Patent ID: 10106871

Abstract:
A Ni-based alloy tube includes a base metal having a chemical composition consisting, by mass percent, of C: 0.15% or less, Si: 1.0% or less, Mn: 2.0% or less, P: 0.030% or less, S: 0.030% or less, Cr: 10.0 to 40.0%, Ni: 50.0 to 80.0%, Ti: 0.50% or less, Cu: 0.60% or less, Al: 0.20% or less, N: 0.20% or less, and the balance: Fe and impurities; and a low Cr content complex oxide film having a thickness of 25 nm or smaller at least on an inner surface of the base metal, wherein contents of Al, Ni, Si, Ti, and Cr in the film satisfy [at % Al/at % Cr≤2.00], [at % Ni/at % Cr≤1.40], and [(at % Si+at % Ti)/at % Cr≥0.10].