Method of compounding a multimodal polyethylene composition

Abstract: Method of compounding a multimodal polyethylene composition in a compounding device, wherein the total residence time of the polyethylene composition in the compounding device is at least 1 minute, the total drive specific energy (SEC) applied on the polyethylene composition is from 0.240 to 0.450 kWh/kg, and, optionally, a specific cooling energy (SCC) of at most 0.200 kWh/kg is applied on the polyethylene composition, such that the total specific energy, which is the difference between the total drive specific energy SEC and the specific cooling energy SCC, applied on the polyethylene composition is from 0.220 to 0.330 kWh/kg.

Description: The present invention relates to a method of compounding of multimodal polyethylene compositions and more particularly to a method of compounding a multimodal polyethylene composition comprising a low molecular weight ethylene polymer and a high molecular weight ethylene polymer. Multimodal polyethylene compositions are well known in the art. The term "multimodal" polyethylene compositions refers to the form of the molecular weight distribution curve of the composition, i.e. the appearance of the graph of the polymer weight fraction as function of its molecular weight. When a polymer is produced in a sequential step process, utilising reactors coupled in series and using different conditions in each reactor, the different fractions produced in the different reactors will each have their own molecular weight distribution. When the molecular weight distribution curves from these fractions are superimposed into the molecular weight distribution curve for the total resulting polymer product, that curve will show two or more maxima or at least be distinctly broadened in comparison with the curves for the individual fractions. Such a polymer product, produced in two or more serial steps, is called bimodal or multimodal depending on the number of steps. However, the multimodal polyethylene compositions may alternatively be produced by physical mixing of the different components prepared separately. It is well known in the art that when producing a polymer compound that can be used for the manufacture of different objects, the ingredients thereof, such as the different polymers, additives, etc, should be mixed intimately in order to obtain a compound as homogeneous as possible. Usually, this mixing is done in a compounding device wherein the ingredients are mixed together and the polymers and optionally some of the additives are melted so that intimately mixing can occur. The melt is then extruded into a rod, cooled and granulated. In this form the resulting compound can then be used for the manufacturing of different objects. Although the conventional compounding tools such as tandem mixer-single screw extruders and twin screw extruders, offering residence time in the order of, or shorter than, 1 minute, generally lead to acceptable quality results in compounding polymer compositions, problems are encountered when compounding multimodal polymer compositions, and more particularly multimodal polymer compositions comprising a low molecular weight ethylene polymer and a high molecular weight ethylene polymer. When compounding multimodal polymer compositions, e.g. for the manufacture of pipes, so called « white spots » occur in the compounded material. These white spots have a size of about 10-80 µm and consist mainly of high molecular weight polymer particles that have not been adequately compounded in the composition. In addition to being disfiguring the white spots may adversely influence the strength of the composition. Further, when compounding multimodal polymer compositions, e.g. for the production of film, gel particles with a size of about 0.01-1 mm often occur. These gel particles appear as disfiguring heterogeneities in the finished film and consist mainly of high molecular weight polymer particles that have not been adequately compounded, i.e. dispersed, in the composition. The above described white spots and gel particles are a serious problem in the polymer industry and a solution to the problem would mean the removal of an obstacle to use otherwise superior multimodal polymer compositions. WO 00/01473 A1 provides a polymer mixing device for mixing and homogenisation of polymers by elongational deformation, the device having a casing and a core defining between them a conically tapered mixing space which is divided by circumferential protrusions into slits alternating with chambers, said protrusions being arranged on the core and/or the inner wall of the casing. US patent 6,031,027 aims to overcome this problem by providing a method of compounding a multimodal polymer composition wherein the composition is maintained at a temperature range from 10 °C below to 10 °C above the melting point of the low molecular weight polyethylene polymer during a period from 10 to 60 seconds. Such method needs a very good control of the temperature of the polymer composition and is therefore difficult to execute on the currently used industrial compounding devices. WO 00/24821 relates to an extrusion process of particular multimodal polyethylene compositions using an extruder equipped with a gear pump. However this technology does not permit to obtain very good results with all multimodal compositions, in particular with multimodal compositions rich in low molecular weight polymer. The present invention provides a new method of compounding multimodal polymer compositions which overcomes the above mentioned problems and which permits to obtain a very homogeneous compound which has a reduced level of white spots and/or gels and which has superior mechanical properties. The present invention therefore relates to a method of compounding multimodal polyethylene composition in a compounding device wherein a) the total residence time of the polyethylene composition in the compounding device is at least 1 minute, b) the total drive specific energy (SEC) applied on the polyethylene composition is from 0.240 to 0.450 kWh/kg, c) optionally, a specific cooling energy (SCC) of at most 0.200 kWh/kg is applied on the polyethylene composition, d) the total specific energy, which is the difference between the total drive specific energy SEC and the specific cooling energy SCC, applied on the polyethylene composition is from 0.220 to 0.330 kWh/kg. The present invention is related to the compounding of a multimodal polyethylene composition. For the purpose of the present invention, multimodal polyethylene composition is meant to designate compositions comprising at least a low molecular weight ethylene polymer and at least a high molecular weight ethylene polymer. For the purpose of the present invention the expression « ethylene polymer » comprises ethylene homopolymers and ethylene copolymers comprising at least 90 % by weight of units derived from ethylene. In connection with the present invention the molecular weight of the polymer is defined by way of its melt flow rate, such as measured according to ASTM 1286-90b standard. For a specific type of polymer the higher the value of its melt flow rate, the lower its mean molecular weight. Generally, the low molecular weight ethylene polymer has a melt flow rate MI 2 , measured at 190 °C under a 2.16 kg load according ASTM 1286-90b, of 0.1 to 5000 g/10min, preferably from 100 to 2000 g/10min. Generally, the high molecular weight ethylene polymer has a melt flow rate HLMI, measured at 190 °C under a 21.6 kg load according ASTM 1286-90b, from 0.001 to 10.0 g/10 min, preferably from 0.001 to 1.0 g/10 min. The multimodal polyethylene compositions as determined above comprise generally from 30 to 70 % by weight of the low-molecular ethylene polymer and from 30 to 70 % by weight of the high-molecular ethylene polymer. In the method according to the invention, the total residence time of the multimodal polyethylene composition in the compounding device is preferably at least 3 minutes, most preferably at least 4.5 minutes. Generally, the total residence time of the polyethylene composition in the compounding device does not exceed 15 minutes, preferably not 10 minutes. The total residence time of multimodal polyethylene in the compounding device is calculated based on free volume and fill factor of the compounding device, rate (polymer throughput) and density of the molten polyethylene composition (0.7636 g/ cm 3 at 190°C). The calculated residence time values are confirmed by a manual measurement using a colour tracer introduced at the entry of the compounding device and detected at the exit of the compounding device. In the method according to the invention, the total drive specific energy (SEC) applied on the polyethylene composition is preferably at least 0.325 kWh/kg. Good results have been obtained when the total specific energy (SEC) applied on the polyethylene composition was at least 0.360 kWh/kg. The total drive specific energy (SEC) applied on the polyethylene composition preferably does not exceed 0.415 kWh/kg. Good results have been obtained when the total drive specific energy (SEC) applied on the polyethylene composition did not exceed 0.400 kWh/kg. In the method according to the invention, the total drive specific energy (SEC) applied on the polyethylene composition is the ratio of consumed power in the compounding device, expressed in kW, and the rate of polymer composition throughput in the compounding device, expressed in kg/h. According to a preferred variant of the method according to the invention, the compounding device is equipped with a cooling device such that a specific cooling energy (SCC) can be applied on the polyethylene composition. The specific cooling energy (SCC) applied on the polyethylene composition is calculated from the temperature difference of the cooling medium at the inlet and outlet of the cooling device and the flow rate and specific heat capacity of the cooling medium. In the method according to the invention, the specific cooling energy (SCC) applied on the polyethylene composition is generally lower than 0.145 kWh/kg, most preferably lower than 0.120 kWh/kg. Generally, the specific cooling energy (SCC) applied on the polyethylene composition is at least 0.045 kWh/kg, preferably at least 0.070 kWh/kg, most preferably at least 0,080 kWh/kg. In the method according to the invention, the total specific energy, which is the difference between the total drive specific energy SEC and the specific cooling energy SCC applied on the polyethylene composition, is preferably at least 0.240 kWh/kg, most preferably at least 0.255 kWh/kg. The total specific energy applied on the polyethylene composition does preferably not exceed 0.320 kWh/kg. The compounding device used in the method according the invention can be any equipment that, batchwise or continuously, permits to satisfy the conditions (in terms of residence time and specific energy applied to the multimodal polyethylene composition) of this method. According to a preferred embodiment of the method according to the invention, the compounding device comprises at least one melting zone preceding at least one homogenising zone. By melting zone, it is meant to understand in the present invention, a zone wherein the specific energy applied on the polyethylene composition is kept as low as possible to strictly melt the polymer composition, without any or having as less as possible homogenising efficiency. This strict melting implies that the drive specific energy applied to the polyethylene composition in this melting zone (SEC melting ) is controlled. Generally the drive specific energy applied to the polyethylene composition in the melting zone (SEC melting ) does not exceed 0.260 kWh/kg, preferably not 0.240 kWh/kg. Generally, the drive specific energy applied to the polyethylene composition in this melting zone (SEC melting ) is at least 0.190 kWh/kg, preferably at least 0.220 kWh/kg. The drive specific energy (SEC melting ) is the ratio of consumed power in the melting equipment, expressed in kW, and the rate of polymer composition throughput in the melting zone, expressed in kg/h. The residence time of the polyethylene composition in the melting zone is generally at least 10 seconds, preferably at least 15 seconds. The residence time of the polyethylene composition in the melting zone does generally not exceed 60 seconds, preferably not 45 seconds. Generally, the melt temperature of the polyethylene composition coming out of the melting zone is from 210 to 260 °C, preferably from 220 to 250 °C. Most preferred the melt temperature of the polyethylene composition coming out of the melting zone is from 230 to 240 °C. The melt temperature is measured with a temperature probe immersed 2 centimetres deep in the polymer at the exit of the melting equipment. The average shear rate applied in the melting zone is generally between 30 and 500 s -1 . By homogenising zone, it is meant to understand a zone wherein intensive homogenisation of the multimodal polyethylene composition occurs. The temperature of the polyethylene composition entering the homogenising zone is generally from 210 to 260 °C, preferably from 220 to 250 °C. Most preferred the temperature of the polyethylene composition entering the homogenising zone is from 230 to 240 °C. The residence time of the polyethylene composition in the homogenising zone is generally at least 1 minute, preferably at least 1.5 minutes. Most preferably, the residence time in the homogenising zone is at least 3 minutes. The residence time of the polyethylene composition in the homogenising zone does generally not exceed 14 minutes, preferably not 9 minutes. The drive specific energy applied to the polyethylene composition in the homogenising zone (SEC homogenising ) does generally not exceed 0.200 kWh/kg, preferably not 0.175 kWh/kg. Generally, the drive specific energy applied to the polyethylene composition in this homogenising zone (SEC homogenising ) is at least 0.100 kWh/kg, preferably at least 0.125 kWh/kg. The drive specific energy SEC homogenising is the ratio of consumed power in the homogenising equipment, expressed in kW, and the rate of polymer composition throughput in the homogenising zone, expressed in kg/h. Preferably, cooling is applied in this homogenising zone, generally through circulation of refrigerant in the envelope of the homogenising device, which at least partially compensate the specific drive energy consumption in this homogenising zone. This specific cooling energy (SCC homogenising ) is generally at least 0.045 kWh/kg, preferably at least 0.070 kWh/kg and most preferably at least 0.080 kWh/kg. This specific cooling energy does generally not exceed 0.145 kWh/kg, preferably not 0.120 kWh/kg. Generally, the melt temperature of the polyethylene composition coming out of this homogenising zone will remain below the degradation threshold. Preferably, the melt temperature of the polyethylene composition coming out of this homogenising zone is in range of 265 to 295°C and most preferably at about 275 to 285 °C. The melt temperature is measured with a temperature probe immersed 2 centimetres deep in the polymer at the exit of the homogenising equipment. The average shear rate applied in the homogenising zone is preferably kept as low as possible. Generally, the average shear rate in the homogenising zone does not exceed 100 s -1 , preferably not 50 s -1 . In this preferred embodiment of the method according to the invention, the compounding device is preferably a tandem assembly of a melting equipment and homogenising equipment. Both equipments can be exemplified by a continuous mixer or by an extruder, which may be of the single screw or twin screw type. Most preferred is a compounding device comprising a continuous mixer as melting device and an extruder, especially a single screw extruder, as homogenising device. When the homogenising device is a single screw extruder it may be constituted of classical conveying elements or it may comprise dispersive mixing elements developing shear and/or elongation stress. Preferably elements are used developing elongation stress with an application time of at least 0.5 seconds. The compounding device used in the method according to the invention may comprise other elements currently used in known compounding devices, such as pelletizers, filters, gear pumps. In the method according to the invention a compounding device comprising no gear pump is preferably used. The method according to the invention is very suitable for compounding multimodal polyethylene compositions comprising from 30 to 70 % by weight of low molecular ethylene polymer having a melt flow rate MI 2 , measured at 190 °C under a 2.16 kg load according ASTM 1286-90b, of 1 to 5000 g/10min, preferably from 100 to 2000 g/10min, and from 30 to 70 % by weight of high molecular weight ethylene polymer having a melt flow rate HLMI, measured at 190 °C under a 21.6 kg load according ASTM 1286-90b, from 0.001 to 10.0 g/10 min, preferably from 0.001 to 1.0 g/10 min. Such multimodal polyethylene compositions are known in the art, they have for example being disclosed in US 6,136,924 and US 6,225,421. Usually the multimodal polyethylene compositions have a melt flow rate MI 5 , measured at 190 °C under a 5 kg load according ASTM 1286-90b, from 0.01 to 10.0 g/10 min, preferably from 0.1 to 1.0 g/10 min and a density, measured according to ASTM D 792 standard, of 930 to 965 kg/m 3 , preferably of 935 to 960 kg/m 3 . In general, the density of the low molecular weight polyethylene present in the multimodal polyethylene composition is at least 960 kg/m 3 , preferably at least 965 kg/m 3 , most preferably at least 970 kg/m 3 . In general, the density of the high molecular weight polyethylene present in the multimodal polyethylene composition is from 910 to 940 kg/m 3 , preferably from 915 to 935 kg/m 3 . The method according to the invention has been very suitable for compounding multimodal polyethylene compositions comprising from 51 to 65 % by weight of low molecular ethylene polymer having a melt flow rate MI 2 higher than 100 g/10min and a density higher than 970 kg/m 3 and from 35 to 49 % by weight of high molecular weight ethylene polymer having a melt flow rate HLMI from 0.001 to 1.0 g/10 min and a density lower than 928 kg/m 3 . Usual compounding methods, such as single and twin screw extruders do generally not permit to obtain homogeneous compounds of these mixtures. The multimodal polyethylene composition used in the method according to the invention may comprise further ethylene polymers having a melt flow rate different from the low molecular weight and the high molecular weight ethylene polymers. Generally, the total quantity of these ethylene polymers does not exceed 20 %, preferably not 10 %, by weight of the multimodal polyethylene composition. The multimodal polyethylene composition used in the invention is preferably produced in a sequential step process, utilising reactors coupled in series and using different conditions in each reactor, the different fractions produced in the different reactors will each have their own molecular weight. Alternatively, the multimodal polyethylene composition may be produced by physically mixing the different ethylene polymers prepared separately. The multimodal polyethylene composition may also be produced by a combination of both preparation methods. In the compounding method according to the invention, the different ethylene polymers forming the multimodal polyethylene composition may be added to the compounding device at the same time. Alternatively, some of the ethylene polymers or fractions of the different ethylene polymers may be added to the compounding device in a differentiated stage during the compounding process. Figures 1 to 5 schematically represent some possible ways to execute the method according to the invention. In figures 1 to 5, S1, S2 and S3 represent different ethylene polymers, one of which is a high molecular weight ethylene polymer and one of which is a low molecular weight ethylene polymer. In figure 1, a multimodal polyethylene composition comprising 3 different ethylene polymers S1, S2 and S3 (obtained by sequential polymerisation or by physical mixing) is processed in compounding device comprising a melting zone M and a homogenising zone H. In figure 2, the different ethylene polymers S1, S2 and S3 (separately polymerised) are molten in separate melting devices M1, M2 and M3 and mixed together before entering the homogenising zone H. In figure 3, ethylene polymers S2 and S3 (separately polymerized) are molten in separate melting devices M2 and M3, mixed together before entering the homogenising zone and ethylene polymer S1 is molten in melting device M1 before addition to homogenising zone H in a differentiated stage. In figure 4, ethylene polymers S1 and S2 (separately polymerized) are molten in separate melting devices M1 and M2, mixed together before entering the homogenising zone and ethylene polymer S3 (in solid form) is added to homogenising zone H in a differentiated stage. In figure 5, a mixture of ethylene polymers (obtained by sequential polymerisation or by physically mixing) is processed in the compounding device C and ethylene polymer S3 (in solid form) is processed in the compounding device C in a differentiated stage. Additives usually added to polyethylene compositions, such as antioxidants, anti-UV agents, anti-static agents, dispersive aid agents, processing aids, pigments, ... may be added to the multimodal polyethylene composition before or during compounding. The total content of these additives does generally not exceed 10 parts, preferably not 5 parts, by weight per 100 parts by weight of multimodal polyethylene composition. It has been surprisingly found that the addition of from 0.005 to 1 part by weight per 100 parts of multimodal polyethylene composition, of an antioxidant additive comprising a compound of formula wherein R represents an alkyl or an alkenyl chain comprising from 8 to 35 carbon atoms, preferably from 12 to 24 carbon atoms, to the multimodal polyethylene composition permits to improve even more the homogeneity of the resulting multimodal compound so that substantially no gels appear any more. Antioxidant additives responding to formula (I) are well known. Goods results have been obtained with stearyl beta-(3,5-di-t-butyl-4-hydroxyphenyl)propionate (R= C 18 H 37 ). Such additive is for example commercialised under the name of Irganox ®1076. Especially preferred was the addition of an antioxidant additive comprising a compound of formula (I) in combination with a phosphite type antioxidant, more particularly in combination with tris(2,4-di-t-butylphenyl)-phosphite. Very good results were obtained with an antioxidant additive comprising about 20 % by weight of stearyl beta-(3,5-di-t-butyl-4-hydroxyphenyl)propionate and about 80 % by weight of tris(2,4-di-t-butylphenyl)-phosphite. Such antioxidant additive was for example commercialised under the name of Irganox®B900. The method of compounding multimodal polyethylene compositions according to the invention offers the advantage that a homogenous compounded material, also called multimodal compound, is obtained containing a low level of white spots or gels, without substantially any degradation of the polymers present in the composition. The quality of the multimodal compounds obtained with the compounding method described above can be measured according to ISO 13949 (1997) standard. Generally, the method according to the invention permits to obtain a dispersion quotation according to this standard which is smaller than 3, as far as the pigment and the « white spots » are concerned, and even smaller than 1.5, as far as the « white spots » are concerned. The distribution quotation usually is A2-B1, as far as the pigment and the « white spots » are concerned. The method according to the invention permits to obtain a compound comprising a low quantity of gels. A complete gels free quality can be obtained. The presence of gels is quantified by counting the "gels" (manually or with optical cameras) on blown films having a 200 microns thickness made from the compound. The present examples illustrate the method according to the invention. Example 1 (according to the invention) A multimodal polyethylene composition was prepared by polymerisation in two reactors disposed in series. The multimodal composition had a density of 954.0 kg/m 3 and a melt index MI 5 of 0.35 g/10min and comprised : 60.3 part by weight of low molecular weight polyethylene having a density of 975.1 kg/m 3 and a melt index MI 2 of 772 g/10min; 39.7 part by weight of high molecular weight polyethylene (ethylene-hexene copolymer) having a density of 920.2 kg/m 3 and a melt index HLMI of 0.1 g/10min. To this multimodal polyethylene composition were added, for 100 parts of multimodal polyethylene composition, 0.35 part by weight of antioxidant IRGANOX® B225, 0.10 part by weight of calcium stearate and 2.25 parts by weight of carbon black. This additivated composition was extruded on a compounding device comprising a melting zone (single screw extruder, 90mm screw diameter, 24D length) and a homogenising zone (single screw extruder, 90 mm diameter screw, 36D length) according to the conditions specified in table 1. At the end of the compounding device, the resulting compound was passed through a strand pelletizer and pellets of the resulting compound were recuperated and examined. The results obtained are presented in table 2. Example 2 (according to the invention) Example 1 was reproduced under the conditions specified in table 1, by adding to the multimodal composition of example 1, per 100 parts by weight of multimodal polyethylene composition : 0.35 part by weight of antioxidant IRGANOX® B225, 0.25 part by weight of antioxidant IRGANOX® B900, 0.10 part by weight of calcium stearate and 2.25 parts by weight of carbon black. Example 3 and 4 (according to the invention) A multimodal polyethylene composition was prepared by polymerisation in two reactions disposed in series having a density of 955.6 kg/m 3 and a melt index MI 5 of 0.6 g/10min and comprising : 59.5 part by weight of low molecular weight polyethylene having a density of 973.5 kg/m 3 and a melt index MI 2 of 581 g/10min; 40.5 part by weight of high molecular weight polyethylene (ethylene-hexene copolymer) having a density of 930.6 kg/m 3 and a melt index HLMI of 0.2 g/10min. To this multimodal polyethylene composition were added, for 100 parts by weight of multimodal polyethylene composition, 0.35 part by weight of antioxidant IRGANOX® B225, 0.10 part of calcium stearate and 2.25 parts of carbon black. This additivated composition was extruded on the compounding device described in Example 1 according to the conditions specified in table 1. The results obtained are presented in table 2. Comparative Example 4R (not according to the invention) The additivated multimodal composition described in example 1 was extruded on a twin screw extruder (commercial Werner® ZSK 40 extruder, run in adiabatic mode, comprising a twin screw of 40 mm diameter, 26D length) and a strand pelletizer, in the conditions specified in Table 3. The properties of the resulting compound are presented in table 4. Comparative Examples 5R, 6R, and 7R (not according to the invention) The additivated composition described in example 3 was extruded on a twin screw extruder (commercial Werner® ZSK 40 extruder, run with controlled temperature profile, comprising a twin screw of 40 mm diameter, 26D length) and a strand pelletizer, in the conditions specified in table 3. The properties of the resulting compound are presented in Table 4.

Claims: Method of compounding a multimodal polyethylene composition in a compounding device comprising a tandem assembly of a melting equipment and homogenising equipment, wherein a) the total residence time of the polyethylene composition in the compounding device is at least 1 minute, b) the total drive specific energy (SEC) applied on the polyethylene composition is from 0.240 to 0.450 kWh/kg, c) optionally, a specific cooling energy (SCC) of at most 0.200 kWh/kg is applied on the polyethylene composition, d) the total specific energy, which is the difference between the total drive specific energy SEC and the specific cooling energy SCC, applied on the polyethylene composition is from 0.220 to 0.330 kWh/kg. Method according to claim 1, wherein the total residence time of the polyethylene composition in the compounding device is at least 3 minutes. Method according to claim 1 or 2, wherein the total drive specific energy (SEC) applied on the polyethylene composition is from 0.325 to 0.415 kWh/kg and wherein the specific cooling energy (SCC) applied on the polyethylene composition is from 0.045 to 0.145 kWh/kg. Method according to any one of claims 1 to 3, wherein the compounding device comprises at least one melting zone preceding at least one homogenising zone. Method according to claim 4, wherein the drive specific energy applied to the composition in the melting zone (SEC melting ) is from 0.190 to 0.260 kWh/kg. Method according to claim 4 or 5, wherein the temperature of the composition coming out of the melting zone and entering the homogenising zone is from 210 to 260 °C. Method according to any one of claims 4 to 6, wherein the residence time of the polyethylene composition in the homogenising zone is at least 1,5 minutes. Method according to any one of claims 4 to 7, wherein the drive specific energy applied to the polyethylene composition in the homogenising zone (SEC homogenising ) is from 0.100 to 0.200 kWh/kg and wherein a specific cooling energy (SCC homogenising ) from 0.045 to 0.145 kWh/kg is applied on the polyethylene composition in the homogenising zone. Method according to any one of claims 4 to 8, wherein the temperature of the composition coming out of the homogenising zone is from 265 to 295 °C. Method according to any one of claims 4 to 9, wherein the homogenising zone comprises a single screw extruder. Method according to claim 10, wherein the single screw extruder comprises mixing elements developing shear and/or elongation stress. Method according to anyone of claims 1 to 11, wherein from 0.005 to 1 part, per 100 parts of multimodal polyethylene composition, of a antioxidant additive comprising a compound of formula wherein R represents an alkyl or an alkenyl chain comprising from 8 to 35 carbon atoms, is added to the multimodal polyethylene composition. Method according to anyone of claims 1 to 12 wherein the multimodal polyethylene composition has a melt flow rate MI 5 from 0.01 to 10.0 g/10 min and a density of 930 to 965 kg/m 3 and comprises from 30 to 70 % by weight of a low molecular weight ethylene polymer having a melt flow rate MI 2 from 1 to 5000 g/10 min and a density of at least 960 kg/m 3 , and from 30 to 70 % by weight of a high molecular weight ethylene polymer having a melt flow rate HLMI from 0.001 to 10.0 g/10 min and a density of 910 to 940 kg/m 3. Method according to any preceding claim, wherein the average shear rate applied in the homogenising zone does not exceed 100 s -1 , preferably not 50 s -1 .

Inventors: RATY MARIE-FRANCE, RATY, MARIE-FRANCE
Applicants: INNOVENE MFG BELGIUM NV, INNOVENE MANUFACTURING BELGIUM NV
Application year: 2001
Main classification: B29B7
IPC codes: B29B7, B29K23