PENGARUH FRAKSI VOLUME KOMPOSIT SERBUK CANGKANG KELAPA SAWIT/EPOKSI TERHADAP KEKERASAN DAN LAJU KEAUSAN
Authors: Perdana Mastariyanto 
Published: May 2019

<p><em>Natural composite is one of materials that have been </em><em>utilized</em><em> in the </em><em>engineering </em><em>field. Utilization of</em><em> </em><em>natural composite is </em><em>due to nature of</em><em> environment</em><em>ally friendly</em><em> and </em><em>better on </em><em>mechanical properties. The </em><em>aim</em><em> of this study was determine the effect of </em><em>volume </em><em>fraction of composite-based oil palm shell powder to hardness and wear rate. In this study, the main </em><em>materials </em><em>of composite are </em><em>oil </em><em>palm shells as a </em><em>reinforcement</em><em> and epoxy resin as binder</em><em>s</em><em>. </em><em>Oil p</em><em>alm shells are crushed into powder with size 420-595 μm. </em><em>Va</em><em>riation </em><em>of </em><em>volume fraction between oil palm shell and epoxy </em><em>are</em><em> 45%:55%, 50%:50% </em><em>and </em><em>55%:45%. The results showed that composite hardness was increasing with the addition of oil palm shell powder composition. Hardness of composites </em><em>based oil palm </em><em>shell</em><em> powder/</em><em>epoxy at volume fractions of 45%:55%, 50%</em><em>:</em><em>50% </em><em>and </em><em>55%:45% </em><em>are </em><em>10.69 V</em><em>H</em><em>N, 11.64 V</em><em>H</em><em>N, and 12.36 </em><em>VH</em><em>N</em><em>, </em><em>respectively. </em><em>W</em><em>ear rate of composites decreases with the addition of oil palm shell composition. </em><em>W</em><em>ear rate of composite </em><em>based oil palm</em><em> shell</em><em> </em><em>powder/epoxy at a volume fraction of 45%:55%, 50%:50% </em><em>and </em><em>55%:45% </em><em>are</em><em> 4.7 x 10</em><em><sup>-7</sup></em><em> g/mm</em><em><sup>2</sup></em><em>.</em><em>s</em><em>, 2.5 x 10</em><em><sup>-7</sup></em><em> g/mm</em><em><sup>2</sup></em><em>.</em><em>s</em><em>, and 1.9 x 10</em><em><sup>-7</sup></em><em> g/mm</em><em><sup>2</sup></em><em>.</em><em>s, </em><em>respectively.</em><em> Analysis of fracture surface of composite has been done using Scanning Electrone Microscope. </em></p><p> </p><p class="ListParagraph1">Komposit alam merupakan salah satu material yang telah dimanfaatkan pada bidang keteknikkan. Pemanfaatan komposit alam ini tidak terlepas dari sifat ramah terhadap lingkungan dan sifat mekanik yang relatif baik. Tujuan penelitian ini adalah untuk mengetahui pengaruh dari fraksi volume komposit berbahan dasar serbuk cangkang kelapa sawit terhadap kekerasan dan laju keausan. Pada penelitian ini, bahan utama dari material komposit adalah cangkang kelapa sawit sebagai pengikat (<em>reinforcement</em>) dan resin epoksi sebagai pengikat (<em>binder</em>). Cangkang kelapa sawit dihaluskan menjadi serbuk dengan ukuran 420-595 µm. Variasi fraksi volume antara cangkang kelapa sawit dan epoksi adalah 45%:55%, 50%:50%, dan 55%:45%. Hasil penelitian menunjukkan bahwa kekerasan komposit semakin meningkat dengan penambahan komposisi serbuk cangkang kelapa sawit. Kekerasan dari komposit serbuk cangkang/epoksi pada fraksi volume 45%:55%, 50%:50% dan 55%:45% berturut-turut sebesar 10.69 VHN, 11.64 VHN, dan 12.36 VHN. Laju keausan dari komposit semakin menurun dengan penambahan komposisi serbuk cangkang kelapa sawit. Laju keausan dari komposit serbuk cangkang/epoksi pada fraksi volume 45%:55%, 50%:50% dan 55%:45% berturut-turut sebesar 4.7 x 10<sup>-7</sup> g/mm<sup>2</sup>.dt, 2.5 x 10<sup>-7</sup> g/mm<sup>2</sup>.dt, dan 1.9 x 10<sup>-7</sup> g/mm<sup>2</sup>.dt. Pengamatan permukaan patahan dari komposit telah dilakukan menggunakan <em>Scanning Electron Microscope</em> (SEM).</p>