IMPROVEMENTS IN BUILDING BLOCKS

Abstract: A cementitious mix for preparing a building block wherein the mix includes the ingredients; sand, cement, sawdust and water; wherein said sawdust comprises the greater proportion of the mix constituents; and wherein the dry density of the mix ranges between 700 kg/m<3> and 1500 kg/m<3>.

Description: IMPROVEMENTS IN BUILDINGS BLOCKS BACKGROUND The present invention relates to building blocks and more particularly relates to light weight cement blocks for use in masonry construction having improved strength, shape and appearance characteristics. More particularly the invention relates to construction bricks or blocks which include wood, wood fibre or wood products in the mix. PRIOR ART There are a number of lightweight cement construction blocks available which incorporate sawdust as a constituent along with a predetermined ratio of cement and water. One such construction block is disclosed in US patent 5,241,795 which teaches a building material constructed from paper sludge and waste paper mixed with clay, portland cement and selected resins. The building material described in that patent has unusual compression strength properties which enables elastic deformation of the material under load rather than brittle fracture. That patent also recognises the use of wood fibre materials such as saw dust bound with resins. US patent 5,569,426 teaches the use of a cement block which is formed by mixing sawdust, water, sand and cement such that the sawdust is within the range of 30% - 70% by volume, the sand is within the range of 10% - 40% and the cement is in the range of 10% - 40%. The blocks described in that patent are characterised by the use of sawdust as a primary constituent of the block. There are a number of additional US patents which disclose various building blocks which employ a variety of constituent materials. Examples of these are US patent 4,885,203 and US Patent 5,024,035. US patent 5,782,970 discloses a lightweight concrete product which includes a cement mix which contains sawdust, diatomite, bentonite and lime. The material so formed may be used for the construction of 0 ' 1 n ^* A ~ e panels. Another form of building block is disclosed in US patent 5,890,332. which teaches a reconstituted block modular building system. The reconstituted blocks are positioned horizontally side by side and stacked vertically downwardly. US patent 5,741,589 discloses a woody group material and cement which are combined to form a construction material. The material has finely split pieces of split wood, bamboo or the like. None of the above patents disclose a method of constructing a construction block using a blend of ingredients in which sawdust is the highest proportion ingredient and which includes a finish which is produced by establishing a predetermined slump in the concrete mix. Nor does the prior art teach the -advantages and affects of using different sand types and how that may impact on Strength, Aesthetics, Porosity, and Durability of the blocks. The prior art has to date concentrated merely on the use of wood and wood derivatives in a cementitious mix for making blocks but has not considered to any practical extent, the variations in strength, aesthetics, porosity and durability of the blocks which might be achieved by substantial or subtle changes to the mix proportions and constituents. In relation to strength and durability characteristics, the prior art teaches the use of sand that is clean or washed. That is, very little fines smaller than 150 microns and no fines smaller than 75 microns. Conventional wisdom teaches that good concreting sand tends to have large particle size which varies from approximately 3 mm down to 150 micron. Anything smaller than 150 microns is called Fines. Fines are normally a mixture of clay particles (alumina) or fine silica particles. There may also be other trace elements and organic impurities. Sand mining companies go to a great deal of effort to remove all or most of the fines, so that they can offer to various concrete companies clean washed sand. These companies in turn produce a range of concrete products such as bricks, pipes, dual top panels, concrete foundations etc. Such companies ask for a test certificate on the particle size distribution. This ensures that there are not too many fines, which normally compromise the structural integrity of the product. Cement and aggregate is then added to this washed sand to produce concrete. The prior art makes no reference to the best of the applicant's knowledge to the use and advantages of different sand types. Use of wood and wood products in masonry blocks necessitates consideration of potential termite attack, but the prior art makes no reference to problems raised by the presence of termites or other timber-eating creatures. Previously, the known blocks were constructed in standard regular shaped moulds without much attention paid if any, to overall finish. INVENTION The present invention seeks to provide building blocks and methods of construction of such blocks as an alternative to the known wood based building blocks and to the known methods of construction of such blocks by providing a matrix and applying methods of construction which enhance the strength, aesthetics, porosity, finish and durability and appearance in the finished product. According to one embodiment, the finished block may resemble the rounded appearance of cobblestone with a rock face finish. According to an alternative embodiment the block includes a peripheral border on at least one face and a split rock face finish. According to a further embodiment, the block may include a channel for interlocking and/or a channel for services. According to a preferred embodiment, the dry density of the mix ranges between 909kg/m3 and 1300kg/m3. In its broadest form the present invention comprises; a cementitious mix for preparing a building block wherein the mix includes the ingredients; sand, cement, sawdust and water; wherein said sawdust comprises the greater proportion of the mix constituents; and wherein the dry density of the mix ranges between 800kg/m3 and 1500kg/m3. Preferably the cementitious mix ingredients are mixed in the following proportions; Sawdust: within the range 23 litres to 35 litres (2.3 - 2.9 parts) Sand: within the range 10 litres to 23 litres (1.7 -- 2.3 parts) Cement: lOKg (1 part) Water: within the range 12 litres to 14 litres (1.2 parts) wherein the sand includes fines in a proportion per unit volume greater than 10% which would pass through a 150 micron mesh and wherein the fine sand includes silica and/or clay (alumina). Preferably, the proportion of silica is greater than the proportion of alumina with fine sand whose particulate size falls within the range of 150 microns or less. The mix forms a construction block including at least one outer face in which at least part of said at least one outer face lies in a plane spaced apart from a plane in which the remaining part of said at least one face lies. Said at least one outer face is generally convex outward wherein said at least one part of said outer face provides the construction block with a rock face or cobblestone appearance. The mix when wet may according to one embodiment have a slump within the range 0.5mm to 15mm. According to one embodiment, the construction block includes at least one internal cavity for services and /or a recess for keying or interlocking with adjacent blocks. The construction block is made by pouring said mix when wet into a mould. In another broad form, the present invention comprises: a lightweight construction block formed in a mould from a mix of ingredients which include sand, water and a lightweight aggregate which is mixed according to a predetermined time /temperature regime; wherein the mix is capable of a wet slump during formation within the range of 0.5 to 15mm, the slump resulting in a formation on said construction block which provides the block with at least one generally curved or irregular outer surface on at least one face of the block. In a broad form of the method asnect the oresent invention comprises; a method of producing a construction block from a cementitious mix including the ingredients; sand, cement, sawdust and water; wherein said saw dust comprises the greater proportion of the mix constituents; and wherein the dry density of the mix ranges between 700kg/m3 and 1500kg m3 wherein the method comprises the steps of; a) dry blending said ingredients; b) adding water during or after said dry blending of said ingredients to form a wet mix having a slump within the range of 0.5mm to 15mm; c) placing said wet mix in a mould d) allowing said wet mix to dry for a predetermined period e) removing said mould to expose a formed construction block. The sand includes fine sand whose particulate size falls within the range of less than 150 microns wherein the fine sand includes silica and/or clay (alumina). Preferably, the proportion of silica is greater than the proportion of alumina. Preferably the method includes the step of blending the ingredients in the following proportions; Sawdust: within the range 23 litres to 35 litres (2.3 - 2.9 parts) Sand: within the range 11 litres to 23 litres (1.7 ~ 2.3 parts) Cement: lOKg (1 part) Water: within the range 12 litres to 14 litres (1.2 parts) The method comprises the further step of causing in at least one face of said construction block, a rock face formation in which at least part of said at least one outer face lies in a plane spaced apart from a plane in which the remaining part of said at least one face lies. According to one embodiment the method further comprises introducing into an outer face of said block a peripheral border region. In another broad form of the method aspect the present invention comprises: a method of construction of a lightweight building block wherein the method comprises the steps of : a) selecting a specific type of sand with a predetermined level of clay content for use in a mix to form a construction block; K. takino- a„. predetermined mix of at least sawdust and cement; c) mixing said sand , cement and sawdust according to predetermined proportions with a predetermined quantity of water; d) introducing said mix into a mould; e) allowing said mix to set for a predetermined period; wherein the block produced from said mould has at least one of its faces which are generally curved in appearance, wherein said rock like appearance of at least one face of said block is achieved by selecting a mix which is capable of a predetermined level of slump and removing said mould at a predetermined time during setting of said mix. In a further form of the method aspect the invention comprises: a method of constructing a lightweight building block wherein the method comprises the steps of: a) selecting a specific type of sand with a predetermined level of clay content for use in a mix to form a construction block; b) taking a predetermined quantity of said sand and blending the sand with a predetermined mix of at least a cellulose fibre material and cement; c) mixing said sand , cement and cellulose fibre according to predetermined proportions with a predetermined quantity of water; d) introducing said mix into a mould; e) allowing said mix to set for a predetermined period; wherein the block produced from said mould has at least one of its faces which are rock like in appearance, wherein said rock like appearance of at least one face of said block is achieved by selecting a mix which is capable of a predetermined level of slump. Preferably the method comprises the further step; when at least two blocks are removed from the mould, opposing faces of said at least two blocks undergo slump to an extent that said faces engage whereupon release of said faces results in a block having a rock face appearance on said opposing faces. In a further form the present invention comprises; a lightweight construction block formed in a mould from a mix which includes sand, water and a lightweight aggregate which is mixed according to a predetermined time and mix regime; wherein the mix when wet, has a slump which falls within the range of 0.5 to 20mm; wherein the slump is such that it enables a formation in said construction block which provides a generally convex outward appearance on at least one face of the block; and wherein the block is held in a mould for a time period in the region of 20 - 40 minutes prior to removal of the mould, Preferably, at least two faces of said block are convex outward, wherein said convex faces are formed when said mould is removed. Two opposing faces of adjacent blocks engage during setting of said mix and after slump of the mix, whereupon disengagement between said blocks prior to setting results in each said opposing faces having a rock like appearance. Preferably, the block includes a border about the periphery of said rock face. According to one embodiment the ingredients may be mixed in the following proportions: Sawdust: 29 litres ( 2.9 parts) Sand: 17 litres (1.7 parts) Cement: lOKg (1 part) Water: 12 litres (1.2 parts), and the block includes chemical additives to resist termite attack. The construction block additives for termite resistance may be selected from chemicals such as arsenic, cyanide, boron oxide, barium oxide or other toxic or non-toxic additives. Preferably, the additives are placed in said water and said water is mixed with said saw dust to form a slurry prior to mixing said slurry with cement and sand. In another broad form the present invention comprises; a lightweight construction block including sand, water and a wood fibre aggregate which is mixed according to a predetermined mix regime; wherein the mix prior to setting is capable of a predetermined slump during formation of the block, the slump resulting in a formation on said construction block which provides generally curved faces and with at least one of said faces having a rock face appearance. In another broad form the present invention comprises; a lightweight construction block which includes sand, cement, wood products as fillers or aggregate and additives such that the block is capable of resisting termite attack due to inclusion in the mix of termite resistant chemicals. In another broad form of the method aspect the present invention comprises a method of constructing a lightweight building block wherein the method comprises the steps of: a) selecting a specific type of sand with a predetermined level of clay content for use in a mix to form a construction block; b) taking a predetermined quantity of said sand and blending the sand with a predetermined mix of at least a cellulose fibre material and cement; c) mixing said sand , cement and cellulose fibre according to predetermined proportions with a predetermined quantity of water; d) introducing said mix into a mould; e) allowing said mix to set for a predetermined period; wherein the block produced from said mould has at least one of its faces which are rock like in appearance, wherein said rock like appearance of at least one face of said block is achieved by selecting a mix which is capable of a predetermined level of slump. In another broad form of the method aspect the present invention comprises; a method of constructing a lightweight building block having a rock face appearance on at least one face of the block, wherein the method comprises the steps of: a) selecting a specific type of sand with a predetermined level of clay content for use in a mix to form a construction block; b) taking a predetermined quantity of said sand and blending the sand with a predetermined mix of at least a cellulose fibre material and cement; c) mixing said sand , cement and cellulose fibre according to predetermined proportions with a predetermined quantity of water; d) introducing said mix into a mould; e) allowing said mix to set for a predetermined period; wherein, the block produced from said mould has at least one of its faces which are rock like in appearance, wherein said rock like appearance of at least one face of said block is achieved by selecting a mix which is capable of a predetermined level of slump and allowing opposing faces of said blocks to come in contact as a result of said slump. Preferably, the predetermined level of slump occurs when the block is released from the mould. DETAILED DESCRIPTION The invention will now be described in more detail according to a preferred embodiment and with reference to the accompanying illustrations wherein; Figure 1 shows a typical mould prior to filling with a mix for formation of construction blocks. Figure 2 shows .a typical mould having its mould cavities filled with a mix according to one embodiment of the invention. Figure 3 show ' s a the mould assembly of figure 2 with construction blocks released from the mould according to a preferred embodiment of the invention. Figure 4 shows a mould according to an alternative embodiment in which a mould cavity includes formations which provide formations in blocks such as channels or recesses. Figure 5 shows an alternative block configuration produced from a corresponding mould. Figure 6 shows an alternative block configuration produced from a corresponding mould. Figure 7 shows an alternative block configuration produced from a corresponding mould. Figure 8 shows an alternative block configuration produced from a corresponding mould. Figure 9 shows an arrangement of blocks according to one embodiment including a recess for services and power points light switches and the like. Figure 10 shows an exploded view of a mould wherein a spacer or divider is used to create a border and rock face or cobblestone finish on a face of a brick. Figure 11a shows a block made from the mould assembly of figure 10; and Figure lib shows the block of figure 11a rotated to illustrate the block profile. The invention to be described below with reference to various embodiments is enabled by use of a special blend of selected ingredients which when mixed according to the method aspects of the invention impart properties including durability, structural integrity and aesthetics to the finished construction blocks. The mix is formed from a blend of at least sand, cement, wood or wood derivatives such as saw dust and water. The inventor made particular observations from the behaviour of conventional sand used in known block construction. An assumption which might be made, is that use of the same type of sand blend which would be selected for known block construction would result in similar properties and the same structural characteristics when sawdust was used as an aggregate material in block construction. Sand can have particulate matter which includes, silica, alumina ( clay) which are described as fines. Sand with an unacceptable amount of fines in conventional concrete construction ( i.e. more than 10% that passes through 150 micron mesh) will normally result in a structural compromise to the block. In convention cement block construction, by using clean sand the block will normally demonstrate better compression test results than blocks made using a sand with an excess of fines. The inventor found that the opposite is true where wood based aggregates such as saw dust are used in block construction. When sand was used with fines which would normally be considered to be in excess, the resultant blocks out performed blocks made with the same sand but using an aggregate or filler other than wood based products. Blocks constructed in accordance with the invention using sand having an excess of fines performed better in compression compared to the same blocks constructed using clean sand ( i.e. sand with a minimum of fines). There were also improvements in durability, in that sand that is fine and has more than 10% fines produces a more durable product than its clean or coarse counterpart. The finer particles help to bind the ingredients together. The end result is that there is less crumbling and particle dislodgment. There is however, an upper limit to the percentage of fines as an excess will begin to reverse the gained advantage. Generally, fine sand outperforms coarse sand in block compression tests for blocks made in accordance with the mix described herein . It was found that sand that has in its fines a larger portion of silica particles rather than alumina (clay) particles, performs better in compression tests. Fines are normally a percentage blend of clay particles (alumina) and or silica particles. The presence of very fine silica or clay particles gives sand its fatty or sticky feel. Such sand can be easily compacted and will go hard in time. Sand that is fine or has with it more that 10% fines, produce a product that has less porosity than those sands that are washed or that are coarse. Sand that has with its fines, a small percentage of iron oxide, produces a more desirable colour. These colours range from Yellow Ochre to Orange Ochre through to Red Ochre. Colours can be blended in the moulds to produce a marbling affect. Mottled brick walls can be produced by using various coloured sands in each mix. If the sand doesn't inherit these colours, pigments or oxides need to be added. The Cobblestone or sand stone effect is partly created by carefully selecting the correct sand colour. Preferably, the mix will remain in the mould according to the prevailing drying conditions but this will normally be for a time period between 5 - 45 minutes. In hot dry conditions, the mix stays in the mould for as little as 5 minutes before the moulds are removed. In cold wet conditions, the time period will be as much as 45 minutes. In extreme prevailing drying conditions, these time periods may decrease or increase. The cement constituent of the mix is ordinary off white, white or common grey cement although white cements are preferred. Use of wood products such as sawdust or wood fibre differentiate the construction blocks from conventional masonry blocks. Sawdust has been used in blocks in the past but it is the blend of ingredients as described herein which differentiate the blocks constructed with the mix according to the invention from the known blocks which employ wood based aggregate. There are many types of timbers (sawdust) available but they fall into two broad categories, a) Soft woods and b) Hard woods Soft woods are low-density or light weight timbers. Hard woods are high-density or heavy weight timbers. The inventor found that that low-density timber used in construction blocks significantly outperforms its high-density counterpart in thermal conductivity tests (R rating tests). The density of hard wood ranges from about 750kg/m 3 to 1000kg m 3 . The density of soft woods range from 350 kg/m 3 to 500 kg/m 3 . It was found that low-density timber enhances R-values without significantly compromising structural integrity. Referring to figure! there is shown a typical mould having its mould cavities filled with a mix according to one embodiment of the invention. Mould 1 includes an array of mould cavities 2-13 in which a mix according to a preferred embodiment of the invention is placed. Although the mould shown has 29 cavities it will be appreciated that this is an example only and moulds may be employed with a lesser or greater number of mould cavities. A typical mix for production of a construction block according to the invention will be blended in the following proportions: Sawdust: 29 litres ( 2.9 parts) Sand: 17 litres (1.7 parts) Cement: lOKg (1 part) Water: 12 litres (1.2 parts), such that the dry density will preferably be 900kg/m3. Another mix may comprise the following proportions: SAND: 23 litres by volume SAWDUST 23 litres by volume CEMENT 8 litres by volume or 10 kilos WATER 14 litres by volume. Referring to figure 2 there is shown mould 1 of Figure 1 in which all cavities 2 - 29 are filled with a mix 30 according to a preferred embodiment of the invention. When mix 30 is poured into mould cavities 2- set for a predetermined period which will largely depend upon the prevailing thermal conditions. According to one embodiment the required finish of the blocks will be determined by the design slump. When mould 1 is removed, block walls are unsupported in which case, where the mix is not fully set a slump will occur for each block. The amount of the slump will determine the final shape of the block. Blocks according to one embodiment of the invention having curved outer walls will be described below, although it will be appreciated that a more conventional rectangular block shape may be achieved by allowing mix 30 to stiffen ( dry) such that when released from mould 1 the blocks do not undergo slump. In that case the block walls will be vertical but the block will otherwise demonstrate the strength, durability aesthetic and thermal properties enabled by mix 3. According to one embodiment, the blocks are characterised in that on completion they have a curved appearance on at least one face and in addition a rock face appearance on at least one face, The finished appearance of the blocks is achieved by means of a predetermined mix of constituents which provide a predetermined slump preferably between 0.5 - 15mm which occurs following removal of the mould. The mix for the blocks will typically contain selected sand, water, cement and a filler or aggregate which can be sawdust or wood/cellulose based material as indicated above. Insufficient water in the mix will result in stiffness of the block and too much water will cause collapse of the block upon release from mould 1 and will also interfere with the structural integrity of the blocks. It will however be appreciated by persons skilled in the art that alternative mixes may be used to achieve the finish required and the requisite slump to achieve that finish. The correct mix is achieved by using a specific type of sand having the correct amount of clay content. Insufficient clay content prevents slump whereas too much clay content interferes with the structural integrity of the block under load. The blocks may be constructed according to the following methodology. The dry ingredients for the mix are selected according to requisite proportions which are preferably in accordance with those indicted previously. The mix may be prepared first by dry mixing following which water is added. Alternatively, the water may be placed in a mixer first following which the ingredients such as saw dust, sand and nay additives etc are added The mixing may take place using a conventional mixer or it may be hand mixed where a small quantity is required. Once the required mix has been achieved mix 30 is then introduced into mould 1 which may be single ( ot shown) or multiple cavity as shown in figure 1. From this point in the manufacture of the blocks, the steps taken are critical. Mix 30 is left in the mould for a period which will be in the region of 5- 45 minutes depending upon prevailing weather conditions but would normally be 30 minutes. The duration will largely depend upon the water content. Judgement will be required as to when the moulds should be released. Should mould 1 be released too early, the blocks produced by the mould will slump into a heap and will be unusable. If mould 1 is taken away too late, the cement content will cause the blocks to set and become too stiff to undergo slump, so a curved finish will not be achieved. That in fact may be a desirable result in some cases. Referring to figure 3 there is shown mould 1 with blocks 31 - 38 released from cavities 7, 8, 14, 15, 21, 22, 28, 29 . The figure is abbreviated for clarity, but it will be appreciated that all blocks formed by mix 30 will be released at the same time. Once mix 30 ( see figure 2) has set according to a predetermined time period, blocks may be released from the mould. Mould 1 will normally be placed on a flat surface 39 which will define a bottom surface of each block. Each mould cavity is separated from an adjacent cavity, by a network of walls such as walls 40, 41, 42 and 43 arranged to form the plurality of cavities 2-29 each of which is separated only by the wall thickness. Once a predetermined setting period has elapsed, the mould is released from the blocks in the direction of arrow 44. This exposes the blocks 31 - 38 which are now free standing. Figure 3 shows by way of example two rows of adjacent blocks laid end to end. Leading blocks 38 and 39 are placed such that walls 45 and 46 oppose. It can be seen from the embodiment of figure 3 that opposing walls 45 and 46 and outside walls 47 and 48 are curved. This effect is achieved by removing mould 1 at a predetermined time during setting and while the mix is still wet enough to allow a slump in the block when walls 45 - 48 are unsupported once mould 1 is removed. The same effect will occur in the remaining blocks as they will be fabricated from the same mix. Allowing slump in the block is optional. Accordingly, where it is required that the walls of the blocks produced from the mould remain vertical, the mix will be allowed to stiffen by an increase in the setting period based on environmental conditions at the time of setting. In an alternative embodiment, the blocks are finished with at least one rock face. When blocks are released from mould 1 each block is separated by gaps which result from the thickness of the cavity walls. For example, walls 43 and 49 will create gaps 50 and 51. In the case where the rock face finish is required, gap 51 for example will be critical. The mould cavity wall thickness will typically be between 10 and 25 mm to allow the slump to occur when the mould is removed. Mould walls thinner than 10mm will prevent slump as the blocks released from mould 1 will engage too early so the required slump will not be achieved. Moulds having walls wider than 25 mm will create too large a gap between the opposing faces of the blocks such that the opposing block faces will not contact each other to achieve the rock face finish. When slump occurs as mould is released, opposing walls 45 and 46 engage as these walls displace laterally. When blocks 38 and 39 are eventually separated, the mutual engagement of the opposing wall surfaces results in the rock face appearance described. It is important that sand having the correct clay content be selected and the appropriate cement water / cement ratio be introduced. Once the correct mix is achieved and a mould having an appropriate wall width is selected, the remaining step which is the time the mix remains in the moulds is critical to the desired finish and is a matter of judgement by the manufacturer. Ideally around 30 minutes will be the appropriate setting time. The bricks described above can be nailed or screwed and offer both thermal and insulating properties. Figure 4 shows a mould 60 according to an alternative embodiment in which a mould cavities 61, 62 and 63 respectively include formations 64, 65 and 66 which provide corresponding recesses 67, 68 and 69 in blocks 70, 71 and 72. Figure 5 shows an alternative block configuration produced from a corresponding mould ( not shown) . Blocks 80 - 87 are shown with a horizontal channel which can house water pipes, electrical conduits, steel rods or horizontal bracing. Figure 6 shows an alternative block configuration produced from a corresponding mould. Blocks 90 - 97 each include a grooves 98 approximately 35mm wide and a little over half way through the block to accommodate electrical conduits, water pipes or steel rods for cyclonic conditions and/or vertical bracings. Figure 7 shows an alternative block configuration produced from a corresponding mould. Blocks 100 - 107 each include a large cavities 108 and 109 from top to bottom approximately 100mm in diameter or square. The cavity houses a steel rod and is also filled with high strength concrete for a vertical bracing or increased load bearing. Blocks may contain double cavities as in block 105 or single cavities as in block 100. Figure 8 shows an alternative block configuration produced from a corresponding mould. Blocks 110 - 117 include an electrical housing box 118 placed into the blocks. Blocks 110 may be combined with blocks 90 - 97 shown in figure 6 in which case electrical conduits and other services may be used in conjunction with box 118 as shown for blocks 110 - 117. Electrical housing box 118 maybe placed anywhere along the block and houses light switches, power points, fan switches or the like. An alternative block arrangement was shown in figure 4 and includes grooves 67 - 69 approximately 35mm wide out of one end of the block to house electrical conduits, water pipes, steel rods or vertical bracings. Combinations of the configurations of the above block types may also be achieved. The blocks described may accommodate electrical conduits, power point boxes, water pipes and steel cyclone rods. Block types shown in figures 4, 5 and 6 eliminate the arduous task of cutting channels to house services, which is the normal practice for single skinned structures. Block type shown in figure 8 houses a power point box, which also saves time and expense which would other wise be the case in having to cut out holes to mount a flush type power point or light switch. In an alternative embodiment a block includes a bevelled and split face block with the bevelled and split face on one or more sides, and on the other side or sides either flat or cobble stone. According to an alternative embodiment, a steel, alloy or timber plate 5mm - 20mm wide and 5mm - 50mm deep may be used as a block divider during formation of the blocks. The steel, alloy or timber divider is used which may be flat or triangular. The blocks that are made using type the divider are initially joined. The divider whether it is the flat type or the triangular type creates a weakness where the blocks are split once they have hardened. The grooves left by the dividers create a weakness and prevent the split from running off track. According to an alternative embodiment, a divider may be 10mm-50mm high and 2mm- 18mm thick. Known construction blocks which employ wood products as filler and /or aggregate do not include additives which render the timber products to be free from termite attack. According to one embodiment there is provided a construction block which includes therein an internal membrane or physical barrier which prevents termite attack. An alternative approach is to select timber products which are less prone to termite attack. A further alternative is to utilize chemicals which are termite resistant. Such chemicals may include arsenic, cyanide, boron oxide, barium oxide or other toxic or non-toxic additives. These additives are placed in the water whereupon the sawdust is mixed with the water and allowed to sit for a time whilst the sawdust is 'marinated' with the chemical deterrent. To this water mix, the cement and sand is then added. Figure 9 shows an arrangement of blocks according to one embodiment including a recess for services and power points light switches and the like. Blocks 120 and 121 are laid according to conventional methods. Blocks 120 and 121 have respective recesses 122 and 123 which receive service conduit 124. Service conduit 124 may feed power point or light socket 125. Preferably, power point socket 125 is placed in the mould when the mix is still wet. Blocks 120 and 121 are similar to those described as for Figure 6. Figure 10 shows an exploded view of a mould 126 wherein a spacer or divider 127 is used to create a border and rock face or cobblestone finish on a face of a block. Mould 126 produces blocks 128 and 129 which are initially delivered from mould 126 with spacer 127. disposed therebetween. This keeps apart a border region of the blocks but allows partial face contact between opposing faces 130 and 131 due to opening 132 of spacer 127. Figure 11a shows block 128 made from the mould assembly of figure 10 with face 130 exposed. Block 128 includes border region 133 which is formed by spacer 127. Figure lib shows the block 128 of figure 11a rotated to show its profile. Preferably, the blocks are split when cured. The table below provides examples of block specifications BLOCK SPECIFICATION AND LAYING DIMENSIONS Average Block Size Dry Weight Density Compressive strength Type Mm kg kg m 3 Tonnes 405L x l65h 200w 11.6 909 3.3mpa or 27 tonnes Lightweight 405L x 165h x 200w 16.5 1300 5.3mpa or 45 tonnes Extra Strong 405L x 165h x 200w 7.5 909 3.3mpa or 16 7 tonnes Lightweight 405L x l65h 200w 10.4 1300 5.3mpa or 28 tonnes Extra Strong BLOCK WEIGHT PER m 2 .200mm wide 181 kg/ m 2 Lightweight .200mm wide 260 kg/ m 2 Extra Strong .120mm wide 109 kg/ 2 Lightweight .120mm wide 156 kg/ m 2 Extra Strong TEST RESULTS Compressive tests were performed on blocks made from the mix according to the preferred embodiment of the invention. Blocks tested had dimensions 190mm long, 186mm wide and 168mm high. The results of the compression tests are set out in the table below. TABLE MIX SAND TYPE LOAD TO FAILURE 5 Parts saw dust Course washed sand 144kN 3 Parts sand 5 Parts saw dust Yellow brick layers sand 196kN 3 Parts sand ( All fines) 4 Parts saw dust Washed concreting sand 4 Parts sand ( Common grade) 207kN 4 Parts saw dust Ye -id 4 Parts sand ( All fines ) 281kN 4 Parts saw dust Alternative Yellow brick layers sand 4 Parts sand ( Common grade) 299kN The above tests demonstrate that a mix using saw dust either greater to or equal to the sand content and using sand with a high percentage of fines will deliver higher compressive strength compared to a block formed using washed or equivalent sand. During the tests, the loads were applied normal to horizontal surfaces of the blocks.

Claims: THE CLAIMS DEFINING THE INVENTION ARE AS FOLLOWS: 1 A cementitious mix for preparing a building block wherein the mix includes the ingredients; sand, cement, sawdust and water ; wherein said sawdust comprises the greater proportion of the mix constituents; and wherein the dry density of the mix ranges between 700kg/m3 and 1500kg/m3. 2 A cementitious mix according to claim 1, wherein the ingredients are mixed in the following proportions; Sawdust: within the range 23 litres to 35 litres (2.3 - 2.9 parts) Sand: within the range 11 litres to 23 litres (1.7 - 2.3 parts) Cement: lOKg (1 part) Water: within the range 12 litres to 14 litres (1.2 parts) 3 A cementitious mix according to claim 2 wherein the sand includes fines in a proportion per unit volume greater than 10% which would pass through a 150 micron mesh. 4 A cementitious mix according to claim 3 wherein the fine sand includes silica and/or clay (alumina). 5 A cementitious mix according to claim 4 wherein the proportion of silica is greater than the proportion of alumina. 6 A cementitious mix according to claim 5, wherein the sand includes fine sand whose particulate size falls within the range of less than 150 microns. 7 A cementitious mix according to claim 6 wherein said mix forms a construction block including at least one outer face in which at least part of said at least one outer face lies in a plane spaced apart from a plane in which the remaining part of said at least one face lies. 8 A mix according to claim 7 wherein said at least one outer face is generally convex outward. 9 A mix according to claim 8 wherein said at least one part of said outer face provides said construction block with a rock face appearance. 10 A mix according to claim 9 wherein the mix when wet. has a slump within the range 0.5mm to 15mm. 11 A mix according to claim 10 wherein the construction block includes at least one internal cavity for services. 12 A mix according to claim 7 wherein the block includes a recess for keying or interlocking with adjacent blocks. 13 A mix according to any of the foregoing claims wherein the construction block is made by pouring said mix when wet into a mould. 14. A lightweight construction block formed in a mold from a mix of ingredients which include sand, water and a lightweight aggregate which is mixed according to a predetermined time regime; wherein the mix is capable of a wet slump during formation within the range of 0.5 - 20mm, the slump resulting in a formation on said construction block which provides the block with at least one generally curved or irregular outer surface on at least one face of the block. 15 A construction block according to claim 14, wherein the ingredients of said mix are blended in the following proportions; Sawdust: within the range 23 litres to 35 litres (2.3 - 2.9 parts) Sand: within the range 11 litres to 23 litres (1.7 - 2.3 parts) Cement: lOKg (l part) Water: within the range 12 litres to 14 litres (1.2 parts) 16 A construction block according to claim 15, wherein the sand includes with fines, sand whose particulate size falls within the range of less than 150 microns 17 A construction block according to claim 16 wherein the fine sand includes silica and/or clay (alumina). 18 A construction block according to claim 17 wherein the proportion of silica is equal to or greater than the proportion of alumina. 19 A construction block mix according to claim 18 wherein the sand includes fines in a proportion per unit volume greater than 10% which would pass through a 150 micron mesh. 20 A construction block according to claim 19 including at least one outer face in which at least part of said at least one outer face lies in a plane spaced apart from a plane in which the remaining part of said at least one face lies. 21 A construction block according to claim 20 wherein said at least one outer face is generally convex outward. 22 A construction block according to claim 21 wherein said at least one part of said outer face provides said construction block with a rock face appearance. 23 A construction block according to claim 22 wherein the mix when wet. has a slump within the range 0.5 - 20mm laterally relative to a wall of said mould. 24 A construction block according to claim 20 wherein the construction block includes at least one internal cavity for services. 25 A construction block according to claim wherein block includes a recess for keying or interlocking with adjacent bricks. 26 A method of producing a construction block from a cementitious mix placed in a mould including the ingredients; sand, cement, sawdust and water; wherein said saw dust comprises the greater proportion of the mix constituents; and wherein the dry density of the mix ranges between 700kg/m3 and 1500kg/m3 wherein the method comprises the steps of; a) blending said ingredients; b) adding water before, during or after said dry blending of said ingredients to form a wet mix having a slump within the range of 0.5 - 20mm laterally relative to a wall of said mould c) placing said wet mix in a mould d) allowing said wet mix to dry for a predetermined period e) removing said mould to expose a formed construction block. 27 A method according to claim 26, wherein the sand includes fine sand whose particulate size falls within the range of less than 150 microns. 28 A method according to claim 27 wherein the fine sand includes silica and/or clay (alumina). 29 A method according to claim 28 wherein the proportion of silica is greater than the proportion of alumina. 30 A method according to claim 29, wherein the ingredients are mixed in the following proportions; Sawdust: within the range 23 litres to 35 litres (2.3 - 2.9 parts) Sand: within the range 11 litres to 23 litres (1.7 - 2.3 parts) Cement: lOKg (1 part) Water: within the range 12 litres to 14 litres (1.2 parts) 31 A method according to claim 30 wherein the sand includes fines in a proportion per unit volume greater than 10% which would pass through a 150 micron mesh. 32 A method according to claim 31 wherein the construction block formed by said mix includes at least one outer face in which at least part of said at least one outer face lies in a plane spaced apart from a plane in which the remaining part of said at least one face lies. 33 A method according to claim 32 wherein said at least one outer face is generally convex outward. 34 A method according to claim 33 wherein said at least one part of said outer face provides said construction block with a rock face appearance. 35 A method according to claim 34 wherein the mix when wet. has a slump of 0.5 - 20mm laterally of a vertical. 36 A method according to claim 35 wherein the construction block includes at least one internal cavity for services. 37 A method according to claim 36 wherein the block includes a recess for keying or interlocking with adjacent blocks. 38 A method according to claim 37 wherein said block includes a border about said split rock face. 39 A method of construction of a lightweight building block wherein the method comprises the steps of : a) selecting a specific type of sand with a predetermined level of clay content for use in a mix to form a construction block; b) taking a predetermined quantity of said sand and blending the sand with a predetermined mix of at least sawdust and cement; c) mixing said sand , cement and sawdust according to predetermined proportions with a predetermined quantity of water; d) introducing said mix into a mould; e) allowing said mix to set for a predetermined period; wherein the block produced from said mould has at least one of its faces which are generally curved in appearance, wherein said rock Uke appearance of at least one face of said block is achieved by selecting a mix which is capable of a predetermined level of slump and removing said mould at a predetermined time during setting of said mix. 40 A method of constructing a lightweight building block wherein the method comprises the steps of: a) selecting a specific type of sand with a predetermined level of clay content for use in a mix to form a construction block; b) taking a predetermined quantity of said sand and blending the sand with a predetermined mix of at least a cellulose fibre material and cement; c) mixing said sand , cement and cellulose fibre according to predetermined proportions with a predetermined quantity of water; d) introducing said mix into a mould; e) allowing said mix to set for a predetermined period; wherein the block produced from said mould has at least one of its faces which are rock like in appearance, wherein said rock like appearance of at least one face of said block is achieved by selecting a mix which is capable of a predetermined level of slump. 41 A method according to claim 40 wherein when at least two blocks are removed from the mould, opposing faces of said at least two blocks undergo slump to an extent that said faces engage whereupon release of said faces results in a block having a rock face appearance on said opposing face. 42 A method of constructing a lightweight building block having a rock face appearance on at least one face of the block, wherein the method comprises the steps of: a) selecting a specific type of sand with a predetermined level of clay content for use in a mix to form a construction block; b) taking a predetermined quantity of said sand and blending the sand with a predetermined mix of at least a cellulose fibre material and cement; c) mixing said sand , cement and cellulose fibre according to predetermined proportions with a predetermined quantity of water; d) introducing said mix into a mould; e) allowing said mix to set for a predetermined period; wherein, the block produced from said mould has at least one of its faces which are rock or cobblestone like in appearance, wherein said rock like appearance of at least one face of said block is achieved by selecting a mix which is capable of a predetermined level of slump and allowing opposing faces of said blocks to come in contact as a result of said slump. 43 A method according to claim 42 wherein a divider is placed in said mould to separate a border region of said opposing faces of said blocks. 44 A method according to claim 43 wherein the divider comprises a frame having an interior opening which allows contact between said opposing faces of said blocks. 45 A method according to claim 44 wherein said divider is either rectangular or triangular in profile. 46 A lightweight construction block formed in a mould from a mix which includes sand, water and a lightweight aggregate which is mixed according to a predetermined time and mix regime; wherein the mix when wet, has a slump which falls within the range of 0.5 - 20mm relative to a vertical wall of said mould; wherein the slump is such that it enables a formation in said construction block which provides a generally convex outward appearance on at least one face of the block; and wherein the block is held in a mould for a time period in the region of 20 - 40 minutes prior to removal of the mould. 47 A construction block according to claim 46 wherein at least two faces of said block are convex outward, wherein said convex faces are formed when said mould is removed. 48. A construction block according to claim 47 wherein two opposing faces of adjacent blocks engage during setting of said mix whereupon disengagement between said blocks prior to setting results in each said opposing faces having a rock like appearance. 49. A construction block according to claim 48 wherein the block includes a border about the periphery of said rock face. 50 A lightweight construction block according to claim 49 wherein the ingredients are mixed in the following proportions: Sawdust: within the range 23 litres to 29 litres (2.3 ~ 2.9 parts) Sand: within the range 17 litres to 23 litres (1.7 - 2.3 parts) Cement: lOKg (1 part) Water: within the range 12 litres to 14 litres (1.2 parts) and wherein the dry density of the block falls within the range of 700kg/m3 and 1500kg/m3. 51 A lightweight construction block according to claim 50 wherein the ingredients are mixed in the following proportions: Sawdust: 29 litres ( 2.9 parts) Sand: 17 litres (1.7 parts) Cement: lOKg (1 part) Water: 12 litres (1.2 parts). 52 A lightweight construction block according to claim 51 wherein the block includes chemical additives to resist termite attack. 53 A lightweight construction block according to claim 52 wherein said chemical additives may be selected from arsenic, cyanide, boron oxide, barium oxide or other toxic or non-toxic additives. 54 A lightweight construction block according to claim 53 wherein said additives are placed in said water and said water is mixed with said saw dust to form a slurry prior to mixing said slurry with cement and sand. 55 A lightweight construction block including sand, water and a wood fibre aggregate which is mixed according to a Dredetermined mix regime; wherein the mix prior to setting is capable of a predetermined slump during formation of the block , the slump resulting in a formation on said construction block which provides generally curved faces and with at least one of said faces having a rock face appearance. 56 A lightweight construction block which includes sand, cement, wood products as fillers or aggregate and additives such that the block is capable of resisting termite attack. 57 A lightweight construction block which includes sand, cement, wood products as fillers or aggregate and additives such that the block is capable of resisting termite attack due to inclusion in the mix of termite resistant chemicals.

Inventors: COLLIER PETER, COLLIER, PETER
Applicants: COLLIER PETER, COLLIER, PETER
Application year: 2001
Main classification: C04B16
IPC codes: B28B1, B28B7, B28B11, B28B17, B28B23, C04B16, C04B18, C04B28, E04B1, E04B2, E04C1