Judul: Rasio Molar dan Konsentrasi Katalis Methyl Ester Sulfonic Acid pada Proses Sintesis Gliseril Ester
Abstrak: Glycerol is a by-product of biodiesel industry production which still can be further processed into more value-added products. The example is the utilization of glycerol by means of esterification between glycerol and oleic acid with methyl ester sulfonic acid (MESA) catalyst, producing glyceril ester. The purpose of this study was to obtain the conditions of esterification with variable factors were molar ratio between oleic acid and glycerol and the concentrations of added MESA catalyst. Before esterification, crude glycerol was purified by adding 5% (v/v) phosphoric acid 85%, producing glycerol with ±80% glycerol content. Furthermore, glycerol was then esterified with supply of nitrogen, at temperature of 180 °C, and the stirring speed of 400 rpm for 90 minutes. The best combination of molar ratio and concentration of catalyst MESA is on ratio molar 0,8:1 (glycerol : oleic acid) with 0,5% added of catalyst MESA. Esterification on that condition produced glyceryl ester with the yield of 79,55%, density 0,940 g/cm3, acid value 44 mg KOH/g sample, viscosity 90 cP (30 oC), kinematic viscosity 49,04 cSt (40 oC), flash point 206 oC, pour point -1,5 oC, and boiling point 105 oC.
Keyword: Bogor Agricultural University (IPB), glyceryl ester, esterification, MESA, glycerol

Judul: Esterifikasi Gliserol Dengan Asam Lemak Sawit Menggunakan Katalis Methyl Ester Sulfonic Acid (Mesa)
Abstrak: Esterifikasi gliserol merupakan salah satu metode yang banyak digunakan untuk mengkonversi gliserol menjadi produk turunan yang bernilai tambah lebih tinggi. Produk yang dihasilkan bersifat terbarukan dan ramah lingkungan sehingga sangat berpotensi dimanfaatkan pada berbagai industri. Penelitian ini bertujuan untuk mengetahui pengaruh jenis asam lemak (asam oleat, asam stearat, asam palmitat, asam miristat) dan lama proses esterifikasi gliserol terhadap sifat fisiko-kimia gliserol ester yang dihasilkan. Penelitian ini terdiri atas dua tahap. Tahap pertama adalah persiapan sampel yang meliputi pemurnian gliserol hasil samping produksi biodiesel olein sawit dan analisis sifat fisiko-kimia sampel gliserol dan katalis MESA. Tahap selanjutnya dilakukan sintesis gliserol ester dengan mereaksikan gliserol 94 % dengan asam oleat, asam stearat, asam palmitat dan asam miristat menggunakan katalis MESA 0,5 % dalam reaktor yang dialiri gas nitrogen 100 cc/menit. Proses esterifikasi dilakukan pada suhu 180°C, dengan kecepatan pengadukan 400 rpm selama 90 menit, 120 menit dan 150 menit. Selanjutnya dilakukan analisis sifat fisiko-kimia gliserol ester yang meliputi rendemen, bilangan asam, densitas, viskositas kinematis, titik nyala, titik tuang dan pencirian spektrum dengan mengunakan FTIR. Sifat-sifat gliserol ester ditentukan oleh karakteristik struktural asam lemak dan gliserol reaktannya. Penggunaan jenis asam lemak yang berbeda dan gliserol 94% pada proses sintesis gliserol ester memberikan pengaruh terhadap sifat fisiko-kimia gliserol ester yang dihasilkan. Rendemen yang dihasilkan semakin besar dengan meningkatnya lama proses esterifikasi dengan nilai tertinggi dihasilkan pada kondisi lama proses 150 menit. Gliserol ester oleat memiliki rendemen 93,1-98,1 % dengan sifat fisiko-kimia sebagai berikut bilangan asam 18,6-24,7 mg KOH/g sampel, densitas 0,910-0,913 g/cm3, viskositas kinematis (100 oC) 7,3-8,8 cSt, titik nyala 202-213 oC, dan titik tuang 0 oC. Gliserol ester stearat memiliki rendemen 94,5-96,1 % dengan sifat fisiko-kimia sebagai berikut bilangan asam 22,7-24,8 mg KOH/g sampel, densitas 0,899-0,903 g/cm3, viskositas kinematis (100 oC) 10,6-11,3 cSt, titik nyala 203-207 oC, dan titik tuang 54-55,5 oC. Gliserol ester palmitat memiliki rendemen 93,8-96 % dengan sifat fisiko kimia sebagai berikut bilangan asam 21,4-24,2 mg KOH/g sampel, densitas 0,907-0,909 g/cm3, viskositas kinematis (100 oC) 10,2-11,2 cSt, titik nyala 197-204 oC, dan titik tuang 54 oC. Gliserol ester miristat memiliki rendemen 92,3-96,0 % dengan sifat fisiko kimia sebagai berikut bilangan asam 20,9-24,1 mg KOH/g sampel, densitas 0,812-0,813 g/cm3, viskositas kinematis (100 oC) 4,2-4,3 cSt, titik nyala 173-179 oC, dan titik tuang 57 oC. Berdasarkan hasil ANOVA dan Duncan pada α = 0,05 menunjukkan bahwa perlakuan jenis asam lemak dan lama proses memberikan pengaruh yang berbeda nyata terhadap sifat fisiko-kimia gliserol ester. Namun interaksi antara kedua perlakuan tersebut tidak berpengaruh nyata. Parameter uji rendemen, bilangan asam, densitas, viskositas kinematis, titik nyala dan titik tuang gliserol ester dari keempat jenis asam lemak menunjukkan nilai yang berbeda nyata. Variasi lama proses esterifikasi hanya berpengaruh pada nilai rendemen dan bilangan asam.
Keyword: gliserol, asam lemak, MESA, esterifikasi, gliserol ester

Judul: Beberapa aspek anatomi alat sirkulasi ruang dada kancil
Abstrak: Telah dilakukan penelitian dengan menggunakan 10 ekor kancil dewasa jantan dan betina dengan tujuan untuk menge- tahui beberapa aspek anatomi alat sirkulasi di dalam ruang dada, meliputi jantung, pembuluh darah yang keluar dan ma- suk jantung serta ukuran-ukuran jantung. Kancil merupakan ruminansia terkecil di dunia, hidup di daerah tropika India, Thailand, Malaysia dan Indonesia bagian barat. Hewan ini dilindungi dan mempunyai prospek yang baik untuk hewan penelitian maupun dibudidayakan. Hasil penelitian menunjukkan bahwa berat jantung rаta-rata adalah 0.69% dari berat rata-rata kancil. Dan ini mirip pada jantung kuda dan anjing. Bentuk jantung lonjong seperti halnya ruminansia. Demikian pula letaknya di dalam ruang dada seperti pada ruminansia dengan adanya Ligamentum sternopericardiacum. Di dalam ventrikel kanan membersit sebuah Musculus (M.) papillaris dari dindingnya dan tiga sampai empat Musculi (Mm.) papillares dari Septum interventriculare. Hanya dua buah Mm. papillares yang berukuran besar dibersitkan dari dinding ventrikel kiri. Percabangan Arteri (A.) coronaria sinistra lebih dominan dari pada A. coronaria dextra. Sedangkan A. sub clavia sinistra dicabangkan langsung dari aorta di dorso- caudal pembersitan Truncus (Tr.) brachiocephalicus…
Keyword: