Patent ID: 10544474

Abstract:
A high-strength cold-rolled steel sheet includes, as a component composition, by mass %: C: 0.075% to 0.300%; Si: 0.30% to 2.50%; Mn: 1.30% to 3.50%; P: 0.001% to 0.050%; S: 0.0001% to 0.0100%; Al: 0.001% to 1.500%; and N: 0.0001% to 0.0100%, in which a surface microstructure contains residual austenite of 3% to 10% and ferrite of 90% or less by volume fraction, an inner microstructure at a depth of t/4 from the surface assuming that a sheet thickness is t contains residual austenite of 3% to 20% by volume fraction, a ratio Hvs/Hvb between a surface hardness Hvs of the steel sheet surface and a hardness Hvb at a depth of ¼ of the thickness is more than 0.75 to 0.90, and a maximum tensile strength is 700 MPa or more.