Abstract:
Multiple properties of plasmonic assemblies are determined by their geometrical organization. This patent focuses on the formation of Janus structure of the asymmetric assembly structure of the gold nanorods and gold nanoparticles. Chiral structure of gold nanorods and gold nanoparticles can be obtained through the characterization of optical spectra of the Janus structure. And it opens the door for the explanation of the mechanism of the chirality, plays a strong guiding role in the negative refractive material above and has good application prospects.

Description:
TECHNICAL FIELD 
       [0001]    The present invention relates to nanoparticle assembly and the intense optical property of these superstructures. Specifically, the invention relates to collective chirality of binary plasmonic nanoparticles Janus assemblies. 
       BACKGROUND OF THE INVENTION 
       [0002]    In recent years, the gold nanomaterial assemblies with specific shapes possess unique properties which are different from those of monodisperse gold nanomaterials and gold materials, making them extremely bright prospect. Therefore, the self-assemblies of gold nanomaterials attract widespread attentions of nano-scientists around the world. Gold nanomaterials mainly include gold nanoparticles and gold nanorods. These nanomaterials possess specific optical absorption, light scattering and Raman enhancement effects depending on the size and shape, which make these two nanoparticles the most widely used materials in the nanoscience and nanotechnology research field, especially the gold nanorods. 
         [0003]    A single gold nanorod has two localized surface plasmon resonance peaks, which are a longitudinal plasmon resonance peak (near infrared or infrared region) and a transverse plasmon resonance peak (around 520 nm), due to the two resonant directions of conduction band electrons on the rod. And gold nanorods, with spatial geometry and chemical anisotropy, can achieve strong light absorptions in the visible or near infrared region by adjusting the aspect ratio of gold nanorods (the ratio of length to diameter of the gold nanorods). Theses unique properties make gold nanorods to be the excellent raw material for the controllable self-assembly, and then provide a good model for theoretical analysis of the self-assembly materials. Thus the physical and chemical properties of macroscopic materials can be better understood by studying nature of the controllable, dynamic self-assembled materials. Notably to mention, the spatial geometry and chemical anisotropy are the key factors for the nanomaterials to achieve controllable self-assembly. 
         [0004]    Janus particle was proposed by De Gennes in 1991 for the first time in the Nobel award ceremony, in order to describe a particle with different spherical nature. The difference of this nature is mainly due to the different spherical geometry of the particle. And Janus particle now attracts extensive attention of the scientific community, due to its unique asymmetric structure and properties, making it strong application prospects. Recently, the preparation methods of Janus particle are mainly including microfluidic surface modification synthesis, topology selection, the template self-assembly synthesis, controllable phase separation, and controllable surface nucleation. Self-assembly of gold nanomaterials has very strong plasmon coupling effects, leading to the strong electromagnetic enhancements. And binary plasmonic self-assemblies show fascinating properties different from that of the two separate nanomaterials, really makes the assembly of nanoparticles Janus wonderful and brilliant. Surprisingly, there is no reported method that successfully achieve high-yield binary nanoparticle Janus assemblies yet. Therefore, it is particularly important to establish a method to obtain high-yield binary nanoparticles Janus assemblies. 
       SUMMARY OF THE INVENTION 
       [0005]    Accordingly, one aspect of the present invention is directed to a method of preparing the asymmetrical DNA functionalized gold nanorods (Au NRs) coupling with the enzymatic ligation and the magnetic separation of the superstructures of Au NRs and magnetic NPs. 
         [0006]    Another aspect of the present invention is directed to the formation of binary plasmonic nanoparticles Janus assemblies of Au NPs and Au NRs resulting in the hybridization of DNA1 (SEQ ID NO: 1) and DNA4 (SEQ ID NO: 4) strands. 
         [0007]    A further aspect of the present invention is directed to the measurement chiral property of the formed binary Janus nanoparticle assemblies. 
         [0008]    The present invention provides the fabrication of the chiral binary plasmonic nanoparticles assemblies, which involves the preparation of Au NPs and Au NRs, the modification of DNA with the Au NRs, Au NPs and magnetic nanoparticles, the formation of binary nanoparticles Janus assemblies. And the fabrication method comprises: 
         [0009]    a) Gold nanoparticles are synthesized by reduction of HAuCl 4  using trisodium citrate; 
         [0010]    b) Gold nanorods are prepared by a seed-mediated growth procedure; 
         [0011]    c) The synthesized gold nanoparticles based on step a), couple with sulfydryl modified DNA to form the complexes of Au NP-DNA; 
         [0012]    d) The prepared gold nanorods based on step b), are modified with DNA on the sides of Au NR; 
         [0013]    e) Magnetic nanoparticles (MNP) conjugate with amino modified DNA by an EDC procedure; 
         [0014]    f) The prepared Au NR-DNA complexes hybridize with MNP-DNA complexes, according to steps d) and e), forming the assembly of gold nanorods and magnetic nanoparticles; 
         [0015]    g) After adding DNA4 (SEQ ID NO: 4) strand complementary to the remaining sequence of DNA3 (SEQ ID NO: 3) modified on the magnetic nanoparticles, the DNA ligase is added for asymmetric extension of DNA modified on the gold nanorods; 
         [0016]    h) The gold nanorods are recovered through magnetic separation following the dissociation of superstructures of gold nanorods and magnetic nanoparticles formed in the step g) at the melting temperature; 
         [0017]    i) Based on steps c) and h), the prepared Au NP-DNA complexes hybridize with Au NR-DNA complexes to obtain binary plasmonic nanoparticles Janus assemblies; 
         [0018]    j) The prepared binary nanoparticles Janus assemblies based on step i) are charactering by transmission electron microscopy (TEM), circular dichroism spectra (CD) as well as synchrotron small-angle X-ray scattering (S-SAXS). 
     
    
     
       BRIEF DESCRIPTION OF THE DRAWINGS 
         [0019]      FIG. 1  is a schematic view illustrating the synthetic method for the binary plasmonic nanoparticle Janus assemblies; 
           [0020]      FIG. 2  shows the TEM images of the binary plasmonic NPs assemblies samples; 
           [0021]      FIG. 3  shows S-SAXS experimental results and modeling patterns with scaling factor 0.2. (A: experimental results, the insert: amplification curve in the range of 0.021≦q≦0.1; B: S-SAXS modeling patterns respectively.) The numbers in Angstroms in  FIG. 2B  means the main peak to confirm the relative size of the assemblies; 
           [0022]      FIG. 4  illustrates the CD spectrum of binary plasmonic NPs Janus assemblies; and 
           [0023]      FIG. 5  shows a table listing the sequence and length of DNA involved in the present invention. 
       
    
    
     DETAILED DESCRIPTION OF THE INVENTION 
       [0024]    The detailed information of the invention is further described through the steps listed in the following text. All the reagents involved are analytical grade purify. Notably to mention that the following detailed steps are as exemplifications, while the present invention is not limited to the content as follows: 
         [0025]    Step 1: Synthesis of Gold Nanoparticles 
         [0000]    Au NPs are synthesized by reduction of HAuCl 4  using trisodium citrate. Typically, an aqueous trisodium citrate solution (2.5 mL, 1% by weight, freshly prepared) is quickly added to a boiling aqueous solution of HAuCl 4  (100 mL, 0.25 mM) under vigorous stirring and reflux. After several minutes, the color of the solution changes from pale yellow to brilliant red. After boiling for 10 minutes, the heat source is removed to allow the reaction solution to cool to room temperature, diluting the solution to 100 mL, and it was subsequently stored at 4° C. 
         [0026]    Step 2: The Synthesis of Gold Nanorods 
         [0000]    (1) Au NRs with an aspect ratio of approximately 3 are prepared by a seed-mediated growth procedure. Initially, a 2 g/L HAuCl 4  (0.1 mL) is added to 0.2 M CTAB solution (1 mL) that is kept at a constant temperature of 28.0° C. Immediately, a deep-orange solution is obtained. Then, freshly prepared 0.01M NaBH4 solution (0.12 mL) is added in one portion, and the solutions are mixed by inversion. After stirring rapidly for 2 min, the solution turns pale-brown in color.
 
(2) To prepare the Au NR, 2 g/L HAuCl 4  (5 mL) is mixed with 0.2 M CTAB solution (1 mL) and 4 mL of water. After that, 65 μL of 0.1 M ascorbic acid solution and 0.125 mL of 0.01M AgNO 3  solution are added to the reaction media followed by mixing for 2 min, which resulted in a colorless solution. Finally, 0.05 mL of the seed solution is added with gentle mixing for about 20 seconds. The Au NRs can be used after aging for 4 hours.
 
         [0027]    Step 3: Preparation of Single-Strand DNA-Modified Au NPs 
         [0000]    (1) The prepared Au NPs (10 mL) based on step 1, are centrifuged (10000 rpm) for 10 min, followed by dispersing the precipitate with 1 mL of 0.01 M pH 8.0 phosphate buffers, while maintaining a SDS concentration of 0.01%. It is stored at 4° C. before application.
 
(2) DNA1 oligomers (SEQ ID NO: 1) are added to Au NPs in 0.01 M phosphate buffer with 0.01% sodium dodecylsulfate (SDS). The solution of DNA1 and Au NP is incubated at room temperature for 20 min. The concentration of NaCl is increased to 0.05 M using 2 M NaCl and 0.01 M pH 8.0 phosphate buffers, while maintaining a SDS concentration of 0.01%. The solution of DNA and Au NP is then sonicated for 10 seconds followed by a 20 min incubation period at room temperature. This process is repeated for one more increment of 0.01 M NaCl and for every 0.1 M NaCl increment thereafter until a concentration of 0.4 M NaCl is reached. The ionic strength adaptation process was followed by incubation overnight at room temperature.
 
(3) To remove the excess of DNA1 (SEQ ID NO: 1), Au NPs are centrifuged, and the supernatant is removed, leaving a pellet of Au NPs at the bottom. The particles are then resuspended in 0.01% SDS. This washing process is repeated for one more time. The conjugate was stored at 4° C.
 
         [0028]    Step 4: Fabrication of Single-Strand DNA-Modified Au NRs 
         [0000]    The prepared Au NRs (100 μL) based on step 1, is reacted with 10 μL of 10 μM DTT for 12 h, followed by addition of 40 μL of DNA2 (SEQ ID NO: 2) to modify the sides of Au NRs. After stirring for 12 h, the solution is centrifuged at 5000 rpm for 6 min. And the supernatant is removed. The precipitate particles are then resuspended in 100 μL of water. This washing process is repeated for one more time before storing at 4° C. 
         [0029]    Step 5: Fabrication of Single-Strand DNA-Modified MNPs 
         [0030]    Carboxyl-modified magnetic nanoparticles of 200 nm are synthesized through solvothermal method. A volume of 0.5 mL MNP prepared above, N-hydroxysuccinimide (NHS) (0.62 mg) and N-ethyl-N′-[(3-dimethylamino) Cyl] carbodiimide hydrochloride (EDC-HCl) (1.13 mg) are stirred for reaction at room temperature overnight, and then centrifugalize, remove the precipitate, add 15 μL 100 μM DNA3 (SEQ ID NO: 3) to the supernatant for reaction under stir at 4° C. overnight. After reaction, the solution is separated by the magnetic separation to remove the supernatant. Then add the PBST as the washing liquid, this washing process is repeated for one more time. Finally, resuspend in 1 mL of 0.02 mol/L pH 7.6 Tris buffer and stored at 4° C. 
         [0031]    Step 6: Self-Assembly of Au NRs and MNPs 
         [0000]    The prepared asymmetric modified gold nanorods 10 μL and magnetic nanoparticles-DNA3 (SEQ ID NO: 3) complex 50 μL are added into 60 μL pH7.5 0.01M Tris-HCl hybridization buffer, maintaining 0.01% SDS, 10 mM MgCl 2 , and react for 12 hours under shake condition. Finally, the complex of gold nanorods and magnetic nanoparticles are separated using magnetic separation, removal of the free gold nanorods. 
         [0032]    Step 7: Asymmetric Extension of DNA Modified on the Au NRs 
         [0000]    A 4 μL of DNA4 (SEQ ID NO: 4) (100 μM) is added to complex assemblies of Au NRs and MNPs prepared in the above step 6, under stirring for 5 h at room temperature. And then, 1 μL ATP (100 μM) and T4 DNA ligase (4000 units of final enzyme activity/mL) are shaking for 5 h to allow for incubation. Finally, complexes of asymmetric extension modified DNA of Au NRs and MNPs after magnetic separation under the addition magnetic field. 
         [0033]    Step 8: The Dissociation of Complexes of Au NRs and MNPs 
         [0000]    The superstructure complexes of Au NRs and MNPs are dissociated due to incubation at 90° C. for 10 minutes. And then MNPs are removed through magnetic separation, the supernatant is centrifuged 8000 rpm for 10 minutes. Finally, the remained nanoparticles are resuspended in 10 μL of 0.01 M pH 8.0 phosphate buffer, maintaining 0.01% SDS, and stored at 4° C. 
         [0034]    Step 9: Formation of Binary Plasmonic Nanoparticle Janus Assemblies 
         [0000]    In order to form the binary Janus assemblies, 10 μL of asymmetric modified Au NRs are mixed with 50 μL of complex of Au NPs-DNA1 in 6 μL of 0.01 M Tris-HCl buffer (0.01% SDS, MgCl 2  20 mM, pH 8.0). The mixture was incubated for 12 hours at room temperature. 
         [0035]    Step 10: Structure Characterization and Simulation of Binary Plasmonic Nanoparticle Janus Assemblies 
         [0000]    (1) Following a 12-hour incubation of NPs and NRs resulting in the hybridization of DNA1 (SEQ ID NO: 1) and DNA4 (SEQ ID NO: 4) strands, NR and NP assemblies were structurally examined by transmission electron microscopy (TEM), circular dichroism (CD) spectra as well as synchrotron small-angle X-ray scattering (S-SAXS). The representative TEM images clearly demonstrate the conformations of the ensembles.
 
(2) To obtain detailed information about ensembles in solution, SAXS, as an indirect technique, can be used. Above the SAXS characterization experiments, there are two curves in the data: one is based on the gold nanorods and gold nanoparticles simply mixing without hybrid assembly, another one is based on the hybridization of gold nanorods and gold nanoparticles, forming Janus structures. In order to confirm the assembly of specific structures in solution, we utilized the “Forcite” module in Materials Studio 5.5 to perform SAXS calculations. The calculations were based on the intensities of each hid reflection:
 
         [0000]        I ( hkl )= fn  cos 2( hxn+kyn+lzn )2+ fn  sin 2( hxn+kyn+lzn )2  (1)
 
         [0036]    Where hkl is equivalent to the scattering vector (q), fn is the scattering factor of atom n, and xn, yn, zn are the fractional coordinates of atom n. 
         [0037]    While the foregoing embodiments of the invention have been illustrated and described, it will be appreciated that various changes can be made therein without departing from the spirit and scope of the invention. 
         [0038]    The embodiments of the invention in which and exclusive properties or privilege is claimed are defined as follows.