Process for the dehydrogenation of a hydrocarbon feed stock

Abstract: Process for the dehydrogenation of a hydrocarbon feed comprising a step of dehydrogenating the hydrocarbon feed and a step of removing hydrogen being formed by dehydrogenation reactions, wherein the dehydrogenation and hydrogen removal steps are performed simultaneously in presence of a dehydrogenation catalyst being combined with a metal compound being reduced in presence of hydrogen.

Description: FIELD OF THE INVENTION The present invention relates to a process for dehydrogenation of a hydrocarbon feedstock by contacting the feed at elevated temperature with a dehydrogenation catalyst. More particularly, the invention provides a method for in-situ removal of hydrogen by addition of a metal oxide capable of releasing oxygen at reducing conditions and able to uptake oxygen at oxidation conditions. PRIOR ART A number of processes comprising dehydrogenation reactions are known in the art. In general, these processes suffer from a number of disadvantages including low yield of the desired product due to thermodynamic limitation. In addition, the need for addition of large amounts of heat limits the conversion to the desired product. These processes are disclosed in e.g. US Patent No. 4,914,075; Dunn R.O. et al. (Proceedings, DeWitt Petrochemical Review, Houston, Texas, 1992, 01); Wilcher F.P. et al. (Proceedings, DeWitt Petrochemical Review, Houston, Texas, 1990, T1) and in US Patent No. 4,746,643. The known processes for selective removal of hydrogen in a hydrocarbon stream apply a separate stage for the removal of hydrogen. Typically removal of hydrogen is performed by interstage contacting of a partially dehydrogenated stream mixed with oxygen with a noble metal catalyst. Examples of this technology are given in US Patent Nos. 4,418,237, 4,435,607, 4,788,371 and 4,886,928. The limitation of the above mentioned interstage removal of hydrogen is, besides oxidation of hydrogen in presence of oxygen, it may also effect oxidation of the organic compounds present with formation of carbon dioxide and carbon monoxide as a result. Most dehydrogenation technologies involve at least two steps. A dehydrogenation step where the dehydrogenation catalyst is contacted with a feed of hydrocarbons and a regeneration step where the catalyst is contacted with a feed containing oxygen. Thus, in the dehydrogenation step the reduction potential is high, whereas in the oxidation step the oxidation potential is high. It is known that many metal oxides are reduced with hydrogen and reoxidised in presence of oxygen at elevated temperature. Such metal oxides are in the following termed redox-oxides. In the above mentioned dehydrogenation cycles these redox-oxides can be reduced in the dehydrogenation step by reaction of metal lattice oxygen with hydrogen forming water, and oxidised in the oxidation step by reaction with oxygen. By mixing the dehydrogenation catalyst with the redox-oxide and contacting the catalyst and the redox-oxide with a feed containing organic compounds, it is possible to convert organic compound(s) by dehydrogenation reactions that are beyond the known thermodynamic limitation. An example of such application limited to redox-oxide of the perovskites type is given in European Patent Publication No. 558,148 A1. Simultaneous dehydrogenation of a hydrocarbon feed and adsorption or oxidation of formed hydrogen is furthermore disclosed in WO 94/05608. Suitable catalyst mentioned for use in the process is any reducible oxide or hydrogen adsorber selected from 1B, IIB or VIII metals. SUMMARY OF THE INVENTION In accordance with the above findings this invention is a process for the dehydrogenation of a hydrocarbon feed comprising simultaneous dehydrogenation of the hydrocarbon feed and removal of hydrogen being formed during dehydrogenation in presence of a dehydrogenation catalyst being combined with a metal compound which is reduced in presence of hydrogen, wherein the metal compound is vanadium phosphate. In the process of the invention, hydrogen, which is formed upon dehydrogenation of organic compound(s), is oxidised by a redox-oxide with high selectivity providing a higher overall conversion and selectivity of the dehydrogenation process. Catalysts being active in the dehydrogenation of hydrocarbon compounds are conventionally in the art and known from the literature including the above mentioned patent publications. In general, any metal compound being able reversibly to change state of oxidation at process conditions employed in the process will be useful as redox metal compound in the inventive process for the removal of formed hydrogen. Those redox metal compounds include oxidic metal compounds and metal oxides. The combined dehydrogenation and vanadium phosphate catalysts may be prepared by conventional methods known in the art, e.g. physically admixing particles of the dehydrogenation catalyst with the redox metal compound or co-precipitation of the components and optionally with calcination in air. Example 1 A quartz fluid-bed reactor was charged with 100 ml of a dehydrogenation catalyst sample of a chromium-on-alumina catalyst. The catalyst was in form of spheres with an average particle size of 70 µm. The reactor was operated at a pressure slightly above atmospheric pressure and in a cyclic mode with the following steps: 1. Oxidation in air at 650°C, 30 min. 2. Purge with nitrogen at 650°C, 15 min. 3. Reduction with CH4 at 650°C, 4 min. 4. Cooling with nitrogen from 650°C to 580°C, 15 min. 5. Dehydrogenation of i-butane at 550-580°C, 15 min. 6. Purge with nitrogen, 15 min. Steps 1 to 6 were repeated several times and the temperature in the dehydrogenation step was varied. As a comparison example, pure dehydrogenation catalyst was used. The feed flow in the dehydrogenation step was 40 Nl/h. The exit gas from both oxidation step and the following purge step was collected in a bag. In a separate bag the exit gas from the dehydrogenation step and the following purge step was collected. The composition of the gas in the two bags was analysed by gas chromatography. The results are given in Table 1. Example 2 After addition of 2% wt of silica coated vanadium phosphorous redox-oxide the tests described under Example 1 were repeated. The results are given in Table 1. Example 3 After addition of 5% wt of silica coated vanadium phosphorous redox-oxide the tests described under Example 1 were repeated. The results are given in Table 1. i-butane dehydrogenation Experiment Temperature °C Conversion %wt Selectivity %wt 1 Pure dehydrogenation 550 41,15 91,20 1 Pure dehydrogenation 560 44,91 89,79 1 Pure dehydrogenation 570 49,48 87,14 1 Pure dehydrogenation 580 54,05 83,17 2 +2%wt redox-oxide 550 39,57 94,30 2 +2%wt redox-oxide 560 43,39 93,51 2 +2%wt redox-oxide 570 47,60 92,10 2 +2%wt redox-oxide 580 52,13 90,18 2 +2%wt redox-oxide 590 56,35 87,86 3 +5%wt redox-oxide 560 39,59 93,94 3 +5%wt redox-oxide 570 44,70 92,87 3 +5%wt redox-oxide 580 49,39 92,03 Example 4 A quartz fluid-bed reactor was charged with 100 ml of a dehydrogenation catalyst sample of a chromium-on-alumina catalyst. The catalyst was in form of spheres with an average particle size of 70 µm. The reactor was operated at a pressure slightly above atmospheric pressure and in a cyclic mode with the following steps oxidation in air at 650°C, 30 min: 1. Purge with nitrogen at 650°C, 15 min. 2. Dehydrogenation of propane at 550-620°C, 15 min. 3. Purge with nitrogen, 15 min. The steps 1 to 4 were repeated several times and the temperature in the dehydrogenation step was varied. As a comparison example the pure dehydrogenation catalyst was used. The feed flow in the dehydrogenation step was 52 Nl/h. The exit gas from both oxidation step and the following purge step was collected in a bag. In a separate bag the exit gas from the dehydrogenation step and the following purge step was collected. The composition of the gas in the two bags was analysed by gas chromatography. The results are given in Table 2. Example 5 After addition of 5% wt of silica coated vanadium phosphorous redox-oxide the experiments described under Example 4 were repeated. The results are given in Table 2. Example 6 After addition of 10% wt of silica coated vanadium phosphorous redox-oxide the experiments described under Example 4 were repeated. The results are given in Table 2. Propane dehydrogenation Experiment Temperature °C Conversion %wt Selectivity %wt 4 Pure dehydrogenation 575 45,31 63,53 5 +5%wt redox-oxide 575 30,80 86,12 5 +5%wt redox-oxide 605 43,67 75,09 5 +5%wt redox-oxide 612 46,42 73,89 6 +10%wt redox-oxide 612 38,59 62,52

Claims: Process for the dehydrogenation of a hydrocarbon feed comprising simultaneous dehydrogenation of the hydrocarbon feed and removal of hydrogen being formed during dehydrogenation in presence of a dehydrogenation catalyst being combined with a metal compound, which is reduced in presence of hydrogen, characterised in that the metal compound is vanadium phosphate. Process of claim 1, characterised in that vanadium phosphate is combined with the dehydrogenation catalyst in form of a physical mixture Process of claim 1, characterised in that the vanadium phosphate is combined with the dehydrogenation catalyst by coprecipation of corresponding precursor material and thermal treatment.

Inventors: BLOM NIELS JORGEN, NIELSEN POUL ERIK, PERREGAARD JENS, STAHL ANNI, BLOM, NIELS JORGEN, NIELSEN, POUL ERIK, PERREGAARD, JENS, STAHL, ANNI, NIELSEN, POUL ERIK HOJLUND
Applicants: TOPSOE HALDOR AS, HALDOR TOPSOE A/S
Application year: 2000
Main classification: C07C5
IPC codes: B01J27, C07C11, B01J23, C07B35, C07B61, C07C5