Abstract:
Improved tack, green strength or non-black filler interaction capability are realized in a treated diene rubber. The method of treating diene rubber to achieve the improvements is shown, together with a composition in which maleamic acid or derivatives of maleamic acid are combined with sulfur or an organic sulfur compound capable of generating a thiyl radical.

Description:
This Application is a continuation-in-part of Application Ser. No. 322,142, filed Nov. 17, 1981, and now abandoned. 
    
    
     BACKGROUND OF THE INVENTION 
     This invention relates to an improved diene rubber, to a method for treating diene rubber and to a treatment composition comprising maleamic acid or derivatives thereof combined with sulfur or an organic sulfur compound capable of generating a thiyl radical effective in improving the tack, green strength or non-black filler interaction capability of the diene rubber. 
     The introduction of synthetic diene rubber as a total or partial replacement for natural rubber in portions of pneumatic tires and other rubber articles presented problems in that the behavior of the synthetic materials differed from that of natural rubber. One significant area of difference concerned tack and green strength. Typically, unvulcanized synthetic diene rubber has significantly lower green strength and tack properties than does natural rubber. This difference has presented problems in that articles such as tires failed to maintain their structural integrity during handling and shaping prior to vulcanization. As a result, searching for improvements in the green strength and tack of rubber compounds containing synthetic rubber has been a continuing effort. 
     Synthetic polyisoprene has been produced which resembles natural rubber closely, consisting of essentially all cis-1,4-polyisoprene. Perhaps the most significant difference between synthetic polyisoprene and natural rubber is that the former has considerably less green strength and tack. Thus, much of the effort toward green strength and tack improvement concerns synthetic polyisoprene. Other synthetic diene rubbers which are widely used are polybutadiene and styrene-butadiene copolymer rubber (SBR). 
     Efforts to increase the tack and green strength of diene rubber include a variety of treatments such as the addition of a wide variety of resin tackifiers to synthetic rubber compounds. In general, these materials have been ineffective for the desired purpose, primarily because of the inherently lower green strength of the synthetic rubber polymers. U.S. Pat. Nos. 3,151,161 and 3,225,100 teach incorporation of nitrosoanilinoalkanes into rubber, and improvements in green strength have been realized in synthetic rubber thus treated. Problems of dispersion of these materials into rubber have been encountered, compounded by the fact that relatively small amounts are generally used. 
     Additionally, the use of non-black fillers in diene rubber compounds is limited because of the poorer physical properties of vulcanizates as compared to carbon black reinforced rubber. Little interaction appears to occur between non-black fillers and diene rubber, in most instances. 
     SUMMARY OF THE INVENTION 
     It is an object of this invention to provide a composition which comprises diene rubber having improved green strength, tack or non-black filler interaction. It is another object of this invention to provide a method of treating diene rubber so as to improve its green strength, tack or non-black filler interaction. It is yet another object to provide a treatment composition suitable for use in improving the properties of diene rubber. 
     These and other objects are realized in the instant invention by a composition of matter comprising diene rubber treated, in the presence of a modification promoting amount of (A) sulfur or an organic sulfur compound capable of generating thiyl radicals, by (B) a compound of the formula ##STR1## n being an integer of 1-3, wherein R 1  is hydrogen or alkyl of 1-10 carbon atoms and, if n=1, R 2  is selected from hydrogen, alkyl of 1-10 carbon atoms, optionally forming a heterocyclic moiety with the N atom of the formula and R 1 , either with or without an added N or O atom, ##STR2## wherein Y is an oxygen or sulfur atom, x is an integer of 1-12, R 3  is hydrogen, --OH, --COOH, --NO 2 , alkoxy of 1-5 carbon atoms or ##STR3## and R 4  and R 5  are the same or different selected from hydrogen, phenyl and alkyl of 1-10 carbon atoms, including cycloalkyl of from 3 to 10 carbon atoms, optionally forming a heterocyclic moiety together with one or both of the N atoms in the formula, with or without an added hetero N or O atom; if n=2, R 2  is selected from phenylene, divalent aliphatic hydrocarbon radicals of 2-20 carbon atoms and ##STR4## and if n=3, R is s-triazinyl or a trivalent aliphatic hydrocarbon radical of 2-20 carbon atoms, said composition having been treated at an appropriate temperature above 130° C. for a long enough time to impart to the composition improved green strength, tack or non-black filler interaction capability. 
     The instant invention also includes the method of treating diene rubber comprising treating the rubber, in the presence of a modification promoting amount of (A) sulfur or an organic sulfur compound capable of generating thiyl radicals, with (B) a compound of the formula as defined above, at an appropriate temperature above 130° C. for sufficient time to impart to the composition improved green strength, tack or non-black filler interaction capability. 
     Further, the invention includes a composition of matter comprising from 5 to 95 parts by weight of (A) sulfur or an organic sulfur compound capable of generating thiyl radicals and from 95 to 5 parts by weight of (B) a compound of the formula ##STR5## n being an integer of 1-3, wherein R 1  is hydrogen or alkyl of 1-10 carbon atoms and, if n=1, R 2  is selected from hydrogen, alkyl of 1-10 carbon atoms, optionally forming a heterocyclic moiety with the N atom of the formula and R 1 , either with or without an added N or O atom, ##STR6## wherein Y is an oxygen or sulfur atom, x is an integer of 1-12, R 3  is hydrogen, --OH, --COOH, --NO 2 , alkoxy of 1-5 carbon atoms or ##STR7## and R 4  and R 5  are the same or different selected from hydrogen, phenyl and alkyl of 1-10 carbon atoms, including cycloalkyl of from 3 to 10 carbon atoms, optionally forming a heterocyclic moiety together with one or both of the N atoms in the formula with or without an added hetero N or O atom; if n=2, R 2  is selected from phenylene, divalent aliphatic hydrocarbon radicals of 2-20 carbon atoms and ##STR8## and if n=3, R is s-triazinyl or a trivalent aliphatic hydrocarbon radical of 2-20 carbon atoms. 
     The derivatives of maleamic acid which form component (B) as defined above include (in addition to maleamic acid, itself) alkyl amides, for example, N-methyl maleamic acid, N-ethyl maleamic acid, N-propyl maleamic acid, N-isopropyl maleamic acid, N-butyl maleamic acid, N-isobutyl maleamic acid, N-tert-butyl maleamic acid, N-pentyl maleamic acid and N-1,2-dimethylpropyl maleamic acid. N-substituted alkyl carboxy derivatives of maleamic acid are exemplified by N-carboxymethylmaleamic acid, N-carboxyethylmaleamic acid, N-carboxypropylmaleamic acid, N-carboxybutylmaleamic acid, N-carboxyamylmaleamic acid and N-carboxy hexylmaleamic acid and carboxy dodecyl maleamic acid. N-phenyl- and N-substituted-phenyl derivatives are exemplified by N-phenylmaleamic acid and the ortho, meta and para isomers of N-methoxyphenylmaleamic acid, N-ethoxyphenylmaleamic acid, N-propoxyphenylmaleamic acid, and the like, the ortho-, meta- and para-isomers of N-anilinophenylmaleamic acid, and the ortho-, meta- and para-isomers of phenylene-bis-maleamic acid. 
     Carbamoyl and substituted carbamoyl derivatives include N-carbamoylmaleamic acid (sometimes called maleuric acid) and the products of the reaction of one mole of maleic anhydride with one mole of 1,3-dimethylurea, ethylurea, phenylurea, and the like, and the product of the reaction of one mole of melamine with three moles of maleic anhydride. Thiocarbamoyl and substituted thiocarbamoyl derivatives include N-thiocarbamoylmaleamic acid and the products of the reaction of one mole of maleic anhydride with one mole of phenylthiourea, ethylthiourea and the like. 
     Bis-maleamic acid compounds include methylene-bis-maleamic acid, ethylene-bis-maleamic acid, trimethylene-bis-maleamic acid, tetramethylene-bis-maleamic acid, N,N&#39;-bis-(4,4&#39;-dithiophenyl)maleamic acid and phenylene-bis-maleamic acid. 
     Other maleamic acids include 4,4-dithio-bis-(N-phenyl-maleamic acid) and the reaction products of maleic anhydride with N-(1,3-dimethylbutyl)-N&#39;-phenyl-p-phenylenediamine and with 2-imidazolidone. 
     While the compositions and methods of the invention are described as employing a compound (B) which is maleamic acid or a derivative thereof, if desired, two or more of the above listed compounds can be used to form the component (B). 
     Component (A) of the invention is defined as sulfur or an organic sulfur compound capable of generating a thiyl radical. The sulfur compound is preferably a polymeric sulfide or a compound of the formula (R 6  S z ) y  R 7 , wherein z is an integer of 1-5, y is an integer of from 1-4, R 7  is a radical selected from aliphatic hydrocarbon radicals of 3-18 carbon atoms optionally containing one or more ether or ester linkages and optionally substituted by one or more nitro, amino or carboxyl groups; cycloalkyl of 3-10 carbon atoms; benzyl or phenyl optionally ring-substituted by one or more nitro, amino, carboxyl, or 1-5 carbon-atom alkyl grops; or benzothiazyl; dialkylthiocarbamoyl; alkylamino of 4-12 carbon atoms; morpholino or dialkylthiophosphoroyl; R 2  having a valence of y; and R 6  is hydrogen or a radical selected from the same group as R 7 . 
     Such sulfur compounds include, for example, thiokol polymers and phenyl disulfide, 4,4&#39;-diaminophenyldisulfide, 4,4&#39;-dinitrophenyldisulfide, 2,2&#39;-diaminophenyldisulfide, 4,4&#39;-dicarboxyphenyldisulfide, cyclohexyldisulfide, benzyldisulfide, the compound n--C 8  H 17  --S x  --C 8  H 17  --n, where x is an average of 3.5; N,N&#39;-dimorpholinodisulfide, N-t-butyl-2-benzothiazyl sulfenamide, tetramethyl thiuram disulfide; mercaptans, such as n-decyl mercaptan, n-dodecyl mercaptan, phenyl mercaptan and 2-mercaptobenzothiazole; and compounds of the formula Acc--SS--R--SS--Acc, where Acc stands for an accelerator moiety such as benzothiazyl, dialkyldithio carbamoyl, and the like, and R is divalent hydrocarbon radical such as alkylene, p-phenylene, p-xylene and the like. 
     Examples of this latter variety of compounds are ##STR9## A preferred example of (A) is 2,2&#39;-dithiobis-benzothiazole, sometimes known as benzothiazyldisulfide, or MBTS. 
     If sulfur is used as component (A) it can generally be used in lesser amounts than the organic sulfur compounds. The use of too much sulfur may actually reduce tack since appreciable vulcanization may occur during the treatment. 
     By diene rubber is meant an elastomer which is a polymer from diene monomer, either a natural or synthetic polymer, including mixtures of two or more of natural and synthetic polymers. Natural diene rubber includes Hevea rubber, in the form of smoked sheet, crepe or other typical forms, guayule, and other naturally occurring elastomers. Synthetic polymers which are included in the definition of &#34;diene rubber&#34; include polymers from isoprene and butadiene, either homopolymers or copolymers with one or more co-monomers, which can be dienes or other polymerizable materials. For example, copolymers of isoprene or butadiene with styrene, acrylonitrile, isobutylene, or unsaturated carboxy acids and esters such as maleic, fumaric, itaconic, acrylic and methacrylic acids, and methylmethacrylates are included. EPDM rubbers (polymers from ethylene, propylene and a non-conjugated diene monomer) are also included. 
     The invention finds a particular usefulness in use with synthetic polyisoprene of a high cis-1,4 content, and with blends thereof with polybutadiene or SBR (styrene/butadiene copolymer rubber). 
     Component (A) is to be used in reaction promoting amount. This amount can vary, depending on the diene rubber, the particular component (B) employed, the improvement desired and, especially, the nature of the particular component (A) used. In general, the amount is preferably from 0.01 to 15 parts, more preferably from 0.02 to 4 parts and most preferably from 0.05 to 2.5 parts by weight of component (A) per 100 parts by weight of diene rubber. If (A) is sulfur, less than 0.25 parts per 100 parts of treated rubber is preferred. 
     Component (B) can similarly be present in varying amount, but is preferably used at level of from 0.1 to 20 parts, more preferably from 0.2 to 8 parts and most preferably from 0.25 to 5 parts by weight per 100 parts by weight of diene rubber. The use of amounts of either components (A) or (B) which are less than the preferred lower limits can result in insufficient improvement in the desired properties of the diene rubber. Also, the use of amounts of the components in excess of the preferred under limits can be counter-productive. Optimum levels can be easily determined by a few simple experiments. 
     Treatment of the diene rubber means incorporating components (A) and (B) into the rubber, with good dispersion, and maintaining the mixture at the appropriate temperature (above 130° C.) for sufficient time to permit the modification to occur. Preferably the temperature should be at least 150°, more preferably above 160° and most preferably from 160° to 210° C. A convenient method of treating involves admixture of components (A) and (B) into the rubber using the type of high-shear equipment normally used for mixing rubber compounds, such as rubber mills, and, preferably, internal mixer exemplified by Banbury mixers and the like. Such mixing produces a temperature rise in the rubber mixture which can be controlled within the desired temperature range. Alternatively, components (A) and (B) can be incorporated into the diene rubber at a relatively low temperature (below 130° C.) and then the mixture can be heated to the appropriate higher temperature and held for the required time. 
     Preferably, the treatment time will be from 0.1 to 20 minutes, more preferably from 0.5 to 15 minutes and most preferably from 1 to 10 minutes. Shorter treatment times than the preferred minimum can result in insufficient improvement in the desired properties, and longer treatment times than the preferred maximum can be harmful to the rubber. As with the levels of the components, both optimum times and optimum temperatures for a specific combination of ingredients can easily be determined by a limited number of experiments. 
     Other rubber compounding ingredients can optionally be present during the treatment, and the presence of carbon black and/or non-black fillers is preferred. Because of the conditions employed, however, the complete vulcanization system is preferably not present during the treatment, as it could result in a premature curing or scorch of the diene rubber compound. If it is desired to have non-black fillers present in the diene rubber compound, particular advantage is realized by having the fillers present during the treatment step. This method can produce interaction between the non-black filler and the diene rubber so as to obtain better physical properties in the vulcanized compounds. These better physical properties are evidenced in improvements in stress-strain properties among other properties. 
     Preferably, during the treatment step the presence of amines such as antidegradants should be avoided lest they react with component (B) before it can react with the rubber polymer. Such compounding ingredients and others which can react adversely with component (B) should be added after the treatment, either as a separate step or simply added after sufficient reaction time. 
     Often, when treating the diene rubber, amounts of components (A) and (B) will be substantially less than the maximum preferred levels set forth above, such as, for example, less than three parts by weight per 100 parts of diene rubber by weight, but higher amounts can be employed, especially if a &#34;masterbatch&#34; technique is used. This technique can involve treating only a portion of the diene rubber, then subsequently blending the untreated portion into the treated portion. From ten parts or less up to 1,000 parts or more additional rubber can be admixed to the treated rubber, as desired. The additional rubber can be the same as, or different from the rubber originally treated. The masterbatch technique can be effective in providing more efficient use of the masticating equipment, thus allowing higher throughput of rubber. 
     During the treatment step the appropriate amounts of components (A) and (B) are both present in the diene rubber. They can be added separately; however, it has been found to be convenient to add both components together as a mixture in the composition as set forth above. This mixture can be added to the rubber as a simple blend of components (A) and (B), however, alternatively, the rubber treatment composition of matter of the invention, if desired, can advantageously be incorporated into a binder or carrier material, thus forming an additive which is easier to handle and easier to use. Any such binder should, of course, be compatible not only with the composition of the invention, but also with the materials to be treated. According to the method of this invention those materials comprise diene rubber. Organic polymers are suitable binders, and polyolefins, especially polyethylene, are particularly effective. The composition is preferably blended into the binder, using such relative amounts as to achieve a final amount of from 5 to 95 weight percent of the composition of the invention based on the total weight of the mixture of binder and composition. Since the composition is used in relatively small proportions in diene rubber, its incorporation into a mixture with the binder facilitates dispersion of the composition into the diene rubber. Alternatively, the composition can be blended with an inert carrier material for improved dispersion. Clay, or a similar carrier is recommended for this purpose. 
     As mentioned above, the improvement of tack and green strength is of great practical importance. The nature of these two properties in uncured rubber compounds has been explored by a number of investigators. A review of recent developments was recently published, written by G. R. Hamed of the University of Akron, entitled &#34;Tack and Green Strength of Elastomeric Materials&#34;, Rubber Chemistry and Technology, 54, pp. 576-595 (1981). This review brings out the basic fact that tack and green strength are interrelated. Tack has been defined as the ability of two materials to resist separation after bringing their surfaces into contact for a short time under a light pressure. Green strength in an elastomer is its resistance, before vulcanization, to deformation or fracture. Green strength can be determined independently, but tack is dependent to a certain degree on green strength. 
     In general, the compounds which constitute part (B) of the compositions of the invention can be produced by reacting maleic anhydride with ammonia or a primary or secondary amine or amide in an acidic medium, such as glacial acetic acid. The use of acid can be helpful to prevent addition across the double bond of the maleic anhydride molecule. 
    
    
     DETAILED DESCRIPTION 
     A more complete understanding of the invention may be realized by reference to the following examples, in which all parts are by weight, unless otherwise specified. 
     EXMAPLE I 
     N-carbamoyl maleamic acid, one of the preferred compounds for component (B) of the composition of the invention, is prepared as follows: 
     Into a three-neck flask having a three liter capacity are charged 500 g. (5.1 mole) maleic anhydride, 300 g. (4.99 mole) urea and 1,000 ml. glacial acetic acid. The flask is equipped with stirrer, heating mantle with thermostat, a thermometer and a condenser. The reaction mixture is stirred at 50° C. for 48 hours. The precipitate which forms is filtered, washed with 300 ml. acetone, and dried overnight at 60° C. The product of 606 g. of a white solid having a melting point of 164°-165° C. Calculated as N-carbamoyl maleamic acid, the yield was 76.6%. 
     In a similar manner, N-carboxymethyl maleamic acid is prepared by first charging 150.1 g. (2.0 moles) glycine together with 500 ml. glacial acetic acid into a two-liter, three-necked flask equipped with stirrer, heating mantle with thermostat, a thermometer and a condenser. Separately, 196.1 g. (2.0 moles) maleic anhydride and 500 ml. glacial acetic acid is combined, and stirred until a homogeneous mixture is obtained. This mixture is then charged dropwise to the flask, with agitation, over a one-hour period. The temperature is adjusted to 60° C. and the reaction mixture stirred for one hour. The flask is then left overnight, whereupon the precipitate which forms is filtered, washed with acetone as before and dried in a 65° C. oven over the weekend. The yield is 343 g. of a white solid having a melting point of 192°-193° C. The yield calculates to 99.1%. 
     Similarly, t-butylamine is reacted with an equimolar amount of maleic anhydride to produce 97% yield of N-t-butyl maleamic acid, a white crystalline material melting at 138°-142° C. 
     In the same manner, equimolar amounts of 3-aminopropionic acid and maleic anhydride are reacted to produce N-carboxyethylmaleamic acid (M.P. 150°-152° C.) in 68% yield. 
     In a similar manner, equimolar amounts of ethylurea react with maleic anhydride to produce a white crystalline powder (after recrystallization from ethyl acetate) identified as N-(ethylcarbamoyl)maleamic acid, melting at 125°-127° C. 
     Similarly, phenylthiourea is reacted with an equimolar amount of maleic anhydride giving a white solid, N-(phenylthiocarbamoyl)maleamic acid, melting at 200°-202° C. 
     Similarly, equimolar amounts of 2-imidazolidone and maleic anhydride react to produce a white powder melting at 154°-155° C., and identified as having the following formula: ##STR10## 
     In a similar manner, 4-aminophenyl disulfide is reacted with twice its molar equivalent of maleic anhydride to produce N,N&#39;-bis(4,4&#39;-dithiophenyl)maleamic acid, melting (with some decomposition) at 195°-200° C. 
     Similarly, maleic anhydride is reacted in equimolar amounts with ammonia and with 4-amino butanoic acid to produce, respectively, maleamic acid (91% yield, M.P. 176°-177° C.) and N-carboxypropylmaleamic acid (84.5% yield, M.P. 164°-166° C.). 
     In the same manner, two moles of maleic anhydride are reacted with one mole each of hexamethylenediamine and dodecamethylene diamine to produce, respectively, N,N&#39;-hexamethylenebismaleamic acid (95% yield, M.P. 175°-176° C.) and N,N&#39;-dodecamethylenebismaleamic acid (90% yield, M.P. 164°-166° C.). 
     Similarly, equimolar amounts of p-carboxy aniline and maleic anhydride reacted to produce N-(p-carboxyphenyl)maleamic acid. 
     The compounds prepared in Example I are combined with 2,2&#39;-dithiobisbenzothiazole in different weight ratios and the compositions thus formed are tested in rubber for their effect on the green strength and tack of the uncured rubber compounds. The various compositions are easily mixed to homogeneous powdery blends which are quite stable on storage. 
     The compositions thus made are mixed into rubber formulations and masticated according to the method of the invention; then the rubber compounds are tested according to the accepted tests for green strength and tack, as follows. 
     Green strength measurements are performed using a standard tensile testing machine. Samples of the stock to be tested are pressed into slabs approximately three millimeters in thickness, from which slab specimens are die-cut measuring about 20.3×2.4 cm. The specimens are bench marked (to a test length of 2.54 cm.) in the center, and the exact width and thickness is measured. Specimens are pulled at a crosshead speed of 50.8 cm. per minute, with the stress recorded at desired levels of elongation up to 1200%, or break. Stress values are calculated based on the original cross-section area of each specimen, and the maximum stress value is also recorded. 
     Tack measurements are made using the Monsanto Tel-Tak instrument, as described in an article by J. R. Beatty in Rubber Chemistry and Technology, 42, 1040 (1969). Fabric-backed rubber specimens are cut to a width of 6.35 mm and placed at right angles to give a contact area of 0.403 cm 2 . A contact pressure of 227 grams is used for all tests, with a 30-second dwell time. Sample &#34;stickiness&#34; is measured by substituting a polished stainless steel surface for one specimen, and the result is subtracted from the tack value to give a &#34;true tack&#34; measurement. The units of these measurements are in grams per square centimeter, representing the maximum force per unit area required to separate the specimens, at a separation rate of 2.54 cm. per minute. 
     Stress-strain properties of the vulcanizates are measured in the conventional manner. 
     EXAMPLE II 
     The compounds prepared in Example I are combined with 2,2&#39;-dithiobisbenzothiazole (MBTS) in the ratio of 2 to 1, so that the composition contains 331/3% part (A) and 662/3% part (B). Masterbatch compounds as shown in Table I based on Natsyn 2200, a synthetic polyisoprene rubber, are mixed and masticated in a laboratory Banbury mixer according to the following schedule: 
     1. Charge rubber and test compound; mix 1 minute, controlling temperature between 150° and 154° C. 
     2. Charge 1/2 of carbon black; mix 1 minute. 
     3. Charge oil and remainder of carbon black; mix 1 minute. 
     4. Charge remaining ingredients; mix 1 minute. 
     5. Sweep down; mix 1 minute. 
     6. Dump. Actual rubber temperature (using probe) should be 170°-200° C. 
     Masterbatch A is a control with no treating agent. Masterbatch B contains a known treating agent, N-(2-methyl-2-nitropropyl)-4-nitrosoaniline used at its recommended level. 
     
                       TABLE I______________________________________            Masterbatch            A     B      C      D______________________________________PolymerNatsyn 2200        100.0   →                             →                                  →Test CompoundsNITROL ® + Clay              --      0.75   --   --N--Carbamoylmaleamic acid              --      --     1.0  --N--Carboxymethylmaleamic acid              --      --     --   1.0MBTS               --      --     0.5  0.5Other IngredientsN-330 Black        50.0    →                             →                                  →Circosol 4240 Oil  5.0     →                             →                                  →Zinc Oxide         5.0     →                             →                                  →Stearic Acid       2.0     →                             →                                  →Antidegradant      2.0     →                             →                                  →Batch Dump Temp. (Probe) °C.              188     183    182  188______________________________________ *NITROL ® is a registered trade mark for 33% N--(2methyl-2-nitropropyl)-4-nitrosoaniline on an inert carrier. 
    
     The masterbatches are then tested for green strength and tack, as set forth above. Results are shown in Table II following. 
     
                       TABLE II______________________________________             Masterbatch             A     B      C      D______________________________________Green Strength @Room Temp. (MPa)Stress At:100%                0.26    0.31   0.43 0.37300%                0.19    0.40   1.25 1.02400%                0.18    0.54   1.98 1.75U.E., %*            &gt;1200   620    450  450Tack, Monsanto Tel-TakTack                44      66     121  114Stickiness          11      12     12   13&#34;True&#34; Tack         33      54     109  101______________________________________ *Ultimate Elongation 
    
     The data in Table II show that the additives in Masterbatches C and D give significantly better improvements in both green strength and tack than the known material. The control sample shows a drop-off of green stress with increased elongation, whereas all the treating materials reverse this trend. 
     EXAMPLE III 
     To determine the effect of curatives on the green strength and tack of the masterbatches of Example II, sulfur and accelerator are added to each on a mixing mill, and the properties are again measured. Results are set forth in Table III, following. 
     
                       TABLE III______________________________________             Stocks             1    2       3      4______________________________________IngredientsMasterbatch A       164.0Masterbatch B              164.75Masterbatch C                      165.5Masterbatch D                           165.5Sulfur              2.5    →                              →                                   →Accelerator         0.5    →                              →                                   →Test Compound,      --     0.75    1.0  1.0(phr in masterbatch)MBTS (phr in masterbatch)               --     --      0.5  0.5Green Strength @Room Temp. (MPa)Stress At:100%                0.23   0.33    0.32 0.34300%                0.16   0.69    0.72 0.75400%                0.14   1.16    1.16 1.30U.E., %             950    560     520  530Tack, Monsanto Tel-TakTack                36     48      74   65Stickiness          15     14      18   16&#34;True&#34; Tack         21     34      56   59______________________________________ 
    
     The data in Table III indicate that, generally, both green strength and tack are lowered by adding curatives. The compounds of the invention, in Stocks 3 and 4, still show significantly better properties than the controls. 
     EXAMPLE IV 
     In a manner similar to Example II a series of masterbatches is prepared based, in this instance, on SKI-3 polyisoprene rubber (USSR). The treatment compositions are varied, both in the ratio of the components and in the total amount used. The mixing schedule used is the same as that in Example II. Proportions and data are set forth in Table IV. 
     Analysis of the data in Table IV indicates that, at low levels of treatment, such as 0.6 phr (parts per hundred of rubber) in masterbatches G and L, the effect on green strength is minimal, yet tack is significantly better than the control. 
     The green strength and tack values for masterbatch 0 show that, for this particular composition, a relatively high (about 91 to 9) ratio of maleamic acid derivative to MBTS is very effective. 
     
                                           TABLE IV__________________________________________________________________________              Masterbatch              E   F  G  H  I  J  K  L  M  N  O  P__________________________________________________________________________Polymer, Test CompoundsSKI-3 Polyisoprene 100.0                  →                     →                        →                           →                              →                                 →                                    →                                       →                                          →                                             →                                                →NITROL + Clay      --  0.75                     -- -- -- -- -- -- -- -- -- --N--carbamoylmaleamic acid              --  -- 0.5                        0.5                           0.75                              1.0                                 1.0                                    -- -- -- -- --N--carboxymethylmaleamic              --  -- -- -- -- -- -- 0.5                                       0.5                                          0.75                                             1.0                                                1.0acidMBTS               --  -- 0.1                        0.5                           0.3                              0.1                                 0.5                                    0.1                                       0.5                                          0.3                                             0.1                                                0.5Other IngredientsN-330 Black        50.0                  →                     →                        →                           →                              →                                 →                                    →                                       →                                          →                                             →                                                →Circosol 4240 Oil  5.0 →                     →                        →                           →                              →                                 →                                    →                                       →                                          →                                             →                                                →Zinc Oxide         5.0 →                     →                        →                           →                              →                                 →                                    →                                       →                                          →                                             →                                                →Stearic Acid       2.0 →                     →                        →                           →                              →                                 →                                    →                                       →                                          →                                             →                                                →Antidegradant      2.0 →                     →                        →                           →                              →                                 →                                    →                                       →                                          →                                             →                                                →Masterbatch Temp. at              188 185                     191                        185                           185                              187                                 188                                    185                                       185                                          185                                             188                                                191Dump, °C.Green Strength @ Room Temp. (MPa)Stress At:100%               0.23                  0.24                     0.25                        0.25                           0.26                              0.27                                 0.30                                    0.26                                       0.26                                          0.26                                             0.30                                                0.33300%               0.17                  0.30                     0.21                        0.30                           0.35                              0.25                                 0.70                                    0.23                                       0.33                                          0.42                                             0.43                                                0.79400%               0.15                  0.43                     0.23                        0.40                           0.52                              0.29                                 1.27                                    0.23                                       0.45                                          0.66                                             0.68                                                1.39U.E., %            &gt;1200                  610                     970                        730                           610                              800                                 480                                    970                                       650                                          600                                             590                                                480Tack, Monsanto Tel-TakTack               42  69 51 69 73 50 113                                    49 74 74 88 40Stickiness         24  25 30 31 22 23 21 16 28 18 16 17&#34;True&#34; Tack        18  44 21 38 51 27 92 33 46 56 72 23__________________________________________________________________________ 
    
     EXAMPLE V 
     This example shows the operation of the masterbatch technique, treating a portion of diene rubber with a high level of treating composition and blending with additional diene rubber. 
     In a manner similar to that of Example II, masterbatches Q and R were prepared and masticated. The following recipes were used: 
     
         ______________________________________            Parts by WeightMaterial           Q         R______________________________________Natsyn 2200 Polyisoprene              100.0     --Natural Rubber (SMR 5-CV)              --        100.0N-330 Carbon Black 15.0      50.0N--carbamoylmaleamic acid              8.5       8.5MBTS               1.5       1.5Circosol 4240 Oil  --        5.0Zinc Oxide         --        5.0Stearic Acid       --        2.0Antidegradant      --        2.0TOTAL              125.0     174.0______________________________________ 
    
     Masterbatches Q and R were then mixed with additional natural or synthetic polyisoprene rubber and other compounding ingredients, and the mixtures were tested for green strength and tack as before. Proportions and test results are set forth in Table V. 
     
                                           TABLE V__________________________________________________________________________             Mixtures             5   6  7  8  9  10__________________________________________________________________________AdditionsNatsyn 2200 Polyisoprene             100.0                 90.0                    90.0                       -- -- --Natural Rubber (SMR-5 CV)             --  -- -- 100.0                          90.0                             90.0N-330 Carbon Black             50.0                 →                    →                       →                          →                             →Circosol 4240 Oil 5.0 →                    →                       →                          →                             →Masterbatch Q     --  12.5                    -- -- 12.5                             --Masterbatch R     --  -- 17.4                       -- -- 17.4Zinc Oxide        5.0 →                    →                       →                          →                             →Stearic Acid      2.0 →                    →                       →                          →                             →Antidegradant     2.0 →                    →                       →                          →                             →Green Strength at Room Temp., MpaStress At:100%              0.29                 0.41                    0.40                       0.46                          0.45                             0.50300%              0.26                 0.37                    0.40                       0.63                          0.83                             1.03400%              0.27                 0.43                    0.45                       0.94                          1.33                             1.61U.E., %           &gt;1200                 830                    840                       590                          540                             510Tack, Monsanto Tel-TakTack              56  72 72 90 90 99Stickiness        13  15 13 13 11 12&#34;True&#34; Tack       43  57 59 77 79 87__________________________________________________________________________ 
    
     The data in Table V show that the treatment of a relatively small amount of rubber with a relatively high level of treating composition produces a masterbatch which can then be blended with additional rubber to impart improved green strength and tack thereto. 
     Masterbatches Q and R are treated with 10 parts by weight of the treating compound, per 100 parts of synthetic polyisoprene and natural rubber, respectively. The masterbatches are then added to additional rubber at a ratio of one part masterbatch to nine parts rubber (based on the rubber content). 
     The test data show that the green strength and tack of both synthetic polyisoprene and natural rubber were improved by addition of the masterbatch. The natural rubber tack was only marginally increased, but substantial green strength improvements were achieved in all mixtures. 
     EXAMPLE VI 
     In order to evaluate several compounds for their effectiveness as component (A) of the composition of the invention, a series of masterbatches was run. N-carbamoylmaleamic acid was used as component (B), and MBTS, diphenyldisulfide, and 4,4&#39;-dinitrodiphenyldisulfide as component (A). The masterbatches were compounded as shown in Table VI and were mixed and masticated in the same manner as in Example II. The results of green strength and tack tests are also shown in Table VI. 
     
                       TABLE VI______________________________________Masterbatch      S       T      U    V    W______________________________________PolymerNatsyn 2200      100.0   →                           →                                →                                     →Test CompoundsNITROL + Clay    --      0.75   --   --   --N--carbamoylmaleamic acid            --      --     1.0  1.0  1.0MBTS             --      --     0.5  --   --Diphenyldisulfide            --      --     --   0.5  --4,4&#39;-dinitrodiphenyldisulfide            --      --     --   --   0.5Other IngredientsN-330 Black      50.0    →                           →                                →                                     →Circosol 4240 Oil            5.0     →                           →                                →                                     →Zinc Oxide       5.0     →                           →                                →                                     →Stearic Acid     2.0     →                           →                                →                                     →Antidegradant    2.0     →                           →                                →                                     →Green Strength @ R.T., MPaStress At:100%             0.30    0.37   0.42 0.35 0.33300%             0.19    0.48   0.81 0.40 0.54400%             0.17    0.64   1.34 0.58 0.80U.E., %          &gt;1200   610    490  690  590Tack, Monsanto Tel-TakTack             50      80     93   69   82Stickiness       14      15     16   14   15&#34;True&#34; Tack      36      65     77   55   67______________________________________ 
    
     The test data in Table VI show that both diphenyl disulfide and 4,4&#39;-dinitrodiphenyldisulfide are effective in the composition of the invention, but neither is as effective as MBTS. 
     EXAMPLE VII 
     A number of maleamic acid derivatives, together with maleamic acid itself are compared for their effect on the green strength and tack of synthetic polyisoprene, Natsyn 2200. MBTS was combined with each, in an amount of 0.15 parts compared with 0.85 parts of maleamic acid or derivative, based on 100 parts of rubber by weight. 
     Each masterbatch contained the following additional ingredients, expressed as parts by weight per 100 parts of rubber: 
     
         ______________________________________N-330 Carbon Black             50.0Circosol 4240 Oil 5.0Zinc Oxide        5.0Stearic Acid      2.0Antidegradant     2.0______________________________________ 
    
     The ingredients in each masterbatch were added and masticated in the same manner as in Example II, as shown in Table VII. Test data on green strength and tack are also set forth. 
     
                                           TABLE VII__________________________________________________________________________              X   Y  Z  AA AB  AC AD AE AF AG__________________________________________________________________________Test IngredientN--carbamoylmaleamic Acid              --  0.85N--Carboxyethylmaleamic Acid              --  -- 0.85N--t-Butylmaleamic Acid              --  -- -- 0.85N--Cyclohexylmaleamic Acid              --  -- -- -- 0.85N--phenylmaleamic Acid              --  -- -- -- --  0.85Maleamic Acid      --  -- -- -- --  -- 0.85N--4-Carboxyphenylmaleamic Acid              --  -- -- -- --  -- -- 0.85N,N&#39;--hexamethylene-bis-              --  -- -- -- --  -- -- -- 0.85maleamic AcidN--4-diphenylaminomaleamic Acid              --  -- -- -- --  -- -- -- -- 0.85MBTS               --  0.15                     →                        →                           →                               →                                  →                                     →                                        →                                           →Masterbatch Temp. at Dump, °C.              191 197                     197                        195                           194 191                                  193                                     194                                        193                                           189Green Strength @ Room Temp., MpaStress At:100%               0.31                  0.32                     0.28                        0.27                           0.36                               0.25                                  0.30                                     0.32                                        0.27                                           0.28300%               0.27                  0.50                     0.31                        0.23                           0.19                               0.20                                  0.32                                     0.48                                        0.29                                           0.21400%               0.23                  0.78                     0.39                        0.23                           0.19                               0.19                                  0.39                                     0.69                                        0.33                                           0.21U.E., %            &gt;1200                  520                     760                        1100                           &gt;1200                               1180                                  730                                     540                                        760                                           &gt;1200Tack, Monsanto Tel-TakTack               34  89 67 48 46  43 89 88 57 52Stickiness         18  16 20 28 25  34 8  31 18 20&#34;True&#34; Tack        16  73 47 20 21  9  77 57 39 32__________________________________________________________________________ 
    
     The data in Table VII show that the various derivatives of maleamic acid are effective, together with MBTS, in improving the green strength or tack or both of synthetic polyisoprene, as is maleamic acid itself. 
     EXAMPLE VIII 
     N-Carbamoylmaleamic acid and N,N&#39;-(4,4&#39;-dithiophenyl)bis-maleamic acid are compared, together with MBTS, for their effect on the green strength and tack of Natsyn 2200. 
     The ingredients, as set forth in Table VIII, are combined as in Example II. Data on green strength and tack are shown. 
     From the data in Table VIII, it is apparent that both masterbatches AK and AL, treated according to the method of the invention, give significant improvements in both the green strength and tack of Natsyn 2200. In fact, both exhibit better green strength and tack than either the masterbatch treated with the known agent (AI) or the masterbatch made from natural rubber (AH). 
     
                       TABLE VIII______________________________________          AH   AI      AJ     AK   AL______________________________________PolymerNatural Rubber (SMR 5-CV)            100.0  --      --   --   --Natsyn 2200      --     100.0   →                                →                                     →Test CompoundsNITROL + Clay    --     --      0.75 --   --N--Carbamoylmaleamic Acid            --     --      --   0.85 --N,N&#39;--(4,4&#39;-dithiophenyl)-bis-            --     --      --   --   0.85maleamic acidMBTS             --     --      --   0.15 0.15Other IngredientsN-330 Carbon Black            50.0   →                           →                                →                                     →Circosol 4240 Oil            5.0    →                           →                                →                                     →Zinc Oxide       5.0    →                           →                                →                                     →Stearic Acid     2.0    →                           →                                →                                     →Antidegradant    2.0    →                           →                                →                                     →Green Strength @Room Temp., MPa Stress At:100%             0.33   0.24    0.28 0.29 0.29300%             0.40   0.17    0.35 0.48 0.42400%             0.56   0.15    0.48 0.64 0.58U.E., %          600    &gt;1200   560  520  580Tack, Monsanto Tel-TakTack             50     43      64   88   77Stickiness       11     12      14   17   24&#34;True&#34; Tack      39     31      50   71   53______________________________________ 
    
     
                       TABLE IX______________________________________             AM   AN       AO______________________________________PolymerNatsyn 2200         100    →                            →                                 →                                     →Test CompoundsN--Carbamoylmaleamic Acid               --           0.85     --N--(Phenylthiocarbamoyl)maleamic Acid               --           --       0.85MBTS                --           0.15     0.15Other IngredientsN-330 Carbon Black  50.0   →                            →                                 →                                     →Circosol 4240 Oil   5.0    →                            →                                 →                                     →Zinc Oxide          5.0    →                            →                                 →                                     →Stearic Acid        2.0    →                            →                                 →                                     →Antidegradant       2.0    →                            →                                 →                                     →Green Strength @ Room Temp., MPaStress At:100%                0.37         0.40     0.40300%                0.37         0.92     0.62400%                0.41         1.41     0.80U.E., %             820          460      610Tack, Monsanto Tel-TakTack                56           82       75Stickiness          14           17       17&#34;True&#34; Tack         42           65       58______________________________________ 
    
     EXAMPLE IX 
     The data in Table IX show that treatment with either N-carbamoylmaleamic acid and MBTS or N-(Phenylthiocarbamoyl)maleamic acid and MBTS produces significant increases in the green strength and tack of synthetic polyisoprene. 
     EXAMPLE X 
     Several compounds are compared as part (A) of the composition, together with N-carbamoylmaleamic acid. Formulations and test results are set forth in Table X. The treatment was performed as in Example II. 
     As shown in Table X, the various part (A) components are all effective, in combination with N-carbamoylmaleamic acid, to improve the green strength and tack of Natsyn 2200. Without N-carbamoylmaleamic acid (Masterbatches AU, AW, AY, BA) the treatment is ineffective. Best results are obtained using MBTS. 
     
                                           TABLE X__________________________________________________________________________             AP  AQ AR AS AT AU AV AW  AX AY  AZ BA__________________________________________________________________________PolymerNatsyn 2200       100.0                 →                    →                       →                          →                             →                                →                                   →                                       →                                          →                                              →                                                 →Test CompoundsN--Carbamoylmaleamic Acid             --  1.0                    0.8                       0.8                          0.8                             -- 0.8                                   --  0.8                                          --  0.8                                                 --MBTS              --  -- -- 0.2                          -- -- -- --  -- --  -- --Sulfur            --  -- -- -- 0.05                             0.05                                -- --  -- --  -- --n-C.sub.8 H.sub.17 S.sub.x C.sub.8 H.sub.17.n             --  -- -- -- -- -- 0.2                                   0.2 -- --  -- --Cyclohexyldisulfide             --  -- -- -- -- -- -- --  0.2                                          0.2 -- --Benzyldisulfide   --  -- -- -- -- -- -- --  -- --  0.2                                                 0.2Other IngredientsN-330 Carbon Black             50.0                 →                    →                       →                          →                             →                                →                                   →                                       →                                          →                                              →                                                 →Circosol 4240 Oil 5.0 →                    →                       →                          →                             →                                →                                   →                                       →                                          →                                              →                                                 →Zinc Oxide        5.0 →                    →                       →                          →                             →                                →                                   →                                       →                                          →                                              →                                                 →Stearic Acid      2.0 →                    →                       →                          →                             →                                →                                   →                                       →                                          →                                              →                                                 →Antidegradant     2.0 →                    →                       →                          →                             →                                →                                   →                                       →                                          →                                              →                                                 →Green Strength @ Room Temp., MPaStress At:100%              0.27                 0.32                    0.32                       0.32                          0.32                             0.28                                0.32                                   0.26                                       0.32                                          0.27                                              0.33                                                 0.27300%              0.18                 0.32                    0.28                       0.44                          0.31                             0.23                                0.31                                   0.21                                       0.29                                          0.21                                              0.32                                                 0.21400%              0.17                 0.39                    0.31                       0.63                          0.39                             0.23                                0.37                                   0.21                                       0.33                                          0.19                                              0.39                                                 0.19U.E., %           &gt;1200                 730                    840                       550                          730                             1100                                790                                   &gt;1200                                       810                                          &gt;1200                                              770                                                 &gt;1200Tack, Monsanto Tel-TakTack              47  69 60 86 71 47 52 48  71 49  65 47Stickiness        16  17 16 15 16 16 12 16  16 14  15 15&#34;True&#34; Tack       31  52 44 71 55 31 40 32  55 35  50 32__________________________________________________________________________ 
    
     EXAMPLE XI 
     In order to evaluate the effect of the treatment of the invention upon non-black filled rubber, several filler materials are incorporated into Natsyn 2200 polyisoprene. The fillers are clays, of various types, identified as follows. The NUCAP samples were included as recommended for their improved reinforcing properties. 
     
         ______________________________________Designation     Type______________________________________NUCAP 100       Mercapto-functional Clay           0.3 micronNUCAP 290       Mercapto-functional Clay           0.3 micronPOLYFIL DL      Water-washed Clay, 1.0 micronPOLYFIL HG-90   Water-washed Clay, 0.3 micronSUPREX CLAY     Air-floated Clay, 0.3 micronPARAGON CLAY    Air-floated Clay, 1.3 micron______________________________________ 
    
     The various clays are incorporated into masterbatches in the same manner as in Example II and tested for green strength and tack as shown in Table XI. 
     The data in Table XI indicate generally lower green strength for all masterbatches, as would be expected with clay fillers as compared with carbon black. The increase in green strength for those clay samples which contained the composition of the invention is substantial. Modest increases in tack are seen, except in the case of air-floated clays, which are significantly improved by the treatment. 
     
                                           TABLE XI__________________________________________________________________________             Masterbatch             BB BC BD BE BF BG BH BI BJ BK__________________________________________________________________________PolymerNatsyn 2200       100                →                   →                      →                         →                            →                               →                                  →                                     →                                        →Test CompoundsN--Carbamoylmaleamic Acid             -- -- -- 1.70                         -- 1.70                               -- 1.70                                     -- 1.70MBTS              -- -- -- 0.30                         -- 0.30                               -- 0.30                                     -- 0.30Other IngredientsNUCAP 100         72.0                -- -- -- -- -- -- -- -- --NUCAP 290         -- 72.0                   -- -- -- -- -- -- -- --Polyfil DL        -- -- 72.0                      72.0                         -- -- -- -- -- --Polyfil HG-90     -- -- -- -- 72.0                            72.0                               -- -- -- --Suprex Clay       -- -- -- -- -- -- 72.0                                  72.0                                     -- --Paragon Clay      -- -- -- -- -- -- -- -- 72.0                                        72.0Zinc Oxide        5.0                →                   →                      →                         →                            →                               →                                  →                                     →                                        →Stearic Acid      2.0                →                   →                      →                         →                            →                               →                                  →                                     →                                        →Antioxidant       1.0                →                   →                      →                         →                            →                               →                                  →                                     →                                        →Green Strength @ Room Temp., MPaStress At:100%              0.17                0.16                   0.15                      0.28                         0.12                            0.17                               0.15                                  0.23                                     0.12                                        0.19300%              0.09                0.08                   0.07                      0.56                         0.06                            0.23                               0.08                                  0.45                                     0.04                                        0.30400%              0.08                0.07                   0.06                      0.74                         0.05                            0.28                               0.07                                  0.61                                     0.03                                        0.41U.E., %           690                600                   890                      475                         450                            700                               725                                  445                                     290                                        595Tack, Monsanto Tel-TakTack              38 35 37 44 35 38 41 55 38 53Stickiness        16 28 19 19 15 20 21 17 16 15&#34;True&#34; Tack       22 7  18 25 21 18 20 38 22 38__________________________________________________________________________ 
    
     The masterbatches are then further mixed with sulfur and accelerators, and the stocks are tested for stress-strain properties as shown in Table XII. 
     The data on the cured stocks 11-20 in Table XII show that, while the treatment of the invention slows cure times somewhat, it produces stocks having much higher 300% moduli. For example, Stocks 14, 16, 18, and 20 show a 300% modulus which is 54%, 44%, 77% and 80% higher, respectively, than Stocks 13, 15, 17 and 19. Thus the treatment has the added, unexpected advantage of greatly increasing the reinforcing effect of clay fillers. 
     EXAMPLE XII 
     Other non-black fillers are compared for the effect on rubber stocks of the treatment of the invention. In the same manner as Example II, various non-black fillers are incorporated into Natsyn 2200 masterbatches and tested for green strength and tack, as indicated in Table XIII. The following is an identification of the fillers: 
     
         ______________________________________Designation    Type______________________________________Mistron Super Frost          Talc, 2 micronsStanwhite 500  Wet-ground CaCO.sub.3, 5.3 micronsHi-Sil 233     Precipated Silica, 0.022          micron______________________________________ 
    
     The NUCAP clays were also included as in Example XI. 
     
                                           TABLE XII__________________________________________________________________________          Stocks          11 12 13 14 15 16 17 18 19 20__________________________________________________________________________MasterbatchBB             180.0             -- -- -- -- -- -- -- -- --BC             -- 180.0                -- -- -- -- -- -- -- --BD             -- -- 180.0                   -- -- -- -- -- -- --BE             -- -- -- 182.0                      -- -- -- -- -- --BF             -- -- -- -- 180.0                         -- -- -- -- --BG             -- -- -- -- -- 182.0                            -- -- -- --BH             -- -- -- -- -- -- 180.0                               -- -- --BI             -- -- -- -- -- -- -- 182.0                                  -- --BJ             -- -- -- -- -- -- -- -- 180.0                                     --BK             -- -- -- -- -- -- -- -- -- 182.0CurativesSulfur         2.5             →                →                   →                      →                         →                            →                               →                                  →                                     →N--t-butyl-2-benzothiazyl          1.25             →                →                   →                      →                         →                            →                               →                                  →                                     →SulfenamideTetramethylthiuram disulfide          0.30             →                →                   →                      →                         →                            →                               →                                  →                                     →Cure Time, Minutes          14 14 15 19 14 19 12 17 15 20Hardness, Shore A          63 65 66 70 64 67 62 68 62 65Stress at Indicated Strain, MPa100%           3.47             3.69                3.61                   5.53                      2.48                         3.05                            2.70                               4.36                                  2.46                                     3.65200%           6.38             7.38                4.37                   8.54                      3.81                         5.27                            4.38                               7.79                                  3.72                                     6.42300%           9.36             11.21                7.50                   11.56                      5.45                         7.83                            6.41                               11.34                                  5.21                                     9.38Break Stress   21.86             21.28                16.86                   13.35                      19.33                         10.93                            20.31                               15.49                                  18.56                                     12.67Break Strain, %          516             479                482                   339                      556                         384                            549                               385                                  542                                     376__________________________________________________________________________ 
    
     
                                           TABLE XIII__________________________________________________________________________             Masterbatch             BL BM BO BP BQ BR  BS  BT__________________________________________________________________________PolymerNatsyn 2200       100.0                →                   →                      →                         →                            →                                →                                    →Test CompoundN--Carbamoylmaleamic Acid             -- -- -- 1.70                         -- 1.70                                --  1.70MBTS              -- -- -- 0.30                         -- 0.30                                --  0.30Other IngredientsNUCAP 100         72.0                -- -- -- -- --  --  --NUCAP 290         -- 72.0                   -- -- -- --  --  --Mistron Super Frost             -- -- 76.0                      76.0                         -- --  --  --Stanwhite 500     -- -- -- -- 75.0                            75.0                                --  --Hi-Sil 233        -- -- -- -- -- --  56.0                                    56.0Zinc Oxide        5.0                →                   →                      →                         →                            →                                →                                    →Stearic Acid      2.0                →                   →                      →                         →                            →                                →                                    →Antioxidant       1.0                →                   →                      →                         →                            →                                →                                    →Triethanolamine   -- -- -- -- -- --  1.0 1.0Green Strength @ Room Temp., MPaStress At:100%              0.16                0.14                   0.15                      0.38                         0.10                            0.16                                0.34                                    0.55300%              0.05                0.07                   0.06                      0.78                         0.03                            0.12                                0.27                                    1.59400%              -- 0.05                   0.04                      0.89                         0.02                            0.12                                0.28                                    2.50U.E., %           300                450                   610                      430                         400                            &gt;1200                                &gt;1200                                    480Tack, Monsanto Tel-TakTack              39 37 36 48 37 43  54  81Stickiness        17 17 21 14 14 17  17  16&#34;True&#34; Tack       22 20 15 34 24 26  37  65__________________________________________________________________________ 
    
     The data in Table XIII show some increase in tack for the masterbatches treated according to the invention, and more increase in green strength. The improvements in each property were greater for the masterbatches containing the talc and silica than those containing calcium carbonate. 
     As in Example XI, the masterbatches are then completely compounded and tested for cured properties as shown in Table XIV. 
     Again, as in Example XI, the 300% moduli of the cured stocks which were treated according to the invention are higher than the untreated stocks by 65%, 99% and 71%, respectively. 
     
                                           TABLE XIV__________________________________________________________________________          Stocks          21 22 23 24 25 26 27 28__________________________________________________________________________MasterbatchesBL             180.0BM             -- 180.0BO             -- -- 184.0BP             -- -- -- 186.0BQ             -- -- -- -- 183.0BR             -- -- -- -- -- 185.0BS             -- -- -- -- -- -- 165.0BT             -- -- -- -- -- -- -- 167.0CurativesSulfur         2.50             →                →                   →                      →                         →                            →                               →N--t-butyl-2-benzothiazyl          1.25             →                →                   →                      →                         →                            →                               →SulfenamideTetramethylthiuram Disulfide          0.30             →                →                   →                      →                         →                            →                               →Cure Time, Minutes          18 20 20 20 20 20 10 12Hardness, Shore A          62 66 69 72 62 63 65 71Stress at Indicated Strain, MPa100%           3.30             3.51                3.92                   6.57                      1.62                         2.59                            1.49                               2.37200%           6.01             6.97                5.34                   9.29                      2.14                         4.23                            2.62                               4.52300%           8.60             10.49                7.18                   11.87                      3.08                         6.12                            4.27                               7.32Break Stress   18.97             18.20                21.05                   19.11                      11.96                         9.65                            25.48                               25.73Break Strain, %          509             456                535                   439                      502                         394                            739                               644__________________________________________________________________________ 
    
     EXAMPLE XIII 
     For further screening of compounds effective as component (A) of the composition of the invention, the following compounds are evaluated and compared with MBTS in combination with N-carbamoylmaleamic acid. 
     
         __________________________________________________________________________Material    Identification__________________________________________________________________________Morfax ®       2-(morpholinodithio)benzothiazoleVulcanizing Agent A        ##STR11##Thiurad ®       tetramethylthiuram disulfideVulcanizing Agent B        ##STR12##Methyldithiopropionate       (SCH.sub.2CH.sub.2COOCH.sub.3).sub.2Sulfasan ® R       dimorpholino disulfideSantocure ® NS       Nt-butyl-2-benzothiazyl sulfenamideThiokol ® LP 32       Organic Polysulfide, 4000 m.w.__________________________________________________________________________ 
    
     The compounds were incorporated into the rubber and masticated using the procedure of Example II. 
     Formulations and the results of green strength and tack testing are set forth in Table XV. 
     The data in Table XV show that all of the compounds used as component (A) of the composition are, to varying degrees, effective in improving the properties of synthetic polyisoprene. MBTS is clearly superior to the others in this experiment. 
     EXAMPLE XIV 
     In order to evaluate the effect of the treatment method on blends of natural rubber and SBR, a series of trials at 50/50 and 25/75 NR/SBR blend ratios is prepared. The treatment is performed as in Example II, and the combination of MBTS and N-carbamoylmaleamic acid is used, at several levels. The masterbatches and the green strength and tack test results are set forth in Table XVI. 
     The masterbatches are then fully compounded and the resultant stocks cured and tested, as shown in Table XVII. (It should be noted that the SBR rubbers contain oil, so that allowance must be made in the formulas for this.). 
     The data in Table XVI show that increasing amounts of the composition of the invention produce increasing green strength in the 50/50 NR/SBR blends and the 25/75 NR/SBR blends. Tack is increased in the 50/50 blends, but is essentially unimproved in the 25/75 blends. 
     The data in Table XVII show that increasing levels of the composition of the invention increase the 300% modulus of stocks made from both blends. 
     
                                           TABLE XV__________________________________________________________________________             BU  BV BW BX BY BZ CA CB CC CD__________________________________________________________________________PolymerNatsyn 2200       100.0                 →                    →                       →                          →                             →                                →                                   →                                      →                                         →Test CompoundsN--Carbamoylmaleamic acid             --  0.8                    →                       →                          →                             →                                →                                   →                                      →                                         →MBTS              --  0.2                    -- -- -- -- -- -- -- --Morfax            --  -- 0.2                       -- -- -- -- -- -- --Vulcanizing Agent A             --  -- -- 0.2                          -- -- -- -- -- --Thiurad           --  -- -- -- 0.2                             -- -- -- -- --Vulcanizing Agent B             --  -- -- -- -- 0.2                                -- -- -- --Methyldithiopropionate             --  -- -- -- -- -- 0.2                                   -- -- --Sulfasan R        --  -- -- -- -- -- -- 0.2                                      -- --Santocure NS      --  -- -- -- -- -- -- -- 0.2                                         --Thiokol LP 32     --  -- -- -- -- -- -- -- -- 0.2Other IngredientsN-330 Carbon Black             50.0                 →                    →                       →                          →                             →                                →                                   →                                      →                                         →Circosol 4240 Oil 5.0 →                    →                       →                          →                             →                                →                                   →                                      →                                         →Zinc Oxide        5.0 →                    →                       →                          →                             →                                →                                   →                                      →                                         →Stearic Acid      2.0 →                    →                       →                          →                             →                                →                                   →                                      →                                         →Antidegradant     2.0 →                    →                       →                          →                             →                                →                                   →                                      →                                         →Green Strength @ Room Temp., MPaStress At:100%              0.26                 0.32                    0.32                       0.33                          0.30                             0.29                                0.30                                   0.30                                      0.32                                         0.33300%              0.19                 0.53                    0.38                       0.35                          0.26                             0.25                                0.26                                   0.41                                      0.34                                         0.31400%              0.17                 0.79                    0.48                       0.43                          0.28                             0.28                                0.28                                   0.56                                      0.47                                         0.37U.E., %           &gt;1200                 540                    720                       740                          1120                             1140                                980                                   610                                      680                                         810Tack, Monsanto Tel-TakTack              50  80 56 75 57 57 50 67 76 46Stickiness        17  20 19 16 23 17 16 19 19 18&#34;True&#34; Tack       33  70 37 59 34 40 34 48 57 28__________________________________________________________________________ 
    
     
                                           TABLE XVI__________________________________________________________________________             Masterbatch             CE CF CG CH CI CJ CK CL CM__________________________________________________________________________PolymerNR(SMR 5-CV)      50.0                →                   →                      →                         →                            25.0                               →                                  →                                     →SBR 1778          36.0                →                   →                      →                         →                            54.0                               →                                  →                                     →SBR 1502          24.0                →                   →                      →                         →                            36.0                               →                                  →                                     →Test CompoundsNITROL + Clay     -- 0.75                   -- -- -- -- 0.75                                  -- --N--Carbamoylmaleamic Acid             -- -- 0.85                      1.27                         1.70                            -- -- 0.85                                     1.70MBTS              -- -- 0.15                      0.23                         0.30                            -- -- 0.15                                     0.30Other IngredientsN-660 Carbon Black             70.0                →                   →                      →                         →                            →                               →                                  →                                     →Zinc Oxide        3.0                →                   →                      →                         →                            →                               →                                  →                                     →Stearic Acid      1.0                →                   →                      →                         →                            →                               →                                  →                                     →Antioxidant       1.0                →                   →                      →                         →                            →                               →                                  →                                     →Green Strength @ Room Temp., MPaStress At:100%              0.42                0.54                   0.53                      0.63                         0.79                            0.42                               0.49                                  0.51                                     0.83300%              0.34                1.31                   0.88                      1.60                         2.38                            0.29                               0.68                                  0.60                                     1.71400%              0.34                1.77                   1.06                      2.08                         3.10                            0.24                               0.76                                  0.59                                     1.79U.E., %           1020                460                   650                      490                         420                            450                               780                                  550                                     440Tack, Monsanto Tel-TakTack              64 53 72 72 62 33 22 36 31Stickiness        11 14 12 15 14 12 13 14 14&#34;True&#34; Tack       53 39 60 57 48 21 9  22 17__________________________________________________________________________ 
    
     
                                           TABLE XVII__________________________________________________________________________          Stocks          29 30  31 32 33 34 35  36 37__________________________________________________________________________MasterbatchCE             185.0             --  -- -- -- -- --  -- --CF             -- 185.75                 -- -- -- -- --  -- --CG             -- --  186.0                    -- -- -- --  -- --CH             -- --  -- 187.0                       -- -- --  -- --CI             -- --  -- -- 188.0                          -- --  -- --CJ             -- --  -- -- -- 190.0                             --  -- --CK             -- --  -- -- -- -- 190.75                                 -- --CL             -- --  -- -- -- -- --  191.0                                    --CM             -- --  -- -- -- -- --  -- 190.3CurativesSulfur         2.0             →                 →                    →                       →                          →                             →                                 →                                    →MBTS           0.8             →                 →                    →                       →                          →                             →                                 →                                    →N--t-butyl-2-benzothiazyl          0.5             →                 →                    →                       →                          →                             →                                 →                                    →sulfenamideCure Time, Min. @ 153° C.          35 25  40 45 45 60 40  60 60Shore A Hardness          68 67  68 70 70 68 70  68 71Stress-Strain PropertiesStress at Indicated Strain, MPa100%           3.42             3.79                 3.85                    4.09                       4.10                          3.12                             3.38                                 3.48                                    4.00200%           9.29             10.51                 10.43                    10.99                       11.11                          8.27                             9.42                                 9.69                                    10.62300%           15.34             17.13                 16.62                    17.40                       17.94                          13.92                             15.85                                 15.67                                    17.33Break Stress   20.75             20.24                 20.22                    20.28                       18.73                          18.63                             19.65                                 20.29                                    20.13Break Strain, %          425             358 377                    347                       313                          414                             384 400                                    352__________________________________________________________________________ 
    
     To evaluate the effectiveness of mercaptans as component (A) a series of compounds is prepared containing 2-mercaptobenzothiazole and thiophenol compared with MBTS as component (A). The rubber compounds, based on synthetic polyisoprene, are prepared and tested as before, using N-carbamoyl malemic acid as component (B). 
     Formulations and results are set forth in Table XVIII. The data show that the mercaptans are effective as component (A). 
     
                       TABLE XVIII______________________________________          MASTERBATCH          CN    CO     CP     CQ   CR______________________________________PolymerNatsyn 2200      100.0   →                           →                                →                                     →Test CompoundsN--Carbamoyl maleamic acid            --      1.0    0.85 →                                     →MBTS             --      --     0.15 --   --2-Mercaptobenzothiazole            --      --     --   0.15 --Thiophenol       --      --     --   --   0.15Other IngredientsN-330 Carbon Black            50.0    →                           →                                →                                     →Circosol 4240 Oil            5.0     →                           →                                →                                     →Zinc Oxide       5.0     →                           →                                →                                     →Stearic Acid     2.0     →                           →                                →                                     →Antidegradant    2.0     →                           →                                →                                     →Green Strength @ RoomTemp., MPa Stress At:100%             0.30    0.38   0.36 0.34 0.28300%             0.23    0.37   0.43 0.42 0.38400%             0.21    0.47   0.58 0.58 0.53U.E., %          &gt;1200   690    600  590  610Tack, Monsanto Tel-TakTack             53      71     57   52   46Stickiness       23      18     19   19   22&#34;True&#34;  Tack     31      54     38   34   24______________________________________ 
    
     The diene rubber of the invention has been shown to possess improved properties, especially improved green strength and tack. As a result of these improved properties, processing of the diene rubber is facilitated, and rubber objects such as tires, for example, which are fabricated from a plurality of components can be produced with greater speed and with fewer defects. The improved diene rubber of the invention thus is useful for hose, belts, and a variety of other rubber products in addition to tires. 
     Although the invention has been illustrated by typical examples, it is not limited thereto. Changes and modifications of the examples of the invention herein chosen for purposes of disclosure can be made which do not constitute departure from the spirit and scope of the invention.