Abstract:
In one aspect, the invention encompasses a semiconductor processing method comprising contacting a surface with a liquid solution comprising at least one fluorine-containing species and a temperature of at least about 40° C. In another aspect, the invention encompasses a method of passivating a silicon-comprising layer comprising contacting the layer with a liquid solution comprising hydrogen fluoride and a temperature of at least about 40° C. In yet another aspect, the invention encompasses a method of forming hemispherical grain polysilicon comprising: a) forming a layer comprising substantially amorphous silicon over a substrate; b) contacting the layer comprising substantially amorphous silicon with a liquid solution comprising fluorine-containing species and a temperature of at least about 40° C.; c) seeding the layer comprising substantially amorphous silicon; and d) annealing the seeded layer to convert at least a portion of the seeded layer to hemispherical grain polysilicon.

Description:
RELATED PATENT DATA 
     This patent is a divisional application of U.S. patent application Ser. No. 09/018,228, which was filed on Feb. 3, 1998 now U.S. Pat. No. 6,083,849, and is hereby incorporated in its entirety by reference, which is a continuation-in-part of U.S. patent application Ser. No. 08/659,145, filed on Jun. 5, 1996 now U.S. Pat. No.5,783,495, and hereby incorporated in its entirety by reference; which is a continuation-in-part of U.S. patent application Ser. No. 08/559,188, filed on Nov. 13, 1995 now abandoned and hereby incorporated in its entirety by reference. 
    
    
     TECHNICAL FIELD 
     This invention pertains to semiconductor processing methods in which materials are exposed to liquid solutions comprising fluorine-containing species. 
     BACKGROUND OF THE INVENTION 
     Many semiconductor fabrication processes comprise one or more steps wherein a material is exposed to fluorine-containing species. The fluorine-containing species can be, for example, in the form of hydrogen fluoride. An example use of hydrogen fluoride in semiconductor fabrication processes is to strip silicon dioxide from a surface. Another example use of hydrogen fluoride is to passivate a silicon surface (i.e., to react hydrogen with dangling silicon bonds). 
     Passivation of silicon surfaces and/or stripping of silicon dioxide can be utilized to enhance formation of hemispherical grain (HSG) polysilicon. Example HSG polysilicon fabrication processes are described in U.S. Pat. Nos. 5,634,974 and 5,691,228, which are incorporated herein by reference. Generally, the fabrication processes disclosed in such patents comprise forming a layer of amorphous silicon, passivating and/or cleaning the layer of amorphous silicon with hydrofluoric acid, and converting the amorphous silicon to HSG polysilicon. A method of converting amorphous silicon to HSG polysilicon comprises seeding the amorphous silicon by, for example, irradiation or doping, to form nucleation centers for subsequent growth of individual grains of HSG polysilicon. HSG polysilicon is grown from the nucleation centers by annealing the seeded amorphous silicon at, for example, a temperature of from about 200° C. to about 1500° C. and a pressure of from about 1×10 31 8  Torr to about 1 atmosphere for a time of from about one second to about five hours. 
     The hydrofluoric acid treatments utilized in the above-described fabrication of HSG polysilicon either comprise an HF vapor clean, or a dip within an HF solution. If a dip is utilized, the temperature of the dip solution will be about 21.5° C. The dip solution is generally kept within a vessel configured to cool the dip solution to maintain a temperature of about 21.5° C. An advantage of the 21.5° C. temperature is that it is a temperature which has traditionally been used for HF dipping, and accordingly there is a large amount of information available pertaining to appropriate dipping times and conditions for various applications. Another advantage is that the equipment presently manufactured for dipping within HF solutions is configured to maintain a temperature of about 21.5° C. If the temperature were to vary significantly, it would introduce unwanted variability into a fabrication process. 
     It is desired to develop alternative methods of utilizing fluorine-containing species for treating materials during semiconductive fabrication processes. 
     SUMMARY OF THE INVENTION 
     In one aspect, the invention encompasses a semiconductor processing method wherein a surface is contacted with a liquid solution comprising one or more fluorine-containing species and a temperature of at least about 40° C. 
     In another aspect, the invention encompasses a method of passivating a silicon-comprising layer wherein the layer is contacted with a liquid solution comprising hydrogen fluoride and a temperature of at least about 40° C. 
     In another aspect, the invention encompasses a method of forming HSG polysilicon. A layer comprising substantially amorphous silicon is formed over a substrate. The layer comprising substantially amorphous silicon is contacted with a liquid solution comprising one or more fluorine-containing species and a temperature of at least about 40° C. The layer comprising substantially amorphous silicon is seeded and annealed to convert at least a portion of the layer to HSG polysilicon. 
     In yet another aspect, the invention encompasses a method of forming a wordline. A silicon layer is formed over a substrate. The silicon layer is passivated by contacting it with a liquid solution comprising hydrogen fluoride. The liquid solution is at a temperature of at least about 40° C. during the contacting. After the passivating, a silicide layer is formed over the silicon layer. 
    
    
     BRIEF DESCRIPTION OF THE DRAWINGS 
     Preferred embodiments of the invention are described below with reference to the following accompanying drawings. 
     FIG. 1 is a fragmentary, diagrammatic, cross-sectional view of a semiconductor wafer fragment at a preliminary processing step of a method of the present invention. 
     FIG. 2 is a view of the FIG. 1 wafer fragment shown at a processing step subsequent to that of FIG.  1 . 
     FIG. 3 is a view of the FIG. 1 wafer fragment shown at a processing step subsequent to that of FIG.  2 . 
     FIG. 4 is a view of the FIG. 1 wafer fragment shown at a processing step subsequent to that of FIG.  3 . 
     FIG. 5 is a fragmentary, diagrammatic, cross-sectional view of a semiconductor wafer fragment illustrating a capacitor construction formed by an alternative embodiment of the present invention. 
     FIG. 6 is a fragmentary, diagrammatic, cross-sectional view of a semiconductor wafer fragment being processed according to a second embodiment method of the present invention. 
     FIG. 7 is a view of the FIG. 6 wafer fragment at a processing step subsequent to that of FIG.  6 . 
     FIG. 8 is a graph of surface enhancement versus etch time, comparing silicon surfaces treated according to a method of the present invention with silicon surfaces treated according to prior art methods. 
    
    
     DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS 
     This disclosure of the invention is submitted in furtherance of the constitutional purposes of the U.S. Patent Laws “to promote the progress of science and useful arts” (Article 1, Section 8). 
     A first embodiment process of the present invention is described with reference to FIGS. 1-4, wherein the first embodiment process is a method of forming a capacitor. Referring first to FIG. 1, a wafer fragment  10  comprises a substrate  12  and an insulative material  14  formed over substrate  12 . Substrate  12  can comprise, for example, a monocrystalline silicon wafer lightly doped with a background p-type dopant. To aid in interpretation of the claims that follow, the term “semiconductive substrate” is defined to mean any construction comprising semiconductive material, including, but not limited to, bulk semiconductive materials such as a semiconductive wafer (either alone or in assemblies comprising other materials thereon), and semiconductive material layers (either alone or in assemblies comprising other materials). The term “substrate” refers to any supporting structure, including, but not limited to, the semiconductive substrates described above. 
     Insulative layer  14  can comprise, for example, borophosphosilicate glass (BPSG). An opening  16  is formed through insulative layer  14  and to substrate  12 . A node location  18  is defined within substrate  12  at a bottom of opening  16 . Node location  18  can comprise, for example, a conductively doped diffusion region within substrate  12 . Such diffusion region can be formed either before or after formation of insulative layer  14  by conventional methods, such as, for example, ion implanting. 
     Referring to FIG. 2, an amorphous silicon layer  20  is formed over insulative layer  14  and within opening  16 . Amorphous silicon layer  20  can be formed by conventional methods, such as, for example, chemical vapor deposition. In accordance with the present invention, layer  20  is exposed to a liquid solution comprising one or more fluorine-containing species and maintained at a temperature of at least about 40° C. The liquid solution can be in the form of, for example, a liquid bath with the vast majority (greater than 99%) of the liquid in the bath comprising a temperature of at least about 40° C. Such bath will preferably be in a vessel configured to heat the bath to maintain the temperature of at least about 40° C. Thus, the bath will have a temperature of at least about 40° C. before contacting layer  20 , and will maintain such temperature during contacting of layer  20 . 
     Exposure of layer  20  to the liquid passivates and/or strips oxide from over layer  20 . After the exposure to the liquid solution comprising fluorine-containing species, layer  20  is converted to an HSG layer  30  (shown in FIG.  3 ). The conversion to HSG layer can be accomplished by seeding and annealing procedures, such as, for example, those described in U.S. Pat. Nos. 5,634,974 and 5,691,228. 
     The treatment of layer  20  with the liquid solution comprising fluorine-containing species can occur, for example, for a time of from about five seconds to about 20 minutes, with times of from about one minute to about two minutes being more preferred. It is to be understood, however, that treatment times are generally not critical to methods of the present invention. Accordingly, the present invention encompasses applications in which an upper limit of the treatment time can extend beyond 20 minutes. Also, treatment pressures are generally not critical to methods of the present invention, and treatment pressures can be higher, lower or equal to about one atmosphere. 
     A treatment liquid of the present invention is a liquid solution comprising fluorine-containing species. An example liquid solution comprising fluorine-containing species is a solution comprising from about 0.1% to about 49% hydrogen fluoride (by weight) and from about 51% to about 99.9% water (by weight). Such solutions can be formed, for example, by mixing commercial hydrogen fluoride solutions (generally obtained as a 49% (by weight) HF solution) with water. Another example liquid solution comprising fluorine-containing species is a solution comprising from about 0.1% to about 49% hydrogen fluoride (by weight), from about 28% to about 99.85% water (by weight), and from about 0.05% to about 23% tetramethyl ammonium hydroxide (TMAH) (by weight). Such solutions can be formed, for example, by mixing commercial hydrogen fluoride solutions (generally obtained as 49% (by weight) HF in water) with commercial TMAH solutions (generally obtained as 25% (by weight) TMAH in water), and water. 
     It can be advantageous to utilize liquid solutions comprising both TMAH and HF when differing materials are to be exposed to the liquid solutions, because the TMAH can equalize a rate at which HF etches differing materials. Specifically, the TMAH can form a diffusion barrier over surfaces as the surfaces are exposed to a mixture of HF and TMAH. The diffusion barrier can change a rate limiting step of an HF etch from etch chemistry to diffusion through the barrier layer, and can thereby equalize a rate at which hydrogen fluoride etches differing materials. For instance, if a wafer surface comprises silicon dioxide and BPSG, the BPSG and silicon dioxide surfaces will typically be etched at vastly different rates by HF. However, if TMAH is present, the TMAH will form a diffusion barrier over the BPSG and silicon dioxide surfaces. The HF will then need to diffuse through the barrier layer before etching the BPSG and silicon dioxide surfaces. If such diffusion through the barrier layer becomes a rate-limiting step, the barrier layer can equalize a rate at which the BPSG and silicon dioxide are etched. 
     The present invention utilization of a liquid hydrogen fluoride solution at a temperature of at least about 40° C. can create significant advantages over prior art utilizations of liquid hydrogen fluoride solutions at about 21° C. For instance, the graph of FIG. 8 illustrates that processing temperatures above 40° C. significantly enhance the capacitive characteristics of a HSG polysilicon layer formed according to the method of the present invention relative to HSG polysilicon layers formed according to prior art methods. Specifically, FIG. 8 is a graph of surface enhancement versus etch time (i.e., exposure time to an HF solution) for various HSG layers. Surface enhancement is defined as (Cap grain −Cap flat )/Cap flat ), wherein Capgrain refers to the capacitance of a capacitor formed with HSG generated from amorphous silicon exposed to liquid HF at an indicated temperature, and Capflat refers to the capacitance of a capacitor formed from non-HSG polysilicon. Etch time is the time for which an amorphous silicon layer is exposed to a liquid solution comprising HF (specifically, HF and tetramethyl ammonium hydroxide (TMAH)), and comprising an indicated temperature. The graph indicates that treatment of amorphous silicon with an HF solution at temperatures above 40° C. will enhance capacitance of HSG formed from such amorphous silicon layers. The graph further indicates that the enhanced capacitance gained by treating amorphous silicon with liquid HF above 40° C. is beyond what can be achieved by conventional HF etching at about 21° C., regardless of how long the conventional etching lasts. 
     Referring to FIG. 4, HSG polysilicon layer  30  is incorporated into a capacitor construction  50 . Specifically, a dielectric layer  32  and a capacitor plate layer  34  are formed over HSG polysilicon layer  30 . Dielectric layer  32  can comprise, for example, silicon nitride and/or silicon dioxide, and can be formed by conventional methods, such as, for example chemical vapor deposition. Upper capacitor plate layer  34  can comprise, for example, conductively doped polysilicon, and can also be formed by conventional methods, such as, for example, chemical vapor deposition. Capacitor assembly  50  can be incorporated into integrated circuitry by methods known to persons of ordinary skill in the art. 
     Although the above-described method for forming a capacitor construction utilized an amorphous silicon layer  20  (shown in FIG. 2) which was subsequently converted to a HSG polysilicon layer  30  (shown in FIG.  3 ), it is to be understood that the invention can encompass other methods of forming a capacitor which are not shown. For instance, the layer  20  shown in FIG. 2 can be a polysilicon layer. Such polysilicon layer can be treated with a liquid solution comprising fluorine-containing species and a temperature of at least 40° C. in accordance with the method of the present invention to passivate the polysilicon layer. The polysilicon layer can then be incorporated directly into a capacitor structure, without converting the polysilicon layer to HSG polysilicon. 
     The embodiment of FIGS. 1-4 illustrates a method of utilizing the present invention to form a container capacitor construction. The present invention also encompasses methods of forming alternative capacitor constructions. For instance, FIG. 5 illustrates a wafer fragment  100  comprising an alternative capacitor construction  102 . Wafer fragment  100  comprises a substrate  104  and a conductive plug  106  formed over the substrate. 
     Substrate  104  can comprise, for example, monocrystalline silicon, and conductive plug  106  can comprise, for example, conductively doped polysilicon. 
     An insulating layer  108  is formed over substrate  104  and around plug  106 . Insulating layer  108  can comprise, for example, silicon dioxide. 
     An electrical node  110  is formed within substrate  104  and against plug  106 . Node  110  can comprise, for example, a diffusion region. 
     A first capacitor plate  112 , dielectric layer  114  and second capacitor plate  116  are formed operatively adjacent plug  106  to form capacitor construction  102 . First and second capacitor plates  112  and  116  can comprise, for example, conductively doped polysilicon, and first capacitor plate preferably comprises conductively doped hemispherical grain polysilicon. One or both of first and second capacitor plates  112  and  116  can be formed by a method comprising dipping a polysilicon layer in a bath comprising fluorine-containing species and a temperature of at least about 40° C. Dielectric layer  114  can comprise, for example, silicon nitride or silicon oxide. 
     The above-described embodiments are methods of forming a capacitor constructions. Another application in which HF dipping can be utilized to clean and passivate a surface is during formation of wordlines. Wordlines are commonly formed by first providing a layer of polysilicon, and subsequently providing a silicide layer over the polysilicon. The silicide layer can be formed, for example, by exposing a surface of the polysilicon to conditions which convert such surface to silicide. Frequently, it is desired to clean a polysilicon surface prior to forming silicide from such surface. A method of cleaning a polysilicon surface is to dip the polysilicon within a liquid solution comprising fluorine-containing species. In accordance with the present invention, such solution can comprise a temperature of at least about 40° C. 
     A method of forming a wordline in accordance with the present invention is described with reference to FIGS. 6 and 7. Referring first to FIG. 6, a wafer fragment  60  comprises a substrate  62 , a gate oxide layer  64  and a polysilicon wordline  66  formed over gate oxide  64 . Substrate  62  can comprise, for example, monocrystalline silicon conductively doped with a background dopant. Gate oxide layer  64  can comprise, for example, silicon dioxide. Wordline  66  can comprise polysilicon conductively doped with a conductivity-enhancing impurity. As will be recognized by persons of ordinary skill in the art, wordline  66  can be formed by patterning a layer of polysilicon into a wordline shape. In accordance with the present invention, wordline  66  is treated with a liquid solution comprising fluorine-containing species and comprising a temperature of at least about 40° C. to passivate silicon within wordline  66 . Treatment of the polysilicon of wordline  66  can occur before or after the patterning of a layer of polysilicon into the wordline shape. 
     Referring to FIG. 7, a silicide layer  68  is formed over the treated polysilicon of wordline  66 . Silicide layer  68  can be formed by conventional methods such as, for example, by depositing a metal over an upper surface of the polysilicon of wordline  66  and reacting the metal with the silicon to form silicide layer  68 . As will be recognized by persons of ordinary skill in the art, sidewalls of wordline  66  will generally be blocked by, for example, sidewall spacers, as a metal is formed over the upper surface of wordline  66  to prevent metal from depositing on the sides. Sidewall blocking materials are not shown in FIGS. 6 and 7 because they are not germane to the present invention, and because persons of ordinary skill in the art will readily recognize how and when to incorporate sidewall spacers into a method of the present invention. 
     In compliance with the statute, the invention has been described in language more or less specific as to structural and methodical features. It is to be understood, however, that the invention is not limited to the specific features shown and described, since the means herein disclosed comprise preferred forms of putting the invention into effect. The invention is, therefore, claimed in any of its forms or modifications with in the proper scope of the appended claims appropriately interpreted in accordance with the doctrine of equivalents .