Abstract:
A capacitor having a storage electrode and a plate electrode, wherein both are made of metal or metal oxide, a high dielectric film formed between the electrodes, and a method of manufacturing the same. A diffusion prevention film is found at the side of the storage electrode and on the plate electrode. Therefore, the invention prevents deterioration of the property in the dielectric film due to penetration of hydrogen ions during a subsequent thermal process thereby improving the reliability of a device.

Description:
BACKGROUND OF THE INVENTION  
         [0001]    1. Field of the Invention  
           [0002]    The invention relates generally to a method of manufacturing a high dielectric capacitor. More particularly, the present invention relates to a high dielectric capacitor capable of preventing deterioration of dielectric property of a dielectric film generated during a subsequent thermal process.  
           [0003]    2. Description of the Prior Art  
           [0004]    Generally, as the degree of integration of a semiconductor device such as a DRAM is increased, the area a memory cell occupies in a semiconductor device or chip is rapidly reduced. For the operation of the memory device, however, capacitance of more than a certain amount per unit memory cell is necessarily secured. Therefore, there is a need for development of process technology by which the area occupied by a capacitor can be minimized while maintaining the capacitance necessary for the operation of the memory cell.  
           [0005]    In order to secure a capacitance necessary for the operation of a semiconductor device in a limited area, the effective surface area of a storage electrode must be increased or a dielectric material having an improved dielectric property must be used.  
           [0006]    Therefore, in compliance with these needs, a capacitor is manufactured using Ta 2 O 5 , BST (barium strontium titanate), or other suitable compounds in a manufacturing process of a device having a memory capacity more than four gigabytes (G). For reference, Ta 2 O 5  has more than five times the dielectric constant of a conventional dielectric made of an oxide film and a nitride film, and the dielectric constant of BST is higher than that of Ta 2 O 5 . The structure of the capacitor is formed as a MIS (metal insulator silicon) type made of, from top to bottom, a metal electrode, a dielectric, and a silicon electrode; or as a MIM (metal insulator metal) type made of, from top to bottom, a metal electrode, a dielectric, and a metal electrode.  
           [0007]    If the lower electrode of the capacitor is formed of a metal instead of polysilicon, as in a MIS type, reduction in the capacitance due to formation of a depletion layer can be prevented. On the other hand, if the lower electrode is formed using polysilicon, as in a MIM type, a depletion layer is necessarily formed during operation of the semiconductor. The depletion layer acts as a capacitor serially connected to the capacitor, which is a component of a DRAM, thus reducing the total capacitance. If the lower electrode is formed of a metal, however, reduction in the capacitance as above is not generated since the thickness of the depletion layer is negligible.  
           [0008]    Therefore, as the integration degree of a device is increased, a structure of a capacitor is such that only either an upper electrode or a lower electrode is formed of a metal or both the upper and lower electrodes are formed of metals.  
           [0009]    A method of manufacturing a conventional capacitor having a MIM structure in which the upper and lower electrodes are formed of metals will be explained by reference to FIGS. 1A to  1 D.  
           [0010]    [0010]FIG. 1A shows a cross-sectional view of a semiconductor device in which after a first insulating film  3  is formed on a semiconductor substrate 1 in which a junction  2  is formed, the first insulating film  3  is applied in a pattern which exposes the junction  2 , forming a contact hole. A plug  4  is formed within the contact hole  2   a  by stacking polysilicon Ti/TiN  4   b  on top of  4   a . The Ti/TiN  4   b  acts to reduce contact resistance with a metal electrode formed thereon and to prevent the polysilicon  4   a  and metal from diffusing.  
           [0011]    [0011]FIG. 1B shows a cross-sectional view of the semiconductor device in which, after an etching prevention layer  5  and an oxide film  6  are sequentially formed on the entire structure including the plug  4 , the oxide film  6  and the etching prevention layer  5  are sequentially patterned. The etching prevention layer  5  is formed by depositing a nitride film with thickness of several hundredths of an anstrum so that loss of the first insulating film  3  can be prevented upon etching the oxide film  6 .  
           [0012]    [0012]FIG. 1C shows a cross-sectional view of the semiconductor device in which, after a metal is deposited on the entire surface, the metal deposited on the oxide film  6  is removed for electrical separation between the memory cells, and a storage electrode  7  is formed at the patterned portion of the oxide film  6  and the etching prevention layer  5  so that it can contact the plug  4 . The metal deposited on the oxide film  6  is removed by an etch-back process or chemical mechanical polishing (CMP) process.  
           [0013]    [0013]FIG. 1D shows a cross-sectional view of the semiconductor device in which, after a dielectric film  8  and a plate electrode  9  are sequentially formed on the entire structure, a second insulating film  10  is formed on the plate electrode  9  so that the surface of the plate electrode  9  is essentially flat . The dielectric film  8  is formed of a high dielectric, e.g., Ta 2 O 5  or BST.  
           [0014]    In case of adopting a COB (capacitor over bit line) structure, after the manufacture of the capacitor as above is completed, a metal wiring is formed. Then, in order to optimize the property of the MOS transistor, a thermal process is performed under a gas atmosphere in which hydrogen (H 2 ) or hydrogen and nitrogen (N 2 ) are mixed. In other words, as a word line, a bit line, a capacitor and a metal wiring are formed after the transistor is formed, during this process, the memory cell is degraded. Dangling bonds are therefore easily formed at the interface, which degrades the dielectric property of the transistor. If the thermal process is performed under a hydrogen gas atmosphere, so that hydrogen atoms can be diffused into the transistor located at the base portion, the dangling bonds are removed yielding a transistor having a desired property.  
           [0015]    However, it has been reported that if the above thermal process is performed, the electrical property of the dielectric film is heavily degraded, generating a leakage current. The cause of this problem has yet to be clearly determined but it is thought that the cause are hydrogen atoms that penetrate into the dielectric film  8  during the thermal process, which causes a reduction reaction with the dielectric film since most dielectric films are made of oxide.  
           [0016]    Current solutions to this problem include a technology in which a capping layer made of Al 2   0   5  is formed on the plate electrode (Ru) of a capacitor having a Ru/Ta 2 O 5 /Ru structure in order to prevent penetration of hydrogen ions. However, although penetration of hydrogen ions from the upper plate electrode is blocked, penetration of hydrogen ions from the bottom storage electrode is not blocked. Further problems exist when SiH 4  and NH 3  are used as a source gas when a nitride film, used as the etching prevention layer  5 , is deposited. If hydrogen ions remaining after deposition are not completely removed, the remaining hydrogen ions may penetrate into the dielectric film  8 .  
         SUMMARY OF THE INVENTION  
         [0017]    A high dielectric capacitor in which a diffusion prevention film is fonned at the side of a storage electrode and on a plate electrode to prevent penetration of hydrogen (H) ions during a subsequent thermal process, and a method of manufacturing the same are described.  
           [0018]    In order to accomplish the above, a high dielectric capacitor has a storage electrode and a plate electrode, both made of metal or a metal oxide, and a high dielectric film formed between the electrodes. The dielectric film includes diffusion prevention films for preventing penetration of gas ions formed at the side of the storage electrode and on the plate electrode.  
           [0019]    The high dielectric capacitor can be manufactured by the steps of: forming an insulating film on a semiconductor device in which a junction is formed so that the junction is exposed to form a contact hole  2   a ; forming a plug within the contact hole  2   a ; sequentially forming a first diffusion prevention film and an oxide film on the entire structure; sequentially patterning the oxide film, the first diffusion prevention film, and the etching prevention layer using a mask; forming a storage electrode at the patterned portions of the oxide film, the first diffusion prevention film, and the etching prevention layer so that the storage electrode contacts the plug; and sequentially forming a dielectric film, a plate electrode, and a second diffusion prevention film on the entire structure.  
           [0020]    Preferred embodiments include first and second diffusion prevention films made of Al 2   0   3  with a thickness between about 5 Å and about 200 Å. Further preferred embodiments include the storage electrode and the plate electrode comprised of a metal or metal oxide selected from Ru, Pt, RuO 2 , Ir, TrO 2 , W, WN, and TiN, and the high dielectric selected from the group including Ta 2 O 5 , TaON, and BST. 
       
    
    
     BRIEF DESCRIPTION OF THE DRAWINGS  
       [0021]    The aforementioned aspects and other features will be explained in the following description, taken in conjunction with the accompanying drawings, wherein:  
         [0022]    [0022]FIGS. 1A to  1 D are cross-sectional views for explaining a method of manufacturing a conventional high dielectric capacitor; and  
         [0023]    [0023]FIGS. 2A to  2 E are cross-sectional views for explaining a method of manufacturing a high dielectric capacitor described herein.  
     
    
     DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS  
       [0024]    The invention will be described in detail by way of a preferred embodiment with reference to accompanying drawings.  
         [0025]    As shown in FIG. 2A, a first insulating film  13  is formed on a semiconductor device  11  in which a junction  12  is formed so that the junction  12  is exposed to form a contact hole  12   a . Then, a plug  14  is formed within the contact hole  12   a . The plug  14  is formed by stacking polysilicon  14   a  and Ti/TiN  14   b . The Ti/TiN  14   b  acts to reduce the contact resistance with a metal electrode to be formed thereon and to prevent the polysilicon  14   a  and a metal from diffusing each other. Ti/TiAlN or Ti/TiSiN may be used instead of Ti/TiN.  
         [0026]    Referring to FIG. 2B, an etching prevention layer  15 , a first diffusion prevention film  16 , and an oxide film  17  are sequentially formed on the entire structure, including the plug  14 . The oxide film  17 , the first diffusion prevention film  16 , and the etching prevention layer  15  are sequentially patterned using a mask for storage electrode. The etching prevention layer  15  is formed by depositing a nitride film to a thickness between about 500 Å and about 1000 Å so that loss of the first insulating film  13  is prevented when the oxide film  17  is etched. The first diffusion prevention film  16  is formed by depositing Al 2 O 3  to a thickness between about 50 Å and about 200 Å by utilizing an atomic layer deposition (ALD) method, and the oxide film  17  has a thickness between about 5000 Å and about 12000 Å so that it can exhibit a sufficient capacitance.  
         [0027]    Referring to FIG. 2C, a metal or metal oxide, preferably including at least one of Ru, Pt, RuO 2 , Ir, IrO 2 , W, WN, and TiN, is deposited to a thickness between about 200 Å and about 400 Å on the entire structure. The metal deposited on the oxide film  17  is removed in order to electrically separate the memory cells. Thus, a storage electrode  18  is formed at the portion in which the oxide film  17 , the first diffusion prevention film  16  and the etching prevention layer  15  are patterned so that the storage electrode can contact the plug  14 . The metal deposited on the oxide film  17  is removed by utilizing an etch-back process or a chemical mechanical polishing (CMP).  
         [0028]    [0028]FIG. 2D shows a cross-sectional view of the device in which a dielectric film  19  and a plate electrode  20  are sequentially formed on the entire structure. The process of forming the dielectric film  19  includes depositing a high dielectric, e.g., Ta 2 O 5 , TaON, or BST, to a thickness between about 100 Å and about 250 Å by utilizing a chemical vapor deposition (CVD) method having a good coverage property, and then performing a low-temperature thermal process at a temperature range between about 350° C. and about 450° C. by utilizing an oxygen (O 2 ) plasma or UV/O 3  method, or by performing a high-temperature thermal process in a reactive furnace or a rapid thermal processing equipment having a temperature range between about 550° C. and about 700° C. so that organic impurity contained in the source can be removed. The plate electrode  20  is formed of a metal or metal oxide, preferably including at least one of Ru, Pt, RuO 2 , Ir, IrO 2 , W, WN, and TiN.  
         [0029]    Additionally, it is preferred that Ta 2 O 5  and TaON are formed with a thickness between about 100 Å and about 150 Å and the BST is formed with a thickness between about 150 Å and about 250 Å.  
         [0030]    [0030]FIG. 2E shows a cross-sectional view of the device in which Al 2 O 3  is deposited at a thickness between about 50 Å and about 200 Å on the plate electrode  20  by utilizing the ALD method to form a second diffusion prevention film  21 . A second insulating film  22  is then formed on the second diffusion prevention film  21  so that the surface of the second diffusion prevention film is essentially flat.  
         [0031]    In the capacitor manufactured as above, penetration of hydrogen ions from the etching prevention layer  15  and the bottom can be prevented by the presence of the first diffusion prevention film  16 . Also, penetration of hydrogen ions from the outside can be prevented by the presence of the second prevention film  21 . In this way deterioration of the dielectric property of the dielectric film  19  due to penetration of hydrogen ions does not occur.  
         [0032]    As the property of the dielectric film is preserved, degradation of reliability of a device due to generation of a leakage current can be prevented. Also, the invention can maintain the property of a MOS transistor at an optimal state by eliminating the problems generated during a thermal process. Further, the invention makes it possible to effectively generate a desired capacitance depending on the use of a dielectric and a metal electrode, thus facilitating a higher integration of a device.  
         [0033]    The invention has been described with reference to a particular embodiment in connection with a particular application. Those having ordinary skill in the art and access to the teachings of the present invention will recognize additional modifications and applications within the scope thereof.  
         [0034]    It is therefore intended by the appended claims to cover any and all such applications, modifications, and embodiments within the scope of the present invention.