Patent ID: 11525169

Abstract:
A non-oriented electrical steel sheet with an average magnetostriction λp-p at 400 Hz and 1.0 T of not more than 4.5×10−6, and area ratio of recrystallized grains at a section in rolling direction of steel sheet of 40 to 95% and an average grain size of 10 to 40 μm is obtained by subjecting a steel slab containing, in mass %, C: not more than 0.005%, Si: 2.8 to 6.5%, Mn: 0.05 to 2.0%, Al: not more than 3.0%, P: not more than 0.20%, S: not more than 0.005%, N: not more than 0.005%, Ti: not more than 0.003%, V: not more than 0.005% and Nb: not more than 0.005% and satisfying Si—2Al—Mn≥0 to hot rolling, hot-band annealing, cold rolling and finish annealing under adequate cold rolling and finish annealing conditions, and a motor core is manufactured by such a steel sheet.