A preparation method of a ceramic membrane support is disclosed. Take aluminum hydroxide, produced through a carbon decomposing process by a sintering method, as a raw material, pre-sinter the aluminum hydroxide, and obtain a low-temperature alumina product A; add a first amount of mineralizer into the product A, grind after calcining the added product A, and obtain a α-alumina product B; mix the product B with Al2O3.nH2O, calcine after adding a second amount of mineralizer into the mixed product B, and obtain a α-alumina product C; grind, scatter and grade the calcined and heat-preserved α-alumina product C, and obtain polyhedral alumina powders; mix the polyhedral alumina powders, water, humectant and dispersant and then sinter, and finally obtain the porous alumina support. The prepared support is easy to be sintered, is high in alumina purity, is good in corrosion resistance, and is improved in porosity and flux.