A METHOD FOR TRANSFERRING AND STACKING OF SEMICONDUCTOR DEVICES

Abstract: The present invention is related to a method of producing an apparatus comprising at least one semiconductor device (21), said method being characterized by the fact that it comprises the following steps : forming a stack of layers, being substantially semiconductor layers, on a first substrate (1), singulating the whole of said first substrate (1) and said stack of layers, to obtain a plurality of sub-parts, attaching at least one of said sub-parts to a second substrate (9), whereby contact is made between said second substrate and said stack of layers, removing from each sub-part thus attached, essentially the singulated part of said first substrate, the remainder of said sub-part thus forming a semiconductor device (21) on said second substrate.

Description: A METHOD FOR TRANSFERRING AND STACKING OF SEMICONDUCTOR DEVICES Field of the invention [0001] The present invention relates to semiconductor devices, in particular to micro- or millimeterwave devices, embedded in an interconnect platform and manufacturing methods thereof. Background of the invention [0002] The increasing usage of MMIC's (Monolithic Millimeterwave Integrated Circuit) in application fields such as the automotive industry is a strong driving force to develop alternative technologies with equal performance level but at lower cost . In standard MMIC technology the active element and the passive circuitry are formed in a monolithic way on a single substrate. This substrate must fulfil all the requirements with respect to e.g. the growth of semiconductor layers, high frequency performance, manufacturability and cost. An alternative technology is the hybrid integration of individual HEMT's (High Electron Mobility Transistor) with passive circuitry on low-cost substrates. In this way, the epitaxial area consumption per chip can be reduced dramatically. [0003] In document US-A-5 , 675, 295, a microwave oscillator device for a receiver or a transmitter is described. This oscillator device comprises a high frequency oscillating circuit including an active device. The active device, i.e. a vertical diode, is formed on an undoped, semi-insulating, GaAs substrate. This manufacturing method comprises the steps of depositing a sacrificial layer on this GaAs substrate, followed by the deposition on this sacrificial layer and subsequent patterning of the layers, e.g. semiconductor layers, which compose the active device. An example of a manufacturing method of such active elements can be found in "W-band high-gain amplifier using InP dual-gate HEMT technology", by K. van der Zanden et al, in Proc . InP and related Materials, lpp7, pp249-252. The thus formed vertical active device (see figure lb) is then separated from the undoped GaAs substrate e.g. by applying the epitaxial lift-off (ELO) technique wherein the sacrificial layer, sandwiched between the active device and the semi-insulating substrate, is selectively etched. After separation the active device is transferred to and attached on a second substrate. This second substrate can be any other substrate, comprising passive circuitry and interconnects. Aim of the invention [0004] A first aim of the invention is to provide improved high frequency devices comprising at least one semiconductor element interconnected to a passive circuitry. [0005] Another aim of the invention is to provide a manufacturing method for hybrid integration of individual semiconductor devices with passive circuitry. [0006] Another aim of the invention is to disclose a manufacturing method for forming tandem solar cells. Summary of the invention [0007] The present invention is related to a method of producing an apparatus comprising at least one semiconductor device, said method being characterized by the fact that it comprises the following steps : forming a stack of layers, being substantially semiconductor layers, on a first substrate, singulating the whole of said first substrate and said stack of layers, to obtain a plurality of sub-parts, - attaching at least one of said sub-parts to a second substrate, whereby contact is made between said second substrate and said stack of layers, removing from each sub-part thus attached, essentially the singulated part of said first substrate, the remainder of said sub-part thus forming a semiconductor device on said second substrate. [0008] According to one embodiment, the method according to the invention further comprises the steps of forming resistors, capacitors and interconnects on said second substrate, said steps being performed after the step of removing essentially the singulated part of said first substrate. [0009] According to another embodiment, the method according to the invention, further comprises the steps of forming resistors and capacitors on said second substrate, said steps being performed before the step of attaching at least one of said sub-parts to said second substrate, and further comprising the step of forming interconnects on said second substrate, said step being performed after the step of removing essentially the singulated part of said first substrate. [0010] According to a preferred embodiment, the steps of forming resistors, capacitors and interconnects are according to a Multi-Chip Module Dielectric (MCM-D) process flow. [0011] According to a preferred embodiment, said semiconductor device formed on said second substrate is a High Electron Mobility Transistor (HEMT) . [0012] According to a preferred embodiment, said apparatus is an active microwave circuit. [0013] According to a preferred embodiment, said first substrate is a Ge-substrate. [0014] According to a preferred embodiment, after the step of attaching said sub-parts, said Ge-substrate is removed in a CF 4 -0 2 plasma etch. [0015] According to a preferred embodiment, the method according to the invention further comprises the step of forming an optical waveguide in said apparatus . [0016] The invention is equally related to a method of producing an apparatus by forming a first semiconductor device with the method according to the invention, further comprising the steps of forming an interconnect pattern and dielectric isolation, and the step of forming a second semiconductor device on top of said first semiconductor device, said second device equally being formed by the method according to the invention. [0017] According to a preferred embodiment, said apparatus is a tandem solar cell. [0018] The invention is equally related to an apparatus produced by the method according to the invention. Short description of the drawings [0019] Figure 1: prior art cross section of a metamorphic HEMT structure grown on a Ge-substrate. a: cross section through device stack after deposition, b: cross section through device after removal of the Ge substrate and buffer layer. [0020] Figure 2: prior art schematic representation of an MCM-D technology. [0021] Figure 3: method of embedding an active device, e.g. HEMT, in an interconnect technology, e.g. MCM-D, comprising passive devices according to one embodiment of the present invention. [0022] Figure 4: method of embedding an active device, e.g. HEMT, in an interconnect technology, e.g. MCM-D, comprising passive devices according to another embodiment of the present invention. [0023] Figure 5: Top SEM picture of an integrated transistor according to one embodiment of the present invention. [0024] Figure 6: schematic representation of system build-up for a short range radar system, illustrating the industrial application of the present invention. [0025] Figure 7: Schematic cross section of a microwave patch antenna in MCM-D technology, illustrating the industrial application of the present invention. [0026] Figure 8: integration of components, processed in the same or different technology, on a MCM (- D) substrate, illustrating an embodiment of the present invention [0027] Figure 9: cross section of a photodetector HEMT and an optical waveguide illustrating an embodiment of the present invention [0028] Figure 10: formation of an optical waveguide in a stack of BCB layers and further embedding of a photodetector HEMT according to an embodiment of the present invention [0029] Figure 11: schematic cross section of a tandem solar cell according to one embodiment of the invention [0030] Figure 12: electrical equivalent scheme of the cross section given in figure 11. Detailed description of the invention [0031] Figure 1 gives an schematic overview of an active device, in this example a metamorphic HEMT structure with a graded InAlAs buffer and a double doped heterostructure, grown on a Ge-substrate 1. Such a stack of semiconductor layers can be grown on a variety of substrates such as Ge, GaAS, InP. Prefeably Ge is used as substrate as such substrate is very well applicable for growing InGaAs/InAlAs High Electron Mobility Transistors. Ge substrates are more advantageous compared to GaAs of InP substrate as these Ge substrates can be larger, are less fragile and less expensive. The high dielectric loss of the Ge substrate for combining passive circuitry and active devices however has a number of disadvantages: e.g. the cut-off frequency f τ of the transistors drops to 45 GHz whereas comparable devices formed on GaAs or InP substrates can have a cut-off frequency f τ of 90GHz or higher. Moreover the losses of the transmission lines in the microwave circuits formed on a Ge substrates become very large . [0032] Various low-cost substrates can be used as second substrate. A very suitable and known technology platform is the so-called MCM-D technology, which is also used in US 5,675,295. MCM-D (Multi Chip Module- Dielectric) is a thin film technology in which alternatively thin layers of insulating and conductive materials are deposited on a low-cost substrate, such as glass or sapphire. The metal lines in one conductive layer run perpendicular to the metal layers in another conductive layer. In this MCM-D technology fixed passive components, such as resistors or capacitors, can also be formed simultaneously, while on top of the MCM-stack chips can be die-bonded by means of solder bump or flip chips techniques. Openings, i.e. via's, in these insulating layers are created to interconnect the passive components, the chips and the wiring layers . Compared to the standard MMIC technology, MCM-D technology offers a substrate with lower dielectric losses at lower cost. The cross section given in figure 2 shows an example of such low-cost substrate technology. This MCM-D technology consists of a build-up of 3 metal layers (15-16, 17, 18) embedded in BCB (12, 13), a dielectric material with low dielectric constant ( r =2.7) and low dielectric losses (loss angle tan =8 10 "4 ) . Layer 15 is an Al layer of e.g. 2μm thickness; layer 16 is equally Al of e.g. Iμm thickness. Layer 17 may be 5μm of Ti/Cu/Ti; layer 18 may be 2 μm of Ti/Cu. Layer 19 may be Ni/Au. The thickness of BCB layers 12 and 13 may be 5μm each. The complete structure is built on a low dielectric loss glass substrate 9. During the build-up of the stack of conductive and dielectric layers, passive components are formed. This metal-dielectric multilayer stack comprises TaN resistors 14, Ta 2 0 5 capacitors (10-11) , inductors and distributed microwave components. TaN resistors are mainly used as high-frequency 50 ohm terminations. Ta capacitors are used for realising large capacitors. For small capacitors a parallel plate BCB capacitor can be used. Both the TaN resistors and the Ta capacitors can be used for realizing a stable biasing of active circuitry. [0033] In relation to the appended drawings the present invention is described in detail in the sequel. It is apparent however that a person skilled in the art can imagine several other equivalent embodiments or other ways of executing the present invention, the spirit and scope of the present invention being limited only by the terms of the appended claims . [0034] In a first aspect of the invention the integration of ultra-thin semiconductor devices with passive circuitry on a low-cost substrate with good dielectric properties is disclosed. The semiconductor device comprises a stack of layers, e.g. semiconductor layers, grown on a first substrate. After forming the semiconductor device this first substrate is singulated (i.e. divided into several parts or 'dies') and the dies are transferred to a second substrate. After removal of the first substrate the attached dies are interconnected on this second substrate with passive elements, thereby employing a interconnect technology. Finally an active microwave circuit is obtained. [0035] In a preferred embodiment of this first aspect a metamorphic HEMT grown on a Ge-substrate is embedded in an MCM-D interconnect platform. This embodiment uses backside contacting of the HEMTs to the MCM-D lines, as illustrated in figure 3 (a-e) . This technique combines the advantages of a less expensive, good growth substrate with a high performance active microwave circuit. [0036] The Ge substrate measures 50 x 50 mm 2 and has a thickness of 200 μm. Although highly Ge resistive substrates are available, a Ge substrate 1 having a 50 ohm cm resistivity is chosen from a cost point of view, releasing the constraints on material purity. Since the Germanium only acts as a sacrificial substrate, as will be later on explained, its conductivity is not significant for the performance of the final device or circuit. The MBE (Molecular Beam Epitaxy) grown layer structure is depicted in Figure la and is very similar to what can be grown on GaAs. After an initial GaAs nucleation layer 2 the buffer 3 is graded from AlAs to In. 57 Al. 43 As, followed by an inverse step to In. 52 Al. 48 As to form a stress relaxation layer 4. The double Si δ-doped structure (upper doping level is 5-10 12 cm -2 and the lower is 2.5-10 12 cm "2 ) is grown lattice matched on this virtual substrate. The substrate is called virtual as the lattice constant of GaAs, grown on the Ge substrate, is transformed into the lattice constant of InP trough the relative thick buffer layer 3. The HEMT active layers are formed as if these layers were grown on a full InP substrate. This stack of HEMT active layers comprises a buffer 5a, a spacer 5b, the channel 6, followed by spacer 7b and a Schottky layer 7a. Finally a capping layer of a Si-doped In.5 3 Ga. 47 As layer 8 for oh ic contact formation is deposited. The active area of the HEMT device is obtained by wet mesa etching, deposition and alloying of Ni/Au/Ge ohmic contacts (20a, 20b) and Cr/Au c-gate metal deposition 20c. The Ge substrate is singulated to yield individual devices or array of devices. As contact levels are applied in this step of the processing, some devices can be interconnected into an array. Figure lb shows a cross section of the HEMT device after removal of the Ge substrate and the buffer layer. The contact pads to source 20a and drain 20b are free and can be contacted from the backside. In the prior art, e.g. US 5,675,295, the device, as shown in figure lb, would be ready for transfer to another substrate . [0037] Although Ge can be used as substrate material e.g. for the growth of metamorphic devices with a high level of performance and a DC behavior comparable to GaAs- based devices, its less likely to use Ge as substrate for the construction of performant RF circuits. Because the cut-off frequency f τ and the maximum oscillation frequency fa for the Ge based devices (respectively 45 and 68 GHz) are low compared to similar GaAs based devices (f τ = 90 and fa x =130 GHz) , there is a need for to remove the Ge-substrate to expel capacitive parasitics originating from the conductive Ge. In this preferred embodiment an MCM-D substrate is used, e.g. glass, as such substrate has a low-cost and good dielectric characteristics. The main disadvantage of such technology platform is the absence of active material e.g. to construct high frequency components such as microwave circuits. To realise complete microwave circuits active components are added to the passive microwave MCM-D by using flip chip. [0038] The InAlAs/InGaAs HEMTs are integrated in the MCM-D stack by flip chip connecting the HEMT 21 (see figure 3e) on the glass substrate 9, as illustrated by figure 3a. After device formation and singulation of the Ge-substrate into single HEMT devices, the HEMT devices 21 on top of the Ge-substrate 1 are transferred to the MCM-D substrate 9. As the relatively thick Ge-substrate 9 is still present during this transfer, the handling of the HEMT devices becomes very easy and the transfer process is more suitable for industrial application. [0039] A thin non-cured BCB layer 22 is used for the adhesion between the glass substrate 9 and the HEMT 21. Preferably a thin layer, e.g. 1 m or less, of BCB is deposited by spin-coating on top of the substrate 9. The HEMT device 21 is upward-down or flip chip connected to this adhesion layer 22. The BCB layer is then cured to improve the adhesion further (figure 3a) . A BCB layer is used as adhesion layer as it is compatible with the other materials used in the MCM-D technology. [0040] After attaching the stack of the HEMT device and the Ge-substrate to the MCM-D substrate the Ge substrate 1 is next removed in a CF 4 -0 2 plasma etch (see figure 3b) . A highly selective etch process has been developed, based on CF 4 and 0 2 plasma Reactive Ion Etching (RIE) , being a straightforward method compared to GaAs thinning. The settings of this selective etching process are: CF 4 flow is 100 seem, 0 2 flow is 10 seem and the pressure is 300 mTorr. The etching of the Ge-substrates takes place at 30 °C with 50 Watt RF input power. The etch rate of Ge typically is 3.5 μm/min, resulting in an etch time of about 60 minutes to remove the complete 200 μm thick substrate, leaving only the 2 μm thick epitaxial layer. Approximately 200 μm Ge is etched in 70 min, with a selectivity to the GaAs buffer layer 2 of about 1/100. The Ge can be reused by capturing the Ge from the reaction gas flow present at the exhaust of the RIE process chamber. The recycled Ge can be used to grow again Ge-substrates. As can be noticed in figure 3b the BCB layer, not covered by the HEMT stack, is also etched during the RIE step, but the glass substrate remains essentially unaffected. The GaAs buffer 2 is removed by a non-selective H 2 SO4-H2O 2 solution. This wet etching step thins the HEMT device, including the contact pads, to about 3-5 μm, preferably less then 3μm, and leads to the structure of figure 3b. Only the InGaAs/lnAlAs HEMT layers (3-8) and the Au contacts 20 remain. Such a thin structure can be integrated in the MCM-D stack without detoriating the planarising properties of the MCM-D substrate and allows the further processing of the MCM-D stack and the fixation of chips on top of this MCM-D substrate. The step height created by the embedding of the transferred HEMT device is smaller than the thickness of the applied BCB layers. The following steps are the realisations of the Ta and TaN structures on the MCM-D, e.g. used to form the resistor 14 and capacitors (10-11) . The bottom Al layer 15 covers the HEMT structure and protects it during these processing steps (figure 3c) . [0041] After patterning the Ta and TaN structures, a photoresist layer (not shown in figure 3d) is deposited and patterned to cover the Ta/TaN structures (14, 10) and the active area (23) of the transistor. By using a phosphoric acid solution only the active area of the transistor remains and the contacts (20a, 20b) , initially formed on the top of the HEMT stack before their transfer to the second substrate 9 , become free (figure 3d) . The last steps include the stacking and patterning of the BCB (12,13) and copper layers (17,18) for the realisation of the passive structures. The metallisation (17, 18-19) is also used for contacting the HEMT. This gives finally the active microwave MCM-D structure (figure 3e) . The Ni/Au component layer 19 is formed and allows the bonding of chips or other components on the MCM-D stack. Chips can be attached to further process signals from and to the active microwave MCM-D structure. [0042] In a second embodiment of the invention, a metamorphic HEMT grown on a Ge-substrate is embedded in an MCM-D interconnect platform after forming resistors and capacitors. This second embodiment uses an optimized flip chip type of interconnection with Indium used as a bonding material, rather then as bump material [0043] According to this embodiment, an alternative integration of InAlAs/lnGaAs HEMTs in MCM-D is realised by doing flip chip of the HEMT on the glass substrate using Indium (In) as a bonding material. This approach is illustrated in figure 4 (a-e) . [0044] First the TaN 14 and Ta layers (10-11) are realised using a standard MCM-D process. This process also realises the Al bottom contacts 25 for the HEMT device (figure 4a) . A thin In layer 26 is evaporated and patterned on Al (figure 4b) . The thin, e.g. 300 nm or less, In layer is used as mechanical and electrical interconnection layer between the MCM-D substrate and the HEMT. The HEMT 21 is put on the In bonding layer 26 by the flip chip bonder and subsequently heated to 150 °C (figure 4c) . The Ge substrate 1 is next removed in a CF 4 -0 2 plasma etch selective to the GaAs layer 2 as disclosed previously. The GaAs buffer is removed by a non-selective H 2 S0 4 -H2θ 2 solution as disclosed previously. The HEMT device is hence again thinned to about 3-5 μm or less and leads to the structure of figure 4d. The last steps include the stacking and patterning of the BCB (12,13) and copper layers (17,18-19) for the realisation of the passive structures. The copper metallisation is also used for contacting the HEMT. This gives finally the active microwave MCM-D structure shown in figure 4e. [0045] Figure 5 shows a SEM top view of such a structure. It shows a transistor 21 integrated to an MCM-D substrate 9. Around the device 21 are the contacts 25. Small rectangles 36, used for aligning the HEMTs on the MCM-D structure, can be seen. The active area is isolated by the final etch as illustrated in figure 4d. [0046] The hybrid integration as illustrated above can be used for a large number of applications in the microwave and even millimeter range. As an example the integration of two HEMT devices is given to obtain a short- range radar system which can be used in collision avoidance systems. In figure 6 an outline is given of a short range radar system based on frequency modulation techniques. An oscillator 29 can be tuned in frequency and sends a frequency modulated signal to the antenna that radiates in the front direction. The radiation is reflected at a metallic object such as a car and arrives back at a second antenna. This received signal is mixed 30 with the sent signal to generate a low frequency beat signal whose frequency is proportional to the distance and the incoming speed of the object. To generate a complete system in MCM- D, the MCM-D technology is extended with a back-side processing step to generate a patch antenna 27, which is fed by a coplanar line 28, inside the MCM-D layout (figure 7) . Such patch antennas can be used to radiate the frequency modulate signal or to detect the reflected signal. For the construction of the doppler radar in principle one HEMT is sufficient when one uses a self- oscillating mixer concept. In such a structure this single HEMT is used for generating the microwave oscillation and the down conversion of the reflected signal at the same time. This circuit has however a trade-off between output power of the oscillator and noise generation in the mixer. This effectively limits the range of the radar to a couple of meters. By using two transistors, one for the oscillator 29 and one for the mixer 30, the biasing and matching of both devices can be optimized to get sufficient oscillator output power with a reasonable noise figure for the mixer. This is the topology given in figure 6. All microwave circuits, e.g. matching circuits, biasing circuits and antennas are realized in the MCM-D technology. The two HEMT devices can be integrated by flip chip according to one of the options outlined above. The quasi-monolithic technique according to one of the above options, by embedding and back-contacting the HEMTs, should eliminate the parasitic effects of the interconnection as much as possible and should result in much better results especially at the higher millimeter frequencies. [0047] According to another embodiment of the invention an optical interconnect system on the low-cost substrate is disclosed. The semiconductor devices grown on the first substrate can be transferred to the second substrate in which an optical waveguide is formed. The semiconductor devices are used as an optical receiver/transmitter to convert electrical signals into optical signals and vice versa. [0048] As disclosed in previous embodiments, HEMT devices can be integrated or embedded into a circuit which is defined on the MCM substrate or within the composing layers. The MCM technologies, e.g. MCM-D, offer a platform to combine different technologies, such as III-V or BiCMOS 31, allowing the integration of devices, each having optimized properties with respect to data processing and operation frequency, on a single substrate as shown in figure 8. As stated before, chips can be attached to the MCM-D stack to further process signals from and to the active microwave MCM-D structure, comprising the HEMT device. The exchange of data between the components in or on an MCM-D stack is normally done by electrical signals. If however this data transmission could be done by light signals, very high data transmission rates could be obtained. In order to perform such communication, "light channels" or "light waveguides" and "transducing devices" are required. The "light channels" will transport the light from one "transducing device" to another. The "transducing device" will transduce or convert the light signal received from the "light channel" into an electrical signal that can be further processed by normal electronic circuitry. [0049] The "light channels" are created by forming a trench of a first material (core layer) in a substrate of a second material (cladding layer) . Both materials have different optical characteristics, such as their refractive index n. A schematic cross-section of the operation of such light channel is given in figure 9. The light being transported in the first material (core) 35, will not be encapsulated completely within this first material but some part of the Electro-Magnetic (EM) wave (32: dashed circles) , as light is an EM-signal, will extend outside this trench, in the cladding layer 13. This exponentially decaying part of the light wave is called the "evanescent field", as it is located outside the core of the light waveguide. The BCB (Benzo-Cyclo-Butene) layers (12, 13), used to electrically isolate the conductive layers in the MCM-D metal-dielectric stack, are available in different variants, each variant having different optical properties. An optical waveguide or light waveguide can be created making use of the difference in optical characteristics of the different variants of BCB. An overview of the optical properties of BCB is given in "Fabrication and Characterization of Singlemode Polymeric Optical Waveguides", by Daniel Schneider, Ph. D. dissertation university of Trondheim, Norway 1998. BCB can be used as a first material (core: 35), using the 4022 variant, and can be used as a second material (cladding: 13), using the 3022 variant. The first variant, 4022, is similar to a photosensitive resin and therefore can be exposed to light and being wet developed afterwards. The second variant 3022 is not light sensitive and has to be patterned using standard exposing and etching techniques. Normally this 3022 variant is used as dielectric layer in the MCM stack. The pattering of the BCB layers is done when via's, e.g. 33, are created to contact underlying metal levels. At this level or stage in the MCM-D processing simultaneously a trench can be formed outlining the optical waveguide. After removal of the resist used during this patterning step, the trench can be filled with the optical variant BCB4022. The filling can e.g. be done by spin-coating of the BCB material, followed by an etch-back of the BCB only leaving the trench filled with BCB4022. As BCB4022 has resin like properties, BCB4022 can be spin-coated on top of the bottom part (13a) of the cladding layer (13) , exposed to light using a mask and wet developed to have only the optical waveguide 35 line remaining. Afterwards the remaining part (13b) of the cladding layer is deposited and the overall structure is planarized. [0050] In the example illustrated in figure 8, the photoHEMT is placed on top of the MCM-stack and the optical waveguide is formed in the top BCB layer 13. Another approach is illustrated in figure 10. On top of the MCM-D substrate 9 the optical waveguide is created by first forming the stack of the cladding layer 34 comprising the optical waveguide 35. On top of this stack processing can continue as illustrated by figures 3a-e. [0051] A HEMT device has photosensitive properties, as for example the current between drain and source contacts of the HEMT can be modulated to a minor extent by incident light. No specific processing is therefore required to manufacture dedicated light transducers as such "light sensing transistor" is established simultaneously with and is equivalent to the other HEMT transistors, used e.g. in mixers 29 or down-converters 30 as explained above. Only the interconnection to such HEMT used as light-sensing device is different compared to a HEMT used as electronic device, but this only requires design effort and no change in processing technology. Both high frequency devices and optical devices can be formed on the same substrate, preferably MCM-D substrate, comprising the optical waveguide . [0052] If a HEMT device is processed and transferred in an hybrid way on top of the MCM-D stack in a way similar to other embodiments of the present invention, the gate of the device 20c can be located right on top of such "light channel" as shown in figure 9. As can be seen in this figure some of the light will be penetrating in the heterolayers (5a-8) of the devices and affect e.g. the gate leakage current . This penetrated light will be absorbed in these semiconductor layers and creates electron-hole pairs . A HEMT device consists of III-V compound semiconductor material . [0053] According to another embodiment of the invention, the stacking of ultra-thin semiconductor devices to form tandem solar cells is disclosed. [0054] If semiconductor devices are grown on a first, sacrificial substrate, and then, after singulating, transferred to a second substrate, one can use this technique to obtain a stack of semiconductor slices . In tandem solar cells, slices of semiconductor material having different band gaps are stacked. As each slice comprises a semiconductor or compound semiconductor material with a band gap different from the materials present in the other slices, each slice will be sensitive to a particular range of electro-magnetic radiation. Whereas standard silicon solar cells are only susceptible for light having energy quanta larger than the bandgap of silicon (l.lev), a tandem solar cell e.g. comprising a slice of silicon and a slice of GaAs can detect not only light in 1. leV wavelength range but also in larger wavelengths as the bandgap of GaAs is smaller (about 0.92ev) . The overall efficiency of such tandem solar cell is higher then of the single solar cell . The present invention allows the stacking of several slices of semiconductor material. Figure 11 illustrates this embodiment. Both opposite sides of the semiconductor slices (40, 41) are contacted by a set of perpendicular metal wiring (44, 43) to contact opposite sides of the junctions formed in these semiconductor slices. To connect these two slices, each slice forming a p-n junction in series, the metal level in one direction at a given level is contacted with the metal wiring in the same direction at a higher level. The metal wiring (44) is contacted by openings (45) in the insulating layer (42) . The metal wiring (43) is contacted by openings (46) in the insulating layer (42) . The insulating layer electrically isolates the p-n junctions and the wiring. Figure 12 gives the electrical equivalent scheme of the structure given in figure 11. It clearly illustrates the parallel connection of the p-n junctions. The stack given in figure 11 can be formed using other embodiments of the present invention. The semiconductor slice 40 can be grown on another substrate to yield the desired p-n junction. This substrate can be singulated into a slice having the desired dimensions. The device can be transferred to a second substrate 47 and attached hereto, e.g. by using a BCB adhesion layer. As disclosed in other embodiments, the first substrate on which this semiconductor slice was formed will be removed, e.g. during a dry etch processing step. Metal wiring can be formed before or after attaching the die 40. A second BCB layer is deposited on top of the first metal wiring 44 and on top of the slice 40. A second metal wiring 43 is deposited in a direction substantially perpendicular to the direction of the first metal wiring. This second metal wiring contacts the opposite side of the p-n junction formed in the semiconductor slice. Again a layer of BCB is deposited to electrically isolate the different levels of metal wiring and to act as a glue layer to fix a second slice 41 transferred to this stack. The processing sequence disclosed above can be repeated. Openings are formed in the dielectric layers 42 to connect the appropriate levels of metal wiring to obtain e.g. a series or a parallel connection of the devices.

Claims: CLAIMS 1. A method of producing an apparatus comprising at least one semiconductor device (21) , said method being characterized by the fact that it comprises the following steps : forming a stack of layers, being substantially semiconductor layers, on a first substrate (1) , singulating the whole of said first substrate (1) and said stack of layers, to obtain a plurality of sub- parts, attaching at least one of said sub-parts to a second substrate (9) , whereby contact is made between said second substrate and said stack of layers, removing from each sub-part thus attached, essentially the singulated part of said first substrate, the remainder of said sub-part thus forming a semiconductor device (21) on said second substrate. 2. The method according to claim 1, further comprising the steps of forming resistors (14) , capacitors (10,11) and interconnects (17, 18, 19) on said second substrate (9) , said steps being performed after the step of removing essentially the singulated part of said first substrate (1) . 3. The method according to claim 1, further comprising the steps of forming resistors (14) and capacitors (10,11) on said second substrate, said steps being performed before the step of attaching at least one of said sub-parts to said second substrate (9) , and further comprising the step of forming interconnects (17, 18, 19) on said second substrate, said step being performed after the step of removing essentially the singulated part of said first substrate (1) . 4. The method according to any one of claims 2 or 3 , wherein the steps of forming resistors, capacitors and interconnects are according to a Multi-Chip Module Dielectric (MCM-D) process flow. 5. The method according to any one of the preceding claims, wherein said semiconductor device (21) formed on said second substrate is a High Electron Mobility Transistor (HEMT) . 6. The method according to any of the preceding claims, wherein said apparatus is an active microwave circuit . 7. The method according to any of the preceding claims, wherein said first substrate (1) is a Ge- substrate. 8. The method according to claim 7, wherein after the step of attaching said sub-parts, said Ge- substrate is removed in a CF 4 -0 2 plasma etch. 9. The method according to any of the preceding claims, further comprising the step of forming an optical waveguide (35) in said apparatus. 10. A method of producing an apparatus by forming a first semiconductor device (40) with the method according to claim 1, further comprising the steps of forming an interconnect pattern and dielectric isolation, and the step of forming a second semiconductor device (41) on top of said first ' semiconductor device, said second device equally being formed by the method described in claim 1. 11. The method according to claim 10, wherein said apparatus is a tandem solar cell. 12. An apparatus produced by the method according to any one of the preceding claims.

Inventors: BEYNE ERIC, BORGHS STAF, VANDERSMISSEN RAF, BEYNE, ERIC, BORGHS, STAF, VANDERSMISSEN, RAF
Applicants: BEYNE ERIC, BORGHS STAF, IMEC INTER UNI MICRO ELECTR, UNION MINIERE SA, VANDERSMISSEN RAF, BEYNE, ERIC, BORGHS, STAF, INTERUNIVERSITAIR MICRO-ELEKTRONICA CENTRUM, UNION MINIERE, VANDERSMISSEN, RAF
Application year: 2001
Main classification: H01L21
IPC codes: H01L21, H01L23, H01L25, H01L31, H05K3