METHOD FOR THE PRODUCTION OF PARTS OF A CONSIDERABLE SPECIFIC GRAVITY BUILT ON FERROUS INERT MATERIALS, AND PARTS MANUFACTURED WITH SUCH A METHOD

Abstract: Method for manufacturing parts having a high specific gravity, comprising the phases of moulding a plastic shell; preparing a conglomerate having a specific gravity of at least 3.6 kg/dm<3> and containing waste ferrous materials acting as inert fillers, further to at least a cement-based binder and water; filling the conglomerate into the shell; hardening the conglomerate. The shell is moulded to the shape and size of the finished part to be manufactured, and the conglomerate is filled into the shell in a volumetrically metered quantity that is equal to the internal volume of the shell, while at the most imparting just a few final settling jolts.

Description: METHOD FOR THE PRODUCTION OF PARTS OF A CONSIDERABLE SPECIFIC GRAVITY BUILT ON FERROUS INERT MATERIALS, AND PARTS MANUFACTURED WITH SUCH A METHOD DESCRIPTION The present invention relates to a method for the production of parts manufactured to a high specific gravity based on the use of ferrous inert materials Manufactured parts of this kind typically include counterweights such as the ones used m home appliances, in particular the counterweights mounteα on the outer surface of the suspended tub that is a part of the washing assembly installed within the outer casing of a clothes washing or similar machine Ideally, manufactured parts of such a kind should - have the highest possible specific gravity, with particularly tight weight and dimensional tolerances so as to be able to take up a space which not only is the smallest possible one, but is also weϋ-defϊneα withm the outer casing of the washing machine, - be considerably strong an robust to withstand both localized stresses imparted by the attachment means on to the outer surface of the washing tub and the dynamic stresses induced by the oscillations of the suspended washing assembly during operation; - be capable of being manufactured in a manner that is consistent with the requirements imposed by the so-called "Just-in-Time" delivery system and, of course, at reduced costs and investments; - last, but not least, be easily separated from the other parts of the machine when the latter is discarded and scrapped, in view of a subsequent recycling in compliance with environment safeguard principles. For the production of such manufactured parts the practice is known since a rather long time to make use of cement-based conglomerates, in which the inert fillers are at least partly composed of ferrous oxides or similar materials in order to increase the specific gravity thereof. For instance, the method disclosed in US-A-3 185 255 includes following sequence of phases: - moulding of a shell of plastic material having the outer shape and size of the final counterweight, - casting, through the upper open portion of this shell, of a fluid conglomerate formed of concrete addeα with hematite (Fe 0 3 ), - hardening of the conglomerate, - closing of the upper open portion of the shell with a lid. Apart from the fact that the so achievable specific gravity (200 lbs/cu.ft, equal to approx. 3.2 kg/dm " ) is not compatible with the necessary mass and the reduced dimensions availab.e m modem clothes washing machines of the residential type, the above cited methoα, owing to the fact that it does not call for any use of accelerators for the cong.omerate harαening phase, certainly requires rather long processing times that are clearly not meeting the requirements of the above cited "Just-in-Time" delivery system. More recently, the European patent application EP-A-0 623 436 disclosed in this connection both the use of a plastic shell, reinforced by appropriate metal inserts, and a particularly fluid cement conglomerate comprising, further to metal chips as heavy inert fillers, undefined accelerating and/or binding additives. This method calls for the shell to be kept under continuous vibratory conditions in order to cause the conglomerate to become duly compacted before it starts to first solidify and then harden. While the presence of the reinforcing inserts can on the one side be understood as indicating the fact the conglomerate itself has just moderate inherent mechanical properties and, on the other side, causes the manufacturing costs of the counterweight to clearly increase, the need for the shell to be kept vibrating during the process introduces a clearly appreciable complication m this method. Still more recently, the European patent application EP-A-0 81 946 disclosed a method calling for the ferrous inert materials (rolling scales and the like) to be mixed with water. Owing to the shell requiring again to be kept m a continuous vibratory state m order to enable the conglomerate to become compacted, this method practically does not do away with the above cited drawbacks. It therefore is a mam purpose of the present invention to provide a method for producing manufactured parts with a high specific gravity industrially, which is again based on the used of waste materials from steel-making mills and the like (eg., ferrous oxides), is not connected to the afore mentioned drawbacks and is moreover able to meet all of the afore mentioned requirements A method with the features recited m the appended claims actually enables this and further aims to be reached. Anyway, characteristics and advantages of the present invention will become more readily apparent from the description that is given below by way of non- limiting example of a possible, although not sole implementation with reference to the production of a counterweight (being typically m a substantially toroiαal or crescent-like shape) which is adapted to be mounted on the outer surface of the oscillating tub that is part of the suspended washmg assembly of a home-type clothes washmg machine The plastic outer shell of the counterweight is manufactured m a traditional manner by means of a method such as injection moulding or blow moulding Thanks to the characteristics of the conglomerate, which will be described in greater detail further on, the shape and the dimensions of the shell (and, therefore, its inner volume) are exactly the final shape and dimensions of the counterweight, as they are set by the design engineer of the same clothes washmg machine in accordance with the other parts thereof that are intended to fit therewith, m particular the outer casmg of the machine and the washing tub The next phase of the manufacturing process of the counterweight consists m filling into the shell a conglomerate which, accordmg to the present mvention, is substantially formed from a cement bmder, waste ferrous material (micro-spheres or rolling scales) from a steel mill or similar steel making plant as inert fillers, and water The ferrous material is sifted and/or ground to a largest allowable gram size m the order of 6 millimetres A particularly appropnate cement bmder consists m turn of an ennched Portland cement powder having at a temperature of 20°C - a specific gravity of 1 035 kg/dm 5 - a pH value of approx 12 a good miscibility with water Accordmg to the present mvention the preparation of the conglomerate takes for instance place, while m any case continuously stirring the materials bemg processed m the drum of a concrete mixer accordmg to the following sequence of phases A Mixing of the inert fillers and the cement bmder m the appropriate mass- percentages of approx 80 to 85 mass percent and approx 15 to 20 mass percent i espectively foi some seconαs and unαer dry conditions B. Gradual addition, to the above indicated mix, of water in which there has been dissolved a liquid de-aerating agent, in order to obtain a conglomerate. Such a water addition amounts to approx. 35 to 40 mass-percent (taking the actual degree of humidity of the inert fillers into due account) of the above mentioned binder, The de-aerating substance is preferably formed from a mixture of phosphoric acid esters having at 20° C: - a specific gravity from 1.005 to 1.01 kg/dm 3 - a pH value from 7.5 to 10.5 - a viscosity from 7 to 14 mPas as well as following safety-relevant properties: - boiling pomt: 130°C - decomposition point: approx. 290°C - meltmg point: < -70°C - flash point: >150°C - self-ignition temperature: 400°C - vapour pressure at 20°C. 0.008 mbar - idem at 50°C. 0.08 mbar so that it is sufficient for a rather small amount of it to be used, generally m the order of approx. 0.04 mass-percent of the above cited cement bmder. This phase has typically a duration of approx 2 to 3 minutes. C. Addition to the conglomerate of a substance having the function of stabilizing the conglomerate and conferring it the necessary viscosity for the next phase of the counterweight manufacturing method accordmg to the present mvention, this substance bemg a combmahon of organic poly- hydroxides in an aqueous solution To this purpose, a particularly suitable substance is a combmahon of organic poly- hydroxides having at 20°C. - a specific gravity from 1.005 to 1.01 kg/dm 3 - a pH value from 7.5 to 10.5 - a viscosity from 7 to 14 mPas further to a good solubility in water. The stabilizing and viscosity-boosting substance can be metered into the conglomerate in a quantity varying from 0.3 to 0.5 mass-percent of the cement binder. This phase has a duration in the order of 15 to 25 percent of the duration of the preceding phase B, ie. it has a duration of just a few tens of seconds. A conglomerate according to the present invention has a specific gravity of at least 3.6 kg/dm 3 and advantageously has such a homogeneity and such a consistency as to be able to be metered volumetrically, ie. in a manner conforming to the inner volume of the shell, rather than by weighting as in the case of the conglomerates prepared according to prior-art methods. This is the reason why, as already hinted to earlier in this description, with a shell that has been moulded to exactly the same final shape and size of the counterweight, the latter has always the weight as set by the design engineer. As this has been found and demonstrated experimentally, the conglomerate filling phase that has been just described above does not therefore require that the shell be kept vibrating throughout the filling time. At most, just a few final jolts may be required, which anyway can also be imparted by hand. A further advantage of the present mvention, therefore, lies m the fact that the fabrication of the manufactured pails turns out to be facilitated and the necessary tools ' to be simplified to a quite significant extent. Filling the cement conglomerate mto the shell is furthermore done through a small aperture m the outer surface thereof, which can be plugged immediately thereafter smce, thanks to the synergetic effect of the de-aeratmg substance and the stabilizing and viscosity-promoting substance, the conglomerate is capable of gaining good mechanical properties very quickly. Laboratory tests have ascertained a flexural strength of the conglomerate in excess of 40 kg/cm ' , and a compressive strength in excess of 200 kg/cm 2 , after just 24 hours from filling into the shell. In an advantageous manner, anyway, the hardening of the conglomerate takes place in a closed, ie. sealed shell, so that the counterweight is capable of being immediately handled, although not used. In all cases, it clearly appears that the production of the counterweight according to the present invention is fully compatible with the "Just-in-Time" system, which is largely known to only admit a very short time between an order and the corresponding delivery of a manufactured part. The final mechanical characteristics of the conglomerate are definitely rewarding, since flexural strengths in excess of 80 kg/cm 2 and compressive strengths in excess of 450 kg/cm 2 have been measured in the laboratory after 28 days, ie. values that are at least the double of those measured after just 24 hours. As a result, no need seems to arise for metal inserts to be used to reinforce the counterweight, as opposed to prior-art solutions.

Claims: CLAIMS 1. Method for the production of a manufactured part having a high specific gravity, compnsmg the phases of: - moulding a shell of plastic material, eg. by injection or blow moulding; - preparing a conglomerate having a specific gravity of at least 3.6 kg/dm 3 and containing waste ferrous materials from steel mills or steel works act g as inert fillers, such as for instance oxides, further to at least a cement-based bmder and water; - filling the conglomerate mto the shell; and - hardening the conglomerate, characterized in that with said moulding phase the shell is formed to the same shape and the same dimensions as the finished manufactured part, and the phase of filling the conglomerate mto the shell m a volumetrically metered quantity that is equal to the internal volume of the shell, while at the most requiring just a few final settling jolts to be imparted to the same shell. 2. Method according to claim 1 , characterized in that the phase of hardening the conglomerate takes place after that the aperture used to fill the conglomerate therethrough has been plugged immediately upon the conglomerate havmg been so filled, so that lexurai and compressive strength values of the conglomerate after just 24 hours from filling are approximately fifty percent of the ultimate values 3. Method accordmg to claim 1 or 2, characterized in that the preparation of the conglomerate, which is carried out while continuously stirring the materials bemg processed, eg m the arum of a concrete mixer, consists m turn of following phases. A. mixing the inert fillers, which have been previously sifted and/or ground so as to obtain a grain size thereof not exceeding 6 mm, under dry conditions with a cement binder in the corresponding percentages of approx. 80 to 85 mass-percent and approx. 15 to 20 mass-percent, respectively; B. gradual addition of water in a quantity amounting to approx. 35 to 40 mass- percent of said cement binder, at least a de-aerating substance being dissolved in said water in a proportion of approx. 0.04 mass-percent of the same cement binder; C. addition to the so obtained conglomerate of at least a stabilizing and viscosity-promoting substance in a proportion of approx. 0.3 to 0.5 mass-percent of the same cement binder; 4. Method according to claim 3, characterized in that said phase C of addition of the stabilizing and viscosity-promoting substance has a duration in the order of 15 to 25 percent of the duration of said phase B of addition of water with de-aerating substance. 5. Method according to claim 3 or 4, characterized in that as a de-aerating substance use is made of a mixture of phosphoric acid esters having at 20°C: a specific gravity from 1.005 to 1.01 kg/dm 3 ; a pH value from 7.5 to 10.5; a viscosity from 7 to 14 mPas. 6. Method according to any of the preceding claims 3 to 5, characterized in that as a stabilizing and viscosity -promoting substance use is made of a combination of organic poly-hydroxides having at 20°C: a specific gravity from 1.005 to 1.01 kg/dm 3 ; a pH value from 7.5 to 10.5; a viscosity from 7 to 14 mPas, further to a good water solubility. 7. Manufactured part comprised substantially of an outer shell of plastic material and an inner cement conglomerate, in particular counterweight for the oscillating group of a clothes washing machine or other home appliance, characterized in that it is produced with the method according to any of the preceding claims.

Inventors: GRISONI LUCA, QUATTRIN ROBERTO, SANDRIN GIANNINO, GRISONI, LUCA, QUATTRIN, ROBERTO, SANDRIN, GIANNINO
Applicants: ELECTROLUX ZANUSSI ELETTRODOME, GRISONI LUCA, QUATTRIN ROBERTO, RO SA PLAST SPA, SANDRIN GIANNINO, SIKA ITALIA S P A, ELECTROLUX ZANUSSI S.P.A., GRISONI, LUCA, QUATTRIN, ROBERTO, RO-SA PLAST S.P.A., SANDRIN, GIANNINO, SIKA ITALIA S.P.A.
Application year: 2000
Main classification: D06F37
IPC codes: B28B19, C04B14, C04B28, D06F37