Abstract:
A method of making a formable hockey stick blade, the method comprising: (a) providing a foam core having a blade element with a thickness, the foam having a Poisson ratio of at least 0.33; (b) forming an uncured stick blade by wrapping the foam core with a layer of fibers pre-impregnated with a thermoplastic material; (c) placing the uncured stick blade in a mold; (d) applying heat and pressure to the mold for curing the uncured stick blade and for compressing the uncured stick blade such that the thickness of the blade element of the foam core is reduced; and (e) removing the cured stick blade from the mold.

Description:
FIELD OF THE INVENTION  
       [0001]     The present invention relates to a method of making a formable hockey stick blade.  
       BACKGROUND OF THE INVENTION  
       [0002]     Typical hockey stick blades or replacement blades are generally made of a wooden core reinforced with one or more layers of synthetic material such as fiberglass, carbon fiber or graphite. The core of the blade may also be made of a synthetic material reinforced with layers of fibers material. The layers are usually made of woven filament fibers, typically soaked in a resin and glued to the surfaces of the core of the blade. Expandable fibers braids may also be used for recovering the core of the blade.  
         [0003]     U.S. Pat. No. 6,062,996 discloses a sport implement comprising a blade structure having a core with an elongated insert and a peripheral frame. The blade structure is non-deformable at a first temperature and is formable at a second temperature that is greater that the first temperature and less than 250° F.  
         [0004]     There is a demand for a formable hockey stick blade that has a weight, stiffness and strength adapted for high-level hockey players and can be heated and shaped repeatedly to selected curvatures.  
       SUMMARY OF THE INVENTION  
       [0005]     As embodied and broadly described herein, the invention provides a method of making a formable hockey stick blade, the method comprising: (a) providing a foam core having a blade element with a thickness, the foam having a Poisson ratio of at least 0.33; (b) forming an uncured stick blade by wrapping the foam core with a layer of fibers pre-impregnated with a thermoplastic material; (c) placing the uncured stick blade in a mold; (d) applying heat and pressure to the mold for curing the uncured stick blade and for compressing the uncured stick blade such that the thickness of the blade element of the foam core is reduced; and (e) removing the cured stick blade from the mold.  
         [0006]     Other objects and features of the invention will become apparent by reference to the following description and the drawings. 
     
    
     BRIEF DESCRIPTION OF THE DRAWINGS  
       [0007]     A detailed description of the embodiments of the present invention is provided herein below, by way of example only, with reference to the accompanying drawings, in which:  
         [0008]      FIG. 1  is a perspective view of first and second core portions used in the construction of a formable hockey stick blade according to the invention;  
         [0009]      FIG. 2  is a perspective view of the first and second core portions of  FIG. 1  with first and second fibers braids used in the construction of the blade;  
         [0010]      FIG. 3  is a perspective view of the first and second core portions and first and second fibers braids of  FIG. 2  with further third and fourth fibers braid used in the construction of the blade of  FIG. 1 ;  
         [0011]      FIG. 4  is a perspective view of the first and second core portions and the fibers braids of  FIG. 3  with a further fifth fibers braid used in the construction of the blade of  FIG. 1 ;  
         [0012]      FIG. 5  is a perspective view of the uncured blade before the molding operation;  
         [0013]      FIG. 6  is a cross-sectional view taken along lines  6 - 6 ;  
         [0014]      FIG. 7  is a perspective view of the uncured blade of  FIG. 6  and a mold;  
         [0015]      FIG. 8  is a perspective view of the formable hockey stick blade construed in accordance with the invention; and  
         [0016]      FIG. 9  is a cross-sectional view taken along lines  9 - 9 . 
     
    
       [0017]     In the drawings, the embodiments of the invention are illustrated by way of examples. It is to be expressly understood that the description and drawings are only for the purpose of illustration and are an aid for understanding. They are not intended to be a definition of the limits of the invention.  
       DETAILED DESCRIPTION OF THE EMBODIMENTS  
       [0018]      FIG. 8  illustrates a formable hockey stick blade  10  constructed in accordance with the invention. As used herein, the word “formable” means that the blade  10  can be heated and softened for shaping it to a selected curvature. The blade  10  is formable when heated to a temperature exceeding the glass transition point of the thermoplastic material used for making the blade  10 . In fact, the temperature must be sufficiently high in order to bring the thermoplastic material to its amorphous form. The temperature increment can range between 25° F. and 50° F. above the glass transition point temperature. The glass transition point temperature of the thermoplastic-fibers matrix may be between 280° F. and 320° F. Moreover, since a thermoplastic material is used for making the blade  10 , the blade  10  is also “reformable” i.e. it can be heated, softened and shaped a couple of times without suffering any substantial basic alteration in its properties.  
         [0019]     The blade  10  comprises a shank  18 , a heel section  20  and a blade element  22 . The heel section  20  is located at the junction of the shank  18  and the blade element  22 . The shank  18  comprises a tenon  24  adapted to be inserted into a hollow hockey stick shaft made of aluminum, composite or graphite. The blade element  22  comprises a top edge  26 , a tip edge  28  and a bottom edge  30 .  
         [0020]     Referring to  FIGS. 1 and 9 , the blade  10  comprises a foam core  12  extending along a longitudinal axis A-A. The foam core  12  has the general shape of a hockey stick blade. The foam core  12  comprises a first portion  14  located above and aligned with a second portion  16 . The first and second portions  14 ,  16  are dimensioned such as to have the shape of a blade when aligned with one another. The first and second portions  14 ,  16  are made of expandable foam. For example, the first and second portions  14 ,  16  may be made of a closed-cell polymethacrymilide foam sold by Rohacell under the number 200 WF, this foam having a Poisson ratio of 0.33. The Poisson ratio is the ratio of lateral strain to the longitudinal strain for a given material subjected to a uniform longitudinal stress with a proportional limit. Other suitable foam will be the RC 51 WF, RC 71 WF, RC 110 WF, RC 300 WF, foams sold by Rohacell and having respective Poisson ratios of 0.34, 0.37, 0.37 and 0.38. The first and second portions  14 ,  16  may be made of a closed-cell polyetherimid foam sold under the name AIREX R82. The first and second portions  14 ,  16  may also be made of a styrene acrylo nitrile thermoplastic foam produced by ATC Chemical Corporation under the name CORCE-CELL T and having a density of around 5.0 to 5.6 lbs/cubic.  
         [0021]     The first and second portions  14 ,  16  form the blade element of the foam core  12  and may further comprise respective shank portions  32 ,  34  defining the core of the shank  18 , these shank portions  32 ,  34  comprising respective tenon portions  36 ,  38 . The shank portions  32 ,  34  generally extend upwardly and rearwardly from the heel section  20 . Hence, the core  12  comprises the first portion  14  with its shank portion  32  and the second portion  16  with its shank portion  34 .  
         [0022]     It is understood that the core may comprise first and second portions that do not comprise respective first and second shank portions. In fact, the first and second portions of the core may be confined to the blade element of the hockey stick blade (from the heel section to the tip edge) and the shank may be a separate component that is joined to the blade element. For example, the shank may be made of wood and comprises a groove in which a tongue portion provided on the blade element is inserted for joining together both components.  
         [0023]     As shown in  FIG. 2 , a first fibers braid  40  is wrapped over the first portion  14  and a second fibers braid  42  is wrapped over the second portion  16 . As shown in  FIG. 3 , third and fourth fibers braid  44 ,  46  are wrapped over the respective first and second fibers braids  40 ,  42  of the first and second portions  14 ,  16 . As shown in  FIG. 4 , a fifth fibers braid  48  is wrapped over the third and fourth fibers braids  44 ,  46  of the first and second portions  14 ,  16  such as to realize an uncured blade  50  as shown in  FIG. 5 . Note that the uncured blade  50  comprises the foam core  12  and the fibers braids covering that foam core and is a “preformed” blade since it has to be placed in a mold in order to manufacture and form a cured blade such as the blade  10 .  
         [0024]     The fibers braids are expandable so as to conform to the shape of the first and second portions  14 ,  16  and are made of woven fibers selected from the group consisting of carbon fibers, glass fibers, KEVLAR fibers, ceramic fibers, boron fibers, quartz fibers, spectra fibers, polyester fibers and polyethylene fibers. The fibers are pre-impregnated with a thermoplastic material such as Nylon or polypropylene. Examples of suitable materials are the pre-impregnated fibers braid sold under the name HEXCEL TOWFLEX TF-CN6-100 (matrix of Nylon 6) and the pre-impregnated fibers braid sold under the name SCHAPPE TPFL-CARBON PA12 (matrix of Nylon 12). The fibers braids may be made of fibers crossing at 45°. However, any other fibers crossing at between 30° and 60° may be used. Unidirectional fiber braids may also be used. Note that the foam core  12  and the fibers braids should have similar processing temperatures. In other words, the softening point of the thermoplastic-fibers matrix should be similar to the softening point of the foam.  
         [0025]     As shown in  FIG. 7 , the uncured blade  50  is afterwards inserted in a mold in order to manufacture the cured blade  10 . At that point, the mold may be at a temperature of about 420° F. It is understood that the mold may be heated before or after the introduction of the uncured blade  50  in the mold or it may remain at a steady temperature during the entire process. Heat is therefore applied to the mold in order to melt the thermoplastic-fibers matrix and soften the foam core  12  of the uncured blade  50 . Pressure is also maintained on the mold in order to compress the blade during the process. It is understood that the pressure exerted on the mold must be sufficient to keep the male-female mold parts together, to crush the form core  12  and to sustain the internal pressure created by the foam when heated.  
         [0026]     As previously indicated, the foam core  12  has the general shape of a hockey stick blade. However, the foam core has an initial thickness greater then its final thickness. For instance, the initial thickness of the foam core may be 1.5 to 10 times greater than the final thickness of the blade element  22  of the cured blade  10 . Indeed, due to the Poisson ratio of at least 0.33, the foam core  12  may flow and conform to the internal cavity of the mold while applying pressure to the outer layers of pre-impregnated fibers in order to consolidate together the thermoplastic material and the fibers, which then form the thermoplastic-fibers matrix. The internal pressure created by the heated foam should also be sufficient to bond together the foam core and the thermoplastic-fibers matrix. The thickness of the foam core  12  may be then considerably reduced. In fact, the foam core, more particularly the blade element of the foam core, is crushed during the process and its density may increase from 5 to 6 lbs/cubic foot to 6.5 to 20 lbs/cubic foot and its thickness may be reduced from 6 to 30 mm to 1 to 3 mm. For example, if the foam has an initial density of 5 lbs/cubic foot, this foam will have a density of around 15 lbs/cubic foot at the end if the initial thickness of the blade element of the foam core is three (3) times greater than its final thickness. The density of the crushed foam is therefore the density of the initial foam multiply with the initial thickness of the foam core divided with the thickness of the final foam core.  
         [0027]     The mold remains at a temperate of at least 420° F. for at least 2 minutes in order to cure the uncured blade  50 . It is understood that a minimum temperature of about 375° F. may be used but the processing time would then be longer. When the fibers-thermoplastic matrix is cured, the mold is opened and the cured blade  10  is removed from the mold. Note that the blade  10  has the general shape of a straight hockey stick blade. Excess material may be trimmed off.  
         [0028]      FIG. 6  shows a cross section view of the uncured blade  50  for illustrating the fiber braids before the molding process. In fact, once the thermoplastic-fibers matrix is cured (see large lines on  FIG. 9 ), the cured blade  10  comprises an interface between the first and second portions  14 ,  16 , this interface comprising fibers oriented transversely relative to the longitudinal axis A-A. The thermoplastic-fibers matrix of the edges  26 ,  28 ,  30  (see large lines on  FIG. 9 ) may also comprise fibers oriented transversely relative to the longitudinal axis A-A.  
         [0029]     The blade  10  is a formable straight blade and it is therefore possible to supply this blade to stores that will then tailor the blade  10  by heating and applying pressure to shape it according to a curvature selected by a customer.  
         [0030]     The above description of the embodiments should not be interpreted in a limiting manner since other variations, modifications and refinements are possible within the spirit and scope of the present invention. The scope of the invention is defined in the appended claims and their equivalents.