Abstract:
A method for the heat treatment of a steel reinforcing element (F) for a tire, comprises a step of reducing the temperature of the reinforcing element by continuous cooling: from an initial temperature of the austenite range, to a final temperature of the ferrite-pearlite range, passing through at least one transformation range of the steel, the transformation range(s) being distinct from the bainite range. The temperature reduction step comprises a transformation (C2, C3) from the austenitic microstructure to the ferritic-pearlitic microstructure. The temperature of the reinforcing element is strictly decreasing during the reduction step. The mean rate of temperature reduction during the transformation (C2, C3) of the steel microstructure is greater than or equal to 30° C.·s−1 and less than or equal to 110° C.·s−1.