Abstract:
A method is provided for conducting electrolysis at or below 1.23 V. The method comprises filling an electrolysis reactor having an aluminum anode and a copper cathode with a sufficient amount of solution such that at least a portion of the anode and the cathode are immersed in the solution; the solution comprising water, an electrolyte and a catalyst; and applying a voltage across the reactor of less than or equal to 1.23 V. The solution is comprised of water, aluminum sulfate and an ammonium salt. The method allows for total gas to be produced at a rate in excess of the theoretical maximum 1.06 l/min at a current of 93 amps.

Description:
CROSS-REFERENCE TO RELATED APPLICATIONS 
     This application claims priority to U.S. Provisional App. No. 61/155,809 filed Feb. 26, 2009 and which incorporated herein by reference. 
    
    
     STATEMENT REGARDING FEDERALLY SPONSORED RESEARCH OR DEVELOPMENT 
     Not Applicable. 
     TECHNICAL FIELD 
     This invention relates to electrolysis of water, and, in particular, to a method for carrying out electrolysis below 1.23 volts (V). 
     BACKGROUND OF THE INVENTION 
     Hydrogen exists in its atomic state throughout interstellar space, on the order of about one hydrogen atom per cubic meter of space. Hydrogen exists across Earth in the form of chemical compounds like carbohydrates, hydrocarbons, hydrogen halides, metal hydrides, and even comprises about 0.00005% by volume of the Earth&#39;s atmosphere. Considering the vast size of the Earth&#39;s atmosphere, even this small percentage represents a large amount of hydrogen gas. And finally, the most abundant hydrogen-containing chemical compound found on Earth is water. Water covers about 70% of the surface of the Earth, which indicates that there is plenty of hydrogen available from which to produce hydrogen gas (H 2 ). The challenge is figuring out how to extract the hydrogen from its known sources in an environmentally beneficial and energy economical manner. 
     Hydrogen containing compounds fall into two groups: 1) hydrogen bearing and 2) hydrogen and energy bearing. Water belongs in the first group. Compounds, such as methane, belong in the second group. 
     Methane will react with steam over a nickel catalyst at 1200° K and one atmosphere to produce hydrogen as follows:
 
CH 4  (g)+H 2 O (v)→CO (g)+3H 2  (g)  (1)
 
     This is a spontaneous reaction with a ΔG=−77.7 kJ/mole CH 4 . 
     When a spontaneous chemical reaction occurs, the decrease in free energy, −ΔG, corresponds to the maximum amount of useful work, W max , which can be obtained from the reaction:
 
−Δ G=W   max   (2)
 
     For a chemical reaction which is not spontaneous, ΔG is positive and W max  is negative. What this means is that work must be done on the system through an external source of energy to cause the reaction to occur. The minimum amount of work that must be done on the system is given by ΔG. 
     Water will theoretically react with four electrons influenced by an electric potential of 1.23 volts (V) to produce hydrogen as follows:
 
2H 2 O (l)           O 2  (g)+4H +  (aq)+4 e   −   (3)
 
4H +  (aq)+4 e   −           2H 2  (g)  (4)
 
Net: 2H 2 O (l)         O 2  (g)+2H 2  (g) ΔH=−48.5 kJ/mole H 2   (5)

     This is an exothermic reaction. 
     However, the theoretical 1.23 V is not achieved in commercial-scale electrolysis. In commercial scale electrolysis, water will react with four electrons influenced by an electric potential of ˜1.75 V to produce hydrogen as follows:
 
Net: 2H 2 O (l)           O 2  (g)+2H 2  (g) ΔH=+51.8 kJ/mole H 2   (6)

     Unlike the theoretical reaction (5), this is an endothermic reaction, and thus requires the input of energy for the reaction to be initiated and run. 
     The enthalpy of reaction (ΔH) for the theoretical reaction of water with four electrons at 1.23 V, described by equation (5), is a combination of the energy terms for both the forward electrolysis reaction and the reverse recombination reaction, the difference between the energy of formation for hydrogen from water (237.4 kJ/mole H 2  @ 1.23 V) and the heat of formation (ΔH f ) of water (285.9 kJ/mole H 2 O) (i.e., heat of combustion of one mole of H 2 ) or:
 
237.4 kJ/mole−285.9 kJ/mole=−48.5 kJ/mole H 2   (7)
 
     Because electrolysis in the real world does not operate at the theoretical minimum potential of 1.23 V, but instead operates at ˜1.75 V, we are forced to work with the endothermic reaction found in equation (6) instead of the exothermic reaction found in equation (5). 
     The forward electrolysis reaction described by equation (5) moves through a theoretical potential of 1.23 volts and yields the specific energy of formation for hydrogen found in equation (7):
 
(4 e   − /2 molecules H 2 )×(1.6022×10 −19  C/ e   − )×(1.23 J/C)=3.9414×10 −19  J/molecule H 2   (8)
 
(3.9414×10 −19  J/molecule H 2 )×(6.0221×1023 molecules/mole)=237.4 kJ/mole H 2   (9)
 
     The heat of formation (ΔH f ) for one mole of water is:
 
ΔH f  of H 2 O (liquid)=285.9 kJ/mole H 2 O  (10)
 
     Since there is one mole of H 2  for every mole of H 2 O:
 
ΔH combustion of H 2  (g)=285.9 kJ/mole H 2   (11)
 
     The enthalpy of reaction for the actual reaction of water with four electrons at 1.75 V, described by equation (6), is a combination of the energy terms for both the forward electrolysis reaction and the reverse recombination reaction:
 
337.7 kJ/mole (@1.75 V)−285.9 kJ/mole=+51.8 kJ/mole H 2   (12)
 
     The forward electrolysis reaction described by equation (6) moves through an actual potential of 1.75 volts and yields the specific energy of formation for hydrogen found in equation (12):
 
(4 e   − /2 molecules H 2 )×(1.6022×10 −19  C/ e   − )×(1.75 J/C)=5.6077×10 −19  J/molecule H 2   (13)
 
(5.6077×10 −19  J/molecule H 2 )×(6.0221×1023 molecules/mole)=337.7 kJ/mole H 2   (14)
 
     Because commercial-scale electrolysis of water takes place at ˜1.75 V, instead of the theoretical minimum potential of 1.23 V, the maximum system energy recovery from electrolysis achieved through the reverse recombination reaction found in equation (6) is:
 
(285.9 kJ/mole)/(337.7 kJ/mole)×100%=84.7%  (15)
 
     Hydrogen-powered fuel cells operate at 1.23 V of electrical potential. Therefore, the maximum system energy recovery that could be achieved by running a fuel cell from the hydrogen gas generated by the 1.75 V potential forward electrolysis reaction found in equation (6) is:
 
(237.4 kJ/mole)/(337.7 kJ/mole)×100%=70.3%,  (16)
 
     which is the ratio of 1.23 volts to 1.75 volts times 100%. 
     From an energy economical standpoint, equation (1) would be the more favorable route for producing hydrogen gas. However, there is a limited supply of methane and the oxidation of the carbon monoxide produces carbon dioxide, which is a greenhouse gas. From an environmentally beneficial standpoint, equation (6) would be the more favorable route for producing hydrogen. However, this route requires an external source of clean energy to maintain its environmental benefit. 
     The energy recovery of a system that combusts the hydrogen produced from the forward electrolysis reaction in equation (6) is 84.7%, as illustrated by equation (15). The energy recovery of a system that runs a fuel cell from the hydrogen produced from the forward electrolysis reaction in equation (6) is 70.3%, as illustrated by equation (16). These are two pathways that demonstrate that water is in fact a hydrogen carrier as opposed to a material like methane which is both a hydrogen and energy carrier. Therefore, the only way to increase the efficiency of converting electrical energy into hydrogen from water is to find a spontaneous or exothermic chemical reaction that could take place in the electrolysis cell and would couple the excess energy with the impressed voltage to lead to low splitting voltages—i.e., less than 1.23 volts. 
     BRIEF SUMMARY OF THE INVENTION 
     Briefly stated, and as set forth in the claims below, an electrolysis reactor and electrolytic solution are provided which allows for electrolysis at and below 1.23 V. 
     The reactor comprises a reactor vessel, an anode, a cathode, and a power supply in electrical communication with the cathode and anode. The power supply has a positive terminal and a negative terminal, with the positive terminal being in electrical communication with the anode and the negative terminal being in electrical communication with the cathode. The power supply can be a battery, a plurality of batteries connected in series or parallel, or an AC to DC converter power supply which is connected to a wall outlet. 
     The anode can be made from aluminum or an aluminum alloy and comprises at least one generally vertically extending pipe or rod. In one embodiment, the anode comprises an aluminum pipe. In another embodiment, the anode comprises a central aluminum pipe and at least one aluminum pipe or rod adjacent to the outer surface of the central aluminum pipe. In a further embodiment, the anode can be a central aluminum pipe with at least one aluminum pipe and rod adjacent to the outer surface of the central aluminum pipe. 
     The cathode can be made from copper or a copper alloy and comprises a coiled tube or solid wires, which surrounds the anode. The coil comprises about 3.67 to about 4.80 turns per vertical foot of the cathode. Thus, for example, if the copper cathode coil is 30″-36″ tall, the cathode would comprise 11-12 turns. Additionally, the copper coil comprises about 16.67° to about 20.80° of cathode tube or solid wires per vertical foot of the cathode. Thus, for example, for a cathode that is about 30″-36″ tall, the coiled tube or solid wires of the cathode has an overall length of about 50′-52′ (for a variable diameter coiled tube that is about 14″-19″ in diameter and constant diameter coiled solid wires that are 20″ in diameter). 
     The solution comprises water, an electrolyte, and a catalyst. For the copper cathode and the aluminum anode, the electrolyte can be aluminum sulfate and the catalyst can be an ammonium salt. The ammonium salt can be a halogen based tetrabutylammonium salt, and in a preferred embodiment, the tetrabutylammonium salt is tetrabutylammonium bromide (T-BAB). The solution can be about 0.10 M to about 0.20 M electrolyte and about 0.03 M to about 0.04 M catalyst. The electrolyte and catalyst are present in a ratio of about 3.3:1 to about 5.0:1 by molarity. 
     The method comprises conducting electrolysis by applying a voltage across the reactor of less than or equal to 1.23 V. The electrolysis can be performed at ambient (i.e., room) temperature and pressure. The current of the system is between about 0.1 amps and about 6.0 amps; and the resistance of the system is between about 0.1 ohms and about 0.2 ohms at these currents. We have found that this electrolysis method can separate water into its constituent elements (i.e., produce O 2  and H 2  gas) at voltage levels as low as 0.01 V, and once the procedure has started, will continue to produce gas even when the voltage is 0.00 V. Additionally, the total gas (i.e., both H 2  and O 2 ) is produced at a rate in excess of 1.06 l/min, which is greater than the theoretical maximum total gas flow rate for a current of 93 amps (A). 
    
    
     
       BRIEF DESCRIPTION OF THE SEVERAL VIEWS OF THE DRAWINGS 
         FIG. 1  is a perspective view of an electrolysis reaction tank; and 
         FIGS. 2-4  are schematic drawings of various anode configurations used in the electrolysis processes. 
     
    
    
     Corresponding reference numerals will be used throughout the several figures of the drawings. 
     DETAILED DESCRIPTION OF THE INVENTION 
     The following detailed description illustrates the invention by way of example and not by way of limitation. This description will clearly enable one skilled in the art to make and use the invention, and describes several embodiments, adaptations, variations, alternatives and uses of the invention, including what we presently believe is the best mode of carrying out the invention. Additionally, it is to be understood that the invention is not limited in its application to the details of construction and the arrangements of components set forth in the following description or illustrated in the drawings. The invention is capable of other embodiments and of being practiced or being carried out in various ways. Also, it is to be understood that the phraseology and terminology used herein is for the purpose of description and should not be regarded as limiting. 
     The electrolysis reactor  10  is shown in  FIG. 1 . The reactor comprises a 55 gallon cylindrical tank  12  having a side wall  12   a  and a bottom  12   b . A preferred tank has a tank wall thickness of 0.125″, an ID of 20″ and a height of 40″. A tank lid  14  is fitted over the tank. A channel is formed near the circumference of the lid to receive a ring such that an air-tight seal can be formed between the tank and the lid. Two 1″ tubes  22  and  23 (are fitted to the top of the tank to direct gases from the tank. The tube  22  defines an O 2  exit port for the electrolysis reactor; and the tube  23  defines an H 2  exit port  23  for the electrolysis reactor. 
     A cathode  18  is positioned in the tank. The cathode  18  is formed from a tube, and as seen, is formed into a spiral. As shown in the drawing, the cathode spiral generally has an hour-glass shape. However, the spiral could by cylindrically shaped, or could be convex, rather than concave. Other cathode shapes could be used as well. For example, the cathode could comprise a plurality of tubes which extend vertically into the tank. The cathode  18  that was used for the tests described below was comprised of a coiled 50′ copper tube having a wall thickness of 0.032″ and an OD of about 0.5″, providing for a cross-sectional area of about 0.3 cm 2 . The cathode coil was approximately 3′ tall and was comprised of 12 turns. In the embodiment shown, the coil had a diameter of about 19″ at its widest and a diameter of about 14″ at its narrowest point. The cathode coil is held erect in the tank by PVC rods and copper rods which run from the top to the bottom of the coil. In other embodiments, the coil was cylindrical in shape and had an outer diameter of about 20″, so that it would be received snuggly within the tank  12 . 
     An anode  20  is positioned in the tank. As seen in  FIG. 1 , the anode  20  extends through the center of the spiral defined by the cathode  18 . The anode is surrounded by a cylinder  25  to separate the O 2  and H 2  which are formed during electrolysis. The cylinder that was used was a clear plastic cylinder. The cylinder  25  serves to separate the O 2  and H 2  gases produced during electrolysis. The O 2  exit port tube  22  extends into the area surrounded by the cylinder  25 , and the H 2  exit port tube  23  extends into the area of the reaction tank outside of the cylinder  25 . 
     The anode  20  can be a single tube. Alternatively, the anode can have a configuration as shown in  FIGS. 2-4 , in which the anode comprises a central hollow tube  20   a  with one or more smaller diameter rods  20   b  positioned around the central tube. The additional rods  20   b  are solid and increase the effective surface area of the anode  20 . The central anode  20   a  used in the tests described below is formed from an aluminum pipe that is about 3 ft (about 0.9 m) long and has an outer diameter of about 8.5″ (about 21.7 cm) and a wall thickness of about 0.3″ (about 0.7 cm). The aluminum used for the central anode  20   a  was 6061 T6 aluminum alloy. The aluminum anode has a handle (not shown) at its top. The handle can be made from an aluminum rod to assist in the lifting of the anode in and out of the tank. The rod can, for example, be about 0.5″ (about 1.3 cm) in diameter. The aluminum anode  20  sits on a heavy plastic base 24 that lifts the anode  20  about 0.4″ (about 1.0 cm) from the bottom of the tank which allows for easy positioning of the anode in the tank. 
     A power supply is connected between anode and cathode to provide a portion of the energy for the electrolysis. As set forth below, the power supply can be batteries or a DC power supply. Other forms of power supplies could be used as well. The DC power supply used in several of the tests was a 1000 watt DC power supply that allows for 0.01 volt increments when selecting the voltage set point. This feature gives high resolution capability to the experimental process. The 1000 watt DC power supply produces a maximum of 130 amps across a voltage range of 0.00 volts to 7.66 volts. The power supply was a Xantrex XHR 7.5-130 1000 watt DC unit. 
     The solution received in the tank  10  is comprised of three distinct chemical compounds: water, aluminum sulfate, and tetrabutylammonium bromide (a catalyst/surfactant). Sufficient aluminum sulfate (alum) and tetrabutylamonium bromide (T-BAB) are added to the water such that they have molarities of about 0.1 M to about 0.2 M and 0.03 M to about 0.04 M, respectively. These three chemical compounds react inside the electrolysis reactor  10  in a manner which is not quite understood, but which results in the production of an insoluble, white crystalline precipitate material believed to be aluminum hydroxide (Al(OH) 3 ), and oxygen and hydrogen gas at voltages at or below 1.23 volts. Exactly how these two separate, yet coupled, reactions (i.e., production of Al(OH) 3  and production of H 2 ) occur is not fully understood but it is believed that the reaction that forms the aluminum hydroxide releases energy which couples with the applied voltage and allows for splitting of water at low voltages. In other words, the primary or driving reaction is the reaction occurring on the solid aluminum anode which produces aluminum hydroxide. Excess energy from this reaction adds or couples to the energy being supplied by the external power supply to provide sufficient energy to electrolyze water and break water into hydrogen gas and oxygen gas at low voltages. This is best explained as follows. 
     Based on experimental data, the electrolysis reactor system has demonstrated its ability to split water into hydrogen and oxygen gas at 1.00 volt and produces 2.6 amps of electrical current:
 
(2 molecules H 2 /4 e   − )×( e   − /1.6022×10 −19  C)×(mole/6.0221×1023 molecules)×(2.6 C/sec)=0.000013473 moles H 2 /sec  (17)
 
     By running the hydrogen gas generated at 1.00 volt and 2.6 amps, as shown in equation (17), through a fuel cell operating at 1.23 volts, as shown in equations (8) and (9), we can then calculate the output power from the electrolysis system which can then be compared to its input power:
 
(4 e   − /2 molecules H 2 )×(1.6022×10 −19  C/ e   − )×(1.23 J/C)=3.9414×10 −19  J/molecule H 2   (8)
 
(3.9414×10 −19  J/molecule H 2 )×(6.0221×1023 molecules/mole)=237.4 kJ/mole H 2   (9)
 
(1.3473×10 −5  moles H 2 /sec)×(237.4 kJ/mole H 2 )=3.1984902 J/sec=3.1984902 watts (output power)  (18)
 
     The input power is calculated as follows:
 
(1.00 volt)×(2.6 amps)=2.6 watts (input power)  (19)
 
Input−Output=Accumulation  (20)
 
     Substituting equations (18) and (19), for 1.00 volt, into equation (20) results in the following:
 
2.6 watts−3.2 watts=−0.6 watts  (21)
 
     Equation (21) shows that the primary reaction that forms the material believed to be aluminum hydroxide is in fact an exothermic reaction running at 0.6 watts of power, while the electrolysis reactor is running at an applied voltage of 1.00 volt. The primary chemical reaction runs without any energy input and produces an appreciable quantity of the insoluble, white crystalline material believed to be aluminum hydroxide. This reinforces the conclusion that this primary reaction is an exothermic reaction. 
     Based on experimental data, the electrolysis reactor system has demonstrated its ability to split water into hydrogen and oxygen gas at 0.50 volts and produces 0.8 amps of electrical current:
 
(2 molecules H 2 /4 e   − )×( e   − /1.6022×10 −19  C)×(mole/6.0221×1023 molecules)×(0.8 C/sec)=4.146×10 −6  moles H 2 /sec  (22)
 
     By running the hydrogen gas generated at 0.50 volts and 0.8 amps, as shown in equation (22), through a fuel cell operating at 1.23 volts, as shown in equations (8) and (9), the output power from the electrolysis system can then be calculated and compared to its input power:
 
(4 e   − /2 molecules H 2 )×(1.6022×10 −19  C/ e   − )×(1.23 J/C)=3.9414×10 −19  J/molecule H 2   (8)
 
(3.9414×10 −19  J/molecule H 2 )×(6.0221×1023 molecules/mole)=237.4 kJ/mole H 2   (9)
 
(0.000004146 moles H 2 /sec)×(237.4 kJ/mole H 2 )=0.984260400 J/sec=0.984260400 watts (output power)  (23)
 
     The input power is calculated as follows:
 
(0.50 volt)×(0.8 amps)=0.4 watts (input power)  (24)
 
     Substituting equations (23) and (24), for 0.50 volts, into equation (20) results in the following:
 
0.4 watts−1.0 watts=−0.6 watts  (25)
 
     Equation (25) further supports the idea that the reason the electrolysis reactor is able to achieve low voltage splitting of water into hydrogen and oxygen gas is because of the exothermic reaction that produces the material believed to be aluminum hydroxide. 
     The chemistry of this exothermic chemical reaction, as noted above, is not fully understood. However, the mechanisms believed to be occurring that result in the overall reaction which allows the electrolysis reactor to achieve its high level of performance under impressed (or applied) voltage are as follows.
 
Al 2 (SO 4 ) 3 +6H 2 O+2Al→2Al(OH) 3 +Al 2 (SO 4 ) 3 +3H 2   (26)
 
Al 2 (SO 4 ) 3 +6H 2 O→Al(OH) 3 +3H 2 SO 4   (27)
 
     Equations (26) and (27) are spontaneous reactions and together result in the following overall reaction:
 
Al 2 (SO 4 ) 3 +12H 2 O+2Al→4Al(OH) 3 +3H 2 SO 4 +3H 2   (28)
 
     It is believed that the sulfuric acid formed in equation (28) is neutralized in the following way:
 
4Al(OH) 3 +3H 2 SO 4 +3H 2             2Al(OH) 3 +Al 2 (SO 4 ) 3 +3H 2 +6H 2 O  (29)

     All of these reactions are occurring at the following concentration ranges: 
     0.10 M-0.20 M aluminum sulfate (alum) 
     0.03 M-0.04 M tetrabutylammonium bromide (surfactant/catalyst) 
     EXAMPLES 
     Example 1 
     26.83 cups of Al 2 (SO 4 ) 3  and 1500 g surfactant (tetrabutylammonium bromide) were added to 46 gallons of water (H 2 O) in the tank. The solution thus had an alum concentration of about 0.10 M. 
     The reactor initially operated at a reverse electromotive force (emf) of 0.70 V. The reverse emf then dropped to 0.60 V after using an older set of 5-1.5 V D-cell batteries connected in a parallel configuration. A new set of 5-1.5 V D-cell batteries connected in a parallel configuration were attached to the electrolysis tank. With the new batteries, the voltage in the system initially measured 1.30 V, then dropped to 1.25 V at 2.1 amps, yielding a resistance of 0.60 ohms. The system settled in at 1.20 V at 2.1 amps and 0.57 ohms. Gas production was robust even when the system voltage dropped to 1.05 V. 
     Example 2 
     The solution used was the same as for Example 1. The system was operated using 5-1.5 V D-cell batteries connected in a parallel configuration resulting in 1.15 V and a current of 1.0 amp. Gas production was very good. A rheostat was attached to the batteries, and the voltage was lowered to 0.50 V at 0.2-0.3 amps, yielding a system resistance of 2.00 ohms. Hydrogen and oxygen were electrolytically produced at the voltage of 0.50 V. The voltage was lowered to 0.20 V temporarily, but the system equilibrated at 0.50 V. Gas production at 0.50 V was light but consistent at steady state. The reactor was able to split water into hydrogen and oxygen at 0.50 V. When the rheostat was removed, voltage returned to 1.15 V at 1.5 amps, yielding a system resistance of 0.77 ohms. After removing the applied voltage, tapping on the outside of the tank released the residual hydrogen from the cathode which resulted in the reverse emf returning to 0.60 V. After 10-15 minutes, the reverse emf returned to 0.50 V which was the initial reading at the beginning of the experiment. 
     Example 3 
     In this example, the solution was the same as in Example 1. The system was operated using 5-1.5 V D-cell batteries connected in a parallel configuration resulting in 1.15 V and a current of 1.5 amps. Gas production was very good. Initially, the reverse emf was 0.50 V. By tapping the side of the tank, hydrogen gas was released from the cathode and the reverse emf increased to about 0.60 V. 
     The same experiment was run using different power sources. In a first test, two 1.5 V D-cell batteries were placed in series and the voltage across the tank increased to 1.60 V at 1.8 amps. In a second test, three 6 V battery chargers were placed in parallel, and voltage across the tank decreased to 1.20 V at 1.9 amps. Then one 12 V battery charger was connected across the tank and the voltage increased to 6.50 V at 34.9 amps (switch was on 10 amps). In a last test, the 12 V battery charger was again connected across the tank, and the voltage measured 7.50 V at 42.1 amps (with the switch set to 50 amps). In all four tests, gas production was excellent. 
     Example 4 
     In this example, the solution was the same as in Example 1. The system was operated using 5-1.5 V D-cell batteries connected in a parallel configuration resulting in 1.15 V and a current of 1.5 amps. Gas production was very good. Initially, the reverse emf was 0.25 V. The reverse emf was low due to the large quantities of hydrogen gas on the cathode from the high amperage runs of Example 3. 
     In a second test, two 1.5 V D-cell batteries were placed in series across the tank. The voltage in the tank increased to 1.60 V at 1.8 amps. Gas production was very good. In a third test, five 1.5 V D-cell batteries were then placed in series across the tank. The voltage measured 1.30 V at 2.8 amps. Gas production remained very good. In a fourth test, three 6 V battery chargers were placed in parallel, and voltage across the tank decreased to 1.10 V at 1.7 amps. Production of gas was very good. In a final test, one 12 V battery charger was placed across the electrodes. The voltage across the tank was 6.40 V at 34.7 amps (switch at 10 amps), and 7.50 V at 42.5 amps (with the switch at 50 amps). Production of gas was excellent. 
     AC current was 7.0 amps at circuit voltage (˜115V) for an % c of about 40%. On several occasions, the volt-ohm-amp meter (VOAM) measured 0.50 V when the emf was removed. 
     A clear plastic tube  25  was placed over the anode during a later test using the 5-1.5 V D-cell batteries connected in series as the power supply. The 5-1.5 V D-cell batteries in series gave rise to 5.20 V at 0.7 amps. When the plastic tube was removed, the voltage dropped to 1.20 V at 2.2 amps. The plastic tube thus acted as a resistor in the circuit. To reduce the electrical resistance, the plastic tube was subsequently replaced with a cloth covered “skeleton” plastic structure. 
     Example 5 
     To 50 gallons of water, sufficient amounts of aluminum sulfate and tetrabutylammonium bromide (T-BAB) were added such that the solution was 0.12 M Al 2 (SO 4 ) 3  and 0.03 M T-BAB. This amounted to about 7761 g Al 2 (SO 4 ) 3  and about 1828 g T-BAB. The solution was placed in the electrolysis reactor tank. The anode was as described above (i.e., the single 36″ tall×8 9/16″ OD tube). The cathode was also as described above. The anode and cathode coil were both 36″ tall. The power supply was a Xantrex XHR 7.5-130 1000 watt DC power supply. This power supply allowed for accurate control of the voltage within increments of 0.01 V. 
     The following voltages and amps were achieved across the tank as set forth below in Table I. 
     
       
         
               
               
               
             
               
               
               
               
               
             
           
               
                 TABLE I 
               
               
                   
               
               
                   
                   
                 Ave. 
               
               
                 Volts 
                 Amps 
                 Amps 
               
               
                   
               
             
             
               
                   
               
             
          
           
               
                 1.23 
                 4.4 
                 4.5 
                 4.5 
                 4.5 
               
               
                 1.00 
                 2.8 
                 3.0 
                 2.9 
                 2.9 
               
               
                 0.75 
                 1.4 
                 1.8 
                 1.4 
                 1.5 
               
               
                 0.50 
                 0.9 
                 1.0 
                 1.0 
                 1.0 
               
               
                 0.23 
                 0.6 
                 0.6 
                 0.6 
                 0.6 
               
               
                 0.10 
                 0.3 
                 0.3 
                 0.4 
                 0.3 
               
               
                   
               
             
          
         
       
     
     Hydrogen and oxygen gases were produced at each voltage level. Thus, electrolysis was achieved at voltages as low as 0.10 V. 
     Example 6 
     To 50 gallons of water, sufficient amounts of aluminum sulfate and tetrabutylammonium bromide (T-BAB) were added such that the solution was 0.12 M Al 2 (SO 4 ) 3  and 0.03 M T-BAB, which is the same solution that was prepared in Example 5. The anode was described as above. The cathode was formed from solid ½″ OD, 19 strand, 4/0 HC, 52′ copper coil (with 11 turns). The anode was 36″ tall and the cathode coil was 30″ tall. The power supply was a Xantrex XHR 7.5-130 1000 watt DC power supply. 
     The following voltages and amps were achieved across the tank as set forth below in Table II. 
     
       
         
               
               
               
               
               
               
             
               
               
               
               
               
               
               
               
             
           
               
                   
                 TABLE II 
               
               
                   
                   
               
               
                   
                   
                   
                 Ave. 
                 Amps 
                   
               
               
                   
                   
                 Amps 
                 Amps 
                 Anode 
                 % Increase in 
               
               
                   
                 Volts 
                 Anode I 
                 Anode I 
                 II 
                 Amperage 
               
               
                   
                   
               
             
             
               
                   
               
             
          
           
               
                   
                 1.23 
                 3.6 
                 3.4 
                 3.5 
                 3.5 
                 5.0 
                   43% 
               
               
                   
                 1.00 
                 2.2 
                 2.1 
                 2.2 
                 2.2 
                 3.2 
                   48% 
               
               
                   
                 0.75 
                 1.3 
                 1.4 
                 1.3 
                 1.3 
                 1.7 
                   28% 
               
               
                   
                 0.50 
                 0.8 
                 1.0 
                 0.9 
                 0.9 
                 1.0 
                   11% 
               
               
                   
                 0.23 
                 0.4 
                 0.5 
                 0.4 
                 0.4 
                 0.4 
                  −8% 
               
               
                   
                 0.10 
                 0.3 
                 0.3 
                 0.3 
                 0.3 
                 0.3 
                    0% 
               
               
                   
                   
               
             
          
         
       
     
     The amperage readings under the column “Anode I” use an anode as described above (i.e., a 3′ long pipe having an 8 9/16″ OD and a wall thickness of 9/32″ made from 6061 T6 aluminum alloy). The anode for the first runs had an external surface area of 968.4 in 2 . The amperage readings under the column “Anode II” are the result of a second set of runs after inserting four 3″ OD, 6061 T6 511 aluminum rods that are 36″ tall at 0°, 90°, 180°, and 270° around the perimeter of the anode and in contact with it, as seen in  FIG. 2 . Four gallons of solution had to be removed from the tank due to the volume change resulting from the placement of the four 3″ OD aluminum rods into the tank (i.e., Archimedes&#39; Principle). The external surface area of the anode along with the four external rods was approximately 2325.6 in 2 . Thus, these rods effectively increased the surface area of the anode by approximately 140% (or about 35% per external rod). As can be seen, for voltages of 0.50 V and above, the increase in surface area of the anode significantly increased the amperage of the system. 
     Hydrogen and oxygen gases were produced at each voltage level. Thus, electrolysis was achieved at voltages as low as 0.10 V. 
     Example 7 
     The electrolysis reactor tank contained the 46 gallons of solution, as described in Example 6, at 0.12 M Al 2 (SO 4 ) 3  and 0.03 M T-BAB. This amounted to about 7140 g Al 2 (SO 4 ) 3  and about 1682 g T-BAB. The anode was comprised of the 3′ tall, 8 9/16″ OD, 6061 T6 alloy aluminum pipe with four 36″ tall, 3″ OD, 6061 T6 511 alloy aluminum rods placed at 0°, 90°, 180°, and 270° around the perimeter of the 8 9/16′″ OD aluminum pipe, and a fifth 36″ tall, 3″ OD, 6061 T6 511 alloy aluminum rod in contact with the interior wall of the aluminum pipe (as shown in  FIG. 3 ). The cathode was formed from solid ½″ OD, 19 strand, 4/0 HC, 52′ copper coil (with 11 turns). The anode was 36″ tall and the cathode coil was 30″ tall. The power supply was a Xantrex XHR 7.5-130 1000 watt DC power supply. 
     The following voltage and amps were achieved across the tank as set forth below in Table III. 
     
       
         
               
               
               
               
               
             
           
               
                 TABLE III 
               
               
                   
               
               
                   
                   
                 Amps 
                 Amps 
                   
               
               
                   
                 Volts 
                 Anode I 
                 Anode II 
                 % increase 
               
               
                   
               
             
             
               
                   
                 1.23 
                 4.6 
                 5.0 
                 8.7% 
               
               
                   
               
             
          
         
       
     
     In the table above, the column “Anode I” used an anode as just described above (i.e., as shown in  FIG. 3 ). The column “Anode II” denotes a second run in which the fifth 3″ OD aluminum rod was removed from the interior of the aluminum pipe and was positioned next to the exterior rod positioned at 270° (as seen in  FIG. 4 ). This effectively increased the external surface area of the anode. In this example, the external surface area of the anode from “Anode I” to “Anode II” was increased from about 2325.6 in 2  by 339.3 in 2  to about 2664.9 in 2  for an increase in external anode surface area of about 14.6%. The increased surface area increased the amperage by 0.4 amps, or about 8.7%. Comparing these results with the results from Example 6 supports the conclusion that each 3″ OD, 3′ long aluminum rod increased the current by about 0.4 amps. Inasmuch as the production of hydrogen and oxygen via electrolysis is dependent upon current, the increase in current also leads to an increase in hydrogen and oxygen production. 
     Example 8 
     The electrolysis reactor tank contained the 46 gallons of solution, as described in Example 7, at 0.12 M Al 2 (SO 4 ) 3  and 0.03 M T-BAB. The anode was comprised of the 3′ tall, 8.5625″ OD, 6061 T6 alloy aluminum pipe with five 36″ tall, 3″ OD, 6061 T6 511 alloy aluminum rods placed at 0°, 90°, 180°, ˜270° and ˜270° around the perimeter of the 8.5625″ OD aluminum pipe, and in contact with it. That is, the anode was generally as shown in  FIG. 4 . The cathode was formed from solid ½″ OD, 19 strand, 4/0 HC, 52′ copper coil (with 11 turns). The anode was 36″ tall and the cathode coil was 30″ tall. The power supply was a Xantrex XHR 7.5-130 1000 watt DC power supply. 
     The following voltage and amps were achieved across the tank as set forth below in Table IV. 
     
       
         
               
               
               
             
           
               
                 TABLE IV 
               
               
                   
               
               
                   
                 Amps 
                 Amps 
               
               
                 Volts 
                 Anode I 
                 Anode II 
               
               
                   
               
             
             
               
                 1.23 
                 5.0 
                 3.1 
               
               
                   
               
             
          
         
       
     
     In the column “Anode I”, the anode was as just described above. In the column “Anode II”, a second run was conducted in which the five aluminum rods were removed from the tank and the four gallons of solution were added back into the tank, resulting in 50 gallons of solution in the tank. Removal of the rods from the exterior of the anode reduced the surface area of the anode from about 2664.9 in 2  to about 968.4 in 2 . Accordingly, the amperage was reduced as well. As seen in Table IV, the amperage was reduced by about 1.9 amps for a current reduction of 0.38 (or about 0.4) amps per rod. 
     The results of Examples 6, 7, and 8 in which the surface area of the anode was altered, shows that the electrical current and attendant hydrogen and oxygen gas production at and below 1.23 V (actual value) can be increased by increasing the surface area of the anode. 
     Example 9 
     To 50 gallons of water, sufficient amounts of aluminum sulfate and tetrabutylammonium bromide (T-BAB) were added such that the solution was 0.14 M Al 2 (SO 4 ) 3  and 0.04 M T-BAB. The solution was placed in the electrolysis reactor tank. The anode was comprised of the 3′ tall, 8 9/16″ OD, 6061 T6 alloy aluminum pipe. The cathode was formed from solid ½″ OD, 19 strand, 4/0 HC, 52′ copper coil (with 11 turns). The anode was 36″ tall and the cathode coil was 36″ tall. The power supply was a Xantrex XHR 7.5-130 1000 watt DC power supply. 
     The following voltages and amps were achieved across the tank as set forth below in Table V. 
     
       
         
               
               
               
             
               
               
               
               
               
             
           
               
                 TABLE V 
               
               
                   
               
               
                   
                   
                 Ave. 
               
               
                 Volts 
                 Amps 
                 Amps 
               
               
                   
               
             
             
               
                   
               
             
          
           
               
                 1.23 
                 3.8 
                 4.0 
                 4.1 
                 4.0 
               
               
                 1.00 
                 2.6 
                 2.9 
                 3.0 
                 2.8 
               
               
                 0.75 
                 1.5 
                 1.8 
                 1.7 
                 1.7 
               
               
                 0.50 
                 0.9 
                 0.8 
                 0.9 
                 0.9 
               
               
                 0.23 
                 0.5 
                 0.4 
                 0.5 
                 0.5 
               
               
                 0.10 
                 0.3 
                 0.3 
                 0.3 
                 0.3 
               
               
                 0.08 
                 0.3 
                 0.3 
                 0.3 
                 0.3 
               
               
                 0.06 
                 0.3 
                 0.2 
                 0.3 
                 0.3 
               
               
                 0.04 
                 0.2 
                 0.2 
                 0.2 
                 0.2 
               
               
                 0.02 
                 0.2 
                 0.2 
                 0.2 
                 0.2 
               
               
                 0.01 
                 0.2 
                 0.2 
                 0.2 
                 0.2 
               
               
                   
               
             
          
         
       
     
     Hydrogen was produced at all voltage levels. 
     Example 10 
     The electrolysis reactor tank contained the 50 gallons of solution, as described in Example 9, at 0.14 M Al 2 (SO 4 ) 3  and 0.04 M T-BAB. The anode was comprised of the 3′ tall, 8.5625″ OD, 6061 T6 alloy aluminum pipe with four 2⅞″ OD, 6061 T6 alloy aluminum pipes that are 36″ tall placed at 0°, 90°, 180°, and 270° around the external perimeter of the 8.5625″ OD pipe and in contact with the pipe. The cathode was formed from solid ½″ OD, 19 strand, 4/0 HC, 52′ copper coil (with 11 turns). The anode was 36″ tall and the cathode coil was 36″ tall. The power supply was a Xantrex XHR 7.5-130 1000 watt DC power supply. 
     The following voltages and amps were achieved across the tank as set forth below in Table VI. 
     
       
         
               
               
               
             
               
               
               
               
               
             
           
               
                 TABLE VI 
               
               
                   
               
               
                   
                   
                 Ave. 
               
               
                 Volts 
                 Amps 
                 Amps 
               
               
                   
               
             
             
               
                   
               
             
          
           
               
                 1.23 
                 4.9 
                 4.9 
                 4.9 
                 4.9 
               
               
                 1.00 
                 3.7 
                 3.0 
                 3.5 
                 3.4 
               
               
                 0.75 
                 1.9 
                 2.3 
                 2.0 
                 2.1 
               
               
                 0.50 
                 0.9 
                 1.4 
                 0.9 
                 1.1 
               
               
                 0.23 
                 0.5 
                 0.7 
                 0.5 
                 0.6 
               
               
                 0.10 
                 0.3 
                 0.4 
                 0.3 
                 0.3 
               
               
                 0.08 
                 0.3 
                 0.4 
                 0.3 
                 0.3 
               
               
                 0.06 
                 0.3 
                 0.3 
                 0.3 
                 0.3 
               
               
                 0.04 
                 0.2 
                 0.3 
                 0.2 
                 0.2 
               
               
                 0.02 
                 0.2 
                 0.2 
                 0.2 
                 0.2 
               
               
                 0.01 
                 0.2 
                 0.2 
                 0.2 
                 0.2 
               
               
                   
               
             
          
         
       
     
     Hydrogen was produced at all voltage levels. 
     Example 11 
     The electrolysis reactor tank contained the 50 gallons of solution, as described in Example 10, at 0.14 M Al 2 (SO 4 ) 3  and 0.04 M T-BAB. The anode was comprised of the 3′ tall, 8.5625″ OD, 6061 T6 alloy aluminum pipe with four 2⅞″ OD, 6061 T6 alloy aluminum pipes that are 36″ tall placed at 0°, 90°, 180°, and 270° around the external perimeter of the 8.5625″ OD pipe and in contact with the pipe. The cathode was formed from solid ½″ OD, 19 strand, 4/0 HC, 52′ copper coil (with 11 turns). The anode was 36″ tall and the cathode coil was 36″ tall. The power supply was a Xantrex XHR 7.5-130 1000 watt DC power supply. 
     The following voltages and amps were achieved across the tank as set forth below in Table VII. 
     
       
         
               
               
               
             
               
               
               
               
               
             
           
               
                 TABLE VII 
               
               
                   
               
               
                   
                   
                 Ave. 
               
               
                 Volts 
                 Amps 
                 Amps 
               
               
                   
               
             
             
               
                   
               
             
          
           
               
                 1.23 
                 5.3 
                 5.2 
                 5.3 
                 5.3 
               
               
                 1.00 
                 3.7 
                 3.3 
                 3.6 
                 3.5 
               
               
                 0.75 
                 2.3 
                 2.5 
                 2.3 
                 2.4 
               
               
                 0.50 
                 1.4 
                 1.5 
                 1.4 
                 1.4 
               
               
                 0.23 
                 0.6 
                 0.7 
                 0.6 
                 0.6 
               
               
                 0.10 
                 0.4 
                 0.5 
                 0.4 
                 0.4 
               
               
                 0.08 
                 0.4 
                 0.5 
                 0.4 
                 0.4 
               
               
                 0.06 
                 0.4 
                 0.4 
                 0.4 
                 0.4 
               
               
                 0.04 
                 0.3 
                 0.4 
                 0.3 
                 0.3 
               
               
                 0.02 
                 0.3 
                 0.3 
                 0.3 
                 0.3 
               
               
                 0.01 
                 0.3 
                 0.3 
                 0.3 
                 0.3 
               
               
                   
               
             
          
         
       
     
     Hydrogen was produced at all voltage levels. 
     In Examples 10 and 11, the anode, cathode, and solution for Examples 10 and 11 were the same, such that Examples 10 and 11 were operated under substantially the same conditions. However, it will be noted that the amps produced in Example 11 were slightly higher at each voltage level than in Example 10. The experiments for the Example 11 results were run the day after the Example 10 experiments were run. After the Example 9 experiments were run, the new anode was placed in the tank, and the tank was allowed to run at 1.00 V for about four hours before being turned off for the night. Before being turned off, the amp meter was reading 4.0 amps (which is noted to be higher than the amps obtained during the day experiments). The increase in amperage was due to the extra reaction surface area provided by the new anode. Before turning the system off, the voltage was increased to 1.23 V, and the current settled in at 5.9 amps. The next day (the day the Example 10 experiments were run), when the system was turned on, the current climbed to 4.9 amps (at 1.23 volts), rather than the 5.9 amps that was recorded the previous evening. Even though the conditions for the Example 10 and Example 11 experiments were substantially the same, the performance improved for an unknown reason. This might be attributable to the system having been run for a period of time prior to beginning the Example 11 experiments. It is notable that the day after the Example 11 experiments were run, the system was able to produce hydrogen at a system current of 0.3 amps, even though the voltage was set at 0.00 volts. 
     Example 12 
     The electrolysis reactor tank was filled with 50 gallons of water. Sufficient Al 2 (SO 4 ) 3  and T-BAB were added to the water so that the solution was 0.20 M Al 2 (SO 4 ) 3  and 0.04 M T-BAB. The anode was comprised of the 3′ tall, 8.5625″ OD, 6061 T6 alloy aluminum pipe with four 2⅞″ OD, 6061 T6 alloy aluminum pipes that were 36″ tall and placed at 0°, 90°, 180°, and 270° around the external perimeter of the 8.5625″ OD pipe and in contact with the pipe. That is, the anode was as shown in  FIG. 2 . The cathode was formed from solid ½″ OD, 19 strand, 4/0 HC, 52′ copper coil (with 11 turns). The turns of the coil were sized (in diameter) and spaced apart vertically, such that the cathode would be received in the tank, surrounding the anode, and have a height of 36″. The power supply was a Xantrex XHR 7.5-130 1000 watt DC power supply. 
     The following voltages and amps were achieved across the tank as set forth below in Table VIII. 
     
       
         
               
               
               
             
               
               
               
               
               
             
           
               
                 TABLE VIII 
               
               
                   
               
               
                   
                   
                 Ave. 
               
               
                 Volts 
                 Amps 
                 Amps 
               
               
                   
               
             
             
               
                   
               
             
          
           
               
                 1.23 
                 5.7 
                 5.4 
                 5.3 
                 5.5 
               
               
                 1.00 
                 3.2 
                 3.2 
                 3.2 
                 3.2 
               
               
                 0.75 
                 1.8 
                 1.8 
                 1.8 
                 1.8 
               
               
                 0.50 
                 0.9 
                 1.0 
                 0.9 
                 0.9 
               
               
                 0.23 
                 0.4 
                 0.6 
                 0.4 
                 0.5 
               
               
                 0.10 
                 0.3 
                 0.3 
                 0.3 
                 0.3 
               
               
                 0.08 
                 0.3 
                 0.3 
                 0.3 
                 0.3 
               
               
                 0.06 
                 0.2 
                 0.2 
                 0.3 
                 0.2 
               
               
                 0.04 
                 0.2 
                 0.2 
                 0.2 
                 0.2 
               
               
                 0.02 
                 0.2 
                 0.2 
                 0.2 
                 0.2 
               
               
                 0.01 
                 0.1 
                 0.1 
                 0.2 
                 0.1 
               
               
                 0.00 
                 0.1 
                 0.1 
                 0.1 
                 0.1 
               
               
                   
               
             
          
         
       
     
     Hydrogen was produced at all voltage levels. This example demonstrates that even when no voltage is being supplied to the reactor from the power supply, the electrolysis of water will continue. From this data, it is believed that the chemical reactions as set forth above in equations (26) and (27) provide sufficient energy to the system to allow the system to continue the electrolysis of water in the absence of voltage from the external power source after the power source has been shut down. 
     Example 13 
     The electrolysis reactor tank was filled with 50 gallons of water. Sufficient Al 2 (SO 4 ) 3  and T-BAB were added to the water so that the solution was 0.20 M Al 2 (SO 4 ) 3  and 0.04 M T-BAB. The anode was comprised of (1) the 3′ tall, 8.5625″ OD, 6061 T6 alloy aluminum pipe, (2) four 2⅞″ OD, 6061 T6 alloy aluminum pipes that were 36″ tall and placed at 0°, 90°, 180°, and 270° around the external perimeter of the 8.5625″ OD pipe, and (3) four 3″ OD, 6061 T6 511 alloy aluminum rods that were 36″ tall and placed at 45°, 135°, 225°, and 315°. The four 2⅞″ tubes and four 3″ rods were all 36″ tall and were placed in the noted positions around the external perimeter of the 8.5625″ OD pipe and in contact with the pipe. With the four extra rods, the external surface area of the anode was about 3626.2 in 2 . The cathode was formed from solid ½″ OD, 19 strand, 4/0 HO, 52′ copper coil (with 11 turns). The turns of the coil were sized (in diameter) and spaced apart vertically, such that the cathode would be received in the tank, surrounding the anode, and have a height of 36″. The power supply was a Xantrex XHR 7.5-130 1000 watt DC power supply. 
     The following voltages and amps were achieved across the tank as set forth below in Table IX. 
     
       
         
               
               
               
             
               
               
               
               
               
             
           
               
                 TABLE IX 
               
               
                   
               
               
                   
                   
                 Ave. 
               
               
                 Volts  
                 Amps 
                 Amps 
               
               
                   
               
             
             
               
                   
               
             
          
           
               
                 1.23 
                 6.0 
                 5.8 
                 5.8 
                 5.9 
               
               
                 1.00 
                 3.7 
                 3.7 
                 3.7 
                 3.7 
               
               
                 0.75 
                 2.1 
                 2.1 
                 1.9 
                 2.0 
               
               
                 0.50 
                 1.3 
                 1.5 
                 1.2 
                 1.3 
               
               
                 0.23 
                 0.8 
                 0.9 
                 0.7 
                 0.8 
               
               
                 0.10 
                 0.5 
                 0.5 
                 0.4 
                 0.5 
               
               
                 0.08 
                 0.4 
                 0.4 
                 0.4 
                 0.4 
               
               
                 0.06 
                 0.4 
                 0.3 
                 0.3 
                 0.3 
               
               
                 0.04 
                 0.3 
                 0.3 
                 0.3 
                 0.3 
               
               
                 0.02 
                 0.3 
                 0.3 
                 0.3 
                 0.3 
               
               
                 0.01 
                 0.3 
                 0.3 
                 0.2 
                 0.3 
               
               
                 0.00 
                 0.2 
                 0.2 
                 0.2 
                 0.2 
               
               
                   
               
             
          
         
       
     
     Hydrogen was produced at all voltage levels. This example again demonstrated that even when no voltage is being supplied to the reactor from the power supply, the electrolysis of water will continue. 
     Other Observations 
     In various tests, a maximum current of 93 amps was achieved. At this current level, the theoretical maximum production of total gas production (i.e., production of both H 2  and O 2 ) would be 1.06 l/min. However, a total gas flow rate of greater than 1.1 l/min was being produced. Thus, not only did the reactions of equations (26) and (27) enable electrolysis of water (and hence production of hydrogen and oxygen gases) at low voltage levels, they increased the production of gas such that the gas production exceeded the maximum theoretical production rate that could be achieved using electricity alone to power the electrolysis of water. The above experiments were conducted over a period of many months. During the entire time, the anodes remained immersed in solution. The aluminum anode spent some 28 months in solution. At the start of this 28 month time period, the 8 9/16″ aluminum anode had a wall thickness of 4.5/16″ (i.e., 9/32″ or ˜7.1 mm); and at the end of this period, the wall thickness was still 4.5/16″. There was pitting on the surface of the aluminum anode but for all intents and purposes the anode is intact. Based on this, it is thought that equation 26 cannot be the only exothermic reaction at play. If it were, more degradation in the aluminum anode should have been observed. 
     As various changes could be made in the above constructions without departing from the scope of the invention, it is intended that all matter contained in the above description or shown in the accompanying drawings shall be interpreted as illustrative and not in a limiting sense.