Abstract:
The present invention mechanically protects a surface of a miniaturized liquid crystal display device for mobile phone or the like without deteriorating image quality and without increasing a thickness of a whole display device. To achieve such an object, in the present invention, a liquid crystal display panel is constituted of a TFT substrate and a color filter substrate, a lower polarizer is adhered to a lower surface of the TFT substrate, and an upper polarizer is adhered to an upper surface of the color filter substrate. A face plate is adhered to the upper polarizer using an acrylic adhesive material which is cured by ultraviolet rays. For enhancing strength and adhesion property of the face plate, corners and side portions of the face plate are chamfered. By making a profile of the face plate smaller than a profile of the upper polarizer, the adhesion property of the face plate is enhanced. The present invention can protect the surface of the liquid crystal display panel without deteriorating image quality and without largely increasing a thickness of the display device.

Description:
CROSS-REFERENCE TO RELATED APPLICATIONS 
     The disclosure of Japanese Patent Application No. 2007-171665 filed on Jun. 29, 2007 including the specification, drawings and abstract is incorporated herein by reference in its entirety. 
     BACKGROUND OF THE INVENTION 
     1. Field of the Invention 
     The present invention relates to a liquid crystal display device, and more particularly to a technique which enhances strength and visibility of a miniaturized display device used in a mobile phone or the like. 
     2. Description of the Related Art 
     With respect to a liquid crystal display device, there has been a strong demand for the reduction of a thickness of a liquid crystal display panel along with a demand for the reduction of a profile size of a set while maintaining a screen at a fixed size. To decrease the thickness of the liquid crystal display panel, after manufacturing the liquid crystal display panel, an outer side of the liquid crystal display panel is polished to decrease the thickness of the liquid crystal display panel. 
     The liquid crystal display device is constituted of a TFT substrate which forms pixel electrodes, TFTs and the like thereon or a color filter substrate which forms color filters thereon. A glass substrate which is served for forming the TFT substrate and the color filter substrate has a thickness thereof standardized to 0.5 mm or to 0.7 mm. It is difficult to acquire such standardized glass substrate from a market. Further, an extremely thin glass substrate gives rise to drawbacks on mechanical strength, deflection or the like in manufacturing steps thereof thus lowering a manufacturing yield rate. As a result, after forming the liquid crystal display panel using the standardized glass substrate, an outer surface of the liquid crystal display panel is polished to decrease the thickness of the liquid crystal display panel. 
     The reduction of the thickness of the liquid crystal display panel gives rise to a drawback on mechanical strength. That is, there exists a possibility that the liquid crystal display panel is broken when mechanical pressure is applied to a display screen of the liquid crystal display panel. To prevent such breaking of the liquid crystal display panel, as shown in  FIG. 10 , in assembling the liquid crystal display panel in a set such as a mobile phone, a front window (hereinafter referred to as face plate) is mounted on a screen side of the liquid crystal display panel. The face plate is usually formed larger than the color filter substrate. 
     To prevent the application of a force to the liquid crystal display panel when an external force is applied to the face plate, the face plate is arranged in a spaced-apart manner from the liquid crystal display panel. However, the constitution shown in  FIG. 10  gives rise to a drawback that display quality is deteriorated as described later. Japanese Patent Laid-Open Hei11-174417 (patent document 1) discloses a technique which copes with the drawback attributed to the structure shown in  FIG. 10 , for example. 
     SUMMARY OF THE INVENTION 
     The related art shown in  FIG. 10  gives rise to a drawback that an image appears as a duplicate image.  FIG. 10  is a view explaining the drawback by taking a reflective liquid crystal display panel as an example. In  FIG. 10 , an incident external light L passes a face plate, is reflected on the liquid crystal display panel, passes the face plate again, and enters human eyes. Here, although the external light L is refracted on the face plate, the refraction is ignored in  FIG. 10 . 
     A portion of light reflected on a screen P 1  of the liquid crystal display panel is reflected on a lower surface Q 1  of the face plate, is incident on a screen P 2  of the liquid crystal display panel, and is reflected on the screen P 2  of the liquid crystal display panel. When a viewer recognizes light reflected on the screen P 2  with his/her eyes, a phenomenon that an image appears as a duplicate image occurs. Although the explanation has been made by taking the reflective liquid crystal display panel as an example in  FIG. 10 , the same goes for a transmissive liquid crystal display panel. That is, in the transmissive liquid crystal display panel, when light passes the liquid crystal display panel at an angle equal to an angle of reflection light on a screen P 1  each of the liquid crystal display panel, light is reflected on a lower surface Q 1  of a face plate, and traces a path in the same manner as a path of the reflective liquid crystal display panel. The phenomenon which makes the image appear as a duplicate image deteriorates image quality. 
     In the technique described in patent document 1, for example, which copes with such a drawback, an adhesive resilient body is arranged between the face plate and the liquid crystal display panel. The adhesive resilient body protects the liquid crystal display panel from an external force. Further, by setting reflectance of the adhesive resilient body to a value close to reflectance of the face plate, the reflection on an interface with the face plate can be suppressed. However, the technique disclosed in patent document 1 requires the uniform adhesion of the face plate eliminating the presence of bubbles or the like between the face plate and the adhesive resilient body and hence, it is extremely difficult to apply the technique to the mass production of the liquid crystal display panels. Further, there arises a drawback in selecting a material which can approximate the reflectance of the adhesive resilient body to the reflectance of the face plate. In addition to these drawbacks, since the adhesive resilient body requires considerable thickness, the technique disclosed in patent document 1 cannot completely overcome the drawback that the image appears as the duplicate image. 
     The present invention has been made to overcome the above-mentioned drawbacks of the related art, and the specific constitutions of the present invention are as follows. 
     (1) The present invention is directed to a liquid crystal display device including a liquid crystal display panel which has a TFT substrate on which pixel electrodes and TFTs for controlling signals to the pixel electrodes are arranged in a matrix array and a color filter substrate on which color filters corresponding to the pixel electrodes are formed, wherein an upper polarizer is adhered to the color filter substrate, a face plate made of glass is adhered to the upper polarizer, and the upper polarizer and the face plate are adhered to each other using a ultraviolet curing resin. 
     (2) The liquid crystal display device described in the constitution (1) is characterized in that the ultraviolet curing resin is a liquid containing an acrylic resin at the time of initially adhering the face plate and the upper polarizer adhered to the liquid crystal display panel. 
     (3) The liquid crystal display device described in the constitution (1) is characterized in that the ultraviolet curing resin is a liquid containing an acrylic oligomer at the time of initially adhering the face plate and the upper polarizer adhered to the liquid crystal display panel. 
     (4) The present invention is also directed to a liquid crystal display device including a liquid crystal display panel which has a TFT substrate on which pixel electrodes and TFTs for controlling signals to the pixel electrodes are arranged in a matrix array and a color filter substrate on which color filters corresponding to the pixel electrodes are formed, wherein an upper polarizer is adhered to the color filter substrate, a face plate made of glass is adhered to the upper polarizer, and a corner portion of the face plate is chamfered with a cutting size of 0.3 mm or more. 
     (5) The liquid crystal display device described in the constitution (4) is characterized in that the corner portion of the face plate is chamfered with a cutting size of 0.5 mm or more. 
     (6) The liquid crystal display device described in the constitution (4) is characterized in that a side portion of the face plate is chamfered with a cutting size of 0.05 mm or more. 
     (7) The liquid crystal display device described in the constitution (4) is characterized in that the side portion of the face plate is chamfered with a cutting size of 0.15 mm or more. 
     (8) The present invention is also directed to a liquid crystal display device including a liquid crystal display panel which has a TFT substrate on which pixel electrodes and TFTs for controlling signals to the pixel electrodes are arranged in a matrix array and a color filter substrate on which color filters corresponding to the pixel electrodes are formed, wherein an upper polarizer is adhered to the color filter substrate, a face plate made of glass is adhered to the upper polarizer, and a corner portion of the face plate is rounded with a corner radius R of 0.3 mm or more. 
     (9) The liquid crystal display device described in the constitution (8) is characterized in that the corner portion of the face plate is rounded with a corner radius R of 0.5 mm or more. 
     (10) The liquid crystal display device described in the constitution (8) is characterized in that a side portion of the face plate is chamfered with a cutting size of 0.05 mm or more. 
     (11) The liquid crystal display device described in the constitution (8) is characterized in that the side portion of the face plate is chamfered with a cutting size of 0.15 mm or more. 
     (12) The present invention is also directed to a liquid crystal display device including a liquid crystal display panel which has a TFT substrate on which pixel electrodes and TFTs for controlling signals to the pixel electrodes are arranged in a matrix array and a color filter substrate on which color filters corresponding to the pixel electrodes are formed, wherein an upper polarizer is adhered to the color filter substrate, a face plate made of glass is adhered to the upper polarizer, and the face plate has a profile smaller than a profile of the upper polarizer. 
     (13) The liquid crystal display device described in the constitution (12) is characterized in that the upper polarizer and the face plate have an approximately rectangular shape, and the face plate is shorter than the upper polarizer by 0.5 mm or more with respect to a short-axis length and a long-axis length. 
     (14) The liquid crystal display device described in the constitution (12) is characterized in that the corner portion of the face plate is chamfered with a cutting size of 0.3 mm or more. 
     (15) The liquid crystal display device described in the constitution (12) is characterized in that the corner portion of the face plate is rounded with a corner radius R of 0.3 mm or more. 
     According to the present invention, the face plate made of glass can be adhered to the liquid crystal display panel and hence, the deterioration of image quality attributed to the interface reflection between the face plate and the liquid crystal display panel can be largely reduced. That is, in initially adhering the face plate to the liquid crystal display panel, that is, before the adhesive material is cured by ultraviolet rays, the adhesive material is in a liquid state and hence, it is possible to uniformly adhere the face plate to the liquid crystal display panel. 
     Further, according to the present invention, the glass face plate can be used and hence, the face plate exhibits high surface hardness whereby the deterioration of image quality attributed to flaws on the face plate or the like can be largely reduced. Further, by adhering the glass face plate to the liquid crystal display panel using the adhesive material, the thickness of the whole liquid crystal display device can be set smaller than the whole thickness of the conventional liquid crystal display device. 
     Since proper chamfered portion or rounded portion is formed on a corner portion of the face plate according to the present invention and hence, the strength of the face plate can be increased and, at the same time, a phenomenon that the face plate is peeled off at the corner portion can be prevented. 
     In addition to the above-mentioned advantageous effects, chamfering is applied to all sides of the face plate according to the present invention and hence, strength of the face plate can be enhanced and, at the same time, white dot defect attributed to burrs on the side portions of the face plate can be prevented. 
     Further, the face plate according to the present invention is smaller than the upper polarizer in size and hence, the generation of bubbles at the time of adhering the face plate to the upper polarizer can be suppressed thus allowing the face plate to be uniformly adhered to the liquid crystal display panel. 
     According to the present invention, by adopting the above-mentioned constitutions, the direct adhesion of the glass face plate to the liquid crystal display panel which has been impossible conventionally can be realized. 
    
    
     
       BRIEF DESCRIPTION OF THE DRAWINGS 
         FIG. 1  is an exploded perspective view of a liquid crystal display device to which the present invention is applied; 
         FIG. 2  is a cross-sectional view taken along a line A-A in  FIG. 1 ; 
         FIG. 3  is a view showing a state that a face plate is mounted on a liquid crystal display panel; 
         FIG. 4A  to  FIG. 4C  are views showing a profile of the face plate of an embodiment 1; 
         FIG. 5  is a flowchart showing manufacturing steps of the face plate; 
         FIG. 6  is a schematic view showing a profile-polishing machine of the face plate shown in  FIG. 4 ; 
         FIG. 7  is a schematic view showing a state that the face plate is wrapped; 
         FIG. 8A  to  FIG. 8C  are views showing a profile of a face plate of an embodiment 2; 
         FIG. 9A  to  FIG. 9C  are schematic views showing a profile-polishing machine of the face plate shown in  FIG. 8 ; and 
         FIG. 10  is a view showing the relationship between a face plate and a liquid crystal display panel of the related art. 
     
    
    
     DESCRIPTION OF THE PREFERRED EMBODIMENT 
     The present invention is explained in detail in conjunction with embodiments. 
     Embodiment 1 
       FIG. 1  is an exploded perspective view showing a liquid crystal display device of an embodiment 1 according to the present invention.  FIG. 2  is an exploded cross-sectional view taken along a line A-A in  FIG. 1 . In  FIG. 1 , a liquid crystal display panel is constituted of a TFT substrate  11  and a color filter substrate  12 . Pixel electrodes are formed on the TFT substrate  11  in a matrix array. TFTs (Thin Film Transistors) for changing over a signal supplied to respective pixel electrodes are also formed on the TFT substrate  11 . The color filter substrate  12  which forms color filters thereon is arranged to face the TFT substrate  11  in an opposed manner. 
     Respective thicknesses of glass substrates used in the manufacture of the TFT substrate  11  and the color filter substrate  12  are set to 0.5 mm. After completion of manufacturing of the liquid crystal display panel by filling and sealing liquid crystal between the substrates, outer sides of the liquid crystal display panel are polished so as to reduce a thickness of the whole liquid crystal display panel. In this embodiment, a thickness of the liquid crystal display panel after polishing is approximately 0.6 mm. That is, the thicknesses of the respective glass substrates are decreased by 0.2 mm by polishing. 
     The TFT substrate  11  is larger than the color filter substrate  12  in size, and a drive IC  13  and a flexible printed circuit board  15  are mounted on a portion of the TFT substrate  11  where the color filter substrate  12  does not overlap with the TFT substrate  11 . The liquid crystal display panel is housed in a resin mold  16  so that the liquid crystal display panel is mechanically protected. Although a portion of the liquid crystal display panel where the TFT substrate  11  and the color filter substrate  12  overlap with each other is mechanically strong, a portion of the liquid crystal display panel which is constituted of only the TFT substrate  11  is mechanically weak. Accordingly, the liquid crystal display panel adopts the mold  16  structure for preventing an impact from being applied to such a mechanically weak portion. 
     A backlight is arranged below the mold  16 . In  FIG. 1 , among components of the backlight, only a light guide plate  17  is shown. The flexible printed circuit board  15  is routed to a back side of the mold  16 , and is arranged below the backlight. LEDs  18  (Light Emitting Diode) which constitute a light source of the backlight are mounted on the flexible printed circuit board  15 , and are arranged on a side surface of the light guide plate  17 . On the flexible printed circuit board  15 , not only the LEDs  18  and a power source for the LEDs  18 , but also a power source for driving the liquid crystal display panel, lines for supplying signals to scanning lines and data signal lines and the like are arranged. 
     In  FIG. 1 , an upper polarizer  14  is mounted on an upper surface of the liquid crystal display panel. A face plate  30  is mounted on the upper polarizer  14 . The face plate  30  is made of glass and has a thickness of 0.95 mm. Due to the formation of the face plate  30  using reinforced glass along with the possession of such a thickness larger than the thickness of the liquid crystal display panel, the face plate  30  has the sufficient mechanical strength for protecting the liquid crystal display panel. In addition to the above-mentioned advantageous effects, by properly chamfering the face plate described later, the deterioration of the strength of the face plate is prevented. The face plate  30  is adhered to the liquid crystal display panel, to be more specific, to the upper polarizer  14  using an acrylic adhesive material  31 . 
       FIG. 2  is a cross-sectional view taken along a line A-A in  FIG. 1  and also is an exploded cross-sectional view. In the actual structure, the liquid crystal display panel and the backlight are housed in the inside of the mold  16 . The face plate  30  is adhered to the liquid crystal display panel. In  FIG. 2 , the TFT substrate  11  and the color filter substrate  12  are arranged with a gap of several μm therebetween, and the liquid crystal is sandwiched between the TFT substrate  11  and the color filter substrate  12 . A sealing material  19  is arranged on peripheries of the TFT substrate  11  and the color filter substrate  12  and the liquid crystal is sealed inside the sealing material  19 . 
     On the TFT substrate  11 , in addition to the pixel electrodes and the TFTs, scanning lines, data signal lines and the like are arranged. These lines extend to the outside after penetrating the sealing material  19 , and are connected to a drive IC  13  or a flexible printed circuit board  15 . The flexible printed circuit board  15  extends to a position behind the backlight. The LEDs  18  mounted on the flexible printed circuit board  15  are arranged on a side surface of the light guide plate  17  and constitute the light source of the backlight. A plurality of LEDs  18  is mounted on the flexible printed circuit board  15 . 
     In  FIG. 2 , the light guide plate  17  plays a role of directing the light from the LEDs  18  arranged on the side surface thereof toward a liquid-crystal-display-panel side. A reflection sheet  25  is provided for directing the light which advances downwardly from the light guide plate  17  toward the liquid-crystal-display-panel side. A lower diffusion sheet  21  is arranged on the light guide plate  17 . Although the plurality of LEDs  18  is arranged on the side surface of the light guide plate  17 , a gap exists between the LEDs  18  and the side surface of the light guide plate  17  and hence, light which advances upwardly from the light guide plate  17  becomes non-uniform. That is, a portion of the light guide plate  17  in the vicinity of the LEDs  18  becomes brighter than other portions of the light guide plate  17 . The lower diffusion sheet  21  is provided to cope with such non-uniformity of light and plays a role of making the light advancing upwardly from the light guide plate  17  uniform. 
     A lower prism sheet  22  is arranged on the lower diffusion sheet  21 . A large number of prisms which extends in the lateral direction of a screen is formed on the lower prism sheet  22  at fixed intervals, for example, at intervals of approximately 50 μm. Due to such prisms, light which is emitted from the light guide plate  17  focuses the light which tends to spread in the longitudinal direction of the screen in the direction perpendicular to the liquid crystal display panel. An upper prism sheet  23  is arranged on the lower prism sheet  22 . A large number of prisms which extends in the direction orthogonal to the prisms formed on the lower prism sheet  22 , that is, in the longitudinal direction of the screen, is formed on the upper prism sheet  23  at fixed intervals, for example, at intervals of approximately 50 μm. Due to such prisms, light which is emitted from the light guide plate  17  focuses the light which tends to spread in the lateral direction of the screen in the direction perpendicular to the liquid crystal display panel. In this manner, with the use of the lower prism sheet  22  and the upper prism sheet  23 , it is possible to focus the light which tends to spread in the longitudinal direction as well as in the lateral direction of the screen in the direction perpendicular to the screen. That is, with the use of the lower prism sheet  22  and the upper prism sheet  23 , it is possible to increase the front brightness. 
     An upper diffusion sheet  24  is arranged on the upper prism sheet  23 . The prisms which extend in the fixed direction are arranged on the prism sheets at intervals of 50 μm, for example. That is, bright and dark stripes are formed at intervals of 50 μm. On the other hand, on the liquid crystal display panel, scanning lines are formed in the lateral direction of the screen at fixed intervals, and data signal lines are formed in the longitudinal direction of the screen at fixed intervals. Accordingly, the interference occurs between the scanning lines and the lower prism sheet  22  or between the data signal lines and the upper prism sheet  23  thus generating moiré. The upper diffusion sheet  24  plays a role of reducing this moiré by making use of a diffusion effect. 
     The light which passes through the upper diffusion sheet is incident on the lower polarizer  20  which is adhered to the liquid crystal display panel and hence, the light is polarized. Transmissivity of the polarized light is controlled by the liquid crystal for every pixel in the inside of the liquid crystal display panel so as to form an image. The light which passes through the liquid crystal display panel is polarized again by the upper polarizer  14  and a viewer recognizes the light with his/her naked eyes. 
     The face plate  30  is arranged on the upper polarizer  14 . The face plate  30  according to the present invention is made of glass. Glass exhibits high hardness and hence, the face plate  30  made of glass can prevent flaws or the like formed on a front surface of the face plate  30  compared to the face plate  30  made of plastic or the like. The face plate  30  is adhered to the upper polarizer  14  using an adhesive material  31 .  FIG. 3  shows a state after the face plate  30  is adhered to the upper polarizer  14 . A thickness of the face plate  30  is 0.95 mm. Compared to a thickness of the whole liquid crystal display panel including the TFT substrate  11  and the color filter substrate  12  which is 0.6 mm, the thickness of the face plate  30  is set considerably large. Further, reinforcing treatment is applied to the face plate  30  and hence, the face plate  30  exhibits the strength considerably higher than the strength of the liquid crystal display panel. Accordingly, it is possible to sufficiently enhance a mechanical protection effect. In addition to the above-mentioned advantageous effects, as described later, the face plate is suitably chamfered at the corner portions and the side portions thereof thus preventing the deterioration of the strength of the face plate. 
     The face plate  30  is smaller than the upper polarizer  14  in size. It is preferable to set both of a short-axis length and a long-axis length of the face plate  30  shorter than a short-axis length and a long-axis length of the upper polarizer  14  by 0.5 mm or more respectively. Conventionally, the face plate  30  is arranged in a spaced-apart manner from the liquid crystal display panel with a gap therebetween. One of the reasons is that when the liquid crystal display panel and the face plate  30  are adhered to each other, the uniform adhesion cannot be acquired due to the intrusion of bubbles or the like. According to the present invention, by making the size of the face plate  30  smaller than the size of the polarizer, the probability of the intrusion of bubbles or the like at the time of adhering the face plate  30  to the liquid crystal display panel can be extremely lowered thus realizing the adhesion of the face plate  30  to the liquid crystal display panel in practice use. 
     Further, according to the present invention, by specifying a material of the adhesive material  31  used for adhering the face plate  30  to the liquid crystal display panel, the face plate  30  can be uniformly adhered to the liquid crystal display panel. That is, when the face plate  30  is adhered to the upper polarizer  14  of the liquid crystal display panel, the adhesive material  31  is in a liquid state. At the time of initially adhering the upper polarizer and the face plate to each other, the adhesive material is in a liquid state and hence, even when there exists a slight gap between the face plate  30  and the upper polarizer  14 , the gap is easily filled with the liquid. Accordingly, it is possible to prevent the intrusion of the bubbles. 
     By radiating ultraviolet rays to the adhesive material  31  which is in a liquid state initially, the adhesive material  31  is cured so that the face plate  30  is fixed to the liquid crystal display panel. Due to such a process, it is possible to uniformly adhere the face plate  30  to the liquid crystal display panel. As the adhesive material  31  which is initially in a liquid state, for example, an acrylic resin which contains 27% to 30% of acrylic oligomer, UV-reactive monomer, an additive for photo-polymerization and the like can be used. A thickness of the adhesive material  31  after curing is several μm and hence, it is possible to prevent a phenomenon that an image appears as a duplicate image described in conjunction with  FIG. 10  as a conventional example. 
       FIG. 4A  to  FIG. 4C  show a shape of the face plate  30 . The face plate  30  is provided for mechanically protecting the liquid crystal display panel and hence, the face plate  30  per se is required to be mechanically strong. The thickness t of the face plate  30  is set to 0.95 mm and reinforced glass is used as glass so as to increase the strength of the face plate  30 . However, to impart the sufficient strength to the face plate  30 , it is important to take a shape of the face plate  30  into consideration besides the material and the thickness of the face plate  30 . A particularly important point lies in a chamfer CC of corner portions and a chamfer C on side portions shown in  FIG. 4A  to  FIG. 4C . 
     In  FIG. 4A  to  FIG. 4C , the chamfer CC is formed on each corner portions. The chamfer CC is a portion which is formed by removing a sharp corner portion by shaving the corner of the glass substrate having a rectangular shape. In this embodiment, the face plate  30  is chamfered simultaneously with the formation of an accurate profile of the face plate  30  by polishing peripheries of the face plate  30 . A value C 1  which determines the shape of the chamfer CC is 0.5 mm. The value C 1  may preferably be set to 0.5 mm or more. However, when the value C 1  is set to 0.3 mm or more, it is possible to acquire the advantageous effect. On the other hand, a profile of the face plate  30  is formed smaller than a profile of the upper polarizer  14  and hence, when the value C 1  is excessively increased, the chamfer CC extends over a display region of the liquid crystal display panel. Accordingly, the value C 1  is usually set to 3 mm or less. Another significant advantageous effect acquired by the formation of the chamfers CC lies in that, by forming the chamfers on the face plate  30 , the face plate  30  is hardly peeled off from the liquid crystal display panel. According to an experiment, peeling-off of the face plate  30  from the liquid crystal display panel starts from the corner portion of the face plate  30 . Accordingly, by chamfering the corner portions of the face plate  30 , it is possible to prevent the peeling-off of the face plate  30 . 
     With respect to the strength of the face plate  30 , the next important point is the formation of the chamfer C on side portions shown in  FIG. 4A  to  FIG. 4C . All sides of the face plate  30  are chamfered. Burrs are liable to be formed on the side portion, and when burrs are generated in such a portion, the generated burrs may cause cracks. In this embodiment, a value C 1  indicative of a size of the chamfer shown in  FIG. 4C  is set to 0.15 mm. The chamfer on the side portion may preferably be set to 0.15 mm or more. However, when the value C 1  is set to 0.05 mm or more, it is possible to acquire the advantageous effect. On the other hand, an upper limit of a value C 2  of the chamfer C is determined based on the relationship between the thickness of the face plate  30  and the display region. When the thickness of the face plate  30  is set to 0.95 mm as in the case of this embodiment, the upper limit of the value C 2  is set to approximately 0.3 mm. 
     Further, in view of the relationship that the face plate  30  is smaller than the upper polarizer  14  in size, when the value C 2  of the chamfer C is increased, the chamfered portions extend over the display region. Accordingly, the upper limit of the value C 2  varies based on the thickness of the face plate  30 , a size of a screen or the like. The formation of the chamfers C also exhibits an advantageous effect in view of not only the strength of the glass but also image quality. That is, when the face plate  30  is not chamfered, burrs are liable to be formed on the side portion. These burrs are visually recognized as white dots in the periphery of the display screen, and these dots are counted as one of image quality defects. By suppressing the burrs by chamfering the face plate  30 , it is possible to prevent the white dot defect in peripheries of the screen. 
     In this embodiment, IG3 (trade name and made by ISHIZUKA GLASS CO., LTD.) is used as a material of the face plate  30 . This glass possesses the strength by 1.5 times as large as the strength of normal soda glass. However, manufacturing steps of the face plate  30  described later includes a process for reinforcing the glass in a chemical solution and hence, normal soda glass can be also used in this embodiment. 
       FIG. 5  is a flowchart showing a process of manufacturing the face plate  30  shown in  FIG. 4 . In  FIG. 5 , a large number of face plates  30  are cut from a large glass substrate in step  1 . Here, the face plate  30  is cut with a size slightly larger than a final size. This is because the face plate  30  is formed in an accurate size by polishing performed later. A large number of burrs are formed on the face plate  30  obtained by cutting the glass substrate in step  1 . In succeeding steps, there may be a case in which the glass cracks at a portion thereof where the burr is formed. In step  2 , the face plate  30  is chamfered for removing the burrs. A size of a chamfer at the time of such chamfering differs from a size of the chamfer in a final shape. 
     An initial thickness of the face plate  30  is 1.4 mm. In step  3 , a thickness of the face plate  30  is decreased to 1.0 mm by coarse polishing. A large number of flaws or the like is formed on normal glass and hence, the normal glass is not suitable for the face plate  30  of the liquid crystal display panel when the normal glass is used as it is. Accordingly, it is necessary to make a surface of the glass uniform by polishing. After finishing coarse polishing, small polishing flaws are formed on the glass surface so that the glass exhibits a frosted glass state. 
     In step  4 , a profile of the glass substrate is polished to bring the size of the profile into an accurate value.  FIG. 6  is a schematic view showing profile polishing of the glass in step  4 . In  FIG. 6 , a face plate  30 G is mounted on a disc-like roller ROL. When the roller ROL is rotated in the direction A, the face plate  30 G is also rotated in the same direction. A cam CM having a four-leaf-clover shape is coaxially mounted on a disc-like grinder GR which polishes the face plate  30 . The grinder GR and the cam CM are rotated in the direction B. The grinder GR and the face plate  30  are in contact and hence, the profile of the face plate  30  is polished. 
     The roller ROL which rotates the face plate  30  is brought into contact with the cam CM. Accordingly, by moving the grinder GR in the direction C, an amount which the face plate  30  is shaved can be adjusted. Further, the roller ROL is moved tracing the cam CM and hence, the grinder GR can follow the profile of the rectangular face plate  30 . Due to the complicated shape of the cam CM as shown in  FIG. 6 , it is possible to form the chamfer CC with the value C 1  of 0.5 mm on the corner portion of the face plate  30 . Here, as described above, when the value C 1  is 0.3 mm or more, it is possible to acquire the advantageous effect. The chamfer CC formed on each corner portion of the face plate  30  is extremely important for enhancing the strength of the face plate  30  and hence, the profile of the face plate  30  is controlled by using the grinder shown in  FIG. 6 . 
     In this manner, the profile of the face plate  30  is determined and, thereafter, in step  5  shown in  FIG. 5 , the chamfer C is formed on the face plate  30 . In step  5 , in the same manner as the chamfer C in the final state, the chamfer C with the value C 2  of 0.15 mm is formed on the face plate  30 . As described above, when the value C 2  is set to 0.05 mm or more, it is possible to acquire the advantageous effect. 
     Next, in step  5  shown in  FIG. 5 , precision polishing of the face plate  30  in the thickness direction is performed. Although the face plate  30  is polished in the thickness direction by coarse polishing in step  3 , in a state after coarse polishing, a surface of the face plate  30  exhibits a frosted glass state. In step  5 , the surface of the face plate  30  is polished into a transparent state by precision polishing. The surface of the face plate  30  is slightly shaved by this precision polishing and a plate thickness of the face plate  30  is decreased from 1.0 mm to 0.95 mm. That is, the face plate is polished by 0.025 mm on each side. This polishing amount is small and hence, the chamfer C formed in step  5  is not largely influenced. 
     Then, in step  7 , a polishing agent is removed by cleaning. After cleaning, in step  8 , chemical reinforcement treatment is applied to the face plate  30 . The chemical reinforcement treatment is performed for chemically strengthening glass with an action of ions by immersing the face plate  30  into a chemical solution of high temperature. The chemical reinforcement treatment is performed by immersing the face plate  30  in the chemical solution at a temperature of approximately 400° C. for approximately 10 hours. Although the chemical reinforcement treatment takes time, the treatment can treat a large number of face plates  30  at a time. 
     After performing the chemical reinforcement treatment, the face plate  30  is cleaned by applying ultrasonic cleaning to the face plate  30  thus removing chemical substances remaining on the surface of the face plate  30 . Then, the face plate  30  is wrapped with a sheet and is shipped to a liquid crystal display panel maker. 
       FIG. 7  is a schematic view showing a state in which the face plate  30  is wrapped with a wrapping sheet for shipping. Conventionally, a sheet for such wrapping adopts the following constitution. The wrapping sheet is formed of a polyethylene film. An adhesive material is applied to a surface of the polyethylene film, and the face plates  30  are fixed to the polyethylene film using the adhesive material. A thickness of the whole wrapping film  40  is 70 μm, while a thickness of the adhesive material is 10 μm to 20 μm. 
     After receiving the face plates  30 , the liquid crystal display panel maker cleans the face plates  30 . When the face plate  30  is fixed to the wrapping film  40  using the adhesive material, as described in the related art, the adhesive material is adhered to the face plate  30 . The adhesive material which is adhered to the face plate  30  is peeled off at the time of cleaning the face plate  30  and remains in the cleaning liquid. This adhesive agent is adhered to the face plate  30  again leading to insufficient cleaning. To cope with this insufficient cleaning, in this embodiment, instead of applying the adhesive material to the wrapping film  40 , the face plate  30  is fixed to the wrapping film  40  using static electricity generated on the polyethylene film. After fixing the face plate  30  to the wrapping film  40 , the face plate  30  is covered with the wrapping sheet  40  thus protecting and fixing the face plate  30 . 
     Embodiment 2 
       FIG. 8A  to  FIG. 8C  show a shape of a face plate  30  used in an embodiment 2 of the present invention. The constitution of the liquid crystal display device of this embodiment is substantially equal to the constitution of the liquid crystal display device explained in conjunction with  FIG. 1  and  FIG. 2 . In  FIG. 8 , a point which makes this embodiment different from the embodiment 1 in the shape of the face plate  30  lies in that a rounded portion RC is formed on each corner portions instead of forming the chamfer. The rounded portions RC are formed on the face plate  30  to enhance the strength of the face plate  30  as well as to cope with the peeling-off of the face plate  30 . 
     In this embodiment, instead of the chamfers, the rounded portions are formed on the face plate  30 . Since corner portions are not formed in a square shape in this embodiment, the strength of the glass can be further advantageously enhanced. Further, this embodiment can also acquire the advantageous effect that peeling-off of the face plate  30  from the liquid crystal display panel can be prevented in the same manner as the embodiment 1. A size of the rounded portion RC is 0.5 mm in this embodiment. When the size of the rounded portion RC is 0.3 mm or more, it is possible to acquire the advantageous effect attributed to rounding of the corner portion. Further, when the size of the rounded portions RC is excessively increased, the rounded portion RC extends over the corner of the display surface and hence, it is necessary to determine the size of the rounded portion RC by taking a display area into consideration. In general, the size of the rounded portion RC is set to 3 mm or less. However, an upper limit of the size of the rounded portion RC is determined based on the size of an effective display screen and hence, it is not necessary to set an upper limit with respect to strength of the face plate  30  or peeling-off of the face plate  30 . 
     Also in this embodiment, the chamfers C are formed on side portions of the face plate  30 . In the same manner as the embodiment 1, the chamfers C are formed on the face plate  30  for enhancing the strength of the face plate  30  and, at the same time, for preventing the generation of white dots in the periphery of the display screen. A size C 2  of the chamfer C shown in  FIG. 8C  is set to 0.15 mm in the same manner as the embodiment 1. The side portion may preferably be chamfered with a cutting size of 0.15 mm or more. However, when the side portion is chamfered with a cutting size of 0.05 mm or more, it is possible to acquire the advantageous effect. On the other hand, in the same manner as the embodiment 1, an upper limit of the cutting size of the chamfer C 2  is determined based on the relationship between the plate thickness of the face plate  30  and the display region. 
     In the same manner as the embodiment 1, the plate thickness of the face plate  30  in this embodiment is set to 0.95 mm. Further, although IG3 (trade name and made by ISHIZUKA GLASS CO., LTD.) is used as a glass material in this embodiment, soda glass may be used as the glass material in the same manner as the embodiment 1. The process flow for manufacturing the face plate  30  of this embodiment is substantially equal to the process flow for manufacturing the face plate  30  of the embodiment 1 explained in conjunction with  FIG. 5 . Here, the face plate  30  of this embodiment differs from the face plate  30  of the embodiment 1 in profile and hence, this embodiment differs from the first embodiment in polishing of the profile of the face plate  30  in step  4  explained in conjunction with  FIG. 5 . 
       FIG. 9A  to  FIG. 9C  are schematic views showing a polishing machine for accurately forming the profile of the face plate  30  shown in  FIG. 8 . Also in  FIG. 9 , this embodiment adopts the substantially same basic constitution as the constitution of the polishing machine shown in  FIG. 6 . That is, the profile of the face plate  30  is polished by moving a grinder GR along with the movement of a roller ROL which corresponds to a cam CM.  FIG. 9A  is a side schematic view of the polishing machine,  FIG. 9B  is a view showing the polishing machine shown in  FIG. 9A  as viewed in the direction A in  FIG. 9A , and  FIG. 9C  is a view showing the polishing machine shown in  FIG. 9A  as viewed in the direction B. 
     In  FIG. 9A ,  FIG. 9B  and  FIG. 9C , for facilitating the understanding of the drawing, although the cam CM is depicted in a state that the cam CM is in a spaced-apart manner from the roller ROL, the cam CM is in contact with the roller ROL in an actual state. Further, in  FIG. 9A ,  FIG. 9B  and  FIG. 9C , although the grinder GR is depicted in a state that the grinder GR is spaced-apart from the face plate  30 , the grinder GR is in contact with the face plate  30  in an actual state. 
     When the roller ROL is rotated, a rotary shaft AX is moved tracing the shape of the cam CM. Then, the grinder GR which is mounted coaxially with the roller ROL is also moved in the same manner as the roller ROL. That is, the grinder GR is moved tracing the shape of the cam CM. The face plate  30  is brought into contact with the grinder GR and hence, a profile of the face plate  30  is polished by the rotating grinder GR tracing the shape of the cam CM. The shape of the cam CM becomes a shape similar to a final profile of the face plate  30 . By forming a rounded portion R corresponding to a corner portion of the face plate  30  on the corner portion of the cam CM, the rounded portion R of the face plate  30  is formed. 
     Steps  5  to  10  which follow step  4  in which the profile of the face plate  30  is determined are substantially equal to steps  5  to  10  of the embodiment 1. Step of adhering the face plate  30  produced in the above-mentioned manner to the liquid crystal display panel is substantially equal to the corresponding step explained in conjunction with the embodiment 1. Further, the profile of the face plate  30  of this embodiment is formed smaller than the size of the upper polarizer  14  adhered to the liquid crystal display panel in the same manner as the embodiment 1. In the same manner as the embodiment 1, the short-axis length and the long-axis length of the face plate  30  may preferably be set smaller than the short-axis length and the long-axis length of the upper polarizer  14  by 0.5 mm or more. According to this embodiment, by forming the rounded portion R on the corner portion of the face plate  30 , it is possible to increase the strength of the face plate  30  and, at the same time, it is possible to prevent peeling-off of the face plate  30  from the liquid crystal display panel at the corner portions.