REDUCTION OF N2O EMISSIONS

Abstract: The invention relates to a method for the selective catalytic reduction of nitrous oxide (N2O) in the presence of a solid catalyst, with the addition of a saturated hydrocarbon as reducing agent. The invention is characterized in that the catalyst used is a promoted, iron-containing zeolite. As a result, it is possible to increase the conversion of (NO2) compared to unpromoted iron-containing zeolite catalysts. The promoted catalyst according to the invention is active at temperatures below 350 DEG C. Furthermore, it has been found that the iron-containing zeolite catalysts which are promoted with precious metal also give low emissions of CO and residual hydrocarbons. The catalyst is also very active under high process pressures and in the presence of sulphur.

Description: Reduction of N 2 O emissions Background Nitrous oxide (dinitrogen oxide, N2O) makes a substantial contribution to the greenhouse effect. The global wanning potential (the extent to which a molecule contributes to the greenhouse effect compared to one molecule of CO 2 ) of N 2 0 is approx. 310, For a number of years, the policy of reducing emissions of greenhouse gases has been developed. The present invention can make a si nificant contribution to this policy. Various significant sources of N 2 O emissions have been identified: agriculture, industrial production of nylon precursors (adipic acid and caprolactam), the production of nitric acid and motor vehicles fitted with a three-way catalyst. In principle, various catalytic and non-catalytic techniques can be employed in order to render nitrous oxide harmless. Various catalysts are known for the direct catalytic decomposition of N 2 to N2 and O 2 (cf, the literature summary provided by Kapteijn et al., Appl. Catal. B9 (1996), pp 25-64 and US-A-5,171,553). However, this reaction is hampered to a considerable extent by the presence of oxygen and water, which are to be found in the off-gases from virtually all the NiO sources listed above. Selective catalytic reduction is a promising alternative. Various catalysts for the conversion of N 2 O with the aid of olefiπs (C π Hι n ), alcohols or ammonia have been studied in the literature (recently: Mauzevin et al. Appl. Catal. B23 (1999) L79- 82 and Pophal et al. Appl Catal. B16 (1998) pp. 177-186 and the literature cited therein). Catalysts employed are often zeolites which have been substituted with a transition metal, such as iron, cobalt or copper. For both technical and economic reasons, the addition of saturated hydrocarbonE (C f ,H2n +2 ) would be preferable to the abovementioned reducing agents. Natural gas (CH 4 ) and LPG (mixture of C 3 H 8 and C4H10) are particularly attractive in this context, It is important that the formation and emission αf carbon monoxide (CO) and emission of unreacted hydrocarbons be minimized. The present invention relates to a catalyst which enables N 2 O to be converted into nitrogen at a relatively low temperature and which allows very low emissions of CO and hydrocarbons to be achieved. Prior art International Patent Application WO 9949954 has described a method for the catalytic reduction of N 2 0 in the presence of a zeolite with the addition of a reducing agent, the reducing ageπ ed_ . beuιg .a^ (CH 4 ), propane (C 3 Hs), LPG (C 3 HB/C 4 HIO), or a combination of these reducing agents. It has been found that complete conversion of ∑O can be achieved at reaction temperatures of 400°C or lower, even with very low concentrations of the reducing agent and in the presence of water vapour, oxygen and sulphur dioxide. The catalyst involves a specially prepared iron-substituted zeolite. Japanese patent publications JP 05103953 and JP 07213864 describe the removal of N 2 O in the presence of, respectively, methane and propane with the aid of (inter alia) and iron-zeolite catalyst. However, these methods take no account αf the emission of CO and unreacted hyrocarbons. To prevent undesirable emission of CO and residual hydrocarbons, Japanese patent publication JP 09000884 describes the mechanical mixing of an iron-zeolite catalyst with a supported platinum or palladium catalyst. The N 2 O conversion is around 60% at 450°C in a gas which contains oxygen and water. The conversion of NaO achieved with the mechanically mixed catalyst is significantly worse than with the iron-zeolite catalyst alone. JP 05103953, JP 07213864 and JP 09000884 all lack information about the effectiveness of the invention under pressure and/or in the presence of sulphur compounds. This is essential for use in the production of nitric acid and caprαlaciam, respectively, Discovery of a novel catalyst One object of the present invention is to provide a method for the removal of NjO from industrial gas streams which contain O2, H2O, NO x and possibly sulphur and which may be at elevated pressure. A further object of the present invention is to bring about the abovementioned removal of N 2 O by the addition of saturated hydrocarbons at a reaction temperature of lower than 400°C, with very low emissions of CO and unreacted hydrocarbons. To this end, the method according to the invention is characterized in that the catalyst used is a promoted, iron-containing zeolite. The zeolite catalyst is preferably promoted with a precious metal. The use of an iron-containing zeolite catalyst which has been promoted preferably with precious metal (Rh, Pd, Ru, Pt, Au, etc.) in the SCR of 2 O with the aid of saturated hydrocarbons (CnF ϊ has surprisingly led to increased conversion of N2O compared to an unpromoted iron-containing zeolite catalyst. The promoted catalyst is active at temperatures of below 350°C. Furthermore, it has been found that the iron-containing zeolite catalyst which has beerLpJLomoted.with. recious met l reduces.the emissions of CO and residual hydrocarbons very considerably at the operating temperature compared to an unpromoted iron-containing zeolite catalyst. In addition, it has been found that the catalyst according to the invention is also active in the removal of nitrogen oxides (NO + Nθ2 = NO )t ). This is important in view of the fact that NO x are also released from the various sources of NjO. It has also been found that the catalyst described is also very active in the desired conversion at elevated process pressure, at which it is even more active than at atmospheric pressure. This is an important fact with regard to its application in the nitric acid industry. Finally, it has been found that the catalyst described is active if sulphur is present in the feed. This is an important fact in connection with its application in the nylon industry. The invention will be explained in more detail with reference to the following examples together with the associated figures, in which: Figure 1 shows the degree of conversion of N 2 O as a function of temperature for four iron-containing zeolite catalysts promoted with precious metal (A, D, E and F). For comparison purposes, the N2O conversion achieved by an unpromoted iron-containing zeolite catalyst (X) is also shown. The test conditions are described in Table 2 (SV - 19,500 h " ', pressure = 3 bara, C 3 H 8 concentration = 1900 ppmv). Figure 2 shows the CO emissions which occur during the conversion of N 2 O using the same catalysts and under the same conditions as in Figure 1. I. Preparation of the catalysts The catalysts according to the present invention are produced by adding zeolite Na-ZSM-5 or NH4-ZSM-5 to a solution of (Mohr's salt). After they have been combined, ion exchange is carried out for 8 hours at 80°C. The resulting suspension is filtered, the solid material is washed, is dried at 80°C and is calcined at 550°C. The Fe-ZS -5 base material obtained in this way is then impregnated with a volume of a solution of a precious metal precursor in demineralized water which is such that the pores of the base material are precisely filled (so-called incipient wetness impregnation). The concentration of the precious metal precursor is set in such a manner that the desired quantity of precious metal on the base material is obtained. Fmally, the catalyst is dried at 80 β C and calcined at 550°C The catalyst powder obtained is pressed into a tablet, is ground and is screened. The following catalysts are used in the examples: Table 1 II. Test apparatus The conversion of NjO by means of SCR using propane and methane was studied in an automated flow arrangement The gases Nj, air, NjO, CsHβ, CH- > , NO, NO 2 are introduced by means of calibrated mass flow controllers (Brooks), Water is added via a Liquiflow controller and a controlled Evaporator Mixer (Bronkhorst). The gases emerging are analysed by means of a calibrated FTTR spectrophotometer (Elsag, Bailey, Hartmann & Brown, type MB 100). The catalyst is in a stainless steel reactor, The gases are passed through a preheating section before they come into contact with the catalyst. The temperature at the entry to and exit from the catalyst bed is measured using thermocouples. The mean of these two temperatures is shown in the results of the tests. The pressure in the test arrangement can be set at levels of between 1 and 5 bar absolute (bara). The gas composition in the examples is representative for use of the catalyst according to the present invention in the nitric acid industry. The general test conditions are aβ follows: Table 2 Til. Influence of the addition of precious metal to iron-containing zeolite Figure 1 shows the NjO conversion curves for the catalyst from Table 1 (test conditions as in Table 2, SV = 19,500 K pressure = 3 bara, C 3 H B concentration - 1900 ppmv). The promoted catalyst (A,D,E,F) are more active than the unpromoted iron-containing zeolite catalyst X. This is evident from the shift of the N.O conversion curves towards a lower temperature compared to the unpromoted Fe-ZSM-5 catalyst X. Figure 2 shows the CO concentrations as a function of temperature for the same catalysts under the same conditions. When using catalyst X and catalyst F, CO is formed throughout the entire temperature range. The other catalysts are excellent at eliminating CO emissions; if catalyst E is used, the amount of CO at over 350 Q C is lower than 10 ppmv, and with catalysis A and D this level is already achieved from 300 β C Comparative tests between catalyst A (containing 0.05% Pd) and catalysts B and C (respectively containing 0,1% and 0.3% Pd) reveal similar curves for both N 2 O conversion and CO formation. This means that a low concentration of precious metal is sufficient, reducing the cost of the catalyst. Table 3 shows the concentrations of the compounds which leave the reactor at a mean temperature of 350°C for a number of catalysts (test conditions as in Table 2, SV = 19,500 h " ', pressure = 3 bara, C 3 Hs concentration = 1900 ppmv). Table 3 ft NO x = NO + NO 2 For all the catalysts, the N 2 O and C 3 Hβ conversion levels are higher than 90% at 350°C. For the catalysts which contain Pd and Rh, the CO emission is negligible. Another surprise is that the catalysts also remove from 60 to 75% of the NO,. IV. Activity of the promoted iron-containing zeolite catalysts at increased process pressure and space velocity Increasing the process pressure has a beneficial affect on the activity of the catalysts. Table 4 shows the concentrations of a number of components of the emerging gas, at -1—3 and-5 bara-and at-a eaction-temρerature-of-3S0 p C (test conditions as in Table 2, catalyst A, SV « 19,500h " ', C 3 H 8 concentration ^ 1900 pmv). The N2O conversion level remains greater than 90%, while propane slippage, CO and NO x emissions fall as the process pressure rises. Table 4 "NO x =NO + NO a At a process pressure of 4 bara and under conditions as in Table 2 (catalyst A, SV ^ 13,000 h"'), increased activity was measured when the propane concentration was increased from 1500 to 2000 ppmv. Further increasing the propane/NϊO ratio had no further positive effect on the conversion of N 2 O. Experiments under conditions as in Table 2 (catalyst A, pressure - 4 bara, C 3 HB concentration = 1900 ppmv) indicate that the space velocity can be increased from 13,000 to 45,000 h "1 without the activity of the catalyst being adversely affected. The stability of the catalyst is tested for 50 hours in the conditions as described in Table 2. No deterioration in the activity was detected. V. NjO conversion in different gas compositions Table 5 demonstrates that the catalyst according to the present invention also functions well with higher water concentrations and higher oxygen concentrations, The table describes experiments in different gas compositions (conditions as in Table 2, catalyst B, SV = 13,000 ft" 1 , no NO and NO 2 present) Table 5 1 In the presence of 250 ppmv NO The catalyst X was tested in the presence of SO 2 (500 ppmv N 2 0, 500 ppmv C 3 Hβ, 6% H20, 500 ppmv NO, 160 ppmv SO^ SV - δOOO h "1 , y = 440-460°C). The catalyst is able to withstand sulphur: no deactivation was detected over a period of 550 hours under the above conditions.

Claims: CLAIMS 1. Method for the selective catalytic reduction of nitrous oxide (N 2 O) in the presence of a solid catalyst, with the addition of a saturated hydrocarbon as reducing agent, characterized in that the catalyst used is a promoted iron-containing zeolite. 2. Method according to Ciaira 1, characterized in that the catalyst is promoted with a precious metal. 3. Method according to Claims 1 and 2, characterized in that the precious metal comprises ruthenium, rhodium, palladium, gold or platinum, or a combination of two or more of these metals. 4. Method according to Claim 1, characterized in that the reducing agent used is natural gas or methane (CH 4 ) or propane (CiH.) or LPG (C3H8/C 4 H 1 0), or a combination thereof. 5. Method according to Claims I and 4, characterized in that the concentration of the reducing agent is set in such a way that the hydrocarbon N2θ molar ratio is in the range from 0.2 to 20, preferably in the range from 0.S to 5. 6. Method according to Claim 1, characterized in that the reduction takes place at an inlet temperature of less than 400°C. 7. Method according to Claim 1, characterized in that the emission of carbonmonoxide (CO) and of hydrocarbon is in each case separately less than 100 ppmv. 8. Method according to Claim 1, characterized in that the process pressure at which the reduction takes place is between 1 and 50 bar absolute.

Inventors: VERHAAK MICHAEL JOHANNES FRANC, VERHAAK, MICHAEL, JOHANNES, FRANCISCUS, MARIA
Applicants: STICHTING ENERGIE, VERHAAK MICHAEL JOHANNES FRANC, STICHTING ENERGIEONDERZOEK CENTRUM NEDERLAND, VERHAAK, MICHAEL, JOHANNES, FRANCISCUS, MARIA
Application year: 2000
Main classification: B01D53
IPC codes: B01D53