Fabrication and characterization of YBa<sub>2</sub>Cu<sub>3</sub>O<sub>7–</sub><inline-formula><tex-math id="Z-20210129174424">\begin{document}$_{ \delta}$\end{document}</tex-math><alternatives><graphic xmlns:xlink="http://www.w3.org/1999/xlink" xlink:href="3-20201291_Z-20210129174424.jpg"/><graphic xmlns:xlink="http://www.w3.org/1999/xlink" xlink:href="3-20201291_Z-20210129174424.png"/></alternatives></inline-formula> step-edge Josephson junctions on MgO substrate for high-temperature superconducting quantum interference devices
Authors: Wang Hong-Zhang , Li Yu-Long , Xu Tie-Quan , Zhu Zi-Qing , Ma Ping , Wang Yue , Gan Zi-Zhao ,   State Key Laboratory for Mesoscopic Physics, Applied Superconductivity Center, School of Physics, Peking University, Beijing 100871, China
Published: January 2021

The YBa<sub>2</sub>Cu<sub>3</sub>O<sub>7–<i>δ</i></sub> (YBCO) step-edge Josephson junction on MgO substrate has recently been shown to have important applications in making advanced high-transition temperature (high-<i>T</i><sub>C</sub>) superconducting devices such as high-sensitivity superconducting quantum interference device (SQUID), superconducting quantum interference filter, and THz detector. In this paper, we investigate the fabrication and transport properties of YBCO step-edge junction on MgO substrate. By optimizing the two-stage ion beam etching process, steps on MgO (100) substrates are prepared with an edge angle <i>θ</i> of about 34°. The YBCO step-edge junctions are then fabricated by growing the YBCO thin films with a pulsed laser deposition technique and subsequent traditional photolithography. The resistive transition of the junction shows typical foot structure which is well described by the Ambegaokar-Halperin theory of thermally-activated phase slippage for overdamped Josephson junctions. The voltage-current curves with temperature dropping down to 77 K exhibit resistively shunted junction behavior, and the Josephson critical current density <i>J</i><sub>C</sub> is shown to follow the <inline-formula><tex-math id="Z-20210127094830-1">\begin{document}$(T_{\rm C}-T)^2$\end{document}</tex-math><alternatives><graphic xmlns:xlink="http://www.w3.org/1999/xlink" xlink:href="3-20201291_Z-20210127094830-1.jpg"/><graphic xmlns:xlink="http://www.w3.org/1999/xlink" xlink:href="3-20201291_Z-20210127094830-1.png"/></alternatives></inline-formula> dependence. At 77 K, the <i>J</i><sub>C</sub> of the junction reaches 1.4 × 10<sup>5</sup> A/cm<sup>2</sup>, significantly higher than the range of 10<sup>3</sup>–10<sup>4</sup> A/cm<sup>2</sup> as presented by other investigators for YBCO step-edge junctions on MgO substrate with comparable <i>θ</i> of 35°–45°. This indicates a rather strong Josephson coupling of the junction, and by invoking the results of YBCO bicrystal junctions showing similar values of <i>J</i><sub>C</sub>, it is tentatively proposed that the presently fabricated junction might be described as an S-s′-S junction with s′ denoting the superconducting region of depressed <i>T</i><sub>C</sub> in the vicinity of the step edge or as an S-N-S junction with N denoting a very thin non-superconducting layer. By incorporating the MgO-based YBCO step-edge junction, high-<i>T</i><sub>C</sub> radio frequency (RF) SQUID is made. The device shows decent voltage-flux curve and magnetic flux sensitivity of 250 <inline-formula><tex-math id="Z-20210128093740-1">\begin{document}$ \text{μ}\Phi_0/{\rm Hz}^{1/2} $\end{document}</tex-math><alternatives><graphic xmlns:xlink="http://www.w3.org/1999/xlink" xlink:href="3-20201291_Z-20210128093740-1.jpg"/><graphic xmlns:xlink="http://www.w3.org/1999/xlink" xlink:href="3-20201291_Z-20210128093740-1.png"/></alternatives></inline-formula> at 1 kHz and 77 K, comparable to the values reported in the literature. To further improve the RF SQUID performance, efforts could be devoted to optimizing the junction parameters such as the junction <i>J</i><sub>C</sub>. By using the YBCO step-edge junction on MgO substrate, high-<i>T</i><sub>C</sub> direct current SQUID could also be developed, as reported recently by other investigators, to demonstrate the potential of MgO-based step-edge junction in making such a kind of device with superior magnetic flux sensitivity.