Abstract:
This invention relates to processes useful for fabricating electronic devices, more particularly to a process for laminating a layer of dielectric material onto a semiconductor.

Description:
FIELD OF THE INVENTION 
   This invention relates to processes useful for fabricating electronic devices, more particularly to a process for laminating a layer of dielectric material onto a semiconductor. 
   TECHNICAL BACKGROUND OF THE INVENTION 
   Thin film transistor (TFT) arrays for flat-panel displays are typically fabricated using amorphous-silicon-on-glass technology. Emerging display applications, such as electronic paper or remotely-updateable posters, will require TFT arrays on flexible substrates fabricated over very large areas, features which are difficult to achieve with amorphous silicon devices. In addition, these new applications will only gain wide acceptance if they can be produced at a significantly lower cost than current capital-intensive techniques allow. Consequently, there is significant interest in printable electronics as a low-cost fabrication technique compatible with large areas and flexible substrates. A common feature to most of these techniques is that the critical semiconductor-gate dielectric interface is formed by deposition of the semiconductor onto the dielectric. C. J. Drury et al., Appl. Phys. Lett., 73 (1998) 108–110 disclose the application of the dielectric via spin-coating to a poly(thienylenevinylene) semiconductor which had been cast from a precursor solution and then cured, rendering it insensitive to the solvent carrier for the dielectric layer. Podzorov et al., Appl. Phys. Lett. 82 (2003) 1739, disclose the deposition of parylene from the gas phase onto a single crystal of rubrene, a process which does not dramatically affect the semiconductor, but which also does not provide much latitude in the choice of dielectric material. In general, the use of solvent-based deposition of materials onto semiconducting layers has been avoided because the applied solvent can compromise the integrity of the semiconductor. 
   As an alternative approach, lamination offers a solvent-free method for transferring a wide range of polymer dielectrics onto a variety of semiconductors. Lamination is a dry process, can be applied over large areas, and is compatible with many of the proposed features of printable electronic technology, e.g. roll-to-roll processing. However, until now, a variety of technical challenges had prevented lamination from being a viable approach. 
   SUMMARY OF THE INVENTION 
   This invention provides a process for laminating a layer of dielectric material onto a semiconductor comprising:
     a. coating a first surface of a flexible substrate with a cushion layer comprising an elastomer to form a backing layer;   b. coating the cushion layer with a dielectric material to form a donor element comprising the substrate, the cushion layer and the dielectric material, wherein the dielectric material has a Tg below a lamination temperature;   c. placing the dielectric material of the donor element in contact with a semiconductor;   d. applying heat and pressure to a second surface of the substrate of the donor element to adhere the dielectric material to the semiconductor thereby transferring the dielectric material to the semiconductor; and   e. optionally removing the backing layer.   

   
     BRIEF DESCRIPTION OF THE FIGURES 
       FIG. 1  is a schematic of a DIGFET 
       FIG. 2   a  is a plot of the bottom-gate drain current characteristics of a DIGFET before lamination of the dielectric 
       FIG. 2   b  is a plot of the bottom-gate behavior of the same DIGFET after lamination of the dielectric 
       FIG. 2   c  is a plot of the top-gate behavior of the same DIGFET 
   

   DETAILED DESCRIPTION OF THE INVENTION 
   The process of this invention is useful in the production of thin film transistors (TFTs). The process provides a method for laminating dielectric materials onto semiconductors by first coating a cushion layer onto a flexible substrate to form a backing layer. The dielectric material is then coated onto the cushion layer to form the donor element. The dielectric material of the donor element is then placed in contact with the semiconductor layer, and sufficient heat and pressure are applied in a lamination step to cause the elastomer to soften or partially melt and the dielectric material to adhere to the semiconductor material. While the elastomer is still soft, the backing layer can be removed, if desired. 
   To illustrate the use of this process, the fabrication of TFTs in which a polymer dielectric is laminated to a cadmium sulfide semiconducting layer is described. Fused silica substrates, measuring 25 mm×50 mm×1 mm, were stamped with a fluorosilane monolayer such that most of the substrate became hydrophobic. Ten 1 mm 2  patches remained hydrophilic. It was onto these areas that the CdS was deposited via CBD (chemical bath deposition). Aluminum source/drain electrodes were evaporated onto the samples. The polymer dielectric was then laminated onto the sample. Finally, aluminum gate electrodes were evaporated, completing the TFT structure. 
   Suitable flexible substrates for the donor element include polymer films and sheets, as well as metal sheets and films. Suitable polymers include polyesters, polyamides, polyimides, polycarbonates and other materials that can be formed into sheets or films and are thermally and dimensionally stable at the lamination temperature. Dimensionally stabilized PET and polyimide films (e.g., Kapton®, DuPont) are preferred. 
   Suitable materials for the cushion layer include elastomers with softening temperatures between 40 C and the decomposition temperature of the flexible substrate or the dielectric material, whichever is lower. Elvax® is a preferred elastomer. 
   Suitable dielectrics for use in the process of this invention include polymers with Tg (glass transition temperature) less than the lamination temperature and a dielectric constant of 3–10. Suitable dielectric materials must also be flexible enough to transfer without cracking. Preferred polymers include PBMA (polybutylmethacrylate), PVP (polyvinylpyridine), PTFEVFP (poly (tetrafluoroethylene-co-vinylidene fluoride-co-propylene)) and PVFMVE (poly(vinylidene fluoride-co-perfluoromethylvinylether)). Fluorinated polymers such as PVFMVE are especially preferred due to their high dielectric constants. 
   In selected combinations of substrate and dielectric polymer, it may be possible to carry out the lamination step without use of a cushion layer. 
   The ability to laminate a gate-dielectric offers a new route to the fabrication of thin-film transistors. Since lamination is compatible with roll-to-roll processing and other high-throughput manufacturing methods, laminated dielectrics may enable the fabrication of large area, low cost electronics. 
   EXAMPLES 
   Microcontact Printing 
   A PDMS (polydimethylsiloxane) stamp was fabricated from a photolithographic master on a silicon wafer using SU-8 as a negative resist with a thickness of 26 microns. The resist was imaged through a film phototool. The master was cut to the desired size, and then bonded onto a glass plate using epoxy glue. Dow Corning Sylgard 184 (10:1 ratio of polymer to curing agent) was degassed for ˜30 min. in a vacuum oven at room temperature. A Teflon O-ring was placed around the master to confine the fluid to be crosslinked into the stamp. Sylgard 184 fluid was poured gently onto the master to fill the area within the O-ring. A glass plate treated with a soluble fluoropolymer was used to define the upper surface of the silicone. A uniform weight of ˜200 g. is kept on this glass plate as the fluid was cured into an elastomer. Cure took place at a temperature of 60° C. for at least 5 hours. The stamp was then carefully peeled apart from the master surface. 
   The cured stamp was spin coated (at 2000 rpm) with 10 mM (heptadecafluoro-1,1,2,2-tetrahydrodecyl) trichlorosilane in perfluoro(butyl-tetrahydrofuran) [Fluoroinert FC-75] solvent. The fluorosilane-coated stamp was dried with N 2  gas before printing the hydrophobic background pattern on the substrate. The stamp was held from one corner with a pair of forceps. It was carefully placed on the substrate starting from the bottom edge and slowly moved in the upward direction until whole of the stamp was in full contact with the substrate. A small sheet of Teflon (the size of the stamp) was placed on the stamp, followed by a round steel weight that was big enough to cover the stamp. This was done to provide uniform pressure on the stamp and assure that it was in full contact with the substrate. The weight was carefully removed, followed by the Teflon sheet. The stamp was removed from the substrate by using forceps, starting from the bottom edge and slowly detaching it in the upward direction so that the stamp did not slip during the detachment procedure. After microcontact printing, the substrate was placed in the CBD bath. 
   Chemical Bath Deposition 
   The CBD baths consisted of 30 mM triethanolamine, 6 mM cadmium acetate, and 6 mM thiourea, held at a temperature of 70° C., pH=9. A piece of gold foil was included in the bath. We found that the inclusion of gold foil in the bath reduced the conductivity of the deposited films. The samples, after removal, were washed with copious amounts of DI water, dried under a stream of nitrogen, and dried on a hotplate at 70° C. 
   Surface Treatments 
   Surface treatments of the CdS films prior to evaporation of the source/drain pairs were accomplished with the aid of a UVOCS cleaning unit or a plasma oven. When a fluorosilane surface modifier was used to pattern CdS deposition, a large portion of the surface exhibited low surface energy, interfering with lamination of the dielectric. To remove the fluorosilane, the surface was treated with either a UV-Ozone cleaning system (UVOCS) or oxygen plasma (300W). Both methods successfully cleaned the surface as determined by observing the wetting of a water drop. After cleaning, lamination occurred without a problem. 
   Source and Drain Electrodes 
   Aluminum source and drain electrodes were evaporated, at a base pressure of ˜5×10 −6  mbar, through a shadow mask onto the CdS film. Aluminum was chosen for the source and drain contacts because it can make ohmic contact to CdS. The mask defined twelve sets of source-drain pairs, each with a channel width W=500 □m wide, and three different channel lengths, L, four each of L=20, 50 and 100 □m. After evaporation, the samples were annealed in an oven with nitrogen purge at 250° C. for 2 hours. 
   Lamination 
   Elvax® (an ethylene/vinyl acetate copolymer) was extruded onto Cronar® (a dimensionally stabilized poly(ethylene terephthalate) (PET) sheet) to a thickness of 2 mils. This sheet was used as the substrate upon which polymer solutions were bar-coated with Meyer rods. The softening temperature of the Elvax® is ˜80° C. Solutions of the dielectric materials of 5–10 wt % were coated with rods varying from #5–#20, to produce polymer films with thicknesses ranging from 0.2–1.5 □m on the Elvax®/Cronar® substrates, which were approximately 1 ft 2  in area. Small strips (5×30 mm 2 ) of these sheets were cut out and placed over the source-drain gaps on the fused silica substrates. The sample was then sandwiched between Teflon® sheets, which were then sandwiched between silicone rubber sheets. The assembly was then placed into a Carver press preheated to 85° C. The press was then closed with a force of 1000–2000 lbs over the 36 in 2  platens, and the sample was held there for 2 minutes. Upon opening the press, the Elvax®/Cronar® substrate is peeled back while the sample is still warm. A clean separation between the polymer coating and the Elvax® occurs practically every time, resulting in complete transfer of the thin polymer film to the substrate. Multiple laminations of thin films can be performed in this fashion, with zero back transfer. 
   Gate Electrodes 
   Aluminum gate electrodes were then evaporated onto the polymer dielectric, completing the TFT structure. 
   Device Testing 
   Transfer curves (gate sweeps), composed of I ds  vs. V g  traces at a fixed V ds , were measured as well as the output curves, I ds  vs. V ds  as a function of V g . Linear and saturated transfer curves were obtained. Typical TFT behavior was observed. The relevant parameters were extracted from the data using standard TFT analysis. 
   Example 1 
   Poly(butylmethacrylate)−PBMA 
   Table 1 summarizes the results for a typical sample. The PBMA thickness d=1.8 □m, and we assumed a dielectric constant k=3.5 was applicable for these experiments. The linear gate sweeps were obtained with V ds =1 V, and the saturated gate sweeps were obtained with V ds =100 V. In both cases, V g  was swept from −100 to +100 V in 0.5 V increments. A Levinson analysis of the linear gate sweep was performed, and the grain boundary mobility □ gb  and the trap density N t  are included in Table 1. Overall, the agreement in □ for the different measurements was good, within the standard deviation. 
   
     
       
             
             
             
             
             
             
           
         
             
               TABLE 1 
             
             
                 
             
             
                 
                 
                 
               □ gb   
               N t   
                 
             
             
               PBMA (30-2), 
               □ × 10 −2 ) 
                 
               (×10 −2 ) 
               (×10 12 ) 
               On/off 
             
             
               N = 10 
               (cm 2/ Vs) 
               V t   
               (cm 2 /Vs) 
               (#/cm 2 ) 
               ratio 
             
             
                 
             
           
           
             
               Linear GS 
               1.6 ± 0.3 
               57 ± 6 
               2.7 ± 0.8 
               .91 ± .14 
               3.5 ± 10 4   
             
             
               Saturated GS 
               1.7 ± 0.5 
               46 ± 6 
                 
                 
               5.6 ± 10 6   
             
             
               Output curve, 
               1.7 ± 0.4 
               67 ± 2 
             
             
               linear region 
             
             
               Output curve, 
               1.6 ± 0.7 
               49 ± 3 
                 
                 
               2.8 ± 10 4   
             
             
               saturated 
             
             
               region 
             
             
                 
             
           
        
       
     
   
   Example 2 
   Poly(4-vinylpyridine)—PVP 
   PVP (MW=60,000; 10 wt % solution in methyl ethyl ketone; dielectric constant, k=3.8 at 200 Hz) was bar-coated onto Elvax®/Cronar® using a #10 rod, resulting in a film with d=1.6 □m thick. The CdS sample was treated in the UVOCS for 15 mins, and then annealed at 250° C. overnight. Aluminum source/drain electrodes were evaporated onto the CdS. Then a single layer of PVP was laminated onto the sample. Aluminum gate electrodes were then evaporated onto this structure. 
   The data from this sample is collected in Table 2. There is very good agreement between the mobility values extracted from the output and transfer curves. 
   
     
       
             
             
             
             
             
             
           
         
             
               TABLE 2 
             
             
                 
             
             
                 
                 
                 
               □ (×10 2 ) 
                 
                 
             
             
               PVP 
                 
                 
               Grain 
             
             
               (24-1), 
               □ × 10 2 ) 
                 
               boundary 
               N t  (×10 12 ) 
             
             
               N = 8 
               (cm 2 /Vs) 
               V t   
               (cm 2 /Vs) 
               (#/cm 2 ) 
               On/off ratio 
             
             
                 
             
           
           
             
               Linear GS 
               1.2 ± 0.2 
               46 ± 3 
               1.7 ± 0.3 
               .87 ± .11 
               2.7 × 10 4   
             
             
               Saturated 
               1.4 ± 0.2 
               45 ± 7 
                 
                 
               3.3 × 10 5   
             
             
               GS 
             
             
               Output 
               1.7 ± 0.4 
               64 ± 4 
             
             
               curve, 
             
             
               linear 
             
             
               region 
             
             
               Output 
               1.2 ± 0.2 
               45 ± 5 
                 
                 
               2.8 × 10 4   
             
             
               curve, 
             
             
               saturated 
             
             
               region 
             
             
                 
             
           
        
       
     
   
   Example 3 
   Poly(vinylidene fluoride-co-perfluoromethyl vinyl ether)—PVFMVE 
   Poly(vinylidene fluoride-co-perfluoromethylvinylether) (dielectric constant k=10 at 40 Hz) was coated to 0.5 mm thickness by drawing a 10 wt % solution of the polymer in methyl ethyl ketone onto an Elvax®/Cronar® receiver sheet with a #8 Meyer rod. The results from several experiments are presented in Table 3. 
   
     
       
             
             
             
             
             
             
             
           
             
             
             
             
             
             
             
           
         
             
               TABLE 3 
             
             
                 
             
             
                 
                 
               Dielectric 
                 
                 
               Sat. 
                 
             
             
                 
                 
               Thickness 
               □ lin   
               □ sat   
               On/off 
             
             
               Sample 
               Treatment 
               (□m) 
               (cm 2 /Vs) 
               (cm 2 /Vs) 
               (median) 
               Sat. V t   
             
             
                 
             
           
           
             
                 
             
           
        
         
             
               104932-015 
               UVOCS 
               1.5 
               0.74 
               0.98 
               4.8 × 10 3   
               12.4 
             
             
               104932-074-1 
               UVOCS 
               0.84 
               — 
               0.20 
               3.0 × 10 5   
               23.5 
             
             
               104932-074-2 
               O 2  plasma 
               1.0 
               0.64 
               8.9 
               1.1 × 10 6   
               14.9 
             
             
               104932-085-3 
               UVOCS 
               1.7 
               1.0  
               2.4 
               1.1 × 10 4   
               27.9 
             
             
               104932-085-4 
               Ar plasma 
               1.7 
               0.60 
               2.0 
               8.0 × 10 3   
               22.3 
             
             
               104932-096-2 
               O 2  plasma 
               1.6 
               0.54 
               1.0 
               5.2 × 10 1   
               −2.3 
             
             
               104932-096-3 
               Ar plasma 
               1.6 
               0.15 
               0.36 
               1.5 × 10 3   
               29.8 
             
             
               104932-096-5 
               UVOCS 
               1.6 
               0.13 
               0.40 
               7.3 × 10 3   
               20.7 
             
             
               104932-105-1 
               Ar plasma 
               1.7 
               0.12 
               0.33 
               4.5 × 10 3   
               27.7 
             
             
               104932-105-2 
               O 2  plasma 
               1.7 
               0.49 
               1.2 
               5.0 × 10 3   
               30.8 
             
             
               104932-105-3 
               UVOCS 
               1.7 
               0.17 
               0.38 
               3.0 × 10 2   
               21.1 
             
             
                 
             
           
        
       
     
   
   We examined the time dependent polarization of the dielectric by performing saturated gate sweeps as a function of delay time and number of data points. These results are collected in Table 4. For all data, V ds =50 V, and V g  was swept from −50 to +50. The initial hold time on the semiconductor parameter analyzer was kept constant at 5 s, and the integration time was set for medium. The dielectric thickness d=1.5 □m. As the delay time decreased, the mobility remained the same, the on/off ratio decreased, and the threshold voltage increased. 
   
     
       
             
             
             
             
             
           
             
             
             
             
             
           
         
             
               TABLE 4 
             
             
                 
             
             
               Delay Time 
               # 
               Peak mobility □ 
                 
                 
             
             
               (s) 
               pts 
               (cm 2 /Vs) 
               On/off 
               V t   
             
             
                 
             
           
           
             
                 
             
           
        
         
             
               0.2 
               400 
               1.2 
               1.1 × 10 7   
               7 
             
             
               0.1 
               400 
               1.4 
               5.5 × 10 7   
               10 
             
             
               0.01 
               400 
               1.4 
               7.3 × 10 6   
               17 
             
             
               0.001 
               400 
               1.5 
               7.0 × 10 6   
               19 
             
             
               0.0001 
               400 
               1.6 
               7.0 × 10 6   
               19 
             
             
               0.0001 
               200 
               2.0 
               3.2 × 10 6   
               26 
             
             
               0.0001 
               100 
               1.5 
               1.1 × 10 6   
               29 
             
             
                 
             
           
        
       
     
   
   Example 4 
   Poly(tetrafluoroethylene-co-vinylidene fluoride-co-propylene) 
   Poly(tetrafluoroethylene-co-vinylidene fluoride-co-propylene) (PTFEVFP) is soluble in common organic solvents and has a relatively large dielectric constant, k=6 at 100 Hz. The low glass transition temperature, T g =−20° C., made lamination very easy. Poling of the dielectric under the influence of the gate field resulted in artificially enhanced mobility values. These are evidenced in Table 5. 
   
     
       
             
             
             
             
             
             
             
           
             
             
             
             
             
             
             
           
         
             
               TABLE 5 
             
             
                 
             
             
                 
                 
               Dielectric 
                 
                 
               Sat. 
                 
             
             
                 
                 
               Thickness 
               □ lin   
               □ sat   
               On/off 
             
             
               Sample 
               Treatment 
               (□m) 
               (cm 2 /Vs) 
               (cm 2 /Vs) 
               (median) 
               Sat. V t   
             
             
                 
             
           
           
             
                 
             
           
        
         
             
               103172-154-1 
               UVOCS 
               1.4 
               2.3 
               3.0 
               2.8 × 10 4   
               12 
             
             
               103172-154-2 
               O 2  plasma 
               1.4 
               3.9 
               20 
               2.3 × 10 5   
               9.7 
             
             
               103172-154-7 
               O 2  plasma 
               1.4 
               11.3 
               90 
               5.8 × 10 3   
               5.1 
             
             
               103172-154-3 
               Ar plasma 
               1.4 
               9.3 
               32 
               5.4 × 10 2   
               8.5 
             
             
                 
             
           
        
       
     
   
   To demonstrate poling of the dielectric, we measured transfer curves on device 7 of 154–3 (L=50 □m, W=500 □m) by sweeping V g  from −20 V to +20 V with V ds =20 V, and varied the delay time. The hold time was held constant at 60 s, the integration time was short, and there were 400 points per scan. The results are summarized in Table 6. We see a pronounced decrease in the measured mobility and the on/off ratio, while V t  was little affected. 
   
     
       
             
             
             
             
             
           
             
             
             
             
             
           
         
             
                 
               TABLE 6 
             
             
                 
                 
             
             
                 
               Delay Time 
               Mobility □ 
                 
                 
             
             
                 
               (s) 
               (cm 2 /Vs) 
               On/off 
               V t   
             
             
                 
                 
             
           
           
             
                 
             
           
        
         
             
                 
               2 
               45 
               5.2 × 10 6   
               11 
             
             
                 
               1 
               18 
               1.6 × 10 6   
               10 
             
             
                 
               .5 
               7.1 
               6.5 × 10 7   
               10 
             
             
                 
               .2 
               2.5 
               2.4 × 10 6   
               10 
             
             
                 
               .1 
               1.2 
               5.2 × 10 5   
               11 
             
             
                 
               .05 
               .48 
               1.9 × 10 5   
               11 
             
             
                 
               .01 
               .063 
               1.3 × 10 4   
               9 
             
             
                 
               .001 
               .017 
               2.3 × 10 4   
               6 
             
             
                 
               .0001 
               .018 
               1.2 × 10 3   
               6 
             
             
                 
                 
             
           
        
       
     
   
   Example 5 
   Production of DIGFETs via a Lamination Process 
   The DIGFET (double insulated-gate field-effect transistor) devices were fabricated on n++ Si wafers with 100 nm thermal oxide on the top surface and a Ti/Au back contact. The wafers were cleaved into ˜2 cm wide strips, washed with methanol and DI water, blown dry with N 2  gas, and cleaned in an oxygen plasma (3 scfh,. 200 W) for 3 minutes. Cadmium sulfide was deposited onto the SiO 2  surface by placing the substrates in a Teflon PFA® breaker containing a basic (pH=9) solution of 2.5 millimolar cadmium acetate, 2.5 millimolar thiourea, and 25 millimolar triethanolamine. The beaker was placed on a hot plate/stirrer to maintain a constant temperature of 74° C. The solution was prepared using cadmium acetate hydrate (99.99+%), thiourea (99+%), and triethanolamine (98%) purchased from Aldrich and used without further purification in deionized water (□˜10 18  □-cm). The thickness of the CdS film was controlled by how long the substrates were kept in the bath, with a typical 15 minute deposition resulting in a 15±5 nm thick (as determined with a stylus profilometer) CdS film. 
   After deposition of the semiconductor, the samples were annealed at 250° C. for 12 hours. Then aluminum source and drain electrodes were deposited onto the CdS film by thermal evaporation through a shadow mask. The mask defined twelve sets of source-drain pairs, each with a channel width W=500 □m, and three different channel lengths L=20, 50, and 100 □m. 
   At this point, the bottom-gate transistors were complete, and their characteristics were checked prior to fabrication of the final DIGFET structure. An Agilent 4155C semiconductor parameter analyzer was used to measure the drain current I d  as a function of drain voltage V ds  and gate voltage V gs  at voltages from 0 V up to V ds =V gs =40 V. All measurements were carried out in the dark and in a nitrogen atmosphere. Values were extracted for the mobility and threshold voltage using the standard TFT analysis. The on/off ratio was defined as the ratio of the current at V gs =40 V to the current at V gs =0 V, at a constant V ds =40 V. The I d  curves for a typical device (#1) are illustrated in  FIG. 2   a , and the results from several devices are summarized in Table 7. The mobility in the saturation regime, μ sat , was typically 0.8±0.2 cm 2 /Vs, and the on/off ratio≧10 5 . 
   
     
       
             
           
             
             
             
             
             
           
             
             
             
             
             
           
         
             
               TABLE 7 
             
           
           
             
                 
             
             
               Summary of TFT characteristics for bottom 
             
             
               gate geometry before lamination of dielectric. 
             
           
        
         
             
                 
                 
               □ sat   
               On/Off 
                 
             
             
                 
               Transistor 
               (cm 2 /Vs) 
               ratio 
               V t,sat   
             
             
                 
                 
             
           
        
         
             
                 
               1 
               1.01 
               7.1E+05 
               12.5 
             
             
                 
               2 
               0.72 
               1.5E+05 
               15.5 
             
             
                 
               3 
               0.70 
               5.6E+05 
               16.3 
             
             
                 
               4 
               0.54 
               6.7E+04 
               16.9 
             
             
                 
               5 
               0.67 
               1.0E+05 
               17.8 
             
             
                 
               6 
               1.08 
               3.9E+05 
               14.9 
             
             
                 
               Median 
               0.71 
               2.7E+05 
               15.9 
             
             
                 
               Average 
               0.79 
               3.3E+05 
               15.7 
             
             
                 
               s.d. 
               0.21 
               2.7E+05 
               1.9 
             
             
                 
                 
             
           
        
       
     
   
   To complete the DIGFET structures, a film of poly(tetrafluoroethylene-co-vinylidenefluoride-co-propylene) was laminated by the process of this invention directly onto the CdS surface. This terpolymer was used as received from Aldrich. To produce the film, a 5 wt % solution in methylethylketone was bar-coated with a #12 Meyer rod onto Elvax® 550/Cronar® base sheet to produce a 450 nm thick film. The lamination was performed in a Carver press at 30 PSI with the sample between sheets of foam rubber to ensure even distribution of the applied force. The platens of the press were heated to 85° C. For the devices described here, two layers of the dielectric were laminated in succession, resulting in a total thickness d=0.9 □m. After lamination, isolated gold gate electrodes were evaporated onto the dielectric above each source-drain electrode pair. From ac impedance measurements on additional films of the terpolymer, it was determined that its dielectric constant k=6 at low frequencies (down to 40 Hz). This value was used to extract the mobility from the top-gate devices. 
   Once the dual-gate structures were completed, the transistor characteristics for the bottom-gate devices were checked again. A summary of these results is included in Table 8a. The mobility was largely unaffected by the addition of the polymer layer, but the threshold voltage was approximately halved to 8.8±1.5 V, and the on/off ratio was reduced by an order of magnitude. 
   
     
       
             
           
             
             
             
             
             
             
           
             
             
             
             
             
             
           
         
             
               TABLE 8a 
             
           
           
             
                 
             
             
               Summary of TFT characteristics after lamination 
             
             
               of dielectric and evaporation of second gate. 
             
           
        
         
             
                 
                 
                 
               ON/Off 
                 
                 
             
             
               Transistor 
               □ sat  (cm 2 /Vs) 
               □ lin  (cm 2 /Vs) 
               ratio 
               V t, sat   
               V t, lin   
             
             
                 
             
           
        
         
             
               1 
               1.14 
               1.92 
               1.2E+03 
               6.4 
               15.6 
             
             
               2 
               0.69 
               1.22 
               5.8E+03 
               9.3 
               17.5 
             
             
               3 
               0.67 
               1.44 
               1.6E+04 
               10.2 
               18.8 
             
             
               4 
               0.61 
               1.31 
               2.2E+04 
               10.0 
               19.0 
             
             
               5 
               0.63 
               1.66 
               4.6E+04 
               8.3 
               18.4 
             
             
               6 
               1.03 
               2.26 
               4.7E+04 
               7.5 
               17.6 
             
             
               Median 
               0.68 
               1.55 
               1.9E+04 
               8.8 
               18.0 
             
             
               Average 
               0.80 
               1.64 
               2.3E+04 
               8.6 
               17.8 
             
             
               s.d. 
               0.23 
               0.40 
               2.0E+04 
               1.5 
               1.3 
             
             
                 
             
           
        
       
     
   
   The procedures for electrical measurements and analysis on the top-gate devices were identical to those used for the bottom-gate ones.  FIG. 2   b  shows the bottom-gate drain current characteristics for device #1. For comparison, the top-gate behavior (post-lamination) of the same device is shown in  FIG. 2   c . Table 8b summarizes the top-gate and post-lamination bottom-gate results (for the same set of devices reported in Table 7). 
   
     
       
             
           
             
             
             
             
           
             
             
             
             
             
             
             
           
             
             
             
             
             
             
             
           
         
             
               TABLE 8b 
             
           
           
             
                 
             
             
               Summary of TFT characteristics after lamination of dielectric. The uncertainties 
             
             
               given in the averages represent the standard deviation for the data shown. 
             
           
        
         
             
                 
               □ sat  (cm 2 /Vs) 
               On/Off ratio 
               V T   
             
           
        
         
             
               Transistor 
               Top-gate 
               Bottom-gate 
               Top-gate 
               Bottom-gate 
               Top-gate 
               Bottom-gate 
             
             
                 
             
           
        
         
             
               1 
               0.12 
               1.14 
               1.3 × 10 2   
               1.2 × 10 3   
               0.5 
               6.4 
             
             
               2 
               0.044 
               0.69 
               2.3 × 10 3   
               5.8 × 10 3   
               7.6 
               9.3 
             
             
               3 
               0.017 
               0.67 
               5.2 × 10 2   
               1.6 × 10 4   
               6.1 
               10.2  
             
             
               4 
               0.012 
               0.61 
               3.8 × 10 2   
               2.2 × 10 4   
               0.2 
               10.0  
             
             
               5 
               0.032 
               0.63 
               9.8 × 10 2   
               4.6 × 10 4   
               11.4  
               8.3 
             
             
               6 
               0.071 
               1.03 
               2.0 × 10 3   
               4.7 × 10 4   
               9.4 
               7.5 
             
             
               Average 
               .05(4) 
               .8(2) 
               1.1(9) × 10 3     
               2(2) × 10 4   
                6(5) 
                9(2)