Abstract:
There is provided a steel material that is excellent in machinability, and that provides a high roller-pitting fatigue strength, a high high-cycle bending fatigue strength, and a high low-cycle bending fatigue strength when being subjected to induction hardening to be produced into an induction-hardened component. The steel material according to the present disclosure includes a chemical composition consisting of, in mass %, C: 0.40 to 0.70%, Si: 0.15 to 2.10%, Mn: 0.30 to 1.15%, Cr: 0.01 to less than 0.50%, S: 0.005 to 0.070%, N: 0.0020 to 0.0200%, Ti: 0.0080 to 0.2000%, B: 0.0005 to 0.0050%, Al: 0.005 to 0.100%, and P: less than 0.050%, with the balance being Fe and impurities, and satisfying Formula (1) to Formula (5) described herein, and has a ferrite area fraction of 40% or less and a martensite area fraction of 10% or less.