Abstract:
A novel material of phenanthrenyl imidazole is applied to a solar cell. A phenanthrenyl-imidazole moiety is introduced to reduce a power band of a polymer, so that a photocurrent and an optoelectrical transformation efficiency are improved. Thus, a polymer having the novel material is very suitable to be used in a solar cell to acquire a high optoelectrical transformation efficiency.

Description:
FIELD OF THE INVENTION 
       [0001]    The present invention relates to phenanthrenyl imidazole; more particularly, relates to a phenanthrenyl-imidazole moiety reducing a band gap of a polymer to improve a photocurrent density and an optoelectrical transformation efficiency. 
       DESCRIPTION OF THE RELATED ARTS 
       [0002]    In recent years, there are a number of ways to improve power conversion efficiencies of solar cell, such as, varying annealing temperatures and time for lowering electrical resistance of devices and introducing lowered work function electrode. On the other hand, copolymerization of different conjugated monomer is investigated to change polymer structure. The material used is mainly poly-(3-hexylthiophene) (P3HT) to improve hot treatment and structure. In addition, an electron transferring moiety is introduced to a main chain of thiophene to obtain a better conjugated polymer. Therein, P3HT has an average photocurrent density of 10 mA/cm 2 ; and a highest photocurrent density is 12 mA/cm 2 . However, the material is insufficient and the photocurrent density is still low. Hence, the prior arts do not fulfill users&#39; requests on actual use. 
       SUMMARY OF THE INVENTION 
       [0003]    The main purpose of the present invention is to reducing a band of poly(3-octyl-thiophene) (P3OT) and to improve its transference capacity. 
         [0004]    To achieve the above purpose, the present invention is a soluble phenanthrenyl imidazole for photo-electrical conversion of a solar cell, where a first monomer and a second monomer, having phenanthrenyl imidazole, are obtained through syntheses and then are polymerized to obtain a thiophene polymer of phenanthrenyl imidazole through a Grignard metathesis (GRIM), having a chemical structure of 
         [0000]    
       
                 
         
             
             
         
       
     
         [0000]    the first monomer is 2,5-dibromo-3-octylthiophene; the second monomer is 2,5-dibromo-phenanthrenyl imidazole thiophene; and the GRIM has a maximum adding ratio of 80% of the second monomer and 20% of the first monomer. Accordingly, a novel soluble phenanthrenyl imidazole for photo-electrical conversion of a solar cell is obtained. 
     
     
       BRIEF DESCRIPTIONS OF THE DRAWINGS 
         [0005]    The present invention will be better understood from the following detailed description of the preferred embodiment according to the present invention, taken in conjunction with the accompanying drawings, in which 
           [0006]      FIG. 1  is the view showing the syntheses of the monomers; 
           [0007]      FIG. 2A  and  FIG. 2B  are the views showing the GRIM; 
           [0008]      FIG. 3A  is the view showing the spectra obtained through the FTIR; 
           [0009]      FIG. 3B  is the view showing the measurement obtained through the cyclic voltammeter; 
           [0010]      FIG. 4A  is the view showing the spectra obtained through the NMR; 
           [0011]      FIG. 4B  is the enlarged view showing the absorption peaks; 
           [0012]      FIG. 5A  is the view showing spectra of ultra violet-visible light for the polymer in the liquid state; 
           [0013]      FIG. 5B  is the view showing the spectra of ultraviolet-visible light for the polymer in the solid state; 
           [0014]      FIG. 6A  is the view showing the PL intensity for the polymer in the liquid state; 
           [0015]      FIG. 6B  is the view showing the PL intensity for the polymer in the solid state; 
           [0016]      FIG. 6C  is the view showing the maximum wavelength and the optical band for the polymer; 
           [0017]      FIG. 7A  is the view showing the photocurrents of the solar cell; and 
           [0018]      FIG. 7B  is the view showing the transformation ratios of the polymer solar cell. 
       
    
    
     DESCRIPTION OF THE PREFERRED EMBODIMENT 
       [0019]    The following description of the preferred embodiment is provided to understand the features and the structures of the present invention. 
         [0020]    The present invention is a soluble phenanthrenyl imidazole for photo-electrical conversion of a solar cell, where a first monomer and a second monomer, which has phenanthrenyl imidazole, are obtained through syntheses; and then are polymerized through a Grignard metathesis (GRIM) to obtain a thiophene polymer of phenanthrenyl imidazole having a chemical structure of 
         [0000]    
       
                 
         
             
             
         
       
     
         [0021]    Please refer to  FIG. 1 ,  FIG. 2A  and  FIG. 2B , which are a view showing syntheses of monomers; and views showing GRIM. As shown in the figure, a thiophene polymer of phenanthrenyl imidazole according to the present invention is made through the following steps: 
         [0022]    (a) 3-bromothiophene [11] and C 8 H 17 MgBr [12] are reacted to obtain a first product [15], coordinated with a catalyzer (Ni(dppp)Cl 2 ) [13] and ether [14], where the first product [15] is 3-octyl-thiophene and has a production ratio of 88%. 
         [0023]    (b) The first product [15] and two equivalent N-bromosuccinimide (NBS) [16] are reacted to obtain a first monomer [17], where the first monomer [17] is poly(3-octyl-thiophene) (P3OT) and has a production ratio of 92%. 
         [0024]    (c) thiophene-3-carboxaldehyde [18], aniline [19] and phenanthrenequinone [20] are reacted to obtained a second product [23] with an acetic acid (CH 3 COOH) [21] as a solvent for ammonium acetate (CH 3 COON H 4 ) [22], where the second product [23] is 1-Phenyl-2-(3-thioenyl)-1H-phenanthro-dimidazole and has a production ratio of 90%. 
         [0025]    (d) The second product [23] and two equivalent NBS [16] are reacted to obtain a second monomer [24] having a phenanthrenyl-imidazole moiety, where the second monomer [24] is phenanthrenyl imidazole thiophene and has a production ratio of 95%; and the functionality of phenanthrenyl-imidazole moiety is similar to oxidiazo-moiety, triazole-moiety, quinoxaline-moiety, imidazole-moiety or triazine-moiety 
         [0026]    (e) And then, CH 3 MgBr [24] is obtained as a solvent for polymerizing the first monomer [17] and the second monomer [24] through a GRIM to obtain a thiophene polymer of phenanthrenyl imidazole [28], where the GRIM has a maximum adding ratio of 80% of the second monomer and 20% of the first monomer. 
       EXAMPLE 
     Preparing a Monomer Having a Structure of ITO/PEDOT:PSS/Polymers:PCBM(1:2,w/w)/Ca/Al 
       [0027]    An indium tin oxide (ITO) glass is precleaned with oxygen plasma prior to use. A polymer/PCBM([6,6]-phenyl C61-butyric acid methyl ester) is solved into a dichlorobenzene solution to 15 mg/mL at 40 Celsius degrees; and then is spin-coated with a thickness of 80 nanometers (nm) on the ITO glass at 1500 rpm. Calcium and aluminum are vacuum-deposited under a pressure below 10 −6  torr, having a thickness of 30 nm and 100 nm respectively. Thus, a device having a material of phenanthrenyl imidazole is obtained. 
         [0028]    Please further refer to  FIG. 3A  and  FIG. 3B , which are views showing spectra obtained through an Fourier Transform InfraRed spectroscopy (FTIR) and a measurement obtained through a cyclic voltammeter. As shown in  FIG. 3A , a second monomer and a synthesized polymer are measured through an FTIR. And it shows that sharp absorption bands at 3067 cm −1  and 3127 cm −1  for the second monomer is corresponding to β-CH stretching absorption of the thiophene Curve at 820 cm −1  for P00 [34] and P37 [33] are corresponding to CH out-of-plane deformation absorption. In the other hand, a curve at 783 cm −1 [35 ] for the second monomer is corresponding to α-CH bending absorption, which is absent at 783 cm −1  for P00 and P37. P37 has a long chain of CH 3 —CH 2  between 2800 and 3000 cm −1 . And curves at 727 cm −1  for the second monomer [36], P00 [38] and P37 [37] have deformation absorptions corresponding to C—S—C ring. Thus, phenanthrenyl-imidazole moiety changes highest occupied molecular orbitals (HOMO) and lowest unoccupied molecular orbitals (LUMO). As shown in  FIG. 3B , the HOMO and the LUMO are obtained by the following formula: 
         [0000]        E   HOMO   =−E   ox −4.4 eV and 
         [0000]        E   LUMO   =−E   red −4.4 eV, 
         [0029]    where E ox  and E red  are the onset potentials of the oxidation and reduction peaks. A band gap exists between the E HOMO and the E LUMO . After introducing the phenanthrenyl-imidazole moiety, the HOMOs for P00 to P82 are increased from −5.40 electron volts (eV) to −5.15 eV; and the LUMOs are decreased from −3.75 eV to −3.55 eV. Thus phenanthrenyl-imidazole moiety increases effective conjugation length of polymers like P00 and P82 by improving coplanarity. 
         [0030]    Please further refer to  FIG. 4A  and  FIG. 4B , which are a view showing spectra obtained through Nuclear Magnetic Resonance (NMR) and an enlarged view showing absorption peaks. As shown in spectra obtained through NMR, absorption peaks at 6.98 ppm for P00 [41], P 37 [42], P 55 [43], P82 [44] show regio-regularity. In the NMR figure for the polymers, only 6.98 ppm peak and no other peak nearby in the spectra shows that the polymers possess a high head-to-tail configuration. The second monomer contributes absorptions at 7.2 ppm˜8.2 ppm and 8.2 ppm˜9.2 ppm; and the first monomer contributes an absorption at 0.3 ppm˜3.0 ppm. 
         [0031]    Please further refer to  FIG. 5A  and  FIG. 5B , which are views showing spectra of ultra violet-visible light for the polymers in a liquid state and in a solid state. As shown in the figures, maximum absorptions in a liquid state increases from 439 nm [51] to 478 nm [52]; and maximum absorptions in a solid state increases from 520 nm [53] to 556 nm [54]. Thus it shows band of the copolymer has an obvious decrease. 
         [0032]    Please further refer to  FIG. 6A ,  FIG. 6B  and  FIG. 6C , which are views showing photoluminescence (PL) intensities for polymers in liquid state and in solid state and a view showing a maximum wavelength and an optical band for the polymer. As shown in the figures, after introducing phenanthrenyl-imidazole moiety, PL intensities for polymers decrease as amounts of phenanthrenyl-imidazole moiety increase. It shows, after main chain of a polymer is photo-excited, electric charges are transferred by the phenanthrenyl-imidazole moiety to increase photo-guiding charge transfer or energy transfer; charge transfer is rapid enough to compete with recombination of the electrons and holes; and thus the PL intensity is decreased. As shown in  FIG. 6C , values for maximum absorption wavelength and optical band are obtained. By introducing phenanthrenyl-imidazole moiety, conjugation length of the polymer is increased so that the maximum absorption wavelength is increased from 520 nm to 556 nm and the optical band is reduced from 1.89 eV to 1.77 eV. 
         [0033]    Please refer to  FIG. 7A  and  FIG. 7B , which are a view showing photocurrents of a solar cell; and a view showing transformation ratios of the solar cell. As shown in the figures, a solar cell is prepared, which has a structure of ITO/PEDOT:PSS/Polymers:PCBM(1:2,w/w)/Ca/Al. The solar cell is measured for its photocurrent. Therein, following the increase in amount of the phenanthrenyl-imidazole moiety, photocurrent intensities are greatly increased from 10.9 mA/cm 2  to 17.7 mA/cm 2 ; open circuit voltages (Voc), from 0.59 volts (V) to 0.69V; fill-factors (FF), from 23.6% to 31.1%; and, maximum power conversion efficiency, from 1.52% to 3.48%, corresponding to P00 to P82 respectively. The open circuit voltage of the solar cell is influenced by not only a difference between LUMO of the electron acceptor and HOMO of the electron donor but also the FF. The lower Voc means better miscibility and interaction between the polymer and PCBM. Short circuit is increased with the introduction amount of the phenanthrenyl-imidazole moieties due to the increasing of the electron mobility of the copolymers. The FFs are low due to thick films, short drift length of excitons, or great inner resistance. The power conversion efficiency increases from 1.52% for P00 to 3.48% for P82 owing to the higher electron mobility of P82 than that of P00. Therefore, the present invention shows that the introduction of the phenanthrenyl-imidazole moieties onto the copolymer are promising polymer materials for application in solar cells. 
         [0034]    To sum up, the present invention is a soluble phenanthrenyl imidazole for photo-electrical conversion of a solar cell, where a current density of a solar cell is greatly improved while a high photoelectrical transformation ratio remains; and thus a breakthrough happens to a solar cell promising a better efficiency in photoelectrical transformation. 
         [0035]    The preferred embodiment herein disclosed is not intended to unnecessarily limit the scope of the invention. Therefore, simple modifications or variations belonging to the equivalent of the scope of the claims and the instructions disclosed here in for a patent are all within the scope of the present invention.