Patent ID: 11905359

Abstract:
A polyurethane elastomer, which can be a foam, generated from (a) an organic diisocyanate, (b) a polyester resin, (c) a chain extender comprised of a polyhydric alcohol, (d) a crosslinker, (e) a plasticizer, (f) a surfactant, (g) a bio-additive, (h) a blowing agent, and (i) an optional dye; and optionally where the elastomer has, for example, a hardness value of, for example, from about 15 Asker C to about 60 Asker C, a tensile strength of from about 1 MPa to about 10 MPa, a resilience of from about 30 percent to about 60 percent, an elongation at break of from about 150 percent to about 700 percent, and a tear strength from about 2 Newtons/millimeters to about 4 Newtons/millimeters, and which elastomers can be selected for footwear.