Thermostability and esterification of a polyethylene‐immobilized lipase fromBacillus coagulansBTS‐3
Authors: Kumar Satyendra , Ola Rajendra Prasad , Pahujani Shweta , Kaushal Rajeev , Kanwar Shamsher S. , Gupta Reena 
Published: August 2006

AbstractExtracellular lipase fromBacillus coagulansBTS‐3 was immobilized on activated (alkylated, 2.5% glutaraldehyde) and native (nonactivated) polyethylene powder, and its thermostability and esterification efficiency were studied. Immobilization on activated support was found to enhance thermostability as well as esterification efficiency. The optimum time for immobilization on activated (AS) and nonactivated (NS) polyethylene support was found to be 10 min, and the binding of the lipase was markedly higher on AS. Lipase was more efficiently bound to AS (64%) than to NS (30%) at an optimum temperature of 37°C. The pH and temperature optima for AS‐ and NS‐bound lipase were 9.0 and 55°C and 8.5 and 55°C respectively. At 55°C the free lipase, which had a half‐life of 2 h, lost most of its activity at elevated temperatures. In contrast, AS‐bound lipase retained 60%–80% of its original activity at 55°C, 60°C, 65°C, and 70°C for 2 h. Exposure to organic solvents resulted in enhanced lipase activity inn‐hexane (45%) and ethanol (30%). Both AS‐ and NS‐bound biocatalysts were recyclable and retained more than 85% of their initial activity up to the fourth cycle of hydrolysis ofp‐nitrophenyl palmitate. The AS‐bound lipase efficiently performed maximum esterification (98%) of ethanol and propionic acid (300 mMeach, 1 : 1) inn‐hexane at 55°C. With free or NS‐bound lipase in similar conditions, the conversion of reactants into ester was relatively low (40%). © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 102: 3986–3993, 2006
Long‐term water uptake behavior of lignocellulosic‐high density polyethylene composites
Authors: Najafi Saeed Kazemi , Tajvidi Mehdi , Chaharmahli Majid 
Published: August 2006

AbstractComposites of different lignocellulosic materials and high‐density polyethylene were prepared and their long‐term water absorption behaviors were studied. Wood flour, rice hulls, newsprint fibers, and kenaf fibers were mixed with the polymer at 25 and 50 wt % fiber contents and 1 and 2% compatibilizer, respectively. Water absorption tests were carried out on injection‐molded specimens at room temperature for five weeks. Results indicated a significant difference among different natural fibers with kenaf fibers and newsprint fibers exhibiting the highest and wood flour and rice hulls the lowest water absorption values, respectively. Very little difference was observed between kenaf fiber and newsprint composites and between rice hulls and wood flour composites regarding their water uptake behavior. The difference between 25 and 50% fiber contents for all composite formulations increased at longer immersion times, especially for the composites with higher water absorption. Kenaf fiber composites containing 50% kenaf fibers exhibited the highest water diffusion coefficient. A strong correlation was found between the water absorption and holocellulose content of the composites. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 102: 3907–3911, 2006
Synergic influence of a surfactant and ultrasonication on the preparation of soluble, conducting polydiphenylamine/silica‐nanoparticle composites
Authors: Lee Kwang‐Pill , Gopalan Anantha Iyengar , Lee See‐Hee , Showkat Ali Md , Nho Young Chang 
Published: August 2006

AbstractConducting polydiphenylamine was used to encapsulate silica nanoparticles through the oxidative polymerization of diphenylamine in the presence of ultrasonic irradiation. The polymerization was performed in the presence of sodium lauryl sulfate as a surfactant. Experiments performed in the absence of ultrasound clearly demonstrated that the application of ultrasonication played multiple roles in the preparation of a composite of polydiphenylamine with silica nanoparticles. Ultrasonication dispersed the silica nanoparticles, converted sodium lauryl sulfate to lauryl alcohol, and augmented the dispersion of the silica‐nanoparticle/polydiphenylamine composite in an organic medium. Silica‐nanoparticle/polydiphenylamine composites were also prepared in the absence of ultrasound and/or sodium lauryl sulfate. The silica‐nanoparticle/polydiphenylamine composites were characterized with Fourier trans form infrared spectroscopy, ultraviolet–visible/near‐infrared spectroscopy, and thermogravimetric analysis. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 102: 3912–3918, 2006
Sequential interpenetrating polymer networks of novolac resin and poly(n‐butyl methacrylate)
Authors: Goswami Sudipta , Chakrabarty Debabrata 
Published: August 2006

AbstractNovolac resin/poly(n‐butyl methacrylate), P(n‐BMA), sequential interpenetrating polymer networks (both semi and full types) were prepared and characterization of the various compositions (up to 40% by weight of PF incorporation) was performed in terms of mechanicals, namely, ultimate tensile strength (UTS), percentage elongation at break (% E.B.), modulus, and toughness. Thermal properties were studied by differential scanning calorimetry and thermogravimetric analysis (TGA). Crosslink densities of the IPNs were calculated using Flory‐Rehner equation. The morphological features were studied through scanning electron microscope. There was a gradual decrease of modulus and UTS with consequent increases in % E. B. and toughness with increasing proportions of P(n‐BMA). An inward shifting and lowering of the glass transition temperatures of the IPNs (compared with that of pure phenolic resin) with increasing proportions of P(n‐BMA) were observed. The TGA thermograms exhibit two‐step degradation patterns. A typical cocontinuous bi‐phasic morphology is evident in the micrographs. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 102: 4030–4039, 2006
Synthesis and properties of novel macromolecular coupling agents prepared by ATRP
Authors: Zhang Hongwen , Jiang Yan , Dong Yongquan , Li Hongtu , Zhang Kai , Wang Di , Wang Jingyuan 
Published: August 2006

AbstractNovel block and graft macromolecular coupling agents with well‐defined structures have been synthesized successfully by atom transfer radical polymerization (ATRP). The molecular weights and molecular weight distributions of those functional copolymers can be controlled because of the living/controlled ATRP. The structures and composition of block and graft copolymers with the monomers of butyl acrylate (BA), styrene (St), and 3‐methacryloxyl‐propyltrimethoxyl silicon (KH‐570) have been characterized by mean of 1H NMR, IR, GPC, and UV. Because the KH‐570 of macromolecular coupling agents owns strong affinity to surface hydroxyl of fillers, inorganic fillers that were treated by the macromolecular coupling agents possess some new properties, for example increasing the effect between matrix and fillers of composites. The mechanical properties and morphology of composites with macromolecular coupling agents have been investigated by the dynamic mechanical spectra and SEM. The results showed that the damping value and compatibility of composites with macromolecular coupling agents were improved greatly when compared with that of composite with small molecular coupling agent. Furthermore with different contents of BA, St, and KH‐570 in the macromolecular coupling agents, the damping value of the composites are different. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 102: 3919–3926, 2006
Polyelectrolyte multilayers of poly(vinylamine hydrochloride‐co‐N‐vinylformamide) with variable primary amine content and a weak polyacid poly(acrylic acid)
Authors: Serizawa Takeshi , Kawanishi Nami , Akashi Mitsuru 
Published: August 2006

AbstractPoly(vinylamine hydrochloride‐co‐N‐vinylformamide) [poly(VAm‐co‐NVF)] with variable VAm content, and a weak polyacid poly(acrylic acid) were assembled on a quartz crystal microbalance (QCM) substrate from their aqueous solutions, thus forming polyelectrolyte multilayers. The effects of varying the VAm content on assembly profiles and film structures were analyzed by quantitative QCM analysis, attenuated total reflection spectra techniques, and atomic force microscopic observation. At a VAm content of less than 40% of the total number of poly(VAm‐co‐NVF) units, the layer‐by‐layer assembly did not proceed, and the frequency shift of the QCM zigzagged with the step number. Above 40% VAm content, the frequency increased continuously with an increasing number of steps. The assembly amount was also maximal at 40% VAm content. The films obtained swelled with water molecules, and this swelling was followed by an increase in thickness in the aqueous phase. The results obtained were compared to those obtained from a combination of poly(VAm‐co‐NVF) and a strong polyacid, poly(sodium styrenesulfonate). © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 102: 3927–3933, 2006
Rheological properties of high molecular weight (HMW) syndiotactic poly(vinyl alcohol) (PVA)/HMW atactic PVA blend solutions
Authors: Lyoo Won Seok , Yeum Jeong Hyun , Kwon Oh Wook , Shin Dong Soo , Han Sung Soo , Kim Byoung Chul , Jeon Han Yong , Noh Seok Kyun 
Published: August 2006

AbstractTo identify the effect of blend ratios of syndiotacticity‐rich poly(vinyl alcohol) (s‐PVA)/atactic PVA (a‐PVA) having similar number‐average degrees of polymerization (Pn)s of 4000 and degrees of saponification (DS)s of 99.9% on the rheological properties of s‐PVA/a‐PVA/water solutions, water‐soluble s‐PVA and a‐PVA with different syndiotactic diad contents of 58.5 and 54.0%, respectively, were prepared by bulk copolymerization of vinyl pivalate and vinyl acetate (VAc) and solution polymerization of VAc, followed by saponifying the corresponding copoly(vinyl pivalate/vinyl acetate) and poly(vinyl acetate). The blend ratios played a significant role in rheological behavior. Over the frequency range of 10−1–102 rad/s, s‐PVA/a‐PVA blend solutions with larger s‐PVA content show more shear thinning at similar (Pn)s and (DS)s of polymer, suggesting that PVA molecules are more readily oriented as s‐PVA content increases. Yield stress is higher for s‐PVA/a‐PVA blend solutions with larger s‐PVA content at similar (Pn)s and (DS)s of polymer. This indicates that more domains with internal order are produced at larger s‐PVA content in s‐PVA/a‐PVA blend solutions. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 102: 3934–3939, 2006
Synthesis, characterization, and optoelectronic properties of two new polyfluorenes/poly(p‐phenylenevinylene)s copolymers
Authors: Yu Zongqiang , Tan Songting , Zou Yingping , Fan Benhu , Yuan Zhuliang , Li Yongfang 
Published: August 2006

AbstractTwo novel copolymers of polyfluorenes/poly(p‐phenylenevinylene)s copolymers with p‐tert‐butyl‐phenylenemethylene groups in the C‐9 position of alternating fluorene unit, poly[1,4‐(2,5‐dibutyloxyl)‐phenyleneviny lene‐alt‐9‐(p‐tert‐butyl‐phenylenemethylene)fluorene] and poly[1,4‐(2,5‐dioctyloxyl)‐phenylenevinylene‐alt‐9‐(p‐tert‐butyl‐phenylenemethylene)fluorine], have been synthesized via the Heck polycondensation reaction. The synthesized polymers were characterized by FTIR, NMR, DSC, TGA, UV–vis, and PL spectra. The polymers showed high glass transition temperatures and good thermal stability. A polymer light‐emitting diode with the configuration ITO/PEDOT:PSS/P2/Ca/Al has been fabricated. The device emitted a yellow light with a peak wavelength of 578 nm similar to the PL spectra of the copolymer film. A maximal luminance of 534 cd/m2 was obtained at a driving voltage of 24.5 V. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 102: 3955–3962, 2006
Superfine structure, physical properties, and dyeability of alkaline hydrolyzed soly(ethylene terephthalate)/silica nanocomposite fibers prepared by in situ polymerization
Authors: Yang Yongzhe , Gu Hongchen 
Published: August 2006

AbstractIn this study, poly(ethylene terephthalate) (PET)/SiO2 nanocomposites were synthesized by in situ polymerization and melt‐spun to fibers. The superfine structure, physical properties, and dyeability of alkaline hydrolyzed PET/SiO2 nanocomposite fibers were studied. According to the TEM, SiO2 nanoparticles were well dispersed in the PET matrix at a size level of 10–20 nm. PET/SiO2 nanocomposite fibers were treated with aqueous solution of sodium hydroxide and cetyltrimethyl ammonium bromide at 100°C for different time. The differences in the alkaline hydrolysis mechanism between pure PET and PET/SiO2 nanocomposite fibers were preliminarily investigated, which were evaluated in terms of the weight loss, tensile strength, specific surface area, as well as disperse dye uptake. PET/SiO2 nanocomposite fibers showed a greater degree of weight loss as compared with that of pure PET fibers. More and tougher superfine structures, such as cracks, craters, and cavities, were introduced, which would facilitate the certain application like deep dyeing. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 102: 3691–3697, 2006
Effect of coal filler on the properties of soy protein plastics
Authors: Guang‐Heng Wang , An‐ning Zhou , Xiao‐Bing Hu 
Published: August 2006

AbstractThe influence of ultrafine coal filler (UFC) content on tensile properties, water absorption, and biodegradability of soy protein plastics were investigated. The addition of UFC in the soy protein plastics, with different content of glycerol as a plasticizer, was at different ratio varying from 10:0 to 6:4. Blend sheets of the soy protein composites were prepared by the compression molding processing. The results show that, with 23.08 wt % glycerol, the tensile strength and elongation at break for the soy protein sheet with coal filler (range from 5 to 30 parts) can be enhanced as compared with nonfilled soy protein plastics. Water resistance of the soy protein plastics improves with the increase in UFC content. The derivative thermogravimetry (DTG) curves indicate a double‐stage degradation process for defatted soy flour (SPF), while three‐stage degradation process for soy plastics and the soy protein composites. FT‐IR, XPS, and SEM were applied to study the interfacial interaction between coal macromolecules and soy protein molecules in UFC filled soy protein plastics. The results demonstrated that there is strong interfacial interaction in the soy protein plastics caused by the compression molding processing. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 102: 3134–3143, 2006
Sorption of Cr(III)‐containing cations on strongly basic anion exchangers
Authors: Drutsa Raisa , Gutsanu V. , Rusu V. 
Published: August 2006

AbstractIt is shown that strongly basic anion exchangers AV‐17 and Varion‐AD in definite conditions are able to retain Cr(III)‐containing ions from Cr(III) sulfate solution. It is found that the sorption of Cr(III)‐containing ions on the polymers is essentially dependent on the pH, temperature, and Cr(III) sulfate concentration. The maximum temperature dependence of sorption was found to be about 60°C. The sorption isotherms are well described by Langmuir's equations. The sorption kinetics is determined by the diffusion of Cr(III)‐containing ions into polymer's phase. It is assumed that the Cr(III)‐containing ions are retained through formation, in polymer's phase, of the jarosite‐type mineral compounds: R4N[Cr3(OH)6(SO4)2], H3O[Cr3(OH)6(SO4)2], and K[Cr3(OH)6(SO4)2]. For comparison of sorptional capacities, the sorption of Cr(III)‐containing ions was determined on different cation and anion exchangers. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 102: 3978–3985, 2006
Mechanical and thermomechanical characterization of PVC/polyalkylacrylate blends
Authors: Chakrabarti Rupa , Chakraborty Debabrata 
Published: August 2006

AbstractThe effect of blending poly(ethyl acrylate) and poly(butyl acrylate) in various proportions with suitably stabilized and plasticized polyvinyl chloride (PVC) was studied with reference to their physical, mechanical, thermal, and morphological properties. The tensile modulus and ultimate tensile strength indicated a rise initially, followed by their steady decrease with increasing concentration of the polyalkyl acrylates. A corresponding behavior of elongation at break and toughness are exhibited. The various polyblends exhibit thermal stability over unmodified PVC, as reflected from their thermomechanical studies, in which the penetration is also inversely related to the respective moduli. The biphasic cocontinuous systems as explicit from the morphological studies support phase mixing at the initial stages, with subsequent phasing‐out tendency, with increasing percentage of polyalkyl acrylate incorporation. The thermomechanical parameters are in conformity to their mechanical parameters, which have been further supported by their morphological studies. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 102: 3698–3703, 2006
Hydrophobically graded polyester polyol acrylate polymers: Synthesis, characterization, and microencapsulation of sulfamethoxazole for controlled release application
Authors: Nivasu M. Venkata , Tammishetti Shekharam 
Published: August 2006

AbstractPolyester polyol macromers were prepared by using diacid‐diol condensation reaction using succinic acid as the acid component and polyethylene glycol 200 (PEG 200) as the diol component. Replacing PEG 200 with increasing amounts of butanediol resulted in macromers, which upon acrylation of end hydroxy groups and polymerization resulted in polymers with graded hydrophobicity depending on the amount of butanediol present in the polymer. These polymers showed expected trends in water equilibrium swells, equilibrium water contact angles, and in vitro degradation times depending on the amount of modification with butanediol. These polymers were used to microencapsulate sulfamethoxazole as a model drug and the in vitro delivery of the drug also followed the expected trend depending on the polymer hydrophobicity. Thus, it was shown that it is possible to prepare polyesters of graded properties by judicious selection of diacids and diols. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 102: 4058–4065, 2006
Studies on blends of polychloroprene and polybutadiene rubber containing phosphorylated cardanol prepolymer: Melt rheology, cure characteristics, and mechanical properties
Authors: Menon A. R. R. , Visconte L. L. Y. 
Published: August 2006

AbstractMelt rheology, cure characteristics, and mechanical properties of blends of polychloroprene (CR) and polybutadiene rubber (BR) in the presence and absence of phosphorylated cardanol prepolymer (PCP) were studied. The melt rheology parameters of the blends over a wide range of shear rates and temperatures were studied using a capillary rheometer (Rheoflixer SWO). The plasticizing effect of PCP in the blends was indicated by reduction in apparent melt viscosity and activation energy for melt flow. Good compatibility between the blend components (CR and BR) in the presence of PCP was evidenced by the lower values of principal normal stress difference. The self crosslinking behavior of the blends in the presence and absence of PCP was studied at different temperatures, using a Brabender Plasicorder and the kinetic parameters of crosslinking were evaluated. The cure characteristics of blends of CR and BR containing different dosages of PCP (0–10 phr) in a semi efficient vulcanization system were also studied at temperatures ranging from 150°C to 180°C, using an oscillating disk rheometer. The increase in tensile modulus, tensile strength, and tear strength of the vulcanizates in the presence of 5 phr of PCP is presumed to be an indication of reinforcement resulting from accelerated cross linking reaction as evidenced by higher chemical crosslink density index. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 102: 3195–3200, 2006
Experimental investigation of infrared rapid surface heating for injection molding
Authors: Chang Pei‐Chi , Hwang Sheng‐Jye 
Published: August 2006

AbstractA low cost and practical infrared rapid surface heating system for injection molding is designed and investigated. The system was designed to assemble on the mold and a control system was used to operate the motion of the lamp holder. Four infrared halogen lamps (1 kW each) were used as the radiative source to heat the surface of mold insert. The temperature increase is verified on the mold plate with a thermal video system. Two types of specular reflectors combined with different bulb configurations were applied to study the heating ability of radiation heating. A modified spiral flow mold was used to test the enhancing filling ability of the rapid surface heating system. Three resins, PP, PMMA and PC were molded in the spiral flow injection molding experiments. If spherical reflector and centralized lamp configuration are used, the temperature at the center of the mold surface is the highest. The temperature of mold center surface is raised from 83°C to 188°C with 15 s of infrared heating. Because the surface temperature of the mold insert is higher than the glass transition temperature of resins before filling, the flow distance of resins in the modified spiral flow mold will be increased. The location effect of the infrared surface heating system on a thin‐long cavity was studied to demonstrate the possibility of using smaller infrared heating area on a large mold surface. A microprobe cavity also demonstrated that with the assistance of infrared heating technology the formability of a microprobe can be greatly improved. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 102: 3704–3713, 2006
Accelerated aging versus realistic aging in aerospace composite materials. II. Chemistry of thermal aging in a structural composite
Authors: Dao B. , Hodgkin J. , Krstina J. , Mardel J. , Tian W. 
Published: August 2006

AbstractSamples of an aerospace structural epoxy composite (8552/IM7) were subject to long‐term (≈ 1 year) thermal aging at temperatures of 70°, 120°, 170°, and 200°C (in air). The changes to the chemical and physicochemical structure of the composite were analyzed by a range of different techniques, including gravimetric analysis, Fourier transform infrared (FTIR), and dynamic mechanical analysis (DMA) to compare the effects of different severities of degradation treatment. The results highlighted the large differences in chemical effects between the surface and the interior of the composite with very minor changes in the latter even at quite high aging temperatures and long aging times. The oxidative changes at the surface, however, varied from highly selective molecular changes for particular chemical groups at the lower aging temperatures (70° and 120°C), to quite general and extensive oxidative degradation at the higher aging temperatures (170° and 200°C). The results indicated that the mechanical changes in an aged composite of this type will vary greatly with the material thickness and surface protection as well as the aging temperature the composite is exposed to. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 102: 3221–3232, 2006
Development of novel film using paramylon prepared from Euglena gracilis
Authors: Kawahara Yutaka , Koganemaru Akihiro 
Published: August 2006

AbstractA novel film was developed using paramylon from Euglena gracilis and its physical properties were investigated. Formic acid was suitable for the preparation of a solution of paramylon, and a transparent even yellow film was obtained by casting the solution on a glass plate and drying the cast film in air without using coagulation bath. However, the spinability of a paramylon solution was fairly low. The spinability was a little enhanced by blending polyvinyl alcohol (PVA) up to 70%. The paramylon/PVA blend fibers were produced through wet spinning using coagulation bath of conc. Na2SO4 at a room temperature. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 102: 3495–3497, 2006