Patent ID: 10156024

Abstract:
Disclosed is a self-supporting zinc oxide substrate composed of a plate composed of a plurality of zinc-oxide-based single crystal grains, wherein the plate has a single crystal structure in an approximately normal direction, and the zinc-oxide-based single crystal grains have a cross-sectional average diameter of greater than 1 μm. This substrate can be manufactured by a method comprising providing an oriented polycrystalline sintered body; forming a layer with a thickness of 20 μm or greater composed of zinc-oxide-based crystals on the oriented polycrystalline sintered body so that the layer has crystal orientation mostly in conformity with crystal orientation of the oriented polycrystalline sintered body; and removing the oriented polycrystalline sintered body to obtain the self-supporting zinc oxide substrate. The present invention can provide a self-supporting zinc oxide substrate being inexpensive and also suitable for having a large area as a preferable alternative material for a zinc oxide single crystal substrate.