Abstract:
This invention provides a precursor film stack for use in the production of MEMS devices. The precursor film stack comprises a carrier substrate, a first layer formed on the carrier substrate, a second layer of an insulator material formed on the first layer, and a third layer of a sacrificial material formed on the second layer.

Description:
FIELD OF THE INVENTION 
   This invention relates generally to fabrication processes for microelectromechanical systems (MEMS) devices and more specifically to the manufacture of interferometric modulators. 
   BACKGROUND OF THE INVENTION 
   An interferometric modulator is a class of MEMS (micro-electromechanical systems) devices which have been described and documented in a variety of patents including U.S. Pat. Nos. 5,835,255, 5,986,796, 6,040,937, 6,055,090, and U.S. Pending patent application Ser. Nos. 09/966,843, 09/974,544, 10/082,397, 10/084,893, and 10/878,282, herein incorporated by reference. One of the key attributes of these devices is the fact that they are fabricated monolithically using semiconductor-like fabrication processes. Specifically, these devices are manufactured in a sequence of steps which combine film deposition, photolithography, and etching using a variety of techniques. More detail on these processes is described in patent application Ser. No. No. 10/074,562 filed on Feb. 12, 2002, and herein incorporated by reference. 

   
     BRIEF DESCRIPTION OF THE DRAWINGS 
       FIG. 1  shows a block diagram of an integrated MEMS processing facility; 
       FIG. 2  shows a block diagram of a non-integrated MEMS processing facility; 
       FIG. 3  shows a block diagram of a MEMS device which can be fabricated using a precursor stack of the present invention; and 
       FIGS. 4A  to  4 F show block diagrams of precursor stacks of the present invention, according to different embodiments. 
   

   DETAILED DESCRIPTION OF THE INVENTION 
   In the following detailed description of embodiments of the invention, numerous specific details are set forth such as examples of specific materials, machines, and methods in order to provide a thorough understanding of the present invention. It will be apparent, however, to one skilled in the art that these specific details need not be employed to practice the present invention. In other instances, well known materials, machines, or methods have not been described in detail in order to avoid unnecessarily obscuring the present invention. 
   A common characteristic of processes for manufacturing MEMS devices is that they begin with the deposition of a stack of thin films which are crucial to the operation and subsequent fabrication of the device. These precursor films are useful in the fabrication of a broad variety of MEMs devices including interferometric modulators, and their deposition can occur as a part of a larger process to manufacture the MEMS device. In one embodiment of the present invention the films are deposited separately in a stand alone facility to form a precursor stack, which is then sent to multiple facilities which complete the processing. The primary benefit is that the stand alone facility can be optimized to produce these films or precursor stacks at very high throughputs that allow for economies of scale not possible in an integrated factory, i.e., one that does both the deposition and post-deposition processing. Furthermore, since the technology development of the precursor stack occurs at the stand alone facility, entities which desire to perform the subsequent processing steps are faced with a lower technological barrier to entry. 
   Patent application Ser. No. 10/074,562 herein incorporated by reference describes a prototypical fabrication sequence for building interferometric modulators. In general, interferometric modulator fabrication sequences and categories of sequences are notable for their simplicity and cost effectiveness. This is due in large part to the fact that all of the films are deposited using physical vapor deposition (PVD) techniques with sputtering being the preferred and least expensive of the approaches. Part of the simplicity derives from the fact that all interferometric modulator structures, and indeed many other planar MEMS structures are bound by the fact that they require a lower electrode, an insulating structure to prevent shorting, a sacrificial material, and an actuatable or movable structure. An insulating structure differs from a film in that it is not continuous in its form but by mechanical means is able to prevent electrical contact through its body. This fact presents an opportunity in that a subset of these films, a precursor stack comprising one or more of the lower electrode, insulating structure, the sacrificial layer, and optionally an actuatable structure may be manufactured separately and in advance of the actuatable structure or structures. 
     FIG. 1  of the drawings provides a block diagram of an integrated MEMS fabrication facility  102 . A precursor film deposition tool  100 , comprises a single or series of deposition tools which are configured to deposit these films using one or more deposition techniques, e.g., sputtering. The films are deposited on a suitable carrier substrate, which could be glass or plastic, for example, depending on the application, and subsequently transported to micro-machining loop  104 . Here, and as described in the aforementioned patent applications, a sequence of repeated steps, such as etching, patterning, and deposition, are performed and serve to define the actuatable structure of the MEMS device. 
     FIG. 2  of the drawings shows a non-integrated MEMS processing facility. Referring to  FIG. 2 , a pre-cursor facility  200  contains only a precursor film deposition tool  100  which is equivalent to that described in  FIG. 1 , hence the use of the same reference numeral. The facility  200  is capable of providing variations on both precursor film type and substrate size. After the deposition, the substrates are containerized and shipped as appropriate to one or more processing facilities indicated by reference numeral  202 . These facilities then perform the machining steps as required for the particular MEMS product that they are designed to produce. 
     FIG. 3  shows a schematic drawing of a simple MEMS device which can be fabricated using a precursor stack of the present invention. In this case an actuatable membrane  304 , is supported on posts  306 . Films  302  comprise materials which at a minimum provide a lower electrode and an insulating structure, though other functions, as will be discussed, may be incorporated. The entire assembly resides on a substrate  300 . 
     FIGS. 4A  to  4 F of the drawings show block diagrams of precursor stacks in accordance with different embodiments of the invention. In  FIGS. 4A  to  4 F, the same reference numerals have been used to identify the same or similar features/components. 
     FIG. 4B  shows a block diagram of a generalized precursor stack  400 A that includes conductor stack or structure  404 , an insulator layer  406 , and a sacrificial material layer  408 . All the films reside on a substrate  402 . The conductor stack  404 may comprise a single metal, a conductive oxide or polymer, a fluoride, a silicide or combinations of these materials. The exact composition of the conductive stack is determined by the requisite electrode properties of the MEMS device to be manufactured. The insulator  408 , can be any one or a combination of a variety of insulating materials which include but are not limited to oxides, polymers, fluorides, ceramics, and nitrides. The sacrificial material  408 , may include, for example, a single layer of materials such as silicon, molybdenum, or tungsten which are all etchable by XeF2, which is a process etch gas that has been described in prior patents. Other materials are possible subject to the compatibility of the etching medium to the materials and structures which must remain. Thicknesses vary according to the requisite behavior of the final device. 
     FIG. 4B  shows a block diagram of a precursor stack  400 B designed for use in the fabrication of an interferometric modulator device. The stack  400 B includes a conductor stack  404 , the composition of which has been described above. Suitable metals for the conductor stack  404  in the present case include glossy metals such as Chromium, Tungsten, Molybdenum, or alloys thereof. The conductor stack  404  may have a thickness of up to 150 angstroms. Transparent conductors suitable for use in the conductor stack  404  include indium tin oxide (ITO), zinc oxide (ZnO), and titanium nitride (TiN). Typical thicknesses for the transparent conductors range from 100 to 800 angstroms. The conductor stack  404  resides on a transparent compensating oxide layer  410 , in one embodiment. The oxide layer  410  may be of a metallic oxide, such as zirconia (ZrO2) or hafnia (HfO2), which have a finite extinction coefficient within the visible range. The compensating oxide layer  410  is an optional film for all the designs discussed in this patent application. Typical thicknesses for the oxide layer  410  range from 100 to 800 angstroms. It should be noted that the positions of the conductor stack  404  and the compensating oxide layer  410  are interchangeable with only subtle changes in the optical behavior. This design, however, can be considered an embedded optical film design since the metal, which plays the primary optical function, resides on the side of insulator layer  406 , opposite that of the sacrificial layer  408 . The insulator layer  406 , may comprise a silicon dioxide film with a thickness ranging from 280 to 840 angstroms for good black states, although other thicknesses are useful for different interference modulator operational modes. Other oxides or combinations of oxides are possible as well. The sacrificial layer  408  may include a single layer of materials such as silicon, molybdenum, tungsten, for example, which are all etchable by XeF2, a process etch gas which has been described in prior patents. For the stack  400 B, the thickness of the layer  408  may vary from 1000, to 7000 angstroms. 
     FIG. 4C  shows a block diagram of a precursor stack  400 C, in accordance with another embodiment. In this case, the conductor stack  404  does not perform any optical functions. Instead, a separate optical film  412  performs the optical function. The optical film  412  is separated from the conductor stack  404  by an insulator film or structure  414 . This design allows for high quality white states to be achieved when the actuatable membrane is driven. In this case the optical film  412  does not serve as a conductor. It is the transparent conductor stack  404  which functions as a conductor. An ancilliary insulator film or structure which is not shown in  FIG. 4C  but which is similar to the insulator layer  406  of  FIG. 4B , may reside between the sacrificial layer  408  and the optical film  412 , in some embodiments. The thickness of the insulator film or structure may be less than 100 angstroms for this design. 
     FIG. 4D  shows an embodiment  400 D of a precursor stack, known as a buried optical film design. In this case, an optical film  412 , resides over an optical compensation film  410 , which resides below an insulator film/structure  406 . A transparent conductor film or film stack  404 , follows and is capped by an additional oxide layer  416 , and a sacrificial film layer  408 . One advantage of the stack  400 D is that it allows for the effective optical distance between the optical film  412  and the mechanical film to be large while allowing the driving voltages to remain small. This is because the driving voltages are significantly determined by the distance between the conductor and the actuatable membrane. 
     FIG. 4E  shows a precursor stack  400 E which includes a multi-layer etch stop stack  418  incorporated instead of a single layer sacrificial film. This  418  stack provides a convenient means for predefining the heights for multiple actuatable structures to be defined during subsequent micro-machining processes. In one embodiment, the stack  418  comprises at least two materials which can be etched using the same release etch, but can utilize alternative and different etch chemistries so that one material may act as an etch stop for the other. One example would be a combination of molybdenum and silicon that are both etchable in XeF2. However, a phosphoric based wet etchant may be used to etch molybdenum without attacking silicon, and a tetra-methyl-ammonium hydroxide (TMMA) which may be used to etch silicon without etching molybdenum. Many other combinations exist and can be identified and exploited by those skilled in the art. Further, it should be noted that the etch stop stack may be applied to any of the previously defined precursor stacks in place of the single sacrificial layer. 
     FIG. 4F  of the drawings shows an embodiment  400 F of a precursor stack The precursor stack  400 F includes a mechanical structural material  420 . Using proper micro-machining techniques and sequences, a functioning MEM device may be fabricated using the precursor stack  400 F using only patterning and etching. Thus, during post-processing of the precursor stack  400 F no deposition is required. This means that a post-processing facility such as the facility  202  (see  FIG. 2 ) does not require capital investment in deposition tools. The material  420  may comprise any number of materials, including but not limited to metals, polymers, oxides, and combinations thereof, whose stress can be controlled.