α-Fe2O3/Graphene Nanocomposite as Anode Material for Sodium-Ion Batteries with Enhanced Capacity Retention
Authors: Zhang Zhijia , Wang Yunxiao , Chou Shulei , Li Huijun , Liu Hua Kun , Wang Jiazhao 
Published: February 2020

Among the different energy storage systems, rechargeable lithium-ion batteries (LIBs) have been widely applied in various portable electronic devices due to their high energy densities, long cycle life, and lack of significant memory effect [1]. For wide-scale implementation of renewable energy, LIBs, however, face challenges related to their safety, lifetime, and cost. Based on the wide availability and low cost of sodium, sodium-ion batteries (SIBs) have the potential for meeting the demands of large-scale and sustainable applications. Many cathode materials have been proposed, whereas only a few anode materials have been investigated for SIBs [2]. The sodium ion (1.02 Å) has a larger ionic radius than the lithium ion (0.76 Å), so that graphite cannot be used as anode for SIBs [3]. There is less choice of anode materials for SIBs. Transition metal oxides have been investigated as possible negative electrodes, relying on insertion of Na+ at low voltages. Valvo et al. reported that the electrochemical sodiation of nanostructured Fe2O3 is reversible with the voltage range of 0.05-3.0 V vs. Na+/Na, and its specific capacity is 350 mAh g-1 over 30 cycles at 40 mA g-1 [4, 5]. Fe2O3 requires further modifications, however, to overcome its limitations for SIBs, such as poor electronic conductivity, volume variations, and related cycling issues. To improve the electronic conductivity and capacity retention, we prepared α-Fe2O3/Graphene nanocomposite using the ultrafast and environmentally friendly microwave autoclave method [6].

The α-Fe2O3/Graphene nanocomposite was analysed by field emission scanning electron microscopy (FESEM) and X-ray diffraction (XRD) to determine their morphology and structural properties. Graphene contents in the composites were determined by thermogravimetric analysis (TGA). α-Fe2O3 nanoparticles are embedded in conductive and interconnected graphene networks [Fig 1(a)]. This nano-architecture increases the electronic conductivity and buffers volume change in α-Fe2O3/Graphene nanocomposite electrode. It can be observed in the XRD pattern in Fig. 1 that the α-Fe2O3/Graphene nanocomposite has more broad peaks than the α-Fe2O3 [Fig 1(b)]. The electrochemical results show that the composite electrode containing 10 wt.% graphene has higher initial capacity recovery (69 %) than the pure Fe2O3 electrode (59 %) [Fig 1(c)] [4]. Moreover, the composite shows better capacity retention than in the reported results in the literature, retaining 401 mAh g-1 at current density of 40 mA g-1 after 30 cycles in the range of 0.05-2.60 V vs. Na+/Na [Fig 1(d)] [3, 4].

References

[1] P. Poizot, S. Laruelle, S. Grugeon, L. Dupont, J.M. Tarascon, Nature 407(6803) (2000) 496.

[2] M.D. Slater, D. Kim, E. Lee, C.S. Johson, Adv. Funct. Mater. 23 (2013) 947.

[3] H. Xiong, M.D. Slater, M. Balasubramanian, C.S. Johnson, T. Rajh, J. Phys. Chem. Lett. 2 (2011) 2560.

[4] M. Valvo, F. Lindgren, U. Lafont, F. Björefors, K. Edström, J. Power Sources 245 (2014) 967.

[5] M.C. López, P. Lavela, G.F. Ortiz, J.L. Tirado, Electrochem. Commun. 27 (2013) 152.

[6] C. Zhong, J. Wang, Z. Chen, H. Liu, J. Phys. Chem. C 115 (2011) 25115.

Figure captions

Figure 1. (a) FESEM image and (b) XRD pattern of α-Fe2O3/Graphene nanocomposite with 10 wt.% graphene; (c) discharge/charge curves of the selected cycles between 0.05 and 2.60 V vs. Na+/Na at a gravimetric current density of 40 mA g-1 for the α-Fe2O3/Graphene nanocomposite electrode with 10 wt.% graphene.