Judul: Sulfonation of waste cassava to produce superabsorbent.
Abstrak: Onggok is a waste product of tapioca industries which has low economical value. The aim of this research is to find a way to increase the added value of onggok by transforming it into a superabsorbent. The making of superabsorbent from onggok was preparated through sulfonation and preceded by oxidation. In this experiment the oxidation was carried out with 3 levels of reaction time, i.e. 210, 270, and 330 minutes. While sulfonation was carried out with 3 levels of concentration of NaHSO3, that are 15, 20 and 35 g and 3 levels of sulfonation time of 120, 180 and 240 minutes. The absorption capacity of the product was evaluated through their absorption capacity, carried out by immersing the product for 4 hours in a known volume of distill water. Its absorptive capacity is calculated based on its sample weight increases due to water absorption. The results show that the highest absorption capacity was indicated by the sample with 270 minutes of oxidation, 240 minutes of sulfonation time and 20 g of NaHSO3. Its absorption capacity was 38.54 g/g. The result of FTIR spectroscopic study and sulfur analysis indicated that bisulfite ions are incorporated into cellulose molecules of onggok
Keyword: 

Judul: Sintesis superabsorben melalui kopolimerisasi pencangkokan dan penautan silang onggok dengan akrilamida
Abstrak: Solid wastes of tapioca is known as onggok. This study is aiming to see a possibility to increase the value of onggok by transforming it into a superabsorbent polymer through grafting cross-linking copolymerization of acrylamide as a monomer, N,N’-methylenebisacrylamide as a cross-linker, and ammonium persulfate as an initiator. Onggok was used as a backbone in grafting and cross-linking copolymerization. The copolymerization was conducted at 70oC for 3 hours and the copolymer was saponified with NaOH 1M for 2 hours. Water absorbency capacity of the saponified copolymer as well as unsaponified copolymer thereafter were measured. The saponified copolymer showed significant difference in absorbency capacity, i.e. 28.92 g/g and 1040.08 g/g, for unsaponified and saponified copolymer, repectively. This was obtained from copolymer composed of 25% onggok, 75% acrylamide, 25 mg N,N’-methylenebisacrylamide, and 250 mg ammonium persulfate. The occurrence of grafting cross-linking copolymer was confirmed by fourier transformed infrared spectra, where it was found to exhibit all characteristic bands of both polysaccharide fractions of onggok and acrylamides units.
Keyword: 

Judul: Kecepatan Terbang Burung Merpati Balap Lokal (Tipe Tinggian)
Abstrak: Penelitian ini dilaksanakan di wilayah Jakarta, tepatnya Rawamangun Selatan, Gg. Kana Tanah Merah Lama, Jakarta Timur. Ternak yang digunakan dalam penelitian ini adalah 46 ekor burung merpati lokal terdiri dari 23 pasang burung merpati jantan dan betina yang berumur 9 bulan samapi 12 bulan. Jarak melepaskan burung merpati pada penelitian ini sekitar 4 km. Waktu terbang diukur dengan cara sewaktu burung merpati dilepas dari tempat diterbangkan, joki yang melepas memberi aba-aba melalui handphone kepada joki yang berada di kandang bahwa burung merpati siap dilepas. Peubah yang diamati adalah karakteristik kualitatif, kecepatan terbang, pola terbang dan ukuran tubuh burung merpati balap tipe tinggian. Data disajikan secara deskriptif tentang karakteristik kualitatif, kecepatan terbang, pola terbang dan ukuran tubuh burung merpati balap tipe tinggian. Rataan, simpangan baku dan koefisien keragamannya dihitung untuk mengetahui keragaman dan keseragaman pada ukuran tubuh burung merpati balap tipe tinggian dengan menggunakan rumus koefisien keragaman (Walpole, 1992). Kecepatan terbang burung merpati balap tipe tinggian dilakukan selama tiga kali giring. Kecepatan antar periode giring diuji dengan uji t dengan menggunakan rumus (Walpole, 1992). Nilai koefisien keragaman (KK) dari yang paling besar sampai paling kecil adalah lebar pangkal ekor (12,37%), panjang bulu ekor (10,27%), panjang punggung (9,43%), lebar bulu ekor (9,27%), bobot badan (8,15%), dalam dada (7,41%), panjang bulu sayap (7,17%), lingkar dada (3,62%) dan lebar dada (3,48%). Berdasarkan urutan tersebut, maka ukuran tubuh yang paling beragam adalah lebar pangkal ekordan yang paling seragam adalah lebar dada. Lebar pangkal ekor dapat dijadikan penentu seleksi burung merpati balap tipe tinggian karena berpengaruh nyata negatif (P<0,05) terhadap kecepatan terbang burung merpati balap tipe tinggian. Kecepatan terbang merpati tidak berbeda nyata antara periode giring satu dengan periode giring yang lain, hal ini menunjukan bahwa setelah burung merpati dilatih maka kemampuan terbangnya cenderung stabil. Hasil analisis korelasi untuk lingkar dada, lebar dada, panjang punggung, panjang bulu sayap dan panjang bulu ekor tidak menunjukkan hubungan yang nyata dengan kecepatan terbang. Bobot badan, dalam dada, lebar bulu ekor dan lebar pangkal ekor menunjukkan hubungan yang nyata dengan kecepatan terbang. Pada pengamatan di lapang diperoleh beberapa pola terbang burung merpati balap tinggian yaitu 1). Pola berputar lalu terbang lurus (burung merpati warna kelabu dan tritis) dengan kecepatan rata-rata masing-masing 18,69 dan 18,65 m/detik, 2). Pola langsung terbang lurus (burung merpati warna megan, hitam, gambir dan megan 2). Dengan kecepatan rata-rata masing-masing 23,62; 25,39; 28,88 dan 29,18 m/detik, 3). Terbang lalu ditengah perjalanan dahulu setelah itu terbang lurus (burung merpati warna blorok, tritis megan, blantong dan kelabu selap) dengan kecepatan rata-rata masing-masing 20,18; 20,21; 21,94 dan 21,94 m/detik. Burung merpati balap tinggian yang memiliki kecepatan terbang tertinggi (29,18 m/detik) mempunyai pola terbang langsung terbang lurus, bobot badan (330 g), lingkar dada (22 cm), dalam dada (5,4 cm), lebar dada (8 cm), panjang punggung (12 cm), panjang bulu sayap (18 cm), lebar bulu ekor (4,4 cm), lebar pangkal ekor (3,5 cm) dan panjang bulu ekor (11 cm).
Keyword: high racing pigeon, flight pattern, flight speed, quantitative characterstics