A high-strength cold rolled steel sheet having mechanical characteristics having a tensile strength of not less than 780 MPa, a yield ratio of not more than 70%, and a small in-plane anisotropy of a tensile characteristicis obtained by hot rolling a steel slab comprising by mass % C: 0.07 to 0.12%, Si: not more than 0.7%, Mn: 2.2 to 2.8% and Ti and Nb: 0.02 to 0.08% in total, and cold rolling the sheet, followed by continuous annealing to form a steel texture comprised of ferrite having an area ratio of 40 to 80% with respect to the whole texture, and a second phase constituted by tempered martensite, fresh martensite and bainite, wherein the total area ratio of the bainite and the tempered martensite to the second phase is 50 to 80%, and the aspect ratio of the fresh martensite is in the range of 1.0 to 1.5.