Abstract:
A method for recycling rubber tires includes mixing the rubber tires and a hydrophobic ionic liquid in a vessel. The hydrophobic ionic liquid is heated to an elevated vapor temperature to produce dissolved components from the rubber tires. A precipitate is produced from at least some of the dissolved components.

Description:
RELATED APPLICATION 
       [0001]    This application claims priority from U.S. provisional application 61/562,617, filed Nov. 22, 2011, which is incorporated by reference herein in its entirety. 
     
    
     BACKGROUND 
       [0002]    Disposing of vulcanized polymers represents a significant solid waste problem. Polymers that have been vulcanized have long been deemed as “permanent” or “irreversible”. This is due to the crosslinking of polymer chains, creating a rubber that no longer melts, but instead disintegrating at high temperatures. 
         [0003]    One particular type of vulcanized polymer that presents a significant disposal problem is rubber tires. For instance, according to the California Integrated Waste Management Board Report, people in California wear out roughly 28 million tires per year. Across the country, there are altogether about 240 million old tires which are replaced each year. Commonly employed methods of disposal include incineration and discarding in landfills. Both approaches have significant problems. For instance, the incineration of rubber tires releases large quantities of pollutants, which inevitably increases the problem of air pollution in the region. Discarding of rubber tires in landfills is also problematic because they are not easily degradable, making them less than suitable for disposal in landfills. 
         [0004]    Recently, ionic liquids have been explored for their potential use in recycling vulcanized polymers such as rubber tires. Ionic liquids are known for their nonvolatility and stability at high temperature making them suitable for consideration in a low emission recycling system. 
       SUMMARY 
       [0005]    In accordance with one aspect of the invention, a method is provided for depolymerizing a vulcanized polymer. The method includes contacting the vulcanized polymer with a hydrophobic ionic liquid and heating the hydrophobic ionic liquid to an elevated vapor temperature to produce dissolved components from the vulcanized polymer. The dissolved components from the ionic liquid. 
         [0006]    In accordance with another aspect of the invention, a method for recycling rubber tires includes mixing the rubber tires and a hydrophobic ionic liquid in a vessel. The hydrophobic ionic liquid is heated to an elevated vapor temperature to produce dissolved components from the rubber tires. A precipitate is produced from at least some of the dissolved components. 
     
    
     
       BRIEF DESCRIPTION OF THE DRAWINGS 
         [0007]      FIG. 1  is a flowchart showing one example of a method recycling rubber tires. 
       
    
    
     DETAILED DESCRIPTION 
       [0008]    It has been found that certain ionic liquids can be used as solvents in effecting the depolymerization of vulcanized polymers such as rubber tires. In particular, the components of vulcanized polymers can be recovered with the use of hydrophobic ionic liquids as a solvent. One example of a hydrophobic ionic liquid that may be employed as a solvent is [(C 6 H 13 ) 3 C 10 H 21 P] +  [(CF 3 SO 2 ) 2 )N] − , which is commercially available and known by the abbreviation RyPTf2N. 
         [0009]    In a generally applicable method to depolymerize vulcanized polymers the following procedure may be used. The vulcanized rubber is mixed with the hydrophobic ionic liquid in a sealed vessel and heated to an elevated temperature. In one embodiment the mixture is heated to a vapor temperature exceeding 175° C., more specifically to a vapor temperature exceeding 300° C. and more specifically still to a vapor temperature equal to or exceeding 330° C. The vulcanized rubber is depolymerized while at this elevated temperature, dissolving in the hydrophobic ionic liquid. 
         [0010]    The dissolved components of the vulcanized rubber can be separated from the ionic liquid in a number of different ways. For example, a precipitate can be formed in the ionic liquid by the addition of a suitable substance to the mixture. One example of a substance may be a non-polar organic material such as hexane. This process renders a gooey-type tar residue that reacts with the hexane to render precipitate at the bottom of the vessel. The residue that is obtained includes about 80% carbon (similar to carbon black), 10% oxygen, with the remaining including calcium and silicon. 
         [0011]    Ionic liquids with hydrophobic anions and cations allow for the material to be broken down. The hydrophobic nature of such liquids lets organic solvents out, including hexane. This allows for the separation of the ionic liquid/polymer in one container and the water/carbon black in another. The hydrophobic nature of the ionic liquid is thus important to retrieving and separating the carbon black. 
         [0012]      FIG. 1  is a flowchart showing one example of a method for recycling rubber tires. The method begins at  110  when the one or more rubber tires are shredded or otherwise cut up into convenient size pieces. At  120  the rubber tire pieces are mixed with a hydrophobic ionic liquid in a closed vessel. The hydrophobic ionic liquid may be [(C 6 H 13 ) 3 C 10 H 21 P] +  [(CF 3 SO 2 ) 2 )N] − . Next, at  130  the mixture is heated to a vapor temperature of about 330° C. and the tire pieces are allowed to dissolve. The constituents of the rubber tires are recovered at  140  by producing a precipitate by the addition of hexane to the mixture, which can then be filtered to recover the solid material. 
         [0013]    The foregoing disclosure constitutes a description of specific embodiments illustrating how the invention may be used and applied. Such embodiments are only exemplary. The invention in its broadest aspects is further defined in the claims which follow. These claims and terms used therein are to be taken as variants of the invention described. These claims are not restricted to such variants but are to be read as covering the full scope of the invention implicit within the disclosure herein.