Comparative Study of Particle Size and Shape Effects on Powder Packing Densities
Authors:   Department of Mechanical and Manufacturing Engineering, Faculty of Engineering and Built Environment, The National University of Malaysia, Bangi 43600, Selangor, Mazlan Mohd Rhafiq , Jamadon Nashrah Hani ,   Department of Mechanical and Manufacturing Engineering, Faculty of Engineering and Built Environment, The National University of Malaysia, Bangi 43600, Selangor,   Advanced Materials Engineering & Smart Manufacturing (MERCU), Department of Mechanical and Manufactuing Engineering, Faculty of Engineering & Built Environment, Universiti Kebangsaan Malaysia, 43600 Bangi, Selangor, Malaysia, Sulong Abu Bakar ,   Department of Mechanical and Manufacturing Engineering, Faculty of Engineering and Built Environment, The National University of Malaysia, Bangi 43600, Selangor,   Advanced Materials Engineering & Smart Manufacturing (MERCU), Department of Mechanical and Manufactuing Engineering, Faculty of Engineering & Built Environment, Universiti Kebangsaan Malaysia, 43600 Bangi, Selangor, Malaysia, Aripin Mohammad Azlan ,   Department of Mechanical and Manufacturing Engineering, Faculty of Engineering and Built Environment, The National University of Malaysia, Bangi 43600, Selangor,   Department of Mechanical Engineering, Faculty of Engineering, City University 46100, Petaling Jaya, Malaysia., Jamhari Fathin Iliana ,   Department of Mechanical and Manufacturing Engineering, Faculty of Engineering and Built Environment, The National University of Malaysia, Bangi 43600, Selangor, Yusof Farazila ,   Department of Mechanical Engineering, Faculty of Engineering, University of Malaya, Jalan Professor Diraja Ungku Aziz, 50603 Kuala Lumpur, Wilayah Persekutuan Kuala Lumpur, Malaysia
Published: November 2024

Uncertainties in powder spreading in powder bed-based additive manufacturing (AM) have posed challenges in the quality and repeatability aspects of manufactured parts. These challenges result in high porosity due to voids existing between the powder bed particles. This work focuses on identifying the uncertainty induced by particle size distribution (PSD) on powder flowability using SS316L as a model material. Various sizes of particles, ranging from 10 µm to 100 µm, as well as spherical and satellite-shaped particles with a bimodal ratio of 70:30, were analyzed. The tapped density, apparent density, and Hausner ratio of each sample will be determined using USP 616. Smaller particle sizes have been shown to reduce both bulk and apparent density. Meanwhile, the shapes of particles also contribute to the packing ability between the powder particles. Satellite powder has been proven to increase the diameter of the powder, consequently enhancing the bulking density of the powder particles. Moreover, bimodal particles have been shown to increase both bulk and tapped density, whereas smaller powder is not able to fill the voids that exist between the larger particles. However, the bulk density decreases as the size ratio between the powder particles increases, indicating that smaller powder is capable of filling the gaps between the particles. When comparing the powder particles in terms of Hausner ratio value, bimodal particles have been shown to cause the poorest flowability with a value of 1.19856. This is due to the fact that the smaller particles between the larger particles increase the friction between the powders. Therefore, this study illustrates how particle size and shape influence powder packing densities, which is crucial for optimizing material design and processing techniques.