Patent ID: 11462367

Abstract:
Provided is a method of manufacturing a contact material, including the steps of: forming a Ni alloy film having a film thickness of 40 nm or more and 110 nm or less on a surface of WC powder having an average particle diameter of 2 μm or more and 10 μm or less by an electroless Ni plating method; performing heat treatment for degassing at a temperature of 500° C. or more and 860° C. or less; crushing Ni alloy-coated WC powder after the heat treatment; mixing the crushed Ni alloy-coated WC powder and Cu powder having an average particle diameter of 1 μm or more and 100 μm or less; and compressing the resultant mixture, followed by sintering the mixture at a temperature of more than 1,083° C. and less than 1,455° C.