Judul: Modifikasi pori Hidroksiapatit dari Tulang Ikan Alu-alu (Sphyraena barracuda)
Abstrak: Hydroxyapatite (HAp) is an important material used in biomedical implants. Currently, porous HAp is widely explored. Large pores surface improve osteoconductivity and adsorption strength. Fish bone can be used as source of HAp since it has high level of calcium and phosphorus in the form of mineral apatite. Therefore, the objective of this study was to modify porous Hap from alu-alu (Sphyraena barracuda) fish bone with starch as the porogen. HAp was formed at temperature of 500, 750, 1000, 1250, 1300, and 1350 ºC. cConcentrations of starch used for porogen were 5, 10, 20, 40, and 60% w/w. X-ray diffraction pattern indicated that HAp was formed in the initial powder fish bone but it had low crystalinity and some impurities. HAp phases with good crystallinity were formed at temperatures of 750–1250 ºC. Electron microscope photographs showed pores with good uniformity was exhibited in the modification using fish bone material with starch concentration of 10%; the sizes were 2.38-3.28 μm.
Keyword: 

Judul: Sintesis Hidroksiapatit Berbasis Limbah Cangkang Keong Sawah (Bellamya javanica) dan Modifikasi Pori Menggunakan Gelatin
Abstrak: Hydroxyapatite is a ceramic material with a structure and composition similar to bone. In this study, hidroxyapatite was synthesized using shell of rice field snail as basic ingredients as a source of calcium (Ca(OH)2) and (NH4)2HPO4 as a source of phosphate. Synthesis method used was the wet method. In the synthesis process, porogen in the form of gelatin was added to increase the pore size. Concentrations of the added gelatin, were 20% and 30%. X-Ray diffraction results showed that the HAp phase has been formed with a fairly high purity. The best pores size resulted from the 30% gelatin concentration, was 0.5-3.98 μm. Infrared spectrum showed that the porogened and nonporogened Hap indicated functional group of HAp constituent
Keyword: shell of rice field snail., pore modification, hydroxyapatite, gelatin

Judul: Analisis faktor dan model persamaan struktural unyuk pengujian model bipolaritas dan dualitas
Abstrak: Perilaku sosial merupakan fenomena yang menarik untuk diamati. Fred Kerlinger, seorang peneliti yang tertarik dengan masalah-masalah sosial, mengamati · perilaku Sistem Liberalis dan Sistem Konservatifpada 530 guru di Texas dan North Carolina [Kerlinger, 1986]. Kerlinger menemukan suatu fenomena dimana masyarakat cenderung menganggap bahwa kedua sistem tersebut adalah dua ha! yang bertolak belakang. Pendapat inilah yang kemudian dikenal sebagai Model Bipolar. Selain itu ada pendapat lain yang mengatakan bahwa kedua sistem merupakan dua ha! yang berdiri sendiri-sendiri dan saling terpisah. Pendapat ini kemudian dikenal sebagai Model Dualitas. Permasalahannya adalah menentukan mana diantara kedua model tersebut yang lebih tepat dalam menjelaskan fenomena yang ada. Hal inilah yang membuat Kerlinger melakukan perbandingan terhadap kedua model dengan cara melakukan pengujian terhadap kedua sistem dengan menggunakan data berupa korelasi variabel­variabel observasi yang mewakili kedua sistem tersebut. Proses pengujian dilakukan dengan menggunakan dua metode analisis, yaitu : Analisis Faktor dan Model Persamaan Struktural. Hasil dengan Analisis Faktor menunjukan bahwa Model Dualitas lebih tepat dalam menjelaskan fenomena yang ada. Hal ini juga didukung oleh Model Persamaan Struktural.
Keyword: