Judul: Sintesis ZnO dengan Tambahan Surfaktan Kationik dan Anionik Menggunakan Metode Hidrotermal
Abstrak: ZnO is a semiconductor material that has been widely used in various applications, such as solar cell. This study aimed to synthesis ZnO with ZnSO4 and KOH using hydrothermal method and evaluate the effect of surfactants on the synthesis process. First, ZnO was synthesized with various concentrations of ZnSO4:KOH (1:2, 1:3, 1:4 and 1:5). The best result was chosen by X-ray diffraction analysis. Synthesis of ZnO with the best ratio was carried out again with the addition of cationic surfactant, cetyltrimethylammonium bromide (CTAB), and anionic surfactant, sodium dodecyl sulphate (SDS). Based on the diffractograms, the best ratio was 1:2 with 86.29% crystallinity. This ratio was chosen due to the high crystallinity and the least impurities. Synthesis with the addition of CTAB and SDS gave higher crystallinity, 88.76% and 89.13%, respectively. Based on calculation using Scherrer’s equation, it showed that the addition of CTAB resulted the smallest crystal size. Based on those data, it can be concluded that surfactants have improved the characteristics ZnO by increasing the crystalinity and reducing the crystal size.
Keyword: 

Judul: Sintesis dan Karakterisasi Nanopartikel ZnO dengan Variasi Suhu Kalsinasi dan Penambahan Surfaktan menggunakan Metode Kopresipitasi Kimia
Abstrak: ZnO merupakan oksida logam yang memiliki karakteristik yang menarik dengan energi celah pita yang lebar. Penelitian ini bertujuan menyintesis ZnO dengan metode kopresipitasi dan mengkarakterisasi menggunakan berbagai instrumentasi. Perlakuan variasi suhu kalsinasi dilakukan agar dihasilkan partikel dengan ukuran dan tingkat kristalinitas yang baik. Penambahan surfaktan polivinil pirolidon (PVP) pada saat sintesis ZnO bertujuan mencegah terjadinya aglomerasi. Karakterisasi ZnO menggunakan spektroskopi ultraviolet-tampak (UV-Vis), difraksi sinar-X (XRD), spektroskopi inframerah transformasi fourier (FTIR), dan mikroskop elektron pemayaran (SEM). Hasil penelitian menunjukkan bahwa nilai celah pita ZnO meningkat seiring dengan kenaikan suhu. ZnO yang disintesis pada suhu kalsinasi 800 °C memiliki struktur wurtzit heksagonal. Ukuran kristal ZnO adalah 45,64 nm, sedangkan ZnO-PVP sebesar 40,37 nm. Tingkat kristalinitas ZnO terbaik adalah 61,34%. Spektrum FTIR menunjukkan serapan ZnO pada daerah sidik jari. Mikrograf SEM memperlihatkan bahwa ZnO tanpa penambahan PVP mengalami aglomerasi. ZnO hasil sintesis menunjukkan aktivitas antibakteri dengan terbentuknya zona hambat., ZnO is a metal oxide that has special characteristics with a wide band gap energy. This study aims to synthesize ZnO by coprecipitation method and to characterize it using various instrumentation techniques. The calcination temperature variation treatment was carried out in order to produce particles with good size and crystallinity level. The addition of polyvinyl pyrrolidone (PVP) surfactant during the synthesis of ZnO aims to prevent agglomeration. ZnO characterization used visible- ultraviolet spectroscopy (UV-Vis), X-ray diffraction (XRD), Fourier transform spectroscopy (FTIR), and scanning electron microscopy (SEM). The result showed that the value of the ZnO band gap increased with increasing temperature. ZnO synthesized at a calcination temperature of 800 °C has a hexagonal wurtzite structure. The crystal size of ZnO is 45,64 nm, while that of ZnO-PVP is 40,37 nm. The best ZnO crystallinity level is 61,34%. The FTIR spectrum shows ZnO absorption in the fingerprint region. SEM micrographs showed that ZnO without the addition of PVP agglomerated. The synthesized ZnO has antibacterial activity which is indicated by the formation of an inhibition zone.
Keyword: antibacterial, coprecipitation, polyvinyl pyrrolidone, temperature, ZnO

Judul: Characteristics and Nest Distribution of Red-breasted Parakeet (Psittacula alexandri) and Long-tailed Parakeet (Belocercus longicaudus) at the IPB Darmaga Campus
Abstrak: Betet biasa dan betet ekor-panjang merupakan dua spesies burung paruh bengkok yang terancam punah. Penelitian ini bertujuan untuk mengidentifikasi karakteristik tempat bersarang dan memetakan persebaran pohon sarang kedua jenis betet yang berada di Kampus IPB Darmaga. Tempat bersarang betet dicari dengan menggunakan metode eksplorasi dan metode wawancara, sedangkan pola persebaran pohon sarang betet dianalisis dengan menggunakan metode Nearest Neighbour Statistic (R). Hasil penelitian menunjukkan bahwa kedua jenis betet yang berada di Kampus IPB Darmaga bersarang pada lima jenis pohon. Kedua jenis betet cenderung lebih memilih bersarang pada pohon yang memiliki tajuk dominan dengan bentuk tajuk rounded dan bentuk percabangan vertical atau tortuous. Pohon yang digunakan sebagai tempat bersarang oleh kedua jenis betet merupakan pohon tidak sehat dengan berat jenis kayu yang rendah. Lubang sarang betet ditemukan pada cabang pohon yang memiliki dimensi tinggi dan besar. Pola persebaran pohon sarang kedua jenis betet cenderung berkelompok.
Keyword: Belocercus longicaudus, nest-characteristics, Psittacula alexandri