Judul: Combination of Polylactic Acid−Cellulose−Granule Organic Fertilizer as Bioplastic Compostable High Nutrient
Abstrak: Bioplastik ramah lingkungan berpotensi sebagai pengganti plastik konvensional. Pada umumnya bioplastik dibuat dari campuran polimer alam dan polimer sintetik yang sulit terurai sehingga masih menimbulkan polutan mikroplastik. Penelitian ini bertujuan membuat bioplastik paduan dari poliasam laktat (PLA), selulosa dan pupuk organik granula (POG) yang bersifat compostable. Bioplastik dibuat dengan metode solution casting. Jumlah POG yang ditambahkan ke dalam paduan tersebut pada berbagai variasi konsentrasi b/b. Sampel bioplastik A berupa kontrol (0%); B (9%); C (17%); D (23%); dan E (28%). Bioplastik yang dihasilkan memiliki karakteristik sifat mekanik sesuai dengan SNI 7818:2014 pada semua variasi. Bioplastik sampel B memperoleh nilai laju transmisi uap air terendah sebesar 2,41 ×10-6 gcm-1s-1, daya serap airsebesar 4,03%, dan laju degradasi dengan nilai tertinggi sebesar 13,79%. Penambahan POG berbanding lurus dengan laju pertumbuhan dan jumlah daun. Bioplastik paduan PLA−selulosa POG terbukti dapat terurai, ramah lingkungan, dan kandungan unsur hara pada bioplastik sangat baik untuk pertumbuhan tanaman
Keyword: bioplastic, compostable, granulated organic fertilizer, nutrient, polylactic acid

Judul: The Effect of Lignin Consentration on Physical and Mechanical Properties of Bioplastic with Polylactic acid (PLA) based
Abstrak: Plastik dengan sifat biodegradable mudah dihancurkan dan ramah lingkungan. Bioplastik dapat menjadi solusi pengganti plastik karena dapat terurai oleh aktivitas mikroorganisme tanpa menyisakan residu beracun, terbuat dari bahan yang dapat diperbarui, dan dapat menjaga kualitas produk. PLA merupakan polimer alami yang mempunyai sifat biodegradable dalam pembuatan bioplastik. Penambahan lignin dalam pembuatan bioplastik dapat menjadi agen penguat yang baik dalam polimer matriks PLA dan merupakan kandidat yang potensial untuk bahan pembuatan bioplastik. Salah satu sumber lignin adalah tandan kosong kelapa sawit (TKKS). Tujuan dari penelitian ini adalah mengisolasi lignin dari TKKS dan menganalisis sifat fisik dan mekanik bioplastik PLA-lignin. Lignin diperoleh dari proses isolasi lignin dan ultrasonikasi. Bioplastik PLA-lignin dihasilkan dari campuran PLA sebagai matriks dengan penambahan konsentrasi lignin yang berbeda (0%, 2.5%, 5%, 7.5%, 10%). Pembuatan bioplastik dilakukan dengan metode solvent casting. Komposisi lignin dalam TKKS diperoleh dengan uji proksimat. Karakterisasi morfologi lignin dan film bioplastik dianalisis menggunakan scanning electron microcopy (SEM), komponen gugus fungsi dianalisis dengan fourier transform infrared (FTIR), sifat mekanik dianalisis dengan uji mekanik tensile strength, dan laju transmisi uap air pada film bioplastik dianalisis dengan uji WVTR. Bioplastik PLA-lignin menghasilkan adhesi permukaan dan kompatibilitas yang baik ketika ukuran lignin diperkecil. Lignin dengan konsentrasi 5% pada pembuatan bioplastik dapat menghasilkan adhesi permukaan dan kompatibilitas yang lebih baik dibandingkan dengan konsentrasi diatas 5%. Pencampuran PLA dan lignin dapat meningkatkan sifat fisik dan mekanik dari film bioplastik PLA-lignin seperti meningkatkan kuat tarik, elongasi, dan modulus Young dibandingkan dengan bioplastik dari PLA murni., The properties of biodegradable plastic are easily decomposed and ecofriendly. Bioplastics can be a plastic replacement solution because they can be decomposed by microorganism activity without leaving toxic residues, made from renewable materials, and maintaining the product quality. PLA is a natural polymer that has biodegradable properties in bioplastics manufacturing. The addition of lignin can be a good reinforcement agent in PLA matrix polymers and potential candidates in bioplastic manufacturing materials. One of the lignin sources is oil palm empty fruit bunches (OPEFB). The research aims to isolate the lignin from OPEFB and analyze the physical and mechanical properties of PLA-lignin. Lignin from OPEFB is obtained from isolation and ultrasonication process. PLA-lignin-based bioplastics are produced from a mixture of PLA as matrix and lignin in different concentrations (0%, 2.5%, 5%, 7.5%, 10%). The casting method was applied to produce the bioplastics. The composition of lignin in OPEFB was obtained by proximate test. Morphological structure of lignin, bioplastic films and functional group components were analyzed by Scanning Electron Microscopy (SEM) and Fourier Transform Infrared (FTIR), respectively. Mechanical properties and water transmission rate of bioplastic films were analyzed by mechanical tensile strentgh and WVTR test, respectively. PLA-lignin-based bioplastics produce a good compatibility and surface adhesion when the size of lignin is reduced. The 5% of lignin concentration in bioplastics showed that the better compatibility and surface adhesion compared to the higher concentration. Compared to PLA-based bioplastics, PLA-lignin-based bioplastics can increase the mechanical and physical properties, such as tensile strength, elongation, and Young’s modulus.
Keyword: bioplastic, lignin, Polylactic acid (PLA), TKKS, physical and mechanical properties

Judul: Babesiosis pada kuda
Abstrak: Babesiosis pada kuda adalah penyakit menular yang di- sebabkan oleh Babesia caballi dan Babesia equi, yaitu pa- rasit protozoa perusak sel darah yang termasuk dalam genus Babesia. B. equi diduga oleh beberapa ahli termasuk dalam genus Theileria. Karena itu klasifikasi genus Babesia di- bicarakan dan siklus hidup B. caballi dan B. equi diulas. Kuda pada semua umur dapat terserang oleh dua parasite tersebut di atas. Tetapi kuda-kuda yang sudah dewasa (tua) lebih rentan jika dibandingkan dengan kuda-kuda yang masih muda. Kasus-kasus yang paling sering dijumpai adalah kasus-kasus yang bersifat akut walaupun kasus-kasus yang bersifat perakut, subakut dan kronik kadang-kadang terlihat. Serangan oleh parasit Babesia biasanya menyebabkan kerusаkan sel darah merah yang hebat sehingga kuda-kuda yang terserang menderita anemia hebat yang dapat menyebabkan kematian bila tidak segera diobati. Untuk mengatasi hal tersebut perlu dilakukan diagnosis yang tepat dan sedini mungkin. Diagnosis dapat dilakukan dengan cara memeriksa gejala-gejala klinik, preparat ulas darah, inokulasi hewan lain dan dengan mengadakan pemeriksaan secara serologik. Gejala-gejala klinik babesiosis pada kuda yang bersifat akut yang paling sering terlihat, ialah : nafsu makan menurun/hilang, lesu, bulu suram dan tidak mau bergerak. Kuda yang dilepaskan di padang rumput akan mengasingkan diri dan jalan sempoyongan. Faeces yang keluar berwarna cok- lat gelap, diselaputi lendir yang berwarna kekuningan dan urimenya berwarna merah tua. Temperatur tubuh meningkat menjadi 39.5 - 41°C dan pulsus meningkat. Terlihat dispnoe, perdarahan petechi pada mukosa membrana nictitans dan conjunctiva yang lebih pucat dari normal dan juga icteris. Kasus-kasus yang bersifat subakut gejala-gejalanya lebih ringan, tetapi bila tidak segera diobati maka gejala- gejala tersebut secara cepat menjadi hebat. Persendian lutut dan persendian gelang puyuh membengkak dan padanya ter- lihat oedema. Pada abdomen, dada dan kepala juga dapat di- temukan oedema. Gejala-gejala klinik yang terlihat pada kasus kronik adalah penurunan kondisi tubuh kuda secara progresif walaupun diberi makan yang banyak. Perubahan temperatur tidak jelas, nafsu makan berubah-ubah, icterus tidak jelas dan anemia mungkin hanya dapat dideteksi dengan menghitung sel darah merah dan kadar hematocrit…dst
Keyword: