Patent ID: 11820172

Abstract:
A pneumatic tire comprises a tread rubber with a groove depth at a shoulder portion that comes into contact with a road surface of 10 mm or greater. A rubber composition of the tread rubber contains: 60 to 70 parts by mass of carbon black having a nitrogen adsorption specific surface area of 70 to 130 m2/g, 0.5 parts or greater by mass of sulfur, and a vulcanization accelerator per 100 parts by mass of diene rubber including 50 to 70 mass % of styrene-butadiene rubber, 20 to 30 mass % of butadiene rubber, and 10 to 30 mass % of natural rubber. The diene rubber has an average glass transition temperature of −65° C. or lower. A ratio of a compounded amount of the vulcanization accelerator to a compounded amount of the sulfur is 1.0 to 1.3. The tread rubber has a rubber hardness of 65 to 70 at 20° C.