ПОРІВНЯННЯ АМІНІВ ЯК ГАЗОУТВОРЮВАЧІВ ВОГНЕЗАХИСНИХ КОМПОЗИЦІЙ ІНТУМЕСЦЕНТНОГО ТИПУ
Authors: VAKHITOVA LIUBOV , KALAFAT KONSTANTIN , TARAN NADIYA , BESSARABOV VOLODYMYR 
Published: January 2022

Purpose. Study of influence of blowing agents amines structure on the construction processes of thermal insulating char layer of intumescent system ammonium polyphosphate/pentaerythritol/amine and fire protection efficiency of this system at high temperatures. Methodology. A fire retardant mixture of ammonium polyphosphate/pentaerythritol/amine was chosen as a model intumescent system. Dispersion of vinyl acetate copolymer with vinyl ether of versatic acid was used as a polymeric component. A step-by-step study of the characteristics of the char layer of the intumescent composition was applied in the study, consisting in the analysis of the characteristics of the char formed after keeping the intumescent composition samples at a certain temperature between 100 and 800 °C, char residue mass (m, %), structure and density of the formed char layer. The method of infrared spectroscopy was used for identification of products of thermolysis of intumescent systems. Determination of fire protection efficiency of intumescent coatings was carried out in a mini-oven under standard fire conditions. Findings. The influence of the structure of amines blowing agents on the formation of char layer of intumescent system ammonium polyphosphate/pentaerythritol/amine was studied. Physico-chemical parameters of char layer formed during high temperature swelling of intumescent system components with varying amine: urea, melamine, dicyandiamide, guanidine, thiocarbamide, formylthiosemicarbazide, thiosemicarbazide, phenylethylcarbamide have been determined. In the temperature range 200–400 oC for systems with linear amines (urea, thiocarbamide, thiosemicarbazide), there is a rapid formation of insulating layer with intense outgassing (high intumescent coefficients K) and the same rapid its destruction with significant losses of char residue mass (Δm). The presence of melamine, dicyandiamide and guanidine in intumescent system provides constancy of intumescent coefficient at minimal mass loss. Chemical transformations of intumescent systems were studied by the method of infrared spectroscopy when the investigated amines were varied. It was found that linear diamines do not form stable spatially branched phosphamide compounds with phosphates as the basis of a thermostable heat-insulating frame. At the same time in IR spectra of char residue systems with melamine, dicyandiamide and guanidine the absorption bands of P-N-C bonds (1070–1050 cm-1) and P-N (980–950 cm-1) up to 600–700 oC are observed. Fire tests proved that melamine, dicyandiamide and guanidine are blowing agents providing maximum protection of metal against fire and can be used for composition of fire retardants for steel constructions.Originality. It has been proved that amines in intumescent polyphosphate system perform at least two functions: blowing agents by means of thermal destruction to incombustible gases and nucleophilic compound that takes part in char layer formation by aminolysis of electrophilic substrates.Practical value. The optimum amine blowing agents for developing formulations of intumescent coatings with enhanced flame retardant properties have been established.