Hekzagonal Bor Nitrür (hBN) İlavesinin Geleneksel Cam İyonomer Simanın Florür Salımı Üzerine Etkisi
Effect of Hexagonal Boron Nitride Addition to Conventional Glass Ionomer Cements on Fluoride Release
Yazar: Eser, Rümeysa; Karakaş, Mert; Balaban, Sena; Kalaycı, Şükrü; Deniz Arısu, Hacer
Dergi: Acta Odontologica Turcica, Vol. 42 No. 3, 2024
Anahtar kelimeler: Restorative Dentistry ; Restoratif Diş Tedavisi ; Cam iyonomer siman,Florür salımı,Hekzagonal bor nitrür ; fluoride release,Glass ionomer cement,hexagonal boron nitride

Amaç: Restoratif materyallerin çürük önleyici özellikleri ve remineralizasyon yeteneği materyallerin florür salımı ile ilişkilidir. Bu çalışmanın amacı geleneksel cam iyonomer simana eklenen farklı hekzagonal bor nitrür(hBN) konsantrasyonlarının simanın florür salımı ve yeniden şarj olabilme kapasitesi üzerindeki etkisini değerlendirmektir.Gereç ve Yöntem: Geleneksel cam iyonomer simanın (Fuji IX GP) tozuna ağırlıkça %0.5, %1 ve %1.5 oranında hBN nanopartikülü ilave edildi. Florür salımını değerlendirmek için kontrol grubu olarak geleneksel cam iyonomer siman kullanıldı. Örnekler silindirik teflon kalıplar kullanılarak hazırlandı (n=10). Karıştırma üretici firma talimatlarına uygun toz/likit oranında, oda sıcaklığında (22 °C) spatula ile elle yapıldı. Örnekler 37±1°C etüvde distile su içerisinde 1, 3, 7, 14 ve 30 gün süreyle saklandı. Ölçüm aralıklarında iyon selektif elektrot (Dionex™ IonPac™ AS9-HC) kullanılarak florür salımı ölçümleri yapıldı. Her ölçümden önce elektrot kalibre edildi. Otuz günün sonunda örnekler %1.23 asidüle fosfat florür jel içerisinde bekletildi ve 1., 3. ve 7. günlerde ölçümler tekrarlandı. Bulgular: Tüm gruplarda en yüksek florür salımının 1. günde meydana geldiği ve bu salımın zaman içerisinde önemli ölçüde azaldığı gözlendi (p0.05). Sonuç: hBN ilavesi geleneksel cam iyonomer simanın florür salım değerleri üzerinde olumsuz etki göstermemiştir. İleriki çalışmalarda biyouyumluluğu ve antibakteriyel etkinliği kanıtlanmış hBN nanopartikülü ile modifiye edilmiş bu simanın mekanik ve biyolojik özellikleri değerlendirilmelidir.

Objective: The fluoride releasing ability of a restorative material can reduce cariogenic potential and produce remineralizing effect. The aim of this study is to evaluate the effect of hBN addition to a conventional glass ionomer cement at different weight ratios on its fluoride release and recharge ability.Materials and methods: To modify conventional glass ionomer cement (Fuji IX GP), 0.5%, 1%, and 1.5% wt hBN nanoparticles were added to its powder. Glass ionomer cement without addition of hBN nanoparticles was used as the control group for the fluoride release. Ten specimens were prepared using cylindrical teflon moulds for each experimental group (n=10). Specimens were prepared by hand mixing with a spatula at room temperature (22 °C) at a powder/liquid ratio in accordance with Fuji IX GP's manufacturer's instructions and subsequent aging (1, 7, 14 and 30 days) were simulated by the storage at 37±1°C in deionized water in an incubator. Quantitative fluoride ions release were measured at 1, 7, 14 and 30 days using a standard ion-selective electrode (Dionex™ IonPac™ AS9-HC, Thermo Fisher Scientific Inc, USA). Before measurements, the ion-selective electrode was calibrated using a series of standards of known concentration. After 30 days, the specimens immersed in 1.23% acidulated phosphate fluoride-gel, and fluoride release were measured at 1 and 7 days.Results: All specimens showed a high release of fluoride on day 1. The amount of fluoride released decreased significantly after day 1. After the recharge procedure, specimens didn’t release fluoride as much as at the beginning of the study. Analysis of variance (ANOVA) test showed statistically significant differences between the control and experimental groups on day 1 (p0.05). There was no statistically significant difference between the groups in the amount of cumulative fluoride release (p>0.05).Conclusion: The addition of hBN did not affect the fluoride release capacity of the conventional glass ionomer cement.