Well cement fluid loss control additive

Abstract: A well cement fluid loss control additive comprises hydroxyethylcellulose of molecular weight, from 30,000 to 90,000, which is ethoxylated with from 1 to 4 moles ethylene oxide per anhydroglucose unit.

Description: The present invention relates to subterranean well cementing operations and, more particularly, to environmentally acceptable well cement fluid loss control additives, well cement compositions containing the additives and methods of using the compositions. Hydraulic cement compositions are commonly utilized in subterranean well completion and remedial operations. For example, hydraulic cement compositions are used in primary cementing operations whereby strings of pipe such as casings and liners are cemented in well bores. In performing primary cementing, a hydraulic cement composition is pumped into the annular space between the walls of a well bore and the exterior surfaces of a pipe string disposed therein. The cement composition is permitted to set in the annular space thereby forming an annular sheath of hardened substantially impermeable cement therein which supports and positions the pipe string in the well bore and bonds the exterior surfaces of the pipe string to the walls of the well bore. Hydraulic cement compositions are also utilized in remedial cementing operations such as plugging highly permeable zones or fractures in well bores, plugging cracks or holes in pipe strings and the like. Fluid loss control agents are used in well cement compositions to reduce fluid loss from the cement compositions to the permeable formations or zones into or through which the cement compositions are pumped. In primary cementing, the loss of fluid, i.e. water, from the cement compositions to a permeable subterranean formation or zone can result in premature gelation of the cement composition whereby bridging of the annular space between the permeable formation or zone and the pipe string being cemented prevents the cement composition from being placed over the entire length of the annulus. Heretofore, environmentally acceptable hydroxyethylcellulose having an average molecular weight of about 90,000 and higher has been utilized as a well cement composition fluid loss control agent. However, the use of such hydroxyethylcellulose as a cement composition fluid loss additive has involved a number of disadvantages. For example, the ability of the hydroxyethylcellulose to prevent fluid loss in a cement composition decreases rapidly at temperatures above about 230°F (110°C). In addition, the hydroxyethylcellulose has a limited salt tolerance. That is, if the salt content of the water in the cement composition is above about 5% by weight of the water, the ability of the hydroxyethylcellulose to prevent fluid loss is reduced. In offshore cementing operations, the hydroxyethylcellulose has been utilized in an aqueous solution so that it can be readily added to the mix water or the cement slurry. In order to prevent the aqueous solution of the hydroxyethylcellulose from having too high a viscosity, the hydroxyethylcellulose must be dissolved in relatively large quantities of water making its mixing and handling more difficult than other fluid loss control agents. Additives for cement compositions are disclosed in the prior art in GB2146320A and in Chemical Abstracts, vol. 103 no. 6, 12 th August 1985 (1985-08-12) Columbus, Ohio US; abstract no. 41616u, HAZAMA-GUMI: page 281; XP002194321 & JP 60021843A (ID) 4 February 1985 There is a need for an improved environmentally acceptable hydroxyethylcellulose fluid loss control agent which can be utilized at temperatures higher than 230°F(110°C), which can be dissolved in relatively small quantities of water without greatly increasing the viscosity of the solution and which has a higher salt tolerance while maintaining the same fluid loss control. We have now found a hydroxyethylcellulose-based composition which can meet the needs described above and overcome or reduce the deficiencies of the prior art. In one aspect, the present invention provides a well cement fluid loss control additive comprised of hydroxyethylcellulose having a molecular weight of from 30,000 to 90,000 and being ethoxylated in an amount of from 1 to 4 moles of ethylene oxide per anhydroglucose unit, and a temperature stability increasing agent. The degree of ethoxylation of the hydroxyethylcellulose provides an average molecular substitution of ethylene oxide of 2.5 per anhydroglucose unit. The fluid loss additive also includes a temperature stability increasing agent to increase the temperature at which the additive remains stable and continue to prevent fluid loss. The temperature stability increasing agent is preferably selected from synthetic hectorite, magnesium oxide and sodium thiosulfate. Of these, magnesium oxide is preferred. The invention also provides well cement compositions basically comprised of a hydraulic cement, water present in an amount sufficient to form a pumpable slurry, and a well cement fluid loss control additive of this invention. When temperature stability increasing agent is selected from synthetic hectorite, magnesium oxide and sodium thiosulfate, the synthetic hectorite or sodium thiosulfate can be added in particulate solid form directly to the hydraulic cement or mix water utilized, or it can be dissolved in water whereby a storable aqueous solution results which can be readily combined with the mix water or cement slurry. Magnesium oxide should only be added to the mix water of the cement slurry. The invention further includes a method of cementing a zone in a subterranean formation penetrated by a well bore, which comprises using a cement composition as described above (which need not necessarily include the temperature stability increasing agent) to cement a zone, and allowing the cement composition to set into an impermeable solid mass therein. The well cement fluid loss control additive of this invention is basically comprised of hydroxyethylcellulose having a reduced molecular weight in the range of from about 30,000 to about 90,000, i.e. an average molecular weight of about 60,000, ethoxylated in an amount in the range of from about 1 to about 4 moles of ethylene oxide per anhydroglucose unit, i.e. an average molecular substitution in the range of from about 2.2 to about 2.7 per anhydroglucose unit, most preferably 2.5 per anhydroglucose unit. The average molecular weight of commercially available hydroxyethylcellulose is about 90,000 or higher. While such hydroxyethylcellulose can be and has been utilized in well cement compositions as an environmentally acceptable well cement fluid loss control additive, it suffers from the disadvantages that it is unstable and its fluid loss control properties are significantly reduced at temperatures above about 230°F (110°C) and/or when it is in contact with salt water containing salt in an amount above about 5% by weight of the water. In addition, when the commercially available hydroxyethylcellulose is dissolved in water so that it can be added to a cement slurry or its mix water as a liquid, the resulting solution has a high viscosity. As a result, a liquid hydroxyethylcellulose solution containing only about 7.5% by weight commercial hydroxyethylcellulose can be used. The above is contrasted with the ethoxylated hydroxyethylcellulose of reduced molecular weight of the present invention which is stable and effectively controls fluid loss from cement compositions at temperatures above 230°F (110°C) to at least about 260°F (127°C), can be utilized in contact with salt water containing salt up to 37.2% by weight without losing effectiveness and can be dissolved in water up to about 12.5% by weight of the resulting solution which remains relatively low in viscosity. In order to improve the temperature stability of the improved ethoxylated hydroxyethylcellulose fluid loss control additive of this invention, a temperature stability increasing agent can be combined with the ethoxylated hydroxyethylcellulose. Suitable temperature stability increasing agents which can be utilized include, but are not limited to, synthetic hectorite, magnesium oxide and sodium thiosulfate. Of these, magnesium oxide is preferred. When used, the temperature stability increasing agent is combined with the ethoxylated hydroxyethylcellulose in an amount in the range of from about 50% to about 500% by weight of the ethoxylated hydroxyethylcellulose, preferably in an amount of about 100%. The improved environmentally acceptable ethoxylated hydroxyethylcellulose fluid loss control additive of this invention can be prepared by treating a commercially available hydroxyethylcellulose having an average molecular weight of about 90,000 or higher with hydrogen peroxide using known techniques and amounts. That is, the commercially available hydroxyethylcellulose is slurried in a mixture of acetone and water and hydrogen peroxide is added to the slurry in an amount and under conditions such that the molecular weight of the hydroxyethylcellulose is reduced to in the range of from about 30,000 to about 90,000, i.e., an average molecular weight of about 60,000. The reduced molecular weight hydroxyethylcellulose formed is separated from the reaction mixture purified, dried and ground. A preferred environmentally acceptable fluid loss control additive of this invention is comprised of hydroxyethylcellulose having a reduced molecular weight in the range of from about 30,000 to about 90,000 ethoxylated in an amount in the range of from about 1 to about 4 moles of ethylene oxide per anhydroglucose unit. Another preferred environmentally acceptable fluid loss control additive of this invention is comprised of hydroxyethylcellulose having a reduced average molecular weight of about 60,000 ethoxylated in an average amount of about 2.5 moles of ethylene oxide per anhydroglucose unit. Yet another preferred fluid loss control additive of this invention is comprised of hydroxyethylcellulose having a reduced molecular weight in the range of from about 30,000 to about 90,000 ethoxylated in an amount in the range of from about 1 to about 4 moles of ethylene oxide per anhydroglucose unit and having a temperature stability increasing agent selected from the group consisting of synthetic hectorite, magnesium oxide and sodium thiosulfate combined therewith in an amount in the range of from about 50% to about 500% by weight of the ethoxylated hydroxyethylcellulose. Still another preferred fluid loss control additive of this invention is comprised of hydroxyethylcellulose having a reduced average molecular weight of about 60,000 ethoxylated in an average amount of about 2.5 moles of ethylene oxide per anhydroglucose unit and having a temperature stability increasing agent comprised of magnesium oxide combined therewith in an amount of about 100% by weight of the ethoxylated hydroxyethylcellulose. The improved well cement compositions of the present invention are basically comprised of a hydraulic cement, sufficient water to form a pumpable slurry and the environmentally acceptable well cement fluid loss control additive described above. A variety of hydraulic cements can be utilized in accordance with the present invention including those comprised of calcium, aluminum, silicon, oxygen and/or sulfur which set and harden by reaction with water. Such hydraulic cements include, but are not limited to, Portland cements, pozzolana cements, gypsum cements, high alumina content cements, silica cements and high alkalinity cements. Portland cements are generally preferred for use in accordance with the present invention, and Portland cements of the types defined and described in API Specification For Materials And Testing For Well Cements , API Specification 10, Fifth Edition, dated July 1, 1990 of the American Petroleum Institute are particularly preferred. API Portland cements include classes A. B, C, G and H. API classes G and H are preferred with class G being the most preferred. The water utilized in the compositions of this invention can be fresh water, salt water, i.e., water containing one or more salts dissolved therein, brine, i.e., saturated salt water produced from subterranean formations, or seawater. Generally, the water can be from any source provided it does not contain an excess of compounds that adversely affect other components in the cement compositions. The water is present in a cement composition of this invention in an amount sufficient to form a pumpable slurry. More particularly, the water is present in a cement composition of this invention in an amount in the range of from about 25% to about 100% by weight of hydraulic cement therein, more preferably in an amount of about 44%. An environmentally acceptable well cement fluid loss control additive of this invention described above is included in a cement composition of this invention in an amount in the range of from about 0.1% to about 2% by weight of cement in the composition. As mentioned, the additive can be comprised of an ethoxylated hydroxyethylcellulose having a reduced molecular weight or it can be comprised of the ethoxylated hydroxyethylcellulose of a reduced molecular weight combined with a temperature stability increasing agent. The additive can be mixed in particulate solid form with the hydraulic cement or mixing water prior to mixing the cement composition or it can be dissolved in water to form a storable liquid additive which can readily be added to the mixing water or to the cement slurry after it is formed. A preferred cement composition of this invention is comprised of a hydraulic cement, water present in an amount sufficient to form a pumpable slurry and an environmentally acceptable fluid loss control additive comprised of hydroxyethylcellulose having a reduced average molecular weight of about 60,000 ethoxylated with an average amount of about 2.5 moles of ethylene oxide per anhydroglucose unit, the fluid loss control additive being present in the composition in an amount of about 0.75% by weight of cement in the composition. Another preferred cement composition of this invention is comprised of hydraulic cement, water present in an amount sufficient to form a pumpable slurry and an environmentally acceptable fluid loss control additive comprised of hydroxyethylcellulose having a reduced molecular weight in the range of from about 30,000 to about 90,000 ethoxylated in an amount in the range of from about 1 to about 4 moles of ethylene oxide per anhydroglucose unit, the fluid loss control additive being present in the composition in an amount in the range of from about 0.1% to about 2% by weight of cement in the composition. Yet another preferred composition of this invention is comprised of a hydraulic cement, water present in an amount sufficient to form a pumpable slurry and an environmentally acceptable fluid loss control additive comprised of hydroxyethylcellulose having a reduced average molecular weight of about 60,000 ethoxylated in an average amount in the range of from about 2.2 to about 2.7 moles of ethylene oxide per anhydroglucose unit combined with a temperature stability increasing agent selected from the group consisting of synthetic hectorite, magnesium oxide and sodium thiosulfate, the temperature stability increasing agent being present in the additive in an amount in the range of from about 50% to about 500% by weight of the ethoxylated hydroxyethylcellulose and the additive being present in the cement composition in an amount in the range of from about 0.1% to about 2% by weight of cement in the composition. Still another preferred composition of this invention is comprised of hydraulic cement, sufficient water to form a pumpable slurry and an environmentally acceptable fluid loss control additive comprised of hydroxyethylcellulose having a reduced average molecular weight of about 60,000 ethoxylated in an average amount of about 2.5 moles of ethylene oxide per anhydroglucose unit combined with a temperature stability increasing agent comprised of magnesium oxide, the temperature stability increasing agent being present in an amount of about 100% by weight of the ethoxylated hydroxyethylcellulose and the fluid loss control additive being present in the cement composition in an amount of about 0.75% by weight of cement in the composition. As will be understood by those skilled in the art, the well cement compositions of this invention can include other conventional well cement additives such as set accelerators, set retarding agents, fillers, weighting materials and the like. The environmentally acceptable fluid loss control additives of this invention are of low cost as compared to synthetic fluid loss control additives, they function to prevent fluid loss at temperatures of 280°F (138°C) and higher, they remain stable in the presence of salt water and they can be dissolved in water to form storable liquid additives in sufficient amounts without increasing the viscosities of the resulting additive solutions or increasing the viscosities of the cement compositions in which they are utilized to unacceptable levels. The methods of the present invention for cementing a subterranean zone penetrated by a well bore are basically comprised of the steps of preparing a cement composition of this invention as described above, placing the cement composition in the zone to be cemented and allowing the cement composition to set into an impermeable solid mass therein. In order to further illustrate the environmentally acceptable well cement fluid loss control additives, well cement compositions and methods of this invention, the following examples are given. Example 1 A cement composition including a commercially available hydroxyethylcellulose fluid loss control additive having an average molecular weight of about 90,000 and other conventional additives was prepared. Various additional cement compositions which included a fluid loss control additive of the present invention and the same other conventional additives were also prepared. The composition including the conventional fluid loss control additive was tested at a temperature of 230°F (110°C) and the compositions containing the fluid loss control additive of the present invention were tested at 250°F (121°C) and 260°F (127°C) for thickening time, rheology, free water, settling, and stirring fluid loss. The results of these tests are set forth in Table I below. The thickening time, rheology, free water and settling tests were all conducted in accordance with the procedures set forth in the above mentioned API Specification 10. The stirring fluid loss and BP-settling tests were performed in accordance with standard test procedures set forth in the Halliburton Global Standard Manual dated May 1997. The specific gravity top-bottom test is conducted by taking four 10 cubic centimeter samples from the cement slurry utilized in the free water test. The specific gravities of the samples are then determined and if there is a large difference between the top and bottom specific gravities, instability is indicated. The results of these tests are given in Table I below. From Table I it can be seen that the fluid loss control additive of the present invention is effective up to a temperature of at least 260°F (127°C). Example 2 Additional test cement slurries were prepared as described in Example 1 except that the ethoxylated hydroxyethylcellulose fluid loss control additive of the present invention included synthetic hectorite and the tests were conducted at temperatures of 230°F (110°C), 260°F (127°F), 275°F (135°C) and 300°F (149°C). The test cement compositions were tested in the same manner as described in Example 1. The results of these tests are given in Table II below. From Table II it can be seen that the fluid loss control additive of this invention including synthetic hectorite had increased temperature stability. Example 3 The procedure set forth in Example 2 was repeated except that the cement composition including the commercially available fluid loss control additive was not tested and the fluid loss control additive of the present invention included magnesium oxide. Also, the tests were conducted at 230°F (110°C), 250°F (121°C), 260°F (127°C) and 280°F (138°C). The test cement compositions were tested in the same manner as described in Example 1 except the BP-settling test was not conducted. The results of these tests are given in Table III below. From Table III it can be seen that the magnesium oxide in the fluid loss control additive increased the temperature at which the fluid loss control additive remains stable.

Claims: A well cement fluid loss control additive comprised of hydroxyethylcellulose having a molecular weight of from 30,000 to 90,000 and being ethoxylated in an amount of from 1 to 4 moles of ethylene oxide per anhydroglucose unit and a temperature stability increasing agent. An additive according to claim 1, wherein said hydroxyethylcellulose has an average molecular weight of about 60,000. An additive according to claim 1 or 2, wherein said hydroxyethylcellulose is ethoxylated in an average amount of about 2.5 moles of ethylene oxide per anhydroglucose unit. An additive according to claim 1, 2 or 3, wherein the temperature stability increasing agent is synthetic hectorite, magnesium oxide or sodium thiosulfate. An additive according to claim 1, 2, 3 or 4, wherein said temperature stability increasing agent is present in said additive in an amount of from 50% to 500% by weight of said ethoxylated hydroxyethylcellulose. An improved well cement composition comprising a hydraulic cement; water present in an amount sufficient to form a pumpable slurry; and a fluid loss control additive as claimed in any of claims 1 to 5. A composition according to claim 6, wherein said hydraulic cement is Portland or the equivalent cement, preferably Portland API Class G cement. A composition according to claim 6 or 7, wherein said water is fresh water or salt water. <> A composition according to claim 6, 7 or 8, wherein said water is present in an amount of from 25% to 100% by weight of cement in said composition. A method of cementing a subterranean zone penetrated by a well bore, which method comprises placing a cement composition in said zone to be cemented; and allowing said cement composition to set into an impermeable solid mass therein; wherein said cement composition comprises a hydraulic cement, water present in an amount to form a pumpable slurry, and a well cement fluid loss control additive comprised of hydroxyethylcellulose having a molecular weight of from 30,000 to 90,000 and being ethoxylated in an amount of from 1 to 4 moles of ethylene oxide per anhydroglucose unit. A method according to claim 10, wherein said hydroxyethylcellulose has an average molecular weight of about 60,000. A method according to claim 10 or 11, wherein said hydroxyethylcellulose is ethoxylated in an average amount of about 2.5 moles of ethylene oxide per anhydroglucose unit. A method according to claim 10, 11 or 12, wherein said hydraulic cement is Portland or the equivalent cement, preferably Portland API Class G cement. A method according to any one of claims 10 to 13, wherein said water is fresh water or salt water. A method according to any one of claims 10 to 14, wherein said water is present in an amount of from 25% to 100% by weight of cement in said composition. A method according to claim 10, wherein the cement composition comprises a cement composition according to any one of claims 6 to 9.

Inventors: DAO BACH, MELBOUCI MOHAND, VIJN JAN PIETER, DAO, BACH, MELBOUCI, MOHAND, VIJN, JAN PIETER
Applicants: HALLIBURTON ENERGY SERV INC, HERCULES INC, HALLIBURTON ENERGY SERVICES, INC., HERCULES INCORPORATED
Application year: 2001
Main classification: C04B24
IPC codes: C04B28, C09K8, C04B24