Electrochemical Intercalation of Fluoride-Ions into Oxyfluorosulfide Via Electrolyte Solution for Liquid-Based Fluoride-Ion Battery
Authors: Zhang Shicong , Okazaki Ken-ichi , Zhong Chengchao , Shimoda Keiji , Orikasa Yuki 
Published: December 2024

Rechargeable batteries with high energy density have been required for recent applications such as battery electric vehicles. Fluoride ion batteries (FIBs) can achieve high energy density by using monovalent fluoride ions as charge carriers and multi-electron reactions of electrode active materials, and have attracted much attention as a candidate to surpass the performance of the current lithium-ion battery (LIB). However, FIB using the metal/metal fluoride conversion reaction, which has a high potential for energy density, has not been fabricated with good reversibility as the current LIB. On the other hand, the FIB using a crystal capable of intercalation (insertion-extraction) reaction of fluoride ions as the active material has been developed [1]. Recently, an all-solid-state fluoride ion battery using an oxyfluorosulfide (Sr2F2Fe2OS2; SFFOS) as the intercalation-type positive active material has been reported, and the battery has operated with high capacity and good reversibility at 413 K [2]. In this study, SFFOS was evaluated as an active material for liquid-based FIB. In particular, the thermal effect on the intercalation reaction of SFFOS in ionic liquid-based electrolyte solution was measured.

The SFFOS was synthesized from four kinds of powder, SrF2, SrO, Fe and S, with molar ratio of 1:1:2:2 referring to the previous papers [2, 3]. These powders were mechanically ground under argon and pressed at 6 MPa to form a pellet. The resulting pellet was vacuum sealed in a quartz tube and sintered at 1073 K for 36 hours to obtain the SFFOS. PbSnF4 as the counter electrode material was prepared from PbF2 and SnF2 by mechanical milling at 600 rpm for 6 h using a planetary ball mill, and then calcined at 673 K for 1 h under an argon atmosphere. The electrolyte solution was prepared by dissolving anhydrous tetramethylammonium fluoride (TMAF) in an ionic liquid, N,N,N-trimethyl-N-propylammonium-bis(trifluoromethanesulfonyl)amide (TMPA-TFSA), at various concentrations such as 0.075 mol/dm3 (the molar ratio of TMAF:TMPA-TFSA=1:50). The working and counter electrodes were prepared by mixing of SFFOS or PbSnF4 with acetylene black and PVdF, respectively. The galvanostatic intercalation reaction of fluoride ions into SFFOS was measured using a three-electrode cell with a Pb|PbF2 reference electrode at 298, 373, and 423 K.

The galvanostatic intercalation reaction (corresponding to a charging reaction) of the SFFOS/AB/PVdF composite electrode showed the charging plateau at about 0.5 V vs. Pb|PbF2. The following deintercalation (discharging) reaction, the discharge plateau was observed around 0 V. The intercalation/deintercalation plateaus were similar to those of the previously reported all-solid-state FIB, well [2].

References:

[1] M. Nowroozi et al., Chem. Mater., 2017, 29, 3441-3453.

[2] Z. Cao, et al., Chem. Mater., 2024, 36, 1928-1940.

[3] H. Kabbour et al., J. Am. Chem. Soc., 2008, 130, 8261-8270.