Patent ID: 10875784

Abstract:
A method for synthesizing ferroelectric nanoparticles comprises introducing solutions of Ba(NO3)2 (1 mmol) in 5 ml of deionized water, NaOH (12.5 mmol) in 5 ml of deionized water, Ti(IV) n-butoxide (1 mmol) in 5 ml of 1-butanol, 2.5 ml of oleic acid, and 5 ml of 1-butanol into a Teflon-lined autoclave vessel; heating the vessel to 135° C. for 18 h, resulting in barium titanate nanoparticles; and ball-milling the barium titanate nanoparticles in a solution of oleic acid and heptane to create a colloidal suspension of nanoparticles. The weight ratio of barium titanate:oleic acid:heptane is 1:1:20. The ball-milling step may further comprise introducing a slurry comprising 0.1 g of synthesized BaTiO3 nanocubes, 0.1 g of oleic acid, and 15 mL of heptane into a ball-mill crucible filled with 2 mm ZrO2 balls; subjecting the slurry to rotation at 500 rpm for 5 hours; converting the resulting nanoparticle suspension to a powder using anhydrous ethanol with sequential washing/drying at ambient temperature.