Abstract:
Embedded passive components such as capacitors are formed in multilayer ceramic circuit boards by screen printing a component precursor compound ink sandwiched between conductor ink layers onto a green tape stack and covering the component ink layer with one or two green tape layers, aligning and laminating the green tapes and firing. Capacitor inks are made from dielectrics chosen from barium titanate, titanium oxide and lead-magnesium-niobate. The green tapes are made of a mixture of a crystallizing glass, a non-crystallizing glass and an oxide filler which does not shrink in the x and y dimensions during firing mounted on a metal support. Thus the embedded components can be made to close tolerances.

Description:
This application is a continuation-in-part of copending application Ser. No. 08/812,151 filed Mar. 6, 1997 now U.S. Pat. No. 5,953,203. 
    
    
     This invention relates to multilayer, ceramic printed circuit boards including co-fired passive components. More particularly, this invention relates to multilayer ceramic printed circuit boards including embedded capacitors and methods of making them. 
     BACKGROUND OF THE INVENTION 
     Low temperature multilayer ceramic circuit boards are known that are suitable for use with low melting temperature conductive metals, such as silver, gold and copper. They have a low thermal coefficient of expansion (TCE) and thus they may be compatible with silicon or gallium arsenide. The ceramic circuit boards are made from glasses that can be fired at low temperatures, i.e., less than 1000° C. The multilayer circuit boards are made in known manner by admixing suitable finely divided glass particles with organic materials, including resin, solvents, dispersants and the like, and casting the resultant slurry as a thin tape called green tape. A circuit may be screen printed onto the green tape using a conductive ink formulation comprising a conductive metal powder, an organic vehicle and a powdered glass, usually the same or a similar glass to that used to make the green tape. 
     When more than one green tape is to be stacked, via holes are punched into the tapes which are filled with a via fill ink, made with conductive material, an organic vehicle and a glass, which will provide electrical contact between the circuits on the various green tape layers. The patterned green tapes are aligned and compressed or laminated under pressure prior to firing. 
     More recently, the multilayer ceramic circuit boards have been adhered to a metal support substrate to increase the strength of the multilayer board. The support board has a metal core that is coated with a bonding glass that adheres the ceramic tapes to the support substrate during co-firing. The use of a bonding glass has another advantage in that it greatly reduces the shrinkage of the green tapes during firing in the x and y dimensions, so that most of the shrinkage occurs only in the z, or thickness, dimension. This means that the printed circuits can be made with closer tolerances. The glasses used for the green tapes must have a thermal coefficient of expansion (TCE) matched to the metal support however, to prevent delamination or cracking of the fired glass. Mixtures of crystallizable and non-crystallizable glasses, optionally including inorganic fillers, are also known that have the desired TCE characteristics. 
     Up to the present time, when multilayer ceramic circuit boards are to include components, such as resistors, capacitors, RF filters and the like, discrete components have been mounted to the top of the fired boards, using solder or epoxy type adhesives, to adhere the components to the multilayer ceramic. The addition of these components increases the number of steps needed to make these circuit boards, i.e., the components must be aligned and adhered to the ceramic multilayer board, and connected to a source of power. Further, in order to accommodate a number of discrete devices, the multilayer boards have to be large. Thus the costs of making such boards is high. 
     It would be advantageous to be able to screen print passive components onto multilayer, low temperature co-fired ceramic circuit boards because the packing density can be increased, reducing the size and cost of the packaging. Using the recently developed low firing temperature glasses and metal support board that reduce shrinkage in the x and y dimensions, screen printing of such components to tight tolerances, and high precision placement, become feasible. Further, because fewer interconnects need to be made, reliability would also be improved. 
     Thus it would be highly desirable to develop appropriate inks that can be screen printed onto green tape layers to form embedded components such as capacitors to tight tolerances with high precision placement. 
     SUMMARY OF THE INVENTION 
     We have found that passive components can be made by screen printing an ink comprising a compound of a component precursor mixed with a low firing temperature glass and an organic vehicle onto a component green tape, sandwiching the component green tape with additional green tape layers, generally having circuitry printed thereon, and aligning and firing the green tape stack, thereby embedding the component. In particular we have found a method of making thick film capacitor inks based on barium titanate, which can include a compound that can modify the thermal coefficient of capacitance, titanium oxide or lead magnesium niobate dielectrics which, when combined with appropriate low firing temperature glasses or glass-containing mixtures, sinter at low temperatures. The capacitors can be made in a wide range of dielectric constant. The capacitor inks can be screen printed onto ceramic green tapes and connected to a silver conductor layer by means of vias in the green tape that are filled with appropriate conductive inks. After printing the capacitors and other circuitry, the multiple green tape layers are aligned with each other and with a support, laminated together and co-fired in air at a temperature of about 850-900° C. 
     Shunt capacitors can also be made by using a ground plane metal as the bottom capacitor plate. The capacitors are located one or more layers from the top of the green tape stack. 
     The embedded capacitors of the invention are made by screen printing capacitors from a capacitor ink onto stacked green tape layers on a metal support substrate one or two layers from the top of the stack; capacitors are terminated by screen printing a conductive layer over and under the printed capacitor (dielectric) ink layer. 
    
    
     BRIEF DESCRIPTION OF THE DRAWING 
     FIG. 1 is a graph of dielectric constant versus capacitor size for low dielectric constant inks. 
     FIG. 2 is a cross sectional view of one embodiment of a buried capacitor of the invention. 
     FIG. 3 is a graph of dielectric constant versus capacitor size for capacitors of the invention. 
     FIG. 4 is a graph of temperature coefficient of capacitance versus capacitor size for capacitors of the invention. 
     FIG. 5 is a graph of dielectric constant versus capacitor size for capacitors of the invention. 
    
    
     DETAILED DESCRIPTION OF THE INVENTION 
     We have discovered low dielectric constant, i.e., K=about 50-700, capacitor dielectric inks based on barium titanate or titanium oxide powders. These powders sinter at high temperatures, about 1100-1300° C., and thus they must be modified by combining them with low melting glasses so that the oxide-glass composition will sinter at lower temperatures of about 850-900° C., to adjust the dielectric constant (K) and to minimize the temperature coefficient of capacitance (TCC). 
     Barium titanate is commercially available from the Degussa Company under the trade name AD302L, (designated below as D) and a mixture of barium titanate and barium tin oxide from the Ferro Corporation under the trade name YL12000 (designated below as F). The properties of these powders are set forth below in Table I, wherein K is the dielectric constant, the dielectric loss is Tanδ and the temperature is in degrees Centigrade. Particle size is given as average particle size (Av. Part. Size) in microns (μm). 
     
                       TABLE I______________________________________Compo-                          Firing                                 Av. part.sition     K           Tanδ                       TCC, %                                T, ° C.                                    Size, μm______________________________________F      12000     0.022  -80*    1200  1.0D                3200                &lt;0.02                    -9**      1140                                      0.6______________________________________ *RT to 125° C. **85° C. 
    
     Titanium oxide powder # 4162-01 is available from Mallincrodt Baker Inc. 
     Prior to making capacitor ink compositions, the barium titanate or titanium oxide powder was mixed with various low firing temperature glasses. The compositions of suitable glasses, in weight percent, is given below in Table II. 
     
                       TABLE II______________________________________Oxide  Glass 1 Glass 2 Glass 3                        Glass 4*                               Glass 5                                     Glass 6______________________________________Al.sub.2 O.sub.3  6.00    10.10                1.0   1.82BaO                                         &lt;2.0B.sub.2 O.sub.3    39.00                    &gt;5.0                                 5.0    8.18Bi.sub.2 O.sub.3                                                       23.0CaO         5.0CdO                               36.0MgO                                    24.50PbO                 50.00                               &gt;70.0                                    25.0                                          68.82SiO2                39.90                     24.50                           &lt;2.0                                    5.0                                          2.23TiO.sub.2                                         9.09ZnO         50.00                           &gt;12.0                                    5.0                                          9.09ZrO.sub.2                                                2.73Particle    11-13      5-7                      10-12                            5.0                                     5.0                                          4.0Size, μm______________________________________ 
    
    
     Representative low dielectric constant capacitor inks made from barium titanate powder were admixed with various glasses and glass mixtures, together with conventional dispersants, resin and solvent, and screen printed onto green tapes. The ink compositions are summarized in Table III below wherein the glass compositions are as shown in Table II. 
     
                       TABLE III______________________________________BaTiO.sub.2                 Dispersant                                Resin                                     SolventType          Wt %          Glass #   Wt %                         Wt %       Wt %                                         Wt %______________________________________F      62.29  1        7.14 1.43     4.07 23.07F               166.09    8.25                         1.52           19.38F               264.89    9.8                          1.49          19.05D               165.62   13.52                         1.57           14.48D               159.99    3.08                         1.44           21.04D               262.27   12.15                         1.54           17.83D               260.86   15.34                         1.52           17.82D               360.10   14.84                         1.50           18.85D               257.05    15.35                         1.54           17.84         SrZrO.sub.3                       3.76D          59.15           2         15.38                         1.54           17.89         SrTiO.sub.3                     1.57D               2.88      15.33                         1.53           17.85         SrZrO.sub.3                     1.94D               2.25      14.04                          1.56          17.73D               2.61      12.79                          1.53          17.66______________________________________ 
    
     The capacitor inks can be screen printed onto green tapes formulated for co-firing onto metal, particularly kovar, support substrates. The primary crystallizing glass used is made from a mixture of the following oxides: 29.4% of ZnO, 24.5% of MgO, 19.6% of B 2  O 3 , 24.5% of SiO 2  and 2.0% of Co 3  O 4 , all % by weight. Typical green tape compositions are given below in Table IV. 
     
                       TABLE IV______________________________________                Amount. wt %                           Amount. wt %Additive      Function                   Green tape 1                             Green tape 2______________________________________Glass    Primary     57.34      57.29       Crystallizing       GlassGlass P12.sup.1       Secondary                    6.98             7.03       Crystallizing       GlassForsterite.sup.2      Ceramic         7.27           4.42Powder          FillerCordierite.sup.3      Ceramic         1.09           3.44Powder          FillerHypermer PS2.sup.4    Dispersant     0.58              0.58Butvar B98.sup.5      Binder           2.04                                     2.04Santicizer       Plasticizer                      1.36            1.36160.sup.6Methyl ethyl     Solvent             11.67                                    11.67KetoneAnhydrous        Solvent          11.67                                    11.67Ethanol______________________________________ .sup.1 Glass composition (wt %) 10.0% Al.sub.2 O.sub.3, 42.0% PbO, 38.0% SiO.sub.2, 10.0% ZnO .sup.2 3-5 μm median particle size .sup.3 2-3 μm median particle size .sup.4 Registered trademark of ICI Americas, Inc. .sup.5 Registered trademark of Monsanto Co. .sup.6 Registered trademark of Monsanto Co. 
    
     The capacitor inks were screen printed onto the above green tapes in square capacitor patterns 1.27, 2.54 and 5.08 mm in size. Three four-layer green tapes were made with the capacitor ink layer one layer from the top of the stack. The green tapes were laminated at 278 psi and co-laminated to a kovar substrate at 347 psi. A silver powder or silver flake-based conductor ink was buried to make an embedded co-fired capacitor. Suitable conductor ink compositions are set forth in Table V. 
     
                       TABLE V______________________________________Component     Ink 1  Ink 2      Ink 3                                Ink 4______________________________________Silver Powder.sup.1         83.78                  20.11Silver-Palladium     84.93Powder.sup.1Silver Flake .sup.1             80.97                                60.30Glass 3       0.65Dispersant    1.22   1.32       0.53 1.21Resin.sup.2   0.88   0.86       0.46 0.46Resin.sup.3                     1.85 1.84Resin.sup.4   0.80   0.79Texanol Solvent         3.22   3.25Terpineol Solvent         6.81   6.73       6.48 6.44Butyl Carbitol         2.54   2.12       9.71 9.66______________________________________ .sup.1 Available from Degussa Corporation, So. Plainfield, NJ .sup.2 Ethyl Cellulose Resin N300 of Aqualon Corp. .sup.3 Ethyl cellulose Resin N14 .sup.4 Elvacite 2045 
    
     The resultant laminated stack was fired at 850° C. The capacitance and dielectric loss (tanδ) were measured at 10 KHz. The dielectric constant for each capacitor was calculated from the measurement of capacitance (C) in pF, the area (A) of the capacitor in square centimeters and the thickness (t) in centimeters in accordance with the equation 
     
         K=Ct/Aε.sub.0 
    
     wherein ε 0  is a constant=0.0885 pF/cm. These capacitor inks were suitable for operation at high frequency (1 GHz). The capacitor sizes and property measurements are given below in Table VI, wherein the thickness is for the fired capacitor, capacitance is measured as pF/mm 2 , dielectric loss is given as tanδ, K is the dielectric constant, and TCC is given in ppm/°C. from room temperature to 125° C. In Table VI, the glass is given in volume % except as otherwise noted. 
     
                       TABLE VI______________________________________Capacitor Size,   Thick,Composition       mm       μm                         pF/mm.sup.2                               Tan δ                                   K     TCC______________________________________F + 13.4% 1.27    32      23.0   0.010                                 83   -115Glass 1                328                           18.9                                0.011                                   68    515F + 15%          1.27                  32       22.1                                0.007                                   80    582Glass 1                .08                                0.012                                   74.5                                       689F + 15%          1.27                  30       10.5                                0.007                                   36    878Glass 2                .07                                0.008                                   31.4D + 25%          1.27                  32       16.1                                0.002                                   59Glass 1                .08                                0.002                                   56D + 26%          1.27                  32       13.5                                0.003                                   48.5                                       -1136Glass 1                .08                                0.001                                   38.4                                         37D + 20%          1.27                  33       30.4                                0.007                                  114    -264Glass 2D + 25%          1.27                  32       15.3                                0.002                                   55    -560Glass 2                .08                                0.004                                   46    -342D + 30%          1.27                  30       13.3                                0.002                                   45    -918Glass 3                .08                                0.002                                   33    34D + 25%          1.27                  29       40.5                                0.009                                   131                                          61Glass 2 +        5.08                                0.008                                   125                                         3606.6 Wt % SrZrO.sub.3D + 25%          1.27                  34       14.8                                0.003                                    57                                        -756Glass 2 +        5.08                                0.003                                    42                                        1932.7 Wt % SrZrO.sub.3D + 25%          1.27                  31       20.7                                0.005                                   72.3                                       -119glass 2 +        5.08                                0.005                                   55    5793.3 Wt % SrZrO.sub.3______________________________________ 
    
     Additional low dielectric constant capacitor inks made of barium titanate were screen printed to form capacitors of various sizes, laminated at 1670 psi, terminated with a silver ink layer, co-laminated to kovar® at 1740 psi, and fired at 865° C. Several screen printings were applied to produce a minimum thickness of the fired capacitor. The composition, size and fired properties are summarized below in Table VII, wherein the glass is given in volume %. 
     
                       TABLE VII______________________________________      Thick   SizeComposition          μm                  mm     pF/mm.sup.2                             K    Tan δ                                        TCC______________________________________25% Glass 2      39      1.27    15.7  71   0.004                                      -127                          13.0    2.54                              56  0.004                                            201                          12.6    5.08                              55  0.004                                            34825% Glass 2 +      32         1.27     22.7                              84  0.007                                             703.3 Wt % SrZrO.sub.3                  2.54                          20.0                              71  0.006                                            313                          20.5   5.08                              74  0.006                                            45323% Glass 2*          32     1.27     19.7                              71  0.003                                          -118                          16.2     2.54                              58  0.003                                            185                          15.2     5.08                              55  0.003                                            29621% Glass 2           35    1.27     25.0                              99  0.004                                          -69                          22.4     2.54                              89  0.004                                            242                          22.1     5.08                              90  0.004                                            36530% Glass 2           35    1.27     14.8                              59  0.002                                            271                          12.9     2.54                              51  0.003                                            360                          12.6     5.08                              50  0.004                                            411______________________________________ *IR was measured to be 1.4 × 10.sup.12 ohms. 
    
     It is apparent that there is a size dependence of capacitance per unit area and dielectric constant for buried capacitors and TCC values. In general, dielectric constant decreases with an increase in capacitor size, as shown in FIG. 1, whereas TCC shows more positive capacitance. The smaller the capacitor, the higher the capacitance, which may be due to fringing capacitance effects and to interaction between capacitors and the surrounding ceramic layers. 
     Designing high dielectric constant buried co-fired capacitors (K=1500) however, is a much more difficult problem. Since the capacitor dielectric materials have a high sintering temperature, the low firing temperature used with the present green tapes results in a porous dielectric; the mixture of barium titanate with a low firing temperature glass dilutes the dielectric constant; the surrounding low dielectric constant glass-ceramics diffuse into the capacitor, resulting in further dilution effects; and the diffusion of silver metal into the capacitor also dilutes the dielectric constant. Thus the resultant buried capacitors based on barium titanate were limited to K values of no more than 700, as shown in Tables VIII and IX. 
     Table VIII summarizes capacitor properties for buried BaTiO 3  -based capacitor inks using a silver powder conductor layer. Green tape and capacitor layers were laminated at 280 psi and fired at 850° C. The glass is given in volume %. 
     
                       TABLE VIII______________________________________Composition    Thick, μm             Size, mm pF/mm.sup.2                            K    Tan δ                                      TCC______________________________________7.5 vol %    29       1.27     123.4 404  0.005Glass 4*                2.54                           120.22                             394   0.007                           107.5   5.08                              352Same                   1.27                           221.3                              725                                   0.008                                         259                           193.6   2.54                              634                                   0.007                                         313                           187.9   5.08                              615                                   0.007                                         305The above capacitors were made with a capacitor dielectric inkapplied above and below the conductor pads as a barrier.7.5 vol %    29       1.27     167.4 549  0.008                                      335Glass 4**                   2.54                           151.3                              496                                   0.008                                         423                           154.1   5.08                              505                                   0.008                                         4337.5 vol %            26                  1.27                           150.0                              441                                   0.014PbTiO.sub.3 /                    5.08                           131.2                              385                                   0.013Bi.sub.2 O.sub.38.8 vol %            32                  1.27                           158.7                              574                                   0.009                                         625Glass 5**                    5.08                           160.0                              586                                   0.010                                         550______________________________________ *using the silver powder as the conductor **using silverpalladium powder as the conductor 
    
     The following capacitors were made by laminating green tape and capacitors at 1670 psi and firing at 865° C. The silver conductor used was silver flake. The glass is given as volume %. 
     
                       TABLE IX______________________________________Composition    Thick, μm             Size, mm pF/mm.sup.2                            K    Tan δ                                      TCC______________________________________7.5% Glass 4*    27.4     1.27     215.9 668  0.007                                      104                           197.9    2.54                             612 0.007                                         56                           214.5    5.08                             664 0.007                                        -1738.8% Glass 5**     27.2        1.27      223.2                             686 0.010                                         166                           220.2    2.54                             677 0.010                                          39                           222.4    5.08                             600 0.010                                        -1307.5% PbTiO.sub.3 /    25.6       1.27        198.7                             575 0.010Bi.sub.2 O.sub.3                   2.54                           186.5                             540 0.010                           183.6   5.08                             531 0.009______________________________________ *IR was 4.7 × 10.sup.10 ohms **IR was 5.1 × 10.sup.10 ohms 
    
     The above capacitor compositions were tailored to promote sintering at low temperatures with a minimum dilution of the dielectric constant and to contain less than 10 volume percent of low melting oxides or glass additives made from PbO, B 2  O 3 , ZnO, CdO or PbTiO 3 , materials that are soluble in the BaTiO 3  perovskite lattice structure. These represent fired compositions having a maximum dielectric constant of about 700. 
     When a low TCC is required, i.e., less than 60 ppm/°C. at a temperature range of either between room temperature to -25° C. or room temperature to 85° C., a barium titanate-based capacitor formulation also includes a TCC modifier, SrZrO 3  in substantial amounts. 
     Table X illustrates compositions of two such suitable capacitor inks, given in % by weight. 
     
                       TABLE X______________________________________Composition        Ink 1  Ink 2______________________________________BaTiO.sub.3        47.7   37.5SrZrO.sub.3                    30.6.9Glass 2                        1.5  12.4Glass 4                          6.8Hypermer PS2                   1.5520% Elvacite/solvent                  22.5                          22.1______________________________________ 
    
     A silver-based ink was made from 83.78% silver powder, 0.65% of glass 3 filler, 4.2% 15% ethylcellulose/texanol solvent, 7.61% of 13% Elvacite in terpineol solvent, 1.22% of Hypermer PS2 and 2.54% of butyl carbitol solvent. The bottom electrode was screen printed as a single layer, the dielectric layer was screen printed in three layers, and the top electrode singly printed. 
     The green tape stacks were laminated at 1670 psi and co-laminated to a kovar® substrate at 1100 psi and the whole fired at 865° C. The dielectric constant (K) and TCC at two temperatures are given below in Table XI. 
     
                       TABLE XI______________________________________      TCCDielectric   Size, mm RT to 85° C.                        RT to -25° C.                                 K______________________________________Ink 1   1.27     13.8        -356.7   97.0                      12.0                                   84.56                   -47.8                                 -430.4                                   77.8Ink 2            1.27                   -440.0                                     88.6                   -388.2                                -28.6                                    77.6                   -335.3                                -73.5                                    75.6______________________________________ 
    
     A capacitor ink having a low TCC and a low dielectric constant can also be made using titanium oxide (TiO 2 ) as the dielectric. A dielectric ink was made using 42.1% of TiO 2  powder, 29.6% of glass 2, 1.4% of Hypermer PS2 dispersant and 26.9% of 20% of Elvacite resin/terpineol solvent. 
     The dielectric ink was applied to green tape at least one layer below the top of the stack, and a termination layer applied thereunder using a conductor ink, and laminated and fired as above. The TCC and dielectric constant K are given in Table XII below. 
     
                       TABLE XII______________________________________  TCCSize, mm RT to 85° C.                  RT to -25° C.                             K______________________________________1.27     68.6          32.4       25.72.54               14.6                             55.4                                         18.55.08                3.0                             69.8                                         15.7______________________________________ 
    
     In order to achieve higher dielectric constants for buried co-fired capacitors (K&gt;1000), we have found that lead-magnesium-niobate-based (PMN) compositions must be used. Suitable high dielectric constant capacitor ink compositions based on PMN are summarized below in Table XIII, wherein % is by weight. 
     
                       TABLE XIII______________________________________% PMN  Additives  %      Dispersant                             Resin                                  Solvent______________________________________75.02  Glass 4    5.33   1.65     3.33 13.32          BaTiO.sub.3                 1.3576.88     Glass 4        3.97                         1.61                               3.31                                    13.32          BaTiO.sub.3                 1.0174.16     PbTiO.sub.3                 6.01                         1.65                               3.28                                    13.11          PbO                        1.60          MgO                        0.2074.93     Glass 5        5.49                         1.65                               3.32                                    13.27          BaTiO.sub.2                 1.3574.93     Glass 6        5.12                         1.65                               3.32                                    13.27          PbTiO.sub.3                 1.7274.70     Glass 5        5.48                         1.64                               3.29                                    13.15          PbTiO.sub.3                 1.74______________________________________ 
    
     Using the above lead-magnesium-niobate-based capacitor inks and co-firing on alumina support substrates produced K values of over 2000 with a silver powder conductor ink. However, when buried in green tape laminates on kovar support substrates, the K values were dramatically lowered to about 30-50 due to the dilution effects discussed above. In order to obtain high dielectric constant capacitors on kovar, a barrier layer can be used to block the diffusion of the ceramics into the capacitors during co-firing. This barrier layer can be of a more effective silver metal composition, or of a different dielectric material. 
     We have found that a BaTiO 3  based capacitor ink can be used as a barrier material when a very low melting glass, lower melting than the glass used in the green tape layers, is used. This barrier glass densifies and crystallizes at a lower temperature than that required for the green tape glasses to soften significantly. Thus the barrier glass blocks the diffusion of the green tape glasses into the capacitor. In such case the barrier is printed as a pad larger than the capacitor, both below the bottom conductor pad and above the top conductor pad, as shown in FIG. 2. In FIG. 2, a three layer capacitor 12 having a two layer top and bottom conductor layers 14 and 15 respectively is sandwiched between two top and bottom two-layer barrier layers 16 and 17 respectively. The buried capacitor is in turn laminated to bottom and top green tape layers 18 and 19 respectively. The bottom green tape layers 18 are mounted on a metal support 20. 
     Using a capacitor ink including Glass 6 as described above and 71.07 percent of BaTiO 3 , a barrier layer was printed as a pad 19×19 mm, centered about a capacitor 5.08×5.08 mm made from a PMN ink including 74.16% of PMN. Silver powder was used to make the conductor ink. Various layers were employed to determine how many barium titanate barrier layers were required to obtain a high dielectric constant capacitor on a kovar® supported multilayer circuit board. Controls without the barrier layers were also tested. The test results are given below in Table XIV wherein the number of prints refers to the number of screen prints used for each layer. 
     
                       TABLE XIV______________________________________                                         IR ×            Thick                        10.sup.10Function   # Prints            μm    pF/mm.sup.2                            K   Tan δ                                       TCC                                           ohms______________________________________Barrier  3        24Conductor    1Capacitor    3           55     181.3                            1132                                0.017Control 1                  58                        5.1                             34Barrier      3       24-48Conductor    2           10Capacitor    3           36     751.6                            3058                                0.038                                     -19.6Control 2                  35                      208.0                             823                                0.022                                     -9.5Barrier      1         10Conductor    2           11Capacitor    3           46      91.6                             493                                0.009                                     -17.5                                           8.3Control 3                  53                      128.2                             689                                0.022                                     -8.5                                           6.4Barrier      2         32Conductor    2           11Capacitor    3           36     360.0                            1463                                0.033                                     -21.5                                           2.3Control 4                  31                       219.0                             766                                0.024                                     -4.2                                           3.8______________________________________ 
    
     Thus when a minimum thickness barrier layer is present, the dielectric constant was much higher than when no barrier layer, or only a thin barrier layer, was used. Buried capacitors having a high dielectric constant were achieved however using a double metallization print, and a double barrier layer print. By increasing the number of barrier prints to three on either side of the conductive layers, dielectric constant (K) values above 3000 were obtained. However, while high dielectric constant capacitors can be made via the above process, several extra printing steps are required, and the barrier thickness must be about 16-20 microns to be effective. 
     However, due to the thickness of the several barrier layers, conductive layers and capacitor layers, the top green tape layer is subject to tearing and care must be taken to prevent that. Further, the large number of screen printing steps required (up to eleven as described above) adds to the costs of the process. 
     Thus a modified buried conductor ink was sought that would be a more effective barrier, one that would require fewer printing steps and one that would have a reduced thickness that would not subject the top green tape layer to tearing. 
     We have further found that a mixture of silver flake and silver powder as the conductive layer makes very effective barrier layers, better than using either silver flake or silver powder alone. Silver powder inks produce low dielectric constant capacitors. Silver flake alone formed a very effective barrier layer (K=3600) but it resulted in tearing of the overlying green tape layer during lamination or firing. Thus a mixture of 75% by weight of silver flake and 25% by weight of silver powder, although not as effective a barrier as silver flake alone, resulted in high dielectric constant capacitors. However, outgassing of capacitors is a problem during firing. If the silver metal seals the capacitor too well, the gases formed from the additives (PbO containing) materials cannot escape. Thus the silver flake, while it results in a high dielectric constant capacitor, forms a structure that becomes too dense during firing, and leads to tears in the overlying green tapes. Thus the use of a mixture of silver powder and silver flake, although a compromise in terms of dielectric constant, does not tear the top green tape layer nor do these structures have outgassing or bubbling problems. 
     A plurality of buried PMN-based capacitors on Kovar®, a trademark of Carpenter Technology for alloys of iron (53.8%), nickel (29%), cobalt (17%) and manganese (0.2%) substrates were made using silver powder, silver flake and a mixed silver powder and silver flake conductor layer. The layers were laminated at 1670 psi and fired at 865° C. The test results are summarized below in Table XV. 
     
                       TABLE XV______________________________________Silver # Prints/ Thick  SizeType           thick                μm                     mm   pF/mm.sup.2                               K     Tan δ                                         TCC______________________________________powder 2/10-11   31     1.27  14.6  51   0.001                                        -2.0      μm                           27.7   2.54                                97   0.010                          112.6                5.08                               394   0.018                                          -6.9powder     2/13μm                35                     1.27                           60.9                               246   0.009                                           11.4                          230    908           2.54                                     0.021                                          -16.5                          482.5                5.08                              1581   0.045                                          -27.6flake      2/10μm                29                     1.27                          447    716                                     0.027                                          -21.7                          716   2346           2.54                                     0.037                                          -27.6                          1066                 5.08                               3601                                     0.040                                          -30.1flake      1/5μm                 21                     1.27                          383    928                                     0.018                                          -30.8                          841   1967           2.54                                     0.027                                          -38.1                         1050   2498           5.08                                     0.026                                          -41.9mixed      1/6μm                 29                     1.27                          228    748                                     0.023                                          -30.8                          477   1564           2.54                                     0.033                                          -39.8                          706   2313           5.08                                     0.045                                          -44.7mixed      2 bott/6.5                29                     1.27                          624   2043                                     0.025                                          -42.7           1 top/3.2                      2.54                          931   3052                                     0.037                                          -49.1                       5.08                         1005   3295                                     0.048                                          -51.8______________________________________ 
    
     Insulation Resistance (IR) of the first capacitor of 5.08 mm size using silver powder was 3.8×10 10  ohms. IR of the second capacitor of 5.08 mm size using silver flake was 6.0×10 10  ohms. The IR of the first capacitor of 5.08 mm size using the mixed silver was 1.0×10 10  ohms. 
     The above buried capacitors made with the mixture of silver flake and silver powder as the conductor layer, required fewer printing steps and fired without any problems with bubbling or outgassing. No tearing of the overlying green tape layer was noted. 
     The dielectric constant of the PMN capacitors exhibit a large size dependence; i.e., the dielectric constant increases with increasing capacitor size, and TCC also increases (becomes more negative) with increasing capacitor size. It is believed this is a result of dilution of the capacitor dielectric by the surrounding low dielectric constant ceramic. Large capacitors have less dilution effect than small capacitors. This is shown in Table XVI below, and schematically in FIGS. 3 and 4, graphs of dielectric constant and TCC versus capacitor size, respectively. In Table XVI the capacitors are based on PMN with mixed silver powder-silver flake conductor/barrier inks. 
     
                       TABLE XVI______________________________________Capacitor    Fired    Size                        IR ×Compositn       Thk, μm              mm     pF/mm.sup.2                           K    Tan δ                                     TCC  10.sup.10______________________________________10% glass 4 +    22.4     1.27   205   518  0.015                                    -45.5BaTiO.sub.3        2.54   496  1259  0.018                                      -55.6                     728  1844 5.08                                0.019                                      -59.7                                          1.97.5% glass 4 +     31         1.27                    7116   400  0.011                                      -38.4BaTiO.sub.3        2.54   334  1154  0.017                                      -50.3                     607  2098 5.08                                0.022                                      -57.310% glass 5 +      24        1.27                     173   456  0.007                                      -37.6BaTiO.sub.3        2.54   508  1367  0.008                                      -47.3                     821  2209 5.08                                0.009                                      -52.9                                           1.510% glass 6 +      30        1.27                     227   484  0.014                                      -24.2BaTiO.sub.3        2.54   253   870  0.016                                      -33.6                     372  1279 5.08                                0.018                                      -38.410% glass 6 +      25        1.27                      68   196  0.011                                      -18.1PbTiO.sub.3        2.54   216   620  0.016                                      -24.8                     329   944 5.08                                0.019                                      -27.1______________________________________ 
    
     Intermediate range (K=500-700) barium titanate-based buried capacitors fabricated with the same mixed silver flake/powder conductor layers, which were also laminated at 1670 psi and fired at 865° C., are not as size dependent. 
     FIG. 5, which is a graph of dielectric constant versus capacitor size using a mixed silver powder/flake conductor, illustrates the differences in the size dependence of barium titanate-based capacitors and PMN-based capacitors. Thus, for applications requiring intermediate dielectric constant values, barium titanate-based buried capacitors will be more consistent and have lower TCC as compared to PMN-based capacitors. 
     The buried capacitors of the invention, buried one or two tape layers below the top of the substrate, have been subject to the HHBT reliability test (85° C./85%RH/50 VDC) for over 1000 hours with no degradation of the capacitance, dielectric loss or insulation resistance (IR) of the buried capacitors. 
     The above co-fired multilayer ceramic circuit boards having buried capacitors of the invention are useful in various applications, such as cellular telephones. 
     Although the invention has been described in terms of specific embodiments, one skilled in the art will be able to, inter alia, substitute other green tape compositions, conductor layers, capacitor compositions and lamination and firing conditions; such variations are meant to be included herein and the invention is meant to be limited only by the scope of the appended claims.