Judul: Penentuan Karakteristik Mekanis Lentur Lamina dan Balok Laminasi Kayu Eukaliptus Menggunakan Beberapa Metode Pengujian Non Destruktif
Abstrak: Metode pengujian non destruktif merupakan sebuah metode untuk mengidentifikasi sifat fisis dan mekanis bahan tanpa menimbulkan kerusakan yang berarti yang dapat mengubah manfaat akhir dari bahan tersebut. Walaupun aplikasi atau penggunaan metode pengujian non destruktif pada bahan kayu sudah banyak dipakai dan terbilang sukses, namun di Indonesia penelitian dan aplikasi dari metode tersebut sangatlah terbatas. Tujuan dari penelitian ini ialah membandingkan nilai kekakuan (MOE) menggunakan beberapa metode pengujian non destruktif pada lamina dan balok laminasi, membandingkan nilai kekakuan (MOE) lamina dengan balok laminasi, membandingkan nilai kekuatan lentur maksimum (MOR) balok laminasi, membandingkan hubungan antar nilai kekakuan (MOE) serta nilai kekuatan lentur maksimum (MOR). Bahan yang digunakan dalam penelitian ini adalah kayu Eukaliptus (Eucalyptus urophylla) umur 4 tahun. Perekat yang digunakan adalah Isosianat. Log kayu Eukaliptus diproses menjadi lembaran-lembaran lamina dengan panjang 110 cm, lebar 8 cm dan tiga tipe ukuran ketebalan lamina yakni 1 cm; 1,5 cm; dan 2 cm dan kemudian dibuat menjadi balok laminasi (glulam) dari ketiga jenis ketebalan lamina yang berbeda tersebut, yakni GA (ketebalan lamina 1 cm), GB (ketebalan lamina 1,5 cm), dan GC (ketebalan lamina 2 cm). Lamina dan balok laminasi diuji dengan menggunakan beberapa metode pengujian non destruktif yaitu metode defleksi dan metode gelombang suara. Metode defleksi menggunakan alat Deflektometer dan UTM Instron, sedangkan metode gelombang suara menggunakan Metriguard® (gelombang sonik) dan SylvatestDuo® (gelombang ultrasonik). Nilai kekakuan (MOE) yang diperoleh dari keempat alat uji non destruktif tersebut kemudian dibandingkan secara deskriptif dan diuji secara statistik. Parameter pengujian yang didapatkan adalah nilai kekakuan menggunakan deflektometer (MOEdef), nilai kekakuan menggunakan UTM (MOEUTM), nilai kekakuan menggunakan metriguard® (MOEsn), dan nilai kekakuan menggunakan sylvatestduo® (MOEusn). Selanjutnya untuk mengetahui kekuatan lentur maksimum glulam dilakukan pengujian destruktif menggunakan UTM Instron untuk menentukan nilai MOR. Pada perbandingan MOE lamina, nilai MOEusn merupakan yang tertinggi kemudian diikuti MOEUTM, MOEsn, dan MOEdef. Sedangkan pada perbandingan MOE balok laminasi, nilai MOEusn juga merupakan yang tertinggi kemudian diikuti MOEsn, MOEUTM, dan MOEdef. Untuk perbandingan antara MOE lamina dengan MOE glulam, pada semua alat uji non destruktif nilai MOE lamina selalu iii lebih besar dari nilai MOE glulam. Pada perbandingan nilai MOR, rata-rata nilai MOR terbesar pada glulam dengan tebal lamina penyusun 1 cm (GA) kemudian disusul oleh glulam dengan tebal lamina penyusun 1,5 cm (GB) dan yang terkecil pada glulam dengan tebal lamina penyusun 2 cm (GC). Analisis regresi linier pada balok laminasi menunjukkan hanya MOEdef sebagai peubah x yang dapat digunakan untuk menjelaskan keragaman total dari peubah y (MOEUTM) pada selang kepercayaan 95%. Selanjutnya pada persamaan regresi dimana MOR sebagai peubah y, hanya MOEdef dan MOEUTM sebagai peubah x yang dapat digunakan untuk menjelaskan keragaman total dari MOR sebagai peubah y.
Keyword: 

Judul: Karakteristik Balok Laminasi (Glulam) Kayu Ekaliptus (Eucalyptus urophylla ST. Blake)
Abstrak: The use of wood for structural purposes requires a large dimension and long span as well as specific requirements of high strength. On the other hand, a lot of wood available today is wood from plantations with fast growing species of small diameter and generally have inferior properties such as defects content, natural durability and strength compared to wood from natural forests. One common way to get the wood to the desired dimension is the lamination technique. One of the laminate product used as a structural material is laminated timber. The aim of the study was glulam composed by three laminas thickness from eucalyptus wood. Three laminas 1cm, 1.5cm, 2cm thickness, were prepared in this study. Each laminae was tested by non destructive evaluation of deflection method to determine Modulusof Elasticity (MOE). The highest MOE of laminae was placed at the outside of glulam, then between laminas were glued by isocyanate resin. The dimension of glulam was (8 x 6 x 110) cm in thick, width, and length. The physical and mechanical properties of glulam were evaluated refering to standard JAS 234:2003. The physical properties of glulam timber of moisture content was in average value of 13.37%. The density mean of glulam timber were 0,65g/cm³ to glulam A composed by 1cm thickness of laminae, 0,63g/cm³ to glulam B composed by 1.5cm thickness of laminae, 0,56g/cm³ to glulam C composed by 2cm thickness of laminae. Delamination properties of hot and cold water were 25.2% and 4.99% for glulam A, 45.9% and 8.03% for glulam B, 73.86% and 0% for glulam C. The average value of mechanical properties Modulus of Elasticity (MOE) were 10.06x10⁴ kgf/cm² for glulam A, 7.42x10⁴ kgf/cm² for glulam B, and 5.63x10⁴ kgf/cm² for glulam C. The Modulus of Rupture (MOR) of glulam beams were 561 kgf/cm², 424 kgf/cm², and 327 kgf/cm² for glulam A, glulam B, and glulam C, respectively. Average value of shear strength properties were 98.42 kg/cm² for glulam A, 90.23 kg/cm² for glulam B, 79.01 kg/cm² for glulam C. Moisture content and delamination on cold water glulam timber were in compliance with JAS standards 234: 2003 while the delamination on heat water not fullfill to meet the standards. The MOE and MOR values the glulam timber (except MOE laminated timber with a thickness of 1.5 cm and 2 cm) were in compliance with JAS standards 234: 2003.
Keyword: 

Judul: Infeksi Virus Parainfluenza Pada Anjing
Abstrak: Virus parainfluenza anjing termasuk famili Paramyxoviridae, berbentuk pleomorf dengan ukuran bervariasi (bergaris tengah antara 100-500 nm), berpembungkus peka ether, berisi genom RNA dan secara serologis mempunyai kesamaan dengan virus SV-5 kera; dikenak sebagai salah satu kausa penting dari sindrom "kennel cough". Infeksinya dapat mengenai anjing semua umur yang belum pernah terinfeksi atau mendapatkan vaksinasi mengakibatkan gejala klinis ringan yang terbatas pada traktus respirasi atu infeksi yang secara klinis tidak memperlihatkan gejala nyata. Gejala klinis yang nampak setelah masa inkubasi (1-5 hari) terlewati berupa batuk yang tidak berat selama beberapa hari, berbagai tingkat tonsilitis dan pharyngitis dan kadang-kadang ditemukan kenaikan temperatur rektal antara 1-2 derajat C dari temperatur normal rat-rata. Anjing terinfeksi mengandung virus pada traktus respirasi bagian atas dan bawah serta limfonoduli sampai hari ke 9 setelah infeksi. Penyebaran virus antar anjing terjadi secara aerogen.
Keyword: