SHAPE MEMORY THERMOPLASTICS AND POLYMER NETWORKS FOR TISSUE ENGINEERING

Abstract: Methods and compositions are described herein for reconstruction of different functional tissues. Dissociated cells, differentiated cells, adult mesenchymal stem cells or embryonic stem cells are seeded on a scaffold. The scaffold will consist of a biocompatible, biodegradable shape memory ("SM") polymers. In addition bioactive substances may be incorporated in the scaffold. Thermoplastic as well as thermoset materials with SM-effect can be used. The shape memory effect will be applied as an interactive link between the cells and the used polymeric scaffold. The degradation kinetics as well as shape memory transition temperature will be tailored by adjusting to monomer ratios of the co-oligomers. The shape memory effect will be used to create a degradation or release of bioactive substances on demand, induce forces on seeded cells or induce proliferation and differentiation of cells.

Description: SHAPE MEMORY THERMOPLASTICS AND POLYMER NETWORKS FOR TISSUE ENGINEERING Background of the Invention The present invention relates to the use of shape memory polymers in tissue engineering and to a method of tissue engineering using shape memory polymers. Up to now biodegradable and biostable thermoplastic or network materials which are biocompatible were used as scaffold material in tissue engineering. Several different polymeric substances were applied from modified biologic to folly synthetic materials. Great achievements have been realized in tissue engineering using these materials, such as tissue engineered artificial skin and other products that are now in the clinical pipeline. However the scaffold material cannot react or be altered independent of the seeded surface, in-growth of vasculature or differentiation of seeded cells. The materials that are needed are therefore: Materials or materials loaded or coated with bioactive substances that have the possibility to induce structuring, proliferation or differentiation of cells in itself. Materials that can control release kinetics of one or more bioactive substances independently by triggering an effect, that may open or close porous structures through an external stimulus. Scaffolds that will only degrade after an external stimulus is set (degradation on demand). Scaffolds that can induce forces on the seeded cells. It is the object of the present invention to overcome the drawbacks of the prior art. This object has been solved with the use and the method according to the independent claims. Preferred embodiments are given in the dependent subclaims. Brief description of the figures Figure 1 shows SMP particles employed for tissue and/or cell engineering. The surface of the seeded particle can be increased by inducing a shape memory effect. Figure 2 shows that separation of grown cells and/or tissue from SMP particle (scaffold) can be achieved by inducing degradation and/or a shape memory effect. Figure 3 shows an example of the use of SMP scaffold for the orientation of cells and/or tissue grown thereon by inducing a shape memory effect. In addition it is shown that bioactive substances, contained in the SMP scaffold are released due to the shape memory effect. First the shape memory polymers (SMP) which may be employed in the present inven ¬ tion are described. SMP are generally characterized as having netpoints and flexible segments. These net- points can be chemical or physical in nature. SMP are characterized as phase segregated linear block co-polymers having a hard segment and a soft segment. The hard segment is typically crystalline, with a defined melting point, and the soft segment is typically amorphous, with a defined glass transition temperature. In some embodiments, however, the hard segment is amorphous and has a glass transition temperature rather than a melting point. i other embodiments, the soft segment is crystalline and has a melting point rather than a glass transition temperature. The melting point or glass transition temperature of the soft segment is substantially less than the melting point or glass transition temperature of the hard segment. When the SMP is heated above the melting point or glass transition temperature of the hard segment, the material can be shaped. This permanent or original shape can be memorized by cooling the SMP below the melting point or glass transition temperature of the hard segment. When the shaped SMP is cooled below the melting point or glass transition temperature of ÷he soft segment while the shape is deformed, a new (temporary) shape is fixed. The original shape is recovered by heating the material above the melting point or glass transition temperature of the soft segment but below the melting point or glass transition temperature of the hard segment . In another method for setting a temporary shape, the material is deformed at a temperature lower than the melting point or glass transition temperature of the soft segment, resulting in stress and strain being absorbed by the soft segment. When the material is heated above the melting point or glass transition temperature of the soft segment, but below the melting point (or glass transition temperature) of the hard segment, the stresses and strains are relieved and the material returns to its original shape. The recovery of the original shape, which is induced by an increase in temperature, is called the thermal shape memory effect. Properties that describe the shape memory capabilities of a material are the shape recovery of the original shape and the shape fixity of the temporary shape. Several physical properties of SMPs other than the ability to memorize shape are significantly altered in response to external changes in temperature and stress, particularly at the melting point or glass transition temperature of the soft segment. These properties include t he elastic modulus, hardness, flexibility, vapor permeability, damping, index of refraction, and dielectric constant. The elastic modulus (the ratio of the stress in a body to the corresponding strain) of an SMP can change by a factor of up to 200 when heated above the melting point or glass transition temperature of the soft segment. Also, the hardness of the material changes dramatically when the soft segment is at or above its melting point or glass transition temperature. When the material is heated to a temperature above the melting point or glass transition temperature of the soft segment, the damping ability can be up to five times higher than a conventional rubber product. The material can readily recover to its original molded shape following numerous thermal cycles, and can be heated above the melting point of the hard segment and reshaped and cooled to fix a new original shape. Preferred SMP or SMP compositions can hold more than one shape in memory. For example, the composition can include a hard segment and at least two soft segments. The T^ ans of the hard segment is at least 10 °C, and preferably 20 °C, higher than the T^ of one of the soft segments, and the Ttrans of each subsequent soft segment is at least 10 °C, and preferably 20 °C, lower than the Tuans of the preceding soft segment. A ultiblock copolymer with a hard segment with a relatively high T trans and a soft segment with a relatively low T,^ can be mixed or blended with a second multiblock copolymer with a hard segment with a relatively low T and the same soft segment as that in the first multiblock copolymer. Since the soft segments in both multiblock copolymers are identical,the polymers are miscible in each other when the soft segments are melted. The resulting blend has three transition temperatures: one for the first hard segment, one for the second hard segment, and one for the soft segment. Accordingly, these materials are able to memorize two different shapes. Articles of manufacture with two or more shapes in memory can be prepared by forming a polymer composition with a hard segment, a first soft segment, and a second soft segment, where the first soft segment has a trans at least 10 °C below that of the hard segment and at least 10 °C above that of the second soft segment. After the composition is shaped at a temperature above the T ans of the hard segment, it can be cooled to a temperature below that of the T of the first soft segment and above that of the second soft segment and formed into a second shape. The composition can be formed into a third shape after it has been cooled below the T tr a ns of the second soft segment." The composition can be heated above the T trans of the second soft segment to return the composition to the second shape. The composition can be heated above the Ttrans of the first soft segment to return the composition to the first shape. The composition can also be heated above the T trans of the hard segment, at which point the composition loses the memory of the first and second shapes and can be reshaped using the method described above. As used herein, the term "biodegradable" refers to materials that are bioresorbable and/or degrade and/or break down by mechanical degradation upon interaction with a physiological environment into components that are metabolizable or excretable, over a period of time from minutes to three years, preferably less than one year, while maintaining the requisite structural integrity. As used herein in reference to polymers, the term "degrade" refer to cleavage of the polymer chain, such that the molecular weight stays approximately constant at the oligomer level and particles of polymer remain following degradation. The term "completely degrade" refers to cleavage of the polymer at the molecular level such that there is essentially complete mass loss. The term "degrade" as used herein includes "completely degrade" unless otherwise indicated. A polymer is a shape memory polymer if the original shape of the polymer is recovered by heating it above a shape recovering temperature (defined as the Trans of a soft segment) even if the original molded shape of the polymer is destroyed mechanically at a lower temperature than the shape recovering temperature, or if the memorized shape is recoverable by application of another stimulus. As used herein, the term "segment" refers to a block or sequence of polymer forming part of the shape memory polymer. As used herein, the terms hard segment and soft segment are relative terms, relating to the Ttrans of the segments. The hard segment(s) has a higher T trans than the soft segment(s). The shape memory polymers can include at least one hard segment and at least one soft segment, or can include at least one kind of soft segment wherein at least one kind of the soft segments are crosslinked, without the presence of a hard segment. The hard segments can be linear oligomers or polymers, and can be cyclic compounds, such as crown ethers, cyclic di-, tri-, or oligopetides, and cyclic oligo(ester amides). The physical interaction between hard segments can be based on charge transfer complexes, hydrogen bonds, or other interactions, since some segments have melting temperatures that are higher than the degradation temperature. In these cases, there is no melting or glass transition temperature for the segment. A non-thermal mechanism, such as a solvent, is required to change the segment bonding. The ratio by weight of the hard segmentrsoft segments is between about 5:95 and 95:5, preferably between 20:80 and 80:20. J Polymer Segments The segments preferably are oligomers. As used herein, the term "oligomer" refers to a linear chain molecule having a molecular weight up to 15,000 Da. The polymers are selected based on the desired glass transition temperature(s) (if at least one segment is amorphous) or the melting point(s) (if at least one segment is crystalline), which in turn is based on the desired applications, taking into consideration the environment of use. Preferably, the number average molecular weight of the polymer block is greater than 400, and is preferably in the range of between 500 and 15,000. The transition temperature at which the polymer abruptly becomes soft and deforms can be controlled by changing the monomer composition and the kind of monomer, which enables one to adjust the shape memory effect at a desired temperature. The thermal properties of the polymers can be detected, for example, by dynamic mechanical thermoanalysis or differential scanning calorimetry (DSC) studies. In addition the melting point can be determined using a standard melting point apparatus. 1. Thermoset or thermoplastic polymers. The polymers can be thermoset or thermoplastic polymers, although thermoplastic polymers may be preferred due to their ease of molding. Preferably, the degree of crystallinity of the polymer or polymeric block(s) is between 3 and 80%, more preferably between 3 and 60%. When the degree of crystallinity is greater than 80% while all soft segments are amorphous, the resulting polymer composition has poor shape memory characteristics. The tensile modulus of the polymers below the T trans is typically between 50 MPa and 2 GPa (gigapascals), whereas the tensile modulus of the polymers above the Trans is typically between 1 and 500 MPa. Preferably, the ratio of elastic modulus above and below the T trans is 20 or more. The higher the ratio, the better the shape memory of the resulting polymer composition. The polymer segments can be natural or synthetic, although synthetic polymers are preferred. The polymer segments can be biodegradable or non- biodegradable, although the resulting SMP composition is biodegradable biocompatible polymers are particularly preferred for medical applications. In general, these materials degrade by hydrolysis, by exposure to water or enzymes under physiological conditions, by surface erosion, bulk erosion, or a combination thereof. Non-biodegradable polymers used for medical applications preferably do not include aromatic groups, other than those present in naturally occurring amino acids. Representative natural polymer segments or polymers include proteins such as zein, modified zein, casein, gelatin, gluten, serum albumin, and collagen, and polysaccharides such as alginate, celluloses, dextrans, pullulane, and polyhyaluronic acid, as well as chitin, poly(3- hydroxyalkanoate)s, especially poly(β-hydroxybutyrate), poly(3- hydroxyoctanoate) and poly(3-hydroxyfatty acids). Representative natural biodegradable polymer segments or polymers include poiysaccharides such as alginate, dextran, cellulose, collagen, and chemical derivatives thereof (substitutions, additions of chemical groups, for example, alkyl, alkylene, hydroxylations, oxidations, and other modifications routinely made by those skilled in the art), and proteins such as albumin, zein and copolymers and blends thereof, alone or in combination with synthetic polymers. Representative synthetic polymer blocks include polyphosphazenes, poly(vinyl alcohols), polyamides, polyester amides, poly(amino acid)s, synthetic poly(amino acids), polyanhydrides, polycarbonates, polyacrylates, polyalkylenes, polyacrylamides, polyalkylene glycols, polyalkylene oxides, polyalkylene terephthalates, polyortho esters, polyvinyl ethers, polyvinyl esters, polyvinyl halides, polyvinylpyrrolidone, polyesters, polylactides, polyglycolides, polysiloxanes, polyurethanes and copolymers thereof. Examples of suitable polyacrylates include poly(methyl methacrylate), poly(ethyl methacrylate), poly(butyl methacrylate), poly(isobutyl methacrylate), poly(hexyl methacrylate), poly(isodecyl methacrylate), ρoly(lauryl methacrylate), poIy(phenyl methacrylate), poly(methyl acrylate), ρoly(isopropyl acrylate), poly(isobutyl acrylate) and poly(octadecyl acrylate). Synthetically modified natural polymers include cellulose derivatives such as alkyl celluloses, hydroxyalkyl celluloses, cellulose ethers, cellulose esters, nitrocelluloses, and chitosan. Examples of suitable cellulose derivatives include methyl cellulose, ethyl cellulose, hydroxypropyl cellulose, hydroxypropyl methyl cellulose, hydroxybutyl methyl cellulose, cellulose acetate, cellulose propionate, cellulose acetate butyrate, cellulose acetate phthalate, carboxymethyl cellulose, cellulose triacetate and cellulose sulfate sodium salt. These are collectively referred to herein as "celluloses". Representative synthetic degradable polymer segments or polymers include polyhydroxy acids, such as polylactides, polyglycolides and copolymers thereof; poly(ethylene terephthalate); poly (hydroxy butyric acid); poIy(hydroxyvaleric acid); poly[lactide-co-(ε-caprolactone)]; polyfglycolide- co-(ε-caprolactone)]; polycarbonates, poly(pseudo amino acids); poly(amino acids); poly(hydroxyalkanoate)s; polyanhydrides; polyortho esters; and blends and copolymers thereof. Examples of non-biodegradable polymer segments or polymers include ethylene vinyl acetate, poly(meth)acrylic acid, polyamides, polyethylene, polypropylene, polystyrene, polyvinyl chloride, polyvinylphenol, and copolymers and mixtures thereof. Rapidly bioerodible polymers such as poly(lactide-co-glycolide)s, polyanhydrides, and p ' olyorthoesters, which have carboxylic groups exposed on the external surface as the smooth surface of the polymer erodes, also can be used. In addition, polymers containing labile bonds, such as polyanhydrides and polyesters, are well known for their hydrolytic reactivity. Their hydrolytic degradation rates can generally be altered by simple changes in the polymer backbone and their sequence structure. Various polymers, such as polyacetylene and polypyrrole, are conducting polymers. These materials are particularly preferred for uses in which electrical conductance is important Examples of these uses include tissue engineering and any biomedical application where cell growth is to be stimulated. These materials may find.particular utility in the field of computer science, as they are able to absorb heat without increasing in temperature better than SMAs. Conducting shape memory polymers are useful in the field of tissue engineering to stimulate the growth of tissue, for example, nerve tissue. 2. Hydrogels. The polymer may be in the form of a hydrogel (typically absorbing up to about 90% by weight of water), and can optionally be ionically crosslinked with multivalent ions or polymers. Ionic crosslinking between soft segments can be used to hold a structure, which, when deformed, can be reformed by breaking the ionic crosslinks between the soft segments. The polymer may also be in the form of a gel in solvents other than water or aqueous solutions. In these polymers, the temporary shape can be fixed by hydrophilic interactions between soft segments. Hydrogels can be formed from polyethylene glycol, polyethylene oxide, polyvinyl alcohol, polyvinyl pyrrolidone, polyacrylates, poly (ethylene terephthalate), poIy(vinyl acetate), and copolymers and blends thereof Several polymeric segments, for example, acrylic acid, are elastomeric only when the polymer is hydrated and hydrogels are formed. Other polymeric segments, for example, methacrylic acid, are crystalhne and capable of melting even when the polymers are not hydrated. Either type of polymeric block can be used, depending on the desired application and conditions of use. For example, shape memory is observed for acrylic acid copolymers only in the hydrogel state, because the acrylic acid units are substantially hydrated and behave like a soft elastomer with a very low glass transition temperature. The dry polymers are not shape memory polymers. When dry, the acrylic acid units behave as a hard plastic even above the glass transition temperature and show no abrupt change in mechanical properties on heating. In contrast, copolymers including methyl acrylate polymeric segments as the soft segments show shape memory properties even when dry. 3. Polymers Capable of Forming a Gel at Increased Temperatures. Certain polymers, for example, polyethylene oxide-co-propylene oxide) (PLURONICS ), are soluble in water at temperatures lower than body temperature and become hydrogels at temperatures higher than body temperature. Incorporation of these polymers as segments in shape memory polymers provides them with the ability to response to changes in temperature in a manner opposite that of typical shape memory polymers. These materials recover their shape when cooled below their shape recovery temperature, rather than being heated above their shape recovery temperature. This effect is called inversed thermal shape memory effect. Shape memory polymer compositions including these polymer segments are useful in various biomedical applications where the polymer can be inserted as a liquid, and cooled to recover an intended shape in situ. The inverse thermal shape memory effect can be obtained by incorporating two different ■ segments into a polymer that are miscible at temperatures lower than T misc , but are immiscible at higher temperatures. The phase separation at higher temperatures stabilizes the temporary shape. The polymers can be obtained from commercial sources such as Sigma Chemical Co., St. Louis, MO.; Polysciences, Warrenton, PA; Aldrich Chemical Co., Milwaukee, WI; Fluka, Ronkonkoma, NY; and BioRad, Richmond, CA. Alternately, the polymers can be synthesized from monomers obtained from commercial sources, using standard techniques. II. Assembly of Polymer Segments The shape memory polymer include one or more hard segments and one or more soft segments, wherein at least one of the segments is biodegradable or at least one of the segments is linked to another segment via a biodegradable linkage. Representative biodegradable linkages include ester-, amide-, anhydride-, carbonate-, or orthoester linkages. 1. Polymer Structures. The shape memory effect is based on the polymer morphology. With respect to thermoplastic elastomers, the original shape of an object is fixed by physical crosslinks caused by the hard segment. With respect to network polymers >, the soft segments are covalently crosslinked instead of having hard segments. The original shape is set by the crosslinking process. In contrast to prior art segmented polyurethane SMPs, the segments of the compositions described herein need not be linear. The segments can be partially grafted or attached in dendremeric side groups. A. Thermoplastic and Thermoelastic Polymers The polymers can be in the form of linear diblock-, triblock-, tetrablock, or multiblock copolymers, branch or graft polymers, thermoplastic elastomers, which contain dendritic structures, and blends thereof. Figure 3 illustrates some of the combinations of suitable classes of thermoplastic materials forming the hard and soft segments. The thermoplastic shape memory polymer composition also can be a blend of one or more homo- or co-polymer with one or more diblock-, triblock-, tetrablock, or multiblock copolymers, branch or graft polymers. These types of polymers are well known to those of skill in the art. As used herein, the term "degradable thermoset" refers to (i) thermosets SMPs containing only one soft segment, which contains cleavable bonds, and (ii) thermosets containing more than one soft segment, wherein at least one soft segment is degradable or wherein the different soft segments are connected by cleavable bonds. There are four different types of thermoset polymers that have shape memory capability. These include polymer networks, semi-interpenetrating networks, inteφenetrating networks, and mixed-interpenetrating networks. /. Polymer Networks A polymer network is prepared by covalently crosslinking macromonomers, i.e., polymers which contain polymerizable endgroups such as carbon-carbon double bonds. The polymerization process can be induced by using light or heat sensitive initiators or by curing with ultraviolet light ("UN-light") without an initiator. Shape memory polymer networks are prepared by crosslinking one or more soft segments which correspond to one or more thermal transitions. In an embodiment preferred for biomedical applications, the crosslinking is performed using a photocrosslinker and requires no chemical initiator. The photocrosslinker advantageously eliminates the need for initiator molecules, which may be toxic. Figure 4 is a diagram of a reaction sequence for the synthesis of a preferred photocrosslinker, which produces an overall yield of about 65%. / ' . Interpenetrating Networks Interpenetrating networks ("IPN") are defined as networks where two components are crosslinked, but not to each other. The original shape is determined by the network with the highest crosslink density and the highest mechanical strength. The material has at least two T^ ns corresponding to the different soft segments of both networks. iii. Mixed Interpenetrating Network A mixed IPN includes at least one physically crosslinked polymer network (a thermoplastic polymer) and at least one covalently crosslinked polymer network . that cannot be separated by any physical methods. The original shape is set by the covalently crosslinked network. The temporary shapes correspond to the T^ ns of the soft segments and the trans of the hard segment of the thermoplastic elastomer component. A particularly preferred mixed interpenetrating network is prepared by polymerizing a reactive macromonomer in the presence of a thermoplastic polymer, for example, by the photopolymerization of carbon-carbon double bonds. In this embodiment, the ratio by weight of thermoset polymer to thermoplastic polymer is preferably between 5:95 and 95:5, more preferably, between 20:80 and 80:20. iv. Semi-Interpenetraiing Networks Semi-inteφenetrating networks ("semi-JTPN") are defined as two independent components, where one component is a crosslinked polymer (a polymer network) and the other component is a non-crosslinked polymer (a homopolymer or copolymer), wherein the components cannot be separated by physical methods. The semi-IPN has at least one thermal transition corresponding to the soft segment(s) and the homo- or co-polymer components. The crosslinked polymer preferably constitutes between about 10 and 90% by weight of the semi-interpenetrating network composition. v. Polymer Blends In a preferred embodiment, the shape memory polymer compositions described herein are formed of a biodegradable polymer blend. As used herein, a "biodegradable polymer blend" is a blend having at least one biodegradable polymer. The shape memory polymers can exist as physical mixtures of thermoplastic polymers. In one embodiment, a shape memory polymer composition can be prepared by interacting or blending two thermoplastic polymers. The polymers can be semicrystalline homopolymers, semicrystalline copolymers, thermoplastic elastomers with linear chains, thermoplastic elastomers with side chains or any kind of dendritic structural elements, and branched copolymers, and these can be blended in any combination thereof. For example, a multiblock copolymer with a hard segment with a relatively high and a soft segment with a relatively low Tt r a n s can be mixed or blended with a second multiblock copolymer with a hard segment with a relatively low Ttrans and the same soft segment as that in the first multiblock copolymer. The soft segments in both multiblock copolymers are identical, so the polymers are miscible in each other when the soft segments are melted. There are three transition temperatures in the resulting blend - that of the first hard segment, that of the second hard segment, and that of the soft segment. Accordingly, these materials are able to memorize two different shapes. The mechanical properties of these polymers can be adjusted by the changing the weight ratio of the two polymers. Other kinds of blends of at least two multiblock copolymers, in which at least one of the segments is miscible with at least one of the segments of the other multiblock copolymers, can be prepared. If two different segments are miscible and build one domain together, then the thermal transition of this domain depends on the weight content of the two segments. The maximum number of memorized shapes results from the number of thermal transitions of the blend. Shape memory blends may have better shape memory capabilities than the blend components alone. Shape memory blends are composed of at least one multiblock copolymer and at least one homo- or copolymer. In principle di-, tri, tetra-block copolymers can be used instead of a multiblock copolymer. Shape memory blends are highly useful in industrial applications, since a broad range of mechanical, thermal, and shape memory capabilities can be obtained from only two or three basic polymers by blending them in different weight ratios. A twin screw extruder is an example of standard process equipment that could be used to mix the components and process the blend. SMP that may be employed preferably in the present invention are biodegradable and biocompatible SMP, polymer networks as well as thermoplastics, described above, which are employed as scaffold for tissue engineering. The shape memory effect can be induced thermally, with near infrared, UV, ultrasound or other energy sources. The thermally induced shape memory effect is due to a glass transition or melting point or another thermal effect. Segmented block copoly(ester-urethane)s (thermoplastics) can be used as polymers with physical crosslinks. These copolymers can be used as thermally stimulated shape memory materials with high strain recovery and high final recovery rate. The main advantage of using copolymers is their improved processing conditions as compared with polymers with chemical crosslinks. As only physical crosslinks are introduced, all conventional processing techniques for thermoplastics can be used, and the materials become easily reusable in the case of non-degradable applications. The results indicate that the high crystallinity of these copolymers at room temperature and the formation of stable physical crosslinks are the two prerequisites for these polymers to exhibit a shape memory effect " . The successful use of block and graft copolymers is indicative of using other polymers of various structure and properties as shape memory materials. Thermoset materials with much better mechanical properties e.g. interpenetrating and semi-interpenetrating networks using the same monomers for the macrodiols synthesis but other multifunctional coupling agents e.g. methacrylates can therefore be used and are preferred. The multiblockcopoly(ester-urethane)s as well as the networks may Comprise of coupled cooligomers of ε-caprolactone, L,L-Dilactide , D,L-Dilactide, diglycolide and para-dioxanone. The coupling will be carried out using 2,2(4),4- Trimethylhexane-diisocyanate in the case of the thermoplastics and using polymerizable methacrylate groups in the case of the thermosets. Synthesis is typically carried out in two steps. In the first step macrodiols with different thermal characteristics are synthesized via ring opening polymerization (ROP) of the cyclic esters and purified. Copolymerization of L-lactic acid with glycolic acid using a tin catalyst for transesterification and ethylene glycol as initiator in a bulk reaction leads to an amorphous soft segment with through the dilactide/diglycolide ratio contiolled T g . The oligomerization degree could be tailored using the monomer/initiator-ratio. As the transesterification catalyst dibutyl-tinoxide is the only catalyst with FDA approval for the use in food sector, the remaining catalyst has to be removed by any of several well-known purification methods. A different approach is the synthesis without a transesterification catalyst which leads to a strong enhancement of the reaction times. The materials are synthesized on medical grade standards, which means that they are ultra-pure for the use in functional tissue engineering. To gain multiblockstructures from the synthesized macrodiols, a coupling method must be used. There are several techniques possible from functionalization with a polymerizable end group to direct coupling with a difunctional compound. Coupling of the different segments is e.g. carried out using 2,2(4),4-Trimethyl-hexane-diisocyanate. The synthesis is finished when all isocyanate groups have vanished in the IR-spectmm. It is here very important to use a coupling compound which didn't add an additional crystalline domain to the rather complex multiblock system. The phase separation of the system could be investigated using DSC and AFM In the case of the thermoset materials the synthesized macrodiols are functionalised using a polymerizable end group as the methacrylate group. The material is melted in the wished form and then cured using e.g. UV light. The shape memory transition temperature can be tailored through different monomer ratios. The materials are biocompatible as the first preliminary results with an CAM test show. The materials are biodegradable through the labile ester bonds. The degradation occurs through hydrolytic scission of the bonds and is therefore mostly independent from the implantation site. The degradation kinetics will be tailored using different monomer ratios. Degradation leads to the formation of e.g. lactic of glycolic acid. Degradation of these materials is not a bulk process and will therefore not lead to strong concentrations of glycolic or lactic acid as could be seen by materials with bulk degradation. One prerequisite for biomedical products is the sterilizability. Several techniques are available for sterilization of medical products as hot sterilization (damp or dry hot air), cold sterilization (ethylene oxide, formaldehyde or ionizing radiation) and aqueous solution sterilization. In the field of sterilization of biodegradable thermoplastics a lot of different techniques are used up to now. They were such as plasma sterilization as well as treatment with ethylene oxide at 50 °C. The use of plasma sterilization is really an interesting idea for the modification of the surface of such materials but not for sterilization of polymers, due to the induced reactions on the surface. Therefore any observed differences in the materials characteristics are difficult to trace back. The same problem exists with the ethylene oxide method at 50 °C. Due to the softening of the implant, ethylene oxide is incoφorated into the implant. After the decrease of temperature and ethylene oxide pressure, there is only a slow release of the gas from the material. Toxic reactions of the seeded cells could occur due to the ethylene oxide which is slowly released or the characteristics of the SM material. The materials are synthesized using medical grade standards and are therefore ultra pure for the use in functional tissue engineering. The mechanical properties of the used shape memory system can be tailored in a rather wide range using different macrodiols compositions Macrostructures: Synthetic segmented blockcopoly(ester-urethane)s with thermal shape memory characteristics can be manufactured as woven or non-woven fibres, porous foams or films, membranes, hollow fibers, mono- or multifilaments as well as shape memory thermoset materials processed as thin films or beads. Processing will be carried out in mono- or multifilament fibres and the formation of 3 -dimensional or 2-dimensional structures through different techniques (wovens, non-wovens), formation of films through different techniques such as spin-casting and the formation of 3-dimensional porous structures through salt-leaching, thermally induced phase separation, double emulsion technique or gas foaming processes. The different macroscopic forms could be combined in more sophisticated devices. Programming of the shape memory effect means the creation of a permanent structure of the device through heating in a form above the transition temperature of the upper domains and out-balancing of the system. The temporary structure is fixed through heating above the transition temperature of the lower domains, fixation of the temporary structure and quenching. The programming of the shape memory effect will be explained on an example of an expandable foam. The foam is processed with controlled pore sizes and pore size distribution and is in its equilibrium. The system is heated up over the transition temperature of the soft segment, compressed and quenched. These materials can be combined with one or more bioactive substances and cells. Bioactive substances: Representative bioactive substances include growth factors, adhesion proteins, angiogenic factors as well as other compounds. Growth factors: Epidermal Growth Factor (EGF), Fibroblast Growth Factors (FGFs), Hepatocyte Growth Factor (FfGF), Insulin-Like Growth Factor-1 (TGF- 1), Insulin-Like Growth Factor-2 (IGF-2), Keratinocyte Growth Factor (KGF), Nerve Growth Factor (NGF), Platelet-Derived Growth Factor (PDGF), Transforming Growth Factor-α (TGF-oc), Transforming Growth Factors-β (TGFs-β), Vascular Endothelial Growth Factor (VEGF), recombinant human Growth Hormone (rhGH), angiogenic and anti-angiogenic factors (see, for example, US Patent 6,024,688 (angiogenic factors) Folkman, J.M.; O'Reilly, M.S.; Cao, Y). Adhesion proteins: RGD, RGDS, GRGDS, cyclic RGD peptides, PHSRN, KQAGDV, LDV, IDAPS, REDV, DGEA, KRLDGS, YIGSR, IKAKV, SIKVAV, CDPGYIGSR-NH2, polylysine, polyomithine, KRSR, RKKRRQRRR, RQK and RNR, VAPG, VGVAPG (Amino acid single letter code). Preferred bioactive substances are given below: Adhesion-promoting oligopeptides. OVERVIEW GROWTH FACTORS. These can be incorporated into the polymeric matrix maintaining their full activity or attached on the surface. The release of one ore more bioactive substances will be controlled using the shape memory effect. The diffusion coefficient of the drug is dependent of the hydrophobicity and porosity of e.g. the outer membrane of the foam. The shape memory effect can be used to alter the polarity and porosity of the surface and lead therefore to a change in the diffusion coefficient of the drug. Therefore the release of two ore more bioactive substances with different polarities can be tailored. The adhesion proteins will remain attached to the surface until the implant is degraded on demand. Therefore the adhesion of the cells on the implant will be enhanced till the process of in-growth is finished and then the polymeric matrix is degraded through the triggering of the shape memory effect. Cells: The cells are seeded on the prepared scaffold and taken into a bioreactor for the proliferation of the cells. The shape memory effect is triggered to induce structuring of the cells through applied forces. The bioactive compounds as growth factors, adhesion proteins, angiogenic factors and differentiating factors are released on demand through a triggering of the shape memory effect. Cells to be seeded on the scaffolds are dissociated using standard techniques. Preferred cell types are mesenchymal adult stem cells, muscle stem cells as well as already differentiated cells as epithelial cells, smooth muscle cells, cardiac muscle cells in co culture, mesothelial cells and chondrocytes, schwann cells, glial cells. In some cases it may also by desirable to include nerve cells. See US Patent 5,869,041 to Vandenburgh relating to muscle cells. For tissue engineered organs where different tissues are needs to be incorporated in one device cocultures of the different cells can be applied. Cells are preferably autologous cells, obtained by biopsy and expanded in culture for subsequent implantation, although cells from close relatives or other donors of the same species may be used with appropriate immunosupression. After cell expansion within the culture plate, the cells can be easily passaged utilizing the usual technique until an adequate number of cells is achieved. The shape memory effect will be used to induce forces on the seeded cells. The cells will be seeded on a contracted film. For the stracturing of e.g. skeletal muscle , cartilage or nerves the shape memory effect will be triggered and a force is used on the seeded cells that will lead to a alignment in the wished direction. Examples of tissue engineered devices: The prepared shape memory scaffolds will be used for cell seeding. One possibility is the use of muscle cells in combination with the SM polymeric scaffolds. Muscle transfer is a common procedure in plastic and reconstructive as well as other surgeries but is associated with the risk of morbidity for the donor area. Fabricating skeletal as well as smooth muscle tissue in vitro offers an alternative for this procedure. The key technology for the fabrication of tissue engineered skeletal muscle tissue lies in the alignment and stracturing of the cells. Here the new smart shape memory material in combination with attached adhesion proteins may be the material searched for. Two possibilities are shortly outlined here: The demographic and social alteration of the population will lead in the future to a further growing health service. One main point is the growing • demand of transplants in this field due to the advancing capabilities in medical care. One problem that has a high socio-ecomomic impact in this field and therefore must be solved is incontinence. One possibility is to provide a transplantable internal sphincter muscle. A sterilized biodegradable thermoplastic shape memory elastomer film will be used as seeding surface for smooth muscle cells. The polymer surface may be grafted with adhesion proteins or growth factors that could be released on demand. Severe heart failure is under the number one death causes in western societies. Cardiac malformations or loss of cardiac muscle may not be under to number one causes for heart failure but show nonetheless important mortality numbers. Mild to severe loss of cardiac muscle is encountered in various types of congenital cardiac malformations and various surgical procedures have been developed to find optimal solutions for their treatment. Despite the pain staking effort in the development of various techniques the mortality rate of children bom with cardiac malformations remains quite high. Loss of cardiac muscle is not only seen in children but is also encountered in the adult population. Until now techniques with limited success have been developed to overcome this problem. As cardiac muscle tissue due not have stem cells, novel approaches for tissue engineered cardiac muscle tissue must be developed. The new smart shape memory materials will provide a scaffold with controllable programmed forces that will affect a co-culture of cardiac muscle tissue with skeletal muscle stem cells. Additional differentiation enhancement may be carried out through in the polymeric scaffold incorporated bioactive substances. The challenge of ordered integration of a complex arteriovenous and cappilary vascular tree into large living tissue engineered organs ex vivo has still to be solved. For the main aim of providing new organs for transplantation this is an important prerequisite. The loading of a biodegradable thermoplastic shape memory scaffold with angiogenesis factors where the release could be controlled by the shape memory effect is a completely new technique. The reconstruction of whole organs is simply not possible if there is no chance to generate a functioning arteriovenous system in the implant. A further interesting direction is the engineering of larger blood vessels for transplantation using shape memory thermoplasts. Seeding of smooth muscle cells on the outer surface of a shape memory tubing could be used as stabilizing part for blood vessels. The inner surface of such an implant may be covered with epithelial cells to avoid thrombosis. Preferred SMP that may be employed in the present invention are lactide free SMP.- It has surprisingly be found that the lactide free SMP show a degradation behavior differing from the corresponding behavior of lactide containing SMP. While the latter do produce small crystalline particles upon degradation, particles which may present potential health hazard when employed in vivo, the lactide free SMP do not produce small crystalline particles upon degradation. This broadens the possibilities to employ those SMP in tissue engineering, particular to uses in vivo. A further possibility to alter the SMP employed in the present invention is the provision of coatings on the SMP scaffolds. Such coatings may be employed to further enhance the control of the degradation kinetics or the release of substances, such as the described bioactive substance, from the SMP scaffold during the use in tissue engineering. Coating of a fast degrading compound with a slow degrading one with low water permeability lead to a degradation on demand. The shape memory effect will be used to alter the diffusion coefficient of water through the slow degrading material or simply destroy the coating through shear forces. The degradation of the coated material will lead to a sharp loss of the structural integrity of the implanted scaffold. Shape memory polymers can be designed so that the degradation rate is varied. For example, in one embodiment, a hydrolytically degradable polymer can be selectively protected by applying a hydrophobic SMP coating that temporarily prevents water from reaching the hydrolytically cleavable bonds of the bulk polymer. The protective feature of the coating then can be modified when desired by applying an external stimulus such that the diffusion properties of coating are altered to permit water or other aqueous solutions to permeate through the coating and initiate the degradation process. If the hydrolysis rate is relatively high compared to the diffusion rate of water, then the diffusion rate of water through the coating determines the degradation rate. In another embodiment, a hydrophobic coating consisting of densely crosslinked soft segments can be used as a diffusion barrier for water or aqueous solutions. The soft segments should be at least partially crosslinked by linkages that can be cleaved by application of a stimulus. The diffusion rate of water can increased by lowering the crosslinking density. A further advantage of the method and use according to the present invention is the fact that the SMP may be seeded with cells while the SMP is present in the temporary form. After proliferation of the seeded cells, even in vivo during reconstruction of destroyed tissues, the shape memory effect i.e. the alteration of the form and/or volume of the SMP scaffold, can " be used to exert mechanical forces on the grown tissue in order to induce orientation and/or differentiation, and/or to release bioactive substances contained within the SMP scaffold. This enables for example the orientation of cartilage tissue and/or muscle tissue grown on SMP scaffolds in vivo without the need of invasive surgery. The SMP scaffolds used in the present invention may be employed in any suitable form, but spheres, pellets, rods, films and tubes are preferred. Usable are also porous materials and foams. A further advantage of the use and the method of the present invention is the possibility to induce a separation of SMP scaffold and tissue grown thereon using the shape memory effect This feature can be employed in particular during the tissue engineering of adhesive cells, such as cartilage cells and/or keratinocytes. For cmturing adhesive cells it is necessary that each cell has physical contact to their next neighbours, when the whole surface of the carrier material is occupied by the cells the cell growing stopped and differentiation takes place. So the surface of the carrier material limits the growing of the adhesive cells. Up to now for the immobilization of adhesive cells or bioactive substances, like enzymes, peptides, growth factors or drugs, biocompatible porous glass beads or collagen coated micro carriers based on dextran were used. SM-microcarriers, preferable porous beads, which can be expand by external stimulus cu-e an innovative tool for more efficient way of cmturing of adhesive cells. For example. Opening pores, or channels by SM-transition in the shell of the microbead causes a controlled continuous swelling of the particle core, that means a continuous increase in the microparticle surface area. This expansion induced by swelling will increase the microparticle surface area in the range of 20% to 500%, preferable from 50% to 200%. Another difficult step in culturing adhesive cells is the removal of the cells from the carrier material. To remove the cells from the glass or collagen coated microcarrier an aggressive enzyme-cocktail is used, which causes the loss of bibactivity of nearly 20% to 35% of the cells. Therefore the need of an minimal or non invasive removal procedure is obvious. This non invasive removal can also be effected by rapid degradation of the microparticle shell. The degradation kinetics as well as shape memory transition temperature will be tailored using d fferent monomer ratios. Another possibility for nnhi al invasive removal of the cells is degradation on demand induced by external stimulus. On the other hand also a second shape memory effect will be used for an easy removal of adhesive cells without loosing their bibactivity, due to drastically changes in the shape of the microcarriers or by switching the surface morphology from smooth to rough or in the different direction. This invention of intelligent shape memory microbeads will lead to more efficient method of cώtaring every kind of adhesive cells. Mucosic cells for example can preferably be cultured on shape memory microbeads having a rough surface. Separation can be effected by inducing a shape memory effect changeing the surface morphologie from rough to smooth. The typical size of the SM- particles is between 10 nanometers and 2,000 microns, preferable 200 nm to 800 μm. The shape of the particles can be spherical, ellipsoidal, cylindrical or random coil shaped, preferable spheres. The microbeads can be solid hard-spheres, or soft-spheres with a determined contend of solvent (gel), or porous material with unifoπn or gradient polymer density. Also hollow spheres like micells, core-shell particles or bi- or multilayered structures like vesicles for example onions can be used as SM-microbeads. The SM-microbeads can include eloctroconductive or magnetic particles or particles for diagnostic imaging like radiopaque materials, or biologically active molecules to be delivered or compounds for targeting the microbeads. These microbeads exhibit an SM-transition with one or more shapes in memory at macroscopic or microscopic lengthscale induced by external stimulus. The SM-microbeads will consist of biocompatible, biodegradable shape memory polymers that contain at least one physical crosslink (Thermoplast) or contain covalent crosslinks (Thermoset). The shape memory polymers can also be inteφenefrating networks or seπninteφenetrating networks. The used biocompatible, biodegradable shape memory thermoplastic microbeads will be a multiblock copolymer with amorphous and/or crystalline domains consisting of coupled cooligomers of ε-caprolactone, ethylene glycol, propylene glycol , Z,Z-lactic acid, D, -lactic acid, glycolic acid and para-dioxanone. For the SM-microbeads the use of s y nthetic segmented blockcopoly(ester-urethane)s with thermal shape memory characteristics as porous foams or films is preferable. These materials will be the porous hydrophobic stmctural basis of the microparticles. The multiblockcopoly(ester-urethane)s will consist of coupled cooligomers of ε-caprolactone, LJL-lactic acid, DJL-lactic acid, glycolic acid and para-dioxanone. The coupling will be carried out using 2^(4),4-T j rimethylhexane-diisocyanate. Synthesis is typically carried out in two steps. In the first step macrodiols with different thermal characteristics are synthesized via ring opening polymerization (ROP) of the cyclic esters and purified. Copolymerization of L-lactic acid with glycolic acid using a tin catalyst for transesterification and ethylene glycol as initiator in a bulk reaction leads to an amoφhous soft segment with through the lactide/glycolide ratio controlled T g . The oligomerization degree could be tailored using the monomer/initiator-ratio . For the covalently crosslinked polymernetworks the telecheleic macrodiols werde di- or higher functionalized with any kind of polymerizable endgroups peferable methacrylates or acrylates. The network formation will be induced by radical polymerization, prferable by irridiation with UV-light Synthesis of the wished micro carriers relates to processing in the needed form, programming of the shape memory effect and determing of the rate and kinetic of the polymer degradation as also sterilization of the material in a non-invasive manner. Processing of the needed form means on the one hand the use of emulsion polymerization techniques for the synthesis of the microparticles. On the other hand all conventional methods of mining and grinding macroscopic material into microparticles can be used, also the use of spraydrying is possible to create the microbeads. The formation of 3-dimensional porous stTucmres can be induced through salt-leaching, thermally induced phase separation, double emulsion technique or gas foaming processes. Programming of the shape memory effect means the creation of a permanent structure and shape of the device through heating in a form above the transition temperature of the upper domains and out-balancing of the system. The temporary structure is fixed through heating above the transition temperature of the lower domains, fixation of the temporary structure and quenching. For example through the application of shear stress to the microparticles. The following synthesis examples illustrate the preparation of SMP materials which may be used in the present invention. Thermoplastic SMP with phase segregated block-copolymers Block-copolymers were produced by connecting macrodiols with diisocyanate. Synthesis of Telechelics, oligomers with functional groups at both ends. The telechelic acrodiol were synthesized by ring opening polymerization of cyclic monomers with di(n-butyl)uhoxide as a transesterfication catalyst under a 2 atmosphere. α,ω-dihydroxy [oligo(ethylene glycol glycolate) ethylene oligo (ethylene glycol glycolate)] - (PDS1200 and J?DS1300) was prepared as follows. The monomer p-dϊoxane-2-one was obtained by distillation (thermal depolymerization) of the oligomer prior to use. 57 g (0.63 ol) of the monomer, 0.673 g (10.9 mol) ethylene glycol, and 0.192 g (0.773 mmol) di(n-butyl) tinoxide were heated to 80 °C for 24 h The end of the reaction (equnibrium) was deterrαined by GPC. The product was soluted in hot 1,2-dichloroethane and filtered hot through a Buechner-funnel filled with silica gel. The product was obtained by precipitation in hexanes and dried in vacuo for 6 h. α,ω-dihydroxy [oligo(£-lactate-co-glycolate) ethylene oligo (L- lactate-co-glycolate)] - (abbr.: PLGA2000-15) was prepared as follows. In a 1000 ml two-neck round bottomed flask, 300 g (2.08 mol) of L,L-dilactide, 45 g (0.34 mol) of diglycolϊde and 4.94 g (0.80 mol) ethylene glycol were heated to melt at 40 °C and stirred. 0.614 g (2.5 mmol) di(n-butyl) tinoxide was added. After 7 h, the reaction reached equilibrium as determined by GPC. The reaction mixture was soluted in 1,2-dichloroethane and purified in a silica gel column. The product was obtained by precipitation in hexanes and dried in vacuo for 6 h. Macrodiols of e-caprolactone: 51,5g (0.452 mole) e-caprolactone, 565.6mg (62.1 mmole) ethylene glycole and 373.1 mg (1.49 mmole) di-n-butyl-tinoxide were stirred at 135°C for 6 hours. The reaction: mixture was soluted in 1,2-dichloroethane and purified in a silica gel column. The product was obtained by precipitation in hexanes and dried in vacuo for 6 h. Polyaddition: The macrodioles were dissolved in dry 1,2-dichloroethane and dried over molecular sieve by azeotropic soxleth distillation. Water content (< 10ppm) was determined in accordance with the Karl Fischer Method. Freshly distilled diisocyanate is introduced into the reaction vessel with a syringe and polymerisation is conducted at 80°C under stirring. The reaction is monitored via GPC. The polymer is obtained by precipitation in hexane, purification is carried out by repeatedly dissolving in 1,2-dichloroethane and precipitating in hexane. The final polymer is dried in vacuum. These polyadducts comprising caprolactone and dioxane are abbreviated PDC in the following The weight-% amount of oligo(p-dioxanone) in the polymer is given by the sample ID. Table 1. Reaction parameters of PDC multiblock copolymers comprising ODX and OCL. m(ODX) n(ODX) m (OCL) n(OCL) m (TDMI) n (TDMI) T Sample ID [g] [mmol] [g] [mmol] [gj [mmol] [h] PDCO 0.00 0.00 5.00 1.66 0.42 1.99 45 PDC9 0.50 0.14 4.50 1.50 0.41 1.95 45 PDC19 1.00 0.28 4.00 1.33 0.41 1.95 45 PDC28 1.50 0.43 3.50 1.17 0.40 1.90 45 PDC38 12.10 3.46 17.70 5.90 2.16 10.24 504 PDC64 3.48 0.99 1.49 0.49 0.45 2.14 45 PDC83 5.85 1.67 0.66 0.22 0.53 2.52 45 Table 2. Chemical composition and molecular weights of PDC multiblock copolymers M„ M„ M w /MnM n (Film) OCL ODX TDMI Sample ID [g-mol "1 ] [g-mof 1 ] [g-mof 1 ] [wt.-%] [wt.-%] [wt.-%] PDCO 184000 77000 2.38 95000 92.3 0.0 7.7 PDC9 159000 76000 2.10 66000 83.2 9.2 7.6 PDC19 158000 69000 2.29 61000 73.9 18.5 7.6 PDC28 134000 63000 2.14 47000 64.8 27.8 7.4 PDC38 118000 41000 2.87 55.4 37.9 6.8 PDC64 63000 35000 1.79 32000 27.5 64.2 8.3 PDC83 65000 38000 1.72 31000 9.4 83.1 7.5 The molecular weights of the synthesized materials are measured by relative GPC in chloroform. Calibration was carried out using narrow polystyrene standards. Table 3. Thermal properties of PDC multiblock copolymers determined by DSC Sample ID T g Δc p T m (OCL) ΔH (OCL) T m (ODX) AH(ODX) C°C] [I-K-g 1 ] [°C1 P ' g 1 ] [°C] [ g 1 ] PDCO - - 41 ±2 45 ±1 PDC9 - - 41 ±2 43 ±1 77±1 2.5 ± 0.5 PDC19 -18 ±2 0.10 ±0.01 40±2 35 ±1 83 ±2 5.0 ±0.5 PDC28 -24 ±2 0.20 ± 0.02 40±2 31 ± 1 85±2 6.5 ±0.5 PDC35 -17 ±2 0.13 ±0.05 40 ±2 25 ±1 81 ±1 ' 15 ±1 PDC64 -17 ±2 0.36 ±0.01 40±2 14±2 85±2 31 ±1 PDC83 -16±2 0.60 ±0.05 - - 85±1 35±2 The thermal transition is independent of the molar ratios of the used oligomers. The thermal transition itself is rather fixed in a predetermined temperature range that could be tailored using different oligomers. Table 4. Mechanical performance of the PDC multiblock copolymers Sample ID T[°C] E[MPa] σ s [MPa! ε s [%] Oxnax [MPa] Smax [so] PDCO 20 • 40 ±5 8±1 33 ±1 17 ±5 1000 ±150 PDC9 20 34±8 9±1 52 ±17 16±1 1037 ±100 PDC19 20 43 ±6 9±1 40 ±4 18±2 900 ±100 PDC28 20 39±5 8±1 35 ±1 21 ±1 1100 ±100 PDC35 20 34±5 8±1 49 ±2 13 ±2 700 ± 50 PDC64 20 70 ±10 ll±l 37 ±1 19 ±1 650 ± 50 PDC83 20 90 ±30 15±2 41 ±4 25 ±4 730 ± 50 PDCO 37 17±2 2.6 ±0.1 24±1 17 ±1 1200 ± 100 PDC9 37 12 ±3 2.6 ± 0.3 33 ±4 14±3 1200 ±170 PDC19 37 14±5 2.9 ±0.4 33 ±8 14±1 1100 ±70 PDC28 37 10 ±3 2.0 ±0.4 32 ±8 11±2 1200 ± 70 PDC35 37 15 ±3 2.6 ±0.5 36 ±8 10±2 800 ± 50 PDC64 37 24 ±3 5.5 ±0.1 35 ±6 12 ±1 550 ± 50 PDC83 37 31±4 6.9 ±0.1 37 ±3 16±2 650 ± 60 PDCO 50 0.2 ±0.1 - - 0.30 ± 0.05 1500 ±200 PDC9 50 0.10 ±0.03 - - 0.40 ±0.15 800 ± 60 PDC19 50 0.3 ±0.1 - - 0.5 ±0.1 820 ± 60 PDC28 50 0.9 ±0.1 - - 0.6 ±0.1 740 ± 60 PDC35 50 2.0 ±0.6 - - 4.0 ± 0.6 560 ±60 PDC64 50 9.1 ±1.2 - - 5.9 ±1.0 30±10 PDC83 50 16.3 ±5.7 - - 8.1 ±1.0 30 ±10 The biodegradable thermoplastic materials show possible deformations from 600 to 1500 %. The mechanical properties strongly depend on the ratio of the used oligomers as well as the molecular weight of the multiblock copolymer. Increasing the amount of oligo(p- dioxanone)diol in the reaction mixture leads to a higher Young's Modulus. This comes along with a decrease of the corresponding elongations at break. This can be observed at all three investigated temperatures and is related to the increasing content of hard segment. Comparing the tensile properties at 20, 37, and 50 °C it can be seen that the materials soften during heating above transition temperature. This is due to the melting of the crystallized switching segments. Table 5. Selected shape memory properties determined from cyclic thermo-mechanical experiments between - 20 and 50 °C PDC9 PDC28 PDC35 PDC9 PDC28 PDC35 N ε prog [%] Rr [%] Rr [%] Rr [%] Rf [%] Rf [%] Rf [%] 1 200 76.0 79.0 80.0 99.5 99.0 98.0 2 200 89.0 93.5 89.5 99.5 99.0 98.0 3 200 99.0 96.0 98.0 99.5 99.0 98.0 4 200 99.0 99.0 99.0 99.5 99.0 98.0 Shape memory properties can be measured using cyclic thermo-mechanical tests according to a method described in literature (B. K. Kim, S. Y. Lee, M. Xu, Polymer 37, 5781 (1996)). The material is pressed to films having a specific thickness. "Dogbone" shaped samples are punched out of the films and mounted in a tensile tester equipped with a thermo-chamber. The strain recovery ratio R, and shape fixity f can be obtained according to the calculation described in H. Tobusbi, H. Hara, E. Yamada, S. Hayashi, S.P.I.E. 2716, 46 (1996). Strain recovery depends on the cycle number N and gradually approaches 100 % after a learning phase during the first couple of cycles. Shape fixity is determined by the amoφhous regions able to undergo entropic elasticity after shape programming and remains constant through the different cycles. The shape memory properties strongly depend on the combination of the two segments. The hard segment is responsible for the mechanical stability of the material, an the soft segment for high strain-recovery ratios. Table 6. Dynamic mechanical properties Sample ID T g (OCL) a) T g (ODX) b E' (turning point) E' (23°C) E' (37°C) E' (50°C) rø r°c] r°cι [MPAl [MPa] [MPA] PDCO -51 ±1 - 48 ±2 360 ±20 240 ±20 10±5 PDC9 -51 ±1 -17 ±1 50±2 280 ±10 190 ±10 15 ±5 PDC 19 -47 ±1 -15 ±1 50±2 280 ±10 190 ±10 15±5 PDC28 -45 ±2 -19±1 48±2 280 ±10 190 ±10 15 ±5 PDC35 -46 ±1 -11 ±1 48±2 320 ±10 230 ±10 20 ±5 PDC64 -39 ±1 -4±1 46±2 340 ± 20 220 ± 20 90 ±10 PDC83 - O±l 39±2 360 ± 20 240 ±20 160 ± 10 a) determined from a maximum in E" b) determined from a maximum in tan δ The dynamic mechanical data can be obtained using dynamic mechanical thermal analysis (DMTA). At room temperature the storage modulus E" is dominated by the crystalline OCL segments and shows little variation with the copolymer composition. This trend is still present at 37 °C although overall E * is lower because of the melting of OCL crystallites. The loss in dynamic mechanical performance is fastest at the turning point of the E' curve. At 50 °C E' is generally low, but increasing with higher content of hard segment, which is due to the crystallinity of the ODX Figure 1. Hydrolytic degradation of thermoplastic shape memory elastomers at pH 7, mass and molecular weight loss of different polymer samples at 70 °C (D: PDC10; O: PDC17; Δ: PDC31; V: PDC42) Degradable biomaterials need to contain links that can be cleaved under physiological conditions. There may be enzymatic or hydrolytic scission of the chemical bonds. The hydrolytic cleavage has the advantage that the degradation rate would be independent of the implantation site. Since enzyme concentrations in the body are varying significantly depending on the location, the enzymatically catalyzed cleavage of chemical bonds would be strongly depending on the implantation site. For that reason we introduced hydrolytically cleavable bonds for the synthesis of biodegradable thermoplastic shape memory elastomers. The degradation kinetics could be changed by modification of the used combination of precursor materials. An increase in the amount of hard segment leads to a faster loss in mass . as well as molecular weight. There are several methods to characterize the degradation of a polymer e.g. mechanical properties, molar mass and weight. The degradation process could be split into 3 stages. In the first stage there is a water uptake and a swelling of the polymer to a considerable amount depending on the hydrophobicity. Some ester linkages are cleaved. In the second stage a considerable loss of the molar mass could be observed. The hydrolysis is auto-catalyzed through acid groups that are built up through the crack of the ester bonds. The mechanical properties are breaking down. The third stage is characterized through the mass loss of the sample. In some cases highly crystalline polymer particles could be observed at the end of the degradation process. The degradation of poly(i-lactic acid) based materials is leading to the formation of such high crystalline particles. If these particles are to great in size the formation of fibrous capsules in- vivo could be observed. The degradation process is stopped and the encapsulated particles stay in the body and may cause inflammation. The materials show also a non-linear mass loss leading to a sudden release of the degradation products from the bulk material and therefore high concentrations of e.g. lactic acid that may cause inflammation (K. Fu, D.W. Pack , A M. Klibanov, R.S. Langer Pharm Res 17:1, 100, (2000); K.A. Hooper, N.D. Macon, J. Kohn J. Biomed. Mat. Res. 32 ,443, (1998). In contrast to these polymers the applied multiblock copolymers are showing a linear mass loss and no formation of crystalline particles. The new smart multiblock shape memory materials show a particle free degradation in in-vitro studies. The interaction of biomaterials with the organism strongly depends on the implantation site. In principle three types of tissue have to be distinguished: soft tissue (connective tissue, muscle tissue), hard tissue (bone, tooth) and blood. Testing of the biocompatibility of a polymer scaffold could be carried out by subcutaneous or intra-muscular implantation (soft tissue compatibility). First biocompatibility tests showed also rather encouraging results. The tissue compatibility of the shape memory polymer system was investigated using CAM tests. This is a very sensitive test on toxicity, were a sterilized polymer film is placed on the chorioallantoic membrane of a fertilized egg and incubated for 2 days. After this time the blood vessels around and under the polymer film were investigated due to any kind of damage or undesired reaction. In a first series the biodegradable multi block copolymers showed good tissue-compatibility. There was no reduction of the number of blood vessels or damage under or in the vicinity of the polymer film. Synthesis of Poly(e-caprolactone) dimethacrylates The synthesis of poly (e-caprolactone) dimethacrylates (PCLDMA) is performed according to the method described by Aoyagi et al. (19). The procedure is described on the example of PCLDMA2000 (Mw=2000). To a solution of 20 g (10 mmol) poly(e-caprolactone) diol and 5,3 ml triethylamin (38 mmol) in 200 ml of dry THF, 3,7 ml (38 mmol) methachroyl chloride is added dropwise at 0 °C. The solution is now allowed to warm up to room temperature and stirred for 3 days. Then the precipitated salt is filtered off and the solvent is evaporated at room temperature under reduced pressure. The crude product is resolved in 200 ml ethyl acetate, filtered again and precipitated into aten-fold excess of a mixture of hexanes, ethyl ether and methanol (18:1:1). The colorless precipitate is collected and soluted in 200 ml of dichlorethane, precipitated again and dried carefully under reduced pressure at room temperature. The degree of methacrylation is determined using lH-NMR-spectroscopy Synthesis of the Polymer Networks A mixture of poly(e-caprolactone) dimethacrylate and the proper amount of n-butylacrylate is heated to 10 °C above the melting temperature (Tm) and filled into a mould formed by two glass plates (25 mm x 75 mm) and a teflon spacer of 0,60 mm thickness. To achieve a good homogenity, the mould is stored at Tm for another hour. Photocuring is performed with a 100 Watt mercury arc lamp (Ultracure lOOss plus, Efos) on a heated plate at Tm and lasts, unless stated otherwise, 15 min. The distance between lamp head and sample is 5,0 cm. After cooling to room temperature, the isolated weight is determined ( iso). The sample is extracted and swollen with a 100-fold excess of dichloromethane overnight, washed carefully and weighted (msw). After drying at room temperature under reduced pressure, the sample is weighted again (md). Mechanical and Thermo-Mechanical Experiments: Tensile tests at room temperature were carried out on an Instron 3100. Experiments at extended temperature and thermocyclic experiments were performed on a Zwick 1410 with a Climatix thermo chamber and an Eurotherm temperature controller. The strain rate was 10 mm/min in all experiments. The thermocyclic program consisted of (a) heating up the sample to Th, extending it to ^ cooling down to Tl in the extended state and (b) unloading to 0 % extension at Tl. Th and Tl were held for at least 10 minutes before loading or unloading the sample. Each cycle (a) - (b) was repeated 5 times. Tab. 1: Copolymerisates ofPCLDMA2000 or PCLDMAIOOOO and n-butyl acrylate. curing gelation degree of PCLDMA2000 n-butyl acrylate temperature degree swelling Sample ID a m [mg] V [μl] r B b T [°C] G [%] Q [%] C2 300.0 - - 50 94 410 C2B(11) 267.9 36 1 50 94 490 C2B(38) 187.5 148 5 45 92 570 C2B(54) 136.8 183 10 40 96 660 C2B(65) 106.5 216 15 40 95 650 C2B(75) 76.2 250 25 30 92 680 C2B(90) 31.5 300 75 23 97 730 CIO 300.0 - - 60 90 760 C10B(20) 239.4 68 10 55 97 800 C10B(39) 183.7 130 25 50 93 800 C10B(50) 149.1 169 40 50 90 840 C10B(60) 119.2 202 60 45 97 880 C10B(71) 85.0 241 100 40 93 1020 57.7 271 166 35 n.b. n.b. The two digit number in brackets of the sample ID gives the weight percentage W B of n-butyl acrylate in the monomer mixture. b ΓB : molar ratio of comonomers; ΓB = n n- but y ι aαyht. / ΠPCLDMAIOOOO c No stable film is obtained. Degree of swelling Q of the films: in dichloromethane Tab. 2: Tensile properties of copolymerisates of n-butyl acrylate and PCLDMA2000 or PCLDMA 10000 at room temperature. E is the elastic modulus (Young's modulus), σ m is the maximum stress, ε m the elongation at σ m , ε R is the elongation and σ R the stress at break. Sample E Sπi σ m S σ R ID [MPa] [%] [MPa] [%] [MPa] C2 35+3 21+1 4.7±0.1 20.6+0.3 4.7+0.1 C2B(11) 5.1+0.2 13+1 0.6±0.2 12.8+1.3 0.6+0.2 C2B(38) 1.6+0.1 28±3 0.4±0.1 29+3 0.4+0.1 C2B(54) 1.2+0.1 41+5 0.4+0.1 44±6 0.4+0.1 C2B(65) l.l±O.l 32+3 0.3±0.1 34+3 0.3+0.1 C2B(75) 0.9+0.1 71±8 0.3+0.1 74+8 0.3+0.1 C2B(90) 0.5±0.1 129+24 0.3±0.1 130+23 0.3+0.1 CIO 71+2 290+30 16.2±0.5 290+30 15.7+0.9 C10B(20) 58+8 421+21 14.6±1.2 423±23 14.1+1.2 C10B(39) 49+6 553±28 10.3±0.3 555+30 10.3±0.3 C10B(50) 30+1 422+11 9.2+0.3 422±11 9.2+0.2 C10B(60) 7+3 433+30 8.0+0.4 435+42 8.0+0.4 C10B(71) 7.8+0.2 406+63 4.3+0.4 406+63 4.3+0.4 Tab. 3: Tensile properties of copolymerisates of n-butyl acrylate and PCLDMAIOOOO at 70 °C. E is the elastic modulus (Young's modulus), σ m is the maximum stress and ε R is the elongation at break. E Sample ID ε R [MPa] [MPa] TO/. CIO 0.70+0.09 0.79+0.10 210+7 C10B(20) 1.01±0.05 1.06+0.17 187+3 C10B(39) 0.84+0.03 0.87+0.08 222+28 C10B(50) 0.80+0.11 0.85+0.12 229+24 C10B(60) 0.60+0.02 1.12+0.01 382+8 C10B(71) 0.43+0.03 0.62+0.11 354+13 Tab. 4: Thermo-mechanical properties of copolymerisates of n-butyl acrylate and PCLDMAIOOOO at T = 0 °C, T h = 70 °C and ε m = 200 %. m B is the weight percentage of n-butyl acrylate in the monomer mixture, Ti is the lower limit temperature, the higher limit temperature Th is 70 °C in all experiments. ε m is the maximum extension. E(2)/E(l) is the relation between the elastic moduli of the first two cycles. σ m is the maximum stress at T (N = 1), σi is the corresponding value at Ti (after thermal contraction). R r (N) is the strain recovery rate of the second cycle, r, tot is the total strain recovery rate after 5 cycles, R f is the average strain fixity rate. Sample mB R(2) Rr.tot Rf E(2)/E(l) σi ID a [wt-%] TO TO/. [MPa] [MPa] CIO — 94.5 93.3 95.5+0.1 91.0 0.69 4.16 C10B(20) 20 94.8 93.6 95.2+0.1 82.1 1.34 2.92 C10B(39) 39 96.1 95.0 95.9±0.1 91.5 1.11 0.81 C10B(50) 50 97.8 96.5 96.1±0.1 95.8 0.75 0.32 C10B(60) 60 98.3 97.6 93.7+0.1 99.4 0.61 0.32 C10B(71) 71 99.0 98.1 82.3±2.5 97.3 0.38 . 0.24

Claims: Claims 1. Use of shape memory polymers in tissue engineering. 2. The use according to claim 1 , wherein the shape memory polymer is biodegradable. 3. The use according to claim 1 or 2, wherein the shape memory polymer furthermore comprises at least one bioactive material. 4. The use according to any of the preceding claims, wherein the shape memory polymer is seeded with dissociated cells. 5. The use according to any of the preceding claims, wherein the shape memory polymer is free of lactide units. 6. Method for tissue engineering, comprising the seeding of a shape memory polymer with cells, proliferating the cells and inducing a shape memory effect of the shape memory polymer. 7. The method according to claim 6 wherein the shape memory polymer used is biodegradable. 8. The method according to claim 6 or 7, wherein the shape memory polymer furthermore comprises at least one bioactive material. 9. The method according to any of the preceding claims, wherein the shape memory polymer is seeded with dissociated cells. 10. The method according to any of the preceding claims, wherein the shape memory polymer is free of lactide units.

Inventors: KNISCHKA RALF, KRATZ KARL, LENDLEIN ANDREAS, KNISCHKA, RALF, KRATZ, KARL, LENDLEIN, ANDREAS
Applicants: KNISCHKA RALF, KRATZ KARL, LENDLEIN ANDREAS, MNEMOSCIENCE GMBH, KNISCHKA, RALF, KRATZ, KARL, LENDLEIN, ANDREAS
Application year: 2001
Main classification: A61L27
IPC codes: A61L27, B29C61, C08L67, C12N5