Abstract:
A fiber reinforced plastic bolt (FRP) and a method for producing the same are disclosed. The FRP bolt is useful in the industrial areas which require a bolt having electric-insulation, anti-corrosive, thermal-insulation, and non-magnetic properties. The method for producing the FRP bolt includes the steps of: winding a prepreg around a surface of an internal body, wherein the internal body includes a first reinforcing fiber which is unidirectionally aligned along the axis of the bolt, and a synthetic resin which is impregnated into the first reinforcing fiber, and the prepreg includes a second reinforcing fiber and a thermosetting resin which is impregnated into the second reinforcing fiber; forming a fiber reinforced plastic round bar by heat-hardening the prepreg; and forming a screw thread on the surface of the fiber reinforced plastic round bar.

Description:
CROSS-REFERENCE TO RELATED APPLICATIONS 
     This application is a Divisional of co-pending application Ser. No. 13,321,414 filed on Nov. 18, 2011, application Ser. No. 13/321,414 is a National Phase of PCT International Application No. PCT/KR2010/003564 filed on Jun. 3, 2010, which claims priority under 35 U.S.C. 119(a) to Patent Application No. 10-2009-0048879 filed in the Republic of Korea on Jun. 3, 2009, all of which are hereby expressly incorporated by reference into the present application. 
    
    
     TECHNICAL FIELD 
     This invention relates to a fiber reinforced plastic bolt and a method for producing the same. The fiber reinforced plastic bolt is particularly useful in the industrial areas which require a bolt having electric-insulation, anti-corrosive, thermal-insulation, and non-magnetic properties. 
     BACKGROUND ART 
     Fiber reinforced plastic (FRP) is prepared by impregnating synthetic resin such as epoxy resin, vinylester resin, phenol resin, and so on into reinforcing fiber such as glass fiber, carbon fiber, aramid fiber and so on. The fiber reinforced plastic is generally used in various areas which require electric-insulation, thermal-insulation, and non-magnetic properties, and is also used as a structural reinforcing material in civil engineering and construction industry. The fiber reinforced plastic is also used to manufacture an article such as a bolt or a nut for fixing substances. 
       FIGS. 3 and 4  are drawings for illustrating a method for producing a FRP bolt in accordance with a conventional method. As shown in  FIG. 3 , in the conventional method, reinforcing long-fiber  12  is impregnated with liquid-phase synthetic resin, and is pultruded with a thermoforming die  20  while being transported in parallel. The pultruded and synthetic resin impregnated fiber is hardened to form a FRP round bar  14 . The hardened round bar  14  is cut with a cutter  22  to a predetermined length. As shown in drawing A in  FIG. 4 , the surface of the FRP round bar  14  is ground with a bite  24  of a screw cutting device to form a screw thread of a FRP bolt  16 . As shown in drawing B in  FIG. 4  which is a longitudinal sectional view of the produced FRP bolt  16 , the produced FRP bolt  16  has long-fiber  12  which is unidirectionally aligned along the axis of the bolt  16 . Thus, the screw thread of the FRP bolt  16  is easily damaged by an external force, and the FRP bolt  16  is not suitable for connecting structures or substances in which a strong force is applied. In other words, as the surface of the FRP round bar  14  is ground away to form the screw thread of the FRP bolt  16 , the reinforcing long-fiber  12  (filament) in the screw thread is cut off, the mechanical strength of the long-fiber  12  is deteriorated, and the tensile strength of the FRP bolt  16  is also deteriorated. 
     Meanwhile, in order to increase the strength of screw thread of a FRP bolt, Japanese Patent Laid-Open No. H07-279933 discloses a bolt having an internal body and a screw thread which are made of different materials from each other, wherein the screw thread covers the internal body and is produced by a molding process. However, the resin impregnation process and the hardening process in a mold are complicated in the method, and thus the productivity of the bolt is not desirable. Alternatively, Japanese Patent Laid-Open No. H06-114859 discloses a method for producing a bolt including the step of forming a round bar made of reinforcing fiber impregnated with thermoplastic resin with the first mold, and forming the round bar into a bolt having a screw thread with the second mold. However, this method requires a molded preform made of thermoplastic resin, and the preform should be molded again. Thus, the method is not desirable in its productivity. Furthermore, for producing a screw thread of a FRP bolt by a molding process, several molds should be prepared for each type or size of the bolt, which result in the high production cost and the low productivity. 
     DISCLOSURE 
     Technical Problem 
     Therefore, it is an object of the present invention to provide a fiber reinforced plastic bolt having a screw thread of high strength. It is other object of the present invention to provide a method for producing a fiber reinforced plastic bolt having a superior quality with a desirable productivity. 
     Technical Solution 
     In order to achieve these and other objects, the present invention provides a method for producing a fiber reinforced plastic bolt comprising the steps of: winding a prepreg around a surface of an internal body, wherein the internal body includes the first reinforcing fiber which is unidirectionally aligned along the axis of the bolt, and a synthetic resin which is impregnated into the first reinforcing fiber, and the prepreg includes the second reinforcing fiber and a thermosetting resin which is impregnated into the second reinforcing fiber, forming a fiber reinforced plastic round bar by heat-hardening the prepreg; and forming a screw thread on the surface of the fiber reinforced plastic round bar. The present invention also provides a fiber reinforced plastic bolt comprising: an internal body which includes the first reinforcing fiber unidirectionally aligned along the axis of the bolt, and a synthetic resin which is impregnated into the first reinforcing fiber, and a hardened prepreg layer which is wound around the internal body, and includes the second reinforcing fiber and a thermosetting resin which is impregnated into the second reinforcing fiber, wherein a screw thread is formed on an outer surface of the hardened prepreg layer. 
     Advantageous Effects 
     In the fiber reinforced plastic (FRP) bolt of the present invention, a screw thread is formed on the hardened prepreg layer having the second reinforcing fiber. The hardened prepreg layer is formed by winding the prepreg around the internal body at least one turn. Therefore, even if the second reinforcing fiber is partially cut or damaged by forming the screw thread, the second reinforcing fiber remains intact and is directed in a circular direction of the screw thread. The remaining reinforcing fiber increases the strength of the screw thread. Furthermore, in the FRP bolt of the present invention, the internal body and the hardened prepreg layer firmly bind together, which increases the tensile strength of the FRP bolt. 
    
    
     
       BRIEF DESCRIPTION OF THE DRAWINGS 
         FIG. 1  is a drawing for illustrating a method for producing a FRP bolt according to an embodiment of the present invention. 
         FIG. 2  shows a longitudinal sectional view (A) and a cross sectional view (B) of a FRP bolt according to an embodiment of the present invention. 
         FIGS. 3 and 4  are drawings for illustrating a method for producing a FRP bolt according to a conventional method. 
     
    
    
     DETAILED DESCRIPTION OF THE INVENTION 
     A more complete appreciation of the invention, and many of the attendant advantages thereof, will be better appreciated by reference to the following detailed description. 
       FIG. 1  is a drawing for illustrating a method for producing a FRP bolt according to an embodiment of the present invention. As shown in  FIG. 1 , the method for producing a FRP bolt according to an embodiment of the present invention includes the step of winding a prepreg  44  around the surface of an internal body  34  (See drawing A of  FIG. 1 ). The internal body  34  includes the first reinforcing fiber  32  which is unidirectionally aligned along the axis of the bolt, and a synthetic resin which is impregnated into the first reinforcing fiber  32 . The prepreg  44  includes the second reinforcing fiber  42  and a thermosetting resin which is impregnated into the second reinforcing fiber  42 . Preferably, as shown in  FIG. 1 , the internal body  34  has the shape of a round bar, and the prepreg  44  has the shape of a sheet. The winding of the prepreg  44  around the internal body  34  can be carried out at least 1 turn, preferably 2˜50 turns, more preferably 10˜40 turns so that a screw thread can be formed on the wound prepreg layer. Then, the wound prepreg  44  is heat-hardened to form a fiber reinforced plastic round bar  54 . Preferably, the heat-hardening can be carried out by winding a heat shrinkable film  52  around the surface of the wound prepreg  44  and heating the heat shrinkable film  52  and the prepreg  44  (See drawing B of  FIG. 1 ). By the heat-hardening, the internal body  34  and the layer of the prepreg  44  firmly bind together. Next, the screw thread is formed on the surface of the fiber reinforced plastic round bar  54  with a cutting device  62  such as a bite to produce the FRP bolt  64  of the present invention (See drawing C of  FIG. 1 ). 
     In the internal body  34 , the first reinforcing fiber  32  is used to reinforce the synthetic resin, and examples of the first reinforcing fiber  32  include carbon fiber, glass fiber, aramid fiber, mixtures thereof, and so on. The selection of the first reinforcing fiber  32  depends on the use or the required properties of the produced FRP bolt  64 . The internal body  34  mainly increases the bending resistance of the FRP bolt  64 . Thus, the preferable first reinforcing fiber  32  is long fiber rather than short staple or monofilament, and is unidirectionally aligned along the direction of the internal body  34  and the FRP bolt  64 . If the short staple or monofilament is used as the first reinforcing fiber  32 , the mechanical strength of the FRP bolt  64  may not be satisfactory. Thus, the more preferable first reinforcing fiber  32  is long fiber continuously extended along the direction of the internal body  34 . Examples of the synthetic resin for impregnating the first reinforcing fiber  32  include epoxy resin, polyester resin, vinylester resin, phenol resin, mixtures thereof, and so on. In the internal body  34 , the volume amount (Vf) of the first reinforcing fiber  32  is preferably 10˜90%, more preferably 30˜80%, and most preferably 45˜60% based on the total volume of the internal body  34 . If the volume amount (VT) of the first reinforcing fiber  32  is less than the above-mentioned range, the bending resistance of the FRP bolt  64  may be unsatisfactory. If the volume amount (VT) of the first reinforcing fiber  32  is more than the above-mentioned range, the internal body  34  may not be properly formed and void can be produced between the first reinforcing fiber  32 , which deteriorate the mechanical strength of the internal body  34 . The internal body  34  can be produced by pultruding the first reinforcing fiber  32  and the synthetic resin. For example, the internal body  34  has a shape of a round bar or a circular cylinder having a diameter of 1˜50 mm, preferably 3˜20 mm. If necessary, before winding the prepreg  44 , the surface of the internal body  34  can be polished and washed. 
     The second reinforcing fiber  42  used in the prepreg  44  can also be made of carbon fiber, glass fiber, aramid fiber, and mixtures thereof. The shape of the second reinforcing fiber  42  can be selected from the group consisting of fabric (plain fabric, plain weave, satin weave, etc) which is woven with long fiber, unidirectionally aligned long fiber, multidirectionally, i.e., randomly aligned short staple or monofilament sheet, non-woven fabric of short staple or monofilament, mixtures thereof, and so on. In this case, the length of the short staple or the monofilament is generally 1˜100 mm, and preferably 2˜50 mm. Considering the workability and the productivity for producing the FRP bolt  64 , the more preferable second reinforcing fiber  42  has the shape of fabric or non-woven fabric. When a plain fabric shaped reinforcing fiber  42  is used as the second reinforcing fiber  42 , the angle between the direction of the internal body  34  and the fiber in the plain fabric shaped reinforcing fiber  42  is between 0˜90 degree, for example, between 10˜80 degree, more specifically between 30˜60 degree. For example, as shown in  FIG. 1 , if the long fibers of the fabric shaped reinforcing fiber  42  which direct to a horizontal direction and a vertical direction (i.e., perpendicularly, with 90 degree) are wound in parallel around the internal body  34 , the angles between the internal body  34  and fibers in the reinforcing fiber  42  are 0 degree and 90 degree. Meanwhile, if the long fibers in the fabric shaped reinforcing fiber  42  which direct to a horizontal direction and a vertical direction (i.e., perpendicularly, with 90 degree) are wound around the internal body  34  with the angle of 45 degree, the angles between the internal body  34  and the fibers in the reinforcing fiber  42  are 45 degree and −45 degree. For increasing the strength of the FRP bolt  64 , the angles are preferably 0 degree and 90 degree. 
     As the thermosetting resin which is impregnated into the second reinforcing fiber  42  in the prepreg  44 , the synthetic resin useful for the internal body  34  can also be used. Specific examples of the thermosetting resin include epoxy resin, polyester resin, vinylester resin, phenol resin, mixtures thereof, and so on. It is preferable that the thermosetting resin can be hardened within 120 minutes at the temperature of 80˜250° C. As the resins for the prepreg  44  and the internal body  34 , different resins can be used. However, if same kind of resin is used for the prepreg  44  and the internal body  34 , the binding strength between the internal body  34  and the prepreg  44  may increase. 
     In the thermosetting prepreg  44 , the volume amount (Vf) of the second reinforcing fiber  42  is preferably 10˜90%, more preferably 30˜80%, and most preferably 45˜60% (in this case, the volume amount (Vf) of the resin is 40˜55%) based on the total volume of the prepreg  44 . If the volume amount (Vf) of the second reinforcing fiber  42  is less than the above-mentioned range, the strength of the screw thread may be insufficient. If the volume amount (Vf) of the second reinforcing fiber  42  is more than the above-mentioned range, the amount of resin in the prepreg  44  is insufficient, and the winding of the prepreg  44  on the internal body  34  cannot be properly performed, and the quality of the FRP bolt  64  may be deteriorated. In the thermosetting prepreg  44 , the weight of the second reinforcing fiber  42  is preferably 5˜500 g/m 2 . Preferably, the prepreg  44  has the shape of a sheet, and the preferable thickness of the sheet is 0.02˜2.5 mm. The number of turns of the prepreg  44  wound around the internal body  34  can be determined according to the depth of the screw thread, and the preferable number of the turns is 2˜50. 
     For heat-hardening the prepreg  44  which is wound on the internal body  34 , the internal body  34  and the prepreg  44  can be inserted into a mold having a smaller diameter than the diameter of the prepreg  44 , and heat and pressure can be applied to the prepreg  44  in the mold for the heat-hardening. However, in this case, several molds should be prepared for each type, size or diameter of the prepreg  44 , which results in the high production cost and the low productivity. Therefore, in the present invention, a heat shrinkable film  52  is preferably used for the heat-hardening process. Specifically, the heat shrinkable film  52  is wound around the prepreg  44 , and heat and pressure are applied to the heat shrinkable film  52 , the prepreg  44  and the internal body  34 , for example, in an oven, to produce the fiber reinforced plastic round bar  54 . The conventional heat shrinkable film can be used in the present invention. The heat shrinkable film  52  can be made of polypropylene, polyester, and so on, and the shrinkage ratio of the heat shrinkable film  52  can be controlled so that the prepreg  44  is heat-hardened to have a predetermined size according to the properties of the prepreg  44  and the internal body  34 . The prepreg  44  has been conventionally used in producing a round bar such as a fishing pole, a golf shaft, and so on, and is suitable for producing the round bar in large quantity. 
     Next, the screw thread is formed on the surface of the fiber reinforced plastic round bar  54 , more specifically, on the hardened prepreg  44  to produce the FRP bolt  64 . The screw thread can be formed with a conventional cutting device  62  such as a bite for grinding a screw thread. In forming the screw thread, it is preferable that the root of the screw thread is formed in the hardened prepreg layer  44 , rather than in the internal body  34 . More preferably, the distance between the root of the screw thread and the internal body  34 , in other words, the minimum thickness of the non-grinded and remaining prepreg  44  is more than 0.1 mm, more preferably 0.5 mm, specifically 0.5˜5 mm. If the distance between the root of the screw thread and the internal body  34  is less than 0.1 mm, the prepreg  44  forming the screw thread can be separated from the internal body  34 , and the tensile strength of the screw thread may decrease. 
       FIG. 2  shows a longitudinal sectional view (A) and a cross sectional view (B) of a FRP bolt according to an embodiment of the present invention. As shown in  FIG. 2 , the FRP bolt  64  of the present invention has a multi-layer structure, which comprises the internal body  34  which includes the first reinforcing fiber  32  unidirectionally aligned along the axis of the bolt, and a synthetic resin which is impregnated into the first reinforcing fiber  32 , and the hardened prepreg layer  44  which is wound around the internal body  32 , and includes the second reinforcing fiber  42  and a thermosetting resin which is impregnated into the second reinforcing fiber  42 , wherein a screw thread is formed on an outer surface of the hardened prepreg layer  44 . If desirable, the heat shrinkable film  52  is wound around the prepreg  44  where the screw thread is not formed as shown in drawing C of  FIG. 1 . In the FRP bolt of the present invention, the screw thread is formed on the prepreg  44 , and the prepreg  44  firmly binds with the internal body  34 , which increase the strength of the screw thread. 
     Hereinafter, the preferable examples and comparative examples are provided for better understanding of the present invention. However, the present invention is not limited by the following examples. 
     EXAMPLE 1 
     Preparation of FRP Bolt 
     A round bar (internal body) having the diameter of 8 mm which included glass fiber unidirectionally aligned along the bar&#39;s axis and epoxy resin impregnated into the glass fiber was prepared by a pultrusion method. A fabric prepreg having the thickness of 0.13 mm which included plain fabric structured glass fiber and epoxy resin impregnated into the glass fiber was wound around the round bar (internal body). The angles between the fiber of the fabric prepreg and the axis of the round bar were 0 degree and 90 degree. Then, a polypropylene heat shrinkable film having the width of 15 mm and the thickness of 30 micron was wound around the prepreg with a tensile force of 3 kgf and a pitch of 1.5 mm. The wound prepreg was hardened for 80 minutes at 125° C. to produce a FRP round bar having the diameter of 13 mm. The hardened prepreg was grinded with a cutting device to form a screw thread (pitch: 1.5, M12). The depth of the screw thread was controlled so that the distance between the root of the screw thread and the internal body is 1.2 mm. 
     EXAMPLE 2 
     Preparation of FRP Bolt 
     A round bar (internal body) having the diameter of 8 mm which included glass fiber unidirectionally aligned along the bars axis and epoxy resin impregnated into the glass fiber was prepared by a pultrusion method. A fabric prepreg having the thickness of 0.13 mm which included plain fabric structured glass fiber and epoxy resin impregnated into the glass fiber was wound around the round bar (internal body). The angles between the fiber of the fabric prepreg and the axis of the round bar were 45 degree and −45 degree. Then, a polypropylene heat shrinkable film having the width of 15 mm and the thickness of 30 micron was wound around the prepreg with a tensile force of 3 kgf and a pitch of 1.5 mm. The wound prepreg was hardened for 60 minutes at 125° C. to produce a FRP round bar having the diameter of 13 mm. The hardened prepreg was grinded with a cutting device to form a screw thread (pitch: 1.5, M12). The depth of the screw thread was controlled so that the distance between the root of the screw thread and the internal body is 1.2 mm. 
     COMPARATIVE EXAMPLE 
     Preparation of FRP Bolt 
     A FRP round bar having the diameter of 13 mm which included glass fiber unidirectionally aligned along the bar&#39;s axis and epoxy resin impregnated into the glass fiber was prepared by a pultrusion method. The FRP round bar was grinded with a cutting device to form a screw thread. The screw thread was formed to have same size with the FRP bolts of Examples 1 and 2 (pitch: 1.5, M12). 
     For measuring the tensile strength of the FRP bolt produced in Examples and Comparative example, two steel nuts having the height of 9.8 mm were respectively fixed at each end of the FRP bolt having the length of 160 mm. Tensile strength was applied to the FRP bolt with a speed of 2.54 mm/minute in a material testing machine, and the tensile strength endured by the screw thread of the FRP bolt was measured and is set forth in Table 1. 
     
       
         
               
               
               
             
               
               
               
             
           
               
                   
                 TABLE 1 
               
               
                   
                   
               
               
                   
                 Tensile strength (kgf) 
                 Improve ratio of tensile strength 
               
               
                   
                   
               
             
             
               
                   
               
             
          
           
               
                 Comparative 
                 200 
                 100% 
               
               
                 example 
               
               
                 Example 1 
                 640 
                 320% 
               
               
                 Example 2 
                 500 
                 250% 
               
               
                   
               
             
          
         
       
     
     As shown in Table 1, when a screw thread is formed on the prepreg layer, the strength of the screw thread improves and the tensile strength of the FRP bolt remarkably increases. In addition, when the directions of the reinforcing fiber in the prepreg are 0 degree and 90 degree (Example 1), the tensile strength of the FRP bolt is superior to the FRP bolt of Example 2 in which the directions of the reinforcing fiber are 45 degree and −45 degree. Furthermore, when the directions of the reinforcing fiber of the FRP bolt are 0 degree and 90 degree (Example 1), the cutting process of the prepreg can be more easily carried out. 
     This application claims the priority benefit of Korean Patent Application No. 10-2009-0048879 filed on Jun. 3, 2009. AU disclosure of the Korean Patent application is incorporated herein by reference.