Abstract:
An active semiconductor device, such as, buried heterostructure semiconductor lasers, LEDs, modulators, photodiodes, heterojunction bipolar transistors, field effect transistors or other active devices, comprise a plurality of semiconductor layers formed on a substrate with one of the layers being an active region. A current channel is formed through this active region defined by current blocking layers formed on adjacent sides of a designated active region channel where the blocking layers substantially confine the current through the channel. The blocking layers are characterized by being an aluminum-containing Group III-V compound, i.e., an Al-III-V layer, intentionally doped with oxygen from an oxide source. Also, wet oxide process or a deposited oxide source may be used to laterally form a native oxide of the Al-III-V layer. An example of a material system for this invention useful at optical telecommunication wavelengths is InGaAsP/InP where the Al-III-V layer comprises InAlAs:O or InAlAs:O:Fe. Other materials for the blocking layers may be InAlGaAs or alternating layers or alternating monolayers of AlAs/InAs. Thus, the O-doped blocking layers may be undoped, impurity doped or co-doped with Fe.

Description:
REFERENCE TO RELATED APPLICATION  
       [0001]    This application claims priority of provisional application, Serial No. 60/340,319, filed Dec. 14, 2001, which provisional application is incorporated herein by its reference. 
     
    
     
       BACKGROUND OF THE INVENTION  
         [0002]    1. Field of the Invention  
           [0003]    This invention relates generally to active semiconductor devices, such as photonic, electronic or optoelectronic devices, and more particularly to buried heterostructure active devices, such as Group III-V buried heterostructure semiconductor lasers, LEDs, modulators, photodiodes, heterojunction bipolar transistors, field effect transistors or other active devices for preventing current flow through designated regions of the device, such as high resistance current blocking layers on adjacent sides of the active region of such devices to provide for current confinement to the active region to enhance device efficiency.  
           [0004]    2. Description of the Related Art  
           [0005]    It is well known in the art to provide blocking layers for current confinement to the active region in buried heterostructure (BH) lasers or other such semiconductor active devices employed, for example, as an optical transmitter source, modulator or optical amplifier in optical telecommunication systems. Such a BH device employs junction blocking or reverse bias layers or blocking junctions, such as combinations of p-InP/n-InP layers. An example of such a blocking layer combination is disclosed in U.S. Pat. Nos. 4,470,143 and 5,148,439. However, due to intrinsic capacitance, these types of blocking junctions may not be readily adaptable for bit rates higher than 2.5 Gb/s. The particular problem with respect to these types of blocking layers is that the reverse biased p-n blocking junction possess a significant junction capacitance, limiting the high speed characteristics of such devices. Also, the reverse biased p-n junction in these devices may possess leakage paths leading to high thresholds in the case of laser diodes as well as low quantum efficiencies in all such devices.  
           [0006]    Another type of blocking layer is made semi-insulating through the addition of one or combinations of Fe, Co, Ni, as a dopant, for example, in AlGaInAs, AlInAs, InP or InGaAsP. In particular, Fe is employed as a high resistance blocking layer such as disclosed in U.S. Pat. Nos. 4,660,208 and 4,888,624. Combination layers of Fe doped InP layers with p or n doped InP layers may be employed as illustrated in European Patent Application No. 0314372. As illustrated in these patents and publications, InP:Fe layers are utilized as blocking layers in BH lasers for current confinement to the active region of a semiconductor active device. Other Group III-V alloys, such as, for example, InGaAsP:Fe, may be employed as a blocking layer as illustrated in U.S. Pat. No. 6,028,875. The use of Fe doped Group III-V blocking layers is a well established current blocking technology but plagued by problems. In particular, Fe doped layers have poor stability so that Fe readily diffuses into adjacent semiconductor layers or materials, particularly the active region of a device. This diffusion process can occur more particularly during subsequent high temperature processing steps. European Patent Application No. 0208209 suggests a solution to this problem with the provision of an undoped spacer layer formed between the active region and adjacent layers and a second-growth InP:Fe, current blocking layer. Such a spacer layer prevents contamination of the active region by the impurity Fe in the adjacent, high resistive current blocking layer since the spacer layer functions as a diffusion inhibitor. Also, the spacer layer is made thin so that the leakage current outside of the buried active region is small. However, there is no mention in this publication of what the material might be for such a spacer layer.  
           [0007]    A more recent approach for providing resistive layers to function as current blocking layers has been reported by S. Bouchoule et al. in an article entitled, “New Buried Heterostructure using MOVPE Selective Regrowth of Semi-Insulating (SI-) InAlAs for Low Capacitance Optical Sources”,  Proceedings of The  14 TH    Annual Meeting of the IEEE Lasers  &amp;  Electro - Optics Society  (LEOS), La Jolla, San Diego, Calif., pp. 883-884, Nov. 14-15, 2001. SI-InAlAs layers were grown by MOVPE under growth conditions to obtain high resistivity with low capacitance and lattice matched to InP substrates. Under optimized conditions, a resistivity of 2×10 7  Ωcm was achieved. Similar results are reported in U.S. Pat. No. 5,679,603, in particular, in the discussion of embodiments 1-3 of that patent where the oxygen forms a deep donor level which is naturally taken into the crystal from residual oxygen and H 2 O in the MOCVD reactor and/or contamination of their source materials with oxygen utilized to growth Group III-V materials. Resistivity values of 5×10 4  Ωcm are indicated. However, for good quantum efficiencies with low current leakage, the resistivity required for the current blocking layer must be much higher than these values, preferably at least about 10 6  to 10 7  Ωcm or higher. U.S. Pat. No. 5,679,603 reports values in the range of a resistivity of 10 3  Ωcm to 10 8  Ωcm for InAlAs and indicates this to be a sufficiently high resistance compound semiconductor for current blocking layers. However, it would be desirable to obtain repeatable, maintained high resistivity values with even lower current leakage values in a narrow, upper resistivity range, e.g., about 10 6  to 10 8  Ωcm.  
           [0008]    Generally, the resistivity for semi-insulating Group III-V or SI-III-V epitaxial growths can be achieved through background doping using low growth temperatures, such as below 550° C. As an example, in U.S. Pat. No. 5,804,840 to Ochi et al., high resistance or SI-InAlAs layers were achieved with growth temperatures of about 500° C. where background oxygen acts as a deep donor compensating the shallow acceptor, such as carbon, having a higher concentration than that of a shallow donor, such as background silicon. By controlling the relationship of deep and shallow donors and acceptors, a SI-layer, for example, of InAlAs, can be achieved. In this case, a resistivity “exceeding” 5×10 4  Ωcm was achieved, which is significantly lower than the desirability for a resistivity range of about 10 6  to 10 8  Ωcm or higher. The dependence on background doping levels in a reactor or other growth apparatus to achieve a desired level of resistivity is a difficult approach to form current blocking layers having uniform characteristics on continuous and repeatable fabrication basis. Background doping levels are a function of many variables, e.g., hydride source oxygen purity, metalorganic source purity, carrier gas purity, integrity of the vacuum seals in the MOCVD reactor, previously deposited materials within the confines of the MOCVD reactor chamber as well as on the susceptor, injector(s), etc. As a result, background doping levels can substantially vary from reactor run to reactor run, resulting in significant variations in the current blocking properties of the compounds and materials formed when utilizing this technique and approach.  
           [0009]    U.S. Pat. No. 6,019,840 to Hartmann et al. does disclose SI-layers with resistances in the range of 10 9  Ωcm for SI-InGaP lattice-matched to GaAs. However, the greater need is for materials lattice-matched to InP for producing light emitting devices emitting and functioning at wavelengths (e.g., 1270 nm to 1650 nm) suitable for optical telecommunication applications, such as InAlAs latticed-matched to InP. As previously indicated relative to U.S. Pat. No. 5,804,840, SI-InAlAs, via low growth temperatures and background impurities, does not provide sufficiently high resistive values or well controlled active semiconductor devices employed particularly in optical telecommunication applications where the active semiconductor devices are integrated as a photonic integrated circuit (PIC) with close device spacing encountered so that the highest achievable levels of low current leakage in such devices are required, e.g., resistivities in a range of about 10 6  to 10 8  Ωcm or more.  
           [0010]    Studies of higher resistivity materials of InAlP lattice-matched to GaAs and InAlAs lattice matched to InP suggested the possibility of achieving high resistance or semi-insulating materials through intentional oxygen doping, such as indicated in the paper of J. C. Chen et al., “Effects of Trimethylindium on the Purity of In 0.5 Al 0.5 P and In 0.5 Al 0.5 As Epilayers Grown by Metalorganic Chemical Vapor Deposition”,  Journal of Electronic Materials,  Vol. 6(4), pp. 362-365, 1997, although this paper was not directed to such intentional oxygen doping. The paper only relates to the study of background doping and impurities of carbon, silicon and oxygen. There has been increasing interest in intentional oxygen doping in MOCVD processing, as illustrated in the patent of U.S. Pat. No. 5,909,051 to Stockman et al., which teaches oxygen doping of p-type confinement layers (e.g. AlGaInP) in LEDs which improves device stability and, therefore, long term device reliability. Also in the case of AlGaInP lattice matched to GaAs, oxygen doping has been studied as indicated the paper of J. S. McCalmont et al., “The Effect of Oxygen Incorporation in Semi-Insulating (Al x Ga 1-x ) y In 1-y P”,  Journal of Applied Physics,  Vol. 71(2), pp. 1046-1048, Jan. 15, 1992. In the case here, besides being lattice matched to GaAs, the source of oxygen was an O 2  flow into the reactor and not from an oxygen source, such as diethyl aluminum ethoxide (DEALO), which has been found to compensate silicon donors due to oxygen-induced multiple deep levels in InGaAs:Si:O. See the article of J. W. Huang et al., “Controlled Oxygen Incorporation in Indium Gallium Arsenide and Indium Phosphide Grown by Metalorganic Vapor Phase Epitaxy”,  Journal of Electronic Materials,  Vol. 24(11), (7 TH  Biennial Workshop on Organmetallic Vapor Phase Epitaxy, Fort Myers, Fla., Apr. 2-5, 1995), pp.1539-1546, November 1995. Also, previous mentioned U.S. Pat. No. 5,679,603 includes examples where the oxygen concentration in the crystal is controlled by the intentional doping of oxygen in AlInAs via an oxygen gas. However, in the embodiments reported, there is no indication of the resistivity levels except for the previously mentioned statement that high resistance semiconductor compounds fall in the range of 10 3  to 10 8  Ωcm. As indicated earlier, this large range is not acceptable for current blocking applications in demanding applications. Furthermore, using O 2  as an oxygen source has the disadvantage of pre-reacting with the Group III-V growth source materials in the MOCVD reactor chamber. These pre-reactions make the controlled incorporation of oxygen difficult and cause other detrimental problems such as undesired deposits in the reactor chamber and problems with composition or constituent control of the epitaxial deposition of Group III-V components comprising the compounds or layers that are being epitaxially grown in the reactor.  
           [0011]    Still another approach for forming semi-insulating blocking layers is to employ lateral oxidation techniques such as disclosed in U.S. Pat. Nos. 5,262,360 and 5,400,354 by exposing Al-containing layers to a wet oxidation process to form a native oxide in such layers or a diffusion process where oxide layer is formed on the surfaces to be oxidized and diffusion of water molecules or oxygen occurs from the oxide surface layer into the aluminum-containing layers to form its native oxide. A similar method may also be employed herein to produce the novel devices contemplated by this invention. In the utilization of this native oxide processing, the lateral oxidation to form the native oxide of the aluminum-containing layers can be controlled so as not enter the defined current flow region by utilizing Al-containing blocking layers containing a higher Al mole fraction than the Al mole fraction of any of the layers formed in the current flow region so that the lateral oxidation can be easily terminated at the lower mole fraction Al-containing layers in the current flow region as taught in U.S. Pat. No. 6,201,264, or by forming a mesa or groove current confinement region where the Al-containing layers are stepped so that the oxidation extends only to layer step region as taught in U.S. Pat. No. 6,287,884. Both of these patents are incorporated herein by their reference.  
         OBJECTS OF THE INVENTION  
         [0012]    It is an object of the present invention to provide a Al-III-V compound semi-insulating layer having high resistivity.  
           [0013]    It is another object of this invention to provide Al containing current blocking layers intentionally doped with oxygen providing resistivities, for example, in excess of about 10 6  to 10 8  Ωcm, on a reliably repeatable basis.  
           [0014]    It is another object of this invention to provide a Al-III-V compound semiconductor layer or region to InP that is employed as a current blocking layer or region in an active semiconductor device which has a higher and/or more controlled oxygen concentration in excess of that achieved by the flow of oxygen gas in a MOCVD or OMVPE reactor through the utilization of a low vapor pressure oxide source for the oxygen dopant.  
           [0015]    It is further object of this invention to provide a current blocking layer that has a high concentration oxygen permitting the additional deep level doping of other impurities (e.g., Fe) into the same layer or into adjacent layers which will block the diffusion of these impurities into adjacent layers or into an adjacent active region of an active semiconductor device as well as preventing the in-diffusion of other dopants into the current blocking layer.  
         SUMMARY OF THE INVENTION  
         [0016]    According to this invention, an Al containing group III-V compound semi-insulating layer is formed during MOCVD growth using an oxygen source to from a current blocking layer or region that defines a current channel or region in an active semiconductor device, such as a buried heterostructure semiconductor lasers, LEDs, modulators, photodiodes, heterojunction bipolar transistors, field effect transistors or other active devices and for preventing current flow through designated regions of the device.  
           [0017]    An important aspect of this invention is the provision of current blocking layers that are formed from intentional oxygen doping during their epitaxial growth. The deployment of intentional oxygen doping provides for better control and greater oxygen incorporation during layer growth over a wider range of growth parameters so that higher, repeatable resistivity values can be achieved under those conditions, such as 10 6-8  Ωcm or higher. These current blocking layers particularly contained Al and are lattice matched to the substrate, such as InAlGaP latticed matched to GaAs or InAlGaAs latticed matched to InP. The oxygen doping may be provided via an O 2  flow into the MOCVD reactor or provided via an oxide source where the oxide is cracked, i.e., the oxygen is dissociated from other gas constituents. However, an oxide source is preferred over an O 2  gas source because the latter provides a higher cracking temperature and reduced pre-reactions as described earlier. The preferred source for intentional oxygen doping is with a low vapor pressure oxide source such as, for example, a nitrogenous oxide (NO x ) or dialkylaluminum aloxides or diethyl aluminum alkoxide (DEALO). An ideal oxygen source is one that has a low cracking temperature without any tendency of pre-acting in the reactor with other source constituents prior to epitaxial wafer deposition. The material regime of particular interest is InAlAs/InP for achieving wavelengths of interest in optical telecommunication systems. Instead of InAlAs:O as a blocking layer material, InAlGaAs:O or AlGaAsSb:O or alternating layers of or alternating monolayers of AlAs:O/InAs or AlGaAs:O/InAs or InAlGaAs:O/InAs may be utilized or substitute InGaAs, InAlAs, InGaAsP for any of the InAs layers here. Also, combinations of the ternary layers and the quaternary layers may be employed, such as alternating layers of InAlAs:O and InAlGaAs:O. In the case of all the embodiments disclosed in this application, Fe can be co-doped with O since the oxygen at donor sites provides a strong holding bond for the out-diffusion of Fe from the material as well as prevention of the in-diffusion of other dopants, such as Zn, into the formed current blocking layer. Furthermore, O-doped layers can bond other layers with mobile elements (e.g., Fe) to prevent the indiffusion or out-diffusion of impurities into or out of these layers.  
           [0018]    It should be understood that with respect to the foregoing Al-containing Group III-V blocking layer materials, there is no Group V phosphor or P. However, it is within the scope of this invention that small amounts of P can be present in these Al-containing Group III-V blocking layer materials.  
           [0019]    To enhance the effect of oxygen doping of the Al-III-V current blocking layer or region and the resulting resistivity level, the Al content in the deposited layer is preferably 0.5 mole fraction or greater.  
           [0020]    In another embodiment of this invention, the current confining channel of the active semiconductor device may be a plurality of Al containing layers formed adjacent to the active region with a current channel formed through the Al containing layers by means of impurity induced disordering (IID) or vacancy induced disordering (VID). Regions of the deposited Al containing layers adjacent to the disordered current channel region are laterally oxidized from a water vapor source to form an Al-bearing native oxide defining current blocking regions on adjacent sides of the disordered current channel region. An example of such a device material regime is an InP substrate with Al containing layers comprising or InAlGaAs or alternating layers of InAlAs and InAlGaAs.  
           [0021]    Another feature of this invention is the inclusion of an active semiconductor device in a photonic integrated circuit (PIC) of the type disclosed in U.S. patent application, Ser. No. 10/267,331, filed Oct. 8, 2002, which provisional application is incorporated herein by its reference.  
           [0022]    Other objects and attainments together with a fuller understanding of the invention will become apparent and appreciated by referring to the following description and claims taken in conjunction with the accompanying drawings. 
       
    
    
     BRIEF DESCRIPTION OF THE DRAWINGS  
       [0023]    In the drawings wherein like reference symbols refer to like parts:  
         [0024]    [0024]FIG. 1 is schematic side view of a first embodiment of this invention.  
         [0025]    [0025]FIG. 2 is a schematic side view of a second embodiment of this invention.  
         [0026]    [0026]FIG. 3 is a schematic side view of a third embodiment of this invention.  
         [0027]    [0027]FIG. 4 is a schematic side view of a fourth embodiment of this invention.  
         [0028]    [0028]FIG. 5 is a schematic side view of a fifth embodiment of this invention.  
         [0029]    [0029]FIG. 6 is a schematic side view of a sixth embodiment of this invention.  
         [0030]    [0030]FIG. 7A is a schematic side view of a seventh embodiment of this invention.  
         [0031]    [0031]FIG. 7B is a schematic side view of a first modified version of the seventh embodiment of this invention.  
         [0032]    [0032]FIG. 7C is a schematic side view of a second modified version of the seventh embodiment of this invention.  
         [0033]    [0033]FIG. 8 is a schematic side view of a eighth embodiment of this invention.  
         [0034]    [0034]FIG. 9A is a schematic side view of a ninth embodiment of this invention.  
         [0035]    [0035]FIG. 9B is a schematic side view of a modified version of the ninth embodiment of this invention.  
         [0036]    [0036]FIG. 10 is a schematic side view of a tenth embodiment of this invention.  
         [0037]    [0037]FIG. 11 is a schematic side view of an eleventh embodiment of this invention.  
         [0038]    [0038]FIG. 12 is a schematic side view of a twelfth embodiment of this invention.  
         [0039]    [0039]FIG. 13 is a schematic side view of a thirteenth embodiment of this invention. 
     
    
     DETAILED DESCRIPTION OF THE INVENTION  
       [0040]    Reference is now made to FIG. 1 illustrating the first embodiment of this invention in a generally generic form. Active semiconductor device  10 A may be, for example, any such semiconductor device that is rendered operative through the establishment of a current channel through the device, such as, a semiconductor laser diode, semiconductor optical amplifier (SOA), LED or EA modulator, just to name a few such devices. Device  10 A comprises a substrate  12 , for example, n-InP, upon which is grown lattice-matched or pseudomorphic strained active layer or layers comprising active region  16 . To provide for carrier recombination under applied bias conditions, Group III-V epitaxially grown layers may be provided with an n-type dopant, such as Si or S, or with a p-type dopant such as Zn or Mg, as is well known in the art. Substrate  12  could also be GaAs but for wavelengths useful in present optical telecommunication systems, the preferable material system for these devices are InP material systems, such as, but not limited to, InGaAsP/InP.  
         [0041]    Device  10 A, as well as most other embodiments of this invention, involves a multi-step growth process employing metalorganic chemical vapor deposition (MOCVD), also known as or organometallic vapor-phase epitaxy (OMVPE) which is well known in the art as documented by Professor Stringfellow in his book entitled,  Orgaometallic Vapor - Phase. Theory and Practice,  1999, Academic Press. As a specific example, in the first growth process, a buffer layer (not shown) may be grown on substrate  12  followed by the growth of a confinement layer  14  of n-InP, such as doped with Si or S. Next, an active region  16  is grown. Active region may be a single layer or multiple layers or a plurality of quantum well (QW) layers. For example, active region  16  may be InGaAsP or a plurality of quantum wells and barriers of different mole fractions of InGaAsP lattice matched to substrate  12  or pseudomorphic strained as is known in the art. These layers include separate confinement layers with a bandgap lower than the adjacent confining region but higher than layers in the active region that are responsible for the emission or absorption of light. These layers or region provide carrier confinement and/or favorable waveguiding characteristics and are well known in the art. The growth of active region  16  is followed by the growth of confinement layer  18  of p-InP, such as with Zn or Mg as the p-type dopant. At this point in time in the MOCVD process, the first growth processing is completed and a selective etch is then performed on the InP wafer via an SiO 2  or SiN mask through the use of patterned photolithography. The etch is performed backed to the region of substrate  12  or n-InP containing layer  14  employing, for example, a dry etching process, reactive ion etching (IRE) or plasma enhance reactive ion etching (PE-IRE), forming a ridge or mesa structure  28  (comprising epitaxial layers  14 ,  16  and  18 ) in regions covered by the mask as illustrated in FIG. 1. The etch may alternatively comprise a wet chemical etch process. The mask can then be retained for the second growth process with MOCVD wherein a high resistance Al-containing Group III-V layer  30  (hereinafter referred to as Al-III-V) is epitaxially deposited. Layer  30  functions a current blocking layer to limit the primary flow of applied current through device  10 A through mesa  28  which defines a current confinement channel for device  10 A.  
         [0042]    As previously mentioned in the background, Al-III-V layer  30  may be grown as an in-situ, non-doped layer due to background doping, such as from background hydrogen, carbon and oxygen due to sources of contamination in the epitaxial process, such as from sources providing the growth material gases to the MOCVD process, or due to leaks or deposits in the reactor from past runs in the reactor itself. This type of background doping, therefore, is not controllable since the resulting resistance of the layer depends on the previous growth history, the particular background doping available from growth to growth in the reactor as well as particular growth conditions, particularly temperature, which is conducted at a low temperature compared to the higher growth temperatures in the epitaxial deposition of other semiconductor Group III-V layers of device  10 A. Moreover, consistently high resistance values to achieve the lowest values of current leakage are not obtainable by means of this approach. A better approach is to intentionally dope rather than depend upon unintentional doping via the MOCVD reactor, i.e., via background doping or related schemes in an attempt to achieve desired background doping levels which are not reliable or stable from growth to growth.  
         [0043]    As also mentioned in the background, others have employed Fe doped Al-III-V for SI, current blocking layer  30 . However, Fe has high mobility in the as-grown material and has a high tendency to migrate into other adjacent layers of the as-grown structure, such as the mesa structure  28 , thereby changing the layer conductivity property or quantum efficiency which is, of course, not desirable. In addition, dopants from the mesa structure  28  may also outdiffuse into the Al-III-V:Fe layers, which will degrade device performance. We intentionally dope layer  30  with oxygen to form the current blocking layer. Oxygen, in particular, provides a diffusion block against the diffusion of other dopants either into or through current blocking layer  30  and also render the material of layer  30  semi-insulating (Si) so that effectively no current flow will exist through this region. The oxygen dopant retards or restricts the diffusion of dopants and/or other crystal point defects which can result in deleterious effects on device performance. Thus, as will be seen in later embodiments, the codoping with Fe:O in Al-III-V compounds, such as InAlAs, provides for tying up Fe from diffusing out of current blocking layer  30  as well as preventing the in-diffusion of other dopants, such as Zn which has high volatility for diffusion, into blocking layer  30 . Thus, the use of oxygen as a dopant to form for a high resistivity layer  30  significantly retards the diffusion of impurities, such as Zn or Fe and/or other crystal point defects into or out of current blocking layers  30 . As a result, a spacer layer, as taught in the prior art previously mentioned in the background, is not required or necessary, i.e., the current blocking layer  30  may be in direct contact with mesa  28  as shown in FIG. 1. In other words, it is possible to eliminate the requirement for any separation or spacer layer between mesa  28  and current blocking layer  30 .  
         [0044]    While the prior art cited in the background discussed the use oxygen doping, the source generally employed is oxygen gas (O 2 ). This type of source does not provide good oxygen incorporation in a continuous and controlled manner. It is preferred that a low vapor pressure oxygen source, such as, nitrogenous oxide (NO x ) or diethyl aluminum ethoxide (DEALO) be employed for best controlled results to achieve the highest, consistent levels of oxygen incorporation at deep level donor sites in the bandgap of the blocking layer material.  
         [0045]    Referring now again to the description of FIG. 1 and the completion of device  10 A, after the growth of the current blocking layers  30  and removal of the SiO 2  or SiN etch mask, the active semiconductor device  10 A is completed by the growth of an additional cladding layer  32  of p-InP followed by a cap or contact layer  20 , such as p ++ -InGaAs. A metal contact  22  is formed in a SiO 2  passivation layer  24 , comprising, for example, AuZn under Au, which is aligned with mesa  28 , all of which is well known in the art. The device is completed with a bottom contact  26  comprising, for example, AuGe under Au as is known in the art.  
         [0046]    It should be noted that in the case of the embodiment of FIG. 1 as well as in all other embodiments, the oxygen doped current blocking layer or layers may include other conductivity type dopants, such as Zn or Mg in the case of p-type, or Si or S in the case of n-type, and/or other SI-dopants such as Fe, Co, Ni or Ti. A principal feature of this invention is the deployment of oxygen for high resistivity, insulating current blocking layer(s), taking advantage of the strong bonding properties of oxygen to hold these other dopants and/or crystal point defects, whether of the insulating type or of the conductivity type, from out-diffusing from the oxygen doped layer(s) or in-diffusing into the oxygen doped layers.  
         [0047]    Reference is now made to FIG. 2 which discloses a second embodiment of this invention. In this embodiment as well as in all subsequent embodiments, the previous description relative to elements and components in FIG. 1 equally apply to all of the same elements and components having the same numerical identification in figures of the subsequent embodiments. FIG. 2 is the same as FIG. 1 except there is, in addition, the deposited layers  34  and  36  between which is formed current blocking Al-III-V layer  30 . These layers  34  and  46  are optionally added in the case where, for example, the close proximity of the Al-III-V:O layer to the mesa  28  or active region  16  ,ay induce deleterious device effects (e.g., high interface recombination). In these cases, it may be desirable to set-back the Al-III-V:O layer with a layer of InP or InP:O. This layer should be in the range of about 100 Å to 2 μm thick, preferably about 500 Å to 5,000 Å thick. In the case of layer  34 , this lower set-back layer may comprise InP, InGaAs or InGaAsP that is doped n-type, unintentionally doped, oxygen doped, or any combinations thereof. Likewise, for layer  36 , this upper set-back layer may comprise InP, InGaAs or InGaAsP that is doped n-type, p-type, unintentionally doped, or oxygen doped. Upper set-back layer  36  provides the utility of an Al-free cap layer after the growth of the current blocking layer. Without this Al cap layer  36 , the underlying, exposed Al-III-V layer would form a “hard” oxide at its surface making it extremely difficult to grow high-quality single crystal material on this layer. Thus, cap layer  36  prevents the formation of such a “hard” oxide since all of the Al containing layers are buried and facilitates subsequent processing and regrowth of layers  32  and  20 . It is essential that cap layer  36  bury or cover all Al-III-V material originally existing at the growth surface. This is true relative to subsequent embodiments herein as shown in FIGS.  3 - 9 . The sandwiching layers  34  and  36  may be respectively doped to form added current blocking properties, such as a reverse biased junction as is known in the art.  
         [0048]    Reference is made to FIG. 3 illustrating a third embodiment of this invention comprising the same layers as shown in FIG. 2 except that here, the material of choice for current blocking layer  30  is InAlAs:O sandwiched between layers  34 A and  36 A of n-InP and p- or n-InP, respectively. Alternatively, layer  36 A can be doped as InP:O. While InAlAs:O is illustrated in this embodiment for blocking layer  30 , it should be understood that blocking layer  30  may also be InAlGaAs:O or alternating layers or monolayers of AlAs:O/InAs, the latter of which will be described in more detail later, such as relative to the embodiment shown in FIG. 6.  
         [0049]    Reference is now made to the fourth embodiment comprising this invention shown in FIG. 4. Active semiconductor device  10 D is the same as that in the embodiment of FIG. 3 except that current blocking layer  38  is co-doped with oxygen (O) and iron (Fe) to provide enhanced current-blocking characteristics. Both of these dopants are deep level impurities and, in combination, the O donors do not allow any Fe mobility as well as any mobility for impurity in-diffusion by other dopants such as Zn. While InAlAs:O:Fe is shown in this embodiment, it should be understood that layer  38  may also be InAlGaAs:O:Fe or alternating layers or alternating monolayers of AlAs:O:Fe/InAs. It should be noted that the presence of Fe as an additional deep level impurity can be provided relative to any of the embodiments of this invention. Note that the controlled introduction of oxygen from an oxide source is suitable for this embodiment. In order to incorporate high levels of active Fe, specific growth conditions are required such as, for example, higher growth temperatures. These conditions are not necessarily consistent with the incorporation of high levels of oxygen from the background. Thus, intentional oxygen doping can enable simultaneously high levels of both active Fe and O in the current blocking layers. Boundary layer  34 B may be comprised of InP, InGaAs or InGaAsP and O-doped and undoped (unintentionally doped) or n-doped or combinations thereof, and boundary layer  36 B may be comprised of InP, InGaAs or InGaAsP and O-doped and undoped (unintentionally doped) or n-doped or p-doped or combinations thereof.  
         [0050]    Reference is now made to the fifth embodiment shown in FIG. 5 illustrating active semiconductor device  10 E. This embodiment is the same as the previous embodiment of FIG. 4 except that a pair of current blocking layers  40  and  42  is employed and upper boundary layer  36 A may be n-InP or n-InP:O where the latter prevents indiffusion or out-diffusion of impurities or crystal point defects. In the case here, one of the two layers  40  and  42  carries more Al content than the other layer in a set of layers  40 ,  42 . For example, layer  40  may be comprised of In x Al 1-x As:O and layer  42  comprises In y Al 1-y As:O where x&gt;y and preferably x may be greater than about 0.5 (Al-rich). The Al-rich alloy layer  40  provides for heightened concentration of oxygen in the grown crystal while the In y Al 1-y As layer  42  provides strain balance or lattice matching to InP substrate  12 . Note that either layer  40  or  42  may be Al-rich. Furthermore, it is only critical that the Al-rich layer be oxygen doped. Thus, in the case here, layer  42  need not be doped.  
         [0051]    In the sixth embodiment shown in FIG. 6, device  10 F is the same as that device shown in FIG. 5 except that there are multiple Al-rich alloy layers  40  interposed with other Al containing layers  42 . For example, alternate layers  40  may be comprised of In x Al 1-x As:O and alternate layers  42  are In y Al 1-y As:O where x&gt;y and preferably x may be greater than about 0.5. These layers are preferably pseudomorphic or strain compensated. Such a current blocking layer combination provides a high resistance, SI-region with very little current leakage.  
         [0052]    In both embodiments of FIGS. 5 and 6, layers  40  and  42  are very thin layers. The InAlAs layers  42  provide for strain balance or compensation relative to the Al-rich layers  40  that will not be lattice matched to InP. Thus, layers  40  and  42  are only grown to a thickness not to exceed the critical thickness, i.e., the thickness does not exceed the point where threading dislocations appear in the material. The strain compensating layers  42  relax the lattice strain brought about by the lattice mismatched, Al-rich layers  40 . As an example, the strain compensating layers  42  may be In 0.7 Al 0.3 As: and the Al-rich layers  40  may be In 0.3 Al 0.7 As:O. The thickness of layers  40 ,  42  may roughly be in the range about 30 Å to about 1,000 Å, depending upon their compositional mole fractions of the layer constituents.  
         [0053]    As stated previously, only the Al-rich layer or layers  40  are required to be O-doped. Furthermore, the position of layers  40  and  42  may be interchanged. Also, in the embodiment of FIG. 6, spacer layers are arbitrary lattice matched or pseudomorphic material may be placed between each pair of layers. Note that in the employment of FIG. 6, Fe-doping may be utilized in the Al-rich or Al-poor layers  40  and  42 , respectively, for enhanced current blocking characteristics, i.e., In x Al 1-x As:O:Fe and/or In y Al 1-y As:O:Fe. In this connection, it should be further noted that not all of the layers need to have the same Fe-doping level. For example, it may be desirable to have the outmost layers free of Fe. A further extension of the embodiments of FIGS. 5 and 6 is to utilize InAlGaAs layers for InAlAs layers  40  and  42 . Note that the lower Al-content layers, such as layers  42 , may contain no aluminum all; for example, they may be InGaAs.  
         [0054]    [0054]FIG. 7A illustrates a further embodiment of the structure shown in FIG. 3 except in active semiconductor device  10 G of FIG. 7A, multiple alternate layers are employed where layers  44  may be InAlAs:O or InAlAs:O:Fe and layers  46  may be InAlAs:O or InAlAs:O:Fe. In this example, the Fe-doped layers may or may not be co-doped with oxygen. Also, Fe may be placed with any deep-level mobile impurity. Furthermore, the Group III-V alloy that is Fe-doped may be InP, InGaAs, InGaAsP or InAlGaAs beside InAlAs. The purpose of the oxygen co-doping is to retard the movement of deep-level impurities and/or enhance the current blocking capabilities of the layers. The adjacent O-doped layers serve to further impede any out-diffusion or in-diffusion of impurities into the Fe or other deep-level impurity doped blocking layer. In this respect, a preferred embodiment would be to utilize InAlAs:O boundary layers that bound a core comprising an InAlAs (or InP):Fe layer or an InAlAs (or InP):Fe:O layer. This device  10 H is shown in the modified embodiment of FIG. 7B relative to core layer  44 . Note that it may be possible to omit the upper layer  46  above layer  44  or, alternatively, layer  36 A or both layers  44  and  36 A. One could omit one or both of these layers provided that out-diffusion or in-diffusion to or from p-InP layers  32  or  18  is not problematic.  
         [0055]    Also, in order to eliminate upper boundary layer  36 A, layer  44  (or layer  46 , if present) should not contain sufficiently high Al content to form a “hard” oxide upon exposure to O-doping, as previously described. An example of this embodiment is device  10 I shown in FIG. 7C where layer  44  is InP:Fe or InP:Fe:O.  
         [0056]    In any of these embodiments shown in FIGS. 7, 7B or  7 C, InAlGaAs may be substituted where InAlAs is utilized in layers  44  or  46 . Also, in connection with these layers  44  or  46 , there may be ten or more alternating layers of InAlAs: Fe[O] and InAlAs:O. Furthermore, layers  44  may be Al-rich layers such as (Al x Ga 1-x ) y In z As:Fe[O] and layers  46  are Al x′ Ga y′ In z′ As:O where x&gt;x′. Optionally, layers  44  may also be co-doped with an n- or p-type impurity or impurities.  
         [0057]    [0057]FIG. 8 illustrates a further embodiment comprising active semiconductor device  10 J where the current blocking layers in device  10 J are modulated alloy layers  48  which may be alternating layers or alternating monolayers of AlAs:O/InAs or AlGaAs:O/InAs or InAlGaAs:O/InAs. It is desirable to utilize these layers where high oxygen content is required. Thus, not all O-doped layers in device  10 J need to contain these alternating layers. Also, any of these layers may also be doped or co-doped with Fe.  
         [0058]    [0058]FIG. 9A illustrates a further embodiment comprising active semiconductor device  10 K where the current blocking layers do not contain an Al-content layer as is the case of all of the previous embodiments. In the case here, the non-Al containing material comprises InP doped with oxygen, The bond of oxygen atoms to InP, however, is not as strong as the bond of oxygen atoms with aluminum atoms in Al-III-V compounds. As a result, the insulating properties are not as good either, i.e., the achievable resistivity will not be as high. However, these O-doped layers may still provide reasonable ability for impeding the out-diffusion or in-diffusion of impurities or crystal point defects. Such a device  10 K has utility where Al-III-V compounds are not desired in the fabrication of the active semiconductor device.  
         [0059]    Active semiconductor device  10 K comprises a current blocking region  50  of oxygen doped InP:O or InP:O:Fe sandwiched between blocking current confinement layers  34 A and  52  respectively comprising n-InP and n-InP or n-InP:Fe. It should be noted that bottom boundary layer  34 A is optional. Moreover, upper boundary layer  52  can also be doped with Fe to provide additional resistance to current flow in combination with current blocking layer  50 . Also, since layer  50  is doped with O, the out-diffusion of Fe into the layers in mesa  28  will be minimized. Alternatively, one can utilize InP:O boundary layers to impede the out-diffusion of sandwiched Fe-doped layers. Such a modified structure is shown in FIG. 9B comprising active semiconductor device  10 L. In the structure here, layers  50  are InP:Fe or InP:Fe:O and outer layers  49  and  53  of the blocking region are InP undoped or n-doped. These outer layers  49  and  53  are optional. Layers  51  of InP:O are also optional in the case where layer  50  is co-doped Fe:O. In any case, the boundary layers  51  of doped O-InP help prevent the out-diffusion of Fe from layer  50 .  
         [0060]    The foregoing embodiments are oxygen doped preferably with a low vapor pressure oxide source, such as DEALO. It is also possible to prepare the oxygen-diffuse current blocking layers by means of the wet oxide approach as mentioned in the background section or from a deposited layer comprising an oxide layer as a diffusion source for oxygen to form a native oxide. Embodiments employing these types of sources for semiconductor active devices are illustrated in FIGS.  10 - 12 .  
         [0061]    In FIG. 10, active semiconductor device  10 M is similar to the structure shown in FIG. 3 except that the oxygen doping of Al-containing, current blocking layer  30  is brought about by native oxide diffusion. In the case here, at least after the deposition of cladding layer  32  of p-InP in the second epitaxial growth process, trenches  60  are formed by selective etching after which a wet-oxidation process is applied, as is known in the art. Then, as taught in U.S. Pat. No. 5,262,360 to Professor Holonyak and associates and other later patents dealing with this process, which patent is incorporated herein by their reference, a wet oxide process is conducted, such as by bubbling nitrogen through H 2 O. As a result, layer  30  is transformed into its native oxide by lateral diffusion via trenches  60 . Core layer  30  may, for example, be InAlAs, AlGaAs or AlAs.  
         [0062]    Reference is now made to the embodiment shown in FIG. 11 comprising active semiconductor device  10 N which comprises a substrate  12  of n-InP upon which is deposited in a first growth process the following layers: n-InP buffer layer  13 ; confining layer  14 A of n-InAlAs or n-InAlGaAs; active region  16 , such as InGaAsP or multiple quantum wells and barriers of InGaAsP; confining layer  18 A of p-InAlAs or p-InAlGaAs; and InP layer  70  to protect the underlying Al containing layer  18 A from oxidation when the device is removed or otherwise exposed to the ambient prior a second growth process. The surface of the wafer containing device  10 N is then covered with a SiO 2  or SiN, mask layer, which is patterned via photolithography as is known in the art. The exposed portions of the photolithographic pattern are removed and an etching process is performed in the exposed regions to produce troughs  60 , as in the case illustrated in FIG. 10, employing an anisotropic dry etching process such as reactive ion etching (IRE) or plasma enhance reactive ion etching (PE-IRE), forming a ridge or mesa structure  28 A (comprising epitaxial layers  14 A,  16  and  18 A), as shown in FIG. 11. This is followed with the performance of the second epitaxial growth process and the deposition of current blocking layer  77  comprising a Al-containing layer, such as, for example, InAlAs, followed by the epitaxial growth of protection layer  72  of InP, cladding layer  74  of p-InP and cap or contact layer  76  of p ++ -InGaAs. Layer  77  can be a Al-rich InAlAs layer where the Al content in the layer is greater than  0 . 5  mole fraction. Next, trenches  71  are formed in the regions of the second growth between mesas  28 A of adjacent devices  10 N in the wafer employing a mask and selective etching process as known in the art. This is followed by the formation of an oxide source layer  78  on InAlAs layer  77 , such as SiO 2  or spin-on-glass (SOG) which is deposited in troughs  71  employing sputter or other such process to form this layer on the side surfaces of troughs  71 . This is followed further by a heat treatment process where an oxide diffusion is generated from layer  78  forming an oxide of InAlAs in layer  77 . The temperature of such a process may be, for example, around 750° C. This oxide process may proceed through layer  77  to mesa  28 A. On the other hand, additional control can be achieved by forming Al-rich layer  77 , i.e., more than 0.5 mole fraction of Al, so that the native oxide of layer  77  is readily formed without oxidizing the Al containing layers within mesa  28 A.  
         [0063]    [0063]FIG. 12 shows the twelfth embodiment of this invention where active semiconductor device  10 P comprises a fabricated planer structure rather than a ridge or mesa structure. In the case here, a n-InP wafer is provided upon which is epitaxially grown the following exemplifying layers: n-InP confining layer  14 , active region  16  such as InGaAsP, a confining layer  18  of InP or InAlGaAs, a group  80  of layers  82 ,  84 ,  86  respective, for example, of InAlGaAs, InAlAs and InAlGaAs where at least one of these layers is Al-rich for purposes of conversion to a high native oxide content , a p-InP layer  32  and cap layer  22  of p ++ -InGaAs. SiO 2  SiN x  layer  24  provides a mask for performing impurity induced disordering (IID) via opening  82  formed in mask  24 A, which opening later receives a metal contact. IID is taught in U.S. Pat. Nos. 4,378,255; 4,594,603; 4,511,408 and 4,639,275, all of which are incorporated herein by their reference. Next, either by trenching or by dicing into chips, the lateral side surfaces of layer group  80  are exposed to an oxide source treatment, as discussed in the preceding embodiments of FIGS.  10  or  11 , to form Si-layers through native oxide formation in regions  88  of the group  80  of layers  82 ,  84 ,  86  via the oxide diffusion  91 . The advantage of the pre-formed IID region  90  is that the diffusion of Zn in this region interdiffuses the Al containing layer constituents, as is known in the art, and functions, in part, as a barrier to oxygen diffusion extending from regions  88  into region  90 , i.e., the oxidation proceeds through regions  88  but not significantly into the interdiffused region  90  because the Al-containing layers  82 ,  84 ,  86  have been disordered via IID to render region  90 , as disordered, generally more Al-poor compared to non-disordered regions  88 . Thus, region  90  is substantially resistant to oxidation compared to oxidized regions  88  so that region  90  functions as a current channel to active region  16  of device  10 P.  
         [0064]    An alternative approach to the IID Zn diffusion region  90  in FIG. 12 is shown in FIG. 13, where the active semiconductor device  10 Q is the same as device  10 P in FIG. 12 except that selective delta doped regions  90 , such as with zinc delta-doping, are formed relative to each of the layers  82 ,  84 ,  86 , via masking during epitaxial growth to form a interdiffused region  92  upon subsequent annealing after completion of device growth. Region  92  is substantially resistant to oxidation compared to subsequently oxidized regions  88  because, in region  92 , layers  82 ,  84 ,  86  have been disordered so that the overall Al content of the disordered layers in this region have low Al content compared to at least one of the same layers in regions  88 . The annealing temperature to form this diffusion may be, for example, around 850° C. This is followed by the oxide diffusion employing, for example, a wet oxide treatment, illustrated at  91 . The conversion to native oxide of layers  82 ,  84 ,  86 , via the oxide diffusion  91 , will significantly terminate at the interface  94  of these layers formed between regions  88  and region  92  due to the previously preformed IID treatment in region  92 .  
         [0065]    While the invention has been described in conjunction with several specific embodiments, it will be evident to those skilled in the art that many further alternatives, modifications and variations will be apparent in light of the foregoing description. For example, instead of InAlAs:O current blocking layers, they can also be comprised of AlGaAsSb or (AlGaIn)AsSb. Thus, the invention described herein is intended to embrace all such alternatives, modifications, applications and variations as may fall within the spirit and scope of the appended claims.