Abstract:
A radiation tolerant solar cell array module which can be efficiently assembled into a larger solar panel to generate power for a spacecraft the module includes at least first and second single-crystal solar cells. The first and second solar cells have front sides and back sides. At least one of the solar cells has a shallow junction N on P structure. A first contact is formed on at least the back side of the first solar cell. A second contact formed on at least the back side of the second solar cell. A conductor is in electrical communication with the first contact and the second contact. A substantially transparent ceria-doped cover overlays at least a portion of each of the solar cells. The cover remains substantially transparent when exposed to an AM 0  space radiation environment. A substantially transparent adhesive is situated between the cover and the solar cell portions. The adhesive remains substantially transparent when exposed to a space radiation environment.

Description:
This application is a continuation of application Ser. No. 09/090,663 filed Jun. 4, 1998, now U.S. Pat. No. 6,156,967. 
    
    
     BACKGROUND OF THE INVENTION 
     1. Field of the Invention 
     The present invention relates to solar cells. In particular, the invention relates to methods and apparatuses for efficient packaging of solar cells for space applications. 
     2. Description of the Related Art 
     Photovoltaic cells, commonly called solar cells, are well-known devices which convert solar energy into electrical energy. Solar cells have long been used to generate electrical power in both terrestrial and space applications. Solar cells offer. several advantages over more conventional power sources. For example, solar cells offer a clean method for generating electricity. Furthermore, solar cells do not have to be replenished with fossil fuels. Instead, solar cells are powered by the virtually limitless energy of the sun. However, the use of solar cells has been limited because solar cells are a relatively expensive method of generating electricity. Nonetheless, the solar cell is an attractive device for generating energy in space, where low-cost conventional power sources are unavailable. 
     Typically, solar cells manufactured for space use have been of fairly small dimensions. Commonly, solar cells have had dimensions of 4 cm×6 cm or less. In space applications, hundreds or thousands of the small solar cells are interconnected together to form large solar arrays. In a typical manufacturing process, a solar cell manufacturer delivers hundreds or thousands of separate, unconnected, solar cells to a solar array assembler. Often, the solar cell manufacturer mounts a coverglass over each cell to protect the cells against space radiation and other environmental conditions. Alternatively, the solar cell manufacturer may ship bare cells to the array assembler. The array assembler then must provide the coverglass. The array assembler also interconnects the individual cells into large, suitably sized panels. 
     The use of individual coverglasses for each cell has several disadvantages. For example, it is expensive and time consuming to mount a separate coverglass on each cell. In addition, the use of small cells incurs several disadvantages. For example, the smaller the cell size, the more cells are required to form an array of a given size. The more cells which must be assembled, the greater the manufacturing costs. In addition, each cell must be tested individually before being assembled into a larger array. Thus, the greater the number of cells required, the greater the number of tests which must be performed. Furthermore, the smaller the cells, the greater the total cell edge length (i.e. the length of all cell sides summed together) for a given array size. Cell edges are typically prone to damage. Thus, the greater the total edge length, the more likely that at least some cells will be damaged during the manufacturing, transport, and assembly of the cells. 
     SUMMARY OF THE INVENTION 
     One preferred embodiment of the present invention is a modular, glass covered solar cell array suitable for use in space. The modular, glass covered solar cell array includes at least physically and electrically interconnected solar cells. At least a portion of both cells are covered by a common, substantially transparent cover. The transparency of the cover will not substantially degrade when exposed to a space radiation environment. In one embodiment, at least one cell is comprised of single-crystal silicon. In another embodiment, at least one cell is comprised of GaAs. In yet another embodiment, at least one cell is comprised of multijunctions. 
     In one embodiment of the present invention, at least one cell has an area of at least 100 cm 2 . In another embodiment, at least-one cell is at least 150 μm thick. In still another preferred embodiment, at least one cell is thinner than 150 μm. 
     In another embodiment of the present invention, the solar array cells are interconnected by at least one conductor mounted on the backs of the cells. In still another embodiment, at least one cell has at least one contact for receiving the conductor. The contact wraps from a first side of the cell to a second side of the cell. In another embodiment, at least one cell has.at least one contact for interconnection to at least one other solar cell array. 
     In one embodiment, the solar cell array includes at least one bypass diode mounted to at least one surface of one of the cells. In another embodiment, the solar cell array includes contacts for connection to at least one externally mounted bypass diode. 
    
    
     BRIEF DESCRIPTION OF THE DRAWINGS 
     These and other aspects, advantages, and novel features of the invention will become apparent upon reading the following detailed description and upon reference to accompanying drawings in which: 
     FIG. 1 a  illustrates one embodiment of a solar cell front side; 
     FIG. 1 b  illustrates one embodiment of a solar cell back side; 
     FIG. 1 c  illustrates one embodiment of a solar cell having wrap around contacts; 
     FIG. 2 illustrates one embodiment of a standard power module; 
     FIG. 3 illustrates components of one embodiment of the standard power module; 
     FIG. 4 illustrates the results of a power density tradeoff analysis; 
     FIG. 5 illustrates the results of a cost versus coverglass quantity tradeoff analysis; 
     FIG. 6 illustrates the results of a cost versus coverglass coating tradeoff analysis; 
     FIG. 7 illustrates the results of a cost versus adhesive mass tradeoff analysis; 
     FIG. 8 illustrates the results of a radiation analysis for one relevant operating environment. 
     FIG. 9 is a graph illustrating mission fluence versus shielding; 
     FIG. 10A illustrates one embodiment of an array of interconnected standard power modules; 
     FIG. 10B is a detailed diagram of a portion of the interconnected standard power modules of FIG.  10 A. 
     FIG. 11 illustrates one embodiment of a solar cell manufacturing process; and 
     FIGS. 12A, B illustrate one embodiment of a standard power module manufacturing flow. 
    
    
     DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS 
     As illustrated in FIGS. 2 and 3, in one preferred embodiment a baseline modular, glass covered solar array  200 , which is interchangeably called a standard power module (SPM), consists of a solar cell circuit matrix that can be readily used to build up a variety of array sizes. In a preferred embodiment, the SPM configuration consists of: 
     A large area (˜20 cm×30 cm) ceria doped borosilicate coverglass microsheet  202 , nominally 100 μm thick, which provides radiation resistant shielding for charged and uncharged particles. One skilled in the art will understand that other suitable coverglass materials and dimensions can be used as well. 
     Six large area (10 cm×10 cm) silicon solar cells  100 , are approximately 200 μm thick. A preferred embodiment of a solar cell is illustrated in greater detail in FIGS. 1 a - 1   c.  The solar cells each have at least one space qualified N/P wraparound contact  102 , although other configurations may be used as well. In a preferred embodiment, each solar cell has two contacts  102 ,  104 , one for each cell doping polarity. 
     Two silver-plated Invar ribbon interconnectors  206 , are approximately 50 μm thick, and may be, welded to each solar cell  100  to provide space qualified thermally matched series connection. One skilled in the art will understand that other interconnect technologies, such as mechanically bonding, crimping and soldering may also be used. 
     As illustrated in FIG. 3, transparent silicone adhesive  300 , nominally 50 μm thick, bonds the solar cell circuit to the coverglass  202  and provides a space qualified non-darkening resilient interface. 
     In one preferred embodiment, the solar cell design is space qualified with a single-crystal silicon design. However, one skilled in the art will understand that other technologies, including GaAs/Ge and multijunction solar cells, can be used as well. In the preferred embodiment, the materials and the cell are optimized for performance in an AM0 spectrum (the spectrum found at Earth&#39;s orbit around the sun, outside of Earth&#39;s atmosphere) and the space radiation environment. As illustrated in FIG. 1 c,  a shallow junction N on P structure  106  which provides satisfactory radiation resistance may be used. By contrast, terrestrial silicon cells have lower radiation resistance because they use deep junctions to prevent punch through of the screen printed contacts. For extraterrestrial applications, the preferred base. silicon material is space qualified, Czochralski grown, boron doped, single-crystal silicon with a base resistivity of 1-3 ohm-cm. This resistivity is a compromise (radiation resistance vs. initial power) for many missions that don&#39;t see radiation fluences greater than about 3E15 e/cm 2  (1 MeV equivalent) where 10 ohm-cm material becomes advantageous. The silicon wafer of the preferred embodiment has been designed. to provide cost reductions compared to conventional designs, while at the same time maintaining those attributes that are important for maintaining radiation resistance, such as the resistivity and minority carrier lifetime. 
     As discussed above, GaAs/Ge and multijunction solar cells may be used in the SPM instead of silicon solar cells. The GaAs/Ge and multijunction solar cells, such as those manufactured by TECSTAR, can provide efficiencies greater than 24%. 
     From a reliability standpoint, an important design concern for solar cells is the contact characteristics. Preferably, both electrical and mechanical integrity are maintained throughout the mission even after many thermal stress cycles. To aid reliability, TiPdAg and AlTiPdAg back surface reflector (BSR) evaporated contacts may be used on silicon-type cells. To reduce costs, a metal shadow mask may be used, rather than much more expensive photolithographic techniques which can be used as well. A workable combination, consisting of bimetallic masks with narrow slots may be used. Mechanical fixturing with permanent magnets may be used to hold the masks firmly against the cell surface during metal evaporation. 
     In the preferred embodiment, the AlTiPdAg contact on the back, side of the solar cell has an evaporated aluminum BSR layer under the TiPdAg contact to reflect the long wavelength light which consequently reduces the absorptivity (α) to 0.71. 
     In a preferred embodiment, a two sided wraparound (WA) contact configuration  102  as shown in FIGS. 1 a - 1   c  is used due to its many advantages. First, the contact “pick-off” at two opposite ends, halves the parasitic series resistance losses associated with 10 cm dimensions. Also, because the contacts  102 ,  104  are located primarily on the back of the cell  100 , the front contact area is reduced, resulting in an increased active area. With all the terminal contacts  102 ,  104  on the back surface, the coverglass can cover the entire front surface, without introducing stress risers, resulting from top-to-bottom interconnects. The coverglass also provides full cell protection from atomic oxygen and high energy particle radiation effects. In the preferred embodiment, the design provides a “give away area” on the rear surface below 5%, adding less than 1% to the resistive losses. 
     As illustrated in FIGS. 1 a - 1   c,  in a preferred embodiment, the contact  102  is electrically coupled to N− material, while the contact  104  is electrically coupled to P+ material. 
     One embodiment of the front of the cell  100  illustrated in FIG. 1 a  has a dimension D 1  of approximately 10 cm, a dimension W 1  of approximately 10 cm, a bus bar width dimension X 1  of approximately 0.1 cm, and a bus bar spacing of approximately 4.57 cm. One embodiment of the back of the cell  100  illustrated in FIG. 1 b  has a contact width dimension T 1  of approximately 0.2175 cm, and an N channel contact length dimension L 1  of approximately 6.55 cm, and a P channel contact length L 2  of approximately 2.29 cm. 
     The estimated conversion efficiency of one embodiment of a 10 cm×10 cm, WA contact cell  100 , is approximately 12.1% (1,367 W/m 2 , AM0). This estimate is based on data from a prior art 13.7% efficient 4 cm×6 cm cells with dual antireflection coating derated by the following factors: 
     0.969 to include the effects of large cell area, series resistance and contact area losses; 
     0.945 to allow for the use of a single low cost layer CVD AR-coating; 
     0.980 for reduced area (obscuration), resulting from the use of low cost shadow masks; 
     0.985 for the WA contact effects, series losses from the give-way area, and shunt losses at the WA edges. 
     Typically, having fewer, larger cells reduces cost since the use of larger cells means there are less parts to handle, less testing, less waste area and consequently less attrition. Thus, the use of 10 cm×10 cm cells, such as are,used in terrestrial applications, as compared with 4 cm×6 cm or 8 cm×8 cm typically used in space applications, are used. This size is also compatible with the size ingots and the mechanization equipment available. 
     To minimize weight, the solar cell should preferably be as thin as practical, and 62 μm silicon cells have been fabricated and used to make flight qualified arrays, and may be used in the present invention. However, without incorporating a costly back surface field (BSF) design, there is a significant power loss for cells thinner than 150 μm. Thus, in one embodiment, a 200 μm cell thickness is used to minimize breakage losses associated with large area cells and to increase delta efficiency by 6%. This performance versus weight trade-offs is discussed further in the SPM discussion below. 
     In one embodiment, the solar cell antireflection coating is a single layer TiOx chemical vapor deposition (CVD) coating instead of the more expensive evaporated dual AR coatings. Both coating types can be used, have been space qualified, and have space flight heritage. However, in recent years, the additional Isc (short circuit current) performance advantage has been desired in spite of the additional costs and expensive evaporator equipment encountered. In order to reduce cost and increase throughput levels, the CVD method to form the AR coating in used in one embodiment. This coating will not delaminate or degrade the cell&#39;s mechanical integrity or electrical performance when operated over the specification environment and mission life. 
     Under dark reverse testing to 110% of Isc for 20 minutes, typical WA contact cells measured reverse voltages of 18-20 Volts. The use of bypass diode protection against reverse voltages is discussed below. 
     A summary of the selected solar cell physical and performance characteristics is presented in Table 1. These characteristics were used to predict on-orbit performance for the mission life. 
     
       
         
               
             
               
               
               
               
               
               
               
             
           
               
                 TABLE 1 
               
               
                   
               
             
             
               
                 The Solar Cell Outputs 1.62 Watts BOL 
               
               
                 (12.1% Efficiency) In Production Quantity 
               
             
          
           
               
                   
                   
                   
                   
                   
                 Weld Pull 
                   
               
               
                   
                   
                 Resistivity 
                 Size 
                 Weight 
                 Strength 
               
               
                   
                 Type 
                 (ohm-cm) 
                 (cm) 
                 (gm) 
                 (gm) 
               
               
                   
               
               
                 Physical 
                 Silicon 
                 1-3 
                 10 × 
                 5.20 
                 ≧300 
               
               
                 Characteristics 
                 N/P, 
                   
                 10 × 
               
               
                   
                 BSR 
                   
                 0.02 
               
               
                   
               
               
                   
                 Front 
                 Back 
                 AR- 
                 Solar 
                 Emittance 
               
               
                   
                 Contacts 
                 Contacts 
                 Coating 
                 Absorptance 
                 (+cover) 
               
               
                   
               
               
                 Physical 
                 TiPdAg, 
                 AlTiPdAg, 
                 TiOx 
                 0.71 
                 0.87 
               
               
                 Characteristics 
                 Wrap- 
                 BSR 
               
               
                   
                 around 
               
               
                   
               
               
                   
                   
                   
                   
                   
                   
                 V Rev   
               
               
                   
                 Isc 
                 Voc 
                 Imp 
                 Vmp 
                 Pmp 
                 −1.1 Isc 
               
               
                   
                 (mA) 
                 (mV) 
                 (mA) 
                 (mV) 
                 (mW) 
                 (V) 
               
               
                   
               
               
                 Electrical Prop. 
                 3700 
                 584 
                 3375 
                 480 
                 1620 
                 18-20 
               
               
                 (AM0, 28° C.) 
               
               
                   
               
               
                   
                 Isc 
                 Voc 
                 Imp 
                 Vmp 
                 Pmp 
               
               
                   
                 (μA/cm 2  ° C.) 
                 (mV/° C.) 
                 (μA/cm 2  ° C.) 
                 (mV/° C.) 
                 (%/° C.) 
               
               
                   
               
               
                 EOL Temp. 
                 +36 
                 −2.28 
                 +35 
                 −2.02 
                 −0.37 
               
               
                 Coefficients 
               
               
                 (28-60° C.) 
               
               
                   
               
               
                   
                 Fluence/cm 2   
                 Isc 
                 Voc 
                 Imp 
                 Vmp 
                 Pmp 
               
               
                   
               
               
                 1 MeV 
                 1E14 
                 0.94 
                 0.965 
                 0.935 
                 0.96 
                 0.90 
               
               
                 Radiation 
                 5E14 
                 0.86 
                 0.93 
                 0.85 
                 0.925 
                 0.785 
               
               
                   
                 2E15 
                 0.76 
                 0.885 
                 0.76 
                 0.885 
                 0.675 
               
               
                   
               
             
          
         
       
     
     As previously discussed, a preferred embodiment baseline SPM design is shown in FIGS. 2 and 3 and consists of six, 10 cm×10 cm, 200 μm BSR silicon solar cells  100  interconnected with 50 μm thick silver-Invar ribbons  206 . However, even larger area coverglass sizes may be used. Each SPM  200  is covered with a 100 μm thick, cerium oxide coverglass  202  which is bonded to the cells with Nusil CV7-2500 adhesive  300 . Component selection was based on system trade studies that evaluated electrical and mechanical performance, mass, reliability, manufacturability, size, cost, schedule and heritage. The preferred embodiment of the baseline SPM design advantageously has the following properties: 
     Reduction in piece parts—higher reliability and lower cost; 
     Low mass—minimal coverglass adhesive, cell and coverglass mass, as illustrated in FIG. 4; 
     Manufacturable, efficient design—all interconnections are made on the back side of the SPM  200 , as illustrated in FIG. 3; However, in other embodiments, the interconnections can be made on other SPM surfaces. 
     Space qualified components 
     Performance parameters are well characterized. 
     In one embodiment of the SPM  200  illustrated in FIG. 2, the SPM  200  has a length Y 2  of approximately 30.17 cm, a width Y 3  of approximately 20.135 cm, and a typical cell gap and edge spacing Y 1  of approximately 0.025 cm. 
     The cell and coverglass trades for the SPM  200  are illustrated in FIG. 4 which shows an approximate power to mass ratio of 100 Watts/kg at End of Life (EOL) for the 0.020 cm/0.010 cm cell/coverglass thickness combination. The power density (W/kg) studies were performed to select the coverglass/cell thickness that would provide an optimum W/kg. As shown in FIG. 4, the 0.015 cm/0.010 cm and 0.020 cm/0.010 cm cover and cell design options provide significantly higher values than the other combinations. These two combinations were subsequently evaluated based on manufacturability (yields) and the net cost of producing all of the required SPMs. This analysis. showed that while the 0.015 cm/ 0.010 cm combination had a higher W/kg, it had a higher manufacturing cost due to lower expected yields than the 0.020 cm/0.010 cm combination. Therefore, based on its better $/kg ratio, 0.020 cm/0.010 cm is used in one preferred embodiment. However, other combinations may be used as well. Table 2 below provides an SPM metric in terms of power, mass and area for one particular design. 
     
       
         
               
             
               
               
               
             
               
               
               
               
             
           
               
                 TABLE 2 
               
             
             
               
                   
               
               
                 A Preferred Embodiment SPM Provides High Power Densities 
               
             
          
           
               
                   
                 BOL 
                 EOL 
               
               
                   
                   
               
             
          
           
               
                   
                 SPM Power (W) 
                 9.62 
                 5.29 
               
               
                   
                 Area (m 2 ) 
                 0.0609 
                 0.0609 
               
               
                   
                 Mass (Kg) 
                 0.05315 
                 0.05315 
               
               
                   
                 W/Kg 
                 181 
                 100 
               
               
                   
                 W/m 2   
                 158 
                 87 
               
               
                   
                   
               
             
          
         
       
     
     One preferred embodiment of the WA cell configuration allows for low cost SPM manufacturing. Manufacturing operations may be performed with the solar cells face side down for glassing, interconnecting, testing and marking. This approach reduces handling and greatly increases throughput. Another advantage of the preferred embodiment baselined cell is the interconnect. The interconnect may be a low cost silver-plated Invar ribbon formed for stress relief as part of the automation process and then welded to each cell of the SPM. The silver-plated Invar interconnect material has a thermal coefficient of expansion which is closely matched with silicon. This reduces weld and thermal elongation stresses resulting in a highly reliable, interconnection. The stress relief has been designed to absorb the 0.008 cm movement within the SPM and the 0.051 cm movement between SPMs. In one embodiment, the interconnect is protected from the effects of atomic oxygen by the design of the SPM which shelters the interconnects by covering them with the solar cell, cover adhesive and coverglass. Techniques other than welding may be used to attach the interconnects. By way of example, soldering or crimping techniques may be used as well. 
     The coverglass used in one preferred embodiment was selected by size, thickness and the need for coatings. FIG. 5 depicts the reduced cost savings of more than 71% by processing six cells under one piece of glass as compared to fabricating an assembly of one cell with one piece of glass. However, larger pieces of glass with a greater number of cells are feasible. FIG. 6 provides the results depicting the cost advantage of approximately 35 percent by using uncoated glass versus coated glass expressed in terms of dollars per watt at end-of-life. However, performance enhancements can be gained with the use of antireflective (AR) coatings with possible increased cost and added complexity at processing (having to keep track of the coated side). Coverglass performance experiments have been conducted, and the results show the uncoated coverglass provides a one percent gain as compared to the bare solar cell which is attributable to the improved optical match of the cover overlaid on the cell. It is also possible to use a coverglass that has increased rigidity when treated by a process called. “toughened.” The toughened glass process is widely used for military aircraft windshield applications and involves cutting-the coverglass to it&#39;s final size, then chemically treating it to replace the sodium ions with potassium ions. 
     Atomic oxygen erosion of the coverglass will be less than 1 micron when exposed to 1.5×10 −21  A/cm 2 . By analysis, one can calculate that even a more reactive material such as Teflon, which has a reaction efficiency of &lt;0.05×10 −24  cm 3 /atom, would lose approximately 0.75 micron. Using a glass with no antireflection coating, as in one preferred embodiment, ensures that an adverse optical property change will not occur. 
     FIG. 7 shows that while EVA adhesive represents a significant cost reduction (approximately 5.4. times) over CV7-2500, this growth in cost only affects the overall SPM cost by 2%. However, the mass increase affects the overall SPM by more than 6%. In one preferred embodiment, the lowest mass approach is used. CV7-2500 also has the advantage of being space qualified and meets outgassing requirements where EVA is still in the “experimental” stage for space use. Nonetheless, in another preferred embodiment, EVA may be used as well. 
     One preferred embodiment of the SPM design facilitates SPM integration into large solar arrays. In a preferred embodiment, silver-plated Invar interconnects protrude from the positive and negative edges of the,SPM to allow for welding of the interconnects between each module. The advantage of this approach is that all SPM level interconnecting is accomplished by overlapping the interconnect tabs and welding or soldering them together. The SPMs are sized and configured to allow for robotic intervention for a convenient pick and place operation. 
     FIG. 10A illustrates multiple SPMs  200  serially connected into a larger array  1000 , thereby providing higher output voltages than are achievable if the SPMs were connected in parallel. The array may optionally be protected using external diodes  1002 . In an alternative embodiment, the SPMs may be connected in parallel and the diode may be mounted within the SPMs. 
     FIG. 10B is a detailed diagram of a portion  1004  of the interconnected standard power modules of FIG.  10 . Interconnects  206  couple the N channel contacts  102  of one cell  100  to the P channel contacts of the adjoining cell. 
     In one preferred embodiment, silicon solar cells are used because they have the inherent capability to withstand reverse bias voltages experienced when cells in strings are partly or totally shadowed. Many satellites have flown without bypass diode protection, but it is customary to include a bypass diode connected across several silicon cells to prevent overheating or degradation of shadowed cells. 
     While bypass diodes may not be required, in one preferred embodiment, bypass diode protection is provided at the array level or on the cells themselves. When a bypass diode is mounted on a cell, the diode is typically mounted onto a cell surface. In one embodiment, placing one bypass diode externally for every 20 cells in series (10 SPMs) serves to protect the cells from degradation after the shadow is removed. 
     In another preferred embodiment, the solar cells are screened to identify and reject cells having reverse bias problems, so that no bypass, diodes are required. 
     A preferred embodiment of the SPM has excellent on-orbit performance characteristics. Performance predictions indicate that the EOL on-orbit power-to-mass ratio will be 100 W/kg with. an areal power density of 87 W/m 2 . These levels of performance translate into significant system-level benefits. The array mass savings can be used to increase the payload mass and augment the capacity of the revenue-generating communications systems. The areal power density performance enables a smaller area array, which reduces on-orbit drag, also reducing the fuel (and mass) that needs to be carried for station-keeping. 
     Power Analysis 
     A power analysis, presented in Tables 3A and 3B, uses typical loss factors, including Af—the array-level loss factor of 0.938. The P SPM  (EOL, on-orbit) and P STC  (deliverable configuration) values.are highlighted in the analysis, and the Rf, Sf, Af, and Tfn factors are identified. The P STC  value is based on SPM operation at the maximum power point. This value may be for acceptance testing and operation at voltages other than the maximum power point. For example, P STC  would be 9.064 W (5.80% reduction) if SPM testing is conducted at: 
     
       
           V test=0.9* Vmp ( STC )=0.855 V. 
       
     
     The cell dimensions are effective dimensions for a rectangular cell having the equivalent area to a preferred embodiment of the cell having cropped corners. A coverglass insertion factor of 1.01 is used. This value results from improved optical coupling to the single-layer AR-coated cell. 
     The temperature coefficients used are end-of-life values, and are applied in the analysis after all the life factors have been taken. These values were determined from FIGS. 3.15-3.18 of the Jet Propulsion Laboratory (JPL) Solar Cell Radiation Handbook (JPL Publication 82-69). The radiation factors are discussed further below. The UV darkening factor is based on similarity. The operating temperature was determined iteratively. 
     Radiation Analysis 
     The following process was used to determine the radiation effects on SPM performance. This method is based on the Solar Cell Radiation Handbook. 
     Typical energy spectra for charged particle environments were enhanced by interpolating energies for which radiation damage coefficients are defined by JPL. Energy spectra values are shown in FIG. 8 for relevant environments, trapped electrons, trapped protons, and solar protons. This is done to increase the resolution and accuracy of the subsequent calculations for equivalent radiation fluence. 
     These enhanced.spectra were then correlated with the JPL damage coefficients for all values of shielding for which coefficients are defined to determine the equivalent 1 MeV electron fluence. This was done for all relevant environments both for Isc-Voc and Pmax solar cell parameters. The results are presented in FIG.  9 . The trapped proton environment is dominant. This data was used for the cell and coverglass thickness trade studies to determine optimum power-to-mass ratio for the preferred embodiment of the SPM design. 
     
       
         
               
             
               
               
               
               
               
               
             
               
               
               
               
               
               
               
               
               
             
               
               
               
               
               
               
               
               
               
               
             
               
               
               
               
               
               
               
               
               
               
             
               
               
               
             
               
               
               
               
               
               
               
               
               
               
             
               
               
               
               
               
               
               
               
               
             
               
               
               
               
             
               
               
               
               
               
               
               
               
               
               
               
             
               
               
               
               
             
               
               
               
               
               
               
               
               
               
               
               
             
               
               
               
             
               
               
               
               
               
               
               
               
               
               
             
           
               
                 TABLE 3A 
               
             
             
               
                   
               
               
                 The SPM Provides 9.62 Watts BOL and 5.29 Watts EOL 
               
             
          
           
               
                   
                 SOLAR CELL 
                 BSR2 
                   
                 CELL THICKNESS (cm) 
                  0.020 
               
               
                   
                 DIMENSIONS 
                 (in)** 
                  3.900  3.900 
                 COVER THICKNESS (cm) 
                  0.010 
               
               
                   
                   
                 (cm)** 
                  9.906  9.906 
                 AREA (cm2) 
                 98.13 
               
             
          
           
               
                   
                 CELL PARAMETERS 
                 FACTOR 
                 Voc 
                 Isc 
                 Vmp 
                 Imp 
                 Pmax 
                   
               
               
                   
                   
               
             
          
           
               
                   
                 BARE CELL 
                 BSR2 
                   
                 0.584 
                 3.70 
                 0.480 
                 3.38 
                 1.62 
                   
               
               
                   
                 SERIES CELLS 
                   
                 2 
                 1.168 
                   
                 0.960 
                   
                 3.24 
               
               
                   
                 PARALLEL CELLS 
                   
                 3 
                   
                 11.10 
                   
                 10.13 
                 9.72 
               
               
                   
                 ASSEMBLY VOLTAGE 
                   
                 0.990 
                 1.156 
                   
                 0.950 
               
               
                   
                 ASSEMBLY CURRENT 
                   
                 0.990 
                   
                 10.99 
                   
                 10.02 
                 9.53 
               
             
          
           
               
                   
                 COVER GLASS 
                 UNCOATED 
                 1.010 
                   
                 11.10 
                   
                 10.12 
                 9.62 
                   
               
             
          
           
               
                 Pstc 
                 SPM PARAMETERS (Pstc) 
                 Efficiency @ 1367 W/m 2   
               
             
          
           
               
                   
                 LAPSS TEST 
                 BOL @ 
                 28° C. 
                 1.156 
                 11.10 
                 0.950 
                 10.12 
                 9.62 
                 Eff = 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                   
                 11.95% 
               
             
          
           
               
                 Af 
                 SPECIFIED ARRAY-LEVEL LOSS 
                 0.938 
                 1.120 
                 10.75 
                 0.920 
                 9.81 
                 9.03 
                   
               
               
                 Sf 
                 SUN INTENSITY (Aphellon) 
                 0.968 
                   
                 10.40 
                   
                 9.49 
                 8.73 
               
               
                 Rf 
                 MICROMETEORITES 
                 0.995 
                   
                 10.35 
                   
                 9.44 
                 8.89 
               
               
                 Rf 
                 UV 
                 0.980 
                 1.120 
                 10.14 
                 0.920 
                 9.25 
                 8.51 
               
             
          
           
               
                 Rf 
                 RADIATION EFFECTS 
                 1-MeV elect 
                   
               
             
          
           
               
                 Rf 
                 Voc 
                 EOL 
                 2.03E+15 
                 0.886 
                 0.992 
                   
                   
                   
                   
                   
               
               
                 Rf 
                 Isc 
                 EOL 
                 1.39E+15 
                 0.789 
                   
                 8.00 
               
               
                 Rf 
                 Vmp 
                 EOL 
                 2.03E+15 
                 0.886 
                   
                   
                 0.815 
               
               
                 Rf 
                 Imp 
                 EOL 
                 1.39E+15 
                 0.784 
                   
                   
                   
                 7.25 
                 5.91 
               
             
          
           
               
                 Tfn 
                 TEMPERATURE (DEG C.) 
                 56.06 
                   
               
               
                 Tfn 
                 EOL TEMP COEFFICIENTS 
               
             
          
           
               
                 Tfn 
                 Voc (mV/C) 
                 −2.28 
                   
                 −0.128 
                 0.864 
                   
                   
                   
                   
                   
               
               
                 Tfn 
                 Isc (uA/C-cm2) 
                 36 
                   
                 0.297 
                   
                 8.30 
               
               
                 Tfn 
                 Vmp (mV/C) 
                 −2.02 
                   
                 −0.113 
                   
                   
                 0.702 
               
               
                 Tfn 
                 Imp (uA/C-cm2) 
                 35 
                   
                 0.289 
                   
                   
                   
                 7.54 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                 5.29 
               
             
          
           
               
                 Psp 
                 SPM PARAMETERS (Pspm) 
                 Efficiency @ 1367 W/m 2   
               
               
                 m 
               
             
          
           
               
                   
                 ON-ORBIT 
                 EOL @ 
                 56.06 
                 0.864 
                 8.30 
                 0.702 
                 7.54 
                 5.29 
                 Eff = 
               
               
                   
                   
                   
                   
                   
                   
                   
                   
                   
                  6.58% 
               
               
                   
                   
               
               
                   
                 **Effective dimensions due fo corner crops  
               
             
          
         
       
     
     
       
         
               
             
               
               
               
               
             
           
               
                 TABLE 3B 
               
               
                   
               
               
                 Test Conditions 
               
               
                   
               
             
             
               
                   
               
             
          
           
               
                   
                 Performance at standard test 
                 P STC   
                 See Table 3A 
               
               
                   
                 conditions 
               
               
                   
                 Combined radiation factor 
                 Rf 
                 See Table 3A 
               
               
                   
                 Efficiency 
                 Eff 
                 See Table 3A 
               
               
                   
                 Temperature coefficients 
                 Tfn 
                 See Table 3A 
               
               
                   
                 Front surface absorptance 
                 αf 
                 0.71 
               
               
                   
                 Front surface hemispherical 
                 εf 
                 0.87 
               
               
                   
                 emittance 
               
               
                   
                   
               
             
          
         
       
     
     The effective shielding was determined for both the front side and back side of the SPM. The values for the baseline design are given in Tables 4 and 5. 
     
       
         
               
             
               
               
               
               
             
           
               
                 TABLE 4 
               
             
             
               
                   
               
               
                  Front Shielding Calculation 
               
             
          
           
               
                 Material 
                 Thickness 
                 Volume Density 
                 Areal Density 
               
               
                   
               
               
                 Microsheet 
                 100 μm 
                 2.605 gm/cm 3   
                 0.0265 gm/cm 2   
               
               
                 CV7-2500 
                  50 μm 
                  1.01 gm/cm 3   
                 0.0051 gm/cm 2   
               
               
                 Total 
                 140 μm 
                   
                 0.0316 gm/cm 2   
               
               
                   
                 of fused silica 
               
               
                   
               
             
          
         
       
     
     
       
         
               
             
               
               
               
               
             
           
               
                 TABLE 5 
               
             
             
               
                   
               
               
                 Back Shielding Calculation 
               
             
          
           
               
                 Material 
                 Thickness 
                 Volume Density 
                 Areal Density 
               
               
                   
               
               
                 Silicon 
                 150 μm* 
                 2.33 gm/cm 3   
                 0.0355 gm/cm 2   
               
               
                 Array 
                   
                   
                 0.0290 gm/cm 2   
               
               
                 Total 
                 290 μm  
                   
                 0.0645 gm/cm 2   
               
               
                   
                 of fused silica 
               
               
                   
               
               
                 *The 200 μm physical cell thickness equates to 150 μm shielding thickness because of reduced red and infrared response in the cell base.  
               
             
          
         
       
     
     The total mission fluence is established from the front and back shielding values given in Tables 4 and 5, respectively, and in FIG.  9 . The results are shown in Table 6 below. It is noted that the Isc curve is used for all solar cell parameters for the back shielding case, consistent with the treatment of Table 6.1 of the Solar Cell Radiation Handbook. The degradation factors used in the power analysis are then taken from Figures 3.55 to 3.59 of the Solar Cell Radiation Handbook. 
     
       
         
               
             
               
               
               
             
               
               
               
               
             
           
               
                 TABLE 6 
               
             
             
               
                   
               
               
                 Total Mission Fluence 
               
             
          
           
               
                   
                 Isc 
                 Voc, Pmax 
               
               
                   
                   
               
             
          
           
               
                   
                 Front 
                 8.20E+14 
                 1.46E+15 
               
               
                   
                 Back 
                 5.66E+14 
                 5.66E+14 
               
               
                   
                 Total 
                 1.39E+15 
                 2.03E+15 
               
               
                   
                   
               
             
          
         
       
     
     A mass analysis for the SPM is shown in Table 7 below. Results of mass measurements for prototype coverglass and silicon wafers, the dominant components of the SPM, were used to validate the calculated values. 
     
       
         
               
             
               
               
               
               
               
               
               
             
               
               
               
               
               
               
               
             
               
               
             
               
               
               
               
               
               
               
             
           
               
                 TABLE 7 
               
             
             
               
                   
               
               
                 Mass Analysis 
               
             
          
           
               
                   
                   
                   
                 Unit 
                 Quantity 
                 Total 
                 % of 
               
               
                   
                 Thickness 
                 Area 
                 Mass 
                 per 
                 Mass 
                 Total 
               
               
                 SPM Components 
                 (μm) 
                 (cm 2 ) 
                 (gm) 
                 SPM 
                 (gm) 
                 Mass 
               
               
                   
               
             
          
           
               
                 Silicon Solar Cell 
                 200 
                 98.131 
                 5.20 
                 6 
                 31.20 
                 58.7 
               
             
          
           
               
                 Solder 
                 N/A (welded) 
               
             
          
           
               
                 Coverglass 
                 100 
                 609.868 
                 16.141 
                 1 
                 16.14 
                 30.4 
               
               
                 Coverglass Bonding Adhesive 
                 50 
                 98.131 
                 0.503 
                 6 
                 3.02 
                 5.70 
               
               
                 (CV7-2500) 
               
               
                 Interconnects 
                   
                   
                 0.155 
                 18 
                 2.79 
                 5.20 
               
               
                 Total 
                   
                   
                   
                   
                 53.15 
                 100.00 
               
               
                   
               
             
          
         
       
     
     The calculated reliability, R SPM , of the SPM is equal to the calculated probability of success. The probability of success is related to component and weld joint failures. The solar cell failure rate, λ, is, expressed in units of “number of failures per operating hour.” The failure rate of 1×10 −9  failures per solar cell operating hour was used based on the JPL solar cell array design handbook. 
     A mission life of ten years and the on-orbit temperature of 56° C. were used to determine the failure rate. The reliability predictions were calculated for three scenarios: 1) two cells in series; 2) six cell in series; and, 3) two cells in series and three in parallel. 
     The solar cell failure rate of 1×10 −9  failures/hour is valid at 30° C. The on-orbit temperature was calculated to be 56° C. (see SPM performance for details). The failure rate increases by 5% per 10° C. increase in temperature. 
     
       
         56° C.−30° C.=26° C. 
       
     
     
       
         26° C.×0.005=0.13 
       
     
     
       
         λ cell=(1×10 −9 )×1.13=1.13×10 −9  @ 56° C. 
       
     
     
       
           R   SPM   =[e   (−number of cells in series×λ cell×mission life in hours) ] ×   
       
     
     where x=number of cells in parallel and where Mission Life=10 years×365 days/year×24 hours/day=87,600 hrs. 
     Scenario 1, 2 Cells in Series 
     
       
           R   SPM   =[e   (−2×1.13×10−9×87,600) ] 
       
     
     
       
           R   SPM =0.9998 
       
     
     Scenario 2, 6 Cells in Series 
     
       
           R   SPM   =[e   (−6×1.13×10−9×87,600) ] 
       
     
     
       
           R   SPM =0.9994 
       
     
     Scenario 3, 2 Cells in Series by 3 in Parallel 
     
       
           R   SPM   =[e   (−2×1.13×10−9×87,600) ] 3   
       
     
     
       
           R   SPM =0.9994 
       
     
     In summary, in at least one preferred embodiment, the SPM design is highly reliable. 
     Cell Manufacture and Test 
     One example of a general solar cell manufacturing process is illustrated in FIG.  11 . It is understood that other processes may be used as well. 
     (1) Wafer Etching  1102   
     In one preferred embodiment, wafers used in the SPM may be wire sawed. The wafers then undergo surface preparation. After sample inspection to verify compliance with size, thickness, resistivity, surface quality and cleanliness, the wafers are chemically etched to remove surface contaminants and damage from the sawing process. The wafers may be acid etched using automated production equipment to prepare the surface and control wafer thickness. The front surface is preferably smooth and free of work damage and provides for a shallow (0.15 μm) N+/P junction with good characteristics. In a preferred embodiment, the back surface polish provides high reflectance for longer wavelengths, reducing solar absorptance giving lower on-orbit cell temperature. For the wraparound (WA) design, this etch method provides a well rounded edge for proper deposition of insulating layers and contact materials. Automated handling from coin-stacked wafers to Teflon boats may be used. The transfer ensures that the two WA edges are etched and returned to a cassette, with all edges correctly aligned. The post-etch wafer thickness is controlled using SPC procedures which measure and control thickness by etchant temperature, concentration and immersion time. 
     Preferably, the manufacturing equipment. provides automation which allows for cassette-to-cassette wafer processing to achieve high throughput and yields. 
     (2) CVD SiO 2  Deposition  1104   
     In one embodiment, a diffusion mask is used on the back surface of the wafer prior to N+ diffusion to prevent doping of the back side of the wafer during the diffusion process, providing uniform and repeatable SiO x  layers. An ellipsometer is used to measure the oxide thickness and the process is controlled by using SPC methods. 
     The CVD production equipment is. available from Watkins-Johnson, and uses a continuous belt process with automatic cassette-to-cassette loaders. The wafers are transported through the furnace on a belt where silane and oxygen are mixed to form SiO 2  on the heated back surface of the wafers. The loaders allow for high throughput and high yields. 
     (3) The Diffusion Process  1106   
     Diffusion is the primary technique for forming the shallow N+/P junction. The wafers are semi-automatically transferred from polypropylene cassettes into a quartz diffusion boat. A transfer, device is used to transfer. the wafers to minimize wafer chipping and breakage and to maintain the alignment of the designated WA edges. The solar cell junction is formed in clean quartz boats and tubes. Phosphorus oxichloride (POCl 3 ) and oxygen are used to form phosphorus pentoxide (P 2 O 5 ) on the surface of the wafers. The high temperature (≈850° C.) drives the phosphorus into the wafer to form the junction. The sheet resistance of the diffused layer is controlled using SPC methods. This control ensures proper junction depth and therefore the good cell performance, both before and after orbital irradiation. 
     The MRL production rate diffusion furnace uses advanced process control capability to control diffusion depths and sheet resistance values. Quartz boats are manually loaded on a quartz paddle to start the process. The computer control system automatically positions the wafers in the hot zone of the furnace, initiates the proper gas flow sequence, and slowly transfers the wafers out of the process tube to cool. The wafers are then transferred back to polypropylene boats. 
     (4) Oxide Etch Process  1108   
     This process removes the oxide formed during the diffusion mask process (CVD) and removes the thin glassy oxides formed during the diffusion process. The etching solution uses a mixture of hydrofluoric acid and deionized water. 
     The oxide etch process is totally automatic and uses the same equipment type as for acid etch. Wafers are staged at the front of the machine in cassettes. The machine picks up the cassettes and automatically processes them through the etch and rinse. steps. It also automatically loads and replenishes, the chemicals using a chemical dispense system. 
     (5) CVD SiO 2  for Dielectric  1110   
     A dielectric oxide is preferably formed on the edges of the wafers, where the WA metal is deposited, to prevent shorting of the P/N junction. The dielectric is formed in the WA areas using CVD SiO 2 . Mechanical masks are used to define the pattern for isolation of the N-contact on the front and back sides of the wafers. The oxide thickness is controlled using SPC criteria. 
     The Watkins-Johnson machine is the same type as used for CVD of SiO 2  for the diffusion mask process. It is a reliable, continuous belt process. The operator positions a mask properly on a wafer, and clamps it with a clip. The wafer and mask assemblies are manually placed on the belt of the CVD SiO 2  furnace, and SiO 2  is deposited in the designated WA areas. 
     (6) Front/Back Metal Evaporation  1112 ,  1114   
     Front (TiPdAg) and back (AlTiPdAg) metal contact depositions are performed in high volume vacuum deposition evaporators used extensively for space cell manufacturing. CHA Industries Mark 50 vacuum deposition system is specifically designed for flexibility and long term reliability to support high volume production. Precision metal masks, with ≈50 μm wide grid openings, are used to form the front grid and bus bar pattern. The mask maintains cell performance while eliminating the usual expensive, labor intensive photolithography processing. A mask is also used for the back side to ensure the proper electrical isolation needed on the back side between the P and N metal contacts. The metal thickness are controlled using SPC methods. 
     (7) Antireflective (A/R) Coating Process  1116   
     The cells are coated with an atmospheric pressure chemical vapor deposited (CVD) antireflective coating on the front surface. The coating operation is a low cost, high volume, continuous belt process using equipment provided by BTU International. Vaporized tetraisopropyltitanate (TPT) and water are mixed and introduced to the heated a surface of the wafers where TiO 2  is formed. With the WA cell design, masks are not required to shield the contacting areas from the AR coating for additional cost reduction. 
     (8) Sintering Process  1118   
     Contact and coating sintering is performed to form good ohmic contact to the cell and to increase adhesion to the silicon wafer. The AR coating adhesion is also improved. Sintering uses a belt furnace supplied by the Thermco Company. Hydrogen and nitrogen are mixed in the furnace to minimize oxidation of the metals during the process. The wafers are placed directly on the moving belt, and process controllers ensure that the correct heating rate, dwell time and cooling rate are maintained for optimum contact sintering. The wafers are then removed from the belt and placed in coin stacks. 
     (9) Cell Lot # Marking  11120   
     Traceability of each evaporation lot is established using a TECSTAR standard high volume, non-contact VideoJet marking system. Other marking systems may also be used. 
     (10) Cell Electrical Test  11122   
     Solar cells are tested with automated cell test equipment incorporating an integrated AM0 solar simulators. The cells are separated into electrical groups based on their individual outputs measured at a constant test voltage. 
     Coin stacks of cells are placed in a load stacker magazine on the tester. A robotic transfer system automatically places the cells under the solar simulator for testing, and then places the cells in the proper electrical group. The operator only needs to pick up the counted stacks of tested cells and to identify electrical groups. The sorted cells are transferred to the assembly area for assembly into SPMs. 
     SPM Manufacture and Test 
     One technique for manufacturing SPMs is illustrated in the SPM Manufacturing Flow diagram of FIG.  12 . It will be understood by one skilled in the art that other known techniques may be used as well. The detailed descriptions of the individual SPM processing, steps are contained in the following paragraphs. 
     (1) Load Cell Pallet  1202   
     An automated cell handling system is used to provide the accuracy and repeatability needed for high volume assembly. 
     Cells may be robotically removed from a cassette and positioned on a six-cell fixture (cell pallet) that maintains the cell alignment throughout the glassing process. Only minimal mechanical contact with the active surface of the cell occurs. Contact of the cells edges and the active surfaces with metal surfaces is eliminated. Unlike a standard front-to-back contact cell, no handling steps involving awkward “tabbed” cells are required. 
     The positioning and adhering of the cell onto a cell pallet removes possible inherent cell bow in addition to maintaining the cell&#39;s location with respect to the other five cells. Varying cell gaps due to cell dimensional tolerances become less critical when interconnects do not pass through them. Having no interconnects on the cell back enables the cells to be placed flat against the pallet for precise control of the adhesive and SPM assembly thickness. 
     The automated rotation (180° flip) of the loaded cell pallet, followed by the cell&#39;s self-aligning placement onto a glass pallet containing a coverglass with glassing adhesive, completes this process step. 
     (2) Load Glass Pallet  1204   
     Manual removal of coverglass from its shipping container provides a dependable and expedient method of separation from the protective packing materials. Next, a cleaning process (nitrogen blow-off) and visual inspection provides screening for potential material defects. The six-cell coverglass is then aligned onto a glass pallet designed to retain its position and protect the glass edges from subsequent damage. The pallet is also designed to reduce or eliminate material “bowing” throughout the glassing process. Maintaining the cells and the coverglass flat to the fixture surfaces is helpful in controlling the adhesive gap during the “wicking” and adhesive cure processes. The transfer and alignment of the pallet onto the adhesive deposit station completes this process step. 
     (3) Adhesive Deposit On Glass  1206   
     Manual adhesive preparation, documentation and equipment calibration have been proven effective for high-volume production. Standard procedures emphasize attention to material pot life and storage conditions. Adhesive materials are packaged in precise mix ratios for accuracy. Prior to dispensing, the adhesive mix is “de-gassed” in a vacuum chamber to remove entrapped air and minimize voids during glassing. 
     An adhesive pattern is deposited onto the coverglass surface with the precision control of a programmed X-Y table in concert with. a multi-head adhesive metering system for consistent placement and repeatable volume dispensing. Transfer of the glass pallet containing a coverglass with glassing adhesive completes this process step. 
     (4) Adhesive Cure  1208   
     The cell/adhesive/glass sandwich is automatically transferred to a conveyor where adhesive “wicking” progresses under ambient conditions under the weight of the cell pallet. The cell pallet remains aligned with the glass pallet via guide pins which allow the sandwich to come together until the cell pallet bottoms-out on the glass pallet and the adhesive gap is fixed. Even with adhesive viscosity changes over the allowable pot life of the material, full wicking is achieved in the time allotted. Any excess adhesive flows into the gaps between the cells. Without any interconnects attached to the cell&#39;s active side, the adhesive gap design is the thinnest and produces the lightest overall weight. The option of glassing with EVA produces an excessive 0.013 cm cell/coverglass gap due to sheet material thickness limitations, so selected liquid silicones with thickness capabilities down to 0.003 cm are preferable. Since interconnects in this area would inhibit and complicate adhesive flow, trap unwanted air and promote cell surface high-spots that may come in contact with the glass, alternatives to the WA cell design are less desirable during this process. 
     At the end of the wicking operation, the fixture assembly passes through a tunnel oven profiled to bring each fixture up to temperature gradually, to thus prevent warping of the assembly or uneven cure of the adhesive. The conveyor belt width is oversized to allow a large range of adjustment without limiting throughput. The end of the conveyor passes through a cooling section designed to bring the assembly back to ambient conditions without stressing the SPM. The conveyor system ensures that each SPM is exposed to identical process parameters unlike a batch oven system that is subject to the human variable. To end this process step, the cell pallet is removed from the assembly, leaving the glass pallet containing the module to be manually transferred to the interconnecting station. 
     (5) Interconnect And Inspect  1210   
     Automated interconnection technology is used to mechanically form individual interconnects from a reel of ribbon and then robotically position them for welding. Redundant welding performed with state-of-the-art “constant power” controlled equipment ensures superior reliability and weld strength consistency by automatically adjusting to variances in cell/interconnect surface conditions via process feedback. All portions of the interconnect, including the formed strain relief and welded areas, are fully exposed and free from adhesive contamination unlike any of the front to back contact options. When contact must be made to the front side of a cell, the interconnects strain relief and weld joints become buried in adhesive during the glassing process, prompting concern with having to endure differential thermal stresses between the front and back-side of the cell. By contrast, welding solely to the cell back-side after glassing, in accordance with one embodiment of the present invention, creates intimate support of every portion of the cell with an adhesive/glass layer producing the lowest mechanical stresses. Welding to a cell&#39;s front side typically requires a pre-glassing weld station, and special handling of interconnected cells, causing increased attrition and manufacturing difficulties. A weld station also attaches the necessary array interconnects to the SPM as detailed above. After welding, an integrated visual inspection identifies candidates to be separated for rework on another weld station to prevent any interruption in product flow. The SPM is then separated from the glassing pallet and transferred to the cleaning station. 
     (6) Clean, Electrical Test And Mark  1212   
     Manual cleaning of SPM coverglass utilizing process compatible solvents to remove adhesive contamination is performed as required. Unlike soldered interconnects, welding leaves no contaminating residue. Additionally, the process used for attaching interconnects after glassing eliminates clean-up which would otherwise be necessary due to adhesive wicking along the interconnect into its strain relief region. The next step is to position the SPM glass-side down on the electrical test fixture. Automated probing of the electrical contacts, flash testing, data collection/storage and marking of the SPM with bar-code and human readable codes are completed at this station to guarantee traceability and minimize further handling steps prior to the inspection process. 
     (7) Inspection  1214   
     Visual in-process inspection is performed by line operators. Final inspection of the SPM may be independently performed by quality assurance personnel in accordance with an approved Acceptance Test Plan. 
     (8) Packaging  1216   
     Completed SPMs are packaged in reusable containers designed for mechanized loading/unloading. 
     While certain preferred embodiments of the invention have been described, these embodiments have been presented by way of example only, and are not intended to limit the scope of the present invention. Accordingly, the breadth and scope of the present invention should be defined only in accordance with the following claims and their equivalents.