Abstract:
A polyhydroxyalkanoate that comprises a unit represented by the following chemical formula (1):  
                         
 
     wherein R1 is a substituent of an aromatic ring selected from the group consisting of H, CH 3 , C 2 H 5 , CH 3 CH 2 CH 2 , (CH 3 ) 2 CH, (CH 3 ) 3 C, a halogen atom, CN, NO 2 , COOR′, and SO 2 R″, wherein R′ is selected from the group consisting of H, Na, K, CH 3 , and C 2 H 5 , and R″ is selected from the group consisting of OH, a halogen atom, ONa, OK, OCH 3 , and OC 2 H 5 ; and x represents an integer of 1 to 8 being the same or different each other in the polyhydroxyalkanoate. A method for producing the polyhydroxyalkanoate is also provided.

Description:
BACKGROUND OF THE INVENTION  
         [0001]    1. Field of the Invention  
           [0002]    The present invention relates to a polyhydroxyalkanoate (hereinafter, also referred to as “PHA” for short) that comprises a novel structural unit and a process for producing the same. More particularly, the present invention relates to a novel biodegradable PHA that comprises 3-hydroxyalkanoic acid units having a substituted or unsubstituted (phenylmethyl)sulfanyl group at the end of the side chain thereof, and to a process for producing PHAs from an alkanoic acid having a substituted or unsubstituted (phenylmethyl)sulfanyl group at the end of the side chain thereof by using a microorganism capable of producing PHA and accumulating it in the cell.  
           [0003]    2. Related Background Art  
           [0004]    It has been reported that various microorganisms can produce poly-3-hydroxybutyrate (hereinafter, also referred to as “PHB” for short) or other PHA and accumulate it in the cell (“Biodegradable Plastics Handbook”, Biodegradable Plastics Society Ed., NTS, pages 178-197 (1995)). These polymers may be utilized for production of various products by, for example, melt processing as with conventional plastics, but unlike many conventional synthetic polymer compounds, these polymers do not cause pollution in the natural environment because they are biodegradable, i.e., they are completely degraded by microorganisms in the natural world. Furthermore, they have good biocompatibility and their applications in the medical field as soft materials are expected.  
           [0005]    Microbial PHAs are known to have different compositions and/or structures depending on, for example, the type of the microorganism, compositions of the culture medium, and culture conditions. Thus, studies have been done to control the composition and structure to improve physical properties of PHA.  
           [0006]    (1) First, the following articles report or disclose synthesis of PHA by polymerization of relatively simple monomer units such as 3-hydroxybutyric acid (hereinafter, abbreviated as 3HB).  
           [0007]    For instance,  Alcaligenes eutrophus  H16 (ATCC No. 17699) and mutants thereof are known to produce copolymers of 3-hydroxybutyrate and 3-hydroxyvalerate (hereinafter, abbreviated as 3HV) with various composition ratios (Japanese Patent Publication No. 6-15604 and Japanese Patent Publication Nos. 7-14352 and 8-19227.)  
           [0008]    Japanese Patent No. 2642937 discloses production of PHA of C 6  to C 12  3-hydroxyalkanoate monomer units by feeding acyclic aliphatic hydrocarbon compounds as substrates to  Pseudomonas oleovorans  (ATCC No. 29347).  
           [0009]    Japanese Patent Application Laid-Open No. 5-7492 discloses a process for producing a copolymer of 3HB and 3HV using a microorganism such as Methylobacterium sp., Paracoccus sp., Alcaligenes sp., and Pseudomonas sp. in contact with C 3  to C 7  primary alcohol.  
           [0010]    Japanese Patent Application Laid-Open No. 5-93049 and Japanese Patent Application Laid-Open No. 7-265065 disclose production of two-component copolymers of 3HB and 3-hydroxyhexanate by cultivating  Aeromonas caviae  with oleic acid or olive oil as a substrate.  
           [0011]    Japanese Patent Application Laid-Open No. 9-191893 discloses that  Comamonans acidovorans  IFO 13852 produces polyester containing 3HB and 4-hydroxybutyrate as the monomer units when it is cultivated in the presence of gluconic acid and 1,4-butanediol as substrates.  
           [0012]    The above-mentioned PHAs are “usual PHAs” including monomer units having an alkyl group as the side chain thereof, synthesized by microorganisms via β-oxidation of hydrocarbons etc. or via fatty acid synthesis from saccharides.  
           [0013]    (2) However, “unusual PHAs”, i.e., PHAs having a substituent other than an alkyl group on the side chain, are expected to be very useful when more extensive application of microbial PHAs is considered, for example, as functional polymers. Certain microorganisms have already been known to produce such “unusual PHAs”, and it has been tried to improve physical properties of microbial PHA with such an approach.  
           [0014]    Examples of the substituents include unsaturated hydrocarbons, ester groups, cyano groups, halogenated hydrocarbons, epoxides, and those containing an aromatic ring or rings. Of these, PHAs having an aromatic ring have been studied actively.  
           [0015]    For example,  Makromol. Chem.,  191, 1957-1965 (1990),  Macromolecules,  24, 5256-5260 (1991), and  Chirality,  3, 492-494 (1991) report that  Pseudomonas oleovorans  produces PHAs containing 3-hydroxy-5-phenylvalerate (hereinafter, abbreviated as 3HPV) as the monomer unit, where changes in physical properties of the PHA are observed probably due to the presence of 3HPV.  
           [0016]    Of the PHAs having a substituent on the side chain thereof, lately those having a phenoxy group on the side chain have been actively developed.  
           [0017]    It has been reported that  Pseudomonas oleovorans  produces from 11-phenoxyundecanoic acids PHA made with monomer units of 3-hydroxy-5-phenoxyvalerate and 3-hydroxy-9-phenoxynonanoate (Macromol. Chem. Phys., 195, 1665-1672 (1994)).  
           [0018]    Macromolecules, 29, 3432-3435 (1996) reports production of PHA having monomer units of 3-hydroxy-4-phenoxybutyrate and 3-hydroxy-6-phenoxyhexanoate from 6-phenoxyhexanoic acids; production of PHA having units of 3-hydroxy-4-phenoxybutyrate, 3-hydroxy-6-phenoxyhexanoate, 3-hydroxy-4-phenoxybutyrate, 3-hydroxy-6-phenoxyhexanoate and 3-hydroxy-8-phenoxyoctanoate from 8-phenoxyoctanoic acid; and production of PHA made with units of 3-hydroxy-5-phenoxyvaleric acid and 3-hydroxy-7-phenoxyheptanoic acid from 11-hydroxyundecanoic acid, by using  Pseudomonas oleovorans.    
           [0019]    Can. J. Microbiol., 41, 32-43 (1995) reports production of PHAs containing 3-hydroxy-6-(4-cyanophenoxy)hexanoic acids or 3-hydroxy-6-(4-nitrophenoxy)hexanoic acid as the monomer units by  Pseudomonas oleovorans  ATCC 29347 or  Pseudomonas putida  KT 2422 using octanoic acid and 6-(4-cyanophenoxy)hexanoic acid or 6-(p-nitrophenoxy)hexanoic acid as a substrate.  
           [0020]    Of unusual PHAs developed, production of those having sulfur atoms in the form of sulfide (—S—) in the side chain thereof is reported in Macromolecules, 32, 8315-8318 (1999), where  Pseudomonas putida  27N01 produced PHAs containing 3-hydroxy-5-(phenylsulfanyl)valeric acid and 3-hydroxy-7-(phenylsulfanyl)heptanoic acid as the monomer units, using octanoic acid and 11-(phenylsulfanyl)undecanoic acid as the substrates. In that case, the  Pseudomonas putida  27N01 is pre-cultured in a culture medium containing octanoic acid only as the growth substrate, and then transferred to a culture medium that contains only 11-(phenylsulfanyl)undecanoic acid as a substrate.  
           [0021]    Also Polymer Preprints, Japan Vol. 49, No. 5, 1034 (2000) reports production of PHAs containing two monomer units of 3-hydroxy-[(phenylmethyl)sulfanyl]valeric acid and 3-hydroxy-7-[(phenylmethyl)sulfanyl]heptanoic acid, by using  Pseudomonas putida  27N01 and 11-[(phenylmethyl)sulfanyl]undecanoic acid as a substrate. In this case also,  Pseudomonas putida  27N01 is precultured in a culture medium that contains only octanoic acid as the growth substrate, and then transferred to a culture medium that contains only 11-[(phenylmethyl)sulfanyl]undecanoic acid.  
           [0022]    Concerning PHAs containing a 3-hydroxy-ω-[(phenylmethyl)sulfanyl]alkanoic acid unit among unusual PHAs, the above articles are the only reports on the biosynthesis of such PHAs. Further, the available production process is limited. Accordingly, the resulting polymers are not sufficient in types, purity, and yield. In the above process for producing the PHAs containing a 3-hydroxy-ω-[(phenylmethyl)sulfanyl]alkanoic acid unit, the polymer production is conducted by culturing the microorganism in a culture medium containing only ω-[(phenylmethyl)sulfanyl]alkanoic acid having a long carbon chain as the substrate, where ω-[(phenylmethyl)sulfanyl]alkanoic acid is also used as the growth substrate. Therefore, it is difficult to control the structure of the polymer.  
           [0023]    PHAs containing a substituted 3-hydroxy-ω-{[(substituted phenyl)methyl]sulfanyl}alkanoic acid unit that has a substituent such as various functional groups on the benzene ring of (phenylmethyl)sulfanyl group at the end of the side chain are PHAs having novel functionalities, and improvement in physical properties of such PHAs is predicted. Application of such PHAs will be expanded to novel fields where conventional PHAs have not been applicable. Thus, development of an efficient process for producing such PHAs is desired.  
         SUMMARY OF THE INVENTION  
         [0024]    Through the intensive research to solve the above-mentioned problems by the present inventors, this invention was accomplished.  
           [0025]    An object of the present invention is to provide a novel PHA and a process for producing the same, in which the PHA comprises a novel unit having a (phenylmethyl)sulfanyl structure in a substituted or unsubstituted side chain thereof.  
           [0026]    According to one aspect of the present invention, there is provided a polyhydroxyalkanoate comprising a unit represented by the following chemical formula (1):  
                         
 
           [0027]    wherein R1 is a substituent of an aromatic ring selected from the group consisting of H, CH 3 , C 2 H 5 , CH 3 CH 2 CH 2 , (CH 3 ) 2 CH, (CH 3 ) 3 C, a halogen atom, CN, NO 2 , COOR′, and SO 2 R″, wherein R′ is selected from the group consisting of H, Na, K, CH 3 , and C 2 H 5 , and R″ is selected from the group consisting of OH, a halogen atom, ONa, OK, OCH 3 , and OC 2 H 5 ; and x represents an integer of 1 to 8 being the same or different each other in the polyhydroxyalkanoate, with the proviso that the polyhydroxyalkanoate does not consist of two units represented by the following chemical formulae (2) and (3):  
                         
 
           [0028]    According to another aspect of the present invention, there is provided a process for producing a polyhydroxyalkanoate that comprises a unit represented by the chemical formula (1) comprising the step of cultivating a microorganism in a culture medium containing a compound represented by the following chemical formula (10):  
                         
 
           [0029]    wherein R2 is a substituent of an aromatic ring and selected the group consisting of H, CH 3 , C 2 H 5 , CH 3 CH 2 CH 2 , (CH 3 ) 2 CH, (CH 3 ) 3 C, a halogen atom, CN, NO 2 , COOR′ and SO 2 R″, wherein R′ is selected from the group consisting of H, Na, K, CH 3 , and C 2 H 5 , and R″ is selected from the group consisting of OH, a halogen atom, ONa, OK, OCH 3 , and OC 2 H 5 ; and k represents an integer of 1 to 8. 
       
    
    
     BRIEF DESCRIPTION OF THE DRAWINGS  
       [0030]    [0030]FIG. 1 shows the  1 H NMR spectrum of a polyhydroxyalkanoate obtained in Example 1;  
         [0031]    [0031]FIG. 2 shows the  13 C NMR spectrum of the polyhydroxyalkanoate obtained in the Example 1;  
         [0032]    [0032]FIG. 3 shows the  1 H NMR spectrum of a polyhydroxyalkanoate obtained in Example 10;  
         [0033]    [0033]FIG. 4 shows the  1 H NMR spectrum of a PHA obtained in Example 19;  
         [0034]    [0034]FIG. 5 shows the  13 C NMR spectrum of the PHA obtained in the Example 19; and  
         [0035]    [0035]FIG. 6 shows the  1 H NMR spectrum of a PHA obtained in Example 29. 
     
    
     DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENT  
       [0036]    A novel polyhydroxyalkanoate according to the present invention has a substituted or unsubstituted (phenylmethyl)sulfanyl structure on the side chain of a unit hydroxyalkanoic acid. This structure provides physical and chemical properties that are significantly different from those of known microbial polyhydroxyalkanoates.  
         [0037]    The novel polyhydroxyalkanoate according to the present invention can be produced by the steps of: culturing a PHA producing microorganism in a culture medium containing a growth substrate and a substituted or unsubstituted ω-[(phenylmethyl)sulfanyl]alkanoic acid as a feedstock; and recovering polyhydroxyalkanoate containing units having a substituted or unsubstituted (phenylmethyl)sulfanyl group at the end of the side chain thereof, the polyhydroxyalkanoates being produced by accumulated in the microorganism during the cultivation step. In the microbial PHAs, the carbons at the 3 position of all 3-hydroxyalkanoic acid units including those represented by the chemical formula (1) are asymmetric carbons whose absolute configuration is R, indicating the biodegradability thereof.  
         [0038]    Examples of the halogen atom in the substituent R on the benzene ring in the above general formulae (1) and (10) include fluorine, chlorine, and bromine.  
         [0039]    The present invention is described more in detail below.  
         [0040]    PHA-Producing Microorganisms  
         [0041]    In the process for producing PHAs according to the present invention, any microorganisms can be used to produce PHA containing a unit having a substituted or unsubstituted (phenylmethyl)sulfanyl group at the end of the side chain thereof represented by the chemical formula (1) (hereinafter referred to as the subject PHA) so long as it can produce the subject PHA and accumulate it in the cells when cultivated in a culture medium containing a corresponding ω-[(phenylmethyl)sulfanyl]alkanoic acid represented by the chemical formula (10) as the source compound. For example, the microorganisms may be those belonging to the genus  Pseudomonas having PHA-producing capabilities.    
         [0042]    Examples of suitable microorganisms of genus Pseudomonas include the following three strains:  Pseudomonas cichorii  YN2 (FERM BP-7375),  Pseudomonas cichorii  H45 (FERM BP-7374), and  Pseudomonas jessenii  P161 (FERM BP-7376). These three microorganisms was first deposited as the national deposit by the applicant, and is deposited as the international deposit under the Budapest Treaty under the above-mentioned accession numbers in International Patent Organism Depositary, National Institute of Advanced Industrial Science and Technology, Independent Administrative Institution, Ministry of Economy, Trade and Industry 1-3, Higashi 1-chome, Tsukuba-shi, Ibaraki-ken, 305 JAPAN (former National Institute of Bioscience and Human-Technology (NIBH) of the Agency of Industrial Science and Technology, Ministry of Economy, Trade and Industry). They are also described in Japanese Patent Application No. 11-371863 (Japanese Patent Application Laid-Open No. 2001-178484) as novel strains capable of producing PHAs.  
         [0043]    Bacteriological properties of the strains YN2, H45, and P161 are given below.  
         [0044]    &lt;Bacteriological Properties of Strain YN2&gt; 
         [0045]    (1) Morphological Properties  
         [0046]    Shape and size of cells: rod, 0.8 μm×1.5 to 2.0 μm  
         [0047]    Polymorphism of cells: negative  
         [0048]    Mobility: motile  
         [0049]    Sporulation: negative  
         [0050]    Gram staining: negative  
         [0051]    Colony shape: circular; entire, smooth margin; low convex; smooth surface; glossy; translucent  
         [0052]    (2) Physiological Properties  
         [0053]    Catalase: positive  
         [0054]    Oxidase: positive  
         [0055]    O/F test: oxidative (non-fermentative)  
         [0056]    Nitrate reduction: negative  
         [0057]    Indole production: positive  
         [0058]    Acid production from glucose: negative  
         [0059]    Arginine dihydrolase: negative  
         [0060]    Urease: negative  
         [0061]    Esculin hydrolysis: negative  
         [0062]    Gelatin hydrolysis: negative  
         [0063]    β-Galactosidase: negative  
         [0064]    Fluorescent pigment production on King&#39;s B agar: positive  
         [0065]    Growth under 4% NaCl: positive (weak growth)  
         [0066]    Poly-β-hydroxybutyrate accumulation: negative (*)  
         [0067]    Tween 80 hydrolysis: positive  
         [0068]    (*) Colonies cultured on nutrient agar were stained with Sudan Black for determination.  
         [0069]    (3) Substrate Assimilation  
         [0070]    Glucose: positive  
         [0071]    L-Arabinose: positive  
         [0072]    D-Mannose: negative  
         [0073]    D-Mannitol: negative  
         [0074]    N-Acetyl-D-glucosamine: negative  
         [0075]    Maltose: negative  
         [0076]    Potassium gluconate: positive  
         [0077]    n-Caprate: positive  
         [0078]    Adipate: negative  
         [0079]    dl-Malate: positive  
         [0080]    Sodium citrate: positive  
         [0081]    Phenyl acetate: positive  
         [0082]    &lt;Bacteriological Properties of Strain H45&gt; 
         [0083]    (1) Morphological Properties  
         [0084]    Shape and size of cells: rod, 0.8 μm×1.0 to 1.2 μm  
         [0085]    Polymorphism of cells: negative  
         [0086]    Mobility: motile  
         [0087]    Sporulation: negative  
         [0088]    Gram staining: negative  
         [0089]    Colony shape: circular; entire, smooth margin; low convex; smooth surface; glossy; cream-colored  
         [0090]    (2) Physiological Properties  
         [0091]    Catalase: positive  
         [0092]    Oxidase: positive  
         [0093]    O/F test: oxidative  
         [0094]    Nitrate reduction: negative  
         [0095]    Indole production: negative  
         [0096]    Acid production from glucose: negative  
         [0097]    Arginine dihydrolase: negative  
         [0098]    Urease: negative  
         [0099]    Esculin hydrolysis: negative  
         [0100]    Gelatin hydrolysis: negative  
         [0101]    β-Galactosidase: negative  
         [0102]    Fluorescent pigment production on King&#39;s B agar: positive  
         [0103]    Growth under 4% NaCl: negative  
         [0104]    Poly-β-hydroxybutyrate accumulation: negative  
         [0105]    (3) Substrate Assimilation  
         [0106]    Glucose: positive  
         [0107]    L-Arabinose: negative  
         [0108]    D-Mannose: positive  
         [0109]    D-Mannitol: positive  
         [0110]    N-Acetyl-D-glucosamine: positive  
         [0111]    Maltose: negative  
         [0112]    Potassium gluconate: positive  
         [0113]    n-Caprate: positive  
         [0114]    Adipate: negative  
         [0115]    dl-Malate: positive  
         [0116]    Sodium citrate: positive  
         [0117]    Phenyl acetate: positive  
         [0118]    &lt;Bacteriological Properties of Strain P161&gt; 
         [0119]    (1) Morphological Properties  
         [0120]    Shape and size of cells: sphere, φ0.6 μm, rods, 0.6 μm×1.5 to 2.0 μm  
         [0121]    Polymorphism of cells: elongated form  
         [0122]    Mobility: motile  
         [0123]    Sporulation: negative  
         [0124]    Gram staining: negative  
         [0125]    Colony shape: circle; entire, smooth margin; low convex; smooth surface; pale yellow  
         [0126]    (2) Physiological Properties  
         [0127]    Catalase: positive  
         [0128]    Oxidase: positive  
         [0129]    O/F test: oxidative  
         [0130]    Nitrate reduction: positive  
         [0131]    Indole production: negative  
         [0132]    Acid production from glucose: negative  
         [0133]    Arginine dihydrolase: positive  
         [0134]    Urease: negative  
         [0135]    Esculin hydrolysis: negative  
         [0136]    Gelatin hydrolysis: negative  
         [0137]    β-Galactosidase: negative  
         [0138]    Fluorescent pigment production on King&#39;s B agar: positive  
         [0139]    (3) Substrate Assimilation  
         [0140]    Glucose: positive  
         [0141]    L-Arabinose: positive  
         [0142]    D-Mannose: positive  
         [0143]    D-Mannitol: positive  
         [0144]    N-Acetyl-D-glucosamine: positive  
         [0145]    Maltose: negative  
         [0146]    Potassium gluconate: positive  
         [0147]    n-Caprate: positive  
         [0148]    Adipate: negative  
         [0149]    dl-Malate: positive  
         [0150]    Sodium citrate: positive  
         [0151]    Phenyl acetate: positive  
         [0152]    Cultivation  
         [0153]    According to the PHA production method of the present invention, by culturing the above-mentioned microorganism capable of producing PHA in a culture medium containing ω-[(phenylmethyl)sulfanyl]alkanoic acid represented by the above chemical formula (10) as a feedstock, PHA represented by the chemical formula (1) containing 3-hydroxyalkanate units having a substituted or unsubstituted (phenylmethyl)sulfanyl group at the end of the side chain thereof is produced by and accumulated in the cells.  
         [0154]    For ordinary culture of the microorganisms used in the present invention, for example, for preparation of stock strains, or for obtaining cells or maintaining activities required in PHA production, culture media are selected to contain ingredients necessary for the proliferation of the microorganisms used. For example, any one of known culture media, such as typical natural culture media (e.g., nutrient broth, yeast extract) and synthetic culture media supplemented with nutrients, may be used as long as the culture medium does not adversely affect the growth and survival of the microorganisms. Cultivation conditions such as temperature, aeration and agitation are appropriately selected depending on the microorganisms used.  
         [0155]    In order to produce the subject PHA by using the PHA-producing microorganism as described above, an inorganic culture medium may be used that contains at least a growth substrate for the microorganism and a compound represented by the above chemical formula (10) corresponding to the monomer unit as the feedstock for PHA production. It is desirable that the compound represented by the above chemical formula (10) be contained in an amount of 0.01% to 1% (w/v), and more preferably 0.02% to 0.2%, per a culture medium. The compound represented by the chemical formula (10) does not always have good water solubility. However, with the microorganisms indicated herein, suspension would cause no trouble.  
         [0156]    The feedstock compound represented by the chemical formula (10) may be, in some cases, added to the culture medium as a solution or suspension in a solvent such as 1-hexadecene or n-hexadecane in order to improve dispersibility. In such a case, the concentration of the solvent is required to be equal to or lower than 3% (v/v) relative to the solution of the culture medium.  
         [0157]    It is preferable to add a growth substrate for microbial proliferation to the culture medium separately. As the growth substrate, nutrients such as yeast extract, polypeptone, and meat extract may be used. The growth substrate may be selected based on the usefulness as the substrate to the strain to be used, from saccharides, organic acids generated in the TCA cycle, organic acids or salts thereof generated from the biochemical reactions one or two steps later than the TCA cycle, amino acids or salts thereof, C 4  to C 12  straight chain alkanoic acids or salts thereof.  
         [0158]    One or more saccharides may suitably be used selected from aldose such as glyceraldehyde, erythrose, arabinose, xylose, glucose, galactose, mannose, and fructose; alditol such as glycerol, erythritol, and xylitol; aldonic acids such as gluconic acid; uronic acid such as glucuronic acid and galacturonic acid; and disaccharide such as maltose, sucrose, and lactose.  
         [0159]    As the organic acids or salts thereof, one or more compounds may suitably be selected from pyruvic acid, malic acid, lactic acid, citric acid, succinic acid, and salts thereof.  
         [0160]    As the amino acids or salts thereof, one or more compounds may suitably be selected from glutamic acid, aspartic acid, and salts thereof.  
         [0161]    Of these, polypeptone and saccharides are preferable. Preferable saccharides include at least one selected from glucose, fructose, and mannose. Preferably, the substrate is contained in an amount of 0.1% to 5% (w/v), and more preferably 0.2% to 2% in the culture medium.  
         [0162]    Sometimes the microbial PHA productivity is improved when the microorganism is fully grown and then transferred to a culture medium in which nitrogen source such as ammonium chloride is limited and a compound serving as a substrate for PHA is added. For example, a multi-step approach may be used that performs two or more steps successively under different cultivation conditions.  
         [0163]    More specifically, a microorganism is grown in a culture medium that contains a compound represented by the chemical formula (10) and polypeptone until from late logarithmic phase to stationary phase (step 1-1), and then collected by using, for example, centrifugation. Subsequently, the microorganism cultivated in the step 1 is further cultivated in a culture medium that contains a compound represented by the chemical formula (10) and an organic acid or a salt thereof as described above (preferably without a nitrogen source) (step 1-2). Alternatively, the microorganism is cultured in a culture medium that contains a compound represented by the chemical formula (10) and a saccharide as described above until from late logarithmic phase to stationary phase (step 1-3), and collected by using, for example, centrifugation. Subsequently, the microorganism grown in the step 1 is further cultivated in a culture medium that contains the compound represented by the chemical formula (10) and a saccharide as described above (preferably without a nitrogen source) (step 1-4). In the first step of this two-step cultivation procedure, the cells are allowed to proliferate while producing the subject PHA from the feedstock compound represented by the above general formula (10). In the second step, the well-proliferated cells continue PHA production in the culture medium containing no nitrogen source to increase the amount of the PHA accumulated in the cells.  
         [0164]    The cultivation temperature should be a temperature at which the above-mentioned strains can proliferate well. For example, the cultivation temperature may be 15° C. to 40° C., preferably 20° C. to 35° C., and more preferably 20° C. to 30° C.  
         [0165]    The cultivation may be performed by any suitable cultivation techniques such as liquid or solid cultivation, with which the above-mentioned microorganisms can proliferate to produce polyhydroxyalkanoates. Furthermore, the type of the cultivation is not limited as long as oxygen is supplied properly. Examples include batch cultivation, fed batch cultivation, semi-continuous cultivation, and continuous cultivation. In liquid batch cultivation, the oxygen may be supplied while shaking the content of a shake flask. Alternatively, the oxygen may be supplied by means of an agitation-ventilation method using a jar fermenter.  
         [0166]    As the inorganic culture medium to be used for the above-mentioned cultivation procedure, any culture medium may be used that contains ingredients that are required for the proliferation of the microorganisms, such as a phosphorous source (e.g., phosphates) and a nitrogen source (e.g., ammonium salts, nitrates). For example, MSB medium and M9 medium may be used.  
         [0167]    The composition of an inorganic culture medium (M9 medium) that is used in a process according to the present invention is given below.  
         [0168]    (M9 Medium)  
                                                       Na 2 HPO 4     6.2 g           KH 2 PO 4     3.0 g           NaCl   0.5 g           NH 4 Cl   1.0 g                      
 
         [0169]    (in 1 liter culture medium; pH 7.0)  
         [0170]    In order to ensure good proliferation, and production of the polyhydroxyalkanoates, it is necessary to add a trace ingredient solution that is indicated below in an amount of about 0.3% (v/v) to the above-mentioned inorganic culture medium.  
         [0171]    (Trace Ingredient Solution)  
         [0172]    Nitrilotriacetic Acid: 1.5 g; MgSO 4 : 3.0 g;  
         [0173]    MnSO 4 : 0.5 g; NaCl: 1.0 g; FeSO 4 : 0.1 g;  
         [0174]    CaCl 2 : 0.1 g; CoCl 2 : 0.1 g; ZnSO 4 : 0.1 g;  
         [0175]    CuSO 4 : 0.1 g; AlK(SO 4 ) 2 : 0.1 g;  
         [0176]    H 3 BO 3 : 0.1 g; Na 2 MoO 4 : 0.1 g; NiCl 2 : 0.1 g  
         [0177]    (1-liter solution; pH 7.0)  
         [0178]    PHA Recovery  
         [0179]    The microorganism used in the present invention produces and accumulates the subject PHA in the cell. Therefore, in the PHA production process of the present invention, a step of recovering the subject PHA from the cells is provided after the cultivation.  
         [0180]    For the purpose of recovering the PHA from the cells, a solvent extraction technique is used, in which a solubilized polyhydroxyalkanoate is separated from insoluble cell components. A standard chloroform extraction technique is the most convenient and simple but a solvent other than chloroform may be used such as dichloromethane, dioxane, tetrahydrofuran, acetonitrile, and acetone.  
         [0181]    In environments where it is difficult to use an organic solvent, components of the strains other than the polyhydroxyalkanoates are removed by treating with, for example, a surfactant such as SDS, with an enzyme such as lysozyme, or with EDTA and cellular components are removed to recover only the polyhydroxyalkanoates. Alternatively, one can use cell disruption treatment such as ultrasonic disruption, homogenization, pressure disruption, disruption with glass beads, trituration, grinding and freeze-thawing to separate and recover the polyhydroxyalkanoates accumulated in the cells.  
         [0182]    It should be understood that the cultivation of the microorganisms of the present invention, the production of the polyhydroxyalkanoates by the microorganisms of the present invention and accumulation of the polyhydroxyalkanoates in the cell, and the recovery of the polyhydroxyalkanoates from the cell are not limited to the above-mentioned techniques and procedures.  
         [0183]    The polyhydroxyalkanoates that are produced by the microorganisms according to the process of the present invention may comprise, in addition to the units represented by the chemical formula (1), 3-hydroxyalkanoic acid units represented by the chemical formula (4) or 3-hydroxyalk-5-enoic acid units represented by the chemical formula (5) that is biosynthesized through a fatty acid synthesizing system by using a proliferation substrate to be added to the culture medium. The carbons at the 3 position of all 3-hydroxyalkanoic acid units contained are asymmetric carbons whose absolute configuration is R, indicating the biodegradability thereof. The presence of the (phenylmethyl)sulfanyl group in the units represented by the chemical formula (1) and the presence of the various substituents positioned on the benzene ring thereof provide new physical and chemical properties to the polymers. Improvements in physical properties of such polymers are expected. The polymers can be expanded to the fields to which they were not applicable in the past.  
       EXAMPLES  
       [0184]    The present invention is described specifically below with reference to examples thereof, but not limited thereto. In the following examples, percentages are by weight unless otherwise specified.  
       Example 1  
       [0185]    [0185] Pseudomonas cichorii  YN2 was inoculated to 200 mL of M9 medium containing 0.5% of D-glucose and 0.1% of 5-[(phenylmethyl)sulfanyl]valeric acid, and cultured with shaking at 125 strokes/min at 30° C. for 48 hours. Then, the cells were collected by centrifugation, re-suspended in 200 mL of M9 medium containing 0.5% of D-glucose and 0.1% of 5-[(phenylmethyl)sulfanyl]valeric acid but no nitrogen source (NH 4 Cl), and cultured at 30° C. with shaking at 125 strokes/min for 48 hours. After that, the cells were collected by centrifugation, washed once with cold methanol, and lyophilized.  
         [0186]    The lyophilized pellet was suspended in 20 mL of chloroform and stirred at 60° C. for 20 hours to extract polyhydroxyalkanoate. The extract was filtered through a membrane filter of a pore size of 0.45 μm and concentrated by a rotary evaporator. The concentrated solution was precipitated with cold methanol. The precipitate was recovered and dried in vacuum to yield 159 mg of polyhydroxyalkanoate.  
         [0187]    The polyhydroxyalkanoate was subjected to NMR analysis under the following conditions.  
         [0188]    &lt;Spectrometer&gt; FT-NMR: Bruker DPX 400 with spectrometer frequencies of 400 MHz for  1 H-NMR and 100 MHz for  13 C.  
         [0189]    &lt;Conditions&gt; 
         [0190]    Nuclear Species:  1 H,  13 C  
         [0191]    Solvent: CDCl 3    
         [0192]    Temperature: room temperature  
         [0193]    [0193]FIGS. 1 and 2 show  1 H-NMR spectra and  13 C-NMR spectra, respectively, of the polyhydroxyalkanoate. Identification results thereof are given in Tables 1 and 2 below.  
                                   TABLE 1                                   Chemical       Splitting               shifts (ppm)   Integration   patterns   Identification                           1.83   2 H   qurt   d1           2.36-2.54   4 H   m   b1, c1           3.67   2 H   s   f1           5.20   1 H   quint   c1           7.20   1 H   m   j1           7.25-7.28   4 H   m   h1, l1 &amp; i1, k1                      
 
         [0194]    [0194]                                         TABLE 2                                   Chemical shifts               (ppm)   Identification                                        26.6   d1           33.0   e1           35.9   f1           38.6   b1           69.7   c1           126.9   j1           128.4   h, l           128.8   i, k           138.0   g1           168.9   a1                        
         [0195]    As clearly shown by Tables 1 and 2, it was confirmed that the polyhydroxyalkanoate is one represented by the following chemical formula (16) containing, as the monomer units, 3-hydroxy-5-[(phenylmethyl)sulfanyl]valerate, and 3-hydroxyalkanoates and/or 3-hydroxyalkenoates corresponding to saturated/unsaturated fatty acids having 4 to 12 carbon atoms such as 3-hydroxybutyric acid and 3-hydroxyvaleric acid. The integration of the  1 H-NMR spectra indicated that the polyhydroxyalkanoate contains 3-hydroxy-5-[(phenylmethyl)sulfanyl]valerate by 85.9 mol %.  
                         
 
         [0196]    The molecular weight of the polyhydroxyalkanoate was determined by gel permeation chromatography (GPC; TOSOH HLC-8220, column; TOSOH TSK-GEL SuperHM-H (trade name), solvent; chloroform, polystyrene equivalent). As a result, Mn was 14,400 and Mw was 56,700.  
       Example 2  
       [0197]    [0197] Pseudomonas cichorii  H45 was inoculated to 200 mL of M9 medium containing 0.5% of D-glucose and 0.1% of 5-[(phenylmethyl)sulfanyl]valeric acid, and cultured with shaking at 125 strokes/min at 30° C. for 48 hours. Then, the cells were collected by centrifugation, re-suspended in 200 mL of M9 medium containing 0.5% of D-glucose and 0.1% of 5-[(phenylmethyl)sulfanyl]valeric acid but no nitrogen source (NH 4 Cl), and cultured at 30° C. with shaking at 125 strokes/min for 48 hours. After that, the cells were collected by centrifugation, washed once with cold methanol, and lyophilized.  
         [0198]    The lyophilized pellet was suspended in 20 mL of chloroform and stirred at 60° C. for 20 hours to extract polyhydroxyalkanoate. The extract was filtered through a membrane filter of a pore size of 0.45 μm and concentrated by a rotary evaporator. The concentrated solution was precipitated with cold methanol. The precipitate was recovered and dried in vacuum to yield 138 mg of polyhydroxyalkanoate.  
         [0199]    The polyhydroxyalkanoate obtained was subjected to NMR analysis under the same conditions as in the Example 1. As a result, it was revealed that this polyhydroxyalkanoate is one represented by the chemical formula (16) containing, as the monomer units, 3-hydroxy-5-[(phenylmethyl)sulfanyl]valerate, and 3-hydroxyalkanoates and/or 3-hydroxyalkenoates corresponding to saturated/unsaturated fatty acids having 4 to 12 carbon atoms such as 3-hydroxybutyric acid and 3-hydroxyvaleric acid. The integration of the  1 H-NMR spectra indicated that the polyhydroxyalkanoate contains 3-hydroxy-5-[(phenylmethyl)sulfanyl]valerate by 95.2 mol %.  
       Example 3  
       [0200]    [0200] Pseudomonas jessenii  P161 was inoculated to 200 mL of M9 medium containing 0.5% of D-glucose and 0.1% of 5-[(phenylmethyl)sulfanyl]valeric acid, and cultured with shaking at 125 strokes/min at 30° C. for 48 hours. Then, the cells were collected by centrifugation, re-suspended in 200 mL of M9 medium containing 0.5% of D-glucose and 0.1% of 5-[(phenylmethyl)sulfanyl]valeric acid but no nitrogen source (NH 4 Cl), and cultured at 30° C. with shaking at 125 strokes/min for 47 hours. After that, the cells were collected by centrifugation, washed once with cold methanol, and lyophilized.  
         [0201]    The lyophilized pellet was suspended in 20 mL of chloroform and stirred at 60° C. for 20 hours to extract polyhydroxyalkanoate. The extract was filtered through a membrane filter of a pore size of 0.45 μm and concentrated by a rotary evaporator. The concentrated solution was precipitated with cold methanol. The precipitate was recovered and dried in vacuum to yield 164 mg of polyhydroxyalkanoate.  
         [0202]    The polyhydroxyalkanoate obtained was subjected to NMR analysis under the same conditions as in the Example 1. As a result, it was revealed that this polyhydroxyalkanoate is one represented by the chemical formula (16) containing, as the monomer units, 3-hydroxy-5-[(phenylmethyl)sulfanyl]valerate, and 3-hydroxyalkanoates and/or 3-hydroxyalkenoates corresponding to saturated/unsaturated fatty acids having 4 to 12 carbon atoms such as 3-hydroxybutyric acid and 3-hydroxyvaleric acid. The integration of the  1 H-NMR spectra indicated that the polyhydroxyalkanoate contains 3-hydroxy-5-[(phenylmethyl)sulfanyl]valerate by 96.7 mol %.  
       Example 4  
       [0203]    [0203] Pseudomonas cichorii  YN2 was inoculated to 200 mL of M9 medium containing 0.5% of polypeptone (Wako Pure Chemical Industries, Ltd.) and 0.1% of 5-[(phenylmethyl)sulfanyl]valeric acid, and cultured with shaking at 125 strokes/min at 30° C. for 48 hours. Then, the cells were collected by centrifugation, washed once with cold methanol, and lyophilized.  
         [0204]    The lyophilized pellet was suspended in 20 mL of chloroform and stirred at 60° C. for 20 hours to extract polyhydroxyalkanoate. The extract was filtered through a membrane filter of a pore size of 0.45 μm and concentrated by a rotary evaporator. The concentrated solution was precipitated with cold methanol. The precipitate was recovered and dried in vacuum to yield 161 mg of polyhydroxyalkanoate.  
         [0205]    The polyhydroxyalkanoate obtained was subjected to NMR analysis under the same conditions as in the Example 1. As a result, it was revealed that this polyhydroxyalkanoate is one represented by the chemical formula (16) containing, as the monomer units, 3-hydroxy-5-[(phenylmethyl)sulfanyl]valerate, and 3-hydroxyalkanoates and/or 3-hydroxyalkenoates corresponding to saturated/unsaturated fatty acids having 4 to 12 carbon atoms such as 3-hydroxybutyric acid and 3-hydroxyvaleric acid. The integration of the  1 H-NMR spectra indicated that the polyhydroxyalkanoate contains 3-hydroxy-5-[(phenylmethyl)sulfanyl]valerate by 83.8 mol %.  
       Example 5  
       [0206]    [0206] Pseudomonas cichorii  H45 was inoculated to 200 mL of M9 medium containing 0.5% of polypeptone (Wako Pure Chemical Industries, Ltd.) and 0.1% of 5-[(phenylmethyl)sulfanyl]valeric acid, and cultured with shaking at 125 strokes/min at 30° C. for 48 hours Then, the cells were collected by centrifugation, washed once with cold methanol, and lyophilized.  
         [0207]    The lyophilized pellet was suspended in 20 mL of chloroform and stirred at 60° C. for 20 hours to extract polyhydroxyalkanoate. The extract was filtered through a membrane filter of a pore size of 0.45 μm and concentrated by a rotary evaporator. The concentrated solution was precipitated with cold methanol. The precipitate was recovered and dried in vacuum to yield 113 mg of polyhydroxyalkanoate.  
         [0208]    The polyhydroxyalkanoate obtained was subjected to NMR analysis under the same conditions as in the Example 1. As a result, it was revealed that this polyhydroxyalkanoate is one represented by the chemical formula (16) containing, as the monomer units, 3-hydroxy-5-[(phenylmethyl)sulfanyl]valerate, and 3-hydroxyalkanoates and/or 3-hydroxyalkenoates corresponding to saturated/unsaturated fatty acids having 4 to 12 carbon atoms such as 3-hydroxybutyric acid and 3-hydroxyvaleric acid. The integration of the  1 H-NMR spectra indicated that the polyhydroxyalkanoate contains 3-hydroxy-5-[(phenylmethyl)sulfanyl]valerate by 96.2 mol %.  
       Example 6  
       [0209]    [0209] Pseudomonas jessenii  P161 was inoculated to 200 mL of M9 medium containing 0.5% of polypeptone (Wako Pure Chemical Industries, Ltd.) and 0.1% of 5-[(phenylmethyl)sulfanyl]valeric acid, and cultured with shaking at 125 strokes/min at 30° C. for 48 hours. Then, the cells were collected by centrifugation, washed once with cold methanol, and lyophilized.  
         [0210]    The lyophilized pellet was suspended in 20 mL of chloroform and stirred at 60° C. for 20 hours to extract polyhydroxyalkanoate. The extract was filtered through a membrane filter of a pore size of 0.45 μm and concentrated by a rotary evaporator. The concentrated solution was precipitated with cold methanol. The precipitate was recovered and dried in vacuum to yield 126 mg of polyhydroxyalkanoate.  
         [0211]    The polyhydroxyalkanoate obtained was subjected to NMR analysis under the same conditions as in the Example 1. As a result, it was revealed that this polyhydroxyalkanoate is one represented by the chemical formula (16) containing, as the monomer units, 3-hydroxy-5-[(phenylmethyl)sulfanyl]valerate, and 3-hydroxyalkanoates and/or 3-hydroxyalkenoates corresponding to saturated/unsaturated fatty acids having 4 to 12 carbon atoms such as 3-hydroxybutyric acid and 3-hydroxyvaleric acid. The integration of the  1 H-NMR spectra indicated that the polyhydroxyalkanoate contains 3-hydroxy-5-[(phenylmethyl)sulfanyl]valerate by 89.8 mol %.  
       Example 7  
       [0212]    [0212] Pseudomonas cichorii  YN2 was inoculated to 200 mL of M9 medium containing 0.1% of nonanoic acid and 0.1% of 5-[(phenylmethyl)sulfanyl]valeric acid, and cultured with shaking at 125 strokes/min at 30° C. for 48 hours. Then, the cells were collected by centrifugation, washed once with cold methanol, and lyophilized.  
         [0213]    The lyophilized pellet was suspended in 20 mL of chloroform and stirred at 60° C. for 20 hours to extract polyhydroxyalkanoate. The extract was filtered through a membrane filter of a pore size of 0.45 μm and concentrated by a rotary evaporator. The concentrated solution was precipitated with cold methanol. The precipitate was recovered and dried in vacuum to yield 90 mg of polyhydroxyalkanoate.  
         [0214]    The polyhydroxyalkanoate obtained was subjected to NMR analysis under the same conditions as in the Example 1. As a result, it was revealed that this polyhydroxyalkanoate is one represented by the chemical formula (16) containing, as the monomer units, 3-hydroxy-5-[(phenylmethyl)sulfanyl]valerate, and 3-hydroxyalkanoates and/or 3-hydroxyalkenoates corresponding to saturated/unsaturated fatty acids having 4 to 12 carbon atoms such as 3-hydroxybutyric acid and 3-hydroxyvaleric acid. The integration of the  1 H-NMR spectra indicated that the polyhydroxyalkanoate contains 3-hydroxy-5-[(phenylmethyl)sulfanyl]valerate by 29.2 mol %.  
       Example 8  
       [0215]    [0215] Pseudomonas cichorii  YN2 was inoculated to 200 mL of M9 medium containing 0.5% of yeast extract, and 0.1% of 5-[(phenylmethyl)sulfanyl]valeric acid, and cultured with shaking at 125 strokes/min at 30° C. for 48 hours. Then, the cells were collected by centrifugation, washed once with cold methanol, and lyophilized.  
         [0216]    The lyophilized pellet was suspended in 20 mL of chloroform and stirred at 60° C. for 20 hours to extract polyhydroxyalkanoate. The extract was filtered through a membrane filter of a pore size of 0.45 μm and concentrated by a rotary evaporator. The concentrated solution was precipitated with cold methanol. The precipitate was recovered and dried in vacuum to yield 103 mg of polyhydroxyalkanoate.  
         [0217]    The polyhydroxyalkanoate obtained was subjected to NMR analysis under the same conditions as in the Example 1. As a result, it was revealed that this polyhydroxyalkanoate is one represented by the chemical formula (16) containing, as the monomer units, 3-hydroxy-5-[(phenylmethyl)sulfanyl]valerate, and 3-hydroxyalkanoates and/or 3-hydroxyalkenoates corresponding to saturated/unsaturated fatty acids having 4 to 12 carbon atoms such as 3-hydroxybutyric acid and 3-hydroxyvaleric acid. The integration of the  1 H-NMR spectra indicated that the polyhydroxyalkanoate contains 3-hydroxy-5-[(phenylmethyl)sulfanyl]valerate by 96.0 mol %.  
       Example 9  
       [0218]    [0218] Pseudomonas cichorii  YN2 was inoculated to 200 mL of M9 medium containing 0.5% of sodium glutamate and 0.1% of 5-[(phenylmethyl)sulfanyl]valeric acid, and cultured with shaking at 125 strokes/min at 30° C. for 48 hours. Then, the cells were collected by centrifugation, washed once with cold methanol, and lyophilized.  
         [0219]    The lyophilized pellet was suspended in 20 mL of chloroform and stirred at 60° C. for 20 hours to extract polyhydroxyalkanoate. The extract was filtered through a membrane filter of a pore size of 0.45 μm and concentrated by a rotary evaporator. The concentrated solution was precipitated with cold methanol. The precipitate was recovered and dried in vacuum to yield 87 mg of polyhydroxyalkanoate.  
         [0220]    The polyhydroxyalkanoate obtained was subjected to NMR analysis under the same conditions as in the Example 1. As a result, it was revealed that this polyhydroxyalkanoate is one represented by the chemical formula (16) containing, as the monomer units, 3-hydroxy-5-[(phenylmethyl)sulfanyl]valerate, and 3-hydroxyalkanoates and/or 3-hydroxyalkenoates corresponding to saturated/unsaturated fatty acids having 4 to 12 carbon atoms such as 3-hydroxybutyric acid and 3-hydroxyvaleric acid. The integration of the  1 H-NMR spectra indicated that the polyhydroxyalkanoate contains 3-hydroxy-5-[(phenylmethyl)sulfanyl]valerate by 86.4 mol %.  
         [0221]    Table 3 shows the dry weight of the cells, the dry weight of the polymer, the ratio of the polymer to the cells by dry weight, and the amount (mol %) of the 3-hydroxy-5-[(phenylmethyl)sulfanyl]valerate (abbreviated as “3HBzyTV”) unit in the resulting polymer in Examples 1-9.  
                                                         TABLE 3                                   Cell Dry           3HBzyTV           Weight   Polymer Dry   Polymer Weight/   Unit           (mg/L)   Weight (mg/L)   Cell Weight (%)   mol %                                    Example 1   1070   795   74.3   85.9       Example 2   875   690   78.9   95.2       Example 3   1015   820   80.8   96.7       Example 4   1070   805   75.2   83.8       Example 5   710   565   79.6   96.2       Example 6   940   630   67.0   89.8       Example 7   705   450   63.8   29.2       Example 8   815   515   63.2   96.0       Example 9   995   435   43.7   86.4                  
 
       Example 10  
     Process for Producing Polyhydroxyalkanoate Containing 3-Hydroxy-4-[(Phenylmethyl)Sulfanyl]Butyrate Monomer Unit  
       [0222]    [0222] Pseudomonas cichorii  YN2 was inoculated to 200 mL of M9 medium containing 0.5% of yeast extract and 0.1% of 4-[(phenylmethyl)sulfanyl]butyric acid, and cultured at 30° C. with shaking at 125 strokes/min for 48 hours. Then, the cells were collected by centrifugation, washed once with cold methanol, and lyophilized. The weight of the lyophilized cells (dry weight of the cells) was weighed.  
         [0223]    The lyophilized pellet was suspended in 20 mL of chloroform and stirred at 60° C. for 20 hours to extract polyhydroxyalkanoate. The extract was filtered through a membrane filter of a pore size of 0.45 μm and concentrated by a rotary evaporator. The concentrated solution was precipitated with cold methanol. The precipitate was recovered and dried in vacuum to yield 39 mg of polyhydroxyalkanoate.  
         [0224]    The average molecular weight of the resulting PHA was determined by gel permeation chromatography (GPC: TOSOH HLC-8220 (trade name), column: TOSOH TSK-GEL SuperHM-H (trade name), solvent: chloroform, polystyrene equivalent). As a result, the number average molecular weight Mn was 44,500 and the weight average molecular weight Mw was 106,800.  
         [0225]    In order to identify the structure of the PHA obtained, the PHA was subjected to NMR analysis under the following conditions.  
         [0226]    &lt;Spectrometer&gt; FT-NMR: Bruker DPX 400 with spectrometer frequency of 400 MHz for  1 H-NMR.  
         [0227]    &lt;Conditions&gt; 
         [0228]    Nuclear Species:  1 H  
         [0229]    Solvent: CDCl 3    
         [0230]    Reference: TMS/CDCl 3  in capillary  
         [0231]    Temperature: room temperature  
         [0232]    [0232]FIG. 3 shows measured  1 H-NMR spectra and identification results thereof are given in Table 4 below.  
                                   TABLE 4                                   Chemical       Splitting               shift (ppm)   Integration   pattern   Identification                           2.48-2.71   4 H   m   B5, d5           3.68   2 H   m   e5           5.27   1 H   m   c5           7.18   1 H   m   i5           7.25   4 H   m   g5, k5, h5, j5                      
 
         [0233]    The results shown in the Table 4 confirm that this polyhydroxyalkanoate contains as the monomer units, 3-hydroxy-4-[(phenylmethyl)sulfanyl]butyrate, and 3-hydroxyalkanoates and/or 3-hydroxyalkenoates corresponding to saturated/unsaturated fatty acids having 4 to 12 carbon atoms such as 3-hydroxybutyric acid or 3-hydroxyvaleric acid. More specifically, the PHA has a structure represented by the following chemical formula (17):  
                         
 
         [0234]    The integration of the  1 H-NMR spectra indicated that the polyhydroxyalkanoate contains 3-hydroxy-4-[(phenylmethyl)sulfanyl]butyrate by 85.4 mol %.  
       Example 11  
       [0235]    [0235] Pseudomonas cichorii  YN2 was inoculated to 200 mL of M9 medium containing 0.1% of nonanoic acid and 0.1% of 4-[(phenylmethyl)sulfanyl]butyric acid, and cultured at 30° C. with shaking at 125 strokes/min for 48 hours. Then, the cells were collected by centrifugation, washed once with cold methanol, and lyophilized. The weight of the lyophilized cells was measured (dry weight of the cells).  
         [0236]    The lyophilized pellet was suspended in 20 mL of chloroform and stirred at 60° C. for 20 hours to extract polyhydroxyalkanoate. The extract was filtered through a membrane filter of a pore size of 0.45 μm and concentrated by a rotary evaporator. The concentrated solution was precipitated with cold methanol. The precipitate was recovered and dried in vacuum to yield 68 mg of polyhydroxyalkanoate.  
         [0237]    The polyhydroxyalkanoate obtained was subjected to NMR analysis under the same conditions as in the Example 10. As a result, it was revealed that this polyhydroxyalkanoate is one represented by the chemical formula (17) containing a monomer unit of 3-hydroxy-4-[(phenylmethyl)sulfanyl]butyrate, and other monomer units of 3-hydroxyalkanoates and/or 3-hydroxyalkenoates corresponding to saturated/unsaturated fatty acids having 4 to 12 carbon atoms such as 3-hydroxybutyric acid or 3-hydroxyvaleric acid. The integration of the  1 H-NMR spectra indicated that the polyhydroxyalkanoate contains 3-hydroxy-4-[(phenylmethyl)sulfanyl]butyrate by 27.7 mol %.  
       Example 12  
       [0238]    [0238] Pseudomonas cichorii  YN2 was inoculated to 200 mL of M9 medium containing 0.5% of sodium glutamate and 0.1% of 4-[(phenylmethyl)sulfanyl]butyric acid, and cultured at 30° C. with shaking at 125 strokes/min for 48 hours. Then, the cells were collected by centrifugation, washed once with cold methanol, and lyophilized. The weight of the lyophilized cells was weighed (dry weight of the cells).  
         [0239]    The lyophilized pellet was suspended in 20 mL of chloroform and stirred at 60° C. for 20 hours to extract polyhydroxyalkanoate. The extract was filtered through a membrane filter of a pore size of 0.45 μm and concentrated by a rotary evaporator. The concentrated solution was precipitated with cold methanol. The precipitate was recovered and dried in vacuum to yield 72 mg of polyhydroxyalkanoate.  
         [0240]    The polyhydroxyalkanoate obtained was subjected to NMR analysis under the conditions as set forth in the Example 10. As a result, it was revealed that this polyhydroxyalkanoate is one represented by the chemical formula (17). The polyhydroxyalkanoate comprises a monomer unit of 3-hydroxy-4-[(phenylmethyl)sulfanyl]butyrate and other monomer units of 3-hydroxyalkanoates and/or 3-hydroxyalkenoates having 4 to 12 carbon atoms such as 3-hydroxybutyrate and 3-hydroxyvaleric acid. The integration of the  1 H-NMR spectra indicated that the resulting polyhydroxyalkanoate contains 50.3 mol % of 3-hydroxy-4-[(phenylmethyl)sulfanyl]butyrate monomer unit.  
       Example 13  
       [0241]    [0241] Pseudomonas cichorii  YN2 was inoculated to 200 mL of M9 medium containing 0.5% of D-glucose and 0.1% of 4-[(phenylmethyl)sulfanyl]butyric acid, and cultured with shaking at 125 strokes/min at 30° C. for 48 hours. Then, the cells were collected by centrifugation, re-suspended in 200 mL of M9 medium containing 0.5% of D-glucose and 0.1% of 4-[(phenylmethyl)sulfanyl]butyric acid but no nitrogen source (NH 4 Cl), and cultured at 30° C. with shaking at 125 strokes/min for 48 hours. After that, the cells were collected by centrifugation, washed once with cold methanol, and lyophilized. The lyophilized cells were weighed (cell dry weight).  
         [0242]    The lyophilized pellet was suspended in 20 mL of chloroform and stirred at 60° C. for 20 hours to extract polyhydroxyalkanoate. The extract was filtered through a membrane filter of a pore size of 0.45 μm and concentrated by a rotary evaporator. The concentrated solution was precipitated with cold methanol. The precipitate was recovered and dried in vacuum to yield 148 mg of polyhydroxyalkanoate.  
         [0243]    The polyhydroxyalkanoate obtained was subjected to NMR analysis under the conditions as set forth in the Example 10. As a result, it was revealed that this polyhydroxyalkanoate is the polyhydroxyalkanoate that is represented by the chemical formula (17). The polyhydroxyalkanoate comprises a monomer unit of 3-hydroxy-4-[(phenylmethyl)sulfanyl]butyrate and other monomer units of 3-hydroxyalkanoicates and/or 3-hydroxyalkenoates having 4 to 12 carbon atoms such as 3-hydroxybutyrate and 3-hydroxyvalerate. The integration of the  1 H-NMR spectra indicated that the resulting polyhydroxyalkanoate contains 66.7 mol % of the 3-hydroxy-4-[(phenylmethyl)sulfanyl]butyrate monomer unit.  
       Example 14  
       [0244]    [0244] Pseudomonas cichorii  H45 was inoculated to 200 mL of M9 medium containing 0.5% of polypeptone (Wako Pure Chemical Industries, Ltd.) and 0.1% of 5-[(phenylmethyl)sulfanyl]butyric acid, and cultured with shaking at 125 strokes/min at 30° C. for 48 hours. Then, the cells were collected by centrifugation, washed once with cold methanol, and lyophilized. The weight of the lyophilized cells was weighed (dry weight of the cells).  
         [0245]    The lyophilized pellet was suspended in 20 mL of chloroform and stirred at 60° C. for 20 hours to extract polyhydroxyalkanoate. The extract was filtered through a membrane filter of a pore size of 0.45 μm and concentrated by a rotary evaporator. The concentrated solution was precipitated with cold methanol. The precipitate was recovered and dried in vacuum to yield 20 mg of polyhydroxyalkanoate.  
         [0246]    The polyhydroxyalkanoate obtained was subjected to NMR analysis under the conditions as set forth in the Example 10. As a result, it was revealed that this polyhydroxyalkanoate is one represented by the chemical formula (17). The polyhydroxyalkanoate comprises a monomer unit of 3-hydroxy-4-[(phenylmethyl)sulfanyl]butyrate and other monomer units of 3-hydroxyalkanoates and/or 3-hydroxyalkenoates corresponding to saturated/unsaturated fatty acids having 4 to 12 carbon atoms such as 3-hydroxybutyric acid and 3-hydroxyvaleric acid. The integration of the  1 H-NMR spectra indicated that the resulting polyhydroxyalkanoate contains 57.2 mol % of 3-hydroxy-4-[(phenylmethyl)sulfanyl]butyrate monomer unit.  
       Example 15  
       [0247]    [0247] Pseudomonas jessenii  P161 was inoculated to 200 mL of M9 medium containing 0.5% of D-glucose and 0.1% of 5-[(phenylmethyl)sulfanyl]valeric acid, and cultured with shaking at 125 strokes/min at 30° C. for 48 hours. Then, the cells were collected by centrifugation, re-suspended in 200 mL of M9 medium containing 0.5% of D-glucose and 0.1% of 5-[(phenylmethyl)sulfanyl]valeric acid but no nitrogen source (NH 4 Cl), and cultured at 30° C. with shaking at 125 strokes/min for 48 hours. After that, the cells were collected by centrifugation, washed once with cold methanol, and lyophilized. The weight of the lyophilized cells was weighed (the cell dry weight).  
         [0248]    The lyophilized pellet was suspended in 20 mL of chloroform and stirred at 60° C. for 20 hours to extract polyhydroxyalkanoate. The extract was filtered through a membrane filter of a pore size of 0.45 μm and concentrated by a rotary evaporator. The concentrated solution was precipitated with cold methanol. The precipitate was recovered and dried in vacuum to yield 64 mg of polyhydroxyalkanoate.  
         [0249]    The polyhydroxyalkanoate obtained was subjected to NMR analysis under the conditions as set forth in the Example 10. As a result, it was revealed that this polyhydroxyalkanoate is one represented by the chemical formula (17). The polyhydroxyalkanoate comprises a monomer unit of 3-hydroxy-4-[(phenylmethyl)sulfanyl]butyrate and other monomer units of 3-hydroxyalkanoates and/or 3-hydroxyalkenoates corresponding to saturated/unsaturated fatty acids having 4 to 12 carbon atoms such as 3-hydroxybutyric acid and 3-hydroxyvaleric acid. The integration of the  1 H-NMR spectra indicated that the resulting polyhydroxyalkanoate contains 31.6 mol % of 3-hydroxy-4-[(phenylmethyl)sulfanyl]butyrate monomer unit.  
         [0250]    Table 5 shows the dry weight of the cells, the dry weight of the polymer, the dry weight ratio of the polymer to the cells, and the amount (mol %) of 3-hydroxy-4-[(phenylmethyl)sulfanyl]butyrate (abbreviated as “3HBzyTB” units) in the resulting polymer in Examples 10-15.  
                                                         TABLE 5                                   Cell Dry   Polymer Dry       3HBzyTB           Weight   Weight   Polymer Weight/   Unit           (mg/L)   (mg/L)   Cell Weight (%)   mol %                                    Example 10   1040   195   18.8   85.4       Example 11   655   340   51.9   27.7       Example 12   955   360   37.7   50.3       Example 13   1370   740   54.0   66.7       Example 14   580   100   17.2   57.2       Example 15   915   320   35.0   31.6                  
 
       Process for Producing Polyhydroxyalkanoate Containing 3-Hydroxy-5-{[(4-Methylphenyl)methyl]Sulfanyl}Valerate Monomer Unit  
     Example 16  
       [0251]    [0251] Pseudomonas cichorii  YN2 was inoculated to 200 mL of M9 medium containing 0.5% of D-glucose and 0.1% of 5-[[(4-methylphenyl)methyl]sulfanyl]valeric acid, and cultured with shaking at 125 strokes/min at 30° C. for 48 hours. Then, the cells were collected by centrifugation, re-suspended in 200 mL of M9 medium containing 0.5% of D-glucose and 0.1% of 5-[[4-methylphenyl)methyl]sulfanyl]valeric acid but no nitrogen source (NH 4 Cl), and cultured at 30° C. with shaking at 125 strokes/min for 48 hours. After that, the cells were collected by centrifugation, washed once with cold methanol, and lyophilized.  
         [0252]    The lyophilized pellet was suspended in 20 mL of chloroform and stirred at 60° C. for 20 hours to extract polyhydroxyalkanoate. The extract was filtered through a membrane filter of a pore size of 0.45 μm and concentrated by a rotary evaporator. The concentrated solution was precipitated with cold methanol. The precipitate was recovered and dried in vacuum to yield 96 mg of polyhydroxyalkanoate.  
         [0253]    The polyhydroxyalkanoate obtained was subjected to NMR analysis under the conditions as set forth in Example 10. As a result, it was revealed that this polyhydroxyalkanoate is one represented by the chemical formula (18). The polyhydroxyalkanoate comprises a monomer unit of 3-hydroxy-5-[[(4-methylphenyl)methyl]sulfanyl]valerate and other monomer units of 3-hydroxyalkanoates and/or 3-hydroxyalkenoates corresponding to saturated/unsaturated fatty acids having 4 to 12 carbon atoms such as 3-hydroxybutyric acid and 3-hydroxyvaleric acid. The integration of the  1 H-NMR spectra indicated that the resulting polyhydroxyalkanoate contains 41.0 mol % of 3-hydroxy-5-{[(4-methylphenyl)methyl]sulfanyl}valerate monomer unit.  
                         
 
         [0254]    The molecular weight of the resulting polyhydroxyalkanoate was determined by gel permeation chromatography (GPC; TOSOH HLC-8220, column; TOSOH TSK-GEL SuperHM-H, solvent; chloroform, polystyrene equivalent). As a result, Mn was 21,500 and Mw was 83,200.  
       Example 17  
       [0255]    [0255] Pseudomonas cichorii  H45 was inoculated to 200 mL of M9 medium containing 0.5% of D-glucose and 0.1% of 5-[[(4-methylphenyl)methyl]sulfanyl]valeric acid, and cultured with shaking at 125 strokes/min at 30° C. for 48 hours. Then, the cells were collected by centrifugation, re-suspended in 200 mL of M9 medium containing 0.5% of D-glucose and 0.1% of 5-[[4-methylphenyl)methyl]sulfanyl]valeric acid but no nitrogen source (NH 4 Cl), and cultured at 30° C. with shaking at 125 strokes/min for 48 hours. After that, the cells were collected by centrifugation, washed once with cold methanol, and lyophilized.  
         [0256]    The lyophilized pellet was suspended in 20 mL of chloroform and stirred at 60° C. for 20 hours to extract polyhydroxyalkanoate. The extract was filtered through a membrane filter of a pore size of 0.45 μm and concentrated by a rotary evaporator. The concentrated solution was precipitated with cold methanol. The precipitate was recovered and dried in vacuum to yield 82 mg of polyhydroxyalkanoate.  
         [0257]    The polyhydroxyalkanoate obtained was subjected to NMR analysis under the conditions as set forth in Example 10. As a result, it was revealed that this polyhydroxyalkanoate is one represented by the chemical formula (18). The polyhydroxyalkanoate comprises a monomer unit of 3-hydroxy-5-[[(4-methylphenyl)methyl]sulfanyl]valerate and other monomer units of 3-hydroxyalkanoates and/or 3-hydroxyalkenoates corresponding to saturated/unsaturated fatty acids having 4 to 12 carbon atoms such as 3-hydroxybutyric acid and 3-hydroxyvaleric acid. The integration of the  1 H-NMR spectra indicated that the resulting polyhydroxyalkanoate contains 56.2 mol % of 3-hydroxy-5-[[(4-methylphenyl)methyl]sulfanyl]valerate monomer unit.  
       Example 18  
       [0258]    [0258] Pseudomonas jessenii  P161 was inoculated to 200 mL of M9 medium containing 0.5% of D-glucose and 0.1% of 5-[[(4-methylphenyl)methyl]sulfanyl]valeric acid, and cultured with shaking at 125 strokes/min at 30° C. for 48 hours. Then, the cells were collected by centrifugation, re-suspended in 200 mL of M9 medium containing 0.5% of D-glucose and 0.1% of 5-[[4-methylphenyl)methyl]sulfanyl]valeric acid but no nitrogen source (NH 4 Cl), and cultured at 30° C. with shaking at 125 strokes/min for 48 hours. After that, the cells were collected by centrifugation, washed once with cold methanol, and lyophilized.  
         [0259]    The lyophilized pellet was suspended in 20 mL of chloroform and stirred at 60° C. for 20 hours to extract polyhydroxyalkanoate. The extract was filtered through a membrane filter of a pore size of 0.45 μm and concentrated by a rotary evaporator. The concentrated solution was precipitated with cold methanol. The precipitate was recovered and dried in vacuum to yield 75 mg of polyhydroxyalkanoate.  
         [0260]    The polyhydroxyalkanoate obtained was subjected to NMR analysis under the conditions as set forth in Example 10. As a result, it was revealed that this polyhydroxyalkanoate is one represented by the chemical formula (18). The polyhydroxyalkanoate comprises a monomer unit of 3-hydroxy-5-[[(4-methylphenyl)methyl]sulfanyl]valerate and other monomer units of 3-hydroxyalkanoates and/or 3-hydroxyalkenoates corresponding to saturated/unsaturated fatty acids having 4 to 12 carbon atoms such as 3-hydroxybutyric acid and 3-hydroxyvaleric acid. The integration of the  1 H-NMR spectra indicated that the resulting polyhydroxyalkanoate contains 38.8 mol % of 3-hydroxy-5-[[(4-methylphenyl)methyl]sulfanyl}valerate monomer unit.  
         [0261]    Table 6 shows the dry weight of the cells, the dry weight of the polymer, the dry weight ratio of the polymer to the cells, and the amount (mol %) of the 3-hydroxy-3-hydroxy-5-{[(4-methylphenyl)methyl]sulfanyl}valerate (abbreviated as “3HMBzyTV” in the resulting polymer in Examples 16-18.  
                                                         TABLE 6                                   Cell Dry   Polymer Dry       3HMBzyTV           Weight   Weight   Polymer Weight/   Unit           (mg/L)   (mg/L)   Cell Weight (%)   mol %                                    Example 16   805   481   59.8   41.0       Example 17   625   408   65.3   56.2       Example 18   710   377   53.1   38.8                  
 
       Example 19  
       [0262]    [0262] Pseudomonas cichorii  YN2 was inoculated to 200 mL of M9 medium containing 0.5% of polypeptone (Wako Pure Chemical Industries, Ltd.) and 0.1% of 5-{[(4-fluorophenyl)methyl]sulfanyl}valeric acid, and cultured with shaking at 125 strokes/min at 30° C. for 48 hours. Then, the cells were collected by centrifugation, washed once with cold methanol, and lyophilized. The weight of the lyophilized cells was weighed (dry weight of the cells).  
         [0263]    The lyophilized pellet was suspended in 20 mL of chloroform and stirred at 60° C. for 20 hours to extract polyhydroxyalkanoate. The extract was filtered through a membrane filter of a pore size of 0.45 μm and concentrated by a rotary evaporator. The concentrated solution was precipitated with cold methanol. The sole precipitate was recovered and dried in vacuum to yield 106 mg of polyhydroxyalkanoate.  
         [0264]    The average molecular weight of the resulting PHA was determined by gel permeation chromatography (GPC; TOSOH HLC-8220, column; TOSOH TSK-GEL SuperHM-H, solvent; chloroform, polystyrene equivalent). As a result, the number average molecular weight Mn was 32,000 and the weight average molecular weight Mw was 96,000.  
         [0265]    In order to identify the structure of the PHA obtained, the PHA was subjected to NMR analysis under the following conditions.  
         [0266]    &lt;Spectrometer&gt;FT-NMR: Bruker DPX 400 with spectrometer frequencies of 400 MHz for  1 H-NMR and 100 MHz for  13 C-NMR.  
         [0267]    &lt;Conditions&gt; 
         [0268]    Nuclear Species:  1 H,  13 C  
         [0269]    Solvent: CDCl 3    
         [0270]    Temperature: room temperature  
         [0271]    [0271]FIG. 4 shows measured  1 H-NMR spectra. Identification results thereof are given in Table 7 below. FIG. 5 shows measured  13 C-NMR spectra. Identification results thereof are given in Table 8 below.  
                                   TABLE 7                                   Chemical       Splitting               shifts (ppm)   Integration   patterns   Identification                           1.83   2 H   qurt   d1           2.35-2.58   4 H   m   b1, e1           3.64   2 H   s   f1           5.20   1 H   m   c1           6.92-6.98   2 H   m   j1, k1           7.23-7.26   2 H   m   h1, l1                      
 
         [0272]    [0272]                           TABLE 8                                   Chemical shifts               (ppm)   Identification                           26.7   d1           33.2   e1           35.3   f1           38.6   b1           69.7   c1           115.1 &amp; 115.4   i1, k1           130.3 &amp; 130.3   h1, l1           133.7    g1           160.6 &amp; 163.0   i1           168.9    a1                        
         [0273]    From the results shown in the Tables 7 and 8, the PHA comprises a monomer unit of 3-hydroxy-5-{[(4-fluorophenyl)methyl]sulfanyl}valerate, and other monomer units of 3-hydroxyalkanoates and/or 3-hydroxyalkenoates having 4 to 12 carbon atoms such as 3-hydroxybutyric acid and 3-hydroxyvaleric acid. More specifically, the PHA has a structure represented by the following chemical formula (19):  
                         
 
         [0274]    The integration of the  1 H-NMR spectra indicated that the resulting PHA contains 76.7 mol % of 3-hydroxy-5-{[(4-fluorophenyl)methyl]sulfanyl}valerate monomer unit.  
       Example 20  
       [0275]    [0275] Pseudomonas cichorii  YN2 was inoculated to 200 mL of M9 medium that contains 0.1% of nonanoic acid and 0.1% of 5-{[(4-fluorophenyl)methyl]sulfanyl}valeric acid and cultured with shaking at 125 strokes/min at 30° C. for 48 hours. Then, the cells were collected by centrifugation, washed once with cold methanol, and lyophilized. The weight of the lyophilized cells was weighed (dry weight of the cells).  
         [0276]    The lyophilized pellet was suspended in 20 mL of chloroform and stirred at 60° C. for 20 hours to extract polyhydroxyalkanoate. The extract was filtered through a membrane filter of a pore size of 0.45 μm and concentrated by a rotary evaporator. The concentrated solution was precipitated with cold methanol. The precipitate was recovered and dried in vacuum to yield 89 mg of polyhydroxyalkanoate.  
         [0277]    The PHA obtained was subjected to NMR analysis and average molecular weight determination under the conditions as in Example 19. From the results of the NMR analysis, it was revealed that the PHA in this example comprises a monomer unit of 3-hydroxy-5-{[(4-fluorophenyl)methyl]sulfanyl}valerate and other monomer units of 3-hydroxyalkanoates and/or 3-hydroxyalkenoates having 4 to 12 carbon atoms such as 3-hydroxybutyrate and 3-hydroxyvalerate to confirm that it has a constitution represented by the chemical formula (19). The integration of the  1 H-NMR spectra indicated that the PHA of this example contains 27.0 mol % of 3-hydroxy-5-{[(4-fluorophenyl)methyl]sulfanyl}valerate monomer unit.  
       Example 21  
       [0278]    [0278] Pseudomonas cichorii  YN2 was inoculated to 200 mL of M9 medium containing 0.5% of yeast extract (DIFCO) and 0.1% of 5-{[(4-fluorophenyl)methyl]sulfanyl}valeric acid, and cultured with shaking at 125 strokes/min at 30° C. for 48 hours. Then, the cells were collected by centrifugation, washed once with cold methanol, and lyophilized. The weight of the lyophilized cells was weighed (dry weight of the cells).  
         [0279]    The lyophilized pellet was suspended in 20 mL of chloroform and stirred at 60° C. for 20 hours to extract polyhydroxyalkanoate. The extract was filtered through a membrane filter of a pore size of 0.45 μm and concentrated by a rotary evaporator. The concentrated solution was precipitated with cold methanol. The precipitate was recovered and dried in vacuum to yield 69 mg of polyhydroxyalkanoate in this Example.  
         [0280]    The PHA obtained was subjected to NMR analysis and average molecular weight determination under the conditions as set forth in the Example 19. From the results of the NMR analysis, it was revealed that the PHA in this example comprises a monomer unit of 3-hydroxy-5-{[(4-fluorophenyl)methyl]sulfanyl}valerate and other monomer units of 3-hydroxyalkanoates and/or 3-hydroxyalkenoates having 4 to 12 carbon atoms such as 3-hydroxybutyrate and 3-hydroxyvalerate to confirm that it has a constitution represented by the above chemical formula (19). The integration of the  1 H-NMR spectra indicated that the PHA of this example contains 76.7 mol % of 3-hydroxy-5-{[(4-fluorophenyl)methyl]sulfanyl}valerate monomer unit.  
       Example 22  
       [0281]    [0281] Pseudomonas cichorii  YN2 was inoculated to 200 mL of M9 medium containing 0.5% of sodium glutamate and 0.1% of 5-{[(4-fluorophenyl)methyl]sulfanyl}valeric acid, and cultured with shaking at 125 strokes/min at 30° C. for 48 hours. Then, the cells were collected by centrifugation, washed once with cold methanol, and lyophilized. The weight of the lyophilized cells was weighed (dry weight of the cells).  
         [0282]    The lyophilized pellet was suspended in 20 mL of chloroform and stirred at 60° C. for 20 hours to extract polyhydroxyalkanoate. The extract was filtered through a membrane filter of a pore size of 0.45 μm and concentrated by a rotary evaporator. The concentrated solution was precipitated with cold methanol. The precipitate was recovered and dried in vacuum to yield 68 mg of polyhydroxyalkanoate in this Example.  
         [0283]    The PHA obtained was subjected to NMR analysis and average molecular weight determination under the same conditions as set forth in Example 19. From the results of the NMR analysis, it was revealed that the PHA in this example comprises a monomer unit of 3-hydroxy-5-{[(4-fluorophenyl)methyl]sulfanyl}valerate and other monomer units of 3-hydroxyalkanoates and/or 3-hydroxyalkenoates having 4 to 12 carbon atoms, such as 3-hydroxybutyrate and 3-hydroxyvalerate, confirming that it has a constitution represented by the chemical formula (19). The integration of the  1 H-NMR spectra indicated that the PHA of this example contains 90.3 mol % of 3-hydroxy-5-{[(4-fluorophenyl)methyl]sulfanyl}valerate monomer unit.  
       Example 23  
       [0284]    [0284] Pseudomonas cichorii  YN2 was inoculated to 200 mL of M9 medium containing 0.5% of D-glucose and 0.1% of 5-{[(4-fluorophenyl)methyl]sulfanyl}valeric acid, and cultured with shaking at 125 strokes/min at 30° C. for 48 hours. Then, the cells were collected by centrifugation, re-suspended in 200 mL of M9 medium containing 0.5% of D-glucose and 0.1% of 5-{[(4-fluorophenyl)methyl]sulfanyl}valeric acid but no nitrogen source (NH 4 Cl), and cultured at 30° C. with shaking at 125 strokes/min for 48 hours. After that, the cells were collected by centrifugation, washed once with cold methanol, and lyophilized. The weight of the lyophilized cells was weighed (dry weight of the cells).  
         [0285]    The lyophilized pellet was suspended in 20 mL of chloroform and stirred at 60° C. for 20 hours to extract polyhydroxyalkanoate. The extract was filtered through a membrane filter of a pore size of 0.45 μm and concentrated by a rotary evaporator. The concentrated solution was precipitated with cold methanol. The precipitate was recovered and dried in vacuum to yield 164 mg of polyhydroxyalkanoate.  
         [0286]    The PHA obtained was subjected to NMR analysis, and the average molecular weight determination under the conditions as set forth in Example 19. The results of the NMR analysis show that the PHA in this example comprises a monomer unit of 3-hydroxy-5-{[(4-fluorophenyl)methyl]sulfanyl}valerate and other monomer units of 3-hydroxyalkanoates and/or 3-hydroxyalkenoates having 4 to 12 carbon atoms, such as 3-hydroxybutyrate and 3-hydroxyvalerate to confirm that it has a constitution represented by the chemical formula (19). The integration of the  1 H-NMR spectra indicated that the PHA of this example contains 85.9 mol % of 3-hydroxy-5-{1[(4-fluorophenyl)methyl]sulfanyl}valerate monomer unit.  
       Example 24  
       [0287]    [0287] Pseudomonas cichorii  H45 was inoculated to 200 mL of M9 medium containing 0.5% of D-glucose and 0.1% of 5-{[(4-fluorophenyl)methyl]sulfanyl}valeric acid and cultured with shaking at 125 strokes/min at 30° C. for 48 hours. Then, the cells were collected by centrifugation, re-suspended in 200 mL of M9 medium containing 0.5% of D-glucose and 0.1% of 5-{[(4-fluorophenyl)methyl]sulfanyl}valeric acid but no nitrogen source (NH 4 Cl), and cultured at 30° C. with shaking at 125 strokes/min for 48 hours. After that, the cells were collected by centrifugation, washed once with cold methanol, and lyophilized. The weight of the lyophilized cells was weighed (dry weight of the cells).  
         [0288]    The lyophilized pellet was suspended in 20 mL of chloroform and stirred at 60° C. for 20 hours to extract polyhydroxyalkanoate. The extract was filtered through a membrane filter of a pore size of 0.45 μm and concentrated by a rotary evaporator. The concentrated solution was precipitated with cold methanol. The precipitate was recovered and dried in vacuum to yield 138 mg of polyhydroxyalkanoate.  
         [0289]    The PHA obtained was subjected to NMR analysis, and the average molecular weight determination under the conditions as set forth in Example 19. The results of the NMR analysis show that the PHA in this example comprises a monomer unit of 3-hydroxy-5-{[(4-fluorophenyl)methyl]sulfanyl}valerate and other monomer units of 3-hydroxyalkanoates and/or 3-hydroxyalkenoates having 4 to 12 carbon atoms, such as 3-hydroxybutyrate and 3-hydroxyvalerate to confirm that it has a constitution represented by the chemical formula (19). The integration of the  1 H-NMR spectra indicated that the PHA of this example contains 90.7 mol % of 3-hydroxy-5-{[(4-fluorophenyl)methyl]sulfanyl}valerate monomer unit.  
       Example 25  
       [0290]    [0290] Pseudomonas jessenii  P161 was inoculated to 200 mL of M9 medium containing 0.5% of D-glucose and 0.1% of 5-{[(4-fluorophenyl)methyl]sulfanyl}valeric acid, and cultured with shaking at 125 strokes/min at 30° C. for 48 hours. Then, the cells were collected by centrifugation, re-suspended in 200 mL of M9 medium containing 0.5% of D-glucose and 0.1% of 5-{[(4-fluorophenyl)methyl]sulfanyl}valeric acid but no nitrogen source (NH 4 Cl), and cultured at 30° C. with shaking at 125 strokes/min for 48 hours. After that, the cells were collected by centrifugation, washed once with cold methanol, and lyophilized. The weight of the lyophilized cells was weighed (the cell dry weight).  
         [0291]    The lyophilized pellet was suspended in 20 mL of chloroform and stirred at 60° C. for 20 hours to extract polyhydroxyalkanoate. The extract was filtered through a membrane filter of a pore size of 0.45 μm and concentrated by a rotary evaporator. The concentrated solution was precipitated with cold methanol. The precipitate was recovered and dried in vacuum to yield 138 mg of polyhydroxyalkanoate.  
         [0292]    The PHA obtained was subjected to NMR analysis, and the average molecular weight determination under the conditions as set forth in Example 19. The results of the NMR analysis show that the PHA in this example comprises a monomer unit of 3-hydroxy-5-{[(4-fluorophenyl)methyl]sulfanyl}valerate and other monomer units of 3-hydroxyalkanoates and/or 3-hydroxyalkenoates having 4 to 12 carbon atoms, such as 3-hydroxybutyrate or 3-hydroxyvalerate to confirm that it has a constitution represented by the chemical formula (19). The integration of the  1 H-NMR spectra indicated that the PHA of this example contains 88.5 mol % of 3-hydroxy-5-{[(4-fluorophenyl)methyl]sulfanyl}valerate monomer unit.  
       Example 26  
       [0293]    [0293] Pseudomonas cichorii  YN2 was inoculated to 200 mL of M9 medium containing 0.5% of polypeptone (Wako Pure Chemical Industries, Ltd.) and 0.1% of 5-{[(4-fluorophenyl)methyl]sulfanyl}valeric acid and cultured with shaking at 125 strokes/min at 30° C. for 48 hours. Then, the cells were collected by centrifugation, re-suspended in 200 mL of M9 medium containing 0.5% of sodium pyruvate and 0.1% of 5-{[(4-fluorophenyl)methyl]sulfanyl}valeric acid but no nitrogen source (NH 4 Cl), and cultured at 30° C. with shaking at 125 strokes/min for 48 hours. After that, the cells were collected by centrifugation, washed once with cold methanol, and lyophilized. The weight of the lyophilized cells was weighed (the cell dry weight).  
         [0294]    The lyophilized pellet was suspended in 20 mL of chloroform and stirred at 60° C. for 20 hours to extract polyhydroxyalkanoate. The extract was filtered through a membrane filter of a pore size of 0.45 μm and concentrated by a rotary evaporator. The concentrated solution was precipitated with cold methanol. The precipitate was recovered and dried in vacuum to yield 125 mg of polyhydroxyalkanoate.  
         [0295]    The PHA obtained was subjected to NMR analysis, and the average molecular weight determination under the conditions as set forth in Example 19. The results of the NMR analysis show that the PHA in this example comprises a monomer unit of 3-hydroxy-5-{[(4-fluorophenyl)methyl]sulfanyl}valerate and other monomer units of 3-hydroxyalkanoates and/or 3-hydroxyalkenoates having 4 to 12 carbon atoms, such as 3-hydroxybutyrate or 3-hydroxyvalerate to confirm that it has a constitution represented by the chemical formula (19). The integration of the 1H-NMR spectra indicated that the PHA of this example contains 89.5 mol % of 3-hydroxy-5-{[(4-fluorophenyl)methyl]sulfanyl}valerate monomer unit.  
       Example 27  
       [0296]    [0296] Pseudomonas cichorii  H45 was inoculated to 200 mL of M9 medium containing 0.5% of polypeptone (Wako Pure Chemical Industries, Ltd.) and 0.1% of 5-{[(4-fluorophenyl)methyl]sulfanyl}valeric acid and cultured with shaking at 125 strokes/min at 30° C. for 48 hours. Then, the cells were collected by centrifugation, re-suspended in 200 mL of M9 medium containing 0.5% of sodium pyruvate and 0.1% of 5-{[(4-fluorophenyl)methyl]sulfanyl}valeric acid but no nitrogen source (NH 4 Cl), and cultured at 30° C. with shaking at 125 strokes/min for 48 hours. After that, the cells were collected by centrifugation, washed once with cold methanol, and lyophilized. The weight of the lyophilized cells was weighed (the cell dry weight).  
         [0297]    The lyophilized pellet was suspended in 20 mL of chloroform and stirred at 60° C. for 20 hours to extract polyhydroxyalkanoate. The extract was filtered through a membrane filter of a pore size of 0.45 μm and concentrated by a rotary evaporator. The concentrated solution was precipitated with cold methanol. The precipitate was recovered and dried in vacuum to yield 154 mg of polyhydroxyalkanoate.  
         [0298]    The PHA obtained was subjected to NMR analysis, and the average molecular weight determination under the conditions as set forth in Example 19. The results of the NMR analysis show that the PHA in this example comprises a monomer unit of 3-hydroxy-5-{[(4-fluorophenyl)methyl]sulfanyl}valerate and other monomer units of 3-hydroxyalkanoates and/or 3-hydroxyalkenoates having 4 to 12 carbon atoms, such as 3-hydroxybutyrate or 3-hydroxyvalerate to confirm that it has a constitution represented by the chemical formula (19). The integration of the  1 H-NMR spectra indicated that the PHA of this example contains 97.9 mol % of 3-hydroxy-5-{[(4-fluorophenyl)methyl]sulfanyl}valerate monomer unit.  
       Example 28  
       [0299]    [0299] Pseudomonas jessenii  P161 was inoculated to 200 mL of M9 medium containing 0.5% of polypeptone (Wako Pure Chemical Industries, Ltd.) and 0.1% of 5-{[(4-fluorophenyl)methyl]sulfanyl}valeric acid and cultured with shaking at 125 strokes/min at 30° C. for 48 hours. Then, the cells were collected by centrifugation, re-suspended in 200 mL of M9 medium containing 0.5% of sodium pyruvate and 0.1% of 5-{[(4-fluorophenyl)methyl]sulfanyl}valeric acid but no nitrogen source (NH 4 Cl), and cultured at 30° C. with shaking at 125 strokes/min for 48 hours. After that, the cells were collected by centrifugation, washed once with cold methanol, and lyophilized. The weight of the lyophilized cells was weighed (the cell dry weight).  
         [0300]    The lyophilized pellet was suspended in 20 mL of chloroform and stirred at 60° C. for 20 hours to extract polyhydroxyalkanoate. The extract was filtered through a membrane filter of a pore size of 0.45 μm and concentrated by a rotary evaporator. The concentrated solution was precipitated with cold methanol. The precipitate was recovered and dried in vacuum to yield 158 mg of polyhydroxyalkanoate.  
         [0301]    The PHA obtained was subjected to NMR analysis, and the average molecular weight determination under the conditions as set forth in Example 19. The results of the NMR analysis show that the PHA in this example comprises a monomer unit of 3-hydroxy-5-{[(4-fluorophenyl)methyl]sulfanyl}valerate and other monomer units of 3-hydroxyalkanoates and/or 3-hydroxyalkenoates having 4 to 12 carbon atoms, such as 3-hydroxybutyrate or 3-hydroxyvalerate to confirm that it has a constitution represented by the chemical formula (19). The integration of the  1 H-NMR spectra indicated that the PHA of this example contains 91.6 mol % of 3-hydroxy-5-{[(4-fluorophenyl)methyl]sulfanyl}valerate monomer unit.  
         [0302]    Table 9 shows the dry weight of the cells, the dry weight of the polymer, the dry weight ratio of the polymer to the cells, and the amount in mol % of the 3-hydroxy-5-{[(4-fluorophenyl)methyl]sulfanyl}valerate unit (abbreviated as “3HFBzyTV”) in the resulting PHA polymer in Examples 19 to 28.  
                                                         TABLE 9                                   Cell Dry   Polymer Dry       3HFBzyTV           Weight   Weight   Polymer Weight/   Unit           (mg/L)   (mg/L)   Cell Weight (%)   mol %                                    Example 19   945   530   56.1   76.7       Example 20   680   445   65.4   27.0       Example 21   915   345   37.7   76.7       Example 22   740   340   45.9   90.3       Example 23   1120   820   73.2   85.9       Example 24   940   690   73.4   90.7       Example 25   955   690   72.3   88.5       Example 26   1015   625   61.6   89.5       Example 27   1125   770   68.4   97.9       Example 28   1215   790   65.0   91.6                  
 
       Process for Producing Polyhydroxyalkanoate Comprising 3-Hydroxy-4-{[(4-Fluorophenyl)Methyl]Sulfanyl}Butyric Acid Monomer Unit  
     Example 29  
       [0303]    [0303] Pseudomonas cichorii  YN2 was inoculated to 200 mL of M9 medium containing 0.5% of yeast extract (DIFCO) and 0.1% of 4-{[(4-fluorophenyl)methyl]sulfanyl}butyric acid, and cultured with shaking at 125 strokes/min at 30° C. for 48 hours. Then, the cells were collected by centrifugation, washed once with cold methanol, and lyophilized. The weight of the lyophilized cells was weighed (dry weight of the cells).  
         [0304]    The lyophilized pellet was suspended in 20 mL of chloroform and stirred at 60° C. for 20 hours to extract polyhydroxyalkanoate. The extract was filtered through a membrane filter of a pore size of 0.45 μm and concentrated by a rotary evaporator. The concentrated solution was precipitated with cold methanol. The precipitate was recovered and dried in vacuum to yield 41 mg of polyhydroxyalkanoate.  
         [0305]    The average molecular weight of the resulting PHA was determined by gel permeation chromatography (GPC; TOSOH HLC-8220, column; TOSOH TSK-GEL SuperHM-H, solvent; chloroform, polystyrene equivalent). As a result, the number average molecular weight Mn was 15,300 and the weight average molecular weight Mw was 37,100.  
         [0306]    In order to identify the structure of the PHA obtained, the PHA was subjected to NMR analysis under the following conditions.  
         [0307]    &lt;Spectrometer&gt; FT-NMR: Bruker DPX 400 with spectrometer frequencies of 400 MHz for  1 1H-NMR.  
         [0308]    &lt;Conditions&gt; 
         [0309]    Nuclear Species:  1 H  
         [0310]    Solvent: CDCl 3    
         [0311]    Reference: TMS/CDCl 3  in capillary  
         [0312]    Temperature: room temperature  
         [0313]    [0313]FIG. 6 shows measured  1 H-NMR spectra. Identification results thereof are given in Table 10 below.  
                                   TABLE 10                                   Chemical       Splitting               shifts (ppm)   Integration   patterns   Identification                           2.40-2.72   4 H   m   b1, d1           3.65   2 H   m   e1           5.27   1 H   m   c1           6.95   2 H   m   h1, j1           7.23   2 H   m   g1, k1                      
 
         [0314]    From the results shown in the Table 10, the subject PHA comprises a monomer unit of 3-hydroxy-4-{[(4-fluorophenyl)methyl]sulfanyl}butyrate and other monomer units of 3-hydroxyalkanoates and/or 3-hydroxyalkenoates having 4 to 12 carbon atoms, such as 3-hydroxybutyrate or 3-hydroxyvalerate. More specifically, the PHA has a structure represented by the following chemical formula (20).  
                         
 
         [0315]    The integration of the  1 H-NMR spectra indicated that the resulting PHA contains 89.8 mol % of 3-hydroxy-4-{[(4-fluorophenyl)methyl]sulfanyl}butyrate monomer unit.  
       Example 30  
       [0316]    [0316] Pseudomonas cichorii  YN2 was inoculated to 200 mL of M9 medium containing 0.1% of nonanoic acid and 0.1% of 4-{[(4-fluorophenyl)methyl]sulfanyl}butyric acid and cultured with shaking at 125 strokes/min at 30° C. for 48 hours. Then the cells were collected by centrifugation, washed once with cold methanol, and lyophilized and weighed to determine dried cell weight.  
         [0317]    The lyophilized pellet was suspended in 20 mL of chloroform and stirred at 60° C. for 20 hours to extract polyhydroxyalkanoate. The extract was filtered through a membrane filter of a pore size of 0.45 μm and concentrated by a rotary evaporator. The concentrated solution was precipitated with cold methanol. The precipitate was recovered and dried in vacuum to yield 45 mg of polyhydroxyalkanoate.  
         [0318]    The PHA obtained was subjected to NMR analysis, and the average molecular weight determination under the conditions as set forth in Example 29. The results of the NMR analysis show that the PHA in this example comprises a monomer unit of 3-hydroxy-4-{[(4-fluorophenyl)methyl]sulfanyl}butyrate and other monomer units of 3-hydroxyalkanoates and/or 3-hydroxyalkenoates having 4 to 12 carbon atoms, such as 3-hydroxybutyrate or 3-hydroxyvalerate to confirm that it has a constitution represented by the chemical formula (20). The integration of the  1 H-NMR spectra indicated that the PHA of this example contains 10.6 mol % of 3-hydroxy-4-{[(4-fluorophenyl)methyl]sulfanyl}butyrate monomer unit.  
       Example 31  
       [0319]    [0319] Pseudomonas cichorii  YN2 was inoculated to 200 mL of M9 medium containing 0.5% of sodium glutamate and 0.1% of 4-{[(4-fluorophenyl)methyl]sulfanyl}butyric acid and cultured with shaking at 125 strokes/min at 30° C. for 48 hours. Then, the cells were collected by centrifugation, washed once with cold methanol, lyophilized and weighed.  
         [0320]    The lyophilized pellet was suspended in 20 mL of chloroform and stirred at 60° C. for 20 hours to extract polyhydroxyalkanoate. The extract was filtered through a membrane filter of a pore size of 0.45 μm and concentrated by a rotary evaporator. The concentrated solution was precipitated with cold methanol. The precipitate was recovered and dried in vacuum to yield 11 mg of polyhydroxyalkanoate.  
         [0321]    The PHA obtained was subjected to NMR analysis, and the average molecular weight determination under the conditions as set forth in Example 29. The results of the NMR analysis show that the PHA in this example comprises a monomer unit of 3-hydroxy-4-{[(4-fluorophenyl)methyl]sulfanyl}butyrate and other monomer units of 3-hydroxyalkanoates and/or 3-hydroxyalkenoates having 4 to 12 carbon atoms, such as 3-hydroxybutyrate or 3-hydroxyvalerate to confirm that it has a constitution represented by the chemical formula (20). The integration of the  1 H-NMR spectra indicated that the PHA of this example contains 84.1 mol % of 3-hydroxy-4-{[(4-fluorophenyl)methyl]sulfanyl}butyrate monomer unit.  
       Example 32  
       [0322]    [0322] Pseudomonas cichorii  YN2 was inoculated to 200 mL of M9 medium containing 0.5% of D-glucose and 0.1% of 4-{[(4-fluorophenyl)methyl]sulfanyl}butyric acid and cultured with shaking at 125 strokes/min at 30° C. for 48 hours. Then, the cells were collected by centrifugation, re-suspended in 200 mL of M9 medium containing 0.5% of D-glucose and 0.1% of 4-{[[4-fluoromethyl]phenyl]methyl}sulfanyl]butyric acid but no nitrogen source (NH 4 Cl), and cultured at 30° C. with shaking at 125 strokes/min for 48 hours. After that, the cells were collected by centrifugation, washed once with cold methanol, lyophilized and weighed as the dry cell weight.  
         [0323]    The lyophilized pellet was suspended in 20 mL of chloroform and stirred at 60° C. for 20 hours to extract polyhydroxyalkanoate. The extract was filtered through a membrane filter of a pore size of 0.45 μm and concentrated by a rotary evaporator. The concentrated solution was precipitated with cold methanol. The precipitate was recovered and dried in vacuum to yield 153 mg of polyhydroxyalkanoate.  
         [0324]    The PHA obtained was subjected to NMR analysis, and the average molecular weight determination under the conditions as set forth in Example 29. The results of the NMR analysis show that the PHA in this example comprises a monomer unit of 3-hydroxy-4-{[(4-fluorophenyl)methyl]sulfanyl}butyrate and other monomer units of 3-hydroxyalkanoates and/or 3-hydroxyalkenoates having 4 to 12 carbon atoms, such as 3-hydroxybutyrate or 3-hydroxyvalerate to confirm that it has a constitution represented by the chemical formula (20). The integration of the  1 H-NMR spectra indicated that the PHA of this example contains 68.5 mol % of 3-hydroxy-4-{[(4-fluorophenyl)methyl]sulfanyl}butyrate monomer unit.  
       Example 33  
       [0325]    [0325] Pseudomonas cichorii  H45 was inoculated to 200 mL of M9 medium containing 0.5% of polypeptone (Wako Pure Chemical Industries, Ltd.) and 0.1% of 4-{[(4-fluorophenyl)methyl]sulfanyl}butyric acid, and cultured with shaking at 125 strokes/min at 30° C. for 48 hours. Then, the cells were collected by centrifugation, re-suspended in 200 mL of M9 medium containing 0.5% of sodium pyruvate and 0.1% of 4-{[(4-fluorophenyl)methyl]sulfanyl}butyric acid but no nitrogen source (NH 4 Cl), and cultured at 30° C. with shaking at 125 strokes/min for 48 hours. After that, the cells were collected by centrifugation, washed once with cold methanol, and lyophilized. The weight of the lyophilized cells was weighed (the cell dry weight).  
         [0326]    The lyophilized pellet was suspended in 20 mL of chloroform and stirred at 60° C. for 20 hours to extract polyhydroxyalkanoate. The extract was filtered through a membrane filter of a pore size of 0.45 μm and concentrated by a rotary evaporator. The concentrated solution was precipitated with cold methanol. The precipitate was recovered and dried in vacuum to yield 38 mg of polyhydroxyalkanoate.  
         [0327]    The PHA obtained was subjected to NMR analysis, and the average molecular weight determination under the conditions as set forth in Example 29. The results of the NMR analysis show that the PHA in this example comprises a monomer unit of 3-hydroxy-4-{[(4-fluorophenyl)methyl]sulfanyl}butyrate and other monomer units of 3-hydroxyalkanoates and/or 3-hydroxyalkenoates having 4 to 12 carbon atoms, such as 3-hydroxybutyrate or 3-hydroxyvalerate to confirm that it has a constitution represented by the chemical formula (20). The integration of the  1 H-NMR spectra indicated that the PHA of this example contains 43.1 mol % of 3-hydroxy-4-{[(4-fluorophenyl)methyl]sulfanyl}butyrate monomer unit.  
       Example 34  
       [0328]    [0328] Pseudomonas jessenii  P161 was inoculated to 200 mL of M9 medium containing 0.5% of D-glucose and 0.1% of 4-{[(4-fluorophenyl)methyl]sulfanyl}butyric acid, and cultured with shaking at 125 strokes/min at 30° C. for 48 hours. Then, the cells were collected by centrifugation, re-suspended in 200 mL of M9 medium containing 0.5% of D-glucose and 0.1% of 4-{[(4-fluorophenyl)methyl]sulfanyl}butyric acid but no nitrogen source (NH 4 Cl), and cultured at 30° C. with shaking at 125 strokes/min for 48 hours. After that, the cells were collected by centrifugation, washed once with cold methanol, and lyophilized. The weight of the lyophilized cells was weighed (the cell dry weight).  
         [0329]    The lyophilized pellet was suspended in 20 mL of chloroform and stirred at 60° C. for 20 hours to extract polyhydroxyalkanoate. The extract was filtered through a membrane filter of a pore size of 0.45 μm and concentrated by a rotary evaporator. The concentrated solution was precipitated with cold methanol. The precipitate was recovered and dried in vacuum to yield 47 mg of polyhydroxyalkanoate.  
         [0330]    The PHA obtained was subjected to NMR analysis, and the average molecular weight determination under the conditions as set forth in Example 29. The results of the NMR analysis show that the PHA in this example comprises a monomer unit of 3-hydroxy-4-{[(4-fluorophenyl)methyl]sulfanyl}butyrate and other monomer units of 3-hydroxyalkanoates and/or 3-hydroxyalkenoates having 4 to 12 carbon atoms, such as 3-hydroxybutyrate or 3-hydroxyvalerate to confirm that it has a constitution represented by the chemical formula (20). The integration of the  1 H-NMR spectra indicated that the PHA of this example contains 48.7 mol % of 3-hydroxy-4-{[(4-fluorophenyl)methyl]sulfanyl}butyrate monomer unit.  
         [0331]    Table 11 shows the dry weight of the cells, the dry weight of the polymer, the dry weight ratio of the polymer to the cells, and the amount in mol % of 3-hydroxy-4-{[(4-fluorophenyl)methyl]sulfanyl}butyrate unit (abbreviated as “3HFBzyTB”) in the resulting PHA polymer in Examples 29 to 34.  
                                                         TABLE 11                                   Cell                       Dry           3HFBzyTB           Weight   Polymer Dry   Polymer Weight/   Unit           (mg/L)   Weight (mg/L)   Cell Weight (%)   mol %                                    Example 29   975   205   21.0   89.8       Example 30   515   225   43.7   10.6       Example 31   955   55   5.8   84.1       Example 32   1365   765   56.0   68.5       Example 33   515   190   30.1   43.1       Example 34   780   235   36.9   48.7