HIGHLY RESISTANT ALUMINUM-BASED ALLOY AND ARTICLE MADE FROM SAID ALLOY

Abstract: The invention relates to high strength aluminium - based alloy of Al-Zn-Mg-Cu system and the articles made thereof. The present alloy is characterized by the combination of improved properties: flowability, technological plasticity, fracture toughness while preserving high levels of strength properties. Said alloy comprises (mass.%): Zn 6.35-8.0 Si 0.01-0.2 Mg 0.5-2.5 Fe 0.06-0.25 Cu 0.8-1.3 Zr 0.07-0.2 Cr 0.001-0.05 Ti 0.03-0.1 Mn 0.001-0.1 Be 0.0001-0.05 and at least one element from the group of alkali-earth metals: K 0.0001-0.01 Na 0.0001-0.01 Ca 0.0001-0.01 Al-balance the sum Zr+2Ti ≤ 0.3%, and the ratio Si:Be ≥ 2. The invented alloy is suitable for producing large-sized, extruded, rolled and forged semiproduct articles used for manufacture of loaded members of aircraft, cars and other machinery.

Description: Field of the Invention. This invention relates to non-ferrous metallurgy, and in particular it relates to high strength aluminium based alloys of Al-Zn-Mg-Cu system. The invented alloy is suitable for producing extruded, rolled and forged semiproducts (mainly articles having large sections) used for manufacture loaded members of aircraft, lorries and cars, seagoing and river vessels, agricultural machinery. Background of the Invention. Al-Zn-Mg-Cu alloys are widely used in the aircraft and aerospace industries. Well-known is the Russian alloy of said system comprising (mass.%): Zn 6.5-7,3 Fe 0.2-0.4 Mg 1.6-2.2 Si <0.2 Cu 0.8-1.2 Al-balance Said alloy doesn't provide high (UTS,YTS) properties and fracture toughness (K IC ). The articles made from said alloy have limited efficiency in weight and unsatisfactory service life (Handbook, Aluminium alloys, 1984, Moscow, publ. "Metallurgy". The American alloys of Al-Zn-Mg-Cu system (7000 series) developed by ALCOA are also well-known. For instance, the alloy described in US Patent 4.828.631 comprises (in mass.%): Zn 5.9-8.2 Ti <0.06 Mg 1.5-4.0 Si <0.12 Cu 1.5-3.0 Fe <0.15 Zr 0.08-0.15 impurities <0.05each and <0.15 in total B<0.01 Al-balance Cr<0.4 This alloy has been developed for particular use in aircraft and aerospace articles. It has superior exfoliation corrosion resistance, but its hardenability is sacrificed. In case the semiproduct has the thickness of more than 100 mm, the service characteristics (fracture toughness, strength, plasticity, corrosion resistance and uniformity of properties in semiproducts' volume) become worse. All these shortcomings do not allow to produce large - sized articles from said alloy. The alloy described in US Patent 4.832.758 comprises (in mass.%): Zn 4.0-8.0 Mg 1.5-3.0 Cu 1.0-2.5 at least one element from the group: Cr 0.05-0.3 Mn 0.1-0.5 Zr 0.05-0.3 Al-balance This alloy is intended to be used for producing semiproducts (plates) of the limited thickness (not more than 64 mm) because when increasing the thickness of a semiproduct, its mechanical properties, fracture toughness and corrosion resistance are essentially reduced. The alloy desclosed in EP 0829552 comprises (in mass.%): Zn 5.2-6.8 Si ≤ 0.06 Mg 1.6-2.1 Fe ≤ 0.06 Cu 1.75-2.4 Fe+Si ≤ 0.11 Zr 0.08-0.15 Al-balance This alloy may be used for manufacture of wing members of jet aircraft, mainly spars, lower skins, etc. The disadvantage of this alloy is its' high sensibility to quenching rate which leads to sharp reducing the strength and fracture toughness in case the semiproduct has the thickness more than 60 mm. Therefore when irregular-shaped members (fittings, landing gear elements, etc) are to be manufactured from said alloy, the great difficulties arise in the process of mechanical working. Pechiney of France also has claimed several alloys of Al-Zn-Mg-Cu system. The alloy described in EP 0391815 comprises (in mass.%): Zn 5.5-8.45 Si ≤ 0.5 Mg 2.0-3.5 Fe ≤ 0.5 Cu 0.5-2.5 other elements 0.05 each but not more Cr 0.3-0.6 than 0.15 in total amount Mn 0.3-1.1 Al-balance This alloy is intended to be used for producing small-sized semiproducts (sheets, plates, extruded articles) prepared by powder metallurgy method. The disadvantage of such products is the low level of fracture toughness (K IC ) and low technological properties. The high strength Al alloy described in PCT/FR 97/00144 comprises (in mass.%): Zn 5.9-8.7 Si<0.11 Mg 1.7-2.5 Fe<0.14 Cu 1.4-2.2 Zr 0.05-0.15 Cr <0.02 Mg+Cu <4.1 Mn <0.02 Al-balance The technological properties (flowability, technological plasticity) of this alloy are insufficient, and besides it has a reduced level of fracture toughness (K IC ). The articles made from this alloy (i.e. fittings, frames) have non-uniform strength properties and fracture toughness upon thickness particularly in case of large sections. Description of the Invention. The object of the present invention is to provide aluminium-based alloy of Al-Zn-Mg-Cu system having the improved combination of properties such as flowability, technological plasticity, increased fracture toughness, and also ensuring the uniformity of mechanical properties and fracture toughness upon product's thickness while preserving high levels of strength properties, and to provide the articles made from said alloy with said properties. Accordingly, there is provided Al-Zn-Mg-Cu alloy comprising (in mass.%): Zn 6.35-8.0 Si 0.01-0.2 Mg 0.5-2.5 Fe 0.06-0.25 Cu 0.8-1.3 Zr 0.07-0.2 Cr 0.001-0.05 Ti 0.03-0.1 Mn 0.001-0.1 Be 0.0001-0.05 at least one element from the group consisting of alkali-earth metals: K 0.0001-0.01 Na 0.0001-0.01 Ca 0.0001-0.01 Al-balance Zr+2Ti ≤ 0.3 andSi:Be ≤ 2 and the article made thereof. Alloying of the claimed alloy with additional elements - Be and at least one element from the group consisting of alkali-earth metals - K, Na, Ca, leads to increase in melt flowability upon casting due to their interaction with blisters and hydrogen being present in the metal, which in turn allows to perform melt filtration and gegassing more effectively, that means to increase its purity and, as a result, to improve the technological plasticity of ingots. The optimum ratio or Zr and Ti combined with lower amount of Cu and in presence of at least one of the alkali-earth metals- K, Na, Ca, provide improved level of fracture toughness while preserving high level of strength properties due to the reduction of volume content of primary phases and their refining, and also provide great uniformity of mechanical properties and fracture toughness upon product's thickness owing to more uniform distribution of secondary phases' particles in micrograin's volume, which ensures better hardenability of the present alloy. Embodiments of the present invention will now be described by way of example. Example. For the purpose of the experiments, the ingots were cast from the alloys, the compositions of which are given in Table 1. The alloys 2-9 are embodiments of the present invention (the present alloys or the claimed alloys), and the alloy 1 - invention of PCT/FR 97/00144. The hand forgings of 60, 100, 150, 200 mm thickness (t) were made from homogenized ingots by the method of upsetting on a vertical press and the strips of 50 and 130 mm thickness (t) were made by extrusion on a horizontal press. Semiproducts were heat treated as follows: solution heat treatment at temperature of 470°C, time (depending upon semiproduct's thickness) varied from 1 to 3 hours; and water-quenching including two steps, the first step at a temperature of 115°C for 6 hours, and the second step at a temperature of 170°C for 10 hours. The alloys flowability was estimated by conventional method by the length of a straight rod cast into a metallic mold. The technical plasticity was estimated by two methods: by upsetting the cylindrical samples on a press until a side crack appeared, and by tensile testing the conventional cylindrical samples. The strength properties and fracture toughness of the alloys were estimated on conventional samples cut from different zones upon the thickness (t) of the semiproducts (1/4 t and 1/2 t) in longitudinal (L or L-T ) and short transverse (S or S-L) directions relative to fiber direction. Table 2 shows the results of testing for technological properties' estimation of the alloys of the present invention and the prior art. The results given in this Table evidently show that the present alloy (compositions 2-9) 1,2-1,4 times exceeds the known alloy in flowability and technological plasticity. Table 3 shows the properties of a central zone of the forgings with 150 mm thickness made of the present alloy and the known alloy. One can evidently see from Table 3, that the present alloy 1.4-1.7 times exceeds the known alloy in fracture toughness in L-T direction, and 1.2-1.4 times - in S-T direction while the strength properties of both alloys are nearly the same. The best values of fracture toughness were defined on the alloys 3-5, 7, 9 which had ratios Ti+2Zr ≤ 0.3 and Si:Be ≥ 2. Table 4 shows the mechanical properties of semiproducts with different thicknesses made of the present alloy and of the prior art alloy. The data of Table 4 shows that the present alloy as compared with the known alloy, provides more uniform mechanical properties and fracture toughness upon semiproducts' thickness what can especially be seen on large section samples with thickness of ≥ 150 mm; said samples show 1,5-2 times less reduction of strength properties and fracture toughness as compared with the known alloy. The present alloy having improved flowability, technological plasticity, fracture toughness, and also more uniform strength properties and fracture toughness upon thickness, allows to produce wide range of semiproducts (forged, extruded and rolled) practically of any shape and dimensions, especially of large section. The large-sized integral articles having uniform properties made of the present alloy will allow to increase by 10-20% the weight efficiency of the structure due to reduction of riveted joints' number and will ensure 15-20% increase of service reliability owing to improved fracture toughness. The improvement of technological properties of the present alloy will ensure reduction of faulty production from said alloy, and use of large-sized semiproducts in aircraft structure will reduce labour intensity of assembling and will make the aircraft more economical by 30-40%. Producing and use of the present alloy and articles thereof do not deteriorate environment from the ecological point of view. Technological properties of experimental alloys Alloy Flowability, mm Technological plasticity, % upon upsetting on a press upon tensile 1 Prior Art 270 70 85 2 360 89 135 3 370 94 140 4 370 97 138 5 380 95 135 6 365 87 133 7 375 95 145 8 360 88 135 9 385 95 143 Properties of hand forgings with 150 mm thickness in central zone (1/2t) Alloy UTS, MPa YTS, MPa K IC MPa √ m L ST L ST L-T S-L 1 Prior Art 490 467 420 405 31,5 26,2 2 528 515 485 477 45,3 31,5 3 520 510 483 470 47,5 33,0 4 495 490 448 442 50,1 34,5 5 505 490 450 440 47,7 34,3 6 508 491 451 443 45,6 32,9 7 509 489 455 450 47,0 34,0 8 512 493 450 448 46,9 32,0 9 502 495 455 450 47,5 34,5

Claims: High strength alloy of aluminium-zinc-magnesium-copper system comprising (in mass.%): Zn 6.35-8.0 Si 0.01-0.2 Mg 0.5-2.5 Fe 0.06-0.25 Cu 0.8-1.3 Zr 0.07-0.2 Cr 0.001-0.05 Ti 0.03-0.1 Mn 0.001-0.1 Be 0.0001-0.05 and at least one element from the group of alkali-earth metals: K 0.0001-0.01 Na 0.0001-0.01 Ca 0.0001-0.01 Al-balance High strength aluminium-based alloy of claim 1, characterized in that the sum Zr+2Ti ≤ 0.3 % High strength aluminium-based alloy of claim 1,2 characterized in that the ratio Si:Be ≥2. The article made of the high strength aluminium-based alloy characterized in that said alloy has the following composition (mass.%) Zn 6.35-8.0 Si 0.01-0.2 Mg 0.5-2.5 Fe 0.06-0.25 Cu 0.8-1.3 Zr 0.07-0.2 Cr 0.001-0.05 Ti 0.03-0.1 Mn 0.001-0.1 Be 0.0001-0.05 and at least one element from the group of alkali-earth metals: K 0.0001-0.01 Na 0.0001-0.01 Ca 0.0001-0.01 Al-balance

Inventors: FRIDLYANDER IOSIF NAUMOVICH, KABLOV EVGENY NIKOLAEVICH, SAMONIN VLADIMIR NIKOLAEVICH, TKACHENKO EVGENIYA ANATOLIEVNA, VALKOV VIKTOR YAKOVLEVICH, FRIDLYANDER, IOSIF NAUMOVICH, KABLOV, EVGENY NIKOLAEVICH, SAMONIN, VLADIMIR NIKOLAEVICH, TKACHENKO, EVGENIYA ANATOLIEVNA, VALKOV, VIKTOR YAKOVLEVICH
Applicants: FEDERALNOE G UNITARNOE PREDPR, JOINT STOCK COMPANY SAMARA MET, FEDERALNOE GOSUDARSTVENNOE UNITARNOE PREDPRIYATIE "VSEROSSIYSKY NAUCHNO-ISSLEDOVATELSKY INSTITUT AVIATSIONNYKH MATERIALOV", JOINT-STOCK COMPANY "SAMARA METALLURGICAL PLANT"
Application year: 2000
Main classification: C22C21
IPC codes: C22C21