Abstract:
A process for forming a DRAM stacked capacitor structure with increased surface area, has been developed. The process features forming lateral grooves in the sides of a polysilicon storage node structure, during a dry etching procedure used to define the storage node structure. The grooves are selectively, and laterally formed in ion implanted veins, which in turn had been placed at various depths in an intrinsic polysilicon layer via a series of ion implantation steps, each performed at a specific implant energy. An isotopic component of the storage node structure, defining dry etch procedure, selectively etches the highly doped, ion implanted veins at a greater rate than the non-ion implanted regions of polysificon, located between the ion implanted veins, resulting in a necked profile, storage node structure, featuring increased surface area as a result of the formation of the lateral grooves.

Description:
This is a Continuation of patent application Ser. No. 10/054,561, filling date Jan. 22, 2002, now U.S. Pat. No. 6,706,591, Method of Forming a Stacked Capacitor Structure with Increased Surface Area for a Dram Device, assigned to the same assignee as the present invention. 

   BACKGROUND OF THE INVENTION 
   (1) Field of the Invention 
   The present invention relates to methods used to fabricate semiconductor devices, and more specifically to a method used to form a stacked capacitor structure, with increased surface area, for a dynamic random access memory (DRAM) device. 
   (2) Description of Prior Art 
   Micro-miniaturization, or the ability to fabricate semiconductor devices using sub-micron features, have allowed the performance of these semiconductor devices to be improved while still decreasing the processing cost of a specific sub-micron device. Dimension reduction, realized via the use of sub-micron features, has resulted in decreases in performance degrading parasitic capacitances. In addition the use of sub-micron features have resulted in a greater number of smaller semiconductor chips attainable from a specific size starting substrate, with device densities of the smaller semiconductor chips still equal to or greater than counterpart larger semiconductor chips fabricated using larger dimensions, thus allowing the processing cost for a specific semiconductor chip to be reduced. However in the area of DRAM technology, the decreasing size of the transfer gate transistor limits the horizontal dimension of an overlying DRAM capacitor structure. To continually increase device performance capacitance increases, or increases in the surface area of the capacitor structure, have to be achieved, however without increasing the horizontal dimension of the capacitor structure. The increased surface area for DRAM stacked capacitor structures, are usually achieved via unique geometric configurations such as crown, cylindrical or fin shaped structures in which additional vertical features are formed as part of the stacked capacitor structure. However to achieve these unique configurations rigorous and complex process sequences are needed, adding additional process cost. 
   This invention will teach a method of forming a stacked capacitor structure, offering increased surface area, however without forming the complex vertical and protruding horizontal features comprised in the crown, cylindrical or fin type structure. This invention will feature a “necked” profile for a capacitor structure, comprised with necked regions, or lateral grooves located in, and extending from, the sides of capacitor storage node structure. The necked capacitor profile, obtained via multiple ion implantation procedures into, and conventional dry etching of, a storage node structure, can result in a capacitor structure exhibiting a surface area of about 3 times greater than a surface area achieved with flat surfaces. Prior art, such as Forbes et al, in U.S. Pat. No. 6,025,225, describe a method of roughening the surface of a trench capacitor structure, while Jun in U.S. Pat. No. 5,691,221, describe a method of forming a fin type, stacked capacitor structure. However neither of these prior arts describe a process for forming the novel, capacitor structure, featuring the necked profile, now described in this present invention. 
   SUMMARY OF THE INVENTION 
   It is an object of this invention to fabricate a DRAM device, on a semiconductor substrate. 
   It is another object of this invention to form a DRAM stacked capacitor structure, featuring a storage node structure with a necked profile, employed to increase the capacitor surface area. 
   It is still another object of this invention to form the necked profile, for the DRAM capacitor structure, via multiple ion implantation procedures, performed at various energies, placing groups of implanted ions at specific depths in a polysilicon storage node structure, followed by a dry etch procedure which laterally removes the implanted regions at a greater rate than the non-implanted regions of the storage node structure, resulting in the desired grooves, or the necked profile, for the polysilicon storage node structure of the DRAM capacitor device. 
   In accordance with the present invention a method of fabricating a DRAM capacitor structure, comprised with a storage node structure featuring a necked profile, used for surface area increases, is described. After formation of an underlying transfer gate transistor, a storage node plug structure is formed in an insulator layer, overlying and contacting a portion of a top surface of the transfer gate transistor source/drain region. An intrinsic polysilicon layer is deposited on the top surface of the insulator layer, overlying and contacting the top surface of the storage node plug structure. A series of ion implantation procedures is performed at multiple implant energies, placing layers of implanted ions in specific regions of the intrinsic polysilicon layer, with intrinsic, or non-implanted regions of polysilicon located between the implanted regions. A dry etch procedure is used to vertically define the polysilicon storage node structure, with the dry etch procedure also laterally, and selectively removing portions of the implanted regions located at the outside surface of the defined storage node structure, resulting in the necked profile storage node structure. After deposition of a capacitor dielectric layer on the necked profile, storage node structure, an upper electrode is formed resulting in a DRAM capacitor structure featuring increased surface area as a result of formation of the storage node structure with the necked profile. 

   
     BRIEF DESCRIPTION OF THE DRAWINGS 
     The object and other advantages of this invention are best described in the preferred embodiment with reference to the attached drawings that include: 
       FIGS. 1–6 , which schematically, in cross sectional style, describe key stages of fabrication used to fabricate a DRAM capacitor structure, featuring a storage node structure formed with a necked profile, designed to increase capacitor surface area. 
   

   DESCRIPTION OF THE PREFERRED EMBODIMENTS 
   The method of fabricating a DRAM capacitor structure, featuring a storage node structure formed with a necked profile, designed to increase capacitor surface area, will now be described in detail. Semiconductor substrate  1 , comprised of P type, single crystalline silicon, featuring a &lt;100&gt; crystallographic orientation, is used and schematically shown in  FIG. 1 . Silicon dioxide gate insulator layer  2 , is thermally grown to a thickness between about 15 to 100 Angstroms, followed by the formation of silicon nitride capped, polycide gate structure  5 . Polycide layer  3 , is comprised of an overlying metal silicide layer such as tungsten silicide, and an underlying, in situ doped, polysilicon layer  3 . The underlying polysilicon layer is obtained via low pressure chemical vapor deposition (LPCVD), procedures, at a thickness between about 200 to 2000 Angstroms, and doped during deposition via the addition of arsine, or phosphine, to a silane ambient. The overlying tungsten silicide layer is also obtained via LPCVD procedures, at a thickness between about 200 to 2000 Angstroms, using silane and tungsten hexafluoride as reactants. Silicon nitride layer  4 , is then deposited at a thickness between about 100 to 1000 Angstroms, via LPCVD or plasma enhanced chemical vapor deposition (PECVD) procedures. A photoresist shape, not shown in the drawings, is used as an mask to allow an anisotropic, reactive ion etching (RIE) procedure, using Cl 2  as an etchant, to define silicon nitride capped, polycide gate structure  5 , shown schematically in  FIG. 1 . The width of silicon nitride capped, polycide gate structure  5 , is between about 100 to 1000 Angstroms. 
   After removal of the photoresist shape used for definition of the silicon nitride capped, polycide gate structure, via plasma oxygen ashing procedures, insulator spacers  6 , on formed on the sides of silicon nitride capped, polycide gate structure  5 . This is accomplished via deposition of a silicon nitride, or a silicon oxide layer, via LPCVD or PECVD procedures, at a thickness between about 100 to 1500 Angstroms. An anisotropic RIE procedure, using CF 4  as an etchant is next used to form silicon nitride, or silicon oxide spacers on the sides of silicon nitride capped, polycide gate structure  5 . Arsenic or phosphorous ions are next implanted into a region of semiconductor substrate  1 , not covered by silicon nitride capped, polycide gate structure  5 , or by insulator spacers  6 , at an energy between about 2 to 100 KeV, at a dose between about 2E13 to 7E14 atoms/cm 2 . An anneal procedure is next performed using either conventional furnace or rapid thermal anneal procedures, to activate the implanted ions, forming N type source/drain region  7 , shown schematically in  FIG. 1 . Although this invention is described for a N channel device, it can also be applied to a P channel device. 
   Insulator layer  8 , such as silicon oxide, or boro-phosphosilicate glass (BPSG), is next deposited at a thickness between about 3000 to 12000 Angstroms, via LPCVD or PECVD procedures. Planarization of insulator layer  8 , is then accomplished via a chemical mechanical polishing (CMP) procedure, resulting in a smooth top surface topography for insulator layer  8 . Photolithographic and anisotropic RIE procedures, using CHF 3  as an etchant, are used to define openings  20 , and  21 , in insulator layer  8 , each now exposing a top portion of source/drain region  7 . After removal of the photoresist shape used to define openings  20 , and  21 , via plasma oxygen ashing procedures, a polysilicon layer is deposited via LPCVD procedures, at a thickness between about 3000 to 12000 Angstroms, completely filling openings  20 , and  21 . The polysilicon layer is doped in situ during deposition, via the addition of arsine, or phosphine to a silane ambient. Regions of unwanted polysilicon, located on the top surface of insulator layer  8 , are then removed via CMP procedures, or via a selective RIE procedure using Cl 2  or SF 6  as an etchant, defining lower polysilicon storage node plug structure  10 , in opening  21 , and polysilicon bit line plug structure  9 , located in opening  20 . Insulator layer  11 , again comprised of either silicon oxide, or BPSG, is next deposited via LPCVD or PECVD procedures, at a thickness between about 3000 to 12000 Angstroms, followed by photolithographic and anisotropic RIE procedures, using CHF 3  as an etchant, resulting in the definition of opening  22 , exposing a portion of the top surface of lower polysilicon storage node plug structure  10 . After removal of the photoresist shape used to define opening  22 , another N type, in situ doped polysilicon layer is deposited via LPCVD procedures, at a thickness between about 1000 to 7000 Angstroms, completely filling opening  22 . Removal of unwanted portions of the polysilicon layer is next accomplished via CMP or selective RIE procedures, resulting in the formation of upper polysilicon storage node plug structure  12 , located in opening  22 , overlying and contacting a portion of the top surface of lower polysilicon storage node plug structure  10 . The result of these procedures is schematically shown in  FIG. 2 . 
   Intrinsically doped, polysilicon layer  13 , shown schematically in  FIG. 3 , is next deposited via LPCVD procedures, at a thickness between about 3000 to 12000 Angstroms. A critical ion implantation procedure is next employed to form multiple veins of implanted ions, with each specific vein of implanted ions placed at a specific depth in intrinsic polysilicon layer  13 . The veins of implanted ions, labelled  14 , and schematically shown in  FIG. 4 , are achieved via multiple, blanket implantation procedures, using either arsenic or phosphorous ions. The number of specific ion implanted veins, can be between about 3 to 10, with the deepest vein created via implantation at an energy between about 50 to 100 KeV, while the shallowest, or the vein closest to the top surface of polysilicon layer  13 , accomplished at an implantation energy between about 2 to 50 KeV. The veins of implanted ions, located between the deepest and shallowest veins, are obtained at energies between about 30 to 80 KeV. The implant dose for each of implanted veins  14 , is between about 2E13 to 7E17 atoms/cm 2 , while the intrinsic, or non-implanted space between implanted vein region, in polysilicon layer  13 , is between about 100 to 5000 Angstroms. An anneal cycle can now be employed to activate the implanted ions. 
   The formation of storage node structure  23 , featuring a necked profile, is next addressed and schematically shown in  FIG. 5 . Photoresist shape  15 , is formed on the top surface of polysilicon layer  13 , and used as a etch mask to define storage node structure  23 . A critical dry etch procedure, performed at specific conditions, is next employed to etch polysilicon layer  13 , featuring an etch rate for portions of polysilicon comprised with ion implanted veins  14 , greater than the etch rate for intrinsic regions of polysilicon, located between ion implanted veins  14 . The dry etch procedure is performed using an inductive coupled plasma (ICP) procedure and tool, at a power for the top plate of the ICP tool between about 100 to 1000 watts, while a power between about 30 to 300 watts is used for the bottom plate. A pressure between about 4 to 50 mtorr, is employed, using an ambient comprised of Cl 2 , HBr, and He as an etchant. These conditions result in a removal rate of intrinsic polysilicon of between about 600 to 1000 Angstroms/min, while the removal rate of polysilicon comprised with ion implanted veins  14 , is greater, between about 1000 to 2000 Angstroms/min. In addition the dry etch conditions, specifically pressure, allow an isotropic component to be present, which in combination with the higher removal rate of implanted ions veins  14 , result in a greater degree of lateral etching for implanted ion vein region, when compared to the smaller level of lateral etching experienced by the intrinsic polysilicon regions, thus resulting in the formation of lateral grooves  16 , in ion implanted veins  14 . The extent of lateral etching, or the lateral dimension of grooves  16 , is between about 50 to 500 Angstroms, creating the necked profile for storage node structure  23 . The increase in surface area for storage node structure  23 , is between 2 to 4 times greater than counterpart storage node structures formed without notching. 
   The completion of DRAM capacitor structure  19 , featuring storage node structure  23 , with the desired necked profile, is next addressed and schematically shown in  FIG. 6 . After removal of photoresist shape  15 , via plasma oxygen ashing, capacitor dielectric layer  17 , is formed on the necked profile surface of storage node structure  23 . Capacitor dielectric layer  17 , can be a tantalum oxide layer obtained via plasma vapor deposition procedures, at a thickness between about 10 to 500 Angstroms. Capacitor dielectric layer  17 , can also be an oxidized silicon nitride on silicon oxide (ONO) layer, or an oxidized silicon nitride (NO) layer, both at an equivalent silicon oxide thickness between about 10 to 100 Angstroms. A polysilicon layer is next deposited via LPCVD procedures at a thickness between about 50 to 500 Angstroms, doped in situ during deposition via the addition of arsine, or phosphine, to a silane ambient. A photoresist shape, not shown in the drawings, is next used as an etch mask to allow an anisotropic RIE procedure, using Cl 2  or SF 6  as an etchant, to define polysilicon upper electrode shape  18 , completing the fabrication of DRAM capacitor structure  19 , comprised of overlying, polysilicon upper electrode structure  18 , capacitor dielectric layer  17 , and storage node structure  23 , in turn featuring a necked profile needed to increase capacitor surface area. 
   While this invention has been particularly shown and described with reference to the preferred embodiments thereof, it will be understood by those skilled in the art that various changes in form and details may be made without departing from the spirit or scope of the invention.