Abstract:
A method of manufacturing a semiconductor device which includes forming first and second gate patterns, forming first and second sidewall spacers on sidewalls of the first and second gate patterns respectively, implanting a first impurity into the semiconductor substrate, forming a third sidewall spacer on the first sidewall spacer and a fourth sidewall spacer on the second sidewall spacer in such a manner that the third sidewall spacer is in contact with the fourth sidewall spacer between the first and second gate patterns, implanting a second impurity into the semiconductor substrate, and removing the third and the fourth sidewall spacers.

Description:
CROSS-REFERENCE TO RELATED APPLICATIONS 
       [0001]    This application is a divisional of U.S. application Ser. No. 12/544,810 filed Aug. 20, 2009, which is based upon and claims the benefit of priority from the prior Japanese Patent Application No. 2008-243309, filed on Sep. 22, 2008, the entire content of which is incorporated herein by reference. 
     
    
     FIELD 
       [0002]    The present invention relate to a method of manufacturing a semiconductor device. 
       BACKGROUND 
       [0003]    The development of the Complementary Metal-Oxide Semiconductor (CMOS) device technology has been supporting the electronics industry and engineers are adopting finer CMOS design rules at an unprecedented pace in order to further improve the performance. As for generations of CMOS devices, which are expressed in terms of technology node, volume production of the 45-nm node has been started, the 32-nm node technology has been developed, and development of the next generation or the 22-nm node has begun. The feature sizes of devices become smaller and smaller and the gate lengths of MOS transistors are now 35 nm or less. 
         [0004]    As the feature size of devices becomes smaller, processes such as the photolithography and etching processes are becoming more difficult to perform. Source-drain impurity profiles are designed so that devices operate even when gate pitches are reduced. Sidewalls are used primarily to set an offset for regions such as source-drain regions to gate electrodes. It is known that a problem of variations in threshold voltage arises as the gate length of a MOS gate transistor decreases. The phenomenon is called the short-channel effect. 
       SUMMARY 
       [0005]    According to an aspect of the invention, a method of manufacturing a semiconductor device includes forming a first and a second gate patterns, forming first and second sidewall spacers on sidewalls of the first and second gate patterns respectively, implanting a first impurity into the semiconductor substrate, forming a third sidewall spacer on the first sidewall spacer and a fourth sidewall spacer on the second sidewall spacer in such a manner that the third sidewall spacer is in contact with the fourth sidewall spacer between the first and second gate patterns, implanting a second impurity into the semiconductor substrate, and removing the third and the fourth sidewall spacers. 
         [0006]    The object and advantages of the invention will be realized and attained by means of the elements and combinations particularly pointed out in the claims. 
         [0007]    It is to be understood that both the foregoing general description and the following detailed description are exemplary and explanatory and are not restrictive of the invention, as claimed. 
     
    
     
       BRIEF DESCRIPTION OF DRAWINGS 
         [0008]      FIGS. 1A to 1Y  are cross-sectional views illustrating a process for fabricating a semiconductor device according to an embodiment; 
           [0009]      FIGS. 2A to 2D  are cross-sectional views illustrating a process for fabricating a semiconductor device according to an embodiment in which NMOS regions are adjacent to each other; 
           [0010]      FIGS. 3A to 3D  are cross-sectional views illustrating a process for fabricating a semiconductor device according to an embodiment in which NMOS regions are adjacent to each other; 
           [0011]      FIGS. 4A and 4B  are graphs illustrating the relationship between the overetching rate (%) of insulating film etching and the resulting sidewall spacer width; and 
           [0012]      FIGS. 5A to 5I  are cross-sectional views illustrating a process for fabricating a semiconductor device according to an embodiment. 
       
    
    
     DESCRIPTION OF EMBODIMENTS 
       [0013]    Referring to  FIGS. 1A to 1Y , a semiconductor device fabrication method according to an embodiment will be described. In the semiconductor device fabrication method according to the present embodiment, an element isolation film  3  having a Shallow Trench Isolation (STI) structure is formed in a semiconductor substrate  2  as illustrated in  FIG. 1A . For example, a resist pattern is formed over the semiconductor substrate  2  by photolithography and an element isolation trench is formed in the semiconductor substrate  2  by Reactive Ion Etching (RIE). The element isolation trench formed in the semiconductor substrate  2  is filled with silicon oxide film and a silicon oxide film is deposited over the semiconductor substrate  2  by a method such as Plasma Enhanced Chemical Vapor Deposition (PECVD). 
         [0014]    The silicon oxide film over the semiconductor substrate  2  is planarized by Chemical Mechanical Polishing (CMP) to form an element isolation film  3  in the semiconductor substrate  2 . The formation of the element isolation film  3  in the semiconductor substrate  2  defines a region where N-type MOS transistor is to be formed (hereinafter referred to as the NMOS region) and a region where a P-type MOS transistor is to be formed (hereinafter referred to as the PMOS region) in the semiconductor substrate  2 . 
         [0015]    Multiple NMOS and PMOS regions may be defined in the semiconductor substrate  2 . In the present embodiment, an example will be described in which NMOS and PMOS regions adjacent to each other are defined in a semiconductor substrate  2 . NMOS regions adjacent to each other may be defined in a semiconductor substrate  2 . Also, PMOS regions adjacent to each other may be defined in a semiconductor substrate  2 . 
         [0016]    The embodiment will be described below in which NMOS transistors adjacent to each other are formed in a single active region of a semiconductor substrate  2 . 
         [0017]    A photoresist  4  is formed over a PMOS region of a semiconductor substrate  2  by photolithography as illustrated in  FIG. 1B . The photoresist  4  is used as a mask to implant B (boron) ions with an acceleration energy of 100 keV and a dose in the range from 1×10 13  cm −2  to 5×10 13  cm −2  to form a P-well  5  in the NMOS region of the semiconductor substrate  2 . Channel implantation is performed in the NMOS region of the semiconductor substrate  2  to form a channel region  5 - 1 . B (boron), for example, is implanted into the NMOS region of the semiconductor substrate  2  by channel stop implantation with an acceleration energy in the range from 15 keV to 25 keV and a dose of 5×10 12  cm −2  to form a channel stop region  5 - 2 . In order to adjust the threshold value of the NMOS transistor, B (boron) ions, for example, are implanted into the NMOS region of the semiconductor substrate  2  with an acceleration energy of 10 keV and a dose in the range from 0.5×10 13  cm −2  to 2×10 13  cm −2 . 
         [0018]    Ashing or a wet process using an agent such as sulfuric acid hydrogen peroxidemixture (SPM) is performed to remove the photoresist  4  formed over the PMOS region of the semiconductor substrate  2 . A photoresist  6  is formed over the NMOS region of the semiconductor substrate  2  by photolithography as illustrated in  FIG. 1C . The photoresist  6  is used as a mask to implant P (phosphorus) ions into the PMOS region of the semiconductor substrate  2  with an acceleration energy in the range from 250 keV to 350 keV and a dose in the range from 1×10 13  cm −2  to 5×10 13  cm −2  to form an N-well  7  in the semiconductor substrate  2 . As (arsenic), for example, is implanted into the PMOS region  2  of the semiconductor substrate  2  by channel stop implantation with an acceleration energy in the range from 100 keV to 150 keV to form a channel stop region  5 - 2  and a dose in the range from 1×10 12  cm −2  to 5×10 12  cm −2 . In order to adjust the threshold value of the PMOS transistor, As (arsenic) ions, for example, are implanted into the PMOS region of the semiconductor substrate  2  with an acceleration energy in the range from 50 keV to 100 keV and a dose in the range from 0.5×10 13  cm −2  to 2×10 13  cm −2  to form a channel region  5 - 1 . 
         [0019]    Ashing or a wet process using an agent such as SPM is performed to remove the photoresist  6  formed over the NMOS region of the semiconductor substrate  2 . In order to activate impurities such as B (boron), P (phosphorus), and As (arsenic) implanted in the semiconductor substrate  2 , annealing is applied to the semiconductor substrate  2  at a heat treatment temperature of 1000° C. for a treatment time of 10 seconds, for example. 
         [0020]    A gate insulating film  8  is formed over the semiconductor substrate  2  as shown in  FIG. 1D . For example, dry oxidization is performed at approximately 900° C. to form a foundation oxide film with a thickness of approximately 1 nm over the semiconductor substrate  2 . Then, plasma nitridation is performed in an atmosphere of NO to form an oxinitride film, which is a gate insulating film  8 , on the semiconductor substrate  2 . The plasma nitridation may be performed in an atmosphere of N 2 O or NH 3 , instead of an atmosphere of NO. The gate oxide film  8  is not limited to an oxinitride film; the gate oxide film  8  may be a high-dielectric-constant (High-k) insulating film. The P-well  5  and the N-well  7  are not illustrated in  FIG. 1D  and the subsequent figures. 
         [0021]    A gate polysilicon  9  is deposited over the gate oxide film  8  to a thickness of approximately 100 nm by a method such as Low Pressure Chemical Vapor Deposition (LPCVD) at 600° C., for example, as illustrated in  FIG. 1E . A photoresist  10  is formed over the gate polysilicon  9  in the PMOS region by photolithography as illustrated in  FIG. 1F . The photoresist  10  is used as a mask to implant n-type impurity ions into the gate polysilicon  9  in the NMOS region. For example, As (arsenic) ions may be implanted into the gate polysilicon  9  in the NMOS region with an acceleration energy in the range from 20 keV to 30 keV and a dose in the range from 3×10 15  cm −2  to 5×10 15  cm −2 . 
         [0022]    The photoresist  10  is removed by ashing or a wet process using an agent such as SPM. A photoresist  11  is formed over the gate polysilicon  9  in the NMOS region by photolithography as illustrated in  FIG. 1G . The photoresist  11  is used as a mask to implant p-type impurity ions into the gate polysilicon  9  in the PMOS region. For example, B (boron) ions may be implanted into the gate polysilicon  9  in the PMOS region with an acceleration energy in the range from 3 keV to 5 keV and a dose of 3×10 15  cm −2  to 5×10 15  cm −2 . 
         [0023]    The photoresist  11  is removed by ashing or a wet process using an agent such as SPM. In order to accelerate diffusion of the n-type and p-type impurities implanted in the gate polysilicon  9  as required, spike annealing may be applied to the semiconductor substrate  2  at a heat treatment temperature of 1000° C. for a treatment time of approximately 5 seconds, for example. 
         [0024]    As illustrated in  FIG. 1H , a photoresist  12  is formed over the gate polysilicon  9  by photolithography. An anti-reflection coating may be formed over the gate polysilicon  9  as required. If an anti-reflection coating is formed over the gate polysilicon  9 , the photoresist  12  is formed over the anti-reflection coating. 
         [0025]    The photoresist  12  is used as a mask to anisotropically etch the gate polysilicon  9  by RIE to form gate patterns  20  and  21  as illustrated in  FIG. 1I . The gate patterns  20  and  21  are formed adjacent to each other as illustrated in  FIG. 1I . The photoresist  12  formed over the gate patterns  20  and  21  are removed by ashing or a wet process using an agent such as SPM. 
         [0026]    As illustrated in  FIG. 1J , an insulating film  22  is formed over the entire NMOS and PMOS regions of the semiconductor substrate  2 . For example, a SiO 2  film is deposited by LPCVD, for example, from Tetra Ethyl Ortho Silicate (TEOS) over the semiconductor substrate  2  to a thickness of 10 nm, for example, at 600° C., for example. For example, a SiN film may be deposited over the semiconductor substrate  2  from dichlorsilane (SiH 2 Cl 2 ) to a thickness of 10 nm by LPCVD at 650° C., for example. 
         [0027]    Overall anisotropic etch back is applied to the insulating film  22  by RIE to form sidewall spacers  23  and  24  as illustrated in  FIG. 1K . That is, the sidewall film  22  is left on the sidewalls of the gate pattern  20  to form a sidewall spacer  23  and the sidewall film  22  is left on the sidewalls of the gate pattern  21  to form a sidewall spacer  24 . The sidewall film  22  and the sidewall spacers  23  and  24  are not essential to the present embodiment. 
         [0028]    A photoresist  25  is formed over the PMOS region of the semiconductor substrate  2  by photolithography. As illustrated in  FIG. 1L , the gate pattern  20 , the sidewall spacer  23 , and the photoresist  25  are used as a mask to apply pocket implantation and extension implantation to the NMOS region of the semiconductor substrate  2 . Here, co-implantation of N (nitrogen) or Ge (germanium) may be used. In this way, the sidewall spacer  23  functions as an offset film for the pocket implantation and extension implantation in the NMOS region of the semiconductor substrate  2 . If the step of forming the sidewall spacer  23  has been omitted, the gate pattern  20  and the photoresist  25  are used as a mask to apply the pocket implantation and extension implantation to the NMOS region of the semiconductor substrate  2 . 
         [0029]    The pocket implantation into the NMOS region of the semiconductor substrate  2  is accomplished by implanting a pocket impurity into the NMOS region of the semiconductor substrate  2 . The pocket impurity to be implanted into the NMOS region of the semiconductor substrate  2  is a p-type impurity such as B (boron) or In (indium). For example, B (boron) ions may be implanted into the NMOS region of the semiconductor substrate  2  with an acceleration energy in the range from 3 keV to 6 keV at a tilt angle in the range from 20 degrees to 30 degrees, with a doze in the range from 0.4×10 13  cm −2  to 1×10 13  cm −2  in four directions. 
         [0030]    The extension implantation into the NMOS region of the semiconductor substrate  2  is accomplished by implanting an extension impurity into the NMOS region of the semiconductor substrate  2 . The extension impurity to be implanted into the NMOS region of the semiconductor substrate  2  is an n-type impurity such as P (phosphorus) or As (arsenic). For example, As (arsenic) ions may be implanted into the NMOS region of the semiconductor substrate  2  with an acceleration energy in the range from 1 kev to 3 kev and a dose in the range from 1.0&#39;10 15  cm −2  to 2×10 15  cm −2 , for example. 
         [0031]    The pocket impurity implantation into the NMOS region of the semiconductor substrate  2  forms a pocket region  26  in the NMOS region of the semiconductor substrate  2  as illustrated in  FIG. 1L . The extension impurity implantation into the NMOS region of the semiconductor substrate  2  forms an extension region  27  in the NMOS region of the semiconductor substrate  2  as illustrated in  FIG. 1L . The pocket impurity is implanted deeper than the extension impurity implanted in the NMOS region of the semiconductor substrate  2 . 
         [0032]    Ashing or a wet process using an agent such as SPM is performed to remove the photoresist  25  formed over the PMOS region of the semiconductor substrate  2 . Pocket implantation and extension implantation into different NMOS regions of the semiconductor substrate  2  may be performed under different conditions. In that case, the steps of forming the photoresist  25 , performing pocket implantation into an NMOS region of the semiconductor substrate  2 , performing extension implantation into the NMOS region of the semiconductor substrate  2 , and removing the photoresist  25  are repeated as many times as required. 
         [0033]    A photoresist  28  is formed over the NMOS region of the semiconductor substrate  2  by photolithography. As illustrated in  FIG. 1M , the gate pattern  21 , sidewall spacer  24 , and the photoresist  28  are used as a mask to apply pocket implantation and extension implantation to the PMOS region of the semiconductor substrate  2 . Here, co-implantation of a material such as C (carbon) or Ge (germanium) may be used. In this way, the sidewall spacer  24  functions as an offset for performing pocket implantation and extension implantation into the PMOS region of the semiconductor substrate  2 . If the step of forming the sidewall spacer  24  has been omitted, the gate pattern  21  and the photoresist  28  are used as a mask to perform the pocket implantation and extension implantation into the PMOS region of the semiconductor substrate  2 . 
         [0034]    The pocket implantation into the PMOS region of the semiconductor substrate  2  is accomplished by implanting a pocket impurity into the PMOS region of the semiconductor substrate  2 . The pocket impurity to be implanted into the PMOS region of the semiconductor substrate  2  is an n-type impurity such as As (arsenic) or Sb (antimony). For example, As (arsenic) ions may be implanted into the PMOS region of the semiconductor substrate  2  with an acceleration energy in the range from 25 keV to 40 keV at a tilt angle in the range from 20 degrees to 30 degrees with a dose in the range from 0.4×10 13  cm −2  to 1×10 13  cm −2  in four directions. 
         [0035]    The extension implantation into the PMOS region of the semiconductor substrate  2  is accomplished by implanting an extension impurity into the PMOS region of the semiconductor substrate  2 . The extension impurity to be implanted into the PMOS region of the semiconductor substrate  2  is a p-type impurity such as boron (B). For example, B (boron) ions may be implanted into the PMOS region of the semiconductor substrate  2  with an acceleration energy of 0.5 keV with a dose in the range from 1.0×10 15  cm −2  to 2×10 15  cm −2 . 
         [0036]    The implantation of pocket impurity into the PMOS region of the semiconductor substrate  2  forms a pocket region  29  in the PMOS region of the semiconductor substrate  2  as illustrated in  FIG. 1M . The implantation of extension impurity into the PMOS region of the semiconductor substrate  2  forms an extension region  30  in the PMOS region of the semiconductor substrate  2  as illustrated in  FIG. 1M . The pocket impurity ions are implanted into the PMOS region of the semiconductor substrate  2  deeper than the extension impurity implanted in the PMOS region of the semiconductor substrate  2 . 
         [0037]    Ashing or a wet process using an agent such as SPM is performed to remove the photoresist  28  formed over the NMOS region of the semiconductor substrate  2 . Pocket implantation and extension implantation into different PMOS regions of the semiconductor substrate  2  may be performed under different conditions. In this case, the steps of forming photoresist  28 , performing pocket implantation into the PMOS regions of the semiconductor substrate  2 , performing extension implantation into the PMOS regions of the semiconductor substrate  2 , and removing the photoresist  28  are repeated as many times as required. 
         [0038]    An insulating film  31  is formed to cover the semiconductor substrate  2 , the gate patterns  20 ,  21 , and the sidewall spacers  23 ,  24  as illustrated in  FIG. 1N . That is, the sidewall film  31  is formed over the entire NMOS and PMOS regions of the semiconductor substrate  2 . For example, a SiON film may be deposited over the semiconductor substrate  2  to a thickness in the range from 20 nm to 40 nm by LPCVD at a low temperature of less than or equal to approximately 600° C. to form the insulating film  31 . If the step of forming the sidewall spacers  23  and  24  has been omitted, the insulating film  31  is formed to cover the semiconductor substrate  2  and the gate patterns  20  and  21 . The insulating film  31  may be exposed to an HF solution in a subsequent process step. The insulating film  31  may be made of SiN because SiN is highly resistant to solutions such as an HF solution. 
         [0039]    As illustrated in  FIG. 10 , overall anisotropic etch back is applied to the insulating film  31  by RIE to form sidewall spacers  32  and  33 . 
         [0040]    A photoresist  34  is formed over the PMOS region of the semiconductor substrate  2  by photolithography. As illustrated in  FIG. 1P , the gate pattern  20 , the sidewall spacers  23 ,  32 , and the photoresist  34  are used as a mask to perform buffer implantation into the NMOS region of the semiconductor substrate  2 . In this way, the sidewall spacer  32  functions as an offset film for buffer implantation into the NMOS region of the semiconductor substrate  2 . If the step of forming the sidewall spacer  23  has been omitted, the gate pattern  20 , the sidewall spacer  32 , and the photoresist  34  are used as a mask to perform buffer implantation into the NMOS region of the semiconductor substrate  2 . 
         [0041]    The buffer implantation into the NMOS region of the semiconductor substrate  2  is accomplished by implanting a buffer impurity into the NMOS region of the semiconductor substrate  2 . The buffer impurity to be implanted into the NMOS region of the semiconductor substrate  2  is an n-type impurity such as As (arsenic). For example, As (arsenic) ions may be implanted into the NMOS region of the semiconductor substrate  2  with an acceleration energy of 10 keV to 15 keV and a dose in the range from 1×10 15  cm −2  to 5×10 15  cm −2 . 
         [0042]    The buffer impurity implantation into the NMOS region of the semiconductor substrate  2  forms a buffer region  35  in the NMOS region of the semiconductor substrate  2  as illustrated in  FIG. 1P . The buffer impurity is implanted into the NMOS region of the semiconductor substrate  2  deeper than the extension impurity implanted in the NMOS region of the semiconductor substrate  2 . 
         [0043]    Ashing or a wet process using an agent such as SPM is performed to remove the photoresist  34  formed over the PMOS region of the semiconductor substrate  2 . Then, a photoresist  36  is formed over the NMOS region of the semiconductor substrate  2  by photolithography. The gate pattern  21 , the sidewall spacers  24  and  33 , and the photoresist  36  are used as a mask to perform buffer implantation into the PMOS region of the semiconductor substrate  2 . In this way, the sidewall spacer  33  functions as an offset film for buffer implantation into the PMOS region of the semiconductor substrate  2 . If the step of forming the sidewall spacer  24  has been omitted, the gate pattern  21 , sidewall spacer  33 , and the photoresist  36  are used as a mask to perform buffer implantation into the PMOS region of the semiconductor substrate  2 . 
         [0044]    The buffer implantation into the PMOS region of the semiconductor substrate  2  is accomplished by implanting a buffer impurity into the PMOS region of the semiconductor substrate  2 . The buffer impurity to be implanted into the PMOS region of the semiconductor substrate  2  is a p-type impurity such as B (boron). For example, B (boron) ions may be implanted into the PMOS region of the semiconductor substrate  2  with an acceleration energy in the range from 10 keV to 15 keV and a dose in the range from 1×10 15  cm −2  to 5×10 15  cm −2 . 
         [0045]    The buffer impurity implantation into the PMOS region of the semiconductor substrate  2  forms a buffer region  37  in the PMOS region of the semiconductor substrate  2  as illustrated in  FIG. 1Q . The buffer impurity is implanted into the PMOS region of the semiconductor substrate  2  deeper than the extension impurity implanted in the PMOS region of the semiconductor substrate  2 . 
         [0046]    Ashing or a wet process using an agent such as SPM is performed to remove the photoresist  36  formed over the NMOS region of the semiconductor substrate  2 . A cap film  38  is formed over the entire NMOS and PMOS regions of the semiconductor substrate  2 . For example, a SiO 2  film may be deposited by LPCVD over the semiconductor substrate  2  to a thickness of 50 nm at a low temperature lower than or equal to 550° C. to form the cap film  38 . If the step of forming the sidewall spacers  23  and  24  has been omitted, the cap film  38  is formed to cover the semiconductor substrate  2 , the gate patterns  20 ,  21 , and the sidewall spacers  32  and  33 . 
         [0047]    A photoresist  39  is formed over the NMOS region of the semiconductor substrate  2  by photolithography. As illustrated in  FIG. 1R , the photoresist  39  is used as a mask to perform anisotropic etching of the cap film  38  in the PMOS region of the semiconductor substrate  2  by RIE to remove the cap film  38  from the PMOS region of the semiconductor substrate  2 . In this way, the photoresist  39  formed over the NMOS region of the semiconductor substrate  2  functions as a mask in removing the cap film  38  in the PMOS region of the semiconductor substrate  2 . The photoresist  39  may be selectively formed over multiple NMOS regions of the semiconductor substrate  2 . With this, the cap film  38  may be selectively removed from the multiple NMOS regions of the semiconductor substrate  2 . 
         [0048]    Ashing or a wet process using an agent such as SPM is performed to remove the photoresist  39  formed over the NMOS region of the semiconductor substrate  2 . As illustrated in  FIG. 1S , the gate pattern  21 , the sidewall spacers  24  and  33 , and the cap film  38  are used as a mask to perform anisotropic etching of the PMOS region of the semiconductor substrate  2  by RIE to form a trench  40  in the PMOS region of the semiconductor substrate  2 . 
         [0049]    As illustrated in  FIG. 1T , the trench  40  formed in the PMOS region of the semiconductor substrate  2  is horizontally extended by wet etching. That is, the trench  40  formed in the PMOS region of the semiconductor substrate  2  is processed by wet etching so that the sidewall of the trench  40  is shaped like a letter E. The trench  40  formed in the PMOS region of the semiconductor substrate  2  is shaped in this way in order to efficiently apply a strain to the channel in the PMOS region of the semiconductor substrate  2 . The shaping of the trench  40  formed in the PMOS region of the semiconductor substrate  2  may be performed as required. Therefore the step of shaping of the trench  40  formed in the PMOS region of the semiconductor substrate  2  may be omitted. 
         [0050]    SiGe (silicon germanium) is selectively epitaxially grown in the trench  40  formed in the PMOS region of the semiconductor substrate  2 . By epitaxially growing SiGe in the trench  40  formed in the PMOS region of the semiconductor substrate  2 , a SiGe layer  41  is formed in the PMOS region of the semiconductor substrate  2  as illustrated in  FIG. 1U . During the epitaxial growth of SiGe, the PMOS region of the semiconductor substrate  2  may be in situ doped with B (boron). If the PMOS region of the semiconductor substrate  2  is in-situ doped with B (boron) in the silicon germanium layer  41  forming process, the step of performing buffer implantation into the PMOS region of the semiconductor substrate  2  may be omitted. 
         [0051]    Because the lattice constant of Si 1-x Ge x  (x=0.1 to 0.3) is greater than that of Si, a compressive strain is caused in the depth direction and a tensile strain is cased in the horizontal direction. As a result, the compressive strain is applied along the channel direction, which increases the hole mobility. The width of the sidewall spacer  33  is set so that a desired distance between the silicon germanium layer  41  and the channel is provided. In order to suppress the growth of SiGe on the gate pattern  21 , an insulating film of a material such as SiO 2  may be formed over the gate pattern  21  before SiGe is epitaxially grown. 
         [0052]    By a wet process using an HF solution, the cap film  38  is removed from the PMOS region of the semiconductor substrate  2 . An insulating film  42  is formed over the entire NMOS and PMOS regions of the semiconductor substrate  2  as illustrated in  FIG. 1V . For example, a SiO 2  film may be deposited over the semiconductor substrate  2  by LPCVD at a temperature equal to or less than 550° C. to a thickness of 50 nm to form the insulating film  42 . If the step of forming the sidewall spacers  23  and  24  has been omitted, the insulating film  42  is formed to cover the semiconductor substrate  2 , gate patterns  20 ,  21 , and the sidewall spacers  32 ,  33 . Because the insulating film  42  is removed in a subsequent process step, the sidewall film  42  is preferably formed of SiO 2  film, which may be removed with an HF solution. 
         [0053]    As illustrated in  FIG. 1W , overall anisotropic etch back is applied to the insulating film  42  by RIE to form sidewall spacers  43  and  44 . 
         [0054]    A photoresist  45  is formed in the PMOS region over the semiconductor substrate  2  by photolithography. As illustrated in  FIG. 1X , the gate pattern  20 , the sidewall spacers  23 ,  32 ,  43 , and the photoresist  45  are used as a mask to perform deep-source-drain (SD) impurity implantation into the NMOS region of the semiconductor substrate  2 . In this way, the sidewall spacer  43  functions as an offset film in deep-SD impurity implantation into the NMOS region of the semiconductor substrate  2 . If the step of forming the sidewall spacer  23  has been omitted, the gate pattern  20 , the sidewall spacers  32  and  43 , and the photoresist  45  are used as a mask to perform the deep-SD impurity implantation into the NMOS region of the semiconductor substrate  2 . The distance between the deep-SD region  46  and the end of the gate pattern  20  may be controlled by the widths of the sidewall spacers  43 ,  23  and  32 . In the present embodiment, an offset between the deep-SD region  46  and the end of the gate pattern  20  in the NMOS region may be set by the provision of the sidewall spacer  43 , independently of an offset between the silicon germanium layer  41  and a channel region in the PMOS region. 
         [0055]    The deep-SD impurity implantation into the NMOS region of the semiconductor substrate  2  is accomplished by implanting a deep-SD impurity into the NMOS region of the semiconductor substrate  2 . The deep-SD impurity to be implanted into the NMOS region of the semiconductor substrate  2  is an n-type impurity such as P (phosphorus). For example, P (phosphorus) ions may be implanted into the NMOS region of the semiconductor substrate  2  with an acceleration energy in the range from 5 keV to 10 keV and a dose in the range from 1×10 15  cm −2  to 5×10 15  cm −2 . 
         [0056]    The deep-SD impurity implantation into the NMOS region of the semiconductor substrate  2  forms the deep-SD region  46  in the NMOS region of the semiconductor substrate  2  as illustrated in  FIG. 1X . Since the deep-SD impurity is implanted into the NMOS region of the semiconductor substrate  2  deeper than the extension impurity implanted in the NMOS region of the semiconductor substrate  2 , the deep-SD region  46  extends to a depth deeper than the extension region  27 . In other words, since the extension impurity is implanted into the NMOS region of the semiconductor substrate  2  shallower than the deep-SD impurity implanted in the NMOS region of the semiconductor substrate  2 , the extension region  27  is formed to a depth shallower than the deep-SD region  46 . 
         [0057]    Since the deep-SD impurity is implanted into the NMOS region of the semiconductor substrate  2  deeper than the buffer impurity implanted in the NMOS region of the semiconductor substrate  2 , the deep-SD region  46  extends to a depth deeper than the buffer region  35 . In other words, since the buffer impurity is implanted into the NMOS region of the semiconductor substrate  2  shallower than the deep-SD impurity implanted in the NMOS region of the semiconductor substrate  2 , the buffer region  35  is formed to a depth shallower than the deep-SD region  46 . 
         [0058]    A photoresist  47  is formed over the NMOS region of the semiconductor substrate  2  by photolithography as illustrated in  FIG. 1Y . The gate pattern  21 , sidewall spacers  24 ,  33 , and  44  and the photoresist  47  are used as a mask to implant a deep-SD impurity into the epitaxial layer  41  in the PMOS region of the semiconductor substrate  2 . For example, B (boron) ions may be implanted as the deep-SD impurity into the PMOS region of the semiconductor substrate  2 . 
         [0059]    The sidewall spacer  44  functions as an offset film for deep-SD impurity implantation into the PMOS region of the semiconductor substrate  2 . If the step of forming the sidewall spacer  24  has been omitted, the gate pattern  21 , sidewall spacers  33  and  44 , and the photoresist  47  are used as a mask to implant the deep-SD impurity into the PMOS region of the semiconductor substrate  2 . 
         [0060]    If the PMOS region of the semiconductor substrate  2  has been doped in situ with B (boron) in the step of forming the epitaxial layer  41 , the deep-SD impurity may not be implanted into the PMOS region of the semiconductor substrate  2  in addition. However, even if the PMOS region has been doped in situ with B (boron) in the step of forming the epitaxial layer  41 , the PMOS region of the semiconductor substrate  2  may be further implanted with the deep-SD impurity in order to reduce bonding leakage or adjust bonding capacity. 
         [0061]    An example in which multiple NMOS regions adjacent to each other are formed and an example in which multiple PMOS regions adjacent to each other are formed will be described.  FIGS. 2A to 2D  illustrate an example in which two adjacent NMOS regions are formed in a semiconductor substrate  2 .  FIGS. 3A to 3D  illustrate an example in which two adjacent PMOS regions are formed in a semiconductor substrate  2 . 
         [0062]    Sidewall spacers  43  and  44  are formed by forming an insulating film  42  over the entire NMOS and PMOS regions of the semiconductor substrate  2  and applying overall anisotropic etch back to the insulating film  42  as described above. In the etching step for forming the sidewall spacers  43  and  44 , the width of the insulating film remaining as the sidewall spacers depends on the gate pitch. The smaller the gate pitch is, the smaller the width of the sidewall spacer will be. 
         [0063]    If the pitch between gate patterns  20 A and  20 B is small as illustrated in  FIG. 2A , the width of the sidewall spacer  43  formed between the gate patterns  20 A and  20 B may be small. The region between gate patterns  20 A and  20 B where the width of a sidewall spacer  43  formed between the gate patterns  20 A and  20 B will be small is herein referred to as a “narrow pitch region”. 
         [0064]    As illustrated in  FIG. 2B , if the pitch between the gate patterns  20 A and  20 B is larger than the gate pitch illustrated in  FIG. 2A , the width of the sidewall spacer  43  formed between the gate patterns  20 A and  20 B will not be small. The region between gate patterns  20 A and  20 B where the width of a sidewall spacer  43  formed between the gate patterns  20 A and  20 B is not small is herein referred to as a “wide pitch region”. 
         [0065]    In order to suppress the short-channel effect of a MOS transistor, it is important to set the width of the sidewall spacer  43  to a proper value. For example, if a deep-SD impurity is implanted into an NMOS region in a narrow pitch region of the semiconductor substrate  2  under the same conditions for deep-SD impurity implantation into an NMOS region in a wide pitch region of the semiconductor substrate  2 , the short-channel characteristics will degrade because the width of the sidewall spacer  43  in the narrow pitch region is small. 
         [0066]    In the present embodiment, if the region between gate patterns  20 A and  20 B is a narrow pitch region as illustrated in  FIG. 2C , sidewall spacers  43 B and  43 C in the narrow pitch region are formed in such a manner that sidewall spacers  43 B and  43 C are in contact with each other. By forming the sidewall spacers  43 B and  43 C in the narrow pitch region in contact with each other, deep-SD impurity implantation into the narrow pitch region of the semiconductor substrate  2  may be reduced. As a result, degradation of the short-channel characteristics may be reduced. Although the deep-SD region  46  is not formed in a region where a narrow-pitch gate pattern  20  is formed as illustrated in  FIG. 2C , the resistance of the source-drain region may be reduced because a buffer region  35 , which is an impurity diffusion region, is formed. 
         [0067]    Thus, an NMOS region of the semiconductor substrate  2  where a deep-SD impurity is not implanted may be used for a circuit, for example an SRAM, for which the short-channel effect has higher priority than a driving current. 
         [0068]    If the pitch between gate patterns  20 A and  20 B is large enough as illustrated in  FIG. 2D , a deep-SD impurity may be implanted into the NMOS region of the semiconductor substrate  2  even if sidewall spacers  43 B and  43 C are formed. 
         [0069]    If the pitch between gate patterns  21 A and  21 B is small as illustrated in  FIG. 3A , the width of the sidewall spacer  44  formed between the gate patterns  21 A and  21 B will be small. 
         [0070]    If the pitch between gate patterns  21 A and  21 B is large enough as illustrated in  FIG. 3B , the width of the sidewall spacer  44  formed between the gate patterns  21 A and  21 B will not be small. 
         [0071]    In order to reduce the short-channel effect, it is important to set the width of the sidewall spacer  44  to a proper value. For example, if a deep-SD impurity is implanted into a PMOS region of the semiconductor substrate  2  in a narrow pitch region under the same conditions for deep-SD impurity implantation into a PMOS region of the semiconductor substrate  2  in a wide pitch region, the short-channel characteristics will degrade because the width of the sidewall spacer  44  in the narrow pitch region is small. 
         [0072]    Therefore, if the pitch between gate patterns  21 A and  21 B is not large enough, sidewall spacers  43 B and  44 C are formed in contact with each other as illustrated in  FIG. 3C  in the present embodiment. That is, if the region between gate patterns  21 A and  21 B is a narrow pitch region, the sidewall spacers  44 B and  44 C in the narrow pitch region are formed in contact with each other. By forming the sidewall spacers  44 B and  44 C in the narrow pitch region so that the sidewall spacers  44 B and  44 C are in contact with each other, deep-SD impurity implantation into the narrow pitch region of the semiconductor substrate  2  may be reduced. As a result, degradation of the short-channel characteristics may be reduced. 
         [0073]    If the pitch between gate patterns  21 A and  21 B is large enough as illustrated in  FIG. 3D , a deep-SD impurity may be implanted into the PMOS region of the semiconductor substrate  2  even if sidewall spacers  44 A and  44 B are formed. 
         [0074]    In  FIG. 4A , horizontal axis shows overetching rate (%) of sidewall film  31 , and vertical axis shows resulting width of sidewall spacers  32  and  33 . In  FIG. 4A , the symbol ◯ represents data on a wide pitch region and □ represents data on a narrow pitch region. The sidewall films  31  in the wide and narrow pitch regions were etched under the same conditions. 
         [0075]    As illustrated in  FIG. 4A , under the same conditions, the resulting widths of the sidewall spacers  32  and  33  in the narrow pitch region is smaller than those of the sidewall spacers  32  and  33  in the wide pitch region. 
         [0076]    In  FIG. 4B , horizontal axis shows overetching rate (%) of sidewall film  42 , and vertical axis shows resulting width of sidewall spacers  43  and  44 . In  FIG. 4B , the symbol ◯ represents data on a wide pitch region and □ represents data on a narrow pitch region. The sidewall films  42  in the wide and narrow pitch regions were etched under the same conditions. 
         [0077]    As illustrated in  FIG. 4B , under the same conditions, the resulting widths of the sidewall spacers  43  and  44  in the narrow pitch region is smaller than those of the sidewall spacers  43  and  44  in the wide pitch region. 
         [0078]      FIGS. 5A to 5I  illustrate a process for fabricating the semiconductor device continued from  FIG. 1Y . The photoresist  47  formed over the NMOS region of the semiconductor substrate  2  is removed by ashing or a wet process using an agent such as SPM. Then spike annealing is applied to the semiconductor substrate  2  in order to activate the impurity implanted in the NMOS and PMOS regions of the semiconductor substrate  2 . The spike annealing is performed at 1050° C., for example. In order to further activate the impurity implanted in the NMOS and PMOS regions of the semiconductor substrate  2  and to reduce abnormal diffusion of the impurity, flashlamp annealing or laser spike annealing may be applied at a temperature higher than or equal to 1150° C. for a millisecond time in addition. 
         [0079]    The sidewall spacer  43  in the NMOS region of the semiconductor substrate  2 , the sidewall spacer  44  in the PMOS region of the semiconductor substrate  2 , and the native oxide film on the surface of the silicon substrate  2  are removed by a wet process using an HF solution. As illustrated in  FIG. 5A , a silicide  48  such as NiSi x  is formed over the gate patterns  20  and  21 , the buffer region  35 , the deep-SD region  46 , and the epitaxial layer  41 . Before forming the silicide  48 , the sidewall spacers  43  and  44  are removed. 
         [0080]    In order to increase the electron mobility in the NMOS, or as an etching stopper in formation of a contact hole, a tensile film  49  having a tensile stress is formed over the entire NMOS and PMOS regions of the semiconductor substrate  2 . For example, SiN film may be deposited over the semiconductor substrate  2  by PECVD to a thickness in the range from 30 nm to 100 nm to form the tensile film  49 . 
         [0081]    A photoresist  50  is formed over the NMOS region of the semiconductor substrate  2  by photolithography. As illustrated in  FIG. 5B , the photoresist  50  is used as a mask to anisotropically etch the tensile film  49  in the PMOS region of the semiconductor substrate  2  by RIE to selectively remove the tensile film  49  from the PMOS region of the semiconductor substrate  2 . The photoresist  50  may be selectively formed over multiple NMOS regions of the semiconductor substrate  2 . With this, the tensile film  49  in the multiple NMOS regions of the semiconductor substrate  2  may be selectively removed. 
         [0082]    The photoresist  50  formed over the NMOS region of the semiconductor substrate  2  is removed by ashing or a wet process using an agent such as SPM. In order to increase the hole mobility in the PMOS region, or as an etching stopper in formation of a contact hole, a compressive film  51  having a compressive stress is formed over the entire NMOS and PMOS regions of the semiconductor substrate  2 . For example, SiN film may be deposited over the semiconductor substrate  2  by PECVD to a thickness in the range from 30 nm to 100 nm to form the compressive film  51 . 
         [0083]    A photoresist  52  is formed over the PMOS region of the semiconductor substrate  2  by photolithography. As illustrated in  FIG. 5C , the photoresist  52  is used as a mask to anisotropically etch the compressive film  51  in the NMOS region of the semiconductor substrate  2  by RIE to selectively remove the compressive film  51  from the NMOS region of the semiconductor substrate  2 . The photoresist  52  may be selectively formed over multiple PMOS regions of the semiconductor substrate  2 . With this, the compressive film  51  in the multiple PMOS regions of the semiconductor substrate  2  may be selectively removed. 
         [0084]    As illustrated in  FIG. 5D , an interlayer insulating film  53  is formed over the tensile film  49  and the compressive film  51 . For example, SiO 2  film may be deposited over the tensile film  49  and the compressive film  51  by CVD from TEOS to a thickness in the range from 0.5 μm to 0.7 μm to form the interlayer insulating film  53 . 
         [0085]    The interlayer insulating film  53  is planarized by CMP. A contact hole pattern is formed over the interlayer insulating film  53  by photolithography. As illustrated in  FIG. 5E , the interlayer insulating film  53  is etched by RIE to form contact holes  54  in the interlayer insulating film  53 . 
         [0086]    A diffusion barrier having a multilayer structure of TiN and Ti is formed in the contact holes  54 . Then, the contact holes  54  are filled with W (tungsten) and W (tungsten) is deposited over the interlayer insulating film  53  by CVD, for example. The W over the interlayer insulating film  53  is polished by CMP. W is left only in the contact holes  54  to form W plugs  55  as illustrated in  FIG. 5F . 
         [0087]    In order to form an interconnect trench for a first interconnect to be formed by a damascene process, a first interconnect interlayer insulating film  56  is formed over the interlayer insulating film  53  and the W plugs  55  as illustrated in  FIG. 5G . The first interconnect interlayer insulating film  56  is an oxide film or a low-dielectric-constant insulating film, for example. A wiring pattern is formed over the first interconnect interlayer insulating film  56  by photolithography. 
         [0088]    As illustrated in  FIG. 5H , the wiring pattern formed over the first interconnect interlayer insulating film  56  is used as a mask to anisotropically etch the first interconnect interlayer insulating film  56  by RIE to form interconnect trenches  57 . 
         [0089]    The interconnect trenches  57  are filled with a barrier metal and Cu (copper) and the barrier metal and Cu are deposited over the first interconnect interlayer insulating film  56 . As illustrated in  FIG. 51 , the barrier metal and Cu on the first interconnect interlayer insulating film  56  is polished by CMP to form a copper interconnect  58 , which is a first interconnect. 
         [0090]    For example, if the gate pitch of adjacent NMOS regions is in the range from 140 nm to 180 nm, the sidewall spacers  43  in the adjacent NMOS regions may be formed in contact with each other to reduce a deep-SD impurity from being implanted into the NMOS regions of the semiconductor substrate  2 . In this case, the sidewall spacers  43  in the adjacent NMOS regions with a gate pitch in the range from 140 nm to 180 nm may be formed in contact with each other by controlling the conditions under which the sidewall film  42  is formed. This applies to adjacent PMOS transistors as well. 
         [0091]    Whether the space between gate patterns in adjacent NMOS regions is to be filled or not is determined based on the gate pitch of the NMOS regions. However, in practice, the gate height is also related and therefore whether the space between gates in adjacent NMOS regions is to be filled or not may be determined by the aspect ratio (AR) of the gate height to gate pitch. For example, in a narrow pitch region with an aspect ratio of 0.4 or less, the widths of sidewalls may be designed so that the space between the gates of adjacent NMOS regions is filled. In a narrow pitch region with an aspect ratio greater than 0.4, the width of side walls may be designed so that the space between gates of the adjacent NMOS regions is not filled. This applies to adjacent PMOS transistors as well. 
         [0092]    The present embodiments have been described with respect to an example in which an n-type impurity is implanted in the gate polysilicon  9  in NMOS regions. However, the step of implanting an n-type impurity in the gate polysilicon  9  in NMOS regions may be omitted because the n-type impurity has been implanted in the gate pattern  20  in the step of implanting the deep-SD impurity in the NMOS regions of the semiconductor substrate  2 . 
         [0093]    The present embodiments have been described with respect to an example in which a p-type impurity is implanted in the gate polysilicon  9  in PMOS regions. However, if the step of implanting a deep-SD impurity into the PMOS regions of the semiconductor substrate  2  is performed, the p-type impurity is also implanted in the gate pattern  21  and therefore the step of implanting the p-type impurity into the gate polysilicon  9  in the PMOS regions may be omitted. 
         [0094]    The sidewall spacers  43  and  44  are removed after the impurity implanted in the semiconductor substrate  2  is activated by heat treatment in the present embodiments. The present invention is not limited to the present embodiments, the impurity implanted in the semiconductor substrate  2  may be activated by heat treatment after the sidewall spacers  43  and  44  are removed. Semiconductor devices and methods for fabricating the semiconductor devices according to the present embodiments include a semiconductor device having multilayer interconnections and a method for fabricating the semiconductor device. 
         [0095]    All examples and conditional language recited herein are intended for pedagogical purposes to aid the reader in understanding the invention and the concepts contributed by the inventor to furthering the art, and are to be construed as being without limitation to such specifically recited examples and conditions, nor does the organization of such examples in the specification relate to a showing of the superiority and inferiority of the invention. Although the embodiments of the present inventions have been described in detail, it should be understood that the various changes, substitutions, and alterations could be made hereto without departing from the spirit and scope of the invention.