Influence of Exchangeable Cation Composition on the Size and Shape of Montmorillonite Particles in Dilute Suspension
Authors: Schramm Laurier L. , Kwak Jan C. T.
Published: August 2006

Viscosity and light-transmission measurements of dilute suspensions of montmorillonites having different exchangeable cations were used to calculate relative particle sizes as a function of cation composition, where particle size is expressed as the number of clay plates per tactoid relative to the number of plates per tactoid for Li-montmorillonite, after exchange of Li, Na, K, Cs, and Mg by Ca. Tactoid sizes increased in the order Li < Na < K < Mg < Ca, with the number of plates per tactoid relative to Li-montmorillonite varying from 1.5 for Na- to 6.1 for Ca-montmorillonite. The results for tactoid sizes derived from light transmission and those derived from viscosity data are in reasonable agreement with each other and with literature data for similar systems. Upon exchange of Ca-counterions for Li-, Na-, or K-coun-terions, a sharp initial decrease in tactoid size was observed over approximately the first 30% of cation exchange. Upon further exchange, tactoid sizes changed only slightly, but when Ca was exchanged for Cs or Mg, a much more gradual decrease in particle size was observed.
Electrical Potential Between Dissimilar Clay Double Layers
Authors: Helmy A. K. , Natale I. M. , Mandolesi M. E.
Published: August 2006

A model describing the electric double layers in clay-electrolyte systems containing particles with different surface charge densities was developed and used to calculate the film thickness of water present in a clay paste. The average water film thicknesses (~18 Å) calculated by considering the clay to contain 9 groups of particles of different charge densities did not differ from those calculated by assuming one average charge density; provided the minimum potential between particles remained constant. These values, however, were higher than those obtained from gravimetric water determinations by about 30%. The overestimation of the average thickness of the water films by the theoretical model is most likely due to the assumption of a complete parallel arrangement of particles in the paste and the validity of the Gouy theory for double layers on clays.
Electrical Conductivity of Na/Ca-Montmorillonite Gels
Authors: Shainberg I. , Oster J. D. , Wood J. D.
Published: August 2006

The specific conductivity, κg, of Na/Ca montmorillonite gels (0.02 and 0.04 g clay/cm3) as a function of the specific conductivity of the interclay solution, κw, was measured. For low values of κw (<3 mmho/cm) the conductivity curves were convex with respect to xw; at higher values they were linear. The κw at which deviation from linearity began increased with increasing sodium content from 0.7 mmho/cm for the Ca-montmorillonite gel to 2.6 mmho/cm for Na-montmorillonite gel. The intercept of the linear portion of the conductivity curve increased and its slope decreased with increasing exchangeable sodium. The experimental results were described by a conductance model comprised of two elements connected in parallel: an element consisting of the solid and solution phases connected in series, and another consisting of the solution phase. At low electrolyte concentrations, the first element accounts for the curvature of the κg-κw curve, whereas at high electrolyte concentrations, the second element dominates, and the curve is linear with a slope determined by a formation factor and an intercept determined by exchangeable cation mobility.

An adjustable parameter in the conductivity term for the first element, which accounts for the thickness of the clay particles, increased with exchangeable Na, and its numerical value indicated that the solid phase also includes the diffuse double layer. The mobility of the exchangeable cation relative to that in water increased from 4% for Ca to 41% for Na with the largest increase occurring between 20 and 40% exchangeable Na. Similar effects of exchangeable Na were evident on the axial ratio of the clay particles calculated from the slopes of the linear lines. These observations are consistent with an exchangeable-ion demixing model where the initial exchangeable Na is adsorbed on the external surfaces of the Ca-montmorillonite tactoids without affecting exchangeable ion mobility or tactoid size. Further additions of exchangeable Na result in Na adsorption on the internal surfaces of the tactoid and tactoid breakdown with a subsequent increase in both exchangeable ion mobility and the axial ratio of the clay particles.
Characterization of Adsorbed Iron in Montmorillonite by Mössbauer Spectroscopy
Authors: Diamant A. , Pasternak M. , Banin A.
Published: August 2006

The Mössbauer effect of Fe57 was used to probe and characterize iron ions adsorbed on the interlayer surfaces of montmorillonite. Measurements were performed with Fe- and Ca-saturated mont-morillonites. At 210°K the intensity of the Fe2+ line was greatly reduced, apparently due to the melting of interlayer water. Neither the structural Fe2+ in Ca-montmorillonite nor the adsorbed Fe3+ in Fe-mont-morillonite were affected by the melting process. From the temperature dependence of the absorption intensity, the effective Debye temperature of all the iron species appears to be approximately the same (θD = 189 ± 5°K). This result allowed for an accurate determination of the population of Fe2+/Fe3+ in various samples.
Methane Solubilities in Clay Slurries
Authors: Stoessell Ronald K. , Byrne Patricia A.
Published: August 2006

Methane solubilities at 25°C were measured at 350, 550, and 750 psia in dilute (< 11 wt. %) clay slurries of Na-montmorillonites and argillaceous sediment. Methane solubilities were not significantly affected by the presence of clay. Water hydrated onto the external clay surfaces did not appear to exclude methane. In addition there was no detectable sorption of methane onto the clays. The measured solubilities are consistent with an open structure of the water hydrated onto the clay surface for which the partial molal volume is larger than that of normal water. The results imply that aqueous methane solubilities measured in the laboratory can be used to determine degrees of methane saturation in interstitial solutions in unconsolidated sediments.
Geochemistry of Hydrothermal Chlorite Replacing Igneous Biotite
Authors: Parry W. T. , Downey L. M.
Published: August 2006

Hydrothermal chlorite replaces igneous biotite in the Gold Hill, Utah, quartz monzonite. Chemical compositions of coexisting biotite and chlorite determined by electron microprobe and wet chemical methods were used to evaluate chemical mass transfer during the alteration process. The mole ratio Mg/(Mg + Fe) varies from 0.52 to 0.65 in the chlorite and from 0.51 to 0.60 in the parent biotite. The Mg content of the chlorite decreases systematically with increase in the volume percent replacement of biotite. Homogenization temperatures of fluid inclusions in nearby quartz microveinlets indicate that the chloritic alteration took place at approximately 200°C.

Textural relationships suggest that the alteration of biotite to chlorite is isovolumetric, but a comparison of mineral compositions and mineral assemblages with phase diagrams in which Al or volume are conserved among solid phases suggests that the chlorite compositions are best explained as a function of reaction progress in an Al-conservative system. The chlorite composition changes in response to changes in solution composition produced by the dissolution of successive small amounts of biotite. Representative mass balance for the alteration of all of the biotite to chlorite in 1 m3 of rock containing 336 moles of biotite indicates that 74 moles of Mg, 35 moles of Fe3+, 420 moles of H+, and 2 moles of Mn are added to the rock and that 311 moles of K, 54 moles of Fe2+, 76 moles of Ti, 53 moles of F, and 6 moles of Cl are lost to solution. The mass transfer for partially altered biotite is 11 to 188 moles of K, 2 to 46 moles of Ti, 2 to 44 moles of F, and 0.3 to 6 moles of Cl removed per cubic meter of rock and 1 to 26 moles of Fe3+ and 20 to 347 moles of H+ added. The mass transfer of Mg varies from 12 moles added to 32 moles removed per cubic meter of rock depending on mineral composition and extent of replacement.
Adsorption of Stearic Acid by Chrysotile
Authors: Berkheiser Vaughn E.
Published: August 2006

Stearic acid adsorption by chrysotile asbestos in hexane was shown to occur by the formation of a Mg-stearate complex on the mineral surface. Infrared spectroscopy showed no evidence of physically adsorbed stearic acid over the range of concentration employed. Absorption bands at 1560 and 1410 cm−1 in the spectrum of the chrysotile-stearic acid complex correspond with band positions in the spectrum of a synthesized Mg-stearate complex. No evidence of the acid form, which produces a band at 1713 cm−1, was present in the spectrum of the chrysotile complexes. At an equilibrium concentration of 0.8 mg stearic acid/ml, the mineral adsorbed 42 mg stearic acid/g. By heating the mineral in molten stearic acid, additional stearic acid beyond that observed by adsorption from solution was adsorbed in the carboxylate form. Calculations based on the molecular dimensions of stearic acid and the crystal structure of chrysotile indicate that the limiting factor in possible surface occupancy is the molecular size of stearic acid rather than the surface density of Mg-OH adsorption sites.
Effects of Temperature on the Sorption of Lanthanides by Montmorillonite
Authors: Miller Steven E. , Heath G. Ross , Gonzalez Richard D.
Published: August 2006

The diffusion of exchanged Yb, Ho, and Eu from interlayer positions in montmorillonite was studied using infrared spectroscopy (IR), X-ray powder diffraction, and cation-exchange measurements. Dehydration of exchanged montmorillonite between 100° and 280°C caused the ions to diffuse into the hexagonal rings of surface oxygens. Subsequent migration into vacant octahedral sites was small regardless of the radius of the cation. Considerable ion fixation in excess of the cation-exchange capacity of the clay was observed at 20°C in both water and a 1:1 water:95% ethanol mixture. Evidence for hydrolysis as a possible mechanism for cation fixation was obtained by observing frequency shifts for deuterated hydroxyl groups using IR spectroscopy. A major IR band centered at 2680 cm−1 was observed for all three lanthanide-exchanged montmorillonites studied and assigned to the OH-stretching frequency of a lanthanide hydroxide. This band intensified on heating at 300°C for 1 hr. An IR band between 690 and 710 cm−1 also was observed for all three lanthanide-exchanged montmorillonites and was assigned to a lanthanide-hydroxyl deformation mode. No hydrolysis was observed for Na-montmorillonite, as expected from the very low hydration energy of Na+.
Effects of Substitution of Germanium for Silicon in Imogolite
Authors: Wada Shin-ichiro , Wada Koji
Published: August 2006

Imogolites in which a part or all of Si was substituted with Ge were synthesized from solutions containing aluminum ion and silicic and/or germanic acid. The products were similar to natural imogolite in their tubular morphology, electron diffraction patterns, and differential thermal analysis curves. However, the external diameter of the tube increased with increasing Ge substitution up to about 33 Å, and associated changes appeared in the X-ray powder diffraction patterns, suggesting that the substitution of Ge for Si caused a decrease in the curvature of the gibbsite sheet with which SiO- or GeO-tetrahedra are associated. Infrared absorption bands at 995 and 930 cm−1 in imogolite disappeared and new bands appeared at 910 and 810 cm−1 on substitution of Ge for Si, whereas those in the region between 700 and 300 cm−1 remained unchanged or changed little. The former two bands were assigned to Si-O vibrations and the latter bands to Al-O vibrations.
Interaction of Uranyl Ions with Synthetic Zeolites of Type A and the Formation of Compreignacite-Like and Becquerelite-Like Products
Authors: Brindley G. W. , Bastovanov Marija
Published: August 2006

Uranyl acetatye solutions, ranging in concentration from about 100 ppm to 3700 ppm, were re-acted with the Na-, K-, and Ca- forms of zeolite A. The crystalline products from the Na- and K-A zeolites resembled compreignacite (K2O·6UO3·11H2O) and from the Ca-A, becquerelite (CaO·6UO3·11H2O). With higher concentrations of uranyl acetate, only X-ray-amorphous products were obtained. The compreignacite-like products gave sharp X-ray powder diffraction patterns and were indexed with orthorhombic, quasi-hexagonal unit cells which showed a significant variation of the axial ratio b/a from values just greater than, to values just less than √3. The becquerelite-like phase was always accompanied by unreacted zeolite. Compreignacite was synthesized from uranyl acetate and KOH solutions at room temperature over a period of several days.
Surface Properties of Allophane, Halloysite, and Imogolite
Authors: Theng B. K. G. , Russell M. , Churchman G. J. , Parfitt R. L.
Published: August 2006

The adsorption of sodium, chloride, and phosphate ions by allophane, imogolite, and halloysite has been studied in relation to the surface structure of the mineral samples. The high adsorption of phosphate (>200 μmole/g) and chloride (10–30 meq/100 g at pH 4) by allophane is ascribed to the small particle size of allophane, its high surface area (∼800 m2/g), and the presence at the surface of Al-OH-Al groups and defect sites. In contrast, halloysite has a relatively large particle size and a Si-O-Si surface. Accordingly, the adsorption of phosphate (5–10 μmole/g) and chloride (1 meq/100 g) by halloysite is very much lower as compared with allophane. Phosphate adsorption by halloysite is also related to particle morphology and the number of edge sites. Thus, a sample consisting entirely of spheroidal particles adsorbed only 5 μmole/g at a solution concentration of 1 × 10−4 M, whereas the tubular types of comparable surface area adsorbed 7–10 μmole/g at the same concentration. This is because spheroidal halloysite particles have few, if any, edge sites at which phosphate can adsorb. The relative degree of order and hydration of halloysite, as indicated by infrared spectroscopy, also affects phosphate adsorption. However, this factor is apparently less important than particle morphology and surface structure. Although imogolite also has an Al-OH-Al surface, it contains relatively few defect sites where phosphate can adsorb. Consequently, much less phosphate (120 μmole/g) was adsorbed as compared with allophane.
Solubility of Two High-Mg and Two High-Fe Chlorites Using Multiple Equilibria
Authors: Kittrick J. A.
Published: August 2006

High-Mg chlorites from Vermont and Quebec and high-Fe chlorites from Michigan and New Mexico were equilibrated at room temperature in the near-neutral pH range. Gibbsite, kaolinite, and hematite of known stability were added to the samples to control unmeasurable variables at calculable levels. Equilibrium solution compositions were obtained from undersaturation and from supersaturation. Other indicators of equilibrium were good agreement between successive analyses over a long period of time, between duplicate samples, between independent systems, and between independent measures of equilibrium. All four chlorites were stable relative to brucite and, with a few exceptions, relative to talc under the conditions of study. When in equilibrium with gibbsite, the pH − ½Mg2+ value of the chlorites ranged from 6.3 to 6.5, at a pH4SiO4 value of 4.0. These values are in good agreement with prior estimates of chlorite stability. The calculated standard free energy of formation of the chlorites is dependent upon solution Fe2+ calculated from the sample Eh and assumed equilibrium with hematite, with the assumption that the Fe2+-Fe3+ couple is at the same Eh as the sample.
Crystal-Chemical Study of Layered [Al2Li(OH)6]+X−·nH2O
Authors: Serna Carlos J. , Rendon Jose L. , Iglesias Juan E.
Published: August 2006

A layered double hydroxide with a chemical composition [Al2Li(OH)6]+X− · nH2O, where X− is an interlayer anion, has been synthesized hydrothermally at 130°C from aluminum-tri-(sec-butoxide) and lithium carbonate. Electron micrographs showed the product to have a platy morphology with distinct hexagonal symmetry, which has been corroborated by selected area electron diffraction patterns corresponding to a projection of the structure on its (001) plane. Evidence for a superlattice with a = 5.32 Å was obtained, indicating cation ordering among octahedral sites. X-ray powder diffraction data also can be interpreted by reference to a hexagonal supercell with dimensions a = 5.32 Å and c = 15.24 Å. The arrangement of the octahedral sites appears to be that of gibbsite, but with the vacancies filled with lithium cations. Anions must be present between the sheets to balance the charge. A complete assignment of the observed infrared lattice vibrations can be made for the anion [Al2LiO6] with the ideal D3d symmetry for motions within one octahedral sheet. The results show that [Al2Li(OH)6]+X− · nH2O is a hydrotalcite-like compound with the octahedral cations largely ordered. The general formula for hydrotalcite-like compounds, [M2+1−xM3+x(OH)2]x+Xm−x/m · nH2O, should be extended to include the monovalent lithium cation.
Hydrolysis and Dehydration Reactions of Exchangeable Cu2+ on Hectorite
Authors: McBride M. B.
Published: August 2006

Electron spin resonance (ESR) analysis of Cu2+-hectorite suspensions provides evidence for the surface-induced hydrolysis of Cu(H2O)62+ at low pH and surface-inhibited hydrolysis (or precipitation) at high pH. Dehydration of the hectorite by heating to 110°C appears to promote hydrolysis in high pH clays further. Heating to even higher temperatures removes ligand water from Cu2+, allowing the metal ion to coordinate with silicate oxygen atoms. The planar Cu(H2O)42+ ion predominates in the interlamellar regions of hectorite that has been air dried or heated to temperatures of 110°C or lower, but more extreme thermal treatment changes the apparent orientation of the Cu2+-ligand axes as some or all of the four water ligands are removed, A loss in ESR signal intensity upon heating Cu2+-hectorite above 110°C is evidence for lowered symmetry of the dehydrated, surface-coordinated Cu2+ ion.
Layer Charge Heterogeneity in Vermiculites
Authors: Lagaly Gerhard
Published: August 2006

The broad charge heterogeneity typical of nearly all smectites is not necessarily characteristic of vermiculites. In addition to vermiculites with pronounced heterogeneity, minerals with no or only limited charge heterogeneities are known. Layer charge and charge heterogeneity of 25 vermiculites were determined by alkylammonium ion exchange. The comparison of experimental basal spacings with dL/n-plots provided a simple determination of the average charge density. The spacings of high-charged vermiculites (≥0.8 eq/(Si,Al)4O10) with paraffin-type interlayers follow a straight line in the dL/n-plots. Lower-charged vermiculites were recognized by stepwise increasing spacings due to mono-, two-, or three-layer chain packings. Charge heterogeneity produced a superposition of the dL/n-curves for different charges, and the basal reflections of some of the alkylammonium derivatives became nonintegral.
Hydrolysis and Decomposition of Hectorite in Dilute Salt Solutions
Authors: Kreit J. F. , Shainberg I. , Herbillon A. J.
Published: August 2006

The hydrolysis and decomposition of M-hectorite (M being Na, Li, Mg, or Ca) in dilute solutions of M-chlorides were studied by recording the changes in electrical conductivity (EC) of the clay suspensions with time, and by chemical analyses of the interclay solutions and resulting solid phases. The rate of hydrolysis of the hectorites in suspension, as evaluated by the change of EC with time, was found to decrease with increase in salt concentration (to zero for Na-hectorite in NaCl concentration of 47 meq/liter), and to decrease with increase in the valency of the adsorbed cation (the rate of hydrolysis of Ca-hectorite was one sixth of that of Na-hectorite). The rate of Na-hectorite hydrolysis was determined by the concentration of protons at the clay surface as calculated from the diffuse double layer theory.

Conversely, in suspensions of Al-hectorite saturated with Na, the hydrolysis rates were not dependent on the electrolyte concentrations. This result can be explained by assuming that the hydroxy-Al polymers at the clay surface determine the proton concentration at the clay surface. Hectorites saturated with structural cations (such as Mg and Li) are chemically more stable than those saturated with Na and Ca. The presence of Li and Mg at the clay surface slowed down the diffusion release of these octahedral ions to the clay surface, compared with Na and Ca hectorite, respectively.
Alteration of Andesite in Wet, Unstable Soils of Oregon's Western Cascades
Authors: Glasmann J. R.
Published: August 2006

Alteration products of andesite cobbles from wet soils formed in volcanic colluvial material were studied using petrographic, electron microscope, X-ray powder diffraction, and thermal techniques. Augite phenocrysts altered by congruent dissolution leaving voids which were subsequently filled with smectite. Plagioclase also altered to produce micrometer-size spheroidal aggregates of smectite. Halloysite was not observed within the altered cobbles, although it was abundant in the soil matrix. The formation of smectite in the altered cobbles was probably favored by the restrictive drainage of the microenvironment in combination with wet soil conditions.
Berthierine and Chamosite in Coal Measures of Japan
Authors: Iljima Azuma , Matsumoto Ryo
Published: August 2006

Berthierine (formerly chamosite) occurs as concretions, lenses, and bands in carbonaceous, kaolinitic shale of freshwater coal-swamp deposits in Paleogene and Upper Triassic coal measures of Japan. Textural relations in thin sections of the Triassic berthierine rocks and a siderite-kaolinite-berthierine-quartz assemblage in Paleogene rocks indicate that the berthierine formed by reaction of siderite with kaolinite. The transformation of siderite and kaolinite to berthierine and quartz occurs progressively under reducing conditions between 65° and 150°C and at burial depths of 2–5 km. Utatsu berthierine is an aluminous, low-Mg variety as compared with berthierine pellets in modern marine and estuarine sediments and in ancient marine ironstones. Fe is the dominant octahedral cation with Fe2+ ≫ Fe3+. The composition of the berthierine varies between different morphological types. Utatsu berthierine transformed to ferrous chamosite when kaolinite in the host shale changed to pyrophyllite. These transformations are estimated to have occurred at ∼160°C and at a burial depth of ∼3 km.
Catalytic Action of Copper on the Oxidation of Structural Iron in Vermiculitized Biotite
Authors: Sayin Mahmut
Published: August 2006

The ferrous iron content of two vermiculitized biotites decreased by treatment with 0.1 N salts of copper at 70°C from 9.1–14% to 1.8–2.6%. Presumably, interlayer copper ions acted as a catalyst (here, an electron carrier) for the oxidation of iron by dissolved oxygen. The oxidized iron was ejected from the structure and formed crystalline iron minerals, such as hematite and goethite. Weight loss determinations, chemical, and X-ray powder diffraction data suggest that Cu(II) ions were polymerized to hydroxy-hydrous compounds in the interlayer space. Poor exchangeability of the resultant complex is attributed to the formation of strong electrostatic attractions between OH groups of the interlayer complexes and silicate oxygens.
Thermodynamic Characterization of Clay/Electrolyte Systems
Authors: Neal C. , Thomas A. G. , Truesdale V. W.
Published: August 2006

Clay/electrolyte systems are best characterized using a new variable, notional interfacial content (NIC). The NIC approach emphasizes that any division of the total amount of a species present in a clay/electrolyte system into that part which ‘belongs’ to the clay and that part which ‘belongs’ to solution is necessarily arbitrary. It carries out this division by choosing one of the species as a reference species and defining it as being completely in a notional bulk solution which had the same composition, but not extent, as the real bulk solution. The NIC of each of the other species present, that is that part of their total amount not in the notional bulk solution, therefore represents the amounts of those species ‘belonging’ to the clay.

The NIC concept is universal and hence encompasses several other, older terms. For example, by choosing different reference species, the variables hitherto called ‘water adsorption’ and ‘negative adsorption’ (which have been used to describe the same phenomenon) may be obtained. Similarly, certain earlier definitions of exchangeable and adsorbed cations (some being pragmatic are not included) as well as that of ion surface excesses may be accounted for. The NIC approach thus provides a rationalization of several earlier terms which are, in fact, plagued by a multiplicity of definition which makes their use very complicated.
Mixed-Layer Kerolite/Stevensite from the Amargosa Desert, Nevada
Authors: Eberl Dennis D. , Jones Blair F. , Khoury Hani N.
Published: August 2006

Mixed-layer clays composed of randomly interstratified kerolite/stevensite occur as lake and/or spring deposits of probable Pliocene and Pleistocene age in the Amargosa Desert of southern Nevada, U.S.A. The percentage of expandable layers of these clays, determined from computer-simulated X-ray diffractograms, ranges from almost 0 to about 80%. This range in expandabilities most likely results from differences in solution chemistry and/or temperature at the time of formation. An average structural formula for the purest clay (sample P-7), a clay with about 70% expandable layers, is:
$${\left[ {\left( {M{g_{2,72}}A{l_{0,07}}F{e_{0.03}}L{i_{0.09}}} \right)\left( {S{i_{3.96}}A{l_{0.04}}} \right){O_{10}}{{\left( {OH} \right)}_2}} \right]^{ - 0.21}}{\left[ {X_{0.21}^ + } \right]^{ + 0.21}}.$$

The data suggest that talc, kerolite, and stevensite form a continuous structural series based on layer charge.
Influence of Relative Humidity on the Crystallization of Fe(III) Oxides from Ferrihydrite
Authors: Torrent J. , Guzman R. , Parra M. A.
Published: August 2006

Ferrihydrite prepared in different manners was kept under relative humidities ranging from 75 to 100% and at temperatures of 45° and 55°C for 180 days. Ferrihydrite transformed to hematite and goethite at relative humidities close to 100%, but at lower relative humidities the transformation was less pronounced and hematite was highly favored over goethite. Increasing temperature also favored hematite over goethite, and Al substitution completely prevented goethite formation. These results suggest that hematite can form in relatively dry, warm soils or sediments, although more slowly than in moister environments.
Effect of Exchangeable Ions and Ionic Strength on Boron Adsorption by Montmorillonite and Illite
Authors: Keren R. , O'Connor G. A.
Published: August 2006

The effects of exchangeable Na and Ca and the ionic strength of NaCl and CaCl2 solutions on the boron adsorption by the Na and Ca forms of montmorillonite and illite at pH 9 were studied. The boron adsorption by montmorillonite was greater for the Ca form than for the Na form at any boron activity in solution and at any ionic strength. For example, the amount of boron adsorbed by Na- and Ca-montmo-rillonite was 2.9 and 4.3 μmole/g, respectively, at an ionic strength of 0.36 and a boron activity of 0.875 mmole/liter in equilibrium solution. The boron adsorption by illite was much greater than by montmorillonite. For example, the amount of boron adsorbed by Na-montmorillonite and Na-illite was 1.5 and 8.7 μmole/g, respectively, at an ionic strength of 0.02 and a boron activity of 0.5 mmole/liter. However, the nature of the exchangeable cation had little effect on the boron adsorption by illite. The effect of the ionic strength on the boron adsorption by Na-montmorillonite was greater than that observed for either Camontmorillonite or illite. The data suggest that the negative electric field around the clay particles is one of the main factors controlling boron adsorption at alkaline pHs.
Surface Properties of Sepiolite from Amboseli, Tanzania, and Its Catalytic Activity for Ethanol Decomposition
Authors: Dandy A. J. , Nadiye-Tabbiruka M. S.
Published: August 2006

The catalytic activity of sepiolite from Amboseli, Tanzania, for the dehydration and dehydrogenation of ethanol at 150°–300°C has been studied using a flow reactor. Both reactions occur, but the catalyst activity decreases with use. The products include water, carbon dioxide, ethene, ethanal (acetaldehyde), diethyl ether, but-1,3-diene, but-2-enal (crotonaldehyde), and an unidentified aromatic compound. The proportions change with temperature, the dehydrogenation reaction being favored at the higher temperatures. The BET surface areas of the sepiolite are 316 m2/g (nitrogen adsorption at — 197°C) and 212 m2/g (ethanol vapor adsorption at 25°C, assuming a molecular cross-sectional area of 24.6 Å2), indicating a possible greater penetration of pores and channels by nitrogen compared with ethanol vapor under these conditions. The pore-size distribution reveals that approximately 55% of the surface area measured by nitrogen adsorption is contributed by micropores.
Oxidation and Reduction of Structural Iron in Chlorite at 480°C
Authors: Borggaard Ole K. , Lindgreen Holger B. , Mørup Steen
Published: August 2006

An iron-rich chlorite, ripidolite, was oxidized by air-heating at 480°C, i.e., below the dehydroxylation temperature and subsequently reduced in hydrogen at the same temperature. On the basis of chemical, differential thermal, infrared, Mössbauer, and X-ray powder diffraction analyses, Fe(II) seems to be present only in the 2:1 layer of the original chlorite in a type of site similar to that of Fe(II) in biotite, with OH in cis-positions. These data also suggest that octahedral Al and Fe(III) are located in the hydroxide sheet of the original chlorite. The structural changes of the mineral due to the oxidation and the subsequent reduction appear limited to minor structural rearrangements and, perhaps, to the introduction of OH in both cis- and trans-positions. The results of the investigation are in agreement with a reaction of the form: [Fe(II)OH]+ ⇋ [Fe(III)O]+ + H(H+ + e−).
Polytypism of Micas: OD-Interpretation, Stacking Symbols, Symmetry Relations
Authors: Dornberger-Schiff K. , Backhaus K. -O. , Ďurovič S.
Published: August 2006

From the symmetry point of view, micas may be classified as follows: those with all three octahedrally coordinated sites occupied by the same cation (homo-octahedral micas), those with only two of these sites occupied by the same cation (meso-octahedral micas), and those with the three sites occupied by different cations or by two different cations and a void, in an ordered manner (hetero-octahedral micas). For any of these three classes, mica polytypes, idealized in accordance with the generalized Pauling model, can be interpreted as OD structures consisting of octahedral OD layering and tetrahedral OD layering in which an interlayer cation plane is sandwiched between tetrahedral sheets. A mica layer built up by an octahedral sheet and two halves of tetrahedral sheets on either side consists of two OD packets linked by a two-fold rotation.

The orientation of any OD packet may be given by a number from 0 to 5 (related to a hexagonal coordinate system). A dot behind or before these numbers is used to denote the position of the octahedral layer (number + dot = orientational character). The displacement of a packet against its predecessor is characterized by a vector from the origin of a packet pn (or qn-1) to the origin of the adjacent packet pn+1 (or p2n). These displacements may also be symbolized by numbers from 0 to 5 (displacement characters); a zero displacement is symbolized by *. Any mica polytype (ordered or disordered) can thus be described by a two-line symbol. The orientational characters are located on the first line, and the displacement characters on the second. Any symbol, therefore denotes unequivocally the stacking layers in a polytype. The space-group symmetry of ordered polytypes follows directly from the symbol.
Factors Affecting Orientation of OH-Vectors in Micas
Authors: Bookin A. S. , Drits V. A.
Published: August 2006

The orientation of the OH-vectors in hydroxyl groups of micas of different compositions, polytype modifications, and symmetry were calculated by the method of minimization of electrostatic energy. The orientations are strongly affected by the peculiarities of structures, and even slight deviations from the ideal dioctahedral periodicity can introduce a correction of as much as 10° to the value of the polar angle. Ordering of cations in octahedra lead to twisting of the OH-bond towards the octahedron with lower charge and larger dimension. The latter is less true for cation ordering in tetrahedra. Because of these factors and the dependence of the hydrogen position on the coordinates of heavy atoms, such calculations can give reliable results only if the structure has been refined with high precision. Different polytypes of micas displayed the same orientation of the OH-vectors with respect to the axes of a separate layer, if the stacking sequence did not introduce specific distortions of the 2:1 layer.
Origin of an Underclay as Revealed by Vertical Variations in Mineralogy and Chemistry
Authors: Rimmer Susan M. , Eberl Dennis D.
Published: August 2006

Regular vertical variations in mineralogy and chemistry indicate that underclay beneath the Herrin (No. 6) coal in southwestern Illinois has undergone in situ alteration. Alteration resulted from the downward movement of hydrogen ions, as indicated by the progressive leaching of acid-sensitive minerals adjacent to the coal. Mineralogical trends observed in the underclay with increasing depth below the coal include: (1) a decrease in the expandability of mixed-layer illite/smectite (I/S); (2) an increase in the amount of ordered I/S with respect to randomly interstratified I/S; (3) an increase in the amount of discrete illite with respect to expandable clays; and (4) an increase in chlorite and calcite. Ordered I/S is the dominant mixed-layer clay where calcite is present, but randomly interstratified I/S dominates where calcite is absent. The pH of the underclay also increases with depth. These trends are consistent with an origin by acid leaching of a preexisting mineral assemblage that included illite, chlorite, and calcite. Other acid-alteration trends may be expected for different precursor minerals and for different leaching intensities and durations.
Organic Anion Adsorption on Aluminum Hydroxides: Spin Probe Studies
Authors: McBride M. B.
Published: August 2006

The nature of organo-phosphate and carboxylate bonding in aqueous suspensions of noncrystalline alumina, boehmite, and gibbsite has been studied using the anionic nitroxide spin probes 3-carboxy-2,2,5,5-tetramethyl-1-pyrrolidinyloxyl and 4-hydroxy-2,2,6,6-tetramethyl-piperidinooxyl dihydrogen phosphate. Analysis of the electron spin resonance (ESR) spectra of these molecules revealed that adsorption of both molecules occurred rapidly on the high surface area alumina and boehmite, whereas only the organophosphate adsorbed on gibbsite. A loss in rotational motion of the molecules accompanied adsorption, with the greater degree of motional restriction observed for the carboxylate attributed to steric restrictions to rotation about the surface-bound C-COO− bond axis. The ease of displacement of adsorbed carboxylate from surface binding sites by weakly adsorbing anions (Cl−, ClO4−) compared to organophosphate suggests that the carboxylate adsorbed by ligand exchange of a single surface OH, whereas the organophosphate probably formed a bidentate bond. The carboxylate bound on noncrystalline alumina showed evidence of nonspecific electrostatic adsorption in addition to ligand exchange of surface OH. This weak bonding was indicated by a moderate loss in rotational motion and ease of exchangeability.
Sorption Properties of Carbon Composite Materials Formed from Layered Clay Minerals
Authors: Putyera Karol , Bandosz Teresa J. , Jagiełło Jacek , Schwarz James A.
Published: August 2006

The sorption properties of carbon-composite materials based on montmorillonite and hydrotalcite matrices have been studied using nitrogen adsorption isotherms and inverse gas chromatography. Carbon composite materials derived from both types of inorganic precursors contain pore structure accessible for adsorbate molecules. Adsorption capacity per unit mass of these composite adsorbents is larger in the case of hydrotalcite than in montmorillonite-based materials. Exposing these materials to ambient conditions results in their hydration. Subsequent water removal by heating under vacuum increases nitrogen adsorption capacity, which is explained by the opening of the adsorption space. The water content of hydrated samples and its effect on adsorption capacity is greater for the case of hydrotalcite-based materials. No direct relationship between carbon content and adsorption properties of the materials studied is observed.
Growth of Smectite from Leached Layer During Experimental Alteration of Albite
Authors: Kawano Motoharu , Tomita Katsutoshi
Published: August 2006

Experimental alteration of albite in deionized-distilled water at 150° to 225°C for various times up to 30 days was performed to elucidate formation processes for alteration products of albite in aqueous solution. The alteration products were examined by X-ray powder diffraction, scanning electron microscopy, transmission electron microscopy (TEM), and energy dispersive X-ray analysis (EDX). The surface compositions of albite before and after alteration were investigated by X-ray photoelectron spectroscopy (XPS). TEM clearly showed that an amorphous leached layer was produced on the albite surface at the earliest alteration stage together with small amounts of allophane. The leached layer increased successively in thickness and tended to be detached from the albite surface as alteration proceeded. Noncrystalline fibers less than 0.5 µm in length appeared within the leached layer matrix and transformed into thin flaky smectite and small amounts of K-mica. The leached layer gave electron diffraction patterns with a diffuse halo, whereas the flaky smectite displayed rings at 4.51, 2.61, and 1.54 Å. EDX confirmed that the flaky smectite consisted mainly of Si and Al, and small amounts of Na. The smectite was formed in the stability field of Na-smectite for the system of Na2O-Al2O3-SiO2-H2O.
Characterization of Mg-Saponites Synthesized from Gels Containing Amounts of Na+, K+, Rb+, Ca2+, Ba2+, or Ce4+ Equivalent to The CEC of the Saponite
Authors: Kloprogge J. Theo , Breukelaar Johan , Geus John W. , Jansen J. Ben H.
Published: August 2006

Saponites were hydrothermally grown in the presence of amounts of NH4+, Na+, K+, Rb+, Ca2+, Ba2+, and Ce4+ equivalent with the CEC of the saponite (155 meq/100 g), with or without F−, at a temperature of 200°C for 72 hr. XRD and CEC data revealed the formation of a two-water-layer saponite with mainly Mg2+ as interlayer cation. Dehydration occurred between 25° and 450°C and dehydroxylation occurred in two steps between 450° and 790°C and between 790° and 890°C. The relatively small length of the b-axis between 9.151 and 9.180 Å is explained by considerable octahedral Al substitution (between 0.28 and 0.70 per three sites) and minor tetrahedral Al substitution (between 0.28 and 0.58 per four sites). Under the synthesis conditions applied in this study, less than 13% of the interlayer sites are occupied by Na+, K+, and Rb+; between 13.3% and 21% by Ca2+ and Ba2+; while NH4+ gives the highest value at 34%. The remaining sites are mainly filled by Mg2+. Ce4+ is not found in the saponite structure due to the formation of cerianite, CeO2. The presence of F− had little influence on the saponite composition. The formation of Mg-saponites is explained by a model in which an increased bayerite formation resulting in a higher octahedral Al3+ substitution and more Mg2+ in solution. Mg2+ is preferentially incorporated compared with the other interlayer cations due to its smallest ionic radius in combination with its 2 + charge.
Studies of the Reactivity of the Ferrihydrite Surface by Iron Isotopic Exchange and Mössbauer Spectroscopy
Authors: Rea Brigid A. , Davis James A. , Waychunas Glenn A.
Published: August 2006

Two-line ferrihydrite is an important adsorbent of many toxics in natural and anthropogenic systems; however, the specific structural sites responsible for the high adsorption capacity are not well understood. A combination of chemical and spectroscopic techniques have been employed in this study to gain further insight into the structural nature of sites at the ferrihydrite surface. The kinetics of iron isotopic exchange demonstrated that there are at least two types of iron sites in ferrihydrite. One population of sites, referred to as labile sites, approached iron isotopic equilibrium within 24 hr in 59Fe-NTA solutions, while the second population of sites, referred to as non-labile, exhibited a much slower rate of isotopic exchange. Adsorbed arsenate reduced the degree of exchange by labile sites, indicating that the anion blocked or greatly inhibited the rate of exchange of these sites. Mössbauer spectra were collected from a variety of samples including 56Fe-ferrihydrite samples with 57Fe in labile sites, samples containing 57Fe throughout the structure, and samples with 57Fe in non-labile sites. The spectra showed characteristic broad doublets signifying poor structural order. Refined fits of the spectra indicated that labile sites have larger quadrupole splitting, hence more local distortion, than non-labile sites. In all cases, the spectra demonstrated some degree of asymmetry, indicating a distribution of Fe environments in ferrihydrite. Overall spectral findings, combined with recent EXAFS results (Waychunas et al., 1993), indicate that labile sites likely are more reactive (with respect to iron isotopic exchange) because they have fewer neighboring Fe octahedra and are therefore bound less strongly to the ferrihydrite structure. The labile population of sites probably is composed of end sites of the dioctahedral chain structure of 2-line ferrihydrite, which is a subset of the entire population of surface sites. Mössbauer spectra of samples containing adsorbed arsenate indicated that the anion may slightly decrease the distortion of labile sites and stabilized the structure as a whole by bidentate bonding.
Clay Minerals in the MacAdams Sandstone, California: Implications for Substitution of H3O+ and H2O and Metastability of Illite
Authors: Jiang Wei-Teh , Peacor Donald R. , Essene Eric J.
Published: August 2006

Clay minerals from the MacAdams Sandstone, Kettleman North Dome, California, have been studied by electron microscopy. The clay minerals fill pore space associated with fractured and brecciated clasts of K-feldspar. Curved packets of muscovite and kaolinite are caused by deformation of detrital muscovite that resulted in opening of fissures subsequently filled with dominant kaolinite and minor intergrown mixed-layer illite/smectite (I/S). Regions of authigenic R1 I/S (rectorite) with characteristic ~20 Å periodicity are intergrown with kaolinite in microfissures within K-feldspar or detrital muscovite. Clusters of small grains of muscovite with nearly ideal composition occur as stacks and intergrown with kaolinite and are tentatively inferred to be authigenic. Contrary to previous reports, no illite was found in these samples.

Electron microprobe analyses previously obtained on Kettleman Dome “illite” and subsequently used as a prime example of analyses of illite rich in excess interlayer water (H2O) and hydronium ion (H3O+) are shown to have been obtained on mixtures, and are not representative of the actual clay mineral compositions. Previous conclusions regarding significant H3O+ and H2O contents of illite are invalid because of inaccuracies inherent in bulk and EMPA analyses of illite, and do not affect arguments regarding the metastability of illite. Hydronium substitution should be favored via the reaction H2O + H+ = H3O+ only in highly acidic fluids. Ordinary illite forming in sedimentary environments with carbonates and iron oxides is unlikely to have significant H3O+ substituted for K+.
Refinement of the Nacrite Structure
Authors: Zheng Hong , Bailey Sturges W.
Published: August 2006

Nacrite crystals from a vug within a matrix of dickite at Red Mountain near Silverton, Colorado, have a = 8.906(2), b = 5.146(1), c = 15.664(3) Å, β = 113.58(3)°, V = 657.9(3) Å3, and space group Cc. The structure was solved by direct methods to determine phase angles, followed by electron density maps to locate all atoms. Refinement by least-squares ceased at R = 4.5%. Each 7 Å layer has structural detail very similar to those of dickite and kaolinite, although nacrite stacking is based on — a/3 interlayer shifts along the 8.9 Å axis (with octahedral cations alternating between the I and II sites in successive layers), whereas dickite and kaolinite are based on shifts of — a/3 along the 5.1 Å axis (with octahedral cations in the same set of sites in each layer). The angle of tetrahedral rotation is 7.8°, and the octahedral counterrotations are 7.6° and 8.1°. The H+ protons were located on DED maps. The inner 0..H1 vector points exactly toward the vacant octahedron and is depressed — 18.6° away from the level of the octahedral cations. All three surface OH groups have 0...H vectors at 50° to 66° to (001), although OH2 may not participate in interlayer hydrogen bonding. All three interlayer OH-H-O contacts are bent to angles between 132° and 141° and form contacts between 2.94 and 3.12 Å. The interlayer separation of 2.915 Å is slightly larger than in dickite, interpreted as due to a less favorable meshing of the oxygen and hydroxyl surfaces in nacrite—a direct consequence of layer shifts along the 8.9 Å axis.