Abstract:
This invention provides a new configuration and manufacturing method of the hetero-junction bipolar transistor. According to the invention, the HBT comprises a semi-insulating InP substrate, a buffer layer on the substrate, a sub-collector layer, a collector layer, a base layer, an emitter layer, and an emitter contact layer These layers are sequentially grown on the buffer layer. Since a pre-processing of forming two depressions in the sub-collector layer before growing the collector layer, the top surface of the emitter layer becomes planar surface. This results on the reduction of pits induced in the etching of the emitter contact layer, thus enhances the reliability and the high frequency performance of the HBT.

Description:
BACKGROUND OF THE INVENTION 
     1. Filed of the Invention 
     This invention relates to a bipolar transistor, especially relates to a hetero-junction bipolar transistor (HBT) made of a combination of III-V compound semiconductor materials. 
     2. Related Prior Art 
     HBT is applying to an amplifier device for a high-speed optical communication system. Although HBT has intrinsically an excellent characteristic in high-frequency band over 10 GHz, further performance is requested in frequency band over 40 GHz. One solution to realize such superior performance is to reduce an area of a sub-collector layer or a collector layer to decrease the capacitance between the collector and the base electrode. 
     A subject accompanying with the conventional HBT and its manufacturing process is explained as referring FIG.  11 . 
     An InGaAs sub-collector is grown on an InP substrate and formed to a sub-collector mesa by an etching (FIG.  11 (D)). Subsequently layer of an InGaAs collector, an InGaAs base, an InP emitter, and an InGaAs emitter contact are formed so as to cover the sub-collector mesa with an octagonal shape as shown in FIG.  11 (B). Cross sections of these layers are bent upwardly and downwardly at both edges of the sub-collector mesa by reflecting the shapes thereof. Further, various crystal surfaces, such as { 111 }, { 211 } and { 331 }, appear in edge surfaces of the octagonal mesa. 
     Forming the emitter contact mesa by etching, a large number of etching-pit comes out, especially in boundaries between { 211 } and { 100 }, and also between { 331 } and { 100 }. This is due to a reason that the etching is promoted at these boundaries. Further, since the thickness of the emitter is only several tenth of nano-meter, etching-pits pierce the emitter and reach the base beneath the emitter. This fails the reliability and the yield of the HBT. 
     SUMMARY OF THE INVENTION 
     An object of the claimed invention is to provide a new configuration of the HBT and a method of producing the HBT. To solve the subject, the present HBT comprises a sub-collector layer on a predetermined surface orientation of a semiconductor substrate, a collector layer on the sub-collector layer, a base layer on the collector layer, an emitter layer on the base layer and an emitter contact layer on the emitter layer. The sub-collector layer has a pair of edges along predetermined axis of the substrate and subsequent layer of the collector, the base, and the emitter layer covers these edges of the sub-collector so as to make planar the surface of the emitter layer. Since the surface of the emitter layer is planar, the generation of etching-pits on the emitter layer can be prevented. Moreover, it is preferable that the emitter contact layer comprises two portions, one portion has a first carrier concentration and contact to the emitter layer, the other portion has a second carrier concentration greater than the first concentration and contacts to the emitter electrode. This directs the lower contact resistance, thus enhances the high frequency performance of the HBT. 
     Next aspect of the present HBT comprises a collector layer on a semi-insulating semiconductor substrate with a predetermined surface orientation, a base layer on the collector layer, an emitter layer on the base layer, and an emitter contact layer on the emitter layer. The collector layer forms a mesa shape with a cross section of a trapezium, and subsequently layers are formed so as to cover the collector mesa. Further, since the surface of the emitter layer is planar, the appearance of etching-pits on the emitter layer can be prevented even when edges of the emitter layer is apart from edges of the emitter contact layer. In this configuration, the thickness of the base layer at the position just above the collector layer is thinner than the thickness at the position peripheral to the collector layer. This directs the reduction of the base resistance, thus enhances the high frequency performance of the HBT. 
     Another aspect of the present invention relates to the method for producing the HBT having the described configuration. The method comprises steps of: 1) etching the sub-collector film deposited on the semiconductor substrate and forming a pair of depression in the sub-collector film, intrinsic region for the operation of HBT is formed therebetween. 2) Forming the collector film so as to plug depressions. 3) Forming the base film, the emitter film, and the emitter contact film on the contact film. 4) Etching the emitter contact film so as to expose portions of the emitter film both sides of the emitter contact layer. Because of the planar surface of the emitter film, etching-pits generated in the etching of the emitter contact film can be reduced. Depressions formed in the sub-collector are along a predetermined crystal axis on the substrate, and the width of the depression is prefer to be greater than 0.5 um and smaller than 2.0 um at the bottom of it. Further, it is preferable to form the contact film, the base film, the emitter film and the emitter contact film by the Metal Organized Chemical Vapor Deposition (MOCVD) technique. To use the MOCVD technique enables to plug depressions in the sub-collector film and to make a planar surface of the emitter film. 
     Still another aspect of the preset invention also relates to the method of the manufacturing process of the HBT. Another method comprises steps of, 1) etching the collector film deposited on the semiconductor substrate and forming a pair of depressions therein, the intrinsic region of the HBT is formed therebetween. 2) Forming the base film so as to plug depressions. 3) Forming subsequently films of the emitter film and the emitter contact film on the base film. Lastly, 4) etching the emitter contact film to make the emitter contact layer and to expose the surface of the emitter film on both sides of the emitter contact layer. The planar surface of the base layer prevents from bringing etching-pits on the emitter film. This enhances the reliability and the yield of the HBT. 
     The etching of the sub-collector film or the collector film is preferable to be done by a wet etching using a specific solution, which forms side edges of depressions to be normal mesa shapes and opening of the depression is wider than the bottom thereof. Therefore, plugging of depressions is facilitated, thus the planar surface of subsequently grown film can be obtained. 
    
    
     BRIEF DESCRIPTION OF DRAWINGS 
     FIG.  1 (A) is a plane view of the first embodiment of the present invention, FIG.  1 (B) is a cross sectional view along I—I in FIG.  1 (A), and FIG.  1 (C) is a cross sectional view along II—II in FIG.  1 (A); 
     FIG.  2 (A) is a plane view showing the first embodiment of the HBT at an intermediate step of the process, FIG.  2 (B) is a cross sectional view along I—I in FIG.  2 (A) and FIG.  2 (C) is a cross sectional view along II—II in FIG.  2 (A); 
     FIG.  3 (A) shows a plane view of the HBT at an intermediate step subsequent to FIG. 2, FIG.  3 (B) is a cross sectional view along I—I in FIG.  3 (A), and FIG.  3 (C) is a cross sectional view along II—II in FIG.  3 (A); 
     FIG.  4 (A) is a plane view of the HBT at an intermediate step next to FIG. 3, FIG.  4 (B) is a cross sectional view along I—I in FIG.  4 (A), and FIG.  4 (C) is a cross sectional view along II—II in FIG.  4 (A); 
     FIG.  5 (A) is a plane view of the HBT at an intermediate step next to FIG. 4, FIG.  5 (B) is a cross sectional view along I—I in FIG.  5 (A), and FIG.  5 (C) is a cross sectional view along II—II in FIG.  5 (A); 
     FIG.  6 (A) is a plane view of the HBT at an intermediate step next to FIG. 5, FIG.  6 (B) is a cross sectional view along I—I in FIG.  6 (A), and FIG.  6 (C) is a cross sectional view along II—II in FIG.  6 (A); 
     FIG.  7 (A) is a plane view of the HBT at an intermediate step next to FIG. 6, FIG.  7 (B) is a cross sectional view along I—I in FIG.  7 (A), and FIG.  7 (C) is a cross sectional view along II—II in FIG.  7 (A); 
     FIG.  8 (A) is a plane view of the HBT at an intermediate step next to FIG. 7, FIG.  8 (B) is a cross sectional view along I—I in FIG.  8 (A), and FIG.  8 (C) is a cross sectional view along II—II in FIG.  8 (A); 
     FIG.  9 (A) is a plane view of the HBT at an intermediate step next to FIG. 8, FIG.  9 (B) is a cross sectional view along I—I in FIG.  9 (A), and FIG.  9 (C) is a cross sectional view along II—II in FIG.  9 (A); 
     FIG.  10 (A) is a plane view of the HBT according to the second embodiment of the present invention, FIG.  10 (B) is a cross sectional view along III—III in FIG.  10 (A), and FIG.  10 (C) is a cross sectional view along IV—IV in FIG.  10 (A); and 
     FIG.  11 (A) is a view showing a sub-collector layer forming by no depressions, FIG.  11 (B) shows a mesa forming on the sub-collector layer in FIG.  11 (A), FIG.  11 (C) shows an emitter layer on an emitter contact layer after the etching of the emitter contact layer, FIG.  11 (D) is a cross sectional view along V—V in FIG.  11 (A), FIG.  11 (E) is a cross sectional view along VI—VI in FIG.  11 (B), and FIG.  11 (F) is a cross sectional view along VII—VII in FIG.  11 (C). 
    
    
     DETAILED DESCRIPTION OF THE INVENTION 
     Detailed description of the present invention will be described referring to the accompanying drawings. Constituents identical to each other or those having functions identical will be referred to with numerals of letters identical to each other without repeating over lapping explanations. In drawings, thickness of respective epitaxial layers does not reflect their real thickness. Axes shown in figures will involve their crystal graphical equivalence. 
     First Embodiment 
     FIG.  1 (A) shows a plane view of the HBT according to the first embodiment, FIG.  1 (B) is a cross sectional view along I—I line in FIG.  1 (A) and FIG.  1 (C) is also a cross section view along II—II line in FIG.  1 (A). The HBT  1  has a semi-insulating substrate  2 , a buffer layer, a sub-collector layer  40 , a collector layer  80 , a base layer  90 , an emitter layer  100 , and an emitter contact layer  110 . 
     The buffer layer  30  comprises an un-doped InGaAs with a thickness around 300 nm. The sub-collector layer  40  is formed by an n-type InGaAs with a thickness around 300 nm. The sub-collector layer is highly doped with Si, the electron concentration of the sub-collector is preferable from 0.5 to 2.0×10 19  cm −3 . This layer forms a mesa structure as shown in FIG.  1 (B) and FIG.  1 (C) with one edge is along [ 1 - 10 ] while the other edge is along [ 110 ]. The edge along [ 1 - 10 ] shows an inverse trapezium, while the edge along [ 110 ] shows a normal trapezium. 
     The collector layer  80  is un-dope InGaAs formed so as to cover the sub-collector layer  40  along [ 110 ], as shown in FIG.  1 (B); thus the width of the collector layer  80  is wider than the sub-collector layer. The top surface of the collector layer is flat. The thickness of the layer  80  is about 400 nm on the sub-collector layer  40  and about 800 nm on the buffer layer. 
     The base layer  90  is p-type InGaAs with a thickness around 50 nm. The plane shape of the base layer  90  corresponds to that of the collector layer  80 . The base layer  90  is highly doped with Zn, hole concentration of this layer is (1.0˜3.0)×10 19 [cm −3 ]. Carbon (C) may be used for p-type dopant substitute for Zn. 
     The emitter layer  100  is n-type InP with a thickness around 10 nm. The top surface of the layer  100  is almost flat. The plane shape of the emitter layer  100  corresponds to that of the base layer  90  and the collector layer  100  so that the width along [ 110 ] of the emitter layer  100  is greater than that of the sub-collector layer  40 . This layer is doped with Si, the electron concentration of the layer is about 4.0×10 18  [cm −3 ]. The thickness of the layer  100  is preferable to be greater than 5 nm and thinner than 20 nm. When the thickness is below 5 nm, the device would not show a transistor operation. On the other hand, the case that the thickness over 20 nm results on the decrease of the current multiplication coefficient. 
     The emitter contact layer  110  is an n-type InGaAs with a thickness around 250 nm. The cross sectional shape along [ 110 ] of the emitter contact layer shows the reverse trapezium, while it shows the normal trapezium along [ 1 - 10 ]. The edge along [ 1 - 10 ] of the emitter contact layer is apart from the edge of the emitter layer  100 . This layer comprises two portions based on the electron concentration, one is within 50 nm from the interface to the emitter layer  100  with the electron concentration is around 5.0×10 18  [cm −3 ], the other is above the former layer with the electron concentration around 2.0×10 19  [cm −3 ]. Greater electron concentration of the latter layer enables to form a superior ohmic contact between the emitter contact layer  110  and an emitter electrode  15  described below. 
     The HBT  1  has the emitter electrode  15  on the emitter contact layer  110 , a base electrode  16  on the emitter layer  100 , and a collector electrode  17  on the sub-collector layer  40 . These electrodes are made of composite metal of titanium (Ti), Platinum (Pt), and Gold (Au) sequentially formed in this order. A emitter wiring  25  is formed on the emitter electrode  15 , a base wiring  26  is on the base electrode  16 , and a collector wiring  27  is on the collector electrode  17 . These wiring are typically made of aluminum (Al). The HBT  1  has silicon nitride (Si 3 N 4 , hereinafter denoted by SiN) films ( 31 ,  32 ) for insulating respective electrodes and for passivating the HBT  1 . 
     Next is an operation of the HBT  1 . When the device is operated in the grounded-emitter connection, carriers flow from the emitter to the collector through the following path. Electrons are injected from the base electrode to the base layer  90  through the emitter layer  100  as minority carriers by the forward biasing between the base electrode and the emitter electrode. Injected carriers into the baser layer  90  flow in the base layer, through the emitter layer  100  and arrive to the emitter electrode. The current from the collector to the emitter flows from the collector electrode  17 , the sub-collector layer  40 , the collector layer  40 , the base layer  90 , the emitter layer  100 , the emitter contact layer  110 , and finally arrives to the emitter electrode  15 . The portion of the collector layer through which the current passes contributes the current multiplication. Namely, the sub-collector layer  40  defines the intrinsic collector. Similarly, although the emitter layer extends to both sides of the emitter contact layer and overlaps with the base layer, the emitter contact layer defines the intrinsic emitter. 
     The advantage of the HBT shown in FIG. 1 is that the top surface of the collector layer  80 , the base layer  90 , and the emitter layer  100  are almost flat in spite of that these layers are formed on the sub-collector layer with an island shape. When these layer bend tracing the shape of the sub-collector layer  40 , numerous etching pits may occur at bending portions of respective layer, thus decreasing the yield of the device. In the present HBT  1 , since top surfaces of these layers are formed almost flat, it prevents the generation of etching pits, which results in the improvement of the performance and the yield of the HBT. 
     Further advantage of the present HBT is that the base layer  90  is fully covered by the emitter layer  100 . When the surface of the base layer  90  is exposed, numerous surface states may be introduced at the manufacturing process such as immersing in a chemical solvent and etching in a reactive gaseous. On the other hand, since the base layer  90  is fully protected by the emitter layer  100  of the present HBT, the leak current due the surface states decreases. Moreover, since the emitter layer  100  can be grown continuously to the base layer  90  in a reactor chamber, it further decreases the surface states in the base layer  90 . 
     The SiN film deposited on the emitter layer  100  made of InP shows superior protective characteristics compared with that on the InGaAs layer. This is due to the fact that the SiN on InP layer shows smaller interface states on the surface of InP than that on the surface of InGaAs. Therefore, the emitter layer  100  covered by the SiN film also decreases the base leak current. 
     Another advantage of the present HBT  1  is the improvement of the high frequency performance due to the decrease of the base-collector capacitance. The area of the highly doped sub-collector layer  40  defines the base-collector capacitance. In the present HBT  1 , since the sub-collector layer is fully covered by the moderately doped collector layer  80  and the are of the sub-collector layer  40  is smaller than the collector layer  80 , the base-collector capacitance decreases which enables to enhance the high frequency performance of the HBT. Moreover, since the thickness of the base layer  90  is thinned to about 50 nm, this also decreases the base-collector capacitance. 
     Next is a manufacturing process of the present HBT referring from FIG. 2 to FIG. 9 that show the configuration at respective process steps. In respective figures, the drawing A shows a plane view, the drawing B shows the cross sectional view along I—I line, and the drawing C shows the cross sectional view along II—II line. 
     In the process, the Metal Organized Chemical Vapor Deposition (MOCVD) technique is applicable to grow respective semiconductor films using various types of source materials, such as Triethyl Gallium (TEGa), Trimethyl Indium (TMIn), Arsine (AsH 3 ), and Phosphine (PH 3 ). To adjust the conduction type and the carrier concentration, silane (SiH 4 ) and diethyl zinc (DEZn) are used for the n-type doping source and p-type doping source, respectively. Tetrachloromethane (CCl 4 ) is substitutable for the diethyl zinc as a dopant for p-conductive type. By supply these source materials into the reaction chamber, desired semiconductor films with the composition and the carrier concentration could be obtained. Temperatures from 600° C. to 750° C. are prefer for respective semiconductor films to take the crystal quality into account. 
     First Epitaxial Growth 
     The buffer film  3  and the sub-collector film  4  are grown on the ( 001 ) surface of the semi-insulating InP substrate  2  by the MOCVD method (FIG.  2 (A)˜FIG.  2 (C)). The buffer film  3  is made of un-dope InGaAs with 300 nm thickness. The sub-collector film  4  is an n-type InGaAs with 300 nm thickness. This film  4  contains Si as n-type dopant with the concentration of 1.0×10 19  [cm −3 ]. 
     Formation of the Sub-Collector Layer 
     An etching mask  5  with a photo resist  4  is formed on the sub-collector film  4  (FIG.  3 (A)˜FIG.  3 (C)). The mask  5  has two openings ( 5   a ,  5   b ) expanding along [ 1 - 10 ] and width along [ 110 ] of openings are about 1.6 um. The sub-collector film  4  is etched by this mask  5  with a solution of sulfuric acid (H 2 SO 4 ): hydrogen peroxide (H 2 O 2 ): water (H 2 O)=1:1:500. This etching forms two depressions ( 6   a ,  6   b ) on the sub-collector film  4  and the sub-collector layer  40  is formed between two depressions. The edges along [ 1 - 10 ] of the sub-collector layer  40  shapes a normal mesa, thus the cross section of the sub-collector layer  40  is a trapezium. The width W T  of the opening at the top thereof is about 1.6 um and that W B  at the bottom is about 0.8 um, respectively. 
     Second Epitaxial Growth 
     Next, the collector file  8 , the base film  9 , the emitter film  10  and the emitter contact film  11  are successively grown on the InP substrate  2 . Films from the base  9  to the emitter contact  11  are contained respective dopant with predetermined concentration, which results on the electron or the hole concentration. The collector film is made of un-doped InGaAs. As shown in FIG.  5 (B), the collector film  8  has the flat top surface because depressions formed in the sub-collector film are filled with InGaAs of the collector film  8 . The base film  9 , the emitter film  10  and the emitter contact film  11  also have flat top surfaces. The flatness of the top surface of the collector film  8  depends on the width of depressions in the cub-collector film  7 . Between 1.0 um and 2.5 um are preferable for the width of the opening W T . Below 1.0 um makes projections on depressions and Over 2.5 um results on undulations. Further, the bottom width W B  of depressions is preferable to be greater than 0.5 um and smaller than 2.0 um. In the growth of the emitter contact film, the quantity of silane supply is increased, which divides the emitter contact film into the lower portion with the electron concentration about 1.0×10 18  [cm −3 ] and the upper portion with the concentration about 2.0×10 19  [cm −3 ]. 
     Formation of Emitter Contact Layer 
     The mask with a predetermined coverage is formed on the emitter contact film  11 . Etching by using a solution of the sulfuric acid, the hydrogen peroxide and the water forms the emitter contact layer  110 . The emitter film  10  shows a function of etch-stopping layer because the etching of InP by this solution is by far smaller than InGaAs. Once exposed the emitter film made of InP, the etching substantially stops. The cross sectional shape of the emitter contact layer shows a reverse trapezium along [ 1 - 10 ] and a normal one along [ 110 ] (FIG.  6 (A) to FIG.  6 (C)). 
     Primary Mesa Formation Step 
     After the formation of the emitter contact layer  110 , another mask is formed so as to cover the primary portion of the device, which contains the emitter contact layer, the emitter layer, the base layer and the collector layer. This mask has a rectangle shape, one edge is along [ 110 ] and the other edge is along [ 1 - 10 ]. The etching for forming the primary mesa is similar to that for the device isolation. Namely, the process comprises the first etching for the InP emitter by the hydrochloric acid solution and the second etching for the other layer by the sulfuric acid solution, which forms the base layer  90 , the collector layer  80 . The second etching is preferable to remove a portion of the sub-collector layer over 100 nm to expose the layer inevitably. Thus, the primary mesa  120  of the collector layer  80 , the base layer  90  and the emitter layer  100  are formed (FIG.  7 (A) to FIG.  7 (C)). 
     Device Isolation Process 
     After the primary mesa formation, another mask for the device isolation covers an area where the HBT is formed. Tow step etching is performed. First, a mixture of the hydrochloric acid and the water removes an area not covered by the mask. Since this solution can not etch InGaAs, the etching completely stops at the exposing of InGaAs base film. Secondly, another solution of the sulfuric acid, the hydrogen peroxide, and the water etches the area the base film  9 , the collector film  8 , and the buffer film  3 , they are not covered by the mask and the just etched InP emitter layer. This second etching isolates respective HBT devices (FIG.  8 (A) to FIG.  8 (C)). 
     Formation of Electrodes 
     Electrodes of the base, and the emitter are formed as follows by a self-alignment process: First, an insulating film of SiN is deposited on the InP substrate  2 , which covers the whole primary mesa  120 . An etching mask if formed on the SiN film by a chemical vapor deposition (CVD) technique. The mask has openings on the emitter layer  100  and on the emitter contact layer  110 . The reactive ion etching (RIE) removes SiN film within openings and exposes the surface of the emitter layer  100  and the emitter contact layer  110 . A combination of metals, such as platinum (Pt), titanium (Ti), platinum (Pt) and gold (Au) are successively deposited in openings. Portions just aside the emitter contact layer  110  on the emitter layer  100 , which are hidden by eaves of the emitter contact layer  110  along [ 1 - 10 ], are escaped from the deposition of metals. This divides the emitter electrode on the emitter contact layer  110  and the base electrode on the emitter layer  100 . This self-alignment process enables to shorten the pass from the base electrode to the emitter electrode through the base layer, which reduces the base resistance of the HBT and enhances the high frequency performance of the device. The lift-off process removes surplus metals on the mask. Namely, metals on the resist mask are lifted off with removing the resist by a solvent. A thermal treatment under the condition of 400° C. and 1 minute in an inactive atmosphere makes the emitter electrode  15  and the base electrode  16  with an ohmic characteristic to respective semiconductor layers. The similar process forms the collector electrode  17  with the emitter and the base electrode formation (FIG.  9 (A) to FIG.  9 (C)). 
     Wiring Process 
     Finally, wiring for respective electrodes are formed. Another insulating film made of SiN is deposited so as to cover all electrodes and the primary mesa of the HBT. A resist mask is formed on the SiN film, which has openings corresponding to via holes on respective electrodes. After etching the SiN film on electrodes by RIE technique and removing the resist, three-layered film of resist/SiO 2 /resist is formed on the SiN film again, which has openings so as to include openings just etched and regions corresponds to their respective wiring. Wiring metal, such as aluminum, is deposited within openings and on the three-layered film, and removing surplus metals on the three-layered film forms wiring for respective electrode. The wiring contacts to electrodes through via holes. The similar process performs wiring for the emitter electrode with that for the base and the collector electrode depicted above. Thus, HBT shown in FIG.  1 (A) to FIG.  1 (C) is competed. 
     Second Embodiment 
     The HBT of the second embodiment has almost similar configuration with the first embodiment except that the HBT has not the sub-collector layer. FIG.  10 (A) is a plane view of the HBT according to the second embodiment. FIG.  10 (B) is a cross sectional view along III—III line and FIG.  10 (C) is a cross sectional view along IV—IV line. The HBT  200  comprises the semi-insulating InP substrate  2 , the buffer layer  30 , the collector layer  800 , the base layer  900 , the emitter layer  100 , and the emitter contact layer  110 . The collector layer  800  is n-type InGaAs with 400 nm thickness and has the electron concentration of 1.0˜10.0×10 18  [cm −3 ] by Si doping. The plane shape of the collector layer is a rectangle, one edge is along [ 1 - 10 ] and the other edge is along [ 110 ]. 
     The base layer  900  is p-type InGaAs that covers the mesa-shaped collector layer  800 . The top surface of the base layer  900  is a flat surface. The thickness of the layer is about 100 nm on the collector  800 , while that is about 500 nm on the buffer layer  30 . The width of the emitter layer  100  along [ 110 ] is wider than the collector layer  800 . Other configurations, such as the composition of Indium in the emitter contact layer and the buffer layer, and the carrier concentration of the emitter contact layer, are same as that of the first embodiment but not restricted to those values. 
     The HBT  200  has the collector electrode on the collector layer  800 , which is peculiar to the second embodiment. Wiring to respective electrodes and the insulating film of SiN are also same as case of the first embodiment. 
     Next describes the manufacturing method of the HBT  200 . First, the buffer film and the collector film are grown on ( 001 ) surface of the InP substrate. Two depressions are formed in the collector film by etching described in the first embodiment. The shape and dimensions of depressions are same as those ( 6   a ,  6   b ) formed in the first embodiment. Regions between depressions operate as the collector layer  800 . After etching of depressions, the base film, the emitter film and the emitter contact film are successively grown on the substrate so as to cover depressions. Since the flatness of the surface of the base film depends on the thickness of subsequently grown film as shown in the first embodiment, it is required to adjust the width of the depression. 
     Next, the emitter contact film is etched by a solution of phosphoric acid and hydrogen peroxide using an etching mask to form the emitter contact layer  110 . The plane shape of the emitter contact layer is rectangle with longer edge extending along [ 1 - 10 ], the cross section of which shows the reverse trapezium. After the formation of the emitter contact layer  110 , a serious of manufacturing process follows, such as the device isolation, the primary mesa formation, electrodes formation, and the wiring formation. Finally, the HBT  200  of the second embodiment is completed. 
     As described before, the thickness of the base layer  900  is about 100 nm on the collector layer  800 , while it is about 500 nm on the buffer layer  30 . This means that the cross section of the pass where the base current flows becomes large, which reduces the base resistance and enhances the high frequency performance of the HBT. 
     From the invention thus described, it will be obvious that the invention may be varied in many ways. The composition of InGaAs is selected so as to match the lattice constant of the material to that of the InP. Where the lattice matching means the difference of the lattice constant between two materials is within±0.1%. Further, undoped means that the intentional doping has not fulfilled. Although embodiments depicts the combination of the InP substrate and the InGaAs layer for the collector, the base layer, the subject of the present invention is applicable to the combination of the GaAs substrate and the AlGaAs layers, and also the combination of the GaAs substrate ant the InGaP layers. Moreover, though embodiments depict the specific solution for the formation of depressions in the sub-collector film, another solution is usable if only the solution makes the depression so as that the bottom is smaller than the opening of it. 
     Such variations are not to be regarded as a departure from the spirit and scope of the invention, and all such modifications as would be obvious to one skilled in the art are intended for inclusion within the scope of the following claims.