Research on HR6W Manufactured Reheater Outlet Header of the Advanced USC Boiler
Authors: Zhihao Tian , Yufeng Zhu , Xiaoli Lu , yu Wang , Kaiyin Yang , Chongbin Wang 
Published: March 2024

Abstract
This paper reports the performance of HR6W iron-nickel based alloy and 617B nickel based alloy which are the candidate material for high temperature reheater outlet header of advanced secondary reheat ultra-supercritical unit boiler with reheat steam 653 °C, and analysis the applicable temperature range of the material. As a result, HR6W is the appropriate material to manufacture high temperature reheater outlet header of A-USC boiler with parameters 620°C /653°C/653°C.
Research on Magnetic Behavior of Austenitic Heat-Resistant Steel Boiler Tubes After Service
Authors: Shi Zhi-gang , Ma Hong , Cui Xiong-hua , Wang Hong-zhe , He Xiao-dong 
Published: March 2024

Abstract
The delivery state of austenitic heat resistant steel boiler tubes is paramagnetic, such as TP304H, TP347H and S30432, the material state, however, appears obviously magnetic after long-time high-temperature service. Vibrating Sample Magnetometer (VSM) has been employed to test the magnetism difference after high-temperature service, and XRD, SEM, TEM, SAED and EDS has been adopted to observe and analyze their microstructure, phase structure and composition. The research results show that compared with the delivery state, the lath α´-Martensite and sometimes the lamellar ε-Martensite will occur in areas adjacent to grain boundaries due to martensite transformation in the microstructure of austenitic heat resistant steel boiler tube after high temperature service. There are high density dislocations tangled together in the substructure of α´-Martensite, and lamellar stacking faults arrayed orderly by a large number of dislocations in the substructure of ε-Martensite. The magnetism of α´-Martensite, its internal stress and carbides is the reason why the austenitic heat resistant steel boiler tubes appear obviously magnetic after high temperature service, and the α´-Martensite plays a major role.
Long-Term Creep Rupture Properties and Microstructures in HR6W (44Ni-23Cr-7W) for A-USC Boilers
Authors: Saito Nobuhiko , Komai Nobuyoshi , Hashimoto Keita , Kitamura Masaki 
Published: March 2024

Abstract
Seeking to reduce CO2 emissions and improve power generation efficiency, a project to develop a 700°C A-USC (advanced ultra super critical) power plant has been under way in Japan since 2008. HR6W (44Ni-23Cr-7W) is a candidate material for application in the maximum temperature areas of A-USC boilers. In this study, the creep rupture properties of plastic deformed material were investigated in comparison with those of solution treated material, in order to clarify the capability of HR6W as a material for use in A-USC plants. The creep strength of 20% pre-strained HR6W was found to increase substantially as compared with the solution treated material. 20% pre-strained material is in a state where high dislocation density has been introduced by plastic forming strain, with M23C6 and Laves phase precipitating preferentially by dislocation diffusion from the early stages of creep. In particular, since high dislocation density is accumulated in connection with creep deformation near the grain boundaries, precipitation is accelerated and the grain boundaries are covered with M23C6 from the early stages of creep. Then, even though the intragranular precipitate density decreases, given that the fraction of grain boundaries affected by precipitation is maintained in a high state, it is presumed that a high density of dislocation is maintained in the long-term region. This was considered to be the reason why the creep rupture strength of the 20% pre-strained material increased so remarkably in comparison with the solution treated material.
Structural Changes in P92-Type Martensitic Steel During Creep at 600°C
Authors: Fedoseeva A. , Nikitin I. , Dudko V. , Dudova N. , Kaibyshev R. 
Published: March 2024

Abstract
Structural changes in P92-type steel after creep at temperature of 600°C under a stress of 140 MPa were investigated. The steel was solution treated at 1050°C and tempered at 780°C. The structure in the grip portion of the creep specimen changed scarcely after creep exposure for 6876 h. In contrast, the structural changes in the gage and neck sections were characterized by transformation of the tempered martensite lath structure into relatively coarse subgrain structure. The formation of a well-defined subgrain structure in the gage and neck sections was accompanied by the coarsening of M23C6 carbides and precipitations of Laves phase during creep. Mechanisms of grain boundary pinning by precipitates are discussed.
Creep Damage Evaluation Method for Welded Joints of Grade 91 Steels
Authors: Yoshida Kimiaki , Tsuruta Hideki , Tabuchi Masaaki , Kobayashi Ken-ichi 
Published: March 2024

Abstract
This study is concerned with the creep damage evaluation for the welded joint of modified 9Cr-1Mo steels. A finite element prediction method based on ductility exhaustion approach has been proposed. Degradation of creep ductility under multi-axial stress state has been formulated from the experimental results of notched bar specimens for the base metal and the fine-grained heat affected zone, and has been taken into the damage model. Creep test of welded joint specimen of modified 9Cr-1Mo steel has been conducted to confirm the accuracy of the damage evaluation method. It has been concluded that the predicted trend of creep damage has good agreement with the experimental results, but the predicted rupture time become longer than the experimental results of rupture time.
Development and Application of T91 Cold Weld Repair Techniques
Authors: Mitchell K.C. 
Published: March 2024

Abstract
The application of cold weld repair techniques in the power industry has been well documented. This type of repair is only considered when a conventional repair (involving post-weld heat treatment) is impracticable or the penalties of time and cost for conventional repair are sufficiently high. A typical cold weld repair in the UK has involved low alloy ferritic steel (½Cr½Mo¼V, 2¼Cr1Mo) components welded with nickel based SMAW consumables or ferritic FCAW consumables. Modified 9Cr steel components have been used in UK power plant since the late 1980’s for a number of applications, such as superheater outlet headers, reheat drums and main steam pipework. The problems associated with this material have also been well documented, particularly premature type IV cracking of welds on creep weakened modified 9Cr steel. RWE Generation UK have developed modified 9Cr cold weld repairs on headers, pipework and tubes. These repairs have been underwritten with extensive testing. This paper will describe the work performed on developing T91 cold weld repairs and where they have been applied on power plant.
Tensile, Creep and Microstructural Behavior of Welded Cast Haynes 282 Alloy for A-USC Steam Turbine Casing Applications
Authors: Maziasz P.J. , Moser J. , Unocic K. , Yang Y. , Purdy D. , Jablonski P.D. 
Published: March 2024

Abstract
Haynes 282 alloy is a relatively new Ni-based superalloy that is being considered for advanced ultrasupercritical (A-USC) steam turbine casings for steam temperatures up to 760°C. Weld properties are important for the turbine casing application, so block ingots of Haynes 282 alloy were cast for properties studies. Good, sound welds were produced using Haynes 282 weld-wire and a hot gas-tungsten-arc welding method, and tensile and creep-rupture properties were measured on cross-weld specimens. In the fully heat-treated condition (solution annealed + aged), the tensile properties of the welded specimens compare well with as-cast material. In the fully heat-treated condition the creep-rupture life and ductility at 750°C/250MPa and 800°C/200MPa of the cross-weld specimens are similar to the as-cast base metal, and repeat creep tests show even longer rupture life for the welds. However, without heat-treatment or with only the precipitate age-hardening heat-treatment, the welds have only about half the rupture life and much lower creep ductility than the as-cast base metal. These good properties of weldments are positive results for advancing the use of cast Haynes 282 alloy for the A-USC steam turbine casing application.
9-10% Cr Steel Forgings for USC Turbines - Experiences in Manufacturing and Development Status of MARBN Steels
Authors: Zeiler Guenter , Paul Stefan , Plesiutschnig Ernst 
Published: March 2024

Abstract
Sufficient energy availability in combination with lowest environmental pollution is a basic necessity for a high living standard in each country. To guarantee power supply for future generations, improved technologies to achieve higher efficiency combined with reduced environmental impact are needed. This challenge is not only aimed to the power station manufacturers, but also to the producers of special steel forgings, who have to handle with more and more advanced materials and complex processes. Bohler Special Steel is a premium supplier of forged high quality components for the power generation industry. This paper reports about experiences in the fabrication of forged components for steam turbines for ultra-supercritical application - from basic properties up to ultrasonic detectability results. The materials used so far are the highly creep-resistant martensitic 9-10% Cr steel class for operating temperatures up to 625°C developed in the frame of the European Cost research program. Additionally our research activities on the latest generation of high temperature resistant steels for operating temperatures up to 650 degree Celsius – the boron containing 9% Cr martensitic steels (MARBN) - are discussed. In order to improve the creep behavior, MARBN steels with different heat treatments and microstructures were investigated using optical microscopy, SEM and EBSD. Furthermore, short term creep rupture tests at 650 degree Celsius were performed, followed by systematic microstructural investigations. As a result it can be concluded, that advanced microstructures can increase the time to rupture of the selected MARBN steels by more than 10 percent.
The Effect of Impurities on Supercritical CO2 Compatibility of Structural Alloys
Authors: Pint B. A. , Brese R. G. , Keiser J. R. 
Published: March 2024

Abstract
In both direct- and indirect-fired supercritical CO2 (sCO2) cycles, there is considerable interest in increasing the size and efficiency of such systems, perhaps by increasing the peak temperature to &gt;700°C. However, relatively little experimental data are available under these conditions with pressures of 200-300 bar. Furthermore, impurities such as O2 and H2O in the CO2 may greatly alter the compatibility of structural alloys in these environments. While an experimental rig is being constructed that can measure and control the impurity levels in sCO2 at 200-300 bar, initial 1 bar experiments at 700°-800°C for 500 h have been conducted in high-purity and industrial grade CO2, CO2+0.15O2 and CO2+10%H2O and compared to exposures in dry air and 200 bar sCO2. These results, focusing on Fe- and Ni-base structural alloys and commercial chromia- and alumina-forming alloys, indicate that modifications in the environment did not strongly affect the reaction products at 700°-800°C.
Oxidation Resistance of Shot Peened Austenitic Stainless Steel Superheater Tubes in Steam
Authors: Tossey Brett M. , Khan Hassan , Andress Tom 
Published: March 2024

Abstract
Steam-side oxidation and the resultant exfoliation of iron-based scales cause unplanned shutdowns at coal-fired power generation plants. Exfoliate removal is currently limited to frequent unit cycling to minimize the volume of exfoliated scale, upgrading a plant with a “blow down” system, or installing a higher alloy. This paper discusses the rate of steam-side oxidation on Type 304H stainless steel (304H) tube after shot peening the internal surface with commercially available techniques. Shot peening the ID of Type 304H austenitic stainless steel superheater tubes has been shown to improve the overall oxidation resistance in steam. Decreasing the oxidation rate directly impacts the volume of exfoliated scale. The adherent spinel scales are thinner and more robust than non-shot peened tubes of the same alloy. Most of the improved oxidation resistance can be attributed to the presence of a spinel oxide layer combined with a continuous chromia layer formed near the steam-touched surfaces. The presence of a continuous chromia layer vastly reduces the outward diffusion of iron and minimizes the formation of iron-based scales that exfoliate. This work showed that a uniform cold-worker layer along the tube ID has a profound effect on oxidation resistance. Incomplete coverage allows oxidation to proceed in the non-hardened regions at a rate comparable to the oxidation rate on unpeened Type 304H.
Experience with 9Cr3W3CoVNbBN Steel in Terms of Welding, Creep and Oxidation
Authors: Abstoss K. G. , Nitsche A. , Mayr P. , Schlacher C. , Gonzalez V. , Agüero A. 
Published: March 2024

Abstract
The presented work summarizes the results of more than 10 years of research at TU Graz and TU Chemnitz and partners on a martensitic boron and nitrogen stabilized 9Cr3W3Co (MARBN) steel grade. The design philosophy of MARBN steels is presented and critical issues regarding boron and nitrogen balance are discussed. Microstructural characterization of two different laboratory heats, is presented and efforts in European projects towards an upscaling of melts are presented. Base material creep testing data at 650 °C up to 50.000 hours is presented and assessed to commercial alloys such as ASTM grades P91 and P92. An increase of creep rupture stress of more than +20% was recorded. Oxidation tests in steam at 650°C revealed an anomalous response of the material. Several specimens exhibited excellent oxidation resistance commonly only seen for grades of higher chromium content. The anomalous oxidation behaviour is identified and discussed, although the causes remain yet unclear. Results of manufacturing, characterization and testing of different MARBN welds, including gas-tungsten-arc-, gas-metal-arc-, friction stir and electron beam welds reveal a microstructure memory effect in the heat affected zone, so that no uniform fine-grained zone is present. The behaviour of crosswelds during long-term creep testing at 650 °C up to more than 32.000 hours is assessed and the susceptibility to Type IV cracking is discussed. The manuscript summarizes research of more than 10 years, presents current research activities on MARBN and describes open questions for an alloy identified as a promising martensitic steel grade for elevated temperature components.
G115 Steel and Its Application for 600+°C A-USC-Power Plants
Authors: Liu Zhengdong , Bao Hansheng , Chen Zhengzong , Xu Songqian , Zhao Haiping , Yan Peng , Wang Qijiang 
Published: March 2024

Abstract
G115 is a novel ferritic heat resistant steel developed by CISRI in the past decade. It is an impressive candidate material to make tubes, pipes, and forgings for advanced ultra super critical (A-USC) fossil fired power plants used for the temperature scope from 600°C to 650°C. The successful development of G115 extends the upper application temperature limitation of martensitic steel from 600°C to about 650°C. This breakthrough is imperative for the design and construction of 610°C to 650°C A-USC fossil fired power plants, from the viewpoint of the material availability and economics of coal fired power plant designs. This paper introduces the development history and progress of G115 steel. The strengthening mechanism of the novel martensitic steel is briefly discussed, and the optimized chemical composition and mechanical properties of G115 steel are described. The details of industrial trials of G115 tube and pipe at BaoSteel in the past years are reviewed, with the emphasis on the microstructure evolution during aging and creep testing. These tests clearly show that the microstructure of G115 steel is very stable up to the temperature of 650°C. Correspondingly, the comprehensive mechanical properties of G115 steel are very good. The creep rupture time is longer than 17000 hours at the stress of 120MPa and at the temperature of 650°C and 25000+ hours at the stress of 100MPa and at the temperature of 650°C, which is about 1.5 times higher than that of P92 steel. At the same time, the oxidation resistance of G115 steel is a little bit better than that of P92 steel. If G115 steel is selected to replace P92 pipes at the temperature scope from 600°C to 650°C, the total weight of the pipe can be reduced by more than 50% and the wall thickness of the pipe can be reduced up to about 55%. In addition, the upper application temperature limitation of G115 steel is about 30°C higher than that of P92 steel. Thus, G115 steel is a strong candidate material for the manufacturing of 600+°C advanced ultra-super-critical (A-USC) fossil fuel power plants in China and elsewhere.
Tantalum and Niobium Based Z-Phase in A Z-Phase Strengthened 12% Cr Steel
Authors: Rashidi Masoud , Lawitzki Robert , Andren Hans-Olof , Liu Fang 
Published: March 2024

Abstract
Higher steam temperature in steam power plants increases their thermal efficiency. Thus there is a strong demand for new materials with better creep and corrosion resistance at higher temperatures, while retaining the thermal flexibility of martensitic steels. Z-phase strengthened 12% Cr steels have been developed to meet the 923 K (650°C) challenge in these power plants. Ta, Nb, or V forms Z-phase together with Cr and N. A new trial steel was produced based on combining Ta and Nb to form Z-phase. It was shown that Z-phase was formed with a composition corresponding to Cr1+x(Nb,Ta)1-xN. The Nb/Ta ratio in Z-phase precipitates was higher than that in MX precipitates. Z-phase precipitates based on Ta and Nb were coarser than precipitates in a similar trial steel based on Ta alone.
Long-Term Microstructural Evolution in a 10%Cr High Creep Resistant Martensitic Steel at 650°C
Authors: Mishnev Roman , Dudova Nadezhda , Kaibyshev Rustam 
Published: March 2024

Abstract
A 10%Cr martensitic steel with 3%Co and 0.008%B exhibits extremely long creep rupture time of approximately 40000 h under an applied stress of 120 MPa at a temperature of 650°C. The steel’s microstructure after creep tests interrupted at different creep stages was examined by transmission and scanning electron microscopy. It was shown that superior creep resistance of this steel was attributed to slow increase in creep rate at the first stage of tertiary creep whereas the rapid acceleration of creep rate took place only at the short second stage of tertiary creep. Transition from minimum creep rate stage to tertiary creep was found to be accompanied by coarsening of Laves phase particles, whereas M23C6 – type carbides demonstrated high coarsening resistance under creep condition. Strain-induced formation of Z-phase does not affect the creep strength under applied stress of 120 MPa due to nanoscale size of Z-phase particles.
Investigation of the Observed Stress Corrosion Cracking of T24 Material
Authors: Ullrich C. , Rademacher H.-G. , Tillmann W. , Zielke R. , Körner P. 
Published: March 2024

Abstract
Starting in 2010 a new generation of coal fired power plants in Europe operating at a steam temperature of up 620°C was commissioned. During that commissioning process many cracks occurred in welds of T24 material which was extensively used as membrane wall material in nearly all of the new boilers. The cracks were caused by stress corrosion cracking (SCC) only occurring in the areas of the wall being in contact to high temperature water during operation. The question which step of the commissioning process really caused the cracking was not answered completely even several years after the damage occurred. To answer this question and to define parameters which will lead to cracking in high temperature water many tests were conducted. Generally it was found that slow tensile tests in controlled environment are well suited to get information about materials SCC sensitivity in the laboratory. In the present paper, first the influence of the cracking of welded T24 material in acidic environment containing well-defined amounts of H2S is investigated to address the question if a chemical cleaning process prior to the testing might lead to hydrogen induced SCC. As a second step, cracking behaviour in high temperature water is being investigated. Here the influence of the temperature, the oxygen concentration of the water, the deformation speed of the sample, the heat treatment and the condition of the material on the SCC is analysed.
Corrosion Products Development on Haynes282 Gamma - Prime (γ') Strengthened Alloy at 550 °C Under Salt Mist Conditions for 500 Hours
Authors: Dudziak T. , Sobczak N. , Sobczak J. , Siewiorek A. , Purgert R. M. 
Published: March 2024

Abstract
Prior to utilizing new advanced materials in coal power plants, a large number of experimental testing is required. Test procedures are needed in specialized high temperature laboratories with state of the art facilities and precise, accurate analytical equipment capable of performing tests at a variety of temperatures and environments. In this study, the results of a unique technique involving salt spray testing at high temperatures are presented. The Haynes 282 gamma – prime (γ’) strengthened alloy fabricated by means of three different manufacturing processes: HAYNES 282 WROUGHT alloy, Haynes 282-SINT alloy, and finally Haynes 282-CAST alloy have been tested. The materials have been exposed to a salt spray corrosion atmosphere using 1% NaCl - 1% Na2SO4. Post exposure investigations have included SEM, EDS and XRD examinations. The test using salt spray of 1% NaCl - 1% Na2SO4 water solution at 550 °C for 500 hours indicted no influence on the corrosion products formation, where Cr2O3 has been developed in all three alloys, whereas NiO has been found only in Haynes 282-CAST material. On the other hand, it has been found that the fabrication process of HAYNES 282 alloy strongly influences the corrosion products formation under the high temperature exposures.
Fabrication Experience of New High Oxidation Material—Thor 115
Authors: Urzynicok Michael , Kwieciński Krzysztof 
Published: March 2024

Abstract
Development of steels used in the power generation industry for the production of boilers characterized by supercritical parameters poses new challenges. The introduction of new combinations of alloying agents aimed at obtaining the best possible mechanical properties, including creep resistance, affects the weldability of new steels. Each of the latter has to undergo many tests, particularly as regards bending and welding, in order to enable the development of technologies ensuring failure-free production and assembly of boiler systems. Martensitic steels containing 9% Cr, used in the manufacturing of steam superheaters, are characterized by excellent creep resistance and, at the same time, low oxidation resistance at a temperature in excess of 600°C. In turn, steels with a 12% Cr content, i.e., VM12-SHC or X20CrMoV12-1 are characterized by significantly higher oxidation resistance but accompanied by lower strength at higher temperatures, which translates to their limited application in the production of boilers operating at the most top parameters.X20CrMoV12-1 was withdrawn from most of the power plants, and VM12-SHC was supposed to replace it, but unfortunately, it failed in regards to creep properties. To fulfill the gap a new creep strength-enhanced ferritic steel for service in supercritical and ultra-supercritical boiler applications was developed by Tenaris and it is designated as Thor115 (Tenaris High Oxidation Resistance). This paper covers the experience gained during the first steps of fabrication, which includes cold bending and welding of homogenous joints.