COOL FORMING OF SPLINED TRANSMISSION HUBS

Abstract: A method for cold forming splined transmission hubs is provided. A blank (10) with an inner surface and an outer surface is secured on a tool insert support member (100). The tool insert support member (100) has an internal spline tooth profile (110) machined into it. A forming roller (120) is inserted inside the blank and then moves radially under pressure until it contacts an inner surface of the blank. A set of teeth (111) are created on the outer surface of the blank (10) and the blank (10) is rotated relative to the forming roller (120) to form an oil reservoir on the inner surface of the blank.

Description: COOL FORMING OF SPLINED TRANSMISSION HUBS Field of the Invention The invention relates to hubs for automotive transmissions. More particularly, this invention relates to a one-step production method for cold forming a hub of an automotive transmission. Description of the Related Art Flow forming of transmission components, such as clutch housings, is a common manufacturing process. Typically, a tubular shell is provided from a stamped disc, and internal drive spline teeth are roll formed while maintaining a smooth and constant outer diameter. In axial roll forming, a cup-shaped blank is mounted on a shaped mandrel, and a roll formed tool moves axially to press the metal to the tooth shape on the mandrel, essentially one tooth at a time. The mandrel is rotated to present the unworked surface to the roll form to allow the entire inner surface to be splined. United States Patent 5,515,955 discloses such a cold forming process to generate spline teeth in a torque converter. And United States Patent 5,384,949 discloses a multi-step cold forming process for forming a clutch housing with an internal radial spline, a torque transmitting tube portion and an axially extending drive portion. Cold forming a series of teeth in the thickened outer rim portion of a starter ring gear is disclosed in United States Patents 5,152,061, 5,203,223, 5,237,744 and 5,404,640. h United States Patent 5,404,640 there is an indication that where the teeth are totally cold formed, tight tolerances are difficult to achieve and an additional cutting step is required after the cold forming step is completed. This additional step adds cost and cycle time to the manufacturing process. The existing methods are limited to housings with internal splines, or housings with external splines that must be subsequently machined or broached to achieve acceptable tolerances. An oil reservoir or dam, typically present to supply lubricant between the spline teeth and contacting clutch plates, is typically machined into housings in a separate and subsequent metal removal step. Summary Of The Invention The invention describes a method for cold forming a transmission hub from a blank having an outer surface and an inner surface using a tool insert support member having a spline tooth portion and a reservoir portion including a forming roller. The. method includes the steps of positioning the blank axially with the spline tooth portion of the tool insert support member, engaging the spline tooth portion with the outer surface of the blank, exerting a radial pressure on the blank forcing the blank into engagement with the spline tooth portion, creating a set of teeth on the outer surface of the blank; and rotating the blank relative to the forming roller to form an oil reservoir on the inner surface of the blank. Brief Description Of The Drawings Advantages of the invention will be readily appreciated as the same becomes better understood by reference to the following detailed description when considered in connection with the accompanying drawings, wherein: Figure 1 is a cross-sectional view of a steel cylindrical blank; Figure 2 is a top view of the steel cylindrical blank; Figure 3 is a cross-sectional view of the forming tool setup; Figure 4 is a perspective, cross-sectional view of a blank illustrating its insertion into a supporting tool insert having a predetermined tooth profile; Figure 5 is a perspective, cross-sectional view according to the invention whereby a forming roller travels vertically and horizontally against the inside of the blank to cold form the material; Figure 6 is a perspective view of the hub manufactured according to the invention; and Figure 7 is a cross-sectional side view, partially cut away, of the hub of Figure 6. Detailed Description Of The Preferred Embodiment As shown in Figure 1, a cup-shaped blank 10 is provided having an internal step, defined in part by gentle radii R, Ri and R . The blank 10 has two diameters defined by an outer diameter D 0 and an inner diameter Dj. The blank 10 includes an outer surface 12 and an inner surface 14. A bottom surface of blank 10 is indicated at 16. The blank 10 is a circular disk that is mounted onto a mandrel or die and is drawn into the shape by well-known techniques. As shown in Figure 2, a pair of circular holes 20 are drilled or otherwise punched out of a bottom surface 16 of the blank 10, the purpose of which will be explained later. The blank 10 is preferably formed from steel, which is capable of being cold formed. In the forming procedure, the blank 10 is positioned in a tool insert support member 100, as shown in Figures 3, 4, and 5. The tool insert support member 100 is inserted into an opei ing (not shown) of a lower tool member 102. The opening of the lower tool member 102 may be adjusted to receive tool insert support members 100 of different sizes. Similarly, a shaft 104 raises and lowers the lower tool member 102 to accommodate different sized tool insert support members 100. As a result, the same lower tool member 102 may be used for cold forming blanks 10 of various shapes. The blank 10 is secured to the tool insert support member 100 by pins (not shown) that are inserted into the lower tool member 102 through the circular holes 20. The tool insert support member 100 has a spline tooth profile 110 permanently machined into its interior. A preformed blank is created by moving a forming roller 120 into the interior volume of the blank 10 and abutting same on the interior surface 14. The forming roller 120 is a component of an upper tool member 124, and is mounted in an opening (not shown) therein. As with the lower tool member 102, the opening of the upper tool member 124 is sized to accommodate rollers of various sizes. Preferably, the upper tool member 124 and the lower tool member 102 are two pieces. However, a one-piece tooling member may also be used. The outer diameter of the forming roller 120 is typically 40-60% of the outer diameter of the blank 10. However, smaller roller diameters can be used to maximize the amount of cold forming per revolution. The forming roller 120 first moves in a vertically downward direction, until it is positioned just above the bottom surface 16 of the blank 10. The forming roller 120 does not make contact with the bottom surface 16 because surface removal of material undesirable. Next, the forming roller 120 moves under radial pressure to force the steel material on the outer surface 12 of the blank 10 into a spline tooth profile 110 of the tool insert support member 100. The contoured shape of the forming roller 120 includes a protrusion 125 and recess 126. The protrusion 125 is pressed against the inner surface 14 of the blank 10 to cold form an oil dam or inner oil reservoir 112 on the inner surface 14 of the blank while the spline teeth 111 are formed on the outer surface 12 of the blank 10. The recess 126 allows material to flow past the protrusion 125 to limit the width of the oil reservoir 112 by creating a wall 113. An edge lip 127 is also provided on the foiming roller 120. The edge lip 127 forms a strengthening shoulder region 140 on the blank 10. During the forming operation, the tool insert 100 is rotated by an electric motor drive or other suitable device. Rotational speeds are normally above 600 rpm, although slower speeds can also be used. The forming roller 120 is free running upon contacting the blank 10 as pressure is applied, h an alternative embodiment, the forming roller 120 may also rotate. Regardless, once the forming roller 120 contacts the rotating blank when a force 121 is applied thereto laterally, the forming roller 120 forces the blank 10 into shape. As shown in Figures 6 and 7, the spline teeth 111 are formed on the outer surface 12 of the blank 10 and the oil reservoir 112 is cold formed on the inner surface 14 of the blank 10. Because the oil reservoir 112 and the spline teeth 111 are created at the same time, no further machining steps are required. In addition, a strengthening shoulder 140 that interconnects the spline teeth 111 is formed along the outer periphery of the blank 10. The invention has been described in an illustrative manner. It is to be understood that the terminology, which has been used, is intended to be in the nature of words of description rather than of limitation. Many modifications and variations of the invention are possible in light of the above teachings. Therefore, within the scope of the appended claims, the invention may be practiced other than as specifically described.

Claims: WHAT IS CLAIMED IS: 1. A method for cold forming a transmission hub from a cup-shaped blank having an outer surface and an inner surface, the method comprising the steps of: positioning the blank axially within of a tool insert support member having a spline tooth portion; exerting a radial pressure on the blank forcing the blank into engagement with the spline tooth portion thereby forming a set of teeth on the outer surface of the blank; and forming an oil reservoir in the inner surface of the blank. 2. A method as claimed in claim 1 wherein said exerting step and said forming step occur simultaneously. 3. A method as claimed in claim 2 wherein said exerting step and said forming step • includes rotating a fomiing roller relative to said blank to form said oil reservoir and exert said radial pressure. 4. A method as set forth in claim 3 wherein said method includes a step of forming a wall defining a portion of said reservoir. 5. A method as set forth in claim 4 including a step of forming a strengthening lip around a periphery of the blank interconnecting said set of teeth. 6. A method as set forth in claim 4 wherein said wall and strengthening lip are formed simultaneously with said set of teeth and said reservoir. 7. A method as set forth in claim 6 wherein said tool insert support member is rotated in excess of 600 RPM. 8. A method as set forth in claim 3 wherein said forming roller has an outer diameter and said blank has an outer diameter, said outer diameter of the forming roller is 40-60% of the outer diameter of the blank. 9. An apparatus for cold forming a transmission hub as set forth in any preceeding claim, comprising a tool insert support member having a spline tooth portion; a freely rotating forming roller; and a drive for rotating said tool insert support member relative to said forming roller and for moving said forming roller radially and axially relative to said tool insert support member.

Inventors: CZYCHORATZKI GISO, HASTINGS RICHARD JAMES, RICCI LUIGI, CZYCHORATZKI, GISO, HASTINGS, RICHARD, JAMES, RICCI, LUIGI
Applicants: CZYCHORATZKI GISO, HASTINGS RICHARD JAMES, RICCI LUIGI, TESMA INT INC, CZYCHORATZKI, GISO, HASTINGS, RICHARD, JAMES, RICCI, LUIGI, TESMA INTERNATIONAL INC.
Application year: 2001
Main classification: B21D
IPC codes: B21D22, B21D53, F16D13