Patent ID: 10961611

Abstract:
A high-strength steel having a yield strength at a level of 800 MPa and a method of manufacturing the same, with the components and amounts thereof by weight percentage being: C: 0.06-0.14%, Si: 0.1-0.30%, Mn: 0.8-1.60%, Cr: 0.2-0.70%, Mo: 0.1-0.40%, Ni: 0-0.30%, Nb: 0.01-0.030%, Ti: 0.01-0.030%, V: 0.01-0.05%, B: 0.0005-0.0030%, Al: 0.02-0.06%, Ca: 0.001-0.004%, N: 0.002-0.005%, P≤0.02%, S≤0.01%, O≤0.008%, the balance of Fe and unavoidable impurities; wherein the above elements meet the following relationships: 0.40%<Ceq<0.50%, Ceq=C+Mn/6+(Cr+Mo+V)/5+(Ni+Cu)/15; 0.7%≤Mo+0.8Ni+0.4Cr+6V≤1.1%; 3.7≤Ti/N≤7.0; 1.0≤Ca/S≤3.0.