Patent ID: 11466145

Abstract:
A cellulose-fiber-dispersing polyolefin resin composite material, containing a polyolefin resin and a cellulose fiber dispersed in the polyolefin resin, in which the composite material contains the cellulose fiber of 3 mass % or more and less than 70 mass %, and when the composite material is subjected to the abrasion test according to ISO 6722 under the following test conditions, the amount of abrasion after 5,000 reciprocations satisfies the [Formula 1]: (Amount of abrasion [mm] of the cellulose-fiber-dispersing polyolefin resin composite material)<−0.003×(Cellulose effective mass ratio of the cellulose-fiber-dispersing polyolefin resin composite material)+0.3,[Test Conditions for Abrasion Test]Load: 1.7 kg, Needle diameter: φ0.45 mm, Stroke length: 10 mm, Period: 60 reciprocations/min, Test piece: length 38 mm×width 6 mm×thickness 1 mm, Temperature: 23° C.