Judul: Pengembangan membran selulosa asetat dengan pengadukan ultrasonik dan tambahan PLURONIC F-127
Abstrak: Membran selulosa asetat (CA) dengan PLURONIC sebagai porogen dapat digunakan untuk proses pervaporasi metanol. Membran dibuat dengan metode pembalikan fase. Larutan diaduk menggunakan pengaduk ultrasonik dengan ragam waktu pengadukan selama 10, 16, 22, dan 28 jam dan dicetak di atas pelat kaca, kemudian direndam dalam air hangat pada suhu 60 ºC. Membran dianalisis dengan beberapa parameter, seperti nilai fluks air, faktor pemisahan, dan nilai indeks pemisahan pervaporasi (PSI). Morfologi membran dianalisis dengan mikroskop elektron payaran dan spektrofotometer inframerah Fourier tertransformasi. Nilai rerata fluks air membran CA murni dan CA-PLURONIC berturut-turut pada waktu pengadukan 10 jam adalah 4.40 dan 13.33 L/m2.jam; pada 16 jam adalah 4.01 dan 13.96 L/m2.jam; pada 22 jam adalah 7.82 dan 130.69 L/m2.jam; dan pada 28 jam 3.29 dan 35.35 L/m2.jam. Membran CA dan membran CA-PLURONIC pada waktu pengadukan 10 jam mengindikasikan nilai PSI yang lebih tinggi, berturut-turut 161.30 dan 186.29. Membran CA dan membran CA-PLURONIC dengan waktu pengadukan 22 jam menunjukkan nilai PSI yang paling rendah berturut-turut 143.20 and 128.68. Oleh karena itu membran dengan waktu pengadukan 22 jam merupakan membran yang kurang baik untuk pervaporasi.
Keyword: Cellulose acetate membrane, Pluronic F-127, Methanol pervaporation, Bogor Agricultural University, Institut Pertanian Bogor, IPB

Judul: Pervaporasi Metanol Menggunakan Membran Selulosa Asetat/Polivinil Pirolidon dan Natrium Dosesil Sulfat
Abstrak: Pervaporation membrane is one of alternative methods to purify methanol. Performance of the pervaporation is affected by its characteristics. Phase inversion technique was used for preparing the membrane. The membrane was prepared by mixing polymeric solution of cellulose acetate (CA) and sodium dodecyl sulfate (SDS) as template in acetone solution. Composition of CA was 17% w/v and composition of SDS were varied 0; 0.5; 1; 1.5; dan 2% w/v. The solution was stirred by ultrasonic for 10 and 20 hours and it was casted on the glass plate surface and then submerged it into water of 60 oC. The membrane was coated by polyvinyl pyrrolidon. The performance of pervaporation was evaluated through permeation flux and separation factor and then was calculated for its pervaporation separation index (PSI) value. In this research, permeation flux and separation factor were contradicted results, but PSI was proportional to the separation factor. High permeation flux and separation factor are desired in the performance of pervaporation. The results showed that methanol concentration from pervaporation product by CA membrane with SDS 2% b/v in 20 hours stirring by ultrasonic was 79% from feed solution of 60%. Therefore, this membrane is applicable for methanol pervaporation, but it still needs some improvements.
Keyword: 

Judul: Ornithonyssus Bursa (Berlese, 1888) Famili Macronyssidae yang Menyerang Unggas Dan Penaggulangannnya
Abstrak: Ornithonyssus bursa adalah tungau penghisap darah pada unggas di daerah tropis dan subtropis. Tungau ini relatif kecil, dengan panjang tubuh antara 700-1000 mikron dan lebarnya 250-490 mikron. Tubuhnya bulat berwarna coklat kekuningan sebelum menghisap darh dan berwarna merah setelah menghisap darah dari induk semangnya.
Keyword: