Abstract:
The present invention relates to a method of synthesizing glycidyl ether compounds without the addition of solvent. In particular, the present invention provides the improved preparation of the glycidyl ethers by using fatty alcohols with epichlorohydrin in the presence of alkali metal hydroxide and phase-transfer catalysts in the appropriate molar ratios of them without water and organic solvents.

Description:
BACKGROUND OF THE INVENTION  
         [0001]    1.Field of the Invention  
           [0002]    The present invention relates to a method of synthesizing glycidyl ether compounds without the addition of solvent. In particular, the present invention provides the improved preparation of the glycidyl ether by using fatty alcohol with epichlorohydrin in the presence of alkali metal hydroxide and phase-transfer catalyst in an appropriate molar ratio of them without water and organic solvents.  
           [0003]    Therefore, the synthetic method of glycidyl ether compounds according to this invention has the following advantages:  
           [0004]    First, the direct merits due to using a solid base are as follows; i) the degree of the corrosion of a reactor can be reduced owing to the non-use of aqueous basic solution, ii) an additional device for preparing an aqueous basic solution is not required since a solid form of base is directly added to the reactor containing other reactants, iii) since the by-products such as sodium hydroxide and sodium chloride can be easily separated into a solid form, they can be handled conveniently, i.e., delivery, storage and separation, and iv) additional devices for solidifying and neutralization processes of by-products are not necessary since solid by-products such as sodium hydroxide and sodium chloride are produced by this method.  
           [0005]    Second, more amounts of reactants can be added to the reactor because of non-use of any solvent in this method. Thus, better productivity per unit size of the reactor can be ensured.  
           [0006]    Third, the generally-available, low-priced phase-transfer catalysts are used in the reaction.  
           [0007]    Fourth, the amounts of reactants such as alkali metal hydroxide and epichlorohydrin used in this method can be reduced in comparison with those in the conventional methods.  
           [0008]    Fifth, this method gives much higher yield than those of the conventional methods for glycidyl ether compounds.  
           [0009]    Therefore, the method of the present invention is suitable for the commercial mass-production.  
           [0010]    2. Description of the Prior Art  
           [0011]    The glycidyl ether compounds are very important intermediates in physical and phamaceutical applications such as preparing softner, antistatic agent, pseudo-ceramide, emulsifier and surface treatment agent.  
           [0012]    There are two typical conventional methods for preparing glycidyl ether compounds. The first method is to react fatty alcohol with epichlorohydrin in the presence of Lewis acid, as shown in the following scheme 1,  
                         
 
           [0013]    wherein R represents an alkyl group.  
           [0014]    The reaction step (a) is performed in the presence of Lewis acid such as sulfuric acid, perchloric acid and trifluoroborane. Further, the reaction step 20 (b) is performed with basic solution in an anhydrous organic solvent.  
           [0015]    However, the reaction of alcohol with epichlorohydrin in the presence of Lewis acid has some disadvantages, i.e., the formation of halohydrin ether and polymerization of compounds in the reaction system. Also, other reaction vessels should be required because of the two-step reactions. For these reasons, the second conventional method, the reaction of fatty alcohol with epichlorohydrin using aqueous sodium hydroxide solution and non-polar solvent such as hexane including phase-transfer catalysts, is more useful than the reaction mentioned above for the preparation of glycidyl ether, as shown in the following scheme 2,  
                         
 
           [0016]    wherein R represents an alkyl group.  
           [0017]    Recently, M. E. Borredon has reported that the yields for various glycidyl ethers through the reaction of alcohol/epichlorohydrin/base (the molar ratio of 1/2/3) in the presence of aqueous basic solution and hexane are between 39 and 76%. [ Syn. Comm.,  24: 3021 (1994)].  
           [0018]    Further, K. Urata has reported that through the reaction of alcohol/epichlorohydrin/base (the molar ratio of 1/2/3) in the presence of basic solution, hexane and phase-transfer catalyst, the glycidylether compound of 72-86% can be obtained [ J. Am. Oil. Chem. Soc.,  65:1299(1988)].  
           [0019]    The conventional one-step synthesis, Scheme 2, has faced several shortcomings in that since 3.5 fold-amount of solvent compared to the composition of base and other reactants, should be necessarily added, the reaction is performed in the two phases; water phase and organic phase. Thus the main problem lies in handling the basic solution in an appropriate manner in terms of the following disadvantages: i) the corrosion of reactor should be settled, ii) separate reactor for preparing the basic solution is necessary, iii) the by-products in a liquid form cannot be easily handled due to more inconvenient delivery and storage, iv) additional reaction process is necessary for neutralizing the basic solution and solidifying the by-products, and v) the amounts of reactants such as epichlorohydrin (more than 2 mol) and base (more than 3 mol) should be excessively employed. Thus, the conventional one-step synthesis according to the scheme 2 has been uneconomical in terms of commercial production method.  
         SUMMARY OF THE INVENTION  
         [0020]    To comply with these drawbacks that the conventional invention has faced, the inventor et al. have made intensive studies and as a result, noted that the glycidyl ether compounds with a very high yield can be prepared by the reaction of alcohol, epichlorohydrin, alkali metal hydroxide and phase-transfer catalyst in an appropriate molar ratios of them without addition of solvent and aqueous basic solution, thus significantly improving several problems of the conventional method. In consequence the inventor et al. have consummated this invention.  
           [0021]    Therefore, the manufacturing method of glycidyl ether compounds according to this invention has the following advantages:  
           [0022]    First, the direct merits due to using a solid base are as follows; i) the degree of the corrosion of a reactor can be reduced owing to the non-use of aqueous basic solution, ii) an additional device for preparing an aqueous basic solution is not required since a solid form of base is directly added to the reactor containing other reactants, iii) since the by-products such as sodium hydroxide and sodium chloride can be easily separated into a solid form, they can be handled conveniently, i.e., delivery, storage and separation, and iv) additional devices for solidifying and neutralization processes of by-products are not necessary since solid by-products such as sodium hydroxide and sodium chloride are produced by this method.  
           [0023]    Second, more amounts of reactants used can be added to the reactor because of non-use of any solvents in this method. Thus, better productivity per unit size of the reactor can be ensured.  
           [0024]    Third, the generally-available, low-priced phase-transfer catalysts are used in the reaction.  
           [0025]    Fourth, the amounts of reactants such as alkali metal hydroxide and epichlorohydrin used in this method can be reduced in comparison with those in the conventional methods.  
           [0026]    Fifth, this method gives much higher yield than those of the conventional methods for glycidyl ether compounds.  
         DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS  
         [0027]    The present invention is characterized by a method of synthesizing glycidyl ether compound via the reaction with fatty alcohol, epichlorohydrin, alkali metal hydroxide and amine- or ammonium-based phase-transfer catalyst in the absence of water and organic solvents.  
           [0028]    The present invention is described in more detail as set forth hereunder.  
           [0029]    The conventional method requires aqueous basic solutions so as to form alkoxide in the reaction of alcohol with epichlorohydrin and it has to be performed in non-polar solvent to avoid any side-reaction of base with other reactants. For more smooth reaction, a phase-transfer catalyst is usually employed in two-phase reaction between aqueous and organic phase. However, even with the addition of a phase-transfer catalyst such as tetrabutylammonium bromide in the conventional method, a variety of drawbacks is being raised: long reaction time, low yield of 72-86%, excessive use of other reactants such as epichlorohydrin and sodium hydroxide to alcohol, especially demerits associated with the use of aqueous basic solution and low productivity due to less use of reactants compared to the size of the reactor in the presence of solvent.  
           [0030]    In contrast, according to the manufacturing process of the present invention, the reaction can be smoothly performed in a manner such that a phase-transfer catalyst selected from amine- and ammonium-based compounds is employed in an appropriate molar ratio, together with solid alkali metal hydroxide. Based upon this, various problems associated with the use of aqueous basic solution can be avoided.  
           [0031]    The method for manufacturing glycidyl ether compounds according to this invention is explained in more detail as set forth hereunder.  
           [0032]    The alcohols used for this invention are a primary, secondary or tertiary alcohol compound with alkyl group containing saturated alkyl group with hydrocarbon chain or fluorocarbon chain, unsaturated alkyl group or aromatics.  
           [0033]    The amount of epichlorohydrin, which is concurrently used with alcohol according to this invention, may vary depending upon the kinds of glycidyl ether compounds, a desired product. For example, the glycidyl ether compound, expressed by the following formula 1a, is prepared under the conditions that 0.8-4 mol of epichlorohydrin is added to 1 mol of alcohol, while 1,3-dialkyloxy-2-propanol, expressed by the following formula 1b, is prepared under the conditions that 0.12-0.7 mol of epichlorohydrin is added to 1 mol of alcohol. These molar ratios are preferred to achieve better reaction yield.  
                         
 
           [0034]    Wherein R 1  and R 2  represent independently an alkyl group containing saturated alkyl group with hydrocarbon chain or fluorocarbon chain, unsaturated alkyl group or aromatics.  
           [0035]    According to this invention, the basic compounds used for this invention are solid alkali metal compounds, preferably alkali metal hydroxide such as sodium hydroxide and potassium hydroxide. The preferred molar ratio of base is in the range of 0.12-4 to alcohol. More specifically, the glycidyl ether compound expressed by the formula 1a is prepared in the molar ratios of 0.8-4 to alcohol, while 1,3-dialkyloxy-2-propanol expressed by the formula 1b is prepared in the molar ratios of 0.2-4 to alcohol.  
           [0036]    Further, according to this invention, the examples of phase-transfer catalysts include amine- and ammonium-based compounds. It is preferred that the phase-transfer catalyst is employed in the molar ratios of 0.0005-0.1 to alcohol. The typical examples of the phase-transfer catalysts include trialkylamine, alkyldimethylbenzylammonium salt, tetraalkylammonium salt, N,N-dialkylamino-3-alkyloxy-2-propanol, N,N,N-trialkyl-3-alkyloxy-2-hydroxypropylammonium salt and alkyltrimethylammonium salt; hence, the anionic part of salt is selected from the group consisting of halide, methylsulfate and hydrogensulfate. The detailed examples of the phase-transfer catalysts include the following compounds, but other amine- or ammonium-based compounds may achieve the same effect, since these phase-transfer catalysts are nothing but the ones to exemplify this invention in more detail: tetrabutylammonium bromide, tetrabutylammonium hydrogensulfate, cetyltrimethylammonium chloride, lauryldimethylbenzylammonium chloride, N,N-dimethylamino-3-hexyloxy-2-propanol, N,N-dimethylamino-3-octyloxy-2-propanol, N,N-dimethylamino-3-dodecyloxy-2-propanol, N,N-dimethylamino-3-octadecyloxy-2-propanol, N,N-dimethylamino-3-(1′H,1′H,2′H,2′H-perfluoro)hexyloxy-2-propanol, N,N-dimethylamino-3-(1′H,1′H,2′H,2′H-perfluoro)octyloxy-2-propanol, N,N-bis(2-hydroxyethyl)amino-3-hexyloxy-2-propanol, N,N-bis(2-hydroxyethyl)amino-3-octyloxy-2-propanol, N,N-bis(2-hydroxethyl)amino-3-dodecyloxy-2-propanol, N,N-bis(2-hydroxyethyl)amino-3-octadecyloxy-2-propanol, N,N-bis(2-hydroxyethyl) amino-3-1′H,1′H,2′H,2′H-perfluoro)hexyloxy-2-propa nol, N,N-bis(2-hydroxyethyl)amino-3-(1′H,1′H,2′H,2′H-perfluoro)octyloxy-2-propa nol, N,N,N-trimethyl-3-hexyloxy-2-hydroxypropylammonium methylsulfate, N,N,N-trimethyl-3-octyloxy-2-hydroxypropylammonium methylsulfate, N,N,N-trimethyl-3-dodecyloxy-2-hydroxypropylammonium methylsulfate, N,N,N-trimethyl-3-octadecyloxy-2-hydroxypropylammonium methylsulfate, N,N,N-trimethyl-3-(1′H,1′H,2′H,2′H-perfluoro)hexyloxy-2-hydroxypropylamm onium methylsulfate, N,N,N-trimethyl-3-(1′H,1′H,2′H,2′H-perfluoro)octyloxy-2-hydroxypropylamm onium methylsulfate, N,N,N-trimethyl-3-octyloxy-2-hydroxypropylammonium chloride, N,N,N-trimethyl-3-octyloxy-2-hydroxypropylammonium bromide, N,N-bis(2-hydroxyethyl)-N-methyl-3-hexyloxy-2-hydroxypropylammonium methylsulfate, N,N-bis(2-hydroxyethyl)-N-methyl-3-octyloxy-2-hydroxypropylammonium methylsulfate, N,N-bis(2-hydroxyethyl)-N-methyl-3-dodecyloxy-2-hydroxypropylammonium methylsulfate, N,N-bis (2-hydroxyethyl)-N-methyl-3-octadecyloxy-2-hydroxypropylammoniu m methylsulfate, N,N-bis(2-hydroxyethyl)-N-methyl-3-(1′H,1′H,2′H,2′H-perfluoro)hexyloxy-2-hydroxypropylammonium methylsulfate, N,N-bis(2-hydroxyethyl)-N-methyl-3-(1′H,1′H,2′H,2′H-perfluoro)octyloxy-2-hydroxypropylammonium methylsulfate, and an esterified compound of octanoic acid and N,N-dimethyl-3-octyloxy-2-propanol, and an esterified compound of hexadecanoic acid and N,N-dimethyl-3-octyloxy-2-propanol.  
           [0037]    Further, the reaction of this invention is performed under the atmospheric pressure at 10-100° C.  
           [0038]    Further, after the reaction of this invention is completed, some by-products such as sodium chloride and sodium hydroxide present in the reaction mixtures are filtered off. Then, the un-reacted epichlorohydrin is reused through recovery process such as distillation. The desired glycidyl ether product can be isolated and purified through a simple filtration process. Other separation process for glycidyl ether is that after the reaction mixture is dissolved in appropriate solvents such as hexane, cyclohexane, heptane, toluene, diethyl ether and dialkyl ether, the desired glycidyl ether product can be separated and purified through filtration and distillation processes.  
           [0039]    This invention herein is explained in more detail based on the following Examples without limitations thereby. 
       
    
    
     EXAMPLE  
       [0040]    Octanol (132 g, 1 mol) was added to a round-bottomed four-neck flask equipped with an agitator, reflux condenser and thermometer at 30° C. Tetrabutylammonium bromide (16.1 g, 0.050 mol) and sodium hydroxide (61.9 g, 1.5 mol) were further added to the flask and stirred, and then, epichlorohydrin (140.1 g, 1.5 mol) was added dropwise for 10 minutes. After the mixture was stirred for 3 hours at the same temperature, by-products such as sodium chloride and sodium hydroxide were filtered off. The unreacted epichlorohydrin was reused via recovery process such as distillation. Then, glycidyl ether compound as the desired product was obtained by a simple filtration.  
         [0041]    The following Table 1 shows the yield of octyl glycidyl ether using each base (1.5 mol) of sodium hydroxide and potassium hydroxide from the above Example.  
                           TABLE 1                                   Base   Yield                           Sodium hydroxide   90%           Potassium hydroxide   90%                      
 
         [0042]    The following Table 2 shows the names and yields of glycidyl ether compounds when various alcohols and their amounts from the above Example were employed.  
                                                   TABLE 2                           Alcohols                    Amount               (Molar               ratio a) /           molar   Desired product            Kinds   ratio b)     Name of product   Yield               Octanol   1.5/1.5   Octyl glycidyl ether   90%           0.47/1.1   1,3-dioctyloxy-2-propanol   90%       Mixed fatty   1.5/1.5   Alkyl glycidyl ether   90%       alcohol 1)         (alkyl = octyl or decyl)           0.47/1.1   1,3-dialkyloxy-2-propanol   90%               (alkyl = octyl or decyl)       1H,1H,2H,2H-   1.5/1.5   Alkyl glycidyl ether   90%       perfluoro-       (alkyl = 1′H,1′H,2′H,2′H-perfluoro       hexyl-1-ol       hexyl)           0.47/1.1   1,3-dialkyloxy-2-propanol   90%               (alkyl = 1′H,1′H,               2′H,2′H-perfluoro hexyl)       Mixed   1.5/1.5   Alkyl glycidyl ether   90%       perfluoroalcohol 2)         (alkyl = 1′H,1′H,2′H,2′H-perfluoro-               hexyl) or               alkyl = 1′H,1′H,2′H,2′H-perfluoro-               octyl)           0.47/1.1   1,3-dialkyloxy-2-propanol   90%               (alkyl = 1′H,1′H,2′H,2′H-perfluoro-               hexyl) or               alkyl = 1′H,1′H,2′H,2′H-perfluoro-               octyl)       2-Ethyl-1-hexanol   1.5/1.5   Alkyl glycidyl ether   90%               (Alkyl = 2′-ethyl-1′-hexyl)       Oleyl alcohol   1.5/1.5   Alkyl glycidyl ether   90%               (Alkyl = oleyl)       2-Octanol   1.5/1.5   Alkyl glycidyl ether   90%               (Alkyl = 2′-octyl)       Nonylphenol   1.5/1.5   Alkyl glycidyl ether   90%               (Alkyl = nonylphenyl)                                                  
 
         [0043]    From the Example, the reactions were performed using 0.05 mol of a phase-transfer catalyst selected from amine- and ammonium-based compounds and their results were shown in the following Tables 3a and 3b.  
                   TABLE 3a                           Yield of           glycidyl           ether       Phase-transfer catalyst   (%)                   Tetrabutylammonium bromide   90%       Tetrabutylammonium hydrogensulfate   90%       Cetyltrimethylammonium chloride   90%       Lauryldimethylbenzylammonium chloride   90%       N,N-dimethylamino-3-hexyloxy-2-propanol   90%       N,N-dimethylamino-3-octyloxy-2-propanol   90%       N,N-dimethylamino-3-dodecyloxy-2-propanol   90%       N,N-dimethylamino-3-octadecyloxy-2-propanol   90%       N,N-dimethylamino-3-(1′H,1′H,2′H,2′H-   90%       perfluoro)hexyloxy-2-propanol       N,N-dimethylamino-3-(1′H,1′H,2′H,2′H-perfluoro)octyloxy-   90%       2-propanol       N,N-bis(2-hydroxyethyl)amino-3-hexyloxy-2-popanol   90%       N,N-bis(2-hydroxyethyl)amino-3-octyloxy-2-propanol   90%       N,N-bis(2-hydroxyethyl)amino-3-dodecyloxy-2-propanol   90%       N,N-bis(2-hydroxyethyl)amino-3-octadecyloxy-2-propanol   90%       N,N-bis(2-hydroxyethyl)amino-3-(1′H,1′H,2′H,2′H-per-   90%       fluoro)hexyloxy-2-propanol       N,N-bis(2-hydroxyethyl)amino-3-(1′H,1′H,2′H,2′H-per-   90%       fluoro)octyloxy-2-propanol                  
 
         [0044]    [0044]                   TABLE 3b                           Yield           of glycidyl       Phase-transfer catalyst   ether (%)                   N,N,N-trimethyl-3-hexyloxy-2-hydroxypropylammonium   90%       methylsulfate       N,N,N-trimethyl-3-octyloxy-2-hydroxypropylammonium   90%       methylsulfate       N,N,N-trimethyl-3-octyloxy-2-hydroxypropylammonium   90%       chloride       N,N,N-trimethyl-3-octyloxy-2-hydroxypropylammonium   90%       bromide       N,N,N-trimethyl-3-dodecyloxy-2-hydroxypropyl-   90%       ammonium methylsulfate       N,N,N-trimethyl-3-octadecyloxy-2-hydroxypropyl-   90%       ammonium methylsulfate       N,N,N-trimethyl-3-(1′H,1′H,2′H,2′H-perfluoro)hexyl-   90%       oxy-2-hydroxypropylammonium methylsulfate       N,N,N-trimethyl-3-(1′H,1′H,2′H,2′H-perfluoro)octyl-   90%       oxy-2-hydroxypropylammonium methylsulfate       N,N-bis(2-hydroxyethyl)-N-methyl-3-hexyloxy-2-hy-   90%       droxypropylammonium methylsulfate       N,N-bis(2-hydroxyethyl)-N-methyl-3-octyloxy-2-hy-   90%       droxypropylammonium methylsulfate       N,N-bis(2-hydroxyethyl)-N-methyl-3-dodecyloxy-2-   90%       hydroxypropylammonium methylsulfate       N,N-bis(2-hydroxyethyl)-N-methyl-3-octadecyloxy-2-   90%       hydroxypropylammonium methylsulfate       N,N-bis(2-hydroxyethyl)-N-methyl-3-(1′H,1′H,2′H,2′H-   90%       perfluoro)hexyloxy-2-hydroxypropylammonium       methylsulfate       N,N-bis(2-hydroxyethyl)-N-methyl-3-(1′H,1′H,2′H,2′H-   90%       perfluoro)octyloxy-2-hydroxypropylammonium       methylsulfate       An esterified compound of   90%       N,N-dimethyl-3-octyloxy-2-propanol and octanoic acid       An esterified compound of   90%       N,N-dimethyl-3-octyloxy-2-propanol and hexadecanoic       acid                    
         [0045]    As described above, this invention is to provide a method for the synthesis of glycidyl ether compound smoothly in the absence of water and organic solvents and to apply effectively to the industrial production of glycidyl ether compounds in a very high productivity.