Judul: Production of Polyvinyl Alcohol-Lignin Nanocomposite Film with Oil Palm Empty Fruit Bunch as Lignin Source
Abstrak: One effort to reduce the food spoilage from microorganisms is by using active packaging that can maintain the quality of the products. Lignin is a material that has antimicrobial properties, antioxidants, anti-UV, and a good reinforcement agent in matrix polymers which is a potential candidate of active packaging material. One source of lignin is oil palm empty bunches (OPEFB). The purpose of this study was to produce lignin nanoparticle (nanolignin) from OPEFB and produce its PVA-nanocomposite. Nanolignin was produced by mechanical treatment by using ultrasonication. PVA-nanocomposites were produced from the mixture of PVA with different molecular weight (degree of polymerization 500 and 2000) as the matrix with the addition of nanolignin (0, 1, 3, and 5 wt%) as the fillers. The casting method was implemented to produce nanocomposite. The morphology of film was observed by using scanning electron method (SEM), chemical component by fourier transform infrared (FTIR), transparency by UV-vis spectrometer, mechanical properties by tensile strength analysis and dynamic mechanical analysis (DMA), and thermal properties by thermogravimetric analysis (TGA) and differential scanning calorimetry (DSC). The addition of nanolignin until 3 wt% increased crystallinity, tensile strength, and thermal properties of nanocomposite films. However, the addition of 5 wt% of nanolignin showed that the nanolignin is well dispersed in the low molecular weight of PVA matrix, which was shown by the high Young’s modulus and low crystallinity. Nanolignin is a good filler for the next-generation functional nanocomposite, especially in the manufacturing of the active packaging.
Keyword: mechanical properties, nanocomposite, nanolignin, oil palm fruit bunch (OPEFB), polyvinyl alcohol (PVA)

Judul: Optimasi Formula Film Nanokomposit Berbasis Polivinil Alkohol Dengan Penambahan Nanopartikel Seng Oksida (Zno) Dan Asam Lemak Stearat
Abstrak: PVA (Polivinil alkohol) adalah salah satu polimer yang secara intensif dipelajari dalam pembuatan kemasan biodegradable karena mampu membentuk film yang baik, larut dalam air, mudah dalam proses, tidak beracun dan biokompatibel. Dibalik keunggulannya tersebut, film PVA memiliki kelemahan pada sifat mekanik dan sifat penghalang, sehingga perlu dikombinasikan dengan bahan pengisi. Salah satu bahan pengisi yang sesuai adalah nanopartikel ZnO yang memiliki luas permukaan yang besar terhadap rasio volume dan memiliki sifat antimikroba yang dapat dirancang untuk menjadi kemasan aktif yang lebih efisien dan meningkatkan reaktifitas permukaan, sifat termal, mekanik, stabil terhadap panas dan tercatat aman (GRAS) oleh Food and Drug Administration (FDA). Selain penambahan nanofiller, penambahan asam lemak seperti asam stearat juga menawarkan sifat penghalang air yang tinggi. Konsentrasi bahan pengisi baik nanopartikel ZnO maupun asam lemak dapat mempengaruhi karakteristik film nanokomposit yang dihasilkan. Dalam menghasilkan formula yang optimum dari film nanokomposit PVA, penelitian ini bertujuan untuk menentukan konsentrasi optimum dari nanopartikel ZnO dan asam lemak stearat sehingga dapat meningkatkan sifat mekanik dan sifat barrier dari film PVA. Proses optimasi dilakukan dengan D-optimal Response Surface Methodology (RSM) dengan memanfaatkan piranti lunak Design Expert7. Film nanokomposit dibuat dengan menggunakan metode casting solvent dengan berbagai formulasi konsentrasi nanopartikel ZnO dan asam stearat. Film nanokomposit tersebut diujikan pada struktur morfologi, sifat mekanik dan fisik, aktivitas antimikroba dan biodegradabilitas. Penambahan bahan pengisi nanopartikel ZnO dan asam stearat mampu meningkatkan kuat tarik dan elongasi, kristalinitas, sifat termal, densitas, ketebalan; menurunkan laju transmisi uap air, warna, transmisi cahaya; serta memiliki aktivitas antimikroba yang cukup baik terhadap bakteri gram positif dan bakteri gram negatif. Formula dengan respon paling optimal adalah pada konsentrasi nanopartikel ZnO 3.4% dan konsentrasi asam stearat 6.6%. Kondisi proses optimal memiliki nilai keinginan mencapai 0.671. Nilai respon yang diprediksi oleh program yaitu, WVTR: 0.0091 g cm2/hari, kuat tarik: 34.9879 MPa, elongasi: 145.931%, kristalinitas: 48.2376%, titik leleh: 226.504oC, entalpi: 70.2065 J/g, jumlah mikroba E. coli: 140.235 cfu/ml, S. aureus: 107.531 cfu/ml. ΔE: 1.3880, transmisi cahaya: 74.1153 %, tebal: 0.0057 cm dan densitas: 1.4611 g/cm3. Film nanokomposit PVA yang dihasilkan tetap mampu terdegradasi secara alami, tetapi sedikit lebih lambat dibandingkan kontrol. Laju degradasi untuk film optimum adalah 9.6496%/hari sedangkan untuk film kontrol 10.419%/hari.
Keyword: polivinil alkohol, nanopartikel ZnO, asam stearat, optimasi, nanokomposit

Judul: Cycle Hamilton pada Graf Lengkap, Graf Regular, dan Graf 2-Connected 4-Regular Berorder Kurang dari Sepuluh.
Abstrak: Suatu graf disebut graf Hamilton apabila graf tersebut memuat cycle Hamilton, yaitu cycle yang melewati setiap vertex tepat satu kali. Menentukan keberadaan cycle Hamilton pada suatu graf dapat menggunakan syarat cukup yang berupa teorema-teorema yang telah diperkenalkan sejak tahun 1950-an. Beberapa syarat cukup yang dibahas dalam karya ilmiah ini adalah syarat cukup yang berhubungan dengan graf lengkap dan graf regular. ,,,
Keyword: graf Hamilton, graf regular, graf lengkap, graf 2-connected 4-regular.