Patent ID: 11981975

Abstract:
Provided is a method for manufacturing a steel sheet, the method including: reheating a steel slab at a temperature of 1200° C. to 1350° C., the steel slab including, by weight %, carbon (C): 0.05% to 0.14%, silicon (Si): 0.01% to 1.0%, manganese (Mn): 1.5% to 2.5%, aluminum (Al): 0.01% to 0.1%, chromium (Cr): 0.005% to 1.0%, phosphorus (P): 0.001% to 0.05%, sulfur (S): 0.001% to 0.01%, nitrogen (N): 0.001% to 0.01%, niobium (Nb): 0.005% to 0.06%, titanium (Ti): 0.005% to 0.11%, and a balance of iron (Fe) and inevitable impurities; finish hot rolling the reheated steel slab under predetermined conditions to obtain a hot-rolled steel sheet; cooling the hot-rolled steel sheet at a cooling rate of 10° C./s to 100° C./s to a temperature of 400° C. to 500° C. after the finish hot rolling; and coiling the steel sheet at a temperature of 400° C. to 500° C. after the cooling.