bluuebunny/crossref_metadata_2025 huggingface dataset:
Modes of inhibiting electrode processes (corrosion included) and their experimental discrimination II. Methodology for the investigation of the different modes of inhibition
Authors: Fischer Hellmuth
Published: December 2004

In the field of inhibiting electrode reactions three methodological aims are to be underlined: 1. to identify inhibition and its modes, 2. to determine the effects of inhibition and 3. to investigate the causes of inhibition.

This work is involving one of the tasks of the Working Party “Inhibitors” of the European Federation of Corrosion.

Physical, chemical and electrochemical methods are used or proposed for these three tasks regarding the interface‐inhibition. For these both modes of inhibition, primary and secondary inhibition are to be distinguished. In the case of electro‐lyte‐layer inhibition, separation of the species mechanical and electrochemical electrolyte layer inhibition is necessary.

As examples of inhibition in applied electrochemistry corrosion inhibition and inhibition in electrocrystallization of metals are treated. As to corrosion inhibition, ultimately, all investigation methods are to be related to the electrode reaction taking place without external electrical field, i.e. at the corrosion potential and the corrosion current density. In corrosion protection, investigation methods should examine especially the completeness of interface‐inhibition, membrane inhibition, passivation and the cooperation of electrolyte‐layer inhibition. On the other hand, for inhibition of the electrocrystallization of metals, the degree of coverage obtained by membrane inhibition or passivation would be too high. The investigation methods must be adapted to a moderate interface inhibition only at certain active sites of the surface. Highly sensitive morphological inhibition which has to be studied by special methods is belonging to the peculiarities of the inhibition in electrocrystallization.
Inhibition der Korrosion 15 (1) Über die Wirkungsweise von Korrosionsinhibitoren des Eisens in Säuren sowie in NaCl‐Lösungen bei Gegenwart von Sauerstoffen
Authors: Horner L.
Published: December 2004

Verf. gibt eine Übersicht von elektrochemischen und nichtelektrochemischen Methoden, die zur Untersuchung des Mechanismus der Korrosionsinhibierung verwendet werden können. Zu den nichtelektrochemischen Methoden gehören UV‐ und IR‐Reflexionsspektroskopie, die Auslöschung von Fluoreszenz durch Amine, die Ellipsometrie, die Elektronenmikroskopie und Röntgenmethoden. Zu den chemischen Methoden gehören die direkte Analyse schützenden Deckschichten, die Analyse mit der Elektronenmikrosonde und die Warburg‐Methode. Bezüglich der Inhibierungsmechanismen werden Beispiele angegeben, welche den Einfluß von Strukturparameter, die Bedeutung der Bindungszustände in der Elektronenbindung und den Einfluß von Reaktionen zeigen, bei welchem Produkte entstehen, die als Sekundärinhibitoren auftreten können (im diesem Zusammenhang werden besonders Oniumverbindungen und Sulfoxide behandelt). Schließlich werden Angaben gebracht über die Inhibitorwirkung einiger technischer oberflächenaktiver Substanzen, sowie von Glycin‐ und Sarcosinderivaten, aromatischen Carboxylsäuren und aromatischen Phosphonsäuren.
Corrosion Inhibitors for Aluminium Alloys
Authors: Desai M. N.
Published: December 2004

Data (including literature data) are presented on the inhibition of the corrosion of Al and some Al alloys in hydrochloride, sulfuric, acetic and oxalic acids and sodium hydroxides. In this context the influence is shown of parameters such as inhibitors structure and concentration, temperature, time, medium concentration and external currents. Inhibitors dealt with include aliphatic and aromatic amines, carbonyl compounds (aldehydes, ketones); in this context it is shown that functional groups and their relative positions may have an important effect on inhibitor efficiencies.
Effect of grid cast structure on the anodic corrosion of lead
Authors: Feliu S. , Galán L. , González J. A.
Published: December 2004

The influence of cast structure on the magnitude of the anodic attack has been studied for six lead base materials.

A comparison of the losses of weight of series of grid samples corresponding to the testing of two well differentiated cast structures for each material (a “coarse” structure and a “fine” one) shows that there is often a significant influence of the structure on the corrosion. The direction of the effect depends on the type of alloy tested. In some cases the “coarse” structure motivates a higher attack than the “fine” structure; in other cases, the opposite effect is encountered.

Finally, a theoretical justification is given of the principal facts observed. This is chiefly based on an analysis of the possibilities of selective attack of the material and disintegration of structural units.
Über das korrosionsverhalten von stahlblechen, die mit verschiedenen Strahlmitteln entrostet und mit Zinkstaubanstrich versehen wurden
Authors: Grubitsch H. , Sammer R. , Willfurth L.
Published: December 2004

Stahlblech, mit verschiedenen Strahlmitteln entzundert, wurde mit Zn‐Staubanstrich aur das Korrosionsverhalten im Salzsprüh‐ und im Bewitterungs‐ versuch geprüft. Die mit Quarzsand, Schlacke und Korund gestrahlten Bleche erwiesen sich im Salzsprühversuch den mit Stahlsplitt behandelten Blechen über‐ legen, weil bei diesen die Rauhtiefe sehr groß ist. Bei der Freibewitterung ist hingegen Entzundern mit Korund am günstigsten. Anstriche sind grundsätzlich günstiger als Spritzüberzüge, deren geringere Haftung die Unterrostung erleichtert.
Influence of the Surface Microgeometry upon the Corrosion Effect. I. Electrochemical corrosion
Authors: Parlapanski M.
Published: December 2004

The surface roughness of a metal may be used as a criterion for the determination of the number and the size of microgeometric corrosion elements. It is then possible to asses the corrosion effect (in terms of corrosion current) of such a microgalvanic cell, disregarding the ohmic resistance which amounts just to some per cent of the total resistance (i.e. anodic and cathodic polarizability); for the sake of simplification, the microelements may be assumed to have an idealized shape consisting of parallel cylindrical protuberances and depressions. The calculated results are in reasonable agreement with the experimental data.
Einfluß der Oberflächenbehandlung nichtrostender Stähle auf deren chemische Beständigkeit insbesondere gegen Spannungsrißkorrosion
Authors: Risch K.
Published: December 2004

Die Beständigkeit nichtrostender austenitischer Stähle gegen Spannungsrißkorrosion ist stark abhängig von der Oberflächenvorbehandlung. Durch Schleifen mit grobkörnigem Material wird die Oberfläche stark anfällig für diese Korrosionsart. Die Anfälligkeit läßt sich durch anschließendes Beizen weitgehend beseitigen, doch muß dabei eine etwa 3 μm dicke Schicht abgetragen werden. Beim Schleifen wird zwar das Gefüge bis in eine Tiefe von 200 μm gestört, doch scheinen in der erwähnten Oberflächenzone ganz spezielle Verhältnisse vorzuliegen, die vor allem zu transkristalliner Spannungsrißkorrosion führen können.

Zur Prüfung auf Anfälligkeit für Spannungsrißkorrosion eignet sich — wenn die Anfälligkeit verschiedener Stäble verglichen werden soll — eine Lösung mit (%) 0,06 Essigsäure, 1 Acetaldehyd und 100 ppm C1‐lonen (als CuC12).

Lochfraß durch Mischsäure kann ebenfalls durch scharfes Beizen von geschliffenem Material weitgehend verhindert werden.
The influence of carbon particles on the corrosion of iron in a humid, sulphur dioxide‐containing atmosphere
Authors: Ericsson R. , Heimler B. , Vannerberg N.‐G.
Published: December 2004

Iron samples covered with a thin layer of activated carbon have been exposed to humid atmospheres at various relative humidities and with a various sulfur dioxide contents. Contrary to expectation the corrosion is initially faster at 55 and 65% relative humidity that at higher humidities. This phenomenon is attributed to adsorption of water vapour on activated charcoal, so that liquid films giving rise to corrosion can be formed at an earlier stage. After extended exposure, however, no accelerating effect can be attributed to the carbon particles.
Zum bakteriologischen Korrosionsprodukt vom Betoneisen im Untermeertunnel
Authors: Yamaguchi S. , Aoyama Y.
Published: December 2004

Auf der mit Stahl armierten Betonwand im neuen Untermertunnel entstand ein spezielles Eisensulfid, und zwar Greigit (Fe3S4 vom Spinelltyp) als Korrosionsprodukt von Stahl. Es bildete sich durch die Tätigkeit der sulfatreduzierenden Bakterien und einen Kolloidchemischen Vorgang. Die Bildung des Greigits im Untermeertunnel gehört zu den Dunkelreaktionen, die mit zweiwertigem Eisen ablaufen.
Spannungsrißkorrosion in α‐Messing in Abhängigkeit von der Anlaßtemperatur und ihr Zusammenhang mit anderen Größen ‐ Teil II
Authors: Wawra H.
Published: December 2004

Untersucht wird die Abhängigkeit der Spannungsrißkorrosion von der Anlaßtemperatur bei konstanter Belastung und konstanter Probenverformung in 0,1%iger Quecksilbernitratlösung. Der Ausgangszustand der untersuchten Metalle — Ms 58, Ms 72, Ms 80 — war 52,3% kaltgewalzt. Optimale Beständigkeit zeigen relativ stabile Gefügezustände (erholtes Gefüge nach Wärmebehandlung bei 280 °C, Primär rekristallisiertes Gefüge nach Wärmebehandlung bei etwa 380 °C und sekundär rekristallisierte Gefüge nach Wärmebehandlung ab etwa 755 °C). Instabile Vorstadien derartiger Gefüge zeigen Minima in der Lebensdauer. Die zweckmäßigste Wärmebehandlung muß aus den Lebensdauerkurven entnommen werden, die häufig wegen intermediärer Verfestigung und Entfestigung zwei Minima aufweisen.
Hitzebeständigkeit von Schweißverbindungen ferritischer Chromstähle
Authors: Pilouš V.
Published: December 2004

In Hinblick auf die Verwendbarkeit von Stählen für Temperaturen bis 1000 °C wurden verschiedene legierte Stähle untersucht. Aufgrund der Ergebnisse kommt man zu den nachstehenden maximalen Anwendungstemperaturen: 13% Cr‐Stahl 800 °C; 13% Cr‐Stahl mit 2% Si und 0,8% Al bis 900 °C; 24% Cr‐Stahl mit Si bis 1000 °C. Als Schweißzusatzwerkstoff kann jeweils ein Material mit etwa gleichem Cr‐Gehalt verwendet werden. Im Falle des hochlegierten Stahls kann auch ein Zusatzwerkstoff mit 16% Cr und 36% Ni eingesetzt werden, da sich dann ein Schweißgerät mit günstigerem Wärmeausdehnungskoeffizienten ergibt. Bezüglich der Nachbehandlung der Schweißnaht sind bestimmte Bedingungen, besonders bei der Abkühlung, einzuhalten, um unerwünschten Gefügeänderungen vorzubeugen.
Zur Korrosion verzinkter Eisenwerkstoffe durch natürliche Brauchwässer
Authors: Müller D. , Dautel R. , Breckenfelder K.‐H. , Schiele C.
Published: December 2004

Laboratoriums‐ und Feldversuche mit verzinktem Eisen zeigen keine eindeutigen Zusammenhänge zwischen Wasserbeschaffenheit und Korrosion. Ebenso ist es nicht möglich, aufgrund von Potentialmessungen Aussagen über die Schutzschichtbildung zu machen. Aus diesem Grunde kann auch die Anwendbarkeit der Untersuchungsmethode nach DIN 50 930 in Zweifel gezogen werden, zumal nur in Einzelfällen die Bildung von ZrCO3 eindeutig nachgewiesen werden konnte.
Corrosion Behaviour of Manganese‐Containing Stainless Steels. III. Their susceptibility towards pitting corrosion
Authors: El Din A. M. Shams , Badran M. M. , Khalil S. E.
Published: December 2004

The pitting susceptibility of stainless steels with (%) 17.39 Cr, 5.3 Ni, 0.3–13.9 Mn in chloride solutions have been studied by a potentiodynamic cyclic polarization technique in solutions 0.1 N H2SO4 + 0.9 N Na2So4 + various amounts of NaCl. At low NaCl concentrations no pronounced influence of the chloride can be found and even at medium concentrations the passivation behaviour is generally maintained; in this region, however, there is an increase of dissolution and passivation current densities. High chloride concentrations, however, result in pitting which may be completely suppressed by a cyclic (anodic/cathodic) polarization technique. As to pitting resistance an alloy containing (%) 17.3 Cr, 5.3 Ni, 5.6 Mn is comparable to the steel CrNi 18 9.
Über den Reaktionsmechanismus und die Wirkungsweise von Komplex‐ und Chelatbildnern bei der Herstellung von Konversionsüberzügen aus Phosphaten und Oxalaten
Authors: Machu W.
Published: December 2004

Komplex‐ und Chelatbildner sind als anodische Depolarisatoren der primären Beizreaktion in Phosphatierungs‐ und Oxalierungslösungen wirksam. Am Beispiel der Beschleunigerwirkung der Fluoride, die mit dem Eisen lösliche und schwach dissoziierte Eisenkryolithe bilden, wurde gezeigt, daß die Fluoride in Zinkphosphatlösungen beispielsweise eine Doppelfunktion ausöben. Sie lösen nicht nur das Eisen mindestens 10mal so schnell wie irgendeine andere Säure auf, sondern sie binden und maskieren die gebildeten Eisenionen in Form von Komplexverbindungen nach Art won Eisenkryolithen. Mit der im Phosphatierungsbad vorhandenen Phosphorsäure und den Phosphationen des Zinkphosphats bilden sich unter Regenerierung der freien Flußsaure Vivianit, Phosphophyllit und Hopeit, welche schwerlöslichen Orthophosphatverbindungen die Schicht bilden. Die Flußsaure wirkt somit ähnlich wie ein Katalysator. In gleicher Weise wirken andere Komplex‐ und Chelatbildner, wie z. B. Pyro‐ oder Polyphosphate.

Ein gleichartiger Reaktionsmechanismus liegt bei Herstellung von Oxalatüterzügen in Gegenwart won aktivierend wirkenden Fluoriden vor. Das Optimum der Reaktionsverhältnisse für die Schichtbildung liegt bei gleichzeitiger kathodischer und anodischer Depolarisation unter Verwendung von Oxydationsmitteln sowie von Komplex‐ und Chelatbildnern als Beschleuniger, Kornverfeinerer und Aktivatoren vor.
Schutz von Bauwerken gegen Verwitterung, Korrosion und Erosion
Authors: Grunau Edv. B.
Published: December 2004

Die Korrosion von Metallkonstruktionen und Bauten wird an einigen Beispielen gezeigt, aus welchen die Folgen fehlerhaften Arbeitens zu ersehen sind. Typische Fälle sind die Korrosion von Kupferfassaden durch Kondenswasser, die Korrosion von Aluminium unterhalb von Anstrichfilmen ungenügender Dichtigkeit, die Korrosion von Mörtel durch feuchte Verbrennungsgase, der Angriff der Betonbewehrung (bei ungenügender Dichtigkeit des Betons oder bei Vorhandensein von Chloriden in Beton), Erosion durch Regenwasser, Verwitterung aufgrund thermischer, mechanischer oder makrobiologischer (Pflanzenwurzeln) Einwirkungen im Falle von Schimmelbefall in feuchten Räumen ist auch die Gefahr von Vergiftungen durch Sporen nicht zu vernachlässigen. Zusammenfassend weist der Autor auf die Notwendigkeit einer ausreichenden Überwachung bei Durchführung der Arbeiten hin, um Fehler zu verhindern, die — trotz zahlreicher Normen und Richtlinien — durch Nachlässigkeit oder Unwissenheit hervorgerufen werden.
Schutz von Betriebsräumen und ‐anlagen durch Beschichtungsstoffe — Teil I
Authors: van Oeteren K. A.
Published: December 2004

Der Verfasser zeigt die Wichtigkeit des Korrosionsschutzes durch Überzüge, der auch heute noch das größte Gebiet innerhalb des Korrosionsschutzes darstellt. Gleichzeitig wird gezeigt, welche Bedeutung der Wahl des geeigneten Anstrichstoffs und der Oberflächenvorbehandlung zukommt. Dabei muß man nämlich „vom Objekt zum Beschichtungsstoff”︁ und nicht „vom Beschichtungsstoff zum Objekt”︁ gehen, denn man muß dabei nicht nur den jeweiligen Anlagentyp berücksichtigen, sondern auch die zu erwartende Beanspruchung, die wiederum von geographischen, klimatischen u. a. Faktoren abhängig ist. Die Bedeutung dieser Faktoren wird mit Hilfe von Schutzmaßnahmen erläutert, die in zahlreichen Fällen der Praxis getroffen wurden, u. a. beim Schutz von Behältern in chemischen Fabriken, Stahlkonstruktionen, Rohrleitungen, Bautenelemente, Waggonwaagen, Kühltürme, Filterrahmen, Gasflaschen, Brennöfen usw.
Mittel und Methoden der Verpackungstechnologie gegen Auftreten von Korrosion an Packgütern
Authors: Schmidt E.
Published: December 2004

Der Schutz von in Verpackungen befindlichen Produkten wird erreicht durch „Barrieren”︁, welche die Diffusion der atmosphärischen Feuchtigkeit verbinden, und zwar entweder mit Hilfe von mehr oder weniger undurchlässigen Wänden oder durch Zusatz von Trockenmitteln oder Gasphaseninhibitoren. Die Wände können dabei durch Umhüllungen oder Überzüge gegeben sein. Mit Hilfe von Tabellen, welche die verfügbaren Stoffe und Methoden einander gegenüber stellen, ist es möglich, geeignete Korrosionsschutzsysteme aufzubauen.
Schutz von Betriebsrämen und ‐anlagen durch Beschichtungsstoffe. Teil II
Authors: van Oeteren K. A.
Published: December 2004

Der zweite Teil dieser Arbeit (Teil I sieche WuK 24 [1973] 6; 496–507) behandelt die folgenden Schutzprobleme: Innen‐ und Außenkorrosionsschutz eines Wasser‐Hochbehälters; Schutz von Stahlformen für Betonblöcke (für Hafenbau); Innen‐Korrosionsschutz von Getriebekästen für ölhydrauliche Anlagen; Schutz von Spundwänden; Schutz der Bodenzone einzubetonierender Stahlkonstruktionen; Schutz von Beizanlagen, besonders von Regenerationsbehältern; Schutz von Lagerbehältern für die Lebensmittel‐ und Getränkeindustrie (u. a. Wein‐ und Bierbehälter); Schutz von Heizöl‐ und Dieselkraftstoffbehältern sowie Rohölbehältern; Schutz von Wasserreinigungsanlagen; Schutz von wasserberieselten Kunststoffspritzanlagen; Korrosionsschutz von Isolierungen aus Polyurethanschaumstoff; Schutz von Abgaskaminen.
Widerstand der Schweißverbindungen kohlenstoffarmer und mit Molybdän legierter korrosionsbeständiger Stähle gegen interkristalline und Messerlinienkorrosion
Authors: Číhal V. , Lehká N. , Matuška K.
Published: December 2004

Schweißverbindungen aus Stählen mit (%) 0,019–0,080 C, 1,00–1,56 Mn, 0,03–0,92 Si, 0–0,026 P, 0–0,018 S, 10–13,60 Ni, 16–20,50 Cr, 0–3 Mo, 0–0,057 Ti, 0–0,87 Nb, hergestellt durch Elektroschlackenschweißen und automatisches UP‐schweißen, sind im allgemeinen nicht anfällig für interkristalline und Messerlinienkorrosion; eine gewisse Anfälligkeit bei den Mo‐haltigen Typen läßt sich durch Glühen bei 650 °C weitgehend verringern. Unterschiede zwischen dem Grundmetall und dem Schweißgut konnten nicht festgestellt werden; in vielen Fällen erwies sich das Schweißgut sogar als beständiger. Als Prüflösungen wurden verwendet: Schwefelsäure + Cu‐Sulfat + Cu, siedend, 48 h, bzw. 65%ige siedende Salpetersäure, 3 · 48 h.
Die potentiodynamische Polarisationskurve des Kupfers in Lösungen von Chloriden
Authors: Bartoníček R.
Published: December 2004

Die potentiodynamische, bei schneller Polarisation erhaltene Kurve gibt nicht nur die Auflösung des Kupfers wieder, sondern auch die Redoxreaktionen, die in diesem ziemlich komplexen System ablaufen. Der erste Teil der Kurve charakterisiert die anodische Reaktion, die zur Bildung von CuC1−2 und CuCl führt; er kann daher zur Untersuchung der spontan ablaufenden Korrosion verwendet werden. Außerdem ermöglicht die schnelle Polarisation die Abschätzung des Einflusses verschiedener Faktoren, insbesondere die Erfassung schnell ablaufender Reaktionen, die bei langsamer Polarisation nicht erfaßt werden. Man könnte auf dieser Grundlage z. B. auch den Einfluß von Gefügeänderungen in Kupferlegierungen untersuchen.
Adsorbability of Thiourea on Iron Cathodes
Authors: Ammar I. A. , El Khorafi F. M.
Published: December 2004

The adsorption of thiourea on iron cathodes has been studied in 0.1 N sulphuric acid solution containing 10−1 and 10−2 Mol of thiourea at 30, 40 and 50 °C. The surface coverage has been calculated by comparing current density (at constant potential and temperature) of solutions with and without inhibitor. The results show that adsorption is due to specific adsorption forces of molecules and HS− anions as well as to electrostatic forces of cations. The authors have determined the adsorption energy and the enthalpy, free standard energy and entropy of adsorption. On the basis of these results it is feasible to presume that thiourea would be rather efficient an inhibitor of the corrosion for iron acid solution.
Bestimmung der pH‐Abhängigkeit und der Aktivierungsenergie der Adsorption von Sauerstoff aus wäßriger Lösung an Platin
Authors: Grubitsch H. , Saiger S.
Published: December 2004

Die Verfasser untersuchten die spontane Adsorption von Sauerstoff an Platin aus wäßrigen Elektrolyten in Abhängigkeit von der Zeit und bei verschiedenen PH− Werten sowie Temperaturen (25, 5 und 75° C) mit Hilfe kathodischer Ladungskurven, die galvanostatisch ermittelt wurden. Die Analyse der Kurven erforderte die Bestimmung der Doppelschichtkapazität bei verschiedenen PH−Werten und die Ermittlung des Rauhigkeitsfaktors der Platinoberfläche. Die Analyse dieser Gleichung führt zu einer ziemlich hohen scheinbaren Aktivierungswärme, woraus zu schließen ist, daß es sich um eine dissoziative Chemisorption von Sauerstoffatomen handelt. Der Kurvenverlauf deutet darauf hin, daß die Doppelschicht im neutralen Bereich Wassermoleküle aufnimmt, im alkalischen und sauren Bereich hingegen OH−‐Ionen. Versuche mit rotierender Scheibenelektrode ergaben keine lineare Beziehung zwischen Quadratwurzel der Winkelgeschwindigkeit. Diese Feststellung ermöglicht den Schluß, daß die Adsorption von Sauerstoff in gerührten Systemen nicht ausschließlich diffusionskontrolliert ist.
Studies on the pitting corrosion of zinc in aqueous solutions I. Variations of the potential of the zinc electrode in relation to the concentration of the aggressive anion
Authors: El Din A. M. Shams , El Haleem S. M. Abd
Published: December 2004

The way in which the stationary potential of a zinc electrode previously treated with various passivating and inhibiting solutions changes in the present of the chloride, bromide and iodide ions is studied in solutions of potassium chromate, disodium hydrogen phosphate and sodium tungstanate. It is shown that the potential change as a function of the halogenide concentration follows a S shaped curve. The potentials are established after an induction period the duration of which decreases as the concentration of the aggressive anion increases and/or the concentration of the inhibiting anion decreases. A linear relationship is obtained for the maximum permissible concentration of the aggressive anion at a given concentration of the inhibiting anion. This relationship is theoretically derived from the defect resulting from the specifical adsorption of both ions at the metal surface. While e.g. a temperature increase shifts the potential in pure chromate solutions to more positive potentials, thus improving the protective effect, the permissible concentration of the aggressive anion is simultaneously decreased. This phenomenon suggests that in these conditions the desorption of the inhibiting anions is increased.
Crevice Corrosion of Titanium and AISI 304 in Acid Solutions. Comparison of experimental and calculated results
Authors: Vicentini B.
Published: December 2004

The beginning of crevice corrosion of titanium and AISI 304 in acid solution was investigated experimentally. In addition, the current and potential distributions along the crevices were determined by numerical integration of the differential equation that describes the phenomenon. The experimental results agree satisfactorily with those obtained by calculation and confirm the assumptions introduced in the schematization of the phenomenon. However, long time experiments revealed a progressive deviation of the experimental results from the calculated ones, in the opposite direction for AISI 304 and titanium. Thus, in the first case, following a time that seems to be independent of the potential imposed upon the free surface, the entire surface within the crevice becomes gradually passivated. In contrast, in the case of Titanium the corrosion behaviour of the area within the crevice reaches a steady state.
Amines as Corrosion Inhibitors for Copper
Authors: Patel N. K. , Franco J.
Published: December 2004

The study of the inhibiting effect of certain pyridine and aniline derivatives on the corrosion of copper in persulphate solutions enables the compounds to be arranged in the following series of decreasing inhibiting power; 2,6‐lutidine – 2‐picoline – pyridine – m‐anisidine – p‐phenetidine – aniline.

Inhibition may generally be attributed to the adsorption of organic molecules, nitrogen being an electron donor and becoming attached to the metal surface. Symmetric substitution by methyl groups in the pyridine molecule increases the inhibiting effect. In the case of aniline derivatives m‐anisidine is superior to the other compounds studied. On the base of electrochemical experiments it may be concluded that the reaction is under cathodic control, the cathode being extremely polarized at high current densities.
Die Ausbreitung von Spannungskorrosionsrissen in der Aluminium‐Legierung AlZnMg 3
Authors: Berggreen J. , Engell H.‐J. , Kaesche H.
Published: December 2004

Die Autoren untersuchten die Rißausbreitung in gekerbten Proben in einer Natriumchloridlösung bei 30°C und unter konstanter Last. Die Rißausbreitung wurde mit Hilfe der Mikrofotografie verfolgt, mit der auch Gleitvorgänge innerhalb des Metalls erfaßt werden konnten. Geht man vom Ruhepotential aus und verschiebt dieses nach mehr kathodischen Werten, so ergibt sich zunächst eine Verlangsamung der Rißausbreitung, was durch einen kathodischen Schutzeffekt zu erklären ist und dann – im Bereich der Wasserstoffentwicklung mit gleichzeitiger kathodischer Korrosion – eine Erhöhung der Rißausbreitungsgeschwindigkeit. Diese Tatsache kann einer Wasserstoffversprödung zugeschrieben werden. Diese höhere Beständigkeit der technischen Legierung im Vergleich zur hochreinen Legierung läßt vermuten, daß die Verunreinigungen verzögernd wirken und zu einer Verlängerung der Inkubationsperiode führen.
Effect of Arsenic on Permeation of Hydrogen Through Steel Membranes polarized cathodically in aqueous solution
Authors: Zakroczymski T. , Szklarska‐Śmiałowska Z. , Smialowski M.
Published: December 2004

A sensitive technique is developed for studying the effect of As and its compounds on the permeation of hydrogen through steel membranes electrolytically charged at various pH values. Use of a rotating disc electrode permits to change pH at the cathode over a large range without changing composition of the bulk electrolyte. The results of this study strongly support previous conclusions as to the dominant part played by promoter hydrides as species accelerating the entry of hydrogen into metals. In the case under consideration, AsH3 has been found to promote the permeation of hydrogen evolved from acid and alkaline media. On the other hand, surface films, deposits, and precipitates of As impede the entry of hydrogen into the steel.
Deposits formed on iron during cathodic polarization in the presence of arsenic and their effect on hydrogen permeation
Authors: Lunarska E. , Szklarska‐Śmiałowska Z. , Smialowski M.
Published: December 2004

Deposits produced on iron and steel during cathodic polarization in the presence and absence of arsenic in acid and alkaline solutions have been studied microscopically, by electron microprobe analysis, and by double layer capacity measurements. The results of these studies are compared with permeation rates of hydrogen through rotating membranes. It is shown that the compactness of the deposits and their effect on the permeation depend on following major factors: surface condition and pre‐treatment of the cathode, pH of the electrolyte, As concentration, electrode potential. Elemental arsenic deposited on the cathode does not promote the permeation of hydrogen. On the contrary, adherent and compact films impede the entry of hydrogen into the metal phase. Arsine adsorbed on the metal surface is the main promoting species.
The Influence of Chloride Concentration on the Kinetic Behaviour for the Initiation Stage of pitting corrosion on aluminium
Authors: Broli Aa. , Holtan H. , Sigurdsson H.
Published: December 2004

Experiments are performed to study the influence of applied potential and chloride concentration on the kinetic behaviour of pitting corrosion initiation for unalloyed aluminium. A potentiostatic method is used at 30°C in deaerated solutions of sodium chloride. The pitting potential, Ep, is determined by the extrapolation method described by Broli, Holtan and Midjo, and a relation between Ep and chloride concentration is found. Kinetic interpretations such as the influence of applied potential and chloride concentration on the induction time are given.
Zum Potentialverhalten der Oberfläche metallischer Werkstoffe bei milder und starker Schwingungskavitation – V. Eisen‐Werkstoffe
Authors: Althof F.‐C. , Buhl H. , Voigt H.
Published: December 2004

Vier Werkstoffe – Reineisen, niedriglegierter Stahl, 13% Cr‐Stahl und CrNi‐Stahl 18 9 – wurden in 1 n NaCl‐Lösung und in künstlichem Meerwasser untersucht, wobei der Sauerstoffgehalt zwischen gesättigt und Null verändert wurde. Die Änderungen des Elektrodenpotentials ermöglichen Schlüsse bezüglich des Kavitationseinflusses. Reineisen und niedriglegierter Stahl sind unter den Versuchsbedingungen in aktivem Zustand; Schwingungen bis 20000 g führen zu einer Potentialverschiebung nach positiverer Richtung. Bei noch höheren Schwingungsbelastungen kommt es zu einer Verschiebung in entgegengesetzter Richtung (zurückzuführen auf Entgasung der Lösung). Der CrNi‐Stahl befindet sich im Passivzustand, doch die Art der Potentialverschiebung ist etwa die gleiche. An der Grenzfläche zur Flüssigkeit kommt es jedoch zu Martensitbildung. Der Chromstahl nimmt eine Zwischenstellung ein und ist in der NaCl‐Lösung aktiv, im Meerwasser hingegen passiv. Die Potentialverschiebung nach negativeren Werten, die bei allen untersuchten Werkstoffen im sauerstoffreien Elektrolyten bei hohen Beschleunigungen beobachtet wird, läßt sich einer Erleichterung der anodischen Teilreaktion zuschreiben.
Zur Eignung des Huey‐Tests als Abnahmeprüfung
Authors: Kohl H. , Souresny H. , Zitter H.
Published: December 2004

Bei Abnahmen nach dem Huey‐Test wird der Vergleichstreubereich zwischen den Laboratorien meist nicht berücksichtigt, bzw. dem Wiederholstreubereich innerhalb eines Laboratoriums gleichgesetzt, was im Falle einer Nachprüfung zu unerwarteten Abweichungen führt. In einer Gemeinschaftsarbeit von 7 Laboratorien wurde bei einer verhältnismäßig geringen Wiederholstreuung von etwa 4 bis 8 Relativprozent eine wesentlich größere Vergleichstreuung von 10 bis 20 Relativprozent festgestellt. Das bedeutet, daß der Sicherheitsabstand gegenüber dem geforderten oder vereinbarten Grenzwert des Gewichtsverlustes merklich ins Gewicht fällt und in manchen Fällen eine Einschränkung des Lieferumfanges bewirken kann.
Pitting Potentials of Aluminium Alloys
Authors: Holtan H. , Sigurdsson H.
Published: December 2004

The pitting potential of the following aluminum alloys in 3% sodium chloride solution was measured using potentiodynamic and potentionstatic methods: Al‐2.7 Mg with 0–0.47% Cr, Al‐2.7 Mg with 0–0.94% Mn, Al‐2.7 Mg‐0.43 Mn with 0–0.31% Cr, Al‐4.7 Mg‐0.13 Cr‐0.78 Mn, Al‐51 Mg with 0.1 and 0.3% Sb, Al 2S‐1/2H (commercial aluminum) super pure Al (99,99% Al). The results show that the pitting potential is not much affected by the alloying elements. The pitting potetial decreases with increasing content of magnesium and increases slightly with increasing content of manganese up to a certain point. The nature and amount of secondary phases do not seem to have any marked influence upon the pitting potential.
Cast Iron with High Al‐Content in Sulfuric Acid
Authors: Defrancq J. N.
Published: December 2004

The corrosion characteristics of Al‐cast iron with 25% of Al in sulfuric acid are determined and compared to the values that were obtained on Al‐cast iron with 1–3% Al. It is concluded that the corrosion current density is very high. The value of B is 0.020. For p the value of 1 was obtained and for q: 1.17 BA is 0.044 and bC = −∞.
Automatische Ermittlung von Kontaktkorrosionsdaten und ihre Auswertung mittels Polarisationsdiagrammen
Authors: Wiedemann K. H. , Gerodetti B. , Dietiker R. , Gritsch P.
Published: December 2004

Zur Beurteilung der Kontaktkorrosionsgefahr an einer Werkstoffkombination interessieren die Ruhepotentiale der beteiligten Werkstoffe, das Mischpotential des Kontaktelementes und der Elementstrom. Es wurde ein Prüfstand mit 6 Meßplätzen entwickelt, auf dem diese Daten von 6 Varianten von Werkstoffkombination/Lösung/Lösungskonditionierung/Temperatur gleichzeitig automatisch erfaßt werden. Die Meßplätze sind mit je zwei elektrolytischen Zellen ausgerüstet. Während in der einen Zelle die Ruhepotentiale der beiden Werkstoffproben ermittelt werden, lassen sich in der anderen an einem kurzgeschlossenen identischen Probenpaar das Mischpotential des Kontaktelements und der Elementstrom messen. Die Meßgrößen werden von einem programmierbaren Meßstellenabtaster nacheinander abgefragt und registriert.

Bei Werkstoffkombinationen aus einem niedriglegierten Baustahl, einem CrNiTi‐Stahl 18 9, einer NiCrFe‐Legierung 72 20 und einer Molybdänlegierung mit 0,5% Ti und 0,1% Zr in je einer basischen und einer sauren reduzierenden Lösung ist der unlegierte Stahl stets der unedlere, die Molybdänlegierung stets der edlere Partner. Stellt man die Meßgrößen in Polarisationsdiagrammen dar, so gewinnt man einen überblick über mögliche Kontaktkorrosionen in den verschiedenen Systemen sowie Hinweise auf den Korrosionsmechanismus.
Die Wasserstoffaufnahme von Eisen bei der Korrosion in neutralen bis schwach sauren Elektrolyten
Authors: Riecke E.
Published: December 2004

Bei der atmosphärischen Korrosion und der Korrosion in wäßrigen Elektrolyten kann Stahl Wasserstoff aufnehmen. Mittels einer Permeations‐Methode wird die im Eisen bei der Korrosion in verdünnten Lösungen von Schwefelsäure, Salzsäure und Eisensalzen auftretende Wasserstoff‐Aktivität im pH‐Bereich von 1 bis 6 untersucht. Bei pH‐Werten unter 5 in sauerstoffarmen und unter 4 in luftgesättigten Lösungen erreicht die Wasserstoffaktivität Werte über 0,1 (bezogen auf aH = 1 für PH2 = 1 bar) und kann damit langsames Rißwachstum in wasserstoffempfindlichen Stählen auslösen. Anionen und Na+‐Ionen beeinflussen diese Ergebnisse nur wenig; der Einfluß von Fe3+‐Ionen und des Sauerstoffgehalts der Lösung wird erörtert.
Dehnungsinduzierte Korrosionsprozesse
Authors: Herbsleb G. , Pöpperling R. , Schwenk W.
Published: December 2004

Bei der Untersuchung der Spannungsrißkorrosion standen bisher statische Belastungen σ im Vordergrund. Eine weitere Einflußgröße, die bisher weniger beachtet wurde, ist die durch eine mechanische Spannung erzeugte Dehnung ϵ. Zunehmend werden auch den zeitlichen Änderungen dieser Einflußgrößen,\documentclass{article}\pagestyle{empty}\begin{document}$ \dot \sigma $\end{document}und\documentclass{article}\pagestyle{empty}\begin{document}$ {\dot \varepsilon }$\end{document}, Beachtung geschenkt. Eine durch Aufbringen einer Last erzeugte Dehnung kann zwei Wirkungen haben: (i) Aufreißen von Schutzschichten und/oder (ii) mechanische Stimulation der anodischen Metallauflösung. Beide Schadenstypen werden erörtert. Der Schadenstyp (i) wird als spannungsinduzierte, der Schadenstyp (ii) als dehnungsinduzierte Korrosion bezeichnet.

Es wird untersucht, ob bei der Spannungsrißkorrosion der Schadenstyp (ii) stets beteiligt ist. Für einige Systeme ist diese Frage mit Sicherheit zu verneinen, bei zahlreichen Systemen hat jedoch die Dehngeschwindigkeit einen Einfluß auf das Auftreten von Spannungsrißkorrosion. Die jeweiligen Systeme werden näher beschrieben. Wesentlich für die aufgestellten Betrachtungen ist die Einführung einer unteren und oberen kritischen Dehngeschwindigkeit für das Auftreten von Spannungsrißkorrosion. Übergänge von dehnungsinduzierter Spannungsrißkorrosion zur Schwingungsrißkorrosion liegen bei sehr hohen unteren kritischen Dehngeschwindigkeiten vor.

Aus dem Einfluß der Dehnung auf die Spannungsrißkorrosion ergeben sich Folgerungen für die Anwendung von Prüfverfahren zum Erkennen einer Anfälligkeit metallischer Werkstoffe für Spannungsrißkorrosion.
Kinetics and mechanism of the reaction of iron with sulfur vapor in the temperature range of 250 to 500°C
Authors: Foroulis Z. A.
Published: December 2004

The kinetics and mechanism of the reaction between iron and sulfur vapor were investigated in the temperature range of 250 to 500°C and sulfur vapor pressures of 10 to 300 mm Hg. The sulfurization of iron has been found to follow a parabolic law. In the temperature range 250 to 370°C the reaction product consisted of an inner FeS scale, and an outer thin FeS2 layer. The activation energy of this process amounts to 27 kcal/mole, and the parabolic reaction rate constant varies according to approximately the 1/2 power of the sulfur pressure. In the temperature range 370 to 500°C the reaction product consists entirely of an FeS scale. The activation energy of the limiting process in this temperature range is about 14 kcal/mole. The parabolic reaction rate constant at 500°C shows a sulfur pressure dependence according to approximately the 1/7 power of the sulfur vapor pressure. The mechanistic significance of the experimental results is considered in some detail.
The high temperature oxidation behaviour of austenitic stainless steels
Authors: Hales Royden
Published: December 2004

High temperature annealing in a dynamic vacuum has been utilised to induce the growth of duplex oxide over the whole surface of stainless steel specimens. It is found that duplex oxide grows at a rate which does not obey a simple power law. The oxidation kinetics and oxide morphology have also been studied for a series of ternary austenitic alloys which cover a range of composition between 5 and 20% chromium.

A model has been developed from the observations to describe the formation of duplex oxide and the subsequent formation of a “healing layer” which virtually causes the oxidation process to stop. This phase tends to form at grain boundaries and a relationship has been derived for the reaction kinetics which relates the reaction rate with grain size of the substrate.
Atmospheric corrosion of zinc as measured by an electrochemical technique
Authors: Haagenrud S. E.
Published: December 2004

The performance of the electrochemical technique first developed by Mattsson and Kučera, has been studied under long term exposure of a zinc cell at the test site Birkenes in Southern Norway. This site has a large impact of long range transported sulphur pollutants, and the measurements have also been used to evaluate the question of possible corrosion effects from these pollutants on zinc. The cell has performed well for almost the whole measuring period, small shortcircuiting periods may be excluded with negligible error. Analysis of the electrochemical and environmental data show significant corrosion effects on zinc from the precipitation as such and also indicate qualitatively short term corrosion effects from rural levels of sulphur pollutants. The study has shown that the electrochemical technique is a promising method for providing informations about short term variation of the corrosion rate and time of wetness under various environmental conditions.
Influence of the surface state on the Initiation of Crevice Corrosion on stainless steels
Authors: Sydberger T.
Published: December 2004

Results from sea‐water and laboratory exposure tests with multiple crevice assemblies are presented. The results from tests on austenitic and ferritic‐austenitic stainless steel samples subjected to various surface treatments demonstrate that an acid treatment greatly improves the crevice corrosion resistance of previously ground surfaces. Pickling in dilute sulphuric acid and passivation in nitric acid has thereby virtually the same beneficial effect as the common nitric + hydrofluoric pickling acid. The beneficial effect of pickling and passivation is related to the removal from the surface of sulphide inclusions, being potential nucleation sites for the initiation of discrete pitting attacks preceding the onset of crevice corrosion. Potentiodynamically determined pitting potentials and results from testing in 10% FeCl3 · 6 H2O according to ASTM G 48–76 show poor correlation with results from sea‐water exposures.
The atmospheric corrosion of unprotected carbon steel – a comparison between field study and laboratory test
Authors: Johansson L.‐G. , Vannerberg N.‐G.
Published: December 2004

A comparison is made between the atmospheric corrosion of unprotected carbon steel in outdoor exposures and results from laboratory tests. The atmospheric corrosion in the outdoor exposures is expressed as a function of certain atmospheric parameters (e.g. SO2 concentration). In the laboratory tests the atmosphere consisted of air containing known amounts of SO2 and water vapour. The experiments were carried out in such a way that both supply and deposition of SO2 was known. There was good agreement between the empirical formula and the results from the laboratory tests provided that the supply of SO2 in the laboratory test was below ca. 0.5 μg · h−1 · CM−2.
Untersuchung zur Schwingungsrißkorrosion an unlegierten und niedrig legierten Stählen
Authors: Weidemann R.
Published: December 2004

Es wurden 6 handelsübliche Stähle – 3 Feinkornstähle im normalisierten Zustand, 1 vergüteter Stahl, 1 warmfester Stahl und 1 vergüteter Stahl hoher Festigkeit – in einer mit Korrosionskammer ausgestatteten Umlaufbiegemaschine geprüft. Als Medium diente 0,05 m NaCl‐Lösung. Das Ergebnis zeigt, daß bei allen untersuchten Stählen die Biegewechselfestigkeit durch dieses schwache Korrosionsmedium deutlich herabgesetzt wird. Der Einfluß der SwRK ist um so größer, je höher die Festigkeit des Stahls ist. Im Vergleich dazu sind die Prüfparameter von untergeordnetem Einfluß. Durch kathodische Polarisation wird die SwRK‐Beständigkeit bei den Stählen hoher Festigkeit und SwRK‐Empfindlichkeit verbessert; bei den Stählen niedrigerer Festigkeit wird vollständiger kathodischer Schutz erzielt.

Auch in kondensierender Feuchtigkeit wird die Biegewechselfestigkeit herabgesetzt.
Phasenumwandlungen in Korrosionsschichten auf Eisen: Mößbauerspektroskopische Untersuchungen
Authors: Meisel W. , Gütlich P.
Published: December 2004

Zur Untersuchung der Korrosion von Stahlblechen wurde die mößbauerspektroskopische Phasenanalyse in Transmissions‐ und Streugeometrie eingesetzt.

Die Korrosion von Stahlblechen führt in einer Atmosphäre von geringer Korrosivität nach langen Expositionszeiten vorwiegend zu den relativ stabilen β‐Phasen der möglichen Fe‐Korrosionsprodukte. Bei durch HCl‐Zusatz erhöhter Korrosivität ergibt sich eine Bevorzugung der Bildung von β‐FeOOH und kein Auftreten der α‐Phasen. Auch der Einfluß von. Beschichtungen auf die Phasenzusammensetzung wird behandelt. Die Entstehung und Umwandlung der verschiedenen Fe‐haltigen Phasen im Rost läßt sich anhand eines Stabilitätsdiagramms verstehen. Auch die Wirkung von sogenannten „Rostumwandlern”︁ wird betrachtet. Sie führen nicht zu den beabsichtigten, sondern eher zu schädlichen Phasenumwandlungen in den Rostschichten.
To the problems of the function and the spreading of sulphate nests in the layer of corrosion products on steel
Authors: Beránek E. , Bartoň K. , Míček K.
Published: December 2004

The formation and propagation of sulphate nests in the corrosion products formed during atmospheric corrosion of steel is controlled to a large extend by the osmotic pressure within these nests. The same importance can be attributed to the composition of the FeOOH containing film covering the nests; as the FeOOH content increases the elasticity of the film is increased, too, so that the membrane is able to remain intact, i.e. without cracking even at increasing osmotic pressures in the nest. This behaviour improves the resistance of steel to atmospheric corrosion. These conditions are very important in particular with periodic wetting regimes. This mechanism also explains the effect of silicon which is incorporated in amorphous form in the corrosion products and thus improves the elasticity of the corrosion product membrane.
Einfluß unterschiedlicher Anlaßtemperaturen auf die Korrosionszeitfestigkeit eines molybdänlegierten 13%igen Chromstahls in chloridhaltigen Medien
Authors: Schmitt‐Thomas Kh. G. , Meisel H. , Haubenberger W. D.
Published: December 2004

Der Werkstoff X 20 CrMo 13 wurde für die Durchführung von Schwingungsrißkorrosionsversuchen auf verschiedene Festigkeitszustände eingestellt. Die Schwingungsrißkorrosionsbeanspruchung erfolgte in 0,01 n NaCl‐Lösung bei Temperaturen von 150 and 200 °C. Es zeigte sich, daß mit einer Steigerung der Festigkeit des Werkstoffs ein starker Abfall der Schwingungsrißkorrosionsbeständigkeit verbunden ist. In der höchsten Festigkeitsstufe zeigt der Werkstoff erwartungsgemäß deutliche Spannungsrißkorrosionsempfindlichkeit. Dennoch läßt: eine zuordnende Morphologieuntersuchung der Bruchfläche erkennen, daß Spannungskorrosionsmechanismen nicht schädigungsbestimmend bei der Ausbildung der Bruchflächen sind. Lochfraßstellen auf der Probenoberfläche stehen in Abhängigkeit von den an die Proben angelegten. Spannungsamplituden. Lochfraß und Anrißbeginn bei der Schwingungsrißkorrosionsbeanspruchung können jedoch nicht in kausalen Zusammenhang gebracht werden. Dünnschichtanalysen weisen auf den Proben eine Deckschicht nach, die einen guten Korrosionsschutz erwarten lassen müßte. Entscheidend für den Ablauf der Schwingungsrißkorrosion ist offensichtlich die Repassivierungsgeschwindigkeit, die durch den Molybdänzusatz gesteigert werden sollte. Bei den gewählten Versuchsbedingungen, insbesondere bei den gewählten Temperaturen, ist jedoch der Molybdänzusatz noch nicht ausreichend, um eine deutliche Verbesserung der Schwingungsrißkorrosionbeständigkeit zu erzielen. Die Versuche werden mit dem gewählten Werkstoff, jedoch unter Zulegierung eines höheren Molybdängehalts fortgesetzt.
Kinetische und kristallografische Modellbetrachtungen zur Korrosion und Passivität von Metallen
Authors: Forker W. , Worch H. , Rahner D.
Published: December 2004

Auf der Basis detaillierter Vorstellungen über Nahordnungsstrukturen und Strukturwandlungen sowie über chemische und elektrochemische Teilvorgänge in Korrosionssystemen Metall/wäßrige Elektrolytlösung wird ein Modell entwickelt, das sowohl kinetische als auch kristallographische Aspekte der Korrosion und Passivierung von Metallen einheitlich erfaßt. Am Beispiel des Eisens werden die atomaren Teilschritte der Auflösung und Deckschichtbildung vom Aktiv‐ bis zum Passivzustand als Ergebnis von Wechselwirkungen zwischen strukturierten kondensierten Phasen verfolgt und mit den formalkinetischen Stromdichte‐Potential‐Korrelationen verglichen.
Abtragungsraten von Zink bei Gleich‐ und Wechselstrombelastung
Authors: von Baeckmann W. G. , Funk D.
Published: December 2004

Die Untersuchungen ergaben, daß Zink sowohl als Reinzink als auch als Verzinkung von Bandeisenerdern durchaus zur Ableitung von Wechselstrom eingesetzt werden kann. Eine durch Wechselstrom bedingte Verschiebung des Potentials in positiver Richtung, wie sie bei Magnesium auftritt, ist nicht gegeben. Bei Wechselstrombelastung wird die Abtragungsrate des Zinks nur unwesentlich erhöht.

Allerdings ist beim Einsatz sowohl von verzinkten Bandeisenerdern als auch von Zinkanoden zur Ableitung von Wechselströmen darauf zu achten, daß bei zusätzlichem kathodischem Schutz keine Potentialwerte negativer als − 1,5 V eingestellt werden. Anderenfalls besteht die Möglichkeit, da es sich bei Zink um ein amphoteres Metall handelt, daß durch die dann entstehende Natronlauge ein erhöhter Materialabtrag stattfindet. Die Untersuchungen zeigen, daß bei Potentialwerten zwischen − 1,1 V bis − 1,5 V der Zinkabtrag erheblich vermindert wird. Bei Einstellung des Potentials muß berücksichtigt werden, daß durch die zusätzliche Wechselstrom‐überlagerung das Zink‐Potential bis etwa 0,1 V negativer werden kann, d. h. daß der Potentialwert nur auf ungefähr − 1,3 V bis − 1,4 V eingestellt werden sollte.
Zur Korrosion von Lötverbindungen
Authors: Yamaguchi S.
Published: December 2004

Eine Lötverbindung in einem elektrischen PtNi‐Kontakt wurde an der Luft unter Bildung von Pb (OH)2 · (PbCO3)2 angegriffen. Dieses Korrosionsprodukt beeinträchtigte aufgrund seiner dielektrischen Eigenschaften den Kontakt zwischen Pt und Ni. Es empfiehlt sich daher, zum Verbinden von elektrischen Kontakten keine bleihaltigen Legierungen zu verwenden.