Ink jet printing method

Abstract: An ink jet printing method, comprising the steps of: A) providing an ink jet printer that is responsive to digital data signals; B) loading the printer with ink-receptive elements comprising a support having thereon a porous ink-receptive layer; C) loading the printer with an ink jet ink composition comprising a water-dispersible polymeric latex and a water-soluble dye; and D) printing on an ink-receptive substrate using the ink jet ink in response to the digital data signals.

Description: This invention relates to an ink jet printing method which employs a porous receiver and an ink jet composition which provides improved stability to light and other environmental contaminants such as ozone. Ink jet printing is a non-impact method for producing images by the deposition of ink droplets on a substrate (paper, transparent film, fabric, etc.) in response to digital signals. Ink jet printers have found broad applications across markets ranging from industrial labeling to short run printing to desktop document and pictorial imaging. The inks used in ink jet printers are generally classified as either dye-based or pigment-based. A dye is a colorant which is molecularly dispersed or solvated by a carrier. The carrier can be a liquid or a solid at room temperature. A commonly used carrier is water or a mixture of water and organic co-solvents. Each individual dye molecule is surrounded by molecules of the carrier. In dye-based inks, no particles are observable under the microscope. Although there have been many recent advances in the art of dye-based ink jet inks, such inks still suffer from deficiencies such as low optical densities on plain paper and poor lightfastness. When water is used as the carrier, such inks also generally suffer from poor water fastness. Ozone is generally present in the air at sea level at concentration of 10 to 50 parts per billion. Under certain conditions, the ozone concentration even exceeds those levels. However, even at the low ozone concentration, dyes such as ink jet dyes can be very sensitive and fade significantly when the air permeability of a receiver is high. US-A-4,460,637 relates to a porous ink jet receiver element. However, there is a problem with this element in that when it is printed using a conventional aqueous dye-based ink, the printed image has poor stability to light and other environmental contaminants such as ozone. JP 08-259863A relates to an ink jet ink composition comprising a water-soluble dye and resin microparticles. However, there is a problem with this ink in that when it is printed onto a conventional, nonporous receiver, the dry time is slow. EP-A-0983866 concerns an ink containing a pigment and thermoplastic polymeric latex particles. It does not teach the use of a water-soluble dye. EP-A-0692528 discloses an ink composition in which fluorescent or non-fluorescent dyes are emulsion polymerized into a water-insoluble tetrapolymer, and in which an anionic surfactant is required. EP-A-1029904 teaches a pigment-based ink that requires two solvents working in conjunction. EP-A-1108757 teaches an ink composition prepared using water-insoluble dyes and a stabilizer for the dye, by incorporating them, in some way, as an integral part of hydrophobic polymer (latex) particles, through a form of loading process. EP A 1 127 707 teaches an ink composition with water-insoluble dyes. It is an object of this invention to provide an ink jet printing method which provides a print having an image which has a fast dry time. It is another object of this invention to provide an ink jet printing method which provides a print having an image which has improved ambient light and ozone stability. These and other objects are achieved in accordance with this invention which relates to an ink jet printing method, comprising the steps of: A) providing an ink jet printer that is responsive to digital data signals; B) loading the printer with ink-receptive elements comprising a support having thereon a porous ink-receptive layer wherein said porous ink-receptive layer comprises from 20% to 90% inorganic particles and from 10% to 80% polymeric binder; C) loading the printer with an ink jet ink composition comprising a water-dispersible polymeric latex and a water soluble dye wherein the water soluble dye and water-dispersible latex exist either individually or are physically mixed; and D) printing on an ink-receptive substrate using the ink jet ink in response to the digital data signals. The support for the ink-receptive element employed in the invention can be paper or resin-coated paper, plastics such as a polyester-type resin such as poly(ethylene terephthalate), polycarbonate resins, polysulfone resins, methacrylic resins, cellophane, acetate plastics, cellulose diacetate, cellulose triacetate, vinyl chloride resins, poly(ethylene naphthalate), polyester diacetate, various glass materials, etc. The thickness of the support employed in the invention can be, for example, from 12 to 500 µm, preferably from 75 to 300 µm. The invention the porous ink-receptive layer contains inorganic particles such as silica, alumina, titanium dioxide, clay, calcium carbonate, barium sulfate, or zinc oxide. The porous ink-receptive layer comprises from 20% to 90% inorganic particles and from 10% to 80% polymeric binder, such as gelatin, poly(vinyl alcohol), poly(vinyl pyrrolidinone) or poly(vinyl acetate). The porous ink-receptive layer can also contain polymer micro-porous structures without inorganic filler particles as shown in US-A-5,374,475 and US-A-4,954,395. A broad range of water-soluble dyes can be used in this invention, such as reactive dyes, direct dyes, anionic dyes, acid dyes, food dyes and the like, such as those described in US-A-5,973,026. In a preferred embodiment of the invention the water-soluble dye may be a cationic or an anionic dye. Examples of anionic dyes which may be used are metal-complex dyes, such as transition metal complexes of 8-heterocyclylazo-5-hydroxyquinoline; azo dyes, such as C.I. Direct Yellow 132; phthalocyanine dyes such as C.I. Direct Blue 199; anthraquinone dyes, or anthrapyridone dyes. U.S. Patent 6,183,548 discloses examples of the above dyes. The water-soluble dye used in method of the invention is present in the ink jet ink in any effective amount, generally from 0.1 to 10% by weight, and preferably from 0.5% to 6% by weight. The ink jet ink containing the water-dispersible polymeric latex employed in the invention consists of water as a continuous phase and polymeric latex as a dispersed phase. The water-soluble dye and the water dispersible polymeric latex are present in the ink so that the water-soluble dye and the water dispersible latex exist either individually or are physically mixed. In a preferred embodiment of the invention, the polymeric latex meets the following test: At 25° C., the polymeric latex must: (a) be capable of forming a stable dispersion with water at a concentration of from 0.2 to 50 percent by weight, preferably 1 to 20 percent by weight, and (b) when 100 ml of the latex is then mixed in an equal volume of the water-miscible organic solvent described above, stirred and allowed to stand for 10 minutes exhibit no observable coagulation of the polymeric latex. In general, the latex should have an average particle size of < 1 µm, preferably < 0.5 µm, more preferably < 0.05 µm. The water-dispersible polymeric latex used in this invention are generally hydrophobic polymers of any composition that can be stabilized in an water-based medium. Such hydrophobic polymers are generally classified as either condensation polymer or addition polymers. Condensation polymers include, for example, polyesters, polyamides, polyurethanes, polyureas, polyethers, polycarbonates, polyacid anhydrides, and polymers comprising combinations of the above-mentioned types. Addition polymers are polymers formed from polymerization of vinyl-type monomers including, for example, allyl compounds, vinyl ethers, vinyl heterocyclic compounds, styrenes, olefins and halogenated olefins, unsaturated acids and esters derived from them, unsaturated nitriles, vinyl alcohols, acrylamides and methacrylamides, vinyl ketones, multifunctional monomers, or copolymers formed from various combinations of these monomers. The water-dispersible polymeric latex can be prepared in aqueous media using well-known free radical emulsion polymerization methods and may consist of homopolymers made from one type of the above-mentioned monomers or copolymers made from more than one type of the above-mentioned monomers. Polymers comprising monomers which form water-insoluble homopolymers are preferred, as are copolymers of such monomers. Preferred polymers may also comprise monomers which give water-soluble homopolymers, if the overall polymer composition is sufficiently water-insoluble to form a latex. The polymer can be prepared by emulsion polymerization, solution polymerization, suspension polymerization, dispersion polymerization, ionic polymerization (cationic, anionic), Atomic Transfer Radical Polymerization, and other polymerization methods known in the art of polymerization. Emulsion polymerization is well known in the art and is described, for example, in F. A. Bovey, Emulsion Polymerization, issued by Interscience Publishers Inc. New York, 1955. In a preferred embodiment of the invention, the water-dispersible polymeric latex comprises a styrene/acrylic polymer, a polyester or a polyurethane. In a more preferred embodiment of the invention, the water-dispersible polymeric latex has glass transition temperature between Tg of -45 to +90 °C and a particle size of from 0.005 to 0.5 µm. A first class of preferred water-dispersible polymeric latices include those styrene/acrylic polymers prepared by free-radical polymerization of vinyl monomers in aqueous emulsion. Polymers comprising monomers which form water-insoluble homopolymers are preferred, as are copolymers of such monomers, which may also comprise monomers which give water-soluble homopolymers, if the overall polymer composition is sufficiently water-insoluble to form a latex. Examples of suitable monomers for the styrene/acrylic polymers are well known in the art as disclosed, for example, in US-A-5,594,047. In a preferred embodiment of the invention, an ester of acrylic acid, an ester of methacrylic acid, and styrene and styrene derivatives is employed. A second class of water-dispersible polymeric latices used in the invention may be aqueous dispersible polyesters. The water-dispersible polyester ionomer polymers used in this invention have the following general formula: wherein: A is the residue of one or more diol components which together comprise 100 mole % of recurring units and is represented by the following structure: -O-(CHR 2 CHR 3 O) m -R 1 -(OCHR 2 CHR 3 ) n -O- wherein: m and n independently represent an integer from 0-4; R 1 represents S, an alkylene group of 1 to 16 carbon atoms; a cycloalkylene group of 5 to 20 carbon atoms; a cyclobisalkylene group of 8 to 20 carbon atoms, a bi- or tri-cycloalkylene group of 7 to 16 carbon atoms, a bi- or tri-cyclobisalkylene group of 9 to 18 carbon atoms, an arenebisalkylene group of from 8 to 20 carbon atoms or an arylene group of 6 to 12 carbon atoms, a carbinol-terminated polydimethylsiloxane segment; and R 2 and R 3 each independently represents H, a substituted or unsubstituted alkyl group of 1 to 6 carbon atoms or a substituted or unsubstituted aryl group of 6 to 12 carbon atoms; B is the residue of a diacid component which comprises 8 to 50 mole % of recurring units and is represented by one or more of the following structures: wherein: M + represents alkali metals, such as Li, Na and K; ammonium groups such as ammonium, methylammonium, triethylammonium, tetralkylammonium, aryltrialkylammonium, etc.; phosphonium groups such as triphenylphosphonium; tetrabutylphosphonium; heteroaromatic ammonium groups such as pyridinium, imidazolium and N-methylammonium; sulfonium groups; guanidinium groups; amidinium groups, etc.; and D is the residue of a diacid component which comprises 50 to 92 mole % of recurring units and is represented by one or more of the following structures: wherein p represents an integer from 2 to 12. Some typical diols which A in the above formula represents include ethylene glycol, diethylene glycol, triethylene glycol, thiodiethanol, cyclohexanedimethanol, bisphenol A, trans-1,4-cyclohexanediol, dodecanediol, cis-exo-2,3-norbornanediol, 5-norbornene-2,2-dimethanol, hydroquinone bis(2-hydroxyethylether), carbinol terminated polydimethylsiloxane, MW=1000 (DMS-C15), (Gelest Inc.), etc. Examples of water dispersible polyesters useful in the invention include Eastman AQ® polyesters, (Eastman Chemical Company). Eastman Polyesters AQ 29, AQ 38, and AQ 55 are composed of varying amounts of isophthalic acid, sodium sulfoisophthalic acid, diethylene glycol, and 1,4-cyclohexanedimethanol. These thermoplastic, amorphous, ionic polyesters are prepared by a melt-phase condensation polymerization at high temperature and low pressure, and the molten product is extruded into small pellets. The solid polymer disperses readily in water at 70°C with minimal agitation to give translucent, low viscosity dispersions containing no added surfactants or solvents. Varying the amount of ionic monomers, i.e., sulfoisophthalic acid, can control the particle size. The particle sizes range from 0.02 to 0.1µm. A third class of polymeric latices used in the invention may be an aqueous dispersible polyurethane. Useful may be prepared as described in "Polyurethane Handbook," Hanser Publishers, Munich Vienna, 1985. Examples of aqueous dispersible polyurethanes are Witcobond® polyurethane dispersion by Witco Corp. or Sancure® polyurethane by BF Goodrich Company. The water dispersible polymer latex used in the current invention is present in the ink jet ink generally from 0.5% to 10% by weight. A humectant is added to the composition employed in the process of the invention to help prevent the ink from drying out or crusting in the orifices of the ink jet printhead. Polyhydric alcohols useful in the composition of the invention for this purpose include, for example, ethylene glycol, diethylene glycol, triethylene glycol, propylene glycol, tetraethylene glycol, polyethylene glycol, glycerol, 2-methyl-2,4-pentanediol, 1,2,6-hexanetriol and thioglycol. As noted above, the humectant is employed in a concentration of from 10 to 50% by weight. In a preferred embodiment, diethylene glycol or a mixture of glycerol and diethylene glycol is employed a concentration of between 10 and 20%. by weight. A co-solvent can also be employed in the composition employed in the process of the invention. The selection of a co-solvent depends on the requirements of the specific application, such as desired surface tension and viscosity, the selected colorant, drying time of the ink jet ink, and the type of paper onto which the ink will be printed. Representative examples of water-soluble co-solvents that may be selected include (1) alcohols, such as methyl alcohol, ethyl alcohol, n-propyl alcohol, isopropyl alcohol, n-butyl alcohol, sec-butyl alcohol, t-butyl alcohol, iso-butyl alcohol, furfuryl alcohol, and tetrahydrofurfuryl alcohol; (2) ketones or ketoalcohols such as acetone, methyl ethyl ketone and diacetone alcohol; (3) esters, such as ethyl acetate, ethyl lactate, ethylene carbonate and propylene carbonate; and (4) sulfur-containing compounds such as dimethyl sulfoxide and tetramethylene sulfone. The ink has physical properties compatible with a wide range of ejecting conditions, i.e., driving voltages and pulse widths for thermal ink jet printing devices, driving frequencies of the piezo element for either a drop-on-demand device or a continuous device, and the shape and size of the nozzle. A penetrant (0-10% by weight) may also be added to the ink composition employed in the process of the invention to help the ink penetrate the receiving substrate, especially when the substrate is a highly sized paper. A preferred penetrant for the inks of the present invention is n-propanol at a final concentration of 1-6% by weight. A biocide (0.01-1.0% by weight) may also be added to prevent unwanted microbial growth which may occur in the ink over time. A preferred biocide for the inks employed in the present invention is Proxel® GXL (Zeneca Colours Co.) at a concentration of 0.05-0.5% by weight. Additional additives which may optionally be present in ink jet inks include thickeners, conductivity enhancing agents, anti-kogation agents, drying agents, and defoamers. Commercially available ink jet printers use several different methods to control the deposition of the ink droplets. Such methods are generally of two types: continuous stream and drop-on-demand. In drop-on-demand systems, a droplet of ink is ejected from an orifice directly to a position on the ink receptive layer by pressure created by, for example, a piezoelectric device, an acoustic device, or a thermal process controlled in accordance with digital data signals. An ink droplet is not generated and ejected through the orifices of the print head unless it is needed. The following example illustrates the utility of the present invention. The following dyes were used in the Example: (C. I. Direct Blue 199) Dye-1 Characterizations of polymeric materials in the following examples were obtained by the following tests or analytical techniques: Glass Transition Temperature and Melting Temperature Both glass transition temperature (Tg) and melting temperature (Tm) of the dry polymer material were determined by differential scanning calorimetry (DSC), using a ramping rate of 20 °C/minute. Tg is defined herein as the inflection point of the glass transition and Tm is defined herein as the peak of the melting transition. Particle Size Measurement All particles were characterized by MICROTRAC II Ultrafine™ article analyzer (UPA) manufactured by Leeds & Northrup. The data reported are the size that 50% of the volume in the sample that is smaller than the indicated size, which is also known as the median diameter. Average Molecular Weight The samples were analyzed by size-exclusion chromatography in tetrahydrofuran using three Polymer Laboratories Plgel™mixed-C columns. The column set was calibrated with narrow-molecular-weight distribution polystyrene standards between 595 (log M=2.76) and 2170000 (log M=6.34) Dalton. Number average molecular weight and polydispersity (defined as the ratio of weight average molecular weight and number average molecular weight) were reported. Preparation of Polymer 1 (aqueous acrylic dispersion) Methyl Acrylate/2-Acrylamido-2-methyl-1-propanesulfonic acid, Sodium Salt (96/4) 400 g of deionized water and 0.6 g Olin 10G™ were charged to a 1-liter three-neck round-bottom flask equipped with a mechanical stirrer and nitrogen inlet. The solution was purged with nitrogen for 30 min and heated to 80 °C in a constant temperature bath. 172.8 g of methyl acrylate and 7.2 g of 2-acrylamido-2-methyl-1-propanesufonic acid(sodium salt) were added and stirred for three minutes. 16.4 g of 10% sodium persulfate solution and 5.5 g of 10% sodium metabisulfite solution were added to initiate the polymerization. Polymerization was continued for one hour and heated one more hour at 80°C. Temperature was reduced to 65-70 °C and 1ml each of t-butyl hydroperoxide (10%) and sodium formaldehyde bisulfite (10%) were post-added. Latex was cooled and filtered. Glass transition temperature was 25 °C, average particle size was 100 nm, and % solids was 30% by weight. Preparation of Polymer 2 (aqueous polyurethane dispersion) In a 1 liter resin flask equipped with thermometer, stirrer, water condenser and a vacuum outlet, 75.07 g polycarbonate polyol KM101733 (Mw = 860) was melted and dewatered under vacuum at 100 C. The vacuum was released and at 40 °C was added 10.24g of dimethylol propionic acid, 21.61g of 1,4-butanediol, 10.0g diethylene glycol, 75g of tetrahydrofuran and 15 drops of dibutyltin dilaurate (catalyst) while stirring. The temperature was adjusted to75 °C. When a homogeneous solution was obtained, 111.47 g isophorone diisocyanate was slowly added, followed by 25 g tetrahydrofuran. The mixture was maintained for about 4 hours to complete the reaction. The NCO (isocyanate determined by IR analysis) was substantially nil. A stoichiometric amount of potassium hydroxide based on dimethylol propionic acid was stirred in and maintained for 5 min. This was mixed with 1300 g of water under high shear to form a stable aqueous dispersion. Tetrahydrofuran was removed by heating under vacuum to give an aqueous dispersion at 19.5% solids by weight solids. The glass transition temperature was 54.5 °C as measured by DSC, the median particle size was 12 nm as measured by UPA, and the weight average molecular weight was 19,100. Aqueous dispersible polyester An AQ55® dispersion was commercially available from Eastman Chemical Co., and was used as received at 28% solids by weight. The Tg was 55 °C as measured by DSC and particle size was 20 nm as measured by UPA. Comparative Ink C-1 To prepare comparative ink jet ink, 4.40 g of Dye 1 (5% active), 0.12 g Surfynol® 465 (from Air Products), 7.0 g glycerol, 4.0 g diethylene glycol, 2.40 g diethyleneglycol monobutyl ether (Dowanol® DB) were added to 22.08 g distilled water. The final ink contained 0.55% dye, 0.30% Surfynol® 465, 17.5% glycerol, 10% diethylene glycol and 6% Dowanol DB. The solution was filtered through a 3 µm polytetrafluoroethylene filter and filled into an Epson SO20089 ink jet cartridge. Comparative Ink C-2 This ink was prepared similar to Comparative Ink 1 except that Dye 2 was used instead of Dye 1. Comparative Ink C-3 This ink was prepared similar to Comparative Ink 1 except that Dye 3 was used instead of Dye 1. Comparative Ink C-4 This ink was prepared similar to Comparative Ink 1 except that Dye 4 was used instead of Dye 1. Ink 1 of the Invention I-1 An ink similar to Comparative Ink 1 was prepared except that Dye 1 and AQ55® dispersion was used instead of Dye 1 alone. To prepare this ink, 4.40 g of Dye 1 (5% active), 7.14g of AQ55® dispersion (28% by weight), 0.12g Surfynol® 465 (from Air Products), 7.0 g glycerol, 4.0 g diethylene glycol, 2.40 g diethyleneglycol monobutyl ether (Dowanol® DB) were added to 14.94 g distilled water. The final ink contained 0.55% dye, 5% AQ55®, 0.30% Surfynol® 465, 17.5% glycerol, 10% diethylene glycol and 6% Dowanol DB™. The solution was filtered through a 3 µm polytetrafluoroethylene filter and filled into an Epson SO20089 ink jet cartridge. Ink 2 of the Invention I-2 An ink similar to Ink I-1 was prepared except that Dye 2 was used instead of Dye 1. Ink 3 of the Invention I-3 An ink similar to Ink I-1 was prepared except that Dye 3 was used instead of Dye 1 Ink 4 of the Invention I-4 An ink similar to Ink I-1 was prepared except that Dye 4 was used instead of Dye 1. Ink 5 of the Invention I-5 An ink similar to Ink I-1 was prepared except an acrylic polymer, Polymer 1 was used instead of polyester, AQ55® Ink 6 of the Invention I-6 An ink similar to Ink I-1 was prepared except a polyurethane, Polymer 2 was used instead of polyester, AQ55®. Ink 7 of the Invention I-7 An ink similar to Ink I-5 was prepared except dye 3 was used instead of dye 1. Ink 8 of the Invention I-8 An ink similar to Ink I-6 was prepared except dye 3 was used instead of dye 1. Printing Elements were prepared using test images consisting of a series of 21 variable density patches, approximately 15 by 13 mm in size, ranging from 5% dot coverage to 100% dot coverage printed onto commercially available Konica Photo IJ QP® paper, a porous receiver with an Epson 800 ink jet printer, using the above inks. The elements were allowed to dry for 24 hours at ambient temperature and humidity. Stability Tests The above elements were then subjected to low intensity florescent irradiation (1 Klux) for four weeks. Additional elements were subjected to an ozone chamber (∼5 ppm ozone level, 50% relative humidity) for 24 hours. The Status A reflection densities of maximum density patch of the elements were measured using an X-Rite® 414 densitometer before and after the fade test. The % retained in Status A density for the 100% dot coverage patches were calculated and listed in Table 1. Element Containing Ink Fluorescence Light Test (% Retained) Ozone Test (% Retained) C-1 101 51 I-1 100 92 I-5 100 98 I-6 100 70 C-2 96 88 I-2 100 96 C-3 9 3 I-3 60 41 I-7 67 48 I-8 62 35 C-4 95 6 I-4 101 86 The above results in Table 1 show that the elements of the invention had improved lightfastness and/or ozone stability as compared to the control elements.

Claims: An ink jet printing method, comprising the steps of: A) providing an ink jet printer that is responsive to digital data signals; B) loading said printer with ink-receptive elements comprising a support having thereon a porous ink-receptive layer wherein said porous ink-receptive layer comprises from 20% to 90% inorganic particles and from 10% to 80% polymeric binder; C) loading said printer with an ink jet ink composition comprising a water-dispersible polymeric latex and a water-soluble dye, wherein the water soluble dye and water-dispersible latex exist either individually or are physically mixed; and D) printing on an ink-receptive substrate using said ink jet ink in response to said digital data signals. The method of Claim 1 wherein said inorganic particles comprise silica, alumina, titanium dioxide, clay, calcium carbonate, barium sulfate, or zinc oxide. The method of Claim 1 wherein said polymeric binder is gelatin, poly(vinyl alcohol), poly(vinyl pyrrolidinone) or poly(vinyl acetate). The method of Claim 1 wherein said water-dispersible polymeric latex has a Tg of -45 to +90 °C and a particle size of from 0.005 to 0.5 µm. The method of Claim 4 wherein said water-dispersible polymeric latex is a styrene/acrylic polymer, a polyester or a polyurethane. The method of Claim 1 wherein said polymeric latex has a average diameter of less than 0.05 µm. The method of Claim 1 wherein said water soluble dye is a cationic dye. The method of Claim 7 wherein said cationic dye is an azo dye, a triarylmethane dye, an azine dye, a phthalocyanine dye, an oxazine dye or a thiazine dye.

Inventors: CHEN HUIJUAN D, ERDTMANN DAVID, YAU HWEI-LING, CHEN, HUIJUAN D., ERDTMANN, DAVID, YAU, HWEI-LING, Chen, Huijuan D., c/o Eastman Kodak Company, Erdtmann, David, c/o Eastman Kodak Company, Yau, Hwei-Ling, c/o EASTMAN KODAK COMPANY
Applicants: EASTMAN KODAK CO, EASTMAN KODAK COMPANY
Application year: 2001
Main classification: C09D11
IPC codes: B41M5, C09D11, B41J2