Judul: Pendadahan karakterisasi dan aplikasi film tipis Ba0,5Sr0,5TiO3 sebagai pengukur konsentrasi gula
Abstrak: Pure Ba0,5Sr0,5TiO3 (BST) thin film, BST doped by niobium (BNST) and BST doped by iron (BFST) have been synthesized on p-type Si (100) substrates using Chemical Solution Deposition (CSD) methods followed by spin coating and annealing techniques. Current-voltage characterizations on these sample result in agreement that all of the BST, BNST, and BFST thin films have photodiode properties. Electrical conductivity values of BST, BNST, and BFST are in the range of conductivity values of semiconductor materials. Niobium or iron doping on the BST samples increase their conductivity value their dielectric constant. This conductivity values may change when a light is exposed on the film surface. Absorbance and reflectance characterizations show that the BST, BNST, and BFST thin films absorb certain range of visible and infrared light. It is convincing that the BST, BNST, and BFST thin films might be used as photodiode light sensor.
Keyword: Thin film, spin coating, Electrical conductivity, Sugar concentration

Judul: Karakterisasi Optik dan Listrik Film Ba0.55Sr0.45TiO3 untuk Aplikasi Sensor Kadar Gula Darah
Abstrak: Ba0.55Sr0.45TiO3 films had been successfully deposited on the substrate of p-type Silicon (100) using Chemical Solution Deposition (CSD) and spin coating method with 3000 rpm rotation speed for 30 seconds and 1 M solubility. Thin film was annealed at temperature of 750 oC, 775 oC, 825 oC, 875 oC and 925 oC for 15 hours with rate of temperature rise 1.67 oC/minute. Optical test results showed the BST films can absorb visible light, so it can be used for non-invasive blood sugar level sensors. Analysis of the band gap energy performed using the Tauc Plot method results with the range of 2.843-3.169 eV. Electrical test results demonstrated the BST films are diodes. SEM results of BST films showed a non-homogeneous surface morphology. EDX results showed that the composition of the BST constituent is not fully in accordance with stoichiometry.
Keyword: Bogor Agricultural University (IPB), blood sugar level sensor, optical properties, electrical properties, EDX, BST

Judul: Prolapsus vagina kronis, kausa dan teknik reposisinya
Abstrak: Prolapsus vagina kronis merupakan penyembulan bagian belakang hewan, khususnya lantai vagina melalui vulva, diikuti dengan perpindahan serviks dan uterus ke belakang. Pada sapi kejadian prolapsus vagina sering pada masa 2-3 bulan akhir kebuntingan, sedangkan pada domba dan hewan sejenisnya terjadi beberapa minggu sebelum melahirkan. Kasus prolapsus vagina kadang-kadang dapat terjadi setelah melahirkan, dan jarang terjadi tanpa ada hubungannya dengan kebuntingan atau kelahiran. Penyebab prolapsus vagina kronis belum dapat dipastikan, beberapa faktor umumnya ambil bagian. Faktor uta- ma adalah tingginya kadar hormon estrogen pada akhir kebuntingan. Faktor mekanis dengan meningkatnya tekanan intra abdominal dan gaya berat dari fetus dalam kandungan. Beberapa faktor predisposisi yang dapat menunjang terjadinya prolapsus vagina adalah: perlukaan saluran kelahiran, kelahiran yang rapat, makanan yang kurang baik, terbatasnya pergerakan, faktor lingkungan dan hereditas. Prolapsus vagina kronis umumnya hampir terjadi pada semua hewan piara, lebih sering pada sapi dan domba. Pada sapi sering terjadi pada sapi potong jenis Hereford ...
Keyword: