Patent ID: 11566125

Abstract:
Provided is a thermoplastic elastomer composition which does not undergo viscosity increase during melt molding, gelation and molding failure, while having excellent heat resistance and durability. A thermoplastic elastomer composition for tires, which contains (A) an ethylene-vinyl alcohol copolymer or a modified ethylene-vinyl alcohol copolymer, (B) a thermoplastic resin or a thermoplastic elastomer, which has a melting point of 200° C. or higher, and (C) an acid-modified elastomer in an amount of 20% by volume or more based on the amount of all polymer components. This thermoplastic elastomer composition for tires is characterized in that if this thermoplastic elastomer composition for tires is extruded at a piston speed of 5 min/min at a temperature that is higher than the melting point of the thermoplastic resin or thermoplastic elastomer (B) by 20° C. in a viscosity measurement by means of a capillary rheometer, the viscosity η2 in 800 seconds after the start of the extrusion is less than 120% of the viscosity η1 in 200 seconds after the start of the extrusion.