Abstract:
An MTJ MRAM cell is formed between or below an intersection of ultra-thin orthogonal word and bit lines of high conductivity material whose thickness is less than 100 nm. Lines of this thickness produce switching magnetic fields at the cell free layer that are enhanced by a factor of approximately two for a given current. The fabrication of a cell with such thin lines is actually simplified as a result of the thinner depositions because the fabrication process eliminates the necessity of removing material by CMP during patterning and polishing, thereby producing uniform spacing between the lines and the cell free layer.

Description:
[0001]     This Application is a Continuation-In-Part of Ser. No.: 10/892,668, filing date: Jul. 16, 2004.  
       RELATED PATENT APPLICATIONS  
       [0002]     This Application is related to Ser. No. 10/910,725, filed on Aug. 3, 2004 and assigned to the same assignee as the present application. 
     
    
     BACKGROUND OF THE INVENTION  
       [0003]     1. Field of the Invention  
         [0004]     This invention relates to the design and fabrication of magnetic tunnel junctions (MTJ) as memory storage devices, particularly to a design wherein word and bit lines are ultra-thin so as to produce higher magnetic flux at the MTJ free layer for a given write current.  
         [0005]     2. Description of the Related Art  
         [0006]     The magnetic tunnel junction (MTJ) basically comprises two electrodes, which are layers of magnetized ferromagnetic material, separated by a tunnel barrier layer, which is a thin layer of insulating material. The tunnel barrier layer must be sufficiently thin so that there is a probability for charge carriers (typically electrons) to cross the layer by means of quantum mechanical tunneling. The tunneling probability is spin dependent, however, because it depends on the availability of tunneling states that accept electrons with different spin orientations. Therefore, the overall tunneling current will depend on the number of spin-up vs. spin-down electrons, which in turn depends on the orientation of the electron spin relative to the magnetization direction of the ferromagnetic layers. Thus, if the relative magnetization directions are varied for a given applied voltage, the tunneling current will also vary. As a result of this behavior of an MTJ, sensing the change of tunneling current for a fixed voltage can enable a determination of the relative magnetization directions of the two ferromagnetic layers that comprise it.  
         [0007]     The use of an MTJ as an information storage device requires that the magnetization of at least one of its ferromagnetic layers can be varied relative to the other and also that changes in these relative directions can be sensed by means of variations in the tunneling current or, equivalently, the junction resistance. In its simplest form as a two state memory storage device, the MTJ need only be capable of having its magnetizations put into parallel (low resistance) or antiparallel (high resistance) configurations, when writing data, and of having its tunneling current variations or resistance variations measured, when reading data.  
         [0008]     In practice, the free ferromagnetic layer of the MTJ can be modeled as having a magnetization which is free to rotate but which energetically prefers to align in either direction along its easy axis (the direction of magnetic anisotropy). The magnetization of the fixed layer may be thought of as being permanently aligned in its easy axis direction. When the free layer is anti-aligned with the fixed layer, the junction will have its maximum resistance, when the free layer is aligned with the fixed layer, the minimum resistance is present. In typical MRAM circuitry, the MTJ devices are located at the intersection of orthogonal current carrying lines called word lines and bit lines. When both lines are carrying current, the device is written upon by having the magnetization direction of its free layer changed. When only one line is carrying current, the resistance of the device can be sensed, so the device is effectively read. Note that an additional current carrying line may be present in some device configurations to sense the resistance of the device, but in simplest terms the device behaves as described above. Such an MTJ device is provided by Gallagher et al. (U.S. Pat. No. 5,650,958), who teach the formation of an MTJ device with a pinned ferromagnetic layer whose magnetization is in the plane of the layer but not free to rotate, together with a free magnetic layer whose magnetization is free to rotate relative to that of the pinned layer, wherein the two layers are separated by an insulating tunnel barrier layer.  
         [0009]     In order for the MTJ MRAM device to be competitive, in terms of power consumption and device density, with other forms of DRAM, it is necessary that the MTJ be made very small, typically of sub-micron dimension. Parkin et al. (U.S. Pat. No. 6,166,948) teaches the formation of an MTJ MRAM cell in which the free layer is formed of two antiparallel magnetized layers separated by a spacer layer chosen to prevent exchange coupling but to allow direct dipole coupling between the layers. The free layer thereby has closed flux loops and the two layers switch their magnetizations simultaneously during switching operations. Parkin notes that sub-micron dimensions are needed to be competitive with DRAM memories in the range of 10-100 Mbit capacities. Parkin also notes that such small sizes are associated with significant problems, particularly super-paramagnetism, which is the spontaneous thermal fluctuation of magnetization in samples of ferromagnetic material too small to have sufficient magnetic anisotropy (a measure of the ability of a sample to maintain a given magnetization direction). To overcome the undesirable spontaneous thermal fluctuations in MRAM cells with very small cross-sectional areas, it is necessary to make the magnetic layers thick. Unfortunately, the size of the required switching field increases with layer thickness, so the price paid for a thermally stable cell is the necessity of expending a great deal of current to change the magnetic orientation of the cell&#39;s free layer.  
         [0010]     Some degree of anisotropy is necessary if an MTJ cell is to be capable of maintaining a magnetization direction and, thereby, to effectively store data even when write currents are zero. As cell sizes have continued to decrease, the technology has sought to provide a degree of magnetic anisotropy by forming cells in a wide variety of shapes (eg. rectangles, diamonds, ellipses, etc.), so that the lack of inherent crystalline anisotropy is countered by a shape anisotropy. Yet this form of anisotropy brings with it its own problems. A particularly troublesome shape-related problem in MTJ devices results from non-uniform and uncontrollable edge-fields produced by shape anisotropy (a property of non-circular samples). As the cell size decreases, these edge fields become relatively more important than the magnetization of the body of the cell and have an adverse effect on the storage and reading of data. Although such shape anisotropies, when of sufficient magnitude, reduce the disadvantageous effects of super-paramagnetism, they have the negative effect of requiring high currents to change the magnetization direction of the MTJ for the purpose of storing data.  
         [0011]     One way of addressing the problem of the high currents needed to change the magnetization direction of a free layer when its shape anisotropy is high, is to provide a mechanism for concentrating the fields produced by lower current values. This approach was taken by Durlam et al. (U.S. Pat. No. 6,211,090 B1) who teach the formation of a flux concentrator, which is a soft magnetic (NiFe) layer formed around a copper damascene current carrying line. The layer is formed around three sides of the copper line which forms the digit line at the underside of the MRAM cell.  
         [0012]     Two additional approaches are taught by Nakao, (U.S. Pat. No. 6,509,621 B2), who, in one embodiment, forms a pinned layer out of a material that produces a high percentage of spin polarized electrons in the current and in another embodiment, applies an offsetting magnetic field produced by a magnetic shield to assist in causing field reversals in the cell element.  
         [0013]     Yet another approach is taught by Sekiguchi et al., (U.S. Pat. No. 6,611,455 B2) who forms free layers with easy axes that are perpendicular to the layer plane, then forms word and bit lines in the same plane.  
         [0014]     The present invention also addresses the problem of reducing the high current required to reorient the magnetization of the free layer in ultra-small MRAM cells wherein the super-paramagnetic behavior requires thick free layers. It does so by forming word and/or bit lines of exceptional thinness, specifically under 100 nm, compared to conventional thicknesses of approximately 300 nm, thereby increasing the switching field at the free layer by as much as a factor of 2. An additional benefit of such thin lines is the ease of their fabrication. The patterning process for their formation requires the removal of less material and can eliminate the need for chemical mechanical polishing (CMP), which can produce uncontrollable variations in line thicknesses. Finally, these ultra-thin lines are easily formed into a variety of configurations with respect to their positions relative to the MTJ cell. In the present invention the cell is positioned between the word and bit lines. In the following description the general method of forming the lines will be described along with illustrations of their placement relative to the cell.  
       SUMMARY OF THE INVENTION  
       [0015]     A first object of this invention is to provide an MTJ MRAM cell that makes more efficient use of word and bit line switching currents, the lines thereby producing magnetic fields of sufficient intensity for switching, while requiring lower currents to do so.  
         [0016]     A second object of this invention is to provide a method for fabricating such a cell and its word and bit lines that simplifies the fabrication process and, in particular, eliminates uncontrollable variations associated with the process of chemical-mechanical polishing (CMP).  
         [0017]     A third object of this invention is to provide such cells and arrays of such cells.  
         [0018]     These objects will be achieved by an MRAM cell design and fabrication method in which word and/or bit lines are formed of highly conductive materials to an exceptional thinness of less than 100 nm. The conducting material can be high conductivity materials such as Al, Cu, Au, Ru, Ta, CuAu, CuAg, NiCr, Rh and multilayers of these materials such as multiple laminations of (NiCr/Cu).  
         [0019]     In conventional word and bit lines of the prior art, the aspect ratio (ratio of thickness,t, to width w) of word/bit lines is close to one. Applying simple physics (Ampere&#39;s Law) indicates that the magnetic field, H s , at the surface of a prior art line of comparable thickness, t, and width, w, carrying current I is given by: H s =πI/w.  
         [0020]     For the proposed ultra-thin word/bit line design, where w&gt;&gt;t, the magnetic field obeys the following relationship: H s =2πI/w. Thus, there is an enhancement of the magnetic field at the wire surface by a factor of two. Since the MRAM cell is located a small distance from the line surface, the benefit will be somewhat reduced, but will still be substantial, particularly since the fabrication method allows the distance between line and cell to be kept uniformly small.  
         [0021]      FIG. 1   a  shows a vertical cross-sectional view of the MTJ MRAM cell of the present invention. The multilayered cell element, whose horizontal cross-section is substantially circular, is at a vertically separated intersection of an ultra-thin write word line ( 10 ) extending in length along the z-axis of the illustrated axes (its width being in the x-direction and its thickness in the y-direction), and an ultra-thin bit line ( 20 ) extending in length along the x-axis (its width being in the z-direction and its thickness being in the y-direction) and vertically below the word line. These lines are used to perform write operations on the cell, i.e. to switch the magnetization of its free layer. The write word line and bit lines are separated by an insulating layer ( 15 ) and are also surrounded peripherally by insulation. The write word and bit lines have thicknesses, t w  and t b  respectively that are substantially less than their widths, w w  and w b (not shown) in accord with the objects of the present invention, wherein t w  and t b  are both less than approximately 100 nm and their widths are between approximately 100 and 1000 nm. It is once again noted that word and bit lines of the prior art are formed with comparable widths and thicknesses, both being between approximately 300 and 500 nm. A description of the ultra-thin write word or bit line fabrication process will be described more fully below.  
         [0022]     An MTJ MRAM cell element ( 50 ), of thickness between approximately 200 and 400 angstroms and lateral dimension between approximately 0.1 and 1.0 microns, is shown positioned between the intersection of the word ( 10 ) and bit lines ( 20 ). The cell element is a horizontal multi-layer fabrication comprising a seed layer ( 51 ), formed on the bit line, an antiferromagnetic pinning layer ( 52 ), a synthetic ferrimagnetic pinned layer which includes a second ( 53 ) and first ( 55 ) ferromagnetic layer separated by a coupling layer ( 54 ), a tunnel barrier layer ( 56 ), a free layer ( 57 ), which can also be a laminated structure, and a capping layer ( 58 ) beneath the bit line. An additional conducting electrode, called a read word line ( 59 ), used in read operations, is formed on an upper surface of the cell. The word line is separated by insulation ( 15 ) from the conducting electrode. It is also possible to eliminate the electrode and have the word line electrically contact the upper cell surface. A detailed description of materials and dimensions used in the cell and in the fabrication process will be discussed below within the description of the preferred embodiment. 
     
    
     BRIEF DESCRIPTION OF THE DRAWINGS  
       [0023]      FIG. 1   a  is a schematic vertical cross-sectional view of an MTJ MRAM cell having its cell element formed between ultra-thin word and bit lines of the present invention.  
         [0024]      FIG. 1   b  schematically shows a vertical cross-sectional view of an MTJ MRAM cell of the present invention in an alternative configuration to that in  FIG. 1   a.    
         [0025]      FIG. 1   c  schematically shows a vertical cross-sectional view of an MTJ MRAM cell of the present invention in an alternative configuration to that in FIG&#39;S.  1   a  and  1   b.    
         [0026]      FIG. 1   d  schematically shows a vertical cross-sectional view of an MTJ MRAM cell of the present invention in an alternative configuration to that in FIG&#39;S.  1   a,    1   b  and  1   c.    
         [0027]      FIG. 1   e  is a schematic drawing of an array (two being illustrated) of MTJ MRAM cells of the typed illustrated in  FIG. 1   b  formed between ultra-thin word and bit lines.  
         [0028]      FIG. 1   f  schematically shows an array of two cells of the type illustrated in  FIG. 1   a,  formed between ultra-thin word and bit lines.  
         [0029]      FIG. 1   g  schematically shows an array of two cells of the typed illustrated in  FIG. 1   d,  formed between ultra-thin word and bit lines.  
         [0030]      FIG. 1   h  schematically shows an array of two cells of the type illustrated in  FIG. 1   c,  formed between ultra-thin word and bit lines.  
         [0031]     FIG&#39;S.  2   a - e  provide a more detailed schematic description of the formation of an ultra-thin word or bit line, indicating how the thinness of the word and bit lines makes their formation simpler. 
     
    
     DESCRIPTION OF THE PREFERRED EMBODIMENTS  
       [0032]     Each of the preferred embodiments of the present invention provides an MTJ MRAM cell formed at an intersection of ultra-thin word and bit lines, either between those lines, as in FIG&#39;S.  1   a,    1   b,  and  1   c,  or below (or above) those lines, as in  FIG. 1   d.  In each embodiment, it is the advantage of the invention that currents can still produce adequate switching fields at the location of the cell free layer.  
         [0033]     Referring again to  FIG. 1   a,  there is shown the multi-layered MTJ cell element ( 50 ) formed between orthogonally directed, vertically separated ultra-thin word ( 10 ) and bit ( 20 ) lines of the invention. The two lines extend in vertically separated horizontal planes, crossing over each other but insulated from each other and forming, thereby, an intersection at which the cell is located. In all that follows, the term “intersection” is taken to mean a vertically separated crossing of lines. The word line is directed perpendicularly out of the figure plane, the bit line is within the figure plane. An additional conducting electrode, (alternatively denoted a read-word line), used in read operations ( 59 ), is formed on an upper surface of the cell. During operation of the cell, the conducting electrode will normally be connected to an accessing transistor which is used to determine the logic state of the MRAM cell. The electrode is insulated from and separated from the word line, but it is clear that the separation should be kept as small as possible to maintain the field strength of the word line at the free layer of the cell. The bit line ( 20 ) can be formed as a single layer of high conductivity material such as Al, Cu, Au, Ru, Ta, CuAu, CuAg, NiCr, Rh and multilayers of these materials such as multiple laminations of (NiCr/Cu), formed to a thickness of approximately  100  nm or less and a width between approximately 100 and 1000 nm. As previously noted, an additional conducting electrode ( 59 ), called a read word line, extending along the x-direction is formed contacting the upper surface of the cell and is used in conjunction with the bit line ( 20 ) for read operations. A connecting line ( 60 ) goes from the electrode ( 59 ) to a terminal of an accessing transistor (not shown), which is a part of the circuitry used to determine the logic state (i.e. its resistance) of the MRAM cell. In the particular configuration shown in  FIG. 1   a,  a single MRAM cell is connected to a single transistor. A partial array of two such cells, an example of which is shown in  FIG. 1   f,  each formed between vertically separated, intersecting word and bit lines and each accessed by its own transistor, would form part of a particular MRAM array design.  
         [0034]     Referring back to the cell element ( 50 ), a seed layer ( 51 ) is formed on the bit line ( 20 ) and promotes the high quality formation of subsequently formed layers of the cell. The seed layer can be a layer of NiCr or NiFe formed to a thickness between approximately 5 and 100 angstroms. A single pinned layer or, as in this embodiment, a synthetic ferrimagnetic pinned layer is formed on the seed layer. The synthetic layer includes an antiferromagnetic pinning layer ( 52 ), a second ferromagnetic layer ( 53 ), a coupling layer ( 54 ) and a first ferromagnetic layer ( 55 ). The antiferromagnetic layer pins the magnetization of the second ferromagnetic layer unidirectionally and the first ferromagnetic layer is magnetized in an antiparallel direction to that of the first layer. The first and second ferromagnetic layers are layers of CoFe formed to thicknesses between approximately 5 and 100 angstroms and matched so that the net magnetic moment of the configuration is substantially zero. The coupling layer is a layer of Rh, Ru, Cr or Cu of proper thickness to maintain strong antiparallel coupling between the magnetic moments. The antiferromagnetic pinning layer ( 52 ) can be a layer of PtMn, NiMn, OsMn, IrMn, PtPdMn, PtCrMn or FeMn of thickness between approximately 10 and 100 angstroms.  
         [0035]     A tunneling barrier layer ( 56 ) is formed on the first ferromagnetic layer ( 55 ) of the pinned layer. This layer is a layer of insulating material such as oxidized Al or an oxidized Al—Hf bilayer and is formed to a thickness between approximately 3 to 30 angstroms. A ferromagnetic free layer ( 57 ) is formed on the barrier layer. The free layer can be a single layer of ferromagnetic material, such as a layer of CoFe or NiFe formed to a thickness between approximately 5 and 100 angstroms or it can be a multilayer, comprising first and second ferromagnetic layers, magnetized in antiparallel directions and separated by a spacer layer of non magnetic but conducting material such as Rh, Ru, Cr or Cu, which is of the proper thickness to maintain strong antiparallel coupling between the two ferromagnetic layers. During formation of the cell it is advantageous to set the magnetic anisotropy direction of the ferromagnetic layers either perpendicular or parallel to the bit line. A capping layer ( 58 ) is formed on the free layer and completes the cell element ( 50 ). The capping layer can be a layer of Ru, or Ta or a multilayer of Ru/Ta formed to a thickness between approximately 5 and 100 angstroms. The read word line ( 59 ) is formed on the capping layer ( 58 ) of the cell element ( 50 ). A layer of insulating material ( 15 ) surrounds the cell and separates the write word line ( 10 ) from the bit line ( 20 ) and the read word line ( 59 ) from the word line ( 10 ). The write word line ( 10 ), like the bit line, is an ultra-thin layer of conducting material less than 100 nm in thickness formed in accord with the method of this invention. It is further noted that the separation between the read and write word lines must be kept as small as possible to maintain the strength of the write word line magnetic field at the cell element free layer. A separation no greater than the thickness of the ultra-thin lines is preferable.  
         [0036]     Referring to  FIG. 1   b,  there is shown an MTJ MRAM design employing the ultra-thin word ( 10 ) and bit ( 20 ) lines of the present invention, but differing from the design of  FIG. 1   a  in that the read word line (( 59 ) in  FIG. 1   a ) is absent and, instead, the write word line ( 10 ) is formed contacting the upper surface of the cell element ( 50 ). The cell element is identical to the cell element in  FIG. 1   a,  so it is not drawn in detail. In this configuration, the logic state of the cell is determined using only the write word line and bit line.  
         [0037]     Referring now to  FIG. 1   c,  there is shown an embodiment in which the multi-layered MTJ cell element ( 50 ) is formed between orthogonally directed, vertically separated ultra-thin word ( 10 ) and bit ( 20 ) lines of the invention. The two lines extend in vertically separated horizontal planes, crossing over each other but insulated from each other and forming, thereby, an intersection at which the cell is located. Unlike the configuration schematically illustrated in  FIG. 1   a,  the cell is now formed on the conducting electrode ( 59 ), (alternatively denoted a read-word line), used in read operations, so the conducting electrode now contacts a lower surface of the cell, specifically the cell seed layer ( 51 ) on which the cell is sequentially formed. During operation of the cell, the conducting electrode ( 59 ) will be connected by means of a conducting stud ( 60 ) to external circuitry that is used to determine the logic state of the MRAM cell.  
         [0038]     The word line ( 10 ), here formed beneath the conducting electrode and separated from it by a thin layer of insulation ( 15 ), can be formed as a single layer of high conductivity material such as Al, Cu, Au, Ru, Ta, CuAu, CuAg, NiCr, Rh and multilayers of these materials such as multiple laminations of (NiCr/Cu), formed to a thickness of approximately 100 nm or less and a width between approximately 100 and 1000 nm. The formation of this word line (and bit line as well) will be described in greater detail with reference to FIG&#39;S.  2   a - e.    
         [0039]     Referring back to the cell element ( 50 ), a seed layer ( 51 ) is formed on the conducting electrode ( 59 ) and promotes the high quality formation of subsequently formed layers of the cell. The seed layer can be a layer of NiCr or NiFe formed to a thickness between approximately 5 and 100 angstroms. A single pinned layer or, as in this embodiment, a synthetic ferrimagnetic pinned layer is formed on the seed layer. The synthetic layer includes an antiferromagnetic pinning layer ( 52 ), a second ferromagnetic layer ( 53 ), a coupling layer ( 54 ) and a first ferromagnetic layer ( 55 ). The antiferromagnetic layer pins the magnetization of the second ferromagnetic layer unidirectionally and the first ferromagnetic layer is magnetized in an antiparallel direction to that of the first layer. The first and second ferromagnetic layers are layers of CoFe formed to thicknesses between approximately  5  and  100  angstroms and matched so that the net magnetic moment of the configuration is substantially zero. The coupling layer is a layer of Rh, Ru, Cr or Cu of proper thickness to maintain strong antiparallel coupling between the magnetic moments. The antiferromagnetic pinning layer ( 52 ) can be a layer of PtMn, NiMn, OsMn, IrMn, PtPdMn, PtCrMn or FeMn of thickness between approximately 10 and 100 angstroms.  
         [0040]     A tunneling barrier layer ( 56 ) is formed on the first ferromagnetic layer ( 55 ) of the pinned layer. This layer is a layer of insulating material such as oxidized Al or an oxidized Al—Hf bilayer and is formed to a thickness between approximately  3  to  30  angstroms. A ferromagnetic free layer ( 57 ) is formed on the barrier layer. The free layer can be a single layer of ferromagnetic material, such as a layer of CoFe or NiFe formed to a thickness between approximately 5 and 100 angstroms or it can be a multilayer, comprising first and second ferromagnetic layers, magnetized in antiparallel directions and separated by a spacer layer of non magnetic but conducting material such as Rh, Ru, Cr or Cu, which is of the proper thickness to maintain strong antiparallel coupling between the two ferromagnetic layers. During formation of the cell it is advantageous to set the magnetic anisotropy direction of the ferromagnetic layers either perpendicular or parallel to the bit line. A capping layer ( 58 ) is formed on the free layer and completes the cell element ( 50 ). The capping layer can be a layer of Ru, or Ta or a multilayer of Ru/Ta formed to a thickness between approximately 5 and 100 angstroms. The bit line ( 20 ) is formed over insulation surrounding the cell and contacting the capping layer ( 58 ) of the cell element ( 50 ). A layer of insulating material ( 15 ) that surrounds the cell also separates the write word line ( 10 ) from the conducting electrode ( 59 ) by approximately 100 nm. The write word line ( 10 ), like the bit line, is an ultra-thin layer of conducting material less than  100  nm in thickness that can be formed as a single layer of high conductivity material such as Al, Cu, Au, Ru, Ta, CuAu, CuAg, NiCr, Rh and multilayers of these materials such as multiple laminations of (NiCr/Cu), formed to a thickness of approximately  100  nm or less and a width between approximately 100 and 1000 nm. and is formed in accord with the method of this invention. It is further noted that the separation between the read and write word lines is kept as small as possible to maintain the strength of the write word line magnetic field at the cell element free layer. A separation of approximately 100 nm, no greater than the thickness of the ultra-thin lines is preferable.  
         [0041]     Referring now to  FIG. 1   d,  there is shown an alternative embodiment in which the multi-layered MTJ cell element ( 50 ) is formed below orthogonally directed, vertically separated ultra-thin word ( 10 ) and bit ( 20 ) lines of the invention. The two lines extend in vertically separated horizontal planes, crossing over each other but insulated from each other and forming, thereby, an intersection below which the cell is located. Unlike the configuration shown schematically in  FIG. 1   a,  the word line ( 10 ), while still directed perpendicularly out of the figure plane, is now formed above both the bit line ( 20 ) and the cell element and is insulated from the bit line ( 15 ) by approximately 100 nm of insulating material. The bit line ( 20 ), directed transversely to the word line, is directly above the cell element ( 50 ) and contacts an upper surface thereof. The conducting electrode, (alternatively denoted a read-word line), used in read operations ( 59 ), is first formed, then the cell element ( 50 ) is formed on the conducting electrode. Thus, the conducting electrode contacts a lower surface of the cell, specifically the lower surface of the seed layer ( 51 ), that has been deposited on the electrode. Thus, in this embodiment, the cell is formed on the conducting electrode, with the seed layer being deposited first and successive deposited subsequently on the seed layer. During operation of the cell, the conducting electrode ( 59 ) will normally be connected by means of a conducting stud ( 60 ) to external circuitry that is used to determine the logic state of the MRAM cell. The bit line ( 20 ) and word line ( 10 ) can each be formed (in accord with the description of  FIGS. 2   a - e ) as a single layer of high conductivity material such as Al, Cu, Au, Ru, Ta, CuAu, CuAg, NiCr, Rh and multilayers of these materials such as multiple laminations of (NiCr/Cu), formed to a thickness of approximately 100 nm or less and a width between approximately 100 and 1000 nm.  
         [0042]     Referring again to the cell element ( 50 ), a seed layer ( 51 ) is formed on the conducting electrode ( 59 ) and promotes the high quality formation of subsequently formed layers of the cell. The seed layer can be a layer of NiCr or NiFe formed to a thickness between approximately 5 and 100 angstroms. A single pinned layer or, as in this embodiment, a synthetic ferrimagnetic pinned layer is formed on the seed layer. The synthetic layer includes an antiferromagnetic pinning layer ( 52 ), a second ferromagnetic layer ( 53 ), a coupling layer ( 54 ) and a first ferromagnetic layer ( 55 ). The antiferromagnetic layer pins the magnetization of the second ferromagnetic layer unidirectionally and the first ferromagnetic layer is magnetized in an antiparallel direction to that of the first layer. The first and second ferromagnetic layers are layers of CoFe formed to thicknesses between approximately 5 and 100 angstroms and matched so that the net magnetic moment of the configuration is substantially zero. The coupling layer is a layer of Rh, Ru, Cr or Cu of proper thickness to maintain strong antiparallel coupling between the magnetic moments. The antiferromagnetic pinning layer ( 52 ) can be a layer of PtMn, NiMn, OsMn, IrMn, PtPdMn, PtCrMn or FeMn of thickness between approximately 10 and 100 angstroms.  
         [0043]     A tunneling barrier layer ( 56 ) is formed on the first ferromagnetic layer ( 55 ) of the pinned layer. This layer is a layer of insulating material such as oxidized Al or an oxidized Al—Hf bilayer and is formed to a thickness between approximately 3 to 30 angstroms. A ferromagnetic free layer ( 57 ) is formed on the barrier layer. The free layer can be a single layer of ferromagnetic material, such as a layer of CoFe or NiFe formed to a thickness between approximately 5 and 100 angstroms or it can be a multilayer, comprising first and second ferromagnetic layers, magnetized in antiparallel directions and separated by a spacer layer of non magnetic but conducting material such as Rh, Ru, Cr or Cu, which is of the proper thickness to maintain strong antiparallel coupling between the two ferromagnetic layers. During formation of the cell it is advantageous to set the magnetic anisotropy direction of the ferromagnetic layers either perpendicular or parallel to the bit line. A capping layer ( 58 ) is formed on the free layer and completes the cell element ( 50 ). The capping layer can be a layer of Ru, or Ta or a multilayer of Ru/Ta formed to a thickness between approximately 5 and 100 angstroms. The bit line ( 20 ) is formed on the capping layer ( 58 ) of the cell element ( 50 ). A layer of insulating material ( 15 ) surrounds the cell and separates the write word line ( 10 ) from the bit line ( 20 ) by approximately 100 nm. The write word line ( 10 ), like the bit line, is an ultra-thin layer of conducting material less than 100 nm in thickness that can be formed as a single layer of high conductivity material such as Al, Cu, Au, Ru, Ta, CuAu, CuAg, NiCr, Rh and multilayers of these materials such as multiple laminations of (NiCr/Cu), formed to a thickness of approximately 100 nm or less and a width between approximately 100 and 1000 nm. and formed in accord with the method of this invention. It is further noted that the separation between the read and write word lines is kept as small as possible to maintain the strength of the write word line magnetic field at the cell element free layer. A separation of approximately 100 nm., no greater than the thickness of the ultra-thin lines is preferable.  
         [0044]     Referring to  FIG. 1   e,  there is shown, schematically, an array of MRAM cells, in which a plurality of cell elements ( 50 ) (two being shown), each element being identical to the cell element in  FIG. 1   b,  is formed between a common word line ( 10 ) and an individual bit line ( 20 ), in the configuration of  FIG. 1   b.  The word line is then connected to a single accessing transistor (not shown) by a connecting conductor ( 60 ). Each cell, of which only two are shown for clarity and both are labeled ( 50 ), is formed contacting a separate bit line, labeled ( 20 ), which is directed out of the plane of the figure. The upper surface of the cell element, which in this configuration is the seed layer ( 51 ), contacts the lower surface of the bit line ( 20 ) and the lower surface of the cell element, which is the capping layer ( 58 ), contacts the upper surface of the word line ( 10 ). There is no separate electrode, such as that denoted by ( 59 ) in  FIG. 1   a.  The word line ( 10 ) and the bit lines ( 20 ) are formed in accord with the method of the invention to be described below with reference to FIG&#39;S.  2   a - d.  In this configuration, all the cells contacting the common word line are accessed by a single transistor. It is noted that this array can be inverted, so that the word line is above the bit lines, the cell element has its layers inverted and the accessing transistor is above the word line.  
         [0045]     Referring to  FIG. 1   f,  there is shown an array of two MTJ MRAM cells, each of which can be formed in the configuration of  FIG. 1   a.  In this array, each cell element ( 50 ) is placed between intersecting word ( 10 ) and bit ( 20 ) lines formed using the method of the present invention and wherein the same bit line ( 20 ) is common to each cell but a separate word line is above an individual cell element. An electrode ( 59 ) is formed contacting an upper surface of each cell and insulated ( 15 ) from the word line, and each electrode is connected to an accessing transistor (not shown) by a conducting line or stud ( 60 ). In this array configuration there would be one transistor for each cell. Since the cell elements within the array are formed in accord with the configuration described in  FIG. 1   a,  the conducting electrode ( 59 ) contacts the capping layer of the cell element ( 50 ), the bit line contacts the seed layer and the cell element ( 50 ) is formed exactly as shown in  FIG. 1   a.    
         [0046]     Referring to  FIG. 1   g,  there is shown an array of two MTJ MRAM cells, each of which can be formed in the configuration of  FIG. 1   d.  In this array, each cell element ( 50 ) is placed below intersecting word ( 10 ) and bit ( 20 ) lines formed using the method of the present invention and wherein the same bit line ( 20 ) is common to each cell but a separate word line ( 10 ) is above an individual cell element. Each cell is formed on an electrode ( 59 ), so the seed layer ( 51 ) of the cell is formed directly on the electrode. Each electrode is connected to an accessing transistor (not shown) by a conducting line or stud ( 60 ) connected to the electrode. In this array configuration there would be one transistor for each cell. Since the cell elements within the array are formed in accord with the configuration described in  FIG. 1   d,  the bit line ( 20 ) contacts the capping layer of the cell element ( 58 ).  
         [0047]     Referring to  FIG. 1   h,  there is shown an array of two MTJ MRAM cells, each of which can be formed in the configuration of  FIG. 1   c.  In this array, each cell element ( 50 ) is placed between intersecting word ( 10 ) and bit ( 20 ) lines formed using the method of the present invention and wherein the same bit line ( 20 ) is common to each cell but a separate word line is below each individual cell element. Each cell is formed on a conducting electrode ( 59 ), which is itself formed above a word line ( 10 ) and insulated from the word line. Each electrode is connected to an accessing transistor (not shown) by a conducting line or stud ( 60 ). In this array configuration there would be one transistor for each cell. Since the cell elements within the array are formed in accord with the configuration described in  FIG. 1   c,  the bit line ( 20 ) contacts the capping layer of the cell element ( 58 ). It is noted that the actual fabrication of the ultra thin bit lines and word lines used to form an array proceeds in accord with the method of the invention as described in FIG&#39;S.  2   a - e  below.  
         [0048]     Referring now to FIG&#39;S.  2   a - e,  there are schematically shown several of the steps involved in fabricating the bit or word lines of the present invention. The extreme thinness of the lines not only accomplishes the object of the invention, which is to provide an adequate switching field with a smaller current, but they also can be fabricated in an easier fashion than conventional thicker lines since less ion-beam etch (IBE) trimming and CMP polishing is required. It is important to note that the ultra-thin word and bit lines are formed on a planar substrate.  
         [0049]     Referring first to  FIG. 2   a,  there are shown the first of the process steps required to form the ultra-thin word or bit lines of the present invention. First a thin conducting layer ( 100 ) is deposited over a substrate ( 90 ) having a substantially planar upper surface, the conducting layer being deposited to the desired final thickness of the word or bit line by a process of sputtering, ion-beam deposition (IBD) or chemical vapor deposition (CVD). It is noted that the substrate may be a dielectric layer having a planar upper surface or a dielectric layer that includes embedded MTJ MRAM cell elements whose upper surfaces are exposed and are co-planar with the planar upper surface of the dielectric layer, such as is the case in the bit line of FIG&#39;S.  1   c  and  1   d.  When the bit or word line is meant to contact a surface of a cell, as in  1   c  and  1   d,  the exposed cell surface is co-planar with the planar surface of the surrounding dielectric layer. Alternatively the substrate may be a dielectric layer that is formed over a conducting electrode, such as ( 59 ) in  FIG. 1   a  or a dielectric layer that is formed over a previously formed word or bit line, such as ( 15 ) formed over ( 20 ) in  FIG. 1   d.  The substrate in  FIG. 2   a  is shown here devoid of any detail. A layer of photoresist ( 200 ) is then formed on the conducting layer.  
         [0050]     Referring to  FIG. 2   b,  there is shown the photoresist layer now patterned ( 210 ) by a photolithographic process such as is well known in the art. The patterning produces a strip (or a plurality of strips if more than one line is to be formed) that has the width of the line to be formed and extends in the proper line direction.  
         [0051]     Referring to  FIG. 2   c,  there is shown the patterned photoresist ( 210 ) having been used as a mask for an ion-beam etch (IBE) or reactive ion etch (RIE), to remove peripheral portions of the conducting layer and leave behind the desired word/bit line ( 150 ) beneath the photoresist pattern. The photoresist will then be removed (not shown) to leave only the word/bit lines ( 150 ) properly arranged over the substrate ( 90 ).  
         [0052]     Referring to  FIG. 2   d,  there is shown the formation of  FIG. 2   c  wherein an insulating refill layer ( 250 ) has been deposited to fill the spaces between the word/bit line just formed and any others (not shown). In this form, MTJ cells may be formed over the word/bit lines or an orthogonal set of word lines may be formed over these lines if they are bit lines. If the lines just formed ( 150 ) are bit lines (running orthogonally to the figure plane), then the orthogonal lines formed over them will be word lines (running within the figure plane).  
         [0053]     Referring finally to  FIG. 2   e,  there is shown, just as an example, a substrate ( 90 ) that includes an MTJ MRAM cell ( 50 ), so that the ultra-thin word line ( 150 ), formed in accord with FIG&#39;S.  2   a - d,  is positioned on (contacting) the upper surface of the cell. It should be clear to one skilled in the art how other ultra-thin intersecting word/bit line configurations can be formed at the location of cell elements.  
         [0054]     For uniformity and reproducibility it is required that the surfaces of the bit or word lines ( 150 ) not be smoothed or reduced in thickness by a process step of chemical mechanical polishing (CMP). Such polishing will introduce undesirable thickness variations in the lines, which variations, in turn, will adversely affect the maintaining of a sufficiently small and uniform distance between the lines and the free layer within the MTJ cell. The thickness variations result because of the difficulty in controlling the CMP lapping process and obtaining an accurate stopping point. Since CMP is therefore ruled out, the bit lines cannot be made thick, because a thick deposition will inevitably have a highly non-planar upper surface, which, without CMP, is then a cause of subsequent problems, including inaccurate photoresist patterning, poor line continuation and electro-migration. Thus, the thin deposition of the present invention eliminates the requirement of a disadvantageous CMP process and simultaneously provides the increased magnetic fields required.  
         [0055]     As is understood by a person skilled in the art, the preferred embodiments of the present invention are illustrative of the present invention rather than being limiting of the present invention. Revisions and modifications may be made to methods, processes, materials, structures, and dimensions through which there is formed an provided an MTJ MRAM cell, comprising a cell element formed at the intersection of an ultra-thin bit line and an ultra-thin word line, while still forming and providing such an MRAM cell, in accord with the present invention as defined by the appended claims.