Low temperature curing, sag-resistant epoxy primer

Abstract: An epoxy composition is especially designed for use as a primer for sealing and filling small pores in concrete. Advantageously, the composition is a low temperature curing, sag-resistant epoxy primer, which provides good adhesion to concrete and to a polyurea coating applied to the primed concrete. The epoxy primer may be curable at a temperature below 4°C, and comprises an admixture of Component A (comprising a crystallization-resistant reactive epoxy resin) and Component B (an amine curing agent).

Description: FIELD OF THE INVENTION This invention relates to an epoxy composition especially designed for use as a primer for sealing and filling small pores in concrete. Advantageously, the composition has the ability to cure at a low temperature, thereby extending the outdoor use of this sag-resistant epoxy primer through the winter months. BACKGROUND OF THE INVENTION Epoxy resins have long been used for the priming and repair of concrete surfaces. However, the application of these materials are typically conducted at temperatures above freezing, i.e., above 0°C, and not below that temperature due to curing problems often encountered at temperatures below 0°C. Previous attempts at preparing low temperature curing epoxy compositions have generally not progressed below about 4.5°C, as the low temperature cure cut-off point. For example, Rust-Oleum Corporation has advertised a low temperature activator (9103) for use with its System 9100 high performance epoxy resin. According to the company's Internet literature, when the 9103 activator is used in the 9100 system, the coating can be applied and cured at temperatures as low as 4.5°C, which is lower than the curing temperature lower limit for their standard activator. The 9100 epoxy coating is claimed to be suitable for use on abrasive-blasted steel, concrete and masonry surfaces. American Paint & Coatings Journal, Vol. 80, No. 211996, p.49, discloses the properties of three phenalkamine epoxy hardeners for epoxy coatings which can be used for marine and offshore coatings, industrial maintenance, pipe and tank linings, drinking water applications and concrete protection. One formulation (NC-541LV) is said to promote rapid cure at temperatures as low as 5°C. US-A-4221890 discloses a concrete repair material which comprises a 100% solids epoxy-amine composition comprising an epoxy resin, an aliphatic polyamine, a first accelerator comprising Bisphenol-A, a second polyamine composition and a second accelerator. The concrete repair material is claimed to have a cure temperature within the range of -18°C to 60°C. US-A-4 051 195 discloses a polyepoxide-polyacrylate ester two component composition comprising a Component A comprising an epoxy resin based on glycidyl ether compounds and polyacrylates and polymethacrylates with terminal acrylate or methacrylate groups, fillers, reinforcing agents and solvents and Component B comprising curing agents based on amine compounds and mixtures of several amine compounds. EP-0779311-A discloses the use of Mannich base curing agents which can be used as sole curing agents or as co-curing agents for epoxy resin systems. There remains a need for materials which will permit further coatings and afford a strong bond to concrete, and cure at temperatures below 0°C. SUMMARY OF THE INVENTION The present invention is directed to an epoxy primer that helps bond a fast-cure polyurea sprayable coating to a concrete surface. The key requirements of the epoxy primer of the present invention are: 1) curable below 13°C (55°F), more preferably below 4.4°C (40°F), and most preferably below 0°C (32°F); 2) high sag resistance, so as to fill "bug" holes in vertical concrete surfaces. Holes can be as much as 2.54cm (1 inch) in width and depth, and sometimes even larger; 3) good adhesion to concrete; and 4) good adhesion to additional coating compositions, particularly polyurea coatings, sprayed on top of cured primer. The present invention provides a composition which satisfies these criteria. The composition is a two part system, Component A comprising the reactive epoxy resin mixture and Component B comprising the hardener or curing agent mixture. The two parts are mixed before application, and then the mixed primer is applied to the concrete surfaces to be primed and filled. The primer mixture can be mixed and applied manually (e.g., by trowel or sponge float) or by use of automatic metering, mixing and dispensing equipment. In supplying the primer composition as a two-part system, each part is supplied in a separate container. DESCRIPTION OF THE INVENTION Component A comprises the following ingredients: (a) from 75 to 115 parts by weight of a compound containing at least one glycidyl ether epoxide group; (b) from 1 to 10 parts by weight of a Michael addition agent, e.g., a polyfunctional acrylate monomer; (c) from 0 to 1 part by weight of color concentrate (e.g., grey); (d) from 0 to 10 parts by weight of filler and/or thickener materials; and (e) from 1 to 10 parts by weight of a diluent to maintain a low viscosity at low application temperatures. Depending on the epoxy used, the diluent used, and the amount and types of thickeners and/or fillers used, viscosity of Component A may be in the range from 1 kg/ms (1000 cps) to 300 kg/ms (300,000 cps), with a preferred range being 10 kg/ms (10,000 cps) to 100 kg/ms (100,000 cps), and a most preferred range being 25 kg/ms (25,000 cps) to 75 kg/ms (75,000 cps). One currently preferred embodiment has a viscosity of about 53 kg/ms (53,000 cps). The epoxy resin used herein must resist crystallization and thickening at low temperatures, thereby allowing easy application of the primer. The reactive epoxy mixture of the present invention advantageously comprises a bisphenol-epichlorohydrin epoxy resin having an epoxy equivalent weight ranging from 150 to 250. The epoxy equivalent weight is defined as the weight in grams of the resin containing one gram equivalent of epoxide. Suitable epoxy resins of this type are commercially available from the Shell Chemical Company, Resins & Versatics Sales Office, Houston, TX under the trademark Epon®. The currently most preferred epoxy resins are Epon 862 and Epon 828. In addition to the epoxy resin, Component A of the present invention further comprises at least one Michael addition agent. This agent is added to enhance the low temperature reaction with the curing agent. Suitable materials of this type include polyfunctional acrylate monomers which participate in a very rapid Michael's Addition reaction with the primary amine functional groups present in the curing agent. The addition of such a reactive agent assists the curing process at low temperatures, maintaining satisfactory cure rates even at temperatures of -4°C (25°F) or less. One commercially available polyfunctional acrylate monomer of this type is Photomer 4399 from the Henkel Corporation. As described above, Component A further comprises coloring agents, filler and/or thickener materials, and diluents. Examples of suitable filler and/or thickener materials include fumed silicas, and similar inorganic solids. Diluents include alcohols and the like. Currently preferred materials include Cab-O-Sil TS-720 and benzyl alcohol. Color concentrates for a variety of colors (e.g., grey) are widely available. Component B comprises the following ingredients: (aa) from 65 to 105 parts by weight of an amine-based hardener, for example, a Mannich base curing agent; (bb) from 12 to 18 parts by weight of an amine-based accelerator; (cc) from 0 to 1 part by weight of a color concentrate (e.g., grey); (dd) from 0 to 6 parts by weight of one or more thickener materials; and (ee) from 4 to 6 parts by weight of a diluent to maintain a low viscosity at low application temperatures. Depending on the materials used, the viscosity of Component B may be in the range from 0.1 kg/ms (100 cps) to 100 kg/ms (100,000 cps), with a preferred range being 1 kg/ms (1000 cps) to 50 kg/ms (50,000 cps), and a most preferred range being 10 kg/ms (10,000 cps) to 50 kg/ms (50,000 cps). One currently preferred embodiment has a viscosity of about 14.4 kg/ms (14,400 cps). The hardener or curing agent mixture (Component B) advantageously comprises components that react suitably with the reactive ingredients in the Component A mixture, to afford a suitable primer composition that will cure at temperatures below about 0°C. One preferred class of curing agents makes use of Mannich base chemistry, so that the agent reacts rapidly with the Epon epoxy resins, and even more rapidly with the Photomer 4399, present in the resin mixture. Mannich bases, as preferred amine-based components of curing agent composition, are of value in reducing the cure time and they improve strength of the primer bonding. The amines for making Mannich bases may be primary or secondary; they may be diamines or other polyamines. The Ancamine family of curing agents, commercially available from Air Products and Chemicals, Inc., Allentown, PA, USA, are within this class. In the present invention, the preferred amine is triethylenetetramine (TETA). An especially preferred Mannich base curing agent based upon TETA is Ancamine 1637. Ancamine K54 (Air Products and Chemicals) and Capcure EH-30 (Henkel Corporation) are examples of a preferred amine-based accelerator for use herein. These products are the same material, namely 2,4,6-tri(dimethylaminomethyl)phenol, a tertiary amine which catalyzes the epoxy curing reaction to high rates. Diluents may be reactive or non-reactive. Alcohols have been found to be suitable for use as the non-reactive diluent in both Component A and Component B. Benzyl alcohol is an example of a preferred non-reactive diluent which keeps the viscosity low in cold environment. Reactive diluents have one or more functional groups that react with one or more of the other components in the mixture. Examples of suitable reactive diluents include epoxy-functional glycidyl ethers, for example, butyl glycidyl ether, 2-ethylhexyl glycidyl ether and cresyl-glycidyl ether. Fillers which may be used in either of the two parts include talc, kaolin, silica, aluminum and other metal powders, metal oxides and calcium carbonate. Thickening agents (i.e., thixotropic agents) include silicas and similar materials. Preferred thickening agents are the fumed silicas, such as those sold under the trade names Cabosil (Cabot Corp.) and Aerosil (Degussa). Cab-O-Sil TS 720 has been found to be an especially preferred embodiment of the fumed silicas useful herein. Combinations of one or more thickeners and/or fillers may also be employed herein. An especially preferred formulation meeting all of the above requirements can be prepared by mixing the following two-component (resin and hardener) compositions: Component A (resin): Trade Name Parts By Weight Weight Fraction Epon Resin 862 95 0.8370 Photomer 4399 5 0.0441 Color Concentrate 0.5 0.0044 Cab-O-Sil TS-720 8 0.0705 Benzyl Alcohol 5 0.0441 TOTAL 113.50 1.0000 Component B (hardener): Trade Name: Parts By Weight Weight Fraction Ancamine 1637 85 0.7692 Color Concentrate 0.5 0.0045 Cab-O-Sil TS 720 5 0.0452 Capcure EH-30 (Ancamine K54) 15 0.1357 Benzyl Alcohol 5 0.0452 TOTAL 110.50 1.0000 An especially preferred primer composition was prepared using 74.8 parts by weight of Component A and 25.2 parts by weight of Component B. This primer composition (100 grams) had a gel time at 24°C (75°F) of six (6) minutes. The thin film set time (TFST) for this primer composition, at a temperature range of 4° to 0°C (250 to 32°F), was from eight (8) to sixteen (16) hours. The TFST at a temperature range of 4.4° to 10°C (40° to 50°F) was from two (2) to six (6) hours. The measured adhesion strength of this primer composition to polyurea was greater than 1.38 MPa (200 psi), preferably at least 2.07 MPa (300 psi), and most preferably at least 2.76 MPa (400 psi), as measured on an Elcometer using test method ASTM D 4541. As described above, the present invention is directed to an epoxy primer that helps bond a fast-cure polyurea sprayable coating to a concrete surface, at temperatures below 13°C (55°F), preferably below 44°C (40°F), and most preferably at 0°C (32°F) or less. In addition to low temperature curing, the other essential requirements of the epoxy primer of the present invention are (a) high sag resistance, so as to fill holes in vertical concrete surfaces without sagging. Typical "bug" holes in cured concrete can be as large as 2.54 cm (1 inch) in width and/or depth, and sometimes even larger. The primer must fill these holes and not fall out during the curing process. In connection with the filling requirement, good adhesion of the primer to concrete is an essential part of this invention. Finally, the primer must promote good adhesion of additional coating compositions, particularly polyurea coatings, sprayed on top of cured primer. Adhesion is measured using a standard test method, ASTM D 4541, and the primer shows adhesion values (Elcometer) of greater than 1.38 MPa (200 psi). Especially preferred embodiments of the present invention had an adhesion value of greater than 3.45 MPa (500 psi) and most preferably greater than 4.14 MPa (600 psi). Epoxide group-containing materials useful in the compositions of the invention are glycidyl ether derivatives having an oxirane ring polymerizable by ring opening. Such materials, broadly called glycidyl ether epoxides, include monomeric epoxy compounds and epoxides of the polymeric type. Preferably, the epoxides have more than one epoxide group per molecule. These epoxide group-containing materials can vary from low molecular weight monomeric materials to high molecular weight polymers and can vary in the nature of their backbone and substituent groups. Illustrative substituent groups include halogens, ethers, and siloxane groups. The molecular weight of the epoxy containing compound can vary from 150 to 100,000 or more. Mixtures of various epoxy-containing materials can also be used in the composition of this invention. Especially preferred are liquid epoxies that resist crystallization at low temperatures, i.e., below 13°C (55°F). Such epoxide group-containing materials are well known and include such epoxides as glycidyl ether-type epoxy resins and the diglycidyl ethers of bisphenol A or bisphenol F and their higher molecular weight analogs. The Epon® resins (Shell Chemical Company), particularly Epon 828 and 862, are preferred herein. Epon 862 is an especially preferred example of an epoxy resin that resists crystallization and thickening at low temperatures, thereby allowing easy application of the primer. This liquid resin material has a room temperature (25°C) viscosity of 30-45 P and the weight per epoxide is 166-177. Chemically, Epon Resin 862 is a liquid epoxy resin manufactured from epichlorohydrin and Bisphenol-F. The commercially available material contains no diluents or modifiers. Photomer 4399, commercially available from the Henkel Corporation, is a medium viscosity dipentaerythritol monohydroxy pentaacrylate. This compound is commonly used as a diluent for UV and EB-curable lacquers and UV curing agent pigmented coatings used in paper and board coatings, wood finishes and vinyl flooring. Photomer 4399 is also compatible with a variety of polyester, epoxy and urethane acrylate oligomers. Photomer 4399 is a preferred example of a polyfunctional acrylate monomer which participates in a very rapid, Michael addition reaction with the primary amine functional groups present in the curing agent, for example, Ancamine 1637. This chemical reaction proceeds even at a low temperature of -4°C (25°F), at a satisfactory speed. Ancamine 1637 (Air Products and Chemicals, Inc.) is an example of an amine-based fast curing agent which reacts rapidly with Epon 862, and even more rapidly with the Photomer 4399, present in the resin side. Ancamine 1637 is commonly used in conjunction with standard liquid epoxies and/or epoxy novolacs for a variety of applications. Ancamine 1637 curing agent can also be used as an accelerator for other curing agents. Ancamine K54 (Air Products & Chemicals) and Capcure EH-30 (Henkel Corporation) are examples of preferred amine-based accelerators which catalyze the epoxy curing reaction to high rates. Each of these products is a tertiary amine accelerator and a curing agent for epoxy resin systems. Fast cures are commonly obtained with this epoxy resin hardener and accelerator, particularly at room temperature. CAB-O-SIL TS-720, commercially available from Cabot Corporation, is a high-purity fumed silica which has been treated with a dimethyl silicone fluid. The treatment replaces many of the surface hydroxyl groups on the fumed silica with a polydimethyl siloxane polymer. This treatment makes the silica extremely hydrophobic. The present invention will be further illustrated with reference to the following examples which aid in the understanding of the present invention, but which are not to be construed as limitations thereof. All percentages reported herein, unless otherwise specified, are percent by weight. Typical Properties of the Preferred Primer: The preferred primer composition comprises 74.8 parts by weight of Component A and 25.2 parts by weight of Component B. Component A (resin): Trade Name Parts By Weight Weight Fraction Amount (gm) EPON Resin 862 95 0.8370 627.75 PHOTOMER 4399 5 0.0441 33.04 Color Concentrate 0.5 0.0044 3.30 CAB-O-SIL TS-720 8 0.0705 52.86 Benzyl Alcohol 5 0.0441 33.04 TOTAL 113.50 1.0000 750.00 Component A, when mixed at room temperature at a mixing speed of 5 rpm, had a viscosity of 285 kg/ms (285,000 cps ). When mixed at 50 rpm, the room temperature viscosity was 53 kg/ms (53,000 cps). Component B (hardener): Trade Name Parts By Weight Weight Fraction Amount (gm) Ancamine 1637 85 0.7692 218.54 Color Concentrate 0.5 0.0045 1.29 Cab-O-Sil TS 720 5 0.0452 12.86 Ancamine K54 15 0.1357 38.57 Benzyl Alcohol 5 0.0452 12.86 TOTAL 110.50 1.0000 284.10 Component B, when mixed at room temperature at a mixing speed of 5 rpm, had a viscosity of 33.6 kg/ms (33,600 cps). When mixed at 50 rpm, the room temperature viscosity was 14.4 kg/ms (14,400 cps). When Component A (74.8 pbw) and Component B (25.2 pbw) were mixed together at 24°C (75°F), 100 grams had a gel time of six (6) minutes. The thin film set time (TFST) was from 8 to 16 hours at -4°C to 0°C (25°F to 32°F) and 2 to 6 hours at 4°C to 10°C (40°F to 50°F). The adhesion test of the primer, i.e., both to the concrete substrate and a polyurea spray overcoat, using test method ASTM D 4541, was greater than 1.38 MPa (200 psi). Once mixed together as a primer composition, the "pot life" of the composition becomes very important. The "pot life" is a temperature-dependent physical property of the primer, namely the time during which the primer composition may be applied to a concrete surface in a satisfactory manner (working time), yielding satisfactory performance characteristics. The data shown below are reflective of the temperature influence on pot life: Working Time Temp Mixed Volume/Weight 6 minutes 25°C 100 grams 30 minutes 4°C 1 quart (0.95 L) 30-40 minutes 0°C 2-3 gallons (7.6-11.4 L) Finally, the primer "recoat window" was measured. The "recoat window" is defined as the range of elapsed time (in hours) from the primer application during which a coating of polyurea can be sprayed onto the cured primer, while retaining optimum adhesion results. As set forth above, this means an adhesion value as measured by ASTM D 4541 of at least 1.38 MPa (200 psi), preferably at least 300 psi (2.07 MPa), more preferably at least 2.76 MPa (400 psi), and most preferably at least 3.45 MPa (500 psi). Preliminary data regarding the recoat window, showing both the minimum time period and the maximum time period (in hours) at various temperatures, are provided below: Recoat Window (hr) Cure Temp Minimum Maximum 0°C 12 72 4°C 8 36 13°C 2 24

Claims: An epoxy primer for concrete, which binds to concrete at at least 1.38 MPa (ASTM D 4511) and is curable at a temperature below 13°C, which comprises an admixture of two parts, Component A and Component B, wherein Component A comprises: (a) from 75 to 115 parts by weight of a compound containing at least one glycidyl ether epoxide group; (b) from 1 to 10 parts by weight of a Michael addition agent; (c) from 0 to 1 part by weight of a colour concentrate; (d) from 0 to 10 parts by weight of filler and/or thickener materials; and (e) from 1 to 10 parts by weight of a diluent; and Component B comprises: (aa) from 65 to 105 parts by weight of a Mannich base curing agent; (bb) from 12 to 18 parts by weight of an amine-based hardener and accelerator; (cc) from 0 to 1 part by weight colour concentrate; (dd) from 4 to 6 parts by weight of one or more filler and/or thickener materials; and (ee) from 4 to 6 parts by weight of a diluent. An epoxy primer according to claim 1, wherein the reactive epoxy mixture of Component A comprises a bisphenol-epichlorohydrin epoxy resin having an epoxy equivalent weight of from 150 to 250. An epoxy primer according to claim 2, wherein the bisphenol is bisphenol A or bisphenol F. An epoxy primer according to any preceding claim, wherein the Michael addition agent comprises one or more polyfunctional acrylate monomers. An epoxy primer according to any preceding claim, wherein the thickener material comprises fumed silica. An epoxy primer according to any preceding claim, wherein the diluent comprises an alcohol or an epoxy-functional glycidyl ether. A kit for forming a primer according to any preceding claim, which comprises, in separate containers, Component A and Component B.

Inventors: MISHRA VINAY, MORGAN NOREDIN, MISHRA, VINAY, MORGAN, NOREDIN
Applicants: ILLINOIS TOOL WORKS, ILLINOIS TOOL WORKS INC.
Application year: 2001
Main classification: C09D163
IPC codes: C04B41, C08G59, C09D163