Novel dinitroxide mediating agent for stable free‐radical polymerization
Authors: Lizotte Jeremy R. , Anderson Sara G. , Long Timothy E. 
Published: February 2004

AbstractA novel dinitroxide mediating agent that was suitable for stable free‐radical polymerization was synthesized and used in the block copolymerization of styrene and t‐butyl styrene. Quantitative yields of a novel dinitroxide based on 1,6‐hexamethylene diisocyanate and 4‐hydroxy‐2,2,6,6‐tetramethyl‐1‐piperidinyloxy were obtained. Various experimental parameters, including the nitroxide‐to‐initiator molar ratio, were examined, and it was determined that the polymerization was most controlled under conditions similar to those of conventional 2,2,6,6‐tetramethyl‐1‐piperidinyloxy‐mediated stable free‐radical polymerization. Moreover, the dinitroxide mediator proved to be a viable route for the facile two‐step synthesis of triblock copolymers of styrene and t‐butyl styrene. However, the dinitroxide mediation process resulted in a higher than expected level of nitroxide decomposition, which resulted in polymers possessing a terminal alkoxyamine and an adjacent hydroxylamine rather than a preferred internal bisalkoxyamine. This decomposition resulted in the formation of diblock copolymer species during the triblock copolymer synthesis. Gel permeation chromatography was used to monitor the chain‐end decomposition kinetics, and the determined observed rate constant (5.89 × 10−5 s−1) for decomposition agreed well with previous studies for other dinitroxide mediating agents. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 1547–1556, 2004
Synthesis and characterization of naphthyl‐substituted poly(p‐phenylenevinylene)s with few structural defects for polymer light‐emitting diodes
Authors: Lee Nancy Hoi Sim , Chen Zhi‐Kuan , Huang Wei , Xu Yi‐She , Cao Yong 
Published: February 2004

AbstractA series of naphthyl‐substituted poly(p‐phenylenevinylene)s (2N‐PPV, 4N‐PPV, and NAP‐PPV) has been synthesized and characterized by Fourier transform IR, 1H NMR, and elemental analysis. The polymers possess excellent solubility, high molecular weights, good thermal stability, and high photoluminescence efficiencies. Thermogravimetric analysis reveals the onset of degradation to be 347, 301, and 306 °C for 2N‐PPV, 4N‐PPV, and NAP‐PPV, respectively. The differential scanning calorimetry investigation gives the respective glass‐transition temperature values of 118, 135, and 141 °C. The UV and photoluminescence spectra measurements reveal that the polymers exhibit similar optical properties, indicating that side‐chain substitution has little effect on the optical properties of this series of polymers. Proton NMR measurement of the signal due to tolane–bisbenzyl defects at around 2.7 ppm indicates that all the polymers have negligible amounts of tolane–bisbenzyl defects along the polymer main chain as a result of the steric bulk imposed by the naphthalene side chain. The highest occupied and lowest unoccupied molecular orbital energy levels of the polymers are investigated through cyclic voltammetry. Polymer light‐emitting diodes utilizing the polymers as the emissive layer with a configuration of indium tin oxide/poly(3,4‐ethylenedioxythiophene)/polymer/Ba/Al are fabricated and evaluated. The diodes emit blue‐green to yellow‐green light with maximum peaks at 518, 542, and 486 nm for 2N‐PPV, 4N‐PPV, and NAP‐PPV, respectively. The respective turn‐on electric fields of the diodes are 0.84, 0.69, and 0.83 MV/cm and the respective maximum external quantum efficiencies are 0.08, 0.54, and 0.02%. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 1647–1657, 2004
Studies of ethylene–styrene copolymerization with dinuclear constrained geometry complexes with methyl substitution at the five‐membered ring in indenyl of [Ti(η5:η1‐C9H5SiMe2NCMe3)]2 [CH2]n
Authors: Noh Seok Kyun , Lee Mijung , Kum Don Ho , Kim Kiseok , Lyoo Won Seok , Lee Dong‐Ho 
Published: February 2004

AbstractThe new dinuclear half‐sandwich CGC (constrained geometry catalyst) with methyl substitution in indenyl, [Ti(η5:η1‐2‐methylindenyl)SiMe2NCMe3]2 [(CH2)n] [n = 6 (10), n = 9 (11), n = 12 (12)], have been synthesized, and structure of these complexes has been characterized by 1H and 13C NMR. The most important feature is that two protons of methylene directly bonded to the indenyl ring become inequivalent to be shown as two separated resonances at 2.9 and 3.0 ppm, probably due to the formation of planar chirality caused by a titanium complex formation. It has been found that the dinuclear CGCs with methyl substitution at an indenyl ring were very active catalysts for ethylene and styrene copolymerization. The activity increases in the order of 10 < 11 < 12, which indicates that the presence of a longer bridge between two active sites contributes to facilitate the polymerization activity of the dinuclear CGC more effectively. This result might be understood by the implication that the steric factor rather than the electronic factor may play a major role to direct the polymerization behavior of the dinuclear CGC. It is found that the dinuclear catalysts are very efficient to incorporate styrene in the polyethylene backbone. The styrene contents in the formed copolymers ranged from 5 to 40% according to the polymerization conditions. One can observe strong signals at 29.7 ppm of the polyethylene sequences, and, in addition, peaks at 27.5, 36.9, and 46. 2ppm (Sβδ, Sαδ, and Tδδ, respectively) of sequences of EESEE. Weak peak at 25.3 ppm are attributed to Sββ, which represents SES sequence. The absence of a signal for Tββ at 41.3 ppm and for Sαα at 43.6 ppm shows there is no styrene–styrene sequences in copolymers. This result indicates that the dinuclear CGC are very effective to generate well‐distributed poly(ethylene‐co‐styrene)s. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 1712–1723, 2004
Initiator‐fragment incorporation radical copolymerization of divinylbenzene and N‐isopropylacrylamide with dimethyl 2,2′‐azobisisobutyrate: Formation of soluble hyperbranched polymer nanoparticle
Authors: Sato Tsuneyuki , Higashida Naoki , Hirano Tomohiro , Seno Makiko 
Published: February 2004

AbstractThe copolymerization of divinylbenzene (DVB) and N‐isopropylacrylamide (NIPAm) with dimethyl 2,2′‐azobisisobutyrate of a concentration as high as 0.50 mol/L proceeded homogeneously without any gelation at 80 °C in N,N‐dimethylformamide, where the concentrations of DVB and NIPAm were 0.15 and 0.50 mol/L. The copolymer yield increased with time and leveled off over 50 min. Although DVB was consumed more rapidly than NIPAm, both comonomers were completely consumed in 50 min. The homogeneous polymerization system at 80 °C involved electron spin resonance‐observable propagating polymer radicals, the total concentration of which increased with time. The resulting copolymer was soluble in tetrahydrofuran, chloroform, acetone, ethyl acetate, acetonitrile, N,N‐dimethylformamide, dimethyl sulfoxide, and methanol, but insoluble in benzene, n‐hexane, and water. The copolymer showed an upper critical solution temperature (50 °C on cooling) in a methanol–water [11:3 (v/v)] mixture. Dimethyl 2,2′‐azobisisobutyrate fragments as high as 37–45 mol % were incorporated as terminal groups in the copolymers through initiation and primary radical termination. The contents of DVB and NIPAm were 10–30 mol % and 30–50 mol %, respectively. The intrinsic viscosity of the copolymer was very low (0.09 dL/g) at 30 °C in tetrahydrofuran despite high weight‐average molecular weight (1.2 × l06 by multi‐angle laser light scattering). These results indicate that the copolymer was of hyperbranched structure. By transmission electron microscopy observation, the individual copolymer molecules were visualized as nanoparticle of 6–20 nm. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 1609–1617, 2004
Polysiloxanes with chlorobenzyl groups as precursors of new organic‐silicone materials
Authors: Kazmierski K. , Hurduc N. , Sauvet G. , Chojnowski J. 
Published: February 2004

AbstractVarious polysiloxanes bearing chlorobenzyl side groups were synthesized by the hydrolytic polycondensation of the 73:27 mol/mol mixture of [2‐(4‐chloromethylphenyl)ethyl] methyldichlorosilane and [1‐(4‐chloromethylphenyl)ethyl] methyldichlorosilane followed by the cationic equilibration or coequilibration with octamethylcyclotetrasiloxane, D4. 1,3‐Divinyltetramethyl‐disiloxane was used as the chain end blocker to obtain a vinyl–Si ended chlorobenzyl‐substituted polysiloxane. In some cases, the polymer was additionally treated with dimethylvinylchlorosilane to achieve full substitution of chain ends by the vinyl group. Cohydrolysis of the chlorobenzylic monomer mixture with dimethyldichlorosilane was also practiced. Multiblock copolymers were obtained by polyhydrosilylation of the α,ω‐divinylsilyl chlorobenzyl‐substituted polysiloxanes with α,ω‐dihydrosilyl polydimethylsiloxanes. All these polymers and copolymers containing reactive chlorobenzylic groups were demonstrated to be convenient precursors of functional polysiloxanes of potential practical use. Some specific functional groups, such as quaternary ammonium salt groups of biocidal activity or azobenzene groups making the polymer sensitive to external stimuli by light, may be readily generated on polysiloxane under mild conditions. The chlorobenzylic substituted polysiloxanes may be also used as macroinitiators of the atom transfer radical polymerization, to obtain polysiloxanes with grafted organic polymers, such as styrene, 4‐chloromethylstyrene, and n‐butylacrylate. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 1682–1692, 2004
Influence of phenylenediamine additions on the morphology and on the catalytic effect of polyaniline
Authors: Duić Ljerka , Kraljić Marijana , Grigić Sanja 
Published: February 2004

AbstractThe influence of para‐, ortho‐, and meta‐phenylenediamine (p‐, o‐, and m‐PDA) additions on the electrochemical synthesis of polyaniline has been investigated by the use of cyclic voltametry. It has been found that small additions (1 and 5 mmol L−1) of PDA monomers influence significantly the polymerization rate. Whereas p‐PDA increases the polymerization rate, the addition of o‐ or m‐PDA slows it down. Therefore, a different number of potential cycling is necessary to obtain similar thickness of layers. The layers exhibit very different morphology, which changes from “spaghetti‐like” for polyaniline to “sponge‐like” for p‐PDA, to “pebble‐like” for o‐PDA and to “cauliflower‐like” for m‐PDA additions, respectively. The catalytic effect of the synthesized polymer layers has been tested. It has been found that all the layers exhibit catalytic effect in lowering the redox potential of hydroquinone/quinone tested reaction, but the rate of the electrocatalytic reaction varies depending on the PDA monomer added. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 1599–1608, 2004
Aqueous solution properties of pH‐responsive AB diblock acrylamido–styrenic copolymers synthesized via aqueous reversible addition–fragmentation chain transfer
Authors: Sumerlin Brent S. , Lowe Andrew B. , Thomas David B. , Convertine Anthony J. , Donovan Michael S. , McCormick Charles L. 
Published: February 2004

AbstractHere we report the synthesis and solution characterization of a novel series of AB diblock copolymers with neutral, water‐soluble A blocks consisting of N,N‐dimethylacrylamide and pH‐responsive B blocks of N,N‐dimethylvinylbenzylamine. To our knowledge, this represents the first example of an acrylamido–styrenic block copolymer prepared directly in a homogeneous aqueous solution. The best blocking order [with poly(N,N‐dimethylacrylamide) as a macro‐chain‐transfer agent] yielded well‐defined block copolymers with minimal homopolymer impurities. The reversible aggregation of these block copolymers in aqueous media was studied with 1H NMR spectroscopy and dynamic light scattering. Finally, an example of core‐crosslinked micelles was demonstrated by the addition of a difunctional crosslinking agent to a micellar solution of the parent block copolymer. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 1724–1734, 2004
Poly(ethylene terephthalate) modified with aromatic bisester diamides: Thermal and oxygen barrier properties
Authors: Hibbs Michael R. , Holtzclaw Jeremy , Collard David M. , Liu Richard Y. F. , Hiltner Anne , Baer Eric , Schiraldi David A. 
Published: February 2004

AbstractThe synthesis and properties of poly(ethylene terephthalate) (PET) copolymers containing four bisester diamide structural units are reported. Two of the bisester diamides consist of three para‐substituted aromatic rings, and the other two consist of three meta‐substituted aromatic rings. The copolymers have been characterized by nuclear magnetic resonance, differential scanning calorimetry, and dilute solution viscometry. Three of the copolymers can be compression‐molded into amorphous films for oxygen barrier testing, and one of these three films can be oriented for additional barrier testing. The three amorphous films all have lower permeabilities than unoriented PET. However, this difference diminishes upon the orientation of the polymer films. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 1668–1681, 2004
Synthesis and characterization of negative‐type photosensitive hyperbranched polyimides with excellent organosolubility from an A2 + B3 monomer system
Authors: Chen Huan , Yin Jie 
Published: February 2004

AbstractA series of photosensitive hyperbranched polyimides (HB‐PIs) were prepared through facile end‐group modifications of the fully imidized polymer. A triamine, 1,3,5‐tris(4‐aminophenoxy)benzene, and a dianhydride, 4,4′‐(hexafluoroisopropylidene)diphthalic anhydride, were condensed with a dropwise addition method in a molar ratio of 1/2 to afford an anhydride‐terminated poly(amic acid) precursor, which was then end‐capped by 4‐aminophenol and chemically imidized to yield a phenol‐terminated HB‐PI. The modifications of the terminal phenol groups of the polyimide by acyl chloride compounds (acryloyl chloride, methylacryloyl chloride, and cinnamoyl chloride) gave the target polymers. The photosensitive HB‐PIs showed good thermal properties and excellent solubility even in low‐boiling‐point solvents at room temperature, such as acetone, 1,1,2‐trichloroethane, tetrahydrofuran, and chloroform. Photosensitive property studies revealed good photolithographic properties with a resolution greater than 3 μm and a sensitivity of 650–680 mJ/cm2. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 1735–1744, 2004
Pyrrole derivatives for electrochemical coating of metallic medical devices
Authors: Weiss Zehava , Mandler Daniel , Shustak Galit , Domb Abraham J. 
Published: February 2004

AbstractElectropolymerization of medical devices such as cardiovascular stents may posses advantages including a simple and reproducible process with the ability to control the thickness, adherence, and composition of the coating by the duration and intensity of the applied current, the monomer composition and concentration, the solvent, and the reaction conditions. The properties of the polymer can also be controlled by copolymerization of different monomers, grafting substituents to a functionalized polymer, and by entrapping biomolecules. This article describes the synthesis of a range of pyrrole‐based monomers and their electrocoating onto stainless steel surfaces. N‐substituted pyrrole monomers with C1–C18 alkyl chains and poly (ethylene glycol) chains were synthesized in good yields and purity. Electropolymerization of these monomers provided uniform coatings with different hydrophobicities. Studies now focus on the incorporation of drugs in the coated device for release from the surface. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 1658–1667, 2004
Reaction of oligoalcohols with diepoxides: An easy, one‐pot way to star‐shaped, multibranched polymers. II. Poly(ethylene oxide) stars—synthesis and analysis by size exclusion chromatography triple‐detection method
Authors: Lapienis Grzegorz , Penczek Stanislaw 
Published: February 2004

AbstractAn Erratum has been published for this article in Journal of Polymer Science Part A: Polymer Chemistry (2004) 42(10) 2575‐2576
Starlike, highly branched (AxByAz) macromolecules having from a few to 100 arms and molar masses up to 105 were prepared in three stages with the one‐pot, arms‐core‐arms method (By stands for y molcules of former diepoxides introduced into the core). Oligoalcohols, at least partially converted into their alcoholate counterpart states, reacted with diepoxy compounds giving star‐shaped, highly branched macromolecules. With the properly chosen conditions, complete conversion of both starting components was achieved. In this article homostars built with the first and second generation of poly(ethylene oxide) arms (Ax and Az, respectively) are described. The number of arms (f) was determined either by direct measurements of the number‐average molcular weight (Mn) of the first and second stars (Mn of arms Ax and Az is known) or by calculating f from branching indices g and g′ determined from the radius of gyration and the limited viscosity number measured with size exclusion chromatography (SEC) triple detection with TriSEC software. For a few samples, Mn was measured with high‐speed membrane osmometry. The progress of the stars' formation was monitored by 1H NMR, SEC, and matrix‐assisted laser desorption/ionization time‐of‐flight methods. Functionalization of the OH end groups in the second generation of arms was observed by 1H and/or 31P NMR. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 1576–1598, 2004
Linear polyamides from L‐malic acid and alkanediamines
Authors: Regaño Celia , Alla Abdellilah , de Ilarduya Antxon Martínez , Muñoz‐Guerra Sebastián 
Published: February 2004

AbstractA series of linear polyamides (PnMLM) derived from O‐methyl‐protected L‐malic acid and 1,n‐alkanediamines with even n values ranging from 4 to 12 were prepared and fully characterized. L‐Malic acid entered in the chain with a random orientation rendering essentially aregic polymers. PnMLM displayed optical rotation consistent with the content of the polymer in malic units, and they all were crystalline with melting points ranging from 158 to 188 °C and glass‐transition temperatures varying from 37 to 70 °C. PnMLM appeared to be fairly stable to heat with thermal decomposition starting close to 300 °C. Hydrolytic degradation of PnMLM at 37 °C was slow, but the process was significantly faster at 70 °C. Thermal degradation took place with the formation of cyclic malimides in the residual polymer and released the 1,n‐alkanediamine. However, hydrolytic degradation took place in a first stage with the formation of open chains of carboxylic‐ and amine‐ended oligomers. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 1566–1575, 2004
Radical polymerization of allylbiguanide
Authors: Iio Kokoro , Yamasaki Susumu , Tasaki Shinji , Kudoh Hisako , Matsunaga Mutsuo 
Published: February 2004

AbstractMonoallyl compounds are not readily homopolymerized by a conventional free‐radical mechanism. However, we successfully performed the radical polymerization of allylbiguanide hydrochloride in a concentrated acid solution (hydrochloric acid or phosphoric acid) in the presence of a radical initiator at 50 °C. The polymer product was precipitated from the reaction solution through the addition of an excess amount of acetone. The precipitated crude polymer [polyallylbiguanide (PAB)] was then purified by dialysis. PAB was confirmed by elemental analysis, infrared spectroscopy, and 1H NMR. The molecular weight range of PAB was 10,340–113,200, and PAB exhibited a low polydispersity (weight‐average molecular weight/number‐average molecular weight = 1.04–1.68) by multi‐angle laser light scattering. The polymerization of allylbiguanide was quite sensitive to the protonic concentration of the inorganic acid. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 1707–1711, 2004
Theoretical study of the free‐radical copolymerization of styrene with methyl methacrylate: Comparative study to the styrene–acrylonitrile monomer system
Authors: Cieplak Piotr , Kaim Andrzej 
Published: February 2004

AbstractEnthalpic and electronic terminal and penultimate unit effects in the free‐radical copolymerization of styrene (S) with methyl methacrylate (M) were investigated by quantum mechanical calculations at 0 and 298 K. Total energies, zero‐point energies scaled by a 0.96 factor, and thermal enthalpy corrections for all optimized structures were computed at the B3‐LYP/6‐31G(d) level of theory. Differences in enthalpies for elementary propagation reactions at 0 and 298 K did not exceed 0.6 kcal/mol. Enthalpic effects of the replacement of S by M in the penultimate position of the growing radicals in elementary copolymerization propagation reactions (enthalpic penultimate unit effects) were always positive, ranging from 1.2 to 3.3 kcal/mol at 298 K. The values suggested that the elementary propagation reactions involving more S units in the growing polymer chain ends should be slightly thermodynamically preferred. A comparison of these results with those for the S–acrylonitrile monomer system showed that the most crucial feature differentiating enthalpic effects for the two monomer systems is the replacement of M by acrylonitrile in the reaction pair CH3‐S‐M · + M → CH3‐S‐M‐M · and CH3‐M‐M · + M → CH3‐M‐M‐M ·. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 1557–1565, 2004
Thiol‐ene photopolymerization of polymer‐derived ceramic precursors
Authors: Cramer Neil B. , Reddy Sirish K. , Lu Hui , Cross Tsali , Raj Rishi , Bowman Christopher N. 
Published: February 2004

AbstractThe liquid, ceramic precursor monomer VL20 was copolymerized with a thiol monomer in a traditional radical thiol‐ene photopolymerization. Polymerization occurred via addition of the thiol functional group to the vinyl silazane functional group in a 1:1 ratio consistent with a step‐growth polymerization. Gelation occurred at a high conversion of functional groups (70%) consistent with an average molecular weight and functionality of 560 and 1.7, respectively, for VL20 monomers. Initiatorless photopolymerization of the thiol‐VL20 system also occurred upon irradiation at either 365 or 254 nm. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 1752–1757, 2004
Photoinduced cationic ring‐opening frontal polymerizations of oxetanes and oxiranes
Authors: Crivello J. V. , Falk B. , Zonca M. R. 
Published: February 2004

AbstractThe photoinitiated cationic ring‐opening polymerizations of certain epoxides and 3,3‐disubstituted oxetanes display the characteristics of frontal polymerizations. When irradiated with UV light, these monomers display a marked induction period, during which little conversion of the monomer to the polymer takes place. The local application of heat to an irradiated monomer sample results in polymerization that occurs as a front propagating rapidly throughout the entire reaction mass. For the characterization of these frontal polymerizations, the use of a new monitoring technique, employing optical pyrometry, has been instituted. This method provides a simple, rapid means of following these fast polymerizations and quantitatively determining their frontal velocities. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 1630–1646, 2004