Judul: Kemasan Aktif Penyerap Etilen Berbahan Dasar Kitosan dan KMnO4
Abstrak: Active packaging is part of the modern packaging that can change the environmental conditions of food packaging to extend the shelf life, one of the active packaging materials is potassium permanganate (KMnO4). The purpose of this study was to develop active packaging from chitosan and KMnO4, to apply active packaging in tomato storage and to analyze quality changes of the tomatoes in active packaging during storage. Film was prepared by mixing chitosan 6 g, 140 mL of acetic acid 1%, 60 mL of aquadest, 2 mL sorbitol, and KMnO4 with concentration of 3, 5, and 7 g. After 5 days storage, the film used to wrap the tomatoes was sweated. The best formulation to absorb the ethylene was F3 that made by 7 g KMnO4, since it could inhibit tomato fruit ripening process compared to other formulations. Fruits packed at room temperature had lower water content which was equal to 43,41%, furthermore the control sample water content was 52.65%, while at the refrigator temperature it was only F3 formula that had a lower water content which was 34,70%, which control was 37,44%. Fruits were packed at room temperature had a high hardness as much as 17,79 compare to the control sample value of 3,47, while the refrigerator temperature had lower hardness value of the 2,72 compare to the control sample value of 4,29. Addition of KMnO4 on the film can maintain the pH in the range of 4, both in refrigerator and room temperature. Sample F3 had a value of vitamin C higher either in room temperature of 9,38 mg and refrigerator temperature of 7,26 mg, compare to control sample or other samples. Hue value of sample and control were in the range of the yellow to red.
Keyword: tomatoes, potassium permanganate, ethylene absorbent, active packaging

Judul: Beef Tomatoes (Solanum lycopersicum) Storage with Atmospheric Modified Packaging and Ethylene Absorbent Using Potassium Permanganate
Abstrak: Tomat beef merupakan salah satu komoditas holtikultura yang mudah rusak (perishable) dan memiliki umur simpan yang relatif singkat. Untuk memperpanjang masa simpan tomat dapat dilakukan dengan cara menghambat produksi etilen dengan bahan penyerap etilen, salah satunya adalah menggunakan kalium permanganat (KMnO4) dan silika gel. Penelitian ini bertujuan mengkaji laju respirasi tomat pada penyimpanan dingin dan pengaruh penyerap etilen terhadap mutu buah tomat beef dalam kemasan film plastik. Bahan utama yang digunakan adalah tomat beef fase panen pink dengan warna merah 30-60% yang dikemas dalam wadah styrofoam dan plastik polietilen. Penyerap etilen yang digunakan adalah kalium permanganat (KMnO4) dengan konsentrasi 1000 ppm, 2500 ppm, dan kontrol. Buah disimpan pada suhu 5oC, 10oC, dan suhu ruang. Pengamatan mutu dilakukan setiap lima hari selama 30 hari meliputi laju respirasi, susut bobot, kekerasan, total padatan terlarut, warna, dan kadar air. Laju respirasi diukur dengan metode tertutup pada stoples 3300 ml dan berat sampel 700g. Hasil penelitian menunjukkan bahwa laju respirasi tomat beef dipengaruhi oleh suhu penyimpanan. Semakin tinggi suhu penyimpanan semakin tinggi laju respirasi. Laju respirasi tomat beef pada suhu 5oC, 10oC dan suhu ruang (28oC) berturut-turut 1.37 ml/kg.jam, 2.72 ml/kg.jam, dan 6.93 ml/kg.jam untuk laju produksi CO2 dan laju konsumsi O2 tomat beef berturut-turut 2.56 ml/kg.jam, 3.27 ml/kg.jam, 7.63 ml/kg.jam. Penyimpanan tomat beef pada suhu 5°C mengalami chilling injury pada hari penyimpanan ke-7, penyimpanan dengan suhu ruang 28oC hanya mampu mempertahankan mutu buah selama 19 hari karena terdapat jamur pada mahkota buah. Penyimpanan tomat beef pada suhu 10°C mampu mempertahankan mutu buah tomat hingga 22 hari. Penyimpanan tomat beef dalam kemasan atmosfer termodifikasi pada suhu 10oC dengan penambahan penyerap etilen (KMnO4 dan silika gel) menunjukkan hasil yang lebih baik dibandingkan pengemasan tanpa pemberian perlakuan dalam menghambat perubahan persentase susut bobot, perubahan warna, dan perubahan nilai total padatan terlarut buah tomat. Perbedaan konsentrasi penyerap etilen 1000 ppm, 2500 ppm, dan kontrol memberikan pengaruh nyata terhadap persentase susut bobot, perubahan warna, dan nilai total padatan terlarut buah tomat beef tetapi tidak menunjukkan pengaruh nyata terhadap nilai kekerasan dan kadar air. Secara keseluruhan penggunaan bahan penyerap etilen dengan konsentrasi 2500 ppm memberikan hasil yang lebih baik dengan persentase susut bobot sebesar 0.40%, kekerasan 1.76 kgf, perubahan warna dengan nilai L, a, dan b sebesar 52.21, 13.48, dan 18.65 dengan kadar air 94.82% dan mampu mempertahankan kesegaran buah tomat beef hingga penyimpanan hari ke-30.
Keyword: Beef tomatoes, ethylene absorbent, atmosphere modified packaging

Judul: Pengaruh Tingkat Suku Bunga SBI Terhadap Nilai Tukar Rupiah (Terhadap Dollar) Di Indonesia
Abstrak: Karakteristik Indonesia sebagai small open economy (perekonomian terbuka kecil) yang menganut sistem devisa bebas. Serta ditambah dengan beralihnya sistem nilai tukar di Indonesia dari sistem mengambang terkendali (managed floating system) menjadi sistem yang mengambang penuh (freely floating system) pada tanggal 14 Agustus 1997, menyebabkan posisi nilai tukar rupiah ditentukan oleh mekanisme pasar. Namun dengan adanya hal tersebut membuat pergerakan nilai tukar di pasar menjadi sangat rentan oleh pengaruh faktor-faktor ekonomi dan non-ekonomi.
Keyword: