Patent ID: 11430870

Abstract:
After trench etching, trench corner portions are rounded by hydrogen annealing at a temperature of at least 1500 degrees C. Next, n-type regions that cause leak current and are formed in inner walls of the trenches by the hydrogen annealing are removed by a heat treatment (hydrogen etching) under a hydrogen atmosphere of a temperature less than 1500 degrees C. and the inner walls are planarized. Next, the inner walls are nitrided by introducing nitrogen into the heat treatment furnace while the temperature of the hydrogen-etching heat treatment decreases, thereby forming a SiN film along the inner walls. Next, an HTO film is formed, as gate insulating films, on the SiN film along the inner walls of the trenches. Thereafter, by PDA, an oxygen amount of an interface section of a SiO2/SiC interface is set to be at most 1.6×1015/cm2 and a nitrogen amount is set to more than 5.0×1014/cm2.