Organic Anion Adsorption on Aluminum Hydroxides: Spin Probe Studies
Authors: McBride M. B. 
Published: August 2006

AbstractThe nature of organo-phosphate and carboxylate bonding in aqueous suspensions of noncrystalline alumina, boehmite, and gibbsite has been studied using the anionic nitroxide spin probes 3-carboxy-2,2,5,5-tetramethyl-1-pyrrolidinyloxyl and 4-hydroxy-2,2,6,6-tetramethyl-piperidinooxyl dihydrogen phosphate. Analysis of the electron spin resonance (ESR) spectra of these molecules revealed that adsorption of both molecules occurred rapidly on the high surface area alumina and boehmite, whereas only the organophosphate adsorbed on gibbsite. A loss in rotational motion of the molecules accompanied adsorption, with the greater degree of motional restriction observed for the carboxylate attributed to steric restrictions to rotation about the surface-bound C-COO− bond axis. The ease of displacement of adsorbed carboxylate from surface binding sites by weakly adsorbing anions (Cl−, ClO4−) compared to organophosphate suggests that the carboxylate adsorbed by ligand exchange of a single surface OH, whereas the organophosphate probably formed a bidentate bond. The carboxylate bound on noncrystalline alumina showed evidence of nonspecific electrostatic adsorption in addition to ligand exchange of surface OH. This weak bonding was indicated by a moderate loss in rotational motion and ease of exchangeability.
Sorption Properties of Carbon Composite Materials Formed from Layered Clay Minerals
Authors: Putyera Karol , Bandosz Teresa J. , Jagiełło Jacek , Schwarz James A. 
Published: August 2006

AbstractThe sorption properties of carbon-composite materials based on montmorillonite and hydrotalcite matrices have been studied using nitrogen adsorption isotherms and inverse gas chromatography. Carbon composite materials derived from both types of inorganic precursors contain pore structure accessible for adsorbate molecules. Adsorption capacity per unit mass of these composite adsorbents is larger in the case of hydrotalcite than in montmorillonite-based materials. Exposing these materials to ambient conditions results in their hydration. Subsequent water removal by heating under vacuum increases nitrogen adsorption capacity, which is explained by the opening of the adsorption space. The water content of hydrated samples and its effect on adsorption capacity is greater for the case of hydrotalcite-based materials. No direct relationship between carbon content and adsorption properties of the materials studied is observed.
Growth of Smectite from Leached Layer During Experimental Alteration of Albite
Authors: Kawano Motoharu , Tomita Katsutoshi 
Published: August 2006

AbstractExperimental alteration of albite in deionized-distilled water at 150° to 225°C for various times up to 30 days was performed to elucidate formation processes for alteration products of albite in aqueous solution. The alteration products were examined by X-ray powder diffraction, scanning electron microscopy, transmission electron microscopy (TEM), and energy dispersive X-ray analysis (EDX). The surface compositions of albite before and after alteration were investigated by X-ray photoelectron spectroscopy (XPS). TEM clearly showed that an amorphous leached layer was produced on the albite surface at the earliest alteration stage together with small amounts of allophane. The leached layer increased successively in thickness and tended to be detached from the albite surface as alteration proceeded. Noncrystalline fibers less than 0.5 µm in length appeared within the leached layer matrix and transformed into thin flaky smectite and small amounts of K-mica. The leached layer gave electron diffraction patterns with a diffuse halo, whereas the flaky smectite displayed rings at 4.51, 2.61, and 1.54 Å. EDX confirmed that the flaky smectite consisted mainly of Si and Al, and small amounts of Na. The smectite was formed in the stability field of Na-smectite for the system of Na2O-Al2O3-SiO2-H2O.
Characterization of Mg-Saponites Synthesized from Gels Containing Amounts of Na+, K+, Rb+, Ca2+, Ba2+, or Ce4+ Equivalent to The CEC of the Saponite
Authors: Kloprogge J. Theo , Breukelaar Johan , Geus John W. , Jansen J. Ben H. 
Published: August 2006

AbstractSaponites were hydrothermally grown in the presence of amounts of NH4+, Na+, K+, Rb+, Ca2+, Ba2+, and Ce4+ equivalent with the CEC of the saponite (155 meq/100 g), with or without F−, at a temperature of 200°C for 72 hr. XRD and CEC data revealed the formation of a two-water-layer saponite with mainly Mg2+ as interlayer cation. Dehydration occurred between 25° and 450°C and dehydroxylation occurred in two steps between 450° and 790°C and between 790° and 890°C. The relatively small length of the b-axis between 9.151 and 9.180 Å is explained by considerable octahedral Al substitution (between 0.28 and 0.70 per three sites) and minor tetrahedral Al substitution (between 0.28 and 0.58 per four sites). Under the synthesis conditions applied in this study, less than 13% of the interlayer sites are occupied by Na+, K+, and Rb+; between 13.3% and 21% by Ca2+ and Ba2+; while NH4+ gives the highest value at 34%. The remaining sites are mainly filled by Mg2+. Ce4+ is not found in the saponite structure due to the formation of cerianite, CeO2. The presence of F− had little influence on the saponite composition. The formation of Mg-saponites is explained by a model in which an increased bayerite formation resulting in a higher octahedral Al3+ substitution and more Mg2+ in solution. Mg2+ is preferentially incorporated compared with the other interlayer cations due to its smallest ionic radius in combination with its 2 + charge.
Studies of the Reactivity of the Ferrihydrite Surface by Iron Isotopic Exchange and Mössbauer Spectroscopy
Authors: Rea Brigid A. , Davis James A. , Waychunas Glenn A. 
Published: August 2006

AbstractTwo-line ferrihydrite is an important adsorbent of many toxics in natural and anthropogenic systems; however, the specific structural sites responsible for the high adsorption capacity are not well understood. A combination of chemical and spectroscopic techniques have been employed in this study to gain further insight into the structural nature of sites at the ferrihydrite surface. The kinetics of iron isotopic exchange demonstrated that there are at least two types of iron sites in ferrihydrite. One population of sites, referred to as labile sites, approached iron isotopic equilibrium within 24 hr in 59Fe-NTA solutions, while the second population of sites, referred to as non-labile, exhibited a much slower rate of isotopic exchange. Adsorbed arsenate reduced the degree of exchange by labile sites, indicating that the anion blocked or greatly inhibited the rate of exchange of these sites. Mössbauer spectra were collected from a variety of samples including 56Fe-ferrihydrite samples with 57Fe in labile sites, samples containing 57Fe throughout the structure, and samples with 57Fe in non-labile sites. The spectra showed characteristic broad doublets signifying poor structural order. Refined fits of the spectra indicated that labile sites have larger quadrupole splitting, hence more local distortion, than non-labile sites. In all cases, the spectra demonstrated some degree of asymmetry, indicating a distribution of Fe environments in ferrihydrite. Overall spectral findings, combined with recent EXAFS results (Waychunas et al., 1993), indicate that labile sites likely are more reactive (with respect to iron isotopic exchange) because they have fewer neighboring Fe octahedra and are therefore bound less strongly to the ferrihydrite structure. The labile population of sites probably is composed of end sites of the dioctahedral chain structure of 2-line ferrihydrite, which is a subset of the entire population of surface sites. Mössbauer spectra of samples containing adsorbed arsenate indicated that the anion may slightly decrease the distortion of labile sites and stabilized the structure as a whole by bidentate bonding.
Clay Minerals in the MacAdams Sandstone, California: Implications for Substitution of H3O+ and H2O and Metastability of Illite
Authors: Jiang Wei-Teh , Peacor Donald R. , Essene Eric J. 
Published: August 2006

AbstractClay minerals from the MacAdams Sandstone, Kettleman North Dome, California, have been studied by electron microscopy. The clay minerals fill pore space associated with fractured and brecciated clasts of K-feldspar. Curved packets of muscovite and kaolinite are caused by deformation of detrital muscovite that resulted in opening of fissures subsequently filled with dominant kaolinite and minor intergrown mixed-layer illite/smectite (I/S). Regions of authigenic R1 I/S (rectorite) with characteristic ~20 Å periodicity are intergrown with kaolinite in microfissures within K-feldspar or detrital muscovite. Clusters of small grains of muscovite with nearly ideal composition occur as stacks and intergrown with kaolinite and are tentatively inferred to be authigenic. Contrary to previous reports, no illite was found in these samples.Electron microprobe analyses previously obtained on Kettleman Dome “illite” and subsequently used as a prime example of analyses of illite rich in excess interlayer water (H2O) and hydronium ion (H3O+) are shown to have been obtained on mixtures, and are not representative of the actual clay mineral compositions. Previous conclusions regarding significant H3O+ and H2O contents of illite are invalid because of inaccuracies inherent in bulk and EMPA analyses of illite, and do not affect arguments regarding the metastability of illite. Hydronium substitution should be favored via the reaction H2O + H+ = H3O+ only in highly acidic fluids. Ordinary illite forming in sedimentary environments with carbonates and iron oxides is unlikely to have significant H3O+ substituted for K+.
Refinement of the Nacrite Structure
Authors: Zheng Hong , Bailey Sturges W. 
Published: August 2006

AbstractNacrite crystals from a vug within a matrix of dickite at Red Mountain near Silverton, Colorado, have a = 8.906(2), b = 5.146(1), c = 15.664(3) Å, β = 113.58(3)°, V = 657.9(3) Å3, and space group Cc. The structure was solved by direct methods to determine phase angles, followed by electron density maps to locate all atoms. Refinement by least-squares ceased at R = 4.5%. Each 7 Å layer has structural detail very similar to those of dickite and kaolinite, although nacrite stacking is based on — a/3 interlayer shifts along the 8.9 Å axis (with octahedral cations alternating between the I and II sites in successive layers), whereas dickite and kaolinite are based on shifts of — a/3 along the 5.1 Å axis (with octahedral cations in the same set of sites in each layer). The angle of tetrahedral rotation is 7.8°, and the octahedral counterrotations are 7.6° and 8.1°. The H+ protons were located on DED maps. The inner 0..H1 vector points exactly toward the vacant octahedron and is depressed — 18.6° away from the level of the octahedral cations. All three surface OH groups have 0...H vectors at 50° to 66° to (001), although OH2 may not participate in interlayer hydrogen bonding. All three interlayer OH-H-O contacts are bent to angles between 132° and 141° and form contacts between 2.94 and 3.12 Å. The interlayer separation of 2.915 Å is slightly larger than in dickite, interpreted as due to a less favorable meshing of the oxygen and hydroxyl surfaces in nacrite—a direct consequence of layer shifts along the 8.9 Å axis.
Acidified Oxalate and Dithionite Solubility and Color of Synthetic, Partially Oxidized Al-Magnetites and Their Thermal Oxidation Products
Authors: Golden D. C. , Ming D. W. , Bowen L. H. , Morris R. V. , Lauer H. V. 
Published: August 2006

AbstractSubmicron-sized (~3–60 nm) powders of Al-substituted magnetite were synthesized in the laboratory by precipitation methods by mixing appropriate molar volumes FeCl2, FeCl3 and AlCl3 solutions and precipitating with 20% NH4OH. Precipitates were dialyzed for 48 hr to remove excess salts and then freeze-dried. The nominal Al mole fractions [Als = Al/(Al + Fe)] in the initial precipitate ranged from 0.001 to 0.42. Portions of the resulting powders were heated sequentially in air at 400° and 500°C. Powders were examined using X-ray diffraction (XRD), transmission electron microscopy (TEM), and visible and near-IR reflectance spectroscopy. Solubilities were determined in ammonium oxalate (pH = 3) and dithionite-citrate-bicarbonate (DCB) solutions. As determined by XRD, the mineralogy of precipitated powder samples was predominantly magnetite. Powders having Als > 0.20 contained minor goethite and a poorly crystalline iron oxide phase (ferrihydrite?), and powders having Als > 0.25 also contained gibbsite. The color of the magnetites was black throughout the range of Al-substitution. Powders heated to 400°C were reddish brown; Munsell colors ranged from 5R 2/2 to 10R 3/4 for Als from 0.1–41.5%, respectively. By XRD, these powders were maghemite, but hematite was also detected by Mössbauer spectroscopy. XRD and Mössbauer data indicate powders heated to 500°C are hematite; their Munsell colors are not noticeably different from the corresponding 400°C samples. Mean crystallite dimensions (MCDs) of the magnetite powders increase with the Al mole fraction from ~10 nm for Als = 0.001% to a maximum value of 35 nm for Als = 0.15 and decrease slightly with further increasing Al substitution. Heating magnetite powders to 400°C did not change the MCDs significantly. Heating to 500°C resulted in hematites having MCDs larger than those for corresponding precursor magnetites for Als < 0.10. The opposite is true for hematites derived from magnetites having Als > 0.10. For hematite powders with Als > 0.05, MCD decreased with increasing Al-substitution. Solubilities of powders in oxalate solutions were independent of Al content and decreased in the order unheated samples (mostly magnetite) >400°C-heated samples (maghemite + hematite) >500°C-heated samples (hematite). All powders dissolved completely in DCB. The low crystallinity of the magnetite powders and the presence of ferrous iron are responsible for their relatively high solubility in oxalate solutions.
The Microstructure of Vermicular Glaucony
Authors: McMillan Simon G. 
Published: August 2006

AbstractVermicular glaucony grains observed by transmission electron microscopy (TEM) show three irregularly alternating zones. Zone A has a high degree of linear orientation, no void space, and relatively defect-free lattice-fringe images. Zone B has an amalgamated bundle texture with a sub-parallel, linear orientation of bundles to each other and to zone A. Zone B has little or no void space, and lattice images appear to be a combination of those typical of zone C with minor amounts of modified zone A forms. Zone C has a randomly oriented, curved, and circular or semicircular bundle texture. In addition, zone C has much void space and curvilinear and linear lattice-fringe images with numerous defects, including edge dislocations. Such morphologic and crystallographic characteristics indicate that zones B and C probably comprise the glauconitic minerals of the vermicular glaucony grains, and that zone A comprises non-glauconitic micaceous minerals of higher structural order. Zone B is sharply demarcated from zone A, but B zone bundle textures merge gradationally to those of zone C. These spatial relationships suggest that zone B forms first on the surface of zone A. Sub-parallel orientation in the B zone could be produced by initial confinement between adjacent A zones. Once constraints change or are removed, the randomly oriented, curved, and semicircular or circular bundles of zone C develop.
Geology, Occurrence, and Genesis of Eskişehir Sepiolites, Turkey
Authors: Ece Ömer Içik , Çoban Fazli 
Published: August 2006

AbstractThe occurrences of sepiolite beds and nodules in alkaline and saline Miocene Eskisehir lake deposits provide unique examples of ancient lacustrine environments. Stockwork-type magnesite deposits, which were formed very close to the Miocene lake, served as parent rocks for sepiolite nodules (meerschaum). The Miocene succession consists of calcareous clay, clayey carbonate, dolomite, a gypsum-bearing calcareous clay series, siliceous tuffs, sepiolite beds, sepiolite-bearing dolomite, and basal conglomerates of ultramafic rocks. Sepiolite beds were deposited by direct precipitation from Si-supersaturated lake water under alkaline and saline conditions. They are underlain by a gypsum series. Organic matter-rich sepiolites suggest the presence of water stratification with anoxic bottom waters, which developed due to high sulphate input at the base from the ascending hydrothermal solutions along the fracture systems with extensive fresh water input near to the surface. Sepiolite nodules resulted from diagenetic replacement of magnesite pebbles at shallow burial under alkaline conditions in the vicinity of paleo-shorelines. Sepiolite beds were deposited in three ways: 1) black (up to 2.8 wt. % TOC) sepiolite beds rich in organic matter accumulated in an anaerobic paleoenvironment; 2) brown (about 0.5 wt. % TOC) sepiolite beds poor in organic matter, containing minor amounts of white, 2–6 mm long, discontinuous, and very soft dolomite laminae formed in a dysaerobic paleoenvironment; and 3) white dolomitic sepiolite beds in which dolomite content is about 20–40% in an aerobic paleoenvironment.Cyclic dolomite and gypsum series indicate hypersaline-evaporative paleoenvironments with rapid changes in lake water chemistry. These cyclic evaporatic conditions are also related to cyclic changes in water depth. Based on X-ray powder diffraction data, except degree of crystallinity, no mineralogic difference was found between sepiolite in beds and nodules. SEM studies revealed fibers about 0.2 µm wide and up to 30 µm long in sepiolite beds; crystals less than 5 µm long with bent tips; and a more compacted appearance in sepiolite nodules.
Effect of 1,4-Dioxane on the Expansion of Montmorillonite Layers in Montmorillonite/Water Systems
Authors: Wu Jun , Low P. F. , Roth C. B. 
Published: August 2006

AbstractSuspensions were produced by mixing Na-saturated, Upton montmorillonite with aqueous solutions containing different concentrations of 1,4-dioxane. Each suspension was deposited on a porous ceramic filter in an environmental chamber, and the solution was expressed from it by admitting gaseous helium to the chamber at a slightly elevated pressure. The chamber was fitted 1) with beryllium windows so that X-rays could be transmitted into and out of it and 2) with a drain so that the expressed solution could be conducted to the outside atmosphere. Once a filter cake had formed on the filter, the pressure of the gaseous helium was raised in successive increments and, after each increment, the c-axis layer spacing(s) was determined by X-ray diffraction. Increasing the concentration of 1,4-dioxane caused some of the fully expanded layers to collapse to the partially expanded state (c-axis spacing = 15 Å) and appeared to cause the remaining fully expanded layers to move farther apart, especially at the higher pressures. Alternative explanations were given for these apparently contradictory results.
Fe-Speciation in Kaolins: A Diffuse Reflectance Study
Authors: Malengreau Nathalie , Muller Jean-Pierre , Calas Georges 
Published: August 2006

AbstractDiffuse reflectance spectra of kaolins have been recorded in samples from different environments. They show the systematic presence of Fe-oxides, even in bleached kaolins, with no contribution from the Fe3+ ions substituted in kaolinite. Second derivative spectra of various Fe-phases (hematite, goethite, lepidocrocite, maghemite, akaganeite, ferrihydrite and Fe-polymer) may be differentiated by the position of a diagnostic band corresponding to the 2(6A1) → 2(4T1(4G)) transition. The systematic comparison of diffuse reflectance spectra of unbleached and bleached kaolins has demonstrated the differences between the Fe-oxides occurring as coatings and as occluded phases. The features observed in second derivative spectral curves are consistent with assignments of crystal field transitions to goethite, hematite, akaganeite, and aged hydrous ferric oxides. The optical determination of the Fe-phases associated to kaolins assists in the interpretation of the formation conditions of these minerals.
Preparation and Characterization of Montmorillonites Pillared by Cationic Silicon Species
Authors: Fetter Geolar , Tichit Didier , Massiani Pascale , Dutartre Roger , Figueras François 
Published: August 2006

AbstractThe hydrolysis of 2-(2-trichlorosilylethyl)pyridine (TCSEP) or 3-aminopropyltrimethoxysilane (APTMS) yields a complex mixture of oligomers, the composition of which is a function of time. 29Si NMR measurements show that the same oligosilsesquioxanes can be obtained from both compounds after prolonged hydrolysis. Ion exchange by montmorillonite with the pillaring solution obtained from TCSEP results in partial intercalation, with a noticeable fraction of the clay exchange sites occupied by protons not by the Si cationic species. Calcination of this pillared clay results in a mixture of phases showing 1.86 or 1.56 nm basal spacings. Pillaring of the same montmorillonite by the solution obtained by partial hydrolysis of APTMS results in a homogeneous solid with a basal spacing of 2 nm, which reduces to 1.65 nm upon calcination above 773 K. The microporous volume (pores < 1 nm) of these Si-clays, determined after calcination at 773 K, 0.15 ml/g for the PILC obtained from TCSEP, and 0.186 ml/g for the PILC obtained from APTMS is comparable to that measured for Al or Zr pillared clays. A better thermal stability is observed for the clay pillared by APTMS, which retains a large microporosity (0.167 ml/g) up to 973 K in air. These Si-pillared clays show a small number of weakly acidic sites and some strongly acidic sites retaining ammonia up to 723 K, which are most likely localized on the clay layers.
Synthesis and Properties of Hexacyanoferrate Interlayered in Hydrotalcite. I. Hexacyanoferrate(II)
Authors: Hansen Hans Christian Bruun , Koch Christian Bender 
Published: August 2006

AbstractHydrotalcite (HT) interlayered with hexacyanoferrate(II) ions ([Mg4.62Al1.52(OH)12][(Fe(CN)6)0.30-(CO3)0.29]) has been synthesized from the carbonate-HT ([Mg4.52Al1.50(OH)12][(CO3)0.77]) through double ion exchange reactions, and the products have been studied by chemical and physical methods. Mössbauer spectroscopy shows that hexacyanoferrate(II) is held rigidly in the interlayer by electrostatic forces and is characterized by a singlet at 0.01 mm s−1at 80 K. X-ray diffraction shows an increase of the basal spacing (d003from 0.78 to 1.1 nm following exchange. Hexacyanoferrate(II) in the interlayer was oxidized to hexacyanoferrate(III) (up to 20%) by dioxygen on dehydrating the interlayer either by drying at 70°C or by washing with nonaqueous solvents like acetone or ethanol. The CN (ν6) band of hexacyanoferrate(II) and (III) is found at 2036 cm−1and 2112 cm−1, respectively. The presence of an absorption band at 2080 cm−1, assigned to free cyanide anions in the interlayer, suggests that the hexacyanoferrate(II,III) complexes are not inert in the interlayer, cyanide ligands being substituted with either water or hydroxyls. Oxidation and ligand exchange of the hexacyanoferrate(II) are also indicated by Mössbauer spectroscopy.