Patent ID: 11365460

Abstract:
A high-carbon cold rolled steel sheet having a specified chemical composition, and a method for manufacturing the same. The method includes forming a hot rolled steel sheet, performing cooling at an average cooling rate of 30° C./s or more and 70° C./s or less through a temperature range of a finish rolling end temperature to 660° C., coiling a hot rolled steel sheet at a temperature of 500° C. or more and 660° C. or less, and, optionally, pickling the coiled hot rolled steel sheet, and then performing a first box-annealing of holding at an annealing temperature in a temperature range of 650 to 720° C., then performing cold rolling at a rolling reduction ratio of 20 to 50%, and then performing a second box-annealing of holding at an annealing temperature in a temperature range of 650 to 720° C.