Patent ID: 10040145

Abstract:
When two high-strength steel sheets (1A, 1B) whose sheet thickness ratio={the sum of sheet thicknesses of the steel sheets}/{the sheet thickness of the thinner steel sheet (when they have the same thickness, the sheet thickness per one sheet)} is within a range of not less than 2 nor more than 5 and which both have tensile strength of not less than 780 MPa nor more than 1850 MPa are stacked to be subjected to resistance spot welding, a first welding step being pre-welding with a pressurizing force P1 kN and a welding current I1 kA and a second welding step being main welding with a pressurizing force P2 kN and a welding current I2 kA are performed, the pressurizing forces P1, P2 are set to a fixed pressurizing force P=P1=P2 all through the first welding step and the second welding step and are set within a range expressed by {0.5≤P≤3.0t(1/3)}, where t mm is an average sheet thickness of the steel sheets (1A, 1B), the welding current I1 is set within a range of not less than 30% nor more than 90% of the welding current I2, and the second welding step is started within 0.1 s after the first welding step is finished.