Abstract:
Polycarbonate compositions comprising a small amount of a certain halogenobenzotriazole were found to be particularly suitable for optical purposes since they feature a desirable high UV-cutoff and since they are processable at high temperatures.

Description:
This application is a division of application Ser. No. 722,029, filed Apr. 11, 1985, now abandoned. 
    
    
     FIELD OF THE INVENTION 
     The present invention relates to polycarbonate compositions and more particularly to UV-stable polycarbonate compositions. 
     SUMMARY OF THE INVENTION 
     Polycarbonate compositions comprising a small amount of a certain halogenobenzotriazole were found to be particularly suitable for optical purposes since they feature a desirable high UV-cutoff and since they are processable at high temperatures. 
     BACKGROUND OF THE INVENTION 
     While the use of polycarbonate in the field of the safety eyewear market has been established, its use for molding of certain opthalmic vision care products which also protect against UV radiation has been limited. Existing polycarbonate products are satisfactory for applications where moderate UV screening is required, i.e. up to about 380 NM (nanometers) cutoff. Recent information indicates that radiation between 274 NM and 400 NM may be damaging to the eye and studies point to that UV radiation is a cause of cataracts. The current standards respecting opthalmic lenses include requirements of 0% transmission at 390 NM, 0 to 8% transmission at 395 NM and 0.1 to 15%Z transmission at 400 NM. For safety goggle lenses the standards require 0% transmission at 400 NM. 
     The art recognizes the need to improve the UV stability of polycarbonate resins and to minimize the transmission of harmful UV radiation through polycarbonate molded parts. While UV absorbers are generally known, not all are compatible with polycarbonate resins at the high temperature required for moldings. Representative of the art in this connection is U.S. Pat. No. 4,096,115 which discloses a large number of UV stabilizers said to be effective in any of a great number of polymeric compositions. 
     The relevant art is noted to include U.S. Pat. No. 3,322,719 which discloses polycarbonates made stable in respect to UV radiation upon the incorporation therewith of a co-stabilizer selected from a group which includes phosphoric acids, boric acid, and certain phosphates and any member selected among certain benzophenones and a certain 2-(2&#39;-hydroxy-5&#39;-tertiary octylphenyl)-benzotriazole (Cyasorb®5411). Also relevant in this context is U.S. Pat. No. 3,367,958 which discloses UV stabilized polycarbonates containing up to 0.5% of 2-(2&#39;-hydroxy-5&#39;-methylphenyl)-benzotriazole. 
     U.S. Pat. No. 3,502,613 is noted to disclose polypropylene compositions which are made UV stable by the incorporation of the stabilizer of the present invention as a co-additive. Also, U.S. Pat. No. 3,892,889 discloses the UV stabilization of polycarbonate by treating the surface of the molded articles with a liquid mixture containing UV absorbers. The absorbers encompass within their scope the stabilizer of the present invention. U.S. Pat. No. 4,206,111 discloses that certain benzotriazoles--including stabilizers of the present invention--are made more efficient as stabilizers of polyolefins upon the addition to the compositions of certain diphosphonites and an oxidation inhibitor. U.S. Pat. No. 4,283,327 discloses UV stabilizers, including certain benzotriazoles which are effective in the context of polycarbonate compositions. 
     DETAILED DESCRIPTION OF THE INVENTION 
     The polycarbonate resins useful in the practice of the invention are homopolycarbonate, copolycarbonate and terpolycarbonate resins or mixtures thereof. Preferably, the polycarbonate resins have molecular weights of 10,000-200,000 (weight average molecular weight), more preferably 20,000-80,000, and may alternatively be characterized by their preferred melt flow of 1-24 gm/10 min. at 300° C. per ASTM D-1238. These polycarbonates may be prepared, for example, by the known diphasic interface process from phosgene and dihydroxy compounds by polycondensation (see German OS Nos. 2,063,050; 2,063,052; 1,570,703; 2,211,956; 2,211,957 and 2,248,817 and French Pat. No. 1,561,518 and the monograph, H. Schnell, Chemistry and Physics of Polycarbonates, Interscience Publishers, New York, 1964, all incorporated herein by reference). 
     In the present context, dihydroxy compounds suitable for the preparation of the polycarbonates of the invention conform to the structural formulae (1) or (2) ##STR1## wherein A denotes an alkylene group with 1 to 8 carbon atoms, an alkylidene group with 2 to 8 carbon atoms, a cycloalkylene group with 5 to 15 carbon atoms, a cycloalkylidene group with 5 to 15 carbon atoms, a carbonyl group, an oxygen atom, a sulfur atom, and --SO-- or --SO 2  -radical; or a radical of the general formula ##STR2## g denotes the number 0 or 1; e denotes the number 0 or 1; 
     Z denotes F, Cl, Br or a C 1  -C 2  alkyl and if several Z radicals are substituents in one aryl radical, they may be identical or different; 
     d denotes 0 or an integer of from 1 to 4; and 
     f denotes 0 or an integer of from 1 to 3. 
     Among the useful dihydroxy compounds in the practice of the invention are hydroquinone, resorcinol, bis-(hydroxyphenyl)-alkanes, bis-(hydroxyphenyl)-cycloalkanes, bis-(hydroxyphenyl)-ethers, bis-(hydroxyphenyl)-ketones, bis-(hydroxyphenyl)-sulfoxides, bis-(hydroxyphenyl)-sulfones and α,α-bis(hydroxyphenyl)-diispropyl-benzenes. These and further suitable aromatic dihydroxy compounds are described, for example, in U.S. Pat. Nos. 3,028,365; 2,999,835; 3,148,172; 3,271,368; 2,991,273; 3,271,367; 3,280,078; 3,014,891 and 2,999,846 (all incorporated herein by reference), in German Offenlegungsschriften Nos. (German Published Specifications) 1,570,703; 2,063,050; 2,063,052; 2,211,956 and 2,211,957, in French Patent Specification No. 1,561,418 and in the monograph, H. Schnell, Chemistry and Physics of Polycarbonates, Interscience Publishers, New York, 1964. Further examples of suitable dihydroxy compounds are 2,2-bis-(4-hydroxyphenyl)-propane (bisphenol A), 2,4-bis-(4-hydroxyphenyl)-2-methyl-butane, 1,1-bis-(4-hydroxyphenyl)-cyclohexane, α,α-bis-(4-hydroxyphenyl)-p-diisopropyl-benzene, 2,2-bis-(3-chloro-4-hydroxyphenyl)propane, hydroxybenzophenone and 4,4&#39;-sulfonyl diphenol; the most preferred one is 2,2-bis-(4-hydroxyphenyl)propane (bisphenol A). 
     The polycarbonates of the invention may entail in their structure, units derived from one or more of the suitable dihydroxy compounds. 
     The preparation of polycarbonate resins may be carried out in accordance with any of the processes known in the art, for example by the interfacial polycondensation process, polycondensation in a homogeneous phase or by transesterification. 
     The suitable processes and the associated reactants, catalysts, solvents and conditions are known in the art and have been described, inter alia, in German Pat. Nos. 1,046,311 and 962,274 and in U.S. Pat. Nos. 3,248,414; 3,153,008; 3,215,668; 3,187,065; 3,028,365; 2,999,846; 2,999,835; 2,964,974; 2,970,137; 3,912,638 and 1,991,273. 
     In the preparation of the polycarbonate resins of the invention monofunctional reactants such as monophenols may be used in order to limit their respective molecular weights. Branching agents may also be employed. Branching may be obtained by the incorporation of small amounts, preferably of between about 0.05 and 2.0 mol % (relative to diphenols employed), of trifunctional or more than trifunctional compounds, especially compounds having three or more phenyl aromatic hydroxyl groups. Polycarbonates of this type are described, for example, in German Offenlegungsschriften Nos. (German Published Specifications) 1,570,533; 1,595,762; 2,116,974 and 2,113,347; British Specification No. 1,079,821 and U.S. Pat. No. 3,544,514 (incorporated herein by reference). 
     Some examples of compounds with three or more than three phenyl hydroxyl groups which can be used are phloroglucinol, 4,6-dimethyl-2,4,6-tri-(4-hydroxyphenyl)-heptane, 2,4,6-trimethyl-2,4,6-tri-(4-hydroxyphenyl)-heptane, 1,4,5-tri-(4-hydroxyphenyl)-benzene, 1,1,1-tri-(4-hydroxyphenyl)-ethane, tri-(4-hydroxyphenyl)-phenylmethane, 2,2-bis[4,4-bis-(4-hydroxyphenyl)-cyclohexyl]-propane, 2,4-bis(4-hydroxyphenylisopropyl)-phenol, 2,6-bis-(2-hydroxy-5&#39;-methylbenzyl)-4-methylphenol, 2-(4-hydroxyphenyl)-2-(2,4-dihydroxyphenyl)-propane, hexa(4-(4-hydroxyphenylisopropyl)phenyl)-orthoterephthalic acid ester, tetra-(4-hydroxyphenyl)-methane, tetra-(4-(4-hydroxyphenylisopropyl)phenoxy)-methane and 1,4-bis-((4&#39;,4&#34;-dihydroxytriphenyl)-methyl)-benzene. Some of the other trifunctional compounds are 2,4-dihydroxy-benzoic acid, trimesic acid, cyanuric chloride and 3,3-bis-(4-hydroxyphenyl)-2-oxo-2,3-dihydroindole. 
     Among the resins suitable in the practice of the invention are included phenolphthalein-based polycarbonate, copolycarbonates and terpolycarbonates such as are described in U.S. Pat. Nos. 3,0Z36,036 and 4,210,741, both incorporated by reference herein. 
     The ultraviolet stabilizer in the present context is a halogen substituted benzotriazole having the general formula ##STR3## wherein hal denotes chlorine or bromine, 
     R 1  denotes a linear C 1  -C 10  alkyl group, a tertiary butyl radical or an aralkyl radical and where 
     R 2  is R 1 , preferably a C 1  -C 10  alkyl radical. 
     The preferred embodiment is represented by the formula below ##STR4## It is available commercially from Ciba-Geigy as Tinuvin®326, chemically termed 2-(3&#39;-tert-butyl-2&#39;-hydroxy-5&#39;-methylphenyl)-5-chlorobenzotriazole. Tinuvin 326 is a light yellow crystalline powder having a melting point of 140°-141° C. It appears that the thermal and light stability of the stabilizer of the present invention is attributable to an internal chelate bonding of the pnenolic hydoxyl and the benzotriazole ring. 
     Further, although the precise mechanism operating in the invention is not entirely clear, the experiments leading up to the invention strongly suggest the importance of the halogen substitution in imparting the stability in the present context. The dissociation constant of Tinuvin 326 is about 13 (in 80% aqueous dioxane) rendering the stabilizer relatively less affected by alkalies. The absorption maxima of Tinuvin 326, in chloroform, are 312 NM and 350 NM and the specific extinction coefficients -E- are 46 and 50. In methanol the absorptive maxima values are 298 NM and 343 NM and the specific extinction coefficients -E- are 47 and 51. A further characterization of the preferred stabilizer of the invention is found in Ciba-Geigy Corporation&#39;s bulletin A-2701M119A entitled &#34;Tinuvin 326; Ultraviolet Light Absorber for Plastics and Coatings&#34;, which document is incorporated herein by reference. 
     In the preparation of UV-stable compositions in accordance with the invention, a stabilizing amount, i.e. an amount sufficient to render the polycarbonate composition fairly non-transparent to UV light is added to the resin and the composition processed in accordance with known procedures in the polycarbonate art. Preferably, the amount of the stabilizer is in the range of about 0.05 to about 0.5 percent, more preferably the range is about 0.3 to about 0.4 percent, relative to the weight of the composition. Most preferably, for opthalmic lens applications, the amount of Tinuvin 326 is about 0.05 to about 0.3 percent by weight. The most preferable range of stabilizer addition for safety goggle lens applications is about 0.1 to about 0.5 percent by weight. 
     In one method of preparing the compositions of the invention, the components are dry blended until the additive practically coats the polycarbonate granules. The thus coated granules are then extruded in a conventional extruder and pelletized. Incorporating the stabilizer of the invention may also be carried out by adding it directly to the polycarbonate melt via, for instance, a DV extruder. Further processing of the pellets such as by injection molding will produce a polycarbonate product having an excellent resistance to UV-degradation and be at least substantially opaque to transmission of UV radiation in the 275-400 MN range. 
     The polycarbonate compositions thus described may contain further agents known in the relevant art for their utility. These include mold release agents, heat stabilizers and plasticizers as well as dyes and pigments, etc. The stabilized compositions are especially useful for applications in the opthalmic and optical lens field as well as for sports and recreation eyewear and are useful for the preparation of films, fibers, coatings, lacquers and variously shaped articles. 
     The invention is further illustrated but is not intended to be limited by the following examples where all parts and percentages are by weight unless otherwise specified. 
    
    
     EXAMPLES 
     Examples 1-16 
     Compositions containing prior art UV-stabilizers were compared to the composition of the invention. The optical and rheological characteristics were determined for compositions containing a polycarbonate resin--a homopolycarbonate based on bisphenol A--(Merlon M-40 from Mobay Chemical Corporation) and about 0.3% of the indicated UV-stabilizer. A phosphorous containing thermal stabilizer added to each of the compositions (0.075%) has no criticality in the present context. The compositions were extruded (Werner-Pfleiderer twin screw extruder) at 255°-265° C. The injection moldings of these and the remaining examples were carried out under either of the conditions which are noted below: 
     
         ______________________________________3 oz. Farrel______________________________________Standard Temperature:               nozzle - 290° C.               front - 295° C.               mid - 295° C.               back - 295° C.Gate-to-gate time:  80 mil disc - 30 sec.(no purge between shots)               l00 mil disc - 35 sec.               250 mil disc - 55 sec.               500 mil disc - 7 min.High Temperature:   nozzle - 270° C.               front - 370° C.               mid - 370° C.               back - 370° C.Gate-to-gate time:  l00 mil disc - 56.5 sec.(no purge between shots)______________________________________ 
    
     The extruded recipes were molded into 3&#34; discs of 0.100&#34; thickness. Pellet and part melt flow rates and the optical properties of the compositions were determined and the results are summarized below (Tables I and II). 
     
                                           TABLE I__________________________________________________________________________Optical Properties of Polycarbonate Compositions.sup.(1)Containing 0.3% UV Stabilizers (Visible Region)                              % TransmissionExampleUV-Stabilizer.sup.(2)        % Transmission                Yellowness Index                         % Haze                              @ 400 NM__________________________________________________________________________1    Cyasorb 5411        85.7    2.0      2.4  57.02    Tinuvin P        85.6    1.8      2.1  57.03    Tinuvin 350        85.7    2.6      1.8  30.04    Tinuvin 234        35.3    2.3      2.3  28.05    Uvinul D-49        83.8    17.0     1.7  50.06    Tinuvin 326        86.1    4.7      1.8  ˜0.07    Tinuvin 327        85.9    3.7      1.9  0.58    Tinuvin 622        85.0    3.7      2.2  71.0**__________________________________________________________________________ .sup.(1) molded at 550° F. .sup.(2) The chemical structures of the UVstabilizers are noted below. **Distorted UV scan 
    
     
         1. Cyasorb 5411 ##STR5##2(2-hydroxy-5-t-octylphenyl)benzotriazole2. TINUVIN P ##STR6##2(2&#39;-hydroxy-5&#39;-methylphenyl)benzotriazole3. TINUVIN 350 ##STR7##2(3&#39;-sec-butyl-5&#39;-t-butyl-2&#39;-hydroxyphenyl) benzotriazole4. TINUVIN 234 ##STR8##2(3&#39;,5&#39;-bis(1-methyl-1-phenylethyl)-2&#39;-hydroxyphenyl) benzotriazole5. UVINUL ® D-49 ##STR9##2,2&#39;-dihydroxy-4,4&#39;-dimethoxy-benzophenone6. TINUVIN 326 ##STR10##2(3&#39;-t-butyl-2&#39;-hydroxy-5&#39;-methylphenyl)-5-chlorobenzotriazole7. TINUVIN 327 ##STR11##2(3&#39;,5&#39;-di-t-butyl-2&#39;-hydroxyphenyl)-5-chlorobenzotriazole8. TINUVIN 622 ##STR12##succinate polymer with 4-hydroxy-2,2,6,6,-tetramethyl-1-piperidineethanolA second series of compositions identical to the above was similarlyprepared and molded except that the molding temperature was about700° F. 
    
     
         TABLE II__________________________________________________________________________Optical Properties of Polycarbonate Composition.sup.(1)Containing 0.3% UV-Stabilizer (Visible Region)                               % TransmissionExampleUV-Stabilizer.sup.(2)         % Transmission                 Yellowness Index                          % Haze                               @ 400 NM__________________________________________________________________________ 9   Cyasorb 5411         84.9    6.1      2.0  55.010   Tinuvin P         84.8    5.7      2.2  62.011   Tinuvin 350         84.2    8.1      1.9  35.012   Tinuvin 234         84.5    6.0      2.3  28.013   Uvinul D-49         73.4    40.7     1.8  34.0**14   Tinuvin 326         85.6    7.2      1.9  0.015   Tinuvin 327         85.0    7.2      2.2  0.516   Tinuvin 622         22.9    137.0    4.1  0.0**__________________________________________________________________________ .sup.(1) Molded at 700° F. .sup.(2) The chemical structures of the UVstabilizers are noted below. **Distorted UV scan 
    
     The transmission values were determined using a spectrophotometer (Cary 219) at 550 NM in accordance with ASTM D-1003. Haze values were determined in accordance with ASTM D-1003. Yellowness Index was determined in accordance with ASTM D-1925. 
     The experience with the UV stabilizers has shown that Cyasorb 5411 does not provide the desirable level of UV absorption as shown by the values of transmission at 400 NM. It was also noted that this stabilizer appears to react with the polycarbonate resin at elevated temperature. Tinuvin 350 provides sufficient absorption at 400 NM. However in order to obtain 0% transmission, a relatively large amount of Tinuvin 350 is required which amount tends to cause processing difficulties, i.e. plate-out. Uvinul D-50 and American Cyanamid&#39;s Cyasorb UV24 were found to be unstable at 700° F. Tinuvin 622 was determined to be incompatible with polycarbonates. While the stabilizer of the present invention is structurally similar to Tinuvin 327 and to Tinuvin 350, it was found that its efficacy is greater since smaller amounts thereof are required for obtaining the desired properties of the compositions. 
     Melt flow rates of the compositions in accordance with the invention were determined and compared to the corresponding rates of prior art counterparts (Table III). The rates were determined in accordance with ASTM D-1238, 300° C., 1200 gm. 
     
                                           TABLE III__________________________________________________________________________EXAMPLE 17 (MELT FLOW RATES)     0.1% STABILIZER*                  0.3% STABILIZER      0.75% STABILIZER*UV-STABILIZER     Pellets          Parts @ 550° F.                  Pellets                       Parts @ 550°                               Parts @ 700° F.                                       Pellets                                            Parts @ 550°__________________________________________________________________________                                            F.Cyasorb 5411     5.6  7.7     7.4  7.5     10.8    6.0  6.3Tinuvin P 5.8  7.8     7.4  7.6     11.2    6.9  6.8Tinuvin 350     5.4  7.0     7.1  7.9     10.3    5.6  6.4Tinuvin 234     5.5  7.0     7.2  7.9      9.8    5.5  5.9Uvinul D-49     --   --      7.6  8.2     15.6    --   --Tinuvin 326     5.8  7.2     7.8  7.2      6.3    5.8  5.8Tinuvin 327     6.3  7.0     7.3  7.8      8.6    5.5  6.1Tinuvin 622     --   --      10.7 12.4    71.3    --   --__________________________________________________________________________ *The extrusions of compositions containing 0.1 and 0.75% of UV stabilizer were carried out in MPM 2&#34;, single crew extruder at a temperature range o 270-275° C. 
    
     Examples 18-25 
     A further comparison between the present stabilizer and its prior art counterparts has been carried out and the findings are presented below. A thermogravimetric analysis, isothermal at 300° C. (seal in pan with pinhole) showed that the relative weight loss due to evaporation of these stabilizers is a function of their time duration at that temperature. 
     
                       TABLE IV______________________________________THERMOGRAVIMETRY OF UV-STABILIZERS            % Weight LossExample    Stabilizer  5 minutes                           10 minutes______________________________________18         Cyasorb 5411                  51       10019         Tinuvin P    94*     --20         Tinuvin 350 57        100**21         Tinuvin 234   2.5     822         Uvinul D-49 50       7923         Tinuvin 326 51       9224         Tinuvin 327 51       9125         Tinuvin 622  4       10______________________________________ *After 3 minutes **100% loss occurred after 8.5 minutes 
    
     Examples 26-55 
     Further compositions within the scope of the invention were prepared--standard molding temperature--and their properties determined and compared to prior art compositions, The concentration of the stabilizers was varied from 0.1% to 0.75% and the physical properties (% Transmission, Yellowness Index, Haze and Transmission at 400 NM) were measured on discs of different thicknesses as noted in Tables V and VI. 
     
                                           TABLE V__________________________________________________________________________OPTICAL DATA IN VISIBLE REGION               % Transmission                           Yellowness Index                                       % HazeExampleConcentration        UV-Stabilizer               .08&#34;                  .10&#34;                     .25&#34;                        .50&#34;                           .08&#34;                              .10&#34;                                 .25&#34;                                    .50&#34;                                       .08&#34;                                          .10&#34;                                             .25&#34;                                                .50&#34;__________________________________________________________________________26   0.1%    Cyasorb 5411               87.4                  86.9                     82.5  1.4                              1.0                                 .80   .42                                          .68                                             1.227   0.1%    Tinuvin P               87.2                  86.9                     82.4  1.6                              1.1                                 .88   .44                                          .71                                             1.028   0.1%    Tinuvin 350               87.1                  86.9                     82.1  2.2                              1.3                                 1.6   .54                                          .73                                             1.429   0.1%    Tinuvin 234               87.5                  86.8                     82.6  1.2                              1.5                                 1.3   .45                                          .44                                             .8430   0.1%    Tinuvin 326               87.5                  87.0                     82.6  2.3                              2.4                                 3.6   .38                                          .37                                             .7931   0.1%    Tinuvin 327               87.5                  87.1                     82.5  1.8                              1.9                                 2.3   .43                                          .44                                             1.032   0.3%    Cyasorb 5411               86.6                  85.7                     80.8  1.8                              2.0                                 2.7   .98                                          2.4                                             2.433   0.3%    Tinuvin P               86.8                  85.6                     81.0  1.9                              1.8                                 2.8   1.0                                          2.1                                             2.234   0.3%    Tinuvin 350               86.9                  85.7                     80.8  2.2                              2.6                                 4.2   .89                                          1.8                                             2.335   0.3%    Tinuvin 234               86.5                  85.3                     79.4  2.2                              2.3                                 4.1   1.4                                          2.3                                             3.836   0.3%    Tinuvin 326               87.2                  86.1                     81.1                        71.6                           4.1                              4.7                                 7.7                                    14.7                                       .84                                          1.8                                             2.6                                                5.137   0.3%    Tinuvin 327               87.1                  85.9                     80.9                        70.6                           3.4                              3.7                                 6.4                                    11.1                                       .86                                          1.9                                             2.7                                                5.438   0.5%    Cyasorb 5411               87.3                  86.3                     81.0  1.6                              2.4                                 2.6   .65                                          .70                                             1.639   0.5%    Tinuvin P               87.1                  86.1                     80.2  1.8                              2.1                                 3.3   .74                                          .80                                             1.940   0.5%    Tinuvin 350               87.2                  86.4                     80.8  2.3                              2.5                                 4.3   .68                                          .69                                             1.741   0.5%    Tinuvin 234               87.2                  86.4                     81.1  2.2                              2.6                                 2.9   .55                                          .66                                             1.742   0.5%    Tinuvin 326               87.0                  86.2                     80.5                        70.6                           5.7                              6.4                                 10.2                                    15.6                                       .71                                          .70                                             1.5                                                4.343   0.5%    Tinuvin 327               87.2                  86.5                     81.3                        72.4                           3.9                              4.6                                 7.8                                    12.9                                       .92                                          .62                                             1.2                                                2.844   0.75%   Cyasorb 5411               86.9                  86.2                     81.2  2.5                              2.4                                 3.3   .60                                          .72                                             1.645   0.75%   Tinuvin P               86.4                  85.6                     79.4  2.8                              3.1                                 5.5   .84                                          1.1                                             2.646   0.75%   Tinuvin 350               86.7                  86.0                     80.2  3.2                              3.5                                 5.5   .73                                          .91                                             2.047   0.75%   Tinuvin 234               86.9                  86.3                     80.9  3.0                              2.8                                 3.9   .62                                          .75                                             1.848   0.75%   Tinuvin 326               86.6                  85.9                     78.7  7.1                              8.5                                 13.3  .72                                          .82                                             2.749   0.75%   Tinuvin 327               87.1                  86.4                     80.6  5.0                              6.1                                 10.6  .64                                          .68                                             1.8__________________________________________________________________________ 
    
     
                                           TABLE VI__________________________________________________________________________% TRANSMISSION AT 400 NM       0.1%     0.3%        0.5%        0.75%ExampleUV-Stabilizer       .08&#34;          .10&#34;             .25&#34;                .08&#34;                   .10&#34;                      .25&#34;                         .50&#34;                            .08&#34;                               .10&#34;                                  .25&#34;                                     .50&#34;                                        .08&#34;                                           .10&#34;                                              .25&#34;__________________________________________________________________________50   Cyasorb 5411       76 75 61 60 57 28    55 45 18    42 35 1251   Tinuvin P       75 72 54 62 57 36    53 46 20    29 27 552   Tinuvin 350       63 60 35 40 30 7     30 17 3     12 9  .553   Tinuvin 234       63 59 37 40 28 10    26 18 2     10 6  .254   Tinuvin 326       8.5          5.5             .2 .4 .2 0  0  0  0  0  0  0  0  055   Tinuvin 327       20 14 1.0                1.2                   .5 0  0  .2 0  0  0  0  0  0__________________________________________________________________________ 
    
     Examples 56-61 
     Optical properties and color data were determined on moldings produced from the polycarbonate compositions of the invention, using Tinuvin 326 at various concentrations and at two different molding conditions as noted above. Table VII below indicates the properties of these compositions all of which included 0.075% of a thermal stabilizer having no critical effect on the present invention. 
     
                                           TABLE VII__________________________________________________________________________        STANDARD TEMPERATURE                        HIGH TEMPERATUREConcentration        % T @ Total Trans.                        % T @                             Total Trans.Example%       400 NM              Y, %   YI 400 NM                             Y, %   YI__________________________________________________________________________Thermal Stabilizer - #156   0.05    18    86.0   2.0                        22   83.5   6.757   0.10    5     85.6   2.4                        10   84.5   5.958   0.30    0     86.0   4.6                         0   85.2   7.4Thermal Stabilizer - #259   0.05    12    85.7   3.0                        12   85.7   4.960   0.10    6     86.0   3.3                         8   85.9   5.061   0.30    0     86.1   5.1                         0   85.5   7.6__________________________________________________________________________ 
    
     Although the invention has been described in detail in the foregoing for the purpose of illustration, it is to be understood that such detail is solely for that purpose and that variations can be made therein by those skilled in the art without departing from the spirit and scope of the invention except as it may be limited by the claims.