Abstract:
As etch-stop films or Cu-diffusion barrier films used in insulation films constituting conductor layers of a stacked structure, films having smaller dielectric constant than silicon nitride films are used, and an insulation film at a lower-layer part of the stacked structure is made to have smaller dielectric constant than that at an upper-layer part thereof, and further this insulation film is a silicon oxide (SiO) film and has, in the interior thereof, nano-pores of from 0.05 nm or more to 4 nm or less in diameter as chief construction. This makes it possible to dramatically reduce effective dielectric constant while keeping the mechanical strength of the conductore layers themselves, and can materialize a highly reliable and high-performance semiconductor device having mitigated the wiring delay of signals which pass through wirings.

Description:
BACKGROUND OF THE INVENTION  
       [0001]     1. Field of the Invention  
         [0002]     This invention relates to a semiconductor device in which low-dielectric-constant insulators are used as interconnecting insulation layers (interlayer insulation films) so as to mitigate any wiring delay of signals (delay in wirings of interconnection) to improve device performance.  
         [0003]     2. Description of the Related Art  
         [0004]     As semiconductor devices are made to have higher integration and smaller chip size, wirings are being made to scale down in length, to have narrower wiring pitches and to be formed in a larger number of metal layers (i.e., wirings are being made finer, more narrow-pitch and more multiple-layer). With such progress, the delay coming when signals pass through wirings, i.e., the wiring delay tends to increase. This is a problem of great proportions in using electronic equipment making use of semiconductor devices.  
         [0005]     In general, the speed of signals which pass through wirings depends on the product (RC) of wiring resistance (R) and wiring-to-wiring capacitance (C). Hence, in order to mitigate the wiring delay, it is necessary to make the wiring-to-wiring capacitance small, i.e., to make the interconnecting insulation layer have a low dielectric constant.  
         [0006]     As measures to lower the wiring resistance, it is set forward in high-performance semiconductor devices to change their wiring material from aluminum to copper. In particular, the damascene structure where copper wirings are buried in interconnecting insulation layers is actively applied in processing.  
         [0007]     As measures to make the interconnecting insulation layer have a low dielectric constant, inorganic materials such as a silicon oxide film (SiO 2 : dielectric constant about 4.0) and a silicon nitoride film (SiN: dielectric constant about 7.0) formed by CVD (chemical vapor deposition) have conventionally been used in interconnecting insulation layers of semiconductor devices. Then, recently, these are succeeded by employment of a fluorine-dopped silicon oxide film (SiOF: dielectric constant about 3.6) as a material with low dielectric constant that can continue conventional processes.  
         [0008]     However, the fluorine-doped silicon oxide film has a relatively high dielectric constant, and can not have a sufficient effect of lessening the wiring-to-wiring capacitance when it is used as the interconnecting insulation layer. Accordingly, in semiconductor devices since the generation of wiring process of 90 nm nodes, materials having much lower dielectric constant are required.  
         [0009]     As materials of interconnecting insulation layers having a property that the dielectric constant is lower than 3.5, various materials are proposed. In rough classification, studies are made on what is called spin-on-glass materials with which substrates are coated followed by heating to form films, on organic materials similarly formed into films, and on methods of forming films by CVD.  
         [0010]     As the spin-on-glass materials, there are materials containing a hydrogen silsesquioxane compound, a methyl silsesquioxane compound, and the like. The materials composed chiefly of a hydrogen silsesquioxane compound or a methyl silsesquioxane compound are preferred. In the present specification, a chief ingredient is a compounent of the hightest combination ratio (a mole ratio).  
         [0011]     A coating solution composed chiefly of the hydrogen silsesquioxane compound is one prepared by dissolving the compound, which is represented by the general formula: (HSiO 3/2 ) n , in a solvent such as methyl isobutyl ketone. A substrate is coated with this solution, which is then subjected to intermediate heating at a temperature of approximately from 100° C. to 250° C., followed by heating at a temperature of from 350° C. to 450° C. in an inert atmosphere, e.g., in an atmosphere of nitrogen, so that an insulation layer is formed in which Si—O—Si bond networks are formed in ladder structure and which is finally chiefly composed of SiO.  
         [0012]     A coating solution composed chiefly of the methyl silsesquioxane compound is one prepared by dissolving the compound, which is represented by the general formula: (CH 3 SiO 3/2 ) n , in a solvent such as methyl isobutyl ketone. A substrate is coated with this solution, which is then subjected to intermediate heating at a temperature of approximately from 100° C. to 250° C., followed by heating at a temperature of from 350° C. to 450° C. in an inert atmosphere, e.g., in an atmosphere of nitrogen, so that an insulation layer is formed in which Si—O—Si bond networks are formed in ladder structure and which is finally chiefly composed of SiO.  
         [0013]     As organic insulation layer materials, polymeric materials such as polyimide, poly(p-xylylene), poly(arylene) ether, poly(arylene), benzcyclobutene and polynaphthalene, which are hydrocarbon type resins, are known in the art. These materials contain carbon atoms, in virtue of which the film is made to have a low density, and also the polarizability of molecules (monomers) themselves is made small, in virtue of which the film achieves a low dielectric constant.  
         [0014]     As methods of more reducing the dielectric constant of interconnecting insulation layers such as the above spin-on-glass films, organic films and CVD films, it is known to form nano-pores in films to make the films into porous films. With regard to the above materials and processes, they are disclosed in International Technology Roadmap for Semiconductors, 1999 Edition, pp. 163-186, and Japanese Patent Applications Laid-open No. 2000-340569 and No. 2001-274239.  
         [0015]     However, in the above related art, the interconnecting insulation layers having the property that the dielectric constant is lower than 3.5 involve a problem that the insulation layers have fundamentally lower mechanical strength such as hardness and elastic modulus than the Silicon oxide film and Silicon nitride film formed by CVD.  
         [0016]     In such insulation layers, it has been considered not realistic that the nano-pores are formed in films to make the films into porous films in order to more reduce the dielectric constant, because this may come toward further deterioration of mechanical strength.  
         [0017]     As a means for lowering the dielectric constant of insulation layers, insulating organic polymers such as polyimide are used in some cases. Such organic polymers are favorable because their dielectric constant is less than 4, but have disadvantages that they physically have a lower mechanical strength and also higher hygroscopicity and moisture permeability than inorganic films. When used as interconnecting insulation layers, they may also cause a problem on the reliability of devices, e.g., a lowering of mechanical strength of device structure and corrosion of wirings which is due to absorbed moisture.  
       SUMMARY OF THE INVENTION  
       [0018]     Accordingly, especially in multi-layer wiring semiconductor devices employing the damascene structure where copper wirings are filled in interconnecting insulation layers, the present inventors have made studies on how to lower the dielectric constant of the whole of interconnecting insulation layers while keeping the mechanical strength of device structure from lowering.  
         [0019]     Under the technical background as stated above, the present invention proposes a method in which a stacked structure made up of the film with a low dielectric constant and the film with a high dielectric constant as stated above is formed and also the combination and structure of their materials are made optimum so that the achievement of both electrical properties and mechanical properties of insulation layers themselves can be materialized.  
         [0020]     In particular, the present invention has made it possible to provide, in a semiconductor device having a stacked structure employing a damascene structure where copper wirings made to have low wiring resistance are filled in interconnecting insulation layers, a semiconductor device having highly reliable and high-performance characteristics which has mitigated the wiring delay of signals (delay in wirings of interconnection) while keeping the mechanical strength of interconnecting insulation layers from lowering.  
         [0021]     The semiconductor device of the present invention is a semiconductor device having a substrate on which-transistor elements and semiconductor circuit components have been formed, and stacked thereon a plurality of sets of conductor layers each having i) a first insulation layer, a second insulation layer and a third insulation layer and ii) a conductor wiring having been so formed as to extend through these three layers. Here, the insulation layers are so formed that the first and third insulation layers constituting each conductor layer are formed of silicon carbonitride, silicon carbide or silicon oxide, and a second insulation layer of a conductor layer positioned at a lower-layer part among the conductor layers contains silicon oxide, and a second insulation layer of a conductor layer positioned at an upper-layer part among them contains fluorine-doped silicon oxide or carbon-doped silicon oxide.  
         [0022]     Here, where copper wiring is used as conductor wiring to serve as a component, the first insulation layer serves as an etch-stop film when insulation layers are holed in order to fill with the copper wiring. The third insulation layer also serves as a Cu-diffusion barrier film of the copper wiring.  
         [0023]     Conventionally, silicon nitride films are used as the etch-stop film and Cu-diffusion barrier film. In the present invention, a film comprised of silicon carbonitride (Si—C—N: dielectric constant about 4.6), silicon carbide (Si—C: dielectric constant about 4.4) or silicon oxide is used, having lower dielectric constant than silicon nitride, and hence, even in the whole of conductor layers formed in multi-layer stacked structure, its dielectric constant can be reduced.  
         [0024]     The second insulation layer of a conductor layer positioned at an upper-layer part among the conductor layers is formed of fluorine-doped silicon oxide or carbon-doped silicon oxide (dielectric constant: about 2.9). This enables more reduction of the dielectric constant of the whole of conductor layers than in a case in which all the second insulation layers constituting the corresponding conductor layers are formed of silicon oxide.  
         [0025]     The semiconductor device of the present invention is also so constructed that the second insulation layer of a conductor layer positioned at a lower-layer part is comprised of an insulating film material having a dielectric constant of less than 3.0 and the second insulation layer of a conductor layer positioned at an upper-layer part is formed of fluorine-doped silicon oxide or carbon-doped silicon oxide. That is, the second insulation layers are made to differ in constituents between the conductor layer positioned at a lower-layer part and the conductor layer positioned at an upper-layer part so that the latter insulation layer can have a smaller dielectric constant than the former insulation layer.  
         [0026]     The semiconductor device of the present invention is also so constructed that the second insulation layer of a conductor layer positioned at a lower-layer part is an insulation film having characteristics of a dielectric constant of less than 3.0 and containing SiO and that more than half of nano-pores present in the insulation film are chiefly comprised of pores of from 0.05 nm or more to 4 nm or less in diameter. In the present invention, as having the nano-pores in the film, the film density can be reduced, and, as making use of the insulation film having characteristics of a dielectric constant of less than 3.0 and containing SiO, the dielectric constant can be more reduced in the whole of conductor layers formed in multi-layer stacked structure.  
         [0027]     Here, a method may be used in which the nano-pores are formed in the insulation film to lower its density and make-its dielectric constant to that of vacuum. This can make the dielectric constant of the insulation film lower than the dielectric constant of the silicon oxide film. In particular, the size and density of such nano-pores maybe controlled. This enables formation of an insulation film having any desired dielectric constant.  
         [0028]     However, the size of the nano-pores to be incorporated in the insulation film must be controlled with great care because, if the nano-pores have a large diameter, problems may instead arise such that the mechanical strength as a structure of the insulation film lowers and the leak current flows greatly through the insulation film to lower the breakdown strength that is a characteristic feature as the insulation film.  
         [0029]     Accordingly, in the present invention, the range of pore diameter is controlled so that the mechanical strength and breakdown strength of the insulation film can be kept from lowering. Here, the nano-pores may chiefly comprise pores of from 0.05 nm or more to 4 nm or less in diameter. In such a case, a semiconductor device having high reliability can be provided without lowering the mechanical strength of the insulation film.  
         [0030]     The insulation film having the above nano-pores is formed of an insulation film composed chiefly of SiO, obtained by heating a spin-on film composed chiefly of a hydrogen silsesquioxane compound or a methyl silsesquioxane compound.  
         [0031]     A coating solution composed chiefly of the hydrogen silsesquioxane compound is one prepared by dissolving the compound, which is represented by the general formula: (HSiO 3/2 ) n , in a solvent such as methyl isobutyl ketone. Also, a coating solution composed chiefly of the methyl silsesquioxane compound is one prepared by dissolving the compound, which is represented by the general formula: (CH 3 SiO 3/2 ) n , in a solvent such as methyl isobutyl ketone.  
         [0032]     A substrate may be coated with any of these solutions, Which is then subjected to intermediate heating at a temperature of approximately from 100° C. to 250° C., followed by heating at a temperature of from 350° C. to 450° C. in an inert atmosphere, e.g., in an atmosphere of nitrogen, so that Si—O—Si bond networks are formed in ladder structure and finally an insulation layer composed chiefly of SiO is formed.  
         [0033]     In the insulation film composed chiefly of SiO, obtained by heating the spin-on film composed chiefly of the hydrogen silsesquioxane compound or methyl silsesquioxane compound, as a technique by which the diameter of the pores present in the insulation film is controlled, a method is available in which, e.g., a silsesquioxane compound solution is incorporated with components other than the solvent such as methyl isobutyl ketone so that the traces made upon decomposition of the main component in the film can form the pores, where the formation of pores is controlled by regulating film formation temperature to change the behavior of decomposition so that the range of pore diameter can be kept within a selective range.  
         [0034]     As a method of coating the solution for forming the insulation film, it may include rotary coating, slit coating and printing. Then, the spin-on film thus formed is heated to form the insulation film. Hence, even where fine wirings are formed in a high density, a good step coverage can be achieved, compared with insulation films formed by CVD. Thus, this is advantageous in that any surface steps can be settled.  
         [0035]     To deal with silicon wafers made to have larger diameter, a large-size film formation apparatus is required when insulation films are formed by CVD, and it follows that the cost of installation has a great influence on device cost. To solve such a problem, in the present invention, the insulation film is formed by a coating-and-heating system, and hence the installation cost can vastly be reduced. Thus, a great effect can be expected such that the investment cost of manufacture lines and further the device cost can be cut down.  
         [0036]     In the case when the insulation film is formed by CVD, an alkylsilane compound or an alkoxysilane compound is used in a source gas as a chief component, and an insulation film finally chiefly composed of SiO is formed by ECR (electron cyclotron resonance), plasma-assisted CVD or the like.  
         [0037]     In this case also, as a technique by which the diameter of the pores present in the insulation film is controlled, a method is available in which, e.g., a component having a high thermal decomposition temperature is fed as a source gas and the film is formed with heating at 350° C. to 450° C. so that the traces made upon decomposition of the main component in the film can form the pores.  
         [0038]     In such a technique, the component having a high thermal decomposition temperature may be selected in variety, where the behavior of decomposition can be changed by regulating film formation temperature. Thus, the formation of pores may be controlled so that the range of pore diameter can be kept within a selective range.  
         [0039]     The semiconductor device of the present invention also has, in the element and device peripheries, a barrier layer (called a guard ring layer in the present specification) comprised of a material capable of forming conductor wiring, in such a way that it encloses the element and device peripheries in order to prevent moisture absorption and moisture permeation from the surroundings of the semiconductor device. This can obstruct any water content which may come from the element surroundings or from the interface between the substrate and the interconnecting insulation layer, permeating through the interior of the interconnecting insulation layer. 
     
    
     BRIEF DESCRIPTION OF THE DRAWINGS  
       [0040]     These and other features, objects and advantages of the present invention will become more apparent from the following description when taken in conjunction with the accompanying drawings wherein:  
         [0041]      FIG. 1  is a cross-sectional view of a semiconductor device having a stacked structure created in First Example of the present invention.  
         [0042]      FIGS. 2A  to  2 D show a flow sheet for illustrating how to produce the semiconductor device of First Example.  
         [0043]      FIG. 3  is a graph showing diameter distribution of pores present in the insulation film.  
         [0044]      FIG. 4  is a graph showing diameter distribution of pores present in the insulation film.  
         [0045]      FIG. 5  is a flow sheet for illustrating how to produce a semiconductor device having a stacked structure according to Seventeenth Example.  
         [0046]      FIG. 6  is a cross-sectional view for illustrating a logic semiconductor device created in Ninetheenth Example.  
         [0047]      FIG. 7  is a cross-sectional view for illustrating a resin-encapsulated semiconductor device according to Twentieth Example.  
         [0048]      FIG. 8  is a cross-sectional view for illustrating a wafer level chip-size-packaging semiconductor device according to Twenty-first Example.  
         [0049]      FIGS. 9A and 9B  are a cross-sectional view and a plan view, respectively, for illustrating a semiconductor device having a guard ring structure according to Twenty-second Example. 
     
    
     DESCRIPTION OF THE PREFERRED EMBODIMENTS  
       [0050]     Embodiments of the-present invention are described below with reference to the accompanying drawings.  
       FIRST EXAMPLE  
       [0051]     In the First Example, as shown in  FIG. 1 , a six-layer wiring semiconductor device of Cu-wiring dual-damascene structure having six conductor layers  100  is produced.  
         [0052]     On a semiconductor substrate  101  on which constituent elements such as MOS transistors (not shown) were formed by a commonly well known method, a silicon carbonitride film  102  serving as a first insulation layer of a first conductor layer  100   a  was formed by CVD in a thickness of 40 nm. This first insulation layer serves as an etch-stop film when a hole is formed for forming a wiring pattern.  
         [0053]     Next, a silicon oxide film  103  serving as a second insulation layer of the first conductor layer  100   a  was formed by CVD in a thickness of 400 nm.  
         [0054]     Next, a silicon carbonitride film  104  serving as a third insulation layer of the first conductor layer  100   a  was formed by CVD in a thickness of 40 nm. This film serves as a first insulation layer of a second conductor layer  100 a, and plays a role also as an etch-stop film or Cu-diffusion barrier film when a hole is formed for forming a wiring pattern.  
         [0055]     Next, a hole  117  was formed in the silicon carbonitride film  104 . The hole was formed using a photoresist and by forming a resist pattern by a known technique, followed by dry etching using the resist as a mask and using an etching gas capable of removing the silicon carbonitride film ( FIG. 2A ). Here, the hole is in a wiring size of the first conductor layer  100   a.    
         [0056]     Next, in the same manner as the formation of the insulation layers of the first conductor layer  100   a , a silicon oxide film  105  serving as a second insulation layer of the second conductor layer  100   a  was formed in a thickness of 400 nm, and a silicon carbonitride film  106  serving as a third insulation layer in a thickness of 40 nm.  
         [0057]     Next, a hole  118  was formed in the silicon carbonitride film  106  ( FIG. 2B ). The hole was formed using a photoresist and by forming a resist pattern by a known technique, followed by dry etching using the resist as a mask and using an etching gas capable of removing the silicon carbonitride film.  
         [0058]     Next, using the silicon carbonitride film  106  as a mask, a hole was formed in the silicon oxide film  105  by dry etching using a CF type gas capable of removing the silicon oxide film. Thus, at its lower part, the silicon oxide film  103  was uncovered through the hole  117  of the silicon carbonitride film  104 .  
         [0059]     Subsequently, using the silicon carbonitride film  104  as a mask, a hole was formed in the silicon oxide film  103  through the former&#39;s hole  117 . Thus, at its lower part, the silicon carbonitride film  102  was uncovered.  
         [0060]     Subsequently, the etching gas was changed for one capable of removing the silicon carbonitride film  102 , and then, using the silicon oxide film  103  as a mask, the silicon carbonitride film  102  was removed by dry etching through the former&#39;s hole to form a hole extending therethrough to reach the semiconductor substrate  101 . Here, the periphery of the hole  117  of the silicon carbonitride film  104  was also etched to make the hole  117  expand to the same size as the hole  118  of the uppermost silicon carbonitride film  106 . Thus, a wiring trench  119  was formed which extended through the layers to reach the semiconductor substrate  101  ( FIG. 2C ).  
         [0061]     Next, a barrier metal layer  120  was formed on the inner surfaces of the wiring trench  119 , and thereafter the wiring trench  119  was filled with Cu  121  by well known plating. As the barrier metal, TiN was used in this Example.  
         [0062]     Then, any unnecessary Cu film present on the uppermost silicon carbonitride film  106  was removed and the surface was cleaned to form a connecting plug and a wiring at the same time. To remove the Cu film, it is advantageous to use alumina or silica as abrasive grains and employ chemical mechanical polishing making use of an abrasive comprised of additives such as a Cu complexing agent and a surface-active agent.  
         [0063]     In this polishing step, the silicon carbonitride film  106  corresponding to the uppermost layer was also removed by polishing. Thus, a dual-damascene structure in which a Cu wiring (inclusive of  120  and  121 ) was formed was produced. ( FIG. 2D )  
         [0064]     Subsequently, the same process as the above was repeated twice to form a third conductor layer  100   c —a sixth conductor layer  100   f , and a six-layer Cu wiring structure is obtained. Here, insulation layers  106 ,  108 ,  110  and  112  are formed of silicon carbonitride films formed by CVD, and insulation layers  107  and  109  are formed of silicon oxide films. Also, insulation layers  111  and  113  are formed of fluorine-doped silicon oxide films.  
         [0065]     Next, a silicon nitride film  114  was formed as the uppermost layer to produce a multi-layer wiring semiconductor device made up of a six-layer Cu wiring  115  ( FIG. 1 ).  
         [0066]     Thus, a high-performance semiconductor device was obtained the dielectric constant of the whole of interconnecting insulation layers of which was lowered in virtue of the use of, as the etch-stop films or Cu-diffusion barrier films, the silicon carbonitride films having lower dielectric constant than silicon nitride films and also in virtue of the use of, in the upper-layer part of the multi-layer stacked structure, the fluorine-doped silicon oxide films having smaller dielectric constant than silicon oxide films.  
       SECOND EXAMPLE  
       [0067]     In this Example, using the same techniques as those in First Example, fluorine-doped silicon oxide films (SiOF films) were formed by CVD also in respect of the insulation layers  107  and  109 . Next, the silicon nitride film  114  was formed as the uppermost layer to produce a multi-layer wiring semiconductor device made up of a six-layer Cu wiring  115 .  
         [0068]     Thus, a high-performance semiconductor device was obtained the dielectric constant of the whole of interconnecting insulation layers of which was lowered in virtue of the use of, as the etch-stop films or Cu-diffusion barrier films, the silicon carbonitride films having lower dielectric constant than silicon nitride films and also in virtue of the use of, in the ⅓ (from the bottom) or more upper-layer part of the multi-layer stacked structure, the fluorine-doped silicon oxide films having smaller dielectric constant than silicon oxide films.  
       THIRD EXAMPLE  
       [0069]     In this Example, using the same techniques as those in First Example, silicon carbide films were formed by CVD in respect of the insulation-layers  102 ,  104 ,  106 ,  108 ,  110  and  112 . Next, the silicon nitride film  114  was formed as the uppermost layer to produce a multi-layer wiring semiconductor device made up of a six-layer Cu wiring 1:15.  
         [0070]     Thus, a high-performance semiconductor device was obtained the dielectric constant of the whole of interconnecting insulation layers of which was lowered in virtue of the use of, as the etch-stop films or Cu-diffusion barrier films, the silicon carbide films having lower dielectric constant than silicon nitride films.  
       FOURTH EXAMPLE  
       [0071]     In this Example, using the same techniques as those in Second Example, silicon carbide films (SiC films) were formed by CVD in respect of the insulation layers  102 ,  104 ,  106 ,  108 ,  110  and  112 . Next, the silicon nitride film  114  was formed as the uppermost layer to produce a multi-layer wiring semiconductor device made up of a six-layer Cu wiring  115 .  
         [0072]     Thus, a high-performance semiconductor device was obtained the dielectric constant of the whole of interconnecting insulation layers of which was lowered in virtue of the use of, as the etch-stop films or Cu-diffusion barrier films, the silicon carbide films having lower dielectric constant than silicon nitride films.  
       FIFTH EXAMPLE  
       [0073]     In this Example, using the same techniques as those in First-Example, carbon-doped silicon oxide films were formed by CVD also in respect of the insulation layers  111  and  113  to produce a multi-layer wiring semiconductor device made up of a six-layer Cu wiring  115 .  
         [0074]     Thus, a high-performance semiconductor device was obtained the dielectric constant of the whole of interconnecting insulation layers of which was lowered in virtue of the use of, in the upper-layer part of the multi-layer stacked structure, the carbon-doped silicon oxide films having smaller dielectric constant than silicon oxide films.  
       SIXTH EXAMPLE  
       [0075]     In this Example, using the same techniques as those in Second Example, carbon-doped silicon oxide films were formed by CVD also in respect of the insulation layers  107 ,  109 ,  111  and  113  to produce a multi-layer wiring semiconductor device made up of a six-layer Cu wiring  115 .  
         [0076]     Thus, a high-performance semiconductor device was obtained the dielectric constant of the whole of interconnecting insulation layers of which was lowered in virtue of the use of, in the ⅓ (from the bottom) or more upper-layer part of the multi-layer stacked structure, the carbon-doped silicon oxide films having smaller dielectric constant than silicon oxide films.  
       SEVENTH EXAMPLE  
       [0077]     In this Example, using the same techniques as those in Fifth Example, silicon carbide films (SiC films) were formed by CVD in respect of the insulation layers  102 ,  104 ,  106 ,  108 ,  110  and  112 . Next, the silicon nitride film  114  was formed as the uppermost layer to produce a multi-layer wiring semiconductor device made up of a six-layer Cu wiring  115 .  
         [0078]     Thus, a high-performance semiconductor device was obtained the dielectric constant of the whole of interconnecting insulation layers of which was lowered in virtue of the use of, as the etch-stop films or Cu-diffusion barrier films, the silicon carbide films having lower dielectric constant than silicon nitride films.  
       EIGHTH EXAMPLE  
       [0079]     In this Example, using the same techniques as those in Sixth Example, silicon carbide films were formed by CVD in respect of the insulation layers  102 ,  104 ,  106 ,  108 ,  110  and  112 . Next, the silicon nitride film  114  was formed as the uppermost layer to produce a multi-layer wiring semiconductor device made up of a six-layer Cu wiring  115 .  
         [0080]     Thus, a high-performance semiconductor device was obtained the dielectric constant of the whole of interconnecting insulation layers of which was lowered in virtue of the use of, as the etch-stop films or Cu-diffusion barrier films, the-silicon carbide films having lower dielectric constant than silicon nitride films.  
       NINTH EXAMPLE  
       [0081]     In this Example, using the same techniques as those in First Example, carbon-doped silicon oxide films were formed by CVD in respect of the insulation layers  103 ,  105 ,  107  and  109  to produce a multi-layer wiring semiconductor device made up of a six-layer Cu wiring  115 .  
         [0082]     Thus, a high-performance semiconductor device was obtained the dielectric constant of the whole of interconnecting insulation layers of which was lowered in virtue of the use of, in the lower-layer part of the multi-layer stacked structure, as the insulation films the carbon-doped silicon oxide films having small dielectric constant and also in virtue of the use of, in the upper-layer part of the multi-layer stacked structure, the fluorine-doped silicon oxide films having smaller dielectric constant than silicon oxide films.  
       TENTH EXAMPLE  
       [0083]     In this Example, using the same techniques as those in Second Example, carbon-doped silicon oxide films were formed by CVD in respect of the insulation layers  103  and  105  to produce a multi-layer wiring semiconductor device made up of a six-layer Cu wiring  115 .  
         [0084]     Thus, a high-performance semiconductor device was obtained the dielectric constant of the whole of interconnecting insulation layers of which was lowered in virtue of the use of, in the lower-layer part of the multi-layer stacked structure, as the insulation films the carbon-doped silicon oxide films having small dielectric constant and also in virtue of the use of, in the ⅓ (from the bottom) or more upper-layer part of the multi-layer stacked structure, the fluorine-doped silicon oxide films having smaller dielectric constant than silicon oxide films.  
       ELEVENTH EXAMPLE  
       [0085]     In this Example, using the same techniques as those in Third Example, carbon-doped silicon oxide films were formed by CVD in respect of the insulation layers  103 ,  105 ,  107  and  109  to produce a multi-layer wiring semiconductor device made up of a six-layer Cu wiring  115 .  
         [0086]     Thus, a high-performance semiconductor device was obtained the dielectric constant of the whole of interconnecting insulation layers of which was lowered in virtue of the use of, in the lower-layer part of the multi-layer stacked structure, as the insulation films the carbon-doped silicon oxide films having small dielectric constant, and also in virtue of the use of, in the upper-layer part of the multi-layer stacked structure, the fluorine-doped silicon oxide films having smaller dielectric constant than silicon oxide films and the use of, as the etch-stop films or Cu-diffusion barrier films, the silicon carbide films having lower dielectric constant than silicon nitride films.  
       TWELFTH EXAMPLE  
       [0087]     In this Example, using the same techniques as those in Fourth Example, carbon-doped silicon oxide films were formed by CVD in respect of the insulation layers  103  and  105  to produce a multi-layer wiring semiconductor device made up of a six-layer Cu wiring  115 .  
         [0088]     Thus, a high-performance semiconductor device was obtained the dielectric constant of the whole of interconnecting insulation layers of which was lowered in virtue of the use of, in the lower-layer part of the multi-layer stacked structure, the carbon-doped silicon oxide films having small dielectric constant, and also in virtue of the use of, in the ⅓ (from the bottom) or more upper-layer part of the multi-layer stacked structure, the fluorine-doped silicon oxide films having smaller dielectric constant than silicon oxide films and the use of, as the etch-stop films or Cu-diffusion barrier films, the silicon carbide films having lower dielectric constant than silicon nitride films.  
       THIRTEENTH EXAMPLE  
       [0089]     In this Example, using the same techniques as those in First Example, in respect of the insulation layers  103 ,  105 ,  107  and  109 , spin-on films of a methyl isobutyl ketone solution composed chiefly of the hydrogen silsesquioxane compound were formed on the substrate, and thereafter heated at 100° C. for 10 minutes and then at 150° C. for 10 minutes and further at 230° C. for 10 minutes in an atmosphere of nitrogen by means of a hot plate.  
         [0090]     Then, the films were further heated at 350° C. for 30 minutes in an atmosphere of nitrogen by means of a furnace to form insulation films in which Si—O—Si bond networks were formed in ladder structure and which were finally chiefly composed of SiO and had the pore-formation-controlled nano-pores in films. Thus, a multi-layer wiring semiconductor device made up of a six-layer Cu wiring  115  was produced. The holes were formed by dry etching using a CF type gas capable of etching SiO.  
         [0091]     In the case of this Example, the above insulation layers are insulation films in which nano-pores having distribution characteristics (diameter distribution) as shown in FIG.  3 , chiefly containing pores of from 0.05 nm or more to 4 nm or less in diameter, are present, having dielectric constant of about 2.3.  
         [0092]     The diameter distribution is determined by calculating diameter distribution of scattering matter in comparison with theoretical scattering intensity based on scattering functions which assume spherical scattering matter, on the basis of X-ray reflection measurement data and X-ray diffuse scattering measurement data which are obtained using an X-ray diffractometer for thin film evaluation (model: ATX-G) manufactured by Rigaku Corporation.  
         [0093]     The above insulation films having the nano-pores in films also have characteristics of a Young&#39;s modulus of 12 Ga. For these characteristics, in respect of like films of 250 nm in layer thickness which have been formed on silicon wafers, the hardness of the films is determined on the basis of the hardness at a surface layer point of ⅕ of the total layer thickness, by indentation micromechanical testing making use of Nano Indenter XP, manufactured by MTS Systems Corporation in U.S.A.  
         [0094]     The Young&#39;s modulus is also the value at the surface layer point of ⅕ of the total layer thickness and is the value calculated on the basis of the Poisson&#39;s ratio 0.17 of molten quartz. A silicon oxide film deposited with p-TEOS (plasma-Tetra-Ethly-Urtho-Silicate) called p-TEOS film in the present specification having substantially the same layer thickness and whose Young&#39;s modulus has been determined by the same method has characteristics of a Young&#39;s modulus of 70 Ga.  
         [0095]     From the foregoing, the insulation films having the nano-pores in films were films having a Young&#39;s modulus of about 17% of that of the p-TEOS film, and low-dielectric-constant insulation films having superior mechanical properties were obtained, compared with low-dielectric-constant insulation films disclosed in Japanese Patent Application Laid-open No. 2000-340569.  
         [0096]     Thus, a high-performance semiconductor device was obtained the dielectric constant of the whole of interconnecting insulation layers of which was lowered, keeping the mechanical strength of element structure from lowering, in virtue of the use of, in the lower-layer part of the multi-layer stacked structure, the insulation films having dielectric constant of less than 2.5 and superior film strength and also in virtue of the use of, in the upper-layer part of the multi-layer stacked structure, the fluorine-doped silicon oxide films having smaller dielectric constant than silicon oxide films.  
       FOURTEENTH EXAMPLE  
       [0097]     In this Example, using the same techniques as those in Thirteenth Example, silicon carbide films were formed by CVD in respect of the insulation layers  102 ,  104 ,  106 ,  108 ,  110  and  112 . Next, the silicon nitride film  114  was formed as the uppermost layer to produce a multi-layer wiring semiconductor device made up of a six-layer Cu wiring  115 .  
         [0098]     Thus, low-dielectric-constant insulation films having superior mechanical properties were obtained in virtue of the use of, as the etch-stop films or Cu-diffusion barrier films, the silicon carbide films having lower dielectric constant than silicon nitride films and also in virtue of the use of the insulation films having the nano-pores in films, specifying their pore diameter.  
         [0099]     Then, a high-performance semiconductor device was further obtained the dielectric constant of the whole of interconnecting insulation layers of which was lowered, keeping the mechanical strength of element structure from lowering, in virtue of the use of, in the lower-layer part of the multi-layer stacked structure, as the second insulation layers the insulation films having dielectric constant of less than 2.5 and superior film strength and also in virtue of the use of, in the upper-layer part of the multi-layer stacked structure, the fluorine-doped silicon oxide films having smaller dielectric constant than silicon oxide films.  
       FIFTEENTH EXAMPLE  
       [0100]     In this Example, using the same techniques as those in Thirteenth Example, in respect of the insulation layers  103 ,  105 ,  107  and  109 , spin-on films of a methyl isobutyl ketone solution composed chiefly of the hydrogen silsesquioxane compound were formed on the substrate, and thereafter heated at 100° C. for 10 minutes and then at 150° C. for 10 minutes and further at 230° C. for 10 minutes in an atmosphere of nitrogen by means of a hot plate.  
         [0101]     Then, the films were further heated at 350° C. for 30 minutes in an atmosphere of nitrogen by means of a furnace to form insulation films in which Si—O—Si bond networks were formed in ladder structure and which were finally chiefly composed of SiO and had the pore-formation-controlled nano-pores in films. Thus, a multi-layer wiring semiconductor device made up of a six-layer Cu wiring  115  was produced. The holes were formed by dry etching using a gas capable of etching SiO.  
         [0102]     In the case of this Example, the above insulation layers are insulation films in which nano-pores having distribution characteristics (diameter distribution) as shown in  FIG. 3 , chiefly containing pores of from 0.05 nm or more to 4 nm or less in diameter, are present, having dielectric constant of about 2.7.  
         [0103]     The diameter distribution is determined by calculating diameter distribution of scattering matter in comparison with theoretical scattering intensity based on scattering functions which assume spherical scattering matter, on the basis of X-ray reflection measurement data and X-ray diffuse scattering measurement data which are obtained using an X-ray diffractometer for thin film evaluation (model: ATX-G) manufactured by Rigaku International Corporation.  
         [0104]     The above insulation films having the nano-pores in films also have characteristics of a Young&#39;s modulus of 11 Ga. For these characteristics, in respect of like films of 250 nm in layer thickness which have been formed on silicon wafers, the hardness of the films is determined on the basis of the hardness at a surface layer point of ⅕ of the total layer thickness, by indentation micromechanical testing making use of Nano Indenter XP, manufactured by MTS Systems Corporation in U.S.A.  
         [0105]     The Young&#39;s modulus is also the value at the surface layer point of ⅕ of the total layer thickness and is the value calculated on the basis of the Poisson&#39;s ratio 0.17of molten quartz. A p-TEOS film having substantially the same layer thickness and whose Young&#39;s modulus has been determined by the same method has characteristics of a Young&#39;s modulus of 70 Ga.  
         [0106]     From the foregoing, the insulation films having the nano-pores in films were films having a Young&#39;s modulus of about 16% of that of the p-TEOS film, and low-dielectric-constant insulation films having superior mechanical properties were obtained, compared with low-dielectric-constant insulation films disclosed in Japanese Patent Application Laid-open No. 2000-340569.  
         [0107]     Thus, a high-performance semiconductor device was obtained the dielectric constant of the whole of interconnecting insulation layers of which was lowered, keeping the mechanical strength of element structure from lowering, in virtue of the use of, in the lower-layer part of the multi-layer stacked structure, as the second insulation layers the insulation films having dielectric constant of less than 3.0 and superior film strength and also in virtue of the use of, in the upper-layer part of the multi-layer stacked structure, the fluorine-doped silicon oxide films having smaller dielectric constant than silicon oxide films.  
       SIXTEENTH EXAMPLE  
       [0108]     In this Example, using the same techniques as those in Fifteenth Example, silicon carbide films were formed by CVD in respect of the insulation layers  102 ,  104 ,  106 ,  108 ,  110  and  112 . Next, the silicon nitride film  114  was formed as the uppermost layer to produce a multi-layer wiring semiconductor device made up of a six-layer Cu wiring  115 .  
         [0109]     Thus, low-dielectric-constant insulation films having superior mechanical properties were obtained in virtue of the use of, as the etch-stop films or Cu-diffusion barrier * films, the silicon carbide films having lower-dielectric constant than silicon nitride films and also in virtue of the use of the insulation films having the nano-pores in films, specifying their pore diameter. Then, a high-performance semiconductor device was further obtained the dielectric constant of the whole of interconnecting insulation layers of which was lowered, keeping the mechanical strength of element structure from lowering, in virtue of the use of, in the lower-layer part of the multi-layer stacked structure, as the second insulation layers the insulation films having dielectric constant of less than 2.5 and superior film strength and also in virtue of the use of, in the upper-layer part of the multi-layer stacked structure, the fluorine-doped silicon oxide films having smaller dielectric constant than silicon oxide films.  
       SEVENTEENTH EXAMPLE  
       [0110]     Seventeenth Example is an example in which the present invention is applied in forming Cu-wiring dual-damascene structure, and is described with reference to the  FIGS. 5A  to  5 D flow sheet.  
         [0111]     On a semiconductor substrate  501  on which constituent elements such as MOS transistors (not shown) were formed by a commonly well known method, a silicon carbonitride film  502  serving as a first insulation layer of a first conductor layer was formed by CVD in a thickness of 40 nm. This first insulation layer serves as an etch-stop film when a hole is formed for forming a wiring pattern.  
         [0112]     Next, a spin-on film of a methyl isobutyl ketone solution composed chiefly of the hydrogen silsesquioxane compound was formed on the substrate, and thereafter heated at 100° C. for 10 minutes and then at 150° C. for 10 minutes and further at 230° C. for 10 minutes in an atmosphere of nitrogen by means of a hot plate. Then, the film was further heated at 350° C. for 30 minutes in an atmosphere of nitrogen by means of a furnace to form an insulation film in which Si—O—Si bond networks were formed in ladder structure and which was finally chiefly composed of SiO and in which nano-pores having distribution characteristics (diameter distribution) as shown in  FIG. 3 , chiefly containing pores of from 0.05 nm or more to 4 nm or less in diameter, were present, having dielectric constant of about 2.3. This film was formed in a thickness of 400 nm as a second insulation layer  503  of the first conductor layer.  
         [0113]     Next, a silicon carbonitride film  504  serving as a third insulation layer of the first conductor layer was formed by CVD in a thickness of 40 nm. This film serves as a first insulation layer of a second conductor layer, and plays a role also as an etch-stop film or Cu-diffusion barrier film when a hole is formed for forming a wiring pattern.  
         [0114]     Next, a hole  517  was formed in the silicon carbonitride film  504 . The hole was formed using a photoresist and by forming a resist pattern by a known technique, followed by dry etching using the resist as a mask and using an etching gas capable of removing the silicon carbonitride film ( FIG. 5A ). Here, the hole is in a wiring size of the first conductor layer.  
         [0115]     Next, in the same manner as the formation of the second insulation layer  503  of the first conductor layer, an insulation film  505  in which nano-pores having distribution characteristics as shown in  FIG. 3 , chiefly containing pores of from 0.05 nm or more to 4 nm or less in diameter, were present, having dielectric constant of about 2.3, which serves as a second insulation layer of the second conductor layer was formed in a thickness of 400 nm; and a silicon carbonitride film  506  serving as a third insulation layer in a thickness of 40 nm.  
         [0116]     Next, a hole  518  was formed in the silicon carbonitride film  506  ( FIG. 5B ). The hole was formed using a photoresist and by forming a resist pattern by a known technique, followed by dry etching using the resist as a mask and using an etching gas capable of removing the silicon carbonitride film.  
         [0117]     Next, using the silicon carbonitride film  506  as a mask, a hole was formed in the insulation film  505  by dry etching using a gas capable of removing the silicon oxide film. Thus, at its lower part, the insulation film  503  was uncovered through the hole  517  of the silicon carbonitride film  504 .  
         [0118]     Subsequently, using the silicon carbonitride film  504  as a mask, a hole was formed in the silicon oxide film  503  through the former&#39;s hole  517 . Thus, at its lower part, the silicon carbonitride film  502  was uncovered. Subsequently, the etching gas was changed for one capable of removing the silicon carbonitride film  502 , and then, using the silicon oxide film  503  as a mask, the silicon carbonitride film  502  was removed by dry etching through the former&#39;s hole to form a hole extending therethrough to reach the semiconductor substrate  501 . Here, the periphery of the hole  517  of the silicon carbonitride film  504  was also etched to make the hole  517  expand to the same size as the hole  518  of the uppermost silicon carbonitride film  506 . Thus, a wiring trench  519  was formed which extended through the layers to reach the semiconductor substrate  501  ( FIG. 5C ).  
         [0119]     Next, a barrier metal layer  520  was formed on the inner surfaces of the wiring trench  519 , and thereafter the wiring trench  519  was filled with Cu  521  by well known plating. As the barrier metal, TiN was used in this Example.  
         [0120]     Then, any unnecessary Cu film present on the uppermost silicon carbonitride film  506  was removed by chemical mechanical polishing and the surface was cleaned to form a connecting plug and a wiring simultaneously. In this polishing step, the uppermost silicon carbonitride film  506  was not removed by the polishing to leave it. Thus, a dual-damascene structure in which a Cu wiring (inclusive of  520  and  521 ) was formed was produced. ( FIG. 5D )  
         [0121]     Thus, a high-performance semiconductor device was obtained the dielectric constant of the whole of interconnecting insulation layers of which was lowered in virtue of the use of the low-dielectric-constant film as the second insulation layer  503 , which is the chief constituent layer of the interconnecting insulation layers.  
         [0122]     In the construction of this Example, the device has a structure wherein the conductor layers are stacked in two layers. The conductor layers may twice or more repeatedly be stacked to obtain a semiconductor device having multi-layer wiring structure.  
       EIGHTEENTH EXAMPLE  
       [0123]     In this Example, in the same manner as in Seventeenth Example, an SiO insulation film in which nano-pores having distribution characteristics as shown in  FIG. 4 , chiefly containing pores of from 0.05 nm or more to 1 nm or less in diameter, were present, having dielectric constant of about 2.7, was formed in respect of the second insulation layer  503  of the second conductor to produce a dual-damascene structure in which a Cu wiring was formed.  
         [0124]     Thus, a high-performance semiconductor device was obtained the dielectric constant of the whole of interconnecting insulation layers of which was lowered in virtue of the use of the low-dielectric-constant film in respect of the second insulation layer  503 , which is the chief constituent layer of the interconnecting insulation layers. The conductor layers may further twice or more repeatedly be stacked, whereby a high-performance semiconductor device having multi-layer wiring structure can be obtained with ease.  
       NINETEENTH EXAMPLE  
       [0125]      FIG. 6  is a cross-sectional view of a logic semiconductor device. On a semiconductor substrate  601 , an element isolation region  602  was formed by known STI (shallow trench isolation), and MOS transistors  603  were formed in this element isolation region  602  (The hatching of a transistor is omitted for a figure to be looked easily). Then, a silicon oxide film  604  of about 50 nm thick and a BPSG (boron-phosphorus-silicate glass) film  605  of about 500 nm thick were formed by known CVD in order on the surface of the semiconductor substrate  601  inclusive of the MOS transistors  603 , followed by reflow annealing in, e.g., an atmosphere of nitrogen of 800° C. to 900° C.  
         [0126]     Next, the surface of the BPSG film  605  was polished to make flat by chemical mechanical polishing (CMP), and thereafter a contact hole was formed. In this contact hole, a conducting plug  606  was formed. Here, any unnecessary tungsten present on the surface of the BPSG film  605  has been removed by known etchback processing.  
         [0127]     Next, in the same manner as in Seventeenth Example, a silicon carbonitride film  607  serving as a first insulation layer of a first conductor layer. This first insulation layer serves as an etch-stop film when a hole is formed for forming a wiring pattern.  
         [0128]     Next, a spin-on film of a methylisobutyl ketone solution composed chiefly of the hydrogen silsesquioxane compound was formed on the substrate, and thereafter heated at 100° C. for 10 minutes and then at 150° C. for 10 minutes and further at 230° C. for 10 minutes in an atmosphere of nitrogen by means of a hot plate. Then, the film was further heated at 350° C. for 30 minutes in an atmosphere of nitrogen by means of a furnace to form an insulation film in which Si—O—Si bond networks were formed in ladder structure and which was finally chiefly composed of SiO and in which nano-pores having distribution characteristics as shown in  FIG. 3 , chiefly containing pores of from 0.05 nm or more to 4 nm or less in diameter, were present, having dielectric constant of about 2.3. This film was formed in a thickness of 400 nm as a second insulation layer  608  of the first conductor layer.  
         [0129]     Next, a silicon carbonitride film  609  serving as a third insulation layer of the first conductor layer was formed by CVD in a thickness of 40 nm. This film serves as a first insulation layer of a second conductor layer, and plays a role also as an etch-stop film or Cu-diffusion barrier film when a hole is formed for forming a wiring pattern.  
         [0130]     Next, a hole was formed in-the silicon carbonitride film  609 . The hole was formed using a photoresist and by forming a resist pattern by a known technique, followed by dry etching using the resist as a mask and using an etching gas capable of removing the silicon carbonitride film. Here, the hole is in a wiring size of the first conductor layer.  
         [0131]     Next, in the same manner as the formation of the second insulation layer  608  of the first conductor layer, a second insulation layer  610  of a second insulation layer was formed in a thickness of 400 nm; and a silicon carbonitride film  611  serving as a third insulation layer in a thickness of 40 nm.  
         [0132]     Next, a hole was formed in the silicon carbonitride film  611 . Then, using this silicon carbonitride film  611  as a mask, a hole was formed in the insulation film  610  by dry etching using a gas capable of removing the silicon oxide film. Thus, at its lower part, the insulation film  609  was uncovered.  
         [0133]     Subsequently, using the silicon carbonitride film  609  as a mask, a hole was formed in the silicon oxide film  608  through the former&#39;s hole. Then, the etching gas was changed for one capable of removing the silicon carbonitride film  607 , and, using the silicon oxide film  608  as a mask, the silicon carbonitride film  607  was removed by dry etching through the former&#39;s hole to form a hole extending therethrough to reach the conducting plug  606 . Here, the periphery of the hole of the silicon carbonitride film  609  was also etched to make this hole expand to the same size as the hole of the uppermost silicon carbonitride film  611 . Thus, a wiring trench was formed which extended through the layers to reach the conducting plug  606 .  
         [0134]     Next, a barrier metal layer was formed on the inner surfaces of the wiring trench, and thereafter the wiring trench was filled with Cu by well known plating. As the barrier metal, TiN was used in this Example. Then, any unnecessary Cu film present on the uppermost silicon carbonitride film  611  was removed by chemical mechanical polishing and the surface was cleaned to form a connecting plug and a wiring simultaneously. In this polishing step, the uppermost silicon carbonitride film  611  was not removed by the polishing to leave it. Thus, a dual-damascene structure in which a Cu wiring (inclusive of  520  and  521 ) was formed was produced.  
         [0135]     The above steps were repeated to form a four-layer wiring structure.  
         [0136]     Subsequently, the like steps were repeated to further stack a two-layer wiring structure. Here, insulation layers  617 ,  619  and  621  were formed using silicon carbonitride films in a thickness of 40 nm each. Insulation layers  618  and  620  were also formed using silicon carbonitride films in a thickness of 600 nm each. Next, a silicon nitride film  622  was formed as the uppermost layer to produce a multi-layer wiring semiconductor device made up of a six-layer Cu wiring  623 .  
         [0137]     Thus, a high-performance semiconductor device was obtained the dielectric constant of the whole of interconnecting insulation layers of which was lowered in virtue of the use of, as the etch-stop films or Cu-diffusion barrier films, the silicon carbonitride films having lower dielectric constant than silicon nitride films, in virtue of the use of, in the lower-layer part of the multi-layer stacked structure, as the second insulation layers the insulation films having dielectric constant of less than 2.5 and superior film strength and also in virtue of the use of, in the upper-layer part of the multi-layer stacked structure, the fluorine-doped silicon oxide films having smaller dielectric constant than silicon oxide films.  
       TWENTIETH EXAMPLE  
       [0138]      FIG. 7  is a cross-sectional view of a resin-encapsulated logic semiconductor device which is Twentieth Example of the present invention.  
         [0139]     A logic semiconductor device  701  obtained in Nineteenth Example and held in the state that a polyimide surface protective film  702  was formed except the part of bonding pads was fastened to a lead frame in the step of die-bonding. Thereafter, gold wires  704  were attached from chip&#39;s bonding pads to outer leads  706  of the lead frame by means of a wire bonder.  
         [0140]     Next, using a silica-containing biphenyl epoxy type molding resin material, resin encapsulation  703  was so formed as to envelope the logic semiconductor device  701 , the outer leads  706  and so forth. The encapsulation was carried out under conditions of a molding temperature of 180° C. and a molding pressure of 70 kg/cm 2 , but not limited thereto.  
         [0141]     Finally, the outer leads  706  are bent in a given shape to obtain a finished product of the resin-encapsulated logic semiconductor device.  
         [0142]     The insulation films having small dielectric constant but well having kept the mechanical strength from lowering are used in a part of the interconnecting insulation layers of the resin-encapsulated logic semiconductor device. Hence, a resin-encapsulated product can be obtained without causing any cracks in the interior of the device during resin encapsulation processing, against the stress applied to the logic semiconductor device.  
         [0143]     Needless to say that the same effect as that stated in Nineteenth Example can be exhibited as characteristics of the logic semiconductor device, the further encapsulation with resin enables the device to ensure electric performance and reliability from environment.  
       TWENTY-FIRST EXAMPLE  
       [0144]      FIG. 8  is a cross-sectional view for illustrating Twenty-first Example, which is a case in which the logic semiconductor device described in Nineteenth Example is used in wafer level chip-size-packaging products. On the uppermost layer, silicon nitride film  802  of a logic semiconductor device  801 , a polyimide insulation film  804  is formed in such a shape that bonding pads  803  stand uncovered.  
         [0145]     Next, electrical rewiring interconnection (between the die pad and the solder ball)  805  is formed. In this Example, the electrical rewiring interconnection  805  is one consisting of TiN, Cu and Ni three layers formed by sputtering, where, after their film formation, a wiring pattern has been formed by known photolithography technology.  
         [0146]     A polyimide insulation film  806  is further formed thereon. Extending through this polyimide insulation film  806 , under-bump metal layers  807  are provided which are to make electrical connection in some region of the electrical rewiring interconnection  805 . As the under-bump metal layers  807 , three layers of Cr, Ni and Au are formed. Solder balls  808  are formed on the under-bump metal layers  807 .  
         [0147]     High-speed drivable logic semiconductor devices themselves can be formed on wafers by the method described in Nineteenth Example. Hence, this Example enables materialization of a logic semiconductor packaging device having solder balls in the state of a wafer.  
         [0148]     The use of the interconnecting insulation layers having low dielectric constant has already afforded logic semiconductor devices having higher performance than conventional products. However, when packaged semiconductor products are surface-mounted on printed wiring boards (PWBs), the use of the packaged structure as in this Example enables high-speed performance of signal transmission between devices and printed wiring boards and enables further development of the performance of the logic semiconductor device.  
       TWENTY-SECOND EXAMPLE  
       [0149]      FIGS. 9A and 9B  are a cross-sectional view ( FIG. 9A ) and a plan view ( FIG. 9B ) for illustrating Twenty-second Example.  
         [0150]     On a silicon substrate  901 , semiconductor devices  906  (such as MOS transistors) and semiconductor circuits ( 906 ) containing these devices have been formed. On this substrate  901 , the conductor layers described above have been formed. Then, using a material comprised of conductor wiring constituting the conductor layers, guard ring layers  905  are so provided as to surround the semiconductor devices  906  and the semiconductor circuits ( 906 ) containing these devices. These guard ring layers  905  are provided for the purpose of preventing water content from entering the semiconductor devices  906  and the semiconductor circuits ( 906 ) containing these devices, from the outside. These are formed in the step of forming the conductor wiring.  
         [0151]     Thus, especially when the insulation films having nano-pores are used as the interconnecting insulation layers showing characteristics of low dielectric constant, a semiconductor device can be provided which has solved the problems of permeation, or adsorption, of the water content in the interiors of, or on the inner walls of, the pores, and has been improved in moisture resistance reliability of the semiconductor device itself.  
         [0152]     In the above, the present invention has been described in detail giving Examples. Conditions and so forth for accomplishing the present invention and Examples are by no means limited to those of these Examples.  
         [0153]     As having been described above, in the semiconductor device-having multi-layer stacked wirings employing the damascene structure where copper wirings made to have low wiring resistance are buried in interconnecting insulation layers, films having smaller dielectric constant than silicon nitride films are used as etch-stop films or Cu-diffusion barrier films, and also the insulation films in the lower-layer part and upper-layer part of the multi-layer stacked structure are made different. Thus, the high-performance semiconductor device can be obtained which has made the whole device have high mechanical strength and has made the whole of interconnecting insulation layers have low dielectric constant.  
         [0154]     While we have shown and described several embodiments in accordance with our invention, it should be understood that disclosed embodiments are susceptible of changes and modifications without departing from the scope of the invention. Therefore, we do not intend to be bound by the details shown and described herein but intend to cover all such changes and modifications a fall within the ambit of the appended claims.