Patent ID: 11088320

Abstract:
A process flow for forming magnetic tunnel junction (MTJ) cells with a critical dimension CD≤60 nm by using a top electrode (TE) hard mask having a thickness≥100 nm prior to MTJ etching is disclosed. A carbon hard mask (HM), silicon HM, and photoresist are sequentially formed on a MTJ stack of layers. A pattern of openings in the photoresist is transferred through the Si HM with a first reactive ion etch (RIE), and through the carbon HM with a second RIE. After TE material is deposited to fill the openings, a chemical mechanical process is performed to remove all layers above the carbon HM. The carbon HM is stripped and the resulting TE pillars are trimmed to a CD≤60 nm while maintaining a thickness proximate to 100 nm. Thereafter, an etch process forms MTJ cells while TE thickness is maintained at ≥70 nm.