Authors: Batu M. S. , Kolo M. G. , Kolo M. M. , Saka A. R. 
Published: May 2024

Telah dilakukan penelitian tentang adsorpsi logam kalsium (Ca) dan magnesium (Mg) dalam air tanah menggunakan arang aktif dari limbah sabut pinang. Penelitian ini bertujuan untuk mengetahui karakteristik dari arang aktif, waktu kontak dan massa adsorben optimum pada proses adsorpsi logam Ca dan Mg dalam air tanah menggunakan arang aktif limbah sabut pinang. Pembuatan arang aktif dilakukan melalui 2 tahapan yaitu tahap karbonasi yang dilakukan pada suhu 400 oC selama 15 menit dan tahap aktivasi kimia menggunakan NaOH 1,5 M selama 24 jam. Proses adsorpsi menggunakan metode batch dengan variasi waktu kontak 30; 60; 90; 120 dan 180 menit dan massa adsorben 0,5; 1; 1,5; 2 dan 2,5 gram. Berdasarkan hasil penelitian diperoleh arang aktif dari sabut pinang memiliki kadar air sebesar 8,13%, kadar abu 13,43%, daya serap terhadap iodin sebesar 1.179,98 mg/g dan analisis gugus fungsi menggunakan FTIR menunjukkan adanya gugus O–H, C–H alifatik dan aromatik, gugus C?O, dan C?C. Waktu kontak optimum pada proses adsorpsi menggunakan arang aktif limbah sabut pinang terhadap logam Ca dan Mg adalah pada waktu 120 menit dengan efisiensi adsorpsi untuk logam Ca sebesar 49% dan 73% untuk logam Mg, sedangkan massa adsorben optimum pada proses adsorpsi adalah pada massa 1,0 gram dengan efisiensi adsorpsi 48% untuk logam Ca dan 72% untuk logam Mg. Penelitian ini memberikan kontribusi dalam meningkatkan pengetahuan mengenai penanganan logam kalsium dan magnesium dalam air tanah dengan memanfaatkan limbah sabut pinang sebagai adsorben.
Kata kunci: limbah sabut pinang, arang aktif, adsorpsi, kalsium, magnesium.
ABSTRACT
The research has been carried out on the adsorption of calcium (Ca) and magnesium (Mg) metals in groundwater using activated charcoal from areca coir waste. This study aims to determine the characteristics of activated charcoal, contact time and optimum adsorbent mass in the adsorption process of Ca and Mg metals in groundwater using activated charcoal from areca coir waste. The production of activated charcoal was done in 2 stages, namely the carbonation stage, which was carried out at 400 oC for 15 minutes and the chemical activation stage, using 1.5 M NaOH for 24 hours. The adsorption process used a batch method with a variation of contact time of 30; 60; 90; 120, and 180 minutes and the adsorbent mass was 0.5; 1; 1.5; 2 and 2.5 grams. Based on the research results, it was found that activated charcoal from areca nut has a moisture content of 8.13%, ash content of 13.43%, absorption of iodine of 1,179.98 mg/g and functional group analysis using FTIR showed the presence of O–H, C–H aliphatic and aromatic, C?O, and C?C groups. The optimum contact time in the adsorption process using activated charcoal from areca and Mg waste for Ca and Mg metal was 120 minutes, with adsorption efficiency for Ca metal of 49% and 73% for Mg metal, while the optimum adsorbent mass in the adsorption process was at mass 1, 0 gram with adsorption efficiency of 48% for Ca metal and 72% for Mg metal. This research contributes to increasing knowledge regarding handling calcium and magnesium metals in groundwater by utilizing areca coir waste as an adsorbent.
Keywords: areca coir waste, activated charcoal, adsorption, calcium, magnesium