APPARATUS AND METHOD FOR FORMING COMPLEX-SHAPED COMPONENTS IN A HEATED POLYMERIC FILM

Abstract: A thin-walled polymeric component (50) that may have a selected complex shape, and a method of forming the component (50). The method includes heating a portion of a polymeric film (68) to a selected malleable temperature, and forming a protrusion (80) in the heated portion while it is malleable. The protrusion (80) defines a protrusion (80) having a first shape. The method also includes positioning a forming tool (74) in the protrusion's interior and drawing a partial vacuum from within the protrusion (70) so as to exert a force on the protrusion (80) and move the protrusion's sidewalls inwardly into engagement with the forming tool (74). As the partial vacuum is drawn, the protrusion (80) moves to a second shape that may be different than the first shape and that closely conforms to the selected shape of the forming tool (74). The protrusion (80) is cooled below the malleable temperature and the forming tool (74) is then removed. The distal portion (84) of the protrusion (80) having the selected shape forms the polymeric component (50) and that distal portion (84) is separated from the remaining portion of the protrusion (80), thereby providing the thin-walled polymeric component (50).

Description: APPARATUS AND METHOD FOR FORMING COMPLEX-SHAPED COMPONENTS IN A HEATED POLYMERIC FILM TECHNICAL FIELD The present invention is directed toward a method of making medical components, and more particularly toward a method of making contoured, thin-walled, complex-shaped medical components usable with intrabody medical devices. BACKGROUND OF THE INVENTION The use of intrabody medical equipment, such as endoscopes, catheters, and the like, for diagnostic and therapeutic indications is rapidly expanding. To improve performance, the equipment has been optimized to best accomplish the selected purpose. As an example, endoscopes have been optimized and refined so as to provide upper endoscopes for the examination of the esophagus, stomach, and duodenum, colonoscopes for examining the colon, angioscopes for examining blood vessels, broπchoscopes for examining the bronchii, laparoscopes for examining the peritoneal cavity, arthroscopes- for examining joints spaces, nasopharygoscopes for examining nasal passages and pharynx, and intubation scopes for examination of a person's airway. Optimization of the intrabody medical devices for such therapeutic and diagnostic procedures has resulted in sterile, inexpensive disposable equipment that is used alone or with non-disposable equipment. In the field of endoscopes, a conventional endoscope 10, shown in Figure 1, has an insertion tube 12 that is connected at its proximal end 14 to a handle or control body 16. The insertion tube 12 is adapted to be inserted into a patient's body cavity to perform a selected therapeutic or diagnostic procedure. The insertion tube 12 contains an imaging system 18 having optical fibers or the like extending along the length of the insertion tube and terminating at a viewing window 19 in the insertion tube's distal end 20. The imaging system 18 conveys an image from the viewing window 19 to an eyepiece 22 on the control body 16 or to a monitor (not shown), so the user can see into a selected body cavity during an endoscopic procedure. The endoscope 10 is described in greater detail in U.S. Patent No. Re 34, 110 and U.S. Patent No. 4,646,722, which are incorporated by reference herein. Disposable endoscopic sheath assemblies are used to cover the insertion tube 12 and protect it from being contaminated. Accordingly, the sheath assemblies alleviate the problem and cost of cleaning and sterilizing the insertion tube 12 between endoscopic procedures. As seen in Figure 1, .a conventional sheath assembly 24, shown partially cut away for illustrative purposes, includes a flexible, elastic sheath 26 that tightly surrounds the endoscope's insertion tube 12. The sheath 26 may also contain one or more working channels 32 that extend along the insertion tube 12 and that are adapted to receive conventional endoscopic accessories therethrough without contaminating the endoscope itself during the endoscopic procedure. The sheath 26 has a distal end portion 21 that includes an endcap 34 having a transparent window 28 positioned to cover the viewing window 19 at the insertion tube's distal end 20 when the sheath assembly is installed. The endcap 34 formed of a relatively rigid material and is sealably secured to the sheath's distal end portion 21. Endoscopic sheath assemblies used with insertion tubes that have a complex cross-sectional shape, such as C-shaped, often must have an endcap with a corresponding complex cross-sectional shape to snugly fit over the insertion tube's distal end 20. The complex-shaped endcap can be a costly and laborious component to manufacture for the sheath assembly. Other thin-walled components that would be required to have a complex shape if used with endoscopic sheaths or other medical devices having complex shapes may include precision detent mechanisms and short- pitched threads that are manufactured with the necessary accuracy and tolerances required for intricate medical devices. U.S. Patent No. 5,443,781 to Saab teaches a method of forming a disposable sheath with an optically transparent window that is integral with the sheath. The transparent window is formed so as to maintain a thin-walled, relatively inelastic, yet flexible sheath for an optical medical instrument. Saab teaches forming the sheath by heating a sheet or film of optically transparent polymeric material until the material's viscosity is substantially reduced and the film is malleable. As shown in Figure 2, a mandrel 35 having a relatively simply cylindrical shape is thrust into the heated film 37 causing the film to stretch and to generally conform to the mandrel's shape. As a result, the heated film 37 is formed into a closed-end sheath 39 having sidewalls 36, a flange or collar 38 at its open proximal end 40, and a closed distal end 42. The mandrel 35 is selected based upon its simple geometrical shape to define the shape of the sheath 39. Accordingly, sheaths having different shapes and sizes are formed using different mandrels with the corresponding shapes and sizes. The sheath and technique of making the sheath as discussed in Saab, however, results in the film being heated, stretched, and then cooled to remain the shape that generally corresponds to the mandrel's simple. The resulting sheath is limited to having a relatively simple geometrical shape. The method of Saab does not sufficiently allow for making complex-shaped components having close tolerances. In the design of intrabody medical devices and accessories, including optical and non-optical devices, the need for components having a complex geometry has become more and more apparent. As an example, there is a need for highly-detailed components, such as endcaps, used with more complicated endoscopes. There is further a need for precisely manufactured catheter components or the like with accurately positioned detents or close-pitched threads. Other medical devices and accessories would be benefited by inexpensive thin-walled components with close tolerance demands. SUMMARY OF THE INVENTION The present invention provides a method capable of forming complex- shaped medical components in a heated polymeric film to provide thin-walled, durable, low-cost components that may be manufactured to close tolerances, which has been problematic in the prior art. In an exemplary embodiment of the present invention, the method of forming a thin-walled polymeric component includes the steps of heating a portion of the polymeric film to a malleable temperature, and using a forming tool to form a protrusion in the film's heated portion while the polymeric film is malleable. The formed protrusion has an open proximal end, a distal end spaced apart from the proximal end, and sidewalls extending between the proximal and distal ends. The sidewalls and distal end define a first shape of the protrusion and also define an interior of the protrusion. The forming tool has a shaping portion that may have a selected complex shape that is different than the protrusion's first shape. The method further includes the step of exerting a force radially inwardly on the protrusion and moving the protrusion into firm engagement with the forming tool's shaping portion so the protrusion moves from the first shape to a second shape that closely conforms to the selected shape of the forming tool's shaping portion. In the exemplary embodiment, the radially inward force exerted on the protrusion is achieved by creating a differential pressure so the pressure within the interior of the protrusion is less than the pressure outside the protrusion, thereby causing • the protrusion's sidewalls to move inwardly to the second shape. In one embodiment, the step of exerting a differential pressure on the protrusion is achieved by drawing a partial vacuum inside the protrusion. The partial vacuum may be drawn through the forming tool and through at least one vacuum port in the forming tool. The present invention is also directed toward a polymeric medical component that may have a selected complex shape that is made by the above-described process. . The present invention is also directed toward a vacuum-forming tool capable of forming the medical component from a malleable polymeric protrusion. The vacuum-forming tool includes a shaft having an air passageway and a forming portion, and the forming portion has a shape corresponding to the selected shape of the medical component. The forming portion has an outer surface and a plurality of apertures extending from the outer surface to the air passageway. The shaft is connectable to a vacuum source so the air passageway communicates with the vacuum source to allow the vacuum source to draw air through the apertures into the air passageway, thereby forming a partial vacuum within the malleable polymeric protrusion during the formation of the medical component. BRIEF DESCRIPTION OF THE DRAWINGS Figure 1 is an isometric view of a prior art endoscope and endoscopic sheath assembly. Figure 2 is an isometric view of a thermal plastic film of the prior art stretched by a mandrel. Figure 3 is an isometric view of a distal portion of an endoscopic sheath having a thin-walled, polymeric endcap formed in accordance with one embodiment of the present invention. Figure 4 is an isometric view of a heated thin-walled polymeric film with a funnel-shaped projection formed therein in accordance with one embodiment of the present invention and shown in an extended position, and a complex-shaped forming tool is shown positioned in the protrusion and connected to a vacuum source. Figure 5 is an isometric view of the heated polymeric film of Figure 4 with the projection shown in a contracted position in solid lines on the forming tool, and the projection is shown in the extended position in phantom lines. Figure 6 is an isometric view of the protrusion of Figure 5 shown with a distal portion of the protrusion being separated from a proximal to provide the selected thin-walled polymeric endcap with complex shape. Figure 7 is an isometric view of an alternate embodiment of the present invention with the thin-walled component having close-pitched threads formed therein by a complex-shaped threaded forming tool shown in phantom lines. Figure 8 is an isometric view of an alternate embodiment of the present invention with the thin-walled component having detents formed therein by a forming tool shown in phantom lines. DETAILED DESCRIPTION OF THE INVENTION A thin-walled polymeric medical component 50 having a complex shape made in accordance with one embodiment of the present invention is described herein with reference to the attached drawings. An exemplary embodiment of a thin-walled medical component 50, shown in Figure 3, is attached to a distal end 52 of a sheath 54. The sheath 54 is shaped and sized to receive and isolate, as an example, an endoscope insertion tube 56 shown in phantom lines. The illustrated medical component 50 is a sheath endcap 51 that is sealably attached to the sheath's distal end 52 so as to provide a viewing window therein that allows clear imaging through the endoscope's imaging system 58, also shown in phantom lines. The distal end portion 55 of the illustrated insertion tube 56 has a generally C-shaped cross-section and the endcap 51 is formed with a corresponding complex geometrical shape that closely conforms to the insertion tube's distal end ■ portion. More specifically, the C-shaped cross-section of the illustrated endcap 51 is defined by a curved outer axial wall 60 that has a selected radius and a curved inner axial wall 62 that is integrally connected to the outer axial wall 60. The inner axial wall 62 has a radius which is smaller than the radius of the outer axial wall 60. The inner axial wall 62 defines a receiving area 64 that is shaped and sized to receive one or more selected working channels 66, shown in phantom lines, extending through the sheath 54. As an example, the illustrated endoscopic sheath 54 includes a tubular working channel 66 that extends through the sheath and that is sealably connected to the sheath's distal end 52. The tubular working channel 56 snugly fits in the endcap's receiving area 64, while the distal end of the endoscope's insertion tube 56 is snugly received in the endcap 51 between the inner and outer walls. Accordingly, the thin- walled endcap 51 is provided with a complex geometrical shape that receives and retains the insertion tube's distal end therein and retains the working channel 66 adjacent to the distal end while minimizing the cross-sectional area of the sheath and insertion tube combination which is to be inserted into a patient. While the medical component 50, such as the end cap 51, and the method of making the component is discussed herein with reference to an endoscopic sheath, the method of the present invention is equally applicable to medical components used in procedures for medical devices other than endoscopic procedures. As an example, the medical component 50 in alternate embodiments are complex-shaped components used with catheters, optical medical equipment, and non-optical imaging medical equipment. The thin-walled polymeric medical component 50 is made by forming a thin polymeric film into the desired shape. The preferred polymeric film used with the present invention is a thermoplastic material including PVC, acrylic, polycarbonate, polyethylene terephthalate, or other thermoplastic polyester material. The polymeric material used by the present invention allows for thin-walled medical components that are substantially inelastic, flexible, and have- high strength, and that can be easily, inexpensively, and quickly manufactured. The polymeric film is selected so the medical component 50 has a wall thickness in the range of approximately 0.0005 to 0.015 inches, inclusive, and preferably in the range of approximately 0.0008 to 0.005 inches, inclusive. In the exemplary embodiment illustrated in Figures 3, 4 and 5, the medical component 50 is formed from a material that is optically transparent to visible light. The polymeric film, however, may be selected to provide a desired degree of transparency to electromagnetic radiation in the visible spectrum, or in the non-visible spectrum, e.g., radar, laser, or microwave. The polymeric film may also be selected, when needed, to provide a desired degree of transparency to sound waves, such as for use with ultrasound devices. As best seen in Figure 4, the polymeric film 62, is retained in a selected position so as to substantially define a plane. An interior portion of the film 68 is heated by a conventional heating device 72 to a selected malleable temperature to form a malleable, heated portion 70 of the film. The heated portion 70 is then stretched and formed into a protrusion 80, as discussed in greater detail below, by a forming tool 74. The forming tool 74 has a contoured shaping portion 78 with a complex geometrical shape that co esponds to the shape of the endcap or other medical component to be formed. In the illustrated embodiment, the forming tool's shaping portion 78 has a C-shaped cross-section with curved inner and outer surfaces that correspond to the endcap's C-shaped cross-section discussed above. After the film's heated portion 70 is malleable, the forming tool's shaping portion 78 is pressed into the heated portion generally perpendicular to the plane defined by the film 68, and the forming tool stretches the heated portion away from the plane to form a thin-walled, generally funnel-shaped protrusion 80. The protrusion 80 has an open proximal end 82, a closed distal end 84 spaced away from the open proximal end and sidewalls 86 extending between the proximal and distal ends. The closed distal end 84 and the sidewalls 86 define an interior 88 of the protrusion 80 that contains the forming tool's shaping portion 78 as the protrusion is formed. As the protrusion 80 is formed, the protrusion has a generally tubular shape that only roughly conforms to the outer shape of the forming tool's shaping portion 78, but the protrusion's sidewalls 86 do not yet closely conform to the complex shape of the forming tool's shaping portion. As an example, the protrusion's sidewalls 86 conform to the shaping portion's outer curved surface but do not conform to the shaping portion's inner curved surface, such that the protrusion has a generally D-shaped cross-section, rather than the C-shaped cross-section of the shaping portion. While still malleable, the protrusion's sidewalls 86 and the closed distal end 84 are then brought into firm and close engagement with the forming tool's shaping portion 78, as shown in Figure 5, thereby closely conforming to the shaping portion's complex geometrical shape. In the exemplary embodiment, the protrusion 80 is brought into firm engagement with the shaping portion 78 by drawing a partial vacuum within the projection's interior 88. The partial vacuum causes a differential pressure in the protrusion that is exerted on the sidewalls 86, so the pressure within the protrusion is less than the pressure outside of the protrusion. Accordingly, the partial vacuum moves the protrusion's sidewalls 86 against the forming tool's shaping portion 78 to achieve the selected complex geometrical shape for the medical component 50. After the protrusion 80 has moved to the contracted position and has cooled from the malleable temperature, the forming tool 74 is removed from the protrusion's interior 88 and the protrusion remains in the contracted position. As best seen in Figures 4 and 5, the forming tool 74 is a partially hollow member with at least one and preferably a plurality of vacuum ports 89 formed in the shaping portion 78. The forming tool 74 is connected to a conventional vacuum source 90 by a vacuum line 92. The vacuum source is adapted to draw air into the forming tool's shaping portion 78 through the vacuum ports 89, thereby creating the partial vacuum within the interior. As best seen in Figure 6, after the forming tool 74 is removed, a distal portion of the protrusion 80, which has the complex-shape formed therein, is cut or otherwise separated from the remaining portion of the protrusion, and that distal portion is the thin-walled polymeric medical component 50. The component 50, such as the illustrated C-shaped endcap 51, is then connected to the selected medical device, such as the distal end 52 of the endoscopic sheath 54, as illustrated in Figure 3. In an alternate embodiment (not shown), the protrusion 80 is moved to the contracted position by exerting substantially uniform, exterior pressure on the protrusion in a radially inward direction. As an example, the distal portion of the protrusion 80 and the forming tool's shaping portion 78 are positioned, as a unit, within a pneumatic pressure-generating device or other suitable device that exerts the exterior pressure, and the pressure generating device moves the protrusion's sidewalls 86 from the expanded position to the contracted position and into close engagement with the forming tool's shaping portion 78. Accordingly, the radially inward directed forces on the protrusion 80 may be achieved by generating a vacuum in the protrusion's interior or by creating a pressure external to the protrusion. The preferred method, however, is to use the partial vacuum within the protrusion's interior 88 because the partial vacuum does not disturb the temperature profile of the heated polymeric film. In addition to forming medical components having complex contoured shapes, such as the C-shape cross-sectional shape, the disclosed embodiment of the present invention also allows easy and inexpensive formation of a thin-walled, polymeric medical component 50 having close-pitched, accurately-located threads formed therein. As best seen in Figure 7, the forming tool 74 has a plurality of close-pitched threads 100 formed in the shaping portion 78. The forming tool 74 is pressed into the heated portion 70 of the polymeric film 68 when at malleable temperature, thereby forming the protrusion 80 . Accordingly, the protrusion's sidewalls 86 are generally adjacent to the threads 100 on the forming tool 74, but do not yet closely conform to the threads. The differential pressure is then generated in the protrusion's interior 88, moving the sidewalls 86 to the contracted position and into close engagement with the threads 100, thereby forming the close-pitched, accurately positioned threads 102 in the protrusion. The forming tool 74 is then removed preferably by rotating it so the shaping portion 78 unscrews from the threads 102 formed in the protrusion 80. The present invention also allows for easy and inexpensive formation of a thin-walled polymeric medical component 50, as shown in Figure 8, having precisely located detents 120 formed in selected positions that correspond to detent receiving portions on a selected medical device, not shown. The medical component 50 may also have a concave-shaped distal end 122 that follows the contour of the selected medical device. The medical component 50 illustrated in Figure 8 is formed using a forming tool 74 with a shaping portion 78 having one or more detent molds 124 in a selected position and having a concave distal end surface 125 The shaping portion 78 also has the vacuum ports 89 formed therein for creating the partial vacuum in the protrusion's interior portion 88. Accordingly, when the forming tool 74 is pressed into the film ' s heated portion 70 to form the protrusion 80 and the partial vacuum is drawn through the vacuum ports 89, the protrusion's sidewalls 86 are drawn into firm engagement with the forming tool's detent molds 124 so as to form the detents 120 in the protrusion. Similarly, the protrusion ' s closed distal end 84 is drawn into firm engagement with the forming tool's concave distal end 125, thereby forming a medical component 50 with a concave closed distal end. After the polymeric material is cooled, the forming tool 74 is removed from the protrusion's interior 88 and the selected shaping portion of the protrusion 80 is cut in order to remove the complex-shaped medical component 50 from the rest of the protrusion. In the embodiment wherein a detent or the like is formed in the medical component 50, the forming tool 74 may be removed from the protrusion's interior 88 by slightly deflecting the sidewalls 86 of the protrusion 80 until sufficient clearance is provided between the sidewalls and the forming tool's shaping portion 78. Such deflection is possible because the thin- walled polymeric material is sufficiently flexible to move so as to allow removal of the forming tool without permanent deformation of the medical component 50 In alternate embodiments, the thin-walled polymeric medical component 50 is formed by stretching or drawing the protrusion 80 in two or more steps, so selected portions of the component have a different thickness than the thickness of other portions of the component. In one embodiment, an endcap with an integral optical lens is formed by pressing a first forming tool 74 into the heated portion 70 to form the protrusion 80, and the differential pressure is applied to the protrusion, as discussed above. The first forming tool 74 is specifically designed to form the lens of the endcap to provide the selected thickness and optical characteristics of the lens. After the lens is formed, the first forming tool is removed from the • protrusion 80. While the protrusion 80 is still malleable, a second forming tool is pressed into the protrusion to further draw or stretch the protrusion's sidewalls 86 to form thinner sidewalls. The second forming tool is designed to support the lens portions so there is substantially no further drawing of the lens while the sidewalls 86 are being drawn. The differential pressure is exerted on the protrusion so the protrusion conforms to the second forming tool, and the second forming tool is then removed. Accordingly the lens maintains its selected thickness, and the sidewalls are thinner than when formed by the first forming tool. In another one of the alternate embodiments, the protrusion 80 is formed with portions having different thicknesses by heating the film 68 a first time and forming the protrusion with a forming tool as discussed above. The protrusion 80 is then allowed to cool to below the malleable temperature. A selected portion of the protrusion 80, such as the sidewalls 86, is heated a second time to . the malleable temperature, and the sidewalls or other selected portion is further stretched or drawn with the same or a different forming tool. Accordingly, the protrusion's selected portion that is reheated and further drawn is thinner while the protrusion's other portions that were not heated a second time are not further thinned by the second drawing process. If further drawing is needed at other specific portions of the protrusion 80, additional steps of heating and drawing can be performed to achieve the specific size, thickness, and characteristics of the component 50. In another alternate embodiment (not shown), the thin-walled polymeric medical component 50 is formed by pressing the forming tool 74 into the polymeric film's heated portion 70, such that the distal end of the forming tool pierces the distal end of the protrusion. In this alternate embodiment, the protrusion's sidewalls are substantially sealably connected to the forming tool's shaping portion 78, so a partial vacuum can still be generated to draw the sidewalls into firm engagement with the shaping portion. In yet another embodiment (not shown), the complex-shaped medical component 50 is further modified or machined after formation of the component so as to remove or modify a selected portion of the medical component. As an example, polymeric material is removed from a distal end portion of a selected medical component to allow a selected medicai device to be positioned partially within the component, while a selected portion of the device extends through the thin-walled polymeric medical component. Accordingly, the thin-walled, polymeric medical component can be formed with a selected complex shape for use with a wide range of medical devices. From the foregoing it will be appreciated that, although specific embodiments of the invention have been described herein for purposes of illustration, various modifications may be made without deviating from the spirit and scope of the invention. Also, although the various embodiments of the invention have been described as being used to form complex components, it will be understood that relatively simple components may also be formed in accordance with the invention. Accordingly, the invention is not limited except as by the appended claims.

Claims: CLAIMS 1. A method of forming a medical component, comprising the steps of: heating a portion of a sheet of a selected material to a malleable temperature to form a malleable heated portion of the sheet; forming a protrusion in the heated portion while the heated portion is malleable, the protrusion having an open proximal end, a distal end, and sidewalls extending between the proximal and distal ends, the sidewalls and distal end defining a first shape of the protrusion; positioning a forming tool in the interior of the protrusion, the forming tool having a shaping portion with a selected shape that is different than the first shape of the protrusion; and exerting an inwardly directed force on the protrusion while the heated portion is malleable, the force being sufficient to move a portion of the protrusion inwardly into engagement with the shaping portion so the protrusion changes from the first shape to a second shape that conforms to the selected shape of the forming tool's shaping portion. 2. The method of claim 1 wherein the step of exerting a force includes creating an interior pressure in the protrusion's interior, the interior pressure being less than an exterior pressure that is exterior of the protrusion's interior causing the protrusion to change to the second shape. 3. The method of claim I, further including the steps of cooling the protrusion to a temperature below the malleable temperature after the protrusion has changed to the second shape, and removing the forming tool from the protrusion after the protrusion has cooled to the temperature below the malleable temperature. ■ 4. The method of claim 1 wherein the step of forming the protrusion includes pressing the shaping portion of the forming tool into the heated portion to form a generally funnel-shaped protrusion with the protrusion's proximal end having a first cross- sectional area and a distal portion of the sidewalls having a second cross-sectional area that is smaller than the first cross-sectional area when the distal end and sidewalls define the first shape, and the distal portion of the sidewalls having a third cross-sectional area that is smaller than the second cross-sectional area when the protrusion has changed to the second shape. 5. The method of claim 1 wherein the step of exerting the force on the protrusion includes creating a partial vacuum in the protrusion's interior when the heated portion is malleable to draw the portion of the protrusion into engagement with the forming tool's shaping portion. 6. The method of claim 5 wherein the forming tool has at least one vacuum port therein and the forming tool is adapted to draw a partial vacuum therethrough, and the step of creating a partial vacuum in interior includes drawing the partial vacuum through the vacuum port when the vacuum port is positioned in the interior of the protrusion. 7. The method of claim 1 wherein the step of exerting the force on the protrusion includes exerting from outside the protrusion an exterior pressure on the portion of the protrusion to press the portion of the protrusion inwardly and into engagement with the forming tool's shaping portion. 8. The method of claim 1 wherein the step of exerting an inwardly directed force on the protrusion includes exerting the force on the sidewalls to move the sidewalls into engagement with the forming tool's shaping portion. 9. The method of claim I wherein the step of exerting an inwardly directed force on the protrusion includes exerting the force on the distal end to move the distal end of the protrusion into engagement with the forming tool's shaping portion. 10. The method of claim 1 wherein the forming tool's shaping portion includes a detent mold thereon , and the step of exerting a force on the protrusion to. move the portion of the protrusion inwardly includes moving the portion of the protrusion into engagement with the detent mold to form a detent member therein that mates with the detent mold on the forming tool's shaping portion. 11. The method of claim 1 wherein the protrusion has integrally connected proximal and distal portions after the protrusion has changed to the second shape, and the method further comprising the step of separating the distal portion from the proximal portion. 12. The method of claim 1, further comprising the step of forming an aperture in the distal end of the protrusion. 13. The method of claim 1 wherein the forming tool has a shaping portion with substantially C-shaped cross-section defined by a first outer axial surface with a first radius and a second outer axial surface connected to the first outer axial surface and having a second radius that is smaller than the first radius, the step of exerting a force on the protrusion includes moving the sidewalls to the second shape having a substantially C-shaped cross- section defined by a third outer axial surface with a third radius that substantially conforms to the first radius and a fourth outer axial surface with a fourth radius that substantially conforms to the second radius.. 14. The method of claim I wherein the forming tool's shaping portion' has a plurality of first threads thereon and the step of exerting a force on the protrusion includes moving the protrusion's sidewalls into engagement with the first threads to form a plurality of second threads in the sidewalls that mate with the first threads on the forming tool's shaping portion. 15. The method of claim 1, further including the steps of cooling the protrusion to a temperature below the malleable temperature, and after the cooling step heating a selected portion of the protrusion to the malleable temperature and changing the thickness of the selected portion of the protrusion from a first thickness to a second thickness • that is less than the first thickness. 16. The method of claim 1, further including the steps of removing the forming tool from the protrusion after the protrusion has changed to the second shape, and inserting a second forming tool into the protrusion and changing the thickness of a selected portion of the protrusion from a first thickness to a second thickness that is less that the first thickness. 17. A method of forming a polymeric component having a selected shape, comprising the steps of: retaining a sheet of polymeric film in a selected position; heating the sheet of polymeric film to a malleable temperature to form a heated portion of the sheet; pressing a shaping portion of a forming tool into the heated portion while the heated portion is malleable to form a protrusion having an open proximal end, a distal end, and sidewalls extending between the proximal and distal ends, the sidewalls and distai end defining a first shape having a shape that is different from the shape of the shaping portion of the forming tool; and exerting a differential pressure on the protrusion to move the distal end and sidewalls inwardly to engage with the forming tool's shaping portion with the distal end and sidewalls moving from the first shape to a second shape that conforms to the shape of the forming tool's shaping portion. 18 The method of claim 17, further including the steps of cooling the protrusion to a temperature below the malleable temperature, and removing the forming tool from the protrusion after the protrusion has cooled. 19 The method of claim 17 wherein the step of pressing the shaping portion of the forming tool into the heated portion includes moving the forming tool against the heated portion while malleable to form a generally funnel-shaped protrusion. 20. The method of claim 17 wherein the step of exerting a differential pressure on the protrusion includes creating a partial vacuum within the protrusion when the heated portion is malleable to move the distal end and sidewalls into engagement with the forming tool's shaping portion. 21. The method of claim 20 wherein the forming tool has at least one vacuum port therein and is adapted to draw a partial vacuum therethrough when positioned within the protrusion, and the step of creating a partial vacuum within the protrusion includes drawing the partial vacuum through the vacuum port. 22. The method of claim 17 wherein the step of exerting a differential pressure on the protrusion includes creating an exterior pressure on the protrusion when the heated portion is malleable to press the distal end and sidewalls inwardly into the second shape. 23. The method of claim 17 wherein the forming tool's shaping portion includes a detent mold thereon, and the step of exerting a differential pressure on the protrusion includes moving the sidewalls into engagement with the detent molds to form a detent member therein. 24. The method of claim 17 wherein the shaping portion of the forming tool has a substantially C-shaped cross-section defined by a first outer axial surface with a first radius and a second outer axial surface with a second radius that is smaller than the first radius, and the step of exerting a differential pressure on the protrusion includes moving the sidewalls to the second shape having a substantially C-shaped cross-section defined by a third outer axial surface with a third radius that substantially conforms to the first radius and a fourth outer axial surface with a fourth radius that substantially conforms to the second radius. 25. . The method of claim 17 wherein the forming tool's shaping portion has a plurality of first threads thereon and the step of exerting a differential pressure on the protrusion includes moving the protrusion's sidewalls into engagement with the first threads to form a plurality of second threads in the sidewalls that conform to the first threads on the forming tool's shaping portion. 26. The method of claim 17, further including the steps of cooling the protrusion to a temperature below the malleable temperature, and after the cooling step heating a selected portion of the protrusion to the malleable temperature and changing the thickness of the selected portion of the protrusion from a first thickness to a second thickness that is less than the first thickness. 27. The method of claim 17, further including the steps of removing the forming tool from the protrusion after the distal end and sidewalls have moved to the second shape, and inserting a second forming tool into the protrusion and changing the thickness of a selected portion of the protrusion from a first thickness to a second thickness that is less that the first thickness. 28. A polymeric medical component having a selected shape made by the process of: heating a sheet of polymeric film to a malleable temperature to form a malleable heated portion; forming a protrusion in the heated portion while malleable, the protrusion having an open proximal end. a distal end, and sidewalls extending between the proximal and distal ends, the sidewalls having a thickness in the range of 0.0005 inches to 0.015 inches, inclusive, the sidewalls and distal end defining a first shape of the protrusion; positioning a forming tool in an interior of the protrusion, the forming tool having a shaping portion with a selected shape that is different than the first shape of the protrusion; exerting a force on the protrusion to move a portion of the protrusion inwardly into engagement with the forming tool's shaping portion so the protrusion changes from the first shape to a second shape that conforms to the selected shape of the forming tool's shaping portion; and separating the first portion of the protrusion from the second portion after the protrusion is in the second position wherein the first portion defines the thin-walled polymeric component having the selected shape. 29. The medical component of claim 28 wherein the process step of exerting a force includes exerting a differential pressure on the protrusion so the pressure within the protrusion is less than the pressure exterior of the protrusion to cause the protrusion to change to the second shape. 30. The medical component of claim 28 wherein the process further, includes the steps of cooling the protrusion to a temperature below the malleable temperature, and removing the forming tool from the protrusion after the heated protrusion has cooled to the temperature below the malleable temperature. 31. The medical component of claim 28 wherein the forming tool's shaping portion includes a detent mold thereon, and the process includes the step of exerting a force on the protrusion includes moving the sidewalls into engagement with the detent mold to form a detent member in the sidewalls that conforms to the detent mold on the forming tool's shaping portion. 32. The component of claim 28 wherein the process further includes the step of forming an aperture in the distal end of the protrusion. 33. The component of claim 28 wherein the forming tool's shaping portion has a plurality of first threads thereon and the process step of exerting a force on the protrusion includes moving the protrusion's sidewalls into engagement with the first threads to form a plurality of second threads in the sidewalls that conform to the first threads on the forming tool's shaping portion. 34. The component of claim 28 wherein the distal end of the protrusion is a closed distal end defining an optically transparent viewing window connectable to an endoscopic sheath. 35. The component of claim 28 wherein the process further includes the steps of cooling the protrusion to a temperature below the malleable temperature, and after the cooling step heating a selected portion of the protrusion to the malleable temperature and changing the thickness of the selected portion of the protrusion from a first thickness to a second thickness that is less than the first thickness. 36. The component of claim 28 wherein the process further includes the steps of removing the forming tool from the protrusion after the protrusion has changed to the second shape, and inserting a second forming tool into the protrusion and changing the thickness of a selected portion of the protrusion from a first thickness to a second thickness that is less that the first thickness. 37. A vacuum forming tool capable of forming a medical component from a malleable polymeric protrusion so the medical component has a selected shape, comprising a shaft having an air passageway and having a forming portion that has a shape corresponding to the selected shape of the medical component, the forming portion having a forming surface and an aperture extending from the forming surface to the air passageway, the shaft being connectable to a vacuum source so the air passageway communicates with the vacuum source to allow the vacuum source to draw air through the aperture into the air passageway to form a partial vacuum within the malleable polymeric protrusion during formation of the medical component. 38. The vacuum forming tool of claim 37 wherein the shaft is connectable to the vacuum source so air is drawn through the aperture into the air passageway to create a force sufficient to draw the malleable polymeric protrusion into engagement with the forming surface. 39. The vacuum forming tool of claim 37 wherein the forming portion has a cross-sectional shape that corresponds to a cross sectional shape of the selected medical component. 40. The vacuum forming tool of claim 37 wherein the forming portion is threaded. 41. The vacuum forming tool of claim 37 wherein the forming portion has a generally C-shaped cross-section. 42. The vacuum forming tool of claim 37 wherein the forming tool has a concave distal end. 43. The vacuum forming tool of claim 37 wherein the forming tool has a detent member thereon for forming a detent in the medical component. 44. The vacuum forming tool of claim 37 wherein the forming portion has a plurality of apertures that communicate with the air passageway. 45. An endcap for use with a sheath that covers a portion of a medical device having a selected cross-sectional shape, comprising an open proximal end, a closed distal end, and sidewalls defining an interior area that receives the portion of the medical device, the sidewalls being connectable to the sheath, the sidewalls having a thickness in the range of approximately 0.0005 inches to 0.015 inches, inclusive, the endcap's interior area having a cross-sectional shape that substantially correspond to the medical device's selected cross-sectional shape. 46 . The endcap of claim 45 wherein the closed distal end is an optical lens. 47. The endcap of claim 46 wherein the lens has a first thickness and the sidewalls have a second thickness that is less than the first thickness.

Inventors: GODDARD JAMES M, HARHEN E PAUL, GODDARD, JAMES, M., HARHEN, E., PAUL
Applicants: VISION SCIENCES INC, VISION SCIENCES, INC.
Application year: 2000
Main classification: A61B1
IPC codes: A61B1, B29C51