Patent ID: 11351604

Abstract:
Methods for preparing a layered metal nanocomposite and a layered metal nanocomposite. The method includes mixing a magnesium salt and an aluminum salt to form a Mg2+/Al3+ solution. The Mg/Al has a molar ratio of between 0.5:1 to 6:1. Then a diamondoid compound is added to the Mg2+/Al3+ solution to form a reactant mixture. The diamondoid compound has at least one carboxylic acid moiety. The reactant mixture is heated at a reaction temperature for a reaction time to form a Mg/Al-diamondoid intercalated layered double hydroxide. The Mg/Al-diamondoid intercalated layered double hydroxide is thermally decomposed under a reducing atmosphere for a decomposition time at a decomposition temperature to form the layered metal nanocomposite.