Abstract:
The present invention relates to a method and a system for preparing dental restorations from ceramic or polymeric material to achieve color and opacity gradients simulating natural dentition, wherein an ingot of ceramic or polymeric material is entirely or partially forced through a system of channels in a press mold into a mold cavity in the press mold, wherein the mold cavity corresponds to a dental restoration.

Description:
REFERENCE TO RELATED APPLICATIONS 
       [0001]    This application claims priority pursuant to 35 U.S.C. §119 to European Patent Application No. 07023059.4 filed Nov. 28, 2007. 
       BACKGROUND 
       [0002]    The present invention relates to a method and a system for preparing dental restorations from ceramic or polymeric material to achieve color and opacity gradients that simulate natural dentition. 
         [0003]    A molding method such as that described for example in EP 0 231 773 A1 or U.S. Pat. No. 5,702,514 A is known for the preparation of dental restorations from ceramic material. In that method, a model of a dental restoration made of a material that can be burned out completely is fitted onto a strand forming the later casting channel inside a press muffle and the press muffle is filled with an investment material, so that the model is completely surrounded by the investment material. The investment material is cured to form a refractory press mold and the model is burned out, in order to produce the mold cavity corresponding to a dental restoration in the cured press mold. A ceramic material is then forced through the casting channel into the press mold by applying pressure, in order to fill the mold cavity corresponding to the dental restoration and consequently produce the dental restoration from the ceramic material. 
         [0004]    A disadvantage of the known methods and systems is that the known molding methods are only suitable for dental restorations of a single color. If a naturally appearing reproduction in the form of a dental restoration of color and opacity gradients that occur in a great variety of natural dentition is desired, then according to the prior art, a subsequent surface treatment, such as for example by painting or coating, is unavoidable. Such a subsequent surface treatment is laborious and expensive because of the manual work involved. 
         [0005]    It is therefore an object of the present invention to provide a method and a system for preparing dental restorations from ceramic or polymeric material, wherein color and opacity gradients are achieved without subsequent surface coating. 
       SUMMARY OF THE INVENTION 
       [0006]    These and other objects and advantages are accomplished by the method of preparing dental restorations from ceramic or polymeric materials to achieve color and opacity gradients that simulate natural dentition to provide a restoration having a natural appearance. In one aspect of the method of the invention, an ingot of ceramic or polymeric material is entirely or partially forced through a system of channels in a press mold into a mold cavity in the press mold, wherein the mold cavity corresponds to a dental restoration. The ingot has a first volume region and a second volume region wherein the second volume region differs from the first volume region by a different color or opacity, or by both color and opacity. The system of channels in the press mold directs the ingot into the mold cavity in the molding process in such a way that material of the first volume region reaches the mold cavity at an earlier time than material of the second volume region and/or more material of the first volume region than material of the second volume region is forced into the mold cavity. 
         [0007]    According to a second aspect of the present invention, a system for preparing dental restorations from ceramic or polymeric material to achieve color and opacity gradients that simulate natural dentition is provided, wherein the system comprises an ingot of ceramic or plastic, a press muffle base and a sprue pin system of material that can be burned out completely. The sprue pin system fits onto the press muffle base and attaches to a model of a dental restoration. The sprue pin system and dental model are fabricated of material that can be burned out completely, so that a press mold with a system of channels corresponding to the sprue pin system and a mold cavity corresponding to the model can be produced by fitting the model onto the press muffle base via the sprue pin system. A press mold produced in this way is suitable for forcing an ingot into the mold cavity of the press mold. The ingot has a first volume region and a second volume region, the second volume region differing from the first volume region by a different color or opacity, or both color and opacity. The sprue pin system is prefabricated and configured in such a way that the system of channels created in the production of the press mold has two flow paths, the second flow path having a greater volume than the first flow path. The material of the first volume region is forced into the mold cavity through the first flow path and material of the second volume region is forced into the mold cavity through the second flow path in a molding process. 
         [0008]    According to a third aspect of the present invention, use of an ingot fabricated of a ceramic or polymeric material for preparing dental restorations from ceramic or polymeric material to achieve colour and opacity gradients that simulate natural dentition is provided. The ingot has a first volume region and a second volume region wherein the second volume region differs from the first volume region by a different color or opacity. The ingot is entirely or partially forced through a system of channels in a press mold into a mold cavity in the press mold, wherein the mold cavity corresponds to a dental restoration. In the molding process, the system of channels in the press mold directs the ingot into the mold cavity in such a way that material of the first volume region reaches the mold cavity at an earlier time than material of the second mold region and/or more material of the first volume region than material of the second mold region is forced into the mold cavity. 
         [0009]    In this description, the term “dental restoration” comprises crowns, partial crowns, veneers, bridges, abutments or other appliances. The present invention is also suitable for the overmolding of structures of ceramic, metal or metal alloys. The term “flow path” is defined as the path that the material of a volume region of the ingot follows in the molding process. The volume of a flow path is determined by the surface area of the material of a volume region along the flow path multiplied by the length of the flow path. According to the configuration of the system of channels, the flow path may, for example, divide and form branches that do not lead into the mold cavity. Flow paths of volume regions do not have to run through separate channels in the system of channels but may also run through a common channel. The total volume of a flow path is determined by the volume of the system of channels that is taken up by material of a volume region of the ingot after the molding process. 
         [0010]    The invention also encompasses methods, systems and uses for the simultaneous or non-simultaneous preparation of any desired number of dental restorations with the same or different colour and opacity gradients involving the use of one or more systems of channels or sprue pin systems. 
         [0011]    In a preferred embodiment of the method according to the invention, the system of channels and the mold cavity corresponding to a dental restoration are produced by a prefabricated sprue pin system made of material that can be burned out completely, such as acrylic or wax. Prior to the molding process, a model of a dental restoration made of material that can be burned out completely is fitted onto a press muffle base of a press muffle by means of the sprue pin system. The press muffle is then filled with a refractory die material or investment material so that the model and the sprue pin system are completely surrounded by the investment material. The investment material is cured to form a refractory press mold and the model and the sprue pin system are burned out, in order to produce the mold cavity corresponding to a dental restoration and the system of channels in the cured press mold. 
         [0012]    Preferably, the model of a dental restoration is connected mesially or distally to the sprue pin system. This is more advantageous than attachment of sprue pins to an occlusal side of a restoration since the later detachment of the system of channels is easier and the geometry of the opposite teeth does not have to be taken into consideration. 
         [0013]    In order to produce color and opacity gradients that simulate natural dentition in a dental restoration directly by the molding process, the ingot has, according to the invention, a first volume region and a second volume region, the second volume region differing from the first volume region by a different color or opacity or both color and opacity. The different volume regions may, for example, be a dentine material and an incisal material for the dental restoration. Often, a third volume region is also used, corresponding to a cervical dentine material. The number of volume regions is in principle unlimited. 
         [0014]    Under the effect of pressure during the molding process of forcing the ingot, with optionally prior or simultaneous heating of the ingot, the material of the ingot, i.e. the ceramic or the polymer, becomes viscous or flowable and can be forced into a mold cavity in the press mold that corresponds to a dental restoration. Incidentally, the system of channels in the press mold directs the molding into the mold cavity in the molding process. 
         [0015]    According to the method of the present invention, the ingot, which is flowable in the molding process, is directed into a mold cavity corresponding to a dental restoration in such a way that the first volume region of the molding reaches the mold cavity at a time before the second volume region. As a result, color and opacity gradients that simulate natural dentition are achieved in the dental restoration without the need for subsequent laborious coating and color characterization. Both the nominal volume fraction and the spatial position of the individual volume regions in the dental restoration are in this way controlled by the system of channels. The dental restoration exhibits a natural appearance as a result of the distribution of the differently colored or transparent volume regions of the ingot that is controlled by the system of channels. 
         [0016]    In an aspect of the method according to the invention, the ingot of ceramic or polymeric material can be referred to as a press blank, which may be of a one-piece or multi-part form. In the case of a multi-part molding, the individual parts are fused together by heating or pressing together before the actual molding operation. Preferably, in this case each individual part represents a volume region with a specific color and/or opacity. 
         [0017]    Preferably, the color or opacity gradient between the volume regions of the ingot is steady and gradual, which corresponds to the color variations in natural dentition. The ingot preferably has a molding direction, along which the cross-sectional area of the ingot is constant, so that the ingot can be forced into the press mold along the molding direction. The form of the molding may, in particular, be substantially cylindrical, although other shapes are possible including, but not limited to, round, rectangular, square or polygonal. 
         [0018]    There are various possible ways in which the volume regions with different color or opacity gradients are distributed in the ingot. For example, the volume regions may extend substantially along the molding direction and be substantially adjacent to one another at a plane with a normal that extends substantially perpendicularly to the molding direction of the ingot. As an alternative to this, the volume regions may in each case substantially make up a layer of the ingot and be substantially adjacent to one another at a plane with a normal that extends substantially parallel to the molding direction of the ingot. In addition, it is also possible that the volume regions in each case make up a piece of the ingot and are substantially adjacent to one another at a plane with a normal that extends obliquely to the molding direction of the molding. 
         [0019]    The ingot may have more than a first volume region and a second volume region, with additional volume regions differing neighbouring volume regions by a different colour or opacity. 
         [0020]    In accordance with the configuration of the ingot with the at least two volume regions with a different color and/or opacity, the system of channels in the present mold must be configured such that it is adapted to the ingot. This is advantageously ensured by a prefabricated sprue pin system that matches a specific ingot. The system of channels must ensure that one volume region of the ingot reaches the mold cavity at a time before the other volume region. This can be achieved, for example, by a system of channels that has two flow paths, the second flow path having a greater volume than the first flow path, and the first volume region being forced into the mold cavity through the first flow path and the second volume region being forced into the mold cavity through the second flow path in the molding process. The flow paths may, for example, be separate channels, but they are not limited to separate channels. Both flow paths may lead through a common channel, the system of channels ensuring that one volume region of the ingot fills a greater volume of the system of channels than the other volume region in the molding process. Since uniform pressure prevails within the entire system of channels in the molding process, that is, along both flow paths, that volume region that fills a greater volume in the system of channels reaches the mold cavity later than that volume region that fills a smaller volume in the system of channels. The difference in the volume in the flow paths may be achieved, for example, by the sprue pin system being configured with an extension of the form of any shape that adds volume to the flow path or paths, so that a reservoir corresponding to the extension is obtained as part of the second flow path in the production of the press mold. As a result, during the molding process a reservoir is first filled with one volume region, so that this volume region reaches the mold cavity at a later time than the other volume region. 
         [0021]    The configuration in the form of an extension also has the advantage that the volume of the extension, and consequently the resultant reservoir, can be reduced by shortening the extension before the press mold is produced. The sprue pin system can in this way be adapted to the desired color or opacity gradients in the dental restoration 
         [0022]    It may be preferable to provide an ingot that does not have an exact rotational symmetry along the molding direction. For example, if the volume regions do not make up disc-shaped regions of the ingot, the volume regions are arranged in the ingot in such a way that no rotational symmetry is obtained. With a disturbed rotational symmetry, a distinct orientation of the ingot in a plane with a normal that extends substantially parallel to the molding direction of the ingot is obtained within the press mold. Before the molding process, the ingot is located in a pressing space within the press mold, the pressing space being created by an extension of the press muffle base in the production of the press mold. Consequently, the form of the extension of the press muffle base should correspond substantially to the outer form of the ingot. To this extent, a disturbed rotational symmetry of the ingot is only advisable if the extension of the press muffle base has a corresponding disturbed rotational symmetry. This ensures that a distinct orientation of the ingot is achieved when it is inserted into the press space for the molding process before the production of the press mold by way of arranging the sprue pin system at the extension of the press muffle base. 
         [0023]    For multi-part ingots, which may be put together as desired by the user to form an ingot for the molding process, it may also be advisable if the height of the extension of the press muffle base is adjustable, so that a press space with a corresponding depth is obtained in the press mold in the production of the press mold as a result of the adjusted height of the extension. The ingot is consequently not restricted to a specific height. 
     
    
     
       BRIEF DESCRIPTION OF THE DRAWINGS 
         [0024]    The present invention will be more fully understood and appreciated by reading the following Detailed Description in conjunction with the accompanying drawings, in which: 
           [0025]      FIG. 1  is a schematic representation of a first preferred embodiment of the method or system according to the invention during the production of the press mold with a sprue pin system and a model of a dental restoration; 
           [0026]      FIG. 2  is a schematic representation of a first preferred embodiment of the method or system according to the invention after the production of the press mold with a system of channels, a mold cavity and an ingot inserted into the press space of the press mold, before the molding operation; 
           [0027]      FIGS. 3   a  through  3   c  show embodiments of the ingot produced from the method or system according to the invention; 
           [0028]      FIGS. 4   a  through  4   d  show embodiments of the ingot in the extension of the press muffle base of the method or system according to the invention for the distinct orientation of the ingot in the press mold; 
           [0029]      FIGS. 5   a  through  5   b  show a detailed representation of a first preferred embodiment of the method or system according to the invention during the molding operation; 
           [0030]      FIG. 6  is a detailed representation of a second preferred embodiment of the method or system according to the invention before the molding operation; 
           [0031]      FIG. 7  is a detailed representation of a second preferred embodiment of the method or system according to the invention during the molding operation; 
           [0032]      FIG. 8  is a detailed representation of a second preferred embodiment of the method or system according to the invention after the molding operation; 
           [0033]      FIG. 9  shows an embodiment of the sprue pin system for producing a system of channels of the method or system according to the invention; and 
           [0034]      FIGS. 10   a  through  10   d  show further embodiments of the sprue pin system for producing a system of channels of the method or system according to the invention in connection with matching extensions of the press muffle base. 
       
    
    
     DETAILED DESCRIPTION 
       [0035]    As will be appreciated, the present invention provides an effective and efficient method for manufacturing colored or shaded ceramic dental restorations. Reference is made to  FIG. 1 , which shows how a press mold  1  is produced by means of a press muffle  3  with a press muffle base  5 . The press muffle base  5  includes a cylindrical extension  7 , which extends upward from the plate-shaped bottom  9  of the press muffle base  5 . A press muffle sleeve  11  fits flush with and onto the bottom  9 , and consequently forms together with the bottom  9  an outer filling mold. 
         [0036]    A sprue pin system  15 , which is made of a material that can be burned out completely, such as for example plexiglass or wax, is placed on the upper end face of the cylindrical extension  7 . In this embodiment, the sprue pin system  15  is H-shaped, being placed upright with both legs of the H-shape on the extension  7 . Sprue pin system  15  may be any shape suitable to hold a model of a dental restoration. A model  17  of a dental restoration, likewise made of material that can be burned out completely, such as for example plexiglass or wax, is formed or fitted on one leg of the H-shape of pin system  15 . The press muffle  3  is filled with an embedding compound or a refractory die material, which completely surrounds the extension  7 , the sprue pin system  15  and the model  17 . The embedding compound is any refractory die material, such as, but not limited to a gypsum-like, phosphate-bonded composition, comprising for example silica powder, and is initially flowable and cures to form the press mold  1  after filling in press mold  1 . After curing, the “burn-out” process proceeds to burn out the material of sprue pin system  15  and model  17 . The burn-out process leaves no residue from the sprue pin system  15  and of the model  17 . Thereafter, the press muffle  3 , including press muffle base  5 , bottom  9  and extension  7 , and press muffle sleeve  11  are detached from the press mold  1 . 
         [0037]      FIG. 2  shows the press mold  1  after completion of the burn out process. The burned-out sprue pin system  15  creates a system of channels  19  and the burned-out model  17  creates a mold cavity  21  corresponding to the dental restoration model  17 . The removed press muffle base  5 , in combination with the extension  7  that extends into press mold  1 , creates a press space  23  in the press mold  1 . 
         [0038]    An ingot  24 , also known as a blank or pellet, is inserted in the press space  23 . Ingot  24  has a first volume region  25  and a second volume region  27 . The volume regions  25  and  27  differ from each other by their color and/or opacity. Although there appears to be a sharp contrast in color, opacity and other properties between the first volume region  25  and the second volume region  27  as suggested in the representation, the volume regions  25 ,  27  have steady, gradual and smooth transitions in accordance with the color variations in natural teeth. The ingot  24  has the same outer cylindrical form as the extension  7  of the press muffle base  5 , so that it can be inserted with an exact fit into the press space  23 . 
         [0039]    A press ram or piston  29  with the same cylindrical form as press space  23  can then force the ingot  24  through the system of channels  19  into the mold cavity  21  as soon as the ingot  24  has become viscous or flowable under the effect of heat and/or pressure. In this embodiment, the two volume regions  25 ,  27  are in each case a half-cylinder of the ingot  24 , which are adjacent to each other at an interface which has a normal that extends perpendicularly to the ingot direction, which is indicated by the force arrow F. The ingot  24  is oriented such that, before the molding process, an end face of the first volume region  25  is arranged directly in front of the leg of the H-shaped system of channels  19  into the mold cavity  21  that is directly adjoined by the mold cavity  21 . The other leg of the H-shaped system of channels  19  has in the upper part a blind channel  33 , which is not directly connected to the mold cavity  21  but only via the cross-channel and the upper part of the other leg. Before the molding process, the second volume region  27  is located with an end face directly in front of the leg with the blind channel  33 , so that the second volume region  27  can only reach the mold cavity  21  via the cross-channel and the upper part of the other leg. Since the molding direction, as indicated by the force arrow F, runs in the longitudinal direction of the leg of the H-shaped system of channels  19 , during the molding process, the blind channel  33  is filled with the second volume region  27  before the pressure forces the second volume region  27  laterally through the cross-channel and finally through the upper part of the leg that is directly connected to the mold cavity  21  into the mold cavity  21 . Since the flow path of the second volume region  27  in the system of channels  19  has a greater volume than the flow path of the first volume region  25  in the system of channels  19 , the first volume region  25  reaches the mold cavity  21  before the second volume region  27 . As a result, a greater volume fraction of the mold cavity  21  is filled by the first volume region  25  then by the second volume region  27 . 
         [0040]    In  FIG. 3 , possible configurations of the ingot  24  are shown. Even if only cylindrical forms of the ingot  24  are shown, any other form that has a constant cross-sectional form along a molding direction is also conceivable. The volume regions  25 ,  27  may be distributed in the ingot  24  in various ways. In  FIG. 3   a,  a distribution of the volume regions  25 ,  27  as half-cylinders is shown, corresponding to the exemplary embodiment from  FIG. 2 .  FIG. 3   b  shows the individual volume regions  25 ,  27  as discs, axially aligned atop one another. Apart from the volume regions  25 ,  27 , the ingot  24  may have an additional volume region  35  or a number of additional volume regions. With the distribution of the volume regions  25 ,  27 ,  35  as discs, a configuration of the system of channels  19  such as in  FIG. 2  is unsuitable, and a system of channels  19  or a sprue pin system  15  with a configuration as shown in  FIGS. 6 ,  7 ,  8  and  10  would have to be used. However, it is advantageous that the configuration of the volume regions as discs is conducive to providing the ingot  24  in a multi-part form. Individual parts in disc form then advantageously each form a volume region. The arrangement of the individual parts can then be put together as desired by the user. Before the actual molding operation, the individual parts are fused together under the effect of heat and/or pressure to form an ingot  24  with the corresponding volume regions.  FIG. 3   c  shows that an interface between the volume regions  25  and  27  that is oriented obliquely in relation to the molding direction is also conceivable. 
         [0041]    For the configurations of the ingot  24  according to  FIGS. 3   a  and  3   c  or any other configuration in which the individual volume regions do not have the form of a disc, the orientation about the molding direction of the ingot  24  is not distinct. If, however, the configuration of the system of channels  19  requires a specific orientation about the molding direction of the ingot  24 , as represented in the embodiment in  FIG. 2 , it is advisable to ensure a distinct orientation by the form of the ingot  24 .  FIGS. 4   a  through  4   d  show various possible ways in which the rotational symmetry of the ingot  24  about the molding direction can be disturbed in order that the orientation of the ingot  24  in the press space  23  of the press mold  1  is distinct. In this case, a distinct orientation is only ensured when the extension  7  of the press muffle base  5  has an analogous disturbance of the rotational symmetry. The end face of the ingot  24  that is to be introduced first into the press space  23  of the press mold  1  could, for example, be bevelled as shown in  FIG. 4   a,  the gradient of the bevelling running along the borderline between the volume regions on the end face. The ingot  24  may also be flattened on one side of the lateral surface as shown in  FIG. 4   b,  or have a groove or notch as shown in  FIG. 4   c.  The end face that is to be introduced first into the press space  23  of the press mold may also have a notch or groove, as shown in  FIG. 4   d,  to prevent rotational symmetrical ambiguity in the orientation about the molding direction. In any case, the press space  23  of the press mold  1  must have a corresponding shape or notch that creates a disturbance of the rotational symmetry, in order that the ingot  24  can be inserted with an exact fit and is then directly located in front of the system of channels  19  before the molding process. If parts of the sprue pin system  15  are configured in such a way that the system of channels  19  produced as a result makes up part of the press space  23  of the press mold  1  (see  FIGS. 6 ,  7 ,  8  and  10 ), the sprue pin system  15  may also provide a corresponding disturbance of the rotational symmetry in the press space  23  of the press mold  1 . 
         [0042]    In  FIGS. 5   a  and  5   b,  the embodiment according to  FIG. 2  is shown in more detail during and after the molding process. While the first volume region  25  is already being forced into the mold cavity  21 , the second volume region  27  is still on its way to the mold cavity  21  along the second flow path via the leg with the blind channel  33 , the cross-channel and the upper part of the leg that is connected to the mold cavity  21 . When this happens, the blind channel  33  is filled, since the pressure in the molding direction has first forced a first flow direction of the second volume region  27  into the blind channel  33  until the latter is filled. Once the blind channel  33  is filled, the flow direction of the second volume region  27  follows the cross-channel and finally the pressure in the molding direction forces it to the mold cavity  21  along the upper part of the leg that is connected to the mold cavity  21 . The flow path that the flow direction of the second volume region  27  follows therefore has a greater volume than the flow path followed by the flow direction of the first volume region  25  to the mold cavity  21  directly through the leg that is connected to the mold cavity  21 . In the upper part of the leg that is connected to the mold cavity  21 , the volume regions  25 ,  27  are reunited. 
         [0043]    After the molding process, the mold cavity  21  has a higher volume fraction of the first volume region  25  than of the second volume region  27 . Color and opacity gradients creating natural tooth color and opacity effects are thereby achieved in the dental restoration. Following the molding process, the ingot  24 , which has been forced into mold space  21 , is cured. The press mold  1  is then removed by cutting, milling, sand-blasting, etching and/or other customary methods. Subsequently, the dental restoration, which comprises the filling of the mold cavity  21 , is separated from the material of the ingot  24  that has filled the system of channels  19 . At the point at which the model  17  was fitted on the sprue pin system  15 , the dental restoration must be manually reworked in order to ensure mesial and distal surfaces of the dental restoration that correspond to the natural tooth. It is beneficial if the sprue pins for the model are not provided occlusally, but mesially or distally, since then the form of the opposite teeth does not have to be taken into consideration in the manual reworking. 
         [0044]    A further embodiment of the invention is shown in  FIGS. 6 ,  7  and  8 . This embodiment is particularly well suited for the simultaneous preparation of a number of dental restorations at the same time. This example encompasses two dental restorations that are prepared at the same time in one molding operation, but it may also encompass three or more restorations. In this example, an ingot  24 , such as that shown in  FIG. 3   b,  is used. The volume regions  25 ,  27  and  35  are in the form of discs and together form the cylindrical ingot  24 . The volume region  25  corresponds to the dentine material, the volume region  27  corresponds to the incisal material and the volume region  35  corresponds to the cervical dentine material. 
         [0045]    The system of channels  19  in the press mold  1  has been created by a sprue pin system  15  such as that shown in  FIG. 10 . The sprue pin system  15  substantially comprises a sheet of, for example, plastic or wax material and can be inserted into a continuous slit providing an exact fit on the end face of the extension  7  of the press muffle base  5 . When this happens, the sprue pin system  15  completely fills the slit and protrudes laterally from the lateral surfaces of the extension  7  of the press muffle base  5 . The models of the dental restorations are fitted onto these lateral protrusions. The sprue pin system  15  also has an extension  30 , which protrudes from the end face of the extension  7  in the press muffle base  5  in the molding direction. In order that, after insertion, the sprue pin system  15  is also seated centrally in the slit on the end face of the extension  7  of the press muffle base  5 , the sprue pin system  15  may have a tongue  39 , which engages in a corresponding groove  41  in the slit on the end face of the extension  7  of the press muffle base  5 . After the embedding, curing and burning out of the press mold  1 , a system of channels  19  and two mold cavities  21  are obtained, as shown in  FIGS. 6 to 8 . 
         [0046]    A third volume region  35  of the ingot  24  lies directly at the front edge of the press space  23  and a reservoir  31 , which is obtained from the burned-out sprue pin system  15  with the extension  30 . Further reservoirs  31  are arranged on the underside of the system of channels  19 , in order that the flow path for the second volume region  27 , i.e. the incisal material, runs through the volume of the lower reservoir  31 . The number and configuration of reservoirs  31  and their arrangement and orientation on the system of channels  19  may be chosen as desired by way of the configuration of the sprue pin system  15 . 
         [0047]    The first volume region  25 , here in the form of the dentine material, represents the middle layer, which is adjoined by the third volume region  35 , that is to say the cervical dentine material, which is in direct contact with the press ram  29 .  FIG. 7  shows what happens when the ingot  24  is forced into channels  19 . The third volume region  35  is forced into the reservoir  31  and also laterally into the channels, while the other volume regions  25 ,  27  are forced exclusively laterally into the channels. Since the lateral pressure during the filling of the upper reservoir  31  increases as it becomes more distant from the upper reservoir  31 , the third volume region  35  experiences a lower lateral pressure than the other volume regions  25 ,  27 , as long as the upper reservoir  31  is not yet filled. Only after the upper reservoir  31  is filled, the third volume region  35  is forced into the mold cavities  21  with the same force as the other volume regions  25 ,  27 . The filling of the lower reservoir  31  with the second volume region  27 , i.e. the incisal material, proceeds in an analogous way. As a result, less incisal material than dentine material is forced into the mold cavities  21 . 
         [0048]    As shown in  FIG. 7 , the third volume region  35  already lags behind the other volume regions  25 ,  27 , so that less volume of the mold cavities  21  is filled by the third volume region  35 , i.e. the cervical dentine material, than by the first volume region  25 , i.e. the dentine material. Because of the reservoirs  31 , a number of flow fronts or directions are obtained for the second volume region  27  and for the third volume region, partially extending into the reservoirs  31  and consequently forming in each case an overall flow path with a greater volume than the flow path of the first volume region  25 . 
         [0049]    In  FIG. 9 , an H-shaped sprue pin system  15  corresponding to the first embodiment of  FIG. 2  is represented. The leg of the H-shaped sprue pin system  15  that is not intended to provide a sprue pin for the model  17  has in the upper part an extension  30 , which leads to a blind channel  33  in the creation of the press mold  1 . Since the length of the extension  30  has an effect on the volume of the blind channel  33 , and consequently directly on the volume fraction of the second volume region  27  in the dental restoration, it is advisable that the length of extension  30  be adjustable for the user. Consequently, the extension  30  advantageously has a scale, on the basis of which the user can shorten the length of the extension  30  by cutting it off, in order to achieve a desired distribution of the volume regions  25 ,  27  in the dental restoration. As shown in  FIG. 10   a,  the extensions  30  of the second exemplary embodiment may also each have a scale for cutting off. 
         [0050]    While the invention has been described with reference to exemplary embodiments, it will be understood by those skilled in the art that various changes may be made and equivalents may be substituted for elements thereof without departing from the scope of the invention. In addition, many modifications may be made to adapt a particular situation or material to the teachings of the invention without departing from the essential scope thereof. Therefore, it is intended that the invention not be limited to the particular embodiment disclosed as the best mode contemplated for carrying out this invention, but that the invention will include all embodiments falling within the scope of the appended embodiments.