PROCESS FOR THE STAINING OF WOOD WITH AQUEOUS WOOD STAINS

Abstract: The present invention relates to a process for the staining of wood, which comprises treating the unstained wood with an aqeous preparation comprising a) at least one dye, and b) at least one dye stabilizer of the formulae (I) or (II) in which G1 and G2, independently of one another, are C1-C4 alkyl or together are pentamethylene, Z1 and Z2 are methyl, or Z1 and Z2 form a bridging member which is unsubstituted or substituted by an ester, ether, hydroxyl, oxo, cyanohydrin, amido, amino, carboxyl or urethane radical, E is oxyl or hydroxyl, and X is an inorganic or organic anion, and the total number of cations h corresponds to the total number of anions j, to a wood stain comprising a dye and a dye stabilizer of the formula (I) or (II), and to the use of this wood stain for the staining of wood.

Description: Process for the staining of wood with aqueous wood stains The present invention relates to aqueous wood stains and to their use in a process for the staining of wood. Stained woods, or the dyes applied to the wood often exhibit undesired bleaching or changes in shade as a result of the action of light and/or heat. Furthermore, the stained woods often display a colour unlevelness. The use of solvent-containing wood stains for the photochemical and thermal stabilization of the (unstained) material wood is known, for example, from EP-A-0 943 665. EP-A-0 479 075 discloses the treatment of wood with a wood stain comprising a colorant, a solvent and a stabilizer. There continues to be a need for an improved protection of the stained wood against light and evolution of heat, and for a process which permits even penetration of the wood and uses low-solvent or solvent-free wood stains. The object of the present invention was therefore to provide a process according to which the stained wood would satisfy today's requirements with regard to penetration, photostability and heat stability. It has now been found that using the special wood stains described below it is possible to achieve good penetration and very good stabilization of stained wood. Accordingly, the present invention provides a process for the staining of wood, which comprises treating the unstained wood with an aqueous preparation (stain) comprising a) at least one dye and b) at least one dye stabilizer of the formulae (I) or (II) in which Gi and G 2 , independently of one another, are Cι-C 4 alkyl or together are pentamethylene, Zι and Z 2 are methyl, or Zi and Z 2 form a bridging member which is unsubstituted or substituted by an ester, ether, hydroxyl, oxo, cyanohydrin, amido, amino, carboxyl or urethane radical, E is oxyl or hydroxyl, and X is an inorganic or organic anion, and the total number of cations h corresponds to the total number of anions j. Preference is given to dye stabilizers of the formulae (I) and (II) in which Z, and Z 2 are methyl or a bridging member containing 1-200 carbon atoms and 0-60 oxygen and/or nitrogen atoms. X is, for example, phosphate, carbonate, bicarbonate, nitrate, chloride, bromide, bisulfite, sulfite, bisulfate, sulfate, borate, carboxylate, alkylsulfonate, arylsulfonate or phosphonate, for example diethylenetriaminepentamethylenephosphonate. X as carboxylate is, in particular, a formate, acetate, benzoate, citrate, oxalate, tartrate, acrylate, polyacrylate, fumarate, maleate, itaconate, glycolate, gluconate, malate, mandalate, tiglate, ascorbate, polymethacrylate, nitrilotriacetate, hydroxyethylethylenediaminetriacetate, ethylenediaminetetraacetate or diethylenetriaminepentaacetate. X is preferably chloride, bisulfite, bisulfate, sulfate, phosphate, nitrate, ascorbate, acetate, citrate, ethylenediaminetetraacetate or diethylenetriaminepentaacetate; X is particularly preferably bisulfate or citrate. h and j are preferably 1 -5. As a bridging member, Z^ and Z 2 preferably contain 2 or 3 carbon atoms or 1 or 2 carbon atoms and a nitrogen or oxygen atom which together with the radical of the formulae (I) or (II) form a 5-membered or 6-membered heterocyclic ring which may be further substituted. The substituents of and Z 2 can also contain radicals of sterically hindered amines. Preference is given to compounds of the formulae (I) and (II) containing 1 -4, in particular 1 or 2, sterically hindered amines or sterically hindered ammonium radicals. Aryl is to be understood as meaning, for example, C6-Ci 2 aryl, in particular phenyl or naphthyl, especially phenyl. The dye stabilizers given under b) can be used individually or as mixtures with one another. Alkyl is to be understood as meaning, for example, d-Cι 8 alkyl, such as methyl, ethyl, n-propyl, isopropyl, n-butyl, isobutyl, sec-butyl, tert-butyl, pentyl, hexyl, heptyl, octyl, nonyl, decyl, undecyl, dodecyl, tridecyl, tetradecyl, pentadecyl, hexadecyl, heptadecyl or octadecyl. Alkylene is to be understood as meaning, for example, methylene, 1 ,2-ethylene, 1 ,1 - ethylene, 1 ,3-propylene, 1 ,2-propylene, 1 ,1 -propylene, 2,2-propylene, 1 ,4-butylene, 1 ,3- butylen, 1 ,2-butylene, 1 ,1 -butylene, 2,2-butylene, 2,3-butylene, or -C 5 Hι 0 -, -C 6 Hι 2 -, -C 7 Hι 4 -, -CβHi6-, -C9H18-, -C-10H20-, -C11H22-1 -Cl2H2 ", -C13H26-, -Cι H28-, -C15H30-, -C16H32-, -Cι H 3 - and -Cι 8 H 36 -. Cycioalkyl or cycloalkoxy are to be understood as meaning, for example, C 5 -Ci 2 -cycloalkyl or C 5 -Ci2-cycloalkoxy, such as cyclopentyl, cyclohexyl, cycloheptyl, cyclooctyl, cyclononyl, cyclodecyl, cycloundecyl or cyclododecyl, cyclopentoxy, cycloheptoxy, cyclodecyloxy or cyclododecyloxy. Cycloalkenyl is to be understood as meaning, for example, C 5 -Cι 2 cycloalkenyl, such as cyclopentenyl, cyclohexenyl, cycloheptenyl, cyclooctenyl or cyclononenyl. Aralkyl and aralkoxy are preferably phenylalkyl or phenylalkoxyl, such as benzyl, benzyloxy, α-methylbenzyl, α-methylbenzyloxy, cumyl or cumyloxy. Alkenyi radicals are, for example, C 2 -C 18 alkenyl, in particular allyl. Alkynyl radicals are, for example, C 2 -Cι 2 alkynyl, in particular propargyl. Acyl is, for example, a radical R(C=O)-, in which R is an aliphatic or aromatic radical. Aliphatic or aromatic radical means, for example, an aliphatic or aromatic Ci- C 30 hydrocarbon; for example aryl, alkyl, cycioalkyl, alkenyl, cycloalkenyl, bicycloalkyl, bicycloalkenyl, and a combination of these radicals. Examples of acyl are C 2 -Cι 2 alkanoyl, C 3 -Ci 2 alkenoyl and benzoyl. Examples of aikanoyl are formyl, propionyl, butyryl, pentanoyl, octanoyl and, in particular, acetyl. Alkenoyl is preferably acryloyl or methacryloyl. The alkyl substituents may be linear or branched. Examples of Cι-C 6 alkyl are methyl, ethyl, n-propyl, isopropyl, n-butyl, isobutyl, sec-butyl, tert- butyl, pentyl and hexyl. Examples of C 2 -C 4 alkenyl are ethenyl, propenyl and butenyl. Examples of C C alkyl which is interrupted by one or two oxygen atoms are -CH -O-CH 3 , -CH2-CH2-O-CH3, -CH 2 -CH 2 -O-CH 2 -CH 3 , -CH 2 -O-CH 2 -CH 2 -O-CH3 and -CH 2 -O-CH 2 -O-CH 3 . Preference is given to the dye stabilizers given under b) chosen from the compounds A to EE and A * to EE * and III to lllc E in which E is oxyl or hydroxyl, R is hydrogen or methyl, in the formulae A and A * , n is 1 or 2, if n is 1 , Ri is hydrogen, Cι-Cι 8 alkyl, C 2 -Cι 8 alkenyl, propargyl, glycidyl, C 2 -C 5 oalkyl which is unsubstituted or substituted by one to ten hydroxyl groups and which may be interrupted by one to twenty oxygen atoms, or Ri is Cι-C 4 alkyl substituted by carboxyl or -COOZ, in which Z is hydrogen, d-C 4 alkyl or phenyl or in which Z is Cι-C 4 alkyl substituted by -(COO " ) n M π+ , in which n is a number 1 -3 and M is a metal ion from the first, second or third group of the Periodic Table or is Zn, Cu, Ni or Co, or M is a group N n+ (R 2 ) 4 , in which R 2 is CrC 8 alkyl or benzyl, if n is 2, Ri is Cι-C 12 alkylene, C 4 -Cι 2 alkenylene, xylylene or Cι-C 5 oalkylene which is unsubstituted or substituted by one to ten hydroxyl groups and which may be interrupted by one to twenty oxygen atoms, in the formulae B and B*, m is 1 to 4, if m is 1 , R 2 is C Ci 8 alkyl, C 3 -C 18 alkyl interrupted by -COO-, C 3 -Cι 8 alkyl substituted by COOH or COO-, or R 2 is -CH 2 (OCH 2 CH 2 ) n OCH 3 , in which n is a number from 1 to 12, or R 2 is C 6 -Cι 2 aryl which is unsubstituted or is substituted by one to four C C alkyl, or R 2 is -NHR 3 , in which R 3 is d-Cι 8 alkyl, C 5 -Cι 2 cycloalkyl, C 6 -Cι 2 aryl which is unsubstituted or is substituted by one to four Cι-C alkyl, or R 2 is -N(R 3 ) 2 , in which R 3 is Ci-Cisalkyl, C 5 -Cι 2 cycloalkyl, C 6 -Cι aryl which is unsubstituted or is substituted by one to four CrC 4 alkyl, if m is 2, R 2 is Cι-Cι alkylene, C 4 -Ci 2 alkenylene, xylylene, C 2 -Cι 2 alkylene interrupted by -COO-, C 3 -Cι 8 alkylene substituted by COOH or COO-, or R 2 is -CH 2 (OCH 2 CH2)nOCH2-, in which n is a number from 1 to 12, or R 2 is C 5 -Cι cycloalkylene, C 7 -Cι 5 aralkylene or C 6 -Ci 2 arylene, or R 2 is -NHR 4 NH-, in which R is C 2 -Cι 8 alkylene, C 5 -Cι 2 cycloalkylene, C 8 -Cι 5 aralkylene or Ce-C^arylene, or R 2 is -N(R 3 )R 4 N(R 3 )-, in which R 3 and R 4 are as defined above, or R 2 is -CO- or -NH-CO-NH-, if m is 3, R 2 is C 3 -C 8 alkanetriyl or benzenetriyl, or if m is 4, R 2 is C 5 -C 8 alkanetetrayl or benzenetetrayl, in the formulae C and C*, R 10 is hydrogen, C C 8 alkyl, C 5 -Cι 2 cycloalkyl, C 7 -Cι 5 aralkyl, C 2 -Cι 8 alkanoyl, C 3 -C 5 alkenoyl or benzoyl, x is 1 or 2, if x is 1 , R 11 is hydrogen, Cι-Cι 8 alkyl, C 2 -Cι 8 alkenyl, propargyl, glycidyl, C 2 -C 5 oalkyl which is unsubstituted or substituted by one to ten hydroxyl groups and which may be interrupted by one to twenty oxygen atoms, or R 11 is Cι-C 4 alkyl which is substituted by carboxyl or -COOZ, in which Z is hydrogen, Cι-C 4 alkyl or phenyl, or in which Z is C C alkyl which is substituted by -(COO ' ) n M n+ , in which n is a number from 1 -3, and M is a metal ion from the first, second or third group of the Periodic Table or is Zn, Cu, Ni or Co, or M is a group N n+ (R 2 ) 4 , in which R 2 is hydrogen, C 1 - C 8 alkyl or benzyl, or if x is 2, R 11 is Cι-C 12 alkylene, C 4 -Cι 2 alkenylene, xylylene, or d-Csoalkylene which is unsubstituted or is substituted by one to ten hydroxyl groups and which can be interrupted by one to twenty oxygen atoms, in the formulae D and D*, R 10 has the meaning given above, y is a number from 1 to 4, and R 12 has the meaning of R 2 , In the formulae E and E * , k is 1 or 2, if k IS 1 , R 20 and R 21 , independently of one another, are d-C^alkyl, C 2 -Cι 2 alkenyl or C 7 -Cι 5 aralkyl, or R 2 o is hydrogen, or R 2 o and R 2 ι are together C 2 -C 8 alkylene which can be substituted by hydroxyl, or C 4 -C 22 acyloxyalkylene or if k is 2, R 20 and R 2 ι are together (-CH 2 ) 2 C(CH 2 -)2, in the formulae F and F * , R 30 is hydrogen, Cι-Cι 8 -alkyl, benzyl, glycidyl or C 2 -C 6 -alkoxyalkyl, g is 1 or 2, if g is 1 , R 3 ι has the meaning of Ri if n is 1 , if g is 2, R 3 ι has the meaning of Ri if n is 2, in the formulae G and G * , Qι is -NR 41 or -O-, Ei is Cι-C 3 alkylene, or Ei is -CH 2 -CH(R 2 )-O- , in which R 42 is hydrogen, methyl or phenyl, or Ei is -(CH 2 ) 3 -NH- or Ei is a direct bond, R 4 o is hydrogen or Cι-Cι 8 alkyl, R 4 ι is hydrogen, Cι-C 18 alkyl, C 5 -Ci 2 cycloalkyl, C 7 -Cι 5 aralkyl, Ce-C^aryl, or R 41 is -CH 2 -CH(R 42 )-OH, in which R 42 is as defined above, in the formulae H and H * , p is 1 or 2, T 4 has the meaning of Rn if x is 1 or 2, M and Y, independently of one another, are methylene or carbonyl, where M is, in particular, methylene and Y is carbonyl, in the formulae I and I*, these formulae are a repeating structural part of a polymer, in which Ti is ethylene or propylene, or a repeating structural part derived from a copolymer of an α-olefin and alkyl acrylate or methacrylate, q is a number from 2 to 100, Qι is -N(R 1 )- or -O-, in which R 4 ι is as defined above, in the formulae J and J * , r is 1 or 2, T 7 has the meaning of R T if n is 1 or 2 in the formula A, in the formulae L and L * , u is 1 or 2, Tι 3 has the meaning of R 1 if n is 1 or 2 in the formula A, with the proviso that T 13 is not hydrogen if u is 1 , in the formulae M and M*, Ei and E 2 are -CO- or -N(E 5 )-, in which E 5 is hydrogen, Cι-Cι 2 alkyl or C 4 -C 22 alkoxy- carbonylalkyl, where Ei and E 2 have different meanings, E 3 is hydrogen, Cι-C 3 oalkyl, phenyl which is unsubstituted or substituted by chlorine or C C 4 alkyl, naphthyl which is unsubstituted or substituted by chlorine or Cι-C alkyl, or C 7 -Cι 2 phenylalkyl which is unsubstituted or substituted by Cι-C 4 alkyl, E 4 is hydrogen, d-C^alky!, phenyl, naphthyl or C 7 -Cι 2 phenylalkyl, or E 3 and E 4 together form a C 4 -Ci 7 polymethylene which is unsubstituted or substituted by one to four C C 4 alkyl radicals, in particular by methyl, in the formulae N and N * , Ri has the meaning of R^ in the formula A if n is 1 , G 3 is the direct bond, d-Cι 2 alkylene, phenylene or -NH-Gi-NH-, in which d is d-Cι 2 alky- lene, in the formulae O and O * , Rio has the meaning of R 10 in the formula C, in the formulae P and P * , E 6 is an aliphatic or aromatic tetravalent radical, in particular neopentanetetrayl or benzenetetrayl, in the formulae T and T * , R 5 ι is hydrogen, C Cι 8 alkyl, C 5 -Cι 2 cycloalkyl or C 6 -Cι 0 aryl, R52 is hydrogen or d-Cι 8 alkyl, or R51 and R5 2 together are C -C 8 alkylene, f is 1 or 2, if f is 1 , R50 has the meaning of R-n in the formula C if x is 1 , or R 50 is -(CH 2 ) 2 COOR 54 , in which z is a number from 1 to 4 and RM is hydrogen or Cι-Cι 8 alkyl, or R M is a metal ion from the first, second or third group of the Periodic Table or is -N(R 55 ) , in which R 55 is hydrogen, Cι-Cι 2 alkyl or benzyl, if f is 2, R 5 o has the meaning of Rn in the formula C if x is 2, in the formulae U and IT, R53. RM, R55 and R 56 , independently of one another, are Cι-C alkyl or together form pentamethylene, in the formulae V and V * , R 5 7, R58, R 5 9 and R 60 , independently of one another, are Cι-C alkyl or together form pentamethylene, in the formulae W and W * , Rβi. e2, R 83 and R 64 , independently of one another, are d-C 4 alkyl, or together form pentamethylene, R 65 is d-C 5 alkyl, M is hydrogen or oxygen, in which, in the formulae X to CC and X * to CC * , n is from 2 to 3, Gi is hydrogen, methyl, ethyl, butyl or benzyl, m is a number from 1 to 4, x is a number from 1 to 4, if x is 1 , Ri and R 2 , independently of one another, are d-Cι 8 alkyl which is unsubstituted or substituted by one to five hydroxyl groups and which may be interrupted by one to five oxygen atoms, or C 5 -Ci 2 cycloalkyl, C 7 -Cι 5 aralkyl, C 6 -Cι 0 aryl which is unsubstituted or substituted by one to three d-C 8 alkyl, or Ri is hydrogen, or R, and R 2 together are tetramethyl, pentamethylene, hexamethylene or 3-oxapentamethylene, if x is 2, Ri is hydrogen, Cι-C 8 alkyl which is unsubstituted or substituted by hydroxyl and may be interrupted by one or two oxygen atoms, R 2 is C 2 -Cι 8 alkylene which is unsubstituted or substituted by one to five hydroxyl groups and may be interrupted by one to five oxygen atoms, o-, m- or p-phenylene which is unsubstituted or substituted by one or two d-C 4 alkyl, or R 2 is -(CH 2 )kO[(CH2)kO] (CH 2 )k-, in which k is a number from 2 to 4 and h is a number 1 to 40, or and R 2 together with the two N atoms to which they are bonded form piperazine-1 ,4-diyl, if x is 3, Ri is hydrogen, R 2 is C 4 -C 8 alkylene interrupted by a nitrogen atom, if x is 4, Ri is hydrogen, R 2 is C 6 -C 12 alkylene interrupted by two nitrogen atoms, R 3 is hydrogen, Cι-C 8 alkyl which is unsubstituted or substituted by hydroxyl and may be interrupted by one or two oxygen atoms, p is 2 or 3, and Q is an alkali metal salt, ammonium or N + (Gι) in which Gi is as defined above and in the formulae DD and DD * m is 2 or 3, if m is 2, G is -(CH 2 CHR-O) r CH 2 CHR- in which r is a number from 0 to 3, and R is hydrogen or methyl and if m is 3, G is glyceryl, in the formulae EE and EE * G 2 is -CN, -CONH 2 or -COOG 3 , in which G 3 is hydrogen, d-Cι 8 alkyl or phenyl, X is an inorganic or organic anion, where the total amount of the cations h corresponds to the total amount of the anions j; and in which, in the formulae III to lllc, An is ORioi 0r NRinRii 2 , R 1 01 is C 2 -C alkenyl, propargyl, glycidyl, C 2 -C 6 alkyl which is unsubstituted or substituted by one to three hydroxyl groups and may be interrupted by one or two oxygen atoms, or R 101 is d-C alkyl which is substituted by carboxyl or an alkali metal, ammonium or Cι-C 4 alkylammonium salts, or R 101 is alkyl which is substituted by -COOE10, in which E 1 0 is methyl or ethyl, R 102 is C 3 -C 5 alkyl which is interrupted by -COO- or by -CO-, or R10 2 is -CH2(OCH 2 CH 2 )cOCH 3 , in which c is a number from 1 to 4, or R10 2 is -NHR 1 03, in which Rι 03 is CrC 4 alkyl, a is a number from 2 to 4, if a is 2, T11 is -(CH2CHRιoo-O)dCH 2 CHRιoo-, in which d is 0 or 1 , and R100 is hydrogen or methyl, if a is 3, T 11 is glyceryl, if a is 4, T11 is neopentanetetrayl, b is 2 or 3, if b is 2, G11 is -(CH 2 CHRιoo-O) e CH 2 CHRιoo-, in which e is a number from 0 to 3 and R100 is hydrogen or methyl, and if b is 3, G1 1 is glyceryl, Rm is hydrogen, Cι-C alkyl which is unsubstituted or substituted by one or two hydroxyl groups and may be interrupted by one or two oxygen atoms, Rn 2 is -CO-Rιι 3 , in which R 113 has the meaning of Rm or Rn 3 is -NHR , in which R 114 is Cι-C alkyl which is unsubstituted or substituted by one or two hydroxyl groups and/or by Cι-C 2 -alkoxy, or Rm and R 112 together are -CO-CH 2 CH 2 -CO-, -CO-CH=CH-CO- or -(CH 2 ) 6 -CO-, with the proviso that if R 113 is Cι-C 4 alkyl, R is not hydrogen. Important dye stabilizers for the process according to the invention are the compounds of the formulae A, A * , B, B * , C, C * , D, D * , Q, Q * , R, R * , S or S * , X, X * , Y, Y * , Z and Z * , in which E is oxyl or hydroxyl, and R is hydrogen, in the formulae A and A * n is 1 or 2, if n is 1 , Ri is hydrogen, d-C 6 alkyl, C 2 -C 6 alkenyi, propargyl, glycidyl, C 2 -C 2 oalkyl which is unsubstituted or substituted by one to five hydroxyl groups and may be interrupted by one to ten oxygen atoms, or Ri is d-C 4 alkyl which is substituted by carboxyl or -COOZ, in which Z is hydrogen or Cι-C alkyl, if n is 2, Ri is Cι-C 8 alkylene, C -C 8 alkenylene, C 2 -C oalkylene which is unsubstituted or substituted by one to five hydroxyl groups and may be interrupted by one to ten oxygen atoms, in the formulae B and B* m is 1 or 2, if m is 1 , R 2 is Cι-C 4 alkyi, or R 2 is CH 2 (OCH 2 CH 2 ) n OCH 3 , in which n is a number from 1 to 12, or R 2 is phenyl which is unsubstituted or substituted by one to three methyl groups, or R 2 is -NHR 3 , in which R 3 is d-C alkyl or phenyl which is unsubstituted or is substituted by one or two methyl groups, if m is 2, R is Cι-C 8 alkylene, C 4 -C 8 alkenylene, or R 2 is -CH 2 (OCH 2 CH 2 ) n OCH 2 -, in which n is a number from 1 to 12, R 2 is NHR 4 NH, in which R 4 is C 2 -C 6 alkyl, C 8 -d 5 aralkylene or C 6 -Cι 2 arylene, or R 2 is -CO- or -NHCONH, in the formulae C and C * , Rio is hydrogen or Cι-C 3 alkanoyl, x is 1 or 2, if x is 1 , Rn is hydrogen, Cι-C 6 alkyl or glycidyl, or Rn is Cι-C 4 alkyl which is substituted by carboxyl or COOZ, in which Z is hydrogen or Cι-C 4 alkyl, if x is 2, Rn is d-C 6 alkylene, in the formulae D and D*, Rio is hydrogen, y is 1 or 2, and Rι 2 has the meaning given above for R 2 , in the formulae Y, Y*, Z and Z*, x is 1 or 2, if x is 1 , Ri and R 2 , independently of one another, are d-C 4 alkyl, or Ri and R 2 together form tetramethylene or pentamethylene, R 2 is hydrogen or d-C 4 alkyl substituted by hydroxyl, if x is 2, Ri is hydrogen, or Cι-C alkyl substituted by hydroxyl, R 2 is C 2 -C 6 alkylene, and R 3 is as defined above. Particularly important dye stabilizers for the process according to the invention are the compounds of the formulae A, A * , B, B * , C, C * , D, D * , Q, Q * , R and R * , in which E is oxyl or hydroxyl and R is hydrogen, in the formulae A and A * , h isl , Ri is hydrogen, d-C 4 alkyl, glycidyl, C 2 -C 4 alkyl which is unsubstituted or substituted by one or two hydroxyl groups and may be interrupted by one or two oxygen atoms, or Ri is Ci- 4 alkyl which is substituted by -COOZ, in which Z is hydrogen or Cι-C alkyl, in the formulae B and B * , m is 1 or 2, R 2 is Cι-C 4 alkyl, or R 2 is CH 2 (OCH 2 CH 2 )nOCH 3 , in which n is a number 1 to 4, if m is 2, R is Cι-C 8 alkylene, in the formulae C and C * , Rio is hydrogen or d-C 2 alkanoyl, x is 1 or 2, if x is 1 , Rn is hydrogen, Cι-C alkyl or glycidyl, or Rn is Cι-C alkyl which is substituted by -COOZ, in which Z is hydrogen or d-C 4 alkyl, if x is 2, Rn is d-C 6 alkylene, in the formulae D and D*. Rio is hydrogen, y is 1 or 2, and Ri 2 has the meaning of R 2 . Very particularly important dye stabilizers for the process according to the invention are the compounds: (a) bis(1 -oxyl-2,2,6,6-tetramethylpiperidin-4-yl) sebacate; (b) bis(1 -hydroxy-2,2,6,6-tetramethylpiperidin-4-yl) sebacate; (c) 1 -hydroxy-2,2,6,6-tetramethyl-4-acetoxypiperidinium citrate; (d) 1 -oxyl-2,2,6,6-tetramethyl-4-acetamidopiperidine; (e) 1 -hydroxy-2,2,6,6-tetramethyl-4-acetamidopiperidine; (f) 1 -hydroxy-2,2,6,6-tetramethyl-4-acetamidopiperidinium bisulfate; (g) 1 -oxyl-2,2,6,6-tetramethyl-4-oxopiperidine; (h) 1-hydroxy -2,2,6,6-tetramethyl-4-oxopiperidine; (i) 1-hydroxy -2,2,6,6-tetramethyl-4-oxopiperidinium acetate; 0) 1 -oxyl-2,2,6,6-tetramethyl-4-methoxypiperidine; (k) 1 -hydroxy-2,2,6,6-tetramethyl-4-methoxypiperidine; (I) 1 -hydroxy-2,2,6,6-tetramethyl-4-methoxypiperidinium acetate; (m) 1 -oxyl-2,2,6,6-tetramethyl-4-acetoxypiperidine; (n) 1 -hydroxy-2,2,6,6-tetramethyl-4-acetoxypiperidine; (o) 1 -oxyl-2,2,6,6-tetramethyl-4-propoxypiperidine; (p) 1 -hydroxy-2,2,6,6-tetramethyl-4-propoxy-piperidinium acetate; (q) 1 -hydroxy-2,2,6,6-tetramethyl-4-propoxypiperidine; (r) 1-oxyl-2,2,6,6-tetramethyl-4-(2-hydroxy-4-oxapentoxy)piperidine; (s) 1 -hydroxy-2,2,6,6-tetramethyl-4-(2-hydroxy-4-oxapentoxy)piperidinium acetate; (t) 1 -oxyl-2,2,6,6-tetramethyl-4-hydroxypiperidine; (u) 1 -hydroxy-2,2,6,6-tetramethyl-4-hydroxypiperidine; (v) 1 -hydroxy-2,2,6,6-tetramethyl-4-hydroxypiperidinium chloride; (w) 1 -hydroxy-2,2,6,6-tetramethyl-4-hydroxypiperidinium acetate; (x) 1 -hydroxy-2,2,6,6-tetramethyl-4-hydroxypiperidinium bisulfate; (y) 1 -hydroxy-2,2,6,6-tetramethyl-4-hydroxypiperidinium citrate; (z) bis(1-hydroxy-2,2,6,6-tetramethyl-4-hydroxypiperidinium) citrate; (aa) tris(1 -hydroxy-2,2,6,6-tetramethyl-4-hydroxypiperidinium) citrate; (bb) tetra(1 -hydroxy-2,2,6,6-tetramethyl-4-hydroxypiperidinium) ethylenediaminetetraacetate; (cc) tetra(1-hydroxy-2,2,6,6-tetramethyl-4-acetamidopiperidinium) ethylenediaminetetraacetate; (dd) tetra(1 -hydroxy-2,2,6,6-tetramethyl-4-oxopiperidinium) ethylenediaminetetraacetate; (ee) penta(1 -hydroxy-2,2,6,6-tetramethyl-4-hydroxypiperidinium) diethylenetriaminepentaacetate; (ff) penta(1 -hydroxy-2,2,6,6-tetramethyl-4-acetamidopiperidinium) diethylenetriaminepentaacetate; (gg) penta(1 -hydroxy-2,2,6,6-tetramethyl-4-oxopiperidinium) diethylenetriaminepentaacetate; (hh) tri(1 -hydroxy-2,2,6,6-tetramethyl-4-hydroxypiperidinium) nitrilotriacetate; (ii) tri(1 -hydroxy-2,2,6,6-tetramethyl-4-acetamidopiperidinium) nitrilotriacetate; (jj) tri(1 -hydroxy-2,2,6,6-tetramethyl-4-oxopiperidinium) nitrilotriacetate; (kk) penta(1-hydroxy-2,2,6,6-tetramethyl-4-hydroxypiperidinium) diethylenetriaminepentamethylenephosphonate; (II) penta(1 -hydroxy-2,2,6,6-tetramethyl-4-acetamidopipehdinium) diethylenetriaminepentamethylenephosphonate; (mm) penta(1 -hydroxy-2,2,6,6-tetramethyl-4-oxopiperidinium) diethylenetriaminepentamethylenephosphonate. Preferred dye stabilizers in the process according to the invention are the compounds 1 -oxyl-2,2,6,6-tetramethyl-4-hydroxypiperidine; 1 -hydroxy-2,2,6,6-tetramethyl-4-hydroxy- piperidine; 1-hydroxy-2,2,6,6-tetramethyl-4-hydroxypiperidinium chloride; 1-hydroxy- 2,2,6,6-tetramethyl-4-hydroxypiperidinium acetate; 1 -hydroxy-2,2,6,6-tetramethyl- 4-hydroxypiperidinium bisulfate; 1 -hydroxy-2,2,6,6-tetramethyl-4-hydroxypiperidinium citrate; bis(1 -hydroxy-2,2,6,6-tetramethyl-4-hydroxypiperidinium) citrate; tris(1 -hydroxy- 2,2,6,6-tetramethyl-4-hydroxypiperidinium) citrate; tetra(1 -hydroxy-2,2,6,6-tetramethyl- 4-hydroxypiperidinium) ethylenediaminetetraacetate; tetra(1 -hydroxy-2,2,6,6-tetramethyl- 4-acetamidopiperidinium) ethylenediaminetetraacetate; tetra(1 -hydroxy-2,2,6,6-tetramethyl- 4-oxopiperidinium) ethylenediaminetetraacetate; penta(1 -hydroxy-2,2,6,6-tetramethyl- 4-hydroxypiperidinium) diethylenetriaminepentaacetate; penta(1 -hydroxy-2,2,6,6-tetramethyl- 4-acetamidopiperidinium) diethylenetriaminepentaacetate and penta(1 -hydroxy- 2,2,6,6-tetramethyl-4-oxopiperidinium) diethylenetriaminepentaacetate. The dye stabilizer which is very particularly preferably used in the process according to the invention is the compound 1-oxyl-2,2,6,6-tetramethyl-4-hydroxypiperidine of the formula The compounds given above and used as dye stabilizers, and the preparation thereof are known, for example, from EP-A-0 943 665. The present invention further provides for the use of the dye stabilizers of the formulae as compositions for protecting stained woods against the effect of light and heat, where G 1 ( G 2 , Z , Z 2 , E, X, h and j have the meanings and preferred meanings given above. The dye stabilizers of the formula (I) or (II) are usually used in an amount of from 1 to 10% by weight, preferably 2 to 6% by weight, based on the weight of the wood to be treated. Dyes which are suitable for use in the process according to the invention for the staining of wood are all customary dyes used in wood staining. In particular, acid dyes, and also cationic dyes, reactive dyes, and metal complex dyes are suitable for use in the process according to the invention. Acid dyes are, for example, those dyes described in the Colour Index, 3rd edition (3rd revision 1987 including Additions and Amendments up to No. 85) under "Acid Dyes". The anionic dyes which can be used may belong to a wide variety of dye classes and may contain one or more sulfonic acid groups. Examples are triphenylmethane dyes with at least two sulfonic acid groups, heavy-metal-free monoazo and disazo dyes each with one or more sulfonic acid groups and heavy-metal-containing, namely copper-, chromium-, nickel- or cobalt-containing monoazo, bisazo, azomethine and formazan dyes, in particular metallized dyes which contain two molecules of azo dye or one molecule of azo dye and one molecule of azomethine dye bonded to a metal atom, especially those which contain mono- and/or disazo dyes and/or azomethine dyes as ligands, and a chromium or cobalt ion as central atom, and also anthraquinone dyes, in particular 1-amino-4-arylaminoanthraquinone-2- sulfonic acids and 1 ,4-diarylamino- or 1-cycloalkylamino-4-arylaminoanthraquinonesulfonic acids. Examples of cationic dyes are those dyes which are described in the Colour Index, 3rd edition, (3rd revision 1987 including additions and amendments up to No.85) under "Basic Dyes". The cationic dyes which can be used may belong to a very wide variety of classes of dye. In particular, the cationic monoazo, anthraquinone and oxazine dyes are used in the process according to the invention. Metal complex dyes are to be understood as meaning, for example, the metal-containing acid dyes described above under acid dyes, and also 1 :1 or 1 :2-metal complex dyes which do not have water-solubilizing groups, in particular do not have sulfo groups. Of the metal complex dyes, particular importance is given to the copper and cobalt complexes of azo, quinone oxime and hydroxyanthraquinone dyes. The reactive dyes are, for example, those dyes described in the Colour Index, 3rd edition (3rd Revision 1987 including Additions and Amendments up to No.85) under "Reactive Dyes". Examples of reactive dyes are dyes from the group of the monoazo, disazo, polyazo, metal complex azo, anthraquinone, phthalocyanine, formazan or dioxazine dyes which contain at least one reactive group. These dyes preferably also contain at least one sulfo group. Reactive groups are understood as meaning radicals which are reactive towards fibres and which are able to react with the hydroxyl groups of cellulose, the amino, carboxyl, hydroxyl and mercapto groups of wool or silk, or with the amino or, where appropriate, the carboxyl groups of synthetic polyamides to form chemical covalent bonds. The reactive groups are usually joined to the dye radical directly or via a bridging element. Suitable reactive groups are, for example, those which have at least one substituent which can be detached from an aliphatic, aromatic or heterocyclic radical, or those in which the radicals have a radical suitable for reaction with the fibre material, for example a halogenotriazinyl, halogenopyrimidinyl or vinyl radical. Of particular preference in the process according to the invention are the dyes of the formulae The dyes of the formulae (1) to (53) are known. Very particular preference is given in the process according to the invention to the dyes of the formulae (1 ), (2), (3), (8), (12), (26), (27), (28), (29), (30), (31 ), (34), (42), (46), (48), (49), (50), (51), (52) and (53). The present invention further provides an aqueous wood stain comprising at least one dye suitable for the staining of wood and at least one dye stabilizer of the formulae (I) or (II) where for Gi, G 2 , Zi, Z 2 , E, X, h and j, and for the dyes used, the meanings and preferred meanings given above apply. The wood stain according to the invention can also comprise further additives, for example UV absorbers, fungicides or insecticides. Examples of UV absorbers are the UV absorbers of the benzotriazole, 2-hydroxybenzophenone, 2-hydroxy-1 ,3,5-triazine and oxalanilide series. Examples of fungicides are 1-chloronaphthalene and pentachlorophenol. Examples of insecticides are DDT, cypermethrin, propiconazole and parathion. Furthermore, the wood stain can comprise organic solvents, in particular glycols, polyglycols, ketones or glycol ethers, and especially alcohols. Wood which can be stained and treated with the dye stabilizer used according to the invention is primarily to be understood as meaning shaped wooden bodies with extensive surfaces, for example wooden planks, plywood and chipboard, which may be veneered, carved wooden objects, and wooden sections glued, nailed or screwed together to give, for example, furniture, but also wood in finely divided form, for example wood chips or sawdust. Also suitable for the process according to the invention are thin wooden boards which are prepared by continuously shaving tree-trunks and which are joined together, e.g. glued together, only after they have been stained to give thicker boards or workpieces. The treatment of the wood to be stained can be carried out, for example, by firstly staining the wood with a dye, optionally drying it and then treating it with a dye stabilizer of the formula (I) or (II), or by treating the wood to be stained directly with a wood stain comprising a dye and a dye stabilizer of the formula (I) or (II). The treatment of the stained wood with the dye stabilizer of the formula (I) or (II) can be carried out, for example, by treating the stained and optionally dried wood with an aqueous formulation of the dye stabilizer of the formula (I) or (II), or by incorporating the dye stabilizer of the formula (I) or (II) into a commercially available nitrocellulose lacquer with which the stained and optionally dried wood is then coated. Depending on the nature and the type of wood, and the contact times of the wood stains comprising a dye stabilizer or a dye stabilizer and a dye, the dye can lie directly on the surface of the wood material or, advantageously, can penetrate deeper inside the wood. The wood stain according to the invention is applied to the wood using customary methods, for example by immersing the wood in a bath of the wood stain, by paint-brushing, spraying or by knife-coating. The exposure time here can be up to several hours, and the temperature of the wood stain bath can generally be between 20 and about 110°C. When the treatment is complete, the wooden objects are generally dried in the air at room temperature. The treated wood can, however, also be dried at elevated temperatures up to about 100°C, e.g. in a convection drying cabinet. The wood stain according to the invention can be used to treat all customary types of wood, for example pine, spruce, fir, oak, ash, beech, maple, walnut tree, pear tree, teak, mahogany, chestnut, birch tree, larch, hazelnut, lime tree, willow, poplar, elm, Scots pine, plane tree, obeche or aspen. The examples below serve to illustrate the invention. Unless stated otherwise, the parts are parts by weight and the percentages are percentages by weight. The temperatures are given in degrees Celsius. The relationship between parts by weight and parts by volume is the same as that between grams and cubic centimetres. Example 1 : A 100 ml bomb of a pressure dyeing apparatus is charged with a liquor consisting of 80 ml of water (adjusted to a pH between 6.5 and 7.0) and 0.08 g of the dye of the formula To this are added 4.0 g of a 0.8 mm-thick obeche board. The bomb is sealed and heated to 110°C. After agitation for 4 hours at this temperature, the contents of the bomb are cooled, and the stained piece of wood is washed in cold water and dried. An aqueous solution of 20.0 g/l of the dye stabilizer of the formula is applied to the stained and dried piece of wood using a knife-coater (groove depth 24 microns) and dried. This gives an even red coloration with complete penetration in the cross section and a very good light-fastness. Example 2: A 0.8 mm wooden board made of ash is sanded on the upper side using fine sandpaper, moistened with a cloth, dried and again very carefully sanded. All of the wood dust is then brushed off the surface. Using a paintbrush or a hand coater, a stain consisting of 93 parts by weight of water, 4 parts by weight of the dye stabilizer of the formula (Hid) dissolved in the water and 3 parts by weight of a 20% aqueous commercial form of the dye of the formula is applied to the wood surface prepared in this way in an amount of about 100 g/m 2 . The stained wood is then dried in the air. This gives a brilliant red-coloured wood with a very good light-fastness. (The ready-stained wood can then be coated with a commercially available nitrocellulose lacquer.) Example 3: A 0.8 mm wooden board made of ash is sanded on the upper side using fine sandpaper, moistened with a cloth, dried and again very carefully sanded. All of the wood dust is then brushed off the surface. Using a paint brush or hand coater, a dye preparation consisting of 97 parts by weight of water and 3 parts by weight of a 20% commercial form of the dye of the formula (45) is applied to the wood surface prepared in this way in an amount of about 100 g/m 2 and dried. The stained wood is then treated with a mordant consisting of 96 parts by weight of water and 4 parts by weight of the dye stabilizer of the formula (Hid). The wood is then dried in the air. This gives a brilliant red-coloured wood with a very good light-fastness. (The ready-stained wood can then be coated with a commercially available nitrocellulose lacquer.) Example 4: A 0.8 mm wood board made of ash is sanded on the upper side using fine sandpaper, moistened with a cloth, dried and again sanded very carefully. All of the wood dust is then brushed off the surface. Using a paint brush or hand coater, a dye preparation consisting of 97 parts by weight of water and 3 parts by weight of a 20% commercial form of the dye of the formula (45) is applied to the wood surface prepared in this way in an amount of about 100 g/m 2 and dried. The stained wood is then coated with a commercially available nitrocellulose lacquer in which 4 parts by weight of the dye stabilizer of the formula has been incorporated into 96 parts by weight of the lacquer. The wood is then dried in the air. This gives a brilliant red-coloured wood with a very good light-fastness. Example 5: The procedure is as stated in Examples 2 to 4, but using, instead of the dye of the formula (45), the same amount of the dye of the formula H 2 N This gives a blue-coloured wood with a very good light-fastness. Example 6: A 0.8 mm wooden board made of ash is sanded on the upper side using fine sandpaper, moistened with a cloth, dried and sanded again very carefully. All of the wood dust is then brushed off the surface. Using a paint brush or hand coater, a stain consisting of 96 parts by weight of water, 3 parts by weight of the dye stabilizer of the formula (Hid) dissolved in the water and 1 part by weight of a 20% aqueous commercial form of the dye of the formula is applied to the wood surface prepared in this way in an amount of about 100 g/m 2 . The stained wood is dried in the air. This gives a yellow-coloured wood with a very good light-fastness. (The ready-stained wood can then be coated with a commercially available nitrocellulose lacquer.) Example 7: The procedure is as stated in Example 6, but using, instead of the dye of the formula (I), the same amount of the dye of the formula (2). This gives a red-coloured wood with a very good light-fastness. (The ready-stained wood can then be coated with a commercially available nitrocellulose lacquer.) Example 8: The procedure is as given in Example 6, but using, instead of the dye of the formula (1 ), the same amount of the dye of the formula (3). This gives a blue-coloured wood with a very good light-fastness. (The ready-stained wood can then be coated with a commercially available nitrocellulose lacquer.) Example 9: The procedure is as given in Example 6, but using, instead of the dye of the formula (1), the same amount of the dye of the formula (8). This gives a blue-coloured wood with a very good light-fastness. (The ready-stained wood can then be coated with a commercially available nitrocellulose lacquer.) Example 10: The procedure is as given in Example 6, but using, instead of the dye of the formula (1), the same amount of the dye of the formula (12). This gives a blue-coloured wood with a very good light-fastness. (The ready-stained wood can then be coated with a commercially available nitrocellulose lacquer.) Example 12: The procedure is as given in Example 6, but using, instead of the dye of the formula (1 ), the same amount of the dye of the formula (26). This gives a yellow-coloured wood with a very good light-fastness. (The ready-stained wood can then be coated with a commercially available nitrocellulose lacquer.) Example 13: The procedure is as given in Example 6, but using, instead of the dye of the formula (1), the same amount of the dye of the formula (27). This gives a red-coloured wood with a very good light-fastness. (The ready-stained wood can then be coated with a commercially available nitrocellulose lacquer.) Example 14: The procedure is as given in Example 6, but using, instead of the dye of the formula (1 ), the same amount of the dye of the formula (28). This gives a brown-coloured wood with a very good light-fastness. (The ready-stained wood can then be coated with a commercially available nitrocellulose lacquer.) Example 15: The procedure is as given in Example 6, but using, instead of the dye of the formula (1), the same amount of the dye of the formula (29). This gives a Bordeaux red-coloured wood with a very good light-fastness. (The ready-stained wood can then be coated with a commercially available nitrocellulose lacquer.) Example 16: The procedure is as given in Example 6, but using, instead of the dye of the formula (1 ), the same amount of the dye of the formula (30). This gives an orange-coloured wood with a very good light-fastness. (The ready-stained wood can then be coated with a commercially available nitrocellulose lacquer.) Example 17: The procedure is as given in Example 6, but using, instead of the dye of the formula (1), the same amount of the dye of the formula (31 ). This gives a red-coloured wood with a very good light-fastness. (The ready-stained wood can then be coated with a commercially available nitrocellulose lacquer.) Example 18: The procedure is as given in Example 6, but using, instead of the dye of the formula (1), the same amount of the dye of the formula (34). This gives a black-coloured wood with a very good light-fastness. (The ready-stained wood can then be coated with a commercially available nitrocellulose lacquer.) Example 19: The procedure is as given in Example 6, but using, instead of the dye of the formula (1), the same amount of the dye of the formula (42). This gives a yellow-coloured wood with a very good light-fastness. (The ready-stained wood can then be coated with a commercially available nitrocellulose lacquer.) Example 20: The procedure is as given in Example 6, but using, instead of the dye of the formula (1), the same amount of the dye of the formula (46). This gives a black-coloured wood with a very good light-fastness. (The ready-stained wood can then be coated with a commercially available nitrocellulose lacquer.) Example 21 : The procedure is as given in Example 6, but using, instead of the dye of the formula (1 ), the same amount of the dye of the formula (48). This gives a blue-coloured wood with a very good light-fastness. (The ready-stained wood can then be coated with a commercially available nitrocellulose lacquer.) Example 22: The procedure is as given in Example 6, but using, instead of the dye of the formula (1 ), the same amount of the dye of the formula (49). This gives a red-coloured wood with a very good light-fastness. (The ready-stained wood can then be coated with a commercially available nitrocellulose lacquer.) Example 23: The procedure is as given in Example 6, but using, instead of the dye of the formula (1), the same amount of the dye of the formula (50). This gives a blue-coloured wood with a very good light-fastness. (The ready-stained wood can then be coated with a commercially available nitrocellulose lacquer.) Example 24: The procedure is as given in Example 6, but using, instead of the dye of the formula (1), the same amount of the dye of the formula (51 ). This gives a black-coloured wood with a very good light-fastness. (The ready-stained wood can then be coated with a commercially available nitrocellulose lacquer.) Example 25: The procedure is as given in Example 6, but using, instead of the dye of the formula (1 ), the same amount of the dye of the formula (52). This gives a blue-coloured wood with a very good light-fastness. (The ready-stained wood can then be coated with a commercially available nitrocellulose lacquer.) Example 26: A 0.8 mm wooden board made of ash is sanded on the upper side using fine sandpaper, moistened with a cloth, dried and then sanded again very carefully. All of the wood dust is then brushed off the surface. Using a paintbrush or hand coater, a stain consisting of 91 parts by weight of water, 3 parts by weight of the dye stabilizer of the formula (Hid) dissolved in the water 3 parts by weight of the UV absorber of the formula and 3 parts by weight of a 20% aqueous commercial form of the dye of the formula is applied to the wood surface prepared in this way in an amount of aboutl 00 g/m 2 . The stained wood is then dried in the air. This gives a brilliant blue-coloured wood with a very good light-fastness. (The ready-stained wood can then be coated with a commercially available nitrocellulose lacquer.) Example 27: The procedure is as given in Example 26, but using, instead of the UV absorber of the formula (100), the same amount of the UV absorber of the formula This gives a blue-coloured wood with a very good light-fastness. (The ready-stained wood can then be coated with a commercially available nitrocellulose lacquer.)

Claims: What is claimed is: 1. A process for the staining of wood, which comprises treating the unstained wood with an aqueous preparation comprising a) at least one dye and b) at least one dye stabilizer of the formulae (I) or (II) in which Gi and G , independently of one another, are d-C alkyl or together are pentamethylene, Zi and Z 2 are methyl, or Zi and Z 2 form a bridging member which is unsubstituted or substituted by an ester, ether, hydroxyl, oxo, cyanohydrin, amido, amino, carboxyl or urethane radical, E is oxyl or hydroxyl, and X is an inorganic or organic anion, and the total number of cations h corresponds to the total number of anions j. 2. A process according to claim 1 , wherein the dye stabilizer used is the compound 1 -oxyl- 2,2,6,6-tetramethyl-4-hydroxypiperidine of the formula 3. A process according to either claim 1 or claim 2, wherein the dyes used are acid dyes, cationic dyes, reactive dyes or metal complex dyes. 4. A process according to any one of claims 1 to 3, which comprises firstly staining the wood and then treating it with a dye stabilizer of the formula in which Gi and G 2 , independently of one another, are Cι-C 4 alkyl or together are pentamethylene, Zi and Z 2 are methyl, or Zi and Z 2 form a bridging member which is unsubstituted or substituted by an ester, ether, hydroxyl, oxo, cyanohydrin, amido, amino, carboxyl or urethane radical, E is oxyl or hydroxyl, and X is an inorganic or organic anion, and the total number of cations h corresponds to the total number of anions j. 5. An aqueous wood stain comprising at least one dye and at least one dye stabilizer of the formulae (I) or (II) in which Gt and G , independently of one another, are Cι-C alkyl or together are pentamethylene, Zi and Z 2 are methyl, or Zi and Z 2 form a bridging member which is unsubstituted or substituted by an ester, ether, hydroxyl, oxo, cyanohydrin, amido, amino, carboxyl or urethane radical, E is oxyl or hydroxyl, and X is an inorganic or organic anion, and the total number of cations h corresponds to the total number of anions j. 6. A process according to either claim 1 or claim 2, wherein the wood is treated with a wood stain according to claim 5. 7. The use of a dye stabilizer of the formula (I) or (II) in which Gi and G 2 , independently of one another, are d-C 4 alkyl or together are pentamethylene, Zi and Z 2 are methyl, or Zi and Z 2 form a bridging member which is unsubstituted or substituted by an ester, ether, hydroxyl, oxo, cyanohydrin, amido, amino, carboxyl or urethane radical, E is oxyl or hydroxyl, and X is an inorganic or organic anion, and the total number of cations h corresponds to the total number of anions j, for the photochemical and thermal stabilization of stained wood. 8. The use of a wood stain according to claim 5 for the staining of wood.

Inventors: KOLLER STEFAN, SCHEIBLI PETER, KOLLER, STEFAN, SCHEIBLI, PETER
Applicants: CIBA SC HOLDING AG, CIBA SPECIALTY CHEMICALS HOLDING INC.
Application year: 2001
Main classification: C09D15
IPC codes: B27K5, C09D15