Patent ID: 11833777

Abstract:
Disclosed in the present invention is a high-strength double-sided stainless steel clad sheet, including a substrate layer, and stainless steel clad layers clad-rolled on double sides of the substrate layer. The substrate layer consists, in mass percent, the chemical elements: C: 0.03-0.12%, 0<Si≤0.30%, Mn: 0.2-1.0%, Al: 0.02-0.04%, Ti: 0.01-0.03%, Nb: 0.005-0.020%, and N: 0.003-0.006%, with the balance being iron and other inevitable impurities. Also disclosed in the present invention is a manufacturing method for the high-strength double-sided stainless steel clad sheet, including the steps of: (1) obtaining the substrate layer and the stainless steel clad layer; (2) billet making; (3) clad-rolling; and (4) solution annealing and pickling treatment: controlling the solution temperature to be 950-1020° C., and then cooling down to room temperature at an average cooling rate of 20-50° C./s.