Judul: Optimization of Self Healing Concrete Parameters using Experimental Design Taguchi Method
Abstrak: Pengembangan self healing concrete dilaksanakan untuk memperbaiki keretakkan dan mengurangi biaya perawatan. Namun, percobaan membutuhkan banyak variasi dari setiap parameter sehingga meningkatkan biaya percobaan. Metode Taguchi digunakan dalam desain eksperimen untuk mendapatkan variasi parameter optimal serta mengurangi biaya percobaan. Tahapan penelitian ini adalah pengumpulan data sekunder peningkatan kekuatan tekan, pengujian metode Taguchi, penentuan parameter kontribusi menggunakan ANOVA, dan model estimasi yang dikembangkan. Metode Taguchi menghasilkan variasi yang optimal, yaitu jenis bakteri Bacillus subtilis, konsentrasi bakteri sebesar 105 sel/ml, pengaplikasian bakteri secara encapsulation, dan waktu curing 28 hari. Konsentrasi bakteri memiliki nilai yang sangat signifikan dengan kontribusi masing-masing sebesar 82,94%, 78,90%, dan 74,36% dalam analisis parameter 2, 3, dan 4. Nilai error terkecil diperoleh dalam analisis percobaan 3 parameter dengan nilai 2,99%. Pemodelan self healing concrete diperoleh dua persamaan yang terdiri dari direct mixing dan encapsulation yang memiliki koefisien determinasi 0,89 dan 0,82., The development of self-healing concrete is carried out to repair cracks and reduce maintenance costs. However, the experiment requires a lot of variation of each parameter thus increasing the cost of the experiment. The Taguchi method is used in experimental design to obtain optimal parameter variations as well as reduce experiment costs. The stages of this study are the collection of secondary data on compressive strength improvement, testing of the Taguchi method, determination of contribution parameters using ANOVA, and the developed estimation model. The Taguchi method produces the optimal variety, which is the type of bacteria is Bacillus subtilis bacteria, bacterial concentrations of 105 cells/mL, application of bacteria by encapsulation, and curing time of 28 days. The concentration of bacteria has a very significant value with contributions of 82.94%, 78.90%, and 74.36% respectively in the analysis of parameters 2, 3, and 4. The smallest error value was obtained in the analysis of the experiment of 3 parameters with a value of 2.99%. Self-healing concrete modeling obtained two equations consisting of direct mixing and encapsulation which have coefficients of determination of 0.89 and 0.82.
Keyword: crack, modeling, parameter contribution, SHC, Taguchi

Judul: Utilization of Soybeans as Bio-Catalyst in Calcite Precipitation Method for Repairing Cracks in Concrete
Abstrak: Beton merupakan material yang memiliki kuat tekan tinggi tetapi memiliki kuat tarik yang lebih rendah sehingga beton seringkali retak. Metode perbaikan mulai beralih dari cara konvensional kepada konsep self-healing concrete yang melibatkan pengendapan CaCO3. Pengendapan CaCO3 dapat dilakukan dengan metode enzymatically-induce carbonate precipitation (EICP) melalui kombinasi urease, urea, dan CaCl2 menjadi larutan. Penelitian ini menggunakan ekstrak kedelai sebagai bahan pengganti enzim urease murni. Variasi kadar konsentrasi tepung kedelai yang digunakan sebagai larutan injeksi yaitu variasi kadar tepung kedelai 15 g/L karena menghasilkan massa kalsit optimum sebesar 2.62 gram. Terjadi peningkatan kuat tekan pada beton retak yang diinjeksi (BI) terhadap beton retak (BR). Selain itu, terjadi penurunan nilai permeabilitas dan porositas seiring dengan jumlah injeksi yang dilakukan. Peningkatan kuat tekan, penurunan permeabilitas, dan penurunan porositas pada beton ini disebabkan karena adanya deposisi CaCO3 pada beton yang mampu menutupi pori-pori serta celah keretakan pada beton, Concrete is a material that has a high compressive strength but has a lower tensile strength so that the concrete often cracks. The repair method began to shift from the conventional method to the concept of self-healing concrete which involves the deposition of CaCO3. Precipitation of CaCO3 can be done by enzymatically-induced carbonate precipitation (EICP) method through a combination of urease, urea, and CaCl2 into a solution. This research used soybean extract as a substitute for pure urease enzyme. Variations in the concentration of soybean flour used as injection solution were variations in the content of soybean flour 15 g/L because it produced an optimum calcite mass of 2.62 grams. There was an increase in the compressive strength of injected cracked concrete (BI) against cracked concrete (BR). In addition, there was a decrease in the value of permeability and porosity along with the number of injections carried out. The increase in compressive strength, decrease in permeability, and decrease in porosity in concrete is due to CaCO3 deposition in the concrete which is able to cover the pores and cracks in the concrete
Keyword: Beton, CaCO3, kuat tekan, permeabilitas, porositas, Concrete, compressive strength, permeability, porosity

Judul: Molecular Systematics of Tree Frog Nyctimystes infrafrenatus infrafrenatus (Tyler 1971) from Papua and Moluccas
Abstrak: Nyctimystes infrafrenatus memiliki permasalahan taksonomi yang cukup kompleks. Spesies ini pertama kali dideskripsikan dengan nama Hyla infrafrenata. Kemudian berdasarkan karakter morfologinya spesies ini dikelompokkan ke dalam genus Litoria dan lebih dikenal dengan nama Litoria infrafrenata namun hasil analisis filogenetika molekuler menempatkan spesies ini pada clade Nyctimystes. Nyctimystes infrafrenatus memiliki dua subspesies yaitu Nyctimystes infrafrenatus infrafrenatus dan Nyctimystes infrafrenatus militarius. Subspesies N. infrafrenatus militarius memiliki distribusi yang terbatas pada Kepulauan Bismarck, Papua New Guinea sedangkan N. infrafrenatus infrafrenatus distribusinya mencakup wilayah utara Sulawesi, Kepulauan Maluku, Pulau Timor, Papua, Australia hingga Kepulauan Solomon. Distribusi yang luas tersebut dapat memunculkan fenomena kriptik spesies. Populasi spesies ini di wilayah Indonesia mewakili dua subregion zoogeografi yang memiliki sejarah pembentukan wilayah yang berbeda yaitu Papua dan Wallacea. Lautan merupakan barrier utama distribusi hewan amfibi karena rendahnya toleransi amfibi terhadap salinitas. Hal ini menimbulkan kemungkinan bahwa N. infrafrenatus infrafrenatus populasi Maluku berbeda dari populasi Papua. Penelitian sebelumnya tentang morfometrik menunjukkan adanya perbedaan ukuran kaki belakang individu betina antara populasi N. infrafrenatus infrafrenatus Papua dan Maluku. Temuan tersebut perlu ditelusuri lebih lanjut dengan pendekatan molekuler. Penelitian ini bertujuan untuk mengevaluasi sistematika N. infrafrenatus infrafrenatus dari Papua dan Maluku. Penanda genetik yang digunakan pada analisis molekuler adalah sekuens gen 16S rRNA. Hasil pensejajaran sekuens ini digunakan untuk rekonstruksi pohon filogenetik, mengestimasi waktu divergensi dan jarak genetik kedua populasi tersebut. Hasil rekonstruksi pohon filogenetik menempatkan semua sampel N. infrafrenatus infrafrenatus pada satu clade monofiletik (MLBS 99%, BPP= 100%). Clade ini kemudian membentuk dua subclade yaitu subclade A yang terdiri atas sampel-sampel dari Papua dan Australia (subclade Papua) serta subclade B yang terdiri dari sampel-sampel Halmahera dan Ternate (subclade Maluku). Hasil estimasi waktu divergensi menunjukkan bahwa kedua subclade tersebut mulai terpisah sejak 6.03 juta tahun lalu (jtl). Jarak genetik antara kedua subclade (2,3,- 4,2%) berada pada threshold beda spesies 3%. Sampel Australia dan populasi Papua mewakili “the true” N. infrafrenatus sedangkan populasi Maluku dengan jarak genetik 3,9-4,2% dengan sampel Australia terindikasi kuat secara genetik merupakan spesies yang berbeda. Berdasarkan artikel 23 ICZN, nama Nyctimystes tennuigranulatus dapat digunakan terutama untuk populasi Maluku bagian utara. Analisis lebih lanjut secara morfologi, akustik dan ekologi yang melibatkan sampel dari Ambon diperlukan untuk menentukan status taksonomi populasi Maluku secara menyeluruh.
Keyword: 16S rRNA, Moluccas, molecular systematics, Nyctimystes, Papua