Abstract:
A method of making a radially expandable fluid delivery device includes providing a tube of biocompatible fluoropolymer material with a predetermined porosity based on an extrusion and expansion forming process, applying a radial expansion force to the tube expanding the tube to a predetermined diameter dimension, and removing the radial expansion force. The tube is radially inelastic while sufficiently pliable to be collapsible and inflatable from a collapsed configuration to an expanded configuration upon introduction of an inflation force, such that the expanded configuration occurs upon inflation to the predetermined diameter dimension. The fluid delivery device is constructed of a microporous, biocompatible fluoropolymer material having a microstructure that can provide a controlled, uniform, low-velocity fluid distribution through the walls of the fluid delivery device to effectively deliver fluid to the treatment site without damaging tissue proximate the walls of the device.

Description:
REFERENCE TO RELATED APPLICATIONS 
       [0001]    This application is a divisional application of U.S. patent application Ser. No. 09/411,797, filed Oct. 1, 1999, which claims priority to U.S. Provisional Application Ser. No. 60/117,152, filed Jan. 25, 1999. This application claims the benefit of and priority to the aforementioned applications (09/411,797 and 60/117,152), which are hereby incorporated herein by reference. 
     
    
     BACKGROUND OF THE INVENTION 
       [0002]    Catheter delivered inflatable balloons are utilized in a wide range of surgical procedures to dilate, obstruct, or restore patency to body vessels and organs, as well as to maintain the position of catheter delivered instruments in vivo. Such balloons are typically attached to the distal tip of a small diameter catheter tube to facilitate delivery of the balloon to a treatment site within the body. The balloon is advanced by the catheter through a body vessel while in a deflated condition until the balloon is appropriately positioned proximate the treatment site. The balloon is inflated by infusing a fluid, such as saline, a contrast media, or water, into the balloon through an inflation lumen provided in the catheter. The inflated balloon is deflated after treatment and subsequently removed from the body. 
         [0003]    Perforated and porous catheter balloons have been proposed to deliver therapeutic agents, e.g. drugs and other medicinal agents, directly to the treatment site while concomitantly performing their primary function of dilation, obstruction, etc. The localized delivery of therapeutic agents to the treatment site can increase the effectiveness of the therapeutic agent and minimize or even negate the systemic side effects of the agent. Generally, the therapeutic agent is delivered through the wall of the catheter either through openings mechanically formed in the wall or through pores present in the material used to form the balloon. A problem common to such conventional catheter balloons is that the flow-rate and the uniform delivery of fluid, and hence the therapeutic agent, through the walls of the balloon is difficult to control. Successful delivery of the therapeutic agent to the treatment site requires the therapeutic agent to penetrate the body tissue at the treatment site to a depth sufficient for the agent to effect the treatment site without effecting healthy tissue or organs proximate the tissue site. For this reason, the flow rate of and the uniform delivery of the therapeutic agent through the walls of the balloon is important. If the flow rate is too low, the therapeutic agent can fail to properly penetrate the tissue at treatment site. If the flow rate is too high, the therapeutic agent can be delivered to areas of the body outside of the treatment area and, in some cases, elevated flow rates can result in the formation of high velocity fluid jets which can traumatize the tissue adjacent the walls of the balloon. 
       SUMMARY OF THE INVENTION 
       [0004]    The present invention provides a radially expandable fluid delivery device for delivering fluid to a treatment site within the body. The radially expandable fluid delivery device can be used, for example, as a catheter delivered balloon for the treatment of body lumens, organs, and grafts. Fluids, including therapeutic agents, can be delivered through the walls of the fluid delivery device to effect localized treatment of sites within the body. The fluid delivery device of the present invention is constructed of a biocompatible material having a microstructure that can provide a controlled, uniform, low-velocity distribution of fluid through the walls of the fluid delivery device to effectively deliver the fluid to the treatment site without damaging tissue proximate the walls of the device. 
         [0005]    In accordance with one aspect of the present invention, the fluid delivery device comprises a member constructed of a biocompatible material. The member is defined by a wall having a thickness extending between an inner and an outer surface. The wall is characterized by a microstructure of nodes interconnected by fibrils. The member is deployable from a first, reduced diameter configuration to a second, increased diameter configuration upon the introduction of a pressurized fluid to the lumen. The member includes at least one microporous portion having a porosity sufficient for the pressurized fluid to permeate through the wall. The spaces between the nodes control the permeation of fluid through the wall of the fluid delivery device. In a preferred embodiment, substantially all of the nodes within the microporous portion are oriented such that spaces between the nodes form generally aligned micro-channels extending from the inner surface to the outer surface of the wall. 
         [0006]    In accordance with another aspect of the present invention, the nodes within the microporous portion of the member can be oriented substantially parallel to the longitudinal axis of the member. The micro-channels are preferably sized to permit the passage of the pressurized fluid from the inner surface to the outer surface of the wall. The size of the microchannels within the microporous portion can be varied longitudinally and/or circumferentially to provide regions of increased porosity within the microporous portion. The presence of regions of differing porosity allows the volume of fluid delivered through the microporous portion of the member to vary, longitudinally and/or circumferentially, across the microporous portion. This allows the microporous portion to be specifically tailored to the size and shape of the site being treated. 
         [0007]    Various biocompatible materials are suitable for the construction of the member. Expanded polytetrafluoroethylene (ePTFE), which is a hydrophobic, biocompatible, inelastic material having a low coefficient of friction, is the preferred material of choice. 
         [0008]    In accordance with a further aspect of the present invention, the member can be provided with first and second microporous portions, each having a porosity sufficient for the pressurized fluid to permeate through the wall of the member. The first and second microporous portions can be spaced apart longitudinally and/or circumferentially. An impermeable or semi-permeable portion can be interposed between the first and second microporous portions. Further microporous portions and/or impermeable or semi-permeable portions can also be provided on the member. The microporous portions and the impermeable portions can be arranged in numerous alternative configurations. For example, microporous ring-shaped portions can be spaced along the longitudinal axis of the member. Alternatively, the microporous portions can be generally rectangular in shape and can be spaced apart about the circumference of the member. The provision of multiple microporous portions allows the fluid delivery device of the present invention to treat multiple sites within the body simultaneously. 
         [0009]    In accordance with one aspect of the present invention, a method is provided for manufacturing a radially expandable device for delivery of a fluid to a treatment site within the body. The method includes the step of forming a tube of inelastic, fluoropolymer material through an extrusion and expansion process having selected process parameters. The tube has a porosity corresponding to the selected process parameters. A radial expansion force is applied to the tube to expand the tube from an initial diameter to a second diameter. The expansion force is then removed. The resultant tube is radially expandable from a reduced diameter to the second diameter upon application of a radial deployment force from a deployment mechanism within the tube. The deployment mechanism can be, for example, a fluid injected into the tube or a radial expansion element inserted into the tube. 
         [0010]    The tube can be constructed through an extrusion and expansion process, including the step of creating a billet by blending a mixture of a fluoropolymer and a lubricant and compressing the mixture. The fluoropolymer is preferably PTFE. The billet can then be extruded to form an extruded article. The lubricant is removed and the extruded article is expanded to form a monolithic tube of inelastic, expanded fluoropolymer material. The stretched tube is then heat set to lock in the microstructure of the tube and maintain the tube in the stretched state. 
         [0011]    In accordance with a further aspect of the present invention, at least one of the extrusion and expansion process parameters can be varied to form a microporous portion of the wall having a porosity sufficient for the pressurized fluid to permeate through the wall. For example, the lubricant density, the lubricant viscosity, the lubricant molecular weight, the amount of lubricant and/or the longitudinal stretch ratio can be selectively varied to form the microporous portion of the tube. The process parameters can also be varied to produce increased regions of porosity with the microporous region or to form multiple microporous regions. 
         [0012]    The extruded article is preferably bilaterally stretched in two opposing directions along the longitudinal axis of the article. Bilaterally stretching the extruded article yields an article that is substantially uniformly stretched over a major portion of its length and has a microstructure of nodes interconnected by fibrils. Bilateral stretching can further result in the formation of a microstructure in which the nodes are oriented substantially perpendicular to the longitudinal axis of the article such that the spaces between the nodes form microchannels extending from the inner to the outer surface of the wall of the member. The bilateral stretching step can be carried out by displacing the ends of the extruded article either simultaneously or sequentially. 
         [0013]    In accordance with another aspect of the present invention, the step of applying a radial expansion force to the tube is carried out by inserting a balloon into the tube and expanding the balloon to apply the radial expansion force to the tube. Preferably, the balloon is constructed from an inelastic material such as, for example, polyethylene terephthalate (PET), nylon, or ePTFE. In a preferred embodiment, the balloon is constructed to be expandable to a predefined size and shape by inflation with a fluid. Radial expansion of the expanded fluoropolymer tube with such an inelastic balloon imparts the predetermined size and shape of the balloon to the expanded fluoropolymer balloon. 
         [0014]    In accordance with a further aspect of the present invention, the step of radially expanding the expanded fluoropolymer tube plastically deforms the tube beyond its elastic limit to the second diameter. Plastically deforming the fluoropolymer tube to the second diameter contributes to the expansion device dependably expanding to the second diameter upon application of the radial deployment force. 
         [0015]    The step of radially expanding the expanded fluoropolymer tube can also include the steps of positioning the tube within the internal cavity of a mold fixture and radially expanding the balloon within the tube while the tube remains positioned in the internal mold cavity. The internal mold cavity preferably has a size and shape analogous to the predefined size and shape of the balloon. The internal cavity of the mold facilitates concentric radial expansion of the balloon and the fluoropolymer tube. 
         [0016]    In accordance with a further aspect of the present invention, the radially expandable fluid delivery of the present invention is particularly suited for treatment of body passages and grafts occluded by disease. The fluid delivery device can be utilized in the manner of a catheter balloon suitable for deployment within a body vessel by a catheter. Exemplary treatment applications of the present application include dilation of stenoic blood vessels in a percutaneous transluminal angioplasty procedure (PCA), removal of thrombi and emboli from obstructed blood vessels, urethra dilation to treat prostatic enlargement due to benign prostate hyperplasia (BPH) or prostatic cancer, and generally restoring patency to body passages such as blood vessels, the urinary tract, the intestinal tract, the kidney ducts, or other body passages. Exemplary therapeutic agents that can be delivered through the fluid delivery device of the present invention include thrombolytics, antibiotics, antisense oligonucleaotides, chemotherapeutics, surfactants, diagnostic agents, steroids, vasodilators, vasoconstrictors, and embolic agents. 
     
    
     
       BRIEF DESCRIPTION OF THE DRAWINGS 
         [0017]    These and other features and advantages of the present invention will be more fully understood by reference to the following detailed description in conjunction with the attached drawings in which like reference numerals refer to like elements through the different views. The drawings illustrate principles of the invention and, although not to scale, show relative dimensions. 
           [0018]      FIG. 1  is a side elevational view in cross-section of a radially expandable fluid delivery device according to the teachings of the present invention, illustrating the device in a first, reduced diameter configuration; 
           [0019]      FIG. 2  is a side elevational view in cross-section of the radially expandable fluid delivery device of  FIG. 1 , illustrating the device in a second, increased diameter configuration; 
           [0020]      FIG. 3  is a side elevational view of an alternative embodiment of the radially expandable fluid delivery device of the present invention, illustrating the device in the second, increased diameter configuration; 
           [0021]      FIG. 4  is a side elevational view of an alternative embodiment of a radially expandable fluid delivery device of the present invention having multiple axially-spaced microporous portions, illustrating the device in the second, increased diameter configuration; 
           [0022]      FIG. 5  is a cross-sectional view of an alternative embodiment of a radially expandable fluid delivery device of the present invention having an arcuate-shaped microporous portion, illustrating the device in the second, increased diameter configuration; 
           [0023]      FIG. 6  is a cross-sectional view of an alternative embodiment of a radially expandable fluid delivery device of the present invention having multiple circumferentially-spaced microporous portions, illustrating the device in the second, increased diameter configuration; 
           [0024]      FIG. 7  is a flow chart illustrating the steps of manufacturing a fluid delivery device according to the teachings of the present invention; 
           [0025]      FIG. 8  is a schematic representation of the microstructure of an expanded fluoropolymer tube used during the manufacturing process of the present invention to yield the fluid delivery device of  FIG. 1 ; 
           [0026]      FIG. 9A  is a side elevational view in cross-section of an inelastic balloon positioned within an expanded fluoropolymer tube, illustrating the inelastic balloon in a deflated condition in accordance with a method of manufacturing a fluid delivery device according to the teachings of the present invention; 
           [0027]      FIG. 9B  is a side elevational view in cross-section of the inelastic balloon and the expanded fluoropolymer tube of  FIG. 9A , illustrating the inelastic balloon in an inflated condition in accordance with a method of manufacturing a fluid delivery device according to the teachings of the present invention; 
           [0028]      FIG. 9C  is a side elevational view in cross-section of the inelastic balloon and the expanded fluoropolymer tube of  FIG. 9A , illustrating the removal of the deflated inelastic balloon from the expanded fluoropolymer tube in accordance with a method of manufacturing a fluid delivery device according to the teachings of the present invention; 
           [0029]      FIG. 10  is a schematic of a system for inflating an inelastic balloon with an expanded fluoropolymer tube in accordance with a method of manufacturing a fluid delivery device according to the teachings of the present invention; 
           [0030]      FIG. 11  is a side elevational view of an inelastic balloon and an expanded fluoropolymer tube positioned within the internal cavity of a mold fixture, illustrating the inelastic balloon in an inflated condition in accordance with a method of manufacturing a fluid delivery device according to the teachings of the present invention; 
           [0031]      FIG. 12  is a side-elevational view in cross-section of a catheter deployed infusion balloon according to the teachings of the present invention, illustrating the infusion balloon expanded within a body vessel; 
           [0032]      FIG. 13  is a flow chart illustrating the steps of an alternative method of manufacturing a fluid delivery device according to the teachings of the present invention; 
           [0033]      FIG. 14A  is an electron micrograph of an external section of an ePTFE tube used in the manufacture of the fluid delivery device of the present invention; 
           [0034]      FIG. 14B  is an electron micrograph of an external section of a fluid delivery device of the present invention; 
           [0035]      FIG. 14C-14D  are electron micrographs of an external section of the neck of the fluid delivery device of  FIG. 14B ; and 
           [0036]      FIG. 15  is a side elevational view in cross-section of a multi-layer radially expandable fluid delivery device in accordance with the present invention, illustrating the device in a second, increased diameter configuration. 
       
    
    
     DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS 
       [0037]    A radially expandable fluid delivery device  10  having an extensible member  12  constructed of a biocompatible fluoropolymer material is illustrated in  FIGS. 1 and 2 . The radially expandable fluid delivery device  10  of the present invention is suitable for a wide range of treatment applications. Such applications include use of the fluid delivery device  10  as a catheter balloon for treatment of body passages and grafts such as blood vessels, the urinary tract, the intestinal tract, kidney ducts, natural and synthetic grafts, etc. Specific examples include as a device for the removal of obstructions such as emboli and thrombi from blood vessels, as a dilation device to restore patency to an occluded body passage, as an occlusion device to selectively obstruct a body passage, and as a centering mechanism for transluminal instruments and catheters. In each of these applications, the fluid delivery device  10  can simultaneously deliver a fluid, such as a therapeutic agent, to the body vessel, or the tissue or organs surrounding the body vessel, to effect local treatment with the agent. 
         [0038]    The extensible member  12  of the radially expandable fluid delivery device  10  is deployable upon application of an expansion force from a first, reduced diameter configuration, illustrated in  FIG. 1 , to a second, increased diameter configuration, illustrated in  FIG. 2 . The extensible member  12  of the fluid delivery device  10  of the present invention preferably features a monolithic construction, i.e., the extensible member  12  is a singular, unitary article of generally homogeneous material. The extensible member  12  is manufactured in accordance with the methods of manufacturing of the present invention, an extrusion and expansion process described in detail below, to yield an extensible member  12  characterized by a seamless construction of inelastic, expanded fluoropolymer having a predefined size and shape in the second, increased diameter configuration. The extensible member  12  can be dependably and predictably expanded to the predefined, fixed maximum diameter and to the predefined shape independent of the expansion force used to expand the device. 
         [0039]    Referring specifically to  FIG. 2 , the extensible member  12  of the fluid delivery device  10  of the present invention is generally tubular in shape when expanded, although other cross sections, such as rectangular, oval, elliptical, or polygonal, can be utilized. The cross-section of the extensible member  12  is continuous and uniform along the length of the extensible member. However, in alternative embodiments, the cross-section can vary in size and/or shape along the length of the extensible member.  FIG. 1  illustrates the extensible member  12  relaxed in the first, reduced diameter configuration. The extensible member  12  has a central lumen  13  extending along a longitudinal axis  14  between a first end  16  and second end  18 . 
         [0040]    A deployment mechanism in the form of an elongated hollow tube  20  is shown positioned within the central lumen  13  to provide a radial deployment or expansion force to the extensible member  12 . The tube  20  can be, for example, a catheter constructed from PEBAX tubing available from Elf Atochem of France. The tube  20  is selected to have an outer diameter approximately equal to the diameter of the central lumen  13  of the extensible member  12  in the reduced diameter configuration. The radial deployment force effects radial expansion of the extensible member  12  from the first configuration to the second increased diameter configuration illustrated in  FIG. 2 . The first end  16  and the second end  18  are connected in sealing relationship to the outer surface of the hollow tube  20 . The first and second ends  16  and  18  can be thermally bonded, bonded by means of an adhesive, or attached by other means suitable for inhibiting fluid leakage from the first and second ends  16  and  18  between the walls of the extensible member  12  and the tube  20 . 
         [0041]    The hollow tube  20  includes an internal, longitudinal extending lumen  22  and a number of side-holes  24  that provide for fluid communication between the exterior of the tube  20  and the lumen  22 . The tube  20  can be coupled to a fluid source (not shown) to selectively provide fluid, such as water, a contrast medium, of saline, to the lumen  13  of the extensible member  12  through the lumen  22  and side-holes  24 . The pressure from the fluid provides a radial expansion force on the extensible member  12  to radial expand the extensible member  12  to the second, increased diameter configuration. Because the extensible member  12  is constructed from an inelastic material, uncoupling the tube  20  from the fluid source or otherwise substantially reducing the fluid pressure within the lumen  13  of the extensible member  12 , does not generally result in the extensible member  12  returning to the first, reduced diameter configuration. However, the extensible member  12  will collapse under its own weight to a reduced diameter. Application of negative pressure, from, for example, a vacuum source, can be used to completely deflate the extensible member  12  to the initial reduced diameter configuration. 
         [0042]    One skilled in the art will appreciate that the expansion device  10  of the present invention is not limited to use with deployment mechanisms employing a fluid deployment force, such as hollow tube  20 . Other known deployment mechanisms can be used to radially deploy the expansion device  10  including, for example, mechanical operated expansion elements, such as mechanically activated members or expansion elements constructed from temperature activated materials such as nitinol. 
         [0043]    The extensible member  12  is defined by a wall  30  of biocompatible fluoropolymer material having a thickness extending between an outer surface  32  and an inner surface  34  of the extensible member  12 . The inner surface  34  defines the lumen  13  of the extensible body  12 . The wall  12  of biocompatible fluoropolymer material is characterized by a microstructure of nodes interconnected by fibrils.  FIGS. 1 and 2  provide schematic representations of the microstructure of the extensible member  12 . For purposes of description, the microstructure of the extensible member has been exaggerated. Accordingly, while the dimensions of the microstructure are enlarged, the general character of the illustrated microstructure is representative of the microstructure of the extensible member  12 . 
         [0044]    The extensible member  12  includes at least one microporous portion  40  having a porosity sufficient for the flow of fluid from the lumen  13  through the wall  30 , i.e. from inner surface  34  to outer surface  32 . The microstructure of the wall  30  within the microporous portion  40  is characterized by a plurality of nodes  36  interconnected by fibrils  38 . Preferably, all or substantially all of the nodes  36  within the microporous portion  40  are oriented perpendicular to the inner surface  34  and the outer surface  32  of the extensible member  12  as well as parallel to each other. This preferred orientation of the nodes  36  provides internodal spaces that form pores or micro-channels  42  that extend between the inner surface  34  and the outer surface  32  of the extensible member  12 . The micro-channels  42  are sized to permit the flow of fluid between the nodes  36  through the wall  30 . 
         [0045]    The size of the micro-channels or pores  42  can be selected through the manufacturing process of the present invention, described in detail below. Preferably, the internodal distance of microstructure of the wall within the microporous region, and hence the width of the micro-channels, is approximately 1 μm to approximately 150 μm. Internodal distances of this magnitude can yield flow rates of approximately 0.01 ml/min to approximately 100 ml/min of fluid through the wall  30  of the extensible member  12 . 
         [0046]    In a preferred embodiment, the size of the micro-channels or pores  42  within the microporous portion  40  is uniform throughout the microporous portion. In this manner, the flow-rate of fluid through the wall of the microporous portion  40  is also generally uniform. In some applications, however, it may be desirable to have an area of increased or decreased porosity within the microporous portion such that the flow-rate can be tailored to the particular geometry of the site being treated. For example, if a particular region at the treatment site requires increased concentrations of the therapeutic agent, the flow rate at the corresponding section of the microporous portion can be increased to thereby increase the volume of therapeutic agent be delivered to the particular region. Additionally, it is often desirable to reduce the volume of therapeutic agent delivered to the periphery of the treatment site to minimize damage to healthy tissue adjacent the site. The pore size within the microporous region thus can be varied axially or circumferentially, or both, to form such areas of increased or decreased porosity. 
         [0047]    The terms “axial” and “axially” as used herein refers to a direction generally parallel to the longitudinal axis of the extensible member  12 . The terms “circumferential” and “circumferentially” as used herein refers to a direction generally parallel to the circumference of the extensible member  12 . The explanation of these terms is not, however, to be construed to limit the extensible member  12  to a circular cross-section. As discussed above, the cross-section can be any of a number shapes. In the case of non-circular cross-sections, the terms “circumferential” and “circumferentially” as used herein to generally refer to a direction parallel to the perimeter of the extensible member. 
         [0048]    The axial length, as well as the axial position, of the microporous portion  40  of the extensible member  12  can be varied to accommodate specific treatment applications. As illustrated in  FIG. 2 , for example, the microporous portion  40  can extend along the entire inflatable length of the extensible member  12 . In particular, the microporous portion  40  includes a section  40   b  that is oriented parallel to the longitudinal axis  14  of the extensible member  12  as well as two spaced apart tapered sections  40   b  and  40   c . In the embodiment illustrated in  FIG. 2 , thus, the microporous portions  40   a ,  40   b , and  40   c  extend along the entire length of the extensible member  12 , absent the first and second ends  16  and  18 , which are sealed to the hollow tube  20 . 
         [0049]    The microporous portion  40  need not extend the entire inflatable length of the extensible member  12  but instead can include only sections of the length of the extensible member  12 . For example, as illustrated in  FIG. 3 , the microporous portion can include only section  40   b , the section oriented parallel to the longitudinal axis  14  of the extensible member  12 . Tapered section  44  and  46  adjacent the microporous portion  40   b  can be substantially impermeable to the fluid within the extensible member  12 . The tapered sections  44  and  46  can formed with the same microstructure as the microporous portions  40   b , i.e. nodes of the same size and orientation, and can be sealed with a coating provided on the inner surface  34  or the outer surface  32  to inhibit fluid flow through the sections  44  and  46 . Alternatively, the microstructure of the tapered sections  44  and  46  can have an impermeable, non-porous structure. For example, the nodes forming the microstructure of the tapered sections  44  and  46  can be spaced apart or oriented to inhibit or prevent fluid from passing therethrough. 
         [0050]    Moreover, two or more microporous portions of similar or different axial lengths can be provided on the extensible member  12 . For example, the extensible member  12  can be provided with three axially spaced microporous portions  40   e , as shown in  FIG. 4 . Each of the microporous portions  40   e  is bordered axially by an impermeable portion  48 . The microporous portions  40   e  provide porous, fluid permeable annular zones that are spaced lengthwise along the extensible member  12 . The microporous portions  40   e  can be equally spaced and of similar size, as illustrated in  FIG. 4 , or, in the alternative, can be distinctly sized and spaced. One skilled in the art will appreciate that the number of independent microporous portions is not limited to three as shown in  FIG. 4 , but can include two or more zones as dictated by the length of the extensible member  12  and the desired size of the microporous portions. 
         [0051]    Referring to  FIGS. 5 and 6 , the size and position of the microporous portion can be varied circumferentially as well as axially. For example, the microporous section need not extend about the entire circumference of the extensible member  12 .  FIG. 5  illustrates an alternative embodiment in which the microporous portion  40   f  generally extends about one-half of the circumference of the extensible member to form an arc-shaped section that is permeable to fluid within the extensible member  12 . An impermeable arc-shaped section  50  is positioned adjacent the arc-shaped microporous portion  40   f . Additionally, two or more microporous portions can be spaced circumferentially about the extensible member  12 .  FIG. 6  shows an alternative embodiment including four equally spaced arcuate microporous portions  40   g . Arc-shaped impermeable portions  52  are spaced between the microporous portions  40   g . As in the case of the embodiments described above, the microporous portions  40   g  can be equally spaced and of similar size, as illustrated in  FIG. 6 , or, in the alternative, can distinctly sized and spaced. Further, the number of microporous portions described is exemplary only; the number of microporous portions is limited only by the circumference of the extensible member  12  and the desired size of the microporous portions. 
         [0052]    The impermeable sections of each of the embodiments described above can be constructed of the same microstructure as the microporous portions adjacent thereto, i.e. nodes having the same size and orientation. The impermeable sections can be made impermeable by sealing the sections with a coating provided on either the inner surface  34  or the outer surface  32 , or both, to inhibit or prevent fluid flow through the sections. Alternatively, the microstructure of the impermeable sections can be constructed to have an inherently impermeable, non-porous structure. For example, the nodes forming the microstructure of the impermeable sections can be spaced apart or oriented to inhibit or prevent fluid from passing therethrough. 
         [0053]    Various fluoropolymer materials are suitable for use in the present invention. Suitable fluoropolymer materials include, for example, polytetrafluoroethylene (PTFE) or copolymers of tetrafluoroethylene with other monomers may be used. Such monomers include ethylene, chlorotrifluoroethylene, perfluoroalkoxytetrafluoroethylene, or fluorinated propylenes such as hexafluoropropylene. ePTFE is the preferred material of choice. Accordingly, while the fluid delivery device  10  can be manufactured from various fluoropolymer materials, and the manufacturing methods of the present invention can utilize various fluoropolymer materials, the description set forth herein refers specifically to ePTFE. 
         [0054]    A method of manufacturing a fluid delivery device in accordance with the present invention will be described in connection with the flow chart shown in  FIG. 7 . The fluid delivery device  10  of the present invention is produced from a tube constructed of expanded fluoropolymer material, which is preferably produced through an extrusion and a longitudinal expansion process. The preferred fluoropolymer material is expanded PTFE (ePTFE), which is a hydrophobic, biocompatible, inelastic material having a low coefficient of friction, although, as discussed above, other inelastic, biocompatible fluoropolymer materials may be used. 
         [0055]    To produce the ePTFE tube, a billet comprising a PTFE resin mixed with an organic lubricant is utilized. Various organic lubricants are suitable such as naphtha, ISOPAR-G and ISOPAR-H available from Exxon Corporation. The blended resin is compressed at low pressure to yield a tubular billet of PTFE resin and lubricant, step  210  of  FIG. 7 . The tubular billet is then extruded through an extruder, for example a ram extruder, to reduce the cross section of the billet and to yield a tubular extrudate, ram extruder, to reduce the cross section of the billet and to yield a tubular extrudate, step  212 . The organic lubricant can be removed from the extrudate by drying the extrudate in a heated oven, step  214 . 
         [0056]    Once the tubular extrudate is produced, the extrudate is expanded by longitudinal stretching, step  216 . Preferably, the extrudate is bilaterally stretched. Bilateral stretching is accomplished by displacing both ends of the extrudate, sequentially or simultaneously, away from the center of the extrudate. Bilateral stretching provides a material that is homogeneously stretched over the majority of its length and yields a uniform porosity over the length of the material. After the extrudate has been stretched, it is heat set to lock in the microstructure of the material, step  218  of  FIG. 7 , and to complete the process of the forming the tube  110  of ePTFE. 
         [0057]      FIG. 8  is a schematic representation of the ePTFE tube  110  as formed by the extrusion and expansion process described above. For purposes of description, the microstructure of the tube  110  has been exaggerated. Accordingly, while the dimensions of the microstructure are enlarged, the general character of the illustrated microstructure is representative of the microstructure prevailing within the tube  110 . 
         [0058]    The microstructure of the ePTFE tube  110  is characterized by nodes  130  interconnected by fibrils  132 . The nodes  130  are generally aligned with one another and are generally oriented perpendicular to the longitudinal axis  114  of the tube  110 . Substantially all of the nodes  130  extend along a transverse axis  134  from an inner surface  136  to an outer surface  138  of the tube  110 . This microstructure of nodes  130  interconnected by fibrils  132  provides a microporous structure having microfibrillar spaces which define generally aligned through-pores or channels  134  extending entirely from the inner wall  136  and the outer wall  138  of the tube  110 . The through-pores  134  are perpendicularly oriented (relative to the longitudinal axis  114 ), internodal spaces that traverse from the inner wall  136  to the outer wall  138 . The size and geometry of the through-passages can be altered through the extrusion and expansion process, to yield a microstructure that is impermeable, semi-impermeable, or permeable. 
         [0059]    Although it is preferable for the micro-channels of the ePTFE tube  110 , and the resultant fluid delivery device  10 , to be oriented generally perpendicular to the longitudinal axis of the tube ePTFE  110  or fluid delivery device  10 , other orientations of the micro-channels can be utilized. For example, by twisting or rotating the ePTFE tube during the extrusion and/or stretching process, the micro-channels can be oriented at an angle to an axis perpendicular to the longitudinal axis of the tube. 
         [0060]    In a preferred embodiment, the ePTFE tube  110 , and the resultant fluid delivery device  10 , has a fine nodal structure that is uniform throughout the cross section and length of the ePTFE tube. The preferred uniform fine nodal structure provides the fluid delivery device  10  with improved expansion characteristics as the expandable device dependably and predictably expands to the second diameter. The preferred fine nodal structure is characterized by nodes having a size and mass less than the nodes found in conventional ePTFE grafts, preferably in the range of 25 μm to 30 μm. Additionally, the spacing between the nodes, referred to as the internodal distance, and the spacing between the fibers, referred to as the interfibril distance, is also preferably less than found in conventional ePTFE grafts, preferably in the range of 1 μm to 5 μm. Moreover, the internodal distance and the interfibril distance in the preferred embodiment is preferably uniform throughout the length and the cross section of the ePTFE tube. The preferred uniform nodal structure can be created by forming the billet with a uniform lubricant level throughout its cross section and length. Stretching the tubular extrudate at higher stretch rates, for example at rates greater than 1 in/s, yields the preferred fine nodal structure. Preferably, the extrudate is stretched at a rate of approximately 10 in/s or greater. 
         [0061]    Continuing to describe the manufacturing method of the present invention and referring to  FIGS. 7 and 9A , the ePTFE tube  110 , having an initial diameter d, is pulled over a balloon  112  to position the balloon  112  within the lumen  114  of the tube  110 , step  220  of  FIG. 7 . The balloon  112  is preferably constructed of an inelastic material such as, for example, PET, nylon, or PTFE, such that the balloon  112 , when inflated, attains a predetermined size and shape. The balloon  112  can be bonded or otherwise coupled to a rigid catheter or hypo-tube  116  to facilitate placement and removal of the ePTFE tube as described below. The catheter  116  has a central inflation lumen  118  and a plurality of side-holes  120  to provide for the delivery of an inflation fluid to inflate the balloon  112 . Prior to placement of the ePTFE tube  110  over the balloon  112 , a small amount of negative pressure (vacuum) can be applied to the balloon  112  to reduce the balloon to a minimum deflated profile. 
         [0062]    Referring to  FIG. 10 , a system  148  for inflating the balloon  112  within the ePTFE tube is illustrated. The balloon  112  and the ePTFE tube  110  are positioned within water heated chamber  150 , step  222  of  FIG. 6 . The catheter  116  is connected by plastic tubing  152  to a pump  154 , such as an ISCO syringe pump, for inflation of the balloon  112  with a fluid. Heated water from a circulating temperature bath  158  is pumped through the chamber  150  by a pump  160  to maintain the water within the chamber  150  at a desired temperature. The water within the chamber  150  is heated to a temperature between approximately 35° C. and approximately 60° C. The preferred temperature of the water within the chamber  150  is 50° C. The constant, elevated temperature provided by the circulating water can contribute to uniform expansion, both circumferentially and longitudinally, of the ePTFE balloon, as well as uniform wall thickness. 
         [0063]    Referring to  FIGS. 9B and 10 , the balloon  112  can be inflated by introduction of pressurized fluid from the pump  154  to the lumen  114  of the ePTFE tube  110 . The overlying ePTFE tube  110  expands with the inelastic balloon  122  until both the balloon  112  and the ePTFE tube  110  obtain the predetermined size and shape of the inflated balloon  112 , step  224  of  FIG. 7 . The inflated balloon  112  thus imparts its predetermined size and shape to the ePTFE tube  110 . This radially expansion process is referred to as “blow-molding”. The PTFE tube  110  shown in  FIG. 9B  is radially expanded from the initial diameter d ( FIG. 9A ) to an increased diameter D. 
         [0064]    It is preferable for the ePTFE tube  110  to be plastically deformed by the radial expansion of the inelastic balloon  112 , step  226  of  FIG. 7 . The terms “plastic deformation” and “plastically deform,” as used herein, is intended to include the radial expansion of the ePTFE tube  110  beyond the elastic limit of the ePTFE material such that the ePTFE material is permanently deformed. Once plastically deformed, the ePTFE material forming the tube  110  becomes substantially inelastic, i.e., the ePTFE tube generally will not, on its own, return to its pre-expansion size and shape. 
         [0065]    The ePTFE tube  110  can be removed from the balloon  112  by removing the inflation fluid from the balloon  112  using the pump  154  and sliding the ePTFE tube  110  relative to balloon  112  and catheter  116 , i.e. in the direction of arrows A in  FIG. 9C , step  228  of  FIG. 7 . The tube  110  can be heat set at a temperature above the sinter point of the material forming the tube, 360° C. for ePTFE, to lock in the structure of the tube  110 , step  230  of  FIG. 7 . The pump  150  can be used to provide a slight vacuum within the balloon  112  to facilitate removal of the ePTFE tube  110 . 
         [0066]    The ePTFE tube  110  can be attached to a deployment mechanism such as hollow tube  20  described above, step  232  of  FIG. 7 . A suitable adhesive can be used to secure the ePTFE tube to the deployment mechanism. 
         [0067]    Referring to  FIG. 11 , an alternative method of manufacturing a radially expandable device employing a mold  202  is illustrated. The mold  202  includes two interconnected sections  204  and  206  forming an internal mold cavity  208  for receiving the ePTFE tube  110  with the balloon  112  positioned therein. The mold  202  is preferably constructed of a rigid, unyielding material such as a metal or metal alloy. Suitable metals or metal alloys include brass and steel alloys. The internal mold cavity  208  preferably has a size and shape analogous to that of the inflated balloon  112  to ensure that the inflated balloon  112 , and the overlying ePTFE tube  110  concentrically expand. 
         [0068]    Referring to the flow chart illustrated in  FIG. 13 , a further alternative method of manufacturing a fluid delivery device according to the teachings of the present invention will be described. A tube constructed of ePTFE is formed in accordance with the methods described above, step  410 . A tube formed of an extruded inelastic material such as PET is used in place of balloon  112  to radially expand the ePTFE tube. The extruded tube is positioned within the ePTFE tube  110 , step  412 . The extruded tube is then sealed at one end and attached to an inflation system at the other end, step  414 . The extruded tube can then be inflated by an inflation medium to radially expand the ePTFE tube, step  416 . The extruded tube and ePTFE tube are preferably heated to the glass transition temperature of the extruded tube, approximately 80° C.-100° C. for PET, as the extruded tube is inflated within the ePTFE tube. It is preferable to limit the temperature of the extruded tube to a temperature less than or equal to the glass transition temperature of the material forming the extruded tube to facilitate removal of the extruded tube from the ePTFE tube. Heating the extruded to a temperature above the glass transition temperature will cause the extruded tube to heat set in an expanded configuration, which makes removing the extruded tube from the ePTFE tube difficult. 
         [0069]    After the extruded tube and ePTFE tube are expanded to desired size and shape, the extruded tube is deflated and removed from the ePTFE tube, step  418 . The ePTFE tube is then heat set to lock in the structure of the ePTFE tube, step  420 . 
         [0070]    A mold, such as mold  202 , can be employed during radial expansion of the ePTFE tube using the PET tube. The mold is preferably heated within the hot water chamber of an inflation system, such as inflation system  148  illustrated in  FIG. 10 , or by other means such as a hot oil bath or through a steam, hot air, electric, radio frequency or infra red heat source. The mold can be constructed of a material having good head transfer characteristics, such as metal or metal alloy, for example brass. The mold includes a mold cavity having a size and shape analogous to the desired size and shape of the fluid delivery device  10  in the second diameter configuration. 
         [0071]    The resultant radially expanded ePTFE tube  110 , produced in accordance with the above described methods, provides a radially expandable fluid delivery device, such as the fluid delivery device  10  illustrated in  FIGS. 1 and 2  and described above, that is radially expandable from a relaxed, collapsed diameter to the second, increased diameter D upon application of a radial deployment force from a deployment mechanism within the tube  110 . Moreover, the microstructure of the radially expanded ePTFE tube  110  can be manufactured through the process of the present invention to have a porosity sufficient to permit fluid to flow therethrough. In particular, the microstructure of the resultant fluid delivery device is analogous to the microstructure of the ePTFE tube  110 , i.e. nodes interconnected by fibrils, the space between the nodes defining micro-channels through the wall of the device. 
         [0072]    One feature of the manufacturing processes of the present invention is that the microporous structure of the ePTFE tube  110  forming the fluid delivery device  10  can be manipulated by varying the extrusion and expansion process parameters to produce different porosity characteristics. For example the longitudinal stretch ratio of the ePTFE tube  110 , i.e., the ratio of final stretched length of the tube to the initial length, and the diametric stretch ratio of the ePTFE tube  110 , i.e., the ratio of the final diameter, after longitudinal stretching, and the initial diameter, and the stretch rate can be varied to yield fluid recovery devices having different porosity. Applicants determined that larger longitudinal stretch ratios, in the order of 2:1 to 3:1, can result in a ePTFE tube having a microstructure characterized by increased internodal distances and interstitial space, i.e., the micro-channels within the microstructure of the ePTFE tube are increase in sized. Suitable longitudinal stretch ratios can be from 1.1:1 to 10:1. 
         [0073]    Fluid delivery devices formed from ePTFE tubes having larger stretch ratios require minimal fluid pressure within the device to achieve the desired flow rate of fluid through the walls of the device. Such fluid delivery devices will consequently provide little radially-outward dilation force, which can be advantageous for some applications such as delivering therapuetic or diagnostic agents to healthy tissue. Conversely, ePTFE tubes having smaller stretch ratios result in fluid delivery devices that are less porous, as the internodal distances are reduced, and, thus, generally require increased fluid pressure to deliver the fluid. Such fluid delivery devices consequently provide increased radially outward dilation force, which can be advantageous for treatment applications such as reducing arterial lesions with pressure. Accordingly, the porosity of the ePTFE tube, and hence the porosity of the resultant fluid delivery device, is dependent on the stretch ratios of the expansion process. By manipulating the stretch ratios of the ePTFE tube, i.e. increasing or decreasing the stretch ratios, the porosity of the fluid delivery device can be tailored to the specific treatment application. 
         [0074]    The porosity of the ePTFE tube, and the subsequent fluid delivery device, can also depend on the density, the viscosity, the molecular weight, and the amount of lubricant used to form the billet used in the extrusion and expansion process. Increasing the amount by weight of lubricant or increasing the density or molecular weight of the lubricant, results in an extrudate having increased internodal distances and interstitial spaces prior to the step of expansion. Once stretched, the resultant ePTFE tube will reflect the increased porosity. 
         [0075]    The process described above can be used to produce fluid delivery devices having a uniform porosity though out the length of the device. To produce discrete microporous portions within the fluid delivery devices a number of different processes can be employed. For example, a coating can be applied at select locations to the inner and/or outer surfaces of the fluid delivery device to produce impermeable sections within the device. The coating preferable seals the microchannels within the microstructure of the device to inhibit or prevent fluid from passing therethrough. 
         [0076]    Alternatively, the porosity of the ePTFE tube can be selectively reduced subsequent to the step of expansion by applying heat to the select sections of the tube to return the sections to the pre-stretched porosity. The selectively heated sections will thus yield sections of reduced porosity. By controlling the amount of heat applied, the sections of reduced porosity can be made semi-permeable or impermeable to fluid. 
         [0077]    In addition to selecting and varying the porosity of the fluid recovery device through the manufacturing process of the present invention, the parameters of the manufacturing process can be varied to produce an ePTFE tube having distinct expansion characteristics. The size and shape of the fluid recovery device of the present invention can also be varied. These processes are described in detail in Applicants&#39; U.S. Pat. No. 6,395,208, which is incorporated herein by reference. 
         [0078]      FIG. 12  illustrates an exemplary embodiment of the fluid delivery device of the present invention in which the fluid delivery device  10  of  FIG. 1  is utilized as a catheter deployed dilation and diffusion balloon  300  for the treatment of a blood vessel  310  partially occluded by plaque deposits  312  adhered to the walls  314  of the blood vessel. This procedure is generally referred to as a Percutaneous Transluminal Angioplasty (PTA) procedure. The balloon  300  can be manufactured in accordance with the methods of the present invention and is shown in the expanded configuration. The ends  302  of the dilation balloon  300  are bonded to a catheter tube  320 , which is used to provide an inflation fluid to the balloon  300  to effect expansion of the balloon  300  to a predefined and fixed maximum diameter. A therapeutic agent, such as antisense oligonucleotides (AS-ODNs), can be delivered through the walls of the balloon with the inflation fluid. The AS-ODNs are delivered locally to the walls of the body vessel to suppress restenosis of the PTA roc vessel subsequent to the PTA procedure. 
         [0079]    A variety of therapeutic agents can be delivered with the fluid delivery device of the present invention. Exemplary therapeutic agents include: thrombolytics, antibiotics, chemotherapeutics, surfactants, diagnostic agents, steroids, hot saline, vasodilators, vasoconstrictors, and embolic agents. The localized delivery of thrombolytics, such as heparin, and urokinase, directly to the surface of thrombosed grafts or native body vessels can inhibit the-clotting of the graphs or native body vessels. The fluid delivery device of the present invention thus can be used as thrombolectomy balloon catheter to remove obstructions from grafts or native body vessels while concomitantly delivering thrombolytics to the walls of the graft or native body vessel. 
         [0080]    The fluid delivery device of the present invention can further be used for the localized delivery of high concentrations of antibiotics to treatment sites such as the ear canal, the throat, and the upper respiratory passages. Anti-cancer agents such as chemotherapeutics delivered using the fluid delivery device of the present invention can increase the effectiveness and negate the systemic side effects of the anti-cancer agents. Exemplary forms of cancer targeted for this application can include: rectal, esophageal, and lung cancer. Surfactants can be delivered directly to the lungs using the fluid delivery device of the present invention to treat cystic fibrosis or hyaline membrane disease. Diagnostic agents can be delivered during angiography procedures through the fluid delivery device of the present invention to improve the visibility of contrast agents delivered locally to the treatment site. The local delivery of steroids, such as anabolic steroids, using the fluid delivery device of the present invention can increase the effectiveness, e.g., promote muscle recovery, and negate systemic side effects such as lung and adrenal gland vantage. 
         [0081]    The fluid delivery device of the present invention can also be provided with hydrophilic or hydrophobic coatings dependant on the particular treatment applications. For example, fluid delivery devices constructed of ePTFE, a naturally hydrophobic material, can be coated with a hydrophilic coating to provide the fluid delivery device with a hydrophilic outer surface. A suitable hydrophilic coating is PHOTOLINK available from Surmodics of Eden Prairie, Minn. 
         [0082]    In an alternative embodiment illustrated in  FIG. 15 , the fluid delivery device of the present invention can be provided with multiple layers. The multi-layer fluid delivery device  500  includes a first layer  502  of biocompatible material, such as ePTFE, and a second layer  504  of biocompatible material that overlies the first layer  502 . The second layer  504  can be constructed from the same or a different biocmopatible material than the first layer  502 . As shown in  FIG. 15 , the first layer  502  and the second layer  504  are preferably coexentsive, however, the second layer  504  need not extend the entire length of the first layer  502 . Likewise, the first layer  502  may be smaller in length than the second layer  504 . 
         [0083]    The first layer  502  and the second layer  504  can each be formed from a separate ePTFE tube. The ePTFE tubes can be constructed in accordance with the manufacturing methods of the present invention such that each tube is characterized by a microstructure of nodes interconnected by fibrils. Preferably the nodes are oriented generally perpendicular to the longitudinal axis. The two ePTFE tubes can then be coaxially disposed and heated to bond the two tubes together. The bonded tubes can be radially expanded by a balloon in accordance with the above manufacturing methods of the present invention. By producing the ePTFE tubes forming the first and second layers using different process parameters, e.g. different stretch ratios or stretch rates, the distance between the nodes can varied between the ePTFE tubes. For example, the internodal distances of the microstructure of the first layer  502  can be generally greater than the internodal distances of the microstructure of the second layer  504 . In this manner, the porosity of the first layer  502  and the porosity of the second layer  504  can be different. 
         [0084]    Although the multi-layer fluid delivery device  500  illustrated in  FIG. 15  includes two layers, additional layers can be provided. Additional layers can be formed from further ePTFE tubes or through other methods, such as by wrapping ePTFE film about the first layer and/or second layer. 
       Example 1 
       [0085]    An exemplary fluid delivery device was constructed according to the manufacturing processes of the present invention by employing 0.068″ (ID)/0.088″ (OD) ePTFE tubing. The longitudinal stretch ratio of the ePTFE tube was 1.5:1, at a stretch rate of 10 inches per second. An electron micrograph of an exterior section of a sample ePTFE tube, after stretching, is shown in  FIG. 14A .  FIG. 14A  illustrates the microstructure of nodes interconnected by fibrils of the ePTFE tubing and, in particular, the orientation of the nodes generally perpendicular to the longitudinal axis of the tubing and the internodal through-pores. An 8 mm×8 cm PET balloon was employed to radially expand the ePTFE tubing. The PET balloon was attached to a vacuum source and a slight vacuum was placed on the PET balloon, about −5 to −10 psi. The ePTFE tubing was then positioned over the deflated PET balloon. The PET balloon and the ePTFE tubing were then connected to a hypo-tube and placed into a water heated chamber. Saline was injected into the PET balloon at a constant flow rate of about 10-15 ml/min. When the pressure within the balloon reached 70-80% of the rated balloon pressure, about 12-15 atm for the PET balloon employed, the flow rate was decreased to 2 ml/min. The balloon was then brought to its rated balloon pressure. The water was then removed from the PET balloon using the pump until a slight vacuum existed within the PET balloon (−5 to −10 psi). The hypo-tube was then removed from the chamber and the ePTFE tube was withdrawn from the balloon. The proximal I.D. of the resultant ePTFE tube was approximately ⅔ Fr larger than the distal I.D. 
         [0086]    The resultant ePTFE balloon was then allowed to completely dry. The ePTFE balloon was cut to a desired length and the proximal tail of the ePTFE balloon was dipped into Loctite 7701 Prism Primer, available from Loctite, Corp. of Rocky Hill, Conn. The distal tail of the ePTFE balloon was then dipped into the primer. The primer was allowed to evaporate for at least two minutes. The ePTFE balloon was then placed on a 5 Fr-4 Fr tipped catheter by pulling the proximal end of the ePTFE balloon onto the 5 Fr end of the catheter body until the distal (4 Fr) end is about 0.1″ from the tip of the catheter. The location of the proximal tail of the ePTFE balloon was then marked on the catheter and the ePTFE balloon was removed from the catheter. Loctite 4011 adhesive was then applied to the catheter shaft at a location slightly distal to the marked position. The ePTFE balloon was then slid back onto the catheter shaft until the proximal end was aligned with the mark. The adhesive was allowed to dry for one minute. A small volume of Loctite 4011 adhesive was dispensed onto the distal end of the catheter shaft adjacent to the distal end of the ePTFE balloon. This adhesive was drawn into the gap between the catheter and the balloon by capillary forces. The adhesive was then allowed to dry for at 24 hours. 
         [0087]    An electron micrograph of an exterior section of a sample ePTFE balloon is shown in  FIGS. 14B-14D .  FIG. 14B  illustrates the microstructure of nodes interconnected by fibrils of the body of the ePTFE balloon.  FIGS. 14C and 14D  are cross-sections of the neck of the ePTFE balloon at varying magnifications.  FIGS. 14B-14D  illustrate the internodal through-pores or channels of the ePTFE balloon as defined by the microfibrillar spaces between the nodes. The through-pores are oriented generally perpendicular to the longitudinal axis of the ePTFE balloon and provide fluid pathways between the inner surface and the outer surface of the ePTFE balloon. 
       Example 2 
       [0088]    Three ePTFE synthetic grafts were treated using an ePTFE diffusion balloon constructed in accordance with the method of Example 1 to determine the permeability of a contrast agent into the grafts. The diffusion balloon employed was 8 cm in length, had an OD of 6 mm and was constructed from an 0.088″ (OD)/0.068″ (ID) ePTFE tube having a stretch ratio of 1.5:1. Each of the grafts treated was an Atrium Hybrid PTFE graft, model no. 01200670, available from Atrium Medical of Hudson, N.H. The grafts had a 6 mm inner diameter and a wall thickness of 0.025 inches. In each case, the balloon was inserted into a graft and inflated by infusing a contrast agent. The balloon was inflated to 1 atm. by the infused fluid. The balloon was then removed from the graft and the graft was flushed with water delivered at 500 ml/min. The contrast agent used was Hypaque-76 available from Mycomed, Inc. Table 1 summarizes each procedure. 
         [0000]    
       
         
               
               
               
               
             
               
               
               
               
             
           
               
                 TABLE 1 
               
               
                   
               
               
                   
                 Duration of Balloon 
                 Balloon Infusion 
                 Graft Flushing 
               
               
                 Graft Sample 
                 Infusion 
                 Fluid 
                 Duration 
               
               
                   
               
             
             
               
                   
               
             
          
           
               
                 1 
                 15 seconds 
                 Saline &amp; Contrast 
                 5 minutes 
               
               
                   
                   
                 Agent 
                   
               
               
                 2 
                 15 seconds 
                 Saline &amp; Contrast 
                 30 seconds 
               
               
                   
                   
                 Agent 
                   
               
               
                 3 
                 15 seconds 
                 Saline 
                 No Flushing 
               
               
                 (Control) 
                   
                   
                   
               
               
                   
               
             
          
         
       
     
         [0089]    X-rays were taken of each of the grafts samples to determine if the contrast agent was present in the grafts post infusion and perfusion (flushing). Table 2 summarizes the results of the X-rays for each graft. 
         [0000]    
       
         
               
               
               
             
               
               
               
             
           
               
                   
                 TABLE 2 
               
               
                   
                   
               
               
                   
                 Graft Sample 
                 Presence of Contrast Agent 
               
               
                   
                   
               
             
             
               
                   
               
             
          
           
               
                   
                 1 
                 Yes 
               
               
                   
                 2 
                 Yes 
               
               
                   
                 3 
                 No 
               
               
                   
                   
               
             
          
         
       
     
         [0090]    Contrast agent was found in the walls of the both ePTFE graft samples infused with contrast agent by the diffusion balloon of the present invention, but not in the control sample. In graft samples 1 and 2, the contrast agent was found to have permeated through the entire wall of the graft. Flushing the grafts with water post infusion was determined to have no effect on the presence and concentration of the delivered contrast agent. 
       Example 3 
       [0091]    The permeability of several ePTFE fluid delivery devices constructed in accordance with the manufacturing processes of the present invention was evaluated and compared with the permeability of selected synthetic grafts. Each of the fluid delivery devices was constructed from an extruded and expanded ePTFE tube as set forth in Table 3. 
         [0000]    
       
         
               
               
               
               
               
             
               
               
               
               
               
             
           
               
                 TABLE 3 
               
               
                   
               
               
                 Fluid  
                 Stretch 
                 Stretch  
                 Wall  
                 Surface  
               
               
                 Delivery 
                 Ratio of 
                 Rate of 
                 Thickness of 
                 Area of 
               
               
                 Device 
                 ePTFE  
                 ePTFE tube 
                 Fluid Delivery 
                 Fluid Delivery 
               
               
                 Sample 
                 tube 
                 (in/s) 
                 Device (in) 
                 Device (in 2 ) 
               
               
                   
               
             
             
               
                   
               
             
          
           
               
                 1 
                 1.5:1   
                 20 
                 0.0068 
                 0.456 
               
               
                 2 
                 1.75:1   
                 10 
                 0.0055 
                 0.469 
               
               
                 3 
                 3:1 
                 10 
                 0.005 
                 0.469 
               
               
                 4 
                 5.1 
                 10 
                 0.003 
                 0.503 
               
               
                 5 
                 125:1  
                 10 
                 0.0075 
                 0.399 
               
               
                 6 
                 1.5:1   
                 0.5 
                 0.0055 
                 0.399 
               
               
                 7 
                 1.5:1   
                 10 
                 0.005 
                 0.399 
               
               
                 8 
                 1.5:1   
                 10 
                 0.005 
                 0.29 
               
               
                   
               
             
          
         
       
     
         [0092]    The synthetic grafts analyzed were standard and thin wall grafts available from Atrium Medical. Corporation and W. L. Gore &amp; Associates, Inc. Information regarding the grafts is set forth in Table 4 
         [0000]    
       
         
               
               
               
               
             
               
               
               
               
             
           
               
                 TABLE 4 
               
               
                   
               
               
                 Graft sample 
                 Type 
                 Wall Thickness (in) 
                 Surface Area(in 2 ) 
               
               
                   
               
             
             
               
                   
               
             
          
           
               
                 A 
                 Atrium 6 mm std 
                 0.025 
                 0.964 
               
               
                 B 
                 Atrium 6 mm thin 
                 0.022 
                 0.963 
               
               
                 C 
                 Gore 7 mm thin 
                 0.016 
                 1.143 
               
               
                 D 
                 Gore 6 mm std 
                 0.024 
                 0.963 
               
               
                 E 
                 Gore 4 mm 
                 0.025 
                 0.59 
               
               
                 F 
                 Atrium 4 mm 
                 0.02 
                 0.49 
               
               
                   
               
             
          
         
       
     
         [0093]    The fluid delivery devices and the synthetic grafts were infused with a fluid to determine the permeability of the samples. The permeability of each of the samples is reflected by the hydrodynamic resistance and the hydraulic conductivity data set forth in Table 5. 
         [0000]    
       
         
               
               
               
             
               
               
               
             
           
               
                 TABLE 5 
               
               
                   
               
               
                   
                 Hydrodynamic resistance 
                 Hydraulic Conductivity 
               
               
                 Sample 
                 (psi * min * mL -1 ) 
                 (cm 4 /(dyne* s) * 10 12 ) 
               
               
                   
               
             
             
               
                   
               
             
          
           
               
                 1 
                 21.2 
                 67 
               
               
                 2 
                 7.18 
                 155 
               
               
                 3 
                 2.76 
                 368 
               
               
                 4 
                 2.81 
                 202 
               
               
                 5 
                 13.4 
                 134 
               
               
                 6 
                 1.59 
                 825 
               
               
                 7 
                 1.5 
                 795 
               
               
                 8 
                 1.7 
                 966 
               
               
                 A 
                 2.394 
                 1031 
               
               
                 B 
                 1.03 
                 2112 
               
               
                 C 
                 0.711 
                 1874 
               
               
                 D 
                 0.623 
                 3808 
               
               
                 E 
                 1.5 
                 2673 
               
               
                 F 
                 1.2 
                 3207 
               
               
                   
               
             
          
         
       
     
         [0094]    Hydraulic conductivity was determined using Darcy&#39;s Law for describing steady flow through a porous media. Darcy&#39;s law is defined in Equation 1 as 
         [0000]        Q/A=−K (Δ P/ΔX ),  (Eq. 1)
 
         [0095]    where Q is flow rate, A is cross sectional area for flow, i.e. the surface area of the sample, P is pressure, X is wall thickness, and K is the hydraulic conductivity. 
         [0096]    Applicants determined that the permeability of a fluid delivery device relative to the permeability of the vessel being treated is an important consideration in establishing effective fluid delivery into the walls of the vessel. In particular, for a given fluid flow rate and pressure, a greater volume of fluid will penetrate the walls of a vessel being treated if the permeability of the vessel is greater than the permeability of the fluid delivery device. Accordingly, it is desirable for the permeability of the fluid delivery device to be less than the permeability of the vessel being treated. The permeability of the fluid delivery device can be tailored to be less than the vessel being treated by varying the process parameters of the manufacturing processes described above. The process parameters include lubricant density, lubricant viscosity, lubricant molecular weight, longitudinal stretch ratio, and stretch rate. 
         [0097]    The permeability data set forth in Table 5 illustrates that the permeability, when measured in terms of the hydraulic conductivity, for each of the fluid delivery devices tested was less than the permeability of each of the synthetic grafts tested. This indicates that the Applicants&#39; fluid delivery device may be particularly effective for delivering fluid to the walls of synthetic grafts. 
         [0098]    Applicants have determined that it is desirable for the hydraulic conductivity of the fluid delivery device to be less than 1000 (cm 4 /(dyne*s)*10 12 ) for treatment of synthetic grafts. Preferably, the fluid delivery device has a hydraulic conductivity of less than 500 (cm 4 /(dyne*s)*10 12 ). For treatment of natural body vessels and grafts, it is preferable for the hydraulic conductivity of the fluid delivery device to be less than 100 (cm 4 /(dyne*s)*10 12 ). 
         [0099]    It will thus be seen that the invention efficiently attains the objects made apparent from the preceding description. Since certain changes may be made in the above constructions without departing from the scope of the invention, it is intended that all matter contained in the above description or shown in the accompanying drawings be interpreted as illustrative and not in a limiting sense. 
         [0100]    It is also to be understood that the following claims are to cover all generic and specific features of the invention described herein, and all statements of the scope of the invention which, as a matter of language, might be said to fall therebetween.