Judul: Hydroxyapatite-Chitosan Composite Coating on Stainless Steel 316 to Improve Corrosion Resistance
Abstrak: Metals that were used in bone implantation should have good corrosion resistance that were not easily corroded when implanted into the body. Metal corrosion resistance of stainless steel 316 can be enhanced through the metal coating by hydroxyapatite-chitosan composite with composition ratio of hydroxyapatite (gram) and chitosan 3% (mL) 0.2:0, 0.2:0.1, 0.2:0.5, 0.2:1.0, and 0.2:1.5. Besides improving the corrosion resistance of metal, the presence of chitosan also maintain the position of hydroxyapatite on metal surfaces. Corrosion resistance increases with increasing amount of chitosan added and the best composition of hydroxyapatite-chitosan composite was 0.2:1.0.
Keyword: 

Judul: Study of Hydroxyapatite-Chitosan Composites with Various Metal Oxides Coated on Metal Alloys as Implant Materials
Abstrak: Kerusakan tulang yang meningkat membutuhkan sintesis biomaterial sebagai bahan implan. Penelitian ini dilakukan untuk meninjau berbagai referensi mengenai penyalutan komposit HAp-kitosan-logam oksida pada paduan logam. Metode yang baik dan banyak dipilih dalam sintesis HAp-kitosan-logam oksida yakni dengan menggunakan metode presipitasi, ex-situ dan metode elektroforesis deposisi (EPD) sebagai metode penyalutannya. Paduan logam yang tersalut komposit HApkitosan-logam oksida memiliki potensi dalam menghasilkan implan yang mampu menghambat bakteri dan ketahanan korosi secara baik. Komposit HAp-ZnOkitosan memiliki zona hambat paling baik terhadap bakteri E. coli yakni sebesar 8 mm. Zona hambat juga dipengaruhi oleh konsentrasi logam oksida yang ditambahkan. Paduan logam yang telah tersalut komposit menunjukkan ketahanan korosi lebih baik dibandingkan sebelum penyalutan. Logam CoCrMo yang tersalut komposit HAp-kitosan memiliki ketahanan korosi paling baik dibandingkan logam Stainless Steel dan Ti6Al4V dengan nilai laju korosi sebesar 0,0035 mpy., Increased bone destruction requires the synthesis of biomaterials as implant materials. This research was conducted to review various references regarding the coating of HAp-metal oxide-chitosan composites on metal alloys. A good and widely chosen method in the synthesis of HAp-chitosan-metal oxide is by using precipitation, ex-situ and deposition electrophoresis (EPD) methods as coating methods. The metal alloy coated with the HAp-chitosan-metal oxide composite has the potential to produce implants that can inhibit bacteria and have good corrosion resistance. The HAp-ZnO-chitosan composite had the best inhibition zone against E. coli bacteria, which was 8 mm. The zone of inhibition also affects the concentration of added metal oxides. The composite coated alloy showed better corrosion resistance than before coating. CoCrMo metal coated with HAp-chitosan composite has the best corrosion resistance compared to Stainless Steel and Ti6Al4V with a corrosion rate of 0,0035 mpy.
Keyword: alloy, antibacterial, anticorrosion, hydroxyapatite-chitosan, metal oxide

Judul: Analisis ekonomi sektor informal di Kota Tangerang
Abstrak: Penelitian ini mengungkapkan bahwa luasnya lapangan kerja di sektor informal merupakan faktor penting dalam proses migrasi di kota. Mengkaji tingkat kesejahteraan migran di sektor informal dengan menelaah perilaku migran pelaku ekonomi informal dalam mengupayakan kehidupannya di kota. Tahap awal merupakan periode paling kritis. Strategi yang digunakan adalah pemenuhan kebutuhan dasar. Selanjutnya adalah strategi peningkatan pendapatan. Analisis regresi berganda digunakan untuk melihat faktor-faktor yang mempengaruhi tingkat pendapatan migran di sektor informal, dan uji Duncan digunakan untuk mengkaji hubungan antara status pekerjaan dengan pendapatan. Responden pelaku ekonomi sektor informal adalah pemulung, lapak, pedagang kakilima makanan dan pedagang kakilima pakaian. Jika dibandingkan upah nominal rata -rata per bulan buruh di Jabotabek tahun 2002 yaitu sebesar Rp. 983.600,00, maka pendapatan rata -rata migran sektor informal lebih baik yaitu sebesar Rp. 1.631.176,00 per bulan. Jika mengacu pada rata-rata biaya hidup di Jabotabek (Republika, 2003) adalah Rp. 400.000,00 per bulan, maka profesi pemulung yang paling rendah rata -rata pendapatannya, yaitu Rp. 444.000,00 per bulan masih tergolong mampu hidup di kota. Hal ini menunjukkan bahwa ekonomi sektor informal tidak dapat diabaikan dalam perekonomian perkotaaan.
Keyword: economic sector, economy, informal sector