Abstract:
A device and method is disclosed for manufacturing optical fiber preforms utilizing microwave plasma assisted chemical vapor deposition. Precursor gas is introduced to the face of a vertically mounted dielectric rod, and a plasma is struck by means of simultaneous excitation of an E01 type wave and an H type wave with rotating linear polarization. The silica rod is positioned so that its face is at the bottom of the tube. Precursor gas is delivered from a position below the face of the silica rod, and microwave energy, which travels through the rod to the rod face, is delivered from a source positioned above the rod. With this configuration, a uniformly dense plasma localized on the face of the rod can simultaneously deposit both a pure or doped core and a doped cladding. It is also useful for creating waveguides, preform cores for use as substrates in creating optical fiber preforms, capillaries and ceramic rods.

Description:
BACKGROUND OF THE INVENTION  
         [0001]    1. Field of the Invention  
           [0002]    The invention relates to the manufacture of optical fiber preforms and preform rods.  
           [0003]    2. Information Disclosure Statement  
           [0004]    Silica activated lightguides with flourine doped silica (SiO 2 —F) claddings and cores doped with Al or Ge and/or Rare earth elements (Neodymium, Erbium, Holmium, Ytterbium, Europium and so on) are widely used for the creation of optical fiber amplifiers, lasers and sensors of different types. In UV fibers, however, the presence of Germanium can result in ultraviolet radiation-induced color centers, which are point defects in the core&#39;s silica that generate absorption bands in the UV and visible spectrum that deteriorate the optical fiber transmission in that spectral region. Lightguides containing an SiON core and SiO 2 —F cladding would be useful for ultraviolet applications because of the absence of Germanium in the lightguide core. SiON cores are useful in that they provide the ability to easily change the refractive index during manufacture within a 1.5-2.0 range by modifying the ratio of O 2  to N 2  in the glass matrix. This enables modification of the numerical aperture of SiO 2 /SiON and SiO 2 —F/SiON lightguides within a wide range. Furthermore, lightguides with SiON cores have a high radiation resistance. It would be extremely useful to have a method for production of such lightguides.  
           [0005]    Presently, the most popular methods for manufacturing optical fiber preforms are Modified Chemical Vapor Deposition (MCVD), Outside Vapor Deposition (OVD), Vapor Axial Deposition (VAD), Plasma Enhanced CVD (PCVD), and Surface Plasma CVD (SPCVD).  
           [0006]    The main disadvantage of MCVD, OVD, and VAD technologies for manufacturing preforms with active cores is that these methods require a step during the deposition in which soot glass layers are formed. The presence of soot makes it difficult to fabricate cores or claddings with steep doping profiles. Another disadvantage of these methods is the difficulty of achieving homogeneous doping, especially for lightguides with high rare earth element (REE) concentrations. Both the ability to deposit glass directly from the gas phase without a soot-forming stage and the ability to reduce the length of the active part of optical fiber lasers and amplifiers at high REE concentrations are the main advantages of deposition with a microwave plasma at low pressure. Additionally, only low pressure microwave plasma techniques have been able to provide effective N 2 -dissociation (when the electron temperature is essentially higher than gaseous one, or when T e &gt;&gt;T g ) because of the high bond energy of N 2 . Despite the advantages of plasma-chemical technologies in optical fiber preform production, effective tubeless microwave plasma-chemical technologies for the production of optical fiber preforms, including for example, activated and N 2 -doped preforms, have not been developed before the present time.  
           [0007]    Methods for manufacturing dielectric rods by low pressure microwave plasma deposition are known. One such method is described in European Patent No. 0094053B1 by Beerwald et al. This method is also described in U.S. Pat. No. 4,508,554 by Beerwald et al, which is in the same family as European Patent No. 0094053B1. However, this method possesses three major drawbacks.  
           [0008]    The first major disadvantage of the Beerwald patent is its inability to produce uniform microwave power density both in the microwave discharge and on the rod face using only either an E 01  excitation mode or a circularly polarized H excitation mode. This results in a nonuniform deposition of doped silica glass on the rod face. Beerwald also provides for rotation of the rod, but rotating the rod is insufficient to fully compensate for the nonuniform deposition.  
           [0009]    The second major disadvantage is that the Beerwald invention is capable of delivering only relatively low microwave power densities on the rod face when the disclosed operating parameters are implemented. For example, only 50-60 W/cm 2  was achieved at the rod face when deposition on a described 60 mm diameter rod was attempted using the described 2 kW generator power under an operating gas pressure of 1 torr. The result of this low power density is a relatively low silica glass deposition rate (0.1-0.2 g/min) because the E 011  resonator used by Beerwald is ineffective (it has low Q-quality in case of microwave plasma ignition).  
           [0010]    The third major disadvantage is the Beerwald invention&#39;s inability to simultaneously provide both a temperature as high as 1200° C. and a high uniform power density (220-250 W/cm2). A high temperature is needed for effective removal of Cl 2  from the deposited glass, and high uniform power density is required to produce a high deposition rate and effective dissociation and ionization of reagents at the rod face and in the microwave discharge. This invention is unable to perform these functions using only a single channel for the control and transmission of continuous microwave energy and thus one excitation mode.  
           [0011]    An additional drawback to the Beerwald invention arises from the configuration of the described device. According to Beerwald, precursor gas is introduced above the substrate rod face. This configuration could lead to potential impurities or nonuniformities in the resultant deposition. Because the gravitational force tends to pull introduced gas particles toward the face of the substrate rod, the potential exists for unwanted particles, such as sootlike particles including Si, SiO 2  and SiO, to drop onto the face of the substrate rod and reduce the purity of the preform produced. Additionally, the additional gravitational force on molecules created in the plasma can reduce control over the deposition of the molecules, and result in less effective control over the thickness of the deposition.  
         OBJECTIVES AND BRIEF SUMMARY OF THE INVENTION  
         [0012]    It is an object of the present invention to provide a method and device for the efficient production of optical fiber preforms and preform rods.  
           [0013]    It is another object of the present invention to provide an effective device and method for the manufacture in one process of both claddings and cores of optical fiber preforms.  
           [0014]    It is yet another object of the present invention to provide an effective device and method for production of preforms with a flourine-doped silica cladding and a core doped by Aluminum, Germanium or Rare Earth Elements.  
           [0015]    It is still another object of the present invention to provide an effective device and method for production of preforms with SiON cores that are useful for ultraviolet wave applications.  
           [0016]    Briefly stated, the present invention provides a device and method for manufacturing optical fiber preforms utilizing microwave plasma assisted chemical vapor deposition. Precursor gas is introduced to the face of a vertically mounted dielectric rod, and a plasma is created by means of simultaneous excitation of an E 01  type wave and an H type wave with rotating linear polarization. The silica rod is positioned so that its face is at the bottom of the tube. Precursor gas is delivered from a position below the face of the silica rod, and microwave energy, which travels through the rod to the rod face, is delivered from a source positioned above the rod. With this configuration, a uniformly dense plasma localized on the face of the rod can deposit both a pure or doped core and a doped cladding simultaneously or in a single process. It is also useful for creating waveguides, preform cores for use as substrates in creating optical fiber preforms, capillaries, and planar waveguides and semiconductor structures. Other materials such as diamond and ceramic materials can be used in this invention.  
           [0017]    The above, and other objects, features and advantages of the present invention will become apparent from the following description read in conjunction with the accompanying drawings, (in which like reference numbers in different drawings designate the same elements.)  
       
    
    
     BRIEF DESCRIPTION OF FIGURES  
       [0018]    [0018]FIG. 1—A diagram of a preferred embodiment, as seen from a plane perpendicular to the rod face.  
         [0019]    [0019]FIG. 2—A schematic of a preferred embodiment utilizing only one microwave generator. 
     
    
     DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS  
       [0020]    The main aim of the present invention is to create an effective method for the production of activated optical fiber preforms. This invention is particularly suited for preforms with SiO 2 —F claddings and cores doped with elements such as Al or Ge, or rare earth elements (REE) such as Nd, Er, Ho, Yb, and Eu. The present invention also addresses the need for SiON core lightguides by providing an effective method for manufacturing preforms with SiON cores and SiO 2  or SiO 2 —F claddings, which are useful for ultraviolet applications. The above core and cladding materials are preferred, though are not the only materials available for use with this invention. Other doping materials and optically transmissive materials can be used. This method can also be used for manufacturing doped or undoped silica rods for use as optical fiber preform cores, which can then be used as substrates for the creation of preforms by depositing claddings by any known method. The method can also be used for the production of silica rods and preforms with other compositions and also for the fabrication of ceramic rods.  
         [0021]    In addition, the present invention is useful for creating optical structure planar waveguides and semiconductor structures, and also for the deposition of diamond and other films on planar quartz substrates or other substrates that can be placed on the surface of the rod face.  
         [0022]    The present invention utilizes the simultaneous excitation of an E 01 -wave type and an H wave type with rotating linear polarization. This excitation in conjunction with the introduction of specific gases creates a microwave plasma at a low pressure characterized by a homogeneous microwave power density that is preferably about 220-250 W/cm 2 .  
         [0023]    The present invention possesses a number of significant features absent in the prior art which make the disclosed device and process superior and able to produce preforms with larger diameters and of higher quality with a minimum of microwave power and precursor gas consumption.  
         [0024]    The first significant difference between the present invention and the prior art relates to the simultaneous use of E 01  mode waves and H mode waves with rotating linear polarization. The Beerwald patent teaches the use of a single radiation source to strike a plasma, consisting of either E 01  mode waves or rotationally polarized H mode waves. Either mode alone cannot maintain sufficiently uniform microwave power density in both the plasma discharge and the rod face, and thus cannot produce preforms of a sufficiently high quality. The present invention prescribes the simultaneous application and coupling of E 01  mode waves and rotationally polarized H mode waves from two independent power sources. This configuration results in a significantly greater uniformity in the microwave power density, and thus produces preform rods of superior quality.  
         [0025]    Another difference is in the configuration of the microwave energy source and the gas source in relation to the deposition surface. The Beerwald patent provides for a cylindrical silica starter disc upon which the preform rod is deposited. Microwave energy enters from below the disk along its central cylindrical axis, forming a plasma at the disk face with process gas entering the tube from above the disk face. Prior convention, especially as described in Beerwald, indicates that plasma deposition should take place above the substrate. It has been found, contrary to prior art teachings, that reversing this configuration is beneficial to the deposition process. The present invention does just this, introducing gas below the rod face (i.e. where the rod face, based on gravitational direction, lies above the gas phasing zone), and then depositing and growing the preform in a downward direction. This configuration is capable of producing preforms of higher quality by reducing impurities. The present configuration reduces impurities by eliminating the possibility of particles, such as sootlike Silicon particles, dropping onto the preform face which can occur with the Beerwald configuration. Additionally, because the present invention, in a preferred embodiment, can simultaneously deposit a preform core and cladding, this configuration allows for greater control over the position of precursor gas molecules, and thus helps prevent cross-contamination between core precursor gas and cladding precursor gas.  
         [0026]    A preferred embodiment, illustrated in FIG. 1, consists of the following components:  
         [0027]    a. pulsed microwave generator  101  to emit pulsed E 01  microwaves with a preferred 2450 MHz frequency,  
         [0028]    b. ferrite circulator  102  connected to generator  101  to protect generator  101  from reflected microwave power,  
         [0029]    c. directional coupler  103  connected to generator  101  for measuring the incident and reflected microwave power,  
         [0030]    d. attenuator  104  to smoothly regulate the microwave power emitted by generator  101 ,  
         [0031]    e. phase rotator  105  connected to generator  101  to maintain the microwave plasma position in the area of maximum electric field,  
         [0032]    f. continuous microwave generator  106  which excites continuous H 11  microwaves,  
         [0033]    g. ferrite circulator  107 , directional coupler  108 , attenuator  109  and phase rotator  110  connected to generator  101  which fulfill the same above-mentioned functions as  102 ,  103  and  105 ,  
         [0034]    h. circular metal waveguide  111 ,  
         [0035]    i. silica conical waveguide  112  to couple E 01  and H 11  waves,  
         [0036]    j. rotating silica rod  113  to rotate the linear polarization of H 11  wave (The silica glass deposition process is carried out on the face of rod  113 ),  
         [0037]    k. tube  123 ,  
         [0038]    l. vacuum chamber  115  with connecting pipes  116  for vacuum pumping,  
         [0039]    m. gas supplying system  119 ,  
         [0040]    n. silica inputs of Al and Er vapors  120  and  121 ,  
         [0041]    [0041] 0 . preform  114  grown by vapor deposition according to the present invention,  
         [0042]    p. microwave discharge  117 , temperature sensor  118 , and microwave plasma shift (height) sensor  122 .  
         [0043]    q. rectangular waveguides  124  and  125   
         [0044]    In the preferred embodiment represented in FIG. 1, pulsed microwave generator  101  excites a pulsed E 01  wave with a preferred frequency of 2,450 MHz and preferred power of about 7.5 kW. The E 01  wave is emitted in pulses with a duration of preferably 1 ms and the pulse frequency is in the preferred range of 10-200 Hz. The E 01  wave is delivered to circular waveguide  111  via H 10  mode rectangular waveguide  124 . Circular waveguide  111  has a preferred diameter of 120 mm. The broad wall of H 10  mode rectangular waveguide  124  of generator  101  is perpendicular to the axis of circular waveguide  111 .  
         [0045]    Simultaneously, continuous microwave generator  106  delivers a continuous H 11  wave, with power preferably in the range of 0-5 kW, to circular waveguide  111  via rectangular waveguide  125 . The broad wall of rectangular waveguide  125  is parallel to the central axis of circular waveguide  111 .  
         [0046]    Windows for input of microwaves into waveguide  111  are covered by metal conductors (plates and wires) to remove cross wave influence and to prevent leakage of microwave energy from circular waveguide  111 . The two microwave energy inputs are thus located in one plane. However, “parasite” H 11  wave, which arises under E 01  wave excitation, doesn&#39;t penetrate in the highway of the continuous generator  106  because polarization plane of “parasite” H 11  wave is perpendicular to polarization plane of specially excited continuous H 11  wave. When exciting H 11  wave in the circular waveguide from two orthogonal energy inputs we have polarization (when E 1  ⊥ E 1′ ) which is introduced through conical rod  112 , which is filled in by a dielectric such as quartz, into silica rod  113  (60 mm) acting as a waveguide. In this embodiment, silica rod  113  rotates and thus rotates the linear polarization of the H 11  wave. In order to couple E 01  and H 11  waves in circular waveguide  111  to silica rod  113 , which itself acts as a waveguide in delivering radiation to the rod face, conical waveguide  112  is used. The conical shape minimizes reflection losses as the waves propagate through the interface of waveguide  111 , which has a diameter of 120 mm, and waveguide  112 . Silica glass deposition for formation of preform rod  114  is carried out on the face of rod  113 .  
         [0047]    The combined radiation then enters tube  123 , which is kept at a preferred operating gas pressure of 8-25 torr, through rotating rod  113 . The temperature at the face of rod  113  (located in a plane perpendicular to the cylindrical axis of rod  113  and tube  123 ) is preferably 1200° C. This setup and method for maintaining the microwave plasma results in a uniform and stable plasma at the rod face.  
         [0048]    Each of the two power sources serve different purposes in sustaining the plasma and maintaining a high efficiency. The high pulsed microwave power emitted by generator  101  produces a high degree of gas ionization at relatively low plasma temperatures, and the presence of continuous waves produced by generator  106  heats plasma electrons during pauses between impulses and thus increases the time required for plasma deionization. Because of this combination of pulsed and continuous radiation, more energy can be introduced into the plasma without raising the temperature unacceptably high, and thus a greater percentage of the precursor gas can be excited resulting in greater efficiency. The increase in deionization time by electron heating results because of a rapid decrease in the recombination coefficient of charged particles when the electron temperature increases. The transfer of the microwave energy to electrons leads to excitation, dissociation and ionization of gas molecules through inelastic collisions between electrons and gas molecules. In all cases, the number of collisions per unit time and unit volume increases as the gas pressure and electron concentration N e  (N e =10 13 -10 14 1/cm 3  during pulsed microwave discharge, whereas N e &lt;10 12 1/cm 3  during continuous microwave discharge) increases. Additionally, the operating gas mixtures can be diluted by a small quantity of argon to increase the degree of ionization and the volume (ie. height) of the microwave discharge. Argon is preferred because it is easily ionized. Microwave plasma energy is used to heat the rod face to a desired 1200° C., and heat tube  123  (ceramics or metal foil stabled to the heating) and microwave dielectric (silica tangent of dielectric losses tg increases when the temperature at the rod face achieves 900-1000 C.).  
         [0049]    A stabilization system is used to regulate the microwave power emitted by each source in order to maintain a constant rod face temperature and microwave power density. This system consists of the following units:  
         [0050]    1. Unit of automatic regulation and control of the microwave power produced by each generator.  
         [0051]    2. Directional couplers to measure the incident and reflected microwave power.  
         [0052]    3. Unit to display (indication unit) incident and reflected microwave power values.  
         [0053]    4. The sensors of microwave plasma shift (or height) and temperature together with electrically controlled phase rotators and attenuators in each channel.  
         [0054]    Both generators  101  and  106  are protected respectively by ferrite circulators  102  and  107  from reflected microwave energy. Generators  101  and  106  are also connected to directional couplers  103  and  108  to measure the incident and reflected microwave power, which are in turn connected to attenuators  104  and  109  to smoothly regulate modifications of microwave power. Generators  101  and  106  are also connected to phase rotators  105  and  110  to maintain the position of the microwave plasma within the region of optimal electric field strength. Phase rotators  105  and  110  maintain plasma position by reacting to readings from sensor  122  that detects shifts in the position of the plasma. The temperature of the plasma is measured by temperature sensor  118 , which is connected to attenuator  109 . Attenuator  109  responds to temperature readings and regulates the power output from  106 . In this way, a constant temperature is maintained in the plasma.  
         [0055]    A pressure stabilization system is applied in the plasma-chemical reaction zone for the maintenance of a constant operating gas pressure. The operating gas dosage system provides a supply of the necessary quantity of chemical reagents in designed concentration to every point of the surface of the rotating rod face.  
         [0056]    The present invention is further illustrated by the following examples, but is not limited thereby.  
       EXAMPLE 1  
       [0057]    Production of a Silica Optical Fiber Preform with a SiO 2 —F Cladding and a SiON Core  
         [0058]    Argon gas is first introduced into tube  123 , generating a pressure of 1 torr in tube  123 . Microwave plasma  126  is ignited on the face of rod  113  with radiation from pulsed generator  101 , which delivers 7.5 kW of power in 1 ms pulses at a 100 Hz repetition rate. The pressure is then increased to 3-5 torr and microwave power delivered by continuous generator  106  is smoothly increased to 0.5 kW by attenuator  109 . This process acts to clean the face of rod  113 .  
         [0059]    In the next step, argon is partially removed and oxygen is introduced. The pressure is raised up to 10-15 torr and the power delivered by generator  106  increases the temperature of the plasma, and thus the temperature of the rod face, as high as 1200° C. Gas mixtures for the formation of both an SiO 2 —F cladding and an SiON core are simultaneously introduced into tube  123  through special precursor gas inputs  120  and  121 . In a preferred embodiment, a mixture of O 2 +SiCl 4 +C 3 F 8 +Ar is used for the SiO 2 —F cladding deposition and a mixture of SiCl 4 +O 2 +N 2 +Ar is used for the SiON core deposition. It is to be noted that the N 2 +O 2  flow is always more than twice the SiCl4 flow (by N 2 ) in the core deposition area and core deposition precursor gas mixture.  
         [0060]    An example of detailed process parameters for this method of producing silica optical fiber preforms with SiO 2 —F reflecting cladding and SiON core is as follows.  
                                                       Microwave power (impulse), E 01  wave, kW   7.5           Impulse duration, ms   1.0           Impulse repetition rates, Hz   100           Microwave power (continuous), H 11  wave   0-4.5           with rotating polarization, kW           Operating gas pressure, torr   12           Mutual operating gas flow, cm 3 /min   9200           N 2  flow for core formation, cm 3 /min   1500           SiCl 4  flow (by N 2 ) for core formation, cm 3 /min   800           O 2  flow for core formation, cm 3 /min   350           Ar flow for core formation, cm 3 /min   100           O 2  flow for cladding formation, cm 3 /min   5000           SiCl 4  flow for cladding formation, cm 3 /min   1250           C 3 F 8  flow for cladding formation, cm 3 /min   100           Ar flow for cladding formation, cm 3 /min   100           Silica rod diameter, mm   60           Rod face temperature, C.   1200           Rate of rod rotation, rev/min   100                      
 
         [0061]    The deposition rate of the SiO2—F/SiON preform is 2.5 g/min. A preform with a 60 mm diameter, a 210 mm length, and a weight of over 2 kg is fabricated by deposition in 14 hours.  
       EXAMPLE 2  
       [0062]    Production of a Preform with Cladding and Al and Er Doped Core  
         [0063]    With the present invention, a preform can be manufactured that features a core whose refractive index is radially variable. The produced reflective cladding consists of fluorine-doped silica and the core consists of silica doped with aluminum and erbium. A gas mixture consisting of O 2 +SiCl 4 +C 3 F 8 +ErCl 3 (waterless vapor)+AlCl 3 (waterless vapor) is supplied to the microwave plasma zone via gas supply system 119. AlCl 3  and ErCl 3  vapors are supplied to the plasma from the closed silica containers 120 and 121, (with ErCl 3  and AlCl 3  powders) which are located under the microwave plasma at the 900° C. temperature zone in the graphite tube  123 . Condensation of ErCl 3  and AlCl 3  in the reaction zone during vapor transportation is avoided because the temperature increases around the supplying vapors in the plasma zone. The activator flow is determined by pressure difference of ErCl 3  and AlCl 3  saturated vapors into containers  120  and  121  and the pressure in the graphite tube and also by resistance of capillaries connecting these two volumes.  
         [0064]    The doping level is modified by changing the temperature of containers  120  and  121 . The temperature of these containers can be changed by changing the container positions with respect to the microwave plasma. The containers are removed from high temperature zone to completely stop supplying ErCl 3  and AlCl 3  vapors to the plasma. In this case saturated vapor pressure decreases and the ErCl 3 , AlCl 3  vapor supply ceases.  
         [0065]    Simultaneous preform core doping with Er and Al by this method can be used for the production of the active part of optical fiber lasers and amplifiers.  
         [0066]    The present invention provides the ability to produce preforms with a wide variety of diameters. For example, a preform with a diameter between 25-30 mm and 80 mm using a 2450 MHz generator frequency and waveguide  111  diameter of 120 mm. To produce preforms in this diameter range, the dielectric permeability of conical waveguide  112  is between 2-2.5 (polystirol, flouroplast) to 20-25 (special ceramic). The deposition rate of doped silica glass can be achieved up to 2.5-3 g/min.  
         [0067]    Suggested detailed process parameters for this method for manufacturing a silica activated optical fiber preform with SiO 2 —F reflecting cladding and core doped by Er and Al are as follows.  
                                                       Microwave power (impulse), E 01  wave, kW   7.5           Impulse duration, ms   1.0           Impulse repetition rates, Hz   100           Microwave power (continuous), H 11  wave   0-4.5           with rotating polarization, kW           Operating gas pressure, torr   12           Mutual gas flow, cm 3 /min   9500           O 2  flow for cladding formation, cm 3 /min   6000           SiCl 4  flow for cladding formation, cm 3 /min   1300           C 3 F 8  flow for cladding formation, cm 3 /min   100           Ar flow for cladding formation, cm 3 /min   100           O 2  flow for core formation, cm 3 /min   1500           SiCl 4  flow for core formation, cm 3 /min   300           AlCl 3  flow for core formation, cm 3 /min   50           ErCl 3  flow for core formation, cm 3 /min   50           Ar flow for core formation, cm 3 /min   100           Silica container (with AlCl 3 , ErCl 3 ) temperature, C.   900           Silica rod diameter, mm   60           Rod face temperature, C.   1200           Rate of rod rotation, rev/min   100                      
 
         [0068]    The deposition rate of doping silica glass (cladding and core) is 2.5 g/min. The preform (60 mm diameter, 210 mm length, more than 2 kg weight) for activated lightguides is produced after 14 hours of continuous deposition.  
       EXAMPLE 3  
       [0069]    Preform Manufacture without Pulsed Generator  106   
         [0070]    This alternative embodiment of the present invention presents a simpler device scheme for manufacturing activated optical fiber preforms, SiON core preforms, SiO 2  rods doped by nitrogen and SiO 2  rods doped by Al (Ge) and different types of REE (Er and so on). In this case the microwave power density on the rod face and in the microwave plasma will be lower (150-160 W/cm 2 ) then in those embodiments that include a pulsed microwave generator. The deposition rate is approximately 1-1.5 g/min in this case. A diagram of this installation is shown in FIG. 2.  
         [0071]    Continuous microwave generator  201  emits radiation at preferably 2450 MHz and 6 kW through ferrite circulator  202 , which “protects” generator  201  from reflected microwave power, to power divider  203  which divides this power into two equal parts for 2 microwave energy channels which are divided by the ferrite circulators  204  and  208 . The excitation process of E 01  and H 11  wave with revolving polarization is performed by the same manner and consistency as in the previous embodiments (FIG. 1). E 01  and H 11  waves with 1 kW power are excited by attenuators  206  and  210 . The microwave discharge is then ignited by argon and the rod face is cleaned. Next, argon is partially substituted by oxygen. The operating pressure increases up to 6-10 torr and the microwave power of E 01  wave smoothly increases up to 2-2.5 kW. To provide the 1200 C. microwave plasma temperature the power of H 11    1  wave should be increased to the proper corresponding value by attenuator  210 . The remaining stages of the process are completed as described in previous embodiments. Phase rotators  207  and  211  have the same functions as in previous embodiments. Directional couplers  205  and  209  serve to control incident and reflected microwave power. The remaining components of the device, including the circular waveguide, conical waveguide, tube, rotating rod, vacuum chamber and gas supply systems are represented by  212 .  
         [0072]    Examples of technological process parameters for manufacturing of activated optical fiber preforms and SiON core preforms are given below. Technological regimes of production of different silica rods for optical fiber preforms (fabricated by installations presented on FIG. 1, 2) are also given. These examples are not exhaustive, and in no way limit the present invention.  
         [0073]    The remaining examples list possible operation parameters for the manufacture of different preform types.  
       EXAMPLE 4  
       [0074]    The Method for Production of an SiON Rod for Use in Subsequent Manufacture of an Optical Fiber Preform  
                                                       Microwave power (impulse), E 01  wave, kW   7.5           Impulse duration, ms   1.0           Impulse repetition rates, Hz   100           Microwave power (continuous), H 11  wave   0-4.5           with rotating polarization, kW           Gas pressure, torr   15           Mutual gas flow, cm 3 /min   12000           N 2  flow, cm 3 /min   6500           O 2  flow, cm 3 /min   1500           SiCl 4  flow, cm 3 /min   3800           Ar flow, cm 3 /min   200           Silica rod diameter, mm   60           Rod face temperature, C.   1200           Rate of rod rotation, rev/min   100                      
 
         [0075]    The deposition rate of SiON glass is 3 g/min. SiON rod (60 mm diameter, 210 mm length, more than 2 kg weight) is fabricated for 12 hours of continuous deposition process.  
       EXAMPLE 5  
       [0076]    The Method for Production of an SiO 2 —GeO 2  Rod  
                                                       Microwave power (continuous), E 01  wave, kW   0-2.5           Microwave power (continuous), H 11  wave   0-2.5           Operating gas pressure, torr     8           Mutual gas flow, cm 3 /min   6320           O 2  flow, cm 3 /min   4800           SiCl 4  flow, cm 3 /min   1200           GeCl 4  flow, cm 3 /min    120           Ar flow, cm 3 /min    200           Silica rod diameter, mm    60           Rod face temperature, C.   1000           Rate of rod rotation, rev/min    100                      
 
         [0077]    The deposition rate of glass is 1.4 g/min.  
       EXAMPLE 6  
       [0078]    The Method for Manufacturing of Silica Rod (Particular Purity)  
                                                       Microwave power (continuous), E 01  wave, kW   0-2.5           Microwave power (continuous), H 11  wave   0-2.5           with rotating polarization, kW           Operating gas pressure, torr     8           Mutual gas flow, cm 3 /min   6750           SiCl 4  flow, cm 3 /min   1300           O 2  flow, cm 3 /min   5250           Ar flow for cladding formation, cm 3 /min    200           Silica rod diameter, mm    60           Rod face temperature, C.   1200           Rate of rod rotation, rev/min    100                      
 
         [0079]    The deposition rate of glass is 1.4 g/min.  
       EXAMPLE 7  
       [0080]    The Method for Production of Silica Rod Doped by Al and Er  
                                                       Microwave power (continuous), E 01  wave, kW   0-2.5           Microwave power (continuous), H 11  wave   0-2.5           with rotating polarization, kW           Operating gas pressure, torr     8           Mutual gas flow, cm 3 /min   6100           O 2  flow, cm 3 /min   4600           SiCl 4  flow, cm 3 /min   1100           AlCl 3  flow, cm 3 /min    100           ErCl 3  flow, cm 3 /min    100           Ar flow, cm 3 /min    200           Silica rod diameter, mm    60           Rod face temperature, C.   1200           Rate of rod rotation, rev/min    100                      
 
         [0081]    The deposition rate of doped silica glass is 1.2 g/min.  
         [0082]    Having described preferred embodiments of the invention with reference to the accompanying drawings, it is to be understood that the invention is not limited to the precise embodiments, and that various changes and modifications may be effected therein by those skilled in the art without departing from the scope or spirit of the invention as defined in the appended claims.