Judul: Preparation of CMC from Pineapple (Ananas comosus-Smooth Cayenne Cultivar) Peel and Its application as Edible Bio-plastics
Abstrak: Pineapple (Ananas comosus–Smooth cayenne cultivar) peel is agricultural waste that rich in cellulose. There is many way to utilize this waste to become more valuable product such as cellulose or its derivative. The objectives of this research are to prepare CMC from pineapple peel (CMCpp) and use the obtained CMC as edible film material. The CMCpp obtained from reacting the extracted cellulose from dried pineapple peel with monochloroacetic acid. The CMCpp has been successfully synthesized with degree of substitution (DS) of 1.040±0.104 for bleached CMC and of 0.601±0.087 for unbleached CMCpp, and the water solubility of bleached CMCpp and unbleached CMC were 76.92% and 33.93%, respectively. The CMCpp had lower solubility than commercial CMC (CMCc) which can be dissolved in water 100% (DS of CMC =1.0). The color measurement showed that the bleached CMC (L*=87.37; a*=-0.71; b*=8.19) was nearly met with the color of CMC (L*=89.57; a*=-0.91; b*=6.86) but brighter than unbleached CMCpp (L*=70.03; a*=4.07; b*=18.90). The effects of plasticizer (glycerol and sorbitol with concentration 10%; 20%; and 30% [w/w of CMC]) on the films properties were also investigated. The results showed that increasing the concentration of plasticizer decreased the tensile strength but increased %elongation of CMC films. The films with glycerol as plasticizer showed lower tensile strength than films with sorbitol as plasticizer. Adding glycerol and sorbitol did not give significant effect to the water solubility index but increased water vapor transmission rate (WVTR) of films. FT-IR spectra showed that the functional groups of each film with and without plasticizer are not significantly different. The results indicated that the film of CMC from pineapple peel can be used as edible film for the other applications.
Keyword: Carboxymethyl cellulose, Edible film, Pineapple peel, Plasticizer

Judul: Optimasi Heat Sealable Film dari Kolang-Kaling (Arenga  pinnata Merr.) sebagai Bahan Kemasan
Abstrak: Kolang-kaling merupakan salah satu bahan baku yang sangat berpotensi untuk dikembangkan sebagai edible film. Namun edible film kolang-kaling dengan kombinasi lilin lebah mempunyai sifat yang mudah rapuh tanpa adanya penambahan plasticizer, sehingga edible film kurang fleksibel. Oleh karena itu untuk memperbaiki karakteristik edible film dapat digunakan gliserol sebagai plasticizer. Penentuan konsentrasi formula kolang-kaling dan lilin lebah harus tepat, sehingga dapat memperbaiki sifat mekanis dan fungsionalnya. Permasalahan tingkat kelarutan lilin lebah yang rendah menyebabkan penghalang terhadap uap air dan oksigen tidak maksimal, untuk memperbaiki karakteristik tersebut diperlukan emulsifier. Mengingat hal tersebut, tujuan dari penelitian ini adalah menghasilkan formula optimum edible film dengan menggunakan kolang-kaling kombinasi konsentrasi Carboxyl Methyl Cellulose (CMC), lilin lebah dan gliserol dengan metode permukaan respon serta menguji karakteristik fisik, mekanik dan organoleptik terhadap produk kantong edible film. Pembuatan edible film kolang-kaling menjadi kantong edible dilakukan dengan pemilihan jenis emulsifier (CMC, gliserol monostearat, tween 80, tween 20 dan span 20) dan optimasi menggunakan response surface methodology (RSM). Kombinasi formula edible film terbaik dibentuk menjadi kantong pembungkus bumbu mi instan. Sampel edible film digunakan untuk analisis ketebalan, heat sealability, nilai WVTR (Water Vapor Transmition Rate) dan kelarutan. Sampel kantong edible digunakan untuk analisis waktu kelarutan dan organoleptik. Analisis data edible film kolang-kaling menggunakan design expert versi 13 (DX-13) dan kantong edible menggunakan independent sample t-test pada taraf kepercayaan 95%. Nilai pengujian heat sealability yang lebih tinggi dan nilai ketebalan yang telah memenuhi standar JIS (Japanese Industrial Standard) menjadikan CMC terpilih menjadi emulsifier yang digunakan dalam pembuatan edible film kolang-kaling. Hasil optimasi kombinasi formula yang terpilih mununjukkan bahwa dengan konsentrasi CMC 3,11% (b/v), lilin lebah 2,00% (b/v) dan gliserol 1,00% (v/v) mampu menghasilkan nilai desirability sebesar 0,870. Edible film yang dibuat dengan formula optimum mempunyai ketebalan 0,15 mm, heat sealability 115,51 N/m, nilai WVTR 2,86 g/m2/jam dan kelarutan 75,61%. Selain itu, hasil pengujian kantong edible pembungkus bumbu bubuk mi instan memiliki nilai waktu kelarutan 2,5 menit dan penilaian organoleptik untuk atribut aroma (6,40), rasa (6,40), mouthfeel (6,30), after taste (6,16) dan overall (6,26) dengan keterangan yaitu disukai. Dengan demikian, pembuatan edible film berbahan dasar kolang-kaling yang dikombinasikan dengan CMC, lilin lebah dan gliserol dapat digunakan menjadi kantong pembungkus bumbu bubuk mi instan., Sugar palm fruit has great potential to be used as raw material for edible film. However, films made only from sugar palm fruit and beeswax without the addition of plasticizer become brittle. Glycerol can be used as a plasticizer to enhance the characteristics of edible film. The determination of concentration from sugar palm fruit and beeswax must be precise to improve the mechanical and functional properties. The low solubility of beeswax causes low barrier properties against water vapor and oxygen, so the emulsifier must be overcome. This study aimed to determine the optimum formula of edible films made from sugar palm fruit blended with carboxyl methyl cellulose (CMC), beeswax and glycerol using response surface methodology and testing physical, mechanical and organoleptic. Edible films made from sugar palm fruits as edible pouches were prepared by selecting emulsifiers (CMC, glycerol monostearate, tween 80, tween 20 and span 20) and optimization parameters using response
Keyword: edible film, heat sealable, kolang-kaling, lilin lebah, optimasi

Judul: Kriteria Osilasi Untuk Pertidaksamaan Diferensial Taklinear Orde Dua
Abstrak: dimana pertidaksamaan dibatasi pada suatu selang [T,oo) dengan T?:O, aCt) kontinu pada selang [0,00) dan j(u) mempunyai turunan pertarna yang kontinu pada selang (-00,00) dengan uj(u) >0 untuk u;"O. Dengan menggunakan Asumsi A dan Asurnsi B, diperoleh beberapa teorerna ten tang kriteria osilasi untuk pertidaksamaan diferensial taklinear orde dua.
Keyword: