Patent ID: 11732319

Abstract:
Proposed is a non-oriented electrical steel sheet being low in iron loss and excellent in tensile strength and fatigue strength, which has a chemical composition comprising C: not more than 0.005 mass %, Si: 3 to 5 mass %, Mn: not more than 5 mass %, P: not more than 0.1 mass %, S: not more than 0.01 mass %, Al: not more than 3 mass %, N: not more than 0.005 mass %, Zn: 0.0005 mass % to 0.003 mass %, and the remainder being Fe and inevitable impurities, an average crystal grain size being not more than 40 μm, the number of the inclusions having a diameter of not less than 5 μm being not more than 5/mm2, a tensile strength being not less than 600 MPa, and the fatigue strength being not less than 450 MPa.