Judul: Analisis Penyelenggaraan Makanan, Tingkat Kesukaan dan Sisa Konsumsi Pangan Narapidana di Lembaga Pemasyarakatan Paledang, Bogor
Abstrak: The purpose of this study was to analyze the food service, preference level and prisoner’s residual of food consumption at Paledang prison Bogor. The design of study was cross sectional, 85 sampel was collected in October 2013. The food service consist of inputs (human resources, space processing, raw materials and funds), the process (menus planning, ordering and purchasing of groceries, grocery receipted, processing, presentation and distribution, recording and reporting, sanitation and hygiene), and output (food availability). The food service at prison Paledang was not good enough and has not complied the standard. The menus of preference level of food consumption are presented belong like and neutral categorized. The residual of food consumption level ranged from 7-63%. Statistical test result showed no significant correlation between individual characteristics of the prisoners with the preference level of food consumption (p>0.05).
Keyword: residual of food consumption, food service, prisoner, prison

Judul: Keragaan Konsumsi Pangan, Aktivitas Fisik dan Status Gizi Narapidana di Lembaga Pemasyarakatan Paledang Bogor
Abstrak: The purpose of this study was to observed food consumption, physical activity and prisoners’s nutritional status at Paledang Prison Bogor. The design of study was cross sectional, 85 samples was collected in October 2013. The sampling technique was purposive, data was collected by questionnaire using an interview structured. The results showed that prisoners adequacy level of energy, protein, vitamin A, and Fe were categorized normal, whereas adequacy level of vitamin C, calcium, and phosphor were categorized deficit. Physical activity levels of prisoners were low category, prisoners nutritional status decrease since they stayed in prison. Chi-Square correlation test results showed there were no correlation between energy intake and protein with nutritional status, and time of detention with nutritional status (p>0.05), however there was negative correlation between physical activity with nutritional status (p<0.05).
Keyword: nutritional status., prisoners, food consumption, physical activity

Judul: Elektrodeposisi Film Tipis Semikonduktor Cu2ZnSnS4 (CZTS) pada Substrat Kaca ITO
Abstrak: Semiconductor Cu2ZnSnS4 (CZTS) thin film that can be used as absorber layers on solar cell module was made via electrodeposition method. CZTS thin film was electrodeposited on the surface of a silicate glass coated with a thin layer of indium tin oxide (ITO). Deposition process was done using potentiostatic mode at room temperature with a potential of 1.05 V for 30, 45, and 60 minutes, followed with annealing the film at 2 different temperatures, 500 ºC using furnace and 180 ºC using hot plate, both treatments for 45 minutes in N2/H2S atmosphere. The X-ray difractograms were analyzed using Match 2 program and showed that the CZTS thin films had kesterit crystalline structure, with a low percentage of CZTS phase. The thin film also contained secondary phases such as Cu2S, ZnS, and SnS. The obtained CZTS thin films had a thickness between 1.039 and 1.676 μm. Absorption study showed that the band gap energy of CZTS thin films which was annealed using furnace ranged from 1.50 to 1.52 eV, whereas that annealed using the hot plate was not observed. The band gap energy value showed that CZTS thin films can be used as sunlight absorber layers on solar cell. The formation of CZTS crystal film on this investigation was effectively performed using furnace annealing process at a temperature of 500 ºC with deposition time of 45 minutes.
Keyword: Thin film, Electrodeposition, Cu2ZnSnS4