Patent ID: 10507520

Abstract:
Processes are provided that include providing a copper-manganese alloy containing copper and manganese and having an amount of manganese that is at least 32 weight percent and not more than 40 weight percent of a combined total amount of the copper and manganese in the copper-manganese alloy, and casting the copper-manganese alloy by multidirectional solidification to produce a product in the form of a casting. The copper-manganese alloy has a composition sufficiently near the congruent melting point of the Cu—Mn alloy system to sufficiently avoid dendritic growth during the multidirectional solidification of the copper-manganese alloy to avoid the formation of microporosity attributable to dendritic growth. The product has a cast microstructure having a cellular and/or planar solidification structure free of dendritic growth and having multidirectional columnar grains.