Patent ID: 10927436

Abstract:
An aluminum alloy consisting essentially of from greater than 6 wt % to about 12.5 wt % silicon; iron present in an amount up to 0.15 wt %; from about 0.1 wt % to about 0.4 wt % chromium; from about 0.1 wt % to about 3 wt % copper; from about 0.1 wt % to about 0.5 wt % magnesium; from about 0.05 wt % to about 0.1 wt % titanium; less than 0.01 wt % of strontium; and a balance of aluminum and inevitable impurities. The aluminum alloy contains no vanadium. A method for increasing ductility and strength of an aluminum alloy without using vacuum and a T7 heat treatment, the method comprising: casting the molten aluminum alloy by a high pressure die-cast process to form a cast structure. The structural castings formed of the aluminum alloy composition disclosed herein exhibit desirable mechanical properties, such as high strength and high ductility/elongation.