A method for tuning characteristics of a polyamide nanofiber nonwoven comprising the step of targeting a specific average nanofiber diameter and/or a specific relative viscosity for the polyamide nanofiber nonwoven. The specific average nanofiber diameter is within a range from 100 nm to 1000 nm and/or the specific relative viscosity is within a range from 5 to 75, e.g., from 15 to 50. The process further comprises the steps of extruding a polyamide composition having a moisture content with a pressurized gas through a fiber forming channel having a channel temperature to form the polyamide nanofiber nonwoven having the target average nanofiber diameter and/or relative viscosity and controlling the moisture content, the pressure of pressurized gas, and/or the channel temperature based on the specific average nanofiber diameter and/or the specific relative viscosity.