Patent ID: 10501830

Abstract:
Provided is a high-strength cold-rolled steel sheet having excellent ductility and stretch-flangeability as well as weldability in a range in which a tensile strength is 980 MPa or higher and a 0.2% yield strength is 700 MPa or higher. In the high-strength cold-rolled steel sheet of the present invention, the chemical composition is adjusted as appropriate, and the area ratio of below-mentioned metal structures at a position of ¼ sheet thickness in the steel sheet satisfies following requirements: tempered martensite: 30 area % or more, bainite: 15 area % to 70 area %, total of tempered martensite and bainite: 90 area % or more, ferrite: 0 area % to 5 area %, and retained austenite: 0 area % to 4 area %. The high-strength cold-rolled steel sheet has excellent ductility, stretch-flangeability, and weldability, and has a tensile strength of 980 MPa or higher and a 0.2% yield strength of 700 MPa or higher.