Effect of various surface coating methods on surface roughness, micromorphological analysis and fluoride release from contemporary glass ionomer restorations
Authors: Alebady Mohanad H. , Hamama Hamdi H. , Mahmoud Salah H. 
Published: April 2024

Objective

To evaluate the effect of various surface coating methods on surface roughness, micromorphological analysis and fluoride release from contemporary resin-modified and conventional glass ionomer restorations.

Materials & methods

A total of 72 permanent human molars were used in this study. The teeth were randomly assigned into 2 groups according to type of restorative materials used; resin modified glass ionomer cement and conventional glass ionomer (SDI Limited. Bayswater Victoria, Australia). Each group was subdivided into 3 subgroups according to the application of coat material; Sub-group1: without application of coat; Sub-group2: manufacturer recommended coat was applied and sub-group3: customized (vaseline) coat was applied. Each group was then subdivided into two divisions according to the time of testing; immediate (after 24 h) and delayed (after 6 months of storage). Three specimens from each sub-group were selected for surface roughness test (AFM) and another 3 specimens for the micromorphological analysis using scanning electron microscope (SEM). For the fluoride release test, a total of 60 cylindrical discs were used (n = 60). The discs were randomly split into 2 groups according to type of restorative materials used (n = 30); resin modified glass ionomer cement and conventional glass ionomer. Each group was subdivided into 3 subgroups (n = 10) according to the application of the coat material; Sub-group1: without application of coat; Sub-group2: with the manufacturer recommended coat and sub-group3: with application of customized (vaseline) coat. Data for each test was then collected, tabulated, were collected, tabulated, and tested for the normality with Shapiro-Wilk test. Based on the outcome of normality test, the significant effects of variables were assessed using appropriate statistical analysis testing methods.

Results

Regarding the data obtained from surface roughness test, Shapiro-Wilk test showed normal distribution pattern of all values (p > 0.05). Accordingly, Two-way ANOVA outcome showed that the ‘type of restoration’ or ‘test time’ had statistically significant effect on the AFM test (p < 0.05). Regarding Fluoride specific ion electrode test 2-way ANOVA followed by Least Significant Difference (LSD) Post-hoc test revealed significant difference among the groups (p < 0.05). It showed that SDI GIC group after 14 days of measurement had the highest mean of fluoride release (36.38 ± 3.16 PPM) and SDI RMGIC after 30 days of measurement had the second highest mean of fluoride release (43.28 ± 1.89 PPM). Finally, regarding the micromorphological analysis using SEM, a slight difference was observed between the studied groups.

Conclusions

Based on the results of this study, various coatings enhance surface roughness in the initial 24 h of restoration insertion. Different coat types seems that have no influence on fluoride release and the micromorphological features of the restoration/dentin interface.