Judul: Oil Palm Fronds Particleboard Bonded with Phenol Formaldehyde and Molasses Adhesive
Abstrak: The utilization of oil palm fronds to be converted as particleboard was considered effective in preserving the environment. The addition of molasses to adhesive mixtures with phenol-formaldehyde (PF) was carried out as an effort to reduce the use of PF adhesive. This research aims to produce particleboard with high-quality and eco-friendly from oil palm fronds and to analyze the effect of adding molasses to PF adhesive on the quality of particleboard. This research method uses 5 levels of PF: molasses adhesive composition, namely 100:0, 75:25, 50:50, 25:75, and 0:100 (wt%). The target density of particleboard is designed to be 0,8 g/cm³ with dimensions of (30×30×0.6) cm³. The adhesive content used is 16% with a compression temperature of 180 °C for 10 minutes. Overall, the results of testing showed that the density, moisture content, thickness swelling, and MOE of the particleboard in this study had met the standard of SNI 03-2105-2006, but in the tests of MOR and IB only the composition of PF: molasses 100:0, 75:25, and 50:50 which had met the standard of SNI 03-2105-2006.
Keyword: adhesive, composition, molasses, oil palm fronds, particleboard

Judul: Papan Partikel Dari Pelepah Kelapa Sawit Menggunakan Perekat Asam Sitrat dan Molase
Abstrak: Pelepah kelapa sawit merupakan biomassa kelapa sawit yang biasanya tidak dimanfaatkan secara optimal, pelepah kelapa sawit memiliki kandungan lignoselulosa yang berpotensi untuk dijadikan papan partikel dan ketersediannya yang cukup melimpah.Penelitian ini bertujuan menghasilkan papan partikel yang ramah lingkungan tanpa menggunakan bahan kimia berbahaya. Selain itu, menganalisis pengaruh kadar perekat dengan menggunakan asam sitrat dan molase terhadap karakteristik sifat fisis dan mekanis papan partikel. Papan dibuat dengan kerapatan target 0,8 g/cm³ dan ukuran 30 x 30x 0,6 cm menggunakan kempa panas suhu 200°C selama 10 menit dengan tekanan 5 Mpa. Pengujian sifat fisis dan mekanis papan partikel mengacu pada standar SNI 03-2105-2006 (kerapatan, kadar air, daya serap air, pengembangan tebal, MOE, MOR, dan keteguhan rekat). Hasil penelitian ini menunjukan kadar perekat berpengaruh nyata terhadap karakteristik sifat fisis dan mekanis papan partikel Semakin tinggi kadar perekat yang ditambahkan mampu meningkatkan sifat fisis dan mekanis pada papan plafon yang dibuat., Palm fronds are palm biomass that is usually not used optimally, palm fronds have lignocellulose content that has the potential to be used as a particleboard and its availability is quite abundant. This study aims to produce environmentally friendly particle boards without the use of harmful chemicals. In addition, it analyzes the effect of adhesive levels using citric acid and molasses on the characteristics of the physical and mechanical properties of particle boards. The board was made with a target density of 0,8 g/cm³ and a size of 30 x 30x 0,6 cm using a heat felt of 200°C for 10 minutes with a pressure of 5 Mpa. Testing of the physical and mechanical properties of particle boards refers to the standard SNI 03-2105-2006 (density, moisture content, water absorption, thickness swelling, MOE, MOR, and internal bounding). The results of this research show that the adhesive content has a significant effect on the characteristics of the physical and mechanical properties of composite ceiling boards. The higher the adhesive content added is able to improve the physical and mechanical properties of the ceiling board made.
Keyword: adhesive content, citric acid, molasses, palm fronds, particle board

Judul: Hydatidosis Pada Anjing
Abstrak: Hydatidosis disebut juga echinococcosis merupakan penyakit parasiter yang menyerang hewan, disebabkan oleh genus Echinococcus dan salah satu spesies pada anjing yang bersifat kosmopolitan serta pernah timbul di Indonesia adalah Echinococcus granulosus. Echinococcus granulosus merupakan cacing pita yang sangat kecil panjangnya hanya 2-5 mm, terdiri dari scolex, neck, dan 3-4 proglottid. Scolex mempunyai 4 sucker dan sebuah rostellum yang dilengkapi dengan 2 baris kait yang masing-masing terdiri dari 30 buah. Kait yang besar panjangnya 33.2-39.8 u sedangkan yang kecil 22.1-34 u. Proglottid yang pertama immature, yang kedua mature, dan yang ketiga proglottid gravid. Lubang kelamin terletak disebelah lateral berselang-seling tidak beraturan, testes berjumlah 38-52 buah. Ovariumnya berbentuk seperti ginjal dan uterusnya mempunyai diverticulum lateral. Jenis cacing ini yang ditemukan di Indonesia tidak mempunyai neck. Siklus hidup E. granulosus memerlukan induk semang intermediate untuk perkembangan telur menjadi kista dan induk semang defenitif untuk perkembangan kista menjadi cacing dewasa. Domba merupakan hewan yang paling subur untuk perkembangan stadium kistanya dan bersama anjing kedua hewan ini memegang peranan penting dalam penyebaran penyakit ini. Domba biasanya terinfeksi melalui makanan atau minuman yang terkontaminasi telur cacing. Telur-telur yang tertelan ini akan menetas menjadi oncosphere, lalu menembus dinding usus masuk ke saluran limfe atau vena kecil di mesenterium yang kemudian dengan aliran darah terbawa ke seluruh tubuh. Oncosphere ini biasanya menetap di hati dan paru-paru. Bila oncosphere telah berubah menjadi kista dan termakan oleh anjing maka infeksi dapat berlangsung pada anjing hingga mencapai bentuk cacing dewasa. Penyakit ini telah tersebar di seluruh dunia, mencakup banyak hewan tanpa membedakan umur dan jenis kelamin. Menyebabkan kerugian ekonomi yang besar terhadap ternak bahkan dapat menyerang manusia. Akibat adanya kista adalah timbulnya kelemahan, anorexia, dyspnoe, kurus, dan akhirnya kematian dari induk semang. Kebersihan lingkungan terutama yang berkaitan dengan anjing adalah tindakan pencegahan yang utama sedangkan tindakan pembedahan merupakan salah satu usaha yang agak memuaskan dalam penanganan penyakit ini.
Keyword: