cometadata/datacite-titles-descriptions-related-identifiers huggingface dataset:
DOI: 10.5290/1900110
title: Small punch tensile/fracture test data for Gr. 91 material at 23 °C and a displacement rate of .005 mm/s

description: In the framework of its institutional project on Gen IV nuclear reactors, the JRC-IET performs pre-normative materials qualification research within the work package PreMaQ. The activities focus on evaluation methods like ultrasonic fatigue, neutron diffraction, thermoelectric power measurements, x-ray tomography, small punch creep and fracture tests, and nano-indentation with the aim to establish or prepare international standards. The current data set belongs to a small punch tensile/fracture mechanics test on the ferritic/martensitic steel Grade 91.
DOI: 10.5290/400029
title: Small punch tensile/fracture test data for P91 material at -30 °C and a displacement rate of .003 mm/s

description: The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation of the data with that obtained from conventional creep tests, supports the need to exploit the recently launched Code of Practice for Small Punch Testing (CEN/WS 21). The present work is specifically concerned with investigating the creep behaviour of P91 steel weldments at 600 Celsius along with low-temperature fracture behaviour. Thin discs, 8 mm in diameter and 0.5 mm thick, were manufactured from different zones of a component containing a P91 welded joint: base metal (BM), service- exposed material (SE), weld metal (WM), fine-grain and coarse-grain heat affected zones (FG-HAZ & CG-HAZ). The results of SP creep tests on these disks, performed at 600 Celsius under different loads carefully following the Code of Practice, could be correlated with uniaxial creep data. The SP test is shown to be a reliable method to depict creep behaviour of this alloy and its weldments and a creep model derived, useful for life time prediction, could also be demonstrated through FEA to predict the creep deformation of the SP discs. Additionally, the SP testing method shows potential to evaluate the fracture properties of P91 weldments, in particular the ductile-to-brittle transition temperature and fracture toughness estimations.
DOI: 10.5290/400047
title: Small punch tensile/fracture test data for P91 material at -135 °C and a displacement rate of .003 mm/s

description: The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation of the data with that obtained from conventional creep tests, supports the need to exploit the recently launched Code of Practice for Small Punch Testing (CEN/WS 21). The present work is specifically concerned with investigating the creep behaviour of P91 steel weldments at 600 Celsius along with low-temperature fracture behaviour. Thin discs, 8 mm in diameter and 0.5 mm thick, were manufactured from different zones of a component containing a P91 welded joint: base metal (BM), service- exposed material (SE), weld metal (WM), fine-grain and coarse-grain heat affected zones (FG-HAZ & CG-HAZ). The results of SP creep tests on these disks, performed at 600 Celsius under different loads carefully following the Code of Practice, could be correlated with uniaxial creep data. The SP test is shown to be a reliable method to depict creep behaviour of this alloy and its weldments and a creep model derived, useful for life time prediction, could also be demonstrated through FEA to predict the creep deformation of the SP discs. Additionally, the SP testing method shows potential to evaluate the fracture properties of P91 weldments, in particular the ductile-to-brittle transition temperature and fracture toughness estimations.
DOI: 10.5290/400061
title: Uniaxial creep test data for P91 material at 600 °C and a stress of 145 MPa

description: The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation of the data with that obtained from conventional creep tests, supports the need to exploit the recently launched Code of Practice for Small Punch Testing (CEN/WS 21). The present work is specifically concerned with investigating the creep behaviour of P91 steel weldments at 600 Celsius along with low-temperature fracture behaviour. Thin discs, 8 mm in diameter and 0.5 mm thick, were manufactured from different zones of a component containing a P91 welded joint: base metal (BM), service- exposed material (SE), weld metal (WM), fine-grain and coarse-grain heat affected zones (FG-HAZ & CG-HAZ). The results of SP creep tests on these disks, performed at 600 Celsius under different loads carefully following the Code of Practice, could be correlated with uniaxial creep data. The SP test is shown to be a reliable method to depict creep behaviour of this alloy and its weldments and a creep model derived, useful for life time prediction, could also be demonstrated through FEA to predict the creep deformation of the SP discs. Additionally, the SP testing method shows potential to evaluate the fracture properties of P91 weldments, in particular the ductile-to-brittle transition temperature and fracture toughness estimations.
DOI: 10.5290/400071
title: Small punch creep test data for P91 material at 600 °C and a load of 217 N

description: The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation of the data with that obtained from conventional creep tests, supports the need to exploit the recently launched Code of Practice for Small Punch Testing (CEN/WS 21). The present work is specifically concerned with investigating the creep behaviour of P91 steel weldments at 600 Celsius along with low-temperature fracture behaviour. Thin discs, 8 mm in diameter and 0.5 mm thick, were manufactured from different zones of a component containing a P91 welded joint: base metal (BM), service- exposed material (SE), weld metal (WM), fine-grain and coarse-grain heat affected zones (FG-HAZ & CG-HAZ). The results of SP creep tests on these disks, performed at 600 Celsius under different loads carefully following the Code of Practice, could be correlated with uniaxial creep data. The SP test is shown to be a reliable method to depict creep behaviour of this alloy and its weldments and a creep model derived, useful for life time prediction, could also be demonstrated through FEA to predict the creep deformation of the SP discs. Additionally, the SP testing method shows potential to evaluate the fracture properties of P91 weldments, in particular the ductile-to-brittle transition temperature and fracture toughness estimations.
DOI: 10.5290/6000301
title: Low cycle fatigue - strain control test data for AISI 316 L material at 550 °C (second repeat test)

description: In May 1985 a European programme on intercomparison of low cycle fatigue (LCF) testing was started under the auspices of the EEC Community Bureau of Reference (BCR). Subsequently, as a result of the Versailles Project on Advanced Materials and Standards (VAMAS), a wider international participation was sought. The objective of the programme was to establish a set of high temperature LCF data representative of accepted testing practice and, subsequently, to identify the significant aspects of testing procedure affecting the repeatability and reproducibility as a basis for defining a standard test procedure. In view of the potential influence of material characteristics on LCF life, three classes of alloy were selected for testing according to their cyclic strain behaviour, namely strain-hardening, strain-softening, and stable. This data collection consists of test results on AISI 316L stainless steel at 550°C, which is representative of the cyclic strain-hardening case.
DOI: 10.6084/m9.figshare.13242485
title: Map and Ped files

description: Map and Ped files for SEC24A SNP genptyping
DOI: 10.5290/400050
title: Small punch tensile/fracture test data for P91 material at -192 °C and a displacement rate of .003 mm/s (third repeat test)

description: The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation of the data with that obtained from conventional creep tests, supports the need to exploit the recently launched Code of Practice for Small Punch Testing (CEN/WS 21). The present work is specifically concerned with investigating the creep behaviour of P91 steel weldments at 600 Celsius along with low-temperature fracture behaviour. Thin discs, 8 mm in diameter and 0.5 mm thick, were manufactured from different zones of a component containing a P91 welded joint: base metal (BM), service- exposed material (SE), weld metal (WM), fine-grain and coarse-grain heat affected zones (FG-HAZ & CG-HAZ). The results of SP creep tests on these disks, performed at 600 Celsius under different loads carefully following the Code of Practice, could be correlated with uniaxial creep data. The SP test is shown to be a reliable method to depict creep behaviour of this alloy and its weldments and a creep model derived, useful for life time prediction, could also be demonstrated through FEA to predict the creep deformation of the SP discs. Additionally, the SP testing method shows potential to evaluate the fracture properties of P91 weldments, in particular the ductile-to-brittle transition temperature and fracture toughness estimations.
DOI: 10.5290/1900113
title: Small punch tensile/fracture test data for Gr. 91 material at -20 °C and a displacement rate of .005 mm/s

description: In the framework of its institutional project on Gen IV nuclear reactors, the JRC-IET performs pre-normative materials qualification research within the work package PreMaQ. The activities focus on evaluation methods like ultrasonic fatigue, neutron diffraction, thermoelectric power measurements, x-ray tomography, small punch creep and fracture tests, and nano-indentation with the aim to establish or prepare international standards. The current data set belongs to a small punch tensile/fracture mechanics test on the ferritic/martensitic steel Grade 91.
DOI: 10.5290/1900114
title: Small punch tensile/fracture test data for Gr. 91 material at -120 °C and a displacement rate of .5 mm/s

description: In the framework of its institutional project on Gen IV nuclear reactors, the JRC-IET performs pre-normative materials qualification research within the work package PreMaQ. The activities focus on evaluation methods like ultrasonic fatigue, neutron diffraction, thermoelectric power measurements, x-ray tomography, small punch creep and fracture tests, and nano-indentation with the aim to establish or prepare international standards. The current data set belongs to a small punch tensile/fracture mechanics test on the ferritic/martensitic steel Grade 91.
DOI: 10.5290/400013
title: Small punch creep test data for P91 material at 600 °C and a load of 280 N (second repeat test)

description: The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation of the data with that obtained from conventional creep tests, supports the need to exploit the recently launched Code of Practice for Small Punch Testing (CEN/WS 21). The present work is specifically concerned with investigating the creep behaviour of P91 steel weldments at 600 Celsius along with low-temperature fracture behaviour. Thin discs, 8 mm in diameter and 0.5 mm thick, were manufactured from different zones of a component containing a P91 welded joint: base metal (BM), service- exposed material (SE), weld metal (WM), fine-grain and coarse-grain heat affected zones (FG-HAZ & CG-HAZ). The results of SP creep tests on these disks, performed at 600 Celsius under different loads carefully following the Code of Practice, could be correlated with uniaxial creep data. The SP test is shown to be a reliable method to depict creep behaviour of this alloy and its weldments and a creep model derived, useful for life time prediction, could also be demonstrated through FEA to predict the creep deformation of the SP discs. Additionally, the SP testing method shows potential to evaluate the fracture properties of P91 weldments, in particular the ductile-to-brittle transition temperature and fracture toughness estimations.
DOI: 10.5290/400036
title: Small punch tensile/fracture test data for P91 material at -150 °C and a displacement rate of .003 mm/s

description: The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation of the data with that obtained from conventional creep tests, supports the need to exploit the recently launched Code of Practice for Small Punch Testing (CEN/WS 21). The present work is specifically concerned with investigating the creep behaviour of P91 steel weldments at 600 Celsius along with low-temperature fracture behaviour. Thin discs, 8 mm in diameter and 0.5 mm thick, were manufactured from different zones of a component containing a P91 welded joint: base metal (BM), service- exposed material (SE), weld metal (WM), fine-grain and coarse-grain heat affected zones (FG-HAZ & CG-HAZ). The results of SP creep tests on these disks, performed at 600 Celsius under different loads carefully following the Code of Practice, could be correlated with uniaxial creep data. The SP test is shown to be a reliable method to depict creep behaviour of this alloy and its weldments and a creep model derived, useful for life time prediction, could also be demonstrated through FEA to predict the creep deformation of the SP discs. Additionally, the SP testing method shows potential to evaluate the fracture properties of P91 weldments, in particular the ductile-to-brittle transition temperature and fracture toughness estimations.
DOI: 10.5290/6000101
title: Low cycle fatigue - strain control test data for AISI 316 L material at 550 °C

description: In May 1985 a European programme on intercomparison of low cycle fatigue (LCF) testing was started under the auspices of the EEC Community Bureau of Reference (BCR). Subsequently, as a result of the Versailles Project on Advanced Materials and Standards (VAMAS), a wider international participation was sought. The objective of the programme was to establish a set of high temperature LCF data representative of accepted testing practice and, subsequently, to identify the significant aspects of testing procedure affecting the repeatability and reproducibility as a basis for defining a standard test procedure. In view of the potential influence of material characteristics on LCF life, three classes of alloy were selected for testing according to their cyclic strain behaviour, namely strain-hardening, strain-softening, and stable. This data collection consists of test results on AISI 316L stainless steel at 550°C, which is representative of the cyclic strain-hardening case.
DOI: 10.5290/400041
title: Small punch tensile/fracture test data for P91 material and a displacement rate of .003 mm/s (repeat test)

description: The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation of the data with that obtained from conventional creep tests, supports the need to exploit the recently launched Code of Practice for Small Punch Testing (CEN/WS 21). The present work is specifically concerned with investigating the creep behaviour of P91 steel weldments at 600 Celsius along with low-temperature fracture behaviour. Thin discs, 8 mm in diameter and 0.5 mm thick, were manufactured from different zones of a component containing a P91 welded joint: base metal (BM), service- exposed material (SE), weld metal (WM), fine-grain and coarse-grain heat affected zones (FG-HAZ & CG-HAZ). The results of SP creep tests on these disks, performed at 600 Celsius under different loads carefully following the Code of Practice, could be correlated with uniaxial creep data. The SP test is shown to be a reliable method to depict creep behaviour of this alloy and its weldments and a creep model derived, useful for life time prediction, could also be demonstrated through FEA to predict the creep deformation of the SP discs. Additionally, the SP testing method shows potential to evaluate the fracture properties of P91 weldments, in particular the ductile-to-brittle transition temperature and fracture toughness estimations.
DOI: 10.5290/400065
title: Uniaxial creep test data for P91 material at 600 °C and a stress of 155 MPa (repeat test)

description: The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation of the data with that obtained from conventional creep tests, supports the need to exploit the recently launched Code of Practice for Small Punch Testing (CEN/WS 21). The present work is specifically concerned with investigating the creep behaviour of P91 steel weldments at 600 Celsius along with low-temperature fracture behaviour. Thin discs, 8 mm in diameter and 0.5 mm thick, were manufactured from different zones of a component containing a P91 welded joint: base metal (BM), service- exposed material (SE), weld metal (WM), fine-grain and coarse-grain heat affected zones (FG-HAZ & CG-HAZ). The results of SP creep tests on these disks, performed at 600 Celsius under different loads carefully following the Code of Practice, could be correlated with uniaxial creep data. The SP test is shown to be a reliable method to depict creep behaviour of this alloy and its weldments and a creep model derived, useful for life time prediction, could also be demonstrated through FEA to predict the creep deformation of the SP discs. Additionally, the SP testing method shows potential to evaluate the fracture properties of P91 weldments, in particular the ductile-to-brittle transition temperature and fracture toughness estimations.
DOI: 10.5290/6020601
title: Low cycle fatigue - strain control test data for IN 718 material at 550 °C (fifth repeat test)

description: In May 1985 a European programme on intercomparison of low cycle fatigue (LCF) testing was started under the auspices of the EEC Community Bureau of Reference (BCR). Subsequently, as a result of the Versailles Project on Advanced Materials and Standards (VAMAS), a wider international participation was sought. The objective of the programme was to establish a set of high temperature LCF data representative of accepted testing practice and, subsequently, to identify the significant aspects of testing procedure affecting the repeatability and reproducibility as a basis for defining a standard test procedure. In view of the potential influence of material characteristics on LCF life, three classes of alloy were selected for testing according to their cyclic strain behaviour, namely strain-hardening, strain-softening, and stable. This data collection consists of test results on IN 718 alloy at 550°C, which is representative of the cyclic strain-softening case.
DOI: 10.5290/400009
title: Small punch creep test data for P91 material at 600 °C and a load of 240 N (repeat test)

description: The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation of the data with that obtained from conventional creep tests, supports the need to exploit the recently launched Code of Practice for Small Punch Testing (CEN/WS 21). The present work is specifically concerned with investigating the creep behaviour of P91 steel weldments at 600 Celsius along with low-temperature fracture behaviour. Thin discs, 8 mm in diameter and 0.5 mm thick, were manufactured from different zones of a component containing a P91 welded joint: base metal (BM), service- exposed material (SE), weld metal (WM), fine-grain and coarse-grain heat affected zones (FG-HAZ & CG-HAZ). The results of SP creep tests on these disks, performed at 600 Celsius under different loads carefully following the Code of Practice, could be correlated with uniaxial creep data. The SP test is shown to be a reliable method to depict creep behaviour of this alloy and its weldments and a creep model derived, useful for life time prediction, could also be demonstrated through FEA to predict the creep deformation of the SP discs. Additionally, the SP testing method shows potential to evaluate the fracture properties of P91 weldments, in particular the ductile-to-brittle transition temperature and fracture toughness estimations.
DOI: 10.5290/400031
title: Small punch tensile/fracture test data for P91 material at -70 °C and a displacement rate of .003 mm/s

description: The data relate to a thesis concerned with demonstrating the suitability of Small Punch (SP) testing for lifetime prediction of metallic materials operating at high temperatures. The lack of standardisation of this technique and doubts about the correlation of the data with that obtained from conventional creep tests, supports the need to exploit the recently launched Code of Practice for Small Punch Testing (CEN/WS 21). The present work is specifically concerned with investigating the creep behaviour of P91 steel weldments at 600 Celsius along with low-temperature fracture behaviour. Thin discs, 8 mm in diameter and 0.5 mm thick, were manufactured from different zones of a component containing a P91 welded joint: base metal (BM), service- exposed material (SE), weld metal (WM), fine-grain and coarse-grain heat affected zones (FG-HAZ & CG-HAZ). The results of SP creep tests on these disks, performed at 600 Celsius under different loads carefully following the Code of Practice, could be correlated with uniaxial creep data. The SP test is shown to be a reliable method to depict creep behaviour of this alloy and its weldments and a creep model derived, useful for life time prediction, could also be demonstrated through FEA to predict the creep deformation of the SP discs. Additionally, the SP testing method shows potential to evaluate the fracture properties of P91 weldments, in particular the ductile-to-brittle transition temperature and fracture toughness estimations.