Patent ID: 10865273

Abstract:
A thermoplastic elastomer contains (a) hard segments of a polyester and (b) soft segments containing repeating units derived from an aliphatic carbonate, wherein the thermoplastic elastomer exhibits a melt flow index (MFI) measured at 230° C. under a load of 10 kg (MFI 230° C./10 kg) according to ISO1133 (2011) of at most 40 g/10 min. The thermoplastic elastomer is produced by subjecting a precursor of the thermoplastic elastomer to solid state post reaction processing at a temperature between 140 and 170° C. until the thermoplastic elastomer has the required MFI of at most 40 g/10 min measured at 230° C. under a load of 10 kg (MFI 230° C./10 kg) according to ISO1133 (2011).