Abstract:
A method for producing a battery comprises a deformation step for moving a first metal foil ( 11 ) forming a pair of perpendicularly intersecting portions ( 44   d   , 44   e ) of a first metal, respectively, toward the outside in a second radial direction while enlarging the inside diameter, in the second radial direction (Y), of a first metal winding part ( 44 ) by making a force act on the pair of perpendicularly intersecting portions ( 44   d   , 44   e ) of a first metal toward the outside in the second radial direction, and a resistance welding step for pressing a pair of first metal welding portions ( 44   b   , 44   c ) toward the inside in a first radical direction under a state where the first terminal welding part ( 53 ) of a first current collecting terminal member ( 50 ) is arranged on the radial by inside of the first metal winding part ( 44 ) after the first metal winding part ( 44 ) is deformed, and then resistance welding the first metal welding portions ( 44   b   , 44   c ) to the first terminal welding part ( 53 ) under a state where the pair of first metal welding portions ( 44   b   , 44   c ) are brought into pressure contact with the first terminal welding part ( 53 ).

Description:
TECHNICAL FIELD 
       [0001]    The present invention relates to a battery and a production method therefor. 
       BACKGROUND ART 
       [0002]    There have been proposed various types of batteries each including an electrode body having: a power generating part made by laminating a first electrode-forming portion having a first electrode mixture layer of a first electrode sheet and a second electrode sheet by interposing a separator therebetween and winding such a laminated body about an axis line into a cylindrical form; and a first metal winding part (a portion formed with no electrode mixture layer) constitute of only a first metal portion made of a first metal foil in a wound form, the first metal winding part being adjacent to the power generating part (for example, see Patent Literature 1). A cylindrical battery disclosed in Patent Literature 1 is provided with a current collecting terminal (a first current collecting terminal member) for collecting electric charge of a first electrode sheet, the current collecting terminal including a portion (a first terminal welding part) being located on the radial inside of the portion with no electrode mixture layer (the first metal winding part) and welded to the first metal winding part. 
       Citation List 
     Patent Literature 
       [0003]    Patent Literature 1: JP-A-2000-231913 
       SUMMARY OF INVENTION 
     Technical Problem 
       [0004]    Meanwhile, Patent Literature 1 discloses a method achieved by radially inward pressing a pair of first metal welding portions of a cylindrical first metal winding part respectively, and welding the first metal welding portions and a first terminal welding part placed on the radial inside of the first metal winding part while holding the first metal welding portions in pressure contact with the first terminal welding part. According to this method, when the first metal welding portions are pressed radially inward to press against the first terminal welding part, parts of the first metal foil may buckle at first metal perpendicularly intersecting portions of the first metal winding part and hence the buckled part of the metal foil may contact an adjacent part of the metal foil. It is to be noted that the first metal winding part does not include a second electrode plate and a separator between the parts of the first metal foil and thus the parts of the first metal foil forming the first metal winding part are apart from each other before pressing. 
         [0005]    If the parts of the first metal foil forming the first metal perpendicularly intersecting portion buckle, the parts caused to contact with each other due to buckling are apt to generate spatters during resistance welding, causing a part (foreign matters) of the first metal foil to scatter and adhere to the electrode body. Thus, the foreign matters may enter in a battery, leading to a decrease in reliability of the battery. Furthermore, a shunt of welding current at the contact portions resulting from buckling may cause welding failures between the first metal winding part and the first terminal welding part. This also may deteriorate the battery reliability. 
         [0006]    The present invention has been made to solve the above problems and has a purpose to provide a highly reliable battery produced by preventing entrance of foreign matters in the battery and including a first metal winding part and a first terminal welding part both being appropriately welded to each other, and a production method therefor. 
       Solution to Problem 
       [0007]    To achieve the above purpose, the present invention provides a method of producing a battery comprising an electrode body and a first current collecting terminal member, the electrode body being provided with: a first electrode sheet having a first electrode mixture layer provided on a surface of a strip-shaped first metal foil, the sheet including: a first electrode-forming portion extending along one side of the first metal foil extending in a longitudinal direction and including the first metal foil and the first electrode mixture layer; and a first metal portion extending adjacently to the first electrode-forming portion and along the one side along the longitudinal direction and consisting of the first metal foil without having the first electrode mixture layer; a strip-shaped second electrode sheet; and a strip-shaped separator, the electrode body including: a power generating part in which the first electrode-forming portion of the first electrode sheet and the second electrode sheet are laminated by interposing the separator therebetween and wound around an axis line into a cylindrical form; and a first metal winding part in which the first metal portion is wound, the first metal winding part being adjacent to the power generating part, and the first current collecting terminal member being configured to collect electric charge of the first electrode sheet and provided with a first terminal welding part placed on a radial inside of the first metal winding part and welded to the first metal winding part, the method comprising: a deforming step of deforming the first metal winding part of the electrode body including: the power generating part; and the first metal winding part in which the first metal portion is wound in a cylindrical form, the deforming step including: when a pair of portions of the first metal winding part to be welded to the first terminal welding part of the first current collecting terminal member, the portions being opposed to each other in a first radial direction of the first metal winding part, is a pair of first metal welding portions, and a pair of portions of the first metal winding part opposed to each other in a second radial direction perpendicular to the first radial direction is a pair of first metal perpendicularly intersecting portions, exerting an outward force in the second radial direction on the pair of metal perpendicularly intersecting portions to enlarge the inside diameter of the first metal winding part in the second radial direction and move parts of the first metal foil forming the pair of first metal perpendicularly intersecting portions outward in the second radial direction respectively, and a resistance welding step of pressing the pair of first metal welding portions inward in the first radial direction while the first terminal welding part of the first current collecting terminal member is placed on the radial inside of the deformed first metal winding part, and resistance-welding the first metal welding portions and the first terminal welding part to each other while holding the pair of first metal welding portions in pressure contact with the first terminal welding part. 
         [0008]    According to the production method of the invention, before the pair of first metal welding portions are pressed against the first terminal welding part in the resistance welding step, an outward force in the second radial direction is applied in advance to the pair of first metal perpendicularly intersecting portions in the deforming step to move the parts of the first metal foil forming the pair of first metal perpendicularly intersecting portions outward in the second radial direction respectively. In the later resistance welding step, accordingly, when the pair of first metal welding portions are pressed inward in the first radial direction to bring the pair of first metal welding portions in pressure contact with the first terminal welding part, the parts of the first metal foil forming the pair of metal perpendicularly intersecting portions are allowed to easily move together outward in the second radial direction. 
         [0009]    According to such deforming technique, the first metal winding part is unlikely to buckle during deforming. Furthermore, the parts of the first metal foil forming the pair of first metal perpendicularly intersecting portions are respectively moved outward in the second radial direction, thus moving the pair of metal welding portions inward in the first radial direction, bringing the first metal winding part closer to the first terminal welding part. 
         [0010]    In the resistance welding step, accordingly, when the pair of first metal welding portions are pressed inward in the first radial direction to bring the pair of first metal welding portions in pressure contact with the first terminal welding part, the parts of the first metal foil forming the first metal winding part can be prevented from buckling. This makes it possible to prevent adhesion of foreign matters to the electrode body caused by the occurrence of spatters, thereby avoiding entrance of the foreign matters into the battery. It is further possible to prevent welding failures between the first metal welding portions and the first terminal welding part due to the influence of a shunt of welding current. Therefore, the production method of the invention can produce a highly reliable battery. 
         [0011]    One example of the deforming step is achieved by deforming the cylindrical first metal winding part into an elliptic form having an inside diameter in the first radial direction shorter than an inside diameter in the second radial direction. 
         [0012]    Furthermore, in the above battery production method, preferably, the first terminal welding part has a shape having such a cross section, taken along a direction perpendicular to the axis line while the first terminal welding part is placed on the radial inside of the first metal winding part, as that a maximum size in the second radial direction is larger than the inside diameter of the first metal winding part before deformed and a maximum size in the first radial direction is smaller than the inside diameter of the first metal winding part before deformed, and he deforming step including inserting the first terminal welding part in the radial inside of the first metal winding part. 
         [0013]    In the production method of the invention, the first terminal welding part is inserted in the radial inside of the first metal winding part to exert an outward force in the second radial direction on the pair of first metal perpendicularly intersecting portions, thereby enlarging the inside diameter of the first metal winding part in the second radial direction and moving the parts of the first metal foil forming the pair of metal perpendicularly intersecting portions respectively outward in the second radial direction. This method is therefore more preferable because easier and faster deforming of the first metal winding part can be achieved as compared with deforming of the first metal winding part using an additional deforming jig and the like. 
         [0014]    Furthermore, in the above battery production method, preferably, the first terminal welding part has a cross section taken along the second radial direction so as to pass the axis line while the first terminal welding part is placed on the radial inside of the first metal winding part, the cross section having such a size in the second radial direction as that the size at a side closest to the power generating part is equal to or less than the inside diameter of the first metal winding part before deformed, the size increases as farther from the power generating part in the axis line direction, and the size at a farthermost side from the power generating part in the axis line direction is larger than the inside diameter of the first metal winding part before deformed. 
         [0015]    Because of the use of the first current collecting terminal member including the first terminal welding part having the above shape, the first terminal welding part can be smoothly inserted in the radial inside of the first metal winding part. Furthermore, as the first terminal welding part is inserted in the first metal winding part, the force applied on the first metal winding part gradually increases. Therefore, the parts of the first metal foil forming the first metal winding part are less likely to break than the case where a large force is applied abruptly. 
         [0016]    Furthermore, one of the above battery production methods, preferably, further comprises: after the deforming step and before the resistance welding step, a foil collecting step of pressing the pair of first metal welding portions inward in the first radial direction while the first terminal welding part is placed on the radial inside of the deformed first metal winding part to collect parts of the first metal foil forming the first metal welding portions inward in the first radial direction while decreasing clearances between the parts of the first metal foil in the first radial direction. 
         [0017]    Before resistance welding, the parts of the first metal foil forming the first metal welding portions are collected in advance inward in the first radial direction while reducing the clearances or spaces between the parts of the first metal foil in the first radial direction, thereby allowing more appropriate resistance welding. In particular, in the later resistance welding step, the first metal winding part is unlikely to be deformed when the first metal welding portions are pressed inward in the first radial direction. Accordingly, this method is more preferable in further preventing buckling of the first metal foil. 
         [0018]    In the deforming step, before the foil collecting step, the parts of the first metal foil forming the first metal perpendicularly intersecting portions are moved outward in the second radial direction. In the foil collecting step, therefore, when the first metal welding portions are pressed inward in the first radial direction, the parts of the first metal foil forming the first metal perpendicularly intersecting portions are easily moved together outward in the second radial direction. Accordingly, it is also possible to prevent the first metal foil from buckling even in the foil collecting step. 
         [0019]    Furthermore, in the above battery production method, preferably, the first terminal welding part has a shape formed with a portion recessed inward in the first radial direction as compared with other portions in a cross section taken along the direction perpendicular to the axis line while the first terminal welding part is placed on the radial inside of the first metal winding part, the recessed portion being to be welded to the first metal welding portions of the first metal winding part, and the foil collecting step includes pressing the first metal welding portions inward in the first radial direction to bring the first metal welding portions in pressure contact with the recessed portion of the first terminal welding part. 
         [0020]    In the foil collecting step, even when the first metal welding portions are pressed inward in the first radial direction to collect the parts of the first metal foil forming the first metal welding portions inward in the first radial direction while reducing the clearances between the parts of the first metal foil in the first radial direction, the parts of the first metal foil forming the first metal welding portions are apt to elastically move outward in the first radial direction due to spring back. 
         [0021]    However, according to the production method of the invention, the first current collecting terminal member includes the first terminal welding part shaped to have the portion recessed inward in the first radial direction as compared with other portions, the recessed portion being to be welded to the first metal welding portions of the first metal winding part when the first terminal welding part is taken along the direction perpendicular to the axis line while the first terminal welding part is placed on the radial inside of the first metal winding part. Then, the first metal welding portions are pressed inward in the first radial direction to bring the first metal welding portions in pressure contact with the recessed portion of the first terminal welding part. Thus, even when the first metal foil causes outward spring back in the first radial direction, the parts of the first metal foil forming the first metal welding portions can appropriately be collected inward in the first radial direction. 
         [0022]    Another aspect of the invention provides a battery comprising an electrode body and a first current collecting terminal member, the electrode body being provided with: a first electrode sheet having a first electrode mixture layer provided on a surface of a strip-shaped first metal foil, the sheet including: a first electrode-forming portion extending along one side of the first metal foil extending in a longitudinal direction and including the first metal foil and the first electrode mixture layer; and a first metal portion extending adjacently to the first electrode-forming portion and along the one side along the longitudinal direction and consisting of the first metal foil without having the first electrode mixture layer; a strip-shaped second electrode sheet; and a strip-shaped separator, the electrode body including: a power generating part in which the first electrode-forming portion of the first electrode sheet and the second electrode sheet are laminated by interposing the separator therebetween and wound around an axis line into a cylindrical form; and a first metal winding part in which the first metal portion is wound, the first metal winding part being adjacent to the power generating part, and the first current collecting terminal member being configured to collect electric charge of the first electrode sheet and provided with a first terminal welding part placed on a radial inside of the first metal winding part and welded to the first metal winding part, wherein when a pair of portions of the first metal winding part welded to the first terminal welding part of the first current collecting terminal member and opposed to each other in a first radial direction of the first metal winding part is a pair of first metal welding portions, and a pair of portions of the first metal winding part opposed to each other in a second radial direction perpendicular to the first radial direction is a pair of first metal perpendicularly intersecting portions, in a cross section taken along a direction perpendicular to the axis line to pass the first metal welding portions, the first metal winding part has an outside diameter in the first radial direction smaller than an outside diameter in the second radial direction, and each part of the first metal foil forming the first perpendicularly intersecting portions is curved to bulge outward in the second radial direction. 
         [0023]    The battery of the invention is configured such that the first terminal welding part placed on the radial inside of the first metal winding part and the first metal welding portions of the first metal winding part are resistance-welded to each other. Furthermore, in the cross section of the first metal winding part taken along the direction perpendicular to the axis line to pass the first metal welding portions, the outside diameter of the first metal winding part in the first radial direction in which the pair of metal welding portions are opposed to each other is determined to be smaller than the outside diameter of the first metal winding part in the second radial direction perpendicular to the first radial direction. 
         [0024]    Such battery is produced in such a manner that the pair of first metal welding portions are pressed respectively radially inward while the first terminal welding part is placed on the radial inside of the first metal winding part and the first metal welding portions are resistance-welded to the first terminal welding part while holding the pair of first metal welding portions in pressure contact with the first terminal welding part. However, when the first metal welding portions are pressed radially inward to press against the first terminal welding part, conventionally, a part or parts of the first metal foil might buckle at the first metal perpendicularly intersecting portions of the first metal winding part and hence come into contact with an adjacent part or parts of the metal foil. If the part of the first metal foil at the first metal perpendicularly intersecting portion buckles, the parts caused to contact with each other due to buckling may generate spatters during the resistance welding, causing a part (foreign matters) of the first metal foil to scatter and adhere to the electrode body. Furthermore, a shunt of welding current in the portions resulting from buckling may cause welding failures between the first metal winding part and the first terminal welding part. This also may deteriorate the battery reliability. 
         [0025]    On the other hand, in the battery of the invention, each of the parts of the first metal foil forming the first metal perpendicularly intersecting portions is curved to bulge outward in the second radial direction. Specifically, the first metal foil does not buckle at the first metal perpendicularly intersecting portions. Thus, the first metal welding portions and the first terminal welding part are resistance-welded to each other while preventing adhesion of foreign matters to the electrode body caused by the occurrence of spatters and welding failures due to a shunt of welding current between the first metal welding portions and the first terminal welding part. From the above, the battery of the invention can be achieved as a highly reliable battery by restraining entrance of the foreign matters into the battery and appropriately welding the first metal winding part and the first terminal welding part to each other. 
     
    
     
       BRIEF DESCRIPTION OF DRAWINGS 
         [0026]      FIG. 1  is a view showing a first electrode sheet in an embodiment; 
           [0027]      FIG. 2  is a view showing a second electrode sheet in the embodiment; 
           [0028]      FIG. 3  is a view to explain a step of laminating the first electrode sheet, the second electrode sheet, and a separator and winding them into a cylindrical form; 
           [0029]      FIG. 4  is a side view of an electrode body in which the first electrode sheet, the second electrode sheet, and the separator are laminated and wound in the cylindrical form; 
           [0030]      FIG. 5  is a plan view of a first current collecting terminal member in the embodiment; 
           [0031]      FIG. 6  is a view showing a state where a first terminal welding part is inserted and placed on the radial inside of a first metal winding part, thereby deforming the first metal winding part; 
           [0032]      FIG. 7  is a sectional view of the first metal winding part after deformed, taken along a line B-B in  FIG. 6 ; 
           [0033]      FIG. 8  is a sectional view of the first metal winding part after deformed, taken along a line C-C in  FIG. 6 ; 
           [0034]      FIG. 9  is a sectional view of the first terminal welding part taken along a second radial direction so as to pass an axis line of a power generating part while the first terminal welding part is placed on the radial inside of the first metal winding part; 
           [0035]      FIG. 10  is a view to explain a foil collecting step in the embodiment; 
           [0036]      FIG. 11  is another view to explain the foil collecting step in the embodiment; 
           [0037]      FIG. 12  is a view showing a state during resistance welding; 
           [0038]      FIG. 13  is a view of a battery in the embodiment; 
           [0039]      FIG. 14  is a sectional view of the first metal winding part of the battery, taken along a line L-L in  FIG. 13 ; 
           [0040]      FIG. 15  is a view to explain a foil collecting step in Comparative example 1; and 
           [0041]      FIG. 16  is another view to explain the foil collecting step in Comparative example 1. 
       
    
    
     REFERENCE SIGNS LIST 
       [0000]    
       
           1  Battery 
           10  First electrode sheet 
           11  First metal foil 
           12  First electrode mixture layer 
           13  First metal part 
           14  First electrode-forming portion 
           20  Second electrode sheet 
           30  Separator 
           40  Electrode body 
           42  Power generating part 
           44  First metal winding part 
           44   b ,  44   c  First metal welding portion 
           44   d ,  44   e  First metal perpendicularly intersecting portion 
           50  First current collecting terminal member 
           53  First terminal welding part 
           53   g  Recess 
         P Axis line 
         X First radial direction 
         Y Second radial direction 
       
     
       DESCRIPTION OF EMBODIMENTS 
       [0061]    A detailed description of a preferred embodiment of a battery  1  embodying the present invention will now be given referring to the accompanying drawings. 
         [0062]    As shown in  FIG. 1 , a first electrode sheet  10  in which a first electrode mixture layer  12  is provided on a surface of a strip-shaped first metal foil  11  is first prepared. This first electrode sheet  10  includes a first electrode-forming portion  14  and a first metal portion  13  adjacent to the first electrode-forming portion  14 . The first electrode-forming portion  14  extends along one side  10   b  of the first metal foil  11  extending in a longitudinal direction (a lateral direction in  FIG. 1 ) and is constituted of a part of the first metal foil  11  and a first electrode mixture layer  12 . The first metal portion  13  is made of the first metal foil  11  without including the first electrode mixture layer  12  and extends along the side  10   b  in the longitudinal direction. 
         [0063]    The first metal foil  11  is for example made of copper. The first electrode mixture layer  12  is constituted of a first electrode active material, a binder, and others. The first electrode active material is for example lithium nickel oxide. 
         [0064]    As shown in  FIG. 2 , furthermore, a second electrode sheet  20  in which a second electrode mixture layer  22  is provided on a surface of a strip-shaped second metal foil  21  is prepared. This second electrode sheet  20  includes a second electrode-forming portion  24  and a second metal portion  23  adjacent to the second electrode-forming portion  24 . The second electrode-forming portion  24  extends along one side  20   b  of the second metal foil  21  extending in a longitudinal direction (a lateral direction in  FIG. 2 ) and includes a second metal foil  21  and a second electrode mixture layer  22 . The second metal portion  23  is made of the second metal foil  21  without including the second electrode mixture layer  22  and extends along the side  20   b  in the longitudinal direction. 
         [0065]    The second metal foil  21  is for example made of aluminum. The second electrode mixture layer  22  is constituted of a second electrode active material, a binder, and others. The second electrode active material is for example natural graphite. 
         [0066]    As shown in  FIG. 3 , successively, the first electrode sheet  10 , a separator  30 , the second electrode sheet  20 , and another separator  30  are laminated in this order. Concretely, they are laminated in such a manner that the first metal portion  13  of the first electrode sheet  10  and the second metal portion  23  of the second electrode sheet  20  are located opposite in a width direction (a vertical direction in  FIG. 3 ) so that the first metal portion  13  does not overlap the separators  30  and the second electrode sheet  20  and the second metal portion  23  does not overlap the separators  30  and the first electrode sheet  10 . Then, the laminated first electrode sheet  10 , separator  30 , second electrode sheet  20 , and separator  30  are wound in a cylindrical form around a cylindrical winding core  45 . 
         [0067]    After the above winding, the winding core  45  is removed. As shown in  FIG. 4 , the electrode body  40  is thus formed to include a power generating part  42 , a first metal winding part  44 , and a second metal winding part  46 . The power generating part  42  includes the first electrode-forming portion  14  of the first electrode sheet  10  and the second electrode-forming portion  24  of the second electrode sheet  20 , both electrode-forming portions  14  and  24  being laminated by interposing the separator  30  therebetween and wound around the axis line P into a cylindrical form. The first metal winding part  44  is adjacent to the power generating part  42  on one side (on a right side in  FIG. 4 ) in the axis direction and is constituted of the wound first metal portion  13 . The second metal winding part  46  is adjacent to the power generating part  42  on the other side (on a left side in  FIG. 4 ) in the axis direction and is constituted of the second metal portion  23 . 
         [0068]    As shown in  FIG. 5 , a first current collecting terminal member (a “terminal member”)  50  is prepared for collecting electric charge of the first electrode sheet  10 . This terminal member  50  includes a first terminal welding part  53  to be placed on the radial inside of the first metal winding part  44  and welded to the first metal winding part  44 , a screw part  55  formed with male threads, and a flange part  57  located between the first terminal welding part  53  and the screw part  55 . The terminal member  50  is preferably made of the same material as that of the first metal foil  11 . For example, when the first metal foil  11  is made of a copper foil, the terminal member  50  is also preferably made of copper. 
         [0069]    In a deforming step, subsequently, as shown in  FIG. 6 , the first terminal welding part  53  of the terminal member  50  is inserted in the radial inside of the first metal winding part  44 , thereby deforming the first metal winding part  44 . 
         [0070]    Herein,  FIG. 7  is a sectional view (taken along a line B-B in  FIG. 6 ) of the first metal winding part  44  taken along a direction perpendicular to the axis line P, in which the first terminal welding part  53  is placed inside in the radial direction of the winding part  44  (see  FIG. 6 ). As shown in  FIG. 7 , the winding part  44  includes a pair of first metal welding portions  44   b  and  44   c  to be welded to the first terminal welding part  53 . The first metal welding portion  44   b  and the first metal welding portion  44   c  are opposed to each other in a first radial direction X of the winding part  44 . Furthermore, the winding part  44  includes a pair of first metal perpendicularly intersecting portions  44   d  and  44   e  opposed to each other in a second radial direction Y perpendicular to the first radial direction X. 
         [0071]      FIG. 8  shows a sectional view taken along a line C-C in  FIG. 6 . In  FIGS. 7 and 8 , the inner periphery C 1  of the first metal winding part  44  in which the first terminal welding part  53  is not yet placed on the radial inside of the winding part  44  (i.e., before deformation thereof) is indicated by a broken line. 
         [0072]    As shown in  FIG. 7 , when the first terminal welding part  53  placed on the radial inside of the first metal winding part  44  is viewed in section taken along a perpendicular direction to the axis line P, the first terminal welding part  53  has a shape including a section  53   b  having a maximum size Q in the second radial direction Y is larger than an inside diameter D 1  of the not-yet-deformed winding part  44  and a maximum size R in the first radial direction X is smaller than the inside diameter D 1  of the not-yet-deformed winding part  44 . As shown in  FIG. 8 , furthermore, when the first terminal welding part  53  placed on the radial inside of the winding part  44  is viewed in section taken along in a perpendicular direction to the axis line P, the first terminal welding part  53  has a shape including a section  53   c  having a maximum size H in the second radial direction Y is larger than the inside diameter D 1  of the not-yet-deformed winding part  44  and a maximum size K in the first radial direction X is smaller than the inside diameter D 1  of the not-yet-deformed winding part  44 . 
         [0073]    Accordingly, the first terminal welding part  53  having the above shape is inserted in the radial inside of the first metal winding part  44 , exerting a radially-outward force on the first metal perpendicularly intersecting portion  44   d  in the second radial direction (upward in  FIG. 7 ) and exerting a radially-outward force on the first metal perpendicularly intersecting portion  44   e  in the second radial direction (downward in  FIG. 7 ). This can enlarge the inside diameter of the first metal winding part  44  in the second radial direction. Thus, the parts of the first metal foil  11  forming the perpendicularly intersecting portion  44   d  can be moved outward in the second radial direction (upward in  FIG. 7 ) and the parts of the first metal foil  11  forming the perpendicularly intersecting portion  44   e  can be moved outward in the second radial direction (downward in  FIG. 7 ). 
         [0074]    In a foil collecting step and a resistance welding step mentioned later, when the pair of first metal welding portions  44   b  and  44   c  are pressed inward in the first radial direction to bring the pair of first metal welding portions  44   b  and  44   c  in pressure contact with the first terminal welding part  53 , the above deformed state allows the parts of the first metal foil  11  forming the pair of first metal perpendicularly intersecting portions  44   d  and  44   e  to easily move together outward in the second radial direction. 
         [0075]    According to the deforming method in the present embodiment, the first metal winding part  44  is unlikely to buckle during deformation. In addition, when the parts of the first metal foil  11  forming the pair of first metal perpendicularly intersecting portions  44   d  and  44   e  are moved outward together in the second radial direction, the pair of first metal welding portions  44   b  and  44   c  are moved inward in the first radial direction. Thus, the first metal welding portions  44   b  and  44   c  can be brought close to the first terminal welding part  53 . 
         [0076]    In the foil collecting step and the resistance welding step mentioned later, while the pair of first metal welding portions  44   b  and  44   c  are pressed inward in the first radial direction to be pressed against the first terminal welding part  53 , the first metal foil  11  forming the first metal winding part  44  can be prevented from buckling. In the deforming step in the present embodiment, the cylindrical first metal winding part  44  can be deformed into an elliptic form having an inside diameter in the first radial direction X shorter than an inside diameter in the second radial direction Y (see  FIGS. 7 and 8 ). 
         [0077]    Herein,  FIG. 9  shows a section  53   d  of the first terminal welding part  53  placed on the radial inside of the first metal winding part  44  and taken along the second radial direction so as to pass the axis line P. As shown in  FIG. 9 , the size of the section  53   d  in the second radial direction Y is determined such that a size F at a side  53   e  closest to the power generating part  42  is equal to or less than the inside diameter D 1  of the not-yet-deformed first metal winding part  44 . The size of the section  53   d  in the second radial direction Y is larger as it is farther from the power generating part  42  in the axis direction (it is closer to a right side along the axis line P in  FIG. 9 ). A size H at a farthest side  53   f  from the power generating part  42  in the axis direction is larger than the inside diameter D 1  of the not-yet-deformed first metal winding part  44 . 
         [0078]    The use of the first current collecting terminal member  50  including the first terminal welding part  53  having the above shape makes it easy to smoothly insert the welding part  53  in the radial inside of the first metal winding part  44 . Additionally, as the welding part  53  is inserted in the winding part  44 , the force acting on the winding part  44  is gradually increased. Accordingly, the parts of the first metal foil  11  forming the winding part  44  are less broken as compared with when a large force is abruptly applied thereon. 
         [0079]    In the foil collecting step, thereafter, while the first terminal welding part  53  is placed on the radial inside of the deformed first metal winding part  44 , the first metal welding portions  44  are pressed inward in the first radial direction. 
         [0080]    Concretely, as shown in  FIG. 10 , a press part  4   c  of the foil collecting device  3  placed outside of the first metal welding portion  44   c  in the first radial direction (on an upper side in  FIG. 10 ) is moved inward in the first radial direction (downward in  FIG. 10 ) toward the first metal winding part  44 . In sync with this, a press part  4   b  of the foil collecting device  3  placed outside of the first metal welding portion  44   b  in the first radial direction (on a lower side in  FIG. 10 ) is moved inward in the first radial direction (upward in  FIG. 10 ). 
         [0081]    As shown in  FIG. 11 , accordingly, the pair of first metal welding portions  44   b  and  44   c  are pressed inward in the first radial direction, thereby closely collecting parts of the first metal foil  11  forming the first metal welding portions  44   b  and  44   c  inward in the first radial direction by decreasing clearances between the parts of the first metal foil  11  in the first radial direction X. 
         [0082]    Before the resistance welding mentioned later, therefore, the parts of the first metal foil  11  forming each of the first metal welding portions  44  are collected inward in the first radial direction by decreasing the clearances between the parts of the metal foil  11  in the first radial direction X, so that the resistance welding can be appropriately performed. In the later resistance welding step, particularly, when the first metal welding portions  44   b  and  44   c  are respectively pressed inward in the first radial direction, the first metal winding part  44  is unlikely to be deformed and therefore the first metal foil  11  can be further prevented from buckling. 
         [0083]    In the deforming step, before the foil collecting step, the parts of the first metal foil  11  forming each of the first metal perpendicularly intersecting portions  44   d  and  44   e  are moved outward in the second radial direction. In the foil collecting step, accordingly, when the first metal welding portions  44   b  and  44   c  are pressed inward in the first radial direction, the parts of the first metal foil  11  forming the first metal perpendicularly intersecting portions  44   d  and  44   e  can be easily moved together outward in the second radial direction. Therefore, even in the foil collecting step, the first metal foil  11  can be prevented from buckling. 
         [0084]    Meanwhile, in the foil collecting step, when the first metal welding portions  44   b  and  44   c  are respectively pressed inward in the first radial direction, decreasing the clearances between the parts of the first metal foil  11  forming each of the first metal welding portions  44   b  and  44   c  in the first radial direction X to collect the parts of the first metal foil  11  inward in the first radial direction, the parts of the first metal foil  11  forming each of the first metal welding portions  44   b  and  44   c  are apt to elastically move outward in the first radial direction due to spring back. Thus, the clearances between the parts of the first metal foil  11  are widened in the first radial direction. 
         [0085]    In the present embodiment, however, as shown in  FIG. 10 , the first terminal welding part  53  is designed such that a portion to be welded to the first metal welding portions  44   b  and  44   c  of the first metal winding part  44  is formed as a recess  53   g  recessed inward in the first radial direction than other portions when viewed in section taken along a direction perpendicular to the axis line P while the first terminal welding part  53  is placed on the radial inside of the first metal winding part  44 . As shown in  FIG. 11 , the first metal welding portions  44   b  and  44   c  are pressed inward in the first radial direction to be brought in pressure contact with the recess  53   g  of the first terminal welding part  53 . Even after the first metal foil  11  causes outward spring-back in the first radial direction, the parts of the first metal foil  11  forming each of the first metal welding portions  44   b  and  44   c  can be appropriately collected inward in the first radial direction. 
         [0086]    In the foil collecting step of the present embodiment, furthermore, not only the first metal welding portions  44   b  and  44   c  but also the entire of recess-corresponding metal portions  44   g  (a region hatched with broken lines in  FIG. 6) and 44   h  of the first metal winding part  44  each of which faces the recess  53   g  of the first terminal welding part  53  in the first radial direction X are pressed under pressure against the recess  53   g  of the first terminal welding part  53 . Concretely, the press parts  4   b  and  4   c  of the foil collecting device  3  press the recess-corresponding metal portions  44   g  and  44   h  against the recess  53   g  of the first terminal welding part  53  and also the press parts  4   b  and  4   c  are moved in a direction along the axis line P (in a direction perpendicular to a drawing sheet of  FIG. 11 ). In this way, the parts of the first metal foil  11  forming the first metal welding portions  44   b  and  44   c  can be more appropriately collected inward in the first radial direction and also the parts of the first metal foil  11  forming the recess-corresponding metal portions  44   g  and  44   h  can be collected inward in the first radial direction. In the later resistance welding step, accordingly, when the first metal welding portions  44   b  and  44   c  are pressed inward in the first radial direction, the first metal winding part  44  is more unlikely to be deformed. This can further prevent the first metal foil  11  from buckling. 
         [0087]    In the resistance welding step, subsequently, the first metal winding part  44  and the first terminal welding part  53  are resistance-welded to each other. Concretely, as shown in  FIG. 12 , a first electrode  7  and a second electrode  8  of a resistance welding machine  6  press the first metal welding portions  44   b  and  44   c  inward in the first radial direction to bring the first metal welding portions  44   b  and  44   c  in pressure contact with the recess  53   g  of the first terminal welding part  53 . In this state, electric current is supplied between the first electrode  7  and the second electrode  8 , thereby resistance-welding the first metal welding portions  44   b  and  44   c  to the first terminal welding part  53 . 
         [0088]    In the present embodiment, as mentioned above, in the deforming step and the foil collecting step, the parts of the first metal foil  11  forming the first metal winding part  44  are prevented from buckling. In the resistance welding step, furthermore, even when the first metal welding portions  44   b  and  44   c  are brought into pressure contact with the recess  53   g  of the first terminal welding part  53 , the parts of the first metal foil  11  forming the first metal winding part  44  can be prevented from buckling. This can prevent the occurrence of spatters during resistance welding and hence avoid adhesion of foreign matters to the electrode body  40  caused by the occurrence of spatters. The use of this electrode body  40  can therefore restrain entrance of the foreign matters into the battery. Moreover, it is possible to prevent welding failures between the first metal welding portions  44   b  and  44   c  and the first terminal welding part  53  due to a shunt of welding current. 
         [0089]    As shown in  FIG. 13 , thereafter, a disc-shaped lid member  61  is prepared and placed on the flange part  57  of the first current collecting terminal member  50  so that the screw part  55  of the terminal member  50  is inserted in a through hole  61   b  of the lid member  61 . In this state, a nut  65  is threaded on the screw part  55  of the terminal member  50  to fasten the lid member  61  to the flange part  57  of the terminal member  50 . Then, an electrolyte is poured in a battery case  62 . 
         [0090]    Subsequently, the electrode body  40  is inserted in the battery case  62  having a bottom-closed cylindrical shape and also the lid member  61  is put on an open end face  62   c  of the battery case  62  to close the opening of the battery case  62 . It is to be noted that an electrical insulating member not shown is placed between the open end face  62   c  of the battery case  62  and the lid member  61  to electrically insulate between the lid member  61  and the battery case  62 . When the opening of the battery case  62  is closed with the lid member  61 , a second current collecting terminal member (not shown) welded to the second metal winding part  46  contacts with a bottom  62   b  of the battery case  62 . Accordingly, the battery case  62  serves as a second electrode. 
         [0091]    Thereafter, the lid member  61  and the battery case  62  are welded to each other. The battery in this embodiment is thus completed. 
         [0092]    In relation to the battery  1  of the present embodiment,  FIG. 14  shows a sectional view of the first metal winding part  44  taken along a direction perpendicular to the axis line P so as to pass the first metal welding portion  44   c . This view corresponds to a sectional view taken along a line L-L in  FIG. 13 . As shown in  FIG. 14 , the first terminal welding part  53  placed on the radial inside of the first metal winding part  44  and the first metal welding portions  44   b  and  44   c  of the first metal winding part  44  are resistance-welded to each other. In addition, an outside diameter N of the first metal winding part  44  in the first radial direction X in which the first metal welding portion  44   b  faces the first metal welding portion  44   c  is determined to be smaller than an outside diameter M of the first metal winding part  44  in the second radial direction Y perpendicular to the first radial direction X. In such battery, conventionally, a first metal foil would buckle at first metal perpendicularly intersecting portions (portions opposed to each other in the second radial direction perpendicular to the first radial direction) of the first metal winding part. 
         [0093]    On the other hand, in the battery  1  of the present embodiment, as shown in  FIG. 14 , each part of the first metal foil  11  forming the first metal perpendicularly intersecting portions  44   d  and  44   e  is curved to outward bulge in the second radial direction Y. In other words, in the first metal perpendicularly intersecting portions  44   d  and  44   e , the first metal foil  11  does not buckle. Accordingly, when the first metal welding portions  44   b  and  44   c  are resistance-welded to the first terminal welding part  53 , it is possible to prevent adhesion of foreign matters to the electrode body  40  caused by the occurrence of spatters and prevent welding failures between the first metal welding portions  44   b  and  44   c  and the first terminal welding part  53  due to a shunt of welding current. Consequently, the battery  1  of the present embodiment can be provided as a highly reliable battery by restraining entrance of foreign matters into the battery and appropriately welding the first metal winding part  44  and the first terminal welding part  53  to each other. 
       Example 1 and Comparative Example 1 
       [0094]    In Example 1, as mentioned in the embodiment, the deforming step, the foil collecting step, and the resistance welding step are sequentially performed to produce a hundred samples (Samples  1  to  100 ) in each of which the first metal winding part  44  and the first terminal welding part  53  are welded to each other, thereby welding the first current collecting terminal member  50  and the electrode body  40 . The battery  1  is then produced in the manner described in the embodiment. 
         [0095]    It is to be noted that, in Example 1, the first metal winding part  44  is designed to have fifty winding turns. The resistance welding step is conducted under the condition that a welding current value is 7000 A, a welding current application time is 116 ms, and a contact pressure between the first electrode  7  and the second electrode  8  is 100 kgf (980 N). 
         [0096]    In Comparative example 1, a first metal winding part having fifty winding turns as with that in Example 1 is not subjected to the deforming step but is subjected to a foil collecting step different from Example 1 and then the resistance welding step as in Example 1. In this way, a hundred samples (Samples  101  to  200 ) in each of which the first current collecting terminal member and the electrode body are welded to each other are produced. 
         [0097]    Concretely, a first current collecting terminal member  150  used in Comparative example 1 has a first terminal welding part  153  having an almost square pole shape whose cross section is almost square (its maximum size is equal to or less than the inside diameter of a first metal winding part  144 ) in a direction perpendicular to the axis line of the first metal winding part  144  wound in a cylindrical form, as shown in  FIG. 15 . Accordingly, even when the first terminal welding part  153  is inserted in the radial inside of the first metal winding part  144 , the first metal winding part  144  will not be deformed. 
         [0098]    In the foil collecting step in Comparative example 1, furthermore, press parts  104   b  and  104   c  each having a flat plate shape and constituting a foil collecting device  103  are moved radially inward while the first terminal welding part  153  is placed on the radial inside of the first metal winding part  144  as shown in  FIG. 15 . Accordingly, as shown in  FIG. 16 , a pair of first metal welding portions  144   b  and  144   c  are pressed inward in the first radial direction, thereby collecting parts of the first metal foil forming the first metal welding portions  144   b  and  144   c  by decreasing clearances between the parts of the first metal foil in the first radial direction X. Then, the resistance welding step is conducted in the same manner as in Example 1 to produce samples  101  to  200 . 
         [0099]    The samples  101  to  200  in Comparative example 1 are examined about each welded state between each of the first metal welding portions  144   b  and  144   c  and the first terminal welding part  153 . The result thereof shows that every welded state is appropriate. However, each electrode body  140  was examined about adhesion of foreign matters resulting from welding spatters, and adhesion of foreign matters was found in five samples. 
         [0100]    On the other hand, the samples  1  to  100  in Example 1 are examined about each welded state between each of the first metal welding portions  44   b  and  44   c  and the first terminal welding part  53 . The result thereof shows that every welded state is appropriate. Each electrode body  40  was examined about adhesion of foreign matters resulting from welding spatters, and no adhesion of foreign matters was found in each sample. 
         [0101]    It is clear from the above results that the production method according to Example 1 can produce a highly reliable battery by preventing entrance of foreign matters into the battery and appropriately welding the first metal winding part and the first terminal welding part to each other. Furthermore, the battery  1  of Example 1 can be achieved as a highly reliable battery produced by preventing entrance of foreign matters into the battery and the first metal winding part and appropriately welding the first terminal welding part to each other. 
         [0102]    The present invention is explained in the above embodiment and Example 1 but is not limited thereto. It should be understood that the present invention may be embodied in other specific forms without departing from the essential characteristics thereof.