CEMENTITIOUS COMPOSITIONS

Abstract: A method of producing a curable cementitiuous composition comprises admixing: a) particles of cement, and b) an aqueous suspension containing a plasticiser and also particles of a pozzolan having a mean particle size which is at most one half that of the mean particle size of the cement, and allowing or causing the admixture to cure.

Description: CEMENTITIOUS COMPOSITIONS The present invention relates to cementitious compositions and methods for producing such compositions. High strength cement products can be produced by adding plasticisers or superplasticisers (usually organic polymers) to cement mixes, followed by high shear mixing, moulding, pressing or extrusion. The polymers serve to improve the rheology of the wet mix, allowing the particles to pack and flow better at lower water contents, thereby improving the cement microstructure in the cured state. For example, US-A-4410366 discloses hardenable cementitious compositions having a specified rheology and containing water in a proportion that is not greater than 25 wt% of the composition and at least one water soluble plasticiser in proportion of 1 to 15wt% of the cement. US-A-4353748 discloses a cement product obtained by mixing from l -5wt% of plasticiser with cement and water, wherein the volume of pores larger than 15 cubic micrometers does not exceed 0.5% of the volume of the product. This cement has a bend strength of higher than 40 MPa and in some cases higher than 50 MPa. EP-A-0 038 126 describes a cement composition where sub-micron particles are added to the cement mix in order to reduce the plasticiser level from to 3wt% of the cement mix. A major problem with these cement compositions is the high proportion of plasticiser that is required to achieve the desired rheology effects. Usually 1 wt% of plasticiser is necessary to observe a change in the rheology properties, 3 wt% gives a more significant change and 5 to 7wt% is required to gain maximum property benefits. This high level of plasticiser addition gives several disadvantages which have contributed to a reduction in the development of such materials. The main disadvantage is the susceptibility of the product incorporating plasticiser to water and environmental attack. Also the problems of excessive shrinkage, expansion, distortion, cracking and chemical attack have been observed under certain conditions. Secondly as the plasticisers are high cost materials, the cost of their addition becomes prohibitively high when they are mixed into cement in the proportions described above. Thirdly, often the current products fail to pass many of the fire resistance tests when containing such high levels of organic additives, i.e. the plasticisers. Obviously this implies that their use is restricted. It is an object of the present invention to obviate or mitigate the abovementioned disadvantages. According to a first aspect of the present invention there is provided a method of producing a curable cementitious composition comprising admixing: - a) particles of cement, and b) an aqueous suspension containing a plasticiser and also particles of a pozzolan having a mean particle size which is at most one half that of the mean particle size of the cement, and and allowing or causing the admixture to cure. It will be appreciated that the method of the invention may be effected with a single plasticiser or a mixture of plasticisers. Similarly the method of the invention may be effected with a single pozzolan or a mixture of pozzolans. Particle sizes as referred to herein may be measured with a Malvern Mastersizer model EBER Version 1.2. We have found, and this forms the basis for the present invention, that curable cement compositions with excellent rheological properties and containing a relatively low amount of plasticiser may be obtained by the use of a cement and a pozzolan. provided that (i) the pozzolan is initially formulated as a suspension in water also containing a plasticiser, and (ii) the pozzolan in the suspension has a mean particle size which is at most one half that of the cement to which the suspension will be added. As discussed more fully below, the amount of plasticiser (or mixture of plasticisers) used ma\ be less than 1% by weight of the curable composition. The cured compositions have good resistance to water and environmental attack. For the subsequent description the aqueous suspension shall be referred to as a milk, although it must be noted that no limitation is intended nor should be implied by the adoption of this term. It is envisaged but not necessarily essential that the milk will provide all of the water required for the curable composition. The milk may have the following composition. Pozzolan 5-60wt% Plasticiser 0.1-5wt% Water 35-95wt% The milk may be produced by mixing together at least one pozzolan, at least one plasticiser and water using a high speed mixer. Examples of a high speed mixer include a blade mixer, a ball mill or a bead mill. The required particle size for the pozzolan may be obtained during production of the milk, e.g. by using a bead mill. The milk may be stable enough to be stored/transported from its place of manufacture to the location at which it is to be used. However, if the milk is to be stored and/or transported then it preferably also incorporates a thickener (e.g. a polymeric thickener) to inhibit settlement of the pozzolan. The thickener may also improve the rheological properties of the cement composition. The amount of thickener may be in the range of 0.0002- 1.0wt%. Examples of thickeners include natural gums such as alginates. guar gum, cellulose, cellulose ethers such as methyl- hydroxyethyl and hydroxypropyl or synthetic polymers such as polyethylene oxides, acrylic co-polymers, polyvinyl alcohol or latex polymers. Preferably the mean particle size of the pozzolan is at most one fifth, more preferably one tenth, even more preferably at most one twentieth, and most preferably at most one thirtieth of that of the cement. It is generally preferred that the mean particle size of the pozzolan material be greater than 0.1 μm. A pozzolan (otherwise known as a pozzolana) is a material, which, though not cementitious by itself, will effectively react with lime, or sources of lime like Portland cement, to produce a cementitious product. Slags, especially granulated slags are often, for reasons of custom and practice, classified differently from pozzolans. Such a difference is more apparent than real. Pozzolans need an alkaline environment (effectively calcium hydroxide) to become cementitious and thus to contribute to long term strength and lower permeability. Slags are regarded as latently hydraulic (cementitious), but form surface films at the beginning of hydration that require an alkaline environment (such as lime or Portland cement) to break them down. In other words, slags and pozzolans are very similar - the differences are very fine. Accordingly, slags can best be regarded as forms of pozzolans, since any differences are at best secondary and in no way primary. The behaviour of slags in cement and pozzolans is very similar, so much so that slags can in reality be regarded as pozzolans. Pozzolans for use in the invention are selected to give a lubricious interaction with the cement and other particles in the composition to be cured. It is particularly preferred that the pozzolan is a plate-like material, having a preferred thickness of around 1 OOnm and a diameter of around 5 microns. Preferred examples of pozzolan for use in the invention include calcined clay, silica, silica fume, aluminosilicates. slags, granulated slags, fuel ashes, rice husk ash, calcined paper waste and calcined china clay. The latter material is known as metakaolin and is available from the English China Clay company. It is preferred that the pozzolan constitutes from 5-30% of the total weight of the cement and pozzolan in the composition. More preferably the pozzolan constitutes from 5-20% and even more preferably 5-10% on the same basis. Conventional curable cement compositions are generally produced with particulate cement having a mean particle sizes of approximately 15 μm. Such particulate cement may be employed for the present invention (indeed it is possible to employ cement having a lower mean particle size. e.g. at least 5μm and at least lOμm) but we have found that good rheological properties may be obtained by the use of a higher mean particle size for the cement. It is particularly preferred in accordance with the invention that the mean particle size of the cement is in the range of 20-1000μm, more preferably in the range of 50- lOOOμm, more preferably in the range of 50-300 μm and even more preferably in the range 75-300μm. It is even more preferred that the cement does not contain more than 10% by weight of particles below 50 μm and most preferred that the cement does not contain more than 5% by weight of particles below 20μm. It is particularly preferred that the particulate cement does not contain more than 5% by weight of particles above 300 μm. The desired particle size range for the cement may of course be obtained by sieving. For a cement having a particle size in the range 50-300μm it is preferred that the pozzolan has a mean particle size in the range 0.1-10μm, with not more than 5% of particles below 0.1 μm and not more than 5% of particles above lOμm. The cement may be any cement, as recognised by those skilled in the art, used in the building/maintenance/protection of structures. Preferred examples of such may be chosen from the group which includes calcium silicate, calcium aluminate (high aluminate) cements or blended cements. Thus, for example, the cement may be a Portland Cement. Alternatively the cement may be calcium sulphate based, calcium aluminate cement, glass based, oxide based, dental/medical cement or mixtures of these cements. The term cement is also intended to encompass clinker, a solid material, usually a ceramic that is totally or partially fused by heat treatment, which is recognised to include calcium silicates. The clinker may be ground after heat treatment. Modifying agents may be incorporated into the clinker, the agents may function as grinding aids. Examples include iron, silicon or aluminium oxides, calcium sulphate, carbonate or stearate. or stearic acid. A further component of the curable composition (incorporated in the milk) is a plasticiser which will generally be an organic polymer. It is particularly preferred to use a supeφlasticiser. Generally the invention allows the use of less than 1 wt% of plasticiser / supeφlasticiser, preferably less than 0.5 wt%, more preferably less than 0.3 wt%, e.g. between 0.05 to 0.15 wt% (this level of plasticiser is particularly useful for extrusion applications). Examples of a plasticiser / supeφlasticiser include polyacrylic acid, poly-carboxylates or salts, co-polymers or derivatives thereof. The derivatives may include polyacrylamides or other precursors, sulphonated naphthalene resins, lignosulphonates, "comb"-type plasticisers, cellulose based, polyvinyl alcohol based polymers, sulphonated melamine-formaldehyde condensates, sulphonated naphthalene-formaldehyde condensates or modified lignosulphonates. Optionally the plasticiser may include a charged moiety. Examples of a charged moiety include carboxylate, sulphonate, oxide or ammonium groups. Most preferably the plasticiser employed in the invention is a supeφlasticiser in the form of a "comb-type " polymer. Such polymers may comprise a backbone having charged and/or uncharged moieties (e.g. carboxylate, sulphonate, ester, amide or hydroxyl) and polyalkylene oxide (e.g. polyethylene oxide) side chains. Preferably the water content of the composition at the mixing stage is less than 20wt%. More preferably the water content is less than 15wt% and even more preferably less than 12%. A curable cementitious composition produced from the abovementioned components, i.e. cement and milk (pozzolan, plasticiser and water), may have the following composition. Cement 50-94 wt% Pozzolan 2-30 wt% Plasticiser 0.05-1.0 wt% Water less than 20 wt% Thickener 0-1.0wt% Preferably the pozzolan (or mixture of pozzolans) is present in the curable cement composition in the range of 5-30wt%. The composition may include other components as described below. The curable cementitious composition has the following properties and advantages. 1 ) High workability. 2) Large or difficult pours can be made with little or no vibration, i.e. self compacting to achieve a dense, very low void free product. 3) The composition can be spread onto a surface by means of a trowel or by spraying or painting. 4) The milk imparts superior capacity to disperse the cement/clinker agglomerates, resulting in minimal water usage and improved control. 5) The cement/clinker exhibits no retardation, gain in strength, low permeability and increased durability. 6) The cement/clinker mixtures remain cohesive, i.e. they show no segregation and can be pumped or sprayed. 7) Excellent surface finish Modifying agents may be incoφorated into the curable cement composition to obtain particular chemical and physical properties. These agents may be incoφorated during mixing or may be applied in the plastic or hardened state of the composition. Examples include an accelerating admixture, a retarding admixture, or an air entraining agent, or a polymer, in amounts known in the art. The accelerating admixture may lower the time of setting and accelerate the rate of strength development. It may be selected from the following group of materials: - (i) Soluble inorganic salts including chlorides, bromides, fluorides, carbonates, thiocyanates, nitrites, nitrates, thiosulphates, silicates, aluminates, alkali hydroxides, alkaline formate, calcium acetate, calcium propionate or calcium butyrate. (ii) Soluble organic compounds including triethanolamine. (iii) Setting admixtures such as those used in Shotcrete and materials that are recognised to promote setting in a few minutes including sodium silicate, sodium aluminate, aluminium chloride, sodium fluoride, strong alkalis or calcium chloride. (iv) Solid admixtures including calcium aluminate, seeds of finely divided Portland cement, silicate materials, aluminate materials, finely divided magnesium carbonate or calcium carbonate. Preferably the retarding admixture is selected from the group which includes lignosulphonates. sugars, hydrox} -carboxylic acids, carbonates, phosphates, inorganic salts of borates, or the halide. sulphate or nitrate salts of lead. zinc, copper, arsenic or tin. It is recognised that air entraining agents capture small air bubbles and thus improve the workability of the composition in the plastic state, reduce bleeding and segregation and hence increase the durability of the composition, particularly with regard to freeze-thawing. Preferably the air entraining agent is selected from the group which includes sodium oleate, sodium lauryl sulphate, and neutralised wood resin. The polymer may be used to improve the properties of the cement compositions, which have delayed hardening characteristics, low tensile strength, large drying shrinkage, low bonding strength in repair applications or low chemical resistance. The use of a polymer allows the production of anti-corrosion linings. Preferably the polymer is selected from the group which includes latices, cement compatible polymer dispersions, water soluble polymers, or liquid resins. Optionally the composition may further include modifying agents, e.g. sodium nitrite, potassium chromate, sodium benzoate or stannous chloride. The composition may further include fillers, e.g. pulverised fuel ash, pigmented materials, blast furnace slag, silica, sand, calcium carbonate, aggregates (natural or man-made) or fibres. Curable cement compositions in accordance with the invention have a variety of end uses, including: - 1 ) High specification mortars, grouts and renders. 2) Decorative materials such as paving slabs, tiles, coatings. 3) Acid resistant products, e.g. for use on farms. 4) Sulphate resistant products, i.e. for increased durability in sulphate containing environments. 5) Chloride resistant products, i.e. for increased durability in chloride containing environments. 6) Products which can prevent alkali silica reactions, reduce reinforcing bar corrosion, lower freeze-thaw damage and prevent efflorescence. 7) Special products, where the properties of the cement can be modified by the addition of fibres. 8) Lightweight products for thermal insulation. 9) Pipelinings. 10) Flooring. 11) Tiles. 12) Boards. 13) Extrusion applications, such as sections for construction. 14) Masonry j oining. 15) Cement paints. The invention will be further illustrated by the following, non-limiting Examples. Example 1 Particles of Metastar 501 (a metakaolin available from English China Clays International) were mixed with water in proportions of 1.2:1 by weight. 1.25wt% of Advacast (a 40wt% solution of polycarboxylate plasticiser, available from Grace Construction Products Ltd) was added to give a concentration of 0.5% plasticiser in the mixture. In addition approximately 0.04wt% of Kelzan (sodium alginate. available from Aldrich Chemicals) was added to the mixture as a thickening agent. The mixture was then bead milled for 30 minutes in order to grind the particles down to approximately 0.5-1 μm, as measured by a Malvern Mastersizer model EBER Version 1.2. This resulted in the production of a stable milky suspension. 50 grams of the milky suspension were added to 100 grams of a sieved Portland cement clinker which passed a 300μm mesh but which was held on a 150μm mesh and which contained a wide distribution of particle sizes to allow good particle packing. On mixing the composition in a blade mixer, a highly plastic composition was produced which could be squeezed to make thin sheets in a press or which could be cast moulded or extruded to produce tubes, bars and more complex shapes. This mixture contained 0.26 grams of organic additive in 150 grams of Portland cement powder, i.e. 0.17wt%. The product was cured in a plastic bag for several days and displayed very good surface quality, high bending strength and low permeability commensurate with its low porosity and uniform fine microstructure. The product was durable in both dry and wet environments, it resisted a blow torch flame and did not smoke excessively in a fire situation. Example 2 Metakaolin (Metastar 501 available from English China Clay Industries) and water in the ratio by mass of 1 :0.6 were mixed together. 1.75wt% of Glenium 51 (a 40wt% solution of polycarboxylate plasticiser, obtained from Feb Master Builders) was added to give a concentration of 0.7% plasticiser in the mixture. The mixture was mixed in a shear mixer for 1 minute in order to grind the particles down to approximately 0.4μm, as measured by a Malvern Mastersizer model EBER Version 1.2. To this mixture 0.05wt% Kelzan (sodium alginate, obtained from Aldrich Chemicals) was added as a thickening agent and mixing continued for a further 1 minute. This resulted in a stable suspension. To this suspension coarsely ground Portland cement was added (mean particle size of around 22 microns) so that the ratio by mass of the suspension to cement was 1 :2.5. Further mixing in a Hobart mixer for five minutes resulted in a very fluid paste, having an overall plasticiser content of 0.2wt%. The paste poured easily into moulds. The hardened material, placed under water for 28 days, exhibited compressive and flexural strengths of 100 and 15Mpa. Example 3 Metakaolin (Metastar 501 available from English China Clay Industries) and water in the ratio by mass of 1 :1.5 were mixed together. 1.25wt% of Glenium 51 (a 40wt% solution of polycarboxylate plasticiser, obtained from Feb Master Builders) was added to give a concentration of 0.5% plasticiser in the mixture. The mixture was mixed in a shear mixer for 1 minute in order to grind the particles down to approximately 0.4μm. as measured by a Malvern Mastersizer model EBER Version 1.2. To this mixture 0.05wt% Kelzan (sodium alginate, obtained from Aldrich Chemicals) was added as a thickening agent and mixing continued for a further 1 minute. This resulted in a stable suspension. To this suspension coarsely ground Portland cement clinker was added (in the particle size range 75-90 microns) so that the ratio by mass of the suspension to clinker was 1 :2. Further mixing in a Hobart mixer for five minutes resulted in a highly workable paste. The paste was poured into a plastic bag and pressed. After 8 hours pressing a strong tile resulted. The tile was strong and dense. This is due to the improved cement microstructure that is formed in the hydrating system. Example 4 Metakaolin (Metastar 501 available from English China Clay Industries), ground granulated blast furnace slag (GX5 obtained from Castle Cement Ltd) and water in the ratio by mass of 1:1 :3 were mixed together. 2.25wt% of Glenium 51 (a 40wt% solution of polycarboxylate plasticiser, obtained from Feb Master Builders) was added to give a concentration of 0.9% plasticiser in the mixture. The mixture was mixed in a shear mixer for 1 minute in order to grind the particles down to approximately 0.4μm, as measured by a Malvern Mastersizer model EBER Version 1.2. To this mixture 0.04wt% Kelzan (sodium alginate, obtained from Aldrich Chemicals) was added as a thickening agent and mixing continued for a further 1 minute. This resulted in a stable suspension. To this suspension coarsely ground Portland cement was added (mean particle size about 22 microns) so that the ratio by mass of the suspension to cement was 1 :2. Further mixing in a Hobart mixer for five minutes resulted in a very fluid paste which poured easily into moulds and was then hardened. The hardened material showed low porosity and permeability and had good surface quality and excellent durability when left exposed to all weather conditions outdoors. The hardened material showed no efflorescence (which would otherwise be caused by leaching of lime and its subsequent carbonation). Example 5 Metakaolin (Metastar 501 available from English China Clay Industries), ground granulated blast furnace slag (GX5 obtained from Castle Cement Ltd) and water in the ratio by mass of 1 :1 :3 were mixed together. 2.38wt% of Glenium 51 (a 40wt% solution of polycarboxylate plasticiser, obtained from Feb Master Builders) was added to give a concentration of 0.95%o plasticiser in the mixture. The mixture was mixed in a shear mixer for 1 minute in order to grind the particles down to approximately 0.4μm. as measured by a Malvern Mastersizer model EBER Version 1.2. To this mixture 0.04 t% Kelzan (sodium alginate, obtained from Aldrich Chemicals) was added as a thickening agent and mixing continued for a further 1 minute. This resulted in a stable suspension. To this suspension coarsely ground Portland cement (mean particle size about 22 microns) and Portland clinker (sieved through 1.18mm mesh) were mixed in the ratio of 1 :0.4 by mass. This resulted in a cement and clinker mixture. This cement and clinker mixture was mixed with the previously prepared suspension in the ratio of cement and clinker mixture to suspension 2:1. Further mixing in a Hobart mixer for five minutes resulted in a very fluid paste which poured easily into moulds and was then hardened. A prismatic sample (160mm x 40mm) was subjected to a standard water test in which the hardened sample is placed in water, the water changed daily and the pH of the water measured when changed. The results obtained were compared with those for a similar sized sample made of a standard 1.5:1 sand and cement mortar The water in the water test of the cement according to Example 5 reached a pH of 9 in 9 days, as compared to a standard 1.5:1 sand and cement mortar which took 35 days to reach the same pH. The shorter time span indicates that a lower amount of alkali (Na + /K + ions) had dissolved out of the cement, due to a more tight microstructure, which allows less material to be leached from the cement. Example 6 Metakaolin (Metastar 501 available from English China Clay Industries), ground granulated blast furnace slag (GX5 obtained from Castle Cement Ltd), water and yellow iron oxide pigment in the ratio by mass of 1 :1 :2.75:0.1 were mixed together. 2.48wt% of Glenium 51 (a 40wt% solution of polycarboxylate plasticiser, obtained from Feb Master Builders) was added to give a concentration of 0.99% plasticiser in the mixture. The mixture was mixed in a shear mixer for 1 minute in order to grind the particles down to approximately 0.4μιm, as measured by a Malvern Mastersizer model EBER Version 1.2. To this mixture 0.04wt% Kelzan (sodium alginate. obtained from Aldrich Chemicals) was added as a thickening agent and mixing continued for a further 1 minute. This resulted in a stable suspension. To the suspension coarsely ground Portland cement (mean particle size about 22 microns) and Portland clinker (sieved through 0.6mm mesh) were mixed in the ratio of 1 :0.4 by mass. This resulted in a cement and clinker mixture. This cement and clinker mixture was mixed with the previously prepared suspension in the ratio of cement and clinker mixture to suspension 2:1. Further mixing in a Hobart mixer for five minutes resulted in a very fluid paste, having an overall plasticiser content of 0.3wt%. The paste poured easily into moulds. The hardened material exhibited comparable properties as in the previous Example. Example 7 Metakaolin (Metastar 501 available from English China Clay Industries), and water in the ratio by mass of 1:1.5 were mixed together. 1.25wt% of Glenium 51 (a 40wt% solution of polycarboxylate plasticiser, obtained from Feb Master Builders) was added to give a concentration of 0.5% plasticiser in the mixture. The mixture was mixed in a shear mixer for 1 minute in order to grind the particles down to approximately 0.4μm. as measured by a Malvern Mastersizer model EBER Version 1.2. To this mixture 0.05wt% Kelzan (sodium alginate, obtained from Aldrich Chemicals) was added as a thickening agent and mixing continued for a further 1 minute. This resulted in a stable suspension. To this suspension was added calcium aluminate cement (obtained from Lafarge Aluminates, mean particle size range 75-90 microns) so that the ratio by mass of suspension to cement was 1 :2. Further mixing in a Hobart mixer for five minutes resulted in a highly workable paste. The paste was poured into a plastic bag and pressed. After 8 hours pressing a strong, dense tile resulted. Firing to 1 150°C resulted in a strong ceramic-like tile being produced, due to the development of ceramic bonding in the system. Example 8 Metakaolin (Metastar 501 available from English China Clay Industries) and water were mixed in the proportion 1 :1.3 by weight. 3.6wt% of Glenium 51 (a 40wt% solution of polycarboxylate plasticiser, obtained from Feb Master Builders) was added to give a concentration of 1.42% plasticiser in the mixture. In addition approximately 0.04wt% of Kelzan (sodium alginate, obtained from Aldrich Chemicals). The suspension was bead milled for 30 minutes in order to get particles of 0.34μm. The suspension was placed in a Hobart mixer and ordinary Portland cement (from Castle Cement, mean particle size 21.8 microns) was added in the ratio of 0.35: 1. This mixture was mixed for 5 minutes to obtain an almost dough like paste, having an overall plasticiser content of 0.35wt%. The paste was placed in an extrusion die (10cm long with 5mm exit hole and 1cm diameter). The paste was extruded by having a loading rate of 1 cm/minute (crosshead speed) into a rod of 5mm diameter. This rod was put in a plastic bag and sealed. After 8 hours the extruded paste rod exhibited an excellent surface finish, showed no shrinkage cracking and on breaking the cross section showed no air bubbles.

Claims: CLAIMS 1. A method of producing a curable cementitious composition comprising admixing: a) particles of cement, and b) an aqueous suspension containing a plasticiser and also particles of a pozzolan having a mean particle size which is at most one half that of the mean particle size of the cement, and allowing or causing the admixture to cure. 2. A method as claimed in claim 1 wherein the composition contains less than 1% by weight of plasticiser. 3. A method as claimed in claim 2 wherein the composition contains less than 0.5%) by weight of plasticiser. 4. A method as claimed in claim 3 wherein the composition contains less than 0.3%) by weight of plasticiser. 5. A method as claimed in claim 4 wherein the composition contains between 0.05 to 0.15%) by weight of plasticiser. 6. A method as claimed in any one of claims 1 to 5 wherein a thickening agent is incorporated in the aqueous suspension 7. A method as claimed in claim 6 wherein the thickening agent is a polymeric thickening agent. 8. A method has claimed in any one of claims 1 to 7 wherein the mean particle size of the pozzolan is at most one fifth of that of the cement. 9. A method has claimed in claim 8 wherein the mean particle size of the pozzolan is at most one tenth of that of the cement. 10. A method as claimed in claim 9 wherein the mean particle size of the pozzolan is at most one twentieth of that of the cement. 11. A method as claimed in claim 10 wherein the mean particle size of the pozzolan is at most one thirtieth of that of the cement. 12. A method as claimed in any one of claims 1 to 11 wherein the pozzolan has a mean particle size greater than 0.1 μm. 13. A method as claimed in claim 12 wherein the pozzolan has a mean particle size in the range of 0.1 to lOμm. 14. A method as claimed in any one claims 1 to 13 wherein the cement has a mean particle size in the range 20-1000μm. 15. A method as claimed in claim 14 wherein the cement has a mean particle size in the range 50-1000μm. 16. A method as claimed in claim 15 wherein the cement has a mean particle size in the range of 50-300μm. 17. A method as claimed in claim 16 wherein the cement has a mean particle size in the range of 75-300μm. 18. A method as claimed in claims 16 or 17 wherein the cement does not contain more than 5% by weight of particles having a size below 20μm and not more than 5% by weight of particles having a size above 300μm. 19. A method as claimed in claim 18 wherein the cement does not contain more than 5%> by weight of particles having a size below 50μm and not more than 5% by weight of particles having a size above 300μm. 20. A method as claimed in any one of claims 1 to 19 wherein the cement is a calcium silicate, calcium aluminate (high alumina), blended, Portland, calcium sulphate, glass based, oxide based, clinker or mixtures of these cements. 21. A method as claimed in any one of claims 1 to 20 wherein the pozzolan is metakaolin. 22. A method of producing a curable cementitious composition comprising admixing :- (a) particles of cement having a particle size in the range of 20-1000μm. and (b) an aqueous suspension containing a plasticiser and also particles of a pozzolan having a particle size in the range of 0.1 -10mm, such that the composition comprises by weight 50-95wt% cement, 2-30wt% pozzolan. and less than 1.0wt% plasticiser, and allowing or causing the mixture to cure. 23. A method according to claim 22 wherein the cement has a particle size in the range of 50-1000μm. 24. A method according to claim 22 or 23 wherein the composition comprises between 5-30% by weight of pozzolan. 25. A method as claimed in claim 22, 23 or 24 wherein the composition contains less than 0.5wt%> by weight of plasticiser. 26. A method as claimed in claim 25 wherein the composition contains less than 0.3wt%> by weight of plasticiser. 27. A method as claimed in claim 26 wherein the composition contains between 0.05 to 0.15wt%> by weight of plasticiser. 28. A method as claimed in claim 27 wherein the pozzolan is metakaolin. 29. A method as claimed in any one of claims 1 to 28 wherein the plasticiser is chosen from the group that includes polyacrylic acid, poly-carboxylates and salts, co-polymers and derivatives thereof, wherein the derivatives include polyacrlyamides and other precursors, sulphonated naphthalene resins, lignosulphonates, "comb " '-type plasticisers, cellulose based, polyvinyl alcohol based polymers. sulphonated melamine-formaldehyde condensates, sulphonated naphthalene-formaldehyde condensates and modified lignosulphonates. 30. A method as claimed in claim 29 wherein the plasticiser is a "comb"-type plasticiser, comprising a backbone having charged and/or uncharged moieties and polyalkylene side chains. 31. A method as claimed in any one of claims 1 to 30 wherein the plasticiser is a supeφlasticiser. 32. A curable cementitious composition according to any of the preceding claims. 33. An aqueous suspension of a pozzolan, said suspension containing a cement plasticiser. 34. An aqueous suspension according to claim 33 which includes a thickening agent.

Inventors: BENSTED JOHN, KENDALL KEVIN, LOTA JASBIR SINGH, BENSTED, JOHN, KENDALL, KEVIN, LOTA, JASBIR, SINGH
Applicants: BENSTED JOHN, KENDALL KEVIN, LOTA JASBIR SINGH, UNIV KEELE, BENSTED, JOHN, KEELE UNIVERSITY, KENDALL, KEVIN, LOTA, JASBIR, SINGH
Application year: 2000
Main classification: C04B40
IPC codes: C04B7, C04B14, C04B20, C04B40