Patent ID: 11486034

Abstract:
A method of preparing an ITO ceramic target includes that: In2O3 powder with mass fraction of 90˜97 and SnO2 powder with mass fraction of 10˜3 are ball-milled and mixed with deionized water, diluent, binder and polymer material by a sand mill to obtain an ITO ceramic slurry with a solid content between 70˜80% and a viscosity between 120˜300 mpa·s, with an average particle size D50 of the mixed powder controlled at 100˜300 nm; the ITO ceramic slurry is shaped by a pressure grouting to obtain an ITO ceramic green body with a relative density of 58˜62%; the ITO ceramic green body is put into a degreasing and sintering integrated furnace, and under a degreasing temperature of 700˜800° C., the ITO ceramic target is degreased in an atmospheric oxygen atmosphere for the time set to 12˜36 hours; the temperature increases from the degreasing temperature to the first sintering temperature of 1,600˜1,650° C.