Patent ID: 11359256

Abstract:
Provided are a high-strength cold-rolled steel sheet that has a tensile strength of 1320 MPa or more, excellent ductility and stretch flangeability, and a low failure rate in a hole expanding test, and a method for manufacturing the same. A high-strength cold-rolled steel sheet comprises a specific composition, wherein a total area ratio of ferrite and bainitic ferrite is 10% to 50%, an area ratio of retained austenite (RA) is more than 15% and 50% or less, an area ratio of tempered martensite is more than 15% and 60% or less, a ratio of RA with an aspect ratio of 0.6 or less is 70% or more, a ratio of RA with an aspect ratio of 0.6 or less in ferrite grain boundaries is 50% or more, and an average KAM value of bcc phase is 1° or less.