Patent ID: 10290432

Abstract:
To fabricate a perovskite solar cell (PSC), a printable carbon electrode is formed on an uppermost layer, either a perovskite layer or an interface layer thereon, of a partially-completed PSC. A carbon ink is first prepared by dispersing carbon materials in a mixture of a polymer binder and a solvent. Then the carbon ink is screen-printed on the uppermost layer to form a wet film thereon. The wet film is baked with a baking temperature not exceeding 100° C. to evaporate the solvent to form the carbon electrode. Advantageously, the wet film is pressed with a pressure during baking such that the carbon electrode becomes denser and yields a lower sheet resistance when compared to one formed without being pressed. Preferably the pressure is at least 16,000 Pa. Experimental results show that the percentage reduction of sheet resistance can reach 40%.