Structural Variations in Chlorite and Illite in a Diagenetic Sequence from the Imperial Valley, California
Authors: Walker Jeffrey R. , Thompson Graham R. 
Published: August 2006

AbstractSamples of cuttings from the Borchard A-2 well, Imperial Valley, California, were collected over a measured borehole temperature interval 135° to 275°C. The <0.5-µm (e.s.d.) fraction was separated using high-gradient magnetic separation (HGMS) to create a nonmagnetic fraction rich in illite and a magnetic fraction rich in chlorite. Chlorite was less easily separated from illite in lower temperature samples (<200°C), presumably due to the presence of polymineralic grains of chlorite and illite. Grains in higher temperature samples were more nearly monomineralic and more easily separated.The chlorite is the IIb polytype. The thickness of coherent scattering domains of chlorite increased until 220°C and then remained constant. The amount of 7-Å interstratified material increased downhole until 195°C and then decreased. Over the same temperature interval, the illite polytypes varied systematically from 1Md (135° to 175°C) to 1M + 2M1 (230° to 275°C) and coherent scattering domains in the mineral became thicker to about 200°C and then remained constant in thickness. The percentage of illite in mixed-layer illite/smectite (I/S) increased from 40% at 135°C to 100% at temperature >205°C; ordering in the I/S changes from R0 to R1 between 135° and 155°C, and from R1 to R ≥ 3 at temperatures >155°C.The concurrent structural changes in chlorite and illite indicate a general improvement in the overall structural order of the clay minerals with increasing temperature. Differences between chlorite and illite suggest that the minerals may have reacted differently to changing conditions or that they may have formed by different mechanisms. The exclusive occurrence of IIb chlorite at temperatures as low as 135°C extends the limit of IIb chlorite stability to temperatures lower than previous estimates.
A Novel Differential Thermal Analysis Method for Quantifying the Sorption Capacity of Smectite Clay
Authors: O'Brien Paul , Williamson Colin J. 
Published: August 2006

AbstractThe enthalpy of freezing of methyl salicylate sorbed by four commercial montmorillonite clays was used to estimate the absorption/adsorption capacity of the clay. Differential thermal analysis was therefore employed to give a quantitative estimate of the sorption capacity of the clay for methyl salicylate. The absorption capacity of the clay depended on the state of hydration and ranged from 30.4% for an 8% water content to 9.7% for a montmorillonite containing 24% water.
Molecular-Scale Imaging of Clay Mineral Surfaces with the Atomic Force Microscope
Authors: Hartman H. , Sposito Garrison , Yang Andrew , Manne S. , Gould S. A. C. , Hansma P. K. 
Published: August 2006

AbstractSpecimen samples of Crook County montmorillonite and Silver Hill illite, purified and prepared in the Na-form, were imaged under 80% relative humidity using an atomic force microscope. The direct images showed clearly the hexagonal array of hexagonal rings of oxygen ions expected for the basal planes of 2:1 phyllosilicates. Fourier transformation of the digital information obtained by the microscope scanning tip led to an estimate of 5.1 ± 0.3 Å for the nearest-neighbor separation, in agreement with the ideal nearest-neighbor spacing of 5.4 Å for hexagonal rings as derived from X-ray powder diffraction data. The atomic force microscope should prove to be a useful tool for the molecular-scale resolution of clay mineral surfaces that contain adsorbed macromolecules.
Study of Some Physicochemical Properties of Pillared Montmorillonites: Acid-Base Potentiometric Titrations and Electrophoretic Measurements
Authors: Avena Marcelo J. , Cabrol Raúl , De Pauli Carlos P. 
Published: August 2006

AbstractThe surface charges and the zeta potential of a Na-montmorillonite (Na-mont) and two pillared montmorillonite (MP1 and MP2) samples with different aluminum contents were determined by Potentiometric titrations and electrophoretic measurements. At pH >9 the two pillared montmorillonite samples showed zeta potentials similar to those of Na-mont, but at pH <8, the negative zeta potential shifted to lower negative values as the aluminum content increased. Sample MP1, which had a greater Al content, showed an isoelectric point (IEP) of 5.0–5.5. Titration curves obtained by acid-base Potentiometrie titration for sample MP1 showed a well-defined cross-over point at pH = 5.0, whereas this point was not observed for sample MP2 in the pH range studied. The results indicate, in principle, that both techniques can be used to characterize surface charges in this type of material. An attempt was also made to relate the data obtained from electrophoretic mobility and Potentiometrie titrations.
Direct High-Resolution Transmission Electron Microscopic Measurement Of Expandability Of Mixed-Layer Illite/Smectite In Bentonite Rock
Authors: Środoń Jan , Andreoli Cristina , Elsass Françoise , Robert Michel 
Published: August 2006

AbstractSamples of mixed-layer illite/smectite were investigated from a single bentonite bed zoned with respect to expandability from 90 to 30%. Chips of natural rocks were embedded in a resin, using a procedure designed to preserve the original fabric, cut with an ultramicrotome, and observed by high-resolution transmission electron microscopy (HRTEM). These observations confirmed the X-ray powder diffraction (XRD) model of mixed-layer clays, i.e., that illite/smectite grains in natural rocks are built of mixed-layer crystals, from 1 to as many as 15 silicate layers thick (4–6 interlayers per crystal on average). These crystals are present either as individual particles (loose crystals) or, typically, they form nearly parallel face-to-face groupings called here quasi-crystals. Free fundamental smectite and illite particles as defined by Nadeau and coworkers were essentially absent.Illite and smectite interlayer spacings were 10 and 13.5 Å, respectively. Crystal thickness and number of interlayers were measured for 35–100 mixed-layer crystals per sample. Illite/smectite expandabilities were calculated from these data in two ways: either neglecting the crystal edges or accounting for them. The former determinations agree well with XRD estimates of expandability and the latter, with expandabilities calculated from the distributions of fundamental particle thickness measured by a shadowing technique in the TEM. This result explains the systematic discrepancy between XRD and TEM measurements of illite/smectite expandability.
Cross-Linked Hydroxy-Al-Montmorillonite as a Stationary Phase in Liquid Chromatography
Authors: Tsvetkov Faina , Mingelgrin U. , Lahav N. 
Published: August 2006

AbstractQuasi-spherical particles (7-µm mean diameter) were prepared from cross-linked hydroxy-Al-montmorillonite (basal spacing =15.3 and 18.6 Å) by spray-drying. These particles (SP-CLM) were used as a packing material for columns in high-pressure liquid chromatography (HPLC). Aromatic phosphate esters, chlorosubstituted phenyl-ureas, monosubstituted benzenes, and the o-, m-, and p-isomers of disubstituted benzenes were separated on the columns, using isopropanol and hexane. Alkyl and alkoxy groups in the solute molecules sterically hindered the interaction of these molecules with the solid phase. The retention of the isomers of disubstituted benzenes that possess one electronegative (or dipolar) and one nonpolar substituent increased in the order: o- < m- < p-. In contrast, for all investigated disubstituted benzenes containing two electronegative (or dipolar) substituents, the o-isomer was retained on the 18.6-Å SP-CLM more strongly than the m- and p-isomers. The chromatographic data suggest that the strength of the interaction of phenolic groups with the solid phase increased with the acidity of these groups. The o-isomers of phenols that contained an additional electronegative (or dipolar) substituent displayed an exceptionally strong adsorption. The capacity of the o-isomers of disubstituted benzenes containing two electronegative (or dipolar) substituents to form chelates with Al probably was responsible for the strong retention of such o-isomers compared with the retention of the corresponding m- and p-isomers.Cross-linked hydroxy-Al-montmorillonite acted as a strong and selective adsorbent for many families of organic compounds. It was used successfully as the solid phase in HPLC separations with eluents ranging from nonpolar (e.g., hexane) to highly polar (e.g., water).
Diagenesis of Oligocene-Miocene Vitric Tuffs to Montmorillonite and K-Feldspar Deposits, Durango, Mexico
Authors: de Pablo-Galan Llberto 
Published: August 2006

AbstractMontmorillonite and K-feldspar deposits of potential economic interest occur in the Late Oligocene-Miocene tuffs of the Vizcarra Formation in the state of Durango, Mexico. The two minerals were formed separately from rhyodacitic to rhyolitic pyroclastic deposits in a closed hydrologie system and diagenetically altered following two different patterns. In material deposited on dry land the glass was completely replaced by K-feldspar, and the interstices between the replaced glass bubbles and shards were filled with chalcedony, quartz, and albite. Pyroclastic material deposited in an alkaline lacustrine environment were diagenetically altered to montmorillonite, which formed the bentonitic tuffs widely exposed beneath the K-feldspar-rich tuff. These bentonitic tuffs contain as much as 85% montmorillonite plus authigenic chalcedony and quartz. Pyrogenic sanidine, quartz, and oxybiotite, coarse glass shards, and clastic grains make up about 8% of the clay-rich tuffs. The composition of the montmorillonite corresponds to the formula (Si3.88Al0.12)(Al1.41Mg0.59)O10(OH)2(Ca0.07Mg0.11,Na0.28K0.06). The montmorillonite is dioctahedral, the surface acidity is of the Lewis type, and the clay swells to one- and two-layer complexes. The cation-exchange capacity is 64 meq/100g; base exchange is Ca2+, 15; Mg2+, 20; Na+, 4.1; and K+, 1.0 meq/100 g. Its interlamellar charge is 18.6 microcoulombs/cm2. Dacitic pyroclastics were deposited later at higher elevations along the margins of the basin. Percolating solutions apparently removed a siliceous leachate from the dacitic glass and partially altered it to clinoptilolite.
Determination of Surface Areas of Mineral Powders by Adsorption Calorimetry
Authors: Ticknor Kenneth V. , Saluja Preet P. S. 
Published: August 2006

AbstractAdsorption calorimetry was used to develop a method for determining the surface area of low-surface-area materials (<1 m2/g), which required no pretreatment of the surface, such as outgassing at elevated temperatures. The method involved flowing heptane through a small amount of sample (0.15 to 1.0 g) in the flow cell of a commercial microcalorimeter. When thermal equilibrium was reached at the powder-heptane interface, pure heptane was replaced with a heptane carrier-solution containing 0.6 volume % n-butanol (n-BuOH) as the preferential adsorbate. The integral enthalpy of preferential saturation adsorption, ΔHsat, of n-BuOH on the surface was found to be a function of the BET surface area of the sample. An empirical relationship between ΔHsat and BET surface area was determined over a surface area range of about three orders of magnitude (0.095 to 81 m2/g) by performing adsorption experiments on five α-alumina standard reference powders. The technique was applied to the determination of surface areas of untreated rock and mineral powders.
Transmission and Analytical Electron Microscopic Study of Mixed-Layer Illite/Smectite Formed as an Apparent Replacement Product of Diagenetic Illite
Authors: Jiang Wei-Teh , Peacor Donald R. , Merriman R. J. , Roberts B. 
Published: August 2006

AbstractOrdered illite/smectite (I/S) and illite in a pelitic rock from a prograde metamorphic sequence in North Wales were observed by transmission electron microscopy. The dominant phyllosilicate noted was diagenetic-metamorphic illite, occurring as subparallel packets of layers, each about a few hundred Ångstroms thick. It exhibited two-layer polytypism (presumably 2M1) and numerous strain features and had a composition of (K1.21Na0.12)(Al3.36Fe0.31Mg0.33)(Si6.28Al1.72)O20(OH)4.I/S occurred as thick packets of wavy layers having 10-Å subperiodicity and sharp differences in contrast in successive lattice fringes. All stages in a replacement series were noted, from one or two layers of smectite within illite, through thin packets of I/S, to thick packets that contained inherited deformation textures of diagenetic-metamorphic illite. Deformed illite was replaced by I/S more commonly than was undeformed illite. The I/S replacing undeformed original illite had significantly greater order, primarily of R1 type (ISISIS…), than that replacing deformed illite. R> 1 I/S occurred as small crystallites and contained relatively less smectite than the ordered I/S, Single smectite layers were spaced within several illite layers, forming curved packets of layers. IISIIS… (R2) and IIISIIIS… (R3) ordering were present locally, as was discrete smectite. Analytical electron microscopic analyses indicated that the I/S, (K0.46Na0.43)(Al3.75Fe0.06Mg0.19)(Si6.26Al1.74)O20(OH)4, was rectorite-like in composition and had smaller (Mg + Fe) contents and greater Al/Si ratios than the coexisting illite, which was also anomalous in terms of general crystal-chemical relationships between coexisting illite and I/S in burial diagenesis environments. The I/S appears to have formed by replacement of diagenetic-metamorphic illite, presumably at very low temperatures under hydrous conditions via dissolution and crystallization.
Transformation of Akaganéite Into Goethite and Hematite in Alkaline Media
Authors: Cornell R. M. , Giovanoli R. 
Published: August 2006

AbstractThe conversion of akaganéite to goethite and/or hematite in alkaline media has been followed by X-ray powder diffraction and transmission electron microscopy (TEM). The rate of transformation fell and the amount of hematite in the product increased as the [OH−] decreased to < 1 M. Kinetic studies and TEM indicated that the transformation involved dissolution of akaganéite followed by reprecipitation of goethite and/or hematite. The rate-determining step was the dissolution of akaganéite.Silicate species retarded the formation of goethite + hematite principally by inhibiting dissolution of akaganéite; to a lesser extent, they interfered with the nucleation of goethite. Silicate modified the morphology of goethite, but not hematite.Comparison of the transformation behavior of akaganéite with that previously observed for ferrihydrite indicated that the composition of the reaction product depended strongly on the transformation conditions, i.e., pH and the presence of foreign species. The nature of the solid precursor was important insofar as its degree of crystallinity governed the dissolution kinetics and its surface properties influenced interaction with any foreign species in the system.
Adsorption of Hydroxy-Al Polycations and Destabilization of Illite and Montmorillonite Suspensions
Authors: Gu Baohua , Doner H. E. 
Published: August 2006

AbstractWater-infiltration characteristics of soil can be improved by preventing clay dispersion. The present study determined the adsorption properties of hydroxy-Al polycations (Al-p) and their relation to the destabilization of clay suspensions. Al-p was synthesized and fractionated into nominal molecular weights between 104 and 5 × 104. The reactions of Al-p with Na-illite and Na-montmorillonite indicated a very strong affinity of Al-p to the clay surfaces. The maximum adsorptions of Al-p by Na-illite and Na-montmorillonite were found to be 0.37 and 1.7 mmole Al/g, and very close to the cation-exchange capacity of the two clays, suggesting that the adsorption was chiefly controlled by the mechanism of charge screening. Adsorption of Al-p increased the points of zero charge (PZCs) and the apparent points of zero salt effect (PZSEs) of illite and montmorillonite. PZSEs for both clays were 4.7 at their maximum Al-p adsorption, and PZCs ranged from 5.3 to 6.4, depending on solution ionic strength and the individual clay minerals. The differences in PZCs were probably due to outer-sphere complex formation between Al-p-treated illite and montmorillonite and the swamping electrolyte. Critical flocculation concentrations (CFCs) of Al-p for Na-illite and Na-montmorillonite were at 0.28 and 1.0 mmole Al/g, whereas zero electrophoretic mobilities were at about 0.36 and 1.67 mmole Al/g Al-p additions. Excessive addition of Al-p reversed this surface charge of clay colloids and restabilized the illite but not montmorillonite suspensions. This difference was probably due to the stronger and more extensive interparticle bridging of montmorillonite particles by Al-p than those of illite. The CFCs for the two clays were also found to be dependent on sodium adsorption ratio (SAR), pH, and ionic strength. Increases in SAR and pH significantly increased the CFC, whereas an increase in ionic strength decreased the CFC.
Orientation of Hexanediamine in Synthetic Fluorhectorite
Authors: Hertl William , Bartholomew Roger F. 
Published: August 2006

AbstractFourier-transform infrared (FTIR) spectroscopic studies were carried out on 1,6-hexanediamine hydrochloride (HDA)-treated synthetic fluorhectorite to determine the orientation of functional groups within the structure. Oriented crystal layers were prepared by flocculating the smectite slurry with glass fibers to obtain a 100-µm-thick paper. Orientations were determined by measuring integrated IR band intensities at various incident beam angles (≤60°), inasmuch as absorption occurred only if the oscillating dipole of the functional group interacted with the electric vector of the incident radiation. The H-N-H plane in amine groups was aligned parallel to the lamellar plane. The H-O-H plane of the small amount of sorbed water was inclined 45° or more to the interlamellar layer, and the OH groups were inclined 45° to this layer.Even with the incorporation of HDA in the interlamellar structure, at high humidity, additional water sorbed. The sorbed water competed with and displaced amine groups from the surface, resulting in randomly oriented amine groups. Many of the amine groups were ionized, whereas the additional sorbed water showed little orientation.This study demonstrated that the orientation of intercalated amines in fluorhectorite can be determined by following the intensity changes in infrared-active bands as a function of the incident beam angle. With intercalated HDA, the orientations were influenced by the presence of interlayer water.
The Nature of Cation-Substitution Sites in Phyllosilicates
Authors: Bleam William F. 
Published: August 2006

AbstractA fundamental property of electrostatic potentials is their additivity. This study demonstrates that the electrostatic potential of a negatively charged, cation-substituted phyllosilicate layer can be represented as the sum of two potentials. Viewing cation substitution as a defect, one potential is derived from the atoms in a charge-neutral, unsubstituted layer such as pyrophyllite or talc. The “neutral-layer” potential rapidly decays to zero with distance from the layer and is determined primarily by the atoms in the first two atomic planes parallel to the (001) surface, i.e., the basal oxygens and tetrahedral cations. The second component, characterized as a “defect” potential, is a long-range potential derived from cation-substitution. The model used to compute the electrostatic potentials, a two-dimensional Ewald lattice sum, represents the atoms of a single phyllosilicate layer as point charges.
Polarized Single-Crystal Fourier-Transform Infrared Microscopy of Ouray Dickite and Keokuk Kaolinite
Authors: Johnston C. T. , Agnew S. F. , Bish D. L. 
Published: August 2006

AbstractSingle-crystal Fourier-transform infrared (FTIR) spectra of Keokuk kaolinite and Ouray dickite were obtained with an FTIR microscope. Although numerous IR, FTIR, and Raman spectra of polycrystalline kaolinite and dickite can be found in the literature, the present data represent the first reported single-crystal vibrational spectra for these clay minerals. The orientation of the crystallographic axes of dickite was determined using a cross-polarizing optical microscope fitted with an 550-nm optical retardation plate. Assignment of the inner hydroxyl group OH1 to the 3623-cm-1 band was confirmed, and the angle of this OH group to the b-axis was determined to be 47° based upon the measured dichroic ratio. The 3702-3710-cm−1 absorption feature appeared to consist of two closely spaced bands having slightly different polarization behavior. The inner-surface hydroxyl group OH3 was assigned to the absorption bands at 3710 cm−1. The calculated angle of the OH3 groups to the b-axis was found to be 22°, which agrees well with the angles determined by X-ray powder diffraction and neutron diffraction. The remaining hydroxyl groups, OH2 and OH4, were assigned to the 3656 cm-1 band; the angle of the OH2 and OH4 groups to the b-axis was measured at 45°. The polarization behavior of the OH-deformation bands of dickite at 911, 937, and 952 cm−1 was found to be similar to that observed in the OH-stretching region. Single-crystal FTIR spectra of Keokuk kaolinite showed that rotation of the electric vector around the c/z axis in the ab plane of kaolinite resulted in a behavior distinct from that of dickite. The OH-stretching bands of kaolinite were found to be considerably more polarized than the corresponding bands of dickite. This is related directly to the fact that dickite possesses a glide plane (space group Cc) compared with kaolinite, which does not (space group C1).
Paramagnetic Defect Centers in Hydrothermal Kaolinite from an Altered Tuff in the Nopal Uranium Deposit, Chihuahua, Mexico
Authors: Muller Jean-Pierre , Ildefonse Philippe , Calas Georges 
Published: August 2006

AbstractPoint defect centers in hydrothermal kaolinite have been investigated using electron paramagnetic resonance (EPR). Kaolinite was sampled in petrographically well-defined materials coming from uranium-rich hydrothermally altered volcanic tuffs (Nopal I uranium deposit, Chihuahua, Mexico), which show extensive kaolinization and an intense redistribution of uranium. Several kaolinite parageneses were defined according to their origin (fissure fillings and feldspar pseudomorphs); their location relative to the U6+ mineralization at the scale of the deposit (mineralized breccia pipe vs. barren surrounding rhyolitic tuffs), and at the scale of mineral assemblages; and their crystal chemistry.Two types of centers of axial symmetry were identified (A- and A′-centers) and represent positive holes trapped on apical oxygens (Si-O−-centers). A-centers were stable to 400°C, whereas A′-centers annealed at 350°C. A relation between defect-center concentration and U content demonstrates that natural irradiation was responsible for these centers. On the other hand, defect-center concentration was not directly linked to the origin (fissural or feldspar pseudomorph) or the crystal chemistry (structural order and substitutional Fe3+ content) of the kaolinite. According to petrographic data, and with respect to the relative thermal stability of A- and A′-centers, two successive irradiations of kaolinite were evidenced: (1) originally during crystallization of kaolinite from radioactive hydrothermal solutions, and (2) permanently when kaolinite was in contact with secondary U-silicates, which led to the formation of A′-centers.Because of the short half-life of U, these two radiation-induced centers were created by short-lived elements of the U-decay series. As a consequence, variations of defect-center concentration possibly reflect variations in radioactive disequilibrium during the history of the alteration system. This provides a unique tool for tracing the dynamics of the transfer of radionuclides in the geosphere: kaolinite may be used as a sensitive in situ dosimeter, which may be useful in the fields of weathering petrology and nuclear waste management.