Abstract:
A method for integrating wide-gap semiconductors, and specifically, gallium nitride epilayers, with synthetic diamond substrates is disclosed. Diamond substrates are created by depositing synthetic diamond onto a nucleating layer deposited or formed on a layered structure that comprises at least one layer of gallium nitride. Methods for manufacturing GaN-on-diamond wafers with low bow and high crystalline quality are disclosed along with preferred choices for manufacturing GaN-on-diamond wafers and chips tailored to specific applications.

Description:
RELATED APPLICATIONS 
     This application claims priority to U.S. Provisional Patent Application Ser. No. 61/604,979 filed Feb. 29, 2012. The disclosure is incorporated herein by reference. 
    
    
     FIELD OF THE INVENTION 
     The present invention relates to high-power electronic and optoelectronic devices and their thermal management, and particularly relates to methods for fabricating devices and structures that include integration of synthetic diamond films and wafers with wide-gap semiconductors, and more particularly with gallium nitride-based electronic and optoelectronic devices; including high-electron mobility transistors, radio-frequency (RF) electronic devices, light-emitting-diodes, and lasers. 
     BACKGROUND OF THE INVENTION 
     Thermal management in semiconductor devices and circuits is a critical design element in any manufacturable and cost-effective electronic and optoelectronic product, such as light generation and electrical signal amplification. The goal of efficient thermal design is to lower the operating temperature of such electronic or optoelectronic device while maximizing performance (power and speed) and reliability. Examples of such devices are microwave transistors, light-emitting diodes and lasers. Depending on the frequency of operation, power requirements, and specific application, these devices have been conventionally made on silicon, gallium arsenide (GaAs), or indium phosphide (InP). In recent years, gallium nitride (GaN), aluminum nitride (AlN) and other wide-gap semiconductors have surfaced as new choices for both power electronics and visible-light generating optoelectronics. Gallium nitride material systems give rise to microwave transistors with high-electron mobility (necessary for high-speed operation), high breakdown voltage (necessary for high power), and thermal conductivity that is greater than GaAs, InP, or silicon, and thus suitable for use in high power applications. GaN is also used in manufacturing of blue and ultraviolet lasers and light-emitting diodes. In spite of the high-temperature performance (owing to its wide bandgap and high critical field), GaN electronic and optoelectronic devices are limited in performance due to relatively low thermal resistance of the substrates commonly used for growth of GaN. This deficiency is most pronounced in high-power microwave and millimeter-wave transistors and amplifiers where reduced cooling requirements and longer device life, both benefiting from lower junction temperature, are in critical demand. Similar need is exhibited in high power blue and ultraviolet lasers where several-micrometer-wide laser cavity stripe dissipates power into the chip though low thermal conductance materials. 
     It is well known that diamond is the most thermally conductive substance known to man. For this reason, the semiconductor industry has been employing diamond heat-sinks and heat spreaders for improved thermal management since the commercialization of synthetic diamond by chemical-vapor deposition in the 1980&#39;s. The objective of optimal heat management is to bring the diamond heat-spreader or diamond layers to close proximity with the heat source in the electronic or optoelectronic devices. This means building devices on thin chips and mounted on diamond heat-spreaders, coating devices with diamond layers, and in more recent times transferring device epilayers onto diamond. 
     Diamond wafers are manufactured by chemical vapor deposition (CVD) by one of three methods: plasma enhanced diamond CVD where the energy to dissociate the reactants comes from a microwave source, hot-filament enhanced diamond CVD where the energy for dissociating gases comes from a hot tungsten filament, and high voltage torch where ions are accelerated using a high DC voltage. 
     The CVD process is carried out in a vacuum chamber within which a substrate on top of which diamond will be grown is provided and which is exposed to the energy source needed to dissociate the molecules of precursor gases needed to form diamond on the surface of the substrate. The precursor gases needed in the chemical vapor deposition of diamond are a source of carbon, typically methane (CH4), ethane (C2H6), carbon monoxide (CO), and acetylene (C2H2), diluted in hydrogen (H2). The gas combination needed for efficient diamond deposition contains a small (several percent) composition of the carbon-carrying gas in hydrogen, and the reaction can be further assisted with very small percentage of oxygen (O2). The preferred carbon-carrying gas in these reactions is methane. 
     GaN-on-diamond technology and resulting devices (described in U.S. Pat. No. 7,595,507) involve structures which feature atomically attached GaN epilayers to diamond substrates. This technology enables bringing together the best heat conductor (diamond) with electronic and optoelectronic devices based on gallium-nitride (GaN) and GaN-related compounds. Due to its inherent high critical electrical field and wide bandgap, gallium nitride devices are preferred for high power electrical and optoelectronic applications, such as, high power RF transistors and amplifiers, power management devices (Schottky diodes and switching transistors), as well as high power blue and ultraviolet lasers or light-emitting diodes. 
     GaN is presently grown on several different substrates: sapphire, silicon, silicon carbide, aluminum nitride, single-crystal diamond, and GaN substrates. With the exception of GaN substrates, all other materials have lattice constants that differ from that of GaN and AlGaN. In order to epitaxially grow high-quality AlGaN alloys on top of substrates with lattice constant different from GaN or the AlGaN alloys, it has been common practice in the industry to grow a layer or a combination of layers on top of the lattice-mismatched substrate in order to terminate the dislocations and produce a lower dislocation density epilayer on top of which growth of a high-quality active layer is possible. The layers grown directly on top of the lattice-mismatched substrate are commonly referred to as transition or nucleation layer or layers, and they can include any number of binary or ternary epitaxial layers. The nucleation layers are then followed by a suitably thick gallium-nitride layer, referred to as the buffer layer, which is added for achieving low dislocation density GaN and distancing the active layers from the highly dislocated nucleation layers. The top surface of the buffer layer generally features high quality material with dislocation density that is sufficiently low to allow the growth of device active layers. Typical dislocation densities achievable for GaN surface grown on silicon, silicon carbide, and sapphire epi-wafers for use in field-effect applications can be between 10 8  l/cm 2  and 10 10  l/cm 2 . Defect density required for efficient operation of bipolar devices, such as, bipolar transistors and optoelectronic devices ranges from 10 6  l/cm 2  to 10 8  l/cm 2 . The GaN buffer layer is often required as a part of the active epilayer structure. For the purposes of this application, the term “transition layers” means all of the layers grown on top of the native substrate and these are needed to (a) convert the lattice constant of the native substrate to that of GaN, and (b) achieve high quality material, i.e. dislocation density low enough to allow the growth of the desired active layer on top. 
     The term device “active layers” refers to epilayer structure and structures required for realization of electronic devices such as a high-frequency transistor, high-voltage switch, Schottky diode, and/or optoelectronic devices such as laser diodes, light-emitting diodes, and super-luminescent diodes. As the GaN buffer layer may serve a function within the active layer and the transition layers, the boundary between the transition layers and the active layers may fall somewhere within the buffer layer. Its precise location may not be physical but functional: the boundary separates what is required for proper device functioning (active layers) from what is not required for device operation (transition layers). 
     The epilayer structure of a typical AlGaN/GaN HEMT shown in  FIG. 1  (Prior Art) includes multiplicity of epilayers  9  disposed on top of a native substrate  1 . The epilayers  9  are divided into two functional parts: the transition layers  8  and active layers  7 . The transition layers  8  comprise of at least one layer, but typically a multiplicity of binary and ternary compound semiconductor epitaxial layers  2  that are grown directly on top of the native substrate  1 , often referred to as nucleation layers, that are then followed by a buffer layer  3 . The quality of the epilayers grown on the native substrate  1  improves as the growth progresses and at some thickness indicated with dashed line  17 , the crystal quality (defect density) of the buffer  3  becomes sufficient for high-crystal quality growth of the active layer  7 . The active layer  7  comprises multiple epitaxial layers whose number, thickness, and material choices are designed and optimized to perform specific functions of the electronic or optical device. The growth of the active layer  7  will start at and/or include growing a part of the buffer  3 . The reason the active layer functionally includes a part of the buffer layer is because the 2DEG at a heterojunction extends into both the large and lower bandgap materials, and hence it is present in the GaN (as the lower bandgap material, namely, at top of the buffer). Furthermore, the active layer may include may include other features, such as, as the back barrier which would make it extend into the buffer. 
     It is essential to note that apart from providing a template for growth of the active layer, the transition layers generally do not serve a function in the device operation. From the point of thermal management, the presence of the nucleation layer  2  (part of the transition layer) is detrimental to device thermal performance. Namely, due to multiple layer-boundaries within the transition layer, alloy scattering, and dislocations, the transition layer generally presents a significant barrier to heat flow perpendicular to the layers and thereby limits the device thermal conductance. 
     The active layers  7  will typically comprise a barrier layer  6  on top of a layer structure  4  that may include a below-channel barrier (not shown) to reduce drain-induced barrier lowering as is well known in the art. The barrier layer  6  may furthermore include a several nanometer thick layer of GaN on top of the barrier layer  6  and/or an MN interlayer below the barrier layer  6  to improve the electron mobility in the two-dimensional electron gas 2DEG  5  as is also known in the art. The active layers  7  may comprise multiple layers of AlGaN or InGaN semiconductor alloys or GaN, AlN, InN or any other related material to realize the desired electrical performance of the HEMT. The buffer is needed to electrically separate the transition layers from the electron gas  5  and its thickness may be increased to improve the device breakdown voltage. The exemplary HEMT shown in  FIG. 1  will also feature contacts to the transistor denoted with  10  (source),  11  (gate), and  13  (drain). The source  10  and the drain  13  contacts will typically make ohmic contacts to the active layers  7 , while the gate  11  may make a Schottky contact to the active layer  7 . Additionally, individual HEMTs may be isolated from adjacent devices on the same wafer or chip using isolation trenches  12  or implantation (not shown) to form monolithically integrated circuits on the same chip. The operation of this transistor and device enhancements described above have been described in publicly available literature, such as, books by Rüdiger Quay titled “Gallium Nitride Electronics”, and Umesh K. Mishra and J. Singh titled “Semiconductor Device Physics and Design”, both books published by Springer in 2008. 
     GaN-based HEMTs are used for numerous high power applications owing to the high density of electrons in the 2DEG in GaN and the high-breakdown field which lead to high operating currents and voltages, higher than GaAs devices of similar geometry. The dominant heat generation in high-electron mobility transistors occurs in an area between the gate and the drain  15 , close to the device surface. In this area, the energy of electrons accelerated with the high drain potential are first converted into optical phonons by electron-phonon scattering and then by phonon-phonon scattering into acoustic phonons which carry heat (heat conduction). Conventionally, the HEMT shown in  FIG. 1  is mounted with the back of the substrate  1  down onto a heat sink: The back metallization  16  is attached to a heat sink (not shown in  FIG. 1 ). The heat generated in the active layers of the transistor has to diffuse to the backside of the wafer and be carried away through the backside  16  by the heatsink and dissipated in the ambient. The temperature rise of the active layer relative to the ambient temperature for a given power dissipated by the device is referred to as the thermal resistance and is an essential design parameter for all electronic devices as the active layer temperature determines the device performance and its reliability. It is the objective high-power electronic and opto-electronic design is to minimize the thermal resistance of any device and thereby improve their reliability and performance over temperature. 
     Thermal resistance of commercial HEMTs with exemplary structure shown in  FIG. 1  is dominated by the relatively low thermal conductivity of the layers in the immediate proximity of the active layer, namely, the thermal conductivity of the active layers  7  and the transition layers  8 . More specifically, the nucleation layers  2  which are a part of transition layers  8  may comprise ternary compound semiconductor alloys which exhibit low thermal conductivity. Finally, materials used commercially for the substrate  1  have low thermal resistance further contributing to the overall low thermal resistance of the devices (eg. sapphire, silicon). The result of these materials and structure limitations is that conventional AlGaN/GaN field-effect transistors are limited thermally, but could be made better if its the thermal resistance could be somehow reduced. In summary, the transition layers and the substrate thermal properties are liming the performance of the devices. 
     There is a need in the industry to improve the thermal performance of AlGaN/GaN HEMTs and similar high-power electronic and optoelectronic devices. This need has spurred a number of investigations in integrating wide-bandgap device active materials with highly thermally conductive substrates by wafer bonding and/or direct growth of wide-gap materials. 
     Related art references include U.S. Pat. No. 5,650,639 by Schrantz, et al., disclosing bonding of epitaxial layers with diamond substrates for the purpose for improving thermal performance; U.S. Pat. No. 7,033,912 Saxler teaching growing diamond on thinned silicon carbide substrates and optionally growing active layers on this structure; U.S. Pat. No. 6,794,276 Letertre, et al. teaching creation of new substrates for semiconductor devices; and U.S. Pat. No. 7,358,152 by Kub and Hobart disclosing a number of methods to improve the heat conductance of electronic devices, specifically, GaN HEMTs, using wafer bonding of either completed devices or blank GaN epiwafers to highly thermally conductive substrates, synthetic diamond included. 
     SUMMARY OF THE INVENTION 
     This application discloses a method for integrating GaN and CVD diamond to form GaN-on-diamond engineered wafers or substrates on which electronic or optoelectronic devices can be manufactured using standard semiconductor processing technology. The disclosed process for manufacturing engineered GaN-on-diamond wafers is described as applied to high-electron mobility transistors. However, the inventions disclosed herein may be implemented using other electronics and optoelectronic devices, such as, bipolar transistors, Schottky diodes, microwave diodes, semiconductor lasers, light-emitting diodes, and super-luminescent diodes without departing from the spirit of the invention. 
     This invention relates to manufacturing of wide-gap compound-semiconductor-on-diamond composite substrates in which a diamond layer is grown upon a dielectric layer disposed on top of wide-gap compound-semiconductor layers. More specifically, this invention discloses methods and apparatuses for manufacturing of gallium-nitride-on-diamond engineered wafers. This invention furthermore relates to thermal management of high power microwave transistors, high-voltage field-effect transistors and Schottky diodes. 
     The objective is to improve GaN-based electronic devices to reach lower thermal resistance. This application discloses a number of preferred methods for manufacture of wafers and devices and discloses a number of preferred wafer and device structures that include epilayer structures and device configurations that result in the above-mentioned improvements. Any one of presented methods and embodiments may be used by themselves and in combination with other disclosed embodiments to achieve an improvement in performance. 
     Terminology 
     Wide-gap semiconductor technology refers to electronic and optoelectronic device and manufacturing technology based on wide-gap semiconductors. 
     Wide-gap semiconductor means (a) semiconductors comprising a bond between nitrogen (N) and at least one Group III element from the Periodic Table of the Elements (boron, aluminum, gallium, indium, and thallium), and (b) semiconductors comprising a bond between carbon (C) and at least one Group IV element from the Periodic Table of the Elements (carbon, silicon, germanium, tin, and lead). In this application, wide-gap means but is not limited to gallium nitride (GaN), aluminum nitride (AlN), indium nitride (InN), aluminum gallium nitride (AlGaN), indium gallium nitride (InGaN), aluminum indium nitride (AlInN), silicon carbide (SiC), and diamond (C). The mentioned materials (a) or (b) are single-crystal. 
     Single-crystal material, wafer or layer means being of one crystal, namely, having a translational symmetry. This term is common for crystal growth, and is a requirement for most semiconductors used in electronics. Real semiconductors have defects, but the defect densities are sufficiently low that assuming translational symmetry is sufficient to explain dominant electronic and optical properties of these materials. 
     Polycrystalline material means consisting of crystals variously oriented or composed of more than one crystal. 
     Amorphous material means a material having no real or apparent crystalline form. 
     Synthetic material means man-made material produced artificially, i.e. not natural, while synthetic diamond means man-made diamond. 
     Synthetic diamond is man-made diamond produced by any one of methods known in the art including, but not limited to high-temperature high-pressure technique and chemical vapor deposition (CVD). 
     CVD diamond includes, but is not limited to hot-filament, microwave plasma, and high-voltage arc chemical vapor deposition processes. 
     Bonding or wafer bonding is a technology in which two surfaces, commonly semiconductor surfaces, are brought into proximity and are caused to adhere firmly. The bonding can be achieved by a chemical bonding or using an adhesive. This process is commonly used in the semiconductor technology. See for example the book by Tong and Gosele: Semiconductor Wafer Bonding, Springer Verlag, 1989. 
     Wafer bow is the difference between the maximum and minimum height of any point on a wafer when it is laid on a flat surface as shown in  FIG. 2  and the height is measured in a direction perpendicular to the flat surface. The surface facing up is the surface being measured. 
     Native substrate is the substrate on top of which working epilayers are grown. For example, when GaN is grown on sapphire, sapphire is the native substrate. When GaN is grown on GaN substrate, the native substrate is GaN. 
     In situ means in natural position or place. In the semiconductor industry it generally means performing a special task during an otherwise essential process where the task is not essential to the process nor is it usually done at the same time. A typical use of this term is to describe, for example, optical monitoring or epitaxial or thin film growth during the growth/deposition. In that case one speaks of in-situ optical monitoring. In another example (and also used in the context of this application), passivation layers are usually added to the surface of field-effect transistors after the epitaxial layers have been grown and the wafers have been taken out of the growth chamber. Recently, there has been development in which silicon nitride passivation layer has been deposited on top of the epilayers while in the same growth chamber. In this case one speaks of in-situ silicon nitride passivation. Examples of in-situ silicon nitride passivation are reported in the following publications: “In situ SiN passivation of AlGaN/GaN HEMTs by molecular beam epitaxy”, Electronics Letters, Vol. 48, No. 14, pages 779-780, and “Surface Stabilization for Higher Performance AlGaN/GaN HEMT with in-situ MOVPE SiN”, MRS Proceedings, Vol. 831, E6.7, 2004. 
     Non-polar or semi-polar gallium nitride. The c-plane of hexagonal gallium nitride is the most common plane on which gallium nitride is grown. This surface is polar and the resulting heterojunctions contain fixed charge distributions at every interface between different gallium-nitride-related alloys. Gallium nitride can also be grown on a number of other crystallographic planes which result in reduced or no interface charges. These planes are referred to as semi-polar or non-polar planes. 
     Transition layers are epitaxial layers grown on top of a native substrate  1  of semiconductor S 1  with lattice constant x 1  and lattice structure L 1  in order to enable growth of a quality semiconductor S 2  with lattice constant x 2  and lattice structure L 2  on top of the native substrate  1 , wherein x 1  and x 2  differ sufficiently to prevent low dislocation-density growth of S 2  directly on S 1 , as is well known in the art. The lattice structure L 1  and L 2  may or may not be different. For example, L 1  may be a face-centered cubic, while L 2  may be hexagonal, or both L 1  and L 2  may be cubic. The requirement on how low the dislocation density has to be is determined by the type of the electronic or optoelectronic device to be fabricated and its performance. The exact structure of the transition layers differs from manufacturer to manufacturer, and for the purposes of this application, transition layers refer to any and all layers required to reach the desired defect/dislocation density so that on top of the transition layers an active layer structure can be grown. For the purposes of this application, the transition layers include nucleation layers (multiplicity of ternary and/or binary layers) and a part of a binary buffer layer. 
     Wafer or Wafers, a typically round plate of made out of semiconductor on top of which electronic or optoelectronic devices are or will be fabricated. 
     Engineered wafer is a wafer that includes a multiplicity of layers which are manufactured prior to joining them to make the wafer. 
     Means for vacuum chamber evacuation include mechanical pumps, turbo-molecular pumps, and any other pumps used in conjunction with drawing vacuum in vacuum chambers as is known in the art. 
     Means for maintaining chuck temperature include capacitive cooling of the wafer that may include liquid cooling and controlling the chuck temperature by adjusting liquid temperature and liquid flow as is well known in the art. 
     Means for monitoring chuck temperature include pyrometer, thermocouple, or open loop control. Open loop control means operating the chuck at powers that are known from calibration study to result in certain chuck temperature. 
     Refractory metals are a class of metals that are extraordinarily resistant to heat and wear. The most common definition of refractory metals includes niobium, molybdenum, tantalum, tungsten, and rhenium. They all have melting points above 2000° C. 
    
    
     
       BRIEF DESCRIPTION OF THE DRAWINGS 
         FIG. 1  shows prior art high-electron mobility transistor epilayer structure. 
         FIG. 2  illustrates the definition of bow measurement. 
         FIG. 3  is a block diagram illustrating a preferred method for manufacturing GaN-on-diamond engineered wafers. 
         FIG. 4  shows (a) an illustration of the parts of wafer  700  and (b) carrier wafer  720 . 
         FIG. 5  shows (a) an illustration of the parts of wafer  730  and (b) carrier wafer  740 . 
         FIG. 6  is an illustration of an exemplary bonding jig used in the process for manufacturing GaN-on-diamond wafers. 
         FIG. 7  is an illustration of the elements of wafer sandwich  750  ready for diamond deposition. 
         FIG. 8  is an illustration of the elements of diamond growth chamber used in the preferred process for manufacturing GaN-on-diamond engineered wafers. 
         FIG. 9  depicts laser trimming of wafer  760 . 
         FIG. 10  illustrates one embodiment of a completed GaN-on-diamond engineered wafer manufactured using the preferred process. 
         FIG. 11  shows an alternative embodiment of a completed GaN-on-diamond engineered wafer manufactured using the preferred process. 
         FIG. 12  illustrates the parts of wafer  710 , gallium nitride epilayers with in-situ silicon nitride. 
     
    
    
     DETAILED DESCRIPTION OF THE INVENTION 
     Preferred methods  100  and  200  are explained with the help of a block diagram in  FIG. 3  and other figures that are used to clarify the structure of wafers used or produced by the preferred processes. In Method  100 , the wafers provided are “GaN on NATIVE SUBSTRATE”  700  having structure illustratively shown in  FIG. 4A  and “CARRIER WAFER”  720  having structure illustratively shown in  FIG. 4B . In Method  200 , the wafers provided are “GaN on NATIVE SUBSTRATE with in-situ silicon nitride”  710  having structure illustratively shown in  FIG. 12  and “CARRIER WAFER”  720  having structure illustratively shown in  FIG. 4B . The methods merge before step  102  and continue with the same steps for either method. Either method can be used to produce an engineered GaN-on-diamond wafer with silicon nitride coating  780  (“WORKING WAFER w/NITRIDE”). Either method can be used to produce an engineered GaN-on-diamond wafer without silicon nitride coating  770  (“WORKING WAFER w/o NITRIDE”) as illustrated in the flow chart in  FIG. 3 . In other words, in either method  100  or  200 , the removal of silicon nitride in step  120  is optional. The choice between the method is determined by the availability of the type of GaN on native substrates: either in-situ silicon nitride or without. The choice is that of the manufacturer of engineered wafers and/or the manufacturer of the devices using the product of the methods. 
     The order of the process steps is given by the order in which the specification is written and the block diagram shown in  FIG. 3 . 
     Method  100   
     STEP  101  “PROVIDE GAN ON NATIVE SUBSTRATE”: In method  100 , an epi-wafer  700  is provided in step  101 , wherein epi-wafer  700  comprises a native substrate and GaN epilayers disposed on top of the native substrate. Structure of wafer  700  is illustrated in  FIG. 4A . The wafer  700  comprises epilayers  704  grown on a native substrate  701 . The epilayers  704  comprise transition layers  708  disposed on top of a native substrate  701  and active layers  707  disposed on top of the transition layers  708 . The active layers  707  comprise a barrier layer  706 , a two-dimensional electron gas  705 , and may optionally include a back barrier (not shown in  FIG. 4A ) and an optional AlN interfacial layer (not shown in  FIG. 4A ) as is known in the art to improve the performance of RF high-electron mobility transistors. The materials included in the active layer include but are not limited to any binary, ternary, quaternary alloy involving Ga, Al, In, B, and N atoms. In one embodiment, the active layer comprises at least one layer with polar gallium nitride and gallium-terminated surface of the active layer is proximal to surface  700 A. In one embodiment, the active layer comprises polar gallium nitride with gallium-terminated surface of the active layer proximal to surface  700 A. The transition layers  708  comprise of nucleation layers  702  adjacent to the native substrate  701  and at least a part of buffer layer  703  disposed on top of the nucleation layers  702 . The buffer layer  703  is preferably made out of GaN. A functional boundary  709  between the active layers  707  and the transition layers  708  appears within or at the edge of the buffer  703 . In one embodiment, the wafer structure  700  represents an AlGaN/GaN HEMT as is known in the art and the active layers are grown on the Ga-face GaN. In one embodiment of present invention, the native substrate  701  is made out of silicon. It is clear that native substrate  701  may also be made out of silicon carbide, sapphire, and aluminum nitride without departing from the spirit of the invention. In one embodiment of the present invention, wafers with preferred design  700 , but not limited to design  700 , are provided as starting material to process  100 . 
     The top surface of epi-wafer  700  is referred to as surface  700 A, while the bottom surface of the epi-wafer  700  is referred to as surface  700 B. 
     STEP  101 B “PROTECT”: The top surface  700 A of wafer  700  is coated with a layer  804  comprising silicon nitride, deposited on top of surface  700 A. The silicon nitride layer is preferably deposited using thermal chemical-vapor deposition. The thickness of silicon nitride layer is preferably 50 nm, but thicker or thinner films can be used without departing from the spirit of the invention. For example, the thicknesses of the silicon nitride that have been experimentally confirmed to work range between 20 nm and 200 nm. The top surface of the coated wafer  700  is now referred to as surface  804 A. 
     STEP  101 C “POLYSILICON”: The top surface  700 A of wafer  700  is coated with a layer of polysilicon  805  deposited on top of silicon nitride surface  804 A. The thickness of the polysilicon layer  805  is preferably 1000 nm, but thicknesses between 100 nm and 2000 nm are possible. The polysilicon layer  805  is deposited using thermal chemical-vapor deposition at 600° C. In one embodiment, POLYSILICON step follows the PROTECT step in-situ, without removing the wafer from the process chamber. The top surface of the coated wafer  700  is now referred to as surface  805 A. 
     Method  200   
     STEP  101  “PROVIDE GAN ON NATIVE SUBSTRATE w/in-situ SiN”: In method  200 , an epi-wafer  710  is provided in step  122 , wherein epi-wafer  710  comprises a native substrate, GaN epilayers disposed on top of the native substrate, and an in-situ deposited silicon nitride layer on top of the GaN epilayers. An exemplary structure of wafer  710  is illustrated in  FIG. 12 . The numbering on the layers comprising wafer  710  that have the same function as the corresponding layers in the structure  700  are kept identical to those in wafer  700 . It is clear to a person skilled in the art that the specific epilayer design used for wafer  700  (layer thicknesses, composition, and number of layers) may differ from wafer  710  without departing from the spirit of the invention. The wafer  710  comprises of epilayers  704  grown on a native substrate  701  and a silicon nitride layer  711  grown in-situ on top of the epilayers  704 . The epilayers  704  comprise transition layers  708  disposed on top of a native substrate  701  and active layers  707  disposed on top of the transition layers  708 . The active layers  707  comprise a barrier layer  706 , a two-dimensional electron gas  705 , and may optionally include a back barrier (not shown in  FIG. 12 ) and an optional AlN interfacial layer (not shown in  FIG. 12 ) as is known in the art to improve the performance of RF high-electron mobility transistors. The materials included in the active layer include but are not limited to any binary, ternary, quaternary alloy involving Ga, Al, In, B, and N atoms. In one embodiment, the active layer comprises at least one layer with polar gallium nitride and gallium-terminated surface of the active layer is proximal to surface  804 A. In another embodiment, the crystal orientation of said active layers  707  may be one of polar, semi-polar, or non-polar. The transition layers  708  comprise of nucleation layers  702  adjacent to the native substrate  701  and at least a part of buffer layer  703  disposed on top of the nucleation layers  702 . The buffer layer  703  is preferably made out of GaN. A functional boundary  709  between the active layers  707  and the transition layers  708  appears within or at an edge of the buffer  703 . In one embodiment, the wafer structure  710  represents an AlGaN/GaN HEMT as is known in the art and the active layers are grown on the Ga-face GaN. In one embodiment of present invention, the native substrate  701  is made out of silicon. It is clear that native substrate  701  may also be made out of silicon carbide, sapphire, and aluminum nitride without departing from the spirit of the invention. In one embodiment of the present invention, wafers with preferred design  710 , but not limited to design  710 , are provided as starting material to Method  200 . The top surface of wafer  710  is referred to as surface  804 A, while the bottom surface of the epi-wafer  710  is referred to as surface  710 B 
     STEP  106  “POLYSILICON”: The top surface  700 A of wafer  700  is coated with a layer of polysilicon  805  deposited on top of silicon nitride surface  804 A. The thickness of the polysilicon layer  805  is preferably 1000 nm, but thicknesses between 100 nm and 2000 nm are possible. The polysilicon layer  805  is deposited using thermal chemical-vapor deposition at 600° C. The top surface of the coated wafer  700  is now referred to as surface  805 A. 
     Steps Common to Methods  100  and  200   
     In further text, the preferred method for manufacturing GaN/diamond engineered wafers is described using the wafer  700  as starting material (Method  100 ). If Method  200  is practiced, wafer  700  and the associated surfaces  700 A and  700 B are to be replaced with wafer  710  and the associated surfaces by  710 A and  710 B, respectively. It is also clear that the surfaces  804 A and  805 A mean the surface of silicon nitride layer  804  when Method  100  is practiced, and that the surface  804 A means the surface of in-situ silicon nitride layer  711  when Method  200  is practiced, and that in either case the  805 A surface is that of polysilicon layer deposited in steps  101 C if Method  100  is used or  106  if Method  200  is used. 
     STEP  102  “MEASURE BOW”: Bow of wafer  700  with surface  700 A up is measured using a surface-profilometer or micrometer. The recorded value of bow is referred to as the first bow value. The typical values of first bow on a 100-mm wafer are negative between −4 μm and −12 μm. 
     STEP  103  “CARRIER WAFER”: A carrier wafer  720  is selected (shown in  FIG. 4B ). In one embodiment, the wafer  720  is a silicon wafer with crystalline orientation (100) or (110). At least one side of wafer  720  is polished. The polished side of wafer  720  is referred to as surface  720 B, and the other side is referred to as surface  720 A. 
     STEP  104  “MEASURE BOW”: The bow of carrier wafer  720  is measured on surface  720 B and the value of bow is referred to as the second bow value. The typical values of second bow on carrier wafer  720  range between 0 and +10 μm. 
     STEP  105  “COMPARE BOW”: The first and second bow values are compared with the purpose of finding an appropriate carrier wafer  720  that will be bonded to the wafer  700  in a later step. The following two conditions have to be met simultaneously for accepting a match between wafers  700  and  720 : 
     (a) Either the first bow value is positive and the second bow value is zero or negative, or the second value of bow is negative and the first bow value is zero or positive, and 
     (b) The absolute difference between first and second bow values is less or equal to 10 μm multiplied by the square of the ratio of the wafer diameter in mm divided by 100 mm. Expressed mathematically, |BOW 1 −BOW 2 |≦10 μm·(D/100) 2 , where BOW 1  is the first bow value, BOW 2  the second bow value, and D the wafer diameter in millimeters. If both (a) and (b) are met, the wafer  720  is used with wafer  700  and one proceeds with wafer  720  to step  108 . If less than both of these two conditions are met, one selects a new carrier wafer  720  in step  103  and the steps  104  and  105  repeat until the bow condition is met and the selected carrier wafer  720  can be used in step  108 . 
     STEPS  107  and  108  “SPIN GLASS”: In step  107 , the surface  805 A of wafer  700  is spin-coated with a glass  806  and in step  108  surface  720 A of wafer  720  is spin-coated with same glass (numbered  807 ) and under same process conditions. Once coated, wafer  700  is referred to as wafer  730  as shown in  FIG. 5A , and wafer  720  is referred to as wafer  740  as shown in  FIG. 5B . The coating process conditions and recipe is described next. These two steps (step  107  and  108 ) may occur sequentially or simultaneously. The glass used in layers  806  and  807  has the following preferred characteristics: (a) it has a melting point or processing temperature at 1000° C. or within 10% of 1000° C., and (b) linear coefficient of thermal expansion (CTE) between 3 ppm/K and 6 ppm/K at room temperature. These specifications have been shown to be necessary for flat adhesion of wafers in later step  110 . An example of such a glass proven to work with the preferred process is Ferro Metal Sealing glass EG2800 manufactured by Ferro Corporation, Mayfield Heights, Ohio. Coating both wafers  700  and  720  with said glass using a conventional semiconductor-foundry-type spinner at 4,000 rpm for 15 seconds results in glass thickness of 3 μm. The glass-coated wafers  730  and  740  are then dried on a hotplate at 120° C. for 5 min, then the wafer backsides ( 720 A and  700 B) are cleaned from any excess glass, and another hotplate at 400° C. for 5 min is applied. Both wafers  730  and  740  are finally baked in a furnace at 750° C. for 30 minutes to dry out. The glass-coated surface of wafer  730  is now referred to as surface  806 A, and the glass coated surface of wafer  740  is now referred to as surface  807 B. In one embodiment, the total glass thickness ( 806  plus 807) is between 100 nm and 10 um. 
     STEP  109  “LOAD JIG”: Wafers  730  and  740  are placed in contact with the glass-coated surfaces  806 A and  807 B touching, and bonded under elevated temperature and axial pressure pressing the wafers against each other. In one embodiment, the wafers are placed into a bonding jig which enables pressure to be applied against the wafers  730  and  740  so that they stay pressed against each other during an annealing step. The wafer sandwich containing the wafer  730  on bottom and wafer  740  on top is referred to as wafer sandwich  721  and the two revealed surfaces of this wafer sandwich  721  are surfaces  720 A and  700 B. A view of an exemplary bonding jig is illustrated in  FIG. 6 . The relative dimensions in the  FIG. 6  are not to scale, the drawing only illustrates the functional elements of the jig necessary for successful completion of preferred process step  109 . 
     The bonding jig  200  comprises at least of a base  201  providing support of the wafers to be bonded, a cross-bar  202  providing pressure from the top on the wafers to be bonded, two-piece angled height adjustment member  208 , and a dome  209  which ensures that the pressure on top of the wafers is applied in the center of the wafer and even distributed to the entire surface of the wafers below it. 
     On the bottom of bonding jig  200 , the following elements are placed in order: at least one alumina plate  203 , first quartz plate  204 , first silicon wafer  205 , the wafer sandwich  721  with the surface  700 B adjacent to first silicon wafer  205 , a second silicon wafer  206 , second quartz plate  207 , and finally the dome  209  on top of this stack. The listed wafer/plate stack ( 203 ,  204 ,  205 ,  721 ,  206 , and  207 ) is referred to as the wafer/plate stack  210 . The dome  209  is pressed down with the angled height-adjusting members  208  which are pressing against the cross-bar  202 . The jig is so loaded at room temperature and the angled height-adjusting members are positioned in such a way that a slight force is exerted on the dome  209 . The cross-bar  202  is coupled to the base  201  in such a way that it resists any movement upwards which is the direction in which the wafers/plate stack  210  will expand when heated. The cross-bar  202  can be easily removed once the angled height adjustment members  208  are moved to release the pressure from the wafer/stack  210 . The quartz plates  204  and  207  have an approximate thickness equal to 3 mm each and bow of the surface facing the wafer sandwich  721  less than 8 μm. The total thickness of the alumina plate or plates  203  is approximately 5 mm. The thickness of the first and second silicon wafers is approximately 500 μm each. The diameter of all the wafers and plates is at least as large as the diameter of the wafer sandwich  721 . 
     The principle of operation of the bonding jig is as follows: The jig is loaded at room temperature and the force on the wafer sandwich  721 , which is a part of the stack  210 , exerted by the jig is set to be small, but sufficient to hold the wafers in place. As the temperature rises, the jig  201  (including the cross-bar  202 , the dome  209 , and the height-adjusting members) and the loaded wafer/plate stack  210  expand with different rates in such a way the force on the wafer sandwich  721  increases. Alumina and silicon have a larger coefficient of thermal expansion than quartz and hence the wafer/plate stack  210  expand more than dimension allowed for it by the base  201 , the cross-bar  202 , the dome  209 , and the height-adjusting members  208 . In this way, at elevated temperature the jig exerts a force pressing the wafer sandwich  721  together and realizes bonding of the wafers  700  and  720  using the spun-on glass layers  806 / 807  between them. The jig base  201 , the cross-bar  202 , the two angled height-adjusting members  208 , and the dome  209  are all preferably made out of quartz with CTE ˜0.6 ppm/K. It is clear that material combination other than alumina or silicon as the high CTE material and quartz as the low CTE material can be used to accomplish the same function without departing from the spirit of the invention. 
     In another embodiment, the pressure and the elevated temperature profiles are applied independently using a suitable apparatus as is known in the art. In one embodiment, the pressure is applied before and during the elevated temperature process, but released (set to near zero) during the cool down. 
     STEP  110  “BOND”: The jig with the wafer sandwich  721  (as a part of the stack  210 ) is loaded into a furnace and heated at a heating rate 10° C./min to 1000° C. where is left to soak for 20 min (soak time) before cooling down at a rate approximately equal to the heating rate. The jig is unloaded and wafer sandwich  721  taken out. The preferred value of force the jig  200  exerts onto the wafer sandwich  721  of diameter 100 mm in the jig at 1000° C. is at least 50 N and not more than 150 N. In one embodiment, the soak time ranges between 5 and 30 minutes. 
     STEP  111  “SPIN GLASS”: The edges of wafer sandwich  721  are manually or robotically coated with glass  806  and then the surface  720 A of wafer sandwich  721  is spin-coated with glass  806  on a conventional semiconductor-foundry-type spinner at 4,000 rpm for 15 seconds. This results in glass thickness of 3 μm on the surface  720 A. The glass-coated wafer  720  is then dried on a hotplate at 120° C. for 5 min, then the wafer surface  700 B is cleaned from any excess glass, and another hotplate at 400° C. for 5 min is applied. Wafer sandwich  721  is finally baked in a furnace at 750° C. for 30 minutes to burn-off polymers. 
     STEP  112  “ANNEAL”: Wafer sandwich  721  is loaded into a furnace and heated at a heating rate 10° C./min to 1000° C. where is left to soak for 20 min before cooling down at a rate approximately equal to the heating rate. The jig is unloaded and the wafer sandwich  721  taken out. 
     STEP  113  “REMOVE NATIVE SUBSTRATE”: The wafer sandwich  721  is now subjected to substrate removal step. In one embodiment, the silicon portion  701  of wafer  700  is removed down to the nucleation layers  702  by first performing a mechanical grinding to 100 um remaining thickness of native substrate  701  using a 6 um grit. The surface of silicon  701  that has been thinned is now exposed to 2 minutes of oxygen plasma to clean, and then the rest of the 100 um of silicon is removed using plasma etching in SF6 at 100 mTorr 290 W and 175 V self-bias. Once the silicon layer  701  has been and the etch stops on the nucleation layer  702 , the self-bias voltage generally jumps up by several volts. Typical etch rate is 1 μm/min and etch lasts around 90 min. The revealed surface of nucleation layer  702  is cleaned with hot acetone. In one embodiment, the step  114  includes the removal of a part of the buffer layer  703 . In another embodiment, the entire native substrate is removed by plasma etching. There is a number of ways, as known in the art, to remove silicon substrates down to an etch stop, any one of which can be applied to this step without departing from the invention. 
     STEP  114  “REMOVE NUCLEATION LAYERS”: In this step, the nucleation layers  708  are removed. In one embodiment, the wafer sandwich  721  is next subjected to a wet chemical etch in hot sulphuric acid at 120° C. with 13 liters of H 2 SO 4  and 0.2 liters H 2 O 2 . This step removes the AlGaN nucleation layers with typical etch rate 500 nm/hr. At the end of this etch the surface  700 B is now GaN buffer layer  703 . In one embodiment, step  114  also includes removal of a part of the buffer layer  703 , preferably the part of the buffer layer  703  between the nucleation layer  702  and the functional boundary  709  beyond which the material quality is high (defect density low). In one embodiment, the nucleation layers are removed by dry etching. In yet another embodiment, the nucleation layers are removed by a combination of dry and wet chemical etching. The surface of the GaN buffer  703  remaining revealed is referred to as surface  703 B. 
     STEP  115  “DEPOSIT DIAMOND NUCLEATION LAYER”: The revealed surface of GaN buffer layer  703 B is now coated with thermal silicon nitride  801  at 600° C. in a furnace. The typical growth rate is approximately 5 nm/min and the time is adjusted for desired thickness. The typical thicknesses range from 10 nm to 60 nm. The deposited silicon nitride  801  is amorphous, but may be polycrystalline. The revealed surface of silicon nitride  801  is not referred to as surface  801 B, and the wafer at this stage is referred to as wafer sandwich  750 . 
     At the end of step  115 , the structure of wafer sandwich  750  prepared for diamond deposition is shown illustratively in  FIG. 7 . The wafer sandwich  750  comprises of the following layers: active layers  707  as were present in the original as-grown wafer  700  (see  FIG. 4A ), a layer of silicon nitride  804  as deposited in step  106  on top of the active layer  707 , glass  806  and  807  deposited in steps  107  and  108  on top of polysilicon layer  805 , carrier wafer  720  as attached in step  109 , and silicon nitride layer  801  on top of the active layer as deposited in step  115 . The revealed surface of the silicon nitride layer  801  is referred to as the new surface  801 B, and the remaining revealed surface of the glass  808  is still referred to as surface  808 A. The structure of the active layer  707  remains the same as in wafer  700 : The active layer  707  comprises a GaN buffer layer  703 , a two-dimensional electron gas  705 , and AlGaN barrier  706 . 
     In one embodiment, a substrate prepared for diamond deposition comprises silicon wafer; a layer of glass disposed on top of said silicon wafer; a poly-silicon layer disposed on top of said glass layer; a first silicon nitride layer disposed on top of said polysilicon layer; a multilayered structure layer comprising at least one layer made out of gallium nitride disposed on top of said polysilicon layer; a second silicon nitride layer with thickness between 10 nm and 100 nm disposed on top of said multilayered structure layer; wherein said second silicon nitride layer is amorphous. In one embodiment, said silicon wafer has thickness greater than 0.2 millimeters. In yet another embodiment, the layer of glass has thickness between 0.1 micrometers and 10 micrometers. In yet another embodiment, the layer of glass has a melting temperature of at least 1000° C. In yet another embodiment, the polysilicon layer has thickness between 0.1 and 2 micrometers. In another embodiment, the first silicon nitride layer is an in-situ silicon nitride. In yet another embodiment, the second silicon nitride layer has thickness between 10 nanometers and 100 nanometers. In yet another embodiment, the at least one gallium nitride layer is semi-polar or non-polar gallium nitride. In yet another embodiment, the multilayered layer has a surface consisting of gallium-terminated gallium nitride, said surface is adjacent to said first silicon nitride. 
     STEP  116  “DEPOSIT DIAMOND”: The  801 B surface of the wafer sandwich  750  is prepared for diamond growth. In one embodiment, the surface  801 A is first seeded with 100-nm diamond grit by dry scratch for 9 min 50-mm or 14 min for 100-mm wafer using a using diamond-grit-loaded cloth. In another embodiment, the wafers are laid down for scratching using large cloth with applying vibratory seeding. In yet another embodiment, the wafers are wet scratched by using the same grit with ultrasonic bath ethanol, methanol, or isopropanol. The process of seeding a surface for diamond growth is a process well known in diamond growth technology. 
     The seeded wafer sandwich  750  is now loaded into a diamond growth chamber and a diamond layer is grown on top of the surface  801 B by chemical-vapor deposition. 
     Illustratively shown in  FIG. 8 , the CVD diamond chamber comprises of (a) a vacuum chamber  901 , (b) a chuck  902  operatively configured to be actively or capacitively temperature controlled on top of an actively-cooled basin  911 , (c) a molybdenum disk  903  having a surface  903 A for holding a wafer  905  of a diameter, said molybdenum disk  903  disposed between said chuck  902  and said wafer  905 , and said molybdenum disk  903  operatively configured to rotate along an axis  904  perpendicular to said wafer  905 , and (d) a multiplicity of filaments  906  arranged in a linear one-dimensional array stretched between filament contacts  911  above said molybdenum disk  903 , said array of filaments  906  being parallel to said surface  903 A, said multiplicity of filaments  903  distanced from said surface  903 A by not more than 25 mm. In one embodiment, said multiplicity of filaments  906  is distanced from said wafer surface by not less than 4 mm. Said vacuum chamber  901  is operatively configured using pipes and manifolds  907  as is known in the art to provide reaction gases  908  to the chamber wherein said reaction gases  908  comprise at least one carbon-bearing gas and hydrogen. In one embodiment, said carbon-bearing gas is methane (CH 4 ). The reaction gases may include oxygen. The vacuum chamber  901  is further equipped with a vacuum pump (located at the exit  910  of  FIG. 8 ) and is operatively configured to operate in a pressure range that includes pressures below 100 Torr. The pressure control may be performed by maintaining constant pump speed and adjusting the gas flow or by controlling a flow control value at the exit  909  from the vacuum chamber  901 . In one embodiment, the filaments are made out of refractory metal. In yet another embodiment the filaments are made out of tungsten. The chuck is cooled so that the surface of the molybdenum disk is maintained at a temperature at or below 800° C. The walls of the vacuum chamber  901  include water cooling. 
     The process recipe comprises of steps of (a) loading the wafer into the chamber by placing the wafer sandwich  750  with surface  808 A facing the molybdenum disk  903 , (b) providing a multiplicity of filaments arranged in a linear one-dimensional array stretched above said wafer sandwich  750  and being parallel to said wafer surface, said multiplicity of filaments distanced from said wafer surface by not less than 4 mm, (c) providing reaction gases to the chamber wherein said reaction gases comprise at least one carbon-bearing gas and hydrogen at flow rates sufficient to adjust the chamber pressure below 100 Torr, (d) providing electrical power to said multiplicity of filaments, said power being at least 3 kW, (d) maintaining growth conditions for sufficient time to grow a pre-determined thickness of diamond. 
     In one embodiment, the wafer size is approximately 100 m and the thickness of the diamond layer is 100 um±20 um, but may range between 20 and 300 um. The completed structure is shown in  FIG. 9  and denoted  760 . The diamond layer is denoted  723  and its last-grown surface  723 B. 
     STEP  117  “MEASURE BOW”: Upon removal from the vacuum chamber  901 , the third value of bow on the wafer sandwich  760  is measured with the surface  723 B up. The bow should be convex (center higher than the edge, i.e., third bow value is positive). In one embodiment, the third bow value is less than 1 mm for an approximately 100 mm diameter wafer  750  with 100 um-thick diamond layer  723  and wafer  750  with nominal thickness of 650 μm. The result of this condition is a low bow of the completed wafer  770  in a later step  120 . In another embodiment, the third bow is between 650 um and 950 um on a 100 mm wafer sandwich  750  with 100 um diamond thickness. The key requirement in achieving flat GaN/diamond engineered wafers  770  and  780  in step  120  is that the third bow of the wafer sandwich  760  is convex and limited to a pre-determined value. 
     STEP  118  “LASER TRIM”: The diamond-coated wafer  750  illustratively shown in  FIG. 9  comprises of the wafer sandwich  750  coated with a layer of diamond  723 . The edges of the wafer sandwich  750  are also in part coated with diamond as illustrated with 751. The wafer  750  is now trimmed to remove the edges coated with diamond in places indicated with dashed lines  755 . The distance between the laser-trimming  755  is slightly less than the diameter of the wafer sandwich  750  by typically 1 mm overall. 
     STEP  119  “REMOVE CARRIER WAFER”: The surface  808 A of the carrier wafer  720  coated with glass  808  both of which are a part of the wafer sandwich  750  are now removed using wet chemical processing. First the glass  808  is exposed to HF for 1 min to remove the glass  808 , Piranha etch comprising of a mixture CH 3 COOH:HNO3:HF (2:2:1 by volume) followed by etching in Tetramethylammonium hydroxide (TMAH) (CH 3 ) 4 NOH to remove carrier wafer  720 , the glasses  806  and  807 , and polysilicon  805 . This step reveals the silicon nitride  804 . 
     STEP  120  “REMOVE SILICON NITRIDE”: In one embodiment, silicon nitride  804  is removed by etching in concentrated HF with etch rate that is approximately 10 nm/min. This process reveals the original active layers  707  of the as-grown epilayers. The resulting engineered wafer is denoted wafer  770  and its structure is illustrated in  FIG. 10 . The engineered wafer  770  comprises of active layers  707 , silicon nitride diamond nucleation layer  801 , and diamond wafer  723 . 
     In another embodiment, step  120  is omitted. This is the case when the devices to be manufactured on this wafer will use the nitride layer  804 . For example, the remaining silicon nitride layer may be used as a passivating layer in a high-electron mobility transistor. In this embodiment, the result of the process is engineered wafer  780 , illustrated in  FIG. 11 . The engineered wafer  780  comprises of active layers  707 , silicon nitride diamond nucleation layer  801 , diamond wafer  723 , and silicon nitride layer  804 . In one embodiment, the silicon nitride  804  is in-situ silicon nitride. In another embodiment, the silicon nitride  804  is thermally grown silicon nitride. 
     Clearly, various modifications of the presented steps for manufacturing GaN-on-diamond wafers are possible without departing from the invention: Varying the thickness of the plates in steps  109 , the times and temperatures in steps  110 ,  112 ,  115 , and  116 . The apparatuses disclosed in steps  109  and  116  may also be used to manufacture a variety of other innovative devices and wafer structures. 
     It is also clear that the preferred methods may be used for manufacturing of engineered wafers that will be used for manufacturing of light-emitting devices, such as, light-emitting diodes, lasers, and super-luminescent light-emitting diodes by varying the specific of the active layer design. For this purpose, it is clear that modifying the crystal orientation of the active layer to suit any of the mentioned application is possible without departing from the spirit of the invention. Specifically, the active layers may be polar, semi-polar, or non-polar. Additionally, the high-electron mobility transistor designed above may be used for power management applications in which the buffer layer thickness and the specific of the epilayer design may be altered to allow for high breakdown voltage. The preferred methods may be used to also manufacture high-voltage Schottky diodes. 
     While certain representative embodiments and details have been shown for purposes of illustrating the invention, it will be apparent to those skilled in the art that various changes in the methods and apparatus disclosed herein may be made without departing from the scope of the invention which is defined in the appended claims.