Abstract:
A method including forming alignment marks in an upper surface of a semiconductor wafer; selectively depositing a mask over the alignment marks leaving portions of the upper surface exposed; depositing an epitaxial layer over the exposed portions of the upper surface; and thereafter removing the mask.

Description:
FIELD OF THE INVENTION 
   The present invention relates to a semiconductor wafer having an epitaxial layer thereon and a method of making the same. 
   BACKGROUND OF THE INVENTION 
   Alignment marks and aligning wafers with respect to those marks are an important part of the process of manufacturing semiconductor devices and integrated circuits. Integrated circuits are manufactured by patterning a sequence of masking layers and the features on successive layers bear a spatial relationship to one another. As part of the manufacturing process each level must be aligned to the previous levels. Alignment of one pattern layer to previous layers is done with the assistance of special alignment patterns designed onto each mask level. When these special patterns are aligned, it is assumed that the remainder of the integrated circuit patterns are also correctly aligned. Since each layer must have alignment marks for proper registration with respect to the next layer, each alignment or registration then becomes layer dependent. 
   The tools that are used to pattern the various layers in a wafer are known as photomask or mask and reticles. The patterns on the mask or the reticle are defined by a combination of opaque and translucent areas. A light source shone through the mask or the reticle projects the pattern onto the surface of a semiconductor wafer, and depending upon the material that has been exposed to the light, the pattern is transferred onto the surface where the light arrives or where no light is shone on a semiconductor wafer surface. A mask contains patterns that can be transferred to an entire wafer in one exposure. A reticle, on the other hand, contains a pattern image that must be stepped and repeated in order to expose the entire semiconductor substrate surface. 
   The adjustments of the image of the mask being exposed to the previously produced patterns was originally performed by human operators, who compared the image locations under a microscope and adjusted the position of the mask to bring it into alignment with the wafer patterns. The decrease in feature sizes, and the increase in the number of alignments per wafer with step-and-repeat projector aligners, has been the impetus for developing automatic alignment systems. 
   Again, patterning is one of the basic steps used in performing semiconductor processing. It is also referred to as photolithography, masking, oxide or metal removal, and microlithography. Patterning enables the selective removal of material deposited on a semiconductor substrate or wafer (or removal of portions of the wafer), as a result of a deposition process. For example, as shown in  FIG. 1A , a layer  104  has been deposited on a substrate  102 . After the photolithography process is performed, as shown in  FIG. 1B , some parts of layer  104  had been selectively removed, such that gaps  106   a  and  106   b  are present within the layer  104 . A photomask, or pattern, is used (as shown in  FIG. 1B ) so that only the material from the gaps  106   a  and  106   b  are removed, and not the other portions of the layer  104 . The process of adding layers and removing selected parts of them, in conjunction with other processes, permits the fabrication of semiconductor devices. 
   Again, alignment is critical in photolithography and deposition, as well as in other semiconductor processes. If layers are not deposited properly, or if they are not selectively removed properly, the resulting semiconductor devices may not function, and may be discarded as scrap. Such misalignment, or overlay shift, is shown in  FIG. 2 . The layer  204  may or may not be deposited in a properly aligned configuration on substrate  202 , whereas subsequent deposition layers  206   a ,  206   b , . . . ,  206   n  are misaligned. This is indicated by the reference marks  210   a ,  210   b , . . . ,  210   n , which are shown in  FIG. 2  for illustrative clarity only. The reference marks  210   a ,  210   b , . . . ,  210   n , should substantially align over the alignment marks  208  of the substrate  202 , however, in this case the marks do not. 
   In comparison to  FIG. 2 , correctly aligned layers are shown in  FIG. 3 . The semiconductor wafer  202  has alignment marks  208 . A layer  204  is aligned thereupon. Similarly the layers  206   a ,  206   b , . . . ,  206   n  are deposited upon the layer  204 , without any, or with minimal, overlay shift. This is indicated by the reference marks  210   a ,  210   b ,  210   n  aligning with the alignment marks  208  of the wafer  202 . 
   Specific type of alignment problems can result when using epitaxial layers grown over a semiconductor substrate. Epitaxy is the process in which a thin layer of a single crystal material is deposited on a substrate. Epitaxial growth occurs in such a way that the crystallographic structure of the substrate is reproduced in the growing material, although the conductivity and the doping level of the epitaxial layer can be independent of the underlying substrate layer. Silicon substrates with epitaxial layers are commonly used in complementary metal-oxide silicon (CMOS) semiconductor devices, bi-CMOS devices, high-voltage devices, and bipolar devices. 
     FIGS. 4A ,  4 B and  4 C show the alignment problems that can occur within a pattern in an epitaxial layer relative to the pattern of a substrate layer. In  FIG. 4A , pattern shift has occurred. The pattern  406  in a substrate layer  402  has shifted to the right as the pattern  408  in the epitaxial, or epi layer  404 . In  FIG. 4B , pattern distortion has occurred. The pattern  436  in the substrate layer  432  has become distorted as the pattern  438  in the epi layer  434 . That is, the pattern  438  is smaller in width than the pattern  436 . In  FIG. 4C , pattern washout has occurred. The pattern  466  in the substrate layer  462  has washed out as the pattern  468  in the epi layer  464 . These types of alignment problems can occur because of non-ideal deposition of the epi layers, and/or because of other improper processing. The patterns of  FIGS. 4A ,  4 B and  4 C can be alignment marks, used for alignment in the subsequent processing of epi layers and other layers. 
   Once the alignment problems of  FIGS. 4A ,  4 B and  4 C occur, adjustments must be made to the position of the features on subsequent layers in order to compensate for the areas induced in the epi layer. Selecting the correct amount of adjustment, however, is usually complicated by the fact that the effects are dependent on such varying factors as substrate orientation, deposition rate, deposition temperature, and silicon source. Further, in the case of pattern washout of  FIG. 4C  in particular, subsequent processing performed relative to the epi layer  464  will likely fail, because the semiconductor processing equipment will most likely not be able to align with the washout pattern  468 . This alignment failure may be corrected by manual alignment that is time intensive and costly. 
   The present invention provides an alternative method of forming an epi layer on a semiconductor wafer. 
   SUMMARY OF THE INVENTION 
   One embodiment of the invention includes a method of selectively depositing an epitaxial material on selective portions of an upper surface of a semiconductor wafer leaving portions of the upper surface without the epitaxial material thereon. 
   Another embodiment of the invention includes a method of selectively forming a mask over portions of an upper surface of a semiconductor wafer leaving portions of the upper surface exposed; depositing an epitaxial material on the exposed portions of the upper surface; and thereafter removing the mask. 
   Another embodiment of the invention includes a method including forming alignment marks in an upper surface of a semiconductor wafer; selectively depositing a mask over the alignment marks leaving portions of the upper surface exposed; depositing an epitaxial material over the exposed portions of the upper surface; and thereafter removing the mask. 
   In another embodiment of the invention the mask comprises silicon dioxide. 
   In another embodiment of the invention the semiconductor wafer comprises silicon. 
   In another embodiment of the invention the epitaxial layer comprises silicon. 
   In another embodiment of the invention the depositing an epitaxial material comprises depositing silicon using chemical vapor deposition. 
   In another embodiment of the invention the depositing an epitaxial layer comprises chemical vapor deposition. 
   In another embodiment of the invention the depositing an epitaxial material comprises depositing silicon using chemical vapor deposition and a gas comprising at least one of silicon tetrachloride, silane, dichlorosilane and trichlorosilane. 
   In another embodiment of the invention the depositing an epitaxial material comprises metalorganic chemical vapor deposition. 
   In another embodiment of the invention the depositing an epitaxial material comprises a molecular-beam epitaxial process. 
   In another embodiment of the invention the upper surface includes alignment marks therein and wherein the epitaxial material is not deposited over the alignment marks. 
   In another embodiment of the invention the mask is formed over alignment marks in the upper surface of the semiconductor wafer prior to depositing an epitaxial material. 
   Other embodiments of the present invention will become apparent from the detailed description provided hereinafter. It should be understood that the detailed description and specific examples, while indicating the preferred embodiment of the invention, are intended for purposes of illustration only and are not intended to limit the scope of the invention. 

   
     BRIEF DESCRIPTION OF THE DRAWINGS 
     The present invention will become more fully understood from the detailed description and the accompanying drawings, wherein: 
       FIGS. 1A and 1B  are diagrams showing the effective patterning of a layer deposited on a semiconductor wafer. 
       FIG. 2  is a diagram showing the overlay shift that results when depositing and exposing subsequent layers on a layer deposited on a semiconductor wafer. 
       FIG. 3  is a diagram showing, in comparison to that of  FIG. 2 , how multiple deposits and exposed layers without overlay shift appear on a semiconductor wafer. 
       FIGS. 4A ,  4 B and  4 C are diagrams of pattern shift, pattern distortion and pattern washout, respectively, that can problematically occur in epitaxial layers. 
       FIG. 5A  illustrates a method according to the present invention including providing a semiconductor wafer including alignment marks on an upper surface thereof. 
       FIG. 5B  illustrates a method according to the present invention including providing a mask, such as silicon dioxide, over portions of the upper surface of a semiconductor wafer including alignment marks and leaving portions of the upper surface of the semiconductor wafer exposed. 
       FIG. 5C  illustrates one embodiment of the present invention including depositing an epitaxial layer over the exposed portions of the upper surface of a semiconductor wafer. 
       FIG. 5D  illustrates one embodiment according to the present invention including removing the mask from the structure shown in  FIG. 5C . 
   

   DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS 
   The following description of the preferred embodiment(s) is merely exemplary in nature and is in no way intended to limit the invention, its application, or uses. 
   Referring now to  FIG. 5A , one embodiment of the present invention includes providing a semiconductor wafer  10 . The semiconductor wafer  10  may include any semiconductor material known to those skilled in the art including germanium and silicon. Alternative semiconductor materials may also be utilized including compound semiconductors formed from Group IIIA and Group VA of the periodic table (often referred to as III-V compounds). Including for example, gallium arsenide (GaAs). Further, other semiconductor compounds from elements found in Groups IIA and VIA may be utilized. The semiconductor wafer  10  includes an upper surface  16  in which or on which alignment marks  17  may be formed. The alignment marks  17  may include raised features  18  and channels  20 . Typically the alignment marks  17  are formed by selectively etching portions of the semiconductor wafer to form the channels  20  leaving raised features  18  or islands. The semiconductor wafer may also include a plurality of dopants including, boron and phosphorus. The semiconductor wafer may also include a first region  12  and a second region  14  which may include a high dose of buried oxide. Alternatively, the alignment marks  17 , in particularly the raised features  18 , may be deposited on the semiconductor wafer  10 . 
   Referring now to  FIG. 5B , one embodiment of the present invention includes providing a mask  22  selectively formed over portions of the upper surface  16  of a semiconductor wafer  10 . Exposed portions  24  of the upper surface  16  are left without the mask  22  deposited thereon. Preferably the mask  22  covers the alignment mark  17  including the raised features  18  and channels  20 . The mask  22  may include any material known to those skilled in the art including, but not limited to, silicon dioxide, silicon oxynitride and photoresist materials. 
   Referring now to  FIG. 5C , an epitaxial material  26  is deposited over the exposed regions  24  of the upper surface  16  of the semiconductor wafer  10 . For example, the semiconductor wafer  10  may include silicon that is used as a seed crystal to grow a thin layer of silicon (epitaxial layer) on the semiconductor wafer  10 . A crystal structure of the new epitaxial layer  26  will duplicate that of the semiconductor wafer  10 . Since the substrate wafer  10  is monocrystal, the epitaxial layer  26  is monocrystal. Further, the dopant of the epitaxial layer can be n-type or p-type and is independent of the initial wafer dopant type. For example, it is possible to grow a p-type epitaxial layer  26  on a p-type wafer with a lower concentration of electrically active dopant in the epitaxial layer than what was found on the wafer  10 . The epitaxial layer  26  provides flexibility for device design in order to optimize performance by controlling the epi layer, doping thickness, concentration and profile, independent of the semiconductor wafer  10 . This control is accomplished by the intentional addition of dopants during the epitaxial growth process. The epi layer also reduces the occurrence of latchup in CMOS devices. The epitaxial layer  26  may be formed by methods including chemical vapor deposition. Before the epitaxial growth, the wafer  10  may be cleaned of oxide and any residual organic or metal impurities. In one embodiment of the invention, possible gas sources for the epitaxy reaction are the hydrogen reduction of silicon tetrachloride (SiCl 4 ), silane (SiH 4 ), dichlorosilane (SiH 2 Cl 2 ) or trichlorosilane. In one embodiment of the invention, deposition temperatures may range from 1050°-1250° C. In one embodiment of the invention, different epitaxial growth methods may also be used to grow single-crystal epitaxial layers on the silicon wafer  10  including solid-phase, liquid-phase, vapor-phase, and molecular I-beam epitaxy. In one embodiment of the invention, the growing of an epitaxial layer on the silicon wafer may be accomplished by one of vapor-phase epitaxy, metalorganic chemical vapor deposition, and molecular-beam epitaxy methods. 
   Referring now to  FIG. 5D , after the epitaxial material or layer  26  has been deposited, the mask  22  is removed for example by etching. 
   The description of the invention is merely exemplary in nature and, thus, variations that do not substantially depart from above description are intended to be within the scope of the invention. Such variations are not to be regarded as a departure from the spirit and scope of the invention.