Patent ID: 11426793

Abstract:
A method is provided to fabricate a high-power module. A non-touching needle is used to paste a slurry on a heat-dissipation substrate. The slurry comprises nano-silver particles and micron silver particles. The ratio of the two silver particles is 9:1˜1:1. The slurry is pasted on the substrate to be heated up to a temperature kept holding. An integrated chip (IC) is put above the substrate to form a combined piece. A hot presser processes thermocompression to the combined piece to form a thermal-interface-material (TIM) layer with the IC and the substrate. After heat treatment, the TIM contains more than 99 percent of pure silver with only a small amount of organic matter. No volatile organic compounds would be generated after a long term of use. No intermetallic compounds would be generated while the stability under high temperature is obtained. Consequently, embrittlement owing to procedure temperature is dismissed.