OPTICAL WAVEGUIDES AND DEVICES INCLUDING SAME

Abstract: A photosensitive glass made of a ternary compound SiO2:SnO2:R2O where R is a Group I element such as Na, K or Li. The addition of an oxide of a Group I element increases the solubility of tin oxide in a silica matrix and produces a glass which is highly photosensitive and in which optically written refractive index modulations have remarkable temperature stability (solid circles) at least as good as that of the binary glass SiO2:SnO2 (open circles) and much superior to that of conventional germanosilicate glass (solid triangles) or borogermanosilicate glass (open triangles). The inclusion of the Group I oxide effectively increases the solubility of tin oxide in the non-crystalline silica matrix well above the 1 % limit of SiO2:SnO2 photosensitive glass, at which Sn would normally crystallise in the oxide. By contrast to boron or phosphorous co-dopants, the introduction of the Group I element does not appear to cause any increase in the background refractive index, allowing the manufacture of waveguide devices compatible with standard telecommunication fibres.

Description: TITLE OF THE INVENTION OPTICAL WAVEGUIDES AND DEVICES INCLUDING SAME BACKGROUND OF THE INVENTION The invention relates to optical waveguides comprising photosensitive glass, and to optical waveguide devices containing such glass, such as optical fibre gratings, optical fibre dispersion compensators, optical fibre sensors, optical fibre lasers and planar waveguide devices. Photosensitivity of glass materials (i.e. change in refractive index by exposure to optical radiation) is a fundamental property for the realisation of many optical devices. Typical glasses used for these applications are photosensitive to ultraviolet (UV) light. For example, Bragg gratings in optical fibres and planar waveguides have attracted much attention since their first demonstration. Bragg gratings are obtained by exposure of a waveguide made of photosensitive glass to a periodic light pattern. Such devices have many applications, such as sensors, dispersion compensators and laser mirrors. The definition of channel waveguides using UV writing on glass substrates, such as silica on silicon, is also becoming increasingly important for the realisation of multifunctional integrated optical components. Telecommunications optical fibres, i.e. Si0 fibres with a low content of Ge0 2 (~3%), show only relatively small refractive index changes when exposed to UV radiation. In addition, the UV photoinduced index change in standard germanosilicate waveguides is not sufficient for writing complex structures with a high degree of integration. With known photosensitive glasses, it is thus necessary to increase the photosensitivity of optical fibres or planar waveguides through post-fabrication methods and co-doping. Typical post-fabrication methods are hydrogen/deuterium loading and flame brushing. Typical co-dopants are B 2 0 , Sn0 2 and rare earth elements. Sn0 2 is used mainly as a codopant in germanosilicate, phosphosilicate and aluminosilicate glasses [see references 1,2,3,4]. Optical fibre with numerical apertures (NA) between 0.23 and 0.29 and refractive index modulations of ~10° can be produced in this way. Recently, optical fibres made from Sn0 :Si0 have been investigated [5]. Tin doped glass is also mentioned by other workers [6-8]). In reference [5], it has been shown that small concentrations (~0.15 mol %) of Sn0 in a silica network give permanent refractive index changes with a high degree of photorefractivity. Under similar UV irradiation conditions, the degree of photorefractivity is nearly two orders of magnitude higher than the concentrations of Ge0 2 required in Si0 :Ge0 fibres. Compared to the above-mentioned post-fabrication and co-doping techniques, the use of Sn0 2 has several potential attractions. It should keep the absorption low in the third telecom window at 1.5 μm. Processing is potentially less time consuming and potentially cheaper. However, in practice, preparation of Sn0 :Si0 2 glasses is limited by the low solubility of Sn which crystallises out of Sn0 at concentrations greater than about 1 mol %. Inclusion of Sn0 2 at higher concentration leads to a crystalline material which is not viable for realisation of devices with low optical loss. Although non-crystalline photosensitive silica glass with Sn0 concentrations of close to 1 mol% could potentially lead to the production of practical devices, the 1% solubility limit represents a major practical limitation, which limits the amount of photosensitivity (refractive index modulation) and the control of NA. Another problem with the production of Sn0 2 doped or co-doped fibre via modified chemical vapour deposition (MCVD) or solution doping techniques is related to the high volatility of Sn0 2 at the temperature required for preform collapse. This problem effectively prevents high Sn0 concentrations being incorporated into a fibre. An analogous problem can be expected to arise for other glass preparation processes. It is therefore an aim of the invention to provide a photosensitive glass for fabricating fibre-optic and planar waveguides that allows tin oxide to be incorporated in a silica matrix at concentrations above its normal solubility limit of 1 mol%, and -j - also that reduces the effects of high volatility during preform collapse or other glass preparation process. SUMMARY OF THE INVENTION It has been discovered that inclusion of a Group I element such as sodium in a tin-doped silica glass matrix provides a glass with highly desirable properties for use in waveguides, either made from optical fibres with the glass forming the core, or as part of a planar waveguide structure. Accordingly, the invention provides an optical waveguide having a waveguiding channel of photosensitive glass with a modified refractive index optically written therein, wherein the photosensitive glass comprises an oxide of sodium or another Group I element such as lithium or potassium in a matrix of silicon and tin oxides. The optical waveguide may be an optical fibre, with the waveguiding channel being formed by a core of the optical fibre comprising the photosensitive glass. The optical waveguide may also be a planar waveguide device comprising a layer of the photosensitive glass with a waveguiding channel optically written into the layer. Integrated planar waveguide structures may thus be fabricated by writing a channel network into the photosensitive glass layer. Inclusion of an oxide of a Group I element such as Na, Li or K can be used to increase the solubility of tin in the oxide up to 20 times above the 1 mol% limit of tin in the binary compound Si0 :Sn0 2 thereby allowing larger refractive index modulations to be achieved. In an embodiment of the invention, the glass comprises the oxides Si0 , Sn0 2 and Na 0. The inclusion of sodium oxide with silica and tin oxide has been shown to produce a photosensitive glass with a highly desirable combination of properties. A further advantage of inclusion of Na is that the effects related to high volatility of Sn during preform collapse are reduced. Moreover, refractive index modulations optically written into the Si0 2 :Sn0 :Na 2 0 glass have been shown to have remarkable temperature stability, much superior to conventional Si0 2 :Ge0 glasses. It has been shown that the temperature stability is at least as good as that of the binary photosensitive glass Si0 2 :Sn0 2 . Sodium oxide incorporation can thus be used to increase Sn concentration to increase intrinsic photosensitivity, while simultaneously providing a glass in which optically written refractive index modulations are highly stable. The introduction of sodium oxide also does not cause any significant change in the background refractive index. This contrasts with other dopants (e.g. Ge or P) which might be suitable for increasing the solubility limit of Sn but which increase the background refractive index of the silicate glass to a much greater degree. For example, in conventional germanosilicate glass the background refractive index increases by about 0.002 per mol% of Ge0 2 in Si0 2 (see reference 9). On the other hand, for sodium the increase is about 5 times less, being about 0.0004 per mol% for Na 2 O in SiO 2 . This is an important advantage for sodium, because, if the refractive index is too high, it is difficult or impossible to manufacture optical fibres or planar waveguides that are compatible with current telecom fibres. The photosensitive glass preferably comprises between about 1-20 mole % Sn0 2 and 1 -60 mole % R 2 0 (where R=Na, K or Li) to lie within the solubility limit in a generally silica matrix. The photosensitive glass may comprise at least one of: 2, 5 or 10 mole % Sn0 2 and/or at least one of: 2, 5, 10, 20, 30 or 40 mole % R 2 0. It will also be understood that the combination of tin and Group I oxides can be applied not only to pure silica glass, but also to silica doped with other elements, e.g. to germanosilicate glass, phosphosilicate glass or aluminosilicate glass, or combinations thereof. Additional rare earth dopants such as Er, Nd or Yb may also be included to provide gain. References to silica glass and a silica matrix are therefore to be construed as covering silica doped with other elements such as germanium, phosphorous or aluminium. Similarly references to a ternary compound are to be construed as inclusive of quaternary and higher order compounds. The photosensitive glass may be used for many device applications. Specifically, an optical fibre can be provided that has a core made of the photosensitive glass. A planar waveguide comprising the photosensitive glass can also be provided. There can also be provided an optical device having a gain medium comprising the photosensitive glass, for example a laser, optical amplifier or light emitter. To provide gain in the photosensitive glass, suitable dopants such as the rare earth elements Er, Nd, Yb may be included. Moreover, a grating structure may be written into the photosensitive glass, as is described further below in the specific description. Because of the remarkable stability of refractive index modulations optically written into the glass, devices made of the glass are more robust to intrinsic absorption, multi-photon absorption, high temperatures and other related effects which all tend to erase optically-written refractive index modulations. Consequently, the glass is especially attractive for applications such as high power lasers and amplifiers where residual absorption effects or multiphoton absorption are typically large and where significant temperature increases may arise during operation. Since the refractive index modulations can withstand such high operating temperatures, devices incorporating the glass can be run hotter and at higher intensities. In this way cooling requirements are less stringent and devices can be run at higher output levels. More generally, the high temperature stability is indicative of a high characteristic activation energy for the photoinduced refractive index changes, which are thought to originate from electron trapping effects. Consequently, even if device operating temperatures are kept low by cooling or pulsed operation, high power devices incorporating a modulated refractive index profile optically written into the glass are expected to demonstrate enhanced stability. For example, device reliability and operating life are expected to be improved. According to a further aspect of the invention there is provided an optical waveguide device comprising: an optical waveguide formed at least in part of photosensitive glass, wherein the photosensitive glass is doped with tin as a photosensitising dopant; and a refractive index variation optically impressed on the photosensitive glass of the optical waveguide; wherein the photosensitive glass is doped additionally with a Group I element as a dopant for increasing solubility of tin in the glass. According to another aspect of the invention there is provided a method of fabricating an optical waveguide, the method comprising: providing a photosensitive glass doped with tin as a photosensitising dopant and a Group I element as a dopant for increasing solubility of tin in the photosensitive glass; and exposing regions of the photosensitive glass to refractive index change inducing optical radiation, the exposed regions providing a light-guiding core of raised refractive index within the photosensitive glass. According to a still further aspect of the invention there is provided a process for increasing the sensitivity of optical glass to light-induced refractive index variations, the process comprising: doping the optical glass with tin as a photosensitising dopant in combination with a Group I element as a further dopant for incorporating increased amounts of tin in the optical glass, thereby to increase the sensitivity of the optical glass to light induced refractive index variation; and exposing regions of the optical glass to varying optical radiation to modulate the refractive index of the optical glass. BRIEF DESCRIPTION OF THE DRAWINGS For a better understanding of the invention and to show how the same may be carried into effect reference is now made by way of example to the accompanying drawings in which: Figure 1 shows refractive index modulation as a function of exposure time; Figure 2 shows the initial speed of refractive index modulation growth as a function of UV laser intensity in a glass according to an embodiment of the invention; Figure 3A shows temperature stability for gratings written in a glass according to an embodiment of the invention, and three further glasses, in terms of degradation of the amplitude of the gratings' refractive index modulation as temperature is increased; Figure 3B shows temperature stability for the grating according to the embodiment of the invention shown in Figure 3 A in terms of reflection response as temperature is increased; Figure 4 shows solubility limits in the ternary compound Sn0 :SiO?:R 0 for the examples of R=Li (curve 1), R=Na (curve 2) and R=K (curve 3); Figure 5 shows a schematic cross-section of an optical fibre with a core of photosensitive glass in which has been written a refractive index modulation; Figure 6 shows in elevation a planar waveguide structure optically written onto the surface of an epitaxial or bulk layer of photosensitive glass; Figure 7 shows in elevation a planar waveguide structure optically written into a layer of photosensitive glass sandwiched between a buffer layer and cap layer; Figure 8 shows an optical fibre laser with Bragg reflector cavity mirrors; Figure 9 shows a chirped grating; and Figure 10 shows an optical fibre sensor. DET AILED DESCRIPTION An optical fibre was produced by collapsing a Suprasil (TM) cladding onto a small cylindrical glass core rod while pulling. The core was produced by melting powders of Na?0, Si0 and SnO? in a Pt crucible at 1500 °C for 60 minutes. The glass was then consolidated at 1750 °C for 60 minutes. The molar composition of the powder used to produce the glass was: [Si0 2 ]=75%, [Sn0 2 ]=5%, [Na 2 O]=20%. The glass was then cast and drilled with an ultrasonic drill. The cylinder (1.5 mm diameter and 50 mm height) was cleaned in an ultrasonic bath and etched in hydrofluoric acid (HF) to reduce the surface roughness. The refractive index was measured with an Abbe refractometer and found to be n Na = l- 2. The cladding (a Suprasil tube with OD=34 mm and ID=1.6 mm) was collapsed onto the core at 2000 °C whilst pulling the fibre. The fibre had OD=74 μm and 2 nd mode cut-off at 1495 nm. A grating for reflectivity at -1.55 μm was written in the fibre using a pulsed KrF excimer laser (wavelength 248 nm) working at 30 Hz and a phase mask. Pulse duration and fluence were estimated to be 20 ns and 140 mJ/pulse*cm 2 . The grating length was approximately 2 mm. Figure 1 shows the increase of the refractive index modulation with exposure time in minutes. A saturation level is reached at 6.2* 10 " after 120 minutes exposure. Measurements at different intensities have been performed in order to understand whether the photosensitivity of this sample is driven by a one or two-photon absorption process. Figure 2 shows the initial growth of the refractive index modulation as a function of laser intensity, which appears linear and has a gradient of 1.1. This is evidence that the photorefractive effect of the glass is based on a one-photon process. Figure 3A shows the results of temperature stability studies made on gratings written into photosensitive glass of four different composition types. The plot is of the amplitude of the refractive index modulation against temperature in degrees Celsius. The refractive index modulation at the temperature concerned is normalised to the initial refractive index modulation at 20 °C before heating. The refractive index modulation was measured in each case during step heating. The samples were heated first to 205 °C and then to higher temperatures in steps of about 45 °C. Each temperature ramp took about 2 minutes and was followed by keeping the sample at a constant temperature for about 28 minutes, before increasing the temperature again with another step. The four examples are gratings written in the Na 2 0:Sn0 2 :Si0 2 glass (SSN2 - filled circles), in comparison to gratings written in the SiO?: Sn0 2 glasses of reference [5] (SS - open circles), and those written in germanosilicate glass Si0 :Ge0 (SG - filled triangles) and borogermanosilicate glass Si0 :Ge0 :B 2 θ 3 (SGB - open triangles). The enhanced stability of the gratings written into Sn0 2 :Si0 2 and Na 2 O:Sn0 2 :Si0 as compared to germanosilicate and borogermanosilicate is striking. (At this point it should be emphasised that the remarkable thermal properties of SnO?: SiO? binary glass is not known from reference [5], and is not believed to have been previously known elsewhere in the literature). Figure 3B shows the reflection response of the grating written into the Na 2 0:Sn0 2 :Si0 2 glass at various different temperatures, the response curves being measured at points shown in Figure 3A. In order of ascending peak wavelength (left- to-right in the figure), the response curves were taken at: 20 (A) , 205 (B), 343 (C), 484 (D), 580 (E), 681 (F), 767 (G), 852 (H), 895 (I) and 940 °C (J), the peak response wavelength increasing gradually from around 1546 nm. As can be seen, the grating was stable up to and including the 681 °C measurement (response F at 1552 nm), with the first degradation being discernible at 767 °C (response G). Fig. 4 is taken from reference [10] and shows the relation between the concentrations of the constituents in the ternary compounds Sn0 2 :Si0 2 :R 2 0 where R is Li (curve 1) Na (curve 2) or K (curve 3). The curves represent the approximate concentration limits for crystallisation. For all three Group I elements, the maximum concentration of Sn0 2 for non-crystalline material is shown to be around 20 mol%. Inclusion of the Group I elements thus allows up to 20 times more Sn to be incorporated in a non-crystalline silica matrix. The concentrations which can be achieved for the Group I elements range from minimum values of perhaps around 10 mol% to maximum values of about 40% for Li and 60% for Na and K. For Na a preferred concentration range is between about 10 and 60 mol%. It will be understood that this curves apply only for a pure silica matrix. Different curves will apply if, for example, a germanosilicate matrix is used. As described above, grating writing in ternary Siθ 2 :Sn0 2 :Na 2 0 fibre, achieving significant refractive index modulation, has been demonstrated. From measurements of absorption on Sn doped/co-doped silica, it is expected that in the ternary Si0 2 :Sn0 2 :Na 2 0 glass the absorption peak at around 250 nm will be situated at longer wavelengths compared to germanosilicate based glass. This could be useful for grating writing through a coating on an optical fibre (as the coatings are typically more transparent at longer UV wavelengths) and for using commercial laser sources (solid-state based) both via one-photon and two-photons processes. In the above embodiments, the fibre is produced using rod-in-tube techniques, rather than MCVD as in previous work. It is thought this may be helpful for achieving high Sn concentrations. However, MCVD remains an option for low loss fibres where Sn solubility is increased by using Na via solution doping. Although the above-described embodiment relates to UV writing of Bragg gratings in optical glass fibres and waveguides, the teachings herein may find general application for production of optical devices based on photosensitive glass where enhanced photorefractivity is required, for example in the definition of channel waveguides by UV writing. Some waveguide structures and devices incorporating such waveguides are now described with reference to Figures 5 to 10. Figure 5 shows in axial cross-section an optical fibre according to the above- described embodiment. The fibre comprises a core 20 of the photosensitive glass SnO 2 :Siθ 2 :Na 2 0 in which is optically written a grating structure 25. The core is surrounded by a clad 10. Figure 6 shows a planar waveguide structure 25 optically written into a layer 20 of the photosensitive glass Sn0 2 :Si0 2 :Na 2 0 with a writing beam, or lithographically. The photosensitive glass layer 20 is deposited on a silica substrate 5. The waveguiding channel is written into the photosensitive glass layer 20 by focusing a light beam onto the surface of the layer. Figure 7 shows a buried waveguide structure. A silica buffer layer 12 is deposited on a silicon substrate 5. A layer 22 of the photosensitive glass Sn0 2 :Si0 :Na 2 0 is deposited on the buffer layer 12 with a further silica capping layer 1 1 being deposited on the photosensitive glass layer 22. A waveguiding channel 25 is written into the photosensitive glass layer 22 by focusing a light beam 23 so that the beam focus or waist is coincident with the layer 22. Figure 8 is a schematic drawing of an optical fibre laser. A laser cavity is defined by first and second Bragg gratings 30 and 40 optically written into an optical fibre with a core of the photosensitive glass Sn0 2 :Si0 2 :Na 2 0, as described with reference to Figure 5. The gain medium 50 is also made of optical fibre, with the core being doped with Er or another suitable rare earth element such as Nd or Yb. The entire structure may be of a single fibre type, e.g. with a core of Er-doped Sn0 2 :Si0 2 :Na 0 glass. The photosensitive properties of the cavity core can then be utilised to fabricate a DFB (distributed feedback) laser. Alternatively, the Bragg gratings may be written into fibre sections with a core of Snθ 2 :Siθ 2 :Na 2 0, with a separate fibre section being provided for the cavity. The cavity section will include a gain-inducing dopant such as a rare earth element, but need not include any photosensitising dopants. In operation, a pump beam P is used to excite stimulated emission in the cavity to produce a laser output of wavelength λ L . Figure 9 shows a chirped fibre grating 60 with a core of the photosensitive glass Snθ 2 :Siθ 2 :Na 2 θ, as described with reference to Figure 5. The chirped grating may be used as a dispersion compensator in long-haul fibre communication. Figure 10 shows an optical fibre sensor. A plurality of Bragg gratings 74, 76, 78 having respective characteristic reflection wavelengths λι,λ 2 λ n are arranged separated along a section of fibre 80, one end of which is connected to a circulator 72. The fibre comprises a core of the photosensitive glass Sn0 2 :Siθ 2 :Na 2 θ into which the gratings are optically written. The circulator 72 is operable to route a probe light beam P from an input 70 through to the fibre section 80 and to route light reflected from the Bragg gratings to a further section of fibre 82 which leads to an output 77. Light from the output 77 is detected by a photodetector 75 and analysed to determine from which of the Bragg gratings the light was reflected. Spectroscopic or time resolution techniques may be used for the analysis. The device is used as a sensor by placing each of the Bragg gratings at different locations, each of which experiences a different physical environment. Pressure, temperature or strain may for example be measured in this way. REFERENCES 1. L. Dong. J.L. Cruz, L. Reekie, M.G. Xu. and D.N. Payne. IEEE Photonics Tech. Lett.7, 1048 (1995). 2. K. Imamura, T. Nakai, Y. Sudo and Y. Imada, Electronics Lett. 34. 1772 (1998). 3. L. Dong. J.L. Cruz, J.A. Tucknott, L. Reekie, and D.N. Payne, Optics Lett. 20, 1982 (1995). 4. WO 96/34304, Optical Waveguide Device', by Dong et al.. 5. G. Brambilla, V. Pruneri, and L. Reekie, Applied Phys. Lett. 76, 807 (2000). 6. JP 80267676 A. 'Soda lime-silica photosensitive glass and its production'. 7. WO 99/18042. "Light-induced refractive index changes in low temperature glasses'. 8. US 5,698.262, 'Method for forming tin oxide coating on glass'. 9. Bansal & Doremus "Handbook of Optical Glass Properties" Academic Press 1986 ISBN 0-12-078140-9 pages 163, 583 & 584 10. ON. Mazurin, M.V. Streltsina, T.P. Shvaiko-Shvaikovskaya, "Handbook of Glass Data Part C Ternary Silicate Glasses", Elsevier, 1985 - ISBN 0 -444- 42889-5 pages 581, 585, 592, 593 & 601.

Claims: CLAIMS 1. An optical waveguide having a waveguiding channel of photosensitive glass with a modified refractive index optically written therein, characterised in that the photosensitive glass comprises oxides of silicon, tin and at least one Group I element. 2. An optical fibre waveguide having a core of photosensitive glass with a modulated refractive index profile optically written therein, characterised in that the photosensitive glass of the core comprises oxides of silicon, tin and at least one Group I element. 3. A planar waveguide having a layer of photosensitive glass, the layer having at least one waveguiding channel of modified refractive index optically written therein, characterised in that the photosensitive glass of the layer comprises oxides of silicon, tin and at least one Group I element. 4. A waveguide according to claim 3, wherein the photosensitive glass layer is buried under a capping layer. 5. A waveguide according to any one of the preceding claims, including Na as the at least one Group I element. 6. A waveguide according to any one of the preceding claims, including K as the at least one Group I element. 7. A waveguide according to any one of the preceding claims, including Li as the at least one Group I element. 8. A waveguide according to any one of the preceding claims, wherein the photosensitive glass comprises at least: 2, 5 or 10 mole % Sn0 2 . 9. A waveguide according to any one of the preceding claims, wherein the photosensitive glass comprises Si0 2 , Sn0 2 and R2O where R is the at least one Group I element. 10. A waveguide according to claim 9, wherein the photosensitive glass comprises at least: 2, 5, 10, 20, 30 or 40 mole % R 2 0. 1 1. A waveguide according to claim 9, wherein the photosensitive glass comprises between about 1 -20 mole % Sn0 2 and 1 -60 mole % R 2 0. 12. A waveguide according to any one of the preceding claims, doped to provide a gain region. 13. A waveguide according to claim 12, wherein the gain region comprises a rare earth dopant. 14. A waveguide according to claim 13, wherein the rare earth dopant is at least one of Er, Nd and Yb. 15. A laser comprising a waveguide according to claim 14. 16. A laser according to claim 15, further comprising a pair of Bragg reflectors optically written into the photosensitive glass bounding at least a part of the gain region. 17. A laser according to claim 15, further comprising a pair of Bragg reflectors optically written into a further photosensitive glass bounding the gain region. 18. A grating comprising a waveguide according to any one of claims 1 to 14, the grating being defined by a modulated refractive index profile optically written into the photosensitive glass. 19. A dispersion compensator comprising a grating according to claim 18, the grating being a chirped grating. 20. A Bragg reflector comprising a grating according to claim 18. 21. A sensor comprising a plurality of Bragg reflectors according to claim 20 distributed along the waveguide, each Bragg reflector having a characteristic reflection response. 22. An optical waveguide device comprising: an optical waveguide formed at least in part of photosensitive glass, wherein the photosensitive glass is doped with tin as a photosensitising dopant; and a refractive index variation optically impressed on the photosensitive glass of the optical waveguide; wherein the photosensitive glass is doped additionally with a Group I element as a dopant for increasing solubility of tin in the glass. 23. A device according to claim 22, wherein the Group I element is sodium. 24. A method of fabricating an optical waveguide, the method comprising: providing a photosensitive glass doped with tin as a photosensitising dopant and a Group I element as a dopant for increasing solubility of tin in the photosensitive glass; and exposing regions of the photosensitive glass to refractive index change inducing optical radiation, the exposed regions providing a light-guiding core of raised refractive index within the photosensitive glass. 25. A method according to claim 24, wherein the Group I element is sodium. 26. A process for increasing the sensitivity of optical glass to light-induced refractive index variations, the process comprising: doping the optical glass with tin as a photosensitising dopant in combination with a Group I element as a further dopant for incorporating increased amounts of tin in the optical glass, thereby to increase the sensitivity of the optical glass to light induced refractive index variation; and exposing regions of the optical glass to varying optical radiation to modulate the refractive index of the optical glass. 27. A process according to claim 26, wherein the Group I element is sodium.

Inventors: BRAMBILLA GILBERTO, PRUNERI VALERIO, REEKIE LAURENCE, BRAMBILLA, GILBERTO, PRUNERI, VALERIO, REEKIE, LAURENCE
Applicants: BRAMBILLA GILBERTO, PRUNERI VALERIO, REEKIE LAURENCE, UNIV SOUTHAMPTON, BRAMBILLA, GILBERTO, PRUNERI, VALERIO, REEKIE, LAURENCE, UNIVERSITY OF SOUTHAMPTON
Application year: 2001
Main classification: C03C4
IPC codes: C03C3, C03C4, C03C13, G02B6, H01S3