DOI: 10.20350/digitalcsic/16132
title: Dataset for the paper "Barrier Graphene Oxide on a CoCr Alloy via Silane/GO Covalent Bonding and Its Electrochemical Behavior in a Simulated Synovial Fluid Electrolyte"

description: [EN] The electrochemical behaviour of each layer deposited on CoCr surfaces was examined by electrochemical impedance spectroscopy (EIS) for 7 days in 3 g/L hyaluronic acid (HA) aqueous solution. Impedance tests were performed in a three-electrode electrochemical cell with the modified CoCr surfaces acting as the working electrode, a Pt wire acting as counter electrode, and Ag/AgCl (3 M KCl) as a reference electrode. The testing area of the working electrode for all electrochemical tests was 0.39 cm2. An Autolab32 potentiostat/galvanostat was used to generate a sinusoidal wave of 10 mV amplitude in the frequency range 100 kHz to 1 mHz, logarithmically spaced by 5 points/decade, which was applied at the corrosion potential Ecorr. Nova software was used for the data acquisition. All the tests were performed in duplicate. The dataset includes only the experimental data used in the paper. The following files for each surface modification and each immersion time are included: CoCr, CoCr-OH, CoCr-OH-Si45, CoCr-OH-Si45-GO12h, CoCr-OH-Si45-GO24h, CoCr-OH-Si75, CoCr-OH-Si75-GO12h, CoCr-OH-Si75-GO24h. Each file is composed of 5 columns: frequency, real impedance (Z'), imaginary impedance (Z''), Impedance modulus (Z) and phase angle (Phase). All files are in open extension such as .txt and are protected by a Creative Commons Attribution 4.0 International (CC BY 4.0) licence. [ES] El comportamiento electroquímico de cada capa depositada en superficies de CoCr fue examinado mediante espectroscopía de impedancia electroquímica (EIS) durante 7 días sumergidas en una solución acuosa de ácido hialurónico (HA) al 3 g/L. Las pruebas de impedancia se realizaron en una celda electroquímica de tres electrodos con las superficies modificadas de CoCr actuando como electrodo de trabajo, un alambre de Pt actuando como electrodo auxiliar y Ag/AgCl (3 M KCl) como electrodo de referencia. El área de ensayo del electrodo de trabajo para todas las pruebas electroquímicas fue de 0.39 cm2. Se utilizó un potenciostato/galvanostato Autolab32 para generar una onda sinusoidal de amplitud de 10 mV en el rango de frecuencia de 100 kHz a 1 mHz, espaciada logarítmicamente por 5 puntos/década, que se aplicó en el potencial de corrosión Ecorr. Se utilizó el software Nova para la adquisición de datos. Todas las pruebas se realizaron por duplicado. El conjunto de datos incluye solo los datos experimentales utilizados en el artículo. Los siguientes archivos para cada modificación de superficie y cada tiempo de inmersión están incluidos: CoCr, CoCr-OH, CoCr-OH-Si45, CoCr-OH-Si45-GO12h, CoCr-OH-Si45-GO24h, CoCr-OH-Si75, CoCr-OH-Si75-GO12h, CoCr-OH-Si75-GO24h. Cada archivo está compuesto por 5 columnas: frecuencia, impedancia real (Z'), impedancia imaginaria (Z''), módulo de impedancia (Z) y ángulo de fase (Fase). Todos los archivos están en extensión abierta como .txt y están protegidos por una licencia Creative Commons Attribution 4.0 International (CC BY 4.0).
description: [EN] This is the experimental dataset used in the paper “Barrier Graphene Oxide on a CoCr Alloy via Silane/GO Covalent Bonding and Its Electrochemical Behavior in a Simulated Synovial Fluid Electrolyte". The article includes the experimental procedure carried out for the deposition of graphene oxide on CoCr surfaces: CoCr was hydroxylated through alkalization in NaOH 5 M for 2 h, (sample named CoCr-OH). Subsequently, silanization was carried out using APTES. APTES was pre-mixed at 2% vol in isopropanol-water (200:1 v/v) and stirred for 1 h. After this, CoCr-OH samples were immersed in the APTES solution at room temperature for 1 min. The silane-coated samples were kept under curing conditions at 45 °C (CoCr-OH-Si45 sample) and 75 °C (CoCr-OH-Si75 sample) for 24 h and 30 min, respectively. Finally, CoCr-OH-Si45 and CoCr-OH-Si75 surfaces were immersed in 4 g/L GO aqueous suspension at 60 °C for 12 h and 24 h to obtain CoCr-OH-Si45-GO12h, CoCr-OH-Si75-GO12h and CoCr-OH-Si45-GO24h, and CoCr-OH-Si75-GO24h. This data set includes the results of the electrochemical impedance data obtained for each CoCr surface: CoCr (CoCr, CoCr-OH, CoCr-OHSi45, CoCr-OH-Si75 CoCr-OH-Si45-GO12h, CoCr-OH-Si75-GO12h y CoCr-OH-Si45-GO24h, y CoCr-OH-Si75-GO24h, immersed in 3 g/L Hyaluronic acid solution for 7 days.
description: [ES] Este es el conjunto de datos experimentales utilizado en el artículo "Barrera de Óxido de Grafeno en una Aleación CoCr mediante enlace covalente de Silano/GO y su comportamiento electroquímico en un electrolito de fluido sinovial simulado". El artículo incluye el procedimiento experimental llevado a cabo para la deposición de óxido de grafeno sobre superficies de CoCr: CoCr fue hidroxilado mediante alcalinización en NaOH 5 M durante 2 horas (muestra denominada CoCr-OH). Posteriormente, se llevó a cabo la silanización utilizando APTES. APTES fue premezclado al 2% en volumen en isopropanol-agua (200:1 v/v) y agitado durante 1 hora. Después, las muestras de CoCr-OH fueron sumergidas en la solución de APTES a temperatura ambiente durante 1 minuto. Las muestras recubiertas con silano se mantuvieron bajo condiciones de curado a 45 °C (muestra CoCr-OH-Si45) y 75 °C (muestra CoCr-OH-Si75) durante 24 horas y 30 minutos, respectivamente. Finalmente, las superficies CoCr-OH-Si45 y CoCr-OH-Si75 fueron sumergidas en suspensión acuosa de 4 g/L GO a 60 °C durante 12 y 24 horas obteniendo las superficies CoCr-OH-Si45-GO12h, CoCr-OH-Si75-GO12h y CoCr-OH-Si45-GO24h, y CoCr-OH-Si75-GO24h. Este conjunto de datos incluye los resultados de los datos de impedancia electroquímica obtenidos para cada superficie de CoCr (CoCr, CoCr-OH, CoCr-OHSi45, CoCr-OH-Si75 CoCr-OH-Si45-GO12h, CoCr-OH-Si75-GO12h y CoCr-OH-Si45-GO24h, y CoCr-OH-Si75-GO24h sumergidas en una solución de 3 g/L ácido hialurónico durante 7 días.