Cetrimide, cetylpyridinium chloride, benzalkonium chloride ve chlorhexidine ile kombine kullanılan Fuji IX'un fiziksel özelliklerinin değerlendirilmesi
The evaluation of the physical properties of Fuji IX combined with cetrimide, cetylpyridinium chloride, benzalkonium chloride and chlorhexidine
Yazar: TAMER TÜZÜNER
Danışman: PROF. DR. TEZER ULUSU
Gazi Üniversitesi / Sağlık Bilimleri Enstitüsü / Pedodonti Ana Bilim Dalı
Derece: Doktora, 2008
Konu: Diş Hekimliği = Dentistry
Dizin: Cam iyonomer çimentoları = Glass ionomer cements

Özet:
Bu çalışmada kuaterner amonum bileşiklerinden olan Cetrimide (CT), Cetylpyridinium Chloride (CPC), Benzalkonium Chloride (BC) ve Chlorhexidine (CHX) %1 ve %2 oranlarında Fuji IX ile kombine kullanılarak fiziksel özelliklerinde meydana gelen değişiklikler Fourier Transform Infrared Spectroscopy (FTIR) analizi, mikro-gerilme test tekniği ve mikro-sertlik analizi ile değerlendirildi. Kuaterner amonyum bileşiği içermeyen Fuji IX kontrol, diğer gruplar deney grupları olarak belirlendiFTIR analizi sonucunda kontrol grubu ile deney grupları arasında 24 saatlik sürenin sonunda C=O ve C=C kimyasal bağları açısından çok büyük farklılıklar oluşmadığı, mikro-gerilme test tekniği sonrası kontrol ve deney grupları arasında istatistiksel olarak anlamlı farklılık meydana geldiği (p<0,05) ve en yüksek değeri kontrol grubu alacak şekilde büyükten küçüğe doğru sırası ile, %1 BC içeren Fuji IX, %1 CHX içeren Fuji IX, % 2 CHX içeren Fuji IX, %1 CPC içeren Fuji IX, %2 BC içeren Fuji IX, %1 CT içeren Fuji IX, %2 CT içeren Fuji IX, %2 CPC içeren Fuji IX şeklinde olduğu, Mikro-sertlik analizi sonucunda tüm zaman dönemlerinde kontrol ve deney grupları arasında istatistiksel olarak anlamlı farklılık meydana geldiği (p<0,05) ve en yüksek değeri kontrol grubu alacak şekilde büyükten küçüğe doğru sırası ile, %1 CHX içeren Fuji IX , %1 BC içeren Fuji IX , % 2 CHX içeren Fuji IX , %2 BC içeren Fuji IX , %1 CPC içeren Fuji IX , %1 CT içeren Fuji IX , %2 CT içeren Fuji IX, %2 CPC içeren Fuji IX şeklinde olduğu bulgulandıSonuç olarak FTIR, mikro-gerilme test tekniği, mikro-sertlik gerçekleştirilen değerlendirmeler sonucunda çalışmada kullanılan kuaterner amonyum yapılı bileşiklerin değişen oranlarda Fuji IX ile birlikte kullanılabileceği in-vitro koşullarda belirlendiAnahtar sözcükler: fiziksel özellikler, cam iyonomer siman, fuji IX, kuaterner amonyum bileşikleri, FTIR, mikro-gerilme, mikro-sertlik

Abstract:
In this study, the changes in the physical properties of quaternary ammonium compounds such as Cetrimide (CT), Cetylpyridinium Chloride (CPC), Benzalkonium Chloride (BC) and Chlorhexidine (CHX) combined with 1% and 2% Fuji IX was evaluated with Fourier Transform Infrared Spectroscopy (FTIR), micro-tensile testing method and micro-hardness analysis. Fuji IX free of quaternary ammonium compounds was set as control group, while the other groups were determined as study groups.During FTIR analysis of samples, wavenumbers ranging between 400 cm -1 ? 4000 cm -1 were recorded to computer by taking C = O, C=C, C-O chemical bounds into account. The mean bond strength values of primary teeth were calculated with micro-tensile testing technique. The surface hardness properties of samples stored in distilled water for 1,7,15,30,60 and 90 days were assessed by micro-hardness analysisIn FTIR analysis, substantial differences were not observed in terms of C=O and C=C chemical bounds between the control and the study groups at the end of 24 hours, where as a statistically significant difference was found between the control and the study groups with micro-tensile testing (p<0.05). The ranking of mean micro-tensile values were as follows: control group, %1 BC incorporated Fuji IX , %1 CHX incorporated Fuji IX , % 2 CHX incorporated Fuji IX , %1 CPC incorporated Fuji IX , %2 BC incorporated Fuji IX , %1 CT incorporated Fuji IX , %2 CT incorporated Fuji IX , %2 CPC incorporated Fuji IX. In addition, statistically significant differences were observed between the control and the study groups at all time periods as a result of micro-hardness analysis (p<0.05) and the ranking according to micro-hardness values were as follows: control group, %1 CHX incorporated Fuji IX , %1 BC incorporated Fuji IX , % 2 CHX incorporated Fuji IX , %2 BC incorporated Fuji IX , %1 CPC incorporated Fuji IX, %1 CT incorporated Fuji IX, %2 CT incorporated Fuji IX , %2 CPC incorporated Fuji IX.In conclusion, the combination of quaternary ammonium compounds in various concentrations with Fuji IX is determined to be acceptable under in vitro conditions according to the results of FTIR, micro-tensile testing, micro-hardness analysis.Key Words: physical properties, glass ionomer cement, Fuji IX, quaternary ammonium compounds, FTIR, micro-tensile, micro-hardness