Abstract:
This invention relates to a new class of blend containing segments with a peptide base of hydrolysed proteins and gelatin, and segments with a polymer base consisting of variously substituted polyethylenes such as EVA and EVAL, and a method for their preparation.

Description:
FIELD OF INVENTION 
       [0001]    This invention relates to hydrolysed protein or gelatin-polymer blends, processes for their preparation and the use of said adducts in the plastics industry, in particular for the manufacture of packaging, crop protection systems and disposable materials for everyday use. In particular the invention relates to hydrolysed protein-EVA (ethylene vinyl acetate) blends, gelatin-EVA and hydrolysed protein-EVAL (ethylene vinyl alcohol) blends and gelatin-EVAL blends. 
       STATE OF THE ART 
       [0002]    Biodegradable polymers or bioplastics are an innovation which has been developed by the chemical and plastics industry over the last 15-20 years. The growing interest in plastics made of biodegradable polymers is mainly due to the problems involved in the disposal of plastic waste. 
         [0003]    As their structure is similar to that of conventional plastics, bioplastics can be turned into a wide and diversified range of products, using conventional manufacturing methods such as extrusion, moulding, film-coating, thermoforming and production of foam materials. The crucial difference from conventional polymers is that due to their chemical and physical structure, bioplastics can be attacked and degraded by micro-organisms such as fungi and bacteria. Moreover, the use of renewable resources in their manufacturing cycle plays a key role in terms of environmental sustainability. The biomass used in their manufacture constitutes a complement or alternative to resources of fossil origin. The products obtained from it return to the soil at the end of its life cycle through processes of biodegradation or composting, without any release of pollutants. 
         [0004]    Biodegradable materials from renewable sources make an important contribution to the introduction of a green economy based on renewable energy sources, chemical precursors and materials. There are many advantages involved in developing these materials, such as reduced dependence on fossil fuels, reduced greenhouse gas emissions, reduced pollutant emissions and toxicity associated with the various stages in the life cycle of conventional materials and processes, exploitation of waste and stocks in the agrifood industry, reduced quantities of waste sent to tips, and the development of environmentally sustainable technologies in general. 
         [0005]    Biodegradable materials have various fields of application: films, thermoformed, expanded and extruded products and injection mouldings are used in industry, agriculture, waste management, mass distribution, catering, etc. 
         [0006]    This type of material can be divided into two classes: wholly biodegradable polymers and mixtures consisting of a wholly biodegradable polymer (e.g. starch or cellulose) and a non-biodegradable commercial polymer (e.g. LDPE), which are known as biodisintegratable polymers. 
         [0007]    The most suitable materials to reduce pollution problems are the wholly biodegradable type; however, as they often present inferior mechanical properties at excessively high prices, biodisintegratable materials which reduce at least the volume of plastic waste, and offer a good compromise of mechanical properties, are used. Many bioplastics are mixtures or blends which contain synthetic components. Synthetic polymers and additives are often used, though in small quantities, to improve the functional properties of the finished product and expand its range of applications. 
         [0008]    Different types can be combined with others to form compounds or blends, or semi-finished products such as multi-ply film. In this case the properties and range of applications are generally expanded. 
         [0009]    Numerous studies conducted with a view to creating new biodisintegratable materials and evaluating their characteristics are reported in the literature. 
         [0010]    Many of them focus on materials with a filler consisting mainly of cellulose obtained from a variety of renewable sources: wood or sawdust, seaweed, cane, coconut, sago starch, sisal, pineapple, linseed and the like. 
         [0011]    Other experiments have been conducted on composites with a polyethylene matrix and a protein filler. 
         [0012]    Barone J. R. et al. have conducted various studies on polyethylene reinforced with keratin fibres obtained from chicken feathers; after a preliminary feasibility study they evaluated the characteristics of the composite by changing the type of polyethylene used and varying the operating conditions of the Brabender, from which the mixture was obtained, and of the film production press. 
         [0013]    Even more interesting is a study conducted by Saha N. et al., who developed a composite, using as polyolefin a low-density polyethylene produced with metallocene catalysts, which gives a linear structure (mLLDPE), while the filler is hydrolysed protein obtained by enzymatic hydrolysis. 
         [0014]    These studies did not find any bonds between the matrix and the filler, and the hydrolysed protein was uniformly distributed in the polyethylene; the mechanical properties are reduced in the presence of the filler, whereas the biodegradability improves as the percentage of hydrolysed product increases; according to the authors, the ideal composition contains 20% hydrolysed protein. 
     
    
     DESCRIPTION OF THE INVENTION 
       [0015]    This invention relates to blends obtainable by reactive molten mixing of hydrolysed protein or gelatin or mixtures thereof with functional copolymers with an ethylene base having aminic, carboxyl, hydroxyl, amide, ester or heterocyclic groups such as pyrrolidone, preferably hydroxyl or ester groups. 
         [0016]    In particular, the polyethylene copolymer has a degree of substitution, namely the quantity of —(CH 2 —CHR)— units compared with —(CH 2 —CH 2 )— ethylene units, which falls into the range 1-100%. 
         [0017]    Ethylene vinyl acetate (EVA) or ethylene vinyl alcohol (EVAL) copolymers are preferred, wherein the degree of substitution, namely the quantity of —(CH 2 —CHR)— units compared with —(CH 2 —CH 2 )— ethylene units, falls into the range 1-100%. 
         [0018]    Transfer agents, transesterification catalysts or ring opening catalysts or oxidizing agents can be added to the formulation. 
         [0019]    Tetrabutylammonium tetraphenylborate, tin 2-ethylhexanoate or N-acetyl-epsilon caprolactone is preferably added as transfer agent. A preferred oxidizing agent is dicumyl peroxide. 
         [0020]    A plasticiser such as glycerol, polyethylene glycol or propanediol can be added to the reaction mixture. Pigments and/or dyes and reinforcing materials such as fibres and/or particles(e.g. carbon black, natural fibres such as cellulose) may also be added to the mixture. 
         [0021]    According to the invention, the hydrolysed protein and/or gelatin has a nitrogen α-aminic content lower than 0.5% (by weight) per each percent unit of organic nitrogen. The hydrolysed product is preferably obtained from by-products and/or waste and/or residues originating from the tanning industry, obtained before and after the tanning stage, or from by-products and/or products of plant origin, agro-industrial waste, by-products and/or products of animal origin. 
         [0022]    The hydrolysed proteins can be present in the blends according to the invention in percentages ranging between 1 and 95% in order to enhance particular properties associated with the effects required, preferably from 5 to 80%, while ethylene polymers could be present in percentages ranging from 5 to 99%. 
         [0023]    Preferred examples of hydrolysed proteins used in the tests described derive from the processing of tanning waste. They are characterised by a particular aminoacid composition deriving from the starting material. Other hydrolysed proteins of different origins can be used to meet particular market and operational demand such as the need for material deriving only from raw materials not of animal origin, or the need for mechanical characteristics, degradability or differentiated compositions. 
         [0024]    The blends to which the invention relates present optimum mechanical properties which, surprisingly, do not significantly decline as the hydrolysed protein content increases; blends containing up to 35% hydrolysed protein maintain their properties, and the modulus of elasticity actually improves, while blends containing 50% hydrolysed protein still demonstrate very good properties (ultimate elongation approx. 500%) and a modulus of elasticity 10-15 times the modulus of the starting polymer. This result is very surprising in view of the fact that examples of different types of blends wherein the presence of only 20% hydrolysed protein drastically affects the mechanical properties, which are obviously crucial for the purpose of the applications considered, are reported in the literature. 
         [0025]    Further characteristics and advantages of the materials according to the invention will clearly appear from the description below, relating to examples of embodiment. In the examples below, the term “lp” indicates hydrolysed protein or gelatin, while the polymers will be indicated with the conventional codes. 
       EXAMPLES 
     Blends with poly(vinyl alcohol-co-ethylene) (EVAL) 
     Examples 1-3 
     Binary Blends with EVAL 27 
       [0026]    In order to lower the melting point of EVAL, that polymer was mixed with a plasticiser using a Brabender discontinuous mixer. A known quantity of EVAL 27 (ethylene 27 mol %) was loaded into the mixer, and a quantity of glycerol ranging between 12.5 and 30% was added (Table 1). The mixing conditions were: T mixer =220° C., V=50 rpm, time=10 min. The products were then isolated and the calorimetric parameters such as Tg and Tm were assessed (Table 1). 
       Examples 4-8 
     Binary Blends with EVAL 44 
       [0027]    The methodology of examples 1-3 was used, EVAL 44 (ethylene 44 mol %) being loaded into the mixer instead of EVAL 27. Glycerol was then added in a quantity ranging between 20 and 30% (Table 1), and the product was mixed under the following conditions: T mixer =200° C., v=50 rpm, time=10 min. The products were then isolated and the calorimetric parameters such as Tg and Tm were assessed (Table 1). 
         [0000]    
       
         
               
             
               
               
               
               
               
               
               
               
               
             
               
               
               
               
               
               
               
               
               
             
           
               
                 TABLE 1 
               
             
             
               
                   
               
               
                 Ethylene vinyl alcohol (EVAL) plasticised with glycerol 
               
             
          
           
               
                   
                   
                   
                   
                   
                   
                 Wtot 
                   
                   
               
               
                   
                   
                 EVAL27 
                 EVAL44 
                 Glyc. 
                 T mixer 
                 mixer 
               
               
                 Examples 
                 Code 
                 (%) 
                 (%) 
                 (%) 
                 (° C.) 
                 (g) 
                 Tm 
                 Tg 
               
               
                   
               
             
          
           
               
                   
                 EVAL27 
                 100 
                   
                   
                   
                   
                 187.76 
                 63.67 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 133.99 
               
               
                 Es. 1 
                 EVAL27_GLI30 
                 68.75 
                 — 
                 31.25 
                 220 
                 48 
                 160.73 
                 * 
               
               
                 Es. 2 
                 EVAL27_GLI30 (2) 
                 70 
                 — 
                 30 
                 220 
                 52.86 
                 152.69 
                 49.04 
               
               
                 Es. 3 
                 EVAL27_GLI12,5 
                 87.48 
                 — 
                 12.5 
                 220 
                 44.58 
                 171.75 
                 19.02 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 114.55 
               
               
                   
                 EVAL44 
                 100 
                   
                   
                   
                   
                 166.67 
                 61.14 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 127.05 
               
               
                 Es. 4 
                 EVAL44_GLI20 
                 — 
                 80.48 
                 19.5 
                 200 
                 49.7 
                 141.82 
                 32.24 
               
               
                 Es. 5 
                 EVAL44_GLI30 
                 — 
                 70 
                 30 
                 200 
                 54.3 
                 130.43 
                 6.5 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 41.99 
               
               
                 Es. 6 
                 EVAL44 GLI30 (2) 
                 — 
                 71.1 
                 28.9 
                 200 
                 53.61 
                 132.18 
                 44.7 
               
               
                 Es. 7 
                 EVAL44_GLI30 (3) 
                 — 
                 69.35 
                 30.64 
                 200 
                 54.88 
                 131.91 
                 8.25 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 46.12 
               
               
                 Es. 8 
                 EVAL44_GLI30 (4) 
                 — 
                 69.64 
                 30.36 
                 200 
                 54.75 
                 133.26 
                 7.08 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 44.03 
               
               
                   
               
             
          
         
       
     
       Example 9-13 
     Ternary Blends 
       [0028]    The products obtained as described in examples 4-8 were loaded into the discontinuous mixer, and hydrolysed protein (N α-aminic 2.11% w/w) was added in quantities ranging between 35 and 75% (Table 2). The products were mixed under the following conditions: T mixer 150° C., v=50 rpm, time=7 min. The products were then isolated and the calorimetric parameters such as Tg and Tm were assessed (Table 2). 
       Examples 14-16 
     Ternary Blends with Transfer Agents 
       [0029]    The ternary blends Hydrolysed protein-EVAL-Glycerol can be prepared as described in examples 9-13 with the addition of transfer agents such as tetrabutylammonium tetraphenylborate (TB), tin 2-ethylhexanoate (Sn) or N-acetyl-epsilon caprolactone (CL) in the quantity of 1% (weight/weight). The products were mixed under the same conditions as described in example 3, isolated and characterised by DSC (Table 2). 
         [0000]    
       
         
               
             
               
               
               
               
               
               
               
               
               
             
               
               
               
               
               
               
               
               
               
             
           
               
                 TABLE 2 
               
             
             
               
                   
               
               
                 Hydrolysed Protein - (EVAL) - Glycerol 
               
             
          
           
               
                   
                   
                 IP (1) 
                 EVAL44 
                 Glyc 
                 Cat 
                 Tmixer 
                 Wmixer 
                 Tg 
               
               
                 Examples 
                 Code 
                 (%) 
                 (%) 
                 (%) 
                 (1%) 
                 (° C.) 
                 (g) 
                 (° C.) 
               
               
                   
               
             
          
           
               
                   
                 PP 
                 100 
                   
                   
                   
                   
                   
                 129.78 
               
               
                 Es. 9 
                 PP75%_EVAL44_GLI20 
                 74.33 
                 19.68 
                 5.98 
                 — 
                 150 
                 50.92 
                 48.63 
               
               
                 Es. 10 
                 PP60%_EVAL44_GLI20 
                 57.78 
                 31.48 
                 10.74 
                 — 
                 150 
                 52.34 
                 * 
               
               
                 Es. 11 
                 PP55%_EVAL44_GLI30 
                 54.46 
                 31.88 
                 13.66 
                 — 
                 150 
                 55.81 
                 10.43 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 44.1 
               
               
                 Es. 12 
                 PP35%_EVAL44_GLI30 
                 36.6 
                 44.36 
                 19 
                 — 
                 150 
                 54.05 
                 43.86 
               
               
                 Es. 13 
                 PP70%_EVAL44_GLI30 
                 70.34 
                 20.95 
                 8.98 
                 — 
                 150 
                 54.23 
                 25.74 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 71.53 
               
               
                 Es. 14 
                 PP35%_EVAL44_GLI30 (TB) 
                 36.16 
                 44.13 
                 18.9 
                 TB (2) 
                 150 
                 53.93 
                 * 
               
               
                 Es. 15 
                 PP35%_EVAL44_GLI30 (Sn) 
                 36.67 
                 43.77 
                 18.76 
                 Sn (3) 
                 150 
                 54.54 
                 * 
               
               
                 Es. 16 
                 PP35%_EVAL44_GLI30 (CL) 
                 36.51 
                 44.7 
                 18 
                 CL (4) 
                 150 
                 54.23 
                 * 
               
               
                   
               
               
                 (1): IP = hydrolysed protein batch A02/44/02 characterised by: Dry matter 94.07% w/w N α-aminic 2.11% w/w 
               
               
                 (2): TB = tetrabutylammonium tetraphenylborate 
               
               
                 (3): Sn = tin 2-ethylhexanoate 
               
               
                 (4): CL = N-acetyl-epsilon caprolactone 
               
               
                 * = Tg not detectable 
               
             
          
         
       
     
         [0030]    Blends with poly(ethylene-co-vinyl acetate) (EVA) 
       Example 17 
     Binary Blends 
       [0031]    A known quantity of hydrolysed protein was loaded into the mixer and EVA (40 wt. % vinyl acetate) was added (Table 3). The mixing conditions were: T mixer =140° C., v=50 rpm, time=7 min. The products were then isolated and the calorimetric parameters such as Tg and Tm were assessed (Table 3). 
       Examples 18-20 
     Ternary Blends 
       [0032]    Known quantities of hydrolysed protein were loaded into the mixer, and EVA (40 wt. % vinyl acetate) and glycerol were added in the quantities shown in Table 3. The mixing conditions were: T mixer =140° C., v=50 rpm, time=7 min. The products were isolated, and the calorimetric parameters such as Tg and Tm were assessed (Table 3). 
       Examples 21-26 
     Binary Blends with Transfer Agents 
       [0033]    Blends based on hydrolysed protein (up to 50%) and EVA were obtained by mixing the two components in variable percentages (Table 3) in the presence of transfer agents such as tetrabutylammonium tetraphenylborate (TB), tin 2-ethylhexanoate (Sn) or N-acetyl-epsilon caprolactone (CL) in the quantity of 1% (weight/weight). The mixing conditions were: T mixer =140° C., v=50 rpm, time=7 min. The products were then isolated and the calorimetric parameters such as Tg and Tm were assessed (Table 3). 
         [0000]    
       
         
               
             
               
               
               
               
               
               
               
               
             
               
               
               
               
               
               
               
               
             
           
               
                 TABLE 3 
               
             
             
               
                   
               
               
                 Blends with ethylene vinyl acetate (EVA) 
               
             
          
           
               
                   
                   
                 IP (1) 
                 EVA (5) 
                 Glyc 
                 Cat 
                   
                 Tg 
               
               
                 Examples 
                 code 
                 (%) 
                 (%) 
                 (%) 
                 (1%) 
                 Tmixer 
                 (° C.) 
               
               
                   
               
             
          
           
               
                   
                 EVA 
                   
                 100 
                   
                   
                   
                 −32.18 
               
               
                 ES. 17 
                 PP50%_EVA 
                 50.4 
                 49.6 
                 — 
                 — 
                 150 
                 * 
               
               
                   
                 PP50%_EVA 
                 50.4 
                 49.6 
                 — 
                 — 
                 140 
                 * 
               
               
                 Es. 18 
                 PP35%_EVA_GLI30 
                 36.76 
                 45.19 
                 18 
                 — 
                 140 
                 * 
               
               
                 Es. 19 
                 PP55%_EVA_GLI30 
                 53.5 
                 34.57 
                 12 
                 — 
                 140 
                 * 
               
               
                 Es. 20 
                 PP70%_EVA_GLI 
                 70.97 
                 24.47 
                 4.6 
                 — 
                 140 
                 43.44 
               
               
                 Es. 21 
                 PP35%_EVA (TB) 
                 36 
                 63 
                 — 
                 TB (2) 
                 140 
                 43.17 
               
               
                 Es. 22 
                 PP35%_EVA (Sn) 
                 36.15 
                 62.94 
                 — 
                 Sn (3) 
                 140 
                 43.91 
               
               
                 Es. 23 
                 PP35%_EVA (CL) 
                 35.93 
                 63.07 
                 — 
                 CL (4) 
                 140 
                 45 
               
               
                 Es. 24 
                 PP50%_EVA (TB) 
                 49.42 
                 49.55 
                   
                 TB (2) 
                 140 
               
               
                 Es. 25 
                 PP50%_EVA (Sn) 
                 49.7 
                 49.2 
                 — 
                 Sn (3) 
                 140 
               
               
                 Es. 26 
                 PP50%_EVA (CL) 
                 49.48 
                 49.49 
                   
                 CL (4) 
                 140 
               
               
                   
               
               
                 (1): IP = hydrolysed protein batch A02/44/02 characterised by: Dry matter 94.07% w/w N α-aminic 2.11% w/w 
               
               
                 (2): TB = tetrabutylammonium tetraphenylborate 
               
               
                 (3): Sn = tin 2-ethylhexanoate 
               
               
                 (4): CL = N-acetyl-epsilon caprolactone 
               
               
                 (5): poly(ethylene-co-vinyl acetate)(EVA), 40 wt. % vinyl acetate. 
               
               
                 * = Tg not detectable 
               
             
          
         
       
     
       Mechanical Characterisation 
     Example 27 
     Compression Moulding of Specimens and Films 
       [0034]    Specimens and films of variable size and thickness were obtained by compression moulding from the blend obtained as described in the examples described above. The parameters set on the press are: 
         [0000]    
       
         
               
             
               
               
               
               
               
             
               
             
               
               
               
               
               
             
           
               
                   
               
             
             
               
                 1. blends with EVAL 
               
             
          
           
               
                   
                 Melting 
                 T = 150° C. 
                 t = 180 sec 
                 p = 6 bar 
               
               
                   
                 Compression 
                 T = 150° C. 
                 t = 30 sec 
                 p = 30 bars 
               
               
                   
                 Cooling 
                 T = 20° C. 
                 t = 360 sec 
                 p = 30 bars 
               
             
          
           
               
                 2. blends with EVA 
               
             
          
           
               
                   
                 Melting 
                 T = 140° C. 
                 t = 180 sec 
                 p = 6 bars 
               
               
                   
                 Compression 
                 T = 140° C. 
                 t = 30 sec 
                 p = 30 bars 
               
               
                   
                 Cooling 
                 T = 20° C. 
                 t = 360 sec 
                 p = 30 bars 
               
               
                   
                   
               
             
          
         
       
     
         [0035]    The specimens and films are of excellent quality and present no significant surface defects, thus demonstrating the excellent workability of the materials. 
       Example 28 
     Dynamic/Mechanical Tests 
       [0036]    Dynamic/mechanical tests were performed on specimens of a suitable size under the following operating conditions: 
         [0037]    Temperature range considered 30-100° C., heating rate 1° C./min, frequency 5 Hz. With this technique it was possible to determine the dynamic modulus and the glass transition temperature (Tg) of the materials (Table 4). 
       Example 29 
     Tensile Tests 
       [0038]    The tensile test was conducted in accordance with standard ASTM D 882, with a crosspiece advance rate amounting to 10 mm/min. Table 4 shows the modulus of elasticity, yield point, ultimate tensile strength and ultimate elongation of the various materials. 
         [0000]    
       
         
               
             
               
               
               
             
               
               
               
               
               
               
               
             
               
               
               
               
               
               
               
             
           
               
                 TABLE 4 
               
             
             
               
                   
               
               
                 Mechanical properties of the blends obtained 
               
             
          
           
               
                   
                 DMTA 
                 TENSILE 
               
             
          
           
               
                   
                   
                 Tg 
                 E 
                 σf 
                 Δε 
                   
               
               
                 Code 
                 E′ (MPa) 
                 (° C.) 
                 (MPa) 
                 (MPa) 
                 (%) 
                 σy (MPa) 
               
               
                   
               
             
          
           
               
                 EVA 
                   
                   
                 2.39 
                 &gt;1.6 
                 &gt;700 
                 — 
               
               
                 Sicit 51 
                 491.81 
                 54 
                 797.92 
                 14.5 
                 &gt;100 
                 13.67 
               
               
                 PP35%_EVA 
                 — 
                 — 
                 6.76 
                 2.4 
                   320 
                 — 
               
               
                 PP35%_EVA (TB) 
                   
                   
                 6.07 
                 &gt;1.4 
                 &gt;700 
                 1.06 
               
               
                 PP35%_EVA (TB) 
                 7.84 
                   
                 10.93* 
                 &gt;1.4* 
                  &gt;920* 
                 0.99* 
               
               
                 PP35%_EVA (Sn) 
                 7.5 
                   
                 5.18 
                 &gt;1.7 
                 &gt;700 
                 — 
               
               
                 PP35%_EVA (CL) 
                 7.53 
                   
                 5.32 
                 &gt;1.8 
                 &gt;700 
                 — 
               
               
                 PP50%_EVA (TB) 
                   
                   
                 22.55 
                 1.45 
                   237 
                 — 
               
               
                 PP50%_EVA (Sn) 
                   
                   
                 34.95 
                 1.6 
                    95 
                 — 
               
               
                 PP50%_EVA (CL) 
                   
                   
                 28.05 
                 1.3 
                   205 
                 — 
               
               
                 EVAL 
                   
                   
                 2568 
                 55.34 
                    3 
                 — 
               
               
                 PP35%_EVAL44_GLI30 
                   
                   
                 372.3 
                 14.75 
                    14 
                 — 
               
               
                 PP35%_EVAL44_GLI30 (TB) 
                   
                   
                 300 
                 13.38 
                    15 
                 — 
               
               
                 PP35%_EVAL44_GLI30 (Sn) 
                   
                   
                 266.5 
                 12 
                    13 
                 — 
               
               
                 PP35%_EVAL44_GLI30 (CL) 
                   
                   
                 282.2 
                 11.7 
                    15 
                 — 
               
               
                   
               
               
                 *data obtained with specimens different from those specified in the standard. 
               
             
          
         
       
     
       Example 30 
     Maintenance of Crystallinity in Blends with Ethylene Vinyl Alcohol 
       [0039]    Using a calorimetric test conducted with DSC, it was possible to determine the melting enthalpy for the samples presenting crystallinity. By comparison it was found that this crystallinity, due to the presence of the polymer EVAL, is maintained in all blends that contain it. The percentage crystallinity of polymers is a very important parameter because it affects the mechanical, optical and diffusion properties of the product. 
         [0000]    
       
         
               
             
               
               
               
               
             
               
               
               
               
             
           
               
                 TABLE 5 
               
             
             
               
                   
               
               
                 Maintenance of crystallinity in blends with ethylene vinyl 
               
               
                 alcohol 
               
             
          
           
               
                   
                   
                   
                 (ΔHblend − 
               
               
                   
                   
                   
                 ΔHpolym)/ 
               
               
                   
                 Tm 
                 ΔHMelting 
                 ΔHblend 
               
               
                 Code 
                 (° C.) 
                 (J/g) 
                 (%) 
               
               
                   
               
             
          
           
               
                 EVAL44 
                 166.67 
                 54.08 
                 100 
               
               
                 EVAL44_gli20 
                 141.82 
                 46.63 
                 +7.14 
               
               
                 EVAL44_gli30 1 
                 132.18 
                 42.62 
                 +10.84 
               
               
                 EVAL44_gli30 2 
                 131.91 
                 39.88 
                 +6.33 
               
               
                 EVAL44_gli30 3 
                 130.43 
                 43.94 
                 +16.07 
               
               
                 EVAL44_gli30 4 
                 133.26 
                 39.99 
                 +4.72 
               
               
                 PP35_EVAL44_gli30 
                 144.67 
                 26.84 
                 +11.88 
               
               
                 PP35_EVAL44_gli30 (Sn) 
                 146.61 
                 25.65 
                 +8.36 
               
               
                 PP35_EVAL44_gli30 (TB) 
                 144.76 
                 24.01 
                 +0.6 
               
               
                 PP35_EVAL44_gli30 (CL) 
                 144.13 
                 25.12 
                 +3.9