Abstract:
A silicon carbide structure (10) and method capable of using existing silicon wafer fabrication facilities. A silicon wafer (20) is provided which has a first diameter. At least one silicon carbide wafer (30) is provided which has a given width and length (or diameter). The width and length (or diameter) of the silicon carbide wafer (30) are smaller than the diameter of the silicon wafer (20). The silicon wafer (20) and the silicon carbide wafer (30) are then bonded together. The bonding layer (58) may comprise silicon germanium, silicon dioxide, silicate glass or other materials. Structures such as MOSFET (62) may be then formed in silicon carbide wafer (30).

Description:
This is a continuation of application Ser. No. 08/020,820, filed Feb. 22, 1993, now U.S. Pat. No. 5,349,207. 
    
    
     FIELD OF THE INVENTION 
     This invention generally relates to semiconductor devices and processes and more specifically to silicon carbide wafers. 
     BACKGROUND OF THE INVENTION 
     A growing segment of the semiconductor business is high voltage/high power devices and integrated circuits. A critical element in this business is the power MOSFET. Power MOSFETs have many diverse applications in automotive, communications, consumer, data processing, industrial and military markets. For example, power MOSFETs may be used as drivers for motors, lamps, or displays. Most power MOSFETs are built in silicon. However, the performance of power MOSFETs built in silicon are already close to their theoretical limits. Therefore, research efforts have turned to silicon carbide (SIC) wafers. SiC has the potential for significantly (as much as two orders of magnitude) higher performance power MOSFETs compared to silicon wafers. However, one of the limitations in using SiC is that the wafer size is much smaller than present silicon wafers. SiC wafers have been limited to approximately 1 inch diameters. This inhibits their use or production in existing silicon wafer fabrication facilities built to handle large wafers. 
     Both depletion mode and inversion mode MOSFETs have been demonstrated in SiC. A depletion mode device is shown in FIG. 1a. The MOSFET channel was built in a 1.2 um thick n-type b-SiC epitaxial layer. A polysilicon annular gate electrode was used. Source/drain regions were implanted at 773K and contacted with tantalum silicide (TaSi2) which was annealed at 1173K. The depletion threshold voltage was -12.9 V and the device operated up to a drain voltage of 25 V at temperatures up to 923K. An inversion mode MOSFET is shown in FIG. 1b. A p-type b-SiC epitaxial layer was used. The threshold voltage was 9 V and the device operated up to 923K. 
     SUMMARY OF THE INVENTION 
     Generally, and in one form of the invention, a silicon carbide structure and method capable of using existing silicon wafer fabrication facilities is disclosed. A silicon wafer is provided which has a first diameter. At least one silicon carbide wafer is provided which has a given width and length. The width and length of the silicon carbide wafer are smaller than the diameter of the silicon wafer. The silicon carbide wafer is then bonded to the silicon wafer. 
     An advantage of the invention is providing a structure for allowing small diameter silicon carbide wafers to be processed in existing silicon wafer fabrication facilities. 
     A further advantage of the invention is the capability to use existing silicon wafer fabrication facilities and still obtain greater performance than is possible with silicon wafers. 
    
    
     BRIEF DESCRIPTION OF THE DRAWINGS 
     In the drawings: 
     FIGS. 1a-b are cross-sectional views of prior art MOSFETs built in SiC. 
     FIG. 2 is a plot of 1/Rsp characteristics for various materials. 
     FIG. 3a is a top view of the preferred embodiment of the invention. 
     FIG. 3b is a cross-sectional view of the preferred embodiment of the invention. 
     FIGS. 4a-c are cross-sectional views illustrating various states of fabrication of the preferred embodiment of the invention utilizing an oxide to oxide bond. 
     FIGS. 5a-e are cross-sectional views illustrating various states of fabrication of the preferred embodiment of the invention utilizing a silicon germanium bond. 
    
    
     Corresponding numerals and symbols in the different figures refer to corresponding parts unless otherwise indicated. 
     DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS 
     The power MOSFET is a switch, much like an electromechanical relay is a switch, but it is much smaller, more reliable, and can be electronically controlled. The key performance figure for the power MOSFET is specific on-resistance (Rsp), or the resistance of this switch per unit; die area when the device is switched on. A goal in power MOSFET technology is reducing the specific on-resistance as much as possible. This leads to 1/Rsp as a convenient figure of merit which should be maximized. The Rsp, depends on the semiconductor material properties, and the figure of merit can be written as 
     
         FIGURE OF MERIT=1/Rsp˜=ε*μ*εc.sup.3 
    
     where ε is the dielectric constant, μ is the carrier mobility, εc is the avalanche electric field. Table 1 lists the properties of a few candidate materials and FIG. 2 plots the 1/Rsp figure of merit. 
     
                                           TABLE 1__________________________________________________________________________Material Properties and Figure of MeritParameter     Symbol              Units Si    GaAs  SiC   Diamond__________________________________________________________________________Relative Dielectric Constant              C/V.cm                    11.8  12.8  9.7   5.5Mobility      μ cm.sup.2 /V.sec                    1400  8000  300   2200Critical Field         E.sub.c              V/cm  3 × 10.sup.5.sup.                          4 × 10.sup.5.sup.                                2.5   10.sup.6.sup.                                      7 × 10.sup.6.sup.Figure of Merit Factor         ε*μ*Ec.sup.3              --    4.46 × 10.sup.20                          6.55 × 10.sup.21                                4.55 × 10.sup.22                                      4.15 × 10.sup.24Relative Figure of Merit         --   --    1     14.7  102   9300__________________________________________________________________________ 
    
     Gallium arsenide (GaAs) has the potential of an order of magnitude improvement in performance. The material is also available up to 4&#34; wafer size. But it has major drawbacks for power MOSFET use. First, it is very difficult to grow a high quality gate insulator in this material. Second, this material cannot be processed in the same wafer fabrication facilities that run silicon without cross-contamination as gallium and arsenic are contaminants in silicon. 
     Diamond has the potential of highest performance. But diamond technology also lacks the ability to grow a high quality gate insulator. The material is difficult to process, is prohibitively expensive, and is presently not available commercially in wafer form. 
     SiC has the potential of 100X higher performance compared to Si power MOSFETS. It can be oxidized to form high quality silicon dioxide (SiO2) to serve as gate insulator. SiC wafers are commercially available. This material can be processed in the same wafer fabrication facilities that produce silicon devices without any cross-contamination problem. This is very important since new dedicated wafer fabrication facilities require huge capital investment. 
     
                       TABLE 2______________________________________Rating of Candidate Materials for Power MOSFETCriteria     GaAs       SiC        Diamond______________________________________Figure of Merit        Good       Very Good  ExcellentGate Insulator        Poor       Good       PoorCost         Good       Good       PoorAvailability Very Good  Good       PoorProcess in Si        Poor       Excellent  PoorWafer-fabsOverall Rating        Good       Excellent  Poor______________________________________ 
    
     Table 2 summarizes ratings of candidate materials in various categories. Due to a combination of reasons involving theoretical performance potential, device technology issues, economic and practicality factors, SiC is the preferred material for dramatic performance improvement in power MOSFETs. 
     Unfortunately, one of the limitations in using SiC is that the wafer size is much smaller than traditional silicon wafers. SiC wafers have been limited to approximately 1-2 inch diameters. The result of this limitation is that existing silicon wafer fabrication equipment cannot be used. Re-tooling wafer fabrication facilities would prove very costly. An advantage of the preferred embodiment is providing a SiC wafer, or wafers, which can use existing silicon wafer fabrication equipment built to handle larger silicon wafers. 
     The preferred embodiment of the invention will now be described with reference to FIGS. 3a-b. One or more SiC wafers 30 are bonded to a large diameter silicon wafer 20. The diameter of silicon wafer 20 will typically be in the range 4 to 8 inches. The composite wafer 10 having a silicon holder 20 and several SiC wafers 30 can be handled with standard wafer fabrication equipment. FIG. 3a depicts silicon carbide wafers 30 as circular, but it will be apparent to those skilled in the art that the SiC wafers 30 need not be circular or any other particular shape. A mosaic pattern may alternatively be used. 
     Several methods may be used to bond the SiC wafer 30 to the silicon wafer 20. Because of the material properties of SiC, many techniques developed for use in SOI processing may be used to bond SiC wafer 30 to silicon wafer 20. For example, a high temperature oxide to oxide bond may be used. Referring to FIG. 4a, SiC wafer 30 and silicon wafer 20 are thermally oxidized to form oxide layers 40 and 42. Oxide layers 40 and 42 are each on the order of 0.5 um thick. The surface 44 of oxide layer 40 may then be bonded to the surface 46 of oxide layer 42 using a carbon heater at a reduced pressure of 10 -1  Pa while preferably applying a pulse voltage between the SiC wafer 30 and the silicon wafer 20 to provide an electrostatic force, as shown in FIG. 4b. The bonding temperature is on the order of 800° C. The amplitude of the voltage is on the order of 300 V, its width is on the order of 100 ms, and its period is on the order of 500 ms. After bonding, the composite wafer 10 may be annealed, as shown in FIG. 4c. Annealing may, for example, be for approximately 30 minutes in a nitrogen ambient at approximately 1100° C. Annealing increases the bond strength. Other methods will be apparent to those skilled in the art, such as metal bonding in a vacuum, bonding by glass-layer fusing and oxygen-assisted bonding. 
     However, the preferred bonding method uses a metal alloy such as silicon germanium (SiGe) and is described in co-pending U.S. patent application Ser. No. 08/019,295, filed Feb. 19, 1993. Referring to FIG. 5a, SiC surface 50 and silicon surface 52 are well polished. Next, layers of SiGe alloy 54 and 56 are deposited on both SiC surface 50 and silicon surface 52, as shown in FIG. 5b. SiGe layers 54 and 56 may be deposited by chemical vapor deposition (CVD). Other methods such as molecular beam epitaxy (MBE) may alternatively be used. SiGe layers 54 and 56 are then brought in contact with one another (preferably under pressure) and the composite wafer 10 is heated to a temperature above the melting point of SiGe layers 54 and 56, as shown in FIG. 5c. The melting point will be between 950° C. and 1400° C. depending on the germanium concentration in the SiGe layers 54 and 56. When composite wafer 10 is heated, SiGe layers 54 and 56 melt and upon cooling form an inseparable bond layer 58, as shown in FIG. 5d. Once bond layer 58 is formed, structures such as transistor 62 may be formed in SiC wafer 30, as shown in FIG. 5e. Methods for forming transistor 62 will be apparent to those skilled in the art. Transistor 62 may, for example, .comprise a MOSFET, MESFET, JFET or bipolar transistor. 
     A few preferred embodiments have been described in detail hereinabove. It is to be understood that the scope of the invention also comprehends embodiments different from those described, yet within the scope of the claims. 
     While this invention has been described with reference to illustrative embodiments, this description is not intended to be construed in a limiting sense. Various modifications and combinations of the illustrative embodiments, as well as other embodiments of the invention, will be apparent to persons skilled in the art upon reference to the description. It is therefore intended that the appended claims encompass any such modifications or embodiments.