Patent ID: 11408044

Abstract:
There is provided a high-strength steel sheet and a method for producing the same. The high-strength steel sheet has a specified chemical composition and a steel microstructure including, by area fraction, 75.0% or more tempered martensite, 1.0% or more and 20.0% or less fresh martensite, and 5.0% or more and 20.0% or less retained austenite. A hardness ratio of the fresh martensite to the tempered martensite is 1.5 or more and 3.0 or less, the ratio of the maximum KAM value in the tempered martensite in the vicinity of the heterophase interface between the tempered martensite and the fresh martensite to the average KAM value in the tempered martensite is 1.5 or more and 30.0 or less, and the average of ratios of grain sizes of prior austenite grains in the rolling direction to those in the thickness direction is 2.0 or less.