Abstract:
Exemplary embodiments of the present invention teach a structure and process for forming an array of storage capacitors by forming a first set of individual storage node plates, forming alternating storage node pillars, forming a second set of individual storage node plates, forming a cell dielectric material on individual storage node plates, and forming a second capacitor plate over the first and second sets of individual storage node plates. The resulting structure comprises generally parallel running conductive word lines, a first set of individual storage node plates, storage node pillars alternating with individual storage node plates of the first set of individual storage node plates, a second set of individual storage node plates, a cell dielectric material on the first and second sets of individual storage node plates, and a second capacitor plate overlying the first and second sets of individual storage node plates.

Description:
This application is a divisional to U.S. patent application Ser. No. 09/698,887, filed Oct. 27, 2000, now U.S. Pat. No. 6,518,611 which is a continuation to U.S. patent application Ser. No. 09/160,232, now U.S. Pat. No. 6,153,899, filed Sep. 24, 1998 and issued Nov. 28, 2000, which is a divisional to U.S. patent application Ser. No. 08/893,931, now U.S. Pat. No. 5,851,875, filed Jul. 14, 1997 and issued Dec. 22, 1998. 
    
    
     FIELD OF THE INVENTION 
     This invention relates to semiconductor fabrication processing and more particularly to a structure and process for forming an array of capacitors for a dynamic random access memory device. 
     BACKGROUND OF THE INVENTION 
     The continuing trend of scaling down integrated circuits has forced the semiconductor industry to consider new techniques for fabricating precise components at sub-micron levels. Along with the need for smaller components, there has been a growing demand for devices requiring less power consumption. In the manufacture of transistors, these trends have led the industry to refine approaches to achieve thinner cell dielectric and gate oxide layers. 
     In dynamic semiconductor memory storage devices it is essential that storage node capacitor cell plates be large enough to retain an adequate charge (or capacitance) in spite of parasitic capacitance and noise that may be present during circuit operation. As is the case for most semiconductor integrated circuitry, circuit density is continuing to increase at a fairly constant rate. The issue of maintaining storage node capacitance is particularly important as the density of dynamic random access memory, (DRAM) arrays continues to increase for future generations of memory devices. The ability to densely pack storage cells while maintaining required capacitance levels is a crucial requirement of semiconductor manufacturing technologies if future generations of expanded memory array devices are to be successfully manufactured. 
     As disclosed in U.S. Pat. No. 5,418,180, and U.S. Pat. No. 5,407,534, Hemi-Spherical Grain (HSG) silicon enhances storage capacitance when used to form the storage node electrode without increasing the area required for the cell or the storage electrode height. 
     A disadvantage of using HSG to form a capacitor structure (such as a container type structure) in a deep sub-micron process (a process utilizing is lines width of less than 0.25 microns) is that a small change in the processing conditions may result in the grains of the silicon to overgrow and form discontinuous islands. When the size of the container formation needs to be reduced to such a degree that only a thin film is feasible, the grain formation could quite possibly consume all of the silicon film and form completely isolated grains. Additionally, the space between containers needs to have enough margin to prevent shorts that can be caused by subsequent chemical cleaning. Furthermore, capacitor plate surface enhancement is a function of grain size when HSG is used and a grain size of 700-800 angstroms has been found to provide sufficient surface enhancement. However, a 700-800 angstrom grain size will not fit into a 0.18 μm or less container structured capacitor plate. 
     The present invention, develops a method to fabricate a capacitor structure for sub-micron fabrication processes. In particular, the present invention provides a capacitor fabrication solution for processes using a device geometry of 0.18 μm or smaller. 
     U.S. Pat. No. 5,418,180 and U.S. Pat. No. 5,407,534, are hereby incorporated by reference as if set forth in their entirety. 
     SUMMARY OF THE INVENTION 
     An exemplary implementation of the present invention teaches a process for fabricating a capacitor array for a semiconductor device by forming a first set of individual storage node plates for a first set of storage capacitors; forming a set of storage node pillars, the pillars alternating in position with the individual storage node plates of the first set of individual storage node plates, the storage node pillars being approximately equal in height to neighboring storage node plates. Next, a second set of individual storage node plates are formed so that each individual storage node plate is physically connected to an individual storage node pillar. Next, a cell dielectric material is formed on the first and second sets of individual storage node plates; and finally second capacitor plates are formed over the cell dielectric material and consequently the first and second sets of individual storage node plates. 
     Another exemplary implementation of the present invention is a memory array comprising conductive word lines running in a generally parallel direction to one another; a first set of individual storage node plates for a first set of storage capacitors; storage node pillars that alternate in position with the individual storage node plates of the first set of individual storage node plates, the storage node pillars being approximately equal in height to neighboring storage node plates; a second set of individual storage node plates for a second set of storage capacitors, each individual storage node plate of the second set physically connecting to an individual storage node pillar; a cell dielectric material on the first and second sets of individual storage node plates; and a second capacitor plate over the first and second sets of individual storage node plates. 
    
    
     BRIEF DESCRIPTION OF THE DRAWINGS 
     FIG. 1A, is a simplified overhead view taken during a patterning stage of the present invention depicting an array of conductive plugs positioned along a pair of conductive lines. 
     FIG. 1B, is a cross-sectional view of FIG. 1A, depicting storage capacitor access transistors followed by the formation of conductive plugs. 
     FIG. 2A, is a simplified overhead view taken during a patterning stage of the present invention depicting an array of alternating large and small conductive spheres representing lower storage node capacitor plates (large ovoids) and conductive plugs (small ovoids) positioned along a pair of conductive lines. 
     FIG. 2B, is a cross-sectional view of FIG. 2A, depicting the formation of a lower storage node capacitor plate and a conductive extension plug. 
     FIG. 2C, is an alternate embodiment showing a cross-sectional view of FIG. 2A, depicting the formation of a lower storage node capacitor plate, a conductive extension plug and texturizing the lower storage node capacitor plate. 
     FIG. 3A, is a simplified overhead view taken during a patterning stage of the present invention depicting an array of overlapping large conductive spheres representing lower storage node capacitor plates being overlapped by storage node capacitor plates, all of which are positioned along a pair of conductive lines. 
     FIG. 3B, is a cross-sectional view of FIG. 3A, depicting the formation of an upper storage node capacitor plate. 
     FIG. 3C, is an alternate embodiment showing a cross-sectional view of FIG. 3A, depicting the formation of an upper storage node capacitor plate and texturizing of the upper storage node capacitor plate. 
     FIG. 4A, is an alternate embodiment showing a continuing cross-sectional view of FIG. 3B, depicting the formation of HSG: silicon on both the inside and outside surfaces of a storage node capacitor plate, the formation an storage capacitor cell dielectric and a second storage capacitor plate. 
     FIG. 4B, is a continuing cross-sectional view of FIG. 3B, depicting the formation of an storage capacitor cell dielectric and a second storage capacitor plate. 
     FIG. 4C, is an alternate embodiment showing a continuing cross-sectional view of FIG. 3C, depicting the formation of an storage capacitor cell dielectric and a second storage capacitor plate. 
    
    
     DETAILED DESCRIPTION OF THE INVENTION 
     Exemplary implementations of the present invention are directed to a capacitor structure and process for forming a capacitor structure as depicted in FIGS. 1 through 4C. An exemplary implementation is depicted in the cross-sectional views of FIGS. 1B,  2 B,  3 B and  4 B. Another exemplary implementation is depicted in cross-sectional views of FIGS. 2C,  3 C and  4 C. Still another exemplary implementation is depicted in cross-sectional views of FIGS. 1B,  2 B,  3 B and  4 A. 
     Referring to FIG. 1A, this overhead view shows an array of conductive plugs  16  positioned along a pair of conductive lines  13   a  and  13   b . In this figure, two conductive lines run in a generally parallel direction to another which depict an exemplary implementation of the present invention, representing a plurality of word lines that would be present in a memory array, such as a dynamic random access memory (DRAM). The following descriptions of the cross-sectional views are written to describe the formation of a single structure. However, it is intended that, though only a single structure is shown and described, a plurality of structures are being formed to create an array of such structures. 
     Referring to FIG. 1B, this view shows a silicon substrate  10  fabricated to form storage capacitor access transistors made up of source/drain diffusion areas  11   a  and  11   b  formed in substrate  10 . The source/drain diffusion areas  11   a  and  11   b  are spanned by a conductive word lines  13   a  and  13   b  which, in turn, serve as access transistor gates. In this view an entire access transistor is not seen as a portion of the transistor&#39;s diffusion area is outside of the cross-sectional view (refer to the diffusion area  11   a  shown in FIG.  1 A). Furthermore, the separate diffusion areas  11   a  and  11   b  are labeled as such in order to indicate that capacitors formed later in the process, associated with diffusion areas  11   a  and  11   b , are coupled to a different set of digit lines (the formation of the digit lines are not discussed). 
     Isolation material  12 , such as field oxidation, separate active areas  11   a  and  11   b  defined for the storage capacitor access transistors. Once the access transistors have been formed, a first thick insulation layer  14 , such as a chemical vapor deposition, (CVD) oxide or an oxide grown from tetraethylorthosilicate (TEOS), is formed over the access transistors and over isolation material  12 . This first thick insulation layer  14  is planarized and patterned so that a subsequent etch will form openings  15  in insulation layer  14  to provide access to underlying first and second diffusion areas  11   a  and  11   b . Next, a conductive material, such as conductively doped polysilicon or a metal, is formed such that it fills openings  15 . The conductive material is then planarized to form conductive plugs  16 . 
     Referring to FIG. 2A, this overhead view shows the result of an alternating pattern of large and small ovoids (or ellipses) and is intended to show the formation of a first level of capacitor storage nodes plates  22  (large ovoids) and conductive extension plugs  21  (small ovoids) which will be formed after the next defined processing steps. Conductive plugs  16  (also shown as small ovoids) were formed in previous processing steps. 
     Referring to FIG. 2B the process steps to define the above structures are set forth. A second thick insulation layer  20 , such as Borophosphosilicate glass (BPSG), is formed over the planarized first thick insulation layer  14  and over planarized conductive plugs  16 . The second insulation layer  20  is planarized and patterned so that a subsequent etch will form first and second openings  22   a  and  21   a  in second insulation layer  20  to provide access to underlying conductive plugs  16 . First opening  22   a  is patterned and etched so that it is large enough to except the formation of a storage node capacitor plate. During the same patterning and etching step, second opening  22   a  is created to provide access to second conductive plug  16 . Next, a conductive material, such as, for example, conductively doped polysilicon, is formed such that it conforms to the geometry of first opening  22   a  and at the same time fills second opening  21   a  The conductive material is then planarized to form a lower conductive storage node capacitor plate  22  and a conductive extension plug  21  (or storage node pillars). If conductively doped polysilicon is used, the polysilicon may be doped insitu during polysilicon deposition or the polysilicon may be doped after polysilicon deposition by such methods as implanting or diffusion. 
     In an alternate embodiment and referring to FIG. 2C, while lower plate  22  is Hemi-Spherical Grain (HSG) silicon  23  is deposited onto lower plate  22 . The HSG silicon may be formed by various methods known to those skilled in the art and in particular by the methods of HSG formation as disclosed in U.S. Pat. No. 5,418,180 and 5,407,534. The use of HSG silicon will increase the capacitance of storage node capacitor plate  22  by increasing the plate&#39;s surface area. 
     Referring to FIG. 3A, this overhead view shows the overlapping of large ovoids  22  and  32  and is intended to show the formation of a second level of capacitor storage nodes plates  32  which overlap the previously formed first level of capacitor storage nodes plates  22 . 
     Referring to FIG. 3B, a third thick insulation layer  30 , such as, again an CVD oxide or an oxide formed from TEOS, is formed over the planarized second thick insulation layer  20 , lower storage node capacitor plate  22  and planarized conductive extension plug  21 . The third thick insulation layer  30  is planarized and then covered with a fourth thick insulation layer  31 , such as BPSG. Next, the fourth thick insulation layer  31  is patterned so that a subsequent etch will form an opening in fourth insulation layer  31  until the underlying third thick insulating layer  30  is reached. At this point a facet etch, such as an angled sputter etch or reactive ion etch, is performed to provide access to underlying conductive extension plug while creating sloped side walls in third thick insulating layer  30  so that a portion of third thick insulating layer  30  remains intact to completely cover lower storage node capacitor plate  22 . This will ensure complete isolation between an upper storage node capacitor plate  32  that is to be formed in this opening and lower storage node capacitor plate  22 . This opening is patterned large enough to except the formation of storage node capacitor plate  32  and will also overlap the edge of underlying lower storage node capacitor plate  22 , but as previously stated, the upper and lower storage node capacitor plate will be completed isolated from one another other. Next, a conductive material, such as conductively doped polysilicon, is formed such that it conforms to the geometry of opening. The conductive material is then planarized to form a conductive upper storage node capacitor plate  32 , which overlaps the lower storage node capacitor plate  22 . As before, if conductively doped polysilicon is used to form storage node capacitor plate  32 , the polysilicon may be doped insitu during polysilicon deposition or the polysilicon may be doped after polysilicon deposition by such methods as implanting or diffusion. 
     In an alternate embodiment and referring to FIG. 3C, while upper plate.  32  is exposed, Hemi-Spherical Grain (HSG) silicon  33  is deposited onto upper plate  32 . As before, the HSG silicon may be, formed by various methods known to those skilled in the art and in particular by the methods of HSG formation as disclosed in U.S. Pat. Nos. 5,418,180 and 5,407,534. This HSG silicon will increase the capacitance of storage node capacitor plate  32  by increasing the plate&#39;s surface area. 
     Referring to FIGS. 4A and 4B, an isotropic etch is performed that will remove all of fourth thick insulation layer  31  and, a portion of third thick insulation layer  30 . This etch must be performed long enough to ensure that all of the insulation is cleared from the inner surface of lower storage node capacitor plate  22 . At this point, as shown in FIG. 4A, it is desirable to texturize the exposed surfaces (both the inner and outer surfaces) of both the lower and upper storage node capacitor plates  22  and  32 . 
     Alternatively, as shown in FIG. 4B, lower plate  22  and upper plate  32  need not be texturized if sufficient surface area is obtained. However, the overlapping of the storage node plates will allow sufficient surface area to except texturization of the storage node plates by such methods as depositing Hemi-Spherical Grain (HSG) silicon. In fact, a major advantage of the present invention is the overlapping of the upper and lower storage node plates  22  and  32  which will allow the creation of storage capacitors having adequate capacitance to effectively store a charge for a duration necessary for data retention in DRAMs using a device geometry process of 0.18 micrometers (μm) or less. The present invention further provides for the formation of an array of storage capacitors that are relatively consistent in capacitor plate surface area and thus relatively constant in capacitance (a desired capacitance range of 20 to 30 fF for each capacitor) from capacitor to capacitor. 
     Continuing with either FIGS. 4A and 4B, once the conductive surfaces of the lower and upper plates are fabricated as, desired, a storage capacitor cell dielectric  40  is formed next to the conductive surfaces of each lower and upper plate  22  and  33 . Finally, a second capacitor plate  41  is formed over the lower and upper storage capacitor plates to complete the formation of a storage cell comprising an access transistor and a storage capacitor. 
     In an alternate embodiment and referring to FIG. 4C, the inner surfaces of upper and lower plates  22  and  32  have been textured in accordance with the process steps of FIGS. 2C and 3C. Next, a storage capacitor cell dielectric  42  is formed next to the conductive surfaces of each lower and upper plate  22  and  33 . Finally, a second capacitor plate  43  is formed over the lower and upper storage capacitor plates to complete the formation of a storage cell comprising an access transistor and a storage capacitor. 
     Referring back to FIG. 3A, contact  35  shows the location for a contact between an exposed diffusion region and a second conductive line, such as for a digit or bit line in a DRAM. This contact can be formed using conventional fabrication techniques after the second storage cell plate is formed. Alternatively, the exemplary embodiments of the present invention may also be implemented in a process that forms buried digit lines where the word lines and storage capacitors are built over the buried digit lines. In fact, the present invention may integrate into a buried digit line process very effectively. 
     It is to be understood that although the present invention has been described with reference to a preferred embodiment, various modifications, known to those skilled in the art, may be made to the structures and process steps presented herein without departing from the invention as recited in the several claims appended hereto.