BIODEGRADABLE POLYMER COMPOSITIONS, METHODS FOR MAKING SAME AND ARTICLES THEREFROM

Abstract: A polymer composition includes a first component being a hydroxy-functional polymer, a second component being a natural polymer and a third component being a thermoplastic polyester. The first component, second component and third component are compounded to form a polymer composition.

Description: BIODEGRADABLE POLYMER COMPOSITIONS, METHODS FOR MAKING SAME AND ARTICLES THEREFROM GOVERNMENT RIGHTS IN INVENTION The present invention was made with government support under Grant Agreement No. 59-3K95-3-126 awarded by the United States Department of Agriculture, Agricultural Research Services. The government has certain rights in this invention. BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates generally to polymer compositions and, more particularly, to biodegradable polymer compositions, methods for making same and articles therefrom. 2. Description of the Related Art Starches and modified starches have been the focus of considerable research interest in attempts to use these as fillers in order to decrease polymer costs and to use polymers that are biodegradable. Several recent examples, U.S. Patent No. 5,384,187, issued January 24, 1995, inventors Uemura et al., U.S. Patent No. 5,391,423, issued February 21, 1995, inventors nuk et al., and U.S. Patent No. 5,412,005, issued May 2, 1995, inventors Bastioli et al., all represent domestic and foreign based attempts to achieve biodegradable polymer compositions in which natural polymers such as starches have been added to hydroxy-functional polymers . Recent biodegradable polymer compositions have included a starch or a modified starch ana a hydroxy-functional polymer. An example of such a biodegradable polymer composition is disclosed in U.S. Patent No. 5,852,078, issued December 22, 1998, to inventors illett et al. This biodegradable polymer composition includes the use of granular starch and thermoplastic poly(hydroxy ester ethers) (PHEE) made with various difunctional acids such as adipic acid. However, uses of this composition may be extremely limited due to the low glass transition temperature of the PHEE made with adipic. Most articles formed from this composition easily softened and lost their shape at high temperatures of up to and more than 100°C. Further, it is known to mix starch with a thermoplastic polyester such as poly (lactic acid) (PLA) . It is also known that such a mixture is immiscible and any resultant article formed is brittle with poor material properties. Therefore, there is a need in the art to provide polymer compositions with hydroxy-functional polymers and thermoplastic polyesters that are useful m the manufacture of biodegradable plastics, but which are easily prepared and processed into articles that keep their shape at high temperatures . SUMMARY OF THE INVENTION Accordingly, the present invention is polymer composition. The polymer composition includes a first component being a hydroxy- functional polymer, a second component being a natural polymer and a third component being a thermoplastic polyester. The first component, second component and third component are compounded to form the polymer composition. Also, the present invention is an article. The article includes a first component being a hydroxy-functional polymer, a second component being a natural polymer and a third component being a thermoplastic polyester. The first component, second component and third component are compounded to form a polymer composition which is processed into the article. Further, the present invention is a method of making a polymer composition. The method includes the steps of providing a first component being a hydroxy-functional polymer, providing a second component being a natural polymer and providing a third component being a thermoplastic polyester. The method includes the steps of compounding the components to form a polymer composition. The polymer compositions of the present invention are biodegradable and useful in various processes such as molding, extruding and casting to form molded articles and extruded sheets. The hydroxy-functional polymer may be as described by U.S. Patent No. 5,171,820, issued December 15, 1992, to inventors Mang et al., U.S. Patent No. 5,496,910, issued March 5, 1996, to inventors Mang et al . , and PCT application published as International Publication No. WO 97/23564, on July 3, 1997, to inventors Mang et al. Natural polymers for mixture with the hydroxy-functional polymers include polysacchaπdes, modified polysacchar des, naturally-occurring fibers, and particulate fillers. Particularly preferred as the natural polymer are starches. The thermoplastic polyesters for mixture with the natural polymers and hydroxy-functional polymers include poly(lactιc acid) (PLA), bionolle, cellulose acetate, polycaprolactone ana polyhydroxy (butyrate-co-valerate) (PHBV). One advantage of the present invention is that new polymer compositions are provided which are useful m the manufacture of biodegradable plastics. Another advantage of the present invention is that a method is provided of making such polymer compositions. Yet another advantage of the present invention is that articles are easily prepared from such polymer compositions that keep their shape at high temperatures of up to and more than 100°C. Still another advantage of the present invention is that the polymer compositions contain starch and a hydroxy-functional polymer such as poly(hydroxy ester ether) (PHEE) and a thermoplastic polyester such as poly (lactic acid) (PLA) . A further another advantage of the present invention is that the method compounds the composition m at least one compounding step. Yet a further advantage of the present invention is that the compounded composition is pelletized for further processing m various processes such as injection molding. Still a further advantage of the present invention is that the polymer compositions are biodegradable and allow molded items to be formed such as planter pots, disposable razors, cutlery, pen casings, etc., with little concern of softening at h gh temperatures of up to and more than 100°C. Other features and advantages of the present invention will be readily appreciated as the same becomes better understood after reading the subsequent description, examples and the appended claims . DESCRIPTION OF THE PREFERRED EMBODIMENT (S) Broaαly, the present invention is a polymer composition comprising three main components: the first component is a hydroxy- functional polymer, more particularly, a hydroxy-functional polyester having a repeating structure as will hereinafter be described. The hydroxy-functional polymer may be, for example, a thermoplastic poly(hydroxy ester ether) (PHEE). The second component is a natural polymer. The natural polymer may be, for example, a polysaccharide, a modified polysaccharide, or a naturally occurring fiber or particulate filler, but preferably is starch or a modified starch. The third component is a thermoplastic polyester. The thermoplastic polyester may be, for example, a thermoplastic polydactic acid) (PLA). While the amount of the hydroxy-functional polymer selected for use depends on a variety of factors, including the specific polymer employed and the desired end uses of the composition, m general hydroxy-functional polymers can be present m an amount of from 1 to 99 wt . % , preferably from 1 to 95 wt . % , and most preferably from 10 to 90 wt.%, based on the total weight of the composition. Preferably, the thermoplastic polyester is a poly(lactιc acid) (PLA), present m amounts of about equal to or greater than the amount of the hydroxy-functional polymer used in the formulation of the composition. Natural polymers contemplated for use include Piodegradable organic fillers, such as cellulose and other fibers and the like, which are well known. Naturally occurring fibers or particulate fillers which can be employed m the practice of the present invention for preparing tne composition are, for example, wood flour, wood pulp, wood fibers, cotton, flax, hemp, or ramie fibers, rice or wheat straw, chitin, chitosan, cellulose materials derived from agricultural products, nut shell flour, corn cob flour, and mixtures thereof. Polysacchaπdes which can be employed in the practice of the present invention for preparing the composition are the different starches, celluloses, hemicelluloses, gums, pectins, and pullulans. Polysaccharides are known and are described, for example, m Encyclopedia of Polymer Science and Technology, 2nd edition, 1987. Modified polysaccharides which can be employed in the practice of the present invention for preparing the composition are the esters and ethers of polysaccharides, such as, for example, cellulose ethers and cellulose esters, or starch esters and starch ethers. Modified polysaccharides are known and are described, for example, in Encyclopedia of Polymer Science and Technology, 2nd edition, 1987. The natural polymer is m a granular form (hereinafter referred to as the "granular embodiment") . When practicing the granule embodiment of the present invention, the granules of natural polymer preferably will have a particle size of less than about 100 μm, and more preferably have a particle size of up to about 50 μm and a water content of less than about 15 wt . % , more preferably less than about 10 or 11 wt . % . In the granule embodiment, the three main components may be admixed m varying amounts. The natural polymer may be present m a trace amount or in greater amounts up to about "0 wt . % . Suitable Hydroxy-Functional Polymers The preparation and structures for hydroxy-functional polymers, such as hydroxy-functional polyesters, suitable m practicing the present invention may be as described by U.S. Patent No. 5,171,820, issued December 15, 1992, to inventors Mang et al., and U.S. Patent No. 5,496,910, issued March 5, 1996, to inventors Mang et al., the disclosures of which are hereby incorporated in their entireties by reference. Such useful hydroxy-functional polyesters for the present invention may be prepared from base- catalyzed nucleophilic addition of suitable acids to epoxies, which reaction generates both an ester linkage and a pendent hydroxyl group. Transesterification and cross linking reactions are eliminated through use of quaternary ammonium halide salts as initiators for the reaction of diacids with diglycidyl ethers, providing convenient preparation of high molecular weight, thermoplastic, hydroxy-functional polyesters m ether solvents at temperatures from 80°C-160°C. Data provided by the Dow Chemical Company (manufacturer of hydroxy-functional polyesters such as described by U.S. Patents Nos . 5,171,820 and 5,496,910) indicates the biodegradable nature of these polymers through the ability of various soil bacteria (such as Pseudomonas putida ) to use the synthetic polymers as a substrate for cell culture growth. Representative structures for suitable hydroxy-functional polyesters in practicing the present invention are represented by Formula A (where n provides a sufficient molecular weight, such as for example a m.w. of about 50,000-100,000. Higher molecular weights are preferred due to higher strength. FORMULA A In Formula A each of R 1 and R 2 is individually a divalent organic moiety which is predominately hydrocarbon, each R 3 is individually a hydrogen or lower aikyl, y is a fraction from 0 to 0.5 and x is a fraction from about 0.05 to about 0.4. Typically Y is hydrogen or glycidyl and Y' is glycidyl arylene ether, glycidyl alkyene ester, glycidyl alkylene ether or glycidyl arylene ester. Thus, suitable polyesters have repeating units represented by Formula B (where each of R 1 , R 2 , R 3 , x and y are as defined above) . FORMULA B Such polyesters may be prepared from diglycidyl esters of an aliphatic diacid such as adipic due to the ready availability and reasonable price for adipic acid as a source of reactant. Other particularly preferred polyesters may be prepared from dihydric phenols, such as hydroquinone . Four particularly preferred hydroxy-functional polyesters, used extensively to illustrate (but not to limit) the present invention, are sometimes hereinafter designated "BIS CHD," "BIS adipic," "HQ DDCA" and "BIS DDCA." These polymers will include some repeating unit structures, where the repeating units are illustrated respectively by Formulas C-F. FORMULA C In Formulas C-F, "n" preferably is as earlier described. Other suitable nydroxy-functional polymers for practicing the present invention are described py Formula I in PCT application published as International Publication No. WO 97/23564, on July 3, 1997, to inventors Mang et al., tne disclosure of which is hereby incorporated in its entirety by reference. The below illustrated repeating structure αescribed by U.S. Patent No. 5,496,910, issued March 5, 1996, to inventors Mang et al., incorporated herein by reference and designated here as Formula I is believed to encompass Formula B. Thus, the Formula I polymers have repeating units represented PV tne formula: o o )C-R a -COR c OR d O-R c -- I ; wherein R a individually represents a divalent organic moiety which is predominately hydrocarbylene (where the term "hydrocarbylene" means a divalent aliphatic Hydrocarbon moiety, such as alkylene, alkenylene or cycloalkylene having 2 to 20 carbons and optionally containing a heteroatomic group, such as oxygen, sulfur, ammo, sulfonyl, carboxyl, carbonyl or sulfoxyl, m the chain or pendant thereto) or a combination of different organic moieties which are predominantly hydrocarbylene; R c is OH CH,OH —CH,- CH,- or —CI-CH,— and wherein R b is a divalent organic moiety wnich is predominantly rydrocarbylene or R e is hydrogen or lower alkyl, such as methyl, ethyl, butyl and propyl, more preferably hydrogen, R f is independently an organic moiety which is predominantly hydrocarbylene, R 9 is independently hydrogen or methyl, n' is an integer from about 0 to about 100, and x' and y' are independently integers from 0 to 100. Representative divalent organic moieties useful as R a , R D , and R f include alkylene, cycloalkylene, alkylenearylene, poly(alkyleneoxyalkylene) , alkylenethioalkylene, alkylenesulfonylalkylene, alkylene substituted with at least one hydroxyl group, cycloalkylene substituted with at least one hydroxyl group, alkylenearylene substituted with at least one hydroxyl group, poly (alkyleneoxyalkylene) substituted with at least one hydroxyl group, alkylenethioalkylene substituted with at least one hydroxyl group, alkylenesulfonylalkylene substituted with at least one hydroxyl group, arylene, dialkylenearylene, diaryleneketone, diarylenesulfone, diarylene oxide, and diarylene sulfide . In the more preferred hydroxy-functional polyethers, R a , R and R f are independently methylene, ethylene, propylene, butylene, pentamethylene, hexamethylene, heptamethylene, octamethylene, nonamethylene, decamethylene, dodecamethylene, 1, 4-cyclohexylene, 1, 3-cyclohexylene, or 1, 2-cyclohexylene optionally substituted with at least one hydroxyl group, p-phenylene, m-phenylene, or 2,6- naphthalene, diphenyleneisopropylidene, sulfonyldiphenylene, carbonyldiphenylene, oxydiphenylene, or 9, 9-fluorenediphenylene and n' is from 0 to 10. The polymers represented by Formula I may be prepared by reacting diglycidyl esters or aliphatic or aromatic diacids such as diglycidyl terephthalate, or diglycidyl ethers of dihydric phenols or alcohols with aliphatic or aromatic diacids such as adipic or terephthalic acid. Thus, suitable polymers for the present invention can be prepared by reacting a hydroxy-functional aliphatic diacid, optionally the presence of another diacid, with a diglycidyl ether or diglycidyl ester or a mixture of diglycidyl ethers or diglycidyl esters at conditions sufficient to cause the acid moieties to react with the epoxy moieties to form a polymer backbone having ester linkages, as described in U.S. Patent No. 5,171,820. Natural Polymers Among the natural polymers suitable for practicing the present invention are the particularly preferred starches. Starch is a low-cost and abundant natural polymer composed of amylose and amylopectm. Amylose is essentially a linear polymer having a number average molecular weight in the range of 100,000-500,000, whereas amylopectm is a highly branched polymer having a number average molecular weight of up to several million. Unmodified, natural starches are obtained in granular form and may be derived from cereals or grains (such as corn, wheat, rice and sorghum), roots (such as cassava), legumes (such as peas), and tubers such as potato and canna. Such starch granules typically have a particle size less than about 50μm, which is the preferred particle size when practicing tne granule emoodi ent . While less preferred, flours whose contents are predominately starch, and which may also contain protein, oil and fiber, are operative m the present invention. While such other natural polymers are used for granular embodiment formulations, they will be processed so as to be n granular form and preferaoly will have a relatively uniform particle size of about 50 μm or less. Starch granules for use m the granule embodiment will normally have a water content of less than about 15 wt.%, more preferably less than about 10 - 11 wt.%. As will be exemplified, granules may be pre-dried to less than about 1% moisture before compounding. Although preferred, pre-drying is not necessary. Derivatized (modified) starches are also suitable for use in the present invention. "Derivatized starches" is meant to include starches which have been chemically treated so as to form starch esters, starch ethers, and cross-linked starches. "Modified" is meant that the starch can be derivatized or modified by typical processes known in the art (e.g. esterification, etheπfication, oxidation, acid hydrolysis, cross-linking and enzyme conversion). Typically, modified starches include esters, such as the acetate ester of dicarboxylic acids/anhydrides . Particularly useful are the alkenyl-succmic acids, anhydrides, ethers (such as the nyoroxyethyl and hydroxypropyl starches), starches oxidized with hypochlorite, starches reacted with cross-linking agents such as phosphorus oxychloride, epichlorhydrm, hydrophobic cationic epoxides, and phosphate derivatives prepared by reaction with sodium or potassium orthophosphate or tripolyphosphate and combinations thereof. These and other conventional modifications of starch are described in publications such as Starch : Chemistry and Technology, 2nd edition, editor Whistler et al., and Starch Derivatives : Production and Uses, Rutenberg et al., Academic Press, Inc. 1984. For example, starch esters may be prepared using a wide variety of anhydrides, organic acids, acid chlorides, or other esterification reagents. Examples of anhydrides are acetic, propionic, butyric, and so forth. Further, the degree of esterification can vary as desired, such as from one to three per glucosidic unit of the starch, or as appropriate given the number of hydroxyl groups in the monomeric unit of the natural polymer, if selected to be other than starch. Similar or different esterified natural polymers, with varying degrees of esterification, can be blended together for practicing the present invention. Although esterified starches are stable to attack by amylases, in the environment the esterified starches are attached by microorganisms secreting esterases which hydrolyze the ester linkage. Starch esters tend to be hydrophobic in contrast to starch raw materials (that is, derived by usual techniques from natural sources such as corn) . Thus, depending upon the particular application, one may prefer to choose an hydrophobic starch ester rather than a hydrophilic starch in formulating compositions of the present invention. Although starches are preferred for use as the natural polymers, particularly due to ready availability and low cost, but as earlier noted, other suitable natural polymers (in or prepared to be in granular form of a suitable particle size) are hydroxyl containing polymers such as cellulose, hemicellulose, chit , guar gum, locust bean gum, pectin, xanthan, algm, agar, and dextran. Some of these can play the role of filler, also. Excellent results have been obtained with both granulated guar gum and cellulose powder. Suitable Thermoplastic Polyesters The composition includes a thermoplastic polyester. Among the thermoplastic polyesters, a poly(lactιc acid) (PLA) is preferred. The PLA is prepared and used m a pelletized form. Examples of other suitable thermoplastic polyesters include polyhydroxy (butyrate-co-valerate) (PHBV) , bionolle, cellulose acetate and polycaprolactone. It should be appreciated that these thermoplastic polyesters are conventional and known in the art. The thermoplastic polyesters may be prepared with additives to increase the rate of crystallization. For example, an additive such as boron nitride may be added to a thermoplastic polyester such as poly (lactic acid) (PLA) to increase the rate of crystallization of the PLA. It should be appreciated that other suitable additives may be addeα to the thermoplastic polyester to increase the crystallization. Other Components A plasticizer can be added to the inventive compositions to achieve greater material processability and product flexibility, although plasticizers typically soften the compositions m which they are included. This is not always true, however, of compositions of the present invention, as will be discussed hereinafter. Molded articles prepared from blends including plasticizers preferably use plasticizers that are biodegradable. Examples of biodegradable plasticizers include various esters, such as phthalate esters, and various other biodegradable esters known in the chemical arts. Inorganic fillers can be added, such as talc, calcium carbonate, diatomaceous earth, and so forth. Other optional components known m the art, including, but not limited to, anti-blockmg agents, anti-static agents, slip agents, pro-heat stabilizers, antioxidants, pro-oxidant, and additives may be incorporated, depending upon the application. Method of Making A method, according to the present invention, is provided for making a polymer composition. In general, the method includes providing a first component being a hydroxy-functional polymer, providing a second component being a natural polymer such as starch and providing a third component being a thermoplastic polyester such as poly (lactic acid) (PLA). The methoα includes mixing these components m a single screw extruder, a twin screw extruder, a Banbury mixer, a roll mill or any intensive mixer at a temperature and for a time sufficient to provide an intimate, well-dispersed mixture of the components. Preferably, the components are brought together and compounded in an appropriate melt extruder from which the blend is extruded in the form of strands or sheets. The strands or sheets are then pelletized and molded into articles by conventional processes such as injection molding. The method may include the step of forming bars from the sheets. The method may include the step of heating the polymer composition or formed bars for a predetermined time period such as up to 60 minutes ana at a predetermined temperature such as 120°C to increase high temperature stability. It should be appreciated that other additives or treatments may be used to impart high temperature stability of the formed bars. It should also be appreciated that such additives or heating causes an annealing of the polymer composition to increase high temperature stability thereof . EXPERIMENTAL Aspects of the present invention will now be illustrated, without intending any limitation, by the following examples. Unless otherwise indicated, all parts and percentages are by weight . EXAMPLE 1 Compositions of the present invention were made by the metnod, according to the present invention. Granules of starch, m this example cornstarch, pellets of PHEE Adipic (Adipic) and pellets of poly (lactic acid) (PLA) were provided and admixed. The granules of starch were pre-dried to approximately 1 wt.% moisture. These components were hand mixed and compounded. This compounding was performed on a Brabender PL2000 torque rheometer using a mixing screw with a fluteα dispersive mixing section and a notched distributive section. Temperatures during the compounding ranged from about 120°C to about 180°C. The resultant compositions were in the initial form of strands, which were then air cooled and pelletized. Specific compositions were chosen so that the final compounded pellets included as follows: Sample # 1 is 60 wt.% starch and 40 wt.% resin (PLA/Adipic) , of which the 40 wt.% resin consisted of 90% PLA and 10% Adipic, for a ratio of 60/36/4 of starch/PLA/Adipic; Sample #2 is 60 wt.% starch and 40 wt.% resin (PLA/Adipic) , of whicn the 40 wt.% resin consisted of 50% PLA and 50% Adipic, for a ratio of 60/20/20 of starch/PLA/Adipic; and Sample #3 is 60 wt.% starch and 40 wt.% resin, of which the 40 wt.% resin consisted of 10% PLA and 90% Adipic, for a ratio of 60/4/36 of starch/PLA/Adipic. The pellets formed were re-fed to the Brabender PL2000 torque rheometer, but fitted with a slit die (3.54 cm x 0.5 mm) to form a thin sheet. The sheets were stamped to form tensile bars for subsequent physical testing. Sample #1 did not provide a smooth sheet and it was difficult to stamp out representative tensile bars. Sample #2 provided tensile bars that had a tensile strength of 17.6 MPa and Sample #3 provided tensile bars that had a tensile strength of 30.4 MPa. EXAMPLE 2 Compositions of the present invention were made using cornstarch, PLA and Adipic. Starch/Adipic (60/40) pellets were prepared and processeα on a ZSK 30 Twin Screw Extruder. Moisture content of the starch was 4% to provide 60/40 pellets with a moisture content of approximately 2.4%. Samples of the composition were prepared by blending into the starch/Adipic (60/40) pellets various levels of the PLA pellets. The PLA pellets were added to make five different compositions which were compounded on the Brabender PL2000 torque rheometer of Example 1. Pellets were formed as m Example 1 and re-fed to the Brabender as Example 1. The extrudates of the various compositions were thm sheets that were stamped to provide tensile bars for subsequent physical testing. Several properties of the various compositions tested are summarized in Table A. Table A Sample No. 16191-2 Mass 60/40 PLA added %PLA(tot) %Starch %Adιoιc 1 96 4 4 57.6 38.4 2 92 8 8 55.2 36.8 3 88 12 12 52.8 35.2 4 84 16 16 50.4 33.6 5 80 20 20 48 32 Adipic /PLA %PLA Tensile (MPa) 9.6 9.4 31 4.6 17.9 25 2.9 25.4 21 2.1 32.3 25 1.6 38.5 29 EXAMPLE 3 Formulations of starch and resin were prepared into several compositions as in Example 1. These compositions contain 50 wt.% starch and 50 wt.% resin. The 50 wt.% resin consisted of 15 wt. % Adipic and 35 wt.% PLA; 20 wt.% Adipic and 30 wt.% PLA; and 25 wt.% Adipic and 25 wt.% PLA. The formulations were hand mixed and compounded on the Brabender PL2000 torque rheometer as previously described n Example 1. Thm sheets were obtained as in Example 1 for stamping out tensile bars. After allowing the tensile bars to remain for 7 days at 50% RH and 23°C, tensile properties were determined and summarized m Table B. Table B Sample Starch% Adιpιc% PLA% Tensile (MPa) 1 50 15 35 27 2 50 20 30 28 3 50 25 25 33 EXAMPLE 4 Dynamic mechanical analysis (DMA) was used to determine changes in the processed stranαs of composition of Example 3 after a particular heating period. A temperature of 120°C was selected and strands of composition were removed from an oven at zero minutes, 10 minutes, 20 minutes, 30 minutes, 40 minutes and 60 minutes. These neated stranαs were used for DMA. Samples of the strands showed that changes occurred rapidly with time as probe positions showed less and less movement with heating. At the temperature for 40 and 60 minutes, there was little movement as the temperature neared a melting temperature of 150°C. EXAMPLE 5 Additional compositions of 60 wt.% starch were made as Example 1. Starch was dπeα to approximately 1% moisture and hand mixed with various levels of Adipic and PLA as in Example 1. Samples were processed on the Brabender and thm sheets were formed as m Example 1. The thm sheets were stamped into tensile bars and tensile properties were obtained. The properties are summarized in Table C. Sample Starch Adipic PLA Tensile (MPa) 1 180g 24g 96g 14 2 180g 36g 84g 17 3 180α 48q 72g 21 EXAMPLE 6 Samples of the composition were prepared from starch, Adipic and PLA as in Example 1. The samples were hand mixed and compounded on the Brabenαer as in Example 1. The compounded samples were pelletized and used for injection molding on a Cincinnati Milicron 75T to form molded tensile bars. Tensile properties were ootamed and summarized in Table D. Table D Sample Starch Adipic PLA Tensile (MPa) 1 908g 363g 545g 38.6 2 1090g 291g 436g 34.1 EXAMPLE 7 Several samples of the composition were prepared with starch at a level of 40 wt.%, 50 wt.%, 55 wt.%, 60 wt.%, 65 wt.% and 70 wt.% and various levels of Adipic and PLA as m Example 1. The samples were hand mixed, compounded on the Brabender and pelletized as m Example 1. The pellets were used for injection molding on the Cincinnati Milicron 75T to form molded tensile bars as in Example 6. Tensile properties were obtained and summarized in Table E. Table E Sample Starch% Adιpιc% PLA% Tensile (MPa) 1 40 26.7 33.3 39 2 50 15 35 28 3 50 10 40 28 4 55 11 34 28 5 60 12 28 32 6 65 10.5 24.5 - 7 70 9 21 _ EXAMPLE 8 A composition of starch 50 wt.%, Adipic 20 wt.% and 30 wt.% PLA was prepared and hand mixed. Sufficient boron nitride was added into the hand mixed composition to increase the rate of crystallization of PLA and to be approximately 1 wt.% of the PLA added. The composition was compounded on the Brabender and pelletized as in Example 1. The pellets were used for injection molding on the Cincinnati Milicron 75T to form molded tensile bars as in Example 6. Tensile properties of the tensile bars were 29MPa. DMA gave curves similar to a composition made without boron nitride . EXAMPLE 9 Attenuated Total Reflectance by FTIR data was obtained for the samples in the Example 7. The spectra were compared to spectra of PLA and Adipic. The surfaces of the tensile bars consited mostly of PLA. Also, partial spectra of Apidic could be seen. EXAMPLE 10 Two compositions were prepared, one with starch 49.5 wt.%, Apidic 19.8 wt.% and PLA 29.7 wt.%, and the other with starch 59.4 wt.%, Adipic 15.8 wt.% and PLA 23.8 wt.%. To each composition was added WaxOP of 1 wt.% as an external lubricant to assist n compounding and injection molding. The compositions were hand mixed and then compounded on a Leistritz Extruder. Strands produced from the Leistritz were pelletized. The pellets were used for injection molding on a Cincinnati Milicron 75T to form molded tensile bars as in Example 6. For injection molding, a mold temperature of either 205°F or 150°F was selected. Mold hold times were selected as 20 seconds or 60 seconds. Tensile bars were molded, collected and stored at 50% RH and 23°C. Another two compositions were prepared, one with starch 63.7 wt.%, Adipic 13.7 wt.% and PLA 20.67 wt.%, and the other with starch 68.6 wt.%, Adipic 11.8 wt.% and PLA 17.6 wt.%. To each composition was added WaxOP of 2 wt.% as an external lubricant to assist in compounding and injection molding. The compositions were hand mixed and then compounded with a Leistritz Extruder. Strands from Leistritz were pelletized. The pellets were used for injection molding on a Cincinnati Milicron 75T to form molded tensile bars as in Example 6. For injection molding, a mold temperature of 210°F was selected for the 63.7 wt.% starch composition and 150°F was selected for the 68.6 wt.% starch composition. The tensile properties are summarized in Table F. Table F Sample Starch Adipic PLA Mold Temp Mold Time Tensile (MPa) 1 49.5 19.8 29.7 205 20 34 2 205 60 31 3 150 20 33 4 150 60 35 5 59.4 15.8 23.8 205 20 34 6 205 60 37 7 150 20 40 8 150 60 33 g* 54.5 14.5 30.1 150 20 39 10 63.7 13.7 20.6 210 20 37 11 210 60 34 12 68.6 11.8 17.6 217 20 33 13 217 60 38 *Sample 9 was prepared by taking lOOg of pellets from the 60 wt.% starch composition and blending into it lOg of PLA. The blended sample was fed into the Cincinnati Milicron 75T to form molded tensile bars. EXAMPLE 11 Tensile bars from samples in Example 10 were selected for heating trials. Tensile bars containing 49.5 wt.% starch, 63.7 wt.% starch and 68.6 wt.% starch were heated at 100°C in an oven for 30, 15, 10, 5, 2.5 or 0 minutes. The heated tensile bars, after a brief cooling, were placed in a 2000ml beaker filled to approximately 1500ml with water heated to 98°C to 100°C on a heating plate. Water was kept at 98°C to 100°C during the heating trials. Tensile bars were immersed the heated water at about a 45 degree angle so that one could observe any bending of the tensile bars with time m the heated water. All tensile bars that were not heated the oven, zero time, rapidly bent a few seconds. Tensile bars heated for 2.5 minutes also bent with several seconds. All of the other tensile bars heated in the oven for 5, 10, 15 or 30 minutes retained their shape for one hour in the heated water. Upon removal from the heated water, the zero time and 2.5 minute time gave tensile bars that were bent while the other tensile bars retained their shape. EXAMPLE 12 Dry starch has been found useful m compositions of the present invention. The compositions were prepared using two types of starch, one normal cornstarch (Buffalo 3401, Formula I) and a 3:1 blend of potato and rice starches (Formula II). The starches were pre-dried to less than 1% moisture content and then compounded in a ZSK-30 Twin Screw Extruder with Apidic at a 60/40 ratio. Strands from the extruder were pelletized. The pellets were mixed with PLA to give a final ratio of 40/27/33 starch/Apidic/PLA and passed through a Brabender 19mm Single Screw Extruder using a fluted mixing screw at 160°C. Resulting pellets were injection molded to form molded tensile bars on a Cincinnati Milacron injection molder. Formula I had a tensile strength of 43 MPa, elongation of 4.3% and Young's Modulus of 1.4 GPa. Formula II had a tensile strength of 45 MPa, elongation of 4.1% and a Young's Modulus of 1.5 Gpa. EXAMPLE 13 Compos itions were prepared us ing the steps previously outlined Example 1 . The compositions made consisted of 60 wt . % starch and 40 wt . % Adipic/polyhydroxy (butyrate-co-valerate ) ( PHBV) . Resin blends Adipic and PHBV were then compounded on the Brabender as in Example 1. Resin ratios varied from 90/10, 50/50 and 10/90. Pellets of the combined resins were blended with starch and compounded on the Brabender. Strands from the Brabender were pelletized. The pellets were re-fed to the Brabender fitted with a slit die. Thm slit films were collected and stamped to form tensile bars. Tensile properties were 12.3 MPa for the 50/50 resin composition and 26.3 MPa for the 90/10 Adipic PHBV. EXAMPLE 14 Compositions were prepared using Adipic polyester. The Adipic polyester was hand mixed with equivalent amounts of other additional resins. The mixed 50/50 samples were Adipic Bionolle, Adipic Eastman cellulose acetate, and Adipic polycaprolactone. Each of these mixtures were blended with starch to give three compositions of starch 60 wt.% and mixed resins 40 wt.%. These compositions were compounded on the Brabender fitted with a slit die. Tensile bars were stamped from the thm films from the die for physical properties. Tensile properties were 11.8 MPa for the Bionolle, 8.4 MPa for the cellulose acetate and 12.5 MPa for the polycaprolactone . The present invention has been described in an illustrative manner. It is to be understood that the terminology used is intended to be in the nature of words of description rather than of limitation and the examples are intended to illustrate and not limit the scope of the present invention. Therefore, with the scope of the appended claims, the present invention may be practiced other than as specifically described.

Claims: WHAT IS CLAIMED IS: 1. A polymer composition: a first component being a hydroxy-functional polymer; a second component being a natural polymer; and a third component being a thermoplastic polyester, wherein the first component, second component and third component are compounded to form the polymer composition. 2. A polymer composition as set forth in Claim 1 wherein the natural polymer is starch. 3. A polymer composition as set forth Claim 2 wherein the starch is granular. 4. A polymer composition as set forth in Claim 1 wherein the hydroxy-functional polymer is a poly(hydroxy ester ether) (PHEE). 5. A polymer composition as set forth m Claim 1 wherein the thermoplastic polyester is one from a group comprising poly (lactic acid) , bionolle, cellulose acetate, polycaprolactone and polyhydroxy (butyrate-co-valerate) (PHBV) . 6. A polymer composition as set forth m Claim 1 wherein the second component is present an amount up to about 70 wt.%. 7. A polymer composition as set forth in Claim 1 wherein the third component is present an amount about equal to or greater than the first component. 8. A polymer composition as set forth m Claim 1 wherein the polymer composition is compounded a plurality of times. 9. A polymer composition as set forth in Claim 1 wherein the natural polymer has a moisture content of less than about 15 wt.%. 10. A polymer composition as set forth in Claim 1 wherein the first component ranges from about 9 wt.% to about 40 wt.%, the second component ranges from about 40 wt.% to about 70 wt.% and the third component ranges from about 9 wt.% to about 40 wt.%. 11. A polymer composition as set forth in Claim 1 wherein the polymer composition is biodegradable. 12. A polymer composition as set forth m Claim 1 wherein the polymer composition is processed into an article that keeps its shape at temperatures of up to and more than 100°C. 13. A polymer composition as set forth in Claim 1 wherein the polymer composition is annealed to increase high temperature stability. 14. An article comprising: a first component being a hydroxy-functional polymer; a second component being a natural polymer; a third component being a thermoplastic polyester, wherein the first component, second component and third component are compounded to form a polymer composition which is processed into the article. 15. An article as set forth m Claim 14 wherein the natural polymer is starch. 16. An article as set forth in Claim 15 wherein the starch is granular. 17. An article as set forth in Claim 14 wherein the hydroxy- functional polymer is a poly(hydroxy ester ether) (PHEE). 18. An article as set forth in Claim 14 wherein the thermoplastic polyester is one from a group comprising poly (lactic acid) , bionolle, cellulose acetate, polycaprolactone and polyhydroxy (butyrate-co-valerate) (PHBV). 19. An article as set forth m Claim 14 wherein the second component is present m an amount up to about 70 wt.%. 20. An article as set forth in Claim 14 wherein the third component is present in an amount about equal to or greater than the first component. 21. An article as set forth in Claim 14 wherein the first component ranges from about 9 wt.% to about 40 wt.%, the second component ranges from about 40 wt.% to about 70 wt.% and the third component ranges from about 9 wt.% to about 40 wt.%. 22. An article as set forth in Claim 14 wherein the article keeps its shape at temperatures of up to and more than 100 °C. 23. An article as set forth in Claim 14 wherein the article is biodegradable. 24. An article as set forth in Claim 14 wherein the natural polymer has a moisture content of less than about 15 wt.%. 25. An article as set forth in Claim 14 wherein the article is annealed to increase high temperature stability thereof. 26. A method of making a polymer composition, said method comprising the steps of: providing a first component being a hydroxy-functional polymer; providing a second component being a natural polymer; providing a third component being a thermoplastic polyester; and compounding the components to form a polymer composition. 27. A method as set forth in Claim 26 including the step of mixing the first component, second component, and third component together to form a mixture prior to said step of compounding. 28. A method as set forth in Claim 26 including the step of forming strands of the polymer composition. 29. A method as set forth in Claim 26 including the step of extruding the polymer composition. 30. A method as set forth in Claim 26 including the step of pelletizing the polymer composition to form pellets. 31. A method as set forth in Claim 26 wherein said step of providing comprises providing the third component in an amount about equal to or greater than the first component. 32. A method as set forth in Claim 26 including the step of providing the second component in an amount up to about 70 wt.%. 33. A method as set forth in Claim 26 wherein said step of mixing comprises dry blending the mixture. 34. A method as set forth in Claim 26 wherein the natural polymer of the second component is starch. 35. A method as set forth in Claim 26 wherein the hydroxy- functional polymer is a poly(hydroxy ester ether) (PHEE). 36. A method as set forth in Claim 26 wherein the thermoplastic polyester is one from a group comprising poly (lactic acid) , bionolle, cellulose acetate, polycaprolactone and polyhydroxy (butyrate-co-valerate) (PHBV) . 37. A method as set forth in Claim 26 wherein the first component ranges from about 9 wt.% to about 40 wt.%, the second component ranges from about 40 wt.% to about 70 wt.% and the third component ranges from about 9 wt.% to about 40 wt.%. 38. A method as set forth in Claim 27 wherein said step of compounding comprises compounding the mixture from about 120°C to about 180°C. 39. A method as set forth in Claim 27 wherein said step of compounding comprises compounding the mixture in an extruder a plurality of times. 40. A method as set forth in Claim 26 wherein the polymer composition is biodegradable. 41. A method as set forth in Claim 26 including the step of annealing the composition to increase high temperature stability thereof . AMENDED CLAIMS [received by the International Bureau on 29 August 2000 (29.08.00); original claims 8,12,14,22,27 and 39 amended ; remaining claims unchanged (8 pages)] 1. A polymer composition: a first component being a hydroxy-functional polymer; a second component being a natural polymer; and a third component being a thermoplastic polyester, wherein the first component, second component and third component are compounded to form the polymer composition. 2. A polymer composition as set forth in Claim 1 wherein the natural polymer is starch. 3. A polymer composition as set forth in Claim 2 wherein the starch is granular. 4. A polymer composition as set forth in Claim 1 wherein the hydroxy-functional polymer is a poly (hydroxy ester ether) (PHEE) . 5. A polymer composition as set forth in Claim 1 wherein the thermoplastic polyester is one from a group comprising poly (lactic acid) , bionolle, cellulose acetate, polycaprolactone and polyhydroxy (butyrate-co- valerate) (PHBV) . 6. A polymer composition as set forth in Claim 1 wherein the second component is present in an amount up to about 70 wt.%. s 7. A polymer composition as set forth in Claim 1 wherein the third component is present in an amount about equal to or greater than the first component. 8. A polymer composition as set forth in Claim 1 wherein the polymer composition is compounded at least once. 9. A polymer composition as set forth in Claim 1 wherein the natural polymer has a moisture content of less than about 15 wt.%. 10. A polymer composition as set forth in Claim 1 wherein the first component ranges from about 9 wt.% to about 40 wt.%, the second component ranges from about 40 wt.% to about C wt.% and the third component ranges from about 9 wt.% to about 40 wt.%. 11. A polymer composition as set forth in Claim 1 wherein the polymer composition is biodegradable. 12. A polymer composition as set forth in Claim 1 wherein the polymer composition is processed into an article that keeps its shape at temperatures of up to and about 100 β C. S 13. A polymer composition as set forth in Claim 1 wherein the polymer composition is annealed to increase high temperature stability. 14. An article comprising: a first component neing a hydroxy-functional polymer; a second component being a natural polymer; a third component being a thermoplastic polyester, wherein the first component, second component and third component are compounded no form a polymer composition which is processed by at, ieast one cf a group comprising pelletizing, extruding, molding, casting, stamping into the article. 15 . An article as set f orth in Claim 14 wherein the na tu ra l polymer is starch. 16. An article as set forth in Claim 15 wherein the starch is granular . 17. An article as set forth in Claim 14 wherein the hydroxy-functional polymer is a ρoly(hydroxy ester ether) (PHEE) . 18. An article as set forth in Claim 14 wherein the thermoplastic polyester is one from a group comprising poly (lactic acid), bionoLle, cellulose acetate, polycaprolactone and polyhydrox (butyrate-co- valerate) (PHBV) . 19. An article as set fortn in Claim 14 wherein the second component is present in an amount up to about 70 t. % . 20. An article as set forth in Claim 14 wherein the third component is present in an amount about equal to or greater than the first component. 21. An article as set forth in Claim 14 wherein the first component ranges from about 9 wt.% to about 40 wt.%, the second component ranges from about 40 wt.% to about 70 wt.% and the third component ranges from about 9 wt.% to about 40 wt.%. 22. An article as set forth in Claim 14 wherein the article keeps its snape at temperatures of up to and about 100 β C. 23. An article as set forth in Claim 14 wherein the article is biodegradable. 24. An article as set forth in Claim 14 wherein the natural polymer has a moisture content of less than about 15 wt.% . 25. An article as set forth in Claim 14 wherein the article is annealed to increase high temperature stability thereof. 26. A method of making a polymer composition, said method comprising the steps of: providing a first component being a hydroxy- functional polymer; providing a seconc component being a natural polymer; providing a third component being a thermoplastic polyester; and compounding the components to form a polymer composl ion. 27. A method as set forth in Claim 26 including the step of compounding includes pre-mixing the first component, second component, and third component together to form a mixture. 28. A method as set. forth in Claim 26 including the step of forming strands of the polymer composition. 29. A method as set forth in Claim 26 including the step of extruding the poxy er composition. 30. A method as set forth in CΛ aura 26 including the step of pelletizing the polymer composition to form pellets. 31. A method as set forth in Claim 26 wherein said step of providing comprises providing the third component in an amount about equal to or greater than the first component . 32. A method as set forth in Claim 26 including the step of providing the second component in an amount up to about. 70 wt.%. 33. A method as set forth m Claim 26 wherein said step of mixing comprises dry blending the mixture. 34. A method as set forth in Claim 26 wherein the natural polymer of the second component is starch. 35. A method as set forth in Claim 26 wherein the hydroxy-functional polymer is a poly(hydroxy ester ether) (PHEE) . 36. A method as set forth in Claim 26 wherein the thermoplastic polyester is one from a group comprising poly (lactic acid), bionolle, cellulose acetate, polycaprolactone and polyhydroxy (butyrate-co- valerate) (PHBV) . 37. A method as set forth in Claim 26 wherein the first component ranges from about 9 wt.% to about 40 wt.%, the second component ranges from about 40 wt.% to about 70 wt.% and the third component ranges from about 9 wt.% to about 40 wt.%. 38. A method as set forth in Claim 27 wherein said step of compounding comprises compounding the mixture from about l20 β C to about 180 β C. 39. A method as set forth m Claim 27 wherein said step of compounding comprises compounding the mixture in an extruder and re-feeding the compounded mixture to the extruder. 40. A method as set forth in Claim 26 wherein the polymer composition is biodegradable. 41. A method as set forth in Claim 26 including the step of annealing the composition to increase high temperature stability thereof.

Inventors: DOANE WILLIAM M, WILLETT JULIOUS L, DOANE, WILLIAM, M., WILLETT, JULIOUS, L.
Applicants: BIOTECHNOLOGY RES & DEV, BIOTECHNOLOGY RESEARCH AND DEVELOPMENT CORPORATION
Application year: 2000
Main classification: C08J3
IPC codes: C08J3, C08J5, C08K5, C08K11, C08L1, C08L3, C08L5, C08L67