The effect of modification diamond nanopowders detonation synthesis to change their electrokinetic and electrophysical characteristics
Authors:   V.N. Bakul Institute for Superhard Materials National Academy of Sciences of Ukraine, Bazaliy G. , Oliinyk N. ,   V.N. Bakul Institute for Superhard Materials National Academy of Sciences of Ukraine, Ilnytska G. ,   V.N. Bakul Institute for Superhard Materials National Academy of Sciences of Ukraine
Published: December 2020

Development of methods for controlling the change in the functional cover and the energy composition of the surface of detonation synthesis diamond nanopowders is necessary to create stable suspensions and materials from them. The aim of this work is to study changes in the electrokinetic and electrophysical characteristics of the powder as a result of the modification of detonation synthesis diamond nanopowders using a liquid-phase thermochemical treatment. Diamond nanopowders of grades ASUD-75 - ASUD-99 with different sp2-hybridization carbon content, manufactured at the V.I. Bakul National Academy of Sciences of Ukraine from the product of detonation synthesis of diamond from the company "ALIT" (Zhytomyr) investigated. Diamond nanopowders of ASUD-90 grade after their modification by means of liquid-phase thermochemical treatment using: a melt of alkalis, a mixture of nitric and sulfuric acids, a mixture of chromic and sulfuric acids were investigated by electrophoresis using a device "Dzeta-potential-analizer" company "Mikromeritiks". Electrokinetic characteristics of diamond nanopowders: the magnitude and sign of the electrokinetic potential, electrophoretic mobility are determined. The methods were used to study the physicochemical characteristics of nanopowders: electrical resistivity, carbon content of sp2-hybridization, mass fraction of impurities in the form of an incombustible residue, and specific surface area. In this work, it was established by electrophoresis that the value of the electrokinetic potential and electrophoretic mobility of the powder decrease by 2-10 times with a decrease in the mass fraction of sp2-hybridization carbon from 23.6 to 0 wt%. Using the ASUD-90 nanopowder as an example, it is shown that the modification of the nanopowder by the liquid-phase method using thermochemical treatment with mixtures of oxidants leads to a decrease in the values ​​of electrophoretic mobility by 1.1-7.5 times and electrokinetic potential by 1.1-7.3 times. It was found by dielectric measurement that the tangent of the dielectric loss angle of diamond nanopowders of grades ASUD-90 - ASUD-99 is in the range 0.3046 - 0.3146. Modification of the ASUD-90 grade nanopowder using a liquid-phase thermochemical treatment leads to a change in the interval of the dielectric loss tangent, namely 0.2450-0.3249. According to the degree of increase in the ratio of the dielectric loss tangent from 0% humidity to 100% humidity, the methods for modifying nanopowders can be arranged as follows: modifying using a melt of alkalis (ASUD-90-1 sample, S = 12.8%) <mixture of chromic and sulfuric acids (sample ASUD-90-3, S = 13.8%) <mixture of nitric and sulfuric acids (sample ASUD-90-2, S = 20.8 %).