NOVEL RED FLUORESCENT MATERIAL AND ORGANIC ELECTROLUMINESCENT DEVICE CONTAINING SAME

Abstract: A novel red fluorescent material of formula (I) of the present invention has an improved thermostability, and an organic electroluminescent device containing the fluorescent material of formula (I) can provide color ranging from orange to deep red.

Description: NOVEL RED FLUORESCENT MATERIAL AND ORGANIC ELECTROLUMINESCENT DEVICE CONTAINING SAME FTF.T.D OF THF- TNVKNTTON The present invention relates to a novel compound having red-color luminescent characteristics, a process for the preparation thereof and an organic electroluminescent device containing same. RACKCTKOTINT) OF THF. TNVFNTTON Conventional red fluorescent materials used in organic electroluminescent devices generally belong to a class of compounds having an alkyl substituted nitrogen group, e.g., -N(CH 3 ) 2 , as in 4-(dicyanomethylene)-2-memyl-6-(4-dimethylaminostyryl)-4H-pyran (DCM). However, such compounds exhibit low heat stability due to the presence of alkyl substituents, and give partial orange luminescent characteristics, failing to exhibit deep red. ST TM AR V OF THF. TNVFNTTON Accordingly, it is a primary object of the present invention to provide a novel red fluorescent compound having improved thermostability and being capable of emitting color in the range of orange to deep red. It is another object of the present invention to provide a process for preparing said compound. It is a further object of the present invention to provide an organic electroluminescent device comprising said compound. In accordance with one aspect of the present invention, there is provided a novel red fluorescent compound of formula (I): wherein, X is CR^, NR', oxygen or sulfur; Y is NH, oxygen or sulfur; R', R l5 R 2 , R 3 , R 4 , R 5 , R ό and R 7 are each independently hydrogen, C M alkyl, C w alkoxy, aryl, or aryl substituted with C M alkyl or C w alkoxy, R 5 and Re being optionally fused to form a hetero-ring. RKTFF PFSCRTPTTO OF THF. F)K AWTNOS The above and other objects and features of the present invention will become apparent from the following description, when taken in conjunction with the accompanying drawings, which respectively show: FIGs. 1 to 3: NMR spectra of the novel red fluorescent compounds prepared in Examples 1 to 3, respectively; FIG. 4: DSC scan of the compound prepared in Example 1 ; FIG. 5: fluorescence spectrum of the compound prepared in Example 2; FIG. 6: schematic diagram of an organic electroluminescent device prepared in Example 9; and FIGs. 7 to 9: electroluminous spectra, variations of the current density(A/m 2 ) and brightness(cd/m 2 ) as function of applied voltage(V), and change in the luminous effιciency(lnVW) with current density(A/m 2 ), respectively, of the electroluminescent device prepared in Example 9. DF.TATT ,FD PF.SCRTPTTON OF THF. TNVF.NTTON Preferred among the compounds of formula (I) of the present invention are those obtained when X is CRjR or oxygen, Y is oxygen or sulfur, and R' and Rj to R 7 are each independently hydrogen, methyl, isopropyl, t-butyl, methoxy, phenyl, phenyl substituted with methyl, or benzyl; and more preferred are those obtained when X is CRjR , Y is oxygen, and R' and Rj to R 7 are each independently methyl, phenyl or benzyl. The process for preparing the compound of formula (I) of the present invention may be conducted in accordance with Reaction Scheme A as described below: R action Scheme A wherein, X, Y, R', and Ri to R 7 have the same meanings as defined above. Specifically, a compound of formula (I) may be prepared by reacting a pyran derivative of formula (II) with an aldehyde derivative of formula (III) in an alcohol solvent, e.g., methanol, ethanol and propanol, in the presence of an amine such as piperidine. Alternatively, it may be prepared by reacting a compound of formula (II) with a compound of formula (III) in a solvent such as acetic anhydride in the presence of an acid such as phosphoric acid. Such reactions may be performed using molar equivalent amounts of the reactants at a temperature ranging from room temperature to the boiling point of the solvent. A compound of formula (II) employed in the inventive reaction is commercially available, or it may be synthesized in accordance with the method disclosed in US Patent 5,908,581. In addition, a compound of formula (III) may be prepared, in accordance with the Vilsmeier method, by reacting a hetero-ring compound of formula (IV) with POCl 3 in an organic solvent such as dimethylformamide (DMF) as shown in Scheme Reaction B (see US Patent 2,558,285): Reaction Scheme R (IN) (III) wherein, X, Y, R', and Rj to Re have the same meanings as defined above. The organic electroluminescent device of the present invention comprises an organic luminescent layer containing compound of formula (I). The inventive electroluminescent device may be prepared by sequentially stacking on an ITO-coated glass substrate, a hole transport layer, said organic luminescent layer, an electron transport layer (or a luminescent/electron transport layer) and a metallic electrode layer, in accordance with a conventional method. Preferably, the inventive compound of formula (I) may be employed as a doping material for red or orange luminescence. The hole transport layer, luminescent layer and electron transport layer of the inventive electroluminescent device may be formed by a conventional method which may be a wet process, e.g., a spin-coating, doctor-blading, roll-printing and screen-printing method, or a chemical vapor deposition process. The metallic cathode layer may be formed by vapor deposition. Active materials used in the hole transport and electron transport layers may be selected from any of those known in the art, and for the cathode layer, for instance, aluminum, silver, calcium, magnesium, copper or an alloy thereof may be used. The novel red fluorescent material of the present invention has improved thermostability, and the organic electroluminescent device containing same is capable of emitting color in the range of orange to deep red. The present invention is further described and illustrated in Example, which is, however, not intended to limit the scope of the present invention. Preparation Exam le 1 : Preparation of 6,6-dimethyl-3,4,5,6-tetrahydro-2H-l-oxa- 3a-aza-phenalene-8-carbaldehyde (compound of formula (III-a)) The title compound, one of the starting materials for the preparation of the compound of formula (I), was prepared in accordance with Reaction Scheme C as described below: Reaction Scheme C Specifically, 10.91g (0.1 mol) of o-aminophenol (compound (1)) was dissolved into 120ml of isopropanol and cooled to 0 C, and 12.4g (0.12 mol) of acetic anhydride was added thereto and kept at 0~25 C for 1 hour with stirring. Then, the solvent was removed from the reaction mixture under a reduced pressure to obtain 14.6g (yield: 98%) of compound (2). Compound (2), 34ml (4.0 molar equivalent) of dibromoethane and 4.58g of NaOH (1.1 molar equivalent) were added to 150ml of isopropanol and kept at 55~65 C for 2 hours to carry out alkylation. The resulting solution was filtered at 50 C to remove insoluble materials and the solvent was distilled off to obtain 10.3g (yield: 40%) of compound (3). Compound (3) was dissolved in a mixture of 120ml of 6N HC1 and 120ml of ethanol, and heated for 12 hours, followed by distillation of ethanol. The resulting solution was neutralized with NaOH, extracted with ethyl acetate, and the solvent was distilled off to obtain 4.921g (yield: 91%) of compound (4). Compound (4), 4.183g of 4-chloro-2-methyl-2-butene and 2g of calcium carbonate were added to 30ml of DMF, and kept at 70 ° C for 3 hours to carry out N-alkylation. After adding 90ml of water, the resulting solution was extracted with ethyl acetate and the solvent was distilled off to obtain 6.4g (yield: 86.5%) of compound (5). Compound (5) was added to 20ml of methanesulfonic acid and kept at 100 C for 2 hours to obtain 3.4g (yield: 54%) of compound (IV-a). In order to introduce an aldehyde group to compound (IV-a), 1.83ml of POCl 3 was added to 10ml of DMF, cooled to 0 C s and a solution of compound (IV-a) in 5ml of DMF was added thereto. The mixture was heated to 45 ° C and then kept for 12 hours. The reaction mixture was poured into a mixture of lOg of ice and 40g of water, neutralized with NaOH and extracted with chloroform, followed by purification by silica gel chromatography using a mixture of ethyl acetate and hexane (1/4), to obtain 2.527g (yield: 65.4%) of the title compound. 1H NMR (CDC1 3 , 200MHz) δ (ppm) 1.28(s, 6H), 1.77(t, 2H), 3.25(t, 2H), 3.35(t, 2H), 4.21(t, 2H), 7.08(s, 1H), 7.34(s, 1H), 9.62(s, 1H) Preparation Example 2 : Preparation of 8-methoxy-l, 4,4-trimethyl- 1,2,3 ,4-tetra- hydro-quinoline-6-carbaldehyde (compound of formula (III-b)) The title compound, another starting material for the preparation of the compound of formula (I), was prepared in accordance with Reaction Scheme D as described below: Reaction Scheme D (III-b) (IV-b) Specifically, 12.32g (0.1 mol) of o-anicidine (compound (6)), 6g of calcium carbonate and 10.458g of 4-chloro-2-methyl-2-butene were added to 20ml of DMF and kept at 50 ° C for 3 hours with stirring to effect N-alkylation. After adding 90ml of water, the reaction mixture was extracted with ethyl acetate and the solvent was distilled off to obtain 18.47g (yield: 95.1%) of compound (7). Compound (7) was added to 55ml of methanesulfonic acid and kept at 100 ° C for 2 hours with stirring to obtain 9.5g (yield: 55.1%) of compound (8). 2.521g (13.18 mmol) of compound (8) was dissolved in 10ml of DMF, 2.7 lg of dimethylsulfate was added thereto, and kept at 65~70 C for 2 hours with stirring, to obtain 1.12g (yield: 41.4%) of compound (IV-b) . In order to introduce an aldehyde group to compound (IV-b), 0.61ml of POCl 3 was added to 10ml of DMF cooled to 0 and a solution of compound (IV-b) in 2ml of DMF was added thereto. The mixture was heated to 45 C and then kept for 12 hours. The reaction mixture was poured into a mixture of 5g of ice and 20g of water, neutralized with NaOH, and extracted with chloroform, followed by purification by silica gel chromatography using a mixure of ethyl acetate and hexane (1/4), to obtain 0.959g (yield: 75.1%) of the title compound. Η NMR (CDC1 3 , 200MHz) δ (p pm ) 1.29(s, 6H), 1.70(t, 2H), 2.85(s, 3H), 3.14(t, 2H), 3.85(s, 3H), 7.08(s, 1H), 7.37(s, 1H), 9.67(s, 1H) Preparation Example 3 : Preparation of 5,8-dimethoxy-l,4,4-trimethyl-l,2,3,4- tetrahydro-quinoline-6-carbaldehyde (compound of formula (III-c)) The title compound was prepared in accordance with Reaction Scheme E as described below: Reaction Scheme E Specifically, 13.815g (0.1 mol) of dimethoxybenzene (compound (9)) was added to 150ml of acetic acid, heated at 50 C 5 and then 10.52g of 60% nitric acid was added thereto. The solution became light yellow and its temperature rose to 60~70 C . The reaction mixture was allowed to cool and poured into IL of water, when precipitates formed. Compound (10) separated by filtration was suspended into 300ml of ethanol. 1ml of cone. HC1 and 18.43g of Fe were added to the suspension in sequence, heated for 3 hours to carry out reduction, to obtain 8.88g (yield: 58%) of compound (11). Compound (11), 3.2g of calcium carbonate and 6.07g of 4-chloro-2-methyl-2-butene were added to 80ml of DMF and kept at 50 ° C for 3 hours with stirring to perform N-alkylation. 200ml of water was added to the reaction mixture, extracted with ethyl acetate, and the solvent was distilled off to obtain 6.78g (yield: 52.81%) of compound (12). Compound (12) was added to 50ml of methanesulfonic acid, and kept at 100 ° C for 2 hours with stirring to obtain 3.91g (yield: 57.71%) of compound (13). 2.9g (13 mmol) of compound (13) was dissolved into 16ml of DMF, 1.82g of dimethylsulfate was added thereto, and kept at 65~70 C for 2 hours with stirring to obtain 1.65g (yield: 53.4%) of compound (rV-c). In order to introduce an aldehyde group to compound (IV-c), 0.77ml of POCl 3 was added to 10ml of DMF, cooled to 0 C and a solution of compound (IV-c) in 4ml of DMF was added thereto. The mixture was heated to 45 C and then kept for 12 hours. The reaction mixture was poured into a mixture of lOg of ice and 30g of water, neutralized with NaOH, and extracted with chloroform, followed by purification by silica gel chromatography using a mixture of ethyl acetate and hexane (1/4), to obtain 1.324g (yield: 71.8%) of the title compound. Η NMR (CDC1 3 , 200MHz) δ (ppm) 1.29(s, 6H), 1.69(t, 2H), 2.95(s, 3H), 3.13(t, 2H), 3.81(s, 3H), 3.92(s, 3H), 7.30(s, 1H), 9.65(s, 1H) Preparation Example 4 : Preparation of l-benzyl-8-methoxy-4,4-dimethyl-l,2,3,4- tetrahydro-quinoline-6-carbaldehyde (compound of formula (ffl-b)) The title compound was prepared in accordance with Reaction Scheme F as described below: Reaction Scheme F Specifically, 12.32g (0.1 mol) of o-anicidine (compound (6)), 6g of calcium carbonate and 10.458g of 4-chloro-2-methyl-2-butene were added to 20ml of DMF and kept at 50 C for 3 hours with stirring to perform N-alkylation. 90ml of water was added to the reaction mixture, extracted with ethyl acetate, and the solvent was distilled off to obtain 18.47g (yield: 95.1%) of compound (7). Compound (7) was added to 55ml of methanesulfonic acid and kept at 100 C for 2 hours with stirring to obtain 9.5g (yield: 55.1%) of compound (8). 2.521g (13.18 mmol) of compound (8) was dissolved in 10ml of DMF, 1.668g (13.18 mmol) of benzyl chloride was added thereto, and kept at 65-70 ° C for 2 hours with stirring, to obtain 3.1 g (yield: 83.7%) of compound (IV-d). In order to introduce an aldehyde group to compound (IV-d), 2.53g of POCl 3 was added to 10ml of DMF cooled to 0 C and a solution of compound (IV-d) in 2ml of DMF was added thereto. The mixture was heated to 45 C and then kept for 12 hours. The reaction mixture was poured into a mixture of 5g of ice and 20g of water, neutralized with NaOH, and extracted with chloroform, followed by purification by silica gel chromatography using a mixture of ethyl acetate and hexane (1/4), to obtain 2.3g (yield: 67.4%) of the title compound. 1H NMR (CDC1 3 , 200MHz) δ (ppm) 1.29(s, 6H), 1.67(t, 2H), 3.08(t, 2H), 3.87(s, 3H), 4.41(s, 2H), 7.10-7.40(m, 7H), 9.70(s, 1H) Example 1 : Preparation of 2-{2-[2-(6,6-dimethyl-3,4,5,6-tetrahydro-2H-l-oxa-3a- aza-phenalen-8-yl)-vinyl]-6-methyl-pyran-4-ylidene} -malonitrile (compound of formula (I-a)) The compound of formula (I) of the present invention was prepared in accordance with Reaction Scheme G as described below: Reaction Scheme G 0.517g (3.0 mmol) of 4-dicyanomethylene-2,6-dimethyl-4H-pyran (compound (II-a)) and 0.694g (3.0 mmol) of compound (III-a) obtained in Preparation Example 1 were added to 15ml of ethanol, 0.28 lg (3.3 mmol) of piperidine was added thereto and the mixture was refluxed for 12 hours. The solvent was removed from the reaction mixture under a reduced pressure, followed by purification by silica gel chromatography, to obtain 0.55g (yield: 48%) of the title compound as a dark red solid. The DSC(Differential Scanning Calorimeter) analysis result revealed that the melting point and the glass transition temperature of the title compound are 276 C and 120 C 5 respectively. A solution of the title compound in ethylene dichloride exhibited a maximum fluorescence wavelength ranging from 619nm to 636nm (from orange to red), depending on its concentration. Figures 1 and 4 illustrate NMR and DSC scans of the compound thus obtained, respectively. Examples 2 to 8 : Preparation of compound of formula (I) of the present invention The procedures of Example 1 were repeated except that 4-dicyanomethylene-2-phenyl-6-methyl-4H-pyran or 4-dicyanomethylene-2- (2,4,6-trimethyl)phenyl-6-methyl-4H-pyran was used instead of 4-dicyanomethylene-2,6-dimethyl-4H-pyran (compound (ITa)), and one compound selected from compounds (III-b), (IITc) and (Ill-d) obtained in Preparation Examples 2, 3 and 4 was used in place of compound (IITa), to obtain the compounds shown in the Table. An NMR spectrum of the compound obtained in Example 2 is shown in Figure 2, and NMR and fluorescence spectra of the compound obtained in Example 3, in Figures 3 and 5, respectively. Example 9 : Preparation of an Organic Electroluminescent Device Using the compound obtained in Example 3 as a doping material on a luminescent layer composed of tris(8-hydroquinolinato)aluminum (Alq 3 ) host material, an organic electroluminescent device was prepared in accordance with a conventional method. First, a 50nm thick hole transport layer (3) (hole transport material: α. -NPD) was formed on an Indium-tin-oxide(ITO) layer (2) formed on a glass substrate (1) at 10 "6 torr. Alq 3 doped with the compound obtained in Example 3 to a level of 3% was vapor deposited on the hole transport layer to a thickness of 30nm at a rate of 0.03nm/sec to form a luminescent layer (4). Then, an electron transport layer (5) (electron transport material: Alq 3 ) was formed on the luminescent layer to a thickness of 20nm and, subsequently, aluminum was vapor deposited on the electron transport layer to a thickness of 200nm at a rate of lnm/sec at 10 "6 torr to form a cathode layer (6). The schematic diagram of the organic electroluminescent device thus obtained is shown in Figure 6, and the electroluminous spectra, variations of the current density(A/m 2 ) and brightness(cd/m 2 ) as function of applied voltage(V), and the change in luminous efficiency(lm/W) with current density(A/m 2 ) of the device are shown in Figures 7, 8 and 9, respectively. In Figure 8, O corresponds to the brightness and •, the current density. As shown in Figures, the inventive device has stable red luminescence characteristics and can accomplish a high brightness of maximum 12,000 cd/m 2 or more. As can be seen from the above result, the novel fluorescent material of the present invention has improved thermostability and is capable of emitting color in the range of orange to deep red and, therefore, it may be advantageously applied to organic photoconductors, photorefraction thin layer devices, photodiodes and solar cells as well as organic electroluminescent devices. While the invention has been described with respect to the specific embodiments, it should be recognized that various modifications and changes may be made by those skilled in the art to the invention which also fall within the scope of the invention as defined by the appended claims.

Claims: WHAT IS CLAIMED IS: 1. A compound of formula (I) : wherein, X is NR', oxygen or sulfur; Y is NH, oxygen or sulfur; R', R l5 R 2 , R 3 , Rj, R 5 , R and R 7 are each independently hydrogen, C M alkyl, C M alkoxy, aryl, or aryl substituted with C M alkyl or C w alkoxy, R 5 and Re being optionally fused to form a hetero-ring compound. 2. The compound of claim 1, wherein X is CR t R 2 or oxygen, Y is oxygen or sulfur, and R' and R x to R 7 are each independently hydrogen, methyl, isopropyl, t-butyl, methoxy, phenyl, phenyl substituted with methyl, or benzyl. 3. The compound of claim 1 , which is selected from the group consisting of: 4. A process of preparing the compound of claim 1, which comprises reacting a pyrane derivative of formula (II) with an aldehyde of formula (III) in an alcohol solvent in the presence of a base: wherein, wherein, X, Y, R', and Rj to R 7 have the same meanings as defined in claim 1. 5. An organic electroluminescent device comprising an organic luminescent layer containing the compound of claim 1. 6. The organic electroluminescent device of claim 5, wherein the fluorescent material is used as a doping material for red or orange luminescence.

Inventors: HAN KI JONG, HWANG HA KEUN, JUN DAE SEOK, KEUM JI HWAN, KIM YOUNG KYOO, HAN, KI, JONG, HWANG, HA, KEUN, JUN, DAE, SEOK, KEUM, JI, HWAN, KIM, YOUNG, KYOO
Applicants: HAN KI JONG, HWANG HA KEUN, JUN DAE SEOK, KEUM JI HWAN, KIM YOUNG KYOO, NESSDISPLAY CO LTD, HAN, KI, JONG, HWANG, HA, KEUN, JUN, DAE, SEOK, KEUM, JI, HWAN, KIM, YOUNG, KYOO, NESSDISPLAY CO., LTD.
Application year: 2001
Main classification: C09K11
IPC codes: C07D405, C07D498, C09B23, C09K11, H01L51