Abstract:
An aluminum casting alloy has 8.5-9.5 wt. % silicon, 0.5-2.0 wt. % copper (Cu), 0.27-0.53 wt. % magnesium (Mg), wherein the aluminum casting alloy includes copper and magnesium such that 4.7≦(Cu+10Mg)≦5.8, and other elements, the balance being aluminum. Selected elements may be added to the base composition to give resistance to degradation of tensile properties due to exposure to heat. The thermal treatment of the alloy is calculated based upon wt. % composition to solutionize unwanted phases having a negative impact on properties and may include a three level ramp-up and soak to a final temperature followed by cold water quenching and artificial aging.

Description:
CROSS REFERENCE TO RELATED APPLICATIONS 
       [0001]    This application is a continuation of U.S. patent application Ser. No. 13/662,132, filed Oct. 26, 2012, which claims the benefit of U.S. Provisional Application No. 61/628,320, filed Oct. 28, 2011, and 61/628,321, filed Oct. 28, 2011, each of which are incorporated herein by reference in their entirety. 
     
    
     FIELD 
       [0002]    The present invention relates to aluminum alloys, and more particularly, to aluminum alloys used for making cast products. 
       BACKGROUND 
       [0003]    Aluminum alloys are widely used, e.g., in the automotive and aerospace industries, due to a high performance-to-weight ratio, favorable corrosion resistance and other factors. Various aluminum alloys have been proposed in the past that have characteristic combinations of properties in terms of weight, strength, castability, resistance to corrosion, cost, etc. Improvements in alloys to exhibit an improved combination of properties, e.g., that render them more suitable for one or more applications, remain desirable. 
       SUMMARY 
       [0004]    The disclosed subject matter relates to improved aluminum casting alloys (also known as foundry alloys) and methods for producing same. More specifically, the present application relates to an aluminum casting alloy having: 8.5-9.5 wt. % silicon, 0.5-2.0 wt. % copper (Cu), 0.27-0.53 wt. % magnesium (Mg), wherein the aluminum casting alloy includes copper and magnesium such that 4.7≦(Cu+10Mg)≦5.8, up to 5.0 wt. % zinc, up to 1.0 wt. % silver, up to 0.30 wt. % titanium, up to 1.0 wt. % nickel, up to 1.0 wt. % hafnium, up to 1.0 wt. % manganese, up to 1.0 wt. % iron, up to 0.30 wt. % zirconium, up to 0.30 wt. % vanadium, up to 0.10 wt. % of one or more of strontium, sodium, antimony and calcium and other elements being ≦0.04 wt. % each and ≦0.12 wt. % in total, the balance being aluminum. 
         [0005]    In one approach, the aluminum casting alloy includes 1.35-2.0 wt. % copper and 0.27-0.445 wt. % magnesium. 
         [0006]    In one approach, the aluminum casting alloy includes 0.5-0.75 wt. % copper and 0.395-0.53 wt. % magnesium. 
         [0007]    In one approach, the aluminum casting alloy includes 0.75-1.35 wt. % copper and 0.335-0.505 wt. % magnesium. 
         [0008]    In one approach the aluminum casting alloy includes copper and magnesium such that 5.0≦(Cu+10Mg)≦5.5. 
         [0009]    In one approach, the aluminum casting alloy includes copper and magnesium such that 5.1≦(Cu+10Mg)≦5.4. 
         [0010]    In one approach, the aluminum casting alloy contains ≦0.25 wt. % zinc. 
         [0011]    In one approach, the aluminum casting alloy contains 0.5 wt. to 5.0 wt. % zinc. 
         [0012]    In one approach, the aluminum casting alloy contains ≦0.01 wt. silver. 
         [0013]    In one approach, the aluminum casting alloy contains 0.05-1.0 wt. % silver. 
         [0014]    In one approach, the aluminum casting alloy is subjected to a solution heat treatment at TH followed by a cold water quench, where TH (° C.)=570−10.48*Cu-71.6*Mg-1.3319*Cu*Mg-0.72*Cu*Cu+72.95*Mg*Mg, based on Mg and Cu content in wt %, within the range defined by a lower limit for TH:TQ=533.6−20.98*Cu+88.037*Mg+33.43*Cu*Mg-0.7763*Cu*Cu-126.267*Mg*Mg and an upper limit for TH:TS=579.2−10.48*Cu-71.6*Mg-1.3319*Cu*Mg-0.72*Cu*Cu+72.95*Mg*Mg. 
         [0015]    In one approach, the casting aluminum casting alloy contains 0.1-0.12 wt. % titanium. 
         [0016]    In one approach, the casting aluminum casting alloy contains 0.12-0.14 wt. % vanadium. 
         [0017]    In one approach, the casting aluminum casting alloy contains 0.08-0.19 wt. % zirconium. 
         [0018]    In one approach, the casting aluminum casting alloy contains 0.14-0.3 wt. % manganese. 
         [0019]    In one approach, the casting aluminum casting alloy contains 0.15-0.57 wt. % iron. 
         [0020]    In one approach, the casting aluminum casting alloy contains 0.1-0.12 wt. % vanadium. 
         [0021]    In one approach, the casting aluminum casting alloy contains 0.11-0.13 wt. % zirconium. 
         [0022]    In one approach, the casting aluminum casting alloy contains 0.27-0.3 wt. % nickel. 
         [0023]    In one approach, the casting aluminum casting alloy contains 0.15-0.33 wt. % iron. 
         [0024]    In one approach, the casting aluminum casting alloy contains 0.03-0.15 wt. % manganese. 
         [0025]    In one approach, the casting aluminum casting alloy contains 0.05-0.2 wt. % hafnium. 
         [0026]    In one approach, the casting aluminum casting alloy contains 0.1-0.12 wt. % vanadium. 
         [0027]    In one approach, the casting aluminum casting alloy contains 0.012-0.04 wt. % zirconium. 
         [0028]    In one approach, a method of selecting a solutionization temperature includes the steps of:
       (A) Calculating the formation temperature of all dissolvable constituent phases in an aluminum alloy, and identifying a dissolvable constituent phase with the highest formation temperature;   (B) Calculating the equilibrium solidus temperature of an aluminum alloy;   (C) Defining a region in compositional space where the highest formation temperature of dissolvable constituent phases by at least 10° C. below the solidus temperature; and   (D) Selecting a solutionization temperature within said defined region.       
 
         [0033]    In one approach, the constituent phases are the phases formed during solidification. 
         [0034]    In one approach, the identified steps A-D include:
       (A) Calculating the formation temperatures of all dissolvable constituent phases comprised of Al, Cu, Mg and Si, and identify a dissolvable constituent phase with the highest formation temperature; and   (B) Calculating the solidus temperature of an alloy comprised of Al, Cu, Mg, Si and all other alloying elements; and   (C) Defining a region in Al—Cu—Mg—Si space where the highest formation temperature of dissolvable constituent phases is at least 10° C. below the solidus temperature; and   (D) Selecting a solutionization temperature within said defined region.       
 
         [0039]    In one approach, the dissolvable constituent phases are Q-AlCuMgSi, Mg 2 Si, Al 2 Cu, S—AlCuMg, etc. and the dissolvable constituent phase with the highest formation temperature is Q-AlCuMgSi phase in an Al Si Mg Cu alloy. 
         [0040]    In one approach, the formation temperature of dissolvable constituent phases and solidus temperature are determined by computational thermodynamics. 
         [0041]    In one approach, the formation temperature of dissolvable constituent phases and solidus temperature are calculated using Pandat™ Software and PanAluminum™ Database. 
         [0042]    In one approach, an alloy is heat treated by heating the alloy above the formation temperature of all dissolvable constituent phases, but below the calculated solidus temperature. 
         [0043]    In one approach, the alloy is an Al Si Mg Cu alloy and the dissolvable constituent phase with the highest formation temperature is Q-AlCuMgSi phase. 
         [0044]    In one approach, a method for preparation of an alloy, includes the steps of:
       (A) Identifying dissolvable constituent phases present in the alloy;   (B) Identifying a range of temperatures which promotes the solutionization of the dissolvable constituent phases during heat treatment;   (C) Allowing the alloy to solidify;   (D) Heating the solidified alloy to a temperature in the range identified in step (B) and below the solidus temperature of the alloy.       
 
         [0049]    In one approach, a first elemental component and a second elemental component in their relative wt. % amounts in the alloy contribute to properties of the alloy as well as contribute to determining the formation temperature of all dissolvable constituent phases in the alloy and further comprising the steps of ascertaining a range of target properties for the alloy as effected by the first and second elemental components; ascertaining a range of relative wt % amounts for the first and second elemental components that provides the range of target properties prior to step (B) of identifying a range of temperatures. 
         [0050]    In one approach, the first elemental component is Cu and the second elemental component is Mg in an Al Si Mg Cu alloy. 
     
    
     
       BRIEF DESCRIPTION OF THE DRAWINGS 
         [0051]      FIG. 1  is a graph of phase equilibria involving (Al) and liquid in an Al—Cu—Mg—Si system. 
           [0052]      FIG. 2  is a graph of the effect of Cu additions on the solidification path of Al-9% Si-0.4% Mg-0.1% Fe alloy. 
           [0053]      FIG. 3  is a graph of the effect of Cu content on phase fractions in Al-9%-0.4% Mg-0.1% Fe-x % Cu alloys. 
           [0054]      FIG. 4  is a graph of the effect of Cu and Mg content on the Q-phase formation temperature of Al-9% Si—Mg—Cu alloys. 
           [0055]      FIG. 5  is a graph of the effect of Mg and Cu content on the equilibrium solidus temperature of Al-9% Si—Mg—Cu alloys. 
           [0056]      FIG. 6  is a graph of the effect of Mg and Cu content on the equilibrium solidus temperature (T S ) and Q-phase formation temperature (T Q ) of Al-9% Si—Mg—Cu alloys. 
           [0057]      FIG. 7  is a graph of the effect of zinc and silicon on the fluidity of Al-x % Si-0.5% Mg-y % Zn alloys 
           [0058]      FIG. 8  is an SEM (scanning electron micrograph) @200× magnification, showing spherical Si particles and un-dissolved Fe-containing particles. 
           [0059]      FIGS. 9 a - b    are photographs of undissolved Fe-containing particles in the investigated alloys. 
           [0060]      FIGS. 10 a - d    are graphs of the effect of aging condition on tensile properties of the Al-9Si-0.5Mg alloy. 
           [0061]      FIGS. 11 a - d    are graphs of the effect of Cu on tensile properties of the Al-9% Si-0.5% Mg alloy. 
           [0062]      FIGS. 12 a - d    are graphs of the effect of Cu and Zn on tensile properties of the Al-9% Si-0.5% Mg alloy. 
           [0063]      FIGS. 13 a - d    are graphs of the effect of Mg content on tensile properties of the Al-9% Si-1.25% Cu—Mg alloy. 
           [0064]      FIGS. 14 a - d    are graphs of the effect of Ag on tensile properties of the Al-9% Si-0.35% Mg-1.75% Cu alloy. 
           [0065]      FIGS. 15 a - d    are graphs of tensile properties for six alloys aged for different times at an elevated temperature, as described in the disclosure. 
           [0066]      FIG. 16  is a graph of Charpy impact energy (CIE) vs. yield strength for five alloys aged for different times at an elevated temperature. 
           [0067]      FIG. 17  is a graph of S-N fatigue curves of selected alloys aged at 155° C. for 15 hours. Smooth, Axial; stress ratio=−1. 
           [0068]      FIG. 18  is a graph of S-N fatigue curves of selected alloys aged at 155° C. for 60 hours. Smooth, Axial; stress ratio=−1. 
           [0069]      FIG. 19 a - d -23 a - d    are optical micrographs of cross-sections of samples of five alloys as cast and machined and aged for two different time periods at an elevated temperature after 6-hour ASTM G110. 
           [0070]      FIG. 24  is a graph of depth of attack of selected alloys aged for different time periods on the as-cast and machined surfaces after a 6-hour G110 test. 
           [0071]      FIG. 25  is a graph of Mg and Cu content correlated to strength and ductility for Al-9Si—Mg—Cu alloys. 
           [0072]      FIG. 26  is a graph of tensile properties of a specific alloy (alloy 9) after exposure to high temperatures. 
           [0073]      FIGS. 27 a  and 27 b    are scanning electron micrographs of a cross-section of a sample of alloy 9 prior to exposure to high temperatures. 
           [0074]      FIG. 28  is a tensile property graph of alloy 9 and A356 alloy. 
           [0075]      FIGS. 28 a - e    are a series of scanning electron micrographs of a cross-section of alloy 9 after exposure to increasing temperatures correlated to the tensile property graph of alloy 9 and A356 alloy. 
           [0076]      FIG. 29  is a graph of yield strength at room temperature for various alloys. 
           [0077]      FIG. 30  is a graph of yield strength after exposure to 175° C. for various alloys. 
           [0078]      FIG. 31  is a graph of yield strength after exposure to 300° C. for various alloys. 
           [0079]      FIG. 32  is a graph of yield strength after exposure to 300° C. for various alloys. 
           [0080]      FIG. 33  is a graph of yield strength after exposure to 300° C. for various alloys. 
           [0081]      FIG. 34  is a graph of yield strength after exposure to 300° C. for various alloys. 
       
    
    
     DETAILED DESCRIPTION OF EXEMPLARY EMBODIMENTS 
     Example 1 
     High Performance AlSiCuMg Cast Alloys 
     1.1 Alloy Development Methods Based on Computational Thermodynamics 
       [0082]    To improve the performances of Al—Si—Mg—Cu cast alloys, a novel alloy design method was used and is described as follows: 
         [0083]    In Al—Si—Mg—Cu casting alloys, increasing Cu content can increase the strength due to higher amount of θ′-Al 2 Cu and Q′ precipitates but reduce ductility, particularly if the amount of un-dissolved constituent Q-phase increases.  FIG. 1  shows the calculated phase diagram of the Al—Cu—Mg—Si quaternary system, as shown in X. Yan,  Thermodynamic and solidification modeling coupled with experimental investigation of the multicomponent aluminum alloys.  University of Wisconsin—Madison, 2001, which is incorporated in its entirety by reference herein.  FIG. 1  shows the three phase equilibria in ternary systems and the four phase equilibria quaternary monovariant lines. Points A, B, C, D, E and F are five phase invariant points in the quaternary system. Points T 1  to T 6  are the four-phase invariant points in ternary systems and B 1 , B 2  and B 3  are the three phase invariant points in binary systems. The formation of Q-phase (AlCuMgSi) constituent particles during solidification is almost inevitable for an Al—Si—Mg alloy containing Cu since Q-phase is involved in the eutectic reaction (invariant reaction B). If these Cu-containing Q-phase particles cannot be dissolved during solution heat treatment, the strengthening effect of Cu will be reduced and the ductility of the casting will also suffer. 
         [0084]    In order to minimize/eliminate un-dissolved Q-phase (AlCuMgSi) and maximize solid solution/precipitation strengthening, the alloy composition, solution heat treatment and aging practice should be optimized. In accordance with the present disclosure, a thermodynamic computation was used to select alloy composition (mainly Cu and Mg content) and solution heat treatment for avoiding un-dissolved Q-phase particles. Pandat thermodynamic simulation software and the PanAluminum database LLC, Computherm, Pandat Software and PanAluminum Database. http://www.computherm.com were used to calculate these thermodynamic data. 
         [0085]    The inventors of the present disclosure recognize that adding Cu to Al—Si—Mg cast alloys will change the solidification sequence.  FIG. 2  shows the predicted effect of 1% Cu (all compositions in this report are in weight percent) on the solidification path of Al-9% Si-0.4% Mg-0.1% Fe. More particularly, the solidification temperature range is significantly increased with the addition of 1% Cu due to the formation of Cu-containing phases at lower temperatures. For the Al-9% Si-0.4% Mg-0.1% Fe-1% Cu alloy, Q-AlCuMgSi formed at ˜538° C. and θ-Al 2 Cu phase formed at ˜510° C. The volume fraction of each constituent phase and their formation temperatures are also influenced by the Cu content. 
         [0086]      FIG. 3  shows the predicted effect of Cu content on phase fractions in Al-9% Si-0.4% Mg-0.1% Fe-x % Cu alloys. As the Cu content increases, the amount of θ-Al 2 Cu and Q-AlCuMgSi increases while the amount of Mg 2 Si and π-AlFeMgSi decreases. In alloys with more than 0.7% Cu, Mg 2 Si phase will not form during solidification. The amount of Q-AlCuMgSi is also limited by the Mg content in the alloy if the Cu content is more than 0.7%. 
         [0087]    The Q-AlCuMgSi phase formation temperature (T Q ) in Al-9% Si—Mg—Cu alloys is a function of Cu and Mg content. The “formation temperature” of a constituent phase is defined as the temperature at which the constituent phase starts to form from the liquid phase.  FIG. 4  shows the predicted effects of Cu and Mg content on the formation temperature of Q-AlCuMgSi phase. The formation temperature of Q-AlCuMgSi phase decreases with increasing Cu content; but increases with increasing Mg content. 
         [0088]    In accordance with the present disclosure, in order to completely dissolve all the as-cast Q-AlCuMgSi phase particles, the solution heat treatment temperature (T H ) needs to be controlled above the formation temperature of the Q-AlCuMgSi phase, i.e., T H &gt;T Q . The upper limit of the solution heat treatment temperature is the equilibrium solidus temperature (T S ) in order to avoid re-melting. As a practical measure, the solution heat treatment temperature is controlled to be at least 5 to 10° C. below the solidus temperature to avoid localized melting and creation of metallurgical flaws known in the art as rosettes. Hence, in practice, the following relationship is established: 
         [0000]        T   S -10° C.&gt; T   H   &gt;T   Q   (1)
 
         [0089]    In accordance with the present disclosure, to achieve this criterion, the alloy composition, mainly the Cu and Mg contents, should be selected so that the formation temperature of Q-AlCuMgSi phase is lower than the solidus temperature.  FIG. 5  shows the predicted effects of Cu and Mg content on the solidus temperature of Al-9% Si—Cu—Mg alloys. As expected, the solidus temperature decreases as the Cu and Mg content increases. It should be noted that Mg content increases the formation temperature of the Q-AlCuMgSi phase but decreases the solidus temperature as indicated in  FIG. 6 . The Q-AlCuMgSi phase formation temperature surface and the (T S -10° C.) surface (10° C. below the solidus temperature surface) are superimposed in  FIG. 6 . These two surfaces intersect along the curve A-B-C. The area that meets the criterion of Equation (1) is on the right hand side of curve A-B-C, i.e., T Q &lt;T S -10° C. Projection of the curve A-B-C to the Cu—Mg composition plane yields the center line Cu+10Mg=5.25 of the preferred composition boundary, as shown in  FIG. 25 . The lower boundary, Cu+10Mg=4.73, was defined by the intersection of the Q-AlCuMgSi phase formation temperature surface and the (T S -15° C.) surface (15° C. below the solidus temperature surface). The upper boundary, Cu+10Mg=5.78, was defined by the intersection of the Q-AlCuMgSi phase formation temperature surface and the (T S -5° C.) surface (5° C. below the solidus temperature surface). For Al-9% Si-0.1% Fe-x % Cu-y % Mg alloys, Q-AlCuMgSi phase particles can be completely dissolved during solution heat treatment when the Cu and Mg contents are controlled within these boundaries. 
         [0000]    In accordance with the present disclosure, the preferred Mg and Cu content to maximize the alloy strength and ductility is shown in  FIG. 25 . 
         [0090]    The preferred relationship of Mg and Cu content is defined by: 
         [0000]      Cu+10Mg=5.25 with 0.5&lt;Cu&lt;2.0. 
         [0091]    The upper bound is Cu+10Mg=5.8 and the lower bound is Cu+10Mg=4.7. 
         [0092]    The foregoing approach allows the selection of a solutionization temperature by (i) calculating the formation temperature of all dissolvable constituent phases in an aluminum alloy; (ii) calculating the equilibrium solidus temperature of an aluminum alloy; (iii) defining a region in Al—Cu—Mg—Si space where the formation temperature of all dissolvable constituent phases is at least 10° C. below the solidus temperature. The Al—Cu—Mg—Si space is defined by the relative % composition of each of Al, Cu, Mg and Si and the associated solidus temperatures for the range of relative composition. For a given class of alloy, e.g., Al—Cu—Mg—Si, the space may be defined by the solidus temperature associated with relative composition of two elements of interest, e.g., Cu and Mg, which are considered relative to their impact on the significant properties of the alloy, such as tensile properties. In addition, the solutionizing temperature may be selected to diminish the presence of specific phases, e.g., that have a negative impact on significant properties, such as, tensile properties. The alloy, e.g., after casting, may be heat treated by heating above the calculated formation temperature of the phase that needs to be completely dissolved after solution heat treatment, e.g., the Q-AlCuMgSi phase, but below the calculated equilibrium solidus temperature. The formation temperature of the phase that needs to be completely dissolved after solution heat treatment and solidus temperatures may be determined by computational thermodynamics, e.g., using Pandat™ software and PanAluminum™ Database available from CompuTherm LLC of Madison, Wis. 
       1.2 Composition Selection for Tensile Bar Casting 
       [0093]    Based on the foregoing analysis, several Mg and Cu content combinations were selected as given in Table 3. Additionally, studies by the present inventors have indicated that an addition of zinc with a concentration greater than 3 wt % to Al—Si—Mg—(Cu) alloys can increase both ductility and strength of the alloy. As shown in  FIG. 7 , zinc can also increase the fluidity of Al—Si—Mg alloys. Thus, an addition of zinc (4 wt %) was also evaluated. It has also been reported L. A. Angers,  Development of Advanced I/M  2 xxx Alloys for High Speed Civil Transport Applications , Alloy Technology Division Report No. AK92, 1990 Apr. 16 that an addition of Ag can accelerate age-hardening of high Cu-containing (&gt;˜1.5 wt %) aluminum alloys, and increase the tensile strength at room temperature and elevated temperature. An addition of Ag (0.5 wt %) was also included in alloys with higher Cu content such as 1.75 wt % Cu. Hence, ten alloy compositions were selected for evaluation. The target compositions of these alloys are given in Table 3. It should be noted that alloy 1 in Table 3 is the baseline alloy, A359. 
         [0000]    
       
         
               
             
               
               
             
               
               
               
               
               
               
               
               
               
               
             
               
               
               
               
               
               
               
               
               
               
               
             
           
               
                 TABLE 3 
               
             
             
               
                   
               
               
                 Target Compositions 
               
             
          
           
               
                   
                 Target Composition (wt %) 
               
             
          
           
               
                 Alloy 
                 Si 
                 Cu 
                 Mg 
                 Zn 
                 Ag 
                 Fe 
                 Sr* 
                 Ti 
                 B 
               
               
                   
               
             
          
           
               
                 1 
                 Al—9Si—0.5Mg 
                 9 
                 0 
                 0.5 
                 0 
                   
                 &lt;0.1 
                 0.0125 
                 0.04 
                 0.003 
               
               
                 2 
                 Al—9Si—0.35Mg—0.75Cu—4Zn 
                 9 
                 0.75 
                 0.35 
                 4 
                   
                 &lt;0.1 
                 0.0125 
                 0.04 
                 0.003 
               
               
                 3 
                 Al—9Si—0.45Mg—0.75Cu—4Zn 
                 9 
                 0.75 
                 0.45 
                 4 
                   
                 &lt;0.1 
                 0.0125 
                 0.04 
                 0.003 
               
               
                 4 
                 Al—9Si—0.45Mg—0.75Cu 
                 9 
                 0.75 
                 0.45 
                 0 
                   
                 &lt;0.1 
                 0.0125 
                 0.04 
                 0.003 
               
               
                 5 
                 Al—9Si—0.5Mg—0.75Cu 
                 9 
                 0.75 
                 0.5 
                 0 
                   
                 &lt;0.1 
                 0.0125 
                 0.04 
                 0.003 
               
               
                 6 
                 Al—9Si—0.35Mg—1.25Cu 
                 9 
                 1.25 
                 0.35 
                 0 
                   
                 &lt;0.1 
                 0.0125 
                 0.04 
                 0.003 
               
               
                 7 
                 Al—9Si—0.45Mg—1.25Cu 
                 9 
                 1.25 
                 0.45 
                 0 
                   
                 &lt;0.1 
                 0.0125 
                 0.04 
                 0.003 
               
               
                 8 
                 Al—9Si—0.55Mg—1.25Cu 
                 9 
                 1.25 
                 0.55 
                 0 
                   
                 &lt;0.1 
                 0.0125 
                 0.04 
                 0.003 
               
               
                 9 
                 Al—9Si—0.35Mg—1.75Cu 
                 9 
                 1.75 
                 0.35 
                 0 
                   
                 &lt;0.1 
                 0.0125 
                 0.04 
                 0.003 
               
               
                 10 
                 Al—9Si—0.35Mg—1.75Cu—0.5Ag 
                 9 
                 1.75 
                 0.35 
                 0 
                 0.5 
                 &lt;0.1 
                 0.0125 
                 0.04 
                 0.003 
               
               
                   
               
             
          
         
       
     
         [0094]    A modified ASTM tensile-bar mold was used for the casting. A lubricating mold spray was used on the gauge section, while an insulating mold spray was used on the remaining portion of the cavity. Thirty castings were made for each alloy. The average cycle time was about two minutes. The actual compositions investigated are listed in Table 4, below. 
         [0000]                                                                                                                      TABLE 4                   Actual Compositions                Actual Composition (wt %)            Alloy   Si   Cu   Mg   Zn   Ag   Fe   Sr*   Ti   B                    1   Al—9Si—0.5Mg   8.87   0.021   0.48   0       0.079   0.0125   0.05   0.003       2   Al—9Si—0.35Mg—0.75Cu—4Zn   9.01   0.75   0.37   4.03       0.077   0.0125   0.031   0.003       3   Al—9Si—0.45Mg—0.75Cu—4Zn   9.09   0.75   0.46   4.02       0.081   0.0125   0.04   0.003       4   Al—9Si—0.45Mg—0.75Cu   9.18   0.76   0.45           0.083   0.0125   0.042   0.003       5   Al—9Si—0.5Mg—0.75Cu   9.02   0.77   0.49           0.081   0.0125   0.013   0.003       6   Al—9Si—0.35Mg—1.25Cu   9.02   1.25   0.34           0.088   0.0125   0.03   0.003       7   Al—9Si—0.45Mg—1.25Cu   9.11   1.28   0.44           0.082   0.0125   0.04   0.003       8   Al—9Si—0.55Mg—1.25Cu   8.99   1.27   0.53           0.1   0.0125   0.04   0.003       9   Al—9Si—0.35Mg—1.75Cu   9.29   1.83   0.37           0.08   0.0125   0.048   0.003       10   Al—9Si—0.35Mg—1.75Cu—0.5Ag   8.88   1.78   0.35       0.5   0.081   0.0125   0.044   0.003                    
The actual compositions are very close to the target compositions. The hydrogen content (single testing) of the castings is given in Table 5.
 
         [0000]    
       
         
               
             
               
               
               
             
               
               
               
             
           
               
                 TABLE 5 
               
             
             
               
                   
               
               
                 Hydrogen Content of the Castings 
               
             
          
           
               
                   
                 Alloy 
                 H Content (ppm) 
               
               
                   
                   
               
             
          
           
               
                 1 
                 Al—9Si—0.5Mg 
                 0.14 
               
               
                 2 
                 Al—9Si—0.35Mg—0.75Cu—4Zn 
                 0.11 
               
               
                 3 
                 Al—9Si—0.45Mg—0.75Cu—4Zn 
                 0.19 
               
               
                 4 
                 Al—9Si—0.45Mg—0.75Cu 
                 0.11 
               
               
                 5 
                 Al—9Si—0.5Mg—0.75Cu 
                 0.14 
               
               
                 6 
                 Al—9Si—0.35Mg—1.25Cu 
                 0.15 
               
               
                 7 
                 Al—9Si—0.45Mg—1.25Cu 
                 0.13 
               
               
                 8 
                 Al—9Si—0.55Mg—1.25Cu 
                 0.16 
               
               
                 9 
                 Al—9Si—0.35Mg—1.75Cu 
                 0.13 
               
               
                 10 
                 Al—9Si—0.35Mg—1.75Cu—0.5Ag 
                 Not measured 
               
               
                   
               
               
                 Note: 
               
               
                 alloy 3 was degassed with porous lance; all other alloys were degassed using a rotary degasser. 
               
             
          
         
       
     
       1.3 the Preferred Solution Heat Treat Temperature as a Function of Cu and Mg 
       [0095]    To dissolve all the Q-AlCuMgSi phase particles, the solution heat treatment temperature should be higher than the Q-AlCuMgSi phase formation temperature. Table 6 lists the calculated final eutectic temperature, Q-phase formation temperature and solidus temperature using the targeted composition of the ten alloys investigated. 
         [0000]    
       
         
               
             
               
               
               
               
             
               
               
               
               
               
             
           
               
                 TABLE 6 
               
             
             
               
                   
               
               
                 Calculated Final Eutectic Temperature, Q-phase Formation Temperature and Solidus 
               
               
                 Temperature for Ten Investigated Casting Alloys 
               
             
          
           
               
                   
                   
                 Q-phase 
                   
               
               
                   
                 Final eutectic 
                 forming 
                 Solidus 
               
               
                 Alloy 
                 temperature, C. 
                 temperature, C. 
                 temperature, C. 
               
               
                   
               
             
          
           
               
                 1 
                 Al—9Si—0.5Mg 
                 560 
                 — 
                 563 
               
               
                 2 
                 Al—9Si—0.35Mg—0.75Cu—4Zn 
                 470 
                 518 
                 540 
               
               
                 3 
                 Al—9Si—0.45Mg—0.75Cu—4Zn 
                 470 
                 518 
                 543 
               
               
                 4 
                 Al—9Si—0.45Mg—0.75Cu 
                 510 
                 541 
                 554 
               
               
                 5 
                 Al—9Si—0.5Mg—0.75Cu 
                 510 
                 541 
                 553 
               
               
                 6 
                 Al—9Si—0.35Mg—1.25Cu 
                 510 
                 533 
                 552 
               
               
                 7 
                 Al—9Si—0.45Mg—1.25Cu 
                 510 
                 536 
                 548 
               
               
                 8 
                 Al—9Si—0.55Mg—1.25Cu 
                 510 
                 538 
                 545 
               
               
                 9 
                 Al—9Si—0.35Mg—1.75Cu 
                 510 
                 528 
                 543 
               
               
                 10 
                 Al—9Si—0.35Mg—1.75Cu—0.5Ag 
                 510 
                 526 
                 543 
               
               
                   
               
             
          
         
       
     
         [0096]    Based on the above mentioned information, two solution heat treatment practices were defined and used. Alloys 2, 3, 9 and 10 had lower solidus temperature and/or lower final eutectic/Q-phase formation temperature than others. Hence a different SHT practice was used. 
         [0097]    The practice I for alloys 2, 3, 9 and 10 was:
       1.5 hour log heat-up to 471° C.   2 hour soak at 471° C.   0.5 hour ramp up to 504° C.   4 hour soak at 504° C.   0.5 hour ramp up to T H      6 hour soak at T H      CWQ (Cold Water Quench)
 
and practice II for other six alloys was:
   1.5 hour log heat-up to 491° C.   2 hour soak at 491° C.   0.25 hour ramp up to 504° C.   4 hour soak at 504° C.   0.5 hour ramp up to T H      6 hour soak at T H      CWQ (Cold Water Quench)       
 
         [0112]    The final step solution heat treatment temperature T H  was determined from following equation based on Mg and Cu content: 
         [0000]        T   H  (° C.)=570−10.48*Cu-71.6*Mg-1.3319*Cu*Mg-0.72*Cu*Cu+72.95*Mg*Mg,  (2)
 
         [0000]    Where, Mg and Cu are magnesium and copper contents, in wt % 
         [0113]    A lower limit for T H  is defined by: 
         [0000]        T   Q =533.6−20.98*Cu+88.037*Mg+33.43*Cu*Mg-0.7763*Cu*Cu-126.267*Mg*Mg  (3)
 
         [0114]    An upper limit for T H  is defined by: 
         [0000]        T   S =579.2−10.48*Cu-71.6*Mg-1.3319*Cu*Mg-0.72*Cu*Cu+72.95*Mg*Mg  (4)
 
         [0115]    The microstructure of the solution heat treated specimens was characterized using optical and SEM microscopy. There were no un-dissolved Q-phase particles detected in all the Cu-containing alloys investigated.  FIG. 8  shows the microstructure of the Al-9% Si-0.35% Mg-1.75% Cu alloy (alloy #9) in the T 6  temper. Si particles were all well-spheroidized. Some un-dissolved particles were identified as β-AlFeSi, π-AlFeMgSi and Al 7 Cu 2 Fe phases. The morphologies of these un-dissolved phases are shown in  FIG. 9  at higher magnification. 
       1.4 Experimental Results 
     1.4.1 Property Characterization 
       [0116]    Tensile properties were evaluated according to the ASTM B557 method. Test bars were cut from the modified ASTM B108 castings and tested on the tensile machine without any further machining. All the tensile results are an average of five specimens. Toughness of selected alloys was evaluated using the un-notched Charpy Impact test, ASTM E23-07a. The specimen size was 10 mm×10 mm×55 mm machined from the tensile-bar casting. Two specimens were measured for each alloy. 
         [0117]    Smooth S-N fatigue test was conducted according to the ASTM E606 method. Three stress levels, 100 MPa, 150 MPa, and 200 MPa were evaluated. The R ratio was −1 and the frequency was 30 Hz. Three replicated specimens were tested for each condition. Test was terminated after about 10 7  cycles. Smooth fatigue round specimens were obtained by slightly machining the gauge portion of the tensile bar casting. 
         [0118]    Corrosion resistance (type-of-attack) of selected conditions was evaluated according to the ASTM G110 method. Corrosion mode and depth-of-attack on both the as-cast surface and machined surface were assessed. 
         [0119]    All the raw test data including tensile, Charpy impact and S-N fatigue are given in Tables 7 to 9. A summary of the findings is given in the following sections. 
         [0000]    
       
         
               
             
               
               
               
               
             
               
               
               
               
               
               
               
               
               
               
               
               
               
             
               
               
               
               
               
               
               
               
               
               
               
               
               
             
               
               
               
               
               
               
               
               
               
               
               
               
               
               
             
           
               
                 TABLE 7 
               
             
             
               
                   
               
               
                 Mechanical properties of various alloys aged at 155° C. for different times* 
               
             
          
           
               
                   
                 Aged at 155° C. for 15 hrs 
                 Aged at 155° C. for 30 hrs 
                 Aged at 155° C. for 60 hrs 
               
             
          
           
               
                   
                 UTS 
                 TYS 
                 E 
                 Q 
                 UTS 
                 TYS 
                 E 
                 Q 
                 UTS 
                 TYS 
                 E 
                 Q 
               
             
          
           
               
                 Alloy 
                 (MPa) 
                 (MPa) 
                 (%) 
                 (MPa) 
                 (MPa) 
                 (MPa) 
                 (%) 
                 (MPa) 
                 (MPa) 
                 (MPa) 
                 (%) 
                 (MPa) 
               
               
                   
               
             
          
           
               
                 1. 
                 Al—9Si—0.5Mg 
                 405.8 
                 323.3 
                 8.3 
                 543.2 
                 398.5 
                 326.5 
                 6.5 
                 520.4 
                 398.7 
                 340.2 
                 5.3 
                 507.7 
               
               
                 2. 
                 Al—9Si—0.35Mg— 
                 431.5 
                 342.0 
                 5.5 
                 542.6 
                 433.5 
                 358.0 
                 4.5 
                 531.5 
                 446.8 
                 366.0 
                 6.5 
                 568.7 
               
               
                   
                 0.75Cu—4Zn 
               
               
                 3. 
                 Al—9Si—0.45Mg— 
                 460.5 
                 370.5 
                 5.5 
                 571.6 
                 469.0 
                 378.5 
                 7.0 
                 595.8 
                 465.3 
                 390.7 
                 5.0 
                 570.2 
               
               
                   
                 0.75Cu—4Zn 
               
               
                 4. 
                 Al—9Si—0.45Mg— 
                 451.5 
                 339.0 
                 6.5 
                 573.4 
                 450.5 
                 354.8 
                 5.0 
                 555.3 
                 464.0 
                 373.5 
                 6.5 
                 585.9 
               
               
                   
                 0.75Cu 
               
               
                 5. 
                 Al—9Si—0.5Mg— 
                 426.0 
                 317.3 
                 8.0 
                 561.5 
                 442.8 
                 348.2 
                 6.7 
                 566.4 
                 442.5 
                 364.5 
                 6.0 
                 559.2 
               
               
                   
                 0.75Cu 
               
               
                 6. 
                 Al—9Si—0.35Mg— 
                 411.2 
                 299.2 
                 7.3 
                 540.2 
                 436.3 
                 326.3 
                 7.0 
                 563.1 
                 446.5 
                 342.8 
                 6.5 
                 568.4 
               
               
                   
                 1.25Cu 
               
               
                 7. 
                 Al—9Si—0.45Mg— 
                 424.3 
                 328.0 
                 4.8 
                 525.8 
                 453.8 
                 353.0 
                 5.8 
                 567.7 
                 455.3 
                 375.8 
                 4.0 
                 545.6 
               
               
                   
                 1.25Cu 
               
               
                 8. 
                 Al—9Si—0.55Mg— 
                 444.8 
                 336.5 
                 6.0 
                 561.6 
                 460.3 
                 365.3 
                 4.8 
                 561.8 
                 475.8 
                 385.0 
                 4.8 
                 577.3 
               
               
                   
                 1.25Cu 
               
               
                 9. 
                 Al—9Si—0.35Mg— 
                 465.7 
                 325.0 
                 9.0 
                 608.8 
                 459.5 
                 355.3 
                 5.5 
                 570.6 
                 478.8 
                 386.3 
                 5.0 
                 583.6 
               
               
                   
                 1.75Cu 
               
               
                 10. 
                 Al—9Si—0.35Mg— 
                 463.3 
                 343.0 
                 7.5 
                 594.5 
                 471.7 
                 364.5 
                 6.3 
                 591.9 
                 471.0 
                 389.3 
                 4.5 
                 569.0 
               
               
                   
                 1.75Cu—0.5Ag 
               
               
                   
               
               
                 *Averaged value from five tensile specimens. 
               
               
                 The Quality Index, Q = UTS + 150 log(E). 
               
             
          
         
       
     
         [0000]    
       
         
               
             
               
               
             
               
               
               
             
               
               
               
               
               
             
               
               
               
               
               
             
           
               
                 TABLE 8 
               
             
             
               
                   
               
               
                 Charpy impact test results for some selected alloys 
               
             
          
           
               
                   
                 Energy (ft-lbs) 
               
             
          
           
               
                   
                 155° C./15 hrs 
                 155° C./60 hrs 
               
             
          
           
               
                 Alloy 
                 specimen 1 
                 Specimen 3 
                 Specimen 7 
                 Specimen 9 
               
               
                   
               
             
          
           
               
                 1. Al—9Si—0.5Mg 
                 6 
                 27 
                 23 
                 27 
               
               
                 3. Al—9Si—0.45Mg—0.75Cu—4Zn 
                 17 
                 18 
                 10 
                 12 
               
               
                 4. Al—9Si—0.45Mg—0.75Cu 
                 32 
                 15 
                 28 
                 13 
               
               
                 7. Al—9Si—0.45Mg—1.25Cu 
                 27 
                 12 
                 7 
                 12 
               
               
                 9. Al—9Si—0.35Mg—1.75Cu 
                 16 
                 15 
                 8 
                 9 
               
               
                   
               
             
          
         
       
     
         [0000]    
       
         
               
             
               
               
             
               
               
               
               
             
               
               
               
               
             
           
               
                 TABLE 9 
               
             
             
               
                   
               
               
                 S—N fatigue results for some selected alloys aged at 155 C. for 60 hours 
               
               
                 (Smooth, Axial; stress ratio = −1) 
               
             
          
           
               
                   
                 Cycles to Failure 
               
             
          
           
               
                   
                 Stress 
                 155 C./ 
                 155 C./ 
               
               
                 Alloy 
                 (MPa) 
                 15 hrs 
                 60 hrs 
               
               
                   
               
             
          
           
               
                 1. Al—9Si—0.5Mg 
                 100 
                 1680725 
                 1231620 
               
               
                 1. Al—9Si—0.5Mg 
                 100 
                 1302419 
                 272832 
               
               
                 1. Al—9Si—0.5Mg 
                 100 
                 4321029 
                 1077933 
               
               
                 1. Al—9Si—0.5Mg 
                 150 
                 71926 
                 148254 
               
               
                 1. Al—9Si—0.5Mg 
                 150 
                 242833 
                 42791 
               
               
                 1. Al—9Si—0.5Mg 
                 150 
                 153073 
                 56603 
               
               
                 1. Al—9Si—0.5Mg 
                 200 
                 16003 
                 54623 
               
               
                 1. Al—9Si—0.5Mg 
                 200 
                 8654 
                 30708 
               
               
                 1. Al—9Si—0.5Mg 
                 200 
                 36597 
                 39376 
               
               
                 3. Al—9Si—0.45Mg—0.75Cu—4Zn 
                 100 
                 160572 
                 248032 
               
               
                 3. Al—9Si—0.45Mg—0.75Cu—4Zn 
                 100 
                 298962 
                 131397 
               
               
                 3. Al—9Si—0.45Mg—0.75Cu—4Zn 
                 100 
                 120309 
                 394167 
               
               
                 3. Al—9Si—0.45Mg—0.75Cu—4Zn 
                 150 
                 120212 
                 12183 
               
               
                 3. Al—9Si—0.45Mg—0.75Cu—4Zn 
                 150 
                 70152 
                 42074 
               
               
                 3. Al—9Si—0.45Mg—0.75Cu—4Zn 
                 150 
                 190200 
                 31334 
               
               
                 3. Al—9Si—0.45Mg—0.75Cu—4Zn 
                 200 
                 38369 
                 18744 
               
               
                 3. Al—9Si—0.45Mg—0.75Cu—4Zn 
                 200 
                 29686 
                 14822 
               
               
                 3. Al—9Si—0.45Mg—0.75Cu—4Zn 
                 200 
                 39366 
                 11676 
               
               
                 4. Al—9Si—0.45Mg—0.75Cu 
                 100 
                 485035 
                 575446 
               
               
                 4. Al—9Si—0.45Mg—0.75Cu 
                 100 
                 4521553 
                 233110 
               
               
                 4. Al—9Si—0.45Mg—0.75Cu 
                 100 
                 3287495 
                 940229 
               
               
                 4. Al—9Si—0.45Mg—0.75Cu 
                 150 
                 170004 
                 141654 
               
               
                 4. Al—9Si—0.45Mg—0.75Cu 
                 150 
                 110500 
                 234640 
               
               
                 4. Al—9Si—0.45Mg—0.75Cu 
                 150 
                 688783 
                 238478 
               
               
                 4. Al—9Si—0.45Mg—0.75Cu 
                 200 
                 108488 
                 22686 
               
               
                 4. Al—9Si—0.45Mg—0.75Cu 
                 200 
                 40007 
                 36390 
               
               
                 4. Al—9Si—0.45Mg—0.75Cu 
                 200 
                 51678 
                 20726 
               
               
                 7. Al—9Si—0.45Mg—1.25Cu 
                 100 
                 1115772 
                 1650686 
               
               
                 7. Al—9Si—0.45Mg—1.25Cu 
                 100 
                 318949 
                 1744140 
               
               
                 7. Al—9Si—0.45Mg—1.25Cu 
                 100 
                 468848 
                 484262 
               
               
                 7. Al—9Si—0.45Mg—1.25Cu 
                 150 
                 102341 
                 232171 
               
               
                 7. Al—9Si—0.45Mg—1.25Cu 
                 150 
                 145766 
                 106741 
               
               
                 7. Al—9Si—0.45Mg—1.25Cu 
                 150 
                 63720 
                 226188 
               
               
                 7. Al—9Si—0.45Mg—1.25Cu 
                 200 
                 41686 
                 21873 
               
               
                 7. Al—9Si—0.45Mg—1.25Cu 
                 200 
                 20709 
                 58819 
               
               
                 7. Al—9Si—0.45Mg—1.25Cu 
                 200 
                 52709 
                 4367 
               
               
                 9. Al—9Si—0.35Mg—1.75Cu 
                 100 
                 2159782 
                 2288145 
               
               
                 9. Al—9Si—0.35Mg—1.75Cu 
                 100 
                 354677 
                 1011473 
               
               
                 9. Al—9Si—0.35Mg—1.75Cu 
                 100 
                 4258369 
                 783758 
               
               
                 9. Al—9Si—0.35Mg—1.75Cu 
                 150 
                 281867 
                 164554 
               
               
                 9. Al—9Si—0.35Mg—1.75Cu 
                 150 
                 135810 
                 188389 
               
               
                 9. Al—9Si—0.35Mg—1.75Cu 
                 150 
                 100053 
                 146740 
               
               
                 9. Al—9Si—0.35Mg—1.75Cu 
                 200 
                 24014 
                 48506 
               
               
                 9. Al—9Si—0.35Mg—1.75Cu 
                 200 
                 30695 
                 8161 
               
               
                 9. Al—9Si—0.35Mg—1.75Cu 
                 200 
                 62211 
                 31032 
               
               
                   
               
             
          
         
       
     
       1.4.2 Mechanical Properties at Room Temperature 
     1.4.2.1 Effect of Aging Temperature on Tensile Properties 
       [0120]    The effect of artificial aging temperature on tensile properties was investigated using the baseline alloy 1-Al-9% Si-0.5% Mg. After a minimum 4 hours of natural aging, the tensile bar castings were aged at 155° C. for 15, 30, 60 hours and at 170° C. for 8, 16, 24 hours. Three replicate specimens were used for each aging condition. 
         [0121]      FIG. 10  shows the tensile properties of the baseline A359 alloy (Al-9% Si-0.5% Mg) at various aging conditions. Low aging temperature (155° C.) tends to yield higher quality index than the high aging temperature (170° C.). Thus, the low aging temperature at 155° C. was selected, even though the aging time is longer to obtain improved properties. 
       2.4.2.2 Effects of Alloy Elements on Tensile Properties 
       [0122]      FIG. 11  compares the tensile properties of baseline Al-9% Si-0.5% Mg alloy and Al-9% Si-0.5% Mg-0.75% Cu alloy. The addition of 0.75% Cu to Al-9% Si-0.5% Mg alloy increases the yield strength by ˜20 MPa and ultimate tensile strength by ˜40 MPa while maintaining the elongation. The average quality index of the Cu-containing alloy is ˜560 MPa, which is much higher than the baseline alloy with an average of ˜520 MPa. 
         [0123]      FIG. 12  compares the tensile properties of four cast alloys, 1, 2, 3 and 4. Alloy 1 is the baseline alloy. Alloy 2-4 all contain 0.75% Cu with various amounts of Mg and/or Zn. Alloys 3 and 4 contain 0.45% Mg, while alloy 2 contains 0.35% Mg and alloy 1 contains 0.5% Mg. Alloys 2 and 3 also have 4% Zn. A preliminary assessment of these four alloys indicates that Mg and Zn increase alloy strength without sacrificing ductility. A direct comparison between alloys 3 and 4 indicates that by adding 4% Zn to the Al-9% Si-0.45% Mg-0.75% Cu alloy, both ultimate tensile strength and yield strength are increased while maintaining the elongation. The 4% Zn addition also increases the aging kinetics as indicated in  FIG. 12 . When aged at 155° C. for 15 hours, yield strength of about 370 MPa can be achieved for the Al-9% Si-0.45% Mg-0.75% Cu-4% Zn alloy, which is about 30 MPa higher than that of the alloy without Zn. 
         [0124]      FIG. 13  shows the effect of Mg content (0.35-0.55 wt %) on the tensile properties of the Al-9% Si-1.25% Cu—Mg alloys (Alloys 6-8). The tensile properties of the baseline alloy Al-9% Si-0.5% Mg are also included for comparison. Mg content showed significant influence on the tensile properties. With increasing Mg content, both yield strength and tensile strength were increased, but the elongation was decreased. The decrease of elongation with increasing Mg content could be related to higher amount of π-AlFeMgSi phase particles even if all the Q-AlCuMgSi phase particles were dissolved. The impact of Mg content on quality indexes of the Al-9% Si-1.25% Cu—Mg alloys was overall found to be insignificant. 
         [0125]      FIG. 14  shows the effect of Ag (0.5 wt %) on the tensile properties of Al-9% Si-0.35% Mg-1.75% Cu alloy. An addition of 0.5 wt % Ag had very limited impact on strength, elongation and quality index of the Al-9% Si-0.35% Mg-1.75% Cu alloy. It should be noted that the quality index of the Al-9% Si-0.35% Mg-1.75% Cu (without Ag) alloy is ˜60 MPa higher than the baseline alloy, A359 (Alloy 1) 
         [0126]      FIGS. 15 a -15 d    show the tensile properties of five promising alloys in accordance with the present disclosure along with the baseline alloy Al-9Si-0.5Mg (alloy 1). These five alloys achieve the target tensile properties, i.e., 10-15% increase in tensile and maintaining similar elongation as A356/A357 alloy. The alloys are: Al-9% Si-0.45% Mg-0.75% Cu (Alloy 4), Al-9% Si-0.45% Mg-0.75% Cu-4% Zn (Alloy 3), Al-9% Si-0.45% Mg-1.25% Cu (Alloy 7), Al-9% Si-0.35% Mg-1.75% Cu (Alloy 9), and Al-9% Si-0.35% Mg-1.75% Cu-0.5% Ag (Alloy 10). 
         [0127]    Based on the data, it is believed that the following tensile properties can be obtained with alloys aged at 155° C. for time ranged from 15 to 60 hrs.
       Ultimate tensile strength: 450-470 MPa   Tensile yield strength: 360-390 MPa   Elongation: 5-7%   Quality index: 560-590 MPa       
 
         [0132]    These properties are much higher than A359 (Alloy 1) and are very similar to A201 (A14.6Cu0.35Mg0.7Ag) cast alloy (UTS 450 MPa, TYS 380 MPa, Elongation 8%, and Q 585 MPa) ASM Handbook Volume 15, Casting, ASM International, December 2008. On the other hand, the castability of these Al-9% Si—Mg—Cu alloys is much better than A201 alloy. The A201 alloy has a poor castability due to its high tendency of hot cracking and Cu macro-segregation. Additionally, the material cost of A201 with 0.7 wt % Ag is also much higher than those embodiments in accordance with the present disclosure that are Ag-free. 
         [0133]    Based on the tensile property results, four alloys without Ag (Alloys 3, 4, 7 and 9) with promising tensile properties along with baseline alloy, A359 (Alloy 1) were selected for further investigation. Charpy impact, S-N fatigue and general corrosion tests were conducted on these five alloys aged at 155° C. for 15 hours and 60 hours. 
       1.4.4 Charpy Impact Tests 
       [0134]      FIG. 16  shows the results of the individual tests by plotting Charpy impact energy vs. tensile yield strength. The filled symbols are for specimens aged at 155° C. for 15 hours and open symbols are for specimens aged at 155° C. for 60 hours. Tensile yield strength increases as the aging time increases, while the Charpy impact energy decreases with increasing aging time. The results indicate that most alloys/aging conditions follow the expected strength/toughness relationship. However, the results indeed show a slight degradation of the strength/toughness relationship with higher Cu content such as 1.25 and 1.75 wt %. 
       1.4.5 S-N Fatigue Tests 
       [0135]    Aluminum castings are often used in engineered components subject to cycles of applied stress. Over their commercial lifetime millions of stress cycles can occur, so it is important to characterize their fatigue life. This is especially true for safety critical applications, such as automotive suspension components. 
         [0136]      FIGS. 17 and 18  show the S-N fatigue test results of five selected alloys aged at 155° C. for 15 and 60 hours, respectively. During these tests a constant amplitude stress (R=−1) was applied to the test specimens. Three different stress levels, 100 MPa, 150 MPa and 200 MPa were applied. The total number of cycles to failure was recorded. 
         [0137]    When aged at 155° C. for 15 hours, all the Cu-containing alloys showed better fatigue performance (higher number of cycles to failure) than the baseline A359 alloy at higher stress levels (&gt;150 MPa). At lower stress levels (&lt;125 MPa), the fatigue lives of the Al-9Si-0.45Mg-0.75Cu and Al-9Si-0.35Mg-1.75Cu alloys are very similar to the A359 alloy, while the fatigue life of the Al-9Si-0.45Cu-0.75Cu-4Zn alloy (alloy 3) was lower than the A359 alloy. The lower fatigue life of this alloy could result from the higher hydrogen content of the casting, as stated previously. 
         [0138]    Increasing aging time (higher tensile strength) tended to decrease the number of cycles to failure. For example, as the aging time increased from 15 hours to 60 hours, the average number of cycles to failure at 150 MPa stress level decreased from 323,000 to 205,000 for the Al-9% Si-0.45% Mg-0.75% Cu alloy and from 155,900 to 82,500 for the A359 alloy. The result could be a general trend of the strength/fatigue relationship of Al—Si—Mg—(Cu) casting alloys. Again, alloy 3 showed a lower fatigue performance than others. 
       1.4.6 Corrosion Tests—ASTM G110 
       [0139]      FIGS. 19 to 23  show optical micrographs of the cross-sectional views after 6-hour ASTM G110 tests for five selected alloys of both the as-cast surfaces and machined surfaces. The mode of corrosion attack was predominantly interdendritic corrosion. The number of corrosion sites was generally higher in the four Cu-containing compositions than in the Cu-free baseline alloy. 
         [0140]    More particularly,  FIGS. 19 a - d    show optical micrographs of cross-sections of Al-9% Si-0.5% Mg after a 6-hour ASTM G110 test: a) of the alloy as cast and aged 15 hours at 155° C.; b) of the alloy as cast and aged 60 hours at 155° C.; c) of the alloy with a machined surface and aged 15 hours at 155° C.; and d) of the alloy with a machined surface and aged 60 hours at 155° C. 
         [0141]      FIGS. 20 a - d    show optical micrographs of cross-sections of Al-9% Si-0.35% Mg-0.75% Cu-4% Zn after a 6-hour ASTM G110 test: a) of the alloy as cast and aged 15 hours at 155° C.; b) of the alloy as cast and aged 60 hours at 155° C.; c) of the alloy with a machined surface and aged 15 hours at 155° C.; and d) of the alloy with a machined surface and aged 60 hours at 155° C. 
         [0142]      FIGS. 21 a - d    show optical micrographs of cross-sections of Al-9% Si-0.45% Mg-0.75% Cu after a 6-hour ASTM G110 test: a) of the alloy as cast and aged 15 hours at 155° C.; b) of the alloy as cast and aged 60 hours at 155° C.; c) of the alloy with a machined surface and aged 15 hours at 155° C.; and d) of the alloy with a machined surface and aged 60 hours at 155° C. 
         [0143]      FIGS. 22 a - d    show optical micrographs of cross-sections of Al-9% Si-0.45% Mg-1.25% Cu after a 6-hour ASTM G110 test: a) of the alloy as cast and aged 15 hours at 155° C.; b) of the alloy as cast and aged 60 hours at 155° C.; c) of the alloy with a machined surface and aged 15 hours at 155° C.; and d) of the alloy with a machined surface and aged 60 hours at 155° C. 
         [0144]      FIGS. 23 a - d    show optical micrographs of cross-sections of Al-9% Si-0.35% Mg-1.75% Cu after a 6-hour ASTM G110 test: a) of the alloy as cast and aged 15 hours at 155° C.; b) of the alloy as cast and aged 60 hours at 155° C.; c) of the alloy with a machined surface and aged 15 hours at 155° C.; and d) of the alloy with a machined surface and aged 60 hours at 155° C. 
         [0145]      FIG. 24  shows the depth of attack after the 6-hour ASTM G110 test. There is no clear difference or trend among the alloys. Aging time did not show obvious impact on the depth of attack either, while some differences were found between the as-cast surfaces and the machined surfaces. In general, the corrosion attack was slightly deeper on the machined surface than the as-cast surface of the same sample. 
         [0146]    Overall, the additions of Cu or Cu+Zn do not change the corrosion mode nor increase the depth-of-attack of the alloys. It is believed that all the alloys evaluated have similar corrosion resistance as the baseline alloy, A359. 
         [0147]    The present disclosure has described Al—Si—Cu—Mg alloys that can achieve high strength without sacrificing ductility. Tensile properties including 450-470 MPa ultimate tensile strength, 360-390 MPa yield strength, 5-7% elongation, and 560-590 MPa Quality Index were obtained. These properties exceed conventional 3xx alloys and are very similar to that of the A201 (2xx+Ag) Alloy, while the castabilities of the new Al-9Si-MgCu alloys are much better than that of the A201 alloy. The new alloys showed better S-N fatigue resistance than A359 (Al-9Si-0.5Mg) alloys. Alloys in accordance with the present disclosure have adequate fracture toughness and general corrosion resistance. 
       Example 2 
     Cast Alloys for Applications at Elevated Temperatures 
       [0148]    Because alloys such as those described in the present disclosure may be utilized in applications wherein they are exposed to high temperatures, such as in engines in the form of engine blocks, cylinder heads, pistons, etc., it is of interest to assess how such alloys behave when exposed to high temperatures.  FIG. 26  shows a graph of tensile properties of an alloy in accordance with the present disclosure, namely, Al-9Si-0.35Mg-1.75Cu (previously referred to as alloy 9, e.g., in  FIG. 15 ) after exposure to various temperatures. As noted, for each test generating data in the graph, the exposure time of the alloys was 500 hours at the indicated temperature. The samples were also tested at the temperature indicated. As shown in the graph, the yield strength of the alloy diminished significantly at temperatures above 150° C. In accordance with the present disclosure, the metal was analyzed to ascertain features associated with the loss in strength due to exposure to increased temperatures. 
         [0149]      FIGS. 27 a  and 27 b    show scanning electron microscope (SEM) micrographs of a cross-section of a sample of alloy 9 prior to exposure to high temperatures, with  27   b  being an enlarged view of the portion of the micrograph of  31   a  indicated as “Al”. As shown in  FIG. 27 a   , the grain boundaries are visible, as well as, Si and AlFeSi particles. The predominately Al portion shown in  FIG. 27 b    shows no visible precipitate at 20,000× magnification. 
         [0150]      FIGS. 28 a - e    show a series of scanning electron microscope (SEM) micrographs of a cross-section of alloy C00 (previously referred to as alloy 9, e.g., in  FIG. 15 ) of the same scale as the micrograph shown in  FIG. 27 b    after exposure to increasing temperatures as shown by the correlation of the micrographs to the data points on the tensile property graph G of alloy 9. The tensile characteristics of A356 alloy in the given temperature range are also shown in graph G for comparison. As can be appreciated from the sequence of micrographs, exposure of alloy 9 to increasing temperatures results in continuously increasing prominence of precipitate particles, which are larger, and which exhibit divergent geometries. 
         [0151]    The inventors of the present disclosure recognized that certain alloying elements, viz., Ti, V, Zr, Mn, Ni, Hf, and Fe could be introduced to the C00 alloy (previously referred to as alloy 9, e.g., in  FIG. 15 ) of the present disclosure in small amounts to produce an alloy that resists strength degradation at elevated temperatures. 
         [0152]    The following table (Table 10) show 18 alloys utilizing additive elements in small quantities to the C00 alloy (previously referred to as alloy 9, e.g., in  FIG. 15 ) for the purpose of developing improved strength at elevated temperatures. 
         [0000]    
       
         
               
             
               
               
             
               
               
               
               
               
               
               
               
               
               
               
               
               
             
               
               
               
               
               
               
               
               
               
               
               
               
               
             
           
               
                 TABLE 10 
               
             
             
               
                   
               
               
                 Alloy Compositions 
               
             
          
           
               
                   
                 Actual Composition (wt %) 
               
             
          
           
               
                 Alloy 
                 Fe 
                 Si 
                 Mn 
                 Cu 
                 Mg 
                 Sr 
                 Ti 
                 B 
                 V 
                 Zr 
                 Nl 
                 Hf 
               
               
                   
               
             
          
           
               
                 C00 
                 0.08 
                 9.29 
                 0 
                 1.83 
                 0.37 
                 0.0125 
                 0.05 
                   
                 0 
                 0 
                 0 
                 0 
               
               
                 C01 
                 0.15 
                 9.3 
                 0.002 
                 1.82 
                 0.002 
                 0.008 
                 0.11 
                 0.0047 
                 0.012 
                 0.002 
                 0 
                 0 
               
               
                 C02 
                 0.15 
                 9.35 
                 0.002 
                 1.82 
                 0.39 
                 0.008 
                 0.11 
                 0.0043 
                 0.012 
                 0.002 
                 0 
                 0 
               
               
                 C03 
                 0.15 
                 9.05 
                 0.002 
                 1.77 
                 0.37 
                 0.007 
                 0.11 
                 0.0051 
                 0.13 
                 0.002 
                 0 
                 0 
               
               
                 C04 
                 0.16 
                 8.95 
                 0.002 
                 1.77 
                 0.36 
                 0.006 
                 0.1 
                 0.0026 
                 0.1 
                 0.091 
                 0 
                 0 
               
               
                 C05 
                 0.16 
                 8.86 
                 0.002 
                 1.76 
                 0.36 
                 0.005 
                 0.1 
                 0.0016 
                 0.13 
                 0.15 
                 0 
                 0 
               
               
                 C06 
                 0.16 
                 8.54 
                 0.002 
                 1.72 
                 0.35 
                 0.004 
                 0.1 
                 0.005 
                 0.13 
                 0.18 
                 0 
                 0 
               
               
                 C07 
                 0.16 
                 9.31 
                 0.15 
                 1.8 
                 0.34 
                 0.004 
                 0.11 
                 0.0044 
                 0.025 
                 0.016 
                 0 
                 0 
               
               
                 C08 
                 0.16 
                 9.32 
                 0.16 
                 1.84 
                 0.34 
                 0.004 
                 0.11 
                 0.0051 
                 0.025 
                 0.017 
                 0 
                 0 
               
               
                 C09 
                 0.17 
                 9.1 
                 0.28 
                 1.8 
                 0.33 
                 0.003 
                 0.11 
                 0.005 
                 0.025 
                 0.016 
                 0 
                 0 
               
               
                 C10 
                 0.32 
                 9.26 
                 0.3 
                 1.83 
                 0.34 
                 0.003 
                 0.11 
                 0.0045 
                 0.024 
                 0.017 
                 0 
                 0 
               
               
                 C11 
                 0.49 
                 8.96 
                 0.3 
                 1.78 
                 0.32 
                 0.003 
                 0.12 
                 0.0055 
                 0.11 
                 0.016 
                 0 
                 0 
               
               
                 C12 
                 0.56 
                 8.97 
                 0.3 
                 1.79 
                 0.32 
                 0.002 
                 0.1 
                 0.0039 
                 0.11 
                 0.12 
                 0 
                 0 
               
               
                 C13 
                 0.15 
                 9.28 
                 0.003 
                 1.82 
                 0.33 
                 0.0125 
                 0.1 
                 0.005 
                 0.0012 
                 0.002 
                 0.28 
                 0 
               
               
                 C14 
                 0.2 
                 9.28 
                 0.004 
                 1.81 
                 0.33 
                 0.004 
                 0.1 
                 0.0026 
                 0.012 
                 0.002 
                 0.28 
                 0 
               
               
                 C15 
                 0.31 
                 9.27 
                 0.03 
                 1.82 
                 0.33 
                 0.004 
                 0.1 
                 0.0032 
                 0.012 
                 0.002 
                 0.28 
                 0 
               
               
                 C16 
                 0.32 
                 9.14 
                 0.1 
                 1.79 
                 0.32 
                 0.003 
                 0.1 
                 0.0032 
                 0.012 
                 0.003 
                 0.27 
                 0.1 
               
               
                 C17 
                 0.32 
                 8.88 
                 0.12 
                 1.75 
                 0.3 
                 0.003 
                 0.1 
                 0.0031 
                 0.11 
                 0.013 
                 0.26 
                 0.1 
               
               
                 C18 
                 0.32 
                 8.89 
                 0.14 
                 1.76 
                 0.3 
                 0.003 
                 0.1 
                 0.003 
                 0.11 
                 0.036 
                 0.27 
                 0.1 
               
               
                   
               
             
          
         
       
     
         [0153]    Table 11 shows the mechanical properties of the foregoing alloys, viz., ultimate tensile strength (UTS), total yield strength (TYS) and Elongation % at 300° C., 175° C. and room temperature (RT). 
         [0000]    
       
         
               
             
               
               
             
               
               
               
               
               
             
               
               
               
               
               
               
               
               
               
               
               
             
               
               
               
             
               
               
               
               
               
               
               
             
               
               
               
               
               
               
               
               
               
               
               
               
               
               
               
               
             
           
               
                 TABLE 11 
               
               
                   
               
               
                 Mechanical Properties at Various Temperatures 
               
               
                   
               
             
             
               
                   
               
             
          
           
               
                   
                 300 C. 
               
             
          
           
               
                   
                 Alloy 
                 UTS(ksi 
                 TYS(ksi) 
                 Elongation(%) 
               
               
                   
                   
               
             
          
           
               
                   
                 C00 
                 8.2 
                 8.4 
                 8.3 
                 6 
                 6.3 
                 6 
                 49 
                 54 
                 29.5 
               
               
                   
                 C01 
                 9.3 
                 9.5 
                 9.6 
                 6.5 
                 6.4 
                 6.7 
                 63 
                 54.5 
                 49.5 
               
               
                   
                 C02 
                 10 
                 10.3 
                 9 
                 6.9 
                 7.2 
                 6.5 
                 51.5 
                 40.5 
                 40.5 
               
               
                   
                 C03 
                 8.8 
                 10.2 
                 10.6 
                 6.8 
                 7.2 
                 7.5 
                 52 
                 43.5 
                 56.5 
               
               
                   
                 C04 
                 10.4 
                 10.3 
                 11.7 
                 7.9 
                 7.4 
                 8 
                 47.5 
                 47 
                 41.5 
               
               
                   
                 C05 
                 10.8 
                 10.7 
                 11.1 
                 8.5 
                 8 
                 8.2 
                 47 
                 41.5 
                 36.5 
               
               
                   
                 C06 
                 11 
                 9.3 
                 11.2 
                 7.7 
                 7.1 
                 8.5 
                 35 
                 36 
                 42.5 
               
               
                   
                 C07 
                 10.5 
                 10.6 
                 10.3 
                 8.1 
                 8 
                 7.7 
                 53 
                 40 
                 43.5 
               
               
                   
                 C08 
                 10 
                 9.7 
                 10.6 
                 7.5 
                 6.7 
                 7.9 
                 39 
                 40.5 
                 36.5 
               
               
                   
                 C09 
                 10.3 
                 10.8 
                 11.7 
                 7.5 
                 7.8 
                 8.6 
                 35 
                 35 
                 36 
               
               
                   
                 C10 
                 10.7 
                 10.7 
                 11.3 
                 8.1 
                 8 
                 8.3 
                 37 
                 40 
                 33 
               
               
                   
                 C11 
                 11 
                 11.3 
                 10.5 
                 7.9 
                 8.1 
                 7.7 
                 27.5 
                 30.5 
                 34.5 
               
               
                   
                 C12 
                 11.7 
                 10.8 
                 11.4 
                 8.2 
                 7.9 
                 8.2 
                 33 
                 28.5 
                 34.5 
               
               
                   
                 C13 
                 10.2 
                 9 
                 9.4 
                 7.5 
                 6.9 
                 7 
                 45.5 
                 53 
                 40 
               
               
                   
                 C14 
                 9.3 
                 9.2 
                 9.9 
                 6.6 
                 6.6 
                 6.9 
                 56 
                 44 
                 42.5 
               
               
                   
                 C15 
                 10 
                 9.8 
                 10 
                 7.2 
                 7.2 
                 7.2 
                 46.5 
                 32 
                 31.5 
               
               
                   
                 C16 
                 10.3 
                 10.3 
                 10.1 
                 7.7 
                 7.5 
                 7.5 
                 44.5 
                 36.5 
                 34.5 
               
               
                   
                 C17 
                 10.5 
                 9.4 
                 10 
                 7.5 
                 7.2 
                 7.2 
                 46.5 
                 42.5 
                 29.5 
               
               
                   
                 C18 
                 10.1 
                 11.4 
                 11.3 
                 7.5 
                 8.6 
                 8.2 
                 29 
                 28.5 
                 25.5 
               
               
                   
                   
               
             
          
           
               
                   
                 175 C. 
                 RT 
               
             
          
           
               
                 Alloy 
                 UTS(ksi 
                 TYS(ksi) 
                 Elongation(%) 
                 UTS(ksi 
                 TYS(ksi) 
                 Elongation(%) 
               
               
                   
               
             
          
           
               
                 C00 
                 34.8 
                 33.7 
                 37.1 
                 28.8 
                 27.8 
                 31 
                 8.5 
                 10.5 
                 10.5 
                 58.4 
                 56.5 
                 47.7 
                 52.4 
                 4 
                 4 
               
               
                 C01 
                 28.1 
                 31 
                 29.4 
                 21.4 
                 23.7 
                 21.8 
                 16.6 
                 24 
                 14.9 
                 37.7 
                 38.4 
                 20.1 
                 20.9 
                 9 
                 12 
               
               
                 C02 
                 43.6 
                 46.2 
                 46.1 
                 38 
                 39.6 
                 40.2 
                 6.9 
                 5.1 
                 5.1 
                 60.2 
                 56.7 
                   
                 46.2 
                 3 
                 3 
               
               
                 C03 
                 44.9 
                 43.1 
                 45.4 
                 40.6 
                 37.4 
                 39.8 
                 0.6 
                 7.4 
                 4 
                 50.5 
                 59.8 
                 48.7 
                 50.3 
                 3 
                 5.5 
               
               
                 C04 
                 46.5 
                 46.5 
                 48.3 
                 40.6 
                 41 
                 42.8 
                 6.9 
                 9.1 
                 4.6 
                 58.7 
                 57.5 
                 49.7 
                 48.1 
                 3 
                 1 
               
               
                 C05 
                 40 
                 47.4 
                 47 
                 35.4 
                 40.7 
                 39.9 
                 2.9 
                 5.1 
                 5.1 
                 52.4 
                 58.2 
                 51.1 
                 47.7 
                 1 
                 3 
               
               
                 C06 
                 44.3 
                 43.6 
                 46.6 
                 38.4 
                 37.4 
                 40.9 
                 5.7 
                 8 
                 3.4 
                 57.9 
                 59.1 
                 48.2 
                 48.8 
                 3 
                 4 
               
               
                 C07 
                 48.3 
                 46.7 
                 43 
                 41.6 
                 40.8 
                 38 
                 6.3 
                 2.3 
                 6.9 
                 57 
                 58.3 
                 48.1 
                   
                 3.5 
                 3.5 
               
               
                 C08 
                 49.3 
                 41.8 
                 42.6 
                 41.2 
                 36.5 
                 36.6 
                 6.3 
                 2.3 
                 6.9 
                 58.6 
                 52 
                 46.2 
                 48.2 
                 3.5 
                 3 
               
               
                 C09 
                 39 
                 45.2 
                 43.9 
                 33.7 
                 39.2 
                 38.6 
                 3.4 
                 3.4 
                 2.3 
                 52 
                 58.1 
                 47.9 
                 48.5 
                 3 
                 3 
               
               
                 C10 
                 35.7 
                 43.6 
                 48.6 
                 30.9 
                 37.3 
                 41.9 
                 2.3 
                 3.4 
                 2.3 
                 55 
                 55.6 
                 47.7 
                 49.6 
                 3 
                 3 
               
               
                 C11 
                 42.4 
                 42.5 
                 47.6 
                 36.5 
                 35.8 
                 41.1 
                 1.1 
                 2.3 
                 2.3 
                 54.1 
                 52.6 
                 49.3 
                 49.1 
                 3 
                 3 
               
               
                 C12 
                 37.9 
                 37.3 
                 37.3 
                 35.3 
                 31.7 
                 31.2 
                 1.1 
                 1.7 
                 4 
                 50.2 
                 52.7 
                 48.5 
                 50.6 
                 1 
                 1.5 
               
               
                 C13 
                 45.3 
                 45.2 
                 41.3 
                 39.2 
                 38.2 
                 35 
                 2.9 
                 6.3 
                 8 
                 56.3 
                 58.5 
                 48.1 
                 45.9 
                 2.5 
                 8 
               
               
                 C14 
                 34.3 
                 38.6 
                 45.7 
                 32.3 
                 32.4 
                 39 
                 0.6 
                 9.1 
                 5.1 
                 61.3 
                 57.1 
                 44.3 
                 44.5 
                 8 
                 4 
               
               
                 C15 
                 40.1 
                 45.2 
                 44.7 
                 34.2 
                 38.5 
                 37.6 
                 2.9 
                 5.1 
                 3.4 
                 56.7 
                 55.8 
                 45.9 
                 47.1 
                 4 
                 4 
               
               
                 C16 
                 42.3 
                 41.6 
                 41.7 
                 35.4 
                 35.2 
                 35.9 
                 4 
                 5.1 
                 2.3 
                 57.4 
                 53.7 
                 46.4 
                 46 
                 4 
                 3 
               
               
                 C17 
                 42.6 
                 38.4 
                 39.5 
                 21.8 
                 38 
                 34.2 
                 14.9 
                 6.9 
                 2.3 
                 57.2 
                 56.1 
                 47.1 
                 46.9 
                 3 
                 3 
               
               
                 C18 
                 37.2 
                 41.4 
                 41.5 
                 35.1 
                 34.6 
                 34.7 
                 1.1 
                 5.1 
                 3.4 
                 48.5 
                 50.6 
                 45.1 
                 46.9 
                 2 
                 2 
               
               
                   
               
             
          
         
       
     
         [0154]      FIG. 29  shows a graph of yield strength at room temperature for foregoing alloys. A356 is shown for comparison. In addition, a department of energy (DOE) published target for strength improvement is shown for comparison [Predictive Modeling for Automotive Light weighting Applications and Advanced Alloy Development for Automotive and Heavy-Duty Engines, Issue by Department of Energy on Mar. 22, 2012]. As can be appreciated, the C00 alloy is comparable in strength at room temperature to alloys C02-C18, all of which substantially exceed the strength of the A356 alloy and the DOE target properties. Alloy C01—without substantial quantities of Mg, has a far lower yield strength. 
         [0155]      FIG. 30  is a graph of yield strength after exposure to 175° C. for 500 hours for the foregoing alloys. The C00, as well as A356 are shown for comparison. As can be appreciated, the C00 alloy substantially exceeds the strength of the A356 alloy. Alloys C02-C18), all show marked improvement over both A356 and C00. 
         [0156]      FIG. 31  is a graph of yield strength after exposure to 300° C. for 500 hours for the foregoing alloys. C00, as well as A356 are shown for comparison.  FIG. 32  shows is a graph of yield strength after exposure to 300° C. for various alloys. More particularly, adjacent alloys (going in the direction of the arrows) show the result of an additional element or the increase in quantity of an element. The highest result in the graph of  FIG. 32  is for C00+0.1T+0.16Fe+0.13V+0.15Zr. The addition of more Zr (to 0.18%) to this combination results in decreased performance. 
         [0157]      FIG. 33  is a graph of yield strength after exposure to 300° C. for various alloys for 500 hours. The graphs show improvements due to the addition of Ti, Fe and Mn to the C00 composition, with the maximum performance noted relative to C00+0.11Ti+0.32Fe+0.3Mn. The addition of V to the foregoing reduces performance and the further addition of 0.12 Zr brings performance almost back to the maximum level. 
         [0158]      FIG. 34  is a graph of yield strength after exposure to 300° C. for various alloys, i.e., due to the addition of elements to the C00 composition. The optimal performance is noted relative to C00+0.1Ti+0.28Ni+0.32 Fe+0.14Mn+0.1Hf+0.11V+0.04Zr. 
         [0159]    It will be understood that the embodiments described herein are merely exemplary and that a person skilled in the art may make many variations and modifications without departing from the spirit and scope of the claimed subject matter. For example, use different aging conditions may produce different resultant characteristics. All such variations and modifications are intended to be included within the scope of the appended claims.