Patent ID: 11371164

Abstract:
Provided is a large diameter InP single crystal substrate having a diameter of 75 mm or more, which can achieve a high electrical activation rate of Zn over a main surface of the substrate even in a highly doped region having a Zn concentration of 5×1018 cm−3 or more; and a method for producing the same. An InP single crystal ingot is cooled such that a temperature difference of 200° C. is decreased for 2 to 7.5 minutes, while rotating the InP single crystal ingot at a rotation speed of 10 rpm or less, and the cooled InP single crystal ingot is cut into a thin plate, thereby allowing production of the InP single crystal substrate having an electrical activation rate of Zn of more than 85% over the main surface of the substrate even in a highly doped region having a Zn concentration of 5×1018 cm−3 or more.