Patent ID: 10427457

Abstract:
A tire comprising an outer tread layer, intermediate sidewall and carcass layers and an innermost air permeation prevention layer: (i) the air permeation prevention (APP) layer having an upper and a lower surface, the layer having a polymer composition exhibiting an air permeation coefficient (APC) of about 25×10−12 cc cm/cm2 sec cmHg (at 30° C.) or less and a Young's modulus of about 1 MPa to about 500 MPa, the polymer composition comprising: (A) at least 10 wt % of at least one thermoplastic resin component having an APC of about 25×10−12 cc cm/cm2 sec cmHg (at 30° C.) or less and a Young's modulus of more than 500 MPa, which is preferably a polyamide resin or mixture, and (B) at least 10 wt % of at least one elastomer component having an APC of more than about 25×10−12 cc cm/cm2 sec cmHg (at 30° C.) and a Young's modulus of not more than 500 MPa, which elastomer component is preferably a halogen-containing rubber or mixture, the total amount (A)+(B) being not less than about 30 wt %, and the elastomer component is a dispersed vulcanized, discontinuous phase in the thermoplastic resin matrix; and (ii) at least one thermoplastic laminate layer bonded to at least said lower surface of the APP layer, the thermoplastic layer comprising a film-forming, semi-crystalline, substantially hydrophobic carbon chain polymer having a glass transition temperature, Tg, of less than about −20° C.