OPTIMIZING NANO-FILLER PERFORMANCE IN POLYMERS

Abstract: A polymer composite comprising a polymer matrix having, dispersed therein, a nano clay in combination with a crosslinking promotor. In method form, the invention relates to a process for enhancing the mechanical properties of a polymer composite, comprising supplying a polymer matrix, combining the matrix with a nano clay and a crosslinking promotor and crosslinking.

Description: OPTIMIZING NANO-FIL ER PERFORMANCE IN POLYMERS The present invention relates to nano clays for use in thermoplastic/ thermoset polymer materials, wherein the nano clay may be combined with another chemical ingredient, such as a crosslinking agent, to thereby provide a unique and overall synergistic effect on mechanical property performance. Polymer composites comprising a polymer matrix having one or more additives such as a particulate or fiber material dispersed throughout the continuous polymer matrix are well known. The additive is often added to enhance one or more properties of the polymer. Useful additives include inorganic layered materials such as talc, clays and mica of micron size. A number of techniques have been described for dispersing the inorganic layered material into a polymer matrix. It has been suggested to disperse individual layers, e.g., platelets, of the layered inorganic material, throughout the polymer. However, without some additional treatment, the polymer will not infiltrate into the space between the layers of the additive sufficiently and the layers of the layered inorganic material will not be sufficiently uniformly dispersed in the polymer. To provide a more uniform dispersion, as described in U.S. Pat. No. 4,889,895 sodium or potassium ions normally present in natural forms of mica-type silicates and other multilayered particulate materials are exchanged with organic cations (e.g., alkylammonium ions or suitably functionalized organosilanes) thereby intercalating the individual layers of the multilayered materials, generally by ionic exchange of sodium or potassium ions. This intercalation can render the normally hydrophilic mica-type silicates organophilic and expand its interlayer distance. Subsequently, the layered material (conventionally referred to as "nanofillers") is mixed with a monomer and/ or oligomer of the polymer and the monomer or oligomer polymerized. The intercalated silicate is described as having a layer thickness of 7 to 12 [Angstrom] and an interlayer distance of 30 [Angstrom] or above. In WO 93/11190, an alternative method for forming a composite is described in which an intercalated layered, particulate material having reactive organosilane compounds is dispersed in a thermoplastic polymer or vulcanizable rubber. Yet additional composites containing these so-called nanofillers and/ or their methods of preparation are described in U.S. Pat. Nos. 4,739,007; 4,618,528; 4,528,235; 4,874,728; 4,889,885; 4,810,734; 4,889,885, 4,810,734; and 5,385,776; German Patent 3808623; Japanese Patent J02208358, European Patent applications 0,398,551; 0,358,415; 0,352,042; and 0,398,551, and J. Inclusion Phenomena 5, 473 (1987); Clay Minerals, 23, (1988), 27; Polym Preprints, 32 (April 1991), 65-66; Polym. Prints, 28, (August 1987), 447-448; and Japan Kokai 76,109,998. Nano clay fillers are also available based on tiny platelets of a special type of surface modified clay called montmorillonite. These surface treatments have been aimed for use with nylon-6 and polypropylene. The two manufacturers in the United States, Nanocor and Southern Clay Products, both ' point to increases in flexural modulus, heat distortion temperature and barrier properties. Furthermore, attention is hereby directed to U.S. Patent Nos. 5,993,415 and 5,998,551 which, although not relating to nano clay fillers, describe the use of crosslinking promotors to improve properties of a thermoplastic material, and, as to be discussed below, are relevant to the present invention. Accordingly, the teachings of these patents are incorporated by reference. In sum, therefore, even with the numerous described composites and methods, it still remains desirable to have an improved composite and method for forming polymer composites derived from a multilayered additive (nano clays) to thereby create composites having improved properties over the polymer on its own. Accordingly, it is an object of this invention to explore the suitability of combining the nano clays with an additional chemical component to establish whether or not the observed mechanical properties of a thermoplastic host resin are improved beyond the use of only a nano clay filler. More specifically, it is an object of this invention to combine nano clays with a suitable crosslinking promotor, and to establish a synergistic effect of such promotors with the nano clay on the mechanical properties of a host thermoplastic matrix. In addition, it is an object of this invention to apply the nano clays and additional chemical component described above (promotor) to develop an improved method to prepare materials suitable for use in medical product applications, such as balloon catheters and catheter shaft production. By way of summary, the present invention comprises a composite comprising a polymer matrix having, dispersed therein, a nano clay in combination with a crosslinking promotor. By use of the term "nano clay" it is noted that such clays are inorganic minerals which have a high aspect ratio with at least one dimension of the particles therein in the nanometer range. By use of the term, "crosslinking promotor" it relates to any chemical compound that will promote crosslinking between those polymer chains that comprise the polymer matrix. Accordingly, it can be appreciate that "crosslinking promotors" include those functionalized chemical compounds that provide the requisite activity, upon activation (irradiation or heat) to chemical react and bond with the polymer chains to form covalent crosslinks between the surrounding polymer chains. Preferably, the crosslinking promotor is trallylisocyanurate or trallylcyanurate, although those skilled in the art will recognize that other types of crosslinking promotors would be suitable and would fall within the broad aspects of this invention. In addition, preferably, the promotor is present in the polymer matrix at a level of about 0.5% to 10% (wt.), and at any increment therebetween in 0.1 % increments. As noted, the nano clays are inorganic minerals with a high aspect ratio as one dimension of the particles therein falls in the nanometer range. A variety of references are available to those skilled in the art which discuss and describe nano clays suitable herein. In such regard, the clays having a plate structure and thickness of less than one nanometer are the clays of choice. The length and width of the clays may fall in the micron range. Aspect ratios of the preferred clays are in the 300:1 to 1,500: 1 range. In addition, the surface area of the exfoliated clays is preferably in the range of 700 m 2 /gram. Nano clays that may be suitable herein include hydrotalcite, montmorillonite, mica fluoride, octasilicate, and mixtures thereof. Nano clay is incorporated herein at a level of 1-10% (wt.) as well as any increment therebetween, in 0.1% increments. Montmorillonite nano clays have a plate like structure with a unit thickness of one nanometer or less. This clay also has an aspect ratio in the 1000:1 range. Because montmorillonite clay is hydrophilic, it is not compatible with most polymers and should be chemically modified to make its surface more hydrophobic. The most widely used surface treatments are amonium cations which can be exchanged for existing cations already on the surface of the clay. The treated clay is then preferably incorported into the polymer matrix herein, by melt mixing by extrusion, more preferably, twin- screw extrusion. In addition, at such time, and as noted above, the crosslinking promotor can also be readily combined with the clay during the melt mixing process. Those skilled in the art will therefore recognize that, in general, any type of melt mixing process can be applied to prepare the composites of the present invention, including extrusion, direct injection molding, the use of a two-roll mill, etc. With regards to the development of crosslinking herein, as noted, a crosslinking promotor is employed, and preferably, the formulations herein are exposed to irradiation. Preferably, the irradiation dosage is between about 1-20 MR, as well as any numerical value and/ or increment therein. In addition, the polymer matrix herein may be selected from any thermoplastic or thermoset type polymer resin host. A representative thermoplastic resin herein is a nylon resin, a nylon block copolymer, nylon block copolymers containing a polyamide block and an elastomeric block, engineering thermoplastic resins (e.g., polycarbonate, polyesters, polysulphones, polyketones, polyetherimides) as well as commodity type materials (polyethylene, polypropylene, polystyrene, poly(vinylchloride)) including thermoplastic elastomers. Representative thermoset materials include polyurethanes, epoxy polymers, etc. In method form, the present invention relates to the steps of supplying a polymer matrix, combining said matrix with a nano clay along with a crosslinking promotor. This combmation is then preferably exposed to irradiation to develop crosslinking. By the practice of such method, and as can be observed in the various working examples below, a synergistic influence of the promotor has been observed on the ability of the nano clay to improve the mechanical properties of a given polymer matrix. More specifically, in accordance with the invention herein, it has been found that should one combine a given polymer matrix with the nano clay, one will generally observe an increase in mechanical property performance, such as an increase in the flexural modulus. However, it has been found herein that upon incorporation of a crosslinking promotor, the effect of the nano clay is enhanced, in the sense that a synergy is observed as between the promotor and the nano clay on mechanical properties. As a consequence of all the above, the formulations of the present invention are particularly suitable for the development of an intravascular catheter having a tubular shaft comprising a nylon block copolymer and a nano clay filler, including a compound which promotes crosslinking therein, and a soft flexible tubular tip distal of and bonded to said shaft, the improvement comprising irradiation crosslinking said nylon block copolymer of said tubular shaft. The crosslinking is observed to increase the rigidity of the shaft relative to the soft distal tip. In addition, the present invention also relates to a balloon type catheter having a tubular shaft comprising a nylon block copolymer and a nano clay filler, including a compound which promotes crosslinking therein, the improvement comprising irradiation crosslinking said nylon block copolymer of the balloon section. Working Examples First Experiment The first experiment consisted of mixing the Nanocor 130 TGC clay and the southern Clay Closite 30B with Nylon 6 and with Nylon 6 and 3% TAIC. The Nylon 6 used with Allied's Capron B135 WP. The flex modulus did increase with the use of both clays as was anticipated. The increase with the use of a crosslinkng promotor was even greater, demonstrating a unique synergy as between the promotor and the nanoclay on mechanical properties. See Table I. Second Experiment The second experiment repeated the first experiment except that the Nylon 6 was replaced by PEBAX® 72 durometer polyamide ether block copolymer. In this case just adding the nano clay did not significantly increase the flex modulus. The surprise was the increase in flex modulus when crosslinking promotors, such as TAIC, was added to the PEBAX® and nano clay. The closite 30B shows the most improvement. A second unqiue effect was the increase in flex modulus when the combination was crosslinked. In fact the combination of PEBAX®, Closite (nano clay) and TAIC followed by crosslinking more than doubles the flex modulus. See Table II. Third Experiment The third experiment was similar to the first experiment noted above except the nylon-6 was replaced by nylon 12, AESNO® from Atochem. The improvements in flex modulus were much like the improvements with the PEBAX® in "Experiment Two", noted above. See Table III. Fourth Experiment The fourth experiment was similar to the third experiment noted above, except that nylon-12 was replaced by nylon-11, BMNO® from Atcohem. The improvements in flex modulus were much like the improvements with the PEBAX® in "Experiment Two". See Table IV. Fifth Experiment The fifth experiment was similar to the above, except that both low density and high density polyethylene were employed s the polymer matrix. An improvement in flex modulus was again observed due to the combination of nano clay and promotor (3% wt. TAIC). See Table V. NANO'S WITH XL-NYLON NYLON 12 TABLE III POLYMER FILLER FORMULATION FILLER % I IRRAA DDOOSSE BK-STRESS '.S 'TTRRAAIINN FLX-MOD NYLON 12 NONE AESNO 0 OMR 10.000 250 200.000 NYLON 12 CLOSITE 30B 29Λ 5 OMR 9.000 200 2D0.000 NYLON 12 3% TAIC CLOSITE 30B 28B 5 OMR 10.750 175 290,000 NYLON 12 3% TAIC CLOSITE 308 2SB $ 5MR 10.250 75 410.000 NYLON 12 3% TAIC CLOSITE 30B 2dB 5 10 R 10.100 50 420,000 NYLON 12 NANO-13 TC m 5 OMR 9,000 200 190.000 NYLON 12 3% TAIC NANO-130TC 29D 5 OMR 10,200 300 200.000 NYLON 12 3% TAIC NANO-130TC 29D 5 5MR 9,500 130 260,000 NYLON 12 3% TAIC NANO-130TC 29D 5 (OMR 9.C0O 125 260.000 NYLON 12 3% TAIC NONE 29F 0 5MR 8,000 75 220.000 ID NANO WITH XL-NYLON NYLON 11 TABLE IV POLYMER FILLER FORMULATION FILLER % IRA DOSE BK-STRESS 'ΛSTRA1N FLX-MOD NYLON 11 NONE BMNO 0 OMR 10,000 250 170,000 NYLON 11 3% TAIC CLOSITE 30B 28C 5 OMR 9,400 200 250.000 NYLON 1 1 3% TAIC CLOSITE 30B 26C 5 5MR 9,000 125 300.000 MYLO 11 3%TAJC CLOSITE 30B 28C 5 10MR 8,500 75 350,000 TABLE V NANO CLA Y IN HDPE & LDPE FLX-MOD POLYMER FILLER FORMULATION FILLER % IRA DOSE BK-STRESS %STRAIN FLX-MOD % INC HDPE NONE 3364 __ 0 OMR 2,317 47 73,602 0 HDPE CLOSITE 30B 30A 6 OMR 2,231 48 81,560 10.8 HDPE CLOSITE 30B 30A 6 5MR 1,734 32 94,853 28.9 HDPE CLOSITE 30B 30A 6 10MR 2,474 29 105,069 42.8 HDPE CLOSITE 30B 30A 6 15MR 2,866 28 111,026 50.8 HDPE CLOSITE 30B 30A 6 20MR 3,160 28 113,733 54.5 LDPE NONE 6005 0 OMR 1,016 49 21,295 0 LDPE CLOSITE 30B 30B 6 OMR 1.000 46 25,856 21.4 LDPE CLOSITE 30B 30B 6 5MR 1,434 33 29,339 37.8 LDPE CLOSITE 30B 30B 6 10MR 1,890 35 31,987 50.2 LDPE CLOSITE 30B 30B 6 15MR 2085 38 31.688 48.8 LDPE CLOSITE 30B 30B 6 20MR 2,034 30 32,864 54.3

Claims: What is claimed is: 1. A polymer composite comprising a polymer matrix having, dispersed therein, a nano clay in combination with a crosslinking promotor. 2. The composite of claim 1, wherein said crosslinking promotor is a chemical compound which promotes crosslinking between polymer chains upon exposure to irradiation. 3. The composite of claim 1 wherein said crosslinking promotor is triallylisocyanurate or triallylcyanurate. 4. The composite of claim 1 wherein said crosslinking promotor is present at a level of about 0.5 to 10 % (wt). 5. The composite of claim 1 wherein said nano clay is present at a level of about 1 to 10 % (wt). 6. The composite of claim 1 wherein said polymer matrix is a thermoplastic polymer or thermoset polymer. 7. The composite of claim 1 wherein said polymer matrix is a polyamide polymer or a polyamide copolymer comprising a polyamide block and an elastomeric block. 8. The composite of claim 7 wherein said polyamide block is a nylon-6, nylon-6,6, nylon-11, nylon-12, copolymers of nylon-6/ nylon-11, copolymers of nylon-6/ nylon-12 or mixtures thereof. 9. The composite of claim 7 wherein said elastomeric block is selected from a polyether, polyester, hydrocarbon, polysiloxane or mixtures thereof. 10. A composite comprising a polymer matrix having, dispersed therein, a nano clay in combination with a crosslinking promotor, wherein said matrix is irradiation crosslinked. 11. A method for enhancing the mechanical properties of a polymer composite, comprising: (a) supplying a polymer matrix; (b) combining said matrix with a nano clay and a crosslinking promotor; and (c) irradiating the combination of step (b) and crosslinking. 12. The method of claim 11 wherein said polymer matrix comprises polymer chains, said promotor is a chemical compound that absorbs irradiation and becomes chemically reactive to form crosslinks, and wherein said crosslinks comprise covalent bonds between said polymer chains. 13. The method of claim 12, wherein said irradiation is 5, 10, 15 or 20 megarads. 14. In an intravascular catheter having a tubular shaft comprising a nylon block copolymer and a soft flexible tubular tip distal of and bonded to said shaft, the improvement comprising adding a nano clay filler and a compound which promotes crosslinking therein to said nylon block copolymer forming said shaft, and irradiation crosslinking said nylon block copolymer of said tubular shaft. 15. In a balloon type catheter having a tubular shaft comprising a nylon block copolymer and an integrally formed balloon section, the improvement comprising adding a nano clay filler and a compound which promotes crosslinking therein to said nylon block copolymer forming said balloon, and irradiation crosslinking said nylon block copolymer of the balloon section.

Inventors: ACQUARULO LAWRENCE A JR, ACQUARULO, LAWRENCE, A., JR.
Applicants: ACQUARULO LAWRENCE A JR, NEIL CHARLES O, XU JIANWEI, ACQUARULO, LAWRENCE, A., JR., O'NEIL, CHARLES, XU, JIANWEI
Application year: 2000
Main classification: C08J3
IPC codes: C08K3, C08K5