Abstract:
An expandable chemical coating compounded by an admixture of a paint, ink or dye with a polymeric composition embodying an encapsulation of a volatile, gas-producing substance which is heat-expandable in a thin polymeric film, said capsules being dispersed in a polymeric composition such that upon application of heat, the encapsulated volatile substance vaporizes to expand and fracture said capsule, thereby trapping the evolving gas in a polymeric medium so that the medium coating is expanded to produce a three-dimensional effect.

Description:
BACKGROUND OF THE INVENTION 
     1. Field of the Invention 
     This invention pertains to chemical coatings made from heat-expandable polymeric compositions, and, in particular, to such compositions as used as a component of art materials such as paints. Basic to the invention is the encapsulation in a monomer film forming agent of a volatile liquid or gas to form a polysphere which expands in the presence of heat. 
     2. Description of the Prior Art 
     This invention relates to chemical coatings made from expandable polymeric compositions which can be expanded by the introduction of heat at some suitable point in the use of the expandable polymeric compositions. The use in particular, is for art purposes by which these expandable polymeric compositions are painted, brushed, stenciled, coated, printed or sprayed in an artful manner to make or create an art form or craft in many unlimited, extensive forms of art. The final effect is realized when the art is subjected to heat in form of a lighted match, electric or gas fired oven, electric hair dryer, electric iron, steam, hot water, hot oil, or other heat source to cause the art form to expand in the desired manner. This invention in specific relates to the expandable polymeric compositions being added or incorporated into the artist material, of such liquid state, to impart the special feature of &#34;expandable art.&#34; The invention also relates to the paints or coatings formed in accordance of this &#34;expandable art&#34; technology. 
     Expandable art has never been employed in an art form, so hence it is a new art medium that has extremely fascinating appeal for it allows for the creation of new effects. It is possible by incorporating &#34;expandable art&#34; into the normal or conventional paints, coatings and printing inks used by artists, craft masters, and art practitioners to add a new dimension to their works. It is to be understood here that the expandable polymeric compositions of this invention are meant only for art and decorative value, not for any utilitarian function, only for appearance effect by the unique topographic texture achieved. 
     It is to be further understood that the &#34;expandable art&#34; as provided by the expandable polymeric compositions of this invention combined into a paint, be it oil based or latex based (water system), and the skill of the artist in varying by degree the quantity of the expanding composition or agent employed create &#34;expandable art&#34; effects. Once the artist or practitioner is familiar with the mechanism of expandable art, he can vary to an unlimited degree the amount of expansion desired by the amount of expanding agent used and the kind of heat effect employed. This new art form is very challenging, and this makes it of value, for it requires skill, and work to become proficient in the use of expandable art. The employment of it is not limited, but expansive, and therein lies its appeal and value as a new art medium, or craft tool. Obviously, it would be beyond the ability in specifying this invention to detail in all exactness how it can be used; as with any truly valid art form it is beyond the ability of one man to cite all that can be created. However it is rather our intention to explain how the expandable art is made, and how it can be achieved. 
     The expansion is achieved by heating, the heat in turn causing the formation of a vapor or a gas that comes from vaporization of an encapsulated liquid, and/or decomposition of a chemical compound. These gas producing chemical compounds are incorporated in a suitable composition that must be especially designed to efficiently disperse and entrap the evolving gas or vapor so that the whole composition expands without allowing the gases or vapors to escape beyond the confines of the expanding compositions. To achieve this kind of expanding action effectively, is the very essence of this invention; for liquids that convert from a liquid to a vapor on heating are known phenomena of science, of which water and acetone are known, water being slow and requiring considerable heat to vaporize, whereas acetone is fast, requiring relatively little heat for vaporization; and chemical compounds that decompose on heat yielding as part of their decomposition products gases such as water, nitrogen and carbon dioxide, are also known, these compounds being azo compounds, sulphohydrazides, and nitroso compounds. These vapor producing or gas producing chemical compounds must be adequately dispersed in a specifically designed polymeric composition that encapsulates these gas producing compounds, so that on exposure to heat, the evolving gas does not escape, but is held sufficiently to cause effective expansion of the encapsulating polymeric composition or whatever subsequent polymeric medium, paint coating, or ink, is utilized so that the expandable polymeric composition is dispersed and admixed or incorporated. 
     To encapsulate the gas-producing chemicals they are formed into what is called &#34;polyspheres&#34;. Polyspheres are formed by incorporation of the &#34;seed&#34; emulsion polymerization. These polyspheres assist in holding or entrapping the evolving gas upon the introduction of heat. However, it is still required that these polyspheres be dispersed further in a polymeric film forming composition which in its design furthers the confinement or non-escape of the gas during heat exposure, without first expanding the whole polymeric mass. The expandable polymeric composition does not have to be dried to help trap the gas, but upon immediate exposure to a temperature of sufficient heat to activate the gas-producing agents, the expandable polymeric composition will function while drying, i.e. if it is dried or set at a temperature that activates the expansion, the whole mass will effectively expand without collapse, or escape of gases. Hence, there is no need to be temperature conscious; any temperature of sufficient heat capacity to activate the expanding agents is sufficient. However, if one wishes to dry the expandable art medium, formed by incorporating the expandable polymeric composition, at a temperature below the decomposition temperature or activating temperature of the polyspheres this is perfectly acceptable. The expansion is then accomplished after the expandable art medium is dry, by subjecting it to a temperature sufficient in heat capacity to activate the polyspheres which encapsulate the gas-producing chemicals. 
     SUMMARY OF THE INVENTION 
     The expandable chemical coatings made from polymeric compositions of this invention are formed by selecting a binder polymer latex that is a film-former, which is normally in the form of a polymeric dispersion (latex) in water. To this is added a dispersing agent to later serve as the dispersant for the polyspheres in the binder dispersion. The term &#34;polysphere&#34; is defined infra in the description of the preferred embodiment. Three types of polyspheres are specified, polyspheres H, polyspheres BH and polyspheres BHS. Next, the polyspheres are added under adequate agitation to achieve intimate dispersion. A defoamer is added to prevent excessive foam development in handling the compositions and mixing it into other mediums. A bridge solvent is next incorporated into the composition to provide compatibility with mixtures into which the composition will be admixed, and to give wetting upon many diverse surfaces into which the expandable art medium might be applied. &#34;Bridge solvent&#34; is trade terminology for an agent which brings together two phases of a mixture which would not normally come together to form a homogeneous mixture. Next is added the thickener, which increases the viscosity of the composition to the desired level; the thickner also serves to give stability upon admixing with other mediums, give suspending action to the polyspheres in the composition, and to develop or maintain the proper application consisting of the resultant expandable art medium. 
    
    
     DESCRIPTION OF THE PREFERRED EMBODIMENT 
     The expandable chemical coatings made from polymeric compositions of this invention are formed by selecting a binder polymer latex that is a film-former, which is normally in the form of a polymeric dispersion (latex) in water. In the preferred embodiments and the examples that follow in this specification, the principal binder of the various compositions is acrylic latex and a terpolymer is included to act as a polymeric plasticizer to yield a softer composition. To this is added a dispersing agent to later serve as the dispersant for the polyspheres in the binder dispersion. Next, the polyspheres are added under adequate agitation to achieve intimate dispersion. The term &#34;polysphere&#34; is defined hereinafter. A defoamer is added to prevent excessive foam development in handling the compositions and mixing it into other mediums. A bridge solvent is next incorporated into the composition to provide compatibility with mixtures into which the composition will be admixed, and to give wetting upon many diverse surfaces into which the expandable art medium might be applied. The term &#34;bridge solvent&#34; has been defined above. In the preferred embodiment, the bridge solvent having a low boiling point, not encapsulated in the polyspheres, providing for the wetting of the various ingredients so that a stable, compatible composition is produced. The polyspheres require a bridge solvent to assist in wetting them so that they can be incorporated in the composition binder latex. Next is added the thickener, which increases the viscosity of the composition to the desired level; the thickener also serves to give stability upon admixing with other mediums, give suspending action to the polyspheres in the composition, and to develop or maintain the proper application consisting of the resultant expandable art medium. 
     The binder polymer latex for the composition can be selected from the following film forming polymers which are: 
     
         ______________________________________polytheylene    polypropylenepolyethylene vinyl acetate           natural rubber1,4 polyisoprene           polyacrylonitrilepolyvinyl fluoride           polyvinylidene chloridepolyvinylidene fluoride           polymonochloridefluoroethylene  polytetrafluorethylenepolychloroprene acrylonitrile-butadiene-styrene           terpolymerpolyvinyl butyral           polystyrenepolyvinyl acetate           polyvinyl alcoholpoly-a-methyl styrene           butadiene-styrenecopolymer       polymethacrylatepolymethyl-a-cyanoacrylate           ethyl vinyl ether and maleic           anhydridepolymethyl-vinylether           copolymer of styrene and ethyl           acrylatecopolymers of styrene and           polyvinylidene chloridevinylidene chloridecopolymers of butylacrylate           copolymers of 2-ethyl nexyla-and vinylacetate           crylateacrylonitrile   copolymer of methyl methacrylate           and ethylacrylatecopolymers methylmethacry-           terpolymers of acrylinitrilelate &amp; acrylonitrilebutylacrylate   vinylacetateterpolymers of acryloni-           2-ethylhexylacrylatetrilesvinylacetate    terpolymers of butylacrylateacrylonitriles  ethylacrylatecopolymers of vinylidene           acrylonitrilechloridecopolymers of vinylidene           copolymers of vinylidene chloridechloride &amp; acrylonitrile           &amp; ethyl acrylatepolyurethane    epoxiespolycarbonates  polyesterspolyamides      urea formaldehydephenol-formaldehyde______________________________________ 
    
     These polymers can be self-crosslinking, crosslinkable, or non-curing. These binders can be employed in a mixture, for example copolymer of ethylacrylate, and butylacrylate, and a copolymer of butadiene and acrylonitrile. 
     The dispersants or dispersing agents are selected from certain types of surface active agents that are particularly effective in dispersing the polyspheres in a water, binder system. The surface-active compounds or agents that have been found effective are benzylphenyldimethyl ammonium salts, nephlanic acid salts, alkylacrylsufonates, sulfamated oils, hydroxylakysulfamide, and hydroxyalkyl phosphates. 
     The polyspheres as employed in this invention are made from &#34;seed&#34; emulsion polymerization techniques, in which the &#34;seed&#34; consists of the volatile liquid or gas producing solid around which the monomeric film-former polymer components are polymerized to completely encapsulate the &#34;seed&#34; emulsion or dispersion to form the final polyspheres, which consist of volatile liquid or gas-producing solid. An essential requirement for the &#34;seed&#34; emulsion to work, is that the volatile liquids and the gas-producing solids be hydrophobic, so that these hydrophobic compounds must be formed into a fine emulsion or dispersion &#34;seed&#34;. This &#34;seed&#34; serves as the site for emulsion polymerization, whereby the monomeric ingredients which are added to the batch or added by delayed addition are polymerized around the &#34;seed&#34; completely encapsulating it. 
     A typical method of making polyspheres is given: a reactor equipped with an agitator, and exterior high shear turbine pumps is charged first with 100 parts of demineralized water, and 3.5 of an hydroxy alkyl phosphate, followed by 17 parts of a gas producing chemical benzene sulfohydrazide. Next is added 12 parts of a 30% colloidal silica dispersion. To this, is added 0.17 parts of a high hydroxyl ethyl cellulose. Next is added 20 parts of a film forming encapsulating polymer formulated from of a 100 parts premix consisting of 78 parts vinylidene chloride, 4 parts acrylonitrile, and 18 parts of ethyl acrylate. This whole mixture is run through an external high shear turbine pump system, recirculating from the bottom of the reactor to the top for 20 minutes until a fine white emulsion is formed (1.5-20 micron, average 2.0 micron dispersed phase size). After this &#34;seed&#34; dispersion is formed, the initiator, 4 parts of benzoyl peroxide is added, the reactor sealed, and after the reaction is initiated the temperature will rise from the exothermic reaction. As the batch temperature reaches 78° C., the remaining 80 parts of the monomer phase is added slowly, maintaining the reaction at a strong pace at 84° C until all the monomer phase is added. At the completion of the reaction; the resultant reaction mix consist of a milky white liquid. This milky white liquid is a dispersion of polyspheres, consisting of benzene sulfohydrazide encapsulated in a sphere of polyvinylidene, acrylonitrile, ethyl acrylate polymer. The particle size of this dispersion is 2 to 20 microns, the average size 2.5 microns. In this form polyspheres H are employed. If the polysphere dispersion is dried at 146° C for 5 minutes a white, fluffy powder results of expanded spheres, resembling &#34;sea-shells&#34;. At this point, the resultant expanded polyspheres are dusty, frayable, crystal-like mass. If polyspheres are to be made using a volatile liquid, like isobutane, which is a vaporizing hydrophobic liquid, then in place of the benzene sulfohydrazide, 20 parts of isobutane is added. This yields polyspheres BH. 
     By utilizing the above technique a wide variety of expandable microcellular polyspheres can be prepared. Such polyspheres now can find wide usage in the making of expandable art. 
     In this invention the polyspheres are formulated into art paints, or coatings for textile substrates in the unexpanded form, applied by the coating techniques of painting, brushing, spraying, dipping, and the like by known simple procedures to give designs, lettering, coatings and similar effects, and then by the selective application of heat, activate the expanding action to achieve the final, &#34;raised&#34; or vertical dimensional effect. A further advantage is the ability to work the unexpanded or expanded art application to give special effects resulting from embossing, creasing, or stamping, etc. 
     The coating and adhesive compositions can be especially formulated by the selective addition of plasticizers, extenders, drying oils, fillers, coloring compounds surfactants, thickeners and the like to make functional, decorative surfaces, such as a &#34;suede&#34; leather effect. The specific combination of the above additives in conjunction with the suitable expanding agent gives the kind of special coating effect desired, either artificial leather or suede. 
     Hence, it is apparent that by the selective combination of the polyspheres with film formers and various functional additives, compositions can be tailored to many diverse end-uses. The designer familiar with the art of this invention can work with designing the polyspheres to give the expanding effect desired, selecting film-formers to give desired properties, and the many kinds of additives to achieve just the kind of performance intended. 
     It can be seen that by the practice of this invention in the making of expandable polymeric compositions many decorative are effects can be achieved, therefore examples are given as an illustration only of this vast technology, and in no way should be construed as limiting the scope of this invention. 
     EXAMPLE NO. 1 
     An expandable polymeric composition made in accordance with the principles of this invention to make an expanding agent for paints by combining the following ingredients in the indicated proportions: 
     
         ______________________________________Ingredients            Parts By Weight______________________________________Water                  41.73Hydroxy ethyl cellulose thickener                  0.2Hydroxy ethyl phosphate                  0.17Butylene Glycol        8.7Terpolymer Latex       9.2Polyspheres H          17.0Acrylic latex          23.0______________________________________ 
    
     This composition can then be combined in any suitable ratio with a commercial artist paint, usually in the ratio of 1 part artist paint to 1 part expanding agent as described above. 
     The terpolymer latex is made from the emulsion polymerization of the following monomers 30 parts 2-ethyl hexyl acrylate, 30 parts butyl acrylate, and 40 parts of ethyl acrylate, at 50% solids. The term &#34;terpolymer&#34; is a standard term of trade usage used to designate a polymer having three principal ingredients, an acrylic monomer, a vinyl acetate monomer and a vinyl monomer. The formula presented in this example is typical. 
     The polyspheres are made by reacting 100 parts of demineralized water, containing 15 parts of colloidal silica, 15 parts of benzene sulfohydrazide (Nitropore OBSH from Stepan Chemical, Wilmington, Massachusetts) 2.8 parts of hydroxyl ethyl phosphate, an encapsulating film forming polymer made from 100 parts of vinylidene chloride, 15 parts acrylonitrile, 5 parts of methacrylic acid, 5 parts of ethyl acrylate, and 0.4 parts of benzoly peroxide, identified as Polyspheres H. In this example, the butylene glycol is the bridge solvent, the terpolymer latex is a plasticizer which serves to soften the composition, the acrylic latex is the binder polymer. 
     The acrylic latex is made by reacting by means of emulsion polymerization the following monomers, 95 parts ethyl acrylate, 2 parts n-methanol acryl amide, 1.0 part acrylic acid, 2 parts acrylonitrile. 
     The above expanding composition mixes easily into any artist or craft paint, either oil or latex based, in any desired ratio, for example, 1 part expanding agent, 1 part paint or 1 part expanding agent, 2 parts paint; this admixed paint then can be skillfully applied to any particular substrate in any of many manners, allowed to air dry, or not, then subjected to a heat source, set at a minimum temperature of 235° F for at least 180 seconds to achieve a puffing or foaming or expanding action to yield a raised, puffed or three dimensional effect. 
     EXAMPLE NO. 2 
     An expandable polymeric composition made in accordance with this invention to make an expanding agent for paints by combining the following ingredients in the indicated proportions: 
     
         ______________________________________Ingredients            Parts by Weight______________________________________Water                  44.88Hydroxy ethyl cellulose thickener                  0.17Butylene Glycol        8.7Terpolymer Latex       9.2Polyspheres BH         17.0Acrylic Latex          23.0______________________________________ 
    
     Hydroxy ethyl cellulose (Cellosize QP52000H from Union Carbide) Acrylic thickener (Acrysol GS from Rohm &amp; Hass). 
     Polyspheres BH are made by &#34;seed&#34; emulsion polymerization by reacting 100 parts of demineralized water, 14 parts of colloidal silica, 8 parts of benzene sulfohydrazide (Nitropore OBSH) 8 parts of Isobutane, 1.5 parts hydroxyl ethyl phosphate, 2.5 parts of nonionic surfactant (Igepal CO880 from GAF Chemical Corp.) In this example, the butylene glycol is the bridge solvent, the terpolymer latex is a plasticizer which serves to soften the composition, the acrylic latex is the binder polymer. 100 parts of vinylidene chloride, 15 parts of acrylonitrile, 5 parts of methacrylic acid, 2 parts of ethyl acrylate, and 0.4 parts of benzoyl peroxide catalyst, identified as polysphere BH. The difference between polyspheres H, polyspheres BH and polyspheres BHS is specified in the formulations presented in Example 1, page 11; Example 2, pages 12, 13; and Example 6, page 15. Polyspheres H contain a hydrazine, OBSH, which tends to break down in water. In polyspheres BH isobutane is added as a bridge solvent in a one-to-one ratio to the OBSH to stabilize this water hydrolysis and to assist in binding the colloidal silica. In polyspheres BHS to ratio os isobutane to OBSH is one-to-two, to provide the same stabilization from water hydrolysis while also providing a higher temperature blowing agent. 
     The above expanding agent is admixed with art or craft paint in any desirable ratio, and expanded by a suitable heat source for 180 seconds at 225° F. 
     EXAMPLE NO. 3 
     An expanding polymeric composition for use as a suede paint, or coating: 
     
         ______________________________________Ingredients           Parts by Weight______________________________________Water                 46.0Hydroxyl ethyl cellulose                 0.15Acrylic Thickener     2.0Precipitated Calcium Carbonate                 12Terpolymer Latex      9Polyspheres BH        22Phosphate ester       4.0Ammonium Stearate     2.0Acrylic Latex         40.0______________________________________ 
    
     Acrylic Latex is Rohm &amp; Haas&#39;s Rhoplex AC-234. The above composition can be painted or coated by any effective technique to various kinds of substrates such as metal, wood, paper, leather or textile, from a 2 mil to 10 mils thickness, or multiple coats, then exposed to a suitable heat source for 180-240 seconds to achieve expansion to a microporous structure that has the feel or touch of suede. 
     EXAMPLE NO. 4 
     An expanding polymeric composition for use as a leather finish, paint or coating. 
     
         ______________________________________Ingredients          Parts by Weight______________________________________Water                48.42Hydroxy ethyl phosphate                0.2Nonionic Surfactant  0.4Bentonite Clay       12.0Aluminum Silicate    12.0Propylene Clycol     2.4Glycol Stearate      1.3Terpolymer Latex     9.0Polyspheres H        27.0Acrylic Latex        40.0Acrylic Thickener    2.0Hydroxy ethyl cellulose                0.12______________________________________ 
    
     The above composition can be coated upon any suitable substrate from a thickness of 2 mils to 20 mils, then exposed to heat for 300 seconds at 240° F. The result is a leather finish having just the right feed and hand. Colorants can be added to this composition either directly, or admised in a polymer vehicle. 
     Triton X100 from Rohm &amp; Haas. 
     Volclay Bentonite Bc-USP from American Colloid Company. 
     Aluminum Silicate-ASP 400 from Minerals &amp; Chemicals Philip Corp. 
     EXAMPLE NO. 5 
     An expanding polymeric composition for use as a soft, opaque, backing for rugs, diapers, furniture cloths, and canvas. 
     
         ______________________________________Ingredients           Parts by Weight______________________________________Water                 70.2Hydroxy ethyl phosphate                 3.0Kaolin Clay           30.0Precipitated Calcium Carbonate                 30.0Glycol Stearate       3.0Butylene Glycol       9.0Terpolymer Latex      11.0Polyspheres H         23.0Styrene-butadiene latex                 43.0Hydroxy ethyl cellulose                 0.2______________________________________ 
    
     This composition is back coated on nonwoven or textile substrates by conventional coating techniques and then exposed to heat for 300 seconds at 250° F. The resultant coating is soft, and very opaque, giving unusual softness and opacity. 
     EXAMPLE NO. 6 
     An expanding polymeric composition for use as a soft, strong, leather-like coating for shoe uppers. 
     
         ______________________________________Ingredients          Parts by Weight______________________________________Water                56.2Hydroxy ethyl phosphate                3.0Kaolin Clay          20.0Attapulgus clay      20.0Butylene Glycol      3.0Terpolymer latex     9.0Polyspheres BHS      23.0Acrylic Latex        40.0Hydroxy ethyl cellulose                0.2______________________________________ 
    
     Polysphere BHS is made by &#34;seed&#34; emulsion polymerization by reacting 100 parts of demineralized water, 12 parts of colloidal silica, 12 parts of benzene sulfo hydrazide (Nitropore OBSH) 4 parts of isobutane, 1.75 parts of hydroxy ethyl phosphate, 2.3 parts of n-octyl phenol ethylene oxide condensate (Igepal CO 730), 80 parts of vinylidene chloride, 15 parts of butyl acrylate, 5 parts of acrylonitrile, 0.5 parts of methacrylic acid, and 0.6 parts of benzoyl peroxide catalyst, identified as Polyspheres BHS. 
     The above composition is coated onto canvas fabric at a thickness of 14 mils for the 1st and 2nd coat with a low temperature drying at 200° F after the 1st coat, and a high temperature drying at 280° F for 300 seconds after the 2nd coat. The resultant coating is strong, and attractive, giving a textile surface feel or touch. 
     EXAMPLE NO. 7 
     Same as Example No. 6 above, only the acrylic latex is replaced with a vinyl chloride/acrylic latex (Geon 460 X2, B. F. Goodrich). This is applied to canvas fabric as cited under example 6, again given a durable, strong finish on canvas fabric, so as to make attractive canvas shoes. 
     EXAMPLE NO. 8 
     An expanding polymeric composition for use as a coating for textile goods. 
     
         ______________________________________Ingredients         Parts by Weight______________________________________Phosphate ester     30Di octyl phthalate  25Poly oil plasticizer               25Geon 121            50Kaolin Clay         15Polyspheres H       15Mineral Oil          5______________________________________ 
    
     This coating composition is applied by conventional coating techniques at 3 to 14 mils in thickness, then exposed to heat at a temperature of 300° F for 360 seconds. This coating is normally embossed while still hot to give an attractive surface pattern. 
     EXAMPLE NO. 9 
     An expanding polymeric composition for use as a craft and art paint. 
     
         ______________________________________Ingredients          Parts by Weight______________________________________Water                36.8Hydroxy ethyl phosphate                3.0Attapulgus Clay      10.0Butylene Glycol      2.5Glycol Stearate      1.0Terpolymer latex     4.5Polyspheres BHS      18.0Acrylic Latex        40.0Defoamer a fatty acid                0.4Pigment Color        4.0Propylene Glycol     1.0Hexanol              2.0Hydroxy ethyl cellulose                0.4______________________________________ 
    
     This composition is an expandable paint for arts and crafts, that is painted onto paper, wood, metal or fabric substrates, air-dried, then exposed to heat for 180 seconds at 240° F. The resultant effect is a raised, lofty, or three dimensional structure that has a unique texture. 
     EXAMPLE NO. 10 
     An expanding polymeric composition for use as texture paint in arts and crafts. 
     
         ______________________________________Ingredients          Parts by Weight______________________________________Water                57.22Hydroxy ethyl phosphate                3.0Butylene Glycol      9.0Wood Flour           14.0Terpolymer Latex     9.0Polyspheres BHS      23.0Acrylic Latex        40.0Hydroxy ethyl cellulose                0.22______________________________________ 
    
     This composition is painted on any substrate, then air-dried, then exposed to heat for 180 seconds at 240° F to yield a highly textured surface. 
     The foregoing examples are given to illustrate the nature and operation of this invention, and should not be construed as limiting upon the scope of this invention as defined in the following claims.