Abstract:
The density of rigid foamed articles made by the thermal decomposition of a blowing agent in a vinyl chloride polymer is reduced by the use of a tin based blowing agent activator(s). The tin based activator also reduces the activation temperature of a chemical blowing agent, allowing for more optimal evolution of gas during plastic processing. Dibutyl tin oxide or tin maleates are superior activators of vinyl chloride polymer blowing agents.

Description:
CROSS-REFERENCE TO RELATED APPLICATIONS 
     This application is a national stage application under 35 U.S.C. §371 of PCT/US2009/057096, filed Sep. 16, 2009, which claims benefit to U.S. Provisional Application No. 61/097,961, filed on Sep. 18, 2008, all of which are hereby incorporated by reference. 
    
    
     FIELD OF THE INVENTION 
     The present invention relates to the preparation of cellular vinyl chloride polymers. It relates more particularly to certain tin compounds that are superior activators for blowing agents employed in the preparation of cellular vinyl chloride polymers. 
     BACKGROUND OF THE INVENTION 
     One important utility for vinyl chloride resins is in the preparation of rigid foamed articles. The articles are manufactured by known methods such as extrusion of a blend of the resin and additives with a suitable chemical blowing agent and choosing the processing temperature such that it is above the decomposition temperature of the blowing agent. The bubbles of gas evolved by the blowing agent are entrapped within the molten resin, thereby forming a cellular structure that are commercially useful articles such as pipe, decorative molding, trimboard, and structural siding. Usually, the polymer is melted at a temperature between 150° and 200° C. and it is necessary to include a stabilizer in the formulation for the purpose of eliminating or at least minimizing the heat-induced discoloration of the vinyl chloride polymer which would otherwise occur at these temperatures. Also, when the decomposition temperature of the blowing agent is much above the processing temperature, activators are employed to hasten the decomposition of the blowing agent and/or lower the blowing agent decomposition temperature. The combination of a blowing agent and an activator increases both the degree and the rate of blowing agent decomposition and potentially the process window of the decomposition. The resultant larger volume of gas generated is desirable, since it reduces the amount of blowing agent required, or can result in lower density foam at similar blowing agent use levels. 
     It is known that a variety of organotin compounds, particularly dibutyltin derivatives of mercaptocarboxylic acid esters, will impart useful levels of heat stability to vinyl chloride polymers. It is also known that organotin chlorides work well by themselves or in combination with organotin carboxylates as activators for typical blowing agents such as azodicarbonamides, 5-phenyl tetrazole, and benzene sulfonylhydrazide. 
    
    
     DETAILED DESCRIPTION OF THE INVENTION 
     The present invention relates to the use of certain tin compounds as activators for blowing agents employed in the preparation of cellular vinyl chloride polymers. The activators of the present invention effectively lower the blowing agent decomposition temperature and increase the rate of blowing agent decomposition thereby enhancing the effect of the blowing agent, which could be evidenced by increased foam thickness and decreased foam specific gravity. The tin compound activators of the present invention also can replace, augment or reduce the need for commonly used additives such as ZnO and oxybisbenzenesulfonyl hydrazide (OBSH). ZnO and OBSH, which are often added to lower the activation temperature of exothermic blowing agents. The tin compounds of the present invention can also serve as a stabilizer in concert with or in place of other stabilizers in the cellular vinyl chloride polymer composition. When the tin compounds are serving a “dual” purpose of activator and stabilizer, higher concentration would typically be used. All percentages herein are by weight unless specified otherwise. 
     Vinyl chloride polymers are made from monomers consisting of vinyl chloride alone or a mixture of monomers comprising, preferably, at least about 70% by weight based on the total monomer weight of vinyl chloride. They are exemplified by copolymers of vinyl chloride with from about 1 to about 30% of a copolymerizable ethylenically unsaturated material such as vinyl acetate, vinyl butyrate, vinyl benzoate, vinylidene chloride, diethyl fumarate, diethyl maleate, other alkyl fumarates and maleates, vinyl propionate, methyl acrylate, 2-ethylhexyl acrylate, butyl acrylate and other alkyl acrylates, methyl methacrylate, ethyl methacrylate, butyl methacrylate and other alkyl methacrylates, methyl alpha-chloroacrylate, styrene, trichloroethylene, vinyl ethers such as vinyl ethyl ether, vinyl chloroethyl ether and vinyl phenyl ether, vinyl ketones such as vinyl methyl ketone and vinyl phenyl ketone, 1-fluoro-2-chloroethylene, acrylonitrile, chloroacrylonitrile, allylidene diacetate and chloroallylidene diacetate. Typical copolymers include vinyl chloride-vinyl acetate (96:4 sold commercially as VYNW), vinyl chloride-vinyl acetate (87:13), vinyl chloride-vinyl acetate-maleic anhydride ((86:13:1), vinyl chloride-vinylidene chloride (95:5); vinyl chloride-diethyl fumarate (95:5), and vinyl chloride 2-ethylhexyl acrylate (80:20). 
     The vinyl chloride polymers constitute the major portion of the compositions of this invention. Thus, they amount to from about 70% to about 95% by weight of the total weight of the unfoamed compositions of this invention. 
     The blowing agent may be any one or a mixture of those commonly used for foaming PVC, including azobisformamide (also commonly known as azodicarbonamide), 5-phenyl tetrazole, benzene sulfonyl hydrazide, citric acid, sodium bicarbonate and mixtures thereof. The concentration of the blowing agent is typically from about 0.1 to about 5.0% by weight of the total composition prior to the formation of foam. 
     The blowing agent activator of the present invention comprises a tin compound including but not limited to dibutyl tin oxide and tin maleates. The activator helps the nitrogen-containing, carbon dioxide containing, and other decomposition type blowing agent to decompose faster and to generate more gases. The activator lowers the temperature for the decomposition of the blowing agent as well as provides for more complete decomposition of the blowing agent. The effect of the blowing agent activator is independent of whether it is added to the vinyl chloride polymer as an aqueous solution, as part of a stabilizer package, as part of a lubricant package, or as part of an additive package. A variety of conventional molding and extruding techniques may be used to form the rigid, cellular vinyl chloride polymers of this invention into pipe or any desired profile or a sheet. 
     Examples of suitable activators include tin salts of monocarboxylic acids and organo-tin stabilizers. Examples of such organo-tin stabilizers include without limitation: dibutyltin dilaurate, dibutyltin maleate, di(n-octyl) tin maleate, dibutyltin bis(lauryl mercaptide), dibutyltin, S,S-bis(isooctyl thioglycoate), dibutyltin β-mercaptoproprionate, di-n-octyltin S,S-bis(isooctyl thioglycolate), dibutylin tin oxide, dibutyl tin dilaurate, di-n-octyltin β-mercaptoproprionate, the reaction product of maleic anhydride, stearyl alcohol, water, and dibutyl tin oxide and mixtures thereof. The activator may be included in any amount useful to cause the activation. Generally, when serving only as an activator, from about 0.001 to 5 wt % of activator may be included in the chemical blowing agent composition comprising the chemical blowing agent and the blowing agent activator. However, when serving as a combination tin stabilizer and activator, the activator can be used at concentrations of from about 0.01 wt % to 10 wt % of the blowing agent composition. The blowing agent composition can be used at concentrations of from about 0.1 wt % to 10 wt % of the overall PVC composition. Alternatively, the activator/stabilizer can be combined directly with the PVC resin at concentrations of from about 0.1-10.0 parts per 100 parts (phr) PVC resin, typically in the 2-3 phr range. The activator particles can range in size from about 5 microns to about 500 microns with a particle size range of from about 10 to 100 being preferred. 
     An exemplary tin maleate material can be prepared via the reaction of stearyl alcohol and a stoichiometric excess of maleic anhydride. The reaction product is then reacted with a stoichiometric excess of dibutyl tin oxide to provide a reaction product containing, in part, tin maleate materials, which can be used without further processing. 
     Vinyl chloride polymer foam compositions typically include a stabilizer in the un-foamed compositions of from about 0.1 to about 10% by weight. They may be incorporated into the compositions by admixing in an appropriate mill or mixer or by any of the other well-known methods that provide for the uniform distribution of the stabilizers throughout the composition. 
     In addition to the blowing agent and activator compositions, the vinyl chloride polymer compositions of the present invention may contain additives for the purpose of increasing resistance to oxidation, flame retardancy and impact resistance of the polymer. Pigments, fillers, dyes, ultraviolet light absorbing agents and the like may also be present. Conventional processing aids such as lubricants and acrylic resins can also be present. 
     Acrylic resins are employed in vinyl chloride polymer foam compositions as processing aids to improve melt elasticity and strength and to prevent the collapse of the cellular structure during processing. The amount of the acrylic resin can vary from about 2 to about 18 parts per hundred parts of the vinyl chloride polymer. The molecular weight of the acrylic resin may be in the range of from 300,000 to 7,500,000 but those having the higher molecular weights are preferred; resins having a molecular weight of 3,000,000 and higher are particularly preferred. 
     Antioxidants may be used in the vinyl chloride polymer foam compositions of the present invention. Typical antioxidants include phenols, particularly those wherein the positions adjacent to the carbon atom bearing the hydroxyl radical contain alkyl radicals as substituents. Phenols wherein this alkyl radical is sterically bulky, e.g. a tertiary butyl radical, are preferred. 
     A small amount, usually not more than 0.3%, of a metal release agent, such as an oxidized polyethylene, also can be included in the vinyl chloride polymer foam compositions of the present invention. 
     A high molecular weight process aid may be included in the foamable composition. High molecular weight process aids are used to provide melt elasticity or melt strength to the polymer melt formed within the extruder and high integrity of the foam cell walls during extrusion. High molecular weight process aids can be acrylic process aids or copolymers of styrene and acrylonitrile. Suitable high molecular weight process aids include those high molecular process aids known in the art. Acrylic process aids which can be used in the present invention include thermoplastic polymethyl methacrylate homo or copolymers with weight average molecular weights greater than 1,000,000; hard, glassy copolymers of styrene and acrylonitrile having a glass transition temperature in excess of 60° C. and a dilute solution viscosity greater than 1.5 as measured in methylethyl ketone at 4% concentration. Copolymers of styrene and an unsaturated nitrile containing more than 50% of said styrene and 10 to 40% of said nitrile are examples of the styrene acrylonitrile process aids. Preferably 10 parts of the styrene acrylonitrile copolymer are added to the composition per 100 parts of PVC polymer. Examples of suitable acrylic process aids include poly(methyl methacrylate). Generally, from about 2 to about 20 parts of the acrylic process aid are added per 100 parts of PVC. 
     The foamable composition preferably includes lubricants or lubricant mixtures as are known to those in the art. Suitable lubricants include for example various hydrocarbons such as paraffin; paraffin oils; low molecular weight polyethylene; oxidized polyethylene; amide waxes, metal salts of fatty acids; esters of fatty acids such as butyl stearate; fatty alcohols, such as cetyl, stearyl or octadecyl alcohol; metal soaps such as calcium or zinc salts of oleic acid; fatty amides of organic acids; polyol esters such ad glycerol monostearate, hexaglycerol distearate and mixtures thereof. 
     Examples of possible fatty acids to be used include but are not limited to stearic acid and calcium stearate. Examples of fatty amides of organic acids include stearamide, and ethylene-bis-stearamide. Since several lubricants can be combined in countless variations, the total amount of lubricant can vary from application to application. Optimization of the particular lubricant composition is not within the scope of the present invention and can be determined easily by one of ordinary skill in the art. Generally from about one to about ten parts of lubricant are added to the foamable composition per one hundred parts of PVC polymer. 
     The foamable composition preferably includes a metal release agent. An example of a metal release agent is a terpolymer of methylmethacrylate, styrene and butyl acrylate. Preferably 2.0 parts of this terpolymer per 100 parts of PVC polymer are added to the lubricant. 
     In addition, enhancing ingredients useful to enhance either the processing of PVC or the PVC foam product can be included in the foamable composition. These include for example but not limited to pigments, such as titanium dioxide, carbon black, and iron oxide, fillers such as calcium carbonate, silica, talc and the like, reinforcing agents such as glass fibers, and graphite fibers or glass spheres, other processing aids, impact modifiers, and alloying polymers and the like, antioxidants, antistatic agents. These enhancing ingredients can be added in an amount effective for the intended purpose. The amount and use would be within the purview of one of ordinary skill in the art and does not form part of this invention. 
     EXAMPLE 1 
     PVC Foam formulations were blended using a high intensity mixer, then cooled and allowed to fully equilibrate at ambient temperature. The formulations were then processed in a Cincinnati Milacron conical twin screw extruder having a 22/1 length to diameter ratio and employing an 8″ wide jacketed sheet die. Pelletized chemical blowing agent was added to the extruder&#39;s feed throat through a calibrated gravimetric feeder. From the die, the PVC melt was allowed to freely expand/foam, commonly called the “Free Foam” extrusion process. The Foam Sheet was routed through three chilled rolls, in order to give the foam a skin-type surface. From there, the foam air-cooled while being routed over roller tables. Finally, the foam reached a puller, operated at a static speed, followed by a cutting table. The foam was extruded using the conditions stated in Table 1. 
     
       
         
               
               
               
             
               
               
             
           
               
                 TABLE 1 
               
               
                   
               
             
             
               
                 Barrel Zone (° F.) 
                 1 
                 355 
               
               
                   
                 2 
                 355 
               
               
                   
                 3 
                 375 
               
               
                   
                 4 
                 375 
               
               
                 Adaptor Zones (° F.) 
                 1 
                 362 
               
               
                   
                 2 
                 362 
               
               
                 Die Zone (° F.) 
                 3-edges 
                 360 
               
               
                   
                 4-side 
                 360 
               
               
                   
                 5-center 
                 345 
               
               
                   
                 6-side 
                 360 
               
             
          
           
               
                 Screw Oil (° F.) 
                 355 
               
               
                 Die Jacket (° F.) 
                 350 
               
               
                 Screw RPM 
                 25 
               
               
                 Die Gap (inches) 
                 0.260 
               
               
                 Roll Stack Temp (° F.) 
                 95 
               
               
                 Line Speed (ft/min.) 
                 1.5 
               
               
                   
               
             
          
         
       
     
     The formulations tested are listed in Table 2. Within each group, the formulations are similar with the exception of the activator and stabilizer. Testing has shown that tin stabilizer concentrations within the range tested here does not statistically affect the key parameters measured here, namely foam specific gravity and sheet thickness. The extrusion results show that the tin maleate stabilizer/activator and the tin oxide activator to have a beneficial effect on specific gravity and sheet thickness. 
     
       
         
               
               
               
               
               
             
               
               
               
               
               
               
               
               
               
               
               
             
               
               
               
               
               
               
               
               
               
               
               
               
             
               
               
               
               
               
               
               
               
               
               
               
             
               
               
               
               
               
               
               
               
               
               
               
             
               
               
               
               
               
               
               
               
               
               
               
               
             
           
               
                   
                 TABLE 2 
               
             
             
               
                   
                   
               
               
                   
                 Group 1 
                 Group 2 
                 Group 3 
                 Group 4 
               
             
          
           
               
                 Formulation 
                 Run# 
                 A 
                 B 
                 C 
                 D 
                 E 
                 F 
                 G 
                 H 
                 I 
               
               
                   
               
             
          
           
               
                 PVC 
                 K = 57 Resin 
                  Start* 
                 100.00 
                 100.00 
                 100.00 
                 100.00 
                 100.00 
                 100.00 
                 100.00 
                 100.00 
                 100.00 
               
               
                 Lubricants 
                 Calcium Stearate 
                  66 C.* 
                 0.70 
                 0.70 
                 0.70 
                 0.70 
                 0.70 
                 0.70 
                 0.70 
                 1.30 
                 1.30 
               
               
                   
                 165 MP Wax 
                 66 C. 
                 1.00 
                 1.00 
                 1.00 
                 1.00 
                 1.00 
                 1.00 
                 1.00 
                 1.00 
                 1.00 
               
               
                   
                 Oxidized Polyethylene 
                 66 C. 
                 0.20 
                 0.20 
                 0.20 
                 0.20 
                 0.20 
                 0.20 
                 0.20 
                 0.20 
                 0.20 
               
               
                 Stabilizer/ 
                 Methyl Tin Stabilizer 
                 Start 
                 3.00 
                 — 
                 — 
                 — 
                 3.00 
                 — 
                 — 
                 — 
                 2.00 
               
               
                 Activator 
                 Butyl Tin Stabilizer 
                 Start 
                 — 
                 2.14 
                 — 
                 2.14 
                 — 
                 2.14 
                 — 
                 3.20 
                 — 
               
               
                   
                 Tin Maleate Stabilizer/Activator 
                 Start 
                 — 
                 — 
                 3.00 
                 — 
                 — 
                 — 
                 3.00 
                 — 
                 — 
               
               
                   
                 Tin Oxide Activator 
                 98 C. 
                 — 
                 0.50 
                 — 
                 — 
                 0.50 
                 — 
                 — 
                 — 
                 0.50 
               
               
                 Acrylic 
                 High MW Acrylic Process Aid 
                 72 C. 
                 10.00 
                 10.00 
                 10.00 
                 7.00 
                 7.00 
                 7.00 
                 10.00 
                 7.00 
                 7.00 
               
               
                   
                 Low MW Acrylic Process Aid 
                 72 C. 
                 2.00 
                 2.00 
                 2.00 
                 2.00 
                 2.00 
                 2.00 
                 2.00 
                 2.00 
                 2.00 
               
               
                 CaCO3 
                 nominal 0.7 um particle size 
                 88 C. 
                 5.00 
                 5.00 
                 5.00 
                 — 
                 — 
                 5.00 
                 5.00 
                 — 
                 — 
               
               
                   
                 nominal 0.07 um particle size 
                 88 C. 
                 — 
                 — 
                 — 
                 5.00 
                 5.00 
                 — 
                 — 
                 5.00 
                 5.00 
               
             
          
           
               
                 Titanium Dioxide 
                 98 C. 
                 4.00 
                 4.00 
                 4.00 
                 4.00 
                 4.00 
                 4.00 
                 4.00 
                 4.00 
                 4.00 
               
               
                 Pelletized CBA (nominal phr) 
                 On-line 
                 0.85 
                 0.85 
                 0.85 
                 0.85 
                 0.85 
                 0.65 
                 0.65 
                 0.65 
                 0.65 
               
             
          
           
               
                 Results 
                 Specific Gravity in water (ASTMD792) 
                 0.734 
                 0.661 
                 0.610 
                 0.705 
                 0.707 
                 0.783 
                 0.679 
                 0.799 
                 0.751 
               
             
          
           
               
                   
                 Sheet Thickness 
                 inches 
                 0.724 
                 0.762 
                 0.791 
                 0.691 
                 0.708 
                 0.687 
                 0.781 
                 0.646 
                 0.663 
               
               
                   
                   
               
               
                   
                 *Addition Temperature to high intensity blender 
               
             
          
         
       
     
     EXAMPLE 2 
     The effect of tin activators was tested via gas yield testing. Gas yield testing is a common test within the chemical blowing agent (CBA) industry. It is used to measure the amount of gas evolved by CBA products and the temperature at which the gas begins to evolve, commonly referred to as activation temperature. In this test, different loadings of tin activators were mixed with a neat exothermic chemical blowing agent, azodicabonamide (CAS#123-77-3). The well-mixed sample was placed in a sample vial within a gas yield analyzer. This equipment heated the vial at a constant rate, while continuously tracking sample temperature and gas evolution from the sample. 
     As shown below in TABLE 3, when compared to the control, both the tin maleate and tin oxide have a clear effect on reducing the activation temperature of the CBA. 
     
       
         
               
               
               
             
               
               
               
               
               
             
               
               
               
               
               
               
             
           
               
                 TABLE 3 
               
             
             
               
                   
               
               
                   
                 Composition 
                   
               
             
          
           
               
                   
                 % Tin 
                 % Tin 
                 % Neat 
                   
               
               
                   
                 Maleate 
                 Oxide 
                 Azo. 
                 Activation Temp 
               
               
                   
               
             
          
           
               
                 Nominal 
                 100 
                 100-200 
                   
                 deg C. 
                 Delta vs. 
               
               
                 Particle Size 
                 microns 
                 microns 
                   
                   
                 Control 
               
               
                 Control 
                   0% 
                   
                 100 
                 204 
                 N/A 
               
               
                   
                 0.5% 
                   
                 99.5% 
                 187 
                 (17) 
               
               
                   
                 1.0% 
                   
                 99.0% 
                 182 
                 (22) 
               
               
                   
                 5.0% 
                   
                 95.0% 
                 183 
                 (21) 
               
               
                   
                 10.0%  
                   
                 90.0% 
                 183 
                 (21) 
               
               
                   
                   
                 0.5% 
                 99.5% 
                 170 
                 (34) 
               
               
                   
                   
                 1.0% 
                 99.0% 
                 165 
                 (39) 
               
               
                   
                   
                 5.0% 
                 95.0% 
                 165 
                 (39) 
               
               
                   
                   
                 10.0% 
                 90.0% 
                 165 
                 (39) 
               
               
                   
                 5.0% 
                 5.0% 
                 90.0% 
                 177 
                 (27) 
               
               
                   
               
             
          
         
       
     
     This phenomena was also observed when a smaller particle size tin oxide was testing. As shown in TABLE 4, tin oxide works as an effective CBA activator over a variety of particle sizes. 
     
       
         
               
               
               
             
               
               
               
               
             
               
               
               
               
               
             
               
               
               
               
               
               
             
           
               
                 TABLE 4 
               
             
             
               
                   
               
               
                   
                 Composition 
                   
               
             
          
           
               
                   
                 % Tin B - 
                 % Neat 
                   
               
             
          
           
               
                   
                 Fine PSD 
                 Azo 
                 Activation Temp 
                   
               
               
                   
               
             
          
           
               
                   
                 Nominal 
                 D 50  = 
                   
                 deg C. 
                 Delta vs. 
               
               
                   
                 Particle 
                 12 um 
                   
                   
                 Std 
               
               
                   
                 Size 
                   
                   
                   
                   
               
               
                   
                 Control 
                 0.00% 
                 100.00% 
                 203 
                 N/A 
               
               
                   
                   
                 0.05% 
                 99.95% 
                 185 
                 (18) 
               
               
                   
                   
                 0.25% 
                 99.75% 
                 180 
                 (23) 
               
               
                   
                   
                 0.50% 
                 99.50% 
                 174 
                 (29) 
               
               
                   
                   
                 0.75% 
                 99.25% 
                 168 
                 (35) 
               
               
                   
                   
                 1.00% 
                 99.00% 
                 166 
                 (37) 
               
               
                   
               
             
          
         
       
     
     EXAMPLE 3 
     Tin oxide was used in a chemical blowing agent (CBA) composite which included an alternate activator/blowing agent, oxybisbenzenesulfonylhydrazide (OBSH, CAS#80-51-3). The use of the tin activator of the present invention may allow the use of a lower concentration of the alternate activator/blowing agent, that is exothermic in nature. This CBA composite also contained other tin-based stabilizer compounds, and a methyl tin mercaptide, known commercially as THERMOLITE® 161, available from Arkema Inc. The tin oxide-containing CBA in accordance with the present invention was evaluated in a PVC foam extrusion study. In this study, it was compared to a commercially available blowing agent that contained OBSH and azodicarbonamide to determine its effect on foam density and color development. 
     A common issue in the PVC Foam Industry is the yellowing of the foam article&#39;s core. This can be due to a variety of reasons, including self-heat from the molten foam, heat from the exothermic decomposition of a blowing agent or the exothermic decomposition of an activator, and by-products of blowing agent decomposition. If the decomposition of the blowing agent activates at a lower temperature, one potential outcome would be a decrease in exothermic heating of the PVC melt, and a potential to improve whiteness of the PVC article. Also, if the tin-based activator allows for a reduction in exothermic activator/blowing agent, one potential outcome would be a decrease in exothermic heating of the PVC melt and a decrease in activator/blowing agent decomposition byproducts, which could have a potential to improve whiteness of the PVC article. 
     TABLE 5 describes the PVC Foam formulation that was used. The formulation was processed on Cincinnati Milacron conical twin screw extruder, as described above in EXAMPLE 1. Several pelletized CBA&#39;s were tested. They were added to the extruder&#39;s feed throat via a calibrated volumetric feeder. The pelletized CBA&#39;s were added to ensure a constant CBA gas yield within the PVC Foam. The foam was extruded using the conditions stated in TABLE 6. 
     
       
         
               
               
               
             
               
               
               
             
           
               
                 TABLE 5 
               
               
                   
               
               
                   
                 Component 
                 phr 
               
               
                   
               
             
             
               
                   
               
             
          
           
               
                   
                 RPVC Resin (K57) 
                 100.0 
               
               
                   
                 Methyltin Heat Stabilizer 
                 2.0 
               
               
                   
                 Calcium Stearate 
                 0.7 
               
               
                   
                 165 MP Wax 
                 1.0 
               
               
                   
                 Oxidized Polyethylene 
                 0.2 
               
               
                   
                 High MW Acrylic Process Aid 
                 8.0 
               
               
                   
                 Low MW Acrylic Process Aid 
                 2.0 
               
               
                   
                 CaCO3 - Ultrafine, Treated 
                 5.0 
               
               
                   
                 Titanium Dioxide 
                 4.0 
               
               
                   
               
             
          
         
       
     
     
       
         
               
               
               
             
               
               
             
           
               
                 TABLE 6 
               
               
                   
               
             
             
               
                 Barrel Zones Temp 
                 1 
                 355 
               
               
                 (° F.) 
                 2 
                 355 
               
               
                   
                 3 
                 375 
               
               
                   
                 4 
                 375 
               
               
                 Adapter Zones Temp 
                 1 
                 362 
               
               
                 (° F.) 
                 2 
                 362 
               
               
                 Die Zones Temp 
                 3-edges 
                 360 
               
               
                 (° F.) 
                 4-side 
                 355 
               
               
                   
                 5-center 
                 359 
               
               
                   
                 6-side 
                 355 
               
             
          
           
               
                 Screw Oil (° F.) 
                 355 
               
               
                 Die Jacket Oil (° F.) 
                 348 
               
               
                 Screw RPM 
                 25 
               
               
                 % Screw Fill 
                 75% 
               
               
                 Die Gap (inch) 
                 0.260 
               
               
                 Roll Stack Temp (° F.) 
                 97 
               
               
                 Line Speed (ft/mini) 
                 1.5 
               
               
                 Vacuum (inches Hg) 
                 28 
               
               
                   
               
             
          
         
       
     
     PVC Foam processing of the tin oxide-containing CBA was similar to the other CBA&#39;s. Additionally, the foam density values for foam produced with the tin oxide-containing CBA was similar to foam produced with other CBA&#39;s. To simulate the slow cooling of a thick PVC Foam sample several samples of each PVC foam lot were put in a laboratory oven held at a constant 190° C., which approximates the processing temperature of the PVC foam. Then, every 15 minutes, one sample of each PVC foam lot was removed. The tin oxide-containing CBA performed demonstrably better at reducing color development, as evidenced in the color readings of the samples, as shown in TABLE 7. In TABLE 7, the whiteness is higher (higher Hunter L value), early yellowness is lower (lower Hunter B value) and overall color change is less (lower Delta E) with the tin oxide composition in accordance with the present invention vs. the control composition. 
     
       
         
               
               
               
               
             
               
             
               
               
               
               
               
             
               
             
               
               
               
               
               
             
               
             
               
               
               
               
               
             
           
               
                 TABLE 7 
               
               
                   
               
               
                   
                   
                 Tin Oxide 
                 Control - 
               
               
                   
                 Control 
                 CBA 
                 Repeat 
               
               
                   
               
             
             
               
                   
               
             
          
           
               
                 Hunter L Value 
               
             
          
           
               
                   
                 Start 
                 89.16 
                 89.97 
                 89.63 
               
               
                   
                 15 min. 
                 89.73 
                 89.52 
                 90.00 
               
               
                   
                 30 min. 
                 88.83 
                 89.98 
                 88.39 
               
               
                   
                 45 min. 
                 86.83 
                 89.31 
                 76.57 
               
               
                   
                 60 min. 
                 71.53 
                 87.09 
                 63.33 
               
               
                   
                 75 min. 
                 61.28 
                 76.73 
                 54.01 
               
               
                   
                 90 min. 
                 55.68 
                 72.57 
                 51.58 
               
             
          
           
               
                 Hunter b Value 
               
             
          
           
               
                   
                 Start 
                 4.90 
                 4.23 
                 3.74 
               
               
                   
                 15 min. 
                 6.56 
                 5.01 
                 5.85 
               
               
                   
                 30 min. 
                 9.50 
                 8.11 
                 8.53 
               
               
                   
                 45 min. 
                 13.80 
                 10.26 
                 13.37 
               
               
                   
                 60 min. 
                 13.68 
                 13.83 
                 13.41 
               
               
                   
                 75 min. 
                 13.24 
                 17.75 
                 12.94 
               
               
                   
                 90 min. 
                 12.74 
                 17.33 
                 12.15 
               
             
          
           
               
                 Total Color Change - Delta E 
               
             
          
           
               
                   
                 Start 
                 0.00 
                 0.00 
                 0.00 
               
               
                   
                 15 min. 
                 1.84 
                 0.95 
                 2.15 
               
               
                   
                 30 min. 
                 4.61 
                 3.96 
                 5.09 
               
               
                   
                 45 min. 
                 9.34 
                 6.23 
                 16.50 
               
               
                   
                 60 min. 
                 19.73 
                 10.13 
                 28.06 
               
               
                   
                 75 min. 
                 29.13 
                 18.95 
                 37.04 
               
               
                   
                 90 min. 
                 34.75 
                 21.88 
                 39.40 
               
               
                   
               
             
          
         
       
     
     While the present invention has been described with respect to particular embodiments thereof, it is apparent that numerous other forms and modifications of this invention will be obvious to those skilled in the art. The appended claims and this invention generally should be construed to cover all such obvious forms and modifications which are within the true spirit and scope of the present invention.