Abstract:
The invention is also a method of making adhesive tape. The coating step includes drop die coating the plurality of adhesive stripes on the backing without causing any “necking-down” problems of the adhesive stripes. The invention is also a drop die for stripe coating a substrate. A face plate is removably and replaceably mounted across the fronts of die blocks. The face plate has a plurality of orifices such that fluid flowing in the die through the first slot exits through the orifices in the face plate in a plurality of stripes.

Description:
TECHNICAL FIELD  
       [0001]    This application is a divisional of pending U.S. patent application Ser. No. 09/586,222 filed Jun. 2, 2000 and entitled METHOD AND APPARATUS FOR MAKING STRIPED ADHESIVE-COATED TAPE, the entire disclosure of which is incorporated by reference herein. The present invention relates to tape. More particularly, the present invention relates to striped adhesive coated tape. 
     
    
     
       BACKGROUND OF THE INVENTION  
         [0002]    Conventional adhesive tapes, such as box sealing tape, are formed with a backing layer, an adhesive layer, and a low adhesion backsize layer (LAB). These pressure-sensitive adhesive tapes are usually prepared by a process in which a layer of pressure-sensitive adhesive is applied to one major surface of the backing layer across the entire width of the backing layer, and a layer of LAB is applied to the other major surface of the backing layer. Some preferred adhesives include rubber-based adhesives which include a blend of natural or synthetic rubber and tackifier resin. Styrene-isoprene-styrene block copolymer based adhesives are often used. Acrylate-based adhesives are also used.  
           [0003]    Box sealing tape is a well-known type of adhesive tape which is typically used to secure the flaps or covers of a box so that the box will not accidentally open during normal shipment, handling, and storage. It maintains the integrity of a box throughout its entire distribution cycle. Box sealing tape can be used on other parts of boxes and on substrates other than boxes and can be used to function similarly to labels. These tapes can be made in roll or pad form. They can be transparent, translucent, or opaque and can have information printed or otherwise applied to the tape.  
           [0004]    In most known applications, the adhesive layer is applied to the backing layer to completely cover the backing layer. In some applications the adhesive layer is applied in stripes to the backing layer and is then smoothed, for example, to spread the adhesive so that it covers the entire backing layer. In other applications, the adhesive layer is applied in stripes and remains in stripes on the backing layer. Some examples of this include WO 96/05108 and U.S. Pat. Nos. 5,217,307; 3,885,559; and 3,811,438. In these applications, the non-adhesive stripes are relatively wide and function as non-adhesive portions. That is, they are intended to be portions of the tape that do not adhere to a substrate. The adhesive and non-adhesive portions are not intended to permit the non-adhesive stripes to be part of a greater adhesive portion of the tape that functions as a continuous band of adhesive such that the uncoated portions do not form a functional non-adhesive portion.  
           [0005]    U.S. Pat. Nos. 4, 386,998 and 4,391,856 disclose contact coating heads that have a series of orifices which apply stripes of adhesive layers onto a substrate. These patents are representative of known coating systems in which the heads contact the substrate on which the adhesive is coated. These dies are typically formed of a one piece construction, which is a round stock of metal with the center drilled out. The center cavity is the adhesive distribution manifold. A series of holes are drilled along the length of the die to the manifold. Adhesive is pumped into the manifold, and exits the die through the holes along the length of the die. The die is brought into contact with the backing on a free span of web, generally located between two idler rolls. The lip of the die is used to level and smooth the coating. High viscosity materials, such as hot melt adhesives, are difficult, if not impossible to smooth on a free span of web, because the web tension is not sufficient to create enough pressure or resistance to permit adequate smoothing. Therefore, these contact dies are typically used for lower viscosity materials (less than 10,000 centipoise).  
           [0006]    U.S. Pat. Nos. 4,774,109 and 4,844,004 also disclose coaters which apply beads of liquid onto a substrate using contact or close proximity dies.  
           [0007]    U.S. Pat. Nos. 5,458,291 and 5,636,790 disclose non-contact hot melt adhesive die coaters which create strands of adhesive at the die and apply them onto a substrate. The adhesive strands are fiberized using hot air streams and are randomly disposed on the substrate as a thin coating.  
           [0008]    PCT Publication No. WO 96/05108 discloses sealing boxes with shortened flaps using a partially coated adhesive tape. The tape has at least two wide stripes of adhesive separated by a wider portion of non-adhesive. There is no disclosure of using narrow stripes of adhesive. And there is particularly no disclosure of replacing a continuous band of adhesive with a plurality of stripes or of creating a continuous band of adhesive with a plurality of stripes.  
         SUMMARY OF THE INVENTION  
         [0009]    The invention is an adhesive tape that has a backing having a first side and a second side, and a plurality of first segments of first adhesive on the first side of the backing. The plurality of segments and any adjacent uncoated segments together create an adhesive portion of the tape that functions as a continuous band of adhesive such that the uncoated segments are part of the adhesive portion and do not form a functional non-adhesive portion.  
           [0010]    The segments can be stripes and can have a width selected in combination with each other to control the tape properties.  
           [0011]    The tape has similar adhesive performance characteristics as a compositionally similar tape having the same backing and at least the same coating weight of the same adhesive coated across the entire surface of the backing. The tape can use at least 10% less adhesive as a similar tape having the same thickness of the same adhesive coated across the entire width of the tape.  
           [0012]    In one version the tape has at least one first portion and at least one second portion. The first and second portions are adjacent each other and the plurality of adhesive stripes are spaced across the first portions of the tape. The second portions can include a plurality of stripes of adhesive or non-adhesive, or uncoated backing. The ratio of the width of the adhesive stripes to the width of the uncoated stripes can range from 2:1 to 10:1; the width of the adhesive stripes can range from 0.0127 to 0.1524 cm; and the width of the uncoated stripes between adjacent adhesive stripes can range from 0.0635 to 0.0 cm.  
           [0013]    The adhesive stripes can be located to contact each other to form a coating having a nonuniform thickness. The adhesive stripes can appear to be ribs which appear to reinforce the tape.  
           [0014]    The adhesive tape can include at least first and second adhesives. The first adhesive can be selected to perform different functions than the second adhesive, broadening the range of effectiveness of the adhesive tape. At least one stripe of the first adhesive can overlap at least part of at least one stripe of the second adhesive. Also, the tape can have the first and second adhesives located along at least a portion of at least one edge of the tape. In another modification, the tape can include an LAB layer on the second side of the backing. The first adhesive adheres more strongly to the backing than to the LAB and the second adhesive adheres more strongly to the LAB than to the backing when the tape is wound into a roll having a plurality of winds of tape. When the tape is subsequently unwound, the first adhesive remains on the first side of the backing and the second adhesive transfers to the LAB layer on the second surface of the backing of the wind of tape underneath it.  
           [0015]    The adhesive tape can be a box sealing tape. The backing can be translucent and the adhesive stripes appear, through the backing, to be ribs. The box sealing tape can have adhesive performance characteristics at least as good as a conventional box sealing tape having adhesive of the same coating weight.  
           [0016]    The invention is also a method of making adhesive tape. The method includes selecting a backing having a first side and a second side; selecting at least a first adhesive to coat on at least part of the first side of the backing; selecting a desired coating weight of adhesive; selecting a width of the first adhesive stripes and a zero or greater width of uncoated stripes in combination with each other to attain desired tape properties; and coating a plurality of first stripes on the first side of the backing. The coating step includes drop die coating the first stripes on the backing without causing any “necking-down” problems of the stripes.  
           [0017]    The method can also include passing the adhesive stripe-coated backing through a roller nip to flatten the adhesive stripes. The method can also include passing the adhesive through a plurality of orifices in at least one multiple orifice drop die to create adhesive stripes while the adhesive is being coated onto the backing. The method can also include providing relative lateral movement between the drop die and the backing.  
           [0018]    The invention is also a die for coating a substrate. The die includes a first die block and a second die block. The second die block is located adjacent the first die block to form a first slot between the first die block and the second die block that has an exit at the front of the first and second die blocks. Fluid is supplied to the slot and a face plate is mounted across the fronts of the die blocks. The face plate has a plurality of orifices such that fluid flowing in the die through the slot exits through the orifices in the face plate in a plurality of stripes. The face plate is easily removable and replaceable to facilitate cleaning the die and to facilitate changing the orifice pattern to change the pattern of coated stripes on the substrate.  
           [0019]    The means for supplying fluid can include a first manifold located in the die and formed in at least one of the die blocks. Also, the means for supplying fluid can include a second manifold located in the die and formed in at least one of the two die blocks and a second slot. The die can coat a first coating through the first slot and a second coating through the second slot. 
       
    
    
     BRIEF DESCRIPTION OF THE DRAWINGS  
       [0020]    [0020]FIG. 1 is a cross-sectional view of an adhesive tape according to one embodiment of the present invention.  
         [0021]    [0021]FIG. 2 is a partial cross-sectional view of an adhesive tape according to another embodiment of the present invention.  
         [0022]    [0022]FIG. 3A is a cross-sectional view of several winds of tape according to another embodiment of the present invention.  
         [0023]    [0023]FIG. 3B is a cross-sectional view of the tape of FIG. 3A after unwinding.  
         [0024]    [0024]FIG. 4 is a top view of an adhesive tape according to another embodiment of the present invention.  
         [0025]    [0025]FIG. 5A is a cross-sectional view of an adhesive tape according to another embodiment of the present invention.  
         [0026]    [0026]FIG. 5B is a cross-sectional view of an adhesive tape according to another embodiment of the present invention.  
         [0027]    [0027]FIG. 6 is a top view of an adhesive tape according to another embodiment of the present invention.  
         [0028]    [0028]FIG. 7 is a top view of an adhesive tape according to another embodiment of the present invention.  
         [0029]    [0029]FIGS. 8A, 8B,  8 C,  8 D,  8 E,  8 F,  8 G,  8 H, and  8 I are cross-sectional views of differently shaped adhesive stripes.  
         [0030]    [0030]FIG. 9 is a cross-sectional view of an adhesive tape according to another embodiment of the present invention.  
         [0031]    [0031]FIG. 10 is a perspective view of a multiple orifice drop die of the present invention.  
         [0032]    [0032]FIG. 11 is a cross-sectional view of the multiple orifice drop die of FIG. 10.  
         [0033]    [0033]FIG. 12 is a front view of the face plate of the die of FIG. 10.  
         [0034]    [0034]FIG. 13 is a perspective view of a multiple orifice drop die according to another embodiment of the present invention. 
     
    
     DETAILED DESCRIPTION  
       [0035]    The invention is an adhesive tape having segments of adhesive. A segment is defined as any discrete portion. Segments include dots, blobs, and stripes, and can have any shape. A stripe is a long narrow band. It can be continuous or discontinuous. It can be linear or non-linear, such as angular or curved.  
         [0036]    This tape with stripes of adhesive can use less adhesive, by coating weight, per unit area of backing than would be used if a uniform, continuous coating of adhesive were applied across the entire width of the tape, as with known tapes. Surprisingly, even with reduced adhesive, the tape is able to display functionally indistinguishable properties to compositionally similar fully-coated tapes. Less adhesive can be used to attain the same performance as known tapes or the same amount of adhesive can be used to attain better performance. By using relatively narrow stripes of adhesive and relatively narrow stripes or areas of non-adhesive between adjacent adhesive stripes (in contrast to using wider stripes), the tape functions well. Surprisingly, the inventors have found that narrow stripes of adhesive separated by narrow (and sometimes narrower) uncoated stripes can increase the bonding effectiveness of the tape. These narrow stripes could permit air between the tape and the surface to which it is adhered to escape to prevent entrapping air bubbles. Based on the way the tape lays down on surfaces, this could also enable the tape to be more flexible, increasing bonding strength. The plurality of adhesive stripes and any adjacent uncoated stripes together create an adhesive portion of the tape that functions as a continuous band of adhesive such that the uncoated portions are part of the adhesive portion and do not form a functional non-adhesive portion. This is contrary to the known tapes. In one embodiment of this invention, a continuous band of adhesive is replaced with a plurality of stripes; in another embodiment, a continuous band of adhesive having a varying thickness and a corrugated appearance is created with a plurality of stripes.  
         [0037]    The tape can be used to replace any known type of tape. Referring to FIG. 1, the tape  10  includes a backing layer  12 , having first and second sides  14 ,  16 . Optionally, a low adhesion backsize (LAB) layer  18  is coated on the second side  16 . A plurality of stripes  20  of adhesive are coated on the first side  14 . The adhesive stripes  20  are separated by uncoated lanes or stripes  22 . In FIG. 1, adhesive stripes  20  of only a first adhesive are shown. Optionally, filaments such as glass fibers can be added to the backing layer  12  or the adhesive stripes  20 .  
         [0038]    The backing layer  12  can be any known material used for backing layers for a particular tape. For example, if the tape is a box sealing tape, the backing layer  12  is any material (which can be a single composition or a blend of materials) or layers of materials that are used for box sealing tape. The backing layer  12  could be, for example, cloth, paper, metal foil, or plastic film. Suitable paper backings include saturated flatstock and crepe. Suitable plastic film backings include polypropylene, polyethylene, copolymers of polypropylene and polyethylene, polyesters, and vinyl acetates. The polypropylene can be cast film, monoaxially oriented polypropylene (MOPP), biaxially oriented polypropylene (BOPP) or simultaneously biaxially oriented polypropylene (SBOPP). The backing material can be compostible, degradable, colored, printable, printed, and can be of different surface textures or embossed or extensible.  
         [0039]    The adhesive  20  can be virtually any adhesive. The adhesive can include hot melt-coated formulations, transfer-coated formulations, solvent-coated formulations, and latex formulations, as well as laminating, thermally-activated, and water-activated adhesives and bonding agents. Useful adhesives according to the present invention include all pressure sensitive adhesives. Pressure sensitive adhesives are well known to possess properties including: aggressive and permanent tack, adherence with no more than finger pressure, and sufficient ability to hold onto an adherend. Examples of adhesives useful in the invention include those based on general compositions of polyacrylate; polyvinyl ether; diene rubber such as natural rubber, polyisoprene, and polybutadiene; polyisobutylene; polychloroprene; butyl rubber; butadiene-acrylonitrile polymer; thermoplastic elastomer; block copolymers such as styrene-isoprene and styrene-isoprene-styrene (SIS) block copolymers, ethylene-propylene-diene polymers, and styrene-butadiene polymers; polyalpha-olefin; amorphous polyolefin; silicone; ethylene-containing copolymer such as ethylene vinyl acetate, ethylacrylate, and ethyl methacrylate; polyurethane; polyamide; epoxy; polyvinylpyrrolidone and vinylpyrrolidone copolymers; polyesters; and mixtures or blends (continuous or discontinuous phases) of the above. Additionally, the adhesives can contain additives such as tackifiers, plasticizers, fillers, antioxidants, stabilizers, pigments, diffusing materials, curatives, fibers, filaments, and solvents. Hot melt adhesives are preferred for coating stripes. Also, each adhesive stripe can be formed of multiple components of continuous phases; that is, in a single stripe there can be different materials side-by-side. Also, the adhesive optionally can be cured by any known method.  
         [0040]    A general description of useful pressure sensitive adhesives may be found in Encyclopedia of Polymer Science and Engineering, Vol. 13, Wiley-Interscience Publishers (New York, 1988). Additional description of useful pressure sensitive adhesives may be found in Encyclopedia of Polymer Science and Technology, Vol. 1, Interscience Publishers (New York, 1964).  
         [0041]    If required, any known LAB materials can be used. Suitable materials for the LAB layer  18  include polyurethanes, silicones, fluorochemicals, acrylates, polyvinylacetates, and combinations. Numerous other layers can be added to the tape, such as primers to increase the adhesion of adhesive layer to backing layer. Also, printed material can be located on the first side of the backing layer under the adhesive, or on the second side of the backing layer either under, within, or over any LAB layer  18 . This printed material can be advertising, instructions, or other information. The tape could contain a wide variety of additives such as deodorants, perfumes, antistatic materials, imaging and indicating materials, and encapsulated cleaning chemicals. Also, the backing layer can be modified by flame treatment, corona treatment, and roughening.  
         [0042]    In the embodiment shown in FIG. 1, the adhesive is applied in narrow lanes or stripes  20  separated by narrower uncoated stripes  22 . The coated adhesive stripes  20  can be 1.27 cm (0.50 in) wide and the uncoated stripes  22  can be 0.025 cm (0.010 in) wide creating a ratio of stripe width to uncoated lane width of 50:1. This ratio can be as low as 2:1 and in some embodiments the ratio can be even lower or the width of the stripes can be less than that of the uncoated lanes. In one embodiment, there are 100 stripes per 15.24 cm (100 per 6 in). More or fewer stripes also can be used.  
         [0043]    The adhesive stripes  20  will be thicker (higher) at their highest point compared to a fully coated tape with the same coating weight of adhesive per unit area (length by width) of tape. Another way to view this is that for a given desired thickness of adhesive, less adhesive can be used to coat stripes than to flood coat the entire backing. Regardless of whether this invention is used to coat (a) the same or thicker stripes with lower coating weight of adhesive or (b) stripes with comparable coating weight, the striped tape of this invention has (a) comparable or (b) improved adhesive performance characteristics, when tested on the same substrate, as a compositionally similar tape having the same adhesive coated across the entire surface of the backing and having more coating weight of adhesive. For a conventional box sealing tape, a typical fully coated adhesive thickness range is 0.0011-0.0036 cm (0.00045-0.0014 in). Thus, in this invention, for box sealing tape, the maximum thickness of the adhesive stripes could be 0.0011 cm or more. Moreover, as discussed below, this tape can be manufactured and coated at much faster coating speeds and with less waste.  
         [0044]    The width of the adhesive stripes can range from 0.0127 to 0.1524 cm (0.005-0.060 in) and the width of the uncoated portions of backing between adjacent stripes of adhesive can range from 0.0635 cm to 0.0 cm (0.025 to 0.0 in), depending on the coating weight and processing conditions (such as the distance between coating plate orifices and the extent of stripe flattening, which is discussed below).  
         [0045]    After the tape is coated, the stripes may be flattened. Flattening can be performed, for example, using a roller nip as explained in more detail below. In one embodiment, the flattened adhesive stripes  20  can contact each other (the width of the uncoated portions is 0) to produce a corrugated appearance and to alter the performance characteristics of the tape  10 .  
         [0046]    In one embodiment, 0.076 cm (0.030 in) unflattened stripes have center-to-center distances of 0.127 cm (0.050 in), yielding a stripe every 0.127 cm (0.050 in) and a ratio (if the entire tape backing is uniformly coated with stripes) of coated area to uncoated area of 3:2. In another embodiment, 0.127 cm (0.050 in) flattened stripes have center-to-center distances of 0.203 cm (0.080 in), yielding a stripe every 0.203 cm (0.080 in) and a ratio (if the entire tape backing is uniformly coated with stripes) of coated area to uncoated area of 5:3. Other embodiments can have any combination of striped adhesive coated areas and striped uncoated areas.  
         [0047]    Depending on the pattern and width of the adhesive stripes  20  that are used, a striped tape  10  according to this invention can significantly reduce the amount of adhesive used. This reduction is about 10-20% but can be as much as 30%. This reduces the cost to make the tape, in addition to providing a unique and visually stimulating product. The ribbed pattern provides a reinforced appearance to the tape. Another advantage is that any streaks that may be generated during the coating of the adhesive do not detract from the appearance of the tape, as they do with fully adhesive-coated tapes.  
         [0048]    Also, by controlling the thickness, number and width of the adhesive stripes  20 , and the width of the non-adhesive stripes  22 , one can control the tape performance properties. Using thicker stripes  20  of adhesive, increasing the number of stripes, or decreasing the width of the uncoated portions between adhesive stripes strengthens the adhesive properties of the tape. Using thinner stripes, fewer stripes, or increasing the spacing between stripes generally provides weaker adhesive properties of the tape.  
         [0049]    In another embodiment of this invention, a tape can be made with stripes of different adhesives. Two or more adhesives can be applied in narrow bands adjacent each other. FIG. 2 shows stripes of alternating first, second, and third adhesives  20 ,  24 ,  26 . The stripes of different adhesives can be separated by non-adhesive stripes  22 , as shown, or the various stripes  20 ,  24 ,  26  can abut each other without any non-adhesive stripes. When two adhesives are used the pattern of the stripes could be ABABAB, AABAABAAB, or any other combination of two adhesives to give the tape a wider range of application, permitting a tape to perform well in a wider range of environments and situations. Embodiments with multiple adhesives would work well where the tape is to be used in different environments such as warm and cold environments and on different surfaces, such as dry and oily, such as with lane marking tape which must be used in a wide range of road conditions. For example, this would allow application of styrene-isoprene-styrene block copolymer and acrylate adhesives side-by-side. The block copolymer adhesive would work well at normal box closure temperatures, while the acrylate adhesive would work well at colder temperatures. The proper combination of these adhesives would enable a tape to adhere and function well in both situations.  
         [0050]    In another embodiment using multiple adhesives, a first adhesive could have a greater thickness than a second adhesive. This could be used, for example, where the first adhesive is less tacky. The tape would be repositionable. The greater thickness, less tacky adhesive could be used to position the tape. If the tape needs repositioning or realigning, this adhesive would permit it. After the tape is properly positioned, the more tacky, second adhesive could be positioned to contact the substrate.  
         [0051]    In another embodiment using multiple adhesives, if, for example, a silicone polyurea LAB was used with two hot melt adhesives, such as SIS and acrylate, a useful and interesting tape results. If the acrylate has sufficient acid groups, it will develop a very good bond with the LAB layer and when the tape is unwound, the acrylic adhesive will adhere more strongly to the LAB of the wind of tape underneath it (closer to the center of the roll) than to its own backing and will transfer to the (non-adhesive) surface of the tape, as shown in FIGS. 3A and 3B. FIG. 3A shows several wraps of tape where the first adhesive  20  is SIS and the second adhesive  24  is acrylate. This is very desirable for several reasons. First, the adhesive stripe on the LAB would allow for load stabilization; when the tape is used to seal boxes and boxes are stacked on top of each other, the adhesive on the exposed LAB side of the tape would prevent boxes stacked on the tape from shifting easily. Second, this could be a mechanism to attach a label to the exterior of the box. In other versions of this “double-sided” tape, the resulting tape could be used to adhere well selectively to different substrates (such as for furniture veneers) or in different environments. These configurations allow single side coating to be used to make a double-sided tape, allowing higher speed manufacturing.  
         [0052]    An additional modification shown in FIG. 4 is to provide more than one adhesive along the edge of the tape to yield features and advantages of multiple adhesives along the edges. This can be accomplished several ways. The tape can be coated at an angle. The tape can be coated longitudinally and slit at an angle. The tape and the coater can have relative movement, by oscillating the tape, the coater, or both.  
         [0053]    In another modification shown in FIG. 5A, at least one stripe of a second adhesive  24  can overlap at least part of at least one stripe of a first adhesive  20 . Also, stripes of a second adhesive  24  can reside completely on top of stripes of the first adhesive  20 , as shown in FIG. 5B. These versions are useful, for example, in having one adhesive that provides quick sticking properties and another that provides strong shear characteristics.  
         [0054]    The plurality of stripes of adhesive can be non-uniformly or uniformly spaced. They can be uniformly spaced across the entire width of the tape. Alternatively, the tape can include one or more first portions  30  and one or more second portions  32  that are adjacent each other, as shown in FIG. 6. A plurality of first portions  30  can be separated by second portions  32 . The plurality of stripes of adhesive  20  can be uniformly spaced across the first portions  30  of the tape  10  and the second portions  32  can include either a plurality of non-uniformly spaced stripes of the first adhesive  20 , a second adhesive  24  (as shown in FIG. 7), or combinations, or uncoated backing (as shown in FIG. 6). These first and second portions  30 ,  32  can be relatively wide. This version could have application in packaging electronic components.  
         [0055]    The cross-sectional shape of the stripes could be any shape, such as circular or oval (FIG. 1) or can have linear or angular sides such as triangular (FIG. 8A), rectangular (FIG. 2), or hexagonal (FIG. 8B). Other shapes include trilobal (FIG. 8C) and pentalobal (FIG. 8D), hourglass-shaped (FIG. 8E), U-shaped (FIG. 8F), and other shapes (FIG. 8G). Also, concentric or annular coextruded stripes (FIG. 8H) having a sheath material and a core material could be used. For example, the core could be a low cost material, perhaps even a non-adhesive material, and the sheath could be a pressure sensitive adhesive. Alternatively, a pressure sensitive adhesive material could be the core surrounded by a non-pressure sensitive adhesive or even a non-adhesive sheath, with the adhesive activated by heat or other means. Side-by-side bi-components (FIG. 8I) also could be used. This stripe could be oriented so that both materials contact the backing layer  12  and the substrate or it could be oriented with one material contacting the backing layer  12  and the other material contacting the substrate. Some shapes lessen the need for flattening the stripes as compared to a circular shape.  
         [0056]    Another possible variation of the tape of this invention for making a similar tape may be to use a swirl pattern with a very fine line of adhesive. An oval pattern can be created with a very fine line spray, building up ridges of adhesive with overlapping ovals. The swirls in adjacent stripes could be separated or could build upon each other with no gap between them.  
         [0057]    In another modification of the invention, an additional layer of material  19  can be formed, such as by coating, on the first side  14  of the backing layer  12 , as shown in FIG. 9. The stripes  20  are coated on this additional layer  19 . This additional layer  19  can be adhesive or non-adhesive. It can even be the same adhesive as that used for the stripes  20 . In a twist on this configuration, the layer  19  could be adhesive and the stripes  20  could be a non-adhesive material. Such a configuration can be used to allow a tape to be properly positioned and repositioned on a surface before final affixing. Additionally, this version of the invention, as well as the other versions, need not necessarily be limited to tapes. For example, this version with non-adhesive segments on an adhesive layer could be used with postage stamps.  
         [0058]    The adhesive tape invention can be used in any arena that adhesive tape is used today. For example, the tape can be used as a box sealing tape. The tape can be made by many different methods, for example, with a rotary rod die with multiple openings. Also, a rotary screen printer could be used to make this tape and produce adhesive stripe patterns. Other dies, such as NRL dies (Naval Research Laboratories melt blown fiber dies) and drilled orifice dies also can be used.  
         [0059]    The invention also is a novel die that can make stripe coated tapes. This die is called a multiple orifice drop die  40 . The drop die  40  can coat hot melts and higher viscosity materials (1,000 to 200,000 centipoise at 375° F.) with extensional properties (the materials are stringy). Materials other than hot melts would be coated without using nip rolls (described below). Stripes could be applied onto the substrate and allowed to flow until dried or cured. Also, stripes could be applied using a contact die in which the lip is used to flatten the stripes.  
         [0060]    Using this die  40 , faster coating speeds can be attained when coating adhesive stripes as compared with fully coating the entire width of the backing layer. This is due, at least in part, to the elimination of the “necking-down” problems associated with conventional drop die coating because although the stripes “neck-down” individually, this does not impair the overall coated tape. Moreover, with this invention, narrower stripes can be coated, as compared with known contact coater methods. Also, the range of material viscosities, and coating weights is larger with this invention.  
         [0061]    Additionally, by coating with a multiple orifice drop die  40 , as compared to a slot fed drop die, there are no thick edge beads because there is no “necking-down” of the adhesive. Each strand drops straight down and “necks-down” individually, which does not affect the total coating width. (This is a significant improvement over non-striped coatings, which “neck-down” as a sheet and prevent uniform edge to edge coating.) Thus, the tape can be coated from edge to edge, if desired, and virtually the entire coated width of tape can be used, reducing waste. Using a multiple orifice drop die  40  creates individual strands of coating (adhesive stripes in the illustrated embodiments) which drop to the tape backing and remain as individual strands during the entire coating process. The strands maintain their integrity and stay separate and are coated on the backing where they become separate stripes of adhesive.  
         [0062]    [0062]FIGS. 10, 11, and  12  show the components of a multiple orifice drop die  40 . In the multiple orifice drop die  40 , a flowable material is forced to flow into the die body  42 , which has a first half or top plate  44  and a second half or bottom plate  46 , which together form a manifold  48  which is generally a tapered tear drop type of manifold typically used for hot melts. An internal choker bar (not shown) can also be used to modify crossweb uniformity. The material exits from the die slot exit  50  of the slot  52 . The portions of the die body  42  adjacent the exit  50  are known as the top die lip  54  and the bottom die lip  56 . The die slot exit  50  is covered by a separate component, a face plate  58 , which includes the top die lip  54  and the bottom die lip  56 . The face plate  58  can be bolted to the manifold  48  on the front of the multiple orifice drop die  40  and can be removed and replaced without taking apart the die.  
         [0063]    A series of holes or orifices  60  are formed in the face plate  58  through which the adhesive exits the die. With the multiple orifice drop die  40 , the adhesive drops or is drawn from the die onto a web, such as a backing. This type of die can coat two or more different adhesives (as discussed above) from separate manifolds (such as in a dual manifold die with a temperature isolation plate) at different temperatures, to prevent adhesive degradation and allow control of the viscosities of the adhesives to better match them up. Such a die is shown in FIG. 13. As an alternative to using a multiple orifice drop die, a plurality of single orifice drop dies can be used.  
         [0064]    After the stripes are coated onto the backing, the stripe-coated backing is passed through a roller nip  62  that flattens the round adhesive stripes, spreading or widening the stripes in the crossweb direction to a predetermined stripe width and thickness. The stripe width and thickness can be controlled by the nip pressure or the gap between the rolls. This increases the coverage of adhesive. The rollers can include a release-coated steel roll  64  and a hard rubber roll  66 . The overall adhesive coating weight (including the uncoated and coated areas) may be equal to or less than that of the backing coated by a conventional drop die (non-stripe coating), yet have equivalent tape properties, such as peel adhesion, tack, shear adhesion, and bonding effectiveness. The thickness (height) of the flattened stripes is greater than that of tape made with a conventional drop die with the same coating weight of adhesive. When coating multiple adhesives, generally, one adhesive is dropped onto the backing and the other adhesive is dropped onto the release roll  64 . The various adhesive stripes then pass through the nip  62 .  
         [0065]    By using the multiple orifice drop die  40  of this invention, changing stripe configurations is relatively simple. Unlike known systems, the stripes are created by orifices  60  which can be located in the face plate which is separate from and bolted to the die body  42  on the front of the die. The face plate  58  can be removed and replaced without taking apart the die to change the coating pattern. The adhesive is pumped into the manifold  48  and exits the die  40  through the face plate  58 , which contains the orifices  60  in a predetermined hole size, shape, spacing, and in some cases, hole pattern. Although the stripes can be formed in known dies by using shims, the individual shim elements would be very narrow and delicate, and could easily bend. Also, it is possible to machine orifices in a one- or two piece die, but this would not allow easy changeover as described above.  
         [0066]    By coating a plurality of stripes of adhesive, less adhesive is used. Thus, during the manufacture of the tape, there is less, and sometimes no, adhesive buildup on the cutting knives used to cut and slit the tape. For example, slitting in the uncoated area would eliminate adhesive buildup on the knives. Another advantage of this is that it enables producing a roll of tape with “dry” edges; that is, the slit flat side is not sticky. This can yield an adhesive tape roll with an extended backing layer, which provides the non-tacky edge, and eliminates the need to de-tack the edge or insert wafers between the rolls when boxing the tape.  
         [0067]    This invention of striped adhesive tape, has been described by example by referring to box sealing tape. The invention can be used in any arena that adhesive tape is used with various advantages. For example, the striped adhesive tape can be used as a tape for closing diapers, for masking and medical purposes, for lane marking tape, and for attaching mechanical fastening surfaces. For example, in the medical arena, a striped tape could allow fluids to flow and escape from under the tape to eliminate the need for extra porous layers.