EXPANDABLE SHEET MATERIAL MANUFACTURE

Abstract: The material (for use in acoustic or RF attenuation) is made by: a) providing a mixture comprising a matrix of elastomer having mixed therewith a sublimable foaming agent which can sublime to produce at least one gaseous decomposition product which is reactive with the matrix to produce at least one solid reaction product; and b) forming the mixture into at least one sheet.

Description: EXPANDABLE SHEET MATERIAL MANUFACTURE The present invention is concerned with manufacture of sheet material, especially sheet material suitable for use in attenuation. It is a general desire to improve the environment through noise reduction. Noise pollution is an environmental problem in many industries. For example noise is a problem in military vehicles, consumer vehicles, factories, and also in communal buildings. It is therefore an aim of the present invention to provide a sheet material suitable for use in attenuation, and which can be used, for example, for acoustic insulation and for noise reduction, or for reduction of interference of radio frequency (RF) waves. Therefore, according to the present invention there is provided a method of manufacturing sheet material, which method includes : a) providing a mixture comprising a matrix of elastomer having mixed therewith a sublimable foaming agent which can sublime to produce at least one gaseous decomposition product which is reactive with the matrix to produce at least one solid reaction product; and b) forming the mixture into at least one sheet. Advantageously, the sheet is subjected to conditions (such as elevated temperature) whereby the sublimable foaming agent is caused to sublime and thereby form the at least one gaseous decomposition product, whereby the sheet is caused to expand with closed cells being formed. A preferred sublimable foaming agent is at least one substantially anhydrous compound which can decompose on sublimation. Suitable examples of such compounds are ammonium salts (such as ammonium chloride) nd/or a sulfate; a particularly preferred such foaming agent is substantially anhydrous aluminium ammonium sulfate (preferably in finely divided particulate or granular form) . Alternatively, the sublimable foaming agent may be an exothermically reactive combination, such as zinc powder mixed with iodine. The at least one gaseous decomposition product typically reacts with the matrix so as to form the closed cells; the closed cells preferably have internal walls which comprise the reaction product of the decomposition product and the matrix. The sublimable foaming agent is preferably in particulate form; preferably the particles have a particle size in the range 25 to 400 microns. The sublimable foaming agent is preferably present in an amount of about 5 to 15 parts per 100 parts of the elastomer. Advantageously, the mixture further includes a filler material, such as particulate carbon black, clay or limestone, or finely divided paper. Particulate silica is preferred. It is preferred that the silica is in finely divided form, preferably in the range of about 50 to 500 microns. A preferred particle size is about 120 microns. If silica is used, it is advantageously waste silica, such as waste silica from skimmings from power station lakes. A further suitable filler is a porous mineral material, such as a montmorillanoid mineral, preferably vermiculite (hydrated magnesium-aluminium-iron silicate) . Optionally, the mixture in step a) may include particulate magnetisable material. The magnetisable material may be a ferrous material, which may, in some embodiments, be coated with copper; this embodiment is particularly preferred when the material is to be used in a Faraday screen. A particularly preferred magnetisable material for use according to the invention is mill scale. Typically, the particulate magnetisable material is finely divided, preferably having a particle size from about 25 to 400 microns (especially preferred being about 300 microns) . The magnetisable material and filler, when present, are preferably in a ratio of about 4 parts by weight of magnetisable material per part by weight of filler. The mixture in step a) may optionally include particulate vulcanised rubber. The particulate vulcanised rubber is preferably present in the elastomer matrix in the. form of discrete particles. The vulcanised rubber should therefore be such that it is substantially free of reaction with the elastomer when the latter is cured. It is preferred that the particulate vulcanised rubber is obtained cryogenically, by comminution of waste rubber compounds (for example, from waste tyres or the like) . Such waste rubber compounds generally include natural rubber and/or SBR. The vulcanised rubber advantageously may include comminuted rubber tyres such as waste or worn tyres. Disposal of waste or worn tyres would previously have been in landfill sites or the like. Therefore, a further advantage of this particular embodiment of the present invention is to provide a use for waste tyres. The above-mentioned vulcanised rubber is preferably in finely divided form. It is further preferred that the vulcanised rubber has a particle size of less than about 500 microns, most preferably less than about 120 microns. An exemplary formulation for the matrix used according to the invention is the following: KELTAN (a Product of DSM-NV Ethylene Propylene Rubber) SPHERON 5000A Medium Fine Carbon Black Zinc Oxide Active Stearic Acid PEG 4000 (polyethylene glycol soap) Britomya BSH 20 (plasticiser) Flexon 815 Liquid (plasticiser) KEZADOL GR (processing aid) RHENOGRAN 580 Sulphur (vulcanising agent) RHENOGRAN TMTD 80 Tetramethylthiuram Disulphide (vulcanising agent) RHENOGRAN MBT 80 Mercaptobenzothiazole (vulcanising agent) RHENOGRAN MBTS 80 Benzothiazyl Disulphide (vulcanising agent) The solid ingredients (including the sublimable foaming agent and the optional ingredients such as magnetisable material, vulcanised rubber and filler material), may be mixed together prior to further mixing with the elastomer, prior to curing or -vulcanisation of the latter. The latter further mixing is typically carried out in a mixer such as a Banbury rotor type mixer. The rotor speed of the mixer is typically in the range of 60 to 100 rpm, preferably about 80 rpm. The elastomer forming the matrix is preferably of a type different to that normally employed in tyres, the latter (as mentioned above) generally including natural rubber and/or SBR, and/or a polyolefin type rubber, such as an ethylene-propylene rubber or EPDM. The sublimable foaming agent may be added to the elastomer before addition of the other solid ingredients, or with the other solid ingredients. Typically the mixing of the solid ingredients with the elastomer is for about 4 to 12 minutes, preferably for about 8 minutes; such mixing is typically at a temperature of about 80°C to 110°C. Exemplary solid mixes for use according to the invention are set out in the following Table 1. Table 1 Matrix Matrix Matrix Matrix A B C D The sheets obtained in step b) may be formed by passing the mixture produced in step a) through a dump mill, then onto a sheeting mill and finally onto a three bowl calender for sheeting off. Advantageously, the thickness of the sheets may be varied. A preferred thickness of the sheets is from about 0.2mm up to about 6mm, when in an unexpanded form. When the attenuation material is to be sheeted, the mixture preferably includes a releasing agent so as to substantially prevent the mixture from sticking to the rollers. A suitable releasing agent is an organo silicone, such as the product commercially sold under the trademark WS180 Struktol. The attenuation level of the material may depend on the thickness of the resulting sheet. The sheets may be used for a wide variety of uses. Typical uses include in buildings (traditionally built buildings with cavity space and roof trusses can be lined with the material according to the present invention) , refitting of buildings (for example, existing buildings that have changed uses to pubs, clubs, discos etc) , building door linings, blinds, in road, rail or air transport (for example as a lining material inside cabins, carriages, tunnels and barriers on roads) and in general household and industrial machinery. Advantageously, the method may further include the step of curing the elastomer matrix formed in step b) . The material may be cured in a number of ways, for example, in line ovens or microwave ovens, however a fast opening press is preferred. It is preferred that curing is at a temperature in the range of about 165°C to about 180°C; such curing would also cause sublimation and decomposition of the foaming agent. A lower temperature range may permit curing of the elastomer matrix; however, this will incur a longer cycle time. Preferably, such curing takes place in a press such that on relief of the press loading, the matrix is permitted to expand following, sublimation of the sublimable foaming agent. The matrix subsequently contracts to a volume substantially greater than the volume of the matrix prior to the initial expansion. As the curing takes place hollow cores are formed in the matrix; it is the formation of the hollow cores which results in the cured matrix being substantially greater than the volume of the matrix prior to the initial expansion. Typically, the mixture further includes stearic acid, preferably in the range 0.1 to 0.25% (further preferably in the range 0.13% to 0.17%) by weight of the mixture. Advantageously, the stearic acid produces stearate which result in a hardening of the surface of the core. Advantageously, the sheets formed in step (b) may be laminated to paperboard, plasterboard, woven fabrics or the like. According to a further embodiment of the present invention, it is preferred that at least one fire retardant is added to the material prior to step b) . Such fire retardants include aluminium sulfate based compounds, such as the compound commercially available under the trademark BACO Superfine 7 from the British Aluminium -Company. In this embodiment it is preferred that the material includes a releasing agent . According to a second aspect of the present invention, it is preferred that the material is magnetised to provide hysteresis characteristics. Advantageously a magnetic screen created around the material provides attenuation of electromagnetic induction and radio frequency (RF) waves. According to yet a further embodiment of the present invention, neoalkoxy zirconate may be added to the mixture in step (b) so as to promote adhesion of the material to a number of materials (for example, steel, aluminium, high performance polymers such as polyamides, or other polymer such as PET) , and also to enhance dispersion of particulate material in the elastomer matrix. It is preferred that the neoalkoxy zirconate is added in the ratio of about 5 parts per 100 of the elastomer.

Claims: CLAIMS : 1. A method of manufacturing sheet material, which method includes : a) providing a mixture comprising a matrix of elastomer having mixed therewith a sublimable foaming agent which can sublime to produce at least one gaseous decomposition product which is reactive with the matrix to produce at least one solid reaction product; and b) forming the mixture into at least one sheet . 2. A method according to claim 1, characterised in that the sheet is subjected to conditions whereby the sublimable foaming agent is caused to sublime and thereby form the at least one gaseous decomposition product, whereby the sheet is caused to expand with closed cells being formed. 3. A method according to claim 1 or 2 , characterised in that the at least one gaseous decomposition product reacts with the matrix so as to form the closed pores. 4. A method according to claim 3, characterised in that the closed pores have internal walls which comprise the reaction product of the decomposition product and the matrix. 5. A method according to any of claims 1 to 4, characterised in that the sublimable foaming agent is in finely divided, particulate or granular form. 6. A method according to any of claims 1 to 5, characterised in that the sublimable foaming agent includes at least one substantially anhydrous compound which can decompose on sublimation. 7. A method according to claim 5, characterised in that the sublimable foaming agent includes an ammonium salt or a sulfate. 8. A method according to any of claims 1 to 7, characterised in that the sublimable foaming agent includes an exothermically reactive combination. 9. A method according to claim 8, characterised in that the sublimable foaming agent includes zinc powder mixed with iodine. 10. A method according to any of claims 1 to 9, characterised in that the sublimable foaming agent is in particulate form having a size in the range of about 25 to about 400 microns. 11. A method according to any of -claims 1 to 10, characterised in that the sublimable foaming -agent is present in an amount of about 5 to 15 parts per 100 parts of the elastomer. 12. A method according to any of claims 1 to 11, characterised in that the mixture further includes a filler material. 13. A method according to claim 12, characterised in that the filler includes particulate carbon black, clay or limestone, finely divided paper, or a porous mineral material, a montmorillanoid mineral (such as vermiculite - hydrated magnesium-aluminium-iron silicate) . 14. A method according to claim 13, characterised in that the filler includes particulate silica, preferably in the range of about 50 to 500 microns. 15. A method according to claim 14, characterised in that the silica includes waste silica, such as waste silica from skimmings from power station lakes. 16. A method according to any of claims 1 to 15, characterised in that the mixture in step a) includes particulate magnetisable material. 17. A method according to claim 15, characterised in that the magnetisable material is a ferrous material, such as mill scale. 18. A method according to claim 16 or 17, characterised in ferrous material is coated with copper. 19. A method according to any of claims 16 to 18, characterised in that the magnetisable material has a particle size of about 25 to 400 microns. 20. A method according to any of claims 1 to 19, characterised in that the mixture in step (a) further includes particulate vulcanised rubber. 21. A method according to claim 20, characterised in that the particulate vulcanised rubber includes cryogenically comminuted waste rubber. 22. A method according to claim 21, characterised in that the waste rubber is obtained from waste or worn tyres. 23. A method according to any of claims 20 to 22, characterised in that the vulcanised rubber has a particle size of less than about 500 microns. 24. A method according to any of claims 1 to 23, characterised in that solid ingredients present are pre-mixed prior to mixing with the elastomer matrix. 25. A method according to any of claims 1 to 24, characterised in that the elastomer matrix includes one or more of natural rubber, SBR and a polyolefin type rubber . 26. A method according to any of claims 1 to 25, characterised in that the sublimable foaming agent is added to the elastomer matrix prior to, or with the mixing of other solid ingredients. 27. A method according to claim 26, characterised in that the elastomer matrix and the solid ingredients are mixed for about 4 to 12 minutes. 28. A method according to claim 27 or 28, characterised in that the mixing is at a temperature of about 80 to 110°C. 29. A method according to any of claims 1 to 28, characterised in that the sheet obtained in step b) is formed by passing the mixture produced in step a) through a dump mill, then onto a sheeting mill and subsequently onto a three bowl calender for sheeting off. 30. A method according to any of claims 1 to 29, characterised in that the sheet formed in step b) has a thickness of about 0.2mm to about 6mm, when in an unexpanded form. 31. A method according to any of claims 1 to 30, characterised in that at least one fire retardant is added to the material prior to step b) . 32. A method according to claim 31, characterised in that the fire retardant is an aluminium sulfate based compound . 33. A method according to any of claims 1 to 32, characterised in that the mixture includes a releasing agent . 34. A method according to claim 33, characterised in that the releasing agent includes an organo silicone. 35. A method according to any of claims 1 to 34, characterised in that the elastomer matrix formed in step b) is cured. 36. A method according to claim 35, characterised in that the curing is at a temperature in the range of about 165°C to 180°C. 37. A method according to claim 35 or 36, characterised in that the curing takes place in a press such that on relief of the press loading, the matrix is permitted to expand following sublimation of the sublimable foaming agents. 38. A method according to any of -claims 1 to 37, characterised in that the mixture further -includes stearic acid. 39. A method according to claim 38, characterised in that the stearic acid is present in the range 0.1 to 0.25% by weight of the mixture. 40. A method according to any of claims 1 to 39, characterised in that the sheets formed .in step (b) are laminated to paperboard, plasterboard, woven fabrics or the like. 41. A method according to any of claims 1 to 40, characterised in that the material is magnetised so to provide hysteresis characteristics. 42. A method according to any of claims 1 to 41, characterised in that the neoalkoxy zirconate is added to the mixture in step (b) .

Inventors: BRYANT JOHN GRAHAM, BRYANT, JOHN, GRAHAM
Applicants: BRYANT JOHN GRAHAM, BRYANT, JOHN, GRAHAM
Application year: 2000
Main classification: C08J9
IPC codes: B29C44, C08J9