Weathering of Ilmenite in a Lateritic Pallid Zone
Authors: Anand R. R. , Gilkes R. J. 
Published: August 2006

AbstractIn a lateritic pallid zone ilmenite crystals alter via pseudorutile to porous leucoxene grains composed of randomly oriented aggregates of ~0.06 μm anatase crystals. This style of alteration differs from that in beach sands where parallel oriented rutile crystals develop from pseudorutile. Increased Si and Al in the altered grains is due to the crystallization from soil solution of halloysite, kaolinite and gibbsite within pores rather than to the incorporation of these elements into anatase crystals. Manganese was a significant constituent (3.2% Mn2O3) of the original ilmenite but was not retained by the leucoxene grains. The minor constituents Ni, Zn, Cu, Mg, Co and Ca were also lost, but Cr and V were retained.
Synthesis and Characterization of Zeolites in the System Na2O-K2O-Al2O3-SiO2-H2O
Authors: Donahoe Rona J. , Liou J. G. , Guldman Sandra 
Published: August 2006

AbstractZeolites having the structures of phillipsite, merlinoite, and gobbinsite were synthesized from clear solutions at 80°C in the system Na2O-K2O-Al2O3-SiO2-H2O and their morphologies, cell parameters, and compositions determined. At 3.5 M silica concentration, the formation of merlinoite (synthetic zeolite W) is favored over the formation of phillipsite (synthetic zeolite ZK-19) by solution conditions of high pH (> 13.6) and low Na/(Na + K) ratios (<0.5).Using the information obtained from the synthesis experiments, the presence of merlinoite was predicted in sediments from Searles Lake, a saline, alkaline lake in California with ideal physiochemical conditions for its formation. Merlinoite was subsequently discovered to occur in tuffaceous sediments as part of an authigenic silicate zonation pattern from phillipsite → phillipsite + merlinoite → merlinoite → K-feldspar with increasing depth. Because of the close similarities in the physical properties of phillipsite and merlinoite, merlinoite may be much more common as an authigenic mineral than is currently realized.
Effects of Exchangeable Cation Composition on the Thermal Expansion/Contraction of Clinoptilolite
Authors: Bish David L. 
Published: August 2006

AbstractTo understand and predict the effects of a thermal pulse induced by a radioactive waste repository on clinoptilolite-bearing rocks, the lattice parameters of 6 natural and 3 cation-exchanged (Ca, K, Na) clinoptilolites were studied as a function of temperature. The samples were examined at room temperature, under vacuum, and at 50°C increments to 300°C using a high-temperature X-ray powder diffractometer. The unit cell of all samples decreased in volume between 20° and 300°C Na-saturated clinoptilolite underwent the greatest volume decrease (8.4%) and K-saturated clinoptilolite the smallest (1.6%), of the clinoptilolites studied. The volume decrease for the Ca-saturated clinoptilolite was 3.6%. The highest percentage decrease for each sample was along the b axis, generally 80–90% of the total volume decrease. The change in the a axis was the smallest and was usually <5%, although 26.5% of the contraction of the Na-exchanged clinoptilolite was along a. The bulk of the volume contraction of many samples occurred on evacuation at room temperature, demonstrating that the observed changes were due to water loss and not to temperature-induced structural changes. Low-angle scattering was significantly reduced upon evacuation for every sample, and the 110 reflection of clinoptilolite at 7.45°2θ became obvious, whereas it was not in the untreated samples.These data show that the effects of heating on the unit-cell volume of clinoptilolite depend strongly on the exchangeable cation content. Significant reductions in the unit-cell volumes of natural, mixed Na-K-Ca clinoptilolites could take place in rocks in a repository environment, particularly if the clinoptilolites occurred in unsaturated, dehydrated rock. The unit-cell volumes of clinoptilolites in partially saturated rocks at temperatures below 100°C, however, should not decrease significantly.
Natroalunite in a Laterite Profile Over Deccan Trap Basalts at Matanumad, Kutch, India
Authors: Chitale D. V. , Güven N. 
Published: August 2006

AbstractAn end-member natroalunite of composition (K0.04Na0.96)(Al2.98Fe0.02)(SO4)2(OH)6 occurs in saprolitic clays in a laterite profile developed over Deccan Trap basalts at Matanumad in the Kutch region of Gujarath state, India. Pseudocubic natroalunite crystals, ranging from 0.5 to 1 µm in size, have replaced pseudohexagonal, 2-µm-size platelets of kaolinite. The reverse reaction (kaolinization of natroalunite) has also been observed in the laterites and bauxites immediately adjacent to the saprolite. The kaolinite crystallites that replaced natroalunite occur as a mosaic of anhedral platelets that range in size from 0.1 to 0.3 µm. The formation of natroalunite at Matanumad postdates the laterization of the basalts. It is related to the post-diagenetic formation of sulfuric acid-rich solutions by the oxidation of pyrite in the Eocene-Oligocene black shales of the Matanumad basin. The kaolinitic clays at the top of the saprolite zone have been intensely altered by the acidic solutions, leading to a high concentration of natroalunite.
Structural Study of a Benzidine-Vermiculite Intercalate Having a High Tetrahedral-Iron Content by 57Fe Mössbauer Spectroscopy
Authors: Cardile C. M. , Slade P. G. 
Published: August 2006

Abstract57Fe Mössbauer spectra obtained at room temperature and 78 K for natural Mg-saturated, Ca-saturated, and benzidinium-intercalated vermiculite having a high tetrahedral iron content are presented. For all samples the spectra were computer-fitted with five overlapping doublets, representing Fe in both tetrahedral and octahedral sites. One doublet has parameters consistent with the weathered ilmenite known to be present as inclusions. For the intercalated vermiculite, the δ value of the doublet assigned to the tetrahedral Fe3+ increased with respect to the untreated sample, suggesting that the electron densities about the Fe sites had decreased following intercalation. A charge movement from the silicate layers towards the interlayer monovalent benzidinium ions is also implied. The direction of this charge movement is opposite to that found when blue monopositive radical cations form on montmorillonite surfaces. The Mössbauer evidence suggests the absence of an interlayer-Fe3+ complex.
Petrology of the Desmoinesian Excello Black Shale of the Midcontinent Region of the United States
Authors: Ece Omer Isik 
Published: August 2006

AbstractThe Excello Shale is one of the best exposed and most laterally continuous of the Pennsylvanian cyclothemic black shales in the midcontinent region of the United States. Its petrology and paleoenvi-ronmental significance were studied to understand the nature of cyclic black shales in general and how they relate to the habitat of hydrocarbon source beds. The Excello is thinly laminated, fissile where weathered, and rich in organic matter and phosphate nodules; it is 90–120 cm thick. Its thin laminations, fine particle size, and high total organic carbon (TOC) content suggest that it was deposited in a quiet water environment of an epeiric sea having anaerobic bottom water. The Excello Shale consists of two lithofacies: non-bioturbated black shale and bioturbated yellow-brown shale. Petrographic studies show that the black shale contains wavy to straight laminations and that the yellow-brown shale contains discontinuous and random laminae and mottled stratification. The close association of organic matter and phosphate-controlled nodule morphology (spherical, elongated, bladed, and platy) appear to be related to progressive decreases in nutrient supply of the sea water from the ancient ocean (Panthalassa).Clay-mineral assemblages consist mainly of detrital illite, kaolinite, chlorite, and illite/smectite (I/S). Grain size and amount of these clays increase and TOC decreases shoreward towards the probable source areas of the clay minerals in the northern Ouachita region and northern Iowa. Quartz, carbonate-fluor-apatite, carbonate fossil fragments, and minor feldspar and pyrite are the principal minerals in the Excello Shale. Minor amounts of fine-silt-size carbonate minerals are present in some samples. Limestone concretions, 90–150 cm in diameter and 30 cm thick, were found at only one locality in Missouri where the Excello is a maximum of about 3 m thick. Fissility increases with weathering along the bedding plane, and laminae are separated by a limonite film. Four petrographically distinct microfabric variations of the Excello Shale appear to be related to the TOC content and bioturbation. Textural and structural properties of the shale are more developed with increasing organic matter content.
Parameters Influencing Layer Stacking Types in Saponite and Vermiculite: A Review
Authors: Suquet Hélène , Pezerat Henri 
Published: August 2006

AbstractSaponites and vermiculites may assume at least 11 ordered or semi-ordered layer stacking sequences. For a given relative humidity, the layer stacking type assumed is a function of the nature of the interlayer cation, the layer charge density, the mean size of the particles, and the di- or trioctahedral character of the sheets. For each interlayer cation, a succession of layer stacking types can be observed as relative humidity increases. For high relative humidity, some particular layer stacking types exist, but only for low-charge minerals. No other differences have been found for saponites and vermiculites in each successive layer stacking type. The degree of order that these layer stacking types imply is probably due to the existence of electrostatic bonds between hydrated interlayer cations and surface oxygens of the substituted tetrahedra. For octahedrally substituted 2:1 phyllosilicates, however, the disorder of the layer stacking sequences is related to a highly delocalized distribution of negative charges on the surface oxygens of the layers.A study of the superstructures detected in saponites and vermiculites indicates that the interlayer cations tend to be located as far as possible from one another. The superstructures exist only with some cations and some layer stacking types and if the layer charge density is compatible with the charge produced by the cation distribution in this kind of superstructure.
Charge Reduction, Octahedral Charge, and Lithium Retention in Heated, Li-Saturated Smectites
Authors: Jaynes W. F. , Bigham J. M. 
Published: August 2006

AbstractReference smectites were examined to determine relationships between Li uptake, cation-exchange capacity (CEC), and octahedral layer charge after Li saturation and heating at 250°C (Hofmann-Klemen effect). Direct measurements of exchangeable Li after heating led to overestimates of charge reduction due to entrapment of Li in collapsed interlayers. Expansion of interlayers by sequential washings with 1 N MgCl2, 0.01 N MgCl2, and ethanol and subsequent determinations of exchangeable Mg provided accurate measurements of reduced charge. The CEC reductions observed in dioctahedral samples as a result of Li saturation and heating equaled octahedral charge values derived from published mineral formulae, and interlayer charge estimates obtained by alkylammonium exchange confirmed that measured CEC reductions were a consequence of uniform decreases in octahedral layer charge.Dioctahedral specimens retained 1 to 10 meq/100 g of non-exchangeable Li in excess of CEC reduction and were acidified in direct proportion to their total Fe contents, apparently as a result of the deprotonation of structural hydroxyl groups. Mild acid treatment reprotonated these hydroxyl groups, released excess Li, and resulted in total Li contents comparable to measured CEC reductions. Heating (250°C) Mg-saturated hectorite induced a loss of octahedral Li, acidification, and a reduction of CEC, indicating that Mg had partially replaced octahedral Li. These results suggest that octahedral Li is mobile at low temperatures and that cation movement into or out of the octahedral sheet is favored if the layer charge is reduced.
Quantitative Determination of Clinoptilolite in Soils by a Cation-Exchange Capacity Method
Authors: Ming Douglas W. , Dixon Joe B. 
Published: August 2006

AbstractA cation-exchange capacity (CEC) method based on ion-sieving properties was developed for the quantitative determination of clinoptilolite in soils. In this method, both zeolitic and non-zeolitic exchange sites in the soil sample are saturated with Na+. The CEC of the non-zeolitic exchange sites is determined by replacing the Na− in these sites with tert-butylammonium ions. The tert-butylammonium ion cannot be exchanged into the zeolitic exchange sites because it is too large to pass through the channels in the clinoptilolite structure. The sample is next washed with NH4OAc to replace the Na+ in the zeolitic exchange sites. The amount of soil zeolite is then estimated by comparing the CEC of zeolitic exchange sites to the total zeolite CEC (175 meq/100 g for pure clinoptilolite). Prior to the CEC analyses, carbonates and organic matter must be removed to minimize interference with the exchange process. A high correlation (r2 = .96) was observed between the abundance of clinoptilolite estimated using the CEC method and the abundance estimated by semiquantitative X-ray powder diffraction analysis.The CEC procedure was used to quantify clinoptilolite in an Aridic Calciustoll soil from south Texas. About 2–5% clinoptilolite occurs in the A and B horizons, and concentrations progressively increase with soil depth to as much as 20% in the CBk2 horizon.
Ferrian Saponite in a Gabbro Saprolite at Mont MéGantic, Quebec
Authors: Kodama H. , De Kimpe C. R. , Dejou J. 
Published: August 2006

AbstractGabbroic saprolite at Mont Mégantic, Quebec, was studied in detail mineralogically to gain a better understanding of the origin of ferruginous smectite reported previously from these rocks. The parent rock is a ferrogabbro composed of plagioclase, augite, calc-alkalic amphiboles, biotite, olivine, magnetite, ilmenite, and apatite. Extensive weathering has decomposed most of the mafic minerals and magnetite to goethite, lepidocrocite, and iron-rich clay minerals, which occur in numerous microcracks distributed irregularly in the outer shells of boulders and in cracks and fissures in the bedrock. Some of the felsic minerals have altered to kaolinite. The secondary minerals and the more resistant primary minerals, such as plagioclase, ilmenite, and apatite, have subsequently moved to the lower part of the saprolite. The major ferruginous clay minerals present are smectite and vermiculite, which are compositionally similar, except that the smectite is slightly richer in SiO2 and MgO and poorer in Fe2O3 than the vermiculite.To establish a structural formula for the ferruginous smectite, the oxidation state of Fe in a sample treated with dithionite-citrate-bicarbonate was examined by Mössbauer spectroscopy. All structural iron was found to be ferric. The calculated structural formula of a Na-saturated sample is:
$$N{a_{0.61}}\left( {M{g_{1.39}} + Fe_{0.85}^{3 + }A{l_{0.17}}M{n_{0.03}}} \right)\left( {S{i_{3.49}}A{l_{0.51}}} \right){O_{10}}{\left( {OH} \right)_2},$$ which has a total octahedral population of 2.44. Octahedral (Mg + Mn) exceeds octahedral (Fe3+ + Al). The 060 reflection at 1.527 Å is closer to the 1.530-Å value typical of saponite than to the 1.518-Å value typical of nontronite. The infrared spectra of the ferruginous smectite is also similar to that of saponite. Thus, the mineral is best described as a ferrian saponite. Ferroan saponite originally formed, and due to subsequent oxidation, some Fe3+ was expelled from the octahedral sheets, giving rise to a ferrian saponite containing octahedral vacancies. The expelled iron presumably formed the iron oxyhydroxides that coexist with the saponite.
Statistical Analysis of Clay Mineral Assemblages in Fault Gouges
Authors: Klima K. , Riedmüller G. , Stattegger K. 
Published: August 2006

AbstractThe clay mineral distributions in fault gouges from shear zones in several slates, phyllites, mica schists, and gneisses of the Eastern Alps were statistically analyzed for consistencies in their occurrence. Discriminant analyses suggested significant groupings of the most common minerals: illite, smectite, kaolinite, and chlorite. The clay mineral distributions in the fault gouges appeared to be related to regional geological units. No relationship, however, was found with the piles of nappes of the Alps. The influence of the mineralogical composition of the parent rock on the clay mineral assemblages appeared to be minor, but the shear behavior of the parent rocks, which is mainly a function of rock strength, was found to control the formation of the clay minerals. In hard rocks (e.g., gneisses), solution transfer at an early stage of the shear process was apparently extensive enough to favor kaolinite formation. As shearing continued, the rate of solution transfer gradually decreased and favored the formation of smectite. In softer rocks (e.g., phyllites), the extent of solution transfer during the shear process was less than in the gneisses and generated an environment that favored smectite formation, even during the early stages of shearing.
Interaction of Phenamiphos with Montmorillonite
Authors: Rodríguez J. Maza , López A. Jiménez , Bruque Sebastián 
Published: August 2006

AbstractPhenamiphos interacted with homoionic montmorillonites of Ca2+, Mn2+, Co2+, and Ni2+ to form interlayer complexes having basal spacings of about 16.5 Å. In the infrared spectra, the ν-PO bands were displaced towards lower frequencies suggesting that this group interacted with the exchange cations. Moreover, a small shoulder at 1600 cm−1 indicated the partial protonation of the phenamiphos. After heating the complexes to 110°, 160°, and 200°C, however, the bands corresponding to δ-NH2+ and ν-NH intensified because of increased protonation, whereas the ν-PO bands had the same intensity as in pure phenamiphos. The fundamental implication of these observations is that phenamiphos interacts with exchange cations through molecules of coordinated water, possibly by means of the P=O group.
Electron Transfer Processes Between Hydroquinone and Iron Oxides
Authors: Kung K.-H. , McBride M. B. 
Published: August 2006

AbstractThe kinetics of hydroquinone oxidation by aqueous suspensions of pure hematite and goethite-ferrihydrite mixtures at pH 6.0, 7.4, and 9 was studied using an on-line analysis system. The electron transfer between hydroquinone and the Fe oxides was monitored by UV-visible and electron spin resonance spectroscopy. The adsorption of organics on the Fe oxide surface was detected by Fourier-transform infrared spectroscopy. For different Fe oxides, a higher surface area was correlated with a greater oxidizing ability and greater adsorption of organics, suggesting that the oxidation reaction was a surface process. A reversal of the initially rapid redox reaction was found in this system, suggesting a delayed release of Fe2+ into solution as the reduction of the Fe oxide proceeded. Redox potential calculations confirmed the thermodynamic favorability of the reaction reversal. A distribution of the reduced state over neighboring Fe atoms on the oxide surface probably was responsible for the initial suppression of Fe2+ release into the aqueous phase. Based upon these observations and detection of the semiquinone radical as an intermediate of hydroquinone oxidation, an inner-sphere one-electron transfer mechanism for the oxidation of hydroquinone at the oxide surface is proposed.
Hypothetical Structures of Magadiite and Sodium Octosilicate and Structural Relationships Between the Layered Alkali Metal Silicates and the Mordenite- and Pentasil-Group Zeolites
Authors: Garcés Juan M. , Rocke Stephen C. , Crowder Cyrus E. , Hasha Dennis L. 
Published: August 2006

AbstractHypothetical model structures for magadiite and sodium octosilicate, based on the structure of the zeolite dachiardite, are proposed that consist of layers of 6-member rings of tetrahedra and blocks containing 5-member rings attached to both sides of the layers. The infrared (IR) and nuclear magnetic resonance spectra of magadiite and sodium octosilicate have features in common with spectra of zeolites in the ZSM-5 and mordenite groups. A peak at 1225 cm-1 in the IR spectra of magadiite and sodium octosilicate is characteristic of zeolites containing 5-member rings, such as ZSM-5- and mordenite-type zeolites. The defect structures of pentasil zeolites may therefore be akin to layered alkali metal silicates containing zeolite-like domains, in which part of the silanol groups from adjacent silicate layers are condensed (cross-linked) forming siloxane linkages.
Weathering Sequence and Alteration Products in the Genesis of the Graskop Manganese Residua, Republic of South Africa
Authors: Hawker Loraine C. , Thompson James G. 
Published: August 2006

AbstractAlthough numerous, small, manganese oxide deposits associated with dolomite in the Eastern Transvaal escarpment, Republic of South Africa, have been known for many years, their mineralogical make-up is somewhat controversial. Chemical, mineralogical, and morphological properties of the weathering products of dolomite and the coexisting manganese oxide material in the Graskop area were therefore determined. Mn and Fe occur only in minor accessory minerals in the original rock; however, in the weathering residue, these elements are concentrated and occur as separate mineral phases, chiefly birnessite, nsutite, and goethite. Thin veins of pure muscovite and quartz traverse the residua. Rare, pure calcite and maghemite nodules were noted throughout the residual manganese material. The properties of this weathering sequence suggest that the manganese wad deposits were formed in situ as a result of the congruent dissolution of dolomite, leaving a porous, sponge-like structure, highly enriched in Mn and Fe oxides.
Evaluation of the Alkylammonium Method of Determining Layer Charge
Authors: Laird D. A. , Scott A. D. , Fenton T. E. 
Published: August 2006

AbstractThe layer charge of five smectites, one vermiculitic material, and five reduced-charge clays was determined by the alkylammonium and structural formula methods. The two sets of results were found to be linearly correlated (r =.961); however, the values that were determined by the alkylammonium method were 20 to 30% lower than those determined by the structural formula method, and the regression slope for their linear relationship was 1.67. The fact that the structural formula method includes the effects of cations on the lateral edges of the clay particles probably accounted for some of the differences in the magnitude of the results but should not have caused the regression slope to deviate substantially from 1.00. Therefore, inaccurate estimates of the packing density of alkylammonium cations in the interlayer space of 2:1 phyllosilicates were deemed responsible for the systematic divergence of the results of the two methods. To satisfy the need for a relationship between the two methods of determining layer charge, an empirical means of adjusting the alkylammonium values has been proposed and shown to yield values of layer charge that are comparable to those determined by the structural formula method.