Patent ID: 10822678

Abstract:
When a non-oriented electrical steel sheet is produced by hot rolling a slab containing, by mass %, C: not more than 0.0050%, Si: 1.5-5.0%, Mn: 0.20-3.0%, sol. Al: not more than 0.0050%, P: not more than 0.2%, S: not more than 0.0050% and N: not more than 0.0040% to form a hot rolled sheet, cold rolling the hot rolled sheet without conducting a hot band annealing and then subjecting to a finish annealing, a compositional ratio of CaO in oxide-based inclusions existing in the slab defined by CaO/(SiO2+Al2O3+CaO) is set to not less than 0.4 and/or a compositional ratio of Al2O3 defined by Al2O3/(SiO2+Al2O3+CaO) is set to not less than 0.3, and a coiling temperature in the hot rolling is set to not lower than 650° C.