Conception, development and evaluation of polymer-based screen-printed textile electrodes for biopotential monitoring
Creators: name: ACHILLI, ANDREA
Publisher: name: Universit� degli studi di Genova
Year: 2019

description: Wearable technologies represent the new frontier of vital signs monitoring in different applications, from fitness to health. With the progressive miniaturization of the electronic components, enabling the implementation of portable and hand-held acquisition and recording devices, the research focus has shifted toward the development of effective and unobtrusive textile electrodes. This work deals with the study, development and characterization of organic-polymer-based electrodes for biopotentials. After an overview of the main materials and fabrication technologies presented so far in the scientific literature, the possibility to use these electrodes as an alternative to the Ag/AgCl disposable gelled electrodes usually adopted in clinical practice was tested. For this purpose, several textile electrode realization techniques were studied and optimized, in order to create electrodes with adequate features to detect two fundamental physiological signals: the electrocardiogram (ECG) and the electromyogram (EMG). The electrodes were obtained by depositing on the fabric the organic bio-compatible polymer poly(3,4-ethylenedioxythiophene) doped with poly(4-styrenesulfonate) (PEDOT:PSS) with three deposition procedures: dipcoating, ink-jet printing and screen printing. The physical?chemical properties of the polymer solution were varied for each procedure to obtain an optimal and reproducible result. For what concerns the ECG signal, the research activity focused on screen-printed textile electrodes and their performance was first assessed by benchtop measurements and then by human trials. The first tests demonstrated that, by adding solid or liquid electrolytes the electrodes, the largest part of the characteristics required by the ANSI/AAMI EC12:2000 standard for gelled ECG electrodes can be achieved. Tests performed in different conditions showed that the skin contact impedance and the ECG morphological features are highly similar to those obtainable with disposable gelled Ag/AgCl electrodes (? &gt; 0.99). A trial with ten subjects revealed also the capability of the proposed electrodes to accurately capture with clinical instruments an ECG morphology with performance comparable to off-the-shelf disposable electrodes. Furthermore, the proposed textile electrodes preserve their electrical properties and functionality even after several mild washing cycles, while they suffered physical stretching. Similar tests were performed on screen-printed textile electrodes fabricated in two different sizes to test them as EMG sensors, with and without electrolytes. After a series of controlled acquisitions performed by electro-stimulating the muscles in order to analyze the waveform morphologu of the M-wave, the statistical analysis showed a high similarity in terms of rms of the noise and electrode-skin impedance between conventional and textile electrodes with the addition of solid hydrogel and saline solution. Furthermore, the M-wave recorded on the tibialis anterior muscle during the stimulation of the peroneal nerve was comparatively analyzed between conventional and textile electrodes. The comparison provided an R2 value higher than 97% in all measurement conditions. These results opened their use in smart garments for real application scenarios and for this purpose were developed a couple of smart shirts able to detect the EGC and the EMG signal. The results indicated that this approach could be adopted in the future for the development of smart garments able to comfortably detect physiological signals.