Abstract:
A sputtering target for forming a ZrO 2 —In 2 O 3  based protective film for an optical storage medium, has a component composition made of Zr a In b A c O 100-a-b-c  where “A” represents one, two, or more of Si, Cr, Al, Ce, Ti, and Sn, “a” represents an amount greater than 5 atomic percent and less than 23 atomic percent, “b” represents an amount greater than 12 atomic percent and less than 35 atomic percent, and “c” represents an amount greater than 0 and less than 30 atomic percent, wherein 90% or more of Zr that is included in the sputtering target for forming the protective film for the optical storage medium is in an oxidative product phase in which Zr and In are combined, and is dispersed in a base material of the target.

Description:
BACKGROUND OF THE INVENTION 
     1. Field of the Invention 
     The present invention relates to a sputtering target (hereinafter, it will be referred to as a target) having excellent resistance to cracking, used for forming a ZrO 2 —In 2 O 3  based protective film for an optical storage medium, the optical storage medium being capable of recording, playing, both of recording and playing, or deleting information using a laser light. 
     This application claims priority from Japanese Patent Application No. 2007-231670 filed on Sep. 6, 2007, the contents of which are incorporated herein by reference in their entirety. 
     2. Background Art 
     Generally, a ZnS—SiO 2  based protective film has been known as a typical protective film (the protective film includes a lower section protective film and an upper section protective film) constituting an optical storage medium such as an optical disc. The ZnS—SiO 2  based protective film has component compositions including 20% of silicon dioxide (SiO 2 ) and the rest thereof constituted of zinc sulfide (ZnS). 
     It is known that the ZnS—SiO 2  based protective film having the foregoing component compositions are obtained by sputtering, by use of a ZnS—SiO 2  based target made of a hot-pressed sintered body including 20% of silicon dioxide (SiO 2 ) and the rest thereof constituted of zinc sulfide (ZnS). 
     However, in the ZnS—SiO 2  based protective film that is obtained by sputtering, by use of the ZnS—SiO 2  based target, S of ZnS diffuses to a storage film caused by reiteration of rewriting the storage film and irradiating the storage film with a laser light, there is a drawback in that the performance of reiteration of rewriting is degraded. 
     As a result, development of a protective film without S progresses. As an example of a protective film without S, a ZrO 2 —In 2 O 3  based protective film for an optical storage medium has been proposed. The ZrO 2 —In 2 O 3  based protective film includes zirconium oxide and indium oxide as main components, and component compositions made of Zr a In b A c O 100-a-b-c  in which an oxidative product of the A (SiO 2 , Cr 2 O 3 , Al 2 O 3 , CeO 2 , TiO 2 , SnO 2 , or the like) is included, where “A” represents one, two, or more of Si, Cr, Al, Ce, Ti, and Sn, “a” represents an amount greater than 5 atomic percent and less than 23 atomic percent, “b” represents an amount greater than 12 atomic percent and less than 35 atomic percent, and “c” represents an amount greater than 0 and less than 30 atomic percent. 
     It is also known that a ZrO 2 —In 2 O 3  based protective film for an optical storage medium can be formed by sputtering, by use of a ZrO 2 —In 2 O 3  based target having substantially the same component compositions as the component compositions of the protective film. 
     The foregoing technique has been disclosed in, for example, Japanese Unexamined Patent Application, First Publication No. 2005-56545. 
     In the conventional method for forming a sputtering target for forming a ZrO 2 —In 2 O 3  based protective film for an optical storage medium, zirconium oxide powders, indium oxide powders, and powders of the oxidative product of the A which serve as raw material powders, are prepared. The raw material powders are compound and blended with a predetermined percentage, and mixed powders are produced. The mixed powders are baked in an air atmosphere or in an oxidized atmosphere such as an oxygen atmosphere after the mixed powders are produced. 
     In a conventional target formed in this manner, the large amount of Zr that is included in the conventional target used for forming a ZrO 2 —In 2 O 3  based protective film for an optical storage medium is a zirconium oxide phase. 
     The other are compositions made of a indium oxide phase and an oxidative product phase of the A. 
     However, in the case where a high output sputtering is performed by use of the target used for forming the ZrO 2 —In 2 O 3  based protective film for an optical storage medium, and the large amount of Zr is a zirconium oxide phase and the other compositions are made of an indium oxide phase and the oxidative product phase of the A in the target, there is a problem in that, a crack is generated in the target during the sputtering, and it is impossible to efficiency form the protective film used for an optical storage medium. 
     SUMMARY OF THE INVENTION 
     The invention has an object to provide a target for forming a ZrO 2 —In 2 O 3  based protective film for an optical storage medium, having excellent resistance to cracking, in which a crack is not generated even if a sputtering is performed with a high output. 
     The inventors have researched a target used for forming a protective film for an optical storage medium in order to produce the target, the target having excellent resistance to cracking, in which a crack is not generated in a sputtering even if a high output sputtering is performed. As a result, according to their findings, study conclusions as described below were obtained: 
     (a) even if a high speed sputtering is performed, a crack is not generated in a target used for forming a ZrO 2 —In 2 O 3  based protective film for an optical storage medium, the target has compositions in which 90% (preferably 100%) or more of Zr that is included in the target is in an oxidative product phase in which Zr and In are combined, and is dispersed in a base material of the target; and
 
(b) the oxidative product phase in which Zr and In are combined has a component composition made of Zr x In y O 100-x-y  where “x” represents an amount greater than 20 atomic percent and less than 30 atomic percent, and “y” represents an amount greater than 10 atomic percent and less than 16 atomic percent.
 
     The invention was made with respect to the above-described study conclusions, and provides (1) a sputtering target for forming a ZrO 2 —In 2 O 3  based protective film for an optical storage medium, having excellent resistance to cracking, and having a component composition made of Zr a In b A c O 100-a-b-c  where “A” represents one, two, or more of Si, Cr, Al, Ce, Ti, and Sn, “a” represents an amount greater than 5 atomic percent and less than 23 atomic percent, “b” represents an amount greater than 12 atomic percent and less than 35 atomic percent, and “c” represents an amount greater than 0 and less than 30 atomic percent, wherein 90% or more of Zr that is included in the sputtering target for forming the protective film for the optical storage medium is in an oxidative product phase in which Zr and In are combined, and is dispersed in a base material of the target. 
     In addition, the invention provides (2) the a sputtering target for forming a ZrO 2 —In 2 O 3  based protective film for an optical storage medium, having excellent resistance to cracking, according to above-described (1), wherein the oxidative product phase in which Zr and In are combined has a component composition made of Zr x In y O 100-x-y  where “x” represents an amount greater than 20 atomic percent and less than 30 atomic percent, and “y” represents an amount is greater than 10 atomic percent and less than 16 atomic percent. 
     In order to manufacture the sputtering target for forming a ZrO 2 —In 2 O 3  based protective film for an optical storage medium of the invention, having excellent resistance to cracking, zirconium oxide powders and indium oxide powders which serves as raw material powders are prepared, furthermore, powders of the oxidative product of the A (silicon dioxide powders, aluminum oxide powders, titanium oxide powders, tin oxide powders, cerium oxide powders, chrome oxide powders, or the like) are prepared. 
     The zirconium oxide powders and the indium oxide powders are mixed and molded, thereafter, a baked body is formed by baking. By pulverizing the baked body, powders made of an oxidative product in which Zr and In are combined are produced. 
     The powders of the oxidative product of the A and the indium oxide powders which have been prepared in advance are blended into the powders made of an oxidative product in which Zr and In are combined and mixed powders are made. 
     Consequently, by pressing and shaping the mixed powders, a molded body is obtained, and the molded body is sintered in an oxygen atmosphere or in an air atmosphere. 
     In the foregoing processes, it is possible to produce the sputtering target of the invention, having excellent resistance to cracking, for forming a ZrO 2 —In 2 O 3  based protective film for an optical storage medium. 
     The sputtering target of the invention for forming a ZrO 2 —In 2 O 3  based protective film for an optical storage medium has excellent resistance to cracking and is produced in the above-described manner. 90% or more of the Zr that is included in the sputtering target is in an oxidative product phase in which Zr and In are combined, and is dispersed in a base material. 
     In the sputtering target for forming a ZrO 2 —In 2 O 3  based protective film for an optical storage medium, the more percentage of Zr that is included in the target in which Zr serves as the oxidative product phase in which Zr and In are combined and is dispersed in a base material, the more generation of cracks are reduced, even if a high speed sputtering is performed. 
     Therefore, in the sputtering target for forming a ZrO 2 —In 2 O 3  based protective film for an optical storage medium, the more percentage of Zr that is included in the sputtering target in which Zr serves as the oxidative product phase in which Zr and In are combined and is dispersed in a base material, the more preferable it is. It is most preferable that 100% of Zr which serves as the oxidative product phase in which Zr and In are combined be dispersed in a base material. 
     Consequently, the oxidative product phase in which Zr and In are combined has a component composition made of Zr x In y O 100-x-y  where “x” represents an amount greater than 20 atomic percent and less than 30 atomic percent, and “y” represents an amount greater than 10 atomic percent and less than 16 atomic percent. 
     In the target of the invention used for forming a ZrO 2 —In 2 O 3  based protective film for an optical storage medium, even if a high output sputtering is performed, since a crack does not occur in the target, it is possible to form a ZrO 2 —In 2 O 3  based protective film for an optical storage medium with a further improved efficiency. 
    
    
     DESCRIPTION OF THE PREFERRED EMBODIMENTS 
     Subsequently, an example of a target of the invention used for forming a ZrO 2 —In 2 O 3  based protective film for an optical storage medium, having excellent resistance to cracking will be specifically described. 
     As raw material powders, ZrO 2  powders having an average particle diameter of 0.5 μm, and whose degree of purity is greater than or equal to 99.99%; In 2 O 3  powders having an average particle diameter of 0.5 μm, and whose degree of purity is greater than or equal to 99.9%; SiO 2  powders having an average particle diameter of 0.2 μm, and whose degree of purity is greater than or equal to 99.99%; Al 2 O 3  powders having an average particle diameter of 0.5 μm, and whose degree of purity is greater than or equal to 99.9%; TiO 2  powders having an average particle diameter of 0.2 μm, and whose degree of purity is greater than or equal to 99.99%; CeO 2  powders having an average particle diameter of 1 μm, and whose degree of purity is greater than or equal to 99.99%; SnO 2  powders having an average particle diameter of 1 μm, and whose degree of purity is greater than or equal to 99.99%; and Cr 2 O 3  powders having an average particle diameter of 0.5 μm, and whose degree of purity is greater than or equal to 99.9% were prepared. 
     Firstly, ZrO 2  powders and In 2 O 3  powders which have been prepared in advance were blended so as to obtain the percentage indicated in Table 1, the obtained blended powders were mixed by use of zirconia balls whose diameter is 1 mm, for 10 minutes and in a bead mill of a wet grinding apparatus, and mixed powders whose average particle diameter is 0.3 μm were produced. 
     Deionized water was used as dispersion liquid, the dispersion liquid in which pulverization was completed was heated up using a hot plate at 150° C., and the mixed powders were dried. 
     The mixed powders that were dried in this manner were baked in the condition indicated in Table 1; thereafter, the mixed powders were pulverized, and powders A to F made of oxidative products in which Zr and In are combined were produced. The powders A to F include component composition of Zr x In y O 100-x-y  having “x” and “y” indicated in Table 1. 
     
       
         
               
               
               
               
             
               
               
               
               
               
               
               
               
             
               
               
               
               
               
               
               
               
               
             
           
               
                   
                 TABLE 1 
               
             
             
               
                   
                   
               
               
                   
                   
                   
                 MEASURED 
               
               
                   
                   
                   
                 COMPONENT 
               
               
                   
                   
                   
                 COMPOSITION OF 
               
               
                   
                   
                   
                 POWERED 
               
               
                   
                   
                   
                 OXIDATIVE 
               
               
                   
                   
                   
                 PRODUCT 
               
               
                   
                 COMPONENT 
                   
                 IN WHICH 
               
               
                   
                 COMPOSITION 
                   
                 Zr AND In ARE 
               
               
                   
                 OF RAW 
                   
                 COMBINED, BY 
               
               
                   
                 MATERIAL 
                   
                 USE OF EPMA 
               
               
                   
                 POWDERS 
                   
                 Zr x In y O 100−x−y   
               
               
                   
                 (MOL %) 
                 BAKING CONDITIONS 
                 (ATOM %) 
               
             
          
           
               
                 TYPE 
                 ZrO 2   
                 In 2 O 3   
                 ATMOSPHERE 
                 TEMPERATURE (° C.) 
                 TIME (H) 
                 x 
                 y 
               
               
                   
               
             
          
           
               
                 POWDERED 
                 A 
                 82 
                 REMNANT 
                 OXYGEN 
                 1450 
                 3 
                 21.3 
                 14.7 
               
               
                 OXIDATIVE 
                 B 
                 80 
                 REMNANT 
                 OXYGEN 
                 1450 
                 4 
                 23.9 
                 13.4 
               
               
                 PRODUCT IN 
                 C 
                 81 
                 REMNANT 
                 OXYGEN 
                 1450 
                 5 
                 24.6 
                 12.9 
               
               
                 WHICH Zr 
                 D 
                 49 
                 REMNANT 
                 OXYGEN 
                 1450 
                 3 
                 26.7 
                 14.2 
               
               
                 AND In ARE 
                 E 
                 80 
                 REMNANT 
                 OXYGEN 
                 1450 
                 3 
                 27.4 
                 13.4 
               
               
                 COMBINED 
                 F 
                 78 
                 REMNANT 
                 OXYGEN 
                 1450 
                 5 
                 29.0 
                 14.5 
               
               
                   
               
             
          
         
       
     
     Example 1 
     SiO 2  powders and In 2 O 3  powders which had been prepared in advance were added to the powders A to F which were made of oxidative products in which Zr and In are combined, and which had been prepared in advance as indicated in Table 1, so as to obtain the percentage indicated in Table 2; furthermore, zirconia balls having a diameter of 1 mm and the dispersion liquid which serves as deionized water were added thereto and were mixed for 10 minutes in a bead mill of a wet grinding apparatus; and mixed powders were produced. 
     The obtained mixed powders were dried using a hot plate that was heated at 150° C., and moisture was thereby removed. 
     By use of a cold isostatic pressing method (CIP method), a molded body having a diameter of 200 mm and a thickness of 10 mm was produced from the mixed powders from which moisture had been removed by drying in the above-described manner. 
     Consequently, under the conditions indicated in Table 2, a baked body was produced by baking the molded body; furthermore, a surface of the baked body was machined by mechanical working, and targets 1 to 9 of the invention having a diameter of 125 mm and a thickness of 6 mm and having component compositions as indicated in Table 2 were thereby produced. 
     The percentage of Zr, as an oxidative product in which Zr and In are combined, that is included in the targets 1 to 9 of the invention and that is dispersed in a base material, is measured by use of EPMA (JXA-8500F, JEOL Ltd.) in a below-described manner. 
     Firstly, by use of the EPMA and by capture of a Backscattered Electron Image, a composition of a polished cross-sectional face of the target in an area of 5000 μm 2  or more was captured with a magnification ratio of 3000 or more. 
     Furthermore, by use of a WDS (Wavelength-Dispersive Spectrometer) technique, a phase including Zr and a phase simultaneously including Zr and In are determined. An area of the phase including only Zr and an area of the phase made of the oxidative product in which Zr and In are combined are calculated based on the captured image. The percentage of Zr that is included in the target and is in the oxidative product in which Zr and In are combined is determined, and the result thereof is indicated in Table 2. 
     Conventional Example 1 
     ZrO 2  powders, In 2 O 3  powders, and SiO 2  powders which have been prepared as raw material powders in advance were mixed together so as to obtain the percentage indicated in Table 2; furthermore, zirconia balls having a diameter of 1 mm and the dispersion liquid which serves as deionized water were added thereto and were mixed for 10 minutes in a bead mill of a wet grinding apparatus; and mixed powders were produced. 
     The obtained mixed powders were dried using a hot plate that was heated at 150° C., and moisture was thereby removed. 
     By use of a cold isostatic pressing method (CIP method), a molded body having a diameter of 200 mm and a thickness of 10 mm was produced from the mixed powders from which moisture had been removed by drying in the above-described manner. 
     Consequently, under the conditions indicated in Table 2, a baked body was produced by baking the molded body; furthermore, a surface of the baked body was machined by mechanical working, and a conventional target 1 having a diameter of 125 mm and a thickness of 6 mm and having component compositions as indicated in Table 2 were thereby produced. 
     The percentage of Zr, as an oxidative product in which Zr and In are combined, that is included in the conventional target 1, and that is dispersed in a base material, is measured by use of EPMA (JXA-8500F, JEOL Ltd.) in a below-described manner. 
     Firstly, by use of the EPMA and by capture of a Backscattered Electron Image, a composition of a polished cross-sectional face of the target in an area of 5000 μm 2  or more was captured with a magnification ratio of 3000 or more. 
     Furthermore, by use of a WDS (Wavelength-Dispersive Spectrometer) technique, a phase including Zr and a phase simultaneously including Zr and In are determined. An area of the phase including only Zr and an area of the phase made of the oxidative product in which Zr and In are combined are calculated based on the captured image. The percentage of Zr that is included in the target and is in the oxidative product in which Zr and In are combined is determined, and the result thereof is indicated in Table 2. 
     In a state where each of the targets 1 to 9 of the invention and conventional target 1 which are obtained in the above-described manner is solder-mounted to a water-cooling backing plate made of oxygen-free copper, the target is attached to a sputtering apparatus, the inside of the apparatus is evacuated by use of a vacuum evacuation device so as to be less than or equal to 1×10 −6  Torr; thereafter, the inside of the apparatus is set to a gas partial pressure of 10 mTorr of Ar in an atmosphere by supplying Ar gas into the apparatus. 
     By use of the targets 1 to 9 of the invention and the conventional target 1 in the above-described conditions, a sputtering is performed for 3 minutes by applying 2 kW greater than normal of sputtering power by use of an RF power source; thereafter, the sputtering is stopped for 1 minute. 
     The foregoing operation in which the sputtering is stopped for 1 minute after the sputtering for 3 minutes was repeated at 10 times. 
     Subsequently, the target is removed from the sputtering apparatus, the target is observed and it is determined whether or not a crack has been generated in the target, and the results of which are indicated in Table 2. 
     
       
         
               
               
               
               
               
               
             
               
               
               
               
               
               
               
               
             
               
               
               
               
               
               
               
               
               
               
             
               
               
               
               
               
               
               
               
               
               
               
               
             
               
               
               
               
               
               
               
               
               
               
               
               
               
             
               
               
               
               
               
               
               
               
               
               
               
             
           
               
                   
                 TABLE 2 
               
             
             
               
                   
                   
               
               
                   
                   
                   
                   
                 PERCENTAGE 
                   
               
               
                   
                   
                   
                   
                 OF 
               
               
                   
                 COMPONENT COMPOSITION OF 
                   
                   
                 Zr THAT IS 
               
               
                   
                 RAW MATERIAL POWDERS 
                   
                   
                 INCLUDED IN 
               
               
                   
                 (MOL %) 
                   
                   
                 TARGET AND 
               
             
          
           
               
                   
                 POWDERED 
                   
                   
                   
                 COMPONENT 
                 THAT SERVES 
                   
               
               
                   
                 OXIDATIVE 
                   
                   
                 BAKING 
                 COMPOSITION 
                 AS OXIDATIVE 
               
               
                   
                 PRODUCT IN 
                   
                   
                 CONDITIONS 
                 OF TARGET 
                 PRODUCT IN 
                 EXISTENCE 
               
             
          
           
               
                   
                 WHICH Zr AND In 
                   
                   
                   
                 TEM- 
                   
                   
                 WHICH Zr 
                 OF CRACK IN 
               
               
                   
                 ARE COMBINED 
                   
                   
                 AT- 
                 PERA- 
                   
                 (ATOM %) 
                 AND In ARE 
                 TARGET 
               
               
                   
                 SHOWN IN 
                   
                   
                 MOS- 
                 TURE 
                 TIME 
                 Zr a In b Si c O 100−a−b−c   
                 COMBINED 
                 USED IN 
               
             
          
           
               
                 TARGET 
                 TABLE 1 
                 In 2 O 3   
                 SiO 2   
                 PHERE 
                 (° C.) 
                 (H) 
                 a 
                 b 
                 c 
                 (%) 
                 SPUTTERING 
               
               
                   
               
             
          
           
               
                 INVENTION 
                 1 
                 A: 30 
                 40 
                 REMNANT 
                 AIR 
                 1400 
                 4 
                 6.3 
                 23.2 
                 7.7 
                 99 
                 NONE 
               
               
                   
                 2 
                 A: 50 
                 30 
                   
                   
                   
                   
                 10.8 
                 20.6 
                 5.3 
                 98 
                 NONE 
               
               
                   
                 3 
                 B: 40 
                 30 
                   
                   
                   
                   
                 8.5 
                 20.2 
                 8.0 
                 98 
                 NONE 
               
               
                   
                 4 
                 C: 25 
                 35 
                   
                   
                   
                   
                 5.3 
                 20.9 
                 10.5 
                 98 
                 NONE 
               
               
                   
                 5 
                 C: 70 
                 20 
                   
                   
                   
                   
                 15.5 
                 18.2 
                 2.7 
                 97 
                 NONE 
               
               
                   
                 6 
                 D: 70 
                 30 
                   
                   
                   
                   
                 14.2 
                 23.0 
                 2.7 
                 96 
                 NONE 
               
               
                   
                 7 
                 E: 40 
                 60 
                   
                   
                   
                   
                 7.3 
                 31.2 
                 5.1 
                 98 
                 NONE 
               
               
                   
                 8 
                 E: 30 
                 70 
                   
                   
                   
                   
                 5.3 
                 33.6 
                 5.5 
                 99 
                 NONE 
               
               
                   
                 9 
                 F: 90 
                 5 
                   
                   
                   
                   
                 20.0 
                 14.2 
                 1.4 
                 95 
                 NONE 
               
             
          
           
               
                 CONVEN- 
                 ZrO 2 : 50, In 2 O 3 : 30 
                   
                   
                   
                   
                 13.9 
                 16.7 
                 5.5 
                 70 
                 EXISTING 
               
               
                 TIONAL 1 
               
               
                   
               
             
          
         
       
     
     Based on the result indicated in Table 2, in the targets 1 to 9 of the invention, 90% or more of Zr as the oxidative product phase in which Zr and In are combined is dispersed in a base material. In the conventional target 1, an amount of Zr that is less than 90%, which serves as the oxidative product phase in which Zr and In are combined, is dispersed in the base material. 
     Compared with the conventional target 1 having compositions in which a ZrO 2  phase exists in large numbers, it is seen that a crack is not generated in a high output sputtering in the targets 1 to 9 of the invention. 
     Example 2 
     Al 2 O 3  powders and In 2 O 3  powders which had been prepared in advance were added to the powders A to F which were made of oxidative products in which Zr and In are combined, and which had been prepared in advance as indicated in Table 1, so as to obtain the percentage indicated in Table 3; furthermore, zirconia balls having a diameter of 1 mm and the dispersion liquid which serves as deionized water were added thereto and were mixed for 10 minutes in a bead mill of a wet grinding apparatus; and mixed powders were produced. 
     The obtained mixed powders were dried using a hot plate that was heated at 150° C., and moisture was thereby removed. 
     By use of a cold isostatic pressing method (CIP method), a molded body having a diameter of 200 mm and a thickness of 10 mm was produced from the mixed powders from which moisture had been removed by drying in the above-described manner. 
     Consequently, under the conditions indicated in Table 3, a baked body was produced by baking the molded body; furthermore, a surface of the baked body was machined by mechanical working, and targets 10 to 18 of the invention having a diameter of 125 mm and a thickness of 6 mm and having component compositions as indicated in Table 3 were thereby produced. 
     The percentage of Zr that is included in the targets 10 to 18 of the invention as the oxidative product phase in which Zr and In are combined and that is dispersed in a base material is determined in a manner similar to the Example 1, and the result thereof is indicated in Table 3. 
     Conventional Example 2 
     ZrO 2  powders, In 2 O 3  powders, and Al 2 O 3  powders which have been prepared as as raw material powders in advance were mixed together so as to obtain the percentage indicated in Table 3; furthermore, zirconia balls having a diameter of 1 mm and the dispersion liquid which serves as deionized water were added thereto and were mixed for 10 minutes in a bead mill of a wet grinding apparatus; and mixed powders were produced. 
     The obtained mixed powders were dried using a hot plate that was heated at 150° C., and moisture was thereby removed. 
     By use of a cold isostatic pressing method (CIP method), a molded body having a diameter of 200 mm and a thickness of 10 mm was produced from the mixed powders from which moisture had been removed by drying in the above-described manner. 
     Consequently, under the conditions indicated in Table 3, a baked body was produced by baking the molded body; furthermore, a surface of the baked body was machined by mechanical working, and a conventional target 2 having a diameter of 125 mm and a thickness of 6 mm and having component compositions as indicated in Table 3 were thereby produced. 
     The percentage of Zr that is included in the conventional target 2 as the oxidative product phase in which Zr and In are combined and that is dispersed in a base material is determined in a manner similar to the Conventional Example 1, and the result thereof is indicated in Table 3. 
     In a state where each of the targets 10 to 18 of the invention and conventional target 2 which are obtained in the above-described manner is solder-mounted to a water-cooling backing plate made of oxygen-free copper, the target is attached to a sputtering apparatus, the inside of the apparatus is evacuated by use of a vacuum evacuation device so as to be less than or equal to 1×10 −6  Torr; thereafter, the inside of the apparatus is set to a gas partial pressure of 10 mTorr of Ar in an atmosphere by supplying Ar gas into the apparatus. 
     By use of the targets 10 to 18 of the invention and the conventional target 2 in the above-described conditions, a sputtering is performed for 3 minutes by applying 2 kW greater than normal of sputtering power by use of an RF power source; thereafter, the sputtering is stopped for 1 minute. 
     The foregoing operation in which the sputtering is stopped for 1 minute after the sputtering for 3 minutes was repeated at 10 times. 
     Subsequently, the target is removed from the sputtering apparatus, the target is observed and it is determined whether or not a crack has been generated in the target, and the results of which are indicated in Table 3. 
     
       
         
               
               
               
               
               
               
             
               
               
               
               
               
               
               
               
             
               
               
               
               
               
               
               
               
               
               
             
               
               
               
               
               
               
               
               
               
               
               
               
             
               
               
               
               
               
               
               
               
               
               
               
               
               
             
               
               
               
               
               
               
               
               
               
               
               
             
           
               
                   
                 TABLE 3 
               
             
             
               
                   
                   
               
               
                   
                   
                   
                   
                 PERCENT- 
                   
               
               
                   
                   
                   
                   
                 AGE 
               
               
                   
                   
                   
                   
                 OF 
               
               
                   
                   
                   
                   
                 Zr THAT IS 
               
               
                   
                 COMPONENT COMPOSITION OF 
                   
                   
                 INCLUDED 
               
               
                   
                 RAW MATERIAL POWDERS 
                   
                   
                 IN TARGET 
               
               
                   
                 (MOL %) 
                   
                   
                 AND THAT 
               
             
          
           
               
                   
                 POWDERED 
                   
                   
                   
                   
                 SERVES AS 
                   
               
               
                   
                 OXIDATIVE 
                   
                   
                 BAKING 
                 COMPONENT 
                 OXIDATIVE 
               
               
                   
                 PRODUCT IN 
                   
                   
                 CONDITIONS 
                 COMPOSITION 
                 PRODUCT IN 
                 EXISTENCE 
               
             
          
           
               
                   
                 WHICH Zr AND In 
                   
                   
                   
                 TEM- 
                   
                 OF TARGET 
                 WHICH Zr 
                 OF CRACK IN 
               
               
                   
                 ARE COMBINED 
                   
                   
                 AT- 
                 PERA- 
                   
                 (ATOM %) 
                 AND In ARE 
                 TARGET 
               
               
                   
                 SHOWN IN 
                   
                   
                 MOS- 
                 TURE 
                 TIME 
                 Zr a In b Al c O 100−a−b−c   
                 COMBINED 
                 USED IN 
               
             
          
           
               
                 TARGET 
                 TABLE 1 
                 In 2 O 3   
                 Al 2 O 3   
                 PHERE 
                 (° C.) 
                 (H) 
                 a 
                 b 
                 c 
                 (%) 
                 SPUTTERING 
               
               
                   
               
             
          
           
               
                 INVENTION 
                 10 
                 A: 30 
                 40 
                 REMNANT 
                 AIR 
                 1400 
                 4 
                 5.4 
                 20.1 
                 13.3 
                 99 
                 NONE 
               
               
                   
                 11 
                 A: 50 
                 30 
                 REMNANT 
                   
                   
                   
                 9.8 
                 18.6 
                 9.5 
                 99 
                 NONE 
               
               
                   
                 12 
                 B: 40 
                 30 
                 REMNANT 
                   
                   
                   
                 7.3 
                 17.4 
                 13.8 
                 98 
                 NONE 
               
               
                   
                 13 
                 C: 40 
                 20 
                 REMNANT 
                   
                   
                   
                 7.4 
                 12.7 
                 18.4 
                 98 
                 NONE 
               
               
                   
                 14 
                 C: 70 
                 20 
                 REMNANT 
                   
                   
                   
                 14.7 
                 17.2 
                 5.2 
                 97 
                 NONE 
               
               
                   
                 15 
                 D: 70 
                 20 
                 REMNANT 
                   
                   
                   
                 14.2 
                 17.8 
                 5.1 
                 97 
                 NONE 
               
               
                   
                 16 
                 E: 40 
                 40 
                 REMNANT 
                   
                   
                   
                 7.3 
                 22.0 
                 9.2 
                 97 
                 NONE 
               
               
                   
                 17 
                 E: 60 
                 20 
                 REMNANT 
                   
                   
                   
                 11.9 
                 15.8 
                 9.9 
                 98 
                 NONE 
               
               
                   
                 18 
                 F: 90 
                 5 
                 REMNANT 
                   
                   
                   
                 19.5 
                 13.8 
                 2.8 
                 94 
                 NONE 
               
             
          
           
               
                 CONVEN- 
                 ZrO 2 : 50, In 2 O 3 : 30 
                 REMNANT 
                   
                   
                   
                 12.5 
                 15.0 
                 10.0 
                 70 
                 EXISTING 
               
               
                 TIONAL 2 
               
               
                   
               
             
          
         
       
     
     Based on the result indicated in Table 3, in the targets 10 to 18 of the invention, 90% or more of Zr as the oxidative product phase in which Zr and In are combined is dispersed in a base material. In the conventional target 2, an amount of Zr that is less than 90%, which serves as the oxidative product phase in which Zr and In are combined, is dispersed in the base material. 
     Compared with the conventional target 2 having compositions in which a ZrO 2  phase exists in large numbers, it is seen that a crack is not generated in a high output sputtering in the targets 10 to 18 of the invention. 
     Example 3 
     TiO 2  powders and In 2 O 3  powders which had been prepared in advance were added to the powders A to F which were made of oxidative products in which Zr and In are combined, and which had been prepared in advance as indicated in Table 1, so as to obtain the percentage indicated in Table 4; furthermore, zirconia balls having a diameter of 1 mm and the dispersion liquid which serves as deionized water were added thereto and were mixed for 10 minutes in a bead mill of a wet grinding apparatus; and mixed powders were produced. 
     The obtained mixed powders were dried using a hot plate that was heated at 150° C., and moisture was thereby removed. 
     By use of a cold isostatic pressing method (CIP method), a molded body having a diameter of 200 mm and a thickness of 10 mm was produced from the mixed powders from which moisture had been removed by drying in the above-described manner. 
     Consequently, under the conditions indicated in Table 4, a baked body was produced by baking the molded body; furthermore, a surface of the baked body was machined by mechanical working, and targets 19 to 27 of the invention having a diameter of 125 mm and a thickness of 6 mm and having component compositions as indicated in Table 4 were thereby produced. 
     The percentage of Zr that is included in the targets 19 to 27 of the invention as the oxidative product phase in which Zr and In are combined and that is dispersed in a base material is determined in a manner similar to the Example 1, and the result thereof is indicated in Table 4. 
     Conventional Example 3 
     ZrO 2  powders, In 2 O 3  powders, and TiO 2  powders which have been prepared as raw material powders in advance were mixed together so as to obtain the percentage indicated in Table 4; furthermore, zirconia balls having a diameter of 1 mm and the dispersion liquid which serves as deionized water were added thereto and were mixed for 10 minutes in a bead mill of a wet grinding apparatus; and mixed powders were produced. 
     The obtained mixed powders were dried using a hot plate that was heated at 150° C., and moisture was thereby removed. 
     By use of a cold isostatic pressing method (CIP method), a molded body having a diameter of 200 mm and a thickness of 10 mm was produced from the mixed powders from which moisture had been removed by drying in the above-described manner. 
     Consequently, under the conditions indicated in Table 4, a baked body was produced by baking the molded body; furthermore, a surface of the baked body was machined by mechanical working, and a conventional target 3 having a diameter of 125 mm and a thickness of 6 mm and having component compositions as indicated in Table 4 were thereby produced. 
     The percentage of Zr that is included in the conventional target 3 as the oxidative product phase in which Zr and In are combined and that is dispersed in a base material is determined in a manner similar to the Conventional Example 1, and the result thereof is indicated in Table 4. 
     In a state where each of the targets 19 to 27 of the invention and conventional target 3 which are obtained in the above-described manner is solder-mounted to a water-cooling backing plate made of oxygen-free copper, the target is attached to a sputtering apparatus, the inside of the apparatus is evacuated by use of a vacuum evacuation device so as to be less than or equal to 1×10 −6  Torr; thereafter, the inside of the apparatus is set to a gas partial pressure of 10 mTorr of Ar in an atmosphere by supplying Ar gas into the apparatus. 
     By use of the targets 19 to 27 of the invention and the conventional target 3 in the above-described conditions, a sputtering is performed for 3 minutes by applying 2 kW greater than normal of sputtering power by use of an RF power source; thereafter, the sputtering is stopped for 1 minute. 
     The foregoing operation in which the sputtering is stopped for 1 minute after the sputtering for 3 minutes was repeated at 10 times. 
     Subsequently, the target is removed from the sputtering apparatus, the target is observed and it is determined whether or not a crack has been generated in the target, and the results of which are indicated in Table 4. 
     
       
         
               
               
               
               
               
               
             
               
               
               
               
               
               
               
               
             
               
               
               
               
               
               
               
               
               
               
             
               
               
               
               
               
               
               
               
               
               
               
               
             
               
               
               
               
               
               
               
               
               
               
               
               
               
             
               
               
               
               
               
               
               
               
               
               
               
             
           
               
                   
                 TABLE 4 
               
             
             
               
                   
                   
               
               
                   
                   
                   
                   
                 PERCENT- 
                   
               
               
                   
                   
                   
                   
                 AGE 
               
               
                   
                   
                   
                   
                 OF 
               
               
                   
                   
                   
                   
                 Zr THAT IS 
               
               
                   
                 COMPONENT COMPOSITION OF 
                   
                   
                 INCLUDED 
               
               
                   
                 RAW MATERIAL POWDERS 
                   
                   
                 IN TARGET 
               
               
                   
                 (MOL %) 
                   
                   
                 AND THAT 
               
             
          
           
               
                   
                 POWDERED 
                   
                   
                   
                   
                 SERVES AS 
                   
               
               
                   
                 OXIDATIVE 
                   
                   
                 BAKING 
                 COMPONENT 
                 OXIDATIVE 
               
               
                   
                 PRODUCT IN 
                   
                   
                 CONDITIONS 
                 COMPOSITION 
                 PRODUCT IN 
                 EXISTENCE 
               
             
          
           
               
                   
                 WHICH Zr AND In 
                   
                   
                   
                 TEM- 
                   
                 OF TARGET 
                 WHICH Zr 
                 OF CRACK IN 
               
               
                   
                 ARE COMBINED 
                   
                   
                 AT- 
                 PERA- 
                   
                 (ATOM %) 
                 AND In ARE 
                 TARGET 
               
               
                   
                 SHOWN IN 
                   
                   
                 MOS- 
                 TURE 
                 TIME 
                 Zr a In b Ti c O 100−a−b−c   
                 COMBINED 
                 USED IN 
               
             
          
           
               
                 TARGET 
                 TABLE 1 
                 In 2 O 3   
                 TiO 2   
                 PHERE 
                 (° C.) 
                 (H) 
                 a 
                 b 
                 c 
                 (%) 
                 SPUTTERING 
               
               
                   
               
             
          
           
               
                 INVENTION 
                 19 
                 A: 30 
                 40 
                 REMNANT 
                 AIR 
                 1400 
                 4 
                 6.3 
                 23.2 
                 7.7 
                 98 
                 NONE 
               
               
                   
                 20 
                 A: 50 
                 30 
                 REMNANT 
                   
                   
                   
                 10.8 
                 20.6 
                 5.3 
                 97 
                 NONE 
               
               
                   
                 21 
                 B: 40 
                 30 
                 REMNANT 
                   
                   
                   
                 8.5 
                 20.2 
                 8.0 
                 98 
                 NONE 
               
               
                   
                 22 
                 C: 25 
                 35 
                 REMNANT 
                   
                   
                   
                 5.3 
                 20.9 
                 5.0 
                 98 
                 NONE 
               
               
                   
                 23 
                 C: 70 
                 20 
                 REMNANT 
                   
                   
                   
                 15.5 
                 18.2 
                 2.7 
                 97 
                 NONE 
               
               
                   
                 24 
                 D: 70 
                 20 
                 REMNANT 
                   
                   
                   
                 15.0 
                 18.8 
                 2.7 
                 96 
                 NONE 
               
               
                   
                 25 
                 E: 40 
                 40 
                 REMNANT 
                   
                   
                   
                 8.1 
                 24.2 
                 5.1 
                 98 
                 NONE 
               
               
                   
                 26 
                 E: 60 
                 20 
                 REMNANT 
                   
                   
                   
                 13.2 
                 17.6 
                 5.5 
                 99 
                 NONE 
               
               
                   
                 27 
                 F: 90 
                 5 
                 REMNANT 
                   
                   
                   
                 20.0 
                 14.2 
                 1.4 
                 94 
                 NONE 
               
             
          
           
               
                 CONVEN- 
                 ZrO 2 : 50, In 2 O 3 : 30 
                 REMNANT 
                   
                   
                   
                 13.9 
                 16.7 
                 5.5 
                 60 
                 EXISTING 
               
               
                 TIONAL 3 
               
               
                   
               
             
          
         
       
     
     Based on the result indicated in Table 4, in the targets 19 to 27 of the invention, 90% or more of Zr as the oxidative product phase in which Zr and In are combined is dispersed in a base material. In the conventional target 3, an amount of Zr that is less than 90%, which serves as the oxidative product phase in which Zr and In are combined, is dispersed in the base material. 
     Compared with the conventional target 3 having compositions in which a ZrO 2  phase exists in large numbers, it is seen that a crack is not generated in a high output sputtering in the targets 19 to 27 of the invention. 
     Example 4 
     CeO 2  powders and In 2 O 3  powders which had been prepared in advance were added to the powders A to F which were made of oxidative products in which Zr and In are combined, and which had been prepared in advance as indicated in Table 1, so as to obtain the percentage indicated in Table 5; furthermore, zirconia balls having a diameter of 1 mm and the dispersion liquid which serves as deionized water were added thereto and were mixed for 10 minutes in a bead mill of a wet grinding apparatus; and mixed powders were produced. 
     The obtained mixed powders were dried using a hot plate that was heated at 150° C., and moisture was thereby removed. 
     By use of a cold isostatic pressing method (CIP method), a molded body having a diameter of 200 mm and a thickness of 10 mm was produced from the mixed powders from which moisture had been removed by drying in the above-described manner. 
     Consequently, under the conditions indicated in Table 5, a baked body was produced by baking the molded body; furthermore, a surface of the baked body was machined by mechanical working, and targets 28 to 36 of the invention having a diameter of 125 mm and a thickness of 6 mm and having component compositions as indicated in Table 5 were thereby produced. 
     The percentage of Zr that is included in the targets 28 to 36 of the invention as the oxidative product phase in which Zr and In are combined and that is dispersed in a base material is determined in a manner similar to the Example 1, and the result thereof is indicated in Table 5. 
     Conventional Example 4 
     ZrO 2  powders, In 2 O 3  powders, and CeO 2  powders which have been prepared as raw material powders in advance were mixed together so as to obtain the percentage indicated in Table 5; furthermore, zirconia balls having a diameter of 1 mm and the dispersion liquid which serves as deionized water were added thereto and were mixed for 10 minutes in a bead mill of a wet grinding apparatus; and mixed powders were produced. 
     The obtained mixed powders were dried using a hot plate that was heated at 150° C., and moisture was thereby removed. 
     By use of a cold isostatic pressing method (CIP method), a molded body having a diameter of 200 mm and a thickness of 10 mm was produced from the mixed powders from which moisture had been removed by drying in the above-described manner. 
     Consequently, under the conditions indicated in Table 5, a baked body was produced by baking the molded body; furthermore, a surface of the baked body was machined by mechanical working, and a conventional target 4 having a diameter of 125 mm and a thickness of 6 mm and having component compositions as indicated in Table 5 were thereby produced. 
     The percentage of Zr that is included in the conventional target 4 as the oxidative product phase in which Zr and In are combined and that is dispersed in a base material is determined in a manner similar to the Conventional Example 1, and the result thereof is indicated in Table 5. 
     In a state where each of the targets 28 to 36 of the invention and conventional target 4 which are obtained in the above-described manner is solder-mounted to a water-cooling backing plate made of oxygen-free copper, the target is attached to a sputtering apparatus, the inside of the apparatus is evacuated by use of a vacuum evacuation device so as to be less than or equal to 1×10 −6  Torr; thereafter, the inside of the apparatus is set to a gas partial pressure of 10 mTorr of Ar in an atmosphere by supplying Ar gas into the apparatus. 
     By use of the targets 28 to 36 of the invention and the conventional target 4 in the above-described conditions, a sputtering is performed for 3 minutes by applying 2 kW greater than normal of sputtering power by use of an RF power source; thereafter, the sputtering is stopped for 1 minute. 
     The foregoing operation in which the sputtering is stopped for 1 minute after the sputtering for 3 minutes was repeated at 10 times. 
     Subsequently, the target is removed from the sputtering apparatus, the target is observed and it is determined whether or not a crack has been generated in the target, and the results of which are indicated in Table 5. 
     
       
         
               
               
               
               
               
               
             
               
               
               
               
               
               
               
               
             
               
               
               
               
               
               
               
               
               
               
             
               
               
               
               
               
               
               
               
               
               
               
               
             
               
               
               
               
               
               
               
               
               
               
               
               
               
             
               
               
               
               
               
               
               
               
               
               
               
             
           
               
                   
                 TABLE 5 
               
             
             
               
                   
                   
               
               
                   
                   
                   
                   
                 PERCENT- 
                   
               
               
                   
                   
                   
                   
                 AGE OF 
               
               
                   
                   
                   
                   
                 Zr THAT IS 
               
               
                   
                 COMPONENT COMPOSITION OF 
                   
                   
                 INCLUDED 
               
               
                   
                 RAW MATERIAL POWDERS 
                   
                   
                 IN TARGET 
               
               
                   
                 (MOL %) 
                   
                   
                 AND THAT 
               
             
          
           
               
                   
                 POWDERED 
                   
                   
                   
                   
                 SERVES AS 
                   
               
               
                   
                 OXIDATIVE 
                   
                   
                 BAKING 
                 COMPONENT 
                 OXIDATIVE 
               
               
                   
                 PRODUCT IN 
                   
                   
                 CONDITIONS 
                 COMPOSITION 
                 PRODUCT IN 
                 EXISTENCE 
               
             
          
           
               
                   
                 WHICH Zr AND In 
                   
                   
                   
                 TEM 
                   
                 OF TARGET 
                 WHICH Zr 
                 OF CRACK IN 
               
               
                   
                 ARE COMBINED 
                   
                   
                 AT- 
                 PERA- 
                   
                 (ATOM %) 
                 AND In ARE 
                 TARGET 
               
               
                   
                 SHOWN IN 
                   
                   
                 MOS- 
                 TURE 
                 TIME 
                 Zr a In b Ce c O 100−a−b−c   
                 COMBINED 
                 USED IN 
               
             
          
           
               
                 TARGET 
                 TABLE 1 
                 In 2 O 3   
                 CeO 2   
                 PHERE 
                 (° C.) 
                 (H) 
                 a 
                 b 
                 c 
                 (%) 
                 SPUTTERING 
               
               
                   
               
             
          
           
               
                 INVENTION 
                 28 
                 A: 30 
                 40 
                 REMNANT 
                 AIR 
                 1400 
                 4 
                 6.3 
                 23.2 
                 7.7 
                 99 
                 NONE 
               
               
                   
                 29 
                 A: 50 
                 30 
                 REMNANT 
                   
                   
                   
                 10.8 
                 20.6 
                 5.3 
                 97 
                 NONE 
               
               
                   
                 30 
                 B: 40 
                 30 
                 REMNANT 
                   
                   
                   
                 8.5 
                 20.2 
                 8.0 
                 98 
                 NONE 
               
               
                   
                 31 
                 C: 25 
                 35 
                 REMNANT 
                   
                   
                   
                 5.3 
                 20.9 
                 10.5 
                 97 
                 NONE 
               
               
                   
                 32 
                 C: 70 
                 20 
                 REMNANT 
                   
                   
                   
                 15.5 
                 18.2 
                 2.7 
                 96 
                 NONE 
               
               
                   
                 33 
                 D: 70 
                 20 
                 REMNANT 
                   
                   
                   
                 15.0 
                 18.8 
                 2.7 
                 96 
                 NONE 
               
               
                   
                 34 
                 E: 40 
                 40 
                 REMNANT 
                   
                   
                   
                 8.1 
                 24.2 
                 5.1 
                 96 
                 NONE 
               
               
                   
                 35 
                 E: 60 
                 20 
                 REMNANT 
                   
                   
                   
                 13.2 
                 17.6 
                 5.5 
                 98 
                 NONE 
               
               
                   
                 36 
                 F: 90 
                 5 
                 REMNANT 
                   
                   
                   
                 20.0 
                 14.2 
                 1.4 
                 95 
                 NONE 
               
             
          
           
               
                 CONVEN- 
                 ZrO 2 : 50, In 2 O 3 : 30 
                 REMNANT 
                   
                   
                   
                 13.9 
                 16.7 
                 5.5 
                 65 
                 EXISTING 
               
               
                 TIONAL 4 
               
               
                   
               
             
          
         
       
     
     Based on the result indicated in Table 5, in the targets 28 to 36 of the invention, 90% or more of Zr as the oxidative product phase in which Zr and In are combined is dispersed in a base material. In the conventional target 4, an amount of Zr that is less than 90%, which serves as the oxidative product phase in which Zr and In are combined, is dispersed in the base material. 
     Compared with the conventional target 4 having compositions in which a ZrO 2  phase exists in large numbers, it is seen that a crack is not generated in a high output sputtering in the targets 28 to 36 of the invention. 
     Example 5 
     SnO 2  powders and In 2 O 3  powders which had been prepared in advance were added to the powders A to F which were made of oxidative products in which Zr and In are combined, and which had been prepared in advance as indicated in Table 1, so as to obtain the percentage indicated in Table 6; furthermore, zirconia balls having a diameter of 1 mm and the dispersion liquid which serves as deionized water were added thereto and were mixed for 10 minutes in a bead mill of a wet grinding apparatus; and mixed powders were produced. 
     The obtained mixed powders were dried using a hot plate that was heated at 150° C., and moisture was thereby removed. 
     By use of a cold isostatic pressing method (CIP method), a molded body having a diameter of 200 mm and a thickness of 10 mm was produced from the mixed powders from which moisture had been removed by drying in the above-described manner. 
     Consequently, under the conditions indicated in Table 6, a baked body was produced by baking the molded body; furthermore, a surface of the baked body was machined by mechanical working, and targets 37 to 45 of the invention having a diameter of 125 mm and a thickness of 6 mm and having component compositions as indicated in Table 6 were thereby produced. 
     The percentage of Zr that is included in the targets 37 to 45 of the invention as the oxidative product phase in which Zr and In are combined and that is dispersed in a base material is determined in a manner similar to the Example 1, and the result thereof is indicated in Table 6. 
     Conventional Example 5 
     ZrO 2  powders, In 2 O 3  powders, and SnO 2  powders which have been prepared as raw material powders in advance were mixed together so as to obtain the percentage indicated in Table 6; furthermore, zirconia balls having a diameter of 1 mm and the dispersion liquid which serves as deionized water were added thereto and were mixed for 10 minutes in a bead mill of a wet grinding apparatus; and mixed powders were produced. 
     The obtained mixed powders were dried using a hot plate that was heated at 150° C., and moisture was thereby removed. 
     By use of a cold isostatic pressing method (CIP method), a molded body having a diameter of 200 mm and a thickness of 10 mm was produced from the mixed powders from which moisture had been removed by drying in the above-described manner. 
     Consequently, under the conditions indicated in Table 6, a baked body was produced by baking the molded body; furthermore, a surface of the baked body was machined by mechanical working, and a conventional target 5 having a diameter of 125 mm and a thickness of 6 mm and having component compositions as indicated in Table 6 were thereby produced. 
     The percentage of Zr that is included in the conventional target 5 as the oxidative product phase in which Zr and In are combined and that is dispersed in a base material is determined in a manner similar to the Conventional Example 1, and the result thereof is indicated in Table 6. 
     In a state where each of the targets 37 to 45 of the invention and conventional target 5 which are obtained in the above-described manner is solder-mounted to a water-cooling backing plate made of oxygen-free copper, the target is attached to a sputtering apparatus, the inside of the apparatus is evacuated by use of a vacuum evacuation device so as to be less than or equal to 1×10 −6  Torr; thereafter, the inside of the apparatus is set to a gas partial pressure of 10 mTorr of Ar in an atmosphere by supplying Ar gas into the apparatus. 
     By use of the targets 37 to 45 of the invention and the conventional target 5 in the above-described conditions, a sputtering is performed for 3 minutes by applying 2 kW greater than normal of sputtering power by use of an RF power source; thereafter, the sputtering is stopped for 1 minute. 
     The foregoing operation in which the sputtering is stopped for 1 minute after the sputtering for 3 minutes was repeated at 10 times. 
     Subsequently, the target is removed from the sputtering apparatus, the target is observed and it is determined whether or not a crack has been generated in the target, and the results of which are indicated in Table 6. 
     
       
         
               
               
               
               
               
               
             
               
               
               
               
               
               
               
               
             
               
               
               
               
               
               
               
               
               
               
             
               
               
               
               
               
               
               
               
               
               
               
               
             
               
               
               
               
               
               
               
               
               
               
               
               
               
             
               
               
               
               
               
               
               
               
               
               
               
             
           
               
                   
                 TABLE 6 
               
             
             
               
                   
                   
               
               
                   
                   
                   
                   
                 PERCENT- 
                   
               
               
                   
                   
                   
                   
                 AGE OF 
               
               
                   
                   
                   
                   
                 Zr THAT IS 
               
               
                   
                 COMPONENT COMPOSITION OF 
                   
                   
                 INCLUDED 
               
               
                   
                 RAW MATERIAL POWDERS 
                   
                   
                 IN TARGET 
               
               
                   
                 (MOL %) 
                   
                   
                 AND THAT 
               
             
          
           
               
                   
                 POWDERED 
                   
                   
                   
                   
                 SERVES AS 
                   
               
               
                   
                 OXIDATIVE 
                   
                   
                 BAKING 
                 COMPONENT 
                 OXIDATIVE 
               
               
                   
                 PRODUCT IN 
                   
                   
                 CONDITIONS 
                 COMPOSITION 
                 PRODUCT IN 
                 EXISTENCE 
               
             
          
           
               
                   
                 WHICH Zr AND In 
                   
                   
                   
                 TEM- 
                   
                 OF TARGET 
                 WHICH Zr 
                 OF CRACK IN 
               
               
                   
                 ARE COMBINED 
                   
                   
                 AT- 
                 PERA- 
                   
                 (ATOM %) 
                 AND In ARE 
                 TARGET 
               
               
                   
                 SHOWN IN 
                   
                   
                 MOS- 
                 TURE 
                 TIME 
                 Zr a In b Sn c O 100−a−b−c   
                 COMBINED 
                 USED IN 
               
             
          
           
               
                 TARGET 
                 TABLE 1 
                 In 2 O 3   
                 SnO 2   
                 PHERE 
                 (° C.) 
                 (H) 
                 a 
                 b 
                 c 
                 (%) 
                 SPUTTERING 
               
               
                   
               
             
          
           
               
                 INVENTION 
                 37 
                 A: 30 
                 40 
                 REMNANT 
                 OXY- 
                 1400 
                 4 
                 6.5 
                 24.2 
                 6.5 
                 98 
                 NONE 
               
               
                   
                 38 
                 A: 50 
                 30 
                 REMNANT 
                 GEN 
                   
                   
                 11.0 
                 21.0 
                 4.7 
                 98 
                 NONE 
               
               
                   
                 39 
                 B: 40 
                 30 
                 REMNANT 
                   
                   
                   
                 8.5 
                 20.2 
                 7.8 
                 97 
                 NONE 
               
               
                   
                 40 
                 C: 25 
                 35 
                 REMNANT 
                   
                   
                   
                 5.5 
                 21.0 
                 10.0 
                 98 
                 NONE 
               
               
                   
                 41 
                 C: 70 
                 20 
                 REMNANT 
                   
                   
                   
                 15.9 
                 18.2 
                 3.1 
                 97 
                 NONE 
               
               
                   
                 42 
                 D: 70 
                 20 
                 REMNANT 
                   
                   
                   
                 15.0 
                 18.8 
                 2.7 
                 96 
                 NONE 
               
               
                   
                 43 
                 E: 40 
                 40 
                 REMNANT 
                   
                   
                   
                 8.3 
                 24.5 
                 4.5 
                 99 
                 NONE 
               
               
                   
                 44 
                 E: 30 
                 20 
                 REMNANT 
                   
                   
                   
                 13.1 
                 17.6 
                 5.6 
                 98 
                 NONE 
               
               
                   
                 45 
                 F: 90 
                 5 
                 REMNANT 
                   
                   
                   
                 20.0 
                 14.7 
                 0.9 
                 94 
                 NONE 
               
             
          
           
               
                 CONVEN- 
                 ZrO 2 : 50, In 2 O 3 : 30 
                 REMNANT 
                   
                   
                   
                 14.1 
                 16.9 
                 5.1 
                 78 
                 EXISTING 
               
               
                 TIONAL 5 
               
               
                   
               
             
          
         
       
     
     Based on the result indicated in Table 6, in the targets 37 to 45 of the invention, 90% or more of Zr as the oxidative product phase in which Zr and In are combined is dispersed in a base material. In the conventional target 5, an amount of Zr that is less than 90%, which serves as the oxidative product phase in which Zr and In are combined, is dispersed in the base material. 
     Compared with the conventional target 5 having compositions in which a ZrO 2  phase exists in large numbers, it is seen that a crack is not generated in a high output sputtering in the targets 37 to 45 of the invention. 
     Example 6 
     Cr 2 O 3  powders and In 2 O 3  powders which had been prepared in advance were added to the powders A to F which were made of oxidative products in which Zr and In are combined, and which had been prepared in advance as indicated in Table 1, so as to obtain the percentage indicated in Table 7; furthermore, zirconia balls having a diameter of 1 mm and the dispersion liquid which serves as deionized water were added thereto and were mixed for 10 minutes in a bead mill of a wet grinding apparatus; and mixed powders were produced. 
     The obtained mixed powders were dried using a hot plate that was heated at 150° C., and moisture was thereby removed. 
     By use of a cold isostatic pressing method (CIP method), a molded body having a diameter of 200 mm and a thickness of 10 mm was produced from the mixed powders from which moisture had been removed by drying in the above-described manner. 
     Consequently, under the conditions indicated in Table 7, a baked body was produced by baking the molded body; furthermore, a surface of the baked body was machined by mechanical working, and targets 46 to 54 of the invention having a diameter of 125 mm and a thickness of 6 mm and having component compositions as indicated in Table 7 were thereby produced. 
     The percentage of Zr that is included in the targets 46 to 54 of the invention as the oxidative product phase in which Zr and In are combined and that is dispersed in a base material is determined in a manner similar to the Example 1, and the result thereof is indicated in Table 7. 
     Conventional Example 6 
     ZrO 2  powders, In 2 O 3  powders, and Cr 2 O 3  powders which have been prepared as raw material powders in advance were mixed together so as to obtain the percentage indicated in Table 7; furthermore, zirconia balls having a diameter of 1 mm and the dispersion liquid which serves as deionized water were added thereto and were mixed for 10 minutes in a bead mill of a wet grinding apparatus; and mixed powders were produced. 
     The obtained mixed powders were dried using a hot plate that was heated at 150° C., and moisture was thereby removed. 
     By use of a cold isostatic pressing method (CIP method), a molded body having a diameter of 200 mm and a thickness of 10 mm was produced from the mixed powders from which moisture had been removed by drying in the above-described manner. 
     Consequently, under the conditions indicated in Table 7, a baked body was produced by baking the molded body; furthermore, a surface of the baked body was machined by mechanical working, and a conventional target 6 having a diameter of 125 mm and a thickness of 6 mm and having component compositions as indicated in Table 7 were thereby produced. 
     The percentage of Zr that is included in the conventional target 6 as the oxidative product phase in which Zr and In are combined and that is dispersed in a base material is determined in a manner similar to the Conventional Example 1, and the result thereof is indicated in Table 7. 
     In a state where each of the targets 46 to 54 of the invention and conventional target 6 which are obtained in the above-described manner is solder-mounted to a water-cooling backing plate made of oxygen-free copper, the target is attached to a sputtering apparatus, the inside of the apparatus is evacuated by use of a vacuum evacuation device so as to be less than or equal to 1×10 −6  Torr; thereafter, the inside of the apparatus is set to a gas partial pressure of 10 mTorr of Ar in an atmosphere by supplying Ar gas into the apparatus. 
     By use of the targets 46 to 54 of the invention and the conventional target 6 in the above-described conditions, a sputtering is performed for 3 minutes by applying 2 kW greater than normal of sputtering power by use of an RF power source; thereafter, the sputtering is stopped for 1 minute. 
     The foregoing operation in which the sputtering is stopped for 1 minute after the sputtering for 3 minutes was repeated at 10 times. 
     Subsequently, the target is removed from the sputtering apparatus, the target is observed and it is determined whether or not a crack has been generated in the target, and the results of which are indicated in Table 7. 
     
       
         
               
               
               
               
               
               
             
               
               
               
               
               
               
               
               
             
               
               
               
               
               
               
               
               
               
               
             
               
               
               
               
               
               
               
               
               
               
               
               
             
               
               
               
               
               
               
               
               
               
               
               
               
               
             
               
               
               
               
               
               
               
               
               
               
               
             
           
               
                   
                 TABLE 7 
               
             
             
               
                   
                   
               
               
                   
                   
                   
                   
                 PERCEN- 
                   
               
               
                   
                   
                   
                   
                 TAGE OF 
               
               
                   
                   
                   
                   
                 Zr THAT IS 
               
               
                   
                 COMPONENT COMPOSITION OF 
                   
                   
                 INCLUDED 
               
               
                   
                 RAW MATERIAL POWDERS 
                   
                   
                 IN TARGET 
               
               
                   
                 (MOL %) 
                   
                   
                 AND THAT 
               
             
          
           
               
                   
                 POWDERED 
                   
                   
                   
                   
                 SERVES AS 
                   
               
               
                   
                 OXIDATIVE 
                   
                   
                 BAKING 
                 COMPONENT 
                 OXIDATIVE 
               
               
                   
                 PRODUCT IN 
                   
                   
                 CONDITIONS 
                 COMPOSITION 
                 PRODUCT IN 
                 EXISTENCE 
               
             
          
           
               
                   
                 WHICH Zr AND In 
                   
                   
                   
                 TEM- 
                   
                 OF TARGET 
                 WHICH Zr 
                 OF CRACK IN 
               
               
                   
                 ARE COMBINED 
                   
                   
                 AT- 
                 PERA- 
                   
                 (ATOM %) 
                 AND In ARE 
                 TARGET 
               
               
                   
                 SHOWN IN 
                   
                   
                 MOS- 
                 TURE 
                 TIME 
                 Zr a In b Cr c O 100−a−b−c   
                 COMBINED 
                 USED IN 
               
             
          
           
               
                 TARGET 
                 TABLE 1 
                 In 2 O 3   
                 Cr 2 O 3   
                 PHERE 
                 (° C.) 
                 (H) 
                 a 
                 b 
                 c 
                 (%) 
                 SPUTTERING 
               
               
                   
               
             
          
           
               
                 INVENTION 
                 46 
                 A: 30 
                 40 
                 REMNANT 
                 AIR 
                 1400 
                 4 
                 5.6 
                 20.2 
                 13.0 
                 99 
                 NONE 
               
               
                   
                 47 
                 A: 50 
                 30 
                 REMNANT 
                   
                   
                   
                 9.9 
                 18.9 
                 9.1 
                 99 
                 NONE 
               
               
                   
                 48 
                 B: 40 
                 30 
                 REMNANT 
                   
                   
                   
                 7.3 
                 17.5 
                 13.6 
                 99 
                 NONE 
               
               
                   
                 49 
                 C: 40 
                 20 
                 REMNANT 
                   
                   
                   
                 7.4 
                 12.9 
                 18.0 
                 98 
                 NONE 
               
               
                   
                 50 
                 C: 70 
                 20 
                 REMNANT 
                   
                   
                   
                 14.7 
                 17.2 
                 5.2 
                 97 
                 NONE 
               
               
                   
                 51 
                 D: 70 
                 20 
                 REMNANT 
                   
                   
                   
                 14.2 
                 17.8 
                 5.1 
                 97 
                 NONE 
               
               
                   
                 52 
                 E: 40 
                 40 
                 REMNANT 
                   
                   
                   
                 7.5 
                 22.2 
                 8.8 
                 98 
                 NONE 
               
               
                   
                 53 
                 E: 60 
                 20 
                 REMNANT 
                   
                   
                   
                 12.0 
                 15.9 
                 9.7 
                 99 
                 NONE 
               
               
                   
                 54 
                 F: 90 
                 5 
                 REMNANT 
                   
                   
                   
                 19.5 
                 13.8 
                 2.8 
                 96 
                 NONE 
               
             
          
           
               
                 CONVEN- 
                 ZrO 2 : 50, In 2 O 3 : 
                 REMNANT 
                   
                   
                   
                 12.7 
                 9.5 
                 9.5 
                 70 
                 EXISTING 
               
               
                 TIONAL 6 
               
               
                   
               
             
          
         
       
     
     Based on the result indicated in Table 7, in the targets 46 to 54 of the invention, 90% or more of Zr as the oxidative product phase in which Zr and In are combined is dispersed in a base material. In the conventional target 6, an amount of Zr that is less than 90%, which serves as the oxidative product phase in which Zr and In are combined, is dispersed in the base material. 
     Compared with the conventional target 6 having compositions in which a ZrO 2  phase exists in large numbers, it is seen that a crack is not generated in a high output sputtering in the targets 46 to 54 of the invention.