COATED IMPLANTABLE MEDICAL DEVICE

Abstract: A medical device (10) includes a structure (12) adapted for introduction into a patient, the structure (12) being formed of a preferably non-porous base material (14) having a roughened or textured surface (16). The structure (12) is conveniently configured as a vascular stent with a base material (14) of stainless steel, nitinol or another suitable material. The medical device (10) also includes a layer (18) of a bioactive material posited directly upon the roughened or textured surface (16) of the base material (14) of the structure (12). The surface (16) of the base material (14) is roughened or textured by etching or by abrasion with sodium bicarbonate or another suitable grit. A preferred roughened or textured surface (16) is thought to have a mean surface roughness of about 10 mu in. (about 250 nm) and a surface roughness range between about 1/ mu in. and about 100 mu in. (about 25 nm and about 2.5 mu m). The particularly preferred use of sodium bicarbonate as the abrasive to provide roughness or texture to the surface (16) of the base material (14) of the structure (12) is additionally advantageous in the low toxicity of the sodium bicarbonate to production workers, the ease of product and waste cleanup, and the biocompatibility of any residual sodium bicarbonate.

Description: COATED IMPLANTABLE MEDICAL DEVICE Description Technical Field This invention relates generally to human and veterinary medical devices and, more particularly, to devices incorporating drugs, bioactive agents, therapeutic agents or diagnostic agents. Background of the Invention It has become common to treat a variety of medical conditions by temporarily or permanently introducing an implantable medical device partly or completely into the esophagus, trachea, colon, biliary tract, urinary tract, vascular system or other location within a human or veterinary patient. Many treatments of the vascular or other systems entail the introduction of a device such as a stent, a catheter, a balloon, a wire guide, a cannula or the like. For this purpose, a stent may most simply be considered as a cylinder of relatively short length which opens a body passage or lumen or which maintains a body passage or lumen in an open condition. Such medical devices are generally capable of serving their intended purposes quite well. Some drawbacks can be encountered during their use, however. For example, when a device is introduced into and manipulated through the vascular system of a patient, the blood vessel walls can be disturbed or injured. Clot formation or thrombosis often results at the injured site, causing stenosis (closure) of the blood vessel. Moreover, if the medical device is left within the patient for an extended period of time, thrombus often forms on the device itself, again causing stenosis. As a result, the patient is placed at risk of a variety of complications, including heart attack, pulmonary embolism, and stroke. Thus, the use of such a medical device can entail the risk of precisely the problems that its use was intended to ameliorate. Another way in which blood vessels undergo stenosis is through disease. Probably the most common disease causing stenosis of blood vessels is atherosclerosis. Many medical devices and therapeutic methods are known for the treatment of atherosclerotic disease. One particularly useful therapy for certain atherosclerotic lesions is percutaneous transluminal angioplasty (PTA). During PTA, a balloon-tipped catheter is inserted in a patient's artery, the balloon being deflated. The tip of the catheter is advanced to the site of the atherosclerotic plaque to be dilated. The balloon is placed within or across the stenotic segment of the artery, and then inflated. Inflation of the balloon "cracks" the atherosclerotic plaque and expands the vessel, thereby relieving the stenosis, at least in part. While PTA presently enjoys wide use, it suffers from two major problems. First, the blood vessel may suffer acute occlusion immediately after or within the initial hours after the dilation procedure. Such occlusion is referred to as "abrupt closure." Abrupt closure occurs in perhaps five percent or so of the cases in which PTA is employed, and can result in myocardial infarction and death if blood flow is not restored promptly. The primary mechanisms of abrupt closures are believed to be elastic recoil, arterial dissection and/or thrombosis. It has been postulated that the delivery of an appropriate agent (such as an antithrombic) directly into the arterial wall at the time of angioplasty could reduce the incidence of thrombotic acute closure, but the results of attempts to do so have been mixed. A second major problem encountered in PTA is the re-narrowing of an artery after an initially successful angioplasty. This re-narrowing is referred to as "restenosis" and typically occurs within the first six months after angioplasty. Restenosis is believed to arise through the proliferation and migration of cellular components from the arterial wall, as well as through geometric changes in the arterial wall referred to as "remodeling." It has similarly been postulated that the delivery of appropriate agents directly into the arterial wall could interrupt the cellular and/or remodeling events leading to restenosis. However, like the attempts to prevent thrombotic acute closure, the results of attempts to prevent restenosis in this manner have been mixed. Non-atherosclerotic vascular stenosis may also be treated by PTA. For example, Takayasu arteritis or neurofibromatosis may cause stenosis by fibrotic thickening of the arterial wall. Restenosis of these lesions occurs at a high rate following angioplasty, however, due to the fibrotic nature of the diseases. Medical therapies to treat or obviate them have been similarly disappointing. A device such as an intravascular stent can be a useful adjunct to PTA, particularly in the case of either acute or threatened closure after angioplasty. The stent is placed in the dilated segment of the artery to mechanically prevent abrupt closure and restenosis. Unfortunately, even when the implantation of the stent is accompanied by aggressive and precise antiplatelet and anticoagulation therapy (typically by systemic administration), the incidence of thrombotic vessel closure or other thrombotic complication remains significant, and the prevention of restenosis is not as successful as desired. Furthermore, an undesirable side effect of the systemic antiplatelet and anticoagulation therapy is an increased incidence of bleeding complications, most often at the percutaneous entry site. Other conditions and diseases are treatable with stents, catheters, cannulae and other medical devices inserted into the esophagus, trachea, colon, biliary tract, urinary tract and other locations in the body. A wide variety of bioactive materials (drugs, therapeutic agents, diagnostic agents and other materials having biological or pharmacological activity within a patient) have been applied to such medical devices for the purpose of introducing such materials into the patient. Unfortunately, the durable application of bioactive materials to stents and the like, sufficient for such introduction to successfully occur, is often problematic. A range of containment or layering materials have been applied to such devices to permit the timed release of bioactive materials from such devices, or even to permit bioactive materials to be applied to such devices at all. Unfortunately, the use of such containment materials can significantly increase the time and cost of manufacturing suitable implantable devices. Moreover, some bioactive materials may not be able to withstand incorporation in known containment materials. Additionally, certain containment materials may not be biocompatible and may cause problems of the type desired to be reduced. It would be desirable to develop devices and methods for reliably delivering suitable therapeutic and diagnostic agents, drugs and other bioactive materials directly into a body portion during or following a medical procedure, so as to treat or prevent the conditions and diseases mentioned above, for example, to prevent abrupt closure and/or restenosis of a body portion such as a passage, lumen or blood vessel. It would also be desirable to limit systemic exposure of the patient to such bioactive materials. This would be particularly advantageous in therapies involving the delivery of a chemotherapeutic agent to a particular organ or site through an intravenous catheter (which itself has the advantage of reducing the amount of agent needed for successful treatment), by preventing stenosis both along the catheter and at the catheter tip. It would be desirable to similarly improve other therapies. Of course, it would also be desirable to avoid degradation of the agent, drug or bioactive material during its incorporation on or into any such device. It would further be highly desirable to develop a method for coating an implantable medical device with a drug, therapeutic agent, diagnostic agent or other bioactive material which entailed a minimum number of steps, thereby reducing the ultimate cost of treating the patient. It would be desirable to deliver the bioactive material without causing additional problems with a poor biocompatible carrier or containment material. Finally, it would be highly desirable to develop a method for coating an implantable medical device with a drug, therapeutic agent, diagnostic agent or other bioactive material which could be carried out in such a way as to minimize any environmental or personal risks or inconveniences associated with the manufacture of the device. Summary of the Invention The foregoing problems are solved and a technical advance is achieved in an illustrative embodiment of a medical device of the present invention coated (at least in part) with a drug, therapeutic agent, diagnostic agent or other bioactive or pharmacologically active material. (Hereinafter, any or all of these will be collectively referred to as "a bioactive material" or "bioactive materials."). The specific improvement of the present invention entails attaining a desired surface roughness, or texturing, on the surface of the device by whatever treatment of the surface and applying the bioactive material directly to that roughened or textured surface without the need of any further overlying or containment layer or coating. Unexpectedly, this straightforward expedient yields a coated implantable medical device which is sufficiently durable to withstand the desired implantation without suffering an unacceptable amount of loss (if any) of bioactive material from the device. In one aspect of the invention, at least a part of the surface of the device, for example the outer surface of a stent, is treated to produce a roughened, uneven, or unsmooth surface, and the bioactive material is formed or posited on at least the part of the surface. The degree of surface treatment is controlled to provide sufficient adhesion of the bioactive material to the device surface. In the preferred embodiment of the medical device of the present invention, the device first comprises a structure adapted for temporary or permanent introduction into the esophagus, trachea, colon, biliary tract, urinary tract, vascular system or other location in a human or veterinary patient. The structure comprises a base material (preferably non-porous) having a roughened or textured surface. The surface of the base material can be roughened or textured by etching but is preferably roughened or textured by abrasion with an abrasive grit, most preferably sodium bicarbonate (USP) . The medical device of the present invention also comprises a layer of bioactive material posited directly upon the roughened or textured surface of the base material of the structure. Furthermore, the device advantageously does not require or is free of any additional coating or layer atop the layer of bioactive material. As described in more detail below, the base material of the structure and the bioactive material posited on that base material can comprise any of a wide range of suitable materials. The selection of a specific combination of base material, bioactive material and surface roughness or texture depends upon the intended use of the medical device. Although texture may have a meaning of a repeatable pattern, this is clearly not the intent. The surface of the stent is that of any topography, whether repeatable or not, that helps improve adhesion of the bioactive material on the base material or modification thereof. Hereinafter, a textured surface will include a roughened, uneven, or unsmooth surface. The suitability of a chosen combination can readily be determined by an adhesion test which simulates the actual delivery of bioactive material during introduction and deployment of the device in a patient. Such a test is straightforward and is believed not to entail an undue amount of experimentation, particularly in comparison to the amount and technical level of testing required before a product of this type can be marketed in the United States. The medical device of the present invention and its method of manufacture have several advantages over prior stents and other medical devices and methods for manufacturing them. The time and cost of manufacture of the medical device are minimized by the absence of any steps to incorporate the bioactive material in a containment layer, or to apply a containment or time-release layer over the bioactive material. The particularly preferred use of sodium bicarbonate as the abrasive to treat, roughen, or texture the surface of the base material of the structure enjoys several indirect cost savings resulting from the low toxicity of the sodium bicarbonate to production workers, the ease of product and waste cleanup, and the biocompatibility of any residual sodium bicarbonate. Worker safety and ease of product and waste cleanup are, of course, important advantages in their own right. In a first aspect, then, the present invention is directed to a medical device comprising: a structure adapted for introduction into a patient, the structure comprising a base material (preferably non-porous) having a at least one of a roughened, uneven, unsmooth, or textured surface; and a layer of a bioactive material posited directly upon the surface of the base material of the structure. Furthermore, the medical device does not require or is free of any additional coating or layer atop the layer of bioactive material for delivering the bioactive material. The structure is preferably configured as a stent, such as a vascular or other stent. The base material of the structure preferably comprises at least one of: stainless steel, tantalum, titanium, nitinol, gold, platinum, inconel, iridium, silver, tungsten, or another biocompatible metal, or alloys of any of these; carbon or carbon fiber; cellulose acetate, cellulose nitrate, silicone, polyethylene terephthalate, polyurethane, polyamide, polyester, polyorthoester, polyanhydride, polyether sulfone, polycarbonate, polypropylene, high molecular weight polyethylene, polytetrafluoroethylene, or another biocompatible polymeric material, or mixtures or copolymers of these; polylactic acid, polyglycolic acid or copolymers thereof, a polyanhydride, polycaprolactone, polyhydroxybutyrate valerate or another biodegradable polymer, or mixtures or copolymers of these; a protein, an extracellular matrix component, collagen, fibrin or another biologic agent; or a suitable mixture of any of these. The bioactive material of the layer on the roughened, uneven, unsmooth, or textured surface of the base material preferably comprises at least one of: paclitaxel; estrogen or estrogen derivatives; heparin or another thrombin inhibitor, hirudin, hirulog, argatroban, D-phenylalanyl-L-poly-L-arginyl chloromethyl ketone or another antithrombogenic agent, or mixtures thereof; urokinase, streptokinase, a tissue plasminogen activator, or another thrombolytic agent, or mixtures thereof; a fibrinolytic agent; a vasospasm inhibitor; a calcium channel blocker, a nitrate, nitric oxide, a nitric oxide promoter or another vasodilator; an antimicrobial agent or antibiotic; aspirin, ticlopdine or another antiplatelet agent; colchicine or another antimitotic, or another microtubule inhibitor; cytochalasin or another actin inhibitor; a remodelling inhibitor; deoxyribonucleic acid, an antisense nucleotide or another agent for molecular genetic intervention; GP llb/llla, GP Ib-IX or another inhibitor or surface glycoprotein receptor; methotrexate or another antimetabolite or antiproliferative agent; an anti-cancer chemotherapeutic agent; dexamethasone, dexamethasone sodium phosphate, dexamethasone acetate or another dexamethasone derivative, or another anti-inflammatory steroid; dopamine, bromocriptine mesylate, pergolide mesylate or another dopamine agonist; 60 Co (having a half life of 5.3 years), 192 lr (73.8 days), 32 P (14.3 days), 111 ln (68 hours), 90 Y (64 hours), 99m Tc (6 hours) or another radiotherapeutic agent; iodine-containing compounds, barium-containing compounds, gold, tantalum, platinum, tungsten or another heavy metal functioning as a radiopaque agent; a peptide, a protein, an enzyme, an extracellular matrix component, a cellular component or another biologic agent; captopril, enalapril or another angiotensin converting enzyme (ACE) inhibitor; ascorbic acid, alphatocopherol, superoxide dismutase, deferoxyamine, a 21 - aminosteroid (lasaroid) or another free radical scavenger, iron chelator or antioxidant; angiopeptin; a 14 C-, 3 H-, 131 l-, 32 P- or 36 S-radiolabelled form or other radiolabelled form of any of the foregoing; or a mixture of any of these. Preferably, the roughened, uneven, unsmooth, or textured surface of the base material of the structure has a mean surface roughness of about 10 //in. (about 250 nm) and a surface roughness range between about 1 //in. and about 1 00 //in. (about 25 nm and about 2.5 μm). In a second aspect, the present invention is directed to a medical device comprising: a structure adapted for introduction into a patient, the structure comprising a base material having a roughened, uneven, unsmooth, or textured surface, the structure being configured as a vascular stent and the base material comprising at least one of stainless steel, nitinol, or an allow of nickel and titanium; and a layer of a bioactive material posited directly upon the roughened or textured surface of the base material of the structure, the bioactive material comprising paclitaxel; wherein the medical device does not require or is free of any additional coating or layer atop the layer of bioactive material; and wherein the roughened or textured surface of the base material of the structure has a mean surface roughness of about 10 //in. (about 250 nm) and a surface roughness range between about 1 //in. and about 100 //in. (about 25 nm and about 2.5 μm). In a third aspect, the present invention is directed to a method of manufacturing a medical device comprising the steps of: providing a structure adapted for introduction into a patient, the structure comprising a base material (preferably non-porous) having a surface; roughening or texturing the surface of the base material of the structure; and positing a layer of a bioactive material directly upon the roughened or textured surface of the base material of the structure; the method being characterized in that the resulting medical device does not require or is free of any additional coating or layer atop the layer of bioactive material. Preferably, the method is carried out with a structure configured as a stent, such as a vascular stent. The method is preferably carried out with a base material and a bioactive material as described in the first aspect of the invention above. The positing step of the method is preferably carried out by spraying a solution of the bioactive material on the roughened or textured surface of the base material of the structure. Dipping the base material in a solution of the bioactive material is also contemplated in the practice of the present invention. The roughening or texturing step of the method is preferably carried out by abrading the surface of the base material of the structure. Etching of the surface is also contemplated in the practice of the present invention. Abrading of the surface of the base material is preferably carried out with an abrasive grit comprising at least one of sodium bicarbonate (USP), calcium carbonate, aluminum oxide, colmanite (calcium borate), crushed glass or crushed walnut shells. More preferably, the abrading is carried out with an abrasive grit having a particle size of about 5 microns (5 μm) to about 500 microns (500 μm) . Even more preferably, the abrading is carried out with sodium bicarbonate (USP) having a nominal particle size of about 50 microns (50 μm) . Abrading of the surface of the base material is preferably carried out with an abrasive grit delivered at a pressure under flow of about 5 to about 200 PSI (about 34 to about 1 380 KPa) and at a grit feed rate of about 1 to about 1 000 g/min. Abrading of the surface is preferably carried out so as to yield a textured surface on the base material having a mean surface roughness of about 10 //in. (about 250 nm) and a surface roughness range between about 1 //in. and about 100 //in. (about 25 nm and about 2.5 μm) . In another aspect, the present invention is directed to the product of the method described in the third aspect of the invention, above. In yet a further aspect, the present invention is directed to a method of medical treatment or diagnosis which comprises introducing the medical device of the present invention, or the product of the method of the present invention, into a human or veterinary patient. Again, as indicated above, the medical device of the present invention and its method of manufacture have several advantages over prior stents and other medical devices and methods for manufacturing them. The time and cost of manufacture of the medical device of the present invention are minimized by the absence of any steps to incorporate the bioactive material in a containment layer, or to apply a containment or time-release layer over the bioactive material. The particularly preferred use of sodium bicarbonate as the abrasive to roughen or texture the surface of the base material of the structure enjoys cost savings resulting from the low toxicity of the sodium bicarbonate to production workers, the ease of product and waste cleanup, and the biocompatibility of any residual sodium bicarbonate. It should go without saying that the good worker safety and ease of product and waste cleanup enjoyed by the method of the present invention are highly desirable advantages, without regard to any costs saved. Brief Description of the Drawing A better understanding of the present invention will now be had upon reference to the following detailed description, when read in conjunction with the accompanying drawing, wherein like reference characters refer to like parts throughout the several views, and in which: Fig. 1 is a side view showing one of the steps of the method of the preferred embodiment of the present invention; and Fig. 2 is an enlarged cross-sectional view of a portion of the medical device and product of the preferred embodiment of the present invention. Detailed Description With reference now to the Figures, an implantable medical device 1 0 in accordance with the present invention is thereshown. The medical device 10 of the present invention first comprises a structure 1 2 adapted for temporary or permanent introduction into a human or veterinary patient. "Adapted" means that the structure 1 2 is particularly configured, shaped and sized for such introduction. By way of example, the structure 1 2 is most preferably configured as a vascular stent adapted for insertion into the vascular system of the patient. The structure 1 2 can of course be particularly configured for use in other systems and sites such as the esophagus, trachea, colon, biliary ducts, urethra and ureters, among others. Indeed, the structure 1 2 can alternatively be configured as any conventional vascular or other comparable medical device, and can include any of a variety of conventional stent or other adjuncts, such as helically wound strands, perforated cylinders or the like. Moreover, because the problems addressed by the present invention arise primarily with respect to those portions of the device actually positioned within the patient, the inserted structure 1 2 need not be an entire device, but can merely be that portion of a vascular or other device which is intended to be introduced into the patient. Accordingly, the structure 1 2 can be configured as at least one of, or any portion of, a catheter, a wire guide, a cannula, a stent, a vascular or other graft, a cardiac pacemaker lead or lead tip, a cardiac defibrillator lead or lead tip, a heart valve, a suture, a needle, an angioplasty device or a pacemaker. The structure 1 2 can also be configured as a combination of portions of any of these. For ease of understanding the present invention, Figs. 1 and 2 show only a structure 1 2 configured as a stent, and more particularly, a vascular stent. More preferably, the structure 1 2 is configured as a vascular stent such as the"LOGIC" stent, the "V-FLEX PLUS" stent, or the "ACHIEVE" stent, all commercially available from Cook Incorporated, Bloomington, Indiana. Such stents are cut from a cannula of suitable material and possess a plurality of interconnected struts allowing the stents to expand upon inflation of a balloon on which they are carried. They possess a flat outer surface, which as a practical matter makes them easier to process via the present invention than stents made of a plurality of round wires; the latter are more difficult to abrade. These stents possess a smooth inside surface to reduce the possibility of thrombogenesis. The particular shape and dimensions of the structure 1 2 should of course be selected as required for its specific purpose and for the particular site in the patient at which it will be employed, such as in the coronary arteries, aorta, esophagus, trachea, colon, biliary tract or urinary tract. A structure 1 2 intended for each location will have different dimensions particularly suited to such use. For example, aortic, esophageal, tracheal and colonic stents may have diameters up to about 25mm and lengths about 100 mm or longer. Vascular stents are generally shorter, typically about 10 to 60 mm in length, and often preferably about 1 2 to 25 mm in length. Such vascular stents are typically designed to expand to a diameter of about 2 to 6 mm when inserted into the vascular system of a patient, often preferably about 2 to 4 mm. The structure 1 2 is composed of a base material 1 4 suitable for the intended use of the structure 1 2. The base material 1 4 is preferably biocompatible. A variety of conventional materials can be employed as the base material 14. Some materials may be more useful for structures other than the coronary stent exemplifying the structure 12. The base material 14 may be either elastic or inelastic as required for its intended use in the patient. The base material may be either biodegradable or nonbiodegradable, and a variety of biodegradable polymers are known. The base material 14 can also be porous or preferably non-porous, again based on its intended use or application. Accordingly, the base material 1 4 can include at least one of stainless steel, tantalum, titanium, nitinol, gold, platinum, inconel, iridium, silver, tungsten, or another biocompatible metal, or alloys of any of these; carbon or carbon fiber; cellulose acetate, cellulose nitrate, silicone, polyethylene terephthalate, polyurethane, polyamide, polyester, polyorthoester, polyanhydride, polyether sulfone, polycarbonate, polypropylene, high molecular weight polyethylene, polytetrafluoroethylene, or another biocompatible polymeric material, or mixtures or copolymers of these; polylactic acid, polyglycolic acid or copolymers thereof, a polyanhydride, polycaprolactone, polyhydroxybutyrate valerate or another biodegradable polymer, or mixtures or copolymers of these; a protein, an extracellular matrix component, collagen, fibrin or another biologic agent; or a suitable mixture of any of these. Stainless steel is particularly useful as the base material 14 when the structure 1 2 is configured as a vascular stent. In the practice of the present invention, however, particularly preferred base materials 14 include stainless steel, nitinol, tantalum, polylactic acid, polyglycolic acid and biodegradable materials. Molybdenum-rhenium alloy and magnesium may also possibly be useful base materials 1 4 as well. Of course, when the structure 1 2 is composed of a radiolucent material such as polypropylene, polyethylene or others above, a conventional radiopaque marker or coating may and preferably should be applied to it at some limited location. The radiopaque marker or coating provides a means for identifying the location of the structure 1 2 by X-ray or fluoroscopy during or after its introduction into the patient's vascular system. The base material 14 of the structure 12 of the medical device 10 of the present invention includes a roughened or textured surface 1 6 extending at least partly over the base material 14. The surface 1 6 is roughened or textured in a manner described in more detail below. While the surface 1 6 can be the entire surface of the base material 14, in the preferred embodiment of the present invention (where the structure 1 2 is configured as a vascular stent) the surface 1 6 is the outer surface of the base material 14. The medical device 1 0 of the present invention further comprises at least one layer 1 8 of a bioactive material posited directly upon the roughened or textured surface 1 6 of the base material 14 of the structure 1 2. The medical device 10 of the present invention is characterized in that it does not require or is free of any additional coating or layer atop the layer 1 8 of bioactive material. Although, it is to be understood that for any reason an additional coating or layer atop or below the layer 1 8 of bioactive is desired, such coating or layer can be applied and still be within the contemplation of the present invention. The layer 1 8 may be smoother or rougher than the roughened or textured surface 1 6. The base material 14 of the structure 1 2 is preferably non-porous, although the structure 1 2 itself can be perforate. The difference between a porous material and a non-porous but perforate material is a practical one; the relatively smaller open cells of a porous material are of a character and number sufficient to retain an appreciable amount of an applied bioactive material therein, while the relatively larger perforations of a non-porous material are of a character and number which are not sufficient to retain an appreciable amount of an applied bioactive material therein. Alternatively, the open cells of a porous material can be considered generally microscopic, while perforations through a non-porous material can be considered generally macroscopic. A vast range of drugs, medicants and materials can be employed as the bioactive material in the layer 1 8. Particularly useful in the practice of the present invention are materials which prevent or ameliorate abrupt closure and restenosis of blood vessels previously opened by stenting surgery or other procedures. Thrombolytics (which dissolve, break up or disperse thrombi) and antithrombogenics (which interfere with or prevent the formation of thrombi) are especially useful bioactive materials when the structure 1 2 is a vascular stent. Particularly preferred thrombolytics are urokinase, streptokinase and the tissue plasminogen activators. Particularly preferred antithrombogenics are heparin, hirudin and the antiplatelets. Urokinase is a plasminogen activating enzyme typically obtained from human kidney cell cultures. Urokinase catalyzes the conversion of plasminogen into the fibrinolytic plasmin, which breaks down fibrin thrombi. Heparin is a mucopolysaccharide anticoagulant typically obtained from porcine intestinal mucosa or bovine lung. Heparin acts as a thrombin inhibitor by greatly enhancing the effects of the blood's endogenous antithrombin III. Thrombin, a potent enzyme in the coagulation cascade, is key in catalyzing the formation of fibrin. Therefore, by inhibiting thrombin, heparin inhibits the formation of fibrin thrombi. Of course, bioactive materials having other functions can also be successfully delivered by the device 1 0 of the present invention. For example, an antiproliferative agent such as methotrexate will inhibit over-proliferation of smooth muscle cells and thus inhibit restenosis of the dilated segment of the blood vessel. Additionally, localized delivery of an antiproliferative agent is also useful for the treatment of a variety of malignant conditions characterized by highly vascular growth. In such cases, the device 1 0 of the present invention could be placed in the arterial supply of the tumor to provide a means of delivering a relatively high dose of the antiproliferative agent directly to the tumor. A vasodilator such as a calcium channel blocker or a nitrate will suppress vasospasm, which is common following angioplasty procedures. Vasospasm occurs as a response to injury of a blood vessel, and the tendency toward vasospasm decreases as the vessel heals. Accordingly, the vasodilator is desirably supplied over a period of about two to three weeks. Of course, trauma from angioplasty is not the only vessel injury which can cause vasospasm, and the device 1 0 may be introduced into vessels other than the coronary arteries, such as the aorta, carotid arteries, renal arteries, iliac arteries or peripheral arteries for the prevention of vasospasm in them. A variety of other bioactive materials are particularly suitable for use when the structure 1 2 is configured as something other than a coronary stent. For example, an anti-cancer chemotherapeutic agent can be delivered by the device 1 0 to a localized tumor. More particularly, the device 10 can be placed in an artery supplying blood to the tumor or elsewhere to deliver a relatively high and prolonged dose of the agent directly to the tumor, while limiting systemic exposure and toxicity. The agent may be a curative, a pre-operative debulker reducing the size of the tumor, or a palliative which eases the symptoms of the disease. It should be noted that the bioactive material in the present invention is delivered across the device 1 0, and not by passage from an outside source through any lumen defined in the device 1 0, such as through a catheter employed for conventional chemotherapy. The bioactive material of the present invention may, of course, be released from the device 10 into any lumen defined in it, and that lumen may carry some other agent to be delivered through it. Paclitaxel is a particularly preferred anti-cancer agent and/or anti- angiogenic agent as the bioactive material of the layer 1 8. The angiogenesis- dependent diseases are those diseases which require or induce vascular growth, for example, certain types of cancer. Estrogen and estrogen derivatives are also particularly preferred as the bioactive material of the layer 1 8. Dopamine or a dopamine agonist such as bromocriptine mesylate or pergolide mesylate is useful for the treatment of neurological disorders such as Parkinson's disease. The device 1 0 could be placed in the vascular supply of the thalamic substantia nigra for this purpose, or elsewhere, localizing treatment in the thalamus. The present invention also contemplates the use of bioactive materials which covalently bond to the roughened or textured surface 1 6 of the base material 14 of the structure 1 2. It should be clear that a wide range of other bioactive materials can be delivered by the device 10. Accordingly, it is preferred that the bioactive material of the layer 18 comprises at least one of: paclitaxel; estrogen or estrogen derivatives; heparin or another thrombin inhibitor, hirudin, hirulog, argatroban, D-phenylalanyl-L- poly-L-arginyl chloromethyl ketone, or another antithrombogenic agent, or mixtures thereof; urokinase, streptokinase, a tissue plasminogen activator, or another thrombolytic agent, or mixtures thereof; a fibrinolytic agent; a vasospasm inhibitor; a calcium channel blocker, a nitrate, nitric oxide, a nitric oxide promoter or another vasodilator; an antimicrobial agent or antibiotic; aspirin, ticlopdine or another antiplatelet agent; colchicine or another antimitotic, or another microtubule inhibitor; cytochalasin or another actin inhibitor; a remodelling inhibitor; deoxyribonucleic acid, an antisense nucleotide or another agent for molecular genetic intervention; GP llb/llla, GP Ib-IX or another inhibitor or surface glycoprotein receptor; methotrexate or another antimetabolite or antiproliferative agent; an anti-cancer chemotherapeutic agent; dexamethasone, dexamethasone sodium phosphate, dexamethasone acetate or another dexamethasone derivative, or another anti-inflammatory steroid; an immunosuppressive agent (such as cyclosporin or rapamycine); an antibiotic (such as streptomycin, erythromycin or vancomycine); dopamine, bromocriptine mesylate, pergolide mesylate or another dopamine agonist; 60 Co (having a half life of 5.3 years), 192 lr (73.8 days), 32 P (14.3 days), 111 ln (68 hours), 90 Y (64 hours), 99m Tc (6 hours) or another radiotherapeutic agent; iodine-containing compounds, barium-containing compounds, gold, tantalum, platinum, tungsten or another heavy metal functioning as a radiopaque agent; a peptide, a protein, an enzyme, an extracellular matrix component, a cellular component or another biologic agent; captopril, enalapril or another angiotensin converting enzyme (ACE) inhibitor; ascorbic acid, alphatocopherol, superoxide dismutase, deferoxyamine, a 21 -aminosteroid (lasaroid) or another free radical scavenger, iron chelator or antioxidant; angiopeptin; a 1 C-, 3 H- , 131 l-, 32 P- or 36 S-radiolabelled form or other radiolabelled form of any of the foregoing; or a mixture of any of these. When the structure 1 2 is configured as a vascular stent, however, particularly preferred materials for the bioactive material of the layer 1 8 are heparin, anti-inflammatory steroids including but not limited to dexamethasone and its derivatives, and mixtures of heparin and such steroids. Other materials may possibly be useful as the bioactive material in the practice of the present invention, including: smooth muscle cell inhibitors, collagen inhibitors, anti-coagulants and cholesterol reducing agents; forskolin, vapiprost, prostaglandin and analogues thereof, prostacyclin and prostacyclin analogues, dextran and dipyridamole; angiotensin converting enzyme inhibitors such as Captopril ® (available from Squibb), Cilazapril ® (available from Hoffman-LaRoche), or Lisinopril ® (available from Merck); fibroblast growth factor (FGF) antagonists, fish oil (omega 3-fatty acid), histamine antagonists, Lovastatin ® (an inhibitor of HMG-CoA reductase, a cholesterol-lowering drug from Merck), methotrexate, monoclonal antibodies (such as to PDGF receptors), nitroprusside, phosphodiesterase inhibitors, prostaglandin inhibitor (available from Glaxo), vascular endothelial growth factor (VEGF) or analogues thereof, various cell cycle inhibitors such as the protein product of the retinoblastoma tumor suppressor gene or analogues thereof), Seramin (a PDGF antagonist), serotonin blockers, steroids, thioprotease inhibitors, triazolopyrimidine (a PDGF antagonist), nitric oxide, alpha-interferon and genetically engineered epithelial cells. The present invention is also directed to a method of manufacturing the medical device 10 disclosed above. More particularly, the method of the present invention first comprises providing a structure 1 2 adapted for the temporary or permanent introduction into a patient. The structure 1 2 comprises a preferably non- porous base material 14 having a surface 1 6 and is configured, for example, as a stent (such as a vascular stent) . The structure 1 2 and the base material 1 4 have been described in detail above, and for brevity, such details will not be repeated here. Stainless steel, nitinol, tantalum, polylactic acid, polyglycolic acid and biodegradable materials are particularly preferred as the base material 1 4 of the structure 1 2. The method of the present invention further comprises the steps of attaining a desired roughness or texture on the surface 1 6 of the base material 14 of the structure 1 2, and positing a layer 1 8 of a bioactive material directly upon the roughened or textured surface 1 6 of the base material 14. A wide range of bioactive materials useful in the layer 1 8 has been disclosed in detail above; again, for brevity, such detail will not be repeated. Paclitaxel, a taxane or another paclitaxel analogue, estrogen and estrogen derivatives are particularly preferred as bioactive materials in the layer 1 8. The method of manufacturing a medical device 10 according to the present invention is characterized in that the resulting medical device 10 does not require or is free of any additional coating or layer atop the layer 1 8 of bioactive material. The method of the present invention therefore does not include any steps in which the bioactive material is covered by or contained within a time-release or containment layer. While the method of the present invention contemplates the use of a base material 1 4 which itself comprises a plurality of layers or constituents, such an arrangement may not be preferred in the practice of the present invention. In any event, it would be the outermost one of such plural layers or constituents which possesses the roughened or textured surface 1 6 on which the layer 1 8 of bioactive material is posited directly. The step of directly positing the layer 1 8 of bioactive material on the roughened or textured surface 1 6 of the base material 1 4 can be carried out in any convenient manner. The structure 1 2 (or suitable portion thereof) can be dipped or soaked in an appropriate solution of the desired bioactive material, and the solvent of the solution evaporated to leave a layer 1 8 of the bioactive material on the roughened or textured surface 1 6 of the base material 14. Preferably, however, the positing step is carried out by spraying a solution of the bioactive material on the roughened or textured surface 1 6 of the base material 14 of the structure 1 2 and allowing the structure 1 2 to dry. While spraying may have a relatively low efficiency in transferring the bioactive material to the roughened or textured surface 1 6, it is adequate for the purposes of the present invention. By way of example, paclitaxel (the particularly preferred bioactive material in the present invention) can be posited by spraying an ethanolic solution of it on the roughened or textured surface 1 6 of the base material 1 4. The solution conveniently contains about 2 to about 4 mg of paclitaxel per ml of ethanol. (The ethanol should be 100% USP grade or equivalent, not denatured alcohol or 95% ethanol.) Taking a stent of 1 5mm in length and 3 mm in diameter as typical, having a textured, gross outer surface area on the order of 25 mm 2 , spraying can be readily carried out to posit about 5 to about 500 μg, preferably 50 to 1 50 μg, of paclitaxel on the roughened or textured surface 1 6 of the base material 14. Perhaps less than about 1 % of the paclitaxel is ultimately posited from solution onto the textured surface 1 6. The selection of suitable solvents and concentrations for other bioactive materials, or the selection of other techniques for positing other bioactive materials directly upon the roughened or textured surface 1 6, should be well within the skill of those in the art in view of the present disclosure. Any experimentation required should be minimal, particularly in view of the extensive testing required before devices of this type can be distributed in the U.S. The surface 1 6 of the base material 14 of the structure 1 2 can be roughened or textured in any convenient manner, such as by etching. Preferably, however, the surface 1 6 is roughened or textured by abrading, for example, by abrading with an abrasive grit 24 comprising at least one of sodium bicarbonate (USP), calcium carbonate, aluminum oxide, colmanite (calcium borate), crushed glass, crushed walnut shells, or mixtures of these or other abrasive particulates. Such roughening or texturing is most easily carried out by placing the medical device 1 0 on a mandrel 20 in a position such that abrasive grit 24 delivered from a nozzle 22 impinges on the surface 1 6. The initial surface of the base material prior to roughening or texturing may be smoother than the desired surface roughness, or it may be even rougher. The grit size and feed rate of the abrasive grit 24, the structure of the nozzle 22, the pressure at which the abrasive grit 24 is delivered from the nozzle 22, the distance of the surface 1 6 from the nozzle 22 and the rate of relative movement of the medical device 1 0 and the nozzle 22 are all factors to be considered in achieving an appropriate desired roughness or texture of the surface 1 6 of the base material 1 4 of the structure 1 2. By way of non-limiting example, when the base material 1 4 is stainless steel, the abrading step can be carried out with an abrasive grit 24 having a particle size of about 5 microns (5 μm) to about 500 microns (500 μm). More preferably, the abrading step is carried out with sodium bicarbonate (USP) having a nominal particle size of about 50 microns (50 μm), with approximately 50% greater than 40 microns (40 μm) and approximately 1 % greater than 1 50 microns (1 50 //m). Such abrading is preferably carried out with the sodium bicarbonate or other abrasive grit 24 delivered at a pressure under flow of about 5 to about 200 PSI (about 34 to about 1 380 KPa), most preferably about 100 PSI (about 690 KPa). Such abrading is also preferably carried out with the sodium bicarbonate or other abrasive grit 24 delivered at a grit feed rate of about 1 to about 1 000 g/min, most preferably about 1 0 to about 1 5 g/min. The carrier gas or propellent for delivery of the abrasive grit is preferably nitrogen, air or argon, and most preferably nitrogen, although other gases may be suitable as well. When the medical device 1 0 is configured as disclosed above, the distance from the outlet of the nozzle 22 to the center of the mandrel 20 can be about 1 to about 1 00 mm. A preferred nozzle 22 is the Comco Microblaster; when employed, the preferred distance from the outlet of the nozzle 22 to the center of the mandrel 20 is about 5 to about 10 mm. The Paasche LAC #3 is also useful as the nozzle 22. To provide a uniform roughening or texturing of the surface 1 6 of the base material 14 of the structure 1 2, it is highly desirable that relative movement of the surface 1 6 and the nozzle 22 be provided during abrasion of the surface 1 6. Any pattern of motion which achieves the desired uniformity of roughness or texture may be employed. It is preferred that such motion entail both longitudinal or lengthwise movement along the structure 1 2 and circumferential movement or repositioning about the structure 1 2. Repeated longitudinal movement with repeated passes at different circumferential positions is most preferable. More particularly, abrading of the surface 1 6 can entail from 1 to about 50 axial passes per circumferential position, while the number of circumferential positions for such axial passes can range from about 4 to an unlimited number of circumferential positions. This last is achieved by continuous relative rotation of the surface 1 6 and the nozzle 22. The sweep rate of the nozzle 22 along the surface 1 6 can range from about 1 to about 70 mm/sec for the particular stent dimensions disclosed above. When the base material 14 of the structure 1 2 is stainless steel, and the abrasive grit 24 is 50 micron sodium bicarbonate (USP), a particularly preferred combination of abrading conditions is: Nozzle 22: Comco Microblaster Propellant: Nitrogen gas Pressure: 1 20 PSI (828 KPa) (under flow) Spray plan: 8 equally-spaced circumferential positions 4 axial passes per circumferential position Sweep rate: About 1 6 mm/sec Grit feed rate: About 0.1 5 to 0.30 g/sec Nozzle outlet to mandrel center: about 5 to 10 mm When abrading is carried out in this manner, a roughened or textured surface 1 6 is obtained which is thought to have a mean surface roughness (that is, a mean height of surface features) of about 10 //in. (about 250 nm) and a surface roughness range between about 1 //in. and about 1 00 //in. (about 25 nm and about 2.5 μm). Such a surface 1 6 is capable of retaining on it a highly substantial portion of bioactive material posited directly on it without requiring any additional covering or containment layer. More particularly, the adhesion of paclitaxel to two types of stainless steel, grit abraded stents was compared to its adhesion to stents of those types whose surfaces had instead been plasma treated prior to the direct deposition of paclitaxel thereon (control stents). The coated stents of both types, that is, medical devices 1 0 of the present invention and control stents, were then subjected to a physical adhesion test which simulated the rate at which paclitaxel would be delivered during introduction and deployment of the stents in clinical use. The adhesion test involved passing each stent through a water-filled guiding catheter of appropriate diameter and inflating the balloon catheter to expand each stent to its intended diameter. The stents are already mounted before coating. The amount of paclitaxel remaining on each stent was then measured by spectrometry and compared to the amount of paclitaxel initially posited on each stent. Stents having surfaces 1 6 roughened or textured by abrasion with different abrasive grits 24 retained 84.1 ± 10.2% of the paclitaxel originally applied, while stents having plasma treated surfaces retained only 44.3 ± 8.7% of the paclitaxel originally applied (p <0.0001 ). This appears to demonstrate the successful retention of the layer 1 8 of bioactive material on the roughened or textured surface 1 6 of the base material 1 4 of the structure 1 2 of the medical device 10 of the present invention. In view of the foregoing disclosure, those skilled in the art should readily be able to perform any trial-and-error testing to obtain the optimal processing conditions for any desired combination of particular base materials 14 and bioactive materials. Such testing simply requires roughening or texturing the surface 1 6 of a particular base material 14 in a selected manner, applying a layer 1 8 of a particular bioactive material to the roughened or textured surface 1 6 and measuring the retention of bioactive material on the roughened or textured surface 1 6 after clinical introduction and deployment has been mimicked. It should be clear that the present invention provides a medical device 10 and method for manufacturing the same which is particularly advantageous over prior devices and methods for making such devices. The time and cost of manufacture of the medical device of the present invention are minimized by the absence of any steps to incorporate the bioactive material in a containment layer, or to apply a containment or time-release layer over the bioactive material. The particularly preferred use of sodium bicarbonate as the abrasive to provide roughness or texture to the surface of the base material of the structure is advantageous in the low toxicity of the sodium bicarbonate to production workers, the ease of product and waste cleanup, and the biocompatibility of any residual sodium bicarbonate. These are important advantages in their own right, but incidentally also reduce the time and cost for manufacture of the medical device 1 0. The details of the construction or composition of the various elements of the medical device 1 0 of the present invention not otherwise disclosed are not believed to be critical to the achievement of the advantages of the present invention, so long as the elements possess the strength or mechanical properties needed for them to perform as disclosed. The selection of any such details of construction are believed to be well within the ability of one of even rudimentary skills in this area, in view of the present disclosure. For practical reasons, however, most embodiments of the medical device 10 of the present invention should probably be considered to be single-use devices, rather than being reusable. Industrial Applicability The present invention is useful in the performance of various surgical procedures and in the manufacture of devices for the performance of various surgical procedures, and therefore finds applicability in human and veterinary medicine. It is to be understood, however, that the above-described device is merely an illustrative embodiment of the principles of this invention, and that other devices and methods for using them may be devised by those skilled in the art, without departing from the spirit and scope of the invention. It is also to be understood that the invention is directed to embodiments both comprising and consisting of the disclosed parts. In particular, it is contemplated that only part of a medical device 1 0 according to the present invention need be coated with bioactive material. It is further contemplated that different parts of a medical device 1 0 could be coated with different bioactive materials. It is also to be understood that various parts, recesses, portions, sides, segments, channels, and the like of the device can be posited with the bioactive material either singly or in combination with other bioactive, coating, or layering materials. This can be done to further control the release of the bioactive material to the delivery site. Such configurations are contemplated and disclosed in U.S. Patents No. 5,380,299; 5,609,629; 5,824,049; 5,873,904; 6,096,070; 6,299,604 and are incorporated by reference herein. Likewise, presently pending patent applications claiming priority to these patents such as Serial Nos. 08/956,71 5; 09/027,054; and 09/850,691 are also contemplated and incorporated by reference herein. As previously suggested, the medical device of the present invention can also include channels, grooves, recesses, indentations, projections, buildups, and the like to increase the surface area of the device to which the bioactive material can be posited therein.

Claims: Claims 1 . A medical device for introduction into a patient, wherein at least part of the surface of the device is treated to produce a roughened, uneven, unsmooth, or textured surface, and wherein bioactive material is formed on at least said part of the surface. 2. The medical device according to claim 1 , wherein the degree of treatment is controlled to provide sufficient adhesion of the bioactive material to the surface. 3. A medical device comprising: a structure adapted for introduction into a patient, the structure comprising a base material having at least one of a roughened, uneven, unsmooth, or textured surface; and a layer of a bioactive material posited directly upon the at least one surface of the base material of the structure. 4. The medical device according to claim 3, wherein the base material of the structure comprises at least one of: stainless steel, tantalum, titanium, nitinol, gold, platinum, inconel, iridium, silver, tungsten, or another biocompatible metal, or alloys of any of these; carbon or carbon fiber; cellulose acetate, cellulose nitrate, silicone, polyethylene terephthalate, polyurethane, polyamide, polyester, polyorthoester, polyanhydride, polyether sulfone, polycarbonate, polypropylene, high molecular weight polyethylene, polytetrafluoroethylene, or another biocompatible polymeric material, or mixtures or copolymers of these; polylactic acid, polyglycolic acid or copolymers thereof, a polyanhydride, polycaprolactone, polyhydroxybutyrate valerate or another biodegradable polymer, or mixtures or copolymers of these; a protein, an extracellular matrix component, collagen, fibrin or another biologic agent; or a suitable mixture of any of these. 5. The medical device according to claim 3, wherein the bioactive material of the layer comprises at least one of: paclitaxel, a taxane or other paclitaxel analogue; estrogen or estrogen derivatives; heparin or another thrombin inhibitor, hirudin, hirulog, argatroban, D-phenylalanyl-L-poly-L-arginyl chloromethyl ketone, or another antithrombogenic agent, or mixtures thereof; urokinase, streptokinase, a tissue plasminogen activator, or another thrombolytic agent, or mixtures thereof; a fibrinolytic agent; a vasospasm inhibitor; a calcium channel blocker, a nitrate, nitric oxide, a nitric oxide promoter or another vasodilator; an antimicrobial agent or antibiotic; aspirin, ticlopdine or another antiplatelet agent; vascular endothelial growth factor (VEGF) or analogues thereof; colchicine or another antimitotic, or another microtubule inhibitor; cytochalasin or another actin inhibitor; a remodeling inhibitor; deoxyribonucleic acid, an antisense nucleotide or another agent for molecular genetic intervention; a cell cycle inhibitor (such as the protein product of the retinoblastoma tumor suppressor gene, or analogues thereof); GP llb/llla, GP Ib-IX or another inhibitor or surface glycoprotein receptor; methotrexate or another antimetabolite or antiproliferative agent; an anti-cancer chemotherapeutic agent; dexamethasone, dexamethasone sodium phosphate, dexamethasone acetate or another dexamethasone derivative, or another anti-inflammatory steroid; prostaglandin, prostacyclin or analogues thereof; an immunosuppressive agent (such as cyclosporine or rapamycin); an antibiotic (such as streptomycin), erythromycin or vancomycin; dopamine, bromocriptine mesylate, pergolide mesylate or another dopamine agonist; 60 Co, 192 lr, 32 P, 1 1 ln, 90 Y, 99m Tc or another radiotherapeutic agent; iodine-containing compounds, barium-containing compounds, gold, tantalum, platinum, tungsten or another heavy metal functioning as a radiopaque agent; a peptide, a protein, an enzyme, an extracellular matrix component, a cellular component or another biologic agent; captopril, enalapril or another angiotensin converting enzyme (ACE) inhibitor; ascorbic acid, alphatocopherol, superoxide dismutase, deferoxyamine, a 21 - aminosteroid (lasaroid) or another free radical scavenger, iron chelator or antioxidant; angiopeptin; a 14 C-, 3 H-, 131 l-, 32 P- or 36 S-radiolabelled form or other radiolabelled form of any of the foregoing; or a mixture of any of these. 6. The medical device according to claim 3, wherein the at least one surface of the base material of the structure has a mean surface roughness of about 1 0 //in. (about 250 nm) and a surface roughness range between about 1 //in. and about 100 //in. (about 25 nm and about 2.5 μm). 7. The medical device according to claim 3, wherein the medical device does not require or is free of any additional coating or layer atop the layer of bioactive material. 8. A medical device comprising: a structure adapted for introduction into a patient, the structure comprising a base material having at least one of a roughened, uneven, unsmooth, or textured surface, the structure being configured as a vascular stent and the base material comprising at least one of stainless steel, nitinol, and an alloy of nickel and titanium; and a layer of a bioactive material posited directly upon the at least one surface of the base material of the structure, the bioactive material comprising paclitaxel; wherein the medical device does not require any additional coating or layer atop the layer of bioactive material; and wherein the at least one surface of the base material of the structure has a mean surface roughness of about 10 //in. (about 250 nm) and a surface roughness range between about 1 / in. and about 100 //in. (about 25 nm and about 2.5 μm). 9. A method of manufacturing a medical device comprising the steps of: providing a structure adapted for introduction into a patient, the structure comprising a base material having a surface; roughening or texturing the surface of the base material of the structure; and positing a layer of a bioactive material directly upon the roughened or textured surface of the base material of the structure; the method being characterized in that the resulting medical device does not require any additional coating or layer atop the layer of bioactive material. 10. The method according to claim 8, wherein the method is carried out with a base material comprising at least one of: stainless steel, tantalum, titanium, nitinol, gold, platinum, inconel, iridium, silver, tungsten, or another biocompatible metal, or alloys of any of these; carbon or carbon fiber; cellulose acetate, cellulose nitrate, silicone, polyethylene terephthalate, polyurethane, polyamide, polyester, polyorthoester, polyanhydride, polyether sulfone, polycarbonate, polypropylene, high molecular weight polyethylene, polytetrafluoroethylene, or another biocompatible polymeric material, or mixtures or copolymers of these; polylactic acid, polyglycolic acid or copolymers thereof, a polyanhydride, polycaprolactone, polyhydroxybutyrate valerate or another biodegradable polymer, or mixtures or copolymers of these; a protein, an extracellular matrix component, collagen, fibrin or another biologic agent; or a suitable mixture of any of these. 1 1 . The method according to claim 8, wherein the method is carried out with a bioactive material of the layer comprising at least one of: paclitaxel, a taxane or a paclitaxel analogue or derivative; estrogen or estrogen derivatives; heparin or another thrombin inhibitor, hirudin, hirulog, argatroban, D-phenylalanyl-L-poly-L-arginyl chloromethyl ketone, or another antithrombogenic agent, or mixtures thereof; urokinase, streptokinase, a tissue plasminogen activator, or another thrombolytic agent, or mixtures thereof; a fibrinolytic agent; a vasospasm inhibitor; a calcium channel blocker, a nitrate, nitric oxide, a nitric oxide promoter or another vasodilator; an antimicrobial agent or antibiotic; aspirin, ticlopdine or another antiplatelet agent; colchicine or another antimitotic, or another microtubule inhibitor; cytochalasin or another actin inhibitor; a remodeling inhibitor; deoxyribonucleic acid, an antisense nucleotide or another agent for molecular genetic intervention; GP llb/llla, GP Ib-IX or another inhibitor or surface glycoprotein receptor; methotrexate or another antimetabolite or antiproliferative agent; an anti-cancer chemotherapeutic agent; dexamethasone, dexamethasone sodium phosphate, dexamethasone acetate or another dexamethasone derivative, or another anti-inflammatory steroid; dopamine, bromocriptine mesylate, pergolide mesylate or another dopamine agonist; 60 Co, 192 lr, 32 P, 111 ln, 90 Y, 99m Tc or another radiotherapeutic agent; iodine-containing compounds, barium-containing compounds, gold, tantalum, platinum, tungsten or another heavy metal functioning as a radiopaque agent; a peptide, a protein, an enzyme, an extracellular matrix component, a cellular component or another biologic agent; captopril, enalapril or another angiotensin converting enzyme (ACE) inhibitor; ascorbic acid, alphatocopherol, superoxide dismutase, deferoxyamine, a 21 -aminosteroid (lasaroid) or another free radical scavenger, iron chelator or antioxidant; angiopeptin; a 14 C-, 3 H-, 131 l-, 32 P- or 36 S-radiolabelled form or other radiolabelled form of any of the foregoing; or a mixture of any of these. 1 2. The method according to claim 9, wherein the positing step is carried out by spraying a solution of the bioactive material on the roughened or textured surface of the base material of the structure. 1 3. The method according to claim 9, wherein the roughening or texturing step is carried out by abrading the surface of the base material of the structure. 14. The method according to claim 1 3, wherein the abrading is carried out with an abrasive grit comprising at least one of sodium bicarbonate, calcium carbonate, aluminum oxide, colmanite, crushed glass or crushed walnut shells. 1 5. The method according to claim 1 3, wherein the abrading is carried out with an abrasive grit having a particle size of about 5 microns (5 μm) to about 500 microns (500 μm). 1 6. The method according to claim 1 3, wherein the abrading is carried out with sodium bicarbonate having a nominal particle size of about 50 microns (50 μm). 1 7. The method according to claim 1 3, wherein the abrading is carried out with an abrasive grit delivered at a pressure under flow of about 5 to about 200 PSI (about 34 to about 1 380 KPa). 1 8. The method according to claim 1 3, wherein the abrading is carried out with an abrasive grit delivered at a grit feed rate of about 1 to about 1000 g/min. 1 9. The method according to claim 1 3, wherein the abrading is carried out so as to yield a roughened or textured surface on the base material of the structure having a mean surface roughness of about 1 0 //in. (about 250 nm) and a surface roughness range between about 1 //in. and about 1 00 //in. (about 25 nm and about 2.5 μm). 20. The product of the method of claim 9.

Inventors: BATES BRIAN L, BOURDEAU WILLIAM J, CHOULES BRIAN D, FEARNOT NEAL E, PURDY JAMES D, RAGHEB ANTHONY O, STEWART JOSEPH M IV, BATES, BRIAN, L., BOURDEAU, WILLIAM, J., CHOULES, BRIAN, D., FEARNOT, NEAL, E., PURDY, JAMES, D., RAGHEB, ANTHONY, O., STEWART, JOSEPH, M., IV
Applicants: COOK INC, MED INST INC, COOK INCORPORATED, MED INSTITUTE, INC.
Application year: 2001
Main classification: A61L31
IPC codes: A61F2, A61K31, A61L27, A61L29, A61L31, A61P9, A61P35