Patent ID: 10801571

Abstract:
The present invention provides a friction material used for a disc brake pad, which is able to secure the braking effectiveness and the wear resistance under the high speed and high load braking conditions while satisfying laws and regulations relating to the required amount of the content of the copper component. A friction material used for a disc brake pad, which is manufactured by forming a non-asbestos organic friction material composition, in which the friction material composition contains 1-15 weight % of ferrous sulfide (FeS) particles relative to the total amount of the friction material composition as a lubricant, and the total amount of the copper component involved in the friction material composition is less than 5 weight % relative to the total amount of the friction material composition. Furthermore, it is preferable to contain 0.3-5 weight % of flaky graphite particles with 1-100 μm of average particle diameter or the aggregates thereof relative to the total amount of the friction material composition.