Abstract:
A regenerative water treatment composition and a process of making a regenerative water treatment composition by adhesively coating a first bacteria killing material such as a zinc carrier with a second bacterial killing material such as silver chloride for insitu killing of bacteria and a second bacteria killing material for killing and carrying away the dead bacteria on the silver chloride to allow the silver chloride to continue to kill or damage bacteria that comes into contact with the silver chloride.

Description:
CROSS REFERENCE TO RELATED APPLICATIONS 
     This application is a divisional application of U.S. Ser. No. 08/957,265 titled Water Treatment Composition filed Oct. 24, 1997 now U.S. Pat. No. 6,217,892. 
    
    
     FIELD OF THE INVENTION 
     This invention relates generally to a coactive bacteria killing composition and to a process of forming a regenerative coactive bacteria killing composition and, more specifically, to a process of forming a water treatment composition by adhesively securing a bacteria adhering metal to a bacteria adhering carrier in manner to enable both the bacteria adhering metal and the bacteria adhering carrier to remain in a bacteria reactive destroying state. 
     BACKGROUND OF THE INVENTION 
     In water treatment systems it is believed that a bacteria killing materials such as silver ions are effective in killing bacteria because the bacterial cell walls contain various chemical groups that have an affinity for silver. It is believed that when the bacteria cell wall comes in contact with the silver ion, the bacteria cell is strongly bound to the surface of the silver by the various chemical groups in the bacteria cell. The process alone helps prevent the bacteria from multiplying. However, in the presence of dissolved oxygen or very low levels of chlorine a further action can occur in which the various chemical groups in the bacteria cell react chemically with the silver ion and kill the bacteria by damaging or destroying the cell walls of the bacteria. Thus silver ions provide an ideal insitu bacterial killing material, however, without removal of the dead bacteria the surfaces of the silver becomes contaminated with dead bacteria and the reaction stops. 
     Another bacteria killing material is zinc, zinc is believed to react in a similar manner as the silver; however, it is believed that when zinc is present with the silver the zinc is also effective in keeping the surface of the silver clean so that the silver can continue to react or bind with the bacteria in the water. It is believed that the bacteria on the silver also combines with the zinc ions. The zinc reacts to and removes the bacteria which is attached to the silver and thus cleans or regenerates the silver surface. That is, the zinc ions, which react with the chemicals in the bacteria affix themselves to the dead bacteria and are carried away by the flow of water where the zinc and dead bacteria can be trapped in a filter. Thus the combination of two metals that have bacteria killing characteristics and particularly one of them that provides insitu killing the bacteria and the other that combines with the dead bacteria on the first bacteria killing material to carry away with the dead bacteria produces an enhanced or regenerative bacteria killing composition. 
     Although two bacteria killing materials, and particularly two bacteria killing metals such as zinc and silver work well together, silver does not have a natural affinity for zinc. Therefor one must be able to maintain the silver proximate the zinc so both the zinc and silver can be maintained in a state where they are free to react with the chemicals in the bacteria. The present invention provides a process for forming such a supported relationship between the two materials. The process includes applying a silver coating, which is silver chloride, on zinc surface that enables both the zinc and the silver chloride to remain in a reactive state. 
     It has been found that by use of an adhesive that is securable to both the zinc and the silver one can hold the zinc and silver proximate one another. By forming the adhesive in a matrix one can maintain both the silver and the zinc in a reactive state and still provide access to the silver and the zinc so that the bacteria containing water can come into contact with the silver that is dispersed in the matrix. That is, the adhesive, which remains unreactive to the bacteria chemicals, secures the silver therein. By adhesively affixing the silver proximate to the zinc and within an adhesive matrix one provides multiple surfaces areas so the bacteria cells in the water can come into contact with both the silver ions and the zinc ions. 
     SUMMARY OF THE INVENTION 
     Briefly, the present invention comprises a process of adhesively coating a first bacteria killing material such as zinc with a second bacteria killing material such as silver to maintain both the silver and the zinc in a bacteria reactive state by forming an adhesive matrix that is securable to both the zinc and the silver with the matrix providing paths for bacteria laden water to come into contact with both the silver and the zinc to enable the zinc and silver to coactively kill the bacteria in the bacteria laden water and to enable the zinc to remove dead bacteria from the surface of the silver. 
    
    
     BRIEF DESCRIPTION OF THE DRAWINGS 
     FIG. 1 is a perspective view of zinc pellet having a matrix carrying a silver yielding ion thereon; and 
     FIG. 2 is a sectional view taken along lines  2 — 2  of FIG. 1 to show the adhesive matrix located around the zinc pellet. 
    
    
     DESCRIPTION OF THE PREFERRED EMBODIMENT 
     In the present process one forms a water treatment composition in pellet form suitable for inserting into an inline feeder in a water supply. The water treatment pellets comprise a bacteria adhering carrier, which in the preferred embodiment are zinc pellets. Attached to the zinc pellets is a second bacteria killing material which in the preferred embodiment comprises a silver chloride (AgCl) coating located thereon. The silver chloride particles are suspended in an adhesive matrix that adhesively secures the silver chloride particles proximate to the surface of the zinc pellets to produce a zinc pellet with a silver chloride coating. The matrix allows both the silver and the zinc remain in a reactive state so that both the silver and zinc can be used in a water treatment systems. 
     Silver chloride is a white powder that can be melted or cast like a metal, and is derived from heating a silver nitrate solution and adding hydrochloric acid or salt solution to the produce a silver chloride solution which is then boiled or filtered in the dark or under a ruby red light to produce the silver chloride powder. In the present process the silver chloride while still in solution is combined with an adhesive to form an adhesive silver chloride solution. The adhesive and the silver chloride solution are then applied to the zinc pellets. The adhesive is then cured to produce zinc pellets having a silver chloride coating adhesively adhered thereto with both the zinc and the silver chloride available for reacting with the chemicals within a bacteria cell to kill or damage the bacteria. The term adhesively secured herein is meant to include a surface attachment structure between two bacterial adhering materials that does not prevent either of the bacteria adhering materials from binding with the bacteria in the water to damage or destroy the bacteria in the water. 
     Referring to FIG. 1 there is shown a water treatment pellet  10  having an adhesive matrix coating  12 . Adhesive matrix coating  12  comprises an adhesive that secures itself to the surface of both the silver chloride  13  and to the zinc pellet  11  without preventing either the zinc or the silver chloride from adhering to and damaging or killing bacteria located in the water. The present process is describe in relation to forming a silver coating on a zinc pellet so that both the zinc and the silver remain in a reactive state to react with the chemicals in the bacteria and effectively damage or kill the bacteria. Thus while the preferred carrier for the silver chloride comprises zinc pellets the carrier need not be zinc as long as the carrier is compatible with the bacteria adhering material on the carrier. The silver chloride coated particle  10  is shown to be in the form of a cylinder and is cut from zinc wire, however, any of many different shape pellets could be used with the present invention. 
     FIG. 2 is a cross sectional view of the silver chloride coated pellet  10  of FIG. 1 showing zinc particle  11  centrally located within adhesive matrix  12  that contains silver chloride  13  dispersed throughout the adhesive matrix  12 . As can be seen from the drawing the silver chloride  13  is maintained in the matrix proximate the zinc pellet  11  to enable water to contact both the zinc and the silver chloride located within the matrix and thus enable the composition to rid the water of harmful bacteria. 
     In the present invention one coats a particle such as a zinc pellet with a silver ion yielding material such as silver chloride by adhesively affixing or securing the silver chloride and the zinc pellets proximate to each other through a non-soluble water porous adhesive matrix. A suitable material for adhesively securing the silver chloride proximate the zinc pellets is commercially available gelatin which can be cross linked with an aqueous solution of formaldehyde or glutaraldehyde to form a non-soluble water penetrable matrix on the exterior surface of the carrier. 
     In the present process one forms a plurality of carriers or water treatment members typically an ⅛ inch or smaller which are suitable for inserting into an inline feeder. The carrier which comprises zinc pellets have a silver chloride coating so the water treatment pellet can be used in water filtration and treatment systems to kill and remove bacteria. The zinc pellets which comprise the carrier can be formed from zinc wire by cutting the zinc wire into cylindrical sections about an ⅛ of an inch long. 
     The following example illustrates how a silver chloride coating was affixed proximate to the exterior surface of a zinc pellet. 
     EXAMPLE 1 
     In order to coat a batch of zinc pellets with an adhesive matrix containing silver chloride one mixes 12.5 grams of silver nitrate in 25 ml of distilled water to form an aqueous silver nitrate mixture. 
     Next one mixes 1.5 grams of gelatin in 25 mil of distilled water to form a gelatin mixture. The gelatin mixture is heated to a temperature of about 140 degrees F. 
     To eliminate lumps in the gelatin mixture the gelatin mixture is strained through a screen. At this point 5 grams of sodium chloride are mixed into the gelatin mixture. The gelatin mixture was then combined with the aqueous silver nitrate mixture to convert the silver nitrate into silver chloride to thereby form an aqueous silver chloride gelatin mixture. A batch of zinc pellets having a maximum dimension of about ⅛ inch were heated to about 140 degrees F. The pellets are then sprayed with the heated aqueous, silver chloride, gelatin mixture. In order to form a matrix to affix the silver chloride to the zinc pellets the a silver chloride gelatin mixture were immersed in a aqueous bath of glutaraldehyde for about 12 hours to react the gelatin with the glutaraldehyde. The curing produce an adhesive matrix that secured the zinc pellets with the silver chloride that is dispersed throughout the adhesive matrix. After curing the zinc pellets, which are covered with a coating of silver chloride, were rinsed and air dried to produce zinc pellets with a silver chloride coating affixed proximate to the zinc pellets. 
     EXAMPLE 2 
     The above process was repeated except instead of immersing the zinc particles with the silver chloride gelatin mixture in an aqueous bath of formaldehyde the zinc particle with the silver chloride gelatin mixture were cured in an aqueous bath of formaldehyde. 
     In the above examples the zinc pellets had a maximum dimension of about ⅛ of an inch. Larger or smaller pellets could be used; however, for use as a water treatment composition in a dispensing valve it is preferred to have carrier in multiple pellets in order to present a large surface area to the water containing the bacteria. 
     In the preferred method the adhesive used was gelatin as the gelatin is capable of adhering to the surfaces of both the zinc and the silver chloride. That is, gelatin which can be cross linked in the presence of formaldehyde or glutaraldehyde to obtain the necessary adhesive characteristics remains non-soluble in the water and unreactive with either the zinc or the silver chloride and thus can hold the silver chloride proximate the zinc. That is the cross linked gelatin not only forms a surface attachment but forms a matrix to support or secure the silver chloride in proximity to the surface of the zinc pellet. As the gelatin matrix is securable to the surfaces of both the silver chloride and to the zinc pellets one is assured that the silver and zinc will remain proximate each other so that the regenerative, coactive relationship between the zinc and silver can be retained. While other adhesives could be used gelatin is preferred as it does not leave unwanted residues that might be dissolved in the water during the water treatment process. Also the gelatin is desirable since the porosity of the adhesive matrix formed from gelatin allows bacteria containing water access to both the zinc and the silver to enable the both the zinc and the silver to coactively kill the bacteria in the water.