Article comprising a substrate containing silicon and a barrier layer which functions as a protective/thermal barrier coating

Abstract: A barrier layer for a silicon containing substrate comprises an alkaline earth aluminosilcate and an additive component capable of forming a reaction product with silica.

Description: The present invention relates to an article comprising a substrate containing silicon and a barrier layer which functions as a protective environmental and/or thermal barrier coating which inhibits the formation of gaseous species of Si, particularly Si(OH) x when the article is exposed to a high temperature, aqueous (water and/or steam) environment and, more particularly, a barrier layer having an additive component which is capable of forming a reaction product with free silica thereby prohibiting a reaction between free silica and the barrier coating. Ceramic materials containing silicon and metal alloys containing silicon have been proposed for structures used in high temperature applications as, for example, gas turbine engines, heat exchangers, internal combustion engines, and the like. A particularly useful application for these materials is for use in gas turbine engines which operate at high temperatures in aqueous environments. It has been found that these silicon containing substrates can recede and lose mass as the result of formation of volatile Si species, particularly Si(OH) x and SiO when exposed to high temperature, aqueous environments. For example, silicon carbide when exposed to a lean fuel environment of approximately 1 ATM pressure of water vapor at 1200°C will exhibit weight loss and recession at a rate of approximately 6 mils per 1000 hrs. It is believed that one possible reaction mechanism involves oxidation of the silicon carbide to form silica and carbon monoxide and/or carbon dioxide on the surface of the silicon carbide followed by reaction of the silica with steam to form volatile species of silicon such as Si(OH) x . Other mechanisms are possible such as direct oxidation of SiC to Si(OH) x species by steam. A barrier coating for silicon containing substrates which would form a reaction product with the silica created during the oxidation of the silicon carbide and thus inhibit the formation of volatile species of silicon, namely, Si(OH) x and SiO, is known. In accordance with the invention, an additive is made to the barrier layer which additive reacts with any free silica. This prohibits reaction between silica and the barrier layer which results in a low melting point problem. Free silica occurs from two sources: (1) deposits on the surface of the barrier layer from the environment, i.e. sand, and (2) because the barrier layer works well, oxidation of the silicon containing substrate beads to silica which is stable because the barrier layer prevents water from getting to that surface. The US-A-5 985 470 explains a coating system for a substrate containing a silicon-based material, such as silicon carbide-containing ceramic matrix materials containing silicon carbide and used to form articles exposed to high temperatures, including the hostile thermal environment of a gas turbine engine. The coating system includes a layer of barium strontium aluminosilicate (BSAS) as a bond coat for a thermal-insulating top coat. As a bond coat, the BSAS layer serves to adhere the top coat to a SiC-containing substrate. The BSAS bond coat,exhibits sufficient environmental resistance such that, if the top coat should spall, the BSAS bond coat continues to provide a level of environmental protection to the underlying SiC-containing substrate. The teaching of JP 61 068 380 A shows an IR radiator film which is formed on an oxide-bearing surface of a sintered SiC substrate to form an IR radiator. Thus, an unpressed sintered SiC substrate contg. 1.0 % of wt. B and 2.0 % of wt. free C, and having a d. of 3.1 g/cm 3 was impregnated with a 1 % of wt. alumina sol. contg. 2 g CaCl 2 1.00 mL, dried at 110° for 1 h, and heated at 1400° for 8 h to form an oxide surface. A mixt. of cordierite 40, MnO 2 36, Fe oxide 12, Co oxide 6, and Cu oxide 6 % of wt. was pre-fired at 110° for 1 h, ground, mixed with Et cellulose and carbitol acetate, pasted on the oxide surface of the substrate, and heated at 1150° for 1 h to form an IR radiator for heating. A barrier layer for a silicon containing substrate which inhibits the formation of gaseous species of silicon when exposed to a high temperature aqueous environment comprises a calcium alumina silicate is discussed by the EP-A-1 044 946. A barrier layer comprises alumina silicate having a composition of CaO, Al 2 O 3 and SiO 2 . Accordingly, it is the principle object of the present invention to provide an article comprising a silicon containing SUbstrate with a barrier layer which includes an additive component capable of forming a reaction product with free silica and thereby inhibit the formation of reactions between the barrier layer components and silica. Further objects and advantages of the present invention will appear hereinbelow. The problems are solved by the teaching according to the independent claims. Particular developments are given in the dependent claims. The present invention relates to an article comprising a silicon containing substrate having a barrier layer on the substrate, wherein the barrier layer functions to both inhibit the formation of undesirable gaseous species of silicon when the article is exposed to a high temperature, aqueous environment and to provide thermal protection such as exists in a gas turbine combustion environment. By high temperatures is meant the temperature at which the Si in the substrate forms Si(OH) x and/or SiO in an aqueous environment. By aqueous environment is meant a water and/or steam environment. The silicon containing substrate is preferably a ceramic or metal alloy containing silicon. The barrier layer in accordance with the present invention comprises an aluminosilicate selected from the group consisting of barium aluminosilicate, strontium aluminosilicate and barium strontium aluminosilicate and an additive component capable of forming a reaction product with free silica. In accordance with the present invention the aluminosilicate is alkaline earth based such as barium strontium aluminosilicate comprising 0.75 BaO·0.25 SrO·Al 2 O 3 ·2SiO2. The additive component in accordance with the present invention is selected from the group consisting of Al 2 O 3 , BaO·6Al 2 O 3 , BaO·Al 2 O 3 , SrO·6Al 2 O 3 , SrO·Al 2 O 3 and mixtures thereof. The alkaline earth based aluminosilicate plus additive can also be referred to as non-stoichiometric BAS, BSAS, or SAS in that it is sub-stoichiometric with respect to silica. The barrier layer in accordance with the present invention has an increased capacity for silica over barrier layers heretofore known. By the addition of the additive component, roughly 32 more silica may be tolerated when compared to a barium strontium aluminosilicate barrier layer without the additive component. Said barrier layer comprises up to 50 % by wt. of said additive component, balance essentially barium strontium aluminosilicate or up to 30 % by wt. of said additive component. Said additive component is Al 2 O 3 up to 30 % by wt. or up to 30 % by wt. BaO·6Al 2 O 3 or SrO·6Al 2 O 3 , comprises from about 10 to 25 % by wt. BAO·6Al 2 O 3 or SrO·6Al 2 O 3 , from about 40 % by wt. BaO·Al 2 O 3 or SrO·Al 2 O 3 , or from about 10 to 25 BaO·Al 2 O 3 or SrO·Al 2 O 3 , balance essentially barium strontium aluminosilicate. Further advantages, characteristics and details of the invention are apparent from the following detailed description of preferred embodiments of the invention with reference to the attached drawings. Figures 1 through 3 are photomicrographs showing high resolution electron microprobe images and compositional maps of a barrier layer coating of the present invention. Figure 4 is a high resolution electron microscope image of the microstructure of Figures 1 through 3. The present invention relates to an article comprising a silicon containing substrate and a barrier layer, wherein the barrier layer inhibits the formation of gaseous species of silicon when the article is exposed to a high temperature, aqueous environment by preventing water from reaching the silicon containing surface and by reducing oxidation of that surface. In addition, the present invention also contains an additive in the barrier layer to react with any silica formed to prevent reactions between the free silica and the barrier layer. According to the present invention, 'the silicon containing substrate may be a silicon containing ceramic substrate or a silicon containing metal alloy. In a preferred embodiment, the silicon containing substrate is a silicon containing ceramic material as, for example, silicon carbide, silicon nitride, silicon carbon nitride, silicon oxynitride and silicon aluminum oxynitride. In accordance with a particular embodiment of the present invention, the silicon containing ceramic substrate comprises a silicon containing matrix with reinforcement such as fibers, particles, and the like and, more particularly, a silicon carbide based matrix which is fiber-reinforced. Particularly suitable ceramic substrates are a silicon carbide coated silicon carbide fiber-reinforced silicon carbide particle and silicon matrix, a carbon fiber-reinforced silicon carbide matrix and a silicon carbide fiber-reinforced silicon nitride matrix. Particularly useful silicon-metal alloys for use as substrates for the article of the present invention include molybdenum-silicon alloys, molybdenum-silicon-boron alloys, niobium-silicon alloys, and other Si containing alloys having a coefficient of thermal expansion compatible with the barrier layer of the present invention. Barrier layers in the article of the present invention are aluminosilicate selected from the group consisting of alkaline earths such as barium aluminosilicate, strontium aluminosilicate and barium strontium aluminosilicate layers with additive component capable of forming a reaction product with free silica. In accordance with a preferred embodiment of the present invention the barrier layer is a barium strontium aluminosilicate comprising 0.75 BaO·O.25SrO·Al 2 O 3 ·2SiO 2 . The additive component in the barrier layer is selected from the group consisting of Al 2 O 3 , BaO·6Al 2 O 3 , BaO·Al 2 O 3 , SrO·6Al 2 O 3 , SrO·Al 2 O 3 and mixtures thereof. The preferred composition of the barrier layer depends on the particular additive component used. In a preferred embodiment of the present invention, the barrier layer comprises up to 50% by weight of the additive component with the balance essentially barium strontium aluminosilicate. A preferred barrier layer comprises up to 30% by weight of the additive component. It has been found that when Al 2 O 3 is used as the additive component, the Al 2 O 3 may be present up to 30 and preferably from about 10 to 25 % by wt.. While it is preferred to add as much of the additive component as possible so as to maximize the formation of the silica and additive reaction product, the upper limit of the additive component is limited in that the coefficient of thermal expansion of the barrier layer must be compatible with the silicon containing substrate material. Thus, depending on the chemical composition of the additive component, the maximum of each additive component in the barrier layer will vary. As noted above, when Al 2 O 3 is the additive component, the barrier layer may contain up to 30 % by wt. Al 2 O 3 . When BaO·6Al 2 O 3 is the additive component, the barrier layer may likewise contain up to 30 % by wt. BaO·6Al 2 O 3 , and preferably between about 10 to 25 percent BaO·6Al 2 O 3 . When BaO·Al 2 O 3 is used as the additive component, the additive component may be present in an amount up to 40 % by wt. and, preferably, between 25 to 35 % by wt.. When SrO·6Al 2 O 3 is the additive component, the barrier layer may likewise contain up to 30 wt.% SrO·6Al 2 O 3 , and preferably between about 10 to 25 wt.% SrO·6Al 2 O 3 . When SrO·Al 2 O 3 is used as the additive component, the additive component may be present in an amount up to 40 wt.% and, preferably, between 25 to 35 wt.%. Again, as noted above, it is important to maintain compatability between the coefficient of thermal expansion of the silicon containing substrate and the barrier layer. The coefficient of thermal expansion of the barrier layer should be within ± 3.0 ppm per degrees centigrade of the coefficient of thermal expansion of the silicon containing substrate. The barrier layer should be present in the article at a thickness of greater than or equal to about 0.5 mils, preferably between about 3 to about 30 mils and ideally between about 3 to about 5 mils. The barrier layer may be applied to the silicon based substrate by any suitable manner known in the art. The advantages in the article of the present invention will become clear from consideration of the following example. Example A silicon containing substrate was coated with a barrier layer of barium strontium aluminosilicate comprising 0.75 BaO·0.25SrO·Al 2 O 3 ·2SiO 2 having an additive component o'f 15 Al 2 O 3 . Figures 1 through 4 show high resolution electron microprobe images and compositional x-ray maps for barium, strontium, aluminum, and silicon along with analyses of each phase present in atomic percent composition at the interface between a SiC/SiC composite and the barium strontium aluminosilicate coating plus 15% alumina additive after 100 hrs. exposure in air at 1350°C. Phase "A" (see composition in Table 1) is a thin silica layer forming on the silica former and having the composition SiO 2 . Above the silica, phases "B" and "C" (see Table 1) are aluminum silicates having a nominal composition of AlSi 4 O 18 or ½Al 2 O 3 ·4SiO 2 . It is expected that ½Al 2 O 3 ·4SiO 2 would be very refractory and have a melting point greater than 1700°C based on the three phase Al 2 O 3 ·BaO·SiO 2 diagram (Figure 556, "Phase Diagrams for Ceramists", M. Resor - Editor, The American Ceramic Society , Columbus, Ohio). The 1.2 to 1.6% Ba and 0.1 to 0.2 % Sr seen in the ½Al 2 O 3 ·4SiO 2 phase could lower the melting point slightly but it would still remain substantially above 1600°C. Phase "D" is an aluminum silicate having the nominal composition Al 6 Si 2 O 12 which is 3Al 2 O 3 ·2SiO 2 and is commonly known as mullite. Mullite is also a very refractory material having a melting point above 1800°C (see the above reference). The 0.1% Ba seen in phase "D" (see Table 1) is expected to have very little effect on the melting point of the mullite. Finally, phase "E" (see Table 1) is the barium strontium aluminosilicate plus alumina additive that represents the present invention. The example shows that the reaction between the invention and a silica former under high temperature oxidizing conditions results in the formation of high temperature refractory phases rather than low temperature phases such as barium aluminosilicate plus silica which has a melting point of about 1300°C (see above reference, Figure 4544). Atomic Composition Percentages of Phases A, B, C, D, E Figures 1-4 Phase A%(O) A%(Al) A%(Si) A%(Sr) A%(Ba) A 66.4 0.9 32.5 0.0 0.3 B 64.6 7.4 26.3 0.2 1.6 C 64.8 7.0 26.8 0.1 1.2 D 62.0 27.7 10.1 0.0 0.1 E 59.9 16.7 15.4 2.1 5.9

Claims: An article comprising : a substrate comprising silicon; and a barrier layer comprising an alkaline earth aluminosilicate selected from the group consisting of barium aluminosilicate, strontium aluminosilicate and barium strontium aluminosilicate with an additive component capable of forming a reaction product with free silica, said additive component is selected from the group consisting of Al 2 O 3 , BaO·6Al 2 O 3 , BaO·Al 2 O 3 , SrO·6Al 2 O 3 , SrO·Al 2 O 3 , and mixtures thereof. An article according to claim 1, wherein said aluminosilicate is barium strontium aluminosilicate comprising 0.75BaO 0.25 SrO·Al 2 O 3 2SiO 2 . An article according to claim 1 or 2 wherein said barrier layer comprises up to 50 % by wt. of said additive component, balance essentially barium strontium aluminosilicate. An article according to claim 1 or 2 wherein said barrier layer comprises up to 30 % by wt. of said additive component, balance essentially barium strontium aluminosilicate. An article according to claim 1 or 2 wherein said additive component is Al 2 O 3 up to 30 % by wt. An article according to claim 5 wherein said barrier layer comprises from 10 to 25 % by wt. Al 2 O 3 , balance essentially barium strontium aluminosilicate. An article according to claim 1 or 2 wherein said additive component is up to 30 % by wt. BaO·6Al 2 O 3 or SrO·6Al 2 O 3 . An article according to claim 1 or 2 wherein said additive component comprises from 10 to 25 % by wt. BaO·6Al 2 O 3 or SrO·6Al 2 O 3 , balance essentially barium strontium aluminosilicate. An article according to claim lor 2 wherein said additive component comprises up to 40 % by wt. BaO·Al 2 O 3 or SrO·Al 2 O 3 , balance essentially barium strontium aluminosilicate. An article according to claim 1 or 2 wherein said additive component comprises from 25 to 35 % by wt. BaO·Al 2 O 3 or SrO·Al 2 O 3 , balance essentially barium strontium aluminosilicate.

Inventors: BRENNAN JOHN J, CHIN STEPHEN, EATON HARRY E JR, BRENNAN, JOHN J., CHIN, STEPHEN, EATON, HARRY E., JR.
Applicants: UNITED TECHNOLOGIES CORP CORP, UNITED TECHNOLOGIES CORPORATION CORPORATION OF THE U.S.A.
Application year: 2001
Main classification: C04B41
IPC codes: C23C26, C04B35, C04B41, F01D5, C23C22, C23C4, C23C30, F02K1, C23C18