Patent ID: 11008251

Abstract:
The present invention belongs to the field of composite materials, particularly to an underwater non-dispersible quick-setting and rapid-hardening cement-based composite material and the preparation method and application thereof. The material consists of the following raw materials in percentage by weight: 32%-34% of silicate cement, 8.8%-9% of calcium aluminate, 5%-7% of magnesium oxide, 0.5%-2% of sulfur trioxide, 0.2%-0.3% of polycarboxylate high performance water-reducing agent, 0.3%-0.7% of flocculant, 0.05%-0.2% of setting accelerator, 0.05%-0.2% of air-entraining agent, 0.05%-0.3% of rust inhibitor, 26%-31% of fine aggregate, 13%-18% of coarse aggregate, and 8.4%-8.5% of water. The material can be used for rapid repair of cement buildings in water conservancy projects, the repair material can be quickly set and the initial strength can be guaranteed.