A Correlation Between The Electrochemical Behaviours of Copper Tubes and Copper Rotating Cylinders in Synthetic Sea Water
Authors: Ponzano G. P. , Bassoli M. , Bonora P. L.
Published: May 2005

The experimental conditions corresponding to those which are ascertained in a heat exchanger have been reconstructed in laboratory, with the possibility of performing very accurate electrochemical measurements. The electrochemical results have been compared with those derived from the use of simple geometric electrochemical cells. A mathematical correlation has been obtained between the electrochemical measurements obtained on a rotating cylinder and on the interior surface of a tube‐shaped electrode, through which a solution flows. It has been concluded that:

the fluid‐dynamic conditions, in the two electro‐chemical cells we investigated, are comparable between each other, by an electrochemical point of view, when identical values of thickness of the limiting diffusion layers are obtained in the two cases.

it is possible to utilize simple cell geometries, such as the one employing a rotating cylinder, to investigate on the corrosion problems which happen in pipes or heat exchangers, in which an electrolyte flows, (even if its aggressiveness is as high as synthetic sea water is) as a function of fluid‐dynamic conditions.
Film Growth and Dissolution of Iron Ions at passive iron in neutral solutions containing chloride
Authors: Heusler K. E. , Fischer L.
Published: May 2005

The passivating oxide layer on iron grows by transfer of oxygen ions from the solution into the oxide. As expected theoretically, the dissolution rate of iron ions increases with the growth rate of the layer. In neutral solution the current efficiency for oxide growth is larger than in acid solutions. By addition of chloride to the solution the current efficiency is further enhanced, because chloride catalyzes the transfer of oxygen ions more strongly than the transfer of iron ions. Chloride in the solution does not change the ionic conductivity of the oxide to a measurable extent. During galvanostatic polarization in solutions containing chloride, fluctuations of the potential and of the dissolution rate of Fe(II) are observed. The frequency of the fluctuations increases with current density and chloride concentration.
Einfluß einer Wärmenachbehandlung auf die mechanischen Eigenschaften und das Korrosionsverhalten nichtrostender Stähle
Authors: Stanz A. , Schäfer K.
Published: May 2005

Ungünstige Gefügezustände, die bei der Verarbeitung von Stählen entstehen und deren Verhalten beeinträchtigen können, lassen sich durch nachträgliche Wärmebehandlung beseitigen. Eine Kaltverfestigung kann durch Glühen bei etwa 1000°C bei einer Haltezeit von etwa 1 min weitgehend beseitigt werden; Auflösung von Chromcarbidausscheidungen erfordert etwa 3 min Haltezeit bei 1030 °C und Auflösung der Sigma‐Phase etwa 10 min Haltezeit bei 1050°C. Voraussetzung für den Erfolg ist, daß die genannten Temperaturen im gesamten Werkstück erreicht werden und daß die Abkühlung nach der Wärmebehandlung ausreichend rasch erfolgt.
Die Beeinflussung des Schwingungsrißkorrosionsverhaltens des Stahles X 20 Cr 13 durch einen Molybdänzusatz in chloridhaltigen Medien
Authors: Schmitt‐Thomas Karlheinz G. , Haubenberger G. W. D. , Meisel H.
Published: May 2005

Das Schwingungsrißkorrosionsverhalten von 13% Cr‐Stahl (eingesetzt für Turbinenschaufeln) wurde in Abhängigkeit von der Carbidausbildung und vom Molybdänzusatz ermittelt, und zwar in wässerigen NaCl‐Lösungen verschiedener Konzentrationen bei Temperaturen zwischen Raumtemperatur und 200°C. Weitere Versuche in Autoklaven wurden durchgeführt, um die oberhalb 150°C ohne Belastung entstehenden Deckschichten zu untersuchen. Durch Zusatz von 1% Mo wird die Korrosionszeitfestigkeit bei Raumtemperatur wesentlich erhöht, während sich Unterschiede in der Carbidausbildung nicht auswirken. Bei 150°C ist die Korrosionszeit‐festigkeit weitgehend unabhängig von der NaCl‐Konzentration (0,1 bis 27%), d. h. daß schon geringe NaCl‐Mengen genügen, um bei Lastspielzahlen über 106 starke Korrosion in Naßdampf hervorzurufen. Besonders geeignet für Untersuchungen ist der Belastungsbereich zwischen ± 150 und ± 200 N/mm2 bei 150°C, da diese Bedingungen betriebsnah sind. Die Passivierungsschichten sind sehr dünn (Interferenzerscheinungen). Aufgrund der Verbesserung der Korrosionsbeständigkeit bei 1% Mo‐Zusatz wird erwartet, daß 2,5% Mo eine deutliche weitere Verbesserung bringen, besonders im Hinblick auf die Lochkorrosion, da der Bruch an Lochkorrosionsstellen seinen Ausgang nimmt.
Elektrochemische Methode zur Untersuchung der Anfälligkeit korrosionsbeständiger Stähle für interkristalline Korrosion
Authors: Číhal V. , Fürychová J. , Kubelka J.
Published: May 2005

In der vorliegenden Arbeit wird in Anknüpfung an die früher vorgeschlagene Methode zur elektrochemischen Prüfung der Anfälligkeit korrosionsbeständiger Stähle für interkristalline Korrosion eine potentiodynamische Polarisationsmethode auf dem Prinzip der Reaktivierung aus dem passiven Zustand ausgearbeitet. Diese Methode wurde an austenitischen Chromnickel‐und Chromnickelmolybdänstählen mit abgestuftem Kohlenstoffgehalt überprüft. Zur Überprüfung und Modifizierung der Empfindlichkeit der neuen Methode wurden gleichzeitig Prüfungen der interkristallinen Korrosion in einer Standardlösung in Gegenwart von Kupferspänen durchgeführt. Die Anfälligkeit der einzelnen Stähle für interkristalline Korrosion wurde aufgrund der dabei gefundenen Bereiche der interkristallinen Korrosion in Abhängigkeit von der Temperature und der Dauer der Sensibilisierung ‐ sogenannte Rollason‐Kurven ‐ beurteilt. Als optimales quantitatives Kriterium zur Beurteilung der Anfälligkeit erscheint das Verhältnis der Ladung bei der Reaktivierung zur Ladung im aktiven Bereich der Polarisationskurve (bei steigendem Potential), ausgedrückt in Prozent. Aufgrund eines Vergleichs mit den Ergebnissen in der Standardlösung kann von einem bestimmten Wert dieses Verhältnisses an (bei Chromnickelstählen z. B. ab 18%) mit Anfälligkeit für interkristalline Korrosion gerechnet werden. Die Empfindlichkeit der Methode kann für die einzelnen Typen der Stähle sowohl durch die Prüfbedingungen, vor allem Temperature und Potentialänderungsgeschwindigkeit, als auch durch die Auswahl oder die Modifikation der chemischen Zusammensetzung des Elektrolyten verändert werden.
The Corrosion Performance of Nickel‐Based Alloys containing group II‐V elements in a gas turbine material test rig
Authors: Strafford K. N.
Published: May 2005

The corrosion of eight Ni‐based ternary alloys (15 w/o Cr plus 1 w/o X, where X = Mg, La, Ce, Gd, Th, U, Zr or V), and a binary control alloy (15 w/o Cr) has been assessed in a rig designed to simulate combustion conditions in gas turbines operating on a contaminated Diesel fuel. Performance has been evaluated in terms of metal loss (radius measurements), scale thicknesses and depths of internal corrosion after 10 and 200 h exposure: the morphology and composition of corrosion products have also been examined. Although the pattern of oxide scale formation was broadly similar from alloy to alloy, considerable differences in the type and depth of the internal corrosion taking place were apparent. The possibility of the use of some of these addition elements in future turbine materials, particularly coatings, is considered in the light of these observations.
Lochkorrosion stickstofflegierter austenitischer CrNiMnMoN‐Stähle in 3%iger NaCl‐Lösung
Authors: Richter B. , Prause W.
Published: May 2005

Stickstofflegierte austenitische CrNiMnMoN‐Stähle zeigen bei elektrochemischen Untersuchungen in chloridhaltigen wäßrigen Lösungen eine Lochfraßanfälligkeit, die mit den Werkstoffzuständen nach Lösungsglühen und Kaltverformungen zusammenhängt. Der Passivbereich der hochchromhaltigen Stähle reicht bis zu einem Potential von E ≈︁ 1300 mVH, bei dem nach Überschreiten des Grenzpotentials stabile Lochkorrosion EL Lochfraßschäden und Kaltverformungen zusammenhängt. Der Passivbereich der hochchromhaltigen Stähle; reicht bis zu einem Potentialen von E ≈︁ 300 mVH bis EL bilden sich verschiedene Stromdichtemaxima, die mit dem Entstehen von Löchern auf den Schnittflächen der Proben den Bereich des repassivierbaren Lochfraßes anzeigen. Nach Kaltwalzen der Bleche ist die Stromdichte im gesamten Potentialbereich erhöht, da die Lochdichte auf den Schnitt‐und Walzflächen mit steigendem Verformungsgrad zunimmt. Kaltverformungen verändern die Lage des Grenzpotentials für stabile Lochkorrosion EL nicht. Untersuchungen über den Entstehungsort der Löcher sagen aus, daß die Keimbildung bevorzugt an Sulfideinschlüssen erfolgt, deren unterschiedliche Formen auf den verschiedenen Flächen der Proben zu Lochfraßschäden mit entsprechendem Aussehen führen. Das Lochwachstum wird von den entstehenden Vertiefungen nach dem Herauslösen der Sulfide und von Gitterstörungen des Metalls beeinflußt.
Corrosion Fatigue Behaviour of Armco‐Iron as a function of heat treatments
Authors: Bonora P. L. , Ponzano G. P. , Sangiorgi R.
Published: May 2005

A corrosion fatigue testing device is presented which satisfies in a simple way many needs of this kind of research. In particular, the behaviour of stresses and strains vs. time is known at every point of the specimen; load may be varied and controlled; electrochemical measures are easily obtained; reproducibility is assured. The specimen acts as a cantilever beam. Results are presented and discussed concerning alterations in the structure of Armco iron as a consequence of the following two heat treatments:

A. heating in a vacuum furnace at 760°C for two hours, quenching in water (some experiments have been performed quenching in NaCl solution or in aqueous oil emulsion) at 20 °C.

B. heating in a vacuum furnace at 760°C for one hour, then at 925°C for four hours, quenching under the same conditions as in A.

Sensitization and protection with respect to intergranular attack and consequently to the rate of fatigue corrosion cracking respectively follow the two above mentioned heat treatments.
Die Korrosionsverluste und ihr Anteil am Brutto‐Sozialprodukt der ČSSR
Authors: Kuliš Miloš
Published: May 2005

Die finanziellen Auswirkungen der durch Korrosion hervorgerufenen Wertminderung von Werkstoffen können in direkte und in indirekte Korrosionsverluste eingeteilt werden. Zu den direkten Verlusten – ausgedrückt als Kostenfaktoren – gehören die erhöhten Produktionskosten infolge der Verwendung von korrosionsbeständigen Werkstoffen oder Korrosionsschutzmaßnahmen wie Beschichtungen oder Überdimensionierungen, die durch Korrosionsschutzmaßnahmen bedingt erhöhten Transportkosten, die Erhöhung der eigentlichen Betriebskosten infolge von Reparaturen und Instandhaltungsarbeiten einschließlich der kosten für das Wartungspersonal. Indirekte Kosten sind u. a. Verluste durch Produktionsausfälle wegen Ausfalls von Anlagen, Verluste an Rohstoffen und Zwischenprodukten bei Produktionsausfall, oder Vertragsstrafen bei Nichteinhaltung von Lieferterminen. Der Autor stellt aufgrund umfassender Untersuchungen in Betrieben der ČSSR die Bilanz der kosten auf, die durch die oben erwähnten Faktoren bedingt sind; danach betrugen die direkten Korrosionsverluste 1975 1, 73% des Brutto‐Sozialproduktes; man hofft, durch gezielte Maßnahmen bis 1980 diesen Anteil auf 1,30% verringern zu können.
Aufkohlung von Schleudergußrohren in der petrochemischen Industrie und Erklärung dieses Verhaltens durch Laborversuche mit Chrom‐Nickel‐Stählen und ‐ Werkstoffen im Temperaturbereich von 800–1150°C
Authors: Steinkusch W.
Published: May 2005

Das Aufkohlungsverhalten von unter den Bedingungen der petrochemischen Crackverfahren verwendeten Rohren ist von allem abhängig von der Temperature. Bis 1000°C ist die Kohlenstoffaufnahme gering. ab 1150°C ist jedoch mit starker Kohlenstoffaufnahme und größser werdender Aufkohlungstiefe zu rechne. Ursache dieser Temperaturabhängigkeit ist der Umstand, daß bei 1050°C das Gleichgewicht zwischen Chromoxid und Chromcarbid erreicht wird, so daß das Oxid nicht mehr beständig ist und die ursprünglich vorhandene Schutzwirkung der Oxidschicht verlorengeht. Deshalb ist auch eine Voroxidation der Rohre nur sehr bedingt geeignet: beim Abkühlen kann es zu Rißbildung in der Oxidschicht kommen, wodurch schon bei Temperaturen um 800°c Randaaufkohlung möglich wird. Verzögert wird die Aufkohlung durch hohe Gehalte an Cr, Ni und Si: für Verwendung bei 1100° sind z. B. mindestens 28% Cr, 32% Ni und 2,5% Si erforderlich.
Über den Einfluß des Flächenverhältnisses auf die Stromdichte in galvanischen Zellen und Belüftungszellen
Authors: Grubitsch H. , Herzog G. , Tomašic S.
Published: May 2005

Im Hinblick auf die Korrosionsvorgänge an gängigen Metallkombinationen wurde die Korrosionsstromdichte in Abhängigkeit vom Flächenverhältnis Kathode: Anode in Belüftungszellen (Fe/Zn, Fe/Fe, Zn/Zn, mit Na‐Sulfat und NaCl als Elektrolyt) und in galvanischen Zellen (Cu/Fe, Cu/Zn, mit Kupfer‐, Ammonium‐ und Zinksulfat als Elektrolyt) untersucht. Dabei sollte festgestellt werden, inwieweit die theoretischen Vorstellungen von Mansfeld und Akimov bezüglich der Durchtritts‐ und Diffusionskontrolle hierauf anwendbar sind. Es wird gefunden, daß zur Interpretation der Korrosionsstromdichte der Belüftungszellen das Konzept von Mansfeld um die tatsächlichen Elektrodenpotentiale erweitert werden muß. Bei den galvanischen Zellen ergibt sich eine Begrenzung durch den Zellenwiderstand, der durch unabhängige Widerstandsmessungen nachgewiesen wird. Das Korrosionsverhalten der untersuchten Metalle wird auf der Grundlage der gemessenen Stromdichten gedeutet.
Peculiarities in the Behaviour of Thiourea as corrosion‐inhibitor
Authors: El Din A. M. Shams , El Hosary A. A. , Saleh R. M. , El Kader J. M. Abd
Published: May 2005

The dissolution of Fe, cu, Zn and Al in nitric, hydrochlorid and sulfuric acids is retarded by low concentrations of thiourea, while higher thiourea concentrations may bring about a stimulation of corrosion. In nitric acid thiourea is probably oxidised (heat evolution); the dithioformamidine formed at first is then hydrolysed to give diaminocarbonyl disulfide which again is reduced to thiocarbamic acid at the cathodic sites of the surface. The depolarisation thus produced gives rise to accelerated dissolution. In non‐oxidising acids a monomolecular layer of thiourea is adsorbed at the metal at first; its subsequent reduction to sulfide and hydrogen sulfide again gives rise to an enhancement of corrosion. The critical concentration of the transition from inhibition to stimulation depends ont he type of the acid and its concentration.
Thin Film oxidation of metals at the Curie temperature
Authors: Chatterjee B.
Published: May 2005

Anomalies in the Arrhenius plot of the thin film (102–105 Å) oxidation of nickel and iron at the Curie temperature are discussed. Amongst the various theories, a mechanism which takes into account the importance of both the surface‐state charge at the metal/oxide interface and the space charge int he oxide during the logarithmic oxidation of metals, is considered suitable to explain such anomalies.
Durch Industrieemissionen verursachte Korrosionsschäden an Stahlbauten im Industriegebiet Ostrava
Authors: Kuliš M.
Published: May 2005

Um zumindest Näherungsdaten zu erhalten, welche eine Beurteilung der durch korrosion verursachten finanziellen Verluste ermöglichen, wurden vom Autor entsprechende Untersuchungen durchgeführt. Dabei wurden Stahlkonstruktionen, vor allem Brücken, Gasbehälter, Leitungsmasten und Fördertürme als Grundlagen für die Beurteilung herangezogen und auch die Einsparungen ermittelt, welche durch Beschichtungen (einschließlich der periodischen Erneuerung der Mehrschichtensysteme) erreicht werden können. Es wird gezeigt, daß die periodische Reparatur der Anstrichsysteme beträchtliche Vorteile im Vergleich zur vollständigen Erneuerung der unbeschichteten Konstruktion bietet, wenn man die aus Sicherheitserwägungen erreichbare Lebensdauer zugrundelegt. Die Lebensdauer konnte durch entsprechende Anstriche auf das Dreifache erhöht werden, wobei die Kosten für die Beschichtungen nur ein Drittel der Kosten einer Konstruktion ausmachten.
Untersuchungen zur Lötbrüchigkeit hochlegierter Stähle
Authors: Herbsleb G. , Schwenk W.
Published: May 2005

Durch Einwirken von Zink bei höheren Temperaturen auf nichtrostende austenitische Chrom‐Nickel‐Stähle kann eine als „Lötbruch”︁ oder „Lötrissigkeit”︁, engl. „Liquid Metal Embrittlement”︁, bezeichnete, auf die Bildung einer niedrigschmelzenden nickelreichen, zinkhaltigen Phase zurückzuführende Korngrenzenchädigung entstehen. Diese Erscheinung ist an anderen Metallen und Metallegierungen bereits seit längerer Zeit bekannt und im Schrifttum verschiedentlich beschrieben worden. Über die Lötbrüchigkeit der hochlegierten Stähle liegen jedoch bisher nur verhältnismäßig wenig Angaben vor.
Probenhalterungen für elektrochemische Korrosionsversuche
Authors: Gerodetti B. , Wiedemann K. H.
Published: May 2005

Um Reproduzierbarkeit und Zuverlässigkeit der Ergebnisse von elektrochemischen Messungen zu gewährleisten, müssen die Apparaturen und insbesonders die Probenhalterungen gewährleisten, daß die folgenden Anforderungen erfüllt werden können: definierte Fläche; gleicher Abstand zwischen Probe und Bezugselektrode; guter elektrischer Kontakt zwischen Probe und Kabel; kein Elektrolytzutritt zu Metalloberflächen außerhalb der Probe. Die Autoren haben Halterungen entwickelt, welche den Aufbau von Versuchs einrichtungen ermöglichen, die diesen An forderungen entsprechen. Angefertigt wurden u. a. Anordnungen für die Ermittlung von Stromdichte/Potential‐Kurven und zur Untersuchung der Kontaktkorrosion.
Zum Einfluß werkstoffunabhängiger Größen auf die Spannungsriß‐korrosion unlegierter, kohlenstoffarmer Stähle in Kalziumnitratlösungen
Authors: Nürnberger U.
Published: May 2005

Untersuchungen bei Nitratkonzentrationen zwischen 30 und 0,01% bei Temperaturen zwischen Siedepunkt und 25 °C und Versuchsdauern bis max. 6000 h. Bei konstanten chemischen und physikalischen Bedingungen ist unterhalb der Streckgrenze und oberhalb einer für jeden Werkstoff charakteristischen Grenzspannung eine geradlinige Abhängigkeit zwischen der Spannung und der Lebensdauer erkennbar. Auch zwischen der Temperatur und der Lebensdauer besteht unter diesen Bedingungen eine geradlinige Abhängigkeit. Zwischen der mechanischen und chemischen Beanspruchung ergibt sich eine komplexe Beziehung, die keine Lebensdauervorhersagung mit einfachen mathematischen Mitteln ermöglicht. Bezüglich des pH‐Wertes liegt das Maximum der Empfindlichkeit bei 2–9.5, wobei der untere Grenzwert noch nicht zuverlässig festliegt. Bei erhöhter Calciumnitratkonzentration ist die Lebensdauer größer.
Kupfer‐, Nickel‐ und Titanlegierungen für Seewasseranwendungen
Authors: Richter Herbert
Published: May 2005

Als Werkstoffe für Wärmetauscher in schiffen, Kraftwerken und Chemieanlagen sowie für Leitungssysteme haben sich aufgrund ihrer Korrosionsbeständigkeit gegen Seewasser Kupfer und Nickellegierungen sowie Titan bewährt. Sondermessing und Kupfer‐Nickellegierungen, die Standard werkstoffe für Kondensatoren und Kühler, können jedoch abhängig von Wasserqualität und Strömungsgeschwindigkeit und den konstruktiven Gegebenheiten angegriffen werden. Die Korrosionsmechanismen werden diskutiert. Unter besonders schwierigen Wasserbedingungen bietet sich Titan als Wärmetauscherwerkstoff an. Nickelbasislegierungen bieten vor allem bei anwendung höherer Temperaturen Vorteile, z. B. in chemischen Prozessen und bei Eindampfvorgängen. Es werden Beispiele für die Anwendung und Maßnahmen zur Verhütung von Korrosionsschäden beschrieben.
Die Lochkorrosionsanfälligkeit des Vergütungsstahles X20Cr13 in Natriumchloridlösungen
Authors: Effertz P.‐H. , Forchhammer P.
Published: May 2005

Als schaufelwerkstoff für Dampfturbinen wendet man überwiegend Vergütungsstähle mit 13% Cr (X 20 Cr 13) an. Schaufelbrüche im Gebiet beginnender Dampfnässe der Turbine ließen sich häufig auf Schwingungsrißkorrosion zurückführe, die ihren Ausgang von Werkstoffinhomogenitäten, im allgemeinen jedoch von durch Lochkorrosion entstandenen löchern nahm. Ursache der Lochkorrosion sind festgestellte chloridhaltige Schaufelbeläge. Um das Lochkorrosionsverhalten dieses Stahles zu untersuchen, wurden in Natriumchlloridlösungen das Ruhe‐ und Lochkorrosionspotential, Massenverlust und Lochzahldichte und das Redoxpotential der Lösungen in Abhängigkeit von der temperatur (20–80°C), pH‐Wert (5–7–9), Sauerstoffgehalt (20 μg/l bis sauerstoffgesättigt) und Chloridkonzentration (8 × 10−5 m/l bis 5,4 m/l (ges.)) bestimmt. Es ergab sich, daß der Stahl X20Cr13 wegen seiner nur gering ausgeprägten Passivität in praktisch allen technisch möglichen chloridhaltigen Elektrolyten bis hinab zu 10−5m/l Cl anfällig gegen Lochkorrosion ist.
Corrosion studies under conditions of thermal desalination I. Pilot test loops for the simulation of plant conditions
Authors: Manner R. , Heitz E.
Published: May 2005

In a pilot test loop conditions of thermal sea‐water desalination were simulated, i. e., temperatures between room temperature and 120°C, oxygen contents between saturation and 2 ppb, flow velocities up to 6 m/s and various pH values were controlled over a long time with appropriate regulation devices. In two specimen chambers of different design corrosion rates of non alloyed and low alloyed steels were measured and compared by weight loss and polarisation resistance. Good agreement was obtained in 100 hr experiments and short duration parameter studies. This work contains the experimental and methodical requirements for investigation into the influence of oxygen, flow velocity, pH value and impurities during sea‐water desalination which will be presented in part II of the publication.
Elektrochemische Untersuchungen zur Hochtemperaturkorrosion von Chrom‐Nickel‐Stählen in Alkalisulfatschmelzen bei 700°C
Authors: Schwenk W.
Published: May 2005

CrNi‐Stahl X 5 CrNi 189 wurde in verschiedenen Wärmebehandlungszuständen hinsichtlich seiner Kornzerfallsanfälligkeit nach DIN 50914 entkohlt und aufgekohlt sowie vergleichend die stabilisierten Stähle X 10 CrNiTi 189 und X 10 CrNiNb 189 bei 700°C in eutektischer Alkalisulfatschmelze mit/ohne Zusatz von 10% NaCl bzw. 1% SO3 korrodiert. Selektive Korrosion von Carbiden und chromverarmten Bereichen konnte nicht nachgewiesen werden. Durch NaCl tritt bevorzugt mit fallendem Potential schwacher Korngrenzenangriff auf. Bei sehr negativen Potentialen bilden sich keine Schutzschichten und instabile Grenzflächen Stahl/Zunder mit innerer Oxidation. Die “Aktivkorrosion” durch Chloride und instabile Grenzflächen werden durch Ni unterstützt.
Korrosion in Alkalimetallkreisläufen. II – Untersuchungsmethoden
Authors: Borgstedt H. U. , Frees G.
Published: May 2005

Die zur Untersuchung der Korrosion durch flüssige Alkalimetalle an metallischen Werkstoffen gebräuchlichen Versuchsaufbauten werden beschrieben und ihre Beziehungen zu den Fragstellungen der Versuche diskutiert. Einfache und billige Versuchsaufbauten bedingen stagnierende Metallschmelzen und nur kleine Temperaturgradienten, lassen aber vor allem in instrumentierten Behältern durchaus interessante Versuchsergebnisse erwarten. Für anwendungsnahe Untersuchungen müssen die technisch wichtigen Parameter wie Strömungsgeschwindigkeit, Temperaturgradienten und Reinheit der Schmelzen einstellbar und meßbar sein, will man auf die Technik übertragbare Ergebnisse erhalten. Die für solche Versuche üblichen Kreisläufe können bis zu Tonnen der Metallschmelzen aufnehmen und sehr aufwendig werden. Aus den hier gewonnenen Erfahrungen lassen sich Korrosionsuntersuchungen in anderen Metallschmelzen in ihrer Versuchstechnik befruchten.
The oxidation of an 18/8 type stainless steel in CO2
Authors: Smith A. F.
Published: May 2005

The oxidation behaviour of an 18/8 type stainless steel has been studied in the temperature range 873‐1258 K (600–985 °C) by continous weight gain measurements, metallography and scanning electron microscopy. An initial high oxidation rate was followed by a much slower rate. Duplex scales formed at an early stage of oxidation and the decrease in oxidation rate is probably due to the formation of an ordered chromium rich spinel at the oxide/metal interface.

A ture parabolic rate constant (kp) was obtained taking into account the formation of the “healing” phase using the Hales model. This gave:

.
where the activation energy is expressed in KJ · mole−1. (55 Kcals mole−1).
Technisch‐ökonomische Auswertung der Korrosionsverluste an Stahlkonstruktionen im Gebiet Nordböhmen
Authors: Kuliš M.
Published: May 2005

Aufgrund von mehrjährigen Bewitterungsversuchen in 15 Bewitterungsstationen in Nord‐Böhmen (ČSSR) wurden die Korrosionsgeschwindigkeit von Baustahl, Zink und Aluminium ermittelt; außerdem wurde in Produktionsbetrieben sowie an Elektrizitätsverteilungssystemen in der Nähe der Bewitterungsstationen die Lebensdauer von dreischichtigen Anstrichsystemen ermittelt. Dabei wird eine Gegenüberstellung der Kosten vorgenommen, die sich durch Ersatz von korrodierten Stahlteilen (Abnahme auf 50% der ursprünglichen Dicke) sowie bei der Verwendung von Korrosionsschutzsystemen (Feuerverzinkung, Aluminiumspritzüberzug und dreischichtiges Anstrichsystem einschließlich der Anstricherneuerung in bestimmten Zeitabständen) ergeben. Sowohl im Hinblick auf die Kosten als auch auf den Arbeitsaufwand ist eine Feuerverzinkung die optimale Lösung.
Untersuchungen des Stofftransports und der chemischen Reaktionen im System Polyäthylen‐weich/Schwefelsäure–Zur Frage der Spannungsrißkorrosion in Kunststoffen–
Authors: Hessel Joachim , Bühler Hans‐Eugen
Published: May 2005

Untersuchungen des Stofftransports und der chemischen Reaktionen im System Polyäthylen‐weich/Schwefelsäure zeigen, daß sowohl an eigenspannungsbehafteten Vollproben ohne äußere Belastung, als auch an im Zeitstandinnendruckversuch geprüften Rohrproben verschiedene Schadens‐ und Reaktionsabläufe zu registrieren sind. Licht‐ und rasterelektronenmikroskopische Ergebnisse führen zu dem Schluß, daß sowohl die werkstoffspezifische Mikrostruktur als auch die herstellungsbedingte Makrostruktur in Verbindung mit inneren und äußeren Spannungen und einem kritischen Medium zu einem Schadensbild führen, das man bei Polymerwerkstoffen als „Spannungsrißkorrosion”︁ bezeichnet.
Vorrichtung zur kontinuierlichen Messung der unter Sauerstoffreduktion verlaufenden Korrosion
Authors: Kiss László
Published: May 2005

Eine Vorrichtung zum Messen der mit Sauerstoffreduktion verbundenen Korrosionsgeschwindigkeit ist beschrieben. Nach dem Grundprinzip des Verfahrens wird der während der Korrosion verbrauchte Sauerstoff durch elektrolytisch hergestellten Sauerstoff ersetzt. Die zur Herstellung des Sauerstoffs benötigte Ladungsmenge ist bequem meßbar und gibt gleichzeitig Aufschluß über das Fortschreiten der Korrosion.
Zusammenhang zwischen Gefüge und Korrosionsverhalten bei Zirkonium
Authors: Günther Tilo
Published: May 2005

Veranlaßt durch Betriebsschäden an Zirkonium 702 in schwefelsauren Medien wurden an ungeschweißtem und an geschweißtem Werkstoff dieses Reinheitsgrades die Gefügebeschaffenheit und das Korrosionsverhalten in den verschiedensten Wärmebehandlungszuständen untersucht. Geglüht wurde verschieden lang (0,5 bis 9 h) bei Temperaturen zwischen 650 und 1000 °C mit anschließender unterschiedlicher Abkühlung (in Wasser, Luft oder im Ofen). Das Korrosions‐verhalten wurde unter bewußt an der Grenze der Korrosionsbeständigkeit liegender Beanspruchung – in siedender 65% iger Schwefelsäure – verfolgt.

Aus den Gefügeuntersuchungen, die durch Mikrosondenuntersuchungen ergänzt wurden, und den Korrosionsversuchen ging hervor, daß das Korrosionsverhalten des Zirkoniums erheblich von der Gefügebeschaffenheit beeinflußt wird, die ihrerseits vom Reinheitsgrad und Behandlungszustand des Werkstoffes abhängt. Verantwortlich sind die Art, Menge und Verteilung von Begleitelementen – vornehmlich von Eisen – bzw. der durch sie bedingten Ausscheidungen.

Die Schäden der Praxis ließen sich damit erklären. Als Maßnahme zur Verbesserung des Korrosionsverhaltens von Reinzirkonium im Grenzfall der chemischen Beanspruchung konnten aus den Untersuchungen abgeleitet werden: (1) ein mehrstündiges Glühen bei 750 °C so wohl des ungeschweißten wei auch des geschweißten Werkstoffes, (2) ein mindestens zweilagiges Schweißen, wenn es genügt, nur das Verhalten des Schweißgutes zu verbessern; dabei muß die erste Schweißlage auf der Seite der kritischen Beanspruchung liegen, (3) Einsatz eines Zirkoniums mit höherem Reinheitsgrad sowohl für den Grundwerkstoff wie auch für den Schweißzusatzwerkstoff. Durchführbarkeit, Wirtschaftlichkeit und Erfolg solcher Maßnahmen hängen selbstverständlich sehr vom Einzelfall ab. Dazu müssen noch praktische Erfahrungen gesammelt werden.
Untersuchungen zum Massetransport an Stahl in einem Natriumkreislauf
Authors: Schneider Helga
Published: May 2005

Es wurden die Veränderungen der Oberflächenzusammensetzung von 2 unstabilisierten Stählen 1.4301 (X 5 CrNi 189) und 1.4919 (X 6 CrNiMo 1713) und 2 stabilisierten austenitischen Stählen 1.4970 (X 10 CrNiMo Ti 1515) und 1.4988 (X 8 CrNiMo VNb 1613) nach 6000 h Einsatz in strömendem Natrium in unterschiedlicher Testposition untersucht. Die Testpositionen lagen im Aufheizbereich bei 570 und 700 °C, im Abkühlbereich bei 590 °C und 500 °C.

Die Untersuchungen erfolgten spektralanalytisch unter Verwendung einer Glimmentladungslampe und mit Hilfe der Auger‐Elektronen‐Spektroskopie. Die Ergebnisse stehen im Einklang mit den bestimmten Gewichtsveränderungen der Proben und den Ergebnissen metallographischer und rasterelektronenmikroskopischer Untersuchungen. Sie werden im Hinblick auf die möglichen Auswirkungen auf den Betrieb eines natriumgekühlten Reaktors diskutiert.
Inhibitoren der Korrosion 25(1) – Über die Rolle der Kationen in Neutralsalzen bei der Korrosion von Eisenwerkstoffen in Gegenwart von Sauerstoff
Authors: Horner L. , Schenk M. , Doms G.
Published: May 2005

Die Geschwindigkeit des Sauerstoffverbrauchs bei der Korrosion von jeweils 500 mg DAB6‐Eisenpulver wird in Abhängigkeit von der Art des Kations in Neutralsalzen (Chloriden) unter Standardbedingungen bestimmt. In Gegenwart von Alkali‐, Quartären Ammonium, Quartären Phosphonium‐und Erdalkalichloriden ist die Geschwindigkeit des Sauerstoffverbrauches vergleichbar groß. Mit Zink‐, Cadmium‐, Nickel‐und Kobaltchloriden wird aber im Bereich von pH5 bis pH7 eine überraschend große Verzögerung der Sauerstoffaufnahme beobachtet. Es handelt sich mit hoher Wahrscheinlichkeit um eine Blockade der kathodischen Bezirke in der Eisengrenzfläche durch Abscheidung der schwerlöslichen basischen Hydroxyde von Zink, Cadmium, Nickel und Kobalt.
Mößbauerspektroskopische Untersuchungen der Eisenkorrosion
Authors: Meisel W. , Molnár B.
Published: May 2005

Die mößbauerspektroskopische Phasenanalyse wird auf die Untersuchung der Flächenkorrosion reinen Eisens angewandt. Es ergeben sich Aussagen über Verlauf Schichtung und Phasenumwandlungen bei Korrosion unter milden und feuchten Bedingungen und bei der Unterrostung von Anstrichen. Die Untersuchung ausgelagerter Proben bringt Informationen über den Einfluß aggressiver Abgase und klimatischer Faktoren. Es werden einige allgemeine Schlüsse über die Bildung der metallnahen Korrosionsschicht und nachfolgende Phasenumwandlungen gezogen.
Untersuchungen zur H‐induzierten Rißkorrosion – Teil 2: Vergleichende Untersuchungen zur Wasserstoffpermeation und Spannungsrißkorrosion
Authors: Pöpperling R. , Schwenk W.
Published: May 2005

Kaltverformte Reineisen‐Proben verschiedener Festigkeit wurden in As2O3‐haltiger Schwefelsäure bei kathodischer Polarisation mit konstanter Last beansprucht. Die kritische Zugspannung für Spannungsrißkorrosion aller Proben ist der Streckgrenze proportional und beträgt 60% Rp. Bei höherer Beanspruchung nehmen die Standzeiten mit zunehmender Streckgrenze ab. Es besteht keine Korrelation mit der Permeationsstromdichte und Wasserstoffgehalt, wohl aber mit der Durchbruchszeit. Einen gleichen Zusammenhang zeigten auch niedriglegierte Stähle in der gleichen Lösung und in H2S‐haltigen Medien. Nach metallografischen Untersuchungen besteht kein Zusammenhang zwischen der Spannungsrißkorrosion und Oberflächenblasen oder H‐induzierten Innenrissen. REM‐Untersuchungen zeigen mannigfaltige Bruchbilder ohne systematischen Zusammenhang.
Untersuchungen zur Korrosionsresistenz von einigen gebräuchlichen Aluminiumwerkstoffen in Meerwasser
Authors: Huppatz G. W. , Krajewski H.
Published: May 2005

An den Aluminiumwerkstoffen Al99,5: AlMn 1 Mg 0,5: AlMg 2 Mn 0,8; AlMg 3; AlMg 4,5 Mn und AlZn 4,5 Mg 1 wurden in künstlichem Meerwasser sowohl potentiostatische Polarisationsmessungen als auch Dauertauchversuche an unpolarisierten Proben unter Registrierung des Freien Korrosionspotentials durchgeführt und die Oberflächenveränderungen mikroskopisch ausgemessen.

Die ermittelten Werte für das Lochfraßpotential von Al99,5 sowie von den untersuchten AlMg‐ und AlMgMn‐Legierungen waren unter den genannten Bedingungen nahezu legierungsunabhängig. Bei den Dauertauchversuchen mit Messung des Freien Korrosionspotentials wurden graduelle Unterschiede im Korrosionsverhalten festgestellt, die in der Verlagerung der Potentiale und im Oberflächenbefund erkennbar waren. Die verschiedenen Untersuchungen lassen im Zusammenhang Rückschlüsse über den Ablauf der einzelnen Teilreaktionen der Korrosion zu. Ihre Ergebnisse deuten darauf hin, daß bei den untersuchten Aluminiumwerkstoffen die Korrosionsreaktionen in lufthaltigem bzw. belüftetem künstlichem Meerwasser von 22°C überwiegend kathodisch gesteuert werden.
The Gaseous Carburisation of Austenitic Steels
Authors: Harrison J. M. , Norton J. F. , Derricott R. T. , Marriott J. B.
Published: May 2005

The paper is concerned with the corrosion behaviour of materials in high temperature gaseous carburisation environments and initially reviews the current ‘state‐of‐the‐art’ in this field. Results of investigations carried out on three 25 Cr‐20 Ni steels exposed to carburising H2‐CH4 mixtures with a controlled carbon activity of 0.8 at 825°C and 1000°C are then presented.

Kinetic data for exposure periods of up to 1100 hours are given and it is shown that gross carburisation of these alloys has occurred after only short exposures at 1000°C. The importance of alloy composition and surface condition, particularly during exposure at 825°C, is demonstrated.

The results of surface and cross‐sectional examinations using a range of optical, electron and X‐ray techniques are reported. The use of a nuclear microprobe technique has enabled accurate carbon concentration profiles to be established and diffusion coefficients for the three alloys have been determined. In addition, the use of a magnetic technique for the non‐destructive monitoring of the extent of sub‐surface carburisation has been investigated.
Beitrag zur Kenntnis der Lotsprödigkeit einiger Kupfersorten und Legierungen sowie zweier hochlegierter Stähle
Authors: Redecker R.
Published: May 2005

Es wurde die Empfindlichkeit von OF‐Kupfer, Elektrolytkupfer, desoxidiertem Kupfer, Kupfer‐Chrom‐Zirkon, Kupfer‐Zirkon, einem Preßmessing sowie einem austenitischen Chrom‐Nickelstahl des 18/8 Typs und einem 12% Chromstahl gegenüber Lotsprödigkeit durch die handelsüblichen Lote L‐Ag 15 P zwischen 660 und 800°C durch Warmbiegeproben untersucht. Von allen geprüften Materialien hat sich nur das Cu Zn 39 Pb 3 unter den beschriebenen Prüfbedingungen als beständig erwiesen. Der Chromstahl wies eine geringfügige Empfindlichkeit nur gegen das L‐Ag 42 Cd bei hohen Temperaturen auf, alle anderen Werkstoffe wurden durch dieses Lot versprödet. Das Lot L‐Ag 15 P erwies sich als weniger reaktionsfreudig. Hier wurde ausschließlich der 18/8 Stahl bei normaler Löttemperatur interkristallin angegriffen.
Huey‐Test als Abnahmeprüfung
Authors: Weingerl H. , Kriszt K. , Zitter H.
Published: May 2005

Die Aussagekraft des Huey‐Tests wird bei der Korrosionsprüfung von Stählen der Werkstoffnummern 1.4306, 1.4404, 1.4550, 1.4580, 1.4541 und 1.4571 verglichen.

Der Einfluß verschiedener Wärmebehandlungen, wie Abschrecken, Ausscheidungsglühen und Stabilisierungsglühen, wurde an Blechproben und analysengleichen Werkstoffen mit Guß‐und Schweißgefüge untersucht. Eine vergleichende Gegenüberstellung der Ergebnisse des normalen mit denen des verkürzten Huey‐Tests zeigt, in welchen Fällen von der Verkürzung der Prüfdauer Gebrauch gemacht werden kann. Nach den vorliegenden Ergebnissen kann von der in der Norm angedeuteten Möglichkeit, bis zu drei Proben in einem Gefäß der kochenden Salpetersäure auszusetzen, Gebrauch gemacht werden, sofern die Massenverlustraten innerhalb der praktisch interessierenden Grenzen liegen. Innerhalb dieser Grenzen besteht ein linearer Zusammenhang zwischen den Ergebnissen der Mehrfachprüfung und denen des üblichen Huey‐Tests, so daß beide Verfahren gleichwertig zur Prüfung verwendet werden können.
Das Aufkohlungsverhalten verschiedener Werkstoffe für Pyrolyserohre
Authors: Steinkusch W.
Published: May 2005

In Anlagen zur Erzeugung von Äthylen befinden sich Röhrenöfen, in denen die Pyrolyserohre aus Schleuderguß bestehen. Im Laufe der Zeit wurden die Betriebsbedingungen verschärft, und es erfolgt heute eine sehr starke Beanspruchung der Rohre bezüglich ihrer Zunder‐ und Aufkohlungsbeständigkeit. Die Rohre werden hauptsächlich aus 25 Cr/20 Ni‐ und 25 Cr/35 Ni‐Stählen geschleudert.

Insbesondere auf der Basis des 25 Cr/35 Ni‐Stahles wurden viele Legierungsvarianten bezüglich ihres Betriebsverhaltens getestet. Darüber hinaus kamen auch versuchsweise zahlreiche Werkstoffe mit hohen Nickel‐Gehalten zum Einsatz.

Die in den letzten Jahren in großen Umgang durchgeführten Laboruntersuchungen zeigten, daß von der Legierungsseite aus neben dem Nickel insbesondere dem Silizium eine große Bedeutung im Hinblick auf die Aufkohlungsbeständigkeit zukommt. Die jetzt durchgeführten Untersuchungen sollen bei 6 verschiedenen Stählen, die heute für die Äthylen‐Herstellung in der Praxis eingesetzt werden, zeigen, ob in der Aufkohlungsbeständigkeit bei unterschiedlichen Silizium‐Gehalten Überlagerungen verschiedener Elemente zu beobachten sind, zumal der Nickel‐Gehalt der zu untersuchenden Werkstoffe zwischen 20% und 35% liegt. Die Ergebnisse dieser neuen Versuchsreihe werden den bereits bekannten gegenübergestellt.

Da für die Beanspruchung der Rohre in der Praxis neben der Aufkohlungsbeständigkeit auch noch die Alterungsbeständigkeit eine Rolle spielt, wurden die Werkstoffe durch entsprechende Glühungen im kritischen Temperaturbereich bis zu einer Dauer von 5000 h untersucht. Unmittelbar mit dem Problem der Alterung hängt auch die Schweißbarkeit bei Reparaturen zusammen.

Eine weitere wichtige Eigenschaft der verschiedenen Werkstoffe ist ihre Zeitstandfestigkeit, da die Restlebensdauer aufgekohlter Rohre im wesentlichen von ihr abhängt.
Zum Repassivierungsverhalten metallischer Werkstoffe am Beispiel einer Titanlegierung
Authors: Rätzer‐Scheibe H.‐J. , Buhl H.
Published: May 2005

Am Beispiel der Titanlegierung Ti6Al4V wird versucht, den zeitlichen Stromverlauf zu beschreiben, der bei der Repassivierung einer aktivierten metallischen Oberfläche im Elektrolyten (1n NaCl) gemessen wird. Dazu werden zeitliche Beziehungen für die verschiedenen Teilströme (Auflösungsstrom, Passivierungsstrom, Dickenwachstumsstrom) unter Berücksichtigung von experimentellen Gegebenheiten (Probenlänge, Probenbreite, Hobelgeschwindigkeit) abgeleitet. Nach Anpassung der theoretischen Funktionen in bestimmten Kurvenbereichen ergibt sich über die gesamte Meßzeit eine relativ gute Übereinstimmung des theoretischen Gesamtstromes mit den experimentellen Stromwerten.
Oxidation und Aufkohlung hochlegierter Werkstoffe für Crackrohre – Teil 2: Das Aufkohlungsverhalten in sauerstoff‐ und kohlenstoffhaltigen Atmosphären hoher Kohlenstoffaktivität
Authors: Ledjeff K. , Rahmel A. , Schorr Monika
Published: May 2005

Es wurden Aufkohlungsversuche an den Gußwerkstoffen 1.4848, 1.4857, 2.4813 und einer 25/20/5‐CrNiSi‐Versuchsschmelze sowie an den Knetlegierungen 1.4301 und 1.4848 in CO‐CO2‐Gemischen mit ac = 1 und in feuchtem Erdgas mit ac > zwischen 1000 und 1200° C durchgeführt. Bei T < etwa 1050° C bilden sich gleichartige oxidische Deckschichten wie an Luft (Werkstoff/Cr2O3/(Mn, Fe)Cr2O4), die eine Aufkohlung verhindern. Eine Aufkohlung tritt erst nach Zerstörung der oxidischen Schutzschichten ein. Dabei müssen mehrere Zerstörungsmechanismen betrachtet werden, (a) durch chemische Reaktion (Umwandlung von Oxid in Carbid; Reduktion von Oxid), (b) durch mechanische Beanspruchung (Temperaturwechsel, Wachsen von Graphitschichten, Kriechverformung).

Reduktionsvorgänge treten nur bei Fe‐reichen Oxidschichten auf. Chromoxidreiche Deckschichten werden, abhängig vom CO‐Partialdruck, in Gasen mit ac = 1 oberhalb etwa 1050° C in Carbid umgewandelt. Die Geschwindigkeit dieser Umwandlung ist stark von der Kohlenstoffaktivität der Gasphase abhängig. Wird Graphit auf der Oberfläche abgeschieden, so läuft die Umwandlung schnell ab, ohne Graphitabscheidung läuft sie selbst bei ac = 1 recht langsam an.

Abgeschiedener Graphit kann auch mechanisch zerstörend wirken, da er in Risse und Poren der Oxidschicht eindringt und so Teile der Oxidschicht abreißt. Bei Vorliegen der porigen Gußoberfläche können sogar Teile des Werkstoffs abgesprengt werden. Das erklärt das schleche Verhalten von Rohren mit Gußoberflächen in Crackanlagen.

Die positive Wirkung des Siliziums beruht auf der Bildung von SiO2‐Schutzschichten zwischen Metall und Cr2O3 bzw. zwischen Metall und äußerer Carbidschicht. Zur Ausbildung geschlossener SiO2‐Schichten darf der Werkstoff einen kritischen Si‐Gehalt nicht unterschreiten.
Korrosion in Halogenkohlenwasserstoffen – Ziele, Abwicklung und Ergebnisse eines Gemeinschaftsprojektes
Authors: Heitz E. , Deuchler W.
Published: May 2005

Eine Reihe von Korrosionsschadensfällen aus der Praxis belegt, daß die Handhabung von Halogenkohlenwasserstoffen nicht ohne Probleme ist. In einem koordinierten Gemeinschaftsprojekt wurde deshalb das Korrosionsverhalten von Eisen‐, Aluminium‐ und Kupferwerkstoffen in ausgewählten Halogenkohlenwasserstoffen untersucht. Die Abwicklung der Gemeinschaftsarbeit wird beschrieben, und die wichtigsten Ergebnisse unter besonderer Berücksichtigung praktischer Aspekte werden zusammengestellt. Diese sind bei den Eisen‐ und Kupferwerkstoffen die besondere Aggressivität von Halogenkohlenwasserstoff/Wasser‐Gemischen und bei den Aluminiumwerkstoffen das Auftreten einer Inkubationszeit des Korrosionsagriffes. Hieraus ergeben sich Folgerungen hinsichtlich des Werkstoffeinsatzes und der Verbesserung der Lösungsmitteleigenschaften.
Korrosionsuntersuchungen an Aluminiumwerkstoffen in praktisch wichtigen Halogenkohlenwasserstoffen
Authors: Dölling H.
Published: May 2005

Es wurde das Korrosionsverhalten von ausgewählten Aluminiumlegierungen (Al99.5 – AlMn – AlMgMn und AlMg4,5Mn) in den Halogenkohlenwasserstoffen (HKW) CCl4, C2Cl4 und CCl3CH3 untersucht.

In den stabilisierten Halogenkohlenwasserstoffen C2Cl4 und CCl3CH3 wurde bei Siedetemperaturen und Expositionszeiten von drei Monaten kein Massenabtrag an den Aluminiumwerkstoffen beobachtet.

Dagegen sind für die Systeme der Aluminiumwerkstoffe in CCl4 (bei Siedetemperatur) sowie in unstabilisiertem CCl3CH3 die Inkubationszeiten charakteristisch, nach denen dann große Korrosionsraten beobachtet wurden.

In den Zweiphasensystemen der untersuchten Halogenkohlenwasserstoffe und Wasser wird die Korrosion an den Aluminiumwerkstoffen durch das Hydrolyseprodukt HCl bestimmt.
Zum Korrosionsverhalten von metallischen Werkstoffen in chlorkohlenwasserstoffhaltigen Lösungsmittelgemischen
Authors: Köser H. J. K. , Lübke M.
Published: May 2005

Die Phänomenologie des korrosiven Angriffs, den ein Kohlenstoffstahl in trichlorethylen‐, perchlorethylen‐ und 1,1,1‐trichlorethanhaltigen Lösungsmitteln erfährt, wurde untersucht. Mischungen mit Ethern, insbesondere mit Tetrahydrofuran (THF), zeigen gesteigerte korrosive Eigenschaften. Eine Oberflächenphase, bestehend aus FeCl2 · 4H2O und β‐FeOOH, bildet sich auf dem Kohlenstoffstahl in diesen Lösungsmitteln aus. Die Gemische mit THF greifen auch nichtrostende Chrom‐Nickel‐(Molybdän)‐Stähle an. Bei Gegenwart von FeCl3 wird dieser Angriff erhöht. Kupfer wird ebenfalls angegriffen.
The Electrochemical and Stress Corrosion Behaviour of an Austenitic Stainless Steel in phosphate solutions at high temperatures and pressures
Authors: Tischner H. , Wendler‐Kalsch E. , Kaesche H.
Published: May 2005

The present investigation concerns the effects of stress corrosion on the behaviour of high‐alloy steels in high‐pressure, high‐temperature phosphate solutions, with the view on service conditions in the secondary loop of pressurized water reactors.

An apparatus is described which enables electrochemical and electrochemically controlled stress‐corrosion experiments up to 300° C with tensile specimens stressed with a defined stress by a bellows arrangement.

The polarization curves of a model system of X 5 CrNi 189 stainless steel (AISI Type 304) and 0.4 M Na2HPO4/0.4 M NaH2PO4 solution exhibit a large increase in current densities at higher temperatures at all potentials investigated. However, the material proves to be spontaneously passive even at 300° C, although the passive current densities are about 10–15 times higher than those at room temperature.

Stress‐corrosion experiments at open circuit potential and under potentiostatic control show that high stresses and exposure times of more than 100 h are necessary to cause cracking.

In addition, some possible effects of thick phosphate layers on the sample surface on the corrosion behaviour of the material are mentioned.
Contribution to the discussion on Localized Corrosion of Stainless Steels in natural sea water
Authors: Mor E. D. , Scotto V. , Mollica A.
Published: May 2005

Electrochemical hysteresis methods are employed to develop experimental potential‐pH diagrams for some commercial austenitic and ferritic stainless steels in 3% sodium chloride solutions at room temperature. The results were compared with the electrochemical and the gravimetric behaviour of the single stainless steels in natural sea water. The comparison suggested some considerations about the mechanism of initiation and growth of pitting and crevice corrosion prevailing in natural environment. The higher probability of pits observed in field exposure was correlated to the deposit of a microbiological slime on metal surface that ennobles the free corrosion potentials of passive surfaces up to +400 ÷ +450 m V SCE. The crevice corrosion initiation was in turn attributed to a moderate local acidification originating in conditions of reduced diffusion under the action of passivity current that makes possible pit nucleation which is otherwise unlikely to occur. The pitting growth speeds up the acidification process in the interstice until it causes general corrosion of the walls.
Tertiary Arsines as Corrosion Inhibitors for Zinc in acid solution
Authors: Rudresh H. B. , Mayanna S. M.
Published: May 2005

Tertiary arsines such as diphenylethyl arsine (DPEA), diphenylmethyl arsine (DPMA) and triphenyl arsine (TPA) have been used as corrosion inhibitors for zinc in perchloric acid solution. These inhibitors inhibit corrosion effectively even in traces. The percentage inhibitor efficiency of the inhibitors are in the order DPEA > DPMA > TPA. The effect of pH and temperature on the inhibitor efficiency is studied. Steady state anodic and cathodic polarization data reveal that tertiary arsines act as interfacial corrosion inhibitors for zinc in acidic solution. The apparent free energies of adsorption of inhibitors have been reported for different possible modes of adsorption.