Patent ID: 10837077

Abstract:
The present invention provides steel sheet excellent in cold formability and ductility after heat treatment and a method for production thereof. The steel sheet of the present invention is steel sheet which has a chemical composition containing, by mass %, C: 0.10 to 0.40%, Si: 0.30 to 1.00%, Mn: 0.30 to 1.00%, Al: 0.001 to 0.10%, P: 0.0001 to 0.02%, and S: 0.0001 to 0.01% and having a balance of Fe and impurities, which steel sheet characterized in that a ratio (B/A) of the number of carbides at the ferrite grain boundaries (B) to the number of carbides inside the ferrite grains (A) is over 1, a ferrite grain size is 5 μm to 50 μm, an average grain size of carbides is 0.4 μm to 2.0 μm, a pearlite area ratio is 6% or less, and a Vicker's hardness is 120 HV to 170 HV.