Abstract:
A method of affixing a stent jacket to a stent, comprising aligning the stent jacket coaxially with the stent, placing a portion of the stent within a portion of the stent jacket, wherein a central axis of the stent is aligned with a central axis of the stent jacket, and affixing the stent jacket to the stent with a plurality of stitches, wherein the plurality of stitches form a plurality of consecutive loops that pass through one or more holes in the stent jacket and through an outer surface of the stent.

Description:
CROSS-REFERENCE TO RELATED APPLICATIONS 
       [0001]    This application is a continuation of U.S. patent application Ser. No. 12/791,008, filed Jun. 1, 2010, now pending, which is a continuation of U.S. patent application Ser. No. 12/513,851, filed May 6, 2009, now abandoned, which is a national stage of PCT/IL2007/001442, filed Nov. 21, 2007, which claims the benefit of U.S. Provisional Application No. 60/860,486, filed Nov. 22, 2006, the disclosure of each of which is hereby incorporated herein by express reference thereto. 
     
    
     FIELD OF THE INVENTION 
       [0002]    The present invention, in some embodiments thereof relates to stent assemblies and, more particularly, but not exclusively, to stent jackets designed to substantially reduce platelet aggregation, thus decreasing, even eliminating dependence on a platelet aggregation reducers. 
       BACKGROUND 
       [0003]    Stents are now implanted in more than 70% of all percutaneous coronary revascularization procedures and routinely used in peripheral stenotic vasculature, for example stenotic carotid vessels and stenotic organ vasculature. 
         [0004]    A typical stent is typically formed with large, mesh-like, apertures that damage surrounding stenotic vessel tissue during stent expansion. During the first two days following stent placement a layer of endothelial cells grows over the stent frame and the vessel, including the damaged tissue. The endothelial cells produce nitrites that prevent emboli and associated sequelae in all but 0.8% of a stent-recipient population. 
         [0005]    While improving local circulation over the short term, stents do not remove the long-term danger of blockage in the very stenotic tissue that the stents treat as the damaged tissue is prone to form new scar tissue that protrude through the stent mesh, leading to vessel blockage, referred to as restenosis. 
         [0006]    Tubular jackets comprising a polymer having small apertures are often deployed with a stent to prevent restenosis through the larger stent apertures. While often preventing restenosis, jacketed stents cause a significant increase in other life-threatening hazards. Groups of cells in the endothelial tissue coating polymer stent jackets are often unstable, presenting a lifetime risk of developing clumps comprising multiple endothelial cells that freely float through the circulation. 
         [0007]    Platelets are sticky, irregularly shaped, disk-like blood-born bodies that promote blood clotting and readily sense, aggregate around, and stick to, clumps of free-floating endothelial cells. An embolism of aggregated platelets and endothelial cells presents a health threat that can form at any time following jacketed stent implantation; causing an estimated 2% of all jacketed stent recipients to eventually develop necrosis of vital organs and/or die. 
         [0008]    Drug eluting jacketed stents, while reducing restenosis more than non-eluting jacketed stents, may pose and even greater threat of embolitic death than non-drug eluting stents. 
         [0009]    (“Late Acute Thrombosis After Paclitaxel Eluting Stent Implantation”: F. Liistro: Heart; September 2001; Vol. 86, pages 262-264). 
         [0010]    The tremendous and constant threat of emboli from jacketed stents has resulted in lifetime administration of prophylactic active pharmaceutical ingredients (APIs) including Clopidogrel Bisulfate, herein Clopidogrel, a platelet aggregation-reducing API marketed as Plavix® by Sanofi-Aventis and Bristol-Myers Squibb. 
         [0011]    Clopidogrel administration is not hazard-free. Clopidogrel is associated with many side effects, including ulcers, skin rashes, syncope (temporary loss of consciousness), myelotoxicity (bone marrow damage), and TTP (thrombotic thrombocytopenic purpura), characterized by spontaneous, formation of assemblyic thrombi that form emboli. The death rate from TTP, even with immediate diagnosis and aggressive treatment, is approximately 30%. 
         [0012]    (“Clopidogrel-Associated TTP: An Update of Pharmacovigilance Efforts Conducted by Independent Researchers, Pharmaceutical Suppliers, and the Food and Drug Administration”; Zakarija, M D, et al; Stroke, February 2004, pages 533-537). 
         [0013]    Moreover, Clopidogrel may not prevent life-threatening emboli as current data shows that up to 30% of Clopidogrel recipients fail to develop sufficiently reduced platelet aggregation. 
         [0014]    (“Resistance To Clopidogrel: A Review Of The Evidence”: Nguyen MSc. Pharm, et al; Journal of the American College of Cardiology; 19 Apr. 2005; Vol. 45, Issue 8, pages 1157-1164). 
         [0015]    Moreover, conditions such as hereditary antithrombin deficiency (HD), are that not responsive to platelet aggregate prophylactic APIs such as Clopidogrel. HD patients receiving Clopidogrel pose a unique at-risk population as HD is often diagnosed only following a serious embolitic event. 
         [0016]    Further, people stricken with Auto Immune Deficiency Syndrome (AIDS) may actually develop hemophilia as a result of Clopidogrel administration. Within the AIDS population, a sub-population particularly at risk for developing hemophilia includes individuals having low CCR5 (CCR5 Delta 32 homozygous genotype), which is resistant to infection with HIV-1. 
         [0017]    Additionally those at risk for acquiring hemophilia appear to be in the population group of immune-suppressed individuals, including geriatrics diabetics and those in the early stages of an HIV infection. 
         [0018]    (“Acquired Haemophilia May Be Associated With Clopidogrel” Montaser Haj at al; British Medical Journal August 2004; pages 329:323). 
         [0019]    In addition to the health hazards affecting the above-noted population groups, there are significant risks to every jacketed stent recipient receiving lifetime Clopidogrel. 
         [0020]    To prevent excessive bleeding in conjunction with virtually any surgery, Clopidogrel administration must be ceased for a significant period of time both pre-operatively and post-operatively. As a result, patients and surgeons are presented with a Hobson&#39;s choice of ceasing Clopidogrel administration and risking death from emboli or continuing Clopidogrel and risking embolism-free bleeding, hemorrhage and death. 
         [0021]    In general, jacketed stents, while aiding in preventing restenosis, are associated with many significant, as yet unsolved, problems that can result in death. 
         [0022]    There is thus a widely recognized need for a stent jacket that does not require the administration of a platelet aggregation reducing API and it would be highly advantageous to have, a stent devoid of the above limitations. 
       SUMMARY OF THE INVENTION 
       [0023]    The disclosure encompasses a stent assembly that includes a stent configured to be positioned in a body lumen, and a stent jacket comprising an expansible mesh structure that is configured be disposed around an external surface of the stent and is coaxially associated therewith, wherein both the stent and stent jacket have a tubular shape and the interior diameter of the stent jacket is larger than the exterior diameter of the stent, wherein the stent jacket is attached to the stent by a plurality of stitches. In one embodiment, the expansible mesh structure comprises a retracted state and a deployed state. In another embodiment, the stent, the stent jacket, and the plurality of stitches are each selected to comprise a biodegradable material. 
         [0024]    In one embodiment, an active pharmaceutical agent is eluted from the stent. The active pharmaceutical agent may be eluted from a coating disposed over a portion of the stent, time-released according to a predetermined treatment schedule, or eluted from the stent jacket or a coating thereof. 
         [0025]    The disclosure also includes a stent assembly, comprising: a stent configured to be positioned in a body lumen; a knitted stent jacket extending along a length of, and surrounding an external surface of, the stent, the knitted stent jacket comprising an expansible mesh structure having a coverage area less than 25% of the total area of the knitted stent jacket and having apertures therethrough, wherein a distal and a proximal portion of the knitted stent jacket is attached to a distal and proximal aspect of the sent; and a plurality of stitches that are configured to attach the knitted stent jacket to the stent, wherein each of the plurality of stitches passes through a section of the knitted stent jacket and through a section of the stent. 
         [0026]    In one embodiment, the plurality of stitches are disposed about a circumference at each end of the stent with equal spacing. In another embodiment, the plurality of stitches comprises a stitch at the distal aspect and at the proximal aspect of the stent. In yet another embodiment, the plurality of stitches are part of a single fiber forming the expansible mesh structure and the plurality of stitches. In a preferred embodiment, an active pharmaceutical agent is eluted from the stent. The active pharmaceutical agent may be eluted from a coating disposed over a portion of the stent or dated from the knitted stent jacket or from a coating thereon. 
         [0027]    A method of affixing a stent jacket to a stent is also provided, comprising: aligning the stent jacket coaxially with the stent; placing a portion of the stent within a portion of the stent jacket, wherein a central axis of the stent is aligned with a central axis of the stent jacket; and affixing the stent jacket to the stent with a plurality of stitches, wherein the plurality of stitches form a plurality of consecutive loops that pass through one or more holes in the stent jacket and through an outer surface of the stent. 
         [0028]    In one embodiment, a distal and a proximal portion of the stent jacket is attached to a distal and proximal aspect of the stent. In another embodiment, the plurality of stitches are disposed about the circumference at each end of the stent with equal spacing. In yet another embodiment, an active pharmaceutical agent is eluted from the stent. The active pharmaceutical agent may be eluted from a coating disposed over a portion of the stent, time-released according to a predetermined treatment schedule, or eluted from the stent jacket or from a coating thereon. 
         [0029]    A method of attaching an expansible stent to a stent jacket to form a stent mesh assembly is also provided, comprising: providing the stent jacket coaxially about the expansible stent with a plurality of stitches, wherein the stent jacket comprises an expansible mesh structure with a tubular shape and where the stitches are disposed only at a proximal or distal end of the expansible stent and stent jacket. 
         [0030]    In one embodiment, stent, the stent jacket, and the plurality of stitches are each selected to comprise a biodegradable material, which may be selected to comprise a polymer or a metal alloy. One embodiment further comprises eluting an active pharmaceutical agent from the stmt. Another embodiment further comprises eluting the active pharmaceutical agent from a coating disposed over a portion of the stent, eluting the active pharmaceutical agent over time according to a predetermined treatment schedule, or eluting the active pharmaceutical agent from the stent jacket or a coating on the expansible mesh structure thereof. Yet another embodiment further comprises stenting the vessel of a patient by inserting the stent mesh assembly in a retracted state to a desired treatment position, and expanding the stent mesh assembly in-situ in the desired treatment position in a vessel of a patient. 
         [0031]    Unless otherwise defined, all technical and/or scientific terms used herein have the same meaning as commonly understood by one of ordinary skill in the art to which the invention pertains. Although methods and materials similar or equivalent to those described herein can be used in the practice or testing of embodiments of the invention, exemplary methods and/or materials are described below. In case of conflict, the patent specification, including definitions, will control. In addition, the materials, methods, and examples are illustrative only and are not intended to be necessarily limiting. 
     
    
     
       BRIEF DESCRIPTION OF THE DRAWINGS 
         [0032]    Exemplary non-limiting embodiments of the invention are described in the following description, read with reference to the figures attached hereto. In the figures, identical and similar structures, elements or parts thereof that appear in more than one figure are generally labeled with the same or similar references in the figures in which they appear. Dimensions of components and features shown in the figures are chosen primarily for convenience and clarity of presentation and are not necessarily to scale. The attached figures are: 
           [0033]      FIG. 1  is a perspective view of an enhanced stent apparatus, in an open, non-crimped mode, in accordance with an exemplary embodiment of the invention; 
           [0034]      FIG. 2  is a cross-sectional side view of an enhanced stent apparatus, in accordance with an exemplary embodiment of the invention; 
           [0035]      FIG. 3  is an illustration of an enhanced stent apparatus in an open mode in situ, in accordance with an exemplary embodiment of the invention; 
           [0036]      FIG. 4  is a perspective view of an enhanced stent apparatus, with multiple helical coils in an open mode, in accordance with an exemplary embodiment of the invention; 
           [0037]      FIG. 5  is a perspective view of an enhanced stent apparatus, in a crimped, closed mode, in accordance with an exemplary embodiment of the invention; 
           [0038]      FIG. 6A  is a perspective view of a knitted porous structure enhanced stent apparatus in an open mode, in accordance with an exemplary embodiment of the invention; 
           [0039]      FIG. 6B  is a detailed view of a knitted porous structure, in accordance with an exemplary embodiment of the invention; 
           [0040]      FIG. 7  is a perspective view of a braided porous structure enhanced stent apparatus, in accordance with an exemplary embodiment of the invention; 
           [0041]      FIG. 8  is a perspective view of an enhanced stent apparatus on an angioplasty balloon, in accordance with an exemplary embodiment of the invention; 
           [0042]      FIG. 9  is a perspective view of an enhanced stent apparatus, provided with longitudinal non-stretchable wires, and horizontal stretchable elastomers in accordance with an exemplary embodiment of the invention; 
           [0043]      FIG. 10  is a perspective view of an enhanced stent apparatus, wherein porous structure is longer than the support element, in accordance with an exemplary embodiment of the invention; 
           [0044]      FIG. 11  is a perspective view of an enhanced stent apparatus, wherein porous structure is significantly greater in diameter than a crimped support element, and is folded on itself for insertion into a lumen, in accordance with an exemplary to embodiment of the invention; 
           [0045]      FIG. 12  is a perspective view of a porous structure significantly greater in diameter than an at least partially deflated balloon wherein the porous structure is folded on itself for insertion into a lumen, in accordance with an exemplary embodiment of the invention; 
           [0046]      FIG. 13  illustrates the use of a funnel to reduce the diameter of at least a porous structure, in accordance with an exemplary embodiment of the invention; 
           [0047]      FIG. 14  illustrates using a stretchable rubber tube for manufacturing a compressed porous structure, in accordance with an exemplary embodiment of the invention; 
           [0048]      FIG. 15  is a graph showing fiber thickness vs. percentage of porous structure surface area that is structure, in accordance with an exemplary embodiment of the invention; 
           [0049]      FIG. 16  is a detailed illustration of a threading method for securing a porous structure to a support element, in accordance with an exemplary embodiment of the invention; 
           [0050]      FIG. 17  is a detailed illustration of a knotting method for securing a porous structure to a support element, in accordance with an exemplary embodiment of the invention; 
           [0051]      FIG. 18  is a cross-section view of an enhanced stent apparatus showing a porous structure folding technique, in accordance with an exemplary embodiment of the invention; 
           [0052]      FIG. 19  is a schematic showing a method for manufacturing a porous structure, in accordance with an exemplary embodiment of the invention; 
           [0053]      FIG. 20A  is an illustration of a typical aneurism; 
           [0054]      FIG. 20B  is an illustration of a prior art technique for treating an aneurism; 
           [0055]      FIG. 20C  is an illustration of a technique for treating an aneurism, in accordance with an exemplary embodiment of the invention; 
           [0056]      FIG. 21A  is a cross-sectional view of a slip ring in a reduced profile configuration, in accordance with an exemplary embodiment of the invention; 
           [0057]      FIG. 21B  is a cross-sectional view of a slip ring in a deployed configuration, in accordance with an exemplary embodiment of the invention; 
           [0058]      FIG. 22  is cross sectional view of a porous structure with an endothelium cell layer overgrowing it, in accordance with an exemplary embodiment of the invention; 
           [0059]      FIG. 23  is an illustration of a prior art situation in which a clump of endothelial cells detaches from a stent strut; 
           [0060]      FIGS. 24   a - 24   d  show deployment of a self-expanding stent, according to embodiments of the invention; 
           [0061]      FIGS. 25-28  show in situ details of a typical stent jacket material in the art, in situ; and 
           [0062]      FIG. 29  shows a portion of the knitted stent jacket, according to embodiments of the invention; 
           [0063]      FIG. 30  shows a plan view of the knitted stent jacket of  FIG. 29 , according to embodiments of the invention; 
           [0064]      FIGS. 31-32  show details of the material comprising the knitted stent jacket of  FIG. 29 , according to embodiments of the invention; and 
           [0065]      FIG. 33  shows in situ details of the material shown in  FIGS. 8-9 , according to embodiments of the invention. 
       
    
    
     DETAILED DESCRIPTION OF EXEMPLARY EMBODIMENTS 
       [0066]    The instant application is divided into a number of labeled sections which generally include, in order, descriptions of apparatuses (e.g. porous structures, stents, etc.), materials and methods for manufacturing the apparatuses, the usage of pharmaceuticals with the apparatuses and methods of using the apparatuses. It should be understood that the section headings are for clarity only, and are not intended to limit the subject matter described therein. Furthermore, some of the subject matter described in a particular section may belong in more than one section and therefore, some of the material could overlap between sections. 
       Introduction 
       [0067]    Aspects of the present invention successfully address shortcomings of the prior art by providing a stent assembly having a low-bulk mesh jacket designed to promote a stable layer of endothelial cells. 
         [0068]    In accordance with some embodiments of the present invention, the mesh comprises a fiber having a low diameter that allows each endothelial cell to fully cover and overlap each fiber, thereby forming a layer of endothelial cells that adhere to tissue on either side of the fiber. The thus formed endothelial layer is substantially stable with a substantially reduced tendency to break away and form emboli. 
         [0069]    In accordance with some embodiments of the present invention, the mesh fiber comprises material that encourages adherence of endothelial cells, thereby encouraging endothelial layer stability. 
         [0070]    In accordance with some embodiments of the present invention, the mesh is not secondarily processed for example with a chemical coating that may diminish endothelial adherence. Additionally, the absence of chemical coatings serves to maintain low bulk fibers and fiber junctions, where a first fiber passes over or under a second fiber-another feature that contributes to endothelial layer stability. 
         [0071]    In accordance with some embodiments of the present invention, each mesh fiber is spaced a distance from a neighboring fiber thereby preventing a single endothelial cell from adhering to more than one fiber, thereby reducing the chance that endothelial cells will break free of the stent, for example as a result of natural stent pulsation during blood flow. 
         [0072]    In accordance with some embodiments of the present invention, the stent jacket optionally comprises a mesh that is knitted. In accordance with some embodiments of the present invention, the stent jacket mesh is optionally formed from a single fiber or a single group of fibers. 
       Overview of Enhanced Stem Apparatus 
       [0073]    The present invention, in some embodiments thereof, relates to stent assemblies, as presented in PCT Patent Application PCT/IB2006/051874, the disclosure of which is hereby incorporated herein by express reference thereto. 
         [0074]    In an exemplary embodiment of the invention, an apparatus is provided which includes a porous structure and, optionally, an underlying support element, such as a stent (wherein underlying means the porous structure is between the support element and a lumen wall). 
         [0075]    In some exemplary embodiments of the invention, an enhanced stent apparatus, including the porous structure and a stent, is used to treat stenosis and/or restenosis. In some exemplary embodiments of the invention, the enhanced stent apparatus furnishes at least one of a multiplicity of benefits over a conventional arterial stent. For example, the enhanced stent apparatus is optionally used to prevent plaque from getting into the blood stream to cause embolism, since the porous structure is made with small enough apertures (sizes indicated below) to hold detached plaque in place. In an embodiment of the invention, use of a porous structure replaces the use of an embolism protection device during stent implantation. Optionally, the “umbrella” type embolism protection device is not used. Optionally, the porous structure is used in conjunction with an embolism protection device for enhanced protection over the method of using an embolism protection device during the implantation of a conventional arterial stent. In an embodiment of the invention, the enhanced stent apparatus delivers more comprehensive pharmacological assistance to a treated area than conventional stents. In some embodiments of the invention, the enhanced stent apparatus is optimized to encourage endothelial cell growth and/or migration. 
         [0076]      FIG. 1  shows a perspective view of an enhanced stent apparatus  100 , in an exemplary embodiment of the invention. A support element  102  is designed and constructed to expand a blood vessel in a radial fashion from a central axis  106  of the enhanced stent apparatus  100 . Optionally, support element  102  is tubular in shape. In some exemplary embodiments of the invention, support element  102  is constructed of a flexible, biocompatible material. Optionally, support element  102  is constructed of stainless steel, nitinol, and/or cobalt chromium and/or other metal alloys (e.g. magnesium alloy). Optionally, support element  102  is constructed of polymer either biostable or bioresorbable. In some exemplary embodiments of the invention, support element  102  is a vascular stent, such as those made by Cordis®, Boston Scientific® and/or Medtronic®, for example. 
         [0077]    In an exemplary embodiment of the invention, support element  102  is covered by at least one porous structure  104 . Optionally, support element  102  acts as a support structure for porous structure  104 , for example to provide radial support and or to maintain a desired shape of porous structure  104 .  FIG. 2 , shows a cross-sectional view of an enhanced stent apparatus. In this embodiment, support element  102  supplies structural support to porous structure  104 , which is located on the exterior of support element  102 . 
         [0078]    In some exemplary embodiments of the invention, porous structure  104  is laid on the exterior of support element  102  and thereby overlaps gaps in support element  102  (making the aperture sizes of the device as a whole smaller, for example 150 microns), since conventional stent construction usually results in multiple gaps in the structure of the stem, typically several millimeters. In other exemplary embodiments of the invention, porous structure  104  covers only a portion of support element  102 . For example, only a portion of support element  102  is covered to avoid restricting luminal flow to a branching vessel. 
         [0079]    In some exemplary embodiments of the invention, porous structure  104  extends past at least one end of support element  102 . This can, for example, better treat the inside surface of a blood vessel at an edge of enhanced stent apparatus  100 , where it is more likely to have restenosis. In an exemplary embodiment of the invention, porous structure  104  pads and/or treats trauma caused by the edge of support element  102  by extending past at least one end of support element  102 . Optionally, porous structure  104  extends no more than 1 mm past the end of support element  102 . Optionally, porous structure  104  extends over 1 mm past the end of support element  102 . Optionally, porous structure  104  extends past only one end or both ends (as shown in  FIG. 10 ) of support element  102 . 
         [0080]    In some exemplary embodiments of the invention, porous structure  104  is attached to support element  102  to prevent porous structure  104  from unraveling and/or causing tissue irritation and/or avoiding dislodgment of the porous structure from the support element during deployment. Optionally, the end of porous structure  104  is folded over the end of support element  102  and attached, providing padding to a potentially trauma causing edge. Optionally, the end of porous structure  104  is folded under itself and is held folded due to the pressure between the support element and the lumen. In an embodiment of the invention, a treatment, such as heat, is used to make the fold sharp and/or permanent. 
         [0081]    It should be understood that while an exemplary configuration of enhanced stent apparatus is shown in  FIGS. 1 and 2 , other configurations could possibly be used, including: a porous structure  104  over a pharmaceutical eluting support element; a pharmaceutical eluting porous structure over a support element  102 ; a pharmaceutical to eluting porous structure over a pharmaceutical eluting support element; a support element in between at least two porous structures, optionally some or all eluting pharmaceuticals; and, an enhanced stent comprised of a plurality of layers which exhibit different optional characteristics such as degradation time and/or pharmaceutical elution. It should be understood that any of the above configurations include biodegradable and/or bioresorbable materials. Optionally, configurations are chosen for specific treatment regimens indicated by the condition of the patient. 
         [0082]    In some exemplary embodiments of the invention, porous structure  104  is used to control the local pressure exerted by the enhanced stent apparatus on the body lumen wall. For example, by increasing or decreasing the coverage area of the porous structure as it at least partially covers the stent, the pressure exerted by the enhanced stent apparatus per unit area can be altered. In some embodiments of the invention, modification of the coverage area considers factors such as the stiffness of support element  102  and the geometry and/or coverage area of the support struts of support element  102 . In an embodiment of the invention, pressure control is used to reduce the likelihood of the enhanced stent apparatus causing plaque to break off of the lumen wall. In some embodiments of the invention, pressure control is used to reduce tissue trauma typically caused by stent implants, thereby enhancing protection against stenosis/restenosis. Furthermore, in some embodiments of the invention, support element  102  struts which could not be used previously due to the likelihood of trauma to the lumen tissue can optionally be used in combination with porous structure  104 . 
         [0083]    In some exemplary embodiments of the invention, bile ducts are treated using at least a porous structure as described herein. For example, the bile ducts often become congested with debris (e.g. cholesterol) which restricts flow. Treatment of the bile ducts using enhanced stent apparatus may increase the diameter of the bile ducts, improving their operation. 
         [0084]    It is known that varying types of body lumens possess varying surface textures, both varying from each other, and sometimes within one type of lumen. Thus, in some exemplary embodiments of the invention, different porous structures with varying surface texture configurations are manufactured and/or used depending on the interior surface texture of a lumen being treated. For example, peaks and valleys in a body lumen are fitted with counter peaks and valleys of a porous structure (i.e. porous structure counter peak goes into lumen valley and porous structure counter valley accepts lumen peak). Optionally, the counter peaks and valleys are of the same magnitude as the peaks and valleys found in the lumen being treated. 
         [0085]    It should be understood that the aperture size, the porous structure thickness, the fiber thickness (or French), and/or the coverage area are varied for different applications. For example when treating the carotids, debris of more than 100 microns should be prevented from reaching the brain, thus the porous structure is designed such that when stent is expanded, usually to about 8 millimeters, the majority of aperture sizes are less than 100 microns. As another example, when treating the coronaries larger debris (&gt;100 microns) is not as problematic, while the endotheliazation process and the non-restriction of flow to side branches is more important. Thus for coronary artery applications, when the support element  102  is in an expanded position, usually about 3 millimeters in diameter, the apertures in the porous structure are optionally larger than 100 microns and below 300 microns. In some embodiments of the invention, the rate of endothelium cell growth over porous structure may be modified by increasing and/or decreasing fiber thickness and porous structure thickness. 
         [0086]    In some exemplary embodiments of the invention, porous structure  104  is used with a balloon expandable support element  102 . In some exemplary embodiments of the invention, porous structure  104  is placed directly on an expandable balloon  802  without or with support element  102 , for example as shown in  FIG. 8 . In some exemplary embodiments of the invention, the balloon catheter may extend past a proximal and/or distal end of support element  102 . It is optionally desirable to provide porous structure  104  which extends past the end of support element  102  to provide a buffer between the balloon and the blood vessel, and optionally to provide pharmaceutical treatment to regions to which the underlying support element  102  does not extend, but may be exposed to the balloon. 
         [0087]    In an exemplary embodiment of the invention, porous structure  104  is under 100 microns in thickness. In some exemplary embodiments of the invention, the porous structure is less than 30 microns thick. Optionally, the porous structure is less than 10 microns in thickness. For example, the porous structure is less than 5 microns or 1 micron thick. Porous structure  104  is optionally comprised of at least one fine, thread-like fiber. In some exemplary embodiments of the invention, porous structure  104  is comprised of at least one fiber that is 40 nm to 40 microns thick. Optionally, to the fiber thickness is similar to or less than the diameter of an endothelial cell to encourage endothelial cell growth between fibers and/or around at least one fiber. In an exemplary embodiment of the invention, a super-fiber is used to construct porous structure  104 , wherein the super-fiber is made of multiple fibers braided together. Optionally, super-fibers are used to enhance the strength of porous structure  104 . 
         [0088]    In an exemplary embodiment of the invention, the fibers of porous structure  104  are spun and/or knitted and/or woven and/or braided to provide structure to and apertures  110  in porous structure  104 . Optionally, the porous structure is woven in an even pattern. Optionally, the porous structure is constructed so that the fibers are randomly positioned in porous structure  104 . Optionally, polymer fibers are used to construct porous structure  104 . Optionally, polymer coverings are applied to porous structure  102  and/or support element  102 . Exemplary porous structure manufacture is described in more detail in the “Methods of Manufacture” section below. 
         [0089]    In an exemplary embodiment of the invention, the polymer covered porous structure  104  is optionally made out of a closed interlocked design and/or an open interlocked design, or semi open design, similar to typical support element  102  designs. The open interlocked design has an advantage when side branching is needed. When treating a junction of two blood vessels, there is sometimes a need to introduce one stent through the side of another one. An open interlocked design allows such a procedure, and when the porous structure is made of metal mesh, an open interlocked design is utilized in order to allow easy side branching stents. Optionally, using a biodegradable polymer coating on a non-biodegradable support element  102  leaves the support element  102  embedded after the biodegradable polymer has degraded. 
         [0090]    In an exemplary embodiment of the invention, porous structure  104  is crimped to a small diameter while still maintaining its flexibility, to enable successful maneuverability through a patient&#39;s blood vessels to the site where enhanced stent apparatus  100  is to be implanted. In an exemplary embodiment of the invention, porous structure  104  is expandable to enable expansion of porous structure  104  with support element  102  upon deployment at a treatment site within a patient&#39;s blood vessel. Optionally, expansion of porous structure  104  along the longitudinal axis matches the expansion of support element  102  along the longitudinal axis. 
         [0091]    In an exemplary embodiment of the invention, at least porous structure  104  is expandable without significant foreshortening or elongation of the length of porous structure  104 . Optionally, porous structure  104  expands differently than support element  102 , for example using sliding connections described herein. As described elsewhere herein, in a knitted embodiment of porous structure  104 , expansion occurs at least partially as a result of the knitted structure, and not necessarily because of the elasticity of the fiber used in constructing porous structure  104 . In an embodiment of the invention, at least one fiber which comprises porous structure  104  is provided with slack during manufacture to provide additional fiber material when porous structure  104  expands.  FIG. 9  shows a perspective view of an enhanced stent apparatus  900 . Enhanced stent apparatus  900  is provided with non-stretchable wires  902 , and stretchable elastomer fibers  904 , in accordance with an exemplary embodiment of the invention. Such an embodiment assists with the preservation of overall apparatus  900  length while allowing expandability and flexibility during implantation. 
         [0092]    In an exemplary embodiment of the invention, an enhanced stent apparatus is provided which is comprised of at least an expandable support element and an expandable porous structure. The support element is optionally a stent, examples of which are known in the art for providing treatment to a wide range of body lumens. In an embodiment of the invention, the porous structure has structure which resembles to fishing net. In an embodiment of the invention, the porous structure is knitted from a fiber approximately 15-20 microns in diameter, has a coverage area of less than 20%, and which has aperture sizes approximately 150.times.200 microns. In some embodiments of the invention, the porous structure is at least temporarily attached to support struts of the support element by stitching. Optionally, the stitches are loose, allowing the porous structure to slide on the support struts, for example to provide extra expendability as described herein with respect to  FIG. 16 . In some embodiments of the invention, the stitching is biodegradable. In some embodiments of the invention, the support element and/or the porous structure are adapted to elute pharmaceutical agents into the body lumen being treated. 
         [0093]    In some embodiments of the invention, different characteristics of the enhanced stem apparatus are chosen based on the intended use or treatment to be rendered. For example, aperture sizes are optionally chosen based on a desire to provide embolic shower protection against debris of a certain size. As another example, coverage area is optionally selected for modifying local pressure on the lumen being treated. Many of these characteristics are interrelated, as described herein and shown in  FIG. 15 , for example. 
         [0094]    In an embodiment of the invention, porous structure  104  is flexible to allow the lumen to naturally change its diameter, to account for pressure changes in the lumen and/or to respond to muscular activity. In some embodiments of the invention, the porous structure  104  divided into a plurality of semi-independent sectors, which react differently to stimuli within or from the lumen. Optionally, the sectors are used to prevent banding of the lumen across the entire length of the porous structure  104 . 
       Exemplary Characteristics and Performance of Porous Structure 
       [0095]    Manufacturing techniques, described in more detail below, such as knitting which provide slack to individual fibers, or sections, of porous structure  104 , enable porous structure  104  to optionally expand upon deployment up to 10 tunes its diameter at insertion (insertion diameter is described in more detail below), in an embodiment of the invention. For example, in coronary applications porous structure  104  may expand from 1 mm to 3 mm in diameter. In other examples, porous structure  104  may expand from 2 mm to 8 mm in carotid applications, while in brain applications porous structure  104  may expand from 0.3 mm to 2.5 mm. These numbers are approximate and are by way of example only. In an embodiment of the invention, expansion of porous structure  104  is effectuated in at least one of three ways: 1) the knitted/braided/woven structure of porous structure  104  (including slack in the fibers and curly fibers); 2) the fiber from which the porous structure  104  is made is at least slightly elastic; 3) sliding connections (described below) between porous structure  104  and support element  102  permit shifting of porous structure  104  during expansion with respect to support element  102 , within certain limits. In an embodiment of the invention, the fiber from which porous structure  104  is made is comprised of between 2% and 80% of non-elastic materials. In some embodiments of the invention, the elastic material of the fiber from which porous structure  104  is made allows for expansion up to 1000% its original size. 
         [0096]    In some exemplary embodiments of the invention, porous structure  104  exhibits a high durability when subjected to twisting, turning, compression and/or elongation, which allows porous structure  104  to withstand the delivery process through the patient&#39;s vasculature to a treatment site. In an embodiment of the invention, porous structure  104  is loosely attached to the balloon at several locations and folded for insertion into a lumen, such as depicted in  FIG. 12 ; such a configuration is optionally used in conjunction with supportive element  102 . The folded porous structure  104  provides a reduced diameter apparatus for easier insertion into body lumens of the patient. As described below, porous structure  104  is at least temporarily fastened to balloon to prevent porous structure  104  from becoming dislodged during implantation. 
         [0097]    In some exemplary embodiments of the invention, 20% of the total area of porous structure  104  is comprised of apertures having an approximate diameter no greater than 50, 200 or more than 200 microns in an expanded configuration. It is recognized that during the course of manufacturing the porous structure, for example with certain manufacturing techniques like electrospinning and/or knitting, apertures created within the porous structure may overlap. This overlap effectively creates an aperture size which is smaller than specified. However, in some exemplary embodiments of the invention, the effective, nominal aperture size is no greater than 50, 200 or more than 200 microns in diameter. In some embodiments of the invention, aperture sizes are selected to encourage endothelial cell overgrowth at a certain rate. 
         [0098]    It should be noted that shapes of apertures are likely to vary at least somewhat as a result of manufacture and/or desired properties of porous structure  104 . For example, in a knitted porous structure, apertures are most likely to be roughly square. In contrast, use of a weaving technique to manufacture porous structure likely produce square and/or rectangular shaped apertures whereas a braided porous structure is likely to exhibit quadrilateral shaped apertures, such as in  FIG. 7 . In describing an approximate “diameter” of an aperture, it should be recognized that all, some or none of the apertures will be actual circles, squares, rectangles and/or quadrilaterals capable of simplistic area measurement using diameter. Therefore, description using diameter is merely an approximation to convey exemplary aperture sizes. For example, “diameter” could be the distance between two parallel sides of a quadrilateral, such as a square or rectangle. 
         [0099]    In some parts of the following description, aperture sizes described herein are in reference to their size upon porous structure deployment in a lumen. In other parts, the sizes refer to the aperture sizes when crimped. Sometimes, the aperture sizes described herein refer to their size in a state intermediate a crimped and deployed configuration. In context, it should be easily perceived which of the above configurations applies, however, in the event it is not clear the aperture sizes could be considered as applying to expanded, crimped or intermediate configurations. When a fiber diameter is referred to, it relates to the fiber used to construct the porous structure  104 . For example, if porous structure  104  is constructed from a super-fiber comprised of a bundle of 10 fibers each 2 microns in diameter, the overall super-fiber diameter is about 20 microns. Furthermore, it should be understood that references to fiber diameter are for approximation and convenience only and does not imply that the fiber is necessarily round. Optionally, fiber sizes are measured in French sizes, for example 0.003 Fr. 
         [0100]    Referring to  FIG. 15 , a graph  1500  is shown which correlates fiber thickness of porous structure with percentage of the coverage area of a support element, for a porous structure with a fishing net type configuration. It can be seen that the general trend is that as the fiber sizes get thinner, the amount of porous structure surface area dedicated to structure is reduced. In an embodiment of the invention, it is desirable to have under 25% coverage area. Optionally, porous structure  104  exhibits less than 20% coverage area. In an embodiment of the invention, the coverage area of the porous structure is adapted to be minimized while still performing an intended lumen treating function, such as those described herein. In some embodiments of the invention, the coverage area of porous structure  104  is minimized in order to avoid undesirable clinical side effects. For example, lumen tissue irritation and pyrogenic effects are considerations for minimizing the coverage area and optionally other characteristics such as aperture size, porous structure thickness and/or fiber thickness, of porous structure  104 . 
         [0101]    In some exemplary embodiments of the invention, the proportion of structure to apertures of porous structure  104 , fiber size and/or apertures are sized in order to allow easy diffusion through porous structure  104  and to facilitate growth of endothelial cells. Since the fiber  2202  diameters used in construction of porous structure  104  are on the order of the size of the endothelial cells  2204 , or smaller, as shown in  FIG. 22 , the integrity of the cells grown over the porous structure will be much better than what is achieved in the prior art. An individual cell, statistically, will have a firm connection to the blood vessel wall, since it is of the same order or larger than the fiber diameter, thus anchoring itself in an embodiment of the invention, in more than one location to its native basalamina intimal layer and enabling better growth conditions. It is thus expected that the chance of late or sub-acute thrombosis can be reduced over what is currently achieved when treatment is performed using a pharmaceutical eluting stent. In addition, porous structure  104  effectively acts as an embolic shower protection device, holding detached plaque in place, preventing it from traveling from the vessel wall into the blood stream. It should be noted that porous structure  104  is configured, accounting for fiber thickness, porous structure thickness and/or aperture size such that endothelial cells will overgrow porous structure  104 , and optionally support element  102 , in order to secure the enhanced stent in place and/or insulate the foreign material of support element  102  and/or porous structure  104  from the bloodstream. In an exemplary embodiment of the invention, endothelial cell layer overgrowth of porous structure  104  is established within hours of implantation. In an embodiment of the invention, overgrowth is accomplished within this time frame due to characteristics of porous structure  104  as they relate to endothelial cells, for example, the overall thickness being on the same order of, or smaller, than an individual endothelial cell. In some embodiments of the invention, it is conceived that a patient&#39;s average stay in the hospital after a stenting procedure can be reduced as a result of the speed of endotheliazation using enhanced stent apparatus. In addition, the speed and efficacy of pharmaceutical treatment can expected to be enhanced as a result of the rapid endotheliazation over at least porous structure  104  of enhanced stent apparatus  100 . 
         [0102]      FIG. 23  shows a disadvantage of using prior art drug eluting stents wherein a clump of endothelium cells have become detached from the stent strut  2304 , revealing an exposed “island”  2302  of the stent. Sometimes a clump falls off strut  2304  due to poor adhesion of the endothelium cells to the polymer coating of the strut  2304 . Contributing to this poor adhesion, the stent strut  2304  is typically an order of magnitude larger than a single endothelium cell, thereby necessitating the creation of a large endothelium cell bridge to cross the strut. The exposed island  2302  can serve as a seed for thrombosis development. In some embodiments of the invention, porous structure  104  is constructed to reduce the likelihood of endothelial cells falling from the porous structure, thereby reducing the chance of development of late or sub-acute thrombosis and exposure of support element  102  to substances within the lumen. For example, endothelial cell retention is optionally encouraged by constructing porous structure  104  from at least one fiber of a thickness and with aperture sizes (to permit growth of endothelial cell therethrough), such as described herein. Optionally, endothelial cells are encouraged to remain on the porous structure by using a fiber layer of a thickness such as those described herein. Optionally, the linear nature of a single fiber porous structure  104 , such as shown in  FIG. 22 , reduces the possibility of a large clump of endothelial cells becoming dislodged. In an embodiment of the invention, porous structure  104 , optionally imbued with a pharmaceutical, is placed on the interior of a bare metal or drug eluting support element in order to reduce the thrombogenicity of the support element. For example, by encouraging endothelial cell growth thereover and/or by reducing the exposed surface area of the support element by covering a portion of it up. 
         [0103]    As suggested above, using a thin fiber whose thickness is similar to, or smaller than, the diameter of an endothelial cell enables an endothelial cell layer to grow over porous structure  104  while still being closely tied to the basal intima layer at least at two points of the endothelial cell, one point on each side of porous structure  104 . In an embodiment of the invention, the anchoring effect of this basal intima layer on the endothelial cell layer reduces the chance of parts of the endothelial cell layer breaking off and entering the lumen. This, in effect, reduces the chances of embolism in the patient and/or also reduces the likelihood of foreign bodies (e.g. the stent and the porous structure) coming into contact and reacting with the contents of the lumen being treated. In the event that a clump of several endothelium cells fall from porous structure  104 , exposing a piece of the fiber, it is believed that there is a reduced chance of harm to the patient since the linear, single endothelial cell width geometry is not as thrombogenic as that shown in  FIG. 23 , where a clump of endothelial cells at least several cells in diameter has fallen off. In addition, the re-endotheliazation will be faster on an exposed porous structure  104  than on the exposed strut  2304  for at least the reason that in the case of the porous structure  104 , an endothelial cell layer is formed when just one endothelial cell overgrows the endothelial cell sized fiber used to construct the porous structure. In contrast, endothelial cell layer overgrowth is only accomplished after multiple endothelial cells have covered the exposed island. 
         [0104]    In an embodiment of the invention, the reduced risk of late or sub-acute thrombosis by using porous structure  104  for pharmaceutical elution optionally allows for a duration and/or dosage reduction in the use of anti-coagulants by the patient. 
         [0105]    In some exemplary embodiments of the invention, fiber thickness, porous structure thickness and/or aperture size are all separately varied depending on the application of porous structure  104  and the needs of the patient. For example, in the coronary arteries it is sometimes helpful to provide for good pharmaceutical dispersion. In such an example, fibers comprising porous structure  104  are optionally located closer together in order to allow for more complete transmission of a pharmaceutical to patient. 
         [0106]    In some exemplary embodiments, when large molecule drugs, which have a poor diffusion into the tissue, are used to fight restenosis, the porous structure can be soaked and/or imbued with an appropriate drug in order to better diffuse it. The maximum concentrations of most of the drugs used are rather limited due to side effects and over toxicity, and at the same time the concentration is not enough in order to allow the optimum pharmacokinetics in areas not covered by the stent struts. The porous structure mesh, having a better geometrical cover of the stent area, provides a better and more optimum pharmacokinetics to the whole area covered by the stent. For example, when high Dalton-large molecule drugs are used, or when liposomes are the carriers of the treatment agents, or when the stereo-chemical structure of the drug is large and/or complicated, and/or when the drug is hydrophobic, relatively even distribution of the drug is highly desirable. In some exemplary embodiments of the invention, pharmacokinetics are also optimized because the drug is located on/in the fibers of porous structure  104 , and is covered and sealed within an endothelium layer, which helps the drug from being washed away by the blood. 
         [0107]    In some exemplary embodiments of the invention, such as in a bypass vein graft, side branching is not an issue, therefore aperture sizes are optionally made smaller, but not so small as to prevent endothelial cell growth therethrough. In another exemplary embodiment of the invention, such as in the carotid arteries, side branching is not generally considered a problem, but catching debris is. Therefore, in some exemplary embodiments of the invention, the aperture sizes of porous structure  104  are decreased to as little as 20 microns in diameter. In other applications, the aperture size can be increased to 50, 100, 200 or even more then 200 microns, depending on the application of enhanced stent apparatus  100 . 
         [0108]    In some exemplary embodiments of the invention, a plurality of porous structures is used. Optionally, at least one porous structure is located on the interior of support element  102 , inside the lumen of support element  102 . Optionally, more than one porous structure is located on the exterior surface of support element  102 . In some exemplary embodiments of the invention, at least some of the porous structures located on support element  102  are configured to be “in-phase” where the apertures of the porous structures coincide with one another. Optionally, the porous structures are “out-of-phase” where the apertures are configured to not coincide with one another. In an exemplary embodiment of the invention, an “out-of-phase” configuration is used to improve contact surface area between porous structures and the lumen interior surface. In an embodiment of the invention, increased contact surface area can improve pharmacokinetics, reduce local pressure exerted by porous structure  104  on the lumen wall, improve embolic shower protection and/or realize other advantageous effects. In some exemplary embodiments of the invention, porous structure  104  is constructed in the same shape and pattern as support element  102 , but on a smaller scale. 
       Exemplary Materials of Manufacture 
       [0109]    It should be noted that in some exemplary embodiments of the invention, a stretchable and/or expandable porous structure  104  is desired. Therefore, in some embodiments of the invention, materials are chosen which are either a) stretchable and/or b) can be used to manufacture a porous structure which is stretchable (e.g. a knitted structure). In some exemplary embodiments of the invention, biodegradable (i.e. are broken down by the body) and/or bioresorbable (i.e. are absorbed into the body) materials are used. In addition, blends of materials are used in accordance with some embodiments of the invention. In an embodiment of the invention, a material is chosen because it exhibits durability during manufacture, deployment and/or use despite being thin. In an embodiment of the invention, other considerations for the material to be used are their biocompatibility, toxicity, hemocompatibility, and thrombogenicity. 
         [0110]    Exemplary materials for manufacturing porous structure  104  include natural-based materials such as modified cellulose and/or collagen. In some embodiments of the invention, metal fibers are used to construct porous structure, optionally constructed of stainless steel, and/or CoCr and/or CoNi alloy among other possibilities. Optionally, the metal fibers used are coated with at least one polymer. In some embodiments of the invention, porous structure is manufactured from a shape memory alloy, such as nitinol. Optionally, carbon fiber is added to porous structure  104  in order to improve strength characteristics of porous structure  104 . Optionally, glass fiber is added to porous structure  104  in order to improve strength characteristics of porous structure  104 . Optionally, a durable, resorbable and/or degradable fiber is added to porous structure  104  in order to improve strength and durability characteristics of the fiber during manufacture, which is degraded or resorbed or washed away to leave a thinner porous structure  104 . 
         [0111]    In an embodiment of the invention, some polymer fibers are chosen for use in constructing porous structure  104  because they are elastic, biocompatible, hemocompatible, can be made not to stick to an expandable angioplasty-type balloon catheter, to stick to endothelium tissue, are selectably bio-stable and/or biodegradable, exhibit the requisite mechanical strength, are sterilizable, have a high temperature transformation zone (solid and non sticky at 37° C.), are capable of hosting an effective amount of pharmaceuticals, and/or can release embedded pharmaceuticals at a controlled rate. In some exemplary embodiments of the invention, other materials which exhibit some or all of these properties are optionally used to construct porous structure  104 . Optionally, coatings are put on porous structure  104 , comprised of materials which exhibit some or all of these properties. 
         [0112]    Polymer fibers are optionally made out of any of the following materials: thermoplastic polymers for example polyethylene terephthalate (PET), polyolefin, oxidized acrylic, PTFE, polyethylene co-vinyl acetate, polyethylene elastomer, PEO-PBT, PEO-PLA, PBMA, polyurethane, Carbosil (PTG product), medical grade polycarbonate urethanes, Nylon, PEEK-Optima, carboxylic acid moiety comprising one or more of a poly acrylic acid, a poly methacrylic acid, a maleic acid, a helonic acid, a laconic acid and/or combinations and/or esters of these monomers, thermoplastic polymers, thermosetic polymers, polyolefin elastomers, polyesters, polyurethanes, polyfluoropolymers, and/or nylon. Optionally, the fibers are constructed of an elastomer. Optionally, the fibers are constructed of a coated fiber with a drug and polymer coating mixed to get a predetermined drug release characteristic, either coating over a metal and/or over a polymer fiber. Optionally, the fibers are constructed of other materials than the exemplary materials listed above. Exemplary polymers which are optionally used for this purpose are manufactured by Cordis®, Surmodix®, Boston Scientific®, Abbott® and Hemoteq® Polymers. Optionally, these polymers are selected for at least one of the reasons specified in the paragraph above. Optionally, the coating is used to facilitate the elution of pharmaceuticals from porous structure  104 . 
         [0113]    In some embodiments of the invention, the porous structure is made out of a resorbable/degradable polymer such as poly lactic-co-polyglycolic (“PLGA”) copolymers, or any other degradable copolymeric combination, such as polycaprolactone (“PCL”), polygluconate, polylactic acid-polyethylene oxide copolymers, poly(hydroxybutyrate, polyanhydride, poly-phosphoester, poly(amino acids), poly-L-lactide, poly-D-lactide, polyglycolide, poly(alpha-hydroxy acid) and combinations thereof. 
         [0114]    In some embodiments of the invention, porous structure  104  is comprised of a material which plastically or elastically deforms when a sufficient amount of radial pressure is applied to it, for example by an angioplasty balloon. 
       Exemplary Methods of Manufacture 
       [0115]    Many of the methods and orientations described herein are designed to provide a porous structure which exhibits at least some expandable quality. Porous structure  104  is optionally adapted and constructed to stretch as it is being deployed within the lumen being treated. In some exemplary embodiments of the invention, porous structure  104  is provided with stretchability in order to ease positioning porous structure  104  on a balloon and/or support element  102 . 
         [0116]    In an exemplary embodiment of the invention, weaving, braiding and/or knitting results in some or all the elasticity of the porous structure being achieved due to the structure of the interlaced and/or crimped and/or textured fibers (curly, slack). This can be achieved by material elongation properties securing the porous structure to the stent. In some exemplary embodiments of the invention, a porous structure is made by combining several interlacing techniques such as knitting over a braided porous structure or braiding over a knitted porous structure. In some embodiments of the invention, multiple layers are combined and/or created using these techniques. In some exemplary embodiments of the invention, a warp knitted porous structure with “laid in” yarns is used. In some exemplary embodiments of the invention, a porous structure is woven using elastomeric or crimped weft to obtain radial elasticity. 
         [0117]    In some exemplary embodiments of the invention, the porous structure is manufactured by combining several techniques such as knitting over a braided porous structure or braiding over a knitted porous structure. In some exemplary embodiments of the invention, a weft knitted porous structure with “laid in” yarns is used. In some exemplary embodiments of the invention, a porous structure is woven using elastomeric and/or crimped weft to obtain radial elasticity. Optionally, porous structure is comprised of at least one fiber oriented generally parallel to the support elements longitudinal axis. 
         [0118]    In an exemplary embodiment of the invention, a manufactured porous structure is added as a cover to support element  102 . Optionally, porous structure  104  is used separately from support element  102 , which is optionally not used for stenting. In some exemplary embodiments of the invention, porous structure  104  is manufactured directly onto support element  102 . 
         [0119]    In an exemplary embodiment of the invention, porous structure  104  is manufactured by a knitting technique known to those skilled in the knitting art for non-analogous arts, such as clothing manufacturing and textiles. Knitting of porous structure  104  is optionally performed by heads having between 20 and 35 needles. Optionally, the head used has between 30 and 45 needles. Optionally, the head used has between 35 and 80 needles. An example of the effect of head size on the porous structure an be seen in  FIG. 15 , described above, in which a 22 size head and a 35 size head are graphed. In FIG. IS, the needle gauges are 40. 
         [0120]    In some embodiments of the invention, the shape and/or size of the knit is controlled by controlling the tension on the fiber being used for knitting. For example to create a knit with larger eyes, slack is provided to the fiber during knitting. Optionally, the fiber is controlled during knitting to achieve a circular shaped eye when porous structure  104  is expanded. In an embodiment of the invention, pre-tension on the fiber during knitting is approximately 10-20 grams. In some embodiments of the invention, post-tension on the fiber during knitting is 15-25 grams. The stitch length is between 300 and 400 microns, in an exemplary embodiment of the invention. In some embodiments of the invention, the knitting machine is run at a relatively slow speed. For example, the knitting machine is run at 10% of speed capacity using a Lamb Knitting Machine Corp. System Model WK6 with a special modification of speed operation measured by percentage. 
         [0121]    In an exemplary embodiment of the invention, a fiber or a super-fiber yarn with a specific fineness, or a range of fineness, between 5 and 100 microns is used to manufacture a knit porous structure. Optionally, yarn with a fineness of 10 to 20 microns is used to manufacture a knit porous structure. Optionally, the yarn is finer than 5 microns. Yarn fineness is often referred to in textile terms by “Tex”. This is the weight in grams of 1000 meters of the yarn. In an exemplary embodiment of the invention, yarn ranging from 0.3 Tex to 10 Tex is used to manufacture porous structure. In some embodiments of the invention, a specific yarn fineness is chosen based on the desired porous structure  104  characteristics. For example, a 0.5 Tex yarn using a 22 gauge needle head will, in some embodiments, produce a porous structure with approximately 12% coverage area. 
         [0122]    An exemplary resulting porous structure using the above components and techniques, should have 5 to 50 courses per cm. Optionally, 20 to 45 courses per cm are manufactured. Optionally, a porous structure with 30-35 courses per an is manufactured.  FIG. 5  illustrates a knitted porous structure  104  and support element  102  in a crimped, closed position.  FIG. 6A  illustrates a knitted porous structure  104  laid on top of a support element  102  in an open position.  FIG. 6B  shows exemplary knitting in detail. 
         [0123]    In another exemplary embodiment of the invention, weaving techniques are used to manufacture porous structure  104 . Narrow needle looms as well as conventional narrow looms can be configured to produce woven tubular structures. In weaving, at least two layers of warp yarns are interlaced with intersecting fill yarns. 
         [0124]    By carrying the fill yarn alternately back and forth across two layers of warp yarns, a tubular shape is created. The size and shape of the weave are optionally controlled by determining the warp and/or fill density, the interlacing pattern and/or frequency, the yarn tension and/or the yarn dimensions and/or elastic properties. The types of weaves used for a porous structure are optionally one of “plain”, “basket”, “twill”, “sateen”, “leno” and/or “jacquard”. Optionally, all of the fibers of porous structure are the same. Alternatively, warp and weft fibers of a weave are not constructed of the same materials. Optionally, different materials are used to take advantage of the inherent properties of the different materials, for example one material may be elastic and a different material may have a high tensile strength. Optionally, warp fibers are coated and/or are pharmaceutical eluting while the weft fibers are not, or vice versa. 
         [0125]    In another exemplary embodiment of the invention, braiding techniques are used to manufacture porous structure  104 , for example as described in Knitting Technology. D. J. Spencer—ed., Woodhead Publishing Limited, Abington Hall, Abington, Cambridge, CB1 6AH, England, the disclosure of which is incorporated herein by express reference thereto. Braiding machines are optionally used to interlace yarns at a variety of intersecting angles. In braiding, multiple yarns are fed to an interlacing zone. Interlacing is optionally achieved by rotation of the yarn spools or by a reciprocating needle bed. The size and shape of the braid is optionally controlled by the number of yarns, the interlacing pattern and/or angle and/or the yarn dimensions and/or elastic properties. Optionally, all of the fibers of porous structure are the same. Optionally, warp and weft fibers of a braid are not constructed of the same materials, for example where weft fibers are used to provide strength and warp fibers are used to provide stretchability of the braid. 
         [0126]    In another exemplary embodiment of the invention, porous structure  104  is manufactured by an electrospinning process. Electrospinning is a technique which utilizes a charged polymer solution (or melt) that is fed through a small opening or nozzle (usually a needle or pipette tip). Because of its charge, the solution is drawn toward a grounded collecting plate (usually a metal screen, plate, or rotating mandrel), typically 5-30 em away, as a jet. Optionally, support element  102  is placed on a delivery catheter which is used as a mandrel. During the jet&#39;s travel, the solvent gradually evaporates, and a charged polymer fiber is left to accumulate on the grounded target. The charge on the fibers eventually dissipates into the surrounding environment. The resulting product is a non-woven fiber porous structure that is composed of tiny fibers with diameters between approximately 40 nanometers and 40 microns (e.g. a felt), depending on the size of the fibers input into the system. If the target is allowed to move with respect to the nozzle position, such as by rotating and/or moving the mandrel along its longer axis, specific fiber orientations (parallel alignment or a random alignment, as examples) can be achieved. In some exemplary embodiments of the invention, porous structure  104  is spun in a helical coil pattern onto the mandrel or support element  102 . Optionally, porous structure  104  is comprised of a plurality of helical coil patterns, constructed by moving the mandrel back and forth, such as depicted in  FIG. 4 . Optionally, porous structure  104  is constructed with fibers oriented substantially parallel to central axis  106 . Optionally, porous structure  104  is constructed with fibers oriented substantially perpendicular to central axis  106 . Optionally, porous structure  104  is constructed with fibers oriented in a combination of any of the orientations described or suggested herein. The mechanical properties of the porous structure are optionally altered by varying the fiber diameter and orientation depending on the requirements for treating a patient. For example, in some embodiments of the invention, a laser is used to cut specific aperture sizes and/or to ensure that the apertures traverse from the exterior side of porous structure  104  to the interior side of porous structure  104 . Optionally, solvent is used to modify aperture sizes. 
         [0127]    Optionally, portions of catheter are masked in order to prevent accidental coverage of the delivery catheter by porous structure  104 . Optionally, support element  102  is coated with an adhesive and/or a pharmaceutical agent prior to putting the porous structure  104  on the top of support element  102 . In some exemplary embodiments of the invention, the material used to produce the porous structure  104  is imbued with pharmaceutical agents. Optionally, pharmaceutical agents are embedded in the material coating the porous structure  104 . In an exemplary embodiment of the invention, porous structure  104  is comprised of at least one inner coating proximal to supporting structure  102  which exhibits different properties than an external coating proximal to patients blood vessel. For example, the inner coating is optionally configured to avoid adhesion to the delivery catheter and/or support structure. Optionally, inner coating is configured to adhere to support element  102 , but not to delivery catheter. 
         [0128]    In some embodiments of the invention, porous structure  104  is designed to be less sensitive to foreshortening and elongation forces as porous structure  104  expands upon deployment. This is in part due to the knitted nature of porous structure  104 , in some embodiments. This property allows porous structure  104  to be secured to support element  102  at its ends, rather than in another location, such as the middle as described in U.S. App. No. 2005/0038503 to Greenhalgh et al., the description of which is incorporated herein by express reference thereto. 
         [0129]    In some exemplary embodiments of the invention, a porous structure is manufactured in an at least partially open, wide diameter, condition. In some exemplary embodiments of the invention, the at least partially stretched porous structure is reduced to a smaller diameter, by heat-setting, crimping and/or folding, after manufacture. 
         [0130]    In an embodiment of the invention, the diameter of the at least partially stretched porous structure is reduced mechanically. Optionally, a funnel  1304  shown in  FIG. 13 , is used to reduce the diameter of the knitted porous structure  1302 , during the manufacture the porous structure. A knitted porous structure  1302  is drawn down from the knitting zone into a narrowing bore, funnel  1304 . This results in a final porous structure diameter that is controllably smaller than the diameter of the needle bed.  FIG. 14 , illustrates how a porous structure is manufactured using a stretched rubber tube  1402 . In this method, the porous structure  1400  is tightly inserted onto a pre-radially stretched tube  1402 , and then the tube is relaxed, compressing the porous structure and creating a smaller aperture sized porous structure, the size of which is controlled by the stretch ratio of the rubber tube. 
         [0131]    Referring to  FIG. 18 , an embodiment is shown in which porous structure  104  is folded in “n” substantially folds, the folds used to reduce the overall diameter of enhanced stent apparatus  100  for easier insertion and navigation through the patient. Optionally, the folds are towards the same direction. In an embodiment of the invention, a folded porous structure  104  is at least temporarily secured to support element  102 .  FIG. 11  shows an alternate folded configuration from a perspective view. 
         [0132]    An additional or alternative embodiment to folding includes heat setting a polymer comprised porous structure  104  to support structure  102 . In an embodiment of the invention, heat setting is used when porous structure  104  is comprised of at least one polymer material. Determination of heat setting conditions is related to the polymer&#39;s heat transition temperatures, in an embodiment of the invention. Heat setting is performed in the temperature range between T g  and T m  of the polymer. At this range the polymer becomes amorphous and is shrunk to support element  102 , establishing an overall enhanced stent apparatus  100  radius that is not much more than the support element  102  radius. For example, porous structure  104  adds less than 10 microns in diameter total to support element  102  which is 1 mm in diameter, in some embodiments of the invention. At T m  the polymer turns into a viscous liquid which loses its mechanical integrity and will stick to support element  102  surface. For example, polyethyleneterephthalate (PET) has a T g  of 70° C. and a T m  of 265° C., therefore the heat set temperature somewhere within that range, in an embodiment of the invention, is 200° C. Using temperatures higher than T m  for heat setting can cause thermal degradation, which results in polymeric chain scission, unzipping of the polymer and/or producing a large array of oligomeric material that changes the mechanical properties of porous structure  104  and/or releases poisonous and/or non-biocompatible materials, causing an inflammatory reaction in the patient. Other exemplary polymers which can be used in heat setting are below in Table 1 (not an exhaustive list): 
         [0000]    
       
         
               
             
               
               
               
               
               
             
           
               
                 TABLE 1 
               
             
             
               
                   
               
               
                 TABLE-US-00001 Exemplary polymers and 
               
               
                 temperatures for heat setting Material name 
               
             
          
           
               
                   
                 Material name 
                 T g   
                 T m   
                 set temp. 
               
               
                   
                   
               
               
                   
                 PP 
                 18° C. 
                 165° C. 
                 140° C. 
               
               
                   
                 NYLON 6,6 
                 80° C. 
                 256° C. 
                 210° C. 
               
               
                   
                 PTFE 
                 150° C.  
                 330° C. 
                 300° C. 
               
               
                   
                 PVA 
                 100° C.  
                 230° C. 
                 190° C. 
               
               
                   
                 Polyurethanes 
                 70° C. 
                 120° C. 
                 100° C. 
               
               
                   
                 PLLA 
                 60° C. 
                 175° C. 
                 100° C. 
               
               
                   
                   
               
             
          
         
       
     
         [0133]    Another additional or alternative embodiment to folding includes crimping using at least a crimped support element  102  in combination with porous structure  104 . In some embodiments of the invention, porous structure  104  is crimped with support element  102 . In an embodiment of the invention, crimping of porous structure  104  and support element  102  is performed when it is desirable to reduce the overall diameter of enhanced stent apparatus  100 . For example, a reduced diameter enhanced stent apparatus  100  allows for easier insertion and navigation of the apparatus to the treatment site. In some embodiments of the invention, at least a crimped support element  102  provides an object with relatively stable mechanical properties for more predictable movement during insertion and navigation. 
         [0134]    Optionally, porous structure  104  is made on a non-crimped support element  102 . A non-crimped support element  102  can be expanded or semi-expanded during manufacture. In an exemplary embodiment of the invention, porous structure  104  and support element  102  are crimped together. Optionally, excess porous structure  104  material, which is created as a result of reducing the profile of support element  102  during crimping, is folded with support element  102 , such as shown in  FIG. 18 . In some exemplary embodiments of the invention, porous structure  104  is made on a crimped or partially crimped support structure  102 . When manufacturing a porous structure for placement on an already crimped support structure, consideration may be given to providing a porous structure which is sufficiently stretchable to expand with the radial expansion of the support structure, when implanted at a treatment site within a lumen. In some embodiments of the invention, a porous structure is placed on a support element already positioned on an angioplasty balloon. 
         [0135]    In electrospinning embodiments of the invention, the procedure for manufacturing a porous structure on a balloon is similar to manufacturing on a stent or mandrel. For example, varying the motion of the balloon with respect to the electrospinning device allows the manufacture of specific fiber orientations. 
       Exemplary Methods for Costing a Fiber 
       [0136]    In another exemplary embodiment of the invention, a manufacturing technique is used to coat a fiber that porous structure  104  is comprised of with at least one polymer layer. For example, a dipping technique, shown in  FIG. 19 , using a biocompatible, hemocompatible, biostable and/or biodegradable polymer dissolved in an organic solvent is utilized to create a dipping solution  1906  for use in coating the fiber comprising porous structure  104 . The fiber to be coated is optionally placed in a spool  1902 , from which the fiber  1904  is drawn to form porous structure  104 . Additives such as drugs, biological components, enzymes, growth factors, and/or any other additive mentioned herein or known in the art, may be incorporated into fiber  1904  during the manufacturing process, for example by placing them in solution  1906  and passing fiber  1904  through solution  1906 . In an embodiment of the invention, at least one layer is used in order to control the drug/biological additive&#39;s release. For example, more than one solution tank may be provided for fiber  1904  to pass through during manufacture. Fiber  1904  is optionally moved into a drying oven  1908  with an operational temperature range from 37-70° C. (in some embodiments of the invention) depending on the drug used, to dry solution  1906  onto fiber  1904 . In an exemplary embodiment of the invention, fiber  1904  is then used by a knitting system to  1910  to manufacture porous structure  104 . Optionally, knitting system  1910  is the Lamb Knitting Machine Corp. System Model WK6. Optionally, porous structure  104  is coated with a polymer layer after it has been manufactured. 
         [0137]    In some exemplary embodiments of the invention, support element  102  and porous structure  104  are coated with an additional substance. Optionally, the additional substance is a polymer. Optionally, the additional substance is drug eluting. Optionally, the coating is hyaluronic acid. Alternatively or additionally, the coating is hyaluronan. Optionally, a different non-woven technology such as wet and/or dry spinning is used to manufacture porous structure  104 . In some embodiments of the invention, additional coatings are added to achieve different effects, for example timed release of pharmaceutical agents and/or release of a plurality of agents at different times. 
       Exemplary Methods for Mounting Porous Structure to Support Element 
       [0138]    In some embodiments of the invention, porous structure  104  is at least temporarily secured to support element  102 . Advantages of securing porous structure  104  to support element  102 , at least temporarily, include: prevention of unraveling and/or run out of fiber from the porous structure weave, dislodgement and/or slipping of porous structure  104  with respect to support element  102  during insertion, delivery and/or deployment. Optionally, support element  102  and porous structure  104  are not secured together using an adhesive and/or other securing means despite being in a coaxial and proximate relationship in many embodiments. 
         [0139]    In some exemplary embodiments of the invention, where support element  102  is optionally coated with a polymer, support element  102  and porous structure  104  are attached together by curing at the same time the polymer support element coating and the polymer comprised porous structure, and/or coated porous structure, thus adhering the polymers together. Optionally, pressure and/or heat is used to adhere a polymer coated support element  102  to a non-coated or polymer coated porous structure  104 , for example when they are both hot. In some exemplary embodiments of the invention, porous structure  104  is comprised of two components, an external component and an internal component, relative to support element  102 . Upon the simultaneous curing of the external and internal components, the polymers of which both are comprised to adhere together, thereby securing porous structure  104  to support element  102 , which is located between the components. 
         [0140]    In an exemplary embodiment of the invention, porous structure  104  is secured to support element  102  in order to avoid porous structure migration, but not limit porous structure  104  and/or support element  102  expendability. 
         [0141]    In some exemplary embodiments of the invention, an adhesive is used to bond support element  102  and porous structure  104  together. Optionally, porous structure  104  is glued to support element  102  utilizing any natural and/or synthetic biocompatible adhesive, such as cyanocrylate, thermo plastic elastomers, silanes, laminin, albumin and/or fibrinogen and/or PEG-PEG adhesive, and/or polyurethane adhesive and/or any other suitable compatible polymeric material. Optionally, when porous structure  104  is glued to support element  102 , wherein the support element  102  is a drug eluting stent, the same polymer as used for the elution of the drug is used for attachment of porous structure  104  to support element  102 . 
         [0142]    In an embodiment of the invention, porous structure  104  is attached to support element  102  at a plurality of points. Optionally, the plurality of points defines a pattern, such as a line or zigzag of points. Optionally, porous structure  104  compresses onto support element  102  to maintain an attachment to support element  102 . Optionally, the porous structure is held in place on support element at least partially by frictional forces. Optionally, porous structure  104  is sewn and/or mechanically entangled onto support element  102 . Optionally, heating, pressure, laser welding, UV curing and/or ultrasound are used as techniques to secure porous structure  104  to support element  102 . Optionally, a primer, such as parylene, is used on support element  102  prior to adhering porous structure  104  to it in order to enhance cohesion. 
         [0143]    In some exemplary embodiments of the invention, elastic and/or expandable o- and/or c-rings are used to hold porous structure  104  on support element  102 . Optionally, c-rings are used to avoid hampering expandability of porous structure  104 . Optionally, the rings are used to at least temporarily secure and/or apply friction to each end of porous structure  104  to support element  102 . Optionally, the rings are coated and/or embedded with pharmaceuticals for elution, such as described herein. Optionally, the rings are constructed of a polymer based material. In some exemplary embodiments of the invention, porous structure  104  is tied to support element  102 , optionally using fibers of porous structure  104 . In an exemplary embodiment of the invention, a slip ring  2102  is used to secure porous structure  104  to support element  102 , as shown in  FIGS. 21A  and B. Slip ring  2102  is adapted to expand with porous structure  104  and support element  102  when they are expanded upon deployment at a lumen treatment site. Optionally, slip ring  2102  is flexible but is rigid enough to secure porous structure  104  to support element  102 . In an embodiment of the invention, slip ring  2102  is coiled around enhanced stent apparatus  100  when it is in a reduced profile configuration such that slip ring  2102  overlaps itself at least partially. Upon deployment, shown in  FIG. 21B , support element  102  and porous structure  104  are expanded to provide treatment to the lumen. In an embodiment of the invention, slip ring  2102  expands with them while maintaining sufficient pressure on porous structure  104  to retain it to support element  102 . In an embodiment of the invention, the overlapping portion of slip ring  2102  is reduced as a result of the overall increase in diameter of the slip ring  2102 . Optionally, slip ring  2102  is comprised of a biodegradable and/or bioresorbable material. In some embodiments of the invention, slip ring  2102  is under 25 microns thick. Optionally, slip ring  2102  is under 15 microns thick. Optionally, slip ring  2102  is under 10 microns thick. 
         [0144]    Referring to  FIG. 16 , an embodiment of the invention is shown in which porous structure  104  is attached to support element  102  using a sliding connection  1602 . In an exemplary embodiment of the invention, the sliding connection is established by attaching at least one loop  1604  of porous structure  104  to support element  102  in a condition that prevents the two from becoming separated, but is loose enough to allow sliding of porous structure  104  with respect to support element  102 . In an embodiment of the invention, a loose stitch is used to attach porous structure  104  to support element  102  in a sliding connection. In an embodiment of the invention, expansion of porous structure  104  is assisted by utilizing the sliding nature of the connection  1602 . For example, porous structure  104  is secured to the outermost strut  1606  of support element  102  at its most outlying position  1608 . In an embodiment of the invention, on the other side of support element  102  porous structure  104  is also attached to the outermost strut at its most outlying position. When support element  102  and porous structure  104  are expanded during deployment, porous structure  104  is afforded additional expendability, in relation to a pre-expanded configuration, as the sliding connection  1602  moves from the most outlying position  1608  on outermost strut  1606  to an innermost position  1610 . The distance  1612 , about 1 mm to 6 mm in an embodiment of the invention, from the most outlying position  1608  to innermost position  1610  provides additional expandability to porous structure  104 . Optionally, sliding is prevented by securing porous structure  104  to strut  1606  at innermost position  1610  as well as most outlying position  1608 . Optionally, sliding is prevented by tightening the connection between the two, for example by providing a tighter stitch. 
         [0145]    In some embodiments of the invention, porous structure  104  is tied to support element  102  using any one of thumb, square, reef, or double surgeon&#39;s knots. Optionally, the at least one fiber used to construct porous structure  104  is used to tie porous structure  104  to support element  102 .  FIG. 17  shows an exemplary method for attaching porous structure  104  to support element  102  using knotting. It can be seen that a knotting fiber  1702  is used to secure porous structure  104  to support element  102  at various points along a support element strut  1704 . Optionally, knotting fiber  1702  is threaded through a plurality of eyes  1706  and over support element strut  1704  wherein a knot  1708  is tied to secure porous structure  104  to support element  102  at least some of the eyes. 
         [0146]    As mentioned above, in some embodiments of the invention, securing porous structure  104  to support element  102  is also used to reduce the likelihood of run outs and/or porous structure unraveling. In an embodiment of the invention, run outs and/or porous structure unraveling are to be avoided for at least the reasons of: avoiding porous structure protrusion into the lumen and/or rendering porous structure ineffective for intended treatment of the lumen. In an embodiment of the invention, porous structure  104  is secured to support element  102  at the ends of support element  102 , at least some intersections where porous structure  104  and support element  102  overlap, or both and/or every eye at both ends. Any of the methodologies of securing described above are optionally used to secure porous structure  104  to support element  102  to prevent run outs and/or unraveling. 
         [0147]    In an exemplary embodiment of the invention, porous structure  104  is treated to supply temporary enhanced adhesion to support element  102  during implantation. 
         [0148]    For example, enhanced stent apparatus  100  is optionally dipped in a liquid which causes porous structure  104  to adhere to support element  102 . Optionally, this adherence is due to surface tension of the liquid. Optionally, this adherence is due to temporary shrinkage of porous structure  104 , which secures it to support element  102  more tightly. In some exemplary embodiments of the invention, temporary cohesion is used to prevent porous structure  104  from slipping off of support element  102  as a result of frictional stress experienced during navigation of the vasculature during implantation. 
       General Pharmacological Usage 
       [0149]    Alternatively or additionally to the physical prevention of debris from entering the bloodstream, porous structure  104  optionally contains pharmaceuticals designed to treat a variety of ailments. In some exemplary embodiments of the invention, pharmaceuticals are optionally provided including one or more pharmacological agents for encouraging cell and/or liposomal growth and/or other endothelial cell growth factors, anti-proliferative, anti-thrombotic, anti-coagulant and/or anti-platelet effects, tissue engineering factors, immunomodulators, antioxidants, antisense oligonucleotides, collagen inhibitors, hydrophobic pharmaceuticals, hydrophilic pharmaceuticals and/or endothelial cell seeding substances. Optionally, pharmacological therapy rendered from a porous structure is used to accelerate vein to artery conversion. Specific examples of pharmaceuticals that are optionally used with porous structure  104  include: anti-proliferative agents like sirolimus, zolimus or zotarolimus (ABT-578®), paclitaxel and other taxanes, tacrolimus, everolimus, vincritine, viblastine, HMG-CoA reductase inhibitors, doxorubicin, colchicine, actinomycin D, mitomycin C, cycloporine, and/or mycophenolic acid, triazolopyrimidine and its derivatives (i.e. Trapidil®, a coronary vasodilating drug); intrapide, glucocorticoids like dexamethasone, methylprednisolone, and/or gamma interferon; antithrombotics like heparin, heparin-like dextran derivatives, acid citrate dextrose, coumadin, warfarin, streptokinase, anistreplase, tissue plasminogen activator (tPA), urokinase and/or abciximab; antioxidants like probucol; growth factor inhibitors like tranilast and/or angiopeptin; antisense oligonucleotides like c-myc and/or c-myb; collagen inhibitors like halofuginone and/or batimistat; liposomes; gemcitabine (i.e. Gemzar®); steroids and corticosteroids for example cortisone and prednisone; cortisone, prednisone; sirolimus (Rapamycin®); statin drugs like lovastatin and/or simvastatin (i.e. Zocor®); VEGF; FGF-2; micro carriers containing endothelial cells; genes; DNA; endothelial cell seeds; and/or hydrogels containing endothelial cells. 
         [0150]    Typically, stents (i.e. support elements) which provide pharmaceutical treatment only have the pharmaceutical embedded on the structure of the stent, in particular on the stent struts. This structure is typically minimized in order to provide flexibility and reduce cost, among other reasons. As a result of a minimized support element structure, the struts of the structure are usually spaced widely apart. Thus, when the stent is in situ, and pharmaceuticals are released into the patient from the stent, the pharmaceutical is only diffused from the widely spaced struts. This prevents even distribution of the pharmaceutical over the entire length of the stent. In addition, stent struts are typically large in relation to endothelial cells and therefore formation of a covering endothelial cell layer typically takes on the order of days or weeks, rendering pharmaceutical elution into body tissues delayed and/or ineffective (due to a number of reasons, including the pharmaceutical being washed away by fluids flowing in the lumen before the endothelial cell layer covers the stent). 
         [0151]    In contrast, usage of a pharmaceutical enhanced porous structure, such as described herein, to cover the stent, including the struts, provides far more surface area in contact with the inner wall of the patient&#39;s blood vessel, thereby enabling more diffusion to take place. In comparison to conventional techniques for stent delivered pharmaceuticals, lower concentrations of pharmaceutical are optionally used with the present invention because of its improved therapy-rendering surface area. In an embodiment of the invention, improved delivery by the presently described invention allows for lower doses of pharmaceutical to be used in order to render the same relative amount of treatment, and reduce the overall dosage needed in order to obtain the same results, thus reducing possible side effects. For example, a currently recommended concentration of taxol on a drug eluting stent is around 1 μg/mm 2  of stent surface. In contrast, a concentration of 0.5 μg/mm 2  is optionally used with porous structure  104 , due to its increased treatment rendering surface area. Optionally, the concentration is less than 0.5 μg/mm 2 . As another example, typical concentrations of rapamycin and Timus drugs today are around 140 μg/mm 2 , however, using the herein described porous structure  104  a concentration of 80 μg/mm 2  is optionally used to achieve the same therapeutic effect. In some exemplary embodiments of the invention, as little as 10 μg/mm 2  is optionally, used to achieve the same therapeutic effect. In some exemplary embodiments of the invention, concentrations of pharmaceutical embedded on porous structure are up to 15 times less than conventionally used today. 
         [0152]    In conventional stents, at the struts, the pharmaceutical may not propagate far enough and/or without effect into the vascular wall, or may overdose a particular section of the vascular wall, without sufficient propagation laterally to the rest of the inner surface where it is needed. Having additional surface area more evenly covering the stent surface area, porous structure  104  can deliver drugs in a more locally homogenous way. Optionally, there is an axial profile change in dosage. Since distribution of the drug into the tissue is governed by diffusion, and since the amount of dosage concentration on the struts is limiting due to over toxicity and side effects, spreading the drug in a more even manner is very helpful for obtaining better pharmacokinetics. 
         [0153]    In an exemplary embodiment of the invention, pharmaceuticals to be administered to patient are located in and/or on the fibers of porous structure  104 . Examples of where and how pharmaceuticals are optionally located in and/or on the fibers of porous structure  104  and/or eluted include: 
         [0154]    1. depositing pharmaceutical in the apertures of porous structure; 
         [0155]    2. mixing pharmaceutical particles into fibers of porous structure at fiber creation; 
         [0156]    3. applying pharmaceutical topically to the porous structure, such as by spraying; 
         [0157]    4. dipping porous structure into a solution containing a pharmaceutical additive, thereby depositing the additive on and/or in the fibers of the porous structure; 
         [0158]    5. encapsulating a pharmaceutical additive on porous structure, optionally using a thermal process; 
         [0159]    6. grafting a pharmaceutical additive onto porous structure using plasma treatment; 
         [0160]    7. etching a pharmaceutical additive into porous structure, for example via spattering or coating; 
         [0161]    8. transferring a pharmaceutical additive to porous structure using concentration differences between the porous structure and an additive containing substance, for example by adhering micro carriers containing to pharmaceutical additive to a porous structure allowing their migration into the porous structure; 
         [0162]    9. any method known to those skilled in the art, such as shown in U.S. Pat. App. No. 2004/0030377 to Dubson et al., U.S. Pat. App No. 2005/0187140 to Hunter et al., U.S. Pat. App. No. 2004/0236407 to Fierens et al., U.S. Pat. No. 6,902,522, to Walsh, et al., U.S. Pat. No. 6,669,961 to Kim, et al., U.S. Pat. No. 6,447,796 to Vook et al, U.S. Pat. No. 6,369,039 to Palasis et al., U.S. Pat. No. 6,939,374 to Banik, et al., and U.S. Pat. No. 6,919,100 to Narayanan, the contents of which are incorporated herein by express reference thereto; 
         [0163]    10. elution of the drug from a polymer coming the porous structure fibers; 
         [0164]    11. elution of the drug from the polymer from which the porous structure is constructed; and 
         [0165]    12. incorporating the drug in a biodegradable polymer. 
         [0166]    Optionally, embedding of the pharmaceutical occurs before (e.g. mixing pharmaceutical particles into fibers of porous structure at fiber creation), during (e.g. using the dipping method of  FIG. 19 ) and/or after (e.g. a spray on pharmaceutical after apparatus is made) the manufacture of enhanced stent apparatus  100 . In some exemplary embodiments of the invention, a pharmaceutically embedded porous structure  104  is placed on top of a pharmaceutically treated support element  102 . In some exemplary embodiments of the invention, porous structure  104  is coated with at least a polymer. In some exemplary embodiments of the invention, a porous structure is provided with a polymer coating which contains a pharmaceutical which elutes from the coating. 
         [0167]    Pharmaceuticals are optionally embedded into porous structure  104  such that they are released into the patient over an approximate predetermined amount of time. For example, pharmaceuticals are optionally embedded into porous structure  104  for release over the course of a week. Other pharmaceuticals are optionally embedded into porous structure  104  for release over the course of months. Factors which vary according to the release schedule of the pharmaceutical include the type of material used to construct porous structure  104 , the type of pharmaceutical being used, the manner in which porous structure  104  is constructed, and/or the amount of coverage of support element  102  that porous structure  104  provides. 
         [0168]    In some exemplary embodiments of the invention, 1 microgram of pharmaceutical per square centimeter of fiber surface coverage (not the area of the fiber themselves, but the area of the tissue it treats) area is embedded on the fibers. Optionally, up to 200 micrograms of pharmaceutical per square centimeter of fiber surface area is embedded on the fibers. Optionally, a higher or lower concentration of pharmaceutical is used depending on the therapeutic needs of the patient and depending on the type of drug used. 
         [0000]    Large and/or Complicated Stereochemistry Molecule Pharmaceutical Usage 
         [0169]    In some exemplary embodiments of the invention, usage of porous structure  104  for enhanced pharmaceutical delivery allows for effective dispersion and delivery of large molecule and complex stereochemistry pharmaceuticals. Traditionally, large molecule pharmaceuticals are not used with drug eluting stents because they don&#39;t diffuse very well and the widely spaced struts of traditional stents do not facilitate even and/or widespread diffusion of the large molecule, as described above. In contrast, use of a device with more extensive coverage of a vascular wall would make treatment using large molecule pharmaceuticals more feasible. This is optionally accomplished by providing porous structure  104  and/or support element  102  with large molecule pharmaceuticals for elution and taking advantage of the increased vascular wall coverage of porous structure  104 , due to the smaller aperture sizes in some exemplary embodiments. Alternatively or additionally, due to the overgrowth of porous structure  104  by cells from the body, large molecule pharmaceuticals are more efficiently delivered to the patient as pharmaceuticals are delivered into tissue, rather than being washed away in the blood stream, for example. Optionally, pharmaceuticals larger than 700 Dalton, 1,000 Dalton, 3,000 Dalton or up to 50,000 Dalton are dispersed and delivered evenly into patient&#39;s vasculature. 
         [0170]    Optionally, liposomes are eluted from at least one porous structure  104  and/or support element  102 . Optionally, steroids, statins, anticoagulants, gemcitabine (Gemzar®), zolimus or zotarolimus (ABT-578®), sirolimus (e.g. Rapamycin®), taxol/paclitaxel, and/or other large or complex molecule pharmaceuticals are eluted from at least one porous structure  104  and/or support element  102 . Referring to  FIG. 3 , pharmaceutical agents  406  are shown eluting from enhanced stent apparatus  100  into artery  400  from lumen wall  404 . Optionally, agents  406  elute from porous structure after at least some growth of endothelial cells  408  through enhanced stent apparatus  100 , for example the time determined by experimental endothelial cell growth data. As described elsewhere herein, porous structure  104  optionally acts to trap debris  402  between the exterior surface of enhanced stent apparatus  100  and lumen wall  404 . 
       Timed Release Pharmaceutical Usage 
       [0171]    In an exemplary embodiment of the invention, pharmaceuticals are eluted from an enhanced stent apparatus into overgrown endothelial tissue and not merely into the interior surface of the lumen being treated. In an exemplary embodiment of the invention, pharmaceutical release is thus optimized by ensuring that only a pre-defined amount of drug is lost into the bloodstream and/or into other non-therapeutic media. In some exemplary embodiments, including, for example, in conjunction with BBB treatment as described below, endothelial cell growth can assist with pharmaceutical therapy by providing a transfer medium for the pharmaceutical from an implanted stent to the body area being treated. 
         [0172]    In some exemplary embodiments of the invention, pharmaceuticals are eluted depending on the extent of endothelial tissue growth. Optionally, pharmacological treatment commences after some endothelial cell growth is exhibited through and/or around the enhanced stent apparatus. Optionally, pharmacological treatment begins upon implantation without regard to endothelial cell growth. In some exemplary embodiments of the invention, the enhanced stent apparatus is adapted and constructed to time-release pharmaceuticals in accordance with a predetermined treatment schedule. Optionally, the predetermined treatment schedule accommodates anticipated and/or actual endothelial cell growth rates by utilizing a coating with a predetermined breakdown rate. Optionally, release of pharmaceuticals is determined by time in situ. For example, if it is estimated that it would take 8 hours for endothelial cell growth to completely encapsulate the implanted stent, pharmaceuticals located in the porous structure of the stent optionally have a predetermined 8 hour delay prior to release and/or elute at a low rate to prevent inefficient or undesirable (i.e. toxic overdose) use of the pharmaceutical. In an embodiment of the invention, it takes only few hours for the endothelial cells to cover the thin porous structure, therefore the time release delay is adapted to match. This may be achieved by coating porous structure  104  with a “diffusion barrier” layer that to inhibits the diffusion of drug for a predefined period. Optionally this may be achieved by using a controlled degradable matrix. Optionally, pharmaceutical release occurs after only partial growth of endothelial cells around and/or through porous structure and/or stent. Optionally, pharmaceuticals begin to elute immediately upon insertion and/or implantation into a body lumen. Optionally, it is sufficient for pharmaceutical therapy that porous structure  104  has any biological covering, such as mucus, etc. In some embodiments of the invention, delay is determined according to the material that is expected to overgrow porous structure  104 . 
         [0173]    In an exemplary embodiment of the invention, timed release of pharmaceuticals is accomplished by coating and/or constructing porous structure  104  and/or support element  102  of multiple biodegradable/resorbable layers. By using layers which offer different performance characteristics (e.g. different pharmaceutical, different degradation time, stickiness to the body lumen, surface treatment modifications (e.g. treatment to make it non-sticky to the lumen)), enhanced stent apparatus  100  can be tailored to perform a specific treatment schedule. For example, layer #1 (the external layer) is comprised of a material which degrades in 2 hours, layer #2 (an inner layer) includes a pharmaceutical for elution into the patient and which degrades in 10 hours minutes, layer #3 (an inner layer) includes a different pharmaceutical for elution into the patient which degrades in 6 hours, and so on. Naturally, depending on the therapy desired for the patient, the layers and/or performance characteristics of those layers are changed to provide the desired treatment. It should be noted that a biodegradable layer can be placed in the outermost position which is timed to the expected endothelial cell growth, as described above. In such an embodiment, the degradation of the outermost layer is completed at approximately the same time as the completion of the endothelial cell layer overgrowth of enhanced stent apparatus  100 , enabling a pharmaceutical to be eluted directly into endothelial tissue from a second layer of enhanced stent apparatus  100 . 
         [0174]    In an exemplary embodiment of the invention, support element  102  elutes pharmaceuticals, but treatment is assisted by porous structure  104  which encourages endothelial cell growth over support element  102 . Optionally, the pharmaceutical located on support element  102  elutes slowly to allow for endothelial cell growth. In some embodiments of the invention, the rate of elution depends on the local concentration and the anticipated diffusion rate of the pharmaceutical through the surrounding body tissue. 
         [0175]    In some embodiment of the invention, a first pharmaceutical agent is eluted, which is designed to encourage endothelial cell overgrowth, followed by a second pharmaceutical agent designed to treat a malady of the patient. 
         [0176]    In some embodiments of the invention, at least porous structure  104  is attached to the lumen using an adhesive which is impermeable to the pharmaceutical in porous structure  104 . However, timed release is achieved by allowing the endothelial layer to overgrow porous structure  104 , such that the pharmaceutical will elute into the endothelial layer that is not proximal to the adhesive. Optionally, the adhesive is biodegradable and/or bioresorbable and merely delays elution. 
       Blood Brain Barrier (BBB) Therapy 
       [0177]    The BBB is the specialized system of capillary endothelial cells that protects the brain from harmful substances in the blood stream, while supplying the brain with the required nutrients for proper function. Unlike peripheral capillaries that allow relatively free exchange of substance across/between cells, the BBB strictly limits transport into the brain through both physical (tight junctions) and metabolic (enzyme) barriers. Thus the BBB is often the rate-limiting factor in determining permeation of therapeutic drugs into the brain. 
         [0178]    In some exemplary embodiments of the invention, a pharmaceutical eluting porous structure is used to enable treatments through the BBB. As described herein, pharmaceutical therapy is often enhanced by endothelial cell growth through and/or around an implanted drug eluting stent. Use of porous structure  104  in brain arteries, allows the endothelium cells to grow over the porous structure  104 , thus embedding porous structure  104  into the arterial tissue. The end result, after the previous endothelial cell layer has been absorbed by the body is that porous structure  104 , which contains a brain treating pharmaceutical, is on the other side of the endothelium layer, thus on the other side of the BBB, with no significant impediment between porous structure  104  and the brain tissue. In addition, some exemplary embodiments of porous structure  104  are suitably sized to be used in the narrow lumens found in the brain. Exemplary pharmaceuticals suitable for use with porous structure  104  in treating through the BBB include gemcitabine (Gemzar®), and enzastamin, dopamine and dopamine derivatives, and anti-cancer drugs. In some embodiments of the invention, porous structure  104  elutes anti-BBB materials for lowering resistance to transmission of substances through the BBB. 
       Pharmaceutical Treatment of Small Lumens 
       [0179]    Currently, small lumens such as small coronary or brain arteries are treated only with a balloon type catheter. These treatments are short term and do not lend themselves to rendering pharmaceutical treatment to the lumen, as is sometimes desired. Traditional stenting is not often performed at the very least due to the difficulty of navigating a stent into the small spaces of these arteries. In an exemplary embodiment of the invention, lumens smaller than 2 mm in diameter are treated with pharmaceuticals using at least a pharmaceutical eluting porous structure  104 , and optionally a support element. Optionally, the support element is a stent. Optionally, the support element is a balloon on which porous structure  104  is placed. In an exemplary embodiment of the invention, a balloon-type catheter is used to insert porous structure  104  in a small lumen. The balloon is expanded to cause porous structure  104  expansion and to instigate contact between porous structure  104  and the lumen wall to be treated. In an embodiment of the invention, porous structure  104  at least partially adheres to the lumen wall. Optionally, a biocompatible adhesive is used to adhere porous structure  104  to the lumen wall. In some embodiments of the invention, porous structure  104  is self-expandable and does not need, or only partially relies on the balloon for expansion. In an embodiment of the invention, the balloon is removed once porous structure has been deployed within the small lumen. 
         [0180]    In some embodiments of the invention, small lumens are treated long term, which is not performed currently. For example, by implanting at least the porous structure of an enhanced stent apparatus  100 , treatment can last on the order of months (e.g. a month or more). Optionally, treatment can last on the order of weeks (e.g. a week or more). 
       Exemplary Treatment Methods 
       [0181]    In an exemplary embodiment of the invention, enhanced stent apparatus  100  is used for treating, dilating, drugging and/or supporting body lumens, such as blood vessels. In some exemplary embodiments of the invention, enhanced stent apparatus  100  is used for treatment of disorders in the carotid arteries. In some embodiments of the invention, enhanced stent apparatus  100  is used for treatment of disorders in the coronary arteries. As described above, treatment can be rendered through the BBB. Stent apparatus  100  can be either a balloon expandable stent or a self-expandable stent, or use any other expansion method. Optionally, support element  102  and/or porous structure  104  are self-expandable. Optionally, pharmaceuticals are used to treat a patient via body lumens, for example, as described herein. In some embodiments of the invention, enhanced stent apparatus  100  is used for treatment of aneurisms (described below), for example in the brain. In some embodiments of the invention, enhanced stent apparatus  100  is used for preventative treatment of vulnerable plaque. 
         [0182]    In operation, enhanced stent apparatus  100  is navigated to the area in a body lumen  400 , as shown in  FIG. 3 , where the enhanced stent apparatus  100  is to be emplaced, using techniques known in the art. In some exemplary embodiments of the invention, enhanced stent apparatus  100  can be expanded within body lumen  400  using a balloon. Optionally, enhanced stent apparatus  100  can be expanded within body lumen  400  using self-expandable techniques known in the art. Optionally, support element  102  and/or porous structure  104  are constructed of a thermo-sensitive, shape memory alloy which, when exposed to a patient&#39;s natural body temperature, assumes an expanded shape within body lumen  400  at some time after situation in the appropriate location to render treatment. Alternatively, super-elastic or elastic release is used for placing a stent in a treatment area. In some exemplary embodiments of the invention, a balloon is used to pre-dilate body lumen  400  at a treatment area prior to implantation of enhanced stent apparatus  100  at that area, in a at least a two step (1. pro-dilate, 2. implant apparatus  100 ) procedure. Optionally, only porous structure  104  is implanted and not the whole enhanced stent apparatus  100 . In some exemplary embodiments of the invention, a balloon is used to post-dilate body lumen  400  at a treatment area after implantation of enhanced stent apparatus  100  at that area, in an at least a two step (1. implant apparatus  100 , 2. post-dilate) procedure. This kind of procedure is commonly used when implant apparatus  100  is a self-expandable stent, such as for carotid applications. 
         [0183]    In some exemplary embodiments of the invention, the porous structure mesh is filled with a material which improves the stiffness of the porous structure temporarily until it arrives at a treatment site in a lumen. In some embodiments of the invention, the material is dissolved by naturally occurring substances in the body, such as enzymes. Optionally, the dissolving is timed to the anticipated overgrowth of porous structure  104  by the endothelial cell layer. Optionally the material is fibrogane. Optionally, the material is albumin fibrogane helonic acid laminin. 
         [0000]    Exemplary Treatment of Embolic Showers at Insertion and/or Deployment 
         [0184]    It is commonplace in stenting procedures to use an embolic shower protection device which is situated only during the stenting procedure downstream from the treatment area, the idea being that the protection device will trap debris which falls from the blood vessel walls during the stenting procedure. In an exemplary embodiment of the invention, usage of enhanced stent apparatus  100  with porous structure  104  obviates the need for an embolic shower protection device. The small aperture size of porous structure  104  is designed to trap arterial wall plaque  402  and other debris of a particular size that becomes dislodged during and/or after the stenting procedure, between porous structure  104  and the lumen wall  404 . In an exemplary embodiment of the invention, debris greater than the size of the apertures in diameter is prevented from entering the bloodstream in this manner. 
         [0185]    An additional advantage of using implanted porous structure  104  instead of a conventional embolic shower protection device is that it remains in place after the procedure. That is, debris which becomes dislodged at some time after the stenting is performed still becomes trapped by porous structure  104 . This is an improvement over the embolic shower protection device conventionally used, which is removed at the conclusion of the stenting procedure. Optionally, enhanced stent apparatus  100  is used with an embolic shower protection device as reassurance during the stenting procedure. Optionally, porous structure  104  filters a particular type or types of debris while support element  102  filters another type or types. 
         [0186]    It should be noted further that in an exemplary embodiment of the invention the aperture sizes of the porous structure  104  are designed and constructed to permit the passage of blood therethrough. This prevents the “jailing” of branching blood vessels which prevents the passage of critical blood components, such as red blood cells from passing into the branching vessel. In an exemplary embodiment of the invention, the aperture size of porous structure  104  is larger than the average size of a red blood cell, or about 7 microns, allowing throughput of red blood cells without the risk of producing significant hemolysis. In some exemplary embodiments of the invention, the approximate aperture diameters are greater than 20 microns. In some exemplary embodiments of the invention, the approximate aperture diameters are smaller than 100 microns thus allowing blood to flow through while holding large debris (&gt;100 microns) in place. 
         [0187]    Carotid stenting is rarely performed currently, due to the high risk of debris becoming dislodged during the stenting procedure. This dislodged debris then travels to the brain where it often causes serious injury to the patient. In order to combat this problem of dislodged debris, enhanced stent apparatus  100 , which includes porous structure  104 , is used fir stenting in the carotid arteries in some exemplary embodiments of the invention. 
       Exemplary Treatment of Aneurisms 
       [0188]    Referring to  FIG. 20A , a typical aneurism volume  2002  is depicted promulgating from a body lumen  2004 .  FIG. 20B  shows a current method of treating an aneurism called coil embolization. Coil embolization is particularly indicated for treatment of cerebral aneurisms. Coil embolization of cerebral aneurisms involves the insertion of a catheter through the groin with a small microcatheter navigated to the aneurism itself through the cerebral arteries. A coil  2006  is then deployed into the aneurism filling it from within and thus disturbing the blood flow in the aneurism volume. This effect that leads to the creation of blood clot, which is trapped in aneurism volume  2002  and which eventually turns into a more solid structure, thus reducing the risk of rupture of the aneurism. In some treatments, a stent  2008  is also used in order to keep coil  2006  from falling out of aneurism volume  2002  and into the blood stream. However, in some cases parts of coil  2006  protrude through stent  2008  and are therefore exposed to the blood flow within the lumen  2004 . Additionally, safe insertion of coil  2006  into aneurism volume  2002  can be a complicated procedure. Additionally, the blood clot produced might grow through the stent struts into the blood vessel lumen, narrowing it possibly to the point of complete occlusion. 
         [0189]    Referring to  FIG. 20C , an embodiment of the invention is shown in which porous structure  104  located on enhanced stent apparatus  100  is used to treat an aneurism while preventing coil  2006  from protruding into lumen  2004 . Optionally, a cerebral aneurism is treated by this method. Porous structure  104  is adapted to have aperture sizes which are small enough to prevent coil  2006  from protruding into lumen  2004 , in accordance with an embodiment of the invention. Optionally, a to plurality of porous structures are used at least slightly out of phase in order to prevent at least a portion of coil  2006  from protruding into lumen  2004 . In some exemplary embodiments of the invention, coil  2006  is covered with a porous structure (separate from porous structure  104 ), thereby creating more surface area for the blood to stick to, enhancing the creation of a blood clot within the aneurism volume  2002 . In some embodiments of the invention, porous structure  104  is manufactured using an electrospinning technique. 
         [0190]    In an exemplary embodiment of the invention, enhanced stent apparatus  100  is used to treat an aneurism without the need for coil  2006 . In some embodiments of the invention, porous structure  104  is adapted to restrict blood flow into aneurism volume  2002 , thus causing the trapped blood in aneurism volume  2002  to clot, which in time will solidity and create a solid tissue structure thus reducing the likelihood of aneurism rupture or expansion as a result of increased blood flow thereto. For example, the aperture sizes in porous structure  104  may be small or spaced widely apart. Optionally, a plurality of “out of phase” porous structures are used together to restrict blood flow into aneurism volume  2002 . Optionally, porous structure  104  has apertures smaller than 20 microns. Eliminating the need of coil  2006  is advantageous, as it makes the procedure faster, safer, and simplifies the delivery catheter that can be used to perform the procedure. 
         [0191]    In some exemplary embodiments of the invention, porous structure  104  is shorter than support element  102 . A shorter porous structure  104  is optionally used so that only the aneurism is treated and not a healthy portion of the lumen. Optionally, a shorter porous structure  104  is used to avoid restricting blood flow to a branching vessel. Optionally, porous structure  104  has small aperture sizes on the aneurism side for restricting flow therethrough, while the other side has larger apertures to avoid restricting blood flow to a branching vessel. 
         [0192]    In some exemplary embodiments of the invention, porous structure  104  is comprised of a self-expending material, such as nitinol, having enough radial force to hold itself in place within the lumen. Optionally, a support element  102  is not used at all and porous structure  104  provides the necessary treatment to the aneurism. Optionally, the radial pressure applied by porous structure  104  is equivalent to about 1 atmosphere. Optionally, the aperture diameters for aneurism treatments are smaller than 30 microns. 
         [0193]    In some embodiments of the invention, porous structure  104  also prevents blood clots and/or other embolism-causing debris from entering the lumen  2004  from aneurism volume  2002 . 
       Exemplary Treatment of Vulnerable Plaque 
       [0194]    Identification of vulnerable plaque areas allows prophylactic treatment of these areas before they can create problems for the patient. In an embodiment of the invention, an enhanced stent apparatus  100  is used to preemptively treat lumen areas expected to trigger problematic conditions for the patient in the future. For example, plaque often builds up in blood vessels which in some cases breaks off in a dump or partially tears, causing a thrombosis. The downstream movement of the plaque or thrombosis is a potential cause of a heart attack, stroke or other malady in the patient. In some embodiments of the invention, an enhanced stent apparatus, including at least porous structure  104  is implanted at a potentially problematic location within a lumen, preventing the plaque from rupturing and, thus, from entering the bloodstream. In some embodiments of the invention, porous structure  104  elutes at least one pharmaceutical used for treating the condition affecting the lumen, such as those described herein. In some embodiments of the invention, porous structure  104  is made of nitinol as a self-expandable stent, having enough radial force to hold itself in place, without the supportive element  102 . 
       Exemplary Method of Implantation 
       [0195]    In some exemplary embodiments of the invention, porous structure  104  is positioned on a catheter, such as an expandable balloon, for implantation in a lumen separately from or without support element  102 . Treatment with a catheter is optionally provided by using the catheter to implant porous structure  104  adapted and constructed for rendering treatment to a lumen over time. Optionally, pharmaceuticals or other therapeutic agents are embedded within porous structure  104 , such as described herein. Positioning, in an exemplary embodiment of the invention, entails inserting the catheter at least partially through the interior of porous structure  104  along central axis  106 . In some embodiments of the invention, a balloon is deflated prior to positioning of porous structure  104  thereon. Optionally, the balloon is at least partially inflated prior to positioning of porous structure  104  thereon and then deflated and/or folded prior to insertion into the patient. 
         [0196]    During delivery of porous structure  104  to a treatment site within a lumen, a balance is optionally struck between securing porous structure  104  to the catheter during delivery, but not so securely as to prevent implantation of porous structure  104  at the treatment site, and allowing deflation of a balloon and/or pulling the catheter out while leaving the porous structure  104  inside the lumen intact. For example, porous structure  104  is optionally adhered to catheter at selected points using an adhesive such as loctite instant adhesive number 40340, 40840, 46040 or 3411-UV curable. The adhesive is strong enough to prevent porous structure  104  from slipping off the catheter during delivery, however upon self-expansion or expansion of balloon the bonds between porous structure  104  and the catheter are broken, allowing for implantation of porous structure  104  at a treatment site within a lumen. In some embodiments of the invention, delivery lasts for 6 hours or less. Optionally, delivery lasts for 3 hours or less. Optionally, delivery lasts for 1 hour or less. 
         [0197]    In some exemplary embodiments of the invention, the catheter is treated with an anti-sticking agent such as Parylene-c, silicon coating and/or Teflon® (PTFE) coating, to help prevent porous structure  104  from staying fastened to catheter after deployment at treatment site. Optionally, a thin film is coated onto the catheter which secures porous structure  104  to the catheter during the delivery, but dissolves upon an approximate lapsing of time, allowing porous structure  104  to be removed from the catheter. Optionally, the thin film is comprised of albumin fibrogane helonic acid laminin. Optionally, the thin film layer is up to a few microns thick. Alternatively, the thin film layer is 0.1 microns in thickness. 
         [0198]    In some exemplary embodiments of the invention, the mesh-like structure of porous structure  104  is filled and/or encapsulated with a gel type material, such as fibrogane, fibrinogen and/or hyaluronic acid and/or laminin. The gel material stiffens porous structure  104  for delivery, however, upon extended exposure to intra-lumen conditions, the gel dissolves leaving only porous structure  104  after some period of time, for example a few hours or days. 
         [0199]    In an embodiment of the invention, an adhesive material which is sensitive to a certain threshold (e.g. 1 atm. up to 20 atm.) of pressure is placed on porous structure  104  such that when the balloon pressures porous structure  104  against the lumen, porous structure  104  adheres to the lumen. In an exemplary embodiment of the invention, when porous structure  104  is coated with the pressure sensitive adhesive it is only coated on the lumen side of porous structure  104 . Optionally, porous structure  104  is covered with a selectively adhesive material which has a high affinity for adhering to body tissue, for example fibrin sealant, biological glue, collagen, hydrogel, hydrocolloid, or collagen algirate, but limited affinity for adhesion to other substances, such as a delivery catheter or balloon. 
         [0200]    Upon arrival at a lumen treatment site, the balloon is expanded in order to place porous structure  104 , in accordance with an exemplary embodiment of the invention. As described above, porous structure  104  is optionally placed on the balloon such that when the balloon is expanded, porous structure  104  is expanded correspondingly. In some exemplary embodiments of the invention, the balloon is expanded until it begins to apply pressure to the internal surface of the lumen being treated. The amount of pressure exerted by the balloon is variable depending on the purpose and technique used to carry out the treatment. In some exemplary embodiments of the invention, the balloon is expanded to press porous structure  104  against an interior surface of the lumen being treated. Optionally, the expansion pressure is used to overcome a stenosis being treated. Optionally, porous structure  104  is at least temporarily fastened to the interior surface of the lumen with the assistance of an adhesive. In some exemplary embodiments of the invention, porous structure  104  is at least temporarily attached using at least one barb or pin located on an exterior surface of porous structure  104  facing the inside surface of the blood vessel. Optionally, the adhesive is applied to the exterior surfaces of porous structure  104  prior to insertion into the lumen. In some exemplary embodiments of the invention, once porous structure  104  is placed at the treatment site within the lumen, a support element  102  is implanted at the same site interior of porous structure  104  in relation to the interior surface of the lumen, thus sandwiching porous structure  104  between support element  102  and the lumen. 
         [0201]    In some exemplary embodiments of the invention, porous structure  104  provides mechanical support to a blood vessel wall. Optionally, porous structure  104  support is in addition to support rendered by support element  102 . Alternatively, porous structure support  104  is in lieu of support rendered by support element  102 . In some exemplary embodiments of the invention, support element  102  provides no or minimal support to the blood vessel wall while supporting porous structure  104 . Optionally, porous structure  104  provides pharmacological treatment to blood vessel while providing no or minimal support to blood vessel. Optionally, porous structure  104  is implanted along with support element  102 , however support element  102  degrades in situ, leaving porous structure  104 . Optionally, porous structure  104  prevents support structure  102  from falling apart in large pieces, permitting release of piece of support structure  102  only when below a certain threshold size, for example under 20 microns in diameter. Optionally, porous structure  104  is implanted along with support element  102 , however porous structure  102  degrades in situ, leaving support element  102 . This last configuration is sometimes indicated when porous structure  104  is made of a polymer containing a pharmaceutical. Eliminating the polymer and the pharmaceutical after period of time has an advantage because it reduces the likelihood of long term side effects such as thrombosis associated with the presence of the polymer and the pharmaceutical. 
         [0202]    Stent assemblies, with or without jackets, are used in opening vessel lumens in a variety of vascular tissue including, inter alia, stenotic coronary arteries, stenotic carotid arteries and stenotic organ vasculature. 
       Prior Art Stent and Jacket Configurations 
       [0203]    Referring to  FIG. 24   a , a stent assembly  100  comprises a stand-alone tubular stent  202 , without a jacket, herein bare stent  202 . Bare stent  202  typically comprises a metal or polymer tubular structure having large, mesh-like, apertures  270 . Bare stent  202  is shown encircling a balloon  260  and, upon expansion of balloon  260 , bare stent  202  expands radially outward. 
         [0204]    As seen in  FIG. 24   b , bare stent  202  has expanded radially in vessel lumen  125  to press against a stenotic area of tissue  240 , thereby compressing and cracking stenotic area  240  radially outward. Following deployment of stent assembly  100 , vessel lumen  125  expands, allowing better circulation through lumen  125 . 
         [0205]    Deployment of bare stent  202 , however, causes damage to a basalamina intimal layer  127  resulting in the formation of scars  242 , plaques  244  and new stenotic lesions  240  that protrude through apertures  270 . Over the long-term, a large percentage of the recipients of bare stents  202  will develop significant stenotic lesions  240  that block vessel lumen  125 , causing what is known as restenosis. 
         [0206]    To prevent restenosis, ( FIG. 24   c ) stent assemblies  200  have been developed comprising stents  202  with an internal or external jacket  204  having small apertures. Stent assembly  200  is shown in position around a spindle holder  180 , emerging from a compression sheath  182 , with stent  202  and stent jacket  204  in substantial tubular alignment. Typically, the jacket is formed of a polymer. 
         [0207]    During expansion, jacket  204  prevents embolitic debris  121  generated from plaques along basalamina intimal layer  127  from entering vessel lumen  125 . 
         [0208]    In  FIG. 24   d , stent assembly  200  is expanded radially in vessel lumen  125  so that jacket  204  presses stenotic tissue  240  radially outward. Following deployment of the stent assembly  200 , stent jacket substantially prevents scars  242 , plaques  244  and stenotic lesions  240  from protruding through apertures  270 . In spite of substantially preventing restenosis, stent jacket  204  creates its own set of problems related to formation of an embolism  300 . 
         [0209]    As noted above, to provide sufficient strength, stent jacket  204  may be made of interlacing knitted fibers, and/or fibers subject to chemical or heat treatments, all of which tend to increase the thickness of fibers  210  and bulk of jacket  204 , seen in  FIG. 25 . 
         [0210]    Within 48 hours following implantation of stent assembly  200  a layer of endothelial cells  220  coat stent jacket fibers  210  and basalamina intimal layer  127 , as seen in  FIG. 25 . 
         [0211]    Endothelial cells  220  have a diameter  222  of approximately 20 micrometers and maintain adherence to basalamina intimal layer  127  but generally do not substantially adhere to jacket fibers  210 . 
         [0212]    Fibers  210  in stent jacket typically have a thickness  212  of 20 micrometers so that endothelial cell  220  that straddles fiber  210 , will have no attachment to basalamina intimal layer  127  and will easily dislodge from fiber  210 . 
         [0213]    Additionally, fibers  210  are typically spaced a distance  218  of less than 20 micrometers so that endothelial cell  220  that straddles between two fibers  210 , will attach to the two adjacent fibers  210  and will have a marginal attachment to basalamina intimal layer  127  therebetween; again resulting in a cell  220  that is easily dislodged from fibers  210 . 
         [0214]    Single endothelial cells  220  that become detached from basalamina intimal layer  127 , are not large enough to be recognized by platelets as foreign bodies around which to aggregate. However, as seen in  FIG. 26 , during natural movement of fibers  210 , for example during regular pulsation of blood in circulation, a release of multiple interconnected cells  220  occurs. 
         [0215]    In this case four endothelial cells  220 , have broken loose from basalamina intimal layer  127 , and are freely floating in vessel lumen. A platelet  310 , having a diameter  320  of between four to ten times the diameter of endothelial cells  220 , is attracted to masses that comprise at least two endothelia cells  220  and endothelial cells  220  provide an excellent attractive target for platelet  310 . 
         [0216]    As seen in  FIG. 27 , a single platelet  310  has adhered to dislodged endothelial cells  220 . As seen in  FIG. 28 , as a result of chemotaxis, additional platelets  310  have aggregated around endothelial cells  220  to form an embolism  300 . 
         [0217]    As noted above, embolism  300 , comprising aggregated platelets  310 , presents a health threat that can form at any time following implantation of stent jacket  204  causing an estimated 2% of all recipients of jacketed stents  204  to eventually develop necrosis of vital organs and/or die. 
         [0218]    The tremendous and constant threat of emboli  300  from stent-and-jacket assembly  204  ( FIG. 26 ) has resulted in lifetime administration of platelet aggregation reduction APIs. There are many life-threatening sequelae associated with Clopidogrel and there are many clinical trials being conducted on alternative platelet aggregation reducing APIs, including: Ticlopidine. Cangrelor, ARMYDA-2, and Prasugrel. 
         [0219]    (Journal of Interventional Cardiology “TCT Annual Meeting: Antiplatelet Agents”; Volume 19 Page 193-April 2006.) 
         [0220]    As noted above, lifetime administration of platelet aggregation reducing APIs, herein Clopidogrel, present problems to many sectors of the population. 
         [0221]    For example, many jacketed stent recipients develop reactions that require cessation of Clopidogrel, such reactions include: ulcers, skin rashes, and syncope. With high bulk jacketed stents, Cessation of Clopidogrel puts the patient at risk for developing a life threatening embolus  300 . 
         [0222]    In addition to the hazards of embolus  300 , there are patients who, not only must cease taking Clopidogrel and its accompanying risks, but may also develop conditions that are life threatening of themselves, including myelotoxicity, acquired hemophilia and TTP. 
         [0223]    Additionally, there are the conditions that the patient may have that prevent the administration of Clopidogrel, including unresponsiveness to a platelet aggregate reducing API, an antithrombin deficiency, hereditary antithrombin deficiency (HD), immune depression, low CCR5 Delta 32 homozygous genotype (CCR5), acquired hemophilia, AIDS, HIV. 
         [0224]    Moreover, there are risks presented to virtually every person receiving a jacketed stent. To prevent excessive bleeding in conjunction with virtually any surgery, Clopidogrel administration must be ceased for a significant period of time both pre-operatively and post-operatively. As a result, a patient who has received a stent and is a candidate for an elective surgery, for example prostate removal, is presented with a Hobson&#39;s choice of ceasing Clopidogrel administration and risking death from emboli, or taking Clopidogrel and risking embolism-free bleeding, hemorrhage and death. 
       Optimized Stent Assemblies 
       [0225]    It has been found that specific configurations of the above-noted stents and jackets appear to provide advantages as is explained in the “Experimental Data” section. The specific features of these configurations will now be addressed. 
         [0226]    Single fiber knits have been used in pantyhose since 1939, and comprise a plurality of interconnected loops known for strength, elastic qualities and thinness. Single fiber knit fabrics would be desirable as low bulk jackets  600  were it not from the problem that any loop along the edge of the nylon material can flip 180 degrees and form a run. 
         [0227]      FIG. 29  shows a knitted stent jacket  600  comprising knitted fibers  620  forming apertures  110 . To prevent flipping in fibers  620 , an elastomeric belt  640  has been passed through apertures  110  at the distal end of stent jacket  600 . Optionally, an elastomeric belt  640  is similarly passed through loops at the proximal end of stent jacket  600  (not shown). 
         [0228]    As used herein, any reference to a “knitted material” includes any material that is manufactured by a knitting process, including, inter alia: a material knitted from a single fiber, comprising either monofilament or multifilament fiber. The single fiber may comprise, inter alia, polyethylene, polyvinyl chloride, polyurethane, nylon, stainless steel, nitinol, or any other metal. 
         [0229]    The biostable polymer comprises, inter alia, any one of a polyolefin, a polyurethane, a fluorinated polyolefin, a chlorinated polyolefin, a polyamide, an acrylate polymer, an acrylamide polymer, a vinyl polymer, a polyacetal, a polycarbonate, a polyether, an aromatic polyester, a polyether (ether keto), a polysulfone, a silicone rubber, a thermoset, and a polyester (ester imide). 
         [0230]    The natural polymer comprises, inter alia, a polyolefin, a polyurethane, a Mylar, a silicone, a polyester and a fluorinated polyolefin. 
         [0231]    As seen in  FIG. 30 , knitted stent jacket  104  includes apertures  110  that are maximized so that fibers  620  provide a small total coverage area in which stent jacket  104  covers a stent  102 . 
         [0232]    In accordance with some embodiments of the present invention, in an expanded state, the area of aperture  110  is between about 50,000 square micrometers and about 70,000 square micrometers. In alternative embodiments, aperture  110  has an area of between about 40,000 square micrometers and about 60,000 square micrometers. In other embodiments, aperture  110  has an area of between about 30,000 square micrometers and about 50.000 square micrometers. 
         [0233]    With knitted stent jacket  104  having fibers  620  presenting a small total coverage, crimping stent  102  for insertion into compression sheath,  182  ( FIG. 24   c ) for example, is relatively simple. 
         [0234]    Additionally, a small total coverage allows crimped stent  102  to have a small profile, allowing easy maneuverability through lumen  125 . 
         [0235]    Moreover, with knitted stent jacket  104  having minimal thickness of fibers  620 , stent jacket  104  substantially has a minimal influence on the mechanical properties of the stent during the delivery and expansion. 
         [0236]    The location of jacket  104  externally on stent  102  protects basalamina intimal layer  127  from damage during expansion of stent  102 . Additionally, the location of jacket  104  externally on stent  102  provides substantial protection against debris  121 , seen in  FIG. 24   d , entering vessel lumen  125  during expansion of stent  102 . 
         [0237]    In accordance with some embodiments of the present invention, a proximal portion of jacket  104  is attached to a proximal aspect of stent  102  using a process selected from the group consisting of: sewing, adhesion, gluing, folding, suturing, riveting and welding. Such an attachment, for example, allows stent  102  to expand with a typically different coefficient of expansion than that of jacket  104  without causing damage to basalamina intimal layer  127 . 
         [0238]    As seen in a plan view of knitted stent jacket  600  in  FIG. 30 , knitted stent jacket  104  comprises a small coverage area noted in Appendix 1, for example about 9%, or about 10%, or about 11%, or about 12% of the surface area of associated self-expanding stent  102 . In general, the coverage area is less than 16%. Hence, in spite of crimping stent  102  prior to deployment, there is no need to fold knitted jacket  104  to fit into sheath  182  ( FIG. 24   c ) prior to deployment; thereby reducing bulk and increasing maneuverability of stent assembly  200 . 
         [0239]    Chart 1 the attached Appendix provides support that the above-noted parameters of a knitted jacket on a self-expanding stent can be easily attained in the present invention using a fiber diameter of about 12.5 micrometers. 
         [0240]      FIG. 31  shows details of knitted jacket  600  in which apertures  110  have a longitudinal length  650  of greater than about 160 micrometers. In other embodiments, longitudinal length  650  is greater than about 180 micrometers. In other embodiments, longitudinal length  650  is greater than about 200 micrometers. 
         [0241]    In accordance with some embodiments of the present invention, apertures  110  have a transverse length  642  of greater than about 250 micrometers. In other embodiments, transverse length  642  is greater than about 240 micrometers. In other embodiments, transverse length  642  is greater than about 230 micrometers. 
         [0242]    It will be appreciated that the shorter one of the longitudinal length  650  and the transverse length  642  defines the minimum center dimension  630  (D) which must be greater than about 230 micrometers, and preferably, greater than 240 micrometers, and still more preferably, greater than 250 micrometers. 
         [0243]      FIG. 32  shows that fibers  620  have a diameter  662 , optionally in a range of between about 7 micrometers and about 18 micrometers. In other embodiments, diameter  662  is in a range of between about 10 micrometers and about 15 micrometers. In still other embodiments, diameter  662  is in a range of between about 11 micrometers and about 14 micrometers. In still other embodiments, diameter  662  is in a range of between about 12 micrometers and about 13 micrometers. In still other embodiments, diameter  662  is in a range of between about 12.25 micrometers and about 12.75 micrometers. In still other embodiments, diameter  662  of about 12.5 micrometers. 
         [0244]    Substantially inherent advantages of the measurements of knitted jacket  600  become readily apparent in  FIG. 33  in which endothelial cells  220  are well adhered and stable against basalamina intimal layer  127  due to the thinness of fibers  620 . 
         [0245]    As a result of such spacing, a typical endothelial cell  220  will have substantial contact with basalamina intimal layer  127  as endothelial cell  220  is prevented from adhering to more than one column of fibers  620  due to the distance therebetween. 
         [0246]    A group of three endothelial cells  220  is seen adhering to a portion of knitted stent jacket  600 . Endothelial cells  220  have an amoeba-like movement so that at a fiber junction  692 , cell  220  will typically touch down on junction  692  and move until a substantial portion of cell  220  is in substantial contact with basalamina intimal layer  127 . In rare cases where a cell  228  fails to properly anchor into basalamina intimal layer  127 , that specific single cell  228 , alone, may have a tendency to dislodge due to movement of fibers  620  during normal pulsation in the blood circulation cycle. Due to the stability of adjacent cells  220  resulting from substantial contact with basalamina intimal layer  127 , multiple cells  220  will not dislodge together with single cell  228 . 
         [0247]    As shown, single endothelial cell  228  has separated from basalamina intimal layer  127 . However, single cell  228  does not have the necessary mass to be recognized by platelet  310  as a body worthy of adherence. As a result, there is no formation of the above-noted life-threatening embolism  300  associated with aggregation of platelets  310 . 
         [0248]    Typically, to ensure stability of endothelial cells  220 , a patient receiving stent jacket  100  will be given a platelet aggregation reducing API, for example Clopidogrel, for no more than six months, and possibly less. For example, the patient may receive Clopidogrel for no more than for five months, no more than for four months, no more than for three months, no more than for two months, or no more than for one month. 
         [0249]    At times, the patient receiving stent jacket  100  will not be given a platelet aggregation reducing API, the unique property of the fiber diameter, as illustrated in  FIG. 32 , and the advantage of the aperture minimum center dimension D, alone or in combination, relieving the need for the platelet aggregation reducing API, altogether. Thus, if the patient is scheduled to undergo elective surgery during the six-month administration, Clopidogrel may be discontinued without substantial fear of platelet aggregation. 
         [0250]    Further, if, during a six-month administration period, the recipient of stent jacket  600  has any reaction, including ulcers, skin rashes, syncope, myelotoxicity, and TTP, Clopidogrel may be immediately ceased without substantial fear of embolism generation. 
         [0251]    Further, Clopidogrel administration may be ceased or not initiated in the face of patient unresponsiveness to Clopidogrel, an antithrombin deficiency, HD, immune depression, low CCR5, acquired hemophilia, AIDS, and HIV. 
       Experimental Data 
       [0252]    Reference is now made to the chart below showing experimental data, which together with the above description, illustrate the invention in a non-limiting fashion. 
         [0253]    Optimization of jacket stent fiber thickness and apeture square area reduces the need for an anti coagulation agent, for example Clopidogrel. 
         [0254]    Maintaining small total coverage areas provides several additional advantages: 
         [0255]    1. crimping the stent for insertion is relatively simple; 
         [0256]    2. profile of the crimped stent is small; 
         [0257]    3. stent jacket substantially has a minimal influence on the mechanical to properties of the stent during the delivery and expansion; and 
         [0258]    4. jacket does not require folding during crimping when the coverage area of the stent is about 9%, or about 10%, or about 11%, or about 12% in self-expanding stent. In general the coverage area is less than 16%. 
         [0259]    The chart below provides support that the above-noted parameters of jacket coverage on a stent can be easily attained in the present invention using a fiber diameter of about 12.5 micrometers. 
         [0000]    
       
         
               
               
               
               
               
             
               
               
               
               
               
               
               
             
               
               
               
               
               
               
               
             
           
               
                 TABLE-US-00002 
               
             
             
               
                   
               
               
                 Stent 
                 Fiber 
                 Head 
                 Apertures Size 
                 Covered 
               
             
          
           
               
                 Size 
                 size 
                 Needle 
                 Aperture 
                 Transverse 
                 Longitudinal 
                 area 
               
               
                 [mm] 
                 [μ] 
                 No. 
                 No. 
                 [μ] 
                 [μ] 
                 [%] 
               
               
                   
               
             
          
           
               
                 2.5 
                 12.5 
                 22 
                 44 
                 166 
                 291 
                 11% 
               
               
                 2.75 
                 12.5 
                 22 
                 44 
                 184 
                 291 
                 10% 
               
               
                 3 
                 12.5 
                 22 
                 44 
                 202 
                 291 
                 10% 
               
               
                 3.5 
                 12.5 
                 22 
                 44 
                 237 
                 291 
                 9% 
               
               
                 4 
                 12.5 
                 35 
                 70 
                 167 
                 291 
                 11% 
               
               
                 4.5 
                 12.5 
                 35 
                 70 
                 189 
                 291 
                 10% 
               
               
                 5 
                 12.5 
                 35 
                 70 
                 212 
                 291 
                 9&amp; 
               
               
                 5.5 
                 12.5 
                 35 
                 70 
                 234 
                 291 
                 9% 
               
               
                   
               
             
          
         
       
     
         [0260]    It is understood that the phraseology and terminology employed herein is for descriptive purpose and should not be regarded as limiting. 
         [0261]    Unless otherwise defined, all technical and scientific terms used herein have the same meaning as commonly understood by one of ordinary skill in the art to which the invention belongs. In addition, the descriptions, materials, methods, and examples are illustrative only and not intended to be limiting. Methods and materials similar or equivalent to those described herein can be used in the practice or testing of the present invention. 
         [0262]    As used herein, the terms “comprising” and “including” or grammatical variants thereof are to be taken as specifying the stated features, integers, steps or components but do not preclude the addition of one or more additional features, integers, steps, components or groups thereof. This tam encompasses the terms “consisting of” and “consisting essentially of”. 
         [0263]    As used herein, “a” or “an” mean “at least one” or “one or more”. The use of the phrase “one or more herein does not alter this intended meaning of a” or “an”. 
         [0264]    It is expected that during the life of this patent many relevant stent jacket materials will be developed and the scope of the term stent jacket is intended to include all such new technologies a priori. 
         [0265]    As used herein the term “about” refers to ±10%. 
         [0266]    Additional objects, advantages, and novel features of the present invention will become apparent to one ordinarily skilled in the art upon examination of the following examples, which are not intended to be limiting. Additionally, each of the various embodiments and aspects of the present invention as delineated hereinabove and as claimed in the claims section below finds experimental support in the following examples. 
         [0267]    It is appreciated that certain features of the invention, which are, for clarity, described in the context of separate embodiments, may also be provided in combination in a single embodiment. Conversely, various features of the invention, which are, for brevity, described in the context of a single embodiment, may also be provided separately or in any suitable subcombination. 
         [0268]    Although the invention has been described in conjunction with specific embodiments thereof, it is evident that many alternatives, modifications and variations will be apparent to those skilled in the art. Accordingly, it is intended to embrace all such alternatives, modifications and variations that fall within the spirit and broad scope of the appended claims. All publications, patents and patent applications mentioned in this specification are herein incorporated in their entirety by reference into the specification, to the same extent as if each individual publication, patent or patent application was specifically and individually indicated to be incorporated herein by reference. In addition, citation or identification of any reference in this application shall not be construed as an admission that such reference is available as prior art to the present invention.