Patent ID: 11114295

Abstract:
An epitaxial silicon carbide single crystal wafer having a small depth of shallow pits and having a high quality silicon carbide single crystal thin film and a method for producing the same are provided. The epitaxial silicon carbide single crystal wafer according to the present invention is produced by forming a buffer layer made of a silicon carbide epitaxial film having a thickness of 1 μm or more and 10 μm or less by adjusting the ratio of the number of carbon to that of silicon (C/Si ratio) contained in a silicon-based and carbon-based material gas to 0.5 or more and 1.0 or less, and then by forming a drift layer made of a silicon carbide epitaxial film at a growth rate of 15 μm or more and 100 μm or less per hour. According to the present invention, the depth of the shallow pits observed on the surface of the drift layer can be set at 30 nm or less.