Abstract:
The invention relates to a method for producing magnetic sliders having a permanent protective coating of carbon over the air bearing surface. The method comprises the steps of: (a) depositing a temporary protective coating on a surface of the slider, the temporary protective coating comprising a layer carbon; (b) depositing a photoresist layer onto the temporary protective coating; (c) imagewise exposing the photoresist layer to radiation; (d) developing the image in the photoresist layer to expose the temporary protective coating; (e) transferring the image through the temporary protective coating and into the slider to form the air bearing pattern in the slider; (f) removing the temporary protective coating using nonreactive plasma; and (g) depositing a permanent protective coating comprising a layer of carbon.

Description:
BACKGROUND OF THE INVENTION 
     1. Field of the Invention 
     The present invention relates to an improved method for the manufacture of sliders. More particularly, the invention relates to an improved method for forming the air bearing surface (ABS) of a slider. 
     2. Description of the Background Art 
     Digital magnetic recording devices for data storage generally comprise a thin film magnetic recording disk and a head or transducer which is moved above the surface of the rotating disk to electromagnetically read and write information on the disk. Advanced thin film magnetic recording disks generally comprise a rigid substrate, a magnetic layer such as a cobalt-based metal alloy, a protective amorphous carbon layer and a lubricant layer, such as a perfluoropolyether disposed on the carbon overcoat. 
     During operation of the disk drive system, an actuator mechanism moves the magnetic transducer to a desired radial position on the surface of the rotating disk where the head electromagnetically reads or writes data. Usually, the head is integrally mounted in a carrier or support referred to as a “slider”. A slider generally serves to mechanically support the head and any electrical connections between the head and the rest of the disk drive system. The slider is aerodynamically shaped to glide over moving air and, therefore, to maintain a uniform distance from the surface of the rotating disk, thereby preventing the head from undesirably contacting the disk. 
     Typically, a slider is formed with an aerodynamic pattern of protrusions (air bearing pattern) on the air bearing surface (ABS) which enable the slider to fly at a constant height close to the disk during operation of the disk drive. 
     The recording density of a magnetic disk drive is limited by the distance between a transducer and the magnetic media. One goal of air bearing slider design is to “fly” a slider as closely as possible to a magnetic medium while avoiding physical impact with the medium. Smaller spacings, or “fly heights”, are desired so that the transducer can distinguish between the magnetic fields emanating from closely spaced regions on the disk. 
     In manufacturing such read/write heads, a large number of sliders are fabricated from a single wafer having rows and columns of the magnetic transducers deposited simultaneously on the wafer surface using semiconductor-type process methods. In one process embodiment, after deposition of the heads is complete, the wafer is cut into four quadrants. Each quadrant is then bonded to a lapping fixture and grounded on a lapping plate to provide accurate head dimensions. After lapping, single row bars of sliders in side by side orientation are cut from the wafer quadrant. These row bars can optionally be lapped again, and the ABS design is formed in each slider using art-known lithographic and dry etching techniques. The ABS is formed by coating the slider surface with a thick layer of protective photoresist, imaging the photoresist with radiation; development of the ABS image in the photoresist and dry etching (transferring) the ABS image into the body of the slider. After the ABS has been formed, the remaining photoresist is removed by solvent or soda blast. Lastly, the row bars are adhered to suitable tape; and each bar is diced, i.e., separated with a diamond-cut saw into individual sliders, each having a magnetic head terminating at the ABS. Each slider is then attached to an actuator for use in a magnetic disk drive. 
     It has been determined that damage can occur to the thin film magnetic sensor during the above described process steps. Grill et al. in U.S. Pat. No. 5,159,508, disclose a dry process for forming a protective coating over the slider prior to the lithographic process. The protective coating comprises two layers, the first layer an adhesion layer, e.g. silicon and a second layer of amorphous carbon. The ABS is then formed in the slider covered with the protective coating. Grill teaches that protective coating should be permanently retained on the slider because the top layer of protective carbon will protect the slider from mechanical damage during subsequent normal operation of the slider. Unfortunately, the carbon layer of the protective coating is, in some cases, damaged during the slider fabrication process. This damage to the protective carbon layer can permit corrosion of the sensor. The damage to the sensor can result in diminished signal amplitude during operation of the disk drive. Chang et al. U.S. Pat. No. 5,271,802, teaches a similar process where the top layer of the protective coating of the slider is silicon oxide. Although silicon is not as easily damaged as carbon during the etching process, silicon oxide is not a suitable protective coating for sliders because of its relatively poor wear resistance. 
     Therefore, there is still a need in this art for a slider manufacturing process which results in sliders having suitable permanent protective coatings over the ABS. 
     It is, therefore, an object of the present invention to provide an improved method for the manufacturing of magnetic sliders. Other objects and advantages will become apparent from the following disclosure. 
     SUMMARY OF THE INVENTION 
     The present invention relates to a method for producing magnetic sliders having a permanent protective coating of carbon over the ABS. The method generally comprises the steps of: (a) depositing a protective layer on a surface of the slider preferably a carbon layer; (b) depositing a photoresist layer onto the first layer of carbon; (c) imagewise exposing the photoresist layer to radiation; (d) developing the image in the photoresist layer to expose the first layer of carbon; (e) transferring the image through the first layer of carbon and into the slider to form the air bearing pattern in the slider; (f) removing the remaining photoresist layer; (g) removing the remaining first layer of carbon from the slider with non reactive plasma; and (h) depositing a second layer of carbon on the surface of the slider to form a permanent protective coating over the ABS. 
     The method provides a slider having uniform protective coating of carbon over the ABS surface of the slider. 
     A more thorough disclosure of the present invention is presented in the detailed description which follows and the accompanying figures. 
    
    
     BRIEF DESCRIPTION OF THE DRAWINGS 
     FIG. 1 is a perspective view of a slider; 
     FIG. 2 is a perspective view of a wafer element having a plurality of magnetic heads fabricated thereon in rows and depicting the detailed structure of a row and a slider. 
    
    
     DETAILED DESCRIPTION OF THE INVENTION 
     The present invention relates to an improved method for the manufacture of sliders. Referring to FIG. 1, there is shown a typical thin film head slider  30  with a negative pressure ABS. The slider  30  is generally rectangular in shape. It consists of two portions, i.e., a slider portion and a head portion, formed on an end face of the slider portion. Typically, this end face of the slider constitutes the slider trailing surface when the slider is suspended above and adjacent a rotating recording disk. 
     The slider portion  34 , which constitutes the bulk of the thin film head slider  30 , is made of a ceramic material such as Al 2 O 3 -TiC (e.g., N58), or other suitable material. In one embodiment, the ABS of the slider comprises, as shown, three dual depth step-pads  35  having top surface  39  and disposed on a recessed face  37  of the slider  30 . Two step-pads are at the leading edge  36  and one is at the trailing edge  12 . The head portion  10  is suitably located on the single step-pad near the trailing surface  38  of the slider  30 . The step pads  35  and the recessed face  37  are all important structural features which enable the head portion  10  to glide a short distance above the surface of a magnetic disk. A variety of other ABS designs are known in the art, such as disclosed in U.S. Pat. No. 5,650,893 (for negative pressure design) and U.S. Pat. No. 4,894,740 (for positive pressure design), the disclosures of which are incorporated herein by reference. 
     The head is typically encapsulated in a thin layer of alumina deposited on the trailing surface of the slider. Suitably, it is a magnetoresistive read element and inductive head for writing data. Electrical terminal pads  41  provide electrical connection for the magnetic head element. 
     Referring to FIG. 2, the above-described thin film head slider  30  has been fabricated from a preprocessed wafer  50 , as shown in FIG. 2, or from a wafer quadrant. The wafer  50  comprises a wafer substrate  44  which is suitably covered by thin layer  40  of alumina. The magnetic head device such as an MR head is formed in the layer  40 . The magnetic heads are arranged in rows and columns are suitably identically oriented. Typically, the thickness of the wafer substrate  44  is equal to the length of the finished slider  30 . 
     The wafer  50  comprises a matrix of slider units  51  arranged in rows  53  which when fully processed will become sliders  30 . The view shown in FIG. 2 is an end view of the individual slider units  51  with the magnetic heads having been formed on the ends of the slider units  51 . As shown in FIG. 2, a plurality of identical row bars  53 , each comprising a row of identical slider units  51 , together with superfluous sections, such as top and bottom sections  57  where no slider units are formed constitute the wafer  50 . Slider row  53  has trailing surface  41  and a top surface  45  which will be modified to form the ABS. The wafer may be fabricated to contain any desirable number of rows  53  of slider units  51  and any desirable number of slider units  51  in each row, depending on the size of the wafer and the size of the sliders. 
     The slider unit  51  shown in FIG. 2 is identical with the finished slider  30  shown in FIG. 1, except that the ABS is not yet formed and the throat height for the poles and the head elements are greater in the unfinished slider unit  51 . The wafer is preferably cut into four quadrants and each quadrant is lapped to obtain the desired throat and element heights. The desired throat heights and head element heights are achieved by the provision of lapping guides. The lapping guides are then used as indicators of element height during the lapping process for the slider units  51 . The final height of the element may be determined by measuring the resistance of the element itself. See, for example, U.S. Pat. Nos. 4,914,868 and 4,912,883, the disclosure of which are incorporated herein by reference for all purposes. 
     When fabrication of the magnetic heads on the sliders is complete at the quadrant level, the quadrant is sliced into rows of the slider. In an alternative embodiment, the wafer can be first sliced into rows, and then the individual rows can be lapped to achieve desired throat and element heights. 
     According to the present invention, at a time after the heads are lapped to the selected throat height and before the ABS pattern is produced on the slider, a temporary protective coating is formed over the slider. The temporary protective coating suitably comprises a layer of carbon, suitably an amorphorus hydrogenated carbon. The carbon layer is a sacrificial layer effective to protect the thin film magnetic head during the processing of the head/slider to form the pattern on the ABS. 
     The layer of hydrogenated amorphous carbon is deposited to a thickness of about 40-150 angstroms. A layer of hydrogenated amorphous carbon as little as 50 angstroms thick has been shown to provide a significant improvement in corrosion protection. However, a thicker layer (e.g. greater than 100 angstroms) is preferable since it provides increased protection. Further, since the layer is removed in the final product, its thickness is chosen based on its corrosion protection rather than the permissible increase in spacing between the magnetic head and the magnetic recording medium. 
     The layer of the protective carbon coating can be deposited by any suitable technique such as ion beam deposition, CVD or sputtering. e.g., RF magnetron sputtering. Optionally, prior to deposition of the protective carbon, the surface of the slider is cleaned by art known means, e.g. sputtering. 
     The deposition parameters of the amorphous hydrogenated carbon layer determine the characteristics of the layer since hydrogen content, density, hardness, and optical density are a function of the sputtering power, the percent hydrogen in the argon carrier gas and the pressure. Suitable deposition technique and conditions are known to those skilled in the art. 
     In an alternative embodiment, a thin adhesion layer of silicon is first applied to the surface of the slider to enhance the adhesion of the carbon layer to the slider. The silicon layer is suitably about 10 to about 50 Å thick. 
     A thick layer of a photoresist material is then deposited over the protective layer. The photoresist material is exposed through an appropriate mask in a pattern of the chosen ABS rail configuration, developed and removed in the exposed areas. The remaining photoresist material serves as a mask for forming the chosen rail pattern on ABS. 
     The masked row of sliders is then subjected to a suitable material removal process such as by sputter etching, by reactive ion etching, by ion milling, or laser etching. (see U.S. Pat. No. 4,301,353). Preferably, the etching is done by ion milling or reactive etching. During the etching process, the unmasked portion of the temporary protective coating is removed first, and the underlying area of the slider is then removed to a depth which is chosen to provide the desired flying characteristics for the slider. The remainder of the photoresist mask is then removed by a suitable solvent or by a soda blast. For more complex ABS patterns with multiple step levels, the lithographic etch step may be repeated. 
     The layer of temporary protective coating acts as a sacrificial layer to protect the sensor during the slider processing, e.g. lithographic/etch/resist removal process. At the end of processing, the temporary protective layer is suitably removed selectively from slider by art known means. The temporary protective coating of carbon is removed with a non-reactive plasma which does not damage the slider or its head. A preferred non-reactive plasma is a argon/hydrogen plasma, preferably comprising about 4% of hydrogen. 
     After the temporary protective layer has been removed from the slider, a new permanent protective layer is applied. The permanent protective layer is suitably a carbon layer, suitably a diamond like carbon layer, suitably deposited in an art known manner similar to the original sacrificial carbon layer. In an alternative embodiment, a thin silicon adhesion layer may be first deposited on the slider. Since the permanent carbon layer is never exposed to the harsh process steps, it is in pristine condition without any process damage. 
     The permanent carbon layer is therefore effective during subsequent normal operation of the head in a magnetic disk file, for example, to protect the head and the ABS from mechanical wear caused by inadvertent contact between the head/slider and the magnetic recording medium during flying. In addition to mechanical wear, the carbon layer also is effective to protect the variety of materials in the magnetic head that are attacked by the normal constituents of the atmosphere from oxidation and corrosion in normal operation of the system. 
     After processing is complete, the row of sliders is then suitably debonded from the carrier and bonded to an adhesive tape for the dicing process where vertical cuts are made in the row to separate each individual slider. 
     The method of the present invention results in sliders having a suitable permanent protective carbon coating over the top portions of the ABS of the slider such as the rails. The process also provides protection to the slider and the sensitive thin film magnetic elements during manufacturing to provide greater yields. Although this invention has been described with respect to specific embodiments, the details thereof are not to be construed as limitations, for it will be apparent that various embodiments, changes and modifications may be resorted to without departing from the spirit and scope thereof; and it is understood that such equivalent embodiments are intended to be included within the scope of this invention.