Patent ID: 11667770

Abstract:
Closed cell chitin foam is provided. The closed-cell chitin foam composition does not absorb water, is biodegradable, and is mechanically characterized by a density range of 16 to 800 kg/m3, closed-cell pore sizes ranging from 50 microns to 1 mm, an elastic modulus of 3 to 175 MPa, and a tensile strength of 0.15 to 6.5 MPa. The chitin is at least 70% acetylated. In one aspect, the foam is enclosed in a shell e.g. in the form of a surfboard. Chitin foam according to this invention is fully biodegradable. The chitin foam overcomes the current problems with foams that contain polyurethane and polystyrene, and which are manufactured from petroleum-based sources. Petroleum based foams are not renewable, have an adverse impact on our environment, and pose significant health hazards to those who manufacture them. The chitin foam with its water-based manufacturing process and naturally sourced chitin, solves these problems.