Abstract:
The present invention relates to compounds, containing a central 1,4,5-trisubstituted 1,2,3-triazole core and a reactive appendage appropriate to form covalent “click” bonds on the surface of materials functionalized with reactive groups including: azide, terminal alkyne, cyclooctalkyne, thiol, maleimide or thiolacid groups. These compound are nonpeptide mimetics of RGD (Arg-Gly-Asp) and/or, OGP 10-14  (Tyr-Gly-Phe-Gly-Gly), osteogenic peptides. Also, the present invention relates to a process for the preparation of the compounds containing a 1,4,5-trisubstituted 1,2,3-triazole core. These compounds are particularly useful for medical devices, in particular implants and tissue engineering and cell culture matrices.

Description:
FIELD OF THE INVENTION 
       [0001]    The present invention relates to compounds containing a central 1,4,5-trisubstituted 1,2,3-triazole core and a reactive appendage appropriate to form covalent “click” bonds on the surface of materials functionalized with reactive groups including: azide, terminal alkyne, cyclooctalkyne, thiol, maleimide or thiolacid groups and to a process for the preparation of these compounds containing a 1,4,5-trisubstituted 1,2,3-triazole core. These compounds are nonpeptide mimetics of RGD (Arg-Gly-Asp) and/or, OGP 10-14  (Tyr-Gly-Phe-Gly-Gly), osteogenic compounds. 
         [0002]    These compounds are particularly useful for medical devices, including endosseous implants, or tissue engineering scaffold or cell culture matrix, suitable for the replacement or regeneration of human and animal organs. 
       BACKGROUND OF THE INVENTION 
       [0003]    Some natural short peptides occurring in the extra cellular matrix (ECM) or in serum are useful to enhance the adhesion, viability and proliferation of osteoblast cells. 
         [0004]    RGD occurs in several ECM proteins, including vitronectin, fibronectin and osteopontin. The technological interest in RGD tripeptide analogues in applications related to osteogenesis stems from their ability to regulate the out-in signaling of ECM with integrin receptors in osteoblast cells (Kantlehner M et al. ChemBioChem 2000 1: 107-114 “Surface coating with cyclic RGD peptides stimulates osteoblast adhesion and proliferation as well as bone formation”). Using RGD analogues may be beneficial to regulate bone remodeling by promoting the recruitment, attachment and differentiation of osteoblasts and osteoclasts, as demonstrated for example in osteoporosis therapy (Chen, W. et al in Biotechnol. Lett. 2005 27: 41-48 “Bone loss induced by ovariectomy in rats is prevents by gene transfer of parathyroid hormone or an Arg-Gly-Asp-containing peptide”). 
         [0005]    The osteogenic growth peptide (OGP) is a short naturally occurring 14-mer growth factor peptide found in serum. As a soluble peptide, OGP regulates proliferation, differentiation, and matrix mineralization in osteoblast lineage cells. Studies have demonstrated sensitivity of osteoblast lineage cells to changes in exogenous concentrations of OGP. It has also been shown in the art that only the OGP 10-14  (Tyr-Gly-Phe-Gly-Gly) pentasegment is essential for the osteogenic activity of OGP (Chen, Y.-Ch. et al. J. Med. Chem. 2002 45: 1624-1632 “Bioactive pseudopeptidic analogues and cyclostereoisomers of osteogenic growth peptide C-terminal pentapeptide, OGP 10-14 ”). 
         [0006]    Attaching RGD peptide analogues to the surface of bone or endosseous implants has shown to be beneficial to improve osteoblast cell adhesion (see for example Kessler H et al. Biomaterials 2003 24: 4385-4415 “RGD modified polymers: biomaterials for stimulated cell adhesion and beyond”; see also: Biltresse S. et al. Biomaterials 2005 26: 4576-4587 “Cell adhesive PET membranes by surface grafting of RGD peptidomimetics”). On the other hand, the effectiveness of immobilized OGP to increase osteoblast cell densities and fasten their proliferation rate on OGP-stained materials has been proven “in vitro” (Moore, N. M. et al. Biomaterials 2010 31: 1604-1611 “The use of immobilized osteogenic growth peptide on gradient substrates synthesized via click chemistry to enhance MC3T3-E1 osteoblast proliferation”). 
         [0007]    Natural RGD and OGP peptides, their pseudopeptide cyclic analogues or their amidic surrogates are prone to suffer a fast deactivation by proteolytic cleavage “in vivo”, leading to lowered serum concentrations in systemic applications or inactive surfaces when grafted to biomaterials. Several RGD analogues known in the art may partially overcome this drawback, including some 1,4-disubstituted 1,2,3-triazole compounds (see Trabocchi, A. et al. J. Med. Chem. 2010, 53: 7119-7128 “Click-Chemistry-derived triazole ligands of Arginine-Glycine-Aspartate (RGD) integrins with a broad capacity to inhibit adhesion cells and both in vitro and in vivo angiogenesis” and Ni, M. H. et al Lett. Drug Design &amp; Discovery 2011, 8: 401-405 “Novel RGD peptidomimetics embedding 1,2,3-triazole as central scaffold; synthesis and αvβ3 integrin affinity”). Conversely, some pseudopeptide OGP mimetics are also known in the art (see Bab, I. et al WO9732594A1 “Synthetic peptides and pseudopeptides having osteogenic activity and pharmaceutical compositions containing the same”). 
         [0008]    However, none of these RGD or OGP10-14 nonpeptide mimetics are amenable to embodiments capable to give further “click” attachment to the surface of biomaterials. 
         [0009]    Thus, from what is known in the art, it is derived that the development of a RGD or an OGP10-14 nonpeptide mimetic material capable to attach to the surface of biomaterials is still of great interest. 
       BRIEF SUMMARY OF THE INVENTION 
       [0010]    Inventors have developed 1,4,5-trisubstituted 1,2,3-triazole compounds mimetics of RGD and/or OGP 10-14  that allow to conduct in a single chemical operation the “click” bonding on the surface of a material. The peptidomimetics bound in this way are stable and do not suffer degradation reactions under physiological conditions. 
         [0011]    Therefore an aspect of the invention relates to a 1,4,5-trisubstituted 1,2,3-triazole compound of formula (I): 
         [0000]    
       
                 
         
             
             
         
       
     
         [0000]    wherein:
 
R 1  is a biradical selected from the group consisting of C 1-20  alkylene; in which 0, 1, 2, 3, 4, 5 or 6 —CH 2 — groups are optionally replaced by groups selected from —O—, —S—, —C(O)O—, —C(O)NH—, —C(O)N(C 1-4 alkyl)-, —NHC(O)NH—, —NHC(O)O—;
 
R 2  is a biradical independently selected from the group consisting of: C 1-6  alkylene; in which 0, 1, 2 or 3 —CH 2 — groups are optionally replaced by groups selected from —O— and —S—; optionally substituted with one or more groups selected from C 1-4  alkyl, phenyl, C 6-10  aryl; and
 
R 3  is a biradical selected from the group consisting of: C 1-6  alkylene; optionally containing one or more —C═C— bonds; optionally containing —C≡C— bonds; in which 0, 1, 2 or 3 —CH 2 — groups are optionally replaced by groups selected from —O— and —S—; optionally substituted with one or more groups selected from C 1-4  alkyl, phenyl, —F, —Cl, —OH, —O(C 1-4 alkyl), —S(C 1-4 alkyl), —SO 2 Ph, —CN, —NO 2 , —CO(C 1-4 alkyl), —CO 2 H, —CO 2 (C 1-4 alkyl), —CONH 2 , —CONH(C 1-4 alkyl), —CON(C 1-4 alkyl) 2 ; and
 
X is a group selected from the group consisting of: azide, N-maleimide, N-maleimide-furan cycloadduct, thiol, thio acid, sulfonylazide, ethynyl, iodoethynyl and an activated cyclooctynyl group represented by the formulae:
 
         [0000]    
       
                 
         
             
             
         
       
     
         [0000]    Y is a group selected from the group consisting of: —NHC(═NH)NH 2 , C 6 H 4 —OH
 
Z is a group selected from the group consisting of: —CO 2 H, Ph
 
and
 
when Y is —NHC(═NH)NH 2 , Z is —CO 2 H and when Y is C 6 H 4 —OH, Z is Ph.
 
         [0012]    Another aspect of the invention is a process for preparing the compounds as defined above wherein Z is —CO2H and Y is —NHC(═NH)NH2, which comprises: 
         [0000]    a) reacting an azide of formula Q-(R 1 )—N 3  (II) with an alkyne of formula T-C≡C—(R 2 )—NH-PG (protecting group) (III) to obtain a triazole of formula (IV);
 
b) reacting a triazole of the formula (IV) with a compound of formula S—(R 3 )—CO 2 R a  (V) or an alkene of formula H 2 C═CH—CO 2 R a  (VI), to provide a compound of formula (VII);
 
c) replacing the Q group in the compounds of formula (VII) by a group X to obtain a compound of formula VIII; and d) removing the protecting group (PG) in compounds of the formula (VIII) and e) reacting the intermediate amines with H 2 NC(═NH)SO 3 H.
 
         [0000]    
       
                 
         
             
             
         
       
     
         [0000]    wherein:
 
R 1 , R 2 , R 3  and X are as defined above; R a  is H, methyl, ethyl, tert-butyl or benzyl; T is H or I; Q is HO, methanesulfonyloxy, p-toluenesulfonyloxy, 2-nitrobenzenesulfonyloxy, 4-nitrobenzenesulfonyloxy, trifluoromethanesufonyloxy, Cl, Br or I; PG is H, tert-butoxycarbonyl, allyloxycarbonyl or benzyloxycarbonyl; S in step b) is B(OH) 2 , methanesulfonyloxy, p-toluenesulfonyloxy, 2-nitrobenzenesulfonyloxy, 4-nitrobenzenesulfonyloxy, trifluoromethanesufonyloxy, Cl, Br or I.
 
         [0013]    Another aspect of the invention is a process for preparing the compound as defined above wherein, Y is C 6 H 4 —OH and Z is Ph, which comprises: 
         [0000]    a) reacting an azide of formula Q-(R 1 )—N 3  (II) with an alkyne of formula T-C≡C—(R 2 )—(C 6 H 4 OH)—PG (IX) to obtain a triazole of formula (X),
 
b) reacting a triazole of the formula (X) with a compound of formula S—(R 3 )-Ph (XI), to provide a compound of formula (XII),
 
c) replacing the Q group in the compounds of formula (XII) by a group X, and
 
d) removing the protecting group PG.
 
         [0000]    
       
                 
         
             
             
         
       
     
         [0000]    wherein:
 
R 1 , R 2 , R 3  and X are as defined above; T is H or I; Q is HO, methanesulfonyloxy, p-toluenesulfonyloxy, 2-nitrobenzenesulfonyloxy, 4-nitrobenzenesulfonyloxy, trifluoromethanesufonyloxy, Cl, Br or I; PG is H, tert-butoxycarbonyl, allyloxycarbonyl or benzyloxycarbonyl; S in step b) is B(OH) 2 ; PG is Si(i-Pr) 3 .
 
         [0014]    The appendage group X of the compound is useful to bind to different materials when their surface is functionalized with reactive groups such as azide, sulfonylazide, terminal alkyne, terminal iodoalkyne, cycloalkyne, N-maleimide, N-maleimide-furan cycloadduct, thiol or thio acid. As a result of such reactions, a material-W-peptidomimetic adduct is formed, which contains at least one of such W groups: 
         [0000]    
       
                 
         
             
             
         
       
     
         [0015]    Therefore another aspect of the invention relates to a material with the surface chemically modified wherein the X group of the 1,4,5-trisubstituted 1,2,3-triazole according to the 1,4,5-trisubstituted 1,2,3-triazole compound of formula (I) as defined above is replaced by a W the group as defined above. 
         [0016]    The compounds of the invention are mimetics of RGD and/or OGP 10-14 . Among them, (Arg-Gly-Asp) tripeptide and OGP 10-14  (Tyr-Gly-Phe-Gly-Gly) pentapeptide have potential interest for “in vitro” tissue engineering and diagnosis technologies, or to improve the osteogenic properties of implants in human and animal therapy “in vivo”. 
         [0017]    Thus another aspect of the invention relates to a medical device, made from the material described above. It can preferentially be an endosseous implant, or tissue engineering scaffold or cell culture matrices. 
     
    
     
       BRIEF DESCRIPTION OF THE DRAWINGS 
         [0018]      FIG. 1  shows the X-ray photoelectron spectroscopy (XPS) spectrum (with three spectra magnifications of C1s, N1s and O1s peaks,  FIGS. 2-4 ) for a compact PEEK sample modified at the surface with a mixture of RGD and OGP mimetics, as described in example 18. 
           [0019]      FIG. 2  shows a  FIG. 1  spectrum magnification of C1s peak. 
           [0020]      FIG. 3  shows a  FIG. 1  spectrum magnification of N1s peak. 
           [0021]      FIG. 4  shows a  FIG. 1  spectrum magnification of O1s peak. 
       
    
    
     DETAILED DESCRIPTION OF THE INVENTION 
       [0022]    As mentioned above, an aspect of the present invention relates to 1,4,5-trisubstituted 1,2,3-triazole compounds of formula (I) as defined above. 
         [0023]    As used herein, the term “alkyl” includes both saturated straight chain and branched hydrocarbon substituents. Preferably, C 1-20  alkyl groups, more preferably C 1-6  alkyl groups. Particularly preferred alkyl groups include, for example, methyl, ethyl, propyl, isopropyl, butyl, isobutyl, tert-butyl, pentyl and hexyl. 
         [0024]    As used herein, the term “alkylene” includes biradical hydrocarbon saturated straight chains and branched chains attaching simultaneously two molecular fragments or functional groups. Preferably, C 1-20  alkylene groups, more preferably C 1-6  alkylene groups. Particularly preferred alkylene groups include, for example, methylene, ethylene, propylene and butylene. 
         [0025]    As used herein, the term “aryl” includes substituted or unsubstituted single-ring aromatic groups in which each atom of the ring is carbon. Preferably the ring is a 5- to 7-membered ring, more preferably a 6-membered ring. 
         [0026]    In a preferred embodiment R 1  is selected from the group consisting of —(CH 2 CH 2 O)rCH 2 CH 2 —; where r is an integer between 0 and 8, R 2  is selected from the group consisting of —CH 2 OCH 2 CH 2 — or —CH 2 OCH 2 —, and R 3  is selected from the group consisting of —CH 2 CH 2 — or —CH═CH—. 
         [0027]    Particularly in the compound of formula (I), Y is —NHC(═NH)NH 2  and Z is —CO 2 H. In other particular embodiment, Y is C 6 H 4 —OH and Z is Ph. Preferably Y is p-C 6 H 4 —OH and Z is Ph. 
         [0028]    Other aspect of the invention relates to a material with the surface chemically modified wherein the X group of the 1,4,5-trisubstituted 1,2,3-triazole compound according to the 1,4,5-trisubstituted 1,2,3-triazole of formula (I) as defined above is replaced by a W group as defined above. Preferably the material with the surface chemically modified wherein in the 1,4,5-trisubstituted 1,2,3-triazole compound Y is —NHC(═NH)NH 2  and Z is —CO 2 H. Preferably the surface chemically modified wherein in the 1,4,5-trisubstituted 1,2,3-triazole compound Y is p-C 6 H 4 —OH and Z is Ph. 
         [0029]    In a preferred embodiment the material is metals, metallic alloys, polymers, ceramics or composites. In particular, those materials that comply with the ISO 10993 standards for evaluating the biocompatibility. Examples of materials are; Ti, Ti alloys, polyethylene, polypropylene, PET, polyamide, polyester, polyurethanes, silicones or PAEK. More preferably the material is PAEK. 
         [0030]    Finally the invention refers to a medical device wherein the device is made from the material as defined above. 
         [0031]    As used herein the term “medical device” means any instrument, apparatus, appliance, material or other article, whether used alone or in combination, intended to be used for the purpose of:
       diagnosis, prevention, monitoring, treatment or alleviation of
 
disease,
   diagnosis, monitoring, treatment, alleviation of or compensation
 
for an injury or handicap,
   investigation, replacement or modification of the anatomy or of
 
a physiological process.
       
 
         [0035]    As used herein the term “medical device” includes stents, stent grafts, catheters, guide wires, balloons, filters (e.g., vena cava filters), vascular grafts, intraluminal paving systems, pacemakers, electrodes, leads, defibrillators, joint and bone implants, spinal implants, access ports, intra-aortic balloon pumps, heart valves, sutures, artificial hearts, neurological stimulators, cochlear implants, retinal implants, and other devices that can be used in connection with therapeutic coatings, prosthetic bone implant, endooseous implant, scaffold for bone tissue regeneration. Such medical devices are implanted or otherwise used in body structures, cavities, or lumens such as the vasculature, gastrointestinal tract, abdomen, peritoneum, airways, esophagus, trachea, colon, rectum, biliary tract, urinary tract, prostate, brain, spine, lung, liver, heart, skeletal muscle, kidney, bladder, intestines, stomach, pancreas, ovary, uterus, cartilage, eye, bone, joints, and the like. Preferably medical device is an implant or cell culture matrix. More preferably endooseous implant or tissue engineering scaffold or cell culture matrices. 
         [0036]    In a preferred embodiment the invention refers a medical device wherein the medical device is an endosseous implant, or tissue engineering scaffold or cell culture matrix, suitable for the replacement of human and animal organs. 
         [0037]    Acronyms of reagents, solvents or techniques used are defined as follows: 
         [0000]    Boc: tert-Butoxycarbonylamino group,
 
Dansyl: 5-(Dimethylamino)naphthalene-1-sulfonyl group,
 
       DIPEA: Diisopropyletylamine, 
     DMF: N,N-Dimethylformamide, 
     NBS: N-Bromosuccinimide, 
     NMR: Nuclear Magnetic Resonance, 
       [0038]    OGP: Osteogenic Growth Peptide. For the purpose of this invention refers to structures of formula (I), wherein Y is p-C 6 H 4 —OH and Z is Ph.
 
PEEK: Poly-ether ether ketone,
 
RGD: Arginine-Glycine-Aspartic acid. For the purpose of this invention refers to structures of formula (I), wherein Y is —NHC(═NH)NH 2  and Z is —CO 2 H
 
       THF: Tetrahydrofuran, 
     TLC: Thin Layer Chromatography. 
       [0039]    The following examples are provided for illustrative means, and are not meant to be limiting of the present invention. 
       Example 1 
     Compound (IV): R 1 =—CH 2 CH 2 —; R 2 =—CH 2 OCH 2 CH 2 —; Q=OH; PG=Boc; T=I 
     4-(4-tert-Butoxycarbonylamino-2-oxa-butyl)-1-(2-hydroxyethyl)-5-iodo-1,2,3-triazole 
       [0040]    To a stirred solution of CuI (218 mg, 1.15 mmol) in dried CH 3 CN, NBS (223 mg, 1.25 mmol), 2-(tert-butoxycarbonylamino)ethyl propargyl ether (208 mg, 1.04 mmol), 2-azidoethanol (100 mg, 1.15 mmol) and DIPEA (200 μl, 1.15 mmol) were added. The mixture was stirred at room temperature for two hours. The solvent was evaporated, the residue was dissolved in CH 2 Cl 2 , washed with 10% aqueous Na 2 S 2 O 3  and the organic phase was dried (MgSO 4 ) and evaporated. The product was purified by column chromatography (silica gel; EtOAc/hexanes 1:1). Yield: 300 mg (70%). 1H NMR (500 MHz, CDCl 3 ) δ 4.63 (s, 2H), 4.54-4.48 (t, J=4.9, 2H), 4.18 (t, J=5.0, 2H), 3.62 (t, J=5.1, 2H), 3.34 (t, J=5.0, 2H), 1.46 (s, 9H). 
       Example 2 
     Compound (VII): R 1 =R 3 =—CH 2 CH 2 —; R 2 =—CH 2 OCH 2 CH 2 —; R a =CH 3 ; Q=OH; PG=Boc 
     4-(4-tert-Butoxycarbonylamino-2-oxa-butyl)-1-(2-hydroxyethyl)-5-(2-methoxycarbonyl-ethyl)-1,2,3-triazole 
       [0041]    A suspension of 4-(4-tert-butoxycarbonylamino-2-oxa-butyl)-1-(2-hydroxyethyl)-5-iodo-1,2,3-triazole (500 mg, 1.21 mmol), Pd(OAc) 2  (27.2 mg, 0.121 mmol) and NaHCO 3  (254.7 mg, 3.03 mmol) in anhydrous DMF (5 mL) was prepared in a flame-dried flask under nitrogen atmosphere. Methyl acrylate (273.1 μL, 3.03 mmol) was added and the mixture was stirred at 85° C. overnight. The solvent was evaporated and the product was purified by column chromatography (silica gel, EtOAc/hexanes 1:1). This intermediate product (355 mg, 0.96 mmol) was dissolved in dry MeOH and ammonium formate (302.2 mg, 4.8 mmol) and 10%-Pd—C (107.8 mg, 0.096 mmol) were added. The mixture was refluxed overnight. The product was purified by filtration over celite. Yield: 330 mg (74%).  1 H NMR (500 MHz, CDCl 3 ): δ 4.55 (s, 2H), 4.40 (t, J=4.7, 2H), 4.06 (t, J=4.7, 2H), 3.64 (s, 3H), 3.54 (t, J=5.1, 2H), 3.26 (s, 2H), 3.05 (t, J=7.3, 2H), 2.68 (t, J=7.4, 2H), 1.41 (s, 9H). 
       Example 3 
     Compound (VIII): R 1 =R 3 =—CH 2 CH 2 —; R 2 =—CH 2 OCH 2 CH 2 —; R a =CH 3 ; X=N3; PG=Boc 
     1-(2-Azidoethyl)-4-(4-tert-butoxycarbonylamino-2-oxa-butyl)-5-(2-carboxyethyl)-1,2,3-triazole 
       [0042]    To a stirred solution of 4-(4-tert-butoxycarbonylamino-2-oxa-butyl)-1-(2-hydroxyethyl)-5-(2-methoxycarbonylethyl)-1,2,3-triazole (135 mg, 0.36 mmol) prepared in Example 2, cooled to 0° C. in dried CH 2 Cl 2  was added triphenyl phosphine (190.2 mg, 0.73 mmol) and NBS (129.0 mg, 0.73 mmol). The mixture was stirred over one hour. The solvent was evaporated and the crude product was dissolved in dried DMF. Then, NaN 3  (94.3 mg, 1.45 mmol) and NaI (54.3 mg, 0.36 mmol) were added and the mixture was stirred at room temperature over 48 hours. After evaporation of the solvent, the crude product was dissolved in THF/H 2 O (1:1) and LiOH.H 2 O (151.9 mg, 3.62 mmol) was added and the mixture was stirred for 8 hours. Then, the solvent was evaporated and the product was purified by acid and basic extraction with CH 2 Cl 2 . Yield: 143.9 mg (70%).  1 H NMR (500 MHz, CD 3 OD) δ 4.64 (s, 2H), 4.57 (t, J=5.5, 2H), 3.88 (t, J=5.5, 2H), 3.54 (t, J=5.5, 2H), 3.25 (t, J=5.3, 2H), 3.12 (t, J=7.3, 2H), 2.73 (t, J=7.2, 2H), 1.45 (s, 9H). 
       Example 4 
     Compound (VIII): R 1 =—[CH 2 CH 2 O] 3 CH 2 CH 2 HN(CO)OCH 2 CH 2 —; R 2 =—CH 2 OCH 2 CH 2 —; R 3 =—CH 2 CH 2 —; R a =CH 3 ; X=N 3 ; PG=Boc 
     1-(16-Azido-5-aza-3,8,11,14-tetraoxa-4-oxohexadecyl)-4-(4-tert-butoxycarbonylamino-2-oxa-butyl)-5-(2-methoxycarbonylethyl)-1,2,3-triazole 
       [0043]    In a flame-dried flask, 4-(4-tert-butoxycarbonylamino-2-oxa-butyl)-1-(2-hydroxyethyl)-5-(2-methoxycarbonyl-ethyl)-1,2,3-triazole (0.27 mmol, 100 mg), prepared as described in Example 2, was dissolved in dry THF (2 mL) under nitrogen atmosphere and after addition of DIPEA (0.54 mmol, 96 μL), the mixture was cooled to 0° C. Subsequently, a solution of triphosgene (0.17 mmol, 49 mg) was added dropwise and then the mixture was allowed to reach the room temperature during 30 min. The suspension was filtered through a celite pad and the solvent was evaporated under pressure to obtain the intermediate chloroformate, which was immediately dissolved in dry CH 2 Cl 2  (2 mL). DIPEA (0.54 mmol, 93 μL) and 8-azido-3,6-dioxaoctylamine (0.27 mmol, 60 mg) were added and the mixture was kept stirring overnight. The product was purified by column chromatography using CH 2 Cl 2 /MeOH 90/10 as eluent. Yield: 85 mg (51%). IR (cm −1 ): 3339, 2869, 2102 (N 3 ), 1704 (C═O), 1522 (tri). 1H NMR (500 MHz, CDCl 3 ) δ 4.61 (s, 2H, OCH 2 C═C tri ), 4.56 (t, J=5.1, 2H, N 1tri CH 2 CH 2 ), 4.49 (t, J=5.0, 2H, N 1tri CH 2 CH 2 ), 3.67 (s, 3H, COOCH 3 ), 3.67-3.51 (m, 14H, OCH 2 CH 2 NHBoc and OCH 2 CH 2 O), 3.40-3.28 (m, 6H, OCH 2 CH 2 NHBoc, OCH 2 CH 2 NHCOO and OCH 2 CH 2 N 3 ), 3.04 (t, J=7.6, 2H, CH 2 CH 2 CO 2 CH 3 ), 2.70 (t, J=7.2, 2H, CH 2 CH 2 CO 2 CH 3 ), 1.43 (s, 9H, tBu). 
       Example 5 
     Compound (I): R 1 =R 3 =—CH 2 CH 2 —; R 2 =—CH 2 OCH 2 CH 2 —; X=N 3 ; Y=—NHC(═NH)NH 2 ; Z=CO 2 H 
     1-(2-Azidoethyl)-5-(2-carboxyethyl)-4-(4-N-guanidyl-2-oxa-butyl)-1,2,3-triazole 
       [0044]    A 6M HCl solution in dioxane (2 mL, 12 mmol) was added to 1-(2-azidoethyl)-4-(4-tert-butoxycarbonylamino-2-oxa-butyl)-5-(2-carboxyethyl)-1,2,3-triazole (80 mg, 0.21 mmol) and the mixture was stirred at room temperature over 1 h. Then, the solvent was evaporated, the crude amine hydrochloride was dissolved in methanol (5 mL) and sodium bicarbonate was added until pH=7. Amino(imino)methanesulfonic acid (31.0 mg, 0.25 mmol) was added, the mixture was stirred at room temperature over 1 h. and it was evaporated to dryness. The residue was extracted with MeOH (3×5 mL) and the solution was evaporated at reduced pressure. Yield (90%).  1 H NMR (500 MHz, D 2 O): δ 4.62 (s, 1H), 4.46 (t, J=5.0, 1H), 3.97 (t, J=5.0, 1H), 3.68 (t, J=4.8, 1H), 3.38-3.33 (m, 1H), 3.00 (t, J=7.6, 1H), 2.43 (t, J=7.6, 1H). 
       Example 6 
     Compound (I): R 1 =—[CH 2 CH 2 O] 3 CH 2 CH 2 HN(CO)OCH 2 CH 2 —; R 2 =—CH 2 OCH 2 CH 2 —; R 3 =—CH 2 CH 2 —; X=N 3  Y=—NHC(═NH)NH 2 ; Z=CO 2 H 
     1-(16-Azido-5-aza-3,8,11,14-tetraoxa-4-oxohexadecyl)-5-(2-carboxyethyl)-4-(4-N-guanidyl-2-oxa-butyl)-1,2,3-triazole 
       [0045]    A 4M HCl solution in dioxane (2 mL, 8 mmol) was added to 1-(16-azido-5-aza-3,8,11,14-tetraoxa-4-oxohexadecyl)-4-(4-tert-butoxycarbonylamino-2-oxa-butyl)-5-(2-methoxycarbonylethyl)-1,2,3-triazole (75 mg, 0.14 mmol) and the mixture was stirred at room temperature over 2 h. Then, the solvent was evaporated, the crude amine hydrochloride (45 mg, 0.08 mmol) was dissolved in methanol (5 mL) and potassium carbonate was added until slightly basic pH. Amino(imino)methanesulfonic acid (11 mg, 0.09 mmol) was added, the mixture was stirred at room temperature over 1 h. Lithium hydroxide (4.0 mg, 0.09 mmol) was added and the solution was stirred for 4 h. Upon completion, the solids were filtered off with MeOH (3×5 mL), the solution was evaporated at reduced pressure and the resulting crude product was purified by preparative reverse phase HPLC (C18 column, MeCN:H 2 O 80:20). Yield (75%).  1 H NMR (500 MHz, D 2 O) δ 4.63 (m, 4H, OCH 2 C═C tri  and N 1tri CH 2 CH 2 ), 4.46 (m, 2H, N 1tri CH 2 CH 2 ), 3.70-3.60 (m, 12H), 3.50 (m, 2H, OCH 2 CH 2 NHCOO), 3.44 (t, J=4.2, 2H, OCH 2 CH 2 N 3 ), 3.36 (t, J=4.7, 2H, OCH 2 CH 2 NHCOO), 3.18 (m, 2H, CH 2 CH 2  guanidine), 3.02 (t, J=7.4, 2H, CH 2 CH 2 CO 2 H), 2.45 (t, J=7.5, 2H, CH 2 CH 2 CO 2 H). 
       Example 7 
     Compound (X): R 1 =—CH 2 CH 2 —; R 2 =—CH 2 OCH 2 —; Q=OH; T=I; PG=Si( i Pr) 3    
     1-(2-Hydroxyethyl)-5-iodo-4-[2-oxa-3-(4-triisopropylsilyloxyphenyl)-propyl]-1,2,3-triazole 
       [0046]    To a stirred solution of CuI (401 mg, 2.11 mmol) in dried CH 3 CN, NBS (409 mg, 2.30 mmol), 4-triisopropylsilyloxy-benzyl propargyl ether (610 mg, 1.92 mmol), 2-azidoethanol (100 mg, 1.15 mmol) and DIPEA (367 μl, 2.11 mmol) were added. The mixture was stirred at room temperature for two hours. The solvent was evaporated, the residue was dissolved in CH 2 Cl 2 , washed with 10% aqueous Na 2 S 2 O 3  and the organic phase was dried (MgSO 4 ) and evaporated. The product was purified by column chromatography (silica gel; EtOAc/hexanes 1:1). Yield: 315 mg (31%).  1 H NMR (500 MHz, CDCl 3 ) δ 7.26 (d, J=8.0, 2H), 6.88 (d, J=8.1, 2H), 4.61 (s, 2H), 4.54 (s, 2H), 4.49 (t, J=4.2, 2H), 4.17 (d, J=3.3, 2H), 1.33-1.23 (m, 3H), 1.12 (ds, 18H). 
       Example 8 
     Compound (XII): R 1 =—CH 2 CH 2 —; R 2 =—CH 2 OCH 2 —; R 3 =—CH═CH—; Q=OH; PG=Si( i Pr) 3    
     1-(2-Hydroxyethyl)-5-[(E)-(2-phenyl)vinyl]-4-[2-oxa-3-(4-triisopropylsilyloxyphenyl)-propyl]-1,2,3-triazole 
       [0047]    A suspension of 1-(2-hydroxyethyl)-5-iodo-4-[2-oxa-3-(4-triisopropylsilyloxyphenyl)-propyl]-1,2,3-triazole (270 mg, 0.52 mmol) prepared in Example 7, E-2-phenylvinylboronic acid (119.8 mg, 0.79 mmol), bis(triphenylphosphine) palladium (II) dichloride (14.7 mg, 0.02 mmol) and potassium hydroxide (58.8 mg, 1.05 mmol) were dissolved in anhydrous THF (4 mL) and kept at 75° C. during 2 h. The product was purified by column chromatography (silica gel, EtOAc/hexanes 1:1). Yield: 330 mg (92%).  1 H NMR (500 MHz, CDCl 3 ) δ 7.49 (d, J=7.2, 2H), 7.41 (t, J=7.3, 2H), 7.39-7.34 (m, 1H), 7.31 (d, J=13.2, 1H), 7.26 (d, J=8.4, 2H), 6.98 (d, J=16.3, 1H), 6.86 (d, J=8.4, 2H), 4.72 (s, 2H), 4.58 (s, 2H), 4.51-4.46 (m, 2H), 4.18 (dd, J=10.2, 5.4, 2H), 1.32-1.22 (m, 3H), 1.11 (d, J=7.4, 18H). 
       Example 9 
     Compound (XII): R 1 =—[CH 2 CH 2 O] 3 CH 2 CH 2 HN(CO)OCH 2 CH 2 —; R 2 =—CH 2 OCH 2 —; R 3 =—CH═CH—; Q=N 3 ; PG=Si( i Pr) 3    
     1-(16-Azido-5-aza-3,8,11,14-tetraoxa-4-oxohexadecyl)-5-[(E)-(2-phenyl)vinyl]-4-[2-oxa-3-(4-triisopropylsilyloxyphenyl)-propyl]-1,2,3-triazole 
       [0048]    In a flame-dried flask, 1-(2-hydroxyethyl)-5-[(E)-(2-phenyl)vinyl]-4-[2-oxa-3-(4-triisopropylsilyloxyphenyl)-propyl]-1,2,3-triazole (0.20 mmol, 100 mg) prepared as shown in Example 7, was dissolved in dry THF (1.5 mL) under nitrogen atmosphere and after addition of DIPEA (0.39 mmol, 69 μL), the mixture was cooled to 0° C. Subsequently, a solution of triphosgene (0.12 mmol, 36 mg) was added dropwise and then the mixture was allowed to reach the room temperature during 30 minutes. The suspension was filtered through a celite pad and the solvent was evaporated under pressure to obtain the intermediate chloroformate [ 1 H NMR (500 MHz, CDCl 3 ) δ 7.50 (d, J=7.3, 2H), 7.45-7.35 (m, 4H), 7.26 (d, J=8.0, 2H), 6.92 (d, J=16.4, 1H), 6.86 (d, J=7.9, 2H), 4.80-4.70 (m, 6H), 4.59 (s, 2H), 1.31-1.21 (m, 3H), 1.11 (d, J=7.3, 18H)]. The product was dissolved in dry CH 2 Cl 2  (1.5 mL) and sequentially DIPEA (0.39 mmol, 69 μL) and tetraethylene glycol (0.20 mmol, 43 mg) were added and the mixture was kept stirring overnight. The product was purified by column chromatography using CH 2 Cl 2 /MeOH 90/10 as eluent. Yield: 116 mg (78%). IR (cm −1 ): 2944, 2866, 2102 (N 3 ), 1720 (C═O), 1509.  1 H NMR (500 MHz, CDCl 3 ) δ 7.47 (d, J=7.7, 2H), 7.42-7.21 (m, 6H), 6.92 (d, J=16.3, 1H), 6.85 (d, J=8.0, 2H), 4.72 (s, 2H), 4.64 (t, J=4.8, 2H), 4.57 (s, 2H), 4.48 (s, 2H), 3.69-3.49 (m, 11H), 3.45-3.41 (m, 2H), 3.39-3.32 (m, 2H), 3.28 (t, J=10.9, 2H), 1.30-1.19 (m, 3H), 1.09 (d, J=7.4, 18H). 
       Example 10 
     Compound (I): R 1 =—CH 2 CH 2 —; R 2 =—CH 2 OCH 2 —; R 3 =—CH═CH—; X=N 3 ; Y=p-C 6 H 4 OH; Z=Ph 
     1-(2-Azidoethyl)-5-[(E)-(2-phenyl)vinyl]-4-[2-oxa-3-(4-triisopropylsilyloxyphenyl)-propyl]-1,2,3-triazole 
       [0049]    In a dried flask cyanuric chloride (55.93 mg, 0.30 mmol) and DMF (61.06 μL) were warmed at 25° C. for 10 min. After the formation of a white solid, CH 2 Cl 2  (0.5 mL) was added, followed by 1-(2-hydroxyethyl)-5-[(E)-(2-phenyl)vinyl]-4-[2-oxa-3-(4-triisopropylsilyloxyphenyl)-propyl]-1,2,3-triazole (70 mg, 0.14 mmol). The mixture was kept at room temperature during one hour and the solvent was evaporated. The resulting crude product was dissolved again in acetone, sodium azide (89.71 mg, 1.38 mmol) was added and the mixture was stirred for 24 hours. Then, cesium fluoride (300 mg, 2.0 mmol) was added, and the resulting crude was evaporated and purified by column chromatography (silica gel, EtOAc/hexanes 1:1).  1 H NMR (500 MHz, CDCl 3 ) δ 7.50 (d, J=7.2, 2H), 7.47-7.33 (m, 4H), 7.33-7.25 (m, 3H), 6.95 (d, J=16.3, 1H), 6.87 (d, J=8.2, 2H), 4.75 (s, 2H), 4.71 (t, J=6.4, 2H), 4.60 (s, 2H), 4.01 (t, J=6.4, 2H). 
       Example 11 
     Compound (I): R 1 =—[CH 2 CH 2 O] 3 CH 2 CH 2 HN(CO)OCH 2 CH 2 —; R 2 =—CH 2 OCH 2 —; R 3 =—CH═CH—; X=N 3 ; Y=p-C 6 H 4 OH; Z=Ph 
     1-(16-Azido-5-aza-3,8,11,14-tetraoxa-4-oxohexadecyl)-5-[(E)-(2-phenyl)vinyl]-4-[2-oxa-3-(4-hydroxyphenyl)-propyl]-1,2,3-triazole 
       [0050]    A suspension of 1-(16-azido-5-aza-3,8,11,14-tetraoxa-4-oxohexadecyl)-5-[(E)-(2-phenyl)vinyl]-4-[2-oxa-3-(4-triisopropylsilyloxyphenyl)-propyl]-1,2,3-triazole (0.14 mmol, 105 mg) prepared in Example 9, and cesium fluoride (0.70 mmol, 106 mg) in methanol (1.5 mL) was stirred at room temperature for one hour. Then the solvent was evaporated and the product was purified by column chromatography using CH 2 Cl 2 /MeOH 95:5 as eluent. Yield: 50 mg (60%). IR(cm −1 ): 3328, 2867, 2101 (N 3 ), 1705 (C═O), 1517.  1 H NMR (500 MHz, CDCl 3 ) δ 7.47 (d, J=7.4, 2H), 7.44-7.25 (m, 5H), 7.20 (dd, J=17.2, 8.0, 2H), 6.86 (d, J=16.6, 1H), 6.80 (d, J=8.1, 2H), 4.75 (s, 2H), 4.64 (d, J=4.8, 2H), 4.57 (s, 2H), 4.47 (s, 2H), 3.58 (ddd, J=35.4, 14.6, 6.2, 10H), 3.39-3.35 (m, 2H), 3.35-3.27 (m, 2H), 3.21 (d, J=4.8, 2H). 
       Example 12 
     Poly(Etheretherketone) PEEK with the Surface Modified as Cycloalkyne. Material According to Formula [PEEK]=N—O—(R 4 )—X, Wherein: R 1 =—CH 2 CH 2 OCH 2 CH 2 O—; X=cyclooctyn-3-yl 
       [0051]    Compact PEEK consisted of mechanically polished PEEK-1000 semicrystalline 20×20×5 mm size square samples from Ketron (KETRON PEEK 1000, ref. 41300000, PoliFluor S.L) and medical grade implantable PEEK CLASSIX LSG compact disk samples from Invibio (PoliFluor S.L). 
         [0052]    Porous PEEK consisted of disk samples (9 mm diameter/3 mm thin), prepared according to patent EP10382243.3 (Porous PEEK article as an implant) with VESTAKEEP® 2000 P. 
         [0053]    Compact PEEK and porous PEEK materials with the surface modified as oxime [PEEK]=N—OH were prepared following a procedure described in  Macromolecules,  1991, 24: 3045-3049. 
         [0054]    PEEK oxime: Both compact and porous PEEK samples were cleaned by immersion in an ultrasonic bath with methanol for 30 min and subsequently dried at room temperature under reduced pressure overnight. Each set of 10 samples of porous and compact PEEK, 3.0 g of hydroxylamine hydrochloride, 10 mL of ethanol, and 2 mL water were introduced to a round-bottomed flask. Sodium hydroxide (5.5 g) was added in five portions, shaking after each addition. The balloon flask was purged with nitrogen, then heated at 40° C. for 24 h, and finally refluxed for 24 h. After cooling the suspension, the samples were extracted, rinsed successively with 10% aqueous HCl (5×30 mL) and ethanol (3×30 mL), and dried at room temperature. 
         [0055]    3-(6-Iodo-1,3-dioxahexyl)-cyclooctyne: To a solution of O-(cyclooctyn-3-yl)-diethylene glycol (100 mg, 0.47 mmol) in anhydrous DMF (10 mL) was added (PhO) 3 PMeI (0.43 g, 0.94 mmol). The resulting solution was stirred at r.t. for 30 min. Then, MeOH (1 mL) was added the mixture was evaporated at reduced pressure. The crude obtained was used without additional purification. Yield: 103.2 mg, (65%).  1 H-NMR (500 MHz, CDCl 3 ): δ 4.24 (t, 1H, —CH—C≡C—), 3.77-3.67 (m, 5H, O—CH 2 ), 3.53 (m, 1H, —CH—O), 1.91 (t, 2H, CH 2 —I), 2.25-1.45 (m, 10H, —CH 2 —). 
         [0056]    Compact and porous PEEK oxime samples (n=2), prepared as above, were introduced under nitrogen atmosphere into a test tube containing a mixture of potassium carbonate (0.41 g), 3-(6-Iodo-1,3-dioxahexyl)-cyclooctyne (0.20 g) and acetone (2 mL). The suspension was stirred at 40° C. for 24 h., and the samples were washed repeatedly with water and methanol. Finally, the samples were dried at r.t. under vacuum for 5 h. 
         [0057]    Surface characterization data for compact PEEK modified as cycloalkyne. XPS analysis: C 83.3%, O 14.8%, N 1.9%. 
         [0058]    Surface characterization data for porous PEEK modified as cycloalkyne. Contact angle: 139.2°±18.0. XPS analysis: C 81.8%, O 17.2%, N 1.0%. 
         [0000]    
       
                 
         
             
             
         
       
     
       Example 13 
     Porous PEEK with the Surface Modified as RGD Mimetic. Material (XIII): R 1 =R 3 =—CH 2 CH 2 —; R 2 =—CH 2 OCH 2 CH 2 —; R 4 =—CH 2 CH 2 OCH 2 CH 2 O—; W=4,5-bicyclooctene-1,2,3-triazole 
       [0059]    Porous PEEK oxime samples (n=2) functionalized as cycloalkyne as described in Example 12, were introduced under nitrogen atmosphere into a test tube containing a 2 mL of a THF/H 2 O 1:1 mixture. Then, 0.2 mg of compound of formula (I): (R 1 =R 3 =—CH 2 CH 2 —; R 2 =—CH 2 OCH 2 CH 2 —; X=N 3 ; Y=—NHC(═NH)NH 2 ; Z=CO 2 H), prepared in Example 5, were added and the suspension was stirred at 40° C. for 24 h. The sample was washed repeatedly with a solution of HCl 0.1M, an aqueous solution of NH 3  (pH=11), water and methanol and dried at room temperature under vacuum for 5 h. 
         [0060]    Surface XPS analysis for porous PEEK modified with RGD mimetic: C 79.4%, O 18.7%, N 1.9%). 
       Example 14 
     Compact PEEK with the Surface Modified as RGD Mimetic. Material (XIII): R 1 =R 3 =—CH 2 CH 2 —; R 2 =—CH 2 OCH 2 CH 2 —; R 4 =—CH 2 CH 2 OCH 2 CH 2 O—; W=4,5-bicyclooctene-1,2,3-triazole 
       [0061]    Compact PEEK-M oxime samples (n=2) functionalized as cycloalkyne as described in Example 12, was reacted with 0.2 mg of RGD mimetic of formula (I): (R 1 =R 3 =—CH 2 CH 2 —; R 2 =—CH 2 OCH 2 CH 2 —; X=N 3 ; Y=—NHC(═NH)NH 2 ; Z=CO 2 H). Reaction conditions and purification were identical to the Example 13. 
         [0062]    Surface characterization data for polished compact PEEK modified with RGD mimetic. XPS analysis: C 84.4%, O 13.3%, N 2.3%. 
       Example 15 
     Compact PEEK-M with the Surface Modified as RGD Mimetic. Material (XIII): R 1 =R 3 =—CH 2 CH 2 —; R 2 =—CH 2 OCH 2 CH 2 —; R 4 =—[CH 2 CH 2 O] 3 CH 2 CH 2 HN(CO)OCH 2 CH 2 —; W=4,5-bicyclooctene-1,2,3-triazole 
       [0063]    Compact PEEK oxime samples (n=2) functionalized as cycloalkyne as described in Example 12, was reacted with 0.2 mg of RGD mimetic of formula (I): (R=—[CH 2 CH 2 O] 3 CH 2 CH 2 HN(CO)OCH 2 CH 2 —; R 2 =—CH 2 OCH 2 CH 2 —; R 3 =—CH 2 CH 2 —; X=N 3 ; Y=—NHC(═NH)NH 2 ; Z=CO 2 H prepared as described in Example 6). Reaction conditions and purification were identical to the Example 13. 
         [0064]    Surface characterization data for polished compact PEEK modified with RGD mimetic. XPS analysis: C 82.2%, O 14.6%, N 3.2%. 
         [0000]    
       
                 
         
             
             
         
       
     
       Example 16 
     Compact PEEK with the Surface Modified as OGP Mimetic. Material (XIV): R 1 =—CH 2 CH 2 —; R 2 =—CH 2 OCH 2 —; R 3 =—CH═CH—; R 4 =—CH 2 CH 2 OCH 2 CH 2 O—; W=4,5-bicyclooctene-1,2,3-triazole 
       [0065]    Compact PEEK oxime samples (n=2) functionalized as cycloalkyne as described in Example 12, was reacted with 0.2 mg of OGP mimetic of formula (I): (R 1 =—CH 2 CH 2 —; R 2 =—CH 2 OCH 2 —; R 3 =—CH═CH—; X=N 3 ; Y=p-C 6 H 4 OH; Z=Ph prepared as described in Example 10). Reaction conditions and purification was identical to the Example 12. 
         [0066]    Surface characterization data for polished compact PEEK modified with OGP mimetic. XPS analysis: C 75.6%, O 21.2%, N 3.2%. 
       Example 17 
     Compact PEEK-M with the Surface Modified with OGP Mimetic. Material (XIV): R 1 =—[CH 2 CH 2 O] 3 CH 2 CH 2 HN(CO)OCH 2 CH 2 —; R 2 =—CH 2 OCH 2 —; R 3 =—CH═CH—; R 4 =—CH 2 CH 2 OCH 2 CH 2 O—; W=4,5-bicyclooctene-1,2,3-triazole 
       [0067]    A compact PEEK oxime discs functionalized as cycloalkyne as described in Example 12, was introduced under nitrogen atmosphere into a test tube containing 1 mL of THF/H 2 O 1:1 mixture, 0.1 mg of OGP mimetic (I) (R 1 =—[CH 2 CH 2 O] 3 CH 2 CH 2 HN(CO)OCH 2 CH 2 —; R 2 =—CH 2 OCH 2 —; R 3 =—CH═CH—; X=N 3 ; Y=p-C 6 H 4 OH; Z=Ph) prepared as described in Example 11. The suspension was stirred at 40° C. for 24 h. The discs were washed repeatedly with THF, water and methanol and dried at room temperature under vacuum for 5 h. 
         [0068]    Surface XPS analysis for the compact PEEK modified with OGP mimetic: C 79.8%, O 17.7%, N 2.5%. 
         [0000]    
       
                 
         
             
             
         
       
     
       Example 18 
     Compact PEEK with the Surface Modified with a Combination of RGD and OGP peptidomimetics. Material (XV): R 1 =R 3 =—CH 2 CH 2 —; R 2 =—CH 2 CH 2 OCH 2 —; R 4 =—OCH 2 CH 2 OCH 2 CH 2 —; R 5 =—CH═CH—; R 6 =—CH 2 OCH 2 —; W=4,5-bicyclooctene-1,2,3-triazole 
       [0069]    Compact PEEK oxime discs (n=2) functionalized as cycloalkyne as described in Example 12, were introduced under nitrogen atmosphere into a test tube containing 2 mL of THF/H 2 O 1:1 mixture, 0.1 mg of RGD mimetic of formula (I) (R 1 =R 3 =—CH 2 CH 2 —; R 2 —CH 2 OCH 2 CH 2 ; X=N 3 ; Y=—NHC(═NH)NH 2 ; Z=CO 2 H) prepared as described in Example 5, and 0.1 mg of OGP mimetic of formula (I) (R 1 =—CH 2 CH 2 —; R 2 =—CH 2 OCH 2 —; R 3 =—CH═CH—; X=N 3 ; Y=p-C 6 H 4 OH; Z=Ph) prepared as described in Example 10. The suspension was stirred at 40° C. for 24 h. The discs were washed repeatedly with a solution of HCl 0.1M, an aqueous solution of NH 3  (pH=11), water and methanol and dried at room temperature under vacuum for 5 h. 
         [0070]    Surface XPS analysis for compact PEEK (XV) modified with RGD and OGP: C 74.9%, O 21.6%, N 3.59% ( FIG. 1 ). 
       Example 19 
     Compact PEEK with the Surface Modified with a Combination of RGD and OGP Peptidomimetics. Material (XV): R 1 =—[CH 2 CH 2 O] 3 CH 2 CH 2 HN(CO)OCH 2 CH 2 —; R 3 =—CH═CH—; R 4 =—OCH 2 CH 2 OCH 2 CH 2 —; R 5 =—CH═CH—; R 6 =—CH 2 OCH 2 —; W=4,5-bicyclooctene-1,2,3-triazole 
       [0071]    Compact PEEK oxime discs (n=2) functionalized as cycloalkyne prepared as described in Example 12, were introduced under nitrogen atmosphere into a test tube containing 2 mL of THF/H 2 O 1:1 mixture, 0.1 mg of RGD mimetic of formula (I) (R 1 =—[CH 2 CH 2 O] 3 CH 2 CH 2 HN(CO)OCH 2 CH 2 —; R 2 =—CH 2 OCH 2 CH 2 —; R 3 =—CH 2 CH 2 —; X=N 3 ; Y=—NHC(═NH)NH 2 ; Z=CO 2 H) prepared as described in Example 10, and 0.1 mg of OGP mimetic (I) (R 1 =—[CH 2 CH 2 O] 3 CH 2 CH 2 HN(CO)OCH 2 CH 2 —; R 2 =—CH 2 OCH 2 —; R 3 =—CH═CH—; X=N 3 ; Y=p-C 6 H 4 OH; Z=Ph) prepared as described in Example 11. The suspension was stirred at 40° C. for 24 h. The discs were washed repeatedly with a solution of HCl 0.1M, an aqueous solution of NH 3  (pH=11), water and methanol and dried at room temperature under vacuum for 5 h.