Abstract:
Field effect transistors include a stack of nanosheets of vertically arranged channel layers. A source and drain region is positioned at respective ends of the vertically arranged channel layers. A gate stack is formed over, around, and between the vertically arranged channel layers. The transistor includes a plurality of internal spacers, each formed between the gate stack and a respective source or drain region, with at least one pair of spacers being positioned above an uppermost channel layer.

Description:
BACKGROUND 
       [0001]    Technical Field 
         [0002]    The present invention relates to stacked-channel field effect transistors and, more particularly, to the use of a sacrificial layer to improve retention of top channel layers. 
         [0003]    Description of the Related Art 
         [0004]    Stacked nanowire and nanosheet devices are proposed for modern and next-generation semiconductor devices. The devices are formed around thin channel materials, configured as either wires or sheets of semiconductor material. Parasitic capacitance in nanosheet devices is a significant performance detractor, which can be mitigated through the formation of an inner spacer between a gate stack and the source and drain regions. 
         [0005]    However, the dummy gate processes used to form stacked nanowire and nanosheet devices can cause significant damage to the small-scale channel structures. In particular, etching processes used to remove dummy gate structures and form inner spacers are not perfectly selective and damages the top layer of a nanowire or nanosheet channel. In many cases, the top layer of a channel is destroyed entirely by the process. 
       SUMMARY 
       [0006]    A field effect transistor includes a stack of nanosheets of vertically arranged channel layers. A source and drain region is positioned at respective ends of the vertically arranged channel layers. A gate stack is formed over, around, and between the vertically arranged channel layers. The transistor includes a plurality of internal spacers, each formed between the gate stack and a respective source or drain region, with at least one pair of spacers being positioned above an uppermost channel layer. 
         [0007]    A field effect transistor includes a stack of nanosheets of vertically arranged channel layers. Merged source and drain regions are formed at respective ends of the vertically arranged channel layers. Each merged source and drain region contacts multiple channel layers. A gate stack is formed over, around, and between the vertically arranged channel layers. Crescent-shaped internal spacers are each formed between the gate stack and a respective source or drain region, with at least one pair of spacers being positioned above an uppermost channel layer. 
         [0008]    A field effect transistor includes a stack of nanosheets of vertically arranged channel layers. Merged source and drain regions are formed at respective ends of the vertically arranged channel layers that are epitaxially grown from and share a crystalline structure with respective ends of the channel layers. Each merged source and drain region contacts multiple channel layers. A gate stack is formed over, around, and between the vertically arranged channel layers. Crescent-shaped internal spacers are each formed between the gate stack and a respective source or drain region, with at least one pair of spacers being positioned above an uppermost channel layer. The source and drain regions have bulges complementary to recesses in the crescent-shaped internal spacers. The gate stack is recessed to accommodate a crescent shape of a topmost pair of inner spacers. 
         [0009]    These and other features and advantages will become apparent from the following detailed description of illustrative embodiments thereof, which is to be read in connection with the accompanying drawings. 
     
    
     
       BRIEF DESCRIPTION OF THE SEVERAL VIEWS OF THE DRAWINGS 
         [0010]    The disclosure will provide details in the following description of preferred embodiments with reference to the following figures wherein: 
           [0011]      FIG. 1  is a cross-sectional diagram of a step in forming a field effect transistor in accordance with the present principles; 
           [0012]      FIG. 2  is a cross-sectional diagram of a step in forming a field effect transistor in accordance with the present principles; 
           [0013]      FIG. 3  is a top-down diagram of a step in forming a field effect transistor in accordance with the present principles; 
           [0014]      FIG. 4  is a cross-sectional diagram of a step in forming a field effect transistor in accordance with the present principles; 
           [0015]      FIG. 5  is a cross-sectional diagram of a step in forming a field effect transistor in accordance with the present principles; 
           [0016]      FIG. 6  is a cross-sectional diagram of a step in forming a field effect transistor in accordance with the present principles; 
           [0017]      FIG. 7  is a cross-sectional diagram of a step in forming a field effect transistor in accordance with the present principles; 
           [0018]      FIG. 8  is a cross-sectional diagram of a step in forming a field effect transistor in accordance with the present principles; 
           [0019]      FIG. 9  is a cross-sectional diagram of a step in forming a field effect transistor in accordance with the present principles; 
           [0020]      FIG. 10  is a cross-sectional diagram of a step in forming a field effect transistor in accordance with the present principles; 
           [0021]      FIG. 11  is a cross-sectional diagram of a step in forming a field effect transistor in accordance with the present principles; 
           [0022]      FIG. 12  is a cross-sectional diagram of a step in forming a field effect transistor in accordance with the present principles; 
           [0023]      FIG. 13  is a cross-sectional diagram of a step in forming a field effect transistor in accordance with the present principles; 
           [0024]      FIG. 14  is a cross-sectional diagram of a step in forming a field effect transistor in accordance with the present principles; 
           [0025]      FIG. 15  is a cross-sectional diagram of a step in forming a field effect transistor in accordance with the present principles; 
           [0026]      FIG. 16  is a cross-sectional diagram of a step in forming a field effect transistor in accordance with the present principles; 
           [0027]      FIG. 17  is a cross-sectional diagram of a step in forming a field effect transistor in accordance with the present principles; and 
           [0028]      FIG. 18  is a block/flow diagram of a method of forming a field effect transistor in accordance with the present principles. 
       
    
    
     DETAILED DESCRIPTION 
       [0029]    Embodiments of the present invention employ a layer of epitaxially grown sacrificial material on a top layer of a nanosheet channel. This sacrificial layer protects the top layer from subsequent etches and prevents damage to the channel material. In addition, the presence of the sacrificial layer leads to the formation of an inner spacer above the uppermost channel layer. 
         [0030]    Referring now to the drawings in which like numerals represent the same or similar elements and initially to  FIG. 1 , a step in the formation of a field effect transistor (FET) is shown. In the present embodiments, a semiconductor-on-insulator (SOI) embodiment is shown. Specifically, the SOI structure includes a bottom semiconductor layer in the form of, e.g., a silicon substrate  100 . An insulating layer  102  lies over the substrate  100  and may be formed from, e.g., silicon dioxide. The semiconductor layer  100  may include any appropriate semiconductor material including, e.g., silicon, silicon germanium, silicon germanium carbide, silicon carbide, polysilicon, epitaxial silicon, amorphous silicon, and multilayers thereof. Although silicon is the predominantly used semiconductor material in wafer fabrication, alternative semiconductor materials can be employed, such as, but not limited to, germanium, gallium arsenide, gallium nitride, silicon germanium, cadmium telluride and zinc sellenide. The insulating layer may be a buried oxide region formed from, e.g., silicon dioxide, but it should be understood that any suitable dielectric material may be used. Exemplary alternative dielectric materials which may be used include, e.g., hafnium oxide, zirconium oxide, lanthanum oxide, aluminum oxide, titanium oxide, strontium titanium oxide, lanthanum aluminum oxide, yttrium oxide, hafnium oxynitride, zirconium oxynitride, lanthanum oxynitride, aluminum oxynitride, strontium titanium oxynitride, lanthanum aluminum oxynitride, yttrium oxynitride, silicates of the above, and alloys of the above. 
         [0031]    On top of the insulating layer  102  is a stack  108  of semiconductor materials. The stack includes alternating layers of sacrificial material  104  and channel material  106 . In one particular embodiment, it is specifically contemplated that the sacrificial material  104  may be formed from, e.g., silicon germanium, while the channel material  106  may be formed from, e.g., silicon. While it is specifically contemplated that the sacrificial material  104  may be silicon germanium, it should be understood that any material may be used that has etch selectivity with the channel material  106 , such that the sacrificial material  104  may be removed without harming structures made from the channel material  106 . 
         [0032]    Suitable materials for the channel material  106  include, for example, silicon, silicon germanium, silicon germanium carbide, silicon carbide, polysilicon, epitaxial silicon, amorphous silicon, multi-layers thereof, germanium, gallium arsenide, gallium nitride, silicon germanium, cadmium telluride, and zinc sellenide. III-V semiconductors may alternatively be used for the channel material  106 . The term “III-V compound semiconductor” denotes a semiconductor material that includes at least one element from Group III of the Periodic Table of Elements and at least one element from Group V of the Periodic Table of Elements. Typically, the III-V compound semiconductors are binary, ternary or quaternary alloys including III/V elements. Examples of III-V compound semiconductors that can be used in the present embodiments include, but are not limited to alloys of gallium arsenic, aluminum arsenic, indium gallium arsenic, indium aluminum arsenic, indium aluminum arsenic antimony, indium aluminum arsenic phosphorus, indium gallium arsenic phosphorus and combinations thereof. 
         [0033]    It is specifically contemplated that the stack  108  may be epitaxially grown. This refers to the growth of a semiconductor material on a deposition surface of a semiconductor material, in which the semiconductor material being grown has substantially the same crystalline characteristics as the semiconductor material of the deposition surface. The term “epitaxial material” denotes a material that is formed using epitaxial growth. In some embodiments, when the chemical reactants are controlled and the system parameters set correctly, the depositing atoms arrive at the deposition surface with sufficient energy to move on the surface and orient themselves to the crystal arrangement of the atoms of the deposition surface. Thus, in some examples, an epitaxial film deposited on a {100} crystal surface will take on a {100} orientation. 
         [0034]    In the case of a silicon channel material  106 , the silicon gas source for epitaxial deposition may be selected from the group consisting of, e.g., hexachlorodisilane, tetrachlorosilane, dichlorosilane, trichlorosilane, methylsilane, dimethylsilane, ethylsilane, methyldisilane, dimethyldisilane, hexamethyldisilane and combinations thereof. In the case of a silicon germanium sacrificial material, the silicon sources for epitaxial deposition may be selected from the group consisting of silane, disilane, trisilane, tetrasilane, hexachlorodisilane, tetrachlorosilane, dichlorosilane, trichlorosilane, methylsilane, dimethylsilane, ethylsilane, methyldisilane, dimethyldisilane, hexamethyldisilane and combinations thereof, and the germanium gas sources may be selected from the group consisting of germane, digermane, halogermane, dichlorogermane, trichlorogermane, tetrachlorogermane and combinations thereof. 
         [0035]    Referring now to  FIG. 2 , a step in the formation of a FET is shown. In this step, the stack  108  is etched to form fins  202  (having a length perpendicular to the cross-section shown. Any appropriate anisotropic etch may be used to form the fins  202 , with material being removed in the direction normal to the surface of the stack  108  at a rate that is greater than in the direction parallel to the surface. Although narrow fins  202  are shown, any width of fin may be used to create structures having any width from nanowires to nanosheets. It should be understood that a nanowire has a cross-sectional height that is on the same order of magnitude as its cross-sectional width (in one specific embodiment, a nanowire has a ratio of cross-sectional width to cross-sectional height of less than 2:1), whereas a nanosheet has a cross-sectional height that is significantly smaller than its cross-sectional width (in one specific embodiment, having a ratio of cross-sectional width to cross-sectional height of greater than 2:1). 
         [0036]    In one exemplary embodiment, a reactive ion etch (RIE) may be used to form the fins  202 . RIE is a form of plasma etching in which, during etching, the surface to be etched is placed on an RF powered electrode. During RIE, the surface to be etched takes on a potential that accelerates the etching species&#39; extracted from plasma toward the surface, with the chemical etching reaction taking place in the direction normal to the surface. Other examples of anisotropic etching that can be used include ion beam etching, plasma etching or laser ablation. Alternatively, the fin structure  202  can be formed by spacer imaging transfer. 
         [0037]    The etch is selective to the material of the insulator layer  102 . As used herein, the term “selective” in reference to a material removal process denotes that the rate of material removal for a first material is greater than the rate of removal for at least another material of the structure to which the material removal process is being applied. In this case, the etch is performed in a manner that is selective between the stack  108  of sacrificial material  104  and channel material  106 . 
         [0038]    Referring now to  FIG. 3 , a top-down view of the step of  FIG. 2  is shown. The fins  202  shown as being disposed on the insulator layer  102  at regular intervals, but it should be understood that any number of fins  202  may be used at any fixed or varying spacing. Also shown with dashed line A is a cross-section to be used for the following figures and discussion. 
         [0039]    Referring now to  FIG. 4 , a cross-sectional view of a step in the formation of a FET is shown along the cross-section A. A set of dummy gates is deposited, with two outside dummy gates  402  and a central dummy gate  404 . The dummy gates  402  and  404  may be formed from a semiconductor material including, e.g., polysilicon or amorphous silicon, that has etch selectivity with the sacrificial material  104 . The dummy gates  402  and  404  cover the ends of the fins  202  and the center of the fins  202 , while leaving the areas between exposed. The dummy gates  402 / 404  may be formed by depositing material over the fins  202  and subsequently patterning the into the dummy gate material using any appropriate lithography or etch process. 
         [0040]    Referring now to  FIG. 5 , a cross-sectional view of a step in the formation of a FET is shown along the cross-section A. Spacers  502  are deposited conformally along the sidewalls of the gates  402  and  404 . Spacer material  502  may be removed from the sidewalls of the fins  202  using an anisotropic etch such as RIE. Note that the present figures are not drawn exactly to scale—the removal of the spacer material  502  from the sidewalls of the fins  202  will result in an etch back along the sidewalls of the dummy gates  404  at least as deep as the height of the fins  202 . Deposition of the spacers  502  may include any appropriate deposition process including, e.g., chemical vapor deposition (CVD), physical vapor deposition, or atomic layer deposition. In one particular embodiment, the spacers  502  may be formed from a hardmask material such as, e.g., silicon nitride. Other hardmask compositions for the spacers  502  include silicon oxides, silicon oxynitrides, silicon carbides, silicon carbonitrides, etc. Spin-on dielectrics may also be utilized as a hardmask material including, but not limited to: silsequioxanes, siloxanes, and boron phosphate silicate glass. 
         [0041]    CVD is a deposition process in which a deposited species is formed as a result of chemical reaction between gaseous reactants at greater than room temperature (e.g., from about 25° C. to about 900° C.). The solid product of the reaction is deposited on the surface on which a film, coating, or layer of the solid product is to be formed. Variations of CVD processes include, but not limited to, Atmospheric Pressure CVD, Low Pressure CVD and Plasma Enhanced CVD, Metal-Organic CVD, and combinations thereof. PVD may include processes such as sputtering where, for example, DC diode systems, radio frequency sputtering, magnetron sputtering, and ionized metal plasma sputtering. 
         [0042]    Referring now to  FIG. 6 , a cross-sectional view of a step in the formation of a FET is shown along the cross-section A. Portions of the fins  202  are etched away, leaving a channel region  602  under the central dummy gate  404 , with remnants  604  embedded in the lateral dummy gates  402 . An anisotropic etch, such as RIE, is used to remove the material in the regions that will eventually become the source and drain of the device. 
         [0043]    Referring now to  FIG. 7 , a cross-sectional view of a step in the formation of a FET is shown along the cross-section A. A selective, timed, isotropic etch is used to remove some of the sacrificial material  104 , recessing the sacrificial material  104  with respect to the channel material  106 . This results in recessed sacrificial material  704  and protruding channel material  702 . The term “isotropic etch” denotes an etch process that is non-directional. By “non-directional” it is meant that the etch rate is not substantially greater in any one direction in comparison to all of the etch directions. The etch is timed, with a known etching rate being used to determine how long to allow the etch to continue to achieve a predetermined degree of recess in the recessed sacrificial material  704 . One notable feature of the recessed sacrificial material  704  is emphasized in the dashed box  706 , shown in greater detail in  FIG. 8  below. 
         [0044]    The isotropic etch may be a wet chemical etch or a dry etch. For example, the etchant may be a corrosive liquid or a chemically active ionized gas, such as a plasma. The precise composition of the etch will depend on the character of the sacrificial material  104  and the channel material  106 , with the etch selectively removing only the sacrificial material. For example, wet etches may include inorganic acids and oxidizing agents that do not attack the channel material  106  may be used. Examples of oxidizing agents may include peroxides, nitrates, nitrites, perchlorates, chlorates, chlorites, hypochlorites, dichromates, permanganates, persulfates or combinations thereof. The inorganic acids can include hydrochloric acid, hydrofluoric acid, sulfuric acid, phosphoric acid, or combinations thereof. 
         [0045]    Referring now to  FIG. 8 , an expanded view of box  706  is shown. In particular, detail on the recessed layers of sacrificial material  704  is shown. The etch that recessed the sacrificial material  704  is not perfectly isotropic, leaving a curved shape  802  to the outward facing surface of the recessed sacrificial material  704 . 
         [0046]    Referring now to  FIG. 9 , a cross-sectional view of a step in the formation of a FET is shown along the cross-section A. In this step, the spacers  502  are removed using an isotropic etch. As above, the isotropic etch may be a wet chemical etch or a dry etch. The removal of the spacers  502  exposes the sidewalls of the dummy gates  402  and  404 . 
         [0047]    Referring now to  FIG. 10 , a cross-sectional view of a step in the formation of a FET is shown along the cross-section A. A layer of spacer material is conformally deposited over the surfaces of the gates  402 / 404 , the recessed sacrificial material  704 , and the protruding channel material  702 . As above, deposition of the spacers  1004  may include any appropriate deposition process including, e.g., chemical vapor deposition (CVD), physical vapor deposition, or atomic layer deposition. In one particular embodiment, the spacers  704  may be formed from a hardmask material such as, e.g., silicon nitride. Other hardmask compositions for the spacers  704  include silicon oxides, silicon oxynitrides, silicon carbides, silicon carbonitrides, etc. Spin-on dielectrics may also be utilized as a hardmask material including, but not limited to: silsequioxanes, siloxanes, and boron phosphate silicate glass. 
         [0048]    An anisotropic etch, such as RIE, is used to remove spacer material from the facing surfaces of the protruding channel material  702 , exposing a face of the channel material. The resulting surface is emphasized in the dashed box  1002  and shown in greater detail below. 
         [0049]    Referring now to  FIG. 11 , an expanded view of box  1002  is shown. In particular, detail on the spacer  1004  is shown. In particular, after removal of the material on the facing surface of the protruding channel material  702 , spacer material  1102  remains in the recessed portions of the recessed sacrificial material  704 . In practice, these spacers  1102  form “crescent moon” shapes that remain as a structural component of the finished device. In contrast to conventional devices, the presence of a layer of sacrificial material  704  on top of the uppermost layer of protruding channel material  702  causes one such spacer  7702  to form above the uppermost layer of protruding channel material  702 . 
         [0050]    Referring now to  FIG. 12 , a cross-sectional view of a step in the formation of a FET is shown along the cross-section A. Source and drain regions are epitaxially grown from the exposed faces of the channel material  702 , with vertically adjacent channel layers merging to produce active source/drain regions  1202  and vestigial source/drain regions  1204 . In the case of a silicon channel material  702 , the silicon gas source for epitaxial deposition may be selected from the group consisting of, e.g., hexachlorodisilane, tetrachlorosilane, dichlorosilane, trichlorosilane, methylsilane, dimethylsilane, ethylsilane, methyldisilane, dimethyldisilane, hexamethyldisilane and combinations thereof. As shown, growth follows a crystalline growth pattern that follows the crystalline structure of the facing surface of the protruding channel material  702 . The vestigial merged source/drain regions  1204  are emphasized in dashed box  1206  and shown in  FIG. 13  below. 
         [0051]    The source/drain regions  1202 / 1204  may be doped with dopant atoms. The dopant atoms may be an n-type dopant (i.e., an element from Group IV or VI of the Periodic Table of Elements) or a p-type dopant (i.e., an element from Group II or VI of the Periodic Table of Elements). Exemplary n-type dopants for a group IV semiconductor include phosphorus, arsenic and antimony. Exemplary p-type dopants for a group IV semiconductor include boron, aluminum, and gallium. Exemplary n-type dopants for a III-V semiconductor include selenium, tellurium, silicon, and germanium. Exemplary p-type dopants for a III-V semiconductor include beryllium, zinc, cadmium, silicon, and germanium. The concentration of dopant within the doped region is typically from about 1011 to about 1015 atoms/cm2, with a concentration of dopant within the doped region from about 1011 to about 1013 atoms/cm2 being more typical. The source/drain regions  1202 / 1204  may be in situ doped as they are grown on the channel material  702  or, alternatively, may be doped through an implantation process. Notably, the channel material  702  that remains underneath the dummy gates  402 / 404  is not doped. 
         [0052]    Referring now to  FIG. 13 , an expanded view of box  1206  is shown. In particular, detail on the merged source/drain region  1204  is shown. It should be understood that the active source/drain regions  1202  and the vestigial source/drain regions  1204  are essentially similar in structure. The vertically adjacent channel layers merge and become a single crystalline structure, with the crescent moon spacers  1102  trapped within. 
         [0053]    Referring now to  FIG. 14 , a cross-sectional view of a step in the formation of a FET is shown along the cross-section A. Dielectric material  1402  is filled to or above the level of the top surface of the dummy gates  402 / 404 . It is specifically contemplated that the dielectric material  1402  may have the same composition as the insulator layer  102  or may, alternatively, be formed from any appropriate insulating material. If the dielectric material  1402  is filled to a level above the top surface of the dummy gates  402 / 404 , the material may then be polished down to the level of the dummy gates  402 / 404  using a chemical mechanical planarization that stops on the material of the dummy gates  402 / 404 . 
         [0054]    Referring now to  FIG. 15 , a cross-sectional view of a step in the formation of a FET is shown along the cross-section A. The dummy gates  402 / 404  have been removed, exposing the remaining sacrificial material  704 . An anisotropic etch is used to remove the dummy gate material, but it should be recognized that no anisotropic etch is perfectly selective. This etch will cause some damage to the top layer of the sacrificial material  704 —the presence of the sacrificial material  704  protects the underlying channel layers from damage. 
         [0055]    Referring now to  FIG. 16 , a cross-sectional view of a step in the formation of a FET is shown along the cross-section A. An isotropic etch is used to remove the remaining sacrificial material  704 , leaving channels  1602  exposed. The etch may be a wet etch or a dry etch. For example, wet etches may include inorganic acids and oxidizing agents that do not attack the channel material  106  may be used. Examples of oxidizing agents may include peroxides, nitrates, nitrites, perchlorates, chlorates, chlorites, hypochlorites, dichromates, permanganates, persulfates or combinations thereof. The inorganic acids can include hydrochloric acid, hydrofluoric acid, sulfuric acid, phosphoric acid, or combinations thereof. 
         [0056]    Referring now to  FIG. 16 , a cross-sectional view of a step in the formation of a FET is shown along the cross-section A. A gate stack  1702  is formed, including for example a gate dielectric layer, a work function metal, and a gate material that may be deposited and planarized according to any appropriate process. The device may be finished by forming electrical contacts to the active source/drain regions  1202  and the gate stack  1702 . 
         [0057]    It is to be understood that the present invention will be described in terms of a given illustrative architecture having a wafer; however, other architectures, structures, substrate materials and process features and steps may be varied within the scope of the present invention. 
         [0058]    It will also be understood that when an element such as a layer, region or substrate is referred to as being “on” or “over” another element, it can be directly on the other element or intervening elements may also be present. In contrast, when an element is referred to as being “directly on” or “directly over” another element, there are no intervening elements present. It will also be understood that when an element is referred to as being “connected” or “coupled” to another element, it can be directly connected or coupled to the other element or intervening elements may be present. In contrast, when an element is referred to as being “directly connected” or “directly coupled” to another element, there are no intervening elements present. 
         [0059]    A design for an integrated circuit chip may be created in a graphical computer programming language, and stored in a computer storage medium (such as a disk, tape, physical hard drive, or virtual hard drive such as in a storage access network). If the designer does not fabricate chips or the photolithographic masks used to fabricate chips, the designer may transmit the resulting design by physical means (e.g., by providing a copy of the storage medium storing the design) or electronically (e.g., through the Internet) to such entities, directly or indirectly. The stored design is then converted into the appropriate format (e.g., GDSII) for the fabrication of photolithographic masks, which typically include multiple copies of the chip design in question that are to be formed on a wafer. The photolithographic masks are utilized to define areas of the wafer (and/or the layers thereon) to be etched or otherwise processed. 
         [0060]    Methods as described herein may be used in the fabrication of integrated circuit chips. The resulting integrated circuit chips can be distributed by the fabricator in raw wafer form (that is, as a single wafer that has multiple unpackaged chips), as a bare die, or in a packaged form. In the latter case the chip is mounted in a single chip package (such as a plastic carrier, with leads that are affixed to a motherboard or other higher level carrier) or in a multichip package (such as a ceramic carrier that has either or both surface interconnections or buried interconnections). In any case the chip is then integrated with other chips, discrete circuit elements, and/or other signal processing devices as part of either (a) an intermediate product, such as a motherboard, or (b) an end product. The end product can be any product that includes integrated circuit chips, ranging from toys and other low-end applications to advanced computer products having a display, a keyboard or other input device, and a central processor. 
         [0061]    Reference in the specification to “one embodiment” or “an embodiment” of the present principles, as well as other variations thereof, means that a particular feature, structure, characteristic, and so forth described in connection with the embodiment is included in at least one embodiment of the present principles. Thus, the appearances of the phrase “in one embodiment” or “in an embodiment”, as well any other variations, appearing in various places throughout the specification are not necessarily all referring to the same embodiment. 
         [0062]    It is to be appreciated that the use of any of the following “/”, “and/or”, and “at least one of”, for example, in the cases of “A/B”, “A and/or B” and “at least one of A and B”, is intended to encompass the selection of the first listed option (A) only, or the selection of the second listed option (B) only, or the selection of both options (A and B). As a further example, in the cases of “A, B, and/or C” and “at least one of A, B, and C”, such phrasing is intended to encompass the selection of the first listed option (A) only, or the selection of the second listed option (B) only, or the selection of the third listed option (C) only, or the selection of the first and the second listed options (A and B) only, or the selection of the first and third listed options (A and C) only, or the selection of the second and third listed options (B and C) only, or the selection of all three options (A and B and C). This may be extended, as readily apparent by one of ordinary skill in this and related arts, for as many items listed. 
         [0063]    Referring now to  FIG. 18 , a block/flow diagram of a method of forming a FET is shown. Block  1802  forms the stack  108  of layers of sacrificial material  104  and layers of channel material  106 , with a layer of sacrificial material at the top of the stack  108 . Block  1802  etches fins  202  into the stack  108 , with each fin  202  providing the basis for a FET and being spaced apart in accordance with design needs and technology limits. 
         [0064]    Block  1806  forms dummy gates  402  and  404  over the spacers, depositing a layer of material and etching away any material that does not belong to the dummy gates  402 / 404  using, e.g., photolithography or an anisotropic etch. Block  1807  forms spacers  502  on the sidewalls of the dummy gates  402 / 404  by, e.g., conformally depositing a layer of spacer material and anisotropically etching them material from horizontal surfaces. Block  1808  then anisotropically etches the fins  202  from areas around the dummy gates  402 / 404 , leaving three fin regions remaining underneath the dummy gates  402 / 404 . 
         [0065]    Block  1810  uses an isotropic etch, for example a wet chemical etch, to selectively recess the sacrificial material and create recessed sacrificial layers  704  with recesses  802 . Block  1812  removes the remaining spacer material from the first spacers  502  and block  1814  forms a second layer of spacers material conformally over the recessed sacrificial layers  704 . Block  1816  anisotropically etches the second spacers  1004 , removing any spacer material on horizontal surfaces or which extends past the protruding channel layers  702  to form the inner spacers  1102 . 
         [0066]    Block  1818  epixtaxially grows source/drain regions  1202 / 1204  from the exposed faces of the protruding channel layers  704 . Block  1820  forms dielectric material  1402  around the dummy gates  402 / 404  to or above the level of the top surface of the dummy gates  402 / 404 . Block  1822  etches away the dummy gates with an anisotropic etch to expose the remaining sacrificial material  704 . The remaining sacrificial material  704  protects the underlying channel layers  1602  from the etch that removes the dummy gates  402 / 404 . Block  1824  removes the remaining sacrificial material  704  to expose the channel layers  1602 . Block  1826  then forms the gate stack  1702  over and around the channel layers  1602 . 
         [0067]    Having described preferred embodiments of a sacrificial layer for channel surface retention and inner spacer formation in stacked-channel FETs (which are intended to be illustrative and not limiting), it is noted that modifications and variations can be made by persons skilled in the art in light of the above teachings. It is therefore to be understood that changes may be made in the particular embodiments disclosed which are within the scope of the invention as outlined by the appended claims. Having thus described aspects of the invention, with the details and particularity required by the patent laws, what is claimed and desired protected by Letters Patent is set forth in the appended claims.