Destruction of polymer insulation and threshold amplitudes of current pulses of different temporal shapes for electric wires and cables in the low- and high-current circuits of pulse power engineering, electrical engineering and electronic devices
Authors: Baranov M.I. , Buriakovskyi S.G. , Kniaziev V.V. 
Published: December 2021

Goal. Development of engineering method for settlement of threshold amplitudes Impk of single-pulse current ip(t) of different temporal shapes for electric wires and cables with polyethylene (PET), polyvinylchloride (PVC) and rubber (R) half-length insulation, used in modern pulsed power engineering, electrical engineering and electronics in their low- and high-current circuits. Methodology. Basis of the theoretical and applied electrical engineering, electrical power engineering, electrophysics bases of technique of high-voltage and large pulsed currents, bases of low- and high-current electronics, measuring technique, electromagnetic compatibility and standardization. Results. Development of engineering method is executed on close calculation determination of threshold amplitudes Impk of single-pulse axial-flow current ip(t) of different temporal shapes for electric wires and cables with copper (aluminum) current-carrying parts and PET, PVC and R half-length insulation, used in the ow- and high-current circuits of pulsed electrical power engineering, electrical engineering and electronics. Electrothermal resistibility of half-length insulation of the examined cable and wire products (CWP), proper maximum to the possible temperatures of heating of current-carrying and insulating parts of the probed wires and cables and shutting out the offensive of the phenomenon destruction in the indicated insulation of CWP, was fixed based on this method. Calculation analytical correlations are obtained for finding in probed CWP of threshold numeral values of Impk amplitudes of pulses of current ip(t), time-varying both on aperiodic dependence of type τf/τp with duration of their front τf and duration of their pulses τp and by law of exponential attenuation sinewave. It is shown that at Imp>Impk destruction of their half-length insulation, resulting in the decline of service life of CWP, will come from the thermal overheat of current-carrying parts of the examined electric wires and cables. The examples of practical application of the offered method are resulted upon settlement for a radiofrequency coaxial cable RC 50-4-11 with middle sizes is easily soiled with continuous PET insulation of threshold amplitudes of Impk of standard aperiodic pulses of current ip(t) from nano-, micro- and millisecond temporal ranges of shape of τf/τp=5 ns/200 ns, τf/τp=10 μs/350 μs and τf/τp=7 ms/160 ms. It is shown that with the proper growth of parameter τp>>τf for flow on a continuous copper tendon and split copper shell of radiofrequency coaxial cable RC 50-4-11 with middle sizes is easily soiled indicated homopolar pulses of current ip(t) substantial diminishing of their threshold amplitudes of Impk (with 531,2 кА for the nanosecond pulse of current of type 5 ns/200 ns to 1.84 кА for the millisecond impulse of current of type of 7 ms/160 ms takes place). Originality. An engineering method is first developed for close settlement of threshold numeral values of Impk amplitudes of single-pulse axial-flow current ip(t) of arbitrary peak-temporal parameters for electric wires and cables with copper (aluminum) current-carrying parts and PET, PVC and R half-length insulation. Practical value. Application in electrical engineering practice of the offered engineering method for determination of threshold amplitudes Impk of the indicated pulses of axial-flow current ip(t) for the probed electric wires and cables will allow considerably to increase service life of examined CWP.