Master alloy for modification and grain refining of hypoeutectic and eutectic Al-Si foundry alloys

Abstract: A master alloy for modification and grain refining of hypoeutectic and eutectic Al-Si based foundry alloys is described. In addition to unavoidable contaminants the alloy contains nucleating and modifying additions of Ti, B and Sr, wherein the content of Ti is between 0,5 and 2,0 % by weight, the content of B is between 0,5 and 2,0 % by weight and the content of Sr is between 3,0 and 12,0 % by weight, with the ratio Ti/B between 0,8 and 1,4. A method for the preparation of said master alloy is also described.

Description: The present application concerns a master alloy for modification and grain refining of hypoeutectic and eutectic Al-Si based foundry alloys. During todays production of aluminium-silicon foundry alloys, additives are used to modify and grain refine the casting structure. Small grains are desirable to among others obtain better castability and smaller pores, as well as better homogeneity and mechanical properties. A modified structure implies a finely divided silicon phase which gives a significant increase in ductility and strength. Grain refining alloys usually contain aluminium, titanium and boron in a certain ratio. An increasingly more common Al-Ti-B master alloy with a ratio 1:1 of Ti:B has been developed for foundry alloys and is described in the applicants' own Norwegian patent application 19990813, not yet published. Modification of the cast structure takes place by introduction of strontium/sodium/antimony to the melt, often by addition of an aluminium-strontium master alloy. The document US-A-4 576 791 discloses a master alloy for the modification of eutectic or hypo-eutectic Al-Si alloys consisting in wt% of : 4-20 % Sr; 0.2-5.0 % Ti; ≤ 1 % B; balance Al. The document EP-A-0 398 449 discloses a master alloy for the modification of eutectic or hypo-eutectic Al-Si alloys consisting in wt% of : 5-25 % Sr; 0.5-5 % Ti; 0.02-2 % B; balance Al. The document EP-A-0 421 549 discloses a master alloy for the modification of eutectic or hypo-eutectic Al-Si alloys consisting in wt% of : 5-35 % Sr; 0.5-5 % Ti; 0.02-2 % B; balance Al. The document Chemical Abstracts, vol. 98, Columbus, Ohio, US; Abstract N°39259, Vakhobov A.V. et al., "Aluminum-base inoculant" (SU-A-939 580) discloses a master alloy for the modification of Al-Si alloys consisting in wt% of: 0.1-10 % Sr; 0.1-5.0 of at least one metal selected from the group consisting of Ti and B; balance Al. The document EP-A-0 396 389 discloses a process for the production of a master Al-alloy containing 2-12 wt% Ti and 0.1-2 wt% B in which the salts K 2 TiF 6 and KBF 4 are mixed before being added to a stirred molten aluminium at a temperature of 700-800°C. The salt residue is then removed and the master Al-alloy does not contain Sr. Common practice is to add modifying and grain refining elements and/or master alloys of these separately. With the present invention a novel alloy has been developed which combines Al-Ti-B and strontium in one and the same product. The invention is characterized by that the content of Ti is between 0,5 and 2,0 % by weight, the content of B is between 0,5 and 2,0 % by weight and the content of Sr is between 3,0 and 12,0 % by weight, and the ratio Ti/B is between 0,8 and 1,4. With the alloy according to the present application a solution has been found to make it possible to simplify the addition practise in the foundries by achievement of modification and grain refining by addition of one and the same alloy. Trials show that modification and grain refining properties are at least equal to those achieved by separate addition of TiB alloy and Sr. The invention will be described in detail in the following by way of example and with reference to the attached drawings where: Fig. 1 shows an example of a microstructure for an alloy according to the invention. Fig. 2 shows the microstructure for an Al-Si alloy where modification and grain refining has been carried out by means of a master alloy according to the invention. Fig. 3 shows the same Al-Si alloy where modification and grain refining has been made by means of a traditional TiB master alloy and with a subsequent addition of Sr. Fig. 4 shows the same Si-Al alloy without addition of modification or grain refining alloy. The main elements in the alloy according to the present invention are Al, Sr, Ti and B, with a composition within the following limits: Sr 3,0 - 12,0 % by weight Ti 0,5 - 2,0 % by weight B 0,5 - 2,0 % by weight Al rest, included possible smaller amounts of impurities In Figure 1 an example of the microstructure in an alloy according to the invention is shown. The existing phases mainly consist of Al-Sr (Al 4 Sr, eutectic), Al-Ti-B ((Al-Ti)B 2 ) and a smaller part of Sr-B (SrB 6 ). Al 4 Sr is present as big grey particles in the picture (size range < 150 µm). (Al,Ti)B 2 can be seen as clouds of small light grey particles (< 1 pm), whereas the Sr-B phases are small and dark grey/black (5-10 µm). Al 4 Sr and eutectic will be dissolved after introduction into the melt and give a modifying effect, whereas (Al,Ti)B 2 particles act as nucleants for α-Al during the seed formation. Figures 2-4 show the casting structure with an alloy according to the invention, an alloy to which has been added conventional type TiB/AlSr, as well as without any addition, respectively. The light areas are α-aluminium, which have been grain refined by (Al,Ti)B 2 . Figures 2 and 3 show corresponding grain size. Figure 4 has no addition of grain refiner, and has a coarser grain structure. The dark phase is the eutectic phase (Al-Si), which has been modified in an at least equal degree in Figure 2 as in Figure 3. Figure 4 shows an unmodified eutectic phase (no strontium added). The master alloy according to the invention is produced by reacting liquid aluminium with a pre-mix of the salts KBF 4 and K 2 TiF 6 , usually with Ti/B = 0,8 - 1,2, or other sources of Ti and B in an equal proportion of mixture. The salts are added to liquid aluminium during stirring at a temperature of 660°C < T > 760°C in a reaction furnace. The salts are added in powder form at a certain rate V > 10 kg/min. during a time adapted to the total amount of salt. During this feeding the metal is moved by e.g. electromagnetic stirring. The salt residue (KAIF) is removed after equilibrium has been reached and melt treatment carried out, the salt is removed by pouring/decanting. Strontium is then added to the alloy at a suitable temperature T = 780 - 900°C, before the alloy is cast out as a rod, bar, waffle, billet or other forms. Example Liquid aluminium, 700°C, was added to a pre-mixture of the salts KBF 4 (168 kg) and K 2 TiF 6 (99 kg) in two reaction furnaces. After the end of the exothermic reaction, the salt residue was removed and the metal transferred to a holding furnace. The total amount of melt was 1920 kg. Into the holding furnace it was added 195 kg metallic strontium at a starting temperature of 800°C, and thereafter casting was carried out as a Properzi bar. The cast alloy had the following composition Ti 1,5 % by weight B 1,1 % by weight Sr 5,3 % by weight The master alloy according to the invention can be used as means for modification and grain refining of all hypoeutectic and eutectic Al-Si based foundry alloys. It can be added to the melt of an Al-Si alloy in a recommended amount which is adapted to the alloy of the customer and requirements for modification/grain refining. To achieve the same addition of strontium as that used at the present time, as well as a certain amount of grain refiner also adapted to the process of the customer, the strontium level in the combination alloy has to be adapted to each customer in the interval 3,0 - 12 % by weight of Sr. Trials with a lower level of Sr compared to the established level and practice has been carried out with the alloy according to the invention and show good results with regard to the modification effect. In many cases the customer has a potential to reduce his use of strontium. The level of titanium in the melt should be min. 0,08 % before addition of the alloy according to the invention. Trial 1 By this trial it was an object to achieve the same modification and grain refinement by use of the master alloy according to the invention as by use of separate addition of grain refining Ti/B alloy and modifying agent. Alloy: A356 A master alloy according to the invention with the following chemical composition was used: Sr 5,3 % by weight Ti 1,5% by weight B 1,1% by weight The level of titanium in the Al-Si alloy to be added to the master alloy was 0,08 % by weight, and the amount of master alloy added was 2,5 g/kg. This corresponds to approximately 130 ppm Sr. For traditional addition 2,5 kg/MT Ti1,6/B1,4 alloy and 200 ppm Sr are added, respectively. Results: Sampling Grain refiner index Modification index Addition of master alloy according to the invention Addition of traditional TiB alloy / AlSr Addition of master alloy traditional according to the invention Addition of TiB alloy / AlSr Ref. Sample 8,6 8,0 0 0 After addition of Ti 12,0 11,5 0,1 0,1 5 min. after grain refiner 13,5 13,4 4,8 4,6 15 min. after grain refiner 12,8 13,1 5,5 5,2 30 min. after grain refiner 13,0 12,2 5,3 4,9 60 min. after grain refiner 12,8 12,1 6,0 4,7 90 min. after grain refiner 12,2 11,9 5,9 4,8 Comments: The grain refiner index is similar for the alloy according to the invention and separate addition of Ti1,6B1,4 alloy/Sr, but GRI for the alloy according to the invention shows better stability during the holding time. The table also shows that a somewhat higher modification index is achieved with a lower level of strontium (130 ppm for the alloy according to the invention, 200 ppm for separate addition). Trial 2 Trials were made with the alloy A356. The composition of the master alloy according to the invention was: Sr 6,49 % by weight Ti 1,49 % by weight B 1,20 % by weight Three different addition levels of the inventive alloy were tested: 0,8 - 1,5-2,3 kg/MT. This corresponds to 50 - 100 - 150 ppm added strontium. As comparison, results from trials with separate addition of TiB alloy (2,5 kg/MT AlSr (200 ppm) are shown. 0,10 % by weight of titanium was added to the Al-Si alloy 15 minutes before addition of the master alloy according to the invention, respective addition of the traditional TiB alloy. Results: Modification properties: Sampling Modification index Master alloy according to the invention Separate addition of TiB/AlSr 0,8 [kg/MT] 1,5 [kg/MT] 2,3 [kg/MT] 2,5 [kg/MT) Ref. Sample 0,2 0 0,1 0,1 After addition of Ti 0,4 0,1 0,2 4,6 5 min. after grain refiner 4,2 4, 5 3,5 5,2 30 min. after grain refiner 5,3 7,8 4,9 4,9 60 min. after grain refiner 5,7 5,6 6,2 4,7 90 min. after grain refiner 6,0 6,4 5,6 4,8 120 min. after grain refiner 5,8 6,5 5,9 5,5 Grain refiner properties: Sampling Grain size [mm] Master alloy according to the invention Separate addition og TiB / AlSr 0,8 [kg/MT] 1,5 [kg/MT] 2,3 [kg/MT] 2,5 [kg/MT] Ref sample (after Ti addition) 814 826 837 682 5 min. after grain refiner 550 401 380 400 30 min. after grain refiner 425 455 375 393 60 min. after grain refiner 545 453 357 388 90 min. after grain refiner 412 423 343 404 120 min after grain refiner 607 454 422 421 Comments: The trials with the alloy according to the invention show at least as good modification properties as separate addition of TiB alloy / Alsr. The grain refining efficiency is highest at 2,3 kg/MT addition of the alloy according to the invention.

Claims: Master alloy for modification and grain refining of hypoeutectic and eutectic Al-Si based foundry alloys, containing, in addition to unavoidable contaminants, nucleating and modifying additions of Ti, B and Sr, characterized in that the content of Ti is between 0,5 and 2,0 % by weight, the content of B is between 0,5 and 2,0 % by weight and the content of Sr is between 3,0 and 12,0 % by weight, with the ratio Ti/B between 0,8 and 1,4. Method for making a master alloy containing Ti, B and Sr, for modification and grain refining of an Al-Si alloy, characterized in that the alloy is made by pre-mixing the salts KBF 4 and K 2 TiF 6 , to give a ratio Ti/B between 0,8 and 1,2, addition to liquid aluminium during stirring at a temperature between 660°C and 760°C in a reaction furnace, whereby the salt residue (KAIF) is removed after equilibrium has been reached, and that Sr then is added to the alloy at a temperature between 780 and 900°C, before casting of the alloy.

Inventors: BONDHUS EIVIND, SAGSTAD TROND, BONDHUS, EIVIND, SAGSTAD, TROND
Applicants: HYDELKO AS
Application year: 2001
Main classification: C22C21
IPC codes: C22C21, C22C1