Patent ID: 10612106

Abstract:
The present invention provides a cold-rolled and annealed steel sheet with a strength greater than 1200 MPa, the composition of which includes, the contents being expressed by weight: 0.10%≤C≤0.25%, 1%≤Mn≤3%, A≥0.010%, Si≤2.990%, S≤0.015%, P≤0.1%, N≤0.008%, it being understood that 1%≤Si+Al≤3%, it being understood that Cr+3Mo≥0.3%, Ti in an amount such that Ti/N≥4 and Ti≤0.040%. A balance of the composition includes iron and inevitable impurities resulting from the smelting. The microstructure of the steel includes 15 to 90% bainite, the remainder includes martensite and residual austenite.