Patent ID: 11772154

Abstract:
A plunger for die casting may include a front injector end made of an iron alloy including, by mass: about 1% to about 6% nickel, about 0.1% to about 5% copper, about 0.2% to about 2.5% aluminum, about 0.5% to about 2% manganese, and about 0.05% to about 0.2% carbon. The iron alloy may be formed into an initial shape of the front injector end, heated to a temperature greater than or equal to about 900° C. and then cooled to form a supersaturated solid solution of iron and dissolved alloying elements. Then, the iron alloy may be heated at a temperature sufficient to precipitate intermetallic nanoparticles from the supersaturated solid solution to form an intermetallic precipitate phase dispersed throughout an iron-based matrix phase. A chemical compound layer may be formed at and along a surface of the iron alloy by exposing the iron alloy to an oxygen-containing and/or nitrogen-containing environment.