COMPOSITIONS AND METHODS FOR THERMOSETTING MOLECULES IN ORGANIC COMPOSITIONS

Abstract: In a method of producing a low dielectric constant polymer, a thermosetting monomer is provided, wherein the thermosetting monomer has a cage compound or aryl core structure, and a plurality of arms that are covalently bound to the cage compound or core structure. In a subsequent step, the thermosetting monomer is incorporated into a polymer to form the low dielectric constant polymer, wherein the incorporation into the polymer comprises a chemical reaction of a triple bond that is located in at least one of the arms. Contemplated cage compounds and core structures include adamantane, diamantane, silicon, a phenyl group and a sexiphenylene group, while preferred arms include an arylene, a branched arylene, and an arylene ether. The thermosetting monomers may advantageously be employed to produce low-k dielectric material in electronic devices, and the dielectric constant of the polymer can be controlled by varying the overall length of the arms.

Description: COMPOSITIONS AND METHODS FOR THERMOSETTING MOLECULES IN ORGANIC COMPOSITIONS This patent application is a continuation-in-part of pending US Serial 09/618,945 filed July 19, 2000. Field of The Invention The field of the invention is reduction of dielectric constants. Background of The Invention As interconnectivity in integrated circuits increases and the size of functional elements decreases, the dielectric constant of insulator materials embedding the metallic conductor lines in integrated circuits becomes an increasingly important factor influencing the performance of the integrated circuit. Insulator materials having low dielectric constants (i.e., below 3.0) are especially desirable, because they typically allow faster signal propagation, reduce capacitive effects and cross talk between conductor lines, and lower voltages to drive integrated circuits. Since air has a dielectric constant of about 1.0, a maj or goal is to reduce the dielectric constant of insulator materials down towards a theoretical limit of 1, and several methods are known in the art for including air into the insulator materials to reduce the dielectric constant of such materials. In some methods, air is introduced into the insulator material by generating nanosized voids in a composition comprising an adequately crosslinked thermostable matrix and a thermolabile (thermally decomposable) portion, which is either separately added to the thermostable matrix material (physical blending approach), or built-in into the matrix material (chemical grafting approach). In general, the matrix material is first crosslinked at a first temperature to obtain a three-dimensional matrix, then the temperature is raised to a second, higher temperature to thermolyze the thermolabile portion, and cured at a third, still higher temperature to anneal and stabilize the desired nanoporous material that has voids corresponding in size and position to the size and position of the thermolabile portion. In both the physical blending approach and the chemical grafting approach, nanoporous materials with desirable dielectric constants of about 2.5 and below may be achieved. However, while there is typically only poor control over pore size and pore distribution in the physical blending approach, the chemical grafting approach frequently poses Honeywell's Docket No. 30-5025 PCT (4780) Practitioner's Docket No. 595.09-PCT significant challenges in the synthesis of the polymers and prepolymers and inclusion of various reactive groups (e.g., to enable crosslinking, addition of thermolabile groups, etc.) into the polymers and prepolymers. Moreover, the chemical nature of both the thermolabile portion and thermostable matrix generally limits processing temperatures to relatively narrow windows which must distinguish the crosslinking (cure) temperature, thermolysis temperature and glass transition temperature, thereby significantly limiting the choice of available materials. In other methods, air or other gas (i.e. voids) is introduced into the insulator material by incorporation of hollow, nanosized spheres in the matrix material, whereby the nanosized spheres acts as a "void carriers", which may or may not be removed from the matrix material. For example, in U.S. Pat. No. 5,458,709 to Kamezaki et al, the inventors teach the use of hollow glass spheres in an insulator material. However, the distribution of the glass spheres is typically difficult to control, and with increasing concentration of the glass spheres, the dielectric material loses flexibility and other desirable physico-chemical properties. Furthermore, glass spheres are generally larger than 20nm, and are therefore not suitable for nanoporous materials where pores smaller than 2nm are desired. To produce pores with a size substantially smaller than glass spheres, Rostoker et al. describe in U.S.Pat. No. 5,744,399 the use of fullerenes as void carriers. Fullerenes are a form of carbon containing from 32 atoms to about 960 atoms, which are believed to have the structure of a spherical geodesic dome, many of which are believed to occur naturally. The inventors mix a matrix material with fullerenes, and cure the mixture to fabricate a nanoporous dielectric, wherein the fullerenes maybe removed from the cured matrix. Although the pores obtained in this manner are generally very uniform in size, homogeneous distribution of the void carriers still remains problematic. Moreover, both Rostoker 's and Kamezaki's methods require addition or admixture of the void carriers to a polymeric material, thereby adding essential processing steps and cost in the fabrication of nanoporous materials. Although various methods are known in the art to introduce nanosized voids into low dielectric constant material, all, or almost all of them have disadvantages. Thus, there is still a need to provide improved compositions and methods to introduce nanosized voids in dielectric material. Honeywell's Docket No. 30-5025 PCT (4780) Practitioner's Docket No. 595.09-PCT Summary of the Invention The present invention is directed to a method of producing a low dielectric constant polymer, hi one step, a star-shaped thermosetting monomer having a core structure and a plurality of arms is provided, and in a subsequent step the thermosetting monomer is incorporated into a polymer, wherein the incorporation into the polymer comprises a reaction of a triple bond that is located in at least one arm. i one aspect of the inventive subject matter, the core structure is a cage compound or aryl, and preferred arms are aryl, branched aryl or arylene ether. It is also preferred that where the core structure is a cage compound, at least one of the arms has a triple bond. Where the core structure is an aryl compound, it is preferred that all of the arms have a triple bond. Especially contemplated core structures include adamantane, diamantane, a phenyl, and a sexiphenylene, and especially contemplated arms include a tolanyl, a phenylethynyl- phenylethynylphenyl, a p-tolanylphenyl, a l,2-bis(phenylethynyl)phenyl, and a p-tolanylphen- yl ether. In another aspect of the inventive subject matter, the incorporation of the thermosetting monomer includes a reaction on more than one triple bond, preferably on three triple bonds located on three arms, and more preferably on all triple bonds located in all arms, hi particularly preferred aspects of the inventive subject matter, the incorporation takes place without participation of an additional molecule and preferably comprises a cyclo-addition reaction. While it is generally contemplated that the thermosetting monomer is incorporated in a backbone of a polymer, other positions including the termini and side chains are also appropriate. Preferred polymers include poly(arylene ethers) and polymers comprising, or consisting of contemplated thermosetting monomers. It is especially contemplated that by increasing the length of the arms of the thermosettmg monomers, the monomers will define an increased void volume between the monomers after crosslinking, thereby decreasing the density of the crosslinked structure and decreasing the dielectric constant of the polymer. Various objects, features, aspects and advantages of the present invention will become more apparent from the following detailed description of preferred embodiments of the invention, along with the accompanying drawing. Honeywell's Docket No. 30-5025 PCT (4780) Practitioner's Docket No. 595.09-PCT Brief Description of The Drawing Figures 1A-1C are exemplary structures for star shaped thermosetting monomers having an adamantane, a diamantane, and a silicon atom as a cage compound, respectively. Figures 2A-2B are exemplary structures for star shaped thermosetting monomers having a sexiphenylene as an aryl group. Figures 3A-3C are exemplary synthetic schemes for star shaped thermosetting monomers according to the inventive subject matter. Figure 4 is an exemplary scheme for the synthesis of substituted adamantanes with aryl arms of varying length. Detailed Description As used herein, the term "low dielectric constant polymer" refers to an organic, organometallic, or inorganic polymer with a dielectric constant of approximately 3.0, or lower. As also used herein, the term "cage compound" refers to a molecule in which a plurality of rings formed by covalently bound atoms define a volume, such that a point located within the volume can not leave the volume without passing through a ring. For example, adamantane-type structures, including adamantane and diamantane are considered a cage compound. In contrast, ring compounds with a single bridge such as norbornane (bicyclo[2.2.1]heptane) are not considered a cage compound, because the rings in a single bridged ring compound do not define a volume. In a method of producing a low dielectric constant polymer, a thermosetting monomer is provided having a general structure as showrϋn Structure 1, R 3 2 (Structure 1) wherein Y is selected from a cage compound and a silicon atom, and R l3 R 2 , R 3 , and R are independently selected from an aryl, a branched aryl, and, an arylene ether, and wherein at least one of the aryl, the branched aryl, and the arylene ether has a triple bond. In a further Honeywell's Docket No. 30-5025 PCT (4780) Practitioner's Docket No. 595.09-PCT step, the thermosetting monomer is incorporated into a polymer thereby forming the low dielectric constant polymer, wherein the incorporation into the polymer comprises a chemical reaction of the at least one triple bond. As used herein, the term "aryl" without further specification means aryl of any type, which may include, for example a branched aryl, or an arylene ether. Exemplary structures of thermosetting monomers that include an adamantane, a diamantane, and a silicon atom are shown in Figures 1A, IB, and 1C, respectively, wherein n is an integer between zero and five, or more. In another method of producing a low dielectric constant polymer, a thermosetting monomer is provided having a general structure as shown in Structure 2, R'l D ' R I 2 Ar R ' 5 R' 4 R ' 3 (Structure 2) wherein Ar is an aryl, and R' l -R' δ are independently selected from an aryl, a branched aryl, an arylene ether and nothing, and wherein each of the aryl, the branched aryl, and the arylene ether have at least one triple bond. In a subsequent step, the thermosetting monomer is incorporated into a polymer thereby forming a low dielectric constant polymer, wherein the incorporation into the polymer comprises a chemical reaction of the at least one triple bond. Exemplary structures of thermosetting monomers that include a tetra-, and a hexasubstituted sexiphenylene are shown in Figures 2A and 2B, respectively. Thermosetting monomers as generally shown in Structures 1 and 2 may be provided by various synthetic routes, and exemplary synthetic strategies for Structures 1 and 2 are shown in Figures 3A-3C. Figure 3A depicts a preferred synthetic route for the generation of star shaped thermosetting monomers with an adamantane as a cage compound, in which a bromoarene is phenylethynylated in a palladium catalyzed Heck reaction. First, adamantane (I) is brominated to tetrabromoadamantane (TBA) (2) following a procedure previously described (J. Org. Chem. 45, 5405-5408 (1980) by Sollot, G.P. and Gilbert, E.E.). TBA is reacted with phenyl bromide to yield tetrabromophenyladamantane (TBPA) (4) as described in Macromolecules, 27, 7015-7022 (1990) by Reichert, V. R, and Mathias L. J., and TBPA is subsequently reacted with a substituted ethynylaryl in a palladium catalyzed Heck reaction following standard reaction procedures to yield tetraarylethynylphenyladamantane (TAEPA) (5). The palladium-catalyzed Heck reaction may also be employed for the synthesis of a star Honeywell's Docket No. 30-5025 PCT (4780) Practitioner's Docket No. 595.09-PCT shaped thermosetting monomer with a sexiphenylene as the aromatic portion as shown in Figure 2C and Figure 2D, in which a tetrabromosexiphenylene and a hexabromosexiphenylene, respectively, is reacted with an ethynylaryl to yield the desired corresponding star shaped thermosetting monomer. Alternatively, TBA (supra) can be converted to a hydroxyarylated adamantane, which is subsequently transformed into a star shaped thermosetting monomer in a nucleophilic aromatic substitution reaction. In Figure 3B, TBA (2) is generated from adamantane (]_) as previously described, and further reacted in an electrophilic tetrasubstitution with phenol to yield tetrakis(hydroxyphenyl)adamantane (THPA) (7). Alternatively, TBA can also be reacted with anisole to give tetrakis(4-methoxyphenyl)adamantane (TMPA) (6), which can further be reacted with BBr 3 to yield THPA (7). THPA can then be reacted in various nucleophilic aromatic substitution reactions with activated fluoroaromatics in the presence of potassium carbonate employing standard procedures (e.g., Engineering Plastics - A Handbook of Polyarylethers by R. J. Cotter, Gordon and Breach Publishers, ISBN 2-88449-112-0) to produce the desired thermosetting monomers, or THPA may be reacted with 4-halo-4'- fluorotolane (with halo=Br or I) in a standard aromatic substitution reaction (e.g., Engineering Plastics, supra) to yield tetrakis[4-(4-halophenylethynylphenoxy)phenyl] adamantane (8). In further alternative reactions, various alternative reactants may also be employed to generate the shaped thermosetting monomers. Similarly, the nucleophilic aromatic substitution reaction may also be utilized in a synthesis of a star shaped thermosetting monomer with a sexiphenylene as the aromatic portion as depicted in Figure 2D, in which sexiphenylene is reacted with 4-fluorotolane to produce a star shaped thermosetting monomer. Alternatively, phloroglucinol maybe reacted in a standard aromatic substitution reaction with l-(4-fluoro- phenylethynyl-4-phenylethynyl)-4-benzene to yield l,3,5-tris(phenylethynylphenylethynyl- phenoxy)benzene. Where the cage compound is a silicon atom, an exemplary preferred synthetic scheme is depicted in Figure 3C, in which bromo(phenylethynyl)aromatic arms (9) are converted into the corresponding lithium(phenylethynyl)aromatic arms (10), which are subsequently reacted with silicon tetrachloride to yield the desired star shaped thermosetting monomer with a silicon atom as a cage compound. Honeywell's Docket No. 30-5025 PCT (4780) Practitioner's Docket No. 595.09-PCT Although it is preferred that the cage compound is an adamantane or diamantane, in alternative aspects of the inventive subject matter, various cage compounds other than an adamantane or diamantane are also contemplated. It should be especially appreciated that the molecular size and configuration of the cage compound in combination with the overall length of the arms R1-R or R' 'β will determine the size of voids in the final low dielectric constant polymer (by steric effect). Therefore, where relatively small cage compounds are desirable, substituted and derivatized adamantanes, diamantanes, and relatively small, bridged cyclic aliphatic and aromatic compounds (with typically less than 15 atoms) are contemplated. In contrast, in cases where larger cage compounds are desirable, larger bridged cyclic aliphatic and aromatic compounds (with typically more than 15 atoms) and fullerenes are contemplated. It should further be appreciated that contemplated cage compounds need not necessarily be limited to carbon atoms, but may also include heteroatoms such as N, S, O, P, etc. Heteroatoms may advantageously introduce non-tetragonal bond angle configurations, which may in turn enable covalent attachment of arms R 1 -R 4 or R ' δ at additional bond angles. With respect to substitutents and derivatizations of contemplated cage compounds, it should be recognized that many substituents and derivatizations are appropriate. For example, where the cage compounds are relatively hydrophobic, hydrophilic substituents may be introduced to increase solubility in hydrophilic solvents, or vice versa. Alternatively, in cases where polarity is desired, polar side groups may be added to the cage compound. It is further contemplated that appropriate substituents may also include thermolabile groups, nucleophilic and electrophilic groups. It should also be appreciated that functional groups may be employed in the cage compound (e.g., to facilitate crosslinking reactions, derivatization reactions, etc.) Where the cage compounds are derivatized, it is especially contemplated that derivatizations include halogenation of the cage compound, and a particularly preferred halogen is fluorine. In further alternative aspects of the inventive subject matter, the cage compound may be replaced by a non-carbon atom with a polygonal, more preferably tetragonal configuration. Contemplated atoms include a silicon atom, and particularly contemplated atoms include atoms that exhibit polygonal ligand configuration and form covalent bonds with a resistance to oxidation greater than a carbon-carbon bond. Furthermore, alternative atoms may also Honeywell's Docket No.30-5025 PCT (4780) Practitioner's Docket No. 595.09-PCT include cationic and anionic species of a particular atom. For example, appropriate atoms are Ge, and P. Where the thermosetting monomer has an aryl coupled to the arms R'ι-R' 6 as shown in Structure 2, it is preferred that the aryl comprises a phenyl group, and it is even more preferred that the aryl is a phenyl group or a sexiphenylene. hi alternative aspects of the inventive subject matter, it is contemplated that various aryl compounds other than a phenyl group or a sexiphenylene are also appropriate, including substituted and unsubstituted bi- and polycyclic aromatic compounds. Substituted and unsubstituted bi- and polycyclic aromatic compounds are particularly advantageous, where increased size of the thermosetting monomer is preferred. For example, where it is desirable that alternative aryls extend in one dimension more than in another dimension, naphthalene, phenanthrene, and anthracene are particularly contemplated. In other cases, where it is desirable that alternative aryls extend symmetrically, polycyclic aryls such as a coronene are contemplated. In especially preferred aspects, contemplated bi- and polycyclic aryls have conjugated aromatic systems that may or may not include heteroatoms. With respect to substitutions and derivatizations of contemplated aryls, the same considerations apply as for cage compounds (vide supra). With respect to the arms R1-R4 and R'l-R'δ, it is preferred that R1-R4 are individually selected from an aryl, a branched aryl, and an arylene ether, and R' R'δ are individually selected from an aryl, a branched aryl, and an arylene ether, and nothing. Particularly contem- plated aryls for R ! ^ and R' l -R' δ include aryls having a tolanyl, a phenylethynylphenylethynylphenyl, and a p-tolanylphenyl moiety, and tolanyl, phenyl- ethynylphenylethynylphenyl, and p-tolanylphenyl moieties. Especially preferred branched aryls include a l,2-bis(phenylethynyl)phenyl, and particularly contemplated arylene ethers include p-tolanylphenyl ether. i alternative aspects of the inventive subject matter, appropriate arms need not be limited to an aryl, a branched aryl, and an arylene ether, so long as alternative arms R 1 -R 4 and R'i-R'g comprise a reactive group, and so long as the incorporation of the thermosetting monomer comprises a reaction involving the reactive group. The term "reactive group" as used herein refers to any element or combinations of elements having sufficient reactivity to be used in incorporating the monomer into a polymer. For example, contemplated arms may be relatively short with no more than six atoms, which may or may not be carbon atoms. Such Honeywell's Docket No. 30-5025 PCT (4780) Practitioner's Docket No. 595.09-PCT short arms may be especially advantageous where the size of voids incorporated into the final low dielectric constant polymer need to be relatively small, hi contrast, where especially long arms are preferred, the arms may comprise a oligomer or polymer with 7-40, and more atoms. Furthermore, the length as well as the chemical composition of the arms covalently coupled to the contemplated thermosetting monomers may vary within one monomer. For example, a cage compound may have two relatively short arms and two relatively long arms to promote dimensional growth in a particular direction during polymerization. In another example, a cage compound may have two arms chemically distinct from another two arms to promote regioselective derivatization reactions. It should further be appreciated that while it is preferred that all of the arms in a thermosetting monomer have at least one reactive group, in alternative aspects less than all of the arms need to have a reactive group. For example, a cage compound may have 4 arms, and only 3 or two of the arms carry a reactive group. Alternatively, an aryl in a thermosetting monomer may have three arms wherein only two or one arm has a reactive group. It is generally contemplated that the number of reactive groups in each of the arms R I -P and R' R' 6 may vary considerably, depending on the chemical nature of the arms and of the qualities of the desired end product. Moreover, reactive groups are contemplated to be positioned in any part of the arm, including the backbone, side chain or terminus of an arm. It should be especially appreciated that the number of reactive groups in the thermosetting monomer may be employed as a tool to control the degree of crosslinking. For example, where a relatively low degree of crosslinking is desired, contemplated thermosetting monomers may have only one or two reactive groups, which may or may not be located in one arm. On the other hand, where a relatively high degree of crosslinking is required, three or more reactive groups may be included into the monomer. Preferred reactive groups include electrophilic and nucleophilic groups, more preferably groups that may participate in a cyclo addition reaction and a particularly preferred reactive group is an ethynyl group. In addition to reactive groups in the arms, other groups, including functional groups may also be included into the arms. For example, where addition of particular functionalities (e.g., a thermolabile portion) after the incorporation of the thermosetting monomer into a polymer is desirable, such functionalities may be covalently bound to the functional groups. Honeywell's Docket No.30-5025 PCT (4780) Practitioner's Docket No. 595.09-PCT The thermosetting monomers can be incorporated into a polymer by a large variety of mechanisms, and the actual mechanism of incorporation predominantly depends on the reactive group that participates in the incorporation. Therefore, contemplated mechanisms include nucleophilic, electrophilic and aromatic substitutions, additions, eliminations, radical polymerizations, and cycloadditions, and a particularly preferred incorporation is a cycloaddition that involves at least one ethynyl group located at least one of the arms. For example, in a thermosetting monomer having arms selected from an aryl, a branched aryl and an arylene ether, in which at least three of the aryl, the branched aryl, and the arylene ether have a single triple bond, the incorporation of the monomer into the polymer may comprise a cycloaddition reaction (i.e. a chemical reaction) of at least three triple bonds. In another example, in a thermosetting monomer wherein all of the aryl, the branched aryl, and the arylene ether arms have a single triple bond, the incorporation of the monomer into the polymer may comprise a cycloaddition (i.e. a chemical reaction) of all of the triple bonds. In other examples, cycloadditions (e.g., a Diels- Alder reaction) may occur between an ethynyl group in at least one arm of the thermosetting monomer and a diene group located in a polymer. It is further contemplated that the incorporation of the thermosetting monomers into a polymer takes place without participation of an additional molecule (e.g., a crosslinker), preferably as a cyclo addition reaction between reactive groups of thermosetting monomers. However, in alternative aspects of the inventive subject matter, crosshnkers may be employed to covalently couple a thermosetting monomer to a polymer. Such covalent coupling may thereby either occur between a reactive group and a polymer or a functional group and a polymer. Depending on the mechanism of incorporation of the thermosetting monomer into the polymer, reaction conditions may vary considerably. For example, where a monomer is incorporated by a cycloaddition employing a triple bond of at least one of the arm, heating of the thermosetting monomer to approximately 250°C for about 45 min is generally sufficient. In contrast, where the monomer is incorporated into a polymer by a radical reaction, room temperature and addition of a radical starter may be appropriate. A preferred incorporation is set forth in the examples. With respect to the position of incorporation of the thermosetting monomer into polymer it is contemplated that thermosetting monomers may be incorporated into the Honeywell's Docket No. 30-5025 PCT (4780) Practitioner's Docket No. 595.09-PCT backbone, a terminus or a side chain of the polymer. As used herein, the term "backbone" refers to a contiguous chain of atoms or moieties forming a polymeric strand that are covalently bound such that removal of any of the atoms or moiety would result in interruption of the chain. Contemplated polymers include a large variety of polymer types such as polyimides, polystyrenes, polyamides, etc. However, it is especially contemplated that the polymer comprises apolyaryl, more preferably a poly(arylene ether). In an even more preferred aspect, the polymer is fabricated at least in part from the thermosetting monomer, and it is particularly contemplated that the polymer is entirely fabricated from the thermosetting monomer. It should be especially appreciated that (1) the size of the cage compound or the aryl, and (2) the overall length of the arms R 1 -R and R'rR' δ that are covalently coupled to the cage compound will determine the nanoporosity imparted by a steric effect. Therefore, where a thermosetting monomer with a cage compound or a silicon atom is part of a low dielectric constant polymer, and wherein the arms R^P have a total length L and the low dielectric constant polymer has a dielectric constant K, the dielectric constant K will decrease when L increases. Likewise, where a thermosetting monomer with an aryl is part of a low dielectric constant polymer, and wherein the arms R'rR'β have a total length L and the low dielectric constant polymer has a dielectric constant K, the dielectric constant K will decrease when L increases. Consequently, the size of the cage compound, the aryl, and particularly the size of the arms in a thermosetting monomer can be employed to fine tune or regulate the dielectric constant of a low dielectric constant polymer harboring the thermosetting monomer. It is especially contemplated that by extension of the arms in a thermosetting monomer the dielectric constant maybe reduced in an amount of up to 0.2, preferably of up to 0.3, more preferably of up to 0.4 and most preferably of up to 0.5 dielectric constant units. i an especially contemplated arm extension strategy depicted in Figure 4, in which AD represents an admantane or diamantane group. Phenylacetylene is a starting molecule that is reacted (Al) with TBA (supra) to yield tetrakis(mono-tolanyl)-adamantane. Alternatively, phenylacetylene can be converted (BI . ) to tolanylbromide that is subsequently reacted (Cl) with trimethylsilylacetylene to form tolanylacetylene. TBA can then be reacted (Al) with tolanylacetylene to tetrakis(bistolanyl)-adamantane. In a further extension reaction, Honeywell's Docket No. 30-5025 PCT (4780) Practitioner's Docket No. 595.09-PCT tolanylacetylene is reacted (B2) with l-bromo-4-iodobenzene to bistolanylbromide that is further converted (C2) to bistolanylacetylene. The so formed bistolanylacetylene may then be reacted (A3) with TBA to yield tetrakis(tristolanyl)-adamantane. It is particularly contemplated that the thermosetting monomers according to the inventive subject matter may be employed in a dielectric layer of an electronic device, wherein preferred dielectric layers have a dielectric constant of less than 3, and preferred electric devices include an integrated circuit. Therefore, a contemplated electrical device may w ere n Y s se ecte om a cage compoun an a s con atom, r s pre era y an R4 are independently selected from an aryl, a branched aryl, and an arylene ether, R' I -R' O are independently selected from an aryl, a branched aryl, and an arylene ether and nothing, and wherein at least one of the aryl, the branched aryl, and the arylene ether has a triple bond. Examples The following examples describe exemplary syntheses of thermosetting molecules according to the inventive subject matter, and preparation of a low dielectric constant film. Example 1 Synthesis ofTetrabromoadamantane (TBA) Adamantane is brominated to TBA following a procedure as previously described in J. Org. Chem. 45, 5405-5408 (1980), by Sollot, G.P. and Gilbert, E.E. Synthesis ofTetrakis(3/4-bromophenyl)adamantane (TBPA) 12 -50% -40% 40% Honeywell's Docket No. 30-5025 PCT (4780) Practitioner's Docket No. 595.09-PCT TBA was reacted with bromobenzene to yield tetrakis(3/4-bromophenyl)adamantane (TBPA) as described in Macromolecules, 27, 7015-7022 (1990) by Reichert, V.R. and Mathias L.J. The reaction resulted in the formation of various byproducts. HPLC-MS analysis showed that the yield of the desired TBPA was approximately 50%, accompanied by 40% of the tribrominated tetraphenyl adamantane and about 10 % of the dibrominated tetraphenyladamantane. Unexpectedly, however, when the product mixture was subjected to fresh reagent and catalyst (bromobenzene and A1C1 3 , lmin at 20°C), TBPA was obtained in yields of approximately 90%. Synthesis of Tetrakis(tolanyl) adamantane (TTA) TBPA was reacted with phenylacetylene to yield the final product tetrakis(tolanyl)adaman- tane following a general reaction protocol for a palladium-catalyzed Heck ethynylation. A TTA prepared by the preceding process was dissolved in cyclohexanone to obtain a 15-20%) (by weight) solution, 5 ml of which were spun onto two silicon wafers using standard procedures well known in the art. The TTA was polymerized on the wafer by heating to a temperature of about 150°C and holding for one minute under N 2 , heating to a temperature of about 200°C and holding for one minute under N 2 , and heating to a temperature of about 250°C and holding for one minute under N 2 , and by curing at 400°C for one hour in N 2 after ramping up from 250°C at 5°K/minute. The k value was obtained by coating a thin film of aluminum on the cured TTA film and then doing a capacitance- voltage measurement at Honeywell's Docket No.30-5025 PCT (4780) Practitioner's Docket No. 595.09-PCT 1MHz and calculating the k value based on the film thickness. The cured TTA film had the following properties: k-value = 2.65, refractive index after bake = 1.702, ref active index after cure = 1.629, thickness after bake = 8449 Angstroms, thickness after cure = 9052 Angstroms, thickness change from bake-to-cure = 7.1%, and the as-prepared adhesion tape test = pass. Example 2 Synthesis ofp-bromotolane In a 500-mL 3 -neck round-bottom flask, equipped with an addition funnel and a nitrogen gas inlet, 4-iodobromobenzene (25.01g, 88.37mmoL), triethylamine (300mL), bis(triphenylphosphine)paladium[II] chloride (0.82g) and copper ] iodide (0.54g) were added. Then, a solution of phenylacetylene (9.025g, 88.37mmoL) in triethylamine (50mL) was added slowly, and the temperature of the solution was kept under 35C under stirring. The mixture was stirred for another 4 hours after addition was completed. The solvent was evaporated on the rotary evaporator and the residue was addecHo 200mL of water. The product was extracted with dichloromethane (2 X 150mL). The organic layers were combined and the solvents were removed by rotary evaporator. The residue was washed with 80mL hexanes and filtered. TLC and HPLC showed a pure product (yield, 19.5g, 86%). Additional purification was performed by short silica column chromatography (Eluent is 1 :2 mixture of toluene and hexanes). A white crystalline solid was obtained after solvent removal. The purity of the product was characterized by GC/MS in acetone solution, and further characterized by proton NMR. Synthesis ofp-Ethynyltolane Honeywell's Docket No. 30-5025 PCT (4780) Practitioner's Docket No. 595.09-PCT The synthesis of p-ethynyltolane from p-bromotolane was performed in two steps. In the first step, p-bromotolane was trimethylsilylethynylated, and in the second step, the reaction product of the first step was converted to the final endproduct. Step 1 (Trimethylsilylethynylation of 4-bromotolane): 4-Bromotolane (10.285g, 40.0mMol), ethynyltrimethylsilane (5.894g, 60.0mMol), 0.505g (0.73mMol) of dichlorobis(triphenylphosphine)palladium[II] catalyst, 40 mL of anhydrous triethylamine, 0.214g (1.12mMol) of copperfl] iodide, and 0.378g (1.44mMol) of triphenylphosphine were placed into the N 2 purged, 5-Liter 4-neck round-bottom flask, equipped with an overhead mechanical stirrer, condenser, and positioned inside a heating mantle. The mixture was heated to a gentle reflux (about 88°C) and maintained at reflux for 1.5 hours. The reaction mixture became a thick black paste and was cooled. Thin-layer chromatographic analysis indicated complete conversion of starting material 4-bromtolane to a single product. The solids were filtered and washed with 50mL of triethylamine, mixed with 400mL of water and stirred for 30 minutes. The solids was filtered and washed with 40mL of methanol. The crude solid was recrystallized from 500mL of methanol. On standing, lustrous silver colored crystals settled out. They were isolated by filtration and washed with 2x 50mL of methanol. 4.662g was recovered (42.5% yield). Step 2 (Conversion of 4-(Trimethylsilyl)ethynyltolane to 4-Ethynyltolane): To a 1-Liter 3 neck round-bottom flask equipped with a nitrogen inlet, an overhead mechanical stirrer, was charged 800mL of anhydrous methanol, 12.68g (46.2mMol) of 4- (trimethylsilyl)ethynyltolane, and 1.12g of anhydrous potassium carbonate. The mixture was heated to 50°C. Stirring continued until no starting material is detected by HPLC analysis (about 3 hours). The reaction mixture was cooled. The crude solids were stirred in 40mL of dichloromethane for 30 min and filtered. The filtered suspended solids by HPLC showed mainly impurities. The dichloromethane filtrate was dried and evaporated to yield 8.75 g of a solid. On further drying in an oven, the final weight was 8.67g, which represented a yield of 92.8%. Synthesis oftetrakis(bistolanyl)admantane(TBTA) P Honeywell's Docket No. 30-5025 PCT (4780) Practitioner's Docket No. 595.09-PCT TBPA (supra) was reacted with 4-ethynyltolane to yield the final product tetrakis(bis- tolanyl)adamaιιtane (TBTA) following a general protocol for a palladium-catalyzed Heck ethynylation reaction. The so prepared TBTA was dissolved in cyclohexanone to obtain a 10% (by weight) solution, 5ml of which were spun onto two silicon wafers using standard procedures well known in the art. The TBTA was polymerized on the wafer by heating to a temperature of about 300°C, and cured at a temperature of 400°C for 1 hour. The k-value was determined to be 2.57. It should be especially appreciated that when the k-value was compared to the k- value of TTA, (which is a structural analog to TBTA with a shortened length of the arms) the k-value of TTA was higher at about 2.60. Thus, the contemplated decrease in the k-value due to an increased length of the arms extending from the cage compound has been experimentally confirmed. Thus, specific embodiments and applications of compositions and methods to produce a low dielectric constant polymer have been disclosed. It should be apparent, however, to those skilled in the art that many more modifications besides those already described are possible without departing from the inventive concepts herein. The inventive subject matter, therefore, is not to be restricted except in the spirit of the appended claims. Moreover, in interpreting both the specification and the claims, all terms should be interpreted in the broadest possible manner consistent with the context. In particular, the terms "comprises" and "comprising" should be interpreted as referring to elements, components, or steps in a non-exclusive manner, indicating that the referenced elements, components, or steps may be Honeywell's Docket No.30-5025 PCT (4780) Practitioner's Docket No. 595.09-PCT present, or utilized, or combined with other elements, components, or steps that are not expressly referenced.

Claims: Honeywell's Docket No. 30-5025 PCT (4780) Practitioner's Docket No. 595.09-PCT CLAIMS What is claimed is: 1. A method of producing a low dielectric constant polymer, comprising: providing a thermosetting monomer having the structure wherein Y is selected from a cage compound and a silicon atom, and R ls R 2 , R 3 , and j. are independently selected from an aryl, a branched aryl, and an arylene ether, and wherein at least one of the aryl, the branched aryl, and the arylene ether has a triple bond; and incorporating the thermosetting monomer into a polymer thereby forming the low dielectric constant polymer, wherein the incorporation into the polymer comprises a chemical reaction of the triple bond. 2. The method of claim 1 wherein Y is selected from the group consisting of an adamantane, and a diamantane. 3. The method of claim 1 wherein the aryl comprises a moiety selected from the group consisting of a tolanyl, a phenylethynylphenylethynylphenyl, and a p-tolanylphenyl. 4. The method of claim 1 wherein the branched aryl comprises a l,2-bis(phenylethyn- yl)phenyl. 5. The method of claim 1 wherein the arylene ether comprises a p-tolanylphenyl ether. 6. The method of claim 1 wherein at least three of the aryl, the branched aryl, and the arylene ether have a triple bond, and wherein the incorporation into the polymer comprises a chemical reaction of the at least three triple bonds. 7. The method of claim 1 wherein all of the aryl, the branched aryl, and the arylene ether have a triple bond, and wherein the incorporation into the polymer comprises a chemical reaction of all of the triple bonds. Honeywell's Docket No. 30-5025 PCT (4780) Practitioner's Docket No. 595.09-PCT 8. The method of claim 1 wherein R ls R 2 , R 3 and R 4 have a total length L, and the low dielectric constant polymer has a dielectric constant K, and wherein K decreases when L increases. 9. The method of claim 1 wherein the polymer comprises a poly(arylene ether). 10. The method of claim 1 wherein the step of incorporating the thermosetting monomer into the polymer takes place without participation of an additional molecule. 11. A method of producing a low dielectric constant polymer, comprising: providing a thermosetting monomer having the structure wherein Ar is an aryl, and R' ls R' 2 , R' 3 , R' 4 , R' 5 , and R' 6 are independently selected from an aryl, a branched aryl, an arylene ether, and nothing, and wherein each of the aryl, the branched aryl, and the arylene ether have at least one triple bond; and incorporating the thermosetting monomer into a polymer thereby forming the low dielectric constant polymer, wherein the incorporation into the polymer comprises a chemical reaction of the at least one triple bond. 12. The method of claim 11 wherein die aryl comprises a phenyl group. 13. The method of claim 12 wherein Ar is selected from the group consisting of a phenyl group and a sexiphenylene. 14. The method of claim 11 wherein R' ls R' 2 , R' 3 , R' , R' 5 and R' 6 have a total length L, and the low dielectric constant polymer has a dielectric constant K, and wherein K decreases when L increases. Honeywell's Docket No. 30-5025 PCT (4780) Practitioner's Docket No. 595.09-PCT 15. The method of claim 11 wherein the step of incorporating the thermosetting monomer into the polymer takes place without participation of an additional molecule. 16. The method of claim 11 wherein the polymer comprises a poly(arylene ether). 17. A thermosetting monomer having the structure wherein Y is selected from a cage compound and a silicon atom, and R 1} R 2 , R 3 , and R 4 are independently selected from an aryl, a branched aryl, and an arylene ether, and wherein at least one of the aryl, the branched aryl, and the arylene ether has a triple bond. 18. A thermosetting monomer having the structure wherein Ar is an aryl, and R'ι, R' 2 , R' 3 , R' 4 , R' 5 , and R' 6 are independently selected from an aryl, a branched aryl, an arylene ether, and nothing, and wherein each of the aryl, the branched aryl, and the arylene ether have at least one triple bond. Honeywell's Docket No. 30-5025 PCT (4780) Practitioner's Docket No. 595.09-PCT 19. A thermosetting monomer having a structure according to formula TM- 1 : (TM-1) wherein n= 1-3. 20. A thermosetting monomer having a structure according to formula TM-2: (TM-2) wherein n= 1-3. Honeywell's Docket No. 30-5025 PCT (4780) Practitioner's Docket No. 595.09-PCT 21. A thermosetting monomer having a structure according to formula TM-3 : (TM-3) 22. An electrical device including a dielectric layer comprising a polymer fabricated from at least one thermosetting monomer from the group consisting of: wherein Y is selected from a cage compound and a silicon atom, and R ls R 2 , R 3 , and t are independently selected from an aryl, a branched aryl, and an arylene ether, and wherein at least one of the aryl, the branched aryl, and the arylene ether has a triple bond; wherein Ar is an aryl, and R , R' 2 , R' 3 , R' , R' 5 , and R' 6 are independently selected from an aryl, a branched aryl, an arylene ether, and nothing, and wherein each of the aryl, the branched aryl, and the arylene ether have at least one triple bond: Honeywell's Docket No.30-5025 PCT (4780) Practitioner's Docket No. 595.09-PCT and: Honeywell's Docket No.30-5025 PCT (4780) Practitioner's Docket No. 595.09-PCT Honeywell's Docket No. 30-5025 PCT (4780) Practitioner's Docket No. 595.09-PCT 23. A dielectric material comprising a polymer fabricated from at least one thermosetting monomer from the group consisting of: / Y >"R 2 R R 3 wherein Y is selected from a cage compound and a silicon atom, and Ri, R 2 , R 3 , and R are independently selected from an aryl, a branched aryl, and an arylene ether, and wherein at least one of the aryl, the branched aryl, and the arylene ether has a triple bond; wherein Ar is an aryl, and R' 1; R' 2 , R' 3 , R' , R' 5 , and R' 6 are independently selected from an aryl, a branched aryl, an arylene ether, and nothing, and wherein each of the aryl, the branched aryl, and the arylene ether have at least one triple bond; Honeywell's Docket No. 30-5025 PCT (4780) Practitioner's Docket No. 595.09-PCT and: Honeywell's Docket No.30-5025 PCT (4780) Practitioner's Docket No. 595.09-PCT 24. The dielectric material of claim 23 wherein said polymer is fabricated from at least one thermosetting monomer from the group consisting of: T' wherein Y is selected from a cage compound and a silicon atom, and R ls R , R 3 , and R 4 are independently selected from an aryl, a branched aryl, and an arylene ether, and wherein at least one of the aryl, the branched aryl, and the arylene ether has a triple bond; Honeywell's Docket No.30-5025 PCT (4780) Practitioner's Docket No. 595.09-PCT 25. A layer comprising the dielectric material of claim 23. 26. A layer comprising the dielectric material of claim 24. 27. A film comprising the dielectric material of claim 23. 28. A film formed from the dielectric material of claim 24. 29. The film of claim 27 wherein the dielectric constant is less than 3. 30. The film of claim 28 wherein the dielectric constant is less than 3.

Inventors: BROUK EMMA, KOROLEV BORIS, LAU KREISLER, LIU FENG QUAN, NALEWAJEK DAVID, ZHEREBIN RUSLAN, BROUK, EMMA, KOROLEV, BORIS, LAU, KREISLER, LIU, FENG, QUAN, NALEWAJEK, DAVID, ZHEREBIN, RUSLAN
Applicants: BROUK EMMA, HONEYWELL INT INC, KOROLEV BORIS, LAU KREISLER, LIU FENG QUAN, NALEWAJEK DAVID, ZHEREBIN RUSLAN, BROUK, EMMA, HONEYWELL INTERNATIONAL INC., KOROLEV, BORIS, LAU, KREISLER, LIU, FENG, QUAN, NALEWAJEK, DAVID, ZHEREBIN, RUSLAN
Application year: 2001
Main classification: C08G14
IPC codes: C08F38, C08G61, H01L21