       17   75% of diol wt       25% of diol wt   15% solids wt       18   50% of diol wt       50% of diol wt   15% solids wt                    
Bio-degradable Hydrogels from Ring Opening Polymerization
 
         [0104]    D. Category: Thermoplastic (Ring Opening Polymerization) 
       Materials: 
       [0105]    Trimethylene carbonate(1,3-Dioxan-2-one),  FIG. 13 . 
         [0106]    Caprolactone,  FIG. 14 . 
         [0107]    Hydroxybutyric acid glycerol ester,  FIG. 15 . 
       Experimental: 
       [0108]    Ring opening polymerization of TMC or CL using Tin(II) 2-ethylhexanoate (catalyzed), with dimethylol propionic acid (DMPA) 
       Variables: 1) TMC 
       [0000]    
       
         
           
             2) CL 
             3) DMPA
 
Constants: 1) Catalyst concentration
 
             2) Solvent 
             3) Temperature 
             4) Polymerization time 
           
         
       
     
       Hydroxybutyric Acid Urethane Work Plan 
       [0114]    E. Category: Thermoplastic 
       Materials: 
       [0115]    Hydroxybutyric acid glycerol ester,  FIG. 15 . 
         [0116]    OH Functional prepolymer,  FIG. 8 , idealized structure example. 
         [0117]    NCO prepolymer,  FIG. 9 . 
         [0118]    Caprolactone Triol cross-linker,  FIG. 10 , e.g. PERSTORP CAPA 3031. 
         [0000]    Variables: 1) Hydroxybutyric acid glycol ester
       i) 90% of diol wt   ii) 75% of diol wt   iii) 50% of diol wt   2) Loading of Carboxylic acid functional Urethane diol
           i) 10% of diol wt   ii) 25% of diol wt   iii) 50% of diol wt   iv)
 
Constants: 1. NCO prepolymer
   
           2. Isocyanate to hydroxyl ratio 1.1/1   3. Solvent NMP   4. Curing temperature and humidity       
 
       Matrix: 
       [0130]      
         [0000]    
       
         
               
               
               
               
             
           
               
                   
               
               
                   
                   
                 Diol 
                   
               
               
                   
                   
                 Carboxylic Acid 
               
               
                   
                 Diols 
                 Functional 
                 Crosslinker 
               
               
                 Formulation: 
                 Poly(lactide diol) 
                 Urethane Diol 
                 CAPA 3031 
               
               
                   
               
             
             
               
                 1 
                 90% of diol wt 
                 10% of diol wt 
                 5% solids wt 
               
               
                 2 
                 75% of diol wt 
                 25% of diol wt 
                 5% solids wt 
               
               
                 3 
                 50% of diol wt 
                 50% of diol wt 
                 5% solids wt 
               
               
                 4 
                 90% of diol wt 
                 10% of diol wt 
                 10% solids wt 
               
               
                 5 
                 75% of diol wt 
                 25% of diol wt 
                 10% solids wt 
               
               
                 6 
                 50% of diol wt 
                 50% of diol wt 
                 10% solids wt 
               
               
                 7 
                 90% of diol wt 
                 10% of diol wt 
                 15% solids wt 
               
               
                 8 
                 75% of diol wt 
                 25% of diol wt 
                 15% solids wt 
               
               
                 9 
                 50% of diol wt 
                 50% of diol wt 
                 15% solids wt 
               
               
                   
               
             
          
         
       
     
         [0131]    The caprolactone polyol (CAPA) and acid functionalized prepolymers were mixed with 0.5 wt. % sodium carbonate and reacted with a commercially available isocyanate prepolymer to produce a biodegradable polymer composition (Table 2). The samples were soaked in 20 wt. % hydrogen peroxide and exposed to 50° C. for 2 hours to obtain oxygen containing polymer foams. It was observed that the polymer matrix did not swell in hydrogen peroxide and eventually did not foam. We believe this could be due to the ionomer concentration on the polymer backbone was not sufficient enough to result in a hydrogel matrix. We could mitigate this challenge by either increasing the ionomer concentration or reducing the molecular weight of CAPA segments. 
         [0000]                                  TABLE 2                   CAPA polymer composition.                    PolyIsocyanate               (Tolonate HDT)       Sample Reference   Prepolymer   wt. %               53424-16-2   50% 550MW CAPA; 50% Acid    5%           Functional Diol       53424-16-3   50% 550MW CAPA; 50% Acid   10%           Functional Diol       53424-16-4   75% 550MW CAPA; 25% Acid    5%           Functional Diol       53424-16-5   75% 550MW CAPA; 25% Acid   10%           Functional Diol       53424-16-6   50% 2,000MW CAPA; 50% Acid    5%           Functional Diol       53424-16-7   50% 2,000MW CAPA; 50% Acid   10%           Functional Diol       53424-16-8   75% 2,000MW CAPA; 25% Acid    5%           Functional Diol       53424-16-9   75% 2,000MW CAPA; 25% Acid   10%           Functional Diol                    
All formulations had 0.5 wt. % sodium carbonate
 
         [0132]    The biodegradation analysis of this polymer matrix was conducted and showed more than 10% weight loss after 10 days ( FIG. 2 ). It was interesting to see the higher ionomer concentration enhanced the rate of biodegradability. This increase in ionomer concentration increased the number of hydration sites that made the environment more conducive for biodegradation. The increase of CAPA molecular weight had no effect on the rate of biodegradation. One might expect the higher molecular weight would have more hydrolyzing repeat units per mole and therefore result in higher biodegradability compared to a low molecular weight CAPA segment. We believe the crosslink density of the polymer matrix was high enough to offset these molecular weight effects. 
         [0133]    Polymer Matrix Derived From Polyethylene Glycol and Acid Functionalized Prepolymer 
         [0134]    The biodegradable polymer containing the polyethylene glycol (PEG) segments was synthesized according to the scheme illustrated in  FIG. 3 . The details of the synthesis and characterization of this polymer matrix are: 
         [0135]    (1) 50% PEG (2000 MW)/50% Acid Functional Precursor 
         [0136]    In a 500 mL round bottom flask fitted with a thermocouple, a water cooled condenser, overhead stirrer, argon inlet for purge, a heating mantle, and fitted with an addition funnel, charge carboxylic acid urethane diol 53424-6-10 (20.4 grams), and polyethylene glycol diol (10.00 grams) then rinse it in with Methyl Ethyl Ketone (23.4 grams). Heat the mixture gently to 60° C., under argon purge, while mixing. Rinse Dibutyl tin dilaurate (0.0102 grams) into the reactor. Fill the addition funnel with Isophorone diisocyanate “IPDI” (3.10 grams). Then begin drop wise addition of the IPDI and control the addition to finish about 1 hour later. 
         [0137]    (2) 75% PEG (2000 MW)/25% Acid Functional Precursor 
         [0138]    In a 500 mL round bottom flask fitted with a thermocouple, a water cooled condenser, overhead stirrer, argon inlet for purge, a heating mantle, and fitted with an addition funnel, charge carboxylic acid urethane diol 53424-6-10 (20.60 grams), and polyethylene glycol diol (30.00 grams) then rinse it in with Methyl Ethyl Ketone (44.50 grams). Heat the mixture gently to 60° C., under argon purge, while mixing. Rinse Dibutyl tin dilaurate (0.0048 grams) into the reactor. Fill the addition funnel with Isophorone diisocyanate “IPDI” (5.10 grams). Then begin drop wise addition of the IPDI and control the addition to finish about 1 hour later. 
         [0139]    (3) 50% PEG (600W)/50% Acid Functional Precursor 
         [0140]    In a 500 mL round bottom flask fitted with a thermocouple, a water cooled condenser, overhead stirrer, argon inlet for purge, a heating mantle, and fitted with an addition funnel, charge carboxylic acid urethane diol 53424-6-10 (20.40 grams), and polyethylene glycol diol (10.01 grams) then rinse it in with Methyl Ethyl Ketone (27.1 grams). Heat the mixture gently to 60° C., under argon purge, while mixing. Rinse Dibutyl tin dilaurate (0.0069 grams) into the reactor. Fill the addition funnel with Isophorone diisocyanate “IPDI” (7.30 grams). Then begin drop wise addition of the IPDI and control the addition to finish about 1 hour later. 
         [0141]    (4) 75% PEG (600W)/25% Acid Functional Precursor 
         [0142]    In a 500 mL round bottom flask fitted with a thermocouple, a water cooled condenser, overhead stirrer, argon inlet for purge, a heating mantle, and fitted with an addition funnel, charge carboxylic acid urethane diol 53424-6-10 (20.50 grams), and polyethylene glycol diol (10.21 grams) then rinse it in with Methyl Ethyl Ketone (30.35 grams). Heat the mixture gently to 60° C., under argon purge, while mixing. Rinse Dibutyl tin dilaurate (0.0101 grams) into the reactor. Fill the addition funnel with Isophorone diisocyanate “IPDI” (10 grams). Then begin drop wise addition of the IPDI and control the addition to finish about 1 hour later. 
         [0143]    (5) Peroxide Swelling Procedure
       1) Weigh each sample   2) Prepare 20% hydrogen peroxide solution by diluting 30% with distilled water   3) Pour enough hydrogen peroxide into a beaker so that the sample is submerged   4) Remove the sample at intervals, blot dry and record the weight   5) Calculate the percent hydration       
 
         [0149]    The polyethylene glycol based urethanes hydrated faster than the CAPA urethanes. There was a distinct trend of increasing hydration rate with PEG molecular weight and decreased crosslinker concentration. 
         [0150]    (6) Dimensional Change with Swelling Procedure
       1) Cut each sample with a ¾ inch diameter round sample punch   2) Prepare 20% hydrogen peroxide solution by diluting 30% with distilled water   3) Pour enough hydrogen peroxide into a beaker so that the sample is submerged   4) Remove the sample at intervals, blot dry and record the diameter   5) Calculate the swelling % change       
 
         [0156]    The final dimensional increase was compared to the two hour hydration percent for a number of PEG based samples. The samples that hydrate the most will swell the most in peroxide. This is understandable and helps to validate the hydration data. 
         [0157]    The PEG diol and acid functionalized prepolymers were mixed with 0.5 wt. % sodium carbonate and reacted with isocyanate prepolymer to produce biodegradable polymer composition. The polymer matrix obtained had significant swelling (Table 3) and the hydration rate increased with the increasing molecular weight of PEG segment. Since these polymers had a high hydration rate, their mechanical properties in the hydrogel state were inadequate. We believe this could be easily improved by optimizing the hydrophilic character of the polymers and increasing the crosslink density of the polymer. The swollen polymer on exposure to heat did not foam. This was surprising as we expected the sodium carbonate present in the swollen polymer matrix would decompose hydrogen peroxide at elevated temperature and release oxygen which would result in the foaming of the polymer matrix. 
         [0158]    We speculate that either the acid based ionomer might have neutralized the catalyst (sodium carbonate) that is necessary to decompose hydrogen peroxide to form oxygen or the isocyanate precursor might have reacted with the carbonates. In order to validate our hypothesis, the sodium carbonate concentration in the resultant polymer matrix was analyzed and compared with initial theoretical loading of sodium carbonate as follows: 
       Titration of Sodium Carbonate 
       [0159]    In order to gauge any interference of the sodium carbonate with residual isocyanate in the urethane, titrations were performed. CAPA-PEG hybrid urethane with 1% crosslinker was formulated with 9.09% sodium carbonate. The sample was cured and cut into pieces of known mass. These pieces, as well as neat sodium carbonate powder, were titrated against HCl to neutralize the sodium carbonate. The method consists of weighing a sample approx. 3-4 g into an Erlenmeyer flask equipped with a magnetic stirrer, and dissolve in 30 mL toluene; close the flask and set on the magnetic stirrer for 10 min so reaction can proceed. Charge 20 mL of Methanol and titrate with HCl to reach a pH of 4. Repeat in triplicate and average the results. The standard deviations overlap, thus suggesting that there is no interference of the isocyanate with the catalyst. 
       Titrino Autotitrator 
       [0000]    
       
         
           
             Titrant: HCl=1 mol/L in methanol 
             Solvents: Toluene and methanol 
             Magnetic Swing-out Stirrer 
             Exchange units 
             Solvotrode Electrode
 
Method: Reference MetroOhm application bulletin No. 200/2 e
 
           
         
       
     
         [0165]    We could not, however, find any convincing evidence for sodium carbonate neutralization with the acid containing ionomer nor by reacting with the isocyanate prepolymer. 
         [0000]    
       
         
               
             
               
               
               
               
               
               
               
             
               
               
               
               
               
               
               
               
               
             
               
               
               
               
               
               
               
               
               
             
           
               
                 TABLE 3 
               
             
             
               
                   
               
               
                 Degree of swelling (or nominal hydration) of polymer matrix derived 
               
               
                 from polyethylene glycol and acid functionalized prepolymer. 
               
             
          
           
               
                   
                   
                   
                   
                   
                   
                 Nominal Hydration 
               
               
                   
                 53424-18 
                 53424-19 
                 53424-20 
                 53424-21 
                   
                 (%) at specified 
               
               
                   
                 600 MW 
                 600 MW 
                 2000 MW 
                 2000 MW 
                 Tolonate 
                 time intervals 
               
             
          
           
               
                 Sample 
                 PEG 50/50 
                 PEG 75/25 
                 PEG 50/50 
                 PEG 75/25 
                 HDT 
                 20 
                 60 
                 120 
               
               
                 Reference 
                 (PEG/pre) 
                 (PEG/pre) 
                 (PEG/pre) 
                 (PEG/pre) 
                 (PolyNCO) 
                 min 
                 min 
                 min 
               
               
                   
               
             
          
           
               
                 53424-22-1 
                 x 
                   
                   
                   
                  (5%) 
                 11 
                 21 
                 28 
               
               
                 53424-22-2 
                 x 
                   
                   
                   
                 (10%) 
                 14 
                 25 
                 28 
               
               
                 53424-22-4 
                   
                 x 
                   
                   
                 (10%) 
                 55 
                 72 
                 71 
               
               
                 53424-22-5 
                   
                   
                 x 
                   
                  (5%) 
                 52 
                 81 
                 93 
               
               
                 53424-22-6 
                   
                   
                 x 
                   
                 (10%) 
                 47 
                 59 
                 65 
               
               
                 53424-22-7 
                   
                   
                   
                 x 
                  (5%) 
                 80 
                 152 
                 213 
               
               
                   
               
             
          
         
       
     
         [0166]    The PEG based polymer showed approximately 20% weight reductions after 10 days. As seen in the CAPA based polymer, the rate of biodegradability of the PEG based polymer increased with higher hydrophilic concentration of the PEG segments. Overall the PEG based polymer showed a higher rate of biodegradation compared to the CAPA based polymer. 
       Polymer Matrix Derived From Caprolactone Polyol and Polyethylene Glycol 
       [0167]    Segmented copolymers containing CAPA and PEG segments are unique and not commercially available. In order to form a polymer matrix with both CAPA and PEG segments, CAPA based isocyanate precursors and PEG based hydroxyl precursors were individually synthesized and reacted together to form a segmented biodegradable matrix. A representative formulation is provided in Table 4. The details of the synthesis are as follows: 
       Details of Synthesis and Characterization of Polymer Matrix Derived From CAPA and PEG Segments 
     PEG Based Hydroxyl Precursor (PEG-IPDI-PEG) 
     53424-43-34 Method: 
       [0168]    In a 250 mL roundbottom flask fitted with a thermocouple, a water cooled condenser, overhead stirrer, argon inlet for purge, a heating mantle, and fitted with an addition funnel, charge Poly(ethylene glycol) (2,000 MW 75.00 grams) rinse it in with methyl ethyl ketone “MEK” (65.00 grams), Dibutyl tin Dilaurate (0.0898 grams) then rinse in with MEK (5.36 grams). Heat the mixture gently to 60° C., under argon purge, while mixing, until the solids dissolve. Fill the addition funnel with Isophorone diisocyanate “IPDI” (40.4 grams). Then begin drop wise addition of the IPDI and finish the addition after 1 hour. Rinse in with more MEK (25.02 grams). Allow the reaction to mix at 60° C. for another hour. Shut off heater, and cool to room temperature while mixing overnight. 
       CAPA Based Isocyanate Precursor (IPDI-CAPA-IPDI) 
     53424-42-34 Method: 
       [0169]    In a 250 mL roundbottom flask fitted with a thermocouple, a water cooled condenser, overhead stirrer, argon inlet for purge, a heating mantle, and fitted with an addition funnel, charge Caprolactone Diol (550 MW 50.24 grams), Dibutyl tin Dilaurate (0.0931 grams) then rinse it in with methyl ethyl ketone “MEK” (65 grams). Heat the mixture gently to 60° C., under argon purge, while mixing, until the solids dissolve. Fill the addition funnel with Isophorone diisocyanate “IPDI” (40.4 grams). Then begin drop wise addition of the IPDI and finish the addition after 1 hour. Rinse in with more MEK (25.02 grams). Allow the reaction to mix at 60° C. for another hour. Shut off heater, and cool to room temperature while mixing overnight. 
       CAPA PEG Hybrid Urethane Formulation 
     53424-74-20 Method: 
       [0170]    In a 1 L reactor fitted with a thermocouple, a water cooled condenser, overhead stirrer, argon inlet for purge, a heating mantle, and fitted with an addition funnel, charge CAPA based Isocyanate Precursor (200.05 grams), Dibutyl tin Dilaurate (0.51 grams) then rinse it in with methyl ethyl ketone “MEK” (251.76 grams). Charge in PEG Based Hydroxyl Precursor (299.95 grams) and rinse in with MEK (255.37 grams). Heat the mixture gently to 60° C., under argon purge, while mixing. Allow the reaction to mix at 60° C. for 1 hour. Shut off heater, and cool to room temperature while mixing overnight. The solution will be very viscous. Charge in Tolonate HDT (2.5 grams), followed by more MEK (102.02 grams). Formulate as needed with catalyst. 
       Peroxide Swelling Procedure 
       [0000]    
       
         1) Weigh each sample 
         2) Prepare 20% hydrogen peroxide solution by diluting 30% with distilled water 
         3) Pour enough hydrogen peroxide into a beaker so that the sample is submerged 
         4) Remove the sample at intervals, blot dry and record the weight 
         5) Calculate the percent hydration 
       
     
       Hydration Time Correlation to CAPA/PEG Hybrid Formulation 
       [0176]    A series of CAPA/PEG hybrid formulations were prepared at different ratios of isocyanate and hydroxyl precursor weight ratios; specifically at ratios of 20/80, 40/60, and 60/40. These formulations correspond to isocyanate/hydroxyl equivalent ratios. Their time to 50% hydration was calculated, and compared to their respective isocyanate to hydroxyl equivalent ratio. The trend observed suggests that the more polyethylene glycol in the formulation, the faster it hydrates. 
         [0000]    
       
         
               
             
               
               
               
               
             
           
               
                 TABLE 4 
               
             
             
               
                   
               
               
                 Polymer matrix formulations based on CAPA and PEG segments. 
               
             
          
           
               
                   
                   
                 Polyisocanate 
                 Sodium 
               
               
                   
                   
                 (Tolonate HDT) 
                 Carbonate 
               
               
                 Sample Ref. 
                 Prepolymer  1   
                 wt. %  2   
                 wt. %  3   
               
               
                   
               
               
                 53424-56-13 
                 40% 550MW CAPA; 60% 
                 3 
                 2 
               
               
                   
                 2000MW PEG Diol 
               
               
                 53424-56-24 
                 40% 550MW CAPA; 60% 
                 1 
                 2 
               
               
                   
                 2000MW PEG Diol 
               
               
                   
               
               
                   1  Prepolymers were synthesized by reacting specified diols with isophorone diisocyanate at NCO/OH ratio of 2:1 for CAPA and 0.5:1 for PEG 
               
               
                   2  Polyisocyanate was added based on prepolymer solids. 
               
               
                   3  Sodium carbonate was added based on total solids and it was ground and sieved to less than 53 microns before mixing. 
               
             
          
         
       
     
         [0177]    The polymer matrix based on CAPA and PEG did swell in 20% hydrogen peroxide solution and showed good foam forming ability after thermal exposure. Oxygen analysis of these foams and the results are reported in Table 5. 
         [0000]    
       
         
               
             
               
               
               
             
           
               
                 TABLE 5 
               
             
             
               
                   
               
               
                 Oxygen concentration results of polymer matrix 
               
               
                 derived from CAPA and PEG segments. 
               
             
          
           
               
                   
                 Lot ID 
                 Total O 2  Delivery 24 hour (ppm) 
               
               
                   
                   
               
               
                   
                 53424-56-13 
                 25.3 
               
               
                   
                 53424-56-24 
                 25.1 
               
               
                   
                 53424-66-22 
                 24.4 
               
               
                   
                   
               
             
          
         
       
     
         [0178]    It was observed that the total oxygen delivery was only 25 ppm over a period of 24 hours. It was speculated that the foam samples may have open cells and therefore did not retain enough oxygen in the matrix. In order to investigate the morphology of the foam samples, SEM investigation was performed. The experimental biodegradable foam samples have a discrete structure with no evidence of expanded foam structure. 
       Polymer Matrix Formulated with Additives for Making Closed Cell Polymer Foam 
       [0179]    This more openness in the foam structure is possibly due to one or both of the following factors:
       (a) Higher foam rigidity or lack of foam coalescence   (b) Rate of decomposition of peroxide is much faster than foam relaxation       
 
         [0182]    The following technical approaches were attempted to address the above challenges: 
         [0183]    (a) Approach 1: Use of Guar Gum 
         [0184]    Guar gum is a natural polymer adhesive. Incorporating Guar gum in the formulation is expected to lower the foam rigidity and enhance foam coalescence. It was incorporated directly into the polymer matrix at various levels and was also first coated onto sodium carbonate (encapsulating sodium carbonate with the additives first) followed by dispersing them into the polymer matrix. The formulations obtained from this approach are provided in Table 6 and the experimental details are as follows: 
       Details of Polymer Matrix Formulated with Alternative Catalysts to Make Closed Cell Polymer Foam 
     CAPA-PEG Hybrid with 50/50 Guar Gum 
       [0185]    Take sodium carbonate (10.0 grams) and dissolve into distilled water (50 grams). After dissolving charge Hercules Supercol U Guar Gum (10.0 grams). Mix vigorously to hydrate thoroughly. The mixture will form a thick paste within a minute, and continue mixing until the consistency is uniform. Let it sit for a half hour to allow any clumps to hydrate evenly. Place in a vacuum oven 60° C. overnight to obtain dry solids. Grind the solids the next day with mortar and pestle and sieve to less than 106 μm. 
         [0186]    Take 59.93 grams of 53424-74-10 (40% 550 MW CAPA; 60% 2000 MW PEG Diol) and mix in 0.503 grams of 50/50 Guar Gum. Cast into a 5×5 Teflon mold and air dry. Note: this appeared to gel faster than the urethane alone. 
       CAPA-PEG Hybrid with 67/33 Guar Gum 
       [0187]    Take sodium carbonate (10.0 grams) and dissolve into distilled water (50 grams). After dissolving, charge Hercules Supercol U Guar Gum (5.0 grams). Mix vigorously to hydrate thoroughly. The mixture will form a thick paste within a minute, and continue mixing until the consistency is uniform. Let it sit for a half hour to allow any clumps to hydrate evenly. Place in a vacuum oven 60° C. overnight to obtain dry solids. Grind the solids the next day with mortar and pestle and sieve to less than 106 μm. 
         [0188]    Take 60.02 grams of 53424-74-10 (40% 550 MW CAPA; 60% 2000 MW PEG Diol) and mix in 0.377 grams of 567/33 Guar Gum. Cast into a 5×5 Teflon mold and air dry. 
       Peroxide Swelling Procedure 
       [0000]    
       
         1) Weigh each sample 
         2) Prepare 20% hydrogen peroxide solution by diluting 30% with distilled water 
         3) Pour enough hydrogen peroxide into a beaker so that the sample is submerged 
         4) Remove the sample at intervals, blot dry and record the weight 
         5) Calculate the percent hydration 
       
     
         [0000]    
       
         
               
             
               
               
             
           
               
                 TABLE 6 
               
             
             
               
                   
               
               
                 Formulations based on guar gum. 
               
             
          
           
               
                 Sample Ref. 
                 Comments 
               
               
                   
               
               
                 53424-78-25 
                 Control 
               
               
                 53424-80-10 
                 Mixed Guar gum with catalyst (50/50 wt. %) 
               
               
                 53424-80-20 
                 Mixed Guar gum with catalyst (33/67 wt. %) 
               
               
                 53424-81-11 
                 Mixed Guar gum with catalyst (50/50 wt. %) and placed 
               
               
                   
                 the catalyst in between two PU films 
               
               
                 53424-81-20 
                 Mixed Guar gum with catalyst (33/67 wt. %) and placed 
               
               
                   
                 the catalyst in between two PU films 
               
               
                   
               
             
          
         
       
       
         
           
             Catalyst used was sodium carbonate 2 wt. % based on prepolymer solids 
             Crosslinker used was Tolonate HDT 1 wt. % based on prepolymer solids 
             Prepolymer comprised of 40% 550 MW CAPA; 60% 2,000 MW PEG Diol 
           
         
       
     
         [0197]    (b) Approach 2: Replacement for Sodium Carbonate to Control the Rate of Peroxide Decomposition in the Foam Matrix 
         [0198]    For this purpose, two alternate catalysts were chosen: (a) Silver and (b) PVP-iodine complex. The reason for choosing these catalysts was due to the fact that they decompose hydrogen peroxide an order of magnitude slower compared to sodium carbonate. Furthermore, both silver and iodine have antiseptic properties and would provide additional benefits to the end user. The formulations obtained from this approach are provided in Table 7 and the experimental details are as follows: 
         [0199]    50/50 Encapsulation of PVP-I2 
         [0200]    Take PVP-Iodine Complex (3.17 grams) and dissolve into distilled water (20 grams). After dissolving, charge Hercules Supercol U Guar Gum (3.22 grams). Mix vigorously to dissolve. Place in a vacuum oven 60° C. overnight to obtain dry solids. Grind the solids the next day with mortar and pestle and sieve to less than 106 μm. 
         [0201]    CAPA-PEG Hybrid with Silver Zeolite 
         [0202]    Grind the granular silver zeolite (Aldrich 382280) with a mortar and pestle, then sieve with a 106 μm screen. 
         [0203]    Take 59.90 grams of 53424-44-10(40% 550 MW CAPA; 60% 2000 MW PEG Diol) and 0.507 grams of the &lt;106 μm zeolite. Mix well and cast into a 5×5inch Teflon mold. Allow it to air dry. 
         [0204]    Peroxide Swelling Procedure
   1) Weigh each sample   2) Prepare 20% hydrogen peroxide solution by diluting 30% with distilled water   3) Pour enough hydrogen peroxide into a beaker so that the sample is submerged   4) Remove the sample at intervals, blot dry and record the weight   5) Calculate the percent hydration   
 
         [0000]    
       
         
               
             
               
               
             
           
               
                 TABLE 7 
               
             
             
               
                   
               
               
                 Formulations based on alternative peroxide decomposition catalyst. 
               
             
          
           
               
                 Sample Ref. 
                 Comments 
               
               
                   
               
               
                 53424-89-6 
                 PVP-Iodine complex (50/50 wt. % with Guar gum) 
               
               
                 53424-89-31 
                 PVP-Iodine complex (50/50 wt. % with Guar 
               
               
                   
                 gum) &lt;106 μm particle reduction 
               
               
                 53424-89-21 
                 Silver exchanged Zeolite 
               
               
                   
               
             
          
         
       
       
         
           
             Prepolymer comprises of 40% 550 MW CAPA; 60% 2,000 MW PEG Diol 
             Crosslinker used was Tolonate HDT 1 wt. % based on prepolymer solids 
             Catalyst used was 2 wt. % based on prepolymer solids 
           
         
       
     
         [0213]    It was observed that the samples based on guar gum when soaked in 20% hydrogen peroxide solution had a very tacky surface and could not be removed from the mesh sheet. This observation supports the assessment that guar gum would form a less rigid foam and would assist in the coalescence of the foam. 
         [0214]    Polymer matrix formulated with PVP-iodine catalysts swelled in 20% hydrogen peroxide solution. However, it was observed that the matrix had uneven texture and after foaming, the test specimen was hard and brittle. 
         [0215]    The polymer matrix with silver based catalyst did not foam the matrix. When samples were soaked in peroxide solution, a froth was noted and the pH of the peroxide medium increased. The silver catalyst used was based on supported zeolites (sodium aluminum silicate) and we speculate the catalyst support was not completely neutralized. The residual base (such as sodium hydroxide) would have initiated the peroxide decomposition during the soak time. It is clear from our studies the rate of peroxide decomposition is critical and a key factor for producing foam with the desired closed cell morphology. 
         [0216]    The foam samples from the above two approaches were cross sectioned and investigated under SEM. The foam samples containing guar gum had closed cell morphology with very limited defects. The oxygen concentration of these samples was found to be only 20-25 ppm (Table 8). This was a surprising result as this closed cell morphology was expected to hold more gas compared to the open cell structure. 
         [0217]    If we believe our earlier samples with open cell architecture have an oxygen concentration of about 25 ppm, then one would expect a higher oxygen concentration from the guar gum formulations that resulted in more closed cell structure. In order to verify, the oxygen permeability (oxygen holding capacity) of the neat polymer matrix cast films, from the formulation comprised of 40% 550 MW CAPA prepolymer and 60% 2,000 MW PEG diol were analyzed. 
         [0000]    
       
         
               
             
               
               
               
             
               
               
               
             
           
               
                 TABLE 8 
               
             
             
               
                   
               
               
                 Oxygen concentration results for the polymer 
               
               
                 matrix formulated with additives. 
               
             
          
           
               
                 Sample 
                   
                 Total O 2   
               
               
                 Reference 
                 Description 
                 Delivery 24 hr 
               
               
                   
               
             
          
           
               
                   
                 Control 
                 22.1 
               
               
                   
                 Mixed Guar gum with catalyst (50/50 wt. %) 
                 22.7 
               
               
                   
                 Mixed Guar gum with catalyst (33/67 wt. %) 
                 24.2 
               
               
                   
                 Mixed Guar gum with catalyst (50/50 wt. %) 
                 24.0 
               
               
                   
                 and placed the catalyst in between two PU 
               
               
                   
                 films 
               
               
                   
                 Mixed Guar gum with catalyst (33/67 wt. %) 
                 23.8 
               
               
                   
                 and placed the catalyst in between two PU 
               
               
                   
                 films 
               
               
                   
                 PVP-Iodine complex (50/50 wt. % with 
                 21.9 
               
               
                   
                 Guar gum) 
               
               
                   
                 PVP-Iodine complex (50/50 wt. % with 
                 22.2 
               
               
                   
                 Guar gum) &lt;106 μm particle reduction 
               
               
                   
                   
               
             
          
         
       
     
         [0218]    We have demonstrated the feasibility of making a biodegradable foam. The top candidate based on covalently linked segments of polycaprolactone and polyethylene glycol met the performance requirements for biodegradability, biocompatibility, and foam forming ability. 
         [0219]    While the disclosure has been described in detail with respect to specific embodiments thereof, it will be apparent to those skilled in the art that various alterations, modifications and other changes may be made to the disclosure without departing from the spirit and scope of the present disclosure. It is therefore intended that the claims cover all such modifications, alterations and other changes encompassed by the appended claims.