Patent ID: 11577964

Abstract:
Process for preparing alumina gel in a single precipitation step consisting of dissolving an aluminium precursor, aluminium chloride, in water, at a temperature of 10° C. to 90° C. such that the pH of the solution is from 0.5 to 5, for a period of 2 to 60 minutes, then adjusting the pH to 7.5 to 9.5 by adding a basic precursor, sodium hydroxide, to the solution obtained to obtain a suspension, at a temperature of 5° C. to 35° C., and for 5 minutes to 5 hours, followed by a filtration step, said process not comprising any washing steps. Also, novel alumina gel having a high dispersibility index, in particular a dispersibility index of more than 80%, a crystallite dimension of 0.5 to 10 nm, a chlorine content of 0.001% to 2% by weight and a sodium content of 0.001% to 2% by weight, the percentages by weight being expressed with respect to the total weight of the alumina gel.