Peroxidase immobilized on acrylic copolymer beads
Authors: Cremonesi Pietro , Mazzola Giorgio , Focher Bonaventura , Vecchio Giuseppe
Published: April 2003

Horseradish peroxidase was immobilized onto crosslinked acrylamide beads after a pretreatment of the enzyme with glycidyl‐methacrylate. The enzyme initiates the polymerization of the acrylic comonomers. The activity of the solid materials increases by increasing the amount of glycidyl‐methacrylate and the time of reaction between the vinyl monomer and the enzyme, while it is not greatly influenced by the concentration of the acrylamides.

The beads obtained showed little dependence on diffusion; the Km values using guaiacol and H2O2 as substrates were the same as for free peroxidase.

No decrease in stability was observed after 150h storage at room temperature or after freeze‐drying.

By continuous flow measurements, using guaiacol or iodide as cosubstrate, a different adsorption of the reaction products was found.
Vinyl polymerization by metal complexes. 22. Initiation by α,ω‐diaminoalkane‐copper(II) complexes
Authors: Inaki Yoshiaki , Nakagawa Shuichi , Kimura Keiichi , Takemoto Kiichi
Published: April 2003

Free radical polymerization of acrylonitrile initiated by various α,ω‐diaminoalkane‐copper(II) complexes was studied in dimethyl sulfoxide solution. It was found that the stable copper(II) complexes, like ethylenediamine copper(II) complex, could hardly initiate the polymerization, while the unstable copper(II) complexes, such as 1,5‐diaminopentane, 1,6‐diaminohexane and n‐butylamine complexes could initiate the polymerization.

Initiation was further studied spectrophotometrically. Reduction of the copper(II) to the copper(I) complexes was ascertained to occur during the polymerization by visible spectroscopy and cuproin coloration method. The rate of reduction was related closely to the stability of the diamine‐copper(II) complexes. From the results the initiation mechanism was discussed.
Iodine reaction of vinyl acetate — vinyl propionate copolymers II. Dependence of iodine affinities of the copolymers on the sequence distribution of vinyl acetate‐units
Authors: Hirai Toshihiro , Tanaka Makoto
Published: April 2003

The reactions of iodine with vinyl acetate (VAc) — vinyl propionate (VPr) copolymers in aqueous solutions of potassium iodide were investigated photometrically. The iodine affinity (I/VAc) of VAc‐units was defined as the number of bound iodine atoms per VAc‐unit and determined from the absorbance of the formed colored complex. The dependence of the I/VAc values on the copolymer composition was discussed with respect to the sequence distribution of VAc‐units in the copolymer chains. The dependence of the I/VAc value on the copolymer composition of block copolymers provided a useful information concerning the saponification of PVAc because the here used block copolymers were prepared by propionylation of partially saponified PVAc.
The analysis of phenol‐, resorcinol‐ and phenol/resorcinol‐formaldehyde resins by catalytic thermometric titrimetry. Part I. Novolacs
Authors: Greenhow Edward Joshua , Hargitt Robert , Shafi Abid Akhter
Published: April 2003

Non‐aqueous catalytic thermometric titration is used for the determination of the phenol and resorcinol components of resins formed by the acid‐catalysed condensation of phenol, resorcinol and mixtures of phenol and resorcinol, with formaldehyde.
Polyreaktionen an Pigmentoberflächen. VI. Mitteilung: Radikalisch initiierte Polyreaktionen an SiO2‐Oberflächen
Authors: Laible Richard , Hamann Karl
Published: April 2003

Durch eine radikalische Polymerisationsreaktion wird Polystyrol kovalent an die Oberfläche von Siliciumdioxid gebunden. Die Pfropfreaktion wird ausgelöst durch kovalent an der SiO2‐Oberfläche gebundene Phenylradikale, die durch thermischen Zerfall von Phenyl‐diazo‐thioäthergruppen entstehen. Die Menge des aufgepfropften Polymeren ist abhängig von den Reaktionsparametern Zeit, Temperatur und Konzentration an Monomerem und an initiierenden Diazogruppen. Die Pfropfpolymerisation verläuft in heterogener Phase nach dem für radikalische Polymerisationen bekannten Zeitgesetz in 1. Ordnung bezüglich Monomerkonzentration und ist beendet, wenn initiierende Radikale infolge von Rekombinationen oder sterischer Hinderung an der SiO2‐Oberfläche die Polymerisation nicht mehr auslösen können.

Der kovalente Charakter der Bindung zwischen Polymerem und Siliciumdioxid wird IR‐spektroskopisch und durch Adsorptions‐Desorptions‐Versuche nachgewiesen. Die durch die radikalische Polyreaktion an der Oberfläche gebundene Menge an Polymerem ist um eine bis zwei Größenordnungen größer als die irreversibel adsorptiv gebundene. Die Struktur der gebundenen Makromoleküle kann als solche sich zum Teil durchdringender, elliptoidisch verformter Knäuel beschrieben werden.
The relationship between the molecular weight and the critical miscibility composition of a solvent‐nonsolvent‐terpolymer system
Authors: Kambe Yuko , Honda Chikako
Published: April 2003

A theoretical equation for the dependence of the apparent molecular weight measured by light scattering on the solvent used has been derived with regard to the composition heterogeneity. Terpolymers corresponding to a partial azeotrope were synthesized from styrene, acrylonitrile, and methyl methacrylate with mole fractions of 0.55, 0.16, and 0.29, respectively. The molecular weight measured by light scattering was found to be independent of the solvent used. Therefore the terpolymer was concluded to be apparently homogeneous in composition. The relationship between the molecular weight M of the terpolymer and the volume fraction of the nonsolvent γ in the solvent mixture at the precipitation point in a butanone‐methanol‐terpolymer system was experimentally proved to follow the equation

equation image

where γ0 and b′ are constants. Between the molecular weight and the limiting viscosity number [η] of the terpolymer the following relationships are valid at 35°C:

equation image

and

equation image
Determination of phenol/formaldehyde molar ratio of resol resins by infrared spectroscopy
Authors: Erä Väinö A. , Salo Hannu , Kaps Tiit , Lindberg J. Johan
Published: April 2003

A series of resol‐type phenol‐formaldehyde resins with varying phenol/formaldehyde (P/F) molar ratio were investigated by infrared spectroscopy. The infrared spectroscopic data suggest that absorbance ratio of D2920, D1610, D1150, D1010, and D760 based on 1 590 cm−1 band can be used for the determination of phenol/formaldehyde molar ratio of the resins.
Theorie des Ultraschallabbaus auf der Grundlage des Perlschnurmolekül‐Modells
Authors: Rieber G. , Schoon Th. G. F.
Published: April 2003

Um Aufschluß über Kinetik und Mechanismus der Ultraschall‐Depolymerisation zu erhalten, wurde der Versuch unternommen, den zeitlichen Ablauf des Abbaus auf der Grundlage des Perlschnurmolekül‐Modells theoretisch zu beschreiben. Nach diesem molekularen Modell sind Makromoleküle – ähnlich einer Perlschnur – aus mehreren, näherungsweise sphärischen, einheitlich und für ein gegebenes Polymeres charakteristisch großen sog. Tertiäreinheiten aufgebaut.

Für den Ultraschall‐Abbau von Perlschnurmolekülen werden zwei verschiedene Mechanismen diskutiert: der fragmentarische, bei dem die Perlschnurmoleküle stufenweise über Bruchstücke nach und nach zu den Tertiäreinheiten abgebaut werden und der stufenlose, bei dem die Depolymerisation der Perlschnurmoleküle unmittelbar zu den Tertiäreinheiten führt, so daß während des Abbaus nur Moleküle vom Anfangs‐ und Grenzmolekulargewicht, M0 und M∞, auftreten. Die mathematische Behandlung des stufenlosen Abbaus lieferte folgende Beziehung:

Mit Hilfe dieser Abbaugleichung lassen sich bei Kenntnis von M0, M∞ und eines einzigen MWertes, der zur Berechnung der „Zertrümmerungskonstanten”︁ π erforderlich ist, Abbaukurven Mi=f (Beschallungszeit i), oder umgekehrt bei Kenntnis nur des Anfangs einer experimentellen Abbaukurve Grenzmolekulargewichte berechnen. Durch Vergleich der berechneten Abbaukurve mit der experimentell bestimmten ist es möglich, zwischen stufenlosem und fragmentarischem Abbau zu unterscheiden.
Die Struktur von teilweise hydrolysiertem Polyacrylnitril
Authors: Šoler J. , Baldrian J.
Published: April 2003

Die Struktur von teilweise hydrolysiertem Polyacrylnitril wurde mit Hilfe der Röntgenstreuung im Kleinwinkel‐ und Weitwinkelbereich untersucht. Das Copolymere ist aus zwei Phasen zusammengesetzt, einer kristallinen und einer amorphen. Die kristalline Phase wird von Kristalliten des Polyacrylnitrils gebildet, die amorphe Phase besteht in trockenem Zustand aus Polyacrylamid und im gequollenen Zustand aus Polyacrylamid mit Wasser. Die Quellung übt keinen Einfluß auf die Kristallite des Polyacrylnitrils aus. Das Zwei‐Phasen‐Modell für die Struktur des Copolymeren wird durch die Kleinwinkelmessungen bestätigt, aus denen hervorgeht, daß die übermolekulare Struktur im trockenen Zustand durch ein parakristallines Gitter mit mittlerer Periode von 100Å gebildet wird. Das vorgeschlagene Strukturmodell steht im Einklang mit der Vorstellung, daß ein Blockcopolymers vorliegt. Bei der Orientierung ordnen sich die Molekülketten des Copolymeren parallel zur Verstreckrichtung. Im übermolekularen Gebiet tritt die Orientierung durch das Entstehen von Fibrillen und Fibrillensträngen in Erscheinung, wobei der minimale Fibrillenquerschnitt im trockenen Copolymeren halb so groß ist wie im gequollenen. Die Quermessungen der Fibrillenstränge haben in beiden Fällen annähernd dieselbe Größe.
Die Polymerisation von Lactamen. VII. Die Autopolymerisation von 8‐Capryllactam
Authors: Falgová Irena , Kondelíková Jaroslava , Králíček Jaroslav
Published: April 2003

Durch Erhitzen von wasserfreiem 8‐Capryllactam ohne Anwesenheit von Katalysatoren auf Temperaturen von 240–280°C entsteht ein Polymerprodukt. Die Polymerisation ist durch eine kurze Induktionsperiode gekennzeichnet, die sich mit ansteigender Temperatur vermindert. Der Polymerisationsgrad bleibt im Bereich von 40–90% Polymergehalt fast konstant, im Gebiet hoher Polymergehalte steigt er steil an. Bei höheren Temperaturen entstehen unlösliche vernetzte Produkte. In der vorliegenden Arbeit wird der mögliche Mechanismus der Autopolymerisation von Lactamen diskutiert.
Reaktive Polymere. II. Die Herstellung von Metallchelaten vernetzter Polymerer
Authors: Kálal Jaroslav , Švec František , Kálalová Eliška , Radová Zdenka
Published: April 2003

Die Reaktionen von zweiwertigen Metallionen (Cu, Co, Ni und Zn) mit Äthylendiamin, das an das homogen vernetzte Terpolymere Glycidylmethacrylat‐Styrol‐Divinylbenzol oder das makroporöse Copolymere Glycidylmethacrylat‐Äthylenglykoldimethacrylat gebunden ist, wurden untersucht. Dabei wurde die Kapazität der Polymeren, die Austauschfähigkeit und die Reaktionsgeschwindigkeit bestimmt.
Quantitative Untersuchungen zum Aushärtungsverhalten von Phenoplasten mittels differentialthermoanalytischer Messungen (DSC)
Authors: Schindlbauer H. , Henkel G. , Weiss J. , Eichberger W.
Published: April 2003

In der vorliegenden Untersuchung wird der Versuch unternommen, mittels DSC‐Analyse das Aushärtungsverhalten verschiedener Phenol‐Formaldehyd‐Harze näher zu studieren. Unter Verwendung eines speziellen dynamisch‐statischen Versuchsprogramms ist es gelungen, den Aushärtungsgrad in Abhängigkeit von der Härtungszeit, der Härtungstemperatur und der gerätebedingten Aufheizrate experimentell zu bestimmen. Weiterhin war es möglich, die für einen bestimmten Aushärtungsgrad eines vorgegebenen Harzes notwendige Härtetemperatur und die notwendige Zeit der Härtung zu bestimmen. Die Interpretation der Meßergebnisse läßt den Schluß zu, daß die Aktivierungsentropie der Vernetzungsreaktion mit zunehmendem Vernetzungsgrad deutlich zunimmt.
Studies on the reactivities of diisocyanates
Authors: Ghatge N. D. , Dandge D. K.
Published: April 2003

Bis(3‐isocyanatophenyl)‐sulfone and Bis(3‐isocyanatophenyl)‐methane were synthesized and their reactivities studied by spectroscopic methods.
Bestimmung von Aminoendgruppen in ionisch gefärbten Polyamidfasern durch Ionenaustausch
Authors: Beines U. , Stein G. , Valk G.
Published: April 2003

Das beschriebene Verfahren gestattet die Bestimmung von Aminoendgruppen an mit Säurefarbstoffen gefärbten Polyamiden. Eine Lösung des gefärbten Polymeren wird zur Entfernung des Farbstoffes einer Austauscherbehandlung unterworfen; die so freigesetzten Aminoendgruppen werden dann durch eine potentiometrische Titration bestimmt.

Unter den Bedingungen der Austauscherbehandlung ist bei Polyamid‐6 und ‐6,6 eine Hydrolyse der Amidbindung, eine hydrolytische Abspaltung von Kettenlängenregulatoren und eine Adsorption des Polymeren am Austauscher auszuschließen. Der störende Einfluß von Faserpräparationen läßt sich durch eine vorherige Extraktion mit polaren Lösungsmitteln beseitigen. Die während des Färbevorganges auftretende Hydrolyse des Polyamids wird durch die Sulfogruppen des Farbstoffes katalysiert.
Organo‐metal carbonyl compounds of iron, molybdenum, and manganese as photosensitisers of the anhydride cure of epoxy resins
Authors: Brown D. L. S. , Connor J. A. , Dobinson B. , Stark B. P.
Published: April 2003

Compounds of the types [π‐C5H5M(CO)nX] (M = Fe, n = 2; M = Mo, n = 3; X = CH3, CH2C6H5, CH2Si(CH3)3, CH2OCH3, Sn(C6H5)3, SnCl3, HgCl, I), [Mn(CO)5CH3], and [(π‐CH3C5H4)Mn(CO)3] have been examined as catalysts for the cure of epoxy resins under various conditions. It was found that the compounds [π‐C5H5Fe(CO)2R] (R = CH3, CH2C6H5) and [π‐C5H5Mo(CO)3CH3] are active photosensitizing agents for the anhydride cure of certain epoxy resins. The mechanism of the process is discussed.
13C‐Angereicherte Monomere zur NMR‐Spektroskopie von Polymeren
Authors: Stützel Bernhard , Ritter Wolfgang , Elgert Karl‐Friedrich
Published: April 2003

Ausgetestete Synthesewege für folgende partiell 13C‐angereicherte Monomere werden beschrieben:
Gemisch aus 1‐13C‐2‐Phenylpropen, 3‐13C‐2‐Phenylpropen und 2‐Phenylpropen,
2‐(1‐13C‐Phenyl)‐propen,
2‐13C‐Butadien‐1,3,
1‐13C‐Butadien‐1,3,
2‐13C‐Methacrylnitril,
13CN‐Methacrylnitril.

Die Dotierungsgrade wurden durch die 13C‐Satelliten im 1H‐NMR‐Spektrum sowie durch Vergleich der 13C‐NMR‐Spektren der Monomeren mit natürlichem und angereichertem 13C‐Gehalt bestimmt.
Phenol‐formaldehyde impregnant characterization by infrared spectroscopy and differential scanning calorimetry
Authors: Erä Väinö A. , Lindberg J. Johan , Mattila Antti , Vauhkonen Leo , Linnahalme Turo
Published: April 2003

A series of resol‐type phenol‐formaldehyde resins was investigated by infrared spectroscopy and differential scanning calorimetry. The molar ratio of phenol to formaldehyde was determined from the absorbance ratio D1010/D1610. Differences between the reactivities of resins were confirmed by the molar phenol to formaldehyde ratio, heat of reaction and gelation time.
Adhesives from polyepichlorohydrin elastomers. I. Studies on the properties of adhesive solutions of polyepichlorohydrin
Authors: Kozakiewicz Janusz , Penczek Piotr
Published: April 2003

The dependence of the specific viscosity of polyepichlorohydrin solutions in various solvents on the concentration of solutions was investigated. It was shown that there is only a little difference between specific viscosity measured in various solvents at the same concentration.

Solubility diagrams for polyepichlorohydrin were made using both Hansen and Lieberman method and some properties (specific viscosity, evaporation rate and solvent retention in adhesive films) of solutions were plotted against the composition of solvent mixtures. A definite dependence of the specific viscosity on the position of solvent mixture in solubility diagrams was found. This behaviour is discussed in terms of intermolecular attractions.
High 1,4‐cis‐polybutadiene by uranium catalyst. III. Strain induced crystallization and processability
Authors: Giuliani G. P. , Sorta E. , Bruzzone M.
Published: April 2003

The crystallization in flow of various 1,4‐cis‐polybutadienes, including an extremely high cis‐polybutadiene content obtained with uranium catalyst, has been studied in a capillary rheometer. The influence on the crystallization in flow of temperature, pressure, shear rate has been investigated and compared with the conditions in the flow field of a roll‐mill. It is shown that when these conditions are suitable for inducing, the crystallization of the rubber, the processability at the roll‐mill is substantially improved. The molecular weight distribution plays only a minor role for the highest cistactic polybutadienes. The reason of the correlation between crystallization and roll‐mill processability is briefly discussed.
High 1,4‐cis‐polybutadiene by uranium catalyst. IV. Stretch induced crystallization and ultimate properties
Authors: Gargani L. , Giuliani G. P. , Mistrali F. , Bruzzone M.
Published: April 2003

Non‐equilibrium tensile properties of high‐cis‐polybutadiene obtained from an uranium based catalyst are evaluated in comparison with other polybutadienes having lower sterical purity. The conditions for incipient stretch induced crystallization are described. Ultimate properties and strain induced crystallization are found strongly related and their dependence on cis‐content is discussed. The higher sterical purity accounts for the best performance of uranium polybutadiene.
An investigation of the effect of gamma rays on the properties of paper
Authors: Szymański W. , Szablewski L.
Published: April 2003

The influence of gamma radiation on the mechanical and physico‐chemical properties of paper has been investigated. The tensile strength, the tear strength, the elongation, and the burst strength have been measured as well as the conductivity and the pH of the water extract. The number of the carboxyl groups and the copper number were also determined. It is shown that the exposure to a 1–10 Mrad dose of gamma radiation results in a not very significant deterioration of the paper quality.
Einfluß der Stabilisatorkonzentration auf die Oxidationsgeschwindigkeit vernetzter Polydiene
Authors: Lorenz Otto , Parks Carl R.
Published: April 2003

Die Oxidationsgeschwindigkeit vox ungefüllter Vulkanisate mit unterschiedlicher Netzwerkstruktur wurde in Abhängigkeit von der Konzentration verschiedener zugesetzter Stabilisatoren der allgemeinen Formel AH, nämlich 2,2′‐Methylen‐bis(4‐methyl‐6‐tert‐butylphenol), N‐Phenyl‐2‐naphthylamin und N,N′‐Diphenyl‐p‐phenylendiamin bestimmt. Die Oxidationsgeschwindigkeit läßt sich durch folgende empirische Gleichung beschreiben:

Im Falle der Amin‐Stabilisatoren hat x den Wert 1, für das Bisphenol den Wert 0,5. Der erste Summand läßt sich auf einen vom Stabilisator bewirkten Kettenabbruch durch Reaktion mit Peroxyradikalen unter Wasserstoffabstraktion von AH zurückführen. Der zweite Summand bringt die direkte Oxidation des Stabilisators zum Ausdruck, die wahrscheinlich zur Bildung freier Radikale führt. Diese Reaktion ist vom Sauerstoffdruck po2 abhängig, sie wird bei Verwendung von 2,2′‐Methylen‐bis(4‐methyl‐6‐tert‐butyl‐phenol) praktisch nicht beobachtet. Das von der Netzwerkstruktur abhängige Glied c trägt nur unwesentlich zu VOX bei.
Synthese von Cellulose‐Austauschern mit chelatbildenden funktionellen Gruppen
Authors: Burba P. , Lieser K. H.
Published: April 2003

Eine neue, breit anwendbare Methode zur Darstellung von Celluloseaustauschern wird beschrieben. Bei der Synthese wird das Reaktionsprinzip der Reaktivfarbstoffe „Remazol”︁® (WZ der Hoechst AG) in veränderter Form zugrunde gelegt. Die Synthese gelingt in zwei Varianten. Nach Variante A lassen sich funktionelle Gruppen direkt an Cellulose binden, nach B werden sie durch Diazo‐Kupplung gebunden.
Bestimmung von Polyäthylen in vernetzten Mischungen aus 1,4‐Polybutadien und Polyäthylen mittels Olefin‐Metathese
Authors: Hummel Klaus , Raithofer Gabriele
Published: April 2003

Mischungen aus 1,4‐Polybutadien und Polyäthylen wurden mit Dicumylperoxid vernetzt. Die Produkte wurden durch Olefin‐Metathese mit 2‐Octen und WCl6/C2H5AlCl2 als Katalysator abgebaut. Das zurückbleibende Polyäthylen wurde bestimmt.
Über die Struktur und einige Eigenschaften von mit Tetrachlorchinon plastifiziertem Polystyrol
Authors: Damjanov S. S. , Kartalov P. S. , Damjanov N. S. , Polisov Ch. T.
Published: April 2003

Es wurde der Plastifizierungsmechanismus von Tetrachlorchinon (TCC) in amorphem Polystyrol (PS) untersucht. Die experimentellen Ergebnisse zeigen, daß dieser interstrukturell ist. Die Glastemperatur des Systems PS/TCC wird bis zu 5 Gew.‐% TCC schroff herabgesetzt, danach nimmt sie nur noch schwach ab, und über 10% TCC hinaus bleibt sie konstant. Die Newtonsche Viskosität η0 nimmt kontinuierlich mit Erhöhung der TCC‐Konzentration im PS ab. Es wurden alle charakteristischen übergänge im PS von 20 bis 200°C auf den Thermo‐Depolarisationsstromogrammen der untersuchten Proben erhalten. Daraus ersieht man, daß die Glastemperatur bis 10% TCC abnimmt, der α‐Übergang zu den niedrigeren Temperaturen verschoben wird und das Temperaturintervall des hochelastischen Zustands vermindert wird. Die röntgenographischen Untersuchungen zeigen, daß infolge der Plastifizierung die Anordnung der Übermolekulargebilde im PS herabgesetzt wird. Die elektronenmikroskopischen Aufnahmen deuten auf die Anwesenheit einer Übermolekularstruktur in dem plastifizierten Polystyrol hin. Die Übermolekularelemente und die Abstände zwischen ihnen nehmen mit Erhöhung der TCC‐Konzentration zu.
Struktur und Eigenschaften von ABS‐Polymeren. XII. Oxydativer Abbau von Polybutadien‐Pfropfpolymeren aus ABS; Vergleich verschiedener Abbaumethoden
Authors: Kranz Dietmar , Dinges Karl , Wendling Peter
Published: April 2003

Zur Charakterisierung von Pfropfpolymerisation auf der Basis von Polybutadien wird eine Abbaumethode beschrieben, bei der zunächst die Pfropfgrundlage einem schonenden Abbau mit tert‐Butylhydroperoxid (t‐BHPO) und OsO4 bei 110°C (30 min) unterworfen und anschließend ein Nachabbau mit Perjodsäure bei Raumtemperatur durchgeführt wird. Als Lösungsmittel dient p‐Dichlorbenzol. Diese Abbaumethode wird mit dem KMnO4‐Abbau und dem Abbau mit t‐BHPO und OsO4 in Toluol und Benzol bei variierten Temperaturen und Zeiten verglichen. Aus den vergleichenden Abbauversuchen an Pfropfpolymerisation und an Styrol‐Acrylnitril‐Copolymerisaten ergibt sich, daß die beschriebene Abbaumethode einen vollständigen Abbau des Polybutadiens bewirkt, ohne daß die Pfropfketten aus Styrol‐Acrylnitril‐Copolymeren selbst angegriffen werden.
Studies in the syntheses, reactivities and polymerization of 4‐ and 2‐isocyanato diphenyl ethers
Authors: Ghatge N. D. , Shinde B. M.
Published: April 2003

The paper describes the syntheses and reactivities of 4‐ and 2‐isocyanato diphenyl ethers. These compounds were polymerized by means of acidic catalysts to form polyamide polymers.
Der Einfluß von niedermolekularen Adsorptiven auf die Adsorption von Polyestern an Aerosiloberflächen
Authors: Dietz Erwin , Hamann Karl
Published: April 2003

In der vorliegenden Arbeit wird der Einfluß von polaren Additiven auf eine Adsorptionsschicht von Polyäthylensuccinat an Aerosil untersucht. Von den untersuchten Additiven besitzt Nitrobenzol den geringsten Einfluß auf die Polyesteradsorptionsschicht. Acetonitril, Dimethoxyäthan, DMF, Phenol und D2O reduzieren sowohl die adsorbierte Menge als auch die Zahl der an die Aerosiloberfläche gebundenen Carbonylgruppen in mehr oder weniger großem Ausmaß, ohne bei einer Additiv‐Konzentration von 0,8 mol/l eine vollständige Desorption des Polyesters zu erreichen. Polyäthylenoxid (M̄n = 400), n‐Butanol und Pyridin verdrängen den Polyester bei einer Additiv‐Konzentration von 0,8 mol/l nahezu vollständig von der Aerosiloberfläche.
Formation of polyurethane networks based on poly(propylene glycol) and 4,4′‐diphenylmethane diisocyanate
Authors: Nesterov A. E. , Lipatova T. E. , Dušek K. , Pelzbauer Z. , Houska M. , Hradil J. , Lipatov Yu. S.
Published: April 2003

The formation of a polyurethane network from poly(propylene glycol) terminated with 4,4′‐diphenylmethane diisocyanate and from 1,1,1‐trimethylolpropane was investigated by light scattering and electron microscopy. The results indicate that the nonhomogeneities are formed in the system and that their size increases with increasing conversion up to gel point. The formation of nonhomogeneities is explained by strong intermolecular interactions with the participation of urethane groups; the existence of such interactions was confirmed on model systems by using inverse gas chromatography. An addition of dimethylformamide to the reaction mixture accelerates the reaction and suppresses nonhomogeneities.
Zur chemie des lignins
Authors: Müller Olav
Published: April 2003

„Brauns”︁‐Lignin liefert in 74,9proz. Schwefelsäure eine Hydrolysen‐Kurve, die nicht die am nativen Lignin nachgewiesenen Abspaltungs‐ und Anlagerungsvorgänge von Wasser erkennen läßt; es kann also nicht identisch mit der nativen Form des Lignins sein. „Brauns”︁‐Lignin enthält eine Zuckerkomponente, die kein wasserunlösliches Saccharid ist.

Buchenschwefelsäurelignin läßt beim Kaltpressen unter hohem Druck ein plastisches Fließen erkennen und hat danach eine Dichte von 1,24 bis 1,28 g/cm3. — Versucht man, Buchenschwefelsäurelignin in eine Caprolactamschmelze einzupolymerisieren, so erhält man eine hellbraune, metallisch glänzende Masse. Aber bereits bei Ligninmengen von weniger als 1% ist das Abspinnvermögen stark beeinträchtigt. Offenbar ist das dreidimensionale Ligninmolekül so starr, daß es die lineare Ausrichtung des Polymerisates und damit die Fadenbildung stört.

Es gelingt, Fichtenschwefelsäurelignin in wäßriger, schwach essigsaurer Suspension mittels Natriumchlorit in eine hochgequollene, transparente, orangefarbene Masse zu verwandeln. — Der weitere oxidative Abbau mit einem Gemisch von Wasserstoffperoxid, Essigsäureanhydrid und Eisessig führt zu sauren Produkten, deren weitere Trennung über ihre Bleisalze mit unterschiedlichen Löslichkeiten gelingt, und die auch als freie Säuren teilweise kristallisieren. Für eine dieser Fraktionen, welche die Hauptmenge bildet, wird eine Strukturformel zur Diskussion gestellt.
Initial synthesis and thermal characterization of hafnium polyethers
Authors: Carraher Charles E. , Jambaya Leonard M.
Published: April 2003

Hafnium polyethers were synthesized utilizing both the interfacial and aqueous solution techniques:
magnified image

Thermal properteis of the polyethers were studied by DSC and TGA analysis. The products exhibit moderate to poor low and high temperature stabilities. Degradation above 200°C occurs via an oxidative mode in air.
Determination of monomer reactivity ratios in copolymerizations with N‐vinylpyrrolidone by means of high‐speed liquid chromatography
Authors: Narita Hiroshi , Hoshii Yasuhiro , Machida Seishi
Published: April 2003

High‐speed liquid chromatography was applied to the studies of the polymerization of N‐vinylpyrrolidone and its copolymerizations with vinyl acetate, glycidyl methacrylate and methyl methacrylate. The conversion was calculated from the decrease in peak‐height in the chromatogram of the monomer. A small change in the amount of monomer was closely determined by using o‐diphenyl benzene (o‐terphenyl) as an internal standard. The calculations of the monomer reactivity ratios gave concordant results with those reported earlier. The obtained copolymer compositions agreed with the data by elementary analysis.

The application of high‐speed liquid chromatography to the determination of copolymerization reactivity ratios was thus found to be advantageous for saving time. The monomer reactivity ratio can be determined without the complicated processings such as separating, drying and analysing the copolymers.
Vinyl polymerization by metal complexes, 28. Polymerization of acrylonitrile initiated by copper(II) chelates of vinylamine‐vinylacetamide copolymers in dimethyl sulfoxide solution
Authors: Kimura Keiichi , Hanabusa Kenji , Inaki Yoshiaki , Takemoto Kiichi
Published: April 2003

The polymerization of acrylonitrile initiated by copper(II) chelates of polyvinylamine, polyvinylacetamide and vinylamine‐vinylacetamide copolymers was studied in dimethyl sulfoxide solution. The copper(II) chelates of vinylamine‐vinylacetamide copolymers were found to initiate the polymerization of acrylonitrile effectively, even in the absence of carbon tetrachloride, while those of polyvinylamine and polyvinylacetamide initiate only in the presence of carbon tetrachloride. The polymerization activity was assumed to be closely related to the stability of these copolymer‐copper(II) chelates. From the results of the polymerization and the visible spectroscopy, an initiation mechanism is discussed.
N‐formylacrylamid, ein neues Monomeres der Acrylatreihe. II. Polymere mit kovalent gebundenen Farbstoffgruppierungen
Authors: Trathnigg Bernd , Junek Hans
Published: April 2003

Gefärbte Polymere werden erhaiten durch Copolymerisation von Styrol mit N‐(2,4‐Dinitrophenylhydrazono‐methylen)‐acrylsäureamid (2), das durch Kondensation von N‐Formylacrylamid (1) mit 2,4‐Dinitrophenylhydrazin dargestellt werden kann, sowie durch Umsetzung von Copolymerisaten des N‐Formylacrylamids mit 1,4‐Diaminoanthrachinon und 4‐Aminoazobenzol. Die Produkte enthalten die Farbstoffe in kovalenter Bindung, wie durch Gelchromatographie gezeigt werden kann.
Darstellung von Polyamidsulfonsäuren auf der Basis von Toluol und Schwefelsäure
Authors: Sass Otto‐E. , Vollmert Bruno
Published: April 2003

Die Synthese eines neuen Monomeren auf der Basis von Toluol und Schwefelsäure wird beschrieben:
magnified image

Durch Reaktion mit aromatischen Diaminen, z. B. Benzidin, 4,4′‐Diaminodiphenyläther und 4,4′‐Diaminodiphenylsulfon in polaren Lösungsmitteln (DMA, N‐Methylpyrrolidon, Nitrobenzol/Pyridin) unter Wasserausschluß entstehen bei normaler Temperatur (0–20°C) Polyamidsulfonsäuren mit Molekulargewichten um M̄w ≈ 20 000. Aus den Lösungen lassen sich bei 150 bis 180°C im Vakuum feste und zähe, klar‐transparente Filme herstellen, die ‐ auch bei 150°C im Vakuum ‐ erhebliche Mengen an Lösungsmittel (um 40%) festhalten.
Die „Inverse Gaschromatographie”︁ zur Charakterisierung von Polymeren, Polymergemischen und Copolymeren I. Zur Charakterisierung synthetischer Polymerer durch Retentionsindices
Authors: Klein Joachim , Widdecke Hartmut
Published: April 2003

Die Bestimmung von Retentionsindices ist im Vergleich zu absoluten gaschromatographischen Retentionsdaten bei geringerem apparativen aufwand einfacher und genauer durchzuführen. Am Beispiel von Polystyrol, Polyvinylacetat und Polyäthylenoxid als stationärer Phase werden Die Retentionsindices von Benzol, Äthanol, Methyläthylketon, Nitromethan und Pyridin bestimmt und Die Aussagekraft der Indices im Rahmen der “Inversen Gaschromatographie” diskutiert. Das Wechselwirkungsverhalten zwischen mobiler und stationärer Phase und damit Die Retention ist in der Regel durch eine Überlagerung verschiedener Sorptionsmechanismen bestimmt. Zu berücksichtigen sind dabei Die Adsorptionen an den Gas/Träger‐, Gas/Polymer‐, Polymer/Träger‐und Polymer/Polymer‐Grenzflächen sowie Die Absorption im Polymeren (Lösung). Es wird gezeigt, daß durch ein unterschiedliches Sorptionsverhalten der polaren Testsubstanzen und der n‐Alkane an der Polymeroberfläche beispielsweise systematische Abhängigkeiten der Indices von der Belegungsmenge auftreten müssen.

Wird das Polymere bei Temperaturen oberhalb des Schmelzpunktes bzw. der Glastemperatur vermessen und werden hohe Beladungsmengen und möglichst inerte Trägermaterialien verwendet, so ist der Index vorwiegend durch Die Wechselwirkung der gelösten Substanz mit der flüssigen Polymerphase bestimmt. Eine Charakterisierung der Polymeren ist dann z. B. unter Verwendung von Testsubstanzen möglich, Die entsprechend ihrer funktionellen Gruppe für bestimmte Weschselwirkungskräfte typisch sind. Die von Rohrschneider vorgeschlagene Methode zur Charakterisierung stationärer Phasen wird in diesem Zusammenhang untersucht.
Ellipsometrische Untersuchung der Adsorption von Polystyrol und Polymethylmethacrylat an Metalloberflächen
Authors: Gebhard Hans , Killmann Erwin
Published: April 2003

Es wird das Adsorptionsverhalten von Polystyrol und Polymethylmethacrylat aus verschiedenen Lösungsmitteln an hochvakuumbedampften Chrom‐, Platin‐ und Goldspiegeln unter Variation des Molekulargewichtes der Polymeren mit Hilfe der Ellipsometrie untersucht.

Für beide Polymere steigen die Dicken und Mengen mit zunehmender Lösungskonzentration an. Die Konzentration des adsorbierten PS‐Filmes fällt mit der Lösungskonzentration ab. Die Filmkonzentration beim PMMA steigt mit der Lösungskonzentration an. Moleküle mit hohem Polymerisationsgrad liefern größere Schichtdicken und adsorbierte Mengen als Moleküle mit niedrigem Polymerisationsgrad. Mit zunehmender Polarität des Adsorbens wird eine Zunahme der Dicke und Menge der adsorbierten Schicht sowie eine Abnahme der Filmkonzentration gefunden. Für steigende Lösungsmittelpolarität ergibt sich eine Abnahme von Dicke und Menge der Adsorptionsschicht, sowie eine Zunahme der Filmkonzentration. In der Sättigung adsorbieren die PS‐Moleküle in Form statistischer Knäuel. Für das polare PMMA wird infolge starker Segmentwechselwirkungen ein abweichendes Adsorptionsverhalten festgestellt.
The analysis of phenol‐, resorcinol‐ and phenol/resorcinol‐formaldehyde resins by catalytic thermometric titrimetry. Part II. Resoles
Authors: Greenhow Edward Joshua , Shafi Abid Akhter
Published: April 2003

Catalytic thermometric titration is used for the determination of the phenol and resorcinol components of resins formed by the sodium hydroxide‐ and ammonia‐catalysed condensations of phenol, resorcinol and mixtures of phenol and resorcinol, with formaldehyde.
Polykondensationsgleichgewicht bei polylaurinlactam
Authors: Feldmann R. , Feinauer R.
Published: April 2003

Durch Aufschmelzen von ungeregelten Polylaurinlactamproben unterschiedlicher Ausgangslösungsviskosität bei 320, 300, 280 und 260°C wurde die Veränderung der Lösungsviskosität in Abhängigkeit vom vorgegebenen Wassergehalt untersucht. Die bei gleichbleibender Lösungsviskosität vor und nach dem Aufschmelzen erhaltenen Gleichgewichtswerte wurden zur Bestimmung der Gleichgewichtswerte für das System Polylaurinlactam/Wasser herangezogen.

Aus den Gleichgewichtskonstanten wurden mit den bekannten Beziehungen zwischen Umsatz, Molekulargewicht und relativer Lösungsviskosität die Gleichgewichtswasserwerte bei verschiedenen Temperaturen für ungeregeltes und für unterschiedlich geregeltes (Menge, Funktionalität) Polylaurinlactam berechnet.
Mechanismus der stabilisierung aromatischer polyamide gegen UV‐licht
Authors: Werner Tilmann , Kramer Horst E. A. , Küster Bernhard , Herlinger Heinz
Published: April 2003

Der Mechanismus der UV‐Stabilisierung stark absorbierender Kunststoffe wird am Beispiel Poly‐(m‐phenylen‐isophthalamid) untersucht; die Wirksamkeit von Energietransfer und Lichtfilterwirkung wird verglichen. Rückschlüsse auf Weg und Ausmaß der Stabilisatoranregung in festen Polyamidfilmen werden durch Messung der Lumineszenz des methylierten Stabilisators 2‐(2′‐Methoxy‐5′‐tert‐butyl‐phenyl)‐benzotriazol‐carbon‐säureanilid‐(5) gewonnen. Die Emission des Letzteren ist bei Anregung im Bereich zwischen 290 nm und 330 nm überwiegend sensibilisierte Phosphoreszenz, daraus wird auf erhebliche Bedeutung des Energietransfers geschlossen. Da sensibilisierte Fluoreszenz nicht gefunden wird, dürfte Triplett‐Triplett‐Transfer vorliegen.
Polycondensation kinetics. NMR study on the formation of furfurylalcohol‐formaldehyde resins
Authors: Boros‐Gyevi E. , Kajtár‐Peredy M. , Várhegyi G. , Hemela J.
Published: April 2003

The polycondensation reaction of furfurylalcohol‐formaldehyde catalyzed by phosphorous acid was studied by NMR. The concentration of the different end‐groups in the reaction mixture and its change with reaction time have been determined. The differential equation system describing the rate of elementary steps of the reactions has been set up. Approximative values of the rate constants of elementary steps have been determined by numerical integration.
Cyclic oligomers produced by heating terephthalate polyesters in the source of a mass spectrometer
Authors: Gilland James C. , Lewis Jack S.
Published: April 2003

Mass spectrometry is not usually considered a satisfactory tool for examining polymers, since polymers usually decompose before vaporizing. However, if low molecular weight oligomers are present in the polymer or if they are formed under the conditions prevailing in the mass spectrometer, then mass spectrometry might be used to characterize these low molecular weight oligomers.

When poly(ethylene terephthalate) (PET) is heated in the source of a mass spectrometer, cyclic oligomers from the dimer through the hexamer are observed. Since the predominant solvent extractable oligomer present in PET is the cyclic trimer, a thorough investigation was made of its mass spectrum to determine the mechanism of ion fragmentation. The information from this investigation was used to identify the other cyclic oligomers produced. An attempt was made to determine the mechanism of formation of the cyclic oligomers by comparing spectra of extracted PET and PET with benzoate capped end groups, but the results were inconclusive because of the improbability of removing all hydroxyl ends.
Synthese von substituierten benzotriazolen zur stabilisierung aromatischer polyamide gegen UV‐licht
Authors: Küster Bernhard , Tschang Chung‐Ji , Herlinger Heinz
Published: April 2003

Zur Stabilisierung aromatischer Polyamide wurden 2‐(2′‐Hydroxyphenyl)‐benzotriazole synthetisiert, die in 5‐ bzw. 5′‐Stellung als Substituenten eine Carbonamidgruppe aufweisen. Der Einfluß der ortho‐ständigen Hydroxylgruppe auf die stabilisierende Wirkung dieser Verbindungen wurde durch Methylierung derselben untersucht.

Die dargestellten Benzotriazole wurden charakterisiert, wobei auf UV‐spektroskopische Daten besonderer Wert gelegt wurde.

Durch Viskositätsmessungen wurde die photolytische Beständigkeit von Poly‐(m‐phenylenisophthalamid), die durch den Zusatz von gezielt synthetisierten Stabilisatoren, wie z. B. 2‐(2′‐Hydroxy‐5′‐tert‐butylphenyl)‐benzotriazolcarbonsäureanilid‐(5), wesentlich verbessert wird, untersucht.
Etude des propriétés viscoélastiques de quelques mélanges polybutène‐1 – polypropène
Authors: Piloz Alain , Decroix Jean‐Yves , May Jean‐François
Published: April 2003

Die viskoelastischen Eigenschaften von Mischungen aus Polybuten‐1 und Polypropen werden im β‐Relaxationsgebiet untersucht. Es gibt nur einen Relaxationspeak, und die Mischungen scheinen in der amorphen Phase verträglich zu sein. Diese Beobachtungen bestätigen die von uns bereits früher aufgestellten Hypothesen über den Einfluß der relativen Länge der Alkylgruppe in Polyolefinmischungen.
Reactions of poly(ethylene imine)with tin‐containing reactants
Authors: Carraher Charles E. , Feddersen Mary F.
Published: April 2003

Modification of poly(ethylene imine) with tin‐containing reactants was effected utilizing the interfacial technique. Products from dihalo reactants are crosslinked while products from monohalo reactants are linear and soluble containing from about 30 to 90% inclusion of the tin‐moiety. Yield maximized about one minute stirring time and decreases at higher stirring times because of heat buildup.
Reaktive polymere. V. Metallkomplexe polymergebundener schiffscher basen
Authors: Kálalová Eliška , Kálal Jaroslav , Švec František
Published: April 2003

Es wurden Komplexe des zweiwertigen Kupfers und des zweiwertigen Kobalts mit Salicylidenäthylendiaminliganden, die an Glycidylmethacrylat‐Äthylendimethacrylat‐Copolymere gebunden sind, synthetisiert und gemäß den IR Spektren charakterisiert. Es wurde auch die Möglichkeit der Sauerstoffübertragung durch den Kobalt(II)‐Komplex verfolgt.
Modifications superficielles de films de polyéthylène par divers traitements chimiques
Authors: Sage Daniel , Berticat Philippe , Vallet Georges
Published: April 2003

Des traitements chimiques tels que l'halogénation, l'oxydation, la chlorophosphorylation ont été effectués pour modifier l'énergie de surface de films de polyéthylène. Ces traitements sont relativement simples et rapides à réaliser. Les réactions ont été suivies par spectroscopie infrarouge A.T.R. Des mesures de tension superficielle permettent de comparer ces différents traitements.
Etude par chromatographie liquide haute pression de polyoléfines et de polyéthylènes modifiés
Authors: Sage Daniel , Berticat Philippe , Collet Gérard , Rocca Jean‐Louis
Published: April 2003

Le comportement en chromatographie en phase liquide haute pression de polyoléfines de cristallinités différentes et avec des ramifications variables (polyéthylène haute et basse densité, copolymère éthylène‐propylène, polypentène) et de polyéthylènes modifiés soit dans la masse (chloration) soit en surface (chloration, chlorophosphorylation, oxydation) a été étudié. Les échantillons sont constitués de billes de verre de 44–50 μm enrobées de polymère. L'étude a été réalisée d'une part en phase mobile apolaire (cyclohexane) avec phénol, ortho‐, méta‐ et paranitrophénol comme solutés, d'autre part en phase mobile polaire (mélanges eau‐méthanol) avec benzène, chlorobenzène et orthodichlorobenzène comme solutés. L'influence d'un agent gonflant du polymère et l'effet de la température ont été considéres. Les résultats obtenus montrent l'intérět de la chromatographie liquide pour étudier les interactions entre un polymère et un couple solvant‐soluté donné.
Kinetik der polykondensation von niedermolekularem polyäthylenterephthalat
Authors: Lasarova R. , Dimov K.
Published: April 2003

Es wurde eine kinetische Untersuchung über die Polykondensation von niedermolekularem Polyäthylenterephthalat in Anwesenheit des Katalysator‐Inhibitor‐Systems Mn(OAc)2‐Triphenylphosphat‐Sb2O3 durchgeführt. Festgestellt wurde, daß für niedrige Konzentrationen des Katalysators bis zu 2,5 · 10−4 mol/mol Monomeres die Polykondensation bei den vier untersuchten Temperaturen 270, 280, 285 und 290°C als Reaktion zweiter Ordnung verläuft. für Konzentrationen von 3,0 und 3,5·10−4 mol/mol bei 285 und 290°C ändert sich die Reaktionsordnung infolge von Abbauprozessen. Die Geschwindigkeitskonstanten erhalten praktisch bedeutende Werte bei 280°C für Katalysatorkonzentrationen von 3,0 und 3,5 · 10−4 mol/mol sowie bei 285 und 290°C und Katalysatorkonzentrationen von 2,0 und 2,5 · 10−4 mol/mol.
Studies on syntheses and permeabilities of special polymer membranes. I. Concentration of aqueous polymer solutions using porous cellulose acetate membranes
Authors: Uragami Tadashi , Fujino Kozo , Sugihara Mizuho
Published: April 2003

The membrane performance of aqueous polymer solutions using porous cellulose acetate membranes is investigated by changing the membrane preparation methods and the permeation conditions. It is found that the rate of water permeability decreases with an increase in the evaporation period using pure water as feed, but the permeation rate is almost constant regardless of the evaporation period using 1.0% aqueous solution of poly(vinyl alcohol) as feed. This phenomenon is attributable to the concentration polarization of poly(vinyl alcohol) molecules onto the membrane surface. The membrane performance is improved by adding some additives to the casting solutions and by treating with certain solutions. The permeation rate decreases with an increase in the feed concentration at a given operating pressure but the solute separation is always 100%, regardless of the feed concentration in the range of 0.5 to 5.0% aqueous solution of the membrane compaction and poly(vinyl alcohol). These phenomena are explained on the basic of the osmotic pressure, the feed viscosity, and the concentration polarization. The permeation rate is constant regardless of the operating pressure. This result is discussed on the basis of the concentration polarization. From comparing the permeation characteristics of aqueous solutions of poly(vinyl alcohol) and poly(ethylene glycol), it is seen that there are differences of the form of polymer molecules in solution and complex interactions between polymer molecules and membrane substrate. The behaviour of polymer solutes and membranes during the concentration of aqueous solutions of polymers is discussed.
Studies on syntheses and permeabilities of special polymer membranes. II. Permeation characteristics of cellulose nitrate membranes
Authors: Uragami Tadashi , Tamura Masahiro , Sugihara Mizuho
Published: April 2003

For the purpose of application in artificial kidneys the permeation characteristics of semipermeable membranes obtained from a system of cellulose nitrate/methyl alcohol/1,4‐dioxane/barium perchlorate were investigated under various conditions. The optimum composition of the casting solution was found to be the proportion cellulose nitrate: methyl alcohol: 1,4‐dioxane as 13:45:42 (wt.‐%). It was found that the permeation rate was influenced by the evaporation period, the maximum permeability lay at 30s. The addition of barium perchlorate to the casting solution increased the permeation rate, especially if more than 60 wt.‐% of barium perchlorate per cellulose nitrate was used. The permeation rate is increasing with the operating pressure, but decreasing with the feed concentration. When several samples of poly(ethylene glycol) having different average molecular weights were used as feed solute, the permeation rate decreased with an increase in average molecular weight. The permeation fraction was 100% in systems of poly(ethylene glycol) with mol. wt. from 200 to 4000 and was 0% in systems of poly(ethylene glycol) 6000 under 200 mm Hg. In blood filtrations the permeation rate of cellulose nitrate membranes had about four‐fold values of cuprophane membranes, and moreover no protein was found in the blood filtrate.
Unstaurated polyester imides
Authors: Maros Catherina L. , de Abajo Javier
Published: April 2003

Imide‐containing polyesters have been prepared by melt polycondensation of propylene glycol with saturated and/or unsaturated diacids and imide diacids. These imide diacids have been synthesized from trimellitic anhydride and aliphatic ω‐amino acids, and differ from each other in the number of CH2groups.

When mixtures of styrene and the unsaturated polyester imides are activated by peroxidic type initiators, crosslinked products are obtained, the properties of which can be related to the proportion of imide rings and the length of the aliphatic chain in its chemical structure.
Polyanhydride‐imides
Authors: González J. Ignacio , de Abajo Javier , González‐Babé Santiago , Fontán José
Published: April 2003

Eight imide‐diacids were synthesized from trimellitic anhydride, pyromellitic anhydride and aminoacids of the formula HOOC(CH2)nNH2, with n = 1,2,3,5. From them, polyanhydride‐imides were obtained following a general method of formation of polyanhydrides in the presence of acetic anhydride1,2.

These co‐polyimides have an aliphatic‐aromatic structure and the relation between the general properties and the amount of the aliphatic part in the repeat unit was studied. IR spectroscopy, elemental analysis and viscosity measurements were used for the characterization. Studies of solubility, hydrolysis resistance and thermal properties were also made.
Etude des propriétés rhéologiques de quelques mélanges polybutène‐1‐polypropène à l'état fondu
Authors: Deri Fawaz , Piloz Alain , May Jean‐François
Published: April 2003

L'examen du comportement rhéologique à l'état fondu de mélanges à base de polybutène‐1 et de polypropène a été effectué en fonction de la température, de la contrainte de cisaillement et de la vitesse de cisaillement. Les courbes de variations de la viscosité apparente en fonction de la composition présentent un minimum qui correspond approximativement à un maximum des courbes de variation du facteur de Barus. Ces résultats semblent montrer que le domaine de faible viscosité soit associé à un domaine de forte élasticité pour les matériaux viscoélastiques examinés.
Determination of cohesive energy densities of 2‐hydroxyethylmethacrylate and methylacrylate copolymers from swelling measurements
Authors: Varma I. K. , Patnaik S.
Published: April 2003

The cohesive energy densities (c.e.d.) of copolymers having varying compositions of 2‐hydroxyethylmethacrylate (HEMA) and methylacrylate (MA) were determined from swelling measurements. It was found that the c.e.d. decreases as the 2‐hydroxyethylmethacrylate content increases in the copolymer.