Patent ID: 10900100

Abstract:
A hot rolled steel sheet having a chemical composition consisting of, in mass %, C: 0.020-0.180%, Si: 0.05-1.70%, Mn: 0.50-2.50%, Al: 0.010-1.000%, N: 0.0060%, P≤0.050%, S≤0.005%, Ti: 0-0.150%, Nb: 0-0.100%, V: 0-0.300%, Cu: 0-2.00%, Ni: 0-2.00%, Cr: 0-2.00%, Mo: 0-1.00%, B: 0-0.0100%, Mg: 0-0.0100%, Ca: 0-0.0100%, REM: 0-0.1000%, Zr: 0-1.000%, Co: 0-1.000%, Zn: 0-1.000%, W: 0-1.000%, the balance: Fe and impurities, wherein a metal microstructure includes, in area %, at a position ¼ W or ¾ W from an end face of the steel sheet and ¼ t or ¾ t from a surface, martensite: more than 2%-10%, retained austenite <2%, bainite 40%, pearlite 2%, the balance: ferrite, an average circle-equivalent diameter of a metallic phase constituted of martensite/retained austenite is 1.0-5.0 μm, an average of minimum distances between adjacent metallic phases is 3 μm or more, and a standard deviation of nano hardness is 2.0 GPa or less.