Judul: Karakteristik Papan Partikel Tanpa Perekat dari Serat Sabut Kelapa dengan Perlakuan Oksidasi, Penambahan Parafin dan Waktu Kempa
Abstrak: Manufacture of binderless particleboard from coconut fiber research was done as an effort to use alternatives raw materials in timber industry which has become limited and to reduce adhesives synthetic that has pollute the environment such as urea formaldehyde (UF). Paraffin was expected to make the physical properties of particleboard better. The purpose of this research was to know the characteristics of binderless particleboard from coconut fiber based on particleboard standard JIS A 5908:2003 and determine the influence of oxidation treatment, additional paraffin and time of pressing on the characteristics of particleboard. Oxidation method was done by spraying hydrogen peroxide (15%) and ferrosulfate (7.5%), 10 minutes of pressing and 20 minutes at temperature 180 ºC with a pressure of 25 kgf/cm2. The results: density (0.44-0.56 g/cm3), moisture content (5.94-10.08%), all treatment met the standards. The results of strong hold spanner (19-80 kgf): only combination of oxidation treatment that met the standards. The result of thickness swelling: only combination of oxidation treatment, paraffin 0.5% and without paraffin with 20 minutes of pressing (8% and 12%) met the standards. In conclusion for all the treatment, the one that didn’t meet JIS standard: Internal Bond (IB), Modulus of Elasticity (MOE) and Modulus of Rupture (MOR).
Keyword: pressing time, particleboard, paraffin, oxidation, JIS A5908:2003, coconut fiber

Judul: Eco-Friendly Particle Board from Coco Fiber with Starch-Based Adhesives
Abstrak: Serat sabut kelapa merupakan serat alami yang memiliki potensi untuk dimanfaatkan sebagai bahan baku pembuatan papan partikel, karena mengandung lignoselulosa dan memiliki sifat ramah lingkungan. Penggunaan perekat maltodekstrin dengan asam sitrat sebagai perekat ramah lingkungan cukup baik dalam mengikat serat kayu sehingga pada penelitian ini mencoba menggunakan maltodekstrin-asam sitrat. Penelitian ini bertujuan untuk mengetahui ukuran partikel yang optimum untuk menghasilkan produk papan partikel. Penelitian ini menggunakan ukuran partikel sebesar 40-50 mesh, 50-60 mesh, dan lolos 60 mesh. Sifat fisis yang diuji dalam penelitian ini antara lain kerapatan, kadar air, daya serap air dan pengembangan tebal. Sifat mekanis yang diuji yaitu Modulus of Elasticity (MOE) dan Modulus of Rupture (MOR). Hasil penelitian menunjukkan ukuran partikel ukuran partikel tidak memberikan pengaruh yang nyata pada kerapatan, kadar air, daya serap air, pengembangan tebal, MOE dan MOR. Nilai sifat fisis yang diuji telah mencapai standar JIS A 5908-2003. Ukuran partikel optimum seratsabut kelapa untuk menghasilkan papan partikel cukup baik yaitu lolos 60 mesh., Coconut fiber is a natural fiber that has the potential to be used as a raw material for making particleboard, because it contains lignocellulose and has environmentally friendly properties. The use of maltodextrin adhesive with citric acid as an environmentally friendly adhesive is quite good in binding woodfibers, so in this study we tried to use maltodextrin-citric acid. This study aims to determine the optimum particle size to produce particleboard products. This study used a particle size of 40-50 mesh, 50-60 mesh, and passed 60 mesh. The physical properties tested in this study include density, moisture content, water absorption and thickness expansion. The mechanical properties tested were the Modulus of Elasticity and the Modulus of Rupture. The results showed that the particle size didn’t have a significant effect on density, moisture content, water absorption, thickness swelling, MOE and MOR. The value of the tested physical properties has reached the JIS A 5908-2003 standard.The optimum particle size of coco fiber to produce particleboard is quite good, which is passed 60 mesh.
Keyword: Coco fiber, Mechanical properties, Particle board, Particle size, Physical properties

Judul: Culicoides spp (Diptera : Ceratopogonidae) Sebagai Vektor Beberapa Penyakit Pada Hewan
Abstrak: Culicoides spp (Diptera : Ceratopogonidae) sebagai Vektor beberapa penyaki t pada Helvan. Culicoides spp (biting midges = Agas) ordo diptera, famili Ceratoponidae, merup3.ka.nlalat kecil (panjang 1,5 - 5 mm) yang berwarna coklat atau hitam, yang biasanya menghisap darah hewan/manusia dan bangsa unggas, yang lebih membedakan lalat ini dengan lalat lainnya karena mempunyai bercak-bercak pada sayapnya serta mempunyai kerangka sayap yane; melintang (cross-vein) yaitu: r - m. Lalat ini biasanya menyerang induk semangnya secara bergerombol dan lebih menyukai hewan yang berada diluar kandang, daerah yang disenanginya biasanya daerah tengkuk dan daerah bawah kaki.
Keyword: