Abstract:
A method of sealing a generator stator bar and a stator bar end fitting receiving the end including the steps of: brazing the fitting to the end of the stator bar with a braze material; applying a metallic barrier coating material to the end of the stator bar in the fitting; heating the fitting at a temperature at least as hot as a liquidus temperature of the metallic coating material and cooler than a solidus temperature of the braze material; coating the end of the stator bar in the fitting with liquid metallic barrier coating material, and solidifying the liquefied metallic coating material to form a metallic barrier coating on the end of the stator bar in the fitting.

Description:
RELATED APPLICATION 
       [0001]    This application is a divisional of application Ser. No. 10/900,184, filed Jul. 28, 2004, which application is incorporated in its entirety by reference herein. 
     
    
     BACKGROUND OF THE INVENTION 
       [0002]    The present invention relates to seals between generator stator bars and their end fitting connections, and to a method for sealing a stator bar end fitting to prevent or reduce corrosion due to coolant water flowing through the fitting and the stator bar. 
         [0003]    Water-cooled stator bars for electrical generators are comprised of a plurality of small rectangular solid and hollow copper strands brazed to one another to form a bar. The ends of the strands are brazed to an end fitting, typically referred to as stator bar clip. The end fitting serves as both an electrical and a cooling flow connection for the stator bar. 
         [0004]    The hollow end fitting typically includes an enclosed chamber for ingress or egress of stator bar cooling liquid, typically deionized water. At one open end, the end fitting receives the ends of the strands of the stator bar. The fitting and the peripherally outermost copper strands of the stator bar are brazed to one another. The opposite end of the fitting is connected to a stator cooling conduit, e.g., a house. 
         [0005]    Over time, leaks can developed about the connection between the stator bar ends and the stator bar fitting as well as between adjacent strands. It is believed that the leak mechanism is due to a two-part corrosion process which initiates in the braze alloy at the interior surface of the braze joint. Stagnant water in the chamber of the fitting has in the past been in contact with the braze alloy and the copper strands. This coolant contact with the braze joint and cooper strands is believed to cause corrosion and consequent leakage. 
         [0006]    Field repair of coolant leaks through the stator bar end connections has been moderately successful. A leak site is identified by external visual examination of where the strands enter the end fitting. External visual leak detection indirectly identifies the leak site because the visible external leak on the outside of the bar and/or fitting may be a considerable distance away from a point within the fitting where the leak begins. This is particularly true if the leak is occurring between the strands of the stator bar. 
         [0007]    Once a leak is identified by visible inspection, a vacuum is drawn inside the fitting and stator bar. An anaerobic cement is applied externally or reflow the braze material around the suspected leak sites. The vacuum suction draws the cement inwardly towards the leak path. However, it has been found that this cement repair method is not 100% effective in repairing the leak and is therefore considered only a temporary repair. 
         [0008]    As an alternative to applying cement to seal a leak, an epoxy barrier coating has been applied to provide protection against water initiated corrosion mechanisms along the brazed length of the strand package. The epoxy barrier coating technique is disclosed in U.S. Pat. No. 5,605,590. The epoxy barrier coating has been an improvement over earlier corrosion protection techniques. However, the epoxy barrier coating may deteriorate when exposed to extreme temperatures and can be difficult to inspect in certain stator clip designs. 
         [0009]    There is a need for an improved barrier coating for stator bar clips. In particular there is a need for corrosion protection between the stator bars and their clips. The corrosion protection should be robust and be applicable to various stator bar clip designs, including clips for raised hollow strand stator designs. 
       BRIEF DESCRIPTION OF THE INVENTION 
       [0010]    The invention may be embodied as a method of sealing a generator stator bar and a stator bar end fitting receiving the end including the steps of: attaching the fitting to the end of the stator bar with a braze material; applying a metallic barrier coating material to the end of the stator bar in the fitting; heating the fitting at a temperature at least as hot as a liquidus temperature of the metallic coating material and cooler than a solidus temperature of the braze material; coating the end of the stator bar in the fitting with liquid metallic barrier coating material, and solidifying the liquefied metallic coating material to form a metallic barrier coating on the end of the stator bar in the fitting. 
         [0011]    The invention may also be embodied as a method of sealing a stator bar end to a stator bar end fitting, the fitting having a chamber for receiving a liquid through an opening and in communication with hollow strands in said stator bar to enable coolant liquid flow through the hollow strands, said method comprising: brazing the fitting to the end of the stator bar; inserting a metallic barrier coating material into the chamber of the fitting; liquefying the metallic barrier coating material by heating the material to a temperature at least as hot as a liquidus temperature of the coating material; coating the end of the stator bar in the fitting with the liquefied metallic barrier coating material, and solidifying the liquefied metallic barrier coating material to form a barrier over the end of the stator bar in the fitting, wherein said hollow end strands comprise end openings extending through the barrier. 
         [0012]    The invention may also be embodied as a fitting for a stator bar of a generator comprising: a fitting housing having a collar at a first end and a cooling fluid coupling at an opposite end, wherein said collar is configured to be brazed to an end of the stator bar; a chamber extending from the first end to the opposite end of the fitting, and a metallic barrier coating on an end of the stator bar in said chamber and forming a seal between the end and a remaining portion of the chamber, wherein said metallic barrier coating has a liquidus temperature lower than a solidus temperature of a braze material applied to braze the stator bar to the fitting. 
     
    
     
       BRIEF DESCRIPTION OF THE DRAWINGS 
         [0013]      FIG. 1  is a schematic illustration of a liquid-cooled stator winding arrangement illustrating the stator bars and end fittings coupled to inlet and outlet coolant headers; 
           [0014]      FIG. 2  is a representative end cross-sectional view of the strands of a stator bar within an end fitting, and 
           [0015]      FIG. 3  is an enlarged cross-sectional view of a stator bar end fitting taken along line  3 - 3  in  FIG. 2 .  FIG. 3  illustrates a barrier coating that has been applied to the end of the bar within the fitting such that hollow strands of the bar extend through the coating, and that the coating otherwise seals the bar end and braze from the coolant. 
           [0016]      FIG. 4  is an enlarged cross-sectional view of a stator bar end and a fitting, wherein inserts are in the open ends of hollow end strands and the inserts extend through the metallic barrier coating in the fitting. 
       
    
    
     DETAILED DESCRIPTION OF THE INVENTION 
       [0017]      FIG. 1  illustrates a liquid-cooled stator winding arrangement used in a typical liquid-cooled generator. A stator core  10  having stator core flanges  12  and core ribs  14 . Stator bars  16  pass through radially extending slots and terminate at opposite ends in end fittings  18  and  20 . Inlet hoses  22  connect the inlet fitting  18  to an inlet coolant header  24 . Outlet hoses  26  connect the outlet fitting  20  to an outlet coolant header  28 . 
         [0018]      FIG. 2  is an end view of a stator bar and one of the stator bar fittings  18 ,  20 .  FIG. 3  is a cross-sectional side view of the end of the stator bar and its end fitting. Each stator bar includes a plurality of solid and hollow copper strands  30  and  32 , respectively, disposed in side-by-side and superposed relation one to the other along the length of the bar. The strands are brazed to one another. The ends of the strands form the end  31  of the stator bar. The inlet fitting  18  and an outlet fitting  20  are brazed to opposite ends of the stator bar  16 . 
         [0019]    The strands  30 ,  32  are brazed to one another, as well as to the inside walls of the end fitting. The brazing material  44  is for example BCuP-5 and/or BCuP-1. The strands are also brazed to one another within the stator bar. It is believed that the initiation of the leakage paths is caused by stagnant coolant liquid in the sub-chamber  40  of the fitting which corrodes the end of the stator bar. 
         [0020]    The end fittings  18 ,  20  are each formed of an electrically conductive material, such as copper. The fitting (also referred to here as a “stator bar clip”) is hollow and includes a collar  34  that slides over the outer side surfaces of the end  31  of the stator bar  16 . Opposite to the collar, the fitting includes a coupling end  36  that is configured to connect to one of the cooling hoses  22 ,  26 . 
         [0021]    The coupling end  36  of the end fitting is normally connected to and closed by a copper hose tube  22 ,  26  which serves as both an electrical connection and as a hydraulic conduit. Liquid coolant, e.g., deionized water, flows through the tubes  22 ,  26  into or from the internal chamber  38  defined by the fitting  20  and the exposed ends  39  of the hollow copper strands  32 . The liquid in the chamber  38  flows into a first fitting, through the hollow strands  32  and out an opposite fitting. The opposite end fittings  18 ,  20  comprise an inlet fitting or receives the liquid coolant from the hollow strands  32  for egress when the fitting is employed as an outlet fitting. 
         [0022]    Each end fitting  18 ,  20  includes an internal chamber  38  generally coaxial with the fitting and extending the length of the fitting. The chamber  38  includes an expanded sub-chamber  40  adjacent to the end  31  of the stator bar, a necked down section and a second expanded sub-chamber configured to receive an end of a hose. The external and internal shapes of a fitting may vary to suit different stator bar configurations. 
         [0023]    To install an end fitting  18 ,  20  on a stator bar end, the bar ends are solidified and brazed to the collar of the fitting. A conventional high-temperature phosphorous copper braze alloy, e.g., BCuP-1, may be applied to the braze the end of the bar to the fitting when the bar is held horizontally or vertically. A BCuP-5 braze alloy may be applied to the joint between the end fitting and stator bar to seal the fitting to the strand ends. A conventional high temperature phosphorous copper braze material, e.g., BCuP-5, may be used to seal the collar of the clip to the strand ends of the stator bar. 
         [0024]    Typically, a BCuP-5 braze alloy has a solidus temperature of 1190° Fahrenheit-F. (643° Celcius-C.), a liquidus temperature of 1475° F. (802° C.) and a brazing range of 1300° F. to 1500° F. (704° C. to 816° C.). Typically, a BCuP-1 braze alloy has a solidus temperature of 1310° Fahrenheit-F. (710° Celcius-C.), a liquidus temperature of 1688° F. (920° C.) and a brazing range of 1454° F. to 1724° F. (790° C. to 940° C.). A solidus is a temperature below which the braze is solid and a liquidus is a temperature above which the braze is entirely liquid. 
         [0025]    When the bar is brazed to the end fitting, the ends of the solid cooper strands  32  are generally flush with a back wall of the expanded sub-chamber  40 . The ends  39  of the hollow cooper strands extend partially into the sub-chamber  40 . The ends  39  of the hollow cooper strands  32  may extend about 10 to 500 mils beyond the ends of solid strands  30  and into the sub-chamber  40 . 
         [0026]    The end  31  of the stator bar is sealed with a metallic barrier coating  46  to prevent coolant corrosion. The coating is applied after the fitting is brazed to the stator bar and a braze seal is applied to the joint between the fitting and bar. The metallic barrier coating seals the end of the stator bar without blocking the openings  39  to the hollow strands and thereby allows coolant to flow through the fitting and the hollow strands. The coating material  46  forms a barrier across the sub-chamber  40  that prevents the coolant from corroding the end of the stator bar. 
         [0027]    The metallic barrier coating material  46  may be a low-liquidus, corrosion resistant braze alloy or solder material. A tin-silver-copper alloy solder, and in particular Sn/3.8Ag/0.7Cu, is suitable as a coating material. The coating material  46  is selected such that its liquidus temperature is lower than the solidus temperature of the braze alloy(s) used to both braze the copper strands together and to braze the fitting to the end of the stator bar. For example, the liquidus of the coating material may be in a range between 150° C. to 600° C., which is below the 643° C. solidus of a BCuP-5 braze alloy applied to bond the end fitting to the stator bar. The coating material when applied to the fitting and bar end may be in the form of a paste, powder, chips or other small size form. 
         [0028]    After being brazed together, the stator bar fitting and stator bar are oriented vertically. This orientation places the end surface of stator bar and the ends of the strands are horizontal and the coupling end  36  of the fitting is upright. The metallic barrier coating material  46  is initially inserted in a solid or liquid form through the coupling end  36  of the fitting, into the sub-chamber  40  and on the end of the stator bar. The coating material is applied over the solid strands  30  end surfaces and around the ends  31  of the hollow strands  32  to form a coating over the end of the stator bar in the clip. 
         [0029]    A bore scope or other inspection instrument may be inserted into the chamber  40  so that a technician may view the end of the stator bar and the coating material to confirm that the coating material is at the bottom of the sub-chamber  40  and on the stator bar, and that the ends of the hollow strands extend up through the coating. This inspection may be accomplished when the coating material is initially inserted into the fitting and/or after the coating material has been liquefied and solidified on the end of the bar. 
         [0030]    Heating the coating material, end of stator bar and fitting to a temperature above the liquidus temperature of the coating material, e.g., 5 degrees Celsius higher, causes the coating material  46  to liquefy and form a barrier coating over the end surface  31  of the bar in the fitting. Because the stator bar end  31  is horizontal, the liquefied coating material forms a pool over the end of the bar and at the bottom of the sub-chamber  40 . The depth of the pool is less than the height of the ends of the hollow strands, e.g., the coating material pool is less than 10 to 500 mils. The hollow end strands protrude above the surface of the pool of the coating material. When the coating cools, the liquid coating material solidifies as a metallic barrier coating over the end of the stator bar. 
         [0031]    The coating  46  forms a metallic barrier  46  over the end of the stator and within the sub-chamber  40  of the fitting. The coating  46  seals potential leakage paths within the fitting. The coating serves as a seal between the liquid coolant and the cooper strands and brazing alloy applied to the strands. 
         [0032]    While the invention has been described in connection with what is presently considered to be the most practical and preferred embodiment, it is to be understood that the invention is not to be limited to the disclosed embodiment, but on the contrary, is intended to cover various modifications and equivalent arrangements included within the spirit and scope of the appended claims.