Abstract:
Copolymers of ethylene and alpha olefins that have been formed by a polymerization reaction in the presence of a single site catalyst, such as a metallocene, are used as a film or as a layer in multiple layer films, including molecularly oriented and irradiated heat shrinkable films. Novel blends of the copolymers with other polymeric materials are disclosed and used as a film or a layer in a film particularly in molecularly oriented and heat shrinkable films. Bags made from the multiple layer films are especially useful for shrink packaging primal cuts of meat. Processes for the formation of flexible films and packages made therefrom are also disclosed.

Description:
This application is a continuation of U.S. patent application Ser. No. 08/481,617, filed Jun. 7, 1995, now abandoned, which is a continuation of U.S. patent application Ser. No. 08/082,226, filed Jun. 24, 1993, now abandoned. 
    
    
     BACKGROUND OF THE INVENTION 
     Polymeric materials have many applications in packaging structures. They are used as films, sheets, lidstock, pouches, tubes and bags. These polymeric materials may be employed as a single layer or one or more layers in a structure. Unfortunately, there are countless polymeric materials available. Furthermore, resin suppliers frequently have a tendency to claim many more applications for a product than the product is actually suitable for. In addition, in view of the specialized applications and processing problems that are encountered despite the suppliers claims, one skilled in the art can not tell whether a particular resin will be suitable for an application unless tested. However, for various reasons there are frequently drawbacks to the use of many of these polymeric Materials. For example, ethylene vinyl alcohol is an excellent oxygen barrier material for use in packaging food products. However, this polymeric material can be affected by moisture that is present in the atmosphere or the packaged product. As a result, it is frequently found that some polymeric materials are better for certain applications than others. 
     One area where there is a need for suitable resins in film applications is in the area of heat shrinkable films. Heat shrinkable polymeric films are commonly used in packaging meats, particularly primal meat cuts and other large pieces of meat. While this description will detail the usage of films for packaging meat and meat by-products, it will be understood that these films are also suitable for packaging a myriad of other products, both including food products and non-food products. 
     Some of the films embodying the present invention are intended to be used by meat packers in the form of heat shrinkable bags with one opened end, which bags are closed and sealed after insertion of the meat. After the product is inserted, air is usually evacuated from the package and the open end of the bag is closed. Suitable methods of closing the bag include heat sealing, metal clips, adhesives etc. Heat is applied to the bag once sealing is completed to initiate shrinkage of the bag about the meat. 
     In subsequent processing of the meat, the bag may be opened and the meat removed for further cutting of the meat into user cuts, for example, for retail cuts or for institutional use. 
     Suitable shrink bags must satisfy a number of criteria. Many bag users seek a bag that is capable of surviving the physical process of filling, evacuating, sealing and heat shrinking. For example, during the shrinking process great stress can be placed on the film by the sharp edges of bone in the meat. The bag must also have sufficient strength to survive the material handling involved in moving the large cuts of meat, which may weigh a hundred pounds or more, along the distribution system. 
     Because many food products including meat deteriorate in the presence of oxygen and/or water, it is desirable that the bags have a barrier to prevent the infusion of deleterious gases and/or the loss or addition of moisture. 
     Conventional packaging for many products has frequently been made of multiple layer films having at least three layers. These multiple layer films are usually provided with at least one core layer of either an oxygen barrier material such as a vinylidene chloride copolymer, ethylene vinyl alcohol, a nylon or a metal foil preferably aluminum. Heat shrinkable meat bags, for example, have generally used vinylidene chloride copolymers. The copolymer of the vinylidene chloride may, for example, be a copolymer with vinyl chloride or methyl acrylate. Collapsible dispensing tubes have generally used one or more foil layers. The foil layers in addition to supplying an oxygen barrier also provide the dispensing tube with “deadfold”, i.e., the property of a collapsible dispensing tube when squeezed to remain in the squeezed position without bouncing back. 
     Outer layers of films used in packaging food products can be any suitable polymeric material such as linear low density polyethylene, low density polyethylene, ionomers including sodium and zinc ionomers such ionomers include Surlyn, ethylene vinyl acetate etc. In conventional shrink bags, the outer layers are generally linear low density polyethylene or blends thereof. Suitable outer layers for meat bags are taught by U.S. Pat. No. 4,457,960 to Newsome, the disclosures of which are incorporated herein by reference. 
     While conventional films have been suitable for many applications, it has been found that there is a need for films that are stronger and more easily processed than conventional films. In meat bags, there is a need for films and bags that have superior toughness and sealability and the ability to undergo cross-linking without undue deterioration. Thus, it is an object of the present invention to provide improved structures, including single and multi-layer films, sheets, lidstock pouches, tubes and bags. In particular, structures for use in shrink bags wherein the shrink bags are capable of withstanding production stresses and the shrink process. 
     SUMMARY OF THE INVENTION 
     The structures of the present invention may be single or multilayer films, sheets, lidstock, pouches, containers, tubes and bags where at least one layer contains a polymer usually a copolymer formed by a polymerization reaction in the presence of a single site catalyst such as a metallocene. Examples of such a polymer are ethylene and propylene polymers and copolymers thereof. One preferred copolymer is a copolymer of ethylene and an alpha olefin where such alpha olefin has a carbon chain length of from C 3 -C 20 . The structures of he present invention may also include blends of polymers and copolymers formed by a polymerization reaction with a single site catalyst or blends of a polymer and copolymer formed by a polymerization reaction with a single site catalyst and another polymeric material. Examples of suitable polymers for blending include: high and medium density polyethylene (HDPE, MDPE), linear low density polyethylene (LLDPE), low density polyethylene (LDPE) , ethylene vinyl acetate (EVA), ultra low density polyethylene (ULDPE or VLDPE), and ionomers such as Surlyn. 
     The present invention may also be a multilayer structure of at least three layers wherein the core layer is a barrier layer. In one embodiment of the present invention, there may be a first outer layer of an ethylene or propylene polymer or copolymer formed by a polymerization reaction in the presence of a single cell catalyst, a barrier layer and a second outer layer of a polymeric material. The second outer layer may be an ethylene or propylene polymer or copolymer formed by a polymerization reaction in the presence of a single site catalyst or a layer of another polymeric material such as high density polyethylene, medium density polyethylene, linear low density polyethylene, ultra low density polyethylene, low density polyethylene, ethylene vinyl acetate, an ionomer or blends thereof. The first outer layer Jay also be a blend of the ethylene copolymer with another suitable polymeric material such as described above. A preferred polymer formed by a single site catalyst is a copolymer of ethylene and an alpha olefin such as octene-1. Additional layers such as adhesive layers or other polymeric layers may be interposed in the structure between one or both of the outer layers or on top of one or both of the outer layers. The structure of the present invention may be rendered oriented either uniaxially or biaxially and cross-linked by any suitable means, such as for example irradiation or chemical cross-linking. 
    
    
     BRIEF DESCRIPTION OF THE DRAWINGS 
     FIG. 1 is a side view of a three layer structure of the present invention. 
     FIG. 2 is a side view of a five layer film of the present invention. 
     FIGS. 3-6 are examples of the structure of metallocene catalysts used in the polymerization of the polymer used in the structures of the present invention. 
    
    
     DETAILED DESCRIPTION OF THE INVENTION 
     The structures of the present invention include films, sheets, lidstock, pouches, containers, tubes and bags. These structures may be a single layer or multi-layer structure. The structures are comprised of polymers that have been polymerized in the presence of a single site catalyst, such as a metallocene. A metallocene is a complex organometallic molecule typically containing zirconium or titanium, with a pair of cyclic alkyl molecules. More specifically, metallocene catalysts are usually compounds with two cyclopentadiene rings fixed to the metal. These catalysts are frequently used with aluminoxanes as a co-catalyst or an activator, one suitable aluminozane is a methaliumoxane (MAO). Besides, titanium and zirconium, hafnium may also be used as the metal to which the cyclopentadiene is bonded. Alternative metallocenes may include Group IVA, VA and VIA transition metals with two cyclopentadiene rings. Also mono-cyclopentadiene rings or sibyl amides may alternatively be in the metallocene instead of two cyclopentadienes. Other metals to which the cyclopentadine may be attached may include the metals in the lanthanide series. FIGS. 3,  4 ,  5  and  6  show representative metallocenes that are suitable single site catalysts. 
     While the reaction mechanism is not completely understood, it is believed that the metallocene, single site catalyst confines the copolymerization reaction to a single site over the polymer thus controlling comonomer placement and side chain length and branching. The copolymers formed from metallocene single site catalysts are highly stereo regular products with narrow molecular weight distribution. The metallocenes can be used to polymerize ethylene, propylene, ethylenic and acetylenic monomers, dienes and carbon monoxide. Comonomers with ethylene and propylene include styrene, substituted styrene, vinyl, acrylonitrile, methyl acrylate, ethyl methacrylate and 1.4-hexadiene. The metallocene single site catalysts are capable of producing isotactic polymers and syndiotactic polymers, i.e., polymers in which the crystalline branches alternate regularly on both sides of the back bone of the polymer. There are two general types of single site catalyst reactions. The first are nonstereoselective catalysts reactions which have been developed by Exxon and Dow and which are used to make Exxon&#39;s Exact resins and Dow&#39;s CGCT resins. See FIGS. 3 and 4. The second type of reactions are stereoselective catalysts developed by Hoechst and Fina for stereo specific polymerization particularly of polypropylene and other olefins such as butene-1, and 4 methylpentene-1. See, e.g., FIGS. 5 and 6. 
     The ethylene alpha olefins polymerized by a single site catalyst have low crystallinity and a density that ranges from 0.854 to 0.97 gm/cc. Although this density range is similar to conventional ethylene polymers, i.e., LDPE, LLDPE and ULDPE, the polymers in the structures of the present invention have a narrow molecular weight distribution and homogeneous branching. The molecular weight distribution of the preferred polymers may be represented by the formula 
     
       
           MWD=M   w   /M   n =&lt;2.5 
       
     
     In addition, the melt processability of these polymers (I 10 /I 2 ) has a range of about 5.5 to about 12 while conventional homogenous polymers are generally less than 6.5 at an MWD of 2. The melt tension of these polymers is in the range of about 1.5 to 3.5 grams. 
     The MWD of these polymers may be determined using a Water&#39;s 150 GPC at 140° C. with linear columns (103 6  A-10 6  A 0 ) from Polymer Labs and a differential refractometer detector. Comparison of the MWD of a 1 MI, 0.920 density CGCT polymer with that of 1 MI, 0.920 density conventional LLDPE illustrates the very narrow MWD of the CGCT polymers which usually have a M W /M N  of approximately 2 compared to 3 or greater for LLDPE. 
     A preferred ethylene copolymer is a copolymer of ethylene and a C 3  to C 20  alpha olefin. A preferred copolymer is a low modulus ethylene octene copolymer sold by Dow. This copolymer is formed by Dow&#39;s constrained-geometry catalyst Technology which uses a single site catalyst such as cyclo-pentadienyl titanium complexes. As best understood, Dow&#39;s constrained geometry catalysts are based on group IV transition metals that are covalently bonded to a monocyclopentadienyl group bridged with a heteroatom. The bond angle between the monocyclopentadienyl group, the titanium center and the heteroatom is less than 115°. When the alpha olefin is present in the copolymer in the range of about 10 to 20% by weight these copolymers are referred to as plastomers. When the percent alpha olefin is greater than 20% these copolymers are called elastomers. The preferred ethylene octene copolymer has the octene comonomer present in an amount less than 25%. Examples of the Dow ethylene octene copolymer have the following physical properties. 
     
       
         
               
               
               
               
               
             
           
               
                   
               
               
                   
                 MOLECULAR 
                   
                   
                   
               
               
                 DENSITY 
                 WEIGHT 
                 MELT 
                 MELT 
                 MELT 
               
               
                 g/cc 
                 DISTRIBUTION 
                 INDEX 
                 FLOW RATIO 
                 STRENGTH 
               
               
                   
               
             
             
               
                 Polymer 1. 
                   
                   
                   
                   
               
               
                 0.920 
                 1.97 
                 1.0 
                 9.5 
                 1.89 
               
               
                 0.910 
                 1.90 
                 1.0 
                 7.9 
                 1.69 
               
               
                 0.902 
                 2.10 
                 1.0 
                 7.6 
                 1.68 
               
               
                   
               
             
          
         
       
     
     Molecular weight distribution is defined as the ratio of weight average molecular weight to number average molecular weight. The lower the figure, the narrower the molecular weight distribution. Melt flow ratio is defined as the ratio of melt index, as tested with a 10-kg load to the melt index with a 2-kg load. The higher the ratio, the more processable the material. Melt flow ratio is defined as melt tension measured in grams. The higher the number the greater the melt strength. Other suitable resins are the Exact resins sold by Exxon, these resins have the following characteristics: 
     
       
         
               
             
               
               
             
               
               
               
               
               
               
               
             
               
               
               
               
               
               
               
             
           
               
                   
               
               
                 Typical properties of Exact 
               
               
                 medical grade polyethylenes 
               
             
          
           
               
                   
                 Value by grade 
               
             
          
           
               
                 Property 
                 4028 
                 4022 
                 4021 
                 4023 
                 4024 
                 4027 
               
               
                   
               
             
          
           
               
                 Melt index (D1238) a   
                 10 
                 6 
                 22 
                 35 
                 3.8 
                 4 
               
               
                 Density, g./cc. 
                 0.880 
                 0.890 
                 0.885 
                 0.882 
                 0.885 
                 0.895 
               
               
                 (D-1505) 
               
               
                 Hardness (D-2240) 
               
               
                 Shore A 
                 78 
                 84 
                 84 
                 80 
                 83 
                 89 
               
               
                 Shore D 
                 29 
                 35 
                 36 
                 27 
                 35 
                 39 
               
               
                 Tensile strength 
                 2220 
                 1700 
                 3260 
                 620 
                 2840 
                 2200 
               
               
                 at break, p.s.i. 
               
               
                 (D-638) 
               
               
                 Tensile elongation 
                 &gt;800 
                 &gt;800 
                 &gt;800 
                 &gt;800 
                 &gt;800 
                 &gt;800 
               
               
                 at break, % (D-638) 
               
               
                 Tensile impact, 
                 145 
                 130 
                 350 
                 280 
                 300 
                 340 
               
               
                 ft.-lb./sq. in. 
               
               
                 (D-1822) 
               
               
                 Flexural modulus, 
                 5040 
                 4930 
                 3980 
                 3100 
                 4180 
                 7230 
               
               
                 p.s.i. (D-790) 
               
               
                 Vicat softening 
                 138 
                 168 
                 158 
                 138 
                 158 
                 181 
               
               
                 point ° F. (D-1525) 
               
               
                   
               
               
                   a : ASTM test method  
               
             
          
         
       
     
     The structure of the present invention is comprised of an ethylene, propylene, or styrene polymer or copolymer formed by a polymerization reaction in the presence of a single site catalyst preferably a metallocene. Ethylene may be copolymerized with any suitable monomer such as C 3 -C 20  alpha olefin including propylene butene-1, 4-methyl pentene-1, haxene-1 and octene-1. A preferred coinonomer is octene-1. The preferred ethylene alpha olefin copolymer of the present invention has a density in the range of 0.380 gm/cc to about 0.920 gm/cc, a more preferred range of 0.390 gm/cc to about 0.915 gm/cc and a most preferred range of about 0.900 gm/cc to about 0.912 gm/cc. 
     FIG. 1 shows a cross section of a three layer coextruded structure. Layer  14  is the core layer which may be a barrier layer that minimizes the transmission of oxygen through the structure. Preferred barrier materials are polyvinylidene chloride copolymers such as copolymers of vinylidene chloride and vinyl chloride or an alkyl acrylate such as methyl acrylate. Other preferred barrier material includes, ethylene vinyl alcohol, nylon or a metal foil such as aluminum. Layer  14  may also be a copolymer of ethylene and styrene formed using a single site catalyst in the polymerization reaction. The copolymer of vinylidene chloride may also be polymerized by the polymerization reaction in the presence of a single site catalyst. In addition, layer  14  may also be a polystyrene formed by a polymerization reaction in the presence of a single site catalyst. One such polystyrene is the crystalline syndiotactic polystyrene sold by Idemitsu Petro-Chemical Co., Tokyo, Japan. 
     On opposite sides of the core layer  14  of FIG. 1 are layers  12  and  16 . At least one of these layers  12  is a polymer formed by a polymerization reaction in the presence of a single site catalyst. The remaining layer  16  may be any suitable polymeric material such as a polyester, co-polyester, polyamide, polycarbonate, polypropylene, propylene-ethylene copolymer, ethylene-propyiene copolymer, combinations of polypropylene and ethylene vinyl acetate copolymer, ultra low density polyethylene, low density polyethylene, medium density polyethylene, high density polyethylene, linear low density polyethylene copolymers, linear medium density polyethylene copolymer, linear high density polyethylene copolymer, ionomer, ethylene acrylic acid copolymer, ethylene ethyl acrylate copolymer, ethylene methyl acrylate copolymer, or ethylene methacrylic acid copolymer. 
     In an alternate embodiment, the layer  12  may be a blend of a polymer formed by a polymerization reaction in the presence of a single site catalyst and a suitable polymeric material such as is identified in connection with the description of layer  16  above. 
     As seen in FIG. 2, the structure may also include embodiments which have a fourth layer  28  over the first layer  22  and a fifth polymeric layer  30  over the third layer  26 . The composition of the fourth layer  28  may be selected from the same grouo of materials from which the composition of the first layer  12  or third layer  16  is selected, and the fifth layer  20  may also be the same composition as the first layer  22  or the third layer  26 . 
     In an alternate embodiment of FIG. 2, the five layer structure may have a first layer  28  similar in composition to layer  12  of FIG. 1, i.e., the film may have a first layer of a polymer formed by the polymerization reaction with a single site catalyst or blends thereof with another suitable polymeric material one or both of the second  22  and fourth  26  layers may be an adhesive layer. 
     The composition of adhesive layers  22  and  26  is selected for its capability to bond the core or barrier layer  24  to the surface layers  28  and  30 . A variety of the well known extrudable adhesive polymers adhere well to the core or barrier layer  24 . Thus, if for example Layer  20  is a polypropylene, an adhesive polymer based on polypropylene is desirably selected for layer  26 . Examples of such adhesives are the extrudable polymers available under the trade designations Admer QF-500, QF550, of (F-551 from Mitsui Petrocnemical Company, or Exxon 5610A2. 
     If the composition of layer  28  or  30  is an ethylene based polymer or copolymer, an adhesive polymer based on ethylene is preferably selected for layer  22 , including ethylene homopolymer and copolymers. Such a preferred adhesive composition is an ethylene vinyl acetate copolymer containing 25% to 30% by weight vinyl acetate. Other ethylene based homopolymer and copolymers, modified to enhance adhesion properties are well known under the trade names of, for example, Bynel and Plexar. Typical base polymers for these extrudable adhesives are the polyethylene and the ethylene vinyl acetate copolymers. Such adhesive polymers, including the polypropylene-based polymers, are typically modified with carboxyl groups such as anhydride. Also acceptable as adhesives are ethylene methyl acrylate copolymers (EMA). 
     Additional layers may also be present in the structures of the present invention. For example, the present invention contemplates  4 ,  6 ,  7 ,  8 , and higher numbers of layers in the film of the present invention and different combinations of layer structures may also be present. For example, there may be more than one barrier layer, i.e., two layers of polyvinylidene chloride copolymers, two layers of foil or two layers of EVOH or nylon. Alternatively, this may be a layer of EVOH and a layer of a polyvinylidene chloride copolymer or a polyamide or a polystyrene and other combinations of the core materials. The additional layers of the present invention also encompass ore than one Polymer formed by the polymerization reaction in the presence of a single site catalyst. The polymers may be in a layer alone or in the form of a blend. Suitable polymers for blending with an ethylene polymer formed in a polymerization reaction with a single site catalyst include other ethylene polymers formed in a polymerization reaction with a single site catalyst, LDPE, LLDPE, ULDPE, EVA, ionomers, ethylene copolymers, ethylene methyl acrylate (EMA), ethylene acrylic acid (EAA), ethyl methyl acrylic acid (EMAA), polypropylene (PP), ethylene normal butyl acrylate (ENBA), ethylene propylene copolymers (PPE). Suitable polymers for blending with a propylene polymers formed in a polymerization reaction with a single site catalyst include ethylene propylene copolymers. 
     Preferred blends using EVA&#39;s are those having lower VA content as they tend to yield EVA layers having better hot strength. EVA&#39;s having higher VA content tend to yield EVA layers having increased adhesion to for example, the vinylidene chloride copolymer layer. EVA&#39;s having virtually any amount of VA will have better adhesion to the vinylidene chloride copolymer layer than an ethylene homopolymer. However, good interlayer adhesion is considered desirable in the invention, and thus, steps are usually taken to enhance adhesion where no unacceptable negative effect is encountered. Thus, higher VA contents, in the range of 6% to 12% vinyl acetate are preferred, a melt index of less than 1 is also preferred. While blend amounts are shown herein in weight percent, VA contents are role percent. Especially preferred EVA&#39;s have VA content of 7% to 9% and melt index of 0.2 to 0.8. Blends of EVA&#39;s to make up the EVA component of layers  16  and  18  are acceptable. 
     The structure of the present invention may be formed by any conventional process. Such processes include extrusion, coextrusion, extrusion coating, extrusion lamination, adhesive lamination and the like, and combinations of processes. The specific process or processes for making a given film which is neither oriented nor cross-linked can be selected with average skill, once the desired structure and compositions have been determined. 
     When the structure of the present invention is a film, the film may also be oriented either uniaxially or biaxially. Orientation can also be done by any conventional process for forming multiple layer films. A preferred process includes the steps of coextrusion of the layers to be oriented, followed by orientation in one of the conventional processes such as blown tubular orientation or stretch orientation in the form of a continuous sheet; both being molecular orientation processes. The double bubble technique disclosure in Pahlke, U.S. Pat. No. 3,456,044 is suitable for use in producing the film of this invention. The films may also be formed by a tubular water quench process. In this process the film may be extruded downwardly as a tube formed by an annular die, and carried into a water quench tank, generally with a cascade of water on the outside surface providing initial cooling. The flattened tape is withdrawn from the quench bath, is reheated (normally in a second water bath) to its orientation temperature, is stretched in the machine direction between two sets of rolls that are so rotated as to establish a linear rate differential therebetween, and is simultaneously oriented in the transverse, or cross-machine, direction as an inflated bubble trapped between the nips of the rolls. In accordance with conventional practice, the film will usually be cooled by air in the orientation zone. 
     The film of the present invention may also be oriented and/or cross-linked. The first step is the formation of a multiple layer film. The formation of the multiple layer film, is usually most easily accomplished by coextrusion of the desired layers. Other formation processes are acceptable so long as the resulting oriented film at the conclusion of fabrication processing is a unitary structure. 
     The second step is orienting the multiple layer film. One method for accomplishing orientation is by heating the film to a temperature appropriate to molecular orientation and molecularly orienting it. The film may then be optionally heat set by holding it at an elevated temperature while its dimensions are maintained. The orientation step is preferentially carried out in line with the first step, which is the film formation step of the process. 
     The third step is subjecting the formed and oriented multiple layer film, to electron beam irradiation. 
     The amount of electron beam irradiation is adjusted, depending on the make-up of the specific film to be treated and the end use requirement. While virtually any amount of irradiation will induce some cross-linking, a minimum level of at least 1.0 megarads is usually preferred in order to achieve desired levels of enhancement of the hot strength of the film and to expand the range of temperature at which satisfactory heat seals may be formed. While treatment up to about 50 megarads can be tolerated, there is usually no need to use more than 10 megarads, so this s a preferred upper level of treatment the most preferred dosage being 2 to 5 megarads. 
     The third step of subjecting the film to electron beam irradiation is performed only after the multiple layer film has been formed, and after molecular orientation, in those embodiments where the film is molecularly oriented. It should be noted that, in the irradiation step, all of the layers in the film are exposed simultaneously to the irradiation sources, such that irradiation of all the layers of the film takes place simultaneously. 
     In one embodiment of the process, the second step of orientation may be omitted and the unoriented multiple layer film may be cross-linked by irradiation treatment to produce a cross-linked, unoriented, multiple layer film. 
     EXAMPLES 
     Multilayer films may be prepared according to the present invention. Biaxially stretched three layer films may be prepared by a “double bubble” process similar to that disclosed in U.S. Pat. No. 3,456,044 by coextruding the following compositions through a multilayer die, biaxially stretching the coextruded primary tube. The films may also be irradiated if desired. 
     Example 1 
     Layer 1—Copolymer of ethylene and an alpha olefin such as Hexene-1 or Octene-1 formed by the polymerization reaction in the presence of a single site catalyst or metallocene (hereinafter CEO) 
     Layer 2—Vinylidene chloride—methyl acrylate (VDC-MA) copolymer 
     Layer 3—Polyolefin. This film may be biaxally stretched and if necessary irradiated. 
     
       
         
               
               
               
               
             
               
               
               
               
             
               
               
               
             
               
               
               
               
             
               
               
               
               
             
               
               
               
             
           
               
                   
               
             
             
               
                   
                 EXAMPLE 2 
                 EXAMPLE 3 
                 EXAMPLE 4 
               
               
                   
               
               
                 Layer 1 
                 CEO 
                 CEO 
                 CEO-EVA blend 
               
               
                 Layer 2 
                 VDC-MA 
                 VDC-MA 
                 VDC-MA 
               
               
                 Layer 3 
                 ULDPE-EVA blend 
                 CEO 
                 CEO-EVA blend 
               
               
                   
               
             
          
           
               
                   
                 EXAMPLE 5 
                 EXAMPLE 6 
                 EXAMPLE 7 
               
               
                   
               
               
                 LAYER 1 
                 CEO 
                 CEO 
                 CEO-EVA blend 
               
               
                 LAYER 2 
                 Nylon 
                 Nylon 
                 Nylon 
               
               
                 LAYER 3 
                 CEO 
                 ULDPE-EVA 
                 CEO-EVA blend 
               
               
                   
               
             
          
           
               
                   
                 EXAMPLE 8 
                 EXAMPLE 9 
               
               
                   
               
               
                 LAYER 1 
                 Polyolefin 
                 Polyolefin 
               
               
                 LAYER 2 
                 Styrene copolymer formed 
                 Propylene copolymer 
               
               
                   
                 by the polymerization reaction 
                 formed by the 
               
               
                   
                 with a single site catalyst 
                 Polymerization 
               
               
                   
                   
                 reaction with a single 
               
               
                   
                   
                 site catalyst 
               
               
                 LAYER 3 
                 Polyolefin 
                 Polyolefin 
               
               
                   
               
             
          
           
               
                   
                 EXAMPLE 10 
                 EXAMPLE 11 
                 EXAMPLE 12 
               
               
                   
               
               
                 LAYER 1 
                 CEO 
                 CEO 
                 CEO-EVA Blend 
               
               
                 LAYER 2 
                 CEO 
                 EVOH 
                 EVOH 
               
               
                 LAYER 3 
                 CEO 
                 ULDPE-EVA Blend 
                 CEO-EVA Blend 
               
               
                   
               
             
          
           
               
                   
                 EXAMPLE 13 
                 EXAMPLE 14 
                 EXAMPLE 15 
               
               
                   
               
               
                 LAYER 1 
                 CEO 
                 CEO 
                 CEO-EVA Blend 
               
               
                 LAYER 2 
                 Tie 
                 Tie 
                 Tie 
               
               
                 LAYER 3 
                 PVDC Copolymer 
                 PVDC Copolymer 
                 PVDC 
               
               
                   
                 or EVOH 
                 or EVOH 
                 Copolymer 
               
               
                   
                   
                   
                 or EVOH 
               
               
                 LAYER 4 
                 Tie 
                 Tie 
                 Tie 
               
               
                 LAYER 5 
                 ULDPE-EVA Blend 
                 CEO 
                 CEO-EVA Blend 
               
               
                   
               
             
          
           
               
                   
                   
                 EXAMPLE 16 
               
               
                   
                   
               
               
                   
                 LAYER 1 
                 EVA-ULDPE 
               
               
                   
                 LAYER 2 
                 ULDPE or CEO 
               
               
                   
                 LAYER 3 
                 PVDC Copolymer or EVOH 
               
               
                   
                 LAYER 4 
                 EVA 
               
               
                   
                 LAYER 5 
                 CEO or blend of CEO and EVA 
               
               
                   
                   
               
             
          
         
       
     
     The following examples may also be prepared in accordance with the present invention: 
     Example 17 
     Meat Film—Forming Web Formed by TWQ Process (Tubular Water Quench Process) 
     LAYER 1 Nylon 
     LAYER 2 Tie 
     LAYER 3 EVOH 
     LAYER 4 Tie 
     LAYER 5 CEH or CEO 
     CEH is a copolymer of ethylene and Hexene-1 formed by the polymerization reaction in the presence of a single site catalyst or a metallocene. Other alpha olefins can be polymerized with the ethylene also. 
     Example 18-20 
     Innerliner Films—These films can be formed either on a blown film line or by using a tubular water quench. 
     LAYER 1 HDPE 
     LAYER 2 Blend of CEH or CEO and EVA and polybutylene 
     LAYER 1 HDPE 
     LAYER 2 CEH or CEO and polybutylene 
     LAYER 1 HDPE 
     LAYER 2 CEH or CEO 
     Example 21 and 22 
     Meat—Non Forming Top Web Film 
     LAYER 1 PVDC coated PET 
     LAYER 2 Adhesive (lamination) 
     LAYER 3 CEO or CEH 
     This film nay be formed by adhesive laminating a film formed of a copolymer of ethylene and an alpha olefin with the PVDC coated PET film. 
     LAYER 1 PVDC coated PET 
     LAYER 2 LDPE—extrusion laminated 
     LAYER 3 LDPE/CEH or CEO coextrusion 
     This film can be formed by extrusion laminating a film of PVDC coated PET or LDPE. 
     Example 23 
     Layer 1—Blend of two or more copolymers of ethylene and an alpha olefin polymerized in the presence of a single site catalyst or metallocene such as CEO with either CEH or CEB. CEB is a copolymer of ethylene and butene-1 formed by a polymerization reaction in the presence of a single site catalyst or a metallocene. 
     Example 24 
     Layer 1—Blend of a copolymer of ethylene and an alpha olefin formed by a polymerization reaction in the presence of a single site catalyst or a metallocene with Polyethylene or other polyolefin such as EVA, EMA, EAA, EMAA, ionomers, ENBA, PP or PPE. 
     The films of example 23 and 24 can either be single layer films or multi layer films where additional layers are present on layer 1.