Abstract:
A process for preparing a metamorphosed metal oxide, which comprises heating, under a non-oxidative (and not hydrogenous) atmosphere, a mixture of at least one metal oxide, said metal being selected from the group consisting of elements of Groups III, IV, V and II b and transition elements in Periodic Table, and a carbide represented by the formula: 
     
       C(M).sub.z 
     
     wherein M is an element except carbon selected from the group consisting of elements of Groups III, IV and V in Periodic Table, and Z is an integer corresponding to the valency of M, is disclosed. The process is simple and safe and the metamorphosed metal oxide obtained is modified in color tint and provided with electroconductivity.

Description:
BACKGROUND OF THE INVENTION 
     1. Field of the Invention 
     The invention relates to a process for preparing a metamorphosed metal oxide. 
     2. Description of the Prior Art 
     Recently, development of metal suboxides has become a subject drawing attention, in accordance with diversified industrial needs. For instance, there has been developed a method of preparing a blacked titanium oxide by metamorphosing and reducing titanium dioxide under a hydrogenous atmosphere. This method, however, was in danger of explosion because the reaction was performed at a high temperature under a hydrogenous atmosphere. Thus, in order to secure safety, it has been required on carrying out the method to solve some troublesome problems in manufacturing equipments and process controls. 
     Moreover, the hydrogenated type titanium oxides thus obtained, which might lose electroconductivity owing to the split off of hydrogen atoms by a possible contact with an oxidative atmosphere, were limited in their use. 
     Under the circumstances, it has been desired to develop a novel process for preparing electroconductive metal oxides which are heat-resistant, colored and free from the above defects. 
     SUMMARY OF THE INVENTION 
     The present invention relates to a process for preparing a metamorphosed metal oxide, which comprises heating, under a non-oxidative atmosphere, a mixture of at least one metal oxide, said metal being selected from the group consisting of elements of Groups III, IV, V and II b and transition elements in Periodic Table, and a carbide represented by the formula: 
     
         C(M).sub.z                                                 (I) 
    
     wherein M is an element except carbon selected from the group consisting of elements of Group III, IV and V in Periodic Table, and z is an integer corresponding to the valency of M. 
     The process of the present invention has the following advantages: 
     (1) Modification of color tint and/or metamorphosis providing electroconductivity of the metal oxides used as the raw materials can be performed effectively, without losing their heat resistance and other properties. 
     (2) Treatment for the metamorphosis is safe and simple, because heating under hydrogenous atmosphere is not necessary. 
     (3) Any step for isolating the carbide used as the raw material from the resulting metamorphosed metal oxide is not necessary, and the latter can be used as it is as a conductive sintered body because those substances derived from said raw material are excellent in heat resistance and maintain good conductivity. 
     DESCRIPTION OF THE PREFERRED EMBODIMENT 
     According to the present invention, at least one metal oxide is used, the metal of which is selected from the group consisting of elements of Groups III, IV, V and II b and transition elements in Periodic Table. Examples of such metal oxides include, titanium oxide, tin oxide, antimony oxide, cesium oxide, potassium oxide, yttrium oxide, indium oxide, silicon oxide, germanium oxide, lead oxide, bismuth oxide, niobium oxide, zinc oxide, iron oxide, nickel oxide, cobalt oxide, etc. Preferred ones among them are titanium oxide, tin oxide, antimony oxide, etc. These metal oxides may be employed either individually or as a mixture of two or more of them. 
     As the carbides of the general formula (I) may be employed any one known in the art. Examples of the carbides are boron carbide, silicon carbide, titanium carbide, germanium carbide, tin carbide, lead carbide, phosphorus carbide, etc. and among them boron carbide, silicon carbide and titanium carbide are preferred. These carbides may be employed either individually or as a mixture of two or more of them. 
     Although the mechanism of the metamorphosis of metal oxides in accordance with the process of the present invention is not thoroughly clarified, it is assumed that, when a mixture of the metal oxide and the carbide of the formula (I) is heated under a non-oxidative atmosphere, the carbide may act as a deoxidant and cause reductive metamorphosis of the metal oxide and yields a product possessing good conductivity and changed color, whereby the carbide also may be dehydrogenized or oxidized and the conductivity of the metamorphosed metal oxide is not reduced. 
     As for the ratio of mixing the metal oxide and the carbide of the formula (I), the two components may be mixed in such ratio that the number of carbon atoms in the carbide is 0.01 to 10 times, preferably 0.1 to 3 times, per one oxygen atom in the metal oxide except the oxygen atom(s) constituting any water of crystallization contained therein, although the ratio may vary depending on the sort of the metal oxide and the carbide employed and also on the purpose of utilizing the product obtained. When the amount of the carbide admixed is too small, difficulties are liable to occur in attaining the purpose of the present invention. On the other hand, when the amount of the carbide admixed is too much, operation for mixing the raw materials becomes troublesome one and a lot of energy is required for the heating. 
     If it is necessary to separate an excessive carbide remaining after the metamorphosis of the metal oxide, the separation may be effected utilizing the difference in specific gravity between the metal oxide and the carbide. However, the remaining carbide in the metamorphosed product usually does not restrict the use of the product. Non-oxidative atmosphere in the present invention means a non-oxidative atmosphere containing substantially more than 90% by volume of one or more of reducing gases such as carbon monoxide, or inert gases such as nitrogen, helium or carbon dioxide. Especially, nitrogen gas atmosphere or carbon dioxide gas atmosphere is preferable. 
     The heat treatment according to the present invention is performed usually at 500° to 1500° C. for 2 to 600 mins., preferably at 800° to 1200° C. for 5 to 180 mins., though the conditions for the treatment may vary depending on the sort of the raw materials and the usage of the resultant. No special furnace is required for the heat treatment, and any usual furnace for heating can be used. 
     Although the heat treatment may be performed by heating a simple mixture of the metal oxide and the carbide as it is, it is preferred to use a uniform mixture of the metal oxide and the carbide both in fine powdery form so that the metal oxide may well contact with the carbide. Further, it is desirable to remove air contained in the mixture, especially, the mixture of powdery metal oxide and powdery carbide, or replace the air with a non-oxidative material, as far as possible. The air contained in the mixture would cause consumption of the carbide before completion of the metamorphosis of the metal oxide, require a prolonged time for the metamorphosis and an excess amount of the carbide, and be liable to incomplete or non-uniform metamorphosis. 
     Therefore, it is preferable in the present invention to remove air from the mixture of the metal oxide and the carbide, for example, by 
     (1) a method comprising first compressing the mixture under reduced pressure into a compact and then heating the compact, or 
     (2) a method comprising admixing with the mixture a binder which is decomposed into non-oxidative gases upon heating, compressing the admixture into a compact, if necessary, and then heating the admixture or the compact. 
     The binder which is decomposed into non-oxidative gases upon heating means those compounds which contain as the main component one or more elements selected from hydrogen, carbon and nitrogen and are decomposed upon heating into water vapor, carbon dioxide gas, carbon monoxide gas or nitrogen gas. The binder may be one arbitrarily selected from water, ammonia, amino compounds, nitrogen-containing compounds, hydrocarbons, carbohydrates and various synthetic resins, or a mixture of them, provided that it is in liquid form at ambient temperature or at the time of molding under pressure and can exert a binding ability necessary for the molding of the mixture of the metal oxide and the carbide. However, from the viewpoint of economy and of the applications of the product, those are exemplified such as water, hydrocarbon compounds, glycerol, ethylene glycol, carbohydrate compounds such as starch, urea derivatives, polyvinyl alcohol, butyral resin, polyvinyl acetate resin, atactic polyethylene, liquid polypropylene, polybutene, acrylic resin, etc.. The amount of these binders to be used may vary without limitation depending on the sorts of the metal oxide and the carbide as well as the purpose of the applications. However, it is preferred to use the binder in an amount not more than 300 parts by weight (hereinafter, parts by weight are referred to as &#34;parts&#34;), more preferably not more than 100 parts, per 100 parts of the total amount of the metal oxide and the carbide. Too large amount of binder is undersirable because it requires excessive heating during the metamorphosis and removal of decomposition products resulting from the remaining binder. 
     By heating under a non-oxidative atmosphere, the above-mentioned binder produces carbides remaining as ash, most of which however are harmless to electroconductive metamorphosis, though they are colored black. Therefore, it is unnecessary to specially separate and remove the decomposition products of the binder before practical use of the product, so far as the binder is used in an appropriate amount. 
     According to the present invention, it is also possible to use a sintering binder in combination, which sinters and acts as a binder of the mixture of metal oxide and carbide on heating. 
     Further, it is possible according to the present invention to obtain a metamorphosed molding or compact having conductivity, by molding a mixture of metal oxide, carbide, sintering binder and, if required, a binder necessary for molding and then heating the molded article under a non-oxidative atmosphere whereby metamorphosis of the metal oxide and the metamorphosis and molding by the sintering binder are effected simultaneously. 
     For the molding of the mixture of metal oxide, carbide and binder, any conventional molding method wherein a uniform mixture prepared by a conventional method and heated at room temperature or at such temperature that does not cause vaporization or decomposition of the binder is subjected to any one of the following molding processes: 
     (1) a process using a compression molding machine, wherein the mixture is filled into a mold and then compressed, 
     (2) a process using a granulating molding machine, wherein the mixture is put into a granulator to obtain granules or flakes, 
     (3) a process using a tablet machine, wherein the mixture is tabletted, and 
     (4) a process using a press rolls, wherein the mixture is passed through the rolls to give a sheet. However, it is preferred from the viewpoint of uniformity and efficiency of the heating during the metamorphosis, to effect the molding in such way that the molding obtained has a larger surface area. In general, the thicker the molding, the larger the temperature gradient therein. It is necessary to control the thickness of moldings in order to avoid unevenness of the heating i.e. unevenness of the metamorphosis. 
     The invention is further illustrated by the following Examples. These Examples, however, are given only for illustration of the present invention and never for restriction of the invention. 
    
    
     EXAMPLE 1 
     2.5 g of anatase type titanium dioxide and 1 g of powdered silicon carbide were thoroughly mixed in a mortar. The mixture was charged in a boat-shaped 30 ml crucible made of highly pure alumina. Air in the crucible was displaced with nitrogen gas. The crucible was put in a tubular electric furnace made of highly pure alumina (inner diameter of the tube: 50 mm, length: 1 m) maintained at 1100° C., heat-treated for 2 hours under nitrogen stream of 50 ml/min., cooled to room temperature also under nitrogen stream and then took out. Titanium oxide changed to pale blue color was obtained. For comparison, titanium dioxide without addition of powdered silicon carbide was heated and modified under the same condition as above. The resultant titanium oxide was white with no change in color. 
     EXAMPLE 2 
     A mixture of anatase type titanium dioxide and powdered silicon carbide prepared by the same method as in Example 1 was pressed in a tableting machine at a pressure of 150 kg/cm 2  for 30 mins. in vacuo, to get tablets of 10 mm diameter and 1 mm thickness which consist of anatase type titanium dioxide and silicon carbide. 
     The tablets was put in a platinum boat followed by putting into an electric furnace same as in Example 1 where nitrogen gas was flowed in for 30 mins. Then tablets were heated and modified at temperatures and periods shown in Table 1 under nitrogen stream. 
     The properties of the resultant tablets of mixtures of metamorphosed titanium oxide and silicon carbide are shown in Table 1. 
     For comparison, the result obtained from an experiment made with titanium dioxide without silicon carbide is shown as Comparative Example 1 in Table 1. 
     
                       TABLE 1______________________________________Condition ofmetamorphosis   temper-Example ature    time    Color      ConductivityNo.     (°C.)            (min)   before                          after  before                                       after______________________________________2        900     30      grayish                          pale   no    yes                    white blue3       1000     20      grayish                          bluish no    yes                    white violet4       1050     30      grayish                          bluish no    yes                    white violet5       1100     15      grayish                          blackish                                 no    yes                    white violet6       1150     10      grayish                          blackish                                 no    yes                    white violetCompar- 1050     30      grayish                          grayish                                 no    noative                    white whiteExample 1______________________________________ Note (1) 
    
     In Table 1, the conductivity was evaluated by the use of Digital Multimeter TR 6841 (made by Takeda Riken Co., Ltd., Japan). 
     The term &#34;no&#34; means the case in which the value of resistance was not less than 10 6  Ω when the electrodes were contacted to both sides of the tablet. The term &#34;yes&#34; means the case in which the value of resistance was not more than 10 3  Ω by the same measurement as above. 
     EXAMPLE 7 
     2.5 g anatase type titanium dioxide, 1 g of silicon carbide and 0.5 g of liquid paraffin as a binder were thoroughly mixed in a mortar. 
     The mixture was filled in mold, pressed at a pressure of 20 kg/cm 2  for 3 mins., to get a cylindrical molded article of 10 mm diameter and 40 mm length. The resultant article in a platinum boat was put into an electric furnace. 
     After aerating for 30 mins. and replacing with nitrogen, the article was heated at 1150° C. for 30 mins. under nitrogen stream of 50 ml/min. to get a cylindrical product of blackish violet color with some voids. The loss in weight was 15%. 
     The surface of this cylindrical product was coated with silver paste, and the conductivity was measured by the same method as in Example 2 to be 5.9×10 4  Ω. The volume resistivity was 1.16×10 4  Ωcm; by calculating the following equation. ##EQU1## 
     For comparison, the same experiment as in Example 7 was carried out except that silicon carbide was not used. The product showed grayish white with no change from the initial material. In addition, when the mixture without addition of the binder was pressed at 20 kg/cm 2  for 3 mins., it did not give a cylindrical and hard molded article. 
     EXAMPLE 8 TO 19 
     Molding was repeated by the same method as in Example 7 except that the sorts of metal oxides, the amounts of the silicon carbide compounds, the sorts and the amount of binders, temperatures and periods of heating, were varied as shown in Tables 2 and 3. The results of metamorphosis are shown in Table 3. 
     
                                           TABLE 2__________________________________________________________________________ExampleMetal oxide      Carbide    BinderNo.  Sort       Amount (g)                 Sort Amount (g)                            Sort     Amount (g)__________________________________________________________________________ 8   titanium dioxide           2.5   silicon                      1     liquid   1.0(anatase)        carbide    paraffin 9   titanium dioxide           4     titanium                      1.5   ethylene 1.0(anatase)        carbide    glycol10   titanium dioxide           2.5   silicon                      1     liquid   1.0(rutile)         carbide    paraffin11   titanium dioxide           4     silicon                      1     10% aqueous                                     0.8(rutile)         carbide    solution of starch12   tin oxide  4     silicon                      1     liquid   1.0(Sn.sub.2 O.sub.3)                 carbide    paraffin13   tin oxide  4     silicon                      1     liquid   1.0(Sn.sub.2 O.sub.3)                 carbide    paraffin14   tin oxide  4     silicon                      1     polybutene                                     0.5(Sn.sub.2 O.sub.3)                 carbide15   tin oxide  4     silicon                      1     7% aqueous                                     0.7(Sn.sub.2 O.sub.3)                 carbide    solution of CMC16   tin oxide (Sn.sub.2 O.sub.3)           3     silicon                      1     liquid   0.8antimony oxide           1     carbide    paraffin17   anatase titanium oxide           3     titanium                      1.5   liquid   1.0tin oxide (Sn.sub.2 O.sub.3)           1     carbide    paraffin18   hydrated   5     silicon                      1     liquid   1.0titanium oxide   carbide    paraffin19   anatase titanium oxide           3     silicon                      1     liquid   1.0antimony oxide           1     carbide    paraffin__________________________________________________________________________ 
    
     
                       TABLE 3______________________________________Condition ofmetamorphosis  temper-                      ConductivityExample  ature    time     Color      of ProductNo.    (°C.)           (min)    before                          after  (Ω)______________________________________ 8      700     120      grayish                          pale   2.9 × 10.sup.7                    white violet 9     1200     60       dark  blackish                                 8.5 × 10.sup.3                    violet                          violet10     1150     60       dark  bluish 4.1 × 10.sup.4                    violet                          violet11     1200     60       dark  deep   9.2 × 10.sup.4                    violet                          violet12      800     30       dark  gray   2.1 × 10.sup.4                    violet13      900     30       dark  gray   1.8 × 10.sup.4                    violet14      950     15       dark  gray   9.3 × 10.sup.3                    violet15      880     60       dark  gray   1.3 × 10.sup.4                    violet16      900     30       dark  gray   4.2 × 10.sup.3                    violet17     1100     60       dark  bluish 2.9 × 10.sup.4                    violet                          violet18     1150     60       dark  bluish 1.7 × 10.sup.4                    violet                          violet19     1050     60       dark  bluish 8.3 × 10.sup.3                    violet                          violet______________________________________