Antibakteriyel hibrit kaplamaların hazırlanması ve karakterizasyonu
Preparation and characterization of antibacterial hybrid coats
Yazar: BELKIZ ÇOŞKUN
Danışman: DOÇ. DR. ATİLLA EVCİN
Afyon Kocatepe Üniversitesi / Fen Bilimleri Enstitüsü / Nanobilim ve Nanoteknoloji Ana Bilim Dalı
Derece: Yüksek Lisans, 2021
Konu: Mühendislik Bilimleri = Engineering Sciences
Dizin: Antibakteriyel ajanlar = Anti-bacterial agents ; Plastik kaplama yöntemleri = Plastic coating method ; Polisilanlar = Polysilanes

Özet:
Bu çalışmada, polikarbonat (PC) ve polimetil metakrilat (PMMA) yüzeylere nano gümüş, boroksit ve nano TiO2 katkılı silan bağlayıcı madde bazlı hibrit kaplamalar uygulanmıştır. Silan esaslı hibrit kaplama yüzeyleri termal ve UV ile kürlenmiştir. Kaplanan PC ve PMMA yüzeyler temas açısı analizi, FTIR analizi, dijital mikroskop ve antibakteriyel aktivite ile karakterize edilmiştir. Katkısız GLYMO kaplamalar PMMA için 95.89°, PC için 87.84° temas açısı vermiştir. FTIR analizlerinde GLYMO, Ag, Ti, Si ve B için karakteristik pikler elde edilmiştir. Dijital mikroskop görüntülerinde kaplama kalınlığı 3.275-16.116 μm aralığında çıkmıştır. Antibakteriyel testinde e. coli için bakteri üremesini önlemiştir. Staphylococcus aureus için ise en etkili olanlar Ag, Ti ve B sırasını takip etmiştir.

Abstract:
In this study, nano silver, boroxide and nano TiO2 doped silane binder-based hybrid coatings were applied to polycarbonate (PC) and polymethyl methacrylate (PMMA) surfaces. Silane-based hybrid coating surfaces are thermally and UV cured. Coated PC and PMMA surfaces were characterized by contact angle analysis, FTIR analysis, digital microscope and antibacterial activity. The undoped GLYMO coatings gave a contact angle of 95.89° for PMMA and 87.84° for PC. Characteristic peaks were obtained for GLYMO, Ag, Ti, Si and B in FTIR analyzes. In digital microscope images, the coating thickness was in the range of 3,275-16,116 μm. In its antibacterial test, it prevented bacterial growth for e. coli. For Staphylococcus aureus, Ag, Ti and B were followed by the most effective ones.
İzmir merkez ve ilçelerinde bulunan tarihi camilerin kıble tayini
Determination of qibla direction of historical mosquesin Izmir center and districts
Yazar: ŞÜKRÜ ÇOBANOĞLU
Danışman: DOÇ. DR. MUSTAFA YILMAZ
Afyon Kocatepe Üniversitesi / Fen Bilimleri Enstitüsü / Harita Mühendisliği Ana Bilim Dalı
Derece: Yüksek Lisans, 2021
Konu: Jeodezi ve Fotogrametri = Geodesy and Photogrammetry

Özet:
Bu tez çalışmasında, İzmir ili merkez ve ilçelerinde, içindeki 14-18 yüzyıllar arasında yapılmış olan 21 camiye ait kıble doğrultuları GNSS tekniği kullanılarak ölçülmüştür. Kıble doğrultuları ölçülen camilerin kıble tayini, jeodezik hesaplamalar kullanılarak yapılmıştır. Ölçülen kıble doğrultuları ile hesaplanan (olması gereken) kıble doğrultuları karşılaştırılmıştır. Karşılaştırma sonucu -22 derece ile +39 derece farklar bulunmuştur. Bu farkların Müslümanların kıble yönünü belirleyen Kâbe doğrultusundan 45 derece sağa ve sola olan hata sınırı içinde kaldığı belirlenmiştir.

Abstract:
In this thesis study, the direction of Qibla of 21 mosques built between 14-18 centuries in the center and districts of İzmir province were measured by using the GNSS technique. Qibla determination of mosques whose direction of the Qibla was measured was made using geodetic calculations. Qibla directions measured and calculated (should be) directions are compared. As a result of the comparison, differences were found between -22 and + 39 degrees. It has been determined that these differences remain within the error limit of 45 degree to the right and left from the direction of the Kaaba, which determines the direction of the Qibla of Muslims.
Güneş ışınımı tahmini için görüntü işleme tabanlı yeni bir yaklaşım
A new image-processing based approach for solar radiation forecasting
Yazar: ARDAN HÜSEYİN EŞLİK
Danışman: DR. ÖĞR. ÜYESİ EMRE AKARSLAN ; PROF. DR. FATİH ONUR HOCAOĞLU
Afyon Kocatepe Üniversitesi / Fen Bilimleri Enstitüsü / Yenilenebilir Enerji Sistemleri Ana Bilim Dalı
Derece: Yüksek Lisans, 2021
Konu: Elektrik ve Elektronik Mühendisliği = Electrical and Electronics Engineering ; Enerji = Energy

Özet:
Güneş kaynağının kesikli ve değişken yapısı, enerjinin verimli bir şekilde kullanımını oldukça zorlaştırmaktadır. Bu sıkıntıların üstesinden gelebilmek ve güneş enerjisinden etkin bir şekilde faydalanabilmek amacıyla güneş ışınımı tahmini gibi günümüze kadar farklı birçok yöntem kullanılmıştır. Bu çalışmada, gün içinde oluşan bulut hareketlerini takip ederek gelecekte gerçekleşecek bulut hareketlerini tahmin eden, ardından elde edilen bulut hareketi tahmini ve atmosfer dışı güneş ışınımı verilerin kullanılmasıyla güneş ışınımı tahmini gerçekleştiren derin öğrenme yaklaşımı geliştirilmiştir. Bu kapsamda, Afyon Kocatepe Üniversitesi Güneş ve Rüzgâr Uygulama ve Araştırma Merkezine kurulan deney düzeneği aracılığıyla belirli aralıklarda toplanan gökyüzü görüntüleri ve ışınım verileri kullanılmıştır. Sıralı gökyüzü görüntülerinde bulut hareketleri Shi-Tomasi ve Lucas-Kanade yöntemleri kullanılarak takip edilmiştir. Görüntüler üzerinde bulut, gökyüzü, güneş tespitleri ise kırmızı/mavi oranı ve K-means kümeleme yönteminden oluşan hibrit bir tespit yaklaşımıyla gerçekleştirilmiştir. Son olarak, 5 dakikalık zaman ufku için 10 saniye çözünürlüklü güneş ışınımı tahminleri gerçekleştirilmiş ve yaklaşımın performansı test edilmiştir.

Abstract:
The intermittent and variable nature of the solar source makes it very difficult to use energy efficiently. In order to overcome these problems and benefit from solar energy effectively, many different methods such as solar radiation estimation have been used until today. In this study, a deep learning approach has been developed that predicts future cloud movements by tracking the cloud movements that occur during the day and then performs solar radiation forecasting using the obtained cloud movement forecast and extraterrestrial solar radiation data. In this context, sky images and radiation data collected at specific intervals through the experimental setup established at Afyon Kocatepe University Sun and Wind Application and Research Center are used. Cloud motions in sequential sky images are followed using Shi-Tomasi and Lucas-Kanade methods. Cloud, sky, and sun detections on the images are performed with a hybrid detection approach consisting of red/blue ratio and K-means clustering method. Finally, solar radiation estimates with a resolution of 10 seconds for the time horizon of 5 minutes are performed, and the performance of the approach is tested.
Uzaktan algılama yöntemleriyle yüzeysel sularda kalite tayini
Quality estimation in surface waters by remote sensing methods
Yazar: HALİL İBRAHİM YİLDİZ
Danışman: PROF. DR. YILMAZ İÇAĞA
Afyon Kocatepe Üniversitesi / Fen Bilimleri Enstitüsü / İnşaat Mühendisliği Ana Bilim Dalı
Derece: Yüksek Lisans, 2021
Konu: İnşaat Mühendisliği = Civil Engineering
Dizin: Hidroloji = Hydrology ; Su kalitesi = Water quality ; Uzaktan algılama = Remote sensing

Özet:
Bu araştırmada, insan yaşantısında önemli bir kaynak olan göl suyu kalitesinin ve kirlilik düzeyi tayininde kullanılabilecek parametreler, daha hızlı bir yöntem olan Uzaktan Algılama (UA) verileriyle belirlenmeye çalışılmıştır. İstanbul il sınırları içinde kalan Terkos gölü ve gölü besleyen akarsular da yüzeysel su kirlilik parametresi olan Toplam Askıda Katı Madde (TAKM), pH, Sıcaklık değerleri saptanmaya çalışılmıştır. Bu değerlerin belirlenmesinde, Sentinel-2 ve Landsat-8 uydularına ait görüntü verisi kullanılıp zamansal değişimler göz önüne alınarak yüzeysel sularda kirlilik değişimleri ortaya konulmuştur. Toplam Askıda Katı Madde değeri kirlik değerinin en yükseği Eylül 2019 ve en düşüğü Kasım 2020 olarak saptanmıştır. pH değerlerinin en yükseği Kasım 2020 tarihinde ve en düşüğü Eylül 2019 tarihinde elde edilmiştir. Bu değişimler İstanbul Su ve Kanalizasyon İdaresi (İSKİ) den alınan verilerle karşılaştırılmıştır. Bu sonuçların korelasyon değerleri; TAKM miktarında r=0,85 pH değerinde r=0,88 ve sıcaklık ölçümlerinde r=0,89 olarak belirlenmiştir. Yüzeysel sularında TAKM, pH ve Sıcaklık parametrelerinin uzaktan algılama yöntemleri ile izlenmesi istatistiksel açıdan kabul edilebilir sonuç vermektedir.

Abstract:
In this research, the parameters that can be used in determining the quality of lake water and pollution level, which is an important resource in human life, were tried to be determined with Remote Sensing (UA) data, which is a faster method. It was tried to determine the surface water pollution parameter of Total Suspended Solid Matter (TAKM), pH, and Temperature values on Terkos Lake and the rivers feeding the lake within the provincial borders of Istanbul. In the determination of these values, the image data of Sentinel-2 and Landsat-8 satellites were used and the pollution changes in the surface waters were revealed by taking into account the temporal changes. It plays an important role in the protection of usable water resources. Suspended Solids value was found to be the highest in September 2019 and the lowest in November 2020. The highest pH values were obtained in November 2020 and the lowest values were obtained in September 2019. These changes were compared with the data received from the Istanbul Water and Sewerage Administration (ISKI). Correlation values of these results; r=0,88 at pH value of r=0,85 in TAKM amount and r=0,89 in temperature measurements. Monitoring of TAKM, pH and temperature parameters in surface waters by remote sensing methods gives statistically acceptable results.
Biyokütle atıklardan elde edilen alternatif yakıt kullanımının motor performans ve emisyonlara etkisi
The effect of using alternative fuel derived from biomass wastes on engine performance and emissions
Yazar: ARİF HAKAN YALÇIN
Danışman: PROF. DR. İBRAHİM MUTLU
Afyon Kocatepe Üniversitesi / Fen Bilimleri Enstitüsü / Makine Mühendisliği Ana Bilim Dalı
Derece: Doktora, 2021
Konu: Makine Mühendisliği = Mechanical Engineering

Özet:
Tez çalışmasında biyokütle atık olan vişne çekirdeklerinin piroliz işlemine tabi tutularak elde edilen vişne çekirdeği pirolitik yağının sıkıştırma ile ateşlemeli (CI) bir test motorunda yakıt olarak kullanılabilirliğine yönelik araştırma yapılmıştır. İlk olarak piroliz işlemi için optimizasyon çalışmaları yapılıp 10 °C/dak. ısıtma hızı, 0,5 L/dak. azot gazı akış hızı ve kırılmış (≤5mm) tanecikler olarak parçacık boyutu, 15 dak. piroliz süresi süresi ve 450 °C'lik reaktör sıcaklığında %29,7 maksimum yağ verimi elde edilmiştir. İkinci aşama olarak elde edilen pirolitik yağın içten yanmalı bir dizel motorunda yakıt olarak kullanılabilirliğine yönelik fizikokimyasal yönden en uygun özelliğe sahip olan yakıt karışımları üzerine araştırılmalar yapılıp ağırlıkça %40 dizel içeren karışım yakıtlar optimum karışım bileşimleri olarak belirlenmiştir. Son olarak fizikokimyasal yönden en iyi özelliğe sahip olan pirolitik yağ ile harmanlanarak elde edilen yakıt karışımlarının tek silindirli ve hava soğutmalı bir dizel motorunda test edilerek motor performans ve emisyonları üzerine olan etkileri dizel ile kıyaslandığında NOx, HC ve is emisyonları yönünden dizele göre daha çevreci olan emisyon değerlerine sahip olduğu için dizel motorlarında çevreci alternatif bir yakıt olarak kullanılabileceği sonucuna varılmıştır.

Abstract:
In this thesis study, a research was conducted on the usability of sour cherry kernel pyrolytic oil as a fuel in a compression ignition (CI) test engine, which is obtained by pyrolysis of sour cherry seeds, a biomass waste. First of all, optimization studies were made for the pyrolysis process whereby the maximum oil yield of 29.7% was obtained at 10 °C/min heating rate, 0.5 L/min nitrogen gas flow rate, particle size as broken (≤5mm) particles, 15 min pyrolysis residence time and reactor temperature of 450 °C. As a second step, investigations were made on the fuel mixtures with the most suitable physicochemical properties for the use of the pyrolytic oil obtained as a fuel in an internal combustion diesel engine and the mixed fuels containing 40% diesel by weight were determined as the optimum mixture compositions. Finally, the fuel mixtures obtained by blending the pyrolytic oil, which has the best physicochemical properties, are tested in a single-cylinder and air-cooled diesel engine, and its effects on engine performance and emissions were compared to diesel. Fuel mixtures obtained are more environmentally friendly in terms of NOx, HC and soot emissions compared to diesel which indicates that it can be used as an environmentally friendly alternative fuel in diesel engines.
Avrupa'da düşman algısının antisemitizmden İslamofobiye dönüşümü (Almanya örneği)
The transformation of enemy perception from anti-semitism to Islamophobia in the Europe (The case of Germany)
Yazar: DİLAY SERTEL
Danışman: PROF. DR. MUSTAFA FİŞNE
Afyon Kocatepe Üniversitesi / Sosyal Bilimler Enstitüsü / Siyaset Bilimi ve Kamu Yönetimi Ana Bilim Dalı / Siyaset Bilimi ve Kamu Yönetimi Bilim Dalı
Derece: Yüksek Lisans, 2021
Konu: Siyasal Bilimler = Political Science ; Uluslararası İlişkiler = International Relations
Dizin: Almanya = Germany ; Antisemitizm = Antisemitism ; Avrupa = European ; Düşman = Enemy ; Irkçılık = Racism ; Zenofobi = Xenophobia ; İslamofobi = Islamophobia

Özet:
Bu çalışma son yıllarda Avrupa'da tartışılmaya başlayan ve birçok karşıt görüşü içinde barındıran antisemitizm ve İslamofobi ilişkisine odaklanmıştır. Çalışmada, Avrupa'nın düşman algısındaki değişim göz önüne alınarak, 11 Eylül sonrası artan ve tehlikeli bir boyuta ulaşan İslamofobinin, Holokost gibi bir geçmişi olan antisemitizmden beslendiği, antisemitizmin İslamofobi için bir ön uyarı olduğu düşüncesi detaylı bir incelemeye tabi tutulmuştur. Genelde Avrupa, özelde Almanya üzerine yoğunlaşan çalışma, İslamofobi ve antisemitizmin temelinde yer alan zenofobi ve ırkçılık kavramlarından yola çıkılarak açıklanmaya çalışılmıştır. Literatürde yeni yeni konuşulmaya başlayan bu konu, karşıt görüşleri barındırsa da her iki kavram arasında bağlantı olduğu genel kabul görmektedir. Bu anlamda çalışmada, kavramlar arasındaki benzer noktaların çok fazla olduğu ve İslamofobinin antisemitizmden beslendiği tespit edilmiştir.

Abstract:
This study focuses on the controversial relationship between anti-Semitism and Islamophobia, which has recently been discussed in Europe. In this study, Islamophobia is discussed as the emerging version of anti-Semitism as Islamophobia has been fed by anti-Semitism, which is rooted in Holocaust. By doing so, the transformation of enemy perception in Europe and the increasing Islamophobia after 9/11 has been considered. This study puts Germany at its center while focusing on Europe, and attempts to explain xenophobia and racism concepts, which are roots of Islamophobia and anti-Semitism. Although this topic is newly emerging in the existing literature, the literature provides controversy about the relationship between the two concepts. The dominant view regarding the dispute is that there is a relationship between them. In this respect, this study concluded that there are several similar points between Islamophobia and anti-Semitism and Islamophobia is a fact that has been fed by anti-Semitism.caktır.
Gümüş ve esansiyel yağ içeren antifungal,  antibakteriyel nanolif kaplı cerrahi maskelerin üretimi
Production of antifungal, antibacterial nanofiber coated surgical masks containing silver and essential oil
Yazar: EMİNE YAŞAR
Danışman: PROF. DR. ATİLLA EVCİN
Afyon Kocatepe Üniversitesi / Fen Bilimleri Enstitüsü / Biyomedikal Mühendisliği Ana Bilim Dalı
Derece: Yüksek Lisans, 2021
Konu: Biyomühendislik = Bioengineering ; Biyoteknoloji = Biotechnology
Dizin: Antibakteriyel aktivite = Antibacterial activity ; Elektroeğirme yöntemi = Electrospinning method ; Esansiyel yağlar =   ; Gümüş = Silver ; Nanolif = Nanofiber

Özet:
Bu çalışmada, selüloz asetat (CA) çözeltisi gümüş nitrat, pelargonium yağı, okaliptüs yağı, citronella yağı ve cypress yağı ile katkılandırılarak 6 adet çözelti elde edilmiştir. Elde edilen çözeltilerden elektroeğirme yöntemi kullanılarak nanolifler üretilip cerrahi maskenin ara katmanı olan melt blown tabakası üretilen nanolifler ile kaplanmıştır. Nanoliflerin morfolojik analizi taramalı elektron mikroskobu (SEM) ile çapı, homojenitesi ve dağılımı ise Fibraquant programı ile saptanmıştır. Fibraquant programı analiz sonuçları nanolif çaplarının 100 nm ile 800 nm aralığında olduğunu göstermiştir. Başlangıçta hazırlanan çözeltiler FTIR analizi, antifungal ve antibakteriyel aktivite ile karakterize edilmiştir. FTIR analizlerinde selüloz asetat, gümüş ve esansiyel yağlar için karakteristik pikler elde edilmiştir. Staphylococcus aureus bakterisine uygulanan antibakteriyel analiz sonucuna göre gümüş nitrat ve okaliptüs yağı katkılı selüloz asetat çözeltisinin en yüksek antibakteriyel etkinliğe sahip olduğu saptanmıştır. Aspergillus flavus ve penicillium notatum mantarları üzerinde yapılan antifungal teste göre ise gümüş nitrat ve pelargonium yağı katkılı selüloz asetat çözeltisinin en yüksek antifungal etkinliğe sahip olduğu görülmüştür.

Abstract:
In this research, 6 solutions were obtained by adding silver nitrate, pelargonium oil, eucalyptus oil, citronella oil and cypress oil to cellulose acetate (CA) solution. Nanofibers were produced from these solutions using the electrospinning method. The meltblown layer, which is the middle layer of the surgical mask, is covered with the produced nanofibers. Morphological analysis of nanofibers was determined by scanning electron microscopy (SEM). The diameter, homogeneity and distribution of nanofibers were determined with the Fibraquant program. Fibraquant program analysis results showed that nanofiber diameters were between 100 nm and 800 nm. The initially prepared solutions were characterized by FTIR analysis, antifungal and antibacterial activity. Characteristic peaks were obtained for cellulose acetate, silver and essential oils in FTIR analysis. According to the results of antibacterial analysis against Staphylococcus aureus bacteria, cellulose solution with silver nitrate and eucalyptus oil was found to have the highest antibacterial activity. According to the antifungal test performed on Aspergillus flavus and penicillium notatum mushrooms, cellulose acetate solution with silver nitrate and pelargonium oil was found to have the highest antifungal activity.
Kazak kişi adlarının yapısal analizi
Structural analysis of Kazakh anthroponymes
Yazar: YASİN ESKİ
Danışman: DOÇ. DR. MURAT ÖZŞAHİN
Afyon Kocatepe Üniversitesi / Sosyal Bilimler Enstitüsü / Çağdaş Türk Lehçeleri ve Edebiyatları Ana Bilim Dalı
Derece: Yüksek Lisans, 2021
Konu: Dilbilim = Linguistics ; Türk Dili ve Edebiyatı = Turkish Language and Literature
Dizin: Adlar = Nouns ; Kazaklar = Kazakhs ; Kazakça = Kazakh language ; Kişi adları = Personal names ; Yapısal analiz = Structural analysis ; İsim verme = Name giving

Özet:
Bu çalışmada söz konusu "Kazak Türklerinde Kişi Adları: / (Ḳazaḳ esimderi) / T.J.
Januzaḳov – K. S. Esbayeva; Türkiye Türkçesine aktaran Nurettin Aksu. —
Ankara: Türk Dil Kurumu, 2003." adlı eserden incelediğimiz 3.256 adet erkek adı,
1204 adet de kadın adı olmak üzere toplam 4460 adet kişi adı bulunmaktadır. Eserde
kişi adları, baba adları ve soyadlarının Kazakça doğru yazılışı, imla kuralları temelinde
sunulmaktadır. Bu adların yapısı oldukça çeşitlilik arz etmektedir. Çalışmamızda da
yapısal olarak çeşitlilik arz eden kişi adlarının anlamlarına, kökenlerine ve yapısal
özelliklerine yer verilip bu konular değerlendirilmiştir.
Anahtar Kelimeler: Adbilim, Kişi Adları, Ad verme, Türk, Kazakistan.

Abstract:
In this study, there are a total of 4460 personal names, consisting of 3.256 male names
and 1204 female names, which are examined from the work named "Kazak
Türklerinde kişi adları: / (Ḳazaḳ esimderi) / T. J. Januzaḳov – K. S. Esbayeva;
Türkiye Türkçesine aktaran Nurettin Aksu. — Ankara: Türk Dil Kurumu, 2003
(Personal names of Kazakh Turks: / (Ḳazaḳ esimderi) / T. J. Januzaḳov – K. S.
Esbayeva; Translated to Turkey Turkish by Nurettin Aksu. — Ankara: Turkish
Language Association, 2003)" In this study, the correct spelling of personal names,
father's names and surnames in Kazakh is provided on the grounds of orthographic
rules. There are many variations in the structure of these names. In this study, the
meanings, origins and structural features of people's names, having many structurally
variations, are included and these matters are evaluated.
Keywords: Onomatology, Personal Names, Name-Giving, Turk, Kazakhstan.
Silan ve metal oksitlerle cam yüzeylerin modifiye edilmesi
Modification of glass surfaces with silane and metal oxides
Yazar: AHMET IŞIK
Danışman: DOÇ. DR. ATİLLA EVCİN
Afyon Kocatepe Üniversitesi / Fen Bilimleri Enstitüsü / Nanobilim ve Nanoteknoloji Ana Bilim Dalı
Derece: Yüksek Lisans, 2021
Konu: Bilim ve Teknoloji = Science and Technology ; Metalurji Mühendisliği = Metallurgical Engineering ; Polimer Bilim ve Teknolojisi = Polymer Science and Technology
Dizin: Daldırma kaplama yöntemi = Dipping coating method ; Film kaplama = Film coating ; Polimer kaplama = Polymer coating ; Polisilanlar = Polysilanes ; Yüzey kaplama = Surface coating

Özet:
Bu araştırmada, sol-jel yöntemi kullanılarak mikroskop lam cam malzemelerin yüzeyleri silan ve metal oksit çözeltileri ile kaplanıp yüzey özelliklerinin geliştirilmesi amaçlanmıştır. Yapılan çalışmanın önemi, cam malzemelerin geliştirilen yüzeylerin sertliği ve çizilme direncinin artırılması için uygun içeriğe sahip çözeltilerin belirlenmesi ve cam yüzeylere uygulanmasıdır. Çalışmada sol-jel yöntemi kullanılarak çeşitli silan ve metal oksitlerin farklı miktarda karıştırması ile hazırlanan çözeltiler ıslak film aplikatörü yardımıyla cam malzemelerin yüzeylerine kaplanmıştır. Kaplanan yüzeylerin özelliklerini incelemek için ışık geçirgenlik, bulanıklık, temas açı ve kalem sertlik testleri uygulanmıştır. Bulanıklık %0,39 ile %37,3, ışık geçirgenlik %85 ile %91,7, temas açı 45,16° ile 115,44° ve kurşun kalem sertlik 2H ile 6H değerleri arasında sonuçlar bulunmuştur. Bulunan değer aralıklarına göre 4. Grup çözeltisine sahip SR13 ve SR14 numuneleri 6H, SR11 ve SR12 numuneleri ise 5H değerleri ile en sert numune olarak gözlenmiştir.

Abstract:
In this research, In this study, it is aimed to improve the surface properties of microscope slide glass materials by coating them with silane and metal oxide solutions using the sol-gel method. The importance of the study is to determine suitable contents to increase the hardness and scratch resistance of the developed surfaces of glass materials and apply on them.  In the study, the solutions prepared by mixing different amounts of various silanes and metal oxides using the sol-gel method were coated on the surfaces of glass materials with the help of a wet film applicator. Light transmittance, haze, contact angle and pencil hardness tests were applied to examine the properties of the coated surfaces. Haze %0,39 to %37,3, light transmittance %85 to %91,7, contact angle between 45,16° and 115,44°, and pencil  harndness test values between 2H and 6H were found. According to the value ranges found, the samples with group 4 solutions; SR13 and SR 14 samples with 6H and SR11 and SR12 samples with 5H values were observed as the hardest samples.