Judul: Enzymatic Fuel Cell (EFC) used carbon-polyaniline nanoparticle composite bioanoda with amobolized Glucose Oxidase (GOD).
Abstrak: Polyaniline nanoparticles is one of the conductive polymer which used as a matrix in the manufacture bioanoda in biofuell cell applications. Polyaniline was synthesized by the interfacial polymerization method interfacial two-phase system of organic solvent or water. Products such as polyaniline precipitate was collected and purified by filtrating. The powder was characterized by SEM for morphology structure analyzing of polyaniline surface porous, the analyzing result of particle size was 60 nm. Characterization of TEM showed the thinnest layer of the sample, the morphologically formed groups or aggregations such as fiber to the size of the average particle diameter of 60-80 nm. The crystallinity of X-ray diffraction results showed partial or semi-crystalline structure of polyaniline with an average crystal size was 10.4 nm. Generally, the diffraction pattern indicates that extends sequence crystallinity of polyaniline nanocrystal structure. FTIR analysis indicated that the sample obtained was a conductive polyaniline forms or emeraldine salt (ES). Polyaniline addition on carbon paste electrode observed in voltammogram curve. The oxidation peak in potential 0,4 and 0,6 V, and the reduction peak was seen at -0,1 and 0,8, although it does not look so sharp. The using of glucose oxidase enzyme in solution is less economical, because the enzyme can not be used repeatedly. For using efficiently of enzymes in analyzing and production process, the enzyme immobilization technique was developed. Immobilization of enzymes were applied to produce electron. Polyaniline (PANI nanoparticles) with nanoscale structures with small particle size which had a large surface area, used as a matrix be able to bind the enzyme free and able to maintain the stability of the catalytic activity of the enzyme better. It can be used as an electrode material for anode reaction process on the EFC. Enzymatic fuel cell is an electrochemical technology converted chemical energy into electricity. The driving force is called enzymatic fuel cells are from glucose oxidase enzyme as a bio-catalyst. It also has a high specificity for glucose substrate. The observation result by lower concentration of glucose (0.25 M) produced higher current (5,05 μA). Increasing of glucose concentration( 0,50 M; 0,75M; 1 M) decresed of current results (2,45 μA; 1,69 μA; 1,35 μA). The same thing happens on observations of potential, with a low glucose concentration (0.25 M) produces a high voltage value of 60.8 mV, but decrease voltage value (20.3 mV; 20.8 mV; 15.4 mV) with increasing concentrations of glucose (0.50 M, 0.75 M, 1 M) The value obtained maximum power density was 0.39 μW/cm2 at low glucose concentrations (0,25 M) with increasing concentrations of glucose (0.50 M, 0.75 M, 1 M) decresed the value of the power density (0.071 μW/cm2, 0.044 μW/cm2, 0.026 μW/cm2). The glucose with lower concentration can produced maximum electrical by current, voltage and power density. The values obtained maximum power density was 0.39 μW/cm2.
Keyword: polyaniline, electroda bioanoda, dan enzymatic fuel cell

Judul: Penggunaan Grafit Mesopori Berlapis Polianilin sebagai Elektroda pada Microbial Fuel Cell.
Abstrak: Microbial fuel cell is a device can generate electricity from organic components through the microbial catabolism. However, the low power density generated in the MFC system is to be one of the main obstacles. The aims study was to determine the excess graphite-coated mesoporous polyaniline as an electrode in the MFC system. This research was conducted by the method of chemical treatment in the formation of mesoporous structure of the graphite surface and electrochemical polymerization potensiostatic in graphite coating with polyaniline. This study resulted in the highest power density were 0.0059 mW.m-2 in the untreated graphite, 0.6 mW.m-2 in mesoporous graphite, 1.895 mW.m-2 in polyaniline coating and 3.557 mW.m-2 in graphite-coated mesoporous polyaniline. The results showed that formation of mesoporouse treatment on the surface of graphite and polyaniline coating on the graphite surface can increase the power density of the MFC system
Keyword: Bogor Agricultural University (IPB), power density, polyaniline, microbial fuel cell, Anode

Judul: Penyakit Infectious Bovine Rhinotracheitis Infectious Pustular Vulvovaginitis Pada Sapi
Abstrak: Penyakit Infectious Bovine Rhinotracheitis - Infectious Pustular Vulvovaginitis adalah penyakit menular pada sapi selain juga dapat menyerang kerbau, babi, kambing, rusa, antilope dan wild beest. agen penyebabnya adalah virus famili Hervesviridae type 1, mempunyai simetri icosahadral, berinti DNA dan berserabut ganda (double stranded) serta mempunyai nucleocaspid.
Keyword: