Abstract:
An optical fiber preform comprising a plurality of longitudinal air holes is subjected to a thermal treatment (i.e., heating), coupled with the application of a compressive force on either end of the heated preform to compress the entire preform structure a predetermined amount. The thermal compression treatment has been found to smooth any roughened glass surfaces and heal microcracks that may have formed during the preform fabrication process, essentially “knitting” the glass material back together and forming a preform of improved quality over the prior art microstructured preforms.

Description:
CROSS-REFERENCE TO RELATED APPLICATIONS 
       [0001]    This application is divisional of U.S. application Ser. No. 11/644,621, filed Dec. 22, 2006 and issued a Notice of Allowance on Jul. 26, 2010. 
     
    
     TECHNICAL FIELD 
       [0002]    The present invention relates to an improved quality optical fiber preform and, more particularly, to a microstructured preform formed using a thermal compression technique to improve the quality of the air/glass interfaces within the microstructured configuration. 
       BACKGROUND OF THE INVENTION 
       [0003]    Several types of optical fibers require the formation of longitudinal air holes within the preform from which the fiber is ultimately drawn. For example, microstructured optical fibers are formed from preforms that include longitudinally disposed air holes. Polarization-maintaining optical fiber preforms include longitudinal holes that are subsequently filled with stress rods to control the propagating polarization state in the drawn fiber. These longitudinal holes may be formed in optical fiber preforms through a variety of conventional techniques including, but not limited to, drilling, piercing, casting or extruding. 
         [0004]    The quality of the air/glass interfaces within optical fiber preforms including longitudinal holes is often problematic due to surface roughness, where the roughness may be a result of several different sources. For example, the glass surface may be damaged from a machining process used to drill the longitudinal holes, the nascent surface from molds and rods used in casting, or damage from de-molding operations associated with conventional Sol-gel casting. 
         [0005]    Regardless of the source of the roughness, the roughness and associated microcracks have been found to attribute to increased signal loss in the drawn optical fiber. In particular, the presence of roughness and microcracks within a microstructured optical fiber (or any fiber including longitudinally disposed components, such as glass rods) leads to loss associated with optical signal scattering and non-uniform hole size in the drawn fiber. Further, if the preform is etched in a hydrofluoric (HF) solution (a conventional processing step), the presence of the etchant will allow for propagation of the already-present microcracks. Pressurization of the preform during draw will also allow for the microcracks to propagate. If the microcrack presence is severe enough, the internal air holes will connect, destroying the fiber geometry and limiting the ability to form fibers with relatively large air/fill fraction configurations (e.g., &gt;50%). 
         [0006]    With respect to polarization-maintaining optical fiber, surface roughness has been found to contribute to the formation of bubbles and distortion of the stress rods, both of which degrade the polarization cross-talk parameter. In stretching preforms made with drilled and polished holes, the surface defects become extended in length, resulting in a defect known as “fiber air lines”, which degrade the ability to perform fusion splices within the drawn fiber. 
         [0007]    In light of all of the above, a need remains in the art for an optical fiber preform well-suited for configurations including longitudinal air holes, such as microstructured fiber preforms or polarization-maintaining optical fiber preforms. 
       SUMMARY OF THE INVENTION 
       [0008]    The need remaining in the prior art is addressed by the present invention, which relates to an improved quality optical fiber preform and, more particularly, to a microstructured preform formed using a thermal compression treatment, prior to drawing the fiber, to improve the quality of the air/glass interfaces within the microstructured configuration. 
         [0009]    In accordance with the present invention, an optical fiber preform comprising a plurality of longitudinal air holes is subjected to a thermal treatment (i.e., heating), coupled with the application of a compressive force on either end of the heated preform to compress the entire preform structure a predetermined amount. Following the compression, the preform may be stretched and then, ultimately, drawn into fiber. The thermal treatment has been found to smooth any roughened glass surfaces and heal microcracks that may have formed during the preform fabrication process, essentially “knitting” the glass material back together and forming a preform of improved quality over the prior art microstructured preforms. 
         [0010]    In one embodiment of the invention, a positive or negative air pressure may be forced (blown) through the longitudinal air holes during the thermal treatment to either increase or decrease the diameter of the air holes running along the longitudinal extent of the preform. 
         [0011]    Other and further embodiments and features of the invention will become apparent during the course of the following discussion and by reference to the accompanying drawings. 
     
    
     
       BRIEF DESCRIPTION OF THE DRAWINGS 
         [0012]    Referring now to the drawings, 
           [0013]      FIG. 1  is an isometric view, and  FIG. 2  a cut-away top view, of an exemplary fiber preform including a plurality of longitudinal air holes that may be subject to rough surfaces and the formation of microcracks during preform fabrication; 
           [0014]      FIG. 3  contains a side view of a conventional prior art microstructured optical preform, with  FIG. 3(   a ) illustrating the preform prior to performing a preform stretching operation and  FIG. 3(   b ) illustrating the preform after the preform stretching operation; 
           [0015]      FIGS. 4-6  illustrate an exemplary process of the present invention for thermally treating a preform to reduce rough surfaces and microcracks; 
           [0016]      FIG. 7  contains a side view of a microstructured optical preform, with  FIG. 7(   a ) illustrating the preform prior to the inventive thermal treatment, and  FIG. 7(   b ) illustrating the preform subsequent to the inventive thermal treatment; 
           [0017]      FIG. 8  illustrates a comparison of microstructured preforms subjected to an etch in hydrofluoric acid, with  FIG. 8(   a ) illustrating a conventional, prior art preform and  FIG. 8(   b ) illustrating a preform formed in accordance with the present invention; 
           [0018]      FIG. 9  illustrates cross-sectional images of microstructured preforms having a relatively large air/fill fraction, formed in accordance with the present invention; and 
           [0019]      FIG. 10  is a graph of hole size as a function of preform diameter, illustrating the change in air hole size as a function of preform diameter. 
       
    
    
     DETAILED DESCRIPTION 
       [0020]      FIG. 1  illustrates, in an isometric view, a typical microstructured prior art optical fiber preform  10 . A cut-away top view of preform  10  is shown in  FIG. 2 . Microstructured preform  10  includes an inner region  12  and an outer region  14 . Inner region  12  is formed of a suitable optic fiber material (such as, for example, silica) and includes a plurality of longitudinal air holes  18 . The particular arrangement of  FIG. 1  also includes a hollow core region  20 . For embodiments where optical preform  10  is utilized to fabricate polarization-maintaining fiber, inner region  12  may further comprise a plurality of glass rods  22  disposed within selected air holes  18 , used to provide longitudinal mechanical strength to the arrangement. Outer region  14  is utilized as a sleeve to support the structure of inner region  12 . The remainder of the following discussion will simply reference to the preform as a “microstructured preform”. It is to be understood that this term equally applies to polarization-maintaining optical preforms, which are also formed to include longitudinal air holes during process and thus create the same surface roughness problems. 
         [0021]    As mentioned above, there exist various techniques (well known in the art) to form the plurality of longitudinal air holes  18  within preform  10 . These techniques include, but are not limited to, drilling, etching, the use of molds and casting forms, and the like. The quality of the large number of air/glass interfaces within optical fiber preforms including longitudinal holes is often problematic due to surface roughness, where the roughness may be a result of several different sources. Many of these microstructured optical performs also include microcracks, where these microcracks are known to propagate along a particular air/glass interface as the preform is “stretched” at the beginning of the fiber draw process.  FIG. 3  contains a photograph of a conventional prior art microstructured optical preform (side view), where the illustration of  FIG. 3(   a ) illustrates the preform prior to stretching. A number of microcracks (denoted as “M” in the illustration) are evident in this view. These microcracks are shown as being larger and more pronounced in the view of  FIG. 3(   b ). which illustrates the same optical preform—subsequent to the conventional stretching operation. 
         [0022]    Moreover, if the preform is etched in an HF solution (a conventional processing step, as mentioned above), the presence of the etchant will encourage the further propagation and/or enlargement of the microcracks along a particular air/glass interface. Pressurization of the preform during draw (another common fabrication environment) will also allow for the microcracks to propagate/enlarge. If the microcrack presence is severe enough, the internal air holes will connect, destroying the fiber geometry and limiting the ability to form fibers with relatively large air/fill fraction configurations (e.g., &gt;50%). While the following discussion will emphasize the ability of the inventive thermal treatment process to eliminate microcracks, it is to be understood that in its most general application the method of the present invention is utilized to reduce/eliminate surface roughness at the air/glass interfaces in general, that is, to “heal” all of the various surface defects associated with the formation of longitudinal air holes. 
         [0023]      FIGS. 4-6  illustrate an exemplary set of thermal processing steps that have been found, in accordance with the present invention, to treat the air/glass interfaces within a microstructured optical fiber preform in a manner such that the surface roughness and microcracks are essentially eliminated, thus improving the quality of the optical fiber ultimately drawn from the microstructured preform. In particular, and as discussed in detail below, a novel controlled compression process has been found to “heal” the damage created by the preform fabrication process. 
         [0024]    Referring to  FIG. 4 , the thermal treatment of the present invention begins with attaching a pair of glass handles  30 ,  32  to opposite ends of a microstructured optical fiber preform, such as preform  10  illustrated above. Once handles  30  and  32  have been attached, the arrangement is mounted in a lathe (not shown) or similar arrangement capable of supporting the arrangement during processing. A plasma torch  34  is used to heat preform  10  to a temperature at which the glass material will flow under stress. For example, a temperature of about 2000° C. has been suitable for this purpose. It is to be understood that various other conventional heat sources, such as an oxy-hydrogen torch or furnace may be used in performing the method of the present invention. 
         [0025]    When the temperature reaches the desired glass flow temperature, a compressive force F c  is applied against handles  30  and  32 , as shown in  FIG. 5 . Compression is preferably accomplished while also rotating preform  10  within a lathe and traversing plasma torch  34  along the rotating preform. The traverse velocity may be, for example, about 2 cm/min. Along with the transversal heating, handles  30  and  32  are simultaneously moved closer together until the desired amount of compression is obtained, where the diameter of the preform may be used as the measure of sufficient compression. Referring to  FIGS. 4 and 5 , an increase in the diameter of preform  10  is illustrated as diameter d i  for the “initial” diameter of preform  10  (for example, 35 mm) in  FIG. 4 , and d c  as the “compressed” diameter of preform  10  (for example, 42 mm) in  FIG. 5 . It has been found that performing compression during this initial heating step will knit together any internal microcracks, and heal surface roughness (i.e., air/glass interfaces along longitudinal holes) through viscous flow. 
         [0026]    Following the compression, preform  10  may be stretched prior to being drawn down into fiber (as in conventional preform fabrication), this step being illustrated in  FIG. 6  with the “stretching force” illustrated by arrows F s . Again, preform  10  is rotated and heated with a transversal movement of, for example, plasma torch  34 , during the stretching. The stretched diameter, denoted d s  may also be a predetermined value utilized to determine when the process is finished (for example, a stretched diameter d s  of 25 mm). Stretching may be performed in a single pass, or with multiple passes. For the stretching operation, the velocity of plasma torch  34  can be controlled, in one instance, by utilizing a feedback signal that monitors the current diameter of the preform. 
         [0027]    As mentioned above, it is possible to modify the diameter of the longitudinal air holes during the thermal treatment process of the present invention. In particular, during either the compression step or the stretching step (or both), a gas may be flowed through the air holes. A positive pressure flow will increase the diameter of the air holes, while a negative pressure flow will decrease the diameter of the longitudinal air holes. 
         [0028]      FIG. 7  contains actual photographs illustrating the improvement in preform quality associated with the thermal compression process of the present invention.  FIG. 7(   a ) is a photograph (side view) of an exemplary microstructured preform prior to thermal treatment. The darker regions correspond to the longitudinal air holes, while the bright regions are the silica material of the preform. Similar to the illustrations of  FIG. 3 , various “microcracks” are evident in the photograph of  FIG. 7(   a ). Subsequent to the thermal compression/stretching process of the present invention, these microcracks have been virtually eliminated, as shown in the photograph of  FIG. 7(   b ). 
         [0029]    One prior art technique for increasing the diameter of the air holes is to subject the preform to an etch in an acidic solution, such as hydrofluoric acid. However, the HF etch operation has been found to increase the severity of the already-present microcracks within the preform.  FIG. 8(   a ) illustrates an exemplary prior art microstructured preform that has been subjected to an HF etch process. The HF etch of this prior art preform shows several large defects that can be attributed to preferential etching along the microcracks of the original preform. In contrast, the use of the thermal treatment process of the present invention prior to an HF etch will minimize/eliminate the microcracks and result in an improved quality preform, as evident by the photograph of  FIG. 8(   b ). 
         [0030]    The thermal treatment of the present invention, as mentioned above and indicative from the illustrations of  FIGS. 7(   b ) and  8 ( b ), yields an essentially uniform surface finish along each of the air/glass interfaces within a microstructured preform. As a result, a microstructured preform with a relatively high air/fill fraction can be created, as shown in  FIG. 9 . For example,  FIG. 9(   a ) contains a cross-sectional image of a microstructured preform with a 70% air/fill fraction. The image of  FIG. 9(   b ) is associated with an 85% air/fill fraction and  FIG. 9(   c ) with a 99% air/fill fraction. Such large fractions would be difficult, if not impossible, to create without the thermal compression treatment of the present invention. Each of the images illustrates that the hole sizes are uniform throughout the cross-section, indicating that the thermal treatment does not alter or distort the topology of the holes. 
         [0031]    One concern with the use of a thermal compression process is that the high temperature of the plasma torch may cause some of the holes to collapse or distort.  FIG. 10  contains a plot associated with a preform that was first compressed from a diameter of 35 mm to a diameter of 42, and then stretched to 15 mm. The air hole sizes were measured as a function of the preform diameter. The hole size shows a consistently linear dependence on the preform diameter, indicating that there is no significant change in the relative hole size within the microstructured preform during the thermal treatment process of the present invention. 
         [0032]    It is to be understood that there exist various modifications that may be made to the inventive thermal treatment process including, but not limited to, the diameter achieved during compression, the compressive and tensile applied forces, the air-fill fraction, and the like. Indeed, the spirit and scope of the present invention is intended to be limited only by the claims appended hereto.