Abstract:
Methods that enable fin cut at very tight pitch are provided. After forming a first set of paired sidewall image transfer (SIT) spacers and a second set of paired SIT spacers composed of different materials, portions of the first set of the paired SIT spacers can be selectively removed without adversely affecting the second set of the paired SIT spacers, even portions of both sets of the paired SIT spacers are exposed by the cut mask due to the different etching characteristics of the different materials.

Description:
BACKGROUND 
     The present application relates to semiconductor device fabrication. More particularly, the present application relates to semiconductor fin formation by using two sets of spacers having different etching characteristics in a sidewall image transfer (SIT) process. 
     As integrated circuits continue to scale downward in size, fin field effect transistors (FinFETs) are becoming increasingly attractive to be used in smaller nodes, e.g., the 22 nm node and beyond. FinFETs can achieve higher drive currents with increasingly smaller dimensions as compared to conventional planar FETs. In order to meet the density targets of advanced nodes, semiconductor fins are typically formed utilizing a sidewall image transfer (SIT) process since the same provides sub-lithographic line widths (i.e., less than 40 nm). In a typical SIT process, spacers are formed on each sidewall of a mandrel structure that is formed on a topmost semiconductor material of a substrate. The mandrel structure is removed and the remaining spacers are used as an etch mask to etch the topmost semiconductor material of the substrate. The spacers are then removed after each semiconductor fin has been formed. 
     One problem that is associated with forming semiconductor fins at tight pitch is that the process window for cutting of unwanted semiconductor fins is quite narrow. More specifically, the space available between fins at a tight pitch decreases the process window for placement of a fin cut mask edge in between fins. As the pitch of the semiconductor fins decreases, it becomes difficult to remove unwanted semiconductor fins without adversely affecting adjacent device fins due to the process variation and small process margin of lithographic processes. As such, a method is needed that is capable of forming semiconductor fins in which the process window for cutting unwanted semiconductor fins is improved. 
     SUMMARY 
     The present application provides methods that enable fin cut at very tight pitch. After forming a first set of paired SIT spacers and a second set of paired SIT spacers composed of different materials, portions of the first set of the paired SIT spacers can be selectively removed without adversely affecting the second set of the paired SIT spacers, even portions of both sets of the paired SIT spacers are exposed by the cut mask due to the different etching characteristics of the different materials. 
     In one aspect of the present application, a method of forming a semiconductor structure is provided. The method includes first forming a plurality of mandrel structures on a substrate, and then forming first spacers on sidewalls of the plurality of mandrel structures. Next, sacrificial spacers are formed on sidewalls of the first spacers. After forming second spacers on sidewalls of the sacrificial spacers, the plurality of mandrel structures and the sacrificial spacers are removed selective to the first spacers and the second spacers. Next, a cut mask including at least one opening therein is formed over the first spacers, the second spacers and exposed surfaces of the substrate. The at least one opening in the cut mask exposes portions of the first spacers and portions of the second spacers. Next, exposed portions of the first spacers are removed selective to exposed portions of the second spacers. 
     In another aspect of the present application, a semiconductor structure is provided. The semiconductor structure includes a plurality of semiconductor fins located on a substrate and arranged in pairs. Each pair of the plurality of semiconductor fins has a first pitch. Adjacent semiconductor fins in the plurality of semiconductor fins have a pitch the same as or 3n times the first pitch, and n is an integer greater than 0. 
    
    
     
       BRIEF DESCRIPTION OF SEVERAL VIEWS OF THE DRAWINGS 
         FIG. 1  is a cross-sectional view of an exemplary semiconductor structure including a plurality of mandrel structures located on a surface of a substrate in accordance with an embodiment of the present application. 
         FIG. 2  is a cross-sectional view of the exemplary semiconductor structure of  FIG. 1  after forming a first spacer material layer over the mandrel structures and exposed surfaces of the substrate. 
         FIG. 3  is a cross-sectional view of the exemplary semiconductor structure of  FIG. 2  after forming a first spacer on each sidewall of the mandrel structures. 
         FIG. 4  is a cross-sectional view of the exemplary semiconductor structure of  FIG. 3  after forming a sacrificial spacer on each sidewall of the first spacers. 
         FIG. 5  is a cross-sectional view of the exemplary semiconductor structure of  FIG. 4  after forming a second spacer on each sidewall of the sacrificial spacers. 
         FIG. 6  is a cross-sectional view of the exemplary semiconductor structure of  FIG. 5  after removing the mandrel structures and the sacrificial spacers. 
         FIG. 7  is a cross-sectional view of the exemplary semiconductor structure of  FIG. 6  after forming a first cut mask over the first spacers and second spacers. 
         FIG. 8  is a cross-sectional view of the exemplary semiconductor structure of  FIG. 7  after removing unwanted pairs of first spacers that are not covered by the first cut mask. 
         FIG. 9  is a cross-sectional view of the exemplary semiconductor structure of  FIG. 8  after forming a second cut mask over remaining first spacers and second spacers. 
         FIG. 10  is a cross-sectional view of the exemplary semiconductor structure of  FIG. 9  after removing unwanted pairs of second spacers that are not covered by the second cut mask. 
         FIG. 11  is a cross-sectional view of the exemplary semiconductor structure of  FIG. 10  after patterning the substrate using the remaining first spacers and the remaining second spacers as an etch mask. 
         FIG. 12  is a cross-sectional view of the exemplary semiconductor structure of  FIG. 11  after removing the remaining first spacers and the remaining second spacers. 
     
    
    
     DETAILED DESCRIPTION 
     The present application will now be described in greater detail by referring to the following discussion and drawings that accompany the present disclosure. It is noted that the drawings of the present application are provided for illustrative purposes only and, as such, the drawings are not drawn to scale. It is also noted that like and corresponding elements are referred to by like reference numerals. 
     In the following description, numerous specific details are set forth, such as particular structures, components, materials, dimensions, processing steps and techniques, in order to provide an understanding of the various embodiments of the present application. However, it will be appreciated by one of ordinary skill in the art that the various embodiments of the present application may be practiced without these specific details. In other instances, well-known structures or processing steps have not been described in detail in order to avoid obscuring the present application. 
     Although the following description and drawings of the present application disclose utilizing the methods of the present application for forming semiconductor fins, the present application is not limited to only the formation of semiconductor Fins. Instead, the present application can be used in forming other types of structures. 
     Referring first to  FIG. 1 , there is illustrated an exemplary semiconductor structure comprising a plurality of mandrel structures  18  located on a surface of a substrate  10  in accordance with an embodiment of the present application. 
     In one embodiment of the present application and as illustrated in the drawings of the present application, the substrate  10  is a semiconductor-on-insulator (SOI) substrate that includes, from bottom to top, a handle substrate  12 , an insulator layer  14  and a top semiconductor layer  16 . In some embodiments, the handle substrate  12  is optional and can be omitted. In another embodiment of the present application, the substrate  10  can be comprised of a bulk semiconductor substrate. By “bulk semiconductor substrate” it is meant a semiconductor material that is comprised entirely of a semiconductor material. For example, the substrate  10  shown in  FIG. 1  would consist entirely of the top semiconductor layer  16 . 
     When present, the handle substrate  12  can include a semiconductor material, a conductive material, and/or a dielectric material. The handle substrate  12  can provide mechanical support to the insulator layer  14 , and the top semiconductor layer  16  of an SOI substrate. The thickness of the handle substrate  12  can be from 30 microns to 2 mm, although lesser and greater thicknesses can also be employed. 
     When present, the insulator layer  14  may be a crystalline, or non-crystalline, oxide or nitride. In one embodiment, the insulator layer  14  is an oxide such as, for example, silicon oxide. The insulator layer  14  may be a single continuous layer that spans the entirety of the handle substrate  12  or it may be discontinuous. When a discontinuous insulator region is present, the insulator region exists as an isolated island that is surrounded by semiconductor material. The thickness of the insulator layer  14  can be from 50 nm to 5 microns, although lesser and greater thicknesses can also be employed. 
     The top semiconductor layer  16  (or the bulk semiconductor substrate) can include a single crystalline semiconductor material or a polycrystalline material. In one embodiment, the top semiconductor layer  16  (or the bulk semiconductor substrate) can include an elemental semiconductor material such as Si or Ge, a semiconductor material primarily composed of Group IV elements such as a silicon-germanium alloy or a silicon-carbon alloy, a III-V compound semiconductor material, a II-VI compound semiconductor material, or an organic semiconductor material. In one embodiment, the top semiconductor layer  16  (or the bulk semiconductor substrate) can include a single crystalline elemental semiconductor material, a single crystalline semiconductor material primarily composed of Group IV elements, a single crystalline III-V compound semiconductor material, a single crystalline II-VI compound semiconductor material, or a single crystalline organic semiconductor material. In another embodiment, the top semiconductor layer  16  (or the bulk semiconductor substrate) can consist essentially of undoped single crystalline silicon or single crystalline silicon doped with p-type dopant atoms or n-type dopant atoms. 
     The mandrel structures  18  can include any material (semiconductor, dielectric or conductive) that can be selectively removed from the structure during a subsequently performed etching process. In one embodiment, the mandrel structures  18  may be composed of amorphous silicon, polysilicon, amorphous or polycrystalline germanium, an amorphous or polycrystalline silicon-germanium alloy material, amorphous carbon, diamond-like carbon, or organosilicate glass. In another embodiment, the mandrel structures  18  may be composed of a metal such as, for example, Al, W, or Cu. 
     The mandrel structures  18  can be formed by first depositing a blanket layer of a mandrel material on the entire topmost surface of substrate  10  (not shown). The mandrel material layer can be formed, for example, by chemical vapor deposition (CVD) or plasma enhanced chemical vapor deposition (PECVD). The thickness of the mandrel material layer can be from 50 nm to 300 nm, although lesser and greater thicknesses can also be employed. Following deposition of the mandrel material layer, the mandrel material layer can be patterned by lithography and etching. The patterning of the mandrel material layer can be performed, for example, by applying a photoresist layer (not shown) above the mandrel material layer, lithographically patterning the photoresist layer to define a set of areas covered by the patterned photoresist layer, and transferring the pattern in the photoresist layer into the mandrel material layer by an anisotropic etch. The anisotropic etch can be selective to the semiconductor materials of the top semiconductor layer  16  of the substrate  10 . The patterned portions of the mandrel material layer constitute the plurality of mandrel structures  18 . 
     Each mandrel structure  18  that is formed may have a rectangular shape in cross-section with a constant width. In one embodiment, the width of each mandrel structure  18  is from 10 nm to 50 nm, although lesser and greater widths can also be employed. The height of each mandrel structure  18  that is formed is from 50 nm to 300 nm, although lesser and greater height can also be employed. In the embodiment that is illustrated in  FIG. 1 , the mandrel structures  18  are arranged parallel to each other to form an array of periodic patterns that is repeated along a direction perpendicular to an elongated direction (i.e., lengthwise direction) of each mandrel structure  18 . In one embodiment, the mandrel structures  18  can have a pitch from 50 nm to 200 nm, although lesser and greater pitch can also be employed. Though the mandrel structures  18  as shown in  FIG. 1  have a constant pitch, in some embodiments of the present application, the mandrel structures  18  may have a non-constant pitch. 
     Optionally, a pad layer which may be comprised of silicon nitride or a bilayer comprised of a silicon nitride layer and an underlying silicon dioxide layer can be deposited on the top semiconductor layer  16  before the deposition of the mandrel layer. The pad layer, when present, protects the top semiconductor layer  16  during the subsequent patterning processes. 
     Referring now to  FIG. 2 , there is illustrated the exemplary semiconductor structure of  FIG. 2  after forming a first spacer material layer  20 L. The first spacer material layer  20 L may be conformally deposited over mandrel structures  18  and exposed surfaces of substrate  10  by a conformal deposition process, such as, for example, CVD. The thickness of the first spacer material layer  20 L may vary depending upon the desired width of final semiconductor fins structures to be formed in the top semiconductor layer  16  of structure  10 , and can be from 5 nm to 15 nm, although lesser and greater thicknesses can also be employed. 
     The first spacer material layer  20 L may include any dielectric material that has a different etching characteristics comparing to the material of the mandrel structures  18  in embodiments in which the mandrel structures  18  comprise a dielectric material, so that the mandrel structures  18  can be selectively removed with respect to the first spacer subsequently formed. 
     In one embodiment of the present application, the first spacer material layer  20 L may include a nitride such as silicon nitride or an oxide such as silicon dioxide. 
     In another embodiment of the present application, the dielectric material that is used in providing the first spacer material layer  20 L may be a dielectric material having a dielectric constant of less than silicon dioxide (such dielectric materials may be referred to herein as low k). Examples of dielectric materials having a low dielectric constant include, but are not limited to, silsesquioxanes, C-doped oxides (i.e., organic silicates) that include atoms of Si, C, O and H, and thermosetting polyarylene ethers. The term “polyarylene” is used throughout the present application to denote aryl moieties or inertly substituted aryl moieties which are linked together by bonds, fused rings, or inert linking groups such as, for example, oxygen, sulfur, sulfone, sulfoxide, carbonyl and the like. 
     In yet another embodiment of the present application, the dielectric material that is used in providing the first spacer material layer  20 L may be a dielectric material having a dielectric constant that is equal to or even greater than that of silicon dioxide (such dielectric materials may be referred to herein as high k). Examples of high k dielectric materials include, for example, a dielectric metal oxide such as, for example, HfO 2 , ZrO 2 , La 2 O 3 , Al 2 O 3 , TiO 2 , SrTiO 3 , LaAlO 3 , Y 2 O 3 , HfO x N y , ZrO x N y , La 2 O x N y , Al 2 O x N y , TiO x N y , SrTiO x N y , LaAlO x N y , Y 2 O x N y , SiON, SiN x , a silicate thereof, and an alloy thereof. Each value of x is independently from 0.5 to 3 and each value of y is independently from 0 to 2. 
     Referring now to  FIG. 3 , there is illustrated the exemplary semiconductor structure of  FIG. 2  after removing horizontal portions of the first spacer material layer  20 L to provide first spacers  20 . Each first spacer  20  comprises a remaining portion of the first spacer material layer  20 L on each sidewall of the mandrel structures  18 . The removal of the horizontal portions of the first spacer material layer  20 L can be achieved utilizing an anisotropic etch, such as, for example, reactive ion etch (RIE). 
     After removal of the horizontal portions of the first spacer material layer  20 L, a topmost surface of each mandrel structure  18  is exposed and is coplanar with a topmost surface of each first spacer  20 . A width of each first spacer, as measured at its base, can be from 5 nm to 10 nm, although lesser and greater thicknesses can also be employed. 
     Referring now to  FIG. 4 , there is illustrated the exemplary semiconductor structure of  FIG. 3  after forming a sacrificial spacer  22  on each sidewall of the first spacers  20 . The sacrificial spacers  22  that are employed in the present application may comprise a sacrificial spacer material that can be selectively removed with respect to materials of the first spacers  20  and the second spacer to be subsequently formed. The sacrificial spacer material can be the same or different from the material used for the mandrel structures  18 . In one embodiment, the sacrificial spacers  22  include amorphous carbon. 
     The sacrificial spacers  22  can be formed by conformally depositing a sacrificial spacer material over the mandrel structures  18 , the first spacers  20  and exposed surfaces of substrate  10  utilizing a conformal deposition process such as, for example, CVD, PECVD, or ALD. After depositing the sacrificial spacer material to provide a sacrificial spacer material layer (not shown), the sacrificial spacer material layer is anisotropically etched to remove horizontal portions of the sacrificial spacer layer. After removal of the horizontal portions of the sacrificial spacer material layer, the topmost surface of each mandrel structure  18  and each first spacer  20  is exposed and is coplanar with a topmost surface of each sacrificial spacer  22 . The remaining vertical portions of the sacrificial spacer layer present on sidewalls of the first spacer  20  constitute the sacrificial spacers  22 . A width of each sacrificial spacer  22  that is formed can be from 10 nm to 50 nm, although lesser and greater thicknesses can also be employed. In one embodiment and as shown in  FIG. 4 , each sacrificial spacer  22  has a width substantially the same as that of each mandrel structure  18 . The term “substantially the same” as used herein in connection with the widths denotes that the width variations are within 10%. In another embodiment of the present application, each sacrificial spacer  22  may have a width different from that of each mandrel structure  18 . 
     Referring now to  FIG. 5 , there is illustrated the exemplary semiconductor structure of  FIG. 4  after forming a second spacer  24  on each exposed sidewall surface of the sacrificial spacers  22 . The second spacer  24  that is employed in the present application may comprise a dielectric material that is different from the materials of the first spacer  20  and sacrificial spacer  22 , so that first spacer  20  and the sacrificial spacer  22  can be selectively removed with respect to the second spacer  24 . In one embodiment and when the first spacer  20  is composes of silicon nitride and the sacrificial spacer  22  is composed of amorphous carbon, the second spacer  24  may be composed of a high k dielectric material, such as, for example, HfO 2 . 
     The second spacer  24  can be formed by conformally depositing a second spacer material over the mandrel structures  18 , the first spacer  20 , the sacrificial spacer  22  and exposed surfaces of substrate  10  utilizing a conformal deposition process such as, for example, CVD, PECVD, or ALD to provide a second spacer material layer (not shown). As shown in  FIG. 5 , the thickness of the second spacer material layer is controlled such that the second spacer material layer does not entirely fill the spaces between adjacent sacrificial spacers  22 . The thickness of the second spacer material layer that is formed can be from 5 to 10 nm, although lesser and greater thicknesses can also be employed. 
     Subsequently, horizontal portions of the second spacer material layer are removed utilizing an anisotropic etch forming the second spacers  24  on sidewalls of the sacrificial spacers  22 . After removal of the horizontal portions of the second spacer material layer, the topmost surface of each mandrel structure  18 , each first spacer  20  and each sacrificial spacer  22  is exposed and is coplanar with a topmost surface of each second spacer  24 . 
     The width of each second spacer  24 , as measured from its base, can be from 5 nm to 10 nm, although lesser and greater thicknesses can also be employed. In one embodiment and as shown in  FIG. 5 , each second spacer  24  has a width substantially the same as that of each first spacer  20 . In another embodiment of the present application, each second spacer  24  may have a width different from that of each first spacer  20 . In one embodiment, a uniform space  26  can be formed between each adjacent second spacers  24 . In one embodiment, each space  26  has a width that is defined by the distance between each adjacent second spacers  24  the same as that of each mandrel structure  18  and each sacrificial spacer  22 . 
     Referring now to  FIG. 6 , there is illustrated the exemplary semiconductor structure of  FIG. 5  after removing the mandrel structures  18  and the sacrificial spacers  22  from the structure. At least one etching process, either a wet etching or a dry etching, can be performed to remove each mandrel structure  18  and each sacrificial spacer  22  selective to each first spacer  20  and each second spacer  24 . The at least one etching process can be an anisotropic or an isotropic etch. Removal of the mandrel structures  18  and the sacrificial spacers  22  provides a plurality of first spacers  20  and a plurality of second spacers  24  which are arranged in a way such that every adjacent pairs of the first spacers  20  are separated from each other by a pair of second spacers  24 , and vice versa. In one embodiment and as shown in  FIG. 6 , each first spacer  20  has a width substantially the same as that of each second spacer  24 , although they may be different from each other. Also shown in  FIG. 6 , the spacing between each adjacent first spacers  20 , second spacers  24  and first and second spacers are substantially the same, although they may be different from each other. 
     Referring now to  FIG. 7 , there is illustrated the exemplary semiconductor structure of  FIG. 6  after forming a first cut mask  28  over the first spacers  20  and second spacers  24 . In one embodiment, the first cut mask  28  can be a photoresist layer that is lithographically patterned to form an opening that exposes unwanted pairs of first spacers  20 . The opening also exposes second spacers  24  adjacent to or between the unwanted pairs of first spacers  20 . 
     Referring now to  FIG. 8 , there is illustrated the exemplary semiconductor structure of  FIG. 7  after removing the unwanted pairs of first spacers  20  that are not covered by the first cut mask  28 . Physically exposed unwanted pairs of first spacers  20  may be removed by an anisotropic etch. The chemistry of the anisotropic etch is selected such that the material of the first spacers  20  is etched during the anisotropic etch, while the material of the second spacers  24  is not etched. A vacancy  20 X is thus provided at a location from which each first spacer  20  is removed. Because the first and the second spacers  20 ,  24  of the present application are composed of two different materials possessing different etching characteristics, the etching process used to remove unwanted first spacers  20  will not adversely affect or cut the exposed second spacers  24 . The second spacers  24  are left intact after the etching process. The cut mask overlay requirements are thus relaxed. This would allow fin cut at a very tight pitch. 
     In one embodiment and as shown in  FIG. 8 , when a width of each first spacer  20  is the same as that of each second spacer  24  and a spacing between each adjacent first spacers  20  is the same as that between each adjacent second spacers  24  and that between each adjacent first and second spacers  20 ,  24 , after removing a pair of first spacers  20  that are located between adjacent pairs of second spacers  24 , in the exposed region, the distance between center points of one second spacer  24  in one pair of second spacers  24  and an adjacent second spacer  24  in an adjacent pair of second spacers  24  (i.e., pitch P 3 ) is three times the distance between center points of each pair of first spacers  20  (i.e., pitch P 1 ) or the distance between center points of each pair of each pair of second spacers  24  (i.e., pitch P 2 ). 
     Subsequently, the first cut mask  28  is removed selective to the first and the second spacers  20 ,  24 . In one embodiment and when the first cut mask  28  is a patterned photoresist layer, the first cut mask  28  can be removed by ashing. 
     Unwanted pairs of the second spacers  24  can also be removed by performing the processing steps described above with respect to the first spacers  20 . Referring now to  FIG. 9 , there is illustrated the exemplary semiconductor structure of  FIG. 8  after forming a second cut mask  30  over the first spacers  20  and second spacers  24 . In one embodiment, the second cut mask  30  can be a photoresist layer that is lithographically patterned to form an opening that exposes an unwanted pair of second spacers  24 . The opening also exposes first spacers  20  adjacent to the unwanted pair of second spacers  24 . 
     Referring now to  FIG. 10 , there is illustrated the exemplary semiconductor structure of  FIG. 9  after removing the unwanted pair of second spacers  24  that are not covered by the second cut mask  30 . Physically exposed unwanted pair of second spacers  24  may be removed by an anisotropic etch. The chemistry of the anisotropic etch is selected such that the material of the second spacers  24  is etched during the anisotropic etch, while the material of the first spacers  20  is not etched. A vacancy  24 X is thus provided at a location from which each second spacer  24  is removed. 
     In one embodiment and as shown  FIG. 10 , after one pair of second spacers  24  is removed, the distance between center points of one first spacer  20  in one pair of the first spacers  20  and an adjacent second spacer  24  in an adjacent pair of second spacer (i.e., pitch P 3 ) is six times the first pitch. 
     Subsequently, the second cut mask  30  is removed selective to the first and the second spacers  20 ,  24 . In one embodiment and when the second cut mask  28  is a patterned photoresist layer, the second patterned mask layer  28  can be removed by ashing. 
     Referring now to  FIG. 11 , there is illustrated the exemplary semiconductor structure of  FIG. 10  after patterning the substrate  10  using remaining first spacers  20  and second spacers  24  as an etch mask. The patterning of the substrate  10  can be performed by utilizing an anisotropic etching process. In one embodiment of the present application and as is illustrated in  FIG. 11 , the patterning of the substrate  10  includes patterning of the topmost semiconductor layer  16  to provide a plurality of first semiconductor fins  32  having a width that is the same as the width of each first spacer  20  and a plurality of second semiconductor fin  34  having a width that is the same as the width of each second spacer  24 . Each first semiconductor fin  32  and each second semiconductor fin  34  comprises a remaining portion of the topmost semiconductor layer  16 . 
     As used herein, a “semiconductor fin” refers to a semiconductor structure including a portion having a shape of a rectangular parallelepiped. The direction along which a semiconductor fin laterally extends the most is herein referred to as a “lengthwise direction” of the semiconductor fin. The height of each first semiconductor fin  32  and each second semiconductor fin  34  can be in a range from 5 nm to 300 nm, although lesser and greater heights can also be employed. The width of each first semiconductor fin  32  and each second semiconductor fin can be in a range from 5 nm to 50 nm, although lesser and greater widths can also be employed. The width of each first semiconductor fin  32  can be the same or different than the width of each second semiconductor fin  34 . Multiple first semiconductor fins  32  and multiple second semiconductor fins  34  may be arranged such that each semiconductor fin has the same lengthwise direction, and is laterally spaced from each other along a horizontal direction that is perpendicular to the lengthwise direction. In this case, the horizontal direction that is perpendicular to the common lengthwise direction is referred to as a “widthwise direction.” Each semiconductor fin ( 32 ,  34 ) includes a pair of parallel sidewalls along the lengthwise direction and a pair of parallel sidewalls along the widthwise direction and at each end segment of the semiconductor fin ( 32 ,  34 ). 
     Referring now to  FIG. 12 , there is illustrated the first exemplary semiconductor structure of  FIG. 11  after removing the remaining first spacers  20  and second spacers  24 . The remaining first and second spacers  20 ,  24  can be removed utilizing at least one etch which can be an anisotropic or an isotropic etch. Alternatively, the remaining pairs of the first and the second spacer  20 ,  24  can also be removed by a chemical mechanical planarization (CMP) process. The removal of the remaining first and second spacers  20 ,  24  exposes topmost surfaces of the first semiconductor fins  32  and the second semiconductor fins  34 . 
     At this point of the present application, a functional gate structure utilizing a gate first or a gate last process can be performed to provide FinFET structures. It is noted that while the above describes a method of forming semiconductor fins from a semiconductor substrate, the method of the present application can be applied to pattern any other type substrate. 
     While the present application has been particularly shown and described with respect to various embodiments thereof, it will be understood by those skilled in the art that the foregoing and other changes in forms and details may be made without departing from the spirit and scope of the present application. It is therefore intended that the present application not be limited to the exact forms and details described and illustrated, but fall within the scope of the appended claims.