Patent ID: 11578377

Abstract:
A grain-oriented electrical steel sheet having excellent iron loss property is produced from a steel slab containing, by mass %, C: 0.002-0.15%, Si: 2.5-6.0%, Mn: 0.01-0.80%, Al: 0.010-0.050% and N: 0.003-0.020%, when: a heating rate between 500-700° C. in decarburization annealing is not less than 80° C./s, a surface roughness Ra of a work roll in final cold rolling is 0.01-3.0 μm, a total content of alkaline earth metals to MgO in annealing separator is 0-5 mass %, an average length L in rolling direction of passed crystal grains is not more than 25 mm, a ratio of crystal grains having a length in rolling direction of not more than 5 mm is 40-90%, and an existence ratio of alkaline earth metal sulfides having a size corresponding to circle of not less than 0.5 μm in a cross section of forsterite film is not more than 0.2/μm per unit length in sheet width direction.