Patent ID: 10351927

Abstract:
The present invention relates to a hot-rolled steel sheet for a high strength galvanized steel sheet, having excellent surface quality, and a method for producing the same, the hot-rolled steel sheet comprising, by weight %: C: 0.05 to 0.15%, Si: 0.03 to 0.10%, Mn: 0.7 to 1.39%, P: 0.001 to 0.05%, S: 0.001 to 0.03%, Al: 0.002 to 0.035%, and the remainder being Fe and unavoidable impurities. The weight ratio of Mn/Si is 15 to 25, the weight ratio of C/Si is 1 to 5, and the weight ratio of Si/P is 3 to 10. The hot-rolled steel sheet has a microstructure consisting of, in area fraction, 10 to 40% of bainite, 20 to 30% of pearlite and 40 to 60% of ferrite, and includes a ternary eutectic compound of FeO, Fe2SiO4 and Fe3(PO)4 formed within 50 μm from the surface.