Patent ID: 11000894

Abstract:
A metal powder material containing no cobalt that is used to produce a three-dimensionally molded article from maraging steel in metal powder lamination molding. The metal powder material contains iron at 76 weight % or more, carbon at 0.03 weight % or less, silicon at 0.12 weight % or less, manganese at 0.12 weight % or less, nickel at 17 weight % or more and 19 weight % or less, molybdenum at 1.5 weight % or more and 2.5 weight % or less, titanium at 0.5 weight % or more and 2.0 weight % or less, aluminum at 1.5 weight % or less (including 0 weight %), with the remainder being inevitably incorporated impurities, and a content of impurities is less than 0.01 weight % for each impurity. Therefore, after aging treatment, the three-dimensionally molded article formed by the metal powder material of the present invention has characteristic of maraging steel, and sufficiently high hardness and relatively high tensile strength can be obtained.