WATER-ABSORBENT RESIN COMPOUND AND PROCESSING

Abstract: The present invention relates to a water-absorbent having excellent malodorproofing effect and a process for preparing the same. The present invention characterized by the properties of increasing the ratio of the carboxyl radical in the resin compound, so that it improves the malodorproofing effect of the resin compound maintaining its original material property. More particularly, the flowability of the resin compound is enhanced by properly adding or spraying the solution of monomer containing the carboxyl radical onto the water-absorbent resin and by selectively adding filler of fumed silica. The water-absorbent resin compound of the present invention is used for the production of sanitary materials such as disposable diapers and sanitary napkins.

Description: WATER-ABSORBENT RESIN COMPOUND AND PROCESSING THE SAME TECHNICAL FIELD This invention relates to a water-absorbent resin compound and a method for the production. More particularly, it relates to a water-absorbent resin compound and a method for the production which possesses an excellent absorption capacity for urine, secretion and other body liquids and removes such malodors as ammonia and t r i ethylamine resulting from the decomposition of urine and secretion even after long wearing of sanitary materials and prevents from skin hives. DESCRIPTION OF THE RELATED ART Heretofore, many water-absorbent resins have been commercialized such as the partially neutralized and cross- linked poly-acrylic acids, hydrolyzed starch-acry loni t r i le graft polymers, neutralized starch-acrylic acid graft polymers, neutralized vinyl acetate-acrylic acid ester copolymers, hydrolyzed acryloni tr i le copolymers or hydrolyzed acrylamide copo lymer s . They are produced by aqueous sol ut i on pol ymer i z t i on , suspension polymerization and rever sed-phase suspension polymer i zat i on. Above mentioned water-absorbent resins can absorb the aqueous liquids and they are mainly used for sanitary materials as well as for agricultural materials and soil mel i oraters . The water-absorbent resin of this class have heretofore been desired to possess good properties like high water- absorption capacity and fine speed of absorption on contact with aqueous liquids, liquid permeability and high strength of the ge l swel l ed with l i qui d . Recently, however, the sanitary materials like disposable diapers and sanitary napkins are needed to possess not only the power of absorbing the body liquids like urine and secretions but the malodorproofing effect even after wearing sanitary materials for a long time and the preventive function from erythema and irritation on the skin on the contact with urine. If people wear the sanitary napkins made of the former water-absorbent resins for a long time, particular malodors like amines raised by effluvia resulting from the decomposition of urine and secretions on the sanitary materials by microbes. Especially, the ammonia which is so volatile, contacts human skin and becomes one of the reasons for dermatitis. So, many methods were proposed to treat the materials with additives and chemicals on the top sheet nonwoven fabric which constructs the sanitary materials to solve the former problems above mentioned. These methods, however, have not been commercialized due to its unfavorable affects onto body on the contact of the chemicals of the top sheet nonwoven fabric with the skin. Therefore, many methods of treatment with additive and chemicals into the water-absorbent resins and fiber of top sheet nonwoven fabric have been tried in order to solve the problem of skin hives and malodors without side-effects to body. More particularly, the method of adding antibiotics with nitrogen into the water-absorvent resin or the fiber of top sheet nonwoven fabric have been disclosed in US patent 4,842,593 and Japanese patent publication 1998-168757. The method of adding the metals like aluminum, copper or si liver into the water-absorbent resin or the fiber of top sheet nonwoven fabric have been disclosed in Japanese patent publication 1993-212094 and Japanese patent publication 1995-165981 disclosed. The method of adding the mul t i cavernous inorganic materials like zeolite into the water-absorbent resin or the fiber of top sheet nonwoven fabric have been disclosed in Japanese patent publication 1993-161671 and Japanese patent publication 1996-176338. But the methods adding antibiotics with nitrogen into the water-absorbent resins and the fiber of top sheet nonwoven fabric can not be commercialized because they are easy to influence side-effects onto the body, in spite of the positive effects to kill the microbes making malodors. The methods adding mul t i cavernous i norgani c mat er i al s like zeolite into the water-absorbent resins and the fiber of top sheet nonwoven fabric have less side-effects onto the body and better malodorproof ing f unct i on , espec i al ly in gas . But it can not get rid of the malodors efficiently if the sanitary material has been weared for a l ong t ime , due to its less capac i ty of def og i ng the malodors in liquids. More i l lust rat i on fol l ows on the ma l odor roof i ng effect of zeolite below. The secretion and urine come out of the body in liquids and they get slowly decomposed by the microbes and produce malodors from the residue. The malodors in gas hide in l iqui els and emi t s l owly by the passage of t ime and it is different from the status where thev move merely as gas in the air Once the mi crocavi t ies of zeolites are filled with the liquids of secretions and urines, the zeolites can not have the malodorproofing effect any more. The purpose of the present invention provides a capable water-absorbent resins, and a process for preparing the same that has excellent absorption capacity, malodorproofing effect and the preventing function from skin hives by eliminating the drawbacks of former methods described hereinabove. SUMMARY OF THE INVENTION The present invention relates to a water-absorbent resin compound and methods for the production. More particularly, it relates to a water-absorbent resin compound comprising 0.1-30 weight part of an monomer containing the carboxyl radical and 0~10 weight part of filler of fumed silica to 100 weight part of a water -absorbent resin. The present invention also relates to the production method of adding properly or spraying the solution of the monomer containing the carboxyl radical over the processing or the produced water-absorbent resins and selectively add the filler of fumed silica. Recently, one of the most common water-absorbent resins comprising the structure of the carboxyl radi ca 1 ( -COOH) and the sodium salt(-COONa) is partly neutralized and cross-linked poly-acrylic acid sodium salt. The said carboxyl radical and the said amines are expected to have the malodorproofing effect with mechanism in accordance with the following formula (I). Water-absorbent resin -COOH+NR'3 → R-C00NHR'3(Malodorproof) (I) The NR ' 3 in the above formula is ammonia or t r i ethyl ami ne . Considering the above mechanism, the inventor noticed i he increases the carboxyl radical in the water-absorbent resin he can remove the old problems such as malodors from the amines caused by the adoption of antibiotics, metals and zeolites into the sanitary materials and prevent the skin hives as well. Therefore, the present invention has the characteristic quality that it sustains the basic property of the water- absorbent resins but increases its malodorproofing capacity and makes it prevent the skin hives, adding the monomers with high amount of the carboxyl radical into the water-absorbent resins. The water-absorbent resin compound in the present invention can be used for various kinds of body liquids absorption goods such as the sanitary napkins, and disposable diapers and be applicable for the injury protecting and curing instruments for the incontinent BRIEF DESCRIPTION OF THE DRAWING FIGURE1 is the overview about the device to measure with the malodorproofing effect of the water-absorbent resin in the invent i on . In FIGURE1, 1 refers to a flask, 2 to the tested materia 3 to a vacuum adaptor, 4 to a measuring pipe, o to a silicon connecting tube, and 6 to a gas collector DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS The resin compound in this invention comprises the water-absorbent resin and the monomers containing the carboxyl radical. The resin compound in this invention may comprise the water-absorbent resin, the monomers containing the carboxyl radical and the filler of fumed silica. The monomers containing the carboxyl radical serves to increase the malodorproofing effect, maximizing the ratio of the carboxyl radical in the water-absorbent resin, and to prevent the skin hives. The filler of fumed silica works to enhance the flowability of the water-absorbent resin. The water-absorbent resin used in the present invention includes partially neutralized and cross-linked poly-acrylic acids, hydrolyzed starch-acryloni tr i le graft polymers, neutralized starch-acrylic acid graft polymers, neutralized vinyl acetate-acrylic acid ester copolymers, hydrolyzed acryloni tr i 1 e copolymers or hydrolyzed acrylamide copolymers. In thi s i nvent i on , the monomers cont ai n i ng carboxyl radical is one or more kinds of compound se 1 ect ed from i ) food add i t i ves like acetic acid, lactic acid, citric acid, tartaric acid and succinic acid, ii) interface activators like lauric acid, myristic acid, palmitic acid, stearic acid, behenic acid, oleic acid, linolenic acid, arachidic acid andr i c inolei c acid, iii) organ ic acids like vit am ins , and i v) other acids l ike am i no acid, benzoic acid, pyruric acid, fumaric acid, maleic acid, propionic acid, bytyric acid, caproic acid, oxalic acid, aliginic acid, ethoxyacetic acid, l ucuroni c ac id , sal i cy lie acid, cinamicacid, deoxycholic acid and allofuranoic acid. From the viewpoint of body safety, it is recommended to use the food additives like acetic acid, lactic acid, citric acid, tartaric acid and succinic acid or the organic acids like vitamins as monomers containing the carboxvl radical. But this invention does not specifically limit the classes of monomers containing the carboxyl radical. The amount of monomers containing the carboxyl radical in the water-absorbent resin compounds of the present invention is -from 0.1 to 30 parts by weight, more preferabh' from 0.2 to 15 parts by weight or most preferably from 0.5 to 10 parts b> weight to 100 parts by weight of a water-absorbent resin. If more than 30 parts by weight are used, it is not economic and the flowability of the water-absorbent resin slows down so rapidly that the production effect ivity of sanitary napkins and the absorption capacity of urine and secretion decreases. In the mean time, the amount of the filler of fumed silica is less than 10 parts by weight or more preferably less than 5 parts by weight, most preferably less than 3 parts by weight to 100 parts by weight of a water-absorbent resin. If the amount of the filler is over 10 parts by weight, the water-absorbent resin tend to stick together, so that they show decreased material properties of water absorbent resin such as the absorption capacity under load. The following description relates to the process for preparing the water-absorbent resins of the present invention. First of all, dissolve the selected monomer containing the carboxyl radical into a solvent, and prepare the solution composed thereof. At the moment, water or water and hvdrophlic organic solvents are used as the solvent. In the production of the monomer solution containing the carboxyl radical , the amount of the solvent depends on the kinds of monomer containing the carboxyl radical and the water-absorbent resins but most of the time it is from 1 to 30 parts by weight and more preferably from 3 to 20 parts by weight to 100 parts by weight of a water- absorbent resin. If the solvent is less than 1 part by weight, it is difficult to equally treat the monomers containing the carboxyl radi cal . If the solvent is more than 30 parts by wei ght , it takes longer to dry and decreases the effective and economic product ivity. The above mentioned monomer solution is sprayed ovei or properly mixed into the processing or produced water-absorbent resins. In this process, rotating mixer, screwing mixer, and level floating dryer can be used for the purpose of equal mixing. To spray and coat the monomer containing the carboxyl radical directly over the produced water-absorbent resins is most desirable because it can maximize the malodorproofing effect and retain the original material property of the resins. After the above mentioned mixing process, heat treatment can be made to help the safe adherence of the monomer containing the carboxyl radical. In the heat treatment, the temperatures are from 30 to 200 ° C , more preferably from 50 to 150 ° C and most preferably from 60 to 100 ° C . In the present invention, the monomer solution containing the carboxyl radical is directly sprayed over or mixed into the water-absorbent resins and the filler which is hydrophilic or Fumed Silica is mixed thereto. The equipments such as the batch type Tumbler mixer and Henkel mixer can be used at this process. From 0.1 to 30 parts by weight of the monomer containing the carboxyl radical and from 0 to 10 parts by weight of the filler of fumed silica are mixed to 100 parts by weight of the water-absorbent resin. Among the water-absorbent resin compounds which were produced in accordance with the above mentioned methods in the present invention, the monomer containing the carboxyl radical increase content of carboxyl radical in the resin and helps it have the malodorproofing effect and prevent from skin hives. The filler of fumed silica serves to increase the flowability of the water-absorbent resin and prevent the resins from st i eking together . As a result, the water-absorbent resin compound in the present invention is excellent in having the malodorproofing effect and preventing from the skin hives, maintaining its original material property. The water-absorbent resin compounds in the present invention has the absorption capacity without load of at least 30g/g to saline and the suction power of at least 5g/g to the pig's blood . In the present invention, the method to measure the property of the water-absorbent resin and its malodorproofing effect is as f ol lows . - Measurement of the absorpt i on capac i ty to phys i o 1 ogi ca 1 s 1 i ne After 0.5g of water-absorbent resin has been left in the lOOg of 0.9% saline for one hour, it is taken out with the ASTM 100 mesh standard net. Its absorption capaci ty(g/g) is measured in accordance with the amount of the absorbed saline - Measurement of the absorption capacity to pig's blood After l.Og of water-absorbent resin has been left in the 60g of fresh pig's blood for one hour, it is taken out with the ASTM 100 mesh standard net. Its absorption capac i ty( g/ ' g ) i measured in accordance with the amount of the absorbed blood - Measurement of the absorption speed to physiological saline The absorption speed is measured in accordance with the lapse of the disappearing vortex when 2.0g of water-absorbent resin is added into the 50g of physiological saline which is revolving at 500rpm. - Measurement of flowability Check the time lapse of lOOg of water-absorbent resin to pass the flowmeter funneHJIS K-3362). - Measurement of malodorproofing effect In the present invention, a measuring equipment is used as in Figure 1 to measure the malodorproofing effect for the malodors emitted from the urine and secretion in liquids as ime passes . lore particularly, the test mater i al (2) is put into the flask(l) which is a water-absorbent resin or the sanitarλ material made of it Then, the solution of odor so l vent (ammoni a or t r i methyl ami ne ) solved in physiological saline or pig's blood which are similar to urine and secretion, is added into the flask(l) with pipet and the flask(l) is sealed up and left in an oven at 40°C for 4 hours. Later, the flask(l) is opened and measure the amount (pp ) of existing odors in the air of flask using measuring pipeN) and gas col 1 edtor (5) . We refer the measured amount to A. Meanwhile, without the test material (2) of water-absorbent resin or the sanitary napkins made of it, just the solution of odor so 1 vent ( ammoni a or t r imethy 1 amine ) solved i n phys i o 1 ogi ca 1 saline or pig's blood which are similar to urine and secretion. is added into the flask(l) and it is sealed up and left in an oven at 40 ° C for 4 hours. Later, the flask(l) is opened and measure the amount(ppm) of existing odors in the air of flask using measuring pipe(4) and gas col I ector (5) . We refer the measured amount to B. The malodorproofing effect iscalculated in accordance with the following formula. -A) la l odorproof i ng effect(%) = 100 The present invention will be more particularly recognized with the following examples and comparative examples. But this invention is not confined in the ϊ o owing examples EXAMPLE 1 The solution is made in the way that 1 part by weight of amino acid and 2 parts by weight of cinamic acid are solved into the 5 parts by weight of methanol to 100 parts by weight of the acrylate sodium salt water-absorbent resin(Kolon Chemical Co. Ltd. K-SAM GS-3300N). The produced solution is sprayed and coated over the surface of the above mentioned water-absorbent resin, dried in an hot wind oven at 70 ° C and left at ordinary temperature. Then, 5 parts by weight of the filler of fumed silica are mixed into it and the water-absorbent resin compound is produced. The 75 weight parts of the above mentioned water-absorbent resin compound is mixed with the 25 weight parts of crushed pulp. sprayed over with distilled water and pressured on to become the water-absorbent st ructureCsani tary material) with the compression density of 0.17g/cc and basis weight of 0.47g/m' Table2 shows the malodorproofing effect of the mentioned water-absorbent resin compound and the watei absorbent st rue ture( sani t ar\ material) made of it, evaluated with the conditions on Tablel. The malodorproofing effect is measured in accordance with the pre-descr ibed measuring methods with the equipment on Figurel. TABLE 1. Evaluation Conditions for the Malodorproofing effect Table3 shows the exaluation result of the material propertx of the produced water-absorbent resin compound EXAMPLE 2 A solution is produced in the way that 2 weight parts of succinic acid is solved into 5 weight parts of methanol and 5 weight parts of ethanol to 100 weight parts of starch acrylatc water-absorbent resin(Sanwet IM-1000) . The solution is sprayed and coated over the above mentioned water-absorbent resin, dried in the hot wind oven at 60°C and left at the ordinary temperature. Then, 0.2 weight parts of filler of fumed silica is mixed to produce the water-absorbent resin compound. Meanwhile, 75 weight parts of the above mentioned water-absorbent resin compound is mixed with 25 weight parts of crushed pulp, sprayed over with the distilled water, and pressured on to obtain the water-absorbent structureC sani t ary mater i al ) . Table2 shows the malodorproofing effect of the water- absorbent resin compound and the water-absorbent structure (sanitary material) made of it evaluated with the conditions of Tablel in Examplel. Table3 shows the result of the evaluation for the material property of the water-absorbent resin compound. EXAMPLE 3 The solution is made in the way that 1 part by weight of ascobic acid and 2 parts by weight of tartaric acid are solved into the 5 parts by weight of distilled water to 100 parts b> weight of the acrylate sodium salt water-absorbent resinCKolon Chemical Co. Ltd. K-SAM GS-3400). The produced solution is properly added and mixed over the surface of the above mentioned water-absorbent resin, dried in an hot wind oven at 100C and left at ordinary temperature. Then. 1 parts by weight of the filler of fumed silica is mixed to produce the water-absorbent resin compound. Meanwhile, the 75 weight parts of the above mentioned water-absorbent resin compound is mixed with the 25 weight part of crushed pulp, sprayed over ith distilled water and pressured on to produce the water-absorbent st ructure(sani t ary mat er i a l ) . Table2 shows the malodorproofing effect of the water- absorbent resin compound and the water-absorbent structure (sanitary material) made of it evaluated with the conditions of Tablel in Examplel. Table3 shows the result of the evaluation for the material propeerty of the water-absorbent resin compound. EXAMPLE 4 The solution is made in the way that 2 part by weight of maleic acid and 2 parts by weight of fumaric acid are solved into the 8 parts by weight of methanol to 100 parts by weight of the acrylate sodium salt water-absorbent resin(SNF Florger Co . Ltd., Flosorb-550) . The produced solution is properly added and mixed over the surface of the above mentioned water-absorbent resin, dried in an hot wind oven at 60 ° C and left at ordinary temperature. Then. 0.5 parts by weight of the filler of fumed silica is mixed to produce the water-absorbent resin compound. Meanwhile, 75 weight parts of the above mentioned water-absorbent resin compound is mixed with the 25 weight parts of crushed pulp, sprayed over with distilled water and pressured on to produce the water-absorbent struct ure(sanitary material). Table2 shows the malodorproofing effect of the water- absorbent resin compound and the water-absorbent structure (sanitary material) made of it evaluated with the conditions of Tablel in Examplel. Table3 shows the result of the evaluation for the material property of the water-absorbent resin compound. COMPARATIVE EXAMPLE 1 75 weight parts of the acrylate sodium salt water-absorbent resin compound(GS-300N) without the monomer containing the carboxyl radical and the filler of fumed silica is mixed with the 25 wei ght parts of crushed pu l , sprayed over with d i st i I l ed water and pressured on to produce the water-absorbent structureCsanitary material). Table2 shows the malodorproofing effect of the water- absorbent resin compound and the water-absorbent structure (sanitary material) made of it evaluated with the conditions of Tablel in Examplel. Table3 shows the result of the evaluation for the material property of the water-absorbent resin compound. COMPARATIVE EXAMPLE 2 75 weight parts of the acrylate sodium salt water-absorbent resin compound( IM-1000) without the monomer containing the carboxyl radical and the filler of fumed silica is mixed with the 25 weight part s of crushed pulp , sprayed over with di st i 11 ed water and pressured on to produce the water-absorbent struc ureCsanitary material ) . Table2 shows the malodorproofing effect of the water- absorbent resin compound and the water-absorbent structure (sanitary material) made of it evaluated with the conditions of Tablel in Examplel. Table3 shows the result of the evaluation for the material property of the water-absorbent resin compound. COMPARATIVE EXAMPLE 3 75 weight parts of the acrylate sodium salt water-absorbent resin compoundCGS-3400) without the monomer containing the carboxyl radical and the filler of fumed silica is mixed with the 25 we i ght parts of crushed pulp , sprayed over with d i s t i 11 ed water and pressured on to produce the water-absorbent structureCsanitary material). Table2 shows the malodorproofing effect of the water- absorbent resin compound and the water-absorbent structure (sanitary material) made of it evaluated with the conditions of Tablel in Examplel. Table3 shows the result of the evaluation for the material property of the water-absorbent resin compound. COMPARATIVE EXAMPLE 4 75 weight parts of the acrylate sodium salt water-absorbent resin compoun (FI osorb-550) without the monomer containing the carboxyl radical and the filler of fumed silica is mixed with the 25 wei ght parts of crushed pulp, sprayed over ith distill ed water and pressured on to produce the water-absorbent structured an itary material ) . Table2 shows the malodorproofing effect of the water- absorbent resin compound and the water-absorbent structure (sanitary material) made of it evaluated with the conditions of Tablel in Examplel. Table3 shows the result of the evaluation for the material property of the water-absorbent resin compound. COMPARATIVE EXAMPLE 5 75 weight parts of the acrylate sodium salt water-absorbent resin compoundCChemda l Co., ASAP-2102) without the monomer containing the carboxyl radical and the filler of fumed silica is mixed with the 25 weight parts of crushed pulp, sprayed over with distilled water and pressured on to produce the water- absorbent structureCsanitary material). Table2 shows the malodorproofing effect of the water- absorbent resin compound and the water-absorbent structure Csanitarv material) made of it evaluated with the conditions of Tablel in Examplel Table3 shows the result of the evaluation for the materia property of the water-absorbent resin compound. TABLE 2. Evaluation result of malodorproofing effect [ % ; TABLE 3. Result of the property test of the water-absorbent resin compound

Claims: /HAT IS CLAIMED IS: 1. A water-absorbent resin compound comprising 0.1-30 weight parts of a monomer having a carboxyl radical and 0~30 weight parts of a filler of fumed silica to 100 weight parts of a water-absorbent resin 2. A water-absorbent resin compound therein of claiml, wherein the water absorbent resin is partially neutralized and cross-linked poly-acrylic acids, hydrolyzed starclv acryloni t r i le graft polymers, neutralized starch-acrylic acid graft polymers, neutralized vinyl acetate-acrylic acid ester copolymers, hydrolyzed acryloni t r i l e copolymers or hydrolyzed acrylamide copolymers. 3. A water-absorbent resin compound therein of claiml, wherein the monomer containing the carboxyl radical is one or more kinds of acids selected from acetic acid, lactic acid, citric acid, tartaric acid, succinic acid, lauric acid, myristic acid, palmitic acid, stearic acid, behenic acid, oleic acid, linolenic acid, arachidic acid, ricinoleic acid, amino acid, benzoic acid, pyruric acid, fumaric acid, maleic acid, propionic acid, bytyric acid, caproic acid, oxalic acid, aliginic acid, ethoxyacetic acid, glucuronic acid, salicλ'lic acid, cinamic acid, deoxvcholic acid and allofuranoic acid. 4. A water-absorbent resin compound therein of claiml, wherein the absorption capacity of the resin compound to saline without load is at least 30g/g and the suction capacity to pig blood is at least 5g/g. 5. A process for preparing a water-absorbent resin compound includes following two mixing stages: Firstly, the monomer sol ut i on cont aini ng the carboxy I r ad i ca l is sprayed over or properly added into the processing or produced water-absorbent resin. Secondly, the filler of fumed silica is mixed into it select i vely . . A process for preparing a water-absorbent resin compound of claimδ, wherein the absorbent resin is obtained by properly adding or spraying 0.1-30 weight parts of monomer containing the carboxyl radical to 100 weight parts of absorbent resin 7. A process for preparing a water-absorbent resin compound of claimS, wherein the absorbent resin is obtained by adding or mixing 0-10 weight parts of fumed silica to 100 weight parts of absorbent resin 8. A process for preparing a water-absorbent resin compound of claim5, wherein the absorbent resin is partially neutr lized and cross-linked poly-acrylic acids, hydrolyzed starch- acry l on i t r i l e graft polymers, neutralized starch-acrylic acid graft polymers, neutralized vinyl acetate-acrylic acid ester copolymers, hydrolyzed acryloni tr i le copolymers or hydrolyzed acryl amide copolymers. A process for preparing a water-absorbent resin compound of claiinS, wherein the monomer containing the carboxyl radical is includes one or more kinds of acids selected from acetic acid, lactic acid, citric acid, tartaric acid, succinic acid, 1 auric acid, myristic acid, palmitic acid, stearic acid, behenic acid, oleic acid, linolenic acid, arachidic acid, ricinoleic acid, amino acid, benzoic acid, pyruric acid. fumaric acid, maleic acid, prop ionic acid, bytyric acid. caproic acid, oxalic acid, aliginic acid, ethoxyacetic acid. gluctironic acid, salicylic acid, cinamic acid, deoxycholic acid and allofuranoic acid

Inventors: CHUN BO KYUNG, KANG BONG SEO, KANG MYUNG KOO, CHUN, BO, KYUNG, KANG, BONG, SEO, KANG, MYUNG, KOO
Applicants: CHUN BO KYUNG, KANG BONG SEO, KANG MYUNG KOO, KOLON CHEMICAL CO LTD, CHUN, BO, KYUNG, KANG, BONG, SEO, KANG, MYUNG, KOO, KOLON CHEMICAL CO., LTD.
Application year: 2000
Main classification: A61L15
IPC codes: A61F5, A61F13, A61K8, A61L15, A61Q15, C08K3, C08K5, C08L101