Abstract:
A piezoelectric ceramic composition which comprises the combination of a pyrochlore composite oxide and a base ceramic mixture of PbTiO 3  and PbZrO 3   is prepared by individually forming pyrochlore composite oxide, PbTiO 3  and PbZrO 3  components; and sintering a mixture of the formed components at a temperature greater than 1,000° C.

Description:
BACKGROUND OF THE INVENTION 
     1. Field of the Invention 
     This invention relates to a piezoelectric ceramic composition. More particularly, it relates to a piezoelectric ceramic composition which has improved dielectric and piezoelectric characteristics. 
     2. Description of the Prior Art 
     Barium titanate type ceramic compositions and lead zirconatetitanate type ceramic compositions have been used as piezoelectric ceramic compositions. These compositions, however, are not stable industrial compositions. Therefore, efforts have been directed to developing improved piezoelectric compositions. One of these improved compositions is a ternary system of a solid solution of Pb(Mg 1/3 .NbHd 2/3)O 3  --PbTiO 3  --PbZrO 3 . It has also been proposed to modify and improve the piezoelectric properties of the composition by the addition of an oxide of Mn, Cr, Co, Fe or Ni to the basic composition. One of the problems with this composition is the moisture absorbing property of the composition containing Mg which interfers with accurate weighing of the composition and the storage of the starting materials. Although the composition has an electro-mechanical coupling coefficient, Kp of 50-58%, the dielectric loss of the composition is as high as 2-2.4%. 
     In the ternary solid solution of the base ceramic components of PbTiO 3  --PbZrO 3  and the additive, Pb(Mn 1/3  Sb 2/3 )O 3 , the dielectric constant ε and the electro-mechanical coupling coefficient Kp are easily changed by small changes in the components. Compositions having Kp values greater than 50% have low dielectric constants of about 500. Since compositions having a dielectric constant greater than 1000 have been limited to rather narrow ranges of the components, the number of industrially suitable piezoelectric has been limited to a relative few. The compositions of the prior art have been combinations of the above base ceramics components and a perovskite type component, ABO 3 . 
     Other proposed improvements for the compositions have involved the addition of certain additives to the base ceramic components of PbTiO 3  --PbZrO 3 . For example, in one procedure, the basic ceramic composition has been modified by substituting Pb by Sr and by the addition of a component of Sb 2  O 3  and MnO 2 . Up to the present, the most effective modified piezoelectric composition has been one whose base ceramic components of PbTiO 3  and PbZrO 3  are in a ratio of 47:53 and which has had values of Kp = 60%, ε = 1750 and tan δ = 2.5%. However, these compositions have had the disadvantage that their performance characteristics are readily changed by the small changes in their component structure. For example, a change in the quantity of Mn of 0.15 wt.% causes a change of Qm from about 1170 to about 300. If it is desired to decrease the tan δ value to 1.0% by adding another component, the value of Kp changes from 60% to 48.3%. To the present, piezoelectric ceramic compositions having the desired combination of Kp, ε, Q and tan δ values which are stable to small changes in the component makeup of the composition have not been obtained. 
     A need therefore, continues to exist for piezoelectric compositions which have Kp, ε, Q and tan δ values which are stable to small changes in the component makeup of the compositions, and which have high piezoelectric constants. 
     SUMMARY OF THE INVENTION 
     Accordingly, one object of the invention is to provide a piezoelectric ceramic composition having a high piezoelectric constant and stability which has an optimum balance of the electro-mechanical coupling coefficient Kp, the dielectric constant ε, the mechanical quality factor Qm and the low dielectric loss factor tan δ. 
     Another object of the invention is to provide a piezoelectric ceramic composition having a high stability to applied voltages and high flex strength which has improved dielectric and piezoelectric characteristics. 
     Yet another object of the invention is to provide a piezoelectric ceramic composition which is useful as a high power ultrasonic transducer in water or as a wide band filter element. 
     Briefly, these objects and other objects of the invention as hereinafter will become more readily apparent can be attained by providing a piezoelectric ceramic composition which comprises the combination of a pyrochlore complex oxide A 2  B 2  O 7  and a mixture of PbTiO 3  --PbZrO 3  ceramic components. 
    
    
     BRIEF DESCRIPTION OF THE DRAWINGS 
     A more complete appreciation of the invention and many of the attendant advantages thereof will be readily obtained as the same becomes better understood by reference to the following detailed description when considered in connection with the accompanying drawings, wherein: 
     FIG. 1 is a triangular coordinate of the ternary system solid solution of the invention; 
     FIG. 2 is a graph showing the relationship of ε v/ ε to a measured terminal voltage; 
     FIG. 3 is a graph showing the relationship of tan δ to a measured terminal voltage; 
     FIG. 4 is a graph showing the relationship of amplitude to a terminal voltage; and 
     FIG. 5 is a graph showing the relationship of the coefficient of temperature of the dielectric constant to the Ti ratio. 
    
    
     DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENT 
     The piezoelectric ceramic, solid solution composition of the invention has the following characteristics: Kp of 50% to 76%, ε of 1000 to 2500 and a tan δ value of less than 2.0%. 
     Pyrochlore type composite oxides which the present composition contains have complicated structures having 8 structural units per unit cell. In addition, the NbO 6  component of the pyrochlore oxide has zig-zag chains of O--Nb--O and one oxygen atom which is bonded by four cadmium atoms. The latter group is independent of the Nb atom. When the pyrochlore type composite oxide of Cd 2  Sb 2  O 7  or Cd 2  Nb 2  O 7  or a composite oxide formed by substituting Pb, Sr or Ba for Cd is combined with the base ceramic components of PbTiO 3  and PbZrO 3  and the mixture is sintered at a temperature greater than 1000° C, a piezoelectric ceramic composition having the following formula is formed: (1-x)[yPbTiO 3  . zPbZrO 3  ] . x(pyrochlore complex oxide -- A 2  B 2  O 7 ) 1/2 , wherein 0.2 ≦ y ≦ 0.8, 0.2 ≦ z ≦ 0.8, y + z = 1.0 and  0.001 ≦ x ≦ 0.2. The mixture of pyrochlore composite oxide and ceramic components can be calcined before it is sintered. Preferably, Mn is added to the composition as MnO 2  in quantities of 0.01-3.0 wt.% relative to the total basic components. FIG. 1 is a triangular coordinate system of the ternary solid solution [x(A 2  B 2  O 7 ) 1/2  . yPbTiO 3  . zPbZrO 3  ] of the invention. 
     When a pyrochlore type composite oxide of (Cd 2  Sb 2  O 7 ) 1/2 , (Cd 2  Nb 2  O 7 ) 1/2  or the oxide in which Pb, Sr or Ba is substituted for Cd, is combined with Pb(Ti . Zr)O 3  in amounts of 1-20 mole %, a piezoelectric composition is obtained whose characteristics change continuously with corresponding degrees of change of the amounts of the components of the composition, that is, the characteristics of the composition do not suddenly and appreciably change upon minor changes of the constituents in the composition. Because of this, the composition is useful industrially. 
     The compositions of the invention which are suitable for broad applications and practical uses, have ratios of PbTiO 3  to PbZrO 3  of 46 - 54 : 54 - 46 mole % and Pb(Ti . Zr)O 3  to (A 2  B 2  O 7 ) 1/2  ratios of 100 - 1˜20 : 1 - 20 mole % wherein A is Cd, Pb, Sr, or Ba and B is Sb or Nb. Suitable pyrochlore oxides A 2  B 2  O 7  include Cd 2  Sb 2  O 7 , Cd 2  Nb 2  O 7 , Pb 2  Sb 2  O 7 , Pb 2  Nb 2  O 7 , Sr 2  Sb 2  O 7 , Sr 2  Nb 2  O 7 , Ba 2  Sb 2  O 7 , and Ba 2  Nb 2  O 7 . 
     The compositions have Kp values greater than about 60%, ε values greater than about 1400 and tan δ of less than 2%. The piezoelectric properties of the compositions are continuous in the range of 1-20 mole % of (A 2  B 2  O 7 ) 1/2 , so that the stability of the composition is remarkably high, as shown in Tables 1 and 5. 
     The pyrochlore composite oxides of (A 2  B 2  O 7 ) 1/2  wherein A is Pb, Sr or Ba and B is Sb or Nb, is combined with Pb(Ti . Zr)O 3 , and characteristics similar to these for the pyrochlore oxides above shown in Table 2 are obtained. 
     When Mn is present in the composition, the mechanical quality factor Qm can be increased to about 2000 to 4500 and the dielectric loss tanδ is decreased to less than 1%. However, the dielectric constant and the electromechanical coupling coefficient do not fluctuate much, so that a remarkable combination of characteristics of Kp, ε, tan δ and Qm can be obtained. Thus, the composition can be readily mass produced. The effects imparted by Mn for improving the mechanical quality factor of the compositions are also attained with the other pyrochlore complex oxides and Pb(Ti . Zr)O 3  whereby the electromechanical coupling coefficient Kp can be greater than 72%, i.e., about 78%, the dielectric constant and the mechanical quality factor are maintained as suitable values and the dielectric loss tan δ can be reduced to values less than 1%, i.e., about 0.2%. 
     The improved characteristics exhibited by the compositions of the invention fluctuate only very slowly when the amounts of the components are altered because the complex pyrochlore oxides have long-range forces which are characteristic of the pyrochlore oxides. They are very different from the ABO 3  type compounds. 
     The ferroelectric piezoelectric ceramic compositions of the invention have the characteristics of being continuously stable while showing only slight fluctuations of the characteristics when the components of the compositions are changed only slightly. Thus, the industrial advantages for these compositions are substantial. 
     The combined characteristics of the compositions of the invention are very good, and as a result, the dielectric characteristics exhibit a high degree of stability to changes of the applied voltage as shown in FIGS. 2 and 3. In comparison to the low stability of the conventional compositions, the solid solutions containing the pyrochlore complex oxides of the invention have remarkable stability. 
     As shown in FIG. 2, the stability of the dielectric constant of the composition of the invention to a change in voltage is very substantial and the temperature coefficient of the dielectric constant is much superior as shown in the tables which follow later. 
     When the piezoelectric ceramic composition is used as an ultrasonic transducer, the input load increases in the generation of high ultrasonic waves. The stability of the dielectric loss (tan δ)-voltage characteristics is important in this regard. 
     An increase in the tan δ value means an increase in the amount of heat which is not desirable. FIG. 3 shows the excellent characteristics of the piezoelectric ceramic composition of the invention. The mechanical quality factor Qm which is in a reciprocal relationship to tan δ, is also very stable to changes in the voltage. 
     FIG. 4 shows the relationship of the mechanical quality factor Q of a bolt fitted Langevin transducer (30 mm diameter) and the amplitude λ under non-loaded conditions in air, which shows excellent overall piezoelectric characteristics with excellent dielectric characteristics. 
     When a conventional transducer is resonated in a range of 0-30 volts, the transducer shows a sudden decrease in the mechanical quality factor Q at about 10 volts, and the amplitude is limited to 3-4 μ. However, transducers made of the composition of the invention show a high stability for the mechanical quality Q factor as shown in FIG. 4. With these transducers it is possible to transduce forcibly at a level of 50 volts to generate high intensity ultrasonic power. Also, the transducer does not deteriorate with increasing applied voltages. Since the solid solutions of the invention contain the pyrochlore complex oxides, they exhibit stability to applied voltages which is a fundamental characteristic of the pyrochlore oxides. If the solid solutions contain from 0.1-20 moles of pyrochlore complex oxides, they exhibit the desired fundamental characteristics of the pyrochlore oxide. 
     When the temperature coefficient of the dielectric constant ε-T.C. is high and the piezoelectric ceramic composition itself is heated, changes in the dielectric constant ε increase while the impedance changes which means that the impedance matching deteriorates and, accordingly, the maximum amplitude cannot be attained. However, the piezoelectric ceramic compositions of the invention have excellent temperature efficiency. 
     The piezoelectric ceramic compositions of the invention have suitable piezoelectric characteristics as ultrasonic transducers. The composition of the invention can also be effectively used in various elements such as ceramic filters, accelerameters, pick-ups and the like, without limiting the effectiveness of the ultrasonic transducer as the three components of the composition are varied or as the amount of manganese additive is varied. 
     Having generally described this invention, a further understanding can be obtained by reference to certain specific examples which are provided herein for purposes of illustration only and are not intended to be limiting unless otherwise specified. 
     EXAMPLE 1 
     PbO, TiO 2 , ZrO 2 , CdO and Sb 2  O 5  were used as the starting powdery materials for the preparation of a piezoelectric ceramic composition. (Sb 2  O 3  can be used instead of Sb 2  O 5  in equimolar amounts.) The starting powdery materials were weighed and mixed to provide the Cd 2  Sb 2  O 7 , PbTiO 3 , and PbZrO 3  components. The mixed starting powdery materials were mixed well in a separate ball mill and the mixture was molded and calcined at 900° C. The resulting Cd 2  Sb 2  O 7 , PbTiO 3  and PbZrO 3  components were weighed and mixed to provide compositions with the atomic ratio of x, y, z shown in Table 1. The mixture was further crushed, mixed by a ball mill and was molded under pressure of 1.5 ton/cm 2  to form a 20 mm diameter disc with a thickness of 1 mm. The disc was sintered at 1200°-1250° C for 2 hours to prepare a ferroelectric piezoelectric ceramic composition. The composition was then used as a piezoelectric element in the conventional manner. A pair of Ag electrodes was placed on both sides of the disc of the piezoelectric element and then the disc was dipped into silicon oil at 100°-150° C. A DC voltage of 3 KV/mm was impressed across the electrodes for 1 hour to polarize them. The disc was operated for 24 hours, and in order to evaluate the piezoelectric properties, i.e., the electromechanical coupling coefficient (Kp) and the mechanical quality factor (Qm), the I.R.E. standard circuit method was used. The coefficient Kp was calculated by the resonant frequency (fr) and the antiresonant frequency (fa). The dielectric constant (ε) and the dielectric loss (tanδ) were made under a frequency of 1 KHz. The value of ε-T.C. was measured as a temperature coefficient of ε. 
     The piezoelectric properties of various (1-x)Pb(Ti y  . Zr z )O 3  . x(Cd 2  Sb 2  O 7 ) 1/2  compositions are shown in Table 1, wherein the amounts of the components and the resulting compositions are shown by x, 1-x,y and z. [x(Cd 2  Sb 2  O 7 ) 1/2  and (1-x)(yPbTiO 3  --zPbZrO 3 ) were combined to form a solid solution.] As is clear from Table 1, high electromechanical coupling coefficients Kp were obtained over a relatively broad range, and the optimum values of Qm, ε/ε o  and tan δ which are necessary for the intended purposes of the composition vary according to the broad range compositions selected. Sample numbers 1-26, 1-27 and 1-28 are conventional PbTiO 3  --PbZrO 3  piezoelectric ceramic compositions. The results of the tests show that the compositions of the invention have substantially superior properties over those of the conventional compositions. 
     
                       Table 1______________________________________x(Cd.sub.2 Sb.sub.2 O.sub.7)1/2 . (1-x)[ y(PbTiO.sub.3) .z)PbZrO.sub.3)]                                            fr T.C.                             tanΔ                                  Kp        (ppm/No.  x      1-x    y    z    ε/ε                             (%)  (%)  Qm   C)______________________________________1-1  0.20   0.80   0.80 0.20  336 1.9  18.2 210  18001-2  0.20   0.80   0.70 0.30  440 2.0  22.2 140  16201-3  0.20   0.80   0.48 0.52 2590 2.2  32.1  50   9001-4  0.20   0.80   0.30 0.70  470 1.8  21.2 110  15901-5  0.20   0.80   0.20 0.80  375 1.7  17.6 140  18001-6  0.10   0.90   0.54 0.46 1330 1.9  584   80  10901-7  0.10   0.90   0.48 0.52 2490 1.8  67.1  60   8701-8  0.10   0.90   0.46 0.54 1480 1.8  58.2  75   8601-9  0.08   0.92   0.56 0.50 2540 2.0  69.5  50  11301-10 0.08   0.92   0.48 0.52 2510 1.9  67.5  50   8301-11 0.05   0.95   0.80 0.20  430 1.3  20.6 145  19201-12 0.05   0.95   0.68 0.32  480 1.5  24.5 130  16801-13 0.05   0.95   0.60 0.40  850 1.4  35.1  95  10301-14 0.05   0.95   0.52 0.48 1800 1.5  55.5  75   9501-15 0.05   0.95   0.50 0.50 2350 1.7  67.2  65   8701-16 0.05   0.95   0.49 0.51 2490 1.9  74.1  60   8501-17 0.05   0.95   0.48 0.52 2390 2.0  76.0  55   8201-18 0.05   0.95   0.46 0.54 1400 2.1  69.3  75   8701-19 0.05   0.95   0.40 0.60  850 2.1  44.4  80  12301-20 0.05   0.95   0.32 0.68  550 1.8  31.7 240  18401-21 0.01   0.99   0.80 0.20  305 1.4  19.2 190  18901-22 0.01   0.99   0.70 0.30  385 1.4  23.5 145  16801-23 0.01   0.99   0.48 0.52 1550 1.5  72.1  60   8201-24 0.01   0.99   0.30 0.70  430 1.8  27.8 250  16401-25 0.01   0.99   0.20 0.80  296 2.0  21.1 300  16201-26 0      1.00   0.20 0.45  340 --    8.0  46  --1-27 0      1.00   0.48 0.52 1060 --   44.0 240  --1-28 0      1.00   0.30 0.70  370 --   27.0 370  --______________________________________ NOTE: x±(1-x)=1 and y+ z=1 
    
     EXAMPLE 2 
     In accordance with the preparation of Example 1, Sr 2  Sb 2  O 7 , Pb 2  Sb 2  O 7  or Ba 2  Sb 2  O 7  was substituted for Cd 2  Sb 2  O 7 . The piezoelectric properties of the resulting compositions are shown in Table 2, together with the components and the compositions. When Cd was substituted by Sr, Ba or Pb, ternary system solid solution ceramics similar to those of Example 1 were obtained. The compositions have high ε/ε o  values which results in high piezoelectric d constants. Kp and ε values, which are bases of the piezoelectric d constant are shown in Table 2. 
     
                                           TABLE 2__________________________________________________________________________x(A.sub.2 Sb.sub.2 O.sub.7).sub.1/2  . (1-x)[y(PbTiO.sub.3) .z(PbZrO.sub.3)]                      tanΔ                          Kp      fr-T.C.No. A  x   1-x y   z   ε/ε.sub.o                      (%) (%) Qm  (ppm/C)__________________________________________________________________________2-1 Sr 0.20      0.80          0.80              0.20                   550                      1.8 21.2                              200 17802-2 Sr 0.20      0.80          0.50              0.50                  3200                      2.0 35.1                              140  9802-3 Sr 0.10      0.90          0.54              0.46                  1530                      1.8 59.8                               80 11202-4 Sr 0.10      0.90          0.46              0.54                  2990                      1.7 60.2                               70  9302-5 Sr 0.05      0.95          0.60              0.40                   890                      1.3 36.0                              100 10202-6 Sr 0.05      0.95          0.52              0.48                  1800                      1.4 58.0                               75  9702-7 Sr 0.05      0.95          0.40              0.60                   850                      1.9 44.5                               80 10002-8 Sr 0.01      0.99          0.52              0.48                  1300                      1.3 69.2                               65 10302-9 Sr 0.01      0.99          0.48              0.52                  1550                      1.5 73.0                               70  8802-10    Pb 0.20      0.80          0.70              0.30                    520                      1.9 20.5                              180 17302-11    Pb 0.20      0.80          0.48              0.52                  3050                      2.2 36.0                              130  9902-12    Pb 0.10      0.90          0.54              0.46                  1490                      1.8 58.3                               80 10302-13    Pb 0.10      0.90          0.46              0.54                  2950                      1.7 60.5                               75  9302-14    Pb 0.05      0.95          0.60              0.40                   800                      1.3 35.5                               95 10102-15    Pb 0.05      0.95          0.52              0.48                  1780                      1.4 57.0                               70  9302-16    Pb 0.05      0.95          0.40              0.60                   830                      1.8 43.5                               85 12802-17    Pb 0.01      0.99          0.52              0.48                  1310                      1.5 69.0                               65  9702-18    Pb 0.01      0.99          0.48              0.52                  1530                      1.6 72.5                               70  9102-19    Ba 0.20      0.80          0.80              0.20                   590                      2.0 22.0                              210 17802-20    Ba 0.20      0.80          0.50              0.50                  3320                      2.3 36.5                              130  9702-21    Ba 0.10      0.90          0.54              0.46                  1580                      1.9 58.9                               82 10902-22    Ba 0.10      0.90          0.46              0.54                  3050                      2.1 61.2                               70  9602-23    Ba 0.05      0.95          0.60              0.40                   900                      1.5 36.5                              100 10702-24    Ba 0.05      0.95          0.52              0.44                  1890                      1.9 60.2                               70  9902-25    Ba 0.05      0.95          0.40              0.60                   920                      2.2 45.5                               80 12502-26    Ba 0.01      0.99          0.52              0.48                  1360                      1.5 68.7                               75  9902-27    Ba 0.01      0.99          0.78              0.52                  1515                      1.7 71.2                               70  910__________________________________________________________________________ NOTE: x +(1-x)=1 and y+z=1 
    
     EXAMPLE 3 
     The procedure for the preparations of Example 1 was followed except that MnO 2  was added to the basic components. The piezoelectric compositions were prepared and the piezoelectric properties were measured as shown in Table 3. The flex strength of the compositions is shown by the Kg/cm 2  unit, and the temperature coefficient of the dielectric constant ε is shown by the ppm/° C unit. 
     As is clear from Table 3, the values of Qm and tan δ were improved by the addition of MnO 2 . However, when more than 3 wt.% MnO 2  was added, the values of Qm and ε/ε o  decreased while the value of tan δ increased. Also, the compositions had inferior insulation properties. Accordingly, the optimum quantity of the manganese (MnO 2 ) component was established in the range of 0.01-3.0 wt.% based on the total weight of basic components. 
     
                                           Table 3__________________________________________________________________________x(Cd.sub.2 Sb.sub.2 O.sub.7).sub.1/2 . (1 - x) [y(PbTiO.sub.3) .z(PbZrO.sub.3)]                              flex                              streng-                                    fr-           MnO.sub.2                   tan δ                       Kp     th    T.C.No.   x  1 - x     y  z  (Wt%)               ε/ε.sub.o                   (%) (%) Qn (Kg/cm.sup.2)                                    (ppm/C)__________________________________________________________________________3-1   0.20 0.80     0.70        0.30           0    440                   2.0 22.2                            40                              830   16203-2   0.20 0.80     0.70        0.30           0.01                432                   1.2 22.1                           1340                              850   16003-3   0.20 0.80     0.70        0.30           0.05                430                   0.9 22.0                           2900                              930   15703-4   0.20 0.80     0.70        0.30           0.1  415                   0.6 22.0                           3500                              990   15303-5   0.20 0.80     0.70        0.30           0.3  407                   0.3 21.7                           4050                              1090  15003-6   0.20 0.80     0.70        0.30           0.5  400                   0.2 21.5                           5500                              1150  14803-7   0.20 0.80     0.70        0.30           1.0  395                   0.03                       20.6                           3200                              1210  15303-8   0.20 0.80     0.70        0.30           3.0  385                   0.6 20.0                           2350                              1060  15403-9   0.20 0.80     0.70        0.30           4.0  325                   1.6 16.2                            480                              980   16503-10   0.10 0.90     0.54        0.46           0   1330                   1.9 58.4                            80                              860   10903-11   0.10 0.90     0.54        0.46           0.05               1150                   0.7 558.0                           1800                              920   11103-12   0.10 0.90     0.54        0.46           0.1 1110                   0.3 56.8                           2230                              980   10503-13   0.10 0.90     0.54        0.46           0.3 1095                   0.2 56.5                           2980                              1040  9903-14   0.10 0.90     0.54        0.46           0.5 1080                   0.2 56.2                           3200                              1180  9503-15   0.10 0.90     0.54        0.46           1.0 105310                   0.3 55.0                           2750                              1210  10803-16   0.10 0.90     0.54        0.46           3.0 1055                   0.7 53.2                           2100                              1100  10703-17   0.05 0.95     0.60        0.40           0    850                   1.4 35.1                            95                              910   10503-18   0.05 0.95     0.60        0.40           0.05                805                   0.6 34.8                           1880                              1020  10103-19   0.05 0.95     0.60        0.40           0.1  795                   0.3 34.5                           2630                              1090  9803-20   0.05 0.95     0.60        0.40           0.3  788                   0.2 34.0                           3750                              1140  9503-21   0.05 0.95     0.60        0.40           0.5  760                   0.2 33.8                           4200                              1230  9103-22   0.05 0.95     0.60        0.40           1.0  715                   0.3 32.5                           2690                              1270  10003-23   0.05 0.95     0.60        0.40           3.0  698                   0.7 30.8                           2200                              1100  10103-24   0.05 0.95     0.49        0.51           0   2490                   0.8 74.1                            60                              910   11203-25   0.05 0.95     0.49        0.51           0.05               2090                   0.6 73.8                           1120                              990   10303-26   0.05 0.95     0.49        0.51           0.1 1980                   0.3 72.8                           1730                              1060  10103-27   0.05 0.95     0.49        0.51           0.3 1710                   0.2 72.8                           2040                              1170  9903-28   0.05 0.95     0.49        0.51           0.5 1624                   0.2 71.6                           2515                              1280  9803-29   0.05 0.95     0.49        0.51           1.0 1422                   0.3 52.3                           1850                              1250  10603-30   0.05 0.95     0.49        0.51           3.0 1050                   0.6 49.5                            940                              1140  10803-31   0.05 0.95     0.40        0.60           0    850                   2.1 44.4                            80                              890   13303-32   0.05 0.95     0.40        0.60           0.05                820                   0.7 44.1                           1540                              1010  12903-33   0.05 0.95     0.40        0.60           0.1  800                   0.4 43.5                           2700                              1130  12703-34   0.05 0.95     0.40        0.60           0.3  790                   0.3 43.2                           3520                              1190  12503-35   0.05 0.95     0.40        0.60           0.5  782                   0.3 42.5                           3830                              1250  12303-36   0.05 0.95     0.40        0.60           1.0  773                   0.4 42.1                           2900                              1270  12603-37   0.05 0.95     0.40        0.60           3.0  758                   0.6 40.6                           2010                              1130  13103-38   0.01 0.99     0.48        0.52           0   1550                   1.5 72.1                            60                              990   8203-39   0.01 0.99     0.48        0.52           0.05               1220                   0.7 70.8                           1580                              980   8303-40   0.01 0.99     0.48        0.52           0.1 1095                   0.3 70.2                           1930                              1050  8203-41   0.01 0.99     0.48        0.52           0.3 1050                   0.3 70.2                           2090                              1180  8103-42   0.01 0.99     0.48        0.52           0.5 1015                   0.2 69.9                           2660                              1190  8103-43   0.01 0.99     0.48        0.52           1.0  996                   0.3 68.7                           2110                              1210  8603-44   0.01 0.99     0.48        0.52           3.0  972                   0.7 65.6                           1280                              1090  9003-45   0.01 0.99     0.30        0.70           0    430                   1.8 27.8                            250                              880   16403-46   0.01 0.99     0.30        0.70           0.05                405                   0.7 27.0                           2020                              990   14803-47   0.01 0.99     0.30        0.70           0.1  398                   0.3 26.5                           2980                              1060  14303-48   0.01 0.99     0.30        0.70           0.3  392                   0.3 26.2                           4030                              1170  14303-49   0.01 0.99     0.30        0.70           0.5  383                   0.2 25.5                           4550                              1210  14003-50   0.01 0.99     0.30        0.70           1.0  380                   0.3 24.3                           3340                              1230  14003-51   0.01 0.99     0.30        0.70           3.0  358                   0.6 23.5                           2370                              1100  1540__________________________________________________________________________ NOTE x + (1 - x) = 1 and y + z = 1 
    
     EXAMPLE 4 
     The procedure of the preparation of Example 2 was followed except that MnO 2  was added to the basic components. The piezoelectric compositions were prepared and the piezoelectric properties were measured as shown in Table 4. As is clear from Table 4, the addition of MnO 2  resulted in substantial improvements in the values of Qm and tan δ. However, when more than 3 wt.% MnO 2  was added, the values of Qm and ε/ε o  decreased and the value of tan δ increased. However, the compositions had inferior insulation properties. Accordingly, the optimum quantity of the manganese (MnO 2 ) component was established in the range of 0.01-3.0 wt.% based on the total weight of basic components. 
     
                                           Table 4__________________________________________________________________________                               flexx(A.sub.2 Sb.sub.2 O.sub.7).sub.1/2 . (1 - x) [y(PbTiO.sub.3 .z(PbZrO.sub.3)]                     stre-             MnO.sub.2                     tan δ                         Kp    ngth  fr-T.C.No.   A x  1 - x       y  z  (Wt%)                 ε/ε.sub.o                     (%) (%)                            Qm (Kg/cm.sup.2)                                     (ppm/C)__________________________________________________________________________4-1   Sr0.05   0.95       0.48          0.52             0   2890                     1.9 78.0                             65                               910   10504-2   Sr0.05   0.95       0.48          0.52             0.01                 2655                     0.9 76.8                            1530                               990   10404-3   Sr0.05   0.95       0.48          0.52             0.05                 2530                     0.5 76.5                            1700                               1080  10604-4   Sr0.05   0.95       0.48          0.52             0.1 2380                     0.3 74.8                            2050                               1160   9704-5   Sr0.05   0.95       0.48          0.52             0.3 1920                     0.2 72.5                            2500                               1190   9404-6   Sr0.05   0.95       0.48          0.52             0.5 1830                     0.2 70.8                            2830                               1255   9904-7   Sr0.05   0.95       0.48          0.52             1.0 1520                     0.3 63.2                            2070                               1250  10004-8   Sr0.05   0.95       0.48          0.52             3.0 1025                     0.7 59.0                            1500                               1190  11104-9   Sr0.05   0.95       0.48          0.52             4.0  698                     1.7 39.5                             380                               1110  11804-10   Pb0.05   0.95       0.49          0.51             0   2610                     2.0 76.5                             60                               890   10804-11   Pb0.05   0.95       0.49          0.51             0.05                 2340                     0.6 75.0                            1330                               990   10904-12   Pb0.05   0.95       0.49          0.51             0.1 2010                     0.4 73.7                            1900                               1050  10304-13   Pb0.05   0.95       0.49          0.51             0.3 1745                     0.3 72.0                            2250                               1170   9404-14   Pb0.05   0.95       0.49          0.51             0.5 1650                     0.2 70.5                            2470                               1230   9004-15   Pb0.05   0.95       0.49          0.51             1.0 1385                     0.4 62.8                            1880                               1245   9204-16   Pb0.05   0.95       0.49          0.51             3.0  980                     0.7 55.7                            1350                               1180   9104-17   Ba0.01   0.99       0.48          0.52             0   1680                     1.8 73.5                             60                               930   10304-18   Ba0.01   0.99       0.48          0.52             0.05                 1510                     0.5 71.2                            1830                               1050  10104-19   Ba0.01   0.99       0.48          0.52             0.1 1440                     0.3 70.8                            2370                               1130   9904-20   Ba0.01   0.99       0.48          0.52             0.3 1320                     0.3 68.6                            2880                               1210   9504-21   Ba0.01   0.99       0.48          0.52             0.5 1280                     0.2 65.2                            3030                               1275   8904-22   Ba0.01   0.99       0.48          0.52             1.0  975                     0.3 5.99                            2460                               1280   9304-23   Ba0.01   0.99       0.48          0.52             3.0  830                     0.6 52.7                            1450                               1150  1050__________________________________________________________________________ 
    
     EXAMPLE 5 
     High dielectric piezoelectric ceramic compositions of the invention were prepared in accordance with the procedure of Example 1 by using PbO, TiO 2 , ZrO 2 , CdO and Nb 2  O 5  as the starting powdery materials. The electromechanical coupling coefficient Kp and the mechanical quality factor Qm of the composition were measured in accordance with the procedure of Example 1. 
     The piezoelectric properties of the various compositions produced are shown in Table 5. As is clear from Table 5, high electromechanical transducing coefficients Kp were obtained over a relatively broad range, and the optimum values of Qm, ε/ε o  and tan δ which are necessary for the intended purposes of the composition vary according to the broad range composition selected. Sample numbers 5-26, 5-27 and 5-28 are conventional PbTiO 3  -- PbZrO 3  piezoelectric ceramic compositions. The properties of the compositions of the invention are substantially superior to those of the conventional compositions. 
     
                                           Table 5__________________________________________________________________________(x(Cd.sub.2 Nb .sub.2 O.sub.7).sub.1/2 (1- x) [y(PbTiO.sub.3) z(PbZrO.sub.3)]                    tan δ                       Kp      fr,TCNo. x   1 - x       y   z   /.sub.o                   (%) (%) Qm  (ppm/C)__________________________________________________________________________5-1 0.20   0.8 0.80           0.20                298                   1.8 20.5                           180 -1655-2 0.20   0.8 0.70           0.30                415                   2.0 24.7                           120 -1505-3 0.20   0.8 0.48           0.52               2360                   2.1 33.4                            60 1005-4 0.20   0.8 0.30           0.70                445                   1.9 22.6                           110 -1505-5 0.20   0.8 0.20           0.80                365                   1.7 19.4                           150 -1605-6 0.10   0.9 0.54           0.46               1230                   1.8 60.5                            75 105-7 0.10   0.9 0.48           0.52               2250                   1.9 66.3                            60 605-8 0.10   0.9 0.46           0.54               1330                   1.9 57.6                            75 - 805-9 0.08   0.92       0.50           0.50               2360                   2.1 68.4                            60 305-10    0.08   0.92       0.48           0.52               2290                   2.0 66.9                            65 505-11    0.05   0.95       0.80           0.20                410                   1.3 22.5                           155 -1205-12    0.05   0.95       0.68           0.32                465                   1.6 26.8                           130 -1105-13    0.05   0.95       0.60           0.40                790                   1.5 37.1                           100 - 305-14    0.05   0.95       0.52           0.48               1805                   1.6 54.8                            80 205-15    0.05   0.95       0.50           0.50               2195                   1.8 66.3                            70 355-16    0.05   0.95       0.49           0.51               2380                   1.9 73.0                             60                               405-17    0.05   0.95       0.48           0.52               2410                   2.0 68.8                            70 505-18    0.05   0.95       0.46           0.54               1380                   2.2 68.6                            75 - 705-19    0.05   0.95       0.40           0.60                810                   2.3 43.8                            85 -1105-20    0.05   0.95       0.32           0.68                545                   1.8 32.0                           180 -1505-21    0.01   0.99       0.80           0.20                315                   1.5 20.2                           175 -1455-22    0.01   0.99       0.70           0.30                368                   1.4 22.5                           130 -1405-23    0.01   0.99       0.48           0.52               1480                   1.6 70.9                            65 255-24    0.01   0.99       0.30           0.70                420                   1.9 27.0                           240 - 805-25    0.01   0.99       0.20           0.80                290                   2.1 21.5                           280 -1205-26    0       0.55           0.45                340    8.0  46 --5-27    0       0.48           0.52               1060    44.0                           240 --5-28    0       0.30           0.70                370    27.0                           370 --__________________________________________________________________________ NOTE: x + (1 - x) = 1 and y + z = 1 
    
     EXAMPLE 6 
     The procedure of the preparation of Example 5 was followed except that the Cd 2  Nb 2  O 7  component was substituted by Sr 2  Nb 2  O 7 , Pb 2  Nb 2  O 7  or Ba 2  Nb 2  O 7 . The piezoelectric properties of the resulting compositions are shown in Table 6, together with the components and the compositions. When Cd was substituted by Sr, Ba or Pb, the ternary system solid solution ceramics similar to those of Example 1 were obtained. The compositions have high ε/ε o  values which give high piezoelectric d constants. The Kp and ε values which are based on the piezoelectric d constant are shown in Table 6. 
     
                                           Table 6__________________________________________________________________________x(A.sub.2 Nb.sub.2 O.sub.7).sub.1/2 . (1 - x) [y (PbTiO.sub.3) . z(PbTiO.sub.3)]                  tan δ                      Kp     fr . TCNo.   x  1 - x     y  x  A ε/ε.sub.o                  (%) (%)                         Qm  (ppm/C)__________________________________________________________________________6-1   0.20 0.8 0.8        0.2           Sr             540  1.0 20.8                         210 -1606-2   0.20 0.8 0.50        0.50           Sr             3150 2.1 34.8                         155 606-3   0.10 0.9 0.54        0.46           Sr             1480 1.9 52.8                         85  206-4   0.10 0.9 0.46        0.54           Sr             2880 1.8 61.3                         70  - 556-5   0.05 0.95     0.60        0.40           Sr             850  1.4 35.8                         100 - 406-6   0.05 0.95     0.52        0.48           Sr             1720 1.4 56.7                         75  356-7   0.05 0.95     0.40        0.60           Sr             855  2.0 45.2                         100 -1206-8   0.01 0.99     0.52        0.48           Sr             1268 1.5 68.2                         75  306-9   0.01 0.99     0.48        0.52           Sr             415  1.6 70.9                         70  206-10   0.20 0.8 0.80        0.20           Pb             505  2.0 21.8                         190 -1506-11   0.20 0.8 0.50        0.50           Pb             2996 2.3 56.2                         150 506-12   0.10 0.9 0.54        0.46           Pb             1380 2.0 57.9                         80  256-13   0.10 0.9 0.46        0.54           Pb             2810 1.8 59.8                         75  - 606-14   0.05 0.95     0.60        0.40           Pb             785  1.5 35.4                         105 - 456-15   0.05 0.95     0.52        0.48           Pb             2270 1.9 70.5                         75  306-16   0.05 0.95     0.40        0.60           Pb             805  1.6 42.9                         90  -1106-17   0.01 0.99     0.52        0.48           Pb             1300 1.8 68.5                         70  256-18   0.01 0.99     0.48        0.52           Pb             1510 2.1 70.8                         70  206-19   0.20 0.8 0.80        0.20           Ba             585  1.9 22.5                         220 -1556-20   0.20 0.8 0.50        0.50           Ba             3180 2.2 36.8                         155 556-21   0.10 0.99     0.54        0.46           Ba             1510 1.8 59.0                         88  306-22   0.10 0.99     0.46        0.54           Ba             2995 2.1 62.5                         73  - 406-23   0.05 0.95     0.60        0.40           Ba             885  1.6 37.0                         110 - 406-24   0.05 0.95     0.52        0.48           Ba             1810 1.9 60.8                         75  356-25   0.05 0.95     0.40        0.60           Ba             905  2.1 46.2                         85  -1206-26   0.01 0.99     0.52        0.48           BA             1590 1.8 71.2                         75  306-27   0.01 0.99     0.48        0.52           Ba             1515 2.0 70.5                         70  20__________________________________________________________________________ NOTE: x + (1 - x) = 1 and y + z = 1  EXAMPLE 7 
    
     The procedure for the preparation of Example 5 was followed except that MnO 2  was added to the basic components. The piezoelectric compositions were prepared and the piezoelectric properties were measured as shown in Table 7 wherein the flex strength is shown by the unit, Kg/cm 2  and the temperature coefficient of the dielectric constant ε is shown by the unit, ppm/° C. 
     As is clear from Table 7, the values of Qm and tan δ were improved by the addition of MnO 2 . However, when more than 3 wt.% of MnO 2  was added, the values of Qm and ε/ε o  decreased and the values of tan δ decreased. However, the compositions had inferior insulation properties. Accordingly, the optimum quantity of the manganese (MnO 2 ) component was established in the range of 0.01-3 wt.% based on the total weight of the basic components. 
     
                                           Table 7__________________________________________________________________________                                     flexx (Cd.sub.2 Nb.sub.2 O.sub.7).sub.1/2 (1 - x) [y (PbTiO.sub.3) z(PbZrO.sub.3)]                            streng-           MnO.sub.2                    tar δ                        Kp      fr . TC                                     thNo.   x  1 - x     y  x  (Wt%)               ε/ε.sub.o                    (%) (%)                           Qm   (ppm/C)                                     (kg/cm.sup. 2)__________________________________________________________________________7-1   0.20 0.8 0.70        0.30           0   415  2.0 24.7                           120  -150 8507-2   0.20 0.8 0.70        0.30           0.01               402  1.2 24.2                           1050 -130 9007-3   0.20 0.8 0.70        0.30           0.05               400  1.0 24.0                           2110 -120 9607-4   0.20 0.8 0.70        0.30           0.1 395  0.5 23.8                           2530 -105 9907-5   0.20 0.8 0.70        0.30           0.3 388  0.3 23.5                           3090 - 90 11007-6   0.20 0.8 0.70        0.30           0.5 375  0.2 23.0                           5250 - 80 12307-7   0.20 0.8 0.70        0.30           1.0 370  0.3 22.2                           3870 - 65 11607-8   0.20 0.8 0.70        0.30           3.0 355  0.7 21.3                           3030 - 40 10907-9   0.20 0.8 0.70        0.30           4.0 305  1.5 18.5                           630  - 30 10607-10   0.10 0.9 0.46        0.54           0   1330 1.9 57.6                           75   - 80 9007-11   0.10 0.9 0.46        0.54           0.05               1095 0.7 56.0                           1690 - 60 9607-12   0.10 0.9 0.46        0.54           0.1 1080 0.4 55.7                           2270 - 50 9907-13   0.10 0.9 0.46        0.54           0.3 1065 0.3 55.2                           2650 - 40 11307-14   0.10 0.9 0.46        0.54           0.5 1062 0.3 54.5                           3080 - 35 12107-15   0.10 0.9 0.46        0.54           1.0 1020 0.3 54.0                           2630 10   11307-16   0.10 0.9 0.46        0.54           3.0 1000 0.8 51.5                           2000 30   11007-17   0.08 0.92     0.50        0.50           0   2360 2.1 68.4                           60   30   9307-18   0.08 0.92     0.50        0.50           0.05               2050 0.9 66.8                           1770 40   9807-19   0.08 0.92     0.50        0.50           0.1 1990 0.4 65.9                           2230 55   10607-20   0.08 0.92     0.50        0.50           0.3 1830 0.3 65.2                           2370 60   12307-21   0.08 0.92     0.50        0.50           0.5 1800 0.2 64.7                           2550 70   12907-22   0.08 0.92     0.50        0.50           1.0 1795 0.3 64.5                           2190 90   12007-23   0.08 0.92     0.50        0.50           3.0 1638 0.7 60.8                           1800 110  10807-24   0.05 0.95     0.49        0.51           0   2380 1.9 73.0                           60   40   9307-25   0.05 0.95     0.49        0.51           0.3 1520 0.2 69.8                           2200 55   10107-26   0.05 0.95     0.49        0.51           0.5 1390 0.2 68.5                           2630 60   11807-27   0.05 0.95     0.49        0.51           1.0 1085 0.4 51.3                           1985 75   12507-28   0.05 0.95     0.49        0.51           3.0 950  0.7 49.0                           1010 100  11307-29   0.05 0.95     0.40        0.60           0   810  2.3 43.8                           85   -110 9707-30   0.05 0.95     0.40        0.60           0.05               790  1.0 43.0                           1980 - 95 10707-31   0.05 0.95     0.40        0.60           0.1 788  0.5 42.5                           2330 - 80 11507-32   0.05 0.95     0.40        0.60           0.3 775  0.3 42.2                           2680 - 60 12307-33   0.05 0.95     0.40        0.60           0.5 762  0.3 41.5                           3520 - 40 12807-34   0.05 0.95     0.40        0.60           1.0 75.0 0.3 41.0                           2790 - 25 12107-35   0.05 0.95     0.40        0.60           3.0 708  0.9 39.7                           1980 - 10 11307-36   0.01 0.99     0.70        0.30           0   368  1.4 22.5                           130  -140 9607-37   0.01 0.99     0.70        0.30           0.05               355  0.6 22.0                           1990 -130 9907-38   0.01 0.99     0.70        0.30           0.1 350  0.3 21.8                           2340 -115 10807-39   0.01 0.99     0.70        0.30           0.3 348  0.2 21.7                           2880 -100 12107-40   0.01 0.99     0.70        0.30           0.5 343  0.2 21.6                           4270 - 85 13207-41   0.01 0.99     0.70        0.30           1.0 340  0.3 21.0                           3110 - 60 12307-42   0.01 0.99     0.70        0.30           3.0 325  0.6 20.2                           2050 - 40 11907-43   0.01 0.99     0.48        0.52           0   1480 1.6 70.9                           65   25   9907-44   0.01 0.99     0.48        0.52           0.05               1230 1.0 69.5                           1670 30   11007-45   0.01 0.99     0.48        0.52           0.1 1225 0.4 69.2                           1830 50   12307-46   0.01 0.99     0.48        0.52           0.3 1223 0.3 68.5                           2130 15   12807-47   0.01 0.99     0.48        0.52           0.5 1205 0.2 68.5                           2580 80   13107-48   0.01 0.99     0.48        0.52           1.0 1196 0.3 67.3                           2100 90   12207-49   0.01 0.99     0.48        0.52           3.0 1135 0.7 64.2                           1390 120  1190__________________________________________________________________________ NOTE: x + (1 - x) = 1 and y + z = 1 
    
     EXAMPLE 8 
     The procedure of the preparation of Example 6 was followed except that MnO 2  was added to the basic components. The piezoelectric compositions were prepared and the piezoelectric properties were measured as shown in Table 8. As is clear from Table 8, the values of Qm and tan δ were improved by adding MnO 2 . However, when more than 3 wt.% MnO 2  was added to the composition, the values of Qm and ε/ε o  decreased and the values of tan δ increased. However, the compositions had inferior insulation properties. Accordingly, the optimum quantity of the manganese (MnO 2 ) component is in the range of 0.01-3.0 wt.% based on the total weight of the basic components. 
     
                                           TABLE 8__________________________________________________________________________           (A.sub.2 Nb.sub.2 O.sub.7).sub.1/2 . (1           - x)[y(PbTiO.sub.3) . z(PbZrO.sub.3)]                     flex                     stren-                     gth               MnO.sub.2                 (kg/    tan δ                             Kp      fr . TCNo. x   1 - x       y   z   A (wt.%)                     cm.sup.2                         ε/ε                             %   %   Qm  (ppm/° C)__________________________________________________________________________8-1 0.05   0.95       0.48           0.52               Sr                 0.  930 2320                             1.8 69.7                                     75    208-2 0.05   0.95       0.48           0.52               Sr                 0.01                     990 2095                             0.7 69.2                                     1830  258-3 0.05   0.95       0.48           0.52               Sr                 0.05                     1090                         2530                             0.5 76.5                                     1700  358-4 0.05   0.95       0.48           0.52               Sr                 0.1 1210                         2380                             0.3 74.8                                     2050  508-5 0.05   0.95       0.48           0.52               Sr                 0.3 1290                         1490                             0.3 68.0                                     2550  608-6 0.05   0.95       0.48           0.52               Sr                 0.5 1310                         1320                             0.2 66.8                                     2630  758-7 0.05   0.95       0.48           0.52               Sr                 1.0 1230                         1065                             0.4 61.5                                     2050  908-8 0.05   0.95       0.48           0.52               Sr                 3.0 1180                         899 0.8 59.8                                     1320  1108-9 0.05   0.95       0.48           0.52               Sr                 4.0 1150                         530 1.6 35.5                                     340   1508-10    0.05   0.95       0.49           0.51               Pb                 0   900 1970                             1.9 70.5                                     75    508-11    0.05   0.95       0.49           0.51               Pb                 0.05                     950 2340                             0.6 75.0                                     1330  608-12    0.05   0.95       0.49           0.51               Pb                 0.1 990 2010                             0.4 73.7                                     1900  758-13    0.05   0.95       0.49           0.51               Pb                 0.3 1180                         1445                             0.3 69.2                                     2380  858-14    0.05   0.95       0.49           0.51               Pb                 0.5 1260                         1398                             0.2 67.7                                     2530  1008-15    0.05   0.95       0.49           0.51               Pb                 1.0 1210                         1090                             0.5 61.5                                     1780  1208-16    0.05   0.95       0.49           0.51               Pb                 3.0 1130                         870 0.8 54.8                                     1040  1408-17    0.01   0.99       0.48           0.52               Ba                 0   930 1515                             1.9 70.5                                     70    208-18    0.01   0.99       0.48           0.52               BA                 0.05                     1030                         1510                             0.5 71.2                                     1830  308-19    0.01   0.99       0.48           0.52               Ba                 0.1 1150                         1440                             0.3 70.8                                     2370  458-20    0.01   0.99       0.48           0.52               Ba                 0.3 1230                         1290                             0.3 68.8                                     2900  558-21    0.01   0.99       0.48           0.52               BA                 0.5 1290                         1215                             0.2 66.2                                     3100  708-22    0.1 0.99       0.48           0.52               BA                 1.0 1230                         1080                             0.4 59.3                                     2240  908-23    0.01   0.99       0.48           0.52               Ba                 3.0 1170                         910 0.7 53.8                                     1550  115__________________________________________________________________________ 
    
     The field dependencies of ε/ε o  and tan δ to the terminal voltage (V) of sample number 4-16 in Table 4 was measured as shown in FIGS. 2 and 3, respectively. As reference compositions, conventional piezoelectric compositions are also shown in FIGS. 2 and 3. When the conventional piezoelectric composition was used under the application of a high voltage, inferior piezoelectric properties resulted because of the increase in tan δ values and the elevation of the temperature. 
     The samples of the invention show low AC field dependency on ε/ε o  and tan δ. These phenomena reveal that the stable compositions of the invention exhibit low heating values when used as high power ultrasonic transducers in order to very efficiently convert input power to ultrasonic wave energy. The piezoelectric ceramic compositions of the invention are very effective in applications where high amplitude characteristics are required. 
     Having now fully described this invention, it will be apparent to one of ordinary skill in the art that many changes and modifications can be made thereto without departing from the spirit or scope of the invention set forth herein.