ALKALI SILICATE-POLYISOCYANATE COMPOSITES

Abstract: A process for preparing alkali silicate-polyisocyanate composites without catalyst separation. The process involves blending a catalyst and a polyisocyanate to form a first component, and bending an alkali silicate and water to form a second component. The first and second components are then mixed together to form a reactive mixture that reacts to form a hardened composite. The progression of the reaction proceeds without excessive foaming, high exotherms, or the release of an offensive odor. Sodium silicate - polyisocyanate composites prepared according to the above process, and a process for using the alkali silicate - polyisocyanate composites to consolidate and seal various types of formations in mining tunneling, and related construction projects are also disclosed.

Description: ALKALI SILICATE - POLYISOCYANATE COMPOSITES Technical Field This invention relates to alkali silicate - polyisocyanate composites, and, more particularly, to a process for preparing alkali silicate - polyisocyanate composites that proceeds without catalyst separation. Background of the Invention Alkali silicate - polyisocyanate composites are frequently used in mining, tunneling, and related construction projects to consolidate and seal various types of formations. The conventional method of preparing alkali silicate - polyisocyanate composites involves mixing a first component, which typically comprises an alkali silicate, water, and a catalyst, with a second component, which typically comprises a polyisocyanate. After the first and second components are mixed together, the reaction proceeds to form a hardened composite according to the following reaction scheme: (I) Upon mixing, the reaction begins when some of the polyisocyanate reacts with the water to produce polyurea and gaseous carbon dioxide. (II) Next, the in-situ formed carbon dioxide reacts instantaneously with the A 2 O portion of the alkali silicate to produce A 2 C0 xH 0 (where A represents an alkali metal), while the Si 2 0 portion of the alkali silicate reacts to form polysilicic acid. (III) As the reaction progresses, heat is released, and the remaining polyisocyanate is trimerized. Unfortunately, the conventional method described above has one major defect. In particular, the high density of the alkali silicate tends to cause the catalyst to separate out from the alkali silicate-water-catalyst mixture. To minimize catalyst separation, the mixture may be mixed immediately prior to use. However, this may be difficult to do in confined areas where this mixture is often used. In addition, because catalyst separation reduces the activity of the catalyst, it is difficult to determine how much catalyst needs to be added to the reactive mixture. To counteract this problem, a surfactant may be added to the alkali silicate- water-catalyst component to keep the catalyst in solution. However, the addition of a surfactant tends to cause excessive foaming in the reaction system, thereby reducing the physical properties of the resulting composite. While catalyst separation is the predominate problem associated with preparing alkali silicate-polyisocyanate composites, several other factors must be considered when preparing such composites. For example, the catalyst used in the preparation of the composite must not contribute to the formation of an excessive amount of carbon dioxide. The formation of an excessive amount of carbon dioxide tends to cause foaming, thereby reducing the physical properties of the resulting composite. Additionally, because alkali silicate - polyisocyanate composites are frequently prepared and used in confined spaces, the exotherm for the reaction preferably should not exceed about 100°C. For the same reason, it is also preferable for the reaction to proceed without giving off an offensive odor. Therefore, what is needed is a process for preparing alkali silicate - polyisocyanate composites that proceeds without catalyst separation, excessive foaming, high exotherms, or the release of an offensive odor. Summary of the Invention Accordingly, the present invention provides for a process of preparing sodium silicate - polyisocyanate composites that proceeds without catalyst separation, excessive foaming, high exotherms, or the release of an offensive odor. To overcome deficiencies in the prior art, the present invention takes the novel approach of incorporating the catalyst into the polyisocyanate component, instead of incorporating the catalyst into the alkali silicate-water component. Incorporation of the catalyst into the polyisocyanate component prevents separation of the catalysts in the reaction mixture. More particularly, the process of the present invention involves blending a catalyst and a polyisocyanate to fonn a first component, and blending an alkali silicate and water to form a second component. After blending, the first and second components are then mixed together to form a reactive mixture that reacts to form a hardened composite. Further, the present invention also provides for sodium silicate - polyisocyanate composites that are prepared by blending a catalyst and a polyisocyanate to form a first component, and blending an alkali silicate and water to form a second component. After blending, the first and second components are then mixed together to form a reactive mixture that reacts to form a hardened composite. In addition, the present invention also includes a process for consolidating and sealing various types of formations in mining, tunneling, and related construction projects. This process involves blending a catalyst and a polyisocyanate to form a first component, and blending an alkali silicate and water to form a second component. After blending, the first and second components are then mixed together to form a reactive mixtare. This reactive mixture is then introduced into a formation, and allowed to react to fonn a hardened composite that consolidates and/or seals the formation. Brief Description of the Drawings Figure 1 is a graph showing the temperature profiles of the reaction systems as a function of time. Detailed Description of the Preferred Embodiment In one embodiment, the present invention provides for a process of preparing sodium silicate - polyisocyanate composites. This process involves blending a catalyst and a polyisocyanate to form a first component, and blending an alkali silicate and water to fonn a second component. The first and second components are then mixed together to fonn a reactive mixture that reacts to form a hardened composite. Advantageously, the process of the present invention proceeds without catalyst separation. In another embodiment, the present invention provides for sodium silicate - polyisocyanate composites that are prepared by blending a catalyst and a polyisocyanate to fonn a first component, and blending an alkali silicate and water to form a second component. After blending, the first and second components are then mixed together to form a reactive mixture that reacts to form a hardened composite. In yet another embodiment of the present invention, the composites prepared according to the present invention may be used to consolidate and/or seal various types of formations in mining, tunneling, and related construction projects. In this embodiment, a catalyst and a polyisocyanate are blended to form a first component, and an alkali silicate and water are blended to form a second component. After blending, the first and second components are then mixed together to form a reactive mixture. This reactive mixture is then introduced, into a formation, and allowed to react to form a hardened composite that consolidates and/or seals the formation. The catalyst used in the present invention may comprise any number of conventionally available catalysts that are stable in polyisocyanantes and promote the reaction of the polyisocyanate component with the alkali silicate and water component. Preferably, the catalysts comprises an amine catalyst that has a relatively low activity, does not cause the exotherm for the reaction to exceed about 100°C, does not contribute to the production of a strong odor, or cause the production of an excessive amount of carbon dioxide. More preferably, the catalyst comprises JEFFCAT® DMDEE (2,2'- dimorpholinodiethylether) (commercially available from the Huntsman Corporation, Houston, Texas). Advantageously, JEFFCAT® DMDEE is stable in polyisocyanantes, promotes the reaction of the polyisocyanate component with the alkali silicate and water component, does not cause excessive foaming, high exotherms, or the release of an offensive odor. The polyisocyanate used in the present invention may comprise any number of polyisocyanates, including, but not limited to, toluene diisocyanates (TDI), diphenylmethane diisocyanate (MDI) - type isocyanates, and prepolymers of these isocyanates. Preferably, the polyisocyanate component has at least two aromatic rings in its structure, and is a liquid product. Polymeric isocyanates having a functionality greater than about two are preferred. More preferably, the polyisocyanate component comprises Rubinate®M, a polymeric diphenylmethane diisocyanate (commercially available from Huntsman ICI Chemicals, LLC, Geismar, Louisiana). The alkali silicate used in the present invention may comprise any number of alkali silicates, including, but not limited to, sodium silicate and potassium silicate. Preferably, the alkali silicate comprises sodium silicate with a Si0 2 : Na 2 O weight ratio from about 1.60 to about 3.22. More preferably, the sodium silicate has a SiO 2 : Na 2 0 weight ratio from about 2.0 to about 3.0. The following examples are illustrative of the present invention, and are not intended to limit the scope of the invention in any way. Example 1 (Comparative) 62.7 grams of Sodium Silicate M (commercially available from the PQ Corporation, Valley Forge, Pennsylvania), with a weight ration of Si0 2 /Na 2 0= 2.58, 49.3 Be', 2.31 grams of water, and 0.90 grams of DABCO® DMP-30 (commercially available from Air Products and Chemicals, Inc., Allentown, Pennsylvania) were mixed in a paper cup. Then, 46.05 grams of Rubinate® M were quickly added to the sodium silicate- water-catalyst mixture, as the mixture was stirred with a tongue depressor. The mixture was then poured into a cylindrical plastic container, and stirring was continued. After the material exothermed, the mixture was allowed to cool to room temperature. The plastic container was then peeled away from the resulting solid composite. The solid composite was then placed in a humidity cabinet for three days. After three days, the composite was crushed in an Instron tester to determine its physical properties. Example 2 62.7 grams of Sodium Silicate M and 2.31 grams of water were mixed in a paper cup. 46.05 grams of Rubinate® M and 0.56 grams of JEFFCAT® DMDEE were mixed in a second paper cup. The isocyanate-catalyst component was then quickly added to the sodium silicate-water component, and the reaction components were stirred with a tongue depressor. The reaction components were then transfened to a cylindrical plastic container, and stining was continued. After the material exothermed, the material was allowed to cool to room temperature. During the preparation of the composite, no catalyst separation was observed. In addition, the excessive production of carbon dioxide, and the release of a strong odor was also not observed. The plastic container was then peeled away from the resulting solid composite. The solid composite was then placed in a humidity cabinet for three days. After three days, the composite was crushed in an Instron tester to determine its physical properties. The results of the Instron testing for the composites made in Examples 1 and 2 are summarized in Table 1. Table 1 Table 1 shows that the physical properties of the composite prepared according to the present invention (Example 2) are comparable to the physical properties of the composite prepared according to conventional methods known in the art (Example 1). This result demonstrates that the incorporation of the catalyst into the polyisocyanate does not adversely alter the physical properties of the resulting composite. Example 3 In order to monitor the temperature of the reaction systems described in Examples 1 and 2, an additional composite sample was prepared for each reaction system, using the same methods disclosed above, except that only one-third of each of the reaction components was used. The temperature of the reaction systems was monitored by a thermocouple, beginning at the time of mixing, and ending shortly after the reaction systems had exotheraied. The temperature data was then graphed to show the temperature profile for each of the reaction systems. (Figure 1) Figure 1 shows that the temperature profile of the reaction system prepared according to the present invention (Example 2) is comparable to the temperature profile of the reaction system prepared according to conventional methods known in the art (Example 1). This result shows that the incorporation of the catalyst into the polyisocyanate does not adversely alter the progression of the reaction, or produce undesirably high exotherms. The temperature profile for the reaction system prepared according to die present invention (Example 2) shows that the exotherm for the reaction was less than 100°C. Although illustrative embodiments have been shown and described, a wide range of modification, changes, and substitution is contemplated in the foregoing disclosure. In some instances, some features of the disclosed embodiments may be employed without a corresponding use of the other features. Accordingly, it is appropriate that the appended claims be construed broadly and in a mamier consistent with the scope of the invention.

Claims: Claims What is claimed is: 1. A process for preparing alkali silicate - polyisocyanate composites comprising: a. mixing a catalyst with a polyisocyanate to form a first component; b. mixing an alkali silicate with water to form a second component; and c. mixing the first and second component to form a reactive mixture that reacts to form a hardened composite. 2. The process of claim 1, wherein the catalyst comprises 2,2'-dimorpholinodiethylether. 3. The process of claim 1, wherein the alkali silicate comprises sodium silicate. 4. The process of claim 3, wherein the sodium silicate has a weight ratio of SiO 2 to Na 2 O from about 1.6 to about 3.32. 5. The process of claim 3, wherein the sodium silicate has a weight ratio of Si0 2 to Na 2 O from about 2.0 to about 3.0. 6. The process of claim 1, wherein the polyisocyanate comprises a polymeric diphenylmethane diisocyanate with a functionality greater than about two. 7. The process of claim 1, wherein the exothenn for the reactive mixture is less than about 100°C. 8. A process for preparing alkali silicate - polyisocyanate composites where the catalyst does not separate out of the reactive mixture comprising: a. mixing a catalyst with a polyisocyanate to form a first component; b. mixing an alkali silicate with water to form a second component; and c. mixing the first and second component to form a reactive mixture that reacts to form a hardened composite. 9. The process of claim 8, wherein the catalyst comprises 2,2'-dimo holinodiethylether. 10. The process of claim 8, wherein the alkali silicate comprises sodium silicate. 11. The process of claim 10, wherein the sodium silicate has a weight ratio of Si0 2 to Na 2 0 from about 1.6 to about 3.22. 12. The process of claim 10, wherein the sodium silicate has a weight ratio of Si0 2 to Na 2 O from about 2.0 to about 3.0. 13. The process of claim 8, wherein the polyisocyanate comprises a polymeric diphenylmethane diisocyanate with a functionality greater than about two. 14. The process of claim 8, wherein the exothenn for the reactive mixture is less than about 100°C. 15. A process for consolidating and sealing various types of formations in mining, tunneling, and related construction projects comprising: a. mixing a catalyst with a polyisocyanate to form a first component; b. mixing an alkali silicate with water to form a second component; c. mixing the first and second component to form a reactive mixture; and d. introducing the reactive mixture into the fonnation, and allowing the reactive mixture to react to form a hardened composite. 16. The process of claim 15, wherein the catalyst comprises 2,2'- dimoφholinodiethylether. 17. The process of claim 15, wherein the alkali silicate comprises sodium silicate. 18. The process of claim 17, wherein the sodium silicate has a weight ratio of Si0 2 to Na 2 0 from about 1.6 to about 3.22. 19. The process of claim 17, wherein the sodium silicate has a weight ratio of SiO 2 to Na 2 0 from about 2.0 to about 3.0. 20. The process of claim 15, wherein the polyisocyanate comprises a polymeric diphenylmethane diisocyanate with a functionality greater than about two. 21. The process of claim 15, wherein the exotherm for the reactive mixture is less than about 100°C. 22. An alkali silicate - polyisocyanate composite that is prepared by: a. mixing a catalyst with a polyisocyanate to form a first component; b. mixing an alkali silicate witii water to fonn a second component; and c. mixing the first and second component to form a reactive mixture that reacts to form a hardened composite. 23. The composite of claim 22, wherein the catalyst comprises 2,2'- dimorpholinodiethylether. 24. The composite of claim 22, wherein the alkali silicate comprises sodium silicate. 25. The composite of claim 24, wherein the sodium silicate has a weight ratio of Si0 2 to Na 2 O from about 1.6 to about 3.32. 26. The composite of claim 24, wherein the sodium silicate has a weight ratio of Si0 2 to Na 2 O from about 2.0 to about 3.0. 27. The composite of claim 22, wherein the polyisocyanate comprises a polymeric diphenylmethane diisocyanate with a functionality greater than about two. 28. The composite of claim 22, wherein the exotherm for the reactive mixture is less than about 100°C.

Inventors: GRIGSBY ROBERT ALLISON JR, GRIGSBY, ROBERT, ALLISON, JR.
Applicants: HUNTSMAN SPEC CHEM CORP, HUNTSMAN PETROCHEMICAL CORPORATION
Application year: 2001
Main classification: C08G18
IPC codes: C08G18, C08G83