Abstract:
The invention relates to a Li a Ni x Co y Mn y′ M′ z O 2  composite oxide for use as a cathode material in a rechargeable battery, with a non-homogenous Ni/M′ ratio in the particles, allowing excellent power and safety properties when used as positive electrode material in Li battery. More particularly, in the formula 0.9&lt;a&lt;1.1, 0.3≦x≦0.9, 0&lt;y≦0.4, 0&lt;y′≦0.4, 0&lt;z≦0.35, e&lt;0.02, 0≦f≦0.05 and 0.9&lt;(x+y+y′+z+f)&lt;1.1; 
     M′ consists of either one or more elements from the group Al, Mg, Ti, Cr, V, Fe, Mn and Ga; N consists of either one or more elements from the group F, Cl, S, Zr, Ba, Y, Ca, B, Sn, Sb, Na and Zn. The powder has a particle size distribution defining a D10, D50 and D90; and the x and z parameters varying with the particles size of the powder, and is characterized in that either one or both of:
 
 x 1− x 2≧0.005
 
and
 
 z 2− z 1≧0.005;
 
x1 and z1 being the parameters corresponding to particles having a particle size D90; and x2 and z2 being the parameters corresponding to particles having a particle size D10.

Description:
This application claims priority to European Patent Application No. 10008566.1, filed Aug. 17, 2010, and U.S. Provisional Patent Application No. 61/344,556, filed Aug. 20, 2010, the entire contents of which are hereby incorporated by reference. 
     TECHNICAL FIELD AND BACKGROUND 
     The invention relates to a Li a Ni x Co y Mn y′ M′ z O 2  composite oxide (M′ being Al, Mg, Ti, Cr, V, Fe, Ga) with a non-homogenous Ni/M ratio in particles of different sizes, allowing excellent power and safety properties when used as positive electrode material in Li battery. 
     Due to their high energy density, rechargeable lithium and lithium-ion batteries can be used in a variety of portable electronics applications, such as cellular phones, laptop computers, digital cameras and video cameras. Commercially available lithium-ion batteries typically consist of graphite-based anode and LiCoO 2 -based cathode materials. However, LiCoO 2 -based cathode materials are expensive and typically have a relatively low capacity of approximately 150 mAh/g. 
     Alternatives to LiCoO 2 -based cathode materials include LNMCO type cathode materials. LNMCO means lithium-nickel-manganese-cobalt-oxide. The composition is LiMO 2  or Li 1+x M 1−x O 2  where M=Ni x Co y Mn y′ M′ z . LNMCO has a similar layered crystal structure as LiCoO 2  (space group r-3m). The advantage of LNMCO cathodes is the much lower raw material price of the composition M versus Co. The preparation of LNMCO is in most cases more complex than LiCoO 2 , because special precursors are needed wherein the transition metal cations are well mixed. Typical precursors are mixed transition metal hydroxides, oxyhydroxides or carbonates. Typical LiNMCO-based cathode materials include compositions having a formula LiNi 0.5 Mn 0.3 Co 0.2 O 2 , LiNi 0.6 Mn 0.2 Co 0.2 O 2  or Li 1.05 M 0.95 O 2 , with M=Ni 1/3 Mn 1/3 Co 1/3 O 2 . Compared with LiCoO 2 , LNMCO tends to have a lower bulk diffusion rate of lithium, which can limit the maximum possible particle size for a given composition. Depending on the composition, the safety of the charged cathode in a real cell can be a problem. Safety events ultimately are caused by reactions between the oxidized surface and the reducing electrolyte. Thus safety problems are more severe if the particles have a high surface area, which is the case if the particle size is small. The conclusion is that the lower performance of LNMCO requires a small particle size which deteriorates safety. 
     A way to improve the safety has been to dope LNMCO materials with inert elements such as Al, Mg, Ti, in order to stabilize the structure when heated in the charged state. A drawback to that major improvement regarding safety is the fact that inert element doping is detrimental for power and reversible capacity within the LNMCO material. In order for this material to be industrially usable, manufacturers had to find a compromise between safety and performance, thus using the lowest amounts of Al, Ti and Mg required for obtaining a satisfying safety, while keeping decent power and capacity performances. Recently there have been numerous disclosures about the influence of Mg and Al doping for LNMCO with Ni:Co:Mn=33:33:33, or other compositions as for example LiNi 1−x−y Mn x Co y O 2 . It is widely expected that such composition will become a commercial product soon. However, as explained above, these products typically suffer from a difficult compromise between safety and electrochemical performances, thus resulting in medium level of overall performances. 
     With the appearance of new applications for large batteries on the market (e.g. for hybrid vehicles or stationary power devices) and a need for meeting high safety requirements, without compromising on power performances, it appears that a breakthrough is needed in the synthesis of these NiMnCo-based materials. 
     As there has always been a concern to manufacture materials that are as homogeneous as possible, the state of the art manufacturing process of Li a Ni x Co y Mn y′ M′ z O 2  (M′=Al, Ti, Mg . . . ) products uses doped precursors such as hydroxides (see for example in U.S. Pat. No. 6,958,139), carbonates, nitrates or oxides, that are sintered at temperatures above 600° C. Thus, the material is perfectly homogeneous in composition, and the resulting positive electrode material shows medium level of global performances. Considering fundamentals from solid state chemistry applied to battery materials, it is known that for LiCoO 2  material, smaller particle size gives better power performances (as discussed in Choi et al., J. Power Sources, 158 (2006) 1419). It is however also known that a smaller particle size gives lower safety, as safety characteristics are somewhat linked to surface area (see for example Jiang et al., Electrochem. Acta, 49 (2004) 2661). It follows that for the LiNi x Co y Mn y′ M′ z O 2  system, where the presence of given amounts of Ni and M′ (M′ being e.g. Al) are focused respectively on improving power behaviour and safety, a homogenous composition both for small and large particles leads to a compromise between power and safety performance. Real powders have a distribution of particles with different size. However, a homogeneous composition of all particles is not preferred at all. For the small particles in which safety behaviour is directly related to M′ content, a higher M′ concentration would be needed to achieve the same safety behaviour as for larger particles. On the other hand, less M′ (inert doping) is needed in the large particles but a decrease of M′ in the large particles would enhance the performances of the LiNi x Co y Mn y′ M′ z O 2  system. 
     The present invention provides a solution to this problem. 
     SUMMARY 
     Viewed from a first aspect, the invention can provide a lithium metal oxide powder for use as a cathode material in a rechargeable battery, having a general formula Li a Ni x Co y Mn y′ M′ z O 2±e A f , with 
     0.9&lt;a&lt;1.1, 0.3x≦0.9, 0&lt;y≦0.4, 0&lt;y′≦0.4, 0&lt;z≦0.35, e&lt;0.02 (mostly e≈0 or e being close to 0), 0≦f≦0.05 and 0.9&lt;(x+y+y′+z+f)&lt;1.1; 
     M′ consisting of either one or more elements from the group Al, Mg, Ti, Cr, V, Fe and Ga; A consisting of either one or more elements from the group F, C, Cl, S, Zr, Ba, Y, Ca, B, Sn, Sb, Na and Zn; the powder having a particle size distribution defining a D10, D50 and D90; the powder having a particle size distribution defining a D10 and a D90; and wherein either:
 
x1−x2≧0.005; or z2−z1≧0.005; or both x1−x2≧0.005 and z2−z1≧0.005;
 
x1 and z1 being the parameters corresponding to particles having a particle size D90; and x2 and z2 being the parameters corresponding to particles having a particle size D10.
 
     In one embodiment both x1−x2≧0.010 and z2−z1≧0.010; in another embodiment x1−x2≧0.020 and z2−z1&gt;0.020 and in another embodiment both x1−x2≧0.030 and z2−z1≧0.030. The more stringent the conditions for the differences between x1 and x2, z1 and z2, the more pronounced are the effects both on safety and electrochemical performances. 
     In another embodiment, the Ni content of the powder increases with increasing particle size, and the M′ content of the powder decreases with increasing particle size. The Ni content may increase continuously, and the M′ content may decrease continuously, resulting in a Ni/M′ ratio that varies continuously with particle size. 
     In yet another embodiment f=0 and M′ consists of Al. In another embodiment A consists of either one or both of S and C with f≦0.02. There is also an embodiment where A consists of C, with f≦0.01. 
     It should be mentioned here that WO2005/064715 describes a cathode active material comprising a lithium transition metal oxide Li a M b O 2 , with M=A z A′ z′ M′ 1−z−z′ , M′ being Mn x Ni y Co 1−x−y , A=Al, Mg or Ti and A′ being a further dopant, where 0≦x≦1, 0≦y≦1, 0≦z+z′&lt;1, z′&lt;0.02. The composition M of this product varies with the size of the particles. In particular, smaller particles contain less cobalt and more manganese than larger particles. The Ni, Al, Mg and Ti contents however do not vary as described above. 
     Viewed from a third aspect, the invention can also provide a process for the manufacture of the powder oxide according to the invention, and comprising the steps of:
         providing a M-precursor powder, with M=Ni x Co y  Mn y′ M′ z A f , having a particle size distribution defining a D10 and a D90; wherein either x1−x2≧0.005; or z2−z1≧0.005; or both x1−x2≧0.005 and z2−z1≧0.005; x1 and z1 being the values of x and z of particles having a particle size D90; and x2 and z2 being the values of x and z of particles having a particle size D10,   mixing the M-precursor powder with a lithium precursor, preferably lithium carbonate, and   heating the mixture at a temperature of at least 800° C.       

     The step of providing a M-precursor powder may comprise the steps of:
         providing at least two M-precursor powders having a different particle size distribution characterized by different D10 and D90 values, and wherein a M-precursor powder having a lower D10 and D90 value has either one or both of a lower Ni content and a higher M′ content, than a M-precursor powder having a higher D10 and D90 value; and   mixing the at least two M-precursor powders.       

     In one embodiment the at least two M-precursor powders are mixed with the lithium precursor, before heating the mixture at a temperature of at least 800° C. 
     By precursor powder is understood that these powders are precursors of the Li a Ni x Co y  Mn y′ M′ z O 2±e A f  lithium transition metal oxides, such as provided in some embodiments: hydroxide or oxyhydroxide compositions obtained by precipitating metal sulphates, nitrates, chlorides or carbonates in the presence of an alkali hydroxide and a chelating agent, preferably ammonia. 
     In an embodiment the difference between the Co content of the M-precursor powder having a lower D10 and D90 value, and the Co content of the M-precursor powder having a higher D10 and D90 value, is less than the difference between both the Ni and M′ contents of the M-precursor powders. Also the difference between the Mn content of the M-precursor powder having a lower D10 and D90 value, and the Mn content of the M-precursor powder having a higher D10 and D90 value, is less than the difference between both the Ni and M′ contents of the M-precursor powders. 
     DETAILED DESCRIPTION 
     The invention can provide a powder having a formula Li a Ni x Co y Mn y′ M′ z O 2  for use as positive electrode in Li batteries, and having a non-homogeneous Nickel-M′ ratio in the particles for a constant cobalt and/or manganese content. The x and z parameters may vary with the particles size of the powder, either one or both of: 
     x1−x2≧0.005 and z2−z1≧0.005 may be valid, where x1 and z1 are the parameters corresponding to particles having a particle size D90 of the powder; and x2 and z2 are the parameters corresponding to particles having a particle size D10. 
     This comes to meet the need for a Li a Ni x Co y Mn y′ M′ z O 2  material to be tailored to achieve at the same time a high nickel content for high power in the larger particles and a high stabilizing metal M′ content, such as aluminum, for high safety in the smaller ones. Hence, as a result, the relative content of each species is strongly correlated to the size of the particle. The Co % Mn contents can be kept constant whatever the particle size, as this contributes to make the synthesis easier by maintaining the layered character of the LiNiO 2 -type material. 
     Compared to prior art and current Li a Ni x Co y Mn y′ M′ z O 2  materials, the advantages of the invention are:
         improved power performances as the Ni and M′ content is optimized (resp. increased and decreased) in the large particles while these large particles are known to be limiting the power performances,   improved safety performances as the Ni and M′ content is optimized (resp. decreased and increased) in the fine particles while these small size particles are known to be detrimental for safety.       

     In an embodiment, the Ni and M′ (preferably Al) concentration should follow a continuous increase and decrease respectively with increasing particle size. 
     In yet another embodiment, Ni and Al should be homogeneously dispersed within each single particle in order to avoid mechanical stresses while intercalating/deintercalating Li when using the powder in a rechargeable battery. 
     In another embodiment, the use of a Li a Ni x Co y  Mn y′ M′ z O 2±e A f  material with a non-homogenous Ni/Al ratio in its particles in the manufacture of a lithium insertion-type electrode is disclosed, by mixing the powder with a conductive carbon-bearing additive. The corresponding electrode mixture is also claimed. 
    
    
     
       BRIEF INTRODUCTION TO THE DRAWINGS 
         FIG. 1 : SEM picture of the material according to the invention showing spherical particles of different sizes. 
         FIG. 2 : variation of the Ni and Al content (in mol %) as a function of particle size (D50) in the material according to the invention. This graph clearly shows that the Ni/Al ratio varies continuously with particle size. 
         FIG. 3 : Ni, Co and Al mapping by EDS on cross-sections of particles of the material according to the invention. This measure clearly shows homogeneous repartition of the species within a single particle. 
         FIG. 4 : Galvanostatic discharge curve of the material of the invention at different rates (from right to left: C/10, C/5, C/2, 1 C, 2 C and 3 C). This shows the excellent capacity and power properties of this material. 
         FIG. 5 : variation of the Ni and Al content (in mol %) as a function of SEM particle size in the state of the art material. This measurement clearly shows that the Ni/Al ratio is constant whatever the particle size. 
         FIG. 6 : XRD pattern for size dependent (1) and non size dependent sample (2). 
         FIG. 7 : Galvanostatic discharge curve of the state of the art material at different rates (from right to left: C/10, C/5, C/2, 1 C, 2 C and 3 C). This shows the low capacity and power properties of the state of the art material. 
     
    
    
     The invention is further illustrated in the following examples: 
     EXAMPLE 1 
     In a first step, a composite Ni—Mn—Co—Al (or NMCA) hydroxide precursor with molar composition 39.9:35.2:12.8:12.2 is precipitated from Ni, Mn, Co and Al sulphates in the presence of NaOH and ammonia. The obtained NMCA hydroxide has a spherical shape and the average particle size as measured from laser granulometry is centered around D50=5.4 μm (D10=3.4 μm, D90=8.9 μm). 
     In a second step, a NMCA hydroxide precursor with molar composition 42.3:35.7:13.7:8.3 is precipitated from Ni, Mn, Co and Al sulphates in the presence of NaOH and ammonia. The obtained NMCA hydroxide shows spherical shape and the average particle size as measured from laser granulometry is centered around D50=9.3 μm (D10=5.0 μm, D90=16.5 μm). 
     In a third step a NMCA hydroxide precursor with molar composition 44.3:35.8:13.8:6.0 is precipitated from Ni, Mn, Co and Al sulphates in the presence of NaOH and ammonia. The obtained NMCA hydroxide shows spherical shape and the average particle size as measured from laser granulometry is centered around D50=15.5 μm. (D10=11.1 μm, D90=21.7 μm). 
     In a last step, the three hydroxide precursor powders as synthesized above are mixed in the ratio 0.4:0.3:0.3 and mixed with Li 2 Co 3  such that Li/(Ni+Co+Mn+Al)=1.075. The mixture is then heated in a tubular furnace under an oxygen flow at 980° C. for 10 h. The global composition of the obtained Li a Ni x Co y Mn y′ Al z O 2  powder as deduced from ICP is Ni:Mn:Co:Al=42.1:35.8:13.8:8.3. 
     The particle size distribution of the product after firing is measured by laser diffraction granulometry and shows a PSD with D10=5.2 μm, D50=9.1 μm, D90=15.5 μm. 
     A FEG-SEM and size vs. composition analysis is performed on the LiNi x Co y Mn y′ Al z O 2  material made according to Example 1 (see  FIG. 1 ). The following experiment confirms that the final powder has retained most of the size dependent composition of the precursor. The composition of different fractions of the final powder is measured by ICP. The different fractions (with different particle size) are obtained by elutriation. In an elutriation experiment, powders are separated by settling down in a slow upward flow of liquid. Thus small particles reach the overflow fast, large particles later. The particle size of the different fractions is measured using laser diffraction granulometry. This clearly shows that the chemical composition (Ni:Mn:Co:Al) of the final product is varying as a function of its particle size (see Table 1a &amp;  FIG. 2 ). 
     
       
         
               
             
               
               
               
               
               
             
               
               
               
               
               
             
           
               
                 TABLE 1a 
               
             
             
               
                   
               
               
                 Molar composition (Ni:Mn:Co:Al) according to particle size. 
               
             
          
           
               
                 D50 (μm) 
                 Ni (mol %)  
                 Mn (mol %) 
                 Co (mol %)  
                 Al (mol %) 
               
               
                   
               
             
          
           
               
                 4.4 
                 40.4 
                 35.0 
                 13.4 
                 11.2 
               
               
                 5.4 
                 41.0 
                 35.5 
                 13.4 
                 10.0 
               
               
                 6.4 
                 41.5 
                 36.0 
                 13.5 
                 9.0 
               
               
                 11.0 
                 42.7 
                 35.7 
                 13.8 
                 7.8 
               
               
                   
               
             
          
         
       
     
     It can be concluded that the values for D10 and D90 should be as in Table 1b: 
     
       
         
               
               
               
               
             
               
               
               
               
             
           
               
                 TABLE 1b 
               
               
                   
               
               
                 particle size 
                 Size (μm) 
                 Ni (mol %) 
                 Al (mol %) 
               
               
                   
               
             
             
               
                   
               
             
          
           
               
                 D90 
                 15.5 
                 &gt;44.1 
                 &lt;5.5 
               
               
                 D10 
                 5.2 
                 &lt;41.0 
                 &gt;10.0 
               
               
                   
               
             
          
         
       
     
     As can be deduced from  FIG. 2 , there is a very good correlation between Ni and Al content (mol %) with particle size as measured from laser granulometry, the linear trend (mol % Ni=s·D+t1 and mol % Al=u·D+t2) being:
         for Ni: Ni (mol %)=0.32·D+39.2   for Al: Al (mol %)=−0.46·D+12.6.       

     In an embodiment of the invention, the dependency (in % mol) of Ni and M′ (preferably Al) with particle size follows a linear trend % mol Ni=s·D+t1, and % mol M′=u·D+t2, D being the particle size as measured from SEM pictures, with s&gt;0 or Abs(s)&gt;0.1, preferably &gt;0.2, and more preferably &gt;0.3; and/or Abs(u)&gt;0.1, preferably &gt;0.2, and more preferably &gt;0.3. 
     Moreover, EDS analysis on a cross section of a single particle (see  FIG. 3 ) clearly shows that the Ni/Mn/Co/Al distribution within a particle is fully homogeneous, with no composition gradient. This allows for optimized electrochemical performances by minimizing the stresses that could occur upon cycling during Li deintercalation/intercalation. 
     The XRD pattern shows a single phase material corresponding to NMCA. Use of the Rietveld refinement software Topas allows obtaining the X-ray crystallite size. The crystallite size is related to the peak broadening. A large size means narrow peaks. If the sample has a size dependent composition there will be a distribution of peak positions around the position of the average composition. As a result the Rietveld refinement of a size dependent composition will have a smaller size than that of a fixed (i.e. not dependent on size) composition. The Rietveld refinement of the composition of Example 1 results in a crystallite size of 134 nm. This value is relatively low and indicates—despite of the high synthesis temperature—the coexistence of several slight deviations from the global composition, due to the fact that particles with slightly different composition coexist within the powder. The hexagonal cell parameters as calculated from XRD (full pattern matching refinement) are a=2.864(1) Å and =14.264(8) Å. 
     A slurry is prepared by mixing the NMCA powder of Example 1 with 5% wt carbon black and 5% PVDF into N-Methyl Pyrrolidone (NMP), and is deposited on an Al foil as current collector. The obtained electrode containing 90% wt active material is used to manufacture coin cells with about 14 mg/cm 2  active material. As electrolyte a LiPF 6  based electrolyte is used. The negative electrodes are made of metallic Li. Capacity and rate performance of the coin cells are tested between 3.0 and 4.3V vs Li+/Li, followed by a stability test at 4.5-3.0V.  FIG. 4  shows that a high reversible capacity is obtained upon cycling with a reversible capacity of 143 mAh/g at a discharge rate of C/10 (Cycle 1: full discharge in 10 h). In the figure the voltage is shown against the cathode capacity during 6 consecutive cycles—the discharge capacities of the cycles are shown from right to left for Cycle 1 to Cycle 6.90% of the capacity is retained at a discharge rate of C (Cycle 4: full discharge in 1 h) with 129 mAh/g, and 85% is obtained at a discharge rate of 2 C (Cycle 5: full discharge in ½ h) with 121 mAh/g. 
     For completeness the cycles&#39; discharge rate is listed below:
         Cycle 1: C/10 (1 st  to the right on  FIG. 4 )   Cycle 2: C/5   Cycle 3: C/2   Cycle 4: 1 C   Cycle 5: 2 C   Cycle 6: 3 C (most left on  FIG. 4 ).       

     EXAMPLE 2 
     Counter Example 
     In a first step, an NMCA hydroxide material with molar composition 41.8:35.7:14.1:8.4 is precipitated from Ni, Mn, Co and Al sulphates in the presence of NaOH and Ammonia. The average particle size as measured from laser granulometry is centered around D50=8.5 μm (D10=2.0 μm, D90=18.0 μm). 
     In a second step, the hydroxide is mixed with Li 2 CO 3  such that Li/(Ni+Mn+Co+Al)=1.075. The mixture is then heated in a chamber furnace under ambient air at 980° C. for 10 h. The composition of the obtained Li a Ni x Co y Al z O 2  powder as deduced from ICP is Ni:Mn:Co:Al 42.1:34.5:14.2:9.2. 
     The particle size distribution from the product after firing is measured by laser diffraction granulometry and gives a PSD with D10=2.4 μm, D50=7.8 μm, D90=20.1 μm. The EDS analysis performed on the product of the counter example shows that the composition does not vary substantially with the particle size (see  FIG. 5  &amp; Table 2). It has to be noted that molar concentrations measured using EDS cannot be taken as absolute values and that they can differ slightly from ICP data. However, EDS allows for relative comparison of molar concentrations between different particle sizes. 
     
       
         
               
             
               
               
               
               
               
             
               
               
               
               
               
             
           
               
                 TABLE 2 
               
             
             
               
                   
               
               
                 Molar composition (Ni:Mn:Co:Al) according to particle size. 
               
             
          
           
               
                 Size from SEM 
                 EDS Ni 
                 EDS Mn 
                 EDS Co 
                 EDS Al 
               
               
                 (μm) 
                 (mol %) 
                 (mol %) 
                 (mol %) 
                 (mol %) 
               
               
                   
               
             
          
           
               
                 2 
                 46.6 
                 32.5 
                 15.4 
                 5.5 
               
               
                 4 
                 47.0 
                 31.7 
                 16.0 
                 5.2 
               
               
                 10 
                 45.3 
                 34.9 
                 14.5 
                 5.3 
               
               
                 21 
                 46.6 
                 33.5 
                 15.6 
                 5.1 
               
               
                   
               
             
          
         
       
     
     The figures for particles corresponding to the D10 and D90 values correspond to the ones in Table 2. 
     As can be deduced from  FIG. 5 , there is a no correlation between Ni and Al content (mol %) and particle size as measured from the SEM picture (D). Notwithstanding this, if a trend is calculated, it is as follows:
         for Ni: Ni (mol %)=−0.0575·D+46.717   for Al: Al (mol %)=−0.016·D+5.4376       

     The s and u factor in the equations (mol %=s (or u)·D+t1 (or t2)) being close to 0 confirms that the Ni and Al contents are constant in the powder. 
     The XRD pattern shows a single phase material corresponding to NMCA. Use of the Rietveld refinement software Topas allows to obtain the X-ray crystallite size. The Rietveld refinement of the composition of Example 2 results in a crystallite size of 148 nm. This value is significantly larger than that obtained for the size dependent composition sample described in example 1, which demonstrates that Example 2 has more narrow X-ray peaks. As expected, and in contrast with Example 1, the narrow XRD lines are typical for a product synthesized at high temperature, and suggest that the Ni, Co and Al elements are homogeneously distributed within the powder. The hexagonal cell parameters as calculated from the XRD are a=2.863(4) Å and c=14.247(1) Å. These are considered to be equivalent to those from the product obtained in Example 1—the difference being within the error margin of the cell parameter refinement.  FIG. 6  compares the shape of selected peaks (003, 110 and 018). The sample without size dependent composition is represented by line  2 , with size dependent composition by line  1 . The figure clearly shows the more narrow peaks obtained for the sample without size dependent composition. The sample without size dependent composition shows a lower FWHM and for the 018 &amp; 110 peaks we can see a separation into the K a1  and K a2  doublet, which cannot be distinguished in the size dependent sample. 
     A slurry is prepared by mixing the LNMCO powder obtained according to Example 2 with 5% wt carbon black and 5% PVDF into N-Methyl Pyrrolidone (NMP), and is deposited on an Al foil as current collector. The obtained electrode containing 90% wt active material is used to manufacture coin cells, with about 14 mg/cm 2  active material. As electrolyte a LiPF 6  based electrolyte is used. The negative electrodes are made of metallic Li. Capacity and rate performance of the coin cells are tested between 3.0 and 4.3V vs Li+/Li, followed by a stability test at 4.5-3.0V.  FIG. 7  (with data representation as in  FIG. 4 ) shows that the reversible capacity obtained upon cycling has a reversible capacity of only 135 mAh/g at a discharge rate of C/10. Only 87% of the capacity is retained at a discharge rate of C with 118 mAh/g, and 82% is obtained at a discharge rate of 2 C with 111 mAh/g, i.e. 8% less capacity at high rate than the product according to the invention. This clearly emphasizes the benefit of the invention as compared to state of the art materials regarding power properties of NMCA materials. 
     EXAMPLE 3 
     5 LiNi 0.47 Mn 0.38 Co 0.15 Al x O 2  compounds were prepared with different molar compositions of Al (x=0%, 1.5%, 3%, 5% and 10%) and measured using DSC (differential Scanning calorimetry) to illustrate the positive influence of Al-content on the safety performance. Small electrodes, containing about 3.3 mg of active material are punched and assembled in coin cells. Coin cells are charged to 4.3V using a C/10 charge rate followed by a constant voltage soak for at least 1 h. After disassembly of the coin cells electrodes are repeatedly washed in DMC to remove remaining electrolyte. After evaporating the DMC the electrodes are immersed into stainless steel cans and about 1.2 mg of PVDF based electrolyte is added, following by hermetic closing (crimping) of the cells. The DSC measurement is performed using a TA instrument DSC Q10 device. The DSC scan is performed from 50-350° C. using a heat rate of 5K/min. DSC cells and crimping equipment were also supplied by TA 
     The total energy released by the exothermic decomposition of the electrode material upon heating is given in Table 3. 
     
       
         
               
             
               
               
               
               
               
             
               
               
               
               
               
             
           
               
                 TABLE 3 
               
             
             
               
                   
               
               
                 DSC data on safety performance as a function of Al-content in  
               
               
                 LiNiMnCoAlO 2  cathode material. 
               
             
          
           
               
                   
                 Temperature 
                 Energy 
                 Capacity 
                 Energy released per 
               
               
                 Al (mol %) 
                 at max (° C.) 
                 released (kJ) 
                 (mAh/g) 
                 capacity (kJ g/mAh) 
               
               
                   
               
             
          
           
               
                 0 
                 304.9 
                 1023.8 
                 183.1 
                 5.6 
               
               
                 1.5 
                 301.9 
                 1082 
                 180.6 
                 6.0 
               
               
                 3 
                 311.4 
                 992.8 
                 181.1 
                 5.5 
               
               
                 5 
                 309.4 
                 994.5 
                 177.2 
                 5.6 
               
               
                 10 
                 317.7 
                 859.1 
                 174.1 
                 4.9 
               
               
                   
               
             
          
         
       
     
     As can be seen in Table 3, with increasing Al-content the total energy released decreases and the temperature of max heat flow increases. Especially when going to a sufficiently high Al-content of −10%, the gain in safety performance is substantial as compared to lower Al-contents. This clearly illustrates the advantage of having a size dependent Al-composition and as such proves that the small particles, which are known to be intrinsically less safe, will benefit from a higher Al-content. Furthermore, these data show that the Al content should be sufficiently high and that the difference in Al-content between the big D90 and small D10 particles should be sufficiently big in order to get the maximum gain in safety performance. 
     While specific embodiments and/or details of the invention have been shown and described above to illustrate the application of the principles of the invention, it is understood that this invention may be embodied as more fully described in the claims, or as otherwise known by those skilled in the art (including any and all equivalents), without departing from such principles.