Olefin-based resin composition

Abstract: There is provided an olefin-based resin composition applied to the coatings of electrical cables used in automobiles. The coatings have neatly balanced properties to satisfy the product requirements, such as wear and flame resistance, tensile strength, flexibility, and heat and freeze resistance. The olefin-based resin composition comprises: (i) a polymeric material in an amount of 100 parts by weight which includes: (a) a propylene-type polymer portion; (b) a polyolefin portion treated with maleic acid anhydride; and (c) an olefin-type polymer portion; and (ii) a metal hydroxide product. The propylene-type polymer portion (a) comprises at least one propylene polymer accounting for a proportion of 50 to 80% by weight of the polymeric material (i). The polyolefin portion treated with maleic acid anhydride (b) comprises at least one polyolefin, a proportion of 0.1 to 10% by weight of which are structurally modified through maleic acid anhydride treatment, and accounts for 1 to 20% by weight of the polymeric material (i). The olefin-type polymer portion (c) comprises at least one thermoplastic resin having a melting point of at least 130°C and a Shore A hardness of 90 at the most, and accounts for 10 to 40% by weight of the polymeric material (i). The metal hydroxide product (ii) comprises at least one metal hydroxide in an amount of 30 to 200 parts by weight relative to the polymeric material (i).

Description: The present invention relates to olefin-based resin compositions, and more particularly halogen-free olefin-based resin compositions. These compositions are used for coating electrical cables used in automobiles. The above compositions must therefore satisfy the prerogatives of the automobile industry, as regards e.g. wear resistance, flame resistance, tensile strength and flexibility. Poly (vinylchloride) has mainly been used as a coating material for automobile electrical cables. The reason is that this polymer has a good mechanical strength, formability at extrusion with electrical cables, flexibility and paintability. The polymer is also an inexpensive material. Recently, however, global environmental concerns have compelled the automobile industry to reconsider the choice of product types used for automobile parts, including the coatings of electrical cables. As a result, halogen-free resin materials are currently replacing poly (vinylchloride). Accordingly, research has been undertaken into the wear-resistant resin compositions that do not generate toxic gases, such as halogen gases, when they are burned. Such compositions include halogen-free compositions containing a polyolefin-based polymer and a metal hydroxide as a flame retardant, as disclosed in Japanese patent applications published under Nos. HEI 7-176219 and HEI 7-78518. Further, Japanese patent application published under No. HEI 7-182930 describes a composition containing a polymeric material consisting of a polypropylene-type resin, a polyethylene treated with an unsaturated carboxylic acid, and an ethylene-type copolymer, on the one hand, and a metal hydroxide, on the other. However, when such disclosed compositions are used in order to retard combustion or perform auto-extinction of the flame, a large amount of metal hydroxides must be added to the compositions. The mechanical strength of the compositions, such as wear resistance and tensile strength, is then greatly diminished. In order to avoid such a deterioration, polypropylene or a high-density polyethylene, which is a relatively hard resin, has been added to the compositions. However, this tends to degrade the flexibility and formability of the coated electrical cables. An object of the present invention is therefore to provide an olefin-based resin composition which is free of halogen and has well-balanced properties required for the coatings of electrical cable used in automobiles. These properties include wear resistance, flame resistance, tensile strength, flexibility, heat resistance and low-temperature resistance. To this end, there is provided an olefin-based resin composition comprising: (i) a polymeric material in an amount of 100 parts by weight which includes: (a) a propylene-type polymer portion; (b) a polyolefin portion treated with maleic acid anhydride; and (c) an olefin-type polymer portion; and (ii) a metal hydroxide product; wherein the propylene-type polymer portion (a) comprises at least one propylene polymer accounting for a proportion of about 50 to about 80% by weight of the polymeric material (i); the polyolefin portion treated with maleic acid anhydride (b) comprises at least one polyolefin, a proportion of about 0.1 to about 10% by weight of which are structurally modified through maleic acid anhydride treatment, the polyolefin portion accounting for about 1 to about 20% by weight of the polymeric material (i); the olefin-type polymer portion (c) comprises at least one thermoplastic resin having a melting point of at least about 130°C and a Shore A hardness of about 90 at the most, the olefin-type polymer portion accounting for about 10 to about 40% by weight of the polymeric material (i); and the metal hydroxide product (ii) comprises at least one metal hydroxide in a an amount of about 30 to about 200 parts by weight relative to the polymeric material (i). Preferably, the polyolefin portion treated with maleic acid anhydride (b) accounts for about 2 to about 10% by weight of the polymeric material (i), the olefin-type polymer portion (c) accounts for about 20 to about 30% by weight of the polymeric material (i), and the metal hydroxide product (ii) comprises at least one metal hydroxide in a an amount of about 50 to about 150 parts by weight relative to the polymeric material (i). Preferably yet, the metal hydroxide product (ii) comprises at least one metal hydroxide in an amount of about 70 to about 90 parts by weight relative to the polymeric material (i). Suitably, the propylene-type polymer portion (a) has a melt flow rate of about 0.1 to about 5g/10 minutes. Further, the propylene-type polymer portion (a) may comprise at least one polymer selected from the group consisting of a propylene-ethylene block copolymer, a propylene-ethylene random copolymer and a propylene homopolymer. Preferably, the polyolefin portion treated with maleic acid anhydride (b) may at least comprise polypropylene structurally modified through maleic acid anhydride treatment. Preferably yet, the olefin-type polymer portion (c) comprises at least one polymer made of polypropylene and propylene-ethylene copolymer. Suitably, the metal hydroxide product (ii) is treated with a silane-type coupling agent. Preferably, the silane-type coupling agent comprises an aminosilane-type coupling agent. As understood from the foregoing, the olefin-based resin composition according to the invention is substantially free of halogen. The invention further concerns an electrical cable coated with such an olefin-based resin composition. The above and the other objects, features and advantages of the invention will be made apparent from the following description of the preferred embodiments, given as non-limiting examples. The propylene-type polymer portion (a) used includes, for example, propylene homopolymer, a block or random copolymer of propylene and ethylene. Preferably, the propylene-type polymer portion (a) has a melt flow rate (MFR) of 0.1 to 5/10 min. MFR is measured according to the method based on Standard JIS K 6921-2. Examples of such propylene polymers include RB610A (block copolymer), RB410 (random copolymer) and RB110 (homopolymer), manufactured and commercialized by TOKUYAMA CORP. When the proportion of such a propylene-type polymer portion exceeds the above-mentioned upper limit of about 80% by weight of the polymeric material (i), the composition obtained becomes less flexible and less formable. Conversely, when its proportion is less than the lower limit of about 50% by weight, the composition obtained becomes less resistant to wear. Examples of organic acid anhydrides used for treating a polyolefin portion include a carboxylic acid anhydride, e.g. maleic acid anhydride, a proportion of about 0.1 to about 10 % by weight of which polyolefin portion are treated with such carboxylic acid anhydride. Examples of such anhydride-treated polyolefin portion (b) include polyethylene, polypropylene, polybutene, ethylene-vinyl acetate copolymer (EVA), ethylene-ethyl acrylate copolymer (EEA), ethylene- methyl acrylate copolymer (EMA), ethylene-methyl methacrylate copolymer, ethylene-propylene rubber and ethylene-butene copolymer. A preferred example is polypropylene treated with maleic acid anhydride, since it gives the inventive composition having a sufficient level of hardness and wear resistance without performing cross-linking. The proportion of acid-anhydride-treated polyolefin portion (b) in the polymeric material (i) ranges from 1 to 20, preferably from about 2 to about 10% by weight. When its proportion exceeds the upper limit of about 20% by weight, the polyolefin portion (b) reacts strongly with the metal hydroxide, so that tensile elongation (elongation rate at breaking point) of the composition is reduced, and its flexibility is impaired. Conversely, when its proportion is less than the lower limit of about 1 % by weight, the wear resistance of the composition cannot be improved. Thermoplastic resins as an olefin-type polymer portion (c) is a polymer formed of polypropylene and propylene-ethylene copolymer. Examples include "PER R410E" and "PER T310J", manufactured and commercialized by TOKUYAMA CORP. The thermoplastic resins have a melting point of at least about 130°C and a Shore A hardness of about 90 at the most. When the melting point is less than about 130°C, the composition may not be sufficiently heat-resistant The proportion of thermoplastic resins as a olefin-type polymer portion (c) in the polymeric material (i) ranges from about 10 to about 40, preferably from about 20 to about 30% by weight. When this proportion exceeds the upper limit of about 40% by weight, the composition becomes less resistant to wear. Conversely, when its proportion is less than the lower limit of about 10% by weight, the composition becomes too hard and less formable. Examples of the metal hydroxide product (ii) include magnesium hydroxide and aluminum hydroxide, preferably in their particle state. Suitably, metal hydroxide particles used in the invention are treated with a coupling agent, preferably a silane-type coupling agent and a higher fatty acid. The silane-type coupling agent includes e.g. an aminosilane-type coupling agent, a vinylsilane coupling agent and an epoxysilane coupling agent. Examples of higher fatty acid include stearic acid and oleic acid. Among the above examples, magnesium hydroxide treated with a silane-type coupling agent, in particular with an aminosilane-type coupling agent, is most preferably used. The part of metal hydroxide product (ii) added to the polymeric material (i) ranges from about 30 to about 200, preferably from about 50 to about 150, more preferably from about 70 to about 90 parts by weight. When the part of metal hydroxide product (ii) is too high, the composition suffers drops in elongation rate, wear resistance, flexibility and formability. On the other hand, when its part is too low, flame resistance of the composition is degraded. The olefin-based resin composition of the present invention may further contain an appropriate amount of usual additives, such as anti-oxidants, copper-damage inhibitors and lubricants, insofar as they do not impair the above-described product features. The inventive olefin-based resin composition can be prepared by mixing and kneading the polymeric material (i) and the metal hydroxide product (ii) supra according to a known method. When the inventive composition is applied to the coatings of electrical cables used in automobiles, these coatings satisfy requirements in terms of wear resistance, flame resistance, tensile strength, flexibility, heat resistance, freeze resistance, etc.. Obviously, these coatings generate no halogen gas. The aminosilane-type coupling agents contain, in their molecule, functional groups reacting with inorganic compounds and those reacting with organic compounds. Accordingly, when a metal hydroxide is treated with an aminosilane-type coupling agent, they are bonded through those functional groups reacting with inorganic compounds. When the metal hydroxide thus treated is added to the composition of the invention, it becomes firmly bound to the organic acid anhydride (e.g. maleic acid anhydride) combined with the polyolefin portion (b) or the olefin-type polymer portion (c), through the aminosilane's functional groups which react with organic compounds. As a result, wear resistance of the inventive composition is markedly improved. When an amino group (as in the above case) and/or an epoxy group is (are) present at the oleophilic group side of the silane-type coupling agent, that or those group(s) react(s) with the organic acid anhydride which is bound with the polyolefin portion (b) or the olefin-type polymer portion (c). The hydrophilicity of the inventive composition therefore decreases, and its waterproofing increases. As a result, the composition procures not only a better mechanical strength, but also better water-resisting qualities. The present invention will be described hereafter with reference to examples and comparative examples. Examples 1 to 3 and Comparative Examples 1 to 4 The components indicated in the upper part of the corresponding columns in Tables I and II were mixed in indicated amounts. The resultant mixtures were kneaded in a biaxial extruder at 250°C. The obtained compositions were extruded around a conductive cable regulated by ISO as 0.5sq (7/0.32 soft copper wires, indicating seven wires with a diameter of 0.32mm, and forming a conductor with a cross-section area of 0.5mm 2 ), to yield a coating thickness of 0.3mm. The extrusion was performed in dies having a diameter of 1.6mm and 1.0mm, respectively, and nipples; at a die temperature of 210 to 230°C and a cylinder temperature of 200 to 240°C; and at a line speed of 100m/min. The terms in Tables are defined as follows. "Propylene BP" indicates a propylene-ethylene block copolymer having a MFR of 0.5g/10 min. An example of such block copolymer is "RB610A" manufactured by TOKUYAMA CORP.. "MAH-PP" indicates a polypropylene, 1% by weight of which is treated with maleic acid anhydride. "PER" indicates "R410E" or "T310J" manufactured by TOKUYAMA CORP.. "MAGNIFIN H5IV" indicates magnesium hydroxide treated with an aminosilane-type coupling agent, manufactured by ALUSUISSE MARTINSWERK GmbH. The anti-aging agent used is a hindered phenol type compound. An example of such compound is "TOMINOX TT", manufactured by YOSHITOMI FINECHEMICALS, Ltd.. The coated electrical cables of Examples 1 to 3 and Comparative Examples 1 to 4 were subjected to tests for flame resistance, tensile strength, elongation rate and wear resistance according to JASO D611 (Japanese Automobile Standard Organization). To test wear resistance, an abrasion frequency exceeding 300 times, averaged on 3 samples, was considered as good. Flexibility was evaluated by hand feeling, when coated electrical cables were bent. Formability was evaluated by observing whether or not whiskers were formed, when coatings were stripped off from the end portion of the coated electrical cables. The results of the tests are shown in the lower part of the corresponding columns in Tables I and II. Example 1 Example 2 Example 3 Propylene BP 60 65 68 MAH-PP 10 5 2 PER 30 30 30 MAGNIFIN H5IV 90 90 90 Anti-aging agent 1 1 1 Total 191 191 191 Flame resistance Good Good Good Tensile strength (Mpa) 39.2 38.3 37.4 Elongation rate (%) 417 527 613 Wear resistance (frequencies) 6539 2594 1201 Flexibility Good Good Good Formability Good Good Good Comparative Example 1 Comparative Example 2 Comparative Example 3 Comparative Example 4 Propylene BP 90 40 90 55 MAH-PP 30 10 5 PER 10 30 40 MAGNIFIN H5IV 120 100 80 300 Anti-aging agent 1 1 1 1 Total 221 201 181 401 Flame resistance Good Good Good Bad Tensile strength (Mpa) 28.8 46.8 26.3 22.3 Elongation rate (%) 650 80 105 76 Wear resistance (frequency) 4437 1658 10000 93 Flexibility Bad Bad Bad Bad Formability Bad Good Bad Bad According to the results obtained for Comparative Example 1, when a hard resin is added to the composition in a large quantity, instead of adding maleic acid-anhydride-treated polyolefin portion (b), the composition loses flexibility. Electrical cables coated with such a composition become thus less formable. The results obtained for Comparative Example 2 show that when an organic acid-anhydride-treated polypropylene is added in a great quantity, magnesium hydroxide becomes bound to the resin too firmly, so that the tensile elongation and flexibility of the composition are degraded. The results obtained for Comparative Example 3 indicate that unless a thermoplastic resin is added, the resin compositions become too hard. The formability of coated electrical cables is thus degraded. According to the results obtained for Comparative Example 4, when magnesium hydroxide is added in a large amount, the composition has a low elongation rate, and becomes less resistant to wear, less flexible and less formable.

Claims: An olefin-based resin composition comprising: (i) a polymeric material in an amount of 100 parts by weight which includes: (a) a propylene-type polymer portion; (b) a polyolefin portion treated with maleic acid anhydride; and (c) an olefin-type polymer portion; and (ii) a metal hydroxide product; characterised in that said propylene-type polymer portion (a) comprises at least one propylene polymer accounting for a proportion of about 50 to about 80% by weight of said polymeric material (i); said polyolefin portion treated with maleic acid anhydride (b) comprises at least one polyolefin, a proportion of about 0.1 to about 10% by weight of which are structurally modified through maleic acid anhydride treatment, said polyolefin portion accounting for about 1 to about 20% by weight of said polymeric material (i); said olefin-type polymer portion (c) comprises at least one polymer made of polypropylene and propylene-ethylene copolymer, being a thermoplastic resin having a melting point of at least about 130°C and a Shore A hardness of about 90 at the most, said olefin-type polymer portion accounting for about 10 to about 40% by weight of said polymeric material (i); and said metal hydroxide product (ii) comprises at least one metal hydroxide in a an amount of about 30 to about 200 parts by weight relative to said polymeric material (i). said portions (a), (b) and (c) being different from one another. The olefin-based resin composition according to claim 1, wherein said polyolefin portion treated with maleic acid anhydride (b) accounts for about 2 to about 10% by weight of said polymeric material (i), said olefin-type polymer portion (c) accounts for about 20 to about 30% by weight of said polymeric material (i), and said metal hydroxide product (ii) comprises at least one metal hydroxide in a an amount of about 50 to about 150 parts by weight relative to said polymeric material (i). The olefin-based resin composition according to claim 1 or 2, wherein said metal hydroxide product (ii) comprises at least one metal hydroxide in a an amount of about 70 to about 90 parts by weight relative to said polymeric material (i). The olefin-based resin composition according to any one of claims 1 to 3, wherein said propylene-type polymer portion (a) has a melt flow rate of about 0.1 to about 5g/10 minutes. The olefin-based resin composition according to any one of claims 1 to 4, wherein said propylene-type polymer portion (a) comprises at least one polymer selected from the group consisting of a propylene-ethylene block copolymer, a propylene-ethylene random copolymer and a propylene homopolymer. The olefin-based resin composition according to any one of claims 1 to 5, wherein said polyolefin portion treated with maleic acid anhydride (b) at least comprises polypropylene structurally modified through maleic acid anhydride treatment. The olefin-based resin composition according to any one of claims 1 to 6, wherein said metal hydroxide product (ii) is treated with a silane-type coupling agent. The olefin-based resin composition according to claim 7, wherein said silane-type coupling agent comprises an aminosilane-type coupling agent. An olefin-based resin composition defined by any one of claims 1 to 8, which is substantially free of halogen. An electrical cable coated with the olefin-based resin composition defined by any one of claims 1 to 9.

Inventors: FUJIMOTO HIROSHI, HASE TATSUYA, SATO MASASHI, FUJIMOTO, HIROSHI, HASE, TATSUYA, SATO, MASASHI, Fujimoto, Hiroshi, Sumitomo Wiring Systems, Ltd., Hase, Tatsuya, Sumitomo Wiring Systems, Ltd., Sato, Masashi, Sumitomo Wiring Systems, Ltd.
Applicants: SUMITOMO ELECTRIC INDUSTRIES, SUMITOMO WIRING SYSTEMS, SUMITOMO ELECTRIC INDUSTRIES, LTD., SUMITOMO WIRING SYSTEMS, LTD.
Application year: 2001
Main classification: C08L23
IPC codes: C08L53, H01B7, H01B3, C08L23, C08K9, C08L51