METHOD OF FORMING SPACERS IN CMOS DEVICES

Abstract: A sidewall spacer is formed in a CMOS device by depositing a layer of silicon nitride on a wafer and anisotropically etching away the silicon nitride layer with a chorinebased plasma etchant.

Description: METHOD OF FORMING SPACERS IN CMOS DEVICES This invention relates a semiconductor fabrication technique, and in particular to a method of forming spacers in CMOS devices. In the fabrication of CMOS devices, a polysilicon gate is typically deposited over a gate oxide grown on the silicon substrate. Ion implantation occurs through the field oxide located between the gates. In order to protect the gate region during the implantation step, the side walls of the gates are protected with vertical walls known as spacers. In the past, amorphous silicon was used for the spacers, but this created problems during subsequent etching in that it was difficult to avoid over-etching and the removal of part of the underlying layer. Over-etching occurs when etching extends into the underlying layer. Often when the spacers were removed, a polysilicon gate would be etched at the same time leaving a notch, known as a "mouse bite" in the polysilicon gate. An object of the invention is to alleviate this problem. In accordance with one aspect of the present invention, the side wall spacers are made of silicon nitride. Silicon nitride has the advantage of offering good selectivity, making it easy to avoid over-etching when the precursor conformal layer is removed. In accordance with an important aspect of the invention, a conformal silicon nitride layer is etched using a chlorine-based plasma etch chemistry. Such etch chemistry consists of chlorine (Cl 2 ), hydrogen bromide (HB r ), and a mixture of helium and oxygen. This is in contrast to the conventional CHF 3 chemistry, which is normally used for silicon nitride etching. The applicants have found that using conventional silicon nitride etch chemistry, it is very difficult to avoid over-etching into the gate oxide because of the high plasma power and the limited oxide/nitride selectivity of 1.8 to 1. In accordance with the present invention, it has been found surprisingly that oxide /nitride select! vities in the order of 3 to 1 can be achieved, which completely protects the gate oxide. In the invention the etching is caused largely by chemical rather than the mechanical interaction associated with CHF 3 plasmas. The Cl " radicals etch the silicon nitride chemically and the HBr component is responsible mainly for mechanical etching by the plasma. The reaction of HBr with silicon nitride also creates a protective polymer layer that protects the more vertical profiles of the etched films, resulting in a more anisoptropic etch. Some spacers are left along the polysilicon lines with a rounded shape. While the etch rate using chlorine-based etch chemistry, typically around 2000 Angstroms per minute, is somewhat slower than CHF 3 -based chemistry, typically around 5000 Angstroms per minute, this trade-off is more than offset by the improvement in selectivity obtainable. The conformal nitride layer is preferably deposited onto a thin oxide layer, typically about 200 Angstroms thick. The invention will now be described in more detail, by way of example only, with reference to the accompanying drawings in which:- Figures 1 to 4 show successive steps in the manufacture of a CMOS device in accordance with the principles of the present invention. Referring now to the drawings, the CMOS device comprises a silicon substrate 10. First, as shown in Figure 1, a silicone nitride layer (not shown) is deposited on the substrate and then patterned to leave regions of exposed silicon. The wafer is then exposed to an oxidizing atmosphere to grow field oxide layer 12 in a conventional manner. After removal of the nitride layer, gate oxide 14 is grown between the field oxide regions 12. After growing the gate oxide 14, a polysilicon layer is grown and subsequently patterned to form polysilicon gates 16 on gate oxide 14 (Figure 2). Typically, after the patterning of the polysilicon gate 16, a first ion implantation takes place to form source and drain active regions 15. Next, an oxidation step takes place (Figure 3) to grow a thin silicon oxide layer 17, which is typically about 200 Angstroms thick. In the next step, a conformal silicon nitride layer 18 is deposited over the surface of the wafer using LPCDN (Low Pressure Chemical Vapor Deposition). The objective is to remove the silicon nitride layer 18 except for the vertical side wall portions 20 protecting the polysilicon gates 16 by etching down to the thin oxide layer 17. The remaining side wall portions 20 forming the spacers slightly rounded as shown. The removal of the horizontal portions of the silicon nitride layer without effecting the underlying layers requires good nitride /oxide selectivity and also good anisotropy to avoid lateral etching into the side walls 20. In accordance with the principles of the invention, the anisotropic etch is performed using an etch recipe comprising chlorine (Cl 2 ), hydrogen bromide (HB r ) and a mixture of helium and oxygen. The etch is performed as an reactive ion etch using a magnetic field to ensure good uniformity on the wafer. The preferred etch variables are set out in the following table: The etch is formed in two steps: the main etch and the over-etch. It will be noted that in the main etch, nitride /oxide selectivities of 3 to 1 are achieved, and in the over-tech, to remove any remaining nitride layer, selectivities as high as 16.5 to 1 are achieved. The etch endpoint is detected using optical methods by detecting the chlorine spectral line at 4705 A. At this point, the chlorine stops being consumed, so by looking at the chlorine spectral line at 470.5 nm, it is possible to determine when the silicon nitride has been completely etched. Finally, as shown in Figure 4, a second polysilicon layer 22 is deposited over the wafer and selectively etched so that the second layer 22 lies over the polysilicon gates 18. Next ion implantation is carried out through the thin oxide layer to form active components, such as transistors. Typically, N+ and P+ species are implanted, and in accordance with the principles of the invention, these are implanted directly through the thin oxide layerl7, which is left in situ. The use of silicon nitride spacers has several advantages. It gives more flexibility in the etching techniques that can be used for the adjacent films. It permits good control of conformability to the wafer surface, and the good selectivity permits the avoidance of over-etching of the underlying layer. This is important because the silicon nitride layer is about 3,000 - 4,000 A thick. It is indeed surprising, but highly significant, that the use of an etch recipe typically applied to polysilicon improves the selectivity and anisotropy of a silicon nitride etch, a fact that leads to a major improvement in the fabrication of CMOS devices.

Claims: We claim: 1. A sidewall spacer in a CMOS device comprising silicon nitride. 2. A method of forming a sidewall spacer in a CMOS device, comprising depositing a layer of silicon nitride on a wafer, and anisotropically etching away lateral portions of said silicon nitride layer using a chorine-based plasma etchant to leave said sidewall spacer. 3. A method as claimed in claim 2, wherein a thin silicon oxide layer is formed prior to the deposition of said silicon nitride layer, and said lateral portions of said silicon nitride are etched away down to said thin oxide layer. 4. A method as claimed in claim 3, wherein chorine-based plasma etchant comprises chlorine, hydrogen bromide, and a mixture of helium and oxygen. 5. A method as claimed in claim 3, wherein said etching step is carried out in the presence of a magnetic field. 6. A method as claimed in claim 5, wherein said etching step is performed as a reactive ion etch. 7. A method as claimed in claim 5, wherein a main etching step is first carried out, and then a subsequent over etch is carried out at reduced pressure and power. 8. A method as claimed in claim 7, wherein the main etch and over etch have the following parameters. 9. A method of forming silicon nitride spacers in the fabrication of a semiconductor device, comprising forming a thin oxide layer on a wafer, forming a silicon nitride layer on said thin oxide layer, and anisotropically etching said nitride layer down to said thin oxide layer using a chorine-based plasma etchant to leave said sidewall spacers. 10. A method as claimed in claim 9, further comprising the step of implanting impurities through said thin oxide layer to form active components in said wafer. 11. A method as claimed in claim 10, wherein said impurities are selected from the group consisting of N + and P + species. 12. A method as claimed in claim 10, wherein said active components are transistors.

Inventors: COUTURE GINETTE, DAIGLE MANON, LESSARD BRUNO, ROY MARC, COUTURE, GINETTE, DAIGLE, MANON, LESSARD, BRUNO, ROY, MARC
Applicants: MITEL CORP, MITEL CORPORATION
Application year: 2001
Main classification: H01L21
IPC codes: H01L21