Patent ID: 11193215

Abstract:
In a deposition method of Ni—P—B system plating film, electroplating is performed in a plating bath containing Ni ions, phosphorous acid ions, alkylamine borane, acetic acid, at least one sort of a primary brightening agent, and a secondary brightening agent including at least one sort of a surface active agent. In the above-mentioned plating bath, concentration of alkylamine borane in said plating bath is 1.37 mmol/L or more, and concentration of acetic acid in said plating bath is 0.70 mol/L or more and less than 2.80 mol/L. Thereby, plating film having high hardness of Hv 700 or more can be deposited with high manufacturing efficiency without baking processing, while reducing occurrence of poor appearance, such as burning and abnormal precipitation, even when current density is increased to 80 A/dm2 or more to raise deposition rate.