Abstract:
The present invention relates generally to a new dielectric forming metal/ceramic laminate magnet and process thereof. More particularly, the invention encompasses a new process for fabrication of a large area laminate magnet with a significant number of holes, integrated dielectric forming metal plate(s) and electrodes for electron and electron beam control. The present invention also relates to a magnetic matrix display and electron beam source and methods of manufacture thereof.

Description:
FIELD OF THE INVENTION  
         [0001]    The present invention relates generally to a new dielectric forming metal/ceramic laminate with discretely distributed magnets with through-holes and process thereof. More particularly, the invention encompasses a new process for fabrication of a large area ceramic laminate with discretely distributed magnets with integrated metal plate(s) which is oxidizable to form thin dielectric layer, and electrodes for electron and electron beam control. The present invention also relates to a magnetic matrix display (MMD) structure and methods of manufacture thereof.  
         BACKGROUND OF THE INVENTION  
         [0002]    A magnetic matrix display is particularly, although not exclusively, useful in display applications, especially flat panel display applications. Such flat panel display applications include television receivers, visual display units for computers, especially, although not exclusively, portable and/or desktop computers, personal organizers, communications equipment, wall monitor, portable game unit, virtual reality visors and the like. Flat panel display devices based on a magnetic matrix electron beam source hereinafter may be referred to as Magnetic Matrix Displays (MMD).  
           [0003]    Conventional flat panel displays, such as liquid crystal display panels, and field emission displays, provide one display technology. However, these conventional flat panel displays are complicated and costly to manufacture, because they involve a relatively high level of semiconductor fabrication, delicate materials, and high tolerance requirements.  
           [0004]    U.S. Pat. No. 5,917,277 (Knox) entitled “ELECTRON SOURCE INCLUDING A PERFORATED PERMANENT MAGNET”, assigned to the assignee of the instant Patent Application and the disclosure of which is incorporated herein by reference, discloses a magnetic matrix electron source and methods of manufacture thereof. Also disclosed is the application of the magnetic matrix electron source in display applications, such as, for example, flat panel display, displays for television receivers, visual display units for computers, to name a few. Also disclosed is a magnetic matrix display having a cathode for emitting electrons, a permanent magnet with a two dimensional array of channels extending between opposite poles of the magnet, the direction of magnetization being from the surface facing the cathode to the opposing surface. The magnet generates, in each channel, a magnetic field for directing electrons from the cathode means into an electron beam. The display also has a screen for receiving the electron beam from each channel. The screen has a phosphor coating facing the side of the magnet remote from the cathode, the phosphor coating comprising a plurality of pixels each corresponding to a different channel. There are grid electrode means disposed between the cathode means and the magnet for controlling the flow of electrons from the cathode means into each channel. The two dimensional array of channels are regularly spaced on an X-Y grid. The magnet area is large compared with its thickness. The flat panel display devices based on a magnetic matrix electron source is referred to as MMD (Magnetic Matrix Display).  
           [0005]    The permanent magnet is used to form substantially linear, high intensity fields in the channels or magnetic apertures for the purpose of collimating the electrons passing through the aperture. The permanent magnet is insulating, or at most, has a small conductivity, so as to allow a field gradient along the length of the aperture. The placement of the beam so formed, on the phosphor coating, is largely dependent on the physical location of the apertures in the permanent magnet.  
           [0006]    In operation, these electron beams are directed at a phosphor screen and collision of the electron beam with the phosphor results in light output, the intensity being proportional to the incident beam current (for a fixed final anode voltage). For color displays, three different colored phosphors (such as red, green and blue) are used and color is obtained by selective mixing of these three primary colors.  
           [0007]    For accurate color reproduction, the location of the electron beams on the appropriate colored phosphor is essential.  
           [0008]    Some degree of error may be tolerated by using “black matrix” to separate the different phosphors. This material acts to delimit individual phosphor colors and also enhances the contrast ratio of the displayed image by making the display faceplate appear darker. However, if the electron beam is misplaced relative to the phosphor, initially the light output from the phosphor is reduced (due to loss of beam current to the black matrix) and this will be visible as a luminance non-uniformity. If the beam is subject to a more severe placement error, it may stray onto a different colored phosphor to that for which it was intended and start to produce visible quantities of light output. Thus the misplaced electron beam is actually producing the wrong light output color. This is called a purity error and is a most undesirable display artifact. For a 0.3 mm pixel, typical phosphor widths are 67 μm with 33 μm black matrix between them.  
           [0009]    It will be apparent that a very precise alignment is required between the magnet used to form the electron beams and the glass plate used to carry the phosphors that receive the electron beams. Further, this precise alignment must be maintained over a range of different operating conditions (high and low brightness, variable ambient temperature etc).  
           [0010]    A number of other magnet characteristics are also important when considering application for a display, such as, for example:  
           [0011]    1. It is generally accepted that the displayed image is formed by a regular array of pixels. These pixels are conventionally placed on a square or rectangular grid. In order to retain compatibility with graphics adaptors the magnet must thus present the electron beams on such an array.  
           [0012]    2. In operation, the spacing between the grids used for bias and modulation of the electron beam and the electron source determines the current carried in the electron beam. Variations of this spacing will lead to variations in beam current and so to changes in light output from the phosphor screen. Hence it is a requirement that the magnet, which is used as a carrier for these bias and modulation grids, maintain a known spacing to the electron source. To avoid constructional difficulties, the magnet should be flat.  
           [0013]    3. The display will be subject to mechanical forces, especially during shipment. The magnet must retain structural integrity over the allowable range of stresses it may encounter. A commonly accepted level is an equivalent acceleration of about 30G (294 ms −2 ).  
           [0014]    One further requirement is that since the magnet is to be used within the display, which is evacuated, it should not contain any organic components which may be released over the life of the display, so degrading the quality of vacuum or poisoning the cathode.  
           [0015]    Finally, the magnet is magnetized in the direction of the apertures, that is the poles correspond to the faces of the magnet.  
           [0016]    The manufacture of such a magnet that satisfies the above conditions is not possible by the use of previously known manufacturing methods. Certainly a magnet (ferrite, for example) of the desired size without apertures is readily obtainable but the presence of the apertures causes some problems.  
           [0017]    If the apertures in the magnet are to be formed after the ferrite plate has been sintered, either laser or mechanical drilling may be used. However, the sintered ferrite is a very hard material and forming the apertures by this technique will be a costly and lengthy process—unsuitable for a manufacturing process.  
           [0018]    Holes could be formed in the ferrite at the green-sheet stage before sintering by known punching/drilling methods typical of multi-layer ceramics for microelectronics applications. However, during sintering a number of problems would be anticipated, such as, for example:  
           [0019]    The magnet plate will be subject to uneven shrinkage leading to the holes “moving”—an unequal radial displacement from their nominal positions;  
           [0020]    The magnet itself is likely to “bow” such that it forms a section of a large diameter sphere;  
           [0021]    Cracking is likely to occur between adjacent apertures due to the apertures acting as stress concentrators; or  
           [0022]    If, to obtain the desired aperture length, multiple thin sheets are stacked on top of one another, misalignment may occur in stacking which could lead to no “line of sight” through the apertures.  
           [0023]    A further problem is that ferrite is a hard but not tough material and the presence of the apertures significantly reduces the mechanical strength of the plate. Thus, during shipment when large shocks may be encountered, complete mechanical failure of the magnet is a distinct possibility.  
           [0024]    U.S. Pat. No. 4,138,236 (Haberey) discloses a method of bonding hard and/or soft magnetic ferrite parts with an oxide glass. The oxide glass may be applied prior to or after pre-firing or main firing. Finally, the ferrite parts are fused at temperatures in excess of the glass softening point.  
           [0025]    U.S. Pat. No. 4,540,500 (Torii) discloses a low temperature sinterable oxide magnetic material prepared by adding 0.1 to 5.0 percent by weight of glass to ferrite. In some situations, the sintering temperature can be reduced to about 1,000° C. or less.  
           [0026]    U.S. Pat. No. 4,023,057 (Meckling) discloses a compound magnet for a motor stator having a laminated structure that includes thin, flexible magnets made from permanently magnetizable particles, such as barium ferrite, that are embedded in a flexible matrix, such as rubber. Various laminated arrangements are contemplated for producing more intense magnetic fields and thin metal spacers are used in most laminated structures to collapse the respective fields of the flexible magnetic components to increase the flux density at the resultant poles and to orient the permanent magnetic fields in the magnetic circuit of the motor.  
           [0027]    Published Japanese Patent Application No. JP60093742 discloses a display having a focus electrode with a conductive magnetic body and a sputtered metal coating on one surface of the magnet body. The conductivity is required for the focusing electrode to perform its function. The coating is sputtered and so is a thin coating, not substantially adding to the mechanical structure of the magnet. Each of the holes in the magnet has a number of electron beams passing through it.  
           [0028]    U.S. Pat. No. 5,857,883, (Knickerbocker), entitled “Method of Forming Perforated Metal/Ferrite Laminated Magnet”, assigned to the assignee of the instant Patent Application and the disclosure of which is incorporated herein by reference, discloses a process for fabrication of a large area laminate magnet with a significant number of perforated holes, integrated metal plate(s) and electrodes for electron and electron beam control.  
           [0029]    U.S. Pat. No. 5,932,498 (Beeteson), entitled “MAGNET AND METHOD FOR MANUFACTURING A MAGNET”, assigned to the assignee of the instant Patent Application and the disclosure of which is incorporated herein by reference, discloses a magnet-photosensitive glass composite and methods thereof.  
           [0030]    U.S. Pat. No. 5,986,395, (Knickerbocker), entitled “Metal/Ferrite Laminate Magnet”, assigned to the assignee of the instant Patent Application and the disclosure of which is incorporated herein by reference, discloses a process for fabrication of a metal/ferrite laminate magnet with a significant number of perforated holes.  
           [0031]    Therefore, there is a need for a dielectric forming metal/ferrite laminate magnet as discussed and described in context of the present invention. The use of such a laminate magnet would be in multiple areas, however, it will have an immediate application in the MMD technology.  
         PURPOSES AND SUMMARY OF THE INVENTION  
         [0032]    The invention is a novel structure and process for dielectric forming metal/ceramic laminate with discretely and orderly distributed magnets with throughholes.  
           [0033]    Therefore, one purpose of this invention is to provide a structure and a process that will form dielectric forming metal/ceramic laminate with discretely distributed magnets.  
           [0034]    Another purpose of this invention is to provide a structure and a process that will provide dielectric forming metal/ceramic laminate with discretely and orderly distributed magnets with through-holes.  
           [0035]    Yet another purpose of this invention is to use the dielectric forming metal/ceramic laminate as a mask to create an image on at least one glass plate to form multi-phosphors (red, green, blue) material which receives an electron beam to create a display.  
           [0036]    Still another purpose of this invention is to provide a structure through which one or more collimated beam(s) of electrons can be formed using the ceramic/magnetic laminate.  
           [0037]    Yet another purpose of this invention is to provide a structure that can be used with any electron sensitive process.  
           [0038]    Still yet another purpose of the invention is to provide a laminated dielectric forming metal/ceramic laminate with discretely distributed magnets that has a plurality of openings for guiding electrons and/or electron beams.  
           [0039]    Therefore, in one aspect this invention comprises a process of making unsintered dielectric forming metal/ferrite laminate magnet, comprising:  
           [0040]    (a) forming at least one opening in a dielectric forming metal sheet having a first surface and a second surface,  
           [0041]    (b) securing at least one dielectric layer to said first surface of said dielectric forming metal sheet,  
           [0042]    (c) filling said at least one opening in said dielectric forming metal sheet with at least one ferritic material,  
           [0043]    (d) forming at least one opening through said ferritic material and said dielectric layer, such that at least a portion of said opening overlaps at least a portion of said opening in said dielectric forming metal sheet, and thereby making said unsintered dielectric forming metal/ferrite laminate magnet.  
           [0044]    In another aspect this invention comprises a process of making unsintered dielectric forming metal/ferrite laminate magnet, comprising:  
           [0045]    (a) forming at least one opening in a dielectric forming metal sheet having a first surface and a second surface,  
           [0046]    (b) securing at least one dielectric layer to said first surface of said dielectric forming metal sheet,  
           [0047]    (c) forming a second hole with first hole as a guide,  
           [0048]    (d) filling said at least one opening in said dielectric forming metal sheet and said dielectric layer with at least one composite magnetic material,  
           [0049]    (e) forming at least one opening through said ferritic material and said dielectric layer, such that at least a portion of said opening overlaps at least a portion of said opening in said dielectric forming metal sheet, and thereby making said unsintered dielectric forming metal/ferrite laminate magnet.  
           [0050]    In still another aspect this invention comprises a process of making dielectric forming metal/ferrite laminate magnet, comprising:  
           [0051]    (a) forming at least one opening in a dielectric forming metal sheet having a first surface and a second surface,  
           [0052]    (b) securing at least one dielectric layer to said first surface of said dielectric forming metal sheet,  
           [0053]    (c) filling said at least one opening in said dielectric forming metal sheet with at least one ferritic material,  
           [0054]    (d) forming at least one opening through said ferritic material and said dielectric layer, such that at least a portion of said opening overlaps at least a portion of said opening in said dielectric forming metal sheet, and sintering the same to form said dielectric forming metal/ferrite laminate magnet.  
           [0055]    In yet another aspect this invention comprises a display device comprising, at least one cathode means and at least one dielectric forming metal/ferrite laminate magnet, wherein said magnet has at least one opening which extends between opposite poles of said magnet, creating at least one magnetic channel, wherein said magnetic channel allows the flow of electrons received from said cathode means into at least one electron beam towards at least one target.  
           [0056]    In still another aspect this invention comprises a display device comprising, a screen for receiving electrons from an electron source, said screen having a phosphor coating facing said side of a magnet remote from said cathode; and means for supplying control signals to a grid electrode means and an anode means to selectively control flow of electrons from said cathode to said phosphor coating via at least one magnetic channel, and thereby producing an image on said screen, and wherein said magnet comprises of at least one dielectric forming metal sheet.  
           [0057]    In still yet another aspect this invention comprises a display device comprising, a screen for receiving electrons from at least one electron source, said screen having a phosphor coating facing said side of a magnet remote from said cathode, said phosphor coating comprising a plurality of groups of different phosphors, said groups being arranged in a repetitive pattern, each group corresponding to a different channel; means for supplying control signals to said grid electrode means and said anode means to selectively control flow of electrons from said cathode to said phosphor coating via said channel; and deflection means for supplying deflection signals to said anode means to sequentially address electrons emerging from said channel to different ones of said phosphors for said phosphor coating thereby to produce a color image on said screen, and wherein said magnet comprises of at least one dielectric forming metal sheet.  
           [0058]    In yet another aspect this invention comprises an apparatus comprising, at least one cathode means, at least one dielectric forming metal/ferrite laminate magnet, wherein said magnet has at least one magnetic channel extending between opposite poles of said magnet, wherein each magnetic channel allows the flow of electrons received from said cathode means into an electron beam, grid electrode means disposed between said cathode means and said magnet for controlling flow of electrons from said cathode means into said magnetic channel, and, anode means remote from said cathode for accelerating electrons through said magnetic channel.  
           [0059]    In yet another aspect this invention comprises a process of making sintered dielectric forming metal/ferrite laminate magnet, comprising:  
           [0060]    (a) forming at least one opening in a dielectric forming metal sheet having a first surface and a second surface,  
           [0061]    (b) securing at least one dielectric layer to said first surface of said dielectric forming metal sheet,  
           [0062]    (c) filling said at least one opening in said dielectric forming metal sheet with at least one ferritic material,  
           [0063]    (d) forming at least one opening through said ferritic material and said dielectric layer, such that at least a portion of said opening overlaps at least a portion of said opening in said dielectric forming metal sheet, and  
           [0064]    (e) sintering said dielectric forming metal sheet and said ferritic material, and thereby making said sintered dielectric forming metal/ferrite laminate magnet. 
       
    
    
     BRIEF DESCRIPTION OF THE DRAWINGS  
       [0065]    The features of the invention believed to be novel and the elements characteristic of the invention are set forth with particularity in the appended claims. The drawings are for illustration purposes only and are not drawn to scale. Furthermore, like numbers represent like features in the drawings. The invention itself, however, both as to organization and method of operation, may best be understood by reference to the detailed description which follows taken in conjunction with the accompanying drawings in which:  
         [0066]    [0066]FIG. 1, illustrates a preferred embodiment of this invention where a dielectric forming metal/ceramic laminate with discretely distributed magnets direct at least one electron beam from a cathode to a display panel.  
         [0067]    FIGS.  2 - 7 , illustrate a preferred process to manufacture the dielectric forming metal/ceramic laminate with discretely distributed magnets of this invention.  
         [0068]    [0068]FIG. 8, illustrates a detailed view of the inventive structure of the dielectric forming metal/ceramic laminate with discretely distributed magnets with at least one hole per magnet wherein the hole extends between the poles of the magnet. 
     
    
     DETAILED DESCRIPTION OF THE INVENTION  
       [0069]    In accordance with the present invention, there is provided an electron source comprising at least one cathode means and at least one ceramic laminate with discretely distributed magnets. The magnets are perforated by at least one channel extending between opposite poles of the magnet, wherein each channel in a magnet that can direct or guide electrons received from the cathode means into an electron beam towards a target with no possible overlap.  
         [0070]    In a preferred embodiment of the present invention, the electron source comprises grid electrode means disposed between the cathode means and the discrete magnets for controlling flow of electrons from the cathode means into the magnetic channels.  
         [0071]    The magnetic channels are preferably disposed in the magnets in a two dimensional array of rows and columns. However, a person skilled in the art could also customize the dimensional array.  
         [0072]    Preferably, the grid electrode means comprise a plurality of parallel row conductors and a plurality of parallel column conductors arranged orthogonally to, and insulated from, the row conductors, each channel being located at a different intersection of a row conductor and a column conductor.  
         [0073]    The grid electrode means may be disposed on the surface of the cathode means facing the magnet. Alternatively, the grid electrode means may be disposed on the surface of the magnet facing the cathode means.  
         [0074]    The cathode means may comprise a cold emission device such as a field emission device. Alternatively, the cathode means may comprise a photocathode. In some embodiments of the present invention, the cathode may comprise a thermionic emission device.  
         [0075]    In a particularly preferred embodiment of the invention, each channel may have a cross-section which varies in shape and/or area along its length.  
         [0076]    In a preferred embodiment of the present invention, each channel may be tapered, the end of the channel having the largest surface area facing the cathode means.  
         [0077]    The laminate with discretely distributed magnets preferably comprises ferrite. In some embodiments of the present invention, the magnet may comprise a ceramic material. In preferred embodiments of the present invention, the magnet may also comprise a binder. The binder may be organic or inorganic. Preferably, the binder comprises an inorganic glass composite containing glass forming oxides for optimized properties in fabrication and use.  
         [0078]    In the preferred embodiment of the present invention, the channel is circular in cross-section. In other embodiments of the present invention, the cross-section of the channel could be selected from a group comprising, triangular, rectangular, polygonal, to name a few. The corners and edges of each channel could also be chamfered.  
         [0079]    The present invention extends to display devices and a computer system comprising: memory means; data transfer means for transferring data to and from the memory means; processor means for processing data stored in the memory means; and a display device comprising the electron source as hereinbefore described for displaying data processed by the processor means.  
         [0080]    It will further be appreciated that the present invention extends to a print-head comprising an electron source as hereinbefore described. Still further, it will be appreciated that the present invention extends to document processing apparatus comprising such a print-head, together with means for supplying data to the print-head to produce a printed record in dependence on the data.  
         [0081]    The present invention in yet another aspect is a triode device comprising: cathode means; a laminate with discretely distributed magnets perforated by at least a channel extending between opposite poles of the magnet wherein each channel forms electrons received from the cathode means into an electron beam; grid electrode means disposed between the cathode means and the magnet for controlling flow of electrons from the cathode means into the channels; and, anode means disposed on the surface of the magnet remote from the cathode for accelerating electrons through the channels towards the glass plate containing phosphors.  
         [0082]    The present invention from still another aspect is a process for making an electron beam collimator, comprising: forming perforated metal plates, perforated greensheets of dielectric and ferrite containing compositions, forming metal electrode conductors and composite magnetic structure to produce a laminate with discretely distributed magnets with desired characteristics.  
         [0083]    The process may comprise mixing the ferrite with a binder prior to forming the discretely distributed magnets. Preferably, the binder comprises glass particles.  
         [0084]    The process may comprise depositing anode means on a perforated face of the magnets.  
         [0085]    Preferably, the process comprises depositing control grid means on the face of the laminate with discretely distributed magnets remote from the face carrying the anode means.  
         [0086]    At least one of the steps of depositing the anode means and the steps of depositing the control grid means may comprise photolithography. Alternatively, plating, screen printing or decal transfer may be used for depositing anode means and control grid means.  
         [0087]    The present invention from still another aspect is a process for making a display device comprising: making an electron source according to the process hereinbefore described; positioning a phosphor coated screen adjacent to the face of the magnet carrying the anode means; and, evacuating spaces between the cathode means and between the magnet and the magnet and the screen.  
         [0088]    The present invention from yet another aspect is a process for addressing pixels of a display screen having a plurality of pixels, each pixel having successively first, second, and third sub-pixels in line, the process comprising: generating a plurality of electron beams, each electron beam corresponding to a different one of the pixels; and, deflecting each electron beam to repetitively address the sub-pixels of the corresponding pixel in the sequence second pixel, first pixel, second pixel, third pixel.  
         [0089]    Referring now to the figures, such as, FIG. 1, a color magnetic matrix display (MMD)  100 , of the present invention comprises: a first or lower plate  10 , such as, a glass plate  10 , carrying at least one cathode  12 , and a second or upper plate  20 , such as, a glass plate  20 , carrying at least one coating of at least one phosphor pixel or dots or stripes  21 . It is preferred that the stripes  21 , are sequentially arranged red, green and blue phosphor stripes  21 , facing the cathode  12 . The phosphor stripes  21 , are made from preferably high voltage phosphors. At least one anode layer  22 , is disposed on or adjacent to the phosphor coating  21 .  
         [0090]    At least one composite magnetic plate or sheet  90 , with discretely distributed magnets is disposed between the plates  10  and  20 . The composite magnetic sheet  90 , has a first or lower surface  91 , and an upper or second surface  93 , and is perforated by a two dimension matrix of perforation or “pixel wells”  23 . Electron beams  14 , are channeled through the “pixel wells”  23 . At least one bias or a control grid  15 , such as, at least one electrically conductive metal  15 , which is preferably near or on the first surface  91 , can be used to channel the electrons in the electron beam  14 .  
         [0091]    At least one anode  22 , could also be secured to the sintered or unsintered dielectric forming metal/ferrite laminate magnet  90 . The anode  22 , could be formed using a process selected from a group comprising photolithography, screen printing, decal transfer, plating, or adhesive patterning, followed by dry deposition of at least one electrically conductive medium.  
         [0092]    At least one control grid  15 , could also be secured to the sintered or unsintered dielectric forming metal/ferrite laminate magnet  90 . The control grid  15 , could be formed using a process selected from a group comprising photolithography, screen printing, decal transfer, plating, or adhesive patterning, followed by dry deposition of at least one electrically conductive medium.  
         [0093]    FIGS.  2 - 7 , illustrate a preferred process for the manufacture of the inventive composite magnetic plate or sheet  90 , comprising at least one dielectric forming metal/ceramic laminate with magnets.  
         [0094]    [0094]FIG. 2, shows at least one rolled dielectric forming metal sheet  30 , which is preferably capable of oxidizing to transform into a dielectric material in oxidizing atmospheres with temperatures up to about 1,000° C. At least one photo resist is applied onto this dielectric forming metal sheet  30 , which is subsequently exposed and developed to produce a pattern of holes or openings  32 . These holes  32 , can be made by methods well known in the art, such as, by etching with at least one etchant that attacks the dielectric forming metal sheet  30 .  
         [0095]    The desired array of holes  32 , made in the dielectric forming metal sheet  30 , can also be inspected to ensure that all the holes  32 , are present, and that the dimensional and positional tolerances of the holes  32 , are met. Hole diameter with a tolerance of about 0.3 mil and hole-to-hole pitch with a tolerance of about 0.2 mil is achievable by this technique.  
         [0096]    For some applications the exposed surface of the dielectric forming metal sheet  30 , may have to be prepared to enhance the adhesion between the dielectric forming metal sheet  30 , and the subsequent layer, such as, a dielectric layer. This could be accomplished by the deposition of or formation of selected adhesion promoting metals or oxides on one or both surfaces of the dielectric forming metal sheet  30 . However, one could also use at least one suitable adhesive to secure a second dielectric layer to the dielectric forming metal sheet  30 .  
         [0097]    As shown in FIG. 3, a sub-laminate structure  45 , is formed by combining the etched dielectric forming metal sheet  30 , with holes  32 , to at least one second thin dielectric layer  40 , such as, a green sheet  40 , on at least one exposed surface to form the primary “green” sub-laminate structure  45 . It is preferred that the sub-laminate structure  45 , is formed in such a way so that there is no movement between the various layers, such as, between the dielectric forming metal sheet  30 , with holes  32 , and the at least one second dielectric layer  40 . This can be done by the simultaneous application of heat and/or pressure to all components or layers of the sub-laminate structure  45 , or by adhesively bonding the layers to the dielectric forming metal sheet  30 . It should be appreciated that the at least one dielectric layer  40 , can be on one side as clearly shown in FIG. 3, or on both sides of the dielectric forming metal sheet  30 , as needed.  
         [0098]    The dielectric layer or sheet  40 , of FIG. 3, can be formed in a number of ways, such as, on at least one exposed surface of the dielectric forming metal sheet  30 , one could form at least one cast sheet  40 . This could be done by combining a glass powder, organic binders, solvents and vehicles to produce a slurry capable of being cast into at least one thin dielectric sheet  40 . The technology used to produce the thin dielectric sheet  40 , is similar to the one used to prepare conventional multilayer ceramic green sheets. After drying, the cast sheet  40 , could be cut to the proper size to form a cast dielectric layer  40 , onto at least one surface of the dielectric forming metal sheet  30 .  
         [0099]    After the primary unsintered sub-laminate structure  45 , has been formed, holes or openings are produced in the dielectric green sheet(s)  40 , using the pre-existing hole  32 , in the dielectric forming metal sheet  30 , as a guide. The holes formed in the green dielectric layer  40 , of the sub-laminate structure  45 , can be made by a myriad of techniques, such as, mechanical, laser beam, electron beam, techniques known to those skilled in the art.  
         [0100]    The insulator layer  40 , could also be formed by mixing at least one dielectric material to form a dielectric slurry; one would then mix, cast and dry the dielectric slurry into a dielectric green sheet  40 ; and then the dielectric green sheet  40 , could be blanked to form the dielectric layer  40 .  
         [0101]    For some applications the insulator layer  40 , could be formed by mixing at least one dielectric material to form a dielectric slurry, paste or powder, and wherein the dielectric mix could be deposited onto the dielectric forming metal sheet  30 , using at least one method selected from a group comprising spraying, screening, dry-pressing, to name a few.  
         [0102]    The insulator layer  40 , could also be formed by mixing the dielectric material to form a dielectric slurry, paste or powder, and wherein the dielectric slurry could be integrated onto the dielectric forming metal sheet  30 , using at least one method selected from a group comprising spraying, casting, screening, dry-pressing, to name a few.  
         [0103]    The insulator layer  40 , could be secured to the surface of the dielectric forming metal sheet  30 , by application of heat and/or pressure. The insulator layer  40 , could also be secured to the surface of the dielectric forming metal sheet  30 , by using at least one adhesive material.  
         [0104]    [0104]FIG. 4, shows that the primary unsintered sub-laminate structure  45 , has now been perforated with holes or openings  52 , that have been produced in the dielectric green sheet  40 , creating a punched dielectric green sheet  40 , that combines with the dielectric forming metal sheet  30 , to form a perforated primary green laminate  55 . It is preferred that the array of holes  32 , in the dielectric forming metal sheet  30 , are slightly larger than the array of holes  52 , in the dielectric layer  40 , to help facilitate subsequent hole formation and also to enhance the reliability of ultimate desired structure.  
         [0105]    The hole  32 , in the dielectric forming metal sheet  30 , could be used to form at least one corresponding hole  52 , in subsequent components, and wherein all of the correspondingly formed holes are preferably held in registration with the hole  32 , in the dielectric forming metal sheet  30 .  
         [0106]    [0106]FIG. 5, illustrates the next step in building the inventive structure that is shown in FIG. 8. The holes  32 , in the dielectric forming metal sheet  30 , and the holes  52 , in the dielectric layer  40 , of the laminate  55 , shown in FIG. 4, are now filled with at least one material  62 , in the opening  32 , in dielectric forming metal sheet  30 , or material  64 , in the opening  52 , in the dielectric layer  40 . This filling could be done by methods well known in the art, such as, by screening. It is preferred that the material  62  and/or  64 , is made of permanent magnetic material, such as, a ferrite. The resulting multi-layered laminate structure  65 , as shown in FIG. 5, with magnetic material  62  and  64 , in the holes of the dielectric forming metal sheet  30 , and dielectric layer  40 . The magnetic material  62  and  64 , are preferably of the same composition and concentration, however, for some applications the composition and concentration of the magnetic material  62  and  64 , could be different from each other.  
         [0107]    The composite magnetic material  62  and/or  64 , used in this invention could also be formed by mixing ferritic material with glass particles, organic binders and solvents to form a ferritic paste, slurry or powder; and applying the ferritic mix to form the ferritic material  62  and/or  64 .  
         [0108]    For some applications the composite magnetic material  62  and/or  64 , could be formed by mixing ferritic material with glass particles, organic binders and solvents to form a ferritic paste, slurry or powder; casting and drying the ferritic paste, slurry or powder, into a ferritic green sheet; and blanking the ferritic green sheet to form the ferritic material  62  and/or  64 .  
         [0109]    It has been found that the composite magnetic material  62  and/or  64 , could also be formed by mixing ferritic material with glass particles, organic binders and solvents to form a ferritic slurry, paste or powder, and wherein the ferritic mix is deposited onto the dielectric forming metal sheet  30 , using at least one method selected from the group comprising spraying, screening, extruding, to name a few.  
         [0110]    The composite magnetic material  62  and/or  64 , could also be formed by mixing ferritic material with glass particles, organic binders and solvents to form a ferritic slurry, paste or powder, and wherein the ferritic mix would be integrated into the dielectric forming metal sheet  30 , using at least one method selected from the group comprising spraying, screening, extruding, etc.  
         [0111]    The composite magnetic material  62  and/or  64 , could be filled into the opening  32 , in the dielectric forming metal sheet  30 , by application of heat and/or pressure.  
         [0112]    In the next step, an unsintered multi-layered laminate structure  75 , as shown in FIG. 6, is obtained by forming through holes  72 , in the magnetic material  62  and  64 , having an inner wall  71 , of magnetic material  74 . However, it should be understood that for some applications, the dielectric forming metal sheet  30 , having a magnetic material  74 , with inner wall  71 , could be formed separately, and the dielectric material  40 , having a magnetic material  74 , with inner wall  71 , could be formed separately, and then they could be joined to form the unsintered multi-layered laminate structure  75 . Of course care must be made to make sure that the openings  72 , are aligned in order for the electrons to pass through the inner wall  71 , during subsequent operation.  
         [0113]    [0113]FIG. 7, illustrates an unsintered multi-layered magnetic laminate  85 , which in this case is the result of securing multiple laminates  75 , from FIG. 6, and which will be subsequently sintered. Of course care must be taken that the holes  72 , and the magnetic material  74 , are appropriately aligned to allow for an uninterrupted passage of the electron beam  14 , as discussed in FIG. 1. It has been shown in FIG. 7, that the two dielectric forming metal sheets  30 , sandwich the two thin dielectric layer  40 , however, for this invention the positioning of the dielectric forming metal sheet  30 , and the thin dielectric layer  40 , is not critical because after sintering the dielectric forming metal sheet  30 , will become or be transformed into a dielectric material  31 ,  33 , as discussed with reference to FIG. 8.  
         [0114]    As shown in FIG. 8, the first or bottom dielectric layer  31 , and the second or top dielectric layer  33 , are formed due to chemical oxidation during sintering from dielectric forming metal sheets  30 , sandwich by at least one dielectric layer  40 . The holes  72 , now stretch from one surface of the first dielectric sheet  31 , to the other surface of the second dielectric sheet  33 , having an inner wall  71 , of magnetic material  74 . However, subsequent to this step, one could also build metal electrodes on the top and bottom surfaces of the laminate  85 . The electrode on either top and/or bottom surface of the sintered laminate  85 , could be made by any conventional thin film technology.  
         [0115]    It should be noted that a plurality of perforated primary unsintered laminate structures  75 , may be combined into a secondary unsintered laminate structure  85 , by the re-application of heat and/or pressure to the components or by the use of an organic adhesive. In this step care must be taken to ensure the alignment of the holes  72 , in the various substructures.  
         [0116]    [0116]FIG. 8, also shows a cross-sectional detailed view of the inventive structure of the dielectric forming metal/ceramic laminate  90 , with at least one hole or opening per discrete magnet. The laminate  90 , is built with a first or bottom metal plate  31 , having surface  91 , a second or top metal plate  33 , having surface  93 , at least one dielectric layer  44 , and at least one discrete magnet  94 . The magnet  94 , has at least one pixel well  23 , having inner wall  92 , that extend from one end of the magnetic pole to the opposite end of the magnet, which is the boundary of the holes  23 , and the electrons from the electron beam  14 , are channeled through the hole  23 , defined by the magnetic inner wall  92 . In a typical 17 inches or 21 inches diagonal display, the MMD laminate  90 , may contain couple of millions of holes  23 , and hence couple of millions of magnets  94 . It is preferred that there be a hole per pixel or a magnet per pixel. The magnets  94 , are discrete and are distributed in the laminate  90 , which is made from the first dielectric forming metals  31  and  33  and the second dielectric  44 . The laminate  90 , is very flat and is manufactured with compatible materials that can not only be co-sintered but also form fully compatible dielectric matrix with discretely distributed magnets. For example, the first dielectric forming metals  31  and  33 , can be aluminum, or alloys such as aluminum+magnesium, aluminum+silicon, etc., which can be fully oxidized to form dielectric layer such as alumina or oxides containing aluminum oxide, the same or similar dielectric layer  44 , could be a ceramic layer  44 , which can be alumina or glass ceramic. The magnet  94 , can be a ferrite or ferrite with glass, to name a few.  
         [0117]    The dielectric forming metal sheet  30 , could be used as a mask to form at least one layer of phosphor on at least one screen  21 . The laminate magnet  90 , could also be used as a mask to form at least one layer of phosphor on at least one screen  21 . For some applications a display device could be made by positioning a phosphor coated screen  21 , adjacent to the face of the magnet carrying the anode means  22 , and, evacuating spaces between the electron source  12 , and between the magnet  94 , and the screen  21 .  
         [0118]    The opening  23  or  32 , in the composite magnetic material  90 , could be formed by partially sintering the ferritic material and using a pressurized impinging medium to open the opening  23  or  32 . The cross-section of the opening  23  or  32 , could be selected from a group comprising circular cross-section, polygonal cross-section, triangular cross-section, rectangular cross-section, to name a few.  
         [0119]    For some applications at least two of the sintered or unsintered dielectric forming metal/ferrite laminate magnet  90 , could be secured to each other such that the dielectric forming metal sheet  30 , sandwiches the dielectric material  40 .  
         [0120]    An alternate method of forming dielectric forming metal/ceramic laminate  90 , with discretely distributed magnets  94 , could be done by forming at least one opening  32 , in a dielectric forming metal sheet  30 , and securing at least one non-magnetic dielectric layer  40 , to the dielectric forming metal sheet  30 . One could then form at least one opening  52 , in the dielectric layer  40 , such as, by punching. The opening  52 , corresponds to at least one opening  32 , in the secured dielectric forming metal sheet  30 , to obtain a laminate structure like  55 . One could then build a multi-laminate structure consisting of at least two structures like  55 , with dielectric layers  40 , secured to each other with all holes aligned, and sintering the dielectric forming metal/dielectric layer assembly with holes to full densification. Subsequently, one could fill the holes in the multi-laminate structure with at least one permanent magnet material, preferably a ferrite in at least one opening in the dielectric forming metal/dielectric layers, extending through top and bottom surfaces of the sintered multi-laminate structure. At this point at least one opening is formed in the at least one permanent magnet material. Now, the dielectric forming metal/dielectric layers with the screened permanent magnet material is sintered, and thereby forming the dielectric forming metal/ceramic laminate with at least one discretely distributed magnet(s) as shown in FIG. 8.  
         [0121]    For some applications the dielectric forming metal sheet  30 , could act as an electron sink.  
         [0122]    For some applications the dielectric forming metal sheet  30 , could act as a heat spreader.  
         [0123]    The dielectric forming metal sheet  30 , could be used to act as a stiffener to prevent any distortion of the laminate magnet  90 .  
         [0124]    In another alternative method, one could build the structure  90 , as shown in FIG. 8, by using the conventional thin film approach like CVD (chemical vapor deposition) to form the permanent magnet material with at least one opening.  
         [0125]    Yet another alternate method of forming dielectric forming metal/ceramic laminate  90 , with discretely distributed magnets  94 , could be done by forming at least one opening  32 , in a dielectric forming metal sheet  30 , and securing at least one nonmagnetic dielectric layer  40 , to the dielectric forming metal sheet  30 . One could then form at least one opening  52 , in the dielectric layer  40 , such as, by punching. The opening  52 , corresponds to at least one opening  32 , in the secured dielectric forming metal sheet  30 , to obtain a laminate structure like  55 . One could then build a multi-laminate structure consisting of at least two structures like  55 , with dielectric layers  40 , secured to each other with all holes aligned, and sintering the metal/dielectric layer assembly with holes to full densification. Subsequently, one could deposit the permanent magnet material by CVD techniques on the side walls  71 , of the sintered openings  52 , to obtain the structure as shown in FIG. 8.  
         [0126]    While the present invention has been particularly described, in conjunction with a specific preferred embodiment, it is evident that many alternatives, modifications and variations will be apparent to those skilled in the art in light of the foregoing description. It is therefore contemplated that the appended claims will embrace any such alternatives, modifications and variations as falling within the true scope and spirit of the present invention.