Catalytic promoters for the catalytic cracking of hydrocarbons

Abstract: Disclosed is a catalytic promoter for fluid catalytic cracking of hydrocarbons, comprising a HZSM-5 zeolite in an amount of 5-65 wt% based on the total weight of the catalytic promoter, said zeolite being modified with Zn and at least one element selected from the group consisting of P, Ga, Al, Ni and rare earth elements, the combined amount of said modifying elements being 0.01-10.37 wt% based on total weight of said modified HZSM-5 zeolite. A reduced olefin content in gasoline from catalytic cracking process, an increased gasoline octane number and an increased lower olefin yield can be obtained using said catalytic promoter.

Description: The present invention relates to a catalytic promoter used in the process of fluid catalytic cracking of hydrocarbons in petroleum refining field. More particularly, it relates to a catalytic promoter used in the process of fluid catalytic cracking of hydrocarbons to reduce olefin content in gasoline from catalytic cracking process, and to the preparation thereof. Gasoline octane number is one of the most important indexes to evaluate motor gasoline. The operating conditions comprising short contact time at an elevated temperature in the presence of an ultrastable zeolite catalyst are now generally employed in a unit for catalytic cracking in a refinery in order to increase gasoline octane number. Such a technique, however, results in increased olefins in gasoline from catalytic cracking process. Olefins in gasoline constitute the major reason for the high amount of contaminants from automobile exhaust emissions. It is necessary to reduce the olefin content in gasoline to meet environmental requirements. Thus, there's a great need to reduce olefin content in catalytically cracked products - gasoline, and meanwhile to increase or maintain gasoline octane number. The use of catalytic cracking catalysts containing high silica zeolite, ZSM-5, to increase gasoline octane number, is well known to one skilled in the art see, for example US 5,961,818 and GB 2,345,293. As disclosed in the art, a ZSM-5 zeolite can be incorporated into a catalytic cracking catalyst as one of the active components. Alternatively, the ZSM-5 zeolite as a single active component can be made into an additive catalyst which is then added to a unit for catalytic cracking in combination with a conventional catalytic cracking catalyst. The amount of the ZSM-5 zeolite added can vary widely; it can be either as little as 0.01-1wt% or as much as 5-10wt% or even more, based on the total weight of the catalyst. The catalyst of US 5,961,818 contains modifying elements such as Na, K, Pt, Sn, Fe and Re. Such elements are alkaline and have a depressive effect on aromatisation reactions As disclosed in USP 4,929,337, a ZSM-5 zeolite modified with Ga is used as an active component for aromatisation. Alkanes and olefins are subjected to cracking/aromatisation by means of the shape selective cracking/aromatisation component. The shape selective aromatisation component converts alkanes and olefins to aromatic hydrocarbons. These catalysts, however, are mainly used in catalytic cracking to increase gasoline octane number, without an effect of reducing olefin content in gasoline. A process of catalytic cracking of heavy oils to increase gasoline octane number is disclosed in USP 4,867,863. A catalyst containing 0.5-5% HZSM-5 zeolite was used in the patent, with the result of an increased gasoline octane number. But the effect of reducing olefin content in gasoline was neither indicated. US 4,975,402 discloses an aromatisation catalyst comprising a HZSM-5 zeolite and a zinc oxide-alumina co-precipitate. The catalyst may be doped with Ni0 in an amount of.0.5 to 3wt% by co-precipitation and was found to produce greater yields of aromatics when contacted with an olefinic and/or paraffinic feedstock than the respective zeolite alone. WO 98/51409 discloses a catalyst comprising a ZSM-5 zeolite impregnated with zinc and at least one element selected from the group consisting of Group 4B, Group 6B, Group 3A, Group 4A and Group 5A of the periodic table. The catalyst can be used to convert paraffin hydrocarbons to olefins and aromatics with a low rate of coke formation. GB 2,345,293 A describes a catalyst comprising a ZSM-5 zeolite impregnated with zinc and lanthanum, either alone or in combination with cerium. The catalyst can be used to reduce the sulfur content of a catalytically cracked petroleum fraction. It is an object of the present invention to provide a catalytic promoter, which can not only reduce olefin content in gasoline but also increase gasoline octane number, at the same time, increase the yield of very useful industrial feedstock, lower olefins. It is another object of the present invention to provide a method for preparing said catalytic promoter. A first aspect of the invention provides a catalytic promoter for the catalytic cracking of hydrocarbons, comprising a HZSM-5 zeolite in an amount of 5-65 wt% based on the total weight of the catalytic promoter, said zeolite being modified with Zn,P and at least one rare earth element, the combined amount of said modifying elements being 0.01-10.37 wt% based on total weight of said modified HZSM-5 zeolite. The applicant also discovered that the most desirable results are achieved by utilizing the present catalytic promoter containing 23%-95.3% by weight of zinc based on the total weight of the modifying elements. The HZSM-5 zeolite used in this invention can be any of the commercially available products. The HZSM-5 zeolite with a SiO 2 /Al 2 O 3 ratio of preferably 20-500, more preferably 30-200, and most preferably 30-100, is highly preferred. ZSM type series zeolites whose representative is HZSM-5 are such a kind of zeolite that have high silica content and structure of three-dimensional crossed straight channel. They are characterized by lipophilicity, hydrophobicity and good thermostability etc. The majority of their pores are about 5.5A in size. The catalytic activity of ZSM type relies on the surface acidity resulting from acid sites therein. Most of acid sites are located in the cavaties of zeolites. ZSM type zeolites exhibit specific shape-selective catalysing as a result of the particular pore path structure in conjunction with acid sites. Different acid-catalyzed reactions require different strength of acidic sites. The strength of acidic sites has a direct effect on the selectivity of a reaction. It is necessary to suitably adjust the amount, strength and distribution of acidic sites in the zeolites in order to induce a desirable reaction. For such a purpose, to modify zeolites is one of the most effective methods. In present invention some elements are incorporated into zeolites to effect such modification. There are a wide variety of methods for incorporating some elements into zeolites, such as ion-exchange, impregnation and high temperature processing as disclosed in CN1,057,408A. The location where the incorporated element is in the zeolite, varies with the method employed, and has an influence on the properties of the zeolite. A second aspect of the invention provides a process for preparing a catalytic promoter according to the first aspect of the invention, comprising the following steps: 1) Modifying HZSM-5 zeolite, comprising impregnating a HZSM-5 zeolite with an aqueous solution containing compounds of said modifying elements at 10-60°C for 1-30 hours; drying the impregnated zeolite at 100-160°C for 1-8 hours and then calcinating it at 500-600°C for 1-8 hours; and pluverizing the resultant zeolite and collecting fine powders of particle size greater than 150 mesh American Standard Screen; 2) Mixing the resultant modified zeolite of step 1) with 15-60 wt% of a support and 10-40 wt% of a binder based on the total weight of said catalytic promoter; then slurrying and homogenizing the resultant mixture at a pH of between 2.5 and 4.8; spray drying the homogenized mixture, washing it with water and then drying it thereby to give the catalytic promoter. Said compound of a modifying element can be any of water soluble compounds such as halide and inorganic or organic acid salts of the modifying element, as long as the modifying element therein can deposit on the zeolites and bind thereto during impregnation. Chloride, nitrate and sulfate salts are preferred. The zeolite can be impregnated with different solutions containing compounds of different modifying elements simultaneously or separately. The concentration of the modifying element in an aqueous solution is determined by the content of modifying elements required in said zeolite. It is preferred to use at least one material selected from SiO 2 , Al 2 O 3 , ZnO 2 , P 2 O 5 , clay, diatomaceous earth or sepiolite or mixtures thereof as the support. At least one material selected from alumina sol, silica-alumina sol, aluminium phosphate sol or mixtures thereof is preferably used as the binder. The homogenized mixture is dried for about 4 hours to obtain the catalytic promoter products. The binder used can be the commercially available product. There are various methods for preparing said binder. For example, the alumina sol binder can be obtained by dissolving the aluminium metal in hydrochloric acid aqueous solution or by dissolving the pseudoboehmite in nitric acid or hydrochloric acid aqueous solution while heating. The alumina is present, in the sol of pH 2.0-3.5, in the range of 10-30wt%. See Examples 12-14 in CN1072201A for the preparation of silica-alumina sol binder. To be specific, 567g of 25% sulphuric acid solution is added to 120g of purified water. Then 0.19L of aluminium sulfate aqueous solution containing 90g/L Al 2 O 3 is added. The mixture is stirred well and cooled to below 10 °C. 2.36 L of water glass containing 124g/l SiO 2 (modulus 3.23-3.3) is added while stirring to obtain the silica-alumina sol. Aluminum phosphate sol can be made by neutralization method. Namely, an appropriate amount of water is added to 85% phosphoric acid. The solution is heated to about 110°C. Aluminum hydroxide solid powder (96% purity) is added slowly. The temperature is maintained above 100°C for one hour. The pH is adjusted to be about 1.4 to obtain the aluminium phosphate sol, which contains about 35% P 2 O 5 and about 8.5% Al 2 O 3 . The present catalytic promoters for the catalytic cracking of hydrocarbons are suitable to process of fluid catalytic cracking of hydrocarbons, in particular to the catalytic cracking of vacuum gas oils (VGO), atmospheric resid or VGO blended with vacuum resid. The present catalytic promoters can be employed in combination of various conventional catalysts for the fluid catalytic cracking of hydrocarbons. A third aspect of the invention provides the use of the catalytic promoter of the first aspect of the invention in catalytic cracking of hydrocarbons, wherein the added amount of said catalytic promoter is 1-15% based on catalyst inventory in catalytic cracking unit, i.e the combined weight of main catalyst and the catalytic promoters charged into the catalytic cracking unit. The present catalytic promoter product is used in the form of finely-divided powders, the bulk density of which being less than 1.0g/ml and the particle size distribution being as follows, thus producing a catalyst maintaining the fluid state during the reaction and regeneration process: 0-40 µm, not more than 20wt% 40-80 µm, not less than 55wt% > 80 µm, not more than 25wt% The present catalytic promoter can be blended with the main catalyst for catalytic cracking and then added to the reaction system through a feeding system connecting a catalyst storage tank. Alternatively, the present catalytic promoter can be added to the reaction system separately through a small catalyst feeding system. The addition of a small amount of the present catalytic promoter to a catalytic cracking unit under conventional catalytic cracking conditions can promote the cracking, hydrogen transfer and aromatisation of olefins in gasoline fraction as well as isomerization of hydrocarbons. Thus the advantages of the present invention compared with prior art lie in a reduced olefin content in gasoline from catalytic cracking, an increased gasoline octane number and an increase in the yield of lower olefins. The present catalytic promoter meets the use requirement of a conventional catalytic cracking process. Heavy oils could be employed as feedstock to produce high-quality gasoline and diesel oil together with a significant amount of liquefied petroleum gas under conventional catalytic cracking conditions. For example, said reaction is carried out at 480-540°C, preferably at 490-535°C, and more preferably at 500-530°C, for 0.5-20 seconds, preferably 0.75-15 seconds, and more preferably 1-7 seconds. Therefore, both reduced olefin content in gasoline and an increased gasoline octane number can be obtained from heavy oils such as atmospheric resid, vacuum resid or mixtures thereof. Accordingly, the quality of gasoline is improved, together with an increase in the yield of liquefied petroleum gas. The advantages of the present invention will become more apparent with reference to following examples, but these examples are not construed with limiting the present invention. The protection scope of the present invention is defined by the appended claims. All percentages or ratios used are by weight unless otherwise stated. Examples 1-5 illustrate the preparation of the modified zeolite in this invention. Examples 6-9 illustrate the preparation of formed catalytic promoter product in this invention. The performance experiments of the present catalytic promoter products are illustrated in Example 10. Example 1 1500g of HZSM-5 zeolite with a silica/alumina ratio of 60 under NKF series commercially available from The Catalyst Factory of Nankai University in Tianjin (the HZSM-5 zeolites used in the following Examples 2-5 are from such source), is impregnated with 4000 ml of 0.1M Zn(NO 3 ) 2 aqueous solution and 2000 ml of 0.6M Ga(NO 3 ) 2 aqueous solution separately. To complete each impregnation, the mixture is slurried by rapidly stirring at 40°C for 2 hours. The resulting slurry is filtered after each impregnation. The resulting filter cake is dried at 110°C for 2 hours, then calcined at 550°C for 3 hours prior to pulverization. The finely-divided powders greater than 150 mesh American Standard Screen are collected, which are referred to briefly as modified zeolite B, namely BMZSM-5, containing 1.73% Zn and 5.6% Ga. Example 2 This example is carried out as in Example 1, except that 1300 ml of a 0.6M mixed rare earth nitrate aqueous solution with a molar ratio of Ce/La/Nd=2 : 1 : 0.1 is used in place of the Ga(NO 3 ) 2 solution. The product obtained is referred to briefly as modified zeolite F, namely FMZSM-5, containing 2.6% Zn and 7.28% mixed rare earth. Example 3 This example is carried out as in Example 1, except that 4000 ml of a 0.1M Zn(NO 3 ) 2 aqueous solution, 50ml of a 0.1M mixed rare earth nitrate aqueous solution with a molar ratio of Ce/La/Nd=2:1:0.1 and a zeolite with a silica/alumina ratio of 50 are used instead. The product obtained is referred to briefly as modified zeolite I, namely IMZSM-5, containing 0.173% Zn and 0.05% mixed rare earth. Example 4 This example is carried out as in Example 1, except that 4000 ml of a 0.1M Zn(NO 3 ) 2 aqueous solution and 1000 ml of a 0.6M Ce 2 (SO 4 ) 3 aqueous solution are used instead. The product obtained is referred to briefly as modified zeolite L, namely LMZSM-5, containing 1.73% Zn and 5.5% Ce. Example 5 This example is carried out as in Example 1, except that 4000 ml of a 0.01M Zn(NO 3 ) 2 aqueous solution, 200 ml of a 0.1M Ce 2 (SO 4 ) 3 aqueous solution and a zeolite with a silica/alumina ration of 120 are used instead. The product obtained is referred to briefly as modified zeolite P, namely PMZSM-5, containing 0.173% Zn and 0.18% Ce. Example 6 1000 ml of distilled water and 90 ml of concentrated nitric acid are added into a 1500 ml round-bottom flask separately. The contents are stirred for 5 minutes. 200g of pseudoboehmite is weighed and added to the flask gradually. The termperature is maintained at 80-95°C while stirring 30 minutes. The slurry obtained is poured into a homogenizer. 860ml of clay slurry containing 25% clay is added, followed by addition of 85g of aluminium phosphate sol (pH 1, 35% P 2 O 5 ). The mixture is stirred for 5 minutes. 380g of PMZSM-5 zeolite is mixed with the above mixture. The resulting mixture is slurried and homogenized while the pH is controlled at 2.5-4.8. The homogenized product is sprayed drying, then washed with water, finally oven dried at 120°C for 4 hours to obtain a catalytic promoter product, called b, containing 49.3% by weight of PMZSM-5 and 3.9% by weight of P 2 O 5 based on the weight of the dried product. Example 7 980 ml of alumina sol (pH 3.01, 21% Al 2 O 3 ) is added to 1860 ml of clay slurry containing 25% clay to produce a mixture. To the mixture was added 105g of aluminium phosphate sol (pH1, 35% P 2 O 5 ). The resulting mixture was stirred for 30 minutes. Then 463.1g of IMZSM-5 zeolite is mixed in. The resulting mixture is slurried and homogenized while the pH is controlled at 2.5-4.8. The homogenized product is sprayed drying, then washed with water, finally oven dried at 120°C for 4 hours to obtain a catalytic promoter product, called c, containing 39.6% IMZSM-5 and 3.1% P 2 O 5 based on the weight of dried product. Example 8 1000 ml of distilled water and 90 ml of concentrated nitric acid are added into a 1500 ml round-bottom flask separately. The contents are stirred for 5 minutes. 200g of pseudoboehmite is weighed and added to the flask gradually. The temperature is maintained at 80-95°C while stirring 30 minutes. The slurry obtained is poured into a homogenizer. 860 ml of clay slurry containing 25% clay is added, followed by addition of 85g of aluminium phosphate sol (pH 1, 35% P 2 O 5 ). The mixture is stirred for 5 minutes. 105g of FMZSM-5 zeolite is mixed with the above mixture. The resulting mixture is slurried and homogenized while the pH is controlled at 2.5-4.8. The homogenized product is sprayed drying, then washed with water, finally oven dried at 120°C for 4 hours to obtain a catalytic promoter product, called e, containing 21.2% FMZSM-5 and 6% P 2 O 5 based on the weight of the dried product. Example 9 1000 ml of distilled water and 90 ml of concentrated nitric acid are added into a 1500 ml round-bottom flask separately. The contents are stirred for 5 minutes. 200g of pseudoboehmite is weighed and added to the flask gradually. The temperature is maintained at 80-95°C while stirring 30 minutes. The slurry obtained is poured into a homogenizer. 860 ml of clay slurry containing 25% clay is added, followed by addition of 58g of aluminium phosphate sol (pH 1, 35% P 2 O 5 ). The mixture is stirred for 5 minutes. 56g of LMZSM-5 zeolite is mixed with the above mixture. The resulting mixture is slurried and homogenized while the pH is controlled at 2.5-4.8. The homogenized product is sprayed drying, then washed with water, finally oven dried at 120°C for 4 hours to obtain a catalytic promoter product, called f, containing 12.8% LMZSM-5 and 4.6% P 2 O 5 based on the weight of the dried product. Example 10 A series of catalytic promoters are prepared by varying the types and amounts of modified zeolites. The experiment is carried out in a pilot plant, with a good result of reduced olefin content in gasoline. The reaction conditions employed in the experiment in a small-scale riser are as follows: Feedstock oil Vacuum gas oil from Shengli Oilfield + 15% vacuum resid Catalyst Ultrastable Y zeolite catalyst DVR-1 (manufactured by the Catalyst Factory of Qilu Petrochemical Corp.) Residence time of reaction stream 2.5-3.5 seconds Catalyst activity 61.1 Catalyst/oil ratio 6.5-6.7 Reaction temp. 510°C In the following table the "control" does not contain the present catalytic promoter, and "5%b" - "5%f" means 5% of one of the b, c, e and f catalytic promoters prepared in the Examples above based on the catalyst inventory in the unit. It can be seen from the results of comparative experiments that the olefin content in gasoline was decreased remarkably by 10.7-51.6% by the addition of 5%, based on the total loading weight of the catalyst charged into the unit, of the present b-c and e-f catalytic promoters to a conventional industrial catalyst for catalytic cracking of hydrocarbons. In addition, gasoline octane number (RON) and yield of propylene in liquefied petroleum gas were increased by 0.1-5.1% and 21.5-55.8% respectively. On the other hand, HZSM-5, which is not modified, couldn't reduce the olefin content in gasoline; instead, the olefin content therefrom was slightly increased.

Claims: A catalytic promotor for the catalytic cracking of hydrocarbons, comprising a HZSM-5 zeolite in an amount of 5-65 wt% based on the total weight of the catalytic promoter, said zeolite being modified with Zn,P and at least one rare earth element, the combined amount of said modifying elements being 0.01-10.37 wt% based on total weight of said modified HZSM-5 zeolite. The catalytic promoter according to claim 1, wherein the modifying elements are present in the HZSM-5 zeolite in an amount of 0.1-5.0 wt% based on the total weight of said modified HZSM-5 zeolite. The catalytic promoter according to claim 1, wherein said catalytic promoter comprises said HZSM-5 zeolite in an amount of 20-50 wt%. The catalytic promoter according to any one of claims 1-3, wherein the amount of zinc in said HZSM-5 zeolite is 23%-95.3 wt% based on the total weight of said modifying elements. The catalytic promoter according to any one of claims 1-3, further comprising at least one support selected from the group consisting of SiO 2 , Al 2 O 3 , ZrO 2 , P 2 O 5 , clay, diatomaceous earth or sepiolite or mixtures thereof in an amount of 15-60 wt%; and at least one binder selected from the group consisting of alumina sol, alumina-silica sol, aluminum phosphate sol or mixtures thereof in an amount of 10-40 wt%, based on the total weight of said catalytic promoter. The catalytic promoter according to claim 5, wherein said support is P 2 O 5 or ZrO 2 . The catalytic promoter according to claim 5 or claim 6 wherein said binder is aluminum phosphate sol, and said P element is incorporated into said catalytic promoter via the addition of said aluminum phosphate sol. The catalytic promoter according to claim 7, wherein pH value of said aluminum phosphate sol is from 2.0-3.5. A process for preparing a catalytic promoter according to any of claims 1-8, comprising the following steps: 1) Modifying HZSM-5.zeoiite, comprising impregnating a HZSM-5 zeolite with an aqueous solution containing compounds of said modifying elements at 10-60°C for 1-30 hours; drying the impregnated zeolite at 100-160°C for 1-8 hours and then calcinating it at 500-600°C for 1-8 hours; and pulverizing the resultant zeolite and collecting fine powders of particle size greater than 150 mesh American Standard Screen; 2) Mixing the resultant modified zeolite of step 1) with 15-60 wt% of a support and 10-40 wt% of a binder based on the total weight of said catalytic promoter; then slurrying and homogenizing the resultant mixture at a pH of between 2.5 and 4.8; spray drying the homogenized mixture, washing it with water and then drying it thereby to give the catalytic promoter. A process according to claim 9, characterised in that the support is selected from one or more of the group consisting of SiO 2 , Al 2 O 3 , ZrO 2 , P 2 O 5 , clay, diatomaceous earth or sepiolite or mixtures thereof in an amount of 15-60 wt%; and the binder is selected from one or more of the group consisting of alumina sol, alumina-silica sol, aluminum phosphate sol or mixtures thereof in an amount of 10-40 wt%, based on the total weight of said catalytic promoter. The use of the catalytic promoter of any one of claims 1-8 in catalytic cracking of hydrocarbons, wherein the added amount of said catalytic promoter is 1-15% based on catalyst inventory in catalytic cracking unit.

Inventors: GONG XUHUI, HAO DAIJUN, LIU DANHE, LIU JINLONG, WANG LONGYAN, WEI XIAOBO, GONG, XUHUI, HAO, DAIJUN, LIU, DANHE, LIU, JINLONG, WANG, LONGYAN, WEI, XIAOBO
Applicants: CHINA PETROCHEMICAL CORP, LUOYANG PETROCHEM ENG, CHINA PETRO-CHEMICAL CORPORATION, LUOYANG PETROCHEMICAL ENGINEERINGCORPORATION SINOPEC (LPEC)
Application year: 2001
Main classification: C10G11
IPC codes: B01J29, C10G11