Judul: Behaviour of Composite Membrane Nanopore Cellulosa Acetat-Polistirene (CA-PS) due to Surfactant and Temperature Effect.
Abstrak: Membrane can be used for separation because of its superiority such as simple, simplicity, low energy consumption, and environmentally sound product. The cellulose acetate membrane is an example of the environmentally sound product and is used widely, such as in waste water treatment installation. This is the follow-up of the previous research and focused at the modification of cellulose acetate membrane by polystyrene and cetiltrimetyl ammonium bromide (CTAB) as porogen. The experiment was started with production of cellulose acetate membrane with polystyrene and CTAB with compositions of CA:PS:CTAB of 9:1:0.5, 9:1:1, 9:1:1.5, and 9:1:2. The membranes were formed by molding the mixture into films followed by characterisation of water flux value, rejection index at pressure 20 psi, and analysis of the surface morphology of membrane by scanning electron microscope (SEM). The SEM photo showed that temperature and CTAB affected the amount and the size of pores, and membrane surface textures. Increasing water flux and decreasing rejection index were decreasing with the increasing amount of CTAB. The highest water flux value showed by membrane with CTAB 1.5 % (MCCT 3) membrane at 40 ºC temperature, that was 160.6054 (L/m2.jam). Whereas the highest rejection index was in MCCT 2 at 40 ºC temperature, 9.30 %. The SEM photo showed that MCCT 4 membrane soaked in 40 ºC had pore size of 0.25 μm (250 nm) whereas those soaked in 60 ºC temperature had pore size of 0.50 μm (500 nm). These the membranes were classified as nanofilter
Keyword: 

Judul: Pengembangan Membran Selulosa Asetat Menggunakan Natrium Dodesil Sulfat
Abstrak: Development of membrane technology is waste treatment unit is growing rapidly and widely used in separation process. Membrane technology is chosen because the process is simple, low energy use, nondestructive, and do not generate new waste, thus classified as a green good technology. The production of membrane was started by preparing polymeric mixture solution of cellulose acetate (CA) and sodium dodecyl sulfate (SDS) in acetone. Composition of CA was 15% w/v and composition of SDS were varied from 0; 0.05; 0.01; to 0.125% w/v. The solution was stirred by ultrasonic for 3 hours and casted on the glass plate surface then immersed in warm water at 60 oC. The membranes were characterized by their rejection index. Rejection index was applied to detergent solution with concentration of 1600 ppm. When compared with values below the critical micelle concentration (CMC), the best average value of rejection index was resulted at the initiation of CMC, with SDS concentration of 0.125%. At that concentration, a quite high average values was obtained for the rejection index (77%). While, at the SDS concentration below CMC, 0.05% and 0.01%, the average index rejection values were 17% and 37%, repectively. The best CMC value was reached at the initiation (0.125%).
Keyword: 

Judul: Ornithonyssus Bursa (Berlese, 1888) Famili Macronyssidae yang Menyerang Unggas Dan Penaggulangannnya
Abstrak: Ornithonyssus bursa adalah tungau penghisap darah pada unggas di daerah tropis dan subtropis. Tungau ini relatif kecil, dengan panjang tubuh antara 700-1000 mikron dan lebarnya 250-490 mikron. Tubuhnya bulat berwarna coklat kekuningan sebelum menghisap darh dan berwarna merah setelah menghisap darah dari induk semangnya.
Keyword: