Abstract:
A lithium non-aqueous secondary electrochemical cell is disclosed having an ester-based organic electrolyte solution and a cathode active material comprising Li x  CoO 2 , (0&lt;×≦1).

Description:
BACKGROUND OF THE INVENTION 
     The invention herein described was made in the course of or under a contract or subcontract thereunder with the Department of the Navy. 
    
    
     1. Field of the Invention 
     The present invention relates generally to the field of high energy non-aqueous electrochemical cells and, more particularly, to an active cathode material and electrolyte solution that, when in combination, can offer significant advantages for both primary and rechargeable cell applications. 
     2. Description of the Prior Art 
     Secondary or rechargeable active metal cells typically consist of a light, strongly reducing anode, normally an alkali metal such as lithium, an aprotic, non-aqueous solvent into which an appropriate quantity of a salt of the anode metal has been dissolved to form a conductive solution, and an oxidizing agent as the cathode material. While these cells have been shown to exhibit good cycle life capabilities, many of the prior art active cathode materials, such as MoS 2  and TiS 2 , are low voltage, low energy density materials. In addition, most of the prior art electrolyte solutions, generally selected o their ability to efficiently recharge the anode, exhibit low conductivities and thus severely limit cell performance with respect to rate capabilities and low temperature operation. 
     One prior art development related to high energy density active cathode materials is the lithium intercalated compound Li xCoO   2 . This compound is disclosed in U.S. Pat. No. 4,497,726, 1985 and further discussed in K. Mizushima, P. C. Jones, P. J. Wiseman, and J. B. Goodenough, &#34;Li x  CoO 2  (0&lt;×&lt;1): A New Cathode Material For Batteries of High Energy Density,&#34; Mat. Res. Bull., Vol. 15, 783(1980). This material offers outstanding performance capabilities, including good reversibility, but has not been used in cells because of the lack of a suitable electrolyte solution. The high oxidizing potentials required to charge Li x  CoO 2  decompose most conventional electrolyte solutions; and, since the material is manufactured in the discharged state and thus must be charged prior to use, this has prevented its application even in primary cells. The few prior electrolyte solutions that have been found to be compatible with Li x  CoO 2 , such as LiAsF 6  /sulfolane and LiAsF 6  /methyl sulfolane, offer very low conductivities and are thus unsuitable for most cell applications. 
     Thus, there has remained a need for improvement in secondary active metal cells with respect to increasing energy density, rate capabilities, and low temperature performance. 
     SUMMARY OF THE INVENTION 
     The present invention involves a high energy lithium electrochemical system that can offer significant advantages over prior art rechargeable technologies. The advantages in energy density are illustrated in Table I which compares the theoretical energy densities of several known cathode materials, including that of the present invention. This system is also very attractive for primary cell applications. 
     The proposed electrochemical system consists of a lithium metal anode, and an active cathode material of Li x  CoO 2  (0&lt;×≦l.0) in combination a high conductivity ester-based electrolyte solution. Preferred solutions include those in which the ester solvent is selected form methyl formate (HCOOCH 3 ), methyl acetate (CH 3  COOCH 3 ) and the like. Electrolyte salts include LiAsF 6 , LiBF 4  (or combinations thereof), LiClO 4 , LiAlCl 4 , LiGaCl 4 , and so on. 
     The cells of the present invention operate at or near 4.0 volts and offer theoretical energy densities in excess of 1000 Wh/Kg, over twice that yielded by TiS 2  or MoS 2 . When combined with ester-based electrolyte solutions, the system of the present invention can operate at moderate to high discharge rates over a wide range of temperatures. In addition to high conductivities, ester-based solutions offer electrochemical stability superior to that of other non-aqueous solutions typically used in lithium cells and so are able to withstand the high potentials required to charge Li x  CoO 2  cells. Through combinations using the unique properties of ester-based solutions, therefore, LixCoO 2  becomes a viable cathode material for high energy density lithium cells in both primary and secondary applications. 
    
    
     BRIEF DESCRIPTION OF THE DRAWINGS 
     In the drawings: 
     FIG. 1 illustrates the discharge performance of Li/Li x  CoO 2  laboratory cells at three different discharge rates at 25° C.; and 
     FIG. 2 graphically illustrates the delivered discharge capacity of a rechargeable Li/Li x  CoO 2  cell versus cycle number. 
    
    
     DESCRIPTION OF THE PREFERRED EMBODIMENTS 
     The present invention takes advantage of the unusually high energy density of Li x  CoO 2  cathode material by combining it with an electrolyte solution which can withstand the high operating potentials characteristic of this system, particularly during charging. It should be noted, however, that charging is a concern even for primary cell applications because Li x  CoO 2  is manufactured in the discharged state and all cells must therefore be charged before use. 
     The present invention describes an electrochemical system consisting of a lithium metal anode, a cathode having Li x  CoO 2  as the active cathode material, and an ester-based electrolyte solution. 
     This system offers superior capabilities over existing systems based on Li x  CoO 2  primarily due to the unique properties of ester-based electrolyte solutions. These solutions offer not only the excellent electrochemical stabilities needed to withstand the high oxidizing potentials present at Li x  CoO 2  cathodes but also possess high conductivities that can allow Li/Li x  CoO 2  cells to operate at high rates of discharge and at low temperatures. Hence, by combining Li x  CoO 2  with the unique and outstanding properties of ester-based electrolyte solutions, an electrochemical system is obtained that offers high energy density, reversibility, and good rate capabilities and which is thus suitable for a wide range of applications. 
     To demonstrate the performance of the system of the present invention, tests were conducted with laboratory cells constructed as follows: 
     The Li x  CoO 2  (x=1.0) was a commercial grade of material purchased from Morton Thiokol, Inc., Alfa Products (Catalog No. 13998). Cathodes consisted of 85 weight percent Li x  CoO 2 , 10 weight percent of Vulcan XC-72R, trademark of Cabot Corporation of Boston, Mass., carbon as the conductive diluent, and 5 weight percent of Teflon powder (polytetrafluoroethylene) as the binder. The individual components were suspended in mineral spirits solvent and then mixed in a high speed blender. Electrodes were fabricated using a roll milling technique. The resulting cathodes were first air dried and then dried at 200° C. under vacuum. Laboratory cells were constructed using a lithium anode and a cathode separated by two or more layers of microporous polyethylene or polypropylene separator material. Each electrode had a geometric surface area of 3.2 cm 2 . The anode consisted of lithium foil pressed onto a nickel expanded metal grid. The cathode employed an aluminum grid as the current collector and the cell assembly was supported between two glass plates. The cell was placed into a sealed vessel containing approximately 2 ml of a 2M LiAsF 6  +0.4M LiBF 4  /methyl formate electrolyte solution. The ends of the separator extended down into the electrolyte solution and thereby wicked the solution up into the cell stack. 
     Table I, compares theoretical values of many known cathode materials including that of the present invention. Note that the performance capabilities of the materials of the cell of the present invention show a drastic improvement over those of the prior art. 
     FIG. 1 depicts experimental results showing the excellent rate capabilities of the proposed system as evidenced by the little loss in delivered capacity or operating voltage that is observed when the discharge rate is increased from 1 mA/cm 2  to 10 mA/cm 2 . 
     FIG. 2 illustrates the rechargeable performance of Li/Li x  CoO 2  cells in limited cycle life tests. The fact that the delivered capacity remains constant as the cell is cycled demonstrates the high reversibility of this cathode material. 
     
                                           TABLE I__________________________________________________________________________INSERTION CATHODE COMPARISON OVER DEMONSTRATEDREVERSIBLE OPERATING RANGE                       Delivered          Discharge                Average                       Specific     Cycle          Cutoff                Open Circuit                       Cathode                             Energy     DOD  Voltage                Voltage,                       Capacity,                             DensityCathode Material     F/Mole          V     V      mAh/gm                             Wh/Kg__________________________________________________________________________TiS.sub.2 1.0  1.7   2.15   239   484V.sub.2 O.sub.5     1.0  2.5   3.22   147   457V.sub.6 O.sub.13     4.0  1.9   2.40   209   475Li.sub.1.05 V.sub.3 O.sub.8     2.0  1.8   2.49   186   442V.sub.2 S.sub.5     4.0  1.7   2.28   409   843MoS.sub.2 (amorphous)     1.0  1.5   1.89   167   303MoS.sub.3 (amorphous)     3.0  1.6   1.90   418   717Li.sub.x Co.sub.1.01 O.sub.2     1.0  3.9   4.24   293   1154__________________________________________________________________________