Olefin polymerization catalysts

Abstract: 1. The invention concerns olefin polymerization catalyst component comprising an organometallic compound of general formula I wherein: M is a transition metal of groups 3, 4-10, lanthanide or actinide of the periodic table of the elements; each R is independently a structural bridge rigidly connecting two ligands L 1 , L 2 and L 3 and is constituted by 1 to 4 chain atoms selected from carbon, silicon, germanium, oxygen, boron; m, n and o are 0 or 1, with the proviso that m+n+o is 2 or 3; L 1 is a ligand of the cyclopentadienyl type or is isolobal to cyclopentadienyl, L 2 is a ligand of the cyclopentadienyl type or is isolobal to cyclopentadienyl, or a monovalent anionic ligand selected from the group consisting of N, P, B when m+n =2, it is selected from the group consisting of NR 1 , PR 1 , BR 1 , O and S when m+n =1; L 3 is a monovalent anionic ligand selected from the group consisting of N, P, B when n+o =2, it is selected from the group consisting of NR 1 , PR 1 , BR 1 , O and S when n+o =1; R 1 is hydrogen, C 1 -C 20 alkyl, C 3 -C 20 cycloalkyl, C 6 -C 20 aryl, C 3 -C 20 alkenyl, optionally comprising 1 to 5 heteroatoms such as Si, N, P, O, F, Cl, Br; each X is independently selected from the group consisting of hydrogen, halogen, NR 2 2 , R 2 with R 2 equal to C 1 -C 20 alkyl, C 1 -C 20 alkyl, C 3 -C 20 cycloalkyl, C 6 -C 20 aryl, C 3 -C 20 alkenyl, optionally comprising 1 to 5 heteroatoms such as Si, N, P, O, F, Cl, Br; q is a number whose value is: 0, 1, 2 or 3, depending on the valence of the metal M; D is a neutral Lewis base, p is a number whose value is: 0, 1, 2 or 3. The invention also concerns catalysts comprising compounds of formula (I) and the polymerization process making use of a catalyst comprising the claimed compounds.

Description: The present invention concerns new organometallic compounds and polymerization catalysts comprising the organometallic compounds. During the last 20 years a lot of research has been carried out in order to establish the relation structure-reactivity in single site olefin polymerization catalysis. As a result, several information concerning the influence of the catalyst structure on molecular weight, tacticity and comonomer insertion are available today. One of the first methods used for achieving a better control of the catalyst properties is the use of a bridge which renders two cyclopentadienyl ligands stereorigid. In this way, it has been possible to obtain highly isotactic and highly syndiotactic propylene polymers. EP 416 815 discloses monocyclopentadienyl catalysts wherein a cyclopentadienyl ligand and an amido ligand are connected through a covalent bridge. The resulting catalyst can incorporate very efficiently long chain alpha-olefins. In the last decade, a lot of effort have been dedicated to the development of these complexes and to the study of the influence of the ligand structure on catalyst activity. EP-A-485 821 describes metallocenes of formula (I) characterized by the fact that the transition metal (M') is bonded to only two anionic ligands. Summary of the invention It has been surprisingly found that it is possible to prepare organometallic compounds wherein a transition metal is bonded to three ligands which are rigidly connected through structural bridges, wherein at least one ligand is of the cyclopentadienyl type or is isolobal to cyclopentadienyl and the remainder(s) are monovalent anionic ligands. These complexes are effective catalysts for olefin polymerization. By varying the type of ligands and the structure of the two (or three) covalent bridges it is possible to modify the characteristics of the resulting catalyst in terms of molecular weight, comonomer incorporation and tacticity of the obtained polymer. Description of the invention The organometallic catalysts of the invention are represented by general formula (I): wherein: M is a transition metal of groups 3, 4-10, lanthanide or actinide of the periodic table of the elements, preferably titanium, zirconium or hafnium; each R is independently a structural bridge rigidly connecting two ligands L 1 , L 2 and L 3 and is constituted by I to 4 chain atoms selected from carbon, silicon, germanium, oxygen, boron; these atoms can be part of fused rings, aromatic rings, aliphatic rings or spiro rings; preferred examples of groups R are: CR 1 2 , SiR 1 2 , CR 1 2 -CR 1 2 , CR 1 2 -SiR 1 2 , SiR 1 2 -SiR 1 2 ; wherein each R 1 is independently selected from hydrogen, C 1 -C 20 alkyl, C 3 -C 20 cycloalkyl, C 6 -C 20 aryl, C 3 -C 20 alkenyl, optionally comprising 1 to 5 heteroatoms such as Si, N, P, O, F, Cl, Br, preferably R 1 is selected from C 1 -C 6 linear or branched alkyls; most preferably is methyl, ethyl, isopropyl, tertbutyl; m, n and o are 0 or 1, with the proviso that m+n+o is 2 or 3; L 1 is a ligand of the cyclopentadienyl type or is isolobal to cyclopentadienyl, preferably a cyclopentadienyl, indenyl or fluorenyl ring, cyclopenteno[b]tiophenyl cyclopenteno[b:b']-dithiophenyl cyclopenteno[b]pyrrolyl, boratabenzene, phospholyl, dihydroindeno[b]indolyl, optionally substituted by one or more R' groups; most preferably a cyclopentadienyl, indenyl or fluorenyl ring, optionally substituted by one or more R' groups; L 2 is a ligand defined as L 1 , or a monovalent anionic ligand selected from the group consisting of N, P, B when m+n =2, from the group consisting of NR 1 , PR 1 , BR 1 , O and S when m+n =1; L 3 is a monovalent anionic ligand selected from the group consisting of N, P, B when n+o =2, from the group consisting of NR 1 , PR 1 , BR 1 , O and S when n+o =1; each X is independently selected from the group consisting of hydrogen, halogen, NR 2 2 , R 2 with R 2 equal to C 1 -C 20 alkyl, C 3 -C 20 cycloalkyl, C 6 -C 20 aryl, C 3 -C 20 alkenyl, optionally comprising 1 to 5 heteroatoms such as Si, N, P, O, F, Cl, Br. q is a number whose value is: 0, 1, 2 or 3, depending on the valence of the metal M, so that q+3 is the valence of M; D is a neutral Lewis base, preferably it is selected from the group consisting of linear or cyclic ethers, amines and phosphines; most preferably it is selected from the group consisting of diethyl ether, tetrahydrofurane, aniline, dimethylaniline, triphenylphosphine, n-butylamine; p is a number whose value is: 0, 1, 2 or 3. When m is 1, n is 0 and o is 1, the formula I becomes the following formula Ia: When m is 1, n is 1 and o is 0, the formula I becomes the following formula Ib: When m is 1, n is 1, o is 0 and L 2 is a ligand defined as L 1 the formula I becomes the following formula Ic When m , n and o are 1 the formula (I) becomes the following formula Id It has been calculated using molecular modeling methods that compounds according to general formula (I) having three ligands rigidly interconnected can have a geometry wherein the bond angles of the metal M are more constrained than the catalyst disclosed in EP 416815. By varying the type of R and the ligands L 1 , L 2 and L 3 it is possible to vary the bond angle as well as the steric hindrance on the metal center, influencing in this way Mw, MWD, long chain branching, short chain branching and, in case of C 3 -C 20 alpha olefins, the tacticity of the polymer. A preferred class of compounds belonging to formula Ia is defined by the following formula II: wherein Cp is a cyclopentadienyl or indenyl ring, optionally substituted by one or more R 1 groups, M is selected from Ti, Zr and Hf each R is independently selected from CR 1 2 , SiR 1 2 , CR 1 2 -CR 1 2 , CR 1 2 -SiR 1 2 , SiR 1 2 -SiR 1 2 , wherein R 1 is hydrogen, C 1 -C 20 alkyl, C 3 -C 20 cycloalkyl, C 6 -C 20 aryl, C 3 -C 20 alkenyl, optionally comprising 1 to 5 heteroatoms such as Si, N, P, O, F, Cl, Br. Two groups R' bonded to the same or to adjacent atoms can unite to form a ring. L 2 and L 3 are independently selected from the group consisting of NR 1 , PR 1 , BR 1 , O and S; X is independently selected from the group consisting of hydrogen, halogen, NR 2 , R 2 with R 2 equal to C 1 -C 20 alkyl, C 3 -C 20 cycloalkyl, C 6 -C 20 aryl, C 3 -C 20 alkenyl, optionally comprising 1 to 5 heteroatoms such as Si, N, P, O, F, Cl, Br. D is a neutral Lewis base; preferably it is selected from the group consisting of linear or cyclic ethers, amines and phosphines; most preferably it is selected from the group consisting of diethyl ether, tetrahydrofurane, aniline, dimethylaniline, triphenylphosphine, n-butylamine; p is a number whose value is: 0, 1, 2 or 3. In one embodiment of the invention, the compounds of formula I are preferably obtained by reacting a compound of formula MX q+3 wherein M is a transition metal of groups 3, 4-10, lanthanide or actinide of the periodic table of the elements, X is a monovalent anionic ligand, preferably selected from the group consisting of N(CH 3 ) 2 , benzyl, and q is 0, 1, 2, 3 depcnding on the valence of M, with a compound of formula III wherein L 1 is a group of the cyclopentadienyl type or is isolobal to cyclopentadienyl, preferably a cyclopentadienyl, indenyl or fluorenyl ring, cyclopenteno[b]tiophenyl cyclopenteno[b:b']-dithiophenyl cyclopenteno[b]pyrrolyl, boratabenzene, phospholyl, dihydroindeno[b]indolyl, optionally substituted by one or more R' groups; most preferably a cyclopentadienyl, indenyl or fluorenyl ring, optionally substituted by one or more R' groups; m, n and o are 0 or 1, with the proviso that m+n+o is 2 or 3. L 2 is a ligand of the cyclopentadienyl type or is isolobal to cyclopentadienyl, preferably a cyclopentadienyl, indenyl or fluorenyl ring, cyclopenteno[b]tiophenyl cyclopenteno[b:b']-dithiophenyl cyclopenteno[b]pyrrolyl, boratabenzene, phospholyl, dihydroindeno[b]indolyl, optionally substituted by one or more R 1 groups; most preferably a cyclopentadienyl, indenyl or fluorenyl ring, optionally substituted by one or more R' groups; or it is selected from the group consisting of N, P, B when m+n =2, it is selected from the group consisting of NR 1 , PR 1 , BR 1 , O and S when m+n =1; L 3 is selected from the group consisting of N, P, B when n+o =2, it is selected from the group consisting of NR 1 , PR 1 , BR 1 , O and S when n+o =1; each R is independently a structural bridge rigidly connecting L 1 , L 2 and L 3 and is constituted by 1 to 4 chain atoms selected from carbon, silicon, germanium, oxygen, boron; these atoms can be part of fused rings, aromatics rings or spiro rings; R 1 is hydrogen, C 1 -C 20 alkyl, C 3 -C 20 cycloalkyl, C 6 -C 20 aryl, C 3 -C 20 alkenyl, optionally comprising 1 to 5 heteroatoms such as Si, N, P, O, F, Cl, Br. In order to have complete substitution of three ligands X with L 1 , L 2 and L 3 it is in some cases preferable to remove from the reaction medium the compound XH formed during reaction. Depending on the reaction conditions, also the intermediate IV can be formed. The intermediate IV is then further reacted with a compound of formula II with X equal to benzyl, to produce the compound of formula I. Alternatively, it is possible to react one mole of compound III with three moles of a strong base such as butyllithium, NaH, KH, etc. The trianion is then treated with MX q+3 , optionally complexed with a Lewis base D, to obtain the compound of formula I, with X equal to halogen, preferably Cl. Another suitable process for the preparation of compounds of formula I is to treat the compound (III) with NR 3 in the presence of MX q+3 . The organometallic compounds of the present invention are useful as catalyst components for polymerizing olefins, preferably alpha-olefins in combination with a co-catalyst. Illustrative but non-limiting examples of co-catalysts are: aluminoxanes (methylaluminoxane (MAO), modified methylaluminoxane (MMAO), etc.), combinations of alkylaluminiums (such as trimethylaluminium, triethylaluminium, tributylaluminium, etc.) and boron Lewis acids (such as trifluoroborane, tris-pentafluorophenylborane, tris[3,5-bis(trifluoromethyl)phenyl]borane, etc.), and compounds of formula J + K - wherein J + is able to react irreversibly with a group X in formula I and K - is an anion which is able to stabilize the catalytic species which originates from the reaction of the two compounds and which is sufficiently labile to be able to be removed from an olefinic substrate (triphenylcarbenium tetrakis(pentafluorophenyl)borate, dimethylanilinium tetrakis(pentafluorophenyl)borate, HBF 4 , AgBF 4 , AgPF 6 , AgSbF 6 , silver tetrakis[3,5-bis(trifluoromethyl)phenyl]borate, sodium tetrakis[3,5-bis(trifluoromethyl)phenyl]borate, etc.). The catalyst component of the present invention, i.e. organometallic compound complex of formula I, can be used either as homogeneous catalyst or heterogeneous. In the latter case, it is preferred to use a organometallic compound (I) wherein at least one L group (selected from L 1 , L 2 and L 3 ) and/or one R group contains a functional group capable or forming a covalent bond with the support. Suitable functional groups are: -O-SiR 2 3 . -SiR 2 nX 3-n , SiR 2 n (OR 2 ) 3-n , -OH. This type of compounds are disclosed in EP 839 836, EP 757 992, EP 293 815, EP 953 580, EP 953 381 and WO 99/52949. The preferred functional group is -O-SiR 2 3 and is preferably linked to the organometallic compound through a divalent radical comprising from 1 to 20 carbon atoms and from 0 to 5 chain atoms different from carbon and preferably selected from silicon, oxygen, sulfur, boron, phosphorus, nitrogen. The divalent radical joins the group -O-SiR 2 3 either to the Cp ring or to one of the atoms of R or to the anionic ligand, as described in EP 839 836. As supporting material, any type of inorganic oxides are used, for example inorganic oxides such as: silica, alumina, silica-alumina, aluminum phosphates and mixtures thereof, obtaining supported catalysts with contents in transition metals between 0.01 and 4% by weight, preferably between 0.1 and 1%. A particularly preferred support is silica calcined at a temperature between 600°C and 800°C and also MAO modified silica. For the polymerization in solution, the cocatalyst is mixed with a solution of a organometallic compound of formula I and a supplementary quantity of it optionally is added to the solution; or the catalyst can directly be added to the polymerization medium, which contains the cocatalyst. For the polymerization in suspension, the cocatalyst is previously mixed with the supported solid catalyst or it is added to the polymerization medium before the supported catalyst, or both operations are sequentially realized. The most proper polymerization procedure can change according to the chosen type of polymerization process (solution, suspension, slurry or gas phase). The process consists in putting in contact the monomer, or, in certain cases, the monomer and the comonomer, with a catalytic composition according to the present invention, that includes at least one organometallic compound of formulas I and/or II, at a proper temperature and pressure. C 2 -C 12 alpha-olefms, such as ethylene, propylene, 1-butene, 1-hexene, 1-octene, 4-methyl-1-pentene, styrene, divinylbenzene are used as monomer. In case ethylene is used as monomer, it can be either homopolymerized, or copolymerized in the presence of at least one comonomer selected from propylene, 1-butene, 1-hexene, 1-octene, 4-methyl-1-pentene. These comonomers are used in proportions from 0.1 to 70% by weight of the total of the monomers. In the case of homopolymerization of ethylene the density of polymers ranges between 0.950 and 0.970 kg/cm 3 in the case of copolymerization of ethylene the density is as low as 0.880 kg/cm 3 . In the particular case of the polymerization technique known as suspension or slurry process, the used temperature will be between 30° and 110 °C, the same which is typically used in gas phase, while for the solution process the usual temperature will be between 120° and 250°C. Preferred compounds of formula I are: Further examples of compounds belonging to the invention are obtained by substituting zirconium in the above listed compounds with titanium or hafnium. These compounds can be synthesized starting from the corresponding compound of formula III, which can be synthesized using methods similar to those described in the experimental part starting from the appropriate cyclopentadienyl derivative, Me 2 SiCl 2 and amine derivatives. Further examples include compounds wherein the tetrahydrofurane ligand in the previous examples shown in b) is replaced by pyrydine. These compounds can be synthesized starting from the corresponding compound of formula III, which can be synthesized using methods similar to those described in the experimental part starting from the appropriate cyclopentadienyl derivative, Me 2 SiCl 2 and amine derivatives. The corresponding compound of formula I can be synthesized using similar methods to those described in the experimental part starting from the compound of formula III and the appropriate chromium III complex, such as CrCl 3 (THF) 2 . c) Further examples include compounds wherein the zirconium atom in the previous examples shown in c) is replaced by Ti, Hf These compounds can be synthesized starting from the corresponding compound of formula III, which can be synthesized using methods similar to those described in Organometallics 1997, 16, 2891; Topics in Catalysis 7, 1999, 37; Eur. J. Inor. Chem. 1998, 1153. Further examples include compounds wherein the zirconium atom in the previous examples shown in d) is replaced by Ti, Hf These compounds can be synthesized starting from the corresponding compound of formula III, which can be synthesized using methods similar to those described in Organometallics 19, 2000, 4071. Further examples include compounds wherein the zirconium atom in the previous examples shown in e) is replaced by Ti, Hf These compounds can be synthesized starting from the corresponding compound of formula III, which can be synthesized using methods similar to those described in EP0839834, EP416185. Further examples include compounds wherein the zirconium atom in the previous examples shown in f) is replaced by Ti, Hf The previous compounds can be synthesized using similar methods described in the literature. The corresponding compound of formula III can be synthesized using similar methods to those described in J. Organomet. Chem. 558, 1998, 139; Chem. Ber. 1996, 129, 275 starting from the appropriate cycolpentadienyl derivative and the appropriate protected amine or alcohol followed by deprotection. g) Further examples include compounds wherein the zirconium atom in the previous examples shown in g) is replaced by Ti, Hf. These compounds can be synthesized starting from the corresponding compound of formula III, which can be synthesized using methods similar to those described in EP953581, EP839836 and European patent application number 99500196.3. Further examples include compounds wherein the zirconium atom in the previous examples shown in h) is replaced by Ti, Hf. These compounds can be synthesized starting from the corresponding compound of formula III, which can be synthesized using methods similar to those described in Organometallics 1999, 18, 4147. Experimental Synthesis of compounds 1-9 All manipulations were performed under an inert atmosphere of argon or nitrogen using syringes or cannulae through Subaseals in Schlenk tubes using high vacuum line techniques or a glovebox. Solvents were dried and distilled under nitrogen: diethyl ether and tetrahydrofurane from sodium benzophenone ketyl; benzene and toluene from sodium and hexane from sodium/potassium alloy. Compound C 5 H 4 -1,1-(SiMe 2 Cl) 2 was prepared according to Organometallics , 1985 , 4 , 2206. The 1 H and 13 C NMR spectra were recorded at 299.95 and 75.43 MHz respectively on a Varian Unity 300 spectrometer; chemical shifts, in ppm, are positive downfield with respect external SiMe 4 ; coupling constants are in Hz. IR spectra were recorded in Nujol mulls for solids on a Perkin-Elmer 583 spectrophotometer. C and H analyses were performed with a Perkin-Elmer 240-B microanalyzer. Preparation of C 5 H 4 [SiMe 2 (NH t Bu)] 2 (1) A solution of 2.1 equivalents of LiNH t Bu in THF was added at 0°C to a solution of 1 equivalent of C 5 H 4 -1,1-(SiMe 2 Cl) 2 in THF and the mixture was stirred for 12 h. The volatiles were removed under vacuum and the residue extracted with hexane to give (1) as a yellow oil in 90% yield. Preparation of [Zr{η 5 -C 5 H 3 [SiMe 2 (NHBu t )][SiMe 2 (η 1 -NBu t )}(NMe 2 ) 2 ] (2) A solution of Zr(NMe 2 ) 4 (3.37g, 12.6 mmol) in THF (70 mL) was cooled to 0°C and 1 (4.09g, 12.6 mmol) was added by syringe. The resulting yellow solution was refluxed during 5 h. When the gas stopped the solvent was removed under vacuum and the residue was extracted into pentane (70 mL). After filtration and removal of the solvent complex 2 was isolated as a light brown oil. (6.19 g, 12.3 mmol, 98 %). 1 H-NMR (300MHz, C 6 D 6 , 20°C, TMS): δ 0.35 (s, 3H, Si Me 2 NH t Bu), 0.42 (s, 3H, Si Me 2 NH t Bu), 0.57 (s, 3H, Si Me 2 N t Bu), 0.59 (s, 3H, Si Me 2 N t Bu), 0.85 (s, 1H, N H t Bu), 1.11 (s, 9H, NH t Bu ), 1.27 (s, 9H, N t Bu ), 2.81 (s, 6H, N Me 2 ), 2.82 (s, 6H, N Me 2 ), 6.39 (m, 1H, C 5 H 3 ), 6.47 (m, 1H, C 5 H 3 ), 6.69 (m, 1H, C 5 H 3 ); 13 C-NMR (300MHz, C 6 D 6 , 20°C, TMS): δ 2.3 (Si Me 2 ), 2.7 (Si Me 2 ), 2.8 (Si Me 2 ), 3.0 (Si Me 2 ), 33.9 (NH t Bu ), 34.9 (N t Bu ), 44.2 (N Me 2 ), 44.5 (N Me 2 ), 49.6 (NH t Bu ipso ), 56.6 (N t Bu ipso ), 111.4 ( C 5 H 3ipso ), 122.6 ( C 5 H 3 ), 122.9 ( C 5 H 3 ); 124.6 ( C 5 H 3 ), 126.7 ( C 5 H 3 ). IR (Nujol) ν =3384 cm -1 (N-H). Anal. Found: C 49.73, H 9.05, N 11.45. Calc.: C 50.24, H 9.24, N 11.16. Preparation of [Zr{η 5 -C 5 H 3 -1,3-[SiMe 2 (η 1 -NBu t )] 2 }(NMe 2 )] (3) When a 1/1 molar ratio of [Zr{η 5 -C 5 H 3 -1,3-[SiMe 2 (η 1 -NBu t )] 2 }(CH 2 Ph)] (see preparation (5) below) and the diamido 2 derivatives in C 6 D 6 was heated for 12h to 120° C in a sealed NMR tube, the amido compund 3 was formed as the unique reaction product and identified by NMR spectroscopy. 1 H-NMR (300MHz, C 6 D 6 , 20°C, TMS): δ 0.51 (s, 6H, Si Me 2 ), 0.55 (s, 6H, Si Me 2 ), 1.31 (s, 18H, N t Bu ), 2.77 (s, 6H, N Me 2 ), 6.34 (m, 1H, C 5 H 3 ), 6.78 (m, 2H, C 5 H 3 ); 13 C-NMR (300MHz, C 6 D 6 , 20°C, TMS): δ 2.9 (Si Me 2 ), 3.0 (Si Me 2 ), 35.6 (N t Bu ), 45.1 (N Me 2 ), 55.8 (N t Bu ipso ), 117.7 ( C 5 H 3ipso ) 119.8 ( C 5 H 3 ), 133.2 ( C 5 H 3 ). Preparation of [Zr{η 5 -C 5 H 3 [SiMe 2 (NHBu t )][SiMe 2 (η 1 -NBu t )} (CH 2 Ph) 2 ] (4) A solution of Zr(CH 2 Ph) 4 (2.93 g, 6.43 mmol) in toluene (70 ml) was cooled to 0° C and 1 ( 2.09 g, 6.43 mmol) was added by syringe. The resulting yellow solution was warmed to 45° C for 5 b. The solvent was removed under vacuum and the residue was extracted into pentane (70 ml). After filtration and removal of the solvent a mixture of complexes 4 and 5 was isolated. Formation of 4 was confirmed by IR and NMR spectroscopy although pure 4 free of 5 could not be isolated. IR (Nujol): ν = 3353 cm -1 (N-H). 1 H-NMR (300MHz, C 6 D 6 , 20°C, TMS) for 4: δ 0.33 (s, 3H, Si Me 2 ), 0.34 (s, 3H, Si Me 2 ), 0.35 (s, 3H, Si Me 2 ), 0.40 (s, 3H, Si Me 2 ), 0.69 (s, 1H, N H t Bu), 1.06 (s, 9H, NH t Bu ), 1.13 (s, 9H, N t Bu ), 1.66 (s, 1H, C H 2 Ph), 1.72 (s, 1H, C H 2 Ph), 2.12 (s, 1H, C H 2 Ph), 2.17 (s, 1H, C H 2 Ph), 6.21 (m, 1H, C 5 H 3 ), 6.35 (m, 1H, C 5 H 3 ), 6.60 (m, 1H, C 5 H 3 ), 6.90-7.30 (m, 10H, C 6 H 5 ). 13 C-NMR (300MHz, C 6 D 6 , 20°C, TMS): δ 1.3 (Si Me 2 ), 2.4 (Si Me 2 ), 2.5 (Si Me 2 ), 2.8 (Si Me 2 ), 33.7 (NH t Bu ), 33.8 (N t Bu ), 49.7 (NH t Bu ipso ), 54.9 (CH 2 Ph ), 57.1 (N t Bu ipso ), 57.9 (CH 2 Ph ), 109.6 ( C 5 H 3ipso ), 122.2 ( C 5 H 3 ), 122.5 ( C 5 H 3 ), 124.2 ( C 5 H 3 ), 125.6 ( C 5 H 3 ), 125.9 ( C 6 H 5 ), 126.4 ( C 6 H 5 ), 126.6 ( C 6 H 5 ), 127.8 ( C 6 H 5 ), 129.3 ( C 6 H 5 ), 129.6 ( C 6 H 5 ), 129.6 ( C 6 H 5 ), 129.8 ( C 6 H 5 ), 131.9 ( C 6 H 5 ), 145.8 ( C 6 H 5ipso ), 146.2 ( C 6 H 5ipso ). Preparation of [Zr{η 5 -C 5 H 3 -1,3-[SiMe 2 (η 1 -NBu t )] 2 }(CH 2 Ph)] (5) A solution of Zr(CH 2 Ph) 4 (2.93 gr, 6.43 mmol) in toluene (70 ml) was cooled to 0°C and 1 (2.09 g, 6.43 mmol) was added by syringe. The resulting yellow solution was refluxed for 5 h. The solvent was removed under vacuum and the residue was extracted into pentane (70 ml). After filtration and removal of the solvent complex 5 was isolated as a brown oil. ( 3.20 g, 6.34 mmol, 99 %). 1 H-NMR (300MHz, C 6 D 6 , 20°C, TMS): δ 0.40 (s, 6H, Si Me 2 ), 0.42 (s, 6H, Si Me 2 ), 1.27 (s, 18H, N t Bu ), 2.12 (s, 2H, C H 2 Ph), 6.14 (m, 1H, C 5 H 3 ), 6.53 (m, 2H, C 5 H 3 ) 6.9-7.23 (m, 5H, C 6 H 5 ). 13 C-NMR (300MHz, C 6 D 6 , 20°C, TMS): δ 2.4 (Si Me 2 ), δ 2.4 (Si Me 2 ), 35.8 (N t Bu ), 55.7 ( C H 2 Ph), 57.1 (N t Bu ipso ), 116.5 ( C 5 H 3ipso ), 120.7 ( C 5 H 3 ), 126.4 ( C 5 H 3 ), 128.5 ( C 6 H 5 ), 129.8 ( C 6 H 5 ), 132.7 ( C 6 H 5 ), 150.6 ( C 6 H 5ipso ). Anal. Found: C 57.01, H 7.65, N 5.48. Calc.:C 57.20, H 8.00, N 5.56. Preparation of [Ti{η 5 -C 5 H 3 [SiMe 2 (NHBu t )][SiMe 2 (η 1 -NBu t )}(CH 2 Ph) 2 ] (6) A solution of Ti(CH 2 Ph) 4 (2.14 g, 5.2 mmol) in toluene (70 ml) was cooled to 0° C and 1 (1.69 g, 5.2 mmol) was added by syringe. The resulting yellow solution was warmed to 65°C for 5 h. When evolution of gas stopped the solvent was removed under vacuum and the residue was extracted into pentane (70 ml). After filtration and removal of the solvent complex 6 was isolated as a red solid. (2.87 g, 5.2 mmol, 100 %). 1 H-NMR (300MHz, C 6 D 6 , 20°C, TMS): δ 0.21 (s, 3H, Si Me 2 ), 0.27 (s, 3H, Si Me 2 ), 0.37 (s, 3H, Si Me 2 ), 0.38 (s, 3H, Si Me 2 ), 0.72 (s, 1H, N H t Bu), 1.07 (s, 9H, NH t Bu ), 1.44 (s, 9H, N t Bu ), 2.47 (d, 2H, J=10.5 Hz, C H 2 Ph), 2.55 (d, 2H, J=10.5 Hz, C H 2 Ph), 2.81 (d, 2H, J=10.5 Hz, C H 2 Ph), 2.97 (d, 2H, J=10.5 Hz, C H 2 Ph), 5.83 (m, 1H, C 5 H 3 ), 6.14 (m, 1H, C 5 H 3 ), 6.83 (m, 1H, C 5 H 3 ), 6.87-7.20 (m, 10H, CH 2 Ph ); 13 C-NMR (300MHz, C 6 D 6 , 20°C, TMS): δ 0.6 (Si Me 2 ), 1.5 (Si Me 2 ), 2.4 (Si Me 2 ), 2.9 (Si Me 2 ), 33.8 (NH t Bu ), 343 (N t Bu ), 49.8 (NH t Bu ipso ), 61.5 (N t Bu ipso ), 79.6 (CH 2 Ph ), 83.7 (CH 2 Ph ), 110.2 ( C 5 H 3ipso ), 122.1 ( C 5 H 3 ), 122.5 ( C 5 H 3 ), 123.0 ( C 5 H 3 ), 125.9 ( C 5 H 3 ), 126.8 ( C 6 H 5 ), 126.8 ( C 6 H 5 ), 127.4 ( C 6 H 5 ), 128.5 ( C 6 H 5 ), 128.6 ( C 6 H 5 ), 128.7 ( C 6 H 5 ), 128.9 ( C 6 H 5 ), 129.8 ( C 6 H 5 ), 132.6 ( C 6 H 5 ), 149.6 ( C 6 H 5ipso ), 150.1 ( C 6 H 5ipso ). IR(nujol); v=3349 cm -1 (N-H). Anal. Found: C 62.58, H 8.75, N 6.08. Calc.: C 62.68, H 8.68, N 5.76. Preparation of [Ti{η 5 -C 5 H 3 -1,3-[SiMe 2 (η 1 -NBu t )] 2 }(CH 2 Ph)] (7) A solution of Ti(CH 2 Ph) 4 (5.34 g, 12.9 mmol) in toluene (70 ml) was cooled to 0° C and 1 (4.21 g, 12.9 mmol) was added by syringe. The resulting deep red solution was refluxed for 5 h. The solvent was removed under vacuum and the residue was extracted into pentane (70 ml). After filtration and removal of the solvent complex 7 was isolated as a deep red solid. (5.93 g, 12.9 mmol, 100 %). 1 H-NMR (300MHz, C 6 D 6 , 20°C, TMS): 8 0.39 (s, 6H, Si Me 2 ), 0.40 (s, 6H, Si Me 2 ), 1.42 (s, 18H, N t Bu ), 2.61 (s, 2H, C H 2 Ph), 6.14 (m, 2H, C 5 H 3 ), 6.40 (m, 1H, C 5 H 3 ), 6.89 (m, 1H, C 6 H 5 ), 7.00 (m, 2H, C 6 H 5 ), 7.22 (m, 2H, C 6 H 5 ); 13 C-NMR (300MHz, C 6 D 6 , 20°C, TMS): δ 2.1 (Si Me 2 ), 2.2 (Si Me 2 ), 35.6 (N t Bu ), 59.3 (N t Bu ipso ), 69.6 ( C H 2 Ph), 117.7 ( C 5 H 3ipso ), 121.5 ( C 5 H 3 ), 126.3 ( C 5 H 3 ), 128.5 ( C 6 H 5 ), 130.3 ( C 6 H 5 ), 132.6 ( C 6 H 5 ), 152.4 ( C 6 H 5ipso ). Anal. Found: C 67.36, H 8.75, N 5.07. Calc.: C 67.82, H 8.71, N 4.81. Preparation of [Zr{η 5 -C 5 H 3 -1,3-[SiMe 2 (η 1 -NBu t )] 2 }] + [(CH 2 Ph)B(C 6 F 5 ) 3 ] - (8) A toluene (20 m) solution of the monobenzyl complex 5 (0.116 g, 0.25 mmol) was treated with B(C 6 F 5 ) 3 (0.126 g, 0.25 mmol) at room temperature and the mixture was stirred for 30 m and cooled to -35° C. The solvent was filtered off from the resulting insoluble residue which was then dried under vacuum to give 8 (0.21 g, 83% yield) as a dark brown oil. 1 H-NMR (300MHz, C 6 D 6 , 20°C, TMS): δ 0.17 (s, 6H, Si Me 2 ), 0.36 (s, 6H, Si Me 2 ), 0.99 (s, 18H, N t Bu ), 3.42 (s, 2H, BC H 2 ), 5.20 (m, 1H, C 5 H 3 ), 6.01 (m, 2H, C 5 H 3 ), 6.10 (m, 1H, p-C 6 H 5 ), 6.34 (m, 2H, m-C 6 H 5 ), 6.87 (m, 2H, o-C 6 H 5 ). 13 C-NMR (300MHz, C 6 D 6 , 20°C, TMS): δ 1.5 (Si Me 2 ), 1.6 (Si Me 2 ), 34.8(N t Bu ), 58.6 (N t Bu ipso ), 121.4 ( C 5 H 3ipso ) 127.4 ( C 5 H 3 ), 127.5 ( C 5 H 3 ), 127.9 ( C 6 H 5 ), 128.1 ( C 6 H 5 ), 128.3 ( C 6 H 5 ), 136.5 ( C 6 F 5 ), 138.3 ( C 6 F 5 ), 147.8 ( C 6 F 5 ), 149.8 ( C 6 F 5 ), 162.0 ( C 6 H 5ipso ). 19 F-NMR (300MHz, C 6 D 6 , 20°C, CCl 3 F): 132.1 (m, 2F, o-C 6 F 5 ), 163.6 (m, 1F, p-C 6 F 5 ), 167.2 (m, 2F, m-C 6 F 5 ). Preparation of [Ti{η 5 -C 5 H 3 -1,3-[SiMe 2 (η 1 -NBu t )] 2 }] + [(CH 2 Ph)B(C 6 F 5 ) 3 ] - (9) A toluene (20 ml) solution of the monobenzyl complex 7 (0.125 g, 0.25 mmol) was treated with B(C 6 F 5 ) 3 (0.126 g, 0.25 mmol) at room temperature and the mixture was stirred for 30 m and cooled to -35° C. The solvent was filtered off from the resulting insoluble residue which was then dried under vacuum to give 9 (0.13 g, 60% yield) as an orange crystalline solid. 1 H-NMR (300MHz, C 6 D 6 , 20°C, TMS): δ 0.19 (s, 6H, Si Me 2 ), 0.38 (s, 6H, Si Me 2 ), 1.12 (s, 18H, N t Bu ), 3.49 (s, 2H, BC H 2 ), 5.03 (m, 1H, C 5 H 3 ), 5.86 (m, 2H, C 5 H 3 ), 6.21-7.10 (m, 5H, C 6 H 5 ). Compound 9 was only slightly soluble in C 6 D 6 , and its 13 C NMR spectrum could not be recorded. 19 F-NMR (300MHz, C 6 D 6 , 20°C, CCl 3 F): 132.1 (m, 2F, o-C 6 F 5 ), 163.6 (m, 1F, p-C 6 F 5 ), 167.2 (m, 2F, m-C 6 F 5 ). Polymerization of ethylene Example 1 Ethylene homopolymer by the use of the compound 5. In a 1.3 1 glass reactor were added 600 ml of dry heptane. The reactor was pressurized with 4 atm ethylene and then 12.9 ml methylaluminoxane (MAO, 1.5 M in toluene) and 4.2 micromoles of compound 5 dissolved in 5 ml toluene were added. The reactor is kept under stirring and thermostated at 70 °C. After 15', the polymerization was stopped by addition of acidified methanol. 2.96 g of polyethylene were obtained. The activity of the catalyst system was 740 kg PE/mol Zr·h·atm; Mw= 541.000, Mw/Mn= 1.9. Example 2 Ethylene-hexene copolymers by the use of compound 5 . In a 1.3 l glass reactor were added 600 ml of dry heptane. The reactor was pressurized with 4 atm ethylene. 10 ml of previously distilled hexene were added, followed by 6.4 ml MAO (1.5 M in toluene) and 2.1 micromoles of compound 5 dissolved in 5 ml toluene. The reactor is kept under stirring and thermostated at 70 °C. After 1h, the polymerization was stopped by addition of acidified methanol. 1.81 g of polyethylene were obtained. The activity of the catalyst system was 226 kg PE/mol Zr·h·atm; Mw= 440.000; Mw/Mn= 2.6 and 0.7 mol % of hexene in the polymer. Example 3 Ethylene-hexene copolymers by the use of compound 5 . Example 2 was repeated but using 12.9 ml of MAO aand 4.2 micromoles of compound 5. After 30' of polymerization 2.78 g of polyemer were obtained. The activity of the catalyst system was 348 kg PE/mol Zr·h·atm; Mw= 408.000; Mw/Mn= 2.2 and 0.7 mol % of hexene in the polymer. Polymerization of propylene Example 4 Propylene homopolymer by the use of the compound 5 . In a 1.3 1 glass reactor were added 600 ml of dry heptane. The reactor was pressurized with 5 atm propylene and then 0.01 mmol of compound 5 in 15 ml MAO (1.5 M in toluene) were added. The reactor was kept under stirring and thermostated at 40 °C. After 1h, the polymerization was stopped by addition of acidified methanol. The solvent was removed by using a rotavapor. The residue was washed with methanol and the polymer is then dried. 2.4 g of atactic polypropylene (according to 13 C NMR) were obtained. Example 5 Propylene homopolymer by the use of the compound 5. In a 1.3 1 glass reactor were added 600 ml of dry heptane. The reactor was pressurized with 5 atm propylene. 4.65 ml MAO (1.5 Min toluene) were added and then 0.01 mmol of compound 5 in 5 ml MAO (1.5 M in toluene) were added. The reactor was kept under stirring and thermostated at 70 °C. After 1h, the polymerization was stopped by addition of acidified methanol. The solvent was removed by using a rotavapor. The residue was washed with methanol and the polymer is then dried. 3.0 g of atactic polypropylene (according to 13 C NMR) were obtained. Polymerization of styrene Example 6 Polystyrene homopolymer by the use of the compound 5. A 500 mL bottle containing a stirring bar, closed with a crown cap and equipped with a septum was purged with N 2 . Cyclohexane (100 mL) and styrene (0,4 mol) was added, followed by MAO (11 mL) and compound 5 (0,017 mmol) dissolved in toluene (3 mL). The system was immersed in a thermostatic bath at 60 °C and the mixture was stirred during 180 min. After this time the polymerization was stopped by addition of acidified methanol. The solvent was removed by using a rotavapor. The residue was washed with methanol and the polymer was then dried. 1,56 g of atactic polystyrene (according to 1 H NMR) were obtained. Example 7 Polystyrene homopolymer by the use of the compound 5. A 500 mL bottle containing a stirring bar, closed with a crown cap and equipped with a septum was purged with N 2 . Cyclohexane (100 mL) and styrene (0,4 mol) was added, followed by MAO (11 mL) and compound 5 (0,034 mmol) dissolved in toluene (6 mL). The system was immersed in a thermostatic bath at 60 °C and the mixture was stirred during 180 min. After this time the polymerization was stopped by addition of acidified methanol. The solvent was removed by using a rotavapor. The residue was washed with methanol and the polymer was then dried. 1,63 g of atactic polystyrene (according to 1 H NMR) were obtained.

Claims: Olefin polymerization catalyst component comprising an organometallic compound of general formula I wherein: M is a transition metal of groups 3, 4-10, lanthanide or actinide of the periodic table of the elements, preferably titanium, zirconium or hafnium; each R is independently a structural bridge rigidly connecting two ligands L 1 , L 2 and L 3 and is constituted by 1 to 4 chain atoms selected from carbon, silicon, germanium, oxygen, boron; m, n and o are 0 or 1, with the proviso that m+n+o is 2 or 3; L 1 is a ligand of the cyclopentadienyl type or is isolobal to cyclopentadienyl, preferably a cyclopentadienyl, indenyl or fluorenyl ring, cyclopenteno[b]tiophenyl cyclopenteno[b:b']-dithiophenyl cyclopenteno[b]pyrrolyl, boratabenzene, phospholyl, dihydroindeno[b]indolyl, optionally substituted by one or more R' groups; most preferably a cyclopentadienyl, indenyl or fluorenyl ring, optionally substituted by one or more R 1 groups; L 2 is a ligand of the cyclopentadienyl type or is isolobal to cyclopentadienyl, or a monovalent anionic ligand selected from the group consisting of N, P, B when m+n =2, it is selected from the group consisting of NR 1 , PR 1 , BR 1 , O and S when m+n =1; L 3 is a monovalent anionic ligand selected from the group consisting of N, P, B when n+o =2, it is selected from the group consisting of NR 1 , PR 1 , BR 1 , O and S when n+o =1; R 1 is hydrogen, C 1 -C 20 alkyl, C 3 -C 20 cycloalkyl, C 6 -C 20 aryl. C 3 -C 20 alkenyl, optionally comprising 1 to 5 heteroatoms such as Si, N, P. O, F, Cl, Br; each X is independently selected from the group consisting of hydrogen, halogen, NR 2 2 , R 2 with R 2 equal to C 1 -C 20 alkyl, C 3 -C 20 cycloalkyl, C 6 -C 20 aryl, C 3 -C 20 alkenyl, optionally comprising 1 to 5 heteroatoms such as Si, N, P, O, F, Cl, Br; q is a number whose value is: 0, 1, 2 or 3, depending on the valency of the metal M; D is a neutral Lewis base, p is a number whose value is: 0, 1, 2 or 3. Catalyst component according to claim 1 wherein n is 0 and each R is independently selected from CR 1 2 , SiR 1 2 , CR 1 2 -CR 1 2 , CR 1 2 -SiR 1 2 , SiR 1 2 -SiR 1 2 ; wherein R 1 is independently selected from hydrogen, C 1 -C 20 alkyl, C 3 -C 20 cycloalkyl, C 6 -C 20 aryl, C 3 -C 20 alkenyl, optionally comprising 1 to 5 heteroatoms such as Si, N, P, O, F, Cl, Br. Catalyst component according to claim 1 wherein D is selected from the group consisting of linear or cyclic ethers, amines and phosphines. Catalyst component according to claim 1 wherein the organometallic compound has formula (II) wherein Cp is a cyclopentadienyl or indenyl ring, optionally substituted by one or more R 1 groups, M is selected from Ti, Zr and Hf each R is independently selected from CR 1 2 , SiR 1 2 , CR 1 2 -CR 1 2 , CR 1 2 -SiR 1 2 , SiR 1 2 -SiR 1 2 , wherein R 1 is hydrogen, C 1 -C 20 alkyl, C 3 -C 20 cycloalkyl, C 6 -C 20 aryl, C 3 -C 20 alkenyl, optionally comprising 1 to 5 heteroatoms such as Si, N, P, O, F, Cl, Br. L 2 and L 3 are independently selected from the group consisting of NR 1 , PR 1 , BR 1 , O and S; X is independently selected from the group consisting of hydrogen, halogen, NR 2 , R 2 with R 2 equal to C 1 -C 20 alkyl, C 3 -C 20 cycloalkyl, C 6 -C 20 aryl, C 3 -C 20 alkenyl, optionally comprising 1 to 5 heteroatoms such as Si, N, P, O, F, Cl, Br. D is a neutral Lewis base; p is a number whose value is: 0, 1, 2 or 3. Catalyst component according to claim 1 wherein o is equal to 0. Catalyst component according to claim 1 wherein at least one L group selected from L 1 , L 2 and L 3 and/or one R group contains a -O-SiR 2 3 group. Catalyst component comprising a compound according to claims 1-6 and a porous support. Olefin polymerization catalyst comprising a catalyst component according to claims 1-7 and a cocatalyst selected from aluminoxanes and boron Lewis acids. Process for the preparation of catalyst components according to claims 1-6 including reacting a compound of formula MX q+3 wherein M is a transition metal of groups 3, 4-10, lanthanide or actinide of the periodic table of the elements, X is a monovalent anionic ligand and q is 0, 1, 2, or 3 depending on the valence of the metal M, with a compound of formula III wherein each R is independently a structural bridge rigidly connecting L 1 , L 2 and L 3 and is constituted by 1 to 4 chain atoms selected from carbon, silicon, germanium, oxygen, boron; these atoms can be part of fused rings, aromatic rings, or spiro rings; m, n and o are 0 or 1, with the proviso that m+n+o is 2 or 3; L 1 is a group of the cyclopentadienyl type or is isolobal to cyclopentadienyl, optionally substituted by one or more R 1 groups; L 2 is a group of the cyclopentadienyl type or is isolobal to cyclopentadienyl, or it is selected from the group consisting of N, P, B when m+n=2, it is selected from the group consisting of NR 1 , PR 1 , BR 1 , O and S when m+n=1; L 3 is selected from the group consisting of N, P, B when n+o=2, it is selected from the group consisting of NR 1 , NR 1 , BR 1 , O and S when n+o=1; and R 1 is hydrogen, C 1 -C 20 alkyl, C 3 -C 20 cycloalkyl, C 6 -C 20 aryl, C 3 -C 20 alkenyl, optionally comprising 1 to 5 heteroatoms such as Si, N, P, O, F, Cl or Br. Process for the polymerization of olefins characterized by the use of a catalyst according to claim 8. A compound obtainable by reacting one mole of a compound of formula (III) with three moles of a strong base selected from the group consisting of butyllithium, NaH and KH, wherein said compound of formula (III) is wherein each R is independently a structural bridge rigidly connecting L 1 , L 2 and L 3 and is constituted by 1 to 4 chain atoms selected from carbon, silicon, germanium, oxygen, boron; these atoms can be part of fused rings, aromatic rings, or spiro rings; m, n and o are 0 or 1, with the proviso that m+n+o is 2 or 3; L 1 is a group of the cyclopentadienyl type or is isolobal to cyclopentadienyl, optionally substituted by one or more R 1 groups; L 2 is a ligand of the cyclopentadienyl type or is isolobal to cyclopentadienyl, or it is selected from the group consisting of N, P, B when m+n =2, it is selected from the group consisting of NR 1 , PR 1 , BR 1 , O and S when m+n = 1; L 3 is selected from the group consisting of N, P, B when n+o =2, it is selected from the group consisting of NR 1 , PR 1 , BR 1 , O and S when n+o =1; and R 1 is hydrogen, C 1 -C 20 alkyl, C 3 -C 20 cycloalkyl, C 6 -C 20 aryl, C 3 -C 20 alkenyl, optionally comprising 1 to 5 heteroatoms such as Si, N, P, O, F, Cl or Br.

Inventors: CANO SIERRA JESUS, FLORES DE PACO MIGUEL ANGEL, PENA GARCIA BEGONA, ROYO GRACIA PASCUAL, CANO SIERRA, JESUS, FLORES DE PACO, MIGUEL ANGEL, PENA GARCIA, BEGONA, ROYO GRACIA, PASCUAL
Applicants: REPSOL QUIMICA SA, REPSOL QUIMICA S.A.
Application year: 2001
Main classification: C07F17
IPC codes: C07F19, C08F10, C07F7, C08F4, C08F210, C07F17, C08F110, C07F5