Time Lapse Visualization of Catalyst Ink Degradation by X-ray CT
Authors: Uemura Suguru , Kameya Yuki , Iriguchi Norio , Yoshida Toshihiko , Hirai Shuichiro 
Published: February 2020

The catalyst layer (CL) is one of critical component for determining the performance of proton exchange membrane fuel cells (PEMFCs), and the production process of CL is important issue. In order to form the CL, catalyst ink mixed with platinum-supported carbon (Pt/C), ionomer solution, and a solvent is necessary. When the catalyst ink is coated on the sheet and dried, the CL is formed. By transferring the catalyst layer to the membrane, catalyst coated membrane can be made [1]. The process from the initial characteristics of the catalyst ink to the drying process determines the structure of CL and dominates the characteristics of the fuel cell. Thus, quality control of the catalyst ink is important to form a high performance and uniform CL [2], but it is difficult to observe how the characteristics of the catalyst ink change with time from the appearance. In this study, time lapse visualization of inside the catalyst ink was performed by X-ray CT.

Catalyst ink was prepared by using the mixture of water and NPA as a dispersant. We used platinum catalyst supported on carbon black and Nafion dispersion D2020 (Chemours). Pre-mixing of catalyst ink was performed using ultrasonicaton to break large Pt/C agglomerates into smaller units. As a main mixing process, a high-speed rotary type mixer Filmix (Primix) utilizing shearing force, specialized for producing nanometer slurry was used. The prepared ink was immediately transferred to a glass sample container and sealed tightly. Thereafter, it was placed in the X-ray CT (Shimadzu) immediately and time lapse three-dimensional visualization was performed.

Figure 1 shows sliced image of catalyst ink. The contrast of the image corresponds to the amount of absorption of X-rays, and it is possible to determine the state of the substance. In the black region, X-rays are easy to transmit, which is a light substance. In the initial state, micro to millimeter scale bubbles (several black dots) were dispersed, however, the other part was uniform light gray, which shows that the catalyst ink was homogeneously mixed.

On the other hand, drastic state change inside the catalyst ink with the passage of time was observed. It was found that the volume of bubbles increased with the passage of time. Different color regions (dark gray) were also emerged between the bubbles. Changes with time of the volume of the homogeneous part of the ink, bubbles, and the emerged phase are shown in the graph (Figure 2).

Observed changes in the catalyst ink are thought to be due to alcohol decomposition by the catalyst. For comparison, pseudo catalyst ink using carbon black not carrying platinum was visualized, but no change was observed. Analysis of the gas phase in the upper part of the glass sample container showed that the CO2 concentration was increased. From these results, NPA was decomposed by the platinum catalyst, and it is considered that generation of gas and formation of different liquid components were occurred. These experimental results suggest the importance of management of catalyst ink preparation, storage, and coating processes.

Acknowledgment:

This study is based on the results obtained from a project commissioned by the New Energy and Industrial Technology Development Organization (NEDO).

 

References:

H.J. Cho et al., Int. J. Hydrogen Energy 36 (2011) 12465.

S.J. Shin et al., J. Power Source 106 (2002) 146-152.

Figure 1