AISI 1050, AISI 304 AND AISI 430 tip çeliklerin yakma alın kaynak yöntemiyle kaynatılması ve mekanik özelliklerin incelenmesi
The investigation of mechanical properties and welding with flash butt welding of AISI 1050, AISI 304 AND AISI 430 types steels
Yazar: MUHANMET YAŞAR ÇİMEN
Danışman: YRD. DOÇ. DR. UĞUR ARABACI
Gazi Üniversitesi / Fen Bilimleri Enstitüsü / Metal Eğitimi Ana Bilim Dalı
Derece: Yüksek Lisans, 2015
Konu: Metalurji Mühendisliği = Metallurgical Engineering

Özet:
Bu çalışmada, AISI 304, AISI 430 paslanmaz çelikleri ile AISI 1050 tip çeliğe yakma alın kaynağı uygulanmış ve bu uygulamanın malzemelerin mekanik ve mikroyapı özellikleri üzerine etkileri araştırılmıştır. Birleştirilen numunelerin sertlikleri, çekme mukavemetleri ve mikroyapı özellikleri incelenerek birbirleri ile mukayeseleri yapılmıştır. Deney çalışmaları esnasında yakma alın kaynak parametreleri sabit tutulmuştur. Bu çalışmada elde edilen sonuçların, yakma alın kaynak yöntemini kullanarak AISI 304, AISI 430 paslanmaz çeliklerin ve AISI 1050 çeliğinin kaynağını yapan imalatçıların kullanabileceği verilerin tespitleri amaçlanmıştır. Araştırma sonunda AISI 304 ve AISI 1050 malzemelerinin en yüksek sertlik değerleri kaynak bölgesinde (ITAB) görülürken, AISI 430 paslanmaz çeliğinin sertlik değerlerinin kaynak bölgesinde düşüşler yaşadığı tespit edilmiştir. AISI 1050 malzemesinin kaynak edildiği numune çiftlerinde sertlik değerlerini ve çekme mukavemetini artırdığı görülmüştür.

Abstract:
In this study, AISI 304, AISI 430 stainless steel AISI type 1050 steel butt welding has been applied and its effects on the microstructure and mechanical properties of these materials were investigated application. The combined stiffness of the specimen, tensile strength, and are compared with each other microstructural features have been examined. Flash-butt welding parameters are kept constant during the test run. The results obtained in this study, using the flash-butt welding AISI 304, AISI 430 and AISI stainless steel are intended to identify the source of data for use by manufacturers, who in 1050 steel. Research at the end of AISI 304 and AISI 1050 material resources in the high hardness values (HAZ), while sources in AISI 430 stainless steel hardness have been found to experience a decline. AIA was found that the stiffness values of duplicate samples where the material source 1050, and improve the tensile strength.
Aydın-Karacasu çömlekçiliği ve ustaları üzerine bir araştırma
Aydın Karacasu a study on pottery and craftsmen
Yazar: RAHŞAN KOÇAK
Danışman: PROF. DR. MEDİHA GÜLER
Gazi Üniversitesi / Eğitim Bilimleri Enstitüsü / El Sanatları Ana Bilim Dalı / Geleneksel Türk El Sanatları Bilim Dalı
Derece: Yüksek Lisans, 2015
Konu: El Sanatları = Crafts
Dizin: Aydın = Aydın ; Aydın-Karacasu = Aydın-Karacasu ; El sanatları = Handicrafts ; Sürahiler = Decanters ; Vazo = Vase ; Çömlek = Pot ; Çömlekçilik = Pottery

Özet:
Araştırmada verilerin toplanması amacıyla uzman görüşleri alınarak 23 soruluk bir anket formu düzenlenmiş ve 25 kişiye uygulanmıştır. Anket formu ile çömlekçilik sanatıyla ilgilenen kişilerin; kişisel bilgilerini, mesleki özelliklerini, çömlek yapımında kullanılan araç-gereçleri, çömlek üretiminde kullanılan teknikleri, çömlek yapımında kullanılan desen ve renk özellikleri, çömlek üretimi ve değerlendirilmesi, çömlekçiliğin pazarlama alanı ve çömlekçilik sanatının yöredeki gelişimi ile ilgili sorulara cevap aranmıştır. Anketlerin sonuçları frekans (f) ve yüzde (%) dağılımları ile tablolaştırılmış ve yorumlanmıştır. Çömlek formlarını tanıtacak bilgi formları oluşturulmuş, 30 adet çömlek ürününün boyut, malzeme, teknik, desen kullanım alanı, kullanılan malzemeler, kullanılan teknikler, desen ve ürünün genel özelliklerini tespit edilmiştir. Tespit edilen ürünlerin fotoğrafları çekilip, çizimleri yapılmış ve bilgi formlarına eklenmiştir.

Abstract:
A questionnaire of 23 questions based on expert opinion in order to collect the data, organized and administered to 23 people . Of people interested in the questionnaire, art pottery ; personal information, professional features, used in pottery tools , techniques used in pottery production , patterns and colors used in pottery , pottery production and evaluation, to answer questions related to the development of the pottery 's marketing and pottery art area have been searched. The results of the survey frequency (f) and percentage ( %) of the distributions tabulated and interpreted. Pottery forms of information forms have been created to introduce 30 pieces of pottery product size, material, technique , pattern of use of space , materials , techniques used , it was found the general features and product designs . Photos of detected items withdrawn and drawings were made and added to the information sheet.
Hafif giydirme cepheli yüksek yapıların akustik performanslarının analizi ve bir örneklem
A review for acoustic performance of high-rise building with curtain wall and a case study
Yazar: BURÇİN ECE BIYIKLI
Danışman: PROF. DR. FÜSUN DEMİREL
Gazi Üniversitesi / Fen Bilimleri Enstitüsü / Mimarlık Ana Bilim Dalı
Derece: Yüksek Lisans, 2015
Konu: Mimarlık = Architecture

Özet:
Günümüzde yapımı hızla artan yüksek binalarda, yapım ve kullanım aşamasında kolaylık sağlaması, esnek tasarım imkanı vermesi ve yüksek standartlarda yapı kabuğu beklentisini karşılaması nedeniyle sıklıkla hafif giydirme cepheler tercih edilmektedir. Isı, ışık, ses ve havalandırma gibi faktörlerin iç mekanda istenen düzeyde filtre edilerek geçirimini sağlamak yapı kabuklarının görevidir. Bu bağlamda, tez çalışmasının amacı, yüksek binalarda yoğunlukla tercih edilen hafif giydirme cephelerin, akustik performansının ortaya konması ve çevresel gürültünün bina yüksekliği ile ilişkisinin yapı kabuğuna etkisinin belirlenmesidir. Ayrıca gürültü denetimi kriterleri araştırılarak bu kriterler kapsamında bir örneklem incelemesi yapılmıştır. Bu amaçla tezde, hafif giydirme cephe sistemleri öncelikle farklı özelliklerine göre sınıflandırılmış, çevresel gürültü ve gürültü kontrolüne ilişkin kavramlar tanımlanmış ve ilgili mevzuat araştırmaları yapılarak hafif giydirme cepheler için akustik performans kriterleri oluşturulmuştur. Sözü edilen performans kriterleri ile bir örneklem üzerinden değerlendirme ve iyileştirme önerileri geliştirilmiştir.

Abstract:
Shell structures are extremely important for their role in filtering the exterior conditions such as heat, light, and sound. Curtain wall systems, a popular kind of shell structure, become increasingly preferable for high-rise buildings nowadays due to the fact that these systems facilitate construction and occupation processes, allow flexible design opportunity, and meet the high expectations of shell structures. In this thesis, we aim to evaluate the acoustic performance of curtain walls against ambient noise and to understand the impact of the ambient noise and height of the structure on the curtain walls. To that end, we categorize curtain wall systems by their varied features and form a performance criteria table for curtains walls. Furthermore, we describe the terms for ambient noise, and present the related regulations. Finally, we choose a high-rise building with curtain walls and analyze the acoustic performance of the building based on the performance criteria table.
Bulanık mantık ve graf tabanlı görüntü ayrıştırma
Fuzzy logic and graph based image segmentation
Yazar: BEHZAD MORADI
Danışman: PROF. DR. RECEP DEMİRCİ
Gazi Üniversitesi / Fen Bilimleri Enstitüsü / Bilgisayar Mühendisliği Ana Bilim Dalı
Derece: Yüksek Lisans, 2015
Konu: Bilgisayar Mühendisliği Bilimleri-Bilgisayar ve Kontrol = Computer Engineering and Computer Science and Control

Özet:
Görüntü ayrıştırma veya sınıflandırma bir sayısal görüntüyü kendisini oluşturan piksellere veya nesnelere ayırma işlemi olup, tanıma ve analizin önemli aşamalarındandır. Ancak söz konusu işlem için kullanıcıdan bağımsız ve tam otomatik bir algoritma bulunmamaktadır.  Günümüze kadar önerilen görüntü ayrıştırma yaklaşımlarının birçoğunun hesapsal maliyeti yüksek olduğu gibi aynı zamanda kullanıcı bağımlıdır. Diğer taraftan son yıllarda önerilen renk benzerliği ve maske tabanlı ayrıştırma algoritmasının hesap maliyeti düşük olmasına rağmen, algoritma ayrıştırma işlemi sırasında kullanıcı tarafından tespit edilmesi gereken iki adet parametreye ihtiyaç duyar: normalizasyon katsayısı ve benzerlik eşik değeri. Bu çalışmada piksellerin renk benzerliği kural tabanlı olarak hesaplanmış ve normalizasyon katsayısına olan ihtiyaç ortadan kaldırılmıştır. Ayrıca benzerlik eşik değeri homojenlik haritası histogramının ağırlık merkezi kullanılarak otomatik olarak çözülmüştür. Önerilen ve klasik yöntemlerle alınan sonuçlar karşılaştırılmalı olarak verilmiştir.

Abstract:
Image segmentation or classification which is a process of separating of pixels or objects of a digital image is one of the important stages in recognition and analysis. A variety of image segmentation approaches recommended so far have high computational cost and at the same time they are user dependent. Nevertheless, there has not been any user independent and fully automatic algorithm for the process. On the other hand, although the recently suggested color similarity and mask-based segmentation algorithm has the low computation cost, it requires two parameters (normalization coefficient and similarity threshold value) that must be selected by user during segmentation process. In this study, color similarities of pixels have been estimated by means of fuzzy reasoning rules and subsequently the requirement of normalization coefficient has been removed. Additionally, the similarity threshold value has been obtained by using the center of gravity of image histogram. The results obtained with the proposed and classical methods have been comparatively given.
Silikon nitrat (Si3N4) filmlerin plazma destekli kimyasal 
buhar biriktirme (PECVD) yöntemi ile üretimi 
ve optik karakterizasyonu
Fabrication and characterization of silicon nitride (Si3N4) films 
by plasma enhancement chemical 
vapor deposition (PECVD)
Yazar: EMRAH ODABAŞI
Danışman: PROF. DR. ELİF ORHAN
Gazi Üniversitesi / Fen Bilimleri Enstitüsü / İleri Teknolojiler Ana Bilim Dalı
Derece: Yüksek Lisans, 2015
Konu: Fizik ve Fizik Mühendisliği = Physics and Physics Engineering

Özet:
Bu tez çalışmasında, silikon nitrat (Si3N4) ince filmler, NH3/SiH4 akış oranı değiştirilerek silikon alttaş üzerine Plazma Destekli Buhar Depolama  (PECVD) yöntemi ile üretildi ve optik karakterizasyonu yapıldı. Si3N4 ince filmlerin üretimi için ana gazlar, silan (SiH4) ve amonyaktır. RF ise paralel plakalar arasında plazma ortamı oluşturmak için kullanılmaktadır. Bu çalışmada, sıcaklık (300°C), RF gücü (15W) ve basınç (1Torr) parametreleri sabit değerlerde tutularak NH3/SiH4 akış oranı değiştirildi. PECVD de büyütülmüş filmlerin kırılma indisleri, soğurma pikleri ve bant tipleri gibi optik özellikleri elipsometre ve Fourier Dönüşümlü Kızılötesi (FT-IR) spektrometre kullanılarak karakterize edildi. Farklı NH3/SiH4 akış oranına göre Si3N4 ince filmlerin kırılma indisleri tayin edildi. Silikon nitrat ince filmlerin kırılma indislerinin 1,813-1,850 aralığında değiştiği, NH3/SiH4 akış oranı azaldıkça filmlerin kırılma indislerinin arttığı gözlemlendi. NH3/SiH4 akış oranı azaldıkça silikon nitrat filmlere ait Si-N soğurma piklerinde de artış gözlemlendi. Bu sonuçlar, üretilen Si3N4 filmlerin optik dalgakılavuzu olarak optoelektronik uygulamalarda kullanılabileceğini göstermektedir.

Abstract:
Silicon nitride (Si3N4) thin films were deposited on silicon substrate by plasma enhanced chemical vapor deposition (PECVD) by changing NH3/SiH4 flow ratio in this thesis.  Silane (SiH4) and ammonia (NH3) were used as precursors for silicon and nitrogen. RF was used to create plasma in parallel-plate configuration. In the present study, NH3/SiH4 flow ratio were varied during deposition while other parameters were maintained at constant value, temperature 300°C, RF power 15W, and chamber pressure 1Torr. For the optical features such as refractive index, absorption pikes, bond types in the Si3N4 thin films were characterized by using elipsometry and Fourier Transform Infrared (FT-IR) spectrometer. The refractive indices for Si3N4 thin films with different ammonia to silane flow rate ratio were measured by elipsometry. The refractive indices of Si3N4 thin films lie within the range of 1.81 to 1.85. It was observed that refractive index increases as NH3/SiH4 flow ratio decreases. The FT-IR spectra exhibit typical peaks corresponding to silicon nitride thin films. It can also be observed that the Si-N peaks increase as the NH3/SiH4 flow ratio decrease by FT-IR spectra.  This indicates that the Si3N4 thin films will be utilized as an optical waveguides for optoelectronics applications.
Gelişimsel kalça displazisi tanısında ultrasonografi ve direkt röntgenogram tetkiklerinin gözlemciler arasındaki değerlendirme farklılıkları /
Yazar: FATİH İLKER CAN
Danışman: PROF. DR. SACİT TURANLI
Gazi Üniversitesi / Tıp Fakültesi / Ortopedi ve Travmatoloji Ana Bilim Dalı
Derece: Tıpta Uzmanlık, 2015
Konu: Ortopedi ve Travmatoloji = Orthopedics and Traumatology
Dizin: Femur = Femur ; Kalça = Hip ; Kalça çıkıkları = Hip dislocation ; Kalça çıkıkları-konjenital = Hip dislocation-congenital ; Radyografi = Radiography ; Teşhis = Diagnosis ; Teşhis-ayırıcı = Diagnosis-differential ; Ultrasonografi = Ultrasonography ; X ışını = X ray

Özet:
Gelişimsel kalça displazisi çocuklarda femoroasetabuler eklemin gelişimi sırasında tanı konulması gereken dinamik bir hastalıktır. Mevcut fizik muayene yöntemlerinin hastalar arasında farklı dönemlerde farklı bulgular vermesi nedeniyle tanının doğru konulması için güvenilir radyolojik yöntemlere ihtiyaç duyulmaktadır.
Kalça ekleminin ağırlıklı olarak kıkırdak yapıda olduğu yaşamın ilk aylarında ultrasonografi, tanıda direkt grafiye göre daha doğru sonuç veren, invazif olmayan bir yöntemdir. Tutarlılık oranlarının muayene eden ve değerlendiren gözlemciler arasında direkt grafiyle benzer olması, ilk aylarda direkt grafiye üstünlüğü nedeniyle tercih edilmesi gereken yöntem olduğu, 6 aydan sonra da yüksek tutarlılık oranları ile kullanılabilecek bir yöntem olduğu kanaatindeyiz.
Anahtar kelimeler: gelişimsel kalça displazisi, ultrasonografi, direkt grafi, gözlemciler arası tutarlılık, gelişimsel kalça displazisi tanısı

Abstract:
Developmental dysplasia of the hip (DDH) is a dynamic disorder which should be diagnosed during the femoroacetabular joint development in children. In consequence of the different physical examination findings, reliable radiological assessments are needed in order to diagnose aproppriately.
In the very first months of the life, ultrasonography is more reliable non-invazive diagnostic method because of the cartilage structure of the hip joint. Owing to the similar consistency ratios by the observers, we believe that it is suitable to use ultrasonography in the diagnosis of DDH in the first months of the life, and it can also be used after six months because of the high consistency ratios.
Diferansiyel puls polarografisi ile eser miktarda vanadyum tayini için yöntem geliştirme
Method development for the determination of trace amounts of vanadium by differential pulse polarography
Yazar: ESEN GÜL ATEŞ
Danışman: PROF. DR. OLCAY ŞENDİL
Gazi Üniversitesi / Fen Bilimleri Enstitüsü / Kimya Ana Bilim Dalı
Derece: Yüksek Lisans, 2015
Konu: Kimya = Chemistry

Özet:
V5+ ve V4+ iyonlarının Diferansiyel Puls Polarografisi (DPP) ile tayini pH=4 HCI/ KCI (0,1M), pH=4 H₃PO₄/ KCI (0,1M) ve pH=6 KCI (0,1M) elektrolit ortamlarında çalışıldı. Her iki vanadyum iyonu üç ortamda da -1,0 V civarında küçük bir indirgenme pikine, -1,65 V civarında katalitik bir pike sahip olduğu gözlendi. -1,0 V'daki indirgenme pikinin iki iyon için her ortamda aynı duyarlılığa sahip olduğu ve bu pikle 10-5 M civarında V4+ ve V5+ derişimlerinin tayin edilebileceği, daha düşük vanadyum derişimlerin tayin edilemeyeceği tespit edildi. -1,65 V'da ortaya çıkan katalitik pikin ise vanadyumun yüküne ve ortama göre büyüklüğünün değiştiği gözlendi. Her üç ortamda da akım aralıkları ayarlanarak V5+ iyonları 10-5 M civarında tayin edilebilirken V4+ iyonları daha düşük derişimlerde, 10-6 M, tayin edildi. Elektroaktif olan bazı katyonlardan Cu2+, Zn2+, Pb2+, Fe3+, Se4+, Cd2+ ve Ni2+'nin girişim etkileri -1,65 V'da çalışıldı. Bu iyonlar 1×10-5 M ve daha düşük derişimlerde ortamda bulunduklarında katalitik pik yüksekliğinin birkaç milimetre düşmesine neden oldular. Fakat pik yüksekliğindeki bu azalmanın vanadyum tayinine önemli bir etkisinin olmadığı tespit edildi. Standart çözeltilerden hazırlanan sentetik bir numuneye geliştirilen metot uygulandı ve pH 6'da KCl elektrolit ortamında 1×10-5 M V5+ % 15, 1×10-6 M V4+  % 5 bağıl hatayla tayin edildi.

Abstract:
Determination of V5+ and V4+ ions with Differential Pulse Polarography (DPP) was studied in the three different electrolyte mediums with pH=4 in HCI/ KCI (0,1M), pH=4 in H₃PO₄/ KCI (0,1M) and pH=6 in KCI (0,1M). It was observed that both vanadium ions had a small reduction peak around -1.0 Volt and a catalytic peak around -1.65 V in the three electrolyte mediums.It was detected that the reduction peaks of two vanadium ions around -1.0 Volt had the same sensitivity. With this reduction peak, V4+ and V5+ concentrations of 10-5 M were determined but concentrations less than 10-5 M vanadium could not be determined. Moreover, the catalytic peak around -1.65 V was observed to vary according to the oxidation number of vanadium and the medium. In each medium by setting current range V5+ ions were determined around 10-5 M and V4+ ions were determined at lower concentrations such as 1×10-6 M. Interference effects of cations Cu2+, Zn2+, Pb2+, Fe3+, Se4+, Cd2+ and Ni2+ were investigated at -1.65 V. In the presence of these cations at 1×10-5 M and lower concentrations the height of catalytic peak was decreased a few millimeters. However this decrease was found not to have a significant impact on the determination of vanadium. The developed method was applied to synthetic sample prepared with standard solutions. 1×10-5 M V5+ and 1×10-6 M V4+ were detected with relative errors 15% and 5% respectively, at pH=6 in KCI (0,1M) electrolyte.
İnşaat şirketlerinde maliyet hesaplarının analizi ve vergi uygulamaları açısından TMS 11'in değerlendirilmesi ve bir uygulama
In cost analysis of construction company accounts and evaluation of taxation and an application in terms of TAS 11
Yazar: HASAN ALTIN
Danışman: PROF. DR. H. KÂMİL BÜYÜKMİRZA
Gazi Üniversitesi / Sosyal Bilimler Enstitüsü / İşletme Ana Bilim Dalı / Muhasebe Bilim Dalı
Derece: Yüksek Lisans, 2015
Konu: İşletme = Business Administration
Dizin: Maliyet = Cost ; Maliyet hesabı = Cost account ; Standartlar = Standards ; Türkiye Muhasebe Standartı 11 = Turkish Accounting Standarts 11 ; Vergilendirme = Taxation ; İnşaat = Construction ; İnşaat işletmeleri = Construction enterprises ; İnşaat sektörü = Construction sector

Özet:
İnşaat şirketlerinde maliyet hesaplarının analizi ve vergi uygulamaları açısından TMS 11'in değerlendirilmesi ve bir uygulama" adlı tez çalışma konumuzu oluşturmaktadır. Amacımız, yıllara yaygın inşaat işi yapan bir işletmenin vergi yasaları ve TMS 11 açısından vergi yükünün hesaplanması ve birbiriyle karşılaştırılmasıdır. Çalışmamızda seçilen işletmenin iki hesap dönemine (2012-2013) ait proje kapsamındaki gelir giderleri ve vergi sorumluluğu incelenmiştir. İşletmeden elde edilen sayısal verilerin vergi yükleri hesaplanarak hem yıllar hem de yöntemler itibariyle karşılaştırılmıştır. Elde edilen sonuçlar; yöntemler arasında yıllık bazda büyük farkların ortaya çıktığını fakat iki yıllık dönem sonunda toplam vergi yükünde her hangi bir değişiklik olmadığını göstermiştir.

Abstract:
Naming, "Cost -benefit analysis of construction companies and assessment of IAS 11 in terms of tax treatment and a case study" constitutes the subject of this thesis. Our aim is the calculation of tax burden of a construction company in terms of both tax regulations and IAS 11, and comparing the results there of.. In this study, duringtwo accounting periods (2012-2013) the selected company's revenues and expenses in the context of the project and tax liability are examined. From the quantitative data obtained, the tax burden of the company in each year by different approaches (IAS vs tax regulations) are calculated and compared. The results obtained show that considerable annual differences are observed between the two approaches but there is no difference at the end of the two-year period.
Yeni bakır (II) komplekslerinin sentezi ve bitki glutatyon redüktaz enzim aktivitesinin incelenmesi
Synthesis of new copper (II) complexes andinvestigation of theirplant glutathione reductase enzyme activities
Yazar: KÜBRA BEGÜM VENEDİK
Danışman: PROF. DR. NURCAN KARACAN
Gazi Üniversitesi / Fen Bilimleri Enstitüsü / Kimya Ana Bilim Dalı
Derece: Yüksek Lisans, 2015
Konu: Kimya = Chemistry

Özet:
Bu çalışmada 9 tane yeni kapalı formülü CuLnX2 olan ( n: 2 veya 4, X: Br, L: 2-aminopiridin (1), 2-aminopirimidin (2), 2-amino-1,3,5- triazin (3), 2-guanidobenzimidazol (4), 1,3,5-triazino(1,2-a)benzimidazol-2-amin,3,4-dihidro-4-(2-tiyofen) (5),  1,3,5-triazino(1,2-a)benzimidazol-2-amin,3,4-dihidro-4-(4-imidazol)  (6), 2-guanidinobenzotiyazol (7), 4H-1,3,5-triazino(2,1-b)benzotiyazol-2-amin, 4-(2-tiyofen) (8), 4H-1,3,5-triazino(2,1-b)benzotiyazol-2-amin, 4-(4-imidazol) (9) ) bakır (II) kompleksleri sentezlenmiş ve yapıları spektrofotometrik  (LC-MS, FTIR) ve iletkenlik yöntemi ile aydınlatılmıştır. Bunlarınkloroplastan izole edilen bitki glutatyon redüktaz enzimi üzerindeki etkileri (IC50) florometrik yöntem ile belirlenmiştir. En yüksek glutatyon redüktaz inhibitör aktivitesini bis{1,3,5-triazino(1,2-a)benzimidazol-2-amin,3,4-dihidro-4-(4-imidazol)}bakır(II) bromür kompleksi göstermiştir. Ayrıca, komplekslerin karbonik anhidraz (CA) ve fotosistem (II) (PS II) inhibitör aktiviteleri Rus ortaklar tarafından (TÜBİTAK Projesi  No: 212T089) çalışılmıştır.

Abstract:
In this study, nine new Cu(II) complexes with molecular formula CuLnX2 (( n: 2 or 4, X: Br, L: 2-aminopyridine (1), 2-aminopyrimidine (2), 2-amino-1,3,5-triazine (3),2-guanidobenzimidazole (4), 1,3,5-triazinone(1,2-a)benzimidazole-2-amine, 3,4-dihydro-4-(2-thiophene) (5), 1,3,5-triazinone(1,2-a)benzimidazole-2-amine,3,4-dihydro-4-(4-imidazole)  (6), 2-guanidinobenzotiyazole(7), 4H-1,3,5-triazinone(2,1-b)benzothiazole-2-amine,4-(2-thiophene) (8), 4H-1,3,5-triazinone(2,1-b) benzothiazol-2-amine,4-(4-imidazole) (9)) were synthesized and their structure were identified with spectrophotometric methods (LC-MS, FTIR) elemental analysis and conductivity measurements. Their effect (IC50) on plant glutathione reductase enzyme isolated from chloroplast weredeterminedby fluorometric method. 1,3,5-triazinone(1,2-a)benzimidazole-2-amine,3,4-dihydro-4-(4-imidazole) copper (II) bromide showed the highest glutathione reductase inhibitory activity. In addition, photosystem (II) andcarbonic anhydrase (CA) inhibitory activities of the complexes was studied by Russian partners (TÜBİTAK Project No: 212T089).