Effects of Trace Elements on Creep Properties of Nickel-Iron Base Superalloy
Authors: Hasebe Yusaku , Maeda Eiji , Takasawa Koichi 
Published: March 2024

Abstract
The aim of this work was to reveal the effects of trace elements on the creep properties of nickel-iron base superalloys, which are the candidate material for the large components of the advanced-ultrasupercritical (A-USC) power generation plants. High temperature tensile and creep properties of forged samples with seven different compositions were examined. No significant differences were observed in the creep rate versus time curves of the samples, of which contents of magnesium, zirconium, manganese and sulfur were varied. In contrast, the curves of phosphorus-added samples showed very small minimum creep rates compared to the other samples. The creep rupture lives of phosphorus-added samples were obviously longer than those of the other samples. Microstructure observation in the vicinity of grain boundaries of phosphorus-added samples after aging heat treatment revealed that there were fine precipitates consisting of phosphorus and niobium at the grain boundaries. The significant suppression of the creep deformation of phosphorus-added sample may be attributed to the grain boundary strengthening caused by the fine grain boundary precipitates.
A Newly Designed Nickel-Based Superalloy GH750 For 700°C Advanced Ultra-Supercritical Power Plants
Authors: Lin Fusheng , Zhao Shuangqun , Fu Rui , Wang Yanfeng , Xie Xishan , Chi Chengyu , Hu Yaohe , Zhang Maicang 
Published: March 2024

Abstract
A new nickel-based superalloy, designated as GH750, was developed to meet the requirements of high temperature creep strength and corrosion resistance for superheater/reheater tube application of A-USC power plants at temperatures above 750°C. This paper introduces the design of chemical composition, the process performance of tube fabrication, microstructure and the properties of alloy GH750, including thermodynamic calculation, room temperature and high temperature tensile properties, stress rupture strength and thermal stability. The manufacturing performance of alloy GH750 is excellent and it is easy to forge, hot extrusion and cold rolling. The results of the property evaluation show that alloy GH750 exhibits high tensile strength and tensile ductility at room and high temperatures. The 760°C/100,000h creep rupture strength of this alloy is larger than 100MPa clearly. Microstructure observation indicates that the precipitates of GH750 consist of the precipitation strengthening phase γ’, carbides MC and M23C6 and no harmful and brittle TCP phases were found in the specimens of GH750 after long term exposure at 700~850°C. It can be expected for this new nickel-based superalloy GH750 to be used as the candidate boiler tube materials of A-USC power plants in the future.
Design, Creep Performance and Deformation Behavior of an Eta-Phase Strengthened Nickel-Base Alloy for A-USC Power Plant Applications
Authors: Milligan W.W. , Sanders P.G. , White C.L. , Shingledecker J.P. , Purdy D.F. 
Published: March 2024

Abstract
By utilizing computational thermodynamics in a Design of Experiments approach, it was possible to design and manufacture nickel-base superalloys that are strengthened by the eta phase (Ni3Ti), and that contain no gamma prime (Ni3Al,Ti). The compositions are similar to NIMONIC 263, and should be cost-effective, and have more stable microstructures. By varying the aging temperature, the precipitates took on either cellular or Widmanstätten morphologies. The Widmanstätten-based microstructure is thermally stable at high temperatures, and was found to have superior ductility, so development efforts were focused on that microstructure. High temperature tensile test and creep test results indicated that the performance of the new alloys was competitive with NIMONIC 263. SEM and TEM microscopy were utilized to determine the deformation mechanisms during creep.
Creep and Creep Rupture Behavior of Nickel-Base Alloys for Superheaters After Cold Working
Authors: Mueller Falk , Oechsner Matthias 
Published: March 2024

Abstract
In order to enable a compact design for boiler superheaters in modern thermal power plants, cold-worked tube bending is an economical option. For service metal temperatures of 700 °C and above, nickel-based alloys are typically employed. To ensure a safe operation of such cold-worked alloys, their long-term mechanical behavior has to be investigated. In general, superheater tube materials in a cold-worked state are prone to a degradation of their long-term creep behavior. To predict this degradation, sensitive experiments have to be conducted. In this publication, the effects of cold working on the long-term creep behavior of three currently used nickel-based alloys are examined. Creep and creep rupture experiments have been conducted at typical service temperature levels on nickel-based alloys, which have been cold worked to various degrees. As a result, Alloy 263 exhibits no significant influence of cold working on the creep rupture strength. For Alloy 617, an increase of creep strength due to cold working was measured. In contrast, Alloy 740 showed a severe degradation of the creep strength due to cold working. The mechanism causing the sensitivity to cold working is not yet fully understood. Various formations of carbide precipitates at the grain boundaries are believed to have a major influence. Nevertheless, the experimentally observed sensitivity should always be considered in material selection for boiler tube design.
Design, Operation, Numerical Simulation and Damage Assessment of a Header in the HWT Test Loop
Authors: Speicher Magdalena , Klenk Andreas , Steck Tobias , Helmrich Andreas , Kluger Frank 
Published: March 2024

Abstract
In the test loop HWT II (High Temperature Materials Test Loop) installed in the fossil power plant Grosskraftwerk (GKM) Mannheim in Germany, thick-walled components made of nickel base alloys were operated up to temperature of 725 °C. The operation mode chosen (creep-fatigue) was to simulate a large number of start-ups and shutdowns with high gradients as expected for future high efficient and flexible power plants and to investigate the damage due to thermal fatigue of the used nickel base alloys. In this paper the damage evolution of a header made of the nickel base alloys Alloy 617 B and Alloy C263, which was a part of HWT II test rig, were investigated using nondestructive and destructive techniques. Furthermore, the damage has been considered and evaluated by using numerical methods. In addition, different lifetime assessment methods of standards and recommendations with focus on creep-fatigue damage were used and evaluated. The different lifetime models are applied to the header and the results were compared to the results of metallographic investigations and damage observations.
Creep Failure Analysis of Superheater Tubes in a Supercritical Boiler
Authors: Che Chang , Qian Gong , Qian Linfeng , Chen Xinzhong 
Published: March 2024

Abstract
Up to now, the amount of supercritical boilers in China has ranked number one in the world. Many supercritical boilers have run for more than 100,000 hours. Creep becomes one of the main reasons for supercritical boiler tubes failure. In this article, the failure of superheater tubes in a supercritical boiler was analyzed, the microstructural evolution of austenitic stainless steel tubes were studied, a full investigation into the failure cause was carried out involving in visual examination, optical microscope, SEM, TEM and XRD. The results show, sigma phase precipitates in this austenitic steel with the extension of service time, sigma precipitates form at grain boundaries by continuous chain. Sigma precipitates are hard and brittle, weaken grain boundaries and cause microscopic damage, eventually lead to boiler tubes failure.
Microstructure Impacts on Mechanical Properties in a High Temperature Austenitic Stainless Steel
Authors: Purdy D. , Maziasz P.J. , Wharry J. , Dolph C. 
Published: March 2024

Abstract
Austenitic and super-austenitic stainless steels are a critical component of the spectrum of high temperature materials. With respect to power generation, alloys such as Super 304H and NF709 span a gap of capability between ferritic and martensitic high chromium steels and nickel-based alloys in boiler tube applications for both conventionally fired boilers and heat-recovery steam generators (HRSG). This research explores a wrought version of a cast austenitic stainless steel, CF8C-Plus or HG10MNN, which offers promise in creep strength at relatively low cost. Various manufacturing techniques have been employed to explore the impact of wrought processing on nano-scale microstructure and ultimately performance, especially in high temperature creep. Transmission electron microscopy has been used to quantify and characterize the creep-strengthening particles examining the relationship between traditional melting and extrusion as compared to powder metallurgy.
Thermal Fatigue Properties of Dissimilar Welded Part of SUPER304H Boiler Steel Tube
Authors: Noguchi Yasutaka , Hirata Hiroyuki , Yoshizawa Mitsuru , Tanaka Katsuki 
Published: March 2024

Abstract
Austenitic stainless steels have been used for boiler tubes in power plants. Since austenitic stainless steels are superior to ferritic steels in high temperature strength and steam oxidation resistance, austenitic stainless steel tubes are used in high temperature parts in boilers. Dissimilar welded joints of austenitic steel and ferritic steel are found in the transition regions between high and low temperature parts. In dissimilar welded parts, there is a large difference in the coefficient of thermal expansion between austenitic and ferritic steel, and thus, thermal stress and strain will occur when the temperature changes. Therefore, the dissimilar welded parts require high durability against the repetition of the thermal stresses. SUPER304H (18Cr-9Ni-3Cu-Nb-N) is an austenitic stainless steel that recently has been used for boiler tubes in power plants. In this study, thermal fatigue properties of a dissimilar welded part of SUPER304H were investigated by conducting thermal fatigue tests and finite element analyses. The test sample was a dissimilar welded tube of SUPER304H and T91 (9Cr-1Mo-V-Nb), which is a typical ferritic heat resistant boiler steel.
Creep Behavior and Microstructure Evolution in AISI 316LN + 0.1 Wt.% Nb Steel at 600 and 625°C
Authors: Vodärek Vlastimil , Řehořek Jakub 
Published: March 2024

Abstract
The paper deals with microstructural evolution in the AISI 316LN + 0.1 wt.% Nb steel during long-term creep exposure at 600 and 625°C. The following minor phases formed: Z-phase (NbCrN), M23C6, M6X (Cr3Ni2SiX type), η-Laves (Fe2Mo type) and σ-phase. M6X gradually replaced M23C6 carbides. Primary Z-phase particles were present in the matrix after solution annealing, while secondary Z-phase particles formed during creep. Precipitation of Z-phase was more intensive at 625°C. The dimensional stability of Z-phase particles was excellent and these particles had a positive effect on the minimum creep rate. However, niobium also accelerated the formation and coarsening of σ-phase, η-Laves and M6X. Coarse particles, especially of σ-phase, facilitated the development of creep damage, which resulted in poor long-term creep ductility.
Influence of Holding Time During Tempering on the Long-Term Creep Rupture Strength of MOD.9Cr-1Mo Steel
Authors: Komai Nobuyoshi , Arisue Ko , Tominaga Kimihiko , Fujita Masaaki 
Published: March 2024

Abstract
The influence of holding time during tempering on the long-term creep rupture strength of mod.9Cr-1Mo steel was investigated in this study, so as to elucidate proper heat treatment for boiler applications. Tempering was conducted at 770°C for 0.5h, 1h, 3h, 10h and 100h for the test materials, after re-normalization at 1050°C for 1h in all cases. Creep rupture tests were conducted at 600°C, and ruptured specimens were investigated to better understand the microstructural changes, including changes in the number density of precipitates, in order to observe and discuss their creep strength. All creep rupture test results for materials tempered within 10h exceeded the average creep strength of T91. Shorter tempering times such as 0.5h and 1h were clearly correlated with longer time to rupture at 600°C under 80MPa to 100MPa stress conditions. Reduction of area in creep-ruptured specimens decreased principally with lowered creep stress. Materials tempered for 0.5h and 100h showed the lowest reduction of area at 90MPa and 100MPa respectively, and their reduction of area recovered at lower than those stress levels. These stresses, showing minimum reduction of area, met inflection stress in the creep rupture strength curve.
Effect of Stress and Strain on Microstructural Changes During Long-Term Creep in T91 Steel
Authors: Sawada Kota , Hara Toru , Kushima Hideaki , Kimura Kazuhiro , Tabuchi Masaaki 
Published: March 2024

Abstract
In order to clarify the effect of stress and strain on microstructural changes during creep for T91 steel, creep interrupted tests were performed at 600°C for 10000h, 20000h, 30000h, 50000h and 70000h. The steel studied was T91 steel with high Ni content (0.28mass%) in the range of specification. Changes of dislocation structure and precipitates distributions were observed for the grip and gauge portions of creep interrupted samples. The subgrain size gradually increased with increasing creep time up to 50000h in both the grip and gauge portions. However, the subgrain size abruptly increased after 50000h in the gauge portion as compared with the grip portion. Decrease in dislocation density inside subgrain was promoted in the gauge portion as compared with the grip portion. The size of M23C6 gradually increased with increasing creep time up to 50000h in both the grip and gauge portions. The increase in M23C6 size was accelerated after 50000h in the gauge portion as compared with the grip portion. The Z phase formation was promoted in the gauge portion as compared with the grip portion. The number density of all kinds of particles gradually decreased with increasing creep time in the gauge and grip potions. After 50000h, the number density rapidly decreased in the gauge portion as compared with the grip portion.
Evaluation of Long Term Creep Strength of Mod. 9Cr Heat Resistant Ferritic Steel with the Aid of System Free Energy Concept
Authors: Murata Yoshinori , Watanabe Naoya , Nagae Yuji 
Published: March 2024

Abstract
In order to evaluate long term creep strength of modified 9Cr ferritic steels, the system free energy of creep ruptured specimens at both 650 and 700 °C is evaluated as the sum of chemical free energy, strain energy and surface energy, which are obtained by a series of experiments, i.e., chemical analysis using extracted residues, X-ray diffraction, and scanning transmission electron microscopy. Change ratio of the system free energy and creep stress showed the relationship with one master curve irrespective of creep conditions, indicating that the steel ruptures when the applied stress exceeds a limited stress depending on the microstructural state expressed by the change ratio of system free energy. Furthermore, it was found that dominant factor of the change ratio was the chemical free energy change. On the basis of these results, long term creep strength of the steel was evaluated at 700 °C, for example, 19MPa at 700 °C after 105 h. It is concluded that long term creep strength of modified 9Cr ferritic steels can be predicted by the system free energy concept using the ruptured specimens with various creep conditions.
Small Scale Impression Creep Testing of an Ex-Service Mis-Heat Treated Seam Welded Grade 91 Hot Reheat Bend
Authors: Brett S J , Lant T , Clark A 
Published: March 2024

Abstract
This paper reports the results of a collaborative small scale creep testing exercise carried out by the UK generating companies Centrica, SSE, Engie and RWE as part of an investigation of an ex-service grade 91 bend.
Impression Creep Testing and Its Role in Power Plant Component Integrity Management
Authors: Dyson C. , Sun W. , Brett S. J. , Hyde T. H. , Hyde C. J. , Shingledecker J. , Purdy D. 
Published: March 2024

Abstract
The impression creep test method using a rectangular indenter has been well established and the applicability of the technique has been supported by the test data for a number of metallic materials at different temperatures and stresses. The technique has proved to be particularly useful in providing material data for on-site creep strength assessments of power plant components operating in the creep regime. Due to these reasons, “standard” assessment procedures using the impression testing method are needed in order for the technique to be more widely used. This paper will first address some key issues related to the use of the impression creep test method, involving the data conversion method, typical test types and validity of the test technique etc. Then some recommendations on a number of practical aspects, such as the basic requirements of test rigs, “standard” specimen geometry, indenter dimensions, sampling procedures for scoop samples, specimen preparation, temperature and loading control, and displacement measurement, are briefly addressed. Finally, applications of the test data to assist with the risk management and life assessment programme of power plant components, particularly those with service-exposed materials, using data obtained from scoop samples, are described. Proposals for future exploitation and for improvement of the technique are addressed.
The Effect of Pre-Service Treatments on the Long Term Properties of 9Cr Steels Strengthened by Boron and Nitrogen
Authors: Sammarco A. , Thomson R. C. , Vanstone R. 
Published: March 2024

Abstract
Martensitic 9Cr steels have been developed which are strengthened by boron in order to stabilize the microstructure and improve their long-term creep strength. Boron plays a key role in these steels by stabilising the martensitic laths by decreasing the coarsening rate of M23C6 carbides, which act as pinning points in the microstructure. In this work two modified FB2 steel forgings are compared. Both forgings have similar compositions but one underwent an additional remelting process during manufacture. Creep tests showed that this additional processing step resulted in a significant increase in time to failure. In order to investigate the effect of the processing route on microstructural evolution during aging and creep, a range of advanced electron microscopy techniques have been used including ion beam induced secondary electron imaging and High Angle Annular Dark Field (HAADF) imaging in the Scanning Transmission Electron Microscope. These techniques have enabled the particle population characteristics of all the second phase particles (M23C6, Laves phase, BN and MX) to be quantified for materials from both forging processes. These quantitative data have enabled a better understanding of how the processing route affects the microstructural evolution of FB2 steels.
Research on Test and Evaluation of High Depth-To-Width Ratio Longitudinal Defects of Boiler Tube Inner Wall
Authors: Zhang Lei , Ma Hong , Cui Jinwen , Shi Zhigang , Cui Xionghua 
Published: March 2024

Abstract
To solve crack problems at the tube elbow induced by high depth-to-width ratio longitudinal defects on the inner wall of boiler tube, a number of testing experiments and testing methods have been applied to analysis on the sensitivity and correspondence of such defects, and it has been found that the flattening test has an outstanding advantage to detect such defects. However, according to relevant standards, the judgment is controversy. It can be noted from the research that if a steel tube with a ratio of wall thickness to outer diameter larger than 0.1 is turned prior to the flattening test, to reduce such ratio to be less than or equal to 0.1, the shortcomings in detection and evaluation of such defects specified in the current relevant standards of many countries can be effectively overcome. The method has been proposed and adopted preliminarily in the relevant Chinese standard.
Analysis on Effect of Piping Stress and Supports and Hangers on Cracking of Tee Welds
Authors: Zhao Bo , Ma Hong , Dong Lei , Wang Junmin , Wang Bining , Deng Linghui , Cheng Yongming 
Published: March 2024

Abstract
The piping stress and thermal displacement corresponding to different types of riser rigid support and hanger devices in different installation directions have been calculated by means of finite element analysis, to further analyze the impact on cracking of adjacent steam tee welds exerted by the constraint effect of riser rigid hangers on angular displacement. It can be seen from the analysis that a riser rigid hanger has a constraint effect on angular displacement, and such a constraint effect, however, is weak and limited on the piping stress and thermal displacement, so the piping stress and supports and hangers are not the main reasons for the cracking of tee welds. In addition, the calculation results alert that for an axial limiting hanger of riser with a dynamic axial pipe clamp and rigid struts, its constraint effect on angular displacement has a significant impact on the piping stress and thermal displacement.
The Influence of Prior Austenite Grain Size on Fatigue Crack Growth Threshold of welds in Cr-Mo-V Steel Components
Authors: Huo Xin , Wang Peng , Hu Mengjia , Cai Zhipeng , Pan Jiluan 
Published: March 2024

Abstract
The fatigue crack propagation thresholds of SAW weld metal of 25Cr2Ni2MoV simulating product of fossil and nuclear power low pressure turbine rotor at different stress ratios are tested. There is a big dispersity of the test results, even at the same stress ratio. The double logarithm curves of the fatigue crack growth rate and stress intensity factor range are researched. The difference of critical points between stable propagation region and near-threshold region in different specimens is found to be an important cause to the dispersity. Their locations in the specimens can be determined by the method of backward inference. After the observation of the microstructures around the critical points, a good correspondence between the size of prior austenite grain and the maximum size of monotonic plastic zone on the crack tip is confirmed. The difference of the critical points at the same stress ratio is caused by the inhomogeneous microstructures. So the inhomogeneous microstructures in the multi-pass and multi-layer weld metal contribute to the dispersity of the experimental threshold values.