Abstract:
A method for forming a fuse for integrated circuits and a fuse produced therefrom is disclosed. The fuse (10) includes a substrate (12) having thick oxide layers (14) with a gap (16) formed therebetween. A second oxide layer (20) is grown onto an N+ region (18). At the intersection between oxide layers (20, 14), a sublithographic area is exposed and a dielectric layer (24) is formed therein. This structure is capable of reducing the capacitance between a polysilicon layer (26) formed thereon and the N+ diffusion region (18).

Description:
This application is a division of U.S. patent application Ser. No. 07/587,508, filed Sep. 21, 1990, U.S. Pat. No. 5,019,532, which is a continuation of U.S. patent application Ser. No. 07/457,443, filed Dec. 27, 1989, now abandoned. 
    
    
     TECHNICAL FIELD OF THE INVENTION 
     The present invention relates to a method for manufacturing integrated circuits and an apparatus made therefrom. More particularly, the invention relates to an improved method for forming a fuse for an integrated circuit. 
     BACKGROUND OF THE INVENTION 
     As the integrated circuit industry becomes more and more competitive, there is a need for more efficient integrated circuits which deliver electronic messages at faster rates than is presently accomplished. To design faster parts, the capacitance associated with interconnects, passive and active devices need to be reduced. For PROMs which use a thin dielectric as the fusing element, the capacitance of the cell will be greatly affected by the capacitance of the thin dielectric. Generally, capacitance per unit area of a thin film capacitor is equal to the ratio of the area divided by the thickness of the dielectric. 
     In the past, this limitation of capacitance has been dealt with by reducing the area of the fuse region and increasing the thickness of the dielectric. Unfortunately thicker dielectrics require higher voltages for fusing (dielectric breakdown). This in turn makes the incorporation of high voltage devices to standard logic process flow more difficult. Higher voltage requirements will as well increase the device isolation space making the cell bigger. 
     For a given lithographic capability, the area of the fuse cell would be limited by the minimum size of the geometry than can be defined by lithography. 
     Therefore, there is a need for a thin dielectric system for lower programming voltage while at the same time having very small area to reduce the capacitance associated with the fuse dielectric. 
     SUMMARY OF THE INVENTION 
     The present invention provides a method for forming a fuse on a semiconductor wafer and a fuse made therefrom. It allows the fabrication of a fuse cell where the area of the thin dielectric region is much smaller than that can be defined by lithography. 
     One aspect of the present invention is an apparatus having a layer of field oxide with a gap area formed therebetween to define a moat area. Within the moat area, an N+ region is fabricated by implanting an arsenic dopant therein. After the dopant has created the N+ region, a second oxide layer is formed in the moat region within the gap area. In its preferred embodiment, the second oxide layer is thinner the field oxide layer formed. A region is formed at the intersection between the first and second oxide layers to expose the N+ region. At this exposed N+ region, a dielectric is formed in accordance with the present invention. In its preferred embodiment, this dielectric is a composite of oxide and nitride. Specifically, a thin layer of oxide is initially grown onto the exposed N+ region. Subsequently, a layer of nitride is deposited onto the oxide layer. Finally, the top surface of the nitride is converted to oxide in an oxidizing ambient to make the dielectric of the present invention. After this dielectric has been formed, a layer of polysilicon is deposited over the entire dielectric stack. 
     A method for fabricating the fuse described above is preferably manufactured by initially growing a field oxide layer to a thickness of approximately 8000 angstroms on a silicon layer to form a moat region therein. This moat region is subsequently implanted with an arsenic having a concentration of approximately 2×10 16  atoms/cm 2  to create an N+ diffused region. The implantation of the arsenic dopant is followed by the growth of a second layer of oxide on the diffused region. A small portion of the N+ region is then exposed by selectively etching through the field and second oxide layers. The dielectric, as described above, is deposited onto the N+ region. Finally, a polysilicon layer is deposited onto the N+ region to complete the preferred embodiment of the present invention. 
     The present invention presents technical advantages over the prior method of fabricating a semiconductor fuse. This invention is capable of having a thin dielectric layer while at the same time having a low capacitance. The present invention has the capability of having a low capacitance by decreasing the area of the dielectric while at the same time maintaining a thin dielectric. 
    
    
     BRIEF DESCRIPTION OF THE DRAWINGS 
     Other aspects of the invention and their advantages may be appreciated with reference to the following Detailed Description taken in conjunction with the appended Drawings in which: 
     FIG. 1a is an enlarged cross-sectional view of a workpiece with a layer of field oxide grown thereon, according to the present invention; 
     FIG. 1b is a top view of the workpiece as illustrated in FIG. 1a; 
     FIG. 2 is an enlarged cross-sectional view of the workpiece as shown in FIG. 1a, illustrating a second oxide layer grown within a moat region as defined by the field oxide layer; 
     FIG. 3a is an enlarged cross-sectional view of the workpiece after a dielectric has been formed thereon; 
     FIG. 3b is a top view of the workpiece as illustrated in FIG. 3a taken substantially along line 3a--3a of FIG. 3b; 
     FIG. 4a is an enlarged cross-sectional view of the workpiece after a polysilicon layer has been deposited to interconnect the N+ region with a contacting element; 
     FIG. 4b is a top view of the workpiece as illustrated in FIG. 4a taken substantially along line 4a--4a of FIG. 4b; and 
     FIG. 5 is a top view of the workpiece 10 having contacts connected thereto, according to the present invention. 
    
    
     DETAILED DESCRIPTION OF THE INVENTION 
     FIG. 1a is an enlarged cross-sectional view of a workpiece according to the present invention, generally designated 10. Workpiece 10 comprises a substrate 12, preferably a silicon wafer, having a boron dopant contained therein to create a P- region. Substrate 12 is generally a semiconductor layer in its broadest sense. A mask is selectively formed on a face of the semiconductor layer to define the area of field oxide layer 14 growth. Grown on substrate 12 is a field oxide layer 14 which functions as an insulator layer. Field oxide layer 14 is selectively grown to define a moat area 16 or diffused region. When forming field oxide layer 14 on substrate 12, it is preferable to heat the wafer to approximately 900 degrees Centigrade (°C.) for approximately 50 minutes with steam at approximately ten atmospheres. This heating of substrate 12 causes field oxide layer 14 to grow to approximately 8,000 angstroms thick. The actual thickness of field oxide layer 14 is dependent upon time, pressure, and temperature of the steam oxidation process. After substrate 12 has been adequately doped, a thin oxide layer 15 is thermally grown to approximately 350 angstroms thick in the moat region 16. 
     Referring now to FIG. 1b, a top view of workpiece 10, as illustrated in FIG. 1a, can be seen. Generally, moat area 16 is defined in a rectangular configuration. Moat area 16 can be formed in any one of several alternative configurations. 
     Referring now to FIG. 2, an enlarged cross-sectional view of a workpiece 10 illustrates subsequent processing steps. Initially, an N+ region 18 is formed in moat area 16 by controllably implanting an N-type dopant. This dopant is preferably arsenic, and is diffused into substrate 12 at an energy of 50 KeV and a dosage of about 1×10 16  atoms/cm 2 . 
     After N+ region 18 has been formed, a second oxide layer 20 is formed in moat region 16. As can be seen, &#34;buried&#34; N+ oxide layer 20 is formed having ends 19 and 21. Layer 20 is formed by heating substrate 12 to approximately 900° C. and in the presence of oxygen for ten minutes. Substrate 12 is next heated to 900° C. for 38 minutes with steam. This process is followed by heating substrate 12 for approximately one minute at -900° C. in the presence of oxygen. This series of heating steps selectively grows oxide layer 20. The above-discussed implantation was self-aligned to the sloping edges of the field oxide 14. The concentration of dopant in region 18 decreases as a function of the thickness of the oxide layer 14 over it. The oxide layer 20 grows at a faster rate than dimples or ends 19 and 21 because the dopant concentration underneath layer 20 is greater. The combination of the sloped sidewalls or &#34;bird&#39;s beak&#34; of oxide layer 14 and the differential growth of oxide layer 20 creates a relative depression in the thickness of the oxide. 
     Now referring to FIG. 3a, photoresist layers are deposited and patterned onto workpiece 10 to define a region for subsequent etching of fuse area 22. The etch is preferably performed using a 10% buffered hydrofluoric acid (HF). Once fuse area 22 has been etched, a gap region forms 23 at end 21 where the N+ region is exposed. This exposed region is subsequently used for the depositing of layers to form a dielectric thereon. The sloping sidewalls of layers 14 and 20 mean that the size of the exposed region 23 can be carefully controlled by timing the etchback. Hence, an extremely small, submicron exposed area may be fabricated without the scaling limitations imposed by microlithography. The reduction in area translates into a reduction of cell capacitance. 
     A dielectric 24 is formed at end 21 by depositing or growing oxides and nitrides thereon. An oxide layer is grown approximately 35 to 40 angstroms thick by submitting workpiece 10 to 700° C. for ten minutes in the presence of nitrogen. Subsequently, workpiece 10 is exposed for 18 minutes to oxygen, followed by the exposure of substrate 12 to nitrogen for ten minutes. After the oxide has been deposited to form the first composite layer of dielectric 24, a nitride is deposited to approximately 85 angstroms thick. Another oxide layer is then deposited. This deposition is performed by submitting workpiece 10 to a temperature of approximately 900° C. for 110 minutes in the presence of argon and oxygen. This method of creating a deposit dielectric can be easily understood by referring to U.S. Pat. No. 4,823,181, issued to Mohsen, et. al., entitled &#34;Programmable Low Impedance Anti-Fusion Element&#34;, and incorporated herein for reference. 
     Referring now to FIG. 3b, a top view of workpiece 10 as illustrated in FIG. 3a can be seen. Fuse area 22 is formed onto moat area 16. As can be appreciated, fuse area 22 can be anywhere along the boundary of moat area 16, depending upon the particular application. 
     Referring now to FIG. 4a, an enlarged cross-sectional view of workpiece 10 can be seen. In accordance with the present invention, a polysilicon layer 26 is deposited to make contact with dielectric layer 24. 
     To complete the fabrication of the present invention, it is preferable that polysilicon layer 26 be deposited to approximately 4,500 angstroms thick. The workpiece 10 is submitted to a phosphorus dopant ambient in POCl 3  at 900° C. for 30 minutes to increase the conductivity of polysilicon layer 26. Once the layer has been formed, an arsenic dopant is implanted into polysilicon layer 26 at approximately 70 KeV and a dosage of 2×10 16  atoms/cm 2 . After polysilicon layer 26 has been initially deposited, the configuration can be defined by depositing a photoresist layer patterning it and etching away the areas not covered by photoresist. 
     FIG. 4b is a top view of workpiece 10, as illustrated in FIG. 4a. 
     Referring now to FIG. 5, contacts are formed to polysilicon layer 26 and the surface of workpiece 10. A contact 29 is made through the oxide layer 20 to diffused region 18 to make electrical connection to the other electrode of the capacitor. Metal strips 30 may next be applied to contacts 28 and 29 to complete the illustrated embodiment of the present invention. 
     The present invention presents technical advantages over the prior art because it reduces capacitance of the formed capacitor. Unfortunately, prior art has not overcome the problems associated with a high capacitance due to a high ratio of the area divided by its thickness. According to the present invention, this specific embodiment is able to overcome problems associated with the prior art because of the small size of the semiconductor electrode. 
     While the preferred embodiment of the present invention and its advantages have been disclosed in the above-detailed description, the present invention is not limited thereto, but only by the spirit and scope of the appended claims.