Patent ID: 11414339

Abstract:
An alkali free glass has an average coefficient of thermal expansion at 50 to 350° C. of 30×10−7 to 43×10−7/° C., a Young's modulus of 88 GPa or more, a strain point of 650 to 725° C., a temperature T4 at which a viscosity reaches 104 dPa·s of 1,290° C. or lower, a glass surface devitrification temperature (Tc) of T4+20° C. or lower, and a temperature T2 at which the viscosity reaches 102 dPa·s of 1,680° C. or lower. The alkali free glass contains, as represented by mol % based on oxides, 62 to 67% of SiO2, 12.5 to 16.5% of Al2O3, 0 to 3% of B2O3, 8 to 13% of MgO, 6 to 12% of CaO, 0.5 to 4% of SrO, and 0 to 0.5% of BaO. MgO+CaO+SrO+BaO is 18 to 22%, and MgO/CaO is 0.8 to 1.33.