Comparative Study of Borohydride Oxidation, at Polycrystalline and Nanostructured Copper Electrodes
Authors: Donato Moreno Julio Ernesto , García-Rodríguez Diana Elizabeth , Alatorre Ordaz Martín Alejandro , Galindo Esquivel Ignacio René , Ponce de León Carlos , Herrasti Pilar , Mendoza-Huizar Luis Humberto 
Published: February 2020

Direct borohydride fuel cell (DBFC) is an energy supplier device, which requires a catalyst for the oxidation of the BH4
- anion; Au nanoparticles supported on carbon substrates has been the best electrode material, followed by Ag [1]. Metals of the group IB show a similar electronic configuration in their valence layer seem to be able to catalyze the borohydride oxidation reaction (BOR). Therefore, metallic copper that belongs to the IB as gold and silver might be a useful-material as catalyst for the BH4
-. In recent studies it has been shown that Au-Cu bimetallic nanoparticles exhibit higher catalytic activity for the direct oxidation of BH4
- than carbon supported pure nanosized Au catalyst [2]. However, up to our knowledge there is not a complete electrochemical study reporting the use of copper nanoparticles as catalyst for BOR in alkaline media. In this work, Cu nanoparticles were synthesized by a chemical approach, using ascorbic acid as a reducing agent as well as stabilizer to control the size of the metallic nanoparticles [3]; subsequently the system has been supported in a vulcan substrate by impregnation followed by a pyrolysis process in order to eliminate organic portion and to prevent the particles agglomeration. Carbon paste electrodes (CPE) were constructed with this composite material. Additionally a Cu foil (99.98%) was used as working polycrystalline electrode to compare the borohydride oxidation with the metallic nanoparticles.
The oxidation of NaBH4 on copper electrodes was studied by cyclic voltammetry at different scan rates and concentrations of NaBH4. Figure 1 shows cyclic voltammograms obtained in a 3M NaOH + 1M NaBH4 aqueous solution of a polycrystalline Cu electrode (curve a) and copper nanoparticles (curves b and c). Curve c shows the study in the absence of borohydride. The experiments started at -1.2 V vs. Ag/AgCl towards positive potential values at a potential sweep scan rate of 100 mVs-1. In these curves, five anodic peaks can be observed, namely peak A1, assigned to the formation of an intermediary due to the hydrolysis of borohydride [4], peak A2 corresponds to the formation of Cu2O (Cu I), peak A3 corresponds to subsequent oxidation in CuO (Cu II), peak A4 corresponds to a parallel reaction forming Cu(OH)2 (Cu II), and finally, peak A5 results from both the formation of Cu (III) and the borohydride oxidation BH4 [5]. Shift in the potentials associated to the peaks A3, A4 and A5 can be observed when compared the voltammogram on the nanostructurated electrode with the PCE. As far as the borohydride oxidation is concerned, the oxidation starts at +0.3 V vs.Ag/AgCl with copper nanoparticles, while in the PCE the value is +0.4 V. A possible correlation between particle size and reactivity will be explored.

References

[1] M. Chatenet, F. Micoud, I. Roche, E. Chainet, Kinetics of sodium borohydride direct oxidation and oxygen reduction in sodium hydroxide electrolyte, Electrochim. Acta. 51 (2006) 5459–5467.
[2] L. Yi, Y. Song, X. Liu, X. Wang, G. Zou, P. He, et al., High activity of Au–Cu/C electrocatalyst as anodic catalyst for direct borohydride-hydrogen peroxide fuel cell, Int. J. Hydrogen Energy. 36 (2011) 15775–15782.
[3] J. Xiong, Y. Wang, Q. Xue, X. Wu, Synthesis of highly stable dispersions of nanosized copper particles using l-ascorbic acid, Green Chem. 13 (2011) 900–904.
[4] D.H. Duan, Y.F. Zhao, S. Bin Liu, A.L. Wu, Electrochemical Oxidation of Borohydride on Cu Electrode, Adv. Mater. Res. 347-353 (2012) 3264–3267.
[5] M.J.A. Shiddiky, A.P. O’Mullane, J. Zhang, L.D. Burke, A.M. Bond, Large amplitude Fourier transformed AC voltammetric investigation of the active state electrochemistry of a copper/aqueous base interface and implications for electrocatalysis., Langmuir. 27 (2011) 10302–11.