Patent ID: 11795518

Abstract:
Provided are a non-oriented electrical steel sheet with which it is possible to improve steel sheet transferability even when punching is performed successively at high speed, and a method of manufacturing a stacked core using the same. The non-oriented electrical steel sheet contains, by mass percent, Si: 2.0 to 5.0%, Mn: 0.4 to 5.0%, Al≤3.0%, C: 0.0008 to 0.0100%, N≤0.0030%, S≤0.0030%, and Ti≤0.0060%, wherein the product of the contents of Mn and C is 0.004 to 0.05 mass %2, the yield strength in rolling direction is more than or equal to 600 MPa, and the Young's modulus is more than or equal to 200 GPa. In the method of manufacturing a stacked core, when manufacturing a stacked core using a progressive die, the steel sheet transfer speed V (m/s) satisfies expression (1). V: VMIN to VMAX (1) VMAX=( 1/25)√(t2×E×YS) (2) VMIN=( 1/25)√(t2×120000) (3) t: Steel sheet thickness (mm), E: Young's ratio (GPa), YS: Yield strength (MPa).