RADIATION CURABLE COATING FOR THERMOPLASTIC SUBSTRATES

Abstract: A liquid, radiation-curable coating suitable for coating thermoplastic substrates is described. The coating composition can be formulated to achieve very low gloss at both high and low angles of incidence and it is suitable for application of adherent coatings to a moldable thermoplastic sheet. The coatings are useful for protecting thermoplastic substrates and achieving a low-gloss surface in a wide variety of applications including the manufacture of automotive interior parts, furniture, and artificial leather articles.

Description: RADIATION CURABLE COATING FOR THERMOPLASTIC SUBSTRATES The present invention relates to a radiation curable coating composition useful for providing adherent coatings for thermoplastic substrates to reduce surface gloss and increase scratch-resistance, and to modify surface feel. BACKGROUND OF THE INVENTION Thermoplastic materials such as polyethylene, polypropylene, thermoplastic olefins, EPDM, vinyl, and various synthetic and natural rubbers have been developed for use in the manufacture of automotive parts, components for furniture and appliances, and for many other commercial applications. Thermoplastic sheet materials are often used for applications where it is desired to have an aesthetically pleasing surface. Such materials that can be molded using, for example, known vacuum in thermoforming techniques, or laminated onto a functional part or assembly. Thermoplastic sheet materials are particularly useful for automotive interior panels and trim pieces, such as dashboards, doorhandles, instrument panels, aircraft headliners, furniture armrests, appliance exteriors, bookbindings, briefcases, and the like. Thermoplastic sheet materials are typically coated to protect the plastic material from marring, abrasion, and exposure to weather conditions such as sunlight, moisture, heat and cold to achieve more durable, longer-lasting parts or to modify the appearance or feel of the surface. Additionally, in automotive interior applications, it is desirable to reduce gloss to minimize potentially dangerous glare. Thermoplastic substrates have widely varying surface properties including surface tension and roughness and such substrates can be subjected to extensive thermal and physical stress during molding processes. This variability in surface properties and the unique chemical nature of certain thermoplastic substances have made it difficult to achieve acceptable adhesion of applied coatings, particularly during/after molding processes typically used in plastics manufacturing operations. A number of solutions to the problem of poor coating adhesion to thermoplastic surfaces have been investigated. Flame treatments, corona treatments, or plasma treatments have been used to oxidize the plastic surface. The application of various surface conditioning compositions containing chlorinated polyolefϊns, with or without the incorporation of polyhydroxylated poly diene polymers, to increase adhesion has also been reported. Oxidative conditioning of the thermoplastic surface by direct flaming poses hazards to the safety of workers as well as the potential for damage to the article being treated. Corona and plasma treatments require costly equipment, and often are not suitable for continuous operations. Additionally, corona and plasma treatments can result in inconsistent adhesion performance due to inconsistent levels of oxidation with resulting surface tension variations. The use of chlorinated polyolefins for surface conditioning has generated environmental concerns due to limitations in the recycling of such treated thermoplastics, or in their disposal. SUMMARY OF THE INVENTION The present invention provides a free-radical curable coating composition for applying adherent, functional coatings to thermoplastic surfaces. The composition comprises about 20 to about 100 percent by weight free-radical curable resin components comprising monomers, oligomers, or combinations thereof, each a mono or poly-ester of acrylic acid or methacrylic acid. Significantly, each of the component esters are selected to have a boiling point greater than 162°C and a molecular weight of about 150 to about 10,000. The compositions typically include about 0.1 to about 10 percent by weight of a free radical initiator, typically a photoinitiator, and about 0 to about 60% by weight of an organic solvent. The composition can be formulated in various embodiments of the invention so that at least a portion of the curable resin components in the radiation curable composition is carboxy functional or carbamate function and/or at least a portion of the curable resin components can be selected from an acrylic acid or methacrylic acid ester of a polyol containing at least 4 carbon atoms, an acrylic acid or methacrylic acid esters of isoborneol, and beta-carboxyethyl acrylate or beta-carboxyethyl methacrylate. In one embodiment of the invention the coating composition can further comprise about 0 to about 50 percent by weight of polymeric beads or powder having a median particle size of about 1 to about 60 microns dispersed in the composition. The polymeric beads or powder are typically polymers or copolymers of acrylic or methacrylic acid, esters thereof and styrene. Alternatively, the beads or powder can be formed of polyamide, polyurethane, ureaurea methanol condensate or polyurea. In yet another embodiment of the invention the coating composition can further comprise up to 30 percent silica by weight dispersed in the composition. Also in accordance with this invention there is provided a method for reducing the gloss of the surface of a thermoplastic substrate. The method comprises the steps of applying a radiation curable composition as described above to the surface, irradiating the coated surface with actinic radiation, typically UN radiation, for a time sufficient to initiate polymerization of free radical curable components. In still another embodiment of the invention there is provided a method of manufacturing a low-gloss, scratch-resistant thermoplastic article. The method comprises the steps of obtaining a thermoplastic sheet stock, applying to the thermoplastic sheet stock a radiation curable composition as described herein, irradiating the coated surface for a time sufficient to initiate polymerization of free radical curable components, and optionally forming the thermoplastic sheet stock to a pre-determined shape. An article of manufacture prepared in accordance with either of the above-described methods is also provided. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS This invention provides a radiation curable composition that can be applied to a thermoplastic surface to provide a uniform, adherent, scratch-resistant low gloss coating. The composition comprises about 20 to about 100 percent by weight free-radical curable resin components comprising monomers, oligomers, or combinations thereof, each a mono or poly-ester of acrylic acid or methacrylic acid, and each of said esters having a boiling point greater than 162°C, preferably above 180°C and most preferably above 200°C, and a molecular weight of about 150 to about 10,000. The coating composition further comprises about 0.1 to about 10 percent by weight of a free radical initiator, and about 0 to about 60% by weight of an organic solvent. It is substantially free of any curable resin components having a boiling point less than 162°C. In other embodiments the composition further comprises about 1 to about 50 percent by weight of polymeric beads or powder and/or up to about 30 percent silica by weight dispersed in the composition. Any of a wide variety of monomers and oligomers can be used to formulate the free-radical curable resin component of the present compositions. They are preferably mono or polyesters of acrylic or methacrylic acid. Each of the esters has boiling point greater than 162°C, preferably above 180°C, and most preferably above 200°C. These monomers and oligomers include, but are not limited to, the following: tefrahydrofurfuryl methacrylate isodecyl methacrylate 2(2-ethoxyethoxy) ethylacrylate stearyl acrylate tetrahydrofuryl acrylate lauryl methacrylate stearyl methacrylate lauryl acrylate 2-phenoxyethyl acrylate 2-phenoxyethyl methacrylate glycidyl methacrylate isodecyl acrylate isobornyl methacrylate isooctyl acrylate tridecyl acrylate tridecyl methacrylate caprolactone acrylate ethoxylated nonyl phenol acrylate isobornyl acrylate propoxylated allyl methacrylate methoxy polyethylene glycol polypropylene glycol monomethacrylate monomethacrylate ethoxylated nonyl phenol methacrylate beta-carboxyethyl acrylate beta-carboxyethyl methacrylate octyl acrylate decyl acrylate octyl methacrylate decyl methacrylate ethoxylated alkylphenol acrylate ethoxylated alkylphenol methacrylate hexadecyl acrylate hexadecyl methacrylate behenyl acrylate behenyl methacrylate nonyl phenol propoxylate monoacrylate, nonyl phenol propoxylate monomethacrylate polyethylene glycol dimethacrylate polyethylene glycol diacrylate tetraethylene glycol diacrylate triethylene glycol diacrylate tripropylene glycol diacrylate 1,3 butylene glycol dimethacrylate ethoxylated bisphenol a dimethacrylate ethoxylated bisphenol a diacrylate cyclohexane dimethanol diacrylate cyclohexane dimethanol dimethacrylate polypropylene glycol diacrylate polypropylene glycol dimethacrylate polyethylene glycol diacrylate polyethylene glycol dimethacrylate 1,6 hexane diol diacrylate 1,6 hexane diol dimethacrylate propoxylated neopentyl glycol propoxylated neopentyl glycol diacrylate dimethacrylate ethoxylated neopentyl glycol diacrylate ethoxylated neopentyl glycol dimethacrylate dipropylene glycol diacrylate dipropylene glycol dimethacrylate tripropylene glycol dimethacrylate trimethylolpropane trimethacrylate trimethylolpropane triacrylate tris (2-hydroxy ethyl) isocyanurate triacrylate tris (2-hydroxy ethyl) isocyanurate ethoxylated trimethylolpropane trimethacrylate triacrylate propoxylated trimethylolpropane ethoxylated trimethylolpropane triacrylate trimethacrylate propoxylated trimethylolpropane pentaerythritol triacrylate trimethacrylate pentaerythritol trimethacrylate propoxylated glyceryl triacrylate propoxylated glyceryl trimethacrylate ethoxylated glyceryl triacrylate ethoxylated glyceryl trimethacrylate pentaerythritol tetraacrylate di-trimethylolpropane tetraacrylate dipentaerythritol pentaacrylate ethoxylated pentaerythritol tetraacrylate From the Sartomer Division of Total: SR 9209, alkoxylated aliphatic SR 9041, a pentaacrylate ester; diacrylate; SR 9008, an alkoxylated tnfunctional CD 9009, a trifunctional methacrylate acrylate ester; ester; SR 9012, a trifunctional acrylate ester; CD 9050, a monofunctional acid ester; CD 9051, a trifunctional acid ester; SR 802, an alkoxylated diacrylate; SR 500 trifunctional monomer; SR 515 trifunctional monomer; SR 516 difunctional monomer; SR 517 trifunctional monomer; SR 518 tetrafunctional monomer; SR 519 trifunctional monomer; SR521 difunctional monomer; SR633 metallic diacrylate; SR634 metallic dimethacrylate; SR 636 metallic diacrylate; SR 705 metallic diacrylate; SR 708, metallic dimethacrylate; SR 709, metallic monomethacrylate; CN 934, urethane acrylate; CN 945, trifunctional urethane CN953, urethane acrylate; acrylate; CN 961, urethane acrylate; CN 962, urethane acrylate; CN 963, urethane acrylate; CN 964, urethane acrylate; CN 965, urethane acrylate; CN 966, urethane acrylate; CN 980, urethane acrylate; CN 981, urethane acrylate; CN 982, urethane acrylate; CN 983, urethane acrylate; CN 984 urethane acrylate; CN 985, urethane acrylate; CN 986, urethane acrylate; CN 970, urethane acrylate; CN 971, urethane acrylate; CN 972, urethane acrylate; CN 973, urethane acrylate; CN 975, hexafunctional urethane acrylate; CN 977, urethane acrylate; CN 978, urethane acrylate; CN 1963, urethane methacrylate; CN 104, epoxy acrylate; CN 111, epoxidized soy bean oil CN 112, epoxy novolak acrylate; acrylate; CN 115, modified epoxy acrylate; CN 117, modified epoxy acrylate; CN 118, acid modified epoxy acrylate; CN120 epoxy acrylate; CN 124, epoxy acrylate; CN 151, epoxy methacrylate; CN 130, aliphatic monoacrylate; CN 131, aromatic monoacrylate; CN 132, aliphatic diacrylate; CN 920, polyester acrylate; CN 704, acrylated polyester; CN 301, polybutadiene dimethacrylate; SB 400,401,402, 500,510, 520, aromatic acid methacrylate; From UCB Chemicals: Ebecryl ™ 111, an epoxy Ebecryl ™ ell 039 a urethane monoacrylate monoacrylate Ebecryl ™ 150, a bisphenol a Ebecryl ™ 745, acrylated acrylic derivative diacrylate Ebecryl ™ 754 acrylated acrylic Ebecryl ™ 1701 acrylated acrylic Ebecryl ™ 1710 acrylatedacrylic Ebecryl ™ 1755 acrylated acrylic Ebecryl ™ 230 acrylated urethane Ebecryl ™ 244, acrylated urethane Ebecryl ™ 264 acrylated urethane Ebecryl ™ 270 acrylated urethane Ebecryl ™ 284 acrylated urethane Ebecryl ™ 1290 acrylated urethane Ebecryl ™ 2001 acrylated urethane Ebecryl ™ 4830 acrylated urethane Ebecryl ™ 4833 acrylated urethane Ebecryl ™ 4835 acrylated urethane Ebecryl ™ 4842 acrylated urethane Ebecryl ™ 4866 acrylated urethane Ebecryl ™ 4883 acrylated urethane Ebecryl ™ 5129 acrylated urethane Ebecryl ™ 8301 acrylated urethane Ebecryl ™ 8402 acrylated urethane Ebecryl ™ 8800 acrylated urethane Ebecryl ™ 8803 acrylated urethane Ebecryl ™ 8804 acrylated urethane Ebecryl ™ 8807 acrylated urethane Ebecryl ™ 3604 rubber modified Ebecryl ™ 3605 acrylated bisphenol a epoxy acrylate epoxy Ebecryl ™ 3702 fatty acid modified Ebecryl ™ 3703 amine modified epoxy acrylate bisphenol a acrylate Ebecryl ™ 3411 fatty acid modified Ebecryl ™ 3600 amine modified epoxy acrylate bisphenol a acrylate Ebecryl ™ 168 methacylated acidic Ebecryl ™ 170 acrylated acidic monomer monomer Ebecryl ™ 350 acrylated silicone Ebecryl ™ 1360 silcone hexaacrylate From Rahn: Genomer ™ 4188 urethane acrylate Genomer ™ 4205 urethane acrylate Genomer ™ 4215 urethane acrylate Genomer ™ 4246 urethane acrylate Genomer ™ 4269 urethane acrylate Genomer ™ 4297 urethane acrylate Genomer ™ 4302 urethane acrylate Genomer ™ 4312 urethane acrylate Genomer ™ 4316 urethane acrylate Genomer ™ 4510 urethane acrylate Genomer ™ 4661 urethane acrylate Genomer ™ 4205 urethane acrylate Genomer ™ 5248 urethane acrylate Genomer ™ 5275 urethane acrylate Genomer ™ 5695 urethane acrylate Genomer ™ 7154 urethane acrylate From Photomer Energy Curing Chemicals: Photomer ® 5018, polyester acrylate Photomer ® 5018, polyester acrylate RCC™ 13-429, polyester acrylate RCC™ 13-430, polyester acrylate RCC™ 13-432, polyester acrylate RCC™ 13-433, polyester acrylate Photomer ® 6008, urethane acrylate Photomer ® 6010, urethane acrylate Photomer ® 6022, urethane acrylate Photomer ® 6184, urethane acrylate Photomer ® 6210, urethane acrylate Photomer ® 6217, urethane acrylate Photomer ® 6788-20r, urethane Photomer ® 6893, urethane acrylate acrylate RCC ™ 12-891, urethane acrylate RCC ™ 12-892, urethane acrylate RCC ™ 13-363, urethane acrylate Photomer ® 6173, aromatic acrylate RCC ™ 13-424, polyester acrylate. The monomers and oligomers useful for the UN coating compositions of the present invention can have one or more alpha, beta ethylenically unsaturated functional groups. Monomers and oligomers having one, two, three, or four alpha, beta ethylenically unsaturated functional groups per molecule are well-known. It is generally understood that as the number of alpha, beta ethyleneically unsaturated functional groups are increased from one per molecule to more than one per molecule the number of branches and crosslinks in the cured coating will increase. The degree of crosslinking can result in harder coatings that may have improved solvent resistance or may demonstrate other desirable properties. However, this increase in hardness generally must be balanced by the result that the higher level of crosslinking may provide a less flexible film. In applications where a high degree of flexibility is an important characteristic for the coating, a significant majority of the monomer and oligomer components would be selected from monofunctional and difunctional materials. To achieve the highest levels of flexibility, the monomers and oligomers are selected exclusively from monofunctional and difunctional monomers and oligomers with a significant majority being monofunctional monomers and oligomers. The monomers and oligomers used in the present coating compositions can also be selected to have additional functionality, for example, to impart improved adherence of the applied coatings to the surface of thermoplastic substrates. Thus, at least a portion of the esters in the present radiation curable coating composition can be carboxy functional; they can be an acrylic acid or methacrylic acid ester of a polyol containing at least 4 carbon atoms; they can include carbamate functionality; they can be acrylic acid or methacrylic acid esters of isoborneol, and/or they can include beta- carboxyethyl acrylate or beta-carboxyethyl methacrylate. The present UN-curable coating compositions include a free-radical initiator, typically a photoinitiator, to promote the polymerization of unsaturated monomers and oligomers. Photoinitiators typically form about 0.1 to about 10 percent by weight of the coating composition and may be used singly, in combination, or with the addition of suitable synergists. Exemplary of photoinitiators that may be use in accordance with the present invention are the following: benzil dimethyl ketal; trimethylbenzophenone; benzophenone; 1-hydroxycyclohexylphenyl ketone; 2-benzyl-2-(dimethylamino)-4'- isopropylthioxanthone; morpholinobutyrophenone;2,2- dimethoxy-2-phenylacetophenone; hydroquinone; hydroquinone monomethyl ether; p-benzoquinone; 4-chlorobenzophenone, 4-hydroxy benzophenone; 4,4-bis-(n,n-dimethylamino)- thioxanthones; benzophenone; xanthones; acridine derivatives; quinoxaline derivatives and 1-phenyl- naphthaquinone; 1 ,2-propanedione-2-o-benzoyl oxime; anthraquinone; 2-methylanthraquinone; 2-ethylanthraquinone; 2-tert-butylanthraquinone; 1 -chloroanthraquinone; 2-chloroanthraquinone benzylidene; 2-amylanthraquinone; triphenylphosphine; phenyl-bis-(2,4,6- 2,4,4 trimethylpentyl-bis-(2',6'- trimethylbenzoyl)phosphine oxide; dimethoxybenzoyl)phosphine oxide; acetophenone; 2,2-dimethoxyacetophenone; 1 , 1-dichloroacetophenone; propiophenone; cyclcopropyl phenyl ketone; benzaldehyde; beta-naphylphenyl ketone; d,l-camphorquinone; ,beta-naphthaldehyde; beta-acetonaphthone; 2,3-pentanedione; benzil; fluorenone; benzanthrone; bis(parahydroxybenzylidene)acetone; benzoin; benzoin methyl ether; benzoin ethyl ether; benzoin isopropyl ether; benzoin phenyl ether; benzoin acetate; deoxybenzoin; chlorodeoxybenzoin; 2,2-dimethyloxy-2-phenyl, 1 ,3,5- triacetyl benzene; 2,5-diethoxy stilbene; thioxanthone; anthracene; pyrene; picramide; nitronaphthalene; 5-nitroacenaphthalene; 2-nitrofluorene; rose bengal; acridine orange; chlorophyllin; crystal violet; eosin y; fluorescein; flavin mononucleotide; hematoporphyrin; hemin; malachite green; methylene blue; rhodamine b; chlorophyll; cosine; erthrosin; methylene green; toluidine blue; thionine; azidobenzene; p-phenyl bisazide; p-azidobenzophenone; 4,4' -diazidobenzophenone;4,4' - diazidodiphenylmethane;4,4 ' -diazido- stilbene; 4,4'-diazidochalcone;3,6-di(4'- p-diazodiphenylamine azidobenzal)cyclohexanone;2,6-di(4'- paraformaldehyde condensates; azidobenzal)-4-methylcyclohexanone; 1 -diazo-4-dimethylaminobenzene l-diazo-3-methyl-4-dimethylaniline hydro-fluoroborate; sulfate; 1 ,2-napthoquinonediazide; 2,3 ,4-trihydroxybenzophenone; bis-(naphthoquinone- 1 ,2-diazido-5- 2-(naphthoquinone- 1 ,2-diazido-5- sulfonate); sulfonyloxy)-3-hydroxynaphthalene; naphthoquinone- 1 ,2-diasido-5-sulfonic naphthoquinone- 1 ,2-diazido-5- acid novolak ester; sulfanilide; azidobenzoic acid; azidophthalic acid; benzene chromium tricabonyl; 2-methyl-4'-(methylthio)-2- morpholinopropiophenone; 2-hydroxy-2-methylpropiophenone. There are a wide variety of silica flatting pigments that can be used to formulate the filled composition of the present invention; these pigments can be, for example, of the precipitated type, the hydrothermal type, the hydro gel type, the aerogel type. The radiation-curable coating composition of this invention can be formulated to include up to about 30 percent silica by weight dispersed in the composition. Silica flatting pigments that are useful for preparing low-gloss, scratch- resistant coatings of the present invention include, but are not limited to, the silica flatting pigments shown in Table 1. Table 1 The coating compositions of the present invention can also be formulated with about 0 to about 50 percent by weight of insoluble polymeric beads or powders to achieve low-gloss coatings that have a "leather-like" feel, as well as resistance to marring and scratching. The polymeric beads may comprise polymers or copolymers of acrylic or methacrylic acid, esters thereof and styrene, a polyamide, a polyurethane, urea/urea methanol condensate or polyurea. The polymeric beads useful in formulating the coating compositions of the present invention typically have a median particle size of about 1 to about 60 microns. Exemplary of polymer beads that may be used in the radiation-curable compositions of the present invention are those listed in Table 2 . Table 2 The present coating composition may optionally be further modified with polymeric binder materials, resin-dependent curing agents or catalysts, flow aids, wetting agents, dispersing agents, fillers, fibers, antistatic agents, lubricants, surfactants, plasticizers, rheology modifiers, and coupling agents. Optionally, colored, or other functional pigments may also be included in the composition. The compositions can be cured, for example, by irradiation under a Mercury vapor lamp or by electron beam irradiation with or without photoinitiators. The coating compositions are produced using standard techniques for making organic, solvent-based coatings. The ingredients are combined and mixed using standard mixing equipment, normally in a tank or vessel. It is normal to add the liquid ingredients first and then add the solid materials while the liquid is being agitated. High speed dispersers may be used to break up any solid materials that tend to agglomerate during the mixing process. The application of the present coating composition is carried out by any conventional coating techniques including air atomized spray, high volume low pressure spray, airless spray, air assisted airless spray, electrostatic air atomized spray, electrostatic bell, electrostatic disk, roll coating, reverse roll coating, curtain coating, dipping, or flow coating. For the application to moldable plastic sheets, spray application, rollcoating, or curtain coating are preferred. The viscosity of the coating may be adjusted by the selection and addition of suitable solvents as is well known to those skilled in the art of coating formulations and their application. Further the coating composition of the present invention may be used as the sole film-forming composition on the substrate, or may be utilized as a primer or adhesion promoting layer for subsequent applications of organic film-forming compositions. Optionally, the coating composition can be reduced in viscosity with a suitable solvent for purposes of application. For conventional air spray, airless spray, flow coating, or curtain coating applications, the viscosity is preferably about 10 to about 350 centipose, more preferably a viscosity from about 10 to about 100 centipose. For roll coating applications the viscosity of the coating composition is about 100 to about 500 centipose, more preferably about 100 to about 200 centipose. The composition of the present invention may be applied to thermoplastic sheet materials and is particularly useful for automotive interior panels and trim pieces, such as dashboards, doorhandles, and other trim pieces, instrument panels, aircraft headliners, furniture armrests, appliance exteriors, bookbindings, briefcases, and the like. The composition may be applied with or without any surface preparation or pretreatment. Such preparation may include mechanical or chemical treatments, such as the use of conventional cleaning liquids or solvents such as isopropanol, naptha, mineral spirits, methyl isobutyl ketone, acetone, or any other well-known or suitable solvent. The pretreatment may also include, for example, treatments such as abrasive sanding, flame treatment, corona treatment, or plasma treatment, however, preferred coating compositions in accordance with this invention exhibit excellent surface adherence without such surface pretreatment procedures. Also provided in accordance with this invention is a method of reducing the gloss of the surface of a thermoplastic substrate. The method enables the manufacture of a low-gloss, scratch-resistant thermoplastic article. The method comprises the steps of applying the radiation-curable composition of the present invention to a thermoplastic sheet stock , irradiating the coated surface, typically with UN radiation, for a time sufficient to initiate polymerization of free radical curable components. The thermoplastic sheet stock can thereafter be formed to a predetermined shape. According to the method of the present invention, the thermoplastic sheet stock may first be irradiated to cure the composition and then formed to a pre-determined shape, or, alternatively, the thermoplastic sheet stock may be formed to a pre-determined shape and then coated and irradiated to initiate polymerization of free radical curable components. The pre-determined shape is that of the article being manufactured such as automotive interior panels and trim pieces, including dashboards, doorhandles, and other trim pieces, instrument panels, aircraft headliners, furniture armrests, appliance exteriors, bookbindings, briefcases, and the like. Articles of manufacture in accordance with this invention are coated with from about 1 to about 60 microns of the coating composition according to the methods of the present invention. More typically, the coatings are applied at about 5 to about 60 microns, and preferably from about 10 to about 40 microns, and more preferably about 20 to about 30 microns dry film thickness. The invention is further described by reference to the following examples. These examples are illustrative of the present invention and are not intended to limit the scope of the invention. EXAMPLE 1 In a suitable container, the following ingredients were combined and mixed under agitation. The combined ingredients were mixed under moderate agitation for at least 15 minutes prior to use. The coating composition was mixed in air, and not under a nitrogen blanket, although it would be possible to mix and store the coating composition under a nitrogen atmosphere, and this could improve the shelf life of the compositions. Examples: 1A IB 1C ID IE Ingredients: HDODA 58.5 IBOA 58.5 DEGDA 58.5 THEICTA 58.5 BCEA 58.5 Escacure™ TZT 2.3 2.3 2.3 2.3 2.3 Methyl Ethyl Ketone 39.1 39.1 39.1 39.1 39.1 Fluorad™ FC430 QΛ OΛ 0Λ 0Λ QΛ Total: 100 100 100 100 100 HDODA is an abbreviation for 1,6 hexanediol diacrylate. IBOA is an abbreviation for isobornyl acrylate. DEGDA is an abbreviation for diethylene glycol diacrylate. THEICTA is an abbreviation for tris (2-hydroxyethyl) isocyanurate triacrylate BCEA is an abbreviation for beta-carboxyethyl acrylate Escacure ™ TZT is a trade marked product supplied by Sartomer Company, Inc. a member of Total Group, Exton, PA, and has trimethylbenzophenone as the active ingredient. Fluorad ™ FC 430 is a fluorocarbon additive supplied by Minnesota Mining and Manufacturing Company, St. Paul MN. All parts in each example are by weight. EXAMPLE 2 In a suitable container, the following ingredients were combined and mixed under agitation. The combined ingredients were mixed under moderate agitation for at least 15 minutes prior to use. The coating composition was mixed in air, and not under a nitrogen blanket, although it would be possible to mix and store the coating composition under a nitrogen atmosphere, and this could improve the shelf life of the compositions. Examples: 2A 2B 2C 2D 2E 2F Ingredients: IBOA 29.3 29.3 15 BCEA 29.3 ZDMA 15 CN966J75 58.5 Ebecryl™ CL1039 58.5 29.3 30 CN704 5 5c8 5..55 Escacure™ TZT 2 2..33 2 2..33 2 2..3 3 2 2..33 2 2..33 2 2..33 Methyl Ethyl Ketone 3 399..11 3 399..11 3 3S9 )..l1 3 399..00 3 399..00 3 377.6 Fluorad™ FC430 0 0..11 0 0..11 0 0.. 11 0 0..11 0 0..11 0 0..11 Totals: 100 100 100 100 100 100 IBOA is an abbreviation for isobornyl acrylate. BCEA is an abbreviation for beta-carboxyethyl acrylate. ZDMA is an abbreviation for zinc dimethacrylate. CN966J75 is the product code for a urethane acrylate blended with isobornyl acrylate and is supplied by the Sartomer Company, Inc. a member of Total Group, Exton, PA. Ebecryl ™ CL1039 is the trademark for a urethane monoacrylate supplied by the UCB Chemicals Group, Smyrna, Georgia. CN704 is the product code of an acrylated polyester supplied by the Sartomer Company, Inc. a member of Total Group, Exton, PA. Escacure ™ TZT is a trade marked product supplied by Sartomer Company, Inc. a member of Total Group, Exton, PA, and has trimethylbenzophenone as the active ingredient. Fluorad ™ FC 430 is a fluorocarbon additive supplied by Minnesota Mining and Manufacturing Company, St. Paul MN. EXAMPLE 3 In a suitable container, the following ingredients were combined and mixed under agitation. The combined ingredients were mixed under moderate agitation for at least 15 minutes prior to use. The coating composition was mixed in air, and not under a nitrogen blanket, although it would be possible to mix and store the coating composition under a nitrogen atmosphere, and this could improve the shelf life of the compositions. Examples: 3A 3B 3C 3D 3E Ingredients BCEA 55 40.2 Caprolactone Acrylate 55 CN301 55 Ebecryl™ 3604 23.: Escacure™ TZT 2 2 2 Irgacure® 500 1.5 1.5 Methyl Ethyl Ketone 7 7 7 Butyl Acetate 35.9 35.9 35.9 48 75 Fluorad™ FC430 0.1 0.1 0.1 0.1 0.1 Totals: 100 100 100 100 100 BCEA is an abbreviation for beta-carboxyethyl acrylate. CN301 is the product code for polybutadiene dimethacrylate supplied by the Sartomer Company, Inc. a member of Total Group, Exton, PA. Ebecryl ™ 3604 is the trademark for a rubber modified epoxy arylate supplied by the UCB Chemicals Group, Smyrna, Georgia. Escacure ™ TZT is a trade marked product supplied by Sartomer Company, Inc. a member of Total Group, Exton, PA, and has trimethylbenzophenone as the active ingredient. Irgacure ® 500 is a registered trademarked product of Ciba Specialty Chemicals and is a blend of 50% benzophenone and 50% 1-hydroxycyclohexylphenyl ketone. Fluorad ™ FC 430 is a fluorocarbon additive supplied by Minnesota Mining and Manufacturing Company, St. Paul MN. EXAMPLE 4 In a suitable container, the following ingredients were combined and mixed under agitation. The combined ingredients were mixed under moderate agitation for at least 15 minutes prior to use. The coating composition was mixed in air, and not under a nitrogen blanket, although it would be possible to mix and store the coating composition under a nitrogen atmosphere, and this could improve the shelf life of the compositions. Examples: 4A 4B 4C 4D Ingredients Ebecryl™ 5129 50 CN301 50 Lauryl Methacrylate 50 CD9050 50 Irgacure® 500 1.2 1.2 1.2 1.2 Methyl Ethyl Ketone 48.5 48.5 48.5 48.5 Fluorad™ FC430 0.3 0.3 0.3 0.3 Totals: 100 100 100 100 Ebecryl ™ 5129 is the trademark for a hexaftmctional aliphatic urethane acrylate supplied by the UCB Chemicals Group, Smyrna, Georgia. CN301 is the product code for polybutadiene dimethacrylate supplied by the Sartomer Company, Inc. a member of Total Group, Exton, PA. CD9050 is the product code for monofunctional acid ester supplied by the Sartomer Company, Inc. a member of Total Group, Exton, PA. Irgacure ® 500 is a registered trademarked product of Ciba Specialty Chemicals and is a blend of 50% benzophenone and 50% 1-hydroxycyclohexylphenyl ketone. Fluorad ™ FC 430 is a fluorocarbon additive supplied by Minnesota Mining and Manufacturing Company, St. Paul MN. EXAMPLE 5 In a suitable container, the following ingredients were combined and mixed under agitation. The combined liquid ingredients were mixed under moderate agitation, and the dry powders were added under moderate agitation and then dispersed using a high speed disperser for at least 15 minutes. The coating composition was mixed in air, and not under a nitrogen blanket, although it would be possible to mix and store the coating composition under a nitrogen atmosphere, and this could improve the shelf life of the compositions. BCEA is an abbreviation for beta-carboxyethyl acrylate. CN301 is the product code for polybutadiene dimethacrylate supplied by the Sartomer Company, Inc. a member of Total Group, Exton, PA. Escacure ™ TZT is a trade marked product supplied by Sartomer Company, Inc. a member of Total Group, Exton, PA, and has trimethylbenzophenone as the active ingredient. Syloid ™ 169 is the trade name for a hydrogel type silica supplied by the Davison Division of W. R. Grace, Columbia, MD. Techpolymer ™ MB20X-5 is the trade name for an acrylate polymeric bead supplied by Sekisui Plastics Co., Ltd., Tokyo, Japan. Fluorad ™ FC 430 is a fluorocarbon additive supplied by Minnesota Mining and Manufacturing Company, St. Paul MN. EXAMPLE 6 In a suitable container, the following ingredients were combined and mixed under agitation. The combined liquid ingredients were mixed under moderate agitation, and the dry powders were added under moderate agitation and then dispersed using a high speed disperser for at least 15 minutes. The coating composition was mixed in air, and not under a nitrogen blanket, although it would be possible to mix and store the coating composition under a nitrogen atmosphere, and this could improve the shelf life of the compositions. BCEA is an abbreviation for beta-carboxyethyl acrylate. TRPGDA is an abbreviation for tripropylene glycol diacrylate. Ebecryl ™ 3708 is the trademark for an acrylated epoxy resin supplied by the UCB Chemicals Group, Smyrna, Georgia. Ebecryl ™ 168 is the trademark for an acidic methacrylate supplied by the UCB Chemicals Group, Smyrna, Georgia. Escacure ™ TZT is a trade marked product supplied by Sartomer Company, Inc. a member of Total Group, Exton, PA, and has trimethylbenzophenone as the active ingredient. Techpolymer ™ MB20X-5 is the trade name for an acrylate polymeric bead supplied by Sekisui Plastics Co., Ltd., Tokyo, Japan. Spenlite ™ L06-S-30 is an aliphatic urethane resin supplied by Reichhold, Research Triangle Park, NC. Fluorad ™ FC 430 is a fluorocarbon additive supplied by Minnesota Mining and Manufacturing Company, St. Paul MN. EXAMPLE 7 In a suitable container, the following ingredients were combined and mixed under agitation. The combined liquid ingredients were mixed under moderate agitation, and the dry powders were added under moderate agitation and then dispersed using a high speed disperser for at least 15 minutes. The coating composition was mixed in air, and not under a nitrogen blanket, although it would be possible to mix and store the coating composition under a nitrogen atmosphere, and this could improve the shelf life of the compositions. BCEA is an abbreviation for beta-carboxyethyl acrylate. IBOA is an abbreviation for isobornyl acrylate. Ebecryl ™ 3708 is the trademark for an acrylated epoxy resin supplied by the UCB Chemicals Group, Smyrna, Georgia. CN981B88 is the product code for a urethane acrylate blended with tripropylene glycol diacrylate and is supplied by the Sartomer Company, Inc. a member of Total Group, Exton, PA. CN966J75 is the product code for a urethane acrylate blended with isobornyl acrylate and is supplied by the Sartomer Company, Inc. a member of Total Group, Exton, PA. Ebecryl ™ CL1039 is the trademark for a urethane monoacrylate supplied by the UCB Chemicals Group, Smyrna, Georgia. Escacure ™ TZT is a trade marked product supplied by Sartomer Company, Inc. a member of Total Group, Exton, PA, and has trimethylbenzophenone as the active ingredient. Syloid ™ 169 is the trade name for a hydrogel type silica supplied by the Davison Division of W. R. Grace, Columbia, MD. Syloid ™ 244 is the trade name for an aerogel type silica supplied by the Davison Division of W. R. Grace, Columbia, MD. Spenlite ™ L06-S-30 is an aliphatic urethane resin supplied by Reichhold, Research Triangle Park, NC. Fluorad ™ FC 430 is a fluorocarbon additive supplied by Minnesota Mining and Manufacturing Company, St. Paul MN. EXAMPLE 8 In a suitable container, the following ingredients were combined and mixed under agitation. The combined liquid ingredients were mixed under moderate agitation, and the dry powders were added under moderate agitation and then dispersed using a high speed disperser for at least 15 minutes. The coating composition was mixed in air, and not under a nitrogen blanket, although it would be possible to mix and store the coating composition under a nitrogen atmosphere, and this could improve the shelf life of the compositions. BCEA is an abbreviation for beta-carboxyethyl acrylate. Ebecryl ™ 3604 is the trademark for a rubber modified epoxy acrylate resin supplied by the UCB Chemicals Group, Smyrna, Georgia. CN301 is the product code for polybutadiene dimethacrylate and is supplied by the Sartomer Company, Inc. a member of Total Group, Exton, PA. CD9050 is the product code for a monofunctional acid ester and is supplied by the Sartomer Company, Inc. a member of Total Group, Exton, PA. Ebecryl ™ 350 is the trademark for a acrylated silicone supplied by the UCB Chemicals Group, Smyrna, Georgia. Irgacure ® 500 is a registered trademarked product of Ciba Specialty Chemicals and is a blend of 50% benzophenone and 50% 1-hydroxycyclohexylphenyl ketone. Syloid ™ 169 is the trade name for a hydrogel type silica supplied by the Davison Division of W. R. Grace, Columbia, MD. Spenlite ™ L06-S-30 is an aliphatic urethane resin supplied by Reichhold, Research Triangle Park, NC. Fluorad ™ FC 430 is a fluorocarbon additive supplied by Minnesota Mining and Manufacturing Company, St. Paul MN. EXAMPLE 9 In a suitable container, the following ingredients are combined and mixed under agitation. The combined liquid ingredients are mixed under moderate agitation, and the dry powders are added under moderate agitation and then dispersed using a high speed disperser for at least 15 minutes. BCEA is an abbreviation for beta-carboxyethyl acrylate. Escacure ™ TZT is a trade marked product supplied by Sartomer Company, Inc. a member of Total Group, Exton, PA, and has trimethylbenzophenone as the active ingredient. Orgasol™ 1001 UD is the trade name for a polyamide powder supplied by Elf Atochem North America with a sales office in Philadelphia, PA. Soft-Clad ® CFB-101-40 is the trade name for urethane beads supplied by Reichhold Chemicals, Inc., Research Triangle, NC. Pergopak™ M3 and Pergopak™ M4 are trade names for urea methanol condensate powders supplied by Martinswerk GmbH, Bergheim, Germany. Techpolymer ™ SBX-6 is the trade name for an polystyrene bead supplied by Sekisui Plastics Co., Ltd., Tokyo, Japan. Fluorad ™ FC 430 is a fluorocarbon additive supplied by Minnesota Mining and Manufacturing Company, St. Paul MN. EXAMPLE 10 The coatings of examples 1-8 are applied to a suitable substrate using one of a variety of techniques known in the art. The following examples provide illustration of the variety of techniques available, but are not intended to restrict the methods of applying the coatings. As one example, the coatings have been applied using conventional air atomized spray. As another example, the coatings are applied by airless spray equipment. As another example, the coatings are applied using a draw bar to simulate the application of a roll coater. As another example, the coatings are poured down the substrate to simulate the application by flow or curtain coating. Alternatively, and preferably, the coatings are applied on an actual roll coater, reverse roll coater, flow coater, or curtain coater in a normal production environment. The solvents in the coatings were allowed to evaporate for between 10 seconds to several minutes and then cured in a UN processor. Many types of UN processors are available, and a number of different types of UN lamps are also available. As an illustration of the general process, a UN processor made by the Industrial Heating & Finishing Co., Inc., Birmingham, AL was used. A 300 watt/sq. in Mercury vapor lamp was used, and the coatings were cured at a line speed of 15 ft/min. The exposure was between 650 to 1800 kilojoules, and typically about 1300 kilo-joules. EXAMPLE 11 The adhesion of the coatings are tested in accordance with the adhesion test method published by the American Society For Testing And Materials (ASTM) using the method D3359 (Volume 6.01), "Standard Test Methods for Measuring Adhesion by Tape Test", Test Method B - Cross-Cut Tape Test. This method, in abbreviated form, provides for cutting through the film in a Crosshatch pattern of specified spacing, and taping the cut area with a specified tape, and then rapidly removing the tape. The cut area is then inspected to determine if paint has been loosed or removed, and the area is given a rating. A rating of 5B is a perfect rating, requiring that none of the coating be removed. A rating of OB would indicate that 65% or more of the coating was removed, thereby showing poor adhesion of the coating to the substrate. One of the most difficult substrates on which to achieve good adhesion by a coating is thermoplastic olefin (TPO). Most of the of the example coatings were evaluated on a TPO sheet supplied by the Geon Engineered Films Group, headquartered in Winchester, VA; this represents commercial quality TPO moldable sheet stock. The TPO sheet was not subjected to any mechanical or chemical cleaning, nor were any pretreatment processes such as flame treatment, corona treatment, or plasma treatment utilized. Further there was no application of polychlormated olefin adhesion promoters prior to the application of the example coatings. Conventional coating compositions, when applied to the unpretreated TPO substrate used in this example, typically have results of 0B-1B. Surprisingly and unexpectedly, the method/compositions of the present invention was found to provide coatings with perfect adliesion over a very broad range of examples as shown in Table 3. Table 3 It is also well-known that it is difficult to achieve low-gloss coatings with UV-cured compositions. In particular, it is known by those skilled in the art that it is very difficult to achieve low glosses without a visible whitening of a clear film. The gloss of a coating is typically measured using a gloss meter, and such instruments are commonly used in the coatings industry. One example of such instrumentation is the Byk Gardner micro-TRI-gloss meter. Gloss measurements were taken of a number of the example compositions from the present invention using this instrument. -33- Surprisingly and unexpectedly, many of the example compositions of the present invention achieved glosses below 10% on a 60 degree meter without significant or observable whitening. The measured gloss readings of many of the example compositions of the present invention are also shown in Table 3.

Claims: CLATMS: 1. A radiation curable composition comprising about 20 to about 100 percent by weight free-radical curable resin components comprising monomers, oligomers, or combinations thereof, each a mono or poly-ester of acrylic acid or methacrylic acid, and each of said esters having a boiling point greater than 162°C and a molecular weight of about 150 to about 10,000; about 0.1 to about 10 percent by weight of a free radical photoinitiator, and about 0 to about 60% by weight of an organic solvent, said composition being substantially free of free-radical curable resin components having a boiling point less than 162°C. 2. A radiation curable composition of claim 1 wherein at least a portion of the esters is carboxy functional. 3. The radiation curable composition of claim 1 wherein at least a portion of the esters is an acrylic acid or methacrylic acid ester of a polyol containing at least 4 carbon atoms. 4. The radiation curable composition of claim 1 wherein the free-radical curable resin components consist essentially of monomers, oligomers, or combinations thereof, each a mono or poly-ester of acrylic acid or methacrylic acid, and each of said esters having a boiling point greater than 162°C and a molecular weight of about 150 to about 10,000. 5. A radiation curable composition of claim 1 wherein some or all of the free-radical curable monomers and oligomers are the reaction product of either acrylic acid or methacrylic acid and polybutadiene. 6. The radiation curable composition of claim 1 wherein at least a portion of the esters are acrylic acid or methacrylic acid esters of isoborneol. 7. The radiation curable composition of claim 1 wherein at least a portion of the esters is beta-carboxyethyl acrylate or beta-carboxyethyl methacrylate. 8. A radiation curable composition of claim 1 wherein either polybutadiene diacrylate or polybutadiene dimethacrylate is used as at least one of the curable resin components. 9. The radiation curable composition of claim 1 further comprising about 0 to about 50 percent by weight of polymeric beads or powder having a median particle size of about 1 to about 60 microns dispersed in said composition. 10. The radiation curable composition of claim 9 wherein the polymer beads or powder comprises polymers or copolymers of acrylic or methacrylic acid, esters thereof and styrene. 11. The radiation curable composition of claim 9 wherein the polymer beads or powder comprises a polyamide. 12. The radiation curable composition of claim 9 wherein the polymer beads or powder comprises a polyurethane. 13. The radiation curable composition of claim 9 wherein the polymer beads or powder comprises a urea/urea methanol condensate or polyurea. 14. The radiation curable composition of claim 1 further comprising up to about 30 percent silica by weight dispersed in said composition. 15. The composition of claim 14 further comprising up to about 50 percent by weight of polymer beads or powder having a mean particle size of about 1 to about 60 microns dispersed in said composition. 16. A method for reducing the gloss of the surface of a thermoplastic substrate comprising the steps of: applying to said substrate a radiation curable composition of claim 1; and irradiating the coated surface with UV radiation for a time sufficient to initiate polymerization of free radical curable components. 17. The method of claim 16 wherein the plastic sheet stock is selected from the group consisting of thermoplastic olefin, EPDM, vinyl, and synthetic and natural rubber. 18. The method of claims 17 wherein the plastic sheet stock is in the form of a moldable thermoplastic sheet suitable for optional lamination and molding. 19. The method of claim 16 wherein the radiation curable composition is applied by a process selected from the group consisting of air assisted spray application, airless spray application, electrostatic spray application, roll coating, reverse roll coating, curtain coating, dipping, and flow coating. 20. A method of manufacturing a low-gloss, scratch-resistant thermoplastic article comprising the steps of: obtaining a thermoplastic sheet stock; applying to said thermoplastic sheet stock a radiation curable composition of claim 1; irradiating the coated surface with UN radiation for a time sufficient to initiate polymerization of free radical curable components; and forming the thermoplastic sheet stock to a pre-determined shape. 21. The method of claim 20 wherein the thermoplastic sheet stock is selected from the group consisting of thermoplastic olefin, EPDM, vinyl, and synthetic and natural rubber. 22. The method of claims 20 wherein the thermoplastic sheet stock is in the form of a moldable thermoplastic sheet suitable for optional lamination and molding. 23. The method of claim 20 wherein the radiation curable composition is applied by a process selected from the group consisting of air assisted spray application, airless spray application, electrostatic spray application, roll coating, reverse roll coating, curtain coating, dipping, and flow coating. 24. An article of manufacture prepared in accordance with the method of claim 16. 25. An article of manufacture prepared in accordance with the method of claim 20.

Inventors: CLARK PETER, MCCOMAS JERRY, CLARK, PETER, MCCOMAS, JERRY
Applicants: CLARK PETER JOHN, MCCOMAS JERRY, VALSPAR SOURCING INC, CLARK, PETER, MCCOMAS, JERRY, VALSPAR SOURCING, INC.
Application year: 2001
Main classification: C09D4
IPC codes: C08F2, C08F220, C08F222, C08J7, C09D4