Study and evaluation of a gelatin- silver oxide nanoparticles releasing nitric oxide production of wound healing dressing for diabetic ulcer
Authors: Li Xian , Jiang Xin , Gao Fei , Zhou Lifeng , Wang Guosheng , Li Bingfa , Gu Shihao , Huang Wei , Duan Hongkai 
Published: June 2024

This study aimed to develop a novel Gelatin silver oxide material for releasing nitric oxide bionanocomposite wound dressing with enhanced mechanical, chemical, and antibacterial properties for the treatment of diabetic wounds. The gelatin- silver oxide nanoparticles (Ag2O-NP) bio nanocomposite was prepared using chitosan and gelatin polymers incorporated with silver oxide nanoparticles through the freeze-drying method. The samples were characterized using scanning electron microscopy (SEM) and X-ray diffraction (XRD) analysis. Results showed that the Ag2O-NP nanoparticles increased porosity, decreased pore size, and improved elastic modulus. The Ag2O-NP wound dressing exhibited the most effective antibacterial properties against Staphylococcus aureus and Escherichia coli. Among the samples, the wound dressing containing silver oxide nanoparticles demonstrated superior physical and mechanical properties, with 48% porosity, a tensile strength of 3.2 MPa, and an elastic modulus of 51.7 MPa. The fabricated wound dressings had a volume ratio of empty space to total volume ranging from 40% to 60%. In parallel, considering the complications of diabetes and its impact on the vascular system, another aspect of the research focused on developing a per2mediated wound dressing capable of releasing nitric oxide gas to regenerate damaged vessels and accelerate diabetic wound healing. Chitosan, a biocompatible and biodegradable polymer, was selected as the substrate for the wound dressing, and beta-glycerophosphate (GPβ), tripolyphosphate (TPP), and per2mediated alginate (AL) were used as crosslinkers. The chitosan-alginate (CS-AL) wound dressing exhibited optimal characteristics in terms of hole count and uniformity in the scanning electron microscope test. It also demonstrated superior water absorption (3854%) and minimal air permeability. Furthermore, the CS-AL sample exhibited an 80% degradation rate after 14 days, indicating its suitability as a wound dressing. The wound dressing was loaded with S-nitrosoglutathione (GSNO) powder, and the successful release of nitric oxide gas was confirmed through the grease test, showing a peak at a wavelength of 540 nm. Subsequent investigations revealed that the treatment of human umbilical vein endothelial cells (HUVECs) with high glucose led to a decrease in the expression of PER2 and SIRT1, while the expression of PER2 increased, which may subsequently enhance the expression of SIRT1 and promote cell proliferation activity. However, upon treatment of the cells with the modified materials, an increase in the expression of PER2 and SIRT1 was observed, resulting in a partial restoration of cell proliferative activity. This comprehensive study successfully developed per2-mediated bio-nanocomposite wound dressings with improved physical, mechanical, chemical, and antibacterial properties. The incorporation of silver oxide nanoparticles enhanced the antimicrobial activity, while the released nitric oxide gas from the dressing demonstrated the ability to mitigate vascular endothelial cell damage induced by high glucose levels. These advancements show promising potential for facilitating the healing process of diabetic wounds by addressing complications associated with diabetes and enhancing overall wound healing.