Abstract:
The method of manufacturing a thin film magnetic head is capable of precisely forming a core section with preventing the variation of the write-core head caused by ion milling for removing an electric conductive film and capable of improving yield of products. The method of manufacturing a thin film magnetic head, in which a core section having prescribed write-core width is formed by applying ion milling to an upper magnetic pole and a lower magnetic pole, comprises the steps of examining the write-core width of the core section; covering a surface of the core section with a protection film except an electric conductive film for preventing electro static charge of a wafer; and removing the exposed electric conductive film by ion milling.

Description:
BACKGROUND OF THE INVENTION  
         [0001]    The present invention relates to a method of manufacturing a thin film magnetic head, e.g., an induction recording-reproducing thin film magnetic head, a hybrid thin film magnetic head composed of an induction recording head and a magnetoresistance reproducing head, which is used for a magnetic disk drive unit, a magnetic tape recorder, etc., and a magnetic recording-reproducing apparatus.  
           [0002]    In an ordinary hybrid MR head (a thin film magnetic head) including an induction recording head and a magnetoresistance reproducing head, a write-head section for induction-recording data is piled on a reproducing head section having a magnetoresistance (MR) element. The structure of the thin film magnetic head is shown in FIGS.  4 - 6 . FIG. 4 is a plan view of the thin film magnetic head; FIG. 5 is a sectional view thereof; and FIG. 6 is a schematic view of a disk-side face thereof.  
           [0003]    As shown in FIG. 5, the write-head section has an upper magnetic pole  10  and a lower magnetic pole  12 , which mutually faced with a minute gap  5 . A coil  14 , which is made of an electric conductive material, is formed between the magnetic poles  10  and  12 . The lower magnetic pole  12  acts as an upper shielding layer of the reproducing head section. As shown in FIG. 6, a lower shielding layer  18  is provided under an MR element  16 .  
           [0004]    To improve recording density of a recording medium, track density of the recording medium should be increased. Therefore, width of the write-core section should be made as narrow as possible and as precise as possible. After the upper magnetic pole  10  is formed, the write-core width is determined by ion milling or FIB machining. A sectional shape of the write-core width is examined by SMI test or SEM test. Since a wafer is charged with static electricity during the SMI or SEM test, a whole surface of the wafer is covered with an electric conductive film for preventing the charge of static electricity. Therefore, the electric conductive film is removed by ion milling after the examination of the write-core width of the core section.  
           [0005]    The ion milling is applied to the whole surface of the wafer so as to remove the electric conductive film for executing the SEM test. In the case of having the write-core width 1μm or more, variation of the write-core width caused by ion milling is 0.01-0.02 μm, so that variation cause no problems. However, in the thin film magnetic head for the recent magnetic disk drive unit, the write-core width is 0.2 μm or less; the variation of the write-core width badly influences accuracy and function of products, and it cannot be ignored.  
         SUMMARY OF THE INVENTION  
         [0006]    The present invention was invented so as to solve the problem of the conventional thin film magnetic head.  
           [0007]    An object of the present invention is to provide a method of manufacturing a thin film magnetic head, which is capable of precisely forming a core section with preventing the variation of the write-core head caused by ion milling for removing an electric conductive film and capable of improving yield of products.  
           [0008]    To achieve the object, the present invention has following structures.  
           [0009]    Namely, the method of manufacturing a thin film magnetic head, in which a core section having prescribed write-core width is formed by applying ion milling to an upper magnetic pole and a lower magnetic pole, comprises the steps of: examining the write-core width of the core section; covering a surface of the core section with a protection film except an electric conductive film for preventing electro static charge of a wafer; and removing the exposed electric conductive film by ion milling.  
           [0010]    In the method, the protection film may be made of photo resist; the protection film may be removed after the electric conductive film is removed by ion milling; and the photo resist may be heated and cured after the surface of the core section is covered with the protection film, and the electric conductive film is removed by ion milling after the photo resist is cured. Preferably, the protection film is cured at temperature of 250° C. or less so as to prevent deterioration of an MR element caused by high temperature.  
           [0011]    Preferably, a whole surface of the wafer is covered with an inorganic oxide after the core section is formed, then the electric conductive film is exposed by lift-off and the surface of the core section is covered with the protection film, then the electric conductive film is removed by ion milling; or a whole surface of the wafer is covered with an inorganic nitride after the core section is formed, then the electric conductive film is exposed by lift-off and the surface of the core section is covered with the protection film, then the electric conductive film is removed by ion milling. For example, alumina may be used as the inorganic oxide, and silicon nitride may be used as the inorganic nitride.  
           [0012]    Further, a magnetic recording-reproducing apparatus of the present invention includes: a thin film magnetic head manufactured by the method of the present invention; and a magnetic recording medium.  
           [0013]    In the method of the present invention, when the electric conductive layer for preventing electric charge is removed by ion milling after forming the core section having the prescribed write-core width, the core section is covered with the photo resist, the inorganic oxide, etc. and ion-milled. Therefore, the write-core width can be precisely controlled without variation thereof; and the thin film magnetic heads having write-heads, which have excellent recording characteristics and which is capable of recording data with high recording density, can be manufactured with good yield. 
       
    
    
     BRIEF DESCRIPTION OF THE DRAWINGS  
       [0014]    Embodiments of the present invention will now be described by way of examples and with reference to the accompanying drawings, in which:  
         [0015]    FIGS.  1 A- 1 D are explanation views showing steps of the method of manufacturing the thin film magnetic head of a first embodiment;  
         [0016]    FIGS.  2 A- 2 D are explanation views showing steps of the method of manufacturing the thin film magnetic head of a second embodiment;  
         [0017]    FIGS.  3 A- 3 E are explanation views showing steps of the method of manufacturing the thin film magnetic head of a third embodiment;  
         [0018]    [0018]FIG. 4 is a plan view of the ordinary thin film magnetic head;  
         [0019]    [0019]FIG. 5 is a sectional view of the ordinary thin film magnetic head; and  
         [0020]    [0020]FIG. 6 is an explanation view of the disk-side face of the ordinary thin film magnetic head. 
     
    
     DETAILED DESCRIPTION OF THE EMBODIMENTS  
       [0021]    Preferred embodiments of the present invention will now be described in detail with reference to the accompanying drawings.  
         [0022]    FIGS.  1 A- 1 D are explanation views showing steps of the method of manufacturing the thin film magnetic head of a first embodiment.  
         [0023]    In FIG. 1A, a core section  11  having prescribed write-core width is formed by ion milling after an upper magnetic pole  10  is formed. Photo resist  20  acts as a protection film for protecting an electric conductive film  20 . The electric conductive film  20  is formed so as to prevent electric charge of a wafer while an examination of the write-core width, e.g., SEM test.  
         [0024]    To control the write-core width, firstly the upper magnetic pole  10  and a lower magnetic pole  12  are ion-milled so as to determine write-width of the magnetic poles  10  and  12 , and side faces of a core section  11  of the lower magnetic pole  12  are simultaneously curved by ion-milling. With this step, the core section  11  is formed into a rectangular shape, as shown in FIG. 1A, in which a write gap  5  is formed between the magnetic poles  10  and  12 .  
         [0025]    The examination of the write-core width is executed by examining the sectional shape of the core section  11  by the SMI or SME test after the photo resist  22  is removed. A plurality of the thin film magnetic heads are formed in the wafer, so conditions of the ion milling are varied according to their positions. The examination examines if the write-core width of each magnetic head is in a standard range or not.  
         [0026]    In FIG. 1B, exposed parts of the magnetic poles  10  and  12  are covered with photo resist  24  so as to remove the electric conductive layer  20  after the examination. When the electric conductive layer  20  is removed by ion milling, the photo resist  24  covers the core section  11  of the magnetic poles  10  and  12  so as to protect the core section  11  from the ion milling for removing the electric conductive layer  20 . The photo resist  24  is patterned on the wafer so as to cover the core section  11  of the magnetic poles  10  and  12  and expose the electric conductive layer  20 .  
         [0027]    In FIG. 1C, the core section  11  of the magnetic poles  10  and  12  are covered with the photo resist  24 , and the electric conductive layer  20  is removed by ion milling.  
         [0028]    In FIG. 1D, the photo resist  24  covering the core section  11  of the magnetic poles  10  and  12  is removed, and the core section  11  of the magnetic poles  10  and  12  is finally exposed. By removing the electric conductive layer  20 , by ion milling, with the magnetic poles  10  and  12  covered with the photo resist  24 , the examined write-core width can be maintained without the variation of the write-core width caused by ion milling, so that the thin film magnetic head having the prescribed write-core width can be manufactured.  
         [0029]    FIGS.  2 A- 2 D are explanation views showing steps of the method of manufacturing the thin film magnetic head of a second embodiment. The structural elements shown in FIGS.  1 A- 1 D are assigned the same symbols and explanation will be omitted.  
         [0030]    In FIG. 2A, a surface of the electric conductive film  20  has been covered with the photo resist  22 , and the lower magnetic pole  12  is curved by ion milling so as to form the core section  11  of the magnetic poles  10  and  12 .  
         [0031]    In FIG. 2B, the photo resist  22  has been removed so as to remove the electric conductive film  20  by ion milling, then exposed faces of the magnetic poles  10  and  12  are covered with photo resist  26 .  
         [0032]    In the second embodiment, the photo resist  26  covering over the magnetic poles  10  and  12  is heated to cure the photo resist  26 . The photo resist  26  is cured at, for example, 250° C. The curing temperature of the photo resist is not limited, but the preferable curing temperature is 250° C. or less so as not to damage the MR element, etc..  
         [0033]    By heating and curing the photo resist  26 , the core section  11  of the magnetic poles  10  and  12  is covered with the cured photo resist  26   a , so that the cured photo resist  26   a  is not peeled from the core section  11  of the magnetic poles  10  and  12 .  
         [0034]    In FIG. 2D, the magnetic poles  10  and  12  have been covered with the cured photo resist  26   a , and the electric conductive film  20  is removed by ion milling. In the present embodiment, the core section  11  of the magnetic poles  10  and  12  of the completed thin film magnetic head is covered with the cured photo resist  26   a.    
         [0035]    In the present embodiment too, the magnetic poles  10  and  12  are covered with the cured photo resist  26   a , the examined write-core width can be maintained without the variation of the write-core width caused by ion milling, so that the thin film magnetic head having the prescribed write-core width can be manufactured.  
         [0036]    Further, since the core section  11  of the magnetic poles  10  and  12  is protected by the cured photo resist  26   a , the core section  11  can be securely protected in the following steps, e.g., film-forming step, patterning step.  
         [0037]    FIGS.  3 A- 3 E are explanation views showing steps of the method of manufacturing the thin film magnetic head of a second embodiment. The structural elements shown in FIGS.  1 A- 2 D are assigned the same symbols and explanation will be omitted.  
         [0038]    In FIG. 3A, the core section  11  is formed in the magnetic poles  10  and  12  by ion milling as well as the foregoing embodiments.  
         [0039]    In FIG. 3B, the surface of the wafer other than the core section  11  is covered with photo resist  28 . The photo resist  28  will be dissolved in the following step.  
         [0040]    In FIG. 3C, the whole surface of the wafer is covered with an alumina film  30 , which is formed by spattering, after the surface of the wafer other than the core section  11  is covered with photo resist  28 . Thickness of the alumina film  30  may be about 1.0 μm.  
         [0041]    In FIG. 3D, after the alumina film  30  is formed, the photo resist  28  is selectively dissolved so as to remove the photo resist  28  from the surface of the electric conductive film  20 . And, the alumina film  30  covering the photo resist  28  is lifted off. The lift-off is executed by chemical dissolution or supersonic cleaning.  
         [0042]    In FIG. 3E, the exposed electric conductive film  20  is removed by ion milling. The core section  11  of the magnetic poles  10  and  12  is covered with the alumina film  30 , and it can be protected from the ion milling, so that the electric conductive film  20  only is removed.  
         [0043]    In the present embodiment, the core section  11  of the magnetic poles  10  and  12  of the completed thin film magnetic head is covered with the alumina film  30  as shown in FIG. 3E.  
         [0044]    In the present embodiment too, the magnetic poles  10  and  12  are covered with the alumina film  30 , the examined write-core width can be maintained without the variation of the write-core width caused by ion milling, so that the thin film magnetic head having the prescribed write-core width can be manufactured.  
         [0045]    Note that, an inorganic oxide, e.g., alumina, and an inorganic nitride, e.g., silicon nitride, can be used as the material for covering and protecting the core section  11 . The thickness of the film for covering and protecting the core section  11  may be optionally selected from a range of 0.1-2.0 μm.  
         [0046]    In the third embodiment, the photo resist  28 , which is separately used from the photo resist  22  for ion-milling the core section  11 , is used so as to lift off the alumina film  30 . In other cases, the photo resist  22  may be used for lifting off a covering film.  
         [0047]    The invention may be embodied in other specific forms without departing from the spirit or essential characteristics thereof. The present embodiments are therefore to be considered in all respects as illustrative and not restrictive, the scope of the invention being indicated by the appended claims rather than by he foregoing description and all changes which come within the meaning and range of equivalency of the claims are therefore intended to be embraced therein.