Crystalline polyesterpolyol and hot-melt adhesive

Abstract: A crystalline polyesterpolyol having a number average molecular weight of 1,500 to 15,000 and obtainable from a polybasic carboxylic acid component and an aliphatic hydrocarbon diol component comprising 1,10-decanediol and/or 1,12-dodecanediol, and a hot-melt adhesive comprising a reaction product of a polyisocyanate and a polyesterpolyol, which contains a crystalline polyesterpolyol having a number average molecular weight of 1,500 to 15,000 and obtainable from a polybasic carboxylic acid component and an aliphatic hydrocarbon diol component comprising 1,10-decanediol and/or 1,12-dodecanediol are provided.

Description: The present invention relates to a polyesterpolyol blend comprising a crystalline polyesterpolyol obtainable from a polybasic carboxylic acid component and an aliphatic hydrocarbon diol component comprising 1,10-decanediol and/or 1,12-dodecanediol. The crystalline polyesterpolyol of the invention is capable of crosslinking with various crosslinking agents, and is useful for producing paints, adhesives, inks, and sealants. The present invention also relates to a hot-melt adhesive comprising a crystalline polyesterpolyol having a number average molecular weight of 1,500 to 15,000 and obtainable from a polybasic carboxylic acid component and an aliphatic hydrocarbon diol component comprising 1,10-decanediol and/or 1,12-dodecanediol. The hot-melt adhesive of the invention necessitates an extremely short period of time for adhesion and is also excellent in adhesion strength, so that it can be used for various purposes as an adhesive. Polyesters are well known compounds in the art and various polyesters are employed. In particular, polyesterpolyols are capable of crosslinking and curing with various crosslinking agents such as isocyanate compounds, and are widely used as paints, adhesives, inks, and sealants. Among them, a crystalline polyesterpolyol has characteristics that it can be handled as a liquid having relatively low viscosity at a temperature of the melting point or higher and it solidifies within a short period of time through recrystallization when it is cooled at or below the crystallizing temperature in addition to its excellent mechanical properties. Owing to the characteristics, its use as components for reactive hot-melt adhesives and hot melt-type ink jet inks have been expanding. Particularly, the market of the reactive hot-melt adhesives have been rapidly growing since they match social needs of lessening solvent and saving energy together with its excellent strength and adhering speed and high applicability to product lines in assembly industries. Furthermore, there is a strong demand for the enhancement of efficiency of continuous working, and therefore, a reactive hot-melt adhesive having more rapid setting rate is desired. In order to meet the demand, combinations of a reactive hot-melt adhesive with an adhesive resin or a thermoplastic polymer have been examined. For example, European Patent Application Publication No. 0232055A describes a combination with an ethylene/vinyl acetate comonomer or a methylstyrene resin, and European Patent Application Publication No. 0246473A describes a combination with an acrylate oligomer. However, such reactive hot-melt adhesive contains a thermoplastic resin in high ratio ever after the curing by crosslinking, so that the decrease of shear strength at high temperature cannot be avoided. On the other hand, European Patent Application Publication No. 0248658A discloses a polyester-type hot-melt adhesive using an aromatic dicarboxylic acid. The use of an aromatic polyester improves the thermal resistance but there is a disadvantage that the viscosity at the melting is too high and therefore the workability at its application remarkably decreases. Hitherto, as the raw materials used for the reactive hot-melt adhesives, terephthalic acid, isophthalic acid, succinic acid, adipic acid, azelaic acid, sebacic acid, dodecanedioic acid, etc. are known as the polybasic carboxylic acid component, and ethylene glycol, propylene glycol, 1,4-butanediol, 1,5-pentanediol, 1,6-hexanediol, 1,4-cyclohexanedimethanol, etc. as the diol component. On the other hand, it is known, as described in Secchaku , vol. 28, No. 8, p. 5 (1984) and ADHESIVE AGE, p. 32, November (1987), that the crystallinity of a polyesterpolyol affects the setting rate. Namely, a polyesterpolyol having high crystallinity is extremely advantageous for accelerating the setting rate. Among the polyesterpolyols obtained from the above monomer combinations, Japanese Patent Laid-Open No. 88686/1990 discloses those wherein dodecanedioic acid and 1,6-hexanediol or sebacic acid and 1,6-hexanediol are used as raw materials for producing a reactive hot-melt adhesive having improved setting rate, a polyesterpolyol wherein dodecanedioic acid and ethylene glycol are used, and the like. However, it becomes difficult to satisfy the demand for further rapid setting with these combinations. EP-A-448825 discloses a method for adhering surfaces comprising the step of applying a polyester polyol onto at least one surface, wherein the polyester polyol has an average molecular weight of at least 4,500 and wherein the polyol is obtainable from a polybasic carboxylic acid component based on dodecanionic diacid and an aliphatic hydrocarbon diol component having at least 6 carbon atoms. EP-A-484761 discloses an adhesive on the basis of a polyester polyol having a molecular weight of between 1,500 and 10,000, obtainable by reacting a diol such as 1,12-dodecanediol with dodecanionic acid, and a polyester having a molecular weight of between 1,000 and 10,000 and a melting point of from 60 to 150°C. US-A-3,503,932 discloses a hydroxy polyester obtained from the reaction of adipic acid and 1,12-dihydroxy-dodecane. WO 99/28367 discloses a polyester polyol having a molecular weight of not greater than 10,000, obtainable by the reaction of a dicarboxylic acid and a diol. It is the object of the invention to provide a polyesterpolyol blend comprising crystalline polyesterpolyol producible from easily available raw materials, capable of rapid setting and rapid drying as a component of adhesives, paints and inks, and imparting sufficient adhesion strength; and further to provide a hot-melt adhesive producible from easily available raw materials, capable of rapid setting and rapid drying, and imparting sufficient adhesion strength. This object is solved by the polyesterpolyol blend of claim 1 and the hot-melt adhesive of claim 7. Preferred embodiments are set forth in the subclaims. The aliphatic hydrocarbon diol component to be used in the invention comprises 1,10-decanediol and 1,12-dodecanediol. Preferred is 1,12-dodecanediol. These are used solely or as a mixture. Furthermore, they can be mixed with an aliphatic hydrocarbon diol component having carbon atoms less than that of 1,10-decanediol. The amount of 1,10-decanediol or 1,12-dodecanediol to be used at that time is not particularly limited but, in the case of obtaining a crystalline polyesterpolyol, the amount is 1 mol% or more, preferably 5 mol% or more, more preferably 20 mol% or more of the total aliphatic hydrocarbon diol component. In particular, at the amount of 20 mol% or more, a high crystalline polyesterpolyol is obtained. The polybasic carboxylic acid component to be used in the invention includes an aliphatic dicarboxylic acid and an aromatic dicarboxylic acid, and includes an aliphatic dicarboxylic acid having 2 to 12 carbon atoms and an aromatic dicarboxylic acid. Preferred is an aliphatic dicarboxylic acid having 2 to 12 carbon atoms, and more preferred is an aliphatic dicarboxylic acid having 2 to 6 carbon atoms. Concrete examples include oxalic acid, succinic acid, adipic acid, pimelic acid, suberic acid, azelaic acid, sebacic acid, dodecanedioic acid, isophthalic acid, terephthalic acid, and the like. Preferred are oxalic acid, succinic acid, adipic acid, pimelic acid, suberic acid, azelaic acid, sebacic acid, and dodecanedioic acid. These may be used solely or as a mixture. The polyesterpolyol according to the invention can be obtained by subjecting the above-described aliphatic hydrocarbon diol component and the polybasic carboxylic acid component to known dehydrative polycondensation. Usually, the equivalent ratio of the hydroxyl group of the aliphatic hydrocarbon diol component and the carboxyl group of the polybasic carboxylic acid component (hydroxyl group/carboxyl group) is preferably from 1.02 to 1.5, more preferably from 1.05 to 1.3. Concretely, the esterification is carried out by subjecting the predetermined amount of the aliphatic hydrocarbon diol component and the polybasic carboxylic acid component to dehydrative polycondensation in the presence or absence of a catalyst at a temperature range of 150 to 250°C for about 3 to 20 hours. As the catalyst, it is preferable to carry out the reaction in the presence of a titanium catalyst such as titanium tetrabutoxide or a tin catalyst such as dibutyltin oxide owing to its acceleration of the dehydrative polycondensation. The catalyst may be charged together with the diol component and the polybasic carboxylic acid component, or may be added after the proceeding of pre-polymerization in the absence of any catalyst. At the production of the polyesterpolyol, it is desirable to carry out the production so that its both ends become almost hydroxyl groups and no terminal carboxyl group is formed. For this purpose, it is particularly effective and thus preferable to add the above-described catalyst after the pre-polymerization. The number average molecular weight of the polyesterpolyol obtainable from a polybasic carboxylic acid component and an aliphatic hydrocarbon diol component comprising 1,10-decanediol and/or 1,12-dodecanediol is from 1,500 to 15,000, preferably from 2,000 to 10,000, more preferably from 3,000 to 8,000. When the molecular weight is less than the range, thermal resistance, chemical resistance and strength at setting are not sufficient. When it is larger than the range, the viscosity at the melting becomes high and therefore the handling becomes difficult. The crystallinity in the invention is evaluated only by the measurement of crystallinity according to X-ray diffraction method (Ruland method) of the polyesterpolyol solidified from the melted state under cooling at a rate of 10°C/minute. The crystallinity is 50% or more. The polyesterpolyol having the crystallinity of 50% to 70% is more preferable. The polyesterpolyol to be used in the invention is a crystalline polyesterpolyol having a number average molecular weight of 1,500 to 15,000, and obtainable from a polybasic carboxylic acid component and an aliphatic hydrocarbon diol component comprising 1,10-decanediol and/or 1,12-dodecanediol. These may be used solely or as a mixture without problem. Moreover, the polyesterpolyol is used in combination with another polyesterpolyol. The amount of the crystalline polyesterpolyol of the invention is 0.1 wt% or more, preferably 0.5 wt% or more. The polyisocyanate to be used in the hot-melt adhesive of the invention includes usually well-known aromatic, aliphatic and cyclic diisocyantes or highly functional or polymeric polyisocyanates. Concrete examples include 1,5-naphthylene diisocyanate, 4,4'-diphenylmethane diisocyanate, 4,4'-diphenyldimethylmethane diisocyanate, 4,4'-dibenzyl diisocyanate, tetraalkyldiphenylmethane diisocyanate, 1,3-phenylene diisocyanate, 1,4-phenylene diisocyanate, tolylene diisocyanate, butane-1,4-diisocyanate, hexamethylene diisocyanate, 2,2,4-trimethylhexamethylene diisocyanate, 2,4,4-trimethylhexamethylene diisocyanate, cyclohexane-1,4-diisocyanate, xylylene diisocyanate, isophorone diisocyanate, dicyclohexylmethane-4,4'-diisocyanate, 1,3-bis(isocyanatomethyl)cyclohexane, methylcyclohexane diisocyanate, and derivatives thereof. The ratio of the polyesterpolyol and the polyisocyanate to be used is not particularly limited, and they can be used within a usual range. Namely, the molar ratio of the OH group of the polyesterpolyol to the NCO group of the polyisocyanate is from 1:1.2 to 1:3.0, preferably 1:1.5 to 1:2.5. The reaction conditions are also not particularly limited and the reaction is carried out under the usual conditions, concretely, at a temperature range of 50 to 150°C for 1 to 5 hours. Also, the reaction may be carried out in a solvent. The viscosity of the hot-melt adhesive obtainable according to the invention is 100,000 cps or less, preferably 1,000 to 50,000 cps, more preferably 3,000 to 40,000 cps at 120°C. The hot-melt adhesive of the invention may be used as it is, and also may be used after the addition of a plasticizer, a thermoplastic polymer, a tackifier, a filler, an antioxidant, and the like which are employed for usual hot-melt adhesives. The hot-melt adhesive obtainable according to the invention is suitable for adhesion step at continuous working process owing to its short period of time required for adhesion. For example, shoemaking industry, lumber-processing industry, paper-manufacturing industry, metal industry, resin-processing industry may be mentioned. EXAMPLES Analytical method (1) Hydroxyl value, acid value and number average molecular weight The hydroxyl value and acid value of the polyesterpolyol were measured in accordance with JIS K 1557, and the number average molecular weight was calculated from the hydroxyl value. (2) Crystallinity The crystallinity was determined by melting the produced polyesterpolyol under heating at the melting point or higher, solidifying the melt under cooling at a rate of 10°C/minute, and, after pulverization, measuring and calculating according to X-ray diffraction method (Ruland method). EXAMPLE 1 Dodecanedioic acid (230.3 g, 1 mol) and 1,12-dodecanediol (222.6 g, 1.1 mol) were charged into a 500 ml flask equipped with a distillation apparatus and the atmosphere in the flask was replaced with nitrogen. When the flask was heated to 160°C, water began to distill off. After stirring at 160°C for 1 hour, stirring was continued at 170°C for 2 hours and at 180°C for 2 hours. Thereafter, the pressure in the flask was reduced to 100 mmHg with stirring for 0.5 hour, followed by stirring under a pressure of 50 mmHg for 0.5 hour and further under a pressure of 10 mmHg for 2 hours. After the pressure was once rendered to normal pressure, titanium tetrabutoxide (9.5 mg) was added thereto and then stirring was carried out again under a pressure of 10 mmHg for 8 hours to complete the dehydrative polycondensation. The hydroxyl value, acid value, the molecular weight and crystallinity measured by the above-described methods were found to be 28, 0.32, 4,010 and 62%, respectively. EXAMPLES 2 TO 15, REFERENCE EXAMPLES 1 TO 6 AND COMPARATIVE EXAMPLES 1 TO 3 Using the diols and the polybasic carboxylic acid components described in Table 1, the polyesterpolyols were produced in a similar manner to Example 1, and then analyzed. Aliphatic hydrocarbon diol component Polybasic carboxylic acid component Hydroxyl value mgKOH/g Acid value mgKOH/g Number average molecular weight Crystallinity (%) Example 1 DDL DDA 28 0.32 4010 62 Reference Example 1 HD:DDL=95:5 DDA 28 0.17 4040 49 Reference Example 2 HD:DDL=90:10 DDA 24 0.22 4600 49 Example 2 HD:DDL=80:20 DDA 33 0.09 3400 53 Example 3 HD:DDL=60:40 DDA 30 0.19 3730 64 Example 4 HD:DDL=20:80 DDA 32 0.13 3160 62 Comparative Example 1 HD DDA 30 0.20 3740 49 Example 5 DDL SEA 33 0.13 3400 60 Example 6 HD:DDL=80:20 SEA 29 0.18 3870 51 Example 7 HD:DDL=60:40 SEA 32 0.23 3510 56 Example 8 HD:DDL=50:50 SEA 27 0.28 4160 59 Example 9 HD:DDL=40:60 SEA 35 0.11 3210 55 Comparative Example 2 HD SEA 25 0.18 4490 47 Example 10 DDL AA 36 0.19 3120 60 Reference Example 3 HD:DDL=80:20 AA 35 0.15 3210 41 Reference Example 4 HD:DDL=60:40 AA 36 0.19 3120 45 Reference Example 5 HD:DDL=40:60 AA 34 0.18 3300 48 Comparative Example 3 HD AA 26 0.30 4320 43 Example 11 DL SBA 24 0.24 4680 50 Example 12 DL AA 28 0.25 4010 50 Reference Example 6 HD:DDL=9:1 DDA:AA=1:4 31 0.20 3570 45 Example 13 DDL SBA 34 0.16 3300 55 Example 14 DDL SUA 29 0.56 3870 54 Example 15 DL DDA 24 0.30 4680 58 DDL: 1,12-dodecanediol, DL: 1,10-decanediol, HD: 1,6-hexanediol DDA: dodecanedioic acid, SEA: sebacic acid, SBA: suberic acid, AA: adipic acid, SUA: succinic acid The ratio of DDL to HD is a molar ratio. The ratio of DDA to AA is also a molar ratio. As one example illustrating the usefulness of the crystalline polyesterpolyol of the invention, a moisture-curing type hot-melt adhesive was synthesized using 4,4'-diphenylmethane diisocyanate (hereinafter, referred to as MDI), and the setting time was measured and compared. EXAMPLE 16 The crystalline polyesterpolyol obtained in Example 1 (DDL+DDA)(80.0 g) was placed in a 300 ml separable flask and, after the replacement with nitrogen, the whole was heated to melt at 120°C. Then, 1/10N toluene solution of dibutyl phosphate was added in a molar amount of 1.2 times larger than that of titanium tetrabutoxide used in the polyesterpolyol synthesis, followed by stirring at 130°C for 2 hours. Thereafter, an adhesive was synthesized by subjecting to dehydration treatment at 120°C at 50 mmHg for 1 hour under stirring at 250 rpm, replacing with nitrogen for 10 minutes, adding MDI heated to 60°C in advance (2.2 molar equivalents is used relative to the crystalline polyesterpolyol) all at once, and stirring at 120°C for further 1.5 hours under a nitrogen atmosphere. The content of isocyanate group, viscosity and setting time were measured upon the resulting adhesive. The measuring method is as follows: The measuring methods of physical properties (1) Content of isocyanate group The content of isocyanate group in the adhesive synthesized by the above method was calculated according to the following method.The synthesized adhesive (3 to 6 g) was placed in a 300 ml Erlenmeyer flask fitted with stopper, weighed and dissolved in toluene (25 ml) thoroughly. Thereto was added 10 ml of a toluene solution of dibutylamine (prepared by dissolving dibutylamine (26 g) in dry toluene (200 ml)) and the whole was well mixed with shaking. After standing for 15 minutes, 2-propanol (100 ml) and bromocresol green indicator were added and then the solution was titrated with N/2 hydrochloric acid under stirring. Content of isocyanate (%) = 21.01 × (B-A) × f × 100/S × 1000 A: amount of N/2 hydrochloric acid required for titration of sample (ml) B: amount of N/2 hydrochloric acid required for titration at blank test (ml) S: weight of polyesterpolyol (g) f: factor of N/2 hydrochloric acid (2) Viscosity measurement It was measured by BH type viscosimeter, rotor No. 7 ( 3.175 mm, L = 50 mm) at a rotation number of 10 rpm and a temperature of 120°C. (3) Measurement of setting time It was measured in accordance with method A of Japan Adhesive Industry Society Standard JAI7. A cardboard (craft liner B flute) is employed as adherend. The size of test pieces was a width of 50 mm and a length of 100 mm, and two kinds of the test pieces were prepared, one of which has a flute direction parallel to the width (test piece material C) and the other of which has a flute direction perpendicular to the width (test piece material D). An adhesive controlled at a melt temperature of 120°C was applied on the surface of the test piece material C parallel to the flute as a string, the test piece material D was laminated therewith so that the flutes crossed each other at the backside of the material D, and the materials were pressed to form a test piece. The conditions for the adhesion were an applying amount of 3 g/m, open time of 2 seconds, and a pressing load of 2 kg. The applying position of the adhesive was determined to be a position of 25 mm apart from the longitudinal end of the test piece material C. With measuring the pressing time by means of a stopwatch, the test pieces were released from the pressing every a certain period of time. Immediately after the releasing, the adhered parts of the adhered test pieces were broken by peeling. At that time, the shortest lapsed time of the pressing at which the broken mode showed material breaking and 80% or more of the adhered test pieces showed a material breaking rate of 80% was determined as setting time. The measurement of setting time was carried out under an environment of the room temperature of 20°C. The obtained results are summarized in Table 2. EXAMPLES 17 TO 30, REFERENCE EXAMPLES 7 to 12 AND COMPARATIVE EXAMPLES 4 TO 6 Using the polyesterpolyols (produced in Examples 2 to 25 and Comparative Examples 1 to 3) and MDI shown in Table 2, adhesives were synthesized in a similar manner to Example 16 and the content of isocyanate group, viscosity and setting time were measured. The obtained results were also shown in Table 2. Polyesterpolyol used Content of isocyanate (wt%) Viscosity (cps) Setting time (sec) Example 16 DDL+DDA 2.40 10000 1 or less Reference Example 7 (HD:DDL=95:5)+DDA 2.55 11000 2 Reference Example 8 (HD:DDL=90:10)+DDA 1.71 57000 3 Example 17 (HD:DDL=80:20)+DDA 2.36 15000 2 Example 18 (HD:DDL=60:40)+DDA 1.70 unmeasured 2 Example 19 (HD:DDL=20:80)+DDA 2.40 34000 1 Comparative Example 4 HD+DDA 2.80 7500 7 Example 20 DDL+SEA 2.26 7900 3 Example 21 (HD:DDL=80:20)+SEA 1.45 18000 3 Example 22 (HD:DDL=60:40)+SEA 2.35 8000 5 Example 23 (HD:DDL=50:50)+SEA 1.92 14000 3 Example 24 (HD:DDL=40:60)+SEA 2.56 7900 2 Comparative Example 5 HD+SEA 2.53 17000 20 Example 25 DDL+AA 2.16 8300 3 Reference Example 9 (HD:DDL=80:20)+AA 2.59 5900 13 Reference Example 10 (HD:DDL=60:40)+AA 2.57 6400 7 Reference Example 11 (HD:DDL=40:60)+AA 2.27 8000 3 Comparative Example 6 HD+AA 2.59 7500 40 Example 26 DL+SBA 1.55 15000 3 Example 27 DL+AA 2.14 15000 3 Reference Example 12 (HD:DDL=9:1)+(DDA:AA=1:4) 2.39 15000 14 Example 28 DDL+SBA 1.67 12000 1 or less Example 29 DDL+SUA 2.51 7500 2 Example 30 DL+DDA 1.62 22000 1 or less EXAMPLES 31 TO 34 Using the polyesterpolyol compositions as shown in Table 3 and MDI, adhesives were synthesized in a similar manner to Example 16, and the content of isocyanate group, viscosity and setting time were measured. The obtained results were also shown in Table 3. Polyesterpolyol composition used (weight ratio) Content of isocyanate (wt%) Viscosity (cps) Setting time (sec) Example 31 (DDL+DDA) + (HD+SEA) 2.40 8700 4 1 99 Example 32 (DDL+DDA) + (HD+SEA) 2.37 8700 3 5 95 Example 33 (DDL+DDA) + (HD+AA) 2.54 7500 13 1 99 Example 34 (DDL+DDA) + (HD+AA) 2.54 8700 13 5 95 According to the invention, a polyesterpolyol blend comprising a crystalline polyesterpolyol can be provided from easily available raw materials. Such polyesterpolyol is capable of crosslinking with various crosslinking agents within a short period of time and is excellent in adhesive strength, and therefore it is useful for producing paints, adhesives, inks, and sealants. Further, it becomes possible to obtain a hot-melt adhesive producible from easily available raw materials, capable of rapid curing and rapid drying, and imparting sufficient adhesion strength.

Claims: A polyesterpolyol blend comprising a crystalline polyesterpolyol having a number average molecular weight of 1,500 to 15,000 and obtainable from a polybasic carboxylic acid component and an aliphatic hydrocarbon diol component comprising 1,10-decanediol and/or 1,12-dodecanediol, wherein the polyesterpolyol has crystallinity of 50% or more in the measurement of crystallinity by X-ray diffraction method (Ruland method) of the polyesterpolyol solidified from the melted state under cooling at a rate of 10°C/minute, and another polyesterpolyol, wherein the crystalline polyesterpolyol is contained in the amount of 0.1 wt% or more of the total polyesterpolyol. The polyester blend according to claim 1, wherein the crystallinity of the crystalline polyesterpolyol is from 50 to 70%. The polyesterpolyol blend according to claim 1 or 2, wherein the aliphatic hydrocarbon diol component contains 1,10-decanediol and/or 1,12-dodecanediol in the amount of 20 mol% or more of the total diol component. The polyesterpolyol blend according to any one of claims 1 to 3, wherein the polybasic carboxylic acid component contains an aliphatic dicarboxylic acid having 2 to 12 carbon atoms. The polyesterpolyol blend according to claim 1, wherein the crystalline polyesterpolyol is contained in the amount of 0.5 wt% or more of the total polyesterpolyol. A hot-melt adhesive comprising a reaction product of a polyisocyanate and the polyesterpolyol blend as described in any one of claims 1 to 5.

Inventors: ADACHI FUMIO, HOSHINO HARUTOSHI, ICHIHASHI HIDEKI, KANEKO YUKIO, KASHIMA MIKITO, MACHIDA TOSHIKAZU, NODA YUMIKI, ADACHI, FUMIO, HOSHINO, HARUTOSHI, ICHIHASHI, HIDEKI, KANEKO, YUKIO, KASHIMA, MIKITO, MACHIDA, TOSHIKAZU, NODA, YUMIKI, Adachi, Fumio, c/o Ube Industries, Ltd., Hoshino, Harutoshi, c/o Ube Industries, Ltd., Ichihashi, Hideki, c/o Ube Industries, Ltd., Kaneko, Yukio, c/o Ube Industries, Ltd., Kashima, Mikito, c/o Ube Industries, Ltd., Machida, Toshikazu, c/o Ube Industries, Ltd., Noda, Yumiki, c/o Ube Industries, Ltd.
Applicants: UBE INDUSTRIES, UBE INDUSTRIES, LTD.
Application year: 2001
Main classification: C08G18
IPC codes: C08G18, C09J175