Sorption of Benzene, Toluene, Ethylbenzene, and Xylene (BTEX) Compounds by Hectorite Clays Exchanged with Aromatic Organic Cations
Authors: Jaynes W. F. , Vance G. F. 
Published: August 2006

AbstractAdsorptive-type organoclays, where hydrocarbons adsorb directly to the siloxane surfaces, were studied to find new organic cations and to determine the parameters that produce effective sorbents. Organoclays were prepared from hectorite by cation exchange with small, aromatic organic cation salt solutions. Trimefhylphenylammonium (TMPA) chloride was obtained and iodide salts of commercially-unavailable aromatic cations were synthesized and used to prepare organoclays. An aqueous mixture of benzene, toluene, ethylbenzene, and xylenes (BTEX) consistent with the composition of unleaded gasoline was used in sorption isotherms to compare the sorptive properties of the organoclays. Only the TMPA, methylphenylpyridinium (MPPyr), and trimethylammonium indan (Indan) organoclays were effective BTEX sorbents. Organoclays prepared from methylpyridinium (MPyr), trimethylammonium biphenyl (Biphenyl), and trimethylammonium fluorene (Fluorene) were poor sorbents. The MPPyr and TMPA organoclays preferentially sorbed ethylbenzene, whereas the Indan organoclay preferentially sorbed benzene and toluene. Langmuir-type sorption isotherms for the TMPA, MPPyr, and Indan organoclays implied surface adsorption, whereas linear isotherms suggested that partitioning was the sorptive mechanism for the MPyr, Biphenyl, and Fluorene organoclays. Water hydrating the small MPyr cation and the larger bulk of the Biphenyl and Fluorene cations may have blocked BTEX access to the interlayer siloxane surfaces. Although the rather bulky MPPyr and Indan cations produced effective organoclays, compact size and low hydration are organic cation properties that typically yield effective adsorptive-type organoclays.
Modeling of Organic and Inorganic Cation Sorption by Illite
Authors: Polubesova Tamara , Nir Shlomo 
Published: August 2006

AbstractSorption of several organic and inorganic cations on illite (Clay Minerals Society Source Clay Imt-2) was determined experimentally and results compared to model calculations. The cations studied were crystal violet (CV+), benzyltrimethylammonium (BTMA+), benzyltriethylammonium (BTEA+), Ca2+, Mg2+, K+, Na+, Cs+, and Li+. The adsorption-model calculations involved a solution of the electrostatic Gouy-Chapman equations. The model considered specific adsorption and sorption/exclusion in the double-layer region in a closed system. Model calculations considered the simultaneous presence of four to six cations in the system. The adsorption of CV included formation of neutral and charged complexes. The adsorption attained 0.37 mol kg−1 or 150% of the cation exchange capacity (CEC) of illite in aqueous suspension. The adsorption of BTMA and BTEA did not exceed the CEC and was reduced with an increase in ionic strength. The sorption of CV below the CEC was rather insensitive to the ionic strength because of the large binding coefficients and was only slightly reduced in NaCl, CsCl, or Na2SO4 solutions. When added in amounts exceeding the CEC in high ionic strength, 0.667 M NaNO3, NaCl, or CsCl solutions, the adsorbed quantities of CV increased to three times the CEC. At high sulphate concentrations (0.333 M Na2SO4), the adsorption was below the CEC. Model calculations yielded satisfactory simulations for the adsorption, particularly for cations added in amounts approaching or exceeding the CEC. The binding coefficients for formation of neutral complexes followed the sequence: CV > Ca > BTMA > BTEA > Cs > Mg > K > Na > Li. Model calculations also suggested that sites were present which bound exchangeable cations, particularly K+, Na+, and Mg2+, very tightly.
Preparation and Properties of Hematite with Structural Phosphorus
Authors: Gálvez Natividad , Barrón Vidal , Torrent José 
Published: August 2006

AbstractSynthetic hematites prepared in the presence of phosphate can incorporate phosphorus (P) in forms other than phosphate adsorbed by ligand-exchange on the crystal surface. To investigate the nature of such occluded P, which is also found in some natural specimens, we prepared 13 hematites by aging ferrihydrite precipitated from Fe(NO3)3-KH2PO4 solutions. The P/Fe atomic ratio of the resulting hematites ranged from 0 to 3% and all incorporated significant amounts of OH. As P content is raised, particle morphology changes from rhombohedral to spindle or ellipsoid-shaped. Despite the grainy appearance in transmission electron microscope images, X-ray diffraction data indicate that the particles are single crystals. Specific surface area ranged from 66 to 91 m2g−1, partly in micropores. The intensity of the absorption bands due to Fe3+ ligand field transition in the visible region, as measured by the second derivative of the Kubelka-Munk function, suggests that both OH and P contribute to an Fe deficiency in the structure. Such a deficiency is also apparent from the 104/113 peak intensity ratio in the X-ray diffraction patterns. The c unit-cell length increases with increasing P content. The infrared spectra exhibit four bands in the P-OH stretching region (viz., at 936, 971, 1005, and 1037 cm−1) which suggest that occluded PO4 possesses a low symmetry. Congruent dissolution of P and Fe was observed on acid treatment of the hematites, the dissolution rate being negatively correlated with the P content. All observations are consistent with the occluded P in the hematites being structural. A model is proposed where P occupies tetrahedral sites in the hematite structure, thus resulting in an Fe deficiency and facilitating proton incorporation.
Smectites in Iron-Rich Calcareous Soil and Black Soils of Taiwan
Authors: Pai Chuang-Wen , Wang Ming-Kuang , Wang Wei-Min , Houng Kun-Huang 
Published: August 2006

AbstractThe iron-rich calcareous soil (Typic Rhodustalf) from the Penghu island group represents a volcanic area. The black soils (Typic Haplustert, Vertic Endoaquoll, Typic Hapludolls) are typical of eastern Taiwan. Four A horizons and a pedon from the iron-rich calcareous soil and four pedons from the black soils were studied to analyze soil properties and clay compositions. The objective was to compare the properties of smectites developed from different parent materials. The materials were studied by using conventional X-ray diffraction (XRD) of K- and Mg-saturated clays and involved the alkylam-monium (C = 12) method and the Greene-Kelly test. The mean-layer charge of smectites (0.48–0.52 cmol(c)/O10(OH)2) in the iron-rich calcareous soil was found to be higher than the black soils (0.43–0.48 cmol(c)/O10(OH)2). A smectite of higher charge developed from the basalts. This smectite is enriched in Fe and Mg, and lacks Si, thereby forming beidellite and/or nontronite. In contrast, under high precipitation, elevated temperature, base saturation (e.g., Na, K, Ca, Mg), and about equal wet and dry cycles per year in the black soil environments, smectites developed from the complicated geologic site of eastern Taiwan. These smectites transformed to smectite-kaolinite mixed-layer clay and thus, resulted in lower-charge smectites. The K fixation capacity of the iron-rich calcareous soil was higher than the black soils.
The Structure of U6+ Sorption Complexes on Vermiculite and Hydrobiotite
Authors: Hudson Eric A. , Terminello Louis J. , Viani Brian E. , Denecke Melissa , Reich Tobias , Allen Patrick G. , Bucher Jerome J. , Shuh David K. , Edelstein Norman M. 
Published: August 2006

AbstractThe sorption of the uranyl oxo-cation (UO22+)at different types of binding sites on layer silicate mineral surfaces was investigated. Well-characterized samples of vermiculite and hydrobiotite were exposed to aqueous uranyl under conditions designed to promote surface sorption either at fixed charge ionexchange sites or at amphoteric surface hydroxyl sites. The local structure of uranium in the sorption samples was directly measured using uranium L3-edge extended X-ray absorption fine structure (EXAFS). Polarized L1- and L3-edge X-ray absorption near-edge structure (XANES) measurements were used to characterize the orientation of uranyl groups in layered samples. X-ray diffraction (XRD) measurements of interlayer spacings were used to assess the effects of ion-exchange and dehydration upon the mineral structure. The most significant findings are: (1) Under conditions which greatly favor ion-exchange sorption mechanisms, uranyl retains a symmetric local structure suggestive of an outer-sphere complex, with a preferred orientation of the uranyl axis parallel to the mineral layers; (2) Upon dehydration, the ionexchange complexes adopt a less symmetric structure, consistent with an inner-sphere complex, with less pronounced orientation of the uranyl axis; and (3) For conditions which favor sorption at surface hydroxyl sites, uranyl has a highly distorted equatorial shell, indicative of stronger equatorial ligation, and the detection of a neighboring U atom suggests the formation of surface precipitates and/or oligomeric complexes.
Quantification and Characterization of Maghemite in Soils Derived from Volcanic Rocks in Southern Brazil
Authors: da Costa Antonio Carlos S. , Bigham Jerry M. , Rhoton Fred E. , Traina Samuel J. 
Published: August 2006

AbstractMany soils developed from volcanic rocks in southern Brazil exhibit spontaneous magnetization caused by the presence of fine-grained maghemite (γ-Fe2O3), but few attempts were made to quantify or characterize this important soil component. To that end, clays were separated from freely drained soils derived from acid (≥63% SiO2), intermediate (54–62% SiO2), and basic (≤53% SiO2) igneous rocks produced by the Paraná flood volcanism. The sample set included soils with a wide range of pedogenic development on different landscape positions. The Fe oxide mineralogy of these samples was examined by using a combination of selective dissolution, magnetic susceptibility, and X-ray diffraction (XRD) techniques. Hematite and maghemite were the primary Fe oxides in mature soils (Oxisols, Ultisols, and Alfisols) developed from basic rocks; whereas goethite was dominant in all other soils, especially those formed from acid-intermediate rocks. The association of maghemite with basic rock materials suggests that it was primarily formed by oxidation of lithogenic magnetite. A strong, positive correlation (R2 = 0.89) was obtained between mass specific magnetic susceptibility (χ) of the clay fractions and maghemite contents estimated by XRD. Either method could be used for quantitative analyses, but χ was more sensitive than XRD at low maghemite concentrations (<2 wt. %). The clay-sized maghem-ites were superparamagnetic with an estimated value for the mass specific magnetic susceptibility (χlf) value of 91,000 × 10−8 m3 kg−1 and frequency dependent variations of 10–15%. The maghemites also had low unit cell constants, which, if attributed entirely to replacement of Fe by Al, would correlate with Al substitutions in the range of 5–16 mole %. Selective dissolution of the soil maghemites was achieved by treatment of Fe oxide concentrates with 1.8 M H2SO4 at 75°C for 2 h.
Spectroscopy Study of Arsenite [As(III)] Oxidation on Mn-Substituted Goethite
Authors: Sun Xiaohua , Doner Harvey E. , Zavarin Mavrik 
Published: August 2006

AbstractMn-substituted goethite was synthesized and the interaction between arsenite (As(III)) and Mn-substituted goethite was investigated by both solution chemistry and X-ray adsorption near edge structure (XANES) spectroscopy. Results indicate that the oxidation of As(III) is favored by Mn-substituted goethite. This reaction was more sensitive to temperature than to pH. Different reaction mechanisms may account for As(III) oxidation. Since As(III) is more mobile and toxic than As(V), the oxidation reaction of As(III) with Mn-substituted goethite may decrease arsenic toxicity under some conditions.
Refinement of the Kaolinite Structure From Single-Crystal Synchrotron Data
Authors: Neder R. B. , Burghammer M. , Grasl TH. , Schulz H. , Bram A. , Fiedler S. 
Published: August 2006

AbstractThe crystal structure of single crystals of kaolinite from Keokuk, Iowa, was refined using data measured at the microfocus X-ray beamline at the ESRF, Grenoble, France (λ = 0.6883, T = room temperature). The volume of the crystals was 8 and 0.8 μm3, respectively. Unit-cell parameters are: a = 5.154(9) Å, b = 8.942(4) Å, c = 7.401(10) Å, α = 91.69(9)°, β = 104.61(5)°, γ = 89.82(4)°. Space group Cl is consistent with the observed data. All non-hydrogen atoms were independently refined with anisotropic displacement parameters. The positions and isotropic displacement parameters for the three interlayer H atoms were refined also. The position of the intralayer H was found by difference-Fourier methods, although refinement was not possible. Difference-Fourier maps suggested large anisotropic displacement vectors of this intralayer H, however, no evidence for a second maximum was found. The diffraction patterns show diffuse scattering in streaks parallel to [001]* through hkl reflections with hk ≠ 0, which is caused by stacking faults. No twinning was observed for either of the two crystals.
Determination of Illite-Smectite Structures using Multispecimen X-Ray Diffraction Profile Fitting
Authors: Sakharov Boris A. , Lindgreen Holger , Salyn Alfred , Drits Victor A. 
Published: August 2006

AbstractA procedure for structural investigations by X-ray diffraction of mixed-layer structures incorporating swelling layers has been developed. For each sample, specimens saturated with different cations (Na, Mg, and Ca), are analyzed both as air-dried and as glycolated. One structural model fitting all the observed patterns then provides the structure of the sample. Samples tested include: Mite-smectite (I-S) minerals from Kazachstan (a rectorite), Dolna Ves in Slovakia, Kinnekulle in Sweden, the North Sea, and Scania in Sweden. The fitting of the patterns of the Kazachstan rectorite demonstrated that the instrumental parameters applied in the modeling were correct. For the I-S minerals from Slovakia and Kinnekulle the observed patterns were fitted with one two-component I-S model. However, the Ca-saturated and air-dried specimen of the Kinnekulle bentonites had two types of swelling interlayers. For the Slovakian I-S with Reichweite = 2, an alternative two-phase I-S plus I–V (V = vermiculite) model fitted the experimental X-ray diffraction patterns equally well. The I-S mineral from Scania is in fact a three-component I-T-S (T = tobelite) and the North Sea sample is a four-component I-S-V-V, one type of the swelling layers having swelling characteristics intermediately between smectite and vermiculite. In addition to layer types and distribution, interlayer compositions, such as the amount of interlayer glycol and water and of fixed and exchangeable cations, were determined.
Dehydroxylation Behavior of Heat-Treated and Steam-Treated Homoionic cis-Vacant Montmorillonites
Authors: Emmerich Katja , Madsen Fritz Thule , Kahr Guenter 
Published: August 2006

AbstractLi+, Na+, Ca2+, Sr2+, Cu2+, or Zn2+-saturated samples of a cis-vacant montmorillonite from Linden, Bavaria, were heated to temperatures between 200–700°C. Half of each heated sample was subsequently autoelaved under steam at 200°C (∼1.5 MPa) to promote rehydroxylation. The smectites were characterized by cation-exchange capacity (CEC), determination of exchangeable cations, infrared (IR) spectroscopy, and thermoanalytical investigations of evolved water in a thermobalance linked with a mass spectrometer.Changes in the montmorillonite structure and dehydroxylation behavior are related to three respective mechanisms: type of the interlayer cation, interlayer cation radius, and the movement of the interlayer cation. The migration of the smaller Li+, Cu2+, and Zn2+ ions after heating produces a strong reduction of CEC due to the Hofmann-Klemen effect before the initiation of dehydroxylation. Thereafter, the CEC of these smectites remains constant over a large temperature interval during dehydroxylation. After rehydroxylation, Cu2+ and Zn2+-rich samples release 16–23 meq/100 g of Mg2+ from the structure. No Mg2+ release is observed for the Li+-rich montmorillonite. Also the dehydroxylation behavior after rehydroxylation differs between the Cu2+, Zn2+, and Li+-rich samples. The mass curves of the evolved water during thermoanalysis of the rehydroxylated Cu2+ and Zn2+-rich smectites show a peak doublet between 480–700°C. For the Li+, Na+, Ca2+, and Sr2+-rich montmorillonites, the second peak disappeared and a third peak at ∼760°C developed after rehydroxylation. The resulting structure after rehydroxylation of all samples is celadonite-like.
Layer Charge Influences on the Hydration of Expandable 2:1 Phyllosilicates
Authors: Laird David A. 
Published: August 2006

AbstractThe objective of this study was to investigate the influence of layer charge on the hydration of Mg-saturated expandable 2:1 phyllosilicates. Water retained by 12 Mg-saturated clays at 54% relative humidity was quantified gravimetrically. X-ray diffraction and total chemical analysis were used to determine the hydratable surface area (447–759 m2g−1) and layer charge [0.327–0.754 electrons per formula unit (e f.u.−1)] of each sample. Water retained by the clays increased with both hydratable surface area and layer charge of the clays. However, the increase in H2O content with layer charge occurred only on external surfaces of the clays. This result suggests that the H2O on external surfaces is localized around the cation/charge sites rather than forming multi-layers as was suggested previously. A model is proposed for the hydration of expandable 2:1 phyllosilicates. The model assumes that interlayer volume controls interlayer hydration and that the number of cation/charge sites on external surfaces controls hydration of external surfaces.
Swelling of Formamide-Montmorillonite Complexes in Polar Liquids
Authors: Onikata Masanobu , Kondo Mitsuji , Yamanaka Shoji 
Published: August 2006

AbstractA new osmotic-swelling system for montmorillonite with formamide (FA) is described. Water and a variety of polar organic liquids were used to swell FA-montmorillonite complexes. The post-swelling behavior of the complex is interpreted in terms of the bi-functionality of FA as an electron donor/acceptor and the magnitude of the donor number (DN) of the polar liquid relative to that of FA. The FA-montmorillonite complex shows limited swelling of d(001) <2.3 nm for polar liquids with DNs larger than that of FA. In contrast, the FA-montmorillonite complex shows osmotic swelling when the DN of the polar liquid is smaller than that of FA.
Direct Imaging of Zirconia Pillars in Montmorillonite by Analytical Electron Microscopy
Authors: Crozier P. A. , Pan M. , Bateman C. , Alcaraz J. J. , Holmgren J. S. 
Published: August 2006

AbstractAnalytical electron microscopy was used to confirm the location of pillars of zirconia in pillared montmorillonite. Data show that the pillared clay is of “high” quality, with surface areas ranging from 200 to 250 m2/g and (001) spacings in the 17–18 Å range. The zirconia-rich pillars were observed using bright-field imaging, annular dark-field imaging, and energy-filtered imaging. The composition of the pillars was confirmed by performing nano-analysis using energy-dispersive X-ray spectroscopy and electron energy-loss spectroscopy. The pillars apparently have an irregular shape <50 Å in size. The shape and relatively large size of the pillars suggest that zirconia dispersion is not ideally distributed in this sample. This study is apparently the first report of electron microscopy observation of pillaring material in clays.
Effect of Illite Particle Shape on Cesium Sorption
Authors: Rajec Pavol , Šucha Vladimír , Eberl Dennis D. , Środoń Jan , Elsass Françoise 
Published: August 2006

AbstractSamples containing illite and illite-smectite, having different crystal shapes (plates, “barrels”, and filaments), were selected for sorption experiments with cesium. There is a positive correlation between total surface area and Cs-sorption capacity, but no correlation between total surface area and the distribution coefficient, Kd. Generally Kd increases with the edge surface area, although “hairy” (filamentous) illite does not fit this pattern, possibly because elongation of crystals along one axis reduces the number of specific sorption sites.
Nuclear Magnetic Resonance (NMR) Study of Cd2+ Sorption on Montmorillonite
Authors: Di Leo Paola , O'Brien Paul 
Published: August 2006

Abstract113Cd solid-state nuclear magnetic resonance (NMR) was used to identify possible Cd2+ adsorption sites in montmorillonite. The montmorillonite was treated with 0.1 and 1 M CdCl2 aqueous solutions and samples with 13 and 8-µm particle size were used. The data are consistent with a two-site model for sorption of Cd2+ on montmorillonite. Cd2+ is localized in the montmorillonite in two different sites: 1) in the interlayers as hydrated Cd2+ and 2) on the external surface, probably with few H2O molecules hydrating to it. Cadmium is also adsorbed as CdCl+ in the interlayer. Treatment with a 0.1 M CdCl2 solution produces adsorption of free Cd2+ in the interlayer whereas treatment with 1 M CdCl2 resulted in adsorption of Cd2+ in both the interlayer and on surface sites and the adsorption of CdCl+ in the interlayer. A larger particle size favors Cd2+ adsorption on the external surface whereas a smaller particle size favors Cd2+ adsorption in the interlayer.
First Occurrence of a Stacking Sequence Including (±60°, 180°) Rotations in Mg-Rich Annite
Authors: Kogure Toshihiro , Nespolo Massimo 
Published: August 2006

AbstractTransmission electron microscopy (TEM) observation shows narrow regions in a Ti-containing Mg-rich annite of composition (K0.90Na0.02)(Mg0.72Fe2+1.78Mn0.03Ti0.27Al0.05)(Si2.77Al1.23)O10(OH,F)2from a granitic rock, where the ±60° and 180° stacking angles occur extensively. These regions are a few hundreds of nanometers thick along the [001]* direction and are within 1Mor 2M1annite. The stacking sequence in one of these regions was determined by two atomic-resolution images recorded along [1̄10] and [010] of the same crystal. Stacking sequences with ± 120° or 180° rotations are dominant, although those with ±60° rotations occur also. Locally 2Oand more complex sequences exist. Compositional analysis by TEM indicated no difference in the chemical compositions between these regions and the adjacent ones with regular 1Mor 2M1stacking sequence. The origin of these unusual stacking sequences in annite is discussed.
Preparation of Kaolinite-Amino Acid Intercalates Derived from Hydrated Kaolinite
Authors: Sato Makoto 
Published: August 2006

AbstractIntercalation of amino acids into 10.0-Å hydrated kaolinite was studied by powder X-ray diffraction (XRD), differential thermal analysis-thermal gravimetry (DTA-TG), and infrared (IR) spectroscopy. Intercalation was found to be dependent on the chain-length, pH, and the concentration of the amino acid zwitterion. Near the isoelectric point, fully intercalated phases were obtained in solutions of concentration >0.5–1 M for glycine (Gly), 2–3 M for β-alanine (β-Ala), and 12 M for both γ-aminobutyric acid (γ-Aba) and δ-aminovaleric acid (δ-Ava). ∊-aminocaproic acid (∊-Aca) with a long chain (C = 6) was only partially intercalated. Intercalated amino acid formed a mono-molecular arrangement with the alkyl chain tilting toward the layer at an angle related to H2O content. The compositions of the intercalates of the Gly and β-Ala are Al2Si2O5(OH)4·(Gly)0.67·0.24H2O and Al2Si2O5(OH)4·(β-Ala)0.63·0.25H2O, respectively, based on TG data. From IR data, Gly and β-Ala molecules are found intercalated as zwitterions and these molecules form hydrogen bonds with both the Al-OH and Si-O surfaces of kaolinite. Washing the intercalate with water produced a hydrated kaolinite, which may form a second amino-acid intercalate of high order. Thus, hydrated kaolinite intercalates or deintercalates amino acids depending on concentration and conditions.