Abstract:
This invention pertains to cationic acrylic colloidal dispersion polymers which contain a stabilizer that is covalently bonded to the polymer. More particularly, the invention pertains to the use of stabilizer-containing cationic acrylic colloidal dispersion polymer compositions to enhance the ink jet printability of coating formulations.

Description:
[0001]    This application is a continuation-in-part of our commonly assigned, co-pending U.S. patent application Ser. No. 09/803,829 filed Mar. 12, 2001, entitled “Cationic Colloidal Dispersion Polymers For Ink Jet Coatings”. 
     
    
     
       FIELD OF INVENTION  
         [0002]    This invention pertains to cationic acrylic colloidal dispersion polymers which contain a stabilizer that is covalently bonded to the polymer. More particularly, the invention pertains to the use of stabilizer-containing cationic acrylic colloidal dispersion polymer compositions to enhance the ink jet printability of coating formulations.  
         BACKGROUND OF THE INVENTION  
         [0003]    Ink jet printing is widely used to print on a variety of substrates (including paper, textiles, and plastic films). These substrates are often coated with a material that enhances their receptivity for the ink jet ink. In the case of aqueous dye-based inks, which comprise the majority of inks currently used in ink jet printing, two properties are of paramount importance. The first is an affinity for water, as the coating must absorb a large amount of water from the ink in order to obtain a print that is dry to the touch in few seconds. Ink jet ink formulations often contain over 90% water. Furthermore, the coating must maintain its physical integrity while absorbing all of this water. In other words, the receptive coating must be hydrophilic enough to absorb a large quantity of water without actually being water-soluble.  
           [0004]    The second important property is dye fixation. The majority of aqueous ink jet inks are based on dyes rather than pigments. To obtain sharp prints with high color density, the dye molecules must be immobilized almost immediately upon contact of the ink with the substrate. Penetration of the dyes into the substrate will result in reduced color density, while lateral migration of the dye molecules will cause indistinctness in the image formed.  
           [0005]    In order to obtain high water absorption, ink jet receptive coatings have traditionally been formulated with both hydrophilic pigments (such as silica or alumina) and hydrophilic binders. While the most commonly used hydrophilic binders are polyvinyl alcohol (PVOH) and polyvinylpyrrolidinone (PVP), other suitable natural and synthetic polymers are known in the art (e.g., gelatin, starch, polyethylene oxide (PEO), hydroxyethylcellulose, carboxymethylcellulose, and the like). Those polymers that contain hydroxyl groups (such as starch, PVOH, and PEO) are often cross-linked with a compound such as glyoxal or glutaraldehyde to render them water-insoluble while maintaining their hydrophilicity. Fully hydrolyzed polyvinyl alcohol is particularly useful because it can be dissolved in hot water and remains in solution when cooled to room temperature. When the PVOH is coated on a substrate and then dried, it will not readily redissolve in room-temperature water. However, a problem exists with use of PVOH in that PVOH has no dye trapping properties.  
           [0006]    The dyes that are commonly employed in aqueous ink jet inks are anionic, containing sulfonic acid groups. Thus dye fixation is usually accomplished by the employment of cationic polymers, although some highly polar nonionic polymers (such as PVP and polyethyloxazoline) have a limited amount of dye fixing capability. These latter polymers fix dyes by dipolar interactions between their amide groups and the sulfonic acid groups of the dye molecules, while the cationic polymers work by the more efficient mechanism of salt formation.  
           [0007]    The most widely used cationic dye fixative in ink jet receptive coatings is poly(diallyldimethylammonium chloride), although other water-soluble cationic polymers are known in the art. For example, U.S. Pat. No. 6,010,790 teaches the use of poly(vinylbenzylquaternary ammonium salts). Other examples of water-soluble cationic polymers are cationic starch, cationic polyvinyl alcohol, guanidine-formaldehyde resins, epichlorohydrin-polyamine condensates, and water-soluble cationic acrylic resins.  
           [0008]    However, a problem exists with the use of both soluble dipolar polymers and soluble cationic polymers in that, unless these polymers are cross-linked in some way, their presence has a detrimental effect on the water resistance of the ink jet prints.  
           [0009]    As an alternative to water-soluble cationic resins, cationic acrylic or styrenic latices can be used as fixatives for anionic dyes in ink jet receptive coatings. These latices behave like plastic pigments. Attaching the positive charges to the surface of a pigment particle rather than to a soluble resin greatly enhances the water resistance of the ink jet prints. However, using substantial amounts of these cationic plastic pigments in a coating also results in rheological problems, which make the coatings difficult to employ on coating machinery. Furthermore, the level of cationic charge achievable with the cationic plastic pigment may not be high enough to achieve the desired level of dye fixing.  
           [0010]    Anionic acrylic colloidal dispersion polymeric resins are widely used in the ink and coatings industries. Such polymers are manufactured by first making an acrylic latex that contains a substantial amount of an acidic monomer (such as methacrylic acid). Usually the amount of acidic monomer is sufficient to give the polymer an acid number of about 60 to about 120. The acidic functionality of the polymer is subsequently neutralized via the employment of a base (such as sodium hydroxide, potassium hydroxide, ammonia, or a water-soluble amine). This greatly enhances the hydrophilicity of the polymer, and the latex particles first swell and then lose their discreteness. While the resulting anionic acrylic colloidal dispersion polymeric resin product appears to be clear and homogeneous on a macroscopic basis, it is actually inhomogeneous on a molecular level, having some domains that are rich in hydrophobic moieties and other domains that are rich in hydrophilic ones. If a fugitive base is employed in the neutralization, these polymer dispersions dry to form water-insoluble films.  
           [0011]    Ink jet images are commonly formed by spraying ink formulations, the majority of which are aqueous dye-based ink solutions, onto ink jet receptive coatings. The dyes are molecularly adsorbed on the surface of the coating, where they are subsequently exposed to ambient atmospheric pollutants and light. Over time, photochemical reactions and chemical reactions with oxygen, ozone, nitrogen oxides, and/or sulfur oxides commonly cause the dyes to fade.  
           [0012]    Therefore, an object of this invention is to disclose stabilizer-containing cationic acrylic colloidal dispersion polymer compositions which behave like traditional anionic dispersions, but with the opposite electrical charge.  
           [0013]    Another object of this invention is to disclose stabilizer-containing cationic acrylic colloidal dispersion polymer compositions which exhibit properties that allow them to be useful in producing ink jet ink printing coating formulations.  
         SUMMARY OF THE INVENTION  
         [0014]    The objects of this invention are met via the production of stabilizer-containing cationic polymers for ink jet receptive coatings that eliminate many of the problems involved in using cationic latices or soluble cationic polymers. These novel polymers are stabilizer-containing cationic acrylic colloidal dispersion polymer compositions. As used herein the term “stabilizer” means a compound which contains in its molecular chain sites possessing ultraviolet absorbing activity, free radical scavenging activity, antioxidant activity, and/or peroxide decomposing activity.  
           [0015]    As noted above, traditional anionic acrylic colloidal dispersion polymeric resins are produced by employing a base to neutralize the acidic functionality of the core polymer. In contrast, the stabilizer-containing cationic acrylic colloidal dispersion polymer compositions of the present invention may be described as the reverse image of such anionic dispersion resins noted in that the cationic polymer compositions contain basic functionalities which are subsequently neutralized with acid. These basic groups are provided by the employment of amine-functional monomers in the acrylic polymer. Such amine monomers may be any compound that contains both polymerizable ethylenic unsaturation and an amine group (which may be primary, secondary, or tertiary). Ink jet receptive coatings formulated with these stabilizer-containing cationic acrylic colloidal dispersion polymer compositions produce prints having improved fade resistance, enhanced definition, and superior color density.  
         DESCRIPTION OF THE PREFERRED EMBODIMENT  
         [0016]    The stabilizer-containing cationic acrylic colloidal dispersion polymer compositions of the present invention comprise the reaction products produced by:  
           [0017]    (A) reacting in a free radical polymerization reaction a mixture comprising:  
           [0018]    (1) about 1.0% to about 35.0% by total weight of the mixture of a member selected from the group consisting of amine-containing ethylenically unsaturated monomers and combinations thereof;  
           [0019]    (2) about 10.0% to about 50.0% by total weight of the mixture of a member selected from the group consisting of acrylic esters of alcohols containing from 1 to 22 carbon atoms, methacrylic esters of alcohols containing from 1 to 22 carbon atoms, styrene, substituted styrenes, acrylonitrile, methacrylonitrile, vinyl chloride, vinylidene chloride, vinyl ethers, vinyl esters, N-vinyl amides, and combinations thereof;  
           [0020]    (3) about 0.5% to about 20.0% by total weight of the mixture of stabilizer selected from the group consisting of ultraviolet absorbers which contain at least one ethylenically unsaturated group, radical scavengers which contain at least one ethylenically unsaturated group, antioxidants which contain at least one ethylenically unsaturated group, peroxide decomposers which contain at least one ethylenically unsaturated group, and combinations thereof;  
           [0021]    (4) up to about 8.0% by total weight of the mixture of a member selected from the group consisting of ethylenically unsaturated monomers containing at least one quaternary ammonium group and combinations thereof;  
           [0022]    (5) up to about 8.0% by total weight of the mixture of a member selected from the group consisting of ethylenically unsaturated monomers containing at least one hydroxyl group and combinations thereof;  
           [0023]    (6) up to about 8.0% by total weight of the mixture of a member selected from the group consisting of N-hydroxymethyl acrylamide, N-hydroxymethyl methacrylamide, N-hydroxymethyl-substituted acrylamide, N-hydroxymethyl-substituted methacrylamide, and combinations thereof;  
           [0024]    (7) up to about 4.0% by total weight of the mixture of a chain transfer agent;  
           [0025]    (8) about 0.5% to about 8.0% by total weight of the mixture of a surfactant selected from the group consisting of nonionic surfactants, cationic surfactants, and combinations thereof;  
           [0026]    (9) a catalytic amount of polymerization initiator; and  
           [0027]    (10) the balance of the mixture being water; to produce an emulsion polymerization product having a solids content in the range of about 25.0% to about 50.0%; and  
           [0028]    (B) adjusting said emulsion polymerization product to a pH in the range of about 3.5 to about 7.0 to produce the stabilizer-containing cationic acrylic colloidal dispersion polymer composition.  
           [0029]    Preferred stabilizer-containing cationic acrylic colloidal dispersion polymer compositions comprise the reaction products produced by:  
           [0030]    (A) reacting in a free radical polymerization reaction a mixture of monomers comprising:  
           [0031]    (1) about 4.0% to about 30.0% by total weight of the mixture of a member selected from the group consisting of amine-containing ethylenically unsaturated monomers and combinations thereof;  
           [0032]    (2) about 15.0% to about 40.0% by total weight of the mixture of a member selected from the group consisting of acrylic esters of alcohols containing from 1 to 22 carbon atoms, methacrylic esters of alcohols containing from 1 to 22 carbon atoms, styrene, substituted styrenes, acrylonitrile, methacrylonitrile, vinyl chloride, vinylidene chloride, vinyl ethers, vinyl esters, N-vinyl amides, and combinations thereof;  
           [0033]    (3) about 0.5% to about 15.0% by total weight of the mixture of stabilizer selected from the group consisting of ultraviolet absorbers which contain at least one ethylenically unsaturated group, radical scavengers which contain at least one ethylenically unsaturated group, antioxidants which contain at least one ethylenically unsaturated group, peroxide decomposers which contain at least one ethylenically unsaturated group, and combinations thereof;  
           [0034]    (4) up to about 5.0% by total weight of the mixture of a member selected from the group consisting of ethylenically unsaturated monomers containing at least one quaternary ammonium group and combinations thereof;  
           [0035]    (5) up to about 5.0% by total weight of the mixture of a member selected from the group consisting of ethylenically unsaturated monomers containing at least one hydroxyl group and combinations thereof;  
           [0036]    (6) up to about 5.0% by total weight of the mixture of a member selected from the group consisting of N-hydroxymethyl acrylamide, N-hydroxymethyl methacrylamide, N-hydroxymethyl-substituted acrylamide, N-hydroxymethyl-substituted methacrylamide, and combinations thereof;  
           [0037]    (7) up to about 3.0% by total weight of the mixture of a chain transfer agent;  
           [0038]    (8) about 1.0% to about 5.0% by total weight of the mixture of a surfactant selected from the group consisting of nonionic surfactants, cationic surfactants, and combinations thereof;  
           [0039]    (9) a catalytic amount of polymerization initiator; and  
           [0040]    (10) the balance of the mixture being water; to produce an emulsion polymerization product having a solids content in the range of about 30.0% to about 45.0%; and  
           [0041]    (B) adjusting said emulsion polymerization product to a pH in the range of about 4.0 to about 6.0 to produce the stabilizer-containing cationic acrylic colloidal dispersion polymer composition.  
           [0042]    As noted above, the stabilizer-containing cationic acrylic colloidal dispersion polymer compositions of the present invention differ from traditional anionic dispersion resins in that the cationic compositions contain basic groups and are neutralized with acid. These basic groups are provided by the use of amine-functional monomers in the production of the acrylic polymer. Amine-containing ethylenically unsaturated monomers which are suitable for use in the present invention include those compounds containing both polymerizable ethylenic unsaturation and at least one amine group, which may be primary, secondary, or tertiary. Preferred amine-containing ethylenically unsaturated monomers include dimethylaminoethyl acrylate, dimethylaminoethyl methacrylate, diethylaminoethyl methacrylate, t-butylaminoethyl methacrylate, dimethylaminopropyl methacrylamide, allylamine, 2-vinylpyridine, 4-vinylpyridine, and the like. The amine-containing ethylenically unsaturated monomer comprises from about 1.0% to about 35.0%, preferably from about 4.0% to about 30.0%, by weight of the total mixture employed to produce the emulsion polymer.  
           [0043]    In addition to amine-containing ethylenically unsaturated monomers, other functional monomers which contain reactive groups may be incorporated into the free radical polymerization reaction in order to tailor the resulting cationic acrylic colloidal dispersion polymer compositions. For example, the emulsion polymerization product (which is a latex) may be stabilized during the manufacturing process via the inclusion of up to about 8.0% (preferably up to about 5.0%) by weight of the total mixture of ethylenically unsaturated monomers containing at least one quaternary ammonium group. Quaternary ammonium monomers which are suitable for use in the present invention include those compounds which contain both polymerizable ethylenic unsaturation and at least one quaternary ammonium group. Preferred quaternary ammonium monomers include vinylbenzyltrimethylammonium chloride, methacryloyloxyethyltrimethylammonium chloride, methacrylamidopropyltrimethylammonium chloride and the like.  
           [0044]    Where desired, the cationic acrylic colloidal dispersion polymer compositions may be given hydroxyl functionality via the inclusion of up to about 8.0% (preferably up to about 5.0%) by weight of the total mixture of hydroxyl-containing monomers. Hydroxyl-containing monomers which are suitable for use in the present invention include those monomers containing polymerizable ethyleneic unsaturation and at least one hydroxyl group. Preferred hydroxyl-containing monomers include hydroxyethyl acrylate, hydroxypropyl acrylate, hydroxybutyl acrylate, hydroxyethyl methacrylate, hydroxypropyl methacrylate, butanediol monovinyl ether, allyl alcohol, and the like. The presence of hydroxyl groups in the polymer allows it to be cross-linked with cross-linking agents that are conventionally used in coatings (such as aminoplast resins, glyoxal, glutaraldehyde, and the like).  
           [0045]    Where desired, the cationic acrylic colloidal dispersion polymer compositions may also be made self cross-linkable via the inclusion of up to about 8.0% (preferably up to about 5.0%) by weight of the total mixture of a member selected from the group consisting of N-hydroxymethyl acrylamide, N-hydroxymethyl methacrylamide, N-hydroxymethyl-substituted acrylamide, N-hydroxymethyl-substituted methacrylamide, and combinations thereof.  
           [0046]    The remaining monomer component of the mixture may be any non-functional monomers which are customarily employed in the manufacture of acrylic latices. That is, from about 10.0% to about 50.0% (preferably from about 15.0% to about 40.0%) by total weight of the mixture is comprised of a member selected from the group consisting of acrylic esters of alcohols containing from 1 to 22 carbon atoms, methacrylic esters of alcohols containing from 1 to 22 carbon atoms, styrene, substituted styrenes, acrylonitrile, methacrylonitrile, vinyl chloride, vinylidene chloride, vinyl ethers, vinyl esters, N-vinyl amides, and combinations thereof.  
           [0047]    The incorporation of a stabilizer in the free radical polymerization reaction results in the stabilizer being covalently bonded to the polymer. The stabilizer comprises from about 0.5% to about 20.0%, preferably from about 0.5% to about 15.0%, by weight of the total mixture employed to produce the emulsion polymer. Any ultraviolet absorber, radical scavenger, antioxidant, or peroxide decomposer which contains at least one ethylenically unsaturated group (thereby being capable of covalent bonding to the polymer via free radical polymerization reaction) is suitable for use in the present invention. Commonly known methods of producing such compounds containing at least one ethylenically unsaturated group include acryloyation and reacting the compound to be modified with a reactant that contains at least one acryloyl group (e.g., glycidyl (meth)acrylate or isocyanatoethyl (meth)acrylate). Where an ultraviolet absorber is employed as a stabilizer it is preferred that the absorber be a member selected from the group consisting of hydroxyphenylbenzotrazoles containing at least one ethylenically unsaturated group, hydroxyphenylbenzophenones containing at least one ethylenically unsaturated group, porphines which have been modified to contain at least one ethylenically unsaturated group, and combinations thereof. Where a radical scavenger is employed as a stabilizer it is preferred that the scavenger be a member selected from the group consisting of tetramethylpiperidine derivatives containing at least one ethylenically unsaturated group and combinations thereof. Where an antioxidant is employed as a stabilizer it is preferred that the antioxidant be a member selected from the group consisting of sterically-hindered phenols containing at least one ethylenically unsaturated group, diarylamines containing at least one ethylenically unsaturated group, and combinations thereof. Where a peroxide decomposer is employed as a stabilizer it is preferred that the decomposer be a member selected from the group consisting of triphenyl phosphites which have been modified to contain at least one ethylenically unsaturated group, mercaptans which have been modified to contain at least one ethylenically unsaturated group, and combinations thereof. Suitable modified triphenyl phosphites and modified mercaptans (such as modified thiodipropionic acids, thiobenzimidazoles, bisaryldisulphides, and the like) may be produced by any method which results in the modified compound containing at least one ethylenically unsaturated group. For example, triphenyl phosphite can be prepared with a combination of styryl phenol and 2,4-di-tertiary butyl phenol. Likewise, thiodipropionic acid can be reacted with glycidyl methacrylate to produce the modified compound.  
           [0048]    Where desired, up to about 4.0% (preferably up to about 3.0%) by total weight of the mixture of a chain transfer agent may be employed in the polymerization reaction in order to lower the molecular weight of the emulsion polymer. Preferred chain transfer agents include dodecyl mercaptan, 2-mercaptoethanol, alkyl mercaptopropionates, mercaptoacetic acid, mercaptopropionic acid, octyl mercaptan, and the like.  
           [0049]    Surfactants suitable for use in the emulsion polymerization reaction include members selected from the group consisting of nonionic surfactants, cationic surfactants, and combinations thereof. Preferred nonionic surfactants include ethoxylated alkylphenols, ethoxylated fatty alcohols, ethylene oxide/propylene oxide block copolymers, and the like. Preferred cationic surfactants include, but are not limited to, the following: alkyltrimethylammonium salts wherein the alkyl group contains from 8 to 22 (preferably 12 to 18) carbon atoms and the counterion of the salt is a member selected from the group consisting of chloride, bromide, methylsulfate, and ethylsulfate; alkylbenzyldimethylammonium salts wherein the alkyl group contains from 8 to 22 (preferably 12 to 18) carbon atoms and the counterion of the salt is a member selected from the group consisting of chloride, bromide, methylsulfate, and ethylsulfate; and alkylpyridinium salts wherein the alkyl group contains from 8 to 22 (preferably 12 to 18) carbon atoms and the counterion of the salt is a member selected from the group consisting of chloride, bromide, methylsulfate, and ethylsulfate. The surfactant comprises from about 0.5% to about 8.0%, preferably from about 1.0% to about 5.0%, by weight of the total mixture employed to produce the emulsion polymer.  
           [0050]    A catalytic amount of polymerization initiator is used in the free radical polymerization reaction. The amount of initiator employed commonly comprises from about 0.1% to about 3.0% (preferably from about 0.2% to about 2.0%) by weight of the total mixture used to produce the emulsion polymer. Traditional emulsion polymerization initiators (such as thermal initiators, redox initiators, and the like) are suitable for use in the emulsion polymerization reaction. Examples of suitable thermal initiators include, but are not limited to, the following: t-butyl hydroperoxide, di-t-butyl peroxide, benzoyl peroxide, benzoyl hydroperoxide, 2,4-dichlorobenzoyl peroxide, t-butyl peracetate, azobisisobutyronitrile, and isopropyl peroxycarbonate. Examples of suitable redox initiators include cumene hydroperoxide-sodium metabisulfite, cumene hydroperoxide-iron (II) sulfate, and the like. Preferred initiators include water-soluble azo compounds (such as V-50 or VA-086 manufactured by Wako Chemicals).  
           [0051]    Sufficient water is added to the mixture to produce an emulsion polymerization product (latex) having a solids content in the range of about 25.0% to about 50.0%. The preferred solids content for the emulsion polymerization product is in the range of about 30.0% to about 45.0%.  
           [0052]    Neutralization of the initially formed amine-containing latex emulsion polymerization product to form the aqueous dispersion form of the polymer can be accomplished via the addition of mineral acids (such as nitric or hydrochloric acids) or organic acids (such as water-soluble carboxylic acids or water-soluble sulfonic acids). It is preferred to use low molecular weight carboxylic acids such as acetic acid, propionic acid, glycolic acid, lactic acid, and the like for neutralization, as these acids will evaporate readily upon drying of the coating containing the polymer (thereby rendering the coating water-insoluble). Furthermore, carboxylic acids are less corrosive to coating equipment than are the stronger sulfonic and mineral acids.  
           [0053]    For maximum effectiveness as a coating binder, the pH of the neutralized stabilizer-containing cationic acrylic colloidal dispersion polymer composition should be in the range of about 3.5 to about 7.0, preferably from 4.0 to about 6.0.  
           [0054]    The stabilizer-containing cationic acrylic colloidal dispersion polymer compositions of the present invention are superior ink jet receptive coatings. Such ink jet receptive coatings can be employed to produce ink jet printable products via the process of coating a chosen substrate on at least one side with the ink jet receptive coating. Substrates which are suitable for use in producing such ink jet printable products include paper, paperboard, wood, plastic film, metal foil, textiles, and the like. Where desired, any of the pigments traditionally used in ink jet receptive coatings can be employed in the coating provided that the pigments are compatible with a cationic binder. Such pigments include, but are not limited to, the following: silica, alumina, plastic pigments, calcium carbonate, and kaolin clay.  
           [0055]    Where desired, other cationic and nonionic binders can be used in conjunction with the stabilizer-containing cationic acrylic colloidal dispersion polymer compositions. These binders include, but are not limited to, the following: polyvinyl alcohol, cationic polyvinyl alcohol, polyvinylpyrrolidone, cationic vinylpyrrolidone copolymers, polyethyloxazoline, cationic water-soluble acrylic polymers, nonionic water-soluble acrylic polymers, starch, cationic starch, polyethylene glycol, methylcellulose, hydroxyethylcellulose, and mixtures thereof.  
           [0056]    In cases where the stabilizer-containing cationic acrylic colloidal dispersion polymer contains hydroxyl functionality, cross-linkers that are traditionally used with hydroxyl-functional resins can be added to the coating. Such cross-linkers include urea-formaldehyde resins, melamine-formaldehyde resins, glyoxal, glutaraldehyde, titanates, zirconium salts, and the like.  
           [0057]    As appreciated in the art, the exact components and properties of components desired for any coating application can vary and, therefore, routine experimentation may be required to determine the optional components and proportions of components for a given application and desired properties.  
           [0058]    The following examples are provided to further illustrate the present invention and are not to be construed as limiting the invention in any manner. 
       
    
    
     EXAMPLE 1  
       [0059]    A cationic acrylic colloidal dispersion polymer composition containing a bound stabilizer was prepared as follows. To a round-bottomed flask fitted with a mechanical stirrer, heating mantle, and inlet tubes for monomer feed was charged 417.4 g of water and 48.0 g of ARQUAD C-50 (a 50% solution of a cationic surfactant in isopropyl alcohol manufactured by Akzo Nobel). Two monomer feeds were then prepared. The first was a mixture of 132.0 g of styrene, 48.0 g of butyl acrylate, 90.0 g of dimethylaminoethyl methacrylate, and 6.0 g of NORBLOC 7966 (an acrylate-functional ultraviolet absorber manufactured by Ciba Specialty Chemicals). The second feed was 30 g of MHOROMER BM-606 (a 75% aqueous solution of methacryloyloxyethyltrimethylammonium chloride manufactured by Röhm America, Inc.). Fifteen percent of each monomer feed was charged to the flask along with a solution of 6.0 g of V-50 (an azo polymerization initiator manufactured by Wako Chemicals) in 15.0 g of water. The contents of the flask were then heated to 60° C., and the remainders of the two monomer feeds were added concurrently over three hours. Reaction was continued for an additional hour at 60° C., and then 0.45 g of t-butyl hydroperoxide and a solution of 0.88 g of isoascorbic acid in 10.0 g of water were added. Heating was continued at 60° C. to complete the polymerization. The resultant latex had a solids content of 40.7%, a pH of 8.2, a viscosity of 160 cP, and an average particle size of 81 nm. The latex was converted into a stabilizer-containing cationic acrylic colloidal dispersion polymer composition via neutralization with lactic acid to a pH of 5.0.  
         [0060]    A coating was prepared by mixing together 60 parts on a dry basis of TRUDOT™ DPX-7817-83 (a cationic plastic pigment latex manufactured by Westvaco Corp.), 40 parts on a dry basis of CAB-O-SPERSE PG003 (a 40% aqueous dispersion of fumed alumina manufactured by Cabot Corp.), and 10 parts on a dry basis of the stabilizer-containing cationic acrylic colloidal dispersion polymer composition. The solids of the resulting ink jet receptive paper coating was adjusted to 30.4 weight-% with deionized water.  
         [0061]    A traditional polyvinyl alcohol-based coating was produced as a comparative example. The above coating preparation procedure was repeated except that the stabilizer-containing cationic acrylic colloidal dispersion polymer composition was replaced with 10 parts on a dry basis of AIRVOL 205 (a polyvinyl alcohol manufactured by Air Products, Inc.).  
         [0062]    The stabilizer-containing cationic acrylic colloidal dispersion polymer composition coating and the coating of the comparative example were each applied to HAMMERMILL Multipurpose paper using a No. 12 wire-wound rod. The coated sheets were then dried for 5 minutes at 110° C., and test prints were made on the dried sheets with black ink using an Epson 900 printer. The print made on the coating produced with the cationic polymer of the present invention showed much sharper definition, greater color density, and better resistance to light fading when compared with the print produced using the traditional polyvinyl alcohol-based coating.  
       EXAMPLE 2  
       [0063]    A cationic acrylic colloidal dispersion polymer composition containing a bound stabilizer was prepared as follows. To a round-bottomed flask fitted with a mechanical stirrer, heating mantle, and inlet tubes for monomer feed was charged 417.4 g of water and 48.0 g of ARQUAD C-50 (a 50% solution of a cationic surfactant in isopropyl alcohol manufactured by Akzo Nobel). Two monomer feeds had been prepared earlier. The first was a mixture of 132.0 g of styrene, 48.0 g of butyl acrylate, 90.0 g of dimethylaminoethyl methacrylate, and 3.0 g of IRGACURE 2959 (an hydroxyl-functional ultraviolet absorber manufactured by Ciba Specialty Chemicals), 3.0 g of meta-TMI (an isocyanate-functional styrenic monomer manufactured by Cytec Industries), and one drop of dibutyltin dilaurate. This first feed was allowed to stand at room temperature for several hours before use to allow the IRGACURE and the meta-TMI to react to form uv-absorbing, styreneic urethane monomer. The second feed was 30.0 g of MHOROMER BM-606 (a 75% aqueous solution of methacryloyloxyethyltrimethylammonium chloride manufactured by Röhm America, Inc.). Fifteen percent of each monomer feed was charged to the flask along with a solution of 6.0 g of V-50 (an azo polymerization initiator manufactured by Wako Chemicals) in 15 g of water. The contents of the flask were then heated to 60° C., and the remainders of the two monomer feeds were added concurrently over three hours. Reaction was continued for an additional hour at 60° C. The batch was then heated to 70° C., and 0.45 g of t-butyl hydroperoxide and a solution of 0.88 g of isoascorbic acid in 10.0 g of water were added. The batch was then heated to 85° C. and held there for two hours to complete the polymerization. The resultant latex had a solids content of 39.6%, a pH of 8.1, a viscosity of 66 cP, and an average particle size of  108  nm. The latex was converted into a stabilizer-containing cationic acrylic colloidal dispersion polymer composition via neutralization with lactic acid to a pH of 5.0.  
         [0064]    A coating was prepared by mixing together 60 parts on a dry basis of TRUDOT™ DPX-7817-83 (a cationic plastic pigment latex manufactured by Westvaco Corp.), 40 parts on a dry basis of CAB-O-SPERSE PG003 (a 40% aqueous dispersion of fumed alumina manufactured by Cabot Corp.), and 10 parts on a dry basis of the stabilizer-containing cationic acrylic colloidal dispersion polymer composition. The solids of the resulting ink jet receptive paper coating was adjusted to 30.4 weight-% with deionized water.  
         [0065]    A traditional polyvinyl alcohol-based coating was produced as a comparative example. The above coating preparation procedure was repeated except that the stabilizer-containing cationic acrylic colloidal dispersion polymer composition was replaced with 10 parts on a dry basis of AIRVOL 205 (a polyvinyl alcohol manufactured by Air Products, Inc.).  
         [0066]    The stabilizer-containing cationic acrylic colloidal dispersion polymer composition coating and the coating of the comparative example were each applied to HAMMERMILL Multipurpose paper using a No. 12 wire-wound rod. The coated sheets were then dried for 5 minutes at 110° C., and test prints were made on the dried sheets with black ink using an Epson 900 printer. The print made on the coating produced with the cationic polymer of the present invention showed much sharper definition, greater color density, and better resistance to light fading when compared with the print produced using the traditional polyvinyl alcohol-based coating.  
         [0067]    Many modifications and variations of the present invention will be apparent to one of ordinary skill in the art in light of the above teachings. It is therefore understood that the scope of the invention is not to be limited by the foregoing description, but rather is to be defined by the claims appended hereto.