Patent ID: 10724125

Abstract:
Spring steel includes: as a chemical composition, by mass %, C: 0.40% to 0.60%, Si: 0.90% to 2.50%, Mn: 0.20% to 1.20%, Cr: 0.15% to 2.00%, Ni: 0.10% to 1.00%, Ti: 0.030% to 0.100%, B: 0.0010% to 0.0060%, N: 0.0010% to 0.0070%, Cu: 0% to 0.50%, Mo: 0% to 1.00%, V: 0% to 0.50%, Nb: 0% to 0.10%, P: limited to less than 0.020%, S: limited to less than 0.020%, Al: limited to less than 0.050%, and a remainder including Fe and impurities, in a case where [Ti] represents a Ti content and [N] represents a N content by mass %, the chemical composition satisfies ([Ti]−3.43×[N])>0.03, and a total number density of a Ti carbide and a Ti carbonitride having a diameter of 5 nm to 100 nm is more than 50 piece/μm3.