Judul: Analisis Keragaman Genetik Ikan Baung (Hemibagrus nemurus) dengan Menggunakan Teknik PCR-RFLP pada DNA Mitokondria
Abstrak: This research has an objective to analyze the genetic variation among four Hemibagrus nemurus population by using PCR-RFLP of D-loop region of mitochondrial DNA. H. nemurus were collected from Cirata, Serayu, Jambi and Bogor. Four restriction enzymes were used to digest D-loop region mt-DNA, i.e. MboI, HaeIII, AluI and RsaI. Based on this analysis, these four population have seven composite haplotypes. The highest haplotype diversity was found at the population from Jambi. Population from Serayu has just one composite haplotype indicating that this population has the same ancestor. Population from Cirata and from Bogor has the same composite haplotype indicating that there was probably migration between these two populations.
Keyword: 

Judul: Analisis keragaman genetik labi-labi, dogania Subpkma (Testudines: trionychidae), melalui teknik PCR-RFLP
Abstrak: Saat ini telah terjadi penurunan populasi labi-labi yang sebagian besar diakibatkan adanya perburuan liar dan kerusakan lingkungan. Melihat hal itu diperlukan suatu langkah untuk mengumpulkan berbagai informasi biologi labi-labi. Salah satu caranya adalah dengan melakukan anal isis molekular sebelum berbagai informasi lainnya diungkapkan. Penanda molekular genetik yang sering digunakan dalam analisis molekular adalah daerah pengendali (d-loop) genom mitokondria menggunakan teknik PCR-RFLP. Bagian yang paling stabil dari daerah pengendali mtDNA diamplifikasi secara in vitro dengan pasangan primer 577 dan 578. Produk PCR dipotong dengan lima macam enzim restriksi, yaitu Alu I, Hsp92 II, Hha I, Hpa II dan Rsa I yang menghasilkan tujuh haplotipe. Keragaman nukleotida antara haplotipe yang ditemukan di Jawa dan Sumatera (interlokasi) adalah 12.11 %. Angka itu jauh lebih besar dibanding keragaman nukleotida antar haplotipe di dalam Sumatera maupun Jawa (intralokasi) yang berturut-turut adalah 6.5% dan 3%.
Keyword: 

Judul: Pembuatan Film Tipis Cu2ZnSnS4 sebagai Lapisan Penyerap Cahaya pada Sel Surya Menggunakan Metode Elektrodeposisi
Abstrak: Thin film of Cu2ZnSnS4 (CZTS) is an alternative semiconductor used as light absorber layer on solar cell. CZTS can replace silicon that commonly used as commercial semiconductor. The advantage of using CZTS as absorber layer is due to the abundance of its chemical composer on earth, and its high value of absorption coefficient. The absorber layer was made by using electrodeposition method on ITO glass substrates. The films were deposited at room temperature using potentiostatic mode with a potential of –1.05 V for 30, 45, and 60 minutes. After that, the films were annealed at two different temperatures, 180 ºC and 500 °C, for 45 minutes in N2/H2S atmosphere. Based on X-ray diffraction analysis, the polycrystalline thin film obtained fall into kesterite crystal phase. This type of crystal was obtained when the CZTS was annealed at 500 °C in H2S/N2 atmosphere. The value of optical band gap energy for the CZTS thin film was 2.2 eV with the film thickness about 1.228–6.366 μm. The sample of CZTS with electrodeposition time of 45 minutes and annealing temperature of 500 °C showed the best result and in conformity with absorber layers criteria for solar cells.
Keyword: semiconductor, ITO glass, CZTS thin film, electrodeposition