Abstract:
A surface cover having a polarized adhesive material bonded or operably connected to at least a portion of a substrate. The polarized adhesive material may be a hot melt adhesive material. The substrate may have little or no electret capabilities. The electrostatic charge of the polarized adhesive material may allow the surface cover to be removed from a mounting surface for positional adjustment during the application of the surface cover to the mounting surface. Once at its desired location, and/or aligned with the patterns, characters, or images on an adjacent surface cover, the polarized adhesive material may be activated. The adhesive force provided by the activated polarized adhesive material may provide a sufficient force for adhering surface cover along the mounting surface, thereby making the dissipation or loss of electrostatic charge inconsequential to the ability of the surface cover to remain at its desired position along the mounting surface.

Description:
RELATED APPLICATIONS 
       [0001]    This application is a continuation of application Ser. No. 12/032,373, which is a continuation-in-part of application Ser. No. 11/502,847, filed Aug. 11, 2006, which, in turn, claims the benefit of U.S. Provisional Application No. 60/707,405, filed Aug. 11, 2005. The disclosures of application Ser. Nos. 12/032,373, 11/502,847 and 60/707,405 are hereby incorporated herein by reference in their entirety. 
     
    
     BACKGROUND OF THE INVENTION 
       [0002]    Embodiments of the present invention generally relate to a surface cover that includes at least one substrate and a polarized adhesive material, the polarized adhesive material being bonded, embedded, or operably connected to the substrate. The use of a polarized adhesive material may at least temporarily assist with the positioning and eventual attachment or securing of the surface cover, such as wallpaper, borders, and decals, at a desired location on an adjacent mounting surface before the activation of the adhesive material. 
         [0003]    Many common films and substrates (hereinafter collectively referred to as “substrates”) have an adhesive material bonded or operably connected to the backside surface of the substrate to create a surface cover. Examples of such surface covers may include wallpaper, borders, and decals, among others. But in the past, these surface covers have typically required that the adhesive material be activated before the substrate will adhere to an adjacent mounting surface at a desired location. For example, the glue adhesives that are commonly used with wallpaper typically must be wetted before the wallpaper can adhere to a wall at its desired location. Other types of adhesive materials require activation by the exposure of the adhesive material before the substrate may be positioned and secured to a mounting surface, such as through the removal of backing strips. Once the adhesive material has been activated, and the substrate has been secured against the adjacent mounting surface, subsequent attempts at adjust or move the placement of the surface cover may either be very difficult, damage the ability of the adhesive material to adhere to the mounting surface, and/or damage or destroy the substrate. 
         [0004]    Further, having to activate the adhesive material before the surface cover will at least temporarily remain at or around a desired location on the adjacent mounting surface often makes precise positioning of such surface covers, or aligning the patterns or images on the substrate with those on neighboring substrates, difficult. For instance, common wallpaper has traditionally been difficult and cumbersome to install because, after wetting, the adhesive material on the back of the wallpaper may begin to set before the installer has time to properly align the printed patterns on the substrate with those on a neighboring strip of wallpaper. Additionally, wall boarders that incorporate pressure sensitive adhesive material often suffer from similar difficulties and problems in that once the adhesive material is activated, adjustments or realignment of the border often ruins at least a portion of the substrate. The difficulty in properly installing such surface covers often results in misaligned and/or torn or ruined substrates, which may increase material costs and justify the high cost of professional installation. 
         [0005]    In an attempt to overcome such difficulties, some substrates are electrostatically polarized so that the substrate will adhere to an adjacent mounting surface without the need for an adhesive material. Such substrates utilize differences between the polarities of the substrate and the mounting surface to create an adhering bond that may allow the substrate to adhere to an adjacent mounting surface without the use of an activated adhesive material. The absence of an activated adhesive material may allow a polarized substrate that is placed along an adjacent mounting surface to be subsequently removed from that surface. The polarized substrate may then be reapplied to the same adjacent mounting surface, thereby allowing for the position and/or alignment of the substrate to be adjusted, without having to deal with the complications that are commonly associated with attempting to move surface covers that have activated adhesive material. 
         [0006]    Yet, the ability to relatively easily remove or adjust the position of polarized substrates that do not use an adhesive material may also allow for accidental positional adjustments that may occur through inadvertent contact with the substrate. Further, the polarized charge may need to be sufficiently strong so as to support the weight of the entire substrate. Over time, the substrate may also at least partially lose its electrostatic charge. For instance, the presence of elevated temperatures and humidity may cause dissipation of the electrostatic charge. Dissipation of the electrostatic charge may cause the substrate to lose its adhesive connection with the adjacent mounting surface, which may result in the surface cover sagging or eventually falling or slipping from its position on a mounting surface. 
         [0007]    In the past, one solution to this problem has been to attach a non-polarized adhesive material to a polarized substrate. In such devices, the adhesive force used to adhere the substrate to an adjacent mounting surface is created by both the polarized charge of the substrate and the activation of the adhesive material. Thus, in such systems, the electrostatic charge may be an integral part of the substrate being able to remain adhered to the adjacent mounting surface, even after the adhesive material has been activated. 
         [0008]    Yet, as previously mentioned, over time, the polarized charge of the substrate may dissipate, which may reduce the strength of the adhesive connection between the substrate and the adjacent wall. Further, such apparatuses may be limited to use with substrates that have electret capabilities. Additionally, electrostatically charged or chargeable substrates may also create additional manufacturing and handling disadvantages. 
         [0009]    In past situations in which a substrate has not been capable of maintaining or receiving an electrostatic charge, one solution has been to add a second substrate that does have the ability to receive, and at least temporarily maintain, an electrostatic charge for a sufficient amount of time to allow the substrate to be positioned generally around its desired location prior to the activation of the adhesive material. For example, in some apparatuses, the second substrate may be a discrete layer of polarized film. But the inclusion of a second substrate may increase material and handling costs, along with adding weight to the substrate. Furthermore, this second polarized film, if made of conventional electret films such as polypropylene, may have a tendency to distort when exposed to elevated temperatures, which may adversely impact the functionality of the substrate. 
         [0010]    Thus, a need exists for a surface cover that may at least temporarily adhere to a mounting surface at a desired location, and, if needed, subsequently be re-positioned before the activation of an adhesive material. Moreover, a need exists for a surface cover having a polarized adhesive material that may allow for the at least temporary positioning, and subsequent re-positioning, of the surface cover along a mounting surface without damaging the substrate or adhesive capabilities of the adhesive material. 
       BRIEF SUMMARY OF THE INVENTION 
       [0011]    Embodiments of the present invention relate to a surface cover having a polarized adhesive material bonded or operably connected to at least a portion of a substrate. The adhesive material may be polarized before or after being bonded or operably connected to the substrate. Further, the polarized adhesive material may be continuously applied to the back portion of the substrate or at select locations. Prior to the activation of the polarized adhesive material, the surface cover may be positioned and aligned at the desired location, whereby the electrostatic charge carried by the polarized adhesive material may at least temporarily provide the necessary attraction force to maintain the positioning of the surface cover along the adjacent mounting surface. The polarized adhesive material may then be activated, such as through the use of heat or pressure, thereby allowing the surface cover to be supported by the activated adhesive material. The activation of the adhesive material may also result in the dissipation of the polarized charge so that the polarized charge may or may not be an integral part in the adhesive force that adheres the surface cover to the adjacent mounting surface. In one embodiment, the current invention can be used to replace products that rely on pressure sensitive adhesive material, such as, but not limited to, shelf liners, window tinting, and decals, or lamination applications, such as real or synthetic veneers on furniture. 
         [0012]    According to certain embodiments of the present invention, a surface cover includes a metallic substrate having a face portion and a back portion, and a polarized adhesive covering at least a portion of the back portion of the metallic substrate. The metallic substrate may, for example, be foil film. Alternatively, the metallic substrate may be metallized onto the polarized adhesive. The polarized adhesive may be a heat activated material, and may be formed from a polyisobutylene or a cyclic olefin copolymer, for example. 
     
    
     
       BRIEF DESCRIPTION OF SEVERAL VIEWS OF THE DRAWINGS 
         [0013]      FIG. 1  illustrates a side perspective view of a surface cover having a substrate with at least a portion of the backside surface of the substrate being covered with a polarized adhesive material according to an embodiment of the present invention. 
           [0014]      FIG. 2  illustrates a rear view of a surface cover having a substrate with a backside surface being at least partially covered with a polarized adhesive material according to an embodiment of the present invention. 
           [0015]      FIG. 3  illustrates a rear view of a surface cover having a substrate with a polarized adhesive material being positioned in select locations on the backside surface of the substrate according to an embodiment of the present invention. 
           [0016]      FIG. 4  illustrates a rear view of a surface cover having a substrate with a polarized adhesive material and non-polarized adhesive material being positioned in select locations on the backside surface of the substrate according to an embodiment of the present invention. 
           [0017]      FIG. 5  illustrates a side view of a surface cover having a first substrate operably connected to a second substrate, and a polarized adhesive material according to an embodiment of the present invention. 
           [0018]      FIG. 6   a  illustrates a side view of a surface cover having a metallic substrate and a polarized adhesive material according to an embodiment of the present invention. 
           [0019]      FIG. 6   b  illustrates a side view of a surface cover as shown in  FIG. 6   a  with an ultraviolet (UV) or ink coating  22  applied over the metallic substrate. 
           [0020]      FIG. 7  illustrates a side view of a surface cover which incorporates a non-woven substrate  26  is applied over the top of the adhesive material and a polyvinylidene chloride (PVDC) material applied over the top of the non-woven substrate. 
       
    
    
       [0021]    The foregoing summary, as well as the following detailed description of the preferred embodiments of the present invention, will be better understood when read in conjunction with the appended drawings. For the purpose of illustrating the preferred embodiments of the present invention, the drawings depict embodiments that are presently preferred. It should be understood, however, that the present invention is not limited to the arrangements and instrumentality shown in the attached drawings. 
       DETAILED DESCRIPTION OF THE INVENTION 
       [0022]      FIG. 1  illustrates a side perspective view of a surface cover  10  having a substrate  12  with at least a portion of the backside surface  18  of the substrate  12  being covered with a polarized adhesive material  14  according to an embodiment of the present invention. Suitable substrates  12  include wallpaper, boarder materials, paper, film, vinyl, fabric, polyester, and web materials, among others. Additionally, the materials selected for the substrate  12  may lack electret capabilities in that the substrate  12  has no or negligible electret capabilities. In other embodiments of the present invention, the substrate may have electret capabilities that may assist the polarized adhesive material  14  in adhering the surface cover  10  against at least a portion of the mounting surface prior to the activation of the polarized adhesive material  14 . 
         [0023]    The polarized adhesive material  14  may be bonded, embedded, or operably connected to the entire backside surface  18  of the substrate  12 . In other embodiments, the polarized adhesive material  14  may be bonded or operably connected to only select areas of the substrate  18 . Further, although  FIG. 1  illustrates the polarized adhesive material  14  being bonded directly to the backside surface  18  of a single substrate  12 , in other embodiments of the present invention the polarized adhesive material  14  may be applied to at least a portion of one substrate  12  or other backing material that is operably connected to at least one other substrate  12 . 
         [0024]    The physical and electrical characteristics of a polarized polymer greatly impact its ability to accept and maintain a charge. To properly accept a charge, the polymer needs to be a good must be a good insulator; it preferably should have a resistivity of 10 12 ohms/sq or better. Some polymers have good insulating, but poor charge retention properties. Thus, the polymer preferably has a low dissipation factor, e.g., less then 0.005%). 
         [0025]    Pure polymers often make good electrets, but have limited adhesion and lack molten properties such as tack and wettability. Potential additives to improve the adhesive properties include low and medium molecular weight polyisobutylene, propylene-maleic anhydrite graft copolymer, monomodal and bimodal toner binder resins, among others. Coatings to improve adhesion include cyclohexane, heptane, chlorinated polyolefins, for example. 
         [0026]    The operational range of the polarized adhesive is between the glass transition temperature (Tg) and the melt temperature (Tm). Specifically, a polymer based polarized adhesive will dissipate its charge if it is exposed to a temperature above its glass transition temperature. Thus, the polarized adhesive should have a glass transition temperature in excess of the temperatures to which the surface cover  10  may be exposed to prior to installation. For example, it is not uncommon for products to be exposed to temperatures as high as 62° C. during shipping and storage in trailers and warehouses. Accordingly, in certain embodiments of the present invention, the glass transition temperature of the polarized adhesive ranges from about 35° C. to about 65° C. It is desirable to have the melt temperature as low as possible to lower the temperature of the heat source (iron, hair dryer, heat gun) so as not to damage the adjacent mounting surface and speed up the activation of the adhesive material. According to certain embodiments of the present invention, the melt temperature of the polarized adhesive ranges from about 65° C. to about 205° C. 
         [0027]    A number of different adhesive materials may be used in the present invention. In some embodiments, the adhesive material may be a heat activated adhesive material or a pressure activated adhesive material. Suitable heat activated adhesive materials include glues that are commonly used in the manufacturing of laminating film for the printing industry. Further, additives may be formulated into the adhesive material and/or substrate  12  to increase the receptivity and durability of the polarization charge. 
         [0028]    The adhesive material used in the polarized adhesive material  14  may have properties that make it both a good electret and adhesive. Once charged with an electrostatic charge, the adhesive material becomes the polarized adhesive material  14 . Examples of heat based adhesive materials may include polypropylenes, polyisobutylenes, cyclic olefin copolymers (COC), and members from the metallocene family of polymers, among others. In some embodiments, the adhesive material may have dielectric properties similar to that of polypropylene. An example of a commercially available polyisobutylene is Oppanol B200™, which is manufactured by BASF™. The properties of some of these materials are listed in the following table: 
         [0000]    
       
         
               
               
               
               
             
               
               
               
               
             
           
               
                   
                   
               
               
                   
                 Polypropylene 
                 Polyisobutylenes 
                 COC 
               
               
                   
                   
               
             
             
               
                   
               
             
          
           
               
                 Volume 
                 10*16-10*18 
                 1.00E+16 
                 1.00E+17 
               
               
                 Resistivity, 
               
               
                 Ohm*m 
               
               
                 Dielectric 
                 2.2-2.6 
                 2.2 
                 2.35 
               
               
                 Constant @ 
               
               
                 1 MHz 
               
               
                 Dissipation 
                 0.0003-0.0005 
                 0.005 
                 ≦0.0002 
               
               
                 Factor (%) 
               
               
                   
               
             
          
         
       
     
         [0029]    Additives, such as metallocene or maleic-anhydride-modified polypropylene, among others, may be also formulated or added to the adhesive material to improve the electret and/or adhesive properties of the adhesive material. These additives may also be formulated to improve other characteristics or properties of the adhesive material, including the melting temperature, tackiness, and viscosity, among others. In some applications, such as when the surface cover  10  is traditional wallpaper, the adhesive, with or without the inclusion of any necessary additives, may need to be at least semi-flexible when in a solid state so that, when in use, the polarized adhesive material  14  does not prevent the surface cover  10  from being rolled. One suitable commercially available additive is Licomont AR 504, which is manufactured by Clariant GmbH. 
         [0030]    The selection of adhesive materials and/or additives may also consider the temperature of the heat source used to activate the heat based materials, and any desire for that temperature to exceed the melting temperature of the adhesive material. For instance, in some applications, a hair blower may provide heat at about 85° C. for activation of the heat based adhesive material. In such applications, the selected or formulated adhesive material may have a melting temperature of less then about 85° C. In other applications, an iron may be used to activate the adhesive. In such applications, the melt temperature may be on the order of between 100° C. and 200° C. 
         [0031]    Because the charge carried by electrets may be dissipated or lost when the electret is exposed to temperatures above the glass temperature of the adhesive material, additives may also be included to increase glass temperatures. In some embodiments of the present invention, the glass transition temperature (T g ) of the adhesive material may be about 60° C. Further, the glass transition temperature may be relatively close to the melting temperature. 
         [0032]    According to one preferred embodiment of the present invention, the polarized adhesive comprises a COC material. A COC material is beneficial over other materials, such as polypropylene, because of its superior charge retention capabilities. Suppliers of COC include TOPAS Advanced Polymers, Inc., Mitsui Chemical Industries and Nippon Zeon. One example of a suitable commercially COC is a blend of TOPAS® 9506-F COC and TOPAS® TB COC, both of which are available from TOPAS Advanced Polymers, Inc. As mentioned above, the TOPAS® 9506-F COC has a relatively high melt temperature and a relatively low flow rate, resulting in increased flexibility before the adhesive is activated. Topas 9506-F COC is commonly used to make film. The TOPAS® TB COC has a relatively lower melt temperature and a relatively higher flow rate, resulting in increased tack when the adhesive is activated. Topas TB COC is very brittle and would fracture if made into a film by itself. These two materials can be blended to achieve an adhesive that provides desirable properties for a polarized adhesive for use in a surface cover of the type described herein. According to one preferred embodiment, the polarized adhesive is a blend of between 20% and 80% TOPAS® TB COC by weight, with the balance of the blend being TOPAS® 9506-F COC. In one preferred embodiment, the polarized adhesive is a blend of 30% TOPAS® TM COC (by weight) and 70% TOPAS® 9506-F COC. 
         [0033]    Another example of a suitable commercially COC is a blend of TOPAS® 9506-F COC and TOPAS® TM COC, both of which are available from TOPAS Advanced Polymers, Inc. of Florence, Ky. The TOPAS® 9506-F COC has a relatively high melt temperature and a relatively low flow rate, resulting in increased flexibility before the adhesive is activated. The TOPAS® TM COC has a relatively lower melt temperature and a relatively higher flow rate, resulting in increased tack when the adhesive is activated. These two materials can be blended to achieve an adhesive that provides desirable properties for a polarized adhesive for use in a surface cover of the type described herein. According to one preferred embodiment, the polarized adhesive is a blend of between 20% and 80% TOPAS® TM COC by weight with the balance of the blend being TOPAS® 9506-F COC. In one preferred embodiment, the polarized adhesive is a blend of 50% by weight and TOPAS® TM COC and 50% TOPAS® 9506-F COC. 
         [0034]    Some of the properties of these materials are listed in the following table: 
         [0000]    
       
         
               
               
               
               
             
               
               
               
               
             
           
               
                   
                   
               
               
                   
                 TOPAS ® 9506-F 
                 TOPAS ® TM 
                 TOPAS ® 
               
               
                   
                 COC 
                 COC 
                 TB COC 
               
               
                   
                   
               
             
             
               
                   
               
             
          
           
               
                 Glass transition 
                   68° C. 
                    65° C. 
                    65° C. 
               
               
                 temperature 
               
               
                 Melt Flow 
                 6@230° C. 
                 25 @ 115° C. 
                 10 @ 175° C. 
               
               
                 Volume 
               
               
                   
               
             
          
         
       
     
         [0035]    The adhesive properties of polymers such as COC may be enhanced by coating or priming the polymer with chlorinated polyolefin&#39;s, cyclohexane or heptane. Coating or spot coating the polarized adhesive may help in adhering to difficult substrates. Examples include CP343-3 as manufactured by Eastman Chemical or Trapylen and Trapur as manufactured by Rowa GmbH. 
         [0036]    Selection of an appropriate type of substrate  12  may consider such factors as the ability of the substrate  12  to withstand distortion when elevated to high temperatures during the activation of a hot melt adhesive material and/or exposure to humidity. For instance, during installation of the surface cover  10 , the substrate  12  may be exposed to a hot heat source. Often the temperature of the heat source used to activate a hot melt adhesive is set at a temperature substantially above the melting temperature of the polarized adhesive material  14 . For example, an iron used to activate a hot melt adhesive material may be set at temperatures in excess of 70° C. The elevated temperature of the heat source may speed the transfer of heat and activate the polarized adhesive material  14  quickly and easily. However, such high temperatures may damage some types of substrates  12 . For instance, films such as orientated polypropylene or polyester may warp and distort when exposed to temperatures that melt the polarized adhesive layer  14 . 
         [0037]    Other types of substrates  12  materials, such as paper, may be capable of withstanding such high temperatures without having problems with distortion, but are unable to resist distortion due to the absorption of humidity or being rolled up. Conversely, a polyester substrate  12  may resist dimensional instability from exposure to humidity, but distort under heat. A suitable material that may resist distortion or dimensional instability when exposed to high humidity and temperatures may include a nonwoven or woven fabric composed of cellulose and or synthetic fibers, and which has been treated with a chemical binder. An example of such a product is manufactured by Ahlstrom (product 11455 non-heat sealable filter paper). 
         [0038]    Films which have a melt temperature substantially higher then the melt temperature of the polarized adhesive may also be used for forming the substrate. An example of an outer layer film is heat stabilized cast nylon film 6,6 as manufactured by Expopak Performance Films. Another option alternative is Topas 6013F-04 as sold by TOPAS Advanced Polymers, Inc. This material has a glass transition temperature of 140° C. and melt temperature of 240-260° C. 
         [0039]    Alternatively, in accordance with one embodiment of the present invention, the substrate  12  may be operably connected to a second substrate that may act as a cover for the substrate  12  to prevent the substrate by being damaged by the direct exposure of the substrate  12  to the heating source and/or decrease the exposure of the substrate  12  to humidity. In another embodiment, the front surface of the substrate  12  may have a protective coating that prevents damage to the substrate  12  from direct exposure to the heat source and/or protects the substrate  12  from excessive exposure to humidity. 
         [0040]    Application of adhesive material to the substrate  12  may be achieved through extrusion coating. In such a process, pellets of dry adhesive material may be heated and forced through a die that thins out the adhesive material into a continuous web of semi-molten adhesive material. In some applications, the molten adhesive material may then be applied to the substrate  12  while the substrate  12  is part of a continuous web of film via a nip roller. The temperature of the molten adhesive material when it is applied to the substrate  12  may at least in part be dependent on the properties of the polarized adhesive material  14  and/or substrate  12 . 
         [0041]    Polarization of the adhesive material may occur when the adhesive material is in a molten state through the use of a large polarizing electric current. Through polarization of the molten adhesive material, an electric current may orientate molecules in the molten adhesive material so that they are all positively or negatively aligned in the same direction. However, other adhesive materials may be electrostatically charged when the adhesive material is in a solid state. For example, the electrostatic charge may be applied to the adhesive material when it is in a molten state immediately after the adhesive material is extruded through a die, or, alternatively, after the adhesive material has been re-solidified on the substrate  12  following reaching a nip/chill roller. Determination of whether to charge the adhesive material when the adhesive material is in a molten or solid state may depend on a variety of factors, including, but not limited to, the material of the substrate  12 . 
         [0042]    In application, the polarized adhesive material  14  may at least temporarily adhere the surface cover  10 , and more particularly the substrate  12 , to an adjacent mounting surface. Temporary reliance on the adherence created by the differences between the polarities of the polarized adhesive material  14  and the mounting surface may allow the surface cover  10 , and any adjacent or adjoining surface covers, to be installed and repositioned (i.e., via removal or sliding) at desired locations prior to final installation. For some polarized adhesive materials, final installation may involve the activation and setting or curing of the activation of the polarized adhesive material against the mounting surface. 
         [0043]    Once the surface cover  10  is positioned against the mounting surface at its desired location, the polarized adhesive material  14  may be activated. In the illustrated embodiment, activation of a hot melt polarized adhesive material  14  may involve the application of a heat source, such as a iron or blow-drier, to the surface cover  10 , which may result in a rise in temperature in the polarized adhesive material  14  on the backside  18  of the substrate  12 . For example, some hot melt adhesives require a minimum activation temperature of 65° C. The rise in temperature may result in at least a portion of a heat based polarized adhesive material  14  being transformed into a molten state. At some point after the removal of the heat source, the temperature of the heat activated polarized adhesive material  14  may decreased, whereby molten polarized adhesive material may set or cure against both the substrate  12  or other portions of the polarized adhesive material  14  and the mounting surface. In some embodiments of the present invention, activation of the polarized adhesive material  14  may significantly dissipate or remove the electrostatic charge of the polarized adhesive material  14  so that the “sticking” or adhering engagement created by the activated adhesive material, and not the electrostatic charge, may provide a significant portion, if not all, of the adhesive force required to maintain the substrate  12  at its desired location. 
         [0044]    As previously mentioned, the adhesive material, before or after being polarized, may be positioned or coated onto a substantial portion of the substrate  12 , such as the backside of the substrate  12 . However, in other embodiments, the polarized adhesive material  14  may be selectively placed along the substrate  12 . For example,  FIG. 2  illustrates a rear view of a surface cover  10  having a substrate  12  with a backside surface  18  being at least partially covered with a polarized adhesive material  14  according to an embodiment of the present invention. Selective placement of the polarized adhesive material  14  may reduce manufacturing and material costs of the surface cover  10 . In another example, the polarized adhesive material  14  may be applied to the backside surface  18  of the substrate  12  in a grid or lined pattern. 
         [0045]      FIG. 3  illustrates a rear view of a surface cover  10  having a substrate  12  with a polarized adhesive material  14  being positioned in select locations on the backside surface  18  of the substrate  12  according to an embodiment of the present invention. In such an embodiment, adhesive material that is polarized or capable of carrying a polarized charge may be placed in select positions on the substrate  12 , such as the corners, edges, and/or center region on the backside  18  of the substrate  12 . 
         [0046]      FIG. 4  illustrates a rear view of a surface cover  10  having a substrate  12  with a polarized adhesive material  14  and non-polarized adhesive material  16  being positioned in select locations on the backside surface  18  of the substrate  12  according to an embodiment of the present invention. In such embodiments, the amount and location of the polarized adhesive material  14  may be such that the substrate  12  may still be able to at least temporarily positioned along or against an adjacent mounting surface before the introduction of heat to activate either the polarized adhesive material  14  or the non-polarized adhesive material  16 . The non-polarized adhesive material  16 , such as, but not limited to, heat or pressure activated adhesive materials, may be placed at other locations on the substrate  12  that are not occupied by the polarized adhesive material  14 . In another embodiment, the polarized adhesive material  14  may be placed on top of, or at least partially overlap, at least a portion of the non-polarized adhesive materials  16 . But again, in such embodiments, the amount and location of the polarized adhesive material  14  may be such that the substrate  12  may still be able to at least temporarily be positioned along or against the adjacent mounting surface before the activation of the polarized adhesive material  14  and/or the activation of non-polarized adhesive material  16 . 
         [0047]      FIG. 5  illustrates a side view of a surface cover  10  having a first substrate  12   a  operably connected to a second substrate  13   a , and a polarized adhesive material  14   a  according to an embodiment of the present invention. The first substrate  12   a  and the second substrate  13   a  may be operably connected to each other through the use of an adhesive, such as, but not limited to, glues and epoxies. In such an embodiment, both the first and second substrates  12   a ,  13   a , may or may not be capable of receiving or maintaining any electric charge. For example, the first substrate  12   a  and/or second substrate  13   a  may be paper, fabric, film, foil or polyester materials that have little, if any, electret capabilities. Moreover, when both the first and second substrates have no electret capabilities or negligible electret capabilities, the polarized adhesive material  14   a  may provide a sufficient polarized charge to at least temporarily adhere the surface cover  10  at least generally in the desired location until the activation of the polarized adhesive material  14   a . In another embodiment, the material selected for the first substrate  12   a  and/or second substrate  13   a  may have at least some electric capabilities that may assist with polarized adhesive material  14   a  in at least partially securing the surface cover  10  against the mounting surface before activation of the polarized adhesive material  14   a.    
         [0048]      FIG. 6   a  illustrates an embodiment where the substrate  12  comprises a metallic substrate  20 . The metallic substrate  20  may, for example, be formed of a foil film, such as an aluminum foil film. A suitable foil film is commercially available from Republic Foil under the trade name 1145-O. Alternatively, the metallic substrate may be metallized directly onto the polarized adhesive  14 , e.g., through a vaporization process. According to one preferred embodiment the metallic substrate  20  comprises a foil film having a thickness of between 0.015 inches and 0.00020 inches and most preferably on the order of about 0.000258 inches. The foil film and the polarized adhesive are operably connected to each other through a tie layer of adhesive (not shown), such as, but not limited to, glues and epoxies. 
         [0049]    The metallic substrate  20  provides several benefits, particularly when the polarized adhesive  14  is heat activated. For example, the metallic substrate  20  protects the polarized adhesive  14  when heat, e.g. from an iron, is applied to the surface cover  10  during the installation process. The metallic substrate  20  also stiffens the polarized adhesive  14 , which is beneficial, for example in preventing charge wrinkling, which could otherwise occur because of the highly flexible nature of the polarized adhesive  14 . Additionally, the metallic substrate  20  protects the polarized adhesive  14  from moisture, e.g., due to high humidity. As discussed above, high humidity may cause dissipation of the electrostatic charge. The metallic substrate is also beneficial because it transfers heat very quickly and evenly during the installation process, e.g., when an iron or heat gun is used to activate the polarized adhesive  14 . This is to be contrasted with a non-woven substrate, which acts as an insulator and impedes heat transfer to the polarized adhesive  14 . The metallic substrate  20  is also fire retardant and does not emit volatile organic chemicals. Additionally, the metallic substrate  20  is opaque. This is beneficial for example when the surface cover  10  is wall paper because the foil will block out the underlying wall cover. As shown in  FIG. 6   b , an ultraviolet (UV) or ink coating  22  may be applied over the metallic substrate  12  to provide a background color for the surface cover  10 . A print layer  24  may in turn be applied over the coating  22 . Preferably the print layer comprises an UV ink. The UV ink is beneficial because once cured by an ultraviolet light it is a solid with a very high melt temperature and is not affected by the heat of an iron or heat gun. 
         [0050]      FIG. 7  illustrates an embodiment of the present invention, which includes the polarized adhesive material  14 , as discussed above. A non-woven substrate  26  is applied over the top of the polarized adhesive material  14 . A polyvinylidene chloride (PVDC) material  28  is applied over the top of the non-woven substrate  26 . The PVDC material  28  protects the non-woven layer against moisture infiltration. A suitable PVDC material is commercially available from Ixan-Diofan under the trade name Diofan A 115. A UV or ink coating  30  may be applied over the top of the PVDC  28  to provide a background color for the surface cover  10 . A print layer  32  may in turn be applied over the coating  30 . 
         [0051]    While the invention has been described with reference to certain embodiments, it will be understood by those skilled in the art that various changes may be made and equivalents may be substituted without departing from the scope of the invention. In addition, many modifications may be made to adapt a particular situation or material to the teachings of the invention without departing from its scope. Therefore, it is intended that the invention not be limited to the particular embodiment disclosed, but that the invention will include all embodiments falling within the scope of the appended claims.