Abstract:
A phase-shifting mask, having plateau and trench surfaces located on a major surface of the mask, has a defect in the form of an indentation region located on a plateau (or trench) surface. The mask is repaired with respect to the defect by spinning on the major surface of the mask a planarization layer for which dry-etching conditions exist at which this planarization layer anisotropically etches at the same rate as that of the mask substrate material--e.g., quartz. Then the portion of the planarization layer overlying the defect is dry-etched under those conditions, using in one embodiment a patterned protective masking layer, such as chrome, having an aperture overlying the defect. This aperture need not be precisely laterally aligned with the defect (unless the defect extends to an edge of the plateau surface). The etching is continued until it reaches a depth H beneath the level of the plateau (or trench) surface that is equivalent to a phase shift of 2n π radian, where n is an integer (preferably unity).

Description:
TECHNICAL FIELD 
     This invention relates to optical lithography, and more particularly to a method of repairing phase-shifting masks. Such masks typically are used in optical imaging systems for lithographically fabricating microminiature devices, such as semiconductor integrated circuits. These masks are also called &#34;reticles,&#34; particularly when used in optical focusing systems having lateral magnifications that differ from unity. 
     BACKGROUND OF THE INVENTION 
     Lithographic masks have a pattern of features that are desired to be imparted into a workpiece, in order to fabricate, for example, semiconductor integrated circuits or other microminiature devices in the workpiece. Typically, the features of the mask are transferred to the workpiece by first placing the mask on the object plane of an optical imaging system that focuses optical radiation propagating through the mask, in order to transfer the features of the mask to a photoresist layer either overlying the workpiece or overlying a layer of material which overlies the workpiece. Then the photoresist layer is developed in order to form a patterned photoresist layer. Thus, the pattern of the mask features is transferred to the photoresist layer, with a magnification (greater to, equal to, or less than unity) that depends upon the design of the optical imaging system. The resulting pattern of the photoresist features is used to define features in the workpiece--such as edges of ion implant regions, edges of removed portions of the layer(s) of material overlying the workpiece to be removed, or edges of portions of the workpiece itself--all these edges thus being in accordance with the edges of the mask features. 
     A limiting factor in thus transferring the mask features to the photoresist layer is diffraction caused by the non-vanishing wavelength λ (in the vacuum) of the optical radiation that is used in the optical imaging system. As a result of this diffraction, the edges of the images formed by the optical focusing system become less sharp than desired, whereby the resolution of the mask features when focused on the photoresist layer deteriorates. To improve this resolution, phase-shifting masks have been proposed. In these masks, the phases of the optical radiation propagating through the mask are shifted by, say, φ radian in some regions relative to others. For example, a typical portion 9 (FIG. 1) of a prior-art phase-shifting mask (hereinafter, &#34;mask portion 9&#34;) has an opaque chrome (chromium) layer pair 13 located on a portion of the top substantially planar surface 12 of a raised (plateau) region 11 of a transparent, typically quartz, substrate 10. The region 11 has a width x and is thicker, by a distance h, than an adjacent &#34;trench&#34; region having a width w. The top surface 12 of the plateau region 11 which is substantially planar except for the presence of an indentation that forms an undesired defect region 21. As used herein, the term &#34;substantially planar&#34; refers to a situation in which any departures from planarity do not degrade, by more than desired amounts, the sharpness of images produced (e.g., in the photoresist layer) when the mask portion 9 is used in the optical imaging system. 
     The distance h corresponds to the optical phase shift φ (radian). Thus, (hn)/λ-hλ=φ, or h=φλ/(n-1), where n is the refractive index of the quartz. Typically, φ=π radian; so that typically, h=πλ/(n-1). When viewed from above, the contours of the chrome layer pair 13 depend upon the contours of the ultimately desired features in the workpiece (or in a layer overlying the workpiece). 
     One problem that can arise in using the phase-shifting mask portion 9 is the presence of the above-mentioned defect region 21. It should be understood that, in general, the height of the defect region 21 can vary from point to point (as indicated in FIG. 1); that is, the surface of the indentation region can have an irregular shape, such as was formed during earlier processing. Such a defect region can also be located in the plateau region 11. Also, there can be a plurality of such defect regions, each typically (but not necessarily) being located in a different plateau or trench region. 
     Obviously, when the mask portion 9 is used in the optical imaging system, the presence of the defect region 21 can deteriorate the image formed by the mask portion 9 on the photoresist layer located on the workpiece. Rather than discard entirely this mask 9 having such a defect region 21 (the mask being otherwise very valuable) it is desirable to have a method of repairing the mask, i.e., a method of removing the defect region 21 without damaging the rest of the phase-shifting mask 9 (not shown). 
     In the Fourth Hoya Photomask Symposium, held in Japan, a paper entitled &#34;Submicron Photolithography using Phase-Shifting Mask&#34; was delivered by N. Hasegawa et al. In that paper, a method was disclosed for repairing an indentation defect region in a phase-shifting mask. In accordance with at method, the defect region was present in a π-radian optical phase-shifting layer (&#34;main shifter&#34; layer) underneath which there was located another π-radian phase-shifting layer (&#34;sub shifter&#34; layer); and a barrier layer was located underneath the sub shifter layer--the barrier layer thus intervening between the bottom surface of the sub shifted layer and the top surface of a transparent substrate. This barrier layer served as an etch-stopping layer. To repair the mask, a region of both the main and the sub shifter layers laterally encompassing the defect region was etched down to the barrier layer--whereby the resulting phase shift in this (etched) region became equal to 2π, which of course is equivalent to a zero phase shift. In this way, when the mask is used in the optical imaging system, optical image deteriorations caused by the indentation defect region are ameliorated. 
     The need for the barrier layer in that method, however, entails a need for depositing on this barrier layer some sort of transparent material for the π and/or 2π-radian phase-shifting layers, such as chemically vapor deposited (CVD) silicon dioxide layers. The need for these deposited oxide layers complicates the fabrication of the mask&#39;s substrate, as well as the processing and etching of the chromium layer 13. This ned for deposited oxide layers also complicates any required subsequent cleaning of the surface of the mask portion 9--because a chromium layer is not as adherent to a deposited silicon dioxide layer as it is to a quartz substrate; and a deposited oxide layer is not as resistant as quartz to the cleaning procedures used for cleaning the mask. Moreover, the need for these deposited oxide layers has the disadvantage of requiring very close matching of the refractive indices of the various layers. Therefore, it would be desirable to have a method of repairing indentation defect regions without the need for an intervening etch-stopping layer. 
     SUMMARY OF THE INVENTION 
     In order to repair the phase-shifting mask portion 9 (insofar as the indentation defect region 21--located on the surface 12 of the plateau region 11--is concerned), a planarization layer, such as a spun-on polymer layer, is formed on at least the entire width x of the plateau region 11, and typically on the entire top surface of the mask (including all plateau and trench regions). This planarization layer advantageously has a substantially planar top surface, and it advantageously is selected such that there exist dry-etching conditions at which it etches, advantageously substantially anisotropically, at substantially the same rate as that of the substrate (e.g., quartz). As used herein the term &#34;substantially&#34; means that departures from perfection do not degrade, by more than desired amounts, the sharpness of images produced when the mask portion 9 is used in the optical imaging system. Then a protective layer, such as a (commercial grade) chrome layer, is deposited on this planarization layer, the protective layer being supplied with an aperture which is laterally &#34;aligned&#34; with--i.e., which laterally overlies--the defect region. 
     The lateral extent of the defect region can have been determined by an earlier conventional two-dimensional scanning optical microscope inspection of the mask. The &#34;alignment&#34; of each such aperture with its underlying defect region need not be precise (unless the defect region extends to an edge of the plateau region), so long as the aperture extends laterally everywhere farther than the defect region, advantageously by a safety margin, s. The planarization layer is substantially anisotropically etched (in the region where it underlies the aperture in the protective layer) until the etching process reaches the level of the surface 12 of the plateau region 11 plus a depth H. Advantageously, this depth H is substantially equal to the equivalent of a phase shift of 2nπ radian, where n is an integer, preferably one, the phase shift being measured with respect to optical radiation propagating through the mask in the same way as in the optical imaging system--i.e., propagating perpendicular to the surface of the plateau (or trench) region--and the optical radiation having the same wavelength as that to be used in the optical imaging system. At that point in time, the etching process is terminated (stopped). To determine this etch-stopping point in time, end-point etching at a dedicated place (which lacks a defect region) located on the mask can be used. Finally, the planarization layer is removed, typically by means of a wet solvent (whereby the protective layer overlying the planarization layer automatically is removed, or the protective layer can be independently removed first). In this way, a repaired phaseshifting mask is obtained--without the need for any intervening barrier or etchstopping layer, or other intervening layer, in the finished mask portion 9. 
     Because of the substantial equality of the etching rates of the planarization layer and the (e.g., quartz) substrate, the top surface of the etched (&#34;cut&#34;) region in the substrate will be substantially planar. Also, because the height H is the equivalent of a phase shift of 2nπ radian, the thus etched (&#34;cut&#34;) region will impart to a beam of light, propagating along the normal to the top surface of the substrate, a phase shift substantially equivalent to zero. Hence, the cut will not substantially deteriorate the sharpness of the image when the thus repaired mask portion 59 (FIG. 5) is used in the optical imaging system. 
     In practicing this invention only two-dimensional (lateral) inspection of the mask--and not three-dimensional inspection--is thus repaired to ascertain the location and extent of each defect region. Moreover, only one-dimensional control (etch-stopping point detection) over the anisotropic etching is required. Also, the technique of this invention can similarly be used to repair the mask in cases of indentation regions that are located in regions other than plateau regions, such as in localized areas of trench regions. 
     In case there is a plurality of defect regions, each typically (but not necessarily) located on the surface of a separate plateau (or trench) region, the technique of this invention can be used to repair simultaneously all of the defect regions located in the plateau regions (or in the trench regions), simply by forming a plurality of apertures in the protective layer, each aperture overlying a separate defect region. 
    
    
     BRIEF DESCRIPTION OF THE DRAWING(S) 
     This invention, together with its features, characteristics, and advantages, may be better understood from the following detailed description when read in conjunction with the drawing in which: 
     FIG. 1 is a cross-section elevational view of a portion of a prior-art phase-shifting mask to be repaired in accordance with a specific embodiment of the invention; 
     FIGS. 2-5 are cross-section elevational views of various stages in a method of repairing the phase-shifting mask shown in FIG. 1 in accordance with a specific embodiment of the invention. 
     Only for the sake of clarify, none of the drawings is to any scale. 
    
    
     DETAILED DESCRIPTION 
     FIG. 1 depicts the phase-shifting mask portion 9 to be repaired and thus to form a repaired phase-shifting mask portion 59 (FIG. 5). The mask portion 9 includes a transparent essentially quartz substrate 10 having a raised plateau region 11 with a top surface 12 and a width x. As used herein, the term &#34;essentially quartz&#34; includes commercial grade quartz, viz., non-pure quartz as is commercially available. The substrate 10 also has a trench (thinner) region with a top surface 14 and a width w. The top surface 14 of the trench region is located at a depth h beneath the top surface 12 of the plateau region 11. A patterned opaque chromium layer pair 13 (hereinafter, simply &#34;the chrome layer 13&#34;) is located on the top surface 12 of the plateau region 11. Typically, the depth h corresponds to a phase-shift of π radians. The purpose of the chromium layer 13 is to supply an optically opaque portion for the phase-shifting mask portion 9, as known in the art. 
     The phase-shifting mask portion 9 has an indentation defect region 21 illustratively located at the top surface 12 of the plateau region 11. It is desired to repair the mask portion 9 insofar as this defect region 21 is concerned. This defect region 21 can have a variable height--i.e., a height that varies with lateral (two-dimensional) position along the surface 12. 
     The outermost lateral (two-dimensional) contours of the defect region are determined first, such as by an inspection with a two-dimensional scanning optical microscope. 
     Referring now to FIG. 2, there are then successively formed on the top surface of the mask portion 9, as well as typically on the top surface of the rest of the mask (not shown), layers 22, 23, and 24. Layer 22 is a planarization layer, typically a spun-on, essentially polymer layer, such as a polycresolformaldehyde or a polyvinylphenol, as are commercially available. Advantageously this planarization layer possesses anisotropic etching conditions for which it etches at substantially the same rate as that of the (quartz) substrate 10. Layer 23 is essentially chromium (possibly intermixed with some chromium oxide or other impurities) having a uniform thickness typically equal to about 0.03 μm; and layer 24 is a positive or negative tone resist layer--preferably positive tone--having a uniform thickness equal to about 0.5 μm. The thickness of planarization layer 22 at areas overlying the surface 12 of the plateau region 11 is typically equal to about 1 μm. 
     The resist layer 24 is exposed to a patterned beam of actinic radiation (ion beam, photon beam, or electron beam), the two-dimensional contours of the pattern being substantially the same as those of the previously determined (outermost) two-dimensional contours of the defect region 21 plus a non-zero safety margin having a width equal to s. Thus this alignment of the contours of the actinic radiation with those of the defect region need not be precise, so long as there is any safety margin (provided that the defect region 21 does not extend to an edge of the plateau region). The width s of this safety margin depends on the accuracy of the method used for ascertaining the (outermost) contours of the defect region 21, as well as depends on the width x of the plateau region 11. Typically this width s is about 0.5 μm or less. 
     Next, the resist layer 24 is developed, typically by a wet development, whereby it becomes a patterned resist layer. This pattern of the thus patterned resist layer 24 is then transferred to the chromium layer 23, typically by means of a standard technique such as anisotropic dry etching with a gas mixture of Cl 2  and O 2 . Alternatively, by virtue of the relatively small thickness of the chromium layer 23 with respect to undercut tolerance, isotropic wet etching--for example, with ceric ammonium nitrate solution--can also be used without inducing an unwanted undercut of the chrome feature located underneath the resist features. The thus patterned chromium layer 23 will have an aperture of width equal to u overlying the defect region 21, with u being equal to the width of the defect region 21 plus twice the safety margin s. 
     Next, the top surface of the mask portion 9, together with a dedicated auxiliary portion 39 (shown in FIG. 3, but not shown in FIGS. 1, 2, and 5) of the mask which is being repaired is subjected to substantially anisotropic dry etching procedure at which the planarization layer 22 and the (quartz) substrate 10 (including its plateau region 11) etch at substantially equal rates. FIG. 3 shows an intermediate stage of this etching procedure. Typically, this etching procedure is implemented with gaseous CF 4 , or gaseous CHF 3 , or a gaseous mixture of both, or a gaseous mixture of either or both with O 2 . As a result, the (patterned) resist layer 24 tends to be removed and therefore is not shown in FIG. 3. 
     The auxiliary portion 39 (FIG. 3) of the mask which is being repaired has an auxiliary plateau region whose top surface 47 has a width that is advantageously equal to the width x of the plateau region 11 located in the mask portion 9--in order to facilitate fabrication of substantially equal thicknesses of the portion of the planarization layer 22 overlying the plateau region that is located in the auxiliary portion 39 and the portion of the planarization layer 22 overlying the plateau region that is located in the mask portion 9. This equality of these thicknesses ensures proper etch-stopping functioning by the auxiliary mask portion 39. 
     As viewed from above, the auxiliary plateau region typically has contours in the form either of squares or of parallel lines. The aperture in the chromium layer 23 located in the auxiliary mask portion 39 has a width v that is advantageously equal to u. The purpose of the auxiliary plateau region is to act as an etch stop (indicator), as more fully explained below. 
     Advantageously further, in order to enhance the intensity of the etch stop indication, there is a plurality of such auxiliary plateau regions, such that the total surface area covered by the apertures (each of width v) in the auxiliary mask portion 39 is equal to approximately 1 cm 2 . Advantageously, each of these auxiliary plateau regions has the same width x as that of the plateau region 12 located in the mask portion 9. Moreover, these auxiliary plateau regions advantageously are physically separated from one another and thus are not coalesced into a single plateau region, in order that the thickness of the planarization layer 22 overlying the top surface 12 of plateau region located in the mask portion 9 substantially approximates the thickness of the planarization layer 22 overlying the plurality of auxiliary plateau regions, and hence again in order to ensure proper etch-stop functioning by the auxiliary mask portion 39. 
     The anisotropic etching of the planarization layer 22 thus forms cuts of widths u and v therein overlying the mask portion 9 and the auxiliary mask portion 39, respectively. This etching is terminated (FIG. 4) at an elapsed time T after a signal from the auxiliary trench region indicates that the anisotropic etching has progressed to the point that it has just reached the top surface 47 of the auxiliary plateau region(s) located in the (now) cut auxiliary portion 49 and hence automatically also has just reached the top surface 12 of the plateau region of the mask portion 9. This signal can be generated, for example, by detection of the light emitted in the plasma caused by radioactive transitions of decomposition products produced during the anisotropic etching and emanating only from the planarization layer 22 in the plurality of auxiliary plateau regions. 
     The aforementioned elapsed time T is made substantially equal to H/V, where H is equivalent to a phase shift 2nπ (with n being an integer, preferably one), and where V is the (anisotropic) etching rate in the substrate 10 (including the plateau region 11. Thus (FIG. 4) this etching will produce a cut of width v penetrating through the surface 47 of the auxiliary plateau region located in the now cut auxiliary mask portion 49, this cut having a bottom surface 48 located at a depth H beneath the surface 47 of this auxiliary plateau region, where H is the equivalent of a phase shift of 2 nπ. Likewise, this etching will produce a cut of width u penetrating through the surface 12 of the plateau region 11 located in the mask portion 9, this cut having a bottom surface 32 located also at a depth H beneath this surface 12. 
     Because of the substantial equality of etch rates of the planarization layer 22 and of the substrate 10, as well as the substantial equality of the thicknesses of the respective portions of this planarization layer that are located overlying the plateau regions located in the mask portion 9 and in the auxiliary portion 39, the above-described anisotropic etching will have repaired the mask portion 9 the defect region 21, as is desired--that is, in such a way that the surface 32 of the bottom of the cut is substantially planar, viz., with a depth everywhere substantially equal to H, where H is equivalent to a phase shift equal to 2 nπ. 
     Finally the remaining (remnants of the) planarization layer 22 can be removed, typically by means of a wet solvent, whereby the chromium layer 23 is also automatically removed (FIG. 5) and the desired repaired mask portion 59 is formed. 
     In case the indentation defect region is located on the top surface 14 of the trench region, this defect region can be removed in the same way as descried above, except that now the apertures in the planarization layer 22 will be located overlying both this defect region itself (plus the safety margin) and trench regions located in the auxiliary portion 39. 
     In case there is a plurality of defect regions to be repaired, each defect region being located typically in a separate plateau (or trench) region, then the width u of a specific aperture overlying a specific defect region is still advantageously made equal to the width of the specific defect region plus twice the safety margin s. In the auxiliary portion 39, the widths v of the apertures in the chromium layer 23 and hence of the cuts in the planarization layer 22 then typically are all made equal to about 2 μm. Also, as viewed from above, the outer contours of these apertures and cuts in the auxiliary portion 39 are typically squares. 
     As an alternative to the above-described procedure, the planarization layer can be a polymer that is chosen such that it is sensitive to electron beam, ion beam, or photon (UV) beam radiation. By &#34;sensitive&#34; it is meant, for example, that upon exposure to an atmosphere of a vapor of an organometallic compound, such as an organoaluminum amide, the organometallic compound diffuses into the polymer and reacts with it to form an organometallic resist that is resistant to etching by fluorine-containing plasmas only in regions of the polymer that were not exposed to the radiation. The regions that are exposed to such radiation should overlie both the defect region and the portions of width v located in the auxiliary plateau (or trench) regions. In this way, an organometallic polymer that is etch-resistant to fluorine-containing plasmas is formed in those regions that overlie the complement of the defect region and the complement of the auxiliary plateau (or trench) regions. Thus the resist functions in a positive tone manner. Also, again the polymer is to be chosen such that in its exposed regions it will etch---typically, relatively ion etch with gaseous CF 4 , or gaseous CHF 3 , or a gaseous mixture of both, or a gaseous mixture of either or both with O 2  --at the same rate as that of the substrate. 
     For example, in conjunction with a focused ion beam, the polymer can be a polycresolformaldehyde. This polymer resist will crosslink in regions thereof that have been exposed to a focused ion beam; and thus the diffusion of the organometallic compound in the previously exposed regions of the resist will e suppressed, and the reaction of the oganometallic compound with the previously exposed regions of the resist will also be suppressed, whereby this polymer will behave as a positive tone resist. 
     As a further option, the polymer is chose such that an etch-resistant organometallic resist is formed only in those regions that were exposed to the radiation, and these regions, should overlie the complement both of the defect region and of the portions of width v located in the auxiliary plateau (or trench) regions. In this way, again an organometallic resist (that is resistant to etching by fluorine-containing plasmas) is formed in those regions that overlie the complement of the defect region and of the auxiliary plateau (or trench) regions--i.e., in a negative tone manner. 
     Although the invention has been described in detail with respect to specific embodiments, various modifications can be made without departing from the scope of the invention. For example, the chrome layer 23 can be omitted in case the resist layer 24 itself is sufficiently durable so as to be usable as a patterned resist during the anisotropic etching of the planarization layer 22. Instead of chrome, other materials having a good dry-etch resistance during the substrate (quartz) etching can be used, for example aluminum having a thickness of about 0.03 μm, the aluminum being patterned typically by means of a gaseous chlorine plasma etching process. Instead of the aforementioned polymers, other materials can be used for the planarization layer 22, such as silicon dioxide or silicon nitride which have been chemically vapor deposited, or spun-on glass. Also, the chromium layer 23 can be removed, prior to removal of the planarization layer 22, by a known chromium etchant. Instead of quartz, the substrate can be essentially calcium fluoride or magnesium fluoride.