Patent ID: 11912630

Abstract:
The present invention provides a method of preparing a recycled cementitious material by a phosphogypsum-assisted carbon sequestration pretreatment process. The method includes: (1) placing 100 mass parts of phosphogypsum, 1 to 2 mass parts of grinding aid, 10 to 20 mass parts of sodium-containing alkali component, 150 to 300 mass parts of zirconia balls, and 150 to 300 mass parts of water into a wet grinding tank for wet grinding. After 10 min to 30 min of wet grinding, introducing CO2 at a flow rate of 1.5 to 2.2 mass parts/min to keep a temperature of a wet grinding slurry below 40° C. When the wet grinding slurry reaches pH=10, ending the wet grinding and sieving out a wet grinding slurry; (2) mixing the wet grinding slurry with 700 to 1000 mass parts of slag and 100 to 350 mass parts of water to obtain a recycled cementitious material.