Abstract:
An assembly for use on an aircraft wing having an aircraft skin and a fuel tank, the assembly comprising a metal access door for accessing the fuel tank, a metal retainer ring for engaging the wing and the access door. Fasteners removably couple the access door to the retainer ring. A lip, which may be on the wing surface, is configured to receive a perimeter of the access door when the access door is coupled to the retainer ring. A polyurethane elastomeric gel gasket having a metallic skeleton is configured to lay between the access door and a lip of the metal wing surface. Under compression, the polyurethane will deform and squeeze out the edges and flatten so as to provide metal-to-metal contact between the access door and the lip.

Description:
[0001]    This continuation application claims priority to, the benefit of, and incorporates herein by reference U.S. application Ser. No. 15/085,389, filed Mar. 30, 2016; U.S. application Ser. No. 13/788,583, filed Mar. 7, 2013; which claims priority to, the benefit of, and incorporates herein by reference U.S. Provisional Application Ser. No. 61/647,149, filed May 15, 2012. 
     
    
     FIELD OF THE INVENTION 
       [0002]    Gaskets, more specifically, compressed, impregnated gaskets for the fuel access door of an aircraft. 
       BACKGROUND OF THE INVENTION 
       [0003]    A fuel door is typically located on the upper portion of the wing of an aircraft. Removal of fasteners allows removal of the door. Removal of the door provides the ability to access to the fuel tank. The door is removably attached, sealing compressively against a door ring having “O” rings (see  FIG. 13 ). The door retainer ring is urged up against the underside of a perimeter portion of the door or an opposed mating wall, stationary on the wing is provided. A gasket is provided between the inner-facing wall on the door and the opposed wall on the wing. These gaskets are typically conductive in nature. 
       SUMMARY OF THE INVENTION 
       [0004]    Applicants provide a unique electrical conductive gasket configured for use between a fuel door of a winged aircraft and the aircraft, to provide a conductive seal with favorable environmental sealing properties, for example, sealing against the passage of fluids therepast. 
         [0005]    A gasket for use with a fuel access door having a generally flat inner facing mating wall and having an outer perimeter and an opposed generally flat outward facing mating wall having an inner perimeter on a wing of an aircraft, the fuel access door adapted to be removably fastened to the wing, the gasket comprising a porous, partially open metallic skeleton being generally tabular in nature and generally ring shaped, the skeleton having a generally flat upper surface and a generally flat lower surface, an inner perimeter wall and an outer perimeter wall; and a pliable, resilient, elastomeric, sticky, substantially air bubble free polyurethane, coherent body, substantially filling the openings of the skeleton and being generally tabular in nature, the body being ring shaped having a generally flat, tacky upper surface, a generally flat, tacky lower surface, an inner perimeter wall, and an outer perimeter wall; wherein the inner perimeter walls of both the skeleton and the body generally conform to the shape defined by the inner perimeter of the outward facing wall and wherein the outer perimeter walls of both the skeleton and the body generally conform to the shape defined by the outer perimeter of the fuel access door; and wherein the gasket is adapted to lay between the inner facing mating wall member and the outward facing mating wall member. 
         [0006]    A method of making a gasket for use with a generally flat inner facing mating wall having an outer perimeter of a fuel access door and an opposed generally flat outward facing mating wall having an inner perimeter of a wing of an aircraft, the method comprising the steps of providing a mold to receive the skeleton therein; pouring a pre-cured polyurethane mix in the mold to substantially cover the skeleton; removing air from the polyurethane mix; and allowing the polyurethane mix to cure. 
     
    
     
       BRIEF DESCRIPTION OF THE DRAWINGS 
         [0007]      FIGS. 1A and 1B  are illustrations of the knitted, woven metallic fabric that may be used in creation of the gasket or embodiments thereof as set forth herein. 
           [0008]      FIGS. 10 and 1D  illustrate a concentric configuration and spiral configuration of the metallic woven and/or knitted fabric as set forth herein. 
           [0009]      FIGS. 2A and 2B  illustrate pre-compression and post-compression views of the skeleton in concentric configuration. 
           [0010]      FIGS. 3A and 3B  illustrate views of a skeleton having a layered fabric configuration, pre-compression and post-compression. 
           [0011]      FIGS. 4A, 4B, 4C, and 4D  illustrate a method of manufacturing an embodiment of the gel impregnated gasket as describe and disclosed herein. 
           [0012]      FIGS. 5A, 5B, and 5C  illustrate a method of manufacturing embodiment of the gasket disclosed herein utilizing a vacuum drawn following application of a pre-cured mix. 
           [0013]      FIG. 6  illustrates a gasket according to one embodiment of the invention configured for placement between a fuel access door and a fuel access door retaining ring of a wing of an aircraft. 
           [0014]      FIGS. 7, 8 and 9  illustrate an alternate preferred embodiment of a gel impregnated gasket utilizing woven mesh, which mesh is first compressed and then impregnated (soaked) in premix. 
           [0015]      FIG. 10  illustrates an alternate preferred embodiment of Applicants&#39; gasket using multiple, preformed, cured, gel bodied gaskets having a single or multiple skeletons therein. 
           [0016]      FIGS. 11, 12, and 13  illustrate a preferred environment in which Applicants&#39; gasket may be used. 
       
    
    
     DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENT 
       [0017]    This application incorporates by reference, U.S. Pat. Nos. 6,530,577; 6,695,320; and 7,229,516. 
         [0018]    Applicants provide for a gasket  10  that is comprised of a pliable metallic conductive skeleton  12  and an elastomer body  14 , such as a polyurethane. The polyurethane may be the polyurethane set forth in U.S. Pat. Nos. 6,530,577; 6,695,320; and 7,229,516, incorporated herein by reference. 
         [0019]    Strands  16  of a conductor, such as a fine gauge steel, may be woven, in one embodiment, into a knitted or sheet-like metallic fabric  18 . The fabric may be folded, rolled, layered or stacked to create a multi-ply skeleton  12 , which may, in one embodiment, be compressed (see  FIGS. 2A, 2B, 3A, 3B ) and then soaked or impregnated in any suitable way, such as pouring or applying as shown in  FIG. 4C , with a pre-cured elastomer. The elastomer and skeleton may be subject to the removal of any trapped air bubbles  23  (see  FIG. 4C ) in a pre-cured condition, and then allowed to cure. Polyurethane, such as set forth in the patents incorporated by reference may be used for the elastomer, gel body. In one embodiment, multiple skeletal layers  20   a - 20   e  are seen, which layers may be concentric ( FIGS. 10, 2A, and 2B ), spirally wound, tabular ( FIG. 1D ), (that is, separate layers, see FIG.  3 A), and together, may be compressed (before adding the mix) under pressure either within (see  FIG. 3A , for example) or without a mold. 
         [0020]    In one embodiment, pressure is applied to the skeleton to both compress and shape the metallic skeleton. Pressure is typically sufficient to give a set to the metal comprising the skeleton. Thereafter, mix is applied and the mix is allowed to settle, is compressed, or is vacuum drawn into the gasket, after which it is allowed to cure. 
         [0021]    The gasket is typically configured to lie between a fuel door and fuselage of an aircraft or any other suitable location under compression. Typically, some squeeze-out and/or deformation of the elastomer  14  occurs with contact and compression between the fuel door, the skeleton, and the fuselage to ensure conductivity and a good environmental seal between the same (see  FIG. 13 ). 
         [0022]      FIGS. 1A and 1B  are illustrations of a knitted and/or woven metallic fabric that may be used in creation of one embodiment of the gasket or embodiments thereof as set forth herein. The interlocked loop structure is illustrated. This material is available from Metex Corp., of Edison, N.J. (see “metexcorp.com”). 
         [0023]      FIGS. 1C and 1D  illustrate concentric configurations and spiral configurations, respectfully, of the metallic woven and/or knitted fabric or other suitable at least partially open metal skeleton as set forth herein.  FIGS. 2A and 2B  illustrate pre-compression and post-compression views of the skeleton in multiple concentric configurations when skeletal compression (before adding mix) is used.  FIGS. 3A and 3B  illustrate views of a skeleton having a layered fabric configuration, pre-compression and post-compression. The pre-impregnation skeleton shape has been formed and configured to seal between the door retainer lip and the access door as seen in  FIG. 13 . 
         [0024]    Thus, it is seen with respect to  FIGS. 1A-1D , that a skeleton, in one embodiment having a knitted interlocking loop metallic fabric structure may be provided in a number of configurations and compressed into a shape suitable for laying between a fuel access door as seen in  FIG. 13 , and a mating face for compression therebetween. 
         [0025]      FIGS. 4A, 4B, 4C, and 4D  illustrate a method of manufacturing an embodiment of the gasket as describe and disclosed herein.  FIGS. 4A and 4B  illustrate that a skeleton  12  may be configured in a number of ways, including compression in a mold shaped to reflect the contact area between the lip and the access door as illustrated in  FIGS. 12 and 13 .  FIG. 4B  illustrates laying the skeleton in a first container and then applying a two-part polyurethane mix as set forth in U.S. Pat. Nos. 6,530,577; 6,695,320; and 7,229,516, incorporated herein by reference. The skeleton, soaked with pre-cured mix in the first container as seen in  FIG. 4C  may be placed in a vacuum container  24  as seen in  FIG. 4D  and the vacuum drawn as set forth herein.  FIG. 6  illustrates the gasket  10  after air bubbles are removed from the polyurethane mix. 
         [0026]    In  FIG. 4D , a method of forming an gasket as set forth herein is disclosed. What is seen is a pump drawing a vacuum on a vacuum chamber or container with a dome on it, capable of generating a vacuum. A skeleton is placed in a first container and then completely covered, typically by at least a ¼ inch of pre-cured polyurethane mix extending above the skeleton (see, for example,  FIGS. 4B and 4C ). A preferred mix has the consistency and viscosity of about 50 weight motor oil. 
         [0027]    The first container is then placed inside the vacuum chamber and a vacuum is run. While the vacuum is being run, observation allows one to see the air bubbling out of the covered gasket. When the gas stops bubbling out of the covered gasket, the first container is removed from the vacuum chamber (following a return to ambient pressure). After the mix has cured, the gel body is substantially without air bubbles and the skeleton is substantially saturated with the cured polyurethane elastomer. 
         [0028]      FIGS. 5A, 5B, and 5C  show an alternate method of manufacturing and indicate that a modified container  26  be sealed and a vacuum drawn thereupon to remove the air therefrom. 
         [0029]      FIGS. 7, 8 and 9  illustrate an alternate preferred method of making a gasket utilizing woven fabric, such as aluminum mesh. In  FIG. 7 , a multiply woven metallic mesh, such as the metallic skeleton disclosed in the patents incorporated herein by reference, is soaked in pre-cure. The skeleton may be precut to the gasket shape in single or multiple sheets, laid together and soaked. Following soaking and before curing,  FIG. 8  illustrates the addition of pressure or compression. The compression may help remove any air bubbles and also help bring skeletal layers of a multi-ply embodiment closer together. It will typically generate some squeeze out (see  FIG. 8 ). 
         [0030]      FIG. 10  illustrates an alternate preferred embodiment of Applicants&#39; gasket using multiple gaskets having a single or multiple skeletons therein.  FIG. 10  illustrates the gaskets with metallic skeletons that are disclosed in the patents incorporated by reference herein. They are die cut or cut by other means to reflect the shape for use between an access door and the lip (see  FIGS. 12 and 13 ). They are then, already cured, stacked as seen in  FIG. 10  and may be compressed. Stacking will effect a sticking of one to the other. They may then be compressed when they are placed between the access door and the wing. In any case, compression will be sufficient to provide metal-to-metal contact between the access door and the lip. 
         [0031]    Applicants&#39; pre-cured polyurethane mix will when cured produces a gasket suitable for use in the environment set forth herein. This gasket will leave no silicon residue and is removable and reusable. The skeleton in the elastomer is molded and shaped to reflect substantially full coverage flat and adjacent to the underside of the shoulder of the access door D as seen in  FIGS. 12 and 13  and the top side or upper surface of the lip. As can be seen in  FIGS. 12 and 13 , these two surfaces are parallel and spaced apart and, thus the gasket is typically tabular to provide, under compression, substantially full coverage with some squeeze-out of elastomer at the edges as seen in  FIG. 13 . 
         [0032]    It is seen that Applicants&#39; method of making the aircraft gasket typically includes a vacuum step for removing any air bubbles that may have accumulated or become entrained in the mix in the process of adding the liquid mix to the skeleton. Moreover, it is seen that the vacuum step may be achieved by applying a vacuum to the mold as seen in  FIGS. 5A-5C . On the other hand, the vacuum step may be achieved by placing the entire mold with the pre-cured gel poured on the skeleton, to the inside of a vacuum chamber, and drawing a vacuum on the chamber as seen in  FIG. 4D . In both cases, in a few minutes, any bubbles should be cleared from the mix, which can be confirmed, if desired, visually. Typically, the vacuum is then removed and the gel allowed to cure. This may be 30 minutes to one and a half hours, or any other suitable time. 
         [0033]    It is seen that the skeleton is typically comprised of at least one metallic layer and is more typically comprised of multiple metallic layers. It is seen that there may be pre-compressed or compressed after the pre-mix has been poured over and before the pre-mix cures. The skeleton is typically compressed sufficiently so that, if it is multiple layers, it may take a set (permanently deforming, for example), in one embodiment. In another embodiment, the layers are simply pressed close to one another. 
         [0034]    The preferred elastomer is a pliable, resilient, elastomeric, and sticky. A mix that will provide such an elastomer is the polyurethane referenced in the patents incorporated by reference. It forms a coherent body with the skeleton, coherent meaning that it flows between the skeletal openings like hundreds of small arms connecting to one another throughout the openings of the skeletal body. 
         [0035]    In an uncompressed state, the gasket is typically in the range of about 20 mil to 100 mil thick (preferred about 50 to 100 mil (more preferred about 80 mil). When placed between the fuel door and the wing, the fuel door will be fastened, with a multiplicity of fasteners, and compress the gasket. Typically, the fuel door has a flat inner facing mating wall member having an outer perimeter. Opposed to that is a generally flat, outward facing mating wall having an inner perimeter, which is typically on or is part of the wing of an aircraft. The fuel access door is adapted, with multiple fasteners, to removably attach the wing so as to compress the gasket between the two facing walls. 
         [0036]    In one embodiment, a torque of about 90 inch pounds is placed on ¼″-inch fasteners (MD-80 Fuel Access Door), which is typically sufficient to allow deformation of the gasket body (typically flowing out of the perimeter edges), and compression such that the metallic skeleton makes metal-to-metal contact between the two mating walls and between the multiple plies thereof. 
         [0037]    In a compressed condition, the gasket may be between about 40 to 80% of pre-torque thickness, preferably about 50% but typically the compressed condition of the gasket is less than the pre-compression thickness of the skeleton. The thickness of the skeleton (measured before the mix is applied) may be in the range of about 20 to 22 mil preferred in one embodiment. The pressure on the gasket in a compressed condition between the fuel door and the aircraft wing may be in the range of about 1500 to 1900 psi, for example on the MD-80. In other embodiments, it may be about half this range. 
         [0038]    The multiple layers of the skeleton may be comprised of a woven metallic mesh, a metallic fabric, an expanded metal knitted, chopped metal strands, or other suitable skeleton. The multiple layers comprising the skeleton may be separate layers (see  FIG. 3A , for example), or they may be joined at their edges (see  FIG. 2B , for example). 
         [0039]    Compression may be used at several points in the method of making the gasket illustrated herein and in its method of use. In the method of making the gasket, in one embodiment, compression is applied to the metallic skeleton, before the application of the pre-cured polyurethane mix. Enough compression is applied to typically give some set to the metallic skeleton, such that when the pressure is released, it is not as thick as before the pressure was applied. In any of the steps set forth herein, this step can either be utilized or omitted. It typically assists in providing for a thinner gasket and one in which, in a multi-ply embodiment, has the plies laying closer to one another or even touching, before the pre-cured mix is applied. 
         [0040]    The term “compression” is also used when, following the application of the pre-cured mix, pressure is applied, both to help squeeze out bubbles and to help bring the gasket into a thinner condition, this compression step is illustrated, in one example, in  FIG. 8 . This will also typically help bring out any entrained air bubbles from around and within the metallic skeleton. 
         [0041]    After the gasket has been formed and the polyurethane cured, it may be removed from the mold or container. When placed between the retainer ring and the fuel access door, it will be compressed when the fuel access door is snugged down with fasteners. In doing so, there will be squeeze-out typically generated past the edges (as seen in  FIG. 13 ). This may help with an environmental seal. Compression at this point is also sufficient to ensure metal-to-metal contact between the door and the retainer ring, through the metallic. Skeleton. 
         [0042]    While polyurethane is disclosed as a suitable material for the body of the gasket, any material that will affect a good environmental seal between the fuel door and the ring, with sufficient tac or stickiness so as to stick to the mating surfaces and flowability may be sufficient. Moreover, while Applicants&#39; gel bodied gasket is illustrated in a preferred embodiment to be shaped and configured for use in sealing a fuel door to a retainer ring lip or other mating surface, the gasket and the methods of making the same as disclosed herein may be used in any aircraft embodiment or other embodiment where a good environmental seal is needed and where the gasket may be subject to a harsh environment, including temperature extremes and significant pressure differentials. Moreover, the gasket disclosed may be particularly used for, when a metallic skeleton is used, for EMI applications. The term “homogeneous” means substantially consistent physical and chemical properties throughout the gel body of the gasket. 
         [0043]    Although the invention has been described with reference to a specific embodiment, this description is not meant to be construed in a limiting sense. On the contrary, various modifications of the disclosed embodiments will become apparent to those skilled in the art upon reference to the description of the invention. It is therefore contemplated that the appended claims will cover such modifications, alternatives, and equivalents that fall within the true spirit and scope of the invention.