Patent ID: 10378088

Abstract:
[Problem]There is provided an aluminum alloy fin material with high strength, superior brazability and superior corrosion resistance.[Solving means]An aluminum alloy fin material has a composition, in % by mass, of the following: Zr: 0.05 to 0.25%, Mn: 1.3 to 1.8%, Si: 0.7 to 1.3%, Fe: 0.10 to 0.35%, and Zn: 1.2 to 3.0%, the remainder being Al and inevitable impurities. The aluminum alloy fin material has a solidus temperature of 615° C. or higher, a tensile strength after brazing of 135 MPa or higher, a pitting potential after brazing in the range of −900 to −780 mV, and an average crystal grain diameter in a rolled surface after brazing in the range of 200 μm to 1,000 μm.