Patent ID: 11492679

Abstract:
This hot-rolled steel sheet has a predetermined chemical composition, in which in a case where the thickness is denoted by t, a metallographic structure at a t/4 position from the surface includes, by area fraction, 77.0% to 97.0% of bainite or tempered martensite, 0% to 5.0% of ferrite, 0% to 5.0% of pearlite, 3.0% or more of residual austenite, and 0% to 10.0% of martensite, in the metallographic structure, the average grain size excluding the residual austenite is 7.0 μm or less, the average number density of iron-based carbides having a diameter of 20 nm or more is 1.0×106 carbides/mm2 or more, a tensile strength is 980 MPa or more, and an average Ni concentration on the surface is 7.0% or more.