Patent ID: 11230744

Abstract:
A steel sheet having excellent fatigue resistance as a material for automobile parts and a TS of 590 MPa or more, and a method for producing the same. The steel sheet has a composition comprising, by mass %, C: 0.04% or more and 0.15% or less, Si: 0.3% or less, Mn: 1.0% or more and 2.6% or less, P: 0.1% or less, S: 0.01% or less, Al: 0.01% or more and 0.1% or less, N: 0.015% or less, one or two of Ti and Nb: 0.01% or more and 0.2% or less in a total, and the balance being Fe and unavoidable impurities. The steel sheet has 50% or more of ferrite and 10% or more and 50% or less of martensite in terms of an area ratio, and a microstructure in which a standard deviation of nano-hardness is 1.50 GPa or less and tensile strength of 590 MPa or more.