TREATMENT OF MINERAL SUBSTRATES

Abstract: A method for rendering substrates water repellent by applying to the substrate a composition comprising a mixture formed by combining (i) water or a solvent; (ii) a methylhydrogen-siloxane polymer or copolymer; (iii) an alkoxysilane having the formula R>a<Si(OR?1>)4-a in which R represents an alkyl-group containing 1-10 carbon atoms, an alkenyl group containing 2-8 carbon atoms, an aryl group, or an haloalkyl group, a has a value of 1 or 2, and R<1> represents an alkyl group containing 1-6 carbon atoms; and (iv) a silicone resin. The compositions can be applied either by direct application to the substrate or by incorporation into the substrate during its manufacture.

Description: TREATMENT OF MINERAL SUBSTRATES This invention is directed to a method of treating mineral substrates with organosilicon compositions in order to achieve water repellency. Mineral substrates include building materials such as brick, cured concrete, sewer pipe, hollow block, cured mortar, stucco, decorative stone, roofing tile, and structures which incorporate such building materials, such as highway surfaces, bridges, concrete, stone or brick building exteriors, footings, and retaining walls. The invention provides a method of rendering water repellent a mineral substrate, by applying to the mineral substrate a composition comprising a mixture formed by combining (i) water or a solvent; (ii) a methyl hydrogensiloxane polymer or copolymer; (iii) an alkoxysilane having the formula RaSiζOR 1 )^ in which R represents an alkyl-group containing 1-10 carbon atoms, an alkenyl group containing 2-8 carbon atoms, an aryl group, or an haloalkyl group, a has a value of 1 or 2, and R 1 represents an alkyl group containing 1- 6 carbon atoms; and (iv) a silicone resin. The compositions for use in the method according to this invention differ from those known in the prior art in that they contain a unique combination of components, i.e., the polymethylhydrogensiloxane, alkoxysilane, and silicone resin. They may also include either a volatile methyl siloxane or a cationic oil-in-water emulsion of an aminofunctional polydimethylsiloxane. The compositions are low VOC penetrating water-repellent compositions In terms of their function in such compositions, the polymethyhydrogensiloxane excludes water, the alkoxysilane reduces darkening, and the silicone resin increases the ability of a treated substrate to exclude water under conditions involving the application of hydrostatic pressure, i.e., wind-driven rain or high pressure application of water. Suitable polymethylhydrogensiloxanes for use in this invention include compositions having the formula where Rl to R8 represent hydrogen or an alkyl group containing 1-6 carbon atoms, with the proviso that at least one of the groups Rl to R8 is hydrogen, and x is an integer of from 1 to 200. Most preferred are compositions in which about one-half of the groups Rl to R8 in the polymethylhydrogensiloxane are hydrogen, the remainder of the groups being methyl groups. An especially preferred example of a polymethylhydrogensiloxane is a trimethylsiloxy terminated polymethylhydrogensiloxane with a silicon-bonded hydrogen content of 1.4 to 1.75 weight percent, and having a viscosity between 20 to 40 centistoke (mm 2 /sec). Polymethylhydrogensiloxane copolymers can also be used, and suitable copolymers include (alkylmethyl) (methylhydrogen) siloxane copolymers having the formula where the groups R9 - R15 and R18 each represent an alkyl group containing 1-6 carbon atoms, typically a methyl group, R16 represents hydrogen, and R17 represents an higher alkyl group containing more than six carbon atoms. The values of y and z are from 1 to 200. Such polymethylhydrogensiloxane polymers and copolymers are commercially available, for example, from the Dow Corning Corporation, Midland, Michigan, and suitable materials are described, for example, in US Patents 5074912 and 5919296. The alkoxysilane can be a single alkoxysilane or a mixture of alkoxysilanes. The alkoxysilane has the formula In the formula, R represents an alkyl group having 1-10 carbon atoms, preferably 1-8 carbon atoms, an alkenyl group having 2-8 carbon atoms, an aryl group such as phenyl, or an haloalkyl group such as chloropropyl and trifluoropropyl. The value of a is 1 or 2, and R 1 represents an alkyl group having 1-6 carbon atoms. Preferably, R is methyl, isobutyl, or n-octyl, and R 1 is methyl or ethyl. Some suitable alkoxysilanes are methyltrimethoxysilane, methyltriethoxysilane, methyltripropoxysilane, ethyltrimethoxysilane, ethyltributoxysilane, propyltrimethoxysilane, propyltriethoxysilane, ispbutyltrimethoxysilane, isobutyltriethoxysilane, butyltriethoxysilane, hexyltrimethoxy- silane, n-octyltriethoxysilane, dimethyldimethoxysilane, dimethyldiethoxysilane, diethyl- dimethoxysilane, diisobutyldimethoxysilane, phenyltrimethoxysilane, dibutyldiethoxysilane, and dihexyldimethoxysilane. Such alkoxysilanes are commercially available, for example, from the Dow Corning Corporation, and are described, for example, in US Patents 5300327, 5695551, and 5919296. The silicone resin can be any one of the various types of resinous copolymers described in detail in US patent 5695551. However, most preferred for use herein are those resinous copolymers described as: I. A resinous copolymeric siloxane prepared by a method comprising (i) forming an acidic homogenous mixture of a silanol containing resinous copolymeric siloxane with R n 3 SiO 1 /2 units and SiO 4 /2 units; an organohydrogen polysiloxane with the formula R ll bHcSiO( .b- 0 )/2 where b and c are positive integers, with a sum less than four, preferably 1.9-2.1; and an organic solvent, and (ϋ) heating the mixture to remove substantially all organic solvent. R n is selected from; an alkyl group with 1-6 carbon atoms; an aryl group such as phenyl, tolyl, and xylyl; an alkenyl group such as vinyl and allyl; a trifluoropropyl group; an arylalkyl group such as betaphenylethyl and betaphenylpropyl; or a cycloaliphatic group such as cyclopentyl, cyclohexyL and cyclohexenyl. II. A siloxane resin copolymer comprising R n 3 SiOι/2 units and SiO 4 / 2 units in a mole ratio such that the number average molecular weight is 1,200 to 10,000 daltoa Preferably, the mole ratio is 0.7:1.0, and the number average molecular weight is 5,000. R 11 is as defined in I. This resin contains 2.5 weight percent silicon-bonded OH groups. The resin may also contain R 1 ^SiQ∞ units and R 11 SiO 3/2 units. One such copolymer which is especially preferred for use herein is a 70 weight percent xylene solution of a siloxane resin copolymer consisting essentially of (CH 3 ) 3 SiOι/ 2 units and SiO 2 units in a molar ratio of approximately 0.75:1 containing 2.4 to 2.9 weight percent of hydroxy, based on solids as determined by FTIR according to the American Society for Testing & Materials (ASTM Test Procedure E-168. The volatile methyl siloxane can be a linear volatile methyl siloxane (VMS), a cyclic volatile methyl siloxane, or a mixture of VMS. Volatile methyl siloxanes generally correspond to the average unit formula (CH 3 )dSiO( -d) 2 in which d has an average value of two to three. Representative siloxane units which may be present in such compositions are monofunctional "M" units (CH 3 ) 3 SiO 1 2 and difunctional "D" units (CH 3 ) 2 SiO 2 / 2 . The presence of other siloxane units such as trifunctional "T" units CH 3 Siθ3/ 2 and tettafunctional "Q" units SiO 2 results in the formation of branched compositions. Linear VMS have the formula (CH 3 ) 3 SiO{(CH 3 ) 2 SiO} e Si(CH 3 ) 3 in which e is 0-5. and cyclic VMS have the formula {(CH 3 ) SiO} f in which f is 3-9. Preferably, these volatile methyl siloxanes have a boiling point less than about 250°C and a viscosity of 0.65 to 5.0 centistoke (mm 2 /s). (All viscosities are measured at 25°C using Ubbelohde glass viscometers). Examples of linear volatile methyl siloxanes are hexamethyldisiloxane (MM) with a boiling point of 100°C, viscosity of 0.65 mm 2 /s, and formula Me 3 SiOSiMe 3 ; octamethyltrisiloxane (MDM) with a boiling point of 152°C, viscosity of 1.04 mm 2 /s, and formula Me 3 SiOMe 2 SiOSiMe 3 ; decamethyltetrasiloxane (MD 2 M) with a boiling point of 194°C, viscosity of 1.53 mm 2 /s, and formula Me 3 SiO(Me 2 SiO) 2 2SiMe 3 ; dodecamethylpentasiloxane (MD 3 M) with a boiling point of 229°C, viscosity of 2.06 mm 2 /s, and formula Me 3 SiO(Me 2 SiO) 3 SiMe 3 ; tetradecamethylhexasiloxane (MD M) with a boiling-point of 245°C, viscosity of 2.63 mm 2 /s, and formula Me 3 SiO(Me 2 SiO) 4 4SiMe 3 ; and hexadecamethylheptasiloxane (MD 5 M) with a boiling point of 270°C, viscosity of 3.24 mm 2 /s, and formula Me 3 SiO(Me 2 SiO) 5 SiMe 3 . Examples of cyclic volatile methyl siloxanes are hexamethylcyclotrisiloxane (D 3 ), a solid at room temperature, with a boiling point of 134°C and formula {(Me 2 )SiO} 3 ; octamethylcyclotetrasiloxane (D 4 ) with a boiling point of 176°C, viscosity of 2.3 mm 2 /s, and formula {(Me 2 )SiO} ; decamethylcyclopentasiloxane (D5) with a boiling point of 210°C, viscosity of 3.87 mm 2 /s, and formula {(Me 2 )SiO}5; and dodecamethylcyclohexasiloxane (D 6 ) with a boiling point of 245°C, viscosity of 6.62 mm 2 /s, and formula {(Me 2 )SiO} 6 . Examples of branched volatile methyl siloxanes are heptamethyl-3-{(trimethylsilyι)oxy}- trisiloxane (M 3 T) with a boiling point of 192°C, viscosity of 1.57 mm 2 /s, and formula C^HsoOsSύ; hexamethyl-3, 3, bis {(trimethylsilyl)oxy} trisiloxane (M4Q with a boiling point of 222°C, viscosity of 2.86 mm 2 /s, and formula C 12 H 36 O Sis; and pentamethyl {(trimethylsilyl)oxy} cyclotrisiloxane (MD 3 ) with the formula Such volatile methyl siloxanes are commercially available, for example from the Dow Corning Corporation, Midland, Michigan. The cationic oil-in-water emulsion of an animofunctional polydimethylsiloxane is a silicone- containing cationic emulsion of an amine-substituted siloxane polymer having reactive silanol (-SiOH) functionality. The siloxane polymer is generally stabilized in the form of an aqueous emulsion by means of a cationic and a nonionic surfactant. Typically, when these types of emulsions are broken, the siloxane polymer is no longer stabilized, and it is capable of crosslinking and curing by condensation of the silanol groups. The cationic surfactant most typically used in preparing such emulsions is Tallowtrimonium Chloride, a Cosmetic, Toiletry, and Fragrance Association (CTFA) ESFCI name for quaternary ammonium salts of trimethyltallow ammonium chloride pi in N(CH 3 ) 3 ] + Cr in which R 111 is generally an alkyl group derived from tallow. The nonionic surfactant most typically used in preparing such emulsions is Nonoxynol-10, another CTFA INCI name for ethoxylated alkyl phenols C 9 H 1 9C 6 H (OCH 2 CH 2 )gOH in which g is generally about ten. However, other surfactants can also be used in preparing emulsions of this type. Such emulsions are commercially available, for example from the Dow Corning Corporation, and are described, for example, in US Patent 4559227 and US Patent 5326483. Any solvent useful in masonry applications can be used. Typical examples include such compositions as mineral spirits, alcohols such as isopropyl alcohoL and various of the hydrocarbon solvents such as toluene and xylene. One example of a solvent especially preferred for use herein is the composition K IK-DRY® 66, an aliphatic hydrocarbon Stoddard type solvent, commonly known as mineral spirits (Ashland Chemical Co). The solvent can also consist of one or more of the various volatile methyl siloxanes noted above, especially the cyclic species octamethylcyclotetrasiloxane (D 4 ). In addition, glycol ethers such as diethylene glycol butyl ether and propylene glycol methyl ether which are sold under the trademark Dowanol® by The Dow Chemical Co., and polyglycols such as ethylene glycol and propylene glycol, can be employed as the solvent. As surfactant, most preferred is a combination of a low HLB nonionic surfactant and a high HLB nonionic surfactant. In particular, the low HLB nonionic surfactant should have an HLB value of less than 10.5, preferably less than 6.0. The high HLB nonionic surfactant should have an HLB value of greater than 15.0, and preferably greater than 17.0. Examples of surfactants in each category are enumerated in detail in US Patent 5695551, to which reference may be made for specific examples of appropriate surfactant combinations which can be employed. Examples of low HLB ionic surfactants are: (a) Brij 52, a polyoxyethylene cetyl ether (TCI Americas Inc.), HLB value 4.9; (b) Brij 72, a polyoxyethylene stearyl ether (ICI Americas Inc.), HLB value 4.9; (c) Arlacel 60, sorbitan stearate (ICI Americas Inc.), HLB value 4.7; (d) Aldo® MS, glycerol monostearate (Lonza Inc.), HLB value 3.9; (e) Aldo® PGHMS, propylene glycol monostearate (Lonza Inc.), HLB value 3.0; (f) Mapeg® EGMS, ethylene glycol monostearate (PPGTMazer), HLB value 2.9; (g) Hodag DGS, diethylene glycol monostearate (Hodag Chemical Corp.), HLB value 4.7; (h) Ethox SAM-2, a polyoxy- ethvlene Stearvl 17.4; (iv) Triton® X-405, octylphenoxy polyethoxy ethanol (Union Carbide), HLB value 17.9; (v) Macol® SA-20, steareth-20 (PPG/Mazer), HLB value 15.4; and (vi) Tergitol® 15- S-20, a Cl 1-C15 secondary alcohol ethoxylate (Union Carbide), HLB value 16.3. Other possibilities include nonionic surfactants such as Fluorad fluorocarbon-based surfactants (3M); Pluronic® block copolymers of ethylene oxide and propylene oxide sold under the trademark (BASF); Span fatty acid esters and Tween ethoxylated fatty acid esters (ICI Surfactants). Certain anionic polymeric emulsifiers can be used in combination with these nonionic surfactants, such as Pemulen® crosslinked hydrophobically-modified polyacrylic acid polymers and Carbopol® crosslinked hydrophobically-modified polyacrylic acid copolymers (both BF Goodrich). In addition, synthetic water-soluble resins such as polyvinyl alcohols (C 2 H4θ) x can be employed. If desired, an anionic surfactant may be formed in situ by including in the mixture a base such as sodium hydroxide, triethanolamine, or morpholine; and a fatty acid such as stearic acid, oleic acid, or a tall oil fatty acid. In addition, the following surfactants have been found to be especially useful; SPAN 20, sorbitan monolaurate, HLB value 8.6; ARALTONE T, polyoxyethylene 40 sorbitol septaoleate, i.e., PEG-40 Sorbitol Septaoleate, HLB value 9.0; and G-4280, polyoxyethylene 80 sorbitan laurate, i.e., PEG-80 Sorbitan Laurate, HLB value 19.1 (all ICI Surfactants). If desired, a catalyst can be included as a component in compositions according to this invention, and representative catalysts are metal containing compositions such as dibutyltin dilaurate, dibutyltin dioctoate, and dibutyltin diacetate; titanate catalysts such as tetrabutyltitanate and, tetraisopropyltitanate; acid catalysts such as acetic acid; and basic type catalysts, i.e., amines such as triethanolamine, morpholine, and diethylamine. Such catalysts are capable of converting the alkoxysilane to a resinous product by hydrolysis and condensation. There is a range of other optional additives which may be used. A first optional additive is a beading agent. Examples of some suitable beading agents are stearates such as aluminum stearate and magnesium stearate; borate salts such as sodium borate; and hydrophobic silica. These materials assist in shedding films of water from a surface oy forming droplets. A second optional additive is an organic wax. The organic wax is preferably carnauba wax or a blend of petroleum and synthetic waxes. More particularly, the organic wax is a blend which includes both paraffin and polyethylene waxes. The polyethylene waxes can be high or low density polyethylene waxes, or mixtures of high and low density polyethylene waxes. An example of an especially suitable organic wax is JONWAX® 125 (SC Johnson), which is sold as an aqueous emulsion of polyethylene and paraffin waxes with a solids content of about 35%. Other blended paraffin and polyethylene type waxes can also be employed. A third optional additive is a preservative to reduce and or eliminate microbial activity in the water based emulsion. Examples of suitable preservatives are the compound 5-chloro-2- methyl-4-isothiazolin-3-one sold under the tradename KATHON LX (Rohm and Haas), and the compound l-(3-chloroallyl)-3,5,7-triaza-l-azoniaadamantane chloride sold under the trademark Dowicil® 75 (Dow Chemical Co.). A fourth optional additive is an antifoam. Examples of some suitable antifoams are silicone antifoams, such as silica- filled polydimethylsiloxane sold by the Dow Corning Corp.; and organic antifoams such as hydrocarbon oils sold under the trademark Advantage® by Hercules Inc. A fifth optional additive, useful especially where the composition is intended as an exterior coating, is a mildewcide, including materials classified as algicides, antimicrobials, bactericides, disinfectants, or fungicides; and which are organic or inorganic materials which reduce biological activity on a substrate. Examples of suitable mildewcides include proprietary fungicide compositions sold under the trademarks Troysan® and Polyphase® P- 20T (Troy Chemical Company); diiodomethyl-p-tolylsulfone sold under the trademark Amical® (Angus Chemical Co.); tribasic copper sulfate; and stabilized chlorine dioxide. A sixth optional additive, useful again especially when the composition is intended as an exterior coating, is a UV absorber/UV light stabilizer. Examples of suitable UV absorber/UV light stabilizers are substituted benzotriazole and hindered amines sold under the trademark Tinuvin® by Ciba-Geigy Corporation. A seventh optional additive, useful for protecting compositions during storage or in low temperature applications, is a freeze-thaw ingredient such as ethylene glycol. The quantities of the various components used to prepare water-based or solvent-based compositions for use in the method of the invention are not critical, but they generally fell within the following ranges: 0.1-99 percent by weight, preferably 30-90 percent by weight of the polymethylhydrogensiloxane; 0.1-99 percent by weight, preferably 0.1-50 percent by weight of the alkoxysilane; 0.1-99 percent by weight, preferably 0.1-50 percent by weight of the silicone resin; 0-70 percent by weight, preferably 0.1-50 percent by weight of the volatile methyl siloxane or other solvent; 0-10, percent, by, weight, preferably 0.25-5 percent by weight of the cationic oil-in- water emulsion of the aminofunctional polydimethylsiloxane; 0.1-10 percent by weight, preferably 1-5 percent-by weight of the surfactant; 0-2 percent by weight, preferably 0.1-2 percent by weight of the catalyst; 0-20 percent by weight, preferably 0.1-20 percent by weight of the beading agent; 0-20 percent by weight, preferably 0.1-20 percent by weight of the organic wax; and 0.01-5 percent by weight, preferably 0.1-2 percent by weight of each of the optional additives, i.e., preservative, antifoam, mildewcide, UV absorber/UV light stabilizer, and freeze-thaw additive. For water-based compositions, the balance of the solution or emulsion to 100 percent consists of water, while for the solvent-based compositions, the balance of the solution to 100 percent consists of the solvent or volatile methyl siloxane. Generally, the amount of solids in the compositions should be 0.1-90 percent by weight, preferably 5-50 percent by weight. Water-repellent compositions for treating surfaces according to the method of this invention can be made by simply mixing together the various ingredients. Where a composition is desired in the form of an emulsion, it can be made by (i) making one emulsion of the several ingredients; (ii) making several emulsions each containing one or more of the ingredients, and combining the several emulsions; and (iii) following the procedure for (i) or (ii) and then adding some of the ingredients directly to water. These mixtures, solutions, and emulsions can be made using any suitable source of shear, such as a high speed stirrer, a homogenizer, sonolator, micro-fluidizer, Turello change can mixer, Ross mixer, or Eppenbach colloid mill. Where appropriate, hand mixing can also be employed. The procedure for making the mixtures, solutions, and emulsions can include the direct addition of oil to water/solvent, or the indirect addition of water/solvent to oil. Preferably, the particle size of the active ingredient(s) in the discontinuous or internal phase of an emulsion should be between about 0.1 micrometer (μm)/100 nanometer to about 5 micrometer (μm)/5,000 nanometer. These water-repellent compositions can be formulated as a concentrated solution or emulsion having a high solids content for later dilution and direct application to a substrate; or they can be formulated as ready-to-use solutions or emulsions with low solids content for direct application to the substrate. The actual amount of water-repellent composition employed will vary, depending upon the nature of the substrate being treated, but in general, it should be sufficient to provide the substrate with a coating containing about 3-40 percent by weight of the solids in the water-repellent composition being applied. The method of application of the water-repellent composition is preferably by topical treatment or topical coating of the substrate, but an alternative method is incorporation of the composition directly into a substrate during its manufacture, for example, as an admixture in a concrete mix prior to its setting. When applied topically, for best results, it is preferred that 5 the substrate be treated when it is dry, but substrates can be treated when they are damp or wet. Test Methods and Procedures 10 21 Day Water Exclusion Test A modified version of the National Cooperative Highway Research Program (NCHRP) Test Procedure as outlined in their Report No. 244 entitled "21 Day Water Exclusion Testing" was used to determine water repellency characteristics. A lightweight concrete block was 15 obtained and cut into 2" X 2" X 3.5" (5.08 X 5.08 X 8.89 cm) cubes. These cubes were then conditioned at 110 °C for 48 hrs. Once the blocks were conditioned, three cubes were used to evaluate the water repellent coatings, and compared to three cubes which were untreated. The cubes were coated with the water-repellent composition and allowed to cure for 7 days at room temperature before the cubes were placed into a water bath, such that 2.54cm. of 20 water was above the cubes. Water exclusion was calculated by comparing the weight of untreated cubes to that of treated cubes at different times up to 21 days. Water exclusion is calculated by taking the average weight difference of 3 untreated cubes and subtracting the average-weight difference of 3 treated cubes and dividing by the average weight difference of 3 untreated cubes, multiplied by 100; as expressed in the formula below: 25 Percent WE = [(C2 - Cl) - (S4 - S3)] x 100/(C2 - Cl) where S3 is the weight of a treated specimen before water immersion, S4 is the weight of a treated specimen after water immersion, Cl is the weight of an untreated control before water 30 immersion, and C2 is the weight of a treated control after water immersion. In terms of this test procedure, the higher the percent water exclusion the better is the performance. Modified American Society for Testing & Materials (ASTM) Test Procedure E-514 According to this procedure, three block specimens are oven dried at 110 'C for a minimum of 24 hours prior to testing. The weight of each specimen is determined and recorded as the initial untreated weight. Each specimen is connected to the test apparatus using I-beams provided as part of the testing apparatus. Water and air supplies are activated to provide a water flow of 60-70 gallons (227.1 - 265 L) per hour at a pressure of 5.08 cm. of water. The tare weight of the water collection bucket is obtained. Leakage or wet spots which form on the blocks are recorded. The untreated blocks are allowed to remain in the test apparatus until 8.7 L. of water has been removed from the test chamber. The amount of time for removing 8.7 L. of water is recorded. The test blocks are removed and their weight is recorded. The weight of the water collection bucket is also recorded. The leak rate of the 3 blocks is calculated by determining the amount of water in the collection bucket and dividing it by the amount of time it took for the water to pass through the test chamber. After completing the leak rate for untreated blocks, the blocks are re-dried at 110 °C for 24 hrs. A water-repellent composition is applied to each specimen and allowed to cure 7 days at room temperature. Once the water-repellent composition has been cured, the leak rate of the treated block is determined by the same procedure used for the untreated block. The percent reduction in leak rate is determined by taking the difference between the untreated block leak rate and the treated leak rate, and dividing it by the untreated leak rate, and multiplying by 100; according to the formula below: (Al - B1)/A1 X 100 = Percent Reduction where Al is the untreated block leak rate and Bl is the treated block leak rate. In terms of this test procedure, the higher the percent reduction the better is the performance. Darkening One half of a 2" X 2" X 3.50" (5.08 X 5.08 X 8.89 cm) lightweight concrete block is soaked in the water repellent composition. The block is allowed to cure for periods of 1, 4, and 7 days. Each day an observation is made to determine the difference between the treated half and the untreated half. The darkening is then evaluated on a scale of 1 to 5, in which 1 indicates no darkening, 2 indicates very slight darkening, 3 indicates noticeable darking, 4 indicates dark, and 5 indicates extremely dark. Particle Size A MICROTRAC UPA 150 Particle Size Analyzer was used to measure emulsion particle size after the emulsion had been prepared. Two drops of the emulsion were placed into 10 grams of deionized water. The mixture was placed in the analyzer cell and the sample was analyzed to determine the particle size. Emulsification Procedure A mixture of the organosilicon components is formed and weighed into a small beaker, a low HLB surfactant is added to the small beaker, and the contents of the small beaker are mixed for 15 minutes at 300 rpm. The aqueous continuous phase, i.e., water, is weighed and placed into a larger beaker, a high HLB surfactant is added to the larger beaker, and the contents of the larger beaker are mixed for 15 minutes at 300 rpm. The speed of the mixer in the larger beaker is increased to 500-700 rpm, and the contents of the small beaker is slowly poured to the larger beaker. Mixing of the combined contents of the two beakers is then continued for 30 minutes. The crude emulsion is poured into a plastic bottle, and the emulsion is sonolated at 12.41 MPa for about 3 minutes, in order to complete emulsification. EXAMPLES The following examples are set forth in order to illustrate this invention in more detail. Example 1 - A Solvent-Based Composition A mixture was prepared containing a polymethylhydrogensiloxane, a silicone resin, and the alkoxysilane n-octyltriethoxysilane, in a weight ratio of about 8:1:1, respectively. The mixture was diluted to about 20 % solids in KWIK-DRY® 66 aliphatic ' hydrocarbon Stoddard type solvent, and the composition, was applied to a lightweight concrete block. A coverage rate of about 1.35 m 2 /L. was used for this 20 % solids mixture according to ASTM Test Procedure E-514; and a 30 second immersion of test cubes was used in determining the characteristics of this composition under the protocol of the NCHRP 21 Day Water Exclusion Test. The performance of the composition under these conditions is shown in Table 1. The polymethylhydrogensiloxane used in this example and in the following examples was a trimethylsiloxy terminated polymethylhydrogensiloxane with a silicon-bonded hydrogen content of about 1.4 to 1.75 weight percent having a viscosity between about 20 to 40 centistoke (mmVsec). The silicone resin used in this example and in the following examples was a siloxane resin copolymer having R u 3 SiOi/ 2 units and SiO 2 units in a mole ratio of about 0.7:1.0. The number average molecular weight was about 5,000. R 11 was a methyl group. The silicone resin contained about 2.5 weight percent silicon bonded OH groups. Example 2 - An Emulsion Form of Composition An emulsion was prepared with a polymethylhydrogensiloxane, a silicone resin, and alkoxysilane n-octyltriethoxysilane, using the emulsification procedure previously described. The three organosilicon components were combined in a weight ratio of 8:1:1, respectively. The emulsion was prepared using 40 parts by weight of the three organosilicon components, 13.3 parts by weight of a volatile methyl siloxane which was octamethylcyclotetrasiloxane, 0.6, parts by weight of SPAN 20 nonionic surfactant with an HLB of 8.6, 1.0 parts by weight of ARALTONE T nonionic surfactant with an HLB of 9.0, 1.4 parts by weight of G-4280 nonionic surfactant with an HLB of 19.1, i.e., PEG-80 Sorbitan Laurate, 0.8 parts by weight of the freeze-thaw additive ethylene glycol, and 42.9 parts by weight of water. The emulsion was diluted to a 1:1 ratio with more water, and then applied to test substrates. The performance of this emulsion composition is shown in Table 1. Example 3 - Another Emulsion Form of Composition A second emulsion was prepared according to the procedure used in Example 2, except that there was added to the diluted emulsion in Example 2, about 2.2 parts by weight of a cationic 5 oil-in-water emulsion of an aminofunctional polydimethylsiloxane having reactive silanol functionality, stabilized by a cationic and a nonionic surfactant. The performance of this emulsion composition is shown in Table 1. Example 4 - Comparative 10 A solution containing about 20 percent by weight of n-octyltriethoxysilane was prepared using a titanate catalyst in isopropyl alcohol. The composition was applied to a lightweight concrete block. A coverage rate of about 1.35 m 2 /L. was used for this composition according to ASTM Test Procedure E-514; and a 30 second immersion of test cubes was used in 15 determining the characteristics of this composition under the protocol of the NCHRP 21 Day Water Exclusion Test. The performance of the composition under these conditions is shown in Table 1. Example 5 - Comparative 20 Example 4 was repeated except that no titanate catalyst was employed. The performance of the composition is shown in Table 1. Example 6 - Comparative 25 A solution was prepared containing about 20 weight percent of the silicone resin used in Example 1 in KWIK-DRY® 66 aliphatic hydrocarbon Stoddard-type solvent. The composition was applied to a lightweight concrete block. A coverage rate of about 1.35 m 2 /L. was used for this composition according to ASTM Test Procedure E-514; and a 30 30 second immersion of test cubes was used in deteπnining the characteristics of this composition under the protocol of the NCHRP 21 Day Water Exclusion Test. The performance of the composition under these conditions is shown in Table 1. Example 7 - Comparative A solution was prepared containing about 20 weight percent of the polymethylhydrogensiloxane used in Example 1 in KWIK-DRY® 66 aliphatic hydrocarbon Stoddard type solvent. The composition was applied to a Hghtweight concrete block. A coverage rate of about 1.35 m 2 /L. was used for this composition according to ASTM Test Procedure E-514; and a 30 second immersion of test cubes was used in determining the characteristics of this composition under the protocol of the NCHRP 21 Day Water Exclusion Test. The performance of the composition under these conditions is shown in Table 1. Table 1 Table 1 shows that the compositions prepared according to the present invention, i.e., Examples 1-3, provide improved performance overall in practically all categories evaluated, in contrast to compositions in the Comparative Examples 4-7. The shght difference in darkening between ratings of 2 for very slight darkening and ratings of 3 for noticeable darkening is not considered significant. Other variations, may be made in compounds, compositions, and methods described herein without departing from the essential features of the invention. The embodiments of the invention specifically illustrated herein are exemplary only and not intended as limitations on their scope except as defined in the appended claims.

Claims: CLAIMS 1. A method of rendering water repellent the surface of a mineral substrate,, by applying to the mineral substrate a composition comprising a mixture formed by combining (i) water or a solvent; (ii) a methyl hydrogensiloxane polymer or copolymer; (hi) an alkoxysilane having the formula R a Si(OR 1 ) 4-a in which R represents an alkyl-group containing 1-10 carbon atoms, an alkenyl group containing 2-8 carbon atoms, an aryl group, or an haloalkyl group, a has a value of 1 or 2, and R 1 represents an alkyl group containing 1-6 carbon atoms; and (iv) a silicone resin. 2. A method according to claim 1, wherein the composition is applied directly to the substrate. 3. A method according to claim 1, wherein the composition is added to the substrate during the course of its manufacture. 4. A method according to Claim 1 in which the alkoxysilane is selected from the group consisting of methyltrimethoxysilane, methyltriethoxysilane, methyltripropoxysilane, ethyltrimethoxysilane, ethyltributoxysilane, propyltrimethoxysilane, propyltriethoxysilane, isobutyltrimethoxysilane, isobutyltriethoxysilane, butyltriethoxysilane, hexyltrimethoxy- silane, n-octyltriethoxysilane, dimethyldimethoxysilane, dimethyldiethoxysilane, diethyl- dimethoxysilane, dϋsobutyldimethoxysilane, phenyltrimethoxysilane, dibutyldiethoxysilane, and dihexyldimethoxysilane. 5. A method according to Claim 1 in which the silicone resin is a resinous copolymer selected from the group consisting of (I) resinous copolymeric siloxanes prepared by (i) forming an acidic homogenous mixture of a silanol containing resinous copolymeric siloxane with R 11 3 SiO 1 /2 units and SiO / 2 units; an organohydrogen polysiloxane with the formula R U bH c SiO(4-b-c)/2 where b and c are positive integers with a sum less than four; and an organic solvent, and (ii) heating the mixture to remove substantially all organic solvent; in which R 11 is an alkyl group with 1-6 carbon atoms, an aryl group, an alkenyl group, a trifluoropropyl group, an arylalkyl group, or a cycloaliphatic group; and (II) siloxane resin copolymers containing R 11 3 SiO 1 / 2 units and SiO / 2 units in a mole ratio such that the number average molecular weight is 1,200 to 10,000 dalton, in which R 11 is the same as defined in (I), and the resin contains at least 2.5 weight percent of silicon-bonded OH groups. 6. A method according to Claim 1 in which the methylhydrogensiloxane is a polymer having the formula where Rl to R8 represent hydrogen or an alkyl group containing 1-6 carbon atoms, with the proviso that at least one of the groups Rl to R8 is hydrogen, and x has a value of 1-200; or a copolymer having the formula where each of the groups R9 to R15 and R18 each represent an alkyl group containing 1-6 carbon atoms, R16 is hydrogen, R17 is a higher alkyl group containing more than six carbon atoms, and y and z each have a value of 1-200. 7. A method according to Claim 1 further comprising at least one additional component selected from the group consisting of a volatile methyl siloxane, a cationic oil-in-water emulsion of an aminofunctional polydimethylsiloxane, a surfactant, a catalyst, a beading agent, an organic wax, a preservative, an antifoam, a mildewcide, anUV absorber/UV light stabilizer, and a freeze-thaw additive. 8. A method according to Claim 7 in which the additional component is a volatile methyl siloxane or a cationic oil-in-water emulsion of an amino functional polydimethylsiloxane. 9. A method according to Claim 7 in which the additional component is at least two surfactants, one surfactant having an HLB less than 10.5, and the other surfactant having an HLB more than 15. 10. A method according to Claim 9 in which the composition is emulsified.

Inventors: FISHER PAUL DAVID, LIN FEIFEI, STARK-KASLEY LORI ANN, FISHER, PAUL, DAVID, LIN, FEIFEI, STARK-KASLEY, LORI, ANN
Applicants: MBT HOLDING AG
Application year: 2001
Main classification: C04B41
IPC codes: C04B24, C04B40, C04B41, C08G77, C09D183, C09K3