bluuebunny/crossref_metadata_2025_split huggingface dataset:
Cold alkali refining of nitric acid pulps from Egyptian bagasse
Authors: Abou‐State M. A. , Helmy S. A. , El‐Megeid F. F. Abd , El‐Sherbini A. M. 
Published: April 2003

AbstractA low‐alpha and a high‐alpha dissolving pulp prepared from Egyptian bagasse by the nitric acid process were subjected to cold sodium hydroxide refining and the resulting changes in their chemical and physical characteristics were investigated. All alkali refined samples of the low‐alpha pulp showed lower chemical reactivity than the starting pulp. In case of the high‐alpha pulp refining with lower alkali concentrations impaired its chemical reactivity, while refining with higher concentrations resulted in better reactivity than the starting pulp.
ESR‐untersuchungen an γ‐bestrahltem polymethylmethacrylat und an einem copolymerisat mit methacrylsäure
Authors: Wünsche P. , Pfeiffer K. , Lorkowski H.‐J. , Reinhardt J. 
Published: April 2003

AbstractDer Einfluß von Temperung und Sauerstoff auf die Radikalreaktionen in γ‐bestrahlten Copolymeren aus Methacrylsäuremethylester und Methacrylsäure werden im Vergleich zu denjenigen in Polymethylmethacrylat ausgehend von ESR‐Messungen diskutiert.
Mechanismen der plastischen deformation in kautschukmodifizierten schlagzähen polymeren
Authors: Michler G. H. 
Published: April 2003

AbstractFür schlagzähe Polystyrene und ABS‐Polymere werden die in der Literatur vorhandenen Modelle zur Erklärung der verbesserten Zähigkeit kritisch betrachtet. Auf der Grundlage der Ergebnisse einer direkten Untersuchung der Mikroprozesse von Deformation und Bruch an dünnen Dehnproben in einem Höchstspannungs‐Elektronenmikroskop wird die Vielfach‐Craze‐Bildung (nach Bucknall) bestätigt und ein Dreistufen‐Mechanismus (Craze‐Initiierung, Crazeband‐Bildung, Rißwachstumsbehinderung) dargelegt. Seine Anwendbarkeit auf weitere schlagzähe Polymere aus Hartpolymermatrix und disperser Kautschukphase (SAN/CPE, SAN/EVA, PS/EPT) wird gezeigt. Abweichend von der Struktur der Crazes existieren Mikroscherbänder (in SAN), auf deren Bildung eingegangen wird.
Der extrem langsame Prozeß der physikalischen Relaxation in vernetzten Elastomeren
Authors: Bartenev G. M. , Revjakin B. I. , Ljalina N. M. 
Published: April 2003

AbstractDer in früheren Arbeiten gefundene δ1‐Relaxationsprozeß wird nur in vernetzten Elastomeren beobachtet. Obwohl sein Auftreten mit der chemischen Vernetzung des Polymers korreliert, gehört er nicht zur Gruppe der chemischen Relaxationsprozesse. Es wird angenommen, daß der δ1‐Prozeß mit einer kooperativen Umlagerung stark vernetzter Mikrogebiete in Netzwerkpolymeren verbunden ist. Er verläuft langsamer als andere physikalische Relaxations prozesse.
100 Jahre Celluloseregeneratfaserstoffe – Geschichte und Perspektiven
Authors: Klare H. 
Published: April 2003

AbstractDie historische Entwicklung der Celluloseregeneratfasern wird beschrieben, wobei ökonomische Aspekte sowie die gleichzetig entstandenen Kenntnisse über die Polymer‐ und Faserstruktur besondere Beachtung finden. Ausgehend von der Anpassungsfähigkeit der Celluloseregeneratfasern und der sich abzeichnenden völlig neuen Herstellungsverfahren wird auf die noch vorhandene und zunehmende Bedeutung der Cellulose als Rohstoff hingewiesen.
Synthese und Polymerisation von Amidincarbonsäuren
Authors: Adler H.‐J. , Gehrke K. 
Published: April 2003

AbstractSemicyclische Amidincarbonsäuren wurden in reiner Form synthetisiert und deren Polymerisationsverhalten oberhalb ihrer Schmelzpunkte studiert. Zwei homologe Reihen N‐(1‐Azacyclohexen‐1‐yl‐2)‐ω‐aminosäuren (Valeroamidinsäuren) und N‐(Azacyclohepten‐1‐yl‐2)‐ω‐aminosäuren (Caproamidinsäuren) wurden untersucht.
Polysiloxane. 1. GPC‐Kalibrierung für lineare Diethoxypolydimethylsiloxane bei unbekannter Viskositäts‐Molmasse‐Beziehung
Authors: Schimmel K.‐H. , Schröder E. , Chiang C. 
Published: April 2003

AbstractEs wird eine Methode zur Kalibrierung der GPC für lineare Polydimethylsiloxane beschrieben, die auf der Universalgleichung nach Benoit beruht. Die Konstanten ap und Kp der KUHN‐MARK‐HOUWINK‐Beziehung werden aus dem Vergleich der Grenzviskositäten mit den Elutionskurven der Polysiloxane unter Verwendung der Polystyrenkalibrierkurve ermittelt.
Investigation of the hydrodynamic properties of chitosan solutions
Authors: Gamzazade A. I. , Šlimak V. M. , Skljar A. M. , Štykova E. V. , Pavlova S. ‐S. A. , Rogožin S. V. 
Published: April 2003

AbstractThe hydrodynamic properties of solutions of polymer‐homologous of chitosan are studied. The solvents used are 2% acetic acid with 0.2 M sodium acetate and dichloroacetic acid of equal ionic strength. The parameters of equations are determined relating the intrinsic viscosity and sedimentation coefficient to the molecular weight. The calculated conformational parameters of the polymer indicate high permeability of the macromolecular coils in the solvents used.
Zur Bestrahlung gasförmiger Perfluorcarbone. Ein Beitrag zum Mechanismus des strahlenchemischen Abbaus von Polytetrafluorethylen
Authors: Lunkwitz K. , Gross U. , Gloeckner V. 
Published: April 2003

AbstractDurch erneute Einwirkung beschleunigter Elektronen auf die gasförmigen und leicht flüchtigen Produkte des strahlenchemischen PTFE‐Abbaus vom Kettenlängenbereich C1 bis C6 in inerter Atmosphäre werden Reaktionen der Kettenverlängerung ausglöst. Die analytischen Befunde beweisen ein stärkers Auftreten kettenverzweigter Produkte. An Hand der Ergebnisse werden einige grundlegende Aspekte zum Reaktionsmechanismus des strahlenchemischen Abbaus von PTFE diskutiert.
Kalorimetrische Untersuchungen zur Photopolymerisation von (2,2‐Dimethyl‐1,3‐dioxolan‐4‐yl)methylmethacrylat
Authors: Flammersheim H.‐J. , Klemm E. 
Published: April 2003

AbstractDie Photopolymerisation von (2,2‐Dimethyl‐1,3‐dioxolan‐4‐yl)methylmethacrylat führt zu löslichen transparenten Polymern mit Dioxolanseitengruppen an der Polymerkette. Die Kinetik der Polymerisation wird mit einem Differential Scanning Calorimeter bei unterbrochener und durchgängiger Bestrahlung studiert und das Verhältnis kt/kp in Abhängigkeit vom Umsatzgrad bei 21°C und 71°C untersucht.
Determination of hydroxyl groups in polymers. Review
Authors: Boiko V. P. , Grischenko V. K. 
Published: April 2003

AbstractThe analysis of hydroxyl groups in polymers is reviewed. Recent achievements of chemical, physico‐chemical and physical methods for the determination of hydroxyl groups and their differentiation by reactivity have been examined. Particularly, infrared spectroscopy and nuclear magnetic resonance used for this determination are considered.
Studies on the kinetics of the polymerization of 2‐methyl,6‐isopropyl phenol with the complexes of manganese with substituted benzylamines
Authors: Chandra R. , Kathuria Poonam , Verma A. K. , Kumar P. 
Published: April 2003

AbstractWith managanese‐benzylamine complexes the oxidative polymerization of 2‐methyl,6‐isopropyl phenol proceeds by a mechanism resembling to that of a Michaelis‐Menten‐type reaction with the steady state being maintained during the polymerization. From the comparison of the kinetic parameters it was concluded that oxygen takes part in the recyeling step of the catalyst and promotes the catalytic action of the manganese complexes.
An analysis of structural changes in the process of thermal crystallization of poly(epichlorohydrin) by means of WAXS and microscopic methods
Authors: Zmudziński L. , Sokół M. , Turska E. 
Published: April 2003

AbstractThe thermal crystallization of isotactic poly(epichlorhydrin) was examined by means of optical microscopy and WAXS. It was found that radial spherulites were formed, their sizes depending on the crystallization temperature. At 95°C the spherulites reach their maximum size. The spherulite growth is linear and the highest growth rate occurs at 56°C.
Structural features and some physico‐chemical properties of materials prepared from non‐aqueous solutions of cellulose‐synthetic polymer blends. 2. High resolution 13C‐NMR study of cellulose‐synthetic polymer blends in the solid phase
Authors: Zhbankov R. G. , Pupko O. A. , Grinshpan D. D. , Lipmaa Ė. T. , Tėėjaėr R. Ė. , Kaputskii F. N. , Savitskaya T. A. 
Published: April 2003

AbstractBy high resolution 13C‐NMR‐spectroscopy the blends of cellulose with poly(methyl methacrylate), poly(acrylonitrile), poly(vinyl acetate), poly(vinyl alcohol), and poly(dimethyl siloxane) are investigated at different cellulose: polymer ratios.
Structural features and some physico‐chemical properties of materials prepared from non‐aqueous solutions of cellulose‐synthetic polymer blends. 3. X‐ray study of binary cellulose‐synthetic polymer films
Authors: Savitskaya T. A. , Grinshpan D. D. , Kaputskii F. N. , Vasil'ev B. V. , Kagan G. I. , Zhegalova N. N. 
Published: April 2003

AbstractBy wide‐ and small‐angle X‐ray scattering binary films prepared from non‐aqueous solutions of the blends of cellulose with poly(acrylonitrile), poly(vinyl acetate), and poly(vinyl alcohol) are shown to be two‐phase microheterogeneous systems. The structural and morphological features are determined by the difference in chemical nature of the mixed polymer components and their ratio.
Relationship between compatibility, internal stresses and stability in polymer composites. IV. Universal representation of amorphous and crystalline phases
Authors: Drǎgan Gh. 
Published: April 2003

AbstractThe formation and melting processes of ordered phases in semicrystalline and amorphous polymer composites are considered on the basis of an universal procedure. This procedure, recently established by taking into account the topoenergetic principles, involves both experimental standard conditions and new theoretical concepts for univocal determination of the behaviour of composite systems under particular experimental conditions, and represents a generalization of the Arrhenius representation used in previous papers. For a large variety of practical cases, it results that this individual behaviour (ontogeny) is defined by two affine parameters and a threshold value of the driving potential which triggers the overall transformation process.
On the transesterification of dialkyl and diaryl phosphites with some amino alcohols and synthesis of polyurethanes
Authors: Troev K. , Tashev E. , Borissov G. 
Published: April 2003

AbstractThe transesterification reaction of dialkyl and diaryl phosphites with triethanolamine, N‐methyldiethanolamine and diethanolamine was examined. The transesterification process with aminoalcohols begins at considerably lower temperatures than that with aliphatic diols. A probable mechanism of the transesterification of dialkyl and diaryl phosphites with amino alcohols is suggested. Phosphorus‐containing polyurethanes are obtained by using N,N‐diethanolaminoethyl phosphite.
Catalytic decomposition of polyolefins. II. Considerations about the composition and the structure of reaction products and the reaction mechanism on silica‐alumina cracking catalyst
Authors: Vasile C. , Onu P. , Bărboiu V. , Sabliovschi M. , Moroi G. 
Published: April 2003

AbstractThe decomposition of polyethylene and polypropylene on amorphous silica‐alumina cracking catalyst has been studied. The structure of the catalytic decomposition products was investigated by spectroscopic methods. A reaction mechanism considering particularly the secondary reactions occurring frequently on catalyst is proposed. The advantages of catalytic decomposition in polymer wastes recovery were demonstrated.
Potentialuntersuchungen an Polyvinylacetat‐Latices. III
Authors: Hergeth W.‐D. , Schmutzler K. 
Published: April 2003

AbstractDie Ausnutzung elektroviskoser Effekte zur Bestimmung der Partikelladungen bzw. ‐potentiale von Polymerdispersionen wird am Beispiel von PVAC‐Latices diskutiert. Die Ergebnisse werden mit Resultaten anderer Meßmethoden verglichen. Für das Auftreten von Partikelaggregationen im Scherfeld bei Elektrolytkonzentrationen unterhalb der kritischen Koagulationskonzentration wird eine qualitative Erklärung gegeben.
Poly(arylen‐dichlormethylene)
Authors: Raabe D. , Hörhold H.‐H. , Rafikov S. R. , Salaskin S. N. , Solotuchin M. G. , Gileva N. G. 
Published: April 2003

AbstractPoly(arylen‐dichlormethylene) sind neue reaktive, chlorhaltige Polymere, die durch Reaktion von aromatischen Polyketonen mit Phosphor(V)chlorid oder durch direkte elektrophile Substitution von Diphenylether mit Hexachlor‐p‐xylen erhalten werden. Die Verseifung der Poly(arylen‐dichlormethylene) führt zu Polyketonen, die Reaktion mit Anilin ergibt lösliche Poly(azomethine).
On the separation of C4‐hydrocarbon mixtures by oligomerization and polymerization. Part II: Use of organo‐aluminium halide‐complexes as initiators for isobutene polymerization
Authors: Sangalov Yu. A. , Yasman Yu. B. , Nelkenbaum Yu. Ya. , Minsker K. S. , Hartung H. , Heublein G. , Stadermann D. 
Published: April 2003

AbstractLEWIS acids of defined activity, i.e. organo‐aluminium halides in connection with protogenic substances, are suitable initiators for isobutene polymerization out of a B/B‐fraction. The selectivity of isobutene conversion is chiefly determined by the activity of the initiator system used. Increase of selectivity can be reached both by decreasing acid strength and reducing electrophilicity of the growing chain end by interaction with donors and increased nucleophilicity of the counter ion.
Thermo‐oxidative stability of oriented polypropylene films
Authors: Mucha M. , Kryszewski M. 
Published: April 2003

AbstractWith highly orientd and isotropic samples of iostactic polypropylene the thermo‐oxidative stability in air and in fumic nitric acid was studied. The rate of chain scission was found to be higher with isotropic than with oriented samples. Thermo‐oxidation in air and etching of amorphous regions leads to formation of crazes perpendicular and parallel to the orientation direction, respectively. The mechanism of the process is discussed.
13C‐NMR‐spektroskopische Untersuchungen an Cellulosesulfaten
Authors: Nehls I. , Wagenkecht W. , Philipp B. , Zschunke A. 
Published: April 2003

AbstractZur weiteren Klärung ihrer Struktur und Bildungsweise wurden unterschidlich hergestellte Cellulosesulfate mittels 13C‐NMR‐Spektroskopie in wäßriger Lösung (D2O) untersucht. Bei allen unter Auflösung der Cellulose im System N2O4/DMF mit unterschiedlichen Acrylierungsmitteln (SO2, NOSO4H, SO3‐DMF) hergestellten Proben wurde eine bevorzugte Substitution in C‐6‐Stellung beobachtet.
Urea and sodium chloride permeability of crosslinked cellulose
Authors: Ibe E. C. , Ibe S. N. 
Published: April 2003

AbstractThe permeabilities of pure and crosslinked cellulose films to urea and sodium chloride have been studied. The results show that crosslinking reduces the diffusion coefficient of urea and sodium chloride by almost a factor of 1 : 10 and 1 : 5, respectively, compared to pure cellulose. These findings have been compared to a direct dye, and the data were interpreted by reference to the pore model of water swollen cellulose. The use of crosslinking for design of permselective membranes for water desalination or in the artificial kidney is suggested.
Graft copolymerization of cotton fabric with different vinyl monomers using ferrous cellulose thiocarbonate hydrogen peroxide redox system
Authors: El‐Rafie M. H. , Khalil E. M. , Abdel‐Hafiz S. A. , Hebeish A. 
Published: April 2003

AbstractThe effects of hydrogen peroxide concentration, ferrous ion concentration, polymerization temperature and other factors on the graft polymerization of methacrylic acid and other vinyl monomers onto cotton using the redox system ferrous cellulose thiocarbonate — hydrogen peroxide were investigated.
Thermodynamics of polymer miscibility
Authors: Kammer H. W. 
Published: April 2003

AbstractThe phase behaviour of polymer blends containing random copolymers is discussed in terms of the PRIGOGINE‐FLORY theory. For a miscible high molecular mass system the interaction parameter XAB has to be negative in polymer/copolymer systems, however, miscibility does not require any specific interactions. Repulsion between the segments comprisiing the copolymer can lead to XAB < 0 and favour miscibility. At elevated temperatures immiscibility occurs due to the unfavourable free volume term depending on the difference in thermal expansion coefficients of the components. The phase diagrams of polymer/copolymer systems calculated by the presented theory agree satisfactorily with the experimental data.
Mechanochemically initiated copolymerizations. 7. Synthesis of copolymers based on styrene by vibratory milling.
Authors: Oprea C. Vasiliu , Weiner F. 
Published: April 2003

AbstractCopolymerization of styrene with maleic anhydride and isoprene was mechanochemically initiated by vibratory milling. The influence of time, comonomer ratio and addition of acceptors for radicals on the copolymerization process was investigated. The synthesized copolymers were analyzed and the polymerization mechanism is discussed.
Copolymers VI. The terpolymerization of acrylonitrile with vinylacetate and poly(ethyleneglycol)‐nonylphenoxy‐phosphite acrylate
Authors: Nicu M. , Asandei N. 
Published: April 2003

AbstractThe study ofthe terpolymerization of acrylonitrile with vinyl acetate and poly(ethyleneglycol)‐nonylphenoxy‐phosphite acrylate both in bulk and in aqueous solution/suspension revealed that the polymerization proceeds according to the ALFREY‐GOLDFINGER model. The variation of the terpolymer composition as a function of conversion as well as the pecularities of the monomer sequences were estimated.
Chemical modification of polyfunctional water soluble polymer with formaldehyde and carbamide
Authors: Pipeva P. T. , Mladenov I. T. , Verany Ch. J. 
Published: April 2003

AbstractA polyfunctional water soluble polymer obtained on the basis of polyacrylonitrile by methylation was chemicallly modified and then treated with carbamide. The optimum conditions to obtain products having minimum unreacted formaldehyde and carboxylic groups and maximum bound nitrogen were established.
Comparative investigation of thermal and thermohydrolytic degrdation of polycarbodiimides
Authors: Pankratov V. A. , Laktionov V. M. , Achmedov A. I. , Gribkova P. N. , Bilalov Ja. M. , Pavlova S. A. , Koršak V. V. 
Published: April 2003

AbstractThermal and thermohydrolytic degradation of polycarbodiimides having different chemical structures was investigated in the temperature range 200 to 550°C. Gaseous, liquid and solid products of degradation of polycarbodiimides were identified. The chemical structure of the elementary link of polycarbodiimides were found to have a substantial in fluence on their thermostability. The thermohydrolytic stability of polycarbodiimides was also found to increase, provided they are pre‐crosslinked in vacuum or in an inert medium.
Mass spectrometric identification of dimethylterephthalate and butandiol‐1,4 transesterification products
Authors: Pleškova A. P. , Fajdel' G. I. 
Published: April 2003

AbstractThe oligomeric components of the transesterification reaction of dimethylterephthalate and butandiol‐1,4 were determined inambiguously by direct analysis of the reaction mixture by field desorption mass‐spectrometry. Advantages of the field desorption as compared with electron impact and chemical ionization methods are demonstrated. Assumptions about the possibility of thermal transformations of poly(butylenterephthalate) were confirmed by chemical ionization mass spectra.
Radiation‐induced conductivity in polystyrene as a hopping phenomenon
Authors: Tyutnev A. P. , Saenko V. S. , Dubenskov P. I. , Vannikov A. V. 
Published: April 2003

AbstractTransient radiation‐induced conductivity of polystyrene resulting from single pulses (0.3 ms) of 65 keV electrons in vacuum has been investigated. The activation energy of the delayed component was found to be 0.17 eV. Doping of polystyrene with additives (rhodamine‐6G, tetracyanoethylene) is consistent with the fact that this polymer is hole conducting. Transit time effects in polymer films of 20 μm thickness are practically absent at fields less then 108 V/m. The application of the proposed theory of the transient hopping conduction and its relationship to the conventional band model of photo‐ and radiation‐induced conductivity in amorphous semiconductors is also discussed.
Ethylen‐Polymerisation mit trägerfixierten Organometallverbindungen. IV. Über die Desaktivierung des Katalysators Tetrabenzylzirkonium‐Aluminiumoxid
Authors: Ernst E. , Giesemann J. , Mellerowicz Th. , Ulbricht J. 
Published: April 2003

AbstractUnterbrechung der Monomerzufuhr bei der Ethylen‐Polymerisation mit Katalysatoren, hergestellt aus Tetrabenzylzikonium und γ‐Aluminiumoxid, zeigt, daß die Katalysatordesaktivierung nicht durch das gebildete Polyethylen bewirkt wird. Katalysatoren aus Aluminiumoxid mit unterschiedlicher thermischer Vorbehandlung und daher mit unterschiedlichem Gehalt an freien Hydroxylgruppen auf der Oberfläche haben unterschiedliche Desaktivierungsgeschwindigkeit.
On the heterophase polycondensation model
Authors: Blagodatskich I. V. , Dubrovina L. V. , Koršak V. V. , Pavlova S.‐S. A. 
Published: April 2003

AbstractA version of the heterophase polycondensation model is proposed which describes the linear irreversible polycondensation process involving liquid‐liquid phase separation. This version distinguishes from the previous model by the more appropriate description of the beginning of phase separation by selection of suitable initial concentration in the second phase. Differential equations are obtained and solved connecting molecular mass characteristics of the reaction products with the kinetics constants and phase separation parameters. Previous results are a particular case of this concept.
Viskositätsmessungen an mikrogelhaltigen Butadien‐Acrylnitril‐Copolymerlösungen
Authors: Francuskiewicz F. , Glöckner G. , Kratochvíl P. 
Published: April 2003

AbstractMikrogelhaltige Lösungen von Butadien‐Acrylnitril‐Copolymeren in Butanon wurden viskosimetrisch untersucht. Die Ergebnisse wurden mit Resultaten aus der Lichtstreuung verglichen. Die [η]‐Mw‐Beziehungen können sehr verschiedenartig sein und hägen stark von der Beschaffenheit des Probenmaterials ab. Die Ermittlung von relativen Molekülmassen aus Viskositätsmessungen ist bei solchen Lösungen deshalb fragwürdig.
Untersuchung der Heterophasen‐Copolymerisation von Methacrylnitril und Methacrylsäure in DMSO‐Wasser‐Mischungen durch Fraktionierung nach der Zusammensetzung
Authors: Bajoras G. J. , Makuška R. J. , Mjagčenkov V. A. 
Published: April 2003

AbstractEs wurden Fraktioniersysteme entwickelt, die stark oder wenig empfindlich gegenüber der Zusammensetzung von Copolymeren aus Methacrylnitirl und Methacrylsäure sind. Durch fraktionierte Fällung wurden Verteilungskurven für die Zusammensetzung und die Grenzviskosität der Copolymere, die in dem binären System DMSO/Wasser mit unterschiedlicher Zusammensetzung synthetisiert wurden, bestimmt. Durch Analyse der den verschiedenen Phasen des Systems entnommenen Proben wurden die Gesetzmäßigkeiten der Heterophasen‐Copolymerisation untersucht.
Zur Bildung wasserlöslicher Polysalze. 4. Mitt.: Untersuchungen zum Übergang vom löslichen Symplex zur Polysalzfällung
Authors: Kötz J. , Linow K.‐J. , Philipp B. , Dautzenberg He. 
Published: April 2003

AbstractDer Übergang von makroskopisch löslichen Polyanion‐Polykation‐Komplex (Symplex) zur Polysalzfällung wird mittels Kombination von Potentiometrie, Konduktometrie und Turbidimetrie untersucht. Als Ausgangsmaterialien dienen vor allem Cellulosesulfat und Polyethylenimin sowie anionisch und kationisch modifizierte Polyacrylamide. Unter den angewandten Bedingungen wurden bei elektrochemischer bzw. bei turbidimetrischer Endpunktanzeige nur in wenigen Fällen 1: 1‐Symplexe erhalten. Die Endpunkte und der Verlauf der Trübungskurve hängen von der chemischen Struktur der Komponenten, aber in erheblichem Maße auch vom Salzgehalt (NaCl) und von der Wahl der Überschußkomponente ab.