Electrochemical and Impedance Investigation of Ni-Rich LiNi1-x-YCoxAlyO2 Cathode Material for Lithium-Ion Batteries
Authors: Jin En Mei , Lee Min Woo , Jeong Sang Mun 
Published: February 2020

Recently, the lihtium-ion batteries (LIBs) are applied from the power sources of portable electronic devices to large-scale energy storage devices such as electrical vehicles (EVs), hybrid electric vehicles (HEVs), plug-in hybrid electric vehicles (PHEVs), and energy storage system (ESS), based on the cost, safety, and energy density. LiNiO2 has been considered as a promising cathode material for large-scale LIBs due to its low cost and high specific capacity (275 mAh/g) [1]. However, it has several problems, such as difficult synthesis, low thermal stability in chaged state, and capacity fading upon long-term cycling. In order to overcome these problems, several partial substitutions (Co, Mn, Fe, Al, etc.) for nickel have been investigated [2-5]. Among those partial subtitutions, Co has been proven to be a promising cadidate for LIB due to the improved thermal stability of LiNiO2 in the delithiated state. In addition, it was reported that a small amount of Al3+ doping leads to retain Ni in 3+ state and as a result, the stabilization of layerd structure and electrochemical properties of LiNi1-xCoxO2 is improved [6].
In this work, LiNi1-x-yCoxAlyO2 (0.08≤x≤0.15, 0.15≤y≤0.05) powders were prepared by a co-precipitation method in aqueous solution to employ as a cathode material for Li-S batteries. Ni1-xCox(OH)2 precursor was firstly prepared by co-precipitation and then aqueous solution containing Al was added in Ni1-xCox(OH)2 precursor. The pH of Al solution was controlled in a range of 8-10. Final solution was filtered, washed and dried. LiNi1-x-yCoxAlyO2 cathode materials were obtained after calcining Ni1-x-yCoxAly(OH)2 with LiOH (Li/M=1~1.1) under air atmosphere at 700 oC for 20 h. For electrode fabrication, LiNi1-x-yCoxAlyO2 cathode materials, super-P carbon black, and polyvinylidene fluoride (PVdF, Mw: ~ 400,000, Sigma Aldrich) were ground with N-methyl-2-pyrrolidone (NMP, SAMCHUN PURE CHEMICAL) as a solvent. Lithium foil, polyethylene (PE, W-SCOPE, KOREA), and 1.15M LiPF6/EC-EMC (3:7) were used as a counter electrode, separator, and electrolyte, respectively. The morphology of LiNi1-x-yCoxAlyO2 cathode material was characterized using a field emission-scanning electron microscopy (FE-SEM, Carl Zeiss, LEO-1530) and focused ion beam milling (FIB, Carl Zeiss, 1540 EsB). The particle size of LiNi1-x-yCoxAlyO2 synthesized in this work ranged at 5~10 um. The electrical conductivity of the LiNi1-x-yCoxAlyO2 cathode materials were also analyzed by a powder resistivity measurement system (HAN TECH, HPRM-M2). Cycle performance tests were carried out using the 2030 coin type cell by CC/CV method in a potential range of 3.0~4.3 V at 0.1 C rate. Cyclic voltammetry (CV, WonATech, WBCS 3000) was conducted at a scanning rate of 0.1 mV s-1. In addition, electrochemical impedance spectroscopy (EIS, Metrohm Autolab B.V., PGSTAT302N) was performed with a frequency range of 0.5 mHz to 100 kHz at an amplitude of 10 mV. The prepared LiNi1-x-yCoxAlyO2 cathode materials exhibit an excellent performance with a high specific capacity of over 180 mAh g-1 at the first cycle and with a cycling retention higher than 80%.

References

1. J. H. Lim, H. Bang, K. S. Lee, K. Amine, Y. K. Sun, J. Power Sources, 189 (2009), 571.

2. A. Funahashi, Y. Kida, K. Yanagida, T. Nohma, I. Yonezu, J. Power Sources, 104 (2002), 248.

3. S. K. Jung, H. Gwon, J. Hong, K. Y. Park, D. H. Seo, H. Kim, J. Hyun, W. Yang, K. Kang, Adv. Energy Mater., 4 (2014), 1300787.

4. G. Prdo, A. Rougier, L. Fournes, C. Delmas, J. Electrochem. Soc., 147 (2000), 2880.

5. B. Huang, X. Li, Z. Wang, H. Guo, L. Shen, J. Wang, J. Power Sources, 252 (2014) 200.

6. G. Hu, W. Liu, Z. Peng, K. Du, W. Cao, J. Power Sources, 198 (2012), 258.