Abstract:
Disclosed are a magnetoresistance effect element equipped with an magnesium oxide passivation layer, and a high-speed, ultra-low power consumption nonvolatile memory using said element. A tunnel magnetoresistance effect (TMR) film comprised of a ferromagnetic free layer, an insulation layer, and a ferromagnetic fixed layer is provided, and an MgO passivation layer is provided on the side walls of a protective layer and an orientation control layer, thus suppressing elemental diffusion of a tunnel magnetoresistance effect (TMR) element from each layer due to thermal processing at 350° or higher and obtaining a magnetic memory cell and magnetic random access memory having stable, high-output reading and a low current writing characteristics. Furthermore, when CoFeB is used in the ferromagnetic layer and MgO is used in the insulation layer, it is preferable that the MgO passivation layer have an (001) orientation.

Description:
TECHNICAL FIELD  
       [0001]    The present invention concerns a tunnel magnetoresistance element, and a low power consumption non-volatile magnetic memory provided with the same. 
       BACKGROUND ART  
       [0002]    As tunnel magnetoresistance effect (hereinafter referred to as TMR) elements applied to highly integrated magnetic memories in the feature, a TMR element using Al oxide for an insulation layer (Non Patent Literature 1) and a TMR element using magnesium oxide (MgO) for an insulation layer capable of providing a magnetoresistance ratio several times as high as that (Non Patent Literature 2) have been known. Further, a TMR element using CoFe for the magnetic layer and a low power consumption magnetic memory cell and a magnetic random access memory using the same are disclosed in Patent Literature 1. Further, Patent Literature 2 discloses a TMR element using a magnetic pinned layer of a body-centered cubic lattice typically exemplified by CoFeB and a (100) oriented MgO barrier layer, and a magnetic memory cell and a magnetic random access memory using the same. Further, existent non-volatile magnetic memory comprises a memory cell in which a TMR element is formed over an MOSFET. In the switching, information is written by rotating the magnetization direction of a TMR element using a spatial magnetic field induced by a current generated by supplying a current to bit lines and word lines utilizing an MOSFET and the information is read out by the output voltage of the TMR element. 
         [0003]    Further, in addition to the magnetization rotation using the current-induced spatial magnetic field, a so-called magnetization reversal by a spin transfer torque of rotating magnetization by flowing a current directly to a magnetoresistance effect element, in other words, a spin injection magnetization reversal system is known and disclosed, for example, in Patent literature 6 or Patent literature 3. A patent literature 4 discloses a TMR element of applying a free layer formed by stacking plural ferromagnetic layers by way of a non-magnetic layer with an aim of stably conducting magnetization reversal by a spin transfer torque to a magnetic field invading from the outside. Further, Patent Literature 5 discloses an example of applying an insulation film to the side wall of a TMR element with an aim of improving the reliability of a magnetic memory. 
       CITATION LIST  
     Non Patent Literatures 
       [0004]    Non Patent Literature 1: T. Miyazaki and N. Tezuka, J. Magn. Magn. Mater, 139, L231 (1995) 
         [0005]    Non Patent literature 2: S. Yuasa, et al., Nature Material 3, 868(2004). 
       Patent Literatures 
       [0006]    Patent Literature 1: JP-A-2006-269530 
         [0007]    Patent Literature 2: JP-A-2007-59879 
         [0008]    Patent Literature 3: JP-A-2002-305337 
         [0009]    Patent Literature 4: JP-A-2005-294376 
         [0010]    Patent Literature 5: JP-A-2004-349671 
         [0011]    Patent Literature 6: U.S. Pat. No. 5,695,864 
       SUMMARY OF INVENTION  
     Technical Problem 
       [0012]    For attaining a low power consumption non-volatile magnetic memory having high reliability, it is necessary to develop a technique for a magnetoresistance effect element capable of satisfying a high heat stability and a low current writing system by magnetization reversal by a spin transfer torque simultaneously in a free layer (recording layer) of a high output TMR element and capable of withstanding a heat treatment at 350° C. or higher. However, in a TMR element, since elements contained in each of layers as the constituents thereof are diffused by the heat treatment and, particularly, elemental diffusion occurs as far as to the interlayer insulation layer formed on the side wall of the TMR element for flowing a current uniformly in the direction perpendicular to the film surface of the TMR element to deteriorate the voltage withstanding of the interlayer insulation layer. Therefore, it is necessary to form a layer capable of suppressing elemental diffusion due to the heat treatment between the magnetoresistance effect element and the interlayer insulating layer. 
         [0013]    Further, when CoFeB is used for the magnetic layer and MgO is used for the insulating layer of the TMR element, CoFeB which was amorphous during film deposition is crystallized by a heat treatment at 320° C. or higher. Accordingly, it is necessary to provide a layer capable of suppressing elemental diffusion due to the heat treatment and promoting uniformity of crystallization of CoFeB. 
         [0014]    An object of the present invention is to provide a magnetoresistance effect element capable of satisfying a high heat stability and a low power writing system and capable of withstanding a heat treatment at a predetermined level or higher. 
       Solution to Problem 
       [0015]    For addressing the purpose described above, a magnetoresistance effect element of the present invention includes; an amorphous non-magnetic metal layer, an orientation control layer formed over the non-magnetic metal layer, a TMR element formed above the orientation control layer and comprising a ferromagnetic free layer, a ferromagnetic pinned layer, and an insulation layer formed between the ferromagnetic free layer and the ferromagnetic pinned layer, a magnesium oxide passivation layer for covering the side wall of the tunnel magnetoresistance effect element, the side wall of the orientation control layer, and the side wall and the surface of the non-magnetic metal layer, an interlayer insulation layer for covering the magnesium oxide passivation layer, and a pair of electrode layers for flowing a current in a direction perpendicular to the film surface of the TMR element. 
         [0016]    That is, in the configuration of the present invention, elemental diffusion is suppressed by covering the side wall of the TMR element with the MgO passivation layer, thereby suppressing the deterioration of electric characteristics of the interlayer insulating layer. Further, in a preferred configuration of the present invention, by subjecting the MgO passivation layer to (001) orientation, the crystal uniformity of CoFeB of the TMR element that crystallizes at 320° C. or higher can be improved to obtain the best effect of the TMR. 
         [0017]    The TMR element of the present invention is applicable to a magnetic memory cell or a magnetic random access memory. 
       Advantageous Effects of Invention 
       [0018]    According to an aspect of the present invention, even when a heat treatment at 350° C. is performed, the ferromagnetic layer of the magnetoresistance effect element can be crystallized uniformly without deteriorating the voltage withstanding of the interlayer insulating layer thereby obtaining the best TMR effect. By mounting the TMR element to a magnetic memory, it is possible to provide a magnetic memory cell and a magnetic random access memory ensuring rewriting durability for infinite times and non-volatility. 
     
    
     
       BRIEF DESCRIPTION OF DRAWINGS 
         [0019]      FIG. 1  is a view showing the configuration of a TMR element according a first embodiment. 
           [0020]      FIG. 2  is a view showing another configuration of a TMR element according to the first embodiment. 
           [0021]      FIG. 3  is a view showing a further configuration of a TMR element according to the first embodiment. 
           [0022]      FIG. 4  is a view showing a further configuration of a TMR element according to the first embodiment. 
           [0023]      FIG. 5  is a view showing a further configuration of a TMR element according to the first embodiment. 
           [0024]      FIG. 6  is a graph showing the dependency of TMR ratio of the TMR element according to the first embodiment on the annealing temperature. 
           [0025]      FIG. 7  is a view showing a configurational example of a magnetic memory cell according to a second embodiment. 
           [0026]      FIG. 8  is a view showing another configurational example of a magnetic memory cell according to the second embodiment. 
           [0027]      FIG. 9  is a view showing a configurational example of a magnetic random access memory using a magnetic memory cell according to the second embodiment. 
           [0028]      FIG. 10  is a view for explaining a manufacturing process of a TMR element according to the first embodiment. 
           [0029]      FIG. 11  is a table showing materials that can be used for a ferromagnetic pinned layer and a ferromagnetic free layer of the TMR element according to the first embodiment. 
       
    
    
     DESCRIPTION OF EMBODIMENTS  
       [0030]    Embodiments of the invention are to be described with reference to the drawings. In the TMR element to be described below, magnetization reversal (switching) of the ferromagnetic free layer thereof is performed not by a spatial external magnetic field but mainly by providing a torque to the magnetic moment of a ferromagnetic free layer by the spin of a spin-polarized current flowing in the TMR element. The spin-polarized current is generated just by flowing a current to the TMR element. Accordingly, magnetization reversal by spin transfer torque is attained by flowing a current from the outside to the TMR element. A read current which is supplied for reading the magnetization direction of the ferromagnetic free layer of the TMR element is set smaller than a write current for causing magnetic reversal. In the following, the threshold value of a current density at which magnetization reversal by spin transfer torque occurs is defined as Jc. 
       Embodiment 1  
       [0031]      FIG. 1  is a schematic cross sectional view showing the configuration of a TMR element according to a first embodiment. A TMR film  1  comprises a ferromagnetic pinned layer  300 , an insulation layer  301 , and a ferromagnetic free layer  302 . The order of stacking the ferromagnetic pinned layer  300  and the ferromagnetic free layer  302  may be reversed. Further, CoFeB is used preferably for the ferromagnetic pinned layer  300  and the ferromagnetic free layer  302 . In addition to CoFeB, material compositions of CoFe and CoFeNi, a structure comprising Co—Fe series material with addition of B, a structure comprising Ni—Fe series material with addition of B, or a configuration comprising Co—Ni—Fe series material with addition of B in the table shown in  FIG. 11  may also be used. Further, as the additive element, other than B, one or plural Ta, Ru, Cu, Au, Ti, Cr, Ag, Al, Os, Re, C, O, N, Pd, Pt, Zr, Zn, Ir, W, Mo, and Nb may be used. 
         [0032]    For the insulation layer  301 , (001) oriented MgO (magnesium oxide) of a rock salt structure is used preferably and aluminum oxide (Al—O), aluminum nitride (Al—N), magnesium nitride (Mg—N), silicon oxide (Si—O), silicon nitride (Si—N), titanium oxide (Ti—O), or Ca, Ba, Sr, V, Ni, Fe, Co, Cu, Ru, Re, Os, Eu, Bi, Pb, or Zn added to MgO, Al—O, Al—N, Mg—N, Si—O, Si—N, and Ti—O, or oxides thereof may be also be used. 
         [0033]    For controlling the crystal orientation or the crystal structure of the ferromagnetic pinned layer  300  or the ferromagnetic free layer  302 , an orientation control layer  401  is formed below the tunnel magnetoresistance effect film  1 , and, further, a protective film is formed over the ferromagnetic free layer  302  or the ferromagnetic pinned layer  300 . For the orientation control layer  401 , a material such as Ru or Ta is used. By the use of such a material, a smooth CoFeB surface can be formed at a level of atoms with good uniformity when CoFeB is used for the ferromagnetic layer and (001) orientation of MgO thereover can also be improved. As the orientation control layer, amorphous conductive materials can also be used in addition. A metal layer  400  is formed below the orientation control layer. 
         [0034]    The most preferred material for the metal layer  400  is Ta and a metal layer having an amorphous structure, for example, TiN or CuN, TaN is preferred. By using the amorphous structure for the metal layer  400 , the MgO passivation layer  200  is easily put to (001) orientation in the direction perpendicular to the film surface. An MgO passivation layer  200  is formed to cover the side wall of the TMR film  1 , the orientation control layer  4001  and the protective film  402 , and the side wall and the surface of the metal layer  400 , and an interlayer insulation film  201  is formed so as to cover the MgO passivation layer  200 . Electrodes  500  and  501  are disposed in contact with upper and lower portions of the TMR film  1  to form a TMR element. 
         [0035]    Then, a method of writing information and reading information when the TMR element described above is applied to a magnetic memory cell or a magnetic random access memory is to be described. At first, in information writing, a voltage or a current is applied between the electrode  500  and the electrode  501 , and a spin transfer torque generated from a spin current formed by flowing a current in the direction perpendicular to the film surface of the TMR film  1  is exerted on the ferromagnetic free layer  302 , to reverse the magnetization direction of the ferromagnetic free layer  302 , in which magnetic information is recorded as “0” when the magnetization direction of the ferromagnetic free layer  302  is in parallel to the ferromagnetic pinned layer  300  and as “1” when it is in antiparallel thereto. 
         [0036]    Then, a tunnel magnetoresistance ratio (TMR ratio) used for reading information in the magnetization direction of the ferromagnetic free layer  302  of the TMR film  1  is to be described. For the relative angle of the magnetization direction of ferromagnetic free layer  302  and the ferromagnetic pinned layer  300 , a voltage or a current is applied between the electrode  500  and the electrode  501 , and it is distinguished whether the magnetization direction of the ferromagnetic free layer  302  is in parallel or antiparallel to the magnetization direction of the ferromagnetic pinned layer  300  by reading a current or a voltage generated from the TMR film  1 , thereby reading information. This is referred to as a tunnel magnetoresistance effect. The tunnel magnetoresistance effect is attributable to the change of the resistance depending on the magnetization direction between each of the ferromagnetic pinned layer  300 , the insulation layer  301  and the ferromagnetic free layer  302 . For example, the voltage at the TMR film  1  is low (electric resistance is low and current tends to flow easily) when the magnetization direction of the ferromagnetic free layer  302  is in parallel to the magnetization direction of the ferromagnetic pinned layer  300 , and the voltage is high (electric resistance is high and current less flows) when it is in antiparallel thereto. 
         [0037]    Then, a process for manufacturing a portion of the TMR element  50  in  FIG. 1  is to be described specifically with reference to  FIG. 10  together with the feature of the material. A combination of CoFeB for the ferromagnetic pinned layer  300  and the ferromagnetic free layer  302  and MgO for the insulation layer  301  is to be described as a configurational example of a TMR film particularly capable of obtaining the best TMR ratio and magnetization reversal by low current spin torque. 
         [0038]    Step (1); An electrode  500  is deposited. For the electrode  500 , TiN or Ti, Al or AlCu, or Ta or Ta/Ru, etc. can be used. 
         [0039]    Step (2); A metal layer  400  is deposited. The metal layer  400  is preferably has an amorphous structure. For example, Ta or a multilayered film of Ta/metal film/Ta, etc. can be used. 
         [0040]    Step (3); An orientation control layer  401  is deposited. A Ta film of an amorphous structure film is used preferably for the orientation control layer. 
         [0041]    Step (4); A tunnel magnetoresistance effect film  1  comprising the ferromagnetic pinned layer  300 , the insulation layer  301 , and the ferromagnetic free layer  302  is deposited. CoFeB is used for the ferromagnetic pinned layer  300  and the ferromagnetic free layer  302 , and a (001) orientated MgO is used for the insulation film  301 . It is a characteristic feature of this process to enable preferred (001) orientation for the MgO film of the insulation layer  301  by forming the CoFeB film in an amorphous structure for the ferromagnetic pinned layer  300  upon deposition. 
         [0042]    Step (5); The protective film  402  is deposited. As the protective film, a film of Ru, Ta and Ta/Ru, Ta/Ru, MgO/Ta, MgO/Ta/Ru, MgO/Ru/Ta, etc. is used. 
         [0043]    For the steps (1) to (5), it is preferably deposited in continuous stacking by using a sputtering method in vacuum without exposing from a vacuum atmosphere. Further, an entire or a portion of the layer may also be deposited by using a molecular beam epitaxy method. Since this enables to manufacture a high quality TMR element  50  since adsorption of impurities to the interface between each of the layers can be suppressed. Subsequently, a heat treatment may also be applied with an aim of improving the TMR ratio in the step (10) to be described later. The TMR ratio can be improved by applying a magnetic field in the direction horizontal to or perpendicular to the stacking direction during the heat treatment. 
         [0044]    Step (6); They are formed into a pillar shape by performing ion milling or reactive ion etching using a resist or a metal mask of a desired size as a mask. In this step, the surface is exposed at the metal layer  400  by stopping the etching at the surface of the metal layer  400  or at a slightly deep position in the direction of the film thickness from the surface of the metal layer  400  (direction perpendicular to the film surface). The surface and the lateral side of the exposed metal layer  400  are preferably amorphous (amorphous structure). Further, while the TMR element has a 100×200 nm 2  planar size, a TMR element of a smaller width of 45 nm or less can be formed by the method. 
         [0045]    Step (7); The lateral side of the pillar and the surface of the exposed metal layer  400  are covered with an MgO passivation layer  200 . When the surface of the metal layer  400  is in an amorphous structure, the (001) face of the MgO passivation layer  200  is oriented easily in the direction perpendicular to the film surface. 
         [0046]    Step (8); An interlayer insulation film  201  is formed so as to cover the MgO passivation layer  200 . The interlayer insulation film  201  comprises an insulation film, for example, of SiO, SiN, AlO, AlN, etc. and deposited by CVD or the like. Further, this is sometimes formed by sputtering. Particularly, when it is deposited by CVD, a heat at 200° C. or higher is applied. 
         [0047]    Step (9); Finally, the electrode  501  is formed. A material such as W, Al, AlCu, Ti. etc. is used for the electrode  501 . 
         [0048]    Step (10); A heat treatment at 350° C. or higher is performed. This has to be practiced with an aim of attaining the improvement in the TMR ratio of the tunnel magnetoresistance effect element  50  and the effect of reducing the current for spin torque-induced magnetic reversal to a maximum level, and for improving the yield and the improvement in the distribution of the impurity processing in the electrode and electric characteristic after forming the electrode  501 . The TMR ratio can be improved by applying a magnetic field in a direction parallel to or in perpendicular to the stacking direction of the TMR film during the heat treatment. When a heat treatment at 350° C. or higher is performed to the tunnel magnetoresistance effect element  50  as described above, elements diffuse from the orientation control layer and the ferromagnetic layer. Particularly, Mn, Ru, etc. used for examples in the TMR element shown in  FIG. 2  to  FIG. 5  diffuse remarkably. Such elements diffuse while extending as far as the interlayer insulation layer covering the pillar to cause degradation of electric characteristic such as voltage withstanding of the interlayer insulation layer. In this case, the MgO passivation layer  200  of this embodiment has a function of suppressing the diffusion of the elements described above. Further, it is possible to reduce the effect of elemental diffusion to the heating practiced upon deposition of the interlayer insulation layer  201  in the step (8). 
         [0049]      FIG. 6  shows a relation between the improvement in the TMR ratio and the crystal orientation by the heat treatment. When the TMR film  1  is formed as CoFeB/MgO/CoFeB using CoFeB for the ferromagnetic pinned layer  300  and the ferromagnetic free layer  302  and using MgO for the insulation layer  301 , CoFeB which was amorphous upon deposition proceeds crystallization with the (001) oriented MgO put therebetween as a template to optimize the TMR ratio. Usually, CoFeB starts crystallization about at a temperature of 320° C. When the TMR film  1  is an entirely (001) oriented CoFeB/MgO/CoFeB also including CoFeB, the TMR ratio increases along with the heat treatment temperature and the value is at the maximum at a temperature of 400° C. or higher. However, when other crystals than those of (001) orientation are formed, the TMR ratio reaches the local maximum at a low heat treatment temperature and the TMR ratio is also reduced. Since the crystallization of CoFeB is promoted with the (001) oriented MgO insulation layer  301  as a template, the crystallization proceeds from the side wall and the crystallinity of CoFeB is made uniform by the presence of the (001) oriented MgO passivation layer at the pillar end. This enables not only to suppress element diffusion in each of the layers but also make the crystals of CoFeB uniform, thereby preventing lowering of the voltage withstanding of the interlayer insulation film and enabling improvement in the TMR ratio. 
         [0050]    In addition to the structure of the TMR film  1  of the embodiment described above, configurations shown in  FIG. 2  to  FIG. 5  can also be used.  FIG. 2  shows a TMR film  2  having a structure where an antiferromagnetic layer  4011  is in contact with the ferromagnetic pinned layer  300  for pinning the magnetization direction of the ferromagnetic pinned layer  300  stably in one direction. By using a material such as MnIr or MnPt for the antiferromagnetic layer  4011 , a best characteristic can be obtained. Information can be read or written stably by stably pinning the magnetization direction of the ferromagnetic pinned layer  300  in one direction stably. 
         [0051]      FIG. 3  shows a configurational example of a TMR film  3  in which a ferromagnetic pinned layer  300  is a stacked ferromagnetic pinned layer formed of two layers of a ferromagnetic layer  3001  and a ferromagnetic layer  3003  where magnetization is coupled in antiparallel manner by way of a non-magnetic layer  3002  formed, for example, of Ru. With such a configuration, since the magnetization direction of the ferromagnetic pinned layer  300  can be pinned more stably in one direction than that of  FIG. 2 , stable reading and writing can be performed. 
         [0052]      FIG. 4  shows an example of a TMR film  4  in which a ferromagnetic free layer  302  is a stacked ferromagnetic free layer formed of two layers of a ferromagnetic layer  3021  and a ferromagnetic layer  3023  where magnetization is coupled in an antiparallel manner by way of a non-magnetic layer  3022 . By using the stacked ferromagnetic free layer for the ferromagnetic free layer, low current information writing at a current density of 1 MA/cm 2  or less can be attained and information recording can be held for 10 years or more. 
         [0053]      FIG. 5  shows a TMR film  5  having a structure in which each of a ferromagnetic pinned layer  300  and a ferromagnetic free layer  302  has two or more of ferromagnetic layers. This embodiment shows a configurational example where a ferromagnetic pinned layer comprises two layers of a ferromagnetic pinned layer  300  and a ferromagnetic layer  3100 , and a ferromagnetic free layer comprises two layers of a ferromagnetic free layer  302  and a ferromagnetic free layer  3102 . For the ferromagnetic layer  3100  and the ferromagnetic layer  3102 , vertically magnetized films where the magnetization thereof is in a direction perpendicular to the film surface can be used. By using CoFeB for the ferromagnetic pinned layer  300  and the ferromagnetic free layer  302  in contact with the insulation layer  301  and disposing a vertically magnetized film for the ferromagnetic layer  3100  and the ferromagnetic layer  3102 , the magnetization direction of CoFeB is induced to the vertical direction. With such a structure, information record holding for 10 years is further stabilized. 
         [0054]    For the ferromagnetic layers  3100  and  3102 , materials such as TbFeCo, GdFeCo, CoPt, FePt, CoFeBPt, CoFeBCr, CoCrPt, CoCr, CoPtB, FePtB, CoGd, CoFeBCr, etc. can be used. Further, it is possible to use, for example, a Co/Pt multilayered film, a CoFe/Pt multilayered film, a Fe/Pt multilayered film, a Co/Pd multilayered film can be used. 
       Embodiment 2  
       [0055]      FIG. 7  and  FIG. 8  are schematic cross sectional views showing a configurational example of a magnetic memory cell as a second embodiment. In the drawing, the TMR element shown in  FIG. 1  to  FIG. 5  is mounted at a portion shown as a TMR element  50  in the drawing. 
         [0056]    C-MOS  100  comprises two n-type semiconductors  101  and  102  and one p-type semiconductor  103 . An electrode  21  as a drain is electrically connected to an n-type semiconductor  101  and connected to the ground by way of an electrode  41  and an electrode  47 . An electrode  22  as a source is electrically connected to an n-type semiconductor  102 . Further,  23  denotes a gate electrode and ON/OFF of the current between the source electrode  22  and the drain electrode  21  is controlled by ON/OFF of the gate electrode  23 . Over the source electrode  22 , an electrode  45 , an electrode  44 , an electrode  43 , an electrode  42 , and an electrode  500  are stacked and a tunnel magnetoresistance effect film  1  to  5  comprising one of the structures in  FIG. 1  to  FIG. 5  is connected by way of the metal layer  400 . An orientation control layer  401  is formed between the TMR film  1  to  5  and the metal layer  400 . A protective layer  402  is stacked over the TMR film  1  to  5  and, further, an electrode  501  is formed in contact with the protective layer  402 . An interconnect  40  is formed over the electrode  501  and the stacked interconnect of the electrode  501  and the interconnect  400  can form a bit line. Further, the interconnect  40  alone can also constitute the bit line.  FIG. 7  shows an example in which a TMR element  50  is formed just over the electrode  42  and  FIG. 8  shows an example in which the TMR element  50  is formed by extending the electrode  50  and the metal layer  400  from the electrode  42 . In these cases, while the MgO passivation  200  is formed so as to cover at least the side walls of the TMR film  1  to  5 , alignment control layer  401 , and the protective layer  402 , it may be formed so as to cover the metal layer  400 . The interlayer insulation film  201  is preferably formed so as to cover the MgO passivation. 
         [0057]    In the memory cell of the embodiment described above, the magnetization direction of the ferromagnetic free layer  302  of the tunnel magnetoresistance effect film  1  to  5  is rotated by a current flowing to the tunnel magnetic resistance effect film  1  to  5 , so-called spin transfer torque, thereby recording the magnetic information. The spin transfer torque is based on the principle that a torque is given to the magnetic moment of ferromagnetic free layer  302  of TMR film  1  to  5  not by a spatial external magnetic field, but mainly by the spin of the spin-polarized current flowing in the TMR element. The spin-polarized current has a mechanism of generating by flowing a current to the TMR film  1  to  5 . Accordingly, magnetization reversal by the spin transfer torque is realized by providing means for supplying a current from the outside to the TMR film  1  to  5  and flowing the current from the means. In this embodiment, the spin transfer torque is exerted on the ferromagnetic free layer  302  in the TMR film  1  to  5  by the flow of the current between the bit line comprising the interconnect  40  and the electrode  501  or the interconnect  40  solely and the electrode  47 . When writing is performed by spin transfer torque, the power during writing can be decreased to about 1/100 compared with the case of using a current magnetic field. 
         [0058]      FIG. 9  is a view showing a configurational example of a magnetic random access memory in which the magnetic memory cells described above are arranged. Gate electrodes  23  forming a selection section for selecting an optional magnetic memory in the random access memory and interconnects  40  as the bit line are connected electrically to each of the magnetic memory cells  60 . By disposing the magnetic memory cells described specifically above, operation is enabled at low consumption power and a high density magnetic memory at a giga bit class can be realized. 
       INDUSTRIAL APPLICABILITY  
       [0059]    The present invention is extremely useful as a tunnel magnetoresistance element, and as a low power consumption non-volatile magnetic memory provided with the same. 
       REFERENCE SIGNS LIST  
       [0000]    
       
           1  to  5  tunnel magnetoresistance effect film, 
           100  transistor, 
           101  first n-type semiconductor, 
           102  second n-type semiconductor, 
           103  p-type semiconductor, 
           21  source electrode, 
           22  drain electrode, 
           23  gate electrode, 
           200  MgO passivation layer, 
           201  interlayer insulation film, 
           300  ferromagnetic pinned layer, 
           301  insulation layer, 
           302  ferromagnetic free layer, 
           3001  ferromagnetic layer, 
           3002  non-magnetic layer, 
           3003  ferromagnetic layer, 
           3021  ferromagnetic layer, 
           3022  non-magnetic layer, 
           3023  ferromagnetic layer, 
           40  interconnect (bit line), 
           400  metal layer, 
           401  orientation control layer, 
           4011  antiferromagnetic layer, 
           402  protective layer, 
           41  electrode interconnect, 
           42  electrode interconnect, 
           43  electrode interconnect, 
           44  electrode interconnect, 
           45  electrode interconnect, 
           47  electrode interconnect, 
           50  tunnel magnetoresistance effect element, 
           500  electrode, 
           501  electrode, 
           60  magnetic memory cell