Patent ID: 10961600

Abstract:
Provided herein is a plated steel sheet having a yield ratio, strength (tensile strength), elongation, hole expansibility, and CTS. A method for producing the plated steel sheet is also provided, among others. A steel sheet of a specific composition is provided that has a micro structure containing 70 to 90% of ferrite, 5 to 20% of martensite, 5% or less of retained austenite, 10% or less of bainite, and 5% or less of perlite by volume. The ferrite has an average crystal grain diameter of 20 μm or less. The martensite has an average crystal grain diameter of 5 μm or less. The retained austenite has an average crystal grain diameter of 5 μm or less. The bainite has an average crystal grain diameter of 7 μm or less. The steel sheet has a tensile strength of 590 MPa or more.