POLYMERIZABLE DISPERSANT

Abstract: A polymerizable monophosphate ester dispersant, a highly-filled nonaqueous suspension containing the polymerizable monophosphate ester dispersant, and a method for forming cured articles by copolymerization of the resin matrix and dispersant in the suspension. Inclusion of the dispersant in a suspension of resin and solid particulate material enables an increase in the solid loading, which results in reduced shrinkage, a lower coefficient of thermal expansion and generally improved physical properties in an article cured therefrom.

Description: POLYMERIZABLE DISPERSANT Cross Reference to Related Application This application is a continuation-in-part of U.S. Patent Application Serial No. 09/093,778 filed June 9, 1998, and entitled DENTAL RESTORATIVE COMPOSITE, which is incorporated by reference herein in its entirety, and a continuation-in-part of U.S. Patent Application Serial No. 09/306,628 filed May 6, 1999, and entitled DENTAL RESTORATIVE COMPOSITE, which is incorporated by reference herein in its entirety. Field of the Invention This invention relates to polymerizable dispersants, and more specifically, to phosphate-based ester dispersants that are effective in nonaqueous filled suspensions due to polymerizable groups that strengthen the composite after polymerization. Background of the Invention High mechanical forces are required to incorporate solids into liquid media. To reduce the required dispersing forces, it is known to use dispersants, which facilitate the incorporation. Dispersants have been used in paints, molding compositions, coatings, plastic mixtures, printing inks, synthetic resin systems, and the like. The solids to be incorporated into the liquid media include, for example, pigments, fillers and fibers. U.S. Patent No. 5,151,218 discloses phosphoric acid ester dispersants of various structures. Recognized therein is the limited usefulness of certain structures as a dispersant in a broad number of applications. If a compound is not sufficiently compatible with the system, inadequate dispersion occurs due to insufficient interaction with the surrounding medium, and potentially precipitation phenomena with associated dulling, spotting and increased viscosity can occur. There is thus a need to develop dispersants that are broadly useful for wide-ranging applications. In some applications, it is desirable to maximize the amount of solid in the suspension. For example, in a synthetic resin system, it may be desirable to limit the amount of the polymerizable resin and maximize the amount of filler, fiber or pigment material. The main factor limiting the volume fraction (load) of the solid in highly filled suspensions is particle-particle interactions. Dispersants, through their ability to reduce interactions between particles, can improve the flow (reduce the viscosity) of the suspension, thereby allowing a higher load. Dispersants in non-aqueous systems reduce particle interactions by a steric stabilization mechanism. A layer of the dispersant is adsorbed on the surface of the particles keeping them apart from one another, reducing the viscosity. The dispersant structure must contain a chain that allows for steric stabilization in the resin and it also must be strongly adsorbed on the particle surface. There is thus a further need to provide a dispersant that will be effective with a non-aqueous, highly filled suspension containing polymerizable resin. Summary of the Invention The present invention provides a polymerizable monophosphate ester dispersant, a nonaqueous, highly-filled suspension containing the polymerizable monophosphate ester dispersant, and a method for forming cured articles by copolymerization of the resin matrix and dispersant in the suspension. The dispersant of the present invention comprises a phosphate group, polyester group and polymerizable end group. The dispersant is ^functional in nature. An exemplary dispersant of the present invention is a monophosphate ester according to the formula wherein R is a (meth)acrylate group radical or vinyl radical. Further exemplary embodiments include dispersants in which R is one of the following (meth)acrylate group radicals: oxyethyl methacryloyl-, oxyethyl acryloyl-, polyoxypropyl methacryloyl-, glyceryl dimethacryloyl-, and dipentaerythritol pentaacryloyl-. The inclusion of the dispersant, generally in an amount up to about 5 wt.%, in a suspension of resin and filler enables an increase in the filler loading, which results in reduced shrinkage, a lower coefficient of thermal expansion and generally improved physical properties in an article cured therefrom. These and other objects and advantages of the present invention shall become more apparent from the description of the preferred embodiments and the examples. Detailed Description The present invention provides a class of phosphate based dispersants that are effective with nonaqueous, highly-filled suspensions. The dispersant is a trifunctional molecule that binds to the surface of a solid particulate material, reduces particle interactions by steric stabilization, and is copolymerizable with a resin matrix. Bonding with the surface of the solid, inorganic particulate material is accomplished with an anchoring phosphate group or ion. The phosphate ion has an affinity for the inorganic material. A spacer group, for example a polyester group, penetrates into the resin to promote steric stabilization. A polymerizable end group, either a monomer or copolymer, for example vinyl, methacrylate or acrylate, enables the dispersant to be copolymerized with the resin matrix. The presence of these groups ϊn the dispersants of the present invention result in excellent compatibility with a broad range of resin systems, particularly (meth)acrylate-based (meaning methacrylate or acrylate) resin systems. Inclusion of the dispersants of the present invention into filled resin formulations will result in cured articles having lower shrinkage upon polymerization, lower coefficient of thermal expansion, and generally improved properties as compared to a formulation without the dispersant. In addition, copolymerization of the dispersant with the resin matrix provides improved bonding between solid particles and the resin matrix. In one aspect of the present invention, inclusion of a novel dispersant in (meth)acrylate-based resin dental composite formulations results in increased filler loading and decreased viscosity, which after curing of the suspension provides a dental restorative with reduced shrinkage, a lower coefficient of thermal expansion and generally improved physical properties. The dispersants of the present invention preferably comprise about 5 wt.% or less of the highly-filled suspensions, such as a dental composite paste. To obtain good uniformity of distribution of the dispersant in the final suspension, the dispersant is first mixed with the resin, followed by the slow addition of the solid particulate material, such as the inorganic glass fillers used in dental composites. An exemplary dispersant of the present invention is a monophosphate ester of the formula where R is a (meth)acrylate group radical or a vinyl radical. The presence of a carboxylic acid ester group of the dispersant results in excellent compatibility with (meth)acrylate-based resin systems. In exemplary embodiments, the dispersants of the present invention are monophosphate esters according to the above formula where R is one of the following (meth)acrylate group radicals: Compound 1 : R=oxyethyl methacryloyl- Compound 2: R=oxy ethyl acryloyl- Compound 3: R=polyoxypropyl methacryloyl- Compound 4: R=glyceryl dimethacryloyl- Compound 5: R=dipentaerythritol pentaacryloyl- Compound 6: R=polyoxyethyl methacryloyl- Each of Compounds 1-6 may be prepared in two steps. In the first step, the hydroxy functional methacrylate is condensed with caprolactone under ring- opening polymerization conditions in the presence of catalytic amounts of SnCl 2 to prepare a polyester. In the second step, the polyester is reacted with polyphosphoric acid (117.5% concentration) at 65 °C to produce the phosphoric acid (monophosphate) ester. By way of example, the reaction sequence is shown below for the preparation, of the hydroxyethyl methacrylate (HEMA) derivative Compound 1; it should be noted that substantially the same steps and conditions would be utilized to prepare any of Compounds 1-6: HEMA, M =130.14 Caprolactone, MW=114.14 Polycaprolactone-modified HEMA Compound 1 : Polycaprolactone-modified HEMA Phosphate The following examples are intended to further illustrate the present invention, and by no means should be interpreted to limit the scope of the present invention as claimed below. EXAMPLE 1 In a 4-neck reaction kettle containing an air flow tube, a thermocouple, a condenser and a stirrer, 26.0 parts by weight of hydroxyethyl methacrylate (HEMA) were combined with 114.1 parts by weight of caprolactone, 0.14 parts by weight of methyl ether of hydroquinone (MEHQ) and 0.007 parts by weight of stannous chloride under a flow of dry air. The mixture was thermostated at 120°C and stirring was continued for 18 hours. The disappearance of the caprolactone was monitored with HPLC (High Pressure Liquid Chromatography) using a reverse phase column with 70/30 acetonitrile/water as eluant. The resultant liquid polycaprolactone-modified HEMA was essentially colorless. In a three neck flask equipped with a stirrer and a condenser under a constant flow of dry air, 70.0 grams of the above product (polycaprolactone- modified HEMA) was combined with 8.45 grams of 117.5% phosphoric acid. The mixture was heated with stirring for 4 hours at 70 °C. A light yellow oil resulted. Titration with 0. IN NaOH showed that the monophosphate ester was formed. Various methacrylate derivatives prepared using the above procedures are listed in Table 1. Table 1. Polycaprolactone-Modified Methacrylate Monophosphates COMPOUND CHARACTERIZATION A)31P NMR Spectroscopy Phosphate esters are difficult to analyze with 3 IP nuclear magnetic resonance (NMR) spectroscopy because usually only broad and ill-defined resonances are observed. Conversion to their corresponding trimethylsilyl (TMS) esters greatly improves the spectra by increasing the chemical shift differences between phosphoric acid, mono, di, and triester species and increasing the sharpening of all resonances considerably. Samples of the reaction mixtures were initially dissolved in deuterochloroform followed by excess of N, O-bis (trimethylsilyl) trifluoroacetamide. Proton decoupled spectra were obtained at 162 MHz using 85% phosphoric acid as an external reference. The addition of trimethylsilyl groups causes an upfield shift of 9 ppm for each group added (see D.G. Anderson et al, "Hydrolytic Stability of Phosphate Ester Surfactants", Pesticide Formulations and Application Systems: 17th Volume, ASTM STP 1328 (G.R. Goss et al., eds., American Society for Testing and Materials 1997)). Using this technique, some of the phosphate esters were characterized as indicated in Table 2. Table 2. Phosphate Ester Distributions in Weight Percent Inspection of Table 2 shows that the monoester is the main product of the reaction and the amount of phosphoric acid remaining is under 5 wt.% and the amount of pyrophosphoric acid remaining is under 2 wt.%. B)1HNMR Spectroscopy 1H NMR spectra were obtained of Compound lc and 4c dispersants in deuterochloroform at 400 MHz using TMS as reference. The following were observed in each case at the appropriate integral ratios: Ethylenic protons at 5.6 and 6.1 ppm, methyl at 1.9 ppm (methyl group attached to vinyl carbon) and multiplets of methylenes within the following regions: 1.3 to 1.8 ppm (attached to methylene only), 2.25 to 2.4 ppm (attached to carbonyl group), and 4.0 to 4.5 ppm (attached to ester oxygen). C) Mass Spectroscopy Flow injection (electrospray) mass spectrometry was used to characterize Compound lb, lc and Id dispersants. The compounds were dissolved in 50:50 water: acetronitrile at a concentration of 2.5 mg/ml and each run by flow injection at 10 microliters/minute. Spectra were acquired on a Fisons VG Platform single quadrapole mass spectrometer (Bay Bioanalytical Laboratory, Richmond, CA). Negative ions were observed for these compounds using a capillary voltage of 3.22 kV and an extraction cone voltage of 42 kV. Source temperature was 80°C. The spectra of all 3 compounds show one series of ions for each separated by 114 mass units. The series with masses at 323.22, 437.31, 551.28, 665.37, 779.59, 893.80, and 1007.89 are the M-l ions of the molecules with 1 to 7 caprolactone units attached. Prostaglandin E ! (3-hydroxy- 2-(3-hydroxy-l-octenyl)-5-oxocyclopentaneheptanoic acid) was run as a mass calibration check before and after the samples. By way of example and not limitation, all of the above compounds may be used as dispersants in highly filled glass suspensions containing methacrylate resins for use as dental restorative composites. Nine test samples (test samples 1-9) were prepared according the following method. A methacrylate resin, as described in Table 3, was introduced into a planetary mixer and thermostated to 50°C. Table 3. Resin Composition A monophosphate ester with the structure described by the general formula above was then added to the resin so as to comprise 1.5 wt.% of the total resin/filler mixture with an 80 wt.% filler loading. The mixer was started for a few minutes to mix the resin phase and then the filler containing the physically admixed components listed in Table 4 was slowly added over a period of about 3 hours. Table 4. Filler Composition 1 average particle size 2 Degussa Corp., Ridgefield Park, N.J, Degussa Corp., Ridgefield Park, N.J. Mixing was continued for another hour and the resultant paste was deaerated under attenuated oxygen pressure. Table 5 details the physical properties of the test sample pastes (1-9) prepared along with the properties of control sample 1. All measurements were carried out using standard ISO methods except where indicated, and the standard deviations are provided in parentheses. Table 5. Physical Properties of Pastes Prepared with Various Dispersants 1 Average of 3 measurements on the surface of a cylindrical sample 10 mm in diameter and 4 mm in height. The samples were light cured for 40 seconds, and stored in water for 24 hours at 37°C prior to measurement. 2 Precision Penetrometer (GCA Corp., Chicago, JX) with a 1 mm needle was used with no additional weight (Og). The paste was placed in a mold 10 mm in diameter and 8 mm in height. Penetration was performed for 10 seconds. An average of 3 measurements is reported. 3 Same test as above, but using a flat head rather than a needle, to simulate the effect of the impact from dental instruments having a flat head on the composite. The properties shown in Table 5 demonstrate that there is a dramatic reduction of viscosity of the pastes where the monophosphate esters of Compound 1 are included. The penetrometer test is indicative of the viscosity of the paste, although not directly related. The addition of a dispersant of the present invention enabled the higher filler loading of 80 wt.% as compared to the maximum achievable loading of 77 wt.% in the control paste not containing a dispersant. Furthermore, the physical properties of the composites are not significantly reduced by the addition of the polycaprolactone-modified methacrylate monophosphates. As a further comparison, the most efficient dispersant listed above, Compound lc, was also formulated in pastes at different loads and amounts (test samples 10-12). The results of test samples 3 and 10-12 are listed in Table 6. Table 6. Compound lc at Various Loadings The results shown in Table 6 demonstrate that a low relative viscosity paste having acceptable physical properties may be prepared at 82 wt.% filler loading with only 2 wt.% dispersant based on a lc Compound. In contrast, pastes incorporating no dispersant cannot be made with a filler loading above 77 wt.%. See Control Sample 1 in Table 5. While (meth)acrylate polymerizable end groups have been discussed in detail above, it is to be understood that other polymerizable end groups may be used to achieve copolymerization of the dispersant with the resin matrix. An appropriate polymerizable end group may be selected for compatibility with a given resin system. The end group in a dispersant of the present invention may be unsaturated. Representative types of end groups are vinyl and (meth)acryloyl. Also, while dental filler particulate has been described in detail above, it is to be understood that other solid inorganic materials may be incorporated into resin systems with the aid of a dispersant of the present invention. Such solid inorganic materials may include, among others, pigments and fibers. While the present invention has been illustrated by the description of an embodiment thereof, and while the embodiment has been described in considerable detail, it is not intended to restrict or in any way limit the scope of the appended claims to such detail. Additional advantages and modifications will readily appear to those skilled in the art. For example, the dispersant of the present invention may be added to any resin/filler mixture, not just dental composite systems. Moreover, other polymerizable groups may be selected for copolymerization. The invention in its broader aspects is therefore not limited to the specific details, representative method and illustrative examples shown and described. Accordingly, departures may be made from such details without departing from the scope or spirit of applicant's general inventive concept. WHAT IS CLAIMED IS: 1. A dispersant for use in nonaqueous, filled suspensions, the dispersant comprising a phosphate group, a polyester group, and a polymerizable end group. 2. The dispersant of claim 1, wherein the dispersant is a trifunctional molecule in which the phosphate group is capable of binding to the surface of an inorganic solid material, the polyester group is capable of penetrating into a resin matrix, and the polymerizable end group is capable of attaching to a growing polycaprolactone chain. 3. The dispersant of claim 1, wherein the polymerizable end group is a vinyl group. 4. The dispersant of claim 1, wherein the polymerizable end group is a (meth)acrylate group. 5. The dispersant of claim 1, wherein the dispersant is a monophosphate ester of the formula and R is the polymerizable end group. 6. The dispersant of claim 1 , wherein R is a (meth)acrylate radical selected from: oxyethyl methacryloyl-, oxyethyl acryloyl-, polyoxypropyl methacryloyl-, glyceryl dimethacryloyl-, dipentaerythritol pentaacryloyl- and polyoxyethyl methacryloyl-. 7. The dispersant of claim 1, wherein the polymerizable end group is unsaturated.

Claims: 8. A polymerizable dispersant for use in nonaqueous, filled suspensions comprising: a monophosphate ester of the formula wherein R is a (meth)acrylate group radical or vinyl radical. 9. The dispersant of claim 8, wherein the monophosphate ester is a polycaprolactone-modified methacrylate monophosphate. 10. The dispersant of claim 8, wherein R is a radical selected from: oxyethyl methacryloyl-, oxyethyl acryloyl-, polyoxypropyl methacryloyl-, glyceryl dimethacryloyl-, dipentaerythritol pentaacryloyl- and polyoxyethyl methacryloyl-. 11. The dispersant of claim 8, wherein the monophosphate ester is polycaprolactone-modified hydroxyethyl methacrylate phosphate prepared from a mole ratio of caprolactone:hydroxyethyl methacrylate of 1 : 1. 12. The dispersant of claim 8, wherein the monophosphate ester is polycaprolactone-modified hydroxyethyl methacrylate phosphate prepared from a mole ratio of caprolactone :hydroxy ethyl methacrylate of 2:1. 13. The dispersant of claim 8, wherein the monophosphate ester is polycaprolactone-modified hydroxyethyl methacrylate phosphate prepared from a mole ratio of caprolactone:hydroxyethyl methacrylate of 5 : 1. 14. The dispersant of claim 8, wherein the monophosphate ester is polycaprolactone-modified hydroxyethyl methacrylate phosphate prepared from a mole ratio of caprolactone :hydroxy ethyl methacrylate of 7:1. 15. The dispersant of claim 8, wherein the monophosphate ester is polycaprolactone-modified hydroxyethyl acrylate phosphate prepared from a mole ratio of caprolactone:hydroxyethyl acrylate of 5:1. 16. The dispersant of claim 8, wherein the monophosphate ester is polycaprolactone-modified polypropylene glycolmethacrylate phosphate prepared from a mole ratio of caprolactone:polypropylene glycolmethacrylate of 2:1. 17. The dispersant of claim 8, wherein the monophosphate ester is polycaprolactone-modified glycerol dimethacrylate phosphate prepared from a mole ratio of caprolactone: glycerol dimethacrylate of 2:1. 18. The dispersant of claim 8, wherein the monophosphate ester is polycaprolactone-modified glycerol dimethacrylate phosphate prepared from a mole ratio of caprolactone: glycerol dimethacrylate of 5:1. 19. The dispersant of claim 8, wherein the monophosphate ester is polycaprolactone-modified dipentaerythritol pentaacrylate phosphate prepared from a mole ratio of caprolactone: dipentaerythritol pentaacrylate of 2:1. 20. The dispersant of claim 8, wherein the monophosphate ester is polycaprolactone-modified dipentaerythritol pentaacrylate phosphate prepared from a mole ratio of caprolactone:dipentaerythritol pentaacrylate of 5:1. 21. The dispersant of claim 8, wherein the monophosphate ester is polycaprolactone-modified polyethyleneglycol methacrylate phosphate prepared from a mole ratio of caprolactone :polyethyleneglycol methacrylate of 2:1. 22. The dispersant of claim 8, wherein the monophosphate ester is polycaprolactone-modified polyethyleneglycol methacrylate phosphate prepared from a mole ratio of caprolactone :polyethylenegly col methacrylate of 5:1. 23. A nonaqueous suspension comprising: a polymerizable resin; and solid inorganic particles dispersed in the resin, said particles at least partially coated with the dispersant of claim 1, wherein the resin and dispersant are copolymerizable. 24. The suspension of claim 23, wherein the resin is (meth)acrylate-based and the polymerizable end group of the dispersant is a (meth)acrylate group. 25. The suspension of claim 23, wherein the suspension includes at least about 80 wt.% solid particles. 26. The suspension of claim 25, wherein the suspension includes less than about 5 wt.% dispersant. 27. The suspension of claim 23, wherein the dispersant is a polycaprolactone-modified methacrylate monophosphate. 28. The suspension of claim 23, wherein the polymerizable end group is a radical selected from: oxyethyl methacryloyl-, oxyethyl acryloyl-, polyoxypropyl methacryloyl-, glyceryl dimethacryloyl-, dipentaerythritol pentaacryloyl- and polyoxyethyl methacryloyl-. 29. A nonaqueous suspension comprising: a polymerizable resin; and solid inorganic particles dispersed in the resin, said particles at least partially coated with the polymerizable dispersant of claim 8, wherein the resin and dispersant are copolymerizable. 30. The suspension of claim 29, wherein the resin is (meth)acrylate-based and R is a (meth)acrylate group. 31. The suspension of claim 29, wherein the suspension includes at least about 80 wt.% solid particles. 32. The suspension of claim 31, wherein the suspension includes less than about 5 wt.% dispersant. 33. The suspension of claim 29, wherein the dispersant is a polycaprolactone-modified methacrylate monophosphate. 34. The suspension of claim 29, wherein R is a radical selected from: oxyethyl methacryloyl-, oxyethyl acryloyl-, polyoxypropyl methacryloyl-, glyceryl dimethacryloyl-, dipentaerythritol pentaacryloyl- and polyoxyethyl methacryloyl-. 35. A method of making a highly-filled, cured article, comprising: mixing a polymerizable resin and a polymerizable dispersant, wherein the polymerizable dispersant comprises a phosphate group, a polyester group, and a polymerizable end group; mixing into the resin and dispersant an inorganic solid particulate material to form a paste containing at least about 80 wt.% of the particulate material; and copolymerizing the resin and dispersant to form a cured article. 36. The method of claim 35, wherein the paste includes less than about 5 wt.% dispersant. 37. The method of claim 35, wherein the resin is (meth)acrylate-based and the dispersant is a polycaprolactone-modified methacrylate monophosphate. 38. The method of claim 35, wherein the polymerizable end group is a radical selected from: oxyethyl methacryloyl-, oxyethyl acryloyl-, polyoxypropyl methacryloyl-, glyceryl dimethacryloyl-, dipentaerythritol pentaacryloyl- and polyoxyethyl methacryloyl-. 39. A method of making a highly-filled, cured article, comprising: mixing a polymerizable (meth)acrylate-based resin and a polymerizable dispersant, wherein the polymerizable dispersant comprises a monophosphate ester of the formula wherein R is a (meth)acrylate group radical; mixing into the resin and dispersant an inorganic solid particulate material to form a paste containing at least about 80 wt.% of the particulate material; and copolymerizing the resin and dispersant to form a cured article. 40. The method of claim 39, wherein the paste includes less than about 5 wt.% dispersant. 41. The method of claim 39, wherein the dispersant is a polycaprolactone- modified methacrylate monophosphate. 42. The method of claim 39, wherein R is a radical selected from: oxyethyl methacryloyl-, oxyethyl acryloyl-, polyoxypropyl methacryloyl-, glyceryl dimethacryloyl-, dipentaerythritol pentaacryloyl- and polyoxyethyl methacryloyl-.

Inventors: ANGELETAKIS CHRISTOS, ANGELETAKIS, CHRISTOS
Applicants: KERR CORP, KERR CORPORATION
Application year: 2001
Main classification: A61K6
IPC codes: A61K6, C08F2, C08F30