Abstract:
An improved surface acoustic wave device includes a film of a magnetostrictive material disposed on a substrate and spaced apart input and output transducer elements disposed on the film. The input element causes horizontally polarized shear waves to propagate along the film via the magnetostriction of the film. The shear waves propagating along the film are received by the output transducer element. The SAW device can be integrated on a microelectronic circuit useable in single chip radio frequency applications.

Description:
FIELD OF THE INVENTION 
     This invention relates to surface acoustic wave (SAW) devices, and in particular, to a SAW device that uses a meander coil and a ferromagnetic thin film to generate horizontal shear waves via the magnetostrictive effect. It also relates to silicon microelectronic circuits having such devices. 
     BACKGROUND OF THE INVENTION 
     SAW devices are essential components of RF wireless communication devices. They also have potential in other electronics applications because SAW devices exhibit low velocity non-dispersive propagation, with low attenuation up to microwave frequencies, and provide a propagation path which is accessible at the surface of the material. 
     A typical SAW device comprises spaced apart input and output interdigital transducers disposed on the surface of a substrate. The input transducer generates surface waves and the output transducer receives the waves. The substrate is typically about 1 mm thick and provides a propagation medium for the surface waves. Most SAW devices use a substrate composed of a high quality piezoelectric crystal, such as gallium arsenide. In operation, the input transducer generates a spatially periodic electric field in response to an applied oscillatory electrical signal or voltage. This causes a corresponding pattern of mechanical displacements or surface waves to be produced, via the piezoelectric effect. This causes a voltage to appear on the output transducer after a delay determined by the transducer separation and the surface wave velocity. 
     Unfortunately, SAW devices are expensive to produce because high quality piezoelectric crystalline substrates are costly. Moreover, SAW devices based on such substrates can not be readily integrated into silicon microelectronic circuits for single chip RF applications. 
     Accordingly, there is a need for an inexpensive SAW device that can be integrated into silicon microelectronic circuits. 
     SUMMARY 
     An improved SAW device comprises a film of magnetostrictive material disposed on a substrate and spaced apart input and output transducer elements disposed on the film. The input element causes horizontally polarized shear waves to propagate along the film via the magnetostriction of the film. The shear waves propagating along the film are received by the output transducer element. The SAW device can be integrated on a microelectronic circuit useable in single chip radio frequency applications. 
    
    
     BRIEF DESCRIPTION OF THE DRAWINGS 
     The advantages, nature and various additional features of the invention will appear more fully upon consideration of the illustrative embodiments described in detail below, considered together with the accompanying drawings. In the drawings: 
     FIG. 1 is a perspective view of a SAW device; 
     FIG. 2 is a cross-sectional view through line 2--2 of FIG. 1; 
     FIG. 3 is a graph showing the amplitudes of SH waves generated by the input MET of a SAW device similar to that shown in FIGS. 1 and 2, as the static bias magnetic field H o  is decreased from near-saturation levels; and 
     FIG. 4 is a graph showing the complex permeability of a CoTaZr film at a magnetic field strength of 40 Oe. 
     It should be understood that the drawings are for purposes of illustrating the concepts of the invention and are not to scale. 
    
    
     DETAILED DESCRIPTION 
     FIGS. 1 and 2 collectively show a surface acoustic wave (SAW) device 10 comprising a substrate 12 coated with a thin film 14 of magnetostrictive material followed by an insulating film 16 of dielectric material. The substrate 12 can be a silicon (Si) substrate of a microelectronic circuit having a plurality of electrically interconnected circuit components at least one of which is electrically connected to the SAW device 10. Such circuits are used in single chip radio frequency RF applications. An input magneto-elastic transducer (MET) 18 is disposed on a first region of the insulating film 16 and is driven by an oscillatory electrical signal (ac current) at a dynamic frequency ω. The input MET 18 generates a spatially periodic magnetic field in response to an applied oscillatory electrical signal. This causes a corresponding pattern of mechanical displacements in the form of horizontally polarized shear (SH) waves to propagate along the thin film 14 of magnetostrictive material, via the magnetostrictive effect. An output MET 22 is disposed on a second region of the insulating film 16 spaced from the input MET 18. The output MET 22 receives the SH waves propagating along the thin film 14 of magnetostrictive material caused by the operation of the input MET 18. The output MET 22 produces a voltage in response to the receive SH waves after a delay determined by MET separation and the surface wave velocity. Each of the METs 18, 22 comprises a meander coil 20, 24 formed by a continuous, metallic conductor pattern that is deposited on the insulating film 16. The conductor pattern typically has a serpentine shape. 
     The magnetostrictive material used for the thin film 14 should comprise a saturation magnetostriction λ s  greater than 10 ppm (10×10 -6 ) and preferably greater than 20 ppm (20×10 -6 ), a high resistivity, a small dispersion of the easy axis, and a high ferromagnetic resonance frequency. Materials meeting these criteria comprise polycrystalline ferromagnetic alloys such as Ni x  Fe 1-x , preferably with 0.4&lt;×&lt;0.6 or 0.15&lt;×&lt;0.25 and Co x  Fe 1-x , preferably with 0.3&lt;×&lt;0.7; amorphous ferromagnetic alloys of Fe and/or Co with early transition metals such as Co 1-x-y  Ta x  Zr y , preferably with 0.01&lt;×&lt;0.15 and 0.01&lt;y&lt;0.15, and Co 1-x-y  Nb x  Zr y , preferably with 0.01&lt;×&lt;0.15 and 0.01&lt;y&lt;0.15; amorphous ferromagnetic alloys of Fe and/or Co with metalloids such as Fe 1-x-y  Co x  P y , preferably with 0.01&lt;×&lt;0.7 and 0.05&lt;y&lt;0.2; and rare-earth transition-metal ferromagnetic alloys such as Tb x  Dy 1-x  Fe y , preferably with 0.2&lt;×&lt;0.3 and 1.9&lt;y&lt;2.1. Ferromagnetic oxides, such as NiFe 2  O 4 , (NiZn)Fe 2  O 4 , and Fe 3  O 4 , can also be used for the thin film 14. Since these oxides are insulating, they enable the insulating film 16 to be omitted. 
     The thin film 14 of magnetostrictive material is used as an acoustic coupling medium and the film&#39;s magnetic anisotropy is operative as an effective static bias magnetic field H o  thereby generating magnetostriction in the thin film 14. This anisotropy in conjunction with pattern geometries of the film 14 self-bias the MET so that externally applied static fields are not required as is the case with bulk ferromagnetic materials. Thin films made from the magnetic materials described earlier exhibit sufficient magnetostriction to enable the SAW device 10 to generate SH waves. 
     In operation, the effective static bias magnetic field H o  induces a single-magnetic-domain state. The ac current in the MET 18 creates an oscillating field HO that adds perpendicularly to the static bias field H o , and rotates the magnetization in the surface plane of the device 10 creating a shear strain. The amplitude of the SH wave obeys the relationship: 
     Ψ∝δh |∂ε xy  /∂H.sub.ω |, 
     where ε xy  is the magnetostrictive shear strain induced by H o  and H.sub.ω (the derivative ∂ε xy  /∂Hω is referred to as magnetostrictive strain coefficient), h is the magnitude of H.sub.ω at the surface of the device, δ is the skin depth square root of 2/(βσω, where β is the transverse incremental permeability, σ is the conductivity, and ω is the angular frequency. In high static bias fields, where the magnetization remains nearly parallel to the total magnetic field, ∂ε xy  /∂H.sub.ω ≈3λ y  /2Ho o , where λ y  is the magnetostriction coefficient (the longitudinal strain due to H o ). 
     FIG. 3 is a graph showing the amplitudes of SH waves generated by the input MET of a SAW device similar to that shown in FIGS. 1 and 2, as the static bias magnetic field H o  is increased from zero to a high value. The SAW device included a thin film of amorphous CoTaZr deposited on a Si substrate and a 6 mm wavelength input meander coil. The amplitudes of the SH waves were generated at peak transducer driving currents of 25 amps (curve A), 5 amps (curve B), and 1 amp (curve C). The measurement frequency was 771 kHz. The graph shows that for static bias fields H o  above 200 oersteds (Oe), the SH wave amplitudes generated by the SAW device decreased as a function of 1/(square root of H o ) as indicated by the dotted lines. For static bias fields H o  above 400 Oe, the SAW device generated SH wave amplitudes which increased linearly with the driving current of the MET. Maximum SH wave amplitudes were observed at low bias fields H o . As the MET current was decreased, the amplitude peaks of the SH waves shifted to lower static bias fields H o , with minimal changes in the height of the amplitude peaks. 
     In addition to high magnetostriction, thin films selected from the magnetic materials described above also exhibit low dispersion and a ferromagnetic resonance frequency in the GHz range. This enables the SAW device to be advantageously used in RF applications. FIG. 4 is a graph showing the complex permeability of a CoTaZr film at a magnetic field strength of 40 Oe. The graph shows the magnetic permeability μ&#39; of the film vs. frequency and the loss μ&#34; of the film vs. frequency. The CoTaZr film provides low dispersion and a ferromagnetic resonance frequency in the GHz range. The measured permeability μ&#39; is consistent with coherent rotation of the magnetization. 
     The magnetic and insulating films of the SAW device can be deposited on the substrate using established thin film deposition methods. The thin film 14 of magnetostrictive material has a thickness which is typically about 0.1-1.0 um and the insulating film has a typical thickness of about 0.1-1.0 um. The meander coils of the SAW device can be made by depositing a metal film of aluminum having a thickness typically about 0.5 um. The conductor pattern is then defined in the metal film using conventional lithography methods. Because the SAW device is especially suited for fabrication on Si substrates, integration into a Si-based microelectronic circuit is possible. Moreover, thin films of magnetostrictive material are compatible with current microelectronic devices. 
     It should be understood that the above described embodiments are illustrative of only a few of the many possible specific embodiments which can represent applications of the principles of the invention. Numerous and varied other arrangements can also be devised by those skilled in the art without departing from the spirit and scope of the invention.