Abstract:
The invention relates to a method of, and a device for delivering a predetermined ( 1 ) volume of beverage into a thermoplastic container formed from a heated preform, the preform being positioned in a mould, characterized in that the method includes a step of injecting at least some beverage into a recess in the preform so as to promote expansion of the preform inside the mould, the mould defining the shape of the container, a longitudinal displacement of a stretch rod ( 10 ) carried out during a given period ensuring longitudinal elongation of the heated preform, the stretch rod being immobile at the end of the given period, and a volume of beverage greater than a predefined fraction of the predetermined volume, preferably equal to 50%, being present in the recess at said end of the given period.

Description:
PRIORITY CLAIM 
       [0001]    This application is a divisional application of U.S. patent application Ser. No. 13/002,197, filed on Dec. 30, 2010, which is a National Stage of International Application No. PCT/EP2009/058306, filed Jul. 2, 2009, which claims priority to European Application No. 08159855.9, filed Jul. 7, 2008, the entire contents of which are being incorporated herein by reference. 
     
    
     FIELD OF THE INVENTION 
       [0002]    The present invention relates to the field of manufacturing containers made of a polymer material, especially a polyester. More particularly, it relates to the field of manufacturing polyester bottles, preferably polyethylene terephthalate (PET) bottles containing a liquid, preferably water and especially mineral water. 
       BACKGROUND 
       [0003]    For many years, the PET bottles usually found on the market have been manufactured by the blow moulding or stretch-blow moulding of PET preforms using compressed air. 
         [0004]    A preform usually takes the form of a cylindrical tube closed at one of its ends and open at its opposite end. The open head of the preform corresponds to the neck of the container. During the conventional process for manufacturing containers from preforms, the preforms are slipped onto the cylindrical mounts of a continuous conveyor chain, which thus transports the preforms through an oven, essentially formed by a straight section bordered on each side by radiative heating means, so as to temperature-condition the plastic for the subsequent stretch-blow moulding step. 
         [0005]    The hot preform is then taken off and transported into a mould of a blow moulding machine. The transport movement, performed for example by a transfer arm, is coordinated with that of the blow moulding machine, which is generally produced in the form of a rotary carousel that rotates continuously about its vertical axis and carries, on its periphery, a series of identical moulds. Thus, the preform is placed in the mould immediately after it has been opened and the previously formed container has been removed. 
         [0006]    The preform is heated beforehand so as to be in the mould at a temperature above the glass transition temperature (about 100° C.) so as to enable it to be formed by stretch-blow moulding. The temperature of the preform at the end of the heating step is slightly above that required inside the mould of the blow moulding machine, so as to take into account the cooling that takes place over the distance that exists between the heating site and the blow-moulding site. Thanks to the simultaneous presence of several moulds, such a blow moulding machine can produce containers at very high rates, of around several tens of thousands of units per hour, i.e. around 1000 to 2000 bottles per hour per mould. 
         [0007]    The stretch-blow moulding takes place by stretching using a metal rod and by injecting air at pressures ranging from 3 to 40 bar (3×10 5  Pa to 4×10 6  Pa). The air is injected through a nozzle, the end of which is introduced through the opening in the head of the preform. 
         [0008]    Bottles manufactured by injecting pressurized air have a relatively satisfactory lifetime. However, the intrinsic properties and characteristics of PET, in particular its specificity which is to crystallize on being stretched, mean that even better results may be envisaged by modifying the container manufacturing process. In particular, it is known that high crystallinity means better mechanical strength. 
         [0009]    The present invention makes it possible to extend the average lifetime of the containers within the context of normal transport, distribution and consumption. It also makes it possible to speed up the industrial production process, by optimizing the production steps and minimizing the in-line losses. 
         [0010]    The invention applies preferentially to the class of polyesters in general, and to PET in particular. 
       SUMMARY 
       [0011]    The Applicant therefore proposes, within the context presented above, a method of delivering a predetermined volume of beverage into a thermoplastic container formed from a heated preform, the preform being for example approximately cylindrical and positioned in a mould, the method including a step of injecting at least some beverage into a recess in the preform so as to promote expansion of the preform inside the mould, the mould defining the shape of the container, a longitudinal displacement of a stretch rod carried out during a given period ensuring longitudinal elongation of the heated preform, the stretch rod being immobile at the end of the given period, and a volume of beverage greater than 50% of the predetermined volume being present in the recess at said end of the given period. 
         [0012]    This method makes it possible to improve the quality of the containers obtained. In general, the condition whereby the bottle-filling piston has already covered more than half of its total travel when the stretching is stopped is a sine qua non condition for preventing the bottle from exploding in the mould. 
         [0013]    According to one advantageous feature, a volume of beverage greater than 75%, of the predetermined volume is present in the recess at said end of the given period. 
         [0014]    The containers obtained using this method have much better characteristics than those obtained with a conventional stretch-blow moulding method using gaseous fluid to inflate them. In particular, it has been found that, for a given weight and a given type of material, they have a longer lifetime. The degree of crystallinity, i.e. the mass of crystalline phase relative to the mass of polymer, of a container obtained by the method according to the invention may in particular be much higher. 
         [0015]    According to one embodiment, the displacement and the injection are controlled by a programmable computer-aided manufacturing device. 
         [0016]    Alternatively, and optionally in combination, the displacement and the injection are controlled by a cam. 
         [0017]    According to one advantageous feature, during said prior heating step, the temperature of the preform is brought to between 50° C. and 130° C., or even to between 75° C. and 100° C. 
         [0018]    Preferably, a speed of the stretch rod reached during said displacement is between 0.5 and 3.0 m/s, or even between 1 and 2.5 m/s. 
         [0019]    According to a preferred feature, during the injection step, a volume of beverage has a temperature between 1° C. and 120° C., or even a temperature between 10° C. and 90° C. 
         [0020]    Preferentially, provision is made for a longitudinal stretch ratio of the preform, measured between the start and end of the injection step, to be between 2 and 5 or between 2.5 and 4. 
         [0021]    Moreover, according to one embodiment, a radial stretch ratio of the preform, measured between the start and end of the injection step, is between 2 and 7, or even between 3 and 4.5. 
         [0022]    It should be emphasized that the invention applies most particularly well to the case in which the thermoplastic is chosen from the group consisting of polyethylene terephthalates, polypropylenes, polyethylenes, polycarbonates, polystyrenes, polylactic acids, polyvinyl chlorides and combinations thereof. 
         [0023]    Preferably, the method further includes a prior gas injection step so as to promote expansion of said preform, such that the volume of the preform is brought up to a predefined fraction, advantageously 70%, of the predetermined volume. 
         [0024]    Advantageously, the prior gas injection step is followed by a beverage injection step so as to promote expansion of said preform until the preform has reached said predetermined volume. 
         [0025]    This is because air is not as capable as the beverage of cooling the thermoplastic undergoing expansion. These characteristics therefore have the advantage of providing a more stable method and a wider window in implementing the method. 
         [0026]    According to one advantageous feature, the mould is brought beforehand to a temperature at least 50° C. below the melting point of the thermoplastic. 
         [0027]    Again, the method according to the invention may also include a subsequent step of fitting a closure cap onto the container. 
         [0028]    In this case, the step of injecting at least some of the beverage preferably comprises injecting a volume of beverage into which gas has been introduced beforehand so as to create an overpressure in the neck of the container after the closure cap has been fitted. 
         [0029]    Finally, according to one aspect, the longitudinal displacement of the rod is performed at a constant speed. 
         [0030]    Also, the invention takes place through a nozzle having a bell-shaped head, so as to reduce the risks of deforming a neck of the preform. 
         [0031]    The invention also proposes a device for delivering a predetermined volume of beverage into a thermoplastic container formed from a heated preform, the preform being approximately cylindrical and positioned in a mould, the device comprising means for injecting at least some beverage into a recess in the preform so as to promote expansion of the preform inside the mould, the mould defining the shape of the container, means for longitudinally displacing a stretch rod over a given period and for longitudinally elongating the heated preform, the stretch rod being immobile at the end of the given period, and means for ensuring that a volume of beverage greater than a predefined fraction of the predetermined volume, preferably 50%, is present in the recess at said end of the given period. 
         [0032]    Advantageously, this device may include means suitable for carrying out the respective intended steps of the method, taken separately or in combination. 
     
    
     
       BRIEF DESCRIPTION OF THE FIGURES 
         [0033]    The invention will now be described in detail with reference to the appended figures, which relate to exemplary embodiments. 
           [0034]      FIG. 1  shows the monitoring of the formation of a mineral water bottle according to an example of the prior art. 
           [0035]      FIG. 2  shows a crystallinity scale used in relation to the method according to the invention. 
           [0036]      FIG. 3  shows a general diagram of the installation used. 
           [0037]      FIG. 4  shows the monitoring of the formation of a mineral water bottle according to a preferred embodiment of the invention. 
           [0038]      FIG. 5  shows another aspect of the invention. 
       
    
    
     DETAILED DESCRIPTION 
       [0039]    The embodiment given here by way of example relates to a process for manufacturing PET mineral water bottles from a heated preform. The preform has the shape of a cylindrical tube closed at its lower end. The open head of the preform corresponds to the throat or neck of the bottle, onto which a closure cap is screwed. 
         [0040]      FIG. 1  shows the variation over time of the position  1  of the stretch one solution of the prior art. 
         [0041]    In this figure, the x-axis represents time, the y-axis on the left represents the linear position of the stretch cam, while the y-axis on the right represents the air pressure in the preform undergoing expansion. 
         [0042]    During a first phase 4 of the process, in particular between 50 ms and 275 ms, the stretch rod advances linearly, with an approximately constant speed. 
         [0043]    320 ms after the start of the process (reference  3 ), the stretch rod has reached its final position P f , from which it no longer moves. 
         [0044]    During a first part  4   a  of the first phase of the process, the air pressure  2  in the preform, initially equal to the atmospheric pressure P a  and remaining so up to 150 ms after the start of the process, increases up to a value of about 1.4 times the atmospheric pressure, which value is reached 200 ms after the start of the process. 
         [0045]    During a second part  4   b  of the first phase of the process, lasting a further 100 ms, i.e. up to 300 ms after the start of the process, the pressure remains constant. 
         [0046]    During a second phase 5 of the process, the pressure rapidly increases, with an approximately constant rate of rise until 450 ms, when it reaches a value equal to about 8 times the atmospheric pressure. 
         [0047]    From this moment on, the pressure in the expanding preform decreases slightly, while still remaining of the order of magnitude of 8 times the atmospheric pressure. 
         [0048]    Moreover, and without wishing to be tied down by any scientific theory, it is known that polyester preforms are amorphous and that the stretching induces, at the same time, crystallization and an exothermic reaction. Now, the evolution of heat is deleterious to the development of crystallinity. 
         [0049]    Referring to  FIG. 2 , a first stretch is therefore performed with the stretch rod, causing crystallization and evolution of heat, and at that moment the incompressible fluid is introduced, which then absorbs the heat given off and shifts the equilibrium point of the crystallinity obtained in the final container towards high values, preferably between 30 and 35%. 
         [0050]    The crystallinity is measured in a Lloyd-Davenport density column using the following method. The column is filled with a salty (calcium nitrate) solution having a density gradient. The column is calibrated with balls having a known density between 1.335 and 1.455. Next, small pieces of the container according to the invention are immersed in the column and after a certain time these stabilize at a certain height in the column corresponding to a certain density. The measurements are made at 23° C. The table in the figure gives the crystallinity. 
         [0051]    Referring to  FIG. 3 , a stretch rod  10  is inserted into a compressed-air actuator  15 . The stretch rod  10  is controlled by a stretch motor which gives it a longitudinal movement (represented by an arrow). 
         [0052]    The compressed-air actuator  15  comprises a cylinder  17  controlling an injection head  18 , through which the stretch rod  10  passes. The injection head  18  is connected to the neck  20  of a PET preform placed in a mould (not shown), which preform, after being expanded, takes on the shape of a mineral water bottle, this shape being determined by the wall of the mould. 
         [0053]    The actuator comprises three chambers, the upper two chambers  15   a  and  15   b  being filled with compressed air. Between these upper two chambers, a piston wall  19  slides in a direction parallel to the stretch rod (the displacement being represented by an arrow). The stretch rod  10  passes through the centre of this wall  19 . 
         [0054]    The compressed-air actuator also includes a lateral inlet  30  for the beverage, here mineral water, connected to the third chamber  15   c  of the actuator, this being the bottom chamber. The beverage is fed in via a line  32 . 
         [0055]    An external mineral water inlet feeds the liquid via the remote end of this line  32  into a first valve  34 , which is connected to the opening of a single-chamber filling cylinder  40  comprising a piston  42  controlled by a filling motor (movement of which is represented by an arrow). This motor imparts a longitudinal movement on the piston in the single chamber of the filling cylinder  40 . 
         [0056]    On the line  32  there is a second valve  36 , which is in series behind the first valve  34  and the opening of the filling cylinder  40 . The line  32  then runs into the bottom chamber  15   c  of the compressed-air actuator  15 . 
         [0057]    The bottom chamber  15   c  of the compressed-air actuator is penetrated by the cylinder  17  for controlling the filling head  18 , the internal volume of which emerges through the lower outlet of the compressed-air actuator  15  into the filling head  18 . The control cylinder has a lateral opening allowing the beverage to circulate between the bottom chamber of the actuator and the inside of the control cylinder. 
         [0058]    The stretch rod  10  itself passes through the control cylinder  17  as far as the filling head  18  and the neck  20  of the bottle preform. 
         [0059]      FIG. 4  shows the variation over time of the position  101  of the stretch rod and the position  102  of the filling actuator controlling the inflow of the mineral water into the expanded preform. 
         [0060]    The horizontal axis represents the time, the left-hand vertical axis represents the position of the stretch rod and the right-hand vertical axis represents the volume of water introduced into the expanded preform, this being proportional to the position of the filling actuator. 
         [0061]    During a first part of the process, from 0 to 250 ms, the stretch rod advances at an essentially constant rate, according to a preferred embodiment. 
         [0062]    However, according to another embodiment, during a first phase  110  of the process, in particular from 0 to 150 ms, the stretch rod advances at an increasing speed due to a positive acceleration. During a second phase  115  of the process, from 150 ms to 250 ms, the stretch rod advances with a negative acceleration, the speed decreasing until it becomes zero at 250 ms. However, it will be understood that the changes in speed must be sufficiently gentle to ensure regular and reliable stretching of the thermoplastic. 
         [0063]    250 ms after the start of the process (reference  103 ), the stretch rod has reached its final position Pf, from which it no longer moves. 
         [0064]    At the same instant, the filling actuator has introduced a volume V 1  of mineral water into the expanded preform. The volume introduced from the start of the process (therefore between 0 ms and 250 ms) has progressively increased, with a progressive increase in the flow rate (filling actuator displacement acceleration). 
         [0065]    During the moments that follow, which constitute a third phase  120  of the process, up to 320 ms, the total volume of water introduced is constant, the flow rate being invariant. Next, the volume suddenly decreases by a small fraction (around 4%) over a period of 40 ms. 
         [0066]    From this instant on, the total volume introduced stabilizes around the value V 2 , which is finally reached after a few oscillations, the flow rate of liquid being introduced being zero. 
         [0067]    A few instants later, starting from 450 ms after the start of the process (reference  104 ), the filling actuator has reached a final position, from which it no longer moves. At this moment, it has introduced a volume V 2  of mineral water into the expanded preform. The volume V 2  is greater than V 1 , but less than twice the volume V 1 . 
         [0068]    During the method of using the device described, the temperature of the preform is brought beforehand to a value between 50° C. and 130° C., or even between 75° C. and 100° C. In the preferred embodiment, this value is 85° C. 
         [0069]    In general, a bottle is defined to be of high quality on the basis of the fact that it has not exploded in the mould. 
         [0070]    The tests carried out show that it is not possible to form a bottle completely if physically it has not reached 50% of its final volume at the end of the active stretching. 
         [0071]    During the method of using the device described, the temperature of the preform is brought beforehand to a value between 50° C. and 130° C., or even between 75° C. and 100° C. In the preferred embodiment, this value is 95° C., the plastic used being PET. 
         [0072]    The rod has a speed of between 0.5 and 3.0 m/s″1, or even between 1.0 and 5 m/s′. In the preferred embodiment, this value is 1.6 m/s−′. 
         [0073]    The temperature of the beverage is brought beforehand to a value between 1° C. and 120° C., preferably between 10° C. and 90° C. In the preferred embodiment, this value is 30° C. 
         [0074]    The longitudinal stretch ratio of the thermoplastic is between 2 and 5 or even between 2.5 and 4. In the preferred embodiment, this value is 3.5. 
         [0075]    The radial stretch ratio of the thermoplastic is between 2 and 7, or even between 3 and 4.5. In the preferred embodiment, this value is 4. 
         [0076]    The thermoplastic is chosen from the group consisting of polyethylene terephthalates, polypropylenes, polyethylenes, polycarbonates, polystyrenes, polylactic acids, polyvinyl chlorides and combinations thereof. In the preferred embodiment, it is PET. 
         [0077]    The temperature of the mould is at least 50° C. below the melting point of the thermoplastic, which in the case of PET is 230° C. Preferably, this temperature is maintained below 100° C. In the preferred embodiment, the temperature of the mould is equal to the ambient temperature. 
         [0078]    Referring to  FIG. 5 , a bell-shaped nozzle end-piece  500  according to a preferred embodiment is shown. The internal and external pressures on either side of the circumference of the neck of the preform (i.e. on the external surfaces  510  of the neck and on the internal surfaces  520  of the neck) are identical, owing to the presence of a passage  505  connecting the volumes on either side of the circumference, inside the nozzle. During filling, sealing is provided by the flange  530  on the preform. Thanks to this device, there is no risk of the neck of the preform deforming while a pressurized fluid is being injected by the nozzle. 
         [0079]    According to another embodiment, a nozzle end-piece holds the external surfaces  510  of the neck of the preform in such a way that when a pressurized fluid is injected via the top of the nozzle into the recess of the preform, the pressure exerted on the internal walls  520  of the neck of the preform by the fluid is compensated for by the holding by the walls of the bell-shaped nozzle end-piece. The neck of the preform therefore does not deform, despite the high pressure. 
         [0080]    Of course, the invention is not limited to the embodiments described and illustrated by the appended drawings; rather it extends to all variants that can be envisaged by a person skilled in the art within the scope of the claims.