Can the Sterilization Protocol Be Improved to Enhance the Healing of Allograft Tendons? An In Vivo Study in Rabbit Tendons
Authors: Zhang Haoran , Xu Mingyou , Zhao Yiwei , Li Zhiyi , Han Bingtai , Wang Shengru , Zhang Jingyu , Zhang Jianguo , Hu Yongcheng 
Published: March 2024

Background

Peracetic acid and irradiation are common sterilization methods for allograft tendons; however, under some conditions, both methods adversely affect the fiber arrangement and ultimate load of the tendon. An in vitro study showed that low-dose peracetic acid combined with irradiation may be less detrimental to allograft tendon structure and properties, possibly because the breakdown of peracetic acid can lead to an enlargement of the interstitial spaces and an increase in porosity.

Questions/purposes

Using a rabbit Achilles tendon model, we asked: What is the effect of peracetic acid-ethanol combined irradiation on (1) the histopathology and fiber diameter of the allograft tendon, (2) tensile creep and load-to-failure biomechanical properties of allograft tendons, and (3) healing of the treated tendon in vivo compared with fresh-frozen allograft and peracetic acid-ethanol sterilization at 4 and 8 weeks?

Methods

The Achilles tendons used in this study were sourced from euthanized 10-week-old male New Zealand White rabbits previously used for ophthalmic experiments. All allografts were divided into three groups: fresh-frozen group (control group, n = 20), peracetic acid-ethanol sterilization group (n =20), and peracetic acid-ethanol combined irradiation group (n = 20). The sterilization protocols were performed per a predetermined plan. In the peracetic acid-ethanol sterilization group, the tendon tissues were covered with the peracetic acid-ethanol sterilization solution (1% peracetic acid for 30 minutes). In the peracetic acid-ethanol combined irradiation group, the tendon tissues were covered with the peracetic acid-ethanol sterilization solution (0.2% peracetic acid for 30 minutes) and were subjected to 15 kGy gamma irradiation. Thirty 10-week-old male New Zealand White rabbits received bilateral Achilles tendon allografts surgically. Tendon samples from each group were harvested at 4 weeks (n = 30) and 8 weeks (n = 30) postoperatively. For each timepoint, eight tissues were used for histologic staining and electron microscopy, 15 tissues were used for biomechanical testing, and seven tissues were used for hydroxyproline assay and quantitative polymerase chain reaction. Histopathology was determined qualitatively by hematoxylin and eosin and Masson staining, while fiber diameter was measured quantitatively by transmission electron microscopy. Biomechanical properties were measured using cyclic loading tests and load-to-failure tests. The healing outcome was quantitatively judged through healing-related genes and proteins.

Results

At 4 weeks and 8 weeks postoperatively, the peracetic acid-ethanol combined irradiation group visually demonstrated the best continuity and minimal peripheral adhesions. Histologic staining showed that tendon fibers in the peracetic acid-ethanol combined irradiation group maintained consistent alignment without notable disruptions or discontinuities, and there was a qualitatively observed increase in the number of infiltrating cells compared with the control group at the 4-week timepoint (444 ± 49 /mm2 versus 256 ± 43 /mm2, mean difference 188 /mm2 [95% confidence interval 96 to 281]; p < 0.001). At 8 weeks postoperatively, the tendon fiber diameter in the peracetic acid-ethanol combined irradiation groups was similar to that of the control group (0.23 ± 0.04 µm versus 0.21 ± 0.03 µm, mean difference 0.02 µm [95% CI -0.04 to 0.08]; p = 0.56). At 8 weeks postoperatively, the peracetic acid-ethanol combined irradiation group exhibited better properties in terms of both ultimate load (129 ± 15 N versus 89 ± 20 N, mean difference 40 N [95% CI 7 to 73]; p = 0.02) and energy absorption density (17 ± 6 kJ/m2 versus 8 ± 4 kJ/m2, mean difference 8 kJ/m2 [95% CI 0.7 to 16]; p = 0.004) compared with the control group. Gene expression analysis revealed higher expression levels of COL1A1 (2.1 ± 0.8 versus 1.0 ± 0, mean difference 1.1 [95% CI 0.1 to 2.1]; p = 0.003) and MMP13 (2.0 ± 0.8 versus 1.0 ± 0, mean difference 1.0 [95% CI 0.4 to 1.6]; p = 0.03) in the peracetic acid-ethanol combined irradiation group than in the control group. There was a higher amount of collagen Type I in tendons treated with peracetic acid-ethanol combined irradiation than in the control group (0.36 ± 0.03 versus 0.31 ± 0.04, mean difference 0.05 [95% CI 0.01 to 0.09]; p = 0.02).

Conclusion

Treatment with peracetic acid-ethanol combined irradiation did not have any discernible adverse effect on the histology, fiber diameter, enzymatic resistance, collagen content, or biomechanical strength of the allograft tendons compared with the control group. Peracetic acid-ethanol combined irradiation treatment had a positive impact on remodeling of the extracellular matrix and realignment of collagen fibers.

Clinical Relevance

This sterilization method could be helpful to expand the scope and frequency with which allogeneic materials are applied. The long-term healing effect and strength of allograft tendons must be tested before clinical use, and it is necessary to conduct comparative studies on autografts and synthetic materials that are currently widely used clinically.