RARE EARTH POLYMER OPTICAL AMPLIFIER OR FIBER

Abstract: Disclosed are cost-effective, compact, optically pumped, high gain, rare earth polymer materials such as, erbium (Er<3+>) perfluoro polymers, optical fibers made from the materials and waveguide amplifiers made from the materials having low-loss at telecommunications wavelengths for operation in communications network systems. The polymer amplifier is based on the use of novel high performance rare earth (RE) polymer materials. The new discovered highly transparent RE polymer materials are directly synthesized at high RE ion concentrations ( SIMILAR 10<20->10<21> rare earth ion/cm<3> SIMILAR 10 wt.%) with each metal ion encapsulated and physically buffered by insulating, covalently bonded, perfluorinated phosphate ligands that then form the high temperature stable, polymer backbone matrix. This is distinctly different from widely studied inorganic glasses and single crystals where RE ion salts are doped directly into the host but only to relatively low levels (< 0.1 wt.%).

Description: RARE EARTH POLYMER OPTICAL AMPLIFIER OR FIBER BACKGROUND OF THE INVENTION Field of the Invention: The invention relates to rare earth polymer compositions, optical fibers, optical waveguides, and particularly to optical amplifier waveguides and splitters Description of the Related Art Optical communication systems based on glass optical fibers (GOFs) allow communication signals to be transmitted not only over long distances with low attenuation but also at extremely high data rates, or bandwidth capacity This capability arises from the propagation of a single optical signal mode in the low-loss windows of glass located at the near-infrared wavelengths of 0 85, 1 3, and 1 55 μm Since the introduction of erbium-doped fiber amplifier (EDFA), the last decade has witnessed the emergence of single-mode GOF as the standard data transmission medium for wide area networks (WANs), especially in terrestrial and transoceanic communication backbones In addition, the bandwidth performance of single-mode GOF has been vastly enhanced by the development of dense wavelength division multiplexing (DWDM), which can couple up to 160 channels of different wavelengths of light into a single fiber, with each channel carrying gigabits of data per second Moreover, in a recent demonstration, a signal transmission of 1 terabit (10 12 bits) per second was achieved over a single fiber on a 100- channel DWDM system Enabled by these and other technologies, the bandwidth capacities of the communication networks are increasing at rates of as much as an order of magnitude per year The success of single-mode GOF in long-haul communication backbones has given rise to the new technology of optical networking The universal objective is to integrate voice video, and data streams over all-optical systems as communication signals make their way from WANs down to smaller local area networks (LANs), down to the curb (FTTC), home (FTTH), and finally to the end user by fiber to the desktop (FTTD). Examples are the recent explosion of the Internet and use of the World Wide Web, which are demanding vastly higher bandwidth performance in short- and medium-distance applications. Yet as the optical network nears the end user starting at the LAN stage, the system is characterized by numerous fiber connections, splices, and couplings, especially those associated with splitting of the input signal into numerous channels. All of these introduce enormous optical loss. To compensate for the unacceptably high loss penalty, current solutions rely on expensive EDF As that are bulky at fiber lengths of about 40 m. The cost of a typical commercial EDFA can reach many tens of thousands of dollars. Thus, to complete the planned build-out for FTTC, FTTH, and FTTD in the US would require millions of amplifiers and hundreds of billions of dollars An EDFA module is made up of a number of key components One of the most critical components in the module is the erbium doped silica fiber (EDF). Present EDF is limited by low concentrations of erbium atoms, clustering that leads to quenching of photoluminescence, a relatively narrow emission band, a highly wavelength dependent gain spectrum, and an inability to be fabricated in a compact, planar geometry. Efforts have been directed toward the use of other rare earth ions in both fused silica glass hosts and other glasses including fluoride, tellurite and phosphate glasses To this point, these efforts have been limited by the fundamental materials properties of these glass media with regard to their ability to dissolve rare earth atoms, mechanical properties, thermal stability, and other key properties. The benefits of the present invention are based on the development of rare earth fluorphosphinate polymer material that have the following preferred properties • compatibility with a broad range of rare earths that enable coverage of the full 1500 to 1600 nm window (and beyond) using a common host platform; • very high concentrations of rare earth elements without associated quenching and upconversion penalties, allowing for very short lengths of fiber to be used as small as centimeters and less, • very low intrinsic optical loss, • capable of being drawn into single mode optical fiber, and • capable of being cast into films for planar waveguide applications Cost effective, compact integrated optics is a preferred solution to this problem, but currently none exists. It is an object of the present invention to provide novel optical waveguide materials that are easy to process using standard silicon VLSI (very large scale integration) fabrication methods and optical fiber drawing processes. It is a further objective of the present invention to produce a fiber amplifier and material therefor having low-loss in short and medium distance communications network systems. It is an object of the present invention to produce an integrated optical component that is a low-loss splitter that combines amplification and splitting of the input light signal while maintaining a high signal-to-noise ratio. SUMMARY QF THE INVENTION Disclosed are cost-effective, compact, optically pumped, high gain, rare earth polymer materials such as, erbium (Er 3* ) fluorophosphinate polymers, optical fibers made from the materials and optical amplifiers made from the materials having low-loss at telecommunications wavelengths for operation in data communications network systems. The polymer amplifier is based on the use of novel high performance rare earth (RE) polymer materials The highly transparent RE polymer materials are directly synthesized at high RE ion concentrations (~10 2u" 10 21 rare earth ion/cm 3 ~ 10% wt) with each metal ion encapsulated and physically buffered by insulating, covalently bonded, perfluorinated phosphate ligands that then form the high temperature stable, polymer backbone matrix. This is distinctly different from widely studied inorganic glasses and single crystals where RE ion salts are doped directly into the host but only to relatively low levels (< 0.1% wt). The RE polymer material as depicted in Figure 1 is designed for use in an integrated optical circuit element utilizing numerical modeling and computer simulations. Utilizing this RE polymer material, the polymer amplifier length can be as short as several cm because of the ultra high gain coefficient of >5 dB/cm As a complement to the cost effective VLSI methods utilized for the planar waveguide architecture, standard low-cost fiber drawing methods are used to fabricate the fiber amplifier element to further realize significant cost reduction of the final integrated optical device The use of RE polymer materials affords the devices several unique properties and advantages These include high RE ion concentrations with homogeneous distribution, enhanced optical transition moments, controllable decay rates and branching ratios, novel energy transfer effects, and relatively low optical loss across the near infrared region. The combination of these critical features is not available in standard RE-doped silica glasses and inorganic crystals RE polymer systems have many outstanding materials properties. These include simple two-step synthesis by standard organic methods; ease of synthesis modification; ease in fiber and planar waveguide fabrication by standard methods; compatibility with various cladding materials, high thermal, mechanical, and photostabilities; and room temperature operation Further, the new RE polymers easily form highly transparent thin films both by simple casting and standard spin coating methods. For compact optical amplification devices, the processing properties of silica glass and inorganic crystal systems are inferior to the RE polymer materials The successful realization of RE-containing polymers is not straightforward, and the reasons for this are fundamental and intrinsic Common organic polymers contain high-frequency optical phonons, such as O-H stretch (-3600 cm"') and C-H stretch (-3200 cm" 1) vibrations These vibrations play the dominant role in phonon- assisted, nonradiative removal of electronic excitation energy from optically excited RE ions Such nonradiative decay of RE metastable states markedly reduces the radiative efficiency of the RE containing material and, consequently, severely degrades amplifier device performance This is especially strong in the case of Er 1 ' because of the relatively small energy gap between the ground and metastable electronic states Moreover, high order overtones of the same O-H and C-H vibrations are also the origin of unacceptably high optical absorption loss across the entire near infrared region observed in standard polymer optical fibers and waveguides Thus, the same solution of the phonon-assisted, nonradiative decay problem naturally holds for the unwanted absorption loss in optical polymers To achieve the ultra high gain polymer optical fiber amplifiers and provide solutions to these basic problems, we employ the novel RE fluorophosphinate polymers as the active waveguide core material In these materials, all of the usual high frequency O-H and C-H bonds are replaced by C-F bonds having considerably reduced frequency vibrations (-1000-1200 cm"' ) Disclosed are several general classes of high optical transparency RE perfluoro polymers for optical amplification applications The RE ion concentration in these polymers is relatively high on the order of 10 2o - 10 21 RE ions/cm 1 At the same time, we have identified a variety of other fiuoropolymers for use as cladding materials with our new RE perfluoro polymers In addition to Er , all of the RE metal ions can be encapsulated in this manner at high concentrations BRIEF DESCRIPTION OF THE DRAWINGS FIGURE 1 is a schematic polymer chain structure of erbium fluorophosphinate polymers: FIGURE 2 is an energy level diagram of erbium chromophore 3 -level model, FIGURE 3 is a depiction of the optical energy transfer mechanism in RE perfluoro polymers, FIGURE 4 is a setup for picosecond fluorescence and radiative lifetime measurements, and FIGURE 5 is a depiction of the fabrication of polymer channel waveguides utilizing standard silicon VLSI processing steps DESCRIPTION OF THE PREFERRED EMBODIMENTS The preferred material for the rare earth polymer composition is one of the general formula {X(OOPRR') 3 } n where X is a rare earth element Suitable rare earth elements include erbium, europium, samarium, dysprosium, neodymium, praseodymium, thulium and ytterbium Mixtures of these materials are also contemplated All other rare earth ions are also within the contemplation of the invention R is preferably a fully halogenated organic group, and R' is another fully halogenated organic group, the same or different from R R and R' can be fluoroalkyl chains of the general composition C m F 2m+1 , where m> 1, and R=R' or R≠R' Another particular group is a hexafluorophenoxy group of the composition C 6 F 5 O The composition of the polymer can also include commercially available fiuoropolymers, including fluorinated polyimides, polytetrafluoroethylene, fluoroacrylates, fluorosilicones and branded fiuoropolymers such as CYTOP® (Asashi Glass) and THV® (3M) The compositions identified above are used to produce cores for optical fibers The cores can be cladded with suitable materials having a lower refractive index than the core The core/cladding refractive index difference is small enough to result in single optical mode preparation for optical wavelengths from 1200-1700 nm Further, the compositions identified can be used to produce an optical amplifying film, containing a substrate, a buffer film, a guiding layer, and an upper cladding film, such that the refractive indices of the buffer film and the upper cladding film, are less than that of the guiding layer film, with the resulting waveguide guiding a single optical mode for optical wavelengths from 1200- 1700 nm RE waveguide amplifiers operate on the basic 3 -level and 4-level laser transition principles The single pass gain of the waveguide amplifier is the fundamental parameter to be calculated Amplification in a RE polymer waveguide, as with most types of laser systems, can be described with a 3-level model Figure 2 displays the energy level diagram of such a model for Er 1+ ion In an amplif er, the RE ions start out in their ground state, level 1. The electrons are then excited to leve' 2 by a pump beam of photons with energy hcv, equal to the transition energy from 1 ->2. The ions subsequently undergo fast nonradiative decay to level 3, which is the metastable state of the system. The lifetime of this state is very long in comparison to the nonradiative decay. As a consequence, a population inversion is created in level 3 Then, as a signal beam passes by the ions, it stimulates emission of photons with the same signal energy, hω Λ - This stimulated decay is from level 3 to level 1, the ground state. One of the most pronounced advantages of encapsulating the RE ion as a chromophore is the ability to control the manifold of electronic excited states. Provided is an optical energy transfer mechanism between the surrounding organic ligands of the chromophore unit and the central RE ion in which the RE excited state can be populated through selective absorption ("light harvesting") by the chromophore ligand and subsequent energy transfer to the RE site This transfer can approach unit efficiency, and, as a result, can increase the absorption cross-section by a remarkable 10^- 10$ times that of bare RE ions. The process is diagramed in Figure 3, showing how the chromophore ligand singlet band is first excited by pump light and then decays nonradiatively through inter-system crossing (IC) to its bottleneck triplet state. Radiative transitions back to the ground state are spin forbidden and, hence, the chromophore ligand can relax through energy transfer to the encapsulated RE ion This energy transfer is maximized by tuning the energy gap, again through chromophore design, between the ligand triplet state and the upper level of RE fluorescing transition The optical attenuation coefficient of an optical waveguide determines the output intensity of the transmitted signal The various factors contributing to optical loss in optical polymers can be divided into intrinsic and extrinsic loss Intrinsic loss includes vibrational absorption of the polymer materials, electronic transition absorption, and Rayleigh scattering. Extrinsic loss includes absorption due to impurities, scattering from dust and microvoids, and imperfections in fiber parameters Extrinsic loss is related to materials processing and fiber fabrication, and thus can be reduced by perfecting each procedure Intrinsic loss is material related and cannot be reduced without drastic changes in material composition Standard optical polymer materials are based on hydrocarbon (C-H) structures A prototypical example is polymethylmethacrylate (PMMA) which has three principal loss windows located at 570, 650, and 780 nm between absorption maxima arising from C-H vibrational overtone modes In high optical quality samples, the principal window at 650 nm exhibits a measured minimum loss of 1 10 dB/km, very close to the theoretical limit of 106 dB/km Molecular vibrations of aliphatic hydrocarbons in PMMA are the dominant intrinsic loss factor in optical polymer waveguides The fundamental CH vibration occurs at 3 2 μm The attenuation loss in the visible wavelength region is affected mainly by the 5th to 7th high harmonics of CH absorption At the 650 nm window, CH absorption contributes about 90 dB/km to the total loss In the near-infrared region, the minimum loss exceeds 10 4 - 10 5 dB/km, thereby excluding standard optical polymers and RE chromophore structures based on them for use at the three telecommunications wavelengths of 850, 1300, and 1550 nm The intensities of the harmonic absorption bands decrease by one order of magnitude with each successive harmonic If hydrogen is replaced with a more massive atom, the wavelengths of the fundamental vibration and subsequent harmonics would be shifted to longer wavelength regions The order of higher harmonics which affects the near-infrared region would be higher, resulting in significant decreases in vibrational absorption Indeed, when the short wavelength O-H and C-H bonds are replaced by C-F bonds having a markedly longer fundamental stretch vibration at 10 μm, the resulting fluoropolymer waveguide exhibits a reduced loss of 10 dB/km with a practically flat dispersion over the near-infrared range The primary contributing factors to the fluoropolymer loss are wavelength-independent structural waveguide imperfections and Rayleigh scattering, a R = 9.5( ) dB/km, as based on measurements of fluorinated polymer waveguides Losses attributed to electronic absorption are negligible as are absorptions from molecular vibrations The C-F vibrational overtones are basically nonexistent in the visible region and have strengths in the near infrared range of much less than 1 dB/km even up to near 1500 nm Consequently, the total theoretical loss of a perfluorinated polymer waveguide approaches 10 dB/km well into the near-infrared and is less than 25 dB/km over most of the visible spectrum Varieties of fiuoropolymers for passive optical waveguides have been developed for direct use, including, for example, ether-, perfluoromethyl-, and chloro- substituted (polytetrafluoroethylenes), acrylates, silicones, polyimides, and co-and ter- polymers of (polytetrafluoroethylene) PTFE and polyvinylidene fluoride (PVDF) The replacement of O-H and C-H bonds with C-F bonds in the polymer fiber waveguide core materials is critically important to over all radiative efficiency of the RE systems The O-H stretch (-3600 cm" 1 ) and C-H stretch (-3200 cm" 1 ) vibrations play a dominant role in phonon-assisted, nonradiative removal of electronic excitation energy from excited RE ions Such nonradiative decay of RE metastable states markedly reduces radiative efficiency and, consequently, severely degrades amplifier device performance Phonon-assisted decay decreases exponentially with increased number of phonons required to span the energy gap between the metastable state and the ground state In the new RE perfluoro polymers, the high frequency O-H and C-H bonds are replaced by C-F bonds that possess considerably reduced frequency vibrations (-1000- 1200 cm" 1 ), and as a consequence, long metastable (-1-10 ms) lifetimes for the RE sites Disclosed is the design and synthesis of two general classes of high optical transparency RE perfluoro polymers for optical amplification applications (Figure 1 ) The basic perfluoro phosphate structure avoids the introduction of O-H and C-H bonds and utilizes C-F bonds The Er 3+ ion concentration in these novel polymers is relatively high on the order of 10 21 ions/cm 3 Also disclosed is the use of commercially available fiuoropolymers for cladding materials with the new RE perfluoro polymers In addition to Er + , both single as well as combinations of RE metal ions can be encapsulated at high concentrations in the basic polymer structure The radiative properties of the new materials ate measured and characterized The basic structure of these RE chromophores is composed of an isolated single RE ion encapsulated by a molecular "coordination shell " To create such a shell, perfluorinated organic phosphinate ligands are used with coordinating donor atoms, such as oxygen, to chemically bond to the RE ions which not only isolates the RE ion but also forms a physico-chemical barrier for the RE ion These RE polymers are highly compatible with high-temperature perfluorinated polymers suitable as passive cladding materials RE concentrations of ~ 10 20 -10 2! ιons/cm ~ 10% wt RE ion have been achieved with no undesirable effects such as clustering and lifetime quenching These relatively high concentration figures are to be compared to the 0.1% limit common to silica glasses and inorganic crystals. Importantly, the optical properties of the Er 3+ perfluoro polymers have been evaluated using Judd-Ofelt analyses in order to obtain important radiative lifetimes and emission cross-sections for transitions to the metastable state In brief, the results for several cm length polymer waveguides are comparable in performance to that of Er 3* - doped silica glasses commonly used in 40 m length commercial EDF As The results provide further basis for the selected approach of RE perfluoro polymer materials Attached are examples based on erbium The methods described are the same methods used for all the other rare earth ions such as europium, samarium, neodymium, dysprosium, praseodymium, ytterbium, etc Example 1. Erbium tV.v-fiυoropliosphinate polymer To a solution of erbium chloride (ErCl 3 6H 2 O) (0 8736 gm, 0 00229 mol) in 1 1 ml of tetrahydrofuran was added />/.s-(hexafluorophenoxy) phosphinic acid [(C 6 F 5 O) 2 POOH] (l 97 gm, 0 00458 mol) The erbium solution appeared turbid and was heated at reflux for 30 minutes Potassium carbonate (K 2 CO 3 ) (0 475 gm, 0 0034 mol) dissolved in 2 74 ml of water was added dropwise with stirring The solution was then heated to boiling, and the tetrahydrofuran allowed to evaporate Additional water was added to maintain the over all volume of the solution As evaporation neared completion, the solid erbium A/s-fluorophophinate polymer (Er[0 2 P(O C 6 F 5 ) 2 ] 2 (OH)(H 2 O) appeared voluminous The solid residue was filtered and washed several times with water After air drying at room temperature, the slightly pink white powder was dried in a vacuum oven at 1 10°C for 24 hrs The yield after drying was 1 84 gm Analysis Calculated for ErC 24 F 20 H 30 O 10 P 2 , C 27 16, F 35 84, P 5 85, H 0 28, and Er 15 78, Found C 26 90, F 35 39, P 5 63, H O 20, and Er 15 85 Example 2. Erbium t -Fh oropphosphinate polymer To erbium Z>/_>-fluorophosphinate polymer (Er[0 2 P(O C 6 F 5 ) 2 ] 2 (OH)H 2 O) (0 140 gm, 0 13mmol) dissolved in 3 ml of ø-dichlorobenzene was added bis- (hexaflluoro-phenoxy) phosphinic acid [(C 6 F 5 O) 2 POOH] (0 057gm, 0 13 mmol) The solution was heated in an oil bath under nitrogen to 100°C for approximately 10 minutes The resulting solution was clear and light pink in color As soon as the heat was removed, the solution turned viscous The viscous mixture was placed under nitrogen, and the solvent slowly removed The resulting slightly pink white solid was collected and placed in a vacuum oven at 40°C overnight The yield after drying was 130 mg Analysis: Calculated for ErC 36 F 30 O 12 P 3 C 29 73, F 39 18, P 6 39, H 0 0, and Er 1 1 5, Found C 28.52, F 38 94, P 6 61 , H 0 16, and Er 1 1 4 Example 3. Erbium fluoroalkyl phosphinate polymer To a solution of anhydrous erbium chloride (ErCl 3 ) (0 070 gm, 0 257 mmol) in 0 5 ml of dry acetone was added (C 7 F 15 ) 2 POONa (0 618 gm, 0 77 mmol) in 6 ml of dry acetone The resulting solution was stirred at room temperature for approximately 72 hours, after which a light pink solid fell out of solution and was filtered by transferring using acetone The total yield prior to drying was 0 581 gm 21 1 mg of the product was stirred with water, filtered, and dried in a vacuum oven at 65 °C with a yield of l90 mg Analysis Calculated for Er[OOP(C 7 F 15 ) 2 ] 3 C 18 91 , F 63 63, Er 5 49, Found C 17 26, F 60 26, Er 5 69 Example 4. Erbium fluoroalkyl phosphinate polymer To a solution of anhydrous erbium chloride (ErCl 3 ) (0 124 gm, 0 45 mmol) in 0 82 ml of dry acetone was added (C 8 F 17 ) 2 POONa (1 256 gm, 1 36 mmol) in 1 1 ml of dry acetone The solid formed was stirred for approximately 72 hours, after which the light pink solid was filtered and washed with acetone The filtered solid was dried in a vacuum oven at 70 °C for two days with a yield of 1 15 gm of dried solid Calculated for Er[OOP(C 8 F π ) 2 ] 3 C 18 91, F 63 63, Er 5 49, Found C 17 49, F 62 94, Er 6 51 Example 5. Erbium fluoroalkyl phosphinate polymer To a solution of anhydrous erbium chloride (ErCl 3 ) (0 060 gm, 0 222 mmol) in 0 4 ml of dry acetone was added (C 8 F 17 ) 2 POONa (0 615 gm, 0.665 mmol) in 5 ml of dry acetone The reaction mixture was stirred for approximately 72 hours The filtered light pink solid that resulted was washed with acetone and dried in a vacuum oven at 65 °C overnight, yielding 520 mg of dried solid Example 6. Fluorescence lifetime The dried powder of Example 5 was further dried in a vacuum oven at 100°C and the resulting powder was placed between two glass microscope slides This sample was then placed in the apparatus shown in Figure 4, but with the Nd YAG laser replaced by a 980 nm laser, the monochromator replaced by a long pass filter, and the photomultiplier tube (PMT) replaced by a photodiode The long pass filter is designed to block the scattered light at 980 nm but to allow the fluorescing light at 1 500- 1600 nm to be captured by the photodiode The filter was established to be operating properly so that no 980 nm light contributed to the signal The 980 nm laser was modulated at a 50 Hz repetition rate with a square wave modulation profile This 980 light stimulated fluorescence of the Er' 4 fluorophosphinate polymer, and the lifetime of the fluorescence was observed with the oscilloscope The resulting data was fit to a single exponential decay and the lifetime was determined to be 2 57 msec Example 7. Thin film preparation The dried powder of Example 5 was dissolved at 10 wt% in N,N- dimethylacetamide at room temperature The resulting solution was then cast onto microscope slides and dried in an oven at 1 1 5 °C to result in a thin film of the Er 3 ' fluorophosphinate polymer This film was inspected using light and dark field microscopy and was confirmed to consist of an amorphous thin film material, suitable for optical waveguiding Example 8. Disclosed is an amplifier system using RE polymer materials. The principal wavelength of interest in communications systems is 1550 nm. Here, an Er 3" " perfluoro polymer waveguide pumped by 980 nm light and operating at 1550 nm is disclosed and analyzed. The important quantity characterizing an amplifier is its single pass gain. The 1550 nm Er transition operates as a three-level laser transition (Figure 2). Level 2 is an absorption band of the chromophore ligand as discussed above and, therefore, allows for enhanced absorption. Experimentally it is often found that the lifetime of level 2 is much shorter than the metastable state (level 3), and, hence, the steady state population of level 2 is negligible. Therefore, the total number density of ions is given by N = Ny + Nj, where N/ denotes the population of state / ' . The steady state rate equations can then be solved to yield W + (1) N_ N, W 1_2 N w 3l + - + w l2 f N w 3l + - + w l2 T i T 3 where W]2 and W^j are the stimulated absorption and stimulated emission rates, respectively, and 13 is the metastable state lifetime. The stimulated transition rates are given by where σ« is the absorption cross-section at the pump wavelength, hv>p is the pump photon energy, and E, is the pump photon intensity Similarly, σ e is the emission cross- section, IIΌ S is the signal photon energy, and I s is the signal photon intensity Given the steady state populations, (Eq 1), the evolution of the pump and signal beam intensities along the length of the waveguide (z-direction) can be derived Neglecting excited state absorption, the intensity equations are given by {n{r, φ, z)σ c N - a. )I rdrdφ where n(r,§,z) is the RE ion distribution and otp and α s are the absorption coefficients of the undoped polymer waveguide at the pump and signal wavelengths, respectively These first order differential equations are coupled through the steady state population densities and can be solved by integrating the signal and pump wavefunctions over the waveguide cross-section and implementing a fourth order Runge Kutta technique Results for a Er 3* perfluoro polymer waveguide amplifier 6 μm in diameter show that the amplifier gain versus waveguide width for a waveguide of length 3 cm has a maximum gain of approximately 30 dB The dependence of single pass gain on length for a 4 μm wide waveguide suggest the optimal length for a maximum gain of 34 dB is about 5 cm, three orders of magnitude shorter than typical silica glass EDFA This characteristic feature is a direct consequence of the high RE concentrations (~ 10 0 -10 21 ions/cm 3 - 10% wt) compared with silica glass EDF As (<0 1 % wt) Thus, one outstanding advantage of our RE perfluoro polymer systems is that they are conducive to very short length optical waveguide devices on the order of only a few cm and less As described above, a variety of commercially available fiuoropolymers can be used as cladding material ; with our new RE perfluoro phosphate polymers Recently, there has been developed new low melting temperature fluoro phosphate glasses and their fabrication process These glasses are transparent from the near ultraviolet to the near infrared They are dense, chemically durable, relatively hard, and can be readily fabricated into various shapes and sizes Organic chromophores and polymer powders are readily incorporated into these glasses at 280 ° C, making them suitable hosts for many fluorescent organic materials High optical quality organic chromophore doped fluoro phosphate glass hybrid materials have been obtained Er 31 fluorophosphinate polymers at high concentrations can be doped into this low melting temperature fluoro phosphinate glass to form the fiber waveguide core material The lower refractive index undoped fluoro phosphinate glass can serve as the fiber cladding material It is indicated that this material can be pulled into a fiber without dentrifying The optical properties of the RE polymers are measured using the setup of Figure 4 The setup can be used to measure both the metastable state lifetime of the lasing transition and the emission spectrum This experiment uses a laser pump source together with a computer-assisted detection system that includes a PMT, digital oscilloscope, and a monochromator The RE polymer sample is pumped by a picosecond Nd YAG laser using the energy transfer antenna effect Since the pump pulse is much shorter than the lifetimes of the excited metastable states, these lifetimes can be simply measured by monitoring the dynamic decay of the fluorescence signal The fluorescence signal is detected perpendicular to the incident pump beam direction in order to minimize pump scattering The light is focused onto a monochromator, which selects the wavelength, and is detected by a PMT The signal is recorded by a digital oscilloscope and the data is transferred to a computer for analysis A complete fluorescence spectrum is obtained by sweeping the monochromator through a wavelength range and recording the corresponding intensities The Er" perfluoro polymer optical fiber amplifier/splitter can be fabricated using standard melt fiber draw methods together with silicon VLSI techniques well established for integrated passive polymer optical waveguide devices (Figure 5) The RE polymer optical fiber amplifier can be aligned in a V-groove and connected by fiber pig tails to a polymer optical circuit consisting of a 2-channel waveguide fiber coupler for the 1550 nm signal and 980 nm pump and an N-channel splitter formed by standard optical lithography. Each polymer waveguide to be coupled to the fiber amplifier is formed by reactive ion etching and then over coated with suitable polymer over cladding Filtering ofthe optical pump light is accomplished by introducing a suitable Bragg reflector at the output end face for the waveguide Prior to spin-coating, the silicon substrate is etched with periodic rulings which produce the desired Bragg reflector upon RE polymer material deposition Coupling of light into and out ofthe waveguide can be accomplished by using another Bragg grating as an input coupler In addition, simple end fire coupling, filtering, and detection are easy alternative options

Claims: WHAT IS CLAIMED IS: 1 An optical material made from at least one polymer of a general composition {X[OOPRR'] 3 } n where X is a rare earth element, R is a fully halogenated organic group, and R' is a second fully halogenated organic group 2 The material of claim 1 , wherein X is selected from the group consisting of erbium, europium, samarium, dysprosium, neodymium, praseodymium, thulium and ytterbium 3 The material of claim 1 , wherein R and R' are fluoroalkyl chains of a general composition C m F 2m+I where m > 1 and R ≠ R 1 4 The material of claim 1 , wherein R and R' are fluoroalkyl chains of a general composition C m F 2m+1 where m > 1 and R = R' 5 The material of claim 1, wherein R = R' and is a hexafluorophenoxy group of a composition C 6 F 5 O 6 The material as claimed in claim 1, further comprising fiuoropolymers 7 The material as claimed in claim 6, wherein the fluoropolymer is a fluorinated polyimide, polytetrafluorethylene, or a derivative of polytetrafluoroethylene, fluorinated acrylate or fluorinated sihcone 8 The material of claim 1, further comprising at least one halogenated polymer 9 The material of claim 1 , further comprising at least one fluorophosphate glass 10. An optical amplifying fiber comprising a fiber core composed ofthe material of claim 1, and a fiber cladding comprised of a lower refractive index material, such that a core-cladding refractive index difference is small enough to result in a single optical mode propagation for optical wavelengths ranging from 1200-1700 nm. 1 1. An optical amplifying film comprising: a substrate, a buffer film, and a guiding layer film, the guiding layer film composed ofthe material as claimed in claim 1, and an upper cladding layer film, such that refractive indices ofthe buffer film and the upper cladding film are less than that ofthe guiding layer film, with a resulting waveguide guiding a single optical mode for optical wavelengths ranging from 1200-1700 nm.

Inventors: GAO RENYUAN, GARITO ANTHONY F, NORWOOD ROBERT A, PANACKAL ANNA, GAO, RENYUAN, GARITO, ANTHONY, F., NORWOOD, ROBERT, A., PANACKAL, ANNA
Applicants: PHOTON X INC, PHOTON-X, INC.
Application year: 2000
Main classification: H01S3
IPC codes: C08G79, C08K3, C08L85, C08L101, H01S3