COMPOSITION AND METHOD FOR COLOR IMPROVEMENT OF NITROXYL CONTAINING POLYMERS

Abstract: The invention relates to a composition comprising, a) at least one oligomer, cooligomer, polymer or copolymer or blends thereof, containing a stable free nitroxyl radical (1); and b) a reducing agent; with the proviso that the composition is essentially free of a polymerizable monomer. A further subject is a process for improving the color of an oligomer, cooligomer, polymer or copolymer or blends thereof, containing a stable free nitroxyl radical (1); by adding a reducing agent to said polymer and heating said mixture to above the glass temperature in case of amorphous polymers or above the melting point in case of crystalline or semi-crystalline polymers.

Description: Composition and Method for Color Improvement of Nitroxyl Containing Polymers The invention relates to a composition and process for color improvement of nitroxyl or nitroxyl ether containing polymers. Stable free nitroxyl radicals or nitroxyl ethers are for example useful in controlled free radical polymerization (CFRP) and by this way incorporated into the polymer in a significant amount, leading in some cases to slightly colored polymers. Controlled free radical polymerization (CFRP) of ethylenically unsaturated monomers has attracted continuing attention, because of its capability to produce polymers with narrow molecular weight distributions and controlled architecture such as block copolymers. US-A-4 581 429 to Solomon et al., issued April 8, 1986, discloses a free radical polymerization process which controls the growth of polymer chains to produce short chain or oligo- meric homopolymers and copolymers, including block and graft copolymers. The process employs an initiator having the formula (in part) R'R"N-O-X, where X is a free radical species capable of polymerizing unsaturated monomers. The reactions typically have low conversion rates. Specifically mentioned radical R'R"N-O« groups are derived from 1 ,1 ,3,3 tetraethylisoindoline, 1 ,1 ,3,3 tetrapropylisoindoline, 2,2,6,6 tetramethylpiperidine, 2,2,5,5 tetramethylpyrrolidine or di-t-butylamine. US 5322912 to Georges et al. issued June 21 , 1994 discloses a polymerization process using a free radical initiator, a polymerizable monomer compound and a stable free radical agent of the basic structure R'R"N-O« for the synthesis of homopolymers and block copolymers. WO 98/13392 describes open chain alkoxyamine compounds which have a symmetrical substitution pattern and are derived from NO gas or from nitroso compounds which are suitable regulators for this type of radical polymerization. EP-A-621 878 and EP-A-735 052 disclose a method for preparing thermoplastic polymers of narrow polydispersities by free radical-initiated polymerization, which comprises adding a free radical initiator and a stable free radical agent to the monomer compound. WO 96/24620 describes a polymerization process in which very specific stable free radical agents are used, such as for example , bearing a hydrogen atom in α-position to the nitrogen atom. WO 98/30601 discloses specific nitroxyls based on imidazolidinones, which are also useful for stable free radical mediated polymerization. In addition WO 98/44008 discloses specific nitroxyls based on morpholinones, piperazinones and piperazinediones. All nitroxyl radicals useful in such controlled polymerization processes have inherently a reddish color. Polymers made in the presence of such stable nitroxyl radicals or nitroxyl ethers are end- capped by the nitroxyl group. The bond, polymer to nitroxyl group however is a labile bond, which cleaves upon heating, liberating again the nitroxyl radical and giving thus color to the polymer. The color formation depends, therefore, on the concentration of nitroxyl radical / nitroxylether used to synthesize the polymer. As many processing conditions include a heating step, e. g. removing not reacted monomer, shaping parts by extrusion, injection molding, blow molding and the like, undesirable discoloration accompanies these processes. The problem underlying the present invention is to counteract discoloration resulting from stable free nitroxyl radicals. This problem is solved by adding a reducing agent to the polymer, preferably during a processing step, such as extrusion or injection molding One subject of the invention is a composition comprising, a) at least one oligomer cooligomer, polymer or copolymer or blends thereof containing a \ stable free nitroxyl radical N— O« , and b) a reducing agent, with the proviso that the composition is essentially free of a polymeπzable monomer Essentially free of a polymenzable monomer means that in some cases there may be a small amount of monomer left from manufacturing the polymer, which could not be completely removed Preferably no monomer at all is present Usually the excess monomer is present in an amount of a few ppm The nitroxyl radical may be present due to its admixture during polymerization, due to its admixture for monomer stabilization, due to its use as chain stopping agent or due to a grafting reaction after polymerization has been completed The nitroxyl radical may be present as a mixture with the polymer or it may be partially bound to the polymer The polymers, copolymers, oligomers or cooligomers which can be used in the present invention are listed below 1 Polymers of monoolefins and diolefins, for example polypropylene, polyisobutylene, po- lybut-1-ene, poly-4-methylpent-1-ene, polyisoprene or polybutadiene, as well as polymers of cycloolefins, for instance of cyclopentene or norbornene, polyethylene (which optionally can be crosshnked), for example high density polyethylene (HDPE), high density and high molecular weight polyethylene (HDPE-HMW), high density and ultrahigh molecular weight polyethylene (HDPE-UHMW), medium density polyethylene (MDPE), low density polyethylene (LDPE), linear low density polyethylene (LLDPE), (VLDPE) and (ULDPE) Polyolefins, i e the polymers of monoolefins exemplified in the preceding paragraph, preferably polyethylene and polypropylene, can be prepared by different, and especially by the following, methods a) radical polymerisation (normally under high pressure and at elevated temperature) b) catalytic polymerisation using a catalyst that normally contains one or more than one metal of groups IVb, Vb, Vlb or VIII of the Periodic Table These metals usually have one or more than one ligand, typically oxides, halides, alcoholates, esters, ethers, amines, alkyls, alkenyls and/or aryls that may be either p- or s-coordinated These metal complexes may be in the free form or fixed on substrates, typically on activated magnesium chloride, tιtanιum(lll) chloride, alumina or silicon oxide These catalysts may be soluble or insoluble in the polymerisation medium The catalysts can be used by themselves in the polymerisation or further activators may be used, typically metal alkyls, metal hydrides, metal alkyl halides, metal alkyl oxides or metal alkyloxanes, said metals being elements of groups la, lla and/or Ilia of the Periodic Table The activators may be modified conveniently with further ester, ether, amine or silyl ether groups These catalyst systems are usually termed Phillips, Standard Oil Indiana, Ziegler (-Natta), TNZ (DuPont), metallocene or single site catalysts (SSC) 2 Mixtures of the polymers mentioned under 1), for example mixtures of polypropylene with polyisobutylene, polypropylene with polyethylene (for example PP/HDPE, PP/LDPE) and mixtures of different types of polyethylene (for example LDPE/HDPE) 3 Copolymers of monoolefins and diolefins with each other or with other vinyl monomers, for example ethylene/propylene copolymers, linear low density polyethylene (LLDPE) and mixtures thereof with low density polyethylene (LDPE), propylene/but-1-ene copolymers, propylene/isobutylene copolymers, ethylene/but-1-ene copolymers, ethylene/hexene copolymers, ethylene/methylpentene copolymers, ethylene/heptene copolymers, ethylene/octene copolymers, propylene/butadiene copolymers, isobutylene/isoprene copolymers, ethy- lene/alkyl acrylate copolymers, ethylene/alkyl methacrylate copolymers, ethylene/vinyl acetate copolymers and their copolymers with carbon monoxide or ethylene/acry c acid copolymers and their salts (lonomers) as well as terpolymers of ethylene with propylene and a diene such as hexadiene, dicyclopentadiene or ethylidene-norbornene, and mixtures of such copolymers with one another and with polymers mentioned in 1) above, for example polypropylene/ethylene-propylene copolymers, LDPE/ethylene-vinyl acetate copolymers (EVA), LDPE/ethylene-acry c acid copolymers (EAA), LLDPE/EVA, LLDPE/EAA and alter- nating or random polyalkylene/carbon monoxide copolymers and mixtures thereof with other polymers for example polyamides 4 Polystyrene, poly(p-methylstyrene), poly(α-methylstyrene) 5 Copolymers of styrene or α-methylstyrene with dienes or acrylic derivatives, for example styrene/butadiene, styrene/acrylonitnle, styrene/alkyl methacrylate, styrene/butadiene/alkyl acrylate, styrene/butadiene/alkyl methacrylate, styrene/maleic anhydride, styrene/acryloni- tπle/methyl acrylate, mixtures of high impact strength of styrene copolymers and another polymer, for example a polyacrylate, a diene polymer or an ethylene/propylene/diene terpo- lymer, and block copolymers of styrene such as styrene/butadiene/styrene, styrene/iso- prene/styrene, styrene/ethylene/butylene/styrene or styrene/ethylene/propylene/ styrene 6 Graft copolymers of styrene or α-methylstyrene, for example styrene on polybutadiene, styrene on polybutadiene-styrene or polybutadiene-acrylonitπle copolymers, styrene and acrylonitnle (or methacrylonitπle) on polybutadiene, styrene, acrylonitnle and methyl methacrylate on polybutadiene, styrene and maleic anhydride on polybutadiene, styrene, acrylonitnle and maleic anhydride or maleimide on polybutadiene, styrene and maleimide on polybutadiene, styrene and alkyl acrylates or methacrylates on polybutadiene, styrene and acrylonitnle on ethylene/propylene/diene terpolymers, styrene and acrylonitnle on polyalkyl acrylates or polyalkyl methacrylates, styrene and acrylonitnle on acrylate/butadiene copolymers, as well as mixtures thereof with the copolymers listed under 6), for example the copolymer mixtures known as ABS, MBS, ASA or AES polymers 7 Polymers derived from α,β-unsaturated acids and derivatives thereof such as polyacry- lates and polymethacrylates, polymethyl methacrylates, polyacrylamides and polyacryloni- triles, impact-modified with butyl acrylate 8 Copolymers of the monomers mentioned under 7) with each other or with other unsaturated monomers, for example acrylonitnle/ butadiene copolymers, acrylonitnle/alkyl acrylate copolymers, acrylonitrile/alkoxyalkyl acrylate or acrylonitnle/vinyl halide copolymers or acrylonitnle/ alkyl methacrylate/butadiene terpolymers 9 Polymers derived from unsaturated alcohols and amines or the acyl derivatives or acetals thereof, for example polyvinyl alcohol, polyvinyl acetate, polyvinyl stearate, polyvinyl benzoate, polyvinyl maleate, polyvinyl butyral, polyallyl phthalate or polyallyl melamine, as well as their copolymers with olefins mentioned in 1 ) above. 10. Homopolymers and copolymers of cyclic ethers such as polyalkylene glycols, polyethylene oxide, polypropylene oxide or copolymers thereof with bisglycidyl ethers. 11. Polyacetals such as polyoxymethylene and those polyoxymethylenes which contain ethylene oxide as a comonomer; polyacetals modified with thermoplastic polyurethanes, acrylates or MBS. 12. Polyphenylene oxides and sulfides, and mixtures of polyphenylene oxides with styrene polymers or polyamides. 13. Polyurethanes derived from hydroxyl-terminated polyethers, polyesters or polybutadi- enes on the one hand and aliphatic or aromatic polyisocyanates on the other, as well as precursors thereof. 14. Polyamides and copolyamides derived from diamines and dicarboxylic acids and/or from aminocarboxylic acids or the corresponding lactams, for example polyamide 4, polyamide 6, polyamide 6/6, 6/10, 6/9, 6/12, 4/6, 12/12, polyamide 11 , polyamide 12, aromatic polyamides starting from m-xylene diamine and adipic acid; polyamides prepared from hexamethylenediamine and isophthalic or/and terephthalic acid and with or without an elastomer as modifier, for example poly-2,4,4,-trimethylhexamethylene terephthalamide or poly- m-phenylene isophthalamide; and also block copolymers of the aforementioned polyamides with polyolefins, olefin copolymers, ionomers or chemically bonded or grafted elastomers; or with polyethers, e.g. with polyethylene glycol, polypropylene glycol or polytetramethylene glycol; as well as polyamides or copolyamides modified with EPDM or ABS; and polyamides condensed during processing (RIM polyamide systems). 15. Polyureas, polyimides, polyamide-imides, polyetherimids, polyesterimids, polyhydantoins and polybenzimidazoles. 16 Polyesters derived from dicarboxylic acids and diols and/or from hydroxycarboxylic acids or the corresponding lactones, for example polyethylene terephthalate, polybutylene terephthalate, poly-1 ,4-dιmethylolcyclohexane terephthalate and polyhydroxybenzoates, as well as block copolyether esters derived from hydroxyl-terminated polyethers, and also polyesters modified with polycarbonates or MBS. 17. Polycarbonates and polyester carbonates. 18. Polysulfones, polyether sulfones and polyether ketones. 19. Blends of the aforementioned polymers (polyblends), for example PP/EPDM, Poly- amide/EPDM or ABS, PVC/EVA, PVC/ABS, PVC/MBS, PC/ABS, PBTP/ABS, PC/ASA, PC/PBT, PVC/CPE, PVC/acrylates, POM/thermoplastic PUR, PC/thermoplastic PUR, POM/acrylate, POM/MBS, PPO/HIPS, PPO/PA 6.6 and copolymers, PA/HDPE, PA/PP, PA/PPO, PBT/PC/ABS or PBT/PET/PC. Preferred is a composition, comprising a) at least one oligomer, cooligomer, polymer or copolymer, obtained by radical polymerization, which polymerization has been carried out in \ the presence of a stable free nitroxyl radical N— O« and a source of free radicals \ capable of initiating polymerization, or in the presence of a nitroxyl ether N— O — X , / wherein X represents a group having at least one carbon atom and is such that the free \ radical derived from X is capable of initiating polymerization and the remaining N— O« radical forms a stable free nitroxyl radical; and b) a reducing agent; with the proviso that the composition is essentially free of a polymerizable monomer. As mentioned before controlled free radical polymerization of ethylenically unsaturated monomers in the presence of nitroxyl radicals or nitroxyl ethers is a known process described in numerous prior art documents Stable free radicals having a structural element l \j _Q. are for example disclosed in EP-A-621 878. / Further examples such as are given in WO 96/24620 and WO 00/53640. Further examples are: Initiator/regulator compounds containing a structural element r^j Q X are ' n principal known. Suitable compounds and their manufacture are for example described in US 4 581 429, US 5 721 320, US 5627 248, WO 98/13392 , WO98/30601 or in WO 98/44008. Further suitable initiator/regulator compounds and their preparation are described in GB 2 335 190. Further suitable individual prior art compounds are for example Particularly suitable compounds are listed in Table 1. Another preferred class of initiator/regulator compounds is described in the British patent application GB 2 342 649 . Typically the ethylenically unsaturated monomer or oligomer usefull in controlled polymerization processes is selected from the group consisting of ethylene, propylene, n- butylene, i-butylene, styrene, substituted styrene, conjugated dienes, acrolein, vinyl acetate, vinylpyrrolidone, vinylimidazole, maleic anhydride, (alkyl)acrylic acidanhydrides, (alkyl)acrylιc acid salts, (alkyl)acrylic esters, (meth)acrylonitriles, (alkyl)acrylamides, vinyl halides or vinylidene halides. Preferred ethylenically unsaturated monomers are ethylene propylene n-butylene i- butylene isoprene 1 3-butadιene α-C 5 -Cι 8 alkene styrene α-methyl styrene, p-methyl styrene or a compound of formula CH 2 =C(R a )-(C=Z)-R b wherein R a is hydrogen or C r C 4 alkyl R is NH 2 , O (Me + ) glycidyl, unsubstituted d-C^alkoxy, C 2 -C 10 oalkoxy interrupted by at least one N and/or O atom, or hydroxy-substituted unsubstituted C C 18 alkylamιno, hydroxy-substituted CrCι 8 alkylamιno or hydroxy- substituted dι(Cι-C 18 alkyl)amιno, -O-CH 2 -CH 2 -N(CH 3 ) 2 or -O-CH 2 -CH 2 -N + H(CH 3 ) 2 An , An is a anion of a monovalent organic or inorganic acid, Me is a monovalent metal atom or the ammonium ion Z is oxygen or sulfur Examples of acids from which the anion An is derived are d-C^carboxyhc acids, organic sulfonic acids such as CF 3 SO 3 H or CH 3 SO 3 H, mineralic acids such as HCI, HBr or HI, oxo acids such as HCIO or complex acids such as HPF 6 or HBF 4 Examples for R a as C 2 -C 10 oalkoxy interrupted by at least one O atom are of formula phenyl or phenyl substituted by C r C 18 alkyl, R d is hydrogen or methyl and v is a number from 1 to 50 These monomers are for example derived from non ionic surfactants by acrylation of the corresponding alkoxylated alcohols or phenols The repeating units may be derived from ethylene oxide, propylene oxide or mixtures of both Further examples of suitable acrylate or methacrylate monomers are given below An or An , wherein An and R a have the meaning as defined above and R e is methyl or benzyl An is preferably Cl , Br or 0 3 S-CH 3 Further acrylate monomers are Examples for suitable monomers other than acrylates are Preferably R a is hydrogen or methyl, R is NH 2 , gycidyl, unsubstituted or with hydroxy substituted C 1 -C 4 alkoxy, unsubstituted d-Cialkylamino, di(C 1 -C 4 alkyl)amino, hydroxy- substituted Cι-C alkylamino or hydroxy-substituted di(C 1 -C alkyl)amino;and Z is oxygen. Particularly preferred ethylenically unsaturated monomers are styrene methylacrylate ethylacrylate butylacrylate isobutylacrylate tert butylacrylate hydroxyethylacrylate hydroxypropylacrylate, dimethylaminoethylacrylate glycidylacrylates methyl(meth)acrylate ethyl(meth)acrylate, butyl(meth)acrylate hydroxyethyl(meth)acrylate, hydroxypropyl(meth)acrylate, dιmethylamιnoethyl(meth)acrylate, glycιdyl(meth)acrylates, acrylonitnle, acrylamide, methacrylamide or dimethylaminopropyl-methacrylamide The polymerization process may be carried out in the presence of an organic solvent or in the presence of water or in mixtures of organic solvents and water Additional cosolvents or surfactants, such as glycols or ammonium salts of fatty acids, may be present Other suitable cosolvents are described hereinafter If organic solvents are used, suitable solvents or mixtures of solvents are typically pure alkanes (hexane, heptane, octane, isooctane), aromatic hydrocarbons (benzene, toluene, xylene), halogenated hydrocarbons (chlorobenzene), alkanols (methanol, ethanol, ethylene glycol, ethylene glycol monomethyl ether), esters (ethyl acetate, propyl, butyl or hexyl acetate) and ethers (diethyl ether, dibutyl ether, ethylene glycol dimethyl ether), or mixtures thereof The aqueous polymerization reactions can be supplemented with a water-miscible or hydrophilic cosolvent to help ensure that the reaction mixture remains a homogeneous single phase throughout the monomer conversion Any water-soluble or water-miscible cosolvent may be used, as long as the aqueous solvent medium is effective in providing a solvent system which prevents precipitation or phase separation of the reactants or polymer products until after all polymerization reactions have been completed Exemplary cosolvents useful in the present invention may be selected from the group consisting of aliphatic alcohols, glycols, ethers, glycol ethers, pyrrolidines, N-alkyl pyrrolidinones, N-alkyl pyrrolidones, polyethylene glycols, polypropylene glycols, amides, carboxylic acids and salts thereof, esters, organosulfides, sulfoxides, sulfones, alcohol derivatives, hydroxyether derivatives such as butyl carbitol or cellosolve, ammo alcohols, ketones, and the like, as well as derivatives thereof and mixtures thereof Specific examples include methanol, ethanol propanol, dioxane, ethylene glycol, propylene glycol, diethylene glycol, glycerol, dipropylene glycol, tetrahydrofuran, and other water-soluble or water-miscible materials, and mixtures thereof When mixtures of water and water-soluble or water-miscible organic liquids are selected as the aqueous reaction media, the water to cosolvent weight ratio is typically in the range of about 100 0 to about 10 90 Furthermore CFRP is particularly useful for the preparation of block copolymers Block copolymers are, for example, block copolymers of polystyrene and polydienes or polyacrylates (e.g., poly(styrene-b-butadiene), poly(styrene-b-isoprene), poly(styrene-b- acrylate) or poly(styrene-D-acrylate-o-styrene). They are usefull as adhesives or as compatibilizers for polymer blends or as polymer toughening agents. Poly(methylmethacrylate-D-acrylate) diblock copolymers or poly(methylacrylate-b-acrylate-o- methacrylate) triblock copolymers) are useful as dispersing agents for coating systeme, as coating additives (e.g. rheological agents, compatibilizers, reactive diluents) or as resin component in coatings(e.g. high solid paints) Block copolymers of styrene, (meth)acrylates and/or acrylonitnle are useful for plastics, elastomers and adhesives. Block copolymers prepared by CFRP, wherein the blocks alternate between polar monomers and non-polar monomers, are useful in many applications as amphiphilic surfactants or dispersants for preparing highly uniform polymer blends. The (co)polymers may have a number average molecular weight from 1 000 to 400000 g/mol, preferably from 2 000 to 250 000 g/mol and, more preferably, from 2 000 to 200 000 g/mol. The number average molecular weight may be determined by size exclusion chromatography (SEC), matrix assisted laser desorption/ionization mass spectrometry (MALDI-MS) or, if the initiator carries a group which can be easily distinguished from the monomer(s), by NMR spectroscopy or other conventional methods. A plurality of specifically designed polymers and copolymers are accessible by this type of controlled radical polymerization, such as star and graft (co)polymers as described, inter alia, by C. J. Hawker in Angew. Chemie, 1995, 107, pages 1623-1627, dendrimers as described by K. Matyaszewski et al. in Macromolecules 1996, Vol 29, No. 12, pages 4167-4171 , graft (co)polymers as described by C. J. Hawker et al. in Macromol. Chem. Phys. 198, 155- 166(1997), random copolymers as described by C. J. Hawker in Macromolecules 1996, 29, 2686-2688, or diblock and triblock copolymers as described by N. A. Listigovers in Macromolecules 1996, 29, 8992-8993. Preferably the reducing agent is a cyclic ethylenically unsaturated compound having an allylic hydrogen atom, a phosphorous compound with oxidation number l-IV and a valence of 3 to 5 or a sulfur compound with oxidation number l-IV and a valence of 2 or 4 or a mixture thereof Particularly preferred is a composition, wherein the reducing agent is a mixture of a cyclic ethylenically unsaturated compound having an allylic hydrogen atom and a phosphorous compound with oxidation number l-IV and a valence of 3 to 5 or a sulfur compound with oxidation number l-IV and a valence of 2 to 4. Particularly preferred phosphorous compounds are: H 3 PO 2 phosphinic acid, H P 2 O hypodiphosphonic acid, H 3 PO 3 /H 4 P 2 O 5 phosphonic-/diphosphonic acid, H 4 P 2 0 6 hypodiphosphoric acid and their ammonium, alkali or alkali earth salts. The salts may also contain crystal water. Suitable organic phosphorous compounds are R'-H 2 PO 2 , R'R'ΗPO or R'R"HPO 3 , P(OR) 3 wherein R' and R" independently are C 7 - C 18 Aralkyl, phenyl or C C 18 alkyl. Also suitable organic phosphites and phosphonites are for example triphenyl phosphite, diphenyl alkyl phosphites, phenyl dialkyl phosphites, tris(nonylphenyl) phosphite, trilauryl phosphite, trioctadecyl phosphite, distearyl pentaerythritol diphosphite, tris(2,4-di-tert- butylphenyl) phosphite, diisodecyl pentaerythritol diphosphite, bis(2,4-di-tert-butylphenyl) pentaerythritol diphosphite, bis(2,6-di-tert-butyl-4-methylphenyl)-pentaerythritol diphosphite, diisodecyloxypentaerythhtol diphosphite, bis(2,4-di-tert-butyl-6-methylphenyl)pentaerythritol diphosphite, bis(2,4,6-tris(tert-butylphenyl)pentaerythritol diphosphite, tristearyl sorbitol triphosphite, tetrakis(2,4-di-tert-butylphenyl) 4,4'-biphenylene diphosphonite, 6-isooctyloxy- 2,4,8,10-tetra-tert-butyl-12H-dibenz[d,g]-1 ,3,2-dioxaphosphocin, 6-fluoro-2,4,8, 10-tetra-tert- butyl-12-methyl-dibenz[d,g]-1 ,3,2-dioxaphosphocin, bis(2,4-di-tert-butyl-6-methylphenyl) methyl phosphite, bis(2,4-di-tert-butyl-6-methylphenyl) ethyl phosphite, 2,2',2"-nitrilo- [triethylths(3,3 , ,5,5 , -tetra-tert-butyl-1 ,1'-biphenyl-2,2 , -diyl)phosphite], 2-ethylhexyl(3,3',5,5'- tetra-tert-butyl-1 , 1 '-biphenyl-2,2'-diyl)phosphite. Especially preferred are the following phosphites: Tπs(2 4-dι-tert-butylphenyl) phosphite (lrgafos s 168, Ciba-Geigy), trιs(nonylphenyl) phosphite, (G) Particularly preferred sulfur compounds are: H 2 S 2 O 2 /H 2 S 2 O 3 sulfoxylic-/ thiosulfuric acid H S 2 O 4 dithionic acid H 2 SO 3 /H 2 S 2 O 5 sulfurous-/disulfurous acid R-S-OH sulfenic acid R-S=O-OH sulfinic acid and their amonium, alkali or alkali earth salts. The salts may also contain crystal water. Typically the alkali or alkali earth metal is Li, Na, K, Ca, Mg. The salts can contain additional crystal water. Most preferred are H 3 P0 2 (phosphinic acid), or a Na, K, Ca, Mg or ammonium salt thereof, with or without crystal water. Particularly preferred is NaH 2 PO 2 which may contain additional crystal water. Examples of cyclic ethylenically unsaturated compounds are dihydroanthacene and dihydronaphtaline and their derivatives, wherein Rι-R 6 independently are H, alkyl, cycloalkyl, aryl, aralkyl, alkenyl, alkinyl or COOalkyl. The aromatic radicals may also be further substituted. A further group is derived from indene, wherein R 7 -R 9 have the same meanings as given for Also suitable are cycloalkenes as defined below. Wherein R 10 is H, Alkyl, Cycloalkyl, Aryl, Aralkyl, Alkenyl, Alkinyl, COOalkyl. X is (CH 2 ) n ; n is a number from 1-9 or X is CH=CH- (CH 2 ) n and n is 0 - 7 or X is (CH=CH) n and is n = 0 - 2. Also suitable are cyclohexadienes, wherein Rn - R 22 independently have the meaning as defined above for Rι-R 6 . In addition two of each R 12 and R 13 , R 15 and Rι 6 or R 19 and R 20 can be part of a second condensed ring system. A further group are Diels-Alder adducts of cyclopentadienes, wherein R 23 - R 28 independently have the same meaning as given above for Rι-R 6 and Y is -CH 2 -, O, NH or N(C 1 -C 4 alkyl). Further suitable dienes are 1 ,4-dienes , condensed aromatic systems wherein V is -CH 2 -, O, NH or N(C C 4 alkyl); or dihydropyridines L, = 1-20 Particularly suitable are polyindene, poly-α-pinene and poly-β-pinene of the general formulae The substituents R 29 -R50 have the same meaning as given for Rι-R 6 and L2 is a number from 1-100. Preferably the meaning of RrR 50 is hydrogen or Cι-C 4 alkyl. Preferably the reducing agent is a cyclic mono-, sesqui- or di-terpene having an allylic hydrogen atom. Examples are α-terpinene, γ-terpinene, α-phellandrene, β-phellandrene, limonene, α-pinene, β-pinene, α-terpineol, cadinene, β-selinene, β-lonone, abietic acid. Most preferred are γ-terpinene and α-phellandrene. The reducing agent is preferably present in an amount of from 0.01% to 5%, more preferably from of from 0.05% to 3%, based on the weight of the polymer. The concentration to be used depends on the amount of nitroxyl present in the oligomer or polymer. Obviously for high concentrations of nitroxyl, high concentrations of the reducing agent are used. Furthermore it depends on the color improvement (color stability of the polymer) to be targeted If a mixture of a cyclic ethylenically unsaturated compound having an allylic hydrogen atom (a) and a phosphorous compound with oxidation number l-IV and a valence of 3 to 5 (b) is used, the ratio (a):(b) may vary from 1 :10 to 10:1 , preferably it is from 1 :5 to 5:1 and most preferably from 1 :2 to 2:1. The composition can also contain further additives. Examples are given below. 1 Antioxidants 1 1 Alkylated monophenols, for example 2,6-dι-tert-butyl-4-methylphenol 2-tert-butyl-4,6-dι- methylphenol, 2,6-dι-tert-butyl-4-ethylphenol, 2,6-dι-tert-butyl-4-n-butylphenol, 2,6-dι-tert-bu- tyl-4-ιsobutylphenol, 2,6-dιcyclopentyl-4-methylphenol, 2-(α-methylcyclohexyl)-4,6-dιmethyl- phenol, 2,6-dιoctadecyl-4-methylphenol, 2,4,6-trιcyclohexylphenol, 2,6-dι-tert-butyl-4- methoxymethylphenol, nonylphenols which are linear or branched in the side chains, for example, 2,6-dι-nonyl-4-methylphenol, 2,4-dιmethyl-6-(1'-methylundec-1 '-yl)phenol, 2,4-dι- methyl-6-(1'-methylheptadec-1'-yl)phenol, 2,4-dιmethyl-6-(1'-methyltrιdec-1 '-yl)phenol and mixtures thereof 1 2 Alkylthiomethylphenols, for example 2,4-dιoctylthιomethyl-6-tert-butylphenol, 2,4-dιoc- tylthιomethyl-6-methylphenol, 2,4-dιoctylthιomethyl-6-ethylphenol, 2,6-dι-dodecylthιomethyl- 4-nonylphenol 1 3 Hydroquinones and alkylated hydroquinones, for example 2,6-dι-tert-butyl-4-methoxy- phenol, 2,5-dι-tert-butylhydroquιnone, 2,5-dι-tert-amylhydroquιnone, 2,6-dιphenyl-4-octade- cyloxyphenol, 2,6-dι-tert-butylhydroquιnone, 2,5-dι-tert-butyl-4-hydroxyanιsole, 3,5-dι-tert- butyl-4-hydroxyanιsole, 3,5-dι-tert-butyl-4-hydroxyphenyl stearate, bιs-(3,5-dι-tert-butyl-4- hydroxyphenyl) adipate 1 4 Tocopherols, for example α-tocopherol, b-tocopherol, g-tocopherol, d-tocopherol and mixtures thereof (Vitamin E) 1 5 Hydroxylated thiodiphenyl ethers, for example 2,2'-thιobιs(6-tert-butyl-4-methylphenol), 2,2'-thιobιs(4-octylphenol), 4,4'-thιobιs(6-tert-butyl-3-methylphenol), 4,4'-thιobιs(6-tert-butyl- 2-methylphenol), 4,4'-thιobιs-(3,6-dι-sec-amylphenol), 4,4'-bιs(2,6-dιmethyl-4-hydroxyphe- nyl)dιsulfιde 1 6 Alky denebisphenols, for example 2,2'-methylenebιs(6-tert-butyl-4-methylphenol), 2,2'- methylenebιs(6-tert-butyl-4-ethylphenol), 2,2'-methylenebιs[4-methyl-6-(α-methylcyclohexyl)- phenol], 2,2'-methylenebιs(4-methyl-6-cyclohexylphenol), 2,2'-methylenebιs(6-nonyl-4-me- thylphenol), 2,2'-methylenebιs(4,6-dι-tert-butylphenol), 2,2'-ethylιdenebιs(4,6-dι-tert-butyl- phenol), 2,2'-ethylidenebis(6-tert-butyl-4-isobutylphenol), 2,2'-methylenebis[6-(α-methylben- zyl)-4-nonylphenol], 2,2'-methylenebis[6-(α,α-dimethylbenzyl)-4-nonylphenol], 4,4'-methy- lenebis(2,6-di-tert-butylphenol), 4,4'-methylenebis(6-tert-butyl-2-methylphenol), 1 ,1-bis(5- tert-butyl-4-hydroxy-2-methylphenyl)butane, 2,6-bis(3-tert-butyl-5-methyl-2-hydroxybenzyl)-4- methylphenol, 1 ,1 ,3-tris(5-tert-butyl-4-hydroxy-2-methylphenyl)butane, 1 ,1-bis(5-tert-butyl-4- hydroxy-2-methyl-phenyl)-3-n-dodecylmercaptobutane, ethylene glycol bis[3,3-bis(3'-tert- butyl-4'-hydroxyphenyl)butyrate], bis(3-tert-butyl-4-hydroxy-5-methyl-phenyl)dicyclopentadi- ene, bis[2-(3'-tert-butyl-2'-hydroxy-5'-methylbenzyl)-6-tert-butyl-4-methylphenyl]terephthalate, 1 ,1-bis-(3,5-dimethyl-2-hydroxyphenyl)butane, 2,2-bis-(3,5-di-tert-butyl-4-hydroxyphe- nyl)propane, 2,2-bis-(5-tert-butyl-4-hydroxy2-methylphenyl)-4-n-dodecylmercaptobutane, 1 ,1 ,5,5-tetra-(5-tert-butyl-4-hydroxy-2-methylphenyl)pentane. 1.7. Q-, N- and S-benzyl compounds, for example 3,5,3',5'-tetra-tert-butyl-4,4'-dihydroxydi- benzyl ether, octadecyl-4-hydroxy-3,5-dimethyibenzylmercaptoacetate, tridecyl-4-hydroxy- 3,5-di-tert-butylbenzylmercaptoacetate, tris(3,5-di-tert-butyl-4-hydroxybenzyl)amine, bis(4- tert-butyl-3-hydroxy-2,6-dimethylbenzyl)dithioterephthalate, bis(3,5-di-tert-butyl-4-hydroxy- benzyl)sulfide, isooctyl-3,5-di-tert-butyl-4-hydroxybenzylmercaptoacetate. 1.8. Hydroxybenzylated malonates, for example dioctadecyl-2,2-bis-(3,5-di-tert-butyl-2-hy- droxybenzyl)-malonate, di-octadecyl-2-(3-tert-butyl-4-hydroxy-5-methylbenzyl)-malonate, di- dodecylmercaptoethyl-2,2-bis-(3,5-di-tert-butyl-4-hydroxybenzyl)malonate, bis[4-(1 ,1 ,3,3-te- tramethylbutyl)phenyl]-2,2-bis(3,5-di-tert-butyl-4-hydroxybenzyl)malonate. 1.9. Aromatic hydroxybenzyl compounds, for example 1 ,3,5-tris-(3,5-di-tert-butyl-4-hydroxy- benzyl)-2,4,6-trimethylbenzene, 1 ,4-bis(3,5-di-tert-butyl-4-hydroxybenzyl)-2,3,5,6-tetrame- thylbenzene, 2,4,6-tris(3,5-di-tert-butyl-4-hydroxybenzyl)phenol. 1.10. T azine Compounds, for example 2,4-bis(octylmercapto)-6-(3,5-di-tert-butyl-4-hy- droxyanilino)-1 ,3,5-triazine, 2-octylmercapto-4,6-bis(3,5-di-tert-butyl-4-hydroxyanilino)-1 ,3,5- triazine, 2-octyimercapto-4,6-bis(3,5-di-tert-butyl-4-hydroxyphenoxy)-1 ,3,5-triazine, 2,4,6- tris(3,5-di-tert-butyl-4-hydroxyphenoxy)-1 ,2,3-triazine, 1 ,3,5-tris-(3,5-di-tert-butyl-4-hydroxy- benzyl)isocyanurate, 1 ,3,5-tris(4-tert-butyl-3-hydroxy-2,6-dimethylbenzyl)isocyanurate, 2,4,6- tris(3,5-di-tert-butyl-4-hydroxyphenylethyl)-1 ,3,5-triazine, 1 ,3,5-tris(3,5-di-tert-butyl-4- hydroxyphenylpropιonyl)-hexahydro-1 3 5-trιazιne 1 3 5-trιs(3 5-dιcyclohexyl-4-hydroxyben- zyl)ιsocyanurate 1 11 Benzylphosphonates, for example dιmethyl-2,5-dι-tert-butyl-4-hydroxybenzylphospho- nate, dιethyl-3,5-dι-tert-butyl-4-hydroxybenzylphosphonate, dιoctadecyl3,5-dι-tert-butyl-4-hy- droxybenzylphosphonate, dιoctadecyl-5-tert-butyl-4-hydroxy-3-methylbenzylphosphonate, the calcium salt of the monoethyl ester of 3,5-dι-tert-butyl-4-hydroxybenzylphosphonιc acid 1 12 Acylaminophenols, for example 4-hydroxylauranιlιde, 4-hydroxystearanιlιde, octyl N- (3,5-dι-tert-butyl-4-hydroxyphenyl)carbamate 1 13 Esters of b-(3,5-dι-tert-butyl-4-hvdroxyphenyl)propιonιc acid with mono- or polyhydnc alcohols, e g with methanol, ethanol, n-octanol, i-octanol, octadecanol, 1,6-hexanedιol, 1 ,9- nonanediol, ethylene glycol, 1 ,2-propanedιol, neopentyl glycol, thiodiethylene glycol, diethy- lene glycol, tnethylene glycol, pentaerythritol, tπs(hydroxyethyl) isocyanurate, N,N'-bιs(hy- droxyethyl)oxamιde, 3-thιaundecanol, 3-thιapentadecanol, tπmethylhexanediol, tπmethylol- propane, 4-hydroxymethyl-1-phospha-2,6,7-trιoxabιcyclo[2 2 2]octane 1 14 Esters of b-(5-tert-butyl-4-hvdroxy-3-methylphenyl)propιonιc acid with mono- or polyhydnc alcohols, e g with methanol, ethanol, n-octanol, i-octanol, octadecanol, 1 ,6-hexane- diol, 1 ,9-nonanedιol, ethylene glycol, 1 ,2-propanedιol, neopentyl glycol, thiodiethylene glycol, diethylene glycol, tnethylene glycol, pentaerythritol, trιs(hydroxyethyl) isocyanurate, N,N'- bιs(hydroxyethyl)oxamιde, 3-thιaundecanol, 3-thιapentadecanol, trimethylhexanediol, tπmethylolpropane, 4-hydroxymethyl-1-phospha-2,6,7-trιoxabιcyclo[2 2 2]octane 1 15 Esters of b-(3,5-dιcvclohexyl-4-hvdroxyphenyl)propιonιc acid with mono- or polyhydnc alcohols, e g with methanol, ethanol, octanol, octadecanol, 1 ,6-hexanedιol, 1 ,9-nonanedιol, ethylene glycol, 1 ,2-propanedιol, neopentyl glycol, thiodiethylene glycol, diethylene glycol, tnethylene glycol, pentaerythritol, trιs(hydroxyethyl)ιsocyanurate, N,N'-bιs(hydroxyethyl)ox- amide, 3-thιaundecanol, 3-thιapentadecanol, trimethylhexanediol, tπmethylolpropane, 4-hy- droxymethyl-1-phospha-2,6,7-trιoxabιcyclo[2 2 2]octane 1 16 Esters of 3,5-di-tert-butyl-4-hvdroxyphenyl acetic acid with mono- or polyhydnc alcohols, e g with methanol, ethanol, octanol, octadecanol, 1 ,6-hexanedιol, 1 ,9-nonanedιol, ethylene glycol, 1 ,2-propanedιol, neopentyl glycol, thiodiethylene glycol, diethylene glycol, tnethylene glycol, pentaerythritol, ths(hydroxyethyl)isocyanurate, N,N'-bιs(hydroxyethyl)ox- amide, 3-thιaundecanol, 3-thιapentadecanol, trimethylhexanediol, trimethylolpropane, 4-hy- droxymethyl-1-phospha-2,6,7-trιoxabicyclo[2.2.2]octane. 1.17. Amides of b-(3,5-di-tert-butyl-4-hvdroxyphenyl)propionic acid e.g. N,N'-bis(3,5-di-tert- butyl-4-hydroxyphenylpropionyl)hexamethylenediamide, N,N'-bis(3,5-di-tert-butyl-4-hydroxy- phenylpropionyl)trimethylenediamide, N,N'-bis(3,5-di-tert-butyl-4-hydroxyphenylpropionyl)- hydrazide, N,N'-bis[2-(3-[3,5-di-tert-butyl-4-hydroxyphenyl]propionyloxy)ethyl]oxamide (Naugard ® XL-1 supplied by Uniroyal). 1.18. Ascorbic acid (vitamin C) 1.19. Aminic antioxidants, for example N,N'-di-isopropyl-p-phenylenediamine, N,N'-di-sec- butyl-p-phenylenediamine, N,N'-bis(1 ,4-dimethylpentyl)-p-phenylenediamine, N,N'-bis(1- ethyl-3-methylpentyl)-p-phenylenediamine, N,N'-bis(1-methylheptyl)-p-phenylenediamine, N,N'-dicyclohexyl-p-phenylenediamine, N,N'-diphenyl-p-phenylenediamine, N,N'-bis(2-naph- thyl)-p-phenylenediamine, N-isopropyl-N'-phenyl-p-phenylenediamine, N-(1 ,3-dimethylbutyl)- N'-phenyl-p-phenylenediamine, N-(1 -methylheptyl)-N'-phenyl-p-phenylenediamine, N-cyclo- hexyl-N'-phenyl-p-phenlenediamine, 4-(p-toluenesulfamoyl)diphenylamine, N,N'-dimethyl- N,N'-di-sec-butyl-p-phenylenediamine, diphenylamine, N-allyldiphenylamine, 4-isopropoxy- diphenylamine, N-phenyl-1-naphthylamine, N-(4-tert-octylphenyl)-1-naphthylamine, N-phe- nyl-2-naphthylamine, octylated diphenylamine, for example p,p'-di-tert-octyldiphenylamine, 4- n-butylaminophenol, 4-butyrylaminophenol, 4-nonanoylaminophenol, 4-dodecanoylamino- phenol, 4-octadecanoylaminophenol, bis(4-methoxyphenyl)amine, 2,6-di-tert-butyl-4-dime- thylaminomethylphenol, 2,4'-diaminodiphenylmethane, 4,4'-diaminodiphenylmethane, N,N,N',N'-tetramethyl-4,4'-diaminodiphenylmethane, 1 ,2-bis[(2-methylphenyl)amino]ethane, 1 ,2-bis(phenylamino)propane, (o-tolyl)biguanide, bis[4-(1',3'-dimethylbutyl)phenyl]amine, tert- octylated N-phenyl-1-naphthylamine, a mixture of mono- and dialkylated tert-butyl/tert- octyldiphenyiamines, a mixture of mono- and dialkylated nonyldiphenylamines, a mixture of mono- and dialkylated dodecyldiphenylamines, a mixture of mono- and dialkylated isopro- pyl/isohexyldiphenylamines, a mixture of mono- und dialkylated tert-butyldiphenylamines, 2,3-dihydro-3,3-dimethyl-4H-1 ,4-benzothiazine, phenothiazine, a mixture of mono- und dialkylated tert-butyl/tert-octylphenothiazines, a mixture of mono- und dialkylated tert-octyl-phe- nothiazines, N-allylphenothiazin, N,N,N',N'-tetraphenyl-1 ,4-dιamιnobut-2-ene, N,N-bιs- (2,2,6,6-tetramethyl-pιperιd-4-yl-hexamethylenedιamιne, bιs(2,2,6,6-tetramethylpιpeπd-4-yl)- sebacate, 2,2,6,6-tetramethylpιperιdιn-4-one, 2,2,6,6-tetramethylpιperιdιn-4-ol 2. UV absorbers and light stabilisers 2.1. 2-(2'-Hvdroxyphenyl)benzotriazoles, for example 2-(2'-hydroxy-5'-methylphenyl)-benzo- triazole, 2-(3',5'-di-tert-butyl-2'-hydroxyphenyl)benzotriazole, 2-(5'-tert-butyl-2'-hydroxyphe- nyl)benzotriazole, 2-(2'-hydroxy-5'-(1 ,1 ,3,3-tetramethylbutyl)phenyl)benzotriazole, 2-(3',5'-di- tert-butyl-2'-hydroxyphenyl)-5-chloro-benzotriazole, 2-(3'-tert-butyl- 2'-hydroxy-5'-methylphe- nyl)-5-chloro-benzotriazole, 2-(3'-sec-butyl-5'-tert-butyl-2'-hydroxyphenyl)benzotriazole, 2-(2'- hydroxy-4'-octyloxyphenyl)benzothazole, 2-(3',5'-di-tert-amyl-2'-hydroxyphenyl)benzotriazole, 2-(3',5'-bis-(α,α-dimethylbenzyl)-2'-hydroxyphenyl)benzotriazole, 2-(3'-tert-butyl-2'-hydroxy- 5'-(2-octyloxycarbonylethyl)phenyl)-5-chloro-benzotriazole, 2-(3'-tert-butyl-5'-[2-(2- ethylhexyloxy)-carbonylethyl]-2'-hydroxyphenyl)-5-chloro-benzotriazole, 2-(3'-tert-butyl-2'-hy- droxy-5'-(2-methoxycarbonylethyl)phenyl)-5-chloro-benzotriazole, 2-(3'-tert-butyl-2'-hydroxy- 5'-(2-methoxycarbonylethyl)phenyl)benzotriazole, 2-(3'-tert-butyl-2'-hydroxy-5'-(2-octyloxy- carbonylethyl)phenyl)benzotriazole, 2-(3'-tert-butyl-5'-[2-(2-ethylhexyloxy)carbonylethyl]-2'- hydroxyphenyl)benzotriazole, 2-(3'-dodecyl-2'-hydroxy-5'-methylphenyl)benzotriazole, 2-(3'- tert-butyl-2'-hydroxy-5'-(2-isooctyloxycarbonylethyl)phenylbenzotriazole, 2,2'-methylene-bis- [4-(1 ,1 ,3,3-tetramethylbutyl)-6-benzotriazole-2-ylphenol]; the transeste fication product of 2- [3'-tert-butyl-5'-(2-methoxycarbonylethyl)-2'-hydroxyphenyl]-2H-benzotriazole with polyethy¬ lene glycol 300; [R-CH 2 CH 2 — COO-CH 2 CH 2 -3- where R = 3'-tert-butyl-4'-hydroxy-5'-2H- benzotriazol-2-ylphenyl, 2-[2'-hydroxy-3'-(α,α-dimethyibenzyl)-5'-(1 ,1,3,3-tetramethylbutyl)- phenyljbenzothazole; 2-[2'-hydroxy-3'-(1 , 1 ,3,3-tetramethylbutyl)-5'-(α,α-dimethylbenzyl)- phenyljbenzotriazole. 2.2. 2-Hvdroxybenzophenones, for example the 4-hydroxy, 4-methoxy, 4-octyloxy, 4-decyl- oxy, 4-dodecyloxy, 4-benzyloxy, 4,2',4'-trihydroxy and 2'-hydroxy-4,4'-dimethoxy derivatives. 2.3. Esters of substituted and unsubstituted benzoic acids, as for example 4-tertbutyl-phenyl salicylate, phenyl salicylate, octylphenyl salicylate, dibenzoyl resorcinol, bis(4-tert-butylben- zoyl) resorcinol, benzoyl resorcinol, 2,4-di-tert-butylphenyl 3,5-di-tert-butyl-4-hydroxybenzo- ate, hexadecyl 3,5-dι-tert-butyl-4-hydroxybenzoate, octadecyl 3,5-dι-tert-butyl-4-hydroxy- benzoate, 2-methyl-4,6-di-tert-butylphenyl 3,5-dι-tert-butyl-4-hydroxybenzoate. 2.4. Acrylates, for example ethyl α-cyano-b,b-diphenylacrylate, isooctyl α-cyano-b,b-diphe- nylacrylate, methyl α-carbomethoxycinnamate, methyl α-cyano-b-methyl-p-methoxy-cinna- mate, butyl α-cyano-b-methyl-p-methoxy-cinnamate, methyl α-carbomethoxy-p-methoxycin- namate and N-(b-carbomethoxy-b-cyanovinyl)-2-methylindoline. 2.5. Nickel compounds, for example nickel complexes of 2,2'-thio-bis-[4-(1 ,1 ,3,3-tetrame- thylbutyl)phenol], such as the 1 :1 or 1 :2 complex, with or without additional ligands such as n-butylamine, triethanolamine or N-cyclohexyldiethanolamine, nickel dibutyldithiocarbamate, nickel salts of the monoalkyl esters, e.g. the methyl or ethyl ester, of 4-hydroxy-3,5-di-tert- butylbenzylphosphonic acid, nickel complexes of ketoximes, e.g. of 2-hydroxy-4-methyiphe- nyl undecylketoxime, nickel complexes of 1-phenyl-4-lauroyl-5-hydroxypyrazole, with or without additional ligands. 2.6. Sterically hindered amines, for example bis(2,2,6,6-tetramethyl-4-piperidyl)sebacate, bis(2,2,6,6-tetramethyl-4-piperidyl)succinate, bis(1 ,2,2,6,6-pentamethyl-4-piperidyl)sebacate, bis(1-octyloxy-2,2,6,6-tetramethyl-4-pipehdyl)sebacate, bis(1 , 2,2,6, 6-pentamethyl-4-pi- peridyl) n-butyl-3,5-di-tert-butyl-4-hydroxybenzylmalonate, the condensate of 1-(2-hydroxy- ethyl)-2,2,6,6-tetramethyl-4-hydroxypiperidine and succinic acid, linear or cyclic condensates of N,N'-bis(2,2,6,6-tetramethyl-4-piperidyl)hexamethylenediamine and 4-tert-octylamino-2,6- dichloro-1 ,3,5-triazine, tris(2,2,6,6-tetramethyl-4-piperidyl)nithlotriacetate, tetrakis(2,2,6,6- tetramethyl-4-piperidyl)-1 ,2,3,4-butane-tetracarboxylate, 1 ,1'-(1,2-ethanediyl)-bis(3, 3,5,5- tetramethylpiperazinone), 4-benzoyl-2,2,6,6-tetramethylpiperidine, 4-stearyloxy-2,2,6,6- tetramethylpiperidine, bis(1 ,2,2,6,6-pentamethylpiperidyl)-2-n-butyl-2-(2-hydroxy-3,5-di-tert- butylbenzyl)malonate, 3-n-octyl-7,7,9,9-tetramethyl-1 ,3,8-thazaspiro[4.5]decan-2,4-dione, bis(1-octyloxy-2,2,6,6-tetramethyipiperidyl)sebacate, bis(1-octyloxy-2,2,6,6-tetrame- thylpiperidyl)succinate, linear or cyclic condensates of N,N'-bis-(2,2,6,6-tetramethyl-4-piperi- dyl)hexamethylenediamine and 4-morpholino-2,6-dichloro-1 ,3,5-triazine, the condensate of 2-chloro-4,6-bis(4-n-butylamino-2,2,6,6-tetramethylpiperidyl )-1 ,3,5-triazine and 1 ,2-bis(3- aminopropylamino)ethane, the condensate of 2-chloro-4,6-di-(4-n-butylamino-1 , 2,2,6, 6-pen- tamethylpiperidyl)-1 ,3,5-triazine and 1,2-bis-(3-aminopropylamino)ethane, 8-acetyl-3-dode- cyl-7,7,9,9-tetramethyl-1 ,3,8-triazaspiro[4.5]decane-2,4-dione, 3-dodecyl-1-(2,2,6,6-tetrame- thyl-4-pιpeπdyl)pyrrolιdιn-2,5-dιone, 3-dodecyl-1 -(1 ,2,2,6,6-pentamethyl-4-pιperidyl)pyrrolι- dιne-2,5-dιone, a mixture of 4-hexadecyloxy- and 4-stearyloxy-2,2,6,6-tetramethylpιperιdιne, a condensation product of N,N'-bιs(2,2,6,6-tetramethyl-4-pιperιdyl)hexamethylenedιamιne and 4-cyclohexylamιno-2,6-dichloro-1 ,3,5-triazine, a condensation product of 1 ,2-bis(3-amι- nopropylamino)ethane and 2,4,6-thchloro-1 ,3,5-triazιne as well as 4-butylamιno-2,2,6,6-te- tramethylpiperidine (CAS Reg. No. [136504-96-6]); N-(2,2,6,6-tetramethyl-4-piperidyl)-n-do- decylsuccinimid, N-(1 ,2,2,6,6-pentamethyl-4-piperidyl)-n-dodecylsuccinimid, 2-undecyl- 7,7,9,9-tetramethyl-1-oxa-3,8-diaza-4-oxo-spiro[4,5]decane, a reaction product of 7,7,9,9- tetramethyl-2-cycloundecyl-1-oxa-3,8-diaza-4-oxospiro [4,5]decane und epichlorohydrin, 1 ,1- bis(1 ,2,2,6,6-pentamethyl-4-piperidyloxycarbonyl)-2-(4-methoxyphenyl)ethene, N,N'-bis- formyl-N,N'-bis(2,2,6,6-tetramethyl-4-piperidyl)hexamethylenediamine, diester of 4-methoxy- methylene-malonic acid with 1 ,2,2,6,6-pentamethyl-4-hydroxypiperidine, poly[methylpropyl-3- oxy-4-(2,2,6,6-tetramethyl-4-piperidyl)]siloxane, reaction product of maleic acid anhydride-α- olefin-copolymer with 2,2,6,6-tetramethyl-4-aminopiperidine or 1 , 2,2,6, 6-pentamethyl-4- aminopiperidine. 2.7. Oxamides, for example 4,4'-dioctyloxyoxanilide, 2,2'-diethoxyoxanilide, 2,2'-dioctyloxy- 5,5'-di-tert-butoxanilide, 2,2'-didodecyloxy-5,5'-di-tert-butoxanilide, 2-ethoxy-2'-ethyloxanilide, N,N'-bis(3-dimethylaminopropyl)oxamide, 2-ethoxy-5-tert-butyl-2'-ethoxanilide and its mixture with 2-ethoxy-2'-ethyl-5,4'-di-tert-butoxanilide, mixtures of o- and p-methoxy-disubstituted oxanilides and mixtures of o- and p-ethoxy-disubstituted oxanilides. 2.8. 2-(2-Hydroxyphenyl)-1 ,3,5-triazines, for example 2,4,6-tris(2-hydroxy-4-octyloxyphenyl)- 1 ,3,5-triazine, 2-(2-hydroxy-4-octyloxyphenyl)-4,6-bis(2,4-dimethylphenyl)-1 ,3,5-triazine, 2- (2,4-dihydroxyphenyl)-4,6-bis(2,4-dimethylphenyl)-1 ,3,5-thazine, 2,4-bis(2-hydroxy-4-pro- pyloxyphenyl)-6-(2,4-dimethylphenyl)-1 ,3,5-triazine, 2-(2-hydroxy-4-octyloxyphenyl)-4,6-bis- (4-methylphenyl)-1,3,5-triazine, 2-(2-hydroxy-4-dodecyloxyphenyl)-4,6-bis(2,4-dimethylphe- nyl)-1 ,3,5-triazine, 2-(2-hydroxy-4-tridecyloxyphenyl)-4,6-bis(2,4-dimethylphenyl)-1 ,3,5-trι- azine, 2-[2-hydroxy-4-(2-hydroxy-3-butyloxy-propoxy)phenyl]-4,6-bis(2,4-dimethyl)-1 ,3,5-th- azine, 2-[2-hydroxy-4-(2-hydroxy-3-octyloxy-propyloxy)phenyl]-4,6-bis(2,4-dimethyl)-1 ,3,5- thazine, 2-[4-(dodecyloxy/tridecyloxy-2-hydroxypropoxy)-2-hydroxy-phenyl]-4,6-bis(2,4-dι- methylphenyl)-1 ,3,5-triazine, 2-[2-hydroxy-4-(2-hydroxy-3-dodecyloxy-propoxy)phenyl]-4,6- bis(2,4-dimethylphenyl)-1 ,3,5-triazine, 2-(2-hydroxy-4-hexyloxy)phenyl-4,6-diphenyl-1 ,3,5- triazine, 2-(2-hydroxy-4-methoxyphenyl)-4,6-diphenyl-1,3,5-triazine, 2,4,6-tris[2-hydroxy-4-(3- butoxy-2-hydroxy-propoxy)phenyl]-1 3 5-trιazιne, 2-(2-hydroxyphenyl)-4-(4-methoxyphenyl)- 6-phenyl-1 3 5-trιazιne 2-{2-hydroxy-4-[3-(2-ethylhexyl-1-oxy)-2-hydroxypropyloxy]phenyl}- 4 6-bιs(2,4-dιmethylphenyl)-1 ,3,5-trιazιne 3 Metal deactivators, for example N,N'-dιphenyloxamιde, N-salicylal-N'-salicyloyi hydrazine, N,N'-bιs(salιcyloyl) hydrazine, N,N'-bιs(3,5-dι-tert-butyl-4-hydroxyphenylpropιonyl) hydrazine, 3-salιcyloylamιno-1 ,2,4-trιazole, bιs(benzylιdene)oxalyl dihydrazide, oxanilide, isophthaloyl dihydrazide, sebacoyl bisphenylhydrazide, N,N'-dιacetyladιpoyl dihydrazide, N,N'-bιs(salιcyl- oyl)oxalyl dihydrazide, N,N'-bιs(salιcyloyl)thιopropιonyl dihydrazide 4 Hydroxylamines, for example, N,N-dιbenzylhydroxylamιne, N,N-dιethylhydroxylamιne, N.N-dioctylhydroxylamine, N,N-dιlaurylhydroxylamιne, N,N-dιtetradecylhydroxylamιne, N,N- dihexadecylhydroxylamine, N,N-dιoctadecylhydroxylamιne, N-hexadecyl-N-octadecylhy- droxylamine, N-heptadecyl-N-octadecylhydroxylamine, N,N-dιalkylhydroxylamιne derived from hydrogenated tallow amine 5 Nitrones, for example, N-benzyl-alpha-phenyl-nitrone, N-ethyl-alpha-methyl-nitrone, N-oc- tyl-alpha-heptyl-nitrone, N-lauryl-alpha-undecyl-nitrone, N-tetradecyl-alpha-tndcyl-nitrone, N- hexadecyl-alpha-pentadecyl-nitrone, N-octadecyl-alpha-heptadecyl-nitrone, N-hexadecyl- alpha-heptadecyl-nitrone, N-ocatadecyl-alpha-pentadecyl-nitrone, N-heptadecyl-alpha-hep- tadecyl-nitrone, N-octadecyl-alpha-hexadecyl-nitrone, nitrone derived from N,N-dιalkylhy- droxylamine derived from hydrogenated tallow amine 6 Thiosvnergists, for example, dilauryl thiodipropionate or distearyl thiodipropionate 7 Basic co-stabilisers, for example, melamine, polyvinylpyrro done, dicyandiamide, t allyl cyanurate, urea derivatives, hydrazine derivatives, amines, polyamides, polyurethanes, alkali metal salts and alkaline earth metal salts of higher fatty acids for example calcium stearate, zinc stearate, magnesium behenate, magnesium stearate, sodium ncinoleate and potassium palmitate, antimony pyrocatecholate or zink pyrocatecholate 8 Nucleating agents, for example, inorganic substances such as talcum, metal oxides such as titanium dioxide or magnesium oxide, phosphates, carbonates or sulfates of, preferably, alkaline earth metals, organic compounds such as mono- or polycarboxylic acids and the salts thereof, e g 4-tert-butylbenzoιc acid adipic acid diphenylacetic acid sodium succinate or sodium benzoate polymeric compounds such as ionic copolymers (lonomers) 9 Fillers and reinforcing agents, for example, calcium carbonate, silicates, glass fibres, glass bulbs, asbestos, talc, kaolin, mica, barium sulfate, metal oxides and hydroxides, carbon black, graphite, wood flour and flours or fibers of other natural products, synthetic fibers 10 Other additives, for example, plasticisers, lubricants, emulsifiers, pigments, rheology additives, catalysts, flow-control agents, optical bnghteners, flameproofing agents, antistatic agents and blowing agents 11 Benzofuranones and indolinones, for example those disclosed in U S 4,325,863, U S 4,338,244, U S 5,175,312, U S 5,216,052, U S 5,252,643, DE-A-4316611 , DE-A-4316622, DE-A-4316876, EP-A-0589839 or EP-A-0591102 or 3-[4-(2-acetoxyethoxy)- phenyl]-5,7-dι-tert-butyl-benzofuran-2-one, 5,7-dι-tert-butyl-3-[4-(2-stearoyloxyethoxy)phe- nyl]benzofuran-2-one, 3,3'-bιs[5,7-dι-tert-butyl-3-(4-[2-hydroxyethoxy]phenyl)benzofuran-2- one], 5,7-dι-tert-butyl-3-(4-ethoxyphenyl)benzofuran-2-one, 3-(4-acetoxy-3,5-dιmethylphe- nyl)-5,7-dι-tert-butyl-benzofuran-2-one, 3-(3,5-dιmethyl-4-pιvaloyloxyphenyl)-5,7-dι-tert-butyl- benzofuran-2-one, 3-(3,4-dιmethylphenyl)-5,7-dι-tert-butyl-benzofuran-2-one, 3-(2,3-dι- methylphenyl)-5,7-dι-tert-butyl-benzofuran-2-one Another subject of the invention is a process for improving the color of an oligomer, cooligomer, polymer or copolymer or blends thereof, containing a stable free nitroxyl radical \ N-O- , / by adding a reducing agent to said polymer and heating said mixture to above the glass temperature in case of amorphous polymers or above the melting point in case of crystalline or semi-crystalline polymers, with the proviso that essentially no poiymenzable monomer is present There are different reasons, why stable free nitroxyl radicals may be present in a polymer One possibility is that graft polymers have been prepared in the presence of a nitroxyl radical or a nitroxyl ether Such a process typically comprises a first step A), wherein a stable nitroxyl radical is grafted onto a polymer, which step comprises heating a polymer and a compound containing a stable NO * radical to above the melting point of the polymer, mixing and reacting the components at said temperature; and in a second step B) the grafted polymer of step A) is heated in the presence of an ethylenically unsaturated monomer or oligomer to a temperature at which cleavage of the nitroxyl-polymer bond occurs. Such polymers, grafted in the presence of a nitroxyl radical or a nitroxyl ether are also a preferred embodiment of the present invention. The stable free nitroxyl radical may also be present in the polymer due to its admixture for monomer stabilization or due to its use as chain stopping agent. Preferred is a process for improving the color of polymers, obtained by radical polymerization, which polymerization has been carried out in the presence of a stable free \ nitroxyl radical N— O» and a source of free radicals capable of initiating the \ polymerization, or in the presence of a nitroxyl ether N— O — X , wherein / X represents a group having at least one carbon atom and is such that the free radical \ derived from X is capable of initiating polymerization and the remaining N— O * radical forms a stable free nitroxyl radical; by adding a reducing agent to said polymer and heating said mixture to above the glass temperature in case of amorphous polymers or above the melting point in case of crystalline or semi-crystalline polymers; with the proviso that essentially no polymehzable monomer is present. The process is preferably carried out, wherein the mixture is heated to 50°-150° C above the glass temperature in case of amorphous polymers or 20°-180° C above the melting point in case of crystalline or semi-crystalline polymers. The heating step of the process may be performed in any reactor suitable for mixing a polymer melt. Preferably the reactor is an extruder or kneading apparatus as for example described in "Handbuch der Kunststoffextrusion" Vol. I, editor F. Hensen, W. Knappe and H Potente, 1989, pages 3-7. If an extruder is used the process may be described as reactive extrusion process. Examples of reactiv extrusion equipment and processes are given by G. H. Hu et al., in "Reactive Modifiers for Polymers", first edition, Blackie Academic & Professional an Imprint of Chapman & Hall, London 1997, chapter 1, pages 1-97. Preferably, if an extruder is used, a reduced pressure of less than 200 mbar is applied during extrusion. Volatile by products may be removed thereby. Typical reaction times are from a few seconds to several hours. Preferably the reaction time is from 10 seconds to 1 h, most preferably from 20 seconds to 20 min. Another subject is the use of a reducing agent for improving the color of an oligomer, cooligomer, polymer or copolymer or blends thereof, containing a stable free nitroxyl radical \ N-O- / Still another subject of the invention is the use of a reducing agent for removing the discoloration of polymers, obtained by radical polymerization, which polymerization has been \ carried out in the presence of a stable free nitroxyl radical N— O» and a source of free / radicals capable of initiating the polymerization, or in the presence of a nitroxyl ether \ N— O — X , wherein / X represents a group having at least one carbon atom and is such that the free radical \ derived from X is capable of initiating polymerization and the remaining N— O* radical forms a stable free nitroxyl radical. The following examples illustrate the invention The nitroxyl compounds A B and C used in the following examples are known and can be prepared by oxidation of the corresponding amines for example according to US 5 654 434 5,204 473 and GB 2 335 190 Example 1 Color improvement of polystyrene synthesized by controlled free radical polymerization in presence of a nitroxyl radical In a 2 I reactor 1 419 g (5 858 mmol) dibenzoyl peroxide and 2 707 g (7 615 mmol) dodecanoic acιd-(2,2,6,6-tetramethyl-pιperιdιne-4-yl-1-oxyl)ester (nitroxyl A) are added to 1590 g (15 27 mol) styrene under argon atmosphere Dissolved oxygen is removed in repeating evacuation/Ar-purging steps The reaction mixture is stirred and heated under argon atmosphere to 125° C for 6 hours Remaining monomer is removed at 60° C under vacuum The residue is dried in a first step under vacuum and in a second step under normal pressure at 70° C until constant weight is achieved (1390 g polystyrene, 87 % conversion) From the synthesized polystyrene a molded plaque of 2 mm thickness is prepared (molding conditions 1 mm heating, 1 mm molding, 1 mm pressure release, 3 mm molding, T = 220° C) The yellowness index is measured according to DIN 53383 In a twin screw extruder, model TW 100, Haake, the synthesized polystyrene is extruded together with the additives given in table 3 at a temperature T max = 220 °C (heating zones 1 - 5) and 40 r/mm The product is granulated from strands in a water bath From the granules a molded plaque of 2 mm thickness is prepared (molding conditions 1 mm heating, 1 mm molding, 1 mm pressure release, 3 mm molding, T = 220° C) The plaques are stored at 80° C in a circulating air drying oven in order to determine discoloration during thermal aging after definite time intervals Table 1 shows the measured yellowness index at different time intervals (h) Table 1 yellowness index of molded polystyrene prepared by controlled free radical polymerization using nitroxyl A Example 2-4 Color improvement of polystyrene containing nitroxyl-radicals (model experiment) In a twin screw extruder, model TW 100, Haake, a commercial general purpose polystyrene (PS-165/H ex BASF, MFR(200/5) = 2 9) is extruded together with 0 1 % decandioic acid bιs(2,2,6,6-tetramethyl-pιperιdιne-4-yl-1-oxyl)ester (CXA 5415, commercial nitroxyl of Ciba Specialty Chemicals) at a temperature T max = 220 °C (heating zones 1 - 5) and 40 r/mm The product is granulated from strands in a water bath From the granules a molded plaque of 2 mm thickness is prepared (molding conditions 1 mm heating, 1 mm molding, 1 mm pressure release, 3 mm molding, T = 220° C) The yellowness index is measured according to DIN 53383 The nitroxyl radical containing granulate is extruded for a second time together with the additives given in table 1 (T max = 250 °C (heating zone 1 - 5) and 40 r/min), granules are formed and molded plaques are prepared as given above The plaques are stored at 80° C in a circulating air drying oven in order to determine discoloration during thermal aging after definite time intervals Table 2 shows the measured yellowness index at different time intervals (h) Table 2 yellowness index of molded polystyrene Example 5-8 Color improvement of polyethylene containing nitroxyl-radicals (model experiment) In a twin screw extruder, model ZSK 25, Werner & Pfleiderer, a commercial grade low density polyethylene (Lupolen 1812E ex BASF, FR(igo/ 2 -| = 34) is extruded together with 0.1% dodecanoic acid(2,2,6,6-tetramethyl-piperidine-4-yl-1-oxyl)ester at a temperature T max = 200 °C (heating zones 1 - 5) and 100 r/min. The product is granulated from strands in a water bath. From the granules a molded plaque of 2 mm thickness is prepared (molding conditions: 1 min heating, 1 min molding, 1 min pressure release, 3 min molding, T = 220° C). The yellowness index is measured according to DIN 53383. The nitroxyl radical containing granulate is extruded for a second time together with the additives given in table 1 (T max = 220 °C (heating zone 1 - 5) and 100 r/min), granules are formed and molded plaques are prepared as given above. Table 3 shows the measured yellowness index. Table 3: yellowness index of molded polyethylene nitroxyl A = dodecanoic acid(2,2,6,6-tetramethyl-piperidine-4-yl-1-oxyl)ester Example 9-13 Color improvement of polystyrene containing nitroxyl-radicals (model experiment) In a twin screw extruder, model ZSK 25, Werner & Pfleiderer, a commercial general purpose polystyrene (PS-165/H ex BASF, MFR( 2 QO/5) = 2.9) is extruded together with 0.05% octadecanoic acid(2,2,6,6-tetramethyl-piperidine-4-yl-1-oxyl)ester at a temperature T max = 220 °C (heating zones 1 - 5) and 100 r/min. The product is granulated from strands in a water bath. From the granules a molded plaque of 2 mm thickness is prepared (molding conditions: 1 min heating, 1 min molding, 1 min pressure release, 3 min molding, T = 220° C). The yellowness index is measured on a Minolta CM 3600D according to DIN 6167. The nitroxyl radical containing granulate is extruded for a second time together with the additives given in Table 4 (T max = 220 °C (heating zone 1 - 5) and 100 r/min), granules are formed and molded plaques are prepared as given above. Table 4 shows the measured yellowness index. Table 4: yellowness index of molded polystyrene nitroxyl B = octadecanoic acιd-(2,2,6,6-tetramethyl-pιpeπdιne-4-yl-1-oxyl)ester Irgafos TNPP =trιs(nonylphenyl)phosphιte (commercial product of Ciba Specialty Chemicals) Irganox 3052 = 2-(1 ,1-dιmethylethyl)-6-[3-(1 ,1-dιmethylethyl)-2-hydroxy-5- methylphenyl]methyl-4- methylphenyl acrylate (commercial product of Ciba Specialty Chemicals) Example 14-20 Color improvement of polystyrene containing nitroxyl-radicals (model experiment) In a twin screw extruder, model ZSK 25, Werner & Pfleiderer, a commercial general purpose polystyrene (PS-165/H ex BASF, MFR( 2 QO/5) = 3 5) IS extruded together with 0 05% acetic acιd(2,6-dιethyl-2,3,6-trιmethyl-pιperιdιne-4-yl-1-oxyl)ester at a temperature T max = 220 °C (heating zones 1 - 5) and 100 r/min The product is granulated from strands in a water bath From the granules a molded plaque of 2 mm thickness is prepared (molding conditions 1 mm heating, 1 mm molding, 1 mm pressure release, 3 m molding, T = 220° C) The yellowness index is measured on a Minolta CM 3600D according to DIN 6167 The nitroxyl radical containing granulate is extruded for a second time together with the additives given in table 4 (T max = 220 °C (heating zone 1 - 5) and 100 r/min), granules are formed and molded plaques are prepared as given above Table 5 shows the measured yellowness index. Table 5 yellowness index of molded polystyrene nitroxyl C = acetic acιd(2,6-dιethyl-2,3,6-trιmethyl-pιperιdιne-4-yl-1-oxyl)ester Irgafos P-EPQ = tetrakis(2,4-di-tert-butylphenyl)[1 ,1-biphenyl]4,4'-diylbisphosphonite (commercial product of Ciba Specialty Chemicals) Irgafos TNPP = ths(nonyl-phenyl)phosphite (commercial product of Ciba Specialty Chemicals) Irgafos 126 = bis(2,4-di-tert-butylphenyl)pentaerythrol-diphosphite (commercial product of Ciba Specialty Chemicals)

Claims: Claims 1 A composition comprising, a) at least one oligomer, cooligomer, polymer or copolymer or blends thereof, containing a \ stable free nitroxyl radical N— O' ; and b) a reducing agent; with the proviso that the composition is essentially free of a polymerizable monomer. 2. A composition according to claim 1 comprising, a) at least one oligomer, cooligomer, polymer or copolymer, obtained by radical polymerization, which polymerization has been carried out in the presence of a stable free \ nitroxyl radical N— O» and a source of free radicals capable of initiating the \ polymerization, or in the presence of a nitroxyl ether N— O — X , wherein / X represents a group having at least one carbon atom and is such that the free radical \ derived from X is capable of initiating polymerization and the remaining N— O- radical forms a stable free nitroxyl radical; and b) a reducing agent; with the proviso that the composition is essentially free of a polymerizable monomer. 3. A composition according to claim 1 , wherein the reducing agent is a cyclic ethylenically unsaturated compound having an allylic hydrogen atom, a phosphorous compound with oxidation number l-IV and a valence of 3 to 5 or a sulfur compound with oxidation number I- IV and a valence of 2 or 4 or a mixture of said reducing agents. 4. A composition according to claim 3, wherein the reducing agent is a mixture of a cyclic ethylenically unsaturated compound having an allylic hydrogen atom and a phosphorous compound with oxidation number l-IV and a valence of 3 to 5 or a sulfur compound with oxidation number l-IV and a valence of 2 to 4. 5. A composition according to claim 1 , wherein the reducing agent is H 3 PO 2 (phosphinic acid), H 4 P 2 O 4 (hypodiphosphonic acid), H 3 PO 3 /H 4 P 2 O 5 (phosphonic-/diphosphonic acid), H 4 P 2 0 6 (hypodiphosphoric acid), H 2 S 2 O 2 /H 2 S 2 O 3 (sulfoxylic-/ thiosulfuric acid), H 2 S 2 O 4 (dithionic acid), H 2 SO 3 /H 2 S 2 O 5 (sulfurous-/disulfurous acid), R-S-OH (sulfenic acid) or R-S=0-OH (sulfinic acid) or and their ammonium, alkali metal or alkali earth metal salts. 6. A composition according to claim 5, wherein the reducing agent is H 3 PO 2 (phosphinic acid), or a Na, K, Ca, Mg or ammonium salt thereof, with or without crystal water. 7. A composition according to claim 1 , wherein the reducing agent is a cyclic mono-, sesqui- or di-terpene having an allylic hydrogen atom. 8. A composition according to claim 1 , wherein the reducing agent is γ-terpinene or α- phellandrene 9. A composition according to claim 1 , wherein the reducing agent is present in an amount of 0.01% to 5% based on the weight of the polymer. 10. A process for improving the color of an oligomer, cooligomer, polymer or copolymer or \ blends thereof, containing a stable free nitroxyl radical N— O« ; / by adding a reducing agent to said polymer and heating said mixture to above the glass temperature in case of amorphous polymers or above the melting point in case of crystalline or semi-crystalline polymers; with the proviso that essentially no polymerizable monomer is present. 11. A process according to claim 10 for improving the color of polymers, obtained by radical polymerization, which polymerization has been carried out in the presence of a stable free \ nitroxyl radical N— O' and a source of free radicals capable of initiating the / \ polymerization, or in the presence of a nitroxyl ether N— O — X . wherein X represents a group having at least one carbon atom and is such that the free radical \ derived from X is capable of initiating polymerization and the remaining N— O« radical forms a stable free nitroxyl radical; by adding a reducing agent to said polymer and heating said mixture to above the glass temperature in case of amorphous polymers or above the melting point in case of crystalline or semi-crystalline polymers; with the proviso that essentially no polymerizable monomer is present. 12. A process according to claim 9, wherein the mixture is heated to 50°-150° C above the glass temperature in case of amorphous polymers or 20°-180° C above the melting point in case of crystalline or semi-crystalline polymers. 13. Use of a reducing agent for improving the color of an oligomer, cooligomer, polymer or \ copolymer or blends thereof, containing a stable free nitroxyl radical N— O»

Inventors: PFAENDNER RUDOLF, ROTH MICHAEL, WUNDERLICH WIEBKE, PFAENDNER, RUDOLF, ROTH, MICHAEL, WUNDERLICH, WIEBKE
Applicants: CIBA SC HOLDING AG, PFAENDNER RUDOLF, ROTH MICHAEL, WUNDERLICH WIEBKE, CIBA SPECIALTY CHEMICALS HOLDING INC., PFAENDNER, RUDOLF, ROTH, MICHAEL, WUNDERLICH, WIEBKE
Application year: 2000
Main classification: C08K5
IPC codes: C08K3, C08K5, C08L101