Patent ID: 11505844

Abstract:
A cold-rolled steel plate (1) and a manufacturing method therefor. The chemical composition of the steel plate (1) in percentage by weight is: C 0.15-0.25%, Si 1.50-2.50%, Mn 2.00-3.00%, P≤0.02%, S≤0.01%, Al 0.03-0.06%, N≤0.01%, with the balance being Fe and impurities. The surface layer has an inner oxide layer (2) with a thickness of 1-5 μm, and there is no enrichment of Si or Mn on the surface. The steel plate (1) has good phosphating performance and formability, with a tensile strength of ≥1180 MPa and an elongation of ≥14%, and has a complex-phase structure of ferrite, martensite, and retained austenite, the content of the retained austenite being not lower than 5%. A dew point is at −25° C. to 10° C. in continuous annealing, such that external oxidation transitions to internal oxidation.