Abstract:
An electronic device, including an organic semiconductor, the organic semiconductor having a first polymer having a first molecular weight and a first length, and a second polymer having a second molecular weight and a second length, wherein the second length is longer than the first length.

Description:
BACKGROUND 
       [0001]    Organic semiconductor materials have become important components of materials such as flexible, thin film transistors and lightweight photovoltaic cells. The transistors typically comprise a substrate, a dielectric, a source electrode, a drain electrode, and a gate electrode in addition to the semiconductor. A variety of processes can manufacture these devices such as inkjet printing and thermal evaporation. The performance of these devices improves with increases in the mobility of charge carriers in the semiconducting material. Polymeric materials such as poly(3-hexlythiophene) (P3HT) or poly(2,5-bis(3-alkylthiophen-2-yl)thieno[3,2-b]thiophene) (PBTTT) are sometimes employed as the organic semiconductor material. The term polymer is commonly employed to mean a molecule formed by linking together a sequence of identical molecular units called monomers. The length of a polymer consisting of N monomers will be N times the length of the monomer, and the molecular weight of the polymer will be N times the molecular weight of the monomer. Another type of polymer, a co-polymer, is formed by linking together a sequence of at least two types of monomers. The length, or molecular weight, of such a polymer will be the sum of the lengths, or molecular weights, of the monomers. An alternating co-polymer could be specified as A-D-A-D . . . A-D where A and D represent distinct monomers. Indacenodithiophene-co-benzothiadiazole is an example of a co-polymer. Polymeric materials are advantageous because they can be incorporated into a device inexpensively by solution processing, and can achieve mobility of 0.1 to 1 cm2/Vs. 
         [0002]    One approach to increasing the mobility of the charge carriers, holes and electrons, in organic semiconductor materials enhances the electronic connectivity between ordered domains. 
     
    
     
       BRIEF DESCRIPTION OF THE DRAWINGS 
         [0003]      FIG. 1  shows an embodiment of a region of a material in which all the polymers have the same length. 
           [0004]      FIG. 2  shows a connection diagram for a region of a material in which all the polymers have the same length. 
           [0005]      FIG. 3  shows an embodiment of a region of a material in which all the polymers have the same length and are staggered. 
           [0006]      FIG. 4  shows a connection diagram for an embodiment of a region of a material having polymers of different lengths. 
           [0007]      FIG. 5  shows a connection diagram for an embodiment of a region of a material having polymers of different lengths. 
           [0008]      FIG. 6  shows a contour plot of polydispersity index for a mixture of two polymers. 
           [0009]      FIG. 7  shows a plot of the distribution of monomer numbers in a bi-disperse mixture. 
           [0010]      FIG. 8  shows a plot of another embodiment of a bi-disperse mixture. 
       
    
    
     DETAILED DESCRIPTION OF THE EMBODIMENTS 
       [0011]      FIG. 1  shows a region  10  of a material in which all the polymers have the same length. In  FIG. 1  each polymer consists of 8 monomers, and each monomer consists of one thiophene ring and one alkyl side chain. The molecular forces between the polymers tend to cause each polymer to align with its neighbors. Because the polymers are finite in length this alignment can lead to structural breaks at boundaries separating one ordered region from another. This is consistent with experimental observations as discussed in Jimision, et al. “ Charge - Transport Anisotropy Due to Grain Boundaries in Directionally Crystallized Thin Films of Regioregular Poly (3- hexylthiophene,” Advanced Materials,  21 (16) 1568-1572 (2009) This polymer alignment may give rise to a grain boundary. Grain boundaries impede transport of carriers. In the diagram of  FIG. 1 , the grain boundary is shown by line b-b. 
         [0012]      FIG. 2  shows a connection diagram for a region of a material in which all the polymers have the same length, in this example the length is L 1 . The carrier, whether a hole or an electron, has a fast transport path from point  1  to point  2 . Transport from 4 to 5 is impeded because of the grain boundary along b-b. Transport from 2 to 3 is not as fast as the transport along the path from 1 to 2, but is faster than the path between 4 and 5. The transport along path  5  and  6  on the other side of the grain boundary is similar to transport along the path from 1 to 2. 
         [0013]      FIG. 3  shows a second structure in which the monomers are not aligned. Referring back to  FIG. 1 , the material consists of a series of weakly connected domains separated by boundaries perpendicular to the x-axis. In  FIG. 3  the region  20  of the material has every other polymer such as  22  shifted along the x-axis relative to the polymer  24 . The shifting increases the electronic interconnectivity. 
         [0014]    Application of a simple model can estimate the ratio of mobilities of the structures  FIG. 1  and  FIG. 3 . A two dimensional acoustic deformation potential model shows that elimination of the grain boundary leads to an increase in the mobility. In the model, the mobility is determined by scattering of charge carriers by thermally driven fluctuations in the potential. While this is an idealization, it provides a means to make an estimate of the mobility within an organic semiconducting material. The mobility μ is given by: 
         [0000]    
       
         
           
             μ 
             = 
             
               
                 
                   e 
                    
                   
                     
                       h 
                       _ 
                     
                     3 
                   
                    
                   
                     BL 
                     eff 
                   
                 
                 
                   
                     
                       ℰ 
                       
                         a 
                          
                         
                             
                         
                          
                         c 
                       
                       2 
                     
                      
                     
                       ( 
                       
                         
                           k 
                           B 
                         
                          
                         T 
                       
                       ) 
                     
                   
                    
                   
                     ( 
                     
                       
                         m 
                         c 
                       
                        
                       
                         m 
                         d 
                       
                     
                     ) 
                   
                 
               
               . 
             
           
         
       
     
         [0000]    In this expression m c  is the effective mass along the direction of transport and m d  is the density of states mass, which is equal to (m x m y ) 1/2 . ε ac  is the acoustic deformation potential and B is the bulk modulus. L eff  is the effective thickness of the layer in which the transport occurs. 
         [0015]    From electronic structure calculations one may determine the effective masses for the structure of  FIG. 1  and the structure of  FIG. 3 . In order to provide a specific example, the following discussion uses poly(3-ethylthiophene)polymers containing 8 thiophene rings. For the structure of  FIG. 3 , the effective masses along the x and y directions are m x =0.36 m and m y =2.3 m. For the structure of  FIG. 1 , the effective masses along the x and y directions are 2.9 m and 1.7 m. The effective mass values are given as multiples of the free electron m of the electron. The reduction of the effective mass from 2.9 m to 0.36 m by the increased interconnectivity present in the structure of  FIG. 3 . The equation above allows one to estimate the ratio of mobilities between the structures of  FIG. 1  and  FIG. 3 . 
         [0016]    Assuming that the deformation potential, bulk modulus, and L eff  are not affected by the polymer alignment, the mobility ratio can be obtained from the effective mass values. In the below equation, the structure of  FIG. 3  is referred to as II, and the structure of  FIG. 1  is referred to as I. 
         [0000]      μ x ( II )/μ x ( I )=( m   x ( I ) m   y ( I )) 1/2    m   x ( I )/( m   x ( II ) m   y ( II )) 1/2    m   x ( II )=20
 
         [0000]      μ y ( II )/μ y ( I )=( m   x ( I ) m   y ( I )) 1/2    m   y ( I )/( m   x ( II ) m   y ( II )) 1/2    m   x ( II )=1.8.
 
         [0000]    This demonstrates that there is a tremendous enhancement of mobility along the x direction. The enhancement is 20 for transport along the x direction and 1.8 for transport along the y direction. Therefore employing strategies to increase the interdomain connectivity will improve the mobility. 
         [0017]    One strategy would involve employing a mixture of two different polymers where one of the polymers has a longer length than the other. In one example, a mixture of a fraction (1-f) of a first polymer having a first length L 1  and a fraction f of a second polymer having a second length L 2 .  FIG. 4  shows a connection diagram for such a mixture, in which the length L 2  is twice that of L 1 . The transport path between points  1  and  2  is very fast across the grain boundary. 
         [0018]      FIG. 5  shows a connection diagram for a region of a material having a mix of P 1  and P 2 . The connection diagram for an example mix of a fraction f=0.2 (20%) of a polymer P 2 , and a fraction f=0.8 of a polymer P 1 . An example of such a mix would involve P3HT with 16 thiophene rings (P 1 ) and 20 thiophene (P 2 ). The path between points A and B has relatively fast transport. Previously, the materials would have had grain boundaries  32  and  34  across which transport will have been impeded. Now, the carriers can travel across the region where there previously would have been a boundary, and then using the longer polymer P 2  to transport across the entire length of the region of the material. 
         [0019]    One can characterize a variation in molecular weight of an aggregation of polymers using a polydispersity index (PDI). Many polymer aggregates have a PDI of 2 or greater. The PDI is equal to M W /M N  where M W =(1/M T )Σ M i   2  and M N =(1/N)Σ M i . M T  is the total weight of the aggregation, N is the number of polymers in the aggregation, and the sum Σ is over all polymers in the aggregation. If a mixture consists of a fraction f of P 2  and (1-f) of P 1 , where the polymer weight of P 2  is (1+g) times that of P 1 , then PDI=(1+fg(2+g))/(1+fg) 2 . For the case of f=0.2 and g=0.2, the PDI=1.06, and for the case of f=0.5 and g=1, PDI is 1.11.  FIG. 6  shows a contour plot of PDI as a function of f and g. The materials employed in the embodiment generally have a PDI less than 2, and may be less than 1.2. 
         [0020]    A mixture of polymers of primarily two different lengths, and two molecular weights, may be referred to as a bi-disperse mixture. An example of the distribution of polymer lengths in a bi-disperse mixture is shown in  FIG. 7 .  FIG. 7  shows the fraction f of polymers present in the mixture as a function of the number of monomers N in each polymer. The distribution shown there is sharply peaked at two different monomer numbers N 1  and N 2 . The widths, W 1  and W 2 , of the two peaks are optimally less than or equal to 1 monomer, but in practice the widths may be greater than 1 monomer. 
         [0021]    In the example shown in  FIG. 7  there is a fraction f 1 =0.8 of polymers composed of N 1 =20 monomers and a fraction f 2 =0.2 of polymers composed of 40 monomers. The longer monomers will provide connections between ordered domains consisting primarily of the shorter polymers. The presence of a fraction f 2  of longer polymers enhances the mobility of the material. The widths of the peaks are much less than the separation (N 2 −N 1 ) between the peaks. 
         [0022]      FIG. 8  shows another example of a bi-disperse mixture. The function f(N) is the fraction of polymers in the material composed of N monomers. This function f(N) is peaked around N 1  and N 2 . The full-width half-maximum width of the peaks, W 1  and W 2 , may be larger than a few monomers, but each width is required to be less than N 2 −N 1 . A bi-disperse mixture of two polymers having widths W 1  and W 2  that are much less than (N 2 −N 1 ) is expected to exhibit good interconnectivity of ordered domains and superior mobility. 
         [0023]    The embodiments disclosed here provide polymer materials with higher transport mobility. The polymers discussed here may be employed in organic semiconductors and allow for more efficient functioning devices. 
         [0024]    It will be appreciated that several of the above-disclosed and other features and functions, or alternatives thereof, may be desirably combined into many other different systems or applications. Also that various presently unforeseen or unanticipated alternatives, modifications, variations, or improvements therein may be subsequently made by those skilled in the art which are also intended to be encompassed by the following claims.