DOI: 10.20350/digitalcsic/17686
title: Anodic polarization dataset of the paper: Biotribocorrosion of CoCr Surfaces Using Hyaluronic Acid functionalized with Graphene Oxide nanoadditive as hybrid lubricants

description: [EN] This is the experimental anodic polarization dataset used in the paper “Biotribocorrosion of CoCr Surfaces Using Hyaluronic Acid functionalized with Graphene Oxide nanoadditive as hybrid lubricants", that include anodic polarization curve data in duplicate. Anodic polarization curves were carried out on CoCr surfaces after 7 days of immersion in 3 g/L HA, 4 g/L GO and 3 g/L HA + 0.012 wt.% GO. Anodic polarization tests were performed in a three-electrode electrochemical cell with the CoCr surfaces acting as the working electrode, a Pt wire acting as counter electrode, and Ag/AgCl (3 M KCl) as a reference electrode. A Gamry potentiostat/galvanostat was used to apply potentials from the corrosion potential Ecorr to achieve 1 mA in current at a scanning rate of 0.6 V/h. The back curve was also drawn from the potential at which 1 mA was reached until the initial corrosion potential. This data set includes the results of the potential (E, V) and current (I, A) data. Anodic polarization files files are composed of 2 columns: E (V) and I (A). All files are in open extension such as .csv and are protected by a Creative Commons Attribution 4.0 International (CC BY 4.0) licence.
description: [ES] Este es el conjunto de datos experimentales de polarización anódica utilizado en el artículo “Biotribocorrosión de superficies de CoCr utilizando ácido hialurónico funcionalizado con nano-aditivo de óxido de grafeno como lubricantes híbridos”, que incluye los datos de las curvas de polarización anódica por duplicado. Las curvas de polarización anódica de las superficies de CoCr se realizaron después de 7 días de inmersión en 3 g/L de AH (ácido hialurónico), 4 g/L de OG (óxido de grafeno) y 3 g/L de AH + 0.012 % en peso de OG. Los ensayos de polarización anódica se llevaron a cabo en una celda electroquímica de tres electrodos, donde las superficies de CoCr actuaron como electrodo de trabajo, un hilo de platino (Pt) como electrodo auxiliar o contraelectrodo, y un electrodo de referencia Ag/AgCl (3 M KCl). Se utilizó un potenciostato/galvanostato Gamry para aplicar potenciales desde el potencial de corrosión (Ecorr) hasta alcanzar una corriente de 1 mA, con una velocidad de barrido de 0.6 V/h. La curva de rertorno también se trazó desde el potencial alcanzado a 1 mA hasta el potencial de corrosión inicial. Este conjunto de datos incluye los resultados de potencial (E, V) y corriente (I, A). Los archivos de polarización anódica están compuestos por 2 columnas: E (V) e I (A). Todos los archivos se presentan en formato abierto, como .csv, y están protegidos bajo la licencia Creative Commons Attribution 4.0 International (CC BY 4.0).
description: [EN] This is the experimental dataset of the anodic polarization curves used in the paper “Biotribocorrosion of CoCr Surfaces Using Hyaluronic Acid functionalized with Graphene Oxide nanoadditive as hybrid lubricants". The article includes the experimental results of the tribocorrosion behaviour of CoCr surfaces immersed in the next lubricant media: 3 g/L hyaluronic acid, 4 g/L graphene oxide, 3 g/L HA + 0.006 wt.% GO, 3g/L HA + 0.012 wt.% GO and 3 g/L HA + 0.024 wt.% GO. Subsequently, electrochemical impedance spectroscopy for several days and anodic polarization curve measurements of CoCr surfaces in 3 g/L HA, 4 g/L GO and 3 g/L HA + 0.012 wt.% GO were carried out. COF and EIS data are included in the dataset entitled: “Dataset for the paper: Biotribocorrosion of CoCr Surfaces Using Hyaluronic Acid functionalized with Graphene Oxide nanoadditive as hybrid lubricants”. This dataset includes the results of the anodic polarization curves obtained in duplicate for CoCr surfaces immersed in 3 g/L HA, 4 g/L GO and 3 g/L HA + 0.012 wt.% GO lubricants.
description: [ES] Este es el conjunto de datos experimentales de las curvas de polarización anódica utilizadas en el artículo “Biotribocorrosion of CoCr Surfaces Using Hyaluronic Acid functionalized with Graphene Oxide nanoadditive as hybrid lubricants”. El artículo incluye los resultados experimentales del comportamiento a tribocorrosión de superficies de CoCr sumergidas en los siguientes medios lubricantes: 3 g/L de ácido hialurónico, 4 g/L de óxido de grafeno, 3 g/L de AH + 0.006 % en peso de OG, 3 g/L de AH + 0.012 % en peso de OG y 3 g/L de AH + 0.024 % en peso de OG. Posteriormente, se realizaron ensayos de espectroscopía de impedancia electroquímica (EIS) durante varios días y curvas de polarización anódica de las superficies de CoCr en 3 g/L de ácido hialurónico, 4 g/L de óxido de grafeno y 3 g/L de AH + 0.012 % en peso de OG. Los datos de COF y EIS están incluidos en el conjunto de datos titulado: “Dataset for the paper: Biotribocorrosion of CoCr Surfaces Using Hyaluronic Acid functionalized with Graphene Oxide nanoadditive as hybrid lubricants”. Este conjunto de datos incluye los resultados de las curvas de polarización anódica obtenidas por duplicado para superficies de CoCr inmersas en 3 g/L de AH, 4 g/L OG y 3 g/L de AH + 0.012 % en peso de OG.