Patent ID: 10984932

Abstract:
An amorphous soft magnetic alloy of the formula (Fe1-αTMα)100-w-x-y-zPwBxLySiz TipCqMnrCus, wherein TM is Co or Ni; L is Al, Cr, Zr, Mo or Nb; 0≤α≤0.3, 2≤w≤18 at %, 2≤x≤18 at %, 15≤w+x≤23 at %, 1<y≤5 at %, 0≤z≤4 at %; p, q, r, and s represents an addition ratio such that the total mass of Fe, TM, P, B, L and Si is 100, and 0≤p≤0.3, 0≤q≤0.5, 0≤r≤2, 0≤s≤1 and r+s>0; the composition fulfills one of the following conditions: L is Cr, Zr, Mo or Nb; or L is a combination of Al and Cr, Zr, Mo or Nb, wherein 0<Al≤5 at %, 1≤Cr≤4 at %, 0<Zr≤5 at %, 2≤Mo≤5 at %, and 2≤Nb≤5 at %; the alloy has a crystallization start temperature (Tx) which is 550° C. or less, a glass transition temperature (Tg) which is 520° C. or less, and a supercooled liquid region represented by ΔTx=Tx−Tg, which is 20° C. or more.