The Corrosion of metals in an oxidizing‐chloridizing environment at high temperature
Authors: Stott F. H. , Prescott R. , Elliott P. 
Published: May 2005

AbstractAn investigation has been undertaken into the behaviour of metals which form the basis of high‐temperature alloys in an argon −5.5% oxygen −0.96% hydrogen chloride −0.86% sulphur dioxide gas mixture at 900°C. The intention has been to ascertain the reaction products, with particular emphasis on the formation of volatile species which can cause considerable degradation of commercial alloys in this environment. From consideration of the thermodynamics of the gas system, the potentials of the reactive species can be determined and correlated with the possible reaction products. In this gas mixture, the oxides of nickel, iron, cobalt, chromium, molybdenum and tungsten are the stable phases with respect to the corresponding metals. Indeed, on exposure of the metals to the environment, the appropriate oxide scales are developed. However, the reactions are complicated by formation of volatile corrosion products, particularly for nickel, cobalt and molybdenum. Although a Cr2O3 scale is established on chromium, there is evidence for penetration of chlorine‐containing species to the scale/alloy interface. The oxide scale on tungsten is not very protective and thickens rapidly while that on molybdenum is volatile, resulting in rapid consumption of the specimen.
Hochkorrosionsbeständige Sonderstähle für Rauchgas‐Entschwefelungsanlagen
Authors: Kiesheyer Heinrich , Roth Peter 
Published: May 2005

AbstractHochkorrosionsbeständige Edelstähle haben sich unter den in Rauchgas‐Entschwefelungsanlagen (REAs) herrschenden Korrosionsbedingungen bewährt. Neben der allgemeinen, d.h. abtragenden Korrosion, ist vor allem mit Lochfraß‐, Spalt‐ und ggfs. auch mit Spannungsrißkorrosion zu rechnen. Es müssen deshalb Sonderstähle verwendet werden. Als notwendig haben sich Stähle mit einem Mindestzusatz von 2,75% Mo erwiesen. Mit steigendem Chloridanteil und sinkendem pH‐Wert der Suspension müssen immer höher legierte Stähle bis zu etwa 6% eingesetzt werden.Eine Reihe dieser Stähle wird hinsichtlich der Legierungszusammensetzung und der mechanischen Eigenschaften beschrieben. In Labor‐ und Betriebsversuchen wurde der mögliche Einsatzbereich überprüft. Günstig hat sich der Einsatz stickstofflegierter Stähle erwiesen. Durch den Stickstoff‐Zusatz werden die mechanischen Eigenschaften und die Gefügestabilität verbessert. Bei Wärmebeeinflussung wird die Ausscheidung schädlicher intermetallischer Phasen durch Stickstoff zeitlich verzögert, so daß Schweißoperationen mit größerer Sicherheit durchgeführt werden können.Anhand von Beispielen wird die Werkstoffauswahl in verschiedenen Verfahrensprozessen erläutert.In dem Bericht wird auf die bisherigen Erfahrungen mit Rauchgas‐Entschwefelungsanlagen mit Edelstahl‐Komponenten eingegangen.Das Schweißen mit überlegiertem Schweißzusatzwerkstoff auf der mediumberührten Seite hat sich bewährt.
Korrosionsverhalten feuerverzinkter Baustähle in überwiegend sandhaltigen Böden
Authors: Nünberger Ulf 
Published: May 2005

AbstractIn überwiegend sandhaltigen Böden mit unterschiedlichem Feinanteil < 0,06 mm (2,5–20,4%) wurden Proben aus unverzinktem und feuerverzinktem Baustahl im Freien und im Labor ausgelagert. Neben der Bodenzusammensetzung wurde auch der Salzgehalt und die Bodentemperatur variiert. Es wurden die Korrosionsrate und bei unverzinkten Teilen auch das Lochkorrosionsverhalten ermittelt. Weiterhin wurden die das Korrosionsverhalten kennzeichnenden Größen wie spezifischer Bodenwiderstand und Korrosionspotential kontinuierlich verfolgt.Der Metallabtrag war bei unverzinkten Teilen sehr viel ausgeprägter als bei feuerverzinkten und nahm bei unverzinkten auch mit steigendem Feinanteil der Böden zu. Salzzugaben zu Beginn der Versuche bewirkten einen erhöhten Abtrag, beeinflußten bei feuerverzinkten Teilen jedoch nur die Anfangskorrosion. Die erhöhten Abtragungen setzten etwa ab Gehalten von 3 · 10−3 MolCl− + SO/kg ein. Wurden Salze dem Boden erst nach 2 Jahren (nach Deckschichtbildung) zugegeben, dann erhöhten diese zwar bei unverzinkten, nicht jedoch bei feuerverzinkten Proben den Abtrag.Von unverzinkten Stählen in dem Boden mit 20,4% Feinanteil abgesehen, trat nach einer anfänglich stärkeren Korrosion eine Verlangsamung infolge Deckschichtbildung ein.Bei den unverzinkten Proben trat starke Lochkorrosion auf, und zwar in den belüftungsfähigen Böden stärker als in den dichteren und somit wasserhaltigeren. Salzzugaben förderten eher einen allgemeinen Abtrag als eine Lochkorrosion.Bei feuerverzinkten Teilen wurde nach örtlichem Abtrag des Zinks unter extremen Verhältnissen der Stahluntergrund kaum abgetragen. Die zinkfreien Stellen wurden durch das noch vorhandene Zink kathodisch geschützt.Die Korrosion von Stahl ist temperaturabhängig: Bei Erhöhung der Temperatur von 4 auf 20°C wurden Korrosionszunahmen um bis zu 100% festgestellt. Bei Feuerverzinkungen ist der Temperatureinfluß auf die Korrosion nur gering.
Waste incineration plants in the FRG: Construction, materials, investigation on cases of corrosion
Authors: Reichel H.‐H. , Schirmer U. 
Published: May 2005

AbstractThe development and future aspects of waste incineration in Germany are described with emphasis to corrosion problems. The heterogeneity of waste and special components are the cause of higher corrosion risk in comparison with other fuels, e.g. coal.The materials used in waste incineration plants are preferably the same as in fossil fuel fired boilers, namely un‐ and low‐alloyed steels. Constructive measures are used to avoid enhanced corrosion.Examples are given for enhanced fire‐side corrosion of evaporator and superheater tubes. Corrosion in the combustion chamber is to about 50% caused by local reducing conditions. At the other 50% chlorine compounds play a decisive role. Corrosion in the superheater area is usually caused by “high temperature chlorid corrosion”.
Low temperature corrosion in domestic refuse boilers monitored with cooled corrosion probes and test heat exchangers
Authors: Jansen Piet 
Published: May 2005

AbstractCorrosion properties of materials for utilizing of flue gas energy by cooling the gas below the acid dew point have been studied with cooled corrosion probes. The U‐tube corrosion probe is found to be a reliable method where tests can be done in the actual plant environment. Results from one domestic refuse boiler plant with severe low temperature corrosion problems are reported and the results described indicating a minimum temperature of 75°C to avoid corrosion.Another set of results is reported with flue gas cleaning and cooling in an experimental heat exchanger. Unalloyed steel is found to show the same level of corrosion in both raw uncleaned and cleaned flue gas. AISI 316 and 254 SMO stainless steels have shown high corrosion rates in the raw gas but a satisfactory resistance in the cleaned gas.
Untersuchung des SwRK‐Verhaltens des martensitaushärtenden Stahls X 5 CrNiCuNb 17 4 PH im Vergleich zum weichmartensitischen Stahl X 4 CrNiMo 16 5 1 ESU in chloridhaltigen wäßrigen Medien. Teil 1: Korrosionsuntersuchungen und SpRK‐Untersuchungen zur Optimierung der Wärmebehandlung bezüglich der SpRK‐Beständigkeit
Authors: Schmitt‐Thomas Kh. G. , Wunderlich R. , Happle Th. 
Published: May 2005

AbstractDurch eine Optimierung der Werkstoffe sollte die Betriebssicheheit und Wirtschaftlichkeit von SwRK‐beanspruchten Bauteilen, insbesondere bei erhöhten Temperaturen, verbessert werden. Deshalb wurde der Einfluß eines erhöhten Reinheitsgrades durch sekundärmetallurgische Nachbehandlung am elektroschlacke‐umgeschmolzenen, weichmartensitischen Stahl X4CrNiMo 16 5 1 ESU ermittelt, sowie das SwRK‐Verhalten des martensitaushärtenden Stahles X5CrNiCuNb 17 4 PH mit einem im Hinblick auf die Spannungsrißkorrosionsbeständigkeit gezielten Wärmebehandlungszustand untersucht.Die SpRK‐Untersuchungen wurden für alle Wärmebehandlungszustände des 17‐4 PH in 22% NaCl/pH3‐Lösung, und bei einer Temperatur von 80 bis 150°C durchgeführt. Der martensitaushärtende Stahl zeigte mit einer dreistufigen Wärmebehandlung die höchste Beständigkeit gegen SpRK.Die metallurgische Nachbehandlung des weichmartensitischen Stahles brachte keine Verbesserung der SpRK‐Beständigkeit gegenüber dem nicht behandelten Werkstoff. Dies ist durch das instabilpassive Verhalten des Werkstoffes bedingt, das insbesondere bei den 150°C‐Versuchen zur Rißeinleitung an chlorid‐induzierten Lochfraßstellen führt.Die Untersuchung des elektrochemischen Korrosionsverhaltens beider Werkstoffe zeigte, daß der pH‐Wert nur einen geringen Einfluß auf die Korrosionsbeständigkeit hat. Ein Erhöhen des Salzgehaltes führt zu einer gesteigerten Lochfraßinduzierung. Bei Temperaturen von 80°C in gesättigter NaCl‐Lösung kann nicht mehr von einem Passivbereich gesprochen werden. In potentiodynamischen Untersuchungen war ein direkter Übergang vom Aktivbereich zum Lochfraßpotential zu beobachten. Auch hier konnte in Einklang mit den SwRK‐ (Teil II) und SpRK‐Untersuchungen festgestellt werden, daß ein frühzeitiger Ausfall des 17‐4 PH eintritt, wenn Cu‐haltige bzw. Oxidische Einschlüsse an der Oberfläche vorhanden sind.
Inhibition of localized attack on the aluminium alloy AA 6351 in glycol/water solutions
Authors: Monticelli C. , Brunoro G. , Zucchi F. , Fagioli F. 
Published: May 2005

AbstractA previous study had shown that exposure to degraded propylene glycol(PG)/water solution (1:1 in volume) at 80°C for 60 days or to boiling PG/water solution for 30 days induce remarkable localized attack on aluminium alloy AA 6351 (nominal composition: 1% Si, 0.6% Mg, 0.3% Mn, balance Al).In the present work degradation of the solution was achieved by holding the PG/water solution at its boiling temperature for 30 days in contact with AA 6351.The observed localized attack was mainly attributed to the action of copper ions dissolved from the aluminium alloy (copper content = 0.07%) and then deposited as small spots acting as efficient cathodic areas.The objective of this work was to examine the feasibility of enhancing pitting resistance of AA 6351 by adding suitable inhibitors to the solutions. The compounds used were two inorganic salts: sodium molybdate and sodium tungstate and two derivatives of pyrimidine: 2‐aminopyrimidine (2AP) and 2‐hydroxypyrimidine (2HP). The inhibiting efficiencies of these substances were tested by both short‐time electrochemical tests (galvanic coupling tests and polarization curves) and long‐time immersions under experimental conditions causing the localized attack. Molybdate, tungstate and, to some extent, also 2AP efficiently inhibit AA 6351 localized corrosion in degraded solutions at 80°C and in pure boiling solutions, for long exposure periods.The short‐time electrochemical tests suggest that molybdate and tungstate are able to retard the electrochemical processes occurring on both the aluminium alloy and the small copper cathodic area produced by copper deposition. On the other hand, the 2AP efficiency is attributed to some complexing capability of this pyrimidine derivative towards dissolved copper ions, that are stabilized in solution. 2HP does not prevent AA 6351 localized attack.
High performance alloys for solving severe corrosion problems in flue gas desulfurization systems
Authors: Asphahani A. I. , Nicholas A. F. , Silence W. L. , Meyer T. H. 
Published: May 2005

AbstractNickel‐base alloys have been used as cost‐effective measures in a variety of severely corrosive situations in pollution control units for coal‐fired power plants. Cost‐effectiveness and practical answers to corrosion problems are illustrated (specifically the “wallpaper concept”/metallic lining technique). Numerous cases of successful use of HASTELLOY® alloys in Flue Gas Desulfurization (FGD) system are listed. New developments in nickel‐base alloys and their use in FGD components are discussed.In the Ni‐Cr‐Mo‐W alloy family, C‐22™ alloy has the best resistance to localized corrosion in halide environments (chlorides/fluorides‐containing solutions).The H‐9M™ alloy is the latest development in the Ni‐Cr‐Mo‐Fe alloy family. This alloy has shown superior performance in its resistance to localized corrosion, compared to alloy 625. H‐9M alloy has been tested in several FGD systems and placed in field service. This iron‐containing alloy is an attractive candidate due to its moderate cost.
Spannungsrißkorrosion nichtrostender austenitischer Chrom‐Nickel‐Stähle bei Raumtemperatur
Authors: Herbsleb Günter , Theiler Franz 
Published: May 2005

AbstractFür die chloridinduzierte Spannungsrißkorrosion mit transkristallinem Rißverlauf in nichtrostendem austenitischem 18Cr10Ni‐Stahl besteht eine Grenztemperatur zwischen 45 und 50°C. Diese Grenztemperatur gilt jedoch nur für den passiven Zustand des Werkstoffs in annähernd neutralen Chloridlösungen. Im aktiven Zustand kann Spannungsrißkorrosion mit transkristallinem Rißverlauf bei Temperaturen bis herab zu Raumtemperatur auftreten. Der aktive Zustand wird durch stark saure, hochchloridhaltige wäßrige Angriffsmittel erzeugt. Adhärierende Wasserfilme mit diesen Eigenschaften können auf Bauteilen in Hallenschwimmbädern entstehen, wenn das Schwimmbadwasser durch Zugabe von Chlor desinfiziert wird. Unter diesen Voraussetzungen sind Schäden an austentischen CrNi‐ und CrNiMo‐Stählen durch transkristalline Spannungsrißkorrosion bei Raumtemperatur möglich und auch tatsächlich aufgetreten.Spannungsrißkorrosion mit vorwiegend interkristallinem Rißverlauf ist bei Raumtemperatur auch möglich, wenn austenitische nichtrostende Stähle mit sensibilisierten Gefügezuständen verwendet werden. Unter diesen Bedingungen wird der Korrosionsangriff durch unspezifische Angriffsmittel, z. B. chloridfreie adhärierende Wasserfilme, erzeugt. Der Rißverlauf, interkristallin oder gemischt, hängt von der Spannungshöhe ab.
Einfluß betriebsnaher thermischer Belastung auf die Eigenschaften von Y2O3‐teilstabilisierten ZrO2‐Wärmedämmschichten
Authors: Schmitt‐Thomas Kh. G. , Steppe P. 
Published: May 2005

AbstractDurch den Einsatz plasmagespritzter Wärmedämmschichten besteht die Möglichkeit, thermisch hochbeanspruchte Komponenten im Triebwerk vor Überlastung zu schützen. Als keramischer Werkstoff eignet sich besonders Y2O3‐teilstabilisiertes Zirkoniumoxid. Im Hinblick auf die hohen Einsatztemperaturen wurden die Wärmedämmschichten bei Temperaturen bis 1500 °C auf ihre Beständigkeit bezüglich Phasenzusammensetzung, Porosität, Härte und Gefügestruktur untersucht. Es konnte aufgezeigt werden, daß Gefügeveränderungen zu einer starken Erhöhung der Porosität und damit zu einem Härteabfall führen. Bei der Phasenzusammensetzung ergab sich nach der Wärmebehandlung nur eine geringfügige Veränderung zugunsten der monoklinen und kubischen Modifikation.
Versuche zur Natriumkorrosion austenitischer Werkstoffe bei 1000 °C
Authors: Borgstedt Hans Ulrich , Frees Günter , Jesper Heinz 
Published: May 2005

AbstractEine Reihe austenitischer Werkstoffe, die für den Einsatz bei hohen Temperaturen hinreichende Festigkeit aufweisen, wurden auf ihre Beständigkeit gegen flüssiges Natrium bei 1000 °C untersucht. Die höchste Beständigkeit wiesen austenitische Stähle mit etwa 12% Nickel auf, aber auch die Werkstoffe mit 32% Nickel und 20% Chrom zeigten nur mäßige Gewichtsverluste, allerdings auch innere Korrosionseffekte. Nickelbasislegierungen wurden am stärksten angegriffen und sind trotz ihrer hohen Festigkeit für den Einsatz mit Natrium bei sehr hohen Temperaturen weniger geeignet.
Qualification of NICROFER 3127 LC for the Preconcentration of phosphoric acid
Authors: Kirchheiner R. , Schalk W. , Müller H. , Palomino S. M. 
Published: May 2005

AbstractAfter practice‐related corrosion tests in both laboratory and pilot plant as well as in consideration of corrosion data already available, the FeNiCrMoCu alloy NICROFER® 3127 LCNICROFER® and CRONIFER® are registered trademarks of VDM Nickel‐Technologie AG, D‐5980 Werdohl.
could be qualified within a very short time as an alternative for graphite heat exchangers for preconcentrating phosphoric acid.The corrosion rates of this alloy in a 26 to 52 wt.%, halidecontaining phosphoric acid solution at temperatures up to 80 °C are distinctly below 0.1 mm/year. Welding, e.g. by the Plasma‐GMAW or GTAW Process does not adversely affect the corrosion resistance.A fully metallic heat exchanger used for preconcentrating phosphoric acid has proven its value in nearly two years' operation, showing an integral corrosion rate of less than 0.1 mm/year.Starting from this experience, further plant components are being designed or under construction. Two reconstructed plants have been in operation since April 1988.
Korrosionsbeständigkeit von Verbindungen von Rohren aus nichtrostenden Stählen in Wässern
Authors: Herbsleb G. , Szederjei E. 
Published: May 2005

AbstractDie wichtigsten gebräuchlichen Verbindungen von Rohren aus nichtrostenden Stählen, die für den Transport von Wässern und Gasen verwendet werden, sind Schweiß‐ und Hartlötverbindungen. Beide Verbindungen sind bei Korrosionsbelastung durch trockene Gase beständig. In Wässern und wäßrigen Kondensaten bestehen jedoch Anwendungsgrenzen hinsichtlich der Korrosionsbeständigkeit.Die Korrosionsbeständigkeit der Schweißverbindungen von Rohren aus nichtrostenden Stählen wird herabgesetzt durch
– Anlauffarben (Oxidfilme) und Zunderschichten im Bereich der Schweißnaht;
– Gefügeveränderungen in der Umgebung der Schweißnaht (Sensibilisierung des nichtrostenden Stahles);
– Oberflächenbehandlung (Schleifen) nach dem Schweißen;
– Schweißfehler infolge nicht fachgerechten Schweißens.

Art und Umfang von Korrosionsschäden an Schweißverbindungen mit verminderter Korrosionsbeständigkeit hängen von der Beschaffenheit der Wässer, hauptsächlich von deren Chloridgehalten, ab. Kennzeichnende Beispiele der verminderten Beständigkeit von Schweißnähten gegen Korrosion und mögliche Schadensarten, nämlich Lochkorrosion, Spaltkorrosion sowie Spannungsrißkorrosion und deren Ursachen, werden beschrieben. Weiterhin wird gezeigt, durch welche Maßnahmen die Korrosionsbeständigkeit der Schweißverbindungen von Rohren aus nichtrostenden Stählen erhöht wird.Verbindungen von Rohren aus nichtrostenden Stählen mittels Kapillarhartlötfittings sind durch Messerschnittkorrosion an der Phasengrenze Stahl/Lot gefährdet. Messerschnittkorrosion bezeichnet hier ein Aufheben der Haftung Stahl/Lot. Das Ausmaß der Korrosionsgefährdung hängt von der Wasserbeschaffenheit, im wesentlichen vom Chloridgehalt und pH‐Wert der Wässer, ab.Ein verhältnismäßig neues Verbindungssystem in der Installationstechnik ist der Preßfitting mit nichtmetallischer Dichtung. Diese Verbindungstechnik wird beschrieben. Für die Trinkwasser‐Hausinstallation wurde ein Installationssystem mit Rohren und Preßfittings aus nichtrostendem Chrom‐Nickel‐Molybdän‐Stahl Werkstoff Nr. 1.4401 (X 5 CrNiMo 17122) entwickelt. Dieses System ist bei Korrosionsbelastung durch Trinkwässer üblicher Zusammensetzung korrosionsbeständig und wird bereits in erheblichem Umfang betrieblich angewendet.Als weitere Verbindungssysteme gibt es Schweißfittings, Schneidring‐ und Klemmringverschraubungen sowie Gewindefittings aus nichtrostenden Stählen. Diese Systeme sind weniger gebräuchlich als die zuvor beschriebenen Verbindungen.
Influence of the molybdenum content of high‐alloy stainless steels and of the precipitation of intermetallic phases on pitting resistance in chloride‐containing media
Authors: Wallis E. 
Published: May 2005

AbstractThe influence of molybdenum on the resistance of stainless steels and nickel alloys (NiCrMoFe) to pitting corrosion is determined by means of electrochemical measurements (0.5 M NaCl/N2, 0…90°C) in both homogeneous and heterogeneous materials. As far as homogeneous materials are concerned, this influence is due to the inhibiting effect of molybdate formed at the interface passive layer/electrolyte and to a change in structure of the passive layer. The molybdate becomes effective as inhibitor of pitting corrosion only after the transpassive dissolution potential of molybdenum has been exceeded.Due to the precipitation of intermetallic phases, the pitting potential is shifted in cathodic direction. From a certain amount of precipitated intermetallic phases onward, the pitting potential remains constant. Consequently, the pitting potential is not dependent on the concentration of the alloying elements in the depleted matrix. Pitting corrosion preferably occurs at the phase boundaries intermetallic phase/depleted matrix and is due to lattice irregularities. Pit nucleation is observed at potentials at which the molybdate required for the inhibition of pitting corrosion has not yet been formed. Additions of molybdate to the electrolyte inhibit nucleation at the phase boundaries.Molybdenum segregates heavily in the weld microstructure of the afore‐mentioned materials when compared with chromium. Pitting corrosion occurs at the dendrites that are poorer in molybdenum. A comparison of solution‐annealed materials with different molybdenum contents shows that the molybdenum concentration of the dendrites imparts the same pitting resistance as is observed with solution‐annealed materials with the same constant molybdenum content, respectively.
Einfluß von Verformung und spannungsinduzierten Ausscheidungen auf die Korrosionsbeständigkeit von siliciumlegiertem, nichtrostendem Stahl X2CrNiSi 18 15 in Salpetersäure
Authors: Herbsleb G. , Schwaab P. , Jäkel U. 
Published: May 2005

AbstractDie Korrosionsbeständigkeit von siliciumlegiertem, nichtrostendem Stahl X2CrNiSi 18 15 in Salpetersäure wird von Werkstoffverformung sowie vom Ausscheidungszustand beeinflußt. Kaltverformter und anschließend bei 700°C wärmebehandelter Werkstoff erbringt höhere flächenbezogene Massenverlustraten als unverformter Werkstoff. Dies wurde für voneinander isolierte Proben, besonders ausgeprägt aber für Proben in metallenleitendem Kontakt, nachgewiesen. Durch Verformen und nachfolgendes Glühen bei 700°C werden Ausscheidungen auf den Korngrenzen erzeugt, deren Menge mit ansteigendem Verformungsgrad zunimmt und die sich mit ansteigendem Verformungsgrad auch zunehmend an den Gleitlinien anordnen. Bei den Ausscheidungen handelt es sich um chromreiches Carbid M23C6 sowie um ein Silicid Cr5Ni3FeSi2. Durch elektrochemische Korrosionsversuche wurde gezeigt, daß diese Ausscheidungen die kathodische Teilreaktion der Salpetersäurereduktion stimulieren. Verformung des Werkstoffs und spannungsinduzierte Ausscheidungen vermindern somit dessen Korrosionsbeständigkeit in Salpetersäure.
Zunderablösung auf einem Heizrohr
Authors: Grabke H. J. , MüUuller E. M. 
Published: May 2005

AbstractDie Untersuchung wurde durch einen Schadensfall angeregt, ‐ein Heizrohr, auf dem sich der Zunder in kreisrundem Flecken abgelöst hatte. In diesen Flecken konnte kein aggressives Element festgestellt werden, offenbar hatte es sich verflüchtigt. Der Effekt konnte simuliert werden, indem auf das Material, ein 25Cr‐20Ni‐Stahl mit Spinell‐ und Chromoxidschicht, kleine Mengen festes Chlorid gebracht wurden. Nach Erhitzen auf 900°C an Luft hatten sich örtlich dicke lose Oxidkrusten gebildet, die beim Abfallen einen runden kahlen Fleck hinterlassen. Beim Vorgang zersetzt sich das Chlorid unter Chrombildung, das Chlor dringt in die Zunderschicht ein und katalysiert bis zur Verflüchtingung eine beschleunigte Oxidation unter Bildung von Eisenoxiden.
Einfluß von HCl und Cl2 auf die Hochtemperaturkorrosion des 2 1/4 Cr 1 Mo‐Stahls in Atmosphären mit hohen Sauerstoffdrücken
Authors: Bramhoff D. , Grabke H. J. , Reese E. , Schmidt H. P. 
Published: May 2005

AbstractDie Oxidation des 2 1/4Cr1Mo‐Stahls in oxidierenden He‐O2‐HCl‐Atmosphären bei 773 K wurde untersucht. Der Zusatz von HCl zu He‐O2‐Atmosphären führt zu stark beschleunigter Oxidation. Unter porösen und rissigen Oxidschichten bilden sich feste Chloride. Bei niedrigen HCl‐Drücken 0–1000 vppm bestimmt „aktive Oxidation”︁ den Korrosionsprozeß; d.h. Oxidation flüchtiger Chloride innerhalb der Oxidschicht. Bei höheren HCl‐Drücken 1000–3000 vppm erfolgt ein Übergang zum paralinearen Korrosionsverhalten, d.h. gleichzeitiges parabolisches Oxidwachstum und lineare Massenabnahme durch das Abdampfen von Chloriden.