Abstract:
A fibre-based surgical implant stabilized against fraying, includes a thermally crimped flat-knitted fabric of a biocompatible, optionally biodegradable, polymer material having a glass transition temperature or other thermally induced secondary conformational mobility threshold in the temperature range of from 20° C. to +170° C. Also disclosed is a corresponding fabric and methods of producing the implant and the fabric.

Description:
FIELD OF THE INVENTION 
       [0001]    The present invention relates to a fibre-based surgical implant, a fabric for use in the manufacture of the implant, and methods for producing the fabric and the implant. 
       BACKGROUND OF THE INVENTION 
       [0002]    A wide range of fibre-based surgical implants are known in the art. To be tolerated by the organism an implant has to be biocompatible. Certain uses additionally benefit from the implant being made of or comprising biodegradable material. Fibres for use in biocompatible implants are, in particular, made from suitable synthetic polymers. The fibres of an implant can be disposed in form of an ordered pattern, such as in a woven or knitted textile material, or in a non-ordered pattern, such as in a non-woven textile material. Surgical implants comprising knitted materials are disclosed, for instance, in U.S. Pat. No. 6,093,205 A, EP 505 634 B1, and EP 1 351 630 B1. 
         [0003]    For economic reasons a textile fabric for use in implants would benefit from being manufactured in a size allowing the production of multiple implants or implant elements from it. The implants or elements for use in implants would have to be cut out from the fabric. Depending on the production method and textile pattern of the fabric, the degrees of cutting freedom may be restricted by the risk of compromising the integrity of the products by the textile material unraveling or fraying at cut edges. The problem may be aggravated by movements of tissue disposed adjacent to an implant in situ. A common fixation mode for textile implants is by suture(s) penetrating the implant near its fringe(s). Tearing by the suture(s) on implant is an important cause of fraying and of such implants losing their attachment to the respective bone or soft tissue. Fraying of an implanted textile material may cause a malign biological response of host tissue by mechanically induced inflammation and/or particle synovitis. In consequence the implant might require explantation. To avoid the risk of fraying woven fabrics for implant applications should not be cut along the warp. One commercially available woven fabric implant comprised by this restriction is the Artelon® TMC Spacer (Nilsson et al., J Hand Surg, 2005; 30A(2)380-9). Hence, the dimensions of a manufactured implant of this kind will have to be a compromise in view of the need to make an implant of given form and size fit as many patients as possible. Although a woven implant may be available in different sizes its case-by-case refined biometric and anatomic adaptation would be desirable. With a textile design that permits unrestricted cutting in the plane of the fabric a ready-made implant could be supplied with a shape better adapted to anatomical and biometric requirements. Even a final tailoring by the surgeon can be enabled during surgery. The need of adapting a ready-made implant to a patient is particularly pronounced if it is a part of an articular joint surface that needs treatment. In that case it is a definite benefit if the implant can be trimmed by the surgeon or assisting medical personnel. Fraying of a textile implant thus should be avoided by all means. 
       OBJECTS OF THE INVENTION 
       [0004]    An object of the invention is to provide a textile material of the aforementioned kind having little or no tendency to fray at cut edges thereof. 
         [0005]    Another object of the invention is to provide a surgical implant comprising or consisting of such non-fraying textile material. 
         [0006]    A further object of the invention is to provide methods of producing a non-fraying textile material and a corresponding implant. 
         [0007]    Additional objects of the invention will become evident from the following summary of the invention, preferred embodiments thereof illustrated in a drawing, and the appended claims. 
       SUMMARY OF THE INVENTION 
       [0008]    According to a first aspect of the present invention is disclosed fibre-based surgical implant of the aforementioned kind stabilized against fraying at a cut edge. The fibres of the implant are comprised by a flat-knitted fabric of a biocompatible, optionally biodegradable, polymer material. The polymer material is one capable of being thermally crimped. A measure of this capacity is that the polymer has a glass transition temperature, in particular one of from 20° C. to 170° C. However, there are also polymer materials that can be thermally crimped but do not exhibit a distinct glass transition temperature; within the same temperature range these materials do however exhibit at least one thermally induced conformational mobility threshold that is not a melting threshold, i.e. is a threshold of a secondary not a primary transition. One important polymer material of this kind is poly(urethane urea). 
         [0009]    The implant of the invention may comprise fibres of more than one thermally shrinkable polymer material. The implant of the invention may also comprise fibres of varying thickness and/or fibre threads. 
         [0010]    An optimal stabilizing effect is achieved by selecting polymer fibres that can be thermally crimped and a knitting pattern that makes the fibres interlock by their crimping action. The fabric may be crimped by, for instance, running it over heated roller(s). Crimping by means of heated cylindrical rollers will preserve the flatness of the fabric. Alternatively the fabric may be thermally crimped to give a non-flat form. This can be accomplished by, for instance, making the fabric abut a heated surface that is not flat, such as a heated concave metal surface. A fabric holder that negatively mirrors the geometry of the heated non-flat surface may be used to press the tissue gently against the heated surface to make the fabric adopt the form of the non-flat surface during the crimping process. 
         [0011]    “Cut edge” is an edge formed by a cutting operation, such as by excision or punching. The cutting operation may be carried out in an automated fashion in the course of industrial production or manually at bedside by the use of a pair of scissors or a scalpel. The use of laser and particle beam cutting techniques is within the ambit of the invention. 
         [0012]    “Knitted fabric” comprises any fabric manufactured by a knitting method, in particular by warp knitting, but does not comprise woven fabrics. Knitting methods useful in the invention are described, i.a., in: D J Spencer.  Knitting technology, a comprehensive handbook and practical guide . Third edition, Woodhead Publishing Ltd., Cambridge 2001. 
         [0013]    “Crimped knitted fabric” is a thermally crimped fabric. Useful crimping ranges according to the invention in a direction along the weft or perpendicular to the weft are from 10% to 70%, in particular from 25% to 60%, more particularly from 35% to 55%, most preferred about 45%. The thickness of the fabric of the invention is less effected by crimping than the width or length of the fabric, and may even increase as a result of crimping. 
         [0014]    Useful polymer materials include poly(ortho ester), poly(glycolic acid), poly(lactic acid), poly(glycolic, lactic acid), poly(β-hydroxybutyric acid), poly(imino carbonate), poly(ε-caprolactone), poly(glycolic/lactic acid, ε-caprolactone), poly(ethyleneterephthalate), poly(etheretherketone), poly(urethane urea), polyurethane, polyamide. These useful materials are only given for exemplification. Thus any other biocompatible polymer having a glass transition temperature within the range given above may also be used. 
         [0015]    According to a second aspect of the present invention is disclosed a thermally crimped flat knitted fabric of a biocompatible, optionally biodegradable, material. The material is suitable in the manufacture of non-fraying surgical implants by cutting techniques such as excision or punching. The fabric comprises or consists of a polymer material having an ordered domain, in particular a material having a glass transition temperature, in particular one of from 20° C. to 170° C. or a secondary thermally induced conformational mobility threshold within that temperature range. 
         [0016]    According to a third aspect of the present invention is disclosed a method of producing a flat knitted fabric for use in the manufacture of a surgical implant stabilized against fraying, comprising: providing one or more fibres of a biocompatible, optionally biodegradable, polymer material having a glass transition temperature, in particular one of from 20° C. to 170° C., or a secondary thermally induced conformational mobility threshold within that range; knitting a flat fabric from the one or more fibres; crimping the fabric thermally. In particular, the method comprises: (a) knitting in parallel superimposed planes a first fabric ribbon and a second fabric ribbon to form a first fabric ribbon section and second fabric ribbon section; (b) interlacing the fibres used in forming said first and second ribbon sections over a selected ribbon length to knit an interlaced ribbon section; repeating steps (a) and (b) for a selected number of times so as to provide an interlaced fabric ribbon comprising a multitude of alternating double ribbon and interlacing ribbon sections. 
         [0017]    According to a fourth aspect of the present invention is disclosed a method of producing a surgical implant stabilized against fraying comprising: providing the product of the method of producing a flat-knitted fabric for use in the manufacture of a surgical implant stabilized against fraying; forming the implant from the fabric, in particular by cutting. 
         [0018]    According to a fifth aspect of the present invention is disclosed an intraarticular spacer substantially consisting of a crimped flat-knitted fabric of polymer material. 
         [0019]    According to a sixth aspect of the present invention is disclosed an intraarticular spacer excised from a crimped flat-knitted fabric of polymer material. 
         [0020]    According to a seventh aspect of the present invention is disclosed a flat-knitted fabric obtained or obtainable by the method of the invention. 
         [0021]    According to an eight aspect of the present invention is disclosed a surgical implant obtained or obtainable by the method of the invention. 
         [0022]    It is within the ambit of the present invention to provide the fabric of the invention or an implant manufactured from the fabric with agents that improve or safeguard its incorporation into living tissue, such as with hormones, in particular growth hormones, antibiotics, cartilage constituents, including cultured cartilage cells, etc. Such agents are well known to the person skilled in the art and need not to be detailed here. 
         [0023]    The invention will now be explained in more detail by reference to a number of preferred embodiments illustrated in a drawing.  FIGS. 1-1   e  are photographic views. The other figures are roughly drawn sketches; in the sectional views the thickness of knitted fabric and of implants produced from knitted shrunk fabric is grossly exaggerated for reasons of clarity. 
     
    
     
       SHORT DESCRIPTION OF THE FIGURES 
         [0024]      FIG. 1  is a top view of a first embodiment of the implant of the invention, excised from the shrunk flat-knitted ribbon of  FIG. 1   b  or cut to size at bedside from the standardized implant patch of  FIG. 1   d , enlarged; 
           [0025]      FIG. 1   a  is top view of a transverse section a first embodiment of a flat-knitted poly(urethane urea) ribbon, enlarged; 
           [0026]      FIG. 1   b  is a top view of a transverse section of the flat-knitted ribbon of  FIG. 1   a , after shrinking, enlarged; 
           [0027]      FIGS. 1   c - 1   e  are top views of standardised implant patches of comprised by a set of patches punched out from the flat-knitted ribbon of  FIG. 1   b , enlarged; 
           [0028]      FIG. 2  is a partial view of the flat-knitted ribbon of  FIG. 1   a , in a longitudinal section and enlarged; 
           [0029]      FIG. 2   a  is a partial view of the flat-knitted ribbon of  FIG. 1   b , after shrinking; in the same view as that of  FIG. 2 , enlarged; 
           [0030]      FIG. 3   a  is a partial view of a first embodiment of an interlaced double poly(urethane urea) flat-knitted ribbon of the invention comprising interlaced sections separated by non-interlaced sections, in a longitudinal section and enlarged; 
           [0031]      FIG. 3   b  is the interlaced double flat-knitted ribbon of  FIG. 3   a , after shrinking and in the same enlarged view; 
           [0032]      FIG. 4  is a sectional view of an intraarticular spacer implant body of the invention cut out from the flat-knitted ribbon of  FIG. 3   b , enlarged; 
           [0033]      FIG. 4   a  is the double interlaced flat-knitted ribbon of  FIG. 3   b , in the same enlarged view, with cutting planes for the excision of the implant of  FIG. 4  indicated; 
           [0034]      FIG. 4   b  is an intraarticular spacer implant of the invention formed for implantation from the implant body of  FIG. 4 , in the same view; 
           [0035]      FIG. 4   c  is a representation of the implant of  FIG. 4  in a perspective view; 
           [0036]      FIG. 5  is a sectional view of another intraarticular spacer implant body of the invention excised from the flat-knitted ribbon of  FIG. 3   b , enlarged; 
           [0037]      FIG. 5   a  is the double interlaced flat-knitted ribbon of  FIG. 3   b , in the same enlarged view, with cutting planes for excision of the implant of  FIG. 5  indicated; 
           [0038]      FIG. 5   b  is an intraarticular spacer implant of the invention formed for implantation from the implant body of  FIG. 5 , in the same view; 
           [0039]      FIG. 6  is still another intraarticular implant of the invention excised from the flat-knitted ribbon of  FIG. 3   b , in a sectional view (A-A,  FIG. 6   b ), enlarged; 
           [0040]      FIG. 6   a  is the double flat-knitted ribbon of  FIG. 3   b , in the same enlarged view, with cutting planes for the excision of the implant of  FIG. 6  indicated; 
           [0041]      FIG. 6   b  is a top view of the implant of  FIG. 6 , enlarged; 
           [0042]      FIG. 7   a  is the diseased head of a joint, in a sectional view, enlarged; 
           [0043]      FIG. 7   b  is the joint head of  FIG. 7   a  prepared for implantation, in the view of  FIG. 7   a , enlarged; 
           [0044]      FIG. 7   c  is the joint head of  FIG. 7   b , provided with the implant of  FIG. 6 , in the view of  FIGS. 7   a  and  7   b;    
           [0045]      FIG. 8   a  is a partial view of a second embodiment of an interlaced double poly(urethane urea) flat-knitted ribbon of the invention, in a longitudinal section (B-B,  FIG. 8   d ) and enlarged; 
           [0046]      FIG. 8   b  is the interlaced double flat-knitted ribbon of  FIG. 8   a , after shrinking and in the same enlarged view, with cutting planes indicated; 
           [0047]      FIG. 8   c  is an intraarticular spacer implant of the invention excised from the flat-knitted ribbon of  FIG. 8   b , in the same view and enlarged; 
           [0048]      FIG. 8   d  is a top view of the spacer implant of  FIG. 8   c , enlarged. 
       
    
    
     DESCRIPTION OF PREFERRED EMBODIMENTS 
     Example 1 
       [0049]    Shrunk flat-knitted poly(urethane urea) ribbon. Yarn: 13 Tex poly(urethane urea) (Artelon®, Artimplant AB, Göteborg, Sweden). Equipment: Comez DNB/EL-800 (Comez s.p.A., Cilavegna, Italy) double needle bed crochet machine, for the production of technical and medical articles. Machine specifications: 15 gauge, 6 weft bars, double needle bed, latch needles. Heat set unit: Comez HSD/800 comprising 2 heat-set cylinders. 
         [0050]    A plain ribbon  1  of 14 cm width was knit in the machine ( FIGS. 1   a ,  2 ). The ribbon  1  was shrunk in the heat set unit at 130° C. to produce a shrunk ribbon  1   b  a thickness of 0.8 mm ( FIGS. 1   b ,  2   a ). Process parameters: Knitting speed: 26 cm/min; heat set unit speed: 14 cm/min; shrinkage along warp: about 45% (cf D I , width of ribbon  1  and d I , width of ribbon  1   s ); shrinkage across warp: about 45% (cf D t , 20 loops, and d t , 20 loops). Warp thickness is slightly increased by shrinking. The warp knitting pattern is shown in Table 1. It is a sequence of four steps with 12 loops/cm. 
         [0051]    By using the same parameters and knitting pattern a quadrupled thread gives a shrunk fabric of about 2.0 mm thickness. 
         [0000]    
       
         
               
             
               
               
               
               
             
               
               
               
               
               
               
             
               
               
               
               
               
               
               
               
               
               
               
               
             
           
               
                 TABLE 1 
               
             
             
               
                   
               
               
                 Warp knitting pattern of tricot ribbon 
               
             
          
           
               
                 Loop 
                 Binding device movement 
                 Loops/ 
                 Alimentation device setting 
               
             
          
           
               
                 row 
                 2 
                 4 
                 5 
                 cm 
                 (warp feed) 
               
               
                   
               
             
          
           
               
                 1 
                 2 
                 2 
                 3 
                 3 
                 2 
                 2 
                 12.00 
                 1490 
                 2610 
                 1790 
                 1450 
               
               
                 2 
                 2 
                 1 
                 2 
                 1 
                 2 
                 3 
                 12.00 
                 1490 
                 2610 
                 1790 
                 1450 
               
               
                 3 
                 1 
                 1 
                 3 
                 3 
                 2 
                 2 
                 12.00 
                 1490 
                 2610 
                 1790 
                 1450 
               
               
                 4 
                 1 
                 2 
                 4 
                 5 
                 2 
                 1 
                 12.00 
                 1490 
                 2610 
                 1790 
                 1450 
               
               
                 5 
                 2 
                 2 
                 3 
                 3 
                 2 
                 2 
                 12.00 
                 1490 
                 2610 
                 1790 
                 1450 
               
               
                 6 
                 2 
                 1 
                 2 
                 1 
                 2 
                 3 
                 12.00 
                 1490 
                 2610 
                 1790 
                 1450 
               
               
                 7 
                 1 
                 1 
                 3 
                 3 
                 2 
                 2 
                 12.00 
                 1490 
                 2610 
                 1790 
                 1450 
               
               
                 8 
                 1 
                 2 
                 4 
                 5 
                 2 
                 1 
                 12.00 
                 1490 
                 2610 
                 1790 
                 1450 
               
               
                   
               
             
          
         
       
     
       Example 2 
       [0052]    Formation and implantation of an articular head spacer implant from the shrunk flat-knitted poly(urethane urea) ribbon of Example 1. An articular implant  2  is excised from the ribbon  1   s  at bedside. In implantation the implant  2  is disposed, for instance, on the articular head of a proximal interphalangeal joint. The implant  2  is be affixed to the bone by suturing or stapling. 
         [0053]    For convenience of handling, a set of implant bodies of varying size and/or form, such as the set  2   a ,  2   b ,  2   c  illustrated in  FIGS. 1   c - 1   e , can be provided to the medical profession. The availability of the set allows the physician to select an implant body of suitable size and/or form, and to trim it to make it fit the particular purpose. Implants of standardized size and form that need not to be trimmed can also be provided as single items or in form of sets. 
       Example 3 
       [0054]    Shrunk flat-knitted double interlaced poly(urethane urea) ribbon. Yarn: 13 Tex poly(urethane urea) (Artelon®, Artimplant AB, Göteborg, Sweden). Equipment: Comez DNB/EL-800 (Comez s.p.A., Cilavegna, Italy) double needle bed crochet machine, for the production of technical and medical articles. Machine specifications: 15 gauge, 6 weft bars, double needle bed, latch needles. Heat set unit: Comez HSD/800 comprising 2 heat-set cylinders. 
         [0055]    A ribbon  200  of two parallel warp knitted layers was knit, a front layer  201 ,  201 ′,  201 ″, etc. of a thickness of about 1.0 mm, and a rear layer  202 ,  202 ′,  202 ″, etc., of a thickness of about 1.6 mm. The layers  201 ,  201 ′,  201 ″;  202 ,  202 ′,  202 ″ interlace over sections  203 ,  203 ′,  203 ″, etc. separated by the non-interlaced sections disposed equidistantly along the ribbon  200  ( FIG. 3   a ). The ribbon  200  is shrunk in the heat set unit to form a shrunk ribbon  200   s , in which the elements of the non-shrunk ribbon retain their reference numbers followed by “s” ( FIG. 3   b ). Process parameters: Knitting speed: 26 cm/min; heat set unit speed: 14 cm/min; shrinkage along warp: about 45%; shrinkage across warp: about 45%. Reference numbers  206 ,  206   s  indicate separation between non-interlaced sections. 
       Example 4 
       [0056]    Formation and implantation of a first articular spacer from the shrunk flat-knitted poly(urethane urea) double interlaced ribbon of Example 3. Implant bodies  300 , etc. of identical size and shape, each comprising an interlacing section,  203   s ,  203   s ′,  203   s ″ and a pair of adjoining non-interlacing sections, that is a top section  201   s ,  202   s ′;  201   s ″. and a bottom section  202   s ,  202   s ′,  202   s ″ are cut out from the shrunk interlaced ribbon  200   s  along cutting planes S 1 , S 2 , S 3 , S 4  ( FIG. 4   a ). Bending away the non-interlaced sections  201   s ,  202   s  of the implant body  300  in opposite directions results in a T-formed articular spacer  300 ′ ( FIGS. 4   b ,  4   c ) of the general geometric kind disclosed in FIG. 1 of U.S. Pat. No. 7,037,342 B2. Intra-articular implantation of the spacer  300 ′ and fixation is accomplished in a manner substantially corresponding to that disclosed for the known T-formed spacer of U.S. Pat. No. 7,037,342 B2. 
       Example 5 
       [0057]    Formation and implantation of a second articular spacer from the shrunk flat-knitted poly(urethane urea) double interlaced ribbon of Example 3. Implant bodies  310  ( FIG. 5 ), etc. of identical size and shape, each comprising an interlacing section,  203   s ,  203   s ′,  203   s ″, etc. and a pair of adjoining non-interlacing sections, that is a top section  311   s , etc. and a bottom section  202   s ,  202   s ′,  202   s ″, etc. are cut out from the shrunk ribbon  200   s  along cutting lines S 10 , S 10 ′, S 11 , S 11 ′, S 12 , S 12 ′, S 13 , S 13 ′, etc. ( FIG. 5   a ). Bending away the non-interlaced sections  201   s ,  202   s  of the implant body  310  in opposite directions results in a T-formed articular spacer  310 ′ ( FIG. 5   b ) of the general geometric kind disclosed in FIG. 1 of U.S. Pat. No. 7,037,342 B2. Intra-articular implantation of the spacer  310 ′ and fixation is accomplished in a manner substantially corresponding to that disclosed for the known T-formed spacer of U.S. Pat. No. 7,037,342 B2. 
       Example 6 
       [0058]    Formation and implantation of a third articular spacer from the shrunk flat-knitted poly(urethane urea) double interlaced ribbon of Example 3. Implant bodies  410  ( FIGS. 6 ,  6   b ) of identical size and shape, each comprising wings,  412 ,  413  extending diametrically opposite from a central body  411  are cut out from the shrunk ribbon  200   s  along cutting lines S 20 , S 20 ′, S 20 ″, S 20 ′″; S 21 , S 21 ′, S 21 ″, S 21 ′″, etc. ( FIG. 6   a ). In addition, material of the interlaced portion extending from the central body  411  in a transverse direction (in respect of the ribbon  200   s ) has to be removed (cut off) to bring the thickness of portions  414 ,  415  formed from section  203   s  to that of the wings  412 ,  413 , which are formed from non-interlaced portions  201   s ,  201   s′.    
         [0059]    Implantation of the implant  410  on a head  400  of a joint is illustrated in  FIGS. 7   a - 7   c . The central portion of the head  400  is diseased. Some surface areas  402  are entirely lacking cartilage  401  or their cartilage layer is compromised. In addition the subchondral bone of a central area is affected ( FIG. 7   a ). The bone  400  is prepared for implantation by removing diseased cartilage and bone. A shallow depression  405  in the bone  400  in form of the frustrum of a cone is scooped out to remove the diseased bone tissue. The depth and form of the depression  405  matches the portion of the implant&#39;s central body  411  extending from the wings  412 ,  413  towards the smaller circular end face of the central body  411 . This portion of the implant  411  is inserted into the depression  405 . One flat side of the flexible wings  411 ,  412  is now in abutment with a bone surface from which diseased cartilage has been removed. The implant  410  is fastened on the bone  400  by biocompatible glue, optionally in combination suturing to adjacent cartilage. 
       Example 7 
       [0060]    Shrunk flat-knitted double interlaced poly(urethane urea) ribbon. Yarn: 13 Tex poly(urethane urea) (Artelon®, Artimplant AB, Göteborg, Sweden). Equipment: Comez DNB/EL-800 (Comez s.p.A., Cilavegna, Italy) double needle bed crochet machine, for the production of technical and medical articles. Machine specifications: 15 gauge, 6 guide bars, double needle bed, latch needles. Heat set unit: Comez HSD/800 comprising 2 heat-set cylinders. 
         [0061]    A ribbon  600  of two parallel warp knitted layers was knit, a front layer  601 ,  601 ′,  601 ″, etc. of a thickness of about 1 mm, and a rear layer  602 ,  602 ′,  602 ″, etc. of same thickness. The layers  601 ,  601 ′,  601 ″;  602 ,  602 ′,  602 ″ interlace over sections  603 ,  603 ′,  603 ″, etc. separated by the non-interlaced sections disposed equidistantly along the ribbon  600  ( FIG. 8   a ). The ribbon  600  is shrunk in the heat set unit to form a shrunk ribbon  600   s , in which the elements of the non-shrunk ribbon retain their reference numbers followed by “s”. Process parameters: Knitting speed: 18/22 cm/min; heat set unit speed: 10/12 cm/min; shrinkage along warp: about 45%; shrinkage across warp: about 45%. The warp knitting pattern is shown in Table 2. It is a sequence of 120 steps with 8.5 loops/cm for the interlace and 10 loops/cm for the non-interlaced sections. Four guide bars were employed to produce the ribbon  600  shown in  FIG. 8   a . 
         [0000]    
       
         
               
             
               
               
               
               
             
               
               
               
               
               
               
               
             
               
               
               
               
               
               
               
               
               
               
               
               
               
             
               
               
             
               
               
               
               
               
               
               
               
               
               
               
               
               
             
               
               
             
           
               
                 TABLE 2 
               
             
             
               
                   
               
               
                 Warp knitting pattern of interlaced ribbon 
               
             
          
           
               
                 Loop 
                 Binding device movement 
                 Loops/ 
                 Alimentation device setting 
               
             
          
           
               
                 row 
                 2 
                 4 
                 5 
                 7 
                 cm 
                 (warp feed) 
               
               
                   
               
             
          
           
               
                 1 
                 2 
                 2 
                 2 
                 2 
                 2 
                 3 
                 2 
                 1 
                 8.50 
                 2050 
                 2300 
                 2050 
               
               
                 2 
                 2 
                 1 
                 2 
                 3 
                 2 
                 2 
                 1 
                 1 
                 8.50 
                 2050 
                 2300 
                 2050 
               
               
                 3 
                 1 
                 1 
                 2 
                 2 
                 2 
                 1 
                 1 
                 2 
                 8.50 
                 2050 
                 2300 
                 2050 
               
               
                 4 
                 1 
                 2 
                 2 
                 1 
                 2 
                 2 
                 2 
                 2 
                 8.50 
                 2050 
                 2300 
                 2050 
               
             
          
           
               
                 5-56 
                 13x [1-4] 
               
             
          
           
               
                 57 
                 2 
                 2 
                 2 
                 2 
                 2 
                 3 
                 2 
                 1 
                 8.50 
                 2050 
                 2300 
                 2050 
               
               
                 58 
                 2 
                 1 
                 2 
                 3 
                 2 
                 2 
                 1 
                 1 
                 8.50 
                 2050 
                 2300 
                 2050 
               
               
                 59 
                 1 
                 1 
                 3 
                 2 
                 2 
                 2 
                 1 
                 2 
                 10.00 
                 1850 
                 2300 
                 1850 
               
               
                 60 
                 1 
                 2 
                 2 
                 2 
                 2 
                 1 
                 2 
                 2 
                 10.00 
                 1850 
                 2300 
                 1850 
               
               
                 61 
                 2 
                 2 
                 2 
                 1 
                 2 
                 2 
                 2 
                 1 
                 10.00 
                 1850 
                 2300 
                 1850 
               
               
                 62 
                 2 
                 1 
                 2 
                 2 
                 2 
                 3 
                 1 
                 1 
                 10.00 
                 1850 
                 2300 
                 1850 
               
               
                 63 
                 1 
                 1 
                 2 
                 3 
                 2 
                 2 
                 1 
                 2 
                 10.00 
                 1850 
                 2300 
                 1850 
               
               
                 64 
                 1 
                 2 
                 2 
                 2 
                 2 
                 1 
                 2 
                 2 
                 10.00 
                 1850 
                 2300 
                 1850 
               
             
          
           
               
                 65-120 
                 14x [61-65]