Abstract:
The present invention relates to rigid and clear thermosetting compositions formed from dendritic or hyperbranched polymers and cylcoaliphatic epoxy resins. The compositions may be used for coatings such as electronic device packaging, adhesives, wire coatings, and finishes.

Description:
CROSS-REFERENCE TO RELATED APPLICATION 
     This application is a Divisional of U.S. patent application Ser. No. 11/121,206, entitled “HYPERBRANCHED POLYMER AND CYCLOALIPHATIC EPOXY RESIN THERMOSETS,” filed on May 3, 2005, abandoned, the entire disclosure of which is incorporated herein by reference. 
    
    
     FIELD OF THE INVENTION 
     The present invention relates to rigid and clear thermosetting compositions formed from dendritic or hyperbranched polymers and cylcoaliphatic epoxy resins. The compositions may be used for coatings such as electronic device packaging, adhesives, wire coatings, and finishes. 
     BACKGROUND OF THE INVENTION 
     Known commercial thermoset resins from dendritic polymers such as acrylate and urethane thermosets have excellent processing and reactivity characteristics when compared to their linear polymer analogs due to their globular structure and high density of reactive functionalities. However, such thermoset materials may not be suitable for a wide range of electrical and electronic applications due to low thermal stability and moderate electrical properties. On the other hand, epoxy functionalized dendrimers have received little commercial success due to rheological issues associated with their extreme viscosities. 
     Dendritic polymers are a relatively new class of macromolecules with a hyperbranched structure formed from the incorporation of repetitive branching sequences by a multiplicative growth process beginning with a small molecule. As such, dendrimers typically consist of a core, from which branches extend in three-dimensions, forming a globular structure with a large number of end groups at the peripheral surface. Consequently, dendrimers differ significantly from conventional linear polymers in their physical properties. Their compact globular structure coupled with the absence of restrictive interchain entanglements results in low viscosities that are substantially lower than their linear polymer analogues of similar molecular weights as disclosed in “Properties and Applications of Dendritic Polymers”, B. Pettersson, Pyramid Communication AB, Sweden, 2001, and by R. Mezzenga, L. Boogh, and J. E. Manson, Composite Science and Technology, 61, 787, 2001, the disclosure of each expressly incorporated by reference herein. Furthermore, the variability in the chemical compositions of the core molecule, the chain extender, and the high density terminal groups allow for solubilities in a large variety of solvents. 
     To date, only a few dendritic polymers have been successfully commercialized. Among the commercial hyperbranched polymers are those that are based on polyalcohol and an aliphatic tertiary polyester backbone such as the structure shown in  FIG. 1 . They are sold under the trade name Boltorn™ by the Perstrop Specialty Chemicals (Boltorn is a trademark of Perstrop Specialty Chemicals). Most of the commercial applications of this family of dendritic polymers rely on the exceptionally high concentration of reactive hydroxyl groups that provide for a rapid curing in thermosetting applications. The most prominent applications are in the coating and in the polyurethane industries as discussed by D. James in the article “Parquet Coating II,” at the European Coating Conference, 14 Nov. 2002, the disclosure of which is expressly incorporated by reference herein. Currently, different Boltorn™ product grades are used by the radiation curable coating, the powder coating, the decorative coating, and the polyurethane industries in both automotive and non-automotive applications as discussed by D. James in PRA Radcure Coatings and Inks, 24 Jun. 2002, the disclosure of which is expressly incorporated by reference herein. 
     Although the application of dendritic polymers in epoxy resin compositions has been reported by L. Boogh, B. Pettersson, and J. E. Manson in Polymer, 40, 2249, 1999, the disclosure of which is expressly incorporated by reference herein, their utility in these instances is limited to their phase separation-induced toughening effect in the Bisphenol-A family type of epoxy resins that are cured by non-cationic initiation. Functionalization of the dendritic polymer with epoxy groups has also been reported and some commercial grades are available. 
     SUMMARY OF THE INVENTION 
     One embodiment of the present invention includes a coating comprising a dendritic polyol, a cycloaliphatic epoxy resin, and a cationic initiator. The coating may include a cycloaliphatic epoxy resin selected from the group consisting essentially of 3,4-epoxycyclohexyl methyl-3,4-epoxy-cyclohexane carboxylate, bis(3,4-epoxycyclohexyl) adipate, and 2-(3,4-epoxycyclohexyl-5,5-spiro-3,4-epoxy) cyclohexane-meta-dioxane, a dendritic polyol selected from the group consisting essentially of Boltorn H20, Boltorn H30, Boltorn H40, Boltorn H2003, and Boltorn H2004, and/or an initiator selected from the group consisting essentially of FC520, Cp66, Nacure XC 7231, and Nacure super A218. 
     Another embodiment of the present invention includes a process of coating metal with an electrical insulator, the process including the steps of providing a mixture of a dendritic polyol, a cycloaliphatic epoxy resin, and a cationic initiator, coating the metal with the mixture, and heating the mixture. The electrical insulator may include a cycloaliphatic epoxy resin selected from the group consisting essentially of 3,4-epoxycyclohexyl methyl-3,4-epoxy-cyclohexane carbonate, bis(3,4-epoxycyclohexyl) adipate, and 2-(3,4-epoxycyclohexyl-5,5-spiro-3,4-epoxy) cyclohexane-meta-dioxane, a dendritic polyol selected from the group consisting essentially of Boltorn H20, Boltorn H30, Boltorn H40, Boltorn H2003, and Boltorn H2004, and/or an initiator selected from the group consisting essentially of FC520, Cp66, Nacure XC 7231, and Nacure super A218. 
     Another embodiment of the present invention includes a composition of matter comprising a dendritic polyol, a cycloaliphatic epoxy resin, and a cationic initiator. The composition of matter may include a dendritic polyol comprising about 5-30% by weight of the composition. The composition of matter may also include a dendritic polyol comprising about 10-20% by weight of the composition. The composition of matter may also include a cationic initiator comprising about 0.1-3.0% by weight of the composition. 
    
    
     
       BRIEF DESCRIPTION OF THE DRAWINGS 
       The above-mentioned and other features and objects of this invention, and the manner of attaining them, will become more apparent and the invention itself will be better understood by reference to the following description of embodiments of the invention taken in conjunction with the accompanying drawings, wherein: 
         FIG. 1  is a structural diagram a hyperbranched or dendritic polyol such as Boltorn™. 
     
    
    
     Corresponding reference characters indicate corresponding parts throughout the several views. Although the drawings represent embodiments of the present invention, the drawings are not necessarily to scale and certain features may be exaggerated in order to better illustrate and explain the present invention. The exemplifications set out herein illustrate embodiments of the invention in several forms and such exemplification is not to be construed as limiting the scope of the invention in any manner. 
     DETAILED DESCRIPTION OF THE INVENTION 
     The embodiments discussed below are not intended to be exhaustive or limit the invention to the precise forms disclosed in the following detailed description. Rather, the embodiments are chosen and described so that others skilled in the art may utilize their teachings. 
     The present invention includes the a series of thermoset compositions formed from the combination of cycloaliphatic epoxy resins and dendritic polyols and the method or making such compositions. The resulting thermoset compositions have the superior processing and high reactivity characteristics of the multifunctional globular structure of the dendritic polyols and the excellent thermal degradation resistance and electrical properties known for cycloaliphatic/polyol based compositions. As discussed below, the combination of hyperbranched or dendritic polyols with a variety of cycloaliphatic epoxy resins shows excellent reactivities at temperatures as low as 80° C. and high thermal degradation temperatures, greater than 400° C., when catalyzed by certain initiators. Also, cycloaliphatic/polyol based compositions are known to have good outdoor weathering, superior arc-track resistance, good dielectric properties, and low ionic contents. The thermoset compositions of the present invention are moderately tough, clear systems and can be used in the encapsulation of electronics where transparency or “see-through” is important. 
     The thermoset compositions of the present invention are made by dissolving polyalcohol based dendrimers, such as the Boltorn™ family, in cycloaliphatic epoxy resins by heating at a temperature in the range of 80° C.-120° C. The resulting mixture remains after cooling to room temperature. Next, a specific amount of a cationic initiator is added at a specified temperature to cure the mixture. Examples of the this method are described below. The resulting thermoset compositions have excellent rigid and transparent characteristics. Another feature of the present invention is the pot life of the mixture including a polyalcohol based dendrimer, a cycloaliphatic epoxy resin, and a cationic initiator. This one-package mixture may be stored at room temperature for several months. The mixture may then be used, for example as a coating. Heat is applied to the mixture to activate the cationic initiator may cure the mixture leaving the thermoset coating. 
     EXAMPLES 
     The structure and properties of the dendritic polyols, the cycloaliphatic epoxy resins, and the cationic initiators used in the formulations of the following examples of the present invention are given in Tables I, II, and III. Table I illustrates the structure of the cycloaliphatic epoxy resins used in these examples. In the examples described below, three different cycloaliphatic epoxy resins, 3,4-epoxycyclohexyl methyl-3,4-epoxycyclohexane carboxylate, bis(3,4-epoxycyclohexyl) adipate, and 2-(3,4-epoxycyclohexyl-5,5-Spiro-3,4-epoxy) cyclohexane-meta-dioxane, all produced by Dow Chemical, are used. Table II lists the cationic initiators used in these examples along with their approximate structures and their respective manufacturers. The cationic initiators used in the examples described below include FC520, Cp66, Nacure XC 7231, and Nacure super A218. Table III lists characteristics of several different generations of dendrimers of Boltorn™ polyols used in these examples. The dendrimers include Boltorn™ H20, H30, H40, H2003, and H2004. 
     
       
         
               
             
               
               
               
               
             
           
               
                 TABLE I 
               
             
             
               
                   
               
               
                 Structure of Cycloaliphatic Epoxy Resins (Dow Chemical Co.) used in the 
               
               
                 Formulations 
               
             
          
           
               
                   
                   
                   
                 EEW 
               
               
                 Code 
                 Name 
                 Structure 
                 * 
               
               
                   
               
               
                 ERL4221 
                 3,4-epoxycyclohexyl methyl-3,4- epoxy-cyclohexane carboxylate 
                 
                   
                             
                     
                         
                         
                     
                   
                 
                 136 
               
               
                   
               
               
                 ERL4299 
                 Bis(3,4-epoxycyclohexyl) adipate 
                 
                   
                             
                     
                         
                         
                     
                   
                 
                 200 
               
               
                   
               
               
                 ERL4234 
                 2-(3,4-epoxycyclohexyl-5,5- Spiro-3,4-epoxy) cyclohexane- meta-dioxane 
                 
                   
                             
                     
                         
                         
                     
                   
                 
                 144 
               
               
                   
               
               
                 *EEW: Epoxy Equivalent Weight 
               
             
          
         
       
     
     
       
         
               
             
               
               
               
             
           
               
                 TABLE II 
               
             
             
               
                   
               
               
                 Cationic Initiators and Approximate Structures 
               
             
          
           
               
                 Cationic Initiator 
                 Structure 
                 Manufacturer 
               
               
                   
               
               
                 FC520 
                 Diethyl ammonium triflate 
                 3M 
               
               
                 Cp66 
                 S-butenethiophene 
                 Asahi Denka 
               
               
                   
                 hexafluoroantimonate 
               
               
                 Nacure XC 7231 
                 Ammonium hexafluoroantimonate 
                 King Industries 
               
               
                 Nacure super A218 
                 Lewis acid (zinc salt) 
                 King Industries 
               
               
                   
               
             
          
         
       
     
     
       
         
               
             
               
               
               
               
               
               
             
               
               
               
               
               
               
             
           
               
                 TABLE III 
               
             
             
               
                   
               
               
                 Characteristics of Different Generation Dendrimers of Boltorn ™ Polyols 
               
             
          
           
               
                 Product 
                 H20 
                 H30 
                 H40 
                 H2003 
                 H2004 
               
               
                   
               
             
          
           
               
                 Hydroxyl number 
                 505 
                 495 
                 485 
                 298 
                 125 
               
               
                 Mw (g/mole) 
                 1750 
                 3570 
                 7250 
                 2500 
                 3200 
               
               
                 Functionality 
                 16 
                 32 
                 64 
                 12 
                 6 
               
               
                 Viscosity at 110° C. 
                 7 
                 40 
                 110 
                 1 
                 20 
               
               
                 (×10 −3 ) 
               
               
                   
               
             
          
         
       
     
     In the following examples, the formulations of the dendrimer/epoxy mixture were prepared by dissolving an appropriate amount of the dendritic polyol in the cycloaliphatic epoxy resin at about 100° C. The dendritic polymers remained in solution for months after cooling to room temperature. The amount of dissolved dendrimers in the epoxy resin is limited by solubility and by viscosity requirements. Concentrations are in the range of 5-30% by weight of the dendrimer polyol and further concentrations are in the range of 10-20% by weight. As discussed below, non-dendritic polyols may be added to the mixture to reduce the viscosity or to impart desirable characteristics of the non-dendritic polyols to the cured thermoset. 
     Curing of the dendrimer/epoxy solutions was achieved by the addition of one of the cationic initiators listed in Table II. After one of the initiators is added to the dendrimer/epoxy solution, the formulation was heated to a required temperature for an appropriate time period. The preferred amount of cationic initiator is between 0.1-3.0% by weight of the total composition. The optimum amount varies with the type of initiator. Some initiators, such as FC520 and Nacure XC7231, cause coloration of the cured formulations when used at relatively high concentrations (3% by weight). Excessive cure exotherms and lower degradation temperatures of the cured products are other concerns for formulations involving high initiator concentrations. 
     Table IV (shown below) illustrates the influence of the concentration of the cationic initiator, Nacure A218 in this example, on the cure temperature (T max  ° C.) for three different mixtures of dendrimer/epoxy solution. The cure temperature of each formulation depends on the specific initiator and its concentration. For the examples shown in Table IV, each of the three formulations includes about 15% dendrimer and about 85% cycloaliphatic epoxy resin. The three formulations tested are mixtures of Boltorn H20 and ERL4234, Boltorn H40 and ERL4234, and Boltorn H20 and ERL4221, respectively. The cationic initiator used was Nacure A218. For each of the three formulations of dendrimer and cycloaliphatic epoxy resin, three different concentrations of Nacure A218 were added. The cure temperature was determined from the peak maxima of differential scanning calorimetry (DSC) measurements. The three concentrations of Nacure A218 used for the Boltorn H20/ERL4234 and Boltorn H40/ERL4234 formulations were 0.25, 0.5, and 1.0 percent by weight of the mixture. Concentrations of 0.5, 1.0, and 3.0 percent by weight of the mixture were added to the Boltorn H20/ERL4221 formulations. As shown in Table IV, the formulations having the lower concentrations of initiator required a higher cure temperature. 
     
       
         
               
             
               
               
               
               
             
               
               
               
               
             
           
               
                 TABLE IV 
               
             
             
               
                   
               
               
                 The Influence of Initiator (Nacure A218) Concentration on T max   
               
             
          
           
               
                   
                   
                 Concentration 
                   
               
               
                   
                   
                 of Initiator 
               
               
                   
                 Dendrimer/Epoxy (15/85% w/w) 
                 (% wt) 
                 T max , ° C. 
               
               
                   
                   
               
             
          
           
               
                   
                 Boltorn H20/ERL4234 
                 0.25 
                 148 
               
               
                   
                 Boltorn H20/ERL4234 
                 0.5 
                 142 
               
               
                   
                 Boltorn H20/ERL4234 
                 1.0 
                 133 
               
               
                   
                 Boltorn H40/ERL4234 
                 0.25 
                 154 
               
               
                   
                 Boltorn H40/ERL4234 
                 0.5 
                 147 
               
               
                   
                 Boltorn H40/ERL4234 
                 1.0 
                 133 
               
               
                   
                 Boltorn H20/ERL4221 
                 0.5 
                 161 
               
               
                   
                 Boltorn H20/ERL4221 
                 1.0 
                 148 
               
               
                   
                 Boltorn H20/ERL4221 
                 3.0 
                 114 
               
               
                   
                   
               
             
          
         
       
     
     Table V (shown below) illustrates the cure temperatures (T max  ° C.) of a formulation including Boltorn H20 and ERL4221 in a 15:85% weight to weight ratio using four different initiators. The cure temperatures were determined for each of the four initiators for formulations having a concentration of initiator of about 1% and about 3% by weight of the mixture. Tables IV and V illustrate a set of optimum cure temperatures as a function of the initiator and its concentration for representative formulations. The broad range of curing temperatures (T max ) obtained from the different initiators allows for thermoset applications having different process temperature requirements. As should be obvious from the foregoing, a variety of cationic initiators could be used in a variety of concentrations to yield the desired cure temperature and thermoset characteristics. 
     
       
         
               
             
               
               
               
               
             
               
               
               
               
             
           
               
                 TABLE V 
               
             
             
               
                   
               
               
                 Cure Temperatures (T max ) of Boltorn H20/ERL4221 (15:85% w/w) 
               
               
                 Formulations Using Different Initiators 
               
             
          
           
               
                   
                 Initiator 
                 T max  (° C.) at 1% wt** 
                 T max  (° C.) at 3% wt** 
               
               
                   
                   
               
             
          
           
               
                   
                 XC7231 
                 117 
                 98 
               
               
                   
                 A218 
                 148 
                 114 
               
               
                   
                 FC520 
                 180 
                 149 
               
               
                   
                 Cp6 
                 126 
                 — 
               
               
                   
                   
               
               
                   
                 *Cure temperature at maximum of exothermic peak (from DSC) 
               
               
                   
                 **Concentration of initiator 
               
             
          
         
       
     
     Table VI (shown below) compares the cure temperature (T max  ° C.) for formulations having different epoxy resin and cationic initiators. The initiators, Nacure A218 and Nacure XC7213, are about 1% by weight of the dendrimer/epoxy solution. Table VII compares formulations having different dendritic polyols and a single epoxy resin. In all of the examples listed in Table VII, the cycloaliphatic epoxy resin was ERL4221. The ERL4221 was combined with the dendritic polymers Boltorn H20, H40, H2003, and H2004 to four different dendrimer/epoxy solutions. Each of the dendrimer/epoxy solutions were divided into three groups. Nacure XC7231 at a concentration of about 3% by weight of the solution was added to each of the solutions in the first group. Nacure XC7231 at a concentration of about 1% by weight of the solution was added to each of the solutions in the second group. FC520 at a concentration of about 1% by weight of the solution was added to each of the solutions in the third group. The measurements of Tables VI and VII indicate that the reaction or cure temperature (T max ) depends on the type of epoxy resin but is independent of the dendrimer generation. 
     
       
         
               
             
               
               
               
               
             
           
               
                 TABLE VI 
               
             
             
               
                   
               
               
                 Dependence of T max  on the Type of Cycloaliphatic Epoxy Resin 
               
               
                 for Boltor H20/Epoxy (15:85% w/w) Formulations 
               
             
          
           
               
                   
                 Initiator at 1% 
                   
                   
               
               
                   
                 concentration 
                 Epoxy resin 
                 T max  (° C.) 
               
               
                   
                   
               
               
                   
                 Nacure A218 
                 ERL4299 
                 123 
               
               
                   
                 Nacure A218 
                 ERL4221 
                 148 
               
               
                   
                 Nacure A218 
                 ERL4234 
                 133 
               
               
                   
                 Nacure XC7213 
                 ERL4299 
                 110 
               
               
                   
                 Nacure XC7213 
                 ERL4221 
                 117 
               
               
                   
                 Nacure XC7213 
                 ERL4234 
                 110 
               
               
                   
                   
               
             
          
         
       
     
     
       
         
               
             
               
               
               
               
             
               
               
               
               
             
           
               
                 TABLE VII 
               
             
             
               
                   
               
               
                 T max  as a Function of Boltorn Dendrimer Generation in Formulations with 
               
               
                 ERL4221 
               
             
          
           
               
                 Dendritic 
                   
                 Concentration of 
                   
               
               
                 Polymer 
                 Initiator 
                 Initiator (wt %) 
                 T max  (° C.) 
               
               
                   
               
             
          
           
               
                 Boltorn H20 
                 Nacure XC7231 
                 3 
                 101 
               
               
                 Boltorn H40 
                 Nacure XC7231 
                 3 
                 108 
               
               
                 Boltorn H2003 
                 Nacure XC7231 
                 3 
                 98 
               
               
                 Boltorn H2004 
                 Nacure XC7231 
                 3 
                 102 
               
               
                 Boltorn H20 
                 Nacure XC7231 
                 1 
                 117 
               
               
                 Boltorn H40 
                 Nacure XC7231 
                 1 
                 121 
               
               
                 Boltorn H2003 
                 Nacure XC7231 
                 1 
                 113 
               
               
                 Boltorn H2004 
                 Nacure XC7231 
                 1 
                 117 
               
               
                 Boltorn H20 
                 FC520 
                 1 
                 180 
               
               
                 Boltorn H40 
                 FC520 
                 1 
                 178 
               
               
                 Boltorn H2003 
                 FC520 
                 1 
                 184 
               
               
                 Boltorn H2004 
                 FC520 
                 1 
                 186 
               
               
                   
               
             
          
         
       
     
     Non-dendritic polyols may also be incorporated in the formulations to achieve certain desirable properties for the cured thermoset. For example, flexible polyols may be added to improve the impact resistance or to provide for a flexible thermoset products. The addition of non-dendritic polyols at the ratio of 1:2 (non-dendritic:dendritic polyols by weight) did not significantly change the cure temperature of the compositions. Representative examples are given in Table VIII. 
     
       
         
               
             
               
               
               
               
               
             
           
               
                 TABLE VIII 
               
             
             
               
                   
               
               
                 Comparison of Cure Temperatures in Formulations 
               
               
                 with and without Linear Polyols 
               
             
          
           
               
                 Dendrimer/Epoxy 
                   
                   
                   
                   
               
               
                 (15%/85% by 
                 T c   1   
                 T c1   1   
                 Initiator at 
                 Non-dendritic 
               
               
                 weight) 
                 (° C.) 
                 (° C.) 
                 1% by weight 
                 Polyol 
               
               
                   
               
               
                 Boltorn H20/ 
                 110 
                 117 
                 XC7231 
                 BPAE 2   
               
               
                 ERL4299 
               
               
                 Boltorn H20/ER4221 
                 148 
                 154 
                 A218 
                 BPAE 
               
               
                 Boltorn H20/ 
                 117 
                 124 
                 XC7231 
                 BPAE 
               
               
                 ERL4299 
               
               
                 Boltorn H20/ER4221 
                 117 
                 121 
                 XC7231 
                 PTHF 3   
               
               
                   
               
               
                   1 T c  and T c1  are the cure temperatures for formulations containing dendrimer only and linear polyol, respectively. 
               
               
                   2 BPAE is Bisphenol-A ethoxylate (4 ethoxylate/phenol, Mn = 580); at 2:1 Boltorn/BPAE by weight. 
               
               
                   3 Polytetrahydrofuran (Mn = 250); at 2:1 Boltorn/PTHF by weight. 
               
             
          
         
       
     
     As shown in Table VIII, the addition of BPAE and PTHF to several dendrimer/epoxy solutions did not significantly effect the cure temperature of the solutions when the cationic initiator was added. In addition to BPAE and PTHF, other suitable non-dendritic polyols or mixtures of non-dendritic polyols could be added to a dendrimer/epoxy/cationic initiator solution to produce a thermoset having a variety of desired characteristics. 
     
       
         
               
             
               
               
               
               
             
               
               
               
               
             
           
               
                 TABLE IX 
               
             
             
               
                   
               
               
                 Decomposition Temperature in Air Atmosphere for Representative 
               
               
                 Formulations 
               
             
          
           
               
                   
                   
                 Initiator 
                   
               
               
                   
                   
                 Concentration 
               
               
                 Dendrimer/Epoxy (15/85% w/w) 
                 Initiator 
                 (wt %) 
                 T d   1  (° C.) 
               
               
                   
               
             
          
           
               
                 Boltorn H20/ERL4299 
                 XC7231 
                 1 
                 420 
               
               
                 Boltorn H20/ERL4299 
                 XC7231 
                 3 
                 414 
               
               
                 Boltorn H20/ERL4299 
                 XC7231 
                 0.5 
                 424 
               
               
                 Boltorn H40/ERL4221 
                 XC7231 
                 1 
                 390 
               
               
                 Boltorn H20/ERL4299 
                 Cp66 
                 0.5 
                 418 
               
               
                 Boltorn H20/ERL4299 
                 FC520 
                 0.5 
                 358 
               
               
                 Boltorn H20/ERL4221 
                 FC520 
                 0.5 
                 335 
               
               
                 Boltorn H40/ERL4221 
                 FC520 
                 0.5 
                 323 
               
               
                 Boltorn H2004/ERL4221 
                 FC520 
                 0.5 
                 326 
               
               
                 Boltorn H20/ERL4221 
                 A-218 
                 1 
                 311 
               
               
                 Boltorn H20/ERL4299 
                 A-218 
                 0.5 
                 317 
               
               
                 Boltorn H40/ERL4234 
                 A-218 
                 0.25 
                 315 
               
               
                   
               
               
                   1 T d  is the decomposition temperature in air as measured at 5% weight loss by thermogravimetric analysis. 
               
             
          
         
       
     
     The investigated dendritic polyol/cycloaliphatic epoxy compositions show good thermal stability in air. The decomposition temperatures as measured by thermogravimeteric analysis for some of the examples of the dendrimer/epoxy/initiator mixtures are given in Table IX. Compositions cured with Nacure XC7231 or with Cp66 showed the highest decomposition temperatures, greater than 400° C., in an air atmosphere. The concentration of any of the initiators tested to achieve the highest decomposition temperatures is in the range of 0.25-1% by weight of total composition and a further concentration is in the range of 0.5-0.75% by weight. 
     While this invention has been described as having an exemplary design, the present invention may be further modified within the spirit and scope of this disclosure. This application is therefore intended to cover any variations, uses, or adaptations of the invention using its general principles. Further, this application is intended to cover such departures from the present disclosure as come within known or customary practice in the art to which this invention pertains.