Abstract:
A semiconductor component on mutually opposing sides is joined in a first and a second bonded connection with a heat conducting body each. The heat-conducting bodies are joined in a third bonded connection in the region of the sections thereof extending away from the semiconductor element. A spacer, which with regard to the third connection, is disposed on the opposite side of the semiconductor component between the heat-conducting bodies, in conjunction with the joining zone thickness of the third connection being greater than that of the first or the second joining zone to ensure that defined joining zone thicknesses in the bonded connection is maintained during the joining process. The third connection can be used for at least partial heat transfer of the waste heat of the semiconductor component, particularly to a heat sink that is connected to the heat transfer device.

Description:
PRIORITY 
     This patent application claims the priority benefit of International Application PCT/DE2009/000770, filed on Jun. 2, 2009, and German patent application 10 2008 026 801.1, filed Jun. 2, 2008, the disclosure content of both of which is hereby incorporated by reference herein. 
     FIELD 
     The invention relates to a heat transfer device with at least one semiconductor component, in particular a laser or light-emitting diode element, according to the preamble of claim  1 , and to a method for its assembly. 
     BACKGROUND 
     In order to reduce the thermal resistance of heat transfer devices which support the cooling of laser diode bars, it is known for example from the patent and unexamined patent applications U.S. Pat. No. 5,325,384, WO 2006 098 897 A1 and WO 2007 082 508 A1 to attach heat conducting bodies to opposing sides of the laser bar. If the heat removal capacity of the heat conducting bodies is different—for example because the heat sinks connected to the heat conducting bodies have a clearly different thermal resistance, the thermal resistance of the heat transfer device can be reduced by bringing both heat conducting bodies into thermal connection with each other in heat transfer sections beside the laser diode bar, with the result that a part of the heat of the more poorly cooled heat conducting body can be absorbed by the better cooled one. In extreme cases, only one of the heat conducting bodies is connected to a heat sink and must absorb virtually all of the heat of the laser diode bar absorbed by the other heat conducting body. Such an arrangement is known from publication no. 68760Q from Proc. SPIE vol. 6876 (2008) in which, in order to achieve a good thermal connection between the heat conducting bodies, a thermally highly conductive electrically insulating aluminium nitride ceramic plate was soldered with the help of two metallic solder layers on the side of the laser diode bar facing away from the light emission between the epitaxy-side metallic heat removal body and the substrate-side metallic heat conducting body. 
     With this and similar arrangements, there is the problem that the highly heat conductive intermediate element which is arranged between the heat transfer sections of the heat conducting bodies should preferably have the same thickness as the laser diode bars between its two sides, which are connected by heat absorbing sections of the heat conducting bodies for heat dissipation, in order that the thickness of the joining zones between the laser bar and the heat absorbing sections of the heat conducting bodies on the one hand and between the intermediate element and the heat transfer sections of the heat conducting bodies on the other hand can be kept the same on the one hand and kept constant over the extent of each joining zone on the other hand. 
     A constant, uniform and in particular small joining zone thickness is essential in particular for the connection of the laser diode bar in order to ensure a uniform quality and reliability of the diode laser that is both thermally and also electrically and optically highly loaded. The thickness of laser diode bars is different both within a batch and between several batches. The same applies to the intermediate elements. A reproducible matching of the thicknesses of laser diode bars and intermediate elements to less than 2 μm difference is either costly in production terms or accompanied by a time-consuming selection and allocation process. 
     SUMMARY 
     An object of the invention is therefore to describe a heat transfer device with a semiconductor component which eliminates the mentioned disadvantages. 
     The object of the invention is in particular to ensure a uniform and substantially constant thickness of the joining zones between the laser diode bars and the heat-absorbing heat conducting bodies in a continuous production process for diode lasers. At the same time, an object of the invention is to make possible a good heat transfer from one heat conducting body to another. 
     The object is achieved by a heat transfer device with at least one semiconductor component, in particular a laser or light-emitting diode element, with the characterizing features of claim  1 , and a method for its assembly according to claim  15 . 
     Seen from the semiconductor element, the spacer arranged between the support sections is located according to the invention on the other side of the heat transfer sections. When the heat conducting bodies are connected to one another and/or at least one heat conducting body is connected to the semiconductor component, it absorbs part of the compressive force which is exerted by one heat conducting body on the other during assembly, and sets the distance of the heat conducting bodies from one another between the support sections. Because of its preferably great distance from the semiconductor component, this distance need not correspond precisely to the thickness of the semiconductor component plus the first and second joining zones, and the angle error caused by a corresponding difference remains so small that a variation, caused by an angle error, in the thickness of the first and second joining zones is in the negligible range. 
     The thickness of the spacer, or the distance between the support points, is preferably matched to the positions of opposing support surfaces of the support sections in respect of the heat entry surfaces and the thickness of the semiconductor component such that none of the first and second joining zones can vary in thickness by more than +/−50%. Applied to support and heat entry surfaces which are arranged coplanar to each other on each of the two heat conducting bodies on a common axis oriented in a preferred direction, to a parallelepiped semiconductor component and to two equally thick first and second joining zones of average thickness d, the distance between the support points (the thickness of the spacer) preferably differs, at a distance in preferred direction from the centre of the semiconductor component which corresponds to p times the extent of the semiconductor component in preferred direction, by no more than +/−2d·(p−1) from the thickness of the semiconductor component. 
     If the support and heat entry surfaces are parallel to one another, but not coplanar, but offset relative to one another, the abovenamed allowed deviation thus increases or decreases for each such heat conducting body by precisely this offset. 
     Only the fact that the thickness of the third joining zone between the heat transfer sections is greater than the thicknesses of the first or second joining zone makes possible the supporting effect of the spacer, as otherwise the supporting effect lies in the area between the heat transfer sections, which is known to lead to the problems named at the outset on the one hand and has the undesired result on the other hand that the thickness of the third joining zone determines the thickness of at least one of the first and second joining zones. 
     However, for a reliable connection of a laser diode bar it is actually desirable that the thickness of the first and second joining zones determines that of the less important one—namely the third—which is effected by the supporting effect of the spacer during assembly with a thickness of the third joining zone that is greater compared with the first and second joining zones. 
     By joining zone is meant the layer of a solidified joining agent. Joining zone and joining gap differ in that the joining zone contains only joining agent, the joining gap at least one joining zone and optionally further components and joining zones which jointly fully bridge the joining gap by adhesion, bonding, welding or soldering. 
     Thus the third joining zone can fully extend over the joining gap, wherein the joining gap is filled fully and exclusively with joining agent. On the other hand, the third joining zone can also extend with respect to its thickness only over a part of the distance between the heat transfer sections which is determined by the joining gap. In this case, there can be arranged in the joining gap, in addition to the third joining zone, a fourth joining zone as well as an intermediate body positioned between the third and fourth joining zones. As joining agents as a rule display worse heat conducting properties than solids that cannot be used as joining agents it is advantageous, in the case of joint gaps the thicknesses of which correspond approximately to more than half the thickness of the semiconductor component, to use an intermediate body of metal (for example copper), ceramic (for example aluminium nitride) or crystal (for example diamond). 
     The order in which the adhesion bonding of the joining partners takes place, and whether and which joining agents and/or joining auxiliaries are used for connection, is unimportant. The adhesion bonding between the heat transfer sections can a) take place after the adhesion bond has been established between the semiconductor component and the first and the second heat conducting body. The adhesion bonding between the heat transfer sections can in addition b) take place at least at times jointly with the establishment of the adhesion bond between the semiconductor component and the second heat conducting body once the adhesion bond between the semiconductor component and the first heat conducting body has been established—or vice versa. Finally, c) the formation of the adhesion bond between the heat transfer sections can take place at least at times jointly with the formation of the connections by adhesion of the semiconductor component to both heat conducting bodies. 
     In all cases, as a result of its supporting effect the spacer ensures in at least the joining process in which both heat conducting bodies become bonded by adhesion to one another—by means of the semiconductor component via the first and second joining zones or in the region of the heat transfer sections via the third joining zone—a balanced joining zone thickness of the joining zones in the production of which it participates according to the invention. 
     It is advantageous according to the invention if the thickness of the third joining zone is greater than the thickness of the first or second joining zone which is formed at least at times together with the third. 
     If the thicknesses of the first and the second joining zones are similar and small—for example in the range of 1 micrometer to approximately 10 micrometers with a maximum thickness ratio of two—it is advantageous if the thickness of the third joining zone is greater than the thicknesses of the first and the second joining zones—whereby it is greater than whichever is the greater thickness of the first and the second joining zones. 
     To make the assembly requirements less burdensome, at least sections of the third joining zone have a greater thickness than the sum of the thicknesses of the first and second joining zones. 
     The invention establishes an efficient heat redirection by connection by adhesion bonding of heat conducting body parts beside of the semiconductor component, which itself is soldered with high-quality joining precision between the heat conducting bodies for efficient heat emission. 
     The use of a spacer during assembly does not necessarily mean that the spacer must remain in position after assembly. If the heat conducting bodies are metallic at least in the support sections and if their respective metallic region is electrically connected to the corresponding contact surfaces of the semiconductor component, an electrically conductive, preferably metallic, spacer can be used as shorting bridge between the metallic support sections which protects the semiconductor component against electrostatic discharges (ESD). When the assembled semiconductor component, for example a diode laser, is commissioned this shorting bridge is removed and can be reinserted again between the support sections following operation—shorting the semiconductor component. 
     For this, the heat conducting bodies preferably each have at least one metallic region or consist predominantly or completely of metal or an electrically conductive carbon-metal composite material, for example diamond-silver. The electrically conductive regions each extend from the support section into the heat absorbing section of the heat conducting body and are electrically connected to the corresponding contact surfaces of the semiconductor component. If facing heat transfer surfaces of the heat transfer section are each a constituent of these electrically conductive regions, the connection of the two heat transfer sections must have an electrical insulation—either in the form of an electrically insulating intermediate body or in the form of a joining zone with an electrically insulating joining agent. 
     If on the other hand only one, or none, of the facing heat transfer surfaces of the heat transfer sections is a constituent of these electrically conductive regions, an electrically conductive joining agent—for example a metallic solder—can also be used to connect the two heat transfer sections without an electrically insulating intermediate body having to be used. In this case, both heat conducting bodies can be directly connected to each other by a single metallic solder layer. This is possible inter alia with heat conducting bodies that consist predominantly of highly heat conductive electrically insulating materials, for example aluminium nitride, beryllium oxide, diamond etc., and carry electric conductors which extend from opposing support surfaces of the support sections to opposing heat entry surfaces of the heat absorbing sections. Further metallic conductors can be attached to opposing surfaces of the heat transfer sections without being electrically connected to the semiconductor component, in order to facilitate the direct connection of the heat conducting bodies with the help of a metallic solder. An active solder which wets the non-metallic regions of the heat transfer sections can naturally equally be used to form the connection. 
     When using metallic heat conducting bodies, it advantageous to dispense with an electrically insulating intermediate element in favour of an electrically insulating joining agent for production and financial reasons. While the thickness of the electrically insulating joining zone should be as small as possible on thermal grounds, the assembly technique according to the invention requires a thickness of the third joining zone of at least the smaller of the thicknesses of the first and the second joining zones. In addition, it is necessary on electrical grounds to have a thickness which is large enough to reliably ensure the electrical insulation in the production process. Where the thicknesses of the first and second joining zones are small and similar, it is advantageous if the thickness of the third joining zone is greater than the greater of the thicknesses of the first and second joining zones; preferably it is actually greater than their sum. 
     If the spacer is to remain in position after assembly is complete—for example because it was secured to at least one heat conducting body during or before assembly or by adhesion—an electrically insulating spacer is to be used when using heat conducting bodies the opposing support surfaces of which form part of metallic regions which are electrically connected to the semiconductor component. 
     In this sense, it is also clear that the spacer need at no time necessarily be present as a separate component. While in principle, on symmetry grounds vis-à-vis the semiconductor component and the concomitant simplification of the achievement of the required joint tolerances, preference is to be given to the spacer as a distinct physical entity, in a less preferred development of the invention the spacer is an integral constituent of at least one of the two heat conducting bodies and is present in the form of a raised section which projects out of the support section out over the heat transfer section in the direction of the semiconductor component. Advantageously, the number of components used for assembly would thus be reducible by one from five to four or from four to three. 
     Preferably, the electrical connection of the semiconductor component takes place without adding further bodies or components in the heat transfer device by means of the heat conducting bodies, to which end heat entry surfaces rest on metallic regions of the heat absorbing sections. Preferably, both heat conducting bodies are metallic. The heat conducting bodies are preferably connected to the contact surfaces with a metallic solder—for example gold-tin, indium etc. 
     Preferably, the heat conducting bodies are formed plate-shaped. 
     In order to ensure a high thermal conductance of the heat conducting plates, the thickness of the plates in perpendicular direction to at least one of the contact surfaces is preferably greater than at least one lateral dimension of the semiconductor component parallel to one or both contact surfaces. Transferred to individual laser diodes, this means that plate thickness is greater than the width of the laser diode directed perpendicular to the light emission direction/resonator length and parallel to the plane of one or both contact surfaces; transferred to laser diode bars this means that plate thickness is greater than the resonator length of the laser diode bar. 
     In order to ensure a high thermal conductance of the joining zone, the areal extent of the joining zones is greater than the parallel areal extent of the laser diode element. 
    
    
     
       BRIEF DESCRIPTION OF THE FIGURES 
       The invention is explained in more detail below with the help of embodiment examples. There are shown in 
         FIG. 1   a  a side view of the components of a first embodiment example of the heat transfer device according to the invention, 
         FIG. 1   b  a side view of the first embodiment example of the heat transfer device according to the invention, 
         FIG. 2   a  a side view of the components of a second embodiment example of the heat transfer device according to the invention, 
         FIG. 2   b  a side view of the second embodiment example of the heat transfer device according to the invention. 
     
    
    
     DETAILED DESCRIPTION 
     All embodiment examples represent diode laser components with a laser diode bar. Equally, they can also represent radiation sources with one or more single or multiple emitter laser diodes or single or multiple emitter light-emitting diodes or light-emitting diode bars arranged alongside one another. In addition, the heat transfer device is also suitable for cooling semiconductor switching elements, for example high-power transistors, high-power thyristors etc. 
     Embodiment Example 1 
     The components used for the production of a first variant of the first embodiment example of the heat transfer device according to the invention are shown in  FIG. 1   a : The laser diode bar  10  has a first, epitaxy-side contact surface  11  for electrical connection as well as a second, substrate-side contact surface  12  opposite the epitaxy-side contact surface. The laser diode bar has a resonator length of 2 mm. The light emission taking place during operation is identified by the arrow  15  which is arranged on an optical axis. A 100-μm thick aluminium nitride ceramic plate  40  is arranged behind the 120-μm thick laser diode bar in the opposite direction to light emission. It has opposing metallized heat transfer surfaces  41  and  42  oriented epitaxy- and substrate-side. 
     A first, epitaxy-side, plate-shaped heat conducting body  20  consists predominantly of a diamond-silver composite and has a heat entry surface  21  opposite the epitaxy-side contact surface  11  as well as a heat transfer surface  22  which lies opposite the epitaxy-side heat transfer surface  41  of the aluminium nitride ceramic plate  40 . It is 4 mm thick. 
     A second, substrate-side, plate-shaped heat conducting body  30  likewise consists predominantly of a diamond-silver composite and has a heat entry surface  31  opposite the substrate-side contact surface  12  as well as a heat transfer surface  32  which lies opposite the substrate-side heat transfer surface  42  of the aluminium nitride ceramic plate  40 . It is likewise 4 mm thick. 
     The length of the aluminium nitride ceramic plate  40  —i.e. its extent in a preferred direction which corresponds to the extension direction of the heat conducting bodies  20 / 30  from the heat absorbing section  25 / 35  to the support section  27 / 37  (from left to right in the drawing plane) —is 10 mm. 
     In preparation for the establishment of an adhesion bond or material closure between these components  10 ,  20 ,  30 ,  40  for the formation of the first variant of the first embodiment example, the epitaxy-side heat conducting body  20  is coated with 5 μm gold-tin solder in the region of the epitaxy-side heat entry surface  21  and in the region of the epitaxy-side heat transfer surface  22 . Analogously, the substrate-side heat conducting body  30  is coated with 5 μm gold-tin solder in the region of the substrate-side heat entry surface  31  and in the region of the substrate-side heat transfer surface  32 . 
     Furthermore, a foil of a gold-tin solder preform 25 μm thick is introduced between the solder layer on the substrate-side heat transfer surface  32  of the epitaxy-side heat conducting body  20  and the substrate-side heat transfer surface  42  of the aluminium nitride ceramic plate  40 . Arranged on the side of the aluminium nitride ceramic plate  40  facing away from the laser diode bar  10  is a high-grade steel foil  60  125 μm thick as spacer between two opposing support surfaces  23  and  33  of the epitaxy-side heat conducting body  20  and of the substrate-side heat conducting body  30 . 
     Different sections of the heat conducting body with different functions are highlighted in  FIG. 1   b  by dotted dividing lines. 
     To establish the adhesion bond between the components  10 ,  20 ,  30 ,  40  to be joined, in a first joining process the laser diode bar  10  is soldered epitaxy-side onto the epitaxy-side heat absorbing section of the epitaxy-side heat conducting body  20  and the aluminium nitride ceramic plate  40  onto the epitaxy-side heat transfer section  26  of the epitaxy-side heat conducting body  20 . 
     In preparation for the second joining process, which is to connect the substrate-side heat conducting body  30  to the laser diode bar  10  and the aluminium nitride ceramic plate  40 , it is to be taken into account that the stack comprising aluminium nitride ceramic block  40  and solder preform together with the solder layers is at 135 μm the highest point above the plane of the surfaces  21 ,  22  and  23  compared with the plane of the surfaces  31 ,  32  and  33 . Against this, the laser diode bar together with the solder layers is only 130 μm high while the spacer is 125 μm high. Thus the substrate-side heat conducting body rests only in the region of the heat transfer section. 
     During the second joining process the solder preform melts and yields under a pressure exerted via the substrate-side on the epitaxy-side heat conducting body. In doing so the substrate-side heat absorbing section  31  comes into contact with the substrate-side contact surface  12  of the laser diode bar and the substrate-side support section in contact with the spacer which rests on the epitaxy-side support section. 
     At the end of the assembly process, all components have passed through temperature profiles which are suitable to establish both a high-quality soldered connection  13  between the laser diode bar  10  and an epitaxy-side heat absorbing section  25  of the epitaxy-side heat conducting body  20  and a high-quality soldered connection  14  between the laser diode bar  10  and a substrate-side heat absorbing section  35  of the substrate-side heat conducting body  30 , and a high-grade soldered connection  51  between the aluminium nitride ceramic plate  40  and an epitaxy-side heat transfer section  26 , extending against the direction of light emission  15  beyond the laser diode bar  10 , of the epitaxy-side heat conducting body  20 , and a high-quality soldered connection  50  between the aluminium nitride ceramic plate  40  and a substrate-side heat transfer section  36 , extending against the direction of light emission  15  beyond the laser diode bar  10 , of the substrate-side heat conducting body  30 . 
     The soldered connection  50  has a greater thickness than the other three soldered connections  13 ,  14  and  51 . It bridges the certain tolerance of the distance to the substrate-side heat conducting body of the aluminium nitride ceramic plate  40  produced with too small thickness. 
     The spacer  60  prevents the components from tipping towards one another into the solder layer  50  and ensures that the thicknesses of the joining zones  13  and  14  are likewise substantially constant like the thicknesses of the joining zones  50  and  51 . 
     It can be assumed in a simplified description of the joining process that the solder layer thicknesses of all solder layers in the joining process, with the exception of that of the solder preform, do not change, while the thickness of the solder layer of the solder preform adapts to the distances determined by the laser diode bar  10  together with its solder layers (130 μm in total) and the spacer  60  (125 μm). Thus the thickness of the solder of the solder preform decreases by 20% to 40% to 15 to 20 μm. The joining process involves the emergence from the solder layers of joining zones the thickness of which, with the exception of that of the first soldered connection  50 , corresponds to that of the solder layers. The thickness of the joining zone  50  between the aluminium nitride ceramic plate  40  and the substrate-side heat transfer section  36  of the substrate-side heat conducting body  30  varies tapering from 25 μm on the side facing the laser diode bar 10 to 20 μm on the side facing the support element. Overall, the joining gap between the epitaxy-side heat transfer section  26  and the substrate-side heat transfer section  36  also runs tapered because its thickness, which corresponds to the distance between the two heat transfer sections  26  and  36 , is determined by the spacers between the heat entry sections  25  and  35  (laser diode bar  10  with soldered connections  13  and  14 ) and between the support sections  27  and  37  (spacer  60 ). At the end facing the laser diode bar  10 , it is 130 μm thick, at the end facing the spacer  60  125 μm thick. 
     To operate the laser diode bar in the heat transfer device, a heat sink is secured to a heat emitting surface which is arranged on a side  29  facing away from the laser diode bar  10  and the aluminium nitride ceramic plate  40  of the epitaxy-side heat conducting body  20 ; a first electrical connection is attached to the epitaxy-side heat conducting body  20  and a second electrical connection to the substrate-side heat conducting body  30 . The spacer shorting the epitaxy-side and substrate-side contact of the laser diode bar  10  via the heat conducting bodies  20  and  30  is moved out of its position. 
     During operation of the laser diode bar, a first part of the heat produced in the active zone is absorbed by the epitaxy-side heat absorbing section  25  of the epitaxy-side heat conducting body  20  via the epitaxy-side contact surface  11 , the epitaxy-side soldered connection  13  and the epitaxy-side heat entry surface  21  and spread at least partly into the epitaxy-side heat transfer section  26 . A second part of the heat is absorbed by the substrate-side heat absorbing section  35  of the substrate-side heat conducting body  30  via the substrate-side contact surface  12 , the substrate-side soldered connection  14  and the substrate-side heat entry surface  31  and at least almost all of it conducted into the substrate-side heat transfer section  36 . From the substrate-side heat transfer section  36 , the second heat part is transferred via the substrate-side heat transfer surface  32 , the soldered connection  50 , the substrate-side heat transfer surface  42 , the aluminium nitride ceramic plate  40 , the epitaxy-side heat transfer surface  41 , the soldered connection  51  and the epitaxy-side heat transfer surface  22  into the epitaxy-side heat transfer section  26  of the epitaxy-side heat conducting body  20  where it is combined with the first heat part. The heat is then discharged via the heat emitting surface  29  to a heat sink body for heat removal. 
     The aluminium nitride ceramic plate  40  ensures an electrical insulation between the heat conducting bodies  20  and  30  between which there must be a suitable potential difference for the operation of the laser diode bar. As the thickness of the aluminium nitride ceramic plate  40  is only slightly less than that of the laser diode bar, the thicknesses of the soldered connections  50  and  51  are also relatively small, namely 25 μm and 5 μm. Despite the moderate heat conductivity of gold-tin solder, when account is taken of the high thermal conductivity of the aluminium nitride ceramic plate  40 , the thermal resistance of the heat transfer from substrate-side heat transfer section  36  to the epitaxy-side heat transfer section  26  therefore remains small. 
     Thus the substrate-side heat conducting body can in fact be used efficiently for the cooling of the laser diode bar on both sides. 
     Embodiment Example 2 
     Unlike the first embodiment example, the second embodiment example manages without using a plate  40  introduced between the heat conducting bodies for electrical insulation. Instead, a joining zone with an electrical insulating joining agent is used for the electrically insulating connection of the heat conducting bodies. For this, at least one of the heat conducting bodies  20 ,  30  —in the present embodiment example both heat conducting bodies  20  and  20  —is provided with a raised section in the region of the heat transfer section  26 ,  36 , which extends in the adhesion-bonded heat transfer device to the back alignment of the laser diode bar  10 , i.e. between the two contact surface planes. Thus the heat entry surfaces  21 ,  31  of the heat absorbing sections  25 ,  35  each lie together with the support surfaces  23 ,  33  of the support sections  27 ,  37  in a common plane which for its part lies offset parallel vis-à-vis the planes of the heat transfer surfaces  22 ,  32  in the heat transfer sections  26 ,  36 . 
     Unlike the first embodiment example, the second embodiment example manages with only a minimum of components. 
     The components of the second embodiment example are shown in  FIG. 2   a . The heat conducting bodies  20  and  30  consist predominantly of copper. The heat entry surfaces  21  and  31  at the base of recesses in the heat absorbing sections  25  and  35  are offset parallel by 50 μm, in the direction pointing away from the laser diode bar, vis-à-vis the heat transfer surfaces  22  and  32  in the heat transfer sections  26  and  36 . The pair of recesses provides space, as illustrated in  FIG. 2   b , to house the laser diode bar  10 , which is soldered by adhesion on both sides to the heat absorbing sections  25  and  35  of the heat conducting bodies  20  and  30  with indium solder  13  and  14  in a single soldering process. 
     Likewise, the support surfaces  23  and  33  at the base of recesses in the support sections  27  and  37  are offset parallel by 50 μm, in the direction pointing away from the laser diode bar, vis-á-vis the heat transfer surfaces  22  and  32  in the heat transfer sections  26  and  36 . This pair of recesses provides space, as illustrated in  FIG. 2   b , to house a polyimide foil  40  125 μm thick which is secured by means of an adhesive to the support surface  23 ,  33  of one of the heat conducting bodies  20 ,  30  before carrying out the abovenamed soldering process. 
     Together with the mentioned soldering process, an electrically insulating adhesive layer  50  previously introduced between the two heat transfer sections  26  and  36  of the heat conducting bodies  20  and  30  hardens in material closure manner. When initiating the soldering process, the polyimide foil as spacer ensures, when a compressive force is exerted by the substrate-side heat conducting body  20  on the epitaxy-side heat conducting body  30 , that a thickness of the electrically insulating adhesive layer  50  in the region of 25 to 30 μm forms which reliably ensures the electrical insulation of the metallic heat conducting bodies from one another. At the same time, an indium solder layer of sufficient thickness homogeneity is ensured. 
     The polyimide film remains in the heat transfer device after assembly has ended. 
     List of Reference Numbers 
     
         
           10  laser diode element 
           11  epitaxy-side contact surface 
           12  substrate-side contact surface 
           13  epitaxy-side soldered connection 
           14  substrate-side soldered connection 
           15  arrow showing direction of radiation emission 
           20  epitaxy-side heat conducting body 
           21  epitaxy-side heat entry surface 
           22  epitaxy-side heat transfer surface 
           23  epitaxy-side support surface 
           25  epitaxy-side heat absorbing section 
           26  epitaxy-side heat transfer section 
           27  epitaxy-side support section 
           29  heat emitting surface 
           30  substrate-side heat conducting body 
           31  substrate-side heat entry surface 
           32  substrate-side heat transfer surface 
           33  substrate-side support surface 
           35  substrate-side heat absorbing section 
           36  substrate-side heat transfer section 
           37  substrate-side support section 
           40  electrically insulating plate 
           41  epitaxy-side transfer surface 
           42  substrate-side transfer surface 
           50  first joining zone between heat transfer sections 
           51  second joining zone between heat transfer sections 
           60  spacer 
       
    
     While the invention has been described in connection with what is presently considered to be the most practical and preferred embodiments, it will be apparent to those of ordinary skill in the art that the invention is not to be limited to the disclosed embodiments. It will be readily apparent to those of ordinary skill in the art that many modifications and equivalent arrangements can be made thereof without departing from the spirit and scope of the present disclosure, such scope to be accorded the broadest interpretation of the appended claims so as to encompass all equivalent structures and products. 
     The above disclosure is related to the detailed technical contents and inventive features thereof. People skilled in this field may proceed with a variety of modifications and replacements based on the disclosures and suggestions of the invention as described without departing from the characteristics thereof. Nevertheless, although such modifications and replacements are not fully disclosed in the above descriptions, they have substantially been covered in the following claims as appended.