Patent ID: 10490324

Abstract:
In an alloy for an R-T-B-based rare earth sintered magnet of the present invention formed of a rare earth element R, a transition metal T containing Fe as a main component, a metal element M containing one or more types of metals selected from Al, Ga, and Cu, and B and inevitable impurities, 13 at % to 16 at % of R is contained, 4.5 at % to 6.2 at % of B is contained, 0.1 at % to 2.4 at % of M is contained, the balance is T and the inevitable impurities, a proportion of Dy in the entire rare earth element is 0 at % to 65 at %, Formula 1 described below is satisfied, a main phase containing R2Fe14B and an alloy grain boundary phase containing more R than the main phase are included, and a distance between the alloy grain boundary phases is greater than or equal to 3 μm and less than or equal to 11 μm. 0.30≤B/TRE≤0.37  (Formula 1)