Critical Factors Affecting Intergranular Corrosion of AA5083 Under Atmospheric Exposures
Authors: Khullar Piyush , Badilla Jose Vargas , Lim Mary Lyn C. , Hahn Stewart C. , Ellis David W. , Kelly Robert G. 
Published: February 2020

Al-Mg 5XXX series alloys are widely used for marine applications due to their low cost, high strength-to-weight ratio and good weldability. These alloys can become susceptible to intergranular corrosion (IGC) due to precipitation of a more anodic β-phase (Al3Mg2) along grain boundaries after exposure to hot environments during service. A number of studies [1-4]have been conducted to study the role of metallurgical and electrochemical factors on intergranular corrosion penetration. Orientation propagation, the degree of sensitization (DoS) and exposure time have been shown to affect the rate of IGC propagation. Unfortunately, majority of the aforementioned IGC studies have been conducted in full immersion, but much of the marine infrastructure is exposed to atmospheric conditions. There is a need to extend the full immersion corrosion framework and conduct IGC studies under atmospheric and/or thin film conditions. The present work is aimed at identifying critical factors affecting IGC of AA5083 under atmospheric conditions, quantifying their effects and understanding the corrosion mechanisms to better predict IGC of 5XXX alloys in the field.
Preliminary results indicate that oxidizing strength of the environment and material system govern IGC behavior in the thin film conditions. Both persulphate and ozone have been used in laboratory studies to control the oxidizing behavior of the environment. Figure 1 shows the optical microscopic images depicting the IGC of AA5083 exposed to 95% RH and 30⁰C with different persulphate thickness for 100hours. It can be clearly seen that mass of persulphate affects IGC of AA5083 under thin film as the concentration of persulphate is same in both cases.
Another notable result is that the cathode area has a strong influence on IGC of AA5083 under thin film. Figure 2 shows the maximum IGC length for AA5083-H131 exposed to 6ppm ozone at 98% RH and room temperature. The samples were loaded with 1000 µg/cm2NaCl. The graph shows that the maximum length of IGC has a strong correlation with the sample size.
Further work will be presented from electrochemical measurements under thin film conditions and a study of the cathodic kinetics for atmospheric exposures. The effects of critical factors like ozone and persulphate concentration, salt loading density, solution film thickness and aerosol size will be presented to develop a better understanding of IGC corrosion under atmospheric conditions. Intergranular corrosion depth and surface morphology will be used as corrosion indicators.

Acknowledgements

The authors would like to thank Daniel J. Dunmire, Director, DoD Corrosion Policy and Oversight, Office of the Secretary of Defense, for financial support, via the US Air Force Academy Contract#FA7000-12-2-0017.

References

[1] S. Jain, M.L.C. Lim, J.L. Hudson, J.R. Scully, Corros. Sci., 59 (2012) 136-147.
[2] M.L.C. Lim, J.R.Scully, R.G. Kelly, Corrosion, 69 (2013) 35-47.
[3] M.L.C. Lim, R.G. Kelly, J.R. Scully, “Critical Electrochemical Conditions for Intergranular Corrosion in Sensitized AA5083-H131”, in NACE Department of Defense Virtual Corrosion Conference 2013.
[4] Y. Yuan, “Localized Corrosion and Stress Corrosion Cracking of Aluminum-Magnesium Alloys” (Ph.D. diss., University of Birmingham: Birmingham, U.K., 2005)

Figure 1