Abstract:
A method of making micro-structure devices by coating a first layer of resist ( 12 ) on a substrate ( 10 ). A pattern is created on the substrate by radiation induced thermal removal of the resist.

Description:
CROSS REFERENCE TO RELATED APPLICATIONS 
       [0001]    Reference is made to commonly-assigned copending U.S. patent application Ser. No. 11/240,964, filed Sep. 30, 2005, entitled LASER RESIST TRANSFER MICROFABRICATION OF ELECTRONIC DEVICES; by Tredwell et al., the disclosure of which is incorporated herein. 
     
     FIELD OF THE INVENTION 
       [0002]    The present invention relates, in general, to fabrication of microelectronic devices and in particular to fabrication of microelectronic devices using a dry process with a resist formed by laser ablation. 
       BACKGROUND OF THE INVENTION 
       [0003]    Lithographic patterning techniques have been employed in conventional fabrication of microelectronic devices, including thin film transistors (TFT) arrays for flat panel application. Conventional photoresist lithographic techniques applied to microfabrication have proved capable of defining structures and forming regions of material on a substrate to within dimensions of about 100 nm. 
         [0004]    Based on a printing model, the lithographic process forms a pattern of areas that are either receptive or repellent (non-receptive) to a coating (such as ink) or to some other treatment. Conventional photolithography requires a small number of basic steps, with variations according to the materials used and other factors. A typical sequence is as follows:
       (i) wet coating of a positive-working or negative-working photoresist (such as by spin-coating);   (ii) prebake of the photoresist;   (iii) exposure by some form of electromagnetic radiation through an overlay mask using an optical mask aligner to form the pattern;   (iv) curing of the masked pattern, such as by postbake; and   (v) removal of the uncured portion, using a liquid etchant.       
 
         [0010]    Following subsequent coating or treatment of the surface, the protective photoresist pattern can then itself be removed. 
         [0011]    Steps (i)-(v) may be performed in air, such as in a clean room environment, and are typically performed using separate pieces of equipment. Alternately, one or more steps, such as coating deposition, may be performed in a vacuum. Because of the very different nature of processes carried out in each of these steps, it would not be readily feasible to combine steps (i)-(v) in any type of automated, continuous fabrication system or apparatus. 
         [0012]    Considerable effort has been expended to improve upon conventional methods as listed in steps (i)-(v) above in order to achieve better dimensional resolution, lower cost, and eliminate the use of chemicals such as etchants. One improvement of particular benefit has been the refinement of plasma etching techniques that eliminate the need for liquid etchants. With reference to step (v) listed above, the use of plasma etching is an enabler for performing microlithographic fabrication in a dry environment. 
         [0013]    As is well known to those skilled in the microlithographic art, conventional photoresist materials follow “reciprocity law,” responding to the total exposure received, the integral of illumination over time. Conventional photoresists are typically exposed with light in the UV portion of the spectrum, where photon energy is particularly high. Examples of photoresists used microfabrication of semiconductor components are given in U.S. Pat. No. 6,787,283 (Aoai et al.). 
         [0014]    Additional advantages to the conventional process described above are provided by e-beam and X-Ray lithography in that they provide a partial reduction of chemical processing, and while X-Ray lithography still requires the use of masks, e-beams can be used to write patterns in a resist directly without a mask. High energy radiation sufficient to cause bond breaking in organic materials causes chain scission, or depolymerization, in a coated resist such that it can be removed in the image area with solvents that will not remove the non-radiated areas. This type of lithographic process depends on imagewise differential salvation of the resist in the development step, and therefore retains the disadvantageous use of liquid chemicals, in addition to requiring expensive masks. E-beams, when used as a direct pattern writing device, suffer from low throughput due to long scan times as a result of the serial limitation of a single beam exposure, and are thus limited to low volume manufacture. E-beams are used primarily in the microfabrication industry to manufacture masks for conventional processes due to their sub-micron high resolution capability. 
         [0015]    A further improvement is provided by direct phtotoablation of a resist with a high energy laser at wavelengths less than 400 nm with energies sufficient to cause resist bond breaking, volatilization, and material evacuation of the resist in the irradiated areas, thus making the solvent development step unnecessary. However, the laser systems for direct UV ablation are quite expensive, pulse, difficult to maintain, and suffer from low throughput due to their single beam limitations. Large area eximer lasers solve that deficiency, but they suffer from the requirement of a mask to form the pattern. 
         [0016]    Therefore, a need exists for a method of direct writing, or maskless lithography that allows for the use a less expensive and versatile class of laser directed radiation, specifically the solid state IR diode lasers. IR diode lasers offer the advantages of cost, availability, reliability, and lifetime, and are used widely in the communications industry, in a variety of electronic devices such as CD and DVD writers and players, and in the graphic and reprographic arts including digital color printers, laser thermal platewriters, imagesetters, and proofers. In addition, the individual lasers can be joined in an array of up to almost one hundred or more separately modulated lasers dramatically increasing throughput compared to single beam devices. Alternatively, the light can be conjoined from several laser sources into a single bar laser fitted with a segmented light gate modulator of between 200 to up to 1000 separate addressable channels of individually controlled beams. The beam dimensions are limited only by the wavelength of the light they deliver, and can produce spots as small as 2 microns in the array direction as defined by the spatial light modulator. Examples of commercial laser systems with such capability are the Kodak Newsetter and the Creo Trensetter plate-writer-proofer. Feature resolution of 2 microns is therefore possible with such diode laser array systems, which is more than sufficient for thin film transistor array backplanes and color filter arrays used in LCD and OLED displays. These IR lasers, as well as YAG lasers that operate in the visible spectrum, suffer from photon energies less than sufficient to break organic bonds and effect direct ablation of resists. 
         [0017]    Additionally, a need exists for a maskless lithographic method for microstructure construction that limits or eliminates the need for wet chemical processing, in order to reduce cost and to be compatible flexible support substrates and roll to roll continuous manufacture. 
       SUMMARY OF THE INVENTION 
       [0018]    The invention and its objects and advantages will become more apparent in the detailed description of the preferred embodiment presented below. This invention relates to an improved process for manufacture of microstructured devices and especially microelectronic circuitry and thin film transistor and color filter arrays comprising:
       1. coating first layer of resist material on a substrate; and   2. the substrate comprises a top layer of material to be patterned.   3. creating a pattern on the substrate material by image wise radiation induced thermal removal of the first resist material.   4. removing the substrate material to be patterned by means of an etch process, and   5. removing resist from the regions not exposed in step 2 revealing a micropattern of the substrate material.       
 
         [0024]    In a further embodiment, the resist and optionally the material to be patterned is provided with a light to heat conversion substance that absorbs strongly at the predominant wavelength of the image wise radiation source, whereby the radiation source is a laser that emits light at wavelengths greater than 525 nm, and preferably in the far infrared at wavelengths between 750 and 1100 nm. Some embodiments of this invention provide for applying the resist layer in a vacuum or from a vapor source, and this in combination with all dry etch processes, enables an entirely dry method for patterning a material on a substance. 
         [0025]    Therefore, the deficiencies of the current methods of creating micro structures and microelectronic devices are corrected by the elements of this invention, by providing a method that is maskless, can be completely dry and free from all or most of the chemical processing steps, and includes the use of a less expensive and more versatile class of lasers, the solid state IR diode lasers. 
     
     
       BRIEF DESCRIPTION OF THE DRAWINGS 
         [0026]    While the specification concludes with claims particularly pointing out and distinctly claiming the subject matter of the present invention, it is believed that the invention will be better understood from the following description when taken in conjunction with the accompanying drawings, wherein: 
           [0027]      FIG. 1  is a block diagram showing a patterning apparatus for applying a thermoresist pattern according to the present invention; 
           [0028]      FIG. 2  is a substrate that will be used to carry a patterned layer; 
           [0029]      FIG. 3  is a cross-sectional side view, not to scale, of  FIG. 2 ; 
           [0030]      FIG. 4  is block diagram showing a material, which is uniformly deposited that will be patterned on a substrate; 
           [0031]      FIG. 5  is a cross-sectional side view, not to scale, of  FIG. 4 ; 
           [0032]      FIG. 6  shows a resist material, which is uniformly deposited; 
           [0033]      FIG. 7  is a cross-sectional side view, not to scale, of  FIG. 6 ; 
           [0034]      FIG. 8  is a block diagram showing a pattern in the resist, which exposes the non-patterned material below; 
           [0035]      FIG. 9  is a cross-sectional side view, not to scale, of  FIG. 8 ; 
           [0036]      FIG. 10  is a block diagram showing the material etched away exposing the substrate below, while the resist remains unetched; 
           [0037]      FIG. 11  is a cross-sectional side view, not to scale, of  FIG. 10 ; 
           [0038]      FIG. 12  is a block diagram the patterned material exposed after the removal of the resist; 
           [0039]      FIG. 13  is a cross-sectional side view, not to scale, of  FIG. 12 ; 
           [0040]      FIG. 14  is a cross-sectional side view, not to scale, of the resist on a substrate or material to be patterned, that shows incomplete cleanout; and 
           [0041]      FIG. 15  is a cross-sectional side view, not to scale, of  FIG. 14  after a descumming etch. 
       
    
    
     DETAILED DESCRIPTION OF THE INVENTION 
       [0042]    The present invention will be directed in particular to elements forming part of, or in cooperation more directly with the apparatus in accordance with the present invention. It is to be understood that elements not specifically shown or described may take various forms well known to those skilled in the art. 
         [0043]    A material to be patterned, represented by layer  11  in  FIGS. 4 and 5 , affixed to substrate  10  ( FIGS. 2 and 3 ), is coated with a resist layer  12  as in  FIGS. 6 and 7  by any of several methods practiced in the microfabrication industry, including but not limited to spin coating, spray coating, hopper coating, meyer rod coating, gravure coating, inkjet coating, dip coating, supercritical CO2, vapor deposition and plasma vacuum deposition. The resist layer  12  may also be partially patterned by any of the above mentioned coating methods. 
         [0044]    A pattern of intelligence is formed in resist layer  12  by thermally induced ablative removal of the resist material by a source of imagewise heat. Preferably, the imagewise heat is provided by a modulated laser beam or an array of such beams. A schematic representation of such a laser patterning device is shown in  FIG. 1 . 
         [0045]    Referring now to  FIG. 1  there is shown a patterning apparatus hereinafter referred to as laser system  1 , for ablating resist layer  12  from a substrate layer  11  to be patterned on a support substrate  10  in accordance with the ablative pattern of intelligence formation of the present invention. Laser  14  of the patterning apparatus can be a diode laser or any other high power laser that produces laser beam  26  with a preferred wavelength between 750 and 1100 nm, and preferably between 805 and 840 nm. More than one laser  14  or laser beam  26  can be used simultaneously in this invention. In order to scan laser beam  26  to provide relative movement between laser beam  26  and resist layer  12 , a galvanometer  22  that includes a moveable mirror scans the beam through an f-theta lens  24  to form a scan line in direction X. Those skilled in the art will understand that scanning the laser beam can also be accomplished by other kinds of moveable reflective surfaces, such as rotating polygons with mirror faces, or by other devices such as rotating diffraction gratings. Alternately, the needed relative movement could be provided by moving substrate  10  relative to laser beam  26 . 
         [0046]    In the embodiment shown in  FIG. 1 , substrate assembly  10 ,  11 ,  12  is transported in a direction Y, which is orthogonal to the scan line, by a translation stage allowing the full area to be scanned. In the preferred embodiment, the substrate to be patterned is oriented with the resist side facing the laser source, with either a coversheet provided to collect the ablated debris, or a vacuum collection device affixed to remove said debris. Alternatively, use of transparent substrates  10  and a substrate layer  11  would allow the substrate to be placed with the resist side facing away from the laser source and with the ablated material directed to either a flexible undersheet or a vacuum channel. The supporting substrate can be either rigid or flexible. 
         [0047]    The intensity of laser beam  26  at any point in the scan is controlled by the laser power control line  30  using instructions from a control logic processor  28 . Alternatively, the intensity of laser beam  26  can be controlled by a separate modulator such as an acousto-optic modulator (not shown), as is well known by those skilled in the art of laser optics. In an alternative embodiment, substrate assembly  10 ,  11 ,  12  can remain stationary and the laser writing apparatus made to move or laser beam  26  redirected optically. The important feature is that there is relative movement between laser beam  26  and substrate assembly  10 ,  11 ,  12  in order to allow full area scanning. The laser beam power of Laser System I varied from 0 to about 700 milliwatts, with a scan frequency from between 100 to 1 Hz corresponding to dwell times of between about 6 and about 900 microseconds and exposures between about 230 and about 34,000 mJ/cm2. The scan parameters are chosen to optimize the exposure above the resist layer ablation threshold, and below excessive exposure that will create overly wide lines and spots and cause damage to the underlying substances. 
         [0048]    In the preferred embodiment, referred hereinafter as Laser System II consisting of a non-coherent infrared diode laser bar at 808 nm (±10 nm) whose beam is divided into  256  separate addressable channels modulated by a spatial light modulator at  5  micron intervals across the beam&#39;s width, as described in U.S. Patent Application Publication No. 2005/0266172 (Kay et al.), which is incorporated by reference. The beam intensity distribution in the fast scan direction is a Gaussian whose 1/e2 diameter value is 3.6 micrometers. Peak to peak distance in the fast scan direction was limited by the modulation scheme to 5 microns for the examples of this invention yielding a minimum ablated spot at the film plane of about 5 microns maximum representing 1 pixel in any image rendition. The beam was scanned across the sample by a two axis movable stage that held the sample. Exposure occurred as the fast scan axis movable stage ran at speeds between 1.0 and 0.1 meter per second. The powers available on laser system II were between 11 and 55 milliwatts per channel corresponding to a total exposure range of between 0.22 and 11 J/cm2, although the powers and exposures useful for this invention are not limited to these ranges. The slow scan axis movable stage increments the sample a set distance in preparation for another fast scan motion. This sequence continues until the total desired area is exposed. 
         [0049]    The substrate was held against the stage by a vacuum, although those skilled in the art will recognize that many other means exist for affixing the substrate to the stage, for example by clamping, application of pressure, adhesives, with optional heating of the substrate or the like, and including means for accurate placement and registration of the substrate with respect to the ablative pattern. One example of a fixture for this positioning is disclosed in commonly-assigned U.S. Pat. No. 6,695,029 (Phillips et al.) The movable stage can support a substrate oriented either with the resist side face towards the laser source, or away from the laser source when working with transparent substrates  10  and substrate layers  11 . When facing the laser source, the ablation debris can be collected either on a coversheet, or preferably, in a vacuum collection device affixed to the laser head. The pattern information was provided by means of a CPU and a RIP capable of processing test patterns or Tif images wherein 1 pixel was assigned a pattern dimension of 5×5 microns. 
         [0050]    Any infrared or visible YAG laser system could be used in conjunction with the resist layer  12  of this invention, which is not limited to the Laser Systems I and II descried above. The array of lasers could be an assembly of discreet diodes as in the Kodak Approval Digital Proofing System, or bar laser with a segmented light modulator as in the Kodak Newsetter or the Creo Trendsetter Plate Writer-Proofers. The device for transporting the substrate  10  could be a flatbed for rigid substrates and relative motion could be provided by moving either the laser array or the support stage. Drum systems utilizing flexible supports could also be considered, as well as laser arrays mounted in the suitable proximity for a moving web of substrate  10 . There is no limitation to the number of addressable channels or lasers comprising the array, other than the practical limits of the devices themselves, and the ability or the CPU to deliver the information at the appropriate rate. More than one head could be employed simultaneously. 
         [0051]    Modulation of the laser power on the plane of resist layer  12  to produce the desired ablative pattern could be accomplished by any means known if the art, such as binary exposure in the on or off mode as practiced in laser systems I and II of this invention, or by pulse width modulation. The only requirement is that the power in the on mode be sufficient to cause ablation at the scan speed chosen. 
         [0052]    The imagewise radiation supplied to resist layer  12  and substrate layer  11  could also be from any non-laser source such as a Xenon flash through a mask, or any other radiation source with a high enough intensity at the absorptive wavelengths of the light to heat converting substance to cause thermally induced ablation. 
       Light to Heat Converting Substance 
       [0053]    The resist layer  12  or the substrate layer  11  to be patterned, or a combination of layers  12  and  11  of this invention must absorb a portion of the incident radiation by means of a light to heat converting substance in order to generate the heat required to exceed the ablation threshold given the light sources of IR lasers emit at wavelengths that are not capable of breaking bonds. The layers are thereby provided with radiation absorbing materials such dyes, pigments, carbon, or metals. The preferred heat substances absorb radiation in the near infrared between 750 and 1100 nm, and preferably between 800 and 840 nm. In addition, dyes that absorb in the visible spectrum over 525 nm in conjunction with YAG lasers could also be useful in this invention. 
         [0054]    The preferred IR absorbing dyes of this invention are specified in commonly-assigned U.S. Pat. No. 4,973,572 (DeBoer) and U.S. Pat. No. 5,578,416 (Tutt), or described in “Infrared Absorbing Dyes” (ed. Masaru Matsuoka, Plenum Press, 1990). Dye types useful for this invention include, but are not limited to, Cyanines, Squaryliums, Croconiums, Pyryliums, Quinones, Phthalocyanines and their metal complexes, Naphthalocyanines and their metal complexes, azo dyes, and intermolecular charge transfer complexes. Those skilled in the art will recognize that the radiation absorbing chromophores or this invention can be presented to the resist layer  12  as either monomolecular dyes or as pigment particles depending on the particular properties of the absorber, which may also include a carbon black, a metal nanoparticle, or a carbon nanotube. Other radiation absorbers useful for this invention in resist layer  12  are metals or inorganic materials such as chromium, nickel, titanium, molybdenum, tungsten, zirconium, alloys such as NiCr, MoCr, WTi, and the like, oxygen deficient oxides of metals such as aluminum or chromium oxides and the like, or a layered stack of materials that absorb radiation by virtue of their antireflection properties. The main criteria is that radiation-absorbing substance absorb laser light at the given wavelength of the imagewise radiation, at a high enough extinction for ablation of material from resist layer  12 . The efficiency of this transfer is well known to depend on the laser fluence, spot size, beam overlap and other factors. Generally, the optical density of radiation-absorbing material as presented in the substrate-resist stack  10 ,  11 ,  12  should be at least 0.1 (20% of the light is absorbed). 
         [0055]    The radiation absorbers of this invention may be present in the resist layer  12  as a monomolecular species dissolved in the organic binder of the resist layer  12 , or as a separate layer within the confines of resist layer  12 , or as multiple layers with intervening binders layers. In addition, the radiation absorbing substance can be presented as a top layer of the substrate layer  11  to be patterned, such as a vacuum deposited dye or metal, or the substrate layer  11  to be patterned can be a completely radiation absorbing but non-ablating layer. Useful radiation absorbing and top-layer metals for substrate layer  11  include, but are not limited to, Mo, Ni, Ti, Zr, W, Cr, and the like. Such second metal top-layers are common in the microelectronics industry when placed over aluminum for the prevention of hillock defects and as diffusion barriers. The radiation absorbing material when included in the substrate layer  11  to be patterned can also reside in a sub layer. It is a particularly beneficial and preferred embodiment of this invention, for the cleanest and most efficient ablative pattern evacuations of resist layer  12 , to place a radiation absorbing material such as one of the aforementioned metals as the uppermost layer of material  11 , directly adjacent to resist layer  12 , wherein layer  12  also includes a radiation absorbing substance such as a dye. 
         [0056]    The radiation absorbing substances of this invention can be applied to the resist layer  12  or the material to be patterned  11 , in a variety of methods known in the art, such as but not limited to, spin coating, spray coating, hopper coating, gravure coating, ink jet deposition, supercritical CO 2 , and the like, from a solution that may or may not include the binder material. Other methods of application include vacuum or vapor deposition. 
       Binder 
       [0057]    For the purpose of this invention, the binder of resist layer  12  comprises at least a polymeric binder, or a monomeric glass, or a mixture thereof, and preferably also may include an additional gas-producing substance. It is further preferred that the polymeric binder be comprised either wholly or partially of a polymer that is thermally labile or prone to depolymerization at temperatures under 400° C. in order to enhance the efficiency and cleanliness of the ablative pattern. 
         [0058]    The term “ablative removal” is broadly understood to be a heat-induced mass ejection of resist layer  12  from substrate layer  11 , wherein at least a portion of a component of the resist is converted to a gaseous state. The material that is converted to gaseous state may be the resist material itself or may be some other component material of the resist layer  12  that thus serves as a propellant for ablative ejection. Ablative removal also includes fragmentation or particulate ejection, in which at least some portion of the donor material may not actually be converted to gaseous state, but is effectively fragmented and propelled by the conversion to vapor form of some heated component of the donor. It is therefore preferred that the resist layer comprises as much as possible, thermally labile materials as long as the resist withstands the subsequent etching process that forms the final pattern in substrate layer  11 . 
         [0059]    To this end, a preferred class of polymer binders can be defined as polymers derived from a monomer CH═CXY, where X and Y independently are electronegative or resonance stabilized groups, and are further specified as the X and Y are among the groups: Halogen (when X is not equal to Y), —CN , —(C═O)OR, —(C═O)R, —(C═O)NR2, where R can independently be H, any alkyl, cycloalkyl or cycloalkenyl, aryl, —(OCH2CH2) z CH3, —(OCH(CH3)CH2) z CH3, or any substituted alkyl or alkoxide group wherein at least one hydrogen atom is replaced with a halogen, silicon, or titanium atom. Mixtures of the above described polymers can also be included in resist layer  12 . 
         [0060]    Especially useful among polymers under this definition are the alkyl cyanoacrylate polymers wherein X is —CN and Y is (C═O)OR and the R group is methyl, ethyl or a copolymer thereof. Polymers of this type are known to be useful as resins that are efficiently ablated as shown in the following: U.S. Pat. No. 5,468,591 (Pearce et al.); U.S. Pat. No. 5,858,607 (Burberry et al.); and U.S. Pat. No. 6,165,671 (Weidner et al.). Cyanoacrylates have also been cited as useful as electron beam resists by Helbert et al.; Radiation Degradation of α-Substituted Acrylate Polymers and Copolymers; Journal of Applied Polymer Science, Vol. 21, 1977, pp. 797-807, and as a photoablative resist for high-energy UV radiation by Hogan et al.; Laser Photoablation of Spin-on-Glass and Poly(Ethyl Cyanoacrylate) Photoresist; Applied Surface Science 36, 1989, pp. 343-349. 
         [0061]    It is anticipated that the physical properties of the cyanoacrylate polymers may need to be modified, particularly to provide improved adhesion to substrate layer  11 , and etch resistance to the etchant for substrate layer  11 . Such improvements have been applied to their uses as electron beam resists, and include modifying the alkyl groups of the cyanacrylate esters, for example to produce a 3-trimethylsilylpropyl 2-cyanoacrylate as taught in U.S. Pat. No. 5,359,101 (Woods et al.) A widely practiced method for modifying polymer properties of this class involve copolymerization with a wide variety of vinyl monomers to improve etch resistance adhesion, and molecular weight stability, as in EP Patent No. 0343603, U.S. Pat. No. 4,686,168 (Fujii et al.), and JP Patent No. 7-056341. Useful compositions include cyanoacyrlate copolymers with acrylates, methacrylates, fluoroacrylates and fluoromethacrylates, vinyl esters, vinyl ethers, vinyl ketones, styrene, a-methylstyrene, butadiene, isoprene, methacrylamides, acrylamides, acrylonitrile, and methacrylonitrile, and mixtures thereof. In addition, comonomers such as vinyl cinnamate comprising radiation or chemically crosslinkable groups might be included in order to improve etch resistance after the initial ablative patterning of resist layer  12 . 
         [0062]    Cyanoacrylate polymers are known to exhibit molecular weight instability when dissolved in various solvents (Woods et al.; Vapour deposition of poly(alkyl-2-cyanoacrylate) resist coatings: a new electron-beam/deep-ultra-violet photoresist technology; Polymer 1989, Vol. 30, pp. 1091-1098) in that they will equilibrate to a lower molecular weight from a higher molecular weight. In most cases as practiced in this invention, a useful degree of polymerization is almost always maintained, and usually does not degrade to less than 10,000 (Wt average), and typically resides at about 30,000 in solution. This behavior is particularly troublesome for electron beam or X-ray lithography that depends on well defined and consistent solution behavior in order to control the development step. For the purposes of this invention, however, no favored molecular weight is specified as long as a practical ablation threshold energy is provided, and the resist withstands the etching chemistry used for the final pattern of substrate layer  11 . Those knowledgeable in the art will recognize that while ablation efficiency is most likely favored by low molecular weights, other physical and chemical properties such as etch resistance might be favored by higher molecular weights, and that a balance much be struck depending on the demands of the substrate layer  11  and processes used. 
         [0063]    Resist layers  12  comprising polycyanoacrylates and their copolymers can be applied to the substrate layer  11  by any means of coating or deposition practiced in the art, and a particular useful method consists of vapor deposition as taught by in U.S. Pat. No. 4,675,273 (Woods et al.). Such a vapor deposition process offers the possibility of an entirely dry process when combined with a dry plasma etching step for the final pattern formation in  11 . Combination of the vapor deposited cyanoacrylate with a radiation absorbing species such as a dye or a metal could be accomplished by an alternating deposition of separate cyanoacrylate and dye (metal) layers. Those practiced in the art will recognize that a radiation absorbing element adjacent to a thermally labile polymer will impart enough thermal energy to the polymer to effect ablation. 
         [0064]    Other thermally labile and otherwise useful polymers comprising the binder of resist layer  12  include nitrocellulose, copolymers of maleic anhydride including methylvinylether maleic anhydride and styrene maleic anhydride, an alpha-substituted aliphatic polycarbonate, polyketones, polyalkenesufones, alpha-methyl styrene, and a silicone, and their mixtures with polymers of the general structure CH═CXY where X and Y are independently electronegative and resonance stabilized groups. 
         [0065]    The polymeric binders of resist layer  12 , alone or in combination with polymers already cited, may include polymers known to provide resist properties in lithographic processes, such as Shipley G-Line or Microposit™ photoresists from Shipley Company, Marlborough, Mass., and including materials such as polymethacrylates and acrylates, polystyrene and copolymers with butadiene, acrylates and methacrylates, acrylonitrile, polyesters, polyamides, polyimides, polyvinylchlorides and copolymers with vinyl acetate, poly vinyl esters, polyurethanes, polyvinyl acetals and butyrals, epoxides, polyimides, Novolac resins, polyvinyl phenol resins, and the like. Another useful resin that could be employed is this invention include a resin derived from divinylsiloxane bis(benzocyclobutene) (Cyclotene Resins, Dow Chemical). 
         [0066]    Polymeric resins formed in vacuum deposition processes might also be considered as useful binders for the resist layer  12 , as for example, poly p-xylene derived from pyrolyzed [2.2] paracyclophane, (Trade name is Parylene, Union Carbide), and resins formed by glow discharge plasma polymerization such as poly alkenes and poly fluoroalkanes. Such vacuum deposited resins might be co-deposited with radiation absorbing materials such as dyes and metals, or applied in separate layers in the confines of resist layer  12 . 
         [0067]    In addition to polymeric materials, useful binder elements for resist layer  12  include monomeric glasses, defined in U.S. Pat. No. 5,891,602 (Neuman) as a non-polymeric organic material with a glassy state having a glass transition temperature of greater than 25 deg C., capable of forming an amorphous glass in said resist layer, and including the materials claimed and specified therein. Additionally useful monomeric and oligomeric glasses are specified in copending, commonly-assigned U.S. patent application Ser. No. 11/240,964 and include resins as described in previously cited U.S. Pat. No. 6,165,671, such as hydrogenated and partially hydrogenated rosin esters and similar rosin esters. Commercially available materials include the glycerol ester of hydrogenated wood rosin, such as Staybellite Ester  10  (Hercules), the glycerol ester of hydrogenated rosin, such as Foral 85 (Hercules) and the pentaerythritol ester of modified rosin, such as Pentalyn 344 (Hercules). The amorphous organic solids of resist layer  12  may also be oligomeric resins with a molecular weight of less than about 4000 such as the polyester Tone 260. 
         [0068]    The monomeric glasses add organic bulk without adding unnecessary covalent bonds and represent chemical species more likely to be volatilized by the ablation than many typical resins. 
         [0069]    Resist layer  12  may also be partially comprised of monomeric or oligomeric materials capable of release a gas when subject to the elevated temperature of the ablated regions and will thus assist in the mass ejection of material from said ablated pattern. Such materials include tetrazoles and triazoles and their amino derivatives as for example 3-amino tetrazole, sodium azide, used as an automotive air bag propellant, azo compounds such as azo-bis-isobutyrylnitrile, azido-oxetane polymers and oligomers such as “poly-bamo,” and the like. 
         [0070]    Any of the layers of resist layer  12  may include, in addition to the materials already disclosed, surface active agents necessary as coating aids and used for the modification of surface properties, hardeners, adhesion promoting agents, and the like, necessary for the physical integrity during the process steps. Visible dyes absorbing at wavelengths other than the imagewise radiation may also be added to any of the layers of resist  12  to provide process visualization. 
         [0071]    The resist layer  12  can be from 0.10 to 10 microns thick, and preferably is between 0.25 to 2.5 microns. 
         [0072]    Immediately following the thermally induced imagewise ablative pattern formation, a small amount of residual organic material may be remaining at the bottom of an ablated region as depicted by item  13  in  FIG. 14 . This residual layer may be residual resin or other organic thermal decomposition products, and may need to be removed before the final etch process that will be applied to substrate layer  11 . This material can be easily removed by any number of de-scumming operations used in conventional lithography including oxygen plasma, either in a vacuum or at atmospheric pressure. Such operations are typically done at short times and low powers so as to not remove significant amounts of resist in non-ablated areas, but sufficient to clean the intended ablated region.  FIGS. 8 and 9  show the patterned resist after cleaning with the exposed substrate layer  11  ready to be etched. In addition, the oxygen cleaning step may also provide a steeper wall profile in the resist layer  12 .  FIG. 15  shows a side view of an ablated line done by a laser after a pre-etch oxygen etch was done. The sides of the ablated layer are normal to substrate  10  and the bottom of the ablated region is cleaned of any residual resist. 
         [0073]    Examples of substrate layer  11  that could be patterned are all etchable metals or conductors, semiconductors, dielectrics and polymers. Some metals or conductors commonly used with these resists are Al, Mo, MoCr, Ni, NiCr, Cr, W, WTi, Ti, Zr, Ag, Cu, Au, Pt, Pd, tin, ITO, and polythiophene, etc. Semiconductors commonly used are poly silicon, amorphous silicon, doped silicon, zinc oxide, germanium, gallium arsenide, indium phosphide, mercury cadmium telluride, etc. Some commonly used dielectrics used are SiNx, SiO2, Al2O3, etc. Some commonly used polymeric dielectrics are Polymethylmethacrylate, polyphenols, polyimides etc. 
         [0074]    Other functional microstructures of layer  11  that can be patterned by the process of this invention include circuitry for printed circuit boards, interconnects, and microsprings used in flip-chips made from a MoCr alloy. 
         [0075]    The substrate layer  11  to be patterned can be a single material or a plurality of layers. All layers however will be affected in the process. Layers not affected are considered to be in the substrate  10 . The areas of the substrate layer  11  not covered by the resist layer  12  are thus exposed to the etching action of the chemical or plasma etchant. It is assumed that the profile of the edges of resist layer  12  are normal to the substrate but they may be sloped if the process requires it.  FIG. 9  is the side view of  FIG. 8  which depict the device after ablation of resist layer  12  and cleaning of residual organics.  FIG. 10 and 11  show the final patterned device with substrate  10  now exposed where substrate layer  11  was exposed in  FIG. 8 , and with the non-ablated resist layer  12  still on top of substrate layer  11 . 
         [0076]    Substrate layer  11  can be etched by use of a chemical or plasma etch process. The etch process used can be done in vacuum by plasma with a reactive ion etch, with a plasma torch or with wet etches. Examples of etch gases used for plasma etching include Cl 2 , BCl 3 , SF 6 , O 2 , H 2 , CH 4 , chloroform and N 2 . Exemplary wet etches include HCl, nitric acid, acidic acid, phosphoric acid, ferric nitrate. The resist layer maybe effected by the etch process but not to the point at which it compromises the quality of the pattern in substrate layer  11 .  FIG. 11  is the side view of  FIG. 10  which show the pattern after etching and before the final resist removal. 
         [0077]    The remaining resist on substrate layer  11  in the final pattern can be removed by any method commonly practiced in the conventional lithography processes including but not limited to high power O2 plasma, solvent washing, high pressure water jets, and high temperature baking.  FIGS. 12 and 13  show the final pattern of substrate layer  11  now exposed in the areas which were protected in  FIG. 8 . The resist removal step is optional. Depending on the process and the resist, said resist could be left in place, particularly if a secondary pattern is to be make in substrate layer  11  that is inside the confines of the original pattern of substrate layer  11 . 
         [0078]    The substrate  10  could be any material used as a carrier for substrate layer  11 , including glass, a silicon wafer, a metal such as stainless steel, a printed circuit board, and the like. Flexible supports could be used as well, including polyethylene terephthalate, polyethylene, polypropylene, polyethylene napthalate, polysulphone, polyimides, and the like. Alternatively, the substrate  10  can be any preliminary substructure of a final device, which may include functional layers, registration marks for alignment, as for example the various layers of a thin film transistor array backplane for LCDs or OLED displays. 
       Example I 
       [0079]    On a 1.1 mm glass substrate with between 500 and 1000 Angstroms of sputtered aluminum, a laser ablative resist layer was applied by spin coating a solution of 5 wt % Poly(methyl-co-ethyl)cyanoacrylate, 1.0 wt % IR dye (1), 0.5 wt % Cyan Dye (1), 0.05% Fluorcarbon surfactant FC-431 (3M Corp) in 50/50 Acetonitrile/Cyclopentaone at 1000 RPM resulting in a dry thickness of about 0.33 microns. 
         [0080]    Portions of the ablative resist layer were removed in a pattern of intelligence by Laser System I consisting of a single infrared laser beam at 830 nm. The beam size was approximately 16 micrometers by 80 micrometers to the 1/e 2  point scanning along the wide beam direction. Relative movement between the laser beam and the resist and aluminum coated substrate was provided by a galvanometer that included a moveable mirror that scans the beam through an f-theta lens to form a scan line in wide beam direction. The dwell time was 0.9 milliseconds [Scan frequency was 10 Hz with a power setting of 170] with a suitable power density. Removal of the resist layer was effected in the interstitial regions of a grid pattern wherein the non-ablated areas conformed to the grid lines of aluminum which were to be remaining after etching. 
         [0081]    After laser etching of the resist layer, the sample was placed in a Lam model 4600 chlorine based plasma etch tool, product of Lam Research Corporation, Fremont, Calif. The pattern was etched into the metal layer by removal of the aluminum in the laser ablated regions. The sample was then placed in an oxygen plasma Asher and the remaining laser ablative resist material removed. This process transferred the laser resist pattern into the aluminum. Removal of the resist resulted in an aluminum grid pattern with high fidelity with a completely dry patterning process. 
       EXAMPLE II 
       [0082]    On a 1.1 mm glass substrate with about 1000 Angstroms of sputtered aluminum, a laser ablative resist layer was applied by spin coating a solution of 7.5 wt % Poly(methyl-co-ethyl)cyanoacrylate, 1.0 wt % IR dye (1), 0.5 wt % Cyan Dye (1), 0.05% Fluorcarbon surfactant FC-431 (3M Corp) in 50/50 Acetonitrile/Cyclopentaone at 4000 RPM resulting in a dry thickness of about 0.33 microns. 
         [0083]    Portions of the ablative resist layer were removed in a pattern of intelligence by Laser System II consisting of a non-coherent infrared diode laser beam at 808 nm whose beam is divided into 256 separate addressable channels modulated by a spatial light modulator at 5 micron intervals across the beam&#39;s width. The beam was scanned across the sample by a movable stage that held the sample at speeds between 1.0 and 0.1 meter per second. For the purpose of this example, 32 of the 256 available channels were activated. Power densities used were between 11 and 38 milliwatts per channel. Removal of the resist layer was effected in the illuminated regions in patterns of 5 micron lines in parallel and perpendicular to the direction of beam scanning. 
         [0084]    After patterning, the sample was subjected to an oxygen plasma at 50 watts and 300 millitorr for 40 to 80 seconds in order to remove traces of organic material remaining in the ablated regions. This treatment did not substantially reduce the thickness of the resist in the non-ablated regions, nor mitigate its effectiveness as a resist to the etching step. 
         [0085]    A liquid etch was then applied to the sample of example II in order to remove the aluminum in the ablated regions. The etch bath consisted of 25 parts H 2 PO 3 , 1 part HNO 3 , and 5 parts glacial acetic acid for 3 minutes and 15 seconds followed by two rinse baths of distilled water. The resist in the non-ablated regions was removed in an acetone bath resulting in an aluminum line pattern with high fidelity to the non-ablated regions. 
       EXAMPLE III 
       [0086]    A glass substrate was coated in ascending order, with 50 nm Chromium, 300 nm Silicon Nitride, 200 nm amorphous silicon, and 50 nm n-doped amorphous silicon by the PECVD process. To this substrate, a laser ablative resist layer was applied by spin coating a solution of 10 wt % Poly(methyl-co-ethyl)cyanoacrylate, 1.0 wt % IR dye (1), 0.5 wt % Cyan Dye (1), 0.05% Fluorcarbon surfactant FC-431 (3M Corp) in 50/50 Acetonitrile/Cyclopentanone at 1000 RPM resulting in a dry thickness of about 1.0 microns. 
         [0087]    Portions of the ablative resist layer were removed in a pattern of intelligence by Laser System II consisting of a grid of 10 micron ablated lines in the both the vertical and horizontal directions separated by 100 microns. After oxygen plasma treatment as described in Example II to remove any residual resist in the ablated regions, the substrate was treated with an SF6 plasma for 2.5 min to remove the silicon and silicon nitride layers from the ablated regions. The remaining resist was then removed by an O2 plasma at 300 mTorr and 400 watts for 5 minutes. The resulting pattern was a grid array of isolated silicon nitride/a-silicon/n+ silicon blocks, 100 microns on each side separated by 6-10 micron gaps with very sharp and well defined edges. 
         [0088]    The invention has been described in detail with particular reference to certain preferred embodiments thereof, but it will be understood that variations and modifications can be effected within the scope of the invention. 
       Parts List 
       [0000]    
       
           10  substrate 
           12  resist layer 
           11  substrate layer 
           13  residue 
           14  laser 
           22  galvanometer 
           24  lens 
           26  laser beam 
           28  control logic processor 
           30  control line