Judul: Arang Aktif Berbahan Baku sebagai Penyerap Polutan Gas dalam Media Kertas
Abstrak: Bamboo as a lignocellulosic material has a good prospects to be processed as an activated carbon due to its availability and low cost. The purpose of this study was to provide activated carbon from bamboo. The activation was done through 2 methods, i.e. chemical activation (KOH immersion) and physical activation (steamed). The quality indikator of the product was characterized by Indonesian National Standard (SNI 06-3730-1995) to be used as paper filler. In this experiment, the best activated carbon was the KOH treatment and steam as the activator at a temperature of 800 °C for 120 minutes. The characteristics include moisture content of 8.14%, volatile matter 9.08%, ash 16.45%, bound carbon 86.29%, benzene adsorption 14.36%, methylene blue adsorption 154.53 mg/g, and iodine adsorption of 240.213 mg/g. The best paper prepared by mixing the activated carbon was resulted from the ratio pulp of activated carbon, 2:1. The paper absorbed gaseous pollutans in a refrigerator namely 0.01%/cm2 para–hidroksibenzaldehida.
Keyword: 

Judul: Arang Aktif Berbahan Dasar Limbah Biomassa Kehutanan sebagai Penjerap Logam Cr, Pb, Cd, dan Pb dalam Limbah Cair Industri
Abstrak: Indonesia merupakan negara yang hampir setengah bagian dari wilayahnya merupakan hutan. Banyaknya wilayah hutan menghasilkan limbah biomassa oleh karena itu, perlu dilakukan pengolahan limbah biomassa sebagai arang aktif untuk menjerap logam berat limbah cair industri. Bahan yang digunakan adalah serbuk gergaji kayu dan limbah bambu yang banyak mengandung lignin dan selulosa. Proses pembuatan arang aktif terdiri atas dua tahap yaitu karbonisasi dan aktivasi. Penelitian ini bertujuan menentukan kondisi terbaik dalam pembuatan arang aktif dari bahan serbuk gergaji kayu jati dan limbah bambu sebagai penjerap logam berat limbah cair industri. Hasil karakterisasi menunjukkan bahwa arang aktif dari serbuk gergaji kayu dan limbah bambu dengan proses karbonisasi pada suhu 350−800 ℃ dan menggunakan aktivasi fisika, kimia, atau keduanya yang telah memenuhi persyaratan SNI 06-3730-1995. Arang aktif dapat menjerap logam berat seperti Cr, Pb, Cd, Hg cukup tinggi dalam limbah cair industri. Arang aktif yang diaktivasi dengan asam diperkirakan memberikan penjerapan logam berat lebih tinggi jika dibandingkan dengan proses aktivasi lainnya. Kata kunci: adsorpsi, arang aktif, limbah biomassa kehutanan, logam berat, Indonesia is a country where almost half of its territory is forest. Many forest areas produce abundant biomass waste. Therefore, it is necessary to process forest biomass waste as activated charcoal to absorb heavy metals from liquid industrial waste. The materials used in this study are wood sawdust and bamboo waste which contain a lot of lignin and cellulose. Activated charcoal production consists of two stages, namely carbonization and activation. This study aims to determine the best conditions in the manufacture of activated charcoal from teak wood sawdust and bamboo waste as heavy metal sorbents for industrial wastewater. The results showed that activated charcoal from wood sawdust and bamboo waste by carbonization process at a temperature of 350−800 and using physical, chemical, or both activations had met the requirements of SNI 06-3730-1995. Activated charcoal can adsorb heavy metals such as Cr, Pb, Cd, Hg which is relatively high in liquid industrial waste. Activated charcoal with acid is estimated to provide higher heavy metal adsorption when compared to other activation processes. Keywords: activated charcoal, adsorption, forestry biomass waste, heavy metals
Keyword: activated charcoal, adsorption, forestry biomass waste, heavy metals

Judul: Infeksi leucocytozzon simondi (Mathis dan Leger, 1910) pada itik
Abstrak: Leucocytozoonosis pada itik adalah penyakit protozoer yang disebabkan oleh parasit darah Leucocytozoon simondi. Protozoa ini ditularkan oleh lalat penghisap darah (Simulium sp.). Di dalam tubuh induk semang antara (vektor) Simulium parasit mengalami tahap gametogoni yang kedua (pembentukan gamet dan pembuahan) dan sporogoni. Pembuahan makrogamet oleh mikrogamet terjadi segera sesudah vektor menghisap darah itik yang mengandung gametosit. Pembuahan menghasilkan zigot yang dapat bergerak (ookinet) yang masuk dinding usus vektor dan kemudian memasuki tahap sporogoni. Tahap sporogoni memerlukan waktu kira-kira 1 minggu (Fallis dan Desser, 1977) untuk menghasilkan sporozoit. Sporozoit bergerak menuju kelenjar ludah vektor, tempat mereka berkumpul. Sporozoit dipindahkan ke dalam tubuh itik pada saat vektor menghisap darah itik. Di dalam tubuh itik, parasit mengalami tahap skizogoni dan tahap gametogoni yang pertama (pembentukan gametosit). Sporozoit memasuki peredaran darah itik dan memasuki sel-sel parenkhim hati membentuk skizon hepatik (Fallis et al., 1974). Setelah 4 6 hari, skizon hepatik dewasa menghasilkan merozoit dan sinsitia. Merozoit dari skizon hepatik memasuki eritrosit dan eritroblas membentuk gametosit bundar, sedangkan sinsitia memasuki sel-sel RES di seluruh tubuh membentuk megaloskizon. Megaloskizon dewasa terbentuk dalam waktu 5 hari di dalam sel-sel itu dan menghasilkan merozoit. Merozoit dari megaloskizon memasuki limfosit dan leukosit lainnya membentuk gametosit memanjang. ...
Keyword: