Electrolyzer for Hydrogenation of Organic Hydride with Oxygen Evolution Reaction from Water
Authors: Mitsushima Shigenori , Takakuwa Yasutomo , Kohno Yuji , Matsuzawa Koichi , Kato Akihiro , Nishiki Yoshinori 
Published: February 2020

INTRODUCTION

In order to increase renewable energy, less expensive large scale energy storage and transportation technology must be developed. Hydrogen related technologies are suitable for these applications. Energy carriers, such as organic hydrides, ammonia, and liquid hydrogen, have been investigated for large scale energy storage and transportation (1). Toluene/methylcyclohexane system is one of promising organic hydride because high energy density, easy to handle, and low toxicity. Recently, a new catalyst solved difficulty of dehydrogenation of methylcyclohexane, and practical use of the system is starting (2)
The total reaction of hydrogenation of toluene with renewable energy is
Total: C6H5CH3 + 3H2O → C6H11CH3 + 3/2 O2 [1]
Conventional process of eq. [1] is the series reaction of water electrolysis and hydrogenation, and hydrogenation is exothermic, which is theoretical heat loss. One step electrochemical process with following reactions should improve energy conversion efficiency of hydrogenation.
Cathode: C6H5CH3 + 6H+ + 6e- → C6H11CH3 [2]
Anode: 3H2O → + 6H+ + 3/2 O2 + 6e- [3]
In our pervious study, the eq. [2] of electrohydrogenation of toluene was catalyzed by PtRu/C on a membrane electrode assembly for polymer electrolyte fuel cells (3). However, a complete electrolyzer had not been developed.
In this study, the complete electrolyzer with IrO2based electrocatalyst coated Ti has been developed as a feasibility study of electrohydrogenation system.

EXPERIMENTAL

0.5 mgcm-2 of PtRu (TEC61E54, Tanaka Kikinzoku Kogyo) was coated on a carbon paper (35BC, SGL) with Nafion dispersion (DE521, DuPont) as a cathode. The cathode was pressed on a perfluoroethylene sulfuric acid (PFSA) membrane (Nafion® 212CS, DuPont) for a cathode membrane assembly. A DSE® anode with IrO2based electrocatalyst is used for oxygen evolution.
Toluene and 1M (=moldm-3) of H2SO4were supplied to the cathode and anode for hydrogenation of toluene, respectively. Water was supplied to the cathode for water electrolysis as a comparison.
Cell voltage was determined with 4 mVs-1of voltage sweep from 0.6 to 2.0 V for toluene hydrogenation. Upper limit cell voltage for water electrolysis was 2.3 V.
Internal resistance (iR) was determined with higher frequency intercept of AC impedance method in the cell voltage range from 1.0 to 2.5 V. Here, direct current was close to zero during iRmeasurement.

RESULTS AND DISCUSSION

Figure 1 shows internal resistances and cell voltages as a function of current density fed toluene or water to cathode at 60oC with 4 mVs-1 of voltage sweep. Bold and thin lines for cell voltage are iR-free and measured, respectively. The internal resistances were around 3 Wcm2for both toluene and water fed to cathode; however, the resistance for toluene fed decreased with the increase of current density. In the most of industrial electrolysis, evaluated gas bubble between the membrane and the anode increases internal resistance. In this case, absorbed water should increase with current for toluene fed, and the resistance decreased.
The cell voltages as a function of current were almost the same for toluene and water fed; however, gas evolution was not observed for toluene fed electrolysis. Therefore, hydrogenation of toluene would proceed, instead of hydrogen evolution reaction for water fed electrolysis.
Theoretical cell voltage for toluene fed is smaller than that for water fed and the onset potential of toluene hydrogenation was higher than hydrogen evolution reaction (3). Some toluene would permeate through the membrane, and poison oxygen evolution reaction on the anode.
Electrohydrogenation of toluene was stable and efficient electrolysis. Therefore, this electrolysis will become one of the best energy carrier technologies.

ACKNOWLEDGMENT

This research has been supported by the advanced low carbon technology research and development program of Japan science and technology agency. We appreciate person concerned.

REFERENCES

(1) J. Gretz, J. P. Baselt, O. Ullmann, H. Wendt, Int. J. Hydrogen Energy, 15, 419 (1990).
(2) Y. Okada, E. Sasaki, E. Watanabe, S. Hyodo, H. Nishijima, J. Hydrogen Energy, 31, 1348 (2006).
(3) K. Miyoshi, Y. Sato, S. Mitsushima, 224thECS meeting abstracts, #759 (2013).