Judul: Sintesis dan Pencirian Hidroksiapatit dari Limbah Cangkang Kerang Hijau dengan Metode Kering
Abstrak: Hydroxyapatite (HAp) is a calcium phosphate biomaterial utilized in medicine as bone implant and dental fillings. HAp has been synthesized from green mussel shells with dry method. Calcination of green mussel shells at 1100 oC for 18 hours produced CaO with 97.83% crystallinity. Contact of CaO with the air for a night produced Ca(OH)2 with 85.45% crystallinity. Heating of CaO and Ca(OH)2 as the starting materials at 900 and 1100 °C for 2 hours produced HAp as characterized by using X-ray diffractometer (XRD), Fourier transform infrared (FTIR) spectrophotometer, and scanning electron microscope (SEM). The best HAp result was obtained from CaO material. The XRD diffractogram showed the formation of HAp phase accompanied by other calcium phosphate phase at 2θ angles matched with Joint Crystal Powder Diffraction Standard data. The FTIR spectra showed the presence of PO4 3– and OH– groups of the HAp and the SEM picture showed homogenous HAp crystal granule size. With additional treatments, the HAp pore size can be adjusted to be applied as bone implant or dental fillings.
Keyword: 

Judul: Sintesis dan Pencirian Hidroksiapatit dari Cangkang Kerang Hijau dengan Metode Sol-Gel
Abstrak: Hydroxyapatite (HAp) is a major component of bones and teeth. HAp is widely used to repair, fill, extend, and reconstruct damaged bone tissue. In this research, HAp has been synthesized from green mussel shell by using sol-gel method. The controlled synthesis parameter was pH, and the variable being compared was heating temperature at 900 and 1100 oC. The HAp products were characterized by X-ray diffractometer (XRD), Fourier transform infrared spectrophotometer, and scanning electron microscope. The results showed that HAp was formed at alkaline pH. The XRD pattern showed that Hap was formed along with type A apatite carbonate, octacalcium phosphate, α- and β-tricalcium phosphate. The crystallinity was increased by raising the temperature and prolonging the heating time. The quality of HAp will get better with increasing crystallinity, and incrasing the temperature will raise the amount of HAp formed as well
Keyword: 

Judul: Pengaruh kontrol keluarga dan sekolah terhadap perilaku anak dalam menonton tayangan Televisi perbandingan antara SLTP di Desa dan di Kota: Kasus siswa SL TPN I Dramaga, Kabupaten Bogr, SLTP I Bogor, dan SLTP Regina Pacis, Kotamadya Bogor
Abstrak: Perkembangan siaran lelevisi di Indonesia lelah menimbulkan pro dan konlra di kalangan oranglua dan pendidik berkailan dengan pengaruhnya lerhadap perilaku anak dalam menonlon layangan lelevisi. Para oranglua dan pendidik mencoba mengalasi kekhawaliran ini dengan memberikan konlrol berupa lugas, kegialan dan aluran-aluran lertentu agar anak lidak menghabiskan waklunya di depan pesawal televisi. Berdasarkan ha! lersebul limbul pertanyaan bagaimanakah pengaruh konlrol keluarga berupa durasi !es, durasi belajar dan jumlah aluran yang dilerapkan dalam keluarga lerhadap perilaku anak dalam menonlon layangan televisi di desa dan di kola? Bagaimanakah pengaruh kontrol sekolah berupa durasi mengerjakan tugas intrakurikuler dan durasi mengikuli kegialan ekstrakurikuler lerhadap perilaku anak dalam menonlon televisi di desa dan di kola? Sebelumnya akan dilihal lerlebih dahulu pengaruh karakleristik keluarga yang lerdiri dari pendapalan keluarga, pendidikan ayah dan pendidikan ibu lerhadap konlrol keluarga. Selain itu juga akan dilihal pengaruh karaklerislik sekolah terhadap kontrol sekolah Penelilian dilakukan di liga sekolah yang mewakili daerah desa dan kola. SLTPN 1 Dramaga mewakili responden di pedesaan karena sekolah lersebul lidak lerlelak di ibukola kabupaten, mewakili golongan menengah ke bawah dan siswanya linggal di daerah pedesaan. Daerah kola diwakili oleh SLTP 1 Bogor dan SLTP Regina Pacis, karena diduga ada perbedaan antara sekolah negeri dan swasta. Dua sekolah tersebut dipilih mewakili golongan menengah ke atas dan kedua siswanya tinggal di daerah perkotaan.
Keyword: