Patent ID: 10920293

Abstract:
Provided herein is a plated steel having high strength with excellent elongation, excellent hole expansibility, and excellent material uniformity, and a method for producing such a plated steel. The steel sheet provided herein has a specific composition, and a steel structure that contains ferrite as a primary phase, and 2 to 12% of perlite, and 3% or less of martensite by volume, and in which the remainder is a low-temperature occurring phase. The ferrite has an average crystal grain diameter of 25 μm or less. The perlite has an average crystal grain diameter of 5 μm or less. The martensite has an average crystal grain diameter of 1.5 μm or less. The perlite has a mean free path of 5.5 μm or more. The steel sheet has a tensile strength of 440 MPa or more.