cometadata/datacite-titles-descriptions-related-identifiers huggingface dataset:
DOI: 10.5290/400037
title: Small punch tensile/fracture test data for P91 material at -158 °C and a displacement rate of .003 mm/s

description: The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation of the data with that obtained from conventional creep tests, supports the need to exploit the recently launched Code of Practice for Small Punch Testing (CEN/WS 21). The present work is specifically concerned with investigating the creep behaviour of P91 steel weldments at 600 Celsius along with low-temperature fracture behaviour. Thin discs, 8 mm in diameter and 0.5 mm thick, were manufactured from different zones of a component containing a P91 welded joint: base metal (BM), service- exposed material (SE), weld metal (WM), fine-grain and coarse-grain heat affected zones (FG-HAZ & CG-HAZ). The results of SP creep tests on these disks, performed at 600 Celsius under different loads carefully following the Code of Practice, could be correlated with uniaxial creep data. The SP test is shown to be a reliable method to depict creep behaviour of this alloy and its weldments and a creep model derived, useful for life time prediction, could also be demonstrated through FEA to predict the creep deformation of the SP discs. Additionally, the SP testing method shows potential to evaluate the fracture properties of P91 weldments, in particular the ductile-to-brittle transition temperature and fracture toughness estimations.
DOI: 10.5290/400057
title: Small punch tensile/fracture test data for P91 wm material at -192 °C and a displacement rate of .003 mm/s (second repeat test)

description: The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation of the data with that obtained from conventional creep tests, supports the need to exploit the recently launched Code of Practice for Small Punch Testing (CEN/WS 21). The present work is specifically concerned with investigating the creep behaviour of P91 steel weldments at 600 Celsius along with low-temperature fracture behaviour. Thin discs, 8 mm in diameter and 0.5 mm thick, were manufactured from different zones of a component containing a P91 welded joint: base metal (BM), service- exposed material (SE), weld metal (WM), fine-grain and coarse-grain heat affected zones (FG-HAZ & CG-HAZ). The results of SP creep tests on these disks, performed at 600 Celsius under different loads carefully following the Code of Practice, could be correlated with uniaxial creep data. The SP test is shown to be a reliable method to depict creep behaviour of this alloy and its weldments and a creep model derived, useful for life time prediction, could also be demonstrated through FEA to predict the creep deformation of the SP discs. Additionally, the SP testing method shows potential to evaluate the fracture properties of P91 weldments, in particular the ductile-to-brittle transition temperature and fracture toughness estimations.
DOI: 10.5290/6010901
title: Low cycle fatigue - strain control test data for NIMONIC 101 material at 850 °C (eighth repeat test)

description: In May 1985 a European programme on intercomparison of low cycle fatigue (LCF) testing was started under the auspices of the EEC Community Bureau of Reference (BCR). Subsequently, as a result of the Versailles Project on Advanced Materials and Standards (VAMAS), a wider international participation was sought. The objective of the programme was to establish a set of high temperature LCF data representative of accepted testing practice and, subsequently, to identify the significant aspects of testing procedure affecting the repeatability and reproducibility as a basis for defining a standard test procedure. In view of the potential influence of material characteristics on LCF life, three classes of alloy were selected for testing according to their cyclic strain behaviour, namely strain-hardening, strain-softening, and stable. This data collection consists of test results on Nimonic 101 alloy at 850°C, which is representative of the cyclically stable case.
DOI: 10.5290/6020501
title: Low cycle fatigue - strain control test data for IN 718 material at 550 °C (fourth repeat test)

description: In May 1985 a European programme on intercomparison of low cycle fatigue (LCF) testing was started under the auspices of the EEC Community Bureau of Reference (BCR). Subsequently, as a result of the Versailles Project on Advanced Materials and Standards (VAMAS), a wider international participation was sought. The objective of the programme was to establish a set of high temperature LCF data representative of accepted testing practice and, subsequently, to identify the significant aspects of testing procedure affecting the repeatability and reproducibility as a basis for defining a standard test procedure. In view of the potential influence of material characteristics on LCF life, three classes of alloy were selected for testing according to their cyclic strain behaviour, namely strain-hardening, strain-softening, and stable. This data collection consists of test results on IN 718 alloy at 550°C, which is representative of the cyclic strain-softening case.
DOI: 10.5290/1900101
title: Small punch tensile/fracture test data for Gr. 91 material at -150 °C and a displacement rate of .05 mm/s

description: In the framework of its institutional project on Gen IV nuclear reactors, the JRC-IET performs pre-normative materials qualification research within the work package PreMaQ. The activities focus on evaluation methods like ultrasonic fatigue, neutron diffraction, thermoelectric power measurements, x-ray tomography, small punch creep and fracture tests, and nano-indentation with the aim to establish or prepare international standards. The current data set belongs to a small punch tensile/fracture mechanics test on the ferritic/martensitic steel Grade 91.
DOI: 10.5290/1900106
title: Small punch tensile/fracture test data for Gr. 91 material at -60 °C and a displacement rate of .5 mm/s

description: In the framework of its institutional project on Gen IV nuclear reactors, the JRC-IET performs pre-normative materials qualification research within the work package PreMaQ. The activities focus on evaluation methods like ultrasonic fatigue, neutron diffraction, thermoelectric power measurements, x-ray tomography, small punch creep and fracture tests, and nano-indentation with the aim to establish or prepare international standards. The current data set belongs to a small punch tensile/fracture mechanics test on the ferritic/martensitic steel Grade 91.
DOI: 10.5290/400014
title: Small punch creep test data for P91 material at 600 °C and a load of 280 N (third repeat test)

description: The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation of the data with that obtained from conventional creep tests, supports the need to exploit the recently launched Code of Practice for Small Punch Testing (CEN/WS 21). The present work is specifically concerned with investigating the creep behaviour of P91 steel weldments at 600 Celsius along with low-temperature fracture behaviour. Thin discs, 8 mm in diameter and 0.5 mm thick, were manufactured from different zones of a component containing a P91 welded joint: base metal (BM), service- exposed material (SE), weld metal (WM), fine-grain and coarse-grain heat affected zones (FG-HAZ & CG-HAZ). The results of SP creep tests on these disks, performed at 600 Celsius under different loads carefully following the Code of Practice, could be correlated with uniaxial creep data. The SP test is shown to be a reliable method to depict creep behaviour of this alloy and its weldments and a creep model derived, useful for life time prediction, could also be demonstrated through FEA to predict the creep deformation of the SP discs. Additionally, the SP testing method shows potential to evaluate the fracture properties of P91 weldments, in particular the ductile-to-brittle transition temperature and fracture toughness estimations.
DOI: 10.5290/400017
title: Small punch creep test data for P91 haz_cg material at 600 °C and a load of 250 N

description: The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation of the data with that obtained from conventional creep tests, supports the need to exploit the recently launched Code of Practice for Small Punch Testing (CEN/WS 21). The present work is specifically concerned with investigating the creep behaviour of P91 steel weldments at 600 Celsius along with low-temperature fracture behaviour. Thin discs, 8 mm in diameter and 0.5 mm thick, were manufactured from different zones of a component containing a P91 welded joint: base metal (BM), service- exposed material (SE), weld metal (WM), fine-grain and coarse-grain heat affected zones (FG-HAZ & CG-HAZ). The results of SP creep tests on these disks, performed at 600 Celsius under different loads carefully following the Code of Practice, could be correlated with uniaxial creep data. The SP test is shown to be a reliable method to depict creep behaviour of this alloy and its weldments and a creep model derived, useful for life time prediction, could also be demonstrated through FEA to predict the creep deformation of the SP discs. Additionally, the SP testing method shows potential to evaluate the fracture properties of P91 weldments, in particular the ductile-to-brittle transition temperature and fracture toughness estimations.
DOI: 10.5290/400043
title: Small punch tensile/fracture test data for P91 material at -30 °C and a displacement rate of .003 mm/s (repeat test)

description: The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation of the data with that obtained from conventional creep tests, supports the need to exploit the recently launched Code of Practice for Small Punch Testing (CEN/WS 21). The present work is specifically concerned with investigating the creep behaviour of P91 steel weldments at 600 Celsius along with low-temperature fracture behaviour. Thin discs, 8 mm in diameter and 0.5 mm thick, were manufactured from different zones of a component containing a P91 welded joint: base metal (BM), service- exposed material (SE), weld metal (WM), fine-grain and coarse-grain heat affected zones (FG-HAZ & CG-HAZ). The results of SP creep tests on these disks, performed at 600 Celsius under different loads carefully following the Code of Practice, could be correlated with uniaxial creep data. The SP test is shown to be a reliable method to depict creep behaviour of this alloy and its weldments and a creep model derived, useful for life time prediction, could also be demonstrated through FEA to predict the creep deformation of the SP discs. Additionally, the SP testing method shows potential to evaluate the fracture properties of P91 weldments, in particular the ductile-to-brittle transition temperature and fracture toughness estimations.
DOI: 10.5290/400055
title: Small punch tensile/fracture test data for P91 wm material at -192 °C and a displacement rate of .003 mm/s

description: The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation of the data with that obtained from conventional creep tests, supports the need to exploit the recently launched Code of Practice for Small Punch Testing (CEN/WS 21). The present work is specifically concerned with investigating the creep behaviour of P91 steel weldments at 600 Celsius along with low-temperature fracture behaviour. Thin discs, 8 mm in diameter and 0.5 mm thick, were manufactured from different zones of a component containing a P91 welded joint: base metal (BM), service- exposed material (SE), weld metal (WM), fine-grain and coarse-grain heat affected zones (FG-HAZ & CG-HAZ). The results of SP creep tests on these disks, performed at 600 Celsius under different loads carefully following the Code of Practice, could be correlated with uniaxial creep data. The SP test is shown to be a reliable method to depict creep behaviour of this alloy and its weldments and a creep model derived, useful for life time prediction, could also be demonstrated through FEA to predict the creep deformation of the SP discs. Additionally, the SP testing method shows potential to evaluate the fracture properties of P91 weldments, in particular the ductile-to-brittle transition temperature and fracture toughness estimations.
DOI: 10.5290/6000501
title: Low cycle fatigue - strain control test data for AISI 316 L material at 550 °C (fourth repeat test)

description: In May 1985 a European programme on intercomparison of low cycle fatigue (LCF) testing was started under the auspices of the EEC Community Bureau of Reference (BCR). Subsequently, as a result of the Versailles Project on Advanced Materials and Standards (VAMAS), a wider international participation was sought. The objective of the programme was to establish a set of high temperature LCF data representative of accepted testing practice and, subsequently, to identify the significant aspects of testing procedure affecting the repeatability and reproducibility as a basis for defining a standard test procedure. In view of the potential influence of material characteristics on LCF life, three classes of alloy were selected for testing according to their cyclic strain behaviour, namely strain-hardening, strain-softening, and stable. This data collection consists of test results on AISI 316L stainless steel at 550°C, which is representative of the cyclic strain-hardening case.
DOI: 10.5290/6010501
title: Low cycle fatigue - strain control test data for NIMONIC 101 material at 850 °C (fourth repeat test)

description: In May 1985 a European programme on intercomparison of low cycle fatigue (LCF) testing was started under the auspices of the EEC Community Bureau of Reference (BCR). Subsequently, as a result of the Versailles Project on Advanced Materials and Standards (VAMAS), a wider international participation was sought. The objective of the programme was to establish a set of high temperature LCF data representative of accepted testing practice and, subsequently, to identify the significant aspects of testing procedure affecting the repeatability and reproducibility as a basis for defining a standard test procedure. In view of the potential influence of material characteristics on LCF life, three classes of alloy were selected for testing according to their cyclic strain behaviour, namely strain-hardening, strain-softening, and stable. This data collection consists of test results on Nimonic 101 alloy at 850°C, which is representative of the cyclically stable case.
DOI: 10.5290/6010701
title: Low cycle fatigue - strain control test data for NIMONIC 101 material at 850 °C (sixth repeat test)

description: In May 1985 a European programme on intercomparison of low cycle fatigue (LCF) testing was started under the auspices of the EEC Community Bureau of Reference (BCR). Subsequently, as a result of the Versailles Project on Advanced Materials and Standards (VAMAS), a wider international participation was sought. The objective of the programme was to establish a set of high temperature LCF data representative of accepted testing practice and, subsequently, to identify the significant aspects of testing procedure affecting the repeatability and reproducibility as a basis for defining a standard test procedure. In view of the potential influence of material characteristics on LCF life, three classes of alloy were selected for testing according to their cyclic strain behaviour, namely strain-hardening, strain-softening, and stable. This data collection consists of test results on Nimonic 101 alloy at 850°C, which is representative of the cyclically stable case.
DOI: 10.5290/1900100
title: Small punch tensile/fracture test data for Gr. 91 material at -150 °C and a displacement rate of .005 mm/s

description: In the framework of its institutional project on Gen IV nuclear reactors, the JRC-IET performs pre-normative materials qualification research within the work package PreMaQ. The activities focus on evaluation methods like ultrasonic fatigue, neutron diffraction, thermoelectric power measurements, x-ray tomography, small punch creep and fracture tests, and nano-indentation with the aim to establish or prepare international standards. The current data set belongs to a small punch tensile/fracture mechanics test on the ferritic/martensitic steel Grade 91.
DOI: 10.5290/1900105
title: Small punch tensile/fracture test data for Gr. 91 material at -100 °C and a displacement rate of .005 mm/s

description: In the framework of its institutional project on Gen IV nuclear reactors, the JRC-IET performs pre-normative materials qualification research within the work package PreMaQ. The activities focus on evaluation methods like ultrasonic fatigue, neutron diffraction, thermoelectric power measurements, x-ray tomography, small punch creep and fracture tests, and nano-indentation with the aim to establish or prepare international standards. The current data set belongs to a small punch tensile/fracture mechanics test on the ferritic/martensitic steel Grade 91.
DOI: 10.5290/1900117
title: Small punch tensile/fracture test data for Gr. 91 material at -20 °C and a displacement rate of .5 mm/s

description: In the framework of its institutional project on Gen IV nuclear reactors, the JRC-IET performs pre-normative materials qualification research within the work package PreMaQ. The activities focus on evaluation methods like ultrasonic fatigue, neutron diffraction, thermoelectric power measurements, x-ray tomography, small punch creep and fracture tests, and nano-indentation with the aim to establish or prepare international standards. The current data set belongs to a small punch tensile/fracture mechanics test on the ferritic/martensitic steel Grade 91.
DOI: 10.5290/400005
title: Small punch creep test data for P91 wm material at 600 °C and a load of 217 N

description: The main aim of the thesis is to demonstrate the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation of the data with that obtained from conventional creep tests, supports the need to exploit the recently launched Code of Practice for Small Punch Testing (CEN/WS 21). The present work is specifically concerned with investigating the creep behaviour of P91 steel weldments at 600 deg.C along with low-temperature fracture behaviour. Thin discs, 8 mm in diameter and 0.5 mm thick, were manufactured from different zones of a component containing a P91 welded joint: base metal (BM), service- exposed material (SE), weld metal (WM), fine-grain and coarse-grain heat affected zones (FG-HAZ & CG-HAZ). The results of SP creep tests on these disks, performed at 600 deg.C under different loads carefully following the Code of Practice, could be correlated with standard creep data. The SP test is shown to be a reliable method to depict creep behaviour of this alloy and its weldments and a creep model derived, useful for life time prediction, could also be demonstrated through FEA to predict the creep deformation of the SP discs. Additionally, the SP testing method shows potential to evaluate the fracture properties of P91 weldments, in particular the ductile-to-brittle transition temperature and fracture toughness estimations.
DOI: 10.5290/400006
title: Small punch creep test data for P91 wm material at 600 °C and a load of 240 N

description: The main aim of the thesis is to demonstrate the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation of the data with that obtained from conventional creep tests, supports the need to exploit the recently launched Code of Practice for Small Punch Testing (CEN/WS 21). The present work is specifically concerned with investigating the creep behaviour of P91 steel weldments at 600 deg.C along with low-temperature fracture behaviour. Thin discs, 8 mm in diameter and 0.5 mm thick, were manufactured from different zones of a component containing a P91 welded joint: base metal (BM), service- exposed material (SE), weld metal (WM), fine-grain and coarse-grain heat affected zones (FG-HAZ & CG-HAZ). The results of SP creep tests on these disks, performed at 600 deg.C under different loads carefully following the Code of Practice, could be correlated with standard creep data. The SP test is shown to be a reliable method to depict creep behaviour of this alloy and its weldments and a creep model derived, useful for life time prediction, could also be demonstrated through FEA to predict the creep deformation of the SP discs. Additionally, the SP testing method shows potential to evaluate the fracture properties of P91 weldments, in particular the ductile-to-brittle transition temperature and fracture toughness estimations.
DOI: 10.5290/400020
title: Small punch creep test data for P91 haz_fg material at 600 °C and a load of 240 N

description: The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation of the data with that obtained from conventional creep tests, supports the need to exploit the recently launched Code of Practice for Small Punch Testing (CEN/WS 21). The present work is specifically concerned with investigating the creep behaviour of P91 steel weldments at 600 Celsius along with low-temperature fracture behaviour. Thin discs, 8 mm in diameter and 0.5 mm thick, were manufactured from different zones of a component containing a P91 welded joint: base metal (BM), service- exposed material (SE), weld metal (WM), fine-grain and coarse-grain heat affected zones (FG-HAZ & CG-HAZ). The results of SP creep tests on these disks, performed at 600 Celsius under different loads carefully following the Code of Practice, could be correlated with uniaxial creep data. The SP test is shown to be a reliable method to depict creep behaviour of this alloy and its weldments and a creep model derived, useful for life time prediction, could also be demonstrated through FEA to predict the creep deformation of the SP discs. Additionally, the SP testing method shows potential to evaluate the fracture properties of P91 weldments, in particular the ductile-to-brittle transition temperature and fracture toughness estimations.