METHOD FOR FORMING HIGH QUALITY MULTIPLE THICKNESS OXIDE LAYERS BY USING HIGH TEMPERATURE DESCUM

Abstract: A method for forming high quality multiple thickness oxide layers having different thicknesses by eliminating descum induced defects. The method includes forming an oxide layer (2), masking the oxide layer with a photoresist layer (8), and developing the photoresist layer to expose at least one region (10) of the oxide layer. The substrate is then heated and descummed to remove any residue resulting from developing the photoresist. Alternatively, the photoresist layer (8) may be cured prior to heating and descumming the substrate. The oxide layer (2) is then etched, and the remaining photoresist (8) is stripped before another layer of oxide (14) is grown on the substrate.

Description: METHOD FOR FORMING HIGH QUALITY MULTIPLE THICKNESS OXIDE LAYERS BY USING HIGH TEMPERATURE DESCUM TECHNICAL FIELD The present invention pertains to the field of integrated circuit devices and manufacturing processes for the same. More particularly, this invention relates to the formation of a high quality multiple thickness oxide layers on a silicon wafer substrate BACKGROUND ART Non-volatile memory devices arc currently in widespread use in electronic components that require the retention of information when electrical power is terminated Non- volatile memory devices include read-only- memory (ROM), programmable-read-only memory (PROM), erasable-programmable-read-only memory (EPROM). and electπcally-erasablc-programmable-read-only-memory (EEPROM) devices EEPROM devices differ from other non-volatile memory devices in that they can be electrically programmed and erased Flash EEPROM devices are similar to EEPROM devices in that memory cells can be programmed and erased electrically. However, Flash EEPROM devices enable the erasing of all memory cells in the device using a single electrical current pulse. High voltage circuit elements such as program and erase transistors are usually formed on a wafer substrate with a relatively thick gate oxide layer. Such relatively thick gate oxide layers are usually required to prevent transistor circuit breakdown in such a high voltage environment. On the other hand, it is preferable that the low voltage circuitry is implemented with relatively thin gate oxide layers on the wafer substrate. Such thin gate oxide layers typically increase the speed of such circuit elements having relatively short gate lengths and thin oxide layers typically provide increased operation speeds In addition, as process technologies evolve toward shorter and shorter gate lengths it is desirable to reduce the thickness of the gate oxide layer even further in order to achieve greater operating speed However, some circuit elements contained on such integrated circuit devices may not be scalable Non-volatile memory devices, such as flash EEPROMs require the lormation of flash memory cells that include tunnel oxide layers on the waier substrate Such tunnel oxide layers may be thinner than high voltage oxide layers on the wafer substrate However, such tunnel oxide layers usually cannot be scaled down in thickness in the same manner as low voltage oxide layers. Such Hash memory cells, for example, typically suffer from significant endurance and data retention problems if the tunnel oxide layers are too thin Therelore, non-volatile memory devices can usually benefit from the formation of differing oxide thicknesses on the same wafer substrate Transistors with relatively thick select gate oxide layers can accommodate high voltage program and erase opciations while logic transistors with relatively thin gate oxide layers can yield speed advantages as process technologies evolve toward smaller circuit element dimensions In addition, the thickness of tunnel oxide layers for flash memory cells can be scaled for reliability independent of the gate dimensions and oxide thickness of the high and low voltage transistors One method of forming high quality multiple thickness oxide layers involves multiple masking and oxide formation steps For example, a first oxide layer, usually the thickest oxide layei . is initially grown on the wafer substrate Thereafter, a layer of photoresist is formed on the first oxide layer A pattern is formed on the photoresist layer by exposing the photoresist through a mask The photoresist is then developed and removed, leaving a portion of the oxide layer exposed Subsequently, the first oxide layer is etched and the remaining photoresist is stripped A second layer of oxide is then grown on the wafer substrate The second oxide layer forms a thin oxide layer on the wafer substrate while a thicker oxide layer is formed by the combination of the first and second oxide layers This process can be repeated to form additional oxide layers with various thicknesses throughout the process flow During and after development of the photoresist layer, the unmasked or exposed portion of the oxide layer may become contaminated For example, a thin film, undetectable on visual inspection, may form on the exposed portion of the oxide layer This film may consist of photoresist residue such as dried developer and undissolved pieces of photoresist Thus, it is usually necessary to subject the unmasked portion of the oxide layer to a cleaning or descumming process to remove the resist residue The unmasked or exposed portion of the oxide layer is often descummed or cleaned with 0 2 , 0 2 /N 2 or 0 2 /N -Hι chemistries in a barrel asher or a downstream single wafer asher Although the descum process is relatively short in order to avoid any surface damage of the exposed oxide layer, the descum process itself leaves contaminants on the oxide layer The contaminants appear as dark spots on the oxide layer under a high resolution scanning electron microscope (SEM) as shown in FIG 1 An analysis of the dark spots shows that they consist of sulfur compounds and small hydrocarbons, most likely photo active compound, left over from the development of the photoresist These dark spots or detects on the surface of the exposed oxide layer interact with subsequent processing steps, which creates processing problems and degrades reliability and yield For example, when a wet oxide etch is carried out after descum to remove the exposed portion of an oxide layer, the oxide layer under the dark spots cannot be completely removed Thus, the dark spots act as a micromask on the exposed portion of the oxide layer As a result of the dark spots, a subsequently grown oxide layer may not be uniform because the initial oxide layer is not completely removed Therefore, it would be desirable to have a process for preventing these dark spots or defects from forming on oxide layers during the manufactuiing process in order to achieve a higher overall yield ol acceptable wafers DISCLOSURE OF INVENTION A method of forming uniform oxide layers on a semiconductor substrate by reducing descum induced defects is disclosed The semiconductor substrate includes a wafer, an oxide layer on the wafer and a developed photoresist mask on the oxide layer In one embodiment, the semiconductor substrate is heated prior to descumming In an alternative embodiment, the photoresist mask is cured prior to heating and descumming Other features and advantages of the present invention will be apparent Irom the detailed description of the invention BRIEF DESCRIPTION OF SEVERAL VIEWS OF THE DRAWINGS FIG 1 is a photograph of the unwanted dark spots on a wafer substrate after ashing, FIG 2 is a partial cross-sectional view of an oxide layei formed on a wafer substrate, FIG 1 is a partial cross sectional view of the substrate after the formation of a photoresist layer on the oxide layer, FIG 4 is a partial cross sectional view of the wafer substrate after the photoresist has been developed exposing a region of the oxide layer, FIG 5 is a partial cross sectional view of the waler substrate after the oxide layer has been etched, FIG 6 is a partial cross-sectional view of the wafer substrate after the photoresist layer has been stripped, FIG 7 is a partial cross-sectional view of the wafer substrate after a new layer of oxide has been grown, FIG 8 is a partial cross-sectional view of a wafer substrate after the formation of a floating gate on the first and second oxide layers, FIG 9 is a partial cross sectional view of a wafer substrate after formation and development of a photoresist layer and after the substrate has been descummed, FIG 10 is a partial cross sectional view of a wafer substrate alter the oxide layers have been etched, and FIG 1 1 is a partial cross sectional view of the wafer substrate after a third layer of oxide has been grown It should be appreciated that for simplicity and clarity of illustration elements shown in the Figures have not necessarily been drawn to scale For example dimensions of some of the elements are exaggerated relative to each other for clarity MODES FOR CARRYING OUT THE INVENTION Referring to FIG 2, first oxide layer 2, a select gate oxide layer, is formed to overlie the surface of semiconductor substrate 4 Preferably, semiconductor substrate 4 is a single crystal silicon substrate Semiconductor substrate 4 has an upper surface 6 previously processed to remove debris and native oxides and a bottom surface 7 Preferably, first oxide layer 2 is formed by thermally oxidizing surface 6 at an elevated temperature in the presence of dry molecular oxygen Preferably, the oxidation process is carried out at a temperature of about 700 to about 1500°C The oxidation process forms a silicon oxide layer preferably having a thickness of about 50 to about 150 angstroms, and more preferably a thickness of about 100 angstroms The oxidation process can be carried out in a batch-type thermal oxidation furnace After forming the first oxide layer the substrate is processed to remove any impurities, and a photoresist layer 8 is formed to overlie the first oxide layer as illustrated in FIG 1 Preferably, photoresist layer 8 is ultraviolet sensitive and is a positive resist Selected portions of the photoresist layer 8 are then exposed through a mask The exposed photoresist is then developed and removed leaving a portion 10 of the oxide layer exposed The photoresist layer may be developed by methods generally known in the art including but not limited to. immersion, spray and puddle techniques FIG 4 illustrates the exposed portion 10 of the oxide layer 2 After the photoresist is developed, the substrate is generally descummed using Oτ chemistries to remove any undeveloped or residual photoresist The wafer temperature during a conventional descum process is generally between 80-100°C However as prev iously discussed dark spots or delects may occur on the oxide layer 2 after the descum process It is believed that photo active compound left ovei from developing the photoresist adheres to "cold spots" on the exposed portion of the oxide layer during the descumming process, and causes the dark spots to form as shown in FIG 1 It has been discovered that if the substrate is heated before descumming, "cold spots" on the water are eliminated, thus preventing the formation of dark spots on the exposed region of the oxide layer The substrate may be heated by any method well known in the art of semiconductor processing In one embodiment of the present invention, the substrate is heated by a lamp in an enclosed treatment chamber In a preferred embodiment, the wafer is placed under a halogen lamp with a power of 120V/1000W at 80% power or 800 W for 24 seconds In an alternative embodiment, the substrate is positioned over a horizontally disposed heated stage in an enclosed treatment chamber Preferably, the heated stage is at a temperature from 200-270°C The bottom surface 7 of the substrate rests horizontally on top of pins, which extend through openings in the stage Thus, the semiconductor substrate and stage are in parallel horizontal planes In order to heat the substrate, the pins are lowered until the bottom of the substrate is resting on the top of the stage In a preferred embodiment, the substrate remains on the stage for from two to five seconds and is healed to a temperature from 100 to 140°C In another preferred embodiment, the substrate remains on the stage for three seconds and is heated to about 130°C Once the substrate is heated, the pins are raised so the bottom surface of the substrate is no longer in contact with the surface of the stage After the heating step, the substrate is descummed in order to remove any residue that is leftover from developing the photoresist layer The descum process can be carried out in a conventional barrel type batch asher or a downstream wafer to wafer asher After the substrate has been descummed, the exposed region of oxide layer 10 is etched or stripped as illustrated in FIG 5 The oxide layer may be etched by conventional wet or dry methods that are well known in the art semiconductor fabrication Dry etch methods that can be used to etch the exposed region of the oxide layer include plasma etching, ion milling, and reactive ton etching Wet etch methods include using hydrofluoric acid Preferably, a buffered oxide etch of hydrofluoric acid, ammonium fluoride and water is used to etch the exposed region of the oxide layer After the exposed region of the oxide layer is etched, the remaining photoresist 8 is stripped as shown in FIG 6 Both wet and dry methods that are well known in the art of semiconductor fabrication can be used to strip the remaining photoresist layer 8 Such methods include but are not limited to use of sulfuπc acid and oxidant solutions and conventional 0 2 plasma stripping A new oxide layer 14, a tunnel oxide layer, is then grown over the first oxide layer 2 and the wafer substrate 4 as shown in FIG 7 to produce multiple thickness oxide layers When heating the substrate, it is important not to over heat the substrate as overheating will cause the layer of photoresist to begin to melt which will in turn create problems during subsequent processing steps To prevent the flow of the photoresist during some processes, the substrate may be subjected to an ultraviolet (UV) curing process prior to heating The UV cure process hardens the photoresist prior to heating step to ensure that the photoresist profile is maintained Any UV cure methods well known in the art of semiconductor fabrication may be used to cure the photoresist In a preferred UV cure process, the substrate is placed in an enclosed treatment chamber under a UV source and heated for between 40 to 50 seconds In particular, the substrate is placed beneath a UV lamp, which is set at ' low power", 1800-2200W and 100- 1 10 mW/cm 2 , for 10 seconds The power of the UV lamp is then increased to ' high power", 4400-4800W and 275 mW/cra'. and the substrate remains under the UV lamp for an additional 35 seconds While the wafer is beneath the UV lamp, the wafer is on heated stage or plate For the first 20 seconds of the UV cure process, the heated stage is at a temperature of 1 10°C Then, for the last 25 seconds of the UV cure process, the temperature of the heated stage is raised from 1 10°C to 130°C at a rate of 0 8 °C/sec If the temperature of the heated stage is increased too quickly, the photoresist may wrinkle, swell or bubble which will destroy the desired photoresist profile The processes discussed above are described in more detail in the examples below It should be understood that that the present invention is not deemed limited to these specific examples EXAMPLE 1 In an enclosed treatment chamber, the substrate is placed on pins which are above a heated stage having a temperature of 200°C The pins are lowered, and the bottom surface of the substrate is in contact with the heated stage for 3 seconds The pins are then raised so that the substrate is no longer in contact with the heated stage Subsequently, the substrate is descummed by ashing for 2 seconds under the following conditions RF=100 W, Pressures 200mT, 0 2 /N, Ratιo=2000/200 seem EXAMPLE 2 In an enclosed treatment chamber, the substrate is placed on pins, which are above a heated stage having a temperature of 250°C The substrate is UV cured by the preferred process described above The pins are lowered, and the bottom surface of the substrate is in contact with the heated stage for 3 seconds The pins are then raised so that the substrate is no longer in contact with the heated stage Subsequently, the substrate is descummed by ashing for 10 seconds under the following conditions RF=100 W, Pressure= 1200mT, 0 2 /N 2 Ratιo=2000/200 seem EXAMPLE 3 In an enclosed treatment chamber, the substrate is placed on pins, which are above a heated stage having a temperature of 270°C The substrate is UV cured by the preferred process described above The pins are lowered and the bottom surface of the substrate is in contact with the heated stage for 3 seconds The pins are then raised so that the substrate is no longer in contact with the heated stage Subsequently, the substrate is descummed by ashing for 10 seconds under the following conditions RF=1 100 W, Pressure=1400 mT, O 2 =3550 seem EXAMPLE 4 In an enclosed treatment chamber, the substrate is placed on pins, which are above a heated stage having a temperature of 270°C The substrate is UV cured by the preferred process described above, and then heated by a halogen lamp at 800 W for 24 seconds Subsequently, the substrate is descummed by ashing for 10 seconds under the following conditions seem The process described above may be repeated to create additional oxide layers with various thicknesses For example, after growing the tunnel oxide layer 14, a floating gate 16 is formed over oxide layers 2 and 14 as shown in FIG 8 A photoresist layer 18 is then formed to overlie oxide layers 2 and 14 and gate structure 16 As shown in FIG 9, the photoresist layer 18 is exposed through a mask, and the exposed photoresist is then developed leaving a portion 15 of oxide layers 2 and 14 exposed After the resist is developed, the photoresist is UV cured and heated belore the substrate is descummed Then, the exposed portion 15 of oxide layers 2 and 14 is etched away and the remaining photoresist is stripped away as shown in FIG. 10 As illustrated in Figure 1 1 , a third oxide layer 20, the peripheral gate oxide layer, having a thickness different than oxide layers 2 and 14 is grown on the surface of wafer substrate 4 Thus, there has been disclosed in accordance with the invention a process for fabricating multiple uniform oxide layers in a semiconductor device that fully provides the advantages set forth above Although the invention has been described and illustrated with reference to specific illustrative embodiments thereof, it is not intended that the invention be limited to those illustrative embodiments Those skilled in the art will recognize that variations and modifications can be made without departing from the spirit of the invention It is therefore intended to include within the invention all such variations and modifications that fall within the scope of the appended claims and equivalents thereof

Claims: CLAIMS 1 A method for fabricating a semiconductor structure, the method characterized by heating a substrate by placing the substrate on a surface having a temperature from 200°C to 270°C for from 2 to 5 seconds, said substrate characterized by (a) a wafer (4), (b) a first oxide layer (2) on the wafer, (c) a developed photoresist mask (8) on said first oxide layer, and (d) at least one exposed region (10) on the first oxide layer, and descumming the exposed region (10) of the first oxide layer 2 The method Claim 1 , wherein heating the substrate is further characterized by placing the substrate on pins that extend through and above the surface, lowering the substrate onto the surface to heat the wafer, and lifting the substrate above the surface 3 The method of Claim 1 , further characterized by etching the first oxide layer (2) 4 The method of Claim 3, further characterized by stripping the photoresist mask (8) 5 The method of Claim 4, further characterized by growing a second oxide layer (14) on the substrate 6 A method for fabricating a semiconductor structure, the method characterized by heating a substrate by placing the substrate under a halogen lamp for from 15-30 seconds, said substrate characterized by (a) a wafer (4), (b) a first oxide layer (2) on the wafer, (c) a developed photoresist mask (8) on said first oxide layer, and (d) at least one exposed region (10) on the first oxide layer, and descumming the exposed region of the first oxide layer 7 A method of fabricating a semiconductor substrate, the method characterized by heating a substrate by placing the substrate on a surface having a temperature from 200°C to 270°C for from 2 to 5 seconds, said substrate characterized by (a) a wafer (4), (b) a first oxide layer (2) on the wafer (c) a developed and cured photoresist mask (8) on said first oxide layer, and (d) at least one exposed region ( 10) of the oxide layer, and descumming the exposed region ( 10) of the oxide layer 8 The method of Claim 7 wherein the photoresist mask (8) is cured by placing the substrate on a heated stage under a UV lamp for from 40-50 seconds 9. The method of Claim 8 further characterized by etching the first oxide layer (2). 10. The method of Claim 9 further characterized by stripping the photoresist mask (8) and growing a second oxide layer (14).

Inventors: HUI ANGELA T, OGURA JUSUKE, HUI, ANGELA, T., OGURA, JUSUKE
Applicants: ADVANCED MICRO DEVICES INC, FUJITSU LTD, ADVANCED MICRO DEVICES, INC., FUJITSU LIMITED
Application year: 2001
Main classification: H01L21
IPC codes: H01L21, H01L27, H01L29