Patent ID: 10213877

Abstract:
A kind of aluminum alloy and corresponding heat treatment process applied to manufacturing aluminum/steel cladding plates which are resistant to high temperature brazing belong to alloy materials technology field. In the aluminum/steel cladding plates, the aluminum part was alloyed with 0.76%˜0.78% Si and 0.055˜0.10% Er in weight percent and the rest was Al and some unavoidable impurity. The Steel part was 08Al steel. After cladding cold rolling with deformation of 55%±2%, the aluminum/steel cladding plates were annealed at 510˜535° C. for different times. Then simulated brazing process was performed to optimize the range of annealing time and temperature. The so produced Al/St cladding plates could not only effectively solve the low interface strength in Al/St cladding plates, but also meet the mechanical properties which were necessary for further processing of Al/St cladding plates. It was provided a kind of aluminum alloy and corresponding heat treatment process which could effectively solve the low bonding strength under the condition of high temperature brazing because of the existence of brittle Fe—Al phases.