Judul: Sintesis Nanokristal Magnetit Menggunakan Urea sebagai Penjerap Cr(VI)
Abstrak: The study was to synthesize and characterize magnetite nanocrystal. Magnetite powder was synthesized using hydrothermal method from FeSO4 as precursor and sodium hydroxide and urea as the base sources. Characterization of the obtained powder was carried out using X-ray diffraction, scanning electron microscope, and energy dispersive X-ray analyzer. The crystallite size of magnetite by X-ray diffraction was obtained from 18,23 to 67,34 nm. The scanning electron microscope observations showed that magnetite particles underwent agglomeration. Magnetite powder was used as Cr(VI) adsorbent. The results showed that adsorption capacity for urea-based magnetite at pH 1-5 in 2 hours were 1.92; 1.91; 1.59; 1.20; and 1.21 mg/g, respectively. Adsorption capacity for sodium hydroxide-based magnetite (pH 1-5, 2 hours) were 1.74; 1.83; 0.64; 0.69; and 0.77 mg/g. The results indicated that urea-based magnetite is able to increase adsorption capacity.
Keyword: 

Judul: Kinerja Komposit Karbon Aktif-Magnetit sebagai Adsorben Ion Cr(VI).
Abstrak: Komposit karbon aktif-magnetit merupakan adsorben yang dapat digunakan untuk menjerap ion kromium heksavalen. Penelitian ini bertujuan menyintesis komposit karbon aktif-magnetit (KA-Fe3O4), menguji kinerjanya dalam menjerap ion Cr(VI), serta menentukan model adsorpsinya. Komposit karbon aktif-magnetit disintesis dengan metode hidrotermal dan dicirikan dengan spektroskopi inframerah. Parameter uji pada penentuan kondisi optimum adsorpsi berupa konsentrasi awal, pH larutan, dan waktu kontak. Kondisi optimum adsorpsi kedua adsorben diperoleh pada konsentrasi awal 350 mg L-1, pH larutan 3, dan waktu kontak 5 jam. Kapasitas adsorpsi karbon aktif dan karbon aktif-magnetit masingmasing 3.32 dan 3.30 mg g-1. Tambahan magnetit pada komposit karbon aktifmagnetit tidak menunjukkan perbedaan yang nyata dibandingkan dengan adsorben karbon aktif. Komposit karbon aktif-magnetit mengikuti model isoterm Langmuir.
Keyword: adsorpsi, karbon aktif, komposit, kromium, magnetit

Judul: Tingkah Laku Lumba-Lumba Hidung Botol Indo-Pasifik (Tursiops aduncus) di Umah Lumba, Teluk Banyuwedang, Bali
Abstrak: Lumba-lumba Hidung Botol Indo-Pasifik (Tursiops aduncus) merupakan mamalia laut yang umum ditemukan di perairan Indonesia dan telah dikategorikan sebagai hewan hampir terancam punah oleh IUCN, salah satunya akibat tingginya tingkat eksploitasi untuk atraksi mamalia laut. Penelitian ini bertujuan mendeskripsikan tingkah laku Tursiops aduncus di Umah Lumba, Teluk Banyuwedang, Bali. Observasi visual dilakukan pada 3 individu Tursiops aduncus, yaitu Rambo, Rocky, dan Jhony yang telah direhabilitasi sejak September 2019. Ketiga individu dapat diidentifikasi melalui ciri fisik di bagian kepala dan sirip dorsal. Beberapa lumba-lumba telah mengembangkan sifat liar dengan adanya 9 jenis tingkah laku yang mendukung kehidupan di alam, yaitu bernapas, istirahat, jelajah, reproduksi, sosial, berburu, spy hopping, tail clapping, dan sneezing. Sebanyak 3 jenis tingkah laku dikategorikan sebagai tingkah laku dominan karena ditemukan pada setiap sesi waktu penelitian, yaitu bernapas, istirahat, dan jelajah. Program rehabilitasi lumba-lumba sangat penting dilakukan untuk aklimatitasi, adaptasi, dan melatih lumba-lumba bertahan hidup sebelum dilepasliarkan.
Keyword: behavior, dolphin, rehabilitation, Tursiops aduncus, Umah Lumba