Patent ID: 11525174

Abstract:
Disclosed is a grain-oriented electrical steel sheet that has excellent high-frequency iron loss properties and blanking workability. The steel sheet includes: steel components including, by mass %, Si: 1.5-8.0%, Mn: 0.02-1.0%, and at least one selected from Sn: 0.010-0.400%, Sb: 0.010-0.400%, Mo: 0.010-0.200%, and P: 0.010-0.200%; and crystal grains including coarse secondary recrystallized grains having an average grain size of 5 mm or more and fine grains having a grain size of 0.1-2.0 mm, wherein at least some of the coarse secondary recrystallized grains penetrate the steel sheet in a thickness direction and are respectively exposed on front and back surfaces of the steel sheet such that projection planes of the exposed surfaces of these coarse secondary recrystallized grains on the front and back surfaces form an overlapping region, and the fine grains are present at a number density per unit area of 0.6-40 pieces/cm2.