Patent ID: 11117348

Abstract:
Provided is a high-strength hot-rolled coated steel sheet with excellent formability,A high-strength hot-rolled coated steel sheet has a constituent composition containing, in a mass percent, C: 0.03% to 0.15%, Si: 0.4% or less, Mn: 1.2% to 1.9%, Ti: 0.05% to 0.25%, B: 0.0005% to 0.0050%, P: 0.03% or less, S: 0.005% or less, Al: 0.005% to 0.4%, and N: 0.01% or less, the balance being Fe and incidental impurities. The total area fraction of one or more of ferrite and tempered bainite is 90% or more. The steel sheet has a structure in which the volume fraction of Ti carbides having particle sizes of 20 nm or less is 0.05 vol % or more.