NON-PHOTOCHROMIC, COLORED, BOROSILICATE INORGANIC GLASSES WHICH ABSORB ULTRAVIOLET, AND PREPARATIONS

Abstract: The object of the present invention is non-photochromic, colored, borosilicate inorganic glasses, which absorb ultraviolet and which contain effective amounts of silver, of copper, of halogen(s), of reducing agent(s) and of colorant(s). The present invention also relates to the preparation of said glasses. Within the context of said preparation, borosilicate glasses, which absorb ultraviolet and which are of various colors, can be obtained from a single crude borosilicate glass.

Description: NON-PHOTOCHROMIC , COLORED , BOROSILICATE INORGANIC GLASSES WHICH ABSORB ULTRAVIOLET , AND PREPARATIONS . The present invention relates to novel colored borosilicate inorganic glasses, as well as to methods of preparing them. Said novel borosilicate inorganic glasses are both colored and non- photochromic and at the same time absorb ultraviolet and are obtainable in various colors from a single mixture of oxides or a single crude borosilicate glass of defined composition. Said novel glasses of the invention are perfectly suitable as corrective or non-corrective sunglasses. According to prior art, many sunglasses have already been developed, more particularly in the three following basic tints : green, grey and brown. At present, as regards the performances of said glasses, more and more demands are made from the glasses, especially in terms of protection against ultraviolet rays and in terms of recognition of road signals. Conventionally, a given tint is obtained from the presence of an effective amount of colorant(s) in the basic glass composition. A single glass of given color is obtained from said basic composition. Said glass can absorb ultraviolet if it contains iron oxide and/or vanadium oxide. However, UN cut-offs greater than 380 nm, which are compatible with a transmission in the visible which is sufficiently high to render said glass commercially viable, are difficult to obtain according to prior art. In US patent US-A-5,281,562, non-photochromic, borosilicate inorganic glass compositions are described which contain copper halide or copper-cadmium halide crystals, and which have an abrupt optical absorption cut-off at about 400 nm. Within these compositions, the contents of oxides are adjusted in order to maintain a certain basicity (an R value of between 0.15 and 0.45). The glasses in question can contain up to 1% by weight of colorant(s), and can therefore have a particular fixed tint. US patent US-A-5,242,869 also describes non-photochromic borosilicate glasses which, in addition to copper halides for absorbing ultraviolet, contain coloring agents of the iron oxide, nickel oxide, manganese oxide, cobalt oxide, vanadium oxide, chromium oxide, copper oxide, neodymium oxide and palladium oxide type. The (non-photochromic) glass compositions of both these patents do not contain any silver and must be modified in substance in order to obtain various tints. Furthermore, photochromic borosilicate inorganic glasses are known which do not possess any ultraviolet absorbing properties. US patent US-A-3,208,860 describes such photochromic glasses which are not colored. Said glasses contain silver halides and can contain 0.01 to 1 % of copper oxide(s). Colored photochromic glasses of this type also exist. They contain suitable colorants. Finally, it has been described in US patent US-A-3, 892,582 of the possibility of tinting a photochromic transparent borosilicate inorganic glass (which contains silver halide particles) by heating it under a reducing atmosphere. Said heating permanently confers a tint to said transparent glass without altering its photochromic properties. Within such a context, the inventors thus propose novel non-photochromic, colored glasses which absorb ultraviolet (with abrupt absorption cut-offs of greater than 380 nm), and which are obtainable in various colors from a single mixture of oxides. The presently claimed invention is interesting in both terms of product and in terms of process (of processability). The invention enables non-photochromic, colored glasses, which absorb ultraviolet and which are of various colors, to be obtained from a single mixture of starting materials, even from a single crude borosilicate glass of defined composition (which is non-photochromic despite the presence of silver within it, which absorbs ultraviolet if it has undergone a suitable heat-treatment, and which is colored since it contains at least one colorant within it), by heat-treatments which are carried out under given conditions of duration and/or of temperature. Said starting crude colored borosilicate glass, as well as said colored glasses of various colors which are obtainable by treatment of it, all constitute glasses of the invention, which are first generation glasses and second generation glasses, respectively. According to its first object, the presently claimed invention thus relates to a non-photochromic, colored, borosilicate inorganic glass which absorbs ultraviolet and which contains effective amounts of silver, of copper, of halogen(s), of reducing agent(s) and of colorant(s). Said inorganic glass is a glass based on silica (SiO ) and boron oxide (B O 3 ). Its inorganic matrix can obviously contain other oxides, such as Al 2 O 3 , ZrO 2 , Li 2 O, Na 2 O, K 2 O, MgO, CaO, SrO, BaO, ZnO, PbO, TiO 2 , Nb 2 O 5 , La 2 O 3 , Y 2 O 3 ... Compositions by weight of matrices are specified later on in the present text in an illustrative manner. Said borosilicate inorganic glass is a colored glass. It contains an effective amount of at least one colorant. The following oxides : Fe 2 O 3 , NiO, CoO, N 2 O 5 , MnO, SeO 2 , Cr O 3 and Νd 2 O 3 can be cited in a non-limiting manner as suitable colorants which can be incorporated alone or in a mixture within the glasses of the invention. Said colored borosilicate inorganic glass absorbs ultraviolet. It has an abrupt optical absorption cut-off of greater than 380 nm, generally towards or greater than 400 nm (said abrupt UN cut-off, expressed in nm, corresponds to the wavelength at which 1% transmission is observed, below which the glass absorbs at more than 99% and over which it hardly absorbs any more). To this end, it contains suitable amounts of copper, of halogen(s) and of reducing agent(s). The copper is incorporated in the glass of the invention, with reference to the absorption of ultraviolet, in the same way as in the glasses according to US patents US-A-5,281,562 and US-A-5,242,869. It is noted at this juncture that express mention has not been made of the incorporation of said copper in combination with cadmium. The combined presence of copper and cadmium is however not totally excluded, but the person skilled in the art does not ignore the problems of toxicity which are linked to the incorporation of cadmium. Said copper is incorporated in the glass of the invention in amounts which are far greater than in the glasses according to US patent US-A-3,208,860 in which it is incorporated for other purposes. Said copper is generally incorporated in said glasses of the invention at the rate of 0.15 to 1.5 parts by weight per 100 parts by weight of their borosilicate base. Said colored borosilicate inorganic glass which absorbs ultraviolet characteristically further contains silver. In an entirely unexpected way, said silver does not confer photochromic properties to the colored glass of the invention and enables glasses of various colors to be obtained from a single colored base by suitable heat-treatments. Said silver very likely also takes part in the ultraviolet absorption properties of the glasses of the invention. Said silver is in general incorporated in the glasses of the invention at the rate of 0.0020 to 1.5 parts by weight per 100 parts by weight of their borosilicate base. Said silver is present in the first generation and second generation glasses of the invention. It is responsible for the change of color during the heat-treatment of said first generation glasses in order to obtain said second generation glasses. Advantageous variants of the glasses of the invention are now specified below. In general, per 100 parts by weight of their borosilicate base, said glasses of the invention contain : - from 0.0020 to 1.5 parts by weight of Ag, as indicated above ; - from 0.15 to 1.5 parts by weight of Cu, as indicated above ; and - an effective amount of at least one halogen selected from Cl, Br, I and F, which is conjugated to : - an effective amount of at least one reducing agent, said effective amounts of halogen(s) and ~ of reducing agent(s) generating sufficient copper halide(s) for the absorption of the ultraviolet ; as well as - an effective amount of at least one colorant. The reducing agents which can be incorporated, alone or in a mixture, can notably be selected from SnO, SnO 2 , Sb 2 O 3 and As 2 O 3 . The effective amount of their incorporation is generally between 0.1 and 5 parts by weight per 100 parts by weight of the borosilicate base. As regards the halogens, they are incorporated in general at the rate of at least 0.25 part by weight per 100 parts by weight of the borosilicate base. They are incorporated very rarely at more than 10 parts by weight. Advantageously, each halogen which is incorporated is incorporated in an amount which is less than or equal to 3 parts by weight. Advantageously, chlorine and/or bromine is incorporated at least 0.25 part by weight. The colorants which can be incorporated alone or in a mixture can notably be selected from Fe 2 O 3 , NiO, CoO, V 2 O 5 , MnO, SeO 2 , Cr 2 O 3 and Nd 2 O 3 . The glasses of the invention generally contain, per 100 parts by weight of its borosilicate base : up to 7 parts by weight of Fe 2 O 3 , and/or up to 2 parts by weight of NiO, and/or up to 3 parts by weight of CoO, and/or up to 10 parts by weight of V O 5 , and/or up to 2 parts by weight of SeO 2 , and/or up to 2 parts by weight of Cr 2 O 3 , and/or up to 4 parts by weight of Nd O 3 . Said glasses of the invention advantageously contain, as colorant(s), nickel oxide (NiO) and/or cobalt oxide (CoO). These two colorants, which are used independently or in a mixture, ensure, within the context of the invention, particularly interesting colorations to the borosilicate glasses. The advantageous amounts of incorporation of each one of the constituents above of the glasses of the invention, which are characteristically added into the borosilicate base, are specified below. Per 100 parts by weight of their borosilicate base, the glasses of the invention thus advantageously contain : - from 0.0050 to 1 part by weight of Ag ; - from 0.2 to 1 part by weight of Cu ; - from 0 to 2 parts by weight of Cl ; - from 0 to 2 parts by weight of Br, with at least 0.25 parts by weight of Br + Cl ; - from 0 to 2 parts by weight of I ; - from 0 to 2 parts by weight of F ; - from 0.2 to 3 parts by weight of SnO ; - from 0 to 3 parts by weight of SnO ; - from 0 to 3 parts by weight of Sb O 3 ; - from 0 to 3 parts by weight of As 2 O 3 ; - from 0 to 3 parts by weight of Fe 2 O 3 ; - from 0.0100 to 1 part by weight of NiO ; - from 0.0050 to 1 part by weight of CoO ; - from 0 to 5 parts by weight of N 2 O 5 ; - from 0 to 0.5 part by weight of MnO ; - from 0 to 0.5 part by weight of SeO ; - from 0 to 0.5 part by weight of Cr O 3 ; and - from 0 to 0.5 part by weight of Νd 2 O 3 . These advantageous ranges of incorporation set forth in combination are also to be considered independently of each other. Thus, for example, the glasses of the invention advantageously contain, per 100 parts by weight of their borosilicate base, from 0.0050 to 1 part by weight of silver and/or from 0.2 to 1 part by weight of copper and/or from 0.2 to 3 parts by weight of SnO and/or ... As regards the borosilicate base of the glasses of the invention, to which suitable amounts of silver, of copper, of halogen(s), of reducing agent(s) and of colorant(s) are characteristically added, it advantageously has the following composition by weight : SiO 2 25 - 60 %, preferably 30 - 55 % B 2 O 3 10 - 35 %, preferably 15 - 28 % Al 2 O 3 3 - 17 %, preferably 6 12 % ZrO 2 0 - 13 %, preferably 3 8 % Li 2 O 0 - 15 %, preferably 1.5 - 3 % Na 2 O 0 - 15 %, preferably 2 5 % K 2 O 0 - 15 %, preferably 2.5 - 8 % with Li 2 O + Na 2 O + K 2 O > 2 % MgO 0 - 10 %, preferably 0 ■ 3 % CaO 0 - 15 %, preferably 0 • 5 % SrO 0 - 15 %, preferably 0 5 % BaO 0 - 15 %, preferably 3 ■ 8 % with MgO + CaO + SrO + BaO > 1 % Z ZnnOO 0 0 - 15 %, preferably 0 ■ 11 % P PbbOO 0 0 - 8 %, preferably 0 ■ 5 % T TiiOO 22 0 0 - 8 %, preferably 0 • 5 % N Nbb 22 OO 55 0 0 - 8 %, preferably 0 • 5 % L Laa 22 OO 33 0 0 - 8 %, preferably . 0 ■ 5 % Y Y22OO33 0 0 _ 8 %, preferably 0 ■ 5 %. The advantageous and preferable incorporation ranges above can also be considered independently of one another. In any case, they define, respectively, taken in combination, an advantageous composition by weight and a preferred composition by weight of the borosilicate base of the glasses of the invention. Said borosilicate base of the glasses of the invention can therefore contain the components listed above, advantageously and preferably in the relative percentages by weight indicated above. It is not excluded that said base contain other components. As regards the optional components, it is indicated that when they are incorporated, it is generally at least 0.25 - 0.5% (by weight). The first generation glasses and the second generation glasses of the invention, notably the second generation glasses of the invention, as defined above, are more particularly suitable as sunglasses, corrective or not. Such sunglasses constitute the second object of the present invention. Within the first and second objects of the present invention, glasses are found which are particularly interesting and which : - have a suitable refractive index (1.523), - absorb ultraviolet up to greater than 430 nm, - have a transmittance in the UN and visible domains, typically greater than 5% and less than 25%, even between 8 and 18%, - are in accordance to the requirements imposed with reference to the recognition of road signals, such as those defined by the ANSI Z80.3-1986 standard, and - have a suitable color in the tones of green, grey and brown. The third object of the present invention has now been arrived at, i.e. the methods of preparation of the inorganic glasses in question. The person skilled in the art will already have understood that the method in question is more or less complex, depending on whether a first generation glass or a second generation glass is prepared. The method in question for obtaining a first generation glass of the invention may be considered to be an analogous method. It comprises : - preparing a crude borosilicate glass which contains the suitable amounts of silver, of copper, of halogen(s), of reducing agent(s) and of colorant(s) ; and - heat-treating said crude glass in order to generate within it the crystal phase of the halide(s) which is responsible for the absorption of the ultraviolet. The preparation of said colored crude borosilicate glass is classical. It comprises mixing and melting the compounds in question. The heat-treatment of said colored crude glass is of the type of those described in US patents US-A-5,281,562 and US-A-5,242,869. In order to obtain a second generation glass of the invention, the method of the invention comprises : - preparing a crude borosilicate glass which contains the suitable amounts of silver, of copper, of halogen(s), of reducing agent(s) and of colorant(s) ; - optionally heat-treating said crude glass in order to generate within it the crystal phase of the halide(s) which is responsible for the absorption of the ultraviolet ; - polishing the surface of said borosilicate glass which is heat-treated or non-heat-treated ; and - heat-treating said polished borosilicate glass under a reducing atmosphere ; said heat-treatment being carried out under conditions of duration and temperature which are suitable for obtaining the coloration sought after ; said heat- treatment also ensuring the generation of the crystal phase of the halide(s) which is responsible for the absorption of the ultraviolet if this crystal phase has not been generated beforehand. According to a first variant, the method of the invention can therefore comprise obtaining a first generation glass and then, mainly, its heat-treatment under a reducing atmosphere. According to a second variant, the method of the invention can comprise a single heat-treatment under reducing atmosphere which itself alone ensures the results sought after in terms of coloration and of absorption of ultraviolet (which ensures the direct obtaining of a second generation glass). Said single heat-treatment under reducing atmosphere is, within this context, carried out on a glass, which constitutes a potential precursor of a first generation glass of the invention. The surface treatment - polishing - is carried out before the heat-treatment under reducing atmosphere insofar as said heat-treatment under reducing atmosphere produces effects within the first 100 nm of surface. Said surface heat-treatment is a method known per se. The term « polishing » is employed here in an entirely non-limiting manner. In general, it designates any treatment which can confer, to said glass on which it is carried out, the state of the surface sought after for the finished product. With reference to the finishing of the glasses of the invention, a chemical tempering can be added to the steps of the two methods above. Carried out in a classical manner, such a tempering leads to increasing their mechanical resistance. The heat-treatments set forth above are advantageously carried out under the following conditions : - the heat-treatment of the crude borosilicate glass intended to generate a first generation glass of the invention : at a temperature between 450 and 650°C, for 10 minutes to 2 hours ; - the heat-treatment under reducing atmosphere of the polished crude borosilicate glass (potential precursor of a first generation glass of the invention) or of the polished first generation glass of the invention : at a temperature between 250 and 650°C, for 2 minutes to 12 hours. Said reducing atmosphere generally contains hydrogen. Said reducing atmosphere can notably consist of pure hydrogen or of a mixture of nitrogen and hydrogen. The carrying out of this heat-treatment, under reducing atmosphere, on a polished crude borosilicate glass of defined composition containing suitable amounts of silver, of copper, of halogen(s), of reducing agent(s) and of colorant(s) (first generation glass of the invention, if it has undergone the heat-treatment rendering it an ultraviolet- absorber or potential precursor of such a first generation glass, and in any case a precursor of a second generation glass of the invention), in order to confer a different color to said crude glass, is an innovating ste per se. The carrying out of such heat-treatments, under the conditions of different duration or (and) of temperature, on one glass of given suitable composition to generate numerous glasses of various colors, constitutes another object of the present invention. In an entirely surprising way, the inventors have in fact prepared glasses of various colors (which are non-photochromic and which absorb UN) by heat treating, under a reducing atmosphere, a single crude borosilicate glass of defined, particular composition. Said crude borosilicate glass is a first generation glass of the invention or a potential precursor of such a glass (if it has not undergone the heat-treatment conferring ultraviolet-absorbing properties to it). In any case, it contains suitable amounts of silver, of copper, of halogen(s), reducing agent(s) and colorant(s). The invention will now be illustrated under its different aspects, by the following Examples. Glasses A, B, C (First generation glasses - Table I) The first part of Table I gives the compositions by weight of borosilicate bases of three glasses of the invention. The second part of said Table I indicates the parts by weight of the additives added characteristically to said bases (per 100 parts by weight of said bases). The third part of said Table I gives properties of the three glasses, A, B and C, of the invention (first generation glasses). The glasses in question are obtained in a classical manner, i.e. by successively carrying out the following steps : - mixing vitrifϊable starting materials in the suitable amounts indicated in the first and second parts of Table I ; - melting in a crucible between 1,100 and 1,200°C ; - refining between 1,250 and 1,400°C ; - conditioning between 1,200 and 1,250°C with the view to forming ; - said forming for obtaining spectacles mouldings ; - heat-treatment for obtaining the UN cut-off sought after : the mouldings are treated after pressing in an arch at a temperature of 600°C, for 20 minutes. Upon completion of the implementation of these steps, said three glasses A, B and C are obtained. They have a transmission of greater than 25%. Said transmission on the visible spectrum was measured under a thickness of 2 mm. The color of each one of said glasses A, B and C is characterised by its chromatic co-ordinates (x,y) which are determined according to the C.I.E. trichromatic colorimetric system using the D65-illuminant. The UN cut-off, expressed in nm, corresponds to the wavelength at which 1% transmission is observed, lower than which the glass absorbs at more than 99% and greater than which it hardly absorbs any more, given the abrupt character of the optical absorption cut-off. 14 C8ZZT/I0d3/X3d ZΪS9C/Z0 OΛV Glasses 1 to 15 (Second generation glasses - Table II). These second generation glasses were obtained from first generation glasses A, B and C. A surfacing of said glasses A, B and C is first of all made according to usual techniques. An optical correction can be given to the piece during this surfacing, which confers an adapted geometry to it. Then, a heat-treatment under hydrogen is carried out under the various conditions of temperature and/or of duration, which are specified in Table II. The glasses were in fact treated in batches, discontinuously, in an adapted static oven under a flow of pure hydrogen. Obtaining the same results can be entirely conceived by a continuous treatment of said glasses, in an industrial arch having a controlled atmosphere which is equipped to this end. The surfaced pieces were thus heat treated under a reducing atmosphere between 400 and 530°C for 5 to 240 minutes. During this step, the silver atoms and copper atoms present on the surface are reduced. The total UV visible transmission and the tint are also adapted. Six glasses (glasses 1 to 6), six glasses (glasses 7 to 12) and three glasses (glasses 13 to 15), of various colors, were obtained from a same glass A, B or C, respectively. For said glasses 1 to 15, their transmission, their chromatic coordinates (x,y), their UV cut-off, as well as their conformity with the tests of road signal recognition, are also given in Table II. Table II Examples 1 2 3 4 5 6 Crude glass A A A A A A Heat-treatment temperature under hydrogen (°C) 400 400 530 450 450 500 Duration of heat-treatment under hydrogen (min) 120 240 240 120 240 120 Transmission (%) 18.3 15.3 14.9 17.5 14.3 11.2 X 0.3139 0.3330 0.3399 0.3453 0.3773 0.3905 y 0.3348 0.3395 0.3415 0.3472 0.3595 0.3689 UV cut-off (nm) --_.. 410 410 410 410 410 410 Recognition of road signals (Z80) yes yes yes yes yes yes Examples 7 8 9 10 11 12 Crude glass B B B B B B Heat-treatment temperature under hydrogen (°C) 400 400 530 450 450 500 Duration of heat-treatment under hydrogen (min) 120 240 240 120 240 120 Transmission (%) 18.8 15.3 14.8 17.6 14.1 16.0 X 0.3500 0.3675 0.3758 0.3725 0.3985 0.3929 y 0.3738 0.3790 0.3751 0.3755 0.3782 0.4049 UV cut-off (nm) 420 420 420 420 420 420 Recognition of road signals (Z80) yes yes yes yes yes yes Examples 13 14 15 Crude glass C C C Heat-treatment temperature under hydrogen (°C) 530 450 510 Duration of heat-treatment under hydrogen (min) 240 30 5 Transmission (%) 20.3 19.2 24.8 X 0.3550 0.2970 0.2648 y 0.3468 0.3109 0.2882 UV cut-off (nm) 400 400 420 Recognition of road signals (Z80) yes yes yes

Claims: CLAIMS 1. A non-photochromic, colored, borosilicate inorganic glass, which absorbs ultraviolet and which contains effective amounts of silver, of copper, of halogen(s), of reducing agent(s) and of colorant(s). 2. The glass according to claim 1, characterised in that it contains, per 100 parts by weight of its borosilicate base : - from 0.0020 to 1.5 parts by weight of Ag ; - from 0.15 to 1.5 parts by weight of Cu ; and - an effective amount of at least one halogen selected from Cl, Br, I and F, which is conjugated to : - an effective amount of at least one reducing agent, said effective amounts of halogen(s) and of reducing agent(s) generating sufficient copper halide(s) for the absorption of the ultraviolet ; as well as - an effective amount of at least one colorant. 3. The glass according to one of claims 1 or 2, characterised in that said reducing agent(s) is(are) selected from SnO, SnO 2 , Sb 2 O 3 and As 2 O 3 . 4. The glass according to any one of claims 1 to 3, characterised in that said effective amount of reducing agent(s) is between 0.1 and 5 parts by weight, per 100 parts by weight of its borosilicate base. 5. The glass according to any one of claims 1 to 4, characterised in that said effective amount of halogen(s) is between 0.25 and 10 parts by weight, per 100 parts by weight of its borosilicate base ; each halogen being advantageously incorporated in an amount less than or equal to 3 parts by weight. 6. The glass according to any one of claims 1 to 5, characterised in that said colorant(s) is(are) selected from Fe 2 O 3 , NiO, CoO, V 2 O 5 , MnO, SeO 2 , Cr 2 O 3 and Nd 2 O 3 . 7. The glass according to any one of claims 1 to 6, characterised in that it contains, per 100 parts by weight of its borosilicate base, up to 7 parts by weight of Fe 2 O 3 , and/or up to 2 parts by weight of NiO, and/or up to 3 parts by weight of CoO, and/or up to 10 parts by weight of V 2 O 5 , and/or up to 2 parts by weight of SeO , and/or up to 2 parts by weight of Cr 2 O 3 , and/or up to 4 parts by weight of Nd 2 O 3 . 8. The glass according to any one of claims 1 to 7, characterised in that it contains an effective amount of NiO and/or of CoO. 9. The glass according to any one of claims 1 to 8, characterised in that it contains, per 100 parts by weight of its borosilicate base : - from 0.0050 to 1 part by weight of Ag ; - from 0.2 to 1 part by weight of Cu ; - from 0 to 2 parts by weight of Cl ; - from 0 to 2 parts by weight of Br, with at least 0.25 parts by weight of Br + Cl ; - from 0 to 2 parts by weight of I ; - from 0 to 2 parts by weight of F ; - from 0.2 to 3 parts by weight of SnO ; - from 0 to 3 parts by weight of SnO ; - from 0 to 3 parts by weight of Sb 2 O 3 ; - from 0 to 3 parts by weight of As 2 O 3 ; - from 0 to 3 parts by weight of Fe 2 O 3 ; - from 0.0100 to 1 part by weight of NiO ; . - from 0.0050 to 1 part by weight of CoO ; J - from 0 to 5 parts by weight of V 2 O 5 ; - from 0 to 0.5 part by weight of MnO ; - from 0 to 0.5 part by weight of SeO 2 ; - from 0 to 0.5 part by weight of Cr 2 O 3 ; and - from 0 to 0.5 part by weight of Nd 2 O 3 . 10. The glass according to any one of claims 1 to 9, characterised in that its borosilicate base has the following composition by weight : SiO 2 25 - 60% B 2 O 3 10 - 35% AI 2 O 3 3 17% ZrO 2 0 13 % Li 2 O 0 15% Na 2 O 0 15% K 2 O 0 15 % with Li 2 O + Na 2 O + K 2 O > 2 % MgO 0 10% CaO 0 15 % SrO 0 15% BaO 0 15% with MgO + CaO + SrO + BaO > 1 % ZnO 0 15 % PbO 0 8% TiO 2 0 8% Nb 2 O 5 0 8% La 2 O 3 0 8% Y2O3 0 8 % ; advantageously the following composition by weight SiO 2 30 - 55% B2O3 15 - 28% ZrO 2 3 8% Li 2 O 1.5 - 3% Na 2 O 2 5% K 2 O 2.5 - 8% MgO 0 3% CaO 0 5% SrO 0 5% BaO 3 8 % ZnO 0 11 % PbO 0 - 5 % TiO 2 0 - 5 % Nb 2 O 5 0 - 5 % La 2 O 3 0 5 % 11. Sunglasses, which are corrective or non-corrective, made from a glass according to any one of claims 1 to 10. 12. A method of preparing a glass according to any one of claims 1 to 11, characterised in that it comprises : - preparing a crude borosilicate glass which contains the suitable amounts of silver, of copper, of halogen(s), of reducing agent(s) and of colorant(s) ; and - heat-treating said crude glass in order to generate within it the crystal phase of the halide(s) which is responsible for the absorption of the ultraviolet. 13. A method of preparing a glass according to any one of claims 1 to 11, characterised in that it comprises : - preparing a crude borosilicate glass which contains the suitable amounts of silver, of copper, of halogen(s), of reducing agent(s) and of colorant(s) ; - optionally heat-treating said crude glass in order to generate within it the crystal phase of the halide(s) which is responsible for the absorption of the ultraviolet ; - polishing the surface of said borosilicate glass which is heat-treated or non-heat-treated ; and - heat-treating said polished borosilicate glass under a reducing atmosphere ; said heat-treatment being carried out under conditions of duration and temperature which are suitable for obtaining the coloration sought after ; said heat-treatment also ensuring the generation of the crystal phase of the halide(s) which is responsible for the absorption of the ultraviolet if this crystal phase has not been generated beforehand. 14. The method according to one of claims 12 or 13, characterised in that said heat-treatment of the crude glass is carried out, for 10 minutes to 2 hours, at a temperature between 450 and 650°C. 15. The method according to one of claims 12 or 13, characterised in that said heat-treatment under reducing atmosphere is carried out, for 2 minutes to 12 hours, at a temperature between 250 and 650°C. 16. A method for preparing the glasses according to any one of claims 1 to 11, which are of various colors, characterised in that it comprises heat- treating, under a reducing atmosphere, under various conditions of duration or(and) of temperature, a polished crude borosilicate glass which has a defined composition containing suitable amounts of silver, of copper, of halogen(s), of reducing agent(s) and of colorant(s).

Inventors: BROCHETON YVES, CARLIER BERNARD, BROCHETON, YVES, CARLIER, BERNARD
Applicants: BROCHETON YVES, CARLIER BERNARD, CORNING SA, BROCHETON, YVES, CARLIER, BERNARD, CORNING S.A.
Application year: 2001
Main classification: C03C4
IPC codes: C03C3, C03C4