Patent ID: 10610979

Abstract:
Provided is a flux containing not less than 11.0 degrees and not more than 17.0 of a contact angle between the flux and a resist substrate on which the flux has been printed to have 1.0 mm of a diameter and 0.15 mm of a thickness when heating the resist substrate at 150 degrees C. for 30 seconds and cooling the resist substrate to a room temperature. The flux also contains more than zero seconds and not more than 2.0 seconds of a zero-cross time when heating a Cu plate at 150 degrees C. in a thermostat oven for 12 hours, applying the flux onto the baked Cu plate, and dipping the baked Cu plate onto which the flux is applied into a Sn-3.0Ag-0.5Cu alloy at a dipping speed of 15 mm/sec and by 2.0 mm of a dipped depth.