Patent ID: 11453927

Abstract:
A cold rolled steel sheet having a high strength, an aging resistance, a high yield ratio and a small anisotropy of tensile strength is obtained by hot rolling and cold rolling a steel material containing in percent by mass C: 0.06-0.14%, Si: less than 0.50%, Mn: 1.6-2.5%, Nb: not more than 0.080% (including 0%), Ti: not more than 0.080% (including 0%), provided that Nb and Ti are contained in an amount of 0.020-0.080% in total, subjecting a cold rolled steel sheet continuous annealing including steps of soaking-annealing at a temperature of 840-940° C. for a holding time of 30-120 seconds, cooling from the soaking temperature to 600° C. at a rate of not less than 5° C./s, retaining in a temperature range of 600-500° C. for 30-300 seconds and then conducting a secondary cooling to apply such a steel structure that martensite is finely dispersed into ferrite base.