Abstract:
A soil release composition comprising: 
     (A) a polymer comprising 10 to 100% by weight of constituting units of the formula: ##STR1## wherein R f  is a C 3  --C 21  fluoroalkyl group; R 1  is a hydrogen atom or a C 2  --C 4  acyl group; R 2 , R 3 , R 4  and R 5  are, the same or different, each a hydrogen atom, a methyl group or an ethyl group; A is a group of the formula: --CH 2  CH(OR 1 )CH 2  --OCO-- which R 1  is the same as defined in the above, --CO--, --(CH 2 ) k  N(R 2 )CO-- in which R 2  is the same as defined in the above and k is an integer of 1 to 10, or --(CH 2 ) k  -- in which k is the same as defined in the above; h is an integer of 0 to 5; p is an integer of 1 to 40; q and r are, the same or different, each an integer of 0 to 40, 
     (B) a hydrophilic resin, and 
     (C) optionally a water- and oil-repellent, a weight ratio of (A):(B):(C) being 5-95:95-5:0 or 1-95:5-95:1-50, which can impart stainproofing property with good durability to a substrate such as plastics, fabrics and paper.

Description:
FIELD OF THE INVENTION 
     The present invention relates to a soil release composition and a method for imparting a soil release property to a substrate. 
     BACKGROUND OF THE INVENTION 
     Plastics, fabrics, paper and the like are often treated with a soil release composition to increase their values including durability of a substrate. 
     Conventional soil release compositions contain silicone, hydrocarbon polymer or fluorocarbon polymer (cf. Japanese Patent Publication No. 18346/1978 and Japanese Patent Kokai Publication (unexamined) Nos. 134786/1978, 163269/1980, 129281/1981, 164181/1982, 171762/1982 and 171790/1982). 
     The conventional soil release composition containing silicone or the hydrocarbon polymer, however, imparts only a water absorption property and a soil release property to the substrate or alternatively only a water repellent property to the substrate. The conventional soil release composition containing the fluorine polymer only imparts a water- and oil-repellent property or an undurable soil release property to the substrate. 
     SUMMARY OF THE INVENTION 
     One object of the present invention is to provide a soil release composition which can impart a durable water absorption property and oil-repellency as well as the soil release property to a substrate. 
     Another object of the present invention is to provide a soil release composition which can impart durable water- and oil-repellency as well as the soil release property to a substrate. 
     Further object of the present invention is to provide a method for imparting a soil release property to a substrate with the soil release composition. 
     These and other objects are accomplished by a soil release composition according to the present invention which comprises: 
     (A) a polymer comprising 10 to 100% by weight of constituting units of the formula: ##STR2## wherein R f  is a C 3  -C 21  fluoroalkyl group; R 1  is a hydrogen atom or a C 2  -C 4  acyl group; R 2 , R 3 , R 4  and R 5  are, the same or different, each a hydrogen atom, a methyl group or an ethyl group; A is a group of the formula: --CH 2  CH(OR 1 )CH 2  --OCO-- in which R 1  is the same as defined in the above, --CO--, --(CH 2 ) k  N(R 2 )CO-- in which R 2  is the same as defined in the above and k is an integer of 1 to 10, or --(CH 2 ) k  -- in which k is the same as defined in the above; h is an integer of 0 to 5; p is an integer of 1 to 40; q and r are, the same or different, each an integer of 0 to 40, 
     (B) a hydrophilic resin, and 
     (C) optionally a water- and oil-repellent, a weight ratio of (A):(B):(C) being 5-95:95-5:0 or 1-95:5-95:1-50. 
     In the case where the soil release composition of the present invention comprises the polymer (A) and the hydrophilic resin (B) but not the water- and oil-repellent (C), it can impart the water absorption property and oil repellency as well as the soil release property to the substrate. In the case where the soil release composition of the present invention comprises the polymer (A), the hydrophilic resin (B) and the water- and oil-repellent (C), it can impart water- and oil-repellency as well as the soil release property to the substrate. 
     DETAILED DESCRIPTION OF THE INVENTION 
     The polymer (A) comprising the constituting unit (I) may be prepared by homopolymerizing an unsaturated monomeric compound of the formula: 
     
         R.sub.f --(CF.sub.2).sub.h CH(OR.sup.1)CH.sub.2 --O--(CHR.sup.2 CH.sub.2 O).sub.p --(CHR.sup.3 CH.sub.2 O).sub.q --(CHR.sup.4 CH.sub.2 O).sub.r --A--CR.sup.5 ═CH.sub.2                               (II) 
    
     wherein R f , R 1  to R 5 , A, h, p, q and r are the same as defined in the above, or copolymerizing the monomer (II) with at least one of other ethylenically unsaturated monomers. 
     The fluoroalkyl group R f  in the formulae may be a straight or branched one, and preferably the number of the fluorine atoms in the group is larger than that of the carbon atoms, more preferable the former is twice as large as the latter. The carbon chain in R f  may have at least one oxygen atom between the carbon atoms. 
     Specific examples of the monomer (I) are 
     C 5  F 11  CH 2  CH(OH)CH 2  O(CH 2  CH 2  O) 4  COCH═CH 2 , 
     C 7  F 15  CH 2  CH(OH)CH 2  O(CH 2  CH 2  O) 8  COC(CH 3 )═CH 2 , 
     C 8  F 17  CH 2  CH(OH)CH 2  O(CH 2  CH 2  O) 5  CH 2  NHCOCH═CH 2 , 
     C 8  F 17  CH 2  CH(OH)CH 2  O(CH 2  CH 2  O) 8  COC(CH 3 )═CH 2 , 
     C 8  F 17  CH 2  CH(OCOCH 3 )CH 2  O(CH 2  CH 2  O) 9  COCH═CH 2 , 
     C 9  HF 18  CH 2  CH(OH)CH 2  O(CH 2  CH 2  O) 10  COC(CH 3 )═CH 2 , 
     C 9  F 19  CH 2  CH(OH)CH 2  O(CH 2  CH 2  O) 13  CH 2  CH═CH 2 , 
     C 10  F 21  CH 2  CH(OH)CH 2  O(CH 2  CH 2  O) 16  CH 2  CH(OH)CH 2  OCOC(CH 3 )═CH 2 , 
     C 12  F 21  CH 2  CH(OCOCH 3 )CH 2  O(CH 2  CH 2  O) 22  COC(CH 3 )═CH 2 , 
     C 8  F 17  CH 2  CH(OCOCH 3 )CH 2  O(CH 2  CH 2  O) 10  COCH═CH 2 , 
     C 9  F 19  (CH 2 ) 3  CH(OH)CH 2  O(CH 2  CH 2  O) 5  (CH(CH 3 )CH 2  O) 5  COCH═CH 2 , 
     C 15  F 31  CH 2  CH(OCOCH 2  CH 3 )CH 2  O(CH 2  CH 2  O) 13  CH 2  CH═CH 2 , 
     C 11  F 23  CH 2  CH(OH)CH 2  O(CH 2  CH 2  O) 8  CH 2  CH 2  NHCOCH═CH 2 . 
     Specific examples of the ethylenically unsaturated monomer to be copolymerized with the monomer (II) are vinyl chloride, vinyl acetate, styrene, α-methylstyrene, methyl vinyl ketone, acrylic or methacrylic acid or its derivative of the formula: 
     
         CH.sub.2 ═CR.sup.6 COOR.sup.7                          (III) 
    
     wherein R 6  is a hydrogen atom or a methyl group; R 7  is a hydrogen atom, a sodium atom, a potassium atom, an ammonium group, a C 1  -C 18  alkyl group, a glycidyl group or a group of the formula: --(CH 2  CH 2  O) p  R 8  in which R 8  is a hydrogen atom, a C 1  -C 18  alkyl group or a C 2  -C 18  acyl group and p is the same as defined in the above, --(CH 2  CH 2  O) p  --(CH 2  CH(CH 3 )O) q  --(CH 2  CH 2  O) r  --R 8  in which R 8 , p, q and r are the same as defined in the above or --R 9  --OH in which R 9  is a C 2  -C 6  alkylene group; and acryl- or methacryl-amide or its derivative of the formula: 
     
         CH.sub.2 ═CR.sup.6 CONHR.sup.10                        (IV) 
    
     wherein R 6  is the same as defined in the above, R 10  is a hydrogen atom or a group of the formula: --CH 2  OH or --(CH 2 ) p  --N(CH 3 ) 2  in which p is the same as defined in the above. 
     The monomer(s) can be homo- or co-polymerized by a known method described in, for example, Japanese Patent Kokai Publication (unexamined) No. 134786/1978 and the Journal of the Japanese Association of Adhesives, Vol. 17, No. 9 (1981) 371. 
     The hydrophilic resin includes glyoxal resin, melamine resin, polyamide resin, urethane resin, acrylic resin, triazine resin and the like. Some of the hydrophilic resins are commercially available under trade names of HW-100 (Dainippon Ink and Chemicals), Sumitex resin 901, 1000, M-3, NR-2, NS-2, W-2, AR-2 and AMH-3000 (Sumitomo Chemical), Blencope PWB-4021, PEB-4001 and PEB-4002 (Nippon Oil &amp; Fats), Teisan urethane SL-1780 and SL-4780 (Teikoku Chemical Industries) and SR-1000 (Takamatsu Oil &amp; Fats). 
     The water- and oil-repellent may be a conventionally used one and preferably a copolymer of an acrylic acid derivative of the formula: 
     
         R.sub.f CH.sub.2 CH.sub.2 XCOCH═CH.sub.2               (V) 
    
     wherein R f  is the same as defined in the above and X is an oxygen atom or a sulphur atom, and an acrylic or methacrylic acid or its derivative of the formula: 
     
         CH.sub.2 ═CR.sup.6 COOR.sup.11                         (VI) 
    
     wherein R 6  is the same as defined in the above and R 11  is a hydrogen atom, a sodium atom, a potassium atom, an ammonium group or a C 1  -C 18  alkyl group. The preparation of the copolymer of the compounds (V) and (VI) is described in, for example, Japanese Patent Publication Nos. 851/1969, 31202/1971, 42880/1972, 3438/1975, 4800/1975, 2998/1978, 11324/1982 and 9666/1984 and Japanese Patent Kokai Publication (unexamined) Nos. 132694/1979 and 11888/1983. 
     In the case where the soil release composition of the invention comprises the polymer (A) and the hydrophilic resin but not the water- and oil-repellent (C), the copolymer (A) comprises 10 to 100% by weight, preferably 20 to 80% by weight of the constituting unit (I) to impart sufficient oil repellency and the soil release property to the substrate. For the same reason as above, 5 to 95 parts by weight, preferably 20 to 80 parts by weight of the polymer (A) is contained in the composition. 5 to 95 parts by weight, preferably 10 to 80 parts by weight of the hydrophilic resin (B) is contained in the composition to impart the durable water absorption property and oil repellency as well as the soil release property to the substrate. 
     In the case where the soil release composition of the present invention comprises the polymer (A), the hydrophilic resin (B) and the water- and oil-repellent (C), the polymer (A) comprises 10 to 100% by weight, preferably 20 to 90% by weight of the constituting unit (I) to impart sufficient oil-repellency and the soil release property to the substrate. For the same reason as above, 1 to 95 parts by weight, preferably 5 to 90 parts by weight of the polymer (A) is contained in the composition. 5 to 95 parts by weight, preferably 10 to 80 parts by weight of the hydrophilic resin (B) is contained in the composition to improve the durability of water- and oil-repellency as well as of the soil release property. 1 to 50 parts by weight, preferably 20 to 40 parts by weight of the water- and oil-repellent (C) is contained in the composition to impart sufficient water- and oil-repellency as well as the soil release property to the substrate. 
     The soil release composition of the invention may further contain at least one additive used in the conventional soil release composition. The additive includes a catalyst which cures the hydrophilic resin (B) (e.g. zinc nitrate, magnesium chloride and the like) One of the commercially available catalyst is Sumitex accelerator (trade mark of Sumitomo Chemical). 
     The soil release composition of the invention may be applied to the substrate in the form of a solution, a dispersion, a suspension or an emulsion by a conventional method, for example, dip coating, spray coating, flow coating and the like. A medium in which said components are mixed includes water, acetone, ethyl acetate, tetrahydrofuran, trichlorotrifluoroethane, benzotrifluoride, hexafluoro-m-xylene, and mixtures thereof. The components of the invention are usually mixed in the medium in an amount of 0.5 to 1.0 parts by weight per 100 parts by weight of the medium. 
     Now, the present invention will be explained further in detail by following examples. In the examples, the soil release composition comprising the polymer (A) and the hydrophilic resin (B) but not the water- and oil-repellent (C) is examined for the properties of water absorption, oil repellency and soil release as well as their durability. The soil release composition comprising the the polymer (A), the hydrophilic resin (B) and the water- and oil-repellent (C) is examined for the properties of water-repellent, oil-repellent and soil release as well as their durability. In the examples, parts and % are by weight unless otherwise indicated. 
     Copolymers (A1) to (A5) and Polymers (i) to (iii) for comparison to be used in Examples and Comparative Examples were prepared in following Preparation Examples. 
    
    
     PREPARATION EXAMPLE 1 
     Preparation of Copolymer (A1) 
     In a four-necked 200 ml flask equipped with a thermometer, a condenser, a stirrer and an inlet for introducing nitrogen, there were added a fluorine-containing monomer mixture (14 g) of the formula: 
     
         CF.sub.3 CF.sub.2 (CF.sub.2 CF.sub.2).sub.n CH.sub.2 CH(OH)CH.sub.2 --O--Z--COC(CH.sub.3)═CH.sub.2 
    
     in which Z is a polyethyleneoxide residue having an average molecular weight of 400 and which contains the compounds wherein n is 2, 3, 4, 5 and 6 in amounts of 3%, 55%, 28%, 12% and 3%, a methacrylate derivative (14 g) of the formula: 
     
         HO--Z--COC(CH.sub.3)═CH.sub.2 
    
     wherein Z is the same as defined in the above, isopropanol (112 g) and dodecylmercaptan (0.4 g), and stirred at 67° C. for 30 minutes with introducing nitrogen. Thereafter, perbutyl pivalate (0.17 g) was added to initiate the reaction and the polymerization was carried out at the same temperature for 6 hour with stirring. After removing isopropanol from the reaction mixture, the residue was washed with benzene and dried under reduced pressure to obtain Copolymer (A1). 
     PREPARATION EXAMPLES 2-5 AND COMPARATIVE PREPARATION EXAMPLES 1-3 
     Preparation of Copolymers (A2) to (A5) and 
     Polymers (i)-(iii) 
     In the same manner as in Preparation Example 1 but using the following monomers, the polymerization was carried out to obtain the polymer: 
     Preparation Example 2 (Copolymer (A2)) 
     The fluorine-containing monomer mixture as used in Preparation Example 1 (100 parts), the methacrylate derivative as used in Preparation Example 1 (100 parts) and HOCH 2  --NHCOCH═CH 2  (20 parts). 
     Preparation Example 3 (Copolymer (A3)) 
     The fluorine-containing monomer mixture as used in Preparation Example 1 (100 parts), styrene (300 parts) and glycidyl methacrylates (100 parts). 
     Preparation Example 4 (Copolymer (A4)) 
     The fluorine-containing monomer mixture as used in Preparation Example 1 (100 parts) and H--Y--SCH 2  COOCH 2  CH(OH)--CH 2  OCOC(CH 3 )═CH 2  wherein Y is a polystyrene residue having an average molecular weight of 1,500 (100 parts). 
     Preparation Example 5 
     The fluorine-containing monomer mixture as used in Preparation Example 1 (100 parts), the methacrylate derivative as used in Preparation Example 1 (80 parts) and butyl acrylate (20). 
     COMPARATIVE PREPARATION EXAMPLE 1 (Polymer (i)) 
     CF 3  CF 2  (CF 2  CF 2 ) 3  CH 2  CH 2  OCOCH═CH 2  (100 parts), CH 3  O--W--COC(CH 3 )═CH 2  wherein W is a polyethyleneoxide residue having an average molecular weight of 660 (80 parts) and HOCH 2  NHCOCH═CH 2  (20 parts). 
     COMPARATIVE PREPARATION EXAMPLE 2 (Polymer (ii)) 
     H[SCH 2  CH(CH 3 )COO(CH 2  CH 2  O) 4  COC(CH 3 )CH 2  ] 10  SH (10 parts) and C 8  H 17  SO 2  N(C 3  H 7 )CH 2  CH 2  OCOC(CH 3 )═CH 2  (60 parts). 
     COMPARATIVE PREPARATION EXAMPLE 3 (Polymer (iii)) 
     C 8  H 17  SO 2  N(C 3  H 7 )--W--COC(CH 3 )═CH 2  (100 parts) and CH 3  O--W--COCH═CH 2  (100 parts) wherein W is the same as defined in the above. 
     EXAMPLES 1-5 AND COMPARATIVE EXAMPLES 1-2 
     Preparation of a soil release composition 
     The copolymer (A) or the comparative polymer, a hydrophilic resin and other additives were added according to the following composition to 100 parts of water and stirred to prepare a soil release composition with water-absorption property and oil-repellency: 
     Composition 
     Examples 1 and 2 
     Copolymer (A1) (0.5 part), 
     Sumitex resin 901 (0.5 part) and Sumitex resin W-2 (0.5 part) (hydrophilic resins), and 
     zinc nitrate (0.5 part). 
     Example 3 
     Copolymer (A2) (0.5 part), and 
     Blencope PEB-4201 (0.5 part) (a hydrophilic resin) 
     Example 4 
     Copolymer (A3) (0.5 part), and 
     Sumitex resin AR-2 (0.5 part) (a hydrophilic resin). 
     Example 5 
     Copolymer (A4) (0.5 part), and 
     Sumitex resin AR-2 (0.5 part). 
     Comparative Example 1 
     Polymer (ii) (0.5 part), 
     Sumitex resin 901 (0.5 part) and Sumitex resin W-2 (0.5 part), and 
     zinc nitrate (0.5 part). 
     Comparative Example 2 
     Polymer (ii) (0.5 part), and 
     Sumitex resin AR-2 (0.5 part). 
     Each composition prepared in Examples 1-5 and Comparative Examples 1-2 was applied to various substrates and its water-absorption property, oil-repellency property and soil release ability as well as their durability were examined. 
     When the substrate was cloth, it was dipped in the composition for 5 minutes, squeezed with rollers, dried at 80° C. for 10 minutes and heated at 150° C. for 5 minutes. When the substrate was in the form of a plate, it was dipped in the composition for 5 minutes, dried at 80° C. for 10 minutes with leaning it against a wall, and then heated at 150° C. for 5 minutes. 
     The properties of the treated substrate were evaluated as follows: 
     Water-absorption property 
     A drop of water is dropped on the surface of the treated substrate and a time (seconds) till complete disappearance of water is confirmed by naked eyes is measured. 
     Oil-repellency 
     A drop of 4 mm in diameter of a following solvent mixture is dropped on the substrate and a critical composition of the mixture with which the drop maintains its form for three minutes is determined by naked eyes, and following point is assigned to express the oil-repellency. The larger the point, the better the oil-repellency. 
     
         ______________________________________Point     Nujol (vol. %)                 n-Hexane (vol. %)______________________________________100       50          5090        60          4080        70          3070        80          2050        100          0 0        (100% Nujol not retained)______________________________________ 
    
     Stainproofing test 
     The treated substrate was dipped in a waste motor oil for 10 hours and the surface condition was observed by naked eyes. The criteria are as follows: 
     1: Very bad stain remains. 
     2: Bad stain remains. 
     3: Slight stain remains. 
     4: Little stain remains. 
     5: No stain remains. 
     Durability 
     The treated substrate is washed ten times according to JIS H 103 with a detergent concentration of 2 g/l (detergent: &#34;Super Zabu&#34; manufactured by Kao) at 40° C. with a bath ratio of 1:40 and then subjected to the water-absorption test, the oil-repellency test and the soil release tests as described in the above. 
     The results are shown in Tables 1-1 to 1-3. 
     
                                           TABLE 1__________________________________________________________________________Water absorption (sec.) (Before washing/after washing)ExampleNylon    PET.sup.1        PET/cotton               Cotton                   Wool                       PET ABS.sup.2                               PMMA.sup.3                                    AlNo.  cloth    cloth        cloth  cloth                   cloth                       plate                           plate                               plate                                    plate__________________________________________________________________________1    30/30    35/35        30/30  10/10                   30/30                       40/40                           40/40                               40/40                                    40/402    30/30    35/35        30/30  10/10                   30/30                       40/40                           40/40                               40/40                                    40/403    20/20    25/25        20/20  10/10                   20/20                       30/30                           30/30                               30/30                                    30/304    35/35    40/40        30/30  20/20                   35/35                       50/50                           50/50                               50/50                                    50/505    35/35    40/40        30/30  20/20                   35/35                       50/50                           45/45                               45/45                                    45/45Comp. 1Both    Both        Both   Both                   Both                       Both                           Both                               Both Both&gt;60 &gt;60 &gt;60    &gt;60 &gt;60 &gt;60 &gt;60 &gt;60  &gt;60Comp. 2Both    Both        Both   Both                   Both                       Both                           Both                               Both Both&gt;60 &gt;60 &gt;60    &gt;60 &gt;60 &gt;60 &gt;60 &gt;60  &gt;60__________________________________________________________________________   Oil-repellency   (Before washing/after washing)Example PET     PET/cotton                  Cotton   PET AlNo.     cloth   cloth  cloth    plate                               plate__________________________________________________________________________1       90/70   90/70  90/50    90/70                               90/702       90/70   90/70  90/70    90/70                               90/703       90/70   --     90/50    --  --4       --      --     --       --  90/705       --      --     --       --  90/70Comp. 1 80/70   80/70  80/70    90/70                               90/70Comp. 2 90/50   60/50  60/50    --  --__________________________________________________________________________Stainproofing (Before washing)ExampleNylon    PET PET/cotton               Cotton                   Wool                       PET ABS PMMA AlNo.  cloth    cloth        cloth  cloth                   cloth                       plate                           plate                               plate                                    plate__________________________________________________________________________1    --  5/5 5/4    5/4 --  5/5 --  --   5/52    --  5/5 5/4    5/4 --  5/5 --  --   5/53    --  5/4 --     --  --  --  --  5/5  --4    5/5 --  --     --  5/4 --  5/4 --   5/55    5/5 --  --     --  --  --  --  --   --Comp. 13/1 3/1 4/1    4/1 --  4/1 4/1 4/1  4/1Comp. 22/1 2/1 2/1    2/1 --  --  --  --   --__________________________________________________________________________ Note: .sup.1 Polyethylene terephthalate. .sup.2 Acrylonitrile/butadiene/styrene copolymer. .sup.3 Polymethyl methacrylate. 
    
     EXAMPLES 6-15 AND COMPARATIVE EXAMPLES 3-6 
     The copolymer (A) or the comparative polymer, a hydrophilic resin, a water- and oil-repellent and other additives in the following amounts were added according to the following composition to 100 parts of water and stirred to prepare a soil release composition with water-absorption property and oil-repellency: 
     Composition 
     Example 6 
     Copolymer (A1) (0.5 part), 
     Sumitex resin 901 (0.5 part) and Sumitex resin W-2 (0.5 part), 
     a water- and oil-repellent (A) 1 ) (0.1 part), and 
     zinc nitrate (0.5 part). 
     Example 7 
     Copolymer (A2) (0.5 part), 
     Sumitex resin M-3 (0.5 part), 
     a water- and oil-repellent (A) (0.1 part), and 
     Sumitex accelerator (0.5 part). 
     Example 8 
     Copolymer (A2) (0.5 part), 
     Teisan urethane SL-4780 (0.5 part), and 
     a water- and oil-repellent (A) (0.1 part). 
     Example 9 
     Copolymer (A3) (0.5 part), 
     Sumitex resin M-3 (0.5 part), 
     a water- and oil-repellent (A) (0.1 part), and 
     Sumitex accelerator (0.5 part). 
     Example 10 
     Copolymer (A3) (0.5 part), 
     Serbifan MKP1 (0.5 part) 
     a water- and oil-repellent (A) (0.05 part) and a water- and oil-repellent (B) 2 ) (0.2 part), and 
     Serbifan KP2 (0.2 part). 
     Example 11 
     Copolymer (A4) (0.5 part), 
     Sumitex resin M-3 (0.5 part) 
     a water- and oil-repellent (A) (0.1 part), and 
     Sumitex accelerator (0.5 part). 
     Example 12 
     Copolymer (A4) (0.5 part), 
     Sumitex resin NR-2 (0.5 part), 
     a water- and oil-repellent (A) (0.1 part), and 
     zinc nitrate (0.5 part). 
     Example 13 
     Copolymer (A5) (0.5 part), 
     Sumitex resin (0.5 part), 
     a water- and oil-repellent (A) (0.2 part), and 
     Sumitex accelerator (0.5 part). 
     Example 14 
     Copolymer (A5) (0.5 part), 
     Blencope 4001 (0.5 part), and 
     a water- and oil-repellent (A) (0.2 part). 
     Example 15 
     Copolymer (A5) (0.5 part), 
     Serbifan MKP1 (0.5 part), 
     a water- and oil-repellent (A) (0.2 part), and 
     Serbifan KP2 (0.2 part). 
     Comparative Example 3 
     Polymer (i) (1.0 part), 
     Sumitex resin M-3 (0.5 part), 
     a water- and oil-repellent (A) (0.2 part), and 
     Sumitex accelerator (0.5 part). 
     Comparative Example 4 
     Polymer (i) (0.5 part), 
     Serbifan MKP1 (0.5 part) 
     a water- and oil-repellent (A) (0.05 part) and a water- and oil-repellent (B) (0.2 part), and 
     Serbifan KP2 (0.2 part). 
     Comparative Example 5 
     Polymer (iii) (0.5 part), 
     Sumitex resin 901 (0.5 part) and Sumitex resin W-2 (0.5 part), 
     a water- and oil-repellent (A) (0.1 part), and 
     zinc nitrate (0.5 part). 
     Comparative Example 6 
     Polymer (iii) (0.5 part), 
     Teisan urethane SL-4780 (0.5 part), and 
     a water- and oil-repellent (A) (0.1 part). Note: A water- and oil-repellent (A): A copolymer of C 8  F 17  --CH 2  CH 2  OCOCH═CH 2  and stearyl methacrylate having an average molecular weight of 25,000. 
     A water- and oil-repellent (B): A copolymer of C 8  F 17  --CH 2  CH 2  SCOCH═CH 2  and stearyl methacrylate having an average molecular weight of 25,000. 
     Each composition prepared in Examples 6-15 and Comparative Examples 3-6 was applied to various substrates and its water-repellency, oil-repellency and soil release ability as well as their durability were examined. 
     The composition was applied to the substrate in the same manner as in Examples 1-5. 
     The water-repellency was evaluated according to JIS L-1005. The oil-repellency and the soil release ability were evaluated in the same ways as in Examples 1-5. The durability of these properties was also evaluated in the same way as in Examples 1-5. 
     The results are shown in Tables 2-1, 2-2 and 2-3. 
     
                                           TABLE 2__________________________________________________________________________ExampleNylon     PET  PET/cotton                 Cotton                      Wool PET  ABS  PMMA AlNo.  cloth     cloth          cloth  cloth                      cloth                           plate                                plate                                     plate                                          plate__________________________________________________________________________Water-repellancy (Before washing/after washing) 6   --   100/100          90/80  90/80                      --   100/100                                --   --   100/90 7   100/100     100/100          100/100                 100/90                      --   --   100/100                                     --   -- 8   100/100     --   --     --   100/100                           --   100/100                                     --   100/100 9   100/100     100/100          --     --   --   --   --   --   --10   90/80     90/80          --     --   --   --   --   --   90/8011   100/100     100/100          --     --   --   --   --   --   --12   --   --   100/80 100/90                      --   --   --   --   --13   --   100/100          100/100                 100/100                      --   --   --   --   --14   --   --   --     --   --   100/100                                --   100/100                                          100/10015   --   --   --     --   --   100/100                                100/100                                     --   100/100Comp. 390/80     90/80          90/80  90/80                      --   100/90                                --   --   100/90Comp. 4100/100     100/100          --     --   --   100/100                                100/100                                     100/100                                          100/100Comp. 580/60     80/60          80/60  70/60                      80/60                           --   --   --   100/100Comp. 680/60     80/60          80/60  70/60                      80/60                           --   --   --   100/100Oil-repellency (Before washing/after washing) 6   --   100/90          100/80 100/70                      --   100/90                                --   --   100/90 7   100/90     100/90          100/90 100/90                      --   --   100/80                                     --   -- 8   100/90     --   --     --   100/90                           --   90/80                                     --   100/90 9   100/100     100/90          --     --   --   --   --   --   --10   90/80     90/80          --     --   --   --   --   --   90/8011   100/100     100/100          --     --   --   --   --   --   --12   --   --   100/80 100/90                      --   --   --   --   --13   --   100/90          100/90 100/90                      --   --   --   --   --14   --   --   --     --   --   100/100                                --   100/100                                          100/10015   --   --   --     --   --   --   100/100                                     --   100/100Comp. 3100/90     100/90          100/90 100/80                      --   100/90                                --   --   100/90Comp. 490/70     90/70          --     --   --   90/80                                90/80                                     90/80                                          90/80Comp. 590/70     90/70           80/50  80/50                      80/50                           --   --   --   --Comp. 690/70     90/70           80/50  80/50                      80/50                           --   --   --   --Stainproofing (Before washing/after washing) 6   --   5/5  5/4    5/3  --   5/5  --   --   5/5 7   5/5  5/5  5/5    5/5  --   --   5/5  --   -- 8   5/5  --   --     --   5/5  --   5/4  --   5/5 9   5/5  5/5  --     --   --   --   --   --   --10   5/4  5/4  --     --   --   --   --   --   5/411   5/5  5/5  --     --   --   --   --   --   --12   --   --   5/5    5/5  --   --   --   --   --13   --   5/5  5/5    5/5  --   --   --   --   --14   --   --   --     --   --   5/5  --   5/5  5/515   --   --   --     --   --   --   5/5  --   5/5Comp. 32/1  2/1  2/1    2/1  --   2/1  --   --   2/1Comp. 42/2  2/2  --     --   --   2/2  2/2  2/2  2/2Comp. 54/1  4/1  4/1    4/1  4/1  --   --   --   --Comp. 64/2  4/2  4/2    4/2  4/2  --   --   --   --__________________________________________________________________________