Abstract:
Uses are disclosed for a new crystalline molecular sieve designated SSZ-102 synthesized using an N,N′-dimethyl-1,4-diazabicyclo[2.2.2]octane dication as a structure directing agent. SSZ-102 has ESV framework topology.

Description:
REFERENCE TO RELATED APPLICATIONS 
       [0001]    This application is a divisional application of co-pending U.S. patent application Ser. No. 14/716,784, filed on May 19, 2015, which claims the benefit of U.S. Provisional Patent Application Ser. No. 62/068,541, filed on Oct. 24, 2014, the disclosures of which are incorporated herein by reference in their entirety. 
     
    
     TECHNICAL FIELD 
       [0002]    This disclosure is directed to a new crystalline molecular sieve designated SSZ-102 having ESV framework topology, a method for preparing SSZ-102 using an N,N′-dimethyl-1,4-diazabicyclo[2.2.2]octane dication as a structure directing agent and uses for SSZ-102. 
       BACKGROUND 
       [0003]    Molecular sieves are a commercially important class of crystalline materials. They have distinct crystal structures with ordered pore structures which are demonstrated by distinct X-ray diffraction patterns. The crystal structure defines cavities and pores which are characteristic of the different species. 
         [0004]    Molecular sieves are classified by the Structure Commission of the International Zeolite Association according to the rules of the IUPAC Commission on Zeolite Nomenclature. According to this classification, framework type zeolites and other crystalline microporous molecular sieves, for which a structure has been established, are assigned a three letter code and are described in the “ Atlas of Zeolite Framework Types ,” Sixth Revised Edition, Elsevier, 2007. 
         [0005]    ERS-7 is a single crystalline phase zeolite having a structure consisting of 17-sided (4 6 5 4 6 5 8 2 ) “picnic basket”-shaped cages connected by 8-membered ring windows with 4.7×3.5 Å free dimensions. The framework structure of ERS-7 has been assigned the three-letter code ESV by the Structure Commission of the International Zeolite Association. 
         [0006]    Italian Patent No. 1270630 discloses zeolite ERS-7 and its synthesis using an N,N-dimethylpiperidinium cation as a structure directing agent. ERS-7 is reported to have a SiO 2 /Al 2 O 3  mole ratio between 15 and 30. 
         [0007]    It has now been found that crystalline molecular sieves having ESV framework topology and having a SiO 2 /Al 2 O 3  mole ratio of from 5 to 12 can be prepared using an N,N′-dimethyl-1,4-diazabicyclo[2.2.2]octane cation as a structure directing agent. 
       SUMMARY 
       [0008]    This disclosure is directed to a family of crystalline molecular sieves with unique properties, referred to herein as “molecular sieve SSZ-102” or simply “SSZ-102”. SSZ-102 has the framework topology designated “ESV” by the International Zeolite Association. 
         [0009]    In one aspect, there is provided a crystalline molecular sieve having ESV framework topology and having a SiO 2 /Al 2 O 3  mole ratio of from 5 to 12. Molecular sieve SSZ-102 has, in its calcined form, the X-ray diffraction lines of Table 4. 
         [0010]    In another aspect, there is provided a method for preparing a crystalline molecular sieve having ESV framework topology by contacting under crystallization conditions: (1) at least one source of silicon; (2) at least one source of aluminum; (3) at least one source of an element selected from Groups 1 and 2 of the Periodic Table; (4) hydroxide ions; and (5) N,N′-dimethyl-1,4-diazabicyclo[2.2.2]octane dications. 
         [0011]    In yet another aspect, there is provided a process for preparing a molecular sieve having ESV framework topology by: (a) preparing a reaction mixture containing: (1) at least one source of silicon; (2) at least one source of aluminum; (3) at least one source of an element selected from Groups 1 and 2 of the Periodic Table; (4) hydroxide ions; (5) N,N′-dimethyl-1,4-diazabicyclo[2.2.2]octane dications; and (6) water; and (b) subjecting the reaction mixture to crystallization conditions sufficient to form crystals of the molecular sieve. 
         [0012]    In still yet another aspect, there is provided a crystalline molecular sieve having ESV framework topology and having a composition, as-synthesized and in its anhydrous state, in terms of mole ratios, as follows: 
         [0000]                                                              Broad   Exemplary                                        SiO 2 /Al 2 O 3      5 to 12    5 to 10           Q/SiO 2     0.015 to 0.15   0.04 to 0.10           M/SiO 2     0.010 to 0.20   0.05 to 0.20                        
wherein Q is an N,N′-dimethyl-1,4-diazabicyclo[2.2.2]octane dication and M is selected from the group consisting of elements from Groups 1 and 2 of the Periodic Table.
 
         [0013]    There are also disclosed herein processes using crystalline molecular sieves having ESV framework topology and having a SiO 2 /Al 2 O 3  mole ratio of from 5 to 12. 
     
    
     
       BRIEF DESCRIPTION OF THE DRAWINGS 
         [0014]      FIG. 1  is a powder X-ray diffraction (XRD) pattern of the as-synthesized molecular sieve prepared in Example 1. 
           [0015]      FIG. 2  is a Scanning Electron Micrograph (SEM) image of the as-synthesized molecular sieve prepared in Example 1. 
           [0016]      FIG. 3  shows a comparison of two X-ray diffraction patterns, the top one being calcined SSZ-102 as prepared in Example 10 and the bottom one being as-synthesized SSZ-102 as prepared in Example 1. 
       
    
    
     DETAILED DESCRIPTION 
       [0017]    Reaction Mixture 
         [0018]    In preparing SSZ-102, an N,N′-dimethyl-1,4-diazabicyclo[2.2.2]octane dication (“dimethyl DABCO dication”) is used as a structure directing agent (“SDA”), also known as a crystallization template. The SDA useful for making the molecular sieve is represented by the following structure (1): 
         [0000]    
       
                 
         
             
             
         
       
       
         
           
             N,N′-dimethyl-1,4-diazabicyclo[2.2.2]octane dication 
           
         
       
     
         [0020]    SDA dication is typically associated with anions which can be any anion which is not detrimental to the formation of the molecular sieve. Representative anions include elements from Group 17 of the Periodic Table (e.g., fluoride, chloride, bromide and iodide), hydroxide, sulfate, tetrafluoroborate, acetate, carboxylate, and the like. As used herein, the numbering scheme for the Periodic Table Groups is as described in  Chem. Eng. News  63(5), 26-27 (1985). 
         [0021]    In general, molecular sieve SSZ-102 is prepared by: (a) preparing a reaction mixture containing (1) at least one source of silicon; (2) at least one source of aluminum; (3) at least one source of an element selected from Groups 1 and 2 of the Periodic Table; (4) hydroxide ions; (5) N,N′-dimethyl-1,4-diazabicyclo[2.2.2]octane dications; and (6) water; and (b) subjecting the reaction mixture to crystallization conditions sufficient to form crystals of the molecular sieve. 
         [0022]    The composition of the reaction mixture from which the molecular sieve is formed, in terms of mole ratios, is identified in Table 1 below: 
         [0000]                                    TABLE 1                       Reactants   Broad   Exemplary                           SiO 2 /Al 2 O 3      5 to 50   10 to 30           M/SiO 2     0.10 to 1.00   0.40 to 0.90           Q/SiO 2     0.05 to 0.50   0.15 to 0.35           OH/SiO 2     0.10 to 1.20   0.70 to 1.20           H 2 O/SiO 2     10 to 70   15 to 35                        
wherein compositional variables M and Q are as described herein above.
 
         [0023]    Sources useful herein for silicon include fumed silica, precipitated silicates, silica hydrogel, silicic acid, colloidal silica, tetra-alkyl orthosilicates (e.g., tetraethyl orthosilicate), and silica hydroxides. 
         [0024]    Sources useful for aluminum include oxides, hydroxides, acetates, oxalates, ammonium salts and sulfates of aluminum. Typical sources of aluminum oxide include aluminates, alumina, and aluminum compounds such as AlCl 3 , Al 2 (SO 4 ) 3 , Al(OH) 3 , kaolin clays, and other zeolites. An example of the source of aluminum oxide is zeolite Y. 
         [0025]    For each embodiment described herein, the molecular sieve reaction mixture can be supplied by more than one source. Also, two or more reaction components can be provided by one source. 
         [0026]    The reaction mixture can be prepared either batch wise or continuously. Crystal size, morphology and crystallization time of the molecular sieve described herein can vary with the nature of the reaction mixture and the synthesis conditions. 
         [0027]    Crystallization and Post-Synthesis Treatment 
         [0028]    In practice, molecular sieve SSZ-102 is prepared by: (a) preparing a reaction mixture as described herein above; and (b) subjecting the reaction mixture to crystallization conditions sufficient to form crystals of the molecular sieve. 
         [0029]    The reaction mixture is maintained at an elevated temperature until the molecular sieve is formed. The hydrothermal crystallization is usually conducted under pressure and usually in an autoclave so that the reaction mixture is subject to autogenous pressure, at a temperature of from 125° C. to 200° C. 
         [0030]    The reaction mixture can be subjected to mild stirring or agitation during the crystallization step. It will be understood by the skilled artisan that the molecular sieves described herein can contain impurities, such as amorphous materials, unit cells having framework topologies which do not coincide with the molecular sieve, and/or other impurities. 
         [0031]    During the hydrothermal crystallization step, the molecular sieve crystals can be allowed to nucleate spontaneously from the reaction mixture. The use of crystals of the molecular sieve as seed material can be advantageous in decreasing the time necessary for complete crystallization to occur. In addition, seeding can lead to an increased purity of the product obtained by promoting nucleation and/or formation of the molecular sieve over any undesired phases. When used as seeds, seed crystals are added in an amount of from 1 to 10 wt. % of the source of silicon used for the reaction mixture. 
         [0032]    Once the molecular sieve has formed, the solid product is separated from the reaction mixture by standard mechanical techniques such as filtration. The crystals are water-washed and then dried to obtain the as-synthesized molecular sieve crystals. The drying step can be performed at atmospheric pressure or under vacuum. 
         [0033]    The molecular sieve can be used as-synthesized, but typically will be thermally treated (calcined). The term “as-synthesized” refers to the molecular sieve in its form after crystallization, prior to removal of the SDA cation. The SDA cation can be removed by thermal treatment (e.g., calcination), preferably in an oxidative atmosphere (e.g., air, gas with an oxygen partial pressure of greater than 0 kPa) at a temperature readily determinable by the skilled artisan sufficient to remove the SDA from the molecular sieve. The SDA can also be removed by photolysis techniques (e.g., exposing the SDA-containing molecular sieve product to light or electromagnetic radiation that has a wavelength shorter than visible light under conditions sufficient to selectively remove the organic matter from the molecular sieve) as described in U.S. Pat. No. 6,960,327. 
         [0034]    The molecular sieve can subsequently be calcined in steam, air or inert gas at temperatures ranging from 200° C. to 800° C. for periods of time ranging from 1 to 48 hours, or more. Usually, it is desirable to remove the extra-framework cation (e.g., Na + ) by ion exchange or other known method and replace it with hydrogen, ammonium, or any desired metal ion. 
         [0035]    Where the molecular sieve formed is an intermediate material, the target molecular sieve can be achieved using post-synthesis techniques to allow for the synthesis of a target material having a higher Si/Al ratio from an intermediate material by acid leaching or other similar dealumination methods. 
         [0036]    The molecular sieve made by the process described herein can be formed into a wide variety of physical shapes. Generally speaking, the molecular sieve can be in the form of a powder, a granule, or a molded product, such as extrudate having a particle size sufficient to pass through a 2-mesh (Tyler) screen and be retained on a 400-mesh (Tyler) screen. In cases where the catalyst is molded, such as by extrusion with an organic binder, the molecular sieve can be extruded before drying or dried or partially dried and then extruded. 
         [0037]    The molecular sieve can be composited with other materials resistant to the temperatures and other conditions employed organic conversion processes. Such matrix materials include active and inactive materials and synthetic or naturally occurring zeolites as well as inorganic materials such as clays, silica and metal oxides. Examples of such materials and the manner in which they can be used are disclosed in U.S. Pat. Nos. 4,910,006 and 5,316,753. 
         [0038]    Characterization of the Molecular Sieve 
         [0039]    Molecular sieves synthesized by the process described herein have a composition, as-synthesized and in its anhydrous state, as described in Table 2 (in terms of mole ratios): 
         [0000]                                                  TABLE 2                       Broad   Exemplary                                        SiO 2 /Al 2 O 3      5 to 12    5 to 10           Q/SiO 2     0.015 to 0.15   0.04 to 0.10           M/SiO 2     0.010 to 0.20   0.05 to 0.20                        
wherein compositional variables Q and M are as described herein above.
 
         [0040]    Molecular sieves made by the process disclosed herein are characterized by their XRD pattern. The powder XRD pattern lines of Table 3 are representative of as-synthesized SSZ-102 made in accordance with this disclosure. Minor variations in the powder XRD pattern can result from variations in the mole ratios of the framework species of the particular sample due to changes in lattice constants. In addition, sufficiently small crystals will affect the shape and intensity of peaks, leading to significant peak broadening. Minor variations in the powder XRD pattern can also result from variations in the organic compound used in the preparation of the molecular sieve. Calcination can also cause minor shifts in the powder XRD pattern. Notwithstanding these minor pertubations, the basic crystal lattice structure remains unchanged. 
         [0000]    
       
         
               
             
               
               
               
             
               
               
               
             
           
               
                 TABLE 3 
               
             
             
               
                   
               
               
                 Characteristic Peaks for As-Synthesized SSZ-102 
               
             
          
           
               
                 2-Theta (a)   
                 d-Spacing, nm 
                 Relative Intensity (b)   
               
               
                   
               
             
          
           
               
                 7.53 
                 1.173 
                 W 
               
               
                 7.93 
                 1.115 
                 W 
               
               
                 9.64 
                 0.916 
                 W 
               
               
                 11.91 
                 0.743 
                 W 
               
               
                 13.38 
                 0.661 
                 M 
               
               
                 13.64 
                 0.649 
                 M 
               
               
                 14.06 
                 0.630 
                 M 
               
               
                 14.46 
                 0.612 
                 W 
               
               
                 15.27 
                 0.580 
                 W 
               
               
                 15.82 
                 0.560 
                 W 
               
               
                 16.00 
                 0.554 
                 M 
               
               
                 17.08 
                 0.519 
                 M 
               
               
                 17.87 
                 0.496 
                 W 
               
               
                 18.30 
                 0.484 
                 W 
               
               
                 19.04 
                 0.466 
                 VS 
               
               
                 19.16 
                 0.463 
                 M 
               
               
                 19.56 
                 0.453 
                 S 
               
               
                 20.36 
                 0.436 
                 W 
               
               
                 20.75 
                 0.428 
                 W 
               
               
                 21.09 
                 0.421 
                 M 
               
               
                 21.25 
                 0.418 
                 M 
               
               
                   
               
               
                   (a) ±0.20 degrees 
               
               
                   (b) The powder XRD patterns provided are based on a relative intensity scale in which the strongest line in the X-ray diffraction pattern is assigned a value of 100: W = weak (&gt;0 to ≦20); M = medium (&gt;20 to ≦40); S = strong (&gt;40 to ≦60); VS = very strong (&gt;60 to ≦100). 
               
             
          
         
       
     
         [0041]    The X-ray diffraction lines of Table 4 are representative of calcined SSZ-102 made in accordance with this disclosure. 
         [0000]    
       
         
               
             
               
               
               
             
               
               
               
             
           
               
                 TABLE 4 
               
             
             
               
                   
               
               
                 Characteristic Peaks for Calcined SSZ-102 
               
             
          
           
               
                 2-Theta (a)   
                 d-Spacing, nm 
                 Relative Intensity (b)   
               
               
                   
               
             
          
           
               
                 7.60 
                 1.162 
                 W 
               
               
                 8.01 
                 1.103 
                 M 
               
               
                 9.74 
                 0.908 
                 M 
               
               
                 12.02 
                 0.736 
                 M 
               
               
                 13.44 
                 0.658 
                 VS 
               
               
                 13.70 
                 0.646 
                 VS 
               
               
                 14.11 
                 0.627 
                 VS 
               
               
                 14.56 
                 0.608 
                 W 
               
               
                 15.30 
                 0.579 
                 W 
               
               
                 15.87 
                 0.558 
                 W 
               
               
                 16.20 
                 0.547 
                 W 
               
               
                 17.16 
                 0.516 
                 W 
               
               
                 17.96 
                 0.493 
                 W 
               
               
                 18.38 
                 0.482 
                 W 
               
               
                 19.12 
                 0.464 
                 VS 
               
               
                 19.31 
                 0.459 
                 VS 
               
               
                 19.70 
                 0.450 
                 S 
               
               
                 20.39 
                 0.435 
                 W 
               
               
                 20.89 
                 0.425 
                 W 
               
               
                 21.16 
                 0.419 
                 M 
               
               
                 21.34 
                 0.416 
                 M 
               
               
                   
               
               
                   (a) ±0.20 degrees 
               
               
                   (b) The powder XRD patterns provided are based on a relative intensity scale in which the strongest line in the X-ray diffraction pattern is assigned a value of 100: W = weak (&gt;0 to ≦20); M = medium (&gt;20 to ≦40); S = strong (&gt;40 to ≦60); VS = very strong (&gt;60 to ≦100). 
               
             
          
         
       
     
         [0042]    The powder XRD patterns presented herein were collected by standard techniques. The radiation was CuK α  radiation. The peak heights and the positions, as a function of 2θ where 2θ is the Bragg angle, were read from the relative intensities of the peaks, and d, the interplanar spacing corresponding to the recorded lines, can be calculated. 
         [0043]    Processes Using SSZ-102 
         [0044]    SSZ-102 is useful as an adsorbent for gas separations. SSZ-102 can also be used as a catalyst for converting oxygenates (e.g., methanol) to olefins and for making small amines. SSZ-102 can be used to reduce oxides of nitrogen in a gas streams, such as automobile exhaust. SSZ-102 can also be used to as a cold start hydrocarbon trap in combustion engine pollution control systems. SSZ-102 is particularly useful for trapping C3 fragments. 
         [0045]    Gas Separation 
         [0046]    SSZ-102 can be used to separate gases. For example, it can be used to separate carbon dioxide from natural gas. Typically, the molecular sieve is used as a component in a membrane that is used to separate the gases. Examples of such membranes are disclosed in U. S. Pat. No. 6,508,860. 
         [0047]    Oxygenate Conversion 
         [0048]    The present disclosure comprises a process for catalytic conversion of a feedstock comprising one or more oxygenates comprising alcohols and ethers to a hydrocarbon product containing light olefins, e.g.., C 2 , C 3  and/or C 4  olefins. The feedstock is contacted with SSZ-102 at effective process conditions to produce light olefins. The term “oxygenate” as used herein designates compounds such as alcohols, ethers, and carbonyl compounds (e.g., aldehydes, ketones, carboxylic acids). The oxygenate can contain from 1 to 10 carbon atoms, e.g., from 1 to 4 carbon atoms. The representative oxygenates include lower straight chained branched alcohols, and their unsaturated counterparts. Particularly suitable oxygenate compounds are methanol, dimethyl ether, and mixtures thereof. 
         [0049]    The process disclosed can be conducted in the presence of one or more diluents which can be present in the oxygenate feed in an amount of from 1 to 99 mole %, based on the total number of moles of all feed and diluent components. Diluents include helium, argon, nitrogen, carbon monoxide, carbon dioxide, hydrogen, water, paraffins, hydrocarbons (such as methane and the like), aromatic compounds, or mixtures thereof. U.S. Pat. Nos. 4,677,242; 4,861,938; and 4,677,242 emphasize the use of a diluent to maintain catalyst selectivity toward the production of light olefins, particularly ethylene. 
         [0050]    The oxygenate conversion is desirably conducted in the vapor phase such that the oxygenate feedstock is contacted in a vapor phase in a reaction zone with SSZ-102 at effective process conditions to produce hydrocarbons, i.e., an effective temperature, pressure, WHSV and, optionally, an effective amount of diluent. The process is conducted for a period of time sufficient to produce the desired light olefins. In general, the residence time employed to produce the desired product can vary from seconds to a number of hours. It will be readily appreciated that the residence time will be determined to a significant extent by the reaction temperature, the molecular sieve catalyst, the WHSV, the phase (liquid or vapor) and process design characteristics. The oxygenate feedstock flow rate affects olefin production. Increasing the feedstock flow rate increases WHSV and enhances the formation of olefin production relative to paraffin production. However, the enhanced olefin production relative to paraffin production is offset by a diminished conversion of oxygenate to hydrocarbons. 
         [0051]    Light olefin products will form, although not necessarily in optimum amounts, at a wide range of pressures, including but not limited to autogenous pressures and pressures in the range of from 0.1 kPa to 10 MPa. Conveniently, the pressure can be in the range of from 7 kPa to 5 MPa, e.g., from 50 kPa to 1 MPa. The foregoing pressures are exclusive of diluents, if any are present, and refer to the partial pressure of the feedstock as it relates to oxygenate compounds and/or mixtures thereof. Lower and upper extremes of pressure can adversely affect selectivity, conversion, coking rate, and/or reaction rate; however, light olefins such as ethylene and/or propylene still may form. 
         [0052]    The temperature which can be employed in the oxygenate conversion process can vary over a wide range depending, at least in part, on the molecular sieve catalyst. In general, the process can be conducted at an effective temperature of from 200° C. to 700° C. At the lower ends of the temperature range, and thus generally at a lower rate of reaction, the formation of the desired light olefins can become low. At the upper ends of the range, the process may not form an optimum amount of light olefins and catalyst deactivation can be rapid. 
         [0053]    The molecular sieve catalyst can be incorporated into solid particles in which the catalyst is present in an amount effective to promote the desired conversion of oxygenates to light olefins. In one aspect, the solid particles comprise a catalytically effective amount of the catalyst and at least one matrix material selected from the group consisting of binder materials, filler materials and mixtures thereof to provide a desired property or properties, e.g., desired catalyst dilution, mechanical strength and the like to the solid particles. Such matrix materials are often, to some extent, porous in nature and may or may not be effective to promote the desired reaction. Filler and binder materials include, for example, synthetic and naturally occurring substances such as metal oxides, clays, silicas, aluminas, silica-aluminas, silica-magnesias, silica-zirconias, silica-thorias and the like. If matrix materials are included in the catalyst composition, the molecular sieve desirably comprises from 1 to 99 wt. % (e.g., from 5 to 90 wt. % or from 10 to 80 wt. %) of the total composition. 
         [0054]    Synthesis of Amines 
         [0055]    SSZ-102 can be used in a catalyst to prepare methylamine or dimethylamine. Dimethylamine is generally prepared in industrial quantities by continuous reaction of methanol (and/or dimethyl ether) and ammonia in the presence of a silica-alumina catalyst. The reactants are typically combined in the vapor phase, at temperatures of from 300° C. to 500° C., and at elevated pressures. Such a process is disclosed in U.S. Pat. No. 4,737,592. 
         [0056]    The catalyst is used in its acid form. Acid forms of molecular sieves can be prepared by a variety of techniques. Desirably, the molecular sieve used to prepare dimethylamine will be in the hydrogen form, or have an alkali or alkaline earth metal, such as Na, K, Rb, or Cs, ion-exchanged into it. 
         [0057]    The process disclosed herein involves reacting methanol, dimethyl ether, or a mixture thereof and ammonia in amounts sufficient to provide a carbon/nitrogen (C/N) ratio of from 0.2 to 1.5, e.g., from 0.5 to 1.2. The reaction is conducted at a temperature of from 250° C. to 450° C., e.g., from 300° C. to 400° C. Reaction pressures can vary from 7 to 7000 kPa, e.g., from 70 to 3000 kPa. A methanol and/or dimethyl ether space time of from 0.01 to 80 h −1  (e.g., from 0.10 to 1.5 h −1 ) is typically used. This space time is calculated as the mass of catalyst divided by the mass flow rate of methanol/dimethyl ether introduced into the reactor. 
         [0058]    Reduction of Oxides of Nitrogen 
         [0059]    SSZ-102 can be used for the catalytic reduction of the oxides of nitrogen in a gas stream. Typically, the gas stream also contains oxygen, often a stoichiometric excess thereof. Also, the molecular sieve can contain a metal or metal ions within or on it which are capable of catalyzing the reduction of the nitrogen oxides. Examples of such metals or metal ions include lanthanum, chromium, manganese, iron, cobalt, rhodium, nickel, palladium, platinum, copper, zinc, and mixtures thereof. 
         [0060]    One example of such a process for the catalytic reduction of oxides of nitrogen in the presence of a zeolite is disclosed in U.S. Pat. No. 4,297,328. There, the catalytic process is the combustion of carbon monoxide and hydrocarbons and the catalytic reduction of the oxides of nitrogen contained in a gas stream, such as the exhaust gas from an internal combustion engine. The zeolite used is metal ion-exchanged, doped or loaded sufficiently so as to provide an effective amount of catalytic copper metal or copper ions within or on the zeolite. In addition, the process is conducted in an excess of oxidant, e.g., oxygen. 
         [0061]    Treatment of Engine Exhaust (Cold Start Emissions) 
         [0062]    Gaseous waste products resulting from the combustion of hydrocarbon fuels, such as gasoline and fuel oils, comprise carbon monoxide, hydrocarbons and nitrogen oxides as products of combustion or incomplete combustion, and can pose a serious health problem with respect to pollution of the atmosphere. While exhaust gases from other carbonaceous fuel-burning sources, such as stationary engines, industrial furnaces, etc., contribute substantially to air pollution, the exhaust gases from automotive engines are a principal source of pollution. Because of these concerns, the U.S. Environmental Protection Agency has promulgated strict controls on the amounts of carbon monoxide, hydrocarbons and nitrogen oxides which automobiles can emit. The implementation of these controls has resulted in the use of catalytic converters to reduce the amount of pollutants emitted from automobiles. 
         [0063]    In order to achieve the simultaneous conversion of carbon monoxide, hydrocarbon and nitrogen oxide pollutants, it has become the practice to employ catalysts in conjunction with air-to-fuel ratio control means which functions in response to a feedback signal from an oxygen sensor in the engine exhaust system. Although these three component control catalysts work quite well after they have reached operating temperature of about 300° C., at lower temperatures they are not able to convert substantial amounts of the pollutants. What this means is that when an engine and in particular an automobile engine is started up, the three component control catalyst is not able to convert the hydrocarbons and other pollutants to innocuous compounds. 
         [0064]    Adsorbent beds have been used to adsorb the hydrocarbons during the cold start portion of the engine. Although the process typically will be used with hydrocarbon fuels, the instant invention can also be used to treat exhaust streams from alcohol-fueled engines. The adsorbent bed is typically placed immediately before the catalyst. Thus, the exhaust stream is first flowed through the adsorbent bed and then through the catalyst. The adsorbent bed preferentially adsorbs hydrocarbons over water under the conditions present in the exhaust stream. After a certain amount of time, the adsorbent bed has reached a temperature (typically about 150° C.) at which the bed is no longer able to remove hydrocarbons from the exhaust stream. That is, hydrocarbons are actually desorbed from the adsorbent bed instead of being adsorbed. This regenerates the adsorbent bed so that it can adsorb hydrocarbons during a subsequent cold start. The use of adsorbent beds to minimize hydrocarbon emissions during a cold start engine operation is known in the art. See, for example, U.S. Pat. Nos. 2,942,932; 3,699,683; and 5,078,979. 
         [0065]    As stated, this disclosure generally relates to a process for treating an engine exhaust stream and, in particular, to a process for minimizing emissions during the cold start operation of an engine. The engine consists of any internal or external combustion engine which generates an exhaust gas stream containing noxious components or pollutants including unburned or thermally degraded hydrocarbons or similar organics. Other noxious components usually present in the exhaust gas include nitrogen oxides and carbon monoxide. The engine can be fueled by a hydrocarbon fuel. As used herein, the term “hydrocarbon fuel” includes hydrocarbons, alcohols and mixtures thereof. Examples of hydrocarbons which can be used to fuel the engine are the mixtures of hydrocarbons which make up gasoline or diesel fuel. The alcohols which can be used to fuel engines include ethanol and methanol. Mixtures of alcohols and mixtures of alcohols and hydrocarbons can also be used. The engine can be a jet engine, gas turbine, internal combustion engine, such as an automobile, truck or bus engine, a diesel engine or the like. The process of this disclosure is particularly suited for an internal combustion engine mounted in an automobile. 
         [0066]    When the engine is started up, it produces a relatively high concentration of hydrocarbons in the engine exhaust gas stream as well as other pollutants. Pollutants will be used herein to collectively refer to any unburned fuel components and combustion byproducts found in the exhaust stream. For example, when the fuel is a hydrocarbon fuel, hydrocarbons, nitrogen oxides, carbon monoxide and other combustion byproducts will be found in the engine exhaust gas stream. The temperature of this engine exhaust stream is relatively cool, generally below 500° C. and typically in the range of from 200° C. to 400° C. This engine exhaust stream has the above characteristics during the initial period of engine operation, typically for the first 30 to 120 seconds after startup of a cold engine. The engine exhaust stream will typically contain from 500 to 1000 ppm hydrocarbons by volume. 
         [0067]    The engine exhaust gas stream which is to be treated is flowed over a molecular sieve bed comprising molecular sieve SSZ-102 as a first exhaust stream. The first exhaust stream which is discharged from the molecular sieve bed is now flowed over a catalyst to convert the pollutants contained in the first exhaust stream to innocuous components and provide a treated exhaust stream which is discharged into the atmosphere. It is understood that prior to discharge into the atmosphere, the treated exhaust stream can be flowed through a muffler or other sound reduction apparatus well known in the art. 
         [0068]    In one embodiment, the engine exhaust gas stream which is to be treated is flowed over a combination of molecular sieves which preferentially adsorbs the hydrocarbons over water to provide a first exhaust stream, and flowing the first exhaust gas stream over a catalyst to convert any residual hydrocarbons and other pollutants contained in the first exhaust gas stream to innocuous products and provide a treated exhaust stream and discharging the treated exhaust stream into the atmosphere. The combination of molecular sieves includes SSZ-102 in combination with: (1) a small pore crystalline molecular sieve or mixture of molecular sieves having pores no larger than 8-membered rings selected from the group consisting of SSZ-13, SSZ-16, SSZ-36, SSZ-39, SSZ-50, SSZ-52 and SSZ-73 and having a mote ratio of at least 10 of (a) at least one oxide of at least one tetravalent element to (b) one or more oxides selected from the group consisting of oxides of trivalent elements, pentavalent elements, and mixtures thereof; and/or (2) a large pore crystalline molecular sieve having pores at least as large as 10-membered rings selected from the group consisting of SSZ-26, SSZ-33, SSZ-64, zeolite Beta, CIT-1 , CIT-6 and ITQ-4 and having a mole ratio of at least 10 of (a) at least one oxide of at least one tetravalent element to (b) one or more oxides selected from the group consisting of oxides of trivalent elements, pentavalent elements, and mixtures thereof. 
         [0069]    The catalyst which is used to convert the pollutants to innocuous components is usually referred to in the art as a three-component control catalyst because it can simultaneously oxidize any residual hydrocarbons present in the first exhaust stream to carbon dioxide and water, oxidize any residual carbon monoxide to carbon dioxide and reduce any residual nitric oxide to nitrogen and oxygen. In some cases, the catalyst cannot be required to convert nitric oxide to nitrogen and oxygen, e.g., when an alcohol is used as the fuel. In this case, the catalyst is called an oxidation catalyst. Because of the relatively low temperature of the engine exhaust stream and the first exhaust stream, this catalyst does not function at a very high efficiency, thereby necessitating the molecular sieve bed. 
         [0070]    When the molecular sieve bed reaches a sufficient temperature, typically from 150° C. to 200° C., the pollutants which are adsorbed in the bed begin to desorb and are carried by the first exhaust stream over the catalyst. At this point, the catalyst has reached its operating temperature and is therefore capable of fully converting the pollutants to innocuous components. 
         [0071]    The adsorbent bed used in this disclosure can be conveniently employed in particulate form or the adsorbent can be deposited onto a solid monolithic carrier. When particulate form is desired, the adsorbent can be formed into shapes such as pills, pellets, granules, rings, spheres, etc. In the employment of a monolithic form, it is usually most convenient to employ the adsorbent as a thin film or coating deposited on an inert carrier material which provides the structural support for the adsorbent. The inert carrier material can be any refractory material such as ceramic or metallic materials. It is desirable that the carrier material be unreactive with the adsorbent and not be degraded by the gas to which it is exposed. Examples of suitable ceramic materials include sillimanite, petalite, cordierite, mullite, zircon, zircon mullite, spondumene, alumina-titanate, etc. Additionally, metallic materials which are within the scope of this disclosure include metals and alloys as disclosed in U.S. Pat. No. 3,920,583 which are oxidation resistant and are otherwise capable of withstanding high temperatures. 
         [0072]    The carrier material can best be utilized in any rigid unitary configuration which provides a plurality of pores or channels extending in the direction of gas flow. The configuration can be a honeycomb configuration. The honeycomb structure can be used advantageously in either unitary form, or as an arrangement of multiple modules. The honeycomb structure is usually oriented such that gas flow is generally in the same direction as the cells or channels of the honeycomb structure. For a more detailed discussion of monolithic structures, see U.S. Pat. Nos. 3,767,453 and 3,785,998. 
         [0073]    The molecular sieve is deposited onto the carrier by any convenient way well known in the art. A desirable method involves preparing a slurry using the molecular sieve and coating the monolithic honeycomb carrier with the slurry. The slurry can be prepared by means known in the art such as combining the appropriate amount of the molecular sieve and a binder with water. This mixture is then blended by using means such as sonication, milling, etc. This slurry is used to coat a monolithic honeycomb by dipping the honeycomb into the slurry, removing the excess slurry by draining or blowing out the channels, and heating to about 100° C. If the desired loading of molecular sieve is not achieved, the above process can be repeated as many times as required to achieve the desired loading. 
         [0074]    Instead of depositing the molecular sieve onto a monolithic honeycomb structure, the molecular sieve can be formed into a monolithic honeycomb structure by means known in the art. 
         [0075]    The adsorbent can optionally contain one or more catalytic metals dispersed thereon. The metals which can be dispersed on the adsorbent are the noble metals which consist of ruthenium, rhodium, palladium, platinum, and mixtures thereof. The desired noble metal can be deposited onto the adsorbent, which acts as a support, in any suitable manner well known in the art. One example of a method of dispersing the noble metal onto the adsorbent support involves impregnating the adsorbent support with an aqueous solution of a decomposable compound of the desired noble metal or metals, drying the adsorbent which has the noble metal compound dispersed on it and then calcining in air at a temperature of 400° C. to 500° C. for a time of from 1 to 4 hours. By “decomposable compound” is meant a compound which upon heating in air gives the metal or metal oxide. Examples of the decomposable compounds which can be used are set forth in U.S. Pat. No. 4,791,091. Examples of decomposable compounds are chloroplatinic acid, rhodium trichloride, chloropalladic acid, hexachloroiridate(IV) acid and hexachlororuthenate(IV). It is typical that the noble metal be present in an amount ranging from 0.01 to 4 wt. % of the adsorbent support. Specifically, in the case of platinum and palladium the range is from 0.1 to 4 wt. %, while in the case of rhodium and ruthenium the range is from 0.01 to 2 wt. %. 
         [0076]    These catalytic metals are capable of oxidizing the hydrocarbon and carbon monoxide and reducing the nitric oxide components to innocuous products. Accordingly, the adsorbent bed can act both as an adsorbent and as a catalyst. 
         [0077]    The catalyst which is used in this disclosure is selected from any three component control or oxidation catalyst well known in the art. Examples of catalysts are those described in U.S. Pat. Nos. 4,528,279; 4,760,044; 4,791,091; 4,868,148; and 4,868,149. Desirable catalysts well known in the art are those that contain platinum and rhodium and optionally palladium, while oxidation catalysts usually do not contain rhodium. Oxidation catalysts usually contain platinum and/or palladium metal. These catalysts can also contain promoters and stabilizers such as barium, cerium, lanthanum, nickel, and iron. The noble metals promoters and stabilizers are usually deposited on a support such as alumina, silica, titania, zirconia, aluminosilicates, and mixtures thereof with alumina being desirable. The catalyst can be conveniently employed in particulate form or the catalytic composite can be deposited on a solid monolithic carrier with a monolithic carrier being desirable. The particulate form and monolithic form of the catalyst are prepared as described for the adsorbent above. The molecular sieve used in the adsorbent bed is SSZ-102. 
       EXAMPLES 
       [0078]    The following illustrative examples are intended to be non-limiting. 
       Example 1 
       [0079]    0.45 g of a 50% NaOH solution, 2.28 g of deionized water, and 0.50 g of CBV720 Y-zeolite powder (Zeolyst International, SiO 2 /Al 2 O 3  mole ratio=30) were mixed together in a Teflon liner. Then, 1.08 g of a 19% dimethyl DABCO hydroxide solution was added to the mixture. The Teflon liner was then capped and placed within a steel Parr autoclave. The autoclave was placed on a spit within a convection oven and heated at 135° C. for 4 days. The autoclave was removed and allowed to cool to room temperature. The solids were then recovered by filtration, washed thoroughly with deionized water and dried at 95° C. 
         [0080]    The resulting molecular sieve product was analyzed by powder XRD and SEM. The resulting powder XRD pattern is shown in  FIG. 1  and indicates that the product is a pure ESV framework type molecular sieve.  FIG. 2  is a SEM image of the product and shows a uniform field of crystals. 
         [0081]    The product had a SiO 2 /Al 2 O 3  mole ratio of 7.67, as determined by ICP elemental analysis. 
       Example 2 
       [0082]    0.87 g of a 50% NaOH solution, 6.87 g of deionized water, and 1.00 g of CBV720 Y-zeolite powder (Zeolyst International, SiO 2 /Al 2 O 3  mole ratio=30) were mixed together in a Teflon liner. Then, 2.18 g of a 19% dimethyl DABCO hydroxide solution was added to the mixture. The Teflon liner was then capped and placed within a steel Parr autoclave. The autoclave was placed on a spit within a convection oven and heated at 150° C. for 4 days. The autoclave was removed and allowed to cool to room temperature. The solids were then recovered by filtration, washed thoroughly with deionized water and dried at 95° C. 
         [0083]    The product of this preparation was identified by powder XRD analysis as a pure ESV framework type molecular sieve. 
         [0084]    The product had a SiO 2 /Al 2 O 3  mole ratio of 8.74, as determined by ICP elemental analysis. 
       Example 3 
       [0085]    0.50 g of a 50% NaOH solution, 4.50 g of deionized water, and 0.50 g of CBV720 Y-zeolite powder (Zeolyst International, SiO 2 /Al 2 O 3  mole ratio=30) were mixed together in a Teflon liner. Then, 1.10 g of a 19% dimethyl DABCO hydroxide solution was added to the mixture. The Teflon liner was then capped and placed within a steel Parr autoclave. The autoclave was placed on a spit within a convection oven and heated at 135° C. for 4 days. The autoclave was removed and allowed to cool to room temperature. The solids were then recovered by filtration, washed thoroughly with deionized water and dried at 95° C. 
         [0086]    The product of this preparation was identified by powder XRD analysis as a pure ESV framework type molecular sieve. 
         [0087]    The product had a SiO 2 /Al 2 O 3  mole ratio of 8.21, as determined by ICP elemental analysis. 
       Example 4 
       [0088]    0.40 g of a 50% NaOH solution, 1.05 g of deionized water, and 0.51 g of CBV720 Y-zeolite powder (Zeolyst International, SiO 2 /Al 2 O 3  mole ratio=30) were mixed together in a Teflon liner. Then, 1.09 g of a 19% dimethyl DABCO hydroxide solution was added to the mixture. The Teflon liner was then capped and placed within a steel Parr autoclave. The autoclave was placed on a spit within a convection oven and heated at 135° C. for 4 days. The autoclave was removed and allowed to cool to room temperature. The solids were then recovered by filtration, washed thoroughly with deionized water and dried at 95° C. 
         [0089]    The product of this preparation was identified by powder XRD analysis as a pure ESV framework type molecular sieve. 
         [0090]    The product had a SiO 2 /Al 2 O 3  mole ratio of 8.03, as determined by ICP elemental analysis. 
       Example 5 
       [0091]    0.51 g of a 50% NaOH solution, 2.25 g of deionized water, and 0.50 g of CBV720 Y-zeolite powder (Zeolyst International, SiO 2 /Al 2 O 3  mole ratio=30) were mixed together in a Teflon liner. Then, 1.09 g of a 19% dimethyl DABCO hydroxide solution was added to the mixture. The Teflon liner was then capped and placed within a steel Parr autoclave. The autoclave was placed on a spit within a convection oven and heated at 135° C. for 4 days. The autoclave was removed and allowed to cool to room temperature. The solids were then recovered by filtration, washed thoroughly with deionized water and dried at 95° C. 
         [0092]    The product of this preparation was identified by powder XRD analysis as a mixture of ESV framework type molecular sieve and a small portion of ANA framework type molecular sieve. 
       Example 6 
       [0093]    1.90 g of a 50% NaOH solution, 5.14 g of deionized water, and 5.00 g of LZ-210 Y-zeolite powder (SiO 2 /Al 2 O 3  mole ratio=13) were mixed together in a Teflon liner. Then, 14.89 g of a 19% dimethyl DABCO hydroxide solution was added to the mixture. Finally, 6.11 g of a 38.5% sodium silicate solution was added to the mixture and the gel was stirred until it became homogeneous. The Teflon liner was then capped and placed within a steel Parr autoclave. The autoclave was placed on a spit within a convection oven and heated at 150° C. for 6 days. The autoclave was removed and allowed to cool to room temperature. The solids were then recovered by filtration, washed thoroughly with deionized water and dried at 95° C. 
         [0094]    The product of this preparation was identified by powder XRD analysis as a mixture of ESV framework type molecular sieve and ANA framework type molecular sieve. 
       Example 7 
       [0095]    0.38 g of a 50% NaOH solution, 2.02 g of deionized water, and 0.51 g of CBV720 Y-zeolite powder (Zeolyst International, SiO 2 /Al 2 O 3  mole ratio=30) were mixed together in a Teflon liner. Then, 1.45 g of a 19% dimethyl DABCO hydroxide solution was added to the mixture. The Teflon liner was then capped and placed within a steel Parr autoclave. The autoclave was placed on a spit within a convection oven and heated at 135° C. for 4 days. The autoclave was removed and allowed to cool to room temperature. The solids were then recovered by filtration, washed thoroughly with deionized water and dried at 95° C. 
         [0096]    The product of this preparation was identified by powder XRD analysis as a mixture of ESV framework type molecular sieve and a small portion of LEV framework type molecular sieve. 
       Example 8 
       [0097]    2.39 g of a 50% NaOH solution, 6.78 g of deionized water, and 4.00 g of LZ-210 Y-zeolite powder (SiO 2 /Al 2 O 3  mole ratio=13) were mixed together in a Teflon liner. Then, 11.17 g of a 19% dimethyl DABCO hydroxide solution was added to the mixture. Finally, 8.37 g of a 38.5% sodium silicate solution was added to the mixture and the gel was stirred until it became homogeneous. The Teflon liner was then capped and placed within a steel Parr autoclave. The autoclave was placed on a spit within a convection oven and heated at 150° C. for 7 days. The autoclave was removed and allowed to cool to room temperature. The solids were then recovered by filtration, washed thoroughly with deionized water and dried at 95° C. 
         [0098]    The product of this preparation was identified by powder XRD analysis as a mixture of ESV framework type molecular sieve and LEV framework type molecular sieve. 
       Example 9 
       [0099]    1.45 g of a 50% NaOH solution, 2.46 g of deionized water, and 0.49 g of a 50% aluminum hydroxide solution (Barcroft™ USP 0250) were mixed together in a Teflon liner. Then, 5.55 g of a 19% dimethyl DABCO hydroxide solution was added to the mixture. Finally, 6.00 g of colloidal silica (LUDOX® AS-40) was added to the mixture and the gel was stirred until it became homogeneous. The Teflon liner was then capped and placed within a steel Parr autoclave. The autoclave was placed on a spit within a convection oven and heated at 170° C. for 7 days. The autoclave was removed and allowed to cool to room temperature. The solids were then recovered by filtration, washed thoroughly with deionized water and dried at 95° C. 
         [0100]    The product of this preparation was identified by powder XRD analysis as a mixture of ESV framework type molecular sieve, ANA framework type molecular sieve and MOR framework type molecular sieve. 
       Example 10 
     Calcination of SSZ-102 
       [0101]    The as-synthesized molecular sieve product of Example 1 was calcined inside a muffle furnace under a flow of air heated to 540° C. at a rate of 1° C./minute and held at 540° C. for 5 hours, cooled and then analyzed by powder XRD. 
         [0102]      FIG. 3  shows a comparison of two X-ray diffraction patterns, the top one being calcined SSZ-102 prepared in Example 10 and the bottom one being as-synthesized SSZ-102 as prepared in Example 1. The powder XRD pattern indicates that the material remains stable after calcination to remove the organic SDA. 
         [0103]    For the purposes of this specification and appended claims, unless otherwise indicated, all numbers expressing quantities, percentages or proportions, and other numerical values used in the specification and claims, are to be understood as being modified in all instances by the term “about.” Accordingly, unless indicated to the contrary, the numerical parameters set forth in the following specification and attached claims are approximations that can vary depending upon the desired properties sought to be obtained. It is noted that, as used in this specification and the appended claims, the singular forms “a,” “an,” and “the,” include plural references unless expressly and unequivocally limited to one referent. As used herein, the term “include” and its grammatical variants are intended to be non-limiting, such that recitation of items in a list is not to the exclusion of other like items that can be substituted or added to the listed items. As used herein, the term “comprising” means including elements or steps that are identified following that term, but any such elements or steps are not exhaustive, and an embodiment can include other elements or steps. 
         [0104]    Unless otherwise specified, the recitation of a genus of elements, materials or other components, from which an individual component or mixture of components can be selected, is intended to include all possible sub-generic combinations of the listed components and mixtures thereof. 
         [0105]    The patentable scope is defined by the claims, and can include other examples that occur to those skilled in the art. Such other examples are intended to be within the scope of the claims if they have structural elements that do not differ from the literal language of the claims, or if they include equivalent structural elements with insubstantial differences from the literal languages of the claims. To an extent not inconsistent herewith, all citations referred to herein are hereby incorporated by reference.