Judul: Hubungan Pola Komunikasi Organisasi Dengan  Motivasi Kerja Pegawai (Kasus Di Universitas  Pembangunm Nasionai "Veteran" Jakarta)
Abstrak: Faktor personal menjadi salah satu faktor penyebab perbedaan perilaku komunikasi antar individu yang akan membentuk pola komunikasi Pola, Jdim serta kepuasan komunikasi organisasi yang mendukung diperlukan sebagai penumbuh motivasi kerja pegawai. Penelitian ini menganalisis hubungan pola komunikasi dengan motivasi kerja Pegawai (Kasus di UPN "Veteran" Jakarta).
Keyword: 

Judul: Faktor-faktor Komunikasi yang Berhubungan dengan Motivasi untuk Meningkatkan Kinerja Organisasi (Studi Kasus di Pusdiklat Pegawai Departemen Komunikasi dan Informatika Jakarta Barat)
Abstrak: This research attempts to answer the questions of communication factors such as characteristics of personality, human relations, communication organizational have correlation with officials motivation to improvement organization activity. This research was done using survey research method and analyzed of software SPSS version 12.00, statistical method namely Chi-Square and Spearman-Rank test to see correlation among variables. The number of the respondent is 85 officials in Pusdiklat Kominfo. Reliability of instrument has realiable with value Rcount 0,774 (human relations), 0,710 (communication organizational) dan 0,895 (motivation) more high than Rcritical 0,247. The result of this research are (1) There is positive significant correlation between characteristics of personality (education, functionary) with motivation (self actualization, expectation) and negative significant correlation between level of position and physiological needs (2)There is significant correlation between human relations with officials motivation (3) There is significant correlation between organization communication and officials motivation.
Keyword: 

Judul: Pembuatan Film Tipis Cu2ZnSnS4 sebagai Lapisan Penyerap Cahaya pada Sel Surya Menggunakan Metode Elektrodeposisi
Abstrak: Thin film of Cu2ZnSnS4 (CZTS) is an alternative semiconductor used as light absorber layer on solar cell. CZTS can replace silicon that commonly used as commercial semiconductor. The advantage of using CZTS as absorber layer is due to the abundance of its chemical composer on earth, and its high value of absorption coefficient. The absorber layer was made by using electrodeposition method on ITO glass substrates. The films were deposited at room temperature using potentiostatic mode with a potential of –1.05 V for 30, 45, and 60 minutes. After that, the films were annealed at two different temperatures, 180 ºC and 500 °C, for 45 minutes in N2/H2S atmosphere. Based on X-ray diffraction analysis, the polycrystalline thin film obtained fall into kesterite crystal phase. This type of crystal was obtained when the CZTS was annealed at 500 °C in H2S/N2 atmosphere. The value of optical band gap energy for the CZTS thin film was 2.2 eV with the film thickness about 1.228–6.366 μm. The sample of CZTS with electrodeposition time of 45 minutes and annealing temperature of 500 °C showed the best result and in conformity with absorber layers criteria for solar cells.
Keyword: semiconductor, ITO glass, CZTS thin film, electrodeposition