Abstract:
A method of producing Nb 3 Sn superconducting wire, including the steps of: preparing a plurality of Sn modules obtained by burying Sn-based metal cores in a Cu-based metal matrix and a plurality of Nb modules obtained by burying Nb-based metal filaments in a Cu-based metal matrix; bundling the Nb modules and the Sn modules such that the Nb modules surround the Sn modules and obtaining an assembly; inserting the assembly in a tubular member of Cu-based metal which internally comprises tube-like shaped Ta-based metal or Nb-based metal which serves as a diffusion barrier and obtaining a composite; drawing the composite; and heat-treating the composite.

Description:
CROSS-REFERENCE TO RELATED APPLICATION  
       [0001]     The disclosure of Japanese Patent Application No. 2004-177763 filed on Jun. 16, 2004 including specification, drawings and claims is incorporated herein by reference in its entirety  
       BACKGROUND OF THE INVENTION  
       [0002]     1. Field of the Invention  
         [0003]     The present invention relates to a method of producing superconducting wire, and more particularly, to method of producing Nb 3 Sn superconducting wire.  
         [0004]     2. Description of the Related Art  
         [0005]     An Nb 3 Sn superconducting wire, for stability, a structure in which a great number of superconducting filaments having a diameter of a few scores of micrometers are buried in a metal matrix of Cu or the like which has a small resistivity. This structure is called a multifilamentary wire.  
         [0006]     According to a conventional method of producing Nb 3 Sn superconducting wire, first, a plurality of Nb/Cu composites (segments) composed of Cu matrix and Nb multifilament, and Sn cores or Sn alloy cores of the same diameter as that of the segments are prepared. Next, the Sn cores or Sn alloy cores are bundled such that they are surrounded by the segments. Then, they are surrounded by an Nb sheet, and they are inserted in a Cu tube. This is followed by drawing to obtain a wire, and then by heat treatment. In consequence, Sn diffuses in the Cu matrix, Nb 3 Sn is created around the Nb filaments inside the segments, and an Nb 3 Sn superconducting wire is obtained as a multifilamentary wire (JP, 09-16731, A).  
       SUMMARY OF THE INVENTION  
       [0007]     However, with this method of producing Nb 3 Sn superconducting wire, the hardness of the segments is remarkably different from that of the Sn cores or Sn alloy cores and the drawing workability is therefore extremely poor. Hence, there is a problem that the wires get broken during drawing and it is thus very difficult to obtain a long wire.  
         [0008]     In light of this, the inventors discovered that when Sn cores or Sn alloy cores were covered and integrated with Cu tubes, the drawing workability improved and it was possible to obtain a long wire, thus completing the present invention.  
         [0009]     In short, an object of the present invention is to provide a method of producing an Nb 3 Sn superconducting wire which has a high critical current density (Jc) characteristic, which is stable and which is particularly suitable as a long wire.  
         [0010]     The present invention is directed to a method of producing Nb 3 Sn superconducting wire, including the steps of: preparing a plurality of Sn modules obtained by burying Sn-based metal cores in a Cu-based metal matrix and a plurality of Nb modules obtained by burying Nb-based metal filaments in a Cu-based metal matrix; bundling the Nb modules and the Sn modules such that the Nb modules surround the Sn modules; inserting the Nb and Sn modules in a tubular Cu-based metal which internally comprises tube-shaped Ta-based metal or Nb-based metal which serves as a diffusion barrier and obtaining a composite; drawing the composite; and heat-treating the composite.  
         [0011]     Use of the method of producing Nb 3 Sn superconducting wire according to the present invention makes it possible to obtain an Nb 3 Sn superconducting wire which has a high critical current density and favorable drawing workability. 
     
    
     BRIEF DESCRIPTION OF THE DRAWINGS  
       [0012]      FIG. 1  is a cross-sectional view of the precursor wire for use in the Nb 3 Sn superconducting wire according to the embodiment 1 of the present invention;  
         [0013]      FIG. 2  is a cross-sectional view of the precursor wire for use in the Nb 3 Sn superconducting wire according to the embodiment 2 of the present invention; and  
         [0014]      FIG. 3  is a cross-sectional view of the Nb module used in the Nb 3 Sn superconducting wire according to the embodiment 2 of the present invention. 
     
    
     DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS  
     Embodiment 1  
       [0015]      FIG. 1  is a cross-sectional view of a precursor wire which is used for producing of an Nb 3 Sn superconducting wire which has a high critical current density according to the embodiment 1 of the present invention, and the precursor wire is generally denoted at  100 . The method of producing Nb 3 Sn superconducting wire will now be described with reference to  FIG. 1 .  
         [0016]     According to the method of producing Nb 3 Sn superconducting wire, first, an Nb rod  1  is prepared whose size is diameter of 31.2 mm×length of 600 mm. Next, a Cu tube  2  containing Sn is prepared whose size is outer diameter of 35.0 mm×inner diameter of 31.5 mm×length of 600 mm, and the Nb rod  1  is inserted in the Cu tube  2 . Following this, this Cu tube  2  is drawn and reduced in diameter until the outer diameter decreases down to 6.1 mm, and further reduced in diameter until the Cu tube becomes hexagonal rod whose length of the opposite side is 5.2 mm. At this step, a Cu/Nb composite rod  3  is obtained whose cross section is approximately hexagonal.  
         [0017]     Next, the Cu/Nb composite rod  3  is cut to 175 mm, and thus obtained  121  rods are bundled and inserted in a Cu container  4  containing Sn whose size is outer diameter of 70 mm×inner diameter of 63.5 mm×length of 185 mm.  
         [0018]     Next, the Cu container  4  is enclosed with caps at its both ends, and the Cu container  4  and the caps are welded using an electron beam in vacuum and accordingly sealed up, and then HIP-processed and integrated as one, whereby a Cu/multi-Nb composite rod is obtained. The Cu/multi-Nb composite rod is subjected to hot extruding and reduced in diameter until the outer diameter decreases down to 25.0 mm, and the periphery of the Cu/multi-Nb composite rod is machined until the outer diameter becomes 24.5 mm. Further, the Cu/multi-Nb composite rod is drawn and reduced in diameter until the outer diameter decreases down to 2.2 mm, further reduced in diameter until the Cu/multi-Nb composite rod becomes a hexagonal rod whose length of the opposite side is 1.85 mm, and cut to 1000 mm. At this step, Nb modules  7  are completed.  
         [0019]     Meanwhile, separately from fabrication of the Nb modules  7 , a Sn rod  5  containing In is prepared whose size is diameter of 30.7 mm×length of 300 mm and inserted in a Cu tube  6  containing Sn whose size is outer diameter of 35 mm×inner diameter of 31 mm×length of 300 mm. After the Sn rod is drawn and reduced in diameter until the outer diameter decreases down to 2.2 mm, the Sn rod is further reduced in diameter until the Sn rod becomes a hexagonal rod whose length of the opposite side is 1.85 mm, and cut to 1000 mm. Sn modules  8  which are Cu/Sn composite rods are thus completed.  
         [0020]     Next, as shown in  FIG. 1 , eighty-four Nb modules  7  and thirty-seven Sn modules  8  are arranged and bundled, except for those at the outermost periphery, in such a manner that the outer Sn modules  8  are surrounded by the Nb modules  7  as shown in  FIG. 1 . Following this, a Ta tube  9  is prepared whose size is outer diameter of 24.5 mm×inner diameter of 24 mm×length of 1000 mm, and the bundle of the Nb modules  7  and the Sn modules  8  is inserted in the Ta tube  9 .  
         [0021]     Further, a Cu tube  10  is prepared whose size is outer diameter of 34 mm×inner diameter of 26 mm×length of 1000 mm, and the Ta tube  9  is inserted in the Cu tube  10 . At this step, a precursor wire  100  whose cross section is as shown in  FIG. 1  is formed.  
         [0022]     Next, the precursor wire  100  is drawn until the outer diameter decreases down to 0.7 mm. The workability at the drawing step is extremely good and wire having the length of 1800 m without any breakage is obtained. This is because the Sn modules  8  are the Cu/Sn composite rods which are obtained by inserting the soft Sn rod  5  in the Cu tube  6  and the hardness balance of the precursor wire  100  accordingly improves.  
         [0023]     This wire is heat-treated at last, whereby an Nb 3 Sn superconducting wire is obtained. In this example, measurement samples are cut out from drawn wire, then heat-treated in an inert gas atmosphere at 650° C. for ten days, and made as the Nb 3 Sn superconducting wire. At this step, the Nb 3 Sn superconducting wire having a high critical current density is completed.  
         [0024]     The critical current of obtained superconducting wire was measured at the temperature of liquid helium (4.2 K) in a magnetic field of 12 T and found to be 430 A. The critical current density in non stabilized-copper area (non-Cu Jc) was 2200 A/mm 2 .  
         [0025]     From these results, it is clarified that use of the producing method according to this embodiment makes it possible to obtain an Nb 3 Sn superconducting wire which has a high critical current density and favorable drawing workability which can not be obtained with the conventional methods.  
         [0026]     In the case of the precursor wire  100  according to the embodiment 1, a Sn volume ratio of Sn cores in the Sn modules  8  is 78.1%, a Nb volume ratio of Nb filaments in the Nb modules  7  is 67.7%, and a ratio of the number of the Sn modules  8  to the number of the Nb modules  7  is 1:2.27. Even if the diameters and the lengths of the Nb modules  7  and the Sn modules  8  in the precursor wire  100  are changed, and even if the outer diameters, inner diameters and the lengths of the Ta tube  9  and the Cu tube  10  in the precursor wire  100  are changed, and even if the final diameters and the lengths of the precursor wire  100  are changed, the ratio of Nb volume in the Nb modules  7  is stayed within the range from 50% to 75%, or more preferably, the range from 55% to 70%. In the same manner, the Sn volume ratio in the Sn modules  8  is stayed within the range from 70% to 90%, or more preferably, the range from 75% to 85%.  
         [0027]     As for the ratio of the number of the Sn modules  8  to the number of the Nb modules  7 , when the number of the Sn modules  8  is 1, the number of the Nb modules  7  is from 1.9 to 2.5, and more preferably, from 1.95 to 2.35.  
         [0028]     In the precursor wire  100  having such a structure, Nb in the Nb modules  7  (Nb filaments) and Sn in the Sn modules  8  (Sn cores) are buried in separate Cu matrices and structured as separate modules, and therefore, the volume fractions of the Nb filaments and the Sn cores in the precursor wire  100  are increased. As a result, Nb Sn superconducting wire with the high Jc properties is able to be obtained, because the Nb 3 Sn reacted with a high concentration Sn and Nb each other by final heat treatment.  
         [0029]     Further, since the Sn modules are arranged surrounding the Nb modules except for those at the outermost periphery, Sn diffusion gets directed inward in such directions that solid angles become narrow and the Sn modules intercept physical or electromagnetic coupling between the Nb modules. Therefore, the performance of the obtained Nb 3 Sn itself is improved and the Nb 3 Sn superconducting wire with high Jc and high stability is able to be obtained. Consequently, as mentioned above, it is possible to get the Nb 3 Sn superconducting wire with non-Cu Jc exceeding 2000 A/mm 2  at 4.2 K and 12 T.  
         [0030]     In addition, as described above, as the Sn cores are the Sn modules  8  which are buried in the Cu matrix, Cu absorbs the difference in hardness between Nb and Sn and the drawing workability improves. It is therefore possible to easily produce a long length wire.  
         [0031]     However, when the Nb volume ratio in the Nb modules  7  is less than 50% or the Sn volume ratio in the Sn modules  8  is less than 70%, it is not possible to obtain the Nb 3 Sn superconducting wire with such a high current density as that described above, because the amount of Nb 3 Sn generated by heat-treatment is decreased.  
         [0032]     On the contrary, when the Nb volume ratio in the Nb modules  7  is larger than 75% or the Sn volume ratio in the Sn modules  8  is larger than 90%, it is not possible to obtain such a long Nb 3 Sn superconducting wire as that described above, because the drawing workability becomes considerably poor.  
         [0033]     Further, when the ratio of the number of the Sn modules  8  to the number of the Nb modules  7  is that the number of the Nb modules  7  is less than 1.9 relative to the number of the Sn modules  8  of 1, it is not possible to obtain the Nb 3 Sn superconducting wire with such a high current density as that described above, because the amount of Nb 3 Sn generated by heat-treatment is decreased by decreasing the amount of Nb compared with Sn. Conversely, when the ratio of the number of the Sn modules  8  to the number of the Nb modules  7  is that the number of the Nb modules  7  is larger than 2.5 relative to the number of the Sn modules  8  of 1, it is not possible to obtain the Nb 3 Sn superconducting wire with such a high current density as that described above, because the amount of Nb 3 Sn generated by heat-treatment is decreased by decreasing the amount of Sn compared with Nb.  
         [0034]     While the embodiment 1 uses Sn rods whose In dose is 1 wt % as the Sn rods  5  containing In, the In dose is preferably from 0 wt % to 2 wt %, and more preferably, from 0.5 wt % to 1.5 wt %. Since this increases the hardness of the Sn modules and reduces the hardness difference from the Nb modules, it is possible to easily produce a long wire.  
         [0035]     However, when the In dose is more than 2 wt %, it is not possible to obtain the Nb 3 Sn superconducting wire with such a high current density as that realized by the embodiment 1, because the amount of Nb 3 Sn generated by heat-treatment is decreased by decreasing the amount of Sn. When no In is added on the contrary, although the drawing workability somewhat deteriorates, the method of producing the Sn rods becomes simple and a long wire which is approximately similar to that according to the embodiment 1 is obtained.  
         [0036]     Further, while the Sn dose in the Cu tube  2 , the Cu container  4  and the Cu tube  6  is 0.15 wt % in the embodiment 1, the Sn dose is preferably from 0 wt % to 2 wt %, and more preferably, from 0.05 wt % to 0.5 wt %. Since such a structure enhances the hardness of the Sn modules and that of the Nb modules, it is possible to more easily produce a long wire.  
         [0037]     However, when the Sn dose is more than 2 wt %, the drawing workability becomes considerably poor and such long wire as that described above can not be obtained. When no Sn is added on the contrary, although the drawing workability somewhat deteriorates, the method of producing the Cu tubes and the Cu container becomes simple and a long wire which is approximately similar to that according to the embodiment 1 is obtained.  
         [0038]     In addition, although the embodiment 1 uses the Ta tube  9  as a Sn diffusion barrier, a similar effect is attained even using a Ta plate as it is shaped like a tube for instance. Further alternatively, instead of Ta, any Nb-based metal or the like may be used as long as the metal is effective in preventing diffusion of Sn.  
       Embodiment 2  
       [0039]      FIG. 2  is a cross-sectional view of a precursor wire which is used for producing an Nb 3 Sn superconducting wire which has a high critical current density according to the embodiment 2 of the present invention, and the precursor wire is generally denoted at  200 .  FIG. 3  is a cross-sectional view of an Nb module  12  which is used in the precursor wire  200 . In  FIGS. 2 and 3 , the same reference symbols as those used in  FIG. 1  denote the same or corresponding portions.  
         [0040]     The method of producing Nb 3 Sn superconducting wire will now be described with reference to  FIGS. 2 and 3 .  
         [0041]     According to the method of producing Nb 3 Sn superconducting wire, first, as shown in  FIG. 3 , Nb modules  12  are fabricated in which Nb-based metal filaments are arranged in a Cu-based metal matrix.  
         [0042]     To be more specific, a Cu rod containing Sn whose size is diameter of 6.1 mm×length of 3 m is made, and that rod is drawn to a hexagonal rod whose length of the opposite side is 5.2 mm, and cut to 175 mm. In this manner, sixteen Cu rods  11  containing Sn are made. Meanwhile, by a method similar to that according to the embodiment 1, one hundred and five Cu/Sn composite rods  3  are made whose length of the opposite side is 5.2 mm and length is 175 mm.  
         [0043]     Next, as shown in  FIG. 3 , the Cu rods  11  and the Cu/Sn composite rods  3  are bundled such that the Cu rods  11  are lined up in the radius directions which are at 120 degrees with each other. The total number of the Cu rods  11  and the Cu/Sn composite rods  3  is 121.  
         [0044]     Next, these are inserted in the Cu container  4  containing Sn whose size is outer diameter of 70.0 mm×inner diameter of 63.5 mm×length of 185 mm. Following this, the Cu container  4  is enclosed with caps at its both ends, and the container and the caps are welded using an electron beam in vacuum and accordingly sealed up, and then HIP-processed and integrated as one, whereby a Cu/multi-Nb composite rod is obtained.  
         [0045]     By a method similar to that according to the embodiment 1, the Cu/multi-Nb composite rod is then subjected to hot extruding and reduced in diameter until the outer diameter decreases down to 25 mm, and the periphery of the Cu/multi-Nb composite rod is machined until the outer diameter becomes 24.5 mm. Further, the Cu/multi-Nb composite rod is drawn and reduced in diameter down to 2.2 mm, further reduced in diameter until the Cu/multi-Nb composite rod becomes a hexagonal rod whose length of the opposite side is 1.85 mm. This is cut to 1000 mm at last, whereby the Nb modules  12  shown in  FIG. 3  are fabricated.  
         [0046]     Meanwhile, by a method similar to that according to the embodiment 1, the Sn modules  8  whose length of the opposite side is 1.85 mm and length is 1000 mm shown in  FIG. 2  are fabricated.  
         [0047]     Following this, as shown in  FIG. 2 , eighty-four Nb modules  12  and thirty-seven Sn modules  8  are arranged and bundled, except for those at the outermost periphery, in such a manner that the outer Sn modules  8  are surrounded by the Nb modules  12  as shown in  FIG. 2 . Next, the Ta tube  9  is prepared whose size is outer diameter of 24.5 mm×inner diameter of 24.0 mm×length of 1000 mm, and the bundle of the Nb modules  12  and the Sn modules  8  is inserted in the Ta tube  9 .  
         [0048]     Further, the Cu tube  10  is prepared whose size is outer diameter of 34 mm×inner diameter of 26 mm×length of 1000 mm, and the Ta tube  9  is inserted in the Cu tube  10 . At this step, the precursor wire  200  whose cross section is as shown in  FIG. 2  is formed.  
         [0049]     Next, the precursor wire  200  is drawn until the outer diameter decreases down to 0.7 mm. The workability at the drawing step is extremely good and wire material having the length of 1800 m without any breakage is obtained. This is because the Sn modules  8  are the Cu/Sn composite rods which are obtained by inserting the soft Sn rod  5  in the Cu tube  6  and the hardness balance of the precursor wire  200  accordingly improves.  
         [0050]     This wire is heat-treated at last, whereby an Nb 3 Sn superconducting wire is obtained. In this example, measurement samples are cut out from drawn wire, then heat-treated in an inert gas atmosphere at 600° C. for ten days, and made as the Nb 3 Sn superconducting wire. At this step, the Nb 3 Sn superconducting wire having a high critical current density is completed.  
         [0051]     The critical current of obtained superconducting wire was measured at the temperature of liquid helium (4.2 K) in a magnetic field of 12 T and found to be 390 A. The critical current density in non stabilized-copper area (non-Cu Jc) was 2020 A/mm 2 .  
         [0052]     From these results, it is clarified that use of the producing method according to this embodiment makes it possible to obtain an Nb 3 Sn superconducting wire which has a high critical current density and favorable drawing workability which can not be obtained with the conventional methods.  
         [0053]     According to the embodiment 2, as described above, in the Nb module  12 , the area of the plurality of the Cu/multi-Nb composite rods  3  is divided by the Cu rods  11 , which are lined up in the radius directions which are at 120 degrees with each other, into three fan-shaped sections whose central angles are 120 degrees.  
         [0054]     In other words, this is a structure that the area where the Nb filaments are buried in a proportional manner in the Cu matrix (i.e., the Nb filament bundles) is partitioned into the three fan-like sections by the area of the Cu rods  11 .  
         [0055]     By means of this structure, physical or electromagnetic coupling between the Nb filament bundles inside the Nb module  12  is blocked, and an Nb 3 Sn superconducting wire which is highly stable is obtained.  
         [0056]     In the case of the precursor wire  200  according to the embodiment 2, a Sn volume ratio of Sn cores in the Sn modules  8  is 78.1%, a Nb volume ratio of Nb filaments in the Nb modules  12  is 58.8%, and the ratio of the number of the Sn modules  8  to the number of the Nb modules  12  is 1:2.27. Even if the diameters and the lengths of the Nb modules  12  and the Sn modules  8  in the precursor wire  200  are changed, and even if the outer diameters, inner diameters and the lengths of the Ta tube  9  and the Cu tube  10  in the precursor wire  200  are changed, and even if the final diameters and the lengths of the precursor wire  200  are changed, the ratio of Nb volume in the Nb modules  12  is stayed within the range from 50% to 75%, or more preferably, the range from 55% to 70%. In the same manner, the Sn volume ratio in the Sn modules  8  is stayed within the range from 70% to 90%, or more preferably, the range from 75% to 85%.  
         [0057]     As for the ratio of the number of the Sn modules  8  to the number of the Nb modules  12 , when the number of the Sn modules  8  is 1, the number of the Nb modules  12  is from 1.9 to 2.5, and more preferably, from 1.95 to 2.35.  
         [0058]     When the Nb volume ratio in the Nb modules  12  is less than 50% or the Sn volume ratio in the Sn modules  8  is less than 70%, it is not possible to obtain the Nb 3 Sn superconducting wire with such a high current density as that described above, because the amount of Nb 3 Sn generated by heat-treatment is decreased.  
         [0059]     On the contrary, when the Nb volume ratio in the Nb modules  12  is larger than 75% or the Sn volume ratio in the Sn modules  8  is larger than 90%, it is not possible to obtain such a long Nb 3 Sn superconducting wire as that described above, because the drawing workability becomes considerably poor.  
         [0060]     Further, when the ratio of the number of the Sn modules  8  to the number of the Nb modules  12  is that the number of the Nb modules  12  is less than 1.9 relative to the number of the Sn modules  8  of 1, it is not possible to obtain the Nb 3 Sn superconducting wire with such a high current density as that described above, because the amount of Nb 3 Sn generated by heat-treatment is decreased by decreasing the amount of Nb compared with Sn.  
         [0061]     Conversely, when the ratio of the number of the Sn modules  8  to the number of the Nb modules  12  is that the number of the Nb modules  12  is larger than 2.5 relative to the number of the Sn modules  8  of 1, it is not possible to obtain the Nb 3 Sn superconducting wire with such a high current density as that described above, because the amount of Nb 3 Sn generated by heat-treatment is decreased by decreasing the amount of Sn compared with Nb.  
         [0062]     While the area where the Nb filaments are buried in proportional manner in the Cu-based metal matrix is divided into the three fan-shaped sections whose central angles are 120 degrees by the Cu-based metal matrix inside the Nb module  12  according to the embodiment 2, a similar effect is attained even when the number of the divided sections is other than 3 as long as the ratio of Nb volume in the Nb modules  12  is from 50% to 75%, or more preferably, the range from 55% to 70%.  
         [0063]     Further, although the foregoing has described that the Cu rods  11  containing Sn are used as the partitioning material, other metal such as Ta rods for instance may be used instead which can block physical or electromagnetic coupling between the Nb filaments inside the Nb modules. Still further, although the foregoing has described that a plurality of rods are used as the shape of as the partitioning material, other shape such as a plate-like shape may be used instead which is effective in blocking physical or electromagnetic coupling between the Nb filaments inside the Nb modules.  
         [0064]     While Sn rods whose In dose is 1 wt % are used as the Sn rods  5  containing In according to the embodiment 2, similar effect is attained even using Sn-based metal rods whose In dose is preferably from 0 wt % to 2 wt %, and more preferably, from 0.5 wt % to 1.5 wt %.  
         [0065]     However, when the In dose is more than 2 wt %, it is not possible to obtain the Nb 3 Sn superconducting wire with such a high current density as that realized by the embodiment 2, because the amount of Nb 3 Sn generated by heat-treatment is decreased by decreasing the amount of Sn. When no In is added on the contrary, although the drawing workability somewhat deteriorates, the method of producing the Sn rods becomes simple and a long wire which is approximately similar to that according to the embodiment 2 is obtained.  
         [0066]     Although the embodiment 2 uses Cu rods, a Cu tube and Cu container whose Sn dose is 0.15 wt % as the Cu rods  11  containing Sn, the Cu tube  2  containing Sn, the Cu container  4  containing Sn and the Cu tube  6  containing Sn, Cu rods, a Cu tube and a Cu container whose Sn dose is from 0 wt % to 2 wt %, and more preferably, from 0.05 wt % to 0.5 wt % may be used.  
         [0067]     However, when the Sn dose is more than 2 wt %, the drawing workability becomes considerably poor and such a long wire as that described above can not be obtained. When no Sn is added on the contrary, although the drawing workability somewhat deteriorates, the method of producing the Cu rods, the Cu tube and the Cu container becomes simple and a long wire as that described above is obtained.  
         [0068]     Although the embodiment 2 uses the Ta tube  9  as a Sn diffusion barrier, a Ta plate or the like as it is shaped like a tube for instance may be used as the barrier. Further, although Ta is used as the material of the Sn diffusion barrier, other metal such as Nb-based metal may be used instead which is effective in preventing diffusion of Sn.  
         [0069]     In the present invention, Cu-based metal refers to pure Cu or Cu which contains Sn in the amount of 2 wt % or less.  
         [0070]     Nb-based metal refers to pure Nb or Nb which contains at least one of Ta of 10 wt % or less, or Ti of 5 wt % or less.  
         [0071]     Sn-based metal refers to pure Sn or Sn which contains at least one of Ti of 5 wt % or less, or In of 2 wt % or less.