Abstract:
A catalytic conversion process which comprises catalytic cracking reaction of a hydrocarbon feedstock contacting with a medium pore size zeolite enriched catalyst in a reactor, characterized in that reaction temperature, weight hourly space velocity and catalyst/feedstock ratio by weight are sufficient to achieve a yield of fluid catalytic cracking gas oil between 12% and 60% by weight of said feedstock, wherein said weight hourly space velocity is between 25 h −1  and 100 h −1 , said reaction temperature is between 450° C. and 600° C., and said catalyst/feedstock ratio by weight is between 1 and 30. This invention relates to a catalytic conversion process, especially for heavy feedstock oil to produce higher octane gasoline and an enhanced yield of propylene. More particularly, the invention relates to a process to utilize petroleum oil resources efficiently for decreasing the yield of dry gas and coke significantly.

Description:
FIELD OF THE INVENTION 
       [0001]    This invention relates to a catalytic conversion process. More particularly, the invention relates to a catalytic conversion process for converting heavy feedstocks into high octane gasoline and an enhanced yield of propylene, wherein the yields of dry gas and coke decrease significantly, thereby petroleum oil resources are utilized efficiently. 
       BACKGROUND OF THE INVENTION 
       [0002]    Light olefins such as propylene are important organic chemical feedstocks. Commercial propylene is used to produce polypropylene, acrylonitrile and other chemicals. The propylene requirement is increasing year by year with a sharply increasing demand for polypropylene derivates. Worldwide annual propylene requirement amount increased from 15.2 million tons of twenty years ago to 51.2 million tons in 2000 and average annual increasing rate was 6.3%. It is estimated that there will be 86 million tons of propylene requirement in 2010 and average annual increasing rate will be 5.6% during that period. 
         [0003]    Steam cracking and fluid catalytic cracking (FCC) are the main processes to produce propylene. Light oil such as naphtha can be used as the feedstock in steam cracking to produce ethylene and propylene, and the yield of propylene is only about 15% by weight. However, the feedstock of FCC process is heavy oil such as vacuum gas oil (VGO). Currently, 61% amount of propylene is from a byproduct of steam cracking process which produces ethylene, and 34% amount of propylene is produced by FCC, and about 5% amount of propylene is produced by propane dehydrogenation and ethylene-butene metathesis process. 
         [0004]    Petrochemical industry will face to the shortage of light feedstock, deficiency of the processing capacity, high cost and other restrictive factors if ethylene and propylene are produced by the conventional petrochemical process such as steam cracking. 
         [0005]    The role of FCC is increasingly concerned since FCC has advantage of wide adaptability of feedstock and flexible operation. Almost 50% amount of propylene is from FCC in U.S.A. The catalytic cracking technology with enhanced propylene yield is being improved quickly. 
         [0006]    U.S. Pat. No. 4,980,053 discloses a process to produce gaseous olefins by catalytic conversion of hydrocarbons. Various fractions of petroleum, including residual oils and crude oils, are catalytically converted in fluidized or moving bed reactors with solid, acidic catalysts at a temperature of 500° C. to 650° C., and a pressure of 0.15 MPa to 0.3 MPa, with a weight hourly space velocity of 0.2 hr −1  to 20 hr −1  and catalyst to oil ratio of 2 to 12. Catalyst is continuously recycled between the reactor and the regenerator. The total yield of propylene and butene is about 40% by weight of the feedstock, and propylene yield is about 26.34% by weight of the feedstock. 
         [0007]    WO00/31215A1 discloses a process for catalytic cracking to produce light olefin, which uses the catalyst comprising ZSM-5 and/or ZSM-11 as active component and much of inert substance as matrix. However, the yield of the propylene is less than 20% by weight of VGO. 
         [0008]    U.S. Pat. No. 4,422,925 discloses a fluid catalytic cracking process in which a plurality cracking performance of hydrocarbon feedstocks including at least one gaseous paraffinic hydrocarbon feedstock and at least one liquid hydrocarbon feedstock are subjected to different cracking reaction conditions in several reaction zones in the present of regenerated catalyst to produce enhanced yield of light olefins. 
         [0009]    Preserved amount of gasoline automobile has progressed rapidly due to economic development and the requirement of high quality gasoline is increasing. Presently improving gasoline octane number technologies include catalytic reforming, alkylation, isomerization, adding an gasoline octane number enhancing additive, and the like. The advantage of catalytic reforming is the heavy fraction of gasoline having high octane number, however, the octane number of light fraction gasoline is lower, in particular, the reforming catalyst cost is higher and the quality of feedstock is strictly required. Alkylation and isomerization technology can produce high octane number and good sensitivity gasoline which is a desirable high octane number clean gasoline component, there is, however, corrosion and environmental protection problem with the used catalyst. The octane number enhancing additive such as MTBE and ETBE can increase gasoline octane number and improve automobile performance, but the cost is higher. Catalytic cracking gasoline is a main source of automobile gasoline pool. The octane number of catalytic cracking gasoline is affected by lower octane number heavy gasoline fraction. Generally, the quality of FCC diesel is worse than straight-run diesel oil. FCC diesel oil is rich in mono ring aromatic hydrocarbons, which can be catalytically converted to high octane gasoline component and propylene product. 
         [0010]    The prior arts are insufficient in paraffin molecules catalytic conversion, therefore the dry gas is increasing sharply when the propylene yield grows. Because of underutilization of the gasoline potential content of diesel oil which can produce high octane gasoline and light olefins, there still have room to improve for the quality and yield of gasoline. Therefore, it is desirable to develop a process for catalytic cracking of heavy feedstocks to produce an enhanced yield of high octane number gasoline and an enhanced yield of propylene to meet the market requirements of light olefin and gasoline. 
       SUMMARY OF THE INVENTION 
       [0011]    An object of the present invention is to provide a catalytic conversion process; in particular, for converting heavy feedstocks into high octane gasoline and an enhanced yield of propylene, wherein the yields of dry gas and coke decrease significantly, thereby petroleum oil resources are utilized efficiently. 
         [0012]    In an embodiment of the present invention, a catalytic conversion process provided by the present invention comprises catalytic cracking reaction of a hydrocarbon feedstock contacting with a medium pore size zeolite enriched catalyst in a reactor, characterized in that reaction temperature, weight hourly space velocity (WHSV) and catalyst/feedstock ratio by weight (C/O) are sufficient to achieve a yield of fluid catalytic cracking gas oil (FGO) between 12% and 60% by weight of said feedstock, wherein said WHSV is between 25 h −1  and 100 h −1 , said reaction temperature is between 450° C. and 600° C., and said C/O is between 1 and 30. 
         [0013]    In the more preferred embodiment, reaction temperature is between 450° C. and 600° C., and preferably between 460° C. and 580° C., and even more preferably between 480° C. and 540° C. 
         [0014]    In the more preferred embodiment, WHSV is between 30 h −1  and 80 h −1 , and preferably between 40 h −1  and 60 h −1 . 
         [0015]    In the more preferred embodiment, C/O is between 1 and 30, and preferably between 2 and 25, and even more preferably between 3 and 14. 
         [0016]    In the more preferred embodiment, reaction pressure is between 0.10 MPa and 1.00 MPa. 
         [0017]    In the more preferred embodiment, said feedstock is selected from or includes petroleum hydrocarbons and/or other mineral oils, wherein the petroleum hydrocarbon is one selected from the group consisting of vacuum gas oil (VGO), atmospheric gas oil (AGO), coker gas oil (CGO), deasphalted oil (DAO), vacuum residue (VR) and atmospheric residue (AR) or mixtures thereof, and the other mineral oil is one selected from the group consisting of coal liquefied oil, tar sand oil and shale oil or mixtures thereof. 
         [0018]    In the more preferred embodiment, said catalyst comprises zeolite, inorganic oxide and optional clay, which account for the following percent of the total weight of the catalyst respectively: zeolite 1˜50% by weight, inorganic oxide 5˜99% by weight, and clay 0˜70% by weight. Said zeolite is selected from medium pore size zeolite and optional large pore size zeolite. Said medium pore size zeolite accounts for 51˜100% of the total weight of the zeolite, and preferably for 70˜100% of the total weight of the zeolite. Said large pore size zeolite accounts for 0˜49% of the total weight of the zeolite, and preferably for 0˜30% of the total weight of the zeolite. Said medium pore size zeolite is selected from ZSM series zeolites and/or ZRP zeolites and said large pore size zeolite is selected from Y series zeolites. 
         [0019]    In the more preferred embodiment, said reactor is selected from a riser, an iso-linear speed fluidized bed, an iso-diameter fluidized bed, a descending transfer line and a ascending transfer line or a combination thereof, or a combination of same reactors (two or more reactors), wherein said combination includes cascade or/and parallel. Said riser is a conventional iso-diameter riser or various diverse diameter risers. 
         [0020]    In the more preferred embodiment, said feedstock is charged into reactor from one position, or from two or more positions whose height are same or different. 
         [0021]    In the more preferred embodiment, said process comprises: 
         [0022]    (1) Reaction products and catalyst are separated, wherein catalyst is stripped, regenerated by burning off the coke, and then returns to the reactor. 
         [0023]    (2) The separated products include propylene, high octane gasoline and FGO. 
         [0024]    In the more preferred embodiment, the initial boiling point of said FGO is not less than 260° C., and hydrogen content of said FGO is not less than 10.5% by weight. 
         [0025]    In the more preferred embodiment, the initial boiling point of said FGO is not less than 330° C., and hydrogen content of said FGO is not less than 10.8% by weight. 
         [0026]    Another embodiment provides: 
         [0027]    A catalytic conversion process, wherein feedstocks are reacted by contacting with a medium pore size zeolite enriched catalyst in a reactor, which comprises: 
         [0028]    (1) Said feedstocks include hard crackability feedstock and easy crackability feedstock, which are injected into the reactor from one position, or from two or more positions whose height are same or different, 
         [0029]    (2) Hard crackability feedstock reacts in the reactor not later than easy crackability feedstock, 
         [0030]    (3) Reaction temperature, WHSV and C/O sufficient to achieve a yield of FGO between 12% and 60% by weight of easy crackability feedstock, 
         [0031]    (4) Said WHSV of easy crackability feedstock is 5˜100 h −1 . 
         [0032]    In the more preferred embodiment, said hard crackability feedstock is one selected from or includes slurry, diesel, gasoline, hydrocarbons with 4˜8 carbon atoms, or mixture thereof. 
         [0033]    In the more preferred embodiment, said easy crackability feedstock is selected from or includes petroleum hydrocarbons and/or other mineral oils, wherein the petroleum hydrocarbon is one selected from the group consisting of VGO, AGO, CGO, DAO, VR and AR or mixtures thereof, and the other mineral oil is one selected from the group consisting of coal liquefied oil, tar sand oil and shale oil or mixtures thereof. 
         [0034]    In the more preferred embodiment, said catalyst comprises zeolite, inorganic oxide and optional clay, which account for the following percent of the total weight of the catalyst respectively: zeolite 1˜50% by weight, inorganic oxide 5˜99% by weight, and clay 0˜70% by weight. Said zeolite is selected from medium pore size zeolite and optional large pore size zeolite. Said medium pore size zeolite accounts for 51˜100% of the total weight of the zeolite and said large pore size zeolite accounts for 0˜49% of the total weight of the zeolite. Said medium pore size zeolite is selected from ZSM series zeolites and/or ZRP zeolites and said large pore size zeolite is selected from Y series zeolites. 
         [0035]    In the more preferred embodiment, said reactor is selected from a riser, an iso-linear speed fluidized bed, an iso-diameter fluidized bed, a descending transfer line and a ascending transfer line or a combination thereof, or a combination of same reactors (two or more reactors), wherein said combination includes cascade or/and parallel. Said riser is a conventional iso-diameter riser or various diverse diameter risers. 
         [0036]    In the more preferred embodiment, reaction conditions of hard crackability feedstock are; reaction temperature between 600° C. and 750° C., WHSV between 100 h −1  and 800 h −1 , C/O between 30 and 150, reaction pressure between 0.10 MPa and 1.00 MPa and steam/hard crackability feedstock ratio by weight between 0.05 and 1.00. 
         [0037]    In the more preferred embodiment, reaction conditions of easy crackability feedstock are: reaction temperature between 450° C. and 600° C., WHSV between 5 h −1  and 100 h −1 , C/O between 1 and 30, reaction pressure between 0.10 MPa and 1.00 MPa and steam/easy crackability feedstock ratio by weight between 0.05 and 1.00. 
         [0038]    In the more preferred embodiment, the reaction conditions of easy crackability feedstock are: reaction temperature between 460° C. and 580° C.; WHSV between 10 h −1  and 90 h −1 , preferably between 20 h −1  and 60 h −1 , and even more preferably between 30 h −1  and 50 h −1 ; C/O between 3 and 14. 
         [0039]    In the more preferred embodiment, it comprises: reaction products and catalyst are separated, wherein catalyst is stripped, regenerated by burning off the coke, and then returns to reactor, the separated products include propylene, high octane number gasoline and FGO. 
         [0040]    In the more preferred embodiment, the initial boiling point of FGO is not less than 260° C., and hydrogen content of FGO is not less than 10.5% by weight. 
         [0041]    In the more preferred embodiment, the initial boiling point of FGO is not less than 330° C., and hydrogen content of FGO is not less than 10.8% by weight. 
         [0042]    The third embodiment provides: 
         [0043]    A process for producing propylene and high octane number gasoline, which comprises: 
         [0044]    (1) A feedstock comprising hard crackability feedstock is contacted with a medium pore size zeolite enriched catalyst and cracked in a reactor under the conditions of a reaction temperature between 600° C. and 750° C., a WHSV between 100 h −1  and 800 h −1 , a reaction pressure between 0.10 MPa and 1.00 MPa, a C/O between 30 and 150 and a steam/hard crackability feedstock ratio between 0.05 and 1.00 by weight, 
         [0045]    (2) A reaction stream containing hard crackability feedstock, along with easy crackability feedstock, is further cracked under the conditions of a reaction temperature between 450° C. and 600° C., a WHSV between 5 h −1  and 100 h −1 , a reaction pressure between 0.10 MPa and 1.00 MPa, a C/O between 1.0 and 30.0 and a steam/easy crackability feedstock ratio between 0.05 and 1.00 by weight, 
         [0046]    (3) Spent catalyst and product vapors are separated by cyclone separator. Optionally, spent catalyst is charged into stripping section and stripped. The stripped spent catalyst is regenerated by burning off the coke and returns to reactor. The product vapors are separated to obtain a product comprising propylene, high octane number gasoline and FGO, 
         [0047]    (4) Said FGO is hydrotreated or/and is extracted with aromatic hydrocarbons to obtain hydrotreated FGO (HFGO) or/and a raffinate of FGO (RFGO). Said HFGO or/and RFGO return to step (1) or/and step (2) as hard crackability feedstock or/and easy crackability feedstock. 
         [0048]    In the more preferred embodiment, said hard crackability feedstock is one selected from or includes slurry, diesel, gasoline and hydrocarbons with 4˜8 carbon atoms or mixture thereof. Said easy crackability feedstock is selected from or includes petroleum hydrocarbons and/or other mineral oils, wherein the petroleum hydrocarbon is one selected from the group consisting of VGO, AGO, CGO, DAO, VR and AR or mixtures thereof, and the other mineral oil is one selected from the group consisting of coal liquefied oil, tar sand oil and shale oil or mixtures thereof. Said gasoline is one selected from or includes gasoline obtained from this process, catalytic cracking gasoline, straight-run gasoline, coker gasoline, pyrolysis gasoline, thermal cracking gasoline and hydrogasoline or mixture thereof, wherein catalytic cracking gasoline, straight-run gasoline, coker gasoline, pyrolysis gasoline, thermal cracking gasoline and hydrogasoline are those that are not obtained from the process of the present invention. Said diesel is one selected from or includes diesel obtained in this process, catalytic cracking diesel, straight-run diesel, coker diesel, pyrolysis diesel, thermal cracking diesel and hydrodiesel or mixture thereof, wherein catalytic cracking diesel, straight-run diesel, coker diesel, pyrolysis diesel, thermal cracking diesel and hydrodiesel are those that are not obtained from the process of the present invention. Said hydrocarbon with 4˜8 carbon atoms is one selected from or includes those obtained from this process, or those that may be obtained from conventional catalytic cracking process, coking process, pyrolysis process, thermal cracking process, hydrotreating process and the like. 
         [0049]    In the more preferred embodiment, said catalyst comprises zeolite, inorganic oxide and optional clay, which account for the following percent of the total weight of the catalyst respectively: zeolite 1˜50% by weight, inorganic oxide 5˜99% by weight, and clay 0˜70% by weight. Said zeolite is selected from medium pore size zeolite and optional large pore size zeolite. Said medium pore size zeolite accounts for 51˜100% of the total weight of the zeolite and said large pore size zeolite accounts for 0˜49% of the total weight of the zeolite. The medium pore size zeolite is selected from ZSM series zeolites and/or ZRP zeolites, or ZSM and ZRP zeolites modified with nonmetal elements such as phosphor and/or transition metal elements such as iron, cobalt and nickel. See U.S. Pat. No. 5,232,675 for more detailed description of ZRP zeolites. The ZSM series zeolite is one selected from the group consisting of ZSM-5, ZSM-11, ZSM-12, ZSM-23, ZSM-35, ZSM-38, ZSM-48, and other zeolites with similar structure, or mixture thereof. See U.S. Pat. No. 3,702,886 for more detailed description of ZSM-5 zeolties. The large pore size zeolite is one selected from Y series zeolites, which include: rare-earth Y (REY), rare-earth HY (REHY), ultrastable Y and high silica Y obtained by different processes or mixtures thereof. The inorganic oxide as a binder is selected from silica (SiO 2 ) and/or alumina (Al 2 O 3 ). The clay as a matrix (i.e. support) is selected from kaolin and/or halloysite. The catalytic cracking catalyst in each reactor may be identical or different. 
         [0050]    In the more preferred embodiment, product vapors in step (3) can be separated to obtain a fraction of distillation range 180˜260° C. The fraction can return to step (1) or/and step (2) as hard crackability feedstock or/and easy crackability feedstock. 
         [0051]    Said fraction of distillation range 180˜260° C. may be either obtained from this process, or from conventional catalytic cracking process, coking process, pyrolysis process, thermal cracking process, hydrotreating process and the like, or includes any other fraction rich in mono-ring aromatics. 
         [0052]    In the more preferred embodiment, said reactor is selected from a riser, an iso-linear speed fluidized bed, an iso-diameter fluidized bed, a descending transfer line and a ascending transfer line or a combination thereof, or a combination of same reactors (two or more reactors), wherein said combination includes cascade or/and parallel. Said riser is a conventional iso-diameter riser or various diverse diameter risers. The velocity of the gas in the fluidized bed is between 0.1 m/s and 2.0 m/s (catalyst is neglected). The velocity of the gas in the riser is between 2 m/s and 30 m/s (catalyst is neglected). 
         [0053]    One best embodiment of the present invention is conducted in a diverse diameter riser reactor. More detailed description of this reactor is referred to Chinese Patent Application CN1237477A. 
         [0054]    In order to increase the catalyst/feedstock ratio in a downstream zone of the reactor and the catalyst activity, a part of medium can be fed, which is selected from or/and includes hot/cooled regenerated catalyst, regenerated catalyst, semi-regenerated catalyst, spent catalyst, fresh catalyst and the like. The cooled regenerated catalyst and the cooled semi-regenerated catalyst are obtained by cooling catalyst through catalyst cooler after the spent catalyst is regenerated in two-stage and one-stage regeneration respectively. The regenerated catalyst refers to a catalyst that has a residual carbon content of below 0.1% by weight, more preferably below 0.05% by weight. The semi-regenerated catalyst refers to a catalyst that has a residual carbon content of from 0.1% to 0.9% by weight, more preferably from 0.15% to 0.7% by weight. The spent catalyst refers to a catalyst that has a residual carbon content of above 0.9% by weight, more preferably from 0.9% to 1.2% by weight. 
         [0055]    The process for separating products such as propylene from the reaction product is the same as those well known to the ordinary skilled in the art. The fraction of distillation range 180˜260° C., more preferably 190˜250° C. can be separated in an existing FCC fractionation column or an individual fractionation column. For the FGO fraction having an initial boiling point of above 250° C. or above 260° C. or above 330° C., it can be conveyed to an extractor to obtain heavy aromatic products and non-aromatic products (i.e. raffinate oil), or a hydrotreater to obtain the hydrotreated FGO, or it also can be used as the feedstock of FCC. 
         [0056]    The extraction solvent of FGO is one selected from or includes dimethyl sulfoxide, furfural, dimethylformamide, monoethanolamine, ethylene glycol and 1,2-propanediol or mixture thereof. The extraction solvent can be recycled. The extraction temperature is 100° C., and the solvent/feedstock ratio is between 0.5 and 5.0 by volume. The extracted heavy aromatics are desired products, and the FGO raffinate oil (i.e. non-aromatic hydrocarbons) can be used as one of the FCC feedstocks. 
         [0057]    The hydrotreating of FGO is conducted in the presence of hydrogen gas by contacting with a catalyst at the following conditions: hydrogen partial pressure 3.0 MPa˜20.0 MPa, reaction temperature 300˜450° C., hydrogen/oil ratio 300˜2000 by volume, and volume hourly space velocity 0.1˜3.0 h −1 . The hydrotreated FGO can be used as the feedstock of FCC. 
         [0058]    The embodiment(s) of the present invention can integrate the fluid catalytic cracking process with the FGO hydrotreating process or/and the solvent extraction process of the aromatics of FGO to obtain a high octane gasoline and an improved yield of light olefins, particularly propylene, from heavy feedstocks having a relative low hydrogen content. The present invention has several important advantages over the prior art in that: 
         [0059]    1. The propylene yield and the propylene selectivity in LGP are improved greatly, and the propylene yield is as high as 27% by weight. 
         [0060]    2. The gasoline yield increases obviously, and the gasoline octane number is improved significantly. 
         [0061]    3. The yields of dry gas and coke decrease while the propylene yield increases markedly. 
         [0062]    4. The light oil yield increases and the slurry yield decreases significantly; therefore, the process of the present invention can utilize petroleum oil resources efficiently. 
         [0063]    5. The run period of hydrotreating units increases considerably. 
     
    
     
       DESCRIPTION OF DRAWINGS 
         [0064]      FIG. 1  is a schematic representation for the first embodiment of the process of the present invention. 
           [0065]      FIG. 2  is a schematic representation for the second embodiment of the process of the present invention. 
           [0066]      FIG. 3  is a schematic representation for the third embodiment of the process of the present invention. 
       
    
    
     DETAILED DESCRIPTION OF THE EMBODIMENTS 
       [0067]    The accompanying drawing, which is hereby incorporated in this specification, illustrates several embodiments of the invention and together with the description serve to explain but not limit the scope of the present invention. Thus, it will be apparent to one skilled in the art that certain modifications may be made to the invention as described without departing from the scope of the claims set out below. 
         [0068]    According to the first specific embodiment of the present invention, the process of the present invention can be carried out according to the scheme shown in  FIG. 1 . 
         [0069]    A prelift medium is introduced via a line  1  into the bottom of a riser reactor  2 . The regenerated catalyst from a standpipe  16  is lifted by the prelift medium and moves upward. A portion of the feedstock from a line  3 , along with the atomized steam from a line  4 , is injected into the bottom of the reaction zone I of the riser reactor  2 , and mixed with the existing stream in the riser reactor. Said feedstock cracks on the hot catalyst, and it moves upward. Another portion of feedstock from a line  5 , along with the atomized steam from a line  6 , is injected into the middle upper part of the reaction zone I of the riser reactor  2 , and mixed with the existing stream in the riser reactor. The feedstock cracks on the lower catalyst having a deposited coke thereon, and it moves upward into the reaction zone II to continue to react. The resulting reaction product vapors and the deactivated spent catalyst, through a line  7 , enter a cyclone separator of a disengager  8 , wherein the spent catalyst and the reaction product vapors are separated. The reaction product vapors exit the cyclone and flow into a plenum chamber  9 . Fine catalyst particles go back to the disengager via a dipleg. The spent catalyst in the disengager flows into a stripping section  10  and contacts with a steam from a line  11 . The reaction product vapors stripped out of the spent catalyst enter the plenum chamber  9 , via the cyclone. The stripped spent catalyst flows into a regenerator  13  via a standpipe  12 . A main air enters the regenerator via a conduit  14  to burn off the coke deposited on the spent catalyst and regenerate the deactivated spent catalyst. Flue gas flows into turbine via a line  15 . The regenerated catalyst is recycled into the riser reactor via the standpipe  16 . 
         [0070]    Reaction product vapors in the plenum chamber  9  are transported via a transfer line  17  and introduced into a sequent separation system  18 . The separated LPG product is removed via a line  20 ; the separated gasoline product is removed via a line  21 ; the separated dry gas product is removed via a line  19 ; the separated diesel product is removed via a line  22 ; and the separated FGO product is removed via a line  23 . The boiling ranges of various fractions can be adjusted according to the requirements of refinery. 
         [0071]    According to the second specific embodiment of the present invention, the process of the present invention can be carried out according to the scheme shown in  FIG. 2 . 
         [0072]    A prelift medium is introduced via a line  1  into the bottom of a riser reactor  2 . The regenerated catalyst from a standpipe  16  is lifted by the prelift medium and moves upward. A hard crackability feedstock from a line  3 , along with the atomized steam from a line  4 , is injected into the bottom of the reaction zone I of the riser reactor  2 , and mixed with the existing stream in the riser reactor. Said hard crackability feedstock cracks on the hot catalyst, and it moves upward. An easy crackability feedstock from a line  5 , along with the atomized steam from a line  6 , is injected into the middle upper part of the reaction zone I of the riser reactor  2 , and mixed with the existing stream in the riser reactor. The easy crackability feedstock cracks on the lower catalyst having a deposited coke thereon, and it moves upward into the reaction zone II to continue to react. The resulting reaction product vapors and the deactivated spent catalyst, through a line  7 , enter a cyclone separator of a disengager  8 , wherein the spent catalyst and the reaction product vapors are separated. The reaction product vapors exit the cyclone and flow into a plenum chamber  9 . Fine catalyst particles go back to the disengager via a dipleg. The spent catalyst in the disengager flows into a stripping section  10  and contacts with a steam from a line  11 . The reaction product vapors stripped out of the spent catalyst enter the plenum chamber  9 , via the cyclone. The stripped spent catalyst flows into a regenerator  13  via a standpipe  12 . A main air enters the regenerator via a conduit  14  to burn off the coke deposited on the spent catalyst and regenerate the deactivated spent catalyst. Flue gas flows into turbine via a line  15 . The regenerated catalyst is recycled into the riser reactor via the standpipe  16 . 
         [0073]    Reaction product vapors in the plenum chamber  9  are transported via a transfer line  17  and introduced into a sequent separation system  18 . The separated propylene product is removed via a line  219 ; the separated propane product is removed via a line  228 ; the C4 olefin is removed via a line  220  and a portion thereof is recycled back to the riser reactor  2 ; the catalytic cracked dry gas is removed via a line  221 ; the boiling range 180˜260° C. fraction is recycled back to the riser reactor  2  via a line  222 ; the boiling range 260˜330° C. diesel fraction may be removed via a line  229 , or may be removed along with the FGO into an extraction unit  224 ; the FGO is introduced via a line  223  into the extraction unit  224 , wherein the separated heavy aromatics product is removed via a line  226  and the RFGO is recycled back to the riser reactor  2  via a line  225 ; the high octane number gasoline product (C5˜180° C.) is removed via a line  227 . The boiling ranges of various fractions can be adjusted according to the requirements of refinery. 
         [0074]    According to the third specific embodiment of the present invention, the process of the present invention can be carried out according to the scheme shown in  FIG. 3 . 
         [0075]    A prelift medium is introduced via a line  1  into the bottom of a riser reactor  2 . The regenerated catalyst from a standpipe  16  is lifted by the prelift medium and moves upward. A hard crackability feedstock from a line  3 , along with the atomized steam from a line  4 , is injected into the bottom of the reaction zone I of the riser reactor  2 , and mixed with the existing stream in the riser reactor. Said hard crackability feedstock cracks on the hot catalyst, and it moves upward. An easy crackability feedstock from a line  5 , along with the atomized steam from a line  6 , is injected into the middle upper part of the reaction zone I of the riser reactor  2 , and mixed with the existing stream in the riser reactor. The easy crackability feedstock cracks on the lower catalyst having a deposited coke thereon, and it moves upward into the reaction zone II to continue to react. The resulting reaction product vapors and the deactivated spent catalyst, through a line  7 , enter a cyclone separator of a disengager  8 , wherein the spent catalyst and the reaction product vapors are separated. The reaction product vapors exit the cyclone and flow into a plenum chamber  9 . Fine catalyst particles go back to the disengager via a dipleg. The spent catalyst in the disengager flows into a stripping section  10  and contacts with a steam from a line  11 . The reaction product vapors stripped out of the spent catalyst enter the plenum chamber  9 , via the cyclone. The stripped spent catalyst flows into a regenerator  13  via a standpipe  12 . A main air enters the regenerator via a conduit  14  to burn off the coke deposited on the spent catalyst and regenerate the deactivated spent catalyst. Flue gas flows into turbine via a line  15 . The regenerated catalyst is recycled into the riser reactor via the standpipe  16 . 
         [0076]    Reaction product vapors in the plenum chamber  9  are transported via a transfer line  17  and introduced into a sequent separation system  18 . The separated propylene is removed via a line  319 ; the separated propane is removed via a line  328 ; the C4 olefin is removed via a line  320  or may be recycled back to the bottom of the reaction zone I of the riser reactor  2 ; the catalytic cracked dry gas is removed via a line  321 ; the catalytic cracked gasoline is remove via a line  327 ; the boiling range 180˜260° C. fraction is recycled back to the bottom of the reaction zone I of the riser reactor  2  via a line  322 ; the boiling range above 260° C. fraction is introduced via a line  323  into a hydrotreating unit  324 , wherein the separated light component is removed via a line  325  and the HFGO is recycled back to the middle upper part of the reaction zone I of the riser reactor  2  via line  326 . The boiling ranges of various fractions can be adjusted according to the requirements of refinery. 
         [0077]    The following examples are used to demonstrate the effect of the present invention and are not intended to limit the scope of the invention to the detailed examples shown herein. The properties of the feedstocks are listed in table 1. 
         [0078]    Catalyst used in the examples was prepared as follows: 
         [0079]    1) 20 g NH 4 Cl was dissolved in 1000 g water, and 100 g (dry basis) crystallized product ZRP-1 zeolite (an MFI-structured zeolite produced in Qilu Petrochemical Co. with a SiO 2 /Al 2 O 3  molar ratio of 30, a content of rare earth RE 2 O 3 =2.0% by weight) was added to this solution, after exchanging at 90° C. for 0.5 h, filtering to yield a filter cake. 4.0 g of H 3 PO 4  (with a concentration of 85 wt %) and 4.5 g of Fe(NO 3 ) 3  were dissolved in 90 g water to obtain a solution. The filter cake was impregnated with the obtained solution and dried. The resultant solid was calcined at 550° C. for 2 hours to yield an MFI-structured medium pore sized zeolite containing phosphor and iron. The anhydrous chemical formula of the catalyst was 
         [0000]      0.1Na 2 O.5.1Al 2 O 3 .2.4P 2 O 5 .1.5Fe 2 O 3 .3.8RE 2 O 3 .88.1SiO 2 . 
         [0080]    2) 75.4 kg halloysite clay (an industrial product of Suzhou Porcelain Clay Co. with a solid content of 71.6% by weight) was slurried with 250 kg deionized water, whereto 54.8 kg pseudo-boehmite (an industrial product of Shandong Alumina Plant with a solid content of 63% by weight) was added. The PH value was adjusted at 2˜4 with hydrochloric acid. The slurry was uniformly stirred and laid aside for aging at 60˜70° C. for 1 hour. The temperature was decreased to below 60° C. while maintaining the PH value at 2˜4, and then 41.5 kg alumina sol (a product of Qilu Petrochemical Co. with an Al 2 O 3  content of 21.7% by weight) was added. After stirring for 40 min, a mixed slurry was obtained. 
         [0081]    3) 22.5 kg (dry basis, prepared in step 1) MFI-structured medium pore sized zeolite containing phosphor and iron and 2.0 kg (dry basis) DASY zeolite (an ultrastable zeolite-Y product of Qilu Petrochemical Co. with a unit cell size of 2.445˜2.448 nm) were added into the mixed slurry (prepared in step 2) and uniformly stirred to yield a slurry. The obtained slurry was shaped by spray drying, and the product was washed off the free Na +  with ammonium dihydrogen phosphate solution (phosphor content 1% by weight). After drying, a sample of the catalytic cracking catalyst was obtained. The composition of the catalyst was 18 by weight of MFI-structured medium pore sized zeolite containing phosphor and iron, 2% by weight of DASY zeolite, 28% by weight of pseudo-boehmite, 7% by weight of alumina sol, and balanced kaolin. 
       EXAMPLE 1   
       [0082]    The experiment of the present example was carried out according to the scheme shown in  FIG. 1 . Feedstock A was directly used as the feedstock of catalytic cracking and the experiment was conducted in a pilot riser reactor plant. Feedstock A was injected into the reaction zone I, wherein the catalytic cracking reaction was conducted. The reaction temperature was 530° C., the WHSV was 30 h −1 , the C/O was 10, and the weight ratio of steam/the feedstock was 0.15. Reaction product vapors and the coked spent catalyst were separated in the disengager, and then the products were separated, wherein propylene, the gasoline and the FGO were withdrawn. Operating conditions and product slate were listed in table 2. 
         [0083]    It can be seen from Table 2 that the yield of propylene attains as high as 18.29% by weight and those of dry gas and coke are only 2.36% and 3.95% by weight respectively, and the FGO yield is 30.12% by weight whose hydrogen content is 11.08% by weight. 
       EXAMPLE 2   
       [0084]    The experiment of the present example was carried out according to the scheme shown in  FIG. 2 . Feedstock A was directly used as the feedstock of catalytic cracking and the experiment was conducted in a pilot riser reactor plant. Easy crackability feedstock was injected into the middle-upper portion of reaction zone I, wherein the reaction temperature was 580° C., the WHSV was 60 h −1 , the catalytic cracking catalyst/the easy crackability feedstock (m/m) was 10, the weight ratio of steam/the easy crackability feedstock was 0.15. Hard crackability feedstock was charged in the bottom of the reaction zone I, wherein the reaction temperature was 640° C., the WHSV was 180 h −1 , the catalytic cracking catalyst/the hard crackability feedstock (m/m) was 60, and the weight ratio of steam/the hard crackability feedstock was 0.20. In reaction zone II, the reaction temperature was 540° C., the WHSV was 30 h −1 , and the weight ratio of steam/the easy crackability feedstock was 0.15. Reaction product vapors and the spent catalyst were separated in the disengager, and then the products were separated, wherein propylene and the gasoline were withdrawn and a portion of C4 olefin and 180˜260° C. fractions were returned to the riser reactor. The FGO (the yield was 28.45% by weight and the hydrogen content was 11.01% by weight) was extracted with furfural, wherein the extraction temperature was 100° C., the solvent/FGO ratio was 3.0 (v/v), and then non-aromatic hydrocarbons and heavy aromatics were separated. The RFGO (that is said non-aromatic hydrocarbons) was mixed with the easy crackability feedstock and returned to the riser reactor. Operating conditions and product slate were listed in table 3. 
         [0085]    It can be seen from Table 3 that the yield of propylene attains as high as 29.02% by weight; the gasoline yield is 33.71% by weight, and its research octane number (RON) and motor octane number (MON) are as high as 96.0 and 84.0 respectively. 
       EXAMPLE 3  
       [0086]    The experiment of the present example was carried out in the same plant as that in Example 2. Feedstock B was directly used as the feedstock of catalytic cracking and the experiment was conducted in a pilot riser reactor plant. Easy crackability feedstock was injected into the middle-upper portion of reaction zone I, wherein the reaction temperature was 580° C., the WHSV was 60 h −1 , the catalytic cracking catalyst/the easy crackability feedstock (m/m) was 10, and the weight ratio of steam/the easy crackability feedstock was 0.15. Hard crackability feedstock was charged in the bottom of the reaction zone I, wherein the reaction temperature was 640° C., the WHSV was 180 h −1 , the catalytic cracking catalyst/the hard crackability feedstock (m/m) was 60, and the weight ratio of steam/the hard crackability feedstock was 0.20. In addition, a portion of the stripped spent catalyst was introduced from the stripping section into the bottom of the reaction zone II, so as to decrease the temperature and the WHSV in the reaction zone II. In the reaction zone II, the reaction temperature was 530° C., the WHSV was 20 h −1 , and the weight ratio of steam/the easy crackability feedstock was 0.15. Reaction product vapors and the spent catalyst were separated in the disengager, and then the products were separated, wherein propylene and the gasoline were withdrawn and a portion of C4 olefin and 190˜250° C. fraction were returned to the riser reactor. The FGO (the yield was 32.83% by weight and the hydrogen content was 10.98% by weight) was extracted with furfural, wherein the extraction temperature was 100° C., the solvent/FGO ratio was 3.0 (v/v), and then non-aromatic hydrocarbons and heavy aromatics were separated. The RFGO (that is said non-aromatic hydrocarbons) was mixed with the feedstock and returned to the riser reactor. Operating conditions and product slate were listed in table 3. 
         [0087]    It can be seen from Table 3 that the yield of propylene attains as high as 28.01% by weight; the gasoline yield is as high as 35.20% by weight, and its research octane number (RON) and motor octane number (MON) are as high as 97.1 and 85.0 respectively. 
       EXAMPLE 4  
       [0088]    The experiment of the present example was carried out according to the scheme shown in  FIG. 3 . Feedstock A was directly used as the feedstock of catalytic cracking and the experiment was conducted in a pilot riser reactor plant. Easy crackability feedstock was injected into the middle-upper portion of reaction zone I, wherein the reaction temperature was 580° C., the WHSV was 60 h −1 , the catalytic cracking catalyst/the easy crackability feedstock (m/m) was 10, and the weight ratio of steam/the easy crackability feedstock was 0.15. Hard crackability feedstock was charged in the bottom of the reaction zone I, wherein the reaction temperature was 640° C., the WHSV was 180 h −1 , the catalytic cracking catalyst/the hard crackability feedstock (m/m) was 60, and the weight ratio of steam/the hard crackability feedstock was 0.20. In reaction zone II, the reaction temperature was 540° C., the WHSV was 30 h −1 , and the weight ratio of steam/the easy crackability feedstock was 0.15. Reaction product vapors and the spent catalyst were separated in the disengager, and then the products were separated, wherein propylene and the gasoline were withdrawn and a portion of C4 olefin and 180˜260° C. fractions were returned to the riser reactor. The FGO (the initial boiling point is above 260° C. and the yield was 28.46% by weight and the hydrogen content was 11.01% by weight) was hydrotreated, wherein the reaction temperature was 350° C., the hydrogen partial pressure was 18.0 MPa, the hydrogen/oil ratio was 1500 by volume, and the volume hourly space velocity was 1.5 h −1 . The resulting HFGO was returned to the above-mentioned pilot riser reactor. Operating conditions and product slate were listed in table 4. 
         [0089]    It can be seen from Table 4 that the yield of propylene attains as high as 30.02% by weight; the dry gas yield is only 3.32% by weight, and the liquid yield is 90.68% by weight. 
       EXAMPLE 5  
       [0090]    The experiment of the present example was carried out in the same plant as that in Example 4. Feedstock B was directly used as the feedstock of catalytic cracking and the experiment was conducted in a pilot riser reactor plant. Easy crackability feedstock was injected into the middle-upper portion of reaction zone I, wherein the reaction temperature was 580° C., the WHSV was 60 h −1 , the catalytic cracking catalyst/the easy crackability feedstock (m/m) was 10, and the weight ratio of steam/the easy crackability feedstock was 0.15. Hard crackability feedstock was charged in the bottom of the reaction zone I, wherein the reaction temperature was 640° C., the WHSV was 180 h −1 , the catalytic cracking catalyst/the hard crackability feedstock (m/m) was 60, and the weight ratio of steam/the hard crackability feedstock was 0.20. In addition, a portion of the stripped spent catalyst was introduced from the stripping section into the bottom of the reaction zone II, so as to decrease the temperature and the WHSV in the reaction zone II. In the reaction zone II, the reaction temperature was 530° C., the WHSV was 20 h −1 , and the weight ratio of steam/the easy crackability feedstock was 0.15. Reaction product vapors and the spent catalyst were separated in the disengager, and then the products were separated, wherein propylene and the gasoline were withdrawn and a portion of C4 olefin and 180˜260° C. fractions were returned to the riser reactor. The FGO (the initial boiling point is above 260° C. and the yield was 32.56% by weight and the hydrogen content was 10.97% by weight) was hydrotreated, wherein the reaction temperature was 450° C., the hydrogen partial pressure was 10.0 MPa, the hydrogen/oil ratio was 500 by volume, and the volume hourly space velocity was 0.5 h −1 . The HFGO was returned to the above-mentioned pilot riser reactor. Operating conditions and product slate were listed in table 4. 
         [0091]    It can be seen from Table 4 that the yield of propylene attains as high as 27.55% by weight; the dry gas yield is only 3.16% by weight, and the liquid yield is 90.64% by weight. 
         [0000]    
       
         
               
               
               
             
               
               
               
               
             
           
               
                   
                 TABLE 1 
               
               
                   
                   
               
               
                   
                 Examples 
                 Examples 
               
               
                   
                 1, 2, 4 
                 3, 5 
               
               
                   
                   
               
             
             
               
                   
               
             
          
           
               
                   
                 No. Feedstock 
                 A 
                 B 
               
               
                   
                 Property of feedstock 
               
               
                   
                 Density (20° C.), g/cm 3   
                 0.8886 
                 0.9134 
               
               
                   
                 Sulfur content, ppm 
                 4700 
                 5800 
               
               
                   
                 Nitrogen content, ppm 
                 1600 
                 2900 
               
               
                   
                 Aromatics m % 
                 26.3 
                 32.6 
               
               
                   
                 C, m % 
                 86.46 
                 86.23 
               
               
                   
                 H, m % 
                 12.86 
                 12.69 
               
               
                   
                 Boiling range (ASTM D-1160), ° C. 
               
               
                   
                 IBP 
                 312 
                 327 
               
               
                   
                 10% 
                 361 
                 363 
               
               
                   
                 30% 
                 412 
                 409 
               
               
                   
                 50% 
                 452 
                 450 
               
               
                   
                 70% 
                 478 
                 482 
               
               
                   
                 90% 
                 506 
                 504 
               
               
                   
                 95% 
                 532 
                 526 
               
               
                   
                 EP 
                 546 
                 542 
               
               
                   
                   
               
             
          
         
       
     
         [0000]    
       
         
               
               
             
               
               
               
             
           
               
                   
                 TABLE 2 
               
               
                   
                   
               
               
                   
                 Example 1 
               
               
                   
                   
               
             
             
               
                   
               
             
          
           
               
                   
                 No. Feedstock 
                 A 
               
               
                   
                 Operation condition 
               
               
                   
                 Reaction temperature, ° C. 
                 530 
               
               
                   
                 WHSV, h −1   
                 30 
               
               
                   
                 Steam/feedstock ratio, m/m 
                 0.15 
               
               
                   
                 C/O, m/m 
                 10 
               
               
                   
                 Product distribution, m % 
               
               
                   
                 Dry gas 
                 2.36 
               
               
                   
                 LPG 
                 39.68 
               
               
                   
                 Propylene 
                 18.29 
               
               
                   
                 Gasoline 
                 21.53 
               
               
                   
                 Diesel 
                 2.36 
               
               
                   
                 FGO 
                 30.12 
               
               
                   
                 Hydrogen content, m % 
                 11.08 
               
               
                   
                 Boiling range, ° C. 
               
               
                   
                 IBP 
                 263 
               
               
                   
                 EP 
                 554 
               
               
                   
                 Coke 
                 3.95 
               
               
                   
                 Total 
                 100.00 
               
               
                   
                   
               
             
          
         
       
     
         [0000]    
       
         
               
               
               
             
               
               
               
               
             
           
               
                   
                 TABLE 3 
               
               
                   
                   
               
               
                   
                 Example 2 
                 Example 3 
               
               
                   
                   
               
             
             
               
                   
               
             
          
           
               
                   
                 No. Feedstock 
                 A 
                 B 
               
               
                   
                 Catalytic cracking unit 
               
               
                   
                 Operation condition 
               
               
                   
                 Riser outlet temperature, ° C. 
                 530 
                 520 
               
               
                   
                 Riser reaction zone II 
               
               
                   
                 Reaction temperature, ° C. 
                 540 
                 530 
               
               
                   
                 WHSV, h −1   
                 30 
                 20 
               
               
                   
                 Steam/feedstock ratio, m/m 
                 0.15 
                 0.15 
               
               
                   
                 Riser reaction zone I 
               
               
                   
                 Reaction temperature, ° C. 
                 640/580 
                 640/580 
               
               
                   
                 C/O, m/m 
                 60/10 
                 60/10 
               
               
                   
                 WHSV, h −1   
                 180/60  
                 180/60  
               
               
                   
                 Steam/feedstock ratio, m/m 
                 0.20/0.15 
                 0.20/0.15 
               
               
                   
                 Solvent extraction unit 
               
               
                   
                 Temperature, ° C. 
                 100 
                 100 
               
               
                   
                 Solvent/FGO, v/v 
                 3.0 
                 3.0 
               
               
                   
                 Product distribution, m % 
               
               
                   
                 Dry gas 
                 3.86 
                 3.46 
               
               
                   
                 LPG 
                 50.23 
                 48.16 
               
               
                   
                 Propylene 
                 29.02 
                 28.01 
               
               
                   
                 Gasoline 
                 33.71 
                 35.20 
               
               
                   
                 Heavy aromatics 
                 5.15 
                 6.01 
               
               
                   
                 Coke 
                 7.05 
                 7.17 
               
               
                   
                 Total 
                 100.00 
                 100.00 
               
               
                   
                 Gasoline octane number 
               
               
                   
                 RON 
                 96.0 
                 97.1 
               
               
                   
                 MON 
                 84.0 
                 85.0 
               
               
                   
                   
               
             
          
         
       
     
         [0000]    
       
         
               
               
               
             
               
               
               
               
             
           
               
                   
                 TABLE 4 
               
               
                   
                   
               
               
                   
                 Example 4 
                 Example 5 
               
               
                   
                   
               
             
             
               
                   
               
             
          
           
               
                   
                 No. Feedstock 
                 A 
                 B 
               
               
                   
                 Catalytic cracking unit 
               
               
                   
                 Operation condition 
               
               
                   
                 Riser outlet temperature, ° C. 
                 530 
                 520 
               
               
                   
                 Riser reaction zone II 
               
               
                   
                 Reaction temperature, ° C. 
                 540 
                 530 
               
               
                   
                 WHSV, h −1   
                 30 
                 20 
               
               
                   
                 Steam/feedstock ratio, m/m 
                 0.15 
                 0.15 
               
               
                   
                 Riser reaction zone I 
               
               
                   
                 Reaction temperature, ° C. 
                 640/580 
                 640/580 
               
               
                   
                 C/O, m/m 
                 60/10 
                 60/10 
               
               
                   
                 WHSV, h −1   
                 180/60  
                 180/60  
               
               
                   
                 Steam/feedstock ratio, m/m 
                 0.20/0.15 
                 0.20/0.15 
               
               
                   
                 Hydrotreating unit 
               
               
                   
                 Hydrogen partial pressure, Mpa 
                 18.0 
                 10.0 
               
               
                   
                 Reaction temperature, ° C. 
                 350 
                 450 
               
               
                   
                 Hydrogen/feedstock ratio, v/v 
                 1500 
                 500 
               
               
                   
                 Volume hourly space velocity, h −1   
                 1.5 
                 0.5 
               
               
                   
                 Product distribution, m % 
               
               
                   
                 Dry gas 
                 3.32 
                 3.16 
               
               
                   
                 LPG 
                 51.23 
                 48.12 
               
               
                   
                 Propylene 
                 30.02 
                 27.55 
               
               
                   
                 Gasoline 
                 31.12 
                 33.05 
               
               
                   
                 Diesel 
                 8.33 
                 9.47 
               
               
                   
                 Coke 
                 6.0 
                 6.2 
               
               
                   
                 Total 
                 100.00 
                 100.00