FORMULATIONS OF HYALURONIC ACID FOR DELIVERY OF OSTEOGENIC PROTEINS

Abstract: An injectable formulation is disclosed for delivery of osteogenic proteins. The formulation comprises a pharmaceutically acceptable admixture of an osteogenic protein; and formulations comprising osteogenic protein, hyaluronic acid derivatives and tricalcium phosphate are also disclosed. Methods for formulating porous injectable gels and pastes from hyaluronic acid are also disclosed.

Description: FORMULATIONS OF HYALURONIC ACID FOR DELIVERY OF OSTEOGENIC PROTEINS BACKGROUND OF THE INVENTION The subject invention relates to the field of osteogenic proteins and pharmaceutical formulations thereof. More particularly, the subject invention involves injectable pharmaceutical formulations comprising hyaluronic acid derivitives and osteogenic proteins. The invention further provides methods for formulating porous injectable gels and pastes from hyaluronic acid. Osteogenic proteins are those proteins capable of inducing, or assisting in the induction of, cartilage and/or bone formation. Many such osteogenic proteins have in recent years been isolated and characterized, and some have been produced by recombinant methods. For example, so-called bone morphogenic proteins (BMP) have been isolated from demineralized bone tissue (see e.g. Urist US 4,455,256); a number of such BMP proteins have been produced by recombinant techniques (see e.g. Wang et al. US 4,877,864 and Wang et al. US 5,013,549); a family of transforming growth factors (TGF-oc and TGF-β) has been identified as potentially useful in the treatment of bone disease (see e.g. Derynck et al., EP 154,434); a protein designated Vgr-1 has been found to be expressed at high levels in osteogenic cells (see Lyons et al. (1989) Proc. Nat'l. Acad. Sci. USA 86, 4554-4558); and proteins designated OP-1, COP-5 and COP-7 have purportedly shown bone inductive activity (see Oppermann, et al. U.S. 5,001,691). Various formulations designed to deliver osteogenic proteins to a site where induction of bone formation is desired have been developed. For example, certain polymeric matrices such as acrylic ester polymer (Urist, US 4,526,909) and lactic acid polymer (Urist, US 4,563,489) have been utilized. A biodegradable matrix of porous particles for delivery of an osteogenic protein designated as OP is disclosed in Kuber A. Sampath, U.S. 5,108,753. Brekke et al., United States Patents 4,186,448 and 5,133,755 describe methods of forming highly porous biodegradable materials composed of polymers of lactic acid ("OPLA"). Okada et al, US 4,652,441, US 4,711,782, US 4,917,893 and US 5,061,492 and Yamamoto et al., US 4,954,298 disclose a prolonged-release microcapsule comprising a polypeptide drug and a drug-retaining substance encapsulated in an inner aqueous layer suπounded by a polymer wall substance in an outer oil layer. Yamazaki et al., Clin. Orthop. and Related Research. 234:240-249 (1988) disclose the use of implants comprising 1 mg of bone morphogenetic protein purified from bone and 5 mg of Plaster of Paris. United States Patent 4,645,503 discloses composites of hydroxyapatite and Plaster of Paris as bone implant materials. Collagen matrices have also been used as delivery vehicles for osteogenic proteins (see e.g. Jeffries, U.S. 4,394,370). SUMMARY OF THE INVENTION The present invention provides injectable formulations for delivery of osteogenic proteins. In one embodiment the composition comprises the osteogenic protein and hyaluronic acid esters. In another embodiment, the composition may further include tricalcium phosphate. The injectable formulations of the invention allows for closed fracture repair and other skeletal tissue without an open reduction procedure as is necessary with implantable devices. The present invention further provides methods for preparing injectable gels or pastes useful as a carrier for osteogenic proteins by transforming various non-woven pads and sponges of hyaluronic acid benzyl ester into injectable gel or paste formulations by hydration or solvent addition. In another embodiment, the invention comprises compositions comprising the transformed injectable gel or paste formulations. The methods and compositions of the present invention are useful for the preparation of formulations of osteoinductive proteins which can be used, among other uses, to promote the formation of cartilage and/or bone, for repair of tissue damage and fractures. The invention further provides methods for treating patients in need of cartilage and/or bone repair and/or growth. BRIEF DESCRIPTION OF THE DRAWINGS Figure 1 sets forth in vitro release kinetics of 125 I-rhBMP-2 in Hyaff gels. Figure 2 sets forth in vivo retention of 125 I-rhBMP-2 in Hyaff- 11/PEG, ACS, and buffer. Figure 3 sets forth in vitro release kinetics of 125 I-rhBMP-2 in Hyaff gels/TCP. Figure 4 sets forth in vivo biodistribution of 125 I-rhBMP-2. DETAILED DESCRIPTION OF THE INVENTION The invention provides injectable formulations for delivery of osteogenic proteins. The compositions comprise an injectable formulation of hyaluronic acid esters and osteogenic protein. The present invention further provides processes for preparing injectable gel or paste formulations by transforming various non- woven pads and sponges of hyaluronic acid benzyl ester by hydration or solvent addition yielding gels with in vivo residence times from days to up to several months. Total or partial esters of hyaluronic acid are described in US 5,336,767. Partial esters of Hyaff solids are transformed into gels using aqueous buffer or organic solvents (such as N-methyl pyπolidinone, dimethyl sulfoxide, etc), while complete esters of Hyaff solids are transformed into gels using organic solvents. In other embodiments pore formers may be introduced to the solublized carriers to increase porosity. The addition of pore formers would allow in situ pore formation after injection in vivo by solubilization of pore former and precipitation/phase inversion of carrier. Suitable liquid pore formers include polyethylene glycol or PEG at 10 - 90 % volume per volume ratios) and solid pore formers (such as sodium bicarbonate, sodium chloride, citric acid, sucrose, etc., at 1 :1 - 21:1 pore formeπHyaff weight per weight ratios) to increase porosity. The gel/paste can also contain TCP (tri-calcium phosphate) particles as a mineral component for example, at 0.1 - 100 % weight per volume range. The amount , type and size of the pore forming agent is optimized to leave voids sufficient for cell ingrowth into injectable gel when pore forming agent and solvent are extracted from the carrier in vivo by solubilization of pore forming agent and precipitation/phase inversion of caπier in situ. The osteogenic proteins useful with the injectable earners made in accordance with the subject invention are well known to those skilled in the art and include those discussed above. The prefeπed osteogenic proteins for use herein are those of the BMP class identified as BMP-1 through BMP-12 in US 4,877,864; US 5,013,649; WO 90/1 1366 published October 4, 1990; WO 91/18098 published November 28, 1991; WO 93/00432, published January 7, 1993; United States Serial Numbers 08/247,908 and 08/247,904, both filed May 20, 1994; and United States Serial Number 08/217,780, filed on March 25, 1994. The disclosure of the above publications are hereby incorporated by reference. The most prefeπed is BMP-2, the full length cDNA sequence of which is described in detail in the '649 patent. Of course, combinations of two or more of such osteogenic proteins may be used, as may fragments of such proteins that also exhibit osteogenic activity. Such osteogenic proteins are known to be homodimeric species, but also exhibit activity as mixed heterodimers. Heterodimeric forms of osteogenic proteins may also be used in the practice of the subject invention. BMP heterodimers are described in WO93/09229, the disclosure of which is hereby incorporated by reference. Recombinant proteins are prefeπed over naturally occurring isolated proteins. The amount of osteogenic protein useful herein is that amount effective to stimulate increased osteogemc activity of infiltrating progenitor cells, and will depend upon the size and nature of defect being treated as well as the carrier being employed. The formulations may be injected for example into tendons, damaged cartilage tissue, ligaments, and or their attachment sites to bones. Injectable formulations may also find application to other bone sites such as bone cysts, bone defects, intraosseous sites and closed fractures. The dosage regimen will be determined by the clinical indication being addressed, as well as by various patient variables (e.g. weight, age, sex) and clinical presentation (e.g. extent of injury, site of injury, etc.). In general, the dosage of osteogenic protein will be in the range of from about 0.1 to 4 mg/ml. The injectable osteogenic protein formulations may be provided to the clinic as a single formulation, or the formulation may be provided as a multicomponent kit wherein, e.g. the osteogenic protein is provided in one vial and the injectable hyaluronic paste is provided separately. The compositions of the subject invention allow therapeutically effective amounts of osteoinductive protein to be delivered to an injury site where cartilage and/or bone formation is desired. The formulations may be used as a substitute for autologous bone graft in fresh and non-union fractures, spinal fusions, and bone defect repair in the orthopaedic field; in cranio/maxillofacial reconstructions; for prosthesis integration, especially as a surface coating to improve fixation of prosthetic implants such as hydroxyapatite coated prostheses; in osteomyelitis for bone regeneration; and in the dental field for augmentation of the alveolar ridge and periodontal defects and tooth extraction sockets. The methods and formulations of the present invention may be useful in the treatment and/or prevention of osteoporosis, or the treatment of osteoporotic or osteopenic bone. In another embodiment, formulations of the present invention may be used in the process known as distraction osteogenesis. When used to treat osteomyelitis or for bone repair with minimal infection, the osteogenic protein may be used in combination with porous microparticles and antibiotics, with the addition of protein sequestering agents such as alginate, cellulosics, especially carboxymethylcellulose, diluted using aqueous glycerol. The antibiotic is selected for its ability to decrease infection while having minimal adverse effects on bone formation. Prefeπed antibiotics for use in the devices of the present invention include vancomycin and gentamycin. The antibiotic may be in any pharmaceutically acceptable form, such as vancomycin HC1 or gentamycin sulfate. The antibiotic is preferably present in a concentration of from about 0.1 mg/mL to about 10.0 mg/mL. The traditional preparation of formulations in pharmaceutically acceptable form (i.e. pyrogen free, appropriate pH and isotonicity, sterility, etc.) is well within the skill in the art and is applicable to the formulations of the invention. Hyaluronic derivitive compositions of the invention prepared by hydration or solvent addition of insoluble or partially soluble non- woven pads or sponges may also be ultilized in combination with other drugs, growth factors, peptides, proteins, cytokines, oligonucleeotides antisense oligonucleotides, DNA and polymers. These compounds may be added by mixing them with the carriers. Or by covalent attachment to the polymer carriers. The hyaluronic derivitive compositions may also be used with DNA encoding for BMPs and cells transduced or transfected with genes encoding BMP proteins. The following examples are illustrative of the present invention and are not limiting in any manner. Modifications, variations and minor enhancements are contemplated and are within the present invention. EXAMPLE 1 PREPARATION OF INJECTABLE HYALURONIC ACID ESTERS The starting Hyaff hyaluronic acid (Fidia Advanced Biopolymers, Abano Terme, Italy) materials are solids such as non-woven pads, felts, sheets, powders, sponges, and microspheres. The Hyaff materials are esters of hyaluronic acid exhibiting various ester moities (e.g., benzyl, ethyl.propyl pentyl or larger molecules such as hydrocortisone or methyl prednislone, etc.) as well as various degrees of esterification (i.e., partial esters or complete esters). Partial esters of Hyaff are designated by percent esterfication ranging from 50-99 % (e.g., Hyaff-1 lp65, Hyaff-1 lp80, etc.), while complete esters are 100 % esters of hyaluronic acid (e.g., Hyaff-11). Hyaff gel classification used in supporting data is as follows and is followed by examples of select formulations: - Hyaff-11 gel: Hyaff- 11 non- woven pad transformed into gel with organic solvent to yield 10 % solids - Hyaff-11 /bicarbonate gel: Hyaff-11 gel mixed with sodium bicarbonate as pore former at 15:1 (w/w) bicarbonate to Hyaff- 11 - Hyaff-l 1/PEG gel: Hyaff-11 gel mixed with polyethylene glycol(200mw) as pore former at 33 - 50 % (v/v) range - Hyaff-11/TCP gel: Hyaff-11 gel mixed with 30 % w/v TCP - Hyaff- 11 bicarbonate/TCP gel : Hyaff- 11 /bicarbonate gel mixed with 30 % w/v TCP - Hyaff-11/PEG/TCP gel: Hyaff-11/PEG gel mixed with 30 % w/v TCP - Hyaff-1 lp80 gel: Hyaff-1 lp80 non-woven pad transformed into gel with organic solvent to yield 5 % solids - Hyaff-1 lp65 gel: Hyaff-1 lp65 non-woven pad hydrated with aqueous buffer to yield 6 - 15 % solids - Hyaff-1 lp65/TCP gel: Hyaff-1 lp65 gel mixed with 30 % w/v TCP Hyaff-1 lp65 non- woven pads were hydrated with glutamic acid buffer (pH 4.5) containing rhBMP-2 (0.1 mg/mL final cone.) to yield either 6 % - 15 % solids (w/v) and mixed thoroughly to form a paste. Hyaff-1 lp80 and Hyaff-1 1 non-woven pads were solubilized in N-methyl-pyπolidinone (NMP) or dimethyl sulfoxide(DMSO)to yield a 1 - 30 % w/v solution. These solutions were then mixed with either rhBMP-2-containing buffer (10 % v/v, 0.1 mg/mL rhBMP-2), or lyophilized rhBMP-2 (0.1 mg/mL) followed by the addition of various pore formers (polyethylene glycol, sodium bicarbonate, sucrose, NaCl, citric acid)and tricalcium phosphate (TCP). Particle size of solid pore formers and TCP used was < 600um, preferably <200umLiquid pore formers such as PEG(200mw) were mixed at 10-90% v/v ratios, and solid pore formers were mixed at 9:1 - 21 :1 (w/w) pore former to caπier ratios. TCP was mixed at 0.1-30% (w/v). TCP (45-125 micron particle size) was mixed thoroughly into rhBMP-2/Hyaff-l 1 or rhBMP-2/Hyaff-l lp65 gel at 30% (w/v). Separately, rhBMP-2 was adsorbed onto TCP first, followed by mixing with Hyaff-11 or Hyaff-1 lp65 gel.Formulations were chosen based on injectability through an 18 g needle. Micro structure was characterized by scanning electron microscopy (SEM). SEMS revealed varying degrees of pore structure and porosity. Hyaff-1 lp65 6% gel exhibited longer fibers than the 15% formulation; with both displaying a high level of porosity. Both Hyaff-11 and Hyaff-1 lp80 gels showed minimal pore structure and porosity, whereas those carriers with pore formers displayed a high level of porosity. Pore formers and/ or additives that yielded injectable mixtures were PEG, sodium bicarbonate and TCP. EXAMPLE 2 IN VITRO RELEASE KINETICS rhBMP-2 was radiolabeled with 125 I using the Iodogen method (Pierce) and used as a tracer for 0.1 mg/ml rhBMP-2 delivered in 100 ul Hyaff-l lp65 gel, Hyaff-1 lp80 gel, Hyaff- 1 lgel and Hyaff-11/PEG (n=4). 125 I-rhBMP-2 loaded samples (50,000 cpm/sample) were incubated in 1 ml fetal calf serum (Hy clone) at 37°C on a shaker, and radioactivity of the carrier measured up to 14 days using a gamma counter. Fresh serum was replaced after each time point. 125 I-rhBMP-2 release from injectable formulations were compared to those of implantable sponges and pads of Hyaff-11 and Hyaff-1 lp80. Auto cross-linked polysaccharide form of derivitized hyaluronic acid, ACP gel, is used for the in vitro release study and the rat ectopic assay. For the in vitro release study, 2 ml ACP gel is mixed with 1.53 mg rhBMP-2 cake (which coπesponds to 0.2 mg actual rhBMP-2 at 8 mg rhBMP-2 per 61 mg cake weight) and ,2 T-rhBMP-2 (100 ml total, 20 mCi/200 ml gel) and drawn up into 1 ml syringes resulting in approximately 10 % gel dilution. ACP gel for the rat ectopic study does not contain the tracer but is diluted with MRF-00906 buffer. 200 ml injections are performed using a 22 gauge needle. The final concentration of rhBMP-2 will be 0.1 mg/ml, or 20 mg per 200 ml injection. The final concentration of 125 I-rhBMP-2 will be approximately 20 mCi per 200 ml injection. The ACP gel will be injected at room temperature. In vitro release kinetics showed greatest retention of rhBMP-2 over the 2 weeks in the Hyaff-11/PEG gel followed by Hyaff-1 lp80 gel and Hyaff-11 gel (Fig. 1). Hyaff-l lp65 gel released rhBMP-2 the fastest. Sponges and pads of Hyaff-11 and Hyaff-1 lp80 retained less rhBMP-2 than Hyaff-11/PEG or Hyaff-1 lp80 gel, but more than Hyaff-1 lp65. Addition of TCP to Hyaff-11 gel increased rhBMP-2 retention. The release profile in all caπiers exhibited moderate to rapid burst release followed by a slow, sustained release of rhBMP-2. All Hyaff- 11 and Hyaff-1 lp80 gel formulations retained rhBMP-2 well (> 50 % remaining after 14 days) except Hyaff-1 lp65. EXAMPLE 3 RAT ECTOPIC ASSAY Hyaff-11 based gels (200 ul/site, n = 6) with 0.1 mg/ml rhBMP-2 were injected subcutaneously (ventral thorax) or injected intramuscularly (quadriceps) in 3-4 week old male Long Evans rats. Rats were sacrificed after 2 weeks and bone formation in the explants analyzed histologically using Goldners's trichrome stain. Bone scores (0= no bone, 5=100% bone) were assigned based on histomorphometry. Total bone (mm 3 ) was calculated using explant size and bone score. Radiographs of explants were also taken. All Hyaff-11 based gels formed significant ectopic bone in the rat model (Table 1) in the presence of rhBMP-2, although differences in bone formation existed between carrier types as confirmed by radiographs and histology. Hyaff-1 lp65 at varying doses (0.1-1.5 mg/mL) of rhBMP-2 exhibited a dose dependent increase in bone formation (and bone score) but was inconsistent in explant size which yielded less total bone (0.1 mg/mL rhBMP-2 data shown). Hyaff-1 lp80 explants were large but had a lower bone score, while Hyaff-11 showed good bone score and total bone. Hyaff-11/PEG and Hyaff-11 /sodium bicarbonate radiographically showed equivalent radioopacity as those of Hyaff-1 1 and Hyaff-1 lp80. Histologically, both Hyaff-1 1 and Hyaff-1 lp80 caπiers showed residual remaining matrix due to their slow degradation rates, although Hyaff- 1 lp65 completely degraded by 2 weeks. Bone formed within pores, shown by mineralizing osteoblasts as well as through a cartilage intermediate. Addition of TCP to Hyaff- 11 gel with or without pore formers also showed comparableradiographic evidence of bone formation as those of other Hyaff based gels. Table 1. Histomorphometry results of rat ectopic bone formation assay. EXAMPLE 4 IN VIVO BIODISTRIBUTION Retention of rhBMP-2 within each carrier was analyzed in vivo using a rabbit ulna fracture model. Bilateral 0.5 mm osteotomy defects were created in the ulna of New Zealand White rabbits and 150 uL rhBMP-2/caπier injected into the defect (n=8/group). Gels were loaded with 40 uCi 1 T labeled rhBMP-2 and 0.67 mg/ml unlabeled rhBMP-2. Amount of radioactivity retained at the fracture site was measured by gamma scintigraphy as a function of time. In vivo biodistribution of rhBMP-2 from Hyaff-11/PEG gel in the rabbit ulna fracture model showed better retention of rhBMP-2 than absorbable collagen sponge (ACS) and buffer caπier (MFR-842) (Fig. 2). Hyaff- 11/PEG retained approximately 40 % rhBMP-2 after 7 days. Hyaff-1 lp65 gel showed poorer retention of rhBMP-2 than Hyaff-11/PEG gel, but displayed comparable fracture callus radiographically. EXAMPLE 5 IN VITRO RELEASE KINETICS rhBMP-2 was radiolabeled with 125 I using the Iodogen method (Pierce) and used as a tracer for 0.1 mg/ml rhBMP-2 delivered in 100 uL Hyaff-1 1 gel ± TCP and Hyaff-1 lp65 gel ± TCP (n=4). 125 I-rhBMP-2 loaded samples (50,000 cpm/sample) were incubated in 1 mL fetal calf serum (Hyclone) at 37°C on a shaker, and radioactivity of the caπier measured up to 14 days using a gamma counter. Fresh serum was replaced after 1, 3, 7, and 14 days. Addition of TCP enhanced retention of rhBMP-2 over the course of 2 weeks in both Hyaff-11 and Hyaff-1 lp65 gels (Figure 3). Hyaff-11/TCP retained the most rhBMP-2, followed by Hyaff-11, Hyaff-1 lp65/TCP, and Hyaff-1 lp65. Hyaff-11 retained more rhBMP- 2 than Hyaff-1 lp65 due to its hydrophobicity and insolubility. Preadsorbing rhBMP-2 on TCP increased rhBMP-2 retention in Hyaff-11 gel, as opposed to mixing rhBMP-2 into the Hyaff- 11 phase. Preadsorbing or mixing rhBMP-2 into either TCP or Hyaff-1 lp65 phase resulted in similar rhBMP-2 retention, both of which were greater than Hyaff-1 lp65 without TCP. EXAMPLE 6 IN VIVO REDISTRIBUTION AND EFFICACY Retention of rhBMP-2 within Hyaff-11/TCP and Hyaff-1 lp65/TCP was analyzed in vivo using a rabbit ulna fracture model. Bilateral 0.5 mm osteotomy defects were created in the ulna of New Zealand White rabbits (n=3/carrier) and 150 uL carrier or buffer (0.67 mg/mL rhBMP-2) injected around the defect. 20 uCi 125 I-rhBMP-2 was used as a tracer. Amount of radioactivity left within each carrier at the fracture site was measured by gamma scintigraphy over the course of several weeks and in vivo rhBMP-2 retention calculated over time. Fracture repair efficacy was analyzed in these rabbits (n=8) by torsional biomechanical testing after a 4 week sacrifice to obtain maximum torque. Contralateral limbs served as surgical controls. In vivo retention of rhBMP-2 at the rabbit ulna fracture site showed a similar pattern as that of the in vitro study (Figure 4). Hyaff-11/TCP gel (rhBMP-2 adsorbed to TCP phase first) exhibited the greatest retention (40% remaining after 4 weeks) followed by Hyaff- 1 lp65/TCP gel (rhBMP-2 undetectable at 14 days) and buffer (undetectable at 7 days). rhBMP-2 accelerated fracture healing when delivered in Hyaff-1 lp65/TCP or Hyaff-1 lp65 gel. Maximum torque (N-m) for Hyaff-1 lp65/TCP and Hyaff-1 lp65 were significantly greater than their contralateral surgical controls (85.6% and 96.9%, respectively) but not statistically different from each other (Table 1). Table 1. Maximum torque (N-m) of rabbit ulna defects ier r h B M Control P value P-2 0.571 0.290 0.0001 ± 0.225 ± 0.158 /TCP 0.475 ± 0.197 0.256 ± 0.087 0.0091 The foregoing descriptions detail presently perfeπed embodiments of the present invention. Numerous modifications and variations in practice thereof are expected to occur to those skilled in the art upon consideration of these descriptions. Those modifications are believed to be encompassed within the claims appended hereto.

Claims: What is claimed is: 1. A composition for injectable delivery of osteogenic proteins comprising a pharmaceutically acceptable admixture comprising (a) an osteogenic protein; and (b) injectable hyaluronic acid derivitives. 2. The composition of claim 1 further comprising tricalcium phosphate. 3. The composition of claim 1 further comprising pore formers. 4. The composition of claim 1 wherein the osteogenic protein is selected from the group consisting of members of the BMP family. 5. The composition of claim 4 wherein the osteogenic protein is BMP-2. 6. The composition of claim 4 wherein the osteogenic protein is OP- 1. 7. A composition for injectable delivery of osteogenic proteins comprising a pharmaceutically acceptable admixture comprising (a) BMP-2; (b) an injectable hyaluronic acid derivitive; and (c) Tricalcium phosphate. 8. A composition providing an injectable matrix for osteogenic proteins comprising a hyaluronic acid derivitive. 9. A method for making an injectable hyaluronic acid derivitive comprising transforming insoluble or partially solublenon- woven pads or sponges of hyaluronic acid benzyl esters by hydration or solvent addition. 10. The method of claim 9 further comprising the introduction of pore formers to the solubilized caπiers.

Inventors: CALLEGARO LANFRANCO, KIM HYUN, LI REBECCA, PAVESIO ALESSANDRA, CALLEGARO, LANFRANCO, KIM, HYUN, LI, REBECCA, PAVESIO, ALESSANDRA
Applicants: FIDIA ADVANCED BIOLOGY, GENETICS INST, GENETICS INSTITUTE, INC.
Application year: 2000
Main classification: A61L27
IPC codes: A61K9, A61K38, A61K47, A61L27, A61P19