Judul: Penentuan Komposisi Campuran Cat Bakar Akrilat untuk Aplikasi pada Media Plastik Polipropilena
Abstrak: Car parts that need paint coating consist of 2 main substances, metal and plastic. Metal car body needs acrylic paint types whereas polypropylene plastic car bumper use polyurethane paint, so color matching needs to be carried out between the two materials. In terms of price, as well, polyurethane paint is more expensive than acrylic paint. Based on these conditions, application of acrylic paints onto both metal and plastic surfaces has been studied to reduce production costs and produce better color closeness between the two parts of the car. Acrylic paint was mixed with hardener, which is commonly added in polyurethane paints, with varied ratios and was tested for its coating qualities with hardness and adhesion on both types of materials as the test parameters. The proximity of colors had also been tested for grape red pearl metallic color. The results showed that the appropriate compositions for hardness test were 1:0.25 and 1:0.20 ratios of paint and hardener material, the test used Mitsubishi type HB up to F pencil size. The composition that met the adhesive power test were 1:0.35, 1:0.30, and 1:0.25 ratios of paint and hardener material, all three had adhesion power of 100/100 unpeeled paint coating. Color matching test indicated that the appropriate composition was 1:0.25 ratio of paint and hardener material with delta E value <0.5. It can be concluded that the composition producing painting quality that fulfil the three parameters are paint-hardener material 1:0.25.
Keyword: 

Judul: Pengaruh komposisi katalisator dan waktu pembuatan terhadap sifat mekanik resin poliester
Abstrak: Penelitian ini bertujuan untuk mengetahui komposisi katalisator yang tepat yang memberikan sifat mekanik resin poliester optimal yang disesuaikan dengan waktu pembuatan. Bahan baku resin poliester yang digunakan jenis Palatal P4N. Pembuatan spesimen uji dikerjakan di PT. Marine Specialist (Marspec), Tanjung Priok - Jakarta pada bulan Desember 1994. Pengujian spesimen uji terdiri dari uji tekan, uji tarik dan uji lentur yang semuanya dilakukan pada bulan Juni 1995. Pengujian tekan dan lentur dikerjakan di Lab. Keteknikan Kayu, Jurusan Teknologi Hasil Hutan, Fakultas Kehutanan IPB dan pengujian tarik dilakukan di Lab. Bahan dan Alat Penangkapan Ikan, Jurusan Pemanfaatan Sumberdaya Perikanan, Fakultas Perikanan IPB. Metode penelitian yang digunakan yaitu eksperimen laboratorium (laboratorium experiment). Hasil penelitian menunjukkan bahwa resin poliester yang telah membeku memiliki sifat keras, getas dan berat jenis yang lebih besar dari berat jenis air tawar (1,000 gr/cm³) dan air laut (1,025 gr/cm³). Karakteristik mekanik resin poliester dipengaruhi oleh faktor penyusun bahan (gaya ikat antar molekul dan berat molekul polimer), faktor lingkungan (suhu udara dan kelembaban) dan faktor lain yang terjadi ketika resin poliester dilaminasi. Penggunaan katalisator mengakibatkan terjadinya penurunan Energi Aktifasi bahan, sehingga terjadi kesetimbangan kimia (reaksi bersifat eksoterm). Hasil perhitungan nilai rata-rata tegangan tekan menunjukkan selang 535,93- 770,84 kgf/cm² dengan nilai rata-rata total 609,29 kgf/cm². Hasil analisa keragaman menunjukkan bahwa kombinasi perlakuan waktu dan komposisi katalisator berpengaruh sangat nyata. Hasil uji lanjut BNT menunjukkan bahwa beda perlakuan T2K1 dengan T2K3 berpengaruh paling besar terhadap nilai rata-rata tegangan tekan. Hasil perhitungan nilai rata-rata tegangan tarik menunjukkan selang 353,90-540,95 kgf/cm² dengan nilai rata-rata total 437,11 kgf/cm². Hasil perhitungan nilai rata-rata Modulus Young uji tarik menunjukkan selang 8.370,05-12.789 kgf/cm² dengan nilai rata- rata total 10.444,24 kgf/cm². Hasil perhitungan nilai rata-rata tegangan tarik spesifik menunjukkan selang 287,83-437,26 kgf cm/gr dengan nilai rata-rata total 355,57 kgf cm/gr. Hasil perhitungan nilai rata-rata Modulus Young spesifik menunjukkan selang 7.187,81-11.156,94 kgf cm/gr dengan nilai rata-rata total 9.045,49 kgf cm/gr. Hasil analisa keragaman terhadap keempat parameter penelitian diatas menunjukkan bahwa kombinasi perlakuan waktu pembuatan dan komposisi katalisator tidah berpengaruh. Hasil perhitungan nilai rata-rata regangan menunjukkan selang 1,19%-3,19% dengan nilai rata-rata total 2,04%. Hasil analisa keragaman menunjukkan bahwa kombinasi perlakuan waktu dan komposisi katalisator terhadap regangan berpengaruh sangat nyata…dst
Keyword: 

Judul: Epivag Sebagai Penyebab Kegagalan Reproduksi Dan Penanggulangannya Pada Sapi
Abstrak: "Epivag" merupaka suatu penyakit viral yang menyerang organ reproduksi baik pada sapi jantan maupun betina, disebabkan oleh virus dan hanya terdapat di benua Afrika. Nampaknya sapi-sapi sialng Inggris di Afrika sangant peka terhadap penyakit tersebut. Mengingat bahwa sapi-sapi silang Inggris sudah banyak di impor ke Indonesia, maka perlu diperhitungkan kemungkinan penyebaran penyakit tersebut di Indonesia.
Keyword: