Judul: Characterizations of low alloy steel sae 4422  plated with chromic acid (Cro3)
Abstrak: Characterizations of low alloy steel SAE 4422 plated with chromic acid (CrOrO3) was use Optical Microscopy (OM), Scanning Electron Microscopy (SEM), X-Ray Diffraction (XRD), RD),Energy Dispersive Analysis of X-Ray (EDAX), Hardness Test and Roughness Test. Microstructures analysis exhibits cracks and grain boundaries microcracks as a characteristics of chrome metal found at plating metal. Perlite and Ferrite as grains of steel found at base metal with grain boundaries around it. Phase analysis of plating metal appropriate to chrome metal with lattice constant (a) is 2.559 Å and phase analysis of base metal appropriate to iron ferrite with lattice constant (a) is 3.318 Å. Both plating and base metal have cubic system. Chemical analysis of plating metal at surface section exhibits that cracks area have highest value of carbon element compare with grains and grains boundaries area. While chemical analysis of base metal at cross section exhibits that perlite have highest value of carbon element compare with ferrite and grain boundaries. The hardness value of plating metal at surface section and cross section are 753 and 637 VHN. While, the hardness value of base metal and interface area at cross section are 205 and 373 VHN. The roughness value at measurement points of chrome surface for as received sample are 0.445 μm. Observation used Optical Microscopy and Scanning Electron Microscopy exhibits surface irregularities combine to form surface texture of plating metal at surface section.
Keyword: 

Judul: Modifikasi Pelapisan Seng pada Baja dengan Chromating Trivalent menggunakan Bahan Organik Pereduksi
Abstrak: Baja merupakan logam yang banyak digunakan dalam industri perakitan dan konstruksi. Pelapisan seng pada baja diperlukan untuk memenuhi sifat fisik tahan korosi dan ketebalan yang sesuai kebutuhan industri. Perlakuan chromating pada proses pelapisan yang menggunakan kromium heksavalen dapat bersifat toksik sehingga harus direduksi menjadi kromium trivalen menggunakan bahan organik pereduksi. Penelitian ini bertujuan mengetahui pengaruh konsentrasi dan waktu pencelupan pada tahapan chromating terhadap laju korosi dan ketebalan lapisan seng pada baja. Penelitian dilakukan dalam larutan kromium dengan variasi konsentrasi 5; 10; 15 mL/L serta variasi waktu 10 dan 60 detik. Larutan kromium dibuat dari beberapa jenis sumber kromium yang berbeda, yaitu H2CrO4, Na2CrO4, K2Cr2O7. Ketebalan baja diukur dengan mikrometer sekrup digital dan pengukuran laju korosi menggunakan metode kehilangan berat. Hasil modifikasi terbaik ditunjukkan oleh spesimen yang dicelupkan pada larutan kromium trivalen 15 mL/L dari K2Cr2O7 dengan waktu 60 detik. Ketebalan yang dihasilkan adalah 0,0025 mm dengan laju korosi 0,0063 mm/tahun., Steel is a metal that is widely used in the manufacturing and construction industries. Zinc coating on steel is required to fulfill the physical properties of corrosion resistance and thickness suitable for industrial needs. The chromating treatment in the coating process using hexavalent chromium can be toxic, therefore it must be reduced to trivalent chromium by using reducing organic matter to avoid the negative impact. This study aims to determine the effect of concentration and immersion time in the chromating stage on the corrosion rate and the thickness of the zinc layer on the steel. This research was conducted in a chromium solution with concentration variation of 5; 10; 15 mL/L and time variations of 10 and 60 seconds. There are several chromium sources that used in this research, i.e H2CrO4, Na2CrO4, and K2Cr2O7. Thickness was measured with a digital screw micrometer and corrosion rate was measured using the weight loss method. The best modification results were shown by a specimen that was dipped in a 15 mL/L trivalent chromium solution of K2Cr2O7 for a time of 60 seconds. The resulting thickness is 0,0025 mm with a corrosion rate of 0,0063 mm/year.
Keyword: chromating, corrosion, steel, trivalent chrome, zinc plating

Judul: Inseminasi buatan pada primata non manusia
Abstrak: Inseminasi buatan pada primata merupakan salah satu cara untuk meningkatkan populasi primata, agar hewan tersebut dapat dicegah kepunahannya, selain itu untuk kepen- tingan biomedis pada kedokteran manusia. Pubertas pada monyet betina terjadi kira-kira pada umur 2 sampai 4 tahun, sedangkan pada kera kira-kira pada umur 2 sampai 8 tahun. Menstruasi pertama terjadi pada umur 2,5 sampai 4 tahun pada monyet dan 9 tahun pada kera. Lamanya siklus menstruasi berkisar antara 28 sampai 35 hari dengan waktu ovulasinya terjadi kira-kira pada per- tengahan siklus menstruasi yaitu antara hari ke 11 sampai ke 15, pada saat inilah waktu yang tepat untuk melakukan. inseminasi buatan. Tehnik yang paling efisien dalam pengumpulan semen adalah dengan cara elektroejakulator, sedangkan metode. inseminasi dapat dilakukan secara intravaginal, intrasertival, intrauterin dan intraperitoneal. Inseminasi buatan dengan semen beku sudah berkembang di negara-negara maju, karena semen monyet yang kaya akan sperma dapat diencerkan dan dibekukan secara bertahap.
Keyword: