Judul: Karakterisasi Optik dan Uji Respon Piezoelektrik Film BaCexTi1-xO3.
Abstrak: Barium Titanat (BaTiO3) merupakan material ferroelektrik sekaligus piezoelektrik yang unggul. Film barium titanat berhasil dibuat dengan variasi konsentrasi pendadah CeO2 0%, 2%, 4%, 6% menggunakan metode Chemical Solution Deposition (CSD) dengan proses annealing pada suhu 550 °C selama 23.5 jam dan teknik spin coating dengan kecepatan 8000 rpm. Hasil uji sifat kristal menunjukkan bahwa parameter kisi pada konsentrasi 0%, 2%, 4%, 6% pendadah CeO2 secara berurutan a = b = 4.0491 Å dan c = 4.0258 Å; a = b = 4.0627 Å dan c = 4.0355 Å; a = b = 4.0549 Å dan c = 4.0249 Å; a = b = 4.0547 Å dan c = 4.0385 Å sehingga struktur kristalnya berbentuk tetragonal. Hasil uji sifat optik menghasilkan indeks bias secara berturut turut 1.4842, 1.4508, 1.4917, 1.5175. Hasil uji respon piezoelektrik mendapatkan nilai konstanta tegangan piezoelektrik pada rentang 33.3322 Vm/N sampai 43.1052 Vm/N, konstanta muatan piezoelektrik pada rentang 1.4700 x 10-7 C/N sampai 1.9074 x 10-7 C/N dan regangan mekanik pada rentang 166.0147 sampai 329.1333. Berdasarkan hasil karakterisasi dan pengujian, film BaTiO3 didadah CeO2 memiliki potensi untuk dikembangkan sebagai sensor piezoelektrik.
Keyword: annealing, BaTiO3, CeO2, Chemical Solution Deposition, op-amp

Judul: Analysis of Saturation Current, Barrier  Voltage, and Electron Mobility of Ferium-Doped Barium Titanate Thin Films
Abstrak: Perkembangan teknologi khususnya elektronika gencar dilakukan untuk menciptakan inovasi devais berukuran kecil dengan performa yang maksimal, seperti film tipis. Film tipis Barium Titanat (BaTiO3) didadah Ferium dengan variasi konsentrasi pendadah (0%; 0,5%; dan 1%) berhasil dibuat. Larutan sampel disaring menggunakan filter PVDF kemudian dideposisi menggunakan metode chemical solution deposition (CSD) di atas substrat silikon tipe-p (100) dengan teknik spin coating pada kecepatan putar 3000 rpm selama 60 detik. Proses annealing dilakukan pada suhu 850°C dan ditahan selama 8 jam. Berdasarkan pengujian I-V meter, film tipis memiliki karakteristik dioda dan responsif terhadap perubahan intensitas iradiasi cahaya. Peningkatan intensitas iradiasi cahaya menyebabkan nilai arus saturasi meningkat namun nilai potensial penghalang menurun. Mobilitas elektron Barium Titanat pada konsentrasi pendadah Ferium 0%, 0,5%, dan 1% didapatkan berturut-turut 2,02×10-6cm2/Vs, 3,16×10-6cm2/Vs, dan 3,03×10-6cm2/Vs. Hasil sifat listrik ini menunjukkan bahwa film tipis BaTiO3 didadah Fe berpotensi sebagai sensor cahaya., The development of technology, especially in electronics, is actively pursued to create innovative devices that are small in size yet deliver maximum performance, such as thin films. Ferium-doped Barium Titanate (BaTiO3) thin films with varying dopant concentrations (0%, 0,5%, and 1%) have been successfully fabricated. The sample solution was filtered using a PVDF filter and then deposited on p-type silicon (100) substrates using the chemical solution deposition (CSD) method with spin coating technique at a spin speed of 3000 rpm for 60 seconds. The annealing process was performed at a temperature of 850°C and held for 8 hours. Based on I-V meter testing, the thin films exhibited diode characteristics and were responsive to changes in light irradiation intensity. Increasing the intensity of light irradiation resulted in an increase in saturation current while the barrier potential decreased. The electron mobility of Barium Titanate with Ferium dopant concentrations of 0%, 0,5%, and 1% were found to be 2,02×10-6cm2/Vs, 3,16×10-6 cm2/Vs, and 3,03×10-6cm2/Vs, respectively. These electrical properties indicate that Fe-doped BaTiO3 thin films have the potential to be used as light sensors.
Keyword: Barium Titanate, CSD, Dopant, I-V meter, Thin films

Judul: Penyebaran virus Newcastle-Disease (ND) pada burung liar
Abstrak: Banyak usaha yang telah dilakukan untuk mencegah dan mengendalikan terjadinya serangan wabah ND, seperti misalnya peningkatan sanitasi dan vaksinasi ND. Akan tetapi sam pai saat ini pengendaliannya belum dapat dilakukan secara tuntas. Banyak masalah yang menyebabkan kegagalan dari usaha untuk mengendalikan wabah ND, salah satu masalah yang perlu dipertimbangkan dalam penanggulangan wabah ND adalah sumber dan penyebaran virus ND oleh burung liar (Ronohardjo, 1980). Walaupun telah diketahui bahwa burung liar mempunyai peranan dalam penyebaran penyakit unggas, tetapi harus diakui bahwa sedikit sekali informasi mengenai jenis burung yang mempunyai potensi sebagai sumber dan penyebar virus ND. Selain menyebarkan penyakit unggas, burung liar juga dapat menyebarkan penyakit mammalia (Ottis and Bachmann, 1983). ...
Keyword: