FOAM COMPOSITE

Abstract: A foam composite made up of a scaffold of an open cell hydrophobic material having plurality of surfaces defining a plurality of pores, and a coating of a substantially hydrophilic foam material disposed upon the surfaces of the hydrophobic foam. The resulting foam composite exhibits structural characteristics of the hydrophobic foam and absorbency characteristics of the hydrophilic foam.

Description: FOAM COMPOSITE RELATED APPLICATION This application is a continuation-in-part of U.S. Application Serial No. 09/540,009 filed March 31, 2000. FIELD OF THE INVENTION The present invention relates to the field of polymer chemistry and, in particular, to the field of foam composites having properties of both conventional hydrophobic and hydrophilic polyurethane foams. BACKGROUND OF THE INVENTION Conventional polyurethanes have taken a prominent position in the world as an inexpensive material for use in such diverse applications as foam insulation, adhesives, structural foams, shoe sole and others. The properties of conventional polyurethanes that make these uses possible are its physical strength, low cost, ability to make very low density foam, chemical resistance, and thermal stability. One of the variations of the product family is the manufacture of what are called reticulated foams. These foams are constructed such that the "windows" that separate the individual cells making up the foam structure are open and the material in the windows collapse into the "struts and beams". Thus when fully cured and viewed in a microscope, all one sees is a matrix of "tinker-toy-like" rods connected to one another at the ends. One ofthe advantages of this structure is that it presents very low resistance to the flow of air or water. It is often used as a filter media due to their typically low density and corresponding low cost per unit volume. These foams are hydrophobic, i.e. they do not absorb water. Hydrophilic polyurethanes, on the other hand, while being of similar chemistry, are used in applications where being compatible with water is the primary reason for their use. These uses include controlled delivery devices, chronic wound care dressings and agricultural media. An advantage of hydrophilic polyurethanes over conventional reticulated polyurethanes is their ability to be formulated with active ingredients. Hydrophilic polyurethanes are conventionally made by the emulsification and curing of an aqueous phase with a hydrophilic polyurethane prepolymer. The aqueous phase may contain an active ingredient in which case the ingredient is dispersed in the matrix of the resultant foam. In part, it is this ability to incorporate a wide variety of components in the aqueous phase that makes this chemistry commercially attractive. The essential difference between these two related chemistries is that the hydrophilic polyurethane is compatible with and absorbs water while the conventional polyurethanes are hydrophobic and are incompatible with water. While this hydrophilic nature gives hydrophilic polyurethane its unique applications, it also leads to certain deficiencies. Among these are low physical strength, poor cell size control, relatively high densities causing a relatively high cost per unit volume, and the fact that foam swells considerably upon absorption. OBJECTS OF THE INVENTION It is an object ofthe present invention to provide improved foam composites which have properties of both conventional hydrophobic and hydrophilic polyurethane foams. It is another object ofthe present invention to provide foam composites which can be used as devices to release active ingredients into a fluid stream. SUMMARY OF THE INVENTION The present invention which addresses the needs ofthe prior art provides broadly composite polyurethanes that include both hydrophobic and hydrophilic polyurethane foam entities. By combining these two types of foams, the resulting composite overcomes the disadvantages associated with each, while maintaining their respective advantages. The composite includes a hydrophobic scaffold foam, such as an open cell or open cell reticulated polyurethane foam, coated with an open cell hydrophilic polyurethane foam. This is accomplished by coating the inside surface ofthe open cell foam with a polyurethane prepolymer emulsion and allowing the composite to cure. What results is a foam composite that uses the open cell polyurethane foam as a scaffold or a substrate on which the hydrophilic polyurethane foam is cast. In another aspect ofthe present invention, the composite foams are formed by contacting a reticulated hydrophobic polyurethane foam with a solution of a hydrophilic polyurethane prepolymer in a solvent such as acetone and the like. The solvent ofthe polyurethane prepolymer solution is subsequently recovered thus coating the reticulated hydrophobic polyurethane foam with the hydrophilic polyurethane prepolymer. In another embodiment ofthe invention the composite foams are provided by contacting the hydrophobic polyurethane foam with a liquid phase of a hydrophilic polyurethane prepolymer at temperatures sufficient to lower the viscosity and thereby control the coating weight ofthe hydrophilic prepolymer. It is yet another aspect ofthe invention to provide a composite that overcomes the disadvantages of both hydrophobic and hydrophilic foams while maintaining their respective advantages. Specifically, the hydrophilic coating, which may or may not contain an active ingredient, provides for the hydrophilic character, while the reticulated foam provides for physical strength and the good flow-through aspects that characterize a reticulated foam. Thus, while the hydrophilic coating will swell when it absorbs water, the reticulated foam is sufficiently strong to prevent an increase in the size ofthe composite. It is a further aspect ofthe invention to provide a composite for use as a device for the controlled release of a component into a stream of fluid passing through it. The stream can be a gas or liquid, but in either case the action ofthe composite is to release into the stream a component resident in the hydrophilic polyurethane foam coating. Examples include devices for the controlled release of a pharmaceutical to blood, the controlled release of a fragrance to an air stream, the controlled release of a soap to water stream, and the humidification of a gas stream by the evaporation of water from the hydrophilic coating. It is a further aspect ofthe invention to provide a composite for use as a device that will chemically or biologically act on the stream that passes through it. The stream can be a gas or liquid, but in either case the action ofthe composite is to act upon the stream to produce a chemical or compositional change. One example being a device for the bioremediation of a waste stream through the action of bacteria, enzymes, algae, yeasts or other biological species on the waste stream. Another example includes devices that produce an action comparable to those of living cells, such as liver cells, on physiological fluids to remove or react natural or synthetic toxins. Another example includes devices doped or grafted with ion exchange resins for removing complex inorganic ions from the stream. Further examples include devices having foams in doped or grafted with activated carbons or zeolite which have the ability to remove components from a stream by an adsorption or entrapment mechanism. Another example includes devices for the production or removal of chemicals in a process stream through the action of bacteria, enzymes, algae, yeasts or other biological species. Still another example includes devices for the removal of organic species from a process stream by adsorption on the surface ofthe hydrophilic coating. Finally, other examples might be the removal of water from a process stream through absorption by the hydrophilic polyurethane foam. It is a further aspect ofthe invention to provide a composite for use in devices for the moderation of inhaled air temperatures in low temperature environments. One example of such a device moderates the temperature of inhaled air by passing the air stream over an appropriate phase change material entrapped in the hydrophilic coating. The heat contained in the exhaled air is subsequently trapped by breathing out through another chamber that also contains the phase change material. It is a still further aspect ofthe invention to provide a composite for use as an advanced soil-less growing media. These aspects ofthe invention are not meant to be exclusive and other features, aspects, and advantages ofthe present invention will be readily apparent to those of ordinary skill in the art when read in conjunction with the following description, appended claims and accompanying drawings. BRIEF DESCRIPTION OF THE DRAWINGS Figure 1 is a schematic view ofthe foam composite ofthe present invention. Figure 2 shows the pressure drop of hydrophobic polyurethane foams at 575 ft/min of air. Figure 3 is a graph ofthe surface area of hydrophobic polyurethane as a function of pore size. Figure 4 illustrates the juxtaposition ofthe CO abstraction and the polymerization reactions to produce various foams. Figure 5 is an outline of manufacturing steps in the production of hydrophilic polyurethane. Figure 6 is a process flow diagram of atypical emulsification of a typical polyurethane prepolymer. Figure 7 illustrates a pin mixer used in the emulsification of polyurethane prepolymer. Figure 8 is a flow diagram of process to manufacture the foam composite by the emulsion process. Figure 9 is a graph illustrating the reduction of viscosity with increasing temperature. Figure 10 is a flow diagram ofthe process to manufacture the foam composite by the solvent process. Figure 11 is a flow diagram ofthe process to manufacture the foam composite by the direct cast process. Figure 12 is a schematic view of an embodiment in which the foam composite ed in a device for soil-less growing media. Figure 13 is a schematic view of an embodiment in which the foam composite ed in a controlled release device. Figure 14 is a schematic view of an embodiment in which the foam composite ed in a cell for bioremediation. Figure 15 is a schematic view of an embodiment in which the foam composite ed in a fermentation device. Figure 16 is a schematic view of an embodiment in which the foam composite ed in a device for the treatment of milk. Figure 17 is a schematic view of an embodiment in which the foam composite ed in an enzymatic reactor. Figure 18 is a schematic view of an embodiment in which the foam composite ed in a device used in a femoral shunt. Figure 19 is a schematic view of an embodiment in which the foam composite ed as a scaffold for the propagation of living cells. Figure 20 is a schematic view of an embodiment in which the foam composite ed in the drug delivery system. Figure 21 is a schematic view of an embodiment in which the foam composite ed in an adsorption cell. Figure 22 is a schematic view of an embodiment in which the foam composite ed in a device used for the removal of drugs from blood. Figure 23 is a schematic view of an embodiment in which the foam composite ed in a device used to deionize water. Figure 24 is a schematic view of an embodiment in which the foam composite is utilized in a humidifier for incubators. Figure 25 is a schematic view of an embodiment in which the foam composite is utilized in a humidifier for anesthetics. Figure 26 is a schematic view of an embodiment in which the foam composite is utilized in a device used for administering anesthetic. Figure 27 is a schematic view of an embodiment in which the foam composite is utilized in a device used for drying hydrocarbons. Figure 28 is a schematic view of an embodiment in which the foam composite is utilized in a respirator. Figure 29 is a schematic view of an embodiment in which the foam composite is utilized as a flow-through analytical column for multiple sequential analysis. Figure 30 is an illustration of a column packed with the foam composite ofthe invention used to determine the relationship of flow rate and pressure drop. Figure 31 is a graph illustrating the relationship between flow rate and pressure drop across hydrophobic polyurethane. Figure 32 is a graph illustrating the relationship between flow rate and a ratio ofthe weight of hydrophilic polyurethane to the weight hydrophobic polyurethane in foam composites ofthe invention. Figure 33 is a graph illustrating the relationship between the content of polyurethane prepolymer in solution and the ratio ofthe weight of hydrophilic polyurethane to the weight of hydrophobic polyurethane. Figure 34 is a graph illustrating the effect of temperature on the foam composites of examples 11-15. Figure 35 is a schematic representation of an apparatus using the composites ofthe invention to continuously remove biomass from waste streams containing pollutants or to extract components from a liquid. Figure 36 is a schematic representation of a biofilter cartridge using the composites ofthe invention. Figure 37 is a schematic representation of a filtration process using the cartridge of Figure 36. Figure 38 is a bar graph showing the results obtained by lobster fisherman using the lobster baits prepared as described in Example 16. DETAILED DESCRIPTION OF THE INVENTION Definitions The term " reticulated hydrophobic polyurethane foam" refers to a polyurethane foam having a mesh like structure that does not readily absorb water. This term is defined further below. The term "open cell, hydrophilic polyurethane form" refers to a highly flexible polyurethane foam that absorbs water readily. This term is more specifically defined further below. The term "curing" refers to the conversion of a raw product to a finished and useful condition by application of water for a period of time sufficient to induce physicochemical changes. This term is more specifically defined below. The term "surface area" refers to the total surface area of a substance measurable by the BET technique. The term "functional group" refers to groups of atoms that give the composite or substance to which they are linked characteristic chemical and physical properties. A "functionalized" surface refers to a surface on which chemical groups are absorbed or chemically attached. The term "bioaffecting or active agent" refers to an additive that is a biological entity or produces an effect upon a biological entity or acts upon a biological entity so as to effect a response therefrom. The term "non-bioactive ingredient" refers to an additive other than bioaffecting agents. Detailed Description The invention relates broadly to composites comprising open cell hydrophobic polyurethane foams and open cell hydrophilic foams. The cells in the hydrophobic foams may vary in their degree of openness. Hydrophobic foams useful in the practice ofthe invention include those having a reticulated or substantially reticulated cell structure as well as those having an open-cell non-reticulated structure. Hydrophobic foams having an open cell, non-reticulated structure lend themselves to applications in which absorbency is particularly important. Hydrophobic foams having a more open, reticulated structure lend themselves to applications in which a gas or liquid is passed through the structure, as in a filter, and where fluid flow and pressure drop considerations are of particular importance. In the following description the terms open cell, reticulated or substantially reticulated may be used to characterize the open cell structure ofthe hydrophobic foam. It will be understood that these terms may in contexts be used interchangeably and are not meant to limit the scope o the invention. Referring first to Figure 1, the foam composite 10 is shown. The hydrophobic polyurethane foam forms a reticulated scaffold 12. The hydrophobic foam scaffold 12 forms a backbone for an open cell foam coating 14, such as open cell hydrophilic polyurethane. The hydrophobic polyurethane foam scaffold 12 is typically a reticulated foam made from water insoluble polyester or polyether backbones and diisocyanates as caps to the polyols. Other ingredients, such as surfactants and catalysts, may be added to aid production. Only small amounts of water are added as a necessary component ofthe chemistry. The reticulated foams useful in the present mvention are typically produced by the so-called "one-shot" process wherem all of the ingredients are mixed in a single step to produce the final foam product. Using heat and pressure in specially designed vessels, a flexible skeletal foam structure without cell membranes is produced. The open-pore structure can be produced in a range of precisely controlled pore sizes that contain void volumes of up to 98% and surface areas of up to 2000 ft 2 /ft 3 . Narious pore sizes, typically from 4 to 100 pores per linear inch (ppi) enable the use ofthe hydrophobic polyurethane in specific applications. The high porosity of this material also helps control permeability and adds to design flexibility. Among the benefits of reticulated hydrophobic polyurethane foams are easy fabrication and chemical resistance. Such reticulated foams also exhibit high tensile strength, elongation and tear properties that allow such fabrication techniques as cutting, shaping, stapling, tacking, stitching, cementing, laminating and grommeting. The reticulated hydrophobic polyurethane is supplied in sheets, rolls, die-cuts, and complex compound shapes. Hydrophobic polyurethane foams which have been found suitable for use in the foam composite ofthe present invention include without limitation those marketed under the trademarks Crest Foam and FoamEx. These products are commercially available from Crest Foam, Moonachie, New Jersey, USA and FoamEx, Eddystone, Pennsylvania, USA. There are many commercial applications for reticulated hydrophobic polyurethane foams. Generally, these applications are based on properties such as the unusual physical strength ofthe hydrophobic foam, controlled pore size, and surface area. Table 1 below summarizes the physical properties of hydrophobic polyurethane foams useful in the present invention. The information set forth in Table 1 below was obtained based on tests conducted according to ASTM 3574-91 on hydrophobic polyurethane foams from Crest® foam. Table 1: Physical Properties of Reticulated Foams Property S-10 S-40 S-90 Pores/Linear Inch 10.0 40.0 90.0 Density lb/ft 3 1.9 1.9 1.9 25% Compression Load Deflection psi 0.5 0.5 0.5 Tensile Strength psi 16.0 20.0 30.0 Elongation % 180.0 160.0 240.0 Tear Strength lb/in 4.0 4.0 3.5 Compression Set @ 50% Deflection psi 15.0 15.0 15.0 Air Flow cfin 25.0 14.0 4.0 The pressure drop of hydrophobic reticulated foam of various pore sizes is shown in Figure 2 at 575 ft/min. of dry air through 1 ft 2 of 1 inch thick foam. The surface area of a hydrophobic reticulated foam is seen as a function of pore size in Figure 3. The chemistry of making open cell hydrophobic polyurethane foams is described as being an isocyanate-capped polyether polyol and is discussed in more detail further below. Prepolymers made of this chemistry which are suitable for the present invention are described in U. S. Patent Nos. 3,903,232 and 4,137,200 both to Wood, et al. incorporated herein by reference as if set forth in full. The isocyanate- capped polyol is known in the industry as a prepolymer or a quasipolymer. Isocyanates suitable for this invention are aromatic, such as, for example, toluene diisocyanate (TDI) or methylene diphenyl isocyanate (MDI), or with a aliphatic diisosyanate, such as hydrogenated MDI or isopherone diisocyanate. Isocyanates and polyols useful in making the open cell hydrophilic polyurethane foam for use in the foam composite ofthe invention are described in U.S. Patent Nos. 5,064,653 and 5,065,752 both to Session, et al. incorporated herein by reference as if set forth in full. Polyether polyols are homopolymers of ethylene oxide, also known as polyethylene glycols, or copolymers of ethylene oxide and propylene oxides. The value of this class of prepolymers is based on its compatibility with water. It is the ability to be emulsified with large amounts of water that forms the basis for the value of these prepolymers. Within the water compatible components can be included a wide variety of other materials. Among those are mineral fillers that are used to affect the compression characteristics ofthe foam. Peat moss can be added to foam to form the basis of a high value soil-less growing medium. While fillers can be added, they are not necessary. At the other end ofthe spectrum is the inclusion ofa simple emulsifying agent. The result is a low extractable, biocompatible material useful for a wide variety of medical products. The ability to incorporate other materials in hydrophilic polyurethane foam offers the product designer a material that has functionality greater than its physical characteristics. This flexibility comes at a price. The physical strength of hydrophobic polyurethane is low. The wet tensile strength of open cell hydrophilic polyurethane is only about 4 psi which is significantly lower than the tensile strength of hydrophobic polyurethane. The reaction to form hydrophilic polyurethane utilizes large amounts of water and results in a relatively high density and poor cell size control. The compressive strength ofthe polymer product is also low. In some applications, this is a positive characteristic since products made from this material are soft and have a pleasant feel. However, this is an undesirable characteristic for many industrial applications. The physical characteristics of open-cell hydrophilic polyurethane foam are summarized in Table 2. Table 2: Physical Properties of Hydrophilic Polyurethane Foams 1 Property Pores/Linear Inch 200.0 Density, lb/ft 3 6.0 25% Compression Load Deflection, psi 0.1 Tensile Strength, psi 4.0 Elongation % 300.0 Tear Strength, lb/in 2.0 Compression Set @ 50% Deflection, psi 2.0 Air Flow cfm @ 0.5 ΔP 0.2 Medical Grade The above properties are for single component polymer systems, but other compositions are also possible. Trudell, et al. teach in U.S. PatentNo. 5,207,705 a collagen polyurethane foam blend that is useful as a biocompatible surface for human cell propagation. This system is within the scope of this invention. The collagen is added to an aqueous phase. It is then emulsified with a hydrophilic polyurethane prepolymer and applied to the scaffold as described within. Once the open cell coating polyurethane is formed, it can be post treated by grafting ligands onto its surface thereby forming a functionalized surface. In one embodiment ofthe present invention, acrylic acid can be grafted onto the surface of an unsaturated hydrophilic polyurethane coated scaffold using a grafting process for hydrophilic polyurethane described by Mekras, C.L., et al, Immobilization ofalpha- chymotrypsin onpoly (urethane graft-acrylic acid), Int. J.Biol. Macromol, 1989 vol. 11 No. 2, pp. 113-118 incorporated herein by reference. The graft was prepared using 2,2'-azo-bis-isobutyronitrile as a radical initiator and acrylic acid as the monomer. In another embodiment ofthe invention, a polyurethane polymer was treated with hydrogenated methylene diphenyl-isocyanate and then with human serum albumin to produce a grafted albumin surface. Such treated polymers is reported by Rye, G. et al. to have unique blood compatibility characteristics. Prepolymers suitable for use in the present invention are isocyanate-capped polyether prepolymers with an NCO functionality of greater than 5% as more particularly described below. The prepolymers are based on polyether polyols capped with aromatic isocyanates such as for example toluene diisocyanate (TDI) or methylene diphenyl isocyanate (MDI) or with aliphatic isocyanates, such as, for example isopherone diisocyanate (IPDI) or hydrogenated methylene diphenyl isocyanate (HMDI). The polyether polyols are hydrophilic polyoxyalkylenes with a minimum of 40 mole% ethylene oxide. Crosslinking sites are developed, when necessary, during the prepolymer formation by using the techniques described in Saunders, J.H., et al., Polyurethanes, Chemistry and Technology. Part II, Interscience Publishers, New York The method of analysis is described in Analytical Chemistry of he Polyurethanes, Robert E. Krieger Publishing Company, Huntington, NY 1979 pp357-359 incorporated herein by reference. These techniques are as follows: 1. The addition of water to the prepolymer polyols to form urea and subsequently biuret linkages in the prepolymer; 2. The formation of allophanate linkages by prolonged heating at elevated temperatures; 3. The branching of prepolymers by the addition of triols or tetrols, such as for example, trimethylolpropane, glycerol, or pentaerythritol; 4. The formation of branches by the use of selective catalysts. Isocyanate-capped polyether prepolymers which have been found to be suitable for use in the practice ofthe present invention include without limitation prepolymers commercially available from the following companies: Lendell Manufacturing, St. Charles, Michigan, U.S.A.; Rynel Ltd. Inc. Boothbay, Maine, U.S. A; Dow Chemical, Midland, Michigan, U.S.A.; and Mace Adhesives and Coatings, Dudley, Massachusetts, U.S.A. Table 3 below lists polyurethane prepolymers of these companies and the NCO functionality content of their respective prepolymers. Table 3 Rynel Prepolymer Type % NCO B-l 7.4 - 8.32 A-62 10.0 - 11.4 Trepol 5.2 - 6.4 Mace Adhesives & Coatings Bipol 5.5-6.5 Dow Chemical Hypol 2000 6.3-7.2 Hypol 2002 6.3-7.2 Hypol 3000 9.5-10.3 Hypol 5000 9.5-11.13 Lendell Manufacturing Prepol 8.0-8.5 The method of analysis ofthe NCO functionality is described in Analytical Chemistry of Polyurethanes, Robert E. Krieger Publishing Company, Huntington, New York (1979). Unlike the process used to make hydrophobic polyurethanes, hydrophilic polyurethanes are preferably made by the so-called pre-polymer or pseudo pre- polymer method. In this technique, the polyol and the isocyanate are reacted in various ratios and by various reaction schemes to produce an intermediate product called a pre-polymer or quasi pre-polymer. This is then emulsified in an aqueous phase to produce the final foam product 14. The isocyanate end groups on prepolymer molecules are reactive to any compound with an active hydrogen. Thus if a prepolymer is mixed with an alcohol or an amine, a reaction takes place that essentially caps the prepolymer and terminates the reaction as shown below: If the alcohol or amine is difunctional (that is having an amine or alcohol group at two positions on the molecule) it will continue to react with other isocyanate end groups. The result of this process is a continuous building of molecular weight until the isocyanate groups or the other reactants are consumed. This is the basis of the elastomer technology, applicable not only to hydrophilic polyurethanes but also to all polyurethanes. This reaction is used to obtain coatings for fabric, leathers and many other surfaces. When practiced to produce hydrophilic polyurethanes a film with a very high water vapor transmission rate is obtained. When applied to a fabric such as a continuous film, it is said to have high breathability. It has the typical disadvantages of hydrophilic polyurethanes in that it is physically weak and swells upon the addition of moisture. There are a variety of amines that are used for this purpose. Each adds it own physical properties to the resultant film. The molecular weight, molecular structure, and the hydrophilicity of the amine contribute to the properties of the resultant film. The reaction with amines is typically very fast relative to the reaction with water. If the prepolymer has little or no crosslinking, the resultant elastomer can be thermoplastic. With crosslinking, however, the film can develop significant strength. If a chain-terminating component is added to the elastomer reaction, the molecular weight ofthe film can be limited to remain within the adhesive boundaries. Thus by the proper control ofthe reaction conditions, a high moisture vapor transmissive adhesive film can be produced. The reaction of primary interest, however, is the reaction of a hydrophilic prepolymer with water as shown below. O=C=N-R-N=C=O + HOH ► O=C=N-R-NH 2 + CO 2 In this reaction, the production of CO 2 and an amine proceed simultaneously to develop, ultimately a stable foam. This is the core reaction of hydrophilic polyurethane foam technology. The amine product ofthe reaction develops the physical strength ofthe foam composite by polymerization to contain the evolution ofthe CO 2 . As a result ofthe CO 2 evolution, a radical change in the rheology ofthe reacting mass takes place early in the process. Once the water and the prepolymer are mixed, the rheology ofthe emulsion is that of a liquid. If it remained a liquid, the CO 2 would be able to escape the emulsion and the result would be a closed cell, high density foam of little commercial interest. Commercially available prepolymers have a significant degree of crosslinking and thus, soon after the reaction is initiated, the emulsion changes its rheology from a true liquid to a gel. It is part ofthe design requirements of a commercial prepolymer that there be sufficient crosslinking to rapidly develop enough gel strength to withstand the internal pressures developed by the evolving CO . Since the evolution of CO 2 and the polymerization are two separate reactions, each with its own activation energy, a change in temperature affects the rate ofthe reaction to a different degree. For instance, an increase in temperature of even a few degrees, accelerates the CO 2 reaction more than it accelerates the amine reaction. In as much it is the amine that produces the gelling ofthe mass, the CO evolves, at first, in a liquid environment and, even if the emulsion has gelled, the CO 2 internal pressure may exceed the ability of the gel to contain it. As a result, the foam may expand initially, but the emulsion will reach a point where it will visibly collapse. This can be used to advantage if a high density hydrophilic polyurethane is required, but typically this is not desired. Alternatively, if the temperature is lowered, the strength ofthe gel increases faster relative to the rate of evolution of CO 2 . However, the CO 2 reaction must take place first to produce the amine. Lowering the temperature has the effect of decreasing the difference in reaction rates. From a practical point of view, the gel strength develops so as to be able to withstand the internal pressures. This is evidenced by a slower rate of rise and the result is a higher density product. In the extreme, a closed cell foam is produced. An efficient process must juxtapose these reactions so as to produce the desired product as illustrated graphically in the Figure 4. Accordingly, the control of temperature is a critical process parameter. An efficient process will focus the control efforts on the temperatures ofthe components, the degree to which the two phases are emulsified and other classical control methods. Once the emulsion is made and dispensed, there is little that can be done to control what happens. In this sense, the process changes to a more or less chaotic condition. From a control point of view, every thing that can be done to moderate the process must be done before or during the emulsion stage. The flow diagram shown in Figure 5 is common to most if not all hydrophilic polyurethane foam manufacturing processes. The preparation refers to the treatment ofthe prepolymer and the aqueous phases before they are pumped into an emulsifier. This is typically tempering them with respect to temperature. This usually done in a jacketed vessel. A prepolymer tank is closed and is usually blanketed with dry nitrogen to prevent reaction with the humidity in the air. Inasmuch as the prepolymer is a high viscosity liquid at room temperature, the prepolymer temperature can be raised to between 80°F and 100°F. This lowers the viscosity ofthe prepolymer enough to be pumped without fear of cavitating the pump. As a final control ofthe temperature it is typically pumped through a heat exchanger designed to ensure that the temperature ofthe prepolymer is controlled to within 1°F of a set point. If a temperature above room temperature is used, heated lines are recommended. Delivery ofthe prepolymer to the mixer is typically accomplished by using a gear pump. These are positive displacement devices, which ensure a precisely controlled volume of material is delivered to the emulsifier. Care must be taken, however, that an uninterrupted flow of prepolymer to the pump on the low pressure side is maintained. Attempting to pump liquid faster than the prepolymer can flow into it results in cavitation which changes the flow rates and can gel the prepolymer. Figure 6 shows a typical prepolymer process flow diagram. The preparation of the aqueous stream is similar. Due to the usually lower viscosity ofthe aqueous stream, a gear pump is not recommended. A progressive cavity pump, such as a Moyno-type, is preferred. A consideration in the choice of pumps is the components ofthe aqueous phase. If the aqueous phase contains a solid, as in a slurry or emulsion, a Moyno-type pump is highly preferred. When using latices, the shear forces created by the pump can coagulate the fluid. Typically, the temperature ofthe aqueous stream is used to adjust the quality ofthe foam. For instance, if a foam is found to have large cells and a low density, the temperature ofthe aqueous stream might be lowered. Thus the aqueous temperature can be viewed as a primary means to fine-tune the process of preparing open-cell hydrophilic polyurethanes. Other control methods exist, such as adjusting the emulsifier speed, but controlling the temperature ofthe aqueous phase is the more convenient method. As with the prepolymer stream, the important parameters ofthe aqueous stream are temperature and flow rate. Any pump system that meet these parameters will be effective. Pulsatory pumps, such as peristaltic, piston, diaphragm, and the like should be avoided, but can be made to work if a pulse-reducing chamber or coil is used. Depending on the nature ofthe aqueous stream, continuous agitation might be required. With those exceptions, a process flow scheme ofthe aqueous stream would be similar to that for the prepolymer flow diagram shown in Figure 6. In both cases, the prepolymer and the aqueous streams must be engineered in such a way as to deliver safely both streams to the emulsifier at a precise flow rate and a precise temperature. The absolute values are determined by a number of process specific requirements, but the ratio of aqueous to prepolymer should be controlled to within 1% preferably to within 0.5% and the temperatures should be controlled to within 1.0°F and preferably 0.5°F. The next step in producing an open cell hydrophilic polyurethane foam for use in the invention is the emulsification ofthe prepolymer and aqueous phases. The device that performs this operation is typically called the mix head. There is a wide variety of equipment whose purpose is to produce the emulsion. The preferred designs fall into the category of what are called pin mixers. Figure 7 shows a typical design of a pin mixer. Although not shown in Figure 7 , the mixer can have what are called stators. These are pins attached to the walls ofthe mix head and, therefore, they do not spin. These stators increase the turbulence inside the mixhead. What results, typically, is a prepolymer in water emulsion, i.e., with water as the continuous phase. Inasmuch as this is essentially the last stage in which we can control the quality ofthe foam, there are a number of variables to be discussed. The temperature is of critical importance to a well-controlled process. For the most part, it is the temperature ofthe emulsion leaving the mix head which is of principal concern. This is essentially determined by the temperatures ofthe component parts, but in the context that a few degrees can be significant, the mix head itself can have an effect on the emulsion. Depending on the speed at which the mixer spins, it can add 2-3 °F to the emulsion. It is the function ofthe mixhead, however, to create an emulsion. It is the quality ofthe emulsion that, for the most part, defines the cell structure ofthe resultant foam. Emulsions of very small droplet sizes will result in a small-celled foam, all other things being equal. Emulsions with a broad droplet size distribution will have a wide variety of cells in the foam. The primary determinant ofthe size and distribution ofthe emulsion and the cell structure ofthe foam is the use of an appropriate emulsifier. The rate at which the foam absorbs water is known by several names, but the most common is wicking. A fast wicking foam will begin to absorb as soon as it is placed in water. Values of less than a second are usually reported as "<1 second". This can be an important technical factor and needs to be given attention during design ofthe open cell hydrophilic polyurethane useful in the present invention. The control of wicking is strictly a function ofthe emulsifier package that is used. The hydrophilic polyurethane foam itself has very slow wicking values (> 5 minutes). If a water-soluble surfactant is used, such as Pluronic F-68, Tween 20, and the like, the wicking will be greatly increased. If a waxy surfactant such as Brij 72, for example, is used the wicking will not be increased as much. The NCO concentration of prepolymers is a measure ofthe amount of CO 2 that can be generated upon the addition of water. Inasmuch as it is the CO 2 that creates the foam structure, the higher the percentage of NCO the more foaming takes place. At concentrations above 1%, enough CO 2 is generated not only to produce a foam but also to develop enough internal pressure to break the "windows" between developing cells ofthe resulting hydrophilic polyurethane. This is the origin ofthe open cell structure that is an essential aspect of this invention. At concentrations below approximately 1%, a dense, closed cell mass is made. On the other hand, at concentrations above 14% so much CO 2 is generated that the gas is able to break through the surface thus liberating so much ofthe CO 2 that the foam collapses. This effect is also seen if the temperature is too high, for instance above 120°F. The range of NCO values for the prepolymers useful in the present invention is from about 5% to about 15% by weight. In a preferred embodiment of this invention in order for the prepolymer to contain sufficient NCO to develop a preferred open-cell foam structure a range from about 6% to about 9% by weight is recommended. The foam composite ofthe present invention is provided by applying an open cell hydrophilic polyurethane foam coating to a reticulated hydrophobic polyurethane foam according to the processes discussed below. By combining these two types of foams, the resulting composite overcomes the disadvantages of both hydrophobic and hydrophilic polyurethane while maintaining their respective advantages. Specifically, a hydrophilic coating, which may or may not contain an active ingredient, provides for the hydrophilic character, while the reticulated foam provides for physical strength and the good flow-through aspects that characterize a reticulated foam. Thus, while the hydrophilic coating will swell when it absorbs water, the reticulated foam is sufficiently strong to prevent an increase in the size ofthe composite. The resulting foam composite ofthe present invention has a density from about 0.03 g/cc to about 0.10 g/cc. Its pore size distribution varies from about 8 pores per linear inch (ppi) to about 100 ppi. In a preferred embodiment the pore size distribution is from about 10 ppi to about 45 ppi, where the ratio ofthe weight ofthe open cell hydrophilic polyurethane coating to the weight ofthe hydrophobic foam is from about 0.01 to about 15, and preferably from about 0.5 to about 10 depending upon the application for which the foam composite has been engineered. The surface area ofthe foam composite ofthe invention varies from about 100 ft 2 /ft 3 to about 2000 ft 2 /ft 3 and preferably from about 300 ft^/ft 3 to about 2000 ft 2 /ft 3 . The absorbency characteristic ofthe foam composite ofthe present invention depends upon the amount ofthe open cell hydrophilic polyurethane coating. Flow characteristics ofthe foam composites ofthe invention have been examined as a function of pore size and amount of open cell hydrophilic foam applied to the reticulated foam structure. It has been found that the smaller the cell size ofthe foam composite the higher the pressure drop at any given flow. For example, a foam composite having a cross sectional area of approximately 2 in and the thickness of approximately 7 inches, a pore size of about 10 ppi and a weight ratio of hydrophilic to hydrophobic polyurethane of 1.1 exhibits a pressure drop of water passing through it from about 0.06 psi to about 1.25 psi at flow rates from approximately 1 to approximately 5 gal/min. A foam composite having the same cross sectional area and thickness and a pore size of 10 ppi, but an increased weight ratio of hydrophilic to hydrophobic polyurethane of approximately 2.6 exhibits a pressure drop from about 0.06 psi to about 1 psi at flow rates from about 1 to about 3 gal/min. The foam composite ofthe present invention is also very durable. In one study, the foam composite ofthe invention was used to remove water from a hydrocarbon fluid. A column of foam composite having a diameter of 4 inches and a thickness of 12 inches was placed in a cartridge and a quantity of 10 gallons per minute ofthe hydrocarbon fluid was pumped through it for 60 minutes without damage to the foam composite. The durability ofthe coating is further demonstrated in a study ofthe hydration/dry cycle. A sample of foam composite consisting of 10 grams of reticulated foam of Crest T-20 coated with 6 grams of an open cell hydrophilic foam made from Lendell PrePol® prepolymer by the emulsion process, as described in Example 1 herein, was immersed in water at ambient temperature for 30 minutes to hydrate it fully. It was then removed and dried at 105°C until the foam composite achieved constant weight. It was rehydrated and dried by this process 10 times. No flaking ofthe hydrophilic foam coating was observed at any time. Table 4 below shows the data: Table 4: Rehydration of Foam Composite Times Hydrated and Dried Total Weight Dry (grams) 1 16.1 3 16.1 5 16.3 7 16.1 10 161 This experiment demonstrates the durability ofthe foam composites ofthe invention as evidenced by their ability to be fully dried and yet not flake off. Without being bound by theory, it is believed that the durability ofthe foam composites ofthe present invention is due in part to the strong bonding existing between the open cell hydrophilic polyurethane coating and the reticulated hydrophobic scaffold. In another preferred embodiment ofthe present invention, the absorption capability ofthe foam composite ofthe present invention is enhanced by contacting the hydrophobic polyurethane scaffold with a mixture of a prepolymer emulsion of the open cell hydrophilic polyurethane and a hydrophilic hydrogel emulsion. Useful hydrophilic hydrogels for this embodiment ofthe invention include without limitation those based on polysaccharides and acrylics. Polysaccharide hydrogels useful in the invention include without limitation alginate, carrageenan, agar, agarose, curdlan, pullulan, gellan and the like. Acrylic hydrogels useful in the invention include, without limitation, polyacrylamide, poly (ethyl methacrylate), poly (glycol methacrylate), poly (hyroxy methyl acrylate), poly (sodium acrylate), mixtures thereof and the like. The hydrophilic polyurethane prepolymer and the hydrophilic hydrogel are preferably in a ratio from about 0.01 to about 10.0 and preferably from about 1.0 to about 5.0 of hydrogel to hydrophilic polyurethane foam. The mixed emulsion containing hydrophilic hydrogel and hydrophilic polyurethane prepolymer when reacted in place becomes firmly bound to the hydrophobic polyurethane scaffold. According to one embodiment ofthe invention, a foam composite is provided by contacting a prepolymer emulsion of hydrophilic polyurethane with a reticulated hydrophobic polyurethane scaffold. The contacting ofthe prepolymer emulsion with the reticulated hydrophobic polyurethane scaffold can be accomplished in anyway available to one skilled in the art. Examples of contacting include, without limitation, dipping ofthe scaffold into a prepolymer bath, coating ofthe reticulated scaffold with the prepolymer emulsion by distributing it with a rolling pin, spraying the prepolymer emulsion over the reticulated scaffold and the like. The contacting step is followed by curing the emulsion impregnated reticulated hydrophobic polyurethane for a period of time sufficient to form the foam composite. Prior to curing, the emulsion impregnated reticulated foam can, optionally, be subjected to a stream of air blowing through the curing composite. This minimizes the formation of windows across cells to ensure that the reticulated structure ofthe foam composite is uniformly retained. A flow diagram showing the emulsion process is shown in Figure 8. Curing the prepolymer emulsion impregnated hydrophobic polyurethane is accomplished by allowing it to age undisturbed for a period of time sufficient for approximately 99%) ofthe isocyanate functionality to have reacted with the water. Generally, the amount of time necessary for curing to take place varies from about 10 minutes to about 30 minutes depending upon the temperature ofthe water and the curing chamber which is typically from 20°C to about 30°C. The curing step is ordinarily followed by an optional drying step during which any excess water present in the foam composite is driven off. The amount of prepolymer in the emulsion used to prepare the hydrophilic foam composition is not particularly critical, but depends on a number of factors including the temperature and pore size ofthe reticulated foam to be coated. A ratio range of from about 0.8:1 to about 2.2:1 of aqueous phase to prepolymer phase is typical, with a ratio range of from about 1 : 1 to about 2:1 being preferred. The higher ratios, which typically result in lower viscosity, are preferred for smaller pore sizes. Lower ratios are preferred for larger pore sizes. Prepolymer emulsions of higher viscosities typical of lower ratios are used when higher coating weights are desired. High ratios are also preferred when the temperature ofthe emulsion needs to be limited. This is the case when enzymes, bacteria or other components that are temperature sensitive are included in the emulsion. The temperature ofthe emulsion used to prepare the hydrophilic foam composition is important for two reasons. First, as indicated above, temperature sensitive components in the emulsion may have to be protected by using low temperature components, i.e., a aqueous phase and prepolymer phase and minimizing the exotherm that is the natural result ofthe reaction of water and the prepolymer. Secondly, the temperature is important in controlling the gel time ofthe emulsion. This point in the reaction, known in the industry as cream time is the point at which the reacting emulsion changes from a liquid to a gel. Gelation is an important step in the development ofthe polyurethane foam structure. It is an essential aspect ofthe present invention that the emulsion be cast onto the structure of the reticulated foam before gelation. Those skilled in the art of prepolymer emulsions will understand that gelation is a separate step for curing. During gelation only approximately up to 10%) ofthe isocyanate functionalities present in the emulsion react primarily with other isocyanate functionalities. The range of temperatures used in the practice of this invention is from about 4° to about 50°C, and preferably from about 15° to about 40°C. A wetting agent is typically included in the emulsion to provide for more uniform wetting ofthe resultant foam. The wetting agent also aids in controlling the cell size ofthe foam. Wetting agents suitable for use include non-ionic surfactants. Examples of materials that are useful in the present invention include but are not limited to block copolymers of ethylene oxide and propylene oxide sold by BASF Wyandotte Corporation of Parsippany, NJ, USA under the trade name Pluronic®. Pluronic L-62 and F-88 available from BASF Wyandotte Corporation are preferred. Pluronic F-88 is suitable and has been used in medical devices due to its biocom- patibility. Generally the amount of wetting agent should be from about 0.01 to about 1.0% based on the weight ofthe aqueous phase. A preferred amount of wetting agent is 0.05-0.5% by weight. In another embodiment, the foam composite ofthe invention is made by a process wherein the reticulated hydrophobic polyurethane foam is prepared by contacting with a solution of a prepolymer in a nonreactive solvent. Useful nonreactive solvents for the solvent process ofthe invention include solvents that are found to dissolve the prepolymer without reacting with it within the time required for deposition on the reticulated foam. Such solvents include without limitation acetone, toluene, xylene, benzene, mixtures thereof or the like. As in the emulsion process, the contacting may be accomplished by coating, spraying or dipping the reticulated scaffold into the prepolymer solution. The coated or otherwise prepolymer impregnated reticulated hydrophobic polyurethane is squeezed or hung in place to remove the excess prepolymer solution. The critical step in this process is to reduce the viscosity ofthe prepolymer solution. A non-reactive solvent is used to dissolve the prepolymer and thus lower the viscosity ofthe prepolymer coating. The degree to which the viscosity is lowered will control the amount of prepolymer that is deposited on the reticulated scaffold. The solvent may be evaporated or recovered for further use. Just as in the emulsion process, there must be a curing step ofthe reticulated scaffold coated with the prepolymer solution for the foam composite ofthe present invention to be formed. Curing can take place in a water bath or in a high humidity chamber. The temperature ofthe water bath can be from about 4°C to about 50°C, and is preferably in the range of 20°C to 40°C. The curing time is generally from about 10 minutes to about 30 minutes. As an alternative, a water vapor curing chamber can be used wherein the water vapor is kept typically at temperatures up to 95°F and high relative humidity in excess of 95%>. The residence time for curing in a water curing chamber varies from about 10 minutes to about 30 minutes. A flow diagram illustrating steps in the solvent process is shown in Figure 10. In yet another embodiment, the foam composite ofthe present invention is prepared by a direct cast process. As is the case with the solvent process, in the direct cast process the critical objective is to reduce the viscosity ofthe prepolymer coating. In this process the reticulated hydrophilic polyurethane scaffold is contacted with the prepolymer directly where the viscosity ofthe prepolymer is controlled by increasing its temperature. Increasing the temperature reduces the viscosity. Figure 9 illustrates the effect of temperature on the viscosity of lendell PrePol® prepolymer. Other prepolymer useful in the present invention have similar viscosity/temperature curves. A flow diagram showing the direct cast process is shown in Figure 11. It is readily apparent from Figure 11 that the direct cast process has the same steps as the solvent process except that the prepolymer is not dissolved in any solvent and its viscosity is controlled by controlling the temperature ofthe prepolymer. Curing can take place in a water bath or in a high humidity chamber as described above. In another aspect ofthe invention, one or more additives may be incorporated in the hydrophilic polyurethane foam. The additives include bioaffecting or active agents and/or nonbioactive ingredients. Bioaffecting or active agents useful in the present invention include without limitation pharmaceuticals, fragrances, soaps, pesticides, herbicides, yeasts, bacteria, algi, enzymes, plants, animal cells, human cells, mixtures thereof and the like. Useful non-bioactive ingredients include without limitation hydrogels, fillers, activated charcoals, zeolites, ion exchange resins, phase change materials, mixtures thereof and the like. In other preferred embodiments ofthe invention one or more additives can be incorporated in the foam composite. The incorporation of additives can be accomplished in any manner known in the art. In one preferred embodiment the additives are immobilized in the foam composite. In another aspect ofthe invention bioaffecting agents such as, for example, antigens or ion exchange ligands are grafted onto the foam composite directly or they are grafted onto a hydrogel containing hydrophilic polyurethane coating. The grafting is accomplished by methods known in the art. Inasmuch as the hydrophilic foam formulation can contain an active ingredient, the foam composite 10 can have a hydrophilic coating containing the active ingredient. In one example, the aqueous phase with which the hydrophilic prepolymer is emulsified may contain a fragrance. When combined with a reticulated foam 12, as described in the above example, a foam composite 10 with the fragrance imbedded in its structure results. Such a device might be used as a room freshener. As set forth with reference to the attached drawings, the invention has many embodiments. Referring first to Figure 12, one embodiment ofthe foam composite 10 contains plant growth media, such as peat moss, to produce a device for growing plants on a soil-less media. This can be used in hydroponics, for growth of high value plants, plants for transplant and plants for export, to name a few applications. Another embodiment is shown in Figure 13. As shown here, the foam composite 10 can be used as a controlled release device. In such an embodiment, the coated foam is formulated to include an additive, such as liquid soaps, fragrances, herbicides or pesticides. These additional components are released when a user uses the foam in a predetermine manner; i.e. mixing with water in the case ofthe soap, herbicides or pesticides, or evaporating into the air in the case of the fragrances. Referring now to Figure 14, in another embodiment ofthe invention, the foam composite 10 is formulated to include algae or bacteria to create a cell for bioremediation device. The hydrophilic foam 14 is prepared according to the procedures taught in Rao, K.K.; Hall, D.O. Trends Biotechnol. 1984. vol. 2, no. 5, pp. 124-129 and combined with the reticulated foam 12. In this embodiment, waste stream water or domestic water flows through the device, and becomes purified via through treatment by the algae or bacteria. In another embodiment ofthe invention, the foam composite 10 is formulated with yeast to yield a fermentation device. The hydrophilic foam 14 is prepared according to the procedures taught in Lorenz, O.; Haulena, F.; Rose, G. Biotechnol. Bioeng. 1987. vol. 29, no. 3, pp. 388-391 and combined with the reticulated foam 12. As shown in Figure 15, as sugar-containing water flows through the cell, the sugar is fermented, resulting in the production of alcohol. Referring now to Figure 16, in another embodiment ofthe invention, the foam composite 10 is formulated with a lactase enzyme which enzymatically converts whole milk into lactose-free milk. The hydrophilic foam 14 is prepared according to the procedures taught by Storey, K.B.; Chakrabarti, A.C. Appl.Biochem. Biotechnol. 1990. vol. 23, no. 2, pp. 139-154, and combined with the reticulated foam 12. Figure 17 shows another embodiment ofthe invention in which the foam composite 10 is formulated with immobilized enzymes or grafted to yield a flow through chemical reactor using enzymes or an ion exchange. Such an enzymatic reactor can be incorporated with any enzyme chosen by the user to perform the desired chemical reaction. In this embodiment, the hydrophilic foam 14 is prepared according to the procedures taught by Hu, Z.C.*; Korus, R.A.; Stormo, K.E. Appl. Microbiol. Biotechnol. 1993 vol. 39, no. 3, pp. 289-295, and combined with the reticulated foam 12. Figure 18 shows another embodiment ofthe present invention, in which the foam composite 10 is formulated to include antibodies specific for a particular antigen and is incorporated into a blood shunt such as a femoral shunt. The antibodies are incorporated into the hydrophilic polyurethane coating or are otherwise immobilized on the surface ofthe foam composite ofthe invention. The foam composite with the immobilized antibody is then placed in a device such as a canister to which blood from a living subject is fed using, for example, a femoral shunt. After the blood passes through the foam composite bearing device, it is returned to a major vein. In operation, as the blood passes through the foam composite filter, the antibodies immobilized on the surface ofthe foam composite complex with the antigen for which they are specific, capture the antigens and remove them from the blood. The device can be used to treat the blood of persons with drug overdoses, to remove HIV virus from the blood or to remove other environmental contaminants from the blood. Other antigens which could be separated by using specific antibodies immobilized in the foam composites ofthe present invention include, without limitations, HIN protease, components of HIN virus, opiates, such as, for example, codeine, cocaine, heroin, their Ci-C 6 analogs and the like. Referring now to Figure 19, another embodiment ofthe invention is a scaffold for the propagation of cells. This embodiment is created by seeding the foam composite 10 with hepatic or other human cells, as taught in Matsushita, T.; Ijima, H.; Koide, Ν.; Funatsu, K. Appl. Microbiol. Biotechnol. 1991. vol. 36, no. 3, pp. 324-326. The resulting embodiment can be used in the development of hybrid artificial organs or for other biomedical applications. Another embodiment ofthe invention is shown in Figure 20. In this embodiment, the foam composite 10 is formulated with a pharmaceutical agent of choice which yields a flow through device for administering pharmaceuticals. The hydrophilic foam 14 in this embodiment is produced by the emulsification of a hydrophilic prepolymer with a solution or dispersion ofthe pharmaceutical in water. This is then combined with reticulated foam 12. Fluid or blood is pumped into the apparatus, and the resulting fluid which comes out is fluid treated with the drug. This embodiment creates an advanced drug delivery system. Referring now to Figure 21, another embodiment ofthe invention is an adsorption cell for the removal of low concentration chemicals for bioremediation. Polyurethanes are known to adsorb organic molecules. (As described in Enkiri, F.; Hulen, C; and Legault-Demare, J. Appl. Microbiol. Biotechnol. 1995 vol. 44, no. 3-4, pp. 539-545). This embodiment is created by producing a foam composite 10 by the method taught in the Example 1 described herein below. A process stream flowing through the cell is thus purified by the adsorption effect. Another embodiment ofthe invention is shown in Figure 22. In this embodiment, the foam composite 10 is formulated with a graft of activated charcoal or zeolite, and creates a device for the removal of drugs from blood. Referring now to Figure 23, another embodiment ofthe invention is a water deionizer. In this embodiment, the foam composite 10 is formulated with commercially available ion exchange is a resins or ligands attached to the surface of the foam composite 10 by grafting. The grafting is accomplished by procedures taught by Sreenivasan, K., Polymer Engineering and Science, v. 33 Oct. '93 p. 1366- 9. As water flows through the device, the water is de-ionized. Related embodiments ofthe invention are shown in Figures 24 and 25. In these embodiments, the invention is used as a humidifier. As shown in Figure 24, this device can be used as a humidifier for incubators. Figure 25 shows the embodiment as a humidifier for dry anesthetics. In both Figures 24 and 25, the foam composite 10, prepared as described in the example 1 herein is wetted with water. The water then evaporates as a gas stream passes over it. This embodiment is not confined to just air and anesthetics, but other substances known in the art that require humidification. As shown in Figure 26, another embodiment ofthe invention is a device for administer-ing anesthetic. In this embodiment, the foam composite 10 is formulated or post-treated with an anesthetic that evaporates in air flowing through the cell. Another embodiment ofthe invention is shown in Figure 27. In this embodiment, a device for removing water from a hydrocarbon is shown. The foam composite 10, due to the nature of its hydrophilic coating, will absorb water from the hydrocarbon stream passing through the cell. Referring now to Figure 28, another embodiment ofthe invention is shown in which the foam composite 10 is utilized as a respirator for use in low temperature applications. The hydrophilic foam 14 in this embodiment contains a phase change material that melts and freezes at just below the temperature ofthe human body (98.6°F / 37° C). The latent heat of fusion ofthe phase change material is used as a reservoir for storing the heat of exhaled air and subsequently releasing that heat to increase the temperature of inhaled air. Thus, in a respirator having two separate chambers and through which a person inhales through one chamber and exhales through the other, cold air enters the inhale side and is heated by the freezing phase change material. Air at body temperature is exhaled through the other chamber and melts the phase change material. This continues until the inhaled air freezes all ofthe phase change material. At that time, a valve is turned that reverses the inhale side to the exhale side and visa versa. The net effect is that the heat energy in the exhaled air is trapped and subsequently used to heat incoming air. The net effect is the breathed air temperature is tempered thus avoiding the body heat lost in very cold weather. Referring now to Figure 29, still another embodiment is shown in which the foam composite 10 is utilized as a flow-through analysis column. In such an embodiment, a column is made of one or more layers of foam 10, each providing an opportunity for analysis. For example, the first layer might be a foam 12 used for filtration. The second layer can be foam 12 coated with hydrophilic foam 14 to which an enzyme has been grafted (as described in Hu, Z.C.*; Korus, R.A.; Stormo, K.E., Appl . Microbiol. Biotehcnol. 1993 vol. 39, no. 3, pp. 289-295). The next layer might be a foam 12 coated with hydrophilic foam 14 to which an antigen that has been adsorbed or graphed. The device, thus constructed, is suitable for the analysis of one or more properties or constituents of a fluid passing through it. The following examples have been carried out to illustrate the invention and to describe the best mode ofthe invention at the present time. These examples further illustrate the various features ofthe invention, and are not intended in any way to limit the scope ofthe invention which is defined in the appended claims. EXAMPLES Equipment The equipment listed below has been used in the preparation ofthe foam composites ofthe invention. All materials used in these examples can be obtained from commercially available sources. 1. Meter/Mix A series of devices whose function was to store, temper (with respect to temperature), meter (through the use of positive displacement pumps) and mix together the hydrophilic polyurethane prepolymer and aqueous phases component are employed. The system included heat exchangers by which the temperature ofthe phases were controlled. Meter/Mix systems are readily commercially available for use with hydrophilic prepolymers from Edge-Sweets & Co., Grand Rapids, Michigan, USA. 2. Web A system by which a continuous roll of reticulated foam is supplied to the process at a constant rate of speed. This equipment is typically custom made to meet the requirements ofthe manufacturing facility with respect to output. 3. Dip Tank A tank or trough through which the reticulated foam web was drawn was employed in order to coat it with the prepolymer solution. 4. Nip Rollers/Doctor Blade A device that distributes the emulsion across the surface of and causes the emulsion to penetrate into the structure ofthe reticulated foam. 5. Air Blow A mechanism designed to blow air through the emulsion-coated reticulated foam in order to minimize the formation of windows across cells such that the reticulated structure ofthe foam composite is maintained. The use of this mechanism is optional. 6. Solvent Recovery A mechanism for the evaporation and recovery ofthe solvent. 7. Immersion Curing Bath Used in connection with a solvent or direct cast process, this equipment is a tank or trough through which the web was drawn to effect the curing ofthe foam composite by immersing it in water was employed. The residence time was sufficient to cure fully the foam composite ofthe invention. 8. Water Vapor Curing Chamber Alternatively, the web of prepolymer solution coated hydrophobic polyurethane scaffold was drawn through a vapor curing chamber wherein the water vapor was typically kept at elevated temperatures of up to 95 °F and a high relative humidity in excess of 95%>. The residence time ofthe web sufficient to complete curing ofthe foam composite. 9. Dryer A mechanism to evaporate the excess water from the foam composite ofthe invention was employed. Radio frequency or hot-air dryers are typically used and are commercially available. Example I This example illustrates the preparation of foam composites by coating hydrophobic polyurethane scaffolds with an emulsion of polyurethane prepolymer. Three (3) pieces of conventional hydrophobic reticulated foam having a pore size of 20 ppi such as Crest Foam, Grade S-20 were cut to 30.5 cm by 30.5 cm by 0.8 cm. Each weighed 16 grams. An emulsion was made using a mechanical mixer of a 0.1%) Pluronic L62 (BASF Corp.) in water at ambient temperature and Rynel® (Grade B-l) hydrophilic polyurethane prepolymer (Rynel Ltd., Inc.). The emulsion was prepared by using 1 part prepolymer to 1.5 parts 0.1 % Pluronic L62 solution. Three different amounts ofthe emulsion were immediately poured onto the three pieces of foam as shown in Table 5. In each case the entire emulsion was uniformly distributed onto the reticulated foam using a rolling pin. After curing, the entire amount ofthe prepolymer in the emulsion was found to form the coating of hydrophilic foam in the foam composite. The foam was allowed to cure in water for 30 minutes at ambient temperature and then dried at 105°C. The resulting foam composites were then dried and re- weighed and then placed in water to measure how much water they would absorb. The following table presents the results of those tests: Table 5: Physical Properties of Uncoated Versus Emulsion-Coated Reticulated Foams Foam Property Reticulated Emulsion Emulsion Emulsion 1 2 3 Size Length (cm) 30.5 30.5 30.5 30.5 Width (cm) 30.5 30.5 30.5 30.5 Thickness (cm) 0.8 0.8 * 0.8 0.8 Weight (grams) 16.00 35.0 45.0 * 63.0 * Density (grams/cc) 0.021 0.047 0.06 0.085 Coating Thickness (grams) - 19.0 29.0 47.0 Water Saturated Weight (grams) 18.0 73.0 110.0 184.0 Grams Water Absorbed per Gram of Foam 0.125 1.09 1.44 1.92 * Total Weight of Foam Composite In this example, the amount of water that each foam composite was able to absorb was used to evaluate the effectiveness ofthe process. The above results indicate that the absorption ofthe foam composite increased with increasing thickness ofthe hydrophilic polyurethane coating. Example 2 This example illustrates the preparation of foam composites by coating reticulated hydrophobic polyurethane scaffolds with a solution of polyurethane prepolymer. A solution ofthe prepolymer was dissolved in a solvent such as acetone. The weight ofthe coating was controlled by varying the viscosity ofthe solution. Three solutions of 10%, 20% and 30% of Rynel® prepolymer in acetone were prepared at ambient temperature. Samples of Crest® reticulated polyurethane foam as described in Example 1 above were dipped into the Rynel® prepolymer solutions. They were immediately removed and allowed to drain. They were then hung in a fume hood and the acetone was allowed to evaporate as evidenced by an absence of the acetone odor. The foam samples were then immersed in water at 25°C for about 10 minutes to cure. The samples were then dried and reweighed. They were subsequently placed in water at 25°C for 1 hour, patted dry to remove surface water and then reweighed to determine the absorbed amount of water. Table 6 below summarizes the results of these tests. Table 6: Physical Properties of Uncoated Versus Reticulated Foams Coated with Prepolymer Solution Foam Property Reticulated 10% 20% 30% Polymer Polymer Polymer Size Length (cm) 30.5 30.5 30.5 30.5 Width (cm) 30.5 30.5 30.5 30.5 Thickness (cm) 0.8 0.8 0.8 0.8 Weight (grams) 16 19 * 23 * 27 * Density (grms/cm3) 0.021 0.026 0.031 0.036 Coating Thickness (grams) - 3.0 7.0 11.0 Water Saturated Weight - 18.0 26.0 43.0 (grams) Grams Water Absorbed per - 0.125 0.37 0.87 Gram of Foam * Total Weight of Foam Composite The results summarized above illustrate that the weight of hydrophilic foam coated on the scaffold increased by increasing the thickness ofthe hydrophilic polyurethane component. Example 3 This example illustrates the preparation of foam composites by coating hydrophobic reticulated polyurethane scaffolds with undiluted polyurethane prepolymers having different viscosities. Prepolymers at three different temperatures were applied directly to Crest Foam® hydrophobic scaffolds as described below. The viscosity of commercial prepolymers was about 15,000 cps. at 25°C. By heating the prepolymers their viscosity was lowered significantly. Three different foam composites having three different levels of open cell hydrophilic polyurethane coating were obtained. Three (3) samples ofthe Rynel® prepolymer as described above were heated to 30°, 35° and 40°C. Three (3) samples of Crest® foam as described in Example 1 were each dipped into a prepolymer dip tank and then squeezed between rubber rollers. The samples were immediately immersed in water at 25°C to cure for about 30 minutes. The samples were dried and re-weighed. They were soaked in water, patted dry and then weighed to determine the amount of water they could absorb. Table 7 below summarizes the results found in this example. Table 7 Direct Coating of a Reticulated Foam Foam Property Reticulated Polymer Polymer Polymer @40°C @35°C @30°C Size Length (cm) 30.5 30.5 30.5 30.5 Width (cm) 30.5 30.5 30.5 30.5 Thickness (cm) 0.8 0.8 0.8 0.8 Weight (grams) 16 25 * 35 * 42* Density (grms/cm3) 0.021 0.034 0.047 0.056 Coating Thickness (grams) - 9.0 19.0 26.0 Water Saturated Weight 18.0 43.0 75.0 99.0 (grams) Grams Water Absorbed per 0.13 0.72 1.14 1.36 Gram of Foam * Total Weight of Foam Composite The above results indicate that the foam composites ofthe invention having a thicker coating of open cell hydrophilic polyurethane deposited as undiluted prepolymer absorbed increasing amounts of water. Example 4 The relationship ofthe pore size of foam composites, the flow rate of water through columns packed with the foam composite ofthe invention and the ratio of hydrophobic foam cast. The above results indicate that the foam composites ofthe invention having a thicker coating of open cell hydrophilic polyurethane deposited as undiluted prepolymer absorbed increasing amounts of water. Example 4 The relationship ofthe pore size of foam composites, the flow rate of water through columns packed with the foam composite ofthe invention and the ratio of hydrophobic foam cast on a hydrophobic reticulated foam scaffold is examined. The effect of these independent variables on the pressure drop across three (3) packed columns of foam composites was studied. The equipment used included as follows: (a) 0-25 oz/in 2 pressure gauge; (b) 1.5 Schedule 40 PVC pipe, 7 inches long; (c) Stop watch; (d) Calibrated vessel to measure volume ofthe flow of water; (e) Narious fittings to build the apparatus shown in Figure 30. Three (3) columns as shown in Figure 30 were packed with foam composites ofthe invention having a pore distribution of 10 ppi, 20 ppi and 45 ppi, respectively. The samples were made using the water emulsion method described in Example 1 using 0.1% Pluronic L62 (BASF Corp.) in water and Rynel® prepolymer to form an emulsion as described in Example 1, and Crest® Foam, T-10, T-20 and T-45 for the reticulated foam. Care was taken not to over or under pack the column by die cutting circles of 1.56 inches in diameter and stacking them into the column to a thickness of 7 inches. The end caps were screwed on and the water passed through it. The flow of water was measured by determining the time to fill a calibrated vessel.. The pressure was recorded at each flow rate. The flow and pressure ofthe system were measured at 39°F and are reported in Table 8. Table 8 Flow Rate (gal/min) lOppi 20ppi 45ppi 1.1 1 1 1 1.7 3.5 1.8 4.9 2.1 2 2 2.2 1.4 2.3 10.5 2.4 2.8 2.7 6 2.9 18 3.0 9.5 3.8 10 3.9 20 4.0 10 18 4.6 18 28 5.0 18 Figure 31 is a plot ofthe data from Table 8. The experiments studied the relationship of flow and pressure drop on several reticulated foams. Crest® T-10, T- 20 and T-45 having pores of 10 ppi, 20 ppi and 45 ppi, respectively were used for the hydrophobic polyurethane scaffold. As is readily apparent from Figure 30, the smaller the cell size the higher the pressure drop at any given flow rate. Example 5 The experiment of Example 4 was repeated with foam composites according to the invention made with samples of Crest® T-10 foam and various amounts of hydrophilic foam. All samples were made using the water emulsion process of Example 1, except that different amounts of prepolymer emulsion as prepared in Example 1 were utilized to produce composites having different weights of open cell hydrophilic polyurethane coating. In Table 9 the amount of hydrophilic foam is expressed as H/R which is the ratio ofthe weight ofthe open cell hydrophilic polyurethane foam to the weight ofthe hydrophobic reticulate foam. Table 9 Flow Rate (gal/min) 0 HR 1.1 H/R 2.63 H/R 3.71 H/R 4.2 HR 1 1 1 1 1 1 1.4 5.2 9 1.7 1.5 1.7 9 1.8 0.5 18 2.1 2 2.2 15.5 2.4 2, 2.7 10 3.0 17 3.8 10 4.0 10 13 4.6 15 5.0 17 20 The plot ofthe data in Table 9 is shown in Figure 32. As expected, as the amount of hydrophilic coating increases the pressure to pump water through the resulting foam composite increases at any given flow rate. Example 6 A block of foam composite was made from a piece of Crest T-45 reticulated hydrophobic foam having a porosity of 45 ppi by the solvent method of Example 2. A solution of 35%> Rynel® prepolymer in acetone at ambient temperature was employed. The dimensions ofthe reticulated hydrophobic foam block was 6 inches by 6 inch by 2 inches thick. Following processing, the block was skived into 0.25 inch sheets each sheet being a square of 6 inch by 6 inch by 0.25 inches in thickness. Each sheet of foam composite was weighed and the amount of hydrophilic coating was determined by the difference. Table 10 below illustrates the data obtained in this experiment. Table 10 Sheet No. Wt. Wt. Foam Wt. Grams Reticulate Composite Hydrophilic Hydrophilic/grams (grams) (grams) (grams) Reticulate Hydrophobic 1 6.0 21.1 15.1 2.52 2 6.0 21.1 15.1 2.52 3 6.0 21.4 15.4 2.57 4 6.0 21.3 15.3 2.55 5 6.0 21.1 15.1 2.52 6 6.0 21.6 15.6 2.60 7 6.0 21.1 15.1 2.52 8 6.0 21.4 15.4 2.57 types of polyurethane The above data indicates a high level of uniformity in the penetration ofthe hydrophilic polyurethane coating into the hydrophobic polyurethane scaffold. Examples 7-15 These examples illustrate the relationship between foam composites prepared by the solvent and direct cast processes, the weight ofthe hydrophilic polyurethane coating and viscosity. The foam composites of examples 7 to 10 were prepared by the solvent method according to the procedure described in Example 2 using the same prepolymer and other processing conditions. Samples of Crest® reticulated hydrophobic polyurethane foam having a pore size of 20 ppi were coated with different concentrations of prepolymer solution in acetone at 68°C. The weight ofthe reticulated polyurethane foam, open cell hydropliilic polyurethane and the ratio of one to the other is summarized in Table 11 and have been plotted in Figure 33. Table 11 Solvent and Direct Cast Process Examples Wt. wt. %Prepolymer Temperature Wt. Wt. Wt. Foam Hydrophilic/ Prepolymer Acetone (grams) (°F) Reticulate Coating Composite Reticulate (grams) (grams) (grams) (grams) (grams) 7 100 30 77% 68 9.0 29.0 38.0 3.2 8 100 50 67% 68 9.0 25.0 34.0 2.8 9 100 70 59% 68 9.0 20.0 29.0 2.2 10 56 216 21% 68 9.0 6.0 15.0 0.7 11 100 0 100% 100 9.0 90.0 99.0 9.0 12 100 0 100% 118 9.0 60.0 69.0 6.7 13 100 0 100% 145 9.0 58.5 67.5 5.5 14 100 0 100% 178 9.0 48.6 • 57.6 4.4 15 100 0 100% 200 9.0 40.0 49.0 4.0 It is readily apparent from Figure 33 that the higher the concentration of prepolymer in the acetone solvent, the higher the weight ofthe hydrophilic polyurethane coating deposited onto the polyurethane scaffold. The foam composites of Examples 11-15 were prepared by the direct cast method according to the procedure described in Example 3. Samples of Crest® reticulated hydrophobic polyurethane foam having a pore size of 20 ppi were coated with 100% Rynel® prepolymer at temperatures graphed in Figure 34 and otherwise processed as described in Example 3. The characteristics ofthe foam composites of examples 11-15 are also summarized in Table 11. Figure 34 illustrates the effect of temperature on the foam composites of examples 11-15. It is readily apparent that as the temperature ofthe prepolymer in liquid phase is increased, the weight ofthe hydrophilic polyurethane coating deposited decreases. Example 16 Artificial lobster bait was prepared as follows. Attractants were prepared from (1) herring brine taken from the bottom of a barrel of salted herring, (2) a concentrated soup stock of crab, (3) a concentrated soup stock of clams (4) ground crabs and (5) ground herring. The crabs (4) and herring (5) were ground in a Waring Laboratory Blender. Lobster baits were prepared form 59 gram sheets of reticulated foam (T20 from Crest Foam of New Jersey). In each experiment 100 grams of an emulsion comprised of equal weight portions of hydropliilic polyurethane (Suprasec 1002 from Huntsman Polyurethane, Brussels, Belgium) and the attractant were applied to the reticulate. The emulsion was massaged into the reticulated foam. The baits thus prepared were allowed to cure and then cut into individual bait samples 6"x6" x 0.25". The baits were delivered to fisherman who used them as lobster bait in traps placed in the Gulf of Maine for a minimum of 3 days. Whole herring, the regular bait, was used as the control. The comparative results are described in Figure 38 which shows that the ground herring impregnated in the composite ofthe invention was nearly 50%) more effective than standard herring bait. Figure 35 depicts an apparatus which operates continuously to remove pollutants from a waste stream. The belt containing the composite ofthe invention moves continuously through the tank which contains a solution containing a pollutant. Biomass builds up on the belt in accordance with normal biological procedures. The belt is indexed outside the tank where it is squeezed or hydro-blasted or subjected to a strong stream of air to dislodge the biomass. The belt is then indexed or continuously advanced back into the tank where it will again develop biomass. The apparatus of Figure 35 may also be used as a cold, solvent recovery device. The belt is used to extract a valuable, water-soluble component from a solvent. The valuable component may be removed from the belt by vaporizing it. Since the composites ofthe invention are biocompatible and can be impregnated with nutrients, they can be used to collect biological samples. Thus the composites can be placed in a pond or other body of water where they will become colonized by resident microorganisms. Alternatively, they can be inoculated with specific organisms (an alga, for instance) or a variety of microorganisms that feed on that pollutant. A microscopic analysis ofthe composite will indicate the presence or absence of a specific pollutant. Alternatively, a nutrient specific to a bacterial specie can be included in the composite formulation so that only that microorganism, (e.g. coliforms or cryptosporidia) will propagate. Alternatively a sampling system can be provided that is made up of a long ribbon of composite that is coiled up and placed in a mesh cylinder. When placed in or dragged through a body of water, the composite will become colonized with microorganisms. The composite is then removed from the mesh cylinder, unrolled and passed under an optical scanner to detect colonies of microorganisms. It can be subjected to biological stains to make the organisms more visible. The composite can also be incubated to increase the resident populations. Figure 36 depicts a biofilter cartridge for use in methods to remove odor- producing components of air exhausted from a manufacturing plant or a water waste treatment facility. The cartridge is comprised of composite encased in a rigid or semirigid mesh material. The composite will become colonized with microorganisms. When placed in a stream of air that contains a pollutant, microorganisms will develop that will feed on that pollutant. In a specific example, a biofilter cartridge can be made composed of composite coiled in a polyethylene or polypropylene mesh cylinder. The composite containing cylinder is placed in an apparatus through which air, from a municipal water- waste treatment plant, is passed. The exhausted air contains hydrogen sulfide and a variety of microorganisms. After a time, thiobacillus bacteria will proliferate on the composite. When a colony of sufficient size develops, the microorganisms will consume the hydrogen sulfide in the air stream, thus reducing its concentration and eliminating odor. The initiation time, the time it takes for the biofilter to develop a large enough colony of microorganisms to reduce the pollutant to an acceptable level, can be effectively reduced by placing the cartridge in an environment where the population ofthe important microorganism is high. For example, if the cartridge is placed in a waste treatment pond for several hours, it will become colonized with a wide variety of organisms, some of which will be effective at reducing the target pollutant. Some pollutants, specifically synthetic chemicals, may not have organisms that readily metabolize them. In such cases the initiation time can be prohibitively long. A recent study on MtBE revealed an initiation time of one year. In such cases a composite can be formulated with an organism that is specifically developed, e.g. by generic engineering, or by harvesting an organism from a successful system. In a variation, biofilters can be placed into trickling filters in which water is continuously fed to the top ofthe cartridge and flows through it. A cartridge containing thiobacillus will produce sulfur dioxide. The sulfur dioxide dissolves in the water yielding sulfiirous acid. If the acidic water is allowed to contact limestone, the reaction produces carbon dioxide. Figure 37 discloses an apparatus which uses the carbon dioxide to feed the thiobacillus, which in turn uses it to produce biomass. Composite can also be saturated with water and frozen to serve as a cold pack for wrapping injuries or for shipping of temperature sensitive products. Composites can be formulated to contain minerals or other materials or to contain waxes or other components that melt and freeze at specific temperatures, thus maintaining a specific temperature as the substance releases or absorbs heat at that temperature. Thus, while there have been described what are presently believed to be preferred embodiments ofthe present invention, those skilled in the art will realize that other and further modifications and changes can be made without departing from the true spirit ofthe invention, and it is intended to include all such changes and modifications as come within the scope ofthe invention. Further, the embodiments of the invention in which exclusive rights are claimed are defined as follows:

Claims: What is claimed is: 1. A foam composite comprising: a scaffold of an open cell hydrophobic polyurethane foam, said scaffold having a plurality of surfaces defining a plurality of pores; and a coating of a substantially open cell hydrophilic polyurethane foam disposed upon said plurality of surfaces of said hydrophobic polyurethane foam; wherein said foam composite exhibits structural characteristics of said hydrophobic polyurethane foam and absorbency characteristics of said open cell hydrophilic polyurethane foam. 2. The foam composite of claim 1, wherein said coating is from about 1% to about 90%) by weight of said foam composite. 3. The foam composite of claim 1 , wherein said coating is the in situ reaction product of a hydrophilic polyurethane prepolymer emulsion having a prepolymer phase and an aqueous phase. 4. The foam composite of claim 3 , wherein the ratio of said aqueous phase to said prepolymer phase is from about 0.8:1 to about 2.2:1. 5. The foam composite of claim 1 , wherein said coating is prepared by the in situ deposition of a hydrophilic polyurethane prepolymer from a solution of said polymer in a nonreactive solvent. 6. The foam composite of claim 5, wherein said hydrophilic polyurethane prepolymer solution is from about 1% by weight to about 60% by weight prepolymer. 7. The foam composite of claim 5, wherein said nonreactive solvent is selected from the group comprising acetone, toluene, xylene, benzene or mixtures thereof. 8. The foam composite of claim 1 , wherein said open cell hydrophilic polyurethane foam comprises the polymerization products of an isocyanate-capped polyether prepolymer having an isocyanate functionality from about 5%o by weight to about 15%) by weight of said prepolymer. 9. The foam composite of claim 8, wherein said isocyanate-capped polyether prepolymer has an isocyanate functionality from about 6% by weight to about 9% by weight of said prepolymer. 10. The foam composite ofclaim 1, wherein said foam composite has a pore size distribution from about 4 pores per linear inch to about 100 pores per linear inch. 11. The foam composite of claim 1 , wherein said foam composite has a void volume from about 20%) to about 98%. 12. The foam composite of claim 1 , wherein said foam composite has a surface area from about 100 ft per cube foot to about 2,000 ft per cubic foot of foam composite. 13. The foam composite of claim 12, wherein said foam composite has a surface area of from about 300 ft 2 per cubic foot to about 2000 ft 2 per cubic foot of foam composite and a pore size distribution in the range from about 10 pore/linear inch to about 95 pore/linear inch. 14. The foam composite ofclaim 1, wherein said foam composite has a rate of absorbency for water at 20°C from about 0.1 seconds to about 60 seconds. 15. The foam composite of claim 1, wherein said foam composite has a pressure drop of about 0.14 inches of water to about 2.7 inches water for 575 ft/minute of dry air through a foam composite having a surface area of 1 ft 2 , a thickness of 1 inch and a pore size in the range from about 10 pore/linear inch to about 90 pore/linear inch. 16. The foam composite of claim 1, wherein said foam composite has a pressure drop rate of from about 0.1 psi to about 2 psi for about 2 gallons of water at 39°F through about 2 in 2 of foam composite having a thickness of 7 inches for foam composites having a weight ratio of hydrophilic polyurethane foam to hydrophobic polyurethane foam in the range of from about 0.1 to 1 to about 4.0 to 1 over a pore size distribution range from about 10 pore/linear inch to about 45 pore/linear inch. 17. The foam composite of claim 16, wherein said foam composite has a pore size distribution in the range 10 pores per linear inch to 100 pores per linear inch. 18. The foam composite of claim 1, wherein said coating of hydrophilic polyurethane foam has a coating weight from about 0.5 grams hydrophilic foam/gram hydrophobic foam to about 10 grams hydrophilic foam/gram hydrophobic foam. 19. The foam composite of claim 1 , wherein said foam composite has a tensile strength from about 10 psi to 35 psi over a pore size distribution range from about 10 ppi to about 90 ppi. 20. The foam composite ofclaim 1, wherein said foam composite has an elongation characteristic from about 150% to about 260%) by weight over a pore size distribution range from about 10 ppi to about 100 ppi. 21. The foam composite of claim 1 , wherein said hydrophilic polyurethane coating further comprises an additive. 22. The foam composite of claim 21 , wherein said additive is a non- bioactive ingredient. 23. The foam composite of claim 22, wherein said non-bioactive ingredient comprises a hydrogel, a filler, an activated charcoal, a zeolite, an ion exchange resin, a phase change material or mixtures thereof. 24. The foam composite of claim 23, wherein said hydrogel is a polysaccharide hydrogel or an acrylic hydrogel. 25. The foam composite of claim 24, wherein said polysaccharide hydrogel is an alginate, a carrageenan, an agar, an agarose, a curdlan, a pullulan, a gellan or mixtures thereof. 26. The foam composite of claim 24, wherein said hydrogel is in an amount from about 0.1%) to about 90%) by weight of said hydrophilic polyurethane coating. 27. The foam composite of claim 24, wherein said acrylic hydrogel is a polyacrylamide, a poly (ethyl methacrylate), a poly (glycol methacrylate), a poly (hyroxy methyl acrytate), a poly (sodium acrylate) or mixtures thereof. 28. The foam composite of claim 22 wherein said bioaffecting agent comprises a pharmaceutical, a fragrance, a soap, a herbicide, a pesticide, a yeast, a bacterium, a algae, an enzyme, a plant, an animal cell, a human cell, or mixtures thereof. 29. The foam composite of claim 1, further comprising an non-bioactive ingredient or a bioaffecting agent. 30. The foam composite of claim 29, wherein said non-bioactive ingredient or said bioaffecting agent is immobilized within said foam composite. 31. The foam composite of claim 30, wherein said non-bioactive ingredient comprises a hydrogel, a filler, an activated charcoal, a zeolite, an ion exchange resin, a phase change material or mixtures thereof. 32. The foam composite of claim 30, wherein said bioaffecting agent comprises a pharmaceutical, a fragrance, a soap, a yeast, a herbicide, a pesticide, an enzyme, a bacterium, a algae, a plant, an animal cell, a human cell or mixtures thereof. 33. The foam composite of claim 29, wherein said bioaffecting agent is grafted onto said non-bioactive ingredient. 34. The foam composite of claim 33, wherein said non-bioactive ingredient is a hydrogel. 35. A process of making a foam composite which comprises: (a) preparing an emulsion of a hydrophilic polyurethane prepolymer which upon curing forms a substantially open cell hydrophilic polyurethane polymer foam; (b) contacting an open cell hydrophobic polyurethane foam having a plurality of surfaces defining a plurality of pores with said hydrophilic polyurethane prepolymer emulsion; (c) curing said hydrophilic polyurethane prepolymer emulsion while in contact with said hydrophobic polyurethane for a period of time sufficient to form a coating of said substantially open cell hydrophilic polyurethane polymer foam on hydrophobic polyurethane foam without closing the pores of said hydrophobic polyurethane foam. 36. The process of claim 35, wherein said contacting is accomplished by dipping said reticulated hydrophobic foam into said polyurethane prepolymer emulsion. 37. The process of claim 35, wherein said contacting is a mechanical extrusion of said polyurethane prepolymer emulsion onto the surface of said reticulated hydrophobic polyurethane substantially uniformly and allowing said emulsion to permeate into said reticulated hydrophobic polyurethane. 38. The process ofclaim 37, wherein said mechanical extrusion is performed with nip rollers or doctor blades. 39. The process of claim 35, further comprising blowing air through said emulsion coated reticulated polyurethane foam prior to said curing step. 40. The process of claim 35, wherein said prepolymer emulsion further comprises an additive selected from the group consisting of non-bioactive ingredients or bioaffecting agents. 41. The process ofclaim 40, wherein said non-bioactive ingredient comprises a hydrogel, a filler, an activated charcoal, a zeolite, an ion exchange resin, a phase change material or mixtures thereof. 42. The process of claim 40, wherein said bioaffecting agent comprises a pharmaceutical, a fragrance, a soap, a herbicide, a pesticide, a yeast, a bacterium, an algae, an enzyme, a plant, an animal cell, a human cell or mixtures thereof. 43. A process of making a foam composite which comprises : (a) preparing a solution of a hydrophilic polyurethane prepolymer which upon curing forms a substantially open cell hydrophilic polyurethane polymer foam and a solvent therefor; (b) contacting an open cell hydrophobic polyurethane foam having a plurality of surfaces defining a plurality of pores with said polyurethane prepolymer solution; (c) recovering said solvent from said polyurethane prepolymer solution in step (b) and leaving a coating of said hydrophilic polyurethane prepolymer on said open cell hydrophobic polyurethane foam; and (d) curing said polyurethane prepolymer for a period of time sufficient to form a coating of said substantially open cell hydrophilic polyurethane polymer foam on said hydrophobic polyurethane foam without closing the pores of said hydrophobic polyurethane foam. 44. The process of claim 43, wherein said solution of step (a) contains from about 20 wt% to about 80 wt% prepolymer in a solvent which is non-reactive with said prepolymer while steps (a) through (c) are performed. 45. The process ofclaim 44, wherein said non-reactive solvent is acetone, toluene, benzene, xylene or mixtures thereof. 46. The process of claim 45, wherein said curing step is immersion curing in a water bath at a temperature in the range of from about 4°C to about 50°C, or water vapor curing in a gas stream at a temperature in the range of from about 30°C to about 100°C and having a relative humidity of about 85% to about 100%. 47. The process of claim 43, further comprising removing excess solvent from said prepolymer solution contacted hydrophobic polyurethane foam after step. 48. The process of claim 43, further comprising blowing air through said prepolymer solution coated hydrophobic polyurethane foam prior to step (c). 49. A process of making a foam composite which comprises: (a) preparing a liquid phase of a hydrophilic polyurethane prepolymer which upon curing forms a substantially open cell hydrophilic polyurethane foam at from about 25°C to about 40°C; (b) contacting an open cell hydrophobic polyurethane foam having a plurality of surfaces defining a plurality of pores with said liquid phase of a hydrophilic polyurethane prepolymer; (c) curing said polyurethane prepolymer for a period of time sufficient to form a coating of said substantially open cell hydrophilic polyurethane polymer foam on said hydrophobic polyurethane foam without closing the pores of said hydrophobic polyurethane foam. 50. A process of making a foam composite which comprises: (a) preparing a scaffold of an open cell hydrophobic polyurethane foam, said scaffold having a plurality of surfaces defining a plurality of pores; (b) preparing a hydrophilic polyurethane prepolymer emulsion which upon curing forms a substantially open cell hydrophilic polyurethane foam; (c) preparing a hydrogel emulsion; (d) mixing said prepolymer emulsion with said hydrogel emulsion to obtain a composite emulsion; (e) contacting said scaffold of an open cell hydrophobic polyurethane foam with said composite emulsion; and (f) curing said composite emulsion while in contact with said reticulated hydrophobic polyurethane to form a coating of said substantially open cell hydrophilic polyurethane polymer foam on said hydrophobic polyurethane foam scaffold without closing the pores of said hydrophobic polyurethane foam. 51. The process of claim 50, wherein said composite emulsion contains from about 1% to about 70% by weight hydrogel. 52. A foam composite as recited in claim 1 wherein said open cell hydrophobic polyurethane foam scaffold is reticulated. 53. A foam composite as recited in claim 52 wherein said foam scaffold is highly reticulated.

Inventors: THOMSON TIMOTHY, THOMSON, TIMOTHY
Applicants: HYDROPHILIX LLC
Application year: 2001
Main classification: B32B3
IPC codes: B32B5, C08J9