Abstract:
A process for producing direct reduced iron (DRI) from iron ores, utilizing a gas produced from fossil fuels, particularly coal, containing sulfur compounds and BTX, wherein said gas is heated in a gas heater, preferably of the regenerative type, wherein heat is transferred from a previously-heated solid material to the gas produced from coal. The hot gas is caused to flow through a bed of DRI particles, iron oxides or other equivalent material, outside of the reduction reactor, where said material adsorbs sulfur compounds and the BTX are destroyed. The gas resulting from this treatment, free from sulfur compounds and BTX, is combined with a reducing gas stream withdrawn from the reduction reactor after H 2 O and CO 2  have at least partially have been removed for regenerating its reducing potential, with or without undergoing a previous cleaning treatment, is used for producing DRI. One of the embodiments of the invention comprises producing DRI at high temperature with the advantage of higher productivity and energy savings when using said hot DRI in an electric arc furnace for steelmaking lowering the capital and operation costs of steelmaking.

Description:
FIELD OF THE INVENTION 
       [0001]    The present invention relates to processes and plants for the direct reduction of iron ores, and more particularly to a process for producing direct reduced iron (DRI) utilizing gases derived from coal pyrolysis or from partial combustion of coal, also known as gasification. 
       BACKGROUND OF THE INVENTION 
       [0002]    Several proposals published in the technical literature of the iron and steelmaking industry and in patents can be found about the utilization of gases derived from the pyrolysis or from gasification of coal (coal gas), of which an example is coke oven gas, for producing direct reduced iron, also known in the industry as sponge iron (DRI in English). 
         [0003]    DRI is a granular solid material produced by the reaction of particulate iron ores, mainly iron oxides, in the form of lumps, pellets of concentrated ore, or mixtures thereof, with a reducing gas mainly composed of hydrogen and carbon monoxide, at a temperature in the range from about 750° C. to about 1100° C. 
         [0004]    Typical DRI plants are shown for example in U.S. Pat. Nos. 3,779,741; 3,765,872; 4,150,972; 4,336,063; 4,834,792; and 5,078,787. These systems commonly comprise vertical shaft reactors having a reduction zone in their upper part and a discharge zone in their lower part. 
         [0005]    The reducing gas fed to the reactor at high temperatures is typically mainly composed of hydrogen and carbon monoxide and after reacting with the iron oxides produces water and carbon dioxide. 
         [0006]    Chemical reduction of iron oxides is carried out by such reducing gas is typically produced by the reformation or the partial combustion of natural gas;however, there is an increasing interest in utilizing other gases derived from gasification (partial combustion) of solid and liquid fossil fuels, such as coal, among which coke oven gas is included. 
         [0007]    Coke oven gas is a by-product of coking of coal. Coke is used in the steel industry as a feedstock for blast furnaces where pig iron is produced. Pig iron is liquid metallic iron used as raw material for steelmaking. Coal is pyrolyzed in coke ovens, i.e. is heated without presence of oxygen whereby the volatile matters contained in coal are evaporated and are thus removed from coal, producing coke. 
         [0008]    The gas effluent from coke ovens at a temperature of about 1100° C. passes to a gas purification plant wherein some of the volatile substances are recuperated. This gas is then cooled and the cooled gas, saturated with water at a temperature of about 80° C. is separated from the cooling water which entrains tars and other condensed organic compounds. 
         [0009]    Coke oven gas typically has the following composition in volume % on a dry basis: 
         [0000]    
       
         
               
               
               
             
           
               
                   
                   
               
             
             
               
                   
                 Hydrogen 
                 55-62% 
               
               
                   
                 Methane 
                 22-26% 
               
               
                   
                 Nitrogen 
                  8-10% 
               
               
                   
                 Carbon monoxide 
                 6-8% 
               
               
                   
                 Carbon dioxide 
                 2-3% 
               
               
                   
                 Hydrocarbons (ethane, propane, etc.) 
                 2-3% 
               
               
                   
                   
               
             
          
         
       
     
         [0010]    Additionally, coke oven gas contains other contaminants and undesired substances, whereby this gas has some special characteristics that condition its utilization, such as:
       Tar vapors   Light oils vapors (aromatics) mainly comprising benzene, toluene and xylene, which jointly are known as BTX.   Naphthalene vapors   Ammonia   Hydrogen sulfide H 2 S   Hydrogen cyanide       
 
         [0017]    The concentration levels of the above-mentioned substances in the available coke oven gas, depends on the cleaning process undergone by the gas effluent from coke ovens. 
         [0018]    So that the coke oven gas can be utilized as fuel in the coke ovens or in other processes in a steelmaking plant, the gas must be treated for condensed water and other contaminant substances; remove the tar aerosols for avoiding plugging of pipes and equipment; remove ammonia for avoiding corrosion of pipes and gas-handling equipment; remove naphthalene for avoiding deposits and plugging of pipes due to its condensation; remove light oils if there is interest in recuperating BTX; and remove sulfur compounds, for example hydrogen sulfide and mercaptans, for complying with environmental regulations. 
         [0019]    Since coke oven gas is mainly composed of H 2  and CH 4 , it has been proposed to utilize it for chemical reduction of iron ores and obtain metallic iron in solid form for increasing steel production. 
         [0020]    However, coke oven gas can not be fed directly to the direct reduction plant if it is not previously treated to clean out those substances which may cause damages to the plant equipment or which are noxious pollutants for the environment. 
         [0021]    The cleaning and conditioning process for coke oven gas entails a high cost since it implies installation and operation of several chemical plants for cooling the gas stream effluent from coke ovens and for separation of condensed oils and ammonia as well as removal of sulfur compounds. The normal separation processes for thiophene, mercaptans and other aromatic sulfur compounds requires that these substances be previously transformed into hydrogen sulfide (H 2 S) which is suitable of being absorbed by chemical solvents. This process however also has a high capital and operating cost which can be avoided or significantly lowered by applying the present invention. 
         [0022]    The cost of cleaning coke oven gas, mainly the desulfurization and removal of BTX, can be lowered by the present invention, by synergistically utilizing the coke oven gas in a direct reduction plant, not just as a fuel, but instead make its utilization snore cost effective as a chemical agent. 
         [0023]    It has been proposed, for example in U.S. Pat. No. 4,270,739, to have a direct reduction process which utilizes coke oven gas for reduction of iron ores to metallic iron, wherein the coke oven gas is heated in a direct fired heater before being introduced to the upper part of a reduction reactor wherein the sulfur compounds are adsorbed by the iron care particles. The coke oven gas, free of sulfur compounds, is withdrawn from said reactor and is fed to a catalytic reformer wherein the hydrocarbons present in the gas are reformed to H 2  and CO and are then fed to a lower zone where the reduction of iron ores to metallic iron is effected at a higher temperature than the temperature in the adsorption zone of the reactor. This process has the disadvantage that the heater used for heating the coke oven gas to a temperature of 700° C. or higher is a direct-fired heater and therefore the sulfur compounds cause corrosion of the heating pipes and the high level of hydrocarbons cause carbon deposits in the heating pipes which entail damages and problems in the operation of the heater. Furthermore this patent proposes that the reactor have two gas distributing plenums: one for distributing the hot coke oven gas in the upper zone of the reactor and another for distributing the hot reducing gas produced in the reformer. 
         [0024]    U.S. Pat. No. 4,351,513 discloses a process for utilizing coke oven gas in a direct reduction reactor wherein the iron ore fed to the upper part of the reactor adsorbs sulfur compounds. This patent does not mention removal of BTX and necessarily produces DRI at low temperature, because coke oven gas, after passing through the iron ore bed is extracted from the reduction reactor and fed to its lower part where it is used for cooling the DRI before its discharge from said reactor. The coke oven gas exiting from the lower part of the reactor is cooled and fed to a reformer to reform the hydrocarbons, mainly CH 4 , to H 2  and CO by reaction of the CH 4  with CO 2  in the presence of a catalyst. The principal object of this process is the desulfurization of coke oven gas before it passes through the catalytic reformer to avoid the catalyst poisoning by sulfur. 
         [0025]    U.S. patent application No. 20090211401 describes a direct reduction process utilizing coke oven gas wherein the coke oven gas is mainly fed to the lower part of the reduction reactor wherein it is contacted with high temperature DRI produced in the upper part of the reactor. The DRI is cooled by the coke oven gas stream, and at the same time the DRI adsorbs the BTX and the sulfur compounds present in the coke oven gas; so that the gas withdrawn from the lower part of the reactor is clean of the undesirable contaminants and is driven to the reduction zone located at the upper part of the reactor wherein the reducing agents H 2  and CO react with the iron oxides to produce the DRI. This process however cannot be used when high-temperature DRI is to be produced without any cooling; so as to take advantage of the thermal energy of the DRI when charged directly into the electric arc furnace thus achieving important economic advantages through the electric energy savings and by the increase of steel output productivity due to the shortening of the melting time and of the over all steel furnace heat time, in general. 
         [0026]    The processes described in the above-cited patents all are limited with respect to the amount of coke oven gas that can be treated with the DRI produced in the reactor, because sulfur trapped in the DRI must afterwards be eliminated or its concentration minimized in the electric arc furnace where said DRI is utilized for steelmaking. 
         [0027]    In contrast with the above limitation, applying the present invention a relatively small amount of DRI (or equivalent material) is used because it can become saturated with sulfur and properly disposed of without contamination of the DRI produced in the reactor. 
       OBJECTS AND SUMMARY OF THE INVENTION 
       [0028]    It is therefore an object of the invention to provide a method and apparatus for producing DRI utilizing a gas produced from coal, for example coke oven gas, wherein purification of said gas in respect to elimination of BTX, sulfur compounds and heavy hydrocarbons is carried out without contaminating with such eoiminated materials the DRI produced in the reduction reactor. 
         [0029]    It is another object of the invention to provide a method and apparatus for producing DRI utilizing a gas produced from coal, for example coke oven gas, where the problems caused by the heavy hydrocarbons that can form carbon deposits and other condensed materials which plug or corrode the heater tubes are eliminated or minimized. 
         [0030]    Other objects of the invention will be pointed out later or will be evident from the following description of the invention. 
         [0031]    The objects of the present invention are achieved by providing a method and apparatus for producing direct reduced iron (DRI) from particulate iron ores in the form of lumps, pellets or mixtures thereof, utilizing a gas produced from coal, for example coke oven gas, as the reducing agent, in a vertical shaft reactor having a reduction zone in its upper part where the particles of iron ore are caused to react with a reducing gas fed to said reduction zone at a temperature in the range from about 750° C. to 1100° C. The coke oven gas is heated as a first gas stream to a temperature between about 650° C. and 800° C., and this hot coke oven gas is caused to flow through a bed of particles of an adsorbent material outside from said reduction reactor, whereby sulfur compounds and BTX are adsorbed by said adsorbent material and the heavy hydrocarbons are cracked into lighter compounds by contact with said adsorbent material at high temperature. Coke oven gas, free from the sulfur compounds and BTX is combined as a second gas stream with a third gas stream in the form of a reducing gas stream withdrawn from the reduction reactor, from which H 2 O and CO 2  have at least partially been removed for regenerating its reducing potential, and said combined gas is fed as a fourth gas stream to the reduction zone of the reactor, whereby DRI is produced utilizing coke oven gas with low cleaning capital and operating costs. Preferably the adsorbent material is DRI or an equivalent material. 
     
    
     
       BRIEF DESCRIPTION OF THE DRAWINGS 
         [0032]      FIG. 1  is a schematic process diagram showing a direct reduction process for producing DRI at high temperature, wherein coke oven gas is utilized according to the invention, that is after sulfur compounds have been adsorbed in a bed of particles of adsorbent material outside of the reactor and the BTX and heavy hydrocarbons have been destroyed avoiding sulfur contamination of the DRI produced in the reactor. 
           [0033]      FIG. 2  is a schematic process diagram showing another embodiment of the invention as applied to a direct reduction process where the reducing gas withdrawn from the reduction reactor passes through a catalytic reformer for reforming hydrocarbons contained in the coke oven gas before the gas is fed to the reactor. 
           [0034]      FIG. 3  is a schematic process diagram showing a further embodiment of the invention as applied to a direct reduction process where a portion of the reducing gas withdrawn from the reduction reactor passes through a catalytic reformer and another portion of the reducing gas withdrawn from said reactor is recycled to the reactor through a gas heater. 
       
    
    
     DETAILED DESCRIPTION OF THE INVENTION 
       [0035]    In this specification, some preferred embodiments of the invention have been described with reference to the attached figures which will help to better understand the spirit and scope of the invention. It will be understood that the description of the preferred embodiments is merely illustrative and not limitative and that the invention will be defined by the attached claims. 
         [0036]    Although the invention is herein described as applied to the utilization of coke oven gas, it will be evident that it can be applied to the utilization of other gases derived from solid or liquid hydrocarbons, such as coal, which are produced by the partial combustion or gasification of said hydrocarbons and which contain varying proportions of sulfur compounds and aromatic compounds BTX, particularly when the gasification, at least partially, is carried out at temperatures below about 800° C. 
         [0037]    With reference to  FIG. 1 , numeral  10  generally designates a direct reduction reactor, having a reduction zone  12 , through which iron ore particles  15  containing iron oxides flow by gravity at a regulated rate in a manner known in the art. The iron ore particles are into at the upper part of said reduction zone  12  in the form of lumps, pellets or mixtures thereof. 
         [0038]    A reducing gas  16 , mainly composed of hydrogen and carbon monoxide at a high temperature in the range between about 900° C. and about 1100° C., is introduced into the reduction zone  12  where it is caused to react with the iron oxides converting iron oxides to metallic iron, producing DRI by the following chemical reactions, among others: 
         [0000]      Fe x O y +H 2 →Fe°+H 2 O   (1)
 
         [0000]      Fe x O y +CO→Fe°+CO 2    (2)
 
         [0000]      H 2 O+CO→CO 2 +H 2    (3)
 
         [0039]    Due to the chemical equilibrium of the reduction reactions (1) &amp; (2) and of the gas conversion reaction (3) shown above, the reducing gas effluent  18  exiting from the reduction zone  12  through an outlet therefrom contains hydrogen and carbon monoxide (as well as water and carbon dioxide, which are products of said reduction reactions). In order to increase the efficiency of the process, the reducing potential of the gas effluent  18  from the reactor is increased by removing water and carbon dioxide before recycling the gas thereby enhanced back to the reduction zone. The gas effluent  18  from the reduction zone  12  has a temperature in the range between about 350° C. and about 450° C., depending on the conditions of temperature and pressure of the reduction zone  12 , and on the reducibility of the iron ores therein, 
         [0040]    The gas withdrawn from reactor  10  through a pipe and on through the tubes of a heat exchanger  20  where the sensible heat of the gas is transferred to water  22  fed through the exchanger  20 . The water  22  is heated, and exits as steam  24  from the heat exchanger  20 . The steam  24  can be used as a reactant, heat source, or other direct or indirect energy source in the DRI plant, or elsewhere. Specifically, the steam  24  can be used for example in the regeneration process of the solvent utilized for CO 2  absorption in the absorption system  42  and can also be added to the coke oven gas for promoting the reformation of its methane content. The sensible heat of the gas effluent  18  from the reduction zone  12  can also be used for pre-heating the recycled reducing gas before it is further heated in heater  64 . 
         [0041]    The partially cooled reducing gas  28  exiting the heat exchanger  20  through a pipe is further cooled down to ambient temperature in cooler  30  by direct contact with a flow of quench water  32 . As a result,water produced by the reduction reactions is condensed. This water condensate is combined with the quench water  32 , and the resulting water mixture  34  is removed through an outflow pipe. A small portion  38  of the cooled dewatered gas  36  is purged from the recycle loop of the reduction system through a pipe having a pressure control valve  40 . This purged portion  38  serves to prevent build up of N 2  etc. in the reactor and recycle gas and can be utilized as fuel in other equipment of the reduction plant For example, in heater  64  it can substitute for at least some of gas stream  98 , or it can be used in combination with the fuel gas stream  74  from a suitable source  76 , or it can also be used as fuel for pre-heating the refractory material of the regenerative heaters  90  and  92 , or in the coke ovens. 
         [0042]    The remaining portion  42  of the dewatered gas effluent from the reduction zone  12  flows through a pipe to compressor  44  and then passes as a re-pressurized gas  48  through a pipe to a CO 2  separation unit  50 , which can be of the type of chemical absorption or of the type of physical adsorption (PSA or VPSA) in a manner known in the art. Unit  50  separates CO 2  gas  52  from the recycle gas loop. 
         [0043]    The enhanced gas stream  54 , having a reduced content of carbon dioxide, exits the CO 2  separation unit  50  through a pipe and is fed to a humidifier  56  where it gets saturated with water by contact with water  58 , the excess  60  of which exits said humidifier through a discharge pipe. The water-saturated recycle gas  62  is heated in a heater  64  to a temperature in the range from about 720° C. to about 1100° C. The heated reducing gas stream  66 , which will be recycled to the reduction zone  12 , is combined with coke oven gas  68  which has been treated for minimizing its BTX and sulfur compounds content and is heated to a temperature between about 500° C. and 750° C. by contact with DRI in any one of vessels  90  and  92 . Optionally, a controlled amount of gas  70  containing molecular oxygen from a suitable source  72  is added to the combined stream  73  of recycled gas  66  and make-up/treated-COG gas  68 . This gas  70  is preferably pure oxygen but also oxygen-enriched air can be used. The option of oxygen-enriched air however has the drawback that there is more nitrogen introduced to accumulate in the system due to the gas recycle to the reduction reactor  10 . 
         [0044]    In treating the coke oven gas before its introduction into the reducing gas circuit (to combine with the gas stream  66  effluent from heater  64 ), it is initially fed from source  80  through pipes having valves  83  and  85  as gas streams  82  and  84  respectively, and on into alternately operated heaters  90  and  92  of the regenerative type. Heaters  90  and  92  preferably are of the kind where, in a first stage of the operation cycle, a mass of refractory material  94  and  96  is heated by the combustion of a fuel  98  (which can be the reducing gas purge  38  withdrawn from the reduction circuit, with the necessary combustion air  100  and  102 ), and in a second stage of their operation cycle, the accumulated heat in the mass of refractory material  94 and  96  is transferred to the coke oven gas  82 and  84 . This type of heater having refractory material is known in other industrial applications as “stoves” or “pebble heaters”. Fumes from the combustion in the heaters  90  and  92  flow through pipes  110  &amp;  112  (controlled by valves  111  &amp;  113  and are expelled from the system through a suitable stack. 
         [0045]    Regenerative heaters having two vessels connected in series instead of being connected in parallel can also be used. In this type of heater the refractory material is caused to flow from a vessel in the heating stage to another vessel in the heat-transfer stage, where the desired gas stream is heated, and then the cooled refractory material is recycled to the heating vessel where it is heated again by the combustion of a fuel and the operation cycle is repeated. 
         [0046]    One of the important advantages of the present invention, by utilizing regenerative heaters for heating coke oven gas, is that if the heavier hydrocarbons, tar residues and/other other substances form carbon deposits on the refractory material, these deposits are eliminated during the heating stage of the operating cycle of said heaters by the high temperature combustion gases. In other words, the carbon deposits are burned when the combustion is made with an excess of air, and in this way the carbon deposits are eliminated as CO 2  and H 2 O, thus the heaters are cleaned in each combustion stage of the operating cycle. 
         [0047]    Although in a preferred embodiment of the invention, the heaters  90  and  92  are of the regenerative type, heaters with tubes can also be utilized effecting a periodic de-coking (elimination of carbon deposits in the tubes), depending on the rate of carbon accumulation. 
         [0048]    Hydrocarbons contained in coke oven gas can be reformed to H 2  and CO, at least partially if steam  104  is added through pipes  106  and  108 . The amount of steam fed with coke oven gas depends on the content of BTX and heavy hydrocarbons. Typically, the proportion would be between about 5 volume % and 20 volume % of the amount of coke oven gas to be heated and then passes alternately through the DRI (adsorbent) in vessels  90  and  92 . The gas exits vessels  90  or  92 , after its contact with DRI (or with an equivalent adsorbent) at high temperature, through pipes  134  and  136  provided with valves  135  and  137 . Valves  83 ,  85 ,  99 ,  101 ,  103 ,  105 ,  107 ,  109 ,  111 ,  113 ,  135  and  137  make possible to selectively lead the coke oven gas, fuel gas, steam, combustion air and flue gases according to the stage of operating cycle which heaters  90  and  92  are undergoing, in a manner known in the art. 
         [0049]    The hot coke oven gas at a temperature between about 500° C. and 750° C. in heaters  90  and  92 , is caused to pass through vessels  114  and  116  through pipes  118  and  120  provided with valves  122  and  124  so that alternately, one of the vessels  114  or  116  is in a cycle of adsorption of sulfur compounds and destruction of BTX, and the other is the stage of change of adsorbent material. 
         [0050]    The adsorbent material is preferably direct reduced iron (DRI) but other materials can be utilized, such as iron oxides, dolomite or alkali compounds. In the case of iron oxides, hydrogen contained in coke oven gas contacting oxides at high temperature will reduce said oxides to metallic iron and eventually a material similar to DRI will be obtained in vessels  114  and  116 . 
         [0051]    DRI has proved to have the adsorption capacity for sulfur compounds due to its high porosity and to its destructive action on hydrocarbons by cracking or reforming. Preferably, the according to the invention, DRI  124  and  126  produced in the reduction reactor  10  is utilized as adsorbent material and is charged in vessels  114  and  116  with a particle size between about 1 and 4 mm. However, DRI of larger or smaller particle size can be utilized with some variation in the operation costs due to the pressure drop in the bed of DRI, the adsorption effectiveness, and the amount of DRI necessary for a predetermined capacity of coke oven gas cleaning. 
         [0052]    The present invention allows utilization of coke oven gas at a low cost for cleaning of sulfur and oils. Since the DRI used in vessels  90  and  92  will not be used for steelmaking, it can be saturated with sulfur compounds and can be changed with fresh DRI by diverting just a small amount of the DRI produced in the direct reduction plant. This amount of DRI for coke oven gas cleaning may be in the range of about 0.05% of the DRI production on average. Preferably, the DRI to be utilized for coke oven gas cleaning is selected from the DRI having smaller particle size, which in some plants normally is screened from the DRI produced and is separated from the DRI production as “fines”. 
         [0053]    Valves  121 ,  122 ,  129  and  131  allow alternation of operation cycles in vessels  114  and  116  containing DRI for treating coke oven gas, so that while one of the vessels is in operation, the other vessel is in the cycle of discharge of DRI saturated with sulfur and carbon and the charge of fresh DRI. 
         [0054]    After treatment of coke oven gas in vessels  114  and  116 , this treated COG  68  fed via pipes  128  and  130 , provided with valves  129  and  131 , is injected into the reducing gas stream  66  in the reducing gas circuit, to be used as a source of reducing gas in reactor  10  without the problems caused by BTX and sulfur compounds in piping and other gas handling equipment. 
         [0055]    In the process diagrams shown in  FIGS. 1 ,  2  and  3 , the components of the DRI cooling circuit at the lower part of reactor  10 , are shown with dotted lines to indicate that although preferably the invention is addressed to a process and apparatus for producing DRI at high temperatures, above about 500° C., some embodiments of the invention comprise a reduction reactor capable of producing DRI low temperature, when DRI cannot be utilized in a steelmaking plant immediately after its production. To this effect, a cooling gas  140  is circulated through the DRI bed in the lower zone  14  of the reactor, the heated cooling gas  142  is withdrawn from the reactor and is cooled with water  144  in cooler  146  and is recycled back to zone  14  by means of a compressor or equivalent equipment  148 . A cooling gas stream  150  from a suitable source  152  is injected at a rate regulated by valve  154  to the cooling gas circuit as make-up of the gas lost from said circuit by reaction with DRI or which for any reason exits said gas circuit. 
         [0056]    With reference to  FIG. 2 , where the numerals designate equivalent elements of the process and apparatus of  FIG. 1 , another embodiment of the invention is shown as applied to a direct reduction process where the reducing gas effluent from reactor  10 , which is eventually recycled to said reactor, is caused to flow through a catalytic reformer  160  wherein the hydrocarbons present in the recycled gas and additional hydrocarbon make-up gas are reformed to H 2  and CO. Coke oven gas is treated in the same manner as described above with reference to  FIG. 1  and is fed to the reducing gas circuit by its injection to the reducing gas circuit adding it to the reducing gas stream effluent from the reformer  160 . 
         [0057]    In a second embodiment of the invention, coke oven gas is treated in vessels  114  and  116  and thereafter is injected into the reducing gas circuit through pipe  162  before being fed to reformer  160 . 
         [0058]    In  FIG. 3 , a third embodiment of the invention is shown, as applied to a direct reduction process where a portion of the reducing gas withdrawn from the reduction reactor, which is recycled to reactor  10 , is made to flow through catalytic reformer  160  and another portion of said gas is recycled to the reactor through a gas heater  64 . Coke oven gas is treated in the same manner already described with reference to  FIG. 1 . 
         [0059]    In a further embodiment of the invention, coke oven gas from source  80  is passed through a gas heater  64  through pipe  164  after its combination with a gas stream  48  withdrawn from reduction zone  12  and is then passed through pipe  166  through a material capable of adsorb sulfur-compounds in vessels  114  and  116  and then it is combined with a gas stream effluent from the catalytic reformer  160 . 
         [0060]    It will be evident for those skilled in the art that numerous modifications to the embodiments of the invention herein described, as it may best fit the circumstances of a particular application, without departing from the spirit and scope of the invention, which is defined by the attached claims.