Judul: Laju Pelepasan Urea dari Onggok-g-poliakrilat dan Biodegradasinya
Abstrak: Onggok is a byproduct of tapioca production from cassava. Onggok contains 73% of starch which is potential to be transformed into soil conditioner, i.e. hydrogel to control urea release rate. Onggok was copolymerized by grafting with Na-acrylate, ammonium persulfate as initiator, and N,N-methylene-bis-acrylamide as cross-linker to produce onggok-g-polyacrylate hydrogel. Swelling of the hydrogel in water and 1 M urea solution were 250 and 203 g/g, respectively. The amount of urea that could be loaded into the hydrogel 1 M urea solution was 99%. Urea release rate from hydrogel in water followed a sigmoidal pattern, i.e. Richards model with correlation coefficient of 0.997. This hydrogel could inhibit the urea release in water 8.2 times higher compared with conventional urea application. Biodegradation of 0.11 g of hydrogel in 250 g of soil produced 754 mg of CO2 in 29 days so that it can be used in soil for more than 1 month.
Keyword: urea release rate, soil conditioner, onggok-g-polyacrylate, hydrogel, biodegradation

Judul: Analisis Kinetika Pelepasan Pupuk Urea dalam Hideogel dari Onggok Singkong pada Media Tanah Kering
Abstrak: Efisiensi pemupukan dan kontrol ketersediaan air masih menjadi masalah dalam pertanian. Hidrogel dapat dijadikan solusi, karena mampu menyerap air dan pupuk dan melepaskannya secara lambat. Hidrogel disintesis dari asam akrilat-akrilamida dan onggok singkong yang diikat silang dengan MBA, kemudian dimuati urea dengan variasi 0; 2,5; dan 5% menggunakan teknik dua langkah. Parameter yang diamati meliputi fraksi gel, swelling,kinetika swelling, pemuatan dan pelepasan pupuk pada tanah latosol dan podsolik, kinetika pelepasan pupuk serta karakterisasi morfologi permukaan dan gugus fungsi. Penambahan urea dapat menurunkan kemampuan swelling dan semakin tinggi konsentrasinya, maka semakin banyak urea yang termuat dan terlepas. Hidrogel termuat urea 2,5% dan 5% pada tanah podsolik serta 2,5% pada tanah latosol bersifat slow-release karena persen pelepasannya <15% dalam 24 jam. Kinetika pelepasan urea 2,5% mengikuti model Korsmeyer-Peppas, sedangkan pelepasan urea 5% mengikuti model Higuchi. Morfologi permukaan hidrogel terlihat heterogen dan berpori berukuran 0,6–18, 8 µm, saat termuat urea ada bercak putih yang menutupi pori,dan setelah release pada tanah terlihat adanya ruang kosong. Gugus fungsi hidrogel terdiri atas gugus O-H, C=O, C=C, C-H, C-O, C-C-O dan terdapat gugus C-N saat termuat urea., Fertilization efficiency and control of water availability are still problems in agriculture. Hydrogel can be used as a solution, because it is able to absorb water and fertilizer and release slowly. The hydrogel was synthesized from acrylic acid-acrylamide and cassava waste pulp crosslinked with MBA, then loaded urea with variations 0; 2,5; and 5% used a two-step technique. Parameters observed is gel fraction, swelling, swelling kinetics, fertilizer loading and release on latosol and podzolic soils, fertilizer release kinetics, surface morphology characterization and functional groups. The addition of urea decreases ability of swelling and the higher the concentration, the more urea is loaded and released. The hydrogel contains 2,5% and 5% urea in podzolic soils and 2,5% in latosol soils is slow-release because the release percentage is <15% in 24 hours. The kinetics of 2,5% urea release follow Korsmeyer-Peppas model, while the 5% urea release follows Higuchi. The surface morphology of hydrogel looks heterogeneous and porous measuring 0,6–18, 8 µm μm, when loaded urea there are white patches covering the pore, and after release on the soil there is visible empty space. The hydrogel functional group consists of O-H, C=O, C=C, C-H, C-O, C-C-O groups and C-N group when urea is loaded.
Keyword: hydrogel, fertilizer loading, fertilizer release, soil, urea

Judul: Beberapa aspek anatomi alat sirkulasi ruang dada kancil
Abstrak: Telah dilakukan penelitian dengan menggunakan 10 ekor kancil dewasa jantan dan betina dengan tujuan untuk menge- tahui beberapa aspek anatomi alat sirkulasi di dalam ruang dada, meliputi jantung, pembuluh darah yang keluar dan ma- suk jantung serta ukuran-ukuran jantung. Kancil merupakan ruminansia terkecil di dunia, hidup di daerah tropika India, Thailand, Malaysia dan Indonesia bagian barat. Hewan ini dilindungi dan mempunyai prospek yang baik untuk hewan penelitian maupun dibudidayakan. Hasil penelitian menunjukkan bahwa berat jantung rаta-rata adalah 0.69% dari berat rata-rata kancil. Dan ini mirip pada jantung kuda dan anjing. Bentuk jantung lonjong seperti halnya ruminansia. Demikian pula letaknya di dalam ruang dada seperti pada ruminansia dengan adanya Ligamentum sternopericardiacum. Di dalam ventrikel kanan membersit sebuah Musculus (M.) papillaris dari dindingnya dan tiga sampai empat Musculi (Mm.) papillares dari Septum interventriculare. Hanya dua buah Mm. papillares yang berukuran besar dibersitkan dari dinding ventrikel kiri. Percabangan Arteri (A.) coronaria sinistra lebih dominan dari pada A. coronaria dextra. Sedangkan A. sub clavia sinistra dicabangkan langsung dari aorta di dorso- caudal pembersitan Truncus (Tr.) brachiocephalicus…
Keyword: