Patent ID: 11286568

Abstract:
A film forming treatment agent for a composite chemical conversion film for magnesium alloy, and a film forming process method, and a composite chemical conversion film are provided. Components of the film forming treatment agent for a composite chemical conversion film for magnesium alloy comprise a water solution and a suspension of reduced graphene oxide flakes to the water solution. The water solution comprises strontium ions at 0.1 mol/L to 2.5 mol/L and phosphate ions at 0.06 mol/L to 1.5 mol/L, and pH of the water solution is 1.5 to 4.5. Concentration of the reduced graphene oxide varies between 0.1 mg/L and 5 mg/L. The film forming process method for a composite chemical conversion film for magnesium alloy comprises the following steps of: 1) pretreatment on surface of magnesium alloy matrix; 2) immersion of magnesium alloy matrix in the film forming treatment agent; and 3) removal of magnesium alloy pieces for drying in air. The composite chemical conversion film for magnesium alloy is formed by immersing magnesium alloy matrix in the film forming treatment agent. The composite chemical conversion film for magnesium alloy has excellent corrosion-resistance performance in 3.5 wt % NaCl solution.