The Dynamics of Active Metal Catalysts Revealed by In‐Situ Electron Microscopy
Authors: Cao Jing , Farra Ramzi , Wang Zhu‐Jun , Rinaldi Ali , Schlögl Robert , Willinger Marc Georg 
Published: December 2016

Conventional high‐resolution imaging by electron microscopy plays an important role in the structural and compositional analysis of catalysts. However, since the observations are generally performed under vacuum and close to room temperature, the obtained atomistic details describe an equilibrium state that is of limited value when the active state of a catalyst is in the focus of the investigation. Since the early attempts of Ruska in 1942 [1],
in situ
microscopy has demonstrated its potential and, with the recent availability of commercial tools and instruments, led to a shift of the focus from ultimate spatial resolution towards observation of relevant dynamics. [2]

During the last couple of years we have implemented commercially available sample holders for
in situ
studies of catalysts in their reactive state inside a transmission electron microscope. In order to relate local processes that occur on the nanometer scale with collective processes that involve fast movement of a large number of atoms, we have furthermore adapted a commercial environmental scanning electron microscope (ESEM) for the investigation of surface dynamics on active catalysts. Using these two instruments, we are now able to cover a pressure range from 10
−4
to 10
3
mbar and a spatial resolution ranging from the mm to the sub‐nm scale by in situ electron microscopy.

Presently we are investigating the behavior of metal catalysts during hydrocarbon partial oxidation and decomposition reactions as well as structural dynamics during oscillatory red‐ox reactions.
The observations are performed in real‐time and under conditions in which the active state of the catalyst can be monitored by on‐line mass spectroscopy. The latter is of upmost importance, since the key requirement is to observe relevant processes and dynamics that are related to catalytic function.

The ability to directly image the active catalyst and associated morphological changes at high spatial resolution enables us to refine the interpretation of spatially averaged spectroscopic data that was obtained under otherwise similar reaction conditions, for example during near‐ambient‐pressure
in situ
XPS measurements. [3]

It will be shown that the ability of observing the adaption of an active surface to changes in the chemical potential of the surrounding gas phase in real‐time potentially offers new and direct ways of optimizing catalysts and applied reaction conditions. One of the examples that will be demonstrated is the dynamic state of copper, where the simultaneous and very dynamic formation of oxidized and reduced islands is observed during red‐ox conditions in different atmospheres and on different length scales (Figure 1). Direct observation of active catalysts, such as shown in this contribution, will have a big impact on our understanding of their function. It is already clear that some of the assumptions that were published in the catalysis literature on the basis of TEM observations made in vacuum, have to be revised.