Abstract:
An aspect of the present invention is directed to a system for use in oil well drilling applications. The system includes a scintillator material having a cubic garnet host and praseodymium distributed within the host. The scintillator material emits ultraviolet radiation in response to stimulating gamma ray radiation. A radiation detector optically coupled to the scintillator detects the emitted ultraviolet radiation. Another aspect of the invention is a method for detecting oil. A radiation detector is optically coupled to a scintillator material having a cubic garnet host and praseodymium distributed within the host, wherein the praseodymium acts as an activator, and wherein the scintillator material emits ultraviolet radiation in response to stimulating gamma ray radiation. The detector and the scintillator material are lowered below the surface of the earth, and ultraviolet radiation emitted by the scintillator material in response to stimulating gamma ray radiation reflected by hydrogen bearing compounds indicating the presence of oil is detected by the detector.

Description:
BACKGROUND OF THE INVENTION  
       [0001]     This invention relates generally to ultraviolet emitting scintillator materials and, more particularly, to an ultraviolet emitting scintillator material for use in environments such as oil well drilling applications.  
         [0002]     There is currently a need for gamma ray detection in the oil well drilling industry. High energy gamma rays reflected from Hydrogen (H) bearing compounds underground may indicate specific locations which may have oil. A scintillator material which has high ultraviolet luminescence when activated by gamma rays may be desirable for harsh, down-hole environments where shock levels may be near 250 gravitational acceleration (G) and temperatures may approach or exceed 175° Celsius (C.).  
         [0003]     For use in high temperature, harsh environments, the scintillator material may desirably have a number of characteristics. For example, it may be desirable to have a scintillator material which has a sufficient density to absorb as many gamma rays as possible. Second, it may be advantageous for the scintillator material to have a decay time of less than 100 nanoseconds (ns) to limit noise. The scintillator material may also desirably have high transparency in the ultraviolet range, which may be complicated by the number of materials which are opaque in this spectral range. It may also be advantageous for the scintillator material to have low efficiency drop after prolonged exposure to elevated temperatures.  
         [0004]     Known detectors utilize ultraviolet scintillator materials but have disadvantages which may prevent them from being used in harsh conditions. In some instances, the scintillator materials&#39; fluorescent decay times may be too long making the scintillator material impractical for use. In other instances, light yield under gamma ray excitation may be poor. Further, light yield may often decrease with increasing temperature. Other scintillator materials&#39; usable life spans may shorten when exposed to high temperatures, with light yield decreasing the longer that exposure to high temperatures continues. Still other materials have emission wavelengths which do not overlap the sensitivity range of a detector used to measure the emitted radiation.  
         [0005]     Further complicating the choice of a scintillator material appropriate for harsh environments is the difficulty of predicting which materials will emit ultraviolet radiation in a range which overlaps a radiation detector which is also capable of operating in combination with the scintillator material in harsh, high temperature environments.  
         [0006]     These and other drawbacks exist in known systems and techniques.  
       BRIEF DESCRIPTION OF THE INVENTION  
       [0007]     In accordance with an exemplary aspect of the present invention, a system for detection of gamma radiation comprises a scintillator material comprising a cubic garnet host and praseodymium distributed with the host, wherein the praseodymium acts as an activator, and wherein the scintillator material emits ultraviolet radiation in response to the stimulating gamma ray radiation; and a scintillating radiation detector optically coupled to the scintillator material capable of detecting the emitted ultraviolet radiation.  
         [0008]     In accordance with another exemplary aspect of the present invention, a method for oil exploration comprises optically coupling a radiation detector to a scintillator material comprising a cubic garnet host and praseodymium distributed within the host, wherein the praseodymium acts as an activator, and wherein the scintillator material emits ultraviolet radiation in response to stimulating gamma ray radiation; lowering the detector and the scintillator material below the surface of the earth; and detecting ultraviolet radiation emitted by the scintillator material in response to stimulating gamma ray radiation reflected by hydrogen bearing compounds indicating the presence of oil.  
         [0009]     In accordance with another exemplary aspect of the present invention, a method for detecting gamma ray radiation comprises optically coupling a radiation detector to a scintillator material comprising a cubic garnet host and praseodymium distributed within the host, wherein the praseodymium acts as an activator, and wherein the scintillator material emits ultraviolet radiation in response to stimulating gamma ray radiation; exposing the scintillator material to gamma ray radiation; and detecting with the radiation detector ultraviolet radiation emitted by the scintillator material in response to stimulating gamma ray radiation. 
     
    
     BRIEF DESCRIPTION OF THE DRAWINGS  
       [0010]     In order to facilitate a fuller understanding of the present invention, reference is now made to the appended drawings. These drawings should not be construed as limiting the present invention, but are intended to be exemplary only.  
         [0011]      FIG. 1  is a scintillating radiation spectra of Lu 3 Al 5 O 12  with varying mole percent of Pr 3+ .  
         [0012]      FIG. 2  is a chart showing light yield of single crystals of Pr 3+  doped Lu 3 Al 5 O 12  as a function of time during exposure to elevated temperature.  
         [0013]      FIG. 3  is an exemplary radiation detector for use in an exemplary embodiment of a system for detecting oil.  
         [0014]      FIG. 4  is a flowchart for making a radiation detector for use in an exemplary embodiment of a system for detecting oil.  
         [0015]      FIG. 5  is an exemplary embodiment of a system for detecting oil. 
     
    
     DETAILED DESCRIPTION OF EXEMPLARY EMBODIMENTS  
       [0016]     An aspect of the present invention is directed to ultraviolet-emitting scintillator materials for use in oil well drilling applications in harsh, down-hole environments where shock levels may be near 250 gravitational acceleration (G) and/or temperatures may approach or exceed 175° C. Another aspect of the invention is directed to an ultraviolet-emitting scintillator material coupled to a radiation detector.  
         [0017]     The ultraviolet scintillator material according to exemplary embodiments of the present invention generally has a short decay time and little efficiency drop at elevated temperatures. The ultraviolet scintillator material comprises a cubic garnet host doped with an activator. The scintillator material may be a polycrystalline ceramic formed by sintering phosphors of the scintillator material. Alternatively, the scintillator material may be a single crystal formed from such known techniques as the Czochralski method. Light scattering within the cubic garnet host may be reduced by the cubic crystal structure of the host material.  
         [0018]     Garnets are a class of materials with the chemical formula A 3 B 5 O 12  in which the A cations are eight coordinated with oxygens and B cations are either six or four coordinated with oxygens. Suitable elements for site A according to exemplary embodiments of the present invention include lutetium (Lu), yttrium (Y), lanthanum (La) and gadolinium (Gd). Suitable elements for site B according to exemplary embodiments of the present invention include aluminum (Al), gallium (Ga), scandium (Sc) and indium (In). Site A may be occupied by one or more elements, such as Lu 2 Y for example. Site B may also be occupied by one or more elements, such as Ga 2 Al 3  for example. In accordance with exemplary embodiments of the present invention, the luminescence activator is preferably praseodymium.  
         [0019]     The concentration of the activator is expressed herein in terms of mole percent. Mole percent refers to the mole percent of the activator relative to the A site in the garnet A 3 B 5 O 12 . For example, 5.0 mole percent praseodymium in lutetium aluminum garnet means that 5 mole percent of the lutetium is replaced with an equal number of moles of praseodymium.  
         [0020]     The scintillator material of the present invention may be prepared by reacting source compounds via a flux method using 10% AIF 3  flux at about 1450° C. for five hours in a controlled atmosphere to maintain the oxidation state of the activator. Source compounds may include A 2 O 3 , B 2 O 3  and Pr 6 O 11 , for example. The source compounds are preferably 99.99% or higher purity to reduce unknown/uncontrolled impurities in the final composition which can effect radiation damage and quantum efficiency.  
         [0021]     A Pr 3+ -activated garnet material may be made by mixing stoichiometric amounts of oxygen-containing compounds of praseodymium, oxygen-containing compounds of at least one rare-earth metal selected from the group consisting of Gd, Y, La and Lu and oxygen-containing compounds of at least one member selected from the group consisting of Al, Sc, Ga, and In. Typically, at least one fluxing compound such as fluorides of praseodymium, lutetium, aluminum, gallium, of indium are added to the mixture in a quantity sufficient to act as a flux. The mixture is then fired in a reducing atmosphere at a temperature and for a time sufficient to convert the mixture to a rare earth-activated garnet phosphor. The fluxing agent may be added before or during the mixing.  
         [0022]     The oxygen-containing compounds may be mixed together by any mechanical method including, but not limited to, stirring or blending in a high-speed blender or a ribbon blender. The oxygen-containing compounds may be combined and pulverized together in a bowl mill, a hammer mill, or a jet mill. Wet milling may also carry out the mixing. If the mixture is wet, it may be dried first before being fired under a reducing atmosphere at a temperature from about 900° C. to about 1700° C., preferably from about 1000° C. to about 1600° C., more preferably from about 1200° C. to about 1500° C. for a time sufficient to convert all of the mixture to the final garnet composition. The firing may be conducted in a batchwise or continuous process, preferably with a stirring or mixing action to promote good gas-solid contact. The firing time depends on the quantity of the mixture to be fired, the rate of gas conducted through the firing equipment, and the quality of the gas-solid contact in the firing equipment. Typically, a firing time up to about 10 hours is adequate. The reducing atmosphere typically comprises a reducing gas such as hydrogen, carbon monoxide, or a combination thereof, optionally diluted with an inert gas, such as nitrogen, helium, neon, argon, krypton, xenon, or a combination thereof. Alternatively, the mixture may be packed with high-purity carbon particles in the firing furnace so that the carbon particles react with the oxygen of the oxygen-containing compounds, thereby, generating carbon monoxide that is needed to provide the reducing atmosphere  
         [0023]     Samples of (Lu 3 Al 5 O 12 ):Pr3 +  (LAG) were prepared according to the described method from starting materials of Lu 2 O 3 , Al 2 O 3  and Pr 6 O 11 . The mole percent of praseodymium in the LAG ranged from 0.1 to 5.0. During the firing, particles of a coconut charcoal were introduced in a crucible that contained the starting mixture, and the combined assembly was fired at 1450° C. for 5 hours in air. At the end of 5 hours, the solid was cooled at the natural furnace cooling rate. The final phosphor was found to have the required garnet composition.  
         [0024]     These samples were then exposed to x-ray radiation to characterize ultraviolet emitting properties of the scintillator material when exposed to x-ray or gamma ray radiation.  FIG. 1  shows an emission spectrum of the sintered LAG containing varying concentrations of Pr 3+  activator. Highest intensities of emitted ultraviolet radiation occurred when praseodymium concentration was 0.5 mol %. The spectrum is consistent with a transition of electrons from the 4f5d state to the ground states  3 H 4 ,  3 H 5 , and  3 H 6 .  
         [0025]     Results of the scintillator material exposed to x-ray radiation are compared against commercially available reference materials in Table 1. Tests were conducted on the sintered LAG sample having 0.5 mol % Pr 3+ .  
                                                     TABLE 1                                   Stopping   Change in           Peak   Primary   power at   Light Yield:           wavelength   decay   511 keV   150-175° C.       Compound   (nm)   (ns)   (cm −1 )   (%)                                Lu 3 Al 5 O 12 :Pr 3+     310/320/375   19   0.74   −20       BaF 2     310   630   0.45   −75       BaF 2 :Ce 3+     310/325   60   0.45       CsI   305   20   0.55       CeF 3     310/340   27   0.43       Li2HfO3   330/420/610       0.75   −80       BaHfSi3O3   450       0.45   +70       LiAlO 3 :Ce 3+     365   17   0.95       NaI:Tl   410   230   0.34   −50                  
 
         [0026]     As Table 1 shows, the reference materials do not exhibit the combined properties of short peak wavelength, short primary decay, high stopping power, and low change in light yield at elevated temperatures. Peak wavelengths of the scintillator are typically chosen to overlap the sensitivity for a radiation detector, with a wavelength between about 250 and 450 nm, more typically about 250 to about 350 nm, according to one embodiment.  
         [0027]     Alternatively, single crystals of praseodymium doped garnet host may be prepared by the Czochralski method. This known method of crystal growth is accomplished by placing source materials in a high temperature crucible, such as an iridium crucible. The source materials are heated to a temperature above the melting point of the desired crystalline material. This molten material is known as the melt. During growth of the crystal, the melt temperature is held at a value at which an upper portion of the melt is cool enough for a single crystalline material to grow on a seed crystal brought into contact with the melt, but hot enough not to spontaneously nucleate. The seed crystal is then pulled upwards from the melt forming a single crystalline boule.  
         [0028]     Single crystalline boules of Pr 3+  doped LU 3 Al 5 O 12  were grown by the Czochralski method under standard growth conditions for garnet crystals. Source materials for the single crystals were lutetium oxide, aluminum oxide, and praseodymium oxide. Three crystals were grown ranging from 1 to 9 mol % of praseodymium in the melt.  
         [0029]     The single crystalline samples of scintillator material were also exposed to x-ray radiation to determine certain properties of the single crystals in the same way as the sintered materials were. Even as temperature increased from room temperature to 175° C., light output decreased only slightly. Measured primary decay and peak wavelength of the single crystals when exposed to the x-ray radiation substantially corresponded to the values measured with the polycrystalline ceramic scintillator material: a 19 ns primary decay time and a peak wavelength at 310 nm.  
                           TABLE 2                                       Change in Light               Yield: 25-175° C.           Compound   (%)                           LAG   −25%           1% Pr in melt           LAG   −20%           3% Pr in melt           LAG   −18%           9% Pr in melt                      
 
         [0030]     These samples were then maintained at an elevated temperature of 175° C. for 200 hours. As shown in  FIG. 2 , even after prolonged periods at elevated temperatures, light yield remained essentially constant, demonstrating the scintillator material&#39;s ability to withstand extended lengths of time in harsh, high temperature environments such as in down hole oil drilling applications, for example.  
         [0031]     The single crystal samples were also exposed to gamma-ray radiation to measure light yield. These results are summarized below in Table 3, and demonstrate a high transparency of the single crystals in the ultraviolet spectral region.  
                           TABLE 3                                   LAG - Single Crystal   Light Yield           mol % Pr in melt   (photons/MeV)                           1    7,500           9   10,500                      
 
         [0032]     Various detectors may be used to measure ultraviolet radiation emitted by a scintillator material such as photomultiplier tubes (PMTs) and avalanche photodiodes (APDs). APDs are typically high-speed, high sensitivity photodiodes utilizing an internal gain mechanism that functions by applying a reverse voltage. Compared to PIN photodiodes, APDs can typically measure even lower level light and are used in a wide variety of applications requiring high sensitivity.  
         [0033]     APDs are useful as radiation detectors in harsh, high temperature environments. The APD may be constructed of SiC materials. APDs constructed of these materials generally have a sensitivity range of between about 250 to about 350 nm. An APD is a photodiode that operates with a reverse bias voltage that causes a primary photocurrent to undergo amplification by cumulative multiplication of charge carriers. As the reverse-bias voltage increases toward a breakdown, hole-electron pairs are created by absorbed photons. An avalanche effect occurs when the hole-electron pairs acquire sufficient energy to create additional pairs of holes and electrons, thereby achieving a signal gain.  
         [0034]     Epitaxial layers of specific qualities (e.g., doping and thickness) determine operating characteristics (e.g., an avalanche voltage) of devices (e.g., photodiodes) as well as the gain. Ionization coefficients in 4H, which is a specific crystalline phase of SiC, have a positive temperature coefficient, which may be particularly attractive for a SiC photodiode due to the ionization in an avalanche process. 4H SiC is a material with a wide band gap (˜3.2 eV) and a robust chemical nature. This material can absorb ultraviolet light rays, such as are produced by the described scintillator materials. Due at least in part to the wide band gap, the device used in an embodiment of the present invention may operate at high temperatures. The device further uses a p-n junction, via the n-type epitaxial layers and the p-type substrate. This may be a location for avalanche once a high reverse bias has been applied to the device.  
         [0035]     The APD device may include a silicon dioxide (SiO 2 ) passivation layer for providing surface passivation. This SiO 2  layer may also serve as an anti-reflection coating, thereby increasing light collection efficiency and overall detection efficiency of the APD device. In addition, a phosphorous silicate glass (PSG) layer may be deposited on the device to control electrical properties otherwise affected by mobile ions. For example, a PSG layer may be provided to prevent mobile ions from moving throughout the device and lowering device performance. Protective layers of SiO 2  and PSG provide surface passivation and mobile ion trapping, allowing faster and more efficient device operation while extending the lifetime of the device. In addition, methods for metallization may be used to provide low resistance contacts.  
         [0036]      FIG. 3  is an example of a cross sectional view of an avalanche photodiode device in accordance with an embodiment of the present invention.  FIG. 3  shows a cross-section of the APD device with a substrate  110 , a first epitaxial layer  111 , a second epitaxial layer  112  and a third epitaxial layer  114 . The doped substrate  110  serves to provide electrical contact through an anode of the device. The plurality of epitaxial layers may be grown on the substrate for the formation of a desired electric field profile as a function of depth in the material. The first epitaxial layer  111  may serve to terminate defects at a substrate/epitaxial layers interface as well as form a p-n junction. The second epitaxial layer  112  may serve to allow for a relatively large penetration depth of ultraviolet photons, thereby increasing a probability for absorption and carrier generation events. The third epitaxial layer  114  may provide a low resistance contact to a cathode. This configuration may also serve to confine a high electrical field away from a surface of the device and near the p-n junction and further control a field profile.  
         [0037]     The substrate  110  may include a p-doped 4H SiC substrate, the first epitaxial layer  111  may include a p-doped 4H SiC layer, the second epitaxial layer  112  may include an n-doped 4H SiC layer and the third epitaxial layer  114  may include an n-doped SiC layer. More specifically, dopant concentration for substrate  110  may be approximately 5e18 cm −3 ; dopant concentration for the first epitaxial layer  111  may be approximately 1e17 cm −3 , dopant concentration for second epitaxial layer  112  may be approximately 5e16 cm −3  to 6e16 cm −3 ; and dopant concentration for second epitaxial layer  114  may be approximately 5e18 cm −3 . The first epitaxial layer  111  may have a thickness of approximately 1.5 microns, the second epitaxial layer  112  may have a thickness of approximately 3 microns and the third epitaxial layer  114  may have a thickness of approximately 0.4 microns. Other measurements may be implemented as well. For example, the first epitaxial layer  111  may have a thickness of 0.2 to 5 microns with a preferred range of 1 to 2 microns. The second epitaxial layer  112  may have a thickness to facilitate absorption and may range from 2 to 10 microns with a preferred range of 3 to 5 microns. The third epitaxial layer  114  may have a thickness of 0.1 to 2 microns with a preferred range of 0.3 to 0.8 microns.  
         [0038]     Metal electrodes  118  and  120  may comprise a combination of various metals. In particular, metal electrode  118  may include Ni/Ti/Mo/Au at a cathode end. Metal electrode  120  may include Al/Ti/Pt/Au at an anode end. Thin metal layers may be used to form electrodes to both p and n contacts while maintaining a low resistance and minimizing or eliminating a drop in electric field. Other materials providing an ohmic contact may be used. Passivation layers  116  and  122  may comprise SiO 2 , which may have a thickness of 100 Angstroms to several microns (e.g., approximately 5 microns) with a preferred thickness between 1000 Angstroms to 2 microns. In addition, a PSG layer  124  may be implemented to prevent mobile ions from damaging material near the surface and to reduce ultraviolet surface reflection. The PSG layer may have a thickness of approximately 300 Angstroms to 1 micron. Other materials and thickness ranges may be implemented.  
         [0039]     The SiC materials may be processed using a dry ion based etching technique, resulting in a sloped mesa sidewall. For example, a photoresist, ion etch process and/or a Fluorine-based chemistry may be used to form sloped sidewall mesas of the APD device. The sloped mesa shape allows a high electrical field of the APD device to be confined to a center of the device, thereby making an avalanche mechanism scalable with area. In other words, the use of a sloped mesa sidewall for electrical field confinement enables the device to be scaled to different sizes for more or less active area. This is particularly advantageous for concentrating the highest electrical field to be within the device, and not at the edges of the device.  
         [0040]     An APD device for use in an embodiment of the present invention avalanches uniformly over a collecting area of the device, rather than at the device edges. A positive beveled junction of the present invention stretches the electric field out at the bevel edges but not along a uniform planar portion of a p-n junction. As a result, the highest electric field and therefore the avalanche operation occurs in an active area of the device and not along its periphery. As a result, power dissipated during the avalanche operation is spread across a widest possible area thereby avoiding hot spot formation and associated reliability problems. The third epitaxial layer  114  may serve to prevent higher electric fields from reaching a surface through internal manipulation of a depletion region. This device implements a p-n junction at high applied voltages to initialize an electrical avalanche (e.g., breakdown), near an intended operation point of the device. The electrical field in this type of device may be on the order of a few MeV/cm, supported by a depletion region internal to the device and produced by a large external bias. This device takes advantage of the robust chemical nature of SiC materials and its epitaxial layers, to operate at high temperatures (e.g., 150° C. to 200° C.) and/or high vibrations (e.g., 250 G).  
         [0041]     In a separate absorption and multiplication region (SAMR) device, an additional layer may be incorporated between first epitaxial layer  111  and second epitaxial layer  112  wherein the additional layer may be approximately 1.0 micron thick and have an N-dopant concentration of approximately 1e17 cm −3 . This may serve to keep a multiplication region centered around the p-n junction (e.g., where the electric field is highest) apart from an absorption region (e.g., second epitaxial layer  112 ). This may also help to reduce noise observed in the device by minimizing a random absorption phenomena in the multiplication region.  
         [0042]     The avalanche aspect of the exemplary APD device may pose an additional constraint, specifically on the angle of the mesa sidewall. As large electrical fields are required in SiC breakdown and therefore avalanche (e.g., typically in the order to 1-3 MV/cm), it is desirable to confine the electrical field away from the edges of the APD device to minimize current leakage occurring at a surface. A sloped mesa may include sidewalls intersecting a substrate by an angle between approximately 20 to 45 degrees. There are currently wet and dry etch techniques for SiC, however, dry etch techniques are more repeatable and controllable in comparison to wet techniques in general.  
         [0043]     In dry etching techniques, Reactive Ion Etching (RIE) may be implemented to realize a mesa structure. The effects of the etch may be improved by Inductively Coupled Plasma (ICP), which adds a coil to a standard RIE chamber for additional plasma enhancement. Principally, this involves the generation of additional ions near the material surface, which creates an ion rich plasma and one that is spatially more uniform than RIE plasmas. Results may include improvements in etching control (e.g., physical and chemical) and enhanced uniformity.  
         [0044]     Without special treatments to the mask material, the resulting mesa profile may be approximately 0 to 10 degrees variant from the substrate normal, depending on the photoresist (PR) selected and the conditions under which it is treated prior to etching.  
         [0045]     There are at least two methods for creating a mesa with a desired angle. The methods may include reflow of the PR and gray scale masking. PR reflow may be performed by hard baking the photoresist following the exposure, allowing solvents to bake out of the PR and letting the surface become “molten,” thereby changing the shape of the PR. For example, a photoresist may be used to achieve a target etch depth of approximately 4 microns. The photoresist may afford a coating of thicknesses greater than approximately 10 microns, thereby allowing the target etch depth to be reached with a SiC/PR selectivity as low as 0.5 microns, for example.  
         [0046]     Gray scaling takes advantage of a photoresist mask which has been developed in a way to realize several levels of exposure, as determined by transparency or gray scale. Following the exposure through the mask, the photoresist may be developed away, according to a dose of light received through the mask in each area, which may be determined by the transparency of the mask. Thus, the resist may be profiled without heating the resist to a molten state where a desired PR profile may be controllably realized. This profile may be transferred into a semiconductor material as it is etched. The gray scale mask provides a high degree of etching control and repeatability.  
         [0047]      FIG. 4  is a flowchart illustrating a method of fabricating APDs for use in an system in accordance with an embodiment of the present invention. At step  610 , a substrate is prepared which may include preparing a bulk substrate, for example, and a plurality of epitaxial materials. At step  612 , a wafer structure may be cleaned where the wafer structure encompasses the substrate and epitaxial materials of step  610 . At step  614 , mesa patterning may be performed. Mesa patterning may be formed by a photoresist reflow at step  616  or gray scale masking at step  618 . At step  620 , ICP etching may be performed to form a mesa structure. At step  622 , patterning may be performed. In particular, patterning may refer to a photolithography process in which the photoresist is spun onto the wafer at a controlled speed, aligned with a mask, exposed to high energy light, and developed. The resulting photoresist features may include straight sidewalls with photoresist features near vertical. At step  624 , ICP etching may be performed to thin the mesa to a desired thickness. At step  626 , a layer of SiO 2  may be deposited on a surface of the mesa. At step  628 , the SiO 2  layer may be patterned and etched to a desired shape and/or thickness. At step  630 , a cathode and an anode may be formed. The cathode and anode formation may further involve additional steps of patterning, depositing, liftoff, annealing and/or other additional steps. At step  632 , a layer of PSG may be deposited on the surface of the mesa. At step  634 , at least one contact (e.g., a gold contact) may be deposited on the structure.  
         [0048]      FIG. 5  is a drawing of an exemplary embodiment of the invention including a scintillator material and a radiation detector. The above features of the SiC APD device may be used with the scintillator materials describe above which convert gamma ray radiation to ultraviolet radiation, observable directly by the SiC APD. A scintillator material as described in detail above may be implemented for detection of gamma rays down-hole in real time. For example, the SiC APD of the present invention may detect ultraviolet light at approximately 250 to 350 nm, such as that produced by the described scintillator materials.  
         [0049]     An APD  714  may be used in conjunction with a scintillator material  710  to detect gamma ray radiation. System  700  may include a scintillator material  710  as described above for receiving gamma rays, a lens (or lens structure)  712 , APD  714  (e.g., SiC APD) as described in detail above, and amplifier electronics  716 . System  700  may also include a compression plate  718 , shield  720 , and a cable connector  722 . System  700  may be cylindrical in shape to facilitate passage of system  700  through a tube.  
         [0050]     Scintillator material  710  may receive gamma rays, the energy from gamma rays, such as from H bearing compounds underground, for example, which may cause electrons in the Pr 3+  to ascend to higher energy levels. The electrons may return to the ground state, causing an emission of an ultraviolet ray. The ultraviolet ray may be focused by lens  712  (or other lens structure) and received by an APD  714 , such as a SiC APD. Additional electronics, such as amplifier electronics  716  may be used to enhance, amplify or otherwise manipulate the received ultraviolet signal. These components may be incorporated into a tube for down hole deployment in various applications, such as oil well drilling. The system of  FIG. 5  takes advantage of the robust nature of described ultraviolet emitting scintillator materials and a SiC avalanche photodiode, as shown as  714 , operable at high temperatures (e.g., 150° C. to 200° C.) and/or high vibrations (e.g., 250 G).  
         [0051]     The present invention is not to be limited in scope by the specific embodiments described herein. Indeed, various modifications of the present invention, in addition to those described herein, will be apparent to those of ordinary skill in the art from the foregoing description and accompanying drawings. Thus, such modifications are intended to fall within the scope of the following appended claims. Further, although the present invention has been described herein in the context of a particular implementation in a particular environment for a particular purpose, those of ordinary skill in the art will recognize that its usefulness is not limited thereto and that the present invention can be beneficially implemented in other environments for other purposes. Accordingly, the claims set forth below should be construed in view of the full breath and spirit of the present invention as disclosed herein.