Development of 9Cr Steels for High Temperature Steam Turbine Rotors
Authors: Mikami Masato , Miyata Takayuki , Tabuchi Masaaki , Abe Fujio
Published: March 2024

In this study, a possibility of application of advanced 9%Cr steel containing 130 ppm boron for boiler components utilized at around 650 °C to higher temperature steam turbine rotor materials has been investigated by means of reduction in silicon promoting macro-segregation in the case of large size ingots, using laboratory heats. Tempered martensitic microstructure without proeutectoid ferrite in all steels studied is obtained even at the center position of a turbine rotor having a barrel diameter of 1.2 m despite lower amounts of nitrogen and silicon. The strength at room temperature is almost the same level of practical high Cr steels such as X13CrMoCoVNbNB 9-2-1 for ultrasuper critical steam turbine rotors. The toughness is sufficient for high temperature rotors in comparison with CrMoV steels utilized as sub-critical high pressure steam turbine components. The creep rupture strength of the steels is higher than that of the conventional 9-12Cr steels used at about 630 °C. The creep rupture strength of 9%Cr steel containing 130 ppm B, 95 ppm N, 0.07 % Si and 0.05 % Mn is the highest in the steels examined, and it is therefore a candidate steel for high temperature turbine rotors utilized at more than 630 °C. Co-precipitation of M23C6 carbides and Laves phase is observed around the prior austenite grain boundaries after the heat treatments and the restraint of the carbide growth is also observed during creep exposure. An improvement in creep strength of the steels is presumed to have the relevance to the stabilization of the martensitic lath microstructure in the vicinity of those boundaries by such precipitates.
Property Analysis of Waspaloy Alloy As Bolts and Blades for 700°C Steam Turbines
Authors: Wang Yu , Sun Lingen , Yu Wenlong
Published: March 2024

Based on the research and development of Ni-based alloy of 700°C steam turbine bolts and blades worldwide, the process, microstructure, properties characteristics and strengthening mechanism of typical 700°C steam turbine bolts and blades materials Waspaloy are discussed in this study. The result shows that Waspaloy has higher elevated temperature yield strength, creep rupture strength, anti-stress relaxation property and good microstructure stability. The Waspaloy alloy could meet the design requirements of 700°C steam turbine bolts and blades.
Field and Laboratory Observations on the Steam Oxidation Behavior of Creep Strength Enhanced Ferritic Steels and Austenitic Stainless Steels
Authors: Pint B. A. , Wright I. G. , Kung S. , Shingledecker J. P.
Published: March 2024

Because of the problems experienced with steam-side oxidation in commercial power plants, there has been continuing interest in better understanding the steam oxidation behavior of creep strength enhanced ferritic steels such as grades 23, 24 and 91 as well as 300-series stainless steels such as 347H and 304H. Analysis of field-exposed tubes has provided information on the oxidation reaction products but relatively few specimens are available and there is limited information about the kinetics. Specimens have included tube sections with a shot peened surface, a treatment that is now widely used for austenitic boiler tubes. To complement this information, additional laboratory studies have been conducted in 1bar steam at 600°-650°C on coupons cut from conventional and shot-peened tubing. Exposures of 1-15 kh provide some information on the steam oxidation kinetics for the various alloys classes. While shot-peened type 304H retained its beneficial effect on oxidation resistance past 10,000 h at 600° and 625°C, the benefit appeared to decline after similar exposures at 650°C.
High Temperature Oxidation of Austenitic Steels and Nickel-Based Alloys in Steam Environment
Authors: Liang Zhiyuan , Zhao Qinxin , Singh Preet M.
Published: March 2024

Most effective method to increase the boiler efficiency and decrease emissions is to increase the steam temperature of modern coal-fired power plants. The increase in the steam temperature of the AUSC power plants will require higher grade heat-resistant materials to support the long-term safety and service reliability of power plants. The corrosion resistance of alloys is one of the most important factors for the application in AUSC power plants.
Steam Oxidation Resistance of Advanced Austenitic Steels with High Cr Content and Advanced Ni Based Alloys at High Temperatures for A-USC Coal Fired Power Plants
Authors: Dudziak T. , Sobczak N. , Sobczak J. , Deodeshmukh V. , Witkowska M. , Ratuszek W. , Chruściel K.
Published: March 2024

The A-USC technology is still under development due to limited number of materials complying with the requirements of high creep strength and high performance in highly aggressive corrosion environments. Development of power plant in much higher temperatures than A-USC is currently impossible due to the materials limitation. Currently, nickel-based superalloys besides advanced austenitic steels are the viable candidates for some of the A-USC components in the boiler, turbine, and piping systems due to higher strength and improved corrosion resistance than standard ferritic or austenitic stainless steels. The paper, presents the study performed at 800 °C for 3000 hours on 3 advanced austenitic steels; 309S, 310S and HR3C with higher than 20 Cr wt% content and 4 Ni-based alloys including: two solid-solution strengthened alloys (Haynes 230), 617 alloy and two (γ’) gamma - prime strengthened materials (263 alloy and Haynes 282). The high temperature oxidation tests were performed in water to steam close loop system, the samples were investigated analytically prior and after exposures using Scanning Electron Microscopy (SEM) coupled with Energy Dispersive Spectrometry (EDS), and X-Ray Diffractometer (XRD). Mass change data have been examined every 250 hours.
Fireside Corrosion and Steamside Oxidation Behavior of HAYNES 282 Alloy for A-USC Applications
Authors: Deodeshmukh V. P. , Pint B. A.
Published: March 2024

The Advanced Ultrasupercritical (A-USC) power plants are aimed to operate at steam inlet temperatures greater than 700°C; consequently, a complete materials overhaul is needed for the next-generation power plants. HAYNES 282, a gamma-prime strengthened alloy, is among the leading candidates because of its unique combination of properties, superior creep and LCF strength, fabricability and thermal stability. It is currently being evaluated in wrought and cast forms for A-USC turbine rotors, casings, boiler tubings, header, and valves. The candidate materials for A-USC applications not only require oxidation resistance for steam cycles but fireside corrosion resistance to coal ash is also of an extreme importance. In order to study the effect of both environments on the performance of 282 alloy, the alloy was exposed for extended periods in various oxidizing environments, such as air, air plus water vapor (10%), and 17bar steam up to 900°C. The fireside corrosion resistance of 282 alloy was evaluated at 700°C in synthetic coal ash and at 843°C in alkali salt deposits in a controlled gaseous environment.
Supercritical Water Oxidation and Creep Behaviour of Boiler Tube Materials
Authors: Tuurna Satu , Pohja Rami , Yli-Olli Sanni , Penttilä Sami
Published: March 2024

High efficiency in power generation is not only desirable because of economical reasons but also for enhanced environmental performance meaning reduced quantity of forming ash and emissions. In modern medium to large size plants, improvements require supercritical steam values. Furthermore, in future there will be an increasing share of renewables, such as wind and solar power, which will enhance the fluctuation of supply with the consequence that other power sources will have to compensate by operating in a more demanding cyclic or ramping mode. The next generation plant will need to operate at higher temperatures and pressure cycles coupled with demanding hot corrosion and oxidation environments. Such an operation will significantly influence the performance of materials used for boilers and heat exchanger components by accelerating oxidation rates and lowering mechanical properties like creep resistance. The paper discusses the oxidation behaviour of San25, 800H and alloy 263 in supercritical water at temperatures 650 and 700 °C at 250 bar, and compares the changes of mechanical properties of materials at these temperatures.
Creep Rupture Strength of Dissimilar CB2-P92 FCW Joint Welds
Authors: Baumgartner Susanne , Pahr Hannes , Schnitzer Ronald
Published: March 2024

As flux cored wires for gas metal arc welding offer several technical and economic advantages they are becoming more and more popular. Matching flux cored wires for welding P92 have already been available for several years. A matching flux cored wire for welding the Co-alloyed cast steel CB2, which is used for turbine and valve casings operating at steam temperatures of up to 620°C, was developed recently. To connect casings with P92 pipes, dissimilar welding of CB2 to P92 is necessary. This can be done with filler metal that matches either CB2 or P92. Pre-tests have confirmed that flux cored arc welding (FCAW) can generally be used for dissimilar joint welding of CB2 to P92. To evaluate creep rupture strength dissimilar welds were performed with filler metal matching CB2 and P92, respectively. TIG welding was used for the root and the second pass and FCAW for the intermediate and final passes. Cross-weld tensile tests, side bend tests and impact tests of weld metals and heat-affected zones were carried out at ambient temperatures after two post-weld heat treatments (PWHT), each at 730°C for 12 hours. Creep rupture tests of cross-weld samples were performed at 625°C. This study compares the results of the mechanical tests at ambient temperature and the creep rupture tests, and discusses why P92 filler metals are preferred for such welds.
Inspection and Evaluation of Defects on the Welds of P92 Header
Authors: He Xipeng , Ma Hong , Wang Fugui , Zhang Baozhu , Cui Jinwen , Cao Haitao
Published: March 2024

The inspection and evaluation of defects in the welds of P92 high temperature reheater header with a diameter of about 1000mm and a wall thickness of about 100 mm have been done by means of hardness test, nondestructive testing on the surface, ultrasonic testing, metallographic and component sampling. By analyzing the results of on-site test and samples removed from the component, it is found that cracks existing in the welds are hydrogen induced delayed cracks. During the welding process and post-heating treatment (hydrogen bake-out), dehydrogenation was insufficient. This fact, combined with welding residual stresses resulted in the observed hydrogen induced cracking.
Thor115 Welding Experience
Authors: Jones D. , Ortolani M. , Mariani P. , Baietta S. , Yamamoto Y.
Published: March 2024

A new martensitic steel was developed for power generation applications. Tenaris High Oxidation Resistance (Thor) is an evolution of Grade 91, designed to have improved steam oxidation resistance and better long-term microstructural stability, with equal or better creep strength. Based on consolidated metallurgical knowledge of microstructural evolution mechanisms, and extensive development performed in the last decade, Thor was engineered to overcome temperature limitations of Grade 91, yet it can be processed in the same fashion, permitting the use of existing best practices for Grade 91 boiler fabrication. Welding trials were performed on Thor tubes and pipe using welding procedures that are routinely employed in the construction of Grade 91 steel components. A summary of relevant results is presented, demonstrating the applicability of long-established and tested welding procedures to components manufactured with Thor steel.
Evaluation of Hardness Levels of T24 Boiler Tube Butt Welds Regarding SCC Susceptibility in High Temperature Water
Authors: Unterumsberger Fabian , Bernds Dietrich , Pohl Michael
Published: March 2024

In Europe between 2006 and 2012 several ultra-super-critical (USC) coal-fired power plants were built employing T24 (7CrMoVTiB10-10 / DIN EN 10216-2:2014-03 / VdTÜV sheet 533/2) in membrane walls. During commissioning stress corrosion cracking (SCC) on the tube-to-tube butt welds appeared. The widespread damages required the development of a new patented commissioning procedure to avoid recurring damages. Although this commissioning procedure was employed successfully and the power plants are in operation since then, a debate about the implementation of a hardness limit for such butt welds was initiated. According to the European standards butt welds of T24 boiler tubes with wall thickness < 10 mm (0.3937 in) do not require any post-weld heat treatment (PWHT) and no hardness limits are given. When looking at manufacturing related issues such as an imminent risk of cold cracking after welding of micro-alloyed steels a widely applied but coarse hardness limit is 350 HV. Based on laboratory tests, some authors reallocated this 350 HV hardness limit for addressing SCC susceptibility of low-alloyed steels. This article describes typical hardness levels of T24 boiler tube TIG butt welds and the SCC behavior in high temperature water. Further the effect of the stress relief heat treatment (SRHT) of the boiler membrane walls between 450 °C and 550 °C (842 °F and 1022 °F) on its hardness values and on the SCC behavior is discussed, showing that the hardness values should not be used as an indicator for SCC susceptibility of T24 boiler tube butt welds.
Environmental Assisted Cracking of Alloy T24 in Oxygenated High-Temperature Water
Authors: Devrient Bastian , Kilian Renate , Unterumsberger Fabian , Bernds Dietrich
Published: March 2024

During commissioning of recently built modern, and highly efficient coal-fired power plants, cracks were detected after very short time of operation within the welds of membrane walls made from alloy T24. The root cause analysis revealed transgranular and mostly intergranular cracks adjacent to the heat affected zone beside weld joints. At that time, the degradation mechanism was rather unclear, which led to an extended root cause analysis for clarification of these failures. The environmentally assisted cracking behavior of alloy T24 in oxygenated high-temperature water was determined by an experimental test program. Hereby, the cracking of 2½% chromium steel T24 and 1% chromium steel T12 were determined in high-temperature water depending on the effect of water chemistry parameters such as dissolved oxygen content, pH, and temperature, but also with respect to the mechanical load component by residual stresses and the microstructure. The results clearly show that the cracking of this low-alloy steel in oxygenated high-temperature water is driven by the dissolved oxygen content and the breakdown of the passive corrosion protective oxide scale on the specimens by mechanical degradation of the oxide scale as fracture due to straining. The results give further evidence that a reduction of the residual stresses by a stress relief heat treatment of the boiler in combination with the strict compliance of the limits for dissolved oxygen content in the feed water according to water chemistry standards are effective countermeasures to prevent environmentally assisted cracking of T24 membrane wall butt welds during plastic strain transients.
Influence of Aluminum Diffusion Layer on T/P92 Steam Oxidation Resistance - A Laboratory and Field Study
Authors: Allenou J. , Pirón-Abellán J. , Hugon E. , Landier C. , Le Guevel Th.
Published: March 2024

The steam oxidation behaviour of boiler tubes and steam piping components is a limiting factor for improving the efficiency of the current power plants. Spallation of the oxide scales formed during service can cause serious damage to the turbine blades. Vallourec has implemented an innovative solution based on an aluminum diffusion coating applied on the inner surface of the T/P92 steel. The functionality of this coating is to protect the tubular components against spallation and increase the actual operating temperature of the metallic components. In the present study, the newly developed VALIORTM T/P92 product was tested at the EDF La Maxe power plant (France) under 167b and 545°C (steam temperature). After 3500h operation, the tubes were removed and characterized by Light Optical Metallography (LOM), Scanning Electron Microscopy (SEM), with Energy Dispersive X-ray spectrometry (EDX) and X-Ray Diffraction (XRD). The results highlight the excellent oxidation resistance of VALIORTM T/P92 product by the formation of a protective aluminum oxide scale. In addition, no enhanced oxidation was observed on the areas close to the welds. These results are compared with the results obtained from laboratory steam oxidation testing performed on a 9%Cr T/P92 steel with and without VALIORTM coating exposed in Ar-50%H2O at 650°C.
Investigating Effects of Variations in Heat Treatment Parameters on Performance of CSEF Welds
Authors: Doubell P , Bezuidenhout M E J , Knutsen R D , Westraadt J
Published: March 2024

There is a constant need for improved knowledge of the influence of non-standard processing on the expected performance of creep strength enhanced ferritic (CSEF) materials as the total installed tonnage of these materials is rapidly increasing across the power generation industry. Cr-Mo-V steel grades micro-alloyed with niobium and titanium designed for pressurized equipment operating in the supercritical steam range proved to be very sensitive to relative minor variations in the principal heat treatment parameters time and temperature, when compared to the traditional Cr-Mo-V grades. A key component for successful welds is optimised post weld heat treatment (PWHT). Under certain conditions premature failures of welds can occur when incorrect weld and heat treatment performance result in a reduction of specified mechanical properties and high temperature creep performance, it is therefore of significant importance to have a good understanding of actual material properties for effective operation and plant life studies. This study investigated the effect and impact variations of post weld heat treatment time and temperature on mechanical properties of tungsten inert gas (TIG) and manual metal arc (MMA) welds on Grade 91 pipes from a set of reference samples. This is in preparation of establishing a benchmark set of tests to determine the integrity and expected long-term performance of butt-welds from limited site sample volumes, providing a non-intrusive methodology to identify welds suspected to have received non-standard PWHT cycles on Grade 91 pipework systems.
Experimental Study of the Creep Performance of Creep Strength Enhanced Ferritic Steel Weldments
Authors: Yu Xinghua , Feng Zhili
Published: March 2024

Fossil fuels continue to be the primary source of energy in the U.S and worldwide. In order to improve the efficiency of fossil power plants, advanced structural materials need to be developed and deployed to meet the need of high temperature creep resistance and corrosion resistance. Examples include creep strength enhanced ferritic (CSEF) steels, austenitic stainless steels, nickel-based superalloys, and oxide dispersion strengthened alloys. Welding is extensively used in construction of fossil power plants. The performance of the weld region can be critical to the safe and economical operation of fossil power plants. Degradations in performance such as reduced creep strength and premature failure in the weld region (e.g. Type IV failure in ferritic steels) are examples of longstanding welding and weldability problems for boiler and other components. In the past, extensive studies have been carried out to characterize the different microstructures in different regions of a weld, and to a certain extent, to establish the correlations between the microstructure and the creep strength. However, the metallurgical or microstructural induced local stress/strain variations have been seldom quantified. In addition, it has been long recognized that, due to the sharp microstructure and property gradients in the weld and HAZ, the standard creep testing procedure for the base metal can produce erroneous results when used for weld testing.
Micromechanics of Co-Nb Laves Phases: Strength, Fracture Toughness, and Hardness as Function of Composition and Crystal Structure
Authors: Luo W. , Kirchlechner C. , Dehm G. , Stein F.
Published: March 2024

Laves phases are intermetallic phases well known for their excellent strength at high temperatures but also for their pronounced brittleness at low temperatures. Especially in high-alloyed steels, Laves phases were long time regarded as detrimental phases as they were found to embrittle the material. Perusing the more recent literature, it seems the negative opinion about the Laves phases has changed during the last years. It is reported that, if the precipitation morphology is properly controlled, transition metal-based Laves phases can act as effective strengthening phases in heat resistant steels without causing embrittlement. For a targeted materials development, the mechanical properties of pure Laves phases should be known. However, the basic knowledge and understanding of the mechanical behavior of Laves phases is very limited. Here we present an overview of experimental results obtained by micromechanical testing of single-crystalline NbCo2 Laves phase samples with varying crystal structure, orientation, and composition. For this purpose, diffusion layers with concentration gradients covering the complete homogeneity ranges of the hexagonal C14, cubic C15 and hexagonal C36 NbCo2 Laves phases were grown by the diffusion couple technique. The hardness and Young's modulus of NbCo2 were probed by nanoindentation scans along the concentration gradient. Single-phase and single crystalline microcantilevers and micropillars of the NbCo2 Laves phase with different compositions were cut in the diffusion layers by focused ion beam milling. The fracture toughness and the critical resolved shear stress (CRSS) were measured by in-situ microcantilever bending tests and micropillar compression tests, respectively. The hardness, Young's modulus and CRSS are nearly constant within the extended composition range of the cubic C15 Laves phase, but clearly decrease when the composition approaches the boundaries of the homogeneity range where the C15 structure transforms to the off stoichiometric, hexagonal C36 and C14 structure on the Co-rich and Nb-rich, respectively. In contrast, microcantilever fracture tests do not show this effect but indicate that the fracture toughness is independent of crystal structure and chemical composition of the NbCo2 Laves phase.
In Situ Measurement of Particulate Erosion Damage on Additively Manufactured IN718
Authors: Fry A.T. , Nunn J. , Gee M.G. , Orkney L.
Published: March 2024

The measurement of damage from high temperature solid particle erosion (HTSPE) can be a lengthy process within the laboratory with many lab-based systems requiring sequential heat and cooling of the test piece to enable mass and/or scar volume measurements to be made ex situ. Over the last few years a new lab-based system has been in development at the National Physical Laboratory which has the ability to measure the mass and volume change of eroded samples in situ without the need to cool the sample. Results have previously been shown demonstrating the in situ mass measurement, more recently the in situ volume measurement capability has been added and used to evaluate the erosion performance of additively manufactured materials. Selective laser melting (SLM) is an advanced manufacturing method which is growing in popularity and application. It offers the ability to manufacture low volume complex parts and has been used in rapid prototyping. As the technique has developed there is increasing interest to take advantage of the ability to manufacture complex parts in one piece, which in some case can be more cost and time effective than traditional manufacturing routes. For all the benefits of SLM there are some constraints on the process, these include porosity and defects in the materials such as ‘kissing bonds’, surface roughness, trapped powder and microstructural variation. These features of the processing route may have implications for component performance such as strength, fatigue resistance wear and erosion. To investigate this further SLM IN718 has been used to evaluate factors such as surface roughness, microstructure and morphology on the erosion performance as measured in situ and compared with conventional produced wrought IN718 material.
Improvement in Creep and Steam Oxidation Resistance of Precipitation Strengthened Ferritic Steels
Authors: Yoshiaki Toda , Yoko Yamabe-Mitarai , Akihiko Kaseya , Osamu Umezawa
Published: March 2024

To save fossil fuel resources and to reduce CO2 emissions, considerable effort has been directed toward researching and developing heat-resistant materials that can help in improving the energy efficiency of thermal power plants by increasing their operational temperature and pressure conditions. Instead of conventional 9-12Cr ferritic heat-resistant steels with a tempered martensitic microstructure, we developed “Precipitation Strengthened 15Cr Ferritic Steel” based on a new material design concept: a solid-solution treated ferrite matrix strengthened by precipitates. Creep tests for 15Cr-1Mo-6W-3Co-V-Nb steels with ferrite matrix strengthened by a mainly Laves phase (Fe2W) showed that the creep strengths of 15Cr ferritic steel at temperatures ranging from 923 K to 1023 K were twice as high as those of conventional 9Cr ferric heat-resistant steel. 15Cr steels have higher steam oxidation resistance than that of conventional steel in the same temperature range as the creep tests. Thus, the new material design concept of heat-resistant steel pro- vides improved creep strength and steam oxidation resistance. We are attempting to determine the optimum compositions, especially that of carbon, in order to improve the high-temperature creep strength.
Creep Behavior and Microstructure of a Prospective Re-Containing 10%Cr-3%Co-3%W Martensitic Steel
Authors: Fedoseeva Alexandra , Nikitin Ivan , Dudova Nadezhda , Kaibyshev Rustam
Published: March 2024

9-10%Cr-3%Co martensitic steels are the prospective materials for elements of boilers, tubes and pipes for fossil power plants which are able to work at ultra-supercritical parameters of steam (T=620-650°C, P=25-30 MPa). The effect of creep on the microstructure of the 10 wt.%Cr-3Co- 3W-0.2Re martensitic steel was investigated in the condition of 650°C and an applied stress of 140 MPa, time to rupture was more than 8500 h. Previously, this steel was subjected to the normalizing at 1050°C and tempering at 770°C. This heat treatment provided the hierarchical tempered martensite lath structure with the mean size of prior austenite grains of 59 μm and with high dislocation density (2×1014 m-2) within martensitic laths. Boundary M23C6 and M6C carbides and randomly distributed within matrix Nb-rich MX carbonitrides were detected after final heat treatment. The addition of Re in the steel studied positively affected creep at 650°C/140 MPa and stabilized the tempered martensite lath structure formed during 770°C-tempering. The formation of the subgrains in the gage section was accompanied by the coarsening of M23C6 carbides and precipitations of Laves phase with fine sizes during creep. No depletion of Re and Co from the solid solution during creep was revealed whereas W content decreased from 3 to 1 wt.% for first 500 h of creep. Reasons of improved creep as well as mechanisms of grain boundary pinning by precipitates are discussed.
On the Precipitation of the Laves Phase Particles in a Martensitic 10% Cr-3% Co-3% W-0.2% Re Steel during Creep at 650°C
Authors: Nikitin Ivan , Fedoseeva Alexandra , Dudova Nadezhda , Kaibyshev Rustam
Published: March 2024

The size and distribution of the Laves phase particles in a 9.85Cr-3Co-3W-0.13Mo-0.17Re- 0.03Ni-0.23V-0.07Nb-0.1C-0.002N-0.008B steel subjected to creep rupture test at 650°C under an applied stresses of 160-200 MPa with a step of 20 MPa were studied. After heat treatment consisting of normalizing of 1050°C and tempering of 770°C, M23C6 and Fe3W3C carbides with the mean sizes of 67±7 and 40±5 nm, respectively, were revealed along the boundaries of prior austenite grains and martensitic laths whereas round NbX carbonitrides were found within martensitic laths. During creep metastable Fe3W3C carbides dissolved and the stable Laves phase particles precipitated; volume fraction of Laves phase increases with time. The Laves phase particles nucleated on the interfacial boundaries Fe3W3C/ferrite during first 100 h of creep and provided effective stabilization of tempered martensitic lath structure until their mean size less than 150 nm.
The Influence of Weld Thermal Cycle Simulations on the Microstructure of VM12-SHC Steel
Authors: Byrne R.G. , Jepson M.A.E. , Thomson R.C. , Shingledecker J.P. , Siefert J.A.
Published: March 2024

For VM12-SHC 11-12 wt. % Cr steel, there have been no systematic investigations to define the regions or characterise the microstructures within the heat-affected zone (HAZ) of weldments. In similar steels, these regions relate to the Ac1 and Ac3 transformation temperatures and can affect weldment performance. In this study, controlled thermal cycles were applied to VM12-SHC parent metal using a dilatometer and the Ac1 and Ac3 temperatures were measured for various heating rates. The Ae1 and Ae3 temperatures were also calculated by thermodynamic equilibrium modeling. Through dilatometry, thermal cycles were then applied to simulate the microstructures of the classically defined HAZ regions. The microstructural properties of each simulated material were investigated using advanced electron microscopy techniques and micro-hardness testing. It was found that the simulated HAZ regions could be classified as; (1) the completely transformed (CT) region, with complete dissolution of pre-existing precipitates and complete reaustenitisation; (2) the partially transformed (PT) region, exhibiting co-existing original martensite with nucleating austenite microstructures with partial dissolution of precipitates; and (3) the over tempered (OT) region, with no phase transformation but precipitate coarsening and decreased hardness.
High Temperature Oxidation Behavior of High Nitrogen Ferritic Steels
Authors: Masuyama Fujimitsu , Matsubara Shoichi , Tonoe Yu , Yamaguchi Tomiko
Published: March 2024

For last half century the development of creep strength enhanced ferritic steels has been continued and presently ASME grades 91, 92 and 122 extremely stronger than conventional low alloy steels have extensively been used worldwide in high efficient power plants. However the use of these creep strength enhanced 9-12%Cr steels is limited to around 630°C or 650°C at maximum in terms of high temperature strength and oxidation resistance. Consequently the appearance of ferritic steels standing up to higher temperature of around 700°C to substitute of high strength austenitic steels is strongly desired. Under the state, the addition of high nitrogen to ferritic steels is attracting considerable attention because of improving high temperature strength and oxidation resistance of them. This work was done to evaluate the oxidation resistance of high nitrogen steels and to investigate the effect nitrogen and microstructure on oxidation resistance using 9-15%Cr steels with about 0.3% nitrogen manufactured by means of Pressurized Electro- Slag Remelting (PESR) method in comparison with ASME grades 91 and 122. As a result, high nitrogen ferritic steels showed excellent oxidation resistance comparing with nitrogen-free steels and ASME grades 91 and 122. The oxidation resistance of 9%Cr ferritic steels depends on the nitrogen content in the each steel. That is, the weight gain decreases with an increase in nitrogen content. Moreover, the oxide scale of high nitrogen steel contained a high concentration of Cr. It is conjectured that, in high temperature oxidation, nitrogen plays a key role in promoting the formation of the oxide scale which has high concentration of Cr, inhibiting oxidation from proceeding. And also it was found that the oxidation resistance of the high nitrogen steels does not depend greatly on Cr content but on their microstructure. The oxidation resistance of high nitrogen ferritic heat-resistant steels increased as the fraction of martensite structure increased. These results indicate for high nitrogen steels Cr diffusion along grain boundaries is further promoted resulting in the formation of protective oxide scale having high Cr concentration. Furthermore as new findings it was confirmed that the Cr diffusion in substrate of steels to form Cr concentrated oxide scale on the metal surface is accelerated by nitrogen while suppressed by carbon in matrix of steel.
A Standardized Approach for the Quantification of Microstructure in 9Cr Steels
Authors: West Geoff D , Jabar Sharhid , Shollock Barbara , Lolla Tapasvi , Siefert John
Published: March 2024

In order to understand the microstructural evolution during service that 9Cr steels experience it is important to be able to quantify key microstructural parameters that define the characteristics of the secondary phases (e.g. precipitated phases and inclusions) and the steel matrix. The average size of M23C6, Laves phase and MX particles in these materials have been reported in many studies, however comparability between these studies is compromised by variations in technique and different/incomplete reporting of procedure. This paper provides guidelines on what is required to accurately measure these parameters in a reproducible way, taking into account macro-scale chemical heterogeneities and the statistical number of particles required to make meaningful measurements. Although international standards do exist for inclusion analysis, these standards were not developed to measure the number per unit area of hard particles that can act as creep cavity nucleation sites. In this work a standardized approach for measuring inclusions from this perspective is proposed. In addition the associated need to understand the segregation characteristics of the material are described, which in addition to defining the area that needs to be analysed to measure the average number of inclusions per unit area, also allows the maximum number of inclusions per unit area to be determined, a parameter which is more likely to define the damage tolerance of the material.
Pre-Straining Effect on the Creep Behavior of Impression Creep Tests for a P91 Steel at 600 °C
Authors: Brett SJ , Dyson C , Maskill S , Sun W , Bridges A
Published: March 2024

This paper investigates the effect of high temperature tensile strain on subsequent creep strength in grade 91 steel. Failed hot tensile specimens have been sectioned at various positions along the specimen axis, and therefore at different levels of hot tensile strain, to obtain material for creep strength evaluation. Because of the limited amount of material available for creep testing obtained in this way, creep testing has been carried out using the specialised small-scale impression creep testing technique. The grade 91 material has been tested in both the normal martensitic condition and in an aberrant mis-heat treated condition in which the microstructure is 100% Ferrite. The latter condition is of interest because of its widespread occurrence on operating power plant with grade 91 pipework systems.
Microstructurally Based Modeling of Creep Deformation of Martensitic Steels
Authors: Sonderegger Bernhard , Riedlsperger Florian , Krenmayr Bernhard , Fercher Bernhard , Niederl Bernd , Sommitsch Christof
Published: March 2024

This work deals with the potential of microstructurally based modeling of the creep deformation of martensitic steels. The motivation for the work stems from the ever increasing demand for higher efficiency and better reliability of modern thermal power plants. Service temperatures of 600°C and stress levels up to 100 MPa are currently the typical requirements on critical components. High creep and oxidation resistance are the main challenges for a lifetime 10+ years in steam atmosphere. New materials may fulfill these requirements; however, the save prediction of the creep resistance is a difficult challenge. The model presented in this work takes into consideration the initial microstructure of the material, its evolution during thermal and mechanical exposure and the link between microstructural evolution and creep deformation rate. The model includes the interaction between the relevant microstructural constituents such as precipitates, grain- lath- and subgrain boundaries and dislocations. In addition, the material damage is included into the model. The applicability of the model is then demonstrated on standard creep resistant alloys. Contrary to phenomenological models, this approach can be tested against microstructural data of creep loaded samples and thus provides higher reliability. Nevertheless, potential improvements are discussed and future developments are outlined.
A Summary of 10 Years Research on Grade 91 and Grade 92 Steel
Authors: Takahashi Yukio , Shigeyama Haruhisa , Siefert John , Parker Jonathan
Published: March 2024

In response to the strong needs for the life assessment of various components in fossil power plants, studies on Grade 91 and Grade 92 steels have been jointly performed by EPRI and CRIEPI for a last decade. These studies have been covering the effects of load variation (creep- fatigue) and stress multiaxiality as well as the behavior under uniaxial creep conditions. Based on abundant test data accumulated in this period and associated analytical evaluation, approaches based on inelastic strain energy have been developed for accurately assessing creep damage and failure lives under various conditions. The essence of these efforts is presented in this paper.
High Temperature Properties of Ni-38-Cr-3.8Al with High Hardness and High Hot Corrosion Resistance
Authors: Koyanagi Yoshihiko , Takabayashi Hiroyuki , Yasuda Hiroyuki Y.
Published: March 2024

Ni-38Cr-3.8Al has high hardness and high corrosion resistance with good hot workability, and therefore, it has been applied on various applications. However, in order to expand further application, it is important to understand the high temperature properties. Then, this study focused on the high temperature properties such as thermal phase stability, hardness, tensile property, creep property and hot corrosion resistance. As the result of studies, we found that the thermal phase stability of (γ/α-Cr) lamellar structure and the high temperature properties were strongly influenced by the temperature. Although the high temperature properties, except for creep property, of Ni-38Cr-3.8Al were superior to those of conventional Ni-based superalloys, the properties were dramatically degraded beyond 973 K. This is because the lamellar structure begins to collapse around 973 K due to the thermal stability of the lamellar structure. The hot corrosion resistance of Ni-38Cr-3.8Al was superior to that of conventional Ni-based superalloys, however, the advantage disappeared around 1073 K. These results indicate that Ni-38Cr-3.8Al is capable as a heat resistant material which is required the hot corrosion resistance rather than a heat resistant material with high strength at high temperature.
Effect of Temperature on Fracture Toughness of Inconel 617B Superalloy Welded Joint
Authors: Li Xiaogang , Li Kejian , Li Shanlin , Pan Jiluan , Cai Zhipeng
Published: March 2024

In the present study, the Inconel 617B superalloy welded trial rotor was fabricated by narrow gap tungsten inert gas (NG-TIG) welding and the effects of temperature on fracture toughness of its welded joint were investigated at 650 ℃ and 730 ℃. Fracture toughness (J0.2) of the base metal was much higher than that of the weld metal at the same temperature, which was attributed to its excellent macroscopical plasticity and the interactions of strain localization, misorientation, and coincidence site lattice (CSL) boundaries. For the base metal, the value of J0.2 was higher at 730 ℃ than at 650 ℃, resulting from the appreciable increase in ductility and decrease in strain localization as the temperature increased. For the weld metal, higher temperature (730 ℃) reduced strength but hardly improved plasticity, and the regions of high strain localization uniformly distributed in the weld metal, resulting in completely tearing the whole interface apart and lower fracture toughness of the weld metal.
Effect of Prior Particle Boundary on Deformability of Powder Processed Turbine Disk Alloy
Authors: Kanno Naoya , Higashi Masaya , Ozaki Tomomichi , Tsuno Nobuyasu , Yamane Koshiro , Takahashi Satoshi
Published: March 2024

The powder metallurgy (P/M) process has been applied to a high strength turbine disk alloy. It is known that P/M alloys show characteristic microstructures such as prior powder boundaries (PPB) compared to microstructures of conventional cast and wrought (CW) alloys. High temperature tensile tests were conducted on CW and P/M processed alloy720Li in order to reveal the effect of temperature and strain rate on deformation behavior and to demonstrate the effect of microstructure derived from P/M process on deformability. The fracture mode of the P/M material changed from grain interior fracture to fracture around large PPB with an increment of strain rate. In addition, samples ruptured at higher temperature showed grain boundary fracture regardless of strain rate. On the other hand, the CW material showed good deformability with chisel point fracture in the entire temperature and strain rate condition range. In the P/M material, melting of grain boundaries occurred at super solvus temperature conditions. Large PPB acts as nucleation site of voids at higher strain rate conditions. Precipitation strengthening by γ’ phase degrades deformability at sub solvus temperature conditions. However, deformability near the solvus temperature and low strain rate condition in as HIPed P/M material increased with fine grain size distribution in spite of the presence of large grains resulting from PPB.
Effects of Phosphorus Addition on the Creep Behavior and Microstructure of Wrought γ′-Strengthened Ni-Based Superalloys
Authors: Hasebe Y. , Yoshida M. , Maeda E. , Ohsaki S.
Published: March 2024

In this work, the effects of phosphorus addition on the creep properties and microstructural changes of wrought γ’-strengthened Ni-based superalloys (Haynes 282) were investigated, focusing on the effects of carbides precipitation. In an alloy with a phosphorus content of 8 ppm, precipitation of M23C6 carbides was observed in both grain boundaries and the grain interior prior to the creep tests. Grain boundary coverage by carbide increased with phosphorus content up to approximately 30 ppm. On the other hand, the amount of M23C6 in the grain interior decreased with phosphorus content. The results of the creep tests revealed the relationship between the time to rupture and the grain boundary coverage by carbides. The microstructure of the crept specimens showed the existence of misorientation at the vicinity of grain boundaries without carbides, as demonstrated via electron backscattered diffraction (EBSD) analysis. These results suggest that the observed improvement in the time to rupture is due to a grain-boundary precipitation strengthening mechanism caused by grain boundary carbides and that phosphorus content affects the precipitation behavior of M23C6 carbides in the grain interior and grain boundaries. These behaviors were different between alloys with the single addition of phosphorus and alloys with the multiple addition of phosphorus and niobium.
Effect of Cold Working on Oxidation Assisted Cracking Behaviors on Alloy 718
Authors: Sueishi Yuichiro
Published: March 2024

This study aims to examine the effects of grain boundary oxidation and creep on crack initiation and fracture behaviors in cold worked surface layer, under static tensile stresses in air. To determine these effects in relation to percent cold work and hardness scale, cold-rolled plates with a reduction ratios between 10% and 50% were prepared. Uniaxial constant load (UCL) tests were conducted at elevated temperature in air using smooth round bar specimen. UCL tests with a load of 0.9σy (926MPa) at 550°C show that rupture time for all cold- rolled materials were shorter than that of as-received material. From cross-sectional observation after UCL testing, surface crack at grain boundary and voids were observed in as-received material, whereas creep cracks were also observed in cold-rolled materials. This implied that crack initiation was assisted by cold working. Comparing test results with a load reduced to 0.8σy (823MPa), difference of rupture time was expected as a factor of 5 for as-received material, and measured as 2-3 for cold-rolled materials. It was suggested that cold worked layer was more sensitive to creep than base metal.
Creep Strength and Microstructure of Ni-Base Alloys for Advanced USC Boiler Tubes and Pipes
Authors: Semba Hiroyuki , Okada Hirokazu , Hamaguchi Tomoaki , Kurihara Shinnosuke , Tanaka Katsuki
Published: March 2024

Development of the advanced USC (A-USC) boiler technology has been promoted in recent years, which targets 700°C steam condition. HR6W (Ni-23Cr-7W-Ti-Nb-25Fe) and HR35 (Ni-30Cr-6W-Ti-15Fe) have been developed for A-USC boiler tubes and pipes. The former alloy is mainly strengthened by Fe2W type Laves phase. The latter one employs precipitation strengthening of α-Cr phase in addition to Laves phase. Characteristic alloy design of both alloys, which does not use precipitation strengthening of γ′ phase (Ni3Al), leads to superior ductility and resistance to stress-relaxation cracking. Stability of creep strength and microstructure has been confirmed by long-term creep rupture tests. The 100,000h average creep rupture strength of HR6W is 85MPa at 700C. That of HR35 is 126MPa at 700°C which is comparable with conventional Alloy617. Tubes of both alloys have been evaluated by the component test in Japanese national A-USC project with γ′ hardened Alloy617 and Alloy263. Detailed creep strength, deformation behavior and microstructural evolution of these alloys are described from the viewpoint of the difference in strengthening mechanisms. Capability of these alloys for A-USC boiler materials has been demonstrated by the component test in the commercial coal fired boiler as the part of the A-USC project.
Crystal Plasticity Mechanism of the Transition Behavior from Opening to Shearing Cracking in a Nickel-Based Single Crystal Superalloy
Authors: Sakaguchi Motoki , Chen Xiaosheng , Kitahara Yu , Inoue Hirotsugu
Published: March 2024

In this study, fatigue crack propagation behavior at lower temperature in single crystal nickel-base superalloys was investigated experimentally and analytically. Four types of compact specimens with different combinations of crystal orientations in loading and crack propagation directions were prepared, and fatigue crack propagation tests were conducted at room temperature and 450°C. It was revealed in the experiments that the crack propagated in the shearing mode at room temperature, while the cracking mode transitioned from the opening to shearing mode at 450°C. Both the crack propagation rate and the transition behavior were strongly influenced by the crystallographic orientations. To interpret these experimental results, crystal plasticity finite element analysis was carried out, taking account some critical factors such as elastic anisotropy, crystal orientations, 3-D geometry of the crack plane and the activities of all 12 slip systems in the FCC crystal. A damage parameter based on the slip plane activities derived from the crystal plasticity analysis could successfully rationalize the effect of primary and secondary orientations on the crystallographic cracking, including the crack propagation paths and crack propagation rates under room temperature. The proposed damage parameter could also explain the transition from the opening to crystallographic cracking observed in the experiment under 450°C.