Patent ID: 11629388

Abstract:
A steel sheet for the manufacture of a press hardened part is provided, having a composition of: 0.15%≤C≤0.22%, 3.5%≤Mn<4.2%, 0.001%≤Si≤1.5%, 0.020%≤Al≤0.9%, 0.001%≤Cr≤1%, 0.001%≤Mo≤0.3%, 0.001%≤Ti≤0.040%, 0.0003%≤B≤0.004%, 0.001%≤Nb≤0.060%, 0.001%≤N≤0.009%, 0.0005%≤S≤0.003%, 0.001%≤P≤0.020%. A microstructure has less than 50% ferrite, 1% to 20% retained austenite, cementite, such that the surface density of cementite particles larger than 60 nm is lower than 10{circumflex over ( )}7/mm2, and a complement of bainite and/or martensite, the retained austenite having an average Mn content of at least 1.1*Mn %. Press-hardened steel part obtained by hot forming the steel sheet, and manufacturing methods thereof.