COATED CEMENTED CARBIDE CUTTING TOOL INSERT

Abstract: According to the present invention there is now provided a cemented carbide with a <70 mu m, preferably 10-40 mu m, thick binder phase enriched surface zone containing W and Mo but depleted in cubic carbide. The overall content of Mo in the surface zone is the same as that in the inner portion of the cemented carbide. By alloying the cemented carbide with Mo, the performcance has been improved particularly when used for turing at conditions causing intermittent termal and mechanical load in stainless steel.

Description: Coated cemented carbide cutting tool insert The present invention relates to a coated cemented carbide cutting tool insert. The cemented carbide insert is based on WC, cubic carbides and has a Co-binder phase enriched surface zone. By alloying the cemented carbide with Mo, the performance has been improved particularly when used for turning at conditions causing intermittent thermal and mechanical load in stainless steel. High performance cutting tools have nowadays to possess high wear resistance, high toughness properties and good resistance to plastic deformation. Improved resistance to plastic deformation of a cutting insert can be obtained by decreasing the WC grain size or by lower- ing the overall binder phase content, but such changes simultaneously result in significant loss in toughness properties . Methods to improve the toughness behaviour without loss in plastic deformation by so called gradient-sin- tering techniques are known. The gradient consists of thick essentially cubic carbide free and binder phase enriched surface zones (<50 μm) of the cemented carbide inserts e.g., through US 4,277,283, US 4,610,931, US 4,830,930, US 5,106,674 and US 5,649,279. Such inserts with essentially cubic carbide free and binder phase enriched surface zones are extensively used today for machining of steel and stainless steel. These patents are examples of the importance of the substrate composition within the surface zone for cutting performance. The properties of the insert such as resistance to plastic deformation and toughness behaviour have to be balanced for optimal performance during machining to ensure long and stable tool life. There are also ways to balance the plastic deforma- tion resistance and toughness properties to a certain extent by controlling the composition of the surface zone by employing special sintering techniques or alloying elements, e. g. US 5,484,468, US 5,549,980, US 5,729,823 EP-A-560 212 or EP-A-569 696. The characteristics of all the above-mentioned patents are that the surface zones are essentially cubic carbide free and binder phase enriched i.e. they consist of WC and Co. Such surfaces zones give the insert good edge toughness but makes the insert less sufficient when working conditions are causing thermal and mechanical load to the insert . It is therefore an object of the present invention to provide a cemented carbide insert with improved properties for turning when the temperature and mechanical load is varying without losing resistance to plastic deformation and edge toughness. It has now been found that by adding Mo to cemented carbide inserts with binder phase enriched surface zones unexpected improvements when turning under intermittent thermal and mechanical conditions are obtained. Fig 1 shows the distribution of Ti, Ta, Co, C and Mo in the surface zone of a cemented carbide insert according to the invention Fig 2 shows the distribution of Ti, Ta, Co, C and (Mo) in the surface zone of a cemented carbide insert according to prior art. Fig 3 shows the microstructure of a cemented carbide insert according to the present invention where A - W-core and B - W+Mo rim. According to the present invention there is now provided a cemented carbide with a <70 μm, preferably 10-40 μm, thick binder phase enriched surface zone containing W and Mo but depleted in cubic carbide. The con- tent of Mo in the surface zone is 0.9-1.1 of that in the inner portion of the cemented carbide. The present invention is applicable to cemented carbides with a composition of 5-15, preferably 7-11, weight percent binder phase comprising mainly Co (Fe and Ni only at impurity level), a total amount of 1-10, preferably 4-7, wt-% of cubic carbides such as TiC, TaC, NbC and balance WC . In addition, the cemented carbide contains 0.5-4 wt-%, preferably 0.5-3 wt-%, most pre- ferably 1-2 wt-% Mo. The average WC grain size is 0.5-4 μm, preferably 1-2 μm. The tungsten carbide grains have a duplex structure made up of a core and a surrounding rim. The content of Mo in the rim varies between roughly 2 and 25 wt-%, with the highest amount close to the core. The cobalt binder phase is highly alloyed with W. The content of W in the binder phase can be expressed as the CW-ratio= M s /(wt-% Co • 0.0161) where M s is the measured saturation magnetisation of the cemented carbide and wt-% Co is the weight percentage of Co in the cemented carbide. The CW-ratio is a function of the W content in the Co binder phase. A low CW-ratio corresponds to a high W-content in the binder phase . According to the invention improved cutting performance is achieved if the cemented carbide body has a CW-ratio of 0.72-0.94, preferably 0.76-0.90. The cemented carbide body may contain small amounts, <5 vo- lume-%, of eta phase (MgC) , without any detrimental effect . Cemented carbide inserts are produced by powder metallurgical methods including; milling of a powder mixture forming the hard constituents and the binder phase including a small amount of N, drying, pressing and sintering under vacuum in order to obtain the desired binder phase enrichment. Mo is added as M02C. Cemented carbide inserts according to the invention are preferably coated with a thin wear resistant coating with CVD-, MTCVD or PVD-technique . Preferably, the coating consists of <1 μm TiN, 1-5 μ MTCVD-TiCN, 1-3 μm K- alumina and <1 μm TiN. Example 1 A.) Cemented carbide tool inserts of the type CMMG 120408-MM, an insert for turning, with the composition 7.5 wt-% Co, 3.8 wt-% TaC, 1.9 wt-% TiC, 0.4 wt-% TiN, 0.4 wt-% Mo 2 C and balance WC with an average grain size of 1.7 μ and a CW-ratio of 0.86 were produced by powder metallurgical methods including milling of a powder mixture forming the hard constituents and the binder phase, pressing and sintering. The pressed bodies were sintered at 1450°C according to standard practice. The sintered blanks achieved a cubic carbide free zone reaching roughly 25 μm into the substrate from the surface, Fig 1. The tungsten carbide phase of the produced inserts, consisted of duplex structure made up of a core and a surrounding rim, Fig 3. The content of Mo in the rim varied between roughly 2 and 25 wt-%, with the highest amount close to the core. After conventional precoating treatment like edge honing, cleaning etc. the inserts were coated in a CVD-process giving a 0.4 μm TiN, 2 μm moderate temperature TiCN, 2 μ K-alumina and 0.8 μm TiN. B.) Cemented carbide tool insert of the type CNMG 120408-MM with the composition 7.5 wt-% Co, 3.8 wt-% TaC, 1.9 wt-% TiC and 0.4 wt-% TiN and balance WC with an average grain size of 1.7 μm and a CW-ratio of 0.87 were produced. The inserts were subject to sintering, pre-coating treatment and coating to achieve the same physical properties as A. The sintered blanks achieved a cubic carbide free zone reaching roughly 25 μm into the substrate from the surface. The tungsten carbide phase of the produced inserts had no rim and core structure. C.) Cemented carbide tool inserts of the type CNMG 120408-MM, an insert for turning, with the composition 9.9 wt-% Co, 3.0 wt-% TaC, 2.5 wt-% TiC, 0.3 wt-% TiN, 0.4 wt-% Mo 2 C and balance WC with an average grain size of 1.7 μm and a CW-ratio of 0.78 were produced by powder metallurgical methods including milling of a powder mixture forming the hard constituents and the binder phase, pressing and sintering. The pressed bodies were sintered at 1450°C according to standard practice. The sintered blank achieved a cubic carbide free zone reaching roughly 20 μm into the substrate from the surface. Me- tallographic investigation showed that the hard constituents of the produced inserts consisted of duplex structures made up of a core and a surrounding rim. After conventional precoating treatment like edge honing, cleaning etc. the inserts were, in a CVD-process giving a 4 μm moderate temperature TiCN, 1.5 μm K-alumina, 0.5 μm TiN coating. TiN was after that removed on the edge- lines by brushing. D.) Cemented carbide tool insert of the type CNMG 120408-MM with the composition 10.0 wt-% Co, 6.0 wt-% TaC, 2.6 wt-% TiC and 0.4 wt-% TiN and balance WC with an average grain size of 2.0 μ and a CW-ratio of 0.81 were produced. The inserts were subjected to the same sintering, pre-coating treatment, coating and edgeline brushing as C. The sintered blank achieved a cubic carbide free zone reaching roughly 20 μm into the substrate from the surface. The tungsten carbide phase of the produced inserts had no rim and core structure. Example 2 Insert variants from A and B were tested with respect to edge toughness behaviour when used for turning in stainless steel, AISI316Ti. Cutting data: Cutting speed= 110 m/min Feed= 0.3 mm/rev Depth of cut= 2.0 mm When the maximum wear exceeded 0.3 mm, the test was stopped. Results: cycles Insert A 5 Insert B 3 Example 3 Inserts from A to B were tested with respect to resistance to plastic deformation when used for turning in stainless steel, AISI304L. Cutting data: Cutting speed= 250 m/min Feed= 0.3 mm/rev Depth of cut= 2.0 mm The plastic deformation was measured as flank wear and the test was stopped when reaching 0.3 mm wear. Results: cycles Insert A 13 Insert B 15 Example 4 Inserts from A to B were tested in turning with respect to intermittent thermal and mechanical load in stainless steel, SS2343. Cutting data: Cutting speed= 190 m/min Feed= 0.3 mm/rev Depth of cut= 2.0 mm When the maximum wear exceeded 0.3 mm, the test was stopped. Results : cycles Insert A 5 Insert B 2 Example 5 Inserts from C to D were tested with respect to resistance to plastic deformation when used for turning in stainless steel, AISI304L. Cutting data: Cutting speed= 200 m/min Feed= 0.3 mm/rev Depth of cut= 2.0 mm The plastic deformation was measured as flank wear and the test was stopped when reaching 0.3 mm wear. Results : cycles Insert C 13 Insert D 14 Example 6 Inserts from C to D were tested in turning with respect to intermittent thermal and mechanical load in stainless steel, SS2343. Cutting data: Cutting speed= 190 m/min Feed= 0.3 mm/rev Depth of cut= 2.0 mm When the maximum wear exceeded 0.3 mm, the test was stopped. Results: cycles Insert C 8 Insert D 4

Claims: Claims 1. Coated cutting tool insert consisting of a cemented carbide substrate and a coating said substrate comprising WC, 5-15 wt-% Co, 1-10 wt-% cubic carbides such as TiC, TaC and NbC, with a binder phase enriched surface zone essentially free of gamma phase c h a r a c t e r i s e d in that the substrate contains 0.5-4 wt-% Mo and said surface zone has a Mo-content 0.9-1.1 of that in the inner portion of the substrate. 2. Coated cutting tool insert according to the preceding claim c h a r a c t e r i s e d in that the WC grains have a duplex structure made up of a core and a surrounding rim containing Mo . 3. Coated cutting tool insert according to any of the preceding claims c h a r a c t e r i s e d in that the cobalt binder phase has a CW-ratio of 0.72-0.94 where the CW-ratio is expressed as CW-ratio= M s /(wt-% Co • 0.0161) where M s is the measured saturation magnetisation of the cemented carbide and wt-% Co is the weight percentage of Co in the cemented carbide. 4. Coated cutting tool insert according to any of the preceding claims c h a r a c t e r i s e d in that the coating consists of <1 μm TiN, 1-5 μm MTCVD-TiCN, 1- 3 μm K-alumina and <1 μm TiN.

Inventors: ANDERSSON GUNILLA, LINDHOLM MIKAEL, ANDERSSON, GUNILLA, LINDHOLM, MIKAEL
Applicants: SANDVIK AB
Application year: 2001
Main classification: C23C30
IPC codes: B23B27, C22C29, C23C16, C23C30