Patent ID: 11745393

Abstract:
Surface material of a mold molding surface and surface treatment method. A molding surface of material including metal and in which the molding surface reaches 50° C. or higher during molding is subjected to rapid thermal processing by injecting a substantially spherical shot with a hardness equal to or greater than the surface hardness of the mold and a size of #220 (JIS R6001-1973) or smaller at an injection pressure of 0.2 MPa or more and bombarding the surface with the shot, causing the temperature to rise locally and instantaneously at a bombarded portion to refine the surface structure of the surface and to form numerous smooth arc-shaped indentations on the entire surface of the surface. Then, powder including titanium having size of #100 or smaller is injected at an injection pressure of 0.2 MPa or more to form a coating of titanium oxide on the surface of the surface.