Patent ID: 10354784

Abstract:
A non-oriented magnetic steel sheet includes a specific chemical composition represented by, in mass %: Si: 3.0% to 3.6%; Al: 0.50% to 1.25%; Mn: 0.5% to 1.5%; Sb or Sn or both of them: [Sb]+[Sn]/2 is 0.0025% to 0.05% where [Sb] denotes an Sb content and [Sn] denotes an Sn content; P: 0.010% to 0.150%; Ni: 0.010% to 0.200%; C: 0.0010% to 0.0040%; and others. The thickness of the non-oriented magnetic steel sheet is 0.15 mm to 0.30 mm. the non-oriented magnetic steel sheet includes magnetic properties represented by, where t denotes a thickness (mm) of the non-oriented magnetic steel sheet: a magnetic flux density B50: “0.2×t+1.52” T or more; a magnetic flux density difference ΔB50: 0.08 T or less; core loss W10/50: 0.95 W/kg or less; and core loss W10/400: “20×t+7.5” W/kg or less. A ratio of a number of intergranular carbides precipitated in grains relative to a sum of the number of the intergranular carbides and a number of grain boundary carbides precipitated on grain boundaries is 0.50 or less.