SEMICONDUCTOR STRUCTURES USING A GROUP III-NITRIDE QUATERNARY MATERIAL SYSTEM

Abstract: A group III-nitride quaternary material system and method is disclosed for use in semiconductor structures, including laser diodes, transistors, and photodetectors, which reduces or eliminates phase separation and provides increased emission efficiency and reliability. In an exemplary embodiment the semiconductor structure includes a first GaAINAs layer of a first conduction type formed substantially without phase separation, an GaAINAs active layer substantially without phase separation, and a third GaAINAs layer of an opposite conduction type formed substantially without phase separation.

Description: SEMICONDUCTOR STRUCTURES USING A GROUP III-NITRIDE QUATERNARY MATERIAL SYSTEM SPECIFICATION RELATED APPLICATIONS This application relates to U.S. Patent Application S.N. 09/277,319 filed 3/26/99 in the names of the same inventors and assigned to the same assignee. FIELD OF THE INVENTION This application relates to semiconductor structures and processes, and particularly relates to group Ill-nitride materials systems and methods such as might be used in blue or ultraviolet laser diodes and other similar semiconductors. BACKGROUND OF THE INVENTION The development of the blue laser light source has heralded the next generation of high density optical devices, including disc memories, DVDs, and so on. Figure 1 shows a cross sectional illustration of a prior art semiconductor laser devices. (S. Nakamura, MRS BULLETIN, Vol. 23, No. 5, pp. 37-43, 1998.) On a sapphire substrate 5, a gallium nitride (GaN) buffer layer 10 is formed, followed by an n-type GaN layer 15, and a 0.1 m thick silicon dioxide (SiO 2 ) layer 20 which is patterned to form 4 μm wide stripe windows 25 with a periodicity of 12 μ in the GaN<1-100> direction. Thereafter, an n-type GaN layer 30, an n-type indium gallium nitride (ln 0 1 Ga 0 9 N) layer 35, an n-type aluminum gallium nitride (AI 0 14 Ga 086 N)/GaN MD-SLS (Modulation Doped Strained-Layer Superlattices) cladding layer 40, and an n-type GaN cladding layer 45 are formed. Next, an ln 002 Ga 098 N/ln 0 15 Ga 085 N MQW (Multiple Quantum Well) active layer 50 is formed followed by a p-type AI 0 2 Ga 0 8 N cladding layer 55, a p-type GaN cladding layer 60, a p-type Al αι 4 Ga 0 86 N/GaN MD- SLS cladding layer 65, and a p-type GaN cladding layer 70. A ridge stripe structure is formed in the p-type AI 4 Ga 0 86 N/GaN MD-SLS cladding layer 55 to confine the optical field which propagates in the ridge waveguide structure in the lateral direction. Electrodes are formed on the p-type GaN cladding layer 70 and n-type GaN cladding layer 30 to provide current injection. In the structure shown in Figure 1 , the n-type GaN cladding layer 45 and the p-type GaN 60 cladding layer are light-guiding layers. The n-type Al 0 , 4 Ga 0 86 N/GaN MD-SLS cladding layer 40 and the p-type Al 0 1 4 Ga 0 86 N/GaN MD-SLS cladding layer 65 act as cladding layers for confinement of the carriers and the light emitted from the active region of the InGaN MQW layer 50. The n-type ln ι Ga g N layer 35 serves as a buffer layer for the thick AIGaN film growth to prevent cracking. By using the structure shown in Figure 1 , carriers are injected into the InGaN MQW active layer 50 through the electrodes, leading to emission of light in the wavelength region of 400 nm. The optical field is confined in the active layer in the lateral direction due to the ridge waveguide structure formed in the p-type AI 0 14 Ga 0 86 N/GaN MD-SLS cladding layer 65 because the effective refractive index underthe ridge stripe region is largerthan that outside the ridge stripe region. On the other hand, the optical field is confined in the active layer in the transverse direction by the n-type GaN cladding layer 45, the n-type Al 0 14 Ga 0 86 N/GaN MD-SLS cladding layers 40, the p-type GaN cladding layer 60, and the p-type AI 0 1 ,Ga 0 86 N/GaN MD- SLS cladding layer 55 because the refractive index of the of the active layer is larger than that of the n-type GaN cladding layer 45 and the p-type GaN cladding layer 60, the n-type Al 0 14 Ga 086 N/GaN MD-SLS layer 40, and the p-type Al 0 14 Ga 0 86 N/GaN MD- SLS cladding layer 60. Therefore, fundamental transverse mode operation is obtained. However, for the structure shown in Figure 1 , it is difficult to reduce the defect density to the order of less than 10 8 cm 2 , because the lattice constants of AIGaN, InGaN, and GaN are sufficiently different from each other that defects are generated in the structure as a way to release the strain energy whenever the total thickness of the n-type ln 0 1 Ga 09 N layer 35, the ln 002 Ga 0 98 N/ln 0 15 Ga 085 N MQW active layer 50, the n-type Al 0 14 Ga 086 N/GaN MD-SLS cladding layer 40, the p-type Al 0 14 Ga 086 N/GaN MD-SLS cladding layer 65, and the p-type Al 0 2 Ga 0 8 N cladding layer 55 exceeds the critical thickness The defects result from phase separation and act as absorption centers for the lasmg light, causing decreased light emission efficiency and increased threshold current The result is that the operating current becomes large, which in turn causes reliability to suffer Moreover, the ternary alloy system of InGaN is used as an active layer in the structure shown in Figure 1 In this case, the band gap energy changes from 1 9 eV for lnN to 3 5 eV for GaN Therefore, ultraviolet light which has an energy level higher than 3 5 eV cannot be obtained by using an InGaN active layer This presents difficulties, since ultraviolet light is attractive as a light source for the optical pick up device in, for example, higher density optical disc memory systems and other devices To better understand the defects which result from phase separation in conventional ternary materials systems, the mismatch of lattice constants between InN, GaN, and AIN must be understood The lattice mismatch between InN and GaN, between InN and AIN, and between GaN and AIN, are 1 1 3%, 13 9%, and 2.3%, respectively Therefore, an internal strain energy accumulates in an InGaAIN layer, even if the equivalent lattice constant is the same as that of the substrate due to the fact that equivalent bond lengths are different from each other between InN, GaN, and AIN In order to reduce the internal strain energy, there is a compositional range which phase separates in the InGaAIN lattice mismatched material system, where In atoms, Ga atoms, and Al atoms are inhomogeneously distributed in the layer The result of phase separation is that In atoms, Ga atoms, and Al atoms in the InGaAIN layers are not distributed uniformly according to the atomic mole fraction in each constituent layer In turn, this means the band gap energy distribution of any layerwhich includes phase separation also becomes inhomogeneous The band gap region of the phase separated portion acts disproportionately as an optical absorption center or causes optical scattering for the waveguided light. As noted above, a typical prior art solution to these problems has been to increase drive current, thus reducing the life of the semiconductor device. As a result, there has been a long felt need for a semiconductor structure which minimizes lattice defects due to phase separation and can be used, for example, as a laser diode which emits blue or UV light at high efficiency, and for other semiconductor structures such as transistors. SUMMARY OF THE INVENTION The present invention substantially overcomes the limitations of the prior art by providing a semiconductor structure which substantially reduces defect densities by materially reducing phase separation between the layers of the structure. This in turn permits substantially improved emission efficiency. To reduce phase separation, it has been found possible to provide a semiconductor device with GaAINAs layers having homogeneous Al content distribution as well as homogeneous As content distribution in each layer. In a light emitting device, this permits optical absorption loss and waveguide scattering loss to be reduced, resulting in a high efficiency light emitting device. By carefully selecting the amounts of Al and As, devices with at least two general ranges of band gaps may be produced, allowing development of light emitting devices in both the infrared and the blue/uv ranges. In a first exemplary embodiment of a GaAINAs quaternary material system in accordance with the present invention, sufficient homogeneity to avoid phase separation has been found when the Al content, represented by x, and the As content, represented by y, ideally satisfy the condition that 3.18(1 -x)(1 -y)+3.99(1 - x)y+3.1 1 x(1-y)+4xy nearly equals to a constant value. In a typical embodimentof a light emitting device, the constant value may be 3.18. The lack of phase separation results because the lattice constants of the constituent layers in the structure are sufficiently close to each, in most cases being nearly equal, that the generation of defects is suppressed. A device according to the present invention typically includes a first layer of GaAINAs material of a first conductivity, an GaAINAs active layer, and a layer of GaAINAs material of an opposite conductivity successively formed on one another. By maintaining the mole fractions essentially in accordance with the formula 3.18(1 - x)(1 -y)+3.99(1 -x)y+3.1 1 x(1 -y)+4xy nearly equals to a constant value, for example on the order of or nearly equal to 3.18, the lattice constants of the constituent layers remain substantially equal to each other, leading to decreased generation of defects. In an alternative embodiment, the semiconductor structure is fabricated essentially as above, using a quaternary materials system to eliminate phase separation and promote homogeneity across the layer boundaries. Thus, as before, the first cladding layer is a first conduction type and composition of GaAINAs, the active layer is GaAINAs of a second composition, and the second cladding layer is an opposite conduction type of GaAINAs having the composition of the first layer. However, in addition, the second cladding layer has a ridge structure. As before, the optical absorption loss and waveguide scattering loss is reduced, leading to higher efficiencies, with added benefit that the optical field is able to be confined in the lateral direction in the active layer under the ridge structure. This structure also permits fundamental transverse mode operation. In a third embodiment of the invention, suited particularly to implementation as a laser diode, the semiconductor structure comprises a first cladding of a first conduction type of an Ga^AI^N^AS y ., material, an active layer of an Ga^AI^N.,. y2 As y2 material, and a second cladding layer of an opposite conduction type of an Ga^Al^N^AS yj material, each successively formed on the prior layer. In such a materials system, x1 , x2, and x3 define the Al content and y1 , y2, and y3 define the As content. Moreover, x1 , y1 , x2, y2, x3, and y3 have a relationship of 0 < x1 <1 , 0 < x2 <1 , 0 < x3 <1 , 0 < y1 <1 , 0 < y2 <1 , 0 < y3 <1 , 0.26x1 + 37y1 <= 1 , 0.26x2 + 37y2 <= 1 , 0.26x3 + 37y3 <= 1 , Eg GaN (1 -x1 )(1 -y1 )+Eg GaAs (1-x1 )y1 +Eg AIN x1 (1 - y1 )+Eg AIAs x1 y1 > Eg GaN (1 -x2)(1 -y2)+Eg GaAs (1 -x2)y2+Eg AIN x2(1 -y2)+Eg AIAs x2y2, and Eg GaN (1 -x3)(1 -y3)+Eg GaAs (1 -x3)y3+Eg AIN x3(1 -y3)+Eg AlAs x3y3 > Eg GaN (1 -x2)(1 - y2)+Eg GaAs (1-x2)y2+Eg AIN x2(1 -y2)+Eg AIAs x2y2, where Eg GaN , Eg GaAs , Eg AlN , and Eg AIAs are the band gap energy of GaN, GaAs, AIN, and AIAs, respectively. To provide a reproducible semiconductor structure according to the above materials system, an exemplary embodiment of GaAINAs layers have Al content, x, and As content, y, which satisfy the relationship 0 < x <1 , 0< y <1 and 0.26x + 37y <=1 . As before, this materials system permits reduction of the optical absorption loss and the waveguide scattering loss, resulting in a high efficiency light emitting device. Moreover, the band gap energy of the GaAINAs of an active layer becomes smaller than that of the first cladding layer and the second cladding layer when x1 , y1 , x2, y2, x3, and y3 have a relationship of 0 < x1 <1 , 0 < x2 <1 , 0 < x3 <1 , 0 < y1 <1 , 0 < y2 <1 , 0 < y3 <1 , 0.26x1 + 37y1 <= 1 , 0.26x2 + 37y2 <= 1 , 0.26x3 + 37y3 <= 1 , Eg GaN (1 -x1 )(1 -y 1 ) + Eg GaAs (1 -x1 )y 1 +Eg AIN x1 ( 1 -y 1 )+Eg AlAs x1 y 1 > Eg GaN (1 -x2)(1 - y 2)+Eg GaAs (1 -x2)y2+Eg AlN x2(1-y2)+Eg AIAs x2y2, and Eg GaN (1-x3)(1-y3)+Eg GaAs (1- x3)y3+Eg AIN x3(1-y3)+Eg AIAs x3y3 > Eg GaN (1-x2)(1-y2)+Eg GaAs (1-x2)y2+Eg AIN x2(1- y2)+Eg A(As x2y2. Under these conditions, the injected carriers are confined in the active layer. In at least some embodiments, it is preferable that the third light emitting device has a GaAINAs single or multiple quantum well active layer whose Al content, xw, and As content, yw, of all the constituent layers satisfy the relationship of 0 < xw <1 , 0< yw <1 , and 0.26xw + 37yw <= 1 . One of the benefits of the foregoing structure is to reduce the threshold current density of a laser diode. This can be achieved by use of a single or multiple quantum well structure, which reduces the density of the states of the active layer. This causes the carrier density necessary for population inversion to become smaller, leading to a reduced or low threshold current density laser diode. It is preferred that in the third light emitting device, the condition of 3.18(1- xs)(1 -ys)+3.99(1 -xs)ys+3.1 1 xs(1 -ys)+4xsys nearly equals to a constant value -- on the order of or near 3.18 - is satisfied, wherein xs and ys are the Al content and the As content, respectively, in each the constituent layers. As before, this causes the lattice constants of the each constituent layers to be nearly equal to each other, which in turn substantially minimizes defects due to phase separation. In a fourth embodiment of the present invention, the semiconductor structure may comprise a first cladding layer of a first conduction type of a material Ga^ ^AI^N^AS yL an Ga^^AI^N^^As^ active layer, and a second cladding layer of an opposite conduction type of a material Ga 1 . x3 AI X3 N 1 . y3 As y3 , each successively formed one upon the prior layer. In addition, the second cladding layer has a ridge structure. For the foregoing materials system, x1 , x2, and x3 define the Al content, y1 , y2, and y3 define the As content, and x1 , y1 , x2, y2, x3, and y3 have a relationship of 0 < x1 <1 , 0 < x2 <1 , 0 < x3 <1 , 0 < y1 <1 , 0 < y2 <1 , 0 < y3 <1 , 0.26x1 + 37y1 <= 1 , 0.26x2 + 37y2 <= 1 , 0.26x3 + 37y3 <= 1 , Eg GaN (1 -x1 )(1 -y1 )+Eg GaAs (1 -x1 )y1 +Eg AIN x1 (1- y1 )+Eg AIAs x1 y1 > Eg GaN (1 -x2)(1 -y2)+Eg GaAs (1 -x2)y2+Eg AIN x2(1 -y2)+Eg AIAs x2y2, and Eg GaN (1 -x3)(1 -y3)+Eg GaAs (1 -x3)y3+Eg A , N x3(1 -y3)+Eg AIAs x3y3 > Eg GaN (1 -x2)(1 - y2)+Eg GaAs (1 -x2)y2+Eg AIN x2(1 -y2)+Eg AIAs x2y2, where Eg GaN , Eg GaAs , Eg A!N , and Eg AIAs are the band gap energy of GaN, GaAs, AIN, and AIAs, respectively. As with the prior embodiments, each of the GaAINAs layers have- a homogeneous Al and As content distribution, which can be obtained reproducibly when Al content, x, and As content, y, of each GaAINAs layer satisfies the relationship 0 < x <1 , 0< y <1 and 0.26x + 37y <=1 . The band gap energy of the GaAINAs active layer becomes smaller than that of the first cladding layer and the second cladding layer when x1 , y1 , x2, y2, x3, and y3 have a relationship of x1 , y1 , x2, y2, x3, and y3 have a relationship of 0 < x1 <1 , 0 < x2 <1 , 0 < x3 <1 , 0 < y1 <1 , 0 < y2 <1 , 0 < y3 <1 , 0.26x1 + 37y1 <= 1 , 0.26x2 + 37y2 <= 1 , 0.26x3 + 37y3 <= 1 , Eg GaN (1 -x1 )(1 -y1 ) + Eg GaAs (1 -x1 )y1 +Eg AIN x1 (1 -y1 )+Eg AIAs x1 y 1 > Eg GaN (1 -x2)(1 - y2)+Eg GaAs (1 -x2)y2+Eg AIN x2(1-y2)+Eg AlAs x2y2, and Eg GaN (1 -x3)(1-y3)+Eg GaAs (1 - x3)y3+Eg AIN x3(1 -y3)+Eg A , As x3y3 > Eg GaN (1-x2)(1-y2)+Eg GaAs (1-x2)y2+Eg AlN x2(1- y2)+Eg A , As x2y2. Similar to the prior embodiments, the injected carriers are confined in the active layer and the optical field is confined in the lateral direction in the active layer under the ridge structure, producing a fundamental transverse mode operation. Also similar to the prior embodiments, the fourth embodiment typically includes an GaAINAs single or multiple quantum well active layer whose Al content, xw, and As content, yw, of all the constituent layers satisfy the relationship of 0 < xw <1 , 0< yw <1 , and 0.26xw + 37yw <= 1. Also, the condition 3.18(1 -xs)(1 -ys)+3.99(1- xs)ys+3.1 1 xs(1 -ys)+4xsys nearly equals to a constant value, for example on the order of or near 3.18 is typically satisfied, where xs and ys are the Al content and the As content, respectively, in each constituent layer. Similar parameters apply for other substrates, such as sapphire, silicon carbide, and so on. The foregoing results may be achieved with conventional processing temperatures and times, typically in the range of 500°C to 1000°C. See "Growth of high optical and electrical, quality GaN layers using low-pressure metalorganic chemical vapor deposition," Appl. Phys. Lett. 58 (5), 4 February 1991 p. 526 et seq. The present invention may be better appreciated by the following Detailed Description of the Invention, taken together with the attached Figures. FIGURES Figure 1 shows a prior art laser diode structure using a conventional ternary materials system Figure 2 shows in cross-sectional view a semiconductor structure according to a first embodiment of the invention Figure 3 shows a graph of the light-current characteristics of a laser diode according to the structure of Figure 1 Figure 4 shows an exemplary series of the fabrication steps for a semiconductor structure in accordance with a first embodiment of the invention. Figure 5 shows in cross-sectional view a semiconductor structure according to a second embodiment. Figure 6 shows a graph of the light-current characteristics of a laser diode according to the structure of Figure 4. Figure 7 shows an exemplary series of the fabrication steps for a semiconductor structure in accordance with the first embodiment of the invention. Figure 8 is a cross-sectional illustration of a semiconductor laser diode of the third embodiment. Figure 9 shows the light-current characteristics of the laser diode of the third embodiment. Figure 10 shows a series of the fabrication steps of a semiconductor laser diode in one experiment example of the third embodiment. Figure 1 1 is a cross-sectional illustration of a semiconductor laser diode of the fourth embodiment Figure 12 shows the light-current characteristics of the laser diode of the fourth embodiment. Figure 13 shows a series of the fabrication steps of a semiconductor laser diode in one experiment example of the fourth embodiment Figure 14 shows in plot form the boundary between the phase separation region and the region without phase separation at various growth temperatures Figure 15 shows the content choice region of Ga content and Al content in InGaAIN to avoid phase separation at a growth temperature below approximately 1000 °C. Figure 16 shows the content choice line of Ga content and Al content in InGaAIN to avoid phase separation at a growth temperature below approximately 1000 °C which, at the same time, creates a lattice constant of InGaAIN substantially equivalent to that of GaN Figures 17A and 17B show representations of bipolar and FET transistors constructed in accordance with the materials system of the present invention Figure 18 shows an implementation of the presention invention as a phototransistor Figure 19 shows an implementation of the present invention as a photodiode DETAILED DESCRIPTION OF THE INVENTION Referring first to Figure 2, shown therein in cross-sectional view is a semiconductor structure according to a first embodiment of the invention. For purposes of illustration, the semicoductor structure shown in many of the Figures will be a laser diode, although the present invention has appliction to a number of device types. With particular reference to Figure 1 , an n-type GaN substrate 100 is provided and an n-type GaN first cladding layer 105 (typically 0.5μm thick) is formed thereon. Thereafter, a second cladding layer 110, typically of an n-type Ga 075 AI 025 N 0979 As 0021 material which may be on the order of 1.5 μm thick, is formed thereon, followed by a multiple quantum well active layer 1 15 which in an exemplary arrangement may comprise three quantum well layers of Ga 095 AI 005 N 0 996 As 0004 material on the order of 35A thick together with four barrier layers of /Ga 085 AI 0 15 N 0987 As 0013 material on the order of 35A thick, arranged as three pairs. Next, a third cladding layer 120 of a p-type Ga 0 75 AI 0 25 N 0 979 As 0 021 (typically on the order of 1 .5 μm thick) is formed, followed by a p-type GaN fifth cladding layer 125 (on the order of 0.5μm thick). A SiO 2 layer 130 having one stripe like window region 135 (3.0μm width) is formed on the p-type GaN fourth cladding layer 125. A first electrode 140 is formed on the n-type GaN substrate 100, while a second electrode 145 is formed on the SiO 2 layer 130 and the window region 135. In order to emit ultra violet light with a wavelength range of 360 nm from the active layer 1 15, the Al content, x, and the As content, y, of all the layers generally satisfies the condition 3.18(1 -x)(1 -y)+3.99(1-x)y+3.1 1 x(1 -y)+4xy nearly equals to a constant value, which may be on the order of 3.18 for at least the first embodiment. To avoid defects due to phase separation, the lattice constants of the various constituent layers are matched to each other by setting the Al content, x, and the As content, y, in each of the layers to meet the condition 3.18(1 -x)(1-y)+3.99(1- x)y+3.1 1 x(1 -y)+4xy nearly equals to a constant value, again, for the first embodiment on the order of 3.18+0.05 so that the equivalent lattice constants of each layers become nearly equal to the lattice constant of GaN. By proper selection of materials, the band gap energy of the n-type second cladding layer 1 10 and the p-type third cladding layer 120 are larger than that of the 3 pairs of multiple quantum well active layers 1 15. This confines the injected carriers from the n-type second cladding layer 1 10 and p-type third cladding layer 120 within the active layer 1 15, where the carriers recombine to lead to the emission of ultraviolet light. In addition, the refractive index of the n-type second cladding layer 1 10 and the p-type third cladding layer 120 are smaller than that of the multiple quantum well active layer 1 15, which confines the optical field in the transverse direction. Because the injected current from the electrode 145 is confined to flow through the window region 135, the region in the active layer 1 15 under the widow region 135 is activated strongly. This causes the local modal gain in the active layer under the window region 6a to be higher than the local modal gain in the active layer under the SiO 2 layer. Therefore, a gain guided waveguide mechanism, leading to a lasing oscillation, is able to be formed in the structure of the first embodiment. Figure 3 shows a plot of the emitted light versus drive current for a laser diode constructed in accordance with the first embodiment. The laser diode is driven with a pulsed current with a duty cycle of 1 %. The threshold current density is found to be 6.0 kA/cm 2 . Figures 4A-4D show, in sequence, a summary of the fabrication steps necessary to construct an exemplary laser diode according to the first embodiment. Since the structure which results from Figures 4A-4D will resemble that shown in Figure 2, like reference numerals will be used for elements whenever possible. With reference first to Figure 4A, an n-type GaN substrate 100 is provided, on which is grown an n-type GaN first cladding layer 105. The first cladding layer 105 is typically on the order of 0.5μm thick. Thereafter, an n-type Ga 0 75 AI 0 25 N 0 979 As 0 021 second cladding layer 1 10 is formed, typically on the order of 1 .5 μm thick. Next, a multiple quantum well active layer 1 15 is formed by creating three quantum wells comprised of three layers of Ga 095 Al 0 05 N 0 996 As 0 004 material each on the order of 35A thick, together with four barrier layers of Ga 0 85 Al 0 15 N 0 987 As 0 013 material on the order of 35A thick. A third cladding layer 120 of p-type Ga 0 75 AI 0 25 N 0 979 As 0021 material, on the order of 1 .5 urn thick, is then formed, after which is formed a fourth cladding layer 125 of a p-type GaN on the order of 0.5μm thick. Each of the layers is typically formed by either the Metal Organic Chemical Vapor Deposition (MOCVD) method or the Molecular Beam Epitaxy (MBE) method. Then, as shown in Figure 4B, a silicon dioxide (SiO 2 ) layer 130 is formed on the p-type GaN fourth cladding layer 125, for example by the Chemical Vapor Deposition (CVD) method. Using photolithography and etching or any other suitable method, a window region 135 is formed as shown in Figure 4C. The window region 135 may be stripe-like in at least some embodiments. Finally, as shown in Figure 4D, a first electrode 140 and a second electrode 145 are formed on the n-type GaN substrate 100 and on the SiO 2 layer 130, respectively, by evaporation or any other suitable process. Referring next to Figure 5, a second embodiment of a semiconductor structure in accordance with the present invention may be better appreciated. As with the first embodiment, an exemplary application of the second embodiment is the creation of a laser diode. The structure of the second embodiment permits a waveguide mechanism to be built into the structure with a real refractive index guide. This provides a low threshold current laser diode which can operate with a fundamental transverse mode. Continuing with reference to Figure 5, for ease of reference, like elements will be indicated with like reference numerals. On an n-type GaN substrate 100, a first cladding layer 105 is formed of an n-type GaN on the order of 0.5μm thick. Successively, an n-type second cladding layer 1 10 is formed of Ga 0 75 AI 0 25 N 0 979 As 0021 material on the order of 1.5 μm thick. Thereafter, a multiple quantum well active layer 1 15 is formed comprising three well layers of Ga 095 AI 005 N 0996 As 0004 material on the order of 35A thick together with four barrier layers of Ga 0 85 AI 0 15 N 0 987 As 0 013 material, also on the order of 35A thick. Next, a third, p-type cladding layer 120 formed of Ga 0 75 AI 0 25 N 0 979 As 0 021 material on the order of 1 .5 μm thick is formed. Thereafter, a p-type GaN fourth cladding layer 125 on the order of 0.5μm thick is formed over the ridge structure 500 of the third cladding layer 120. The third and fourth cladding layers are then partially removed to create a ridge structure 500. A silicon dioxide (SiO 2 ) layer 130 is then formed over the fourth cladding layer 125 as well as the remaining exposed portion of the third cladding layer 120. A window region 135, which may be stripe-like on the order of 2.0μm width, is formed through the Si0 2 layer above the fourth and third cladding layers 125 and 120, respectively. As with the first embodiment, a first electrode 140 is formed on the n-type GaN substrate 100 and a second electrode 145 is formed on the SiO 2 layer 130 and the window region 135. As with the first embodiment, in order to emit violet light with a wavelength in the range of 350 nm from the active layer 14, the Al content, x, and the As content, y, of the well layer is set to be 0.05, 0.004, respectively. Likewise, in order to match the lattice constants of each of the constituent layers to avoid defects due to strain, the Al content, x, and the As content, y, of all the layers satisfies the condition 3.18(1- x)(1 -y)+3.99(1 -x)y+3.1 1 x(1 -y)+4xy nearly equals to a constant value, which may for example be 3.18+0.05. Likewise, the band gap energy of the cladding layers is maintained larger than the band gap energy for the active layer, allowing the emission of violet light. Similarly the refractive index of the materials is as discussed in connection with the first embodiment, permitting the optical field to be confined in the transverse direction. Similar to the operation of the first embodiment, the region of the active layer 1 15 under the window region 135 is activated strongly because of the constraints on the injected current by the SiO 2 layer The result, again, is that the local modal gain in the active layer under the window region 135 is higher than the local modal gain in the active layer underthe SiO 2 layer 130. This, combined with the relatively higher effective refractive index in the transverse direction inside the ridge stripe region compared to that outside the ridge stripe region, provides an effective refractive 5 index step (Δn). This results in a structure which has, built in, a waveguide mechanism of a real refractive index guide. Therefore, the design of the second embodiment provides a low threshold current laser diode which can operate with a fundamental transverse mode. Figure 6 shows in graph form the emitted light versus drive current 10 characteristics of a laser diode in accordance with the second embodiment. The laser diode is driven with a cw current. The threshold current is found to be 38.5 mA. Referring next to Figures 7A-7E, a summary of the key fabrication steps is shown for an exemplary device of a semiconductor laser diode in accordance with the second embodiment. 15 Referring first to Figure 7A and 7B, the formation of the first and second cladding layers 105 and 1 10 on an n-type GaN substrate 100, together with the three-pair multiple quantum well active layer 1 15 are the same as for the first embodiment. Thereafter, the third and fourth cladding layers 120 and 125 are formed and then partially removed - typically by etching - to create a ridge structure 20 500. As before, in an exemplary embodiment the various layers are formed successively by either the MOCVD or the MBE method. Then, as shown in Figure 7C-7E, a silicon dioxide layer 130 is formed overthe fifth and third cladding layers 125 and 120, respectively, typically by the CVD method, after which a window region 135 is formed as with the first embodiment. 25 Electrodes 140 and 145 are then evaporated or otherwise bonded to the structure. Referring next to Figure 8, a third embodiment of the present invention may be better appreciated. The third embodiment provides slightly different mole fractions to permit the emission of ultra violet light, but is otherwise similar to the first embodiment. Thus, an n-type GaN substrate 100 continues to be used, together 30 with an n-type GaN first cladding layer 105. However, the second cladding layer 810 is typically of n-type Ga 0 58 AI 0 42 N 0 983 As 0 017 material on the order of 1 .5 μm thick, while the three-pair quantum well active layer 815 typically includes three barrier layers of Ga 0 78 AI 0 22 N 0 999 As 0 001 material together with four barrier layers of Ga 0 73 AI 0 27 N 0 995 As 0 005 material. The third cladding layer 820 is typically a p-type 35 Ga 0 58 AI 042 N 0 983 As 0017 material, while the fourth cladding layer 125 is, like the first embodiment, a p-type GaN material. The thicknesses of each layer are substantially the same as for the first embodiment. A Si0 2 layer 130, window region 135, and first and second electrodes 140 and 145 complete the structure. In order to emit blue light in a wavelength range of 410 nm from the active layer 815, the Al content and the As content within the well layer 815 is set to be 0.22 and 0.001 , respectively. In order to match the lattice constants of the constituent layers to avoid generation of strain-induced defects, the Al content, x, and the As content, y, of each of the layers is set to satisfy the condition 3.18(1 -x)(1-y)+3.99(1- x)y+3.1 1 x(1 -y)+4xy nearly equals to a constant value. For exemplary purposes of the third embodiment, the constant value may be on the order of 3.17+0.05. Although the third embodiment emits blue light whereas the first embodiment emits ultraviolet light, the band gap energies of cladding layers continue to be set higher than the band gap energy of the three pairs of the multiple quantum well active layer 815. As before, that permits carrier confinement and recombination in the active layer 815. Also as with the first embodiment, the refractive index of the second and third cladding layers is, by design, smaller than that of the active layer, causing the optical field to be confined in the transverse direction. Likewise, the strong current injection under the window region 135 yields comparatively higher local modal gain in the active layer relative to the portion of the active layer underthe SiO 2 layer 130, again resulting in a guided waveguide mechanism which leads to a lasing oscillation. Figure 9 shows a plot of the emitted light versus drive current characteristics of the laser diode in accordance with the third embodiment. The laser diode is driven with a pulsed current with a duty cycle of 1 %. The threshold current density is found to be 5.7 kA/cm 2 . Figures 10A-10D show a series of the fabrication steps of a semiconductor laser diode in one example of the third embodiment. It will be appreciated that the fabrication steps are the same as those described in connection with Figures 4A-4D, and therefore are not further described. Referring next to Figure 1 1 , a fourth embodiment of the present invention may be better appreciated. The fourth embodiment, like the third embodiment, is designed to emit blue light and therefore has the same Al and As content as the third embodiment. However, like the second embodiment, the fourth embodiment is configured to provide a ridge structure to serve as a waveguide. Because the Al and As content is similar to that of Figure 8, similar elements will be described with the reference numerals used in Figure 8. Continuing to refer to Figure 1 1 , the structure of the fourth embodiment can be seen to have a GaN substrate 00 on which is a formed a first cladding layer 105 followed by a second cladding layer 810. A three-pair multiple quantum well active layer 815 is formed thereabove, followed by a third cladding layer 820. A fourth cladding layer 125, silicon dioxide layer 130, windows 135 and electrodes 140 and 145 are all formed as before. The materials, including the Al content and As content, remain as shown for Figure 8, or 0.22 and 0.001 , respectively. Likewise the Al content, x, and the As content, y, of the layers is set to satisfy the condition 3.18(1- x)(1 -y)+3.99(1 -x)y+3.1 1 x(1 -y)+4xy nearly equals to a constant value on the order of 3.17, as with the third embodiment. The band gap energy, refractive index and modal gain for current injection are all substantially as discussed in connection with the third embodiment and are not further discussed. Figure 12 plots drive current versus emitted light of a laser diode constructed in accordance with the fourth embodiment. The laser diode is driven with a cw current. The threshold current is found to be 33.0 mA. Figure 13 shows a summary of the fabrication steps of a semiconductor laser diode in accordance with the fourth embodiment. The steps are essentially identical to those discussed in connection with Figures 7A-7E and are not further discussed. Referring next to Figure 14, the selection of the Al content, x, and the As content, y, and the relationship therebetween forthe constituent GaAINAs layers may be better understood. In particular, the relative Al and As contents are required to satisfy, approximately, the relationship 0 < x <1 , 0 < y <1 , 0.26x + 37y <= 1. In GaAINAs material system, the lattice constant of GaN, AIN, GaAs and AIAs are different from each other. For example, the lattice mismatch between GaN and GaAs, between AIN and AIAs, and between GaN and AIN, are 25.4%, 28.6%, and 2.3%, respectively. Therefore, an internal strain energy is accumulated in GaAINAs layer, even if the equivalent lattice constant is the same as that of the substrate due to the fact that equivalent bond length are different from each other between GaN, AIN, GaAs and AIAs. Figure 14 shows the boundary of phase separation region plotted against various growth temperatures. The lines in Figure 14 show the boundary between the compositionally unstable (phase separation) region and stable region with respect to various temperatures. In those cases where phase separation occurs, Ga atoms, Al atoms, N atoms, and As atoms in the GaAINAs layers are not distributed uniformly according to the atomic content in each constituent layer. Stated differently, the band gap energy distribution of the phase separated layer also becomes inhomogeneous in the layer. The region of the relatively small band gap region in the phase separated layer acts as an optical absorption center, or causes optical scattering for the waveguided light. This means that the phase separation phenomena should be avoided to obtain a high efficiency light emitting device. . Referring still to Figure 14, it can be seen that the phase separation region varies with temperature. The lines in Fig. 14 show the boundary between the compositionally unstable region - that is, resulting in phase separation - and the stable region with respect to various temperatures. The region surrounded with the GaAs-GaN line, AIAs-AIN line and the boundary line shows the phase separation content region. It has been discovered that the ternary alloys AINAs and GaNAs have a large phase separation region due to the large lattice mismatch between AIN and AIAs, and between GaN and GaAs. On the other hand, it has been found that the ternary alloys GaAIN and GaAIAs have no phase separation region at crystal growth temperatures around 1000 °C, due to the small lattice mismatch between AIN and GaN, and between AIAs and GaAs. It has therefore been discovered that an GaAINAs material system can be provided in which the usual crystal growth temperature is in the approximate range of around 600 °C to around 1000 °C. Likewise, it has been discovered that phase separation of the Al content and As content of GaAINAs does not occur in significant amounts at processing temperatures between on the order of 600 °C and on the order of 1000 °C. Finally, by combining the two, the content choice region of Al content and As content in GaAINAs to avoid phase separation at a crystal growth temperature below around 1000 °C is found to be the shadow region in Figure 15, with the line separating the two regions being approximately defined by the relationship 0.26x + 37y = 1. Therefore, for each of the four structural embodiments disclosed hereinabove, the phase separation phenomena can be avoided in an InGaAIN material system by operating at a crystal growth temperature between on the order of 600 °C and around 1000 °C, when the Ga mole fraction, x, and the AIN mole fraction, y, of the all constituent layers of the laser diodes are made to satisfy approximately the relationship of 0 < x <1 , 0 < y <1 , 0.26x + 37y <= 1. The result is the substantially uniform distribution of Ga atoms, Al atoms, N atoms and As atoms in each constituent layer according to the atomic mole fraction. Figure 16 shows the content choice line of Al content, x, and As content, y, in an GaAINAs system to avoid the phase separation phenomenon at growth temperatures below around 1000 °C and still ensure a reasonable lattice match to GaN. The line in Figure 16 shows the exemplary line of 3.18(1-x)(1-y)+3.99(1- x)y+3.Hχ(1-y)+4xy = 3.18. Therefore, by ensuring that the Al content and As content of the constituent GaAINAs layers of a laser diode formed on a GaN substrate have a relationship of 3.18(1-x)(1-y)+3.99(1-x)y+3.11x(1-y)+4xy nearly equals to 3.18, 0 < x <1 , 0 < y <1 , and 0.26x + 37y <= 1 , a laser diode on a GaN substrate with low defect density and no or very little phase separation can be obtained. In addition, other semiconductor structures can be fabricated with the materials system discussed above. Group-Ill nitride materials, especially GaN and AIN, are promising for use in electronic devices which can operate under high-power and high-temperature conditions - for example, microwave power transistors. This 5 results, in part, from their wide band gap (3.5 eV for GaN and 6.2 eV for AIN), high breakdown electronic field, and high saturation velocity. By comparison, the band gaps of AIAs, GaAs, and Si are 2.16 eV, 1.42 eV, and 1.12 eV, respectively. This has led to significant research in the use of AIGaN/GaN materials for such field effect transistors (FETs). However, as noted previously hereinabove, the different lattice 10 constants of AIGaN and GaN cause the generation of significant defects, limiting the mobility of electrons in the resultant structure and the utility of such materials systems for FET use. The present invention substantially overcomes these limitations, in that the GaAINAs/GaN material of the present invention has a lattice constant equal to GaN. 15 As discussed hereinabove, a quaternary materials system of Ga,. x Al x N,. y As y , where the Al content (x) and As content (y) satisfy the relationships 0 < x < 1 , 0 < y <1 , 0.26x + 37Y <= 1 , 3.18(1 -x)(1 -y)+3.99(1 -x)y+3.1 1 x(1 -y)+4xy equals to 3.18, not only has a band gap greater than 3.5 eV, but also has a lattice constant substantially equal to GaN. This permits fabrication of semiconductor structures such as FETs 20 which have substantially uniform atomic content distribution in the various layers. Therefore, by using a GaAINAs/GaN material system in accordance with the present invention, whose Al mole fraction, x and As mole fraction, y satisfy the above relationships, high-power and high-temperature transistors with low defect density can be realized. 25 Referring to Figure 17A, there is shown therein an exemplary embodiment of a heterojunction field effect transistor(HFET) using GaAINAs/GaN material in accordance with the present invention. On a GaN substrate 520, a 0.5 μm i-GaN layer 525 is formed, followed by a thin, approximately 10 nm GaN conducting channel layer 530 and a 10 nm GaAINAs layer 535. Source and drain electrodes 30 540A-B, and gate electrode 545 are formed in a conventional manner.ln the structure, the Al content, x, and As content, y, of the GaAINAs layer are set to be 0.25 and 0.021 , respectively. In this case, the value of x and y satisfy the relationship of 0 < x <1 , 0< y < 1 , 0.26x + 37Y <= 1 , 3.18(1 -x)(1 -y)+3.99(1 -x)y+3.1 1 x(1 -y)+4xy = 3.18 This results in an GaAINAs layer substantially without phase separation and 35 with a lattice constant equal to GaN, In turn, this permits high electron velocities to be achieved because the two dimensional electron gas formed in the heterointerface of GaAINAs and GaN layer is not scattered by any fluctuation in atomic content of the GaAINAs layer (such as would be caused in the presence of defects). Moreover, the band gap of the GaAINAs is larger than 4 eV so that reliable high-temperature operation can be achieved by using the structure shown in Figure 17A. Similarly, Figure 17B shows an embodiment of a heterojunction bipolar 5 transistor(HBT) in accordance with the present invention. On the GaN substrate 550, a 400 nm thick n-type GaAINAs collector layer 555 is formed, followed by a 50 nm thick p-type GaN base layer 560, and a 300 nm thick n-type GaAINAs emitter layer 565. Base electrode 570, collector electrode 575 and emitter electrode 580 are formed conventionally. As with Figure 17A, forthe exemplary embodiment of Figure 10 17B the Al and As contents x and y of the GaAINAs layer are set to be 0.25, 0.021 , respectively, and x and y are required to satisfy the same relationships as discussed above. As with Figure 17A, an GaAINAs layer without significant phase separation and with a lattice constant equal to GaN is realized, resulting in a very high quality heterojunction of GaAINAs/GaN. In addition, the band gap of the GaAINAs emitter 15 layer (4 eV) is larger than that of the GaN base layer (3.5eV) so that holes in the p- type base layer are well confined in that base layer. This results because of the larger valence band discontinuity between GaN and GaAINAs than would occur in a GaN homojunction bipolar transistor. This has the benefit of obtaining a large current amplification of collector current relative to base current. Moreover, as 20 mentioned above, the bandgap of the GaAINAs and the GaN layer is large so that the transistor can be used reliably in high-temperature applications. Referring next to Figure 18, there is shown therein an implementation of the present invention as a phototransistor. In this regard, GaN and AIGaN are attractive materials for photo detectors in ultraviolet(UV) range, since both GaN and AIN have 25 a wide band gap (3.5 eV for GaN which corresponds to the light wavelength of 350 nm, 6.2 eV for AIN which corresponds to the light wavelength of 200 nm). Due to the direct band gap and the availability of AIGaN in the entire AIN alloy composition range, AIGaN/GaN based UV photo detectors have the advantage of high quantum efficiency, as well as tunability of high cut-off wavelength. However, the lattice 30 constant of AIGaN is sufficiently different from GaN that defects tend to be formed, which leads increased leakage current. where the Al content (x) and As content (y) satisfy the relationships 0 < x < 1 , 0 < y <1 , 0.26x + 37y <= 1 , offers not only a band gap larger than 2.8 eV, but also can be fabricated in layers with equal atomic content distribution, so that GaAINAs material also can be used for UV 35 photo detector applications. Moreover, the Ga^A^N^AS y quaternary material whose Al content, x and As content, y satisfy the relationship of 3.18(1 -x)(1 -y)+3.99(1 - x)y+3.1 1 x(1 -y)+4xy =3.18 has a lattice constant equal to GaN and a bandgap larger than 3.5eV. Therefore, by using GaAINAs/GaN material whose Al content, x and As content, y satisfy the above relationship, UV photo detectors with low defect density can be realized. In the event that detection of other frequencies is desired, for example blue light, only slight modification is required. As shown in Figure 18, the semiconductor device of the present invention can be implemented as a heterojunction phototransistor(HPT) using GaAINAs/GaN material. On the GaN substrate 700, a GaAINAs collector layer 705 is formed on the order of 500 nm thick n-type, followed by the formation of a 200 nm thick p-type GaN base layer 710. Thereafter, a GaAINAs emitter layer 715 on the order of 500 nm thick is formed. On the emitter layer, a ring shaped electrode 720 is formed to permit light to impinge on the base layer. In an exemplary structure, the Al content, x and As contnet, y of the GaAINAs layer are set to be 0.25 and 0.021 , respectively. In this case, the value of x and y satisfy the relationship of 0 < x <1 , 0< y < 1 , 0.26x + 37Y <= 1 , 3.18(1 -x)(1 -y)+3.99(1- x)y+3.1 1 x(1 -y)+4xy = 3.18, so that an GaAINAs layer can be formed which substantially avoids phase separation while having a lattice constant equal to GaN, thus permitting the formation of a high quality heterojunction of GaAINAs/GaN. The band gap of the GaAINAs emitter layer (4 eV which corresponds to the light wavelength of 307 nm) is larger than that of GaN base layer (3.5eV which corresponds to the light wavelength of 350 nm). The light impinges on the emitter side. For the embodiment shown, impinging light in the wavelength range between 307 nm and 350 nm is transparent to the emitter layer, so that the light in that range is absorbed in the GaN base layer and generates electron and hole pairs. The holes generated by the optical absorption in the p-type base layer are weil confined in the base layer because the valence band discontinuity between GaN and GaAINAs is larger than that for a conventional GaN homojunction photo transistor. This leads to the induction of a larger emitter current, which offers better electronic neutralization in the base region than in the case of the homojunction photo transistor. Therefore, UV photo detectors with high quantum efficiency and high sensitivity, and the resultant high conversion efficiency from input light to collector current, are obtained. In the event that other frequencies are to be detected, the GaN base layer may be replaced with, for example for blue light, InGaN. In addition to the phototransistor of Figure 18, it is also possible to implement a photodiode in accordance with the present invention. Referring to Figure 19, an n- type substrate 900 is provided, on which is formed an n-type layer 91 O of Ga^ALN,. y As y quaternary material or equivalent, which conforms to the relationships discussed above in connection with Figure 18. An active layer 915 is thereafter formed, and above that is formed a layer 920 of p-type Ga^A N^ y AS y quaternary material. Then, a p-type second cladding layer 925 is formed above the layer 920, and a window 930 is formed therein to expose a portion of the layer 920.The window 930 provides a port by which light can impinge on the layer 920, causing the creation of holes. A pair of electrodes 935 and 940 may be fabricated in a conventional manner, with the electrode 935 typically being a ring electrode around the window 930. It will be appreciated that the band gap of the second cladding layer 925 is preferably larger than the band gap of the layer 920, which is in turn preferably larger than the band gap of the active layer 915; such an approach provides sensitivity to the widest range of wavelength of light. If the event a narrower range is desired, a material with a lower band gap than the layer 920 may be used for the layer 925. In addition, it is also not necessary to include the layer 925 in all embodiments, as the layers 910, 915 and 920 provide, in at least some instances, an adequate photosensitive pn- junction. Having fully described a preferred embodiment of the invention and various alternatives, those skilled in the art will recognize, given the teachings herein, that numerous alternatives and equivalents exist which do not depart from the invention. It is therefore intended that the invention not be limited by the foregoing description, but only by the appended claims.

Claims: We claim: 1. A semiconductor structure comprising: a first cladding layer of GaAINAs material having a first conduction type, an GaAINAs active layer, and a second cladding layer of GaAINAs material having a conduction type opposite the first conduction type, the mole fractions of the constituent elements of each layer being selected to minimize phase separation. 2. A semiconductor structure comprising: a first cladding layer of GaAINAs material having a first conduction type, an GaAINAs active layer, and a second cladding layer of GaAINAs material having a conduction type opposite the first conduction type, the crystal growth temperature and the mole fractions of the constituent elements of each layer being selected to minimize phase separation. 3. A light emitting device according to claim 1 , wherein the Al content, x, and the As content, y, of all the constituent layers satisfy the condition that 3.18(1 -x)(1 - y)+3.99(1 -x)y+3.1 1 x(1-y)+4xy nearly equals to a constant value. 4. A light emitting device according to claim 1 , wherein the GaN mole fraction, x, and the AIN, y, of all the constituent layers satisfy the condition that 3.18(1 -x)(1-y)+3.99(1 -x)y+3.1 1 x(1 -y)+4xy nearly equals 3.18. 5. A light emitting device comprising: a first conduction type of an GaAINAs first cladding layer without phase separation, an GaAINAs active layer without phase separation, and a second conduction type of GaAINAs second cladding layer without phase separation, said GaAINAs second cladding layer having a ridge structure, all successively formed one upon each other. 6. A light emitting device according to claim 4, wherein the Al content, x, and the As content, y, of all the constituent layers satisfy the condition that 3.18(1 -x)(1 - y)+3.99(1 -x)y+3.1 1 x(1 -y)+4xy nearly equals a constant value. 7. A light emitting device according to claim 4, wherein the Al content, x, and the As content, y, of all the constituent layers satisfy the condition that 3.18(1-x)(1- y)+3.99(1-x)y+3.1 1x(1-y)+4xy nearly equals 3.18. 8. A light emitting device comprising: a certain conduction type of a Ga 1 _ x1 Al x1 N 1 . y1 As y1 first cladding layer of said certain conduction type, a Ga 1 . x2 Al x2 N 1 . y2 As y2 active layer, an opposite conduction type of a Ga 1-x3 AI X3 N 1-y3 As y3 second cladding layer, all successively formed one upon each other, wherein x1 , x2, and x3 define the Al content, y1 , y2, and y3 define the As content, and x1 , y1 , x2, y2, x3, and y3 have a relationship of 0 < x1 <1 , 0 < x2 <1 , 0 < x3 <1 , 0 < y1 <1 , 0 < y2 <1 , 0 < y3 <1 , 0.26x1 + 37y1 <= 1 , 0.26x2 + 37y2 <= 1 , 0.26x3 + 37y3 <= 1 , Eg GaN (1 -x1 )(1-y1 )+Eg GaAs (1-x1 )y1 +Eg AIN x1 (1 -y1 )+Eg AIAs x1 y1 > Eg GaN (1 -x2)(1 -y2)+Eg GaAs (1 -x2)y2+Eg AIN x2(1 - y 2)+Eg AIAs x2y2, and Eg GaN (1 -x3)(1 - y3)+Eg GaAs (1 -x3)y3+Eg AIN x3(1 -y3)+Eg AlAs x3y3 > Eg GaN (1 -x2)(1 -y2)+Eg GaAs (1 - x2)y2+Eg AIN x2(1-y2)+Eg AIAs x2y2, where Eg GaN , Eg GaAs , Eg AIN , and Eg AIAs are the band gap energy of GaN, GaAs, AIN, and AIAs, respectively. 9. A light emitting device according to claim 8, wherein said active layer is a GaAINAs single or multiple quantum well active layer where Al content, xw, and As content, yw of all the constituent layers satisfy the relationship of 0 < xw <1 , 0< yw <1 , and 0.26xw + 37yw <= 1. 10. A light emitting device according to claim 8, wherein the condition of 3.18(1 -xs)(1 - ys)+3.99(1 -xs)ys+3.1 1 xs(1-ys)+4xsys nearly equals a constant value is satisfied, where xs and ys are the Al content and the As content, respectively in each constituent layers. 1 1 . A light emitting device according to claim 8, wherein the relationship of 3.18(1 - xs)(1 -ys)+3.99(1 -xs)ys+3.1 1xs(1 -ys)+4xsys nearly equals 3.18 is satisfied, where xs and ys are the Al content and the As content, respectively in each constituent layers. 12. A light emitting device comprising: a certain conduction type of a Ga^AI^N^AS y ., first cladding layer, a Ga^AI^N^AS y ;, active layer, an opposite conduction type of a Ga^AI^N^As^ second cladding layer, said Ga^AI^N^As^ second cladding layer has a ridge structure, all successively formed one upon each other, wherein x1 , x2, and x3 define the Al content, y1 , y2, and y3 define the As content, and x1 , y1 , x2, y2, x3, and y3 have a relationship of 0 < x1 <1 , 0 < x2 <1 , 0 < x3 <1 , 0 < y1 <1 , 0 < y2 <1 , 0 < y3 <1 , 0.26x1 + 37y1 <= 1 , 0.26x2 + 37y2 <= 1 , 0.26x3 + 37y3 <= 1 , Eg GaN (1- x1 )(1 -y1 )+Eg GaAs (1 -x1 )y1 +Eg AlN x1 (1 -y1 )+Eg A]As x1 y 1 > Eg GaN (1 -x2)(1 -y2)+Eg GaAs (1 - x2)y2+Eg AIN x2(1-y2)+Eg AIAs x2y2, and Eg GaN (1-x3)(1-y3)+Eg GaAs (1-x3)y3+Eg AIN x3(1- y3)+E gAWs x3y3 > Eg GaN (1 -x2)(1 -y2)+Eg GaAs (1 -x2)y2+Eg ΛN x2(1 - y 2)+E gA1As x2y2, where Eg GaN . Eg GaAs , Eg AIN , and Eg AIAs are the band gap energy of GaN, GaAs, AIN, and AIAs, respectively. 13. A light emitting device according to claim 12, wherein said GaAINAs active layer is a GaAINAs single or multiple quantum well active layer where Al content, xw, and As content, yw of ail the constituent layers satisfy the relationship of 0 < xw <1 , 0< yw <1 , and 0.26xw + 37yw <= 1. 14. A light emitting device according to claim 12, wherein the condition of 3.18(1- xs)(1-ys)+3.99(1-xs)ys+3.11xs(1-ys)+4xsys nearly equals a constant value is satisfied , where xs and ys are the Al content and the As content, respectively in each constituent layers. 15. A light emitting device according to claim 12, wherein the relationship of 3.18(1- xs)(1 -ys)+3.99(1 -xs)ys+3.11 xs(1 -ys)+4xsys nearly equals 3.18 is satisfied, where xs and ys are the Al content and the As content, respectively in each constituent layers.

Inventors: BABA TAKAAKI, HARRIS JAMES E JR, TAKAYAMA TORU, BABA, TAKAAKI, HARRIS, JAMES, E., JR., TAKAYAMA, TORU
Applicants: MATSUSHITA ELECTRIC CORP, MATSUSHITA ELECTRIC CORPORATION
Application year: 2000
Main classification: H01S5
IPC codes: H01L31, H01L33, H01S5