BINDER FOR MINERAL WOOL PRODUCTS

Abstract: Process for providing a binder for mineral fibers, comprising the steps of: mixing together under reactive conditions an amine and an anhydride whereby water is added thereto, once substantially all the anhydride is dissolved and/or reacted in the amine.

Description: BINDER FOR MINERAL WOOL PRODUCTS The invention relates to a process for providing a binder for mineral fibers, i.e. man made vitreous fibers, for example glass, slag or stone wool, a binder obtainable via such a process, and a mineral wool product comprising such a binder. Mineral wool products generally comprise mineral fibers bonded together by a cured thermoset polymeric material. One or more streams of molten glass, slag or stone wool are drawn into fibers and blown into a forming chamber where they are deposited as a web on to a travelling conveyer. The fibers, while airborne in the forming chamber and while still hot are sprayed with a binder. The coated fibrous web is then transported from the chamber to a curing oven where heated air is blown through the mat to cure the binder and rigidly bond the mineral wool fibers together. During the curing step when hot air is blown through the mat to cure the binder, a binder as disclosed in WO 99/36368 can be displaced within the mineral wool fibers, whereby a non-uniform distribution of the binder results, specifically wherein less binder is to be found at the bottom of the mineral fiber blocks (i.e. the side of the block where the hot air is blown into the product) than in the top thereof . Also during curing, a large amount of the resin may be lost leading to undesirably high emissions and a high binder loss . An object of the present invention is to improve on this situation. According to a first aspect there is provided a process for providing a binder for mineral fibers, comprising the steps of mixing together under reaction conditions, an amine and an anhydride, whereby water is added thereto only after the anhydride has substantially dissolved in and/or reacted with the amine, and the reaction is thus terminated. A second anhydride is preferably added to the reaction mixture whereby the water is preferably added to the reaction mixture immediately before or together with the second anhydride, or when substantially all of the second anhydride is dissolved in and/or reacted with the mixture of the first anhydride and the amine. Water is most preferably added to the reaction mixture in an amount to make this easily pumpable. Low viscous resin binders for mineral wool are known, wherein the usual procedure is to mix diethanolamine with water before adding any anhydride to minimize viscosity/stirring problems and to obtain the desired water solubility. These resins however contain a high amount of rest monomers, i.e. unreacted starting material, and have the disadvantages of providing a low molecular weight binder which has a long curing time. In order to overcome these extensive curing times, it is often necessary to use a high curing temperature with the accompanying problem that the high curing temperature and long curing time cause extensive evaporation of the binder and non-uniform binder distribution. A binder so obtained, yields a high binder loss, high emission and curing problems. By utilizing a process according to the present invention, a binder is provided for bonding mineral wool products, wherein the amount of rest monomers, i.e. unreacted start material is reduced, and having a higher average molecular weight, whilst still maintaining water solubility. Furthermore, the inventors have shown that utilizing the process according to the present invention, the amount of emissions can be reduced, the binder yield can be raised, the curing time can be shortened, whilst the product quality can be improved. It is theorized that the monomers also take part in the binder cross-linking reaction during curing, but if this amount is too high and the curing time is too long, most of the monomers evaporate. The inventors have shown that providing the binder without water addition from the start of the reaction, reduces the amount of unreacted monomers and increases the curing speed yielding a binder having a higher average molecular weight . Furthermore, the inventors have shown that the binder loss during curing is less because of the presence of less unreacted monomers, whereby a rapid viscosity increase is provided due to the shorter curing time and the higher initial Mw. This rapid viscosity increase makes it difficult for the monomers to evaporate from the reaction mixture instead having time to react as a binder component and take part in the cross-linking reaction. Furthermore, due to the increased viscosity of the binder obtainable by the process of the present invention, there is less displacement of the binder in the mineral wool, when the binder has been applied to the mineral wool and curing is taking place. In an embodiment, the amine is heated firstly to a temperature of at least 40, preferably at least 50 and most preferably to about 60 °C whereafter the first anhydride is added, and the reaction temperature then is raised to at least 70, preferably at least about 80 and most preferably to at least about 95 °C at which temperature the second anhydride can be added to the reaction mixture when substantially all the first anhydride has dissolved and/or reacted. Alternatively increasing the reaction temperature from 90-95 °C to 100-200 °C gives a higher conversion of monomers to oligomers. A preferred temperature range is 120-170 °C, and most preferred is 130-150 °C. The temperature is at least 100°, often at least 120°, and preferably about 130 °C. It is normally below 200°, and preferably below 170°, more preferably below about 150 °C. The average molecular weight of oligomers is increased when the reaction temperature is raised. The evaporation loss of binder made of resin reacted at higher temperature is lower when cured. A binder produced under these circumstances wherein water is added when the first anhydride has reacted, together with the second anhydride or at the end of the reaction, in an amount to make the binder easily pumpable, enables a binder with an increased average molecular weight to be provided but still having a desired pumpability, viscosity, and water dilutability. A resin according to the present invention but made with water addition from the start has more than 50% unreacted monomers of diethanolamine and polycarboxylic acids (anhydrides reacted with water) , less than 15% amide of' complete amide formation and an average molecular weight of about 400 and a maximum of about 600. A resin made according to the process of the present invention with water addition at the end, together with a second anhydride, or just before the second anhydride has been added, has less unreacted monomers, especially the polycarboxylic acids, less than 30% compared with water addition from the start, a higher amount of amides, 15% or more of complete amide formation, and an average molecular weight of 500-900 and a maximum of about 2000. The first and second anhydrides, and the amine are also described in claims 7-11. The reaction mixture used as a binder can also comprise an accelerator, a resin additive, a corrosion inhibitor to curb the effect on pipes and the like, and/or a cross-linking agent as described in claims 13- 19. Further characteristics of the process are to be found in claims 20-28. The inventors have shown that the aged strength of the binder mixture can be improved by the addition of silane. The amount of silane in the resin reaction mixture is at least 0.1 %, often at least 0.2% and preferably at least about 1%. It is normally below 5% and preferably below 3% and is often about 1.5%. In order to improve the water solubility of the binder a base might be added upto a pH of about 8 , whereby a pH of between about 6-8 is preferred, more preferred being a pH of about 7. The base can be mixed with a polyacrylic acid and added to the resin after the resin reaction is stopped by water addition. The base thus need first be added after the resin is prepared. The base may be mixed with a carboxylic acid group containing polymer before addition. Suitable bases could be NH 3 , DEA, TEA, or alkali hydroxides. It is found that addition of one or more cross- linking agents with a carboxylic acid group containing polymer increases the curing speed of the binder. The first and second anhydrides are chosen to provide reaction products with a large number of unreacted polycarboxylic acid groups, which is preferable for water solubility. A most preferred binder consists of 30% polymer of DEA (diethanolamine) , THPA (tetrahydrophthalic anhydride) and TMA (trimellitic anhydride) , 15% DEA monomer, 10% THPA monomer reacted with water to diacid, 5% TMA monomer reacted with water to triacid and 40% water. In the polymer preferably about 50% of the reacted DEA has reacted to an amide and the other 50% of the reacted DEA has reacted to an ester. Another preferred binder consists of about 40% or more polymer, (DEA, THPA, TMA) , about 10% or less DEA monomer, about 10% or less THPA monomer and TMA monomer reacted with water to diacid, triacid respectively and 40% water. The invention will now be further clarified by way of the following examples and reference to table 1, wherein a plurality of resin formulations is shown. Resin formulations were made (see tables 1, 2 and 3) . Key to abbreviations in tables : DEA - diethanolamine GLA - glutaric anhydride SCA - succinic anhydride TMA - trimellitic anhydride ADP - adipic acid THPA - tetrahydrophthalic anhydride Base - ammonia, amines or inorganic hydroxides PAA - polyacrylic acid Silan - amino silanes as par example gamma- aminopropyltriethoxysilane (prehydrolysed VS 142 from Witco or not hydrolysed A 1100 from Witco or similar from other producers) PTA - phthalic anhydride Table 1 [ Continued ] co c co co m co I m m 7 ci m ro Table 2 [ Continued ] co c 00 CO m co I m m 7} c m ro Formulation 22 and 23 were prepared as follows: Formulation 22 Resin: 116 kg DEA was transferred to a 400 1 reactor and heated to 60°C whilst stirring. 16.3 kg ADP was added, and the mixture heated and reacted at 130°C for 60 minutes. Thereafter cooled to 85°C and 33.8 kg of THPA was added. Thereafter 82.5 kg PTA was added and the temperature raised to 130°C for 120 minutes. Subsequently the reaction mixture was cooled to 110°C and 100 kg water added. The temperature stabilised at approx. 50°C. The mixture was stirred for a further 15 minutes until homogenous . The resin was cooled and transferred to a storage tank. The resin solids content was determined as 62.2% at 200°C. Rest monomers: 39% of added DEA, 12% of added THPA, 25% of added PTA. Average molweight about 600. The amount of rest monomers was determined by taking seperate samples of the resin for each component. The samples were heated to 200° c in order to remove all water, and then measured. Before use 4% DEA and 25% solids Acumer 1510 calculated on resin solids, 0.4% of sum solids silane and water to 25% solids content, was added. Results of trial Binder yield 60% Delamination strength (EN 1607) 13.4 kPa (Terraenbatts Industri) - Aged 3.6 kPa (70°C/95%RH) Tensile strength 5.5 kPa (Flexi A Batts) Formulation 23 Resin 24 kg DEA was transferred to a 80 1 reactor and heated to 60 °C and stirred. 6.7 kg ADP was added and the mixture heated and reacted at 130°C for 60 minutes. Thereafter cooled to 85°C and 6.9 kg of THPA was added. Thereafter 16.9 kg PTA was added and the temperature raised to 130°C for 120 minutes. Subsequently the reaction mixture was cooled to 110°C and 20.5 kg water added. The temperature stabilised at approx. 50°C. The mixture was stirred for further 15 minutes until homogenous. The resin was cooled and transferred to a storage tank. The resin solids content of 63.4% was determined at 200°C. Rest monomers: 37% of added DEA, 14% of added THPA, 25% of added PTA. Average molweight about 600. The amount of rest monomers was determined by taking out seperate samples of the resin for determination of each component. The samples were heated to 200 °C in order to remove all water, and then measured. Before use 4% DEA and 25% solids Acumer 1510 calculated on resin solids, 0.4% of sum solids silane and water to 25% solids content, was added and analysed. Results of trial Binder yield 70% Delamination strength (EN 1607) 12.1 kPa (Terrsnbatts Industri) - Aged 4.3 kPa (70°C/95%RH) A number of these formulations were investigated for molecular weight and curing time at 250 °C, the results being as follows: Molecular weight analysis of the polymeric part or moiety Formulation: 1) DEA: THPA - water added from start - average Mw 400 - maximum 600 3) DEA: THPA - water added at the end - average Mw 850 - maximum 2000 4) DEA: THPA: TMA - water added from start - average Mw 400 - maximum 600 5) DEA: THPA: TMA - water added from the start - average Mw 500 - maximum 1500 9) DEA: THPA: TMA - water added with TMA - average Mw 500 - maximum 1500 20.3 kg DEA is heated to 60 °C, whereafter 17.7 kg THPA is added during stirring. The temperature is raised to 95 °C and reaction continued for 1 hour, whereafter 25.8 kg water and 11.2 kg TMA are added and right after 11.2 kg TMA is added. Temperature is held at 95 °C for %. hour before the reaction is stopped by cooling to room temperature. Composition of resin: 15% DEA monomer 10% THPA monomer reacted to acid 5% TMA monomer reacted to acid 40% Water Rest 30% is polymer of DEA:THPA:TMA 16) DEA: THPA:SCA - water at the end - average Mw 550 - maximum 1100 Curing time at 250 °C DEA: THPA: TMA or PTA - curing time about 2 minutes, formulation 9) and 12) , table 1; DEA: THP :SCA - curing time about 1 minute, formulation 16) , table 1; DEA: THPA: TMA or PTA added 20% polyacrylic acid - curing time 25-40 seconds, formulation 9) and 12) , table 1; DEA:THPA:SCA added 20% polyacrylic acid - curing time 20 seconds, formulation 16), table 1. The curing time was measured by preheating a droplet of binder placed on a thin glass plate during 45 minutes at 90 °C after which it was heated to 250 °C by placing the glass plate on a heating plate and stirred with a thin needle. The time until the binder droplet was cured was measured after placing on said heating plate. The test method was repeated. Two more droplets of the same binder were tested using the same method. Factory trials utilizing the binder according to the present invention on a mineral wool Marine Slab 100 was carried out as follows. Binder formulations were made based on selected resins to which 20% w/w polyacrylic acid was added as a cross-linking agent and 0.2% w/w silane as a coupling agent was added. Curing was carried out at 250 °C. The delaminating strength was measured according to EN 1607, whereby ageing is defined as remaining delaminating strength after treatment 15 minutes in an autoclave with 120 °C (1 ato) . Results Formulation 16, DEA:THPA:SCA - water at the end. Delamination strength 9 kPa - remaining strength after ageing 25% - binder yield 75% Binder distribution top - bottom is OK Formulation 9, DEA:THPA:TMA - water added during TMA addition. Delaminating strength 10 kPa - remaining strength after ageing 68% - binder yield 80% Binder distribution top - bottom is OK Formulation 13, DEA:THPA: PTA - water at the end. Delaminating strength 10 kPa - remaining strength after ageing 52% - binder yield 65% Less binder in bottom than top Reference formulation 1 DEA:THPA - water added from start . Delamination strength 7 kPa - remaining strength after ageing 40% - binder yield < 50% Almost no binder in the 1/3 bottom part which is cut away before delamination measurements. Example: Reaction temperature at 130 °C compared with 95 °C (see Table 2) Formulation 9) reaction temperature 95°C. Molratio DEA:THPA:TMA = 1 : 0.6 : 0.3, coupling agent 0.4% VS 142 of binder solids. Rest monomers: 55% of added DEA, rest monomers 40% of added anhydrides . Average molecular weight of oligomers 500. Evaporation loss of binder solids in factory trial 25-30% Product quality: Delamination strength (EN 1607) 10 kPa, remaining strength after ageing 6.8 kPa Product quality when using phosphonic acid as curing accelerator Delaminating strength (EN 1607) 12.9 kPa, remaining strength after ageing 7.6 kPa. Formulations 17-20 reaction temperature 130°C. Molratio as formulation 9) DEA:THPA:TMA = 1:0.6:0.3 90 kg DEA was heated to 60°C whereafter 40 kg THPA was added during stirring. The temperature was raised to 95°C whereafter the exothermic reaction continued to raise the temperature to 115°C. A Further 38.5 kg THPA was added and the temperature allowed to rise to 130°C and maintained for 10 minutes before 49.6 kg TMA was added. The temperature was held at 130°C for 60 minutes and then cooled to approximately 50 °C by the addition of 120 1 of water. The reaction mixture was kept at this temperature for 60 minutes until all TMA was dissolved. Rest monomers: 39% DEA of added, rest monomer 18% of added anhydrides . Average molecular weight of oligomers 600. Before further dilution with water a base is added until a pH of about 6-8, preferably 7 results. The base may be an alkalihydroxide, amine or ammoniumhydroxide . In these formulations ammoniumhydroxide was used. Evaporation loss of binder solids was between 15 and 17%. Before use an accelerator/crosslinker, a silane and water was added to 25% solids content. Product quality when using 3% of solids phosphonic acid as curing accelerator (formulation 17) Delaminating strength (EN 1607) 15.2 kPa, remaining strength after ageing 9.1 kPa. Product quality when using PAA as curing agent (Rohm and Haas Acumer 1510) , (formulation 20) . Delamination strength (EN 1607) 11.2 kPa, remaining strength after ageing 4.5 kPa. High silane addition as described in the example above. Silane results The binder mixture in formulation 17 was used for testing different amounts of silane addition. The binding strength was performed according to the grit bar test. Preparation and testing of selected binder samples to evaluate the binding strength towards shots with mineral fibre composition (Grit bar test) Shots with size between 0.25 and 0.5 mm diameter were used to make bars with dimensions 140 mm x 25 mm x 10 mm. For making the bars 90 ml binder solution with 15% solids content and from 0.2%-3.0% silane coupling agent of binder solids were mixed with 450 g shots. The coupling agent was gamma- aminopropyltriethoxysilane . To some of the binder solutions were added NaH 2 P0 2 -H 2 0 (3% of binder solids) as curing accelerator. Out of the 450 g shots mixed with binder solution can be made 8 bars which is cured 2 hours at 200 °C in an incubator. Four of the bars were broken directly (dry strength), the other 4 are placed 3 hours in 80 °C water before they are broken (wet strength) . The binding strength was determined by breaking the bars in a measuring device, where the clamping length is 100 mm and the velocity of the compressing beam was 10 mm/min. Using the clamping length, width and thickness of the bars, the bending strength was determined in N/mm 2 . Grit bar test results: Bending strength Dry N/mm 2 Wet N/mm 2 0.2% silane 9 4 0.4% silane 9 4 0.6% silane 9 5 1.0% silane 9 7 1.2% silane 9 8 3.0% silane 9 8 A resin made according to formulation 22 with a mole ratio DEA:ADP = 1 : 0.5, reaction temperature 130°C was mixed with 25% Acumer 1510 solids of resin solids and further added different amounts of silane VS 142. Grit bar tests show: Bending strength Dry N/mm 2 Wet N/mm ; 0, .2% silane 9 3 0. ,4% silane 9 3.5 0. .6% silane 9 5 1, .0% silane 9 7 1. .2% silane 9 8 3. ,0% silane 9 8 The aged (wet) strength is improved by adding higher amounts of silane. (Silan VS 142 as a % of the sum solids) Conclusions based on results: Water addition at the end yielded less unreacted starting monomers, whereby water addition at the end or together with the second anhydride gives higher yield of amides in the resin. See table 1. SCA as second anhydride yielded short curing time and high yield of amides in the reaction product. When the amount amides in the reaction product is too high(>40% of the DEA added) the delamination strength after ageing of the mineral wool products proved to be poor. The preferable mol. ratio DEA to anhydride proved to be 1:0.9-1.2, whereby higher ratios of anhydrides may provide less water soluble resin. Water should be added at the end, immediately before, or together with the second anhydride. The first anhydride is preferably THPA, mol. ratio 0.5 to 1 related to DEA. The preferred second anhydride is TMA or PTA. SCA as second anhydride yielded good strength before ageing, but poor ageing stability. An example of a preferred resin consists of 30% polymer of DEA, THPA and TMA, 15% DEA monomer, 10% THPA monomer reacted with water to diacid, 5% TMA monomer reacted with water to triacid 40% water. An example of another preferable resin consists of about 40% or more polymer of DEA, THPA and TMA, about 10% or less DEA monomer, about 10% or less THPA monomer and TMA monomer reacted with water to diacid, triacid respectively and about 40% water. In the polymer about 50% of the DEA which has reacted to a polymer is preferably an amide and the other 50% has preferably reacted to an ester. The invention is not limited to the above description but is rather determined by the following claims.

Claims: CLAIMS 1. Process for providing a binder for mineral fibers, comprising the steps of: - mixing together under reactive conditions an amine and an anhydride whereby water is added thereto, once substantially all the anhydride is dissolved in and/or reacted with the amine. 2. Process according to claim 1 wherein a second anhydride is added to the reaction mixture. 3. Process according to claims 1 or 2 wherein the water is added to the reaction mixture when the first anhydride has reacted, immediately before or together with the second anhydride, or when substantially all the second anhydride is dissolved in the mixture of the first anhydride and the amine. 4. Process according to any of the preceding claims wherein water is added in an amount to make the reaction mixture easily pumpable at room temperature. 5. Process according to any of the preceding claims wherein the amine is heated firstly to a temperature of at least 40, preferably at least 50 and most preferably to about 60 °C, whereafter the first anhydride is added, and the reaction temperature raised to at least about 70, preferably at least about 95, and most preferably to at least about 120 °C. 6. Process according to claim 5 wherein the reaction temperature is raised to at least about 90°, for example about at least 100°, preferably at least 120°, and more preferably about 130 °C, and is below about 200°, preferably below about 170°, and more preferably below about 150 °C. 7. Process according to claims 5 or 6 wherein the second anhydride is added to the reaction mixture when substantially all the first anhydride is dissolved. 8. Process according to any of the preceding claims wherein the first anhydride is an aliphatic anhydride . 9. Process according to any of the claims 2-8 wherein the second anhydride is an aromatic anhydride. 10. Process according to any of the preceding claims, wherein the first aliphatic anhydride is selected from the group comprising tetrahydrophthalic anhydride, and/or hexahydrophthalic anhydride, methyltetrahydrophthalic anhydride, succinic anhydride, nadic anhydride, maleic anhydride, glutaric anhydride. 11. Process according to any of the preceding claim 2-10 wherein the second aromatic anhydride is selected from the group comprising phthalic anhydride, trimellitic anhydride, pyromellitic di-anhydride and methylphthalic anhydride. 12. Process according to any of the preceding claims wherein the amine, being a N-substituted beta hydroxy alkylamine, is selected from the group Di- ethanolamine, 1- (m) ethyldiethanolamine, n-butyl- diethanolamine, 1- (m) ethylisopropanolamine, 3-amino-l,2- propanediol, 2-amino-l, 3-propanediol, tris (hydroxymethyl) aminomethane, most preferably diethanolamine . 13. Process according to any of the preceding claims comprising the further step of addition of one or more of the following additives: - an accelerator in order to accelerate curing speed and one or more resin additives such as aminosiloxane to improve adhesion to fibre surface, thermal and UV stabilizers, surface active compounds, fillers such as clay, silicates, magnesium sulfate and pigments such as titanium oxide, hydrophobizing agents such as fluorine compounds, oils, preferably mineral and silicone oils and one or more corrosion inhibitors. 14. Process according to claim 13 , wherein the accelerator is selected from the group comprising the acid or corresponding salts of phosphorous acid, phosphoric acid, phosphonic acid, phosphinic acid, citric acid, adipic acid and β-hydroxyalkylamides . 15. Process according to claim 14 wherein the phosphinic acid has the chemical abstracts number 6303- 12-5-83-P02. 16. Process according to claims 13 or 14, wherein the additives are selected from the group comprising mono-, di-, and polysaccharides, such as sucrose, glucose syrup, modified starch, starch, urea, dicyandiamide, polyglycols, acrylics, furfural, carboxymethyl cellulose and cellulose, and polyvinyl alcohol, melamin. 17. Process according to any of the preceding claims, further comprising addition of a cross-linking agent, wherein the cross-linking agent preferably comprises a carboxylic acid group containing polymer, preferably in the form of polyacrylic acids or polymethacrylic acids. 18. Process according to claim 17 wherein the polycarboxylic acid cross-linking agents are added to the reaction mixture, to be present in the weight percentage range of 5-25 and most preferably being about 20 wt . % . 19. Process according to any of the preceding claims further comprising addition of corrosion inhibitors. 20. Process according to any of the preceding claims, wherein the mole ratio of the amine to the first anhydride lies in the range of 1.0 : 0.1-2.0, preferably 1.0 : 0.5-1.5, and most preferably 1.0 : 0.5-1.0. 21. Process according to claim 20 wherein the amine is diethanolamine, and wherein the first anhydride is tetrahydrophthalic anhydride, and , being present in the mixture at a molar ratio of 1 to 0.5 respectively. 22. Process according to claim 21, wherein the second anhydride is trimellitic anhydride or phthalic anhydride, wherein the second anhydride is present in the mixture at a lower mole ratio than the first anhydride, preferably being present in about half the amount of the first anhydride. 23. Process according to any of the preceding claims, wherein a base is subsequently added to the reaction mixture, following the water addition. 24. Process according to claim 23 wherein the base is selected from the group comprising NH 3 , diethanol amine (DEA) , triethanolamine (TEA) , alkalihydroxides, optionally mixed with a polyacrylic acid, preferably Acumer 1510 Rohm and Haas, Mw. about 60,000. 25. Process according to claim 23 or 24 wherein the base in the resin reaction mixture adjusts the pH upto about 8, preferably to lie in a range of about 6 to about 8 and most preferably adjusts the pH to about 7. 26. Process according to any of the preceding claims wherein an acid is added, preferably before addition of the anhydride and wherein the acid is selected from the group comprising: adipic acid, citric acid, trimellitic acid, sebacic acid, azelaic acid and succinic acid, and is preferably adipic acid. 27. Process according to any of the claims 23- 26, wherein the weight % of the polyacrylic acid in the mixture lies in the range upto 50%, for example 30%, preferably 25% and most preferably upto 20%. 28. Process according to any of the preceding claims further comprising the step of adding a silane, preferably in the range of 0.1%-5%, more preferably 0.2%- 3% and most preferably about 1% by weight of the resin reaction mixture, preferably by weight of the resin solids, whereby the silane is most preferably prehydrolysed gamma-aminopropyltriethoxysilane (VS 142/Vitco) . 29. Binder for mineral fibers, obtainable according to any of the preceding claims 1-28. 30. Binder comprising the reaction product of an amine, a first anhydride, a second anhydride and water and the polymeric part of the binder having a molecular weight of a maximum of about 2000 and preferably having an average molecular weight lying in the range of 300- 1500, preferably 400-1000, and most preferably 500-900. 31. Binder according to claim 30, wherein the first and second anhydrides are those as defined in claims 8-11. 32. Binder according to claims 30 or 31, wherein the amine is selected from those as defined in claim 12. 33. Binder according to any of the claims 30- 32, further comprising a binder additive as defined in any of the claims 13-18. 34. Binder according to any of the claims 29- 33, having a curing time at 250 °C of at the most about 2 minutes, and preferably lying in the range 15-55, for example 20-40 seconds. 35. Use of water to reduce emissions and improve the average molecular weight of a binder for mineral fibers, comprising an amine, a first aliphatic anhydride and a second aromatic anhydride by addition of the water to the reaction mixture once the first anhydride is dissolved in the amine.

Inventors: HANSEN ERLING LENNART, HUSEMOEN THOR, NISSEN POVL, HANSEN, ERLING, LENNART, HUSEMOEN, THOR, NISSEN, POVL
Applicants: HANSEN ERLING LENNART, HUSEMOEN THOR, NISSEN POVL, ROCKWOOL INT, HANSEN, ERLING, LENNART, HUSEMOEN, THOR, NISSEN, POVL, ROCKWOOL INTERNATIONAL A/S
Application year: 2001
Main classification: C03C25
IPC codes: C03C25, C08G69, D06M15