Patent ID: 10808153

Abstract:
The invention relates to a thermally curable adhesive compound consisting of the following components: (A) 4.9 to 34.9 wt % (relative to the total amount of the curable adhesive compound) of an epoxide-functionalized (co)polymer having a weight-average molar mass in the range of 5,000 g/mol to 200,000 g/mol, based on more than 30 to 100 wt %, preferably 50 to 100 wt %, (relative to the total amount of the monomers on which the epoxide-functionalized (co)polymer is based) of at least one type of (meth)acrylic (co)monomer (a) functionalized with an epoxy group, (B) 0.1 to 5 wt % (relative to the total amount of the curable adhesive compound) of at least one thermally activatable curing agent for a cationic curing of epoxides, (C) 65 to 95 wt % (relative to the total amount of the curable adhesive compound) of at least one type of matrix polymer as a film-forming agent, (D) optionally 0 to 30 wt % of additional components.