Patent ID: 10018221

Abstract:
A fracture-separated engine component and a method for manufacturing same is described. The engine component includes first and second parts each having a fracture surface extending along a fracture plane. Prior to fracture separation, the engine component is case-hardened by nitriding and has a nitriding hardness depth of 0.4 to 0.7 mm. After the nitriding, the engine component is cooled such that each one of the subsequent fracture surfaces reaches a temperature below −100° C. The fracture separation is then performed. After, the engine component has two fracture surfaces along a fracture plane, the fracture surfaces having hardened peripheral areas and unhardened core sections. No point of the unhardened core sections located in the fracture plane is located at a distance greater than 1.1 mm from a nearest hardened peripheral area. Each one of the fracture surfaces includes elongated partial fracture surfaces with a width of less than 3.2 mm.