ABSORBENT ARTICLE COMPRISING TOPSHEET WITH LOW SURFACTANT OR NO SYNTHETIC SURFACTANT

Abstract: An absorbent article (10) is provided which comprises a topsheet (12), wherein at least a portion of the topsheet (12) has been treated with an aqueous solution comprising a hydrophilic polymer, and optionally an effective amount of a surfactant. The topsheet (12) is treated to render the topsheet (12) hydrophilic without the use of potentially irritating levels of a surfactant. The hydrophilic polymer is preferably aloe vera, methylcellulose, hydroxypropyl methylcellulose, gum arabic, gum acacia, or polyvinyl alcohol. The optional surfactant is used at low, non-irritating levels to aid in the application of the aqueous solution to the topsheet (12), thereby enhancing the ability of the hydrophilic polymer to coat the surface of the treated portion of the topsheet (12) to render the topsheet (12) hydrophilic.

Description: ABSORBENT ARTICLE COMPRISING TOPSHEET WITH LOW SURFACTANT OR NO SYNTHETIC SURFACTANT FIELD OF THE INVENTION This invention pertains to an absorbent article, such as a disposable diaper, sanitary napkin, adult incontinence garment, training pant or the like, which at a minimum comprises a topsheet, and particularly a topsheet that has been treated to render the topsheet hydrophilic with minimal levels of surfactants. BACKGROUND OF THE INVENTION Commonly, an absorbent article, such as a disposable diaper, adult incontinent garment, training pant or sanitary napkin, comprises a topsheet which is at least partially liquid permeable, a liquid-impermeable backsheet, and an absorbent core formed from (1) cellulosic fibers, which typically are comminuted softwood pulp fibers, and (2) distributed particles of a superabsorbent polymer (SAP). The absorbent core is generally positioned between the topsheet and the backsheet. It is known to provide the absorbent article with one or more other layers formed from cellulosic fibers or other materials to perform various liquid-absorbing, liquid-distributing, and cushioning functions. Polymeric materials are generally used to form the topsheet of such absorbent articles. Polyolefin nonwovens are particularly suited for making these type of products. Absorbent articles desirably include a polymeric nonwoven topsheet which provides rapid intake of fluids such as water or urine, minimal spreading of fluid on the surface before fluid penetration, and good wettability. The topsheet should be durable enough to survive multiple fluid insults. Polyolefin nonwovens and other types of polymeric fabrics are normally hydrophobic. In order to effectively absorb water, the polymeric fabrics must be treated to become hydrophilic. Polymeric fabrics may be rendered hydrophilic by applying a surfactant to the fabric. Conventional surfactants for treating polymeric fabrics include non-ionic surfactants such as octylphenoxypolyethoxy ethanol. Although such conventional surface treatments are effective in making polymeric fabrics wettable, there are still some problems. For example, conventional surface treatment compositions are relatively easily rubbed-off the fabric, particularly when the fabric is wetted. Such surface treatments are often substantially completely removed from the polymeric fabric after only one liquid insult or washing. After the surface treatment is removed, the polymeric fabric again becomes water-repellent and less effective in absorbing water. In order to compensate for the tendency of conventional surface treatments to rub off, conventional surface treatments are often applied to the polymeric fabrics in large quantities. Heavy applications lead to increased costs. Further, such levels of surfactants have been known to cause skin irritation in some individuals, particularly those with sensitive skin. Generally, surfactant levels as high as 1% by weight of the treated portion of the topsheet, and more specifically between 0.3% and 0.6% by weight of the treated portion of the topsheet, have been used. In the past, it was generally believed that applications any less than these would not permit adequate wetting of the topsheet. For example, U.S. Patent No. 5,057,361 to Sayovitz et al. discloses a durable surface treatment for improving the wettability of polymeric fabrics, and particularly treatment of polymeric fabrics with a primary surfactant having a low solubility in water. The primary surfactant is applied to the fabric in an aqueous solution along with a fugitive co-surfactant or co-wetting aid which wets the polymeric fabric during application of the primary surfactant and provides for substantially uniform distribution of the primary surfactant onto the fabric. Although the surface treatment disclosed in the Sayovitz '361 Patent is said to improve wettability of polymeric fabrics, there is still a risk of skin irritation associated with the relatively high levels of surfactants used. Likewise, U.S. Patent No. 5,620,788 to Garavaglia et al. discloses a wettable polymeric fabric comprising a normally water repelling fabric and a sorbitol succinate surfactant substantially uniformly distributed on the surface of the fabric. Suitable succinate surfactants are said to include ethoxylated amino sorbitol succinate salt and alkenyl succinate anhydride ethoxylated fatty amine salt. The succinate surfactant is substantially uniformly distributed on the surface of the polymeric fabric in an aqueous composition comprising a co- wetting aid. The co-wetting aid reduces the surface tension of the aqueous composition and is present in an amount sufficient so that the surfactant is uniformly distributed on the surface of the polymeric fabric during application of the aqueous composition to the surface of the polymeric fabric. The '788 Patent to Garavaglia also discloses that the polymeric fabric includes the first surfactant in an effective amount up to about 3% by weight of the treated portion of the fabric and the second surfactant in an effective amount up to about 3% by weight of the treated portion of the fabric. Preferably, the polymeric fabric includes the first surfactant in an amount from about 0.1% to about 3.0% by weight of the fabric and the second surfactant in an amount from about 0.1% to about 3.0% by weight of the fabric. Although the polymeric fabric disclosed in the '788 Patent is said to improve wettability, the levels of surfactant used still have the potential to cause skin irritation. Among other things, this invention has resulted from ongoing efforts to improve the wettability of the topsheet of an absorbent article, while minimizing the use of surfactants which may cause skin irritation without sacrificing topsheet performance. SUMMARY OF THE INVENTION Accordingly, an object of the present invention is to provide an absorbent article having an improved treated topsheet. Another object of the present invention is to provide an absorbent article having a treated topsheet with enhanced wettability and which at the same time reduces the potential for skin irritation by employing lower levels of surfactants than have been used in the past. Accordingly, the present invention is directed to a topsheet for an absorbent garment. The topsheet is treated with less surfactant than previously used in prior art absorbent garments. Reduced surfactant levels are believed to provide a topsheet that would be potentially milder to sensitive skin. This invention is in part premised on the unexpected discovery that certain combinations of surfactants and hydrophilic polymers provide equal or improved topsheet performance while using a fraction of the surfactant which has conventionally been employed. The surfactant and hydrophilic polymers are mixed in an aqueous solution and applied to the topsheet in amounts sufficient to promote good wettability for urine absorption. These and other objects, features and advantages of this invention are evident from the following description of the preferred embodiments of this invention, with reference to the accompanying drawings. BRIEF DESCRIPTION OF THE DRAWINGS FIG. 1 is a fragmentary, perspective view of a disposable diaper exemplifying an absorbent article according to this invention, in an assembled condition. FIG. 2 is a fragmentary, perspective view of the disposable diaper of FIG. 1 , in a flattened condition. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS The present invention is directed to an absorbent article such as a diaper, training pants, adult incontinent products and sanitary napkins, comprising a topsheet, wherein at least a portion of the topsheet has been treated with an aqueous solution comprising a hydrophilic polymer and optionally an effective amount of a surfactant. Though the present invention is disclosed primarily in reference to surface treatments of nonwovens used as topsheets, it will be readily apparent to those skilled in the art that the low surfactant treatments can be applied to non- woven structures used as transfer or acquisition sublayers of absorbent garments. In this case, the non-woven usually comprises polyester, polypropylene or polyethylene fibers. The surface treated topsheet of the preferred embodiments is preferably formed from polymeric fabrics such as polyolefin nonwoven fabrics. Common polyolefin nonwoven fabrics include polypropylene and polyethylene spunbonded fabrics. Such fabrics are typically produced by processes disclosed in the following patents: U.S. Patent No. 4,340,563 to Appel et al.; U.S. Patent No. 3,692,618 to Dorschner et al.; U.S. Patent No. 3,338,992 to Kinney; U.S. Patent No. 3,341,394 to Kinney; U.S. Patent No. 3,502,538 to Levy; U.S. Patent No. 3,502,763 to Hartmann; U.S. Patent No. 3,909,009 to Hartmann; and U.S. Patent No. 3,542,615 to Dobo et al., all of which are hereby incorporated by reference. Additionally, the topsheet of the present invention can be formed from nonwoven bicomponent polymeric fabrics. Nonwoven bicomponent fabrics are typically produced by processes such as are disclosed in U.S. Patent No. 3,423,266 to Davies et al. and U.S. Patent No. 3,595,731 to Davies, et al, which are hereby incorporated by reference. The wettability of the normally hydrophobic topsheet is enhanced according to the present invention by the application of an aqueous solution comprising a hydrophilic polymer to at least a portion of the topsheet. A hydrophilic film is thereby formed on the surface of selected portions of the topsheet to render it hydrophilic without the addition of elevated levels of surfactants, which have the potential to cause skin irritation to sensitive or damaged skin, i.e., skin already exhibiting diaper rash. Different surfactants are traditionally applied at different levels. By way of example, but without intending to limit the invention, dioctyl sodium sulfosuccinate sold as TRITON ™ GR-5M (manufactured by Union Carbide of Danbury, CT) is typically applied to spunbonded nonwoven so that, when dry, it comprises about 0.3% by weight of the treated portion of the topsheet. Alternatively, sodium alkylarylpolyethersulfonate sold as TRITON™ X-200 may be applied to the topsheet. Another surfactant, SILASTOL™ PST (manufactured by Schill & Seilacher of Bδblingen, Germany), is recommended to be applied at a rate so that, when dry, it comprises about 0.4-0.5% of the treated portion of the spunbond nonwoven topsheet. Treatments above these levels are believed to provide the potential to cause skin irritation. To render a nonwoven hydrophilic, it is necessary to coat the surfaces of individual fibers which form the topsheet. Accordingly, the surface tension of the aqueous solution must be sufficiently low in order to wet the hydrophobic nonwoven during application of the aqueous coating and subsequent drying. In a preferred embodiment of the present invention, the aqueous solution comprising the hydrophilic polymer is applied to at least one portion of the topsheet in conjunction with low, non-irritating levels of a surfactant. According to the present invention, it has been unexpectedly discovered that surfactant may be used in quantities much lower than those previously used to treat topsheets, without sacrificing topsheet performance. The surfactant facilitates the application of the aqueous solution to the surface of the topsheet by lowering the surface tension of the aqueous solution containing the hydrophilic polymer. In other words, the surfactant enhances the ability of the hydrophilic polymer to coat the surface of the treated portions of the topsheet. The hydrophilic polymer of the present invention is preferably one suitable for use in hygienic applications and which can substantially coat the surface of the fibers of the treated portions of the topsheet to render those portions of the topsheet hydrophilic. The hydrophilic polymer is preferably applied with or without the aid of a surfactant. Preferably, the hydrophilic polymer is a non-surface active polymer such as aloe vera, methylcellulose, hydroxypropyl methylcellulose, gum arabic, gum acacia, and polyvinyl alcohol. The hydrophilic polymer is present in the aqueous solution in an amount effective to substantially coat the treated portion of the topsheet, with lower than conventional applications of surfactant, i.e., 0.25% when dry. The term "substantially coat" means that the fibers forming the topsheet are substantially entirely coated with the hydrophilic polymer to such a degree as to render the surface of the topsheet hydrophilic. Preferably, the hydrophilic polymer, when dry, is present on the treated portion of the topsheet in an amount at least about 0.05%o- 1.0% by weight of the treated portion of the topsheet, with a particularly preferred range being about 0.05% to about 0.1% by weight of the dry treated portion of the topsheet. Given the expense of the hydrophilic polymer, particularly aloe, the upper limit of polymer application is primarily defined by economic considerations, though higher levels of the hydrophilic polymer are contemplated by the present invention, such as where the hydrophilic polymer is less expensive, e.g., where methylcellulose or gum arabic are used. If employed, the optional surfactant can be any known surfactant suitable for use in skin contact hygienic applications, as is generally known in the art, and should have a surface tension which is less than the apparent surface free energy of the topsheet. For example, an untreated polypropylene nonwoven fabric, which is hydrophobic, typically has an apparent surface free energy of about 36 ergs/cm . Polyester nonwoven, used as a transfer layer, has a surface free energy of about 43 ergs/cm . Particularly preferred surfactants for use in the present invention include, but are not limited to, TRITON™ GR-5M and SILASTOL™ PST. In the preferred embodiments, it is desirable, though not required, to employ the lowest amount of surfactant which is effective in spreading the hydrophilic polymer on the surface of the treated portion of the topsheet. This invention is premised in part on the unexpected discovery that hydrophobic topsheets may be rendered hydrophilic with a fraction of the surfactant than has been employed in the past, when combined with certain hydrophilic polymers, all the while sustaining and even in some cases improving topsheet performance. The surfactant is present in the aqueous solution sufficient to lower the surface tension of the aqueous solution to a level below about 40 mN/m, more preferably below about 35 mN/m, and most preferably below about 32 mN/m. At these surface tensions, the aqueous solution effectively wets the untreated portion of the topsheet and coats that portion with the hydrophilic polymer. By way of example, but without limiting the invention, the surface tension of water is about 72.8 mN/m, and an aloe vera/water solution has a surface tension of about 71 mN/m. At the preferred concentrations, for example about 30:70 ratio of aloe vera to surfactant at a total solids concentration of about 1%, the surface tension of an aloe vera/surfactant water solution is about 31 mN/m. A sufficient amount of the aqueous solution is applied to the nonwoven such that upon drying the surfactant is present on the treated portions of the topsheet so that when dry it comprises less than about 0.25% by weight of the treated portions of the topsheet, more preferably less than about 0.125% by weight of the treated portions of the topsheet, and most preferably less than about 0.1% by weight of the treated portions of the topsheet. There is evidence that the combination of the surfactant in combination with the hydrophilic polymer provides an otherwise unexpected synergistic result. A 0.82% concentration SILASTOL™ PST treatment solution has a surface tension of about 35.3 mN/m. By comparison, a 0.25% concentration of aloe vera in a treatment solution has a surface tension of about 71.4 mN/m. Surprisingly, a solution consisting of 0.82% PST and 0.25% aloe vera has a surface tension of about 31.5 mN/m. In other words, the addition of aloe vera at a 0.25% concentration to a 0.82% SILASTOL™ PST solution lowers the surface tension from 35.3 mN/m to 31.5 mN/m. It is surprising to discover that a non-surface active polymer, such as aloe vera, can further reduce the surface tension of a surfactant solution by an additional ten percent. The aqueous solution comprising the aloe vera and surfactant is prepared by vigorously pre-mixing the required amount of aloe vera with a portion, e.g., about 10%), of the total water needed for the batch application. This premix is added to the remainder of the water. The surfactant is then added to the solution. This solution may be prepared at room temperature. This method of preparation is applicable to spray and kiss-coat (also known as etched roll or gravure roll) applications, but not foam applications. Foam applications are generally prepared on-line. In this case, each of the surfactant and hydrophilic polymer are supplied from master tanks at the appropriate concentrations to a foam generator as is known to those skilled in the art. The target dry add-on concentration can be achieved by adjusting the concentration of total solids in the aqueous solution and the amount of aqueous solution applied to the nonwoven. Those skilled in the art will recognize many ways to arrive at the preferred target dry concentration by appropriate modification of the foregoing preferred levels for specific methods of application. Low levels of hydrophilic additives such as chamomile and echinacea, and low levels of hydrophobic additives such as Vitamin E, tocopherol acetate, and hamamelis can be added at levels up to less than about 10% of the hydrophilic polymer without significantly reducing the performance of the topsheet. These additives are recognized as providing potential benefits in skin contact hygienic applications. In another preferred embodiment, the synthetic surfactant may be replaced with phospholipids such as phosphoglycerides and sphingolipids. Particularly preferred phosphoglycerides are lecithin and cephalins. Lecithin is a naturally occurring surfactant. When lecithin is employed, no amount of additional surfactant is required to enhance the ability of the hydrophilic polymer to coat the surface of the treated portions of the topsheet. After the nonwoven is wetted with the aqueous solution, it is preferably dried by, e.g., directing the nonwoven through a forced hot air oven or across a bank of infrared lights, steam cans, dielectric dryers or other conventional drying apparatuses as are known to those skilled in the art. The non-woven typically moves across the heating medium at the line speed at which the aqueous solution is applied. Typical line speeds for application of the aqueous solution are around 500-1000 ft/min. As shown in FIGS. 1 and 2, the topsheet treated with the aqueous solution may be employed, for example, in a disposable diaper 10. The disposable diaper 10 may be appropriately sized for infant use or for adult use. If sized for adult use, the disposable diaper 10 may be also called an incontinent garment. It may be here noted that this invention may be also embodied in a wound dressing or another absorbent article other than a disposable diaper, e.g., training pant, adult incontinence garment, sanitary napkin, or the like. Broadly, the disposable diaper 10 comprises a topsheet 12 as described above, a liquid-impermeable backsheet 14, and an absorbent core 16 positioned between the topsheet 12 and the backsheet 14. The disposable diaper 10 has tape fasteners 18, elasticized waistbands 20, and other features well known to those skilled in the art. The topsheet 12 and the backsheet 14 may be bonded adhesively around outer edges 22 of the disposable diaper 10, in a known manner, so as to encapsulate the absorbent structure 16. As described above, the topsheet 12, also called a facing sheet, may be made from polymeric fibers such as polyolefins. The backsheet 14 may be made from a synthetic polymeric film, such as a polyethylene film. The disposable diaper 10 may be substantially similar to the disposable diaper disclosed in Huffman et al. U.S. Patent No. 5,403,301, or in Chmielewski U.S. Pat No. 5,891,120, both assigned to the assignee of the present invention, the disclosures of which are incorporated herein by reference in a manner consistent with this disclosure. As shown in FIG. 2, the absorbent core 32 has an elongate, central portion 40 with a front end 42 and a back end 44, along with two ears 46 near the front end 44. The topsheet 12 is treated with an aqueous solution comprising a hydrophilic polymer according to the present invention to substantially coat the surface of at least a portion of the topsheet to thereby render the topsheet hydrophilic. In one embodiment of the present invention, at least about 35% of the surface of the topsheet is treated. Preferably, the treated portion of the topsheet 12 is that portion which generally corresponds in location to the absorbent core 32, and more preferably that portion which corresponds in location to the central portion 40 of the absorbent core 32. When the topsheet of the preferred embodiments is incorporated into diapers, other diaper configurations are possible without departing from the scope of the preferred embodiments. For instance, in-board leg gathers, i.e., elasticized standing leg gathers disposed inboard of the leg elastics, may be employed. In this situation, the portion of the topsheet located between the standing leg cuffs or gathers is preferably treated with the aqueous solution to render it hydrophilic. The outer portions of the topsheet in this configuration may be left untreated, as urine insults are generally confined between the standing leg cuffs. The untreated outboard portions of the topsheet would advantageously reduce rewetting and contribute to overall liquid containment. In an alternative embodiment, the nonwoven topsheet could be substituted with an apertured plastic film. In this alternative configuration, the apertured plastic film serving as the topsheet is treated in a manner similar to the nonwoven topsheet described previously. The apertured film topsheet, as treated with the surfactant, is rendered hydrophilic with correspondingly less surfactant than has been used in the prior art. Advantageously, such apertured film topsheets also exhibit performance criteria, such as strikethrough and rewet, which are as good as, or better than, conventional topsheets employing higher concentrations of surfactant. Surface treatment processes within the scope of the present invention include kiss-coating and spraying methods. Suitable kiss-coating and spraying methods are disclosed in U.S. Patent No. 5,620,788 to Garavaglia et al. and U.S. Patent No. 5,635, 191 , the disclosures of which are incorporated herein by reference in a manner consistent with this disclosure. Other methods include various foam application techniques. However, it should be understood that the practice of the present invention is not limited to the above-described methods. The following examples are designed to illustrate particular embodiments of the present invention and demonstrate the efficacy of the present invention as compared to conventional surfactant-containing absorbent articles. Example 1 Strikethrough Rewet of Diapers Made with Low Surfactant Topsheet Treated with TRITON™ or SILASTOL™ Sample Description: Paragon Trade Brands' Size Large Ultra 3 diapers were made according to the products' specifications, except that the central portions of the topsheet were treated according to the following three spray application concentrations: 1) 0.075% SILASTOL™ PST, 0.05% aloe; 2) 0.075% TRITON™ GR-5M, 0.05% aloe; and 3) control standard topsheet treated with 0.3% TRITON™ GR- 5M. All numerical values are percentages by weight of the treated portions of the topsheet. Results and Conclusions: Based on the results in Table 1 below, both surfactants in the low surfactant topsheet formula (treatments (1) and (2) above) of the preferred embodiments perform similar to the control topsheet (treatment (3) above) for strikethrough/rewet testing of diapers. Notably, treatments (1) and (2) employ only a fraction of the surfactant of the control, yet topsheet performance is not compromised. Strikethrough is a measure of the rate of absorption of the diaper. Rewet is a measure of the surface wetness of the diaper. Both are affected by the wettability of the topsheet. The strikethrough test is performed by laying the diaper flat and placing an ED ANA (European Disposables and Nonwovens Association) dosing head on the surface of the diaper topsheet. The prescribed amount of fluid, namely 100 ml. of a solution containing 0.9% saline, is metered into the ED ANA dosing head. The time required for all fluid to be absorbed into the diaper core is recorded as the strikethrough time in seconds. After the first dose, the diaper is placed under a load of 0.5 psi for 10 minutes. Then, about 18 grams of pre- weighed dried filter paper is placed on top of the diaper core under a load of 0.5 psi for 10 minutes. The amount of test fluid absorbed by the filter paper is recorded as the rewet in grams. This test is then repeated for second and third doses. The results obtained on six diapers are averaged and tabulated below. TABLE 1 Performance of Low Surfactant Topsheets on Diapers Based on the hydrophilicity of the low surfactant topsheet treatments, the strikethrough times were comparable or better, i.e., lower, than those obtained for a conventional surfactant treated topsheet (Control). These results reveal the surprising and unexpected discovery that the amount of surfactant employed in rendering a topsheet hydrophilic may be significantly reduced, without sacrificing topsheet performance. Furthermore, it was surprising and unexpected that the low surfactant topsheet provided better, i.e., lower, rewet performance. Furthermore, as demonstrated above, the amount of surfactant employed in the topsheet treatments of the preferred low surfactant topsheet is substantially less than that of the Control topsheet. In the control topsheet, 0.3% by weight of the treated portion of the topsheet contained surfactant, whereas only 0.075 wt. % of the treated portion of the topsheet contained surfactant in the preferred embodiments, treatments (1) and (2). This represents a 75% reduction in the amount of surfactant employed in the topsheets of the preferred embodiments as compared to the Control topsheet. The hydrophilic polymer in an amount of only 0.05 wt. % is believed to replace the remaining 0.225 wt. % surfactant that was required in the control topsheet. It was an unexpected discovery that in the preferred formulations, the hydrophilic polymer could in such small quantities replace a much larger amount of surfactant, while providing improved topsheet performance. Example 2 Strikethrough Rewet of Diapers Made with Low Surfactant Topsheet Treated with TRITON™ or SILASTOL™ and Vitamin E Sample Description: Paragon Trade Brands' Size Large Ultra 3 diapers made in accordance with present product specifications were employed, except that portions of the topsheet were treated according to the following three spray application concentrations: 1) 0.075% SILASTOL™ PST, 0.05% aloe vera and 0.005% Vitamin E, 2) 0.075% TRITON™ GR-5M, 0.05% aloe vera, and 0.005% Vitamin E, and 3) the control standard topsheet treated with 0.3% TRITON™ GR-5M (standard Poly Bond topsheet). The topsheets were 15 gsm spunbond, made at Poly Bond in Waynesboro, VA. The strikethrough and rewet testing protocols in this Example 2 are the same as that described above in Example 1. Results and Conclusions: As shown in Tables 2 and 3 below, the performance of the low surfactant topsheets falls within the expected range of results expected for the standard topsheet. TABLE 2 Performance of Low Surfactant Topsheets on Diapers The foregoing results in Table 2 are consistent with the performance of diapers having a low surfactant topsheet in Table 1 above. The addition of hydrophobic materials such as Vitamin E to the low surfactant formulation does not degrade the strikethrough and rewet performance relative to diapers having topsheets with a low surfactant and hydrophilic polymer formulation (Control II). Another test, multiple void runoff, was also performed on each of the diaper samples of Example 2. Multiple void runoff is a measure of the hydrophilicity of the diaper topsheet. The diaper is stretched flat and inclined at an angle of about 30 degrees. Three 100 ml. doses are applied at a point on the diaper pad that is about two inches from the front end of the diaper core. The doses are applied at a rate of about 7 ml./sec. The amount of fluid running off the end of the diaper is collected and weighed. Under this protocol, the following results of Table 3 were obtained: TABLE 3 Multiple Void Runoff Performance of Low Surfactant Topsheets on Diapers The runoff data of Table 3 demonstrates the unexpected performance advantages of using TRITON™ along with aloe vera and Vitamin E over the significantly higher surfactant concentrations of Control I. Even after the third dosing, the TRITON™/aloe/Vitamin E formulation exhibited no runoff, i.e., all of the fluid was collected within the diaper, indicating high topsheet hydrophilicity and high durability of the topsheet surface treatment. Example 3 Strikethrough/Rewet and Multiple Void Runoff of Diapers made with Topsheet Treated with Low Surfactant/Methyl Cellulose Sample Description: Paragon Trade Brands' Size Large diapers were made according to product specifications, except a portion of the topsheet was treated as follows: 0.075% by weight SILASTOL™ PST and 0.25% by weight methyl cellulose (i.e., percent by weight of the treated portion of the topsheet). The run speed was 130 fpm. The topsheet was 15 gsm spunbond. Samples were made for testing by removing the topsheet from machine made diapers and replacing the topsheet with the above-described topsheet. Results and Conclusions: As shown in Tables 4 and 5 below, the performance of the low surfactant topsheets coated with methyl cellulose fall within the expected range of results for a standard topsheet and an aloe vera treated topsheet as shown in Tables 1-3 above. TABLE 4 Performance of Low Surfactant Topsheets on Diapers TABLE 5 Multiple Void Runoff Performance of Low Surfactant Topsheets on Diapers Example 4 Modified Multiple Void Runoff of Lab Treated Low Surfactant/High Aloe/Vitamin E Topsheet Samples Sample Description: Lab treated samples were prepared using 15 gsm untreated spunbond. Samples were cut to approximately 170mm x 480mm. The target treatment was as follows: Sample #1 was treated with an aqueous solution with a target add-on of 0.075% TRITON™ GR-5M, 0.05% aloe vera and 0.005% Vitamin E. Sample #2 was treated with an aqueous solution with a target add-on of 0.075%) SILASTOL™ PST, 0.05% aloe vera and 0.005% Vitamin E. Sample #3 was treated with an aqueous solution with a target add-on of 0.1% SILASTOL™ PST, 0.05% aloe vera and 0.005% Vitamin E. The control was a commercial grade topsheet made on a production line, with a target add-on of TRITON™ GR-5M of 0.3%. Multiple Void Run-off Testing Protocol This protocol is designed to test the durability and amount of "wash-off ' of the surfactant treatment. This test was performed in the same manner as the standard test described above, with the exception that 10 layers of 60 gsm airlaid to simulate the diaper core, cut to approximately 200mm x 500mm, were placed under the nonwoven for the absorbent material. The wet airlaid was replaced after each void with 10 layers of dry airlaid. Results and Conclusions: As indicated in Table 6 below, the results for the lab made samples do not indicate any adverse effects from the addition of Vitamin E in a low surfactant treatment. Also, the two surfactants performed similarly for run-off testing in the low surfactant/high aloe/Vitamin E treatment. This data is consistent with that in the Examples above, where a topsheet treated with low concentrations of surfactant were assessed on diapers. As above, the lower concentrations of surfactant, coupled with low concentrations of Vitamin E, did not degrade topsheet performance. It should be noted that failure of a multiple void run-off test requires 20 gms of fluid run-off over three doses. The data obtained for all of the test samples were well within this product specification. TABLE 6 Multiple Void Run-Off Performance of Low Surfactant Topsheets Example 5 Multiple Void Runoff Test of Topsheet Made with Low Surfactant/ Aloe Vera/Vitamin E Sample Description : A Poly Bond topsheet was treated with an aqueous solution comprising aloe vera and surfactant to obtain a treated topsheet containing 0.075 % by weight surfactant, 0.05 % by weight aloe vera, and 0.01 % by weight Vitamin E. The topsheet was commercially manufactured, 16 gsm SMS (spunbond- meltblown-spunbond), untreated, and cut to a sample size of 162mm x 508mm. Results and Conclusions: There was no runoff for the multiple void runoff test protocol described previously. The treatment of the test nonwoven did not wash off after 3 doses. The foregoing treated topsheets of the preferred embodiments may be further treated with lotions or other emollients as is well known in the art. Such lotions tend to render the topsheet hydrophobic. The invention of the preferred embodiments provides improved performance and as such provides the opportunity to use lotions and emollients without sacrificing topsheet performance. Although the invention has been described in connection with the preferred embodiments, these embodiments are not intended to limit the invention. Those skilled in the art will readily appreciate that various modifications may be made to the preferred embodiments without departing from the scope and spirit of the invention as defined by the appended claims.

Claims: CLAIMS What is claimed is: 1. An absorbent article comprising a nonwoven of hydrophobic fibers, wherein at least one target surface of said nonwoven is treated with an aqueous solution comprising a hydrophilic polymer and a surfactant; wherein said hydrophilic polymer and surfactant substantially coat the target surface of said nonwoven, thereby rendering said target surface of said nonwoven hydrophilic; wherein the surfactant is present on the target surface in an amount less than about 0.25% by weight of the target surface of the nonwoven. 2. The absorbent article of claim 1, further comprising a topsheet, a backsheet and an absorbent core disposed therebetween, said nonwoven comprising a transfer layer positioned between said absorbent core and said topsheet. 3. The absorbent article of claim 1 , wherein said nonwoven is employed as a topsheet of the absorbent article for contact with the skin. 4. The absorbent article of claim 3, wherein said topsheet comprises polyolefinic fibers or film. 5. The absorbent article of claim 3, wherein the hydrophilic polymer and the surfactant are present in the aqueous solution at a ratio of about 30:70. 6. The absorbent article of claim 3 wherein said hydrophilic polymer is selected from the group consisting of aloe vera, methylcellulose, hydroxypropyl methylcellulose, gum arabic, gum acacia, and polyvinyl alcohol. 7. The absorbent article of claim 3 wherein said hydrophilic polymer is aloe vera. 8. The absorbent article of claim 3, wherein the surfactant is selected from a group consisting of nonionic and anionic surfactants. 9. The absorbent article of claim 8, wherein the surfactant is selected from the group consisting of dioctyl sodium sulfosuccinate (TRITON™ GR-5M), sodium alkylarylpolyethersulfonate (TRITON™ X-200), and SILASTOL™ PST. 10. The absorbent article of claim 8, wherein the surfactant is selected from a group of phospholipids known as phosphoglycerides and sphingolipids. 11. The absorbent article of claim 10, wherein said surfactant is selected from the phosphoglycerides group consisting of lecithins and cephalins. 12. The absorbent article of claim 3, wherein said at least one surfactant is present on the target surface in an amount less than about 0.125% by weight of the target surface. 13. The absorbent article of claim 3, wherein said hydrophilic polymer is present on the target surface in an amount ranging from about 0.05% to about 1% by weight of the target surface. 14. The absorbent article of claim 3 wherein said hydrophilic polymer is present on the target surface in an amount of about 0.05%> by weight of the target surface. 15. The absorbent article of claim 3, said topsheet comprising a matrix of discrete fibers, wherein a coating is deposited on the fibers of the target surface from the aqueous solution; once dry said target surface coating comprises from about 10% to about 50% by weight of a water-soluble hydrophilic polymer and from about 50%> to about 90% by weight of a surfactant. 16. An absorbent article comprising a topsheet with a target surface coating; said target surface coating being present in an amount ranging from about 0.10% to about 0.25%> by weight of the target surface; wherein once dry the target surface coating comprises from about 10% to about 50% by weight of a water-soluble hydrophilic polymer and from about 50% to about 90%) by weight of a surfactant. 17. A method for treating a nonwoven for use in an absorbent article comprising the steps of: preparing an aqueous solution comprising a water-soluble hydrophilic polymer and surfactant at a ratio of about 30:70; applying an aqueous solution to a target surface of the nonwoven; and drying the nonwoven; wherein the hydrophilic polymer and the surfactant are present in the aqueous solution at a total concentration ranging from about 5% to about 25% by weight of the total aqueous solution; and wherein the surface tension of said aqueous solution is less than about 40 mN/m. 18. The method according to claim 17, wherein said nonwoven is employed as a topsheet in the absorbent article.

Inventors: CHMIELEWSKI HARRY J, ERDMAN CAROL L, CHMIELEWSKI, HARRY, J., ERDMAN, CAROL, L.
Applicants: PARAGON TRADE BRANDS INC, PARAGON TRADE BRANDS, INC.
Application year: 2000
Main classification: A61F13
IPC codes: A61F13, A61L15