Patent ID: 11732340

Abstract:
Provided is a high-strength hot-rolled coated steel sheet having a TS of 980 MPa or more, excellent bulging formability and stretch flange formability, and excellent coatability.The high-strength hot-rolled coated steel sheet includes a steel sheet having a chemical composition containing, by mass %, C: 0.03% to 0.09%, Si: 0.01% to 1.60%, Mn: 2.20% to 3.60%, P: 0.100% or less, S: 0.0100% or less, Ti: 0.05% to 0.18%, B: 0.0005% to 0.0050%, Al: 0.005% to 0.40%, N: 0.010% or less, and a balance of Fe and inevitable impurities, in which a CSM value expressed by the equation 33.8[% C][% Mn]+12.4[% Si]/[% Mn] is 3.3 to 12.0, and a steel microstructure containing bainite in an amount of 85% or more in terms of area fraction and martensite in an amount of 2.0% or more and 15.0% or less in terms of area fraction and includes a coating layer or an alloyed coating layer on a surface of the steel sheet.