Diagenesis of Clay Minerals from Lower Cretaceous Shales of North Eastern British Columbia
Authors: Foscolos A. E. , Kodama H. 
Published: September 2006

AbstractClay minerals from shale outcrops of the Lower Cretaceous Buckinghorse Formation (4250 ft thick) were investigated in order to assess their degree of diagenesis and their oil-generating potential. Crystallinity index, sharpness ratio, per cent of illite which is the 2M polymorph and presence of discrete minerals have been studied in the whole clay fraction, while the very fine clay fraction has been subjected to X-ray diffraction, differential thermal, thermogravimetric, differential thermogravimetric, i.r. spectroscopy, surface area and chemical analyses. With information derived from these studies and from published data, a classification scheme was devised which relates variation of clay mineralogy to diagenetic stages and burial depth.Data on the < 2 μm size fraction show that the crystallinity index decreases while the sharpness ratio and per cent of illite which is the 2M polymorph increase with burial depth. Results on the <0·08 μm fraction reveal that a three-component interstratified clay mineral exists. In addition, Fourier transform calculations and chemical and physicochemical analyses indicate that both the ratio of the amounts of non-hydrated clays (illite) to hydrated clays and the K2O content of clays increase with burial depth; cation exchange capacity and surface area decrease with burial depth.Based upon a classification scheme, which was devised by combining criteria and data derived from the studies of Weaver (1961a), Kubier (1966), Burst (1969) and Dunoyer de Seconzac (1970), the upper and middle parts of the formation (upper 3250 ft) fall within the middle stage of diagenesis whereas the lower part (1000 ft) is allocated to the beginning of late diagenesis. In terms of Burst’s (1969) work, the upper 3250 ft are transitional between the stability and dehydration zones indicating that, prior to uplift, hydrocarbons may have been in the process of migration. The lower 10000 ft of the formation are in the restricted dehydration zone, indicating that hydrocarbon migration should have been completed.
Comparative Studies on Extraction of Sediment Interstitial Waters: Discussion and Comment on the Current State of Interstitial Water Studies
Authors: Manheim F. T. 
Published: September 2006

AbstractThe implication by Murthy and Ferrell (1972) that interstitial water studies are in a confused state is criticized on the basis that the authors have not drawn on a considerable body of data, especially Soviet studies since the 1950’s, and results of the Deep Sea Drilling Project. Pressure filtration systems for extracting interstitial waters are currently the methods of choice for marine studies and have achieved substantial reliability and reproducibility. Although gaps and problems remain, many aspects of interstitial composition of marine sediments have been clarified; these include the substantial constancy of composition of interstitial waters in deep sea pelagic deposits, depletion of interstitial cations owing to authigenic mineral formation in more rapidly accumulated (especially terrigenous) sediments, and special phenomena in sediments overlying salt deposits.
Effect of Oxidation and Reduction on Potassium Exchange of Biotite
Authors: Ross G. J. , Rich C. I. 
Published: September 2006

AbstractThe selectivity of K over Ca of Amelia biotite increased sharply upon oxidation by H2O2 at pH 6·0. This increase in K selectivity was only partially reversible upon reduction by Na2S2O4. Oxidation by H2O2 of the Ca-form of this biotite resulted in a loss of no more than 2·8 and 0·4 per cent of the total Fe and Al, respectively, and caused a small and perhaps insignificant decrease in layer charge. Although 95 per cent of the structural Fe2+ of the Ca-form of this biotite was ozidized by H2O2, only 17 per cent was reduced again by four treatments with Na2S2O4.The evidence indicates that under the conditions of this experiment the loss of protons from structural hydroxyls was the dominant mechanism by which electroneutrality in the biotite was maintained during oxidation of structural Fe2+. Because this mechanism increases the bond strength of interlayer K, it explains the increased K selectivity of biotite upon H2O2 oxidation. The relatively small reduction by Na2S2O4 of structural Fe3+ to Fe2+, which implies an equally small reprotonation of structural hydroxyls, explains the incomplete reversibility of K selectivity by Na2S2O4 treatment.
Quantitative Clay Petrology: The Trees but Not the Forest?
Authors: Towe Kenneth M. 
Published: September 2006

AbstractGravitational settling and centrifuge techniques have been criticized in the preparation of X-ray specimen mounts for quantitative clay petrology because of the marked mineral segregations that can occur. Although the same factors can operate to produce error in the separation of the traditional less-than-2-μm fraction, this potentially more important source of bias is seldom taken into consideration. A fair representation of the bulk sample deserves at least as much attention as a representative X-ray mount. The most accurate and precise X-ray analyses may be geologically misleading or meaningless otherwise and translate as exercises in precision for its own sake.
The Heterogeneity of the Charge Density in Montmorillonites
Authors: Stul M. S. , Mortier W. J. 
Published: September 2006

AbstractThe heterogeneity of the interlayer cation density and the corresponding mean layer charge density due to isomorphous substitution have been determined for six montmorillonite samples. This has been achieved by considering the transition of a monolayer to a double layer complex with alkylammonium ions. The transition is related to the interlayer cation density, together with the variation of the apparent spacings, which in turn is related to the composition of this two-component mixture.All the samples showed a heterogeneous interlayer cation distribution and a differing mean charge density.
Fabric-Property Relationships in fine Granular Materials
Authors: Mahmood Arshud , Mitchell James K. 
Published: September 2006

AbstractIn this investigation fabric-property relationships were studied in a silty fine sand sized crushed basalt—an artificial ‘soil’ that has previously been used to simulate lunar soil. The fabric was characterized by measuring preferred orientations of grains, and pore size distribution was determined by mercury intrusion porosimetry. When deposited by pouring, the grains acquired strong preferred orientations in the horizontal direction and formed pores between 1 and 30 μm dia. Densification by static or dynamic compaction resulted in near random grain arrangement and pore sizes between 0·1 and 10 μm dia.Strength in direct shear and one-dimensional compressibility with the associated lateral stresses were measured. The strength was up to 30 per cent higher when the sample was sheared normal to the preferred orientation of grains than when the shearing was parallel to the orientation direction. This is to be expected, as shearing across the preferentially oriented grains should involve breakage or reorientation of many grains. At a given initial void ratio the compressibility of statically compacted specimens was larger (up to 30 per cent higher axial strain) than that of dynamically compacted specimens at very low stresses. At higher stresses both samples exhibited equal compressibility, suggesting that the grains become more randomly arranged at low void ratios (comparing samples of equal initial void ratios).
Adsorption and Transformation of HCN on the Surface of Copper and Calcium Montmorillonite
Authors: Cruz M. , Kaiser A. , Rouxhet P. G. , Fripiat J. J. 
Published: September 2006

AbstractAdsorption isotherms of HCN by Cu- and Ca-montmorillonites show that water present in the interlayer space decreases HCN adsorption.For Ca-montmorillonite, i.r. spectra permit distinguishing between HCN interacting with the cations and molecules filling the interlayer space. Both types are removed upon outgassing. The residual water is not displaced by HCN.On Cu-montmorillonite, species (presumably CN− ions) strongly held by the cations are observed in addition to adsorbed HCN molecules. The residual hydroxyls retained in the interlayer space are removed by the adsorption of HCN. These hydroxyls, either OH− or H2O, are characterized by two well defined stretching bands.Infra-red spectra of samples heated below 200°C show that adsorbed HCN is involved in chemical reactions. For both clays, bands appear in the region characteristic of carbonyl and carboxyl groups; the production of ammonium is detected for Cu-montmorillonite. The reactions and the observed spectral features could be accounted for by the formation of formamide.
Aqueous Dissolution Studies of Illite Under Ambient Conditions
Authors: Reesman A. L. 
Published: September 2006

AbstractDissolution data on five of the six illites reported by Reesman and Keller (1968) indicate that these illites are more stable than was previously thought. The revised Gibbs free energies of formation (ΔGf0) with respect to the ‘ideal’ illite formula and the muscovite formula areUse of muscovite formula as an indirect comparator provides a means of predicting the relative stabilities of these chemically complex materials.The response of illite-equilibrated solution to a kaolin ΔGf0 was found in all samples in which a 7 Å mineral phase was detected by X-ray diffraction. Stability diagrams based upon the ΔGf0 with respect to ideal muscovite and kaolin formulas show a rather wide range in chemical conditions through which illites and kaolin minerals with differing ΔGf0 would be stable. However, in carbonate rocks and sea water illite is stable relative to kaolin. During the weathering of carbonates the lower pH zones in the clay-rich residuum above the carbonates favor the transformation of illite to kaolin minerals.
A Golden-Colored, Ferri-Nickel Chloritic Mineral from Morro do Niquel, Minas Gerais, Brazil
Authors: Brindley G. W. , de Souza Jefferson Vieira 
Published: September 2006

AbstractA golden-colored, flaky mineral from Morro do Niquel, Minas Gerais, Brazil, gives an X-ray diffraction pattern of a IIb chlorite polytype, with basal spacing 14·21 ± 0·02 Å and b = 9·23 Å. Thermogravimetric analysis shows a progressive weight (water) loss up to 500°C, followed by a rapid weight loss corresponding to dehydroxylation of the interlayer material and a slower weight loss due to dehydroxylation of the 2:1 layer. The structural formula derived from the chemical analysis on the basis of O10 (OH)8, or total cation valence of +28, shows 5·3 total octahedral cations, i.e. probably 2·3 in the interlayers where normally 3 cations are found. This deficiency together with the appreciable loss of water below 500°C suggests a partially vermiculitized interlayer. A new method for deriving the interlayer composition gives R1·67(OH)4·08(H2O)0·59, and a ratio (OH + H2O)/R = 2·80, which approaches that of a dioctahedral interlayer and is consistent with a predominance of R3+ ions. The mineral may resemble the golden, vermiculitized biotite described by Walker and others.
Fabric of Consolidated Kaolinite
Authors: Martin R. Torrence , Ladd Charles C. 
Published: September 2006

AbstractFabric refers to the spacial arrangement of clay particles in a sample relative to a reference plane. X-ray diffraction data yield an ‘amount of orientation’ (AO) that varies from zero for ideal random to 100 for ideally oriented fabric. The AO has been related to the average angle of inclination of clay particles to the reference plane.Fabric data from 50 samples involving 2000 determinations are presented on the effects of: the method of sample preparation prior to one-dimensional consolidation; the magnitude of consolidation stress from 0·1 to over 1000 kg/cm2; changes in direction of consolidation stress; isotropic consolidation; and disturbance during removal of samples from oedometer cells. The single most important variable was the method of sample preparation, as illustrated by the following data on samples consolidated one-dimensionally to 1·5 kg/cm2:clay initially moist, AO = 27 per cent; air-dry clay, AO = 44 per cent; clay slurries, AO = 76–95 per cent. The change in fabric with increasing consolidation stress was most pronounced with samples at very low stresses, the changes in fabric were small for consolidation stress increments usually encountered in engineering practice.Fabric data provide a very sensitive measure of sample disturbance. Extrusion causes significant disturbance at the center of a 24cm dia, sample cylinder.
The Formation of Hematite from Amorphous Iron(III)Hydroxide
Authors: Fischer W. R. , Schwertmann U. 
Published: September 2006

AbstractThe formation of hematite from amorphous Fe(III)hydroxide in aqueous systems at pH 6 and 70°C, both with and without oxalate, was followed by kinetic measurements, electron microscopy, i.r. spectroscopy and thermal analysis.In the absence of oxalate, small amorphous particles coalesce into aggregates which eventually become single crystals of hematite. When oxalate is present, crystal growth is much faster and does not proceed through the intermediate stage of aggregation. Aggregates, when formed, consist of groups of single crystals. It is suggested that oxalate accelerates the nucleation of hematite crystals by acting as a template, the Fe-Fe distance in Fe-oxalate ions being similar to that in hematite.
Clay Distributions in Recent Estuarine Sediments
Authors: Edzwald James K. , O’Melia Charles R. 
Published: September 2006

AbstractThe distribution of clay minerals in Recent sediments can be explained by the relative stability of the clays. The rates of particle aggregation for three clays were determined in the laboratory in synthetic estuarine solutions; from the kinetic studies stability values were calculated. The results indicate that illite is more stable than kaolinite which is more stable than montmorillonite. The distribution of the clays in the Pamlico River Estuary can be explained on the basis of relative clay stability where kaolinite which aggregates rapidly (relatively unstable clay) is found upstream of illite.
Adsorption of Ethylenediamine (EDA) on Montmorillonite Saturated with Different Cations—III. Na-, K- and Li-Montmorillonite: Ion-Exchange, Protonation, Co-Ordination and Hydrogen-Bonding
Authors: Laura R. D. , Cloos P. 
Published: September 2006

AbstractEthylenediamine (EDA) is adsorbed from aqueous solution on Na-, K- and Li-montmorillonite as the monoprotonated cation (EDAH+) through an ion-exchange process. On washing with distilled water the second amine function is protonated—probably through dissociation of water near the clay surface—and simultaneously formed alkali hydroxide is removed.In air-dried clay films, prepared from unwashed suspensions, EDA is retained mainly through hydrogen-bonding with water co-ordinated to the exchangeable cation.EDA adsorbed from the vapour phase is retained through co-ordination, either direct or indirect (i.e. through a ‘water-bridge’), depending on the hydration properties of the exchangeable cation. Indirect coordination increases the stability of the amino-clay complex against atmospheric humidity and heating in vacuum in the order K+ < Na+ < Li+.Upon heating co-ordinated EDA is almost completely desorbed, whereas EDAH+ and EDAH22+ decompose above 160°C to form NH4+.
Nickel Containing Regularly Interstratified Chlorite-Saponite from Szklary, Lower Silesia, Poland
Authors: Wiewióra Andrzej , Szpila Kazimierz 
Published: September 2006

AbstractThe present paper describes a new mineral species, namely a regularly interstratified chlorite —trioctahedral smectite bearing as much as 24% NiO. The high Ni content proves it to be nickel mineral.On the diffractogram of the raw sample, an integral series of reflections with l.d(001) = 30·1 Å was obtained. To study the nature of the component layers, X-ray examinations of glycerol saturated samples and also dehydrated by heating were accomplished. Thermal and chemical analyses were performed in the usual way.The crystallochemical formula can be presented as follows: saponite layer—(Mg,Ni)3·00 (Si3·75Al0·25) O10(OH)2, charge −0·25; Ca0·06 (Mg,Ni)0·06 K0·01, 4·07 H2O, charge +0·25; chlorite layer—(Mg, Ni)2·02(Al,Fe*)0·65(Si3·76Al0·24) O10(OH)2, charge −0·25; (Mg,Ni)2·75 (Al,Fe3+)0.25 (OH)6, charge +0.25.The full mineral and chemical characteristics lead to precise conclusions concerning the composition and structure not only of the nonexpanding chlorite layers, but especially of the expanding layers. The latter show the chemical composition of saponite but the interlayer material is composed partly of exchange cations and molecular water and partly of “brucite-like pillows”.
Perturbation of Structural Fe3+ in Smectites by Exchange Ions
Authors: McBride M. B. , Pinnavaia T. J. , Mortland M. M. 
Published: September 2006

AbstractThe electron spin resonance of some structural Fe3+ for montmorillonites having low Fe3+ content, is perturbed by electrostatic interaction between exchange cations and structural charge sites. The position of charge centers of organic and inorganic cations in the interlayer can thus be determined at various levels of solvation. Dielectric media between the silicate layers lower the electrostatic attraction between the silicate and the exchange cations. The silicate charge appears to be partially delocalized on structural oxygen atoms as shown by electron spin resonance and i.r. spectroscopy. There is also evidence that divalent exchange cations on dehydrated montmorillonites cause hydrolysis of water; the protons so produced migrate to structural charge sites.
Halloysite-Kaolinite Transformation at Room Temperature
Authors: La Iglesia A. , Galan E. 
Published: September 2006

AbstractHalloysite (metahalloysite) of various particle sizes has been altered with oxalic and EDTA acids, at room temperature and during different periods of time (5–90 days). The oxalic acid attack at first achieved only a recrystallization of halloysite. The recrystallization is much more significant the smaller the size of the treated halloysite particles. Later the material is destroyed. The EDTA treatment also has provoked during the first days a recrystallization of the halloysitic material which is destroyed again after about 20–25 days. Later kaolinite is formed. The kinetic curve of kaolinite formation is symmetrical with respect to that corresponding to the diminution of amorphous material in the sample. The influence of the halloysite particle size and the complexing effect of the acids in relation to the resulting products are discussed.
Structural Hydroxyls in Sepiolites
Authors: Ahlrichs J. L. , Serna C. , Serratosa J. M. 
Published: September 2006

AbstractThree sepiolite clays studied showed evidence for the presence of structural hydroxyl groups in three to five different environments depending on the composition of the clay. A 3720 cm−1 i.r. frequency is shown to be characteristic of SiOH at crystal edges which are very abundant in sepiolites. This band has not been seen by most workers because the Nujol, fluorolube or KBr used in sample preparation perturb it sufficiently to obscure it under other OH stretching bands. The 3680 cm−1 band is confirmed as being from the (Mg)3OH and evidence of a very small band near 3640 cm−1 is suggested to arise from limited trioctahedral substitution. The very crystalline Ampandrandava sepiolite shows only the above three bands. The intermediately crystalline Vallecas shows a 3620 cm−1 band in addition which is characteristic of dioctahedral systems and is due to either some vacancy sites or to the presence of attapulgite. This dioctahedral band is greater in the less crystalline Salinelles sepiolite; in addition, it has a smaller 3585 cm−1 band. Mg-Al-vacancy and Mg-Fe‴-vacancy are suggested as the source of the 3620 cm−1 and 3585 cm−1 bands.
Electrical Conductivity of Na—Montmorillonite Suspensions
Authors: Shainberg I. , Levy Rachel 
Published: September 2006

AbstractThe electrical conductivity of Na-montmorillonite suspensions in various salt and clay concentrations was measured. The weight conductance of the clay suspension was found to decrease with increase in clay concentration between 0 and approximately 0·5 g clay/100 ml, then rose to a plateau at 6–10 g clay/100 ml. The weight conductance of the clay suspensions also increased with an increase in the salt solution concentration. If the model of two resistors in parallel is used in interpreting the experimental data, these changes can be attributed to an increase in the mobility of the adsorbed Na ions. It is proposed that the two resistors in series model is more realistic in describing the conductivity of the suspensions. This model predicts the observed weight conductance changes of the suspensions, while the mobility of the adsorbed ions remains constant. A constant mobility of the adsorbed Na ions in clay-water systems of low to medium salt and clay concentrations also is predicted by the diffuse double layer.
Od-Interpretation of Kaolinite-Type Structures—I: Symmetry of Kaolinite Packets and Their Stacking Possibilities
Authors: Dornberger-Schiff K. , Ďurovič S. 
Published: September 2006

AbstractThe idealized symmetry of kaolinite-type minerals (1:1 phyllosilicates) is analysed in detail. They can be considered as OD-structures consisting of three kinds of OD-layers. Each of them, taken separately, possesses higher symmetry than their combination. This explains the well-known tendency of kaolinite-type minerals to form a wide variety of ordered and disordered polytypes as well as twins. The possible stacking sequences result from the different kinds of pairs of kaolinite layers which are derived for dioctahedral, trioctahedral as well as ‘monoctahedral’ kaolinite-type minerals, the latter being defined as those in which the three octahedral positions are occupied by three different cations or two different cations and a void. The analysis makes use of a simple symbolism and a simplified pictorial representation.A brief summary of the most important terms and definitions of the theory of OD-structures is given in an Appendix.