ULTRAVIOLET FILTER COATING

Abstract: In accordance with the invention, the disclosed coating system is a two-layered system using a typical ultraviolet absorber in its inner layer (called the blocking layer), furthest away from the source of ultraviolet exposure, with a fluorescent material that reflects ultraviolet radiation back as blue light. The ultraviolet absorber in the inner layer is used in sufficient concentration to have an ultraviolet cutoff, which can be extended with the fluorescent material. The ultraviolet block material of the present invention has transmittance of the light within a range of wavelength of 300-380 nm of 10 % or less, preferably transmittance of the light within a range of wavelength of 300-390 nm of 10 % or less, and, particularly preferably, transmittance of the light within a range of 300-400 nm of 10 % or less, while it has a transmittance of the light within a range of 420-800 nm wavelength of 90 % or more, or preferably, 95 % or more.

Description: TITLE OF INVENTION ULTRAVIOLET FILTER COATING RELATED APPLICATIONS Reference is made to the copending provisional application for Letters Patent, Serial No. 60/220,173, filed in the United States Patent and Trademark Office on My 24, 2000; to the copending application for Letters Patent, Serial No. 09/849,884, filed in the United States Patent and Trademark Office on May 4, 2001; and to the copending application for Letters Patent entitled "ULTRAVIOLET FILTER COATING," Serial No. XX/XXX, XXX, filed in the United States Patent and Trademark Office on July 20, 2001; a claim of priority is hereby made to each of these three applications. The entire contents of each of these three applications are incorporated herein by reference. BACKGROUND OF THE INVENTION Field of the Invention: This invention relates generally to the field of light blocking or light absorbing filters, and more particularly to an improved filter material suitable for blocking harmful ultraviolet rays from artificial light transmitting sources. Discussion of the Background: Ultraviolet radiation is composed of three ranges, namely: UVA, which is from 320 to 400 nanometers (nm), UVB which is from wliich is from 280 to 320 nm, and UVC which is from 100 to 280 nm. UVA and UVB are attenuated by the atmosphere, but it still reaches the earth's surface. UVC is usually blocked by the ozone in the atmosphere. Man-made lighting sources also produce ultraviolet radiation. Most fluorescent lighting has a high output in the UVA range. UVB causes more damage than UVA, but all ultraviolet radiation will cause degradation to materials. Ultraviolet rays from the sun, or from man-made sources, degrade many materials by breaking their molecular bonds. Dyes and inks fade from ultraviolet, plastics lose their properties, paints chalk and fade, and many other items are damaged. Strategies to combat ultraviolet degradation include the use of materials that absorb ultraviolet radiation and convert it to heat energy. Most absorbers have an ultraviolet cutoff of 365 nm. A few have higher cutoffs, up to 384 nm with little to no yellowing. The phenomenon of producing a yellow cast when absorbers are used to block all of the ultraviolet radiation is due to the gradual slope of the absorption curve of the absorbing material. This slope, when the cutoff is extended to 400 nm, causes absorption of violet and blue light. The absence of blue light is perceived as yellow, and it is for this reason that most absorbers, especially in clear overcoatings, are not used to block all of the ultraviolet radiation up to 400 nm. The optical density of a filter, an absorber, or a coating, to a range of radiation, is directly related to the concentration and thickness of the layer. The thinner the layer, the higher the concentration of absorber is required. Very thin coating layers, below 10 microns cannot contain sufficient levels of absorption without a significant loss in the properties of the coating material. As an example, a 4 micron clear coating might require thirty percent, by weight, of an absorber to have complete absorption up to the cutoff wavelength of the absorber. Some common classes of ultraviolet absorbers are benzophenones and benzotriazoles. A coating layer that is effective in blocking ultraviolet and is thin has the additional advantage of lower material cost and a higher degree of possible flexibility. A coating with a low concentration of absorber, so that the physical properties of the coating layer are not diminished, as well as the lower cost of using less absorber, that blocks all ultraviolet up to 400 nm, and does not have a significant effect on blue light absorption would provide a significant improvement in the effort to stop ultraviolet damage to materials. It is known in the art to provide ultraviolet light blocking filters which are in the form of coatable fluids, or laminated sheets of clear synthetic resinous materials which are applied directly to an article to be protected to improve the resistance to fading and other deterioration caused by exposure to daylight, and in particular, sunlight. Radiation in the ultraviolet spectrum, and particularly that in the range of 365 nm and 400 nm, is particularly destructive. However, most widely used filtering materials are effective up to about 365 nm, but are of drastically reduced effectiveness above that value. Many valuable, indeed irreplaceable, objects are exhibited in museums, which for the most part are illuminated by artificial light of both fluorescent and incandescent types. For the most part, such lighting does not provide a serious problem. Such museums are, however, visited by millions of viewers each year, many of whom take their own photographs using electronic flash units which transmit light of a quality having sufficient ultraviolet wavelengths including the above-mentioned upper range. While a single exposure produces negligible amounts of ultraviolet light, where even a small fraction of the visitors photograph the same object, the cumulative effect of such exposure is substantial. As a result, many museums forbid the taking of photographs by visitors altogether. Because electronic flash illumination is normally transmitted through a focusing lens, it has not been heretofore possible to filter this light as a practical matter. SUMMARY OF THE INVENTION General Embodiment 1 : The disclosed coating system blocks ultraviolet radiation up to and including 400 nanometers (nm), the upper end of the ultra violet light. Preventing ultraviolet (UV) radiation from reaching materials and surfaces greatly improves weatherability and resistance to physical degradation from the effects of UV radiation on chemical bonds. There currently exist many types of ultraviolet inhibitors, which are meant to be included in materials to improve their resistance to UV radiation. The damage from UV radiation is greater as the wavelengths of UV become shorter. However, considerable damage still occurs from the longer wavelengths of UV radiation. It is desirable to block the UV radiation and not have yellowing effect. The disclosed coating system remains water white. General Embodiment 2: Briefly stated, the invention contemplates the provision of a novel ultraviolet filter material capable of full ultraviolet wave blockage in a coatable fluid form which may be readily permanently adhered to transparent glass or plastic surfaces, and which will not interfere with the transmission of visible and photoactinic energy. This material is applied preferably to the inner surfaces of electronic photo flash lamps or focusing lenses therefor, and may also be used in the manufacture of any light source in wliich the elimination of ultraviolet light is desirable. Most suitably, the composition is applied in a thickness ranging from five to ten microns using standard application techniques, such as flow coating, spray coating, dipping, curtain coating and the like. It may also be used with a coating thickness of as little as 2 microns, with the use of certain precautions. It is a principal object of the present invention to provide a coating which can be applied to the lens or envelope of a light source, or a window which is transmitting light, that will be water white, and efficiently block ultraviolet emission employing a coating thickness of less than 50 microns, typically less than 10 microns. It is also an object of this invention to block ultraviolet transmission from light sources which typically also emit heat. This aspect is important with regard to any resin system thermally degrading and yellowing or cracking. Sources or lenses covering light sources can be coated with resin systems that are themselves, for the most part, transparent to ultraviolet transmission, and so unaffected by it, and that contain ultraviolet inhibitors or other ultraviolet-reducing materials such as fluorescent materials which will efficiently block ultraviolet transmission. These coatings can be applied to laminating films which can be applied to flat surfaces, or to laminating films which can be thermal formed over curved surfaces. Certain of the disclosed embodiments are not only capable of blocking ultraviolet light, but actually converting at least a portion of the ultraviolet light to visible light, thus increasing the efficiency of light transmission which is particularly useful when the covering is applied to an incandescent or fluorescent light source. This effect is obtained by the incorporation of a fluorescent material in larger quantity as compared to the material used for ultraviolet absorption. General Embodiment 3: The ultraviolet block material of the present invention, has transmittance of the light within a range of wavelength of 300-380 nm of 10% or less, preferably transmittance of the light within a range of wavelength of 300-390 nm of 10% or less, and, particularly preferably, transmittance of the light within a range of 300-400 nm of 10% or less, while it has a transmittance of the light within a range of 420-800 nm wavelength of 90% or more, or, preferably, 95%) or more. Especially when the transmittance of ultraviolet light within a range of 350-380 nm wavelength, preferably 350-390 nm or, particularly preferably, 350-400 nm wavelength is too high, such ultraviolet light decomposes the colorant whereby it is not possible to effectively prevent color fading, discoloration and decolorization. When the transmittance of light within a range of 420-800 nm is too low, the ultraviolet block material is colored or the transparency thereof is lowered disadvantageously. BRIEF DESCRIPTION OF THE DRAWINGS A more complete appreciation of the present invention and many of the attendant advantages thereof will be readily obtained as the same becomes better understood by reference to the following detailed description when considered in connection with the accompanying drawings, wherein: Figure 1(a) is a graph showing relative output of a coated vs. an uncoated 20 watt fluorescent tube according to one embodiment of the present invention; Figure 1(b) illustrates the light transmittance spectra of Examples 1-4 and Comparative Examples 1 and 2; Figure 2 illustrates an example of the ultraviolet block material of the present invention; Figures 3(a) and 3(b) illustrate an example of a method for the protection of a material to be layered, using the ultraviolet block material of the present invention; and Figure 4 illustrates an example where the ultraviolet block layer of the present invention is provided on a color sheet which is used for a thermal transfer printing or the like. In Figures 3(a), 3(b), and 4, element 1 is an ultraviolet block material; element 2 is a substrate; element 3 is an ultraviolet block layer; element 4 is a layer containing a fluorescent material; element 5 is a layer existing between the substrate and the layer containing a fluorescent material; element 6 is a layer existing at the side, opposite to the substrate, of the layer containing the fluorescent material; element 7 is an adhesive layer; element 8 is a material to be layered; element 9 is a side of a material to be layered where the image is formed; element 10 is a color sheet; element Y is a color material layer containing a yellow colorant; element M is a color material layer containing a magenta colorant; element C is a color material layer containing a cyan colorant; and element OC is an ultraviolet block layer of the present invention. DETAILED DESCRIPTION OF THE DISCLOSED EMBODIMENTS General Embodiment 1 : In accordance with the invention, the disclosed coating system is a two-layered system using a typical ultraviolet absorber in its im er layer (called the blocking layer), furthest away from the source of ultraviolet exposure, with a fluorescent material that reflects ultraviolet radiation back as blue light. The ultraviolet absorber in the inner layer is used in sufficient concentration to have an ultraviolet cutoff, which can be extended with the fluorescent material. There are natural fluorescent materials such as calcite, willemite, sprite, fluorite, and diamonds. There are also man-made fluorescent materials used to make materials look whiter by reflecting the long- wave ultraviolet radiation as blue light. These are called optical brighteners. Typical optical brighteners are disulphonates, tetrasulphonates, and hexasulphonates. These are water-soluble optical brighteners. An example of a solvent-soluble optical brightener is Uvitex OB from Ciba- Geigy Corp. Such optical brighteners are typically used in textiles at very low concentrations of less than one percent by weight. Their purpose is to reduce the yellowness of a material, dye, plastic, etc. The present invention provides the desired protection by combimng an optical brightener with an ultraviolet radiation absorber, which raises the cutoff wavelength and increases blue light, rather than absorbing blue light as a longer- wavelength cutoff ultraviolet absorber would normally do. This barrier requires high levels of optical brightener to convert the longer- wavelength ultraviolet radiation into blue light and do this effectively enough to block the transmission from the outer layer to the inner layer due to the total conversion of longer- wavelength ultraviolet to blue light. The high level of optical brightener causes a significant fluorescent effect upon exposure to ultraviolet radiation, where this layer will glow with blue light. The surface of the inner, or blocking, layer also has a significant quantity of fluorescent material, which is not protected in depth by the included ultraviolet absorber. This is the primary reason that the second, or outer, coating layer is effective in reducing fluorescence and why it is necessary. The fluorescent material in the inner layer that lies in the matrix of resin and ultraviolet absorber is then protected from excessive fluorescent excitation. Another technique is to use an alkaline material in the outer coating to decompose the surface of the optical brightener of the blocking layer. Still another technique to reduce surface fluorescence is to use an optical brightener quencher such as OBA Quencher from Kalamazoo Paper Chemicals Corp. While a single blocking layer can be used for protection against ultraviolet, the fluorescent blue glow is generally undesirable. In order to significantly reduce this fluorescence, it is necessary to reduce the amount of ultraviolet that reduces this layer in the peak wavelengths for fluorescence. This is done by applying an overcoating to the blocking layer, which contains some level of ultraviolet absorber that reduces the ultraviolet transmission of the wavelengths that cause fluorescence. It is this combined effect and balance, which completely blocks ultraviolet radiation without yellowing. The outer coating can provide other properties such as chemical resistance, scratch resistance, slip, or friction. The outer coating material can be any resin system with an ultraviolet inhibitor, but it is preferably clear and relatively ultraviolet transparent. Materials that do not absorb ultraviolet on their own are relatively unaffected by exposure to it. For this reason, typical clear outer-coating resins would be aliphatic urethanes, polysiloxanes or acrylics. Fluorescent materials have been used in many applications to "whiten" whites, or brighten colors in many products. The technique is to use the fluorescent material to increase the reflected blue light. The increase in blue light is perceived as a reduction in yellow light from the fluorescent material. It typically takes very small quantities of fluorescent material to accomplish this brightening effect. UV absorbers are widely available and are commonly used with the intention of blocking primarily UVB. When these UV absorbers are used to block all UV light, they increase yellow light perception due to the reduction in blue light. Higher concentrations of fluorescent materials in a single layer coating will cause a blue fluorescent glow to the material when it is exposed to UV light. This is cosmetically objectionable. For this reason, only low concentrations are used for brightening. Blocking UV from reaching the surface of an object is a function of film thickness and concentration. Thin films down to 3-5 microns would require very high concentrations of UV absorbers to have complete blocking power. These thin films, such as those in polysiloxane abrasion resistant coatings, would need UV absorber concentrations as high as 30 percent to accomplish an optimal absorption based on the UV absorber. At that concentration, the properties of the coating are drastically degraded. The inside layer of the present system can be in a range of 6 microns or higher, using Uvitex OB (Ciba-Geigy), with 9-15 microns being optimum. This range is based on the maximum solubility of the UV absorber and the fluorescent material. If other UV absorbers and fluorescent materials are chosen, this film thickness range can be adjusted accordingly. In one embodiment of the present invention , the second, or outer, coat, in order to maintain flexibility, is in the 3 micron-3 mil range film thickness depending on the brittleness of the resin system. In order to maintain the properties of the outer coat at this film thickness, the UV absorber in this layer is kept at the maximum level before degradation of the physical properties of the coating occurs. In accordance with the invention, the disclosed system includes an outer coating which also has a UV absorber to prevent the blue glow at the inner surface of an inner layer. This blue glow will appear hazy prior to application of the outer coating. UVA absorbers that block all UV up to 400 nm tend to be significantly yellow in color. This is because oftheir absorption curve. The more gradual the slope of the curve, the more visible blue and violet light is absorbed, which is then perceived as yellow. It is desirable when blocking UV up to 400 nm to have a very steep transmission curve with a transmission cutoff at 400 nm to avoid the yellowing effect. Degradation due to outdoor exposure also occurs from pollutants, which are carried to the item via precipitation and air. These pollutants are typically oxides and various dilute acids such as acid rain. The pollutants can cause colorants to fade, as the molecular bonds are broken. It is desirable to have protection against this type of chemical breakdown such as a chemically resistant barrier. Certain items, such as printed paper, can also be damaged by precipitation such as rain and snow, which, in the form of water, causes the paper to deteriorate and some print materials such as ink to bleed. It is therefore desirable to create a barrier to precipitation for good outdoor weatherability. There currently exist coatings and laminations, which are partial UV blockers, and which are transparent, but have poor abrasion resistance, such as vinyl coatings and laminates. It is desirable to have good abrasion resistance in a product to be used outdoors to prevent changes in gloss levels from abrasion which might be caused by windborne debris or cleaning. The current practice of including UV absorbers in the body of plastic items, or in overcoatings, is often of limited effectiveness because it is weakened by the relationship of film thickness and concentration of UV absorber. The thicker the coating the lower the concentration of UV blocker necessary. Thin coatings are often desirable due to cost and flexibility. When a UV absorber is included in a colored molded item, the surface has the lowest concentration of UV absorber, and so this surface degrades quicker than the material behind this surface. Thus, even though the colored material contains UV absorber, its relative concentration at the surface of the item is low, so the color fades at the surface. With suitable coating, the weatherability of a molded plastic item is improved in terms of physical properties except for a significant improvement in color fade, as this is a surface effect. The bulk of the material has protection in depth. The best combination of protection against color fade is to include pigments, which are resistant to UV degradation, along with UV inhibitors. In the inkjet industry, it is common to combine UV-resistant inks with a UV-inhibiting outer laminate for further protection against fading in applications where long-term exposure to UV is expected. Solvent selection requires compatibility with the resin systems and additives, leveling characteristics, and the prevention of crystallization of the additives. The following examples are illustrative. EXAMPLE 1-1 The following example achieves a 9-10 micron film thickness. Percentages are by weight of volume solids: Inner Coating Acryloid A 21 - (Rohm & Haas) 25% Uvitex OB - (Ciba-Geigy Corp.) 11 % based on solids Tinuvin 328 - (Ciba-Geigy Corp.) 8% based on solids Acetylacetone 8% based on total weight Diluent toluene or xylene - depending upon method of application. Outer Coating A second coating is used to achieve a 3-4 micron film thickness. It comprises: GR 653 polysiloxane coating - 25% solids (Techneglas) 97.5 parts Tinuvin 328 - (Ciba-Geigy Corp.) 1.5 parts Toluene - 1 part. EXAMPLE 1-2 Inside Layer - Urethane Desmodur N-75: Bayer 36% of urethane solids Desmophen 670A-80:Bayer 64% of urethane solids Catalyst, dibutyltindilaurate: 0.1% based on urethane solids UV inhibitor, Tinuvin 328 - (Ciba-Geigy) 8% based on urethane solids Fluorescent, Tinuvin OB - (Ciba-Geigy) 11% based on urethane solids Surfactant, Flurad 430 - (3M) 0.1% based on urethane solids Diluent, Toluene to make 100%. The best order for mixing is to determine the amount of toluene that will be the diluent and stir in the Tinuvin OB until it completely dissolves. Add the UV inhibitor and stir until completely dissolved. Add the Desmophen 670-80A and stir until completely dissolved. Add the dibutyltindilaurate and stir. Add the catalyst and stir gently, until it is completely dissolved. The solids level of this coating can be adjusted to the processing technique and conditions to achieve an approximately 15 micron film thickness. The lower the film thickness, the higher the required level of Tinuvin 328 and Tinuvin OB. The ratio between UV inhibitor and fluorescent material is dependent on the UV absorption of the inhibitor and the wavelength shift of the fluorescent material. The goal is to make the UV cutoff up to 400 nm and then have maximum light transmission for the visible spectrum. Outer Layer - Acrylic Acryloid A-21 - (Rohm & Haas) received at 30% solids, diluted to 25% solids with toluene Flurad 430 (3M) 0.1% based on total coating solids Tinuvin 328 - (Ciba-Geigy) 8% based on A-21 solids Tinuvin OB - (Ciba-Geigy) 11 % based on A-21 solids Acetylacetone • 8% of total weight. EXAMPLE 1-3 Polysiloxane Outer Layer SHC 4000 (General Electric) 98.4% Tinuvin-328 (Ciba-Geigy) 1.5% Triethanolamine (optical brightener) 0.01 % Toluene or xylene solvent to achieve desired film thickness. Acrylic Inner Layer Joncryl 537 - (Johnson's Wax) Aqueous acrylic dispersion Uvinul D40 - (BASF-Wyandotte) 8% based on resin solids Flurad 430 - (3M) 0.1% based on resin solids Triethanolamine 0.1% based on resin solids OB A Quencher - (Kalamazoo Chemical Corp.) 0.1% based on resin solids. The outer coatings provide desired physical properties and they provide quenching of the optical brightener at the surface of the inside coating. This quenching is accomplished by UV transmission reduction by the outer coating and/or by adding a higher pH material, such as minor amounts of tetramethylaminohydroxine, to the outer coating, which quenches the optical brightener. Some typical applications are storefront display windows to protect the items on display from ultraviolet damage; protection of mkjet prints, which are very susceptible to ulfraviolet degradation; plastic sheeting, which degrades and turns yellow in outdoor applications; works of art, which are subject to man-made ultraviolet radiation; and, in general, any item that is damaged by ultraviolet radiation. In order to achieve weatherability of inkjet prints that may be used for signs, posters, billboards, etc., it is often necessary to laminate them with films that provide protection against ulfraviolet radiation. In another embodiment, a thin layer of polyester film is coated on one surface, and the blocking layer and the second coating is applied to the opposite surface. The film is provided with a suitable laminating adhesive, such as heat-activated vinyl, EVA, and similar adhesives. The film may be applied to an inkjet print on the printed side. This embodiment of the coating systems forms a thin, flexible, transparent, tear-resistant laminate that blocks out ultraviolet to less than one percent transmission at 400 nm, and to less than 0.1% transmission below 400 nm down to 280 nm. A polysiloxane coating also provides scratch resistance, as well as chemical resistance. By providing a two-layer system, rather than a single-layer system, it is possible to have the inner layer absorb the bulk of received ultraviolet radiation, and to reflect radiation above 375 nm as blue light, so that the coating is seen as clear rather than as a yellow tint. Most conveniently, both layers are applied using known spraying techniques in serial fashion, which lends itself to the application of both layers upon a thin polyester film, and the like. Other methods are possible, including dipping, flow-coating, curtain coating or by any other liquid application method. General Embodiment 2: There are several commonly available systems that are essentially ultraviolet transparent, and therefore, unaffected by ultraviolet exposure. These include acrylics, urethanes, polysiloxanes, and to a lesser degree, phenoxy resins. The two main classes of ultraviolet inhibitors are benzotriazoles and benzophenones. The benzophenone class tends to be very yellow when used in concentrations that efficiently block ulfraviolet transmission. The benzotriazoles typically block ultraviolet transmission up to 365 nm, and a few of them will block ultraviolet radiation up to 380 nm. Including a fluorescent material that converts long- avelength ultraviolet into longer-wavelength blue light will increase the ulfraviolet blocking efficiency up to 400 nm. The inclusion of fluorescent material may not be necessary if the light source is a man-made light source that does not emit the longer wavelengths of ultraviolet light. The phenoxy resin systems can be cross-linked with typical cross linkers for hydroxy-functional resins, such as melamine, urea-formaldehyde, heat reactive phenolica, and isocyanate-functional prepolymers. Dipping; spraying, flow coating, curtain coating, or any other liquid coating application technique can apply these coatings. The following examples are illustrated. Proportions are by weight of resin solids. EXAMPLE 2-1 Glass and Plastic Surfaces 1. Phenoxy resin, 20% (Paphen PKHC, Phenoxy Specialties, Rock Hill, South Carolina) 2. Melamine Crosslinker 1.6% (Cymel 325, Cytec Industries, Inc., W. Paterson, New Jersey) 3. Tinuvin-328 (Ciba-Geigy) 6% 4. Uvitex OB (Ciba-Geigy) 2.5% 5. Surfactant (Flurad 43, 3M Co.) 0.001% 6. Dioxolane Diluent to 100%. To improve adhesion to glass surfaces, heating to 35 OF is required for ten minutes, or longer times at lower temperatures. In some cases, the heat of an incandescent light source will be sufficient to fully crosslink this coating. EXAMPLE 2-2 Using acrylic solids, the following formulation is suitable; proportions are by volume of resin solids. 1. Acrylic resin (Acryloid A 1 OS Rohm & Haas) 20% 2. Tinuvin-328 (Ciba-Geigy) 6% 3. Uvitex OB (Ciba-Geigy) 2.5% 4. Surfactant (Flurad 430, 3M Co.) 0.001 % 5. Toluene or dioxolane diluent to 100%. To improve adhesion to glass surfaces, it may be necessary to pretreat the glass surface by etching or treating it with a hydrolyzed amino silane coupling agent, or to use other commonly known techniques to provide good adhesion to glass. The Uvitex OB may be omitted if complete ultraviolet absorption is not required. Using the Tinuvin 328 alone at the described concentration to resin solids will produce an ultraviolet cutoff at 380-384 nm at a 9-micron film thickness. These coatings may be further protected by overcoatings for additional chemical resistance or abrasion resistance. Some examples are aliphatic urethanes and polysiloxanes. The described embodiments relate to a thin coating that can be applied to either the inside or outside surface of light sources or display windows. As discussed above, ultraviolet light is the primary cause of photo degradation of many exposed items. It is the primary cause of colors fading, paints chalking, paintings cracking, fabrics fading, and the loss of physical properties, such as tensile and impact strength of many materials. Ultraviolet is defined as light having a wavelength of 400 nm or less. The cunent technology reduces the photodegradation effect of ultraviolet light by including ultraviolet inhibitors in the body of materials to be protected, or by overcoating the products with ultraviolet resin systems. Most ultraviolet inhibitors block or absorb ultraviolet radiation up to 380 nm in coatings that are at least one nm thick. Thinner films usually absorb considerably less ultraviolet, not only in optical density, which is the percentage absorbed, but also not as high as 380 nm. The most common absorption cutoff is 360 nm. Articles formed from materials that have ulfraviolet inhibitors included still have photodegradation at the surface. Absorption efficiency is determined by the absorption characteristics of the inhibitor and is directly related to concentration and thickness. The thinner the film, the higher the required percentage of ulfraviolet absorption material required. For example, a 9-micron film may require 30% based on resin solids for efficient blocking. Most ulfraviolet inhibitors will impair transparency when included in clear coatings at that level, or they will degrade the physical properties of the coating resin system. An example of an application is light sources in museums. Museums are very cautious about picture taking and light sources relative to artwork or artifacts. All incandescent light sources emit ultraviolet radiation, as do all fluorescent light sources. Coating the surface of the emitting source with a total ultraviolet blocking coating protects all items exposed to that source. Electronic flashes are normally provided with a focusing lens which can be coated to completely block ulfraviolet thus making them safe in museum and art galleries. Preferably, this coating is done on the inner surface of such lenses. EXAMPLE 2-3 A Melamine Crosslinked Flexible Resin System Proportions are by volume of resin solids. 1. Paphen phenoxy resin PKHC range 10%-40% (Phenoxy Specialties, Rock Hill, SC) 2. Cymel 303 melamine resin - range 2%-10% (Cytec Industries, Long Beach, NY) 3. P-toluene sulfuric acid catalyst - range 0.001 -%-0.1 % 4. Uvitex OB - range l%-6% (Ciba-Geigy) Optical brightener 5. Tinuvin 328 - range 0.2%-4% (Ciba-Geigy) U.V. absorber 6. Solvents for dilution to create the desired film thickness, including methyl ethyl ketone, dioxolane, toluene and others to make 100%. The above formulation has excellent tensile strength. These properties are of particular value when the coating is applied to a glass light bulb. The coated bulb will tend to be held together when the bulb is broken, for improved safety. EXAMPLE 2-4 A Melamine Resin System 1 Cymel 303 solids - range 20%-50% (Cytec Industries) 2, P-toluene sulfuric acid catalyst - range 0.01% - 0.3% 3. Uvitex OB -range l%-8% (Ciba-Geigy) 4 Tinuvin 328 -range 0.1%-4% (Ciba-Geigy) Solvents for dilution to achieve film thickness, including toluene, xylene, methyl ethyl ketone, dioxolane and others to make 100%. Either sample will cure at temperatures of 250 F - 350 F, with shorter times for higher temperatures. The primary material that blocks most of the ultraviolet light and converts it to visible light is the Uvitex OB, in sufficient quantities ranging from 0.1% to as much as 8%. As indicated by the graph shown in Figure 1(a), this light appears as visible light in the range of 42Q nm to 575 nm, with peaks at 440 nm and 490 nm. This result was obtained by coating a standard 20-watt fluorescent tube to 9 nm thickness. It has been determined that in the case of incandescent and fluorescent lamps, the covered ultraviolet light may range to as much as 30 percent to 50 percent of the total light output. Absorption of ultraviolet radiation up to 380 nm employs a standard ultraviolet absorber. Absorbing up to 380 nm is not a requirement. It may be less than 340 nm provided that the fluorescent material makes up the difference. The fluorescent material converts ultraviolet radiation from about 340 to 400 nm to visible light. This provides a complete ultraviolet cutoff with almost any commercially available ultraviolet absorber combined with a fluorescent material. If intense ultraviolet radiation reaches the disclosed blocking system, it may cause a glow from the. fluorescent material. However, two steps can prevent the glow, using a two-layer coating system, and using a slower drying solvent such as acetylacetone, or similar solvents such as xylene. A requirement is that the solvent dry slowly, and be compatible with the resin system, the ulfraviolet absorber, and the fluorescent material. This can also be accomplished in a single solvent system as thin as 2 microns. The lower film thickness is provided by increasing the percentage of ulfraviolet blocking materials to 40 percent based on resin solids. This is useful, for example, in dye transfer sublimation, where low film thicknesses are absolutely necessary to transfer the coating from a film to the surface of an image. EXAMPLE 2-5 A 2 Micron Example 1. Acryloid A21 (Rohm & Haas) at 7% solids 22.94% 2. Tinuvin 328 (Ciba-Geigy) 1.18% 3. Uvitex OB (Ciba-Geigy) 1.62% 4. FSN 100 (Zonyl surfactant, Dupont) 0.1% 5. Acetylacetone 8% 6. Toluene 37.05% 7. Methyl isobutyl ketone, or methyl ethyl ketone 37.05%. If the film thickness is increased to 9 microns, the level of ulfraviolet blocking materials is decreased to 19 percent based on resin solids. High temperature resin systems can be used with the disclosed system for application to high temperature light sources. Another embodiment is to provide a hybrid lightbulb, one that is coated with a fluorescent material on its outside surface to convert the ulfraviolet emission of the bulb into visible light. No ultraviolet absorber is necessary unless it is necessary to remove the ultraviolet radiation below 340 nm. The object of this embodiment is to increase visible light by converting ulfraviolet light into visible light. A side effect is that the conversion also blocks the ulfraviolet from about 340 nm and higher. If it is also necessary to block lower ulfraviolet wavelengths, then an ultraviolet absorber must be used with the fluorescent material. Each of these coatings uses a binder resin. The properties of the binder resin allow these coatings to be used in different applications. For example, the bulb coating can be made with a fluorescent material and a high temperature resin such as GR 150 or GR 908 (polysiloxane resin, from Techneglas). These resins can withstand very high temperatures for extended periods of time. These resins can also be used on high- intensity halogen bulbs, which have a very high ultraviolet emission. For low temperature applications, such as a fluorescent bulb, acrylic resin can be used. In such applications, it is not a requirement to use an ultraviolet absorber in the lightbulb coating, merely a fluorescent material. The concentration of fluorescent material is optimized in the following example: EXAMPLE 2-6 A Bulb Coating Formulation 1. GR 150 (Techneglas, Long Beach, NY) at 15% solids 2. MIBK/Toluene 50/50% we weight 3. Acetylacetone 8% of total weight 4. Uvitex OB 19% based upon GR 150 solids 5. BYK 330 (BYK Chemie, Middletown, Connecticut) 0.5% based on resin solids. EXAMPLE 2-7 Using the proportions of Example 2-6, GR 150 is substituted by G.R. 908 (Techneglas). It will be appreciated that a variety of ultraviolet absorbing materials may be used in conjunction with an optical brightener wliich will be operative to cover the range commencing the wavelength where the ultraviolet absorber ceases to operate, to provide a substantially complete cutoff. Referring to Figure 1(a), there is illustrated the relative output of a coating versus an uncoated 20 watt fluorescent tube. In the case of the uncoated lamp, radiation commences at about 330 nm, with the bulk of the light put output extending between that point and 425 nm. There are peak outputs at 440 nm, 550 nm, and 575 mn. By contrast, the coated lamp has substantially all radiation up to about 415 nm completely blocked, with the visible output commencing at about 420 nm and extending to about 570 nm. It will be observed that there is an area commencing at 425 nm where the curve crosses and extends above that for the uncoated lamp to about 570 nm, indicating that a portion of the ultraviolet light has been converted to the visible light spectrum. General Embodiment 3: The ultraviolet block material of the present invention usually contains an ultraviolet radiation absorber and a fluorescent material. <Ultraviolet Radiation Absorber> With regard to an ultraviolet radiation absorber, that which mainly absorbs the light within a range of 300-380 nm may be exemplified, and that of a benzophenone type, a benzotriazole type, a salicylic acid type, and a hydroquinone type can be used. Preferably, a benzophenone type and a benzotriazole type are used and, particularly preferably, a benzotriazole type is used. Examples of a benzophenone type are 2-hydroxy-4-n-octoxybenzoρhenone such as CHIMASSORB 81 FL (a product of Ciba-Geigy); 2-hydroxy-4-methoxy-2'- carboxybenzophenone; 2,4-dihydroxybenzophenone; 2,2'-dihydroxy-4,4'-dimethoxy- benzophenone such as Uvinul D-49 (a product of BASF); 2-hydroxy-4- benzoyloxybenzophenone; 2,2'-dihydroxy-4-methoxy-benzophenone such as Cyasorb UV-24 (a product of ACC); 2-hydroxy-4-methoxy-5-sulfonebenzophenone; 2,2 ',4,4' - tetrahydroxybenzophenone; 2,2'-dihydroxy-4,4'-dimethoxy-5-sodium sulfonebenzophenone; 4-dodecyloxy-2-hydroxy-benzophenone; and 2-hydroxy-5- chlorobenzophenone and the like. Examples of a benzotriazole type are 2-(5'-methyl-2'-hydroxyphenyl)- benzotriazole such as Tinuvin P (a product of Ciba-Geigy); 2-(2'-hydroxy-5'-tert- butylphenyl)-benzotriazole such as Tinuvin PS (a product of Ciba-Geigy); 2-[2'-hydroxy- 3',5'-bis(a, -dimethylbenzyl)-phenyl]-2H-benzotriazole such as Tinuvin 234 (a product of Ciba-Geigy); 2-(3',5'-di-tert-butyl-2'-hydroxyphenyl)-benzotriazole such as Tinuvin 320 (a product of Ciba-Geigy); 2-(3'-tert-butyl-5'-methyl-2'-hydroxyphenyl)-5- chlorobenzotriazole such as Tinuvin 326 (a product of Ciba-Geigy); 2-(3',5'-di-tert-butyl- 2'-hydroxyphenyl)-5-chlorobenzotriazole such as Tinuvin 327 (a product of Ciba-Geigy); 2-(3',5'-di-tert-amyl-2'-hydroxyphenyl)-triazole such as Tinuvin 328 (a product of Ciba- Geigy); 5-tert-butyl-3-(5-chloro-2H-benzotriazol-2-yl)-4-hydroxybenzenepropionic acid octyl ester such .as Tinuvin 109 (a product of Ciba-Geigy); and 2-(2'-hydroxy-3,5-di- (l, -dimethylbenzyl)phenyl)-2H-benzotriazole such as Tinuvin 900 (a product of Ciba- Geigy) and the like. Examples of a salicylic acid type are phenyl salicylate such as Seesorb 201 (a product of Shiraishi Calcium); p-tert-butyl salicylate such as Sumisorb 90 (a product of Sumitomo Chemical); and p-octylphenyl salicylate (a product of Eastman Chemical) and the like. Examples of a hydroquinone type are hydroquinone and hydroquinone salicylate and the like. The amount of the ulfraviolet radiation absorber used for the base material is usually not less than 5% by weight, preferably not less than 6% by weight or, more preferably, not less than 10% by weight, and usually not more than 30% by weight or, preferably, not more than 25% by weight. When the amount of the ultraviolet radiation absorber is too small, it is not possible to make the light transmittance of ultraviolet region 10% or less while, when it is too much, there is a possibility that the ultraviolet radiation absorber bleeds out. <Fluorescent Material> A fluorescent material is one that absorbs ultraviolet light of a wavelength region of 340-400 nm and emits the light within a range of 400-500 nm. A fluorescent material absorbs the long- wave region of ultraviolet light and, therefore, fading, discoloration, and decolorization of the colorant can be effectively prevented when a fluorescent material is contained. Examples of a fluorescent material are materials of a diaminostilbene type, an imidazole type, a thiazole type, an oxazole type (such as 2,5-bis[5-tert-butylbenzoxazol- 2-yl]thiophene [Uvitex OB, a product of Ciba-Geigy]), a triazole type, an oxadiazole type, a thiadiazole type, a coumarin type, a naphthalimide type, a pyrazoline type, a pyrene type, an imidazolone type, a benzidine type, a diaminocarbazole type, an oxacyanine type, a methine type, a pyridine type, an anthrapyridazine type, a distyryl type and a carbostyryl type and the like. Preferably, an oxazole type is used. The amount of the fluorescent material contained for the base material is usually not less than 3% by weight, preferably not less than 6% by weight or, more preferably, not less than 10% and usually not more than 30% by weight or, preferably, not more than 25% by weight. When the amount of the fluorescent material is too small, it is not possible to make the light transmittance of ultraviolet region of not shorter than 380 nm 10% or less while, when it is too much, there is a possibility that the fluorescent material bleeds out. Examples of the base material constituting the ultraviolet block material are synthetic resin, oil, gelatin and starch, which are not colored at the visible light region, and, usually, resin is used. Any resin may be used so far as it can be made into film or can form a resin layer as a result of drying and/or hardening when applied on a substrate. To be more specific, polyester resin, polystyrene resin, acrylate resin, polyurethane resin, acrylurethane resin, vinyl chloride resin, polyamide resin, vinyl acetate resin, epoxy resin, phenoxy resin, and cellulose type resin may be exemplified. <Overcoat> As shown in Figure 2, an embodiment of the ultraviolet block material 1 of the present invention is in such a structure having a substrate 2 and an ultraviolet block layer 3 which is provided on the substrate in a releasable manner. Such an ultraviolet block material 1 can be adhered on a material 8 to be transfened by, for example, the following manner. First, as shown in Figure 3(a), the farthest side of the ultraviolet block layer 3 of the ultraviolet block material 1 from the substrate 2 is layered on a material 8 to be attached. The farthest side of the ultraviolet block material 1 from the transcription layer usually has an adhesive layer 7 for making the adhesion with the material to be transferred better. When an image is formed on the surface of the material to be transfened, the side 9 on which the image is formed is piled on the ulfraviolet block material so as to contact the farthest side from the substrate of the ultraviolet block layer thereof. After that, the ulfraviolet block layer and the material to be transferred are adhered by means of heating or pressurization. Finally, as shown in Figure 3(b), the substrate 2 is separated from the ulfraviolet block layer 3 whereby only the ultraviolet block layer 3 is adhered on the material 7 to be transfened. A method where only an ultraviolet block layer is layered on the material to be transfened as such is called overcoat. In an ultraviolet block material comprising a substrate and an ultraviolet block layer provided on the substrate in a releasable manner, the layer which is farthest from the subsfrate of the ultraviolet block layer may be a layer for receiving color materials. When the layer which is farthest from the substrate of the ultraviolet block layer is a color material-receiving layer, it is possible that image is formed on the color material- receiving layer of the ultraviolet block material of the present invention by means of an inkjet printing method, a thermal transfer printing method or the like, then the color material-receiving layer and the subsfrate paper are layered so as to be contacted, the ultraviolet block layer and the substrate paper are stuck, then the ultraviolet block layer and the substrate paper are adhered by means of heating or pressurization, and the substrate is separated from the ulfraviolet block layer whereupon a protected image can be formed. Overcoat: 1> One of the prefened embodiments in an ulfraviolet block material comprising a subsfrate, and an ultraviolet block layer provided on the substrate in a releasable manner, is a structure in which the ultraviolet block layer has a layer containing a fluorescent material, the layer containing the fluorescent material has at least one layer between it and the substrate, and there is also at least one layer on the layer containing the fluorescent material at its side opposite to the subsfrate, and, in addition, any of the layers contains an ultraviolet radiation absorber. As a result of having such a structure, the layer containing a fluorescent material does not directly contact the air even in a state where the ulfraviolet block layer is present on the subsfrate or even in a state where the ultraviolet block layer is layered on the material to be transfened, and therefore, reduction in the ultraviolet blocking ability can be significantly suppressed. When the layer containing the fluorescent material contacts the air, the fluorescent material is decomposed by light and oxygen in air whereby the ultraviolet blocking ability lowers immediately and the ultraviolet block material allows the transmittance of ultraviolet light of near 350-380 nm wavelength. When at least one layer among the layers between the substrate and the layers containing a fluorescent material contains an ultraviolet radiation absorber, the outcome is that the ultraviolet radiation absorber is present outside of the layer containing the fluorescent material under such a state that the ultraviolet block layer is adhered on the material to be transfened. Accordingly, especially in case the material to be transfened is an image, ultraviolet light at first passes through the layer containing the ultraviolet radiation absorber and then arrives the layer containing the fluorescent material whereby the amount of the ultraviolet light arriving the layer containing the fluorescent material can be reduced and the decomposition of the fluorescent material by ultraviolet light can be effectively prevented. Preferably, the layer containing the fluorescent material contains an ultraviolet radiation absorber. When the layer containing the fluorescent material contains an ultraviolet radiation absorber, that is prefened in such a respect that the amount of ultraviolet light affecting the fluorescent material can be reduced as same as in the above- mentioned case. Particularly prefened one is a structure where an ultraviolet radiation absorber is contained in a layer containing the fluorescent material and also in at least one layer among the layer existing between the substrate and the layer containing the fluorescent layer. Such a structure is prefened in such a respect that the ultraviolet light affecting the fluorescent material can be further reduced. <Overcoat: 2> Another prefened embodiment, in an ultraviolet block material comprising a substrate and an ultraviolet block layer provided on the substrate in a releasable manner, is that the ultraviolet block layer comprises a layer containing a fluorescent material and that the layer containing the fluorescent material contains an ultraviolet radiation absorber and a stabilizer. In such a structure, the stabilizer is present in a layer containing the fluorescent material and, therefore, decomposition of the fluorescent material by ultraviolet light and by oxygen can be effectively suppressed. It is prefened in the above structure that the structure has at least one layer between a substrate and a layer containing the fluorescent material or that the structure has at least one layer on the side, opposite to the substrate, of the layer containing the fluorescent material. In a particularly prefened structure, there is at least one layer between the subsfrate and the layer containing the fluorescent material and further, there is at least one layer on the side, opposite to the substrate, of the layer containing the fluorescent material. In case where there is at least one layer between the substrate and the layer containing the fluorescent material, it is prefened that an ultraviolet radiation absorber is contained at least in one of the layers existing between the substrate and the layer containing the fluorescent material. <Overcoat: 3> Another prefened embodiment, in the ultraviolet block material comprising a substrate and an ulfraviolet block layer provided on the subsfrate in a releasable manner, is a structure in which the ulfraviolet block layer has a layer containing a fluorescent material and at least one layer containing an ultraviolet radiation absorber between a substrate and a layer containing a fluorescent material and, in addition, the layer containing the fluorescent material contains a stabilizer. In this structure, the layer containing a fluorescent material contains a stabilizer and, therefore, decomposition of the fluorescent material can be prevented. Further, since there is a layer containing an ultraviolet radiation absorber between a substrate and a layer containing a fluorescent material, the result is that, under a state that the ultraviolet block layer is adhered on the material to be transfened, the ultraviolet radiation absorber is present outside the layer containing the fluorescent material. Accordingly, especially when the material to be transfened is an image, ultraviolet light firstly passes through the layer containing the ultraviolet radiation absorber and then arrives the layer containing the fluorescent material and, therefore, the amount of ultraviolet light arriving the layer containing the fluorescent material can be reduced and decomposition of the fluorescent material by ultraviolet light can be effectively prevented. In this structure, it is prefened that the structure is in such a manner that there is at least one layer on the side, opposite to the substrate, of the layer containing the fluorescent material. <Laminate> One of the embodiments of the ultraviolet block material of the present invention is a structure as shown in Figure 2 having a subsfrate 2 and an ultraviolet block layer 3 layered on the substrate. In that case, the substrate and the ultraviolet block layer are adhered to such an extent that they are not usually detached. Such an ultraviolet block material 1 is adhered on the material 8 to be laminated, for example, by the following manner. First, as shown in Figure 3(a), the side, which is farthest from a substrate, of the ultraviolet block layer 3 of the ultraviolet block material 1 is piled so as to contact the material 8 to be laminated. The farthest surface of the ultraviolet block material from the substrate usually has an adhesive layer 7 in order to make the adhesion with the material to be laminated good. When an image is formed on the surface of the material to be laminated, the surface 9 on which the image is formed and the farthest side of the ultraviolet block layer of the ultraviolet block material from the substrate are piled so as to contact them. After that, the ultraviolet block layer and the material to be laminated are adhered by means of heating or pressurization. The subsfrate is not separated from the ultraviolet block layer, but is adhered to the material to be laminated together with the ultraviolet block layer. A method where the ultraviolet block material is adhered on the material to be laminated as such is called laminate. In an ultraviolet block material comprising a subsfrate and an ulfraviolet block layer adhered on the substrate, the side of the substrate opposite to the ultraviolet block layer or the farthest layer from the substrate of the ultraviolet block material may be a layer receiving color materials (or colorants). In such a case, it is possible to form an image protected by the ultraviolet block layer when an image is formed on the color material-receiving layer of the ultraviolet block material of the present invention by means of an ink jet printing method, a thermal transfer printing method or the like, then the color material-receiving layer and the subsfrate are piled so as to be in contact with each other, and the ulfraviolet block material and the substrate are adhered. <Laminate: 1> In an ulfraviolet block material comprising a subsfrate and an ulfraviolet block layer adhered on the substrate, one of the prefened embodiments is such a structure that the ultraviolet block layer has a layer containing a fluorescent material, there is at least one layer on the side, opposite to the substrate, of the layer containing the fluorescent material, and any of the layers constituting the ultraviolet block layer contains an ultraviolet radiation absorber. In the case of laminate, after the ultraviolet block material is adhered on the material to be laminated, the substrate is not separated from the ultraviolet block layer and, therefore, there is at least one layer outside of the layer containing the fluorescent material whereby the layer containing the fluorescent material is not exposed to air both before and after adhering to the material to be laminated and the ultraviolet blocking effect can be maintained for a long period. When at least one layer between the substrate and the layers containing a fluorescent material contains an ultraviolet radiation absorber, the outcome is that the ultraviolet radiation absorber is present outside of the layer containing the fluorescent material under such a state that the ultraviolet block layer is adhered on the material to be laminated. Accordingly, especially in case where the material to be laminated is an image, ulfraviolet light at first passes through the layer containing the ulfraviolet radiation absorber and then arrives at the layer containing the fluorescent material whereby the amount of the ultraviolet light arriving at the layer containing the fluorescent material can be reduced and the decomposition of the fluorescent material by ultraviolet light can be effectively prevented. Preferably, the layer containing the fluorescent material contains an ultraviolet radiation absorber. When the layer containing the fluorescent material contains an ultraviolet radiation absorber, that is prefened in such a respect that the amount of ultraviolet light affecting the fluorescent material can be reduced as in the above- mentioned case. A particularly prefened structure is one where an ulfraviolet radiation absorber is contained in a layer containing the fluorescent material and also in at least one layer among the layer existing between the substrate and the layer containing the fluorescent layer. Such a structure is prefened in such a respect that the ulfraviolet light affecting the fluorescent material can be further reduced. <Laminate: 2> Another prefened embodiment, in an ultraviolet block material comprising a substrate and an ultraviolet block layer adhered on the subsfrate, is such a structure that the ultraviolet block layer comprises a layer containing a fluorescent material and that the layer containing the fluorescent material contains an ultraviolet radiation absorber and a stabilizer. It is prefened that the ultraviolet block layer has at least one layer between a substrate and a layer containing a fluorescent material and/or has at least one layer on the side, opposite to the substrate, of the layer containing the fluorescent material. Preferably, it is a structure where at least one of the layers existing between a substrate and a layer containing a fluorescent material contains an ultraviolet radiation absorber. <Laminate: 3> Another prefened embodiment, in the ultraviolet block material comprising a subsfrate and an ultraviolet block layer adhered on the subsfrate, is a structure in which the ulfraviolet block layer has a layer containing a fluorescent material and at least one layer containing an ultraviolet radiation absorber between a subsfrate and a layer containing a fluorescent material and, in addition, the layer containing the fluorescent material contains a stabilizer. Preferably, it is a structure where there is at least one layer on the side, opposite to the substrate, of the layer containing the fluorescent material. As hereunder, a substrate constituting an ultraviolet block material and an ultraviolet block material will be illustrated. <Substrate> The subsfrate may be anything that has been known and has some heat resistance and strength. Examples include polyester film such as polyethylene terephthalate, polystyrene film, polypropylene film, polysulfone film, polyphenylsulfide film and polyethylene naphthalate film and prefened ones are polyester film, paraffin paper, glassine paper and condenser paper. Among the polyester film, particularly preferably used one is a polyethylene terephthalate film. Such a substrate may be either in a sheet or in a continuous film. Especially in the case of an ultraviolet block material used for laminate, it is prefened that the transmittance of the substrate for the light within a range of 420-800 mn is 90% or more or, preferably, 95% or more. In the case of an ultraviolet block material used for overcoat, there will be no problem even when the subsfrate is not transparent. Thickness of the subsfrate is usually not less than 0.5 μm or, preferably, not less than 3 μm, and usually not more than 100 μm, preferably not more than 50 μm or, more preferably, not more than 10 μm. When the ultraviolet block layer is provided in a releasable manner, it is prefened that the surface of the substrate 2 or, particularly, the side 10 connecting the ultraviolet block layer has a releasing layer for making the releasing of the ultraviolet block layer good. The releasing layer is a layer comprising a resin having a low surface energy. To be more specific, waxes, silicone resin and fluorine-containing resin; a product where the above resin is graft-bonded to the side chain of acrylate resin or butyral resin; a hardened product of modified silicone oils; a reaction product of modified silicone oil with an isocyanate compound or an epoxy compound; resin where silicone oil is mixed with resin having a good adhesion to the substrate and the like may be used. Silicone resin of a type which is hardened by ultraviolet light, silicone resin of a thermosetting type, and silicone resin of a type that is hardened at room temperature may be used as well. Thickness of the releasing layer is usually 0.02 μm or more or, preferably, 0.05 μm or more, and usually 2 μm or less or, preferably, 1 μm or less. When the ultraviolet block layer is adhered to the subsfrate, the surface of the subsfrate 2 or, particularly, the surface 10 contacting the ultraviolet block layer may have a primer layer for enhancing the adhesion with the ultraviolet block layer. When the ultraviolet block layer is adhered to the subsfrate, it is prefened that there is an abrasion-resisting layer at the subsfrate surface which is opposite to the layer to be adhered, he abrasion-resisting layer is a resin layer having excellent mechanical strength and slipping property. To be more specific, silicone resin and fluorine resin; a product where silicone resin or fluorine resin is subjected to a graft bonding to polycarbonate, butyral resin or acrylate resin; a hardened product of modified silicone oils; a reaction of product of a modified silicone oil with an isocyanate compound or an epoxy compound; resin having a high mechanical strength by mixing with silicone oils; etc. may be used as a binder. Particles may be added to such a binder for reducing contacting area. With regard to the particles, those that are fransparent in a visible region and are fransparent when mixed with a binder are selected. Specific examples thereof are silicone particles, silica particles and resin particles. It is prefened that the refractive index of the particles is near that of the binder because fransparency of the abrasion-resisting layer becomes high by that. With regard to the resin particles, those that are three-dimensionally cross-linked are prefened for preventing their swelling when dispersed in common organic solvents. Thickness of the abrasion-resisting layer is usually 0.1 μm or more or, preferably, 0.5 μ or more, and usually 15 μm or less or, preferably, 5 μm or less. <Ultraviolet Block Layer> Total thickness of the ulfraviolet block layer is usually 0.1 μm or more or, preferably, 0.5 μm or more, and usually 5 mm or less, preferably 20 μm or less, more preferably, 10 μm or less, particularly preferably 9 μm or less or, most preferably, 6 μm or less. Especially when the ultraviolet block material or the ultraviolet block layer of the present invention is layered on the surface of the image, it is usually 10 μm or less, preferably 9 μm or less or, more preferably, 6 μm or less. Particularly when only the ulfraviolet block layer is layered on the material to be transfened, the ulfraviolet block layer is hardly cleaved if the ulfraviolet block layer is too thick while, when it is too thin, the ultraviolet block layer may be cracked. In the ultraviolet block layer, the transmittance of the light within a range of 300- 380 nm wavelength region is 10% or less, preferably that within a range of 300-390 nm is 10% or less or, particularly preferably, that within a range of 300-400 nm is 10% or less and the transmittance of the light within a range of 420-800 nm is 90% or more or, preferably, 95% or more. Usually, a layer containing a fluorescent material constituting an ulfraviolet block layer comprises a base material and a fluorescent material. As to the base material of the layer constituting the fluorescent material, resin is usually used. Examples of the resin are those mainly comprising ethyl cellulose, vinyl acetate resin and derivatives thereof, polyolefin, ethylene-vinyl acetate copolymer, acrylate resin and derivatives thereof, polystyrene and copolymers thereof, polyisobutylene, hydrocarbon resin, polyamide resin, polyester resin, polyurethane resin, acryl-urethane resin, epoxy resin, phenoxy resin, and cellulose type resin and other thermoplastic resins. A thickness of the layer containing the fluorescent material is usually not less than 0.5 μm and usually not more than 10 μm, preferably not more than 9 μm or, particularly preferably, not more than 3 μm. Examples of the fluorescent material are those which were mentioned already. The amount of the fluorescent material in the layer containing the fluorescent material is appropriately decided depending upon a thickness of the layer containing the fluorescent material, titer of the fluorescent material, etc. and is usually not less than 3% by weight, preferably not less than 6% by weight or, particularly preferably, not less than 10% by weight and usually not more than 30% by weight, preferably not more than 25% by weight or, particularly preferably, not more than 20% by weight to the base material. A thickness of the layer 5 between the substrate and the layer containing the fluorescent material is usually not less than 0.5 μm and usually not more than 10 μm, preferably not more than 9 μm or, particularly preferably, not more than 3 μm. Incidentally, when there are plural layers, the thickness means that of one layer. With regard to the material constituting the layer existing between the substrate and the layer containing the fluorescent material, a material that is the same as that used as the base material for the layer containing the fluorescent material may be used. When the ulfraviolet block layer is provided in a releasable manner on the subsfrate, and there is no releasing layer on the surface of the subsfrate contacting ultraviolet block layer, it is prefened that the surface nearest the substrate among the layers 5 between the substrate 2 and the layer 4 containing the fluorescent material is a releasing layer. The releasing layer is peeled together with the ulfraviolet block layer from the subsfrate. The releasing layer is a layer comprising a resin having a low surface energy. To be more specific, there may be used wax, silicone resin, fluorine-containing resin; a product where the above resin is graft-bonded to the side chain of acrylate resin or butyral resin; a hardened product of modified silicone oils; a reaction product of modified silicone oil with an isocyanate compound or an epoxy compound; a resin where silicone oil is mixed with a resin having a good adhesion to the subsfrate; etc. An ultraviolet- setting silicone resin, a thermosetting silicone resin and a silicone resin setting at room temperature may be advantageously used as well. A product where these resins are compounded to particles is preferably used. A thickness of the releasing layer is usually not less than 0.02 μm or, preferably, not less than 0.05 μm and usually not more than 2 μm or, preferably, not more than 1 μm. A thickness of the layer which is in an opposite side of the subsfrate to the layer containing a fluorescent material is usually not less than 0.5 μm, and usually not more than 10 μm, preferably not more than 9 μm or, particularly preferably, not more than 3 μm. Incidentally, when there are plural layers, the thickness means that of one layer. With regard to the material constituting the layer which is in an opposite side of the substrate to the layer containing the fluorescent material, a substance that is same as that used as the base material for the layer containing the fluorescent material may be used. It is prefened that the layer 6 farthest from the substrate among the layers provided on the side, opposite to the substrate, of the layer containing the fluorescent material is an adhesive layer 7 having an adhesive property by means of heating or pressurization because, even when the surface of the material to be layered has no adhesive layer, adhesion to the material to be layered is strong. An example of the adhesive layer is a layer comprising a heat-sensitive adhesive and an example of the heat- sensitive adhesive is a resin having substantially no stickiness and having a glass transition point (Tg) of 40-75°C as described in the Japanese Patent No. 2,999,515. Specific examples are those resins having a good adhesion upon heating such as acrylate resin, polyvinyl chloride resin, polyvinyl acetate resin, vinyl chloride-vinyl acetate copolymer or polyester resin. A thickness of the adhesive layer is usually not less than 0.1 μm and not more than 10 μm. With regard to a color material-receiving layer which is provided in the case of a direct formation of image on an ulfraviolet block material, a color material-receiving layer which is suitable for each image forming method such as dye sublimation or dye diffusion thermal transfer, wax type thermal transfer and inkjet may be appropriately selected. With regard to a color material-receiving layer for a dye sublimation or dye diffusion thermal transfer, known ones may be used and its main component is a thermoplastic resin which is able to receive a thermally sublimating or diffusing dye from a thermal transfer sheet. To be more specific, polyester resin, acrylate resin, polystyrene, styrene type homopolymer, acrylstyrene copolymer, polycarbonate, polysulfone, polyvinylpynolidone, polyamide resin, polyvinyl acetal resin, polyvinyl alcohol resin, polyvinyl chloride, polyvinyl acetate, vinyl chloride-vinyl acetate copolymer, phenoxy resin, epoxy resin, cellulose ester resin, silicone resin and fluorine resin and the like may be exemplified. Besides those resins, it is possible to add various kinds of plasticizer as well as peeling agents and stabilizers that will be mentioned later. Examples of a peeling agent are modified silicone oils and a reaction product of modified silicone oil with an isocyanate compound and an epoxy compound. It is also possible that a color material-receiving layer is cross-linked in a three- dimensional manner for improving the peeling from the thermal transfer sheet, and for improving the heat resistance. In this case, a thickness of the color material-receiving layer is usually not less than 1 μm or, preferably, not less than 2 μm, and usually not more than 10 μm or, preferably, not more than 5 μm. With regard to a color material-receiving layer of a wax type thermal transfer, known porous receiving layer and receiving layer having no fine pores may be exemplified. Examples of the porous receiving layer are those containing a water-dispersible polyurethane resin and, if necessary, pigment as main component(s). A thickness of the color material-receiving layer in this case is usually not less than 0.5 μm or, preferably, not less than 0.8 μm and usually not more than 20 μm or, preferably, not more than 10 μm. With regard to a color material-receiving layer for an in jet method, layers comprising known water-soluble resin and water-insoluble resin may be exemplified. A receiving layer comprising a water-soluble resin is prefened. With regard to the water-soluble resin, there may be used gelatin, polyvinylpynolidone, polyethylene oxide, polyacrylamide, polyvinyl alcohol, terminal- modified polyvinyl alcohol, etc. Such a resin may be compounded with known additives or resin for giving a luster. When the color material-receiving layer is porous, organic or inorganic fine particles are added for forming fine pores in the color material-receiving layer. Preferably, inorganic fine particles are used and, particularly preferably, white inorganic pigment or the like is used. An amount of a coating for the color material-receiving layer is usually not less than 0.3 g/m 2 , particularly not less than 1 g/m 2 or, particularly preferably not less than 2 g/m 2 and usually not more than 30 g/m 2 , preferably not more than 25 g/m 2 or, particularly preferably, not more than 20 g/m 2 . In a direct formation of an image on an ultraviolet block material, although there is no particular limitation for the substrate paper which is layered on the ultraviolet radiation block material of the present invention, there may be used synthetic paper comprising the resin of polyolefm type, polystyrene type, polyester type, etc. and white non-transparent film or foamed sheet; various paper materials such as high-quality paper, art paper, coated paper, cast coated paper, paper impregnated with synthetic resin or emulsion, paper impregnated with synthetic rubber latex, paper lined with synthetic resin, cellulose fiber paper and resin-coated paper where at least one side of the paper has a polyolefin resin-coated layer to which pigment or the like is added (the so-called RC paper); various kinds of plastic films and sheets such as polyolefin, polyvinyl chloride, polyethylene terephthalate, polystyrene, polymethacrylate and polycarbonate etc.; and cards made of polyvinyl chloride or the like. When the substrate paper has a poor tight adhesion to the color material-receiving layer, it is prefened to subject its surface to a primer treatment or a corona discharge treatment. A thickness of the substrate paper is usually about 10-300 μm. With regard to the ulfraviolet radiation absorber, those which were mentioned already may be exemplified. An amount of the ulfraviolet radiation absorber in the layer containing an ultraviolet radiation absorber may be appropriately decided depending upon thickness of the layer, titer of the ultraviolet radiation absorber, etc., and is usually not less than 5% by weight, preferably not less than 6% by weight or, more preferably, not less than 10% by weight and usually not more than 30% by weight, preferably not more than 25%) by weight or, more preferably, not more than 20% by weight. A stabilizer is a substance which prevents the decomposition of the fluorescent material by oxygen or ultraviolet light and it is usually contained in the same layer in which the fluorescent material is contained. Although there is no particular limitation for the stabilizer, its specific examples are antioxidant of a hindered amine type, an antioxidant of a hindered phenol type and a light stabilizer of a benzoate type and the like. An ultraviolet radiation absorber may be used as a stabilizer as well. Examples of an antioxidant of a hindered amine type are bis(2,2,6,6-tetramethyl- 4-piperidyl) sebacate such as Tinuvin 770 (a product of Ciba-Geigy); bis(l, 2,2,6,6- pentamethyl-4-piperidyl) sebacate such as Tinuvin 765 (a product of Ciba-Geigy); and bis(l ,2,2,6,6-pentamethyl-4-piperidyl) 2-(3,5-di-tert-butyl-4-hydroxybenzyl)-2-n- butylmalonate such as Tinuvin 114 (a product of Ciba-Geigy). Examples of an antioxidant of a hindered phenol type are pentaerythritol tetrakis[3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate] such as Irganox 1010 (a product of Ciba-Geigy); thiodiethylenebis[3-(3 ,5-di-tert-butyl-4-hydroxyphenyl) propionate] such as Irganox 1035 (a product of Ciba-Geigy); octadecyl 3-(3,5-di-tert- butyl-4-hydroxyphenyl) propionate such as Irganox 1076 (a product of Ciba-Geigy); ethylenebis[3-(3,5-di-tert-butyl-4-hydroxyphenyl-m-tolyl) propionate] such as Irganox 245 (a product of Ciba-Geigy); 2,6-di-tert-butyl-4-[4,6-bis(octylthio)-l,3,5-triazin-2- ylamino]phenol such as Irganox 565 (a product of Ciba-Geigy); and 4,6- bis(octylthiomethyl)-o-cresol such as Irganox 1520 (a product of Ciba-Geigy). Examples of a light stabilizer of a benzoate type are 2,4-di-tert-butylphenyl 3,5-di- tert-butyl-4-hydroxybenzoate such as Tinuvin 120 (a product of Ciba-Geigy) and the like. An amount of the stabilizer to the base material in the layer containing the fluorescent material is usually not less than 1% by weight or, preferably, not less than 3% by weight and usually not more than 15% by weight or, preferably, not more than 10% by weight. Examples of a method for the formation of each of the layers constituting the ultraviolet block layer on a substrate are gravure coating, reverse gravure coating, roll coating, etc. wherein a solution containing a base material and ultraviolet block materials and/or others for constituting each layer is applied and dried. Each of the layers constituting the ultraviolet block layer may contain lubricant, particles, surfactant, etc. When the material to be layered is a printed image by a dye sublimation or dye diffusion thermal transfer or a wax type thermal transfer, the ulfraviolet block layer may be placed in such a successive manner with the color material layers on the surface of a color sheet as shown in Figure 4. Examples of the material to be layered with an ultraviolet block layer or a whole ulfraviolet block material of the present invention are images such as painting, inkjet printed image, dye sublimation or dye diffusion thermal transfer printed image, wax type thermal transfer printed image and electronic photographic image; glass and fransparent plate, such as glass part of picture frame, window glass for cars and homes, showcase and food case; and fluorescent lamp and sleeve for fluorescent lamp. When the ulfraviolet block material of the present invention is layered on various kinds of glass and transparent plate, ultraviolet light does not reach inside them and, therefore, when it is used for a picture frame for example, it is possible to prevent color fading, discoloration, decolorization, etc. of paintings, letters, etc. in the picture frame. A fluorescent lamp generates ultraviolet light besides the visible light. Insects such as moths have a habit of being attracted by ultraviolet light and, therefore, when the ulfraviolet block material of the present invention is layered on window glass, fluorescent lamp or sleeve for fluorescent lamp, it is possible to prevent swarming of the insects. Although there is no particular limitation for a method of adhering the ultraviolet block layer or the whole ultraviolet block material of the present invention to a material to be layered, it is prefened to adhere by means of heating or pressurization when the material to be layered is image or particularly when it is inkjet printed image, dye sublimation thermal transfer printed image, dye diffusion thermal transfer printed image, wax type thermal transfer printed image, electronic picture image, etc. When the ultraviolet block layer is to be placed in such a successive manner with the color material layers on the surface of a color sheet in the case of a thermal transfer print, it is prefened that adhesion is carried out by means of heating. With regard to a means for heating, it may be carried out by a thennal head in a printer, or by hot plate, hot roll, iron, etc. Examples of the pressurizing means are a pressurizing roll, a pressuring plate, etc. EXAMPLES In the following Examples, Acriloid A21 (an acrylate resin solution; manufactured by Rohm & Haas; a 30% solution), Bilon 103 (saturated polyester resin; manufactured by Toray), PKHC (phenoxy resin; manufactured by Phenoxy Specialties, Rock Hill, SC), Tinuvin 328 (ultraviolet radiation absorber; a product of Ciba-Geigy), Uvitex OB (fluorescent material; a product of Ciba-Geigy), Irganox 1076 (antioxidant of a hindered phenol type; manufactured by a product of Ciba-Geigy), Tinuvin 120 (stabilizer of a benzoate type; a product of Ciba-Geigy), 2,2'-dihydroxy-4,4'-dimethoxybenzophenone (ultraviolet radiation absorber of a benzophenone type; hereinafter, abbreviated as "DHDMOBF"), Fluorad FC-430 (surfactant of a fluorine type; a product of 3M), acetylacetone and a mixed solvent (tolune/ 2-butanone = 1/1) were used. EXAMPLES 1-4 and COMPARATIVE EXAMPLES 1 and 2 A polyethylene terephthalate film (thickness: 12 μm) having a releasing layer on one side was used as a substrate and an application solution as shown in Table 1 was applied on the releasing layer using a Meyer bar. After being applied, it was dried at 120°C for 1 minute to form an ulfraviolet block layer having a thickness of 2 μm on the substrate. The light transmittance spectrum of the ultraviolet block material was measured by a specfrophotometer U-3500 manufactured by Hitachi. The result is shown in Figure 1(b). Table 1 (In the Table, figures indicate parts by weight) EXAMPLES 5-17 and COMPARATIVE EXAMPLE 3 Application solutions were prepared according to the compositions as shown in Table 2. The solution was applied using a Meyer bar on a releasing layer of a polyethylene terephthalate film (thickness: 12 μm) having a releasing layer on one side as a subsfrate so as to give layer constitution as shown in Table 3. After being applied, it was dried at 120°C for 1 minute to prepare an ultraviolet block material. In Examples 6 and 10-17, the application solution was applied on a subsfrate and dried to form an ulfraviolet block layer. Another application solution was applied on a releasing layer of a polyethylene terephthalate film (hereinafter, refened to as PET) comprising the same materials as the subsfrate and dried to form an ulfraviolet block layer. The ultraviolet block layer on the substrate and the ultraviolet block layer on the PET were piled in a state of contacting each other so as to give the layer constitution as shown in Table 3 and preliminarily provided on an image-receiving layer surface of the image-receiving paper of a video print set (VW-APKC 36) for a printer (NV-AP-1) manufactured by Matsushita Electric Industrial), and its four corners were fixed by an adhesive tape so as not to slip off. After that, a transparent polyethylene terephthalate film (thickness: 4.5 μm) having a heat-resisting slipping layer on one side and having no color material layer on another side was prepared, and a marker similar to a color sheet of VW-APKC 36 was formed thereon followed by winding on a bobbin of a color sheet of VW-APKC 36. The color sheet was installed in a color sheet cassette of VW-APKC 36 and then installed in a printer (NV-AP-1). In the meanwhile, the above-piled product of the image-receiving paper and the ultraviolet block material was provided in a paper cassette and the highest energy was applied to the thermal head to heat the whole surface so that they were adhered to each other. After heating, the ultraviolet block material of the present invention was obtained by taking it out from the image-receiving paper on which it was preliminarily placed. Incidentally, although the ultraviolet block layer of the present invention contacted the dye-receiving layer of the image-receiving paper upon heating, an adhesive layer was not provided on the outermost layer of the ulfraviolet block layer and, therefore, it did not happen that the ulfraviolet block layer adhered to the dye-receiving layer. The ultraviolet radiation block material prepared as such was subjected to a light inadiation test from a xenon lamp using a Ci-4000 weather-o-meter manufactured by Atlas. The inadiation condition was that the inadiated light intensity at 340 nm was 0.55 w/m 2 and the inadiating time was 40 hours. The transmittance spectra of each sample before and after the light inadiation test from xenon lamp were measured by a specfrophotometer U-3500 manufactured by Hitachi. Result of the transmittance spectrum after the inadiation test with a xenon lamp is shown under the column of "light stability" in Table 2. Incidentally, the light stability was judged according to the following criteria on the basis of the transmittance spectrum of each sample: very good: transmittance of the light of 380 nm was 5% or less good: transmittance of the light of 380 nm was more than 5% and up to 10% durable: transmittance of the light of 380 nm was more than 10% and up to 20% no good: transmittance of the light of 380 nm was more than 20%. In the meanwhile, result of the transmittance spectrum before the light inadiation from a xenon lamp was "very good" for all of Examples 1-13 and Comparative Example 1. Table 2 (Figures in the Table indicate part(s) by weight) Table 3 EXAMPLES 18-22 and COMPARATIVE EXAMPLE 4 The ulfraviolet block material of the present invention was adhered onto the image and the light stability of the image was compared. The ulfraviolet block material was prepared by the same manner as in Example 1 so as to give the layer constitution as shown in Table 4. In the case of a layered product where the ulfraviolet block layer comprises plural application solutions, the layer nearest the substrate was applied and dried, and then the next layer was applied and dried, whereupon the ultraviolet block layer was formed. In the meanwhile, black (gray), having an optical density of about 1, was printed using a printer NV-AP-1, and a video printing set VW-APKC 36 for the said printer manufactured by Matsushita Electric Industrial. Then the printed image of this printed thing was piled to contact the ultraviolet block layer which was provided in a releasable manner in the ultraviolet block material on the substrate and set in the printer, and the whole surface was heated by a thermal head from the back of the color sheet using a color sheet of the video printing set. Since the substrate of the ulfraviolet block material was thermally fused to the color sheet, the substrate was separated from the image-receiving layer simultaneously with the completion of the heating and only the ultraviolet block layer was layered on the image. The image protected by the ultraviolet block layer prepared as such was subjected to a test of light inadiation from a xenon lamp using a Ci-4000 weather-o-meter manufactured by Atlas under the same condition as in Example 1. The image before and after the light inadiation test was measured by a colorimeter of a Spectroloni type manufactured by Gretag to determine the hue change (ΔE). The result is shown in Table 4. The smaller the ΔE, the smaller the hue change and the better the light stability of the image. In Comparative Example 4, the hue change was measured without layering an ultraviolet block layer on the image. Table 4 Obviously, numerous variations of the present invention are possible in light of the above teachings. It is therefore to be understood that within the scope of the appended claims, the invention may be practiced otherwise than as specifically described herein.

Claims: What is claimed is: 1. An ultraviolet block material, characterized in that, a fransmittance for the light within a wavelength range of 300-380 nm is 10% or less and a fransmittance for the light within a wavelength range of 420-800 nm is 90% or more. 2. The ultraviolet block material according to claim 1, wherein a fransmittance for the light within a wavelength range of 300-390 nm is 10% or less. 3. The ulfraviolet block material according to claim 1, wherein a fransmittance for the light within a wavelength range of 300-400 nm is 10% or less. 4. The ulfraviolet block material according to claim 1, wherein the ultraviolet block material contains an ulfraviolet radiation absorber and a fluorescent material. 5. The ultraviolet block material according to claim 4, wherein the ultraviolet radiation absorber is contained in an amount of 5-30% by weight to the base material. 6. The ulfraviolet block material according to claim 4, wherein the fluorescent material is contained in an amount of 5-30% by weight to the base material. 7. The ulfraviolet block material according to claim 1, wherein the ultraviolet block material has a substrate and an ultraviolet block layer provided on the subsfrate in a releasable manner. 8. The ulfraviolet block material according to claim 7, wherein the ulfraviolet block layer has a layer containing a fluorescent material, the layer having the fluorescent material has at least one layer between it and the subsfrate and also has at least one layer on the side, opposite to the substrate, of the layer containing the fluorescent material and any of the layers has an ultraviolet radiation absorber. 9. The ultraviolet block material according to claim 8, wherein at least one of the layers existing between the subsfrate and the layer containing the fluorescent material contains an ulfraviolet radiation absorber. 10. The ultraviolet block material according to claim 8, wherein the layer containing the fluorescent material contains an ultraviolet radiation absorber. 11. The ulfraviolet block material according to claim 8, wherein at least one layer between the substrate and the layer containing the fluorescent material and the layer containing the fluorescent material has an ultraviolet radiation absorber. 12. The ulfraviolet block material according to claim 7, wherein the ultraviolet block layer has a layer containing a fluorescent material and the layer containing the fluorescent material contains an ultraviolet radiation absorber and a stabilizer. 13. The ultraviolet block material according to claim 12, wherein the ultraviolet block layer has at least one layer between the substrate and the layer containing the fluorescent material. 14. The ultraviolet block material according to claim 12, wherein the ulfraviolet block layer has at least one layer on the side, opposite to the substrate, of the layer containing the fluorescent material. 15. The ultraviolet block material according to claim 12, wherein ulfraviolet block layer has at least one layer between the substrate and the layer containing the fluorescent material and also has at least one layer on the side, opposite to the subsfrate, of the layer containing the fluorescent material. 16. The ulfraviolet block material according to claim 13, wherein the at least one of the layers existing between the substrate and the layer containing the fluorescent material contains an ultraviolet radiation absorber. 17. The ultraviolet block material according to claim 7, wherein the ultraviolet block layer has a layer containing a fluorescent material and at least one layer containing an ultraviolet radiation absorber between the subsfrate and the layer containing the fluorescent material and the layer containing the fluorescent material contains a stabilizer. 18. The ultraviolet block material according to claim 17, wherein the ultraviolet block layer has at least one layer on the side, opposite to the substrate, of the layer containing the fluorescent material. 19. The ultraviolet block material according to claim 14, wherein the farthest layer from the substrate among the layers provided on the side, opposite to the subsfrate, of the layer containing the fluorescent material is an adhesive layer showing tackiness by means of heating or pressurization. 20. The. ultraviolet block material according to claim 7, wherein the farthest layer from the substrate in the ultraviolet block layer is a layer which receives color materials. 21. The ultraviolet block material according to claim 1, wherein the ultraviolet block material has a subsfrate and an ultraviolet block layer adhered on the substrate. 22. The ultraviolet block material according to claim 21, wherein the ulfraviolet block layer has a layer containing a fluorescent material and has at least one layer on the side, opposite to the substrate, of the layer containing the fluorescent material and any of the layers contains an ultraviolet radiation absorber. 23. The ultraviolet block material according to claim 22, wherein the layer containing the fluorescent material contains an ulfraviolet radiation absorber. 24. The ultraviolet block material according to claim 22, wherein there is at least one layer between the substrate and the layer containing a fluorescent material. 25. The ultraviolet block material according to claim 24, wherein the at least one layer between the substrate and the layer containing the fluorescent material contains an ulfraviolet radiation absorber. 26. The ultraviolet block material according to claim 24, wherein the layer containing the fluorescent layer and at least one layer between the subsfrate and the layer containing the fluorescent material contains an ultraviolet radiation absorber. 27. The ultraviolet block material according to claim 21, wherein the ultraviolet block layer has a layer containing a fluorescent material and the layer contaimng the fluorescent material contains an ultraviolet radiation absorber and a stabilizer. 28. The ultraviolet block material according to claim 27, wherein the ulfraviolet block layer has at least one layer between the substrate and the layer containing the fluorescent material. 29. The ultraviolet block material according to claim 27, wherein the fluorescent block layer has at least one layer on the side, opposite to the substrate, of the layer containing the fluorescent material. 30. The ulfraviolet block material according to claim 27, wherein the ulfraviolet block layer has at least one layer between the substrate and the layer containing the fluorescent material and also has at least one layer on the side, opposite to the substrate, of the layer containing the fluorescent material. 31. The ultraviolet block material accordmg to claim 28, wherein at least one of the layers existing between the substrate and the layer contaimng the fluorescent material contains an ultraviolet radiation absorber. 32. The ulfraviolet block material according to claim 21, wherein the ultraviolet block layer has a layer containing a fluorescent material and also at least one layer between the substrate and the layer containing the fluorescent material and the layer contaimng the fluorescent material contains a stabilizer. 33. The ulfraviolet block material according to claim 32, wherein the ultraviolet block layer has at least one layer on the side, opposite to the subsfrate, of the layer containing the fluorescent material 34. The ultraviolet block material according to claim 21, wherein there is an abrasion-resisting layer on the side, opposite to the ulfraviolet block layer, of the substrate. 35. The ultraviolet block material according to claim 29, wherein the farthest layer from the substrate among the layers provided on the side, opposite to the subsfrate, of the layer containing the fluorescent material is an adhesive layer showing a tackiness by means of heating or pressurization. 36. The ulfraviolet block material according to claim 21, wherein the farthest layer from the substrate of the ulfraviolet block layer or the side, opposite to the ulfraviolet block layer, of the subsfrate is a layer which receives color materials. 37. A method for the protection of a material to be transfened, characterized in that, there are included steps where the farthest side from the substrate of the ultraviolet block layer of the ulfraviolet block material mentioned in claim 7 is layered to contact the material to be transfened and then the substrate is separated from the ultraviolet block layer. 38. The method for the protection according to claim 37, wherein image is formed by an inkjet recording system or a thermal transfer printing system on the surface of the material to be transfened with the ultraviolet block layer of the ulfraviolet block material. 39. A method for the protection of the material to be layered, characterized in that, the farthest side of the ultraviolet block layer of the ulfraviolet block material mentioned in claim 21 from the subsfrate is adhered to contact the material to be layered. 40. The method for the protection according to claim 39, wherein image is formed by an inkjet recording system or a thermal transfer printing system on the surface of the material to be layered with the ultraviolet block material. 41. A method for the protection from ultraviolet light, characterized in that, there are included the steps where image is formed on the color material-receiving layer of the ulfraviolet block material mentioned in claim 20, then a substrate paper is layered on the color material-receiving layer and the substrate is separated from the ulfraviolet block layer. 42. A method for the protection of a material to be adhered, characterized in that, image is formed on a color material-receiving layer of the ultraviolet block material mentioned in claim 36 and then a substrate paper is layered on the color material- receiving layer. 43. A material being protected from ultraviolet light, which is prepared by a method ofclaim 37. 44. An ultraviolet block material having a substrate and an ultraviolet block layer provided on the substrate in a releasable manner, the ultraviolet block material which is characterized in that, in the said ultraviolet block layer, the transmittance of the light within a range of 300-380 nm wavelength is 10% or less and the transmittance of the light within a range of 420-800 nm wavelength is 90% or more. 45. A method for the protection of a material to be transfened, characterized in that, the said method includes the steps that the farthest side of the ultraviolet block layer in the ultraviolet block material mentioned in claim 44 from the substrate is layered to contact the material to be transfened and then the substrate is separated from the ultraviolet block layer. 46. A material which is protected from ultraviolet light, characterized in that, the ultraviolet block layer of the ulfraviolet block material mentioned in claim 44 is layered onto the material to be transfened. 47. An ulfraviolet absorbing coating composition comprising a resin system selected from the group consisting of phenoxy resins and acrylic resins, approximately 20% by volume of resin solids, ulfraviolet filter materials selected from the group consisting of benzotriazoles and benzophenones, 2.5% to 8.5%> of volume of resin solids; and an evaporable vehicle to make 100%. 48. A composition in accordance with claim 47, including a melamine crosslinking material up to 6% of total volume of resin solids. 49. In the manufacture of a light emitting device including a glass envelope, the step of coating a surface of said envelope with an ultraviolet light-absorbing coating including a resin selected from the group consisting of phenoxy resins and acrylic resins, and an ultraviolet filter material selected from the group consisting of benzotriazoles and benzophenones. 50. An ultraviolet radiation-absorbing coating composition comprising a resin system selected from the group consisting of phenoxy resins, acrylic resins, and melamine resins ranging from 10% to 40% of resin solids; an ulfraviolet absorption material selected from the group consisting of benzotriazoles and benzophenones ranging from 0.2% to 10% of resin solids; an optical brightener material ranging from 1% to 6% of resin solids, and an evaporable vehicle to make 100%. 51. The coating composition set forth in claim 50, including: P-toluene sulfuric acid catalyst - range 0.01%-0.3% of resin solids. 52. The coating composition set forth in claim 50, in accordance with the following formulation, with proportions based upon resin solids, including an optical brightener: Resin solids - range 20% -50% P-toluene sulfuric acid catalyst - range 0.01%-0.3% Optical brightener - range l%-8% Ultraviolet absorber - range 0.1% - 4%. 53. The coating composition set forth in claim 50, in accordance with the following formulation, with proportions based upon resin solids, including an optical brightener: GR 150 at 15% solids Methyl isobutyl ketone/toluene to make 100% Optical brightener 19% based on resin solids Mix and slip compound 0.08% based on resin solids Acetylacetone 8% of total weight. 54. The coating composition set forth in claim 50, in accordance with the following formulation, with proportions based upon resin solids, including an optical brightener: GR 908 at 15% solids Methyl isobutyl ketone/toluene to make 100% Optical brightener 19% based on resin solids Mix and slip compound 0.08% based on resin solids Acetylacetone 8% of total weight. 55. An ulfraviolet radiation absorbing coating composition for use with a high temperature light source comprising: a polysiloxane resin system, and an optical brightener of approximately nineteen percent of the resin solids. 56. A coating composition in accordance with claim 55, further comprising methyl isobutyl ketone, toluene, and acetylethylacetone as an optical brightener dispersant. 57. An ulfraviolet radiation absorbing coating system comprising a first synthetic resinous layer having an ulfraviolet radiation absorber with an ultraviolet cutoff lower than about 385 nanometers, and a fluorescent material which reflects ulfraviolet radiation of wavelength above 385 nanometers; and a second layer overlying said first layer and having an ulfraviolet radiation absorbent material wliich blocks at least some ulfraviolet radiation affecting the fluorescent material. 58. A coating system in accordance with claim 57, in which said second layer is comprised of a polysiloxane material. 59. A coating system in accordance with claim 57, in which said first and second layers are applied to opposite surfaces of a polyester film. 60. A system in accordance with claim 57, in which said first and second layers are applied to oppositely disposed surfaces of a synthetic resinous film. 61. A system in accordance with claim 60, in which said film includes an adhesive for application to a printed surface of a protected substrate. 62. An ulfraviolet absorbing coating system in accordance with claim 57, including first and second inner and outer coatings of the following formulation, parts are by weight of solids: Inner Coating: Acryloid A 21 - (Rohm & Haas) 25% (solids) Uvitex OB - (Ciba-Geigy Corp.) 11 % based on solids Tinuvin 328 - (Ciba-Geigy Corp.) 8% based on solids Acetylaetone 8% based on total weight Diluent toluene or xylene - depending upon method of application; Outer Coating: GR 653 polysiloxane coating - (Techneglas) 97.5 parts Tinuvin 328 - (Ciba-Geiby Corp.) 1.5% based on GR653 solids Toluene - 1% based on total weight. 63. An ultraviolet absorbing coating system in accordance with claim 57, including first and second inner and outer coatings of the following formulation: Inside Layer - Urethane: Desmodur N-75: Bayer 36% of urethane solids Desmophen 670A-80:Bayer 64%) of urethane solids Catalyst, dibutyltindilaurate: 0.1% based on urethane solids Tinuvin 328 - (Ciba-Geigy) 8% based on urethane solids Tinuvin OB - (Ciba-Geigy) 11 %> based on urethane solids Flurad 430 - (3M) 0.1% based on urethane solids Diluent, Toluene to make 100%; Outer Layer - Acrylic: Acryloid A-21 - (Rohm & Haas) received at 30% solids, diluted to 25% solids with toluene Flurad 430 (3M) 0.1% based on total coating Tinuvin 328 - (Ciba-Geigy) 8% based on A-21 solids Tinuvin OB - (Ciba-Geigy) 11%, based on A-21 solids Acetylacetone 8% of total weight. 64. An ulfraviolet absorbing coating system in accordance with claim 57, said first and second coatings having the following formulation, percentages based on resin solids: Polysiloxane Outer Coating: SHC 4000 (General Electric) 98.4% [or 98.2% as in Claim 8] Tinuvin-328 (Ciba-Geigy) 1.5% Triethanolamine 0.01% Toluene for appropriate coating thickness; Acrylic Inner Layer: Joncryl 537 - (Johnson's Wax) Aqueous acrylic dispersion Uvinul D40 - (BASF-Wyandotte) 8% based on resin solids [or 1.5% as in claim 8] Flurad 430 - (3M) 0.1% based on resin solids Triethanolamine O.P/o based on resin solids OB A Quencher - (Kalamazoo Chemical Corp.) 0.1% based on resin solid.

Inventors: CORNELIUS LESTER E, TORII TOSHINORI, CORNELIUS, LESTER, E., TORII, TOSHINORI
Applicants: CORNELIUS LESTER E, TORII TOSHINORI, CORNELIUS, LESTER, E., TORII, TOSHINORI
Application year: 2001
Main classification: F21V9
IPC codes: B32B7, C08J5, C09D5, C09D7, C09D201, C09K3, G02B5, G02F1