ALLYL URETHANE RESIN COMPOSITIONS

Abstract: The present invention is for a new class of allyl urethane resin which can be cured with peroxide at high temperature alone or in combination with some accelerators. These allyl urethane resins can be used alone or in combination with other free radically polymerizable materials such as allyl monomers and oligomers or (meth)acrylate monomers and oligomers. These new allyl urethane resins contain at least two allyl functional groups.

Description: ALLYL URETHANE RESIN COMPOSITIONS This invention relates to novel isocyanate based allyl ether derivatives which may be cured using free radical initiators. Various polyurethane resins are well known for their coating and protective properties. Differing urethanes have different properties depending on the particular organic compounds used to form the urethanes. Similarly, the method of crosslinking in the urethane resin to form a cured product will vary with the starting materials for the urethanes. For instance, U.S. Patent No. 4,005,041 discloses polyurethane coating compositions with air drying and/or heat curable properties. The urethanes have allyl functionality and are polymers with aliphatic polyols as backbones . The urethanes are high in viscosity and relatively low in allyl functional groups, with air drying properties . U.S. Patent No. 4,829,123 relates to an air dryable resin composition. The composition contains one radical-curable resin which may be an unsaturated polyester resin or an acrylic based resin (urethane- acrylic, polyester-acrylic or epoxy-acrylic) along with a urethane-acrylic oligomer, an ethylenically unsaturated monomer and an initiator. U.S. Patent No. 5,763,099 relates to a binder composition for powder coatings. The low temperature-cure binder is a mixture of unsaturated polyester and an oligomer with 2-12 allyl ether groups having ester or urethane groups included. Preferably, the oligomer is an ester of trimethylolpropanediallylether and polycarboxylic acid (or anhydride) . U.S. Patent No. 5,739,251 to Venhan pertains to ethylenically unsaturated polyisocyanates which contain allophanate groups and have specific weight contents of isocyanate, β , y-ethylenically unsaturated ether groups and allophanate groups . The polyisocyanates are intended to be low viscosity materials for use in solvent- free, one- component coating compositions. The polyisocyanate is then used to make an ethylenically unsaturated polyurethane which is substantially free from isocyanate groups . This polyurethane is then combined with an acrylate material such as trimethylolpropanetriacrylate to produce a coating. U.S. Patent No. 4,005,041 pertains to a method for producing isocyanate adducts . The adducts contain residual isocyanate groups. The adducts are polyurethane coating compositions with air drying and/or heat curable properties . The adducts contain allyl functional groups and have aliphatic polyols as backbones. They are generally high in viscosity and low in allyl functional groups . U.S. Patent No. 5,198,528 to Smith et al . pertains to an alkane resin which is the polymerized product of trimethylolpropanediallylether, an aromatic acid, a drying compound and a polyol . The resin is generally used with a solvent such as mineral spirits. Absent the mineral spirits, the resin has a high viscosity. Therefore, it must be thinned with an appropriate solvent prior to use. U.S. Patent No. 4,031,271 pertains to a radiation curable, alkali resistant composition of a polyene and polythiol . The alkali resistance allows the cured composition to be used as a plating resist in the manufacture of electronic circuitry. U.S. Patent No. 4,433,179 pertains to a process for the preparation of allyl ethers. The allyl ethers are usable as monomers to be converted into crosslinked polymers or as starting materials for the preparation of epoxide compounds . U.S. Patent No. 4,614,761 to Takiama et al . pertains to a process for producing a curable resin having unsaturated groups and side chains through urethane linkages. The resin is produced by reacting a polymer having hydroxyl groups in the side chains with an unsaturated monoisocyanate . The monoisocyanate is obtained by reacting one mole of diisocyanate with one mole of an unsaturated monoalcohol. The polymer having side chain hydroxyl groups can be produced by copolymerizing a final monomer having hydroxyl groups and another vinyl monomer. Allyl alcohol is specifically disclosed as undesirable as the material for synthesizing the polymer because it does not serve to increase the molecular weight of the polymer. U.S. Patent No. 5,236,978 discloses a polymerizable organic resin of a polyol (allyl carbonate) and an aliphatic polyurethane having terminal allylic unsaturation. The resulting polymer has low yellowness and can be used to prepare photochromic articles such as lenses . The foregoing allyl functional resins are generally high molecular weight and high viscosity, which limit their applications and physical properties. Accordingly, there is a need to develop new allyl functional resins with low molecular weight and viscosity which will exhibit higher mobility and better surface cure. Such would be especially useful in coatings, adhesives and sealants. Furthermore, there is a continuing need to develop new resins which will possess different properties from those previously developed. Such new resins, while generally useful as coating compositions, will find applications for which they are specifically suited depending on the specific properties of the resin. A new class of curable allyl functional urethanes have now been developed. These urethanes are free radical-curable oligomer resins having the following formula : R x - [NHCO (OR) y (OCH 2 CH=CH 2 ) J n wherein y is 0 or 1, n is an integer from 2 to 20 or between 2 and 20, m is an integer from 1 to 5 or between 1 and 5, R is one of a (C^- C 10 ) alkyl, arylalkyl, alkenyl , in particular (C 2 -C 10 ) alkenyl, aryl, alkynyl , particularly (C 2 -C 10 ) alkynyl , (C 3 - C 10 ) cycloalkyl, (C 3 -C 10 ) cycloalkenyl, alkoxy, or oligoalkoxy with up to 3 alkoxy units, and R x is one of aryl , arylalkyl, (C 3 -C 10 ) cycloalkyl, (C 3 -C 10 ) cycloalkenyl or heterocyclic . In another embodiment, n is an integer from 2 to 4 or between 2 and 4 , is an integer from 1 to 3, R x is an aryl and R is selected from the group consisting of (C^-C^) alkyl , (C,-C 10 ) alkenyl, alkoxy or oligoalkoxqy with up to 3 alkoxy units . In one preferred embodiment, n = 2, m = 2, y = 1, χ = aryl and R is (C 1 - C 10 ) alkyl. A more specific example of the oligomer resin is the reaction product of isophorone diisocyanate and of allyl alcohol. Also set forth are free-radically curable oligomer resin compositions comprising at least one oligomer resin of the invention and a method for making a cured resin comprising reacting the oligomer compositions with a free radical initiator to cause crosslinking of the resins. The present invention also relates to a new class of allyl functional urethanes and processes for their preparation and use. The new oligomer resins are prepared by the reaction of hydroxyl-containing allyl functional materials with aliphatic, aromatic or cycloaliphatic isocyanates . The new compositions are soluble in typical aliphatic and aromatic solvents and are curable using free radical-based initiators. The compositions are also compatible with typical polymerized monomers and polymers such as unsaturated polyesters . The resins of the present invention are prepared through the reaction of hydroxyl-containing allyl materials with aliphatic or aromatic isocyanates . Preferably, the aliphatic or aromatic isocyanates include two or more isocyanate groups per molecule. As used herein, the term "aliphatic" refers to alkyl, alkenyl, alkynyl, cycloalkyl and cycloalkenyl groups, any of which may be sustituted with up to three halogen atoms . The term "heterocyclic" means an aryl group with one hetero- atom selected from O, N and S. Examples of isocyanates which are suitable for use in the present invention include isophorone diisocyanate, toluene diisocyanate, , 4 ' -dicyclohexylmethane diisocyanate, hexamethylene diisocyanate, 4 , 4 ' -methylene bis (phenyl isocyanate). Suitable isocyanates may also be dimers, trimers and polymers. Specifically, Desmodur™ N 100 and N 3200 (aliphatic polyisocyanate resins based on hexamethylene diisocyanate (HDI) ) , Desmodur™ N 3300 (a polyfunctional aliphatic isocyanate resin based on HDI) and Desmodur™ N 3400 (a polyfunctional aliphatic polyisocyanate resin based on HDI) all from Bayer Corp. are useful as isocyanates in the present invention. Desmodur is a trademark of Bayer Corporation of Pittsburgh, Pennsylvania, U.S.A. The hydroxyl-containing allyl functional materials can be monoallylethers or polyallylethers . These allyl functional materials may be substituted with alkyl groups, halogens, or other conservative substituents . However, substitutions must be well thought out. Hydroxyl groups can be substituents only to the extent that reactivity with the isocyanate component is desired and increasing the number of hydroxyl groups will change the proportions of allyl and isocyanate materials. Similarly, halogen substituents may be used. However, one method for making the hydroxyl containing allyl functional material used in the present invention is by reaction of an allyl halide and an alcohol. Using a halo- substituted allyl halide and alcohol would likely lead to undesirable products . Examples of hydroxyl containing allylethers useful in the present invention include allylalcohol, allylalcohol propoxylates (preferably with up to 3 propoxy units) , allylalcohol ethoxylates (preferably with up to 3 ethoxy units) , trimethylol propane diallylether, trimethylol propane monoallylether, glycerol diallylether, glycerol monoallylether, ethyleneglycol monoallylether, butanediol monoallylether and hexanediol monoallylether. Many of the hydroxyl-containing allylethers useful in the present invention are readily available from chemical supply houses. Alternatively, the hydroxyl-containing allylethers can be prepared from the reaction of an alcohol with an allylhalide in the presence of a base. Conversely, they can be prepared from allylalcohol and organohalides in the presence of base . Both of these reaction schemes are well known, as are the end product allylethers . The condensation reaction between the isocyanate and allylether hydroxy compounds can be carried out with or without a catalyst. Catalyzed reactions are desirable due to shortened reaction time and fewer by-products, which results in simplified purification. The typical catalysts which may be used for this reaction are amines and tin-based catalysts. Specifically, catalysts useful in the present invention include dibutyltin dilaurate, 1, 4-diazabicyclo [2.2.2] -octane (DABCO), 1 , 8-diazabicyclo- [5.4.0] -undec-7-ene (DBU) , N,N-dimethylcyclohexylamine (DMCA) , tetramethyltin, tetrabutyltin, tetraoctyltin, tributyltin chloride, dibutyltin dichloride, dimethyl tin oxide, trimethyltin chloride, dimethyltin dichloride, trioctyltin chloride, dibutyltin oxide, dibutyltin diacetate, butyltin trichloride, dioctyltin dichloride, dioctyltin oxide, dioctyltin dilaurate and dioctyltin diacetate. Zinc, iron, bismuth and zirconium complexes similar to those tin based complexes set forth above would also be useful as catalysts for the condensation reaction of the present invention. In the condensation reaction, it is desirable to use between 0.5 and 2.0, preferably between 0.75 and 1.5, more preferably between 0.9 and 1.1 equivalents of isocyanate for each equivalent of hydroxyl. In this manner, it is assured that there are few free alcohols or free isocyanates remaining in the material. The final, condensed product will contain allyl functional groups. Generally, there will be at least several allyl groups on each molecule and possibly many such groups. Preferably, there be at least two allyl functional groups per molecule to create adequate crosslinking of the resin. Once the resin is produced in this manner, crosslinking can be accomplished by mixing the resin with a free radical type initiator such as a peroxide. The resin can also be air dried, since this will initiate polymerization, although the rate and consistency will be uncontrolled. The resulting condensation product will be of the general formula : R x - [NHCO (OR) y (OCH 2 CH=CH 2 ) J n where R- L is the residue of the isocyanate-containing organic starting material, y is 0 or 1 and R is the organic residue of the hydroxyl-containing allyl ether starting material. The number n corresponds to the number of isocyanate groups per molecule starting material and is the number of allyl ether groups per molecule of starting material. It should be understood, however, that if the allyl-ether starting material includes a plurality of hydroxyl groups (as is preferred) , R will have attachment to multiple R α groups, forming a network. R will bond to R- L groups in the same number as the allyl ether starting material had hydroxyl groups. Furthermore, when m = n = 2, R cannot be ( -CH 2 ) 3 CCH 2 CH 3 . Where the hydroxyl containing allyl ether functional starting material has only one allyl ether group and one hydroxyl group, the formula becomes R τ [NHCO (OR) y CH 2 CH 2 =CH 2 ] n where y is 0 or 1. In the case of allyl alcohol, y = 0. Any suitable free radical initiator should be acceptable and will initiate crosslinking. The crosslinking will occur between allyl groups. Thus, the material is a free radical-curable composition (or air dryable composition) which produces a good surface cure due to the air dryable properties. Furthermore, the properties and extent of the crosslinking in the final product can be controlled by controlling the number of isocyanates per molecule of starting material and the number of hydroxyls per molecule of starting material . The system is very suitable for curing by means of UV curing, for which conventional UV irradiation sources and photoinitiators for example, benzoin derivates, peroxides, benzylketals and acetophenone derivates may be employed. A free-radical curable oligomer resin composition comprising at least one oligomer resin of the invention may further comprise a second compatible oligomer resin or monomer. Such a compatible resin may be an acrylate resin or another allylic resin or an unsaturated polyester resin. Suitable monomers include (meth) acrylates and other allylic monomers . This composition may further comprise at least one free-radical initiator. Free-radical initiator may be a peroxide alone or in the presence of an accelerator and/or a photoinitiator enabling UN curing. Dual curing is possible . Conventional additives such as, for example, pigments, fillers, flow agents and stabilizers can be added to the binder system. Examples of suitable pigments are inorganic pigments, such as titanium dioxide, zinc sulfide, iron oxide and chromium oxide and organic pigments such as azo compounds . Examples of suitable fillers are metal oxides, silicates, carbonates and sulfates. The coating compositions may be used to coat substrates of any kind, such as wood, plastics, leather, paper, textiles, glass, ceramics, plaster, masonry, metals and concrete. They may be applied by standard methods, such as spray coating, spread coating, flood coating, casting, dip coating, roll coating. The coating compositions may be clear or pigmented lacquers . The invention concerns also a method for making a cured resin comprising : making a free-radical curable oligomer resin as defined according to the invention, adding to said curable resin at least one free- radical initiator and allowing the said resin to cure Curing may be by thermal and/or by UV-curing and/or air-drying. In a specific method a second compatible resin, like acrylate or unsaturated polyester, is added before adding at least one free-radical initiator. The present invention is further illustrated by the following examples. Aliphatic Diallyl Urethane Two moles of allyl alcohol were reacted with one mole of isophorone diisocyanate in the presence of a dibutyltin dilaurate catalyst. The reactants were in liquid form, and the reaction was carried out by combining the two reactants and holding the mixture at 90°C for six hours. At that time, the reaction was completed, making a diallylurethane . Aliphatic Tetraallyl Urethane Following the procedure for Aliphatic diallyl urethane above, two moles of trimethylolpropane diallyl ether were reacted with two moles of isophorone diisocyanate and the resulting material was a tetraallyl urethane . Applications for improving surface cure The resins from above were evaluated in two different coating formulations . The first was a two component ambient temperature cure concrete sealer. The second was a two-component low temperature bake metal coating. Examples 1 and 2 .- Concrete Sealer Table I - Formulation All figures are in parts by weight The components of Part A were mixed together by hand until homogeneous. The resulting material was mixed with Part B by hand for 1 minute. The viscosity of the mixed, uncured resin was measured using a Brookfield RVT Viscometer at 25°C with # 4 spindle at 100 rpm. Tack-free cure times were measured by casting a 0.381 mm (15 mil) thick film on an aluminum panel by the wire wound rod draw down method, and determining the time to cure tack-free as measured by touching a gloved fingertip without getting sticking. Table II - Results, Concrete Sealer Examples 3 and 4 ,- Metal Coating Table III Formulation All figures are in parts by weight. The SR-9003, CD-513 and urethane monomers of Part A were blended together by hand until homogeneous . The CN 962 and CN 968 were warmed to 60°C in a forced air oven and then added to the monomer mixture using a high shear mixer. The cobalt accelerator was then added to Part A and mixed until homogeneous. Finally, the peroxide initiator (Part B) was added to Part A and mixed by hand until homogeneous. Viscosity of the uncured mixture was measured by using a Brookfield RVT Viscometer at 23 °C using thermosel and # 21 spindle. Shore D hardness was determined by casting 20 grams of formulation into an aluminum weighing dish, curing at 100°C for 30 minutes and measuring the hardness of the resulting material using a Shore D durometer. Tack-Free Cure Time was measured by preparing 0.381 mm (15 mil) films by the wire wound rod draw down method and determining surface cure by touching with a gloved fingertip without sticking. Table IV Results As can be seen from Tables II and IV, both the concrete sealer resin and the metal coating resin performed much better when the allyl urethane resin compositions of the present invention were incorporated. In the case of the concrete sealer. Table II shows that the tack-free cure times were increased substantially (from greater than 24 hours to 18 or fewer hours) by the addition of only 20% of the resin of the present invention. Similarly, in thirty minutes at 100°C, the metal coating compositions including resins of the present invention were tack-free (cured) . Under the same conditions, for the same time period, the composition without the new resin remained uncured, as shown in Table IV.

Claims: CLAIMS 1 - A free-radical curable oligomer resin having the formula : R,- [NHCO(OR) y (OCH 2 CH=CH 2 )J n wherein n is an integer from 2 to 20, m is an integer from 1 to 5, y is 0 or 1, R 1 is selected from the group consisting of aryl, arylalkyl, (C 3 -C 10 ) cycloalkyl, (C 3 -C 10 ) cycloalkenyl and heterocyclic and R is selected from the group consisting of (C 1 -C I0 ) alkyl, aryl, arylalkyl, (C 2 - C 10 ) alkenyl, (C 2 -C 10 ) alkynyl, (C 3 -C 10 ) cycloalkyl, (C 3 -C 10 ) cycloalkenyl, alkoxy, or (oligo) alkoxy with up to 3 alkoxy units, providing that when m = n = 2, R is not (-CH 2 ) 3 CCH 2 CH 3 . 2 - The oligomer resin of claim 1 wherein the resin is the reaction product of isophorone diisocyanate and allyl alcohol. 3 - The oligomer resin of claim 1 wherein n is an integer from 2 to 4 , m is an integer from 1 to 3 , R x is an aryl and R is selected from the group consisting of (C- L -C^) alkyl, (C 2 -C 10 ) alkenyl, alkoxy or (oligo) alkoxy with up to 3 alkoxy units. 4 - The oligomer resin of claims 1 or 3 wherein n = 2, m = 2, y = 1, R 1 = aryl and R is C^C^ alkyl. 5 - The oligomer resin of anyone of claims 1,3 or 4 wherein n = 2, m = 1, y = 0 and R 1 = aryl. 6 - The oligomer resin of anyone of claims 1 or 3 wherein the said oligomer resin is the reaction product between aliphatic, aromatic or cycloaliphatic isocyanates and hydroxyl -containing allyl ethers selected from : allyl alcohol, allyl alcohol propoxylates, allyl alcohol ethoxylates, trimethylol propane diallylether, trimethylol propane monoallyl ether, glycerol diallylether, glycerol monoallylether, ethylene glycol monoallylether, butanediol monoallylether and hexanediol monoallylether. 7 - A free-radical curable oligomer resin composition comprising at least one oligomer resin as defined in anyone of claims 1 to 6. 8 - A free-radical curable oligomer resin composition further comprising a second compatible acrylate resin. 9 - A free-radical curable oligomer resin composition according to claims 7 or 8, further comprising at least one free-radical initiator. 10 - A method for making a cured resin comprising : making a free-radical curable oligomer resin as defined according to anyone of claims 1 to 6 adding to said curable resin, at least one free- radical initiator ; and allowing said resin to cure 11 - The method of claim 10 further comprising the step of : adding to said curable resin, a second compatible acrylate resin, prior to adding said free- radical initiator. 12 - The method of claims 10 or 11 wherein said free-radical initiator is a peroxide. 13 - The cured resin produced by the process of anyone of claims 10 to 12 or by free-radical curing of oligomer resin compositions as defined according to anyone of claims 7 to 9.

Inventors: CESKA GARY W, FAN MINGXIN, HORGAN JAMES P, CESKA, GARY, W., FAN, MINGXIN, HORGAN, JAMES, P.
Applicants: CRAY VALLEY SA, SARTOMER CO INC, CRAY VALLEY S.A., SARTOMER COMPANY, INC.
Application year: 2001
Main classification: C08G18
IPC codes: C08G18, C09D175