PROCESS FOR THE PREPARATION OF 1-HEXENE

Abstract: Process for the preparation of 1-hexene consisting in effecting the oligomerization of ethylene in the presence of a catalyst comprising a vanadium complex having the formula: (arene)2VX wherein the term arene represents benzene or mono-, di-, or tri-alkylsubstituted benzene, V is a vanadium ion with a low oxidation state, and X is an anion selected from Cl, Br and I halide ions, or from non-coordinated anions such as B(Ar)4<->, AlCl4<->, carboxylates and sulfonates.

Description: PROCESS FOR THE PREP7ARATION OF 1-HEXENE The present invention relates to a process for the preparation of 1-hexene by the oligomeri- zation of ethylene in the presence of vanadium complexes with a low oxidation state. The possibility of preparing olefins with a double terminal bond by means of the oligomerization of lower olefins, for example 1-hexene by the trimerization of ethylene, is already known: for example United States patent 4,668,838 describes a process involving the use of a catalyst which comprises the reaction product between a chromium compound, a hydrocarbon derivative of partially hydrolyzed aluminum and a ligand-donor compound; European patent application 416,304 involves, in the process in question, the use of a catalytic system comprising a pyrrolidic compound of chromium and a compound of aluminum; European patent application 537,609 relates to the process of interest which is carried out in the presence of a catalyst consisting of a complex of chromium with a polydentate ligand and an aluminoxane. In addition to the above references, others can be cited relating to the use of catalytic systems based on compounds of chromium; preparation processes of 1-hexene by the oligomerization of ethylene in the presence of these catalytic systems, however, seem to have various drawbacks such as, for example, insufficient activity of the catalyst or difficulty in its preparation or the low selectivity with respect to the desired product . The Applicant has now found that it is pos- sible to effect the synthesis of 1-hexene by the oligomerization of ethylene using a process which overcomes all the disadvantages which negatively characterize analogous processes described in the state of the art above, and which consequently seem to have all the necessary industrial requisites. The object of the invention, according to the present patent application, therefore relates to a process for the preparation of 1-hexene which consists in subjecting ethylene to oli- gomerization in the presence of a catalyst comprising a vanadium complex with a low oxidation state selected from those included in the following formula: (arene) 2 VX wherein the term arene represents benzene or mono-, di-, or tri-alkylsubstituted benzene, V is a vanadium ion with a low oxidation state, and X is an anion such as Cl, Br, I, non-coordinated anions such as B(Ar) 4 ~ , A1C14-, carboxylates, sul- fonates. The following complexes have proved to be particularly advantageous: bis- (mesitylene) -vanadium trifluoroacetate bis- (mesitylene) -vanadium-tetraphenylborate bis- (mesitylene) -vanadium-iodide bis- (mesitylene) -vanadium-tetrachloroaluminate. Vanadium arenes are already known in the art and can be prepared for example according to the indications, which form an integral part of the present invention, contained in the articles of E.O. Fischer and U.S. Kogler, Chem. Ber. 90, 250 (1957), and F. Calderazzo, Inorg. Chem., _3, 810 (1964) : for example according to the schemes of Table 1. In accordance with a wider aspect of the process of the present invention, these vanadium complexes can be used for the oligomerization of olefins other than ethylene, such as, for exam- pie, propylene, 1-butene, etc.: the reason the Applicant has decided to limit the description of the invention to the preparation of 1-hexene alone is simply because of the specific industrial interest in the production of this com- pound: any expert in the field will be able to understand from this description how to effect the oligomerization reaction starting from olefins other than ethylene, this process being included, however, in the scope of the invention according to the present patent application. The oligomerization reaction of ethylene, according to the process of the present invention is carried out in the absence of co-catalysts, in the presence of the above vanadium compound alone or in the presence of the vanadium compound and a heterocyclic compound selected from pyrrole and derivatives . When this heterocyclic compound is adopted, it is used in a ratio, with respect to the vana- dium complex, ranging from 1 to 20: heterocyclic compounds which can be advantageously used are pyrroles, pyrazoles, phenanthroline, pyridine and other mono and polynitrogenated derivatives . The oligomerization reaction of ethylene, according to the present invention, is carried out in the presence of a solvent which is normally selected from aromatic hydrocarbons and cy- cloaliphatic hydrocarbons: of these, the use of toluene and cyclohexane has proved to be particu- larly advantageous. The reaction is carried out at a temperature ranging from 0 to 150°C, preferably from 25 to 60°C, and at a pressure ranging from 1 to 100 atm. , preferably from 1 to 50 atmospheres. The reaction time is normally less than 36 hours, preferably from 1 to 24 hours. At the end of the reaction, 1-hexene can be separated and recovered from the reaction mixture using techniques well known to experts in the field. Further details are evident from the following operative examples which are provided for a better illustration of the present invention without limiting its scope however in any way. Table I VANADIUM COMPLEXES OCOCF 3 BAr 4 X + Cp 2 Fe Example 1: Synthesis of V(mes) 2 (OCOCF 3 ) 1.723 g of N(mes) 2 (5.9[mmoles) and 50 ml of anhydrous and degassed n-hexane are charged under argon into a 250 ml test-tube. 0.44 ml of anhy- drified trif luoroacetic acid CF 3 C00H (5.9 mmoles) are added to the brown solution. A brown precipitate is formed which, after 4 hours, is filtered and washed with hexane 6 times . The brown, pump- dried solid weighs 1.2 g (yield 52%). Example 2: Synthesis of ferrocene tetra- phenyl bor te Cp 2 Fe(BPh) 1.13 g of ferrocene Cp 2 Fe (MW = 186; 6.10 mmoles) are charged into a 100 ml flask and 10 ml of H2SO4 at 96% are slowly added dropwise. There is a substantial development of heat. 2.6 g of Νa(BPh 4 ) (MW = 342; 7.63 mmoles) dissolved in 25 ml of water are slowly added dropwise to the blue solution, Cp 2 Fe(HS0 4 ) . A blue precipitate is formed, which is filtered and washed with ethanol (5 x 10 ml), followed by ethyl ether (5 x 10 ml) and finally dried for a whole night with a vacuum pump and subsequently on P2O5. Example 3: Synthesis of Vanadium bis- (mesitylene) tetra phenyl borate V(mes) 2 (BPh ) 0.350 g of Cp 2 Fe(BPh 4 ) (MW = 505; 0.7 mmoles) and 0.201 g of N (mes ) 2 (MW = 291; 0.7 mmoles) are charged under argon into a 100 ml test-tube containing 30 ml of anhydrous toluene. The mixture is left under stirring for about 4 hours; the dark solid product is filtered and dried. 0.410 g of product are obtained (yield: 96%) . Example 4 36 mg of V(mes) 2 (OCOCF 3 ) (MW = 404; 0.089 mmoles) are charged under argon into a 100 ml three-necked flask. 20 ml of anhydrous and degassed toluene are added. The resulting brown solution under ethylene becomes lighter. It is left at 45°C for 24 hours. The absorption buret regis- ters an ethylene consumption equal to 500 ml. 1 ml of the solution is removed, 1 ml of a solution of Br 2 in CC1 4 is added and GC analysis is effected. 0.51/22.4 (1/mol) == 0.0223 moles of ethylene used up Activity: 250.5 moles of ethylene/V moles Selectivity: 56% to 1-hexene Example 5 81 mg of V(mes) 2 (OCOCF 3 ) (MW = 404; 2-10 "4 mmoles) are charged under argon into a 250 ml three-necked flask. 30 ml of anhydrous and degassed toluene are added. The brown solution under ethylene becomes lighter. After 10 minutes an absorption equal to 67 ml of ethylene is ob- tained. After 1 hour, as there no longer seems to be any more absorption, 0.080 ml of 2, 5-dimethyl- pyrrole (0.787 mmoles) are added, which causes a further ethylene absorption equal to 33 ml. The green solution, after a night at room tempera- ture, becomes brown again and is analyzed via GC. 0.11/22.4 (1/mol) = 0.00446 moles of ethylene used up Activity: 22.26 moles of ethylene/vanadium mole Selectivity: 55% to 1-hexene Example 6 56 mg of N ( es) 2 (OCOCF 3 ) (MW = 404; 0.138 mmoles) are charged under argon into a 100 ml three-necked flask. 0.042 ml of 2,5- dimethylpyrrole (0.408 mmoles) are added to 20 ml of distilled and degassed cyclohexane. The orange solution under ethylene darkens. It is left at 50°C for 5 hours; after 3 hours the solution is green and has absorbed 70 ml of ethylene. GC analysis is effected. 0.071/22.4 (1/mol) = 0.003125 moles of ethylene used up Activity: 22 . 54 moles of ethylene /vanadium mole Selectivity: 46% to 1-hexene Example 7 64 mg of N (mes) 2 B (Ph) 4 (MW = 610; 1.04-10 ~4 moles) are charged under argon into a 100 ml three-necked flask. The mixture is dispersed in 30 ml of anhydrous toluene. The reddish-brown suspension under ethylene darkens. It is left at room temperature for 20 hours. After this period of time a black suspension is formed. In 10 minutes, 70 ml of ethylene are absorbed. It is injected into GC. 0.071/22.4 (1/mol) = 0.00315 moles of ethylene used up Activity: 29.8 moles of ethylene/vanadium mole Selectivity: 66% to 1-hexene Example 8 0.2 ml of V(mes) 2 at 6% in hexane (MW = 291; 4.12-10 "5 moles) in 20 ml of degassed and anhydrous toluene are charged under argon into a 100 ml test-tube. 21 mg of Cp 2 Fe(BPh 4 ) (MW = 505; 4.12-10 "5 moles) are added to the orange solution. The orange solution is diluted up to 100 ml with toluene, charged into a Buchi 300 ml glass auto- clave and is put under 7 bars of ethylene and maintained at room temperature for 1 hour. It is observed that as ethylene is absorbed, the solution becomes turbid. The autoclave is degassed and the contents discharged without diluting. 1 ml of the solution is removed, 1 ml of a solution of Br 2 in CCl 4 is added and injected into GC: only 1-hexene is present. Activity: 605 moles of ethyl ene/N mole Selectivity: 99% to 1-hexene Example 9 30 mg of V(mes) I (MW = 418; 7.17-10 ~5 moles) in 100 ml of degassed and anhydrous toluene are charged under argon into a 100 ml test-tube. The orange solution is charged into a Buchi 300 ml glass autoclave, put under 7 bars of ethylene and maintained at room temperature for 1 hour. The autoclave is degassed and the contents discharged without diluting. 1 ml of the solution is re- moved, 1 ml of a solution of Br 2 in CC1 is added and injected into GC: no olefins are present. Activity: 0 moles of ethylene/V mole Selectivity: 0% to 1-hexene OLIGOMERIZATION TESTS OF ETHYLENE CATALYZED BY V(I) IN} I 10 Tests carried out at room temperature for 1 hour. 15

Claims: CLAIMS 1. A process for the preparation of 1-hexene consisting in effecting the oligomerization of ethylene in the presence of a catalyst comprising a vanadium complex having the formula: (arene) 2 " VX wherein the term arene represents benzene or mono-, di-, or tri-alkylsubstituted benzene, V is a vanadium ion with a low oxidation state, and X is an anion selected from Cl, Br and I halide ions, or from non-coordinated anions such as B (Ar) 4 ~ , A1C1 4 " , carboxylates and sul- fonates . 2. The process for the preparation of 1-hexene consisting in effecting the oligomerization of ethylene according to the previous claim, characterized in that the reaction is carried out in the presence of a vanadium complex preferably selected from bis- (mesitylene) -vanadium trifluoroacetate bis- (mesitylene) -vanadium-tetraphenylborate bis- (mesitylene) -vanadium-iodide bis- (mesitylene) -vanadium-tetrachloroaluminate. 3. The process for the preparation of 1-hexene consisting in effecting the oligomerization of ethylene according to the first claim, characterized in that the reaction is carried out with the additional presence of a hetero- cyclic compound. 4. The process for the preparation of 1-hexene consisting in effecting the oligomerization of ethylene according to the previous claim, characterized in that the reac- tion is carried out in the presence of a heterocyclic compound preferably selected from pyrroles, substituted pyrroles, phenanthroline, pyridine. 5. The process for the preparation of 1-hexene consisting in effecting the oligomerization of ethylene according to the previous two claims, characterized in that the reaction is carried out in the presence of a heterocyclic compound in a ratio, with respect to the vanadium complex, ranging from 1 to 20. 6. The process for the preparation of 1-hexene consisting in effecting the oligomerization of ethylene according to one or more of the previous claims, characterized in that the reaction is carried out in the presence of a solvent selected from aromatic hydrocarbons and aliphatic hydrocarbons . 7. The process for the preparation of 1-hexene according to the previous claim, characterized in that the reaction is preferably carried out in the presence of a solvent selected from toluene and cyclohexene. 8. The process for the preparation of 1-hexene consisting in effecting the oligomerization of ethylene according to one or more of the previous claims, characterized in that the reaction is carried out at a temperature less than or equal to 150°C. 9. The process for the preparation of 1-hexene according to the previous claim, characterized in that the reaction is preferably carried out at a temperature ranging from 25 to 60°C. 10. The process for the preparation of 1-hexene consisting in effecting the oligomerization of ethylene according to one or more of the previous claims, characterized in that the reaction is carried out at a pressure ranging from 1 to 100 atmospheres. 11. The process for the preparation of 1-hexene according to the previous claim, characterized in that the reac- tion is preferably carried out at a pressure ranging from 1 to 50 atmospheres. 12. The process for the preparation of 1-hexene consisting in effecting the oligomerization of ethylene according to one or more of the previous claims, characterized in that the reaction is carried out for times less than 36 hours . 13. The process for the preparation of 1-hexene according to the previous claim, characterized in that the reaction is preferably carried out for times ranging from 1 to 24 hours.

Inventors: GRANDE MANUELA, MASI FRANCESCO, PROTO ANTONIO, ROMANO ANNA MARIA, SANTI ROBERTO, SOMMAZZI ANNA, GRANDE, MANUELA, MASI, FRANCESCO, PROTO, ANTONIO, ROMANO, ANNA, MARIA, SANTI, ROBERTO, SOMMAZZI, ANNA
Applicants: ENICHEM SPA, GRANDE MANUELA, MASI FRANCESCO, PROTO ANTONIO, ROMANO ANNA MARIA, SANTI ROBERTO, SOMMAZZI ANNA, ENICHEM S.P.A., GRANDE, MANUELA, MASI, FRANCESCO, PROTO, ANTONIO, ROMANO, ANNA, MARIA, SANTI, ROBERTO, SOMMAZZI, ANNA
Application year: 2001
Main classification: C07C11
IPC codes: C07C2