Patent ID: 11898218

Abstract:
Provided is a material for hot stamping including: a steel sheet including carbon (C) in an amount of 0.28 wt % to 0.50 wt %, silicon (Si) in an amount of 0.15 wt % to 0.70 wt %, manganese (Mn) in an amount of 0.5 wt % to 2.0 wt %, phosphorus (P) in an amount less than or equal to 0.05 wt %, sulfur (S) in an amount less than or equal to 0.01 wt %, chromium (Cr) in an amount of 0.1 wt % to 0.5 wt %, boron (B) in an amount of 0.001 wt % to 0.005 wt %, balance iron (Fe), and other inevitable impurities; and fine precipitates distributed in the steel sheet, wherein the fine precipitates include nitride or carbide of at least one of titanium (Ti), niobium (Nb), and vanadium (V), and trap hydrogen.