POROUS AND MAGNETIC, INORGANIC-BASED COMPOSITE MATERIAL USED AS SORBENT FOR CLEANING WATER AND THE ENVIRONMENT FROM OIL SPILL

Abstract: The present invention is about a new porous and magnetic, inorganic-based composite material, its production process and its use as a sorbent to preferentially sorb oil (such as crude oil) in mixtures with waters (oil spills in the sea, lakes etc.) and separate the oil (from waters) by magnetic separation or other mechanical methods and recover the oil with a potential of a nearly 100 % efficieny. The same material and methods can be applied to clean and recover oils from oil spills formed on the ground or other solid surfaces.

Description: POROUS AND MAGNETIC , INORGANIC-BASED COMPOSITE MATERIAL USED AS SORBENT FOR CLEANING WATER AND THE ENVIRONMENT FROM OIL SPILL DESCRIPTION 1. Introduction As of today, the methods used for oil spill cleaning are mechanical and chemical methods. The mechanical methods employ booms to surround the oil spill and special pumps and skimmers to recover the bulk of the oil. This method is messy, time consuming and inefficient. Although it can help remove a major part of the oil, still a large portion remains on the surface of the waters, which by the time reaches the coast causing unrecoverable environmental pollution. To remove the remaining of the oil, special sorbing materials are used (usually based on polypropylene). These materials are good but they are difficult to be applied on the oil spill and difficult to recover from the water. Also, they are quite expensive. The chemical methods employ spraying of chemical dispersants or detergents in order to break the oil spill into very small drops which sink in the bulk of the water and which will "hopefully" biodegrade by time which could be months or years. Usually, the heavy components of the oil sink in the bottom of the waters causing a permanent marine pollution. The disadvantage of the use of the chemical methods is that the oil essentially remains and pollutes the waters for long times causing unpredictable damages to the environment and to the ecology systems around the pollution. In addition, the chemicals used can be considered to be an additional pollutant. Other techniques, such as in situ combustion of the oil, can cause other atmospheric pollution problems (SO2, CO, CO2, C, etc.). Also, the heavy constituents of the oil consolidate and sink at the bottom of the waters causing permanent pollution. As a consequence of the partial efficiency of the existing mechanical methods, the partial efficiency and burdening of pollution by chemical methods, the waters are being day by day more polluted, and there is an urgent need of developing new effective sorbent materials and methods to combat oil spills. In order to minimize the pollution from oil spills, one has to physically remove almost the entire amount (nearly 100%) of oil from the waters. This has to be done in an efficient and cost effective way which requires new materials and new recovery methods. In the present invention, a new low-cost, magnetic and sorbent material is described which can be used to meet all concerns regarding physical removal (nearly 100%) of the oil from the waters and the environment (ground and other solid surfaces). It is a solid state particulate material which can be applied easily on the oil spill, it immediately sorbs the oil forming a cohesive floating mixture of oil trapped in the pores of the solid material, which can be separated from the waters and the environment by magnetic separation. For example, one can use an electromagnet or any magnetic system coming in close distance or contact with the mixture, lifting it and store it on a vessel or in a storage container. Other mechanical methods, for example, "fishing" the mixture in nets can also be used. The new material is named herein "EcoMag" and it has been developed to exhibit the following properties: 1) It is chemically based on inorganic materials (not copolymers or other organic materials) which are inert to the environment (waters, ground, air) and are common earth constituents. 2) It is porous in order to sorb and trap the oil. 3) It is magnetic in order to be attracted by a magnet (electromagnet or permanent magnet) and to be able to be separated by magnetic means. 4) It is by itself oleophilic (not with the use of any surfactants) in order to attract and sorb oil. 5) It is very light in order, even after sorbing the oil, to float on the surface of the waters. 6) The material is usually used in the form of particles, which attract magnetically each other (the degree of magnetic attraction can be controlled). Therefore, after sorbing the oil, the "magnetically connected" particles form cohesive mixtures of "floating islands" which prevent the spreading of the oil spill and retaining its size. 7) By applying the material on the crude oil, it sorbs the crude oil and holds on to the heavier components. Therefore, as natural evaporation of the lighter components of the crude oil occurs, the heavier components (asphalt) are prevented from sinking at the bottom of the sea, an event which causes unrecoverable marine pollution. 8) The oil can be recovered from the mixture by centrifugation or by solvent extraction. 9) The material-oil mixture can be directed for burning, for example in the cement industries, the solid material remaining as inorganic ash which can co-participate in the final cement product of it can be disposed off in the fields (it is inert to the ground). 10) The material can be produced and applied on the oil spill in situ, for example, on the oil spill combating vessel. 11) The cost of the material is very low because of the low cost of the raw materials and the manufacturing cost. It is brought to the attention that, a material with similar sorption and magnetic properties exists in the patent of IAN PCT/GR97/00002 and IPN WO 98/17387 with the name "CleanMag". There is though a tremendous difference between "CleanMag" and "EcoMag". The major porous components of "CleanMag" which sorb the oils are organic copoiymers whereas the major porous component of "EcoMag" is inorganic matter. Therefore, their major components which sorb the oils are completely different materials. Also, they completely differ in their production process. In order to produce "EcoMag", temperatures in excess of 800 °C are needed. At such temperatures, "CleanMag" melts and irreversibly deteriorates by burning due to its organic components. Therefore the two materials are completely different. In the present patent, the claims are based on the materials' copmposition and its production process. Although both materials (CleanMag and EcoMag) can be used for similar applications (oil spill cleaning by magnetic separation), since the materials' compositions and the production process of the two materials ("CleanMag" and "EcoMag") are different, the two patents are different. Also, a major merit of "EcoMag" is that its final cost is much less than that of "CleanMag" due to the much lower raw materials' cost and the simple, cheap production cost. Also, the organic nature of "CleanMag" poses problems for disposal (or atmospheric pollution if burnt), whereas "EcoMag" is friendly to the environment because its components are earth's inorganic constituents. 2. Th© "EsoSSag" fssiaS product EcoMag is an inorganic-based composite consisted of a porous matrix component and a magnetic material component. 2.1 Porous matrix component The porous matrix material is chemically inorganic and consists of several metals (Silicon, Aluminum, Potassium, Sodium, Iron, Calcium, Magnesium, other metallic traces) in the form of pure oxides/silicates and/or in the form of oxide/silicate mixtures, in the crystalline and/or amorphous state. τ . .. . .. volume of voids . ... The porosity fraction ( vo of voids + voK of so|ids ) f the porous matrix can be estimated by the formula, do porosity fraction = (1 - -f-), where, -i ■ j. i i mass of solids % _, ._. * * u * ■ dp is the apparent ( volume of (so , ids + voids) ) dens.ty of the porous matrix, and d s is the bulk ( — : f goι . ds ) density of the matrix (porous-free matrix). The bulk density of the matrix (d s ) is usually between 2000kg/m 3 and 2500kg/m 3 . The porous matrix is considered to be the only component of EcoMag which sorbs the oil. The magnetic material component may sorb small amounts of oil but they are considerably less than that of the porous matrix. It can be shown that the "sorption capacity" of the porous matrix can be calculated from the formula: Volume of oil _ _ v ~ Mass of porous matrix d p " d s Kϋ Mass of oil 1 1 . Mm = -T.- - = o ( T" - T" ) > where d 0 is the oi density. m Mass of porous matrix ° d p d s Assuming d s =2100kg/m 3 , d p =100kg/m 3 and d 0 =800kg/m 3 , the "sorption capacity" (Mv) is estimated to be 9.5x10 "3 m 3 /kg or 9.5 liters of oil per 1kg of porous matrix. The "sorption capacity" (M m ) is also estimated to be 7.6kg of oil per 1kg of porous matrix. If d p =200kg/m 3 , the "sorption capacity" is estimated to be M =4.5 liters and M m = 3.6kg of oil per 1 kg of porous matrix. There is a practical upper limit to the apparent density of the porous matrix (d p ) if it is to be used for waterborne oil spill cleaning. The porous material (without any magnetic material) together with the sorbed oil has to float, and therefore, the density of the mixture (porous matrix + oil) has to be less than that of the water (about 1000kg/m 3 ). In order to meet this "floating criterion" it can be shown that the upper limit to the apparent density of the porous matrix s •hou wld be: d A p = 100 ° - -; — p 1 _°. " d s For an oil density d 0 =800kg/m 3 and a matrix bulk density d s =21 OOkg/m 3 , the upper limit for the apparent density of the porous matrix is estimated to be d p =323kg/m 3 . For light oils, with d 0 =800kg/m 3 and d s between 2000-2500kg/m 3 , the upper limit of the d p should be 333-294kg/m 3 , accordingly. For heavy oils, with d o =950kg/m 3 and d s between 2000-2500kg/m 3 , the upper limit of the d p should be 95-80kg/m 3 , accordingly. Therefore, it is desirable for the apparent density (d ) of the porous matrix to be as low as possible. Practically, it is found that the lower apparent density (dp) which can be achieved is 25kg/m 3 due to processing limitations. If the porous matrix is going to be used in oil spills formed on the ground and/or other solid surfaces, no "floating criterion" has to be met and therefore, there is no strict limitation to its apparent density. It is desirable that the pores of the porous matrix are open cell type in order to sorb the oil. The presence of some closed cell type pores is not deterrent for the sorbing properties of the final product. The sizes of the pores are between 1x10" 9 m and 3x10' 3 m. Usually, there is a broad distribution of the pores sizes which does not affect seriously the sorption properties of the porous matrix. The problem arises only when this distribution is shifted to the higher sizes of the pores (3x10 _3 m). The problems in such a case are related to the fact that the sorbed oil is not strongly trapped in the pores and can start dripping out of the porous matrix, an event which is undesirable. The porous matrix is produced in the form of porous particles with a particle size preferably between 0.2x10 3 m to 20x10 m in average diameter (assuming nearly spherical particles). The shape of the particles can be irregular (any shape) and it is non-important for the final sorbing properties of EcoMag. 2.2 Magnetic material component The magnetic material, used to form the composite together with the porous matrix, is necessary to be ferromagnetic and/or ferrimagnetic at least in the temperature range of -30°C to 50 °C. In practical terms, this means that the magnetic material is necessary to be attracted by a magnetic field at least in the temperature range of -30°C to 50°C, temperature conditions in which one may have to combat oil spills. It is also possible that the magnetic material can be attracted in other temperatures out of this range. Magnetic materials which are not ferromagnetic and/or ferrimagnetic in the temperature range of -30°C to 50°C are excluded. Magnetic materials suitable for this purpose are iron (Fe) metal and/or iron alloys (containing at least 50 wt% Fe), iron(il) Oxides (FeO x , x is about 1), Iron(lll) Oxides (γ-Fβ2θ3 maghemite, α-Fe2θ3 hematite), Iron Hydroxides (Fe(OH)2 or Fe(OH)3), Fβ3θ4 magnetite, Ferrites (such as Sr-ferrite and Ba-ferrite), other Iron, Cobalt and Nickel-based metallic alloys (such as RE-Fe(Co,Ni)-B(C), RE- Co(Fe,Ni) alloys, where, RE=La, Ce, Pr, Nd, Sm, Y, Dy, Tb, Gd, Eu, Yb, Ho). From the final cost point of view, Fe, γ-Fβ2θ3 maghemite, Fesθ4 magnetite, Sr- ferrite, Ba-ferrite, other ferrites, and/or mixtures of them are the most suitable. Magnetic metal alloys containing RE metals may be used only in special occasions where cost is not an important issue. The magnetic material is used in the form of particles with a particle sizes of between 1x10- 9 m to 10x10 _ m in average diameter (assuming nearly spherical particles). The shape of the particles can be irregular (any shape) and it is non- important for the final sorbing and magnetic properties of EcoMag. The magnetic material is usually of very low porosity (nearly porous-free) The magnetic properties of various suitable magnetic materials are listed in Table 1. It is shown that, the Curie Temperatures (temperature at which a material looses its magnetization) of such magnetic materials are far above the room temperature in order to be of practical used. The saturation magnetization (M s ) together with the remanent magnetization (M r ) give a measure of the "magnetic separation ability" of the mixture (EcoMag + oil) by magnetic separation methods. This is because the magnetic attraction force is approximately proportional to the materials' magnetization. The coercive magnetic field (H c ) together with the remanent magnetization (M r ) give a measure of the "degree of cohesiveness" between the EcoMag particles. The EcoMag particles which contain magnetic materials with high H c and M r behave as small permanent magnets which attract each other, binding them together in a cohesive manner. Table 1 Properties of Magnetic Materials 2.3 The EcoMag Composite The EcoMag composite consists of porous matrix particles and magnetic material particles. Usually, the appearance of EcoMag is in the form of one porous matrix particle carrying one or more magnetic material particles. EcoMag is naturally oleophilic because its main components (matrix and magnetic materials) are oleophilic themselves. EcoMag can be characterized by its "sorption capacity", its "magnetic separation ability" and its "degree of cohesiveness". The effects of the increase of the wt% concentration of the magnetic material on EcoMag are: a) The EcoMag's "sorption capacity" drops due to the decrease of the porous matrix. b) The EcoMag's "magnetic separation ability", on the one hand drops due to the increase in EcoMag's apparent density and, on the other hand increases due to the larger magnetic attractive force induced on EcoMag by the magnetic s eparation system. c) The EcoMag's "degree of cohesiveness" enhances due to the larger magnetic attractive force induced among EcoMag particles. The magnetic material component adds to the apparent density of EcoMag. There is an upper limit to the wt% concentration of the magnetic material, if EcoMag is to be used for waterborne oil spill cleaning. This is due to the "floating criterion" which requires the density of EcoMag carrying the sorbed oil to be less than the density of the water (1000kg/m 3 ) in order to float. If the density of the magnetic material (which it is assumed to be free of pores) is d m , the upper limit wt% concentration of the magnetic material (for the overall density of "EcoMag+sorbed oil" to be less than 1000kg/m 3 ) can be estimated as follows: Assuming a wt% concentration of the magnetic material in EcoMag, then the (100-wt%) is the weight percent of porous matrix in EcoMag. The "sorption capacity" (M m ) (mass of oil sorbed per kg of porous matrix) of porous matrix was shown before to be: For the "floating criterion" to be met, Mass of porous matrix+Mass of magnetic material+Mass of oil i n ι, 3 Volume of magnetic material+apparent volume of porous matrix < '^ __ £ 100 + (100 - wt%)xM m J Λ „ ΛI , . , hΘrefore ' " wt% . - (100 - %) '- ~ < 1000k 9 m3 d m dp or after mathematical manipulations, the upper limit of the wt% concentration of the magnetic material in EcoMag has to be: Therefore, the upper limit wt% of magnetic material depends on the apparent density of the porous matrix (d p ), the bulk density of the matrix (d s ), the density of the magnetic material (d m ) and density of the oil (d 0 ). Assuming a porous matrix of d p =100kg/m 3 and d s =2100kg/m 3 , an oil of d o =800kg/m 3 and a magnetic material of d m =5200kg/m 3 (for example for ferrites), the wt% upper limit for the magnetic material to meet the "floating criterion" is estimated to be 63.1 wt%. If d p =300kg/m 3 , this upper limit becomes 5.6 wt%. The lower limit of the wt% concentration of the magnetic material is determined by the desired EcoMag's "magnetic separation ability" (MSA). This is related to the fact that the magnetic material has to be able to induce (in the presence of a magnetic field of the magnetic separation system) an attractive force able to lift the weight of the mixture of EcoMag with the sorbed oil. The "sorption capacity" of EcoMag can be shown to be: Volume of oil _ wt% _1_ _ SCv = Mass of EcoMag = (1 " 100 d p " d s ' Qr _ Mass of oil wt% _1_ _ aυm " Mass of EcoMag " w " 100 n d p ~ d s ' The "magnetic separation ability" (MSA) of EcoMag is defined as the mass (weight) of the mixture "EcoMag+oil" to the EcoMag's original mass (weight) and becomes: wt% 1 1 MSA -n do α - oo- x^ -^ ) ] The lower limit of wt% concentration of the magnetic material in EcoMag in order to meet the "MSA criterion" has to be: _.„, r . . nnn/ wt% =[ 1 - ]x100% For example, the wt% concentration of the magnetic material present in EcoMag able to develop an attractive magnetic force at least equal to MSA times its original weight (MSA=5), assuming, EcoMag with d =100kg/m 3 , d s =21Q0kg/rn 3 , oil density of d 0 =800kg/m 3 , is estimated to be 47.5wt%. If dp=150kg/m s , this value becomes 19.2wt%. Therefore, the wt% concentration of the magnetic material in EcoMag is bounded by wt% = x100% (upper limit) in ■ q o _!_ _L _1_ dp " 1000 [ dp " d s " d m order to me criterion" and by wt% =[ 1 - ]x100% (lower limit) in order to meet the "MSA criterion". For a given magnetic separation system, the magnetic attraction force per kg of EcoMag (F [=] N/kg) is approximately proportional to the magnetization (M [=] emu/kg) of EcoMag's particles: F=kM, where k [=] N/emu, is a proportionality constant which mostly depends on the magnetic separation system and can be determined experimentally. The magnetization (M) of EcoMag is equal wt% to the magnetization of the magnetic material in EcoMag: M= T Q - M S , where, M s [=] emu/kg is the saturation magnetization of the magnetic material (see Table 1). Therefore, for the force to be able to lift the weight of EcoMag it can be wt% written that, k(~T7χ? M s ) = (MSA)g, where g is the acceleration of gravity (of about wt% 1 1 9.8N/kg). Combining this equation with MSA = [ 1 +d 0 (1 - ^ - )( -7- - -7- ) ] , one 1 UU Op Qs can express the lower limit of wt% concentration of the magnetic material as: wt% where g=9.8N/kg Therefore, It becomes clear that magnetic materials with higher saturation magnetization (M s ), are able to develop the same force in smaller quantities, and smaller wt% concentrations of magnetic material are needed. From Table 1 , it can be seen that, Fe (M s =2x10 5 emu/kg) can be used in lower concentrations than the other magnetic materials such as iron oxides of ferrites. For a given magnetic separation system of k=1x10 _2 N/emu, EcoMag with d p =100kg/m 3 , d s =2100kg/m 3 , oil density of d o =800kg/m 3 , and Fe particles (M s =2x10 5 emu/kg, d m =7870kg/m 3 ), the lower limit for the wt% concentration of the magnetic material in EcoMag is estimated to be 4.07%. At the same time, the MSA is 8.31 and the estimated upper limit for the wi:% concentration of the magnetic material in EcoMag is 61.3%. if Sr-ferrite is to be used (M s =0.7x10 5 emu/kg, d m =5200kg/m 3 ), the lower limit for the wt% concentration of the magnetic material in EcoMag is estimated to be 10.90%. At the same time, the MSA is 7.79 and the estimated upper limit for the wt% concentration of the magnetic material in EcoMag is 63.1%. If the EcoMag is going to be used in oil spills formed on the ground and/or other solid surfaces, no "floating criterion" has to be met and therefore, there is no strict upper limitation to its wt% concentration of the magnetic material. Another important property of EcoMag is the "degree of cohesiveness" among the EcoMag particles. This is an important property because the EcoMag particles with the sorbed oil attract each other forming large floating masses which become less mobile and hold on to the oil, preventing the spreading of the oil spill especially when there are waves in the sea. The formation of large floating masses is desirable, adding to the magnetic separation ability and effectiveness of the separation method. The "degree of cohesiveness" depends on the permanent magnetic properties of the magnetic material used in EcoMag. The permanent magnetic properties of the magnetic material are the coercive magnetic force (He) and the remanent magnetization (M r ) (see Table 1 ). Ferrites, such as Sr-ferrites can give a high "degree of cohesiveness" whereas iron particle which exhibit high MSA can give almost none. Therefore, a mixture of ferrite and iron particles could give a reasonable "degree of cohesiveness" and MSA. Another consideration is the cost ("cost criterion") of the magnetic materials. Ferrites are more expensive than iron which is more expensive than magnetite. Therefore it might be desirable to increase the MSA of EcoMag by substituting ferrite (M s =0.7x10 5 emu/kg) by magnetite ( M s =0.85x10 5 emu/kg) rather than iron. Therefore, the general guides in using the magnetic material (type and wt% concentration) in EcoMag are the following: a) Use the smallest possible wt% concentration of magnetic material which meets the "MSA criterion" and the "floating criterion" for a desirable EcoMag's "degree of cohesiveness". b) Use the smallest (with respect to magnetite and iron) amount of ferrites if EcoMag is going to be used in "low energy seas" (low "degree of cohesiveness" is needed) and largest amount in "high energy seas" (high "degree of cohesiveness" is needed), assuming that the "MSA criterion" and the "floating criterion" are met. 3. Raw materials and production of EeoWϋag 3.1 Raw materials The raw materials to produce the final product (EcoMag) are divided into two categories: a) The raw materials for the porous matrix (essentially non-magnetic) component b) The raw materials for the magnetic material component 3.1.1 Raw materials for the porous matrix component The raw materials for the porous matrix component of EcoMag are completely of inorganic nature. The physical properties of the raw materials for the porous matrix component of EcoMag (processed final product) are almost completely different than that of the starting raw materials (pre-processed material). The raw materials for the porous matrix component are metal oxides/silicates of silicon (Si), aluminum (Al), potassium (K), sodium (Na), iron (Fe), calcium (Ca), magnesium (Mg) and other metallic traces, in the form of pure components and/or in the form of processed mixtures, and/or naturally occurring mixtures/minerals (for example silicates/oxides/carbonates), in the crystalline and/or amorphous state. The raw materials are mixed with a small amount of foaming agents (usually inorganic compounds). In the cases where naturally occurring mixtures/minerals are used as raw materials, the foaming agents exist naturally in the raw materials, usually in the form of water (H2O). The foaming agent is very important in order to promote porosity in the final product. The best candidate raw material for the porous matrix component is a naturally occurring mineral known as Perlite. Perlite is not a trade name but a generic term for a naturally occurring silicous glassy rock originating from volcanic lava. Perlite is an abundant mineral occurring in many parts of the world and its price is extremely low (typically, FOB $40/ton). Perlite has the property when heated to a suitable point in its softening range, to expand from four to twenty times its original volume producing a porous matrix (expanded Perlite) material. This expansion is due to the presence of two to six percent combined water (foaming agent) in the crude Perlite rock. When quickly heated to above (870°C), the crude rock pops in a manner similar to popcorn as the combined water vaporizes and creates countless tiny bubbles (pores) which account for the amazing light weight and other exceptional physical properties of expanded Perlite. Since Perlite is a form of natural glass, it is classified as chemically inert and has a pH of approximately 7. 3.1.2 Raw materials for magnetic material component The raw materials for the magnetic material component are iron (Fe) metal and/or iron alloys (containing at least 50 wt% Fe), Iron(ll) Oxides (FeO x , x is about 1), Iron(lll) Oxides (γ-Fβ2θ3 maghemite, α-Fe2θ3 hematite), Iron Hydroxides (Fe(OH)2 or Fe(OH)3), Fβ3θ4 magnetite, Ferrites (such as Sr-ferrite and Ba- ferrite), other Iron, Cobalt and Nickel-based metallic alloys (such as RE-Fe(Co.Ni)- B(C), RE-Co(Fe,Ni) alloys, where, RE=La, Ce, Pr, Nd, Sm, Y, Dy, Tb, Gd, Eu, Yb, Ho). From the final cost point of view, Fe, γ-Fβ2θ3 maghemite, Fβ3θ4 magnetite, Sr-ferrite, Ba-ferrite, other ferrites, and/or mixtures of them are the most suitable. Magnetic metal alloys containing RE metals may be used only in special occasions where cost is not an important issue. Magnetite (Fβ3θ4) and other iron oxides occur as natural minerals and their cost is very low. The price increases when metal iron and ferrites are used. The most suitable magnetic material component is a mixture of ferrites, magnetite and iron particles, depending on the desired final properties of EcoMag, exactly as presented in the previous paragraphs 2.2 and 2.3. Usually, the magnetic material component in EcoMag (final product) is not much different from the original raw magnetic material, which means that the raw magnetic materials remain almost unaffected through the process of EcoMag production. 3.2 Production process of EcoMag There are two processing methods for the production of EcoMag, the "processing and mixing method" and the "pre-mixing and processing method". The "processing and mixing method" is used independent of the nature of the magnetic material used (iron oxides and/or ferrites and/or metallic iron and/or RE-based metallic alloys). The "pre-mixing and processing method" is limited to the cases where the nature of the magnetic material is in the form of iron oxides and/or ferrites and/or metallic iron. The reason is because, RE-based metallic alloys are very sensitive to oxidation during the high temperature processing of EcoMag and their intended good magnetic properties deteriorate loosing their effectiveness. Both methods are very simple and cost effective. The employment of each method depends only on how one plans to use the final product (EcoMag). If EcoMag is going to be produced and applied in situ on the oil spill combating vessel, the "pre-mixing and processing method" is the most suitable because, the pre-mixed and ready for processing material will be already stored on board and the mixing process can be avoided gaining time which is crucial in combating oil spills. Also, It is easier and space saving to store a pre-mixed raw material than EcoMag itself. EcoMag could need a 4 - 40 times more space to store because of its lower density. When the response time is not of a major consideration, for example, in regular EcoMag production, both methods may be used and EcoMag can be stored on the ground for further managing. 3.2.1 Processing and mixing method This production method is based on the separate processing of the raw material to produce the porous matrix component and its subsequent mixing with the desired amount of the magnetic material component with the use of a binder (glue). The processing of the raw material employs the drying of the material to remove the moisture at temperatures between 100 and 800°C, followed by a high temperature treatment at 800 - 1300°C. Usually, and especially when Perlite is used, flash (quick) heating is applied in order to achieve a porous matrix with very low apparent density. Typically, Perlite particles are flash heated on a direct flame (gas or petroleum flame) at 800 to 1300°C in an "expansion reactor", and immediately removed pneumatically and/or by other methods. Usually, the "expansion reactor" is a vertical reactor tube, with Perlite (or other raw material) particles falling by gravity from the top on a regulated flame which is located in the bottom of the tube. Perlite pops and the light product (expanded Perlite) is removed pneumatically from the top of the reactor and stored for further processing. The "expansion reactor" can also be an inclined rotating reactor tube in which Perlite (or other raw material) particles are fed from the top entry and is transferred/guided towards the lower entry where a burner flame expands the Perlite into a light product which is consequently removed pneumatically and stored for further processing. Mixing is done in order to achieve bonding of the magnetic material in the final product (EcoMag). This can be done with the utilization of small quantities of epoxy/acrylic and/or other resins at low temperatures (<100°C), or of polyethylene/polypropylene and/or other polymers at medium temperatures (100 - 300°C), or of inorganic materials such as silicates/borates/phosphates and/or other glassy materials at high temperatures (300 - 1300°C). 3.2.2 Pre-mixing and processing method This production method is based on the pre-mixing of both raw materials (matrix and magnetic raw materials components) at temperatures up to 800°C and the subsequent processing at high temperatures (800 - 1300°C) to directly produce EcoMag. In some cases, depending on the nature of the matrix raw material, a small amount of inorganic binder is added to the mixture in order to promote bonding of the magnetic material in the final product (EcoMag) during the process. The mixture of the raw materials (with/without binder) is processed in a "vertical reactor tube" or in an "inclined rotating reactor tube" as described above in paragraph 3.2.1. 4. Deployment of EcoMag, magnetic separation methods and oil recovery 4.1 Deployment of EcoMag The deployment of EcoMag could take place by spraying EcoMag particles on the oil spill by many ways (vessels, airplanes, helicopters, pneumatic systems, etc) which are presently used to deploy the chemical dispersants and other oil spill combating materials. EcoMag can be deployed from existing EcoMag storages on the ground and/or on vessels. EcoMag could also be produced and pneumatically applied in situ on the oil spill combating vessel itself. 4.2 Magnetic separation methods Magnetic separation of the EcoMag carrying the sorbed oil can be done by a batch magnetic separation method and a continuous magnetic separation method. In both methods, the idea is to magnetically attract the "EcoMag-oil" magnetic mixture by a magnetic system, remove the mixture from the surface of the waters (or of the ground or other solid surface) and store it in a storage container for further oil recovery or use. A combination of both magnetic separation methods could be used to increase the efficiency of oil spill cleaning operation. 4.2.1 Batch magnetic separation method This method is similar to the magnetic methods used employing electromagnets to transfer iron-based scrap metals in the junk yards or in foundries. In the place of an electromagnet one can use a magnetic system made of strong permanent magnets (Nd-Fe-B, Sm-Co, ferrites or AINiCo). The magnetic separation process consists of lowering the magnetic head of the system (with the use of a crane) on the top of the magnetic mixture (EcoMag with sorbed oil), lifting it and store it in a storage container. The procedure is repeated many times until all the mixture is removed. The efficiency of this system depends on the surface area of the magnetic head and the number of systems used. 4.2.2 Continuous magnetic separation method This method is similar to the methods used in enriching iron ores in the mining industry and in magnetic separations of unwanted ferromagnetic materials from wool, tobacco, tea, china clay, liquid coolants, and other solids and liquids. This magnetic separation system is based on a magnetic drum and a conveyor belt as shown in Figure 1. In the case of a waterborne oil spill, EcoMag is applied on the oil spill and floats with the sorbed oil. The magnetic drum, fixed on a vessel, can be lowered partly into the water level, attracts the magnetic mixture which is transferred by the moving conveyor belt on to the vessel and left to fall into a storage container. As the recovery process continues the vessel moves towards the oil spill front in a velocity almost equal to the surface velocity of the conveyor belt. This process can proceed continuously until all the mixture is removed. The efficiency of this system is higher than that of the batch type, and depends largely on the axial length of the magnetic drum and the number of the systems used. 4.3 Oil recovery The oil can be recovered from the "EcoMag-oil" mixture by centrifugation or solvent extraction. The mixture could also be used directly as a fuel (for example in cement factories) producing inorganic ash containing earth constituents. The ash can be used in the cement products or it can be disposed off in the fields.

Claims: CLAIMS 1. The new material (EcoMag) contains a porous matrix materials component (which is essentially non-magnetic) and a magnetic materials component, it is chemically based on inorganic materials (not copolymers or other organic materials), it is simultaneously of a low apparent density, porous, magnetic (it can be attracted by a magnetic field), and oleophilic, and can sorb all kinds of oil (for example, light medium and heavy crude oil, vegetable oils, animal oils, etc) and can be used for oil spill cleaning and oil recovery. 2. The raw materials used to produce the porous matrix (non-magnetic) component of EcoMag, according to claim 1 , are oxides and/or silicates containing, other than oxygen, at least the elements of Silicon, aluminum, Na and K with a chemical composition of Siθ2 = 65 - 80 wt% Al 2 0 3 = 8 - 20 wt% (Na 0+K 2 0) = 5 - 10 wt% with preferable raw material to be the naturally occurring mineral of Perlite with a mean particle size (before processing) of between 1x10 _5 m and 10x10 -3 m and a typical chemical analysis (in wt%) of Siθ2 = 74.75 AI2O3 = 12.90 Na2θ = 3.67 K 2 0 = 3.01 CaO = 1.40 MgO = 0.25 MnO = 0.05 Ti0 2 = 0.10 H 2 0 = 2.81 3. The raw materials for the magnetic materials component of EcoMag, according to claim 1 , are iron (Fe) metal and/or iron alloys (containing at least 50 wt% Fe) and/or iron compounds such as, Iron (II) oxides (such as FeO x , x is about 1) and/or Iron(lll) Oxides (γ-Fβ2θ3 maghemite, α-Fe2θ3 hematite) and/or Iron Hydroxides (Fe(OH)2 or Fe(OH)3) and/or Fβ3θ4 magnetite (Lodestone) and/or hexagonal ferrites (such as Sr-ferrite (typically, Sr0.6Fe2θ3), Ba-ferrite(typically, Ba0.6Fβ2θ3)) and/or other Iron, Cobalt and Nickel-based metallic alloys (such as RE-Fe(Co,Ni)-B(C), RE-Co(Fe,Ni) alloys, where, RE=La, Ce, Pr, Nd, Sm, Y, Dy, Tb, Gd, Eu, Yb, Ho), with the preferable magnetic materials component of EcoMag to be a mixture of Ferrites and/or magnetite and/or metal iron in the form of particles with a mean size of between 5x10 8 m and 1x10" 2 m, preferably between 5x10 _7 m and 2x10 _3 m, a saturation magnetization of the magnetic material component of EcoMag of between 0.6x10 5 emu/kg and 2.2x10 5 emu/kg, exhibiting a ferromagnetic and/or ferrimagnetic behavior at the temperature range of -30°C to 50°C (Magnetic materials which are not ferromagnetic and/or ferrimagnetic in the temperature range of -30°C to 50°C are excluded from this claim. The meaning of ferromagnetic/ferrimagnetic materials is that they exhibit magnetization, in other words they can be attracted by a magnetic field). 4. The wt% concentration of the magnetic materials component, according to claim 1 , is such that EcoMag with the sorbed oil can float ("floating criterion") on the surface of the waters and at the same time EcoMag with the sorbed oil can be attracted ("magnetic separation criterion") by the magnetic separation system in use, and it should be of between 0.1 wt% and 90 wt% for waterborne oil spills and between 0.1 wt% and 99 wt% for oil spills formed on the ground or other solid surfaces. 5. The porous matrix component of EcoMag (as a final product), according to claim 2, resembles (and it is the same, if Perlite is used as a raw material) the "expanded Perlite" with a bulk density (mass of solids per volume of solids) between 2000kg/m 3 and 2500kg/m 3 , typically 2100kg/m 3 , with an apparent density of the porous matrix (excluding the magnetic material component) component of EcoMag, defined as the mass of solids per total volume of solids and voids (pores) comprising the porous matrix, to be between 25kg/m 3 and 400kg/m 3 with a porosity fraction ( — : τ ~ , — ^ — r ~ iϊds ^ °* between 0-8 ar) d 0.99 and a typical chemical analysis of Siθ2 = 76.91 Al 0 3 = 13.27 Na2θ = 3.78 K 2 0 = 3.10 Fe2θ3 = 1.09 CaO = 1.44 MgO = 0.26 MnO = 0.05 Ti0 2 = 0.10 and in the form of particles of mean size of between 0.2x10- 3 m and 20x10 _3 m and/or bonded particles or large blocks of bonded particles in different forms and shapes, for example as EcoMag booms, which can be deployed around waterborne oil spills in order to prevent the spreading of the oil spill and sorbing it at the same time. 6. EcoMag, according to claim 1 , should be able to absorb at least 1 liter of oil per kg of EcoMag, to exhibit an apparent density, defined as the mass of solids per total volume of solids and voids (pores) comprising EcoMag, of between SOkg/m 3 and θδOkg/m 3 , a coercive magnetic field of between 0.00001 Oe and 15000Oe and a saturation magnetization of between 60 emu/kg and 1.5x10 5 emu/kg (in order to be attracted by a magnetic field). 7. EcoMag, according to claim 1 , is oleophilic and sorbs oils (for example, from oil spills) into its pores (because the materials composing EcoMag are themselves oleophilic) and the "EcoMag-oil sorbed" magnetic mixture can be separated (oil spill cleaning) from the waters or ground or other solid surfaces by batch and/or continuous magnetic separation methods, it can be stored and the oil can be recovered (oil recovery) by centrifugation or solvent extraction or used as it is as a fuel in different industries, such as cement industries. 8. The production method of EcoMag involves pre-mixing of the raw materials of both components (matrix and magnetic components) of EcoMag at temperatures up to 800°C and then flash heating the mixture at 800°C to 1300°C in a direct gas or petroleum flame or in an electrically heated furnace in order to directly produce the EcoMag final product. 9. The production method of EcoMag involves flash heating the raw material for the porous matrix component of EcoMag at 800°C to 1300°C in a direct gas or petroleum flame or in an electrically heated furnace and then mixing the porous matrix product with the desirable amount of the magnetic material component of EcoMag at temperatures up to 1300°C, in order to produce the EcoMag final product. 10. For the production of EcoMag, according to claims 8 and 9, a high temperature heating of the raw materials is needed between 800°C and 1300°C, and the EcoMag product can withstand temperatures of as high as 1000 °C, something that excludes the use of polymer organic materials such as those used in CleanMag because they deteriorate (by decomposing or burning) at temperatures as low as 250 °C. AMENDED CLAIMS [received by the International Bureau on 19 November 2001 (19, 11.01); original claims 8-10 amended; remaining claims unchanged (2 pages)] 1. The new material (EcoMag) contains a porous matrix materials component (which is essentially non-magnetic) and a magnetic materials component, it is chemically based on inorganic materials (not copolymers or other organic materials), it is simultaneously of a low apparent density, porous, magnetic (it can be attracted by a magnetic field), and oleophilic, and can sorb all kinds of oil (for example, light medium and heavy crude oil, vegetable oils, animal oils, etc) and can be used for oil spill cleaning and oil recovery. 2. The raw materials used to produce the porous matrix (non-magnetic) component of EcoMag, according to claim 1 , are oxides and/or silicates containing, other than oxygen, at least the elements of Silicon, aluminum, Na and K with a chemical composition of Siθ2 = 65 - 80 wt% AI2O3 = 8 - 20 wt% (Na2θ+K2θ)= 5 - 10 wt% with preferable raw material to be the naturally occurring mineral of Perlite with a mean particle size (before processing) of between 1x10 " ^m and 10x10 ~ 3m and a typical chemical analysis (in wt%) of Si02 = 74.75 AI203 = 12.90 Na2θ = 3.67 K2O = 3.01 Fe2θ3 = 1.06 CaO = 1.40 MgO = 0.25 MnO = 0.05 Tiθ2 = 0.10 H2O = 2.81 3. The raw materials for the magnetic materials component of EcoMag, according to claim 1 , are iron (Fe) metal and/or iron alloys (containing at least 50 wt% Fe) and/or iron compounds such as, Iron (II) oxides (such as FeOχ, x is about 1) and/or Iron(lll) Oxides (γ-Fe2θ3 maghemite, α-Fe2θ3 hematite) and/or Iron Hydroxides (Fe(OH)2 or Fe(OH)3) and/or Fe3θ4 magnetite (Lodestone) and/or hexagonal ferrites (such as Sr-ferrite (typically, Sr0.6Fe2θ3), Ba- ferrite(typically, Ba0.6Fe2θ3)) and/or other Iron, Cobalt and Nickel-based metallic alloys (such as RE-Fe(Co,Ni)-B(C), RE-Co(Fe,Ni) alloys, where, RE=La, Ce, Pr, Nd, Sm, Y, Dy, Tb, Gd, Eu, Yb, Ho), with the preferable magnetic materials component of EcoMag to be a mixture of Ferrites and/or magnetite and/or metal iron in the form of particles with a mean size of between 5x 0 ~8 m and 1x10 -2 m, preferably between 5x10 _7 m and 2x10 ~3 m, a saturation magnetization of the magnetic material component of EcoMag of between 0.6x1 O^emu/kg and 2.2x10 5 emu/kg, exhibiting a ferromagnetic and/or ferrimagnetic behavior at the temperature range of -30°C to 50°C (Magnetic materials which are not ferromagnetic and/or ferromagnetic in the temperature range of -30°C to 50°C are excluded from this claim. The meaning of ferromagnetic/ferrimagnetic materials is that they exhibit magnetization, in other words they can be attracted by a magnetic field). 4. The wt% concentration of the magnetic materials component, according to claim 1 , is such that EcoMag with the sorbed oil can float ("floating criterion") on the surface of the waters and at the same time EcoMag with the sorbed oil can be attracted ("magnetic separation criterion") by the magnetic separation system in use, and it should be of between 0.1 wt% and 90 wt% for waterborne oil spills and between 0.1 wt% and 99 wt% for oil spills formed on the ground or other solid surfaces. 5. The porous matrix component of EcoMag (as a final product), according to claim 2, resembles (and it is the same, if Perlite is used as a raw material) the "expanded Perlite" with a bulk density (mass of solids per volume of solids) between 2000kg/m 3 and 2500kg/m 3 , typically 2100kg/m 3 , with an apparent density of the porous matrix (excluding the magnetic material component) component of EcoMag, defined as the mass of solids per total volume of solids and voids (pores) comprising the porous matrix, to be between 25kg/m 3 and 400kg/m 3 with a porosity fraction (volume of voids/volume of (voids+solids)) of between 0.8 and 0.99 and a typical chemical analysis of Siθ2 = 76.91 AI2O3 = 13.27 Na2θ = 3.78 K2O = 3.10 Fe2θ3 = 1.09 CaO = 1.44 MgO = 0.26 MnO = 0.05 Tiθ2 = 0.10 and in the form of particles of mean size of between 0.2x10 ~3 m and 20x10 _3 m and/or bonded particles or large blocks of bonded particles in different forms and shapes, for example as EcoMag booms, which can be deployed around waterbome oil spills in order to prevent the spreading of the oil spill and sorbing it at the same time. 6. EcoMag, according to claim 1 , should be able to absorb at least 1 liter of oil per kg of EcoMag, to exhibit an apparent density, defined as the mass of solids per total volume of solids and voids (pores) comprising EcoMag, of between 30kg/m 3 and 950kg/m 3 , a coercive magnetic field of between 0.00001 Oe and 15000Oe and a saturation magnetization of between 60 emu/kg and 1.5x10 5 emu/kg (in order to be attracted by a magnetic field). 7. EcoMag, according to claim 1 , is oleophilic and sorbs oils (for example, from oil spills) into its pores (because the materials composing EcoMag are themselves oleophilic) and the "EcoMag-oil sorbed" magnetic mixture can be separated (oil spill cleaning) from the waters or ground or other solid surfaces by batch and/or continuous magnetic separation methods, it can be stored and the oil can be recovered (oil recovery) by centrifugation or solvent extraction or used as it is as a fuel in different industries, such as cement industries. 8. The production method of EcoMag involves pre-mixing (pre-bonding) of the raw materials of both components (matrix and magnetic components) of EcoMag, according to claims 2, 3 and 4, plain or with inorganic binders (for example, silicates/borates/phosphates and/or other glassy materials), using up to 30wt% binders, at temperatures up to 800°C and then flash heating the mixture at 800°C to 1300°C in a direct gas or petroleum flame or in an electrically heated furnace, in order to cause the simultaneous expansion of the raw matrix component (for example, "perlite") and the bonding of the two components, in order to directly produce the EcoMag final product. 9. The production method of EcoMag involves flash heating the raw material in order to produce the porous matrix component (for example, "expanded perlite") of EcoMag, according to claims 2 and 5, at 800°C to 1300°C in a direct gas or petroleum flame or in an electrically heated furnace, then bonding the porous matrix component with the desirable amount of the magnetic material component of EcoMag, according to claims 3 and 4, with the utilization of inorganic binders (for example, silicates/borates/phosphates and/or other glassy materials), using up to 30wt% inorganic binders, at temperatures up to 1300°C, or with the use of organic binders (for example, epoxy resins, polyethylene/polypropylene and/or other polymers preferable in a foamy state), using up to 50wt% organic binders, at temperatures up to 300°C. 10. In the case where organic binders are used, according to claim 9, the inorganic porous matrix component (for example, "expanded perlite") of EcoMag has to be in excess of the one to one (1 :1 ) weight ratio with respect to the organic binder, in order to ensure the low cost of the final product, while retaining its oil-absorbing capacity and its magnetic properties, according to claims 4 and 6.

Inventors: CHRISTODOULOU NEOFYTOU CHRISTO, CHRISTODOULOU, NEOFYTOU, CHRISTODOULOS
Applicants: CHRISTODOULOU NEOFYTOU CHRISTO, CHRISTODOULOU, NEOFYTOU, CHRISTODOULOS
Application year: 2000
Main classification: C09K3
IPC codes: B01D15, B01J20, C09K3