Judul: Dimensional Stability of Surian (Toona sinensis Roem.)  Wood from West Sumatera
Abstrak: One of the important factors that must be understood in order to use wood properly is its dimensional stability. The objective of this study was to examine radial variation in dimensional stability of surian (Toona sinensis Roem.) wood from West Sumatra. Dimensional stability indicators used are the T/R-ratio and level of dimensional change (LDC) from wet to air-dried condition which are measured by using standard methods. The results showed that dimensional stability of surian wood was very good with an average T/R-ratio 1,29 and a LDC of 0,27 (0,19‒0,34) cm for every 1% reduction in wood moisture. T/R-ratio as well as a total of LDCare not influenced by sample location in the stem, while LDC for each direction is significantly influenced. In general, heartwood are more stable than sapwood and transition. Results also showed that average wood density of this surian wood was 0,81 g/cm3, air-dried specific gravity was 0,50, and the FSP was 36,16%. The wood belongs to Strength Class III. The recommended utilization for this wood is as a substitute and/or complement for teakwood for the high-quality wooden furniture and fancy veneer industries., Salah satu faktor penting yang harus diketahui dalam rangka pemanfaatan kayu secara tepat guna adalah stabilitas dimensinya. Penelitian ini bertujuan untuk mengkaji variasi radial stabilitas dimensi kayu surian (Toona sinensis Roem.) asal Sumatera Barat. Indikator stabilitas dimensi yang digunakan adalah T/R-rasio dan tingkat perubahan dimensi (TPD) dari kondisi basah ke kondisi kering udara yang dihitung dengan menggunakan metode standar. Hasil penelitian menunjukkan stabilitas dimensi kayu surian tergolong tinggi dengan rata-rata T/R-rasio 1,29 dan TPDnya 0,27 (0,19‒0,34) cm untuk setiap 1% perubahan kadar air kayu. T/R-rasio dan TPD total tidak dipengaruhi oleh lokasi sampel uji dalam batang, sedangkan TPD masing-masing arah dipengaruhi. Secara keseluruhan, bagian teras lebih stabil dibandingkan bagian gubal maupun peralihan. Hasil penelitian juga menunjukkan rata-rata kerapatan kayu surian yang diteliti adalah 0,81 g/cm3, BJ kayu kondisi kering udara 0,50, dan KA-TJSnya 36,16%. Kayu masuk Kelas Kuat III. Potensi pemanfaatan yang disarankan adalah sebagai pengganti dan/atau pelengkap kayu jati untuk industri wooden furniture dan finir bermutu tinggi.
Keyword: dimensional stability, LDC, surian, T/R-ratio, wooden furniture

Judul: Beberapa Sifat Dasar Kayu Surian (Toona sinensis) asal Kabupaten Indramayu, Jawa Barat
Abstrak: Banyak upaya yang telah dilakukan untuk mengatasi permasalahan terkait dengan kelangkaan kayu sebagai bahan baku industri. Salah satunya adalah dengan membangun dan mengembangkan hutan tanaman termasuk hutan rakyat. Diperkirakan pasokan kayu di masa datang akan terus dipenuhi oleh jenis-jenis kayu dari hutan rakyat. Penelitian ini bertujuan untuk mempelajari sifat fisis dan mekanis kayu surian (Toona sinensis), yang terdiri dari kadar air, kerapatan dan berat jenis (BJ) kayu, modulus of rupture (MOR), modulus of elasticity (MOE), keteguhan tekan sejajar serat (σtk//) dan kekerasan sisinya. Pengujian sifat fisis mengacu kepada ASTM D1762, sedangkan pengujian sifat mekanis mengaju kepada ASTM D143. Bahan utama adalah bagian teras kayu surian (T. sinensis) dari tiga pohon yang berasal dari Kabupaten Indramayu, Jawa Barat. Diameter, umur pohon dan perlakuan silvikulturnya tidak diketahui. Data dianalisis menggunakan rancangan acak lengkap satu faktor (bagian batang) menggunakan software SPSS 13.0 dengan enam ulangan. Hasil penelitian sifat fisis kayu menunjukkan bahwa rata-rata nilai KA, kerapatan dan BJ berturut-turut adalah 14,85%, 0,61 g/cm3, dan 0,52. KA tertinggi (16,37%) terdapat di bagian ujung, sedangkan BJ dan kerapatan yang tertinggi (berturut-turut 0,55 dan 0,64 g/cm3) terdapat di bagian tengah batang. KA terendah (12,69%) terdapat di bagian tengah batang, BJ terendah (0,49) di bagian pangkal batang, sedangkan kerapatan terendah (0,57 g/cm3) terdapat di ujung batang. Hasil penelitian sifat mekanis kayu menunjukkan bahwa rata-rata nilai MOE, MOR, keteguhan tekan sejajar serat (σtk//) dan kekerasan sisi berturut-turut adalah 203.091,10 kg/cm2, 694,10 kg/cm2, 368,94 kg/cm2, 519,05 kg/cm2 (tangensial) dan 432,16 kg/cm2 (radial). MOE serta kekerasan sisi tangensial dan radial yang tertinggi (masing-masing 226.062,97 kg/cm2, 535,67 kg/cm2 dan 518 kg/cm2) terdapat di bagian tengah batang. MOR tertinggi (721,95 kg/cm2) terdapat di bagian pangkal, sedangkan σtk// tertinggi (377,15 kg/cm2) di bagian ujung batang. MOE dan σtk// yang terendah terdapat di bagian pangkal (masing-masing 189.014,93 kg/cm2 dan 359,30 kg/cm2), sedangkan MOR, kekerasan sisi tangensial dan radial yang terendah (masing-masing 638,55 kg/cm2, 486,17 kg/cm2 dan 400,00 kg/cm2), terdapat di bagian ujung batang. Analisis sidik ragam menunjukkan bahwa bagian batang hanya berpengaruh terhadap KA dan kerapatan kayu, sedangkan BJ, MOE, MOR, σtk// dan kekerasan sisi (tangensial dan radial) kayunya tidak. Berdasarkan nilai-nilai BJ, MOE dan MOR, maka kayu surian yang diteliti masuk ke dalam Kelas Kuat III sehingga cocok digunakan sebagai bahan bangunan beban sedang. Dengan nilai MOE yang lebih tinggi dan kekerasan sisi yang relatif sama, secara umum kayu surian dapat menggantikan sebagian peranan kayu jati.
Keyword: 

Judul: Enteric Collibacillosis Pada Anak Babi Baru Lahir: Patogenesa dan Perubahan-Perubahan Patologisnya
Abstrak: Diare disebabkan oleh infeksi bakteri Escherichia coli pada anak-anak babi baru lahir yang peka terhadap en terotoksin produk bakteri tersebut. Dikenal sebagai colibacillosis. Patogenesa dari colibacillosis anak babi baru lahir adalah (1) infeksi oleh E. coli patogen, (2) proliferasi E. coli di lumen usus halus, (3) produksi dan pelepasan enterotoksin, dan (4) aktifitas toksin pada usus halus. Dalam proses proliferasi, adanya antigen pili K88 sangat penting karena memungkinkan bakteri perlekatan dengan epitel mucosa usus halus. mengadakan Setelah ko lonisasi dan proliferasi segera toksin dilepaskan. Akti- fitas toksin menginduksi sekresi yang berlebihan dari u- sus sehingga banyak cairan yang dikeluarkan ke lumen usus. Hal ini mengakibatkan banyak cairan dan elektrolit hilang sehingga timbul diare, dehidrasi dan asidosis yang sering menyebabkan kematian. Perubahan-perubahan patologis yang umum adalah dis tensi usus halus, dilatasi lambung dan infark pada kurva- tura mayor. Perubahan-perubahan histologis yang terjadi adalah enteritis hemorrhagica acuta, oedem dan kongesti pembuluh darah di lamina propria, akumulassi leukosit inti polimorf, sel monosit, dan inti sel mengalami piknosis Thrombus pada vena dan degenerasi serta desquamasi sel epitel usus….
Keyword: