Judul: Studi kasus patologi hernia diafragmatika pada Kucing
Abstrak: Seekor kucing ditemukan dalam keadaan yang kritis. Gejala klinis yang terlihat antara lain adanya perlukaan pada kulit, exophtalmus, anoreksia, kaheksia, dispnoe, anemia, konstipasi dan dehidrasi berat. Pengobatan telah dilakukan namun kucing gagal mengalami persembuhan. Radiografi menunjukkan garis diafragma tidak terlihat disertai adanya perpindahan organ abdomen ke dalam rongga thoraks. Pada pengamatan patologi anatomi terlihat bahwa diafragma mengalami kelainan. Secara umum lesio kongesti dan yang menyertainya ditemukan pada pengamatan histopatologi pada jantung, paru-paru, hati, ginjal, limpa, linfonodus, dan otak. Lesio pada beberapa organ tersebut muncul akibat perpindahan saluran pencernaan dan sebagian hati ke dalam rongga thoraks karena adanya tekanan negatif. Oleh sebab itu jantung dan paru-paru tidak dapat bekerja normal yang memicu kematian akibat gagal jantung kongestif.
Keyword: Bogor Agricultural University, Institut Pertanian Bogor, IPB, Diaphragmatic hernia in cat, Cat disease, Cat pathology, Diaphragm anomalies

Judul: Studi Kasus Patologi Hernia Diafragmatika pada Kucing
Abstrak: A cat was found with several critical conditions such as skin ulceration, exophthalmus, anorexia, cachexia, dyspnoe, anemia, constipation, and severe dehydration. The cat was well-treated with some medications but it failed. Radiographs show that diaphragm line was not seen with some abdominal contents displacement into the thoracic cavity. Necropsy study revealed many lesions in characteristic of congenital diaphragmatic hernia due to diaphragm anomalies. Histopathologically, congestion and other lesions were found in heart, lungs, liver, kidneys, spleen, lymph node, and brain. Those lesions were found due to negative pressure effect which moved the intestine and a part of liver into the thoracic cavity. Therefore, the heart and lungs could not work normal then consequence of the death was caused by congestive heart failure.
Keyword: 

Judul: Characteristics of Rotary-cut Veneer of Boiled Jabon and Sengon Logs.
Abstrak: Fast growing Jabon and Sengon are largely rotary-cut to produce veneer for plywood, com-ply and LVL. In order to provide better information on veneer production and utilization, the effects of wood juvenility and veneer thickness on lathe checks of Jabon and Sengon rotary-cut veneer were evaluated. Before peeling, jabon and sengon log were boiled at 50 and 75 oC for 4 and 8 hours, respectively. The boiled logs were peeled to produce veneer of 1.0, 1.5 and 2.0 mm in thickness. Lathe checks of veneers were measured under an optical video microscope. The rotary-cut veneer was grouped and evaluated separately at every segmented of 1.0 cm width from bark to pith. Results showed that wood juvenility and veneer thickness had an important effect on lathe checks for the rotary-cut veneer. In general, the number of lathe check of the veneer increases with increasing veneer thickness and decrease from pith to bark. Boiling of logs before rotary-cutting could decrease the value of lathe check. The results indicated that boiling of logs at 75 oC for 4 and 8 hours could minimize the number of lathe checks in manufacturing of 1.0, 1.5 and 2.0 mm rotary-cut veneer from juvenile jabon and sengon woods.
Keyword: Boiling, jabon, juvenility, lathe check, sengon, thickness variation