Chromite and chrome spinel occurrences from metacarbonates of the Oetztal–Stubai Complex (Northern Tyrol, Austria)
Authors: Mogessie A. , Purtscheller F. , Tessadri R. 
Published: December 2006

AbstractChromite inclusions in uvarovite-chrome garnet, chemically zoned chromite-chrome spinel and chrome spinel-olivine pairs from metacarbonates of the Oetztal-Stubai Complex (northern Tyrol, Austria) are described in terms of their textural occurrences and chemical compositions. Their genetic relationship in relation to the polymetamorphism of the region is discussed.
Phase relations in the system anorthite–potassium-feldspar at 10 kbar with emphasis on their solid solutions
Authors: Ai Y. , Green D. H. 
Published: December 2006

AbstractPhase relations in the binary system anorthite-K-feldspar at 10 kbar were studied with a solid-media piston cylinder apparatus. The eutectic character of this system is confirmed, with the eutectic point located at An30Kf70 (± 3 mol%), and 1215 ± 15°C, 10 kbar. The mutual solubilities between anorthite and K-feldspar at the solidus are greatly increased at 10kbar compared with those at 1 atm. The maximum solubility of K-feldspar in anorthite is c. 5% at 1 atm, c. 18% at 10 kbar; and that of anorthite in K-feldspar is c. 3% at 1 atm, c. 7% at 10 kbar. The increased solubilities are attributed to the increase in the eutectic temperature at high isostatic pressures. The results imply increased ternary feldspar solid solutions at high pressures and support the existence of homogeneous feldspars with extensive ternary composition under high-P, T and anhydrous conditions.
Curvature of gypsum crystals induced by growth in the presence of impurities
Authors: Rinaudo Caterina , Franchini-Angela Marinella , Boistelle Roland 
Published: December 2006

AbstractGypsum crystals were grown at 25, 35, and 45 °C from solutions containing different ionic impurities (Mg2+, Na+, Cd2+). Curved gypsum crystals formed from the solutions enriched in magnesium or cadmium, whereas, in the presence of sodium, gypsum always grew undeformed. The mechanism of the curvature is described and an interpretation based on crystallographic considerations is given. Curvature is the result of impurity incorporation followed by crack formation and mechanical twinning which releases the internal stresses.
Genesis of the Pb–Zn deposit at Sant’Antonio di Val D’Aspra, Southern Tuscany (Italy): disparity between geo-petrographic data and fluid inclusion microthermometry
Authors: Giamello M. , Riccobono F. , Sabatini G. 
Published: December 2006

AbstractThe Pb–Zn deposit at Sant'Antonio di Val d'Aspra in the Farma Valley (Southern Tuscany) is hosted by Lower Moscovian carbonate rocks and shows many characters commonly found in Mississippi Valley type (MVT) deposits. Ore minerals (essentially sphalerite and galena) are closely confined to dolomitized portions of an only partly preserved black limestone. Mineralized carbonate rocks appear to have been eroded before the deposition of the overlying Upper Moscovian (Late Podolskian) shales. The diffuse presence of structures frequently found in internal sediments of karstic cavities indicates that supergene mechanisms have played an important role in the history of the deposit. A fluid inclusion study carried out on ore and gangue minerals revealed the presence of two different types of inclusions. The homogenization temperatures ranged from 120°C to 225°C but the most frequently found values were around 170°C. Salinity ranged from moderately low values up to 20 eq. wt. % NaCl. Lead isotopic composition rules out any relationship between the Sant'Antonio mineralization and Tertiary hydrothermal base metal occurrences in the same area. When all the data are taken together, a contrast is evident between geo-petrographic and isotopic data on the one hand, and fluid-inclusion microthermometry on the other.
The garnet-orthopyroxene Al barometer: problematic application to natural garnet lherzolite assemblages
Authors: Carswell D. A. 
Published: December 2006

AbstractThe garnet-orthopyroxene Al barometer specifically considers the Al content of orthopyroxene in equilibrium with garnet resulting from Mg-Tschermaks substitution. It is demonstrated that P-T calibrations of this barometer derived solely from experimental data for the MAS system, such as that favoured by Finnerty and Boyd (1984, 1987) based on the data of MacGregor (1974), cannot be expected to yield meaningful pressure estimates for natural garnet lherzolite assemblages. The presence of additional CaO, FeO and Cr2O3 components in natural garnet lherzolites can be expected to influence substantially the Al partitioning between orthopyroxene, garnet and/or spinel at any particular P and T. Thus a more comprehensive barometer formulation is required, such as the one provided by Nickel and Green (1985) that is based on experimental data for the CMAS and SMACCR systems with thermodynamic modelling and addition of an Fe correction term.It is further emphasised that for orthopyroxenes in natural garnet lherzolites the amount of Al introduced as Mg-Tschermaks substitution cannot be assessed simply as the total Al cation content since such orthopyroxenes frequently contain Al cations linked to Na substitution in M2 sites or to Cr, Ti and possibly Fe3+ in M1 sites. Revised algorithms for the calculation of specific orthopyroxene contents are presented. Application to analytical data sets for garnet lherzolite zenolith suites in the Thaba Putsoa and Mothae kimberlites generates revised upper mantle P-T arrays which refute the widely accepted advocacy by Finnerty and Boyd (1984, 1987) and Finnerty (1989) of an upper-mantle palaeogeotherm beneath northern Lesotho that is markedly inflected to a higher thermal gradient at the depths of derivation of the more chemically fertile, porphyroclastic textured, xenoliths.
Kegelite: infrared spectroscopy and a structural hypothesis
Authors: Braithwaite R. S. W. 
Published: December 2006

AbstractThe infrared spectrum of kegelite has been measured and is discussed. The infrared spectra of 1 : 1 molar mixtures of leadhillite with pyrophyllite or with muscovite resemble the spectrum of kegelite, the chemical formula of which is a 1 : 1 stoichiometric sum of those of pyrophyllite and of the leadhillite polymorphs. Kegelite is not a physical mixture of these species, but its structure may be an interlayering of phyllosilicate and leadhillite-like structures within the unit cell. The unit cell parameters of pyrophyllite-1Tc and the leadhillite polymorphs are compatible with each other and can be combined to give a cell with parameters close to those of the kegelite cell. A structural model for kegelite on these bases is suggested, which is also consistent with its thermal analysis. The formula of kegelite can be written as Pb8(SO4)2(CO3)4(OH)4(AlOH)4(Si4O10)2.
Fluid inclusion study of tin-mineralized greisens and quartz veins in the Penouta apogranite (Orense, Spain)
Authors: Mangas J. , Arribas A. 
Published: December 2006

AbstractThe Penouta deposit is associated with a small Hercynian apogranite stock that intrudes Precambrian-Cambrian gneisses of the Ollo de Sapo Formation. Tin ore occurs as disseminations of cassiterite in the apogranite and as greisenized zones and quartz veins which traverse both the alkaline leucogranite and the surrounding metamorphic country rocks.A fluid-inclusion study, utilizing microthermometric, crushing tests and Raman spectroscopic techniques on quartz from an intragranitic vein and a greisen of the host rock, indicates that the evolution of fluids was similar in both samples and occurred in the three main stages: The first stage is characterized by complex CO2 (CO2-N2-CH4-H2S) and complex CO2 aqueous (H2O-NaCl-CO2-N2-CH4-H2S) fluids of low salinity (Tm ice > −6°C), homogenization temperatures between 250 and 410°C homogenization pressures below 900 bars, and thermobarometric trapping conditions with temperatures below 700°C and pressures below 3250 bars. These fluids were probably responsible for the greisenization of the apogranite and wall rocks, and the precipitation of cassiterite. The second stage is represented by low-salinity aqueous solutions (H2O-NaCl) with Tm ice ⩾ −4.5°C, trapped at homogenization temperatures between 110 and 300 °C and homogenization pressures below 100 bars. This stage can be correlated with kaolinization. The third stage is characterized by higher salinity aqueous fluids (Tm ice ⩾ −16.5°C) containing Na+ and other cations, trapped at homogenization temperatures between 100 and 130°C and homogenization pressures below 5 bars. These fluids can be associated with the epigenetic or supergene phases of the orebody.
Coquandite, Sb6O8(SO4).H2O, a new mineral from Pereta, Tuscany, Italy, and two other localities
Authors: Sabelli C. , Orlandi P. , Vezzalini G. 
Published: December 2006

AbstractCoaquandite, a new antimony oxy-sulphate hydrate, occurs as spheroidal knobs of silky fibres or, rarely, as tiny transparent colourless lamellar crystals on stibnite at the Pereta mine, Tuscany, Italy; it is associated with klebelsbergite, peretaite, valentinite, sulfur, gypsum, stibiconite, and senarmontite. Coquandite is triclinic P1, with a 11.434(7), b 29.77(4), c 11.314(4) Å, α 91.07(7)°, β 119.24(3)° γ 92.82(1)° . It has a cell volume of 3352(5)Å3 with Z = 12 and a calculated density of 5.78 g cm−3. The crystals, elongated along [001] and flattened on {010}, display polysynthetic twinning with (010) as the twin plane. Optically, they are biaxial (+) with z ≈ c, 2V ≫ 60° n = 2.08(5). The strongest lines of the X-ray powder pattern are [d in Å, (I), (hkl)] 14.84(50)(020), 9.27(41)(111, 110), 6.81(67)130, 3.304(93)(090), 3.092(100)(330).Coquandite has also been found at the Cetine mine, Tuscany, Italy, and at the Lucky Knock mine, Tonasket, Okanogan County, Washington, USA. 22 microprobe chemical analyses (elemental microanalysis for H) gave Sb2O3 88.91, SO3 8.35, CaO 0.04, Na2O 0.03, H2O 1.43, total 98.76 wt.%, corresponding to the empirical formula (Sb + S = 7) Sb5.98Ca0.01Na0.01O7.96(SO4)1.02.0·78H2O, and to the idealised formula Sb6O8(SO4).H2O. The I.R. spectrum, which confirms the presence of water in the formula, is given.A partial structural arrangement is also given: the Sb polyhedra lie in nine layers perpendicular to [010] and form 'hexagonally' shaped groups surrounded by SO4 tetrahedra.
Sulphide mylonites from the Renström VMS deposit, Northern Sweden
Authors: Duckworth Rowena C. , Rickard David 
Published: December 2006

AbstractSulphide mylonites are fine-grained massive sulphides which have deformed in a plastic manner. In the Renström Zn-Pb-Cu-Ag-Au VMS deposit, one of several operating mines in the Early Proterozoic Skellefte District in Northern Sweden, shear-zone metamorphism has resulted in the development of mylonitic fabrics within the sulphides. The massive sulphide ore is hosted in a shallow submarine to subaerial volcano-sedimentary sequence which has been variably metamorphosed and deformed. Initially, the sequence underwent burial metamorphism which was followed by an amphibolite grade regional metamorphic event at pressures of around 7.5 kbar and temperatures of 540-600°C This has been overprinted by a retrogressive metamorphic event at greenschist facies (at ca. 400°C with concomitant ductile deformation. Finally the area was uplifted to shallower crustal levels with associated cataclastic deformation.Both the regional and dynamic metamorphic events have resulted in the development of specific textures in the sulphide ores. Textural evidence indicates that pressure solution has been mainly responsible for the plastic deformation in pyrite, while the weaker sulphide minerals such as pyrrhotite, chalcopyrite and galena have generally recrystallised in response to the high strains.Sulphide mylonites are probably common rocks in many polydeformed massive sulphide deposits like Renström. They may have previously been misinterpreted as primary depositional textures.
New mineralogical data on uranophane and β-uranophane; synthesis of uranophane
Authors: Cesbron Fabien , Ildefonse Philippe , Sichere Marie-Claude 
Published: December 2006

AbstractUranyl-silicates are widespread minerals in oxidised parts of various uranium deposits, and they frequently contain associations of the polymorphic forms of uranophane. In several recent works devoted to the study of uranium deposits as natural analogues of high-level nuclear waste repository (HLNWR), uranophane is frequently mentioned but without determination of the exact polymorphic species. The existence of two polymorphs presenting different stabilities has to be taken into account when considering the long-term behaviour of these minerals and the use of thermodynamic models for predicting the radionuclide migration in HLNWR. We present here new crystallographic data on betauranophane, and preliminary results of synthesis experiments of uranyl silicates. XRD patterns and calculated parameters of beta-uranophane from a Mexican U-deposit are presented. Synthesis experiments succeeded in crystallising uranophane (alpha form) at different pH, Si-, Ca- and Na activities, but beta-uranophane was never obtained. The controlling physico-chemical parameters responsible for the occurrence of these two polymorphic forms are still unknown.
Asbecasite: crystal structure refinement and crystal chemistry
Authors: Sacerdoti Michele , Parodi Gian Carlo , Mottana Annibale , Maras Adriana , Ventura Giancarlo Della 
Published: December 2006

AbstractThe crystal structure of antimonian asbecasite in an ejectum of hypabyssal origin occurring at Tre Croci near Vetralla, Vico volcanic complex, Roman potassic province, Latium, Italy, has been refined to R = 0.042, and is compared to the original crystal structure determination carried out on the Sb-free asbecasite of hydrothermal metamorphic origin from the type-locality, Cherbandung in Binna valley, Monte Leone nappe, Switzerland. New electron microprobe analyses of samples from both localities demonstrate crystal-chemical features that permit distinction between asbecasites from the two occurrences, so far the only known localities for this mineral.
Iowaite, a re-investigation
Authors: Braithwaite R. S. W. , Dunn P. J. , Pritchard R. G. , Paar W. H. 
Published: December 2006

AbstractIowaite has been re-examined using new, well crystallized material from the Palabora open pit mine, Transvaal. Microprobe, carbon analyser and thermal analyses, powder and single-crystal X-ray diffraction, infrared, UV-visible and mass spectroscopic and optical studies were made. The ideal formula is (OH)16Cl2·4H2O. It is trigonal, R3̄m, a = 3.1183(9), c = 24.113(8) Å, V = 203.1(2) Å3, Z = 3/8; Dobs 2.09 g/cm3.; Dcalc 2.04 g/cm3; hardness (Mohs)=2 1/2. The interlayer Cl− ions are displaced from the threefold axis. It is uniaxial negative, with ω = 1.561 ± 0.002, ε = 1.543 ± 0.002; coloured crystals are intensely pleochroic, due to intervalence charge transfer between the Fe3+ and Fe2+ substituting for Mg2+, with O pale yellow, E deep blue-green.
Phase relations in the system PbS-PbSe-PbTe
Authors: Liu H. , Chang L. L. Y. 
Published: December 2006

AbstractPhase relations in the system PbS-PbSe-PbTe were investigated in the temperature range between 1150 and 300°C. There is a complete solid solution series along the join PbS-PbSe, whereas miscibility gaps exist below ∼ 350°C and 805°C along joins PbSe-PbTe and PbS-PbTe, respectively. Both gaps extend into the ternary system, and the range of the gap between PbS and PbTe reduces in size with temperature as well as Se-content.By using the subregular model of mixing (Ganguly and Saxena, 1987), mixing energetics and activity composition relations of PbXwere derived. The temperature-dependence of the interaction parameters was calculated to be 5057.6 − 1.7T, 9605.2 − 4.4T, 3933.2 − 3.1T(T< 500°C), 6410.3 − 6.35T(T< 500°C) 1649 − 0.26T, 1594.6 − 0.2T, and 12906.3 − 17.3Tfor WWSte, WTeS, WSeTe, WTeSe, WSSe, WSeS, and WSSeTe, respectively. A critical temperature along the join PbS-PbSe at ∼ 100°C was obtained from interaction parameter calculation, which suggests the separation of the PbS-PbSe series.Correlation of solid-solution ranges established in this study with natural occurrences was made.
Wycheproofite: a new hydrated sodium aluminium zirconium phosphate from Wycheproof, Victoria, Australia, and a new occurrence of kosnarite
Authors: Birch William D. , Pring Allan , Bevan D. J. M. , Kharisun  
Published: December 2006

AbstractWycheproofite is a new hydrated sodium aluminium zirconium phosphate from a pegmatite vein in granite at Wycheproof, in northwestern Victoria, Australia. The mineral occurs as compact, finely fibrous masses in small cavities in the quartz/feldspar/muscovite/schorl-bearing pegmatite. The fibrous crystals are between 5 and 10 µm wide and up to several mm long. Accompanying minerals include two other zirconium phosphates — kosnarite and a new species, selwynite, the K-analogue of gainesite — as well as wardite, eosphorite, cyrilovite, leucophosphitc, rockbridgeite, a kidwellite-like mineral and saleeite. The wycheproofite aggregates are pale pinkish to brownish orange, with a vitreous to pearly lustre. The streak is colourless, fracture rough, cleavage not observed and the Mohs hardness is between 4 and 5. Optical data are incomplete due to the fibrous nature of the mineral; the indices of refraction are in the range 1.62–1.64. The measured density is 2.83 g cm−3. Chemical analysis gave (wt.%) Na2O 6.36, K2O 0.44, CaO 0.66, FeO 0.36, MnO 0.21, Al2O3 12.03, Cs2O 0.03, ZrO2 32.43, HfO2 1.24, P2O5 35.85, SiO2 0.23, F 0.34, H2O 9.0, less 0=F 0.14, Total 99.04. The simplified formula is NaAlZr(PO4)2(OH)2·H2O. Wycheproofite is triclinic with unit cell parameters a=10.926(5) Å, b = 10.986(5) Å, c = 12.479(9) Å, α= 71.37(4)°, β = 77.39(4)°, γ= 87.54(3)° V = 1375.9 Å3. For Z= 6, the calculated density is 2.81 g cm-3. The strongest lines in the X-ray powder diffraction pattern are [dobs (Å), Iobs,hkl] 2.603 (100) 040; 4.128 (80) 121; 3.711 (65) 023; 3.465 (60) 030; 8.865 (40) 101; 3.243 (35) 132. The crystal structure has not been solved due to the finely fibrous nature of the material available. The name is for the locality, which in the local Australian Aboriginal language means ‘witchie bushes growing on a hilltop’.Data on the third occurrence of kosnarite, KZr2(PO4)3, at Wycheproof are also given.
Hydrogen bonding in borcarite, an unusual borate-carbonate mineral
Authors: Burns P. C. , Hawthorne F. C. 
Published: December 2006

AbstractThe crystal structure, including hydrogen positions, of borcarite, Ca4Mg[B4O6(OH)6](CO3)2, monoclinic, a = 17.840(4), b = 8.380(2), c = 4.445(1) Å, β = 102.04(3)°, V = 649.9(3) Å3, space group C2/m, has been refined by full-matrix least-squares methods to R = 2.5% and wR = 3.0% for 1020 unique observed [|F| ≥ 5σ(F)] reflections collected using Mo-Kα X-radiation. The H positions were located on difference-Fourier maps and were refined using the ‘soft’ constraint that O-H distances are ∼ 0.96 Å. The 4:4T FBB (fundamental building block) of the borcarite structure contains four Bϕ4 tetrahedra (ϕ = unspecified ligand) which share corners to form a four-membered polyhedral ring. Borcarite is the only mineral known to contain this FBB. The FBBs do not polymerize, but each shares three anions with an Mgϕ6 octahedron on either side, forming rods of composition [MgB4O6(OH)6]4- along the c-axis. The rigidity of these rods is enhanced by hydrogen bonding, and individual rods are connected through Caϕ8 polyhedra, Cϕ3 triangles and hydrogen bonds.
The formation of rhodochrosite–smithsonite (MnCO3–ZnCO3) solid-solutions at 5°C
Authors: Böttcher Michael E. 
Published: December 2006

AbstractMnxZn(1−x)CO3 solid-solutions were prepared at 5°C by precipitation from metal-bearing bicarbonate solutions. The solids were identified by X-ray powder diffraction and infrared spectroscopy. Zn2+ ions substitute extensively for Mn2+ ions in the crystal lattice of anhydrous rhombohedral carbonates. Throughout the 24 h during which the experiments were conducted, the aqueous solutions remained undersaturated with respect to pure oxides, sulphates, hydroxides and hydroxysulphates. The solutions, however, were supersaturated with MnxZn(1−x)CO3 of any given composition. Besides the anhydrous rhombohedral carbonates, Zn4(OH)2(CO3)3·4H2O was precipitated from an aqueous solution with initially high Zn2+ concentration. The negative logarithm of the solubility product of Zn4(OH)2(CO3)3·4H2O was estimated theoretically to be 43.9 (25°C). Remaining saturation with respect to Zn4(OH)2(CO3)3·4H2O was calculated accordingly. The suggestion is made that hydrated zinc hydroxycarbonate is metastable under the experimental conditions used here, but that it should transform into anhydrous carbonates.
The low-temperature behaviour of analcime. 1: high-resolution neutron powder diffraction
Authors: Line C. M. B. , Dove M. T. , Knight K. S. , Winkler B. 
Published: December 2006

AbstractThe structure of a synthetic sample of analcime has been determined as a function of temperature between 30–300 K by high-resolution neutron powder diffraction. Although there are some reports of samples of analcime having non-cubic structures, the sample in our experiments remained cubic (space group la3d), and hence disordered, down to low temperatures. The absence of phase transitions involving ordering of the orientations of the water molecules, ordering of the sodium positions, or a displacive instability as in leucite and related materials, is discussed. We speculate that part of the reason for the absence of ordering of the water molecules or sodium cations is associated with the Al/Si disorder, which cannot order at low temperatures. We also discuss the likely distribution of the orientations of the water molecules at low temperatures, and propose that the water diads lie close to any of the crystal diads with the H-H Vectors lying close to the triads.
An ultrasonic probe for the extraction of microscopic quantities of minerals for X-ray work
Authors: Kovachev Veselin , Strashimirov Strashimir 
Published: December 2006

AbstractThe instrumentation and procedure is described for the extraction of very small and pure samples from polished mounts and thin sections of minerals, for X-ray analysis and other micro-analytical techniques. It uses a stand-mounted, tunable ultrasonic probe (400 W/15–50 kHz) inclined at 45°C to a microscope stage. The tip of the probe, usually a steel needle, is located on the desired mineral and an appropriate ultrasonic frequency is selected. Very fine powders are produced from grains as small as 0.01–0.005 mm. A distinct advantage of this technique is that, as different minerals powder at different rates and different frequencies, it is possible to separate a single mineral from an intergrowth of two or more minerals.