Patent ID: 10017840

Abstract:
A copper alloy of the present invention contains 5.00 to 8.00 atomic percent of Zr and includes Cu and a Cu—Zr compound, and two phases of the Cu and the Cu—Zr compound form a mosaic-like structure which includes no eutectic phase and in which when viewed in cross section, crystals having a size of 10 μm or less are dispersed. This copper alloy is formed by a manufacturing method including a sintering step of performing spark plasma sintering on a Cu—Zr binary system alloy powder at a temperature of 0.9 Tm ° C. or less (Tm(° C.): melting point of the alloy powder) by supply of direct-currant pulse electricity, the Cu—Zr binary system alloy powder having an average grain diameter of 30 μm or less and a hypoeutectic composition which contains 5.00 to 8.00 atomic percent of Zr. The Cu—Zr compound may include at least one of Cu5Zr, Cu9Zr2, and Cu8Zr3.