Abstract:
The system contains a substrate having at least one electrical trace formed thereon. An opening is formed in the substrate. The opening comprising at least one wall. An electrically conductive fill is formed in the opening. The electrically conductive fill is chemically bonded to the wall and electrically contacted with the electrical trace.

Description:
CROSS REFERENCE TO RELATED APPLICATION 
       [0001]    This application claims benefit of U.S. Provisional Application Ser. No. 61/172,935 filed Apr. 27, 2009, the entire disclosure of which is incorporated herein by reference. 
     
    
     FIELD 
       [0002]    The present disclosure is generally related to filled vias and more particularly is related to a method and apparatus for an improved filled via. 
       BACKGROUND 
       [0003]    Filled vias are utilized in circuit manufacturing. As an example, a circuit may be formed on each side of a substantially flat substrate. To electrically connect elements on opposing sides of the substrate, a hole or via may be formed in the substrate, which is filled with a conductive material or fill. The electrical elements then utilize the conductive material to form an electrical path through the substrate. The hole filled with conductive material is an example of a filled via. 
         [0004]    One common method of forming a filled via is to insert a paste made substantially with metal and glass. The paste is heated to a high temperature and, as it cools within the via, it forms a mechanical connection with the walls of the via. Up to approximately 80-85% of the paste may be metal and at least 10% of the paste may be glass. The glass is important because without the glass, or a comparable substance, the metal would be unable to form an adequate mechanical connection with the walls of the via. Also, other conductive metals beyond gold may be utilized in the paste, but gold is recognized as having more favorable properties as compared with other available metals. Tungsten and Copper Tungsten are examples of other compatible metals, for this process, although each still requires a significant percentage of glass or comparable substance. 
         [0005]      FIG. 1  is an illustration of a cross-sectional view of a metal-glass paste composite filled via  10  as is known in a first exemplary embodiment of the prior art. A substrate  12  is shown with a hole formed therein, bordered by a wall  14 . Within the wall  14 , a first paste  16  is utilized to fill the hole, heated and cooled as previously described. The first paste  16  is usually applied and fired at atmosphere. Due to differences in the coefficient of thermal expansion of the first paste  16  and the substrate  12 , gaps or crevices may develop between the wall  14  and the first paste  16  as it cools. A second paste  18  is thereafter applied and fired in a second process of heating and cooling. And a third paste  20  is thereafter applied and fired in a third process of heating and cooling. Each of the firing processes may take place in atmosphere or in special environments. The second and third pastes  18 ,  20  are applied to seal the first paste  16  and prevent foreign substances from entering any gaps in the first paste  16 . However, gaps or voids in any of the layers may cause blisters in the pastes  16 ,  18 ,  20  during subsequent processing. Since these circuits may be used in high-performance military or commercial applications, blisters compromise the integrity of the filled via  10 , increase cost and decrease reliability. 
         [0006]    While described as ‘pastes’, it should be noted that, after cooling, each of the pastes has the approximate rigidity of metal. Also, as glass is not a good conductor of heat or electricity, a metal and glass paste is not as good a conductor of heat or electricity as a pure metal system would be. 
         [0007]      FIG. 2  is an illustration of a cross-sectional view of an electroplate filled via  10 A as is known in a second exemplary embodiment of the prior art. A substrate  12 A is shown with a hole formed therein, bordered by a wall  14 A. A conductive film  16 A is applied to one side of the substrate. The substrate is then electroplated with a material  18 A and the via is filled to form metal “pillars”  20 A in the via. These vias are not well bonded to the substrate  12 A and suffer blistering and reliability issues similar to the metal and glass composite filled vias. 
         [0008]    A via filling process that requires fewer process steps, provides a hermetic bond to the substrate, and/or allows for greater thermal and electrical conductivity would be desirable. 
       SUMMARY 
       [0009]    Embodiments of the present disclosure provide a system and method for filling a via. Briefly described, in architecture, one embodiment of the system, among others, can be implemented as follows. The system includes a substrate. At least one opening is formed in the substrate. The opening includes at least one wall. A metallic adhesion layer is formed in the opening and chemically bonded to the wall. A braze fill material is deposited in the opening and chemically bonded to the metallic adhesion layer. 
         [0010]    The present disclosure can also be viewed as providing methods for filling a via. In this regard, one embodiment of such a method, among others, can be broadly summarized by the following steps: forming an opening in a substrate, wherein the opening comprises at least one wall; chemically bonding a metallic adhesion layer to the wall; and chemically bonding a braze fill material to the metallic adhesion layer to fill the opening. 
         [0011]    Other systems, methods, features, and advantages of the present disclosure will be or become apparent to one with skill in the art upon examination of the following drawings and detailed description. It is intended that all such additional systems, methods, features, and advantages be included within this description, be within the scope of the present disclosure, and be protected by the accompanying claims. 
     
    
     
       BRIEF DESCRIPTION OF THE DRAWINGS 
         [0012]    Many aspects of the invention can be better understood with reference to the following drawings. The components in the drawings are not necessarily to scale. Instead emphasis is being placed upon illustrating clearly the principles of the present disclosure. Moreover, in the drawings, like reference numerals designate corresponding parts throughout the several views. 
           [0013]      FIG. 1  is an illustration of a cross-sectional view of a metal-glass composite filled via as is known in a first exemplary embodiment of the prior art. 
           [0014]      FIG. 2  is an illustration of a cross-sectional view of an electroplated filled via as is known in a second exemplary embodiment of the prior art. 
           [0015]      FIG. 3  is an illustration of a cross-sectional view of a via, in accordance with the first exemplary embodiment of the present disclosure. 
           [0016]      FIG. 4  is an illustration of a cross-sectional view of the via of  FIG. 3  metalized with a metallic adhesion layer, in accordance with the first exemplary embodiment of the present disclosure. 
           [0017]      FIG. 5  is an illustration of a cross-sectional view of the via of  FIG. 4  filled with a braze fill material, in accordance with the first exemplary embodiment of the present disclosure. 
           [0018]      FIG. 6  is an illustration of a cross-sectional view of the via of  FIG. 5  with an electrical trace applied, in accordance with the first exemplary embodiment of the present disclosure. 
           [0019]      FIG. 7  is an illustration of a flowchart illustrating a method of filling the via to form the filled via of  FIG. 4 , in accordance with the first exemplary embodiment of the present disclosure. 
       
    
    
     DETAILED DESCRIPTION 
       [0020]      FIG. 3  is an illustration of a cross-sectional view of a via  110 , in accordance with the first exemplary embodiment of the present disclosure. An opening  116  is formed in the substrate  112 . The substrate  112  may be made of a ceramic or glass, or any other material known in the art for forming a substrate. The opening  116  includes at least one wall  118 . The opening  116  in the substrate  112  may be, for example, prefabricated, drilled, or ablated with a laser. The opening  116  need not extend entirely through the substrate  112 , but may be a cavity or, what his referred to in the art as, a blind via. Drilling, in some circumstances, may be performed with a diamond-tipped drill or with water-jet machining to minimize damage to the substrate  112 . Utilizing a laser may result in a tapered opening  116 , as shown in  FIG. 3 , as well as a laser slag or laser residue  126  formed along the wall(s)  118  of the opening  116 . Also, while the opening  116  is shown to be tapered, such a shape of the opening  116  is not required for practicing the presently disclosed technology, but is a shape not uncommon to substrate openings. 
         [0021]      FIG. 4  is an illustration of a cross-sectional view of the via  110  of  FIG. 3  metalized with a metallic adhesion layer  120 , in accordance with the first exemplary embodiment of the present disclosure. The metallic adhesion layer  120  is formed in the opening  116  against the wall  118 . The metallic adhesion layer  120  is chemically bonded to the wall  118 . The metallic adhesion layer  120  may be titanium, tungsten-titanium, molybdenum and/or nickel, as examples. These, and other metallic adhesion layers, may be provided to allow for an improved chemical bond between the braze fill material  122  (not shown) and the substrate  112 . 
         [0022]      FIG. 5  is an illustration of a cross-sectional view of the via  110  of  FIG. 4  filled with a braze fill material  122 , in accordance with the first exemplary embodiment of the present disclosure. The braze fill material  122  is deposited in each via against the metallic adhesion layer  120  and heated to an approximate melting temperature of the braze fill material  120 , then allowed to cool. The braze fill material  120  may be heated up to approximately 1000 degrees Celsius to melt the braze fill material  120 . The entirety of the braze fill material  122  may be applied in a single step. The melting of the braze fill material  122  may be completed within a vacuum chamber, inert gas atmosphere furnace, or other controlled atmosphere container to limit oxidation of at least of the braze fill material  122 , the metallic adhesion layer, and/or any elements thereof. The braze fill material  122  may be made flush with the substrate  112  on both sides of the substrate  112 . The braze fill material  122  may need to be scraped to bring it flush with the substrate  112 . 
         [0023]    The braze fill material  122  may be a single metal, such as gold, or it may be an alloy such as TiCuSiI. The metallic adhesion layer  120  is used to cover the laser residue  126 . Once the metallic adhesion layer  120  is applied, the braze fill material  122  may be applied. The braze fill material  122  may be heated to an approximate melting point of the braze fill material  122  and completing the bonding to the metallic adhesion layer  120 . 
         [0024]      FIG. 6  is an illustration of a cross-sectional view of the via  110  of  FIG. 5  with an electrical trace  114  applied, in accordance with the first exemplary embodiment of the present disclosure. The electrical trace  114  may be used to transmit a current that travels from one side of the substrate  112  to the other side of the substrate  112 . The electrical trace  114  may be laid down in electrical contact with the previously applied braze fill material  122 . In practice, the substrate with the filled via may be purchased by a customer and the electrical trace  114  may be applied by the customer. 
         [0025]      FIG. 7  is an illustration of a flowchart  300  illustrating a method of filling the via  110  to form the filled via  110  of  FIG. 4 , in accordance with the first exemplary embodiment of the present disclosure. It should be noted that any process descriptions or blocks in flow charts should be understood as representing modules, segments, portions of code, or steps that include one or more instructions for implementing specific logical functions in the process, and alternate implementations are included within the scope of the present disclosure in which functions may be executed out of order from that shown or discussed, including substantially concurrently or in reverse order, depending on the functionality involved, as would be understood by those reasonably skilled in the art of the present disclosure. 
         [0026]    As is shown by block  302 , an opening  116  is formed in a substrate  112 , wherein the opening  116  includes at least one wall  118 . A metallic adhesion layer  120  is chemically bonded to the wall  118  (block  304 ). The braze fill material  122  is chemically bonded to the metallic adhesion layer  120  (block  306 ). 
         [0027]    The metallic adhesion layer  120  and the braze fill material  122  may be chemically bonded by heating the materials to their melting points before applying them to the wall  118  of the substrate  112 . The braze fill material  122  will not chemically bond directly to the wall  118  without application of the metallic adhesion layer  120  as an intermediary. The belief is that the materials that have been utilized for the braze fill material  122  cannot bond to a rough surface, such as a surface that contains laser residue  126 . While it is called laser residue  126 , drilling and water-jet machining can leave a similar uneven surface. The metallic adhesion layer  120  may be applied by sputtering. Either chemical bonding step may be performed in a controlled atmosphere chamber, which may be useful at least for the purpose of diminishing and/or avoiding oxidation of the metallic adhesion layer  120  or the braze fill material  122 , if either material is susceptible to oxidation. The braze fill material  122  may be primarily a single metal, at least 90% by weight. The braze fill material  122  may be primarily gold, at least 90% by weight. The braze fill material  122  may be approximately 100% gold. 
         [0028]    It should be emphasized that the above-described embodiments of the present disclosure, particularly, any “preferred” embodiments, are merely possible examples of implementations, merely set forth for a clear understanding of the principles of the disclosed system and method. Many variations and modifications may be made to the above-described embodiments of the disclosure without departing substantially from the spirit and principles of the disclosure. All such modifications and variations are intended to be included herein within the scope of this disclosure and protected by the following claims.