Judul: Studi tingkah laku seksual pasangan Macaca nemestrina dan Macaca fascicularis dewasa di Pusat studi satwa Primata LP-IPB, Bogor
Abstrak: Penelitian ini dilakukan berdasarkan adanya suatu pemikiran untuk menangkarkan dua spesies Macaca berbeda ke dalam satu areal yang sama dengan pertimbangan efisiensi lahan dan harapan untuk memperoleh hewan model biomedis baru yang lebih baik. Tujuan penelitian adalah untuk mengetahui tingkah laku seksual pasangan M. nemestrina dan M. fascicularis dewasa yang ditempatkan dalam kandang dengan luasan terbatas serta untuk mendapatkan informasi keturunan silangnya.
Keyword: Pigtail monkey, Macaca nemestrina, Macaca fascicularis

Judul: Perilaku seksual monyet ekor panjang (Macaca fascicularis) di Bumi Perkemahan Pramuka Cibubur, Jakarta
Abstrak: Sexual behavior is one of interaction between adult or subadult male and female that has significant role in maintaining group existency. Long-tailed macaques live in multi male multi fe~nale group, polygamous, and has no breeding season. Sosial behavior influenced by sosial hierarchy. Sexual behavior consists of mounting, intromission, thrusting, ejaculation, and dismounting. The objective of this study was to assess sexual behavior of long-tailed macaque (M. fasciszrlaris) in Bumi Perkemahan Pramuka Cihubur, Jakarta. The observation was carried out using ad libitum sampling and focal animal sampling. Daily activities were observed between 06.00 a.m. and 06.00 p.m. for 80 days (329 hour 17 minutes). Sexual activity occured in 2.33 % of total daily activity, and slowed higher frequency in the morning (06.00-10.00 a.m.) than other period of time: afternoon (10.00 a.m.-02.00 p.m.) and evening (02.00-06.00 p.m.). Sexual activity was identified has higher frequency on the ground than other places. The average duration of copulatory was 4.19 second. The high rank male did a lot of copulation, and genital inspect. Mostly, copulation occured without genital inspect. Male and female monkeys are more likely to take a rest after copulation.
Keyword: 

Judul: Pembuatan Film Tipis Cu2ZnSnS4 sebagai Lapisan Penyerap Cahaya pada Sel Surya Menggunakan Metode Elektrodeposisi
Abstrak: Thin film of Cu2ZnSnS4 (CZTS) is an alternative semiconductor used as light absorber layer on solar cell. CZTS can replace silicon that commonly used as commercial semiconductor. The advantage of using CZTS as absorber layer is due to the abundance of its chemical composer on earth, and its high value of absorption coefficient. The absorber layer was made by using electrodeposition method on ITO glass substrates. The films were deposited at room temperature using potentiostatic mode with a potential of –1.05 V for 30, 45, and 60 minutes. After that, the films were annealed at two different temperatures, 180 ºC and 500 °C, for 45 minutes in N2/H2S atmosphere. Based on X-ray diffraction analysis, the polycrystalline thin film obtained fall into kesterite crystal phase. This type of crystal was obtained when the CZTS was annealed at 500 °C in H2S/N2 atmosphere. The value of optical band gap energy for the CZTS thin film was 2.2 eV with the film thickness about 1.228–6.366 μm. The sample of CZTS with electrodeposition time of 45 minutes and annealing temperature of 500 °C showed the best result and in conformity with absorber layers criteria for solar cells.
Keyword: semiconductor, ITO glass, CZTS thin film, electrodeposition