Judul: Sintesis α-Fe2O3 menggunakan metode sol gel
Abstrak: In this reseach was succeeded make powder α-Fe2O3 with particle size 202.64 nm. Synthesis using Sol-Gel method with SiO2 coating derived from Si(OC2H5)4 at temperature of 750 oC for 5 hours. Characterization XRD prove that sample form is α-Fe2O3 (11 peaks) and β-Fe2O3 (2 peaks) with crystal size 20.69125 nm and crystallization 44 %. The cystal structure of α-Fe2O3 is rhombohedral and β-Fe2O3 is hexsagonal. Optic characterization show that the sample absorbing light at wavelength less than 480 nm. Bandgap energy of the optical characterization measurments is 2.74 eV.
Keyword: α-Fe2O3, annealing, bandgap energy, sol-gel, crystal structure.

Judul: Synthesis and Characterization FeTiO3 dopped Strontium (II) Acetate (Sr(CH3COO)2)
Abstrak: Film FeTiO3 dengan variasi konsentrasi pendadah Stronsium (II) Asetat (0%, 0.5%, 1%, 1,5%) telah berhasil dibuat di atas substrat silikon (100) tipe-p menggunakan metode Chemical Solution Deposition (CSD) dengan bantuan teknik spin coating dengan kecepatan putar 8000 rpm. Film FeTiO3 di-annealing dengan kelajuan suhu sebesar 1,67oC dan pada suhu 850 oC ditahan selama 8 jam, lalu mengikuti proses pendinginan suhu kamar selama 12 jam. Film FeTiO3 yang didadah dengan Stronsium (II) Asetat dikarakterisasi menggunakan spektrofotometer UV-Vis dan XRD sehingga menghasilkan nilai energi bandgap secara berturut-turut sebesar 4,14 eV; 3,98 eV; 3,13 eV; 3,08 eV. Analisis data XRD menggunakan metode Cramer-Cohen menghasilkan nilai parameter kisi a=b sebesar 5,0934 Å; 5,1379 Å; 5,1657 Å; dan 5,1779 Å serta parameter kisi c yaitu 14,0787 Å; 14,3008 Å; 14,4038 Å; dan 14,4289 Å, dengan struktur kristal hexagonal. Kata kunci: bandgap, CSD, FeTiO3, spin coating, parameter kisi, FeTiO3 film with the variation of Strontium (II) Acetate (0%; 0,5%;1%;1,5%) has been successfully made on silicon substrate (100) p-type using the Chemical Solution Deposition (CSD) method with the spin coating technique with a rotational speed 8000 rpm. FeTiO3 film was annealed with an increase in temperature of 1,67oC and at 850oC for 8 hours, then follow the cooling process to room temperature for 12 hours. FeTiO3 film with Strontium (II) Acetate doped was characterization using a spectrophotometer UV-Vis and XRD so that the bandgap energy value was 4,14 eV; 3,98 eV; 3,13 eV; 3,08 eV. XRD data analysis using the Cramer-Cohen method resulted in lattice parameter values a=b of 5,0934 Å; 5,1379 Å; 5,1657 Å; and 5,1779 Å in addition for lattice parameter c with a hexagonal crystal structure are 14,0787 Å; 14,3008 Å; 14,4038; and 14,4289 Å. Keywords: band gap, CSD, FeTiO3, spin coating, lattice parameter
Keyword: bandgap, CSD, FeTiO3, spin coating, lattice parameter

Judul: Distribusi spasial kima (Tridacnidae) dan hubungannya dengan kondisi ekologis terumbu karang di Kepulauan Karimunjawa, Jawa Tengah
Abstrak: Indonesia dengan luas lautan 6.87 juta km² memiliki keanekaragaman hayati laut yang kaya, terutama ekosistem terumbu karang dengan luas kurang lebih 50.000 km². Berdasarkan perkiraan, 70 % terumbu karang dunia akan rusak dan hilang pada 10 sampai 40 tahun mendatang akibat dari perubahan iklim global. Kima dari famili Tridacnidae sebagai salah satu penyusun utama terumbu karang merupakan jenis bivalvia berukuran relatif besar yang distribusinya terbatas hanya di daerah ekosistem terumbu karang Indo-Pasifik. Pada beberapa dekade terakhir, kima telah mengalami eksploitasi besar-besaran. Eksploitasi kima secara besar-besaran dapat menyebabkan kepunahan biota kima tersebut dan mengakibatkan kerusakan terumbu karang yang hidup juga (Pasaribu, 1988). Oleh karena itu pemerintah mengumumkan ketujuh kima yang ada di Indonesia sebagai biota laut yang dilindungi berdasarkan Surat Keputusan Menteri Kehutanan no. 12/Kpts - II/1987. Tiga spesies kima (Tridacna gigas, T. derasa dan Hippopus porcellanus) yang dahulu melimpah di seluruh Indonesia kini telah berkurang secara mencolok. Penelitian singkat atas populasi kima di Kepulauan Seribu dan Kepulauan Karimunjawa menunjukkan bahwa T. gigas dan T. derasa telah punah. Spesies­ spesies lainnya, T.crocea, T. squamosa dan Hhippopus, masih ditemukan namun telah mengalami penurunan populasi.
Keyword: