Post CMP Cleaning: a Comparison of Contact and Non-Contact Physical Cleaning Methods
Authors: Dussault Donald , Beck Mark , Fournel Frank , Morales Christophe 
Published: February 2020

Chemical mechanical planarization (CMP) process steps are increasing in frequency and criticality.   The introduction of new, sensitive dielectric materials as well as sensitivity to residual slurry and particle contamination make the post CMP clean an integral part of a good yielding CMP step.

Brush Scrubbing is the traditional method of post CMP cleaning.  With this contact cleaning method particles are removed by direct contact of a rotating brush with the wafer surface.  These particles are then swept away by the cleaning solution.  This method of cleaning has some well known challenges, among them cross contamination from wafer to wafer, brush marking and scratching as well as process feedback and control.

An alternative physical cleaning method utilizes the cavitation created by the presence of Megasonic energy in the process fluid to provide a non-contact method of slurry residual and particulate removal from the planarized surface.   The Megasonic apparatus used in these experiments has been successfully applied to other single wafer cleaning processes and is implemented in many large volume production applications.

Most mass production post CMP cleaning processes consist of a series of cleaning and chemistry steps as well as a mix of physical cleaning approaches.  The challenge in quantifying effect and comparing cleaning efficiency between contact and non-contact physical cleaning has been in the isolation of cleaning results attributed to a change in method.

In this work we were able to provide conditions for a direct comparison of cleaning methods in a special post CMP scrubber.  This tool is configured for brush or Megasonic processes in the same chamber with the identical wafer flow from the polisher.  The CMP was done on thermal SiO2 using  two varieties of conventional slurry and a common pad type.  Fifty wafers were split processed, half with 150835 and half with D3586.  A large delta in particle removal efficiency was observed based on slurry type alone.

The brush parameters were based on a long term process of record. (Table 1)  Several megasonic parameters were varied to better understand the process window.  Analysis of cleaning results was performed using an SP2 with a threshold of 90nm. (Figure 1)

Table 1, Experimental process recipe details

Brush Recipe

Step
Time (sec)
Chemical
Wafer RPM
Brush RPM

1
40
NH4OH 2%
20
80

2
40
DIW
20
80

3
20
DIW
60
No Brush

4
 
Dry
2000
 

Meg Recipe 1

Step
Time (sec)
Chemical
Wafer RPM
W/cm2

1
52
NH4OH 2%
60
2.5

2
48
DIW
60
2.5

3
 
Dry
2000
0

Meg Recipe 2

Step
Time (sec)
Chemical
Wafer RPM
W/cm2

1
52
NH4OH 2%
60
1.85

2
48
DIW
60
1.85

3
 
Dry
2000
0

Meg Recipe 3

Step
Time (sec)
Chemical
Wafer RPM
W/cm2

1
90
NH4OH 2%
60
1.85

2
10
DIW
60
1.85

3
 
Dry
2000
0

These direct comparison tests prove that the non-contact Megasonic method equals or exceeds the cleaning results achieved with the traditional brush cleaning under identical process flow and conditions.

Figure 1: Post CMP clean particle counts 90nm threshold with D3586 slurry.

Figure 1