Abstract:
Provided is a high-concentration carbonyl sulfide conversion-absorption type desulfurizer for use at medium-low temperature and preparation method thereof. The desulfurizer comprises 50%-75% magnetic iron oxide red (Fe 21.333 O 32 ), 5%-10% alkali metal oxide (K 2 O), 5-35% anatase TiO 2 , and 5-10% shaping binder. The method of preparing the desulfurizer comprises: uniformly mixing a metatitanic acid prepared using ferrous sulfate recycled as a by-product from titanium dioxide production with K 2 CO 3 , calcining to activate at 500° C.-700° C., mixing with the magnetic iron oxide red and binder, roll molding at room temperature to form balls which are dried at 100° C.-150° C. to obtain the desulfurizer. The desulfurizer has a hydrolysis conversion of carbonyl sulfide higher than 99%, and has a higher sulfur capacity more than 25%.

Description:
FIELD OF THE INVENTION 
       [0001]    The present invention relates to a desulfurizer for catalytic conversion and absorption of carbonyl sulfide contained in a gas and a desulfurizer for catalytic conversion and absorption of carbon disulfide in a gas and preparation methods thereof, belonging to desulfurization technical field. 
       BACKGROUND OF THE INVENTION 
       [0002]    It is well known organic sulfur widely exists in a feed gas produced by a chemical method using coal, gas and oil as raw materials, and its presence will cause poisoning deactivation of a catalyst in the subsequent processes. More and more studies and researches have been carried out for developing new technologies, such as preparation technologies of a feed gas using a low-grade coal and a coke-oven gas, coal-gas poly-generation technologies, and low-temperature steam transformation technologies. 
         [0003]    Carbonyl sulfide is neutral or slightly acidic, and has a stable chemical property, so it is difficult to be removed completely by using a conventional desulphurization method. There are two removal methods of carbonyl sulfide in industry, i.e. dry desulfurization and wet desulphurization. Fine desulfurization is difficult to be realized by the wet desulphurization as restricted by factors such as chemical equilibrium, so carbonyl sulfide is generally removed by the dry desulfurization method wherein the carbonyl sulfide is converted into hydrogen sulfide by hydrogenolysis or hydrolysis in order for removal. Dry desulfurization generally comprises two methods, i.e. hydrolysis method and hydrogenolysis method. There are two kinds of catalysts for carbonyl sulfide hydrolysis at home and abroad. The first one is a simple conversion type hydrolysis catalyst which only has conversion effect on the carbonyl sulfide and has to be used in combination with a desulfurizer such as zinc oxide and activated carbon. The second one is conversion-adsorption type hydrolysis catalyst which not only has a conversion effect on an organic sulfur such as carbonyl sulfide, but also has an absorption effect on hydrogen sulfide converted from the organic sulfur, so it can be used alone for removal of trace sulfur. In recent years, a conversion-adsorption type bifunctional desulfurizer has drawn a great attention. For example, Chinese patent application CN1069673A discloses a catalyst for organic sulfur hydrolysis at room temperature, comprising potassium carbonate in an amount of 2-25 wt % and a spherical γ-Al 2 O 3 . When this desulfurizer is used at room temperature, the conversion rate of carbonyl sulfide reaches up to 95%, and it is capable of converting the carbonyl sulfide while absorbing hydrogen sulfide. Although the above desulfurizer for carbonyl sulfide conversion can reach a higher conversion rate at room temperature, the disadvantage is that it is just applicable to treat carbonyl sulfide with a lower concentration, such as no more than 30 mgS/m 3 , but is not applicable to treat carbonyl sulfide with a high concentration. Therefore, the problem to be solved in the prior art is how to develop a desulfurizer that can realize efficient conversion and absorption of a high-concentration carbonyl sulfide. In a chemical feed gas, CS 2  generally exists in an amount of approximately 10% of the amount of COS. CS 2  is a polar molecule and its hydrolytic process is as below: 
         [0000]      CS 2 +H 2 O→COS+H 2 S  (1)
 
         [0000]      COS+H 2 O→CO 2 +H 2 S  (2)
 
         [0000]      CS 2 +CO 2 →2COS  (3)
 
         [0004]    In the above process, CS 2  is converted into COS. The hydrolysis conversion rate of CS 2  is subjected to influences of carbonic oxide and hydrogen sulfide atmospheres, and it is difficult to realize a complete removal of CS 2 . In the prior art, Chinese patent application CN10112123A discloses a catalyst for carbon disulfide hydrolysis under moderate temperature, comprising a spherical γ-Al 2 O 3  as a carrier, alkali metal oxide K 2 O as a promoter, and zirconium dioxide ZrO 2  and a rare-earth metal oxide La 2 O 3  as a modifier, and prepared by an incipient-wetness impregnation method comprising impregnating the promoter and modifier followed by calcinations. The obtained catalyst has a better performance against carbon deposition and side reactions not contributing to the conversion. 
         [0005]    Although the above catalyst has a high efficiency for treatment of CS 2  under certain conditions, it is only applicable to treat CS 2  with a concentration range of 200-500 mgS/m 3 , but not applicable to treat CS 2  with a high concentration. Therefore, the problem to be solved in the prior art is how to develop a desulfurizer which can achieve efficient conversion and absorption of a high-concentration CS 2 . 
       SUMMARY OF THE INVENTION 
       [0006]    In order to solve the problem that the hydrolysis catalyst for carbonyl sulfide in the prior art is inapplicable under conditions where the carbonyl sulfide has a high-concentration, the present invention provides a desulfurizer for conversion and absorption of carbonyl sulfide with a wide-range concentration, and also provides a method for preparing the desulfurizer. 
         [0007]    In another aspect, in order to solve the problem that the hydrolysis catalyst of CS 2  in the prior art is inapplicable under conditions where CS 2  has a high concentration, the present invention provides a desulfurizer for conversion and absorption of CS 2  with a wide-range concentration, and also provides a method for preparing the desulfurizer. 
         [0008]    In one aspect, the present invention provides a desulfurizer for conversion and absorption of high-concentration carbonyl sulfide, comprising:
       magnetic iron oxide red Fe 21.333 O 32  in an amount of 50-75 parts by weight; K 2 O in an amount of 5-10 parts by weight;   anatase-type TiO 2  in an amount of 5-35 parts by weight; and   a binder in an amount of 5-10 parts by weight.   In accordance with one embodiment, the binder is selected from a group consisting of bentonite, kaolin clay, attapulgite, Yang Gan soil and any combination thereof.       
 
         [0013]    In another aspect, the present invention provides a method for preparing the desulfurizer, comprising:
       (1) mixing and reacting a FeSO 4  solution with an alkaline substance solution or solid by controlling the alkali ratio of the alkaline substance solution or solid and the FeSO 4  solution to 1-1.1 to form a first mixture, filtering the first mixture to yield a filter cake, and calcining the filter cake at a temperature of 250-400° C. to yield the magnetic iron oxide red Fe 21.333 O 32 ; or   mixing and kneading a FeSO 4  solid with an alkaline substance solid by controlling the alkali ratio of the alkaline substance solid and the FeSO 4  solid to 1-1.1 to form a first mixture, followed by washing with water and filtering the first mixture to yield a filter cake, and calcining the filter cake at a temperature of 250-400° C. to yield the magnetic iron oxide red Fe 21.333 O 32 ; and   (2) mixing 50-75 parts by weight of the magnetic iron oxide red Fe 21.333 O 32  with 5-35 parts by weight of anatase type TiO 2 , 5-10 parts by weight of K 2 O and 5-10 parts by weight of a binder to form a second mixture, followed by roll molding at room temperature and drying the second mixture to produce the desulfurizer.       
 
         [0017]    In accordance with one embodiment, the filter cake in the step (1) is calcined at 350° C. for 2-5 hours. 
         [0018]    In accordance with one embodiment, the alkaline substance is selected from the group consisting of hydroxides of Group IA, Na 2 CO 3 , (NH 4 ) 2 CO 3 , K 2 CO 3 , NaHCO 3 , NH 4 HCO 3 , KHCO 3  and any combination thereof. 
         [0019]    In accordance with one embodiment, the anatase type TiO 2  and K 2 O in Step (2) are prepared by mixing and calcining 6.1-42.7 parts by weight of metatitanic acid and 7.3-14.7 parts by weight of K 2 CO 3  at a temperature of 500-700° C. 
         [0020]    In accordance with one embodiment, the metatitanic acid is prepared by a method comprising
       preparing a ferrous sulfate solution by dissolving a ferrous sulfate solid in water, wherein the ferrous sulfate solid is a by-product from titanium dioxide production by a sulfuric acid method,   heating the ferrous sulfate solution up to 40-100° C.,   adjusting a pH value of the ferrous sulfate solution to 1-2 by adding an acid, and   reacting the ferrous sulfate solution with a flocculating agent to yield a precipitate, followed by filtering the precipitate to obtain the metatitanic acid.       
 
         [0025]    In accordance with one embodiment, the ferrous sulfate solution has a FeSO 4  concentration of 1-2.5 mol/L. 
         [0026]    In accordance with one embodiment, the acid added for adjusting the pH value is selected from the group consisting of nitric acid, hydrochloric acid, sulfuric acid and any combination thereof. 
         [0027]    In accordance with one embodiment, the step (1) of the method for preparing the desulfurizer for conversion and absorption of high-concentration carbonyl sulfide of the present invention comprises: mixing and reacting a FeSO 4  solution with an alkaline substance solution or solid by controlling the alkali ratio of the alkaline substance solution or solid and the FeSO 4  solution to 1-1.1 to form a first mixture, filtering the first mixture to yield a filter cake, and calcining the filter cake at a temperature of 250-400° C. to yield the magnetic iron oxide red Fe 21.333 O 32 . By mixing the FeSO 4  solution with the alkaline substance solution or solid, they will react to produce a precipitate. In a preferred embodiment, the precipitate is filtered to obtain a filter cake, then the filter cake is washed with water prior to calcinations. Alternatively, the above reactions can be realized through solid phase reactions by mixing and kneading a FeSO 4  solid with an alkaline substance solid by controlling the alkali ratio of the alkaline substance solid and the FeSO 4  solid to 1-1.1 to form a first mixture, followed by washing with water and filtering the first mixture to yield a filter cake, and calcining the filter cake at a temperature of 250-400° C. to yield the magnetic iron oxide red Fe 21.333 O 32 . 
         [0028]    In accordance with one embodiment, the step (2) comprises mixing 50-75 parts by weight of the magnetic iron oxide red Fe 21.333 O 32  with 5-35 parts by weight of anatase type TiO 2 , 5-10 parts by weight of K 2 O and 5-10 parts by weight of a binder to form a second mixture, followed by roll molding at room temperature and drying the second mixture to produce the desulfurizer. 
         [0029]    In a preferred embodiment, the anatase type TiO 2  and K 2 O in the step (2) are prepared by mixing and calcining 6.1-42.7 parts by weight of metatitanic acid (TiO(OH) 2 ) and 7.3-14.7 parts by weight of K 2 CO 3  at a temperature of 500-700° C. The inventors found that the desulfurizer, prepared using the mixture of the anatase-type TiO 2  and K 2 O obtained by calcining the metatitanic acid and K 2 CO 3  together, has an unexpectedly excellent sulfur capacity. 
         [0030]    In another aspect, the present invention provides a desulfurizer for catalytic conversion and absorption of carbon disulfide, comprising
       magnetic iron oxide red Fe 21.333 O 32  in an amount of 50-75 parts by weight;   anatase-type TiO 2  in an amount of 5-15 parts by weight;   K 2 O in an amount of 2-8 parts by weight;   γ-Al 2 O 3  in an amount of 5-20 parts by weight; and   a binder in an amount of 5-10 parts by weight.       
 
         [0036]    In accordance with one embodiment, the binder is selected from the group consisting of bentonite, kaolin clay, attapulgite, Yang Gan soil and any combination thereof. In another aspect, the present invention provides a method for preparing the desulfurizer for catalytic conversion and absorption of carbon disulfide, comprising
       (1) mixing and reacting a FeSO 4  solution with an alkaline substance solution or solid by controlling the alkali ratio of the alkaline substance solution or solid and the FeSO 4  solution to 1-1.1 to form a first mixture, filtering the first mixture to yield a filter cake, and calcining the filter cake at a temperature of 250-400° C. to yield the magnetic iron oxide red Fe 21.333 O 32 ; or   mixing and kneading a FeSO 4  solid with an alkaline substance solid by controlling the alkali ratio of the alkaline substance solid and the FeSO 4  solid to 1-1.1 to form a first mixture, followed by washing with water and filtering the first mixture to yield a filter cake, and calcining the filter cake at a temperature of 250-400° C. to yield the magnetic iron oxide red Fe 21.333 O 32 ; and   (2) mixing 50-75 parts by weight of the magnetic iron oxide red Fe 21.333 O 32  with 5-15 parts by weight of anatase-type TiO 2 , 2-8 parts by weight of K 2 O, 5-20 parts by weight of γ-Al 2 O 3  and 5-10 parts by weight of a binder to form a second mixture, followed by roll molding at room temperature and drying the second mixture to produce the desulfurizer.       
 
         [0040]    In accordance with one embodiment, the filter cake in the step (1) is calcined at 350° C. for 2-5 hours. 
         [0041]    In accordance with one embodiment, the alkaline substance is selected from the group consisting of hydroxides of Group IA, Na 2 CO 3 , (NH 4 ) 2 CO 3 , K 2 CO 3 , NaHCO 3 , NH 4 HCO 3 , KHCO 3  and any combination thereof. 
         [0042]    In accordance with one embodiment, the anatase-type TiO 2 , K 2 O and γ-Al 2 O 3  in step (2) are prepared by mixing and calcining 6.1-18.4 parts by weight of metatitanic acid, 2.9-11.7 parts by weight of K 2 CO 3  and 5.9-23.5 parts by weight of pseudo-boehmite at a temperature of 500-700° C. 
         [0043]    In accordance with one embodiment, the metatitanic acid is prepared by a method comprising
       preparing a ferrous sulfate solution by dissolving a ferrous sulfate solid in water, wherein the ferrous sulfate solid is a by-product from titanium dioxide production by a sulfuric acid method,   heating the ferrous sulfate solution up to 40-100° C.,   adjusting a pH value of the ferrous sulfate solution to 1-2 by adding an acid, and   reacting the ferrous sulfate solution with a flocculating agent to yield a precipitate, followed by filtering the precipitate to obtain the metatitanic acid.       
 
         [0048]    In accordance with one embodiment, the ferrous sulfate solution has a FeSO 4  concentration of 1-2.5 mol/L. 
         [0049]    In accordance with one embodiment, the acid added for adjusting the pH value is selected from the group consisting of nitric acid, hydrochloric acid, sulfuric acid and any combination thereof. 
         [0050]    In accordance with one embodiment, the step (1) of the method for preparing the desulfurizer for catalytic conversion and absorption of carbon disulfide comprises mixing and reacting a FeSO 4  solution with an alkaline substance solution or solid by controlling the alkali ratio of the alkaline substance solution or solid and the FeSO 4  solution to 1-1.1 to form a first mixture, filtering the first mixture to yield a filter cake, and calcining the filter cake at a temperature of 250-400° C. to yield the magnetic iron oxide red Fe 21.333 O 32 . In this manner, by mixing the FeSO 4  solution with the alkaline substance solution or solid, they will react to produce a precipitate. In an preferred embodiment, the precipitate is filtered to obtain a filter cake, then the filter cake is washed with water prior to calcinations. 
         [0051]    Alternatively, the above reactions can be realized through solid phase reactions by mixing and kneading a FeSO 4  solid with an alkaline substance solid by controlling the alkali ratio of the alkaline substance solid and the FeSO 4  solid to 1-1.1 to form a first mixture, followed by washing with water and filtering the first mixture to yield a filter cake, and calcining the filter cake at a temperature of 250-400° C. to yield the magnetic iron oxide red Fe 21.333 O 32 . 
         [0052]    In accordance with one embodiment, the step (2) comprises mixing 50-75 parts by weight of the magnetic iron oxide red Fe 21.333 O 32  with 5-15 parts by weight of anatase-type TiO 2 , 2-8 parts by weight of K 2 O, 5-20 parts by weight of γ-Al 2 O 3  and 5-10 parts by weight of a binder to form a second mixture, followed by roll molding at room temperature and drying the second mixture to produce the desulfurizer. In a preferred embodiment, the anatase-type TiO 2 , K 2 O and γ-Al 2 O 3  in step (2) are prepared by mixing and calcining 6.1-18.4 parts by weight of metatitanic acid TiO(OH) 2 , 2.9-11.7 parts by weight of K 2 CO 3  and 5.9-23.5 parts by weight of pseudo-boehmite (i.e. boehmite) at a temperature of 500-700° C. The inventors found that the desulfurizer, prepared using the mixture of the anatase-type TiO 2 , K 2 O and γ-Al 2 O 3  obtained by calcining the metatitanic acid, K 2 CO 3  and pseudo-boehmite together, has an unexpectedly excellent sulfur capacity. 
         [0053]    The present invention has the following advantages: 
         [0054]    (1) The desulfurizer for conversion and absorption of high-concentration carbonyl sulfide comprises magnetic iron oxide red Fe 21.333 O 32 , anatase-type TiO 2 , alkali metal oxide K 2 O and a binder, which ensures that the desulfurizer can achieve conversion and absorption of carbonyl sulfide contained in a gas under moderate temperature, can treat carbonyl sulfide with a wide range of concentration to achieve complete removal of high-concentration carbonyl sulfide, and has a high sulfur capacity when applied at low temperature and moderate temperature. In the present invention, the anatase-type TiO 2 , alkali metal oxide K 2 O and magnetic iron oxide red Fe 21.333 O 32  in specific contents can work synergetically to impart optimized alkaline activity centers to the desulfurizer, so the desulfurizer has excellent conversion and absorption rate even if used in a condition where the carbonyl sulfide has a high-concentration. 
         [0055]    (2) Among the components of the desulfurizer for conversion and absorption of high-concentration carbonyl sulfide, the anatase-type TiO 2  is prepared using ferrous sulfate recycled as a by-product from titanium dioxide production by a sulfuric acid method. The titanium dioxide production by a sulfuric acid method comprises decomposing ilmenite (FeTiO 3 ) with sulfuric acid to form titanium and iron sulfates which then dissolves in the reaction solution. Subsequently iron ions crystallizes as ferrous sulfate solid (FeSO 4 .7H 2 O) which can be separated from the titaniferous solution as a principal by-product. The obtained ferrous sulfate solid contains Ti in an approximate amount of 5%. So far, the ferrous sulfate solid as by-product has not got effectively recycled for further utilization. The present invention employs this by-product and recycles the Ti ion contained therein to prepare metatitanic acid, thus effectively reducing the cost for producing the desulfurizer. 
         [0056]    (3) The desulfurizer for catalytic conversion and absorption of carbon disulfide comprises magnetic iron oxide red Fe 21.333 O 32 , anatase-type TiO 2 , alkali metal oxide K 2 O and γ-Al 2 O 3  and a binder, which ensures that the desulfurizer can achieve conversion and absorption of CS 2  contained in a gas under moderate temperature, can treat CS 2  with a wide range of concentration to achieve complete removal of high-concentration CS 2 , and has a high sulfur capacity when applied at moderate temperature. In the present invention, the anatase-type TiO 2 , alkali metal oxide K 2 O and γ-Al 2 O 3  and magnetic iron oxide red Fe 21.333 O 32  in specific contents can work synergetically to impart optimized alkaline activity centers to the desulfurizer, so the desulfurizer has excellent conversion and absorption efficiency even if used in a condition where the CS 2  has a high concentration. 
         [0057]    (4) Among the components of the desulfurizer for catalytic conversion and absorption of carbon disulfide, the anatase-type TiO 2  is prepared using ferrous sulfate recycled as a by-product from titanium dioxide production by a sulfuric acid method. The titanium dioxide production by a sulfuric acid method comprises decomposing ilmenite (FeTiO 3 ) with sulfuric acid to form titanium and iron sulfates which then dissolves in the reaction solution. Subsequently iron ions crystallizes as ferrous sulfate solid (FeSO 4 .7H 2 O) which can be separated from the titaniferous solution as a principal by-product. The obtained ferrous sulfate solid contains Ti in an approximate amount of 5%. So far, the ferrous sulfate solid as by-product has not got effectively recycled for further utilization. The present invention employs this by-product and recycles the Ti ion contained therein to prepare metatitanic acid, thus effectively reducing the cost for producing the desulfurizer. 
     
    
     
       BRIEF DESCRIPTION OF DRAWINGS 
         [0058]      FIG. 1  shows the XRD pattern of the magnetic iron oxide red Fe 21.333 O 32  prepared in the present invention. 
       
    
    
     DESCRIPTION OF EMBODIMENTS 
     Example 1 
     The Preparation of Metatitanic Acid 
       [0059]    Addling 5 kg of ferrous sulfate solid which is a by-product from titanium dioxide production by a sulfuric acid method into a reactor, dissolving the ferrous sulfate solid with 6 L of water to form a ferrous sulfate solution, heating the ferrous sulfate solution at 60° C. for 30 min, adjusting a pH value of the ferrous sulfate solution to 1 by adding an acid, and reacting the ferrous sulfate solution with polyacrylamide as a flocculating agent to yield a precipitate, followed by filtering the precipitate while hot to obtain a metatitanic acid solid A, and finally drying the metatitanic acid solid A at 110° C. for 1 h. 
         [0060]    Adding 1.67 kg of ferrous sulfate solid which is a by-product from titanium dioxide production by a sulfuric acid method into a reactor, dissolving the ferrous sulfate solid with 6 L of water to form a ferrous sulfate solution, heating the ferrous sulfate solution at 100° C. for 30 min, adjusting a pH value of the ferrous sulfate solution to 2 by adding an acid, and reacting the ferrous sulfate solution with a flocculating agent polyacrylamide to yield a precipitate, followed by filtering the precipitate while hot to obtain a metatitanic acid solid B, and finally drying the metatitanic acid solid B at 110° C. for 1 h. 
       Example 2 
     The Preparation of Anatase Type TiO 2  and K 2 O 
       [0061]    Mixing the metatitanic acid A prepared by example 1 and K 2 CO 3  and calcining at a temperature of 500° C. to obtain the anatase type TiO 2  and K 2 O. 
       Example 3 
       [0062]    The desulfurizer of the present example comprises magnetic iron oxide red Fe 21.333 O 32  in an amount of 50 parts by weight, anatase-type TiO 2  in an amount of 5 parts by weight, K 2 O in an amount of 5 parts by weight, and bentonite in an amount of 5 parts by weight. 
         [0063]    The method for preparing the desulfurizer for catalytic conversion and absorption of carbonyl sulfide comprises: 
         [0064]    (1) putting 500 g of FeSO 4 .7H 2 O solid into a beaker, adding 6 L of water into the beaker and putting the beaker into a water bath at 40° C. until the solid therein is completely dissolved to form a FeSO 4  solution, adding 190 g of Na 2 CO 3  into the FeSO 4  solution by controlling the alkali ratio of the Na 2 CO 3  and FeSO 4  to 1, and reacting for 2 h under stirring to form a first mixture; then filtering the first mixture to yield a filter cake, and calcining the filter cake at a temperature of 350° C. for 3 h to yield the magnetic iron oxide red Fe 21.333 O 32 ; and 
         [0065]    (2) mixing 50 parts by weight of the magnetic iron oxide red Fe 21.333 O 32  with 5 parts by weight of anatase-type TiO 2 , 5 parts by weight of K 2 O, and 5 parts by weight of bentonite to form a second mixture, followed by roll molding at room temperature to form balls having diameter of 4 to 6 mm, and drying the balls to produce the desulfurizer. 
         [0066]    The anatase-type TiO 2  and K 2 O in the present example are prepared by the example 2. 
       Example 4 
       [0067]    The desulfurizer of the present example comprises magnetic iron oxide red Fe 21.333 O 32  in an amount of 75 parts by weight; anatase-type TiO 2  in an amount of 35 parts by weight; K 2 O in an amount of 10 parts by weight; and Yang Gan soil in an amount of 10 parts by weight. 
         [0068]    The method for preparing the desulfurizer for catalytic conversion and absorption of carbonyl sulfide comprises: 
         [0069]    (1) mixing 500 g of FeSO 4 .7H 2 O solid with 333 g of NaHCO 3  solid by controlling the alkali ratio of NaHCO 3  and FeSO 4 .7H 2 O to 1.1 and kneading them in a coating pan for 2 h to yield a first mixture; followed by washing with water for 3 times and filtering the first mixture to yield a filter cake, and calcining the filter cake at a temperature of 350° C. for 3 h to yield the magnetic iron oxide red Fe 21.333 O 32 , which is then ground and screened to obtain Fe 21.333 O 32  powder of 200 mesh; and 
         [0070]    (2) mixing 75 parts by weight of the magnetic iron oxide red Fe 21.333 O 32  with 35 parts by weight of anatase-type TiO 2 , 10 parts by weight of K 2 O, and 10 parts by weight of Yang Gan soil to form a second mixture, followed by roll molding at room temperature to form balls having diameter of 4 to 6 mm, and drying the balls to produce the desulfurizer. 
         [0071]    The anatase-type TiO 2  and K 2 O in the present example are prepared by example 2. 
       Example 5 
       [0072]    The desulfurizer of the present example comprises magnetic iron oxide red Fe 21.333 O 32  in an amount of 59 parts by weight; anatase-type TiO 2  in an amount of 15 parts by weight; K 2 O in an amount of 8 parts by weight; and attapulgite in an amount of 5 parts by weight. 
         [0073]    The method for preparing the desulfurizer for catalytic conversion and absorption of carbonyl sulfide comprises: 
         [0074]    (1) putting 500 g of FeSO 4 .7H 2 O solid into a beaker, adding 454 mL of water into the beaker and putting the beaker into a water bath at 40° C. until the solid therein is completely dissolved to form a FeSO 4  solution, adding 190 g of Na 2 CO 3  into the FeSO 4  solution by controlling the alkali ratio of the Na 2 CO 3  and FeSO 4  to 1, and reacting for 2 h under stirring to form a first mixture; followed by suction filtration to yield a filter cake, and washing the filter cake with water for 3 times and calcining the filter cake at a temperature of 350° C. for 3 h to yield the magnetic iron oxide red Fe 21.333 O 32 , which is ground and screened to obtain Fe 21.333 O 32  powder of 200 mesh; and 
         [0075]    (2) mixing 59 parts by weight of the magnetic iron oxide red Fe 21.333 O 32  with 15 parts by weight of anatase-type TiO 2 , 8 parts by weight of K 2 O, and 5 parts by weight of attapulgite to form a second mixture, followed by roll molding at room temperature to form balls having diameter of 4 to 6 mm, and drying the balls to produce the desulfurizer. 
         [0076]    The anatase-type TiO 2  and K 2 O in the present example are prepared by calcining a mixture of 18.4 parts by weight of metatitanic acid B of example 1 and 11.7 parts by weight of K 2 CO 3  at 500° C. 
       Example 6 
       [0077]    The desulfurizer of the present example comprises magnetic iron oxide red Fe 21.333 O 32  in an amount of 59 parts by weight; anatase-type TiO 2  in an amount of 5 parts by weight; K 2 O in an amount of 5 parts by weight; and bentonite in an amount of 10 parts by weight. 
         [0078]    The method for preparing the desulfurizer for catalytic conversion and absorption of carbonyl sulfide comprises: 
         [0079]    (1) putting 500 g of FeSO 4 .7H 2 O solid into a beaker, adding 454 mL of water into the beaker and putting the beaker into a water bath at 40° C. until the solid therein is completely dissolved to form a FeSO 4  solution, adding 190 g of Na 2 CO 3  into the FeSO 4  solution by controlling the alkali ratio of the Na 2 CO 3  and FeSO 4  to 1, and reacting for 2 h under stirring to form a first mixture; followed by suction filtration to yield a filter cake, washing the filter cake with water for 3 times and calcining the filter cake at a temperature of 350° C. for 3 h to yield the magnetic iron oxide red Fe 21.333 O 32 , which is ground and screened to obtain Fe 21.333 O 32  powder of 200 mesh; and 
         [0080]    (2) mixing 59 parts by weight of the magnetic iron oxide red Fe 21.333 O 32  with 5 parts by weight of anatase-type TiO 2 , 5 parts by weight of K 2 O, and 10 parts by weight of bentonite to form a second mixture, followed by roll molding at room temperature to form balls having diameter of 4 to 6 mm, and drying the balls to produce the desulfurizer. 
         [0081]    The anatase-type TiO 2  and K 2 O in the present example are prepared by calcining a mixture of 6.4 parts by weight of metatitanic acid A of example 1 and 7.3 parts by weight of K 2 CO 3  at 700° C. 
       Example 7 
     The Preparation of Anatase Type TiO 2 , K 2 O and γ-Al 2 O 3    
       [0082]    The anatase type TiO 2  and K 2 O and γ-Al 2 O 3  are prepared by calcining metatitanic acid A prepared by example 1, K 2 CO 3  and pseudo-boehmite at a temperature of 500° C. respectively. 
       Example 8 
       [0083]    The desulfurizer of the present example comprises magnetic iron oxide red Fe 21.333 O 32  in an amount of 50 parts by weight; anatase-type TiO 2  in an amount of 5 parts by weight; K 2 O in an amount of 2 parts by weight; γ-Al 2 O 3  in an amount of 5 parts by weight; and bentonite in an amount of 5 parts by weight. 
         [0084]    The method for preparing the desulfurizer for catalytic conversion and absorption of carbon disulfide comprises: 
         [0085]    (1) putting 500 g of FeSO 4 .7H 2 O solid into a beaker, adding 454 mL of water into the beaker and putting the beaker into a water bath at 40° C. until the solid therein is completely dissolved to form a FeSO 4  solution, adding 190 g of Na 2 CO 3  into the FeSO 4  solution by controlling the alkali ratio of the Na 2 CO 3  and FeSO 4  to 1, and reacting for 2 h under stirring to form a first mixture; then filtering the first mixture to yield a filter cake, and calcining the filter cake at a temperature of 350° C. for 3 h to yield the magnetic iron oxide red Fe 21.333 O 32  which has a XRD pattern as shown in  FIG. 1 ; and 
         [0086]    (2) mixing 50 parts by weight of the magnetic iron oxide red Fe 21.333 O 32  with 5 parts by weight of anatase-type TiO 2 , 2 parts by weight of K 2 O, 5 parts by weight of γ-Al 2 O 3 , and 5 parts by weight of bentonite to form a second mixture, followed by roll molding at room temperature to form balls having diameter of 4 to 6 mm, and drying the balls to produce the desulfurizer. 
         [0087]    The anatase-type TiO 2 , K 2 O and γ-Al 2 O 3  in the present example are prepared by example 7. 
       Example 9 
       [0088]    The desulfurizer of the present example comprises magnetic iron oxide red Fe 21.333 O 32  in an amount of 75 parts by weight; anatase-type TiO 2  in an amount of 15 parts by weight; K 2 O in an amount of 8 parts by weight; γ-Al 2 O 3  in an amount of 20 parts by weight; and Yang Gan soil in an amount of 10 parts by weight. 
         [0089]    The method for preparing the desulfurizer for catalytic conversion and absorption of carbon disulfide comprises: 
         [0090]    (1) mixing 500 g of FeSO 4 .7H 2 O solid with 333 g of NaHCO 3  solid by controlling the alkali ratio of NaHCO 3  and FeSO 4 .7H 2 O to 1.1 and kneading them in a coating pan for 2 h to yield a first mixture; followed by washing with water for 3 times and filtering the first mixture to yield a filter cake, and calcining the filter cake at a temperature of 350° C. for 3 h to yield the magnetic iron oxide red Fe 21.333 O 32 , which is ground and screened to obtain Fe 21.333 O 32  powder of 200 mesh; and 
         [0091]    (2) mixing 75 parts by weight of the magnetic iron oxide red Fe 21.333 O 32  with 15 parts by weight of anatase-type TiO 2 , 8 parts by weight of K 2 O, 20 parts by weight of γ-Al 2 O 3 , and 10 parts by weight of Yang Gan soil to form a second mixture, followed by roll molding at room temperature to form balls having diameter of 4 to 6 mm, and drying the balls to produce the desulfurizer. 
         [0092]    The anatase-type TiO 2 , K 2 O and γ-Al 2 O 3  in the present example are prepared by example 7. 
       Example 10 
       [0093]    The desulfurizer of the present example comprises magnetic iron oxide red Fe 21.333 O 32  in an amount of 59 parts by weight; anatase-type TiO 2  in an amount of 15 parts by weight; K 2 O in an amount of 8 parts by weight; γ-Al 2 O 3  in an amount of 16 parts by weight; and attapulgite in an amount of 5 parts by weight. 
         [0094]    The method for preparing the desulfurizer for catalytic conversion and absorption of carbon disulfide comprises: 
         [0095]    (1) putting 500 g of FeSO 4 .7H 2 O solid into a beaker, adding 454 mL of water into the beaker and putting the beaker into a water bath at 40° C. until the solid therein is completely dissolved to form a FeSO 4  solution, adding 190 g of Na 2 CO 3  into the FeSO 4  solution by controlling the alkali ratio of the Na 2 CO 3  and FeSO 4  to 1, and reacting for 2 h under stirring to form a first mixture; followed by suction filtration to yield a filter cake, and washing the filter cake with water for 3 times and calcining the filter cake at a temperature of 350° C. for 3 h to yield the magnetic iron oxide red Fe 21.333 O 32 , which is ground and screened to obtain Fe 21.333 O 32  powder of 200 mesh; and 
         [0096]    (2) mixing 59 parts by weight of the magnetic iron oxide red Fe 21.333 O 32  with 5 parts by weight of anatase-type TiO 2 , 8 parts by weight of K 2 O, 16 parts by weight of γ-Al 2 O 3  and 5 parts by weight of attapulgite to form a second mixture, followed by roll molding at room temperature to form balls having diameter of 4 to 6 mm, and drying the balls to produce the desulfurizer. 
         [0097]    The anatase-type TiO 2 , K 2 O and γ-Al 2 O 3  in the present example are prepared by calcining a mixture of 6.1 parts by weight of metatitanic acid B of example 1, 11.7 parts by weight of K 2 CO 3  and 18.8 parts by weight of pseudo-boehmite at 500° C. 
       Example 11 
       [0098]    The desulfurizer of the present example comprises magnetic iron oxide red Fe 21.333 O 32  in an amount of 59 parts by weight; anatase-type TiO 2  in an amount of 5 parts by weight; K 2 O in an amount of 2 parts by weight; γ-Al 2 O 3  in an amount of 5 parts by weight; and bentonite in an amount of 10 parts by weight. 
         [0099]    The method for preparing the desulfurizer for catalytic conversion and absorption of carbon disulfide comprises: 
         [0100]    (1) putting 500 g of FeSO 4 .7H 2 O solid into a beaker, adding 454 mL of water into the beaker and putting the beaker into a water bath at 40° C. until the solid therein is completely dissolved to form a FeSO 4  solution, adding 190 g of Na 2 CO 3  into the FeSO 4  solution by controlling the alkali ratio of the Na 2 CO 3  and FeSO 4  to 1, and reacting for 2 h under stirring to form a first mixture; followed by suction filtration to yield a filter cake, and washing the filter cake with water for 3 times and calcining the filter cake at a temperature of 350° C. for 3 h to yield the magnetic iron oxide red Fe 21.333 O 32 , which is ground and screened to obtain Fe 21.333 O 32  powder of 200 mesh; and 
         [0101]    (2) mixing 59 parts by weight of the magnetic iron oxide red Fe 21.333 O 32  with 5 parts by weight of anatase-type TiO 2 , 2 parts by weight of K 2 O, 5 parts by weight of γ-Al 2 O 3  and 10 parts by weight of attapulgite to form a second mixture, followed by roll molding at room temperature to form balls having diameter of 4 to 6 mm, and drying the balls to produce the desulfurizer. 
         [0102]    The anatase-type TiO 2 , K 2 O and γ-Al 2 O 3  in the present example are prepared by calcining a mixture of 6.1 parts by weight of metatitanic acid A of example 1, 2.9 parts by weight of K 2 CO 3  and 5.9 parts by weight of pseudo-boehmite at 700° C. 
         [0103]    The alkaline substance of the present invention for preparing magnetic iron oxide red Fe 21.333 O 32  is not limited to the above mentioned Na 2 CO 3  or NaOH, and also may be selected from the group consisting of (NH 4 ) 2 CO 3 , K 2 CO 3 , NH 4 HCO 3 , KHCO 3 , hydroxides of Group IA except for Na, and any combination thereof. As a preferred embodiment, the anatase-type TiO 2  is prepared using FeSO 4  recycled as a by-product from titanium dioxide production. Alternatively, the anatase-type TiO 2  can also be commercially available industrial grade metatitanic acid. 
         [0104]      FIG. 1  shows the XRD pattern of the magnetic iron oxide red Fe 21.333 O 32  prepared in the present invention. 
       Test Example 1 
       [0105]    In order to demonstrate technical effect of the desulfurizer for conversion and absorption of carbonyl sulfide, the present invention provides the test example 1, the experiment conditions of which are described as follows. 
         [0106]    An evaluation test is performed under normal temperatures and normal pressures by using N 2  as background gas and by using a standard gas containing 3000 ppm (8571 mgS/m 3 ) of carbonyl sulfide at a space velocity of 500 h −1 . The desulfurization exhaust gas is detected by chromatography using WDL-94 trace sulfur analyzer. The test terminates when the outlet gas contains 20 ppm of carbonyl sulfide. The WDL-94 trace sulfur analyzer has a minimal measurement of 0.02 ppm. 
         [0107]    {circle around (1)} COS Hydrolysis Conversion Rate 
         [0000]      COS hydrolysis conversion rate (%)=(inlet concentration of COS−outlet concentration of COS)/inlet concentration of COS×100%
 
         [0108]    {circle around (2)} H 2 S Removal Rate 
         [0000]      H 2 S removal rate (%)=(inlet concentration of COS−outlet concentration of COS−outlet concentration of H 2 S)/(inlet concentration of COS−outlet concentration of COS)×100%
 
         [0109]    {circle around (3)} Sulfur Capacity 
         [0110]    Sulfur capacity is calculated when the COS concentration in the outlet gas reaches 20 ppm according to the below formula: 
         [0000]    
       
         
           
             X 
             = 
             
               
                 
                   
                     V 
                     
                       1 
                       - 
                       C 
                     
                   
                   × 
                   C 
                   × 
                   32 
                   × 
                   2 
                 
                 
                   22.4 
                   × 
                   G 
                 
               
               × 
               100 
             
           
         
       
     
         [0111]    wherein X represents breakthrough sulfur capacity (%); C represents COS content (%) in a gas mixture; V represents volume (L) of gas exclusive of COS measured by a wet gas flow meter after COS is removed; the value 32 is molar mass (g/mol) of sulphur; 22.4 is molar volume (L/mol) of ideal gas under standard condition; G represents the mass (g) of a desulfurizer sample (dry sample). 
         [0112]    The results are listed in the following table: 
         [0000]    
       
         
               
               
               
               
               
             
               
               
               
               
               
             
           
               
                   
                   
               
               
                   
                   
                   
                 Outlet 
                   
               
               
                   
                 COS hydrolysis 
                 H 2 S removal 
                 concentration 
                 Sulfur 
               
               
                   
                 conversion rate 
                 rate 
                 of COS 
                 capacity 
               
               
                   
                   
               
             
             
               
                   
               
             
          
           
               
                 Example 1 
                 &gt;99.9% 
                 &gt;99.9% 
                 &lt;0.02 
                 28% 
               
               
                 Example 2 
                 &gt;99.9% 
                 &gt;99.9% 
                 &lt;0.02 
                 30% 
               
               
                 Example 3 
                 &gt;99.9% 
                 &gt;99.9% 
                 &lt;0.02 
                 33% 
               
               
                 Example 4 
                 &gt;99.9% 
                 &gt;99.9% 
                 &lt;0.02 
                 33% 
               
               
                 Example 5 
                 &gt;99.9% 
                 &gt;99.9% 
                 &lt;0.02 
                 49% 
               
               
                 Example 6 
                 &gt;99.9% 
                 &gt;99.9% 
                 &lt;0.02 
                 51% 
               
               
                   
               
             
          
         
       
     
       Test Example 2 
       [0113]    In order to demonstrate technical effect of the desulfurizer for catalytic conversion and absorption of carbon disulfide, the present invention provides the test example 2, the experiment conditions of which are described as follows: 
         [0114]    An evaluation test is performed under normal temperatures and normal pressures by using N 2  as background gas and by using a standard gas containing 3000 ppm (8571 mgS/m 3 ) of CS 2  at a space velocity of 500 h −1 . The desulfurization exhaust gas is detected by chromatography using WDL-94 trace sulfur analyzer. The test terminates when the CS 2  concentration in the outlet gas reaches 20 ppm. The WDL-94 trace sulfur analyzer has a minimal measurement of 0.02 ppm. 
         [0115]    {circle around (1)} CS 2  Hydrolysis Conversion Rate 
         [0000]      CS 2  hydrolysis conversion rate (%)=(inlet concentration of CS 2 −outlet concentration of CS 2 )/inlet concentration of CS 2 ×100%
 
         [0116]    {circle around (2)} H 2 S Removal Rate 
         [0000]      H 2 S removal rate (%)=(inlet concentration of CS 2 −outlet concentration of CS 2 −outlet concentration of COS−outlet concentration of H 2 S)/(inlet concentration of CS 2 −outlet concentration of CS 2 −outlet concentration of COS)×100%
 
         [0117]    {circle around (3)} Sulfur Capacity 
         [0118]    Sulfur capacity is calculated when the CS 2  concentration in the outlet gas reaches 20 ppm according to the below formula: 
         [0000]    
       
         
           
             X 
             = 
             
               
                 
                   
                     V 
                     
                       1 
                       - 
                       C 
                     
                   
                   × 
                   C 
                   × 
                   32 
                   × 
                   2 
                 
                 
                   22.4 
                   × 
                   G 
                 
               
               × 
               100 
             
           
         
       
     
         [0119]    wherein X represents breakthrough sulfur capacity (%); C represents COS content (%) in a gas mixture; V represents volume (L) of gas exclusive of COS measured by a wet gas flow meter after COS is removed; the value 32 is molar mass (g/mol) of sulphur; 22.4 is molar volume (L/mol) of ideal gas under standard condition; G represents the mass (g) of a desulfurizer sample (dry sample). 
         [0120]    The results are listed in the following table: 
         [0000]    
       
         
               
               
               
               
               
             
               
               
               
               
               
             
           
               
                   
                   
               
               
                   
                   
                   
                 Outlet 
                   
               
               
                   
                 CS 2  hydrolysis 
                 H 2 S removal 
                 concentration 
                 Sulfur 
               
               
                   
                 conversion rate 
                 rate 
                 of CS 2   
                 capacity 
               
               
                   
                   
               
             
             
               
                   
               
             
          
           
               
                 Example 1 
                 &gt;99.9% 
                 &gt;99.9% 
                 &lt;0.02 
                 20% 
               
               
                 Example 7 
                 &gt;99.9% 
                 &gt;99.9% 
                 &lt;0.02 
                 19% 
               
               
                 Example 8 
                 &gt;99.9% 
                 &gt;99.9% 
                 &lt;0.02 
                 19% 
               
               
                 Example 9 
                 &gt;99.9% 
                 &gt;99.9% 
                 &lt;0.02 
                 19% 
               
               
                 Example 10 
                 &gt;99.9% 
                 &gt;99.9% 
                 &lt;0.02 
                 36% 
               
               
                 Example 11 
                 &gt;99.9% 
                 &gt;99.9% 
                 &lt;0.02 
                 38% 
               
               
                   
               
             
          
         
       
     
       Comparative Example 1 
       [0121]    In order to further demonstrate technical effect of the desulfurizer for conversion and absorption of carbonyl sulfide, the present invention provides the comparative example 1 which is described as follows: 
         [0122]    Taking 100 g of γ-Al 2 O 3  powder particles as carrier of the desulfurizer, impregnating 10 g of K 2 CO 3  on the γ-Al 2 O 3  by using an incipient impregnation method, followed by drying at 120° C. to obtaining the desulfurizer. An evaluation test is performed with the desulfurizer under same conditions of test example 1. The results indicate in the condition of 3000 ppm of CS 2 , COS hydrolysis conversion rate is 88%, H 2 S removal rate is 92%, and sulfur capacity is 16%. 
         [0123]    By comparison it can be seen that, the desulfurizer for conversion and absorption of carbonyl sulfide has a higher COS hydrolysis conversion rate, a higher H 2 S removal rate and a higher sulfur capacity when applied in a high-concentration carbonyl sulfide condition. 
       Comparative Example 2 
       [0124]    In order to further demonstrate technical effect of the desulfurizer for catalytic conversion and absorption of carbon disulfide, the present invention provides the comparative example 2 which is described as follows: 
         [0125]    Taking 86 g of γ-Al 2 O 3  powder particles as carrier of the desulfurizer, impregnating a mixed solution of 17.44 g of Zr(NO 3 ) 4 .5H 2 O and 5.32 g of La(NO 3 ) 3 .6H 2 O on the γ-Al 2 O 3  by using an incipient impregnation method for 2 h, followed by drying for 4 h at 100° C. and calcining for 4 h at 550° C. to obtaining a carrier loaded with Zr and La; then impregnating 10.3 g of K 2 CO 3  on the carrier loaded with Zr and La by using an incipient impregnation method for 2 h, followed by drying for 4 h at 100° C. and calcining for 4 h at 550° C. to obtain a material having a composition of 7 wt % K 2 O-5 wt % ZrO 2 -25 wt % LaO-86 wt % γ-Al 2 O 3 , followed by roll molding at room temperature to form balls having diameter of 4 to 6 mm and drying the balls to produce the desulfurizer. An evaluation test is performed with the desulfurizer under same conditions of the test example 2. The results indicate in the condition of 3000 ppm of CS 2 , CS 2  hydrolysis conversion rate is 89%, H 2 S removal rate is 92%, and sulfur capacity is 16%. 
         [0126]    By comparison it can be seen that, the desulfurizer for catalytic conversion and absorption of carbon disulfide has a higher CS 2  hydrolysis conversion rate, a higher H 2 S removal rate and a higher sulfur capacity when applied in a high-concentration carbon disulfide condition. 
         [0127]    It is obvious the above embodiments are merely examples for clear illustration, rather than limit the application. For those skilled in the art, changes and modifications may be made on the basis of the above description, and it is not necessary and could not exhaust all embodiments, thus obvious changes and modifications derived from the above embodiments still fall within the protection scope of the invention.