Polymeric homogeneous catalysts

Abstract: The following invention refers to polymeric homogeneous catalysts, which are obtained by a ring open metathesis polymerisation reaction (ROMP). These catalysts exhibit polymeric backbones, which are due to their unsaturated nature more rigid than those known from the art. This results in a better accessibility of all active sides within the polymer.

Description: The instant invention refers to polymeric homogeneous catalysts comprising an unsaturated polymer backbone. Especially, the polymeric backbone is derived by a so called ring opening metathesis polymerisation reaction (ROMP). Polymeric catalysts are important goals for the production of chemical compounds on industrial scale due to their possible reuse, which often leads to a substantial saving of production costs. In recent years the emphasis was put on the production of, especially, homogeneous forms of catalysts, because the omission of phase transitions during such catalysis leads to an increase in predictability of the reaction behaviour of catalysts in question. One of the driving forces to evaluate more and more sophisticated catalysts lies in the availability of products in enhanced yields and shorter time periods, that is to say in an more economical way. Beneath having a good catalytic system itself a special effort has to be put within the synthesis of the polymeric part of such catalysts. The DE 19910691.6 and DE 19647892.8 offer different solutions for this problem. Nevertheless, there is still a need for the production of new and different polymeric backbones for such compounds with superior properties. Polymerically enlarged homogeneous catalysts disclosed in the art so far possess more or less randomly distributed catalytically active sides along their polymeric backbone and comprise an irregular polymer chain, which could alter the catalytic behaviour negatively. It was, therefore, a task of this invention to disclose new polymerically enlarged homogeneous catalysts exhibiting more rigid polymeric backbones than known in the art, and which are, nevertheless, easy to synthesize. This problem is solved by catalysts of claim one. Preferred embodiments of this invention are objects of claims 2 and 3. Claims 4 to 8 show an advantageous process for the production of catalysts of this invention. Claims 9 to 12 disclose preferred uses. By reacting a compound of formula I wherein U, W are Cl, Br, I, OR Y, Z are PR' 3 , NR' or U R' is (C 6 -C 18 ) -Aryl, (C 3 -C 18 ) -Heteroaryl, (C 3 -C 8 )-Cycloalkyl, (C 1 -C 8 ) -Alkyl, (C 6 -C 18 )-Aryl-(C 1 -C 8 )-Alkyl, (C 3 -C 18 )-Heteroaryl-(C 1 -C 8 )-Alkyl, (C 7 -C 19 )-Aralkyl, (C 4 -C 19 ) -Heteroaralkyl, M is Ru, Mo R is (C 6 -C 18 )-Aryl, (C 3 -C 18 )-Heteroaryl, (C 3 -C 8 )-Cycloalkyl, (C 3 -C 8 )-Cycloalkenyl, H, (C 1 -C 8 ) -Alkyl, (C 2 -C 8 ) -Alkenyl, in a non-reactive organic solvent or solvent mixture with a bicyclic olefin of formula II wherein X is O, NR 5 , C(R 5 ) 2 , S, POR 6 , PR 6 , R 1 , R 2 are independently of each other H, (C 1 -C 8 )-Alkyl, (C 2 -C 8 )-Alkenyl, (C 2 -C 8 ) -Alkynyl, (C 6 -C 18 ) -Aryl, (C 7 -C 19 )- Aralkyl, (C 3 -C 18 )-Heteroaryl, (C 4 -C 19 ) -Heteroaralkyl, (C 3 -C 8 )-Cycloalkyl, (C 3 -C 8 )-Cycloalkenyl, (C 6 -C 18 )-Aryl-(C 1 -C 8 )-Alkyl, (C 3 -C 18 )-Heteroaryl-(C 1 -C 8 )-Alkyl, (C 3 -C 8 )-Cycloalkyl- (C 1 -C 8 ) -Alkyl, (C 1 -C 8 ) -Alkyl- (C 3 -C 8 ) -Cycloalkyl, or form together a =O-group, R 3 , R 4 are independently of each other OR 1 , SR 1 , NR 5 R 1 , OR 7 , SR 7 , NR 5 R 7 provided that at least one residue R 3 , R 4 bears a group R 7 , R 5 is R 1 , R 6 is R 1 provided that it can not be H and R 7 is a catalytically active group, and optionally with a further olefinic compound III, preferably a cycloolefinic compound, polymerically enlarged homogeneous catalysts with a rigid unsaturated polymer backbone can be obtained advantageously in a highly modular way, and thus allow a flexible process optimisation by combining independently selected bicyclic framework and catalytically active subunits. In formula I the dashed lines denote the possibility that groups Y, Z can be connected to the central atom via a double bond or normal bond. In case of NR' as ligand, for example, and Mo as central atom this appears to be the case. Nevertheless, in case of PR 3 ' as ligand and Ru as central atom a normal bond is build up in between. Compounds of formula I and II can be mixed in any proportion. Compound III can optionally be added to this mixture, preferably in a range from 0-100 times by weight of the sum of I and II, most preferably between 0-10 times by weight. Within the framework of this invention the catalytically active subunits embrace the subunit itself optionally-combined with a linker between active side and polymer backbone. Such linking molecules are known to the skilled man and could be introduced into the molecule in question by processes known in the art according to the demands of space and electronic behaviour of the considered reaction (Scheme 1). Linkers, which are feasible, are alkylenic, arylenic or silylenic linkers for example. In DE 19910691.6 further possible linkers are disclosed. A further olefinic compound may be any organic molecule, which possess at least one double bond and which is known to the skilled worker to be suitable to react in ring opening metathesis reaction. This olefinic compound serves as a mean for copolymerization and dilutes the number of active sides per unit of length within the polymeric backbone. Therefore, this is another tool to adopt the catalysts of the invention to the most suitable demands of space necessary for the reaction in question.. Preferred compounds are ethylene, propene, butene, pentene, isobutene, isopropene and cyclic olefines like cyclopropene, cyclobutene, cyclopentene, cyclopentadiene, cyclohexene, cyclopheptene and the like. Even bicyclic olefinic compounds come into consideration, like norbornene, azulene, etc. Preferred are catalysts characterised in that R is Ph, X is O, R 1 , R 2 form together a =O-group, R 3 is R 4 , O(C 1 -C 8 )-Alkyl, R 4 is OR 7 , R 7 is a catalytically active group of alcohols, amines, phospines or other, sulfur or phosphor containing groups. More preferably the catalysts of the invention exhibit a residue R 7 , which is a compound selected from the group of catalysts mentioned in DE 10003110 suitable for the considered families of chemical reactions. Most preferred are catalysts selected from the group of Taddol-ligands (Seebach, Helv. Chim. Acta, 1996, 79, 1710f.), chiral salene-complexes (Salvadori, Tetrahedron Lett., 37, 1996, 3375f.), ligands for Sharpless-epoxidation like dihydrochinidines (Bolm, Angew. Chem., 1997, 773f.), 1,2-diaminoalcohols (Wandrey, Tetrahedron: Asymmetry, 1997, 8, 1529f.) or catalytic hydrogenation catalysts like 1,2-diphosphane-ligands, for example DIOP, DIPAMP; BPPFA, BPPM, CHIRAPHOS, PROPHOS, NORPHOS, BINAP, CYCPHOS, SKEWPHOS (BDPP), DEGPHOS, DuPHOS und PNNP. Most preferred are catalysts mentioned in EP 305180. As already mentioned the catalysts of the invention can be produced by technics known to the artisan with or without linkers between the active subunit and the backbone. Advantageously, a compound of formula I wherein U, W are Cl, Br, I, OR Y, Z are PR' 3 , NR' or U R' is (C 6 -C 18 ) -Aryl, (C 3 -C 18 ) -Heteroaryl, (C 3 -C 8 )-Cycloalkyl, (C 1 -C 8 ) -Alkyl, (C 6 -C 18 ) -Aryl- (C 1 -C 8 ) -Alkyl, (C 3 -C 18 )-Heteroaryl-(C 1 -C 8 )-Alkyl, (C 7 -C 19 ) -Aralkyl, (C 4 -C 19 ) -Heteroaralkyl, M is Ru, Mo R is (C 6 -C 18 )-Aryl, (C 3 -C 18 )-Heteroaryl, (C 3 -C 8 )-Cycloalkyl, (C 3 -C 8 ) -Cycloalkenyl, H, (C 1 -C 8 ) -Alkyl, (C 2 -C 8 ) -Alkenyl, is reacted in a non-reactive organic solvent or solvent mixture with a bicyclic olefin of formula II wherein X is O, NR 5 , C(R 5 ) 2 , S, POR 6 , PR 6 , R 1 , R 2 are independently of each other H, (C 1 -C 8 )-Alkyl, (C 2 -C 8 ) -Alkenyl, (C 2 -C 8 )-Alkynyl, (C 6 -C 18 ) -Aryl, (C 7 -C 19 ) - Aralkyl, (C 3 -C 18 )-Heteroaryl, (C 4 -C 19 )-Heteroaralkyl, (C 3 -C 8 )-Cycloalkyl, (C 3 -C 8 )-Cycloalkenyl, (C 6 -C 18 ) -Aryl-(C 1 -C 8 ) -Alkyl, (C 3 -C 18 )-Heteroaryl-(C 1 -C 8 )-Alkyl, (C 3 -C 8 ) - Cycloalkyl-(C 1 -C 8 )-Alkyl, (C 1 -C 8 )-Alkyl-(C 3 -C 8 )-Cycloalkyl, or form together a =O-group, R 3 , R 4 are independently of each other OR 1 , SR 1 , NR 5 R 1 , OR 7 , SR 7 , NR 5 R 7 provided that at least one residue R 3 , R 4 bears a group R 7 , R 5 is R 1 , R 6 is R 1 provided that it can not be H and R 7 is a catalytically active group, and optionally with a further olefinic compound III, preferably a cycloolefinic compound. Preferably a process is chosen, in which I and II show R is Ph, X is O, R 1 , R 2 form together a =O-group, R 3 is R 4 , O(C 1 -C 8 )-Alkyl, R 4 is OR 7 , R 7 is a catalytically active group. Most preferred is a process, where R 7 is a compound selected from the groups presented above. A feasible non-reactive organic solvent or part of the solvent mixture is a haloalkane, like for example dichloromethane and the like. The process is preferably conducted at temperatures between -20°C to 50°C, more preferably between -5°C and 30°C and most preferably between 5°C and 25°C. The catalysts according to the invention can be used for organic synthesis purposes. Preferred is their use in a reactor, which is able to hold back the polymerically enlarged homogeneous catalysts, while permitting the starting material to be introduced in and the product to be released from the reactor. More preferably these catalysts are used in a membrane reactor. Such reactions and reaction conditions are specified in DE 19910691.6. In case of using optically enriched catalysts according to. the invention a use in a process for the production of optically active compounds is most preferred. The following scheme discloses one possible way to synthesise catalysts of this invention. The catalyst made are employed in a diethylzinc addition to benzaldehyde as a probe reaction. The results are shown down under in table 1. It can be deduced from these experiments that catalysts of the invention can serve as versatile tools in homogeneous catalytic organic reaction. It is envisaged that each single structure of chiral catalysts of this invention denotes all and every possible diastereomers whether in their racemic form or optically enriched. Every of such diastereomers embraces and discloses the possible enantiomers, too. There come into consideration as linear or branched (C 1 -C 8 )-alkyl radicals methyl, ethyl, n-propyl, isopropyl, n-butyl, isobutyl, sec-butyl, tert-butyl, pentyl, hexyl, heptyl or octyl, as well as all the isomers of constitution. The linear or branched (C 2 -C 8 ) -alkenyl radical includes all substituents listed above in connection with the (C 1 -C 8 )-alkyl radical with the exception of the methyl radical, there being at least one double bond present in those radicals. The scope of (C 2 -C 8 )-alkynyl corresponds to that of (C 2 -C 8 )-alkenyl, but at least one triple bond must be present in that case. (C 3 -C 8 )-cycloalkyl is to be understood as being cyclopropyl, cyclobutyl, cyclopentyl, cyclohexyl or cycloheptyl radicals. (C 3 -C 8 )-cycloalkenyl denotes cycloalkylic radicals comprising one or more double bonds within the residue. (C 6 -C 18 )-aryl denotes arylic species with 6 to 18-C-atoms, like phenyl, naphthyl, phenanthryl. (C 7 -C 19 )-aralkyl are arylic radicals connected via a (C 1 -C 8 )-alkyl radikal with the molecule of respect, for example benzyl, 1-, 2-phenylethyl, naphthylmethyl. (C 3 -C 18 )-heteroaryl are arylic molecules in which at least one C-atom is substituted by a heteroatom like N, O, P, S. Molecules, which come into consideration, are pyrolyl, furyl, pyridyl, imidazolyl etc. (C 4 -C 19 )-heteroaralkyl are heteroarylic species bonded via a (C 1 -C 8 )-alkyl radical with the molecule of respect, like furfuryl, pyrolylmethyl, pyridylmethyl, furyl-1-, 2-ethyl, pyrolyl-1-, 2-ethyl. Experimental Section: General. n -Butyl lithium was purchased from Merck-Schuchardt as a 1.6 M solution in n -hexane, diethylzinc was provided as a generous gift from Witco. Bis(tricyclohexylphosphine)benzyliden-ruthenium(II) dichloride was purchased from Strem, (-)- B -chlorodiisopinocampheylborane 'DIP-Chloride™ from Aldrich. Tetrakis(triphenylphosphin)palladium(0) was a donation from Degussa. THF, diethylether, and toluene were distilled from sodium/benzophenone ketyl radical under argon. Dichloromethane was distilled from CaH 2 under argon. All other solvents were reagent grade and used as received. If not stated otherwise, the notion 'standard work-up' refers to quenching the reaction mixture with water, followed by extraction with an organic solvent. Washing of the organic layer subsequently with brine and water, drying of the combined organic phases with anhydrous MgSO 4 and evaporation of the solvent under reduced pressure afforded the crude product. All syntheses of the monomeric and polymeric catalysts and all catalyses were repeated at least twice in order to ensure reproducibility. Given yields are average values. The enantiomeric excess of 1-phenylpropanol was determined by means of HPLC using a chiral column (Chiralcel OD). I. Syntheses of the monomeric precursors exo -7-Oxabicyclo[2.2.1]hept-5-ene-2,3-dicarboxylic acid anhydride (6): A dry Schlenk flask under argon was filled with maleic anhydride (9.81 g, 100 mmol) and 50 mL of toluene. The mixture was warmed to 80°C, and then furan (10.21 g, 150 mmol) was added. After stirring for 24 h at room temperature the mixture was cooled to 0°C, and the solid product was filtered off and washed with 30 mL methyl tert -butylether. Drying in vacuo furnished 11.78 g (71%) of 6 as a fine white powder. Mp: 116°C (decomposition). 1 H NMR (300 MHz, CDCl 3 ): δ 3.16 (s, 2H); 5.43 (s, 2H); 6.55 (s, 2H). 13 C NMR (75 MHz, CDCl 3 ): δ 48.7; 82.1; 136.9; 169.9. Reference: Furdik, M.; Drabek, J. Tetrahedron 1973, 29 , 2445. rac -7-Oxabicyclo[2.2.1]hept-5-ene-2,3-dicarboxylic acid monomethylester (8): Triethylamine (0.51 g, 5 mmol) was added dropwise to a suspension of exo -7-oxabicyclo[2.2.1]hept-5-ene-2,3-dicarboxylic acid anhydride (6) (4.15 g, 25 mmol) in 25 mL of methanol and the mixture was stirred for 24 h at room temperature. After removal of methanol, the residue was dissolved in 25 mL of dichloromethane, and the resulting solution was washed subsequently with 7 mL of 1 M hydrochloric acid and 10 mL brine, followed by drying the organic phase with anhydrous MgSO 4 . Evaporation of the solvent under reduced pressure yielded 3.37 g (68%) of 8 as a pale yellow solid. Mp: 110°C. 1 H NMR (300 MHz, CDCl 3 ): δ 2.86 (s, 2H); 3.71 (s, 3H); 5.27 (s, 1H); 5.31 (s, 1H); 6.48 (s, 2H); 10.20 (s, 1H). 13 C NMR (75 MHz, CDCl 3 ): δ 46.9; 47.2; 52.3; 80.4; 80.6; 136.4; 136.8; 171.8; 177.3. Reference: Guanti, G.; Narisano, E.; Riva, R.; Thea, S. Tetrahedron Lett . 1986 , 38 , 4639. Synthesis of ( R )-1-{6-[4-(2-hydroxyethoxy)phenyl]pyridin-2-yl}-2,2-dimethylpropanol (5): a) 4-( tert -Butyl dimethylsiloxy)phenylboronic acid: Magnesium turnings (0.53 g, 22 mmol) and 20 mL of THF were placed into a two-necked flask. Next, tert -butyldimethylsilyloxyphenyl bromide(5.64 g, 19.6 mmol) was added and the mixture was heated under reflux for 2 h before it was cooled to room temperature. The brown mixture was added to a solution of trimethyl borate (2.43 g, 24 mmol) in 5 mL of THF through a dropping funnel at -78°C and allowed to warm to room temperature overnight. After hydrolysis with 90 mL of ca. 0.1 M hydrochloric acid followed by standard work-up with methyl tert -butyl ether, the brown residue was washed with 20 mL of cold hexane, and the resulting white product (3.86 g, 78%) was dried in vacuo. Mp: 175°C. 1 H NMR (300 MHz, CDCl 3 ): δ 0.25 (s, 6H); 1.01 (s, 9H); 6.95 (d, J = 8.5 Hz, 2H); 8.11 (d, J = 8.5 Hz, 2H). 13 C NMR (75 MHz, CDCl 3 ): δ -4.3; 18.1; 25.7; 119.8; 137.5; 159.8. Reference: Bolm, C.; Derrien, N.; Seger, A. Synlett 1996 , 387. b) (R)-1-[6-(4-Hydroxyphenyl)-pyridin-2-yl]-2,2-dimethylpropanol (4b) : Tetrakis-(triphenylphosphine)palladium(0) (1.16 g, 1 mmol) were dissolved in 50 mL of toluene in a two-necked flask under argon. Then, ( R )-1-(6-bromopyridin-2-yl)-2,2-dimethylpropanol (4.88 g, 20 mmol) was added to the yellow suspension. Subsequently, solutions of sodium carbonate (4.24 g, 40 mmol) in 20 mL of distilled water and 4-( tert -butyldimethylsiloxy)phenylboronic acid in 25 mL of methanol were added and the mixture was heated under reflux for 6.5 h. After cooling to room temperature the reaction was quenched with 120 mL of saturated sodium carbonate solution and 20 mL of aqueous ammonia. The aqueous layer was extracted five times with dichloromethane, and the combined organic phases were washed with brine. Drying with anhydrous MgSO 4 and evaporation of the solvents under reduced pressure gave the crude product which was dissolved in 50 mL of THF. Next, 22 mL of TBAF (1 M in THF) were added' and the mixture was stirred for 5 h at room temperature. Standard work-up with dichloromethane gave crude 4b which was purified by column chromatography followed by recrystallization from toluene/hexane (2:1) to give 4.35 g (85%) of 4 b as white needles. The enantiomeric excess was determined by means of HPLC using a chiral column [Chiracel OD; eluent: n -heptane/ iso -propanol = 85:15; flow: 1.0 mL/min; t R = 8.2 min ( R ); 10.3 min ( S )] Mp: 130°C. [α] D = -18.4 (c= 2.32, acetone). 1 H NMR (300 MHz, CDCl 3 ): δ 0.98 (s, 9H); 4.46 (s, 1H); 5.50 (s, 1H); 6.96 (d, J = 8.8 Hz, 2H); 7.06 (dd, J = 7.8 Hz, 0.8 Hz, 1H); 7.57 (dd, J = 8.0 Hz, 0.8 Hz, 1H); 7.67 (dd, J = 7.7 Hz, 1H); 7.89 (d, J = 8.8 Hz, 2H). 13 C NMR (75 MHz, CDCl 3 ): δ = 26.0; 36.3; 80.0; 115.8; 118.4; 120.5; 128.3; 130.9; 136.6; 155.1; 157.6; 158.4. MS (70 eV): m/z (%) 257 (M, 4), 200 (100). IR (KBr): 1613, 1571, 1519, 1455, 1282, 1173, 1052, 807 cm -1 . Anal. Calcd. for C 16 H 19 NO 2 : C, 74.68; H, 7.44; N, 5.44. Found: C, 74.59; H, 7.37; N, 5.34. c) ( R )-1-{6-[4-(2-Hydroxyethoxy)phenyl]pyridin-2-yl}-2,2-dimethylpropanol (5): A dry 250 mL three-necked flask was charged with ( R )-1-[6-(4-hydroxyphenyl)-pyridin-2-yl]-2,2-dimethylpropanol (4b) (2.54 g, 9.9 mmol), cesium carbonate (6.43 g, 19.8 mmol) and 100 mL of acetonitrile. Next, 2-bromoethyl- tert -butyldimethylsilyl ether was added through a dropping funnel. The mixture was heated under reflux for 2 h and stirred for additional 14 h at room temperature. After standard work-up with ethyl acetate the crude product was dissolved in 25 mL of THF and 11 mL of TBAF (1 M in THF) were added. After stirring for 1 h at room temperature, the solution was quenched with 50 mL of water and standard work-up with dichloromethane followed by column chromatography (SiO 2 , eluent: ethyl acetate/hexanes =1:1) yielded 2.46 g (83%) of 5 as a white powder. Mp: 104°C. [α] D = -14.4 (c = 2.28, acetone). 1 H NMR (300 MHz, CDCl 3 ): δ 0.96 (s, 9H); 2.36-2.40 (m, 1H); 3.95-4.01 (m, 2H); 4.11-4.15 (m, 2H); 4.39 (d, J = 7.4 Hz, 1H); 4.66 (d, J = 7.4 Hz, 1H); 7.01 (d, J = 8.8 Hz, 2H); 7.06 (dd, J = 7.97 Hz, 0.8 Hz, 1H); 7.57 (dd, J = 7.97 Hz, 0.8 Hz, 1H); 7.66 (m, 1H); 7.95 (d, J = 8.8 Hz, 2H). 13 C NMR (75 MHz, CDCl 3 ): δ 26.0; 36.3; 61.4; 69.4; 80.2; 114.7; 118.2; 120.7; 128.2; 131.9; 136.4; 155.0; 159.3; 159.7. MS (70 eV): m/z (%) 301 (M, 7), 244 (100). IR (KBr): 1608, 1576, 1516, 1453, 1255, 1174, 1046, 812 cm -1 . Anal. Calcd. for C 18 H 23 NO 3 : C, 71.73; H, 7.69; N, 4.65. Found: C, 71.59; H, 7.68; N, 4.56. ( R,R )-7-Oxabicyclo[2.2.1]hept-5-ene-(2- exo ,3- exo )-dicarboxylic acid bis-(2-{4- [6-(1-hydroxy-2,2-dimethylpropyl)-pyridin-2-yl]phenoxy}ethyl)ester (7): A dry 25 mL Schlenk flask was charged with exo -7-oxabicylo[2.2.1]hept-5-ene-(2- exo ,3- exo )-dicarboxylic acid anhydride (6) (415 mg, 2.5 mmol), ( R )-1-{6-[4-(2-hydroxyethoxy)phenyl]pyridin-2-yl}-2,2-, dimethylpropanol (5) (1.50 g, 5 mmol) and 15 ml of dichloromethane. Next, triethylamine (759 mg, 7.5 mmol), 4-DMAP (122 mg, 1 mmol) and 2-chloro-1-methylpyridinium iodide (766 mg, 3 mmol) were added, and the resulting yellow mixture was stirred for 48 h at room temperature. Standard work-up with dichloromethane followed by column chromatography (SiO 2 , eluent: methyl tert -butyl ether) of the crude product yielded 1.59 g (85%) of 7 as a white solid, which was stored at 0°C. Mp: 70-75°C. [α] D = -12.3 (c = 2.10, toluene). 1 H NMR (300 MHz, CDCl 3 ): δ 0.95 (s, 18H); 2.89 (s, 2H); 4.15-4.22 (m, 4H); 4.36-4.40 (m, 2H); 4.44-4.48 (m, 4H); 4.59-4.65 (m, 2H); 5.28 (s, 2H); 6.45 (s, 2H); 6.95-7.00 (m, 4H); 7.04-7.08 (m, 2H); 7.52-7.56 (m, 2H); 7.61-7.67 (m, 2H); 7.90-7.97 (m, 4H). 13 C NMR (75 MHz, CDCl 3 ): δ 26.0; 36.3; 46.8; 63.5; 65.9; 80.1; 80.8; 114.8; 118.2; 120.7; 128.1; 132.0; 136.3; 136.7; 154.8; 159.3; 159.4; 171.4. MS (70 eV): m/z (%) 625 (M-C 4 H 4 O-C 4 H 9 , 18), 244 (100). IR (KBr): 1747, 1608, 1571, 1515, 1453, 1249, 1180, 1055, 813 cm -1 . Anal. Calcd. for C 44 H 50 N 2 O 9 : C, 70.38; H, 6.71; N, 3.73. Found: C; 70.10; H, 6.72; N, 3.51. 7-Oxabicyclo[2.2.1]hept-5-ene-(2- exo ,3- exo )-dicarboxylic acid methyl ( R )-(2-{4-{6-(1-hydroxy-2,2-dimethyl-propyl)-pyridin-2-yl]phenoxy}ethyl)ester (9): A dry 100 mL Schlenk flask was filled with 7-oxabicyclo[2.2.1]hept-5-ene-(2- exo ,3- exo )-dicarboxylic acid monomethyl ester (8) (595 mg, 3 mmol), ( R )-1-{6-[4-(2-hydroxyethoxy)phenyl]pyridin-2-yl}-2,2-dimethylpropanol (995 mg, 3.3 mmol) and 20 mL of dichloromethane. Next, 4-DMAP (55 mg, 0.45 mmol) and DCC (743 g, 3.6 mmol) were added and the mixture was stirred over a period of 24 h at room temperature. Standard work-up with dichloromethane followed by column chromatography (SiO 2 , eluent: ethyl acetate/hexane = 2:1) afforded 9 as a white solid (1.35 g, 94%). Mp: 54-60°C. [α] D = -7.2 (c =2.08, toluene). 1 H NMR (300 MHz, CDCl 3 ): δ 0.96 (s, 9H); 2.86 (s, 2H); 3.69 (s, 3H); 4.22-4.27 (m, 2H); 4.36-4.40 (m, 1H); 4.47-4.52 (m, 2H); 4.61-4.66 (m, 1H); 5.26-5.28 (m, 2H); 6.45 (s, 2H); 6.99-7.03 (m, 2H); 7.05-7.09 (m, 1H); 7.56-7.60 (m, 1H); 7.64-7.69 (m, 1H); 7.94-7.98 (m, 2H). 13 C NMR (75 MHz, CDCl 3 ): δ 26.0; 36.3; 46.7; 47.0; 52.3; 63.4; 65.9; 80.1; 80.5; 80.6; 114.8; 118.2; 120.7; 128.2; 132:0; 136.4; 136.6; 136.7; 154.8; 159.3; 159.4; 171.5; 171.9. MS (70 eV): m/z (%) 481 (M, 2), 356 (100). IR (KBr): 1747, 1609, 1571, 1516, 1435, 1248, 1180, 1054, 813 cm -1 . Anal. Calcd. for C 27 H 31 NO 7 : C, 67.20; H, 6.49; N, 2.91. Found: C, 67.35; H, 6.82; N, 3.12. II. Polymerization of bicyclic olefins 7 and 9 A dry Schlenk flask under argon was charged with RuCl 2 (CHC 6 H 5 )[P(C 6 H 11 ) 3 ] 2 (1) which was dissolved in 3 mL of dichloromethane, and a solution of the bicyclic olefin (20, 50 or 100 equiv. of 7; 50 equiv. of 9) in 7 mL of dichloromethane was added. Stirring the mixture for 24 h at room temperature was followed by the addition of 0.3 mL of ethyl vinylether. After having it stirred for an additional hour, the solution was filtered (silica gel, dichloromethane) to remove the ruthenium catalyst and the solvent was evaporated. The grey/green solids were analyzed by 1 H NMR spectroscopy and subjected to GPC. NMR-spectrospcopy: After the reaction no double bond signals for the bicyclic monomers (δ 6.45 ppm) can be detected anymore. Instead, broad signals at 5.5 and 5.8 ppm for the olefinic protons in the polymer were observed. For P1 , P2 and P3 : 1 H NMR (300 MHz, CDCl 3 ): δ 0.90 (s); 2.98-3.20 (m); 4.05 (s); 4.36 (s); 4.50-4.72 (m); 5.17 (s); 5.52 (s); 5.84 (s); 6.80-7.04 (m); 7.38-7.62 (m); 7.76-7.92 (m); all signals are broad. For P4 : 1 H NMR (300 MHz, CDCl 3 ): δ 0.93 (s); 3.10 (s); 3.59 (s); 4.15 (s); 4.32-4.50 (m); 4.55-4.78 (m); 5.10 (s); 5.58 (s); 5.90 (s); 6.88-7.10 (m); 7.44-7.70 (m); 7.86-800 (m); all signals are broad. GPC analysis: Waters HPLC-pump type 510, flow: 1.0 mL/min, eluent: THF p.a., teflon-membrane filter 0.2 µm, 2 columns, each with a length of 500 mm and a diameter with Jordi DVB-gel of 1000Å and 100000 Å, respectively; Melz RI-detector LCD 201, calibration: PSS-Polystyrolstandards 500-750.000. Polymer yields and characterization Polymer Monomer Monomer equivalents Amount of catalyst 1 (mg / µmol) Polymer yield [%] M n M w M w / M n P1 7 20 24.8/30 49 15500 19100 1.2 P2 7 50 9.4/11.4 98 27700 38100 1.4 P3 7 100 5.0/6.0 35 32200 53100 1.7 P4 9 50 8.4 /10.2 99 29800 33300 1.1 III. Diethylzinc addition to benzaldehyde (10) A dry Schlenk flask under argon was charged with 0.05 equiv. of the pyridinyl alcohol. The flask was evacuated twice and flushed with argon. Then, 5 mL of freshly distilled toluene were added followed by 1.5 equiv. of neat diethylzinc while stirred. After stirring for 20 min at room temperature, 1.0 equiv. of benzaldehyde (10) was added at the given temperature (see Table). The proceeding of the reaction was monitored by tlc. After full conversion of the aldehyde, the reaction was quenched by careful addition of 10 mL of 2 M HCl, and the resulting mixture was extracted three times with 25 mL of dichloromethane. The combined organic phases were washed with brine, dried over MgSO 4 , and the solvent was removed under reduced pressure. The crude product was purified by column chromatography (silica gel, hexane/methyl tert -butylether = 10:1) followed by Kugelrohr distillation to give 1-phenylpropanol (11) as a colorless oil. The enantiomeric excess of 11 was determined by HPLC on a stationary phase [CHIRALCEL OD, n -heptane/ iso -propanol = 98:2, 1.0 mL/min; t R = 17.2 min ( R ); 21.5 min ( S )], and the absolute configuration was determined by correlation of the optical rotation with the values reported in the literature (Soai, K.; Ookawa, A.; Kaba, T.; Ogawa, K.; J. Am . Chem. Soc. 1987 , 109, 7111). Reaction of benzaldehyde (10) and diethylzinc catalyzed by various pyridinyl alcohols Pyridinyl alcohol /polymer Amount of pyridinyl alcohol (mg/µmol ) Time [h] Yield of 11 [%] Ee of 11[%] 4a 15.0/62.1 4 91 87 5 15.0/49.8 24 86 83 7 16.8/44.6 24 72 79 9 38.1/79.1 24 89 80 P1 22.6/60.2 48 88 73 P2 23.1/61.5 48 83 73 P3 48.7/130.0 48 77 73 P4 35.3/73.0 48 78 71

Claims: Homogeneous catalysts obtainable by reacting a compound of formula I wherein U, W are Cl, Br, I, OR Y, Z are PR' 3 , NR' or U R' is (C 6 -C 18 ) -Aryl, (C 3 -C 18 ) -Heteroaryl, (C 3 -C 8 )-Cycloalkyl, (C 1 -C 8 ) -Alkyl, (C 6 -C 18 )-Aryl-(C 1 -C 8 )-Alkyl, (C 3 -C 18 )-Heteroaryl-(C 1 -C 8 )-Alkyl, (C 7 -C 19 )-Aralkyl, (C 4 -C 19 ) -Heteroaralkyl, M is Ru, Mo R is (C 6 -C 18 )-Aryl, (C 3 -C 18 )-Heteroaryl, (C 3 -C 8 )-Cycloalkyl, (C 3 -C 8 )-Cycloalkenyl, H, (C 1 -C 8 )-Alkyl, (C 2 -C 8 ) -Alkenyl, in a non-reactive organic solvent or solvent mixture with a bicyclic olefin of formula II wherein X is O, NR 5 , C(R 5 ) 2 , S, POR 6 , PR 6 , R 1 , R 2 are independently of each other H, (C 1 -C 8 ) -Alkyl, C 2 -C 8 )-Alkenyl, (C 2 -C 8 )-Alkynyl, (C 6 -C 18 )-Aryl, (C 7 -C 19 )-Aralkyl, (C 3 -C 18 )-Heteroaryl, (C 4 -C 19 )-Heteroaralkyl, (C 3 -C 8 )-Cycloalkyl, (C 3 -C 8 )-Cycloalkenyl, (C 6 -C 18 )-Aryl-(C 1 -C 8 ) -Alkyl, (C 3 -C 18 )-Heteroaryl-(C 1 -C 8 )-Alkyl, (C 3 -C 8 )-Cycloalkyl- (C 1 -C 8 ) -Alkyl, (C 1 -C 8 ) -Alkyl- (C 3 -C 8 )-Cycloalkyl, or form together a =O-group, R 3 , R 4 are independently of each other OR 1 , SR 1 , NR 5 R 1 , OR 7 , SR 7 , NR 5 R 7 provided that at least one residue R 3 , R 4 bears a group R 7 , R 5 is R 1 , R 6 is R 1 provided that it can not be H and R 7 is a catalytically active group, and optionally with a further olefinic compound III, preferably a cycloolefinic compound. Catalysts according to claim 1, characterised in that , R is Ph, R' is Ph, (C 1 -C 8 ) -Alkyl, X is O, R 1 , R 2 form together a =O-group, R 3 is R 4 , O(C 1 -C 8 )-Alkyl, R 4 is OR 7 , R 7 is a catalytically active group of alcohols, amines, phospines or other, sulfur or phosphor containing groups. Catalysts according to claim 1 and/or 2, characterised in that , R 7 is a compound selected from the group of Taddol-ligands, chiral salene-complexes, ligands for Sharpless-epoxidation like dihydrochinidines, 1,2-diaminoalcohols or catalytic hydrogenation catalysts like 1,2-diphosphane-ligands, for example DIOP, DIPAMP; BPPFA, BPPM, CHIRAPHOS, PROPHOS, NORPHOS, BINAP, CYCPHOS, SKEWPHOS (BDPP), DEGPHOS, DuPHOS und PNNP. Process for the production of homogeneous catalysts according to claim 1, characterised in that , a compound of formula I wherein U, W are Cl, Br, I, OR Y, Z are PR' 3 , NR' or U R' is (C 6 -C 18 )-Aryl, (C 3 -C 18 )-Heteroaryl, (C 3 -C 8 )-Cycloalkyl, (C 1 -C 8 ) -Alkyl, (C 6 -C 18 )-Aryl-(C 1 -C 8 )-Alkyl, (C 3 -C 18 )-Heteroaryl-(C 1 -C 8 )-Alkyl, (C 7 -C 19 )-Aralkyl, (C 4 -C 19 ) -Heteroaralkyl, M is Ru, Mo R is (C 6 -C 18 )-Aryl, (C 3 -C 18 )-Heteroaryl, (C 3 -C 8 )-Cycloalkyl, (C 3 -C 8 )-Cycloalkenyl, H, (C 1 -C 8 )-Alkyl, (C 2 -C 8 ) -Alkenyl, is reacted in a non-reactive organic solvent or solvent mixture with a bicyclic olefin of formula II wherein X is O, NR 5 , C(R 5 ) 2 , S, POR 6 , PR 6 , R 1 , R 2 are independently of each other H, (C 1 -C 8 )-Alkyl, (C 2 -C 8 )-Alkenyl, (C 2 -C 8 )-Alkynyl, (C 6 -C 18 )-Aryl, (C 7 -C 19 ) - Aralkyl, (C 3 -C 18 )-Heteroaryl, (C 4 -C 19 )-Heteroaralkyl, (C 3 -C 8 )-Cycloalkyl, (C 3 -C 8 )-Cycloalkenyl, (C 6 -C 18 ) -Aryl-(C 1 -C 8 )-Alkyl, (C 3 -C 18 )-Heteroaryl-(C 1 -C 8 )-Alkyl, (C 3 -C 8 )-Cycloalkyl- (C 1 -C 8 ) -Alkyl, (C 1 -C 8 ) -Alkyl- (C 3 -C 8 )-Cycloalkyl, or form together a =O-group, R 3 , R 4 are independently of each other OR 1 , SR 1 , NR 5 R 1 , OR 7 , SR 7 , NR 5 R 7 provided that at least one residue R 3 , R 4 bears a group R 7 , R 5 is R 1 , R 6 is R 1 provided that it can not be H and R 7 is a catalytically active group, and optionally with a further olefinic compound III, preferably a cycloolefinic compound. Process according to claim 4, characterised in that , R is Ph, X is O, R 1 , R 2 form together a =O-group, R 3 is R 4 , O(C 1 -C 8 )-Alkyl, R 4 is OR 7 , R 7 is a catalytically active group of alcohols, amines, phospines or other, sulfur or phosphor containing groups. Process according to claim 5 and/or 4, characterised in that , R 7 is a compound selected from the group presented by claim 3. Process according to one or more of claims 4 to 6, characterised in that , the non reactive organic solvent or part of the solvent mixture is a haloalkane, like dichloromethane. Process according to one or more of claims 4 to 7, characterised in that , the temperature during the process is from -20°C to 50°C, preferable between -5°C and 30°C. Use of the catalysts according to claim 1 for organic synthesis purposes. Use according to claim 9 in a reactor, which is able to hold back the polymeric catalysts, while permitting the starting material to be introduced in and the product to be released from the reactor. Use according to claim 10, where the reactor is a membrane reactor. Use according to one or more of claim 9 to 11, in a process for the production of optically active compounds provided that a optically active catalyst is used.

Inventors: BOLM CARSTEN PROF, BROZIO JOERG, DINTER CHRISTIAN, HOECKER HARTWIG PROF, SEGER ANDREAS, BOLM, CARSTEN PROF., BROZIO, JOERG, DINTER, CHRISTIAN, HOECKER, HARTWIG PROF., SEGER, ANDREAS, Brozio, Jörg, Höcker, Hartwig Prof.
Applicants: DEGUSSA, DEGUSSA AG
Application year: 2000
Main classification: B01J32
IPC codes: C08G61, C07F15