WATERBORNE COATING COMPOSITIONS

Abstract: The present invention is directed to a waterborne coating composition prepared from liquid blend raw materials, such as titanium dioxide slurries, extender pigment slurries, thickener slurries, glycol slurries, and latex binders. The liquid blends have substantially the same viscosity characteristics as the final waterborne coating composition, in the range of about 70-125 Krebs units. The method for preparing the waterborne coating composition of the invention comprises providing a plurality of the liquid blend raw materials and admixing the liquid blend raw materials to produce the waterborne coating product. This invention is also directed to pigment slurry compositions useful in liquid blend systems, and the method for preparing the slurries.

Description: WATERBORNE COATING COMPOSITIONS CROSS-REFERENCE TO RELATED APPLICATION This application claims the benefit of U.S. Provisional Application No. 60/250708, filed December 1, 2000. BACKGROUND OF THE INVENTION This invention relates to a waterbome coating produced using all liquid slurry raw materials and an all liquid blend process for making the coatings. The process of this invention reproducibly produces waterbome coating formulations having predetermined quality such as viscosity, pH, NVM, and the like, and reproducible color and gloss. The present invention utilizes novel raw material slurry compositions whereby each raw material, including titanium dioxide, pigment extenders, thickeners, etc., is preformulated as liquid slurries to have substantially the same viscosity. According to this invention, each raw material slurry typically has substantially the same viscosity as that desired of the final waterbome coating product. The slurries are admixed and blended, by volumetric and gravimetric methods, to form coating formulations having predetermined quality and specifications. Conventional waterbome paint manufacturing processes consist of mixing or blending pigments and various liquid and dry additives with latex resins, and then processing or grinding using high speed Cowles dispersers. Dry raw materials commonly used in waterbome coatings include prime hiding, extender and prime colored pigments and hydroxyethylcellulose thickeners. Typically, waterbome formulations contain high levels of these hard-to-grind pigments, which are dispersed with low volume extenders, pigments, and additives in a high speed Cowles disperser. The dispersion paste, is then thinned down by adding other raw materials such as water based vehicles and defoamers, and then subsequently adding other raw materials such as liquid pigment slurries and thickeners to obtain the final unshaded product. Liquid components commonly used in waterbome coatings include additives such as wetting agents, dispersants, defoamers, glycols, mildewcides, bactericides, coalescents, ammonium hydroxide, amines, etc. as well as pigment slurries and latex. Multiple additions of the required shading bases are then necessary to achieve the final color. Other adjustments to the final product to meet specifications for gloss, viscosity, pH, etc., are common. Thus, the raw materials used in waterbome paint formulations typically contain high levels of materials having extremely narrow compatibility tolerances, due to incompatibilities of the components in the mixing. Of particular concern in any system is the ability to reproducibly and consistently obtain the same quality of product . Also, pigments in colorant dispersions and conventional pigment slurries have a tendency to settle, which require agitators that can maintain the dispersions as a reasonably uniform mixture. It is sometimes also necessary to add materials that are incompatible with materials already in the process stream. Such additives, as well as their order of addition, may cause problems associated with stability, seeding and/or settling typically due to these incompatibilities . Thus, there is a need for a process to overcome the incompatibilities between raw materials in formulation. There is also a need to produce waterbome coatings with reproducible quality and characteristics, without the need for making adjustments to the final waterbome coating products that do not meet quality specifications. In accordance with the teachings of the present invention, paint manufacturing process steps can be significantly reduced by first consolidating or interblending the raw materials into liquid blends or slurries, and then continuously, simultaneously, or sequentially admixing the liquid slurries to obtain a final waterbome coating. The waterbome coatings produced according to this invention do not require rebalancing or adjustments to pH, viscosity, color, etc. Thus, in the present invention, a waterbome product can be achieved having predetermined quality and physical properties such as color, viscosity, pH, NVM, and gloss by cross-blending the liquid blends or slurries. SUMMARY OF THE INVENTION The present invention is directed to a waterbome coating composition comprising (a) about 0 to 70 percent by weight, based on the total weight of the composition, of a titanium dioxide slurry; (b) about 0 to 75 percent by weight, based on the total weight of the composition, of at least one extender pigment slurry that can be selected from the group consisting of, but not limited to, calcium carbonate slurry, silica slurry, and kaolin clay slurry; and (c) about 1 to 20 percent by weight, based on the total weight of the composition, of at least one thickener slurry that can be selected from the group consisting of polyacrylates, hydroxyethylcellulose, alkali soluble emulsions, hydrophobic ethoxylated urethane resins, and hydrophobically-modified alkali soluble emulsions; and (d) about 1 to 10 percent by weight of a glycol slurry; and (e) at least one latex binder. The viscosity of the coating composition produced according to this invention can be predetermined and substantially the same as the viscosity of the raw material slurries, and which is preferably within the range of 70-125 Krebs units. A process for producing the waterbome coating composition is also provided. This invention is also directed to pigment slurries comprising (a) about 20 to 90 percent by weight, based on the total weight of the slurry, of titanium dioxide pigment; (b) about 0.5 to 10 percent by weight, based on the total weight of the slurry, of a glycol; and (c) about 0J to 10 percent by weight, based on the total weight of the slurry, of at least one thickener that can be selected from the group consisting of polyacrylates, hydroxyethylcellulose, alkali soluble emulsions, hydrophobic ethoxylated urethane resins, and hydrophobically-modified alkali soluble emulsions. The pigment can be selected from the group consisting of titanium dioxide, calcium carbonate, kaolin clay and silica. The Stormer viscosity of said pigment slurry is in the range of about 70-125 Krebs units. A process for producing the slurry is also provided. Another object is to provide a process for producing a waterbome coating composition having predetermined viscosity characteristics utilizing a total liquid blend process, comprising: (a) providing a plurality of reservoirs containing liquid blend slurries of raw materials, said liquid blend slurries of raw materials have substantially the same viscosities; (b) continuously, simultaneously, or sequentially mixing a latex binder with a controlled amount of the liquid blend slurries from said reservoirs to produce the waterbome coating. The final waterbome coating product has substantially the same viscosity as the liquid blend slurries and does not require additional adjustments for viscosity. The process comprises providing suitable liquid blends of raw materials, such as titanium dioxide slurries or other pigment slurries, such as extender pigment slurries of calcium carbonate, kaolin clay, silica, glycol slurries, and the like, or mixtures thereof. DETAILED DESCRIPTION OF THE INVENTION According to this invention, the raw materials of waterbome coatings which are typically incompatible with each other, are made into compatible liquid blends or slurries prior to formulation. The liquid blends and slurries can then be combined together to obtain a final liquid blend waterbome coating via a continuous, simultaneous or sequential dosing process. The process of making the waterbome coating of this invention uses preferred raw material slurries, such as titanium dioxide slurries and pigment extender slurries, that are preformulated at a viscosity similar to the final paint product. All other liquid blend raw materials, including additives to the formulation, particularly those with narrow compatibility tolerances, such as thickeners, organic solvents, and powders, are preformulated and pre-dispersed in a liquid slurry and preformulated to obtain the desired viscosity characteristics. As used herein, "slurries" is synonymous with intermediates, mixtures, blends, or composites of raw materials, and these terms are used interchangeably. In particular, non-settling titanium dioxide slurries and other raw material slurries, are utilized in this invention, having viscosities substantially the same as the desired final waterbome coating. Typically, aqueous slurries of titanium dioxide pigment are prepared by mixing titanium dioxide pigment powder with dispersants and other additives with water in a batch mixer and stirred for a long time until the required percentage of solids and degree of dispersion is achieved in the slurry. Storage tanks hold the mixed slurry, but there must always be a high degree of agitation occurring in the tanks to prevent the titanium dioxide pigments in the slurry from settling. Due to the non-settling nature of the slurries of this invention, high agitation is not required. All other liquid raw material slurries or blends are also preformulated at the desired final waterbome coating viscosity. Ultimately, ease of manufacture occurs through the total liquid blending process of this invention. In contrast to a conventional latex process where a large number of raw materials are utilized, and adjustments to pH, viscosity, etc. are usually required, the process of the present invention minimizes the number of raw materials required due to consolidation of raw material components in a liquid blend. This process also eliminates the problems associated with settling and seeding in the final blend. Colored shading bases can also be added during the blending process by accurate dispensing and/or metering. The system allows for the greatest formulation flexibility, as well as the best process and quality control designed system, and also minimizes raw materials while maintaining product mix and lowest effective total operation cost. Titanium Dioxide Slurries The titanium dioxide slurries of this invention have a viscosity of a desired final waterbome coating product. The titanium dioxide slurry can be utilized in a liquid blend paint manufacturing system. The predispersed slurry may be stored for considerable periods of time without settling, although occasional agitation in a storage tank is preferred. The present predispersed titanium dioxide slurry has been found to remain free from agglomerates and remain stable in a storage tank for extended periods of time. This process is repeated for all other dry components such as other pigments and pigment extenders. Said dry components are processed into liquid slurries and stored in the same fashion. Thus, all components utilized by this process are converted to an all liquid system prior to the manufacturing process. Preferably, the titanium dioxide slurry comprises (a) about 50 to 90 percent by weight, based on the total weight of the slurry, of titanium dioxide pigment; (b) about 0.5 to 10 percent by weight, based on the total weight of the slurry, of a glycol; and (c) about 0J to 10 percent by weight, based on the total weight of the slurry, of at least one thickener. The thickener can be selected from the group consisting of polyacrylates, hydroxyethylcellulose, alkali soluble emulsions, hydrophobic ethoxylated urethane resins, and hydrophobically-modified alkali soluble emulsions. Examples of alkali-soluble emulsions and polyacrylates include, but are not limited to, ACRYSOL® ASE-60, ACRYSOL® G-l 11, ASE-75, and ASE-95NP, all commercially available from Rohm & Haas Company. Hydrophobically-modified alkali soluble emulsions and hydrophobic ethoxylated urethane resins are generally known as associated thickeners. Hydrophobically-modified alkali soluble emulsions are generally copolymers of high levels of (meth)acrylic acid with hydrophobic monomers, and hydrophobic ethoxylated urethane resins are generally the reaction products of polyethylene glycols with diisocyanates. Examples of hydrophobically-modified alkali soluble emulsions include, but are not limited to, ACRYSOL® RM-5, RM-6, TT-615, and TT-935 (commercially available from Rohm & Haas). Examples of hydrophobic ethoxylated urethane resins include, but are not limited to, ACRYSOL® RM-825, RM-8W, RM-2020NPR, SCT-275, and RM- 12W (commercially available from Rohm & Haas). Glycols useful for the titanium dioxide slurry, as well as any other slurry of this invention, can be any glycol that can provide wettability to the slurry and help prevent the seeding and/or settling of raw material particulates. Useful glycols can include, but are not limited to, ethylene glycol, propylene glycol, diethylene glycol, dipropylene glycol, and the like. Weight percents of the thickeners are adjusted in order to obtain a viscosity of the titanium dioxide slurry in the range of about 70-125 Krebs units. Extender Slurries The pigment extender slurries such as the calcium carbonate and clay slurries each comprise (a) about 50 to 90 percent by weight, based on the total weight of the slurry, of the extender pigment; (b) about 0.5 to 10 percent by weight, based on the total weight of the slurry, of a glycol; and (c) about 0J to 10 percent by weight, based on the total weight of the slurry, of at least one thickener selected from the group consisting of polyacrylates, hydroxyethylcellulose, alkali soluble emulsions, hydrophobic ethoxylated urethane resins, and hydrophobically-modified alkali soluble emulsions. The thickeners and glycols useful for this slurry is as defined under the titanium dioxide slurries. Weight percents of the thickeners are adjusted in order to obtain a viscosity of the extender slurry in the range of about 70-125 Krebs units. The silica pigment extender slurry comprises (a) about 20 to 50 percent by weight, based on the total weight of the slurry, of the silica; (b) about 0.5 to 10 percent by weight, based on the total weight of the slurry, of a glycol; and (c) about 0J to 10 percent by weight, based on the total weight of the slurry, of at least one thickener selected from the group consisting of polyacrylates, hydroxyethylcellulose, alkali soluble emulsions, hydrophobic ethoxylated urethane resins, and hydrophobically-modified alkali soluble emulsions. The thickeners and glycols useful for this slurry is as defined under the titanium dioxide slurries. Weight percents of the thickeners are adjusted in order to obtain a viscosity of the silica slurry in the range of about 70-125 Krebs units. Preferably, the pigment and pigment extender slurries will also contain one or more dispersants, present in an amount between about 0J to 5%, based on the weight of the slurry. Useful dispersants include organic polyelectrolytes such as 2-amino-2-methyl-l-propanol, triethanolamine, sorbitol, mannitol, water soluble sodium salts, for example, alkali polyphosphates, aliphatic carboxylic acids and alkali salts thereof, polyacrylic acids and alkali salts thereof, polyhydroxy alcohols, amino alcohols, sodium salt of polymeric carboxylic acids, such as Tamol 963, sold by Rohm & Haas, and mixtures thereof. For some applications, the preferred range of dispersants can be in an amount of about 0J to 2.0 weight percent, based on the weight of the slurry. It has been found advantageous to further add to the slurry up to about 10% by weight, based on the total weight of the slurry, of a glycol. A preferred glycol for this invention is ethylene glycol. For some applications, ethylene glycol is present in an amount of about 0.5 to 3 weight percent, based on the weight of the slurry. In addition, other conventional additives may be incorporated into the slurry, such as bactericides, preservatives, defoamers, surfactants, and coalescents. Common bactericides include Proxel GXL, manufactured by ICI, used at a concentration of from about 0.01 to about 2 weight percent of the slurry. Defoamers include Nopco 8034, manufactured by the Nopco Division of Diamond Shamrock Corporation. Surfactants include nonylphenols. Coalescents include Texanols manufactured by Eastman Chemical Company, Kingsport, Tennessee. Glycol Slurry Glycol slurries useful for this invention comprises (a) about 5 to 50 percent by weight, based on the total weight of the slurry, of a glycol selected from the group consisting of ethylene glycol, propylene glycol, etc.; and (b) about 1 and 50 percent by weight, based on the total weight of the slurry, of at least one thickener selected from the group consisting of polyacrylates, hydroxyethylcellulose, alkali soluble emulsions, hydrophobic ethoxylated urethane resins, and hydrophobically-modified alkali soluble emulsions. Examples of the thickeners are the same as provided under the titanium dioxide slurries. Weight percents of the thickeners are adjusted in order to obtain a viscosity of the glycol slurry in the range of about 70-125 Krebs units. The slurry is made by admixing a glycol, such as ethylene glycol, with at least one thickener, dispersing with a high speed mixer, then admixing defoamer, coalescent, and cosolvent. Mixing is maintained as thickener and buffer are added to complete the slurry. Thickener Slurry The thickener slurry useful for this invention comprises about 5 to 30% by weight, based on the total weight of the slurry, of at least one thickener selected from the group consisting of polyacrylates, hydroxyethylcellulose, alkali soluble emulsions, hydrophobic ethoxylated urethane resins, and hydrophobically-modified alkali soluble emulsions. Examples of the thickeners are the same as provided under the titanium dioxide slurries. Most preferred is the alkali-soluble emulsions and the hydrophobically-modified alkali-soluble emulsions. Polyacrylates, hydroxyethylcellulose, though a possible thickener, is least desirable due to its dry form and difficulty to incorporate into the slurry. It is essential that the pH of the thickener slurry be in the range of about 5.5 to 6.5. The viscosity of the thickener slurry is in the range of about 70-125 Krebs units. Coating Composition According to this invention, various waterbome coating compositions can be prepared by blending the above-referenced slurries with at least one latex binder having substantially the same viscosity as the desired final waterbome product. The waterbome coating composition can comprise about 0-70 weight percent of the titanium dioxide dioxide slurry, 0 to 50 weight percent of at least one pigment extender slurry selected from the group consisting of calcium carbonate slurry, clay slurry, and silica slurry; 0.5 to 10 weight percent of a glycol slurry; and about 1 to 20 weight percent of a thickener slurry, and the remaining amount being a latex binder. The thickener can be selected from the group consisting of polyacrylates, hydroxyethylcellulose, alkali soluble emulsions, hydrophobic ethoxylated urethane resins, and hydrophobically-modified alkali soluble emulsions, all based on the total weight of the coating composition. The slurries are admixed and blended with at least one latex binder to form a final waterbome coating composition. The latex can be any commercially available latex polymer. The latex binder may be a dispersed polymer having polymer particles dispersed in an aqueous evaporable carrier or it may be either a water soluble polymer, a water-reducible polymer, a mixture of the water soluble and water-reducible polymers in the aqueous evaporable carrier, or a mixture of the dipsersed, water-reducible and water soluble polymers in the aqueous evaporable carrier. If desired, the latex binder may include a mixture of a dispersed polymer with a water soluble or a water-reducible polymer. The latex polymer suitable for use in the present invention includes an emulsion polymer of mono- or poly-ethylenically unsaturated olefmic, vinyl or acrylic monomers, including homopolymers and copolymers of such monomers. Specifically, the dispersed polymer may include poly(vinyl acetate) and copolymers of vinyl acetate with one or more of vinyl chloride, vinylidene chloride, styrene, vinyltoluene, acryluonitrile, methacrylonitrile, acrylamide, methacrylamide, maleic acid and esters thereof, or one or more of the acrylic and methacrylic acid esters, which polymers are well-known as the film-forming component of aqueous base paints; homopolymers of C2-C40 alpha- olefins such as ethylene, isobutylene, octene, nonene, and styrene; copolymers of one or more of these hydrocarbons with one or more esters, nitriles, or amides of acrylic acid or of methacrylic acid or with vinyl esters, such as vinyl acetate and vinyl chloride, or with vinylidene chloride; and diene polymers, such as copolymers of butadiene with one or more of styrene, vinyl tolutene, acrylonitrile, methacrylonitrile, and esters of acrylic acid or methacrylic acid. The vinyl acetate copolymers are well-known and include copolymers such as vinyl acetate/butyl acrylate/2-ethylhexyl acrylate, vinyl acetate/butyl maleate, vinyl acetate/ethylene, vinyl acetate/vinyl chloride/butyl acrylate and vinyl acetate/vinyl chloride/ethylene. Other suitable monomers from which the latex binder may be polymerized from include at least one or more of the following monomers, such as, for example, acrylic and methacrylic ester monomers including methyl (meth) acrylate, ethyl (meth)acrylate, butyl (meth)acrylate, 2-ethylhexyl (meth)acrylate, decyl (meth)acrylate, lauryl (meth)acrylate, isobornyl (meth)acrylate, isodecyl (meth)acrylate, oleyl (meth)acrylate, palmityl (meth)acrylate, stearyl (meth)acrylate, hydroxyethyl (meth)acrylate, and hydroxypropyl (meth)acrylate; acid functional monomers, such as acrylic acid, methacrylic acid, crotonic acid, itaconic acid, famuric acid and maleic acid; monomethyl fumarate; monobutyl fumarate; maleic anhydride, acrylamide or substituted acrylamides; sodium vinyl sulfonate; phosphoethyl (meth)acrylate; acrylamido propane sulfonate; diacetone acrylamide; glycidyl methacrylate; acetoacetyl ethylmethacrylate; acrolein and methacrolein; dicyclopentadienyl methacrylate; dimethyl meta-isopropenyl benzyl isocyanate; isocyanato ethyl-methacrylate; styrene or substituted styrenes; butadiene; ethyleen; vinyl acetate or other vinyl esters, N-vinyl pyrrolidone; amino monomers, such as for example, N, N'-dimethylamino and (meth)acrylate. Preferably, the final waterbome product will have a viscosity substantially the same as each of the slurries, and preferably in the range of about 70-125 Krebs units. Preservatives, defoamers, freeze-thaw agents, and fungicides/mildewcides may be used in the coating composition at concentrations from about 0J to about 10 weight percent, based on the total weight of the coating composition. Shading bases may be added to the coating composition and further blended. The waterbome coating composition of this invention, having predetermined viscosity characteristics can be prepared utilizing a total liquid blend process. A plurality of liquid blend raw materials can be admixed to produce the waterbome coating product. The process can include providing a plurality of reservoirs containing liquid blends of raw materials, each liquid blend of raw materials have substantially the same viscosities, then admixing a controlled amount of the liquid blends from said reservoirs in a mix tank having an appropriate agitation means, such as an impeller or other agitation means known in the art, and then producing a final liquid blend waterbome coating product by exposing the liquid blend slurries in said mix tank with said agitation means. The liquid blend raw materials can include latex binders, titanium dioxide slurries, extender pigment slurries, thickener slurries, and the like, and mixtures thereof. The thickener can be selected from the group consisting of polyacrylates, hydroxyethylcellulose, alkali soluble emulsions, hydrophobic ethoxylated urethane resins, and hydrophobically-modified alkali soluble emulsions. Preferably, the pH of the thickener slurry is in the range of between 5.5 to 6.5. Preferably, the viscosity of the final waterbome coating is in the range of about 70-125 Krebs units. The following examples illustrate the invention but are not intended to limit it thereto. EXAMPLES The pigment slurries are generally prepared by subjecting a pigment with dispersing treatment using a high speed mixer, admixing the dispersed pigment slurry with a glycol, adding at least one thickener which can be selected from the group consisting of polyacrylates, hydroxyethylcellulose, alkali soluble emulsions, hydrophobic ethoxylated urethane resins, and hydrophobically-modified alkali soluble emulsions; and forming an aqueous pigment slurry by dispersing with a mixer. EXAMPLE 1 Titanium Dioxide Slurry An aqueous titanium dioxide slurry can be made according to the formula in Table I. The aqueous Ti02 slurry is prepared by subjecting Ti02 with a water and dispersant mixture, dispersing with a high speed mixer, then admixing defoamer, a glycol, and cosolvent. Mixing is maintained as thickener, buffer, and biocide are added to complete the slurry. (TiPure® titanium dioxide is manufactured by E.I. duPont deNemours & Company.) A titanium dioxide slurry at 61% solids can be prepared according to the following formula listed in the following table: Weight Weight % Description dbs/100 eal) in Slurrv Water Solvent 514 34.67 TKPP (Potassium TriPolyPhosphate) D Diissppeerrssaanntt 2 1.3 Tamol 963 Dispersant 18 1.21 Nonylphenol Surfactant 3 2.0 Ti-Pure® R931 titanium dioxide Pigment 890 60.0 Nopco 8034 Defoamer 1 0.07 Ethylene Glycol 27 1.82 Texanol Coalescent 13.5 0.91 Acrysol TT-935 Thickener 6 0.40 Acrysol TT-615 Thickener 2 0.13 Ammonia Buffer 5 0.34 Proxel GXL Biocide 1 0.07 The titanium dioxide slurry may further comprise an extender selected from the group consisting of calcium carbonate, clay, silica, and others. The titanium dioxide slurry is dispersed at high shear having an impeller sufficient to deagglomerate the titanium dioxide. The dispersed slurry has a Krebs Stormer viscosity in the range of about 70-125 Krebs units, and a solids content of about 60-75%. EXAMPLE 2 Calcium Carbonate Slurry The aqueous calcium carbonate slurry can be prepared by subjecting precipated calcium carbonate 325 mesh with a water and dispersant mixture, dispersing with a high speed mixer, then admixing defoamer, a glycol, and cosolvent. Mixing is maintained as thickener, buffer, and biocide are added to complete the slurry. Weight Description (Tbs/100 eaT) % in Slurrv Water Solvent 410.41 28.00 Tamol 963 Dispersant 10.8 7.4 Nonylphenol Surfactant 3 2J Calcium Carbonate Pigment 995 68.0 Nopco 8034 Defoamer 1 0.07 Ethylene Glycol 20 1.37 Texanol Coalescent 10 0.68 Acrysol TT-935 Thickener 8.6 0.59 Acrysol TT-615 Thickener 2.9 0.20 Proxel GXL Biocide 1 0.07 The dispersed slurry has a Krebs Stormer viscosity in the range of about 70-125 Krebs units, and a solids content of about 60-75%. EXAMPLE 3 Silica Slurry The silica slurry is prepared by subjecting Celite® diatomaceous earth with a water and dispersant mixture, dispersing with a high speed mixer, then admixing defoamer, a glycol, and cosolvent. Mixing is maintained as thickener, buffer, and biocide are added to complete the slurry. Weight Description (lbs/100 sal) % in Slurry Water Solvent 678 68.0 TKPP (Potassium TriPolyPhosphate) D Diissppeerrssaanntt 2 0.2 Tamol 963 Dispersant 6 0.6 Nonylphenol Surfactant 1 0J Celite 400P Pigment 262 27.0 Nopco 8034 Defoamer 1 0J0 Ethylene Glycol 6 0.62 Texanol Coalescent 3 0.31 Acrysol TT-935 Thickener 8.4 0.86 Acrysol TT-615 Thickener 2.8 0.29 Ammonia Buffer 1 0J0 Proxel GXL Biocide 1 0J0 The dispersed slurry has a Krebs Stormer viscosity in the range of about 70-125 Krebs units, and a solids content of about 20-35%. EXAMPLE 4 Thickener Slurry The aqueous thickener slurry is prepared by admixing the following raw materials with a high speed mixer: Weight Description dbs/100 sal) % in Slurry Water Solvent 651.6 77.8 Nopco 8034 Defoamer 5 0.60 Acrysol TT-935 Thickener 130 0J5 Acrysol TT-615 Thickener 43.3 5.17 Ammonia Buffer 6.5 0.78 Proxel GXL Biocide 1 0.12 It is critical to this invention that the pH of the thickener solution be in the range of about 5.5 to 6.5. The thickener slurry has a Krebs Stormer viscosity in the range of about 70-125 Krebs units, and a solids content of about 5-10%. EXAMPLE 5 Glycol Slurry The aqueous glycol slurry is prepared by admixing the following raw materials with a high speed mixer: Weight Description (lbs/100 gal) % in Slurry Water Solvent 506.6 36.84 Nonylphenol Surfactant 7.5 0.55 Nopco 8034 Defoamer 44.9 3.26 Ethylene Glycol 506.6 36.84 Texanol Coalescent 252 18.32 Acrysol TT-935 Thickener 40 2.91 Acrysol TT-615 Thickener 13 0.95 Ammonia Buffer 4.6 0.33 The glycol slurry has a Krebs Stormer viscosity in the range of about 70-125 Krebs units, and a solids content of about 5-10%. One or more of the above slurries, having the desired viscosity characteristics, can be used to produce the waterbome coatings of this invention having substantially the same viscosity characteristics. The slurries can be stored in respective reservoirs, and then directly blended within a processing vessel equipped with mixing means, without the need for grinding or high shear mixing. The manufacturing process can be controlled through computer means or manually dispensed. A typical computer control system can control pump speeds, rates, and quantities of additions of components, and measurements taken on-line by various instrumentation. The order of addition of the liquid raw material slurries/blends is not critical to this invention. Shading bases can also be blended during the raw material blending process to form a finished product. The color shading bases are added after formula blending has occurred by accurate dispensing or metering. COMPARATIVE EXAMPLES As a comparison example, a batch of latex paint was formulated using a conventional paint making process. The formulation is listed in Table I. COMPARATIVE EXAMPLE 1 Conventional Process Formula Grind: The following pigment dispersion is prepared using the ingredients in the following order, and subjected to a dispersing treatment by using a high speed disperser. Weight Description (lbs/100 gal) % Weight Water Solvent 142.5164 13.3726 TKPP (Tetrapotassium Pyrophospahte) Dispersant 0.7073 0.5554 Tamol 963 Dispersant 5.2948 2.0903 Nonylphenol Surfactant 1.3953 0.5975 Nopco 8034 Defoamer 1.2600 0.6283 Ti-Pure® R931 Pigment 228.0941 28.5306 325 Mesh PPT CaCO3 Pigment Extender 61.2491 10.2714 Ethylene Glycol 37.2989 15.2659 Texanol Coalescent 18.5734 8.8880 Water 120.0000 54.7292 The above grind is then pumped to a letdown tank, and the following raw materials are then added: Rovace 661 Vinyl Acrylic Latex 425.000 39.8785 Nopco 8034 Defoamer 2.000 0.1877 Acrysol TT-935 Thickener 13.0844 1.2277 Acrysol TT-615 Thickener 4.3394 0.4072 Ammonia Buffer 2.9731 0.2790 Omacide IPBC 40% Mildewcide 1.0000 0.0938 Proxel GXL Biocide 0.9500 0.0891 The batch is adjusted for pH, color, and viscosity. COMPARATIVE EXAMPLE 2: A second batch of the same latex paint was formulated using the slurries and process of the present invention: Weight (lbs/100 ear) % Weight Water 33.1965 3.1149 Titanium Dioxide Slurry 380.0000 35.6561 (Example 1) Calcium Carbonate Slurry 120.0000 11.2598 (Example 2) Glycol Slurry 50.0000 4.6916 (Example 5) Thickener Slurry 55.0000 5.1608 (Example 4) Rovace 661 425.0000 39.8785 Omacide IPBC 40% 1.0000 0.0938 Proxel GXL 0.5400 0.0507 Ammonia ' 1.0000 0.0938 The above slurries are blended together into a mix tank or container, with no dispersion necessary. The product does not require adjustments for pH, color, or viscosity.

Claims: CLAIMS: 1. A waterbome coating composition comprising: a) about 0 to 70 percent by weight, based on the total weight of the composition, of a titanium dioxide slurry; b) about 0 to 75 percent by weight, based on the total weight of the composition, of at least one extender pigment slurry; c) about 1 to 20 percent by weight, based on the total weight of the composition, of a thickener slurry; and d) about 1 to 10 percent by weight, based on the total weight of the composition, of a glycol slurry; and e) at least one latex binder. 2. The coating composition of claim 1, wherein the viscosity of said coating composition is substantially the same as the viscosity of any one of the slurries. 3. The coating composition of claim 1 , wherein the viscosity of said waterbome coating is in the range of about 70-125 Krebs units. 4. The coating composition of claim 1, wherein the thickener slurry comprises at least one thickener selected from the group consisting of polyacrylates, hydroxyethylcellulose, an alkali soluble emulsions, a hydrophobic ethoxylated urethane resins, and a hydrophobically- modified alkali soluble emulsions 5. The coating composition of claim 1, wherein the at least one extender pigment slurry can be selected from the group consisting of calcium carbonate slurry, silica slurry, and kaolin clay slurry. 6. The coating composition of claim 1 , wherein the pH of said thickener slurry is in the range of between 5.5 to 6.5. 7. The coating composition of claim 1, wherein the titanium dioxide slurry comprises: a) about 50 to 90 percent by weight, based on the total weight of the slurry, of titanium dioxide pigment b) about 0.5 to 10 percent by weight, based on the total weight of the slurry, of a glycol; and c) about 0J to 5.0 percent by weight, based on the total weight of the slurry, of at least one thickener; and wherein the viscosity of said titanium dioxide slurry is in the range of about 70-125 Krebs units. 8. The coating composition of claim 7, wherein the thickener can be selected from the group consisting of polyacrylates, hydroxyethylcellulose, alkali soluble emulsions, hydrophobic ethoxylated urethane resins, and hydrophobically-modified alkali soluble emulsions. 9. The coating composition of claim 1, wherein the calcium carbonate slurry comprises a) about 50 to 75 percent by weight, based on the total weight of the slurry, of a calcium carbonate pigment; b) about 0.5 to 10 percent by weight, based on the total weight of the slurry, of a glycol; and c) about 0J to 5.0 percent by weight, based on the total weight of the slurry, of at least one thickener; and wherein the viscosity of said calcium carbonate slurry is in the range of about 70-125 Krebs units. 10. The coating composition of claim 9, wherein the thickener can be selected from the group consisting of polyacrylates, hydroxyethylcellulose, alkali soluble emulsions, hydrophobic ethoxylated urethane resins, and hydrophobically-modified alkali soluble emulsions. 11. The coating composition of claim 1, wherein the silica slurry comprises d) about 20 to 50 percent by weight, based on the total weight of the slurry, of a silica pigment; e) about 0.5 to 10 percent by weight, based on the total weight of the slurry, of a glycol; and f) about 0J to 5.0 percent by weight, based on the total weight of the slurry, of at least one thickener; and wherein the viscosity of said silica slurry is in the range of about 70-125 Krebs units. 12. The coating composition of claim 11, wherein the thickener can be selected from the group consisting of polyacrylates, hydroxyethylcellulose, alkali soluble emulsions, hydrophobic ethoxylated urethane resins, and hydrophobically-modified alkali soluble emulsions. 13. The coating composition of claim 1, wherein the kaolin clay slurry comprises a) about 50 to 75 percent by weight, based on the total weight of the slurry, of a kaolin clay pigment; b) about 0.5 to 10 percent by weight, based on the total weight of the slurry, of a glycol; and c) about 0J to 10 percent by weight, based on the total weight of the slurry, of at least one thickener selected from the group consisting of polyacrylates, hydroxyethylcellulose, alkali soluble emulsions, hydrophobic ethoxylated urethane resins, and hydrophobically- modified alkali soluble emulsions. 14. The coating composition of claim 13, wherein the thickener can be selected from the group consisting of polyacrylates, hydroxyethylcellulose, alkali soluble emulsions, hydrophobic ethoxylated urethane resins, and hydrophobically-modified alkali soluble emulsions. 15. A method for the preparation of a waterbome coating composition comprising: (a) providing a plurality of liquid blend raw materials; and (b) admixing the liquid blend raw materials to produce the waterbome coating product. 16. The method of claim 15, wherein said liquid blend raw materials can be selected from the group consisting of latex binders, titanium dioxide slurries, extender pigment slurries, thickeners, thickener slurries, glycol slurries, and mixtures thereof. 17. The method of claim 15, wherein the waterbome coating product has a predetermined viscosity. 18. The method of claim 15, wherein the waterbome coating product has substantially the same viscosity as the liquid blend slurries. 19. The method of claim 15 , wherein the viscosity of said waterbome coating is in the range of about 70-125 Krebs units. 20. The method of claim 16, wherein the extender pigment slurries can be selected from the group consisting of calcium carbonate slurry, silica slurry, and kaolin clay slurry, or mixtures thereof. 21. The method of claim 16, wherein the thickener can be selected from the group consisting of polyacrylates, hydroxyethylcellulose, alkali soluble emulsions, hydrophobic ethoxylated urethane resins, and hydrophobically-modified alkali soluble emulsions. 22. The method of claim 15, wherein each liquid blend slurry has substantially the same viscosity. 23. A pigment slurry comprising: a) about 20 to 90 percent by weight, based on the total weight of the slurry, of a pigment; b) about 0.5 to 10 percent by weight, based on the total weight of the slurry, of a glycol; and c) about 0J to 10 percent by weight, based on the total weight of the slurry, of at least one thickener; and wherein the Stormer viscosity of said pigment slurry is in the range of about 70-125 Krebs units. 24. The pigment slurry of claim 23, wherein the thickener can be selected from the group consisting of polyacrylates, hydroxyethylcellulose, alkali soluble emulsions, hydrophobic ethoxylated urethane resins, and hydrophobically-modified alkali soluble emulsions. 25. The pigment slurry of claim 23, wherein the pigment can be selected from the group consisting of titanium dioxide, calcium carbonate, silica, and kaolin clay, or mixtures thereof. 26. The pigment slurry of claim 23, wherein the pigment is about 50 to 70 percent by weight, based on the total weight of the slurry, of titanium dioxide. 27. The pigment slurry of claim 23, wherein the pigment is about 50 to 75 percent by weight, based on the total weight of the slurry, of calcium carbonate. 28. The pigment slurry of claim 23, wherein the pigment is about 20 to 50 percent by weight, based on the total weight of the slurry, of silica. 29. The pigment slurry of claim 23, wherein the pigment is about 50 to 75 percent by weight, based on the total weight of the slurry, of kaolin clay. 30. A glycol slurry comprising: a) about 5 to 50 percent by weight, based on the total weight of the slurry, of a glycol; and b) about 1 and 50 percent by weight, based on the total weight of the slurry, of at least one thickener; and wherein the viscosity of said glycol slurry is in the range of about 70-125 Krebs units. 31. The glycol slurry of claim 30, wherein the at least one thickener can be selected from the group consisting of polyacrylates, hydroxyethylcellulose, alkali soluble emulsions, hydrophobic ethoxylated urethane resins, and hydrophobically-modified alkali soluble emulsions. 32. A method for the preparation of an aqueous pigment slurry which comprises the steps of: a) dispersing a pigment with water to form an aqueous pigment slurry; b) admixing the dispersed aqueous pigment slurry with a glycol; c) adding to the admixture at least one thickener; and d) dispersing the mixture to form an aqueous pigment slurry. 33. The method of claim 32, wherein the pigment can be selected from the group consisting of titanium dioxide, calcium carbonate, silica, kaolin clay, or mixtures thereof. 34. The method of claim 32, wherein the thickener can be selected from the group consisting of polyacrylates, hydroxyethylcellulose, alkali soluble emulsions, hydrophobic ethoxylated urethane resins, and hydrophobically-modified alkali soluble emulsions. 35. The method of claim 32, wherein the pigment slurry comprises between about 20 to 75% by weight, based on the total weight of the slurry, of the pigment. 36. The method of claim 32, wherein the pigment slurry comprises between about 0.5 to 10% by weight, based on the total weight of the slurry, of the glycol. 37. The method of claim 32, wherein the pigment slurry comprises between about 0J to 10% by weight, based on the total weight of the slurry, of the at least one thickener.

Inventors: MULLEN BRIAN A, NEMUNAITIS DANIEL P, PATKA JOHN J SR, SWEITZER GERALD M, MULLEN, BRIAN, A., NEMUNAITIS, DANIEL, P., PATKA, JOHN, J., SR., SWEITZER, GERALD, M.
Applicants: MULLEN BRIAN A, NEMUNAITIS DANIEL P, PATKA JOHN J SR, SHERWIN WILLIAMS CO, SWEITZER GERALD M, MULLEN, BRIAN, A., NEMUNAITIS, DANIEL, P., PATKA, JOHN, J., SR., SWEITZER, GERALD, M., THE SHERWIN-WILLIAMS COMPANY
Application year: 2001
Main classification: C09D5
IPC codes: C09D5