A METHOD FOR TREATMENT OF HEXAVALENT CHROMIUM COMPOUNDS IN WASTE WATER ORIGINATING FROM PROCESSING OF METALS

Abstract: The invention relates to a method for treating hexavalent chromium compounds occurring in effluents originating from the treatment of metals. In this method, hexavalent chromium compounds are reduced in acid conditions, and then the chromium hydroxide is precipitated by adding a base to the solution, and the sludge-like precipitate thus formed is concentrated by pressure-filtering to a high solid matter content. After this, the chromium hydroxide is dehumidified, heated to form amorphous chromium oxide, and the amorphous chromium oxide is heated to form crystalline chromium oxide.

Description: A me hod for treatment of hexavalent chromium compunds in waste water originating from processing of metals. The invention relates to the method defined in claim 1 for treating hexavalent chromium compounds occurring in waste water originating from the processing of metals. The plating of metals enhances the corrosion resistance and hardness of metals. Chromium plating by electrodeposition uses a plating solution with chromid anhydride (Cr0 3 ) as the chromium source. As chromium trioxide is dissolved in water, chchromic acid H 2 Cr 2 θ 7 and/or chromic acid CrH 2 0 4 are obtained, which dissociate into Cr 2 θ 7 2~ and Cr0 4 2" ions depending on the pH. The common denomination "chromic acid" will be used below to denote dichromic acid and chromic acid. The solution used for chromium plating, i.e. the chromium plating bath, contains, besides chromic acid and (di)chromic acid, a catalyst consisting of acid anions or halogen compounds. The most frequent acid anion source is sulphuric acid. In electrodeposition of metals, the chromium plating solution containing chromic • acid and dissociation products Cr 2 θ 7 2" and CrH 2 θ 4 2" results in rinse and storm waters containing chromic acid and its dissociation products. The chromium plating solution used requires periodical replacement due to impurities (mainly rrivalent chromium compounds, iron and copper) accumulating in the solution. Metal processing at foundries and welding plants also results in effluents containing hexavalent chromium compounds. The hexavalent chromium compounds, such as chromic acid and its dissociation products, are most economically and conveniently precipitated in the form of chromium(III)hydroxide from effluents originating from the metal treatment processes mentioned above. Conventional methods for treating effluents containing chromic acid have focused on the precipitation of chromic acid and its dissociation products present in the effluents in different chromium hydroxide forms and on the reconversion of hydroxides into a form that allows easy transportation. In fact, waste solutions containing chromic acid and its dissociation products are usually treated by regulating the pH of the solution with mineral acid (e.g. HN0 3 , HC1, H 2 S0 4 ) to a value under 2.5 and by adding a reducing agent such as sodium hydrogen sulphate or sodium hydrogen bisulphate to the solution. After this, a base such as NaOH is added to the solution in order to regulate the pH to 7-9, the chromic acid and its dissociation products precipitating as a sludge-like chromium hydroxide deposit Cr(OH) 3 , which is removed from the solution by filtering. A typical process of this kind is described in JP patent specification 63,021,223, in which waste solutions containing dissociation products of chromic acid are treated so that Cr(III) and CR(II) hydroxide precipitate is obtained. Chromium hydroxides (Cr(OH)χ, in which x is 1-6) are classified as hazardous waste in the EU waste list, and for this reason their destruction is problematic and often expensive, involving high waste treatment and transport costs. Concentrating chromium hydroxides into a form that is easier to transport does not eliminate the basic problem, i.e. the destruction of hydroxides classified as hazardous wastes. The deposition of chromium hydroxides at waste dumps results in an increased need for hazardous waste treatment plants and is not economically viable, since industries constantly need virgin chromium for various products and production processes in the metal industry. The chief objective of the invention is to overcome the prior art inconveniences. Thus the chief objective of the invention is to convert hexavalent chromium compounds occurring in effluents originating from the processing of metals into a form where they are no longer classified as hazardous wastes, i.e. into chromium hydroxides. Another objective of the invention is to convert hexavalent chromium compounds occurring in effluents originating from the processing of metals into a recyclable form that can be industrially utilised. A further objective of the invention is to provide a treatment of hexavalent chromium compounds occurring in effluents that is as simple and economical as possible. The invention relates to the method of claim 1 for treating (utilising) hexavalent chromium compounds occurring in effluents from metal processing. Waste water contains 0.5-50 percent by weight, preferably 5-30 percent by weight of chromic acids and/or its dissociation products. In addition, waste water may contain metal impurities (e.g. Fe, As V, alkali metals), acid anions, flocculants and halogen compounds, among other things. The waste water may originate e.g. from plating processes in the metal industry, such as metal chromium plating, grinding dust produced by metal grinding, smelting plants, etc. In the method of the invention, hexavalent cluOmium compounds are reduced in acid conditions, and subsequently the chromium hydroxide is precipitated by adding a base to the solution. The chromium hydroxide is heated in order to be converted into chromium oxide. The heating is performed by initial dehumidification of the chromium hydroxide, resulting in hydrous chromium hydroxide. The hydrous chromium hydroxide thus obtained is heated to a temperature above 300°C, preferably 300-50O°C, at which crystal water is removed and amorphous dichromium trioxide is obtained. When the heating is continued, the amorphous dichromium trioxide starts converting, at about 400-800°C, however usually at about 700°C, into ciystalline dichromium trioxide. When dichromium trioxide is further heated, a brown ciystalline form of dichromium trioxide is first obtained and then a green crystalline form. The crystalline dichromium trioxide is washed, dried and ground to the desired particle size. Before the precipitation of hexavalent chromium compounds as chromium hydroxide in the method, heavy metals such as Fe and Cu are preferably removed from the waste water to avoid their presence in the end product. In the method of the invention, hexavalent chromium is precipitated as chromium hydroxide deposit in two steps: In the first step, the pH of the waste water is regulated to a value under 3, preferably 2-2.5. The pH is " preferably regulated with a mineral acid such as H 2 SO 4 , HNO 3 or HC1. Chromic acid and its dissociation products are reduced, using relatively mild reducing agents such as NaHS04 or Na 2 S 2 θs. In the second step, the pH of the solution is regulated to 7-9, preferably 8.5-9.0 with NaOH, and then the sludge-like Cr(OH) 3 deposit precipitates. The precipitate thus produced usually contains a relatively large amount of water, and for this reason it is further concentrated by means of pressure filtering, for instance. In the method of the invention, the sludge-like precipitate is pressure-filtered to a solid matter content above 20 percent by weight. A high solid matter content has the advantage of shortening the subsequent heating period of chromium hydroxide and of reducing the need for heating energy. After this, the hydrous chromium hydroxide precipitate produced is heated in order to produce various forms of chromium oxide. First the hydroxide precipitate is dehumidified at about 100-140°C. When the precipitate is further heated, crystal water is removed at a temperature of about 300-700°C, however usually at a temperature of 300-500°C, approximately according to the following reaction (1): 2 Cr(OH) 3 x Y H 2 0>Cr 2 0 3 +X H 2 0 (g) (1) The water molecule coefficients Y and X appearing in the reaction (1) depend on the amount of crystal water per chromium hydroxide molecule. As crystal water is removed, amorphous dichromium trioxide is produced. As the amorphous dichromium trioxide is further heated, an exothermic reaction usually starts at about 700°C, in which amorphous dichromium trioxide is converted into crystalline dichromium trioxide according to the following reaction (2): Cr 2 0 3 >α- Cr 2 0 3 (2) First, a brown crystal form of chromium oxide is produced in the reaction, and when the heating is continued to 800-1200°C after the end of the exothermic reaction, this forms turns into a green crystal form. The transition temperatures of chromium hydroxide are not very exact due to the foreign metals such as Fe and Cu usually contained in chromium hydroxide. Thus the transition temperature of amorphous and crystalline dichromium trioxide may drop as low as about 400°C or rise to about 800°C due to impurities. In the method described above, chromium hydroxide is converted into chromium oxide under a pressure of 1 arm. Should the operations nonetheless be performed under decreased or increased pressure, the transition temperatures of the various forms of chromium hydroxide and chromium oxide will naturally change as well. In the method of the invention, the heating of chromium hydroxide is preferably performed in CO or hydrogen atmosphere, i.e. in a reducing environment. To provide e.g. a CO atmosphere, oxygen is displaced by burning hydrocarbon. During heating, the crystal structure evolution can be controlled by means of various carbon forms and carbon sources, such as active carbon, graphite, organic carbon sources, sawdust, paper, etc. After this, the temperature of chromium oxide is further dropped to a temperature under 100°C, and then impurities are washed away from the chromium oxide, it is dried and ground to the desired average particle size 0.05-5 μm, preferably 0.25- 1.3 μm. In the method for preparing chromium oxide described above, dehumidification of the chromium oxide precipitate can be performed by other means known per se, such as heating. Other conceivable means of drying are deep-freeze drying, drying under reduced pressure, etc. The colour of the Cr 2 θ 3 pigment prepared can be varied by varying the drying conditions and the particle size of the dichromium trioxide powder. The yellowiest chromium oxide pigments have a more finely divided particle size, whereas the dark hues have a larger particle size and a bluer colour. The chromium oxide resulting from the method is not classified as hazardous waste, but has proved a safe, non- toxic and non-reacting chemical. Dichromium trioxide Cr 2 0 3 is a commonly used reactant in industries, and it has a notable economic impact. The purposes of use of chrormum oxide include colour pigments, raw materials of fireproof materials, catalysts, grinding agents and coating agents/coating powders. The method of the invention clearly differs from conventional methods of preparing dichromium trioxides both with regard to the objectives of the invention, the reactant used and the production process. Conventional methods have aimed to prepare dichromium trioxide using virgin chrome as the reactant. Roasted with alkali carbonate chromes have yielded alkali chromate, from which alkalide chromate has been further produced. Alkalide chromate has subsequently been calcinated to form dichromium trioxide. As stated above, the objective of the method of the invention is instead to convert chromium hydroxides classified as hazardous waste into a recyclable, industrially usable form: Another objective is an optimally economical and simple utilisation of chrormum(VT) compounds occurring in effluents from metal treatment. Compared to conventional methods, the method of the invention yields the following advantages: The method allows easy conversion of the chromium(VI) compounds occurring in effluents from metal (plating) treatment into industrially usable chromium(III)oxide compounds. The method overcomes the environmental nuisance caused by chrormum hydroxides in converting chromium compounds into stable chromium trioxides. Thus chromium hydroxides originating from effluents from the metal industry no longer constitute hazardous waste material, but a recyclable raw material for industries. The method allows an appreciable decrease in the load on special waste treatment plants, because the method of the invention enables chromium hydroxides obtained from effluents from the metal industry to be recovered for utilisation. The method for preparing dichromium trioxide of the invention also involves lower production costs than conventional methods in the field, which produce chromium oxide from virgin chrome; the method of the invention comprises one single energy-requiring roasting step, whereas two roasting steps are needed when chromes are used. The invention is described in greater detail below by means of the accompanying examples. Example 1 A solution for hard chromium plating of metals contained about 200-300 g/1 of dissociation products of chromic acid Cr 2 0 7 2" and CrH 2 θ 4 2" . The Cu and Fe ions were removed by chemical means from the rinse water for chromium plating, which contained about 2 percent by weight of dissociation products of chromic acid Cr 2 θ 7 2" and CrH 2 θ 4 2" . Then the pH of the rinse water was regulated to less than 2.5 • with concentrated sulphuric acid. Na 2 S 2 θ 5 was added to the solution in order to reduce the chromium (VI) compounds to chromium (III) compounds. Then the pH of the solution was regulated to a value in the range 8.5-9.0 with NaOH and a flocculant was added to the solution, so that the sludge-like Cr(OH) 3 precipitate settled on the bottom of the vessel. The sludge-like precipitate was sedimented and pressure-filtered. The solid precipitate produced contained over 20 percent by weight of solid matters, i.e. mainly chromium(III)hydroxide. Then the solid precipitate containing principally Cr(OH) 3 was heated in an oven, first at 100-140°C for dehumidification, yielding bluish-green hydrous Cr(OH) 3 powder (Cr(OH) 3 xYH 2 0. The powder was further heated to approx. 300-500°C in order to remove the crystal water, whereby amorphous chromium oxide was obtained. The amorphous chromium(III)oxide was converted into brown ciystalline chromium oxide by heating at about 400-800°C, at which an exothermic reaction took place: Cr 2 0 > α-Cr 2 0 3 . During the heating of chromium(III)hydroxide at about 200- 300°C, a certain amount of chromium(VI) was also produced as a by-product. The chromium(VI) was thermally decomposed to Cr(III) and further to the desired crystalline Cr 2 0 3 at about 700°C. After this, the crystalline chromium oxide was allowed to cool to less than 100°C, and then it was freed from impurities (i.a. Cr(VI)) by washing. The wash water was recycled to the waste water treatment. After the washing, the product was dried at about 100-140°C, yielding pure ciystalline Cr 2 0 3 as an end product. The ciystalline chromium(iπ)oxide was eventually ground to an average particle size of 1 μm. Example 2 Figure 1 illustrates the reactions that take place in the chromium hydroxide precipitate during heating. Samples of chromium hydroxide precipitate were heated and their DTG and SDTA curves were deteπnined during the heating. The measuring equipment used was a Mettler Toledo TA8000 TGA850 thermo-scale. Before the deteπnination, the samples were dried at 50°C until their weight was stabilised. As the sample batch was brought to standard weight, its weight dropped by 40-50%, i.e. its solid matter content was 50-60% at the beginning of the measurement. The measurement was performed in nitrogen atmosphere and the rate of temperature increase was 10°C/min. The curves shown in figure 1 are averages of the DTG and SDTA curves of five chromium hydroxide samples. Figure 1 shows the heating temperature/°C on the horizontal axis and the ratio of the percent by weight of the sample to the initial weight 50 /°C after the drying. SDTA = Scanning Differential Thermal Analysis and DTG = Differential Thermo Gravimetry. Of these two, SDTA describes the energy variation rate and DTG the weight variation rate. A study of the DTG weight variation rate curve reveals an average turning point at which free water has left the sample at about 145°C (130-160°C) i.e. at the point PI. At the following turning point of the curve P2 (about 440-470°C) the water bound to the crystal lattice starts escaping and amorphous Cr 2 0 3 to form as the weight variation range slows down. At the point P3 (about 550-585°C) the water bound to the crystal lattice has been removed and the main portion of the amorphous Cr 2 0 3 has been formed as the weight variation rate starts increasing again. At the point P4 (about 700°C) the chromium hydroxide has turned into completely amorphous Cr 2 0 3 . At the point P5 (about 720-750°C) an exothermal reaction starts, in which the amorphous Cr 2 0 3 turns into crystalline α-Cr 2 0 3 as the weight variation rate approaches zero. The SDTA curve, in turn, shows a mild bend at the removal temperature of free water (130-160°C), however, the greatest change of the energy variation rate occurs when the amorphous Cr 2 0 3 starts turning into α-Cr 2 0 3 . At a temperature of about 750-1000°C, the amorphous Cr 2 θ 3 in its totality has turned into brown crystalline α-Cr 2 0 3 , appearing as a bend of the SDTA curve almost towards the horizontal, i.e. the energy variation rate approaches zero. If the brown α-Cr 2 θ 3 is further heated, it turns into its green crystal form.

Claims: Claims 1. A method for treating hexavalent chromium compounds occurring in effluents from the treatment of metals, characterised in that - exavalent chromium compounds are reduced in acid conditions, and then the chrormum hydroxide is precipitated by means of a base addition to the solution - the chromium hydroxide is dehumidified - he chromium hydroxide is heated such that it is first converted into amorphous cliromium oxide and subsequently into ciystalline chromium oxide. 2. A method as defined in claim 1, characterised in that the cliromium hydroxide is heated to 300-800°C in order to remove the crystal water and to prepare amorphous dichromium trioxide. 3. A method as defined in claim 2, characterised in that the amorphous dichromium trioxide is heated to a temperature above 400°C, preferably above 700°C, in order to prepare crystalline dichromium trioxide. 4. A method as defined in any of claims 1-3, characterised in that the chromium hydroxide is heated in a protective gas such as in nitrogen, hydrogen or CO atmosphere. 5. A method as defined in claim 4, characterised in that the chromium hydroxide is heated in a reducing environment such as in hydrogen or CO atmosphere. 6. A method as defined in any of claims 1-5, characterised in that the heating is performed in the presence of active carbon, graphite or any other carbon source. 7. A method as defined in any of claims 1-6, characterised in that the waste water contains 0.5-50 percent by weight of chromic acid and/or its dissociation products. 8. A method as defined in any of claims 1-7, characterised in that the waste water derives from the plating of metals, such as chrormum plating of metals by electrodeposition. 9. A method as defined in any of claims 1-8, characterised in that the chromium compounds are reduced at pH 2-2.5 and the chromium hydroxide precipitate is seciimented with a base at pH 6-9, preferably pH 8-9, in the presence of any flocculants used. 10. A method as defined in claim 9, characterised in that the sludge-like precipitate is concentrated by pressure-filtering to a 20 percent by weight concentration of chromium(III)hydroxide.

Inventors: LAUKKANEN PEKKA, SORANTA PETTERI, SYYNIMAA ARI PEKKA, LAUKKANEN, PEKKA, SORANTA, PETTERI, SYYNIMAA, ARI, PEKKA
Applicants: LAUKKANEN PEKKA, SORANTA PETTERI, SYYNIMAA ARI PEKKA, LAUKKANEN, PEKKA, SORANTA, PETTERI, SYYNIMAA, ARI, PEKKA
Application year: 2001
Main classification: C01G37
IPC codes: C01G37, C02F1, C02F11, C25D21