TOUGHENED BENZOCYCLOBUTENE BASED POLYMERS AND THEIR USE IN BUILDING-UP PRINTED WIRING BOARDS

Abstract: The invention is a process for building-up printed wiring boards using metal foil coated with toughened benzocyclobutene-based dielectric polymers. The invention is also a toughened dielectric polymer comprising benzocyclobutene-based monomers or oligomers, ethylenically unsaturated polymer additive, and, optionally, a photoactive compound.

Description: TOUGHENED BENZOCYCLOBUTENE BASED POLYMERS AND THEIR USE IN BUILDING-UP PRINTED WIRING BOARDS Aspects of this invention were made with Government support under Agreement No. MDA972-95-3-0042 awarded by ARPA. The Government has certain rights in the invention. This invention relates to a process for making additional interconnect layers on commercially available printed circuit boards using toughened benzocyclobutene based polymers and metal foils coated with such polymers. This invention also relates to such toughened benzocyclobutene-based polymers. Various printed wiring boards or printed circuit boards (referred to herein as "PWBs") are known and frequently have two to eight layers of laminates. Occasionally, it is desirable to add additional layers to these board structures (see, for example, H. T. Holden, In Printed Circuits Handbook, 4 th ed., C. F. Coombs, Jr., Ed.; McGraw-Hall: New York, 1996, Chapter 4). For high frequency applications, the insulating materials typically used in the PWBs (for example, epoxy materials) may not provide the desired low dielectric loss. Therefore, it would be desirable to have a process and materials, which could provide the desired low dielectric loss. Benzocyclobutene-based polymers (hereinafter referred to as "BCB polymers") are thermosetting polymers. Certain of these polymers have low dielectric constants and thus, are desirable as insulating coatings in various electronics applications (see, for example, "Benzocyclobutene(BCB) Dielectrics for the Fabrication of High Density, Thin Film Multichip Module," Journal of Electronics Materials, Vol. 19, No.12, 1990 and G. Czornyl, M. Asano, R. L. Beliveau, P. Garrou, H. Hiramoto, A. flceda, J. A. Kreuz and O. Rohde, In Microelectronic Packaging Handbook, Volume 2; R. R., Tummala, E. J. Rymaszewski and A. G. Klopfenstein, Eds.; Chapman & Hall: New York, 1997; Chapter 11). However, for certain applications, BCB polymers may not have sufficient toughness. Therefore, it would be desirable to have a BCB polymer with increased toughness without significant loss or degradation of other desirable properties. JP 8-60103 discloses an adhesive sheet comprises a compound having a benzocyclobutene group and a binder polymer. The preferred binder polymers have carbon- carbon unsaturated bonds. The -eference indicates that from 1-95 percent of the composition may be the binder polymer. According to a first embodiment, the present invention is a process comprising providing a printed wiring core board, which comprises a glass fiber reinforced board with conductive metal circuitry, laminating to the printed wiring core board a sheet comprising a foil of a conductive metal and, on the foil, a dielectric layer of a curable composition comprising (a) at least one precursor compound selected from arylcylobutene monomers, arylcyclobutene oligomers, and combinations thereof; and (b) a polymer or oligomer having a backbone comprising ethylenic unsaturation (that is, carbon-to-carbon double bond(s)), wherein, during the lamination step, the dielectric layer is in contact with the printed wiring board, and processing the laminated article to form additional electrical connections. According to a second embodiment, this invention is a preferred composition comprising a) at least one precursor compound selected from arylcylobutene monomers, arylcyclobutene oligomers, and combinations thereof; and b) a polymer or oligomer having a backbone comprising ethylenic unsaturation (that is, carbon-to-carbon double bond(s)) and terminal acrylate or methacrylate groups. The invention is also the partially polymerized (b-staged) reaction product of this composition and the cured reaction product of the b-staged material. According to yet a third embodiment, the invention is a sheet comprising a metal foil and a film comprising the composition of the second embodiment or the partially cured product of that composition. The core board, to which the BCB coated metal foil is laminated, is characterized by having various insulating layers laminated together and separating various metal interconnect lines. Processes for making such PWBs are well-known (see, for example, Printed Circuits Handbook, 4 th Ed., C. F. Coombs, Jr., McGrall-Hill: New York, 1996). Typically, the insulating layers are glass-reinforced epoxy. The metal foil is a very thin layer of a conducting metal, such as Cu or Cu alloy, and is preferably copper. The thickness of the metal foil is preferably 3 to 50 microns. The BCB dielectric layer is preferably coated from a solvent onto foil. Suitable solvents include mesitylene xylenes, toluene, methyl ethyl ketone, cyclic ketones and a mixture of these solvents. After coating, the composition is preferably baked at temperatures from 100°C to 200°C, more preferably 120°C to 180°C in air for 5 to 30 minutes, most preferably at 140°C to 160°C for 10 to 20 minutes. Lamination to the core board may occur according to standard processes, preferably by vacuum hot press at temperatures of 200°C-250°C and pressures of 10-40 Kg/cm 2 . Additional patterning steps may then be performed to the laminate according to known procedures. For example, the metal foil could be stripped or pattern etched followed by via formation with a laser drilling, or the entire laminate could be mechanically drilled through. Electroless plating of additional conductive metal followed by electroplating could be used to form the desired electrical connections. As stated above, the precursor is either an arylcyclobutene monomer, a b-staged oligomer of one or more arycyclobutene monomers, or some combination of b-staged arylcyclobutene oligomers and/or monomers. Preferably, the monomers are of the formula wherein B is an n- valent organic linking group, preferably comprising ethylenic unsaturation, or B 1 is absent. Suitable single valent B 1 groups preferably have the formula - CR 8 =CR 9 Z, wherein R 8 and R 9 are independently selected from hydrogen, alkyl groups of 1 to 6, most preferably 1 to 3 carbon atoms, and aryl groups, and Z is selected from hydrogen, alkyl groups of 1 to 6 carbon atoms, aryl groups, -CO 2 R 7 , wherein R 7 is an alkyl group, preferably up to 6 carbon atoms, an aryl group, an aralkyl group, or an alkaryl group. Most preferably Z is -CO 2 R , wherein R is an alkyl group, preferably up to 6 carbon atoms, an aryl group, an aralkyl group, or an alkaryl group. Suitable divalent B 1 groups include - (CR 8 =CR 9 ) 0 -(Z X ) 0-1 , wherein R 8 and R 9 are as defined previously, o is 1 or 2, and is an alkyl group of 1 to 6 carbon atoms, an aromatic group, or a siloxane group. Most preferably o is 2 and 71 is a siloxane group. Ar 1 is a polyvalent aromatic or heteroaromatic group and the carbon atoms of the cyclobutane ring are bonded to adjacent carbon atoms on the same aromatic ring of Ar 1 , preferably Ar 1 is a single aromatic ring; m is an integer of 1 or more, preferably 1 ; n is an integer of 1 or more, preferably 2-4, more preferably 2; and R 1 is a monovalent group, preferably hydrogen, lower alkyl of up to 6 carbon atoms. The synthesis and properties of these cyclobutarenes, as well as terms used to describe them, may be found, for example, in U.S. Patents 4,540,763; 4,724,260; 4,783,514; 4,812,588; 4,826,997; 4,999,499; 5,136,069; 5,185,391; 5,243,068. According to one preferred embodiment, the monomer (a) has the formula wherein each R 3 is independently an alkyl group of 1-6 carbon atoms, trimethylsilyl, methoxy or chloro; preferably R is hydrogen; each R 4 is independently a divalent, ethylenically unsaturated organic group, preferably an alkenyl of 1 to 6 carbons, most preferably -CH 2 =CH 2 -; each R 5 is independently hydrogen, an alkyl group of 1 to 6 carbon atoms, cycloalkyl, aralkyl or phenyl; preferably R 5 is methyl; each R 6 is independently hydrogen, alkyl of 1 to 6 carbon atoms, chloro or cyano, preferably hydrogen; n is an integer of 1 or more; and each q is an integer of 0 to 3. The preferred organosiloxane bridged bisbenzocyclobutene monomers can be prepared by methods disclosed, for example, in U.S. Patents 4,812,588; 5,136,069; 5,138,081 and WO 94/25903. The preferred compound, where n is 1, q is 0, R 4 is -C=C- R 5 is methyl, and R 6 is hydrogen, is referred to herein as DVS-bisBCB. If an oligomeric precursor is desired, the BCB monomers may be b-staged according to any known process. The monomers may be partially polymerized or b-staged neat (that is, without solvent) by heating (see, for example, U.S. Patent 6,083,661 and U.S. Patent 4,642,329). Alternatively, the monomers may be partially polymerized or b-staged in a solvent (see, for example, U.S. Patent 6,083,661). When oligomeric precursors are used, the weight average molecular weight (Mw) is preferably less than 200,000, more preferably less than 150,000 and preferably greater than 10,000, more preferably greater than 20,000. The second component having the ethylenic unsaturation in the carbon backbone should be selected so that it can withstand the processing conditions (solvents, heating, etc.) used in microelectronics fabrication and not cause a significant deterioration in the electrical insulating properties of the reaction product relative to an unmodified BCB polymer. Suitable materials include polymers based on butadiene, isoprene, ethylene-butene, and ethylene-propylene. Comonomeric units, such as styrene and methylstyrene, may also be used. Preferably, the ethylenically unsaturated polymer is selected from polybutadiene, polyisoprene, styrene-butadiene block copolymers, and styrene-isoprene block copolymers. Applicants have found that the terminal groups on the ethylenically unsaturated polymer can have a profound effect on the performance of the composition. Acrylate or methacrylate terminated polymers are the preferred materials, as recited in the second embodiment of this invention, with acrylate terminated polybutadienes being the more preferred. The most preferred polymer has the formula wherein 1, m and n represent the mole fraction of the respective group in the polymer and (1 + n) is from 0.4 to .95 and m is from 0.05 to 0.6, R and R' are independently in each occurrence alkyl groups of 1 to 10 carbon atoms, and preferably are methyl groups. The molecular weight (Mw) of the second component is preferably less than 150,000, more preferably less than 100,000, most preferably less than 80,000, and preferably greater than 3,000, more preferably greater than 5,000. The amount of the second component used in the composition should be such as to avoid excessive phase separation between the first and second components. When phase separation occurs significantly, it depends upon various factors, such as the molecular weights of the components, the characteristics and relative amounts of any comonomers, the solvents used, and the temperature of processing. Preferably, the amount of the second component is less than 50 parts per hundred parts of the arylcyclobutene material (phr). For the composition of the second embodiment (the preferred composition having acrylate terminal groups), the second component is preferably present in amounts of at least 20 phr to give the maximum combination of toughness, flexibility and dimensional stability. For other non-preferred embodiments, the amount of the second component is preferably less than 15 phr to avoid phase separation and solubility problems. The composition may be cured by any known method, such as, for example, by heating to temperatures from 200°C to 300°C. Frequently, the composition is coated on a substrate (for example, by spin coating, or drawing with a bar) to yield a film, and dried and cured by heating. If desired, a photosensitive compound may be added to render the composition photosensitive. A coated film of the composition can then be patterned by exposure to activating wavelengths of radiation. Photosensitizers that increase the photoactive compound's photosensitivity may also be added. Any photoactive compounds and photosensitizers that are known in the art may be used. Examples of photoactive compounds include bisazides, a combination of bismaleimides, acrylates, acetylenes, and radical initators such as 2,2-dimethoxy-2-phenylacetophenone. The amount of photoactive compound is preferably 0.1 percent to 20 percent by weight, more preferably 0.5 percent to 8 percent, based on total weight of components a and b and the photoactive compound. See U.S. Patent 6,083,661 for additional discussion regarding photocurable BCB compositions and methods of developing such compositions. See also U.S. Serial No. 09/177,819. Flame retardant compounds may be added to render the flame retardancy. Examples of flame retardant compounds include phosphate compounds, such as triphenylphosphate and trishaloethyl phosphate, halogenated compounds, such as polymerized tetrabromo-bis- phenol A and inorganic compounds such as magnesium and calcium carbonate. Multiple flame retardant compounds can be used to enhance the flame retardant effect. The amount of flame retardant compound is preferably 5 percent to 20 percent by weight, more preferably 5 percent to 10 percent, based on total weight of components a and b and the photoactive compound. Other components, such as antioxidants (for example, quinolines, hindered amines, monomethyl ether hydroquinone, and 2,6-di-tert-butyl-4-methylphenol), adhesion promoters, additional cross-linkers (for example, 2,6-bis(4-azidobenzylidene)-4- ethylcyclohexanone) (BAC-E) that are known in the art may also be included in the composition. Using additional cross-linkers that are reactive to BCB under dry, heated conditions are advantageous for the metal-coated foils because they enable one to control resin flow during the lamination process. Suitable solvents for the composition include mesitylene, xylenes, toluene, methyl ethyl ketone, cyclic ketones and mixture of these. Examples Structures and information of polystyrene-polybutadiene-polystyrene (SBS) triblock copolymer (VECTOR from Dexco), dihydroxyl terminated polybutadiene (R45HT from Elf-Atochem) and diacrylate terminated polybutadiene (BAC-45 from Osaka Organic Chemical Industry, Inc.) used in some of the examples are listed below: VECTOR 8505: styrene/diene ratio = 29/71 ; Mw is about 75,000 grams per molecule. VECTOR 6241 : styrene/diene ratio = 43/57; Mw is about 62,000 grams per molecule. (1 + n) = 95 to 50 percent m = 5 to 50 percent R45HT: Mw is about 6,200 grams per molecule; Mn is about 2,800 grams per molecule. HO- CH 2 -CH=CR-CH 22 Wj — cCH 2 -CH CH 2 -CH=CR-CH -OH m CR=CH 2 BAC-45: Mw is about 6,600 grams per molecule; Mn is about 3,000 grams per molecule. Example 1 The ethylenically unsaturated elastomers listed below were evaluated for their usefulness in modifying formulations comprising benzocyclobutene oligomers: TABLE I Liquid Polybutadiene TABLE II SBS Elastomer The compatibility of these materials in a polymer based on the DVS-bisBCB monomer is shown in the following table: TABLE III Compatibility of Elastomer to BCB The various elastomers, in combination with the BCB polymer, were further evaluated for tackiness, amount of curl experienced when coated onto a copper foil and for bend flexibility of the coated copper foil as shown below: TABLE IV B-Stage Polymer Film Evaluation The coated copper foils were then cured or C-staged and further evaluation of toughness of the cured composition occurred as shown below: TABLE V C-Stage Polymer Film Evaluation *Rating: 1 poor — 5 excellent Example 2 - Polymer Coated Cu foil with 15 Percent BAC-45 in Mw of 140.000 G ams per Molecule BCB Eighty weight parts of B-staged BCB (Mw - 140,000 grams per molecule), 15 weight parts of BAC-45, and part of bis-azide cross-linker were blended in 100 parts of mesitylene. The solution was clear. The solution was coated on the matte side of a 0.5 ounce Cu foil with a doctor blade that had a 200 μm gap between the blade and the Cu foil surface so that the thickness of the dry-up BCB film was 100 μm. After coating, the polymer coated Cu foil was placed in a 150°C oven for 15 minutes to evaporate the solvent. The B-stage polymer coated Cu foil was not coiled, and it generated no cracks in the bending test with 10 mm diameter cylindrical spacer. The B-stage polymer coated Cu foil was laid up on a 1.6 mm thick and 30 cm by 30 cm FR-4 laminate board whose Cu circuit had black oxide surface. The set was placed in a vacuum hot press machine. The hot press was programmed so that temperature was ramped at 5°C per minute to 210°C and was kept for 3 hours. The hot press pressure was maintained at 10 Kg/cm 2 until the temperature went up to 170°C and then was increased to 30 Kg/cm 2 and maintained until the press program finished. The post-press thickened polymer layer built on FR-4 core board was approximately 80 μm plus or minus 10 μm. The board was cut into 1-inch by 4-inch strips for Cu foil peel strength measurement. The Cu peel strength was approximately 1.0 Kg per cm and no BCB delamination from core board was observed. Also, the board was cut into 2-inch by 2-inch pieces and the pieces were placed under a pressure cooker test (121°C for 3 hours) and then dipped in a 260°C solder bath for 1 minute. No blister was observed. Example 3 - Polymer Coated Cu foil with 5 Percent BAC-45 and 10 Percent BCB Monomer in Mw of 140.000 Grams per Molecule BCB Ninety weight parts of B-stage BCB (Mw = 140,000 grams per molecule), 5 weight parts of BAC-45, 5 weight parts of BCB monomer and 1 part of bis-azide cross-linker were blended in 100 parts of mesitylene. The solution was clear. The polymer solution was coated on a Cu foil and thermally dried in the same manner as Example 2. Then, the polymer coated Cu foil was laminated in the same manner as Example 2. The post-press thickness polymer layer built on FR-4 core board was 80 μm plus or minus 10 μm. The board was cut into 1-inch by 4-inch strips for Cu foil peel strength measurement. The Cu peel strength was approximately 0.9 Kg/cm 2 and no BCB delamination from core board was observed. Also, the board was cut into 2-inch by 2-inch pieces and the pieces were placed in a pressure cooker test (121 °C for 3 hours) and then dipped in a 260°C solder bath for 1 minute. No blister was observed. Example 4 - Flexible Metalized Sheet with 30 Percent BAC-45 in Mw of 140.000 Grams per Molecule BCB Seventy weight parts of B-stage BCB (Mw = 140,000 grams per molecule), 30 weight parts of BAC-45 and 3 parts of bis-azide cross-linker were blended in 100 parts of mesitylene. The solution was clear. The polymer-coated solution was coated on the shiny side of a ! -ounce Cu foil and thermally dried in the same manner as Example 2. The coating thickness was 100 μm. Then, polished stainless steel plate was laid upon the polymer side of the polymer coated Cu foil, and hot-pressed in the same manner as Example 2. After the hot press process, the polymer coated Cu foil was peeled off from the stainless steel plate. The post-pressed polymer layer thickness was 100 μm. The polymer sheet was subjected to bending test with 1 mm thick spacer. No crack occurred. Example 5 - Glass Reinforced Substrate with 15 Percent BAC-45 in Mw of 140.000 Grams per Molecule BCB Eighty weight parts of B-stage BCB (Mw = 140,000 grams per molecule), 15 weight parts of BAC-45, and 1 part of bis-azide cross-linker were blended in 120 parts of mesitylene. The solution was clear. The polymer solution was coated on and impregnated into a glass mat (Ohji Paper's Glassper) GMC-50E, thickness = 380 μm), which was thermally dried at 150°C for 30 minutes to make a prepreg. The resin content of the prepreg was approximately 90 percent. Three sheets of the prepreg were laid-up and Cu foil sheets were placed on top and bottom. Then, the set of prepreg sheets and 0.5 ounce Cu foil sheets were placed in a vacuum hot press. The hot press was programmed so that the temperature was ramped at 5°C per minute to 250°C and was kept for 3 hours. The hot press pressure was maintained at 10 Kg/cm 2 until the temperature went up to 170°C and then was increased to 30 Kg/cm 2 and maintained until the press program was finished. The post-hot press thickness was 1.1 plus or minus 0.01 mm. The board was cut into 1-inch by 4-inch strips for Cu foil peel strength measurement. The Cu peel strength was approximately 0.9 Kg cm 2 and no BCB delamination from core board was observed. The board was cut into 2-inch by 2-inch pieces and the pieces were placed under a pressure cooker test (121°C for 3 hours) and then dipped in a 260°C solder bath for 1 minute. No blister was observed. Example 6 - Preparation of 10 Percent R45HT (Hydroxy Terminated Polybutadiene) in B-Staged BCB with Mw of 140,000 Grams per Molecule Five hundred grams of 51.2 percent BCB in mesitylene solution was mixed with 28.5 grams of R45HT. One hundred grams of the above solution were diluted with 11.4 grams of mesitylene to generate a solution with 43.5 percent BCB and 4.84 percent R45HT. The solution was spin-coated on a 6-inch Cu coated wafer at 3000 rpm. The cure program was from RT to 150°C in 30 minutes, at 150°C for 20 minutes, from 150 to 250°C in 40 minutes and at 250°C for 1 hour. The film surface had a "scale" pattern, which could be due to migration of R45HT to the surface during cure. The coefficient of thermal expansion (CTE) of a free-standing film was 94 ppm per °C. Example 7 - Preparation of 10 Percent BAC-45 (Acrylate Terminated Polybutadiene) in B-Staged DVS-bisBCB (BCB) with Mw of 140.000 Grams per Molecule One hundred grams of 51.2 percent BCB in mesitylene was mixed with 5.8 grams of BAC-45 and 7 grams of mesitylene. The solution contained 45.5 percent BCB and 5.14 percent BAC-45. A film was spin-coated and curved as in Example 6. The surface of the film was smooth. A portion of the film was freed from the wafer by etching off the copper with a 10 percent ammonium persulfate solution. Examination of the free-standing film by transmission electron microscopy (TEM) did not show any discrete domains. CTE of a free-standing film was 80 ppm per μC. Example 8 - Preparation of 20 Percent BAC-45 in B-Staged DVS-bisBCB (BCB) with Mw of 140.000 Grams per Molecule One hundred and thirty-three grams of 51.2 percent BCB in mesitylene was mixed with 17.1 grams of BAC-45 and 15 grams of mesitylene. The solution contained 41.3 percent BCB and 10.4 percent BAC-45. A film was spin-coated and cured as in Example 6. The surface of the film was smooth. Example 9 - Thin Film from 10 Percent VECTOR 6241 in B-Staged DVS-bisBCB (BCB) with Mw of 140.000 Grams per Molecule Fifty grams of 51.2 percent BCB in mesitylene was mixed with 2.85 grams of VECTOR 8508 and 3 grams of mesitylene. The solution contained 46.0 percent BCB and 5.1 percent VECTOR 6241. A film was spin-coated on a 6-inch copper coated wafer at 4000 rpm and cured. The surface of the film was smooth. A free-standing film was generated as in Example 7. Examination of the free-standing film by transmission electron microphotography (TEM) showed domains of 0.2 μm diameter. Example 10 - Thin Film from 3.9 Percent VECTOR 8508 in B-Staged DVS-bisBCB (BCB) with Mw of 140.000 Grams per Molecule Seven hundred and fifty grams of 50.9 percent BCB in mesitylene was mixed with 15.3 grams of VECTOR 8508 and 60 grams of toluene. The solution was spin-coated on a 4-inch copper coated wafer at 2500 rpm. A free-standing film was examined by TEM and the domains of 0.2 μm diameter were observed. Example 11 - Patterning Thin Film of BCB with 10 Percent BAC-45 To 15 grams of CYCLOTENE (trademark of The Dow Chemical Co.), 4026-46 dielectric was added 0.77 gram of BAC-45. A 0.3 weight percent partially hydrolyzed vinyl triacetate silane solution was applied to a 4-inch silicone wafer as adhesion promoter. The CYCOTENE 4026 solution with BAC-45 was spread at 500 rpm followed by spin-coating at 2700 rpm for 30 seconds. The wafer was prebaked at 85°C for 90 seconds on a hot plate. A Karl Suss photo exposure tool was used with the gap between the wafer and the mask to be 10 μm. The exposure dose was 600 mJ/cm 2 . Predevelopment bake was 50°C for 30 seconds. The wafer was puddle developed with DS-2100, which was a mixture of PROGLYDE DMM (dipropylene glycol dimethyl ether from The Dow Chemical Co.) and Isopar L (from Exxon). The development time was 22 seconds. The wafer was cured and then treated with plasma. Final film thickness was 10.9 μm. All 75 μm vias were open. Example 12 - Patterning Thin Film of BCB with 10 Percent R45HT To 15 grams CYCLOTENE 4026-46 was added 0.77 gram of R45HT. A 0.3 weight percent partially hydrolyzed vinyl triacetate silane solution was applied to a 4-inch silicone wafer as adhesion promoter. The CYCLOTENE 4026 solution with R45HT was spread at 500 rpm followed by spin-coating at 2700 rpm for 30 seconds. The wafer was prebaked at 85°C for 90 seconds on a hot plate. A Karl Suss photo exposure tool was used with the gap between the wafer and the mask to be 10 μm. The exposure dose was 600 mJ/cm . The predevelopment bake was 50°C for 30 seconds. The wafer was puddle developed with DS- 2100. The development time was 22 seconds. The wafer was cured and then treated with plasma. Final film thickness w is 10.3 μm. The shape of the vias was distorted. Cracks were observed around the vias. Example 13 - Patterning Thin Film of BCB with 10 Percent VECTOR 6241 To 100 grams CYCLOTENE 4026-46 was added 5.13 grams of VECTOR 6241 dissolved in 9.2 grams of mesitylene. A 0.3 weight percent partially hydrolyzed vinyl triacetate silane solution was applied to a 4-inch silicone wafer as adhesion promoter. The CYCLOTENE 4026 solution with VECTOR 6241 was spread at 500 rpm followed by spin- coating at 2500 rpm for 30 seconds. The wafer was prebaked at 85°C for 90 seconds on a hot plate. A Karl Suss photo exposure tool was used with the gap between the wafer and the mask to be 10 μm. Exposure dose was 600 mJ/cm 2 . Predevelopment bake was 50°C for 30 seconds. The wafer was puddle developed with DS-2100. The development time was 34 seconds. The film became hazy after development. The wafer was cured and then treated with plasma. The final thickness of the hazy film was 7.6 μm. Example 14 - Tensile Properties of BCB with VECTOR 8508. R45HT and BAC-45 Strips of BCB with 5 percent and 10 percent VECTOR 8508, R45HT, and BAC-45 were generated and tested according to the procedure described by J. Im, et al. at 2 nd International Symposium of Advanced Packaging Materials in Atlanta, GA, March 1996. The results are shown in the table below. TABLE VI Tensile Properties of BCB with VECTOR 8508, R45HT and BAC-45 Example 15 A solution from 2.08 grams VECTOR 8508 SBS triblock copolymer was dissolved in 4 grams of mesitylene and 100 grams of B-staged BCB with Mw of 140,000 grams per molecule and consisted of 50.9 weight percent BCB in mesitylene and was made photosensitive by using BAC-E (2,6-bis(4-azidobenzylidene)-4-ethylcyclohexanone) (1.85 grams, 3.5 weight percent) as photo cross-linker. To a 4-inch diameter wafer was applied a 0.3 weight percent partially hydrolyzed vinyl triacetate silane as adhesion promoter. BCB photo formulation was spread at 500 rpm for 10 seconds followed by spin-coating at 5000 rpm for 30 seconds. The wafer was prebaked on a hot plate at 90°C for 90 seconds. A Karl Suss photo exposure tool was used and the gap between the wafer and the mask was 10 μm. The exposure dose was 413 mJ/cm 2 . The wafer was puddle developed with DS 2100. Development time was 156 seconds. The developed wafer was baked on a hot plate at 90°C for 90 seconds before it was cured at 250°C under nitrogen. The cured wafer was treated with plasma for 45 seconds. The final film thickness was 10.5 μm. The thickness after bake was 12.7 μm. The film retention was 83 percent. All 50 μm vias were open with the bottom of via at 38 to 41 μm. Example 16 VECTOR 8508 SBS (2.1 grams), DVS-bisBCB monomer (52.9 grams) and mesitylene (145 grams) were heated at 165°C under nitrogen until Mw of BCB reached 83,000 grams per molecule. Mw was measured by GPC. Measurement included BCB and SBS. The solution was filtered with 1 μm filter and concentrated to 39 percent by weight of BCB. BAC-E (283 mg, 3.5 weight percent) was added to 20 grams of the BCB/SBS rubber solution. A 0.3 weight percent partially hydrolyzed vinyl triacetate silane was applied to a 4-inch wafer as adhesion promoter. BCB/SBS rubber/BAC-E solution was spread at 500 rpm followed by spin-coating at 2000 rpm for 30 seconds. The wafer was prebaked at 90°C for 90 seconds on a hot plate. A Karl Suss photo exposure tool was used with the gap between the wafer and the mask to be 10 μm. The exposure dose was 1000 mJ/cm . The wafer was puddle developed with DS-2100. Development time was 73 seconds. The developed wafer was baked on a hot plate at 90°C for 90 seconds before it was cured at 250°C under nitrogen. The cured wafer was treated with plasma for 30 seconds. The final film thickness was 9 μm. Film thickness after bake was 11 μm. Film retention was 82 percent. All 75 μm vias were open.

Claims: WHAT IS CLAIMED IS: 1. A process comprising providing a printed wiring core board, laminating to the printed wiring core board a sheet comprising a foil of a conductive metal and, on the foil, a dielectric layer comprising a curable composition (a) at least one precursor compound selected from arylcylobutene monomers, arylcyclobutene oligomers, and combinations thereof; and (b) a polymer or oligomer having a backbone comprising ethylenic unsaturation, wherein during the lamination step the dielectric layer is in contact with the printed wiring board, and processing the laminated article to form additional electrical connections. 2. The process of Claim 1 wherein the ethylenically unsaturated polymer is a polybutadiene. 3. The process of Claim 1 wherein the ethyl enicaly unsaturated polymer is terminated with groups selected from acrylate and methacrylate. 4. The process of Claim 1 wherein the step of processing to form additional electrical connections includes one or more of the following steps: stripping the metal foil, etching the metal foil, drilling through the laminate, opening a via with a CO 2 laser, copper electroless plating, and copper electroplating. 5. The process of Claim 1 wherein the metal foil is copper. 6. A curable composition comprising a) at least one precursor compound selected from arylcylobutene monomers, arylcyclobutene oligomers, and combinations thereof; and b) a polymer or oligomer having a backbone comprising ethylenic unsaturation and terminal acrylate or methacrylate groups. 7. The composition of Claim 5 wherein the ethylenically unsaturated polymer or oligomer is a polybutadiene. 8. The composition of Claim 5 further comprising a cross-linking aid and an antioxidant. 9. An article comprising a metal foil and on that metal foil a layer of the composition of Claim 5. 10. The article of Claim 8 wherein the metal foil is copper. 11. The cured reaction product of the composition of Claim 5. 12. A photoimageable composition comprising (a) at least one precursor compound selected from arylcylobutene monomers, arylcyclobutene oligomers, and combinations thereof; (b) a polymer or oligomer having a backbone comprising ethylenic unsaturation; and (c) a photoactive compound selected from the group consisting of azides, bismaleimides, acrylates, acetylenes, isocyanates, aromatic ketones such as 2,2-dimethoxy- 2-phenyl acetophenone, conjugated aromatic ketones, and benzophenone-containing polymers.

Inventors: ACHEN ALBERT CHARLES MARIE, AKIMOTO HIDEKI, GARROU PHILIP E, KALISZEWSKI BRITTON LEE, MARTIN BRIAN, OHBA KAORU, SO YING HUNG, ACHEN, ALBERT, CHARLES, MARIE, AKIMOTO, HIDEKI, GARROU, PHILIP, E., KALISZEWSKI, BRITTON, LEE, MARTIN, BRIAN, OHBA, KAORU, SO, YING, HUNG
Applicants: DOW CHEMICAL CO, THE DOW CHEMICAL COMPANY
Application year: 2000
Main classification: H05K3
IPC codes: B32B15, C08F2, C08F290, C08G61, H05K1, H05K3