DOI: 10.57760/sciencedb.08751
title: Comparative Study of Plasma-Enhanced-Atomic-Layer-Deposited Al2O3/HfO2/SiO2 and HfO2/Al2O3/SiO2 Tri-Layers for Ultraviolet Laser Applications
title: 等离子体增强原子层沉积Al2O3/HfO2/SiO2与HfO2/Al2O3/SiO2三层薄膜在紫外激光应用中的比较研究

description: High-performance thin films combining large optical bandgap Al2O3 and high refractive index HfO2 are excellent components for constructing the next generation of laser systems with enhanced output power. However, the growth of low-defect plasma-enhanced-atomic-layer-deposited (PEALD) Al2O3 for high-power laser applications, and its combination with HfO2 and SiO2 materials commonly used in high-power laser thin films still face challenges, such as how to minimize defects, especially interface defects. In this work, substrate-layer interface defects in Al2O3 single-layer thin films, layer-layer interface defects in Al2O3-based bilayer and tri-layer thin films, and their effects on the laser-induced damage threshold (LIDT) were investigated via capacitance-voltage (C-V) measurements. The experimental results show that by optimizing the deposition parameters, specifically the deposition temperature, precursor exposure time, and plasma oxygen exposure time, Al2O3 thin films with low defect density and high LIDT can be obtained. Two tri-layer anti-reflection (AR) thin film structures, Al2O3/HfO2/SiO2 and HfO2/Al2O3/SiO2, were then prepared and compared. The tri-layer AR thin film with Al2O3/HfO2/SiO2 structure exhibits a lower interface defect density, better interface bonding performance, and an increase in LIDT by approximately 2.8 times. We believe these results provide guidance for the control of interface defects and the design of thin film structures and will benefit many thin film optics for laser applications.
description: High-performance thin films combining large optical bandgap Al2O3 and high refractive index HfO2 are excellent components for constructing the next generation of laser systems with enhanced output power. However, the growth of low-defect plasma-enhanced-atomic-layer-deposited (PEALD) Al2O3 for high-power laser applications, and its combination with HfO2 and SiO2 materials commonly used in high-power laser thin films still face challenges, such as how to minimize defects, especially interface defects. In this work, substrate-layer interface defects in Al2O3 single-layer thin films, layer-layer interface defects in Al2O3-based bilayer and tri-layer thin films, and their effects on the laser-induced damage threshold (LIDT) were investigated via capacitance-voltage (C-V) measurements. The experimental results show that by optimizing the deposition parameters, specifically the deposition temperature, precursor exposure time, and plasma oxygen exposure time, Al2O3 thin films with low defect density and high LIDT can be obtained. Two tri-layer anti-reflection (AR) thin film structures, Al2O3/HfO2/SiO2 and HfO2/Al2O3/SiO2, were then prepared and compared. The tri-layer AR thin film with Al2O3/HfO2/SiO2 structure exhibits a lower interface defect density, better interface bonding performance, and an increase in LIDT by approximately 2.8 times. We believe these results provide guidance for the control of interface defects and the design of thin film structures and will benefit many thin film optics for laser applications.