Patent ID: 11476432

Abstract:
Provided are an inverted thick 2D hybrid perovskite solar cell insensitive to film thickness and a preparation method thereof, belonging to the field of organic-inorganic hybrid perovskite materials. The solar cell adopts a 2D hybrid perovskite thick-film material as a light absorption layer having thickness in a range of 500-800 nm, which is conducive to the full absorption of sunlight. The thick-film film material can be deposited from a precursor solution added with guanidine hydroiodide, and is composed of large grains growing along the thickness direction. The solar cell with an inverted structure prepared by using the thick-film material as a light absorption layer has an efficiency fluctuation less than 5% in a film thickness range of 500-800 nm. This is of great value for the preparation of high-performance hybrid perovskite solar cells by a large-area solution method.