Patent ID: 11767601

Abstract:
A rapid method of synthesizing nanoflowers made of nanoflakes of nickel molybdate (NiMoO4) directly on nickel foam (NF) through an aerosol-assisted chemical vapor deposition (AACVD) process is disclosed. The nickel molybdate nanoflowers were grown on NF by varying the deposition time for 60 and 120 min at a fixed temperature of 480° C. and their efficiency was investigated as oxygen evolution reaction (OER) catalysts in 1 M KOH electrolyte. The NiMoO4 nanoflowers of NF obtained after 60 minutes of AACVD process showed OER performance with lowest overpotential of 320 mV to reach standard current density of 10 mA cm−2. The catalyst continuously performed the OER for 15 h, signifying its prominent stability under electrochemical conditions.