Judul: Adsorpsi ion Cr(VI) dan Cr(III) dengan montmorilonit termodifikasi oksida besi
Abstrak: Montmorilonit merupakan mineral yang melimpah di Indonesia dan berpotensi menjerap logam berat seperti kromium (Cr). Tujuan penelitian ini, yaitu melakukan aktivasi montmorilonit dengan natrium kemudian dimodifikasi dengan oksida besi untuk mengadsorpsi Cr(VI) dan Cr(III). Parameter yang diuji adalah penentuan kondisi optimum adsorpsi Cr(VI) dan Cr(III), dari segi pH, waktu kontak, konsentrasi awal, dan pola isoterm adsorpsi. Kapasitas adsorpsi Cr(VI) untuk montmorilonit alam, Na-montmorilonit, dan montmorilonit termodifikasi dihasilkan berturut-turut sebesar 3,30 mg/g adsorben (pH 4, selama 48 jam, dan konsentrasi awal 500 mg/L); 3,76 mg/g adsorben (pH 4, selama 48 jam, dan konsentrasi 300 mg/L); dan 3,97 mg/g adsorben (pH 3, selama 48 jam, dan konsentrasi 100 mg/L). Kapasitas adsorpsi Cr(III) untuk montmorilonit alam, Na-montmorilonit, dan montmorilonit termodifikasi berturut-turut sebesar 4,72 mg/g adsorben (pH 7, selama 12 jam, dan konsentrasi 700 mg/L); 4,76 mg/g adsorben (pH 7, selama 36 jam, dan konsentrasi 700 mg/L); dan 4,83 mg/g adsorben (pH 5, selama 6 jam, dan konsentrasi 200 mg/L). Hasil menunjukan bahwa aktivasi montmorilonit dengan natrium dan modifikasi dengan oksida besi telah meningkatkan kapasitas adsorpsi baik Cr(VI) maupun Cr(III) dibandingkan montmorilonit alam.
Keyword: Logam kromium, Bentonit, Isoterm adsorpsi

Judul: Adsorpsi dan desorpsi ion kromium(VI) pada bentonit yang dimodifikasi Heksadesiltrimetilamonium bromida
Abstrak: Bentonite is abundant mineral in Indonesia and potentially as adsorbent. Bentonite has negatively charge, so bentonite has high capability to adsorp cations, while the capability of bentonite to adsorp anion was very low. This research was modified bentonite from Leuwiliang with hexadecyltrimethylammonium bromide (HDTMABr). The result of bentonite modification was changes bentonite surface character from hidrofilic become hidrofobic or organofilic, so that can adsorp anion, like Cr(VI). This research made organobentonite 25, 50, and 100 % CEC. Some methodes were done in this research, they were determination of CEC, acidity, and adsorption optimum condition of Cr(VI) that covered determination of adsorption pH, contact time, isotherm, and desorption of Cr(VI) from organobentonite. Capacity Exchange Cation of bentonite, organobentonite 25 %, organobentonite 50 %, and organobentonite 100 % were 54.53, 45.14, 37.37, and 20.72 me/100 g, respectively. Acidity of bentonite, organobentonite 25 %, organobentonite 50 %, and organobentonite 100 % were 4.95, 3.62, 0.90, and 0.60 mmol/g, respectively. Optimum adsorption condition of Cr(VI) onto bentonite, organobentonite 25 %, organobentonite 50 %, and organobentonite 100 % were consist of pH 2 until 4, contact time 3 until 4 hours, on concentration 200 until 500 ppm. Adsorbtion capacity of bentonite, organobentonite 25 %, organobentonite 50 %, and organobentonite 100 %, respectively were 4.44, 11.96, 22.09, and 20.53 mg/g. Ability of HCl, aquadest, and CaCl2 to desorbed Cr(VI) from organobentonite was low, this matter showed that Cr(VI) was trapped strongly on organobentonite.
Keyword: 

Judul: Pola Reproduksi Anjing
Abstrak: Anjing (Canis familiaris) merupakan hewan liar yang te1ah menga1ami proses domestikasi. Banyaknya kegunaan hewan ini dalam kehidupan manusia sehari-hari, menyebabkan banyak yang memelihara dan mengembangbiakkannya. Siklus reproduksi anjing sangat unik diantara hewan-hewan domestik lainnya. Umumnya hanya mengalami dua kali musim kawin da1am setahun (mono estrus) dan periode berahi yang panjang. Proestrus terjadi kira-kira 9 hari, dan estrus atau berahi yang sebenarnya berlangsung antara 7-9 hari. Ovulasi biasanya terjadi pad a hari ke tiga periode estrus. Jika konsepsi tidak terjadi, periode metestrus akan di1anjutkan dengan terbentuknya kebuntingan palsu (pseodopregnancy) yang 1amanya hampir sarna dengan kebuntingan sebenarnya.
Keyword: