Patent ID: 11279986

Abstract:
Provided is a cold-rolled high-strength steel having a tensile strength of not less than 1500 MPa and an excellent formability, the chemical elements thereof having the following mass percent ratios: 0.25%-0.40% of C, 1.50%-2.50% of Si, 2.0%-3.0% of Mn, 0.03%-0.06% of Al, P≤0.02%, S≤0.01%, N≤0.01% and at least one of 0.1%-1.0% of Cr and 0.1%-0.5% of Mo, with the balance being Fe and other unavoidable impurities. The microstructure of the cold-rolled high-strength steel has 5%-20% of residual austenite and 70%-90% of martensite, and the carbon concentration ratio of the residual austenite to the martensite is greater than 3.5 and less than 15. The cold-rolled high-strength steel sheet has a high strength and an excellent formability through a rational ingredient design and microstructure control.