Judul: Pemanfaatan Kulit Rotan sebagai Filler Bionanokomposit pada Aplikasi Fan Cover Comp Sepeda Motor
Abstrak: The resesarch has been conducted to obtain the optimization of process parameters to synthesize nanoparticle as bionanocomposite filler made from rattan peel waste with polypropilane matrix on fan covercomp motorcycle application. Variations of milling time used in manufacturing process of nanoparticles are 15 minutes, 30 minutes, and 45 minutes using Hammer Mill machine. The distribution of the smallest particle were gained in sample 2 with an average size of 24.35 nm. Manufacturing bionanocomposite using filler were gained from sample 2 (15 minutes). Filler used in the manufacture process of bionanocomposite is 5%, based on the research that has been done before. The quality of rattan peel fibers based on impact strength and hardness test exceeds the HES which using PPFG synthetic composite. Bionanocomposite density test value is equal to 0.84 g cm-3 and PPFG synthetic composite is 1.03 g cm-3. Based on the characteriztion showed that the nanoparticles rattan fibers are suitable for use as a filler of composite material fan covercomp motorcycle.
Keyword: rattan peel., polypropilane, nanoparticle, fan covercomp, bionanocomposite

Judul: Biokomposit filler nanopartikel serat kulit rotan sebagai material pengganti komposit sintetis fiber glass pada komponen kendaraan bermotor
Abstrak: The technology of bionanocomposite development in Indonesia had a good prospects. This is due to the availability of natural resources, especially agricultural products and waste which abundant and can be obtained throughout the year. The rattan bark is one of the agricultural waste that could be used as a source of fiber for bionanocomposite. The objective of this study was to synthesize and characterize bionanocomposite of polypropylene reinforced cellulose nanoparticles of rattan to be used to replace glass fiber as a filler in the composite. Cellulose was made of rattan bark in the form of nanoparticles by mechanical milling method, shaking, heating and ultrsonication in liquid media. These nanoparticles was used as a bionanocomposite filler which was prossesed by injection molding method with variation of concentration from 2% - 20%. The XRD result from the nanoparticles bark of rattan showed β-cellulose phase with monoclinic structure and crystal structure at 2θ = 220 (002). The density of nanoparticles was 0.2492 g cm-3 Keywords: Cellulose, extraction, nanoparticles, biodegradable, ultrasonication, . The surface morphology was elongated like a hollow cylinder. The size of the nanoparticles was 20 nm (TEM testing) with a homogeneous distribution volume of 32 %. Results from EDS and AAT indicated that bionanocomposite comprise of C, H and O as well as minerals Ca, K, Si. The mechanical properties from bionanocomposite of polypropylene reinforced cellulose nanoparticles of rattan was optimum at filler concentrations of 5%. The properties that comparable to synthetic composites were modulus of elasticity, hardness, tensile breaking elongation while, flexural strength and tensile yield strength were lower. This was due to the aglomeration in some areas so that the filler interphase bond was not optimal.
Keyword: 

Judul: Sarkosporidiosis pada sapi yang di sebabkan oleh sarcocystis cruzi
Abstrak: Sarkosporidiosis merupakan penyakit protozoa yang dapat berjalan akut dan kronis. Sarkosporidiosis pada sapi dapat diakibatkan oleh 3 jenis sarkosporidea dengan S. cruzi yang bersifat patogen dan paling banyak menyerang hewan sapi. Kejadian sapi yang terserang, mempunyai hubungan dengan umur dan musim. Sapi dari segala umur dapat terserang, tetapi sapi dengan umur di atas 2 tahun lebih banyak terserang. Mengenai musim, di Indonesia kejadian sarkosporidiosis lebih banyak terjadi pada musim hujan, dan kejadian di Eropa lebih banyak terjadi pada musim semi dan musim panas. Siklus hidup S. cruzi harus mempunyai dua induk semang yaitu herpifora sebagai induk semang antara dan karnifora sebagai induk semang akhir. Secara morfologi, hanya kista yang berisi bradyzoit yang menyebabkan infeksi terhadap karnifora. Bila dirangkumkan, perjalanan siklus hidupnya dapat dibagi dalam 3 tahap, yaitu tahap sporogoni, tahap skizogoni dan tahap gamelogoni. Tahap skizogoni merupakan tahap aseksual pada induk semang antara dan tahap gametogoni merupakan tahap seksual pada Induk semang akhir. togenitas Sarcocystis tidak begitu berat, yang membahayakan adalah toksinnya yang disebut sarkocystin atau sarkosporidin yang dapat merusak susunan syaraf, kelenjar adrenal, jantung dan dinding usus. Pengaruhnya pada penyakit yang bersifat akut, hanya terjadi dalam sejumlah kecil induk semang dan harus pula terhadap jumlah yang besar dari sporokista. Gejala-gejala klinis yang tampak adalah sebagai berikut: gejal umum, kerontokan bulu, hipersalivasi, ikterus kepucatan membaan mukus, limfadenopati periferal, diare, perasaan kedinginan, otot kejang, otot dan kepala tremor, dan paralisis-posterior. Pada sapi perah, gejala klinis yang terlihat umumnya terjadi setelah laktasi dimulai dengan sebelumnya tidak terlihat tanda-tanda yang jelas. Gejala yang ada, adalah demam (41.1°C 12.0°C), hipersalivasi, pengeluaran cairan dari hidung (nasal discharge), dan kehilangan pengkilapan bulu kulit serta kehilangan gerakan dari ekor ("ekor tikus"). ...
Keyword: