Patent ID: 10801085

Abstract:
A high-strength steel sheet having high yield ratio, excellent stretch flange formability, and resistance to secondary working embrittlement. The steel sheet has a composition containing C: 0.02% to less than 0.10%, Si: less than 0.3%, Mn: less than 1.0%, P: 0.10% or less, S: 0.020% or less, Al: 0.01% to 0.10%, N: 0.010% or less, and Nb: 0.003% to less than 0.070% on a mass basis, the remainder being Fe and inevitable impurities. A steel microstructure of the steel sheet contains ferrite: 90% or more and a total of pearlite, martensite, retained austenite, and cementite: 0% to 10% on an area fraction basis, in which the average grain size of the ferrite is 15.0 μm or less, and in which the average aspect ratio of the ferrite is 1.2 or more; and a tensile strength of 500 MPa or less.