Abstract:
A method for fabricating an electron emitter is provided. This emitter structure may be used to form individual emitters or arrays of emitters. The method is comprised of implanting energetic ions into a diamond lattice to form cones or other continuous regions of damaged diamond. These regions are more electrically conducting than the surrounding diamond lattice, and have locally sharp tips at or near the point of entry of the ion into the diamond. The tips may then also be additionally coated with a layer of a wide band-gap semiconductor. An electrically conducting material may also be placed in proximity to the tips to generate an electric field sufficient to extract electrons from the conducting tips into either the region above the surface, or into the wide band-gap semiconductor layer in contact with the tips. Electrical contact is made to the electrically conducting damage tracks and the electrical circuit may be completed with an electrically conducting material on the surface of the wide band-gap semiconductor or diamond, or in the ambient above the surface of the emitter. The surface of the wideband gap semiconductor or diamond may be chemically modified to enhance the emission of electrons from the surface.

Description:
BACKGROUND OF THE INVENTION  
         [0001]    1. Field of the Invention  
           [0002]    The present invention is related to the field of electron emitters and more particularly, relates to a method for making stable, electron emitters and devices therefrom in diamond using an ion implantation technique.  
           [0003]    2. Background of the Invention  
           [0004]    There has been a great deal of research with respect to the physics of, and improved methods for fabricating, stable, modulatable electron (field) emitters (a type of cathode) having high current densities. Electron emitters are commonly used in such devices as power switches, microwave amplifiers, traveling wave tubes and the like.  
           [0005]    Electron emitters emit electrons from structures at their ends, commonly referred to as “tips.” The “tips” of emitters have a very small radius of curvature i.e. the tips are very pointed. The application of relatively small voltages in close proximity to an emitter extracts disproportionately large electron flows from its tip because the small radius of curvature of a tip concentrates the electric field.  
           [0006]    The electric field extracts electrons from the conduction band and/or the valence band and/or Fermi level of the emitter material.  
           [0007]    Devices of this type using tips and gates are commonly referred to as Spindt cathodes. A Spindt cathode is usually comprised of a micron-size cone or other structure with a sharp tip at the apex that is centered in a small-diameter hole. The size of the cone or other structure can vary. Furthermore, the shape of the cone can vary, as long as the structure contains a sharp tip. The cone is usually electrically conducting. Typically there is an electrically conducting film at or near the top of the cathode, usually in the shape of an annulus centered around the tip. The electrically conducting film may be used to apply an electrical potential near the tip of the cone and is called a “gate”. The tip of the cone typically lies in or below the plane of the “gate” and is centered in a hole in the gate. When the cone has a sharp tip, an applied voltage between the cone and the gate causes electrons to emit from the cone tip into the surrounding media (typically a vacuum) and to be collected by a third electrical conductor, the anode. The design of the Spindt cathode allows a small applied voltage between the gate and the tip over a sub-micron distance to extract a comparatively large amount of electrons. Spindt cathodes are typically fabricated in large arrays. Spindt cathodes are typically treated with a material having a low work function such as Cs. This treatment of the cathodes lowers the work function of the cathodes, thereby facilitating emission of the electrons.  
           [0008]    Spindt cathodes often suffer tip instabilities. These instabilities are brought about by processes such as heating of the cathode, electromigration and ion sputtering from the gas phase. Ion sputtering occurs as the electrons ejected from the tip ionize background gas molecules near the tip. The ionized gas molecules are accelerated back towards the substrate containing the tip by the same electric field used to extract the electrons from the tip. The momentum damage from the ion colliding with the tip sputters and blunts the tip of each electron emitter. As the tip is blunted, the radius of curvature of the tip increases. This lowers the enhancement of the electric field at the tip. Furthermore, such processes change the surface composition of the tip by furthering undesirable processes at the tip such as oxidation. This can increase the work function of the tip and lower the electron emission for a given applied voltage.  
           [0009]    Another problem inhibiting development of arrays of these devices is making uniform the voltage applied to, and current extracted from, the individual tips. These non-uniformity problems often occur because of variations in the morphology, form and structure of individual tips. These problems can also occur because of differences in the distance between the individual tips and their gates, and because of variations of the effective work function of the individual tips due to differences in surface chemistry. The results of this lack of uniformity among the individual tips within the array are most commonly: poor overall emission from the array, or emission of most of the current from only a small number of tips in the array. Emission from a small number of tips leaves the tips which are emitting most of the current prone to overheating and to catastrophic failure.  
           [0010]    To address these problems, diamond has received much attention as an emitter surface because under some conditions diamond has negative electron affinity. Because of this negative electron affinity, the vacuum level falls below the conduction band minimum, and an electron in the conduction band encounters little or no energetic barrier to emission into the vacuum. However, for diamond to work here, the electrons must be transmitted thru the diamond. Further, in some applications the electrons must be able to move through the diamond lattice from the point of injection to the front surface of the lattice, and then cross the front surface/vacuum interface and exit the interface into the vacuum or be collected by a conducting film on the surface.  
           [0011]    Because of these electron transport problems, it would be beneficial to minimize the thickness of the lattice through which the electrons move and to create a lattice (or material) which causes minimal or no energy loss to the electrons as they move through the lattice. Further, it is desirable to minimize the work function of the emitting surface, and to minimize any energy losses that occur at the surface during emission.  
           [0012]    There have been attempts in the prior art to address some of the issues discussed above. Prior art patents of interest includes U.S. Pat. No. 5,990,604 to Geis et al.; U.S. Pat. No. 5,945,778 to Jaskie; U.S. Pat. No. 5,857,882 to Pam et al.; U.S. Pat. No. 5,757,344 to Miyata et al.; U.S. Pat. No. 5,670,788 to Geis; U.S. Pat. No. 5,258,685 to Jaskie et al.; U.S. Pat. No. 5,202,571 to Hirabayashi et al.; U.S. Pat. No. 5,141,460 to Jaskie et al.; and U.S. Pat. No. 5,129,850 to Kane et al.  
           [0013]    The Geis et al. (&#39;604) patent discloses a field emitter of wide-bandgap materials composed of a doped diamond film emitter formed by chemical vapor deposition combined with a metal compound through annealing, etching or ion bombardment. The Jaskie (&#39;778) patent discloses an enhanced electron emitter composed of a diamond bond structure with an electrically active defect at the emission site which is said to act like a very thin election emitter with a very low work function and improved current characteristics. The Pam et al. patent discloses a method for the processing of materials for uniform field emission. The field emitters are composed of a polycrystalline film on a substrate formed by carbon ion implantation, annealing and then conditioning by scanning with an electrode. The Miyata et al. patent discloses a cold cathode emitter element composed of a diamond film emitter and a diamond insulating film. The Geis (&#39;788) patent discloses a diamond cold cathode composed of a carbon ion implanted n-type conductivity diamond region and a doped homoepitaxial p-type conductivity diamond region with ajunction between. The Jaskie et al. (&#39;685) patent discloses a field emission electron source employing a diamond coating grown from carbon nucleation sites selectively disposed on a selectively shaped substrate. The Hirabayashi et al. patent discloses an electron emitting device with a diamond emitter layer formed on a semiconductor substrate. The Jaskie et al. (&#39;460) patent discloses a method of making a field emission electron source employing a diamond coating. The diamond coated emitter is formed by ion implantation creating nucleation sites for diamond formation. The Kane et al. patent also discloses a method of making field emitters with a diamond coating disposed on a conductive or semiconductive material, wherein the field emitters are formed by ion implantation of carbon into a selectively shaped substrate to facilitate diamond formation, depositing the conductive layer, and then removing the substrate.  
         SUMMARY OF THE INVENTION  
         [0014]    In accordance with the invention, a method for fabricating an electron emitter is provided. In one embodiment, the method comprises the steps of: implanting one or more ions into the surface of a diamond substrate including a diamond lattice including sp 3  bonded carbon so as to damage the diamond lattice and to change at least a portion of the sp 3  bonded carbon in the diamond lattice to a mixture of sp 3  bonded carbon and sp 2  bonded carbon, the damage to the diamond lattice material forming one or more emitter tips at or near the surface of the diamond lattice material tapering to a corresponding number of wider bases within the diamond lattice material; providing electrical contact to the base of the emitter tips; possibly growing one or more additional advantageous layers on the diamond substrate; and providing at least one gate on or under the surface of the diamond lattice or other additional advantageous layers.  
           [0015]    Preferably, at least one gate is deposited or otherwise created on or below the surface of the protective layer.  
           [0016]    Advantageously, at least one gate is deposited or otherwise created on or below the surface of the diamond substrate material before the protective layer is grown, or the gate can be subsurface.  
           [0017]    Preferably, a mask having one or more holes therein is placed or formed over the surface of the diamond lattice material prior to implantation; and the mask may be removed after implantation.  
           [0018]    Advantageously, the surface of the diamond substrate is terminated so as to lower the work function of the surface. Preferably, the surface is chemically modified with moieties containing one or more of the following: hydrogen, cesium, oxygen, fluorine, potassium, rubidium, lithium or any other alkali metal.  
           [0019]    Preferably, at least a portion of carbon from the damaged area resulting from the implantation is electrochemically or otherwise etched out so as to leave a hollow mold formed from etched out portions of the damaged area, and the mold so formed is filled with a conductive filler material. Prior patents of interest include: U.S. Pat. No. 5,269,890 to Marchywka; U.S. Pat. No. 5,587,210 to Marchywka et al., U.S. Pat. No. 5,702,586 to Pehrsson et al.  
           [0020]    Advantageously, the filler material comprises a metal, amorphous carbon, or silicon.  
           [0021]    Preferably, the protective layer comprises a thin homoepitaxial layer.  
           [0022]    In another embodiment, a conductive material is deposited or otherwise created on or under the thin protective layer so as to provide a gate structure. Advantageously, the conductive material is amorphous carbon.  
           [0023]    In yet another embodiment, the method comprises the steps of: implanting one or more ions into the surface of a doped diamond substrate including a diamond lattice including sp 3  bonded carbon, so as to damage the diamond lattice and to change at least a portion of the sp 3  bonded carbon in the diamond lattice to a mixture of sp 3  bonded carbon and sp 2  bonded carbon, the damage to the diamond lattice material forming one or more tips at or near the surface of the diamond lattice material tapering outwardly to a continuous, electrically conducting base within the diamond lattice material; providing an electrical contact to the implanted region; and if necessary, providing a diamond layer or layers on the diamond substrate; and providing at least one gate.  
           [0024]    Preferably, the diamond substrate is doped with nitrogen.  
           [0025]    Advantageously, the upper protective layer can be doped with boron.  
           [0026]    Advantageously, the thin protective layer or layers are comprised of one or more homoepitaxial diamond layers, either doped or undoped.  
           [0027]    In a further embodiment, the method comprises the steps of: implanting one or more ions into the surface of a diamond substrate including a diamond lattice including sp 3  carbon, so as to damage the diamond lattice and to change at least a portion the sp 3  bonded carbon in the diamond lattice to a mixture of sp 3  bonded carbon and sp 2  bonded carbon, the damage to the diamond lattice material forming one or more implantation areas at or near the surface of the diamond lattice material tapering outwardly to a single base within the diamond lattice material; providing an electrical contact to the implanted regions; possibly providing an additional diamond layer or layers on the diamond substrate; implanting one or more ions into the surface of the diamond layer including a diamond lattice including sp 3  bonded carbon so as to damage the diamond lattice and to change at least a portion of the sp 3  bonded carbon in the diamond lattice to a mixture of sp 3  bonded carbon and sp 2  bonded carbon, the damage to the diamond lattice material forming one or more tips at or near the surface of the diamond lattice material tapering to a corresponding plurality of wider bases within the diamond lattice material, wherein the plurality of wider bases are in conductive contact with the continuous, electrically conducting base within the diamond substrate; possibly growing a thin protective layer on the diamond layer; providing at least one gate; and providing at least one electrical contact to the implanted regions, and extending from the conductive base layer.  
           [0028]    Advantageously, a mask is used over at least a portion of the surface of the diamond layer before implantation.  
           [0029]    The arrays of electron emitters fabricated from the method of the invention are stable, modulatable, and have a high current density. The devices can operate in either a continuous (DC) or a pulsed mode. Further, the field emitting arrays can be fabricated using a group of standard techniques such as lithography, implantation, patterning and etching.  
           [0030]    Other features and advantages of the invention will be set forth in, or will be apparent from, the detailed description of preferred embodiments which follows.  
           [0031]    Advantageously, conductive or metallic material is deposited or otherwise created on or under the surface of the diamond or any of its protective layers. The resulting structure acts as an anode for the capture of electrons emitted from the tips. Its performance in this regard may be enhanced by applying a positive voltage with respect to the tip(s) or gate(s). 
       
    
    
     BRIEF DESCRIPTION OF THE DRAWINGS  
       [0032]    [0032]FIG. 1 a  is a schematic side elevational view of a substrate illustrating one step in a preferred embodiment of the method of the invention.  
         [0033]    [0033]FIG. 1 b  is a schematic side elevational view of the substrate of FIG. 1 a,  illustrating a further step of the method.  
         [0034]    [0034]FIG. 1 c  is a schematic side elevational view of the substrate of FIG. 1 a  illustrating a further step of the method.  
         [0035]    [0035]FIG. 1 d  is a schematic side elevational view of the substrate of FIG. 1 a  illustrating yet another step of the method.  
         [0036]    [0036]FIG. 1 e  is a schematic side elevational view of the finished product resulting from the steps of the method.  
         [0037]    [0037]FIG. 1 f  is a schematic side elevational view of a further finished product resulting from the steps of an alternative embodiment of the method.  
         [0038]    [0038]FIG. 1 g  is a schematic side elevational view of a finished product having an alternative gate structure.  
         [0039]    [0039]FIG. 1 h  is a schematic side elevational view of a substrate produced during an alternative embodiment of one step of the method of the invention.  
         [0040]    [0040]FIG. 2 is a schematic side elevational view of a finished product resulting from yet another embodiment of the method of the invention.  
         [0041]    [0041]FIG. 3 a  is a schematic side elevational view of a substrate illustrating one step in a further preferred embodiment of the method of the invention.  
         [0042]    [0042]FIG. 3 b  is a schematic side elevational view of the substrate of FIG. 3 a  illustrating a further step of the method.  
         [0043]    [0043]FIG. 3 c  is a schematic side elevational view of the substrate of FIG. 3 a  illustrating another step of the method.  
         [0044]    [0044]FIG. 3 d  is a schematic side elevational view of the substrate of FIG. 3 a  illustrating a further step of the method.  
         [0045]    [0045]FIG. 3 e  is a schematic side elevational view of a finished product resulting from the steps of the further preferred embodiment of the method of the invention. 
     
    
     DESCRIPTION OF THE PREFERRED EMBODIMENTS  
       [0046]    Several preferred embodiments of the method of the invention will be discussed with reference to the drawings.  
         [0047]    Referring to FIG. 1 a,  a diamond substrate  10  having a diamond lattice is shown. The diamond lattice within the material is comprised of a lattice of sp 3  bonded carbon atoms. As indicated by the arrows in FIG. 1 a,  a quantity of carbon or other ions are implanted into the diamond lattice material, as depicted by the arrows immediately above the diamond lattice substrate  10 . The quantity of ions are implanted into the diamond substrate  10  at a rate of speed sufficient to pass into part or all of the diamond lattice. The ions are implanted into the diamond substrate  10  so as to selectively damage specific volumes of the diamond lattice. The diamond lattice within the diamond material  10  is converted to a mixture of sp 2  and sp 3  or pure sp 2  carbon by the ions passing through the diamond material  10 .  
         [0048]    Turning to FIG. 1 b,  the diamond lattice substrate  10  is shown as having a damaged portion  11  caused by the ion implant operation and an undamaged portion  12 . Little energy is deposited into the lattice near the surface during the ion implant and because of the small amount of energy deposited at the surface of the diamond material  10 , most of the damage is concentrated at the lower end of the damaged portion  11  below the surface. In this regard, as illustrated, the area of damage of the damaged portion  11  is generally conical and tapers to a point at or near the surface of the diamond substrate  10 . This damage pattern results in high conductance regions with a broad base and comparatively narrow sharp tips at the surface of the diamond material  10 . The base of the damaged portion  11  can be laterally continuous (i.e., with the bases of adjacent cones joined together) depending on the nature of the conductive area being fabricated.  
         [0049]    In FIG. 1 b,  the damaged portion  11  is in the form of a group of individual cones, with a representative cone being denoted  11   a.  As illustrated, cone  11   a  extends downwardly from a point of impact at or near the surface to a wider base within the substrate material. Similarly, in FIG. 1 b,  the undamaged portion  12  separates the individual cones of the damaged area  11  from each other so that, as viewed in cross section, portions of the undamaged portion  12 , denoted  12   a  and  12   b,  isolate cone  11   a  between them. The damage to the lattice from the ion implantation results in changes to some of the bonds between the carbon atoms of the lattice in the damaged portion  11 . More specifically, the sp 3  bonds between the carbon atoms are converted by the damage to the lattice to a mixture of sp 2  and sp 3  bonds. Because of the changes in bond structure, the damaged portion  11  is more electrically conductive than the undamaged and unchanged portion  12  of the diamond substrate  10 .  
         [0050]    Sharp emitter tips are created at the tips of the cones of the damaged portion  11 , with a representative tip at the top of cone  11   a  being denoted  13 . The tips may be so small as to be atomically sharp. The sharpness and higher conductivity of cone  11   a  enable the cone to function effectively as a field emitter.  
         [0051]    The distribution of the damage to the diamond substrate  10  and, hence, the shape of the damaged area  11 , can be adjusted by changes in implantation energy, angle of implantation and ion mass of the implantation ions. The locations of the emitters relative to each other can be controlled by controlling the location of the points of ion implant at the surface of the substrate  10 .  
         [0052]    For example, the locations of the points of ion impact on the surface of the diamond substrate  10  can be adjusted by use of a mask (not shown). By varying the energy of the implanted ions, the borders of the damage can be adjusted so that the damage begins precisely at the surface of the diamond material  10 . Because of this ability to control the location of the damage area  11 , all of the tips of the cones of the damaged area  11  created by the ion implant operation can be made to be coplanar to the extent permitted by the smoothness of the starting surface. If desired, the energy can be adjusted such that the damage begins away from the starting surface.  
         [0053]    Damage to the tip  13  at or near the beginning of the ion implant region may be discontinuous or conduct insufficiently for efficient electron conduction, and hence subsequent processing steps may be required. Poor electron conduction near the tip can be minimized or eliminated by use of the mask to implant multiple ions through small lithographically-created openings in the mask  10 . The use of a mask helps ensure that the tip  13  is damaged from multiple ions such that there is ensured continuity of the damage and electrical contact near the surface to the emitter tips. The mask can be removed after the implantation is finished.  
         [0054]    Turning to FIG. 1 c,  in the step illustrated, a contact  14  is added beneath the diamond material for providing connection of a voltage source or other electrical circuit to the bases of the emitter tips contained in the diamond substrate  10 . The contact can also be made from the side or top of the diamond substrate, if necessary by opening a hole to the bases through any insulating diamond. The contact is typically comprised of a metal and the metal, or other suitable material of the back contact, may be selected to have a low work function. Referring to FIG. 1 d  in the illustrated: step, a series of gates, denoted  16 , are deposited on the surface of the diamond substrate  10 . The gates  16  are used to turn the emitter array on and off. In this embodiment, the gates  16  are formed by depositing a metal or other conducting material on the surface of the diamond substrate  10 . Alternatively, the gates can be created by an additional ion implantation step to form gates beneath the surface of the diamond, but still near or coplanar with the emitter tips.  
         [0055]    Because of the planar alignment of the tips of the cones  11  of the damaged region with each other, the distances between the tips of the cones  11  and the gates  16  are uniform. The degree of uniformity is primarily a function of the smoothness of the starting surface of the diamond substrate  10 .  
         [0056]    Referring to FIG. 1 e,  layer  18  of homoepitaxial diamond is grown on the diamond substrate  10  as a next step. Layer  18  can be more than one layer and can consist of variously doper and/or undoped layers. This results in the thin protective diamond layer  18  overlying a set of coplanar points at a highly uniform distance from the lower surface of the thin diamond layer  18 . Layer  18  protects the emitter tips from oxidation and backsputtering, while providing a low energy pathway for electrons to reach the surface/vacuum or surface/anode interface at the surface of the layer  18 . If the implantation energy was sufficiently high, the emitter tips are subsurface even without the growth of a further layer, and thus also have a protective diamond layer over them.  
         [0057]    In an alternative embodiment shown in FIG. 1 f,  the metal gates  16  are deposited after growth of the homoepitaxial layer  18  onto the layer  18  itself.  
         [0058]    In yet another embodiment, shown in FIG. 1 g,  an alternative gate structure  16 ′ is fabricated by the deposition of a continuous layer of a conductive material onto the diamond layer  18 . In this embodiment, the gate material is typically not a metal, but rather another conductive material, such as amorphous carbon, through which electrons will pass. Alternatively, the resultant array may have no gates or gate layer, as such, but rather use an anode (not shown) positioned on or above the diamond surface to fulfill the function of the gate. Alternatively, the resultant array may have gates or a gate layer below the surface, with an anode (not shown) positioned on or above the diamond surface to collect the emitted electrons.  
         [0059]    Referring to FIG. 1 h,  another embodiment is shown wherein an electrochemical etch or other type of etch is used to etch out the carbon in the damaged areas  11 . The etching leaves a mold recess  11   a corresponding to the removed cone  11   a′.  The mold from the etching is filled with metal, Si, or other suitable material. This process results in an emitter array with a very clean material/diamond interface at the emitter tip. Electrical contact to the emitters is made in the ways described above.  
         [0060]    The emitter array of the invention allows electrons to move through the diamond lattice, from the tip  13 , and to transit a diamond/vacuum or diamond/anode or protective layer/anode interface at the surface of the diamond substrate  10  with little or no energy loss. It has been found that diamond may exhibit ballistic electron transport through the lattice. This is especially true for electron transport over short (sub-micron) distances and for single crystal diamonds. An electron in the conduction band of properly-terminated diamond may encounter little or no energy barrier to prevent emission thereof into the vacuum.  
         [0061]    In an additional alternative step, some or all of the diamond surfaces involved in fabrication of the emitter array are chemically modified by a hydrogenation or cesiation or other process. This chemical modification or surface termination can be carried out with or without prior oxidation of the surface. Properly terminated diamond surfaces exhibit low work functions, and a high secondary electron emission coefficient which are both advantageous in a field emitter array.  
         [0062]    Turning to FIG. 2 a,  another embodiment of the invention using doped diamond layers is shown. In this embodiment, doping is used to assist the electron emission and transport process and in particular, a layer  22  of N-doped diamond material is provided. This layer is typically 1 nm or more thick. The layer  22  can be modified by (multiple) ion implantation(s) to create a region  23  with cone shaped patterns with emitter tips and a continuous electrically conducting damage region. A continuous electrically conducting pathway exists between the emitter tip(s) and the electrically conducting layer. At least one electrical connection between the continuous conducting layer and the emitter tips is provided. Electron injection and transport are assisted by doping the diamond layer  22  into which the ions are implanted, or by implanting into an undoped diamond substrate at low enough energy so as to create the emitter tips at or near the diamond surface, followed by growth of a N-doped diamond layer immediately on top of the undoped diamond. This results in a steep, but very narrow and downward band bending region through which the electrons can tunnel into the conduction band of diamond or to the surface. Turning to FIG. 2 b,  a layer of undoped diamond  25  may be below the emitter tips provided there is a continuous, electrically conducting pathway from the contact to the implanted region. For example, such might be accomplished by implantation at sufficient implantation energies that the ions pass through the N-doped layer and into the undoped material underneath.  
         [0063]    In addition, a layer  24  of undoped diamond material can be deposited on the n-doped diamond layer  22 . The undoped layer  24  minimizes carrier scattering while protecting the emitter tips.  
         [0064]    Further, a layer  26  of B-doped diamond material can be deposited on the surface of the undoped diamond layer  24 . The B-doped layer  26  is grown to maximize emission of both primary and secondary electrons from the surface by altering the band-bending. The B-doped layer  26  also provides a pathway for electron replenishment through lateral electron movement on the surface thereof. Accordingly, the electron injection and transport processes are further assisted by the B-doped diamond layer  26 .  
         [0065]    Turning to FIGS. 3 a - 3   d,  a further embodiment of the invention is illustrated. In FIG. 3 a,  implantation is used to create a buried, continuous conducting layer in a diamond substrate  10 . The substrate  10  is damaged by implantation as discussed in connection with previous embodiments to create a subsurface damage area  28 . A photoresist  10   a  can be used during implantation to define the emitter tips . If the photoresist is used, the photoresist can be removed after implantation. The implantations result in a buried continuous damage layer  28 , rather than a damage area of isolated cones with tips as in previous embodiments. As illustrated, only the areas of initial impact are separate from each other. As in previous embodiments, contact  14  is made between the continuous conducting layer and the emitter tips.  
         [0066]    In the next step, shown in FIG. 3 b,  a homoepitaxial layer  10 ′ can be deposited on the surface of the diamond substrate  10  containing the subsurface damage area  28 .  
         [0067]    As shown in FIG. 3 c,  a mask  32  consisting of photoresist , metal, other material or combinations thereof may be placed on the surface of the homoepitaxial layer  10 ′. Ion implantation is carried out and a damage area comprising a series of cones  32  with sharp tips formed in the diamond layer  10 ′ generally as shown in FIG. 1 b.  Implantation is carried out with a low flux of higher energy ions so as to create isolated tips in contact with the continuous damage layer. If a mask is used, the mask can be removed after implantation.  
         [0068]    In the next step, illustrated in FIG. 3 d,  a homoepitaxial layer  18  can be grown over the homoepitaxial layer  10 ′. Gates  16  are deposited on or under the surface of the layer  18 .  
         [0069]    Referring to FIG. 3 e,  at least one electrical connection between the continuous conducting layer and the emitter tips is provided and in this embodiment, a side connection  36  and a bottom connection  38  are shown. Connections can be made on the side or via a hole on the top or bottom of the device, for example by removing the unimplanted diamond  14  to expose the underlying conductive layer. Alternatively, further implantation can be used to create a conductive path from the surface to the buried subsurface conducting layer and emitting tips.  
         [0070]    Although the invention has been described above in relation to a preferred embodiment thereof, it will be readily understood by those skilled in the art that variations and modifications can be effected without departing from the scope and spirit of the invention.