Patent ID: 11566313

Abstract:
Provided is a method for manufacturing an Ni-based alloy member in which the equilibrium amount of γ′ phase precipitation at 700° C. is from 30 to 70 volume %. The method includes the steps of preparing an Ni-based alloy powder having a predetermined chemical composition; forming a precursor body wherein an average grain diameter of the γ phase grains is 50 μm or less, by using the Ni-based alloy powder; and heating the precursor body to a temperature at least the γ′ phase solvus temperature and subsequently slow-cooling the heated precursor body from the temperature to a temperature at least 100° C. lower than the γ′ phase solvus temperature at a cooling rate of 100° C./h or lower. There is obtained a softened body in that the γ′ phase particles of at least 20 volume % precipitate between/among the γ phase grains having an average grain diameter of 50 μm or less.