Judul: Synthesis of Molybdenum Trioxide (MoO3) by Electrochemical Method for Electrochromics Application
Abstrak: Molybdenum trioxide (MoO3) thin films have been deposited on glass substrates by electrochemical method using ammonium heptamolybdate tetrahydrate ((NH4)6Mo7O244H2O). The films were deposited onto glass substrates as the control temperature at 25○C and annealing treatment at 350○C for 30 mins. The MoO3 thin films were investigated by UV-Vis, X-ray diffraction techniques (XRD), Scanning Electron Microscopy (SEM). The JCPDS card show that orthorhombic MoO3 (α- phase) has been formed. Molybdenum trioxide MoO3 formation was also confirmed by JCPDS card no. 35-0609. The SEM photographs revealed that the spherical and rod-like morphology and their grains size increased with increasing of heating temperatures. The measurement results show that the MoO3 thin film prepared at 350°C transmited about 80% of the visible spectrum. The effect of different heat treatments on surface morphology, thickness and optical properties of the films are discussed in this thesis.
Keyword: Institut Pertanian Bogor, Bogor Agricultural University, IPB, Electrophoretics, electrodeposide, electrochromics, electrochromic materials, electrochromic mechanism

Judul: Effect of Annealing Temperature on Optical and Electrochromic Properties of WO3 Thin Film with Sol-gel Method
Abstrak: Film tipis WO3 dibuat dengan variasi suhu pemanasan 200 °C, 400 °C dan 600 °C telah berhasil dilapiskan di atas substrat ITO dengan menggunakan metode Sol-gel. Film WO3 dibuat dengan tiga kali pelapisan menggunakan teknik spin coating selama 30 detik kemudian dipanaskan pada suhu 200 °C, 400 °C dan 600 °C dengan waktu tahan selama 2 jam. Uji XRD digunakan untuk mengetahui struktur kristal film WO3. Hasil menunjukkan bahwa struktur WO3 yang terbentuk adalah monoklinik dan dapat diketahui bahwa penambahan suhu pemanasan mengakibatkan kristalitas film WO3 semakin meningkat. Film dikarakterisasi menggunakan spektrofotometer UV-Vis untuk mengetahui sifat optik berupa analisis nilai absorbansi, transmitansi, dan energi celah pita. Peningkatan suhu pemanasan pada film WO3 menyebabkan nilai absorbansi pada daerah cahaya tampak meningkat dan energi celah semakin kecil. Uji elektrokromik menunjukkan effisiensi pewarnaan terbaik dimiliki oleh film WO3 yang dipanaskan pada suhu 400 °C.
Keyword: Bogor Agricultural University, Institut Pertanian Bogor, IPB, Annealing temperatur, electrocromic, sol-gel, thin film, wolfram oksida, suhu pemanasan, XRD, X-ray ditraction

Judul: Karakteristik habitat kambing hutan Sumatera, Capricornis sumatraensis Bachstein, 1799 di kawasan Danau Gunung Tujuh, Taman Nasional Kerinci Barat
Abstrak: Kambing hutan sumatera (Capricornis sumatraensis sumatraensis Bachstein, 1799) telah dilindungi sejak tahun 1931 berdasarkan Peraturan Perlindungan Binatang Liar 1931 Nomor : 266. Populasi kambing hutan sumatera di alam dikhawatirkan akan menurun disebabkan adanya berbagai faktor yang mengancam kelestariannya seperti perburuan liar dan perusakan habitat yang terjadi di Kawasan Danau Gunung Tujuh. Menurut Borner (1974) dalam Direktorat Penyuluhan KSDA (1994), kawasan Danau Gunung Tujuh merupakan tempat pembiakan ideal untuk kambing hutan.