Porosity variation and swelling of cation exchangers
Authors: Kolarz Bożena N. , Wieczorek Piotr P. 
Published: April 2003

AbstractPolystyrenesulfonic cation exchangers have been obtained from styrene‐divinylbenzene copolymers modified with organic solvents. The cation exchangers were characterized by varying porosity analogous to that of the parent copolymers. The porosity varied from zero to 0.45 and the specific surface area from zero to 350 m2/g; these changes were induced by drying the cation exchangers from poorly solvating solvents.The sorption degrees towards a model dye (methylene blue) from an aqueous solution reached a value up to unity and the pseudoequilibration time decreased with an increase in the sorption temperature. The sorption degrees of the dye from an acetone solution were lower and proportional to swelling of the gel in acetone.The presented results indicate that, similarly as in copolymers from which the cation exchangers were obtained, the structural changes occur on drying and they result from the surface tension of solvents, but the swollen cation exchangers have the gel structure.
Chinongruppenhaltige Polymere als Träger zur Immobilisierung von Enzymen
Authors: Manecke Georg , Beier Wilfried 
Published: April 2003

AbstractDurch die Reaktion von 3‐Amino‐4‐hydroxyphenylbenzoat mit vernetztem Poly(styrolsulfonsäurechlorid) wurde nach Verseifung und Oxidation ein chinongruppenhaltiger reaktiver Träger erhalten, dessen Eignung für Enzymimmobilisierungsreaktionen mit α‐Chymotrypsin getestet wurde. Mit dem Einführen von Ethylendiaminbzw. Hexamethylendiamin als Spacer zwischen dem Polystyrol‐Gerüst und der Chinonkomponente konnte das Enzymbindungsvermögen des Trägers und die Aktivität des immobilisierten α‐Chymotrypsins erhöht werden. Ausgehend von vernetztem Polyvinylalkohol wurde durch Umsetzung mit p‐Benzochinon ein reaktiver Träger hergestellt, an dem α‐Chymotrypsin immobilisiert werden konnte. Die Aktivität, das pH‐Optimum der Aktivität sowie die Lagerstabilität der unlöslichen α‐Chymotrypsinpräparate wurden untersucht.
Frequency dependence of dielectric loss peak temperature and determination of glass transition temperature
Authors: Gupta A. K. , Maity A. K. 
Published: April 2003

AbstractAmbiguities arising in the identification of the observed dielectric loss peak with the glass transition process are described, in the light of frequency dependence of the loss‐peak‐temperature. The usefulness of the WLF equation in solving these ambiguities is explored and illustrated with the help of data on four polymers. A simplified method is described, for evaluating the parameters, reference temperature of the WLF equation and thereby the glass transition temperature from the data at two frequencies.
Effect of irradiation conditions on the properties of grafted polyethylene
Authors: Ivanova Latinka , Boudevska Hrisanta 
Published: April 2003

AbstractGrafted samples of low‐density polyethylene were prepared by sensitizing the polyethylene with different concentrations of photosensitizer (benzophenone) and irradiation with different doses of UV‐light. These samples which differ in degree of crosslinking and in amount of active sites were grafted with methacrylic acid after different time of staying in the air after irradiation.The effect of dose of irradiation, concentration of photosensitizer and time of staying in the air after irradiation on the degree of crosslinking and graft level has been studied.Electrical resistance, pore size and tensile strength of the grafted polymers were determined.
A study on the thermal behaviour of anisole resins
Authors: Patel R. , Patel J. , Patel K. C. , Patel R. D. 
Published: April 2003

AbstractAn attempt has been made to prepare thermally stable resins from the condensation of anisole and 1,2‐dichloroethane. The anisole resin samples were subjected to the thermal study involving TG and DTA techniques. The kinetic parameters and the stability of the resins have been investigated.
Studies on graft copolymerization of methyl methacrylate onto poly(vinyl chloride)
Authors: Blumczyński Zbigniew , Skowroński Tadeusz , Łaskawski Włodzimierz 
Published: April 2003

AbstractThe grafting of methyl methacrylate on suspension‐grade poly(vinyl chloride) in the presence of lauroyl peroxide has been studied. The reaction was carried out in a water suspension of the starting PVC polymer swollen with the monomer.The influence of reaction temperature, T, starting monomer/polymer ratio, M/P, and initiator concentration, I, in the monomer on the grafting efficiency of both polymers present in the system was found to be well described by the following linear regression equations:

and
Photochemical investigations into cellulosic materials III. Photografting vinyl monomers onto cotton in the presence of various photo‐initiators
Authors: Hérold Robert , Fouassier Jean‐Pierre 
Published: April 2003

AbstractUV‐light induced grafting onto cotton is reported for a large variety of vinyl monomers. The reaction was generally initiated by free radical initiators such as phenylacetophenone derivatives, substituted benzophenone compounds, quantacure SKS, saccharides and so on. % grafting‐time conversion curves were determined. The rate of grafting was lying in the range 0.15–1.3% grafting min‐1. In some cases, the amount of homopolymer was quite low. The efficiency of the initiator is strongly dependent upon the monomer used.
Chemical transformations of polymers, XXI. Imidazole containing polymers from crosslinked macroporous poly(methacrylic acid esters) with reactive sulfoester groups
Authors: Kühn M. , Pommerening K. , Benes M. , Peska J. , Stamberg J. 
Published: April 2003

AbstractNew imidazole containing polymers were synthesized by nucleophilic substitution reactions of poly(ethylene methacrylate arylsulfonates) with imidazole, benzimidazole and some of their derivatives. The reaction time and the solvents used had varying effects on the binding rates. The conversion was best reproducible at high reaction speed in ethanol.
Zum Einfluß von Ultraschall auf die Oberflächenporosität von Polystyrol‐Enzym‐Trägern
Authors: Schmidt Peter , Fischer Jens , Rosenfeld Eike , Millner Rudolf , Häupke Klaus , Schellenberger Alfred 
Published: April 2003

AbstractDie Porosität der äußeren Partikeloberfläche von makroporösen Polystyrol‐Enzym‐Trägern ließ sich durch Ultraschallbehandlung vergrößern, ohne daß die Kugelgestalt des im Suspensionsverfahren hergestellten Polymeren signifikant verändert wurde. Die Änderungen in der Oberflächenstruktur des Polymeren wurden durch elektronenmikroskopische Aufnahmen nachgewiesen. Es wurde der Einfluß der Oberflächenporosität sowohl auf das katalytische Verhalten von immobilisierter α‐Amylase als auch auf die Proteinadsorption der funktionalisierten Polystyrole untersucht. Die Resultate zeigten, daß der Transport von Stärke und Protein in das Matrixinnere nach Ultraschallbehandlung der Polymeren begünstigt wird.
Polychelatogene zur Anreicherung und Abtrennung von Metallionen in homogener Phase mit Hilfe der Membranfiltration
Authors: Bayer Ernst , Eberhardt Hans , Geckeler Kurt 
Published: April 2003

AbstractMakromolekulare Chelatogene wurden zur Komplexierung mit verschiedenen Metallen in homogener Phase unter Anwendung der Membranfiltration synthetisiert und untersucht. Eine Anzahl von wasserlöslichen Basispolymeren, wie z. B. Poly(vinylamin), Poly(acrylsäure), Poly(ethylenimin), ihre Copolymere und Derivate wurden im Hinblick auf ihre Anwendung zur Komplexbildung von Übergangsmetallen dargestellt und untersucht.Die Molmassen der Polymere lagen zwischen 20000 und 200000 Daltons. Die Anwendung der Membranfiltration ermöglicht die Abtrennung von überschüssigen Metallionen vom Polymerkomplex in einem kontinuierlichen oder diskontinuierlichen Verfahren. Studien über die Metallbindungskapazitäten der Polymerliganden zeigten, daß es möglich ist, makromolekulare Chelatogene darzustellen, die für verschiedene Metalle selektiv sind. Danach verbesserte die Einführung von chelatogenen Gruppen, wie Iminodiessigsäure, Thioharnstoff, Pyridin‐2‐aldimin und andere, signifikant die Selektivität für die Metalle Kupfer, Nickel, Palladium, Quecksilber, Eisen, Gold und Platin.Zur Regenerierung der Polymerliganden kann die Elektrolyse oder Protolyse verwendet werden. Die makromolekularen Komplexe blieben unabhängig vom komplexierten Metall und des polymeren Chelatogens wasserlöslich. Nach diesen Studien können bestimmte Metalle selektiv aus Abwasser oder anderen verdünnten Lösungen durch die Anwendung von polymeren Chelatogenen in homogener Phase entfernt werden.
Mark‐Houwink‐Beziehung für Polytetramethylenterephthalat im Vergleich zu Polyethylen‐ und Polyhexamethylenterephthalat
Authors: Horbach A. , Binsack R. , Müller H. 
Published: April 2003

AbstractFür Polytetramethylenterephthalat wird an Fraktionen—ausgehend von der Molekulargewichtsbestimmung mit der Absolutmethode der Streulichtmessung—die Mark‐Houwink‐Beziehung für das Lösemittel Phenol/1,2‐Dichlorbenzol (1 : 1) bei 25°C ermittelt, die—wie nachgewiesen wird—auch für übliche technische Polytetramethylterephthalat‐Produkte gilt.Zum Vergleich werden die [η]‐M‐Beziehungen für Polyethylenterephthalat und Polyhexamethylenterephthalat bestimmt. Die Werte für den Exponenten der Mark‐Houwink‐Beziehung nehmen in der Reihenfolge αPET < αPTMT < αPHMT zu; d. h. die thermodynamische Güte des Lösemittels Phenol/Dichlorbenzol nimmt mit steigender Anzahl an Methylengruppen der Diolkomponente zu.Aus den an den Fraktionen durchgeführten Viskositäts‐ und Molekulargewichtsmessungen werden die “ungestörten” Knäueldimensionen von Polytetramethylenterephthalat nach Stockmayer‐Fixman berechnet, die früher gefundene Werte bestätigen. Der für Polytetramethylenterephthalat ermittelte Behinderungsparameter zeigt, daß innerhalb der Polyalkylenterephthalatreihe Estergruppen die Polymerkette flexibilisieren, was auch für Polyester aus aliphatischen Dicarbonsäuren und aliphatischen Diolen bekannt ist.
Fällungspolymerisation von Acrylnitril in Aliphatischen Kohlenwasserstoffen. Kinetische und mechanistische Aspekte bei Verwendung des Startersystems tert.‐Butylhydroperoxid/Schwefeldioxid/Trichloressigsäure
Authors: Korte Siegfried , Neukam Theo , Süling Carlhans 
Published: April 2003

AbstractDie Fällungspolymerisation von Acrylnitril in aliphatischen Kohlenwasserstoffen steht in inherm kinetischen Erscheinungsbild der Acrylnitril‐Massepolymerisation nahe. Dies gilt insbesondere für den Bereich niedriger Umsätze (<50%). In diesem Zusammenhang werden Ergebnisse diskutiert, die bei der einstufigen kontinuierlichen Polymerisation unter Einstellung kurzer Verweilzeiten erhalten wurden.Das eingesetzte Redoxstartersystem, bestehend aus tert.‐Butylhydroperoxid/Schwefeldioxid/Trichloressigsäure, führt zu charakteristischen Besonderheiten im chemischen Aufbau der Acrylnitril‐Polymeren. In einer parallel zur Polymerisation ablaufenden Umsetzung der Redoxkomponenten mit Acrylnitril entsteht N‐tert.‐Butylacrylamid, das als Struktureelement in die wachsende Polymerkette eingebaut werden kann. Das Initiatorsystem bewirkt weiterhin, daß die anfallenden Polymeren durch spezifische Start‐ und Abbruchreaktionen einen vergleichsweise hohen Gehalt and polymerfixiertem Schwefel, vorwiegend in Form von Sulfonatgruppen, aufweisen und durch Hydrolyse eine relative hohe Konzentration an Carboxylgruppen besitzen.
Neuere wäßrige PUR‐Systeme
Authors: Dieterich Dieter 
Published: April 2003

AbstractNach einer kurzen systematischen Übersicht der Ergebnisse von Umsetzungen verschiedenartiger NCO‐Präpolymerer mit Wasser werden eine Reihe neuer Methoden zur Herstellung wäßriger Dispersionen ionischer und nichtionischer Polyurethane besprochen. Hierzu zählen: Weiterentwicklung des Aceton‐ und des Schmelzidisperigierverfahrens, elektrolyt‐ und foroststabile Dispersionen, die Direkt‐Dispergierung fester Polyurethane, das Ketimin‐ und das Ketazin‐Verfahren. Die bei der „Fällungsdispergierung”︁ nach dem Acetonverfahren ablaufenden Vorgänge werden diskutiert.An neuen Produkten sind hochwertige Beschichtungsmittel für Textiliken, Leder und Weisch‐PVC sowie Spezial‐Klebstoffe zu nennen. Neu erschlossene Einsatzgebiete für PUR‐Dispersionen sind die Beschlichtung von Glasfasern sowie kationische Elektrotauchlacke. Auch für Emulsionen von Polyisocyanaten und NCO‐Präpolymeren sowie für wäßrige PUR‐Lösungen sind Einsatzgebiete erschlossen worcden. Andere wäßrige Systeme sind Mikrokapsel‐Suspensionen, Stützverbände sowie hydrophile Schaumstoffe. Aus W/O‐Emulsionen, die in der wäßrigen Phase anorganische Stoffe dispergieren oder gelöst enthalten, lassen sich interessante Hartschaumstoffe herstellen.
The synthesis of blockcopolymers by radical polymerization
Authors: Oppenheimer Christiane , Heitz Walter 
Published: April 2003

AbstractPolyazoesters are prepared by reacting azoisobutyronitrile with diols. They can be used to prepare blockcopolymers by radical polymerization in a two step procedure. In the first step the polyazo compound is partially decomposed in presence of a monomer to prepared an azogroup‐containing prepolymer. Decomposition of the remaining azogroups in presence of a second monomer result in blockcopolymers containing fractions of homopolymers. Solution and precipitation polymerization are suitable techniques in both steps. The efficiency of the azogroups in the prepolymer is about 0.3. Styrene/methyl methyl methacrylate‐blockcopolymers were obtained in this way. The fraction of blockcopolymers were 60% in solution polymerization and 80% in precipitation polymerization, respectively. Due to termination by disproportionation of methyl methacrylate the blockcopolymer consist mainly of styrene/methyl methacrylate and methyl methacrylate/styrene/methyl methacrylate‐blockcopolymers.
Die basenkatalysierte Isocyanat‐Amin‐Reaktion
Authors: Kleimann Helmunt 
Published: April 2003

AbstractIn einem Integralschaumstoff‐System auf Basis von Polyharnstoffen werden unterschiedlich basische Aktivatoren auf ihre katalytische Wirkung hin untersucht. Die Diskussion der Ergebnisse ergibt, daß Aktivatoren, die zur Protonenübertragung besonders befähigt sind, gute katalytische Wirksamkeit aufweisen. Die Weiterreaktion der Harnstoffgruppe zum Biuret wird durch stark basische Aktivatoren, schwach basische Amine und schnell reagierende Isocyanate begünstigt.
Bistetraphenylethylenorthosilikat als Initiator für radikalische Polymerisationen
Authors: Braun Dietrich , Rengel Reinhard 
Published: April 2003

AbstractBistetraphenylethylenorthosilikat (I) wurde auf seine Initiatoreigenschaften bei der Polymerisation von Methylmethacrylat und Styrol untersucht. Aus der Abhängigkeit der Bruttogeschwindigkeit der Polymerisation von Initiator‐ und Monomerkonzentration muß auf einen beträchtlichen Primärradikalabbruch geschlossen werden. Die holen Molekulargewichte der erhaltenen Polymeren, die relativ hohe Grenzviskosität und die Erniedrigung der Molekulargewichte nach der Hydrolyse der SiOC‐Bindung in den Polymeren lassen schließen, daß (I) durch Spaltung beider CC‐Bindungen Polymerketten starten und abbrechen kann, so daß kurzkettenverzweigte, relativ starre Makromoleküle entstehen. Die Brauchbarkeit von (I) als Hochtemperaturhärter von ungesättigten Polyester‐Harzen wurde durch Vergleich mit Benzpinakol gezeigt.
Einfluß von Carboxymethylcellulose auf das Verhalten von Tonsuspensionen unter besonderer Berücksichtigung des Tiefbohrsektors
Authors: Schriewer Bernd , Mross Wolfgang 
Published: April 2003

AbstractTiefbohrspülungen haben die Aufgabe, das erbohrte Bohrklein auszutragen, die Bohrlochwand zu stützen, den Bohrmeißel zu kühlen und das hydrostatische Gleichgewicht gegen den Formationsdruck aufzubauen.Die für diese Zwecke bevorzugt eingesetzten Tonsuspensionen besitzen Fileßgrenze und Gelstärke, haben aber eine ungenügende Wasserbindung. Durch Carboxymethylcellulose wird die Dispergierung des Tones in H2O und das Wasserrückhaltevermögen der Tonsuspensionen verbessert.Die vorliegende Arbeit untersucht den Einfluß von Carboxymethylcellulose auf die Rheologie und das Wasserrückhaltevermögen von salzfreien und NaCl‐gesättigten Tonsuspensionen in Wasser.
Synthesis and study of poly[3,5‐(1‐carboxy‐2‐hydroxy phenylene) ethylene]
Authors: Patel M. N. , Patel J. B. 
Published: April 2003

AbstractPoly[3,5‐(1‐carboxy‐2‐hydroxy phenylene) ethylene] was prepared by Friedel‐Crafts condensation of salicylic acid (SA) with 1,2‐dichloro ethane (DCE) in presence of anhydrous aluminium chloride. The polymers were prepared varying the catalyst proportion, also in presence of nitrobenzene and tetrachloro ethane. The polymeric samples were characterized by IR and UV spectra and the molecular weights were determined by VPO and conductometric titration in pyridine. Various empirical relations were applied to correlate the viscosity data in DMF with the appropriate concentration function. TGA analysis was carried out to compare the thermal stability of the polymeric samples.
Photo‐induced graft copolymerization, I. Graft copolymerization of methyl methacrylate onto silk in presence of lutidine‐bromine charge transfer complex
Authors: Lenka Subasini , Nayak Padma L. , Mishra Munmay K. 
Published: April 2003

AbstractPhoto‐induced graft copolymerization of methyl methacrylate onto silk was investigated by using Lutidine‐Bromine (Lu‐Br2) charge transfer complex as initiator. The graft yield increased with increasing monomer concentration at the initial stages and thereafter it decreased. The graft yield increased steadily with the increase of the initiator concentration. The initiator exponent was computed to be 0.5. The reaction was carried out at three different temperatures and the overall activation energy was computed. The kinetic data and other evidences indicated that the overall polymerization took place by a radical mechanism. A suitable mechanism has been suggested.
Investigation of the effect of gamma rays on the properties of polyamide fibers, II. Radiation changes in unstabilized and stabilized fibres
Authors: Szymański W. , Rymian B. 
Published: April 2003

AbstractThe effect of γ‐radiation on polyamide fibres of PA 6, poly(ε‐caprolactam), was investigated by a viscosimetric method (unstabilized and stabilized fibres) and by the X‐ray crystal analysis (unstabilized fibres). It was found that stabilizers practically had no effect on the crosslinking and degradation processes occurring in an oxygenfree and oxygen atmosphere, respectively. The study of the degree of crystallinity and of the size of the crystallites showed that the radiation stability of the investigated fibre was relatively high.
Mechanisms of degradation of cotton and effects of mercerization‐stretching upon the course of these mechanisms, III. Heat treatments
Authors: Hebeish A. , Abou‐Zeid N. Y. , Shalaby S. E. , El‐Aref A. T. , Waly A. , Abdel‐Thalouth I. , Tawfik M. 
Published: April 2003

AbstractChanges in the physical as well as chemical structure of scoured and slack mercerized restretched (90–103% of original length) cotton yarns brought about by heat treatments and the effects of these on the strength properties of the cotton yarn were investigated. No striking changes in copper number, carboxyl content, iodine sorption, degree of polymerization (P) and strength properties were observed when the scoured and the mercerized yarns were heated at 160, 180, 200, and 210°C for up to 10 min. On the contrary, with the exception of carboxyl content, marked changes in these properties were determined when heat treatment was carried out for up to 96 h and 5 h at 160°C and 210°C, respectively. However, the mercerized yarns retained higher strengths in spite of higher degradation as compared to scoured yarn. The interrelationship between strength and P as well as strength and percentage of bonds broken together with measurements of frequency of successive regions of high lateral order indicated that mercerized cotton exhibited a more uniform structure which improved the distribution of stress along the fibre.
Synthesis and characterization of poly(keto‐amines). 2. Self‐polycondensation of 4‐methyl‐3‐aminophenacyl chloride and 2‐methyl‐4‐aminophenacyl chloride
Authors: Patel Hasmukh S. , Patel Raman N. , Patel Shanti R. 
Published: April 2003

AbstractPoly(keto‐amines) such as poly(4‐methyl‐3‐iminophenacyls) and poly(2‐methyl‐4‐iminophenacyls) were prepared by self‐polycondensation of 4‐methyl‐3‐aminophenacyl chloride and 2‐methyl‐4‐aminophenacyl chloride under different experimental conditions. All the polymer samples were insoluble in common organic solvents. They were characterized by elemental analysis, IR spectral studies, estimation of M̄n by non‐aqueous conductometric titration and study of thermal properties by DTA. The properties of P4M3IP and P2M4IP were compared with those of poly(4‐iminophenacyls).
A new method to control the polyesterification process. Prospects of application in the production plants
Authors: Pomakis I. , Simitzis I. 
Published: April 2003

AbstractThe progress of the polycondensation reaction in a simple system of a diol and a dibasic acid without another acid as catalayst was studied by determining the Acid Number (AN) on one hand and the amount of the produced water on the other.The system was submitted to different, suitable isothermal and non isothermal heating programs, that lead to the formation of a polyester with Acid Number AN = 40. In general this value constitutes the basis of a technological application of polyester.Then the kinetics of the polyesterification was studied, a mathematical calculation was deduced from the experimental results of AN as well as of the produced water. Two fundamental equations were expressed for both kinds of measurements: an empirical equation and a theoretical one, which contain the kinetic constants of polycondensation as parameters, e.g. activation energy, etc., and which were determined from the above‐mentioned kinetical study of the reaction. Further, the determination of the parameters for the theoretical as well as for the empirical equation was done at different ranges taking into consideration the time from the beginning of heating.From the mathematical model which is based on the measurements of produced water, it is possible to follow continuously the process of polyesterification, contrary to the discontinuous determination of the AN.In addition measurements of the viscosity during the progress of polyesterification may be done in the future, with the aim to contribute to the mathematical model for an effective reaction observation and control of the quality of polycondensates.
Pyro‐feldionenmassenspektrometrische Untersuchungen an unvulkanisierten und vulkanisierten Kautschuken mit Kmponenten geringer Konzentration (Comonomere, Beschleuniger, Metalloxide, Antioxidantien)
Authors: Czybulka G. , Dunker H. , Düssel H.‐J. , Logemann H. , Hummel D. O. 
Published: April 2003

AbstractBuna CB 11 (Poly‐cis‐butenylen), Naturkautschuk SMR‐5 und Natsyn 2200 (Poly (2‐methyl‐cis‐butenylen)), Baypren 210 und Baypren 710 (Poly‐2‐chlorbutenylen), Buna Hüls 1502 (Butadien‐Styrol‐Copolymeres) und Perbunan N 2807 (Butadien‐Acrylnitril‐Copolymeres) wurden in unvulkanisiertem und vulkanisiertem Zustand pyro‐feldionenmassenspektrometrisch untersucht. Der thermische Abbau wurde in Abhängigkeit von der maximalen Pyrolystemperatur (773 K bis 1173 K) studiert. Aus der Zusammensetzung der primären Kettenbruchstücke wurden Abbaumechanismen hergeleitet und Copolymerenanteile identifiziert.Es wurden Beschleuniger verschiedener chemischer Struktur (Guanidine, Thioharnstoffe, Thiurame, Dithiocarbamate, Thiazole und Sulfenamide) im Hochtemperatureinlaßteil eines Massenspektrometers mit kombinierter Elektronenstoß‐/Feldionisationsquelle bei 563 K und 873 K pyrolysiert. Eingehend diskutiert wird das Abbauverhalten von zwei Beschleuingern (Tetraethylthiuramdisulfid und Benzothiazyl‐2‐cyclohexylsulfenamid). Hierfür wurden Abbauschemata aufegestellt.„Standard‐Vulkanisate”︁ aus Kautschukbasis, Ruß Corax A (N 555), Schwefel und Benzothiazyl‐2‐cyclohexylsulfenamid (Vulkacit CZ), jeweils im Massenverhältnis 100:40:2:0,6, zeigten in ihrem Hochvakuum‐Pyrolysat (MS) typische Fragmente des Vulkanisationsbeschleunigers sowie Reaktionsprodukte des Schwefels mit dem Kautschuk.