Analysis of polymeric materials properties changes after addition of reinforcing fibers
Authors: Gnatowski Adam , Kijo-Kleczkowska Agnieszka , Gołębski Rafał , Mirek Kamil 
Published: June 2019

Purpose

The issues concerning the prediction of changes in properties of polymer materials as a result of adding reinforcing fibers are currently widely discussed in the field of polymer material processing. This paper aims to present strengths and weaknesses of composites based on polymer materials strengthened with fibers. It touches upon composite cracking at the junction of a matrix and its reinforcement. It also discusses the analysis of changes in properties of chosen materials as a result of adding reinforcing fibers. The paper shows improvement in the strength of polymer materials with fiber addition, which is extremely important, because these types of composites are used in the aerospace, automotive and electrical engineering industries.

Design/methodology/approach

Comparing the properties of matrix strength with fiber properties is practically impossible. Thus, fiber tensile strength and composite tensile strength shall be compared (González et al., 2011): tensile (glass fiber GF) = 900 [MPa], elongation ΔL≈ 0; yield point (polyamide 66) = 70−90 [MPa], elongation Δ[%] = 3,5-18; tensile (polyamide 66 + 15% GF) = 80-125 [MPa], elongation Δ[%] ≈ 0; tensile (polyamide 66 + 30% GF) = 190 [MPa], elongation Δ[%] ≈ 0; yield point (polyamide 6) = 45-85 [MPa], elongation Δ[%] = 4-15; tensile (polyamide 6 + 15% GF) = 80-125 [MPa], elongation Δ[%] ≈ 0; tensile (polyamide 6 + 30% GF) = 95-130 [MPa] elongation Δ[%] ≈ 0. Comparison of properties of selected polymers and composites is presented in Tables 1−10 and Figures 1 and 2. The measurement methodology is presented in detail in the paper Kula et al. (2018). The increase in fiber content (to the extent discussed) leads to the increase in yield strength stresses and hardness. The value of yield strength for polyamide with the addition of fiberglass grows gradually with the increase in fiber content. The hardness of the composite of polyamide with glass balls increases together with the increase in reinforcement content. The changes of these values do not occur linearly. The increase in fiber content has a slight impact on density change (the increase of about 1 g/mm3 per 10 per cent).

Findings

The use of polymers as a matrix allows to give composites features such as: lightness, corrosion resistance, damping ability, good electrical insulation and thermal and easy shaping. Polymers used as a matrix perform the following functions in composites: give the desired shape to the products, allow transferring loads to fibers, shape thermal, chemical and flammable properties of composites and increase the possibilities of making composites. Fiber-reinforced polymer composites are the effect of searching for new construction materials. Glass fibers show tensile strength, stiffness and brittleness, while the polymer matrix has viscoelastic properties. Glass fibers have a uniform shape and dimensions. Fiber-reinforced composites are therefore used to increase strength and stiffness of materials. Polymers have low tensile strength, exhibit high deformability. Polymers reinforced by glass fiber have a high modulus of elasticity and therefore provide better the mechanical properties of the material. Composites with glass fibers do not exhibit deformations in front of cracking. An increase in the content of glass fiber in composites increases the tensile strength of the material. Polymers reinforced by glass fiber are currently one of the most important construction materials and are widely used in the aerospace, automotive and electro-technical industries.

Originality/value

The paper presents the test results for polyethylene composites with 25 per cent and 50 per cent filler coming from recycled car carpets of various car makes. The tests included using differential scanning calorimetry, testing material hardness, material tensile strength and their dynamic mechanical properties.