Creep-Fatigue Interaction in Grade 92 Steel and Its Predictability
Authors: Takahashi Yukio , Parker Jonathan , Gandy David 
Published: March 2024

Abstract
Creep rupture strength is the principal material property prioritized in designing power generation plants against the steady-state stress due to internal pressure. Increasingly plants must cycle so there is a possibility of life reduction due to creep-fatigue interaction. Grade 92 steel is one of the creep strength enhanced ferritic (CSEF) steels which has superior creep strength compared to other CSEFs. It is expected to be widely used in coal-fired ultra-super critical plants as well as in LNG-fired combined cycle plants. However, at present there is insufficient information regarding the creep-fatigue behavior of this material. A joint study has been conducted to understand the behavior of this steel under creep-fatigue condition and see how accurate the failure life can be estimated. Three kinds of base materials as well as two kinds of welded joints have been tested under strain-controlled cyclic loading with or without hold times as well as under constant load creep condition. Continued decrease in the number of cycles to failure was observed with the extension of hold time in all the base metals and cross-weld specimens. It was found that the modified ductility exhaustion approach based on inelastic strain, as well as its extension employing the inelastic strain energy density, made reasonably accurate predictions of failure lives under a wide range of test conditions. Temperature- and rate-dependencies of fracture limits in terms of inelastic strain and energy density were able to be uniquely expressed using simple thermal activation energy parameters.
Evaluation of Long-Term Creep Rupture Life of Strength Enhanced High Cr Ferritic Steel on the Basis of Its Temperature Dependence
Authors: Maruyama K. , Nakamura J. , Yoshimi K. 
Published: March 2024

Abstract
Conventional time-temperature-parameter (TTP) methods often overestimate long-term creep rupture life of creep strength enhanced high Cr ferritic steels. The cause of the overestimation is studied on the basis of creep rupture data analysis on Gr.91, 92 and 122 steels. There are four regions with different values of stress exponent n for creep rupture life commonly in stress-rupture data of the three ferritic steels. Activation energies Q for rupture life in the regions take at least three different values. The values of n and Q decrease in a longer-term region. The decrease in Q value is the cause of the overestimation of long-term rupture life predicted by the conventional TTP methods neglecting the change in Q value. Therefore, before applying a TTP method creep rupture data should be divided into several data sets so that Q value is unique in each divided data set. When this multi-region analysis is adopted, all the data points of the steels can be described accurately, and their long-term creep life can be evaluated correctly. Substantial heat-to-heat and grade-to-grade variation in their creep strength is suggested under recent service conditions of USC power boilers.
Evaluation of Supercritical Oxidation Resistance of Boiler Tube Materials
Authors: Yli-Olli Sanni , Tuurna Satu , Penttilä Sami , Auerkari Pertti , Zabetta Edgardo Coda , Vänskä Kyösti 
Published: March 2024

Abstract
To improve the efficiency of fossil fuel power plants the operating temperatures and pressures need to be increased. However, at high temperatures the steam side oxidation resistance becomes a critical issue for the steels used especially at the final stages of superheaters and reheaters. Apart from the chemical composition of the material, surface condition is a major factor affecting the oxidation resistance in steam and supercritical water. In this paper, stainless boiler steels (UNS S34710, S31035, S31042, and S30942) are investigated for oxidation resistance in flowing supercritical water. Tests were conducted in an autoclave environment (250 bar, with 125 ppb dissolved oxygen and a pH of 7) at 625°C, 650°C and 675°C for up to 1000 h. Materials were tested with as-delivered, shot peened, milled or spark eroded and ground surface finish. The results show a strong influence of surface finish at the early stages of oxidation. Oxides formed on cold worked surfaces were more adherent and much thinner than on a spark eroded and ground surface. This effect was stronger than the influence of temperature or alloy composition within the tested ranges.
Steam Loop Testing of A-USC Materials for Oxidation and Fireside Corrosion - Alstom’s Experience to Date
Authors: Ganta Reddy , Marion John , Wilhelm Bruce , Pschirer Jim , Goodstine Steve , Boohaker Charles 
Published: March 2024

Abstract
Nickel-based alloys and stainless steel Super304H, along with various coatings, are undergoing testing in a steam loop at Alabama Power’s Plant Barry. These materials are being evaluated for use in advanced ultra-supercritical (A-USC) fossil-fired power plants at temperatures ranging from 538°C to 815°C. The loop has been operational for over 18 months, with the alloys exceeding 6,300 hours above 538°C. An additional 7,000 hours at high temperatures are planned before the loop’s removal in 2014. Initial inspections show minimal material corrosion, suggesting their suitability for A-USC applications. This paper details the loop’s design, materials, manufacturing, operation, and inspection findings. Additionally, it describes a methodology for predicting steam-side oxidation and fireside corrosion rates and highlights the significance of this testing for A-USC development and commercialization.
Effect of Alloy Composition on Fireside Corrosion Rates in Air- and Oxy-Fired Systems
Authors: Pint B.A. 
Published: March 2024

Abstract
Using oxygen, rather than air, in coal-fired boilers has been studied for several years as a strategy to reduce NOx and concentrate CO2 for capture. In combination with flue gas recirculation, higher levels of CO2 are expected but increased H2O and SO2 levels also may occur. In order to understand the role of substrate composition on corrosion, a combination of commercial and model alloys were investigated with synthetic coal ash and gas compositions simulating air- and oxyfiring environments. Exposure temperatures ranged from 600°-800°C to cover current operating temperatures up to advanced ultrasupercritical conditions. Using 500h exposures, no consistent negative effect was found for switching to the oxy-firing environment with the same synthetic ash. For model Fe-Cr alloys, 30%Cr was needed to form a thin protective reaction product across this temperature range. Among the commercial stainless steels, 310-type stainless steel showed low reaction rates with the maximum attack at 650°C. At higher temperatures, the depth of attack on Fe-base type 310 stainless steel was less than for Ni-base alloy 740. Initially, this difference was attributed to the Al and Ti additions in alloy 740. However, cast and hot rolled model Ni-18Cr and -22Cr alloys with various Al and Ti additions showed decreased metal loss with increasing Al and Ti additions in the oxy-firing environment at 700° and 800°C. As expected, metal loss was very sensitive to Cr content. A second set of model alloys also examined the effect of Co and Mo.
Study of Creep Damage in Creep Exposed Martensitic High-Chromium Steel Weldments
Authors: Schlacher C. , Béal C. , Sommitsch C. , Toda H. , Mayr P. 
Published: March 2024

Abstract
Boron and nitride additions are emerging as a promising design concept for stabilizing the microstructure of creep-resistant martensitic high-chromium steels. This approach, known as MarBN steel (martensitic steel strengthened by boron and nitrogen), combines the benefits of solid solution strengthening from boron with precipitation strengthening from nitrides. However, initial welding trials revealed challenges in achieving a uniform fine-grained region in the heat-affected zone (HAZ), which is crucial for mitigating Type IV cracking and ensuring creep strength. Despite these initial hurdles, preliminary creep test results for welded joints have been encouraging. This study presents an improved MarBN steel formulation and its investigation through uniaxial creep tests. Base material and welded joints were subjected to creep tests at 650°C for up to 25,000 hours under varying stress levels. The analysis focused not only on the creep strength of both the base material and welded joints but also on the evolution of damage. Advanced techniques like synchrotron micro-tomography and electron backscatter diffraction were employed to understand the underlying creep damage mechanisms. By combining long-term creep testing data with 3D damage investigation using synchrotron micro-tomography, this work offers a novel perspective on the fundamental failure mechanisms occurring at elevated temperatures within the HAZ of welded joints in these advanced steels.
Creep Properties of Heat Affected Zone in Heterogeneous Welded Rotor
Authors: Dzugan Jan , Novy Zbysek , Konopik Pavel , Podany Pavel , Folková Eva 
Published: March 2024

Abstract
Increasing demand on efficiency and power output of steam generators leads to new designs of welded rotors. The reason for rotor welding is the large size of rotors, which are difficult to produce in a single piece. Secondly, as there are varying operation conditions along the rotor length. In a heterogeneous rotor, several materials appropriate for local service conditions can be used. At the rotor service temperatures, creep properties are crucial for successful design. The weakest point of every welded component is the heat affected zone. Therefore, the creep properties of a heterogeneous weld are subject of the investigation herein the current study, a heterogeneous weld of COST F and COST FB2 materials is investigated. The welding was performed by multi pass technique with overlaying welding beads that applied several heating cycles to heat affected zone. Metallographic investigation of the weld was performed and the weakest microstructure spots were detected. With the use of FEM simulation, appropriate heating/cooling cycles were obtained for the detected weak points. The temperature cycles obtained were subsequently applied to both base materials under laboratory conditions by induction heating. Creep properties of these materials were investigated. The influence of the initial base material’s grain size was also considered in the investigation. Two heating/cooling schedules were applied to both base materials with two grain sizes. Altogether, 8 different microstructures were examined in short term creep tests and the results were summarized.
Investigations on the Degradation Mechanism of Welded Joints of Advanced 9%Cr-Mo-Co-B Steel Used for 620°C USC Steam Turbine
Authors: Gong Xiufang , Gao Zhenhuan , Nie Liping , Zhang Bo , Jiang Lei , Zhang Bangqiang , Yang Gongxian , Zhang Congping 
Published: March 2024

Abstract
The creep rupture properties of welded joints of advanced 9%Cr-Mo-Co-B steel used for 620°C USC steam turbine have been studied. The welded joints were prepared by means of shielded metal arc welding (SMAW). A lot of creep tests have been conducted and the results indicate that fracture usually occurs in the intercritical heat affected zone (ICHAZ) of the welded joint and is typical of Type IV cracking. The microstructure of the HAZ has been investigated by using optical microscopy, SEM and TEM. The degradation mechanism of welded joint of the 9%Cr-Mo-Co-B steel has been explored by analysing the phases of precipitates. Creep voids were observed in the vicinity of the coarse Laves phase particles, resulting in the degradation of the creep rupture properties.
Creep Degradation and Life Assessment of High Temperature Welds
Authors: Masuyama Fujimitsu , Yamaguchi Tomiko 
Published: March 2024

Abstract
In order to improve thermal efficiency of fossil-fired power plants through increasing steam temperature and pressure high strength martensitic 9-12%Cr steels have extensively been used, and some power plants have experienced creep failure in high temperature welds after several years operations. The creep failure and degradation in welds of longitudinally seam-welded Cr- Mo steel pipes and Cr-Mo steel tubes of dissimilar metal welded joint after long-term service are also well known. The creep degradation in welds initiates as creep cavity formation under the multi-axial stress conditions. For the safety use of high temperature welds in power plant components, the complete understanding of the creep degradation and establishment of creep life assessment for the welds is essential. In this paper creep degradation and initiation mechanism in welds of Cr-Mo steels and high strength martensitic 9-12%Cr steels are reviewed and compared. And also since the non-destructive creep life assessment techniques for the Type IV creep degradation and failure in high strength martensitic 9-12%Cr steel welds are not yet practically established and applied, a candidate way based on the hardness creep life model developed by the authors would be demonstrated as well as the investigation results on the creep cavity formation behavior in the welds. Additionally from the aspect of safety issues on welds design an experimental approach to consider the weld joint influence factors (WJIF) would also be presented based on the creep rupture data of the large size cross-weld specimens and component welds.
Effect of Non-Standard Heat Treatments on Creep Performance of Creep-Strength Enhanced Ferritic (CSEF) Steel Weldments
Authors: Yamamoto Yukinori , Santella Michael L. , Yu Xinghua , Suresh Babu Sudarsanam 
Published: March 2024

Abstract
This paper summarizes recent efforts to improve creep performance in Grade 91 (Mod. 9Cr-1Mo, ASTM A387) steel weldments via non-standard heat treatments prior to welding. Such heat treatments offer a potential solution for minimizing Type IV failures in creep strength enhanced ferritic (CSEF) steels. A lower temperature tempering (LTT, 650°C) of the 9Cr steels prior to gas tungsten arc welding (GTAW) resulted in improved creep-rupture life at 650°C compared to the samples tempered at a standard condition (HTT, 760°C) before welding. From detailed characterization of precipitation kinetics in the heat affected zone, it was hypothesized that M23C6 carbides in the fine-grain heat-affected zone (FGHAZ) in the LTT sample were fully dissolved, resulting in re-precipitation of strengthening carbides during post weld heat treatment (PWHT). This was not the case in the HTT sample since M23C6 in the FGHAZ was only partially dissolved prior to welding, which caused coarsening of existing M23C6 after PWHT and premature creep failure in the FGHAZ. However, it was also found that the LTT raised the ductile-brittle transition temperature above room temperature (RT). Two different thermo-mechanical treatments (TMTs); two-step tempering and aus-forging/aus-aging, of the modified 9Cr-1Mo steels were attempted, in order to control the balance between creep properties and RT ductility, through control of precipitation kinetics of the M23C6 carbides and/or MX carbo-nitrides. The hardness map of the TMT samples after GTAW and PWHT were evaluated.
Precipitation Strengthening by the Nitrides in High Cr Containing Ferritic Creep Resistant Steels
Authors: Shinozaki Ippei , Hasegawa Yasushi 
Published: March 2024

Abstract
High nitrogen steel was manufactured by solid state nitriding and Laminate- rolling at laboratory to study the nitride morphology and creep properties through the TEM, EPMA and creep strain test. Nitriding made the nitride dispersing steels possible. Solid state nitriding of thin plates and those laminate rolling enabled the high nitrogen containing thick plate steel. Precipitated coarse nitrides during the nitriding resolved by normalizing and re-precipitated by tempering finely. Needle type VN was detected in V containing high nitrogen steels. Its coherency seems to affect the creep strength significantly. V precipitated steels indicated the higher creep strength than the steels without VN precipitation. Thermodynamically stable precipitates like VN increases the creep rupture strength. Ti and Zr containing high nitrogen steels also will be evaluated and discussed by the presentation.
Precipitation Process of Z-Phase in 9-12%Cr Steels
Authors: Danielsen Hilmar Kjartansson 
Published: March 2024

Abstract
Precipitation of Z-phase, Cr(V,Nb)N, is known to negatively affect creep properties of 9-12%Cr steels for power plant applications as it dissolves finely distributed MX particles, (V,Nb)N, especially in high Cr steels. As the Z-phase precipitates slowly as large particles, this causes a net drop in precipitation strengthening. Two model alloys containing 9 and 12%Cr, but otherwise having similar composition, were produced in order to quantify the difference in Z-phase precipitation speed at different Cr levels. The nitride precipitation behavior was followed at different temperatures using TEM and XRD, allowing for a quantification of the Z-phase precipitation. The Z-phase was found to precipitate 20-50 times faster in the 12%Cr steel compared to 9%Cr steel in the temperature range 600- 650°C. The transformation of MX into Z-phase was followed in a Ta containing alloy without V or Nb. In this alloy the Z-phase precipitates very quickly, and thus appears as finely distributed particles which have the same strengthening effect as MX particles. Investigations using atomic resolution microscopy showed how Cr diffuses from the matrix into the TaN MX particles and gradually transforms them both chemically and crystallographically into Z-phase CrTaN particles.
Alloy Design of Tempered Martensitic 9Cr-Boron Steel for A-USC Boilers
Authors: Abe F. , Tabuchi M. , Tsukamoto S. , Liu Y. 
Published: March 2024

Abstract
The addition of boron without the formation of any boron nitrides during normalizing heat treatment at high temperature minimizes the degradation in creep strength of both base metal and welded joints of 9Cr steel at 650 °C and long times. The enrichment of soluble boron near prior austenite grain boundaries (PAGBs) by the segregation is essential for the reduction of coarsening rate of M23C6 carbides in the vicinity of PAGBs, enhancing boundary and subboundary hardening, and also for the production of same microstructure between the base metal and heat-affected-zone (HAZ) in welded joints, indicating no Type IV fracture in HAZ. Excess addition of boron and nitrogen promotes the formation of boron nitrides during normalizing, which reduces the soluble boron concentration and accelerates the degradation in creep rupture ductility at long times. 9Cr- 3W-3Co-VNb steel with 120 - 150 ppm boron and 60 - 90 ppm nitrogen (MARBN) exhibits not only much higher creep strength of base metal than Gr.92 but also substantially no degradation in creep strength due to Type IV fracture at 650 °C. The pre-oxidation treatment in Ar gas promotes the formation of protective Cr2O3 scale on the surface of 9Cr steel, which significantly improves the oxidation resistance in steam at 650 °C.
Modelling and Optimizing Precipitation in Creep Resistant Austenitic Steel 25Cr-20Ni-Nb-N
Authors: Stojan Vujic , Coline Beal , Christof Sommitsch , Farooq Muhammad , Rolf Sandström , Joanna Zurek 
Published: March 2024

Abstract
25Cr-20Ni-Nb-N (Tp310HCbN) steel is a promising austenitic steel for applications in superheater tubes in coal fired thermal power plants due to the high creep strength and oxidation resistance. In this work, the microstructural evolution of this material during heat treatment and thermal ageing has been investigated. The investigations were carried out by Light Optical Microscopy (LOM), Scanning Electron Microscopy (SEM), Transmission Electron Microscopy (TEM) and Energy Dispersive Spectroscopy (EDS). Besides, equilibrium and Scheil calculations were carried out using the thermodynamic software MatCalc to analyse the stable phases and the solidification process, respectively. Precipitation calculations during solution annealing and subsequent ageing at 650 and 750°C were performed to predict the phase fraction and precipitates radius up to 10.000h ageing time. SEM and TEM investigations of aged specimens revealed the presence of six different precipitates: M23C6, Cr2N, sigma, Z-phase, eta-phase (Cr3Ni2Si(C,N)) and Nb(C,N). These precipitates were predicted and confirmed by MatCalc simulations. The calculated phase fraction and mean radius show good agreement with experimental data. Finally, simulations of different Cr-, C- and N-content in Tp310HCbN were performed.
Development of Boiler Risk Management and Life Prediction System
Authors: Yaojun Li , Dapeng Wang , Shuxue Li 
Published: March 2024

Abstract
Addressing the growing concern of supercritical and ultra-supercritical boilers as potential safety hazards in power plants, a new Boiler Risk Management and Life Prediction System (BRMLPS) has been developed. This system leverages risk-based inspection and assessment techniques alongside life prediction and management methods. The BRMLPS focuses on evaluating and ranking the risk associated with critical boiler components, such as heating surfaces, headers, and drums. This risk assessment allows for the development of targeted and efficient inspection plans and repair strategies, ultimately aiming to minimize accident rates, reduce potential losses, and optimize safety investments. By implementing this system, power plants can achieve maintenance optimization, balancing safety and economic considerations for their specialized equipment.
Harmonizing of Creep-Fatigue Test Methods through Development of ASTM Standards
Authors: Saxena Ashok , Kalyanasundaram Valliappa , Narasimhachary Santosh B. , Holdsworth Stuart R. 
Published: March 2024

Abstract
Creep-fatigue crack formation (endurance) and crack growth rate data are necessary inputs for assessing the structural integrity and for estimating the design life of high temperature components in power generation and aircraft engine industries. Ensuring consistency in the reported test data, as well as an understanding of the inherent scatter and its source in the data, are both necessary for assuring quality and limitations of the analyses that rely on the data. In 2008, the American Society for Testing and Materials (ASTM) under the umbrella of its subcommittees E08.05 on Cyclic Deformation and Crack Formation and E08.06 on Crack Growth, and the sponsorship of Electric Power Research Institute (EPRI) through its international experts’ working group on creep-fatigue embarked on the task of developing separate standard test methods for creep-fatigue crack formation and creep-fatigue crack growth. The first standard entitled, “E-2714-09: Standard Test Method for Creep-fatigue Testing” was developed in 2009 and was followed up with a round-robin consisting of 13 laboratories around the world for testing the newly developed standard. This paper discusses the results of this round-robin concluded in 2012 using the widely used P91 steel that led to the formulation of the Precision and Bias statement contained in the version of the ASTM standard E2714 that was successfully balloted in the year 2013.