Patent ID: 11027361

Abstract:
By obtaining a spot-welded joint being a spot-welded joint formed by overlapping a plurality of pieces of steel plates (1A, 1B) and performing spot welding on the steel plates, including a high-strength steel plate whose tensile strength is 750 (MPa) to 2500 (MPa), being at least one piece of steel plate out of the plurality of pieces of steel plates, in which a carbon equivalent Ceq of the high-strength steel plate is 0.20 mass % to 0.55 mass %, and ten or more of iron-based carbides in each of which a length of a longest portion is 0.1 (μm) or more exist in a square region 103 within a heat-affected zone 4 of a cross section that passes through a center of a welding mark, and is cut along a plate thickness direction of the steel plates (1A, 1B), a cross tensile strength of the spot-welded joint to be formed is improved.