Judul: Pembuatan Film Litium Niobat (LiNbO3) Didadah Variasi Konsentrasi Cerium Oksida (CeO2) Melalui Metode CSD
Abstrak: Pembuatan film litium niobat (LiNbO3) telah berhasil dilakukan di atas substrat Si (100) tipe-p dengan metode chemical solution deposition (CSD) dan variasi pendadah CeO2 0%, 2%, 4%, 6% dan konsentrasi larutan perkusor 1M. Pembauatan film ini menggunakan teknik spin coating dengan kecepetan putar 8000 rpm. Film yang sudah jadi di annealing dengan suhu 850 °C dan ditahan selama 8 jam dengan kenaikan 1.67 °C/menit. Energi bandgap film LiNbO3 yang dihasilkan sebesar 3.56 eV sampai 4.14 eV dengan indeks bias 2.21413661 sampai 2.2141669. Karakterisasi menggunakan XRD diperoleh struktur kristal berbentuk heksagonal dengan nilai parameter kisi a sebesar 5.05 Å sampai 5.67 Å dan c sebesar 13.18 Å sampai 15.80 Å. Dari hasil analisa perangkat lunak Mineral Analysis Using Diffraction (MAUD) didapatkan nilai kecocokan Sigma sebesar 1.91% sampai 20.04% dan nilai kecocokan Rexp sebesar 4.62 % sampai 16.92%.
Keyword: energi bandgap, LiNbO3, CeO2, CSD

Judul: Sintesis dan Karakterisasi Film Tipis Litium Niobat (LiNbO3) Didadah Galium Oksida (Ga2O3)
Abstrak: Film LiNbO3 dengan beberapa persentase pendadah Ga2O3 (0%, 2%, 4%, 6%) berhasil dibuat menggunakan metode Chemical Solution Deposition (CSD). Selain itu, pembuatan film LiNbO3 menggunakan teknik spin coating dengan kecepatan putar 8000 rpm telah berhasil dibuat di atas substrat silikon (100) tipe-p. Suhu yang digunakan pada saat proses annealing sebesar 850oC dan ditahan selama 8 jam dengan kelajuan suhu sebesar 1,67oC/menit, lalu mengikuti proses pendinginan hingga suhu kamar selama 13 jam. Film LiNbO3 yang didadah Ga2O3 (0%,2%,4%,6%) menghasilkan energi bandgap berkisar antara 3,6554 eV sampai 3,7232 eV. Hasil parameter kisi a dan c yang didapatkan pada karakterisasi XRD sebesar 5,411Ǻ; 5,248Ǻ; 5,190Ǻ; 5,084Ǻ dan 14,745Ǻ; 14,348Ǻ; 14,069Ǻ; 13,464Ǻ. Hasil analisis menggunakan perangkat lunak MAUD dan data literatur mendapatkan parameter kisi a dan c sebesar 5,091Ǻ; 5,192Ǻ; 5,163Ǻ; 5,057Ǻ dan 14,274Ǻ; 14,204Ǻ; 13,880Ǻ; 13,487Ǻ. Analisis hasil menggunakan perangkat lunak MAUD dapat diperoleh visualisasi struktur kristal heksagonal pada film LiNbO3., LiNbO3 film with some percentage of Ga2O3 concentration (0%, 2%, 4%, 6%) has been successfully made using the CSD method. In addition, the manufacture of LiNbO3 films using the spin coating technique with a rotational speed of 8000 rpm has been successfully made above 100 p-type silicon substrate. The temperature used during the annealing process is 850C and holds for 8 hours with a temperature speed of 1.67C /minute, then follows the cooling process to room temperature for 13 hours. The LiNbO3 film doped Ga2O3 variation concentration (0%, 2%, 4%, 6%) had a bandgap energy value ranging from 3,6554 eV sampai 3,7232 eV. The results of the lattice parameters a and c obtained based on XRD characterization are 5,411Ǻ; 5,248Ǻ; 5,190Ǻ; 5,084Ǻ dan 14,745Ǻ; 14,348Ǻ; 14,069Ǻ; 13,464Ǻ. The results of the analysis using MAUD software and data literature get lattice parameters a and c of 5,091Ǻ; 5,192Ǻ; 5,163Ǻ; 5,057Ǻ and 14,274Ǻ; 14,204Ǻ; 13,880Ǻ; 13,487Ǻ. In addition the results of the analysis using MAUD software can know the crystal structure hexagonal visualization on the LiNbO3 film.
Keyword: Chemical Solution Deposition, Ga2O3, LiNbO3

Judul: Staphylococcosis Pada Unggas dan Masalah Penanggulangannya
Abstrak: Staphylococcosis pada unggas disebabkan oleh bakteri Staphylococcus aureus (S. aureus). Secara normal kuman tersebut terdapat dimana-mana seperti di selaput lendir manusia dan hewan, kulit, kaki, paruh, udara, mesin penetas dan kandang-kandang unggas. Pada keadaan tertentu jika populasinya menjadi tinggi di dalam tubuh hewan dapat menimbulkan penyakit (Hoofstad et al., 1972; Poernomo, 1978 dalam Achdijati, 1983) yang cukup merugikan terlihat dari angka kematian unggas yang terinfeksi. S Infeksi S. aureus pada unggas dapat bersifat akut dan menahun. Pada kasus yang akut biasanya terdapat kea- daan septikemia dan kematian unggas yang cepat. Sedang- kan kasus yang menahun atau sub akut dijumpai pada keadaan synovitis, dermatitis, arthritis, spondylitis, sternal bursitis dan abses di bawah kulit (Gordon, 1977). ...
Keyword: