Patent ID: 11634335

Abstract:
The present invention provides an iron-loaded aluminosilicate zeolite having a maximum pore opening defined by eight tetrahedral atoms and having the framework type CHA, AEI, AFX, ERI or LTA, wherein the iron (Fe) is present in a range of from about 0.5 to about 5.0 wt. % based on the total weight of the iron-loaded aluminosilicate zeolite, wherein an ultraviolet-visible absorbance spectrum of the iron-loaded synthetic aluminosilicate zeolite comprises a band at approximately 280 nm, wherein a ratio of an integral, peak-fitted ultraviolet-visible absorbance signal measured in arbitrary units (a.u.) for the band at approximately 280 nm to an integral peak-fitted ultraviolet-visible absorbance signal measured in arbitrary units (a.u.) for a band at approximately 340 nm is >about 2. The present invention further provides a method of making an metal-loaded aluminosilicate zeolite having a maximum pore opening defined by eight tetrahedral atoms from pre-existing aluminosilicate zeolite crystallites, wherein the metal is present in a range of from 0.5 to 5.0 wt. % based on the total weight of the metal-loaded aluminosilicate zeolite.