Patent ID: 11492676

Abstract:
A method is for producing a high strength coated steel sheet having a yield stress YS>800 MPa, a tensile strength TS>1180 MPa, and improved formability and ductility. The steel contains: 15%≤C≤0.25%, 1.2%≤Si≤1.8%, 2%≤Mn≤2.4%, 0.1%≤Cr≤0.25%, Al≤0.5%, the remainder being Fe and unavoidable impurities. The sheet is annealed at a temperature higher than Ac3 and lower than 1000° C. for a time of more than 30 s, then quenched by cooling it to a quenching temperature QT between 250° C. and 350° C., to obtain a structure consisting of at least 60% of martensite and a sufficient austenite content such that the final structure contains 3% to 15% of residual austenite and 85% to 97% of martensite and bainite without ferrite, then heated to a partitioning temperature PT between 430° C. and 480° C. and maintained at this temperature for a partitioning time Pt between 10 s and 90 s, then hot dip coated and cooled to the room temperature.