Judul: Pembuatan Film Tipis Barium Titanat ( BaTiO3 ) Didadah Ferium Oksida ( Fe2O3) Menggunakan Metode Chemical Solution Deposition
Abstrak: Telah berhasil membuat film tipis Barium Titanat (BaTiO3) di atas substrat Si (100) tipe p dengan metode Chemical Solution Deposotion (CSD) dengan larutan 2 M berbantuan spin coating dengan kecepatan putar 8000 rpm. Film ini di annealing dengan suhu 850 0C ditahan selama 8 jam. Film tipis Barium Titanat (BaTiO3) pada konsentrasi pendadah 0% , 2%, 4%, 6% Ferium Oksida (Fe2O3) dikarakterisasi sifat optik, XRD , SEM, EDX sehingga menghasilkan energy gap berturut-turut sebesar 3.6 eV, 3.36 eV, 3.28 eV, 2.75 eV. Diperoleh parameter kisi sebesar a = b = 4.034165 Å dan c = 4.027978 Å ; a = b = 4.051396 Å dan c = 4.051422 Å ; a = b = 4.020782 Å dan c = 4.015575 Å ; a = b = 4.062769 Å dan c = 4.067526 Å sehingga struktur kristalnya berbentuk tetragonal , dengan rata-rata ukuran kristal nya sebesar 0.2614, 0.2056, 0.3288, 0.3268 dalam satuan μm.
Keyword: annealing, bandgap, BaTiO3, CSD, Fe2O3

Judul: Synthesis and Characterizations of Barium Titanate (BaTiO3) Thin Film with Varied Concentration of Iron (II) Acetate (Fe(CH3COO)2) as Dopant
Abstrak: Sintesis film tipis BaTiO3 dengan variasi konsentrasi pendadah Fe (0%; 2%; 4%; dan 6%) menggunakan metode chemical solution deposition (CSD) berhasil dilakukan. Larutan sampel dideposisikan di atas substrat silikon (100) tipe-p dengan teknik spin coating pada kecepatan anguler 8000 rpm selama 60 detik. Proses annealing dimulai pada suhu kamar hingga mencapai suhu 850°C dan ditahan selama 8 jam dengan kelajuan suhu sebesar 1,67°C/menit, dilanjutkan dengan pendinginan hingga suhu kamar selama 12 jam. Ketebalan film dihitung dengan metode volumetrik dan hasilnya berturut-turut yaitu 3,9867 μm; 3,8759 μm; 3,6913 μm; dan 3,0454 μm. Analisis dengan persamaan Cramer-Cohen menghasilkan parameter kisi a = b yaitu 3,843 Å; 3,882 Å; 3,898 Å; dan 3,909 Å serta parameter kisi c yaitu 4,002 Å; 3,938 Å; 4,070 Å; dan 4,024 Å dengan struktur kristal tetragonal. Nilai enegi band gap hasil analisis dengan fungsi Kubelka Munk untuk indirect transition berada dalam rentang 3,0689 – 3,2051 eV dan direct transition berada dalam rentang 2,7660 – 3,0417 eV., The synthesis of BaTiO3 thin film with variations in concentration of Fe as dopant (0%; 2%; 4%; and 6%) using chemical solution deposition (CSD) method has been successfully done. The solutions was deposited on p-type silicon (100) substrates with spin coating technique at the angular speed of 8000 rpm for 60 seconds. The annealing process was started at room temperature until 850°C and was held for 8 hours with a temperature speed of 1.67°C/minutes, followed by cooling process to room temperature for 12 hours. Film thickness was calculated using volumetric method and the results are 3.9867 μm; 3.8759 μm; 3.6913 μm; and 3.0454 μm. The results of the analysis using Cramer-Cohen equation obtained that the lattice parameters a = b are 3.843 Å; 3.882 Å; 3.898 Å; and 3.909 Å and c are 4.002 Å; 3.938 Å; 4.070 Å; and 4.024 Å with tetragonal crystal structure. The values of band gap energy that was analyzed using Kubelka-Munk method equation are in range of 3.0689 – 3.2051 eV for indirect transition and 2.7660 – 3.0417 eV for direct transition.
Keyword: thin film, barium titanate, cramer-cohen, kubelka-munk, dopant

Judul: Kajian Patologi Hog Cholera Kasus Outbreak Tahun 2006 Di  Kabupaten Jayapura Provinsi Papua
Abstrak: Hog cholera merupakan salah satu penyakit viral pada babi yang bersifat fatal, secara sporadik penyakit ini masih di temukan di Kabupaten Jayapura dan di anggap sebagai salah satu penyebab kematian babi. Untuk memperoleh pemahaman komprehensif tentang hog cholera telah di lakukan penelaahan dengan tujuan untuk mengetahui 1). Bagaimana perubahan patologi organ babi yang terinfeksi hog cholera, apakah perubahan ini sama dengan perubahan yang di temukan pada kasus-kasus terdahulu di luar Papua. (2). Distribusi antigen hog cholera (3). Bagaimana gambaran histopatologi organ babi dengan tinjauan khusus perubahan pada buluh darah.
Keyword: