Judul: Beberapa Aspek Ekologi Burung Wilwo Mycteria cinerea( Raffles) di Segara Anakan-Cilacap
Abstrak: Wilwo Mycteria cinerea (Raffles) tergolong rentan (vulnerabled) dalam Birds to Watch (Collar & Andrew 1988) dan masuk dalam Apendii I CITES. Penyebaran burung Wilwo terbatas hanya di wilayah Asia Tenggara dengan jumlah populasi terbesar berada di Indonesia. Salah satu lokasi yang potensial sebagai habitat burung Wilwo di Indonesia adalah Segara Anakan-Cilacap (Perennou et al. 1994). Penelitian ini bertujuan untuk mengetahui : a) penyebaran lokal dan jumlah populasi; b) perilaku dan aktivitas harian c) karakteristik habitat (lokasi makan dan lokasi istirahat) dan tingkat penggunaan habitat; d) interaksi manusia; d) implikasi terhadap pengelolaan. Dari basil penelitian ini diharapkan menjadi informasi dalam pengelolaan burung Wilwo di habitat aslinya, khususnya di Segara Anakan dan menjadi masukan dalam penentuan status kawasan Segara Anakan.
Keyword: 

Judul: Studi beberapa aspek ekologi kelompok burung Rangkong (Bucirotidae) pada musim tidak berbiak di Resort Rowobendo Taman Nasional Alas Purwo Banyuwangi - Jawa Timur
Abstrak: Kondisi habitat serta bentuk dan tingkat gangguan terhadap habitat kelompok burung rangkong (perburuan liar, konversi lahan dan perusakan hutan alam) berpengaruh terhadap penyebaran dan kelimpahannya. Penelitian bertujuan untuk mengetahui penyebaran lokal, dugaan kelimpahan populasi serta karakteristik habitat kelompok burung rangkong yang berkaitan dengan ketersediaan pakan, tempat berjemur, bertengger, berlin- dung dan bersarang di hutan alam sekitar padang perumput- an Sadengan Resort Rowobendo Taman Nasional. Alas Purwo. Data mengenai penyebaran lokal diperoleh melalui orientasi lapang dan informasi dari petugas maupun masyarakat sekitar kawasan. Data kelimpahan populasi dan aktivitas harian kelompok burung rangkong diperoleh melalui pengamatan dengan menggunakan metode Concen- tration Count pada pohon-pohon penghasil pakan rangkong. Data vegetasi di habitat kelompok burung rangkong diperoleh dengan menggunakan metode petak tungggal dengan membuat plot-plot contoh secara purposive pada habitat rangkong. Selain itu dibuat plot berukuran 50 m x 20 πι untuk menganalisis komponen habitat....
Keyword: 

Judul: Enhancement of photon absorbtion on BaxSr1-xTiO3 thin films semiconductor using photonic crystals.
Abstrak: In this research, has been conducted BaxSr1-xTiO3 (BST) thin films manufacturing for mole fraction x = 0.25, 0.35, 0.45, and 0.55; and concentration of 1 molar using chemical solution depositon (CSD) method. The materials, which are used in this research, are barium acetate [Ba(CH3COO)2, 99%], strontium acetate [Sr(CH3COO)2, 99%], titanium isopropoxide [Ti(C12O4H28), 97.999%], gallium trioxide [Ga2O3], 2-methoxyethanol [H3COOCH2CH2OH, 99%] and 1 x 1 cm of transparent conductive oxide (TCO) glass as substrate. Two BST thin films are made that for BST thin films which are doped by 10% galium (BGST) as p-type layer and pure BST solution as n-type. BST solution is made by reacting barium acetate [Ba(CH3COO)2, 99%], strontium acetate [Sr(CH3COO)2, 99%] and titanium isopropoxide [Ti(C12O4H28)] into 2-methoxyethanol solvent [H3COOCH2CH2OH, 99%] in accordance with mass gram for each x value. While, BGST solution is made in the same way as BST solution, plus adding gallium at 10% of the mass of BST. Once all materials are reacted, then vibrated using ultrasonic for 90 minutes, and followed by coating BGST / BST on the TCO substrate. Once the layer is formed, then annealed for 15 hours at temperature of 500 °C with increasing rate of 1.67 oC/minute. Characterizations of BST thin films with or without photonic crystals include the absorbance and transmittance in the visible light spectrum, as well as the electrical photoconductivity characterizations. From BST thin films without photonic crystals indicate that our thin films have light absorption area on almost the entire range of the visible light spectrum even to the infrared range with absorption value over than 67.6%, in addition, it can be seen that the maximum absorbance of BST thin films for all mole fractions lie in blue to green light spectrum region, 457 nm ≤ λ ≤ 570 nm and the minimum in yellow to red light spectrum region, 570 nm ≤ λ ≤ 678 nm. The largest absorbance is found at x = 0.25 with average absorbance value of 92.04% and maximum and minimum absorbance peaks at wavelength of 500.89 and 657.72 nm, respectively. At x = 0.35, average absorbance value decreased to 83.55% with maximum and minimum peaks at 505.73 and 613.68 nm, respectively. Then increased to 91.16% at x = 0.45 with maximum and minimum peaks at 506.04 and 618.56 nm, respectively. At x = 0.55, average absorbance value decreased to 80.12% with maximum and minimum peaks at 507.85 and 608.79 nm, respectively. Moreover, it can be seen that the addition of barium mole fraction leads to wider maximum absorbance or minimum transmittance peaks and narrower minimum absorbance or maximum transmittance peaks in the same range of the green and blue & red light spectrums, respectively. BST thin films with photonic crystals show increasing in absorption for all x values in the range of 3.04 into 13.33%. At x = 0.25, average absorbance percentage increased 3.96% from 92.4 into 95.68%, for x = 0.35 average percentage increased 7.07% into 89.45 from 83.55%. Furthermore, average absorbance of BST thin films at x = 0.45 increased 3.04% from 91.16 into 93.93% and x = 0.55 has
Keyword: