Abstract:
A semiconductor device is disclosed. The semiconductor device includes: a substrate having a gate structure thereon and a first interlayer dielectric (ILD) layer surrounding the gate structure; a first hard mask on the gate structure; and a second hard mask on the gate structure, wherein the first hard mask is adjacent to two sides of the second hard mask and the first hard mask and the first hard mask comprises silicon nitride.

Description:
BACKGROUND OF THE INVENTION 
       [0001]    1. Field of the Invention 
         [0002]    The invention relates to a semiconductor device and fabrication method thereof, and more particularly, to an approach of forming a two-layered hard mask on top of gate structure during self-aligned contact (SAC) process. 
         [0003]    2. Description of the Prior Art 
         [0004]    In current semiconductor industry, polysilicon has been widely used as a gap-filling material for fabricating gate electrode of metal-oxide-semiconductor (MOS) transistors. However, the conventional polysilicon gate also faced problems such as inferior performance due to boron penetration and unavoidable depletion effect which increases equivalent thickness of gate dielectric layer, reduces gate capacitance, and worsens driving force of the devices. In replacing polysilicon gates, work function metals have been developed to serve as a control electrode working in conjunction with high-K gate dielectric layers. 
         [0005]    In current fabrication of high-k metal gate transistors, two photo-etching processes are usually conducted to form contact plugs connecting gate structure and source/drain regions during self-aligned contacts (SAC) process. Since the hard mask above gate structure is typically composed of one single material, part of the hard mask is easily removed during formation of contact plugs so that contact plug connected to the gate structure would contact the contact plug connected to the source/drain region and results in short circuit. Hence how to improve this issue has become an important task in this field. 
       SUMMARY OF THE INVENTION 
       [0006]    According to a preferred embodiment of the present invention, a method for fabricating semiconductor device is disclosed. The method includes the steps of: providing a substrate having a gate structure thereon and a first interlayer dielectric (ILD) layer surrounding the gate structure; removing part of the gate structure; forming a first mask layer on the first ILD layer and the gate structure; removing the first mask layer on the first ILD layer and part of the first mask layer on the gate structure for forming a first hard mask on the gate structure; forming a second mask layer on the first ILD layer, the first hard mask, and the gate structure; and planarizing the second mask layer to forma second hard mask on the gate structure, wherein the top surfaces of the first hard mask, the second hard mask, and the first ILD layer are coplanar. 
         [0007]    According to another aspect of the present invention, a semiconductor device is disclosed. The semiconductor device includes: a substrate having a gate structure thereon and a first interlayer dielectric (ILD) layer surrounding the gate structure; a first hard mask on the gate structure; and a second hard mask on the gate structure, wherein the first hard mask is adjacent to two sides of the second hard mask and the first hard mask and the first hard mask comprises silicon nitride. 
         [0008]    According to another aspect of the present invention, a semiconductor device is disclosed. The semiconductor device includes: a substrate having a gate structure and a first ILD layer surrounding the gate structure; a first hard mask on the gate structure; and a second hard mask on the gate structure, wherein the first hard mask is adjacent to two sides of the second hard mask and the first hard mask and the second hard mask both contacting the gate structure directly. 
         [0009]    These and other objectives of the present invention will no doubt become obvious to those of ordinary skill in the art after reading the following detailed description of the preferred embodiment that is illustrated in the various figures and drawings. 
     
    
     
       BRIEF DESCRIPTION OF THE DRAWINGS 
         [0010]      FIGS. 1-3  illustrate a method for fabricating semiconductor device according to a first embodiment of the present invention. 
           [0011]      FIGS. 4-6  illustrate a method for fabricating semiconductor device according to a second embodiment of the present invention. 
           [0012]      FIGS. 7-10  illustrate a method for fabricating semiconductor device according to a third embodiment of the present invention. 
           [0013]      FIGS. 11-14  illustrate a method for fabricating semiconductor device according to a fourth embodiment of the present invention. 
       
    
    
     DETAILED DESCRIPTION 
       [0014]    Referring to  FIGS. 1-3 ,  FIGS. 1-3  illustrate a method for fabricating semiconductor device according to a first embodiment of the present invention. As shown in  FIG. 1 , a substrate  12 , such as a silicon substrate or silicon-on-insulator (SOI) substrate is provided, and a transistor region, such as a PMOS region or a NMOS region is defined on the substrate  12 . At least a first fin-shaped structure  14  and an insulating layer are formed on the substrate  12 , in which the bottom of the fin-shapes structure  14  is preferably enclosed by the insulating layer preferably composed of silicon oxide to form a shallow trench isolation (STI). A gate structure  18  is formed on part of the fin-shaped structure  14 . 
         [0015]    The formation of the fin-shaped structure  14  could be accomplished by first forming a patterned mask (now shown) on the substrate,  12 , and an etching process is performed to transfer the pattern of the patterned mask to the substrate  12 . Next, depending on the structural difference of a tri-gate transistor or dual-gate fin-shaped transistor being fabricated, the patterned mask could be stripped selectively or retained, and deposition, chemical mechanical polishing (CMP), and etching back processes are carried out to form a STI surrounding the bottom of the fin-shaped structure  14 . Alternatively, the formation of the fin-shaped structure  14  could also be accomplished by first forming a patterned hard mask (not shown) on the substrate  12 , and then performing an epitaxial process on the exposed substrate  12  through the patterned hard mask to grow a semiconductor layer. This semiconductor layer could then be used as the corresponding fin-shaped structure  14 . In another fashion, the patterned hard mask could be removed selectively or retained, and deposition, CMP, and then etching back could be used to form a STI surrounding the bottom of the fin-shaped structure  14 . Moreover, if the substrate  12  were a SOI substrate, a patterned mask could be used to etch a semiconductor layer on the substrate until reaching a bottom oxide layer underneath the semiconductor layer to form the corresponding fin-shaped structure. If this means is chosen the aforementioned steps for fabricating the STI could be eliminated. 
         [0016]    The fabrication of the gate structure  18  could be accomplished by a gate first process, a high-k first approach from gate last process, or a high-k last approach from gate last process. Since this embodiment pertains to a high-k first approach, dummy gate (not shown) composed of high-k dielectric layer and polysilicon material could be first formed on the fin-shaped structure  14  and the STI, and a spacer  24  is formed on the sidewall of the dummy gate. A source/drain region  26  and epitaxial layer (not shown) are then formed in the fin-shaped structure  14  and/or substrate  12  adjacent to two sides of the spacer  24 , a contact etch stop layer (CESL)  30  is formed on the dummy gate, and an interlayer dielectric (ILD) layer  32  composed of tetraethyl orthosilicate (TEOS) is formed on the CESL  30 . 
         [0017]    Next, a replacement metal gate (RMG) process could be conducted to planarize part of the ILD layer  32  and CESL  30  and then transforming the dummy gate into a metal gate. The RMG process could be accomplished by first performing a selective dry etching or wet etching process, such as using etchants including ammonium hydroxide (NH 4 OH) or tetramethylammonium hydroxide (TMAH) to remove the polysilicon layer from dummy gate for forming a recess (not shown) in the ILD layer  32 . Next, a conductive layer including at least a U-shaped work function metal layer  34  and a low resistance metal layer  36  is formed in the recess, and a planarizing process is conducted thereafter so that the surfaces of the U-shaped work function metal layer  34  and low resistance metal layer  36  are even with the surface of the ILD layer  32 . This forms a gate electrode  38  of the gate structure  18 . 
         [0018]    In this embodiment, the work function metal layer  34  is formed for tuning the work function of the later formed metal gates to be appropriate in an NMOS or a PMOS. For an NMOS transistor, the work function metal layer  34  having a work function ranging between 3.9 eV and 4.3 eV may include titanium aluminide (TiAl), zirconium aluminide (ZrAl), tungsten aluminide (WAl), tantalum aluminide (TaAl), hafnium aluminide (HfAl), or titanium aluminum carbide (TiAlC), but it is not limited thereto. For a PMOS transistor, the work function metal layer  34  having a work function ranging between 4.8 eV and 5.2 eV may include titanium nitride (TiN), tantalum nitride (TaN), tantalum carbide (TaC), but it is not limited thereto. An optional barrier layer (not shown) could be formed between the work function metal layer  34  and the low resistance metal layer  36 , in which the material of the barrier layer may include titanium (Ti), titanium nitride (TiN), tantalum (Ta) or tantalum nitride (TaN). Furthermore, the material of the low-resistance metal layer  36  may include copper (Cu), aluminum (Al), titanium aluminum (TiAl), cobalt tungsten phosphide (CoWP) or any combination thereof. Since the process of using RMG process to transform dummy gate into metal gate is well known to those skilled in the art, the details of which are not explained herein for the sake of brevity. 
         [0019]    After forming the gate structure  18 , part of the gate electrode  38 , such as part of work function metal layer  34  and low resistance metal layer  36  could be removed to form a recess between the spacer  24 , and a first mask layer  40  and a second mask layer  42  are sequentially deposited on the ILD layer  32 , CESL  30 , spacer  24 , and gate electrode  38 . 
         [0020]    Next, as shown in  FIG. 2 , a CMP process is conducted to planarize part of the second mask layer  42  and part of the first mask layer  40  for forming a first hard mask  44  and a second hard mask  46  on the gate electrode  38 , in which the top surfaces of the first hard mask  44 , second hard mask  46 , spacer  24 , CESL  30 , and ILD layer  32  are coplanar. 
         [0021]    In this embodiment, the first hard mask  44  and second hard mask  46  are preferably composed of different material such as the first hard mask  44  is composed of silicon nitride while the second hard mask  46  is composed of silicon oxide, but not limited thereto. Viewing from a structural perspective, the first hard mask  44  is preferably U-shaped and contacting the gate electrode  38  directly while the second hard mask  46  is disposed on the first hard mask  44  without contacting the gate electrode  38 . 
         [0022]    Next, as shown in  FIG. 3 , another ILD layer  48  is formed on the first hard mask  44 , second hard mask  46 , spacer  24 , CESL  30 , and ILD layer  32 , and a contact plug formation is conducted to form plurality of contact plugs  50  electrically connected to the gate electrode  38  and source/drain region  26 . In this embodiment, the contact plugs  50  could be formed by first using a photo-etching process to remove part of the ILD layer  48  directly above the gate electrode  38  and part of or all of the second hard mask  46  to expose the first hard mask  44  surface, and then using another etching process to remove part of the hard mask  44  so that the remaining first hard mask  44  is only formed against sidewalls of the recess like a spacer. This exposes the top surface of the gate electrode  38  and forms a contact hole. Next, aforementioned photo-etching process is repeated to form two additional contact holes exposing the source/drain region  26 , metals are deposited into the contact holes, and CMP process is conducted to remove part of the metal material or even part of the ILD layer  48  to form contact plugs  50  electrically connected the gate electrode  38  and source/drain region  26 . This completes the fabrication of semiconductor device according to a first embodiment of the present invention. 
         [0023]    Referring to  FIGS. 4-6 ,  FIGS. 4-6  illustrate a method for fabricating semiconductor device according to a second embodiment of the present invention. As shown in  FIG. 4 , after forming the gate electrode  38  composed of U-shaped metal layer  34  and low resistance metal layer  36  according to the first embodiment, it would be desirable to remove part of the gate electrode  38  and part of the spacer  24  for forming a recess within the ILD layer  32 , and then form a first mask layer  40  and second mask layer  42  sequentially on the ILD layer  32 , CESL  30 , spacer  24 , and gate electrode  38 . 
         [0024]    Next, as shown in  FIG. 5 , a CMP process is conducted to planarize part of the second mask layer  42  and part of the first mask layer  40  for forming a first hard mask  44  and second hard mask  46  on the spacer  24  and gate electrode  38 , in which the top surfaces of the first hard mask  44 , second hard mask  46 , CESL  30 , and ILD layer  32  are coplanar. 
         [0025]    In this embodiment, the first hard mask  44  and second hard mask  46  are preferably composed of different material, such as the first hard mask  44  is composed of silicon nitride while the second hard mask  46  is composed of silicon oxide, but not limited thereto. Viewing from a structural perspective, the first hard mask  44  is preferably U-shaped and sitting on the gate electrode  38  and spacer  24  at the same time while the second hard mask  46  is disposed on the first hard mask  44  without contacting the gate electrode  38 . 
         [0026]    Next, as shown in  FIG. 6 , another ILD layer  48  is formed on the first hard mask  44 , second hard mask  46 , CESL  30 , and ILD layer  32 , and a contact plug formation is conducted to form plurality of contact plugs  50  electrically connected to the gate electrode  38  and source/drain region  26 . In this embodiment, the contact plugs  50  could be formed by first using a photo-etching process to remove part of the ILD layer  48  directly above the gate electrode  38  and part of the second hard mask  46  to expose the first hard mask  44  surface, and then using another etching process to remove part of the hard mask  44 . This exposes the top surface of the gate electrode  38  and forms a contact hole. Next, aforementioned photo-etching process is repeated to form two additional contact holes exposing the source/drain region  26 , metals are deposited into the contact holes, and CMP process is conducted to remove part of the metal material or even part of the ILD layer  48  to form contact plugs  50  electrically connected the gate electrode  38  and source/drain region  26 . This completes the fabrication of semiconductor device according to a second embodiment of the present invention. 
         [0027]    Referring to  FIGS. 7-10 ,  FIGS. 7-10  illustrate a method for fabricating semiconductor device according to a third embodiment of the present invention. As shown in  FIG. 7 , after forming the gate electrode  38  composed of U-shaped metal layer  34  and low resistance metal layer  36  according to the first embodiment, it would be desirable to remove part of the gate electrode  38  for forming a recess between the spacer  24 , and then conformally form a first mask layer  40  on the ILD layer  32 , CESL  30 , spacer  24 , and gate electrode  38 . 
         [0028]    Next, as shown in  FIG. 8 , the first mask layer  40  atop the ILD layer  32 , CESL  30 , and spacer  24  and part of the first mask layer  40  on the gate electrode  38  are removed so that the remaining first mask layer  40  is only formed against the sidewalls of the recess like a spacer. This forms a first hard mask  44  on the gate electrode  38  and a second mask layer  42  is formed on the ILD layer  32 , CESL  30 , spacer  24 , first hard mask  44 , and gate electrode  38  thereafter. 
         [0029]    Next, as shown in  FIG. 9 , a CMP process is conducted to planarize part of the second mask layer  42  for forming a second hard mask  46  on the gate electrode  38  between first hard mask  44 , so that the top surfaces of the first hard mask  44 , second hard mask  46 , spacer  24 , CESL  30 , and ILD layer  32  are coplanar. 
         [0030]    In this embodiment, the first hard mask  44  and second hard mask  46  are preferably composed of different material, such as the first hard mask  44  is composed of silicon nitride while the second hard mask  46  is composed of silicon oxide, but not limited thereto. Viewing from a structural perspective, both the first hard mask  44  and second hard mask  46  are disposed on the gate electrode  38  and contacting the gate electrode  38  directly, in which the second hard mask  46  is preferably between the first hard mask  44 . 
         [0031]    Next, as shown in  FIG. 10 , another ILD layer  48  is formed on the first hard mask  44 , second hard mask  46 , spacer  24 , CESL  30 , and ILD layer  32 , and a contact plug formation is conducted to form plurality of contact plugs  50  electrically connected to the gate electrode  38  and source/drain region  26 . In this embodiment, the contact plugs  50  could be formed by first using a photo-etching process to remove part of the ILD layer  48  directly above the gate electrode  38  and part of or all of the second hard mask  46  for forming a contact plug. In contrast to the aforementioned first embodiment and second embodiment of using two-step etching processes to remove part of second hard mask  46  and first hard mask  44  composed of different material for forming contact hole, the first hard mask  44  of this embodiment is not U-shaped and not disposed under the second hard mask  46  so that only one photo-etching process is required to form desirable contact hole for contact plug  50  afterwards. Next, aforementioned photo-etching process is repeated to form two additional contact holes exposing the source/drain region  26 , metals are deposited into the contact holes, and CMP process is conducted to remove part of the metal material or even part of the ILD layer  48  to form contact plugs  50  electrically connected to the gate electrode  38  and source/drain region  26 . This completes the fabrication of semiconductor device according to a third embodiment of the present invention. 
         [0032]    Referring to  FIGS. 11-14 ,  FIGS. 11-14  illustrate a method for fabricating semiconductor device according to a fourth embodiment of the present invention. As shown in  FIG. 11 , after forming the gate electrode  38  composed of U-shaped metal layer  34  and low resistance metal layer  36  according to the first embodiment, it would be desirable to remove part of the gate electrode  38  and part of spacer  24  for forming a recess between the ILD layer  32 , and then conformally form a first mask layer  40  on the ILD layer  32 , CESL  30 , spacer  24 , and gate electrode  38 . 
         [0033]    Next, as shown in  FIG. 12 , the first mask layer  40  atop the ILD layer  32  and CESL  30  and part of the first mask layer  40  on the gate electrode  38  are removed so that the remaining first mask layer  40  is only formed against the sidewalls of the recess like a spacer. This forms a first hard mask  44  on the spacer  24  and a second mask layer  42  is then formed on the ILD layer  32 , CESL  30 , first hard mask  44 , and gate electrode  38  thereafter. 
         [0034]    Next, as shown in  FIG. 13 , a CMP process is conducted to planarize part of the second mask layer  42  for forming a second hard mask  46  on the gate electrode  38 , so that the top surfaces of the first hard mask  44 , second hard mask  46 , CESL  30 , and ILD layer  32  are coplanar. 
         [0035]    In this embodiment, the first hard mask  44  and second hard mask  46  are preferably composed of different material, such as the first hard mask  44  is composed of silicon nitride while the second hard mask  46  is composed of silicon oxide, but not limited thereto. Viewing from a structural perspective, both the first hard mask  44  and second hard mask  46  are disposed on the gate electrode  38  or more specifically, the first hard mask  44  is disposed atop the spacer  24  while the second hard mask  46  is disposed on the gate electrode  38 , in which the second hard mask  46  is between the first hard mask  44 . 
         [0036]    Next, as shown in  FIG. 14 , another ILD layer  48  is formed on the first hard mask  44 , second hard mask  46 , CESL  30 , and ILD layer  32 , and a contact plug formation is conducted to form plurality of contact plugs  50  electrically connected to the gate electrode  38  and source/drain region  26 . In this embodiment, the contact plugs  50  could be formed by first using a photo-etching process to remove part of the ILD layer  48  directly above the gate electrode  38  and part of the second hard mask  46  for forming a contact plug. Similar to the third embodiment, the first hard mask  44  of this embodiment is not U-shaped and not disposed under the second hard mask  46  so that only one photo-etching process is required to form desirable contact hole for contact plug  50  afterwards. Next, aforementioned photo-etching process is repeated to form two additional contact holes exposing the source/drain region  26 , metals are deposited into the contact holes, and CMP process is conducted to remove part of the metal material or even part of the ILD layer  48  to form contact plugs  50  electrically connected to the gate electrode  38  and source/drain region  26 . This completes the fabrication of semiconductor device according to a fourth embodiment of the present invention. 
         [0037]    Overall, the present invention preferably forms two hard masks on gate electrode, in which the first hard mask is disposed adjacent to at least two sides of the second hard mask while the first hard mask is composed of silicon nitride and the second hard mask is composed of silicon oxide. According to the aforementioned embodiments, the design of the first hard mask and second hard mask could include a total of four combinations, in which the first hard mask could be either U-shaped or I-shaped, or the spacer could be etched so that the first hard mask could be sitting on the spacer directly. By using the double hard mask design with first hard mask composed of silicon nitride surrounding second hard mask composed of silicon oxide, it would be desirable to prevent the contact plug electrically connected to the gate structure from contacting the contact plug connected to the source/drain region so that short circuit is minimized. 
         [0038]    Those skilled in the art will readily observe that numerous modifications and alterations of the device and method may be made while retaining the teachings of the invention. Accordingly, the above disclosure should be construed as limited only by the metes and bounds of the appended claims.