Kaolinite-Pyridine Intercalation Compound Derived from Hydrated Kaolinite
Authors: Sugahara Yoshiyuki , Satokawa Shigeo , Yosioka Ken-Ichi , Kuroda Kazuyuki , Kato Chuzo 
Published: August 2006

AbstractA kaolinite-pyridine intercalation compound was prepared using hydrated kaolinite as an intermediate. Hydrated kaolinite having a basal spacing of 10 Å was treated with pyridine to form a well-ordered intercalation compound having a basal spacing of 12.0 Å. Infrared spectroscopy indicated the presence of hydrogen bonding between the hydroxyls of the kaolinite and the pyridine. 29Si nuclear magnetic resonance spectroscopy with cross polarization and magic-angle spinning revealed that intercalated pyridine affected the environment of silicon. The mono-substituted pyridine derivatives were also intercalated with hydrated kaolinite. On the basis of the basal spacings of the intercalation compounds and the stabilities of the derivatives between the layers, the pyridine appeared to be in an approximately perpendicular position, with the nitrogen facing the gibbsitic sheets.
Layer-Charge and Cation-Exchange Characteristics of Vermiculite (Weathered Biotite) Isolated from a Gray Luvisol in Northeastern Saskatchewan
Authors: Ghabru S. K. , Mermut A. R. , St. Arnaud R. J. 
Published: August 2006

AbstractLayer charge and cation-exchange characteristics of weathered biotite isolated from a Gray Luvisol in Saskatchewan showed that this product was a high-charge vermiculite. Cation-exchange capacity (CEC) of the sand-size (100–250 μm) weathered biotite particles from different horizons, as determined by a 30-min Ca/Mg exchange, was low (23–71 meq/100 g). Increasing the exchange period to 24 hr increased the CEC to 33–95 meq/100 g for samples from the solum horizons and to 155–163 meq/100 g for samples from C horizons. The free oxide coatings on the mineral particles in the solum horizon samples apparently prevented the exchange cations from entering the interlayers. Removal of free oxides followed by 24-hr exchange sharply increased the CEC of these samples to 105–155 meq/100 g. Oxidation and loss of structural iron resulted in lower octahedral-cation occupancy (2.4–2.6 per half unit cell), suggesting a transition of the trioctahedral biotite to dioctahedral vermiculite. X-ray powder diffraction and high-resolution transmission electron microscopic analyses of alkylammonium-exchanged samples from the sand fractions of all horizons and magnetic separates of the coarse clays showed a linear increase in the d-value of the vermiculite with increasing chain length of the cations. The linear relationships suggest a paraffin-type arrangement having a uniform and high layer charge (0.70–0.76 per half unit cell in the sand-size particles; 0.80–0.84 in the clay fraction). The empirical relationship between tilt angle (α) and the layer charge density for paraffin-type structures, as suggested by Lagaly and Weiss, cannot be used for accurate layer-charge determination. Based on experimental evidence, a straight line relationship between the tilt angle and layer charge is suggested. The layer charge values show no marked variation within the profile and agree well with those calculated from the chemical composition. The repotassified layers of vermiculite in the sand-size weathered biotite particles did not respond to the Ca/Mg exchange, but were expanded by the alkylammonium cations; in contrast, a pure biotite standard (Bancroft, Ontario) of same particle size was unaffected by either treatment.
Preparation and Characterization of Al-Rich Zn-Al Hydrotalcite-Like Compounds
Authors: Thevenot F. , Szymanski R. , Chaumette P. 
Published: August 2006

AbstractHydrotalcite-like compounds, described by the formula [Zn1-xAlx(OH)2][(CO3)x/2 · nH2O], were prepared by coprecipitation methods at 80°C and characterized by bulk chemical analysis, X-ray powder diffraction (XRD), nuclear magnetic resonance (NMR), and scanning-transmission electron microscopy (STEM). An x value of 0.33 was previously assumed to be an upper limit, but recently, Al-rich hydrotalcite-like compounds have been prepared with x as large as 0.44 by hydrothermal synthesis. In the Zn-Al system, Al-rich hydrotalcite was synthesized at normal pressure by coprecipitation. Zn-Al hydrotalcite-like compounds were obtained in the range of x = 0.3 to 0.4. An Al-rich hydrotalcite-like compound with x = 0.44 was formed in mixtures containing large amounts of a poorly crystalline Zn-Al phase. A continuous contraction of the hydrotalcite-like structure occurred as x increased, both the a and c lattice parameters decreasing for x values as large as 0.44. This study illustrates the advantages of using quantitative analytical electron microscopy with high spatial resolution to complement conventional (and bulk) characterization techniques for correlating structural and compositional characteristics of finely divided materials.
Fe-Smectite-Glauconite Transition in Hydrothermal Green Clays from the Galapagos Spreading Center
Authors: Buatier Martine , Honnorez Jose , Ehret Gabrielle 
Published: August 2006

AbstractX-ray powder diffraction (XRD) and energy-dispersive X-ray analyses (EDX) of individual clay particles from hydrothermal mounds in the Galapagos spreading center (GSC) (Deep Sea Drilling Project, hole 509B) and high-resolution transmission electron microscopy (HRTEM) of the <2-µm size fraction of these sediments were carried out to document the mineralogy, geochemistry, and evolution of their clay horizons. The hydrothermal clay minerals of the GSC mounds were found to be intercalated with pelagic sediments and occurred as irregular interstratified illite/smectite according to X-ray powder diffraction analyses. On the basis of TEM, HRTEM, and EDX data, two types of clays appeared to coexist; these types differed in morphology, potassium content, and mode of stacking sequence. Lath-shaped particles having regular 10-Å, spacings were identified as glauconite, and filmy or veil-like particles, having curly edges and variable 10-13-Å spacings were identified as Fe-smectite (nontronite and Fe-montmorillonite). The absence of lattice fringes between Fe-smectite and glauconite crystallites was observed by HRTEM in clay aggregates. This structural discontinuity between Fe-smectite and glauconite layers suggests that a dissolution-recrystallization mechanism was responsible for the textural and chemical transition from the filmy Fe-smectite to the lath-like glauconite.
Rheological Behavior of Na-Montmorillonite Suspensions at Low Electrolyte Concentration
Authors: Chen J. S. , Cushman J. H. , Low P. F. 
Published: August 2006

AbstractThe prevailing concept that positive-edge to negative-face attraction accounts for the rheological behavior of montmorillonite suspensions at low electrolyte concentration was investigated. In one experiment, Mg2+ released from Na-montmorillonite was measured at several NaCl concentrations; in a second experiment, the viscosity, η, and the extrapolated shear stress, θ, were measured at several clay concentrations, pHs, and NaCl concentrations; and in a third experiment, the absorbance, A, was measured at two wavelengths (450 and 760 nm) at different clay and electrolyte concentrations. The released Mg2+ decreased with increasing NaCl concentration until it became zero at a NaCl concentration between 0.01 and 0.02 M, depending on pH. Thereafter, it increased with increasing NaCl concentration. Both θ and η were highly correlated with the amount of released Mg2+. Also, A remained constant until the NaCl concentration corresponded to that at the minimum of θ. Thereafter, it increased and became linearly related to θ. These results suggest: (1) positive-edge to negative-face interaction cannot solely account for the rheological properties of montmorillonite at low electrolyte concentration, and (2) the release of octahedral Mg2+ from montmorillonite affects θ, because it reduces the negative charge on the particles and, thereby, the repulsive force between them.
Fe Substitution for Al in Glauconite with Increasing Diagenesis in the First Wilcox Sandstone (Lower Eocene), Livingston Parish, Louisiana
Authors: Strickler Michael E. , Ferrell Ray E. 
Published: August 2006

AbstractGlauconites in early ankerite concretions, ferroan calcite-cemented sandstones, and uncemented sandstones in the first Wilcox sandstone of the Lockhart Crossing field, Livingston Parish, Louisiana, show a progressive substitution of Fe for octahedral Al with increasing diagenesis. An octahedral Fe content of 0.50 atoms was calculated from glauconite located in early ankeritic concretions. Octahedral Fe averaged 0.60 and 0.90 atoms in later ferroan calcite-cemented sandstone and uncemented sandstone, respectively. Corresponding octahedral Al averages were 1.16, 1.03, and 0.67, respectively. A systematic increase in average interlayer K from 0.49 to 0.54 to 0.61 was also observed, with apparent increases in diagenesis. All element determinations were made with an electron microprobe and recast on an anion equivalent basis to structural formulae based on the O10(OH)2 unit. The clay preserved in the early ankerite concretions was found to be an illite/smectite containing about 20% expandable layers, and the mineral in the glauconite pellets from uncemented areas of the sandstone, an ordered glauconite. “Minus cement” porosities of the sandstone indicate that glauconitization may have taken place at burial depths greater than 0.6 to 1.8 km, but the mechanism for the incorporation of Fe3+ in the glauconite at that depth is not apparent.
Swelling of n-Butylammonium Vermiculite in Water
Authors: Braganza L. F. , Crawford R. J. , Smalley M. V. , Thomas R. K. 
Published: August 2006

AbstractThe swelling of an n-butylammonium vermiculite in solutions of n-butylammonium chloride has been studied by neutron diffraction as a function of temperature and the concentration of the soaking solution. On heating a swollen sample a transition to the crystalline phase took place at a well-defined temperature, the c-axis spacing changing from 120 to 19.4 Å at 14°C in a 0.1 M solution and from 330 to 19.4 Å at 33°C in a 0.01 M solution. The phase transition was completely reversible, and a study of the temperature-concentration phase diagram was made as high as 50°C The swollen phase was studied in a range of concentrations of the external solution between 0.2 M and 5 × 10-4 M, for which the c-axis spacings were 85 and 910 Å, respectively. The reversibility, sharpness, and reproducibility of the phase change from crystalline to swollen gel suggest that the transition is truly thermodynamic, which is not in accord with DLVO theory. The concentration dependence of the observed d-values also could not be explained satisfactorily by DLVO theory.
Adsorption of Benzene, Toluene, and Xylene by Two Tetramethylammonium-Smectites Having Different Charge Densities
Authors: Lee Jiunn-Fwu , Mortland Max M. , Chiou Cary T. , Kile Daniel E. , Boyd Stephen A. 
Published: August 2006

AbstractA high-charge smectite from Arizona [cation-exchange capacity (CEC) = 120 meq/100 g] and a low-charge smectite from Wyoming (CEC = 90 meq/100 g) were used to prepare homoionic tetra-methylammonium (TMA)-clay complexes. The adsorption of benzene, toluene, and o-xylene as vapors by the dry TMA-clays and as solutes from water by the wet TMA-clays was studied. The adsorption of the organic vapors by the dry TMA-smectite samples was strong and apparently consisted of interactions with both the aluminosilicate mineral surfaces and the TMA exchange ions in the interlayers. In the adsorption of organic vapors, the closer packing of TMA ions in the dry high-charge TMA-smectite, compared with the dry low-charge TMA-smectite, resulted in a somewhat higher degree of shape-selective adsorption of benzene, toluene, and xylene. In the presence of water, the adsorption capacities of both samples for the aromatic compounds were significantly reduced, although the uptake of benzene from water by the low-charge TMA-smectite was still substantial. This lower sorption capacity was accompanied by increased shape-selectivity for the aromatic compounds. The reduction in uptake and increased selectivity was much more pronounced for the water-saturated, high-charge TMA-smectite than for the low-charge TMA-smectite. Hydration of the TMA exchange ions and/or the mineral surfaces apparently reduced the accessibility of the aromatic molecules to interlamellar regions. The resulting water-induced sieving effect was greater for the high-charge TMA-smectite due to the higher density of exchanged TMA-ions. The low-charge Wyoming TMA-smectite was a highly effective adsorbent for removing benzene from water and may be useful for purifying benzene-contaminated water.
Identification of Noncrystalline (Fe,Cr)(Oh)3 by Infrared Spectroscopy
Authors: Amonette James E. , Rai Dhanpat 
Published: August 2006

AbstractIron-chromium hydroxides are important solid phases governing the aqueous concentrations of Cr(III) in soils and fly ashes. Although direct identification of noncrystalline (Fe,Cr)(OH)3 is difficult, the infrared spectra of noncrystalline Fe(OH)3 and Cr(OH)3, coprecipitated (Fe,Cr)(OH)3, and physical mixtures of Fe(OH)3 and Cr(OH)3 can be distinguished on the basis of the asymmetric stretching doublet (v3) of structural carbonate anions. As the Cr mole fraction of the coprecipitated (Fe,Cr)(OH)3 increases, the position of the low-frequency v3 peak (v3″) changes progressively to higher frequencies, and the carbonate v3 splitting decreases. No change in carbonate v3 splitting or v3″ location was observed for physical mixtures of Fe(OH)3 and Cr(OH)3. The changes in v3 splitting are believed to be caused by different degrees of polarization of the carbonate ligand by the Fe and Cr cations.Pure Cr(OH)3 exhibits a strong affinity for carbonate and H2O and tends to remain noncrystalline even at very high pHs. In contrast, pure Fe(OH)3 gradually converts to crystalline goethite at high pH, to the exclusion of much of the H2O and carbonate. The presence of Cr in (Fe,Cr)(OH)3 solid solutions seems to inhibit the transformation to crystalline goethite. The strong association of carbonate with Cr and the kinetic inertness of Cr(III) inner-sphere complexes in general may account for the maintenance of noncrystalline solid-solution materials in lieu of transformation to a crystalline end product.
The Influence of Aluminum on Iron Oxides: XIV. Al-Substituted Magnetite Synthesized at Ambient Temperatures
Authors: Schwertmann U. , Murad E. 
Published: August 2006

AbstractMixtures of magnetite and goethite were formed by the slow oxidation of mixed FeCl2-AlCl3 solutions in an alkaline environment at room temperature. The compositions of the products ranged from almost exclusively magnetite in Al-free systems to goethite only at Al/(Al + Fe) ≈ 0.3. The magnetic phase consisted of a partly oxidized (Fe2+/Fe3+ < 0.5), Al-substituted magnetite. The unit-cell edge length a of the magnetite decreased with increasing Al(Al ≈ 0–0.37 per formula unit, corresponding to 0–14 mole % Al) and decreasing Fe2+ in the structure as described by the empirical relationship α(A) = 8.3455 + 0.0693 Fe2+ - 0.0789 Al. A correlation between the experimentally determined a and that calculated from the unit-cell edge lengths of end-member magnetite, maghemite, and hercynite was highly significant (r = .96) although shifted by about 0.01 Å. Mössbauer spectra showed Al to have entered preferentially the tetrahedral rather than the octahedral sites at low Al substitutions (<0.15 per formula unit), perhaps because of steric reasons. With increasing Al substitution the crystal size of magnetite decreased and structural strain increased, indicating that the structure had a limited capability to incorporate Al under these synthesis conditions. The capacity of the goethite structure to tolerate more Al may explain why goethite replaced magnetite at higher Al concentrations.
Palygorskite in the Eocene Rocks of the Dammam Dome, Saudi Arabia
Authors: Çag̃atay M. Namik 
Published: August 2006

AbstractClay mineralogy and petrography of the Early to Middle Eocene succession of the Dammam dome, Saudi Arabia, comprising the Rus and Dammam Formations, were studied using X-ray powder diffraction, light microscopy, and scanning electron microscopy. These formations consist of alternations of dolomite, dolomitic marl, claystone, and shale. The rocks were deposited and subjected to early diagenetic dolomitization in a shallow, coastal marginal basin characterized by rapid changes in salinity. Palygorskite occurs as interwoven fibrous mats forming fine laminae in shales and as coatings and pore-filling and pore-bridging cements in dolomitic marls. This textural evidence suggests a direct chemical precipitation, mostly post-dating dolomitization. Magnesium concentrations in presence of dolomite was sufficient for palygorskite precipitation; the necessary Si and Al were derived by dissolution of silicates under alkaline conditions. The maximum development of palygorskite was near the top of the Dammam Formation, which was deposited during a marine transgression in the Lutetian. The formation of palygorskite in marginal restricted basins in eastern Saudi Arabia took place during Paleocene-Middle Eocene time and was contemporaneous with similar occurrences in the Tertiary basins of West Africa.
Clay-Modified Electrodes: A Review
Authors: Fitch Alanah 
Published: August 2006

AbstractClay-modified electrode research indicates that adsorbed complexes are electroactive if the adsorption sites are clay edges. Interlayer adsorbed complexes may be electroactive if a charge shuttle is added or if interlayer swelling is large. Conductivity of the film towards anionic species depends upon the swelling of the clay, which depends on the electrolyte concentration and speciation. The diffusion coefficients measured by electrochemical experiments agree well with alternative measurements.
Low-Temperature Alteration of Palygorskite To Smectite
Authors: Golden D. C. , Dixon J. B. 
Published: August 2006

AbstractThe feasibility of transforming palygorskite from two localities to smectite hydrothermally at temperatures ranging from 22° to 160°C was investigated in a series of laboratory experiments, in which alkalinity was maintained in the pH range of 11.4 to 12 by adding NaOH. The smectite formed was characterized by chemical, spectroscopic, and electron microscopic techniques. Smectite formed rapidly at > 100°C; the transformation was slow, however, at 22°C. The introduction of MgCO3 accelerated the alteration process, but changes in alkalinity at pH > 12 and the difference in elemental composition of the palygorskite samples did not significantly affect the alteration. A pressure of one atmosphere and a temperature of 22°C were sufficient for some transformation to occur within a few months, provided the alkalinity was maintained close to pH 12. X-ray powder diffraction characterization of the product indicated a smectite, and infrared spectroscopy indicated saponite. The alteration to smectite was appreciable even at room temperature, which suggests that the reaction can take place without any external heating.
Changes in the Properties of a Montmorillonite-Water System during the Adsorption and Desorption of Water: Hysteresis
Authors: Fu M. H. , Zhang Z. Z. , Low P. F. 
Published: August 2006

AbstractSamples of Na-saturated, Upton montmorillonite were prepared with different contents of water (H2O or D2O) by: (1) adsorption of water from the vapor phase at a specific value of p/p°, the relative humidity, (2) adsorption of water from the vapor phase at p/p° = 1.0 followed by desorption of the water into the vapor phase at a specific p/p° < 1.0, and (3) adsorption of water from the liquid phase followed by desorption of the water into the vapor phase at a specific p/p° < 1.0. Water adsorbed initially from the vapor phase was called V-adsorbed water, and water adsorbed initially from the liquid phase was called L-adsorbed water. The water contents of these samples were determined by gravimetric analysis, the c-axis spacings by X-ray powder diffraction, the O-D stretching frequencies by IR spectroscopy, and the heats of immersion by differential microcalorimetry. No difference was found between V-adsorbed and L-adsorbed water; however, if the final water content was established by adsorption, the system was in a different state than if the final water content was established by desorption. In particular, hysteresis was observed in the following properties: the relative humidity of the adsorbed water, the O-D stretching frequency in this water, and the degree of order in the stacking of the clay layers. The only property that did not exhibit hysteresis was the heat of immersion. Apparently, hysteresis occurred because the orderliness of the system was not reversible, and, thus, any property that depended on orderliness was hysteretic.
Reaction Scheme for the Oxidation of as(III) to as(V) by Birnessite
Authors: Moore Johnnie N. , Walker Jeffrey R. , Hayes Thomas H. 
Published: August 2006

AbstractThe oxidation of As(III) to As(V) by K-birnessite was examined at different temperatures, pHs, and birnessite/As(III) ratios. Experiments ranged in duration from 5 to 64 hr, and solution and solid products were determined at several intervals. All experiments showed that the reaction produced large amounts of K+ to solution and very little Mn2+. As(V) was released to solution and incorporated into the K-birnessite. The oxidation was initially rapid and then slowed. The oxidation of As(III) was probably facilitated initially by autocatalytic Mn-As(V) reactions occurring mostly in the interlayer, in which large amounts of As(V) and K+ could be easily released to solution. The reaction also slowed when interlayer Mn was exhausted by forming Mn-As(V) complexes. Mn(IV) could only be acquired from the octahedral sheets of the birnessite. The two-stage reaction process proposed here depended on the layered structure of birnessite, the specific surface, and presence of exchangeable cations in K-birnessite.
Effect of Pellet Pressing on the Infrared Spectrum of Kaolinite
Authors: Bell Valerie A. , Citro Vincent R. , Hodge Gail D. 
Published: August 2006

AbstractDiffuse reflectance infrared (IR) spectra show that pressing kaolinite into pellets for transmission IR studies changes relative intensities of hydroxyl peaks between 3700–3600 cm-1. The magnitude of change depends on the absolute pressure, the pressing time and whether a salt matrix is used. Pressing with KBr causes larger differences than pressing neat. Diffuse reflectance IR does not require sample pressing, eliminating this variable in kaolinite studies. This improves IR's ability to distinguish kaolinites according to their hydroxyl group differences and may lead to a better understanding of kaolinite hydroxyl structures.