DUPLEX STAINLESS STEEL

Abstract: The present invention relates to a duplex stainless steel alloy with austenite-ferrite structure, which in hot extruded and annealed finish shows, high strength, good corrosion resistance and good weldability, which is characterized in that the alloy contains in weight-% max 0.05 % C, 0-2.0 % Si, 0-3.0 % Mn, 25-35 % Cr, 4-10 % Ni, 2-6 % Mo, 0.3-0.6 % N, as well as Fe and normally occurring impurities and additions, whereby the content of ferrite is 30-70 %.

Description: DUPLEX STAINLESS STEEL FIELD OF THE INVENTION The present invention relates to a duplex stainless steel with high contents of Cr, Mo and N. The content of ferrite lies in the range of 30-70 %. The material is especially suited for production tubes for extraction of crude oil and gas, but can also be used in applications where good corrosion resistance together with high strength is required. BACKGROUND OF THE INVENTION In the description of the background of the present invention that follows reference is made to certain structures and methods, however, such references should not necessarily be construed as an admission that these structures and methods qualify as prior art under the applicable statutory provisions. Applicants reserve the right to demonstrate that any of the referenced subject matter does not constitute prior art with regard to the present invention. Duplex steels are characterized by an austenite-ferrite structure where both phases have different chemical composition. Modern duplex stainless steels will mainly be alloyed with Cr, Mo, Ni and N. Swedish Patent 8504131 -7 describes a duplex stainless steel grade with commercial denotation SAF 2507 (UNS S32750), which is mainly alloyed with high contents of Cr, Mo and N for good resistance to pitting corrosion. This resistance is often described with a PRE-number (PRE = Pitting Resistance Equivalent = %Cr+3.3%Mo+16%N). Thus, the alloy is consequently optimized with respect to this property, and has certainly good resistance in many acids and bases, but above all the alloy is developed for resistance against chloride environments. Cu and W were subsequently also used as alloying additions. Consequently, a steel grade with commercial denotation DP3W has a composition similar in character as SAF 2507, but it has been alloyed with 2 0 % W as substitute for a part of the Mo content in the alloy A steel grade with commercial denotation Zeron 100 is a further steel grade of a similar kind as SAF 2507, but this is alloyed with approximately 0 7 % Cu and approximately 0 7 % W All above described steel grades have a PRE-number higher than 40 irrespective to the method of calculation Another type of duplex alloy with high resistance to chloride is the steel grade described in the Swedish Patent 9302139-2 This alloy is characterized by Mn 0 3-4 %, Cr 28-35 %, Ni 3-10 %, Mo 1 -3 %, Cu max 1 0 % and W max 2 0 %, and has a high PRE-number above 40 The biggest difference compared to the established superduplex steels SAF 2507 and others is that the contents of Cr and N are higher in this steel grade The steel grade has found use in environments where resistance to intergranular corrosion and corrosion in ammonium carbamate is of importance, but the alloy has also a very high resistance to corrosion in chloride environments In oil and gas extraction applications, duplex steels are used in the form of production tubes, e g - tubes that transport oil up from the source to the oil-rig Oil wells contain carbon dioxide (CO2) and sometimes even hydrogen sulphide (H2S) An oil well containing CO2, but no bigger multitudes of H2S is called a sweet oil well A sour oil well, however, contains H2S in varying amounts The production tubes will be supplied in threaded finish By means of couplings the tubes will be joined to the necessary lengths Because oil wells are situated at considerable depth, the length of a production tube can become large. Demands on the material, which shall be used in this application, can be summarized according to the following: * Yield point in tension min 1 10 ksi (760 MPA) * Resistance to corrosion caused by CO2 or H2S. Material should be qualified and included in for example the standard NACE MR-0175 * Good impact toughness down to -46°C, at least 50J * Further the material shall be possible to manufacture in the shape of seamless tubes as well as that one can produce threads and fitting couplings for tubes. In the present-day situation either low alloyed carbon steels, austenitic stainless steel, duplex stainless steel or nickel-based alloys, are used for such applications, depending on the level of corrosive activity in the oil well. Limits for different materials have been taken out. For sweet oil wells one can normally use carbon-steel or low alloyed stainless steel, for example, martensitic 13Cr-steel. In sour oil wells, where the partial pressure for H2S exceeds 0.01 psi, normally the use of a stainless steel is required. Duplex steels are, among other things, are an economical alternative to stainless steels and nickel-based alloys, thanks to a low content of nickel. The duplex steels fill the gap between high-alloyed steels and low-alloyed carbon steels and martensitic 13Cr-steel. A typical application range for duplex steels of the type 22Cr and 25Cr is where the partial pressure of H2S in the gas in the oil well lies in the area 0.2 to 5 psi. Since there is a requirement on the strength level of at least 110 ksi, 22Cr-och 25Cr-steel is supplied with a cold rolled finish, which increases the strength to desired level, but this also limits the resistance of the material against stress corrosion caused by H2S. Material of the type 22Cr, in an annealed condition, has only a yield point limit of 75 ksi, a corresponding value for 25Cr is 80 ksi. Besides, from the production point of view it is difficult to produce production tubes from such materials, because the strength depends of both the total degree of reduction and the type of method for the reduction, i.e. - drawing or rolling. Additionally, a cold rolling operation is costly for the production. The impact toughness of the material deteriorates considerably by the cold rolling, which further limits the applicability of such materials. In order to solve these problems there is a need of an alloy which can be delivered in a hot extruded and annealed finish, where the strength is at least 1 10 ksi. Simultaneously, the alloy shall have good workability and, without problems, can be extruded into seamless tubes. The strength of duplex alloys can be increased by alloying with high contents of the elements Cr, Mo and N. In the present-day situation there are duplex steels with up to 29 % Cr and 0.4 % N, which have yield point limits of 95 ksi, but in this alloy the content of Mo must be held low in order to avoid precipitations of, for example, sigma phase. When the content of Mo is high, the content of Cr has to be reduced to approximately 25% if one wants to retain the structural stability. Thus, there seems to exist an upper limit for the combination of Cr and Mo in order to retain the structural stability. The content of N is limited upwards to 0.3 %, for 25 % Cr-alloys and to 0.4 % for 29 % Cr-alloys. BRIEF DESCRIPTION OF THE DRAWINGS Fig. 1 shows a linearized plot of the yield strength vs. alloy content. Fig. 2a shows the impact toughness as -46°C as feature of N-content in the austenite phase. Fig. 2b shows the impact toughness at -46°C as a feature of the Cr- content in the austenite phase Fig. 3 shows the resulting CPT temperatures vs. calculated PRE- numbers from the ferrite phase. Fig. 4 shows the solution temperature for sigma phase, Tmaxσ, as a function of Si-content. SUMMARY OF THE INVENTION Systematic development work has surprisingly shown that by simultaneously elevating the elements Cr, Mo and N to high levels an unexpected positive synergistic effect of the elements is obtained. Partly it shows that Cr and Mo increase the solubility of N, which in its turn enables higher contents of Cr and Mo without precipitating higher amounts of intermetallic phase such as sigma phase. It is previously known that Cr and Mo increase the solubility of N, but the presently obtained contents are higher compared to what earlier was estimated as upper limits for what is possible to attain. The high contents of Cr, Mo and N give the alloy a very high strength and simultaneously a good workability for extrusion into seamless tubes. The yield point in tension exceeds 1 10 ksi in extruded and annealed condition, and the material also shows good corrosion properties. In order to obtain a combination of high strength and good impact toughness, an accurate combination of the contents of elements Cr, Mo and N must prevail. Besides exhibiting excellent mechanical properties the new alloy has a high resistance to pitting corrosion and crevice corrosion in chloride environments as well as a high resistance to stress corrosion cracking caused by hydrogen sulphide. In addition, the alloy is weldable, which means that the alloy according to the present invention is well suited for applications that require welding, such as for example seamless or seam-welded tubes for various coiled tubing applications Consequently, the alloy is especially suited for hydraulic tubes, such as umbilical tubes, which are used in order to control platforms in oilfields According to one aspect, the present invention provides a duplex stainless steel alloy having austenite-ferrite microstructure exhibiting, when hot extruded and having an annealed finish, good weldability, high strength as well as good and high resistance to corrosion, wherein the alloy comprises, in weιght-%- C max 0.05% Si 0-2.0% Mn 0-3.0%; Cr 25-35%; Ni 4-10 %; Mo 2-6 %; N 0.3-0.6 %; and Fe and normally occurring impurities and additions, wherein the ferrite content is 30-70 % by volume. According to a further aspect, the present invention provides an extruded seamless tube formed from the above-mentioned alloy, the tube having a yield point in tension, which exceeds 760 MPa. According to a further aspect, the present invention provides an umbilical tube formed from the above-mentioned alloy. According to another aspect, the present invention provides an article possessing resistance against corrosion in seawater formed from the above- mentioned alloy. According to yet another aspect, the present invention provides, an article having high strength and good corrosion resistance, the article formed from the above-mentioned alloy, the article being in the form of a seamless tube, a welding wire, a seam-welded tube, a strip, a wire, a rod, a sheet, a flange or a coupling. According to a further aspect, the present invention provides a plurality of butt-welded seamless or seam-welded tubes reeled into a coil formed from the above-mentioned alloy. DETAILED DESCRIPTION OF THE INVENTION According to one aspect, the present invention provides an alloy having a composition, which comprises, in weight-%: C max 0.05% Si 0-2.0% optionally Mn 0 - 3.0% Cr 25 - 35% Ni 4 - 10% Mo 2 - 6% N 0.3 - 0.6% balance Fe and normally occurring impurities and additions whereby ferrite content is 30-70 volume-percent. The principles and advantages of the alloy of the present invention, and selection of the desired ranges of the constituent elements of the alloy of the present invention which render the unexpected superiority of the alloy can be stated as follows. Carbon has to be considered a contaminant in this invention and has a limited solubility in both ferrite and austenite. The limited solubility implies a risk of precipitation of chromium carbides and the content should therefore be limited to max 0.05 %, preferably to max 0.03 % and most preferably to max 0.02 %. Silicon is utilized as deoxidizer under the steel production as well as it increases the floatability under production and welding. It is earlier known that high contents of Si support the precipitation of an intermetallic phase. It has surprisingly shown that an increased content of Si favorably affects the precipitation of sigma phase. For this reason a certain content of Si should optionally be permitted. However, the content of Si should be limited to max 2.0 %. Manganese will be added in order to increase the solubility of N in the material. However, Mn has only a limited influence on the solubility of N in the actual type of alloy. Instead, there are other elements with higher influence on the solubility. Besides, Mn in combination with high contents of sulphur can be the cause of manganese sulfides, which act as initiation points for pitting corrosion. The content of Mn should therefore be limited to between 0-3 %, and preferably 0.5% -1 .5%. Chromium is a very active element in order to improve the resistance to the plurality of corrosion types. Moreover, chromium increases the strength of the alloy. A high content of chromium implies additionally a very good solubility of N in the material. Consequently, it is desirable to keep the Cr-content as high as possible in order to improve the strength and the resistance to corrosion. For the very good strength properties and resistance to corrosion the content of chromium should be at least 25 %, preferably at least 29 %. However, high contents of Cr increase the risk for intermetallic precipitations For this reason the content of chromium should be limited upwards to max 35 % Nickel will be used as an austenite-stabihzing element and will be added to the alloy in suitable level in order to attain desirable content of ferrite In order to attain fernte-contents of between 30-70 %, alloying with 4 - 10 % nickel, preferably 5 - 9 %, is required Molybdenum is an active element, which improves the resistance to corrosion in chloride environments, as well as in reducing acids An excessive Mo-content in combination with a high Cr-content means that the risk for intermetallic precipitations increases Since Mo increases the strength, the content of Mo should in the present invention lie in the range of 2-6 %, preferably 3-5 % Nitrogen is a very active element, which partly increases the resistance to corrosion and partly increases the structural stability as well as the strength of the material Besides, a high N-content improves the reformation of austenite after welding, which ensures good properties for welded joints In order to attain a good effect of N, at least 0 3 % N should be added High contents of N increases the risk for precipitation of chromium nitrides, especially when the content of chromium simultaneous is high Furthermore, a high N- content implies that the risk for porosity increases because of that the solubility of N in the steel melt or weld pool will be exceeded Thus, the N-content should be limited to max 0 60 %, preferably 0 45 -0 55% N The content of ferrite is important in order to obtain good mechanical properties and corrosion properties, as well as good weldability From a corrosion point of view and welding point of view, it is desirable with a content of ferrite between 30-70 % in order to obtain good properties High contents of ferrite cause deterioration in low temperature impact toughness and resistance to hydrogen embhttlement. Therefore, the content of ferrite is therefore 30-70 %, preferably 35-55 %. Example 1 : In the example below the composition of a number of experimental heats illustrates the influence of different alloying elements on the properties. A number of experimental heats were produced by casting of 170 kg ingots, which were hot-forged into round bars. The bars were hot extruded into rods, from which the test material was taken out. From a material point of view the process can be considered being representative for the preparation in bigger scale, for example the production of seamless tubes with the extrusion method. Table 1 shows the composition of these experimental heats. Table 1 . Composition for experimental heats, weight-% Heat Cr Ni Mo Mn N C 605123 30.1 1 3.71 2.98 2.54 0.60 0.01 1 605125 29.93 9.01 3.0 2.87 0.34 0.014 605127 29.7 7.98 1 .03 0.37 0.30 0.01 1 631928 33.4 7.02 2.93 3.01 0.57 0.013 631930 33.7 6.64 1.19 0.29 0.57 0.012 631931 33.8 10.81 0.97 3.05 0.30 0.012 631933 29.8 4.92 2.99 0.32 0.58 0.015 631934 30.6 9.56 2.93 2.89 0.30 0.012 631936 31.1 3.82 1.0 3.0 0.61 0.017 631937 30.7 8.64 1.04 0.31 0.31 0.014 631945 31 .8 8.29 3.48 0.99 0.44 0.013 In order to investigate structural stability, the samples were annealed at 800-1200°C with 50°C steps. At the lowest temperatures, an intermetallic phase was formed. The lowest temperature, where the amount of intermetallic phase was insignificantly small, was determined with the help of studies using a light optical microscope. The material was then annealed at this temperature during three minutes, then it was quenched with a constant rate of -140°C/min to room temperature. The amount of sigma phase in this material was calculated with the assistance of point counting with a light optical microscope. The results are shown in Table 2. Table 2: Amount of sigma phase after quenching with quenching rate of -140°C/min from respective annealing temperature to room temperature. Heat Temperature °C/20MIN Amount σ phase 605123 1150 <1% 605125 1100 50% 605127 1000 <1% 631928 1100 30% 631930 1050 <1% 631931 1150 25% 631933 1150 <1% 631934 1100 40% 631936 1150 <1% 631937 1100 <1% 631945 1100 20% From Table 2 it becomes evident that material which fulfills two of three of the following conditions shows a bigger tendency to form sigma phase during cooling. The three conditions are: * High content of Cr * High content of Mo * Low content of N. The strength and impact toughness were determined for all heats. Static tensile test specimens were produced from extruded rods, which were solution heat treated at temperatures according to Table 2. The results of the investigations are shown in Tables 3 and 4. Table 3: Mechanical properties, rupture strength at room temperature (RT), 100°C and 200°C. Heat Temperature Rp0.2 Rpl .O Rm A5 Z (MPA) (MPa) (%) (%) 605123 RT 749 833 926 36.1 100°C 635 707 843 39.2 61 200°C 558 624 804 36.3 57 605125 RT 667 769 901 36.8 100°C 570 653 816 37.8 72 200°C 503 566 763 32.9 70 605127 RT 586 678 832 39.1 100°C 474 565 750 40 71 200°C 401 473 688 38 70 631928 RT 841 924 994 33.5 100°C 692 783 897 36.6 63 200°C 622 698 856 33.4 59 631930 RT 722 827 943 31 100°C 611 697 850 34.5 53 200°C 538 606 791 30.7 51 631931 RT 749 848 938 32.1 100°C 668 734 859 33.3 67 200°C 583 640 796 29.4 63 631933 RT 740 825 919 36.2 100°C 610 694 833 38.1 64 200°C 558 618 792 36.2 59 631634 RT 666 783 900 35.4 100°C 577 672 826 35.8 72 200°C 502 577 763 32.6 67 631936 RT 695 776 883 39.1 100°C 581 651 801 41.9 66 200°C 512 573 767 39 59 631637 RT 608 705 837 38.4 100°C 507 592 756 39.8 72 200°C 431 501 701 37.2 69 631945 RT 747 841 942 37.1 5 100°C 608 714 855 38.1 68 200°C 562 629 807 34.2 65 Results of the rupture strength tests show, that contents of Cr, Mo and N strongly influence the rupture strength of the material. 0 Table 4: Mechanical properties, impact toughness at room temperature (RT) and -46°C as average of 3 tests. Heat Temperature Impact toughness (J) 5 605123 RT 33 -46°C 5 605125 RT 232 -46°C 237 Λ0 605127 RT 196 -46°C 190 631928 RT 59 5 -46°C 10 631930 RT 36 -46°C 17 631931 RT 180 -46°C 125 631933 RT 50 -46°C 6 631634 RT 224 -46°C 238 631936 RT 47 -46°C 6 631637 RT 250 -46°C 253 631945 RT 206 -46°C 112 It becomes evident that the heats can be divided into in two categories; those with high impact toughness, which have impact toughness above 180 J and those, which are considerable more brittle with impact toughness around or under 60 J. It shows that the impact toughness is much strongly correlated to the chemical composition in the austenite phase, particularly to the content of nitrogen and chromium are of importance. It shows during the continued studies that high N-contents in the austenite result in brittle fractures. The pitting corrosion properties were partly tested by electro-chemical testing in 3 % NaCI and synthetic seawater (6 tests per heat) and partly testing according to ASTM G48C (2 tests per heat). The results from all tests are shown in Table 5. Table 5: CPT for the various heats in degrees Celsius and PRE-number for the total composition of the alloy. Heat PRE CPT °C CPT °C CPT °C (Cr+3.3MO+16N) (3% NaCI) (Synthetic sea-water ASTM G48C ASTM B1 141 ) 605123 49.5 35 45 40 605125 45.3 79 77 78 605127 37.9 66 62 50 631928 52.2 65 67.5 50 631930 46.7 59 63 40 631931 41.8 54 52.5 40 631933 48.9 43 49 40 631934 45.1 62.5 76 80 631936 44.2 32.5 34 40 631937 39.1 61 58 40 631945 50.4 81 82.5 78 The heats 605125, 631934 and 631945 have surprisingly high CPT both at tests according to G48 and electrochemical. These heats have all relatively high PRE-numbers (>45). That there exists a correlation between PRE and CPT is apparent as well as that the PRE-number for the composition of the heat not solely explains CPT. Example 2: In the following example the composition of a number of experimental heats is indicated, which are included in order to illustrate the influence of different alloying elements on the properties. Nine experimental heats were produced by casting of 170 kg ingots, which were hot forged into round bars. Those were hot extruded into rods, from which the test material was taken out. The composition of these nine heats is based on the compositions from EXAMPLE 1 . Table 6 shows the composition for these experimental heats. Table 6: Composition for experimental heats, weight-% Heat Cr Ni Mo Mn N C 605160 31.74 8.1 1 3.50 1.05 0.44 0.012 605161 31.85 7.25 3.47 0.90 0.50 0.014 605162 31.8 7.27 2.98 0.86 0.5 0.012 605164 31.86 7.36 3.95 0.86 0.498 0.012 605165 31.0 6.94 3.98 1 .05 0.49 0.012 605166 30.90 6.10 3.95 0.95 0.544 0.012 605168 32.77 7.88 2.96 1.00 0.502 0.014 605169 32.93 6.96 3.00 0.92 0.542 0.016 The six first heats in Table 6 are variants of heat 631945 in example 1 , the following two heats are variants of heat 631928 in example 1 , and the last is a variant of heat 631931 in example 1 . Distribution of the alloying elements in the ferrite and austenite phases was examined with micro probe analysis, results hereof appear from Table 7. Table 7: Alloying elements in ferrite respective austenite phase. Heat Phase Si Cr Mn Ni Mo N 605160 Aust 0.01 30.1 1.18 9.9 3 0.8 Ferrite 0.05 33.1 1.06 6.4 4.6 0.08 605161 Aust 0 30.4 0.95 8.5 2.9 0.89 Ferrite 0 32.6 0.84 5.6 4.5 0.1 605164 Aust 0 30.4 0.91 8.6 3.3 0.87 Ferrite 0 32.5 0.81 5.8 5.2 0.08 605162 Aust 0 30.2 1 .04 8.4 2.5 0.85 Ferrite 0 32.8 0.92 5.5 3.9 0.08 605165 Aust 0.02 29.2 1.14 8.1 3.3 0.87 Ferrite 0.06 31 1.02 5.4 5.1 0.07 605166 Aust 0 29.3 1 .04 7.2 3.1 0.89 Ferrite 0 30.3 0.92 4.9 4.7 0.05 605168 Aust 0 30.3 1 .1 1 9.3 2.4 0.83 Ferrite 0 32.9 0.99 6.2 3.6 0.06 605169 Aust 0 30.6 0.99 8.2 2.4 0.89 Ferrite 0 32.6 0.87 5.5 3.7 0.06 In order to examine the structural stability of the experimental heats in this example, test specimens were annealed during 20 min at 1025°C, 1050°C, 1075°C, 1 100°C and 1 125°C, thereafter they were quenched in water. The temperature, where the amount of intermetallic phase became insignificantly small was determined with the help of investigations in a light-optical microscope. The test specimens for the investigation of the structural stability were annealed in a vacuum furnace at respective temperature during three minutes, whereafter they were quenched with a rate of - 140°C/min to room temperature. The amount of sigma phase in this material was determined by point counting using a light-optical microscope. The results are shown in Table 8. Table 8: Amount of sigma phase after quenching from respective annealing temperature to room temperature. Heat Temperature °C Amount σ phase 605160 1 100 10% 605161 1 100 <1 % 605162 1075 <1 % 605164 1 100 5% 605165 1100 <1% 605166 1075 <1% 605168 1100 5% 605169 1075 <1% It appears from Table 8 that the optimized composition of the materials diminishes or wholly eliminated the amount of precipitated sigma phase. The Table 8 values lie substantially under the values in example 1 (Table 2). Consequently, these heats have a more optimal composition. The strength and the impact toughness have been determined for all heats in Table 6. Static tensile test specimens were produced from extruded rods, which were heat-treated at temperatures according to Table 8. The results of the tests are shown in Tables 9 and 10. Table 9: Mechanical properties, tensile strength at room temperature. Heat Rp0.2 Rpl.O Rm A5 Z (MPA) (MPa) (MPa) (%) (%) 605160 757 851 975 35 66 605161 761 854 977 35 63 605162 743 830 962 37 64 605164 776 875 978 34 62 605165 771 847 959 34 62 605166 789 869 964 34 58 605168 800 872 962 36 67 605169 809 886 976 34 60 Results of tensile strength tests in example 1 and 2 (Tables 3 and 9) show that the contents of Cr, Mo and N strongly influence the tensile strength in the material. It shows that the mutual influence of the contents of these alloying elements on the tensile strength remains as (0.93 % Cr)+% Mo+(4.5 % N), see Fig. 1 . In order to obtain a tensile strength above 760 MPa following should be valid (0.93 % Cr)+% Mo+(4.5 % N)>35. Table 10: Mechanical properties, impact toughness at room temperature (RT) and -46°C average of 3 tests. Heat Impact toughness (J) (RT) (-46°C) 605160 234 197 605161 198 70 605162 216 100 605164 146 48 605165 218 56 605166 68 19 605168 201 51 605169 72 25 The impact toughness tests in example 1 and 2 (Table 4 and 10) show that the impact toughness strongly depends on the contents of N and Cr in the austenite phase. This relationship is distinct in Fig. 2a-2b. A transition to a more brittle fraction occurs at Cr-contents above 31 % and N-contents above 0.9%, preferably 0.8%. The pitting corrosion properties were investigated by determining the Critical Pitting Corrosion Temperature (CPT) according to ASTM G48C (2 tests per heat) The results appear from Table 1 1 In addition, in Table 1 1 the PRE- numbers for the ferrite respective austenite phase is given, the contents have been obtained by micro probe analysis In this connection the PRE-number is defined as PRE=%Cr+3 3%Mo+16%N Table 1 1 . CPT for the various heats in degrees Celsius and PRE-number for the total composition of the alloy Heat PRE CPT °C (Ferrite) (Austenite) (ASTM G48) 605160 49.6 52.8 75 605161 491 543 80 605162 47.0 521 70 605164 50.9 55.2 88 605165 490 54.0 80 605166 46.6 53.8 60 605168 45.7 51.5 65 605169 458 52.8 53 It is previously known that a linear relationship between that lowest of the PRE-numbers for the austenite or ferrite in a given alloy, and the CPT- value, exists for duplex steels of medium alloy content Consequently, the lowest alloyed phase limits the resistance to pitting corrosion In this investigation it is confirmed that this relationship even exists in those considerably higher alloyed materials This is further illustrated in Fig 3, which shows the measured CPT-values in relation to the calculated PRE-numbers from the ferrite phase, which is the weaker phase in this example. Tests with TIG-remelting were carried out on all heats. Weldability and microstructure have been studied. The results are presented in Table 12. Table 12: Result of tests with TIG-remelting. Heat Precipitations 605160 Small amounts 605161 Small amounts 605162 Small amounts 605164 Small amounts 605165 Small amounts 605166 Cr 2 N 605168 Cr 2 N 605169 Cr 2 N It appears from the above investigation that the weldability of the material is strongly dependent on the N-content. It is possible to find a maximum N-content for this type of alloy. By comparison of the heats 605165 and 605166 it is obvious that the N-content should preferably not exceed 0.5 %. Optimum composition of a preferred embodiment of the present invention: In order to obtain high strength and good impact toughness properties, at the same time as the material is structural stable, weldable and has good corrosion properties, the material should be alloyed according to the following: - Nitrogen-content in the austenite measured with for example micro probe should not exceed 0.9%, preferably 0,8%. - Chromium-content in the austenite phase measured with, for example, a micro probe should not exceed 31 .0%, preferably 30.5%. - Total nitrogen content of the alloy should not exceed 0.50 %. - Chromium, molybdenum and nitrogen should be added so that the relationship 35<0.93Cr+Mo+4.5N is fulfilled - The PRE-number is preferably 45.7 - 50.9 in the ferrite phase. The PRE-number is preferably 51 .5 - 55.2 in the austenite phase. -The ferrite-content should lie in the range of 35-55%, by volume. Example 3 The following example shows the influence of an increased content of Si on the stability of the sigma phase for the alloy. Thermodynamic calculations comparing a test heat and a full scale produced material, where the full scale heat 451260 resulted in an increased content of Si (see Table 13), show reduced sensitivity to precipitation of intermetallic phase, preferably sigma phase. This is illustrated of the lower temperature Tmaxσ in Table 14 for the fullscale-produced alloy 451260 compared with the test heat 605161. Tmaxσ is the temperature, where the sigma phase starts to precipitate at thermodynamic equilibrium, which means that this parameter is a dimension for the structural stability of the alloy. Table 13: Chemical composition for the compared heats. Heat Cr Ni Mo N Mn Si C 451260 31 .71 7.26 3.45 0.47 0.97 0.20 0.01 1 605161 31 .85 7.25 3.47 0.5 0.9 0.05 0.014 Table 14: Tmaxσ for the compared heats. Heat Tmaxσ [°C] 451260 993 605161 1006 Further thermodynamic studies for the composition according to Table 13 for the full scale heat 451260 confirm that an increased content of Si favors the structural stability for the steel. For these calculations the content of Si was varied between 0 and 2.5% and the solution temperature, i.e. Tmaxσ for the sigma phase, was calculated. According to Figure 4, it appears that the stability of the sigma phase diminishes with increasing Si-content in the range between 0-1.7%. At this content, a minimum of the stability of the sigma phase was found and the stability increases afterwards with increasing Si-content. Experimental investigation on full-scale produced, and test heat materials, confirms the theoretical calculations. Heat treatment tests were carried out with the same technique described in examples 1 and 2. The microstructure was made visible by grinding, polishing and etching, and the amount of sigma phase was measured in accordance with that described in examples 1 and 2. The measured contents of sigma phase show that the quenching rates from -120° C/ min and lower give a quick increasing content of sigma phase, while quenching rates from -160°C/ min and higher give a marginal influence on the content of sigma phase (see Table 15). Comparable results from test heat 605161 show that the amount of sigma phase for the same solution and quenching conditions is significantly higher, see Table 15. This confirms that the fullscale produced material shows a significantly better structural stability, compared with the test heat material. By way of thermodynamic calculation this can be related to the higher content of Si in the fullscale material. Table 15: Content of sigma phase as a feature of the solution treatment/quenching rate. Heat 90° C/ min 120° C/ min 140° C/ min 160° C/min 180° C/ min 451260 0.754% 0.227% 0.183% 0.079% 0.087% 605161 10 % 5 % < 1 % Thus, for the purpose of obtaining a more structurally stable material as well as to promote the weldability of the alloy, Si can advantageously be added to the material. However, the content should not exceed 2.0 %. While the present invention has been described by reference to the above-mentioned embodiments, certain modifications and variations will be evident to those of ordinary skill in the art. Therefore, the present invention is to limited only by the scope and spirit of the appended claims.

Claims: What is claimed is: 1 . A duplex stainless steel alloy having ferrite-austenite microstructure exhibiting, when hot extruded and having an annealed finish, shows good weldability, high strength as well as good and high resistance to tensile corrosion, wherein the alloy comprises, in weight-%: C max 0.05%; Si 0-2.0%; Mn 0-3.0%; Cr 25-35%; Ni 4-10 %; Mo 2-6 %; N 0.3-0.6 %; and Fe and normally occurring impurities and additions wherein the ferrite content is 30-70 % by volume. 2. The alloy of claim 1 , further comprising 0 - 2.0 % Si. 3. The alloy of claim 1 , further comprising max 0.03 % C. 4. The alloy of claim 3, further comprising max 0.02 % C. 5. The alloy of claim 1 , wherein the content of ferrite is between 35-55 % 6. The alloy of claim 1 , further comprising 0.5 - 1.5% Mn. 7. The alloy of claim 4, further comprising 29 - 35% Cr. 8. The alloy of claim 6, further comprising 5 - 9% Ni. 9. The alloy of claim 7, further comprising 3 - 5% Mo. 10. The alloy of claim 8, further comprising 0.45 - 0.55% N. 1 1 . The alloy of claim 1 , wherein the relative amounts of the constituent alloying elements are such that (0.93 % Cr)+% Mo+(4.5 % N)≥35. 12. The alloy of claim 1 , wherein the relative amounts of the constituent alloying elements are such that a PRE number, defined as %Cr+3.3%Mo+16%N, in the ferrite phase is 45.7 - 50.9, and the PRE-number in the austenite phase is 51.5 -55.2. 13. The alloy of claim 1 1 , wherein the alloy, when hot extruded and having an annealed finish, shows a yield point limit in tension of above 760 MPa. 14. The alloy of claim 1 1 , wherein the content of N in the austenite phase does not exceed 0.9%, preferably 0.8%. 15. The alloy of claim 1 1 , wherein the content of Cr in austenite phase does not exceed 30.5% 16. The alloy of claim 1 1 , wherein the total content of N does not exceed 0.50% 17. An extruded seamless tube formed from the alloy of claim 1 , the tube having a yield point in tension, which exceeds 760 MPa. 18. An umbilical tube formed form the alloy of claim 1 . 19. An article possessing resistance against corrosion in sea water formed from the alloy of claim 1. 20. An article having high strength and good corrosion resistance, the article formed from the alloy of claim 1 , the article being in the form of a seamless tube, a welding wire, a seam-welded tube, a strip, a wire, a rod, a sheet, a flange or a coupling. 21 . A plurality of butt-welded seamless and seam-welded tubes reeled into a coil formed form the alloy of claim 1.

Inventors: BERGSTROEM OERJAN, CHAI GOUCAI, KANGAS PASI, KLOCKARS MATTIAS, BERGSTROEM, OERJAN, CHAI, GOUCAI, KANGAS, PASI, KLOCKARS, MATTIAS
Applicants: SANDVIK AB
Application year: 2001
Main classification: C22C38
IPC codes: C22C38