Cyclopolymerization. XXI. Radical cyclopolymerization of n,n‐diallylmethacrylamide
Authors: Kodaira Toshiyuki , Liu Quing‐Quing , Urushisaki Michio 
Published: April 2003

AbstractN,N‐Diallylmethacrylamide (DAMA) was synthesized and its radical cyclopolymerizability was investigated. Polymerizations of DAMA were found to proceed according to the standard kinetic equation for radical polymerization except for the diffusion controlled termination reactions owing to higher viscosity of DAMA, in spite of the fact that it contains two allyl groups. DAMA yields polymers with slightly higher degree of cyclization than 50% in dilute solution polymerization. With increasing monomer concentration, the degree of cyclization decreases gradually and it becomes slightly lower value than 50% in concentrated solution polymerizations. It was found that about 86% of pendant unsaturations is allyl group and the rest is methacryloyl group. Structural studies on repeating units showed that possibility for the presence of bicyclic structures (those formed with consumption of three double bonds involved in DAMA) and structural units with two pendant unsaturations (those formed with one double bond in DAMA participated in polymerization) is extremely small. Main repeating cyclic unit was assigned to five‐membered monocyclic lactam with an allyl group on its nitrogen, the content of which is estimated to be approximately 86% based on the allyl content. The main fraction of the rest of repeating cyclic structures was attributed to monocyclic pirolidine ring with a methacryloyl group on its nitrogen. These structural investigations and ESR studies of DAMA revealed that the methacryloyl group of DAMA is less reactive than its allyl group as in the case of N‐methyl‐N‐allylmethacrylamide which has already been reported. © 1995 John Wiley & Sons, Inc.
Diene‐functional macromonomers by a single‐step free radical addition–fragmentation reaction. Syntheses and kinetics
Authors: Reghunadhan Nair C. P. , Chaumont P. , Charmot D. 
Published: April 2003

AbstractA new chain transfer agent, 5‐tert‐butylthio‐1,3‐pentadiene (TBPD or 7, 7‐dimethyl‐6‐thia‐1,3‐octadiene) was used in the free radical polymerization of methyl methacrylate and styrene to produce conjugated diene‐end capped macromonomers by a free radical addition–fragmentation mechanism. The chain transfer was found to be degradative. A new kinetic model was proposed to describe the retarded polymerization. The kinetic parameters per‐taining to transfer, reinitiation, primary radical termination, and mutual termination of the primary radicals were evaluated at different temperatures permitting precise theoretical prediction of the functionalities. The chain transfer constants, calculated using a modified Mayo's equation revealed better transfer properties for MMA. The macromonomers were synthesized by high conversion polymerization. Characterizations of the macromonomers revealed that copolymerization predominated over the fragmentation following 1,4‐addition, although the former reaction is not detrimental for the chain‐end functionalization. © 1995 John Wiley & Sons, Inc.
Heterogeneity of molecular targets on clonal cancer lines derived from a novel hormone‐refractory prostate cancer tumor system
Authors: Freedland Stephen J. , Pantuck Allan J. , Paik Sun H. , Zisman Amnon , Graeber Thomas G. , Eisenberg David , McBride William H. , Nguyen David , Tso Cho‐Lea , Belldegrun Arie S. 
Published: April 2003

AbstractOBJECTIVEWe recently described a new hormone refractory prostate cancer cell line, CL1, derived from LNCaP via in vitro androgen deprivation. To study gene expression during prostate cancer progression and to identify molecular targets for therapy, a pure clonal tumor system was generated.METHODSLimiting dilution of CL1 stably transfected with a green fluorescent protein, generated 35 single‐cell clones, which were expanded into stable cell lines. In vitro responses to various therapeutic modalities were assessed in each clone. Gene expression was determined using reverse transcriptase‐polymerase chain reaction and oligonucleotide microarrays. In vivo biology was assessed following orthotopic injection into intact and castrated severe combined immunodeficient mice.RESULTSIn vitro, all clones demonstrated similar resistance to traditional therapeutic efforts including chemotherapy and radiation therapy, but differential sensitivity to cell‐mediated cytotoxicity. The clones demonstrated differential gene expression relative to each other and to the parental CL1 and LNCaP cell lines. Following orthotopic injection into mice, three distinct growth patterns were observed: fast growth with widespread metastasis; slower grower with widespread metastasis; and no tumor formation. Using oligonucleotide microarrays, several genes were identified as differentially expressed between the most aggressive and the nontumorigenic clone.CONCLUSIONSWe have described a novel fluorescent‐labeled clonal hormone refractory prostate cancer tumor system that exhibited marked heterogeneity in its response to various therapeutic modalities, gene expression, and in vivo biology. Our data suggests that given the marked clonal heterogeneity, multi‐modality approaches directed against multiple molecular targets rather than single agent therapy will be necessary to adequately eradicate the entire malignant cell population. Clonal tumor lines may allow more accurate examination of molecular pathways involved in tumor progression and resistance to treatment. Prostate 55: 299–307, 2003. © 2003 Wiley‐Liss, Inc.
Dendritic cells transfected with interleukin‐12 and pulsed with tumor extract inhibit growth of murine prostatic carcinoma in vivo
Authors: Zhang Shaobo , Zeng Guangyuan , Wilkes David S. , Reed Gerry E. , McGarry Ronald C. , Eble John N. , Cheng Liang 
Published: April 2003

AbstractBACKGROUNDThe induction of anti‐tumor immune response by injection of dendritic cells loaded with specific antigen or transduced with genes encoding tumor‐specific antigens have been studied in animal models and have shown promising anti‐tumor effects. The impact of different routes of administration of dendritic cells on their anti‐tumor effects is uncertain.METHODSWe examined the effect of injection of cloned dendritic cells, which were stably transfected with IL‐12 and exposed to an extract of murine RM‐9 prostate carcinoma cell antigens on tumor growth in vivo. The cloned dendritic cells were injected intramuscularly, subcutaneously, or intraperitoneally into C57BL/6 mice. Seven days later, the mice were inoculated subcutaneously with 100,000 RM‐9 cells. The sizes of the resulting tumors were measured every 3 days.RESULTSCompared with the wild type dendritic cells, the IL‐12‐transfected dendritic cells delayed tumor engraftment by 7 days (P = 0.04), and reduced tumor growth by up to 80% (P = 0.02). Among the three routes of injection, intramuscular injection was most effective. In contrast to wild type dendritic cells, IL‐12‐transfected dendritic cells induced infiltration of mononuclear cells into the tumors, and induced apoptosis and necrosis of tumor cells. Injection of IL‐12‐transfected dendritic cells also significantly delays tumor growth in the preexisting RM‐9 tumors.CONCLUSIONSWe conclude that antigen‐exposed, IL‐12‐transfected dendritic cells have potential as an immunotherapy for prostate carcinoma. Routes of administration of dendritic cells are critical for maximal anti‐tumor effect. Prostate 55: 292–298, 2003. © 2003 Wiley‐Liss, Inc.
Nuclear matrix proteins changes in cancerous prostate tissues and their prognostic value in clinically localized prostate cancer
Authors: Boccardo Francesco , Rubagotti Alessandra , Carmignani Giorgio , Romagnoli Andrea , Nicolò Guido , Barboro Paola , Parodi Silvio , Patrone Eligio , Balbi Cecilia 
Published: April 2003

AbstractBACKGROUNDAfter the discovery that nuclear matrix (NM) directs the spatial organization of DNA transcription and replication, there has been an increasing interest in studying NM changes associated with malignant transformation and their potential usefulness in the clinical setting.METHODSHigh‐resolution two‐dimensional gel electrophoresis was used to analyze the NM proteins (NMP) of specimens of prostate cancer tissue obtained from the prostates of 75 patients undergoing retropubic prostatectomy.RESULTSNine NMP with different molecular weights and isoelectric points have been identified. They were expressed differently by prostate cancer tissues. An increasing trend toward the expression of such proteins like NMP 6–8 was evident with increasing tumor stage and dedifferentiation. NMP 6–8 were also significantly correlated with the risk of biochemical progression. However, Gleason score was the only significant discriminant in this regard in multiparametric models.CONCLUSIONSThis study confirms that prostate cancer progression is related to profound changes in NMP expression patterns. However, due to the complexity of the methods required to define these latter, the clinical relevance of NMP appears to be still limited. Prostate 55: 259–264, 2003. © 2003 Wiley‐Liss, Inc.
Transcription activation function of C/EBPα is required for induction of granulocytic differentiation
Authors: Keeshan Karen , Santilli Giorgia , Corradini Francesca , Perrotti Danilo , Calabretta Bruno 
Published: April 2003

Abstract
The CCAAT/enhancer binding protein-α (C/EBPα) is a transcription factor required for differentiation of myeloid progenitors. In addition to specific DNA binding, C/EBPα is also involved in protein-protein interactions, some of which (p21, Cdk2/Cdk4, E2F) appear to be required for inhibition of proliferation and possibly differentiation. To investigate the mechanisms of C/EBPα-induced granulocytic differentiation, we generated C/EBPα mutants reportedly defective in DNA binding, transactivation, and Cdk2/Cdk4 and E2F interaction and assessed their effects in a myeloid precursor cell line, primary bone marrow and C/EBPα knockout fetal liver precursor cells. We show here that the DNA binding–deficient Lys298Glu mutant, the E2F binding–deficient basic region mutant 2 (BRM-2) carrying the Ile294Ala and Arg297Ala substitutions, and the transactivation-deficient N-terminus truncated p30 mutant all fail to promote differentiation on ectopic expression in myeloid precursor cells. By contrast, ectopic expression of the Cdk2/Cdk4 interaction–deficient Δ177-191 mutant promotes differentiation and induces gene expression as effectively as wild-type C/EBPα. Thus, the integrity of the transactivation and DNA binding domains, but not of the Cdk2/Cdk4 interaction region, is necessary for C/EBPα-induced differentiation. Since the E2F binding–deficient BRM-2 mutant interacted with E2F-1 but failed to activate gene expression, our results lend support to the hypothesis that activation of gene transcription is the determining factor in C/EBPα-dependent differentiation.
A new sea‐floor gravimeter
Authors: Sasagawa Glenn S. , Crawford Wayne , Eiken Ola , Nooner Scott , Stenvold Torkjell , Zumberge Mark A. 
Published: April 2003

A new reservoir management application uses precise time‐lapse gravity measurements on the sea floor to detect seawater infiltration in offshore natural gas fields during production. Reservoir models for the North Sea Troll field predict gravity changes as large as 0.060 mGal within a 3–5‐year period. We have constructed and deployed a new instrument—the ROVDOG (Remotely Operated Vehicle‐deployed Deep‐Ocean Gravimeter) system—for this application. Because the measurements must be relocated accurately (within 3 cm), we required a gravimeter which could be handled by an ROV and placed atop sea‐floor benchmarks. We have built an instrument based upon the Scintrex CG‐3M land gravimeter. Motorized gimbals level the gravimeter sensor within a watertight pressure case. Precision quartz pressure gauges provide depth information. A shipboard operator remotely controls the instrument and monitors the data. The system error budget considers both instrumental and field measurement uncertainties.The instrument prototype was deployed in the North Sea during June 1998; 75 observations were made at 32 stations. The standard deviation of repeated gravity measurements was 0.026 mGal; the standard deviation of pressure‐derived heights, for repeated measurements, was 1.4 cm. A refined instrument was deployed in August 2000 in a three‐sensor configuration. Multiple sensors improved the precision by averaging more samples without incurring additional survey time. A total of 159 measurements were made at 68 stations. The standard deviation of repeated measurements was 0.019 mGal; the standard deviation of pressure‐derived heights was 0.78 cm.A ROVDOG pressure case rated to 4500 m depth has also been constructed. This system was deployed with the Alvin manned submersible in November 2000 to a depth of 2700 m.
Ein Beitrag zur Theorie der Einfrierkinetik von amorphen Polymeren
Authors: Kästner Siegfried 
Published: April 2003

AbstractIn der Theorie der Einfrierkinetik des Volumes v der amorphen Polymere tritt als maßgebende Größe die Relaxationszeit τ auf, die im einfachsten Fall nur eine Funktion der Temperatur T ist. Es gibt allerdings experimentelle Ergebnisse, die erkennen lassen, daß τ auch vom Volumen v selbst beeinflußt wird. In der Arbeit wird der Fall näher untersucht, daß τ von T und v explizit abhängig ist. Aus der Theorie des freien Volumens ist dabei sowohl eine additive als auch eine multiplikative Verknüpfung der Einflußgrößen T und v möglich, die allerdings bezüglich des Einfrierverhaltens zu praktisch gleichen Ergebnissen führen.
ESR‐Untersuchungen zur Oxydation photochemisch erzeugter Radikale in Ethylen‐Vinylacetat‐Copolymeren
Authors: Taplick Thomas , Rätzsch Manfred 
Published: April 2003

AbstractDer Einfluß von molekularem Sauerstoff auf die Reaktionen photochemisch erzeugter Radikale im Ethylen‐Vinylacetat‐Copolymerisat wird diskutiert. Die Experimente zeigen, daß das Acylradikal >CHOĊO nicht oxydierbar ist. Gleichzeitig ist festzustellen, daß die Bildungsreaktion der Acylradikale eine Konkurrenzreaktion zur Oxydation der Alkylradikale darstellt.
Investigation of local chain ordering in polyelectrolyte solutions by small‐angle X‐ray scattering
Authors: Pleštil J. , Mikeš J. , Dušek K. 
Published: April 2003

AbstractThe small‐angle X‐ray scattering method was used in the investigation of the local chain ordering in semidiluted aqueous solutions of poly(methacrylic acid) and poly(acrylic acid) as a function of the degree of neutralization. The scattering curves of all ionized samples exhibit a maximum, which is interpreted as an interference caused by scattering on parallel chain sections. The position of the maximum determines the Bragg distance, which is used in calculating the degree of ordering. The results are in qualitative agreement with the theory of cylindrical polyelectrolytes.
Beitrag zur Untersuchung der Trennung von Homopolymer‐ und Copolymergemischen mittels Phasentrennungsmethoden
Authors: Stejskal Jaroslav , Kratochvíl Pavel 
Published: April 2003

AbstractAus der Untersuchung des Verhaltens von einigen chemisch heterogenen Modellsystemen rnit diskreten Verteilungen der chemischen Zusammensetzung (Homopolymergemische von Polystyrol und Poly(2‐methoxyethylmethacrylat) und Gemischen ihrer statistischen Copolymere) bei der Phasentrennung in verschiedenen Losungsmittelsystemen ergab sich folgendes : (a) Die Trennung solcher Systeme lediglich nach der chemischen Zusammensetzung (ungeachtet der rel. Molekulmasse) ist im Prinzip moglich, wenn sich die einzelnen Systemkomponenten in ihrem Loslichkeits‐verhalten voneinander genugend unterscheiden; (b) Die Trennung ausschließlich nach der rel. Molekulmasse ist sehr schwierig und kann nur in Einzelfallen verwirklicht werden. Der Fraktionierungsverlauf hangt im allgemeinen immer von der chemischen Natur der Komponenten des zu trennenden Gemisches ab.
Untersuchungen zur Übertragungsreaktion zum Polymer bei der Copolymerisation von Trioxan und 1,3‐Dioxolan. III. Zur Umverteilung der Struktureinheiten Oxymethylen und Oxyethylen bei der Reaktion zwischen Trioxan und Polydioxolan
Authors: Opitz Georg , Sommer Holm , Weidlich Brigitte 
Published: April 2003

AbstractDie durch BF3‐Etherat ausgelöste Reaktion zwischen Trioxan und Polydioxolan führt zum Einbau von Oxymethylen in die tote Polymerkette. Von theoretischen Überlegungen zum Spaltungsmechanismus ausgehend, wird die Zeitabhängigkeit der Ausbildung der Mikrostruktur behandelt. Möglichkeiten des Ablaufes der Umverteilung über Kettensegmente und Monomere werden miteinander verglichen. Die kinetische bzw. thermodynamische Kontrolle wird diskutiert. Aus den Aktivierungsparametern wird auf einen SN1‐Mechanismus geschlossen.
Anwendung der Inkrementenmethode UNIFAC auf konzentrierte Polymerlösungen
Authors: Rätzsch Margit T. , Glindemann Dietmar 
Published: April 2003

AbstractDie Anwendbarkeit des UNIFAC‐Modells auf konzentrierte Polymerlösungen wird untersucht. Es ergeben sich relativ große Abweichungen von den experimentellen Werten, die durch die Berücksichtigung von „free volume”︁‐Beiträgen verringert werden können. Die Notwendigkeit der Berücksichtigung solcher Beiträge wird theoretisch begründet.
Vergleichende Untersuchungen an Polymeren mit Tetraphenylmethan‐Struktureinheiten in der Kette
Authors: Rafler G. , Reinisch G. , Minh Le Quoc , Schaaf E. , Vinogradova S. V. , Tur D. R. 
Published: April 2003

AbstractFür eine Reihe durch Lösungspolykondensation hergestellte aromatische Heterokettenpolymere mit Tetraphenylmethaneinheiten wurden Löslichkeit und thermische Eigenschaften bestimmt. Für Poly(tetraphenylmethan‐carbonat), ‐(‐terephthalat) und ‐(‐terephthalamid) sowie ‐(‐isophthalamid) waren die Temperaturen des beginnenden Masseverlustes in Luft nur wenig im Bereich von 350 bis 375°C verschieden. Für Poly(tetraphenylmethan‐pyromellitimid) wurden 465°C ermittelt. Die Erweichungstemperaturen der synthetisierten Polymere weisen demgegenüber größere Differenzierungen in Abhängigkeit von der chemischen Struktur auf.
Untersuchungen über Poly(arylenvinylen)e. 21. Mitteilung. Synthese von Poly(arylen‐1,2‐diphenylvinylen)en durch Dehalogenierungspolykondensation von Bis(α,α‐dichlorbenzyl)aromaten
Authors: Hörhold H.‐H. , Raabe D. 
Published: April 2003

AbstractHochmolekulare, lösliche Poly(arylen‐1,2‐diphenylvinylen)e mit 1,3‐Phenylen‐, 4,4′‐Diphenyl‐, 4,4′‐Diphenylether‐ und 4,4′‐Diphenylsulfid‐Gliedern in der Hauptkette werden durch Dehalogenierungspolykondensation von Bis(α,α‐dichlorbenzyl)aromaten mit Chrom(II)acetat dargestellt. Die Polykondensate zeigen eine hohe Thermostabilität. Poly(4,4′‐diphenylen‐1,2‐diphenylvinylen) ist ein hervorragender Photoleiter, der transparente Filme bildet. Sein Photoleitfähigkeitsspektrum und die sensibilisierende Wirkung von 1,4‐Bis (β‐cyanostyryl)benzol und Delor auf die Photoleitfähigkeit werden mitgeteilt. Ein neues, einfaches Verfahren zur Synthese von Bis (α,α‐dichlorbenzyl)aromaten wird beschrieben, das in einer zweifachen Friedel‐Crafts‐Reaktion von α,α,α‐Trichlormethyl‐benzol mit mehrkernigen oder aktivierten Aromaten (z. B. Diphenyl, Diphenylether, Hydrochinondimethylether) besteht. Verschiedene Synthesewege für Bis(α,α‐dichlorbenzyl)aromaten werden erörtert.
Anisotropie dynamischer Elastizitätskonstanten von Chemiefasern und Folien
Authors: Nosov M. P. , Rysjuk B. D. 
Published: April 2003

AbstractDie Anisotropie von Elastizitätskonstanten einer Reihe Chemiefasern und Folien wurde mit akustischen Methoden in Abhängigkeit von den Strukturparametern und der Molekülorientierung untersucht. Es wurden vier Diagrammtypen der elastischen Anisotropie gefungen, die von der unterschiedlichen chemischen Natur und von den strukturellen Besonderheiten des Polymers verursacht werden. Die Anisotropie des dynamischen E‐Moduls wird eindeutig von der Anisotropie des Kennwertes der mittleren Molekülorientierung bestimmt. Die Anisotropie des dynamischen Schermoduls und des Poisson‐Koeffizienten wurde berechnet. Der Schermodul besitzt drei Symmetrieachsen und ist durch ein Maximum in diagonaler Richtung gekennzeichnet. Der Anisotropiecharakter des POISSON‐Koeffizienten ist für Polymere unterschiedlicher chemischer Natur verschieden.
Thermoanalytische Untersuchungen zum thermooxidativen Verhalten und zur Stabilisierbarkeit von Blockcopolyetherestern
Authors: Zimmermann H. , Dietrich K. 
Published: April 2003

AbstractDie thermooxidative Stabilität von Blockcopolyetherestern des Ethylen‐bzw. Butylenterphthalates mit Polyethylenoxiddiol mit und ohne Zusatz von Antioxidantien wurde durch DTA und TG unter anisothermen und isothermen Bedingungen untersucht. Die Unterschiede in der Temperatur des Beginns und in der Intensität eines exothermen Enthalpieeffektes sowie der unterschiedliche Masseverlust ermöglichen eine Beurteilung der Stabilisatorwirksamkeit. Vergleichende Untersuchungen zur Dauerwärmebeständigkeit ergaben für die Festigkeitsabnahme von Formkörpern und die Induktionsperiode bei thermoanalytischen Messungen übereinstimmende Werte.
Isocyanatreaktionen und Katalyse in der Polyurethanchemie. Fortschrittsbericht
Authors: Thiele L. 
Published: April 2003

AbstractEs wird ein vergleichender Überblick über die Isocyanatreaktionen der Polyurethanchemie gegeben. Über gesicherte Theorien der Reaktionen einfach gebauter Carbonylverbindungen und Reaktivitätsvergleiche werden die speziellen Carbonylreaktionen der Isocyanate homogen mit den Vorstellungen über die Reaktionen ihrer Stoffklasse verknüpft. Vervollständigt wird diese Abhandlung durch Betrachtung der Abbaureaktionen der Umsetzungsprodukte der Isocyanate und durch praktische Aspekte der Katalyse.
Zum Abbau von Polytetrafluorethylen durch energiereiche Strahlung in Gegenwart von Sauerstoff
Authors: Ferse A. , Lunkwitz K. , Grimm H. , Dietrich P. , Engler G. , Gross U. , Prescher D. , Schulze J. 
Published: April 2003

AbstractDer Abbau von Polytetrafluorethylen durch Einwirkung von beschleunigten Elektronen in Sauerstoff wurde untersucht. Aus den strahlenchemisch zunächst gebildeten Radikalen entsteht ein Gemisch von Perfluoralkansäurefluoriden und Perfluoralkanen unterschiedlicher Kohlenstoffkettenlänge neben 40 bis 60% COF2 und wenig Perfluoralkenen. Nach Hydrolyse sind etwa 15 bis 18% der Reaktionsprodukte als Perfluoralkansäuren gewinnbar; zwei Drittel davon gehören dem Kettenlängenbereich C6 bis C14 an. Mit Verringerung des O2‐Angebots sinkt die COF2‐Bildung bei steigender Ausbeute an Perfluoralkenen.
Eine Möglichkeit zur Verbesserung der antielektrostatischen Eigenschaften von Polycaproamidfasern
Authors: Dimov K. , Garvanska R. , Pavlov P. , Simeonov N. 
Published: April 2003

AbstractDie antielektrostatischen Eigenschaften von Polycaproamidfasern werden durch die Pfropfcopolymerisation von Vinylsulfonat und Acrylnitril wesentlich verbessert, ohne daß die mechanischen Kennwerte der Fasern beeinträchtigt werden. Ein Verfahren zur Durchführung der Pfropfcopolymerisation wird beschrieben. Die Ergebnisse einer Untersuchung zur Feststellung optimaler Prozeßparameter werden mitgeteilt.
Untersuchungen zum Reckprozeß synthetischer Faserstoffe, speziell von Polyamidseide. Teil I: Kriechversuche zur Aufstellung eines Modells für das Deformationsverhalten des Fadens
Authors: Dittmann H. 
Published: April 2003

AbstractEs wird cin Modell vorgestellt, mit dem das Kriechverhalten von ungereckter und teilgereckter Polyamid‐6‐Seide approximiert wird. Anhand der Modellparameter wird der Deformationsprozeß der Fäden unter dem Gesichtspunkt diskutiert, daß der Kriechversuch zur Nachbildung des Reckprozesses geeignet ist.
Über die Feinstruktur der Polyamide. XIX. Einfluß von niedermolekularen Bestandteilen auf das Kristallisationsverhalten von Polyamid‐6
Authors: Weigel P. , Lengyel M. , Schulz E. , Szekely T. 
Published: April 2003

AbstractDer Beitrag geht von früheren Untersuchungen zu Gedächtniserscheinungen bei Polyamid‐6 aus. An Proben mit unterschiedlicher Ausgangsstruktur wird der Einfluß der niedermolekularen Anteile auf das Kristallisationsverhalten mittels DSC, Röntgenweitwinkelstreuung und Elektronenmikroskopie nachgewiesen.