Judul: Sifat Fisis, Mekanis dan Finishing Kayu Mindi (Melia azedarach Linn.) Termodifikasi Silikon Emulsi
Abstrak: Kayu mindi (Melia azedarach Linn.) merupakan kayu cepat tumbuh yang mulai banyak ditanam masyarakat. Oleh karena itu teknik pengolahannya perlu dikembangkan. Penelitian ini bertujuan untuk menguji sifat fisis, mekanis dan finishing kayu mindi setelah perlakuan silikon emulsi dengan metode impregnasi vakum-tekan serta kombinasi perendaman dan pemanasan oven. Impregnasi silikon emulsi dilakukan dengan vakum 0.1 atm (1 jam) dilanjutkan pemberian tekanan 5 kg/cm2 (1 jam). Adapun perendaman silikon emulsi dilakukan selama 48 jam dilanjutkan pemanasan oven dengan variasi suhu 60 ᵒC (48 jam), 150 ᵒC (5 jam) dan 200 ᵒC (5 jam). Selanjutnya dilakukan pengujian sifat fisis, mekanis dan finishing kayu mindi. Hasil penelitian menunjukan bahwa perlakuan silikon emulsi dapat meningkatkan sifat fisis, mekanis dan finishing kayu mindi. Kadar air dan stabilitas dimensi kayu mindi setelah perlakuan silikon emulsi nyata lebih baik daripada kayu mindi tanpa perlakuan. Kerapatan kayu mindi setelah perlakuan silikon emulsi dengan metode impregnasi vakum-tekan serta kombinasi perendaman-pemanasan 200 ᵒC meningkat 16.33%. Impregnasi silikon emulsi meningkatkan Modulus of elasticity dan Modulus of rupture kayu mindi menjadi 1.1 kali dan 1.3 kali dari kontrol. Sudut kontak kayu mindi setelah perlakuan silikon emulsi lebih rendah dibanding kontrol yang menunjukan sifat finishing menjadi lebih baik.
Keyword: Impregnasi, kayu mindi, pemanasan, silikon emulsi

Judul: Sifat Fisis, Sifat Mekanis, dan Sifat Finishing Kayu Mindi (Melia azedarach L.) setelah Perlakuan Pemanasan
Abstrak: Mindi (Melia azedarach L.) is a fast-growing wood species which is quite prospective for wood industry but it should be supported with proper technology application to produce good quality wood products. This research was done to evaluate the effect of heating treatment with various times and temperatures on the physical, mechanical, and finishing properties of mindi wood. Wood heating in oven and oil were at temperatures of 120 °C, 150 °C, and 180 °C for 2, 5, and 8 hours. The results showed that the heating wood in various conditions increased wood dimensional stability in both tangensial and radial directions. The moisture content, density, and dimensional stability of wood heated in oil were better than those heated in oven. Heating at 180 °C reduced the mechanical properties of mindi wood. The finishing test with cross cut methode showed that the oven heating did not affect finishing quality, except the 8 hours oil heating at 180 °C that reduced the finishing quality.
Keyword: physical properties, mindi wood, mechanical properties, heat treatment, finishing peroperties

Judul: Hog Cholera
Abstrak: Hog Cholera adalah penyakit pada babi yang sangat infeksius, ditandai dengan penyebarannya yang cepat. Penyebabnya adalah virus dari famili Togaviridae, genus Pestivirus berintikan asm ribonukleat, beruntai tunggal, mempunyai selubung yang mengandung lipida dan "duri-duri" yang mengandung glikoprotein. Penularan dari babi dapat secara vertikal maupun secara horisontal. Secara geographis, penyakit ini9 sudah ada dihampir seluruh dunia, hanya beberapa negara yang relatof bebas HC.
Keyword: