LOW MELT VISCOSITY AMORPHOUS COPOLYESTERS WITH ENHANCED GLASS TRANSITION TEMPERATURES

Abstract: The invention relates to an amorphous copolyester having a maximum melt viscosity at 1 radian/second and at about 260 to about 290 DEG C of about 12000 poise, a glass transition temperature ranging from about 88 DEG C to about 120 DEG C, and an inherent viscosity of at least about 0.6 dl/g. The amorphous copolyesters comprise the reaction product of a diol component and a dicarboxylic acid component. The diol component comprises residues of from about 5.0 to about 50 mole % of 2,2'-(sulfonylbis(4,1-phenyleneoxy))-bis(ethanol) which has chemical formula (I) and from about 50 to about 95 mole % of a mixture of at least two diols selected from the group consisting of ethylene glycol, neopentyl glycol, 1,3-propanediol, 1,4-butanediol, 1,4-cyclohexanedimethanol, and mixture thereof. The dicarboxylic acid component comprises residues of terephthallic acid, isophthalic acid, 1,4-cyclohexanedicarboxylic acid, 2,6-naphtalene dicarboxylic acid and mixtures thereof. The amorphous copolyesters according to the invention have relatively low melt viscosities and high glass transition temperatures. Because of the low melt viscosities and relatively high glass transition temperatures, copolyesters with increased IV or molecular weight can easily be obtained. The copolyesters according to the invention can be used for molded or extruded articles, sheets, and films. Accordingly, the invention also relates to molded and extruded articles, sheets, and films made from a copolyester as described above.

Description: LOW MELT VISCOSITY AMORPHOUS COPOLYESTERS WITH ENHANCED GLASS TRANSITION TEMPERATURES FIELD OF THE INVENTION The invention relates to amorphous copolyesters containing 2,2'-(sulfonylbis(4,l- phenyleneoxy))bis(ethanol). The amorphous copolyesters exhibit enhanced heat distortion temperatures and glass transition temperatures without a significant increase in viscosity at low shear rates. BACKGROUND OF THE INVENTION Amorphous copolyesters are generally defined as copolyesters that do not show a substantial melting point by differential scanning calorimetry when scanned at a rate of 20°C/min. These copolyesters are typically based on terephthalic acid, isophthalic acid, ethylene glycol, neopentyl glycol and 1,4-cyclohexanedimethanol. It is generally known in the art that amoφhous copolyesters possess a combination of desirable properties, such as excellent clarity and color, toughness, chemical resistance and ease of processing. Accordingly, such copolyesters are known to be useful for the manufacture of extruded sheets, packaging materials, and parts for medical devices. However, when compared to other families of materials such as polycarbonates based on bisphenol A and certain acrylic resins like polymethyl methacrylate, amoφhous copolyesters generally have lower glass transition temperatures (Tg) and lower heat distortion temperatures (HDT). The lower Tg and HDT of amoφhous polyesters inhibit their application where resistance to thermal deformation is important, for example, green house panels, skylights and other products prepared by extrusion or injection molding processes. It is also important that amoφhous copolyesters have a low shear melt viscosity. Unlike semi-crystalline polyesters, where ultimate molecular weight values can be raised by polymerization in the crystalline or solid state, high molecular weight amoφhous copolyesters must be obtained directly in the melt phase polymerization. It is not possible or it is too expensive to render the amoφhous copolyesters into a crystalline pellet or particle form. Further, when heated to the temperatures required for solid state polymerization, amoφhous pellets or particles flow together and stick together. Accordingly, there is a need for amoφhous copolyesters having sufficiently low- shear melt viscosities allowing the copolyesters to flow through the reactor at a practical rate allowing the copolyesters to build to a useful molecular weight. It is known in the art that the molecular weight of copolyesters can be conveniently measured in terms of its inherent viscosity ("IV"). Generally, an IV of 0.65 or higher is necessary for useful mechanical properties. Further, the maximum melt viscosity at 1 radian/second (shear rate) generally ranges from about 10,000 poise to about 12,000 poise at the temperature of the melt phase polymerization which is commonly in the range of about 260 to about 290°C. Crystalline copolyesters with good heat resistance and high strength are disclosed by Japanese Patent No. 08295731. These copolyesters are based on terephthalic acid as the acid component and a mixture of 1 ,4-cyclohexanedimethanol, ethylene glycol, and ethylene oxide adducts of bisphenol as the glycol component. Amoφhous copolyesters, however, are not disclosed. A process for preparing polyesters with good transparency and useful in the production of bottles and films is disclosed by Japanese Patent No. 08283398. The process comprises the use of a specific antimony compound as a polycondensation catalyst. Polyester compositions for use in the preparation of optical instruments are disclosed by Japanese Patent No. 4173837. These copolyester compositions comprise an acid component consisting of terephthalic acid and a diol component consisting of 4,4'-bis(β-hydroxyethoxy)-diphenylsulfone (2,2'-(sulfonylbis-(4, 1 - phenyleneoxy))bis(ethanol)) and at least one aliphatic or alicyclic diol having from 2 to 12 carbon atoms and containing a specific combination of at least one metal and phosphorous. According to this Japanese patent, the specific combination of metal and phosphorous is necessary to obtain polyesters with sufficient transparency, hue, Tg, and heat resistance. Japanese Patent No. 50096692 relates to a process for preparing polyesters from (A) a bifunctional carboxylic acid component composed primarily of terephthalic acid and/or an ester forming derivative thereof, (B) a diol with an aromatic nuclei composed primarily of 4,4'-bis-(β-hydroxyalkoxy)-diphenylsulfone (2,2'-(sulfonylbis-(4,l- phenyleneoxy))bis(ethanol)) and another diol. According to this Japanese patent, specific property limitations occur when a third diol, such as neopentyl glycol is incoφorated. Polyester sheets composed of ethylene glycol based glycols and terephthalic acid based dicarboxylic acids and containing diphenylsulfone and cyclohexane groups are disclosed by Japanese Patent No. 5279464. However, in order to obtain polyesters with superior transparency and heat resistant properties, the polyesters must contain both diphenylsulfone and cyclohexane groups at low levels. U.S. Patent No. 5,183,863 discloses viscoelastic resin compositions for vibration damping material. The resin comprises (A) at least one amoφhous polyester resin of low specific gravity in which more than 40 mole % of the dibasic acid moiety is of aromatic type, (B) at least one amoφhous polyester resin of high specific gravity in which more than 80 mole % of the dibasic acid is of aromatic type, and at least one hardener. As shown by Table 1 of the patent, the polyester resins according to this patent have relatively low Tg values ranging from -33 to 68 °C U.S. Patent Nos. 5,356,989 and 5,510,417 disclose aqueous dispersions suitable for use as coatings, paints, or adhesives which comprises a polyester resin, a water soluble organic compound, water, and a neutralizer. The polyester resins contain a polycarboxylic acid component and a polyol component. The glass transition temperature of the polyester resins according to these patents, however, range from - 30°C to 80°C. Copolyesters randomly composed of a first repeating unit containing a naphthalene ring structure and a second containing a naphthalene ring and an additional aryl ether linkage incoφorated into the main chain are disclosed by U.S. Patent No. 5,663,238. According to this patent, the copolyesters have improved solubility and are useful in various applications such as paints, varnishes, and structural adhesives. However, these properties can only be obtained with the specific combination of naphthalene and additional aryl ether linkage. Accordingly, there remains a need for high IV and low melt viscosity amoφhous copolyesters having sufficiently high glass transition temperatures and enhanced heat distortion temperatures yielding copolyesters with enhanced mechanical properties, i.e., toughness, without requiring the specific parameters described above. The invention answers this need. SUMMARY OF THE INVENTION It has been discovered that when the diol component of an amoφhous copolyester comprises residues of from about 5 to about 50 mole % of a 2,2'-(sulfonylbis (4,l-phenyleneoxy))-bis(ethanol), the melt viscosities and glass transition temperatures of such copolyesters are improved. Indeed, the invention relates to an amoφhous copolyester having a maximum melt viscosity at 1 radian/second and at about 260 to about 290°C of about 12,000 poise; a glass transition temperature ranging from about 88 °C to about 120°C; and an inherent viscosity of at least about 0.6. Such amoφhous copolyesters comprise the reaction product of a diol component and a dicarboxylic acid component. The diol component comprises residues of from about 5 to about 50 mole % of 2,2'-(sulfonylbis (4,l-phenyleneoxy))-bis(ethanol) and from about 50 to about 95 mole % of a mixture of at least two diols selected from ethylene glycol, neopentyl glycol, 1,3-propanediol, 1,4-butanediol, 1,4-cyclohexanedimethanol, and mixtures thereof, wherein the total diol component is based on 100 mole %. The dicarboxylic acid component of the copolyesters according to the invention comprsies residues of terephthalic acid, isophthalic acid, 1 ,4-cyclohexanedicarboxylic acid, 2,6-naphthalene dicarboxylic acid, and mixtures thereof. Because the copolyesters according to the invention suφrisingly have relatively low melt viscosities at low shear rates, they can be readily prepared in conventional low- shear melt phase polyester manufacturing equipment. Further, due to the low melt viscosities the IV or molecular weight of the copolyesters according to the invention is easily increased to yield copolyesters with useful mechanical properties, i.e., toughness. In addition, because the copolyesters of the invention have relatively high glass transition temperatures and heat distortion temperatures, they can be used to prepare molded or extruded articles and sheets. Accordingly, the invention also relates to molded and extruded articles, sheets, and films made from a copolyester as described above. Additional objects and advantages of the invention are discussed in the detailed description which follows, and will be obvious from that description, or may be learned by practice of the invention. It is to be understood that both this summary and the following detailed description are exemplary and explanatory only and are not intended to restrict the invention in any way. DETAILED DESCRIPTION OF THE INVENTION The invention relates to an amoφhous copolyester having a maximum melt viscosity at 1 radian/second (shear rate) and at about 260 to about 290°C of about 12,000 poise; a glass transition temperature ranging from about 88°C to about 120°C; and an inherent viscosity of at least about 0.6. As part of its diol component, the amoφhous copolyesters comprise residues of 2,2'-(sulfonylbis (4, 1 -phenyleneoxy))bis(ethanol) ("BDS") which has the following chemical formula: The presence of BDS provides the copolyester with enhanced glass transition temperatures and heat distortion temperatures while suφrisingly maintaining the relatively low shear rate melt viscosities of commercial amoφhous copolyesters. The amoφhous copolyesters of the invention are the reaction product of a diol component and a dicarboxylic acid component, as described below. The diol component comprises residues of from about 5 to about 50 mole %, more preferably from about 10 to about 50 mole%, of BDS and about 50 to 95 mole %, more preferably from about 50 to about 90 mole%, of a mixture of at least two diols selected from the group consisting of ethylene glycol, neopentyl glycol, 1,3-propanediol, 1 ,4-butanediol, 1 ,4-cyclohexanedimethanol, and mixtures thereof. In a preferred embodiment, the diol component comprises residues of from about 10 to about 50 mole % BDS and from about 50 to about 90 mole % of a mixture at least two diols selected from the group consisting of ethylene glycol, neopentyl glycol, cyclohexanedimethanol, and mixtures thereof. While the mole ratio of the diols in the mixture of at least two diols may vary as long as the desired properties discussed above are achieved, the minimum amount of any particular diol should be at least 1 mole %. The mole % of each diol, including BDS and the diols from the mixture of at least two diols in the diol component adds up to a total of 100 mole %. For example, when the diol component contains BDS and a mixture of two other diols (as discussed above), the diol component of the amoφhous copolyester of the invention can easily be represented by the following formula: (X)+(Y)+(Z) In the formula, X is the mole % of BDS which ranges from 5 to 50, as discussed above. Where the mixture of at least two diols in the amoφhous copolyester contains only two diols, Y and Z represent the mole % of the two diols and range from 50 to 95 mole %. In such a preferred embodiment, the mole ratio of Y to Z may vary widely as long as an amoφhous copolyester with the desired properties is achieved. Generally, for example, the mole ratio of Y to Z ranges from 1 :94 to 1 :1. For example, as illustrated by the examples below, the mole ratio of Y to Z can range from 1 :2, 1 :3, 1 :4, 1 :6, and 1 :7. In embodiments where the mixture of at least two diols is a mixture of three or more diols, similar ranges of mole ratios may be used. The dicarboxylic acid component comprises residues of terephthalic acid, isophthalic acid, 1 ,4-cyclohexanedicarboxylic acid, 2,6-naphthalenedicarboxylic acid, or mixtures thereof. Also suitable are the anhydrides thereof, acid chlorides thereof, and lower, e.g., C,-C 8 alkyl esters thereof. Any isomers of the dicarboxylic acid component or mixtures thereof may be used. For example, cis, trans, or cis/trans mixtures of 1,4- cyclohexenedicarboxylic acid may be employed. Examples of suitable naphthalenedicarboxylic acid isomers include 1 ,4-naphthalenedicarboxylic acid, 2-6- naphthalenedicarboxylic acid, 2,7-naphthalenedicarboxylic acid or mixtures thereof. Preferably, the dicarboxylic acid component is terephthalic acid. As discussed above, the amoφhous copolyesters according to the invention have enhanced glass transition and heat distortion temperatures and exhibit improved resistance to thermal deformation in applications where heat is generated. In this regard, the glass transition temperature of the copolyesters of the invention range from about 88 °C to about 120°C, more preferably from about 90 to about 105 °C, as determined by Differential Scanning Calorimetry (DSC) at a heating rate of 20°C/min, generally to a temperature of 280-300°C, in a nitrogen atmosphere. Further, amoφhous copolyesters according to the invention have a maximum melt viscosity at 1 radian/second (shear rate) and at about 260 to about 290 °C of about 12,000 poise as determined by a temperature drop experiment from 290 to 120°C with a 10 degree interval on a Rheometrics Dynamic Analyzer (RDA II) with 25 mm diameter parallel plates. In a preferred embodiment, the amoφhous copolyester of the invention has a melt viscosity ranging from about 3000 poise to about 11,000 poise, most preferably from about 4000 to about 10,000 poise. As discussed above, the presence of BDS in the copolyester of the invention significantly increases the glass transition temperature and the heat distortion temperature. Further, it has suφrisingly been discovered that the low shear rate melt viscosity of the copolyester of the invention are not increased over that of lower glass transition temperature commercial amoφhous copolyesters that do not contain BDS. Due to the low melt viscosity of the copolyester of the invention, its molecular weight (measured as IV) is advantageously increased yielding copolyesters with enhanced mechanical properties, i.e., toughness. Generally, the copolyesters of the invention have an IV of at least about 0.6 measured at a temperature of 25 °C at 0.25 g/dl concentration in a solvent mixture of symmetric tetrachloroethane and phenol having a weight ratio of symmetric tetrachloroethane to phenol of 2:3. In a preferred embodiment, the IV ranges from about 0.65 to about 0.90 dl/g, more preferably, from about 0.70 to about 0.80. The amoφhous copolyesters according to the invention are prepared by conventional polymerization processes known in the art, such as disclosed by U.S. Patent Nos. 4,093,603 and 5,681,918, the disclosures of which are herein incoφorated by reference. Examples of polycondensation processes useful in the present invention include melt phase processes conducted with the introduction of an inert gas stream, such as nitrogen, to shift the equilibrium and advance to high molecular weight or the more conventional vacuum melt phase polycondensations, at temperatures ranging from about 240 °C to about 300°C or higher which are practiced commercially. Although not required, conventional additives may be added to the copolyesters of the invention in typical amounts. Such additives include pigments, colorants, stabilizers, antioxidants, extrusion aids, slip agents, carbon black, flame retardants and mixtures thereof. Typical preparations of the amoφhous copolyesters of the invention are shown in the examples below. As discussed, it may be preferable to conduct the polymerization reaction in the presence of one or more conventional polymerization catalysts. Typical catalysts or catalyst systems for polyester condensation are well-known in the art. Suitable catalysts are disclosed, for example, in U.S. Patent Nos. 4,025,492, 4,136,089, 4,176,224, 4,238,593, and 4,208,527, the disclosures of which are herein incoφorated by reference. Further, R.E. Wilfong, Journal of Polymer Science, 54, 385 (1961), the disclosure of which is herein incoφorated by reference, describes typical catalysts which are useful in polyester condensation reactions. Preferred catalyst systems include Mn/Ti/Co/P, Mn/Ti/P, Zn/Ti/Co/P, Zn/Al. When cobalt is not used in the polycondensation, the use of polymerizable toners are required to control the color of these amoφhous copolyesters so that they are suitable for the intended applications where color may be an important property. In addition to the catalysts and toners other additives, such as antioxidants, dyes, etc. may be used in the copolyesterifications. Due to the relatively high glass transition temperature and heat distortion temperature of the copolyesters according to the invention, the copolyesters are extremely useful for applications in extruded heavy gauge sheet, extruded film and other plastic applications. Common plastic processing techniques such as compression molding, injection molding, and extrusion can be successfully used to manufacture useful articles from these copolyesters. Accordingly, in another embodiment of the invention relates to articles, sheets, and films prepared from the copolyester composition described above. Depending on the catalyst system used and the polycondensation process conditions, the articles, sheets, and films according to the invention can be transparent, preferably having an L* color value of at least about 70, an a* value ranging from about (-)1.5 to 1.5 and a b* value ranging from about (-)1.5 to 1.5. Sheeting made from clear, colored, or pigmented copolyesters of this invention can be advantageously employed in a great number of applications where the enhanced resistance to thermal deformation or flow provided by these copolyesters is important. Such examples include, but are not limited to skylights, solar roof panels, sign boards, greenhouse panels, marquees on stores, etc. The copolyesters of the invention may be used as a single sheet or as coextruded sheets in these kinds of applications with UN protection or color layers contiguous to the enhanced Tg copolyester layer. The higher heat distortion temperatures of the amoφhous copolyesters of the invention are also useful in medical plastic area with improved sterilization performance and improved chemical resistance. EXAMPLES The following examples are intended to illustrate, but not limit, the scope of the present invention. The inherent viscosities were measured at a temperature of 25 °C at 0.25 g/dl concentration in a solvent mixture of symmetric tetrachloroethane and phenol having a weight ratio of symmetric tetrachloroethane to phenol of 2:3. The 2 nd cycle glass transition temperatures were determined according to DSC at a heating rate of 20°C/min to a temperature of 280-300°C, quenching in liquid nitrogen to 0°C, and then rerunning the sample and recording the Tg as the 2 nd cycle glass transition temperature. The melt viscosities were determined by a temperature drop experiment from 290 to 120°C with a 10 degree interval on a Rheometrics Dynamic Analyzer (RDA II) with 25 mm diameter parallel plates. Final copolyester compositions were determined by proton NMR analysis on a 600 MHz JEOL instrument. EXAMPLE 1 A copolyester based on terephthalic acid with a diol composition of 23.3% neopentyl glycol, 61% 1,4-cyclohexanedimethanol, and 15.7 % of BDS was prepared as follows. To a 500ml round bottom flask equipped with a ground glass head, a stirrer and a nitrogen inlet was added 77.6 grams (0.40 moles) of dimethyl terephthalate, 13.1 grams (0.13 moles) of neopentyl glycol, 36.1 grams (0.25 moles) of 1,4- cyclohexanedimethanol, and 21.3 grams (0.06 moles) of BDS. Enough titanium catalyst was added to give 100 parts per million (ppm) titanium in the polymer. The flask was immersed into a Belmont metal bath and heated for 1.5 hr at 200°C and 2 hr at 210°C. After this time the theoretical amount of methanol was collected and the temperature was increased to 275 °C. The pressure in the flask was reduced from atmospheric to between 0.1 and 0.5 mm of Hg over 5 minutes. The temperature was maintained at 275 °C and the pressure between 0.1 to 0.5 mm for 30 minutes. Stirring was reduced as viscosity increased until a minimum stir rate of 15 RPM was obtained. The vacuum was discontinued and nitrogen bled into the flask. The polymer was allowed to cool, removed from the flask, and ground to pass a 3 mm screen. The resulting copolyester had an inherent viscosity of 0.73 dIJg and a 2 nd cycle glass transition temperature of 100.3 °C. The melt viscosity for this copolyester for 1 rad/sec at 280°C was 5724. The color values were as follows: L* = 83.41; a* = (-) 1.17, b* = 3.53. EXAMPLE 2 A copolyester based on terephthalic acid with a diol composition of 17.5 % ethylene glycol, 72.9% 1,4-cyclohexanedimethanol, and 9.6 % BDS was prepared as follows. To a 500ml round bottom flask equipped with a ground glass head, a stirrer and a nitrogen inlet was added 77.6 grams (0.40 moles) of dimethyl terephthalate, 25.1 grams (0.40 moles) of ethylene glycol, 51.3 grams (0.36 moles) of 1,4- cyclohexanedimethanol, and 13.5 grams (0.04 moles) of BDS. Enough titanium, manganese, and cobalt catalyst was added to give 60, 55, and 75 parts per million (ppm) respectively in the polymer. The flask was immersed into a Belmont metal bath and heated for 1.5 hr at 200°C and 2 hr at 210°C. After this time the theoretical amount of methanol was collected. Enough phosphorous was added to give 85 ppm in the polymer and the temperature was increased to 280 °C. The pressure in the flask was reduced from atmospheric to between 0.1 and 0.5 mm of Hg over 5 minutes. The temperature was maintained at 280°C and the pressure between 0.1 to 0.5 mm for 30 minutes. Stirring was reduced as viscosity increased until a minimum stir rate of 15 RPM was obtained. The vacuum was discontinued and nitrogen bled into the flask. The polymer was allowed to cool, removed from the flask, and ground to pass a 3 mm screen. The resulting copolyester had an inherent viscosity of 0.77 dL/g and a 2 nd cycle glass transition temperature of 98.6°C. The melt viscosity of this copolyester for 1 rad/sec at 280°C was 10,305. EXAMPLE 3 A copolyester based on terephthalic acid with a diol composition of 56.4% ethylene glycol, 28.3% 1,4-cyclohexanedimethanol, and 15.3% BDS was prepared as follows. To a 500ml round bottom flask equipped with a ground glass head, a stirrer and a nitrogen inlet was added 97.8 grams (0.50 moles) of dimethyl terephthalate, 47.6 grams (0.77 moles) of ethylene glycol, 23.3 grams (0.16 moles) of 1 ,4-cyclohexanedimethanol, and 26.6 grams (0.08 moles) of BDS. Enough titanium and manganese catalysts were added to give 16 parts per million (ppm) titanium and 46 ppm manganese in the polymer. Red and blue toners were added to give 2 ppm red dye and 3 ppm blue dye in the final polymer. The flask was immersed into a Belmont metal bath and heated for 1.5 hr at 200 °C and 2 hr at 210°C. After this time the theoretical amount of methanol was collected. Enough phosphorous catalyst was added to give 75 ppm in the polymer and the temperature was increased to 285 °C. The pressure in the flask was reduced from atmospheric to 0.5 mm of Hg over 5 minutes. The temperature was maintained at 285 °C and the pressure at 0.5 mm for 30 minutes. Stirring was reduced as viscosity increased until a minimum stir rate of 15 RPM was obtained. The pressure in the flask was reduced from 0.5 to 0.4 mm of Hg over 1 minute. The temperature was maintained at 285 °C and the pressure at 0.4 mm for 100 minutes. The vacuum was discontinued and nitrogen bled into the flask. The polymer was allowed to cool, removed from the flask, and ground to pass a 3 mm screen. The resulting copolyester had an inherent viscosity of 0.71 dL/g and a 2 nd cycle glass transition temperature of 97.7°C. The color values were as follows: L*=78.44, a* = 0.48, b* = (-)0.92. The melt viscosity at 290°C, 280°C, 270°C, and 260°C was 4784, 5460, 6520, and 7842 poise respectively. EXAMPLE 4 A copolyester based on terephthalic acid with a diol composition of 55.9% ethylene glycol, 28.9% 1,4-cyclohexanedimethanol, and 15.2 % BDS was prepared as follows. To a 500ml round bottom flask equipped with a ground glass head, a stirrer and a nitrogen inlet was added 97.0 grams (0.50 moles) of dimethyl terephthalate, 47.6 grams (0.77 moles) of ethylene glycol, 23.3 grams (0.16 moles) of 1,4- cyclohexanedimethanol, and 26.6 grams (0.08 moles) of BDS. Enough titanium and manganese catalysts were added to give 16 parts per million (ppm) titanium and 46 ppm manganese in the polymer. The flask was immersed into a Belmont metal bath and heated for 1.5 hr at 200°C and 2 hr at 210°C. After this time the theoretical amount of methanol was collected. Enough phosphorous catalyst was added to give 75 ppm in the polymer and the temperature was increased to 285 °C. The pressure in the flask was reduced from atmospheric to 0.5 mm of Hg over 5 minutes. The temperature was maintained at 285 °C and the pressure at 0.5 mm for 30 minutes. Stirring was reduced as viscosity increased until a minimum stir rate of 15 RPM was obtained. The pressure in the flask was reduced from 0.5 to 0.4 mm of Hg over 1 minute. The temperature was maintained at 285 °C and the pressure at 0.4 mm for 100 minutes. The vacuum was discontinued and nitrogen bled into the flask. The polymer was allowed to cool, removed from the flask, and ground to pass a 3 mm screen. The resulting copolyester had an inherent viscosity of 0.71 dL/g and a 2 nd cycle glass transition temperature of 96.4 °C. The melt viscosity for this copolyester for 1 rad/sec at 280 °C was 5464. The color values were as follows: L*=84.11, a* = (-) 1.49, b* = 4.82. EXAMPLE 5 A copolyester based on terephthalic acid with a diol composition of 69.7% ethylene glycol, 10.8% 1,4-cyclohexanedimethanol, and 19.5% BDS was prepared as follows. To a 500 ml round bottom flask equipped with a ground glass head, a stirrer, and a nitrogen inlet was added 97.0 grams (0.50 moles) of dimethylterephthalate, 42.8 grams (0.69 moles) of ethylene glycol, 7.9 grams (0.055 moles) of 1,4-cyclohexanedimethanol, and 33.8 grams (0.10 moles) of BDS. Enough titanium, manganese and cobalt catalyst was added to give 60, 55, and 75 parts per million (ppm), respectively in the polymer. The flask was immersed in a Belmont metal bath and was heated for 1.5 hours at 200°C and 2 hours at 210°C. After this time the theoretical amount of methanol had been collected. Enough phosphorus catalyst was added to give 85 ppm in the polymer and the temperature increased to 280°C. The pressure in the flask was reduced from atmospheric to between 0.1 to 0.5 mm of Hg over 5 minutes. The temperature was maintained at 280°C and the pressure between 0.1 to 0.5 mm for 30 minutes. Stirring was reduced as viscosity increased until a minimum stir rate of 15 RPM was obtained. The vacuum was discontinued and nitrogen bled into the flask. The polymer was allowed to cool, removed from the flask and ground to pass a 3-mm screen. The inherent viscosity of the polymer was 0.706 dL/g and 2 nd cycle glass transition temperature of 98 °C as determined by DSC. The heat distortion temperature was measured according to ASTM-D648 at 264 psi as 77 °C. The heat distortion temperature is defined in ASTM-D648 as the temperature at a stress of 264 psi where an F-l molded bar deflects 0.01 inches when heated in an oil bath at 2°C/min. COMPARATIVE EXAMPLE 6 A copolyester based on terephthalic acid with a diol composition of 40% ethylene glycol, 40% 1,4-cyclohexanedimethanol and 20% 2,2,4,4-tetramethyl-l,3- cyclobutanediol was prepared by adding 77.6 g (0.40 moles), 32.3 g (0.52 moles) ethylene glycol, 24.4 g (0.17 moles), and 15.8 g (0.11 moles) of 2,2,4,4-tetramethyl-l,3- cyclobutanediol to a 500 ml glass round bottom polymerization reactor equipped with a stirrer and nitrogen inlet. To this mixture was added 1.09 milliliters of a solution containing 13.5 g of dibutyltin diacetate in 50 ml of n-butanol. The flask was immersed into a Belmont metal bath and heated for 40 minutes at 200 °C, 25 minutes at 215 °C, and 160 minutes at 220 °C. The theoretical amount of methanol was collected during this time. The temperature was increased to 285 °C and the pressure in the flask was reduced from atmospheric to between 0.1 and 0.5 mm Hg over 5 minutes. The temperature was maintained at 285 °C at this pressure for 20 minutes. Stirring was reduced as the melt viscosity increased until a minimum stir rate of 15 RPM was obtained. The vacuum was discontinued and nitrogen purged into the reactor. The polymer was cooled, removed from the flask and ground to pass a 3 mm screen. The inherent viscosity of the polymer was 0.72. The polymer had a 2 nd cycle glass transition temperature of 98 °C. No other transitions were noted. The melt viscosity at 1 radian per second at 280 °C was 33,000 poise. COMPARATIVE EXAMPLE 7 A copolyester was prepared as in Example 7 with a diol composition of 20% ethylene glycol, 55% 1,4-cyclohexanedimethanol, and 25% 2,2,4,4- tetramethylcyclobutane-l,3-diol. The resulting copolyester exhibited an IV of 0.79, had a 2 nd cycle glass transition temperature of 101 °C, and a melt viscosity at 280 °C of 54,210 poise. EXAMPLE 8 This example demonstrates the effect inherent viscosity has on elongation to break. Elongation to break values greater than 100% signify excellent toughness in the plastic, while values less than 20% represent plastics with brittle behavior. The test used was ASTM D638 and was performed on injection molded Type 1 test bars using a constant strain rate of 0.1 /in using a standard Instron Universal Tester. The results are set forth below in Table 1. TABLE 1 1. EG = ethylene glycol 2. CHDM = 1,4-cyclohexanedimethanol

Claims: WHAT IS CLAIMED IS: 1. An amoφhous copolyester having a maximum melt viscosity at 1 radian/second and at about 260 to about 290°C of about 12,000 poise; a glass transition temperature ranging from about 88°C to about 120°C; and an inherent viscosity of at least about 0.6, said amoφhous copolyester comprising the reaction product of a diol component and a dicarboxylic acid component, wherein: the diol component comprises residues of from about 5 to about 50 mole % of 2,2'-(sulfonylbis (4,l-phenyleneoxy))-bis(ethanol) and from about 50 to about 95 mole % of a mixture of at least two diols selected from the group consisting of ethylene glycol, neopentyl glycol, 1,3-propanediol, 1,4-butanediol, 1,4-cyclohexanedimethanol, and mixtures thereof; and the dicarboxylic acid component comprises residues of terephthalic acid, isophthalic acid, 1 ,4-cyclohexandedicarboxylic acid, 2,6-naphthalene dicarboxylic acid, anhydrides thereof, acid chlorides thereof, lower alkyl esters thereof, and mixtures thereof. 2. The amoφhous copolyester according to claim 1, wherein said 2,2'- (sulfonylbis (4,l-phenyleneoxy))bis(ethanol) is present at from about 10 to about 50 mole. 3. The amoφhous copolyester according to claim 1, wherein said mixture of at least two diols comprise a mixture of ethylene glycol, neopentyl glycol and 1,4- cyclohexanedimethanol. 4. The amoφhous copolyester according to claim 1 , wherein the diol component comprises residues of from about 10 to about 50 mole % of 2,2'-(sulfonylbis (4,l-phenyleneoxy))-bis(ethanol); and from about 50 to about 90 mole % of at least two diols selected from the group consisting of ethylene glycol, neopentyl glycol, 1,4- cyclohexanedimethanol, and mixtures thereof . 5. The amoφhous copolyester according to claim 1, wherein the dicarboxylic acid component comprises residues of terephthalic acid. 6. The amoφhous copolyester according to claim 1, wherein the inherent viscosity ranges from about 0.65 to about 0.85. 7. The amoφhous copolyester according to claim 1, wherein the inherent viscosity ranges from about 0.70 to about 0.80. 8. The amoφhous copolyester of claim 1, wherein the melt viscosity ranges from about 3000 poise to about 11,000 poise. 9. The amoφhous copolyester according to claim 1, wherein the glass transition temperature ranges from about 90 to about 110°C. 10. The amoφhous copolyester of claim 1, wherein said amoφhous copolyester is transparent. 11. The amoφhous copolyester of claim 10, having a L* color value of at least about 70. 12. A copolyester composition comprising the amoφhous polyester according to claim 1 and an additive selected from the group consisting of a pigment, a colorant, a stabilizer, an antioxidant, an extrusion aid, a slip agent, carbon black, a flame retardant and mixtures thereof. 13. A method for preparing an amoφhous copolyester having a maximum melt viscosity at 1 radian/second and at about 260 to about 290°C of about 12,000 poise; a glass transition temperature ranging from about 88°C to about 120°C; and an inherent viscosity of at least about 0.6, said method comprising the step of reacting, under polycondensation conditions, a dicarboxylic acid component and a diol component wherein: the diol component comprises residues of from about 5.0 to about 50 mole % of 2,2'-(sulfonylbis (4,l-phenyleneoxy))bis(ethanol) and from 50 to about 95.0 mole % of a mixture of at least two diols selected from the group consisting of ethylene glycol, neopentyl glycol, 1,3-propanediol, 1,4-butanediol, 1,4-cyclohexanedimethanol, and mixtures thereof; and the dicarboxylic acid component comprises residues of terephthalic acid, isophthalic acid, 1,4-cyclohexandedicarboxylic acid, 2,6-naphthalene dicarboxylic acid, anhydrides thereof, acid chlorides thereof, lower alkyl esters thereof, and mixtures thereof. 14. The method according to claim 13, wherein said 2,2'-(sulfonylbis (4,1- phenyleneoxy))bis(ethanol) is present from about 10 to about 50 mole %. 15. The method according to claim 13, wherein said amoφhous copolyester has an inherent viscosity ranging from about 0.65 to about 0.85; a melt viscosity ranging from about 3000 poise to about 11,000 poise; and a glass transition temperature ranging from about 90 to about 110°C. 16. The method according to claim 13, wherein the diol component comprises residues of from about 10 to about 50 mole % of 2,2'-(sulfonylbis (4,1-phenyleneoxy))- bis(ethanol) and from about 50 to about 90 mole % of a mixture of at least two diols selected from the group consisting of ethylene glycol, neopentyl glycol, 1,4- cyclohexanedimethanol, and mixtures thereof. 17. The method according to claim 13, wherein said mixture of at least two diols comprises residues of a mixture of ethylene glycol, neopentyl glycol, and 1,4- cyclohexanedimethanol. 18. A film, molded article, or sheet prepared from amoφhous copolyester according to claim 1. 19. The film, molded article, or sheet according to claim 18, wherein the film, molded article, or sheet is transparent. 20. The film, molded article, or sheet according to claim 18, wherein the film, molded article or sheet has a L* color value of at least about 70.

Inventors: SULBETT BOBBY J, TURNER RICHARD S, SULBETT, BOBBY, J., TURNER, RICHARD, S.
Applicants: EASTMAN CHEM CO, EASTMAN CHEMICAL COMPANY
Application year: 2000
Main classification: C08G63
IPC codes: C08G63, C08J5, C08K3, C08L67