Effects of a Two-Step Silver Diamine Fluoride Varnish on Shear Bond Strength of Restorations, Dentin and Enamel Hardness, and Biofilm Formation
Authors: Tiba Al A , Tiba Amer , Horvath Francis , Huh Eun Y , Ford April A , Arens Daniel K , Sarwar Thamar A , Hwang Yoon Y 
Published: July 2022

ABSTRACT

Introduction
Dental caries are a limiting factor in maintaining dental and medical readiness in the military. Untreated dental caries can lead to dire health consequences. Consistent and comprehensive access to dental care is often limited due to the intensive operational demands on our nation’s warfighters. The standard of care for dental caries is a surgical model where diseased tooth tissue is surgically removed and restored with appropriate restorative materials. While effective, it is not practical in the military operational environment, especially under time constraints. Dental restoratives offer military personnel a simple and preventive treatment of dental caries and are suitable as self-applied first aids. The purpose of this study was to measure the shear bond strengths of two dental restorative materials to human teeth paired with two different fluoride treatments and the hardness and biofilm formation on teeth after applying the fluoride varnishes.

Materials and Methods
Specimens were made of human molar teeth treated with each of the following four materials: glass ionomer cement GC Fuji II LC Capsules, Filtek Z250, Riva Star steps 1 and 2, or Mark3 NaF varnish. Step 1 of Riva Star consists of silver diamine fluoride and step 2 contains potassium iodide. On human molar slabs, 10 circular specimens of 5 cm in diameter were prepared with restoratives according to manufacturer procedures. Etch-Rite and a proprietary aluminum chloride-based cavity conditioner were used as etchants on tooth surfaces for the Filtek Z250 and glass ionomer cement, respectively. After at least 24 hours underwater, each assembly was removed, and the shear bond strength of the adhesive was measured according to International Organization for Standardization (ISO) 29022.
The hardness was measured according to ISO 14233. Hardness measurements were performed before varnish application, then after storage in an incubator at 37 °C for 4 hours in a demineralization solution (pH = 4.5), and after 1 day in a mineralization solution (pH = 7). A crystal violet staining assay was used to measure biofilm formation of Streptococcus mutans bacteria on human molar teeth after the application of fluoride varnish.

Results
We report a 16% increase in shear bond strength of the Filtek Z250/Riva Star coupled treatment compared to the Filtek Z250/Mark3 NaF coupled treatment. We also demonstrate a significant 84% decrease in bond strength with a GC Fuji II LC/Mark3 NaF treatment compared to control (P = .0002), while Riva Star remains statistically unchanged. Enamel and dentinal hardness are significantly improved when Riva Star is applied compared to NaF varnish. A 25%-35% (P &lt; .0001) decrease in oral biofilm formation was observed on samples where a Riva Star or NaF varnish was applied.

Conclusions
Mechanical and antimicrobial testing indicated Riva Star, compared favorably with and in some cases, performed better in the laboratory than a Mark3 NaF varnish. Hardness measurements indicated Riva Star is more effective in dentin tubule occlusion compared to NaF varnish. Our findings help provide practical suggestions to dental treatment, particularly to the unique dental environments seen in the military. Riva Star may be used as an adjunctive treatment prior to placing a final restoration. This study supports the use of Riva Star in conjunction with GC Fuji II LC or Filtek Z250 restorative materials, making it a promising treatment in military dental applications.