Judul: Kajian Pengelolaan Lanskap Agrowisata D’Kandang Amazing Farm, Sawangan, Depok
Abstrak: Agrowisata merupakan suatu kawasan usaha pertanian yang dikembangkan secara kreatif sehingga mempunyai daya tarik wisata. D’Kandang Amazing Farm adalah salah satu agrowisata terbesar di kota Depok. D’Kandang Amazing Farm juga memiliki banyak potensi untuk dikembangkan sehingga layak untuk dijadikan tempat penelitian. Tujuan kegiatan penelitian ini adalah mengidentifikasi aspek-aspek pengelolaan lanskap agrowisata, menganalisis permasalahan lanskap agrowisata, dan menyusun strategi pengelolaan lanskap D’Kandang Amazing Farm secara berkelanjutan. Penelitian ini meliputi observasi, wawancara serta studi literatur. Data dari penelitian kemudian dianalisis menggunakan analisis SWOT untuk menghasilkan strategi dan rekomendasi pengelolaan lanskap D’Kandang Amazing Farm yang berkelanjutan.
Keyword: agrowisata, analisis SWOT, D’Kandang Amazing Farm, rencana pengelolaan lanskap

Judul: Analisis Strategi Promosi Agrowisata D’kandang Amazing Farm pada CV Sawangan Dairy Farm
Abstrak: Agrowisata D’Kandang Amazing Farm merupakan salah satu unit bisnis CV Sawangan Diary Farm di bidang wisata yang potensial karena berkembangnya tren back to nature dan tren wisata pendidikan pada masyarakat perkotaan. Pertumbuhan dan perkembangan objek wisata lain mendorong D’Kandang Amazing Farm untuk menyusun strategi promosi berbasis komunikasi pemasaran terpadu. Tujuan penelitian ini yaitu mengidentifikasi faktor-faktor yang mempengaruhi keputusan strategi promosi D’Kandang Amazing Farm, menganalisis kegiatan promosi CV Sawangan Dairy Farm dalam mengkomunikasikan agrowisata D’Kandang Amazing Farm dan memilih alternatif strategi promosi agrowisata D’Kandang Amazing Farm. Metode analisis yang digunakan adalah analisis IFE, EFE, SWOT dan Analytical Hierarchy Process (AHP). Hasil penelitian menujukkan bahwa alternatif strategi terbaik untuk agrowisata D’Kandang Amazing Farm adalah melakukan rekrutmen staf online dan memaksimalkan promosi melalui internet, serta fokus pada wilayah Depok dan sekitarnya.
Keyword: agrowisata d’kandang amazing farm, komunikasi pemasaran terpadu, strategi promosi, analytical hierarchy process (AHP)

Judul: Enhancement of photon absorbtion on BaxSr1-xTiO3 thin films semiconductor using photonic crystals.
Abstrak: In this research, has been conducted BaxSr1-xTiO3 (BST) thin films manufacturing for mole fraction x = 0.25, 0.35, 0.45, and 0.55; and concentration of 1 molar using chemical solution depositon (CSD) method. The materials, which are used in this research, are barium acetate [Ba(CH3COO)2, 99%], strontium acetate [Sr(CH3COO)2, 99%], titanium isopropoxide [Ti(C12O4H28), 97.999%], gallium trioxide [Ga2O3], 2-methoxyethanol [H3COOCH2CH2OH, 99%] and 1 x 1 cm of transparent conductive oxide (TCO) glass as substrate. Two BST thin films are made that for BST thin films which are doped by 10% galium (BGST) as p-type layer and pure BST solution as n-type. BST solution is made by reacting barium acetate [Ba(CH3COO)2, 99%], strontium acetate [Sr(CH3COO)2, 99%] and titanium isopropoxide [Ti(C12O4H28)] into 2-methoxyethanol solvent [H3COOCH2CH2OH, 99%] in accordance with mass gram for each x value. While, BGST solution is made in the same way as BST solution, plus adding gallium at 10% of the mass of BST. Once all materials are reacted, then vibrated using ultrasonic for 90 minutes, and followed by coating BGST / BST on the TCO substrate. Once the layer is formed, then annealed for 15 hours at temperature of 500 °C with increasing rate of 1.67 oC/minute. Characterizations of BST thin films with or without photonic crystals include the absorbance and transmittance in the visible light spectrum, as well as the electrical photoconductivity characterizations. From BST thin films without photonic crystals indicate that our thin films have light absorption area on almost the entire range of the visible light spectrum even to the infrared range with absorption value over than 67.6%, in addition, it can be seen that the maximum absorbance of BST thin films for all mole fractions lie in blue to green light spectrum region, 457 nm ≤ λ ≤ 570 nm and the minimum in yellow to red light spectrum region, 570 nm ≤ λ ≤ 678 nm. The largest absorbance is found at x = 0.25 with average absorbance value of 92.04% and maximum and minimum absorbance peaks at wavelength of 500.89 and 657.72 nm, respectively. At x = 0.35, average absorbance value decreased to 83.55% with maximum and minimum peaks at 505.73 and 613.68 nm, respectively. Then increased to 91.16% at x = 0.45 with maximum and minimum peaks at 506.04 and 618.56 nm, respectively. At x = 0.55, average absorbance value decreased to 80.12% with maximum and minimum peaks at 507.85 and 608.79 nm, respectively. Moreover, it can be seen that the addition of barium mole fraction leads to wider maximum absorbance or minimum transmittance peaks and narrower minimum absorbance or maximum transmittance peaks in the same range of the green and blue & red light spectrums, respectively. BST thin films with photonic crystals show increasing in absorption for all x values in the range of 3.04 into 13.33%. At x = 0.25, average absorbance percentage increased 3.96% from 92.4 into 95.68%, for x = 0.35 average percentage increased 7.07% into 89.45 from 83.55%. Furthermore, average absorbance of BST thin films at x = 0.45 increased 3.04% from 91.16 into 93.93% and x = 0.55 has
Keyword: