BLISTER-RESISTANT MOLDED POLYUREA POLYMER AND METHOD OF MAKING A BLISTER-RESISTANT MOLDED POLYUREA POLYMER

Abstract: A polyurea-polymer formulation suitable for preparing a molded polyurea polymer includes a polyisocyanate, an isocyanate-reactive material, and a fatty-acid ester. The fatty-acid ester is present in an amount effective for providing a molded polyurea polymer prepared from the formulation with blister resistance such that when the molded polyurea polymer is exposed to moisture and a temperature of at least 350 DEG F (177 DEG C), the molded polyurea polymer is substantially free of blisters. A fatty-acid ester suitable for use with these formulations can be natural or synthetic, and one example includes jojoba oil. A polyurea-polymer formulation can also include other components known to be useful with polyurea polymers such as fillers, catalysts, surfactants, and polyepoxides. A molded polyurea polymer can be prepared from a polyurea-polymer formulation. One method suitable for preparing a molded polyurea polymer includes reaction injection molding.

Description: BLISTER-RESISTANT MOLDED POLYUREA POLYMER AND METHOD OF MAKING A BLISTER-RESISTANT MOLDED POLYUREA POLYMER This invention relates to polyurea polymers and polyurea-polymer lormulations and to methods of making polyurea polymers and polyurea-polymer formulations More particularly, this invention is directed to polyurea-polymer formulations that include a fatty-acid ester in an amount effective for providing blister resistance to a molded polyurea polymer prepared from a polyurea- polymer formulaϋon It is known in the art that isocyanate-based polymers can be useful for preparing moldings such as automobile fascia and body panels These isocyanate-based polymers include polyurea polymers. For example, U S Patent No 4,218,543 issued to Weber et al discloses preparing elastomeπc moldings by a reaction-injection-molding (RIM) process But polyurea polymers can be problematic in some applicaUons When a polyurea polymer is molded into, for example, a RIM part such as automobile fascia or automobile body panels, and the molded polymer is first exposed to moisture and then exposed to a high temperature such as a temperature greater than 350°F (177°C), surface defects in the molded polymer can be observed These defects can be particularly problematic when mica is used as a filler in a polyurea-polymer formulation In one common application, which is reaction inaction molding of body parts for automobiles, a molded polymer can be exposed to temperatures exceeding 350°F (177°C) Moreovei . these body parts can further be subjected to even higher temperatures when the parts are assembled onto an automobile and the automobile is subjected to known production conditions, such as an e-coat process For example, the parts assembled onto an automobile can be subjected to temperatures up to 400°F (204°C) for up to 30 minutes under general production conditions and sometimes for up to 60 minutes under experimental production conditions If a molded polymer contains too much water when it is exposed to heat, it can exhibit surface defects commonly known in the art as blistering Blistering generally occurs when moisture absorbed into the molded polymer interacts with the polymer to produce gas and the gas accumulates to form a gas pocket. In a laboratory, blister resistance is measured by soaking a test panel for two days in water and then exposing the panel to elevated temperatures. The temperature at which the panel fails is identified as the panel's temperature-capable point. One approach that has been used to overcome this blistering problem includes substituting wollastonite for mica as a filler. Another approach that has been used includes admixing a polyepoxide with a polyisocyanate and a polyamine. For example, U.S. Patent No. 5,525,681 issued to Barron et al. teaches polyurea polymers prepared from formulations including a polyisocyanate, a polyamine, and a polyepoxide. But, in some instances, these types of formulations, such as when mica is used as a filler, can lead to molded polymers that have a brittleness that is less than desirable for production conditions. Other solutions to address the blistering problem, such as avoiding exposure to high temperatures or moisture, are less than desirable because of properties that can be provided to a molded polymer from such exposure or because of unavoidable process or manufacturing conditions that a molded polymer can be exposed to. Thus, it would be desirable to prepare alternative polyurea polymers that can remain substantially free of blisters when exposed to moisture and elevated temperatures suitable for traditional production conditions such as postcuring and e-coat conditions. According to the invention, a polyurea-polymer formulation suitable for preparing a molded polyurea polymer includes a polyisocyanate, an isocyanate-reactive material, and a fatty-acid ester. The fatty-acid ester is present in an amount effective for providing blister resistance to a molded polyurea polymer prepared from the formulation such that when the molded polyurea polymer is exposed to moisture and a temperature of at least 350°F (177°C), the molded polyurea polymer is substantially free of blisters. In one embodiment, the fatty-acid ester includes jojoba oil. In another embodiment, the formulation further includes at least one of a chain extender, a catalyst, a surfactant, and an internal-mold-release agent. The formulation can also include a polyepoxide. A molded polyurea polymer can be prepared from a polyurea-polymer formulation of the invention by admixing a polyisocyanate, an isocyanate-reactive material, and a fatty-acid ester to form a mixture, and molding the mixture by using reaction injection molding. A method for preparing a polyurea-polymer formulation of the invention includes admixing a polyisocyanate, an isocyanate-reactive material, and a fatty-acid ester to form a mixture. The fatty- acid ester is added in an amount effective for providing blister resistance to a molded polyurea polymer prepared from the mixture such that when the molded polyurea polymer is exposed to moisture and a temperature of at least 350°F (177°C), the molded polyurea polymer is substantially free of blisters. The invention is directed to a polyurea-polymer formulation that can be used to prepare a molded polyurea polymer having blister resistance. The invention is further directed to a method of preparing a polyurea-polymer formulation that can be used to prepare a molded polyurea polymer having blister resistance. The invention is still further directed to a method of improving blister resistance of a molded polyurea polymer that is prepared from a polyurea-polymer formulation by adding a fatty-acid ester to a polyurea-polymer formulation. A polyurea-polymer formulation of the invention generally includes at least one polyisocyanate, at least one isocyanate-reactive material, and at least one fatty-acid ester. The fatty- acid ester is included in an amount effective for providing a molded polyurea polymer prepared from the formulation with blister resistance blister resistance means that when the molded polyurea polymer is exposed to moisture and a temperature of at least 350°F (177°C), the molded polyurea polymer is substantially free of blisters. A polyurea-polymer formulation of the invention can also include other components known to be useful with polyurea polymers, particularly fillers, catalysts, surfactants, and poly epoxides. A polyurea-polymer formulation of the invention includes a fatty-acid ester Any fatty-acid ester suitable for providing a molded polyurea polymer prepared from a formulation of the invention with blister resistance or improved blister resistance can be used in a formulation of the invention Suitable fatty-acid esters include both natural fatty-acid esters and synthetic fatty-acid esters Examples of natural fatty-acid esters include the following oils canola, castor, coconut, cotton seed, flax seed, hemp seed, jojoba, olive, palm, peanut, pumpkin seed, safflower, sesame, soybean, and sunflower Examples of synthetic fatty-acid esters include compounds such as glycerine tπoleate and pentaerythrttol tetraoleate and commercial esters such as Loxiol* G71S from Henkel Corporation and Polyaldo* DGDO from Lonza, Inc Synthetic fatty-acid esters suitable for use m the invention can be prepared from known methods Generally a synthetic fatty-acid ester can be prepared from reacting a fatty acid with at least one of an alcohol, an amino alcohol, and an amine Fatty acids suitable for preparing a synthetic fatty-acid ester are known and include saturated fatty acids, unsaturated fatty acids, or a combination of saturated and unsaturated fatty acids Examples of suitable fatty acids include πcinoleic acid, oleic acid, alaidic acid, steaπc acid, palmitic acid, linoleic acid, octanoic acids, acids obtained from coconut oil, tallow fatty acids, acids obtained from paraffin oxidation, and tall-oil fatty acids Preferably the fatty acid is oleic acid, linoleic acid, adipic acid, πcinoleic acid, or a combination of these acids More prefer bly the tatty acid is oleic acid. Amines and amino alcohols suitable for reacting with a fatty acid to prepare a synthetic fatty-acid ester are known and include, for example, ammonia, monoalkylamines such as methylamine, dialkylamines such as diethylamine, and amine alkoxylation products such as ethanolamine When a fatty acid is reacted with an amine or an amino alcohol, a mixture of a fatty- acid ester and a fatty-acid amide is typically produced This mixture can be used in a method or a composition of the invention Alcohols suitable for reacting with a fatty acid to prepare a synthetic fatty-acid ester are known and include, for example, butanol, hexanol, isomers of octanol, dodecanol, oleyl alcohol, natural or synthetic steroid alcohols, πcinoleic acid, ethylene glycol, propylene glycol, butanediols, hexanediols, glycerol, polyglycerol, trimethylolpropane, pentaerythritol, sorbitol. hexitol, and various sugars or addition products of alkylene oxides such as ethylene oxide or propylene oxide Preferably a synthetic fatty-acid ester is prepared by condensation of an alcohol and a fatty acid at elevated temperatures, which is a known method The temperature at which the reaction is conducted can be any temperature at which water is formed by reaction of the acid with the alcohol The reaction temperature can depend on other factors such as whether a catalyst is used, the nature and type of the catalyst, and the amount of catalyst present The catalyst can be either acidic or basic The reaction is preferably conducted at a temperature above 212°F (100°C), more pr el er ably above 248°F (120°C), and even more preferably above 302°F (150°C) The temperature preferably is less than 392°F (200°C) Such a reaction can be conducted in a vacuum, and water can be removed from the reaction mixture by, for example, azeotropic distillation But neither the use of a vacuum or removal of water is required A fatty-acid ester can be added to a polyurea-polymer formulation in an amount effective to improve blister resistance of a molded polyurea polymer prepared from a polyurea-polymer formulation of the invention as compared to blister resistance of a molded polyurea polymer prepared from a polyurea-polymer formulation that is substantially free of a fatty-acid ester A fatty-acid ester can also be added in an amount effective for providing a molded polyurea polymer prepared from a polyurea-polymer formulation of the invention with blister resistance such that when the molded polyurea-polymer formulation is exposed to moisture and a temperature of at least 350°F (177°C), preferably at least 375°F (190°C), more preferably at least 390°F (199°C), and still more preferably at least 400°F (204°C). the molded formulation is substantially free of blisters Generally the temperature is no greater than 425 °F (218 °C) , preferably no greater than 415 °F (213°C), and more preferably no greater than 405°F (207°C) A molded polyurea polymer can be exposed to such a temperature for time periods geneially used for production conditions such as time periods suitable lor postcuπng a molded polyurea polymer or time periods suitable for subjecting an automobile having a molded polyurea polymer to, for example, an e-coat process Typically a molded polyurea polymer can be exposed to such a temperature for at least 20 minutes, preferably at least 25 minutes, and more preferably at least 30 minutes Generally the exposure is not longer than 60 minutes, preferably no longer than 50 minutes. and more preferably no longer than 45 minutes The exposure to moisture generally results in the molded polyurea polymer taking up no more than 2 weight-percent water based on the weight of the molded polyurea polymer, pre! ei ably no more than 1 5 weight-percent water, and more preferably no more than 1 0 weight-percent watei Generally the molded polyurea polymer can take up between 1 0 and 1 5 weight-percent watei based on the weight of the molded polyurea polymer Typically a fatty-acid ester is added to a polyurea-polymer formulation in an amount of at least 0 5 weight percent, preferably at least 1 5 weight percent, and more preferably at least 2 weight percent. But a fatty- acid ester should not be added in such a large amount that the formulation becomes prohibitively expensive, becomes substantially difficult to process, or cannot be used lor its intended purpose A fatty-acid ester is generally added in an amount no greater than 5 0 weight percent, preferably no greater than 4 weight percent, and more preferably no greatei than 3 weight percent The weight percent of fatty-acid ester is based on the weight of the reaction mixture that contains the isocyanate-reactive material, which is conventionally known as the B-side reactant The B-side reactant generally reacts with the polyisocyanate, which is conventionally known as the A-side reactant, in the chemistry used to make a polyurea polymei The polyurea-polymer formulation of the invention includes a polyisocyanate A polyisocyanate suitable for use with a formulation of the invention mcludes any polyisocyanate suitable for preparing a molded polyurea polymei A polyisocyanate can be advantageously selected from orgamc polyisocyanates. modified polyisocyanates. isocyanate-based prepolymers, and mixtures thereof These can include aliphatic and cycloaliphatic isocyanates, but multifunctional and particularly difunctional aromatic isocyanates are preferred Preferred are 2,4- and 2,6-toluenedιιsocyanate (TDI) and the corresponding isomeric mixtures, 4,4'-, 2,4'-, and 2.2'-dιιphenylmethanednsocyanate (MDI), mixtures of 4 " , 4 ' -, 2,4 " -. and 2,2'-MDI and polyphenyl polymethylene polyisocyanates (PMDI), and mixtures of PMDI and TDI Also useful for preparing the polyureas of the invention are aliphatic and cycloaliphatic isocyanate compounds such as 1,6-hexamethylenednsocyanate, l-ιsocyanato-3,5,5-tπmethyl-l-3- lsocyanatomethyl cyclohexane, 2,4- and 2,6-hexanhydrotoluenednsocyanate The corresponding isomeric mixtures 4,4 " -, 2,2'-, and 2,4 ' -dιcyclohexylmethanedιιsocyanate as well as the corresponding isomeric mixtures can also be used Isophorone dnsocyanate can also be used with the invention Also advantageously used for the polyisocyanate are the so-called modified multifunctional isocyanates, that is, products that are obtained through chemical reactions of the above polyisocyanates. Examples of such polyisocyanates include polyisocyanates contaimng at least one of esters, ureas, biurets, allophanates, carbodiirrudes, uretonimines, and urethane groups contaimng dusocyanates or polyisocyanates Polyisocyanates containing at least one of a carbodπmide group and a uretonimine group and having an isocyanate group (NCO) content of from 10 to 40 weight percent based on the total weight of isocyanate prepolymer, more preferably from 20 to 35 weight percent, can also be used These include, for example, polyisocyanates based on 4.4 " -, 2,4 " -. oi 2,2'-MDI, the corresponding isomeric mixtures, and mixtures thereof, 2,4-, 2,6-TDI, the corresponding isomeric mixtures, and mixtures thereof, and mixtures of MDI and PMDI, mixtures of TDI and PMDI, diphenylmethane dusocyanates. and mixtures thereof. Suitable and preferred are prepolymers having an NCO content of from 5 to 40 weight percent based on the total weight of isocyanate prepolymer and more preferably from 15 to 30 weight percent These prepolymers are prepared by reaction of the polyisocyanates with materials including lower molecular weight diols or triols, but also they can be prepared with multivalent active hydrogen compounds such as di- and tπ-amines and di- and tπ-thiols Individual examples are aromatic polyisocyanates contaimng urethane groups, preferably having an NCO content of from 5 to 40 weight percent, more preferably 10 to 35 weight percent, obtained by reaction of polyisocyanates with, for example, lower molecular weight diols, tools, oxyalkylene glycols, dioxyalkylene glycols, or polyoxyalkylene glycols having molecular weights up to 800 These polyols can be employed individually or in mixtures as di- and/or polyoxyalkylene glycols For example, diethylene glycols, dipropylene glycols, polyoxyethylene glycols, polyoxypropylene glycols, and polyoxypropylene- polyoxyethylene glycols can be used Even more preferred for use in the invention are (I) polyisocyanates having an NCO content of from 8 to 40 weight percent based on the total weight of isocyanate prepolymer and contaimng carbodumide groups and/or urethane groups, from 4,4 -MDI or a mixture of 4,4"- and 2,4 -MDI, (11) prepolymers contaimng NCO groups, having an NCO content of from 10 to 35 weight percent, based on the weight of the prepolymer, prepared by the reaction of polyoxyalkylene polyols, having a functionality of preferably from 2 to 4 and a molecular weight of from 800 to 15,000 with 4,4 ' - diphenylmethane dnsocyanate or with a mixture of 4,4 " - and 2,4' -MDI and mixtures of (I) and (n), and (in) 2,4- and 2,6-TDI and the corresponding isomeric mixtures A polyurea-polymer formulation of the invention also includes an isocyanate-reactive material such as a polyamine Any polyamine suitable for preparing a molded polyurea polymer can be used in a formulation of the invention A polyamine includes any amine compound having at least two isocyanate-reactive hydrogens per molecule Preferably all isocyanate-reactive hydrogens of the polyamine are amine- group hydrogens. Examples of such polyamines include alkylene polyamines represented by the formula NH 2 C 2 H 4 (NHC 2 H 4 )„X where X is -OH or -NH 2 and where n has the value of 0 to 5 When X is -NH 2 , such alkylene polyamines include ethylene diamine. diethylene tπamine, triethylene tetramine. tetraethylene pentamine, and pentaethylene hexamine. Aromatic amines can be used with the invention as well. Examples of aromatic polyamines include 2,4 and 2,6-toluenedιamιne, n-aminoethylpiperazine, m-phenylenediamine Particularly useful with the invention are diethyltoluenediamine and di-tert-butyl-toluenediamine A particularly useful group of amines are amines derived from polyoxypropylene diols and tπols Preferably these diamines have the formula H 2 NCH(CH 3 )CH 2 [OCH 2 CH(CH 3 )LNH 2 wherein x is an integer of from 2 to 40, and the tπamines have the formula CH 2 [OCH 2 CH(CH,) x NH 2 CH 2 [OCH 2 CH(CH,)] z NH 2 wherein x, y, and z represent integers in the range of from 1 to 15, and the sum of Λ, V, and : is from 3 to 45 The most preferred polyoxypropylene diamines have an average molecular weight of from 230 to 2000 The most preferred polyoxypropylene triannnes have an average molecular weight of from 190 to 5000 Also useful are diamines having the formula H 2 NCH(CH,)CH 2 [OCH(CH,)CH 2 ] t [OCH 2 CH 2 ] y [OCH 2 CH(CH 3 ),NH 2 wherein x + z equals 2 to 10 and y is an integer from 1 to 50 Care should be exercised in choosing the polyisocyanate and polyamine for use in a formulation of the invention Primary amines and aromatic polyisocyanates are particularly mutually reactive Forming polymers from such components can be very difficult because the reaction can be rapid and very exothermic, thereby preventing the formation of a homogenous polymer Therefore, one should choose polyisocyanate and polyamine components that have a mutual reactivity suitable for preparing the desired polyurea polymer. One skilled in the art having read this specification would understand how to choose desirable polyisocyanates and polyamines Polyurea-polymer formulations of the invention can also include other isocyanate-reactive materials besides a polyamine or in combination with a polyamine For example, a polyurea-polymei formulation of the invention can also include polyether or polyester polyols These types of isocyanate-reactive materials are generally used to prepare polyurethane polymers Active hydrogen- containing compounds most commonly used in polyurethane production are those compounds having at least two hydroxyl groups. Those compounds are referred to herein as polyols. The resultant polymers can also have improved physical properties compared to otherwise similar conventional polymers. The terms '"polyurea polymer '* and "polyurea-polymer formulation " are intended to include both polyurea and polyurethane polymers as well as a combination of polyurea and polyurethane polymers and their corresponding formulations. Representative polyols suitable for use in the invention are generally known and are described in such publications as High Polymers, Vol. XVI, "Polyurethanes, Chemistry and Technology " by Saunders and Frisch, Interscience Publishers, New York, Vol. I, pp. 32-42, 444-54 (1962) and Vol. II. pp. 5-6, 198-199 (1964); Organic Polymer Chemistry by K.J. Saunders, Chapman and Hall, London, pp. 323-325 (1973); and Developments in Polyurethanes, Vol. I, J.M. Burst, ed., Applied Science Publishers, pp. 1-76 (1978). But any active hydrogen-containing compound can be used with this invention. Examples of such materials include those selected from the following classes of composition, alone or in mixture: (a) alkylene oxide adducts of polyhydroxyalkanes; (b) alkylene oxide adducts of nonreducing sugars and sugar derivatives; (c) alkylene oxide adducts of phosphorus and polyphosphorus acids; and (d) alkylene oxide adducts of polyphenols. Polyols of these types are referred to herein as "'base polyols. " Examples of alkylene oxide adducts of polyhydroxyalkanes useful according to the invention are adducts of ethylene glycol, propylene glycol, 1 ,3-dihydroxypropane, 1 ,4-dihydroxybutane, and 1,6- dihydroxhexane, glycerol, 1,2,4-trihydroxybutane, 1,2,6-trihydroxyhexane, 1 , 1 , 1 -trimethylolethanc, 1,1,1 -trimethylolpropane, pentaerythritol, polycaprolactone, xylitol, arabitol, sorbitol. and mannitol. Preferably an alkylene oxide adduct of polyhydroxyalkanes is an ethylene oxide adduct of trihydroxyalkanes. Other useful adducts include ethylene diamine, glycerin, ammonia, 1,2,3,4- tetrahydroxy butane, fructose, and sucrose. Also preferred are poly(oxypropylene) glycols, triols, tetrols, and hexols and any of these that are capped with ethylene oxide. These polyols also include poly(oxyproyleneoxyethylene) polyols. The oxyethylene content should preferably comprise less than 80 weight percent of the total based on the total weight of the polyol and more preferably less than 40 weight percent The ethylene oxide, when used, can be incorporated in any way along the polymer chain, for example, as internal blocks, terminal blocks, or randomly distributed blocks, or any combination thereof Polyisocyanate polyaddition active hydrogen-containing compounds (PIPA) can be used with the invention PIPA compounds are typically the reaction products of TDI and tπethanolamine A method for preparing PIPA compounds can be found in, for example, U.S Pat No 4.374,209 issued to Rowlands Another class of polyols that can be used with the invention is '"a copolymer polyol, ' which includes base polyols contaimng stably dispersed polymers such as acrylonitπle-styrenc copolymers Production of these copolymer polyols can be from reaction mixtures comprising a variety of othci materials, including, for example, catalyst such as azobisisobutyronitπle. copolymer-polyol stabilizers, and chain-transfer agents such as isopropanol In addition to the base polyols described above, other active hydrogen-containing materials are useful with the invention Low molecular-weight polyfunctional compounds such as glycols, glycerols, di- and tπ-amino compounds, and polyfunctional amino-alcohols can be included in the formulations of the invention and are particularly useful For example, ethylene glycol and/oi diethyltoluenediamine can be used as chain extenders When additional isocyanate-reactive materials such as a polyol is included in a polyurea- polymer formulation of the invention, it is included in the calculation of ratio of isocyanate groups to isocyanate-reactive groups A polyurea-polymer formulation of the invention can also include known additives and othei known formulation components to prepare molded polyurea polymers with desired properties Generally any additive known to those skilled in the art to be useful in preparing polyurea-polymci formulations can be included in a formulation of the invention so long as the additive is compatible with other components in the formulation For example, when a foamed polymer is desired, the polyurea polymers can be prepared from a formulation including one or more blowing agents such as watei, carbon dioxide, and air A polyurea-polymer formulation of the invention can also include a filler Any filler generally known to one of skill in the art as useful for polyurea polymers can be used Suitable tilleis include mica, clays, glass fibers, glass beads, glass rmcrospheres, and wollastonite A polyurea-polymer formulation can also include a reinforcing substrate Any reinforcing substrate generally known to one of skill in the art as useful lor polyui ea polymers can be used Foi example the polymers of the invention can be prepared with reinforcing mats Other known additives can be included in a polyurea-polymer formulation of the invention Examples of such additives include mold-release agents (e g , zmc stearate), surfactants (e g , silicone surfactant), ultraviolet-light stabilizers, molecular-weight extenders, pigments, catalysts (e g , dimethyl tin dilaurate), and fire retardants These materials are all well known in the art A polyurea-polymer formulation of the invention preferably includes a polyexpoxide A polyexpoxide suitable for use with the invention includes diglycidyl ethers of compounds contaimng an average of more than two, preferably not greater than 2 aromatic, cycloaliphatic, or aliphatic hydroxyl groups per molecule Suitable polyepoxides also include a diglycidyl ether of dihydric bisphenol Other examples are described in U S Patent No 5,525,681 A polyurea-polymer formulation can include up to 20 weight-percent polyepoxide based on the total weight of the formulation The isocyanate index of a polyurea polymer has been known to affect blister resistance ol a molded polyurea polymer The isocyanate index is the molar ratio of isocyanate groups to isocyanate- reactive groups Conventionally the isocyanate index of formulations for RIM polyurea polymers is m a range of from 0 80 to 1 20, preferably from 0 90 to 1 10. and more preferably from 0 95 to 1 05 Notably, while increasing the isocyanate index can improve blister resistance, the molded polymei generally becomes more brittle, which is undesirable for a variety of applications Bnttleness is a signif icant problem at an isocyanate index of 1.40 The isocyanate index of a polyurea-polymer formulation of the invention is desirably in a range of between 1.05 and 1.40, preferably in a range of between 1.20 and 1 40, and more preferably 1.20. The desirable isocyanate index may vary depending on other components added to a formulation of the invention For example, for a polyurea-polymer formulation that further includes a polyepoxide, the isocyanate index is desirably in a range of between 1 00 and 1 40, preferably in a range of between 1 05 and 1 10, and more preferably 1 05 Blister resistance of a molded polyurea polymer can generally be improved by increasing an isocyanate index by a relatively small amount such as 0 05, preferably 0 10, and more preferably 0 15 over a conventional molded polyurea polymer A molded polyurea polymer of the invention can be less brittle, as determined by Gardner Impact, than a conventional molded polyurea polymer having the same isocyanate index but being substantially free of a fatty-acid ester A polyurea-polymer formulation of the invention can be prepared by admixing at least one of a polyisocyanate, at least one of an isocyanate-reactive material, and at least one of a fatty-acid ester The fatty-acid ester is admixed in an amount effective for providing a molded polyurea polymer prepared from the formulation with blister resistance such that when the molded polyurea polymer is exposed to moisture and a temperature of at least 350°F (177°C), the molded polyurea polymer is substantially free of blisters Alternatively, the fatty-acid ester is admixed in an amount effective to improve the blister resistance of a molded polyurea polymer prepared from a polyurea-polymer formulation of the invention as compared to the blister resistance of a molded polyurea polymer prepared from a polyurea-polymer formulation that is substantially free of a fatty-acid ester In a preferred embodiment of the invention, a method for preparing a polyurea-polymer formulation includes mixing a polyisocyanate, an isocyanate-reactive material, and a fatty-acid estei to have an isocyanate index in a range of between 1 05 and 1 40 When the formulation further comprises a polyepoxide, the isocyanate index is in a range of between 1 00 and 1.40 When incorporating a polyexpoxide into a formulation of the invention, a polyisocyanate, a polyepoxide, an isocyanate-reactive material, and a fatty-acid ester can be admixed while heating to a temperature of 302°F (150°C) Alternatively, the components are admixed at a temperature of less than 266°F (130°C) and then postcured at a temperature greater than 302°F (150°C) Preferably the polyepoxide and polyisocyanate are mixed together first and then the isocyanate-reactive material and the fatty-acid ester are admixed The components in a formulation of the invention can be mixed in any way known to those skilled in preparing polyurea-polymer formulations For example, the components can be mixed and poured into an open mold, a process known as casting One useful embodiment of the invention is a cellular polyurea-polymer foam prepared by mixing a polyisocyanate, a fatty-acid ester, and a polyamine in the presence of a blowing agent and injecting the forming polymer into a mold to form a molded foam Preferably a polyurea-polymer formulation is prepared and molded by RIM This process is well known in the art of preparing polyurea-polymer formulations Generally a RIM process relates to a process in which two or more highly reactive streams are brought together under high pressure in a small mixing chamber The material mixes and flows immediately into a warm mold where the chemical reaction is completed sufficiently to allow removal of the molded polymer from the mold The streams are, in the case of the invention, (1) a polyisocyanate stream designated the "A " stream and (2) one or more streams containing an isocyanate-reactive material and additives designated collectively as the "B" component or stream RIM can be performed in a closed-mold process In closed-mold RIM, the mold is composed such that the forming polymer, upon entering the mold, pushes the air from the mold resulting in a polymer substantially free of trapped air RIM can also be performed in an open mold-process The formed polyurea-polymer part is removed from the mold The part may also be postcured by heating the molded part at an elevated temperature such as 375°F (190°C) for a period of time such as 30 minutes Molded polyurea-polymer formulations of the invention can display better heat stability, as evidenced by resistance to blistering, than conventional molded polyurea-polymer formulations. For example, a conventional RIM polyurea polymer, which has been exposed to moisture, can severely blister upon exposure to temperatures of 365°F (185°C). But a molded polyurea polymer of the invention, exposed to similar amounts of moisture, can endure temperatures of at least 350°F (177°C), preferably at least 375°F (190°C), and more preferably at least 390°F (199°C), and generally greater than (400 °F)(204°C) without blistering. The molded polyurea polymers of the invention can also display superior physical properties compared to conventional molded polyurea polymers. For example, a polyurea-polymer formulation of the invention that is prepared and molded by RIM can have lower heat sag, higher modulus, less brittleness as measured by Gardner Impact, higher heat-distortion temperatures, and less blistering than conventional molded polyurea polymers. This invention will be further described by the following Example. This Example is not meant to limit this invention but to further illustrate one embodiment of the invention. EXAMPLES Example 1 and Comparative Example 2 A polyurea-polymer formulation according to the invention was prepared by admixing a polyol blend with an equivalent weight of 280 ("B" side) and an MDI prepolymer (XUS 17054; The Dow Chemical Company; Freeport, Texas) having 19% mica filler (Himod 270 with SMAL surface treatment; Olgay Norton, North Carolina) and having an equivalent weight of 254 ("A" Side). The formulation had an isocyanate index of 1.05. The polyol blend included an aromatic dia ine (diethyltoluenediamine) (available from Albemarle; South Carolina); a polyether polyol (a 5,000 molecular-weight ethylene-oxide capped propylene polyether triol) (XUS 14003.01; available from The Dow Chemical Company; Freeport, Texas); a polyetiierpolyamine (a polyamine having an approximate equivalent weight of 1 ,000 and having difunctionality) (TR2020; available from Huntsman Corporation; Austin, Texas), an internal- mold-release agent (zinc stearate) (available among others from Ferro Corp., Cleveland, OH, or Witco Corp., Chicago, IL); a fatty-acid ester (jojoba oil) (available among others from Desert King Corp., Chula Vista, CA, or Desert Whale Joboba Co., Inc., Tucson, AZ); a catalyst (dimethyl tin dilaurate) (UL28; available from Air Products; Allentown, Pennsylvania); and a silicone surfactant (B8418; available from Goldschmitdt Chemical Corporation; Hopewell, Virginia). A comparative formulation was prepared like the formulation of the invention except that no jojoba oil was included in the comparative formulation. Table 1 lists the approximate composition of the polyol blends ("B" sides) used in Example 1 and Comparative Example 2. The amounts are given in weight percent based on the weight of the polyol blend. TABLE 1 : Polyol-Blend Formulation A plaque (0.6 meters by 0.9 meters) was made under normal processing conditions using reaction injection molding. The plaque was postcured at 370 +1-5 degrees F (188°C) for 60 minutes and then cut into squares (10 cm by 10 cm). Each square was placed into a dry box until the experiment was conducted. For the experiment, each square was immersed in water for 48 hours at room temperature. The squares were removed from the water, dried of excess water by blotting with a paper towel, and then immediately placed in an oven at a temperature of 375°F (190°C), 390°F (199°C), or 400°F (204°C). After 60 minutes, the squares were removed from the oven, cooled to room temperature, and examined for blistering. Table 2 shows the results from this testing for Example 1 and Comparative Example 2. Each square was visually examined to determine whether, and to what extent, blisters were present. A scale of 0-5 was used to subjectively determine the extent of blistering, with 0 being the best in that there were no blisters present on the square after removing it from the oven. TABLE 2

Claims: CLAIMS: 1 A method for preparing a polyurea polymer formulation comprising admixing a polyisocyanate, an isocyanate-reactive material, and a fatty-acid ester to form a mixture, said fatty-acid ester being present in an amount effective for providing blister resistance to a molded polyurea polymer prepared from said mixture such that when said molded polyurea polymer is exposed to moisture and a temperature of at least 350°F (177°C), said molded polyurea polymer is substantially free of blisters 2 The method of Claim 1 , wherein said isocyanate-reactive material is at least one of a polyamine and a polyol 3 The method of Claim 1 , wherein a polyepoxide is admixed with said mixture 4 The method of Claim 1 , wherein said mixture has an isocyanate index of between 1 05 and 1.40. 5 The method of Claim 1, wherein said mixture has an isocyanate index of 1 20 6 The method of Claim 3, wherein said mixture has an isocyanate index of 1 05 7 The method of Claim 1 , wherein the fatty-acid ester is jojoba oil 8 The method of Claim 1 , wherein said fatty-acid ester is present in an amount of at least 0 5 weight percent based on the weight of said mixture excluding the weight of said polyisocyanate 9 The method of Claim 1 , wherein said fatty-acid ester is present in an amount of at least 1 5 weight percent based on the weight of said mixture excluding the weight of said polyisocyanate 10 The method of Claim 1, wherein said molded polyurea polymer is exposed to a temperature of at least 375°F (190°C) 11 The method of Claim 1 , wherein said molded polyurea polymer is exposed to a temperature of at least 390°F (199°C) 12 The method of Claim 1 , wherein said molded polyurea polymer is exposed to a temperature of at least 400°F (204°C). 13. The method of Claim 1 , wherein when said molded polyurea polymer is exposed to moisture, said molded polyurea polymer takes up no more than 2 weight-percent water based on the weight of said molded polyurea polymer. 14. The method of Claim 1 , wherein said molded polyurea polymer is exposed to said temperature for at least 20 minutes and no longer than 60 minutes. 15. The method of Claim 1 , wherein said molded polyurea polymer is molded by reaction injection molding. 16. The method of Claim 1 , wherein said molded polyurea polymer is suitable for use in an e-coat process. 17. A method of improving a molded polyurea polymer's blister resistance, said method comprising: (A) adding an effective amount of a fatty-acid ester to a polyurea-polymer formulation comprising a polyisocyanate and an isocyanate-reactive material to prepare a mixture; and (B) molding said mixture to prepare a molded polyurea polymer, wherein said molded mixture develops substantially fewer blisters, as compared to a molded mixture that is substantially free of a fatty-acid ester, when exposed to moisture and a temperature of at least 350°F (177°C), said molded polyurea polymer being exposed to said temperature for at least 20 minutes and no longer than 60 minutes. 18. The method of Claim 17, wherein said mixture has an isocyanate index between 1.05 and 1.40. 19. The method of Claim 17, wherein said mixture further comprises a polyepoxide. 20. The method of Claim 17, wherein said fatty-acid ester is jojoba oil. 21. The method of Claim 17, wherein said isocyanate-reactive material is at least one of a polyamine and a polyol. 22. The method of Claim 17, wherein said fatty-acid ester is present in an amount of at least 0 5 weight percent based on the weight of said mixture excluding the weight of said polyisocyanate 23 The method of Claim 17, wherein said molded polyurea polymer is exposed to a temperature of at least 375 °F (190°C) 24 The method of Claim 17, wherein when said molded polyurea polymer is exposed to moisture, said molded polyurea polymer takes up no more than 2 weight-percent water based on the weight of said molded polyurea polymer 25 The method of Claim 17, wherein said mixture is molded by reaction injection molding 26 A polyurea-polymer formulation prepared by a method comprising admixing a polyisocyanate, an isocyanate-reactive material, and a fatty-acid ester to form a mixture, said fatty-acid ester being present in an amount effective for providing blister resistance to a molded polyurea polymer prepared from said mixture such that when said molded polyurea polymer is exposed to moisture and a temperature of at least 350°F (177°C), said molded polyurea polymer is substantially free of blisters 27 A molded poyurea polymer prepared by a method comprising (A) admixing a polyisocyanate, an isocyanate-reactive material, and a fatty-acid ester to form a mixture, and (B) molding said mixture using reaction injection molding to form a molded polyurea polymer, wherein said mixture contains said fatty-acid ester in an amount effective for providing blister resistance to said molded polyurea polymer such that when said molded polyurea polymer is exposed to moisture and a temperature of at least 350°F (177°C), said molded polyurea polymer is substantially free of blisters 28 A polyurea-polymer formulation suitable for preparing a molded polyurea polymer, said formulation comprising a polyisocyanate, an isocyanate-reactive material, and a fatty-acid ester, said fatty-acid ester being present in an amount effective for providing blister resistance to a molded polyurea polymer prepared from said formulation such that when said molded polyurea polymer is exposed to moisture and a temperature of at least 350°F (177°C), said molded polyurea polymer is substantially free of blisters. 29. The formulation of Claim 28, wherein said isocyanate-reactive material is at least one of a polyamine and a polyol. 30. The formulation of Claim 28, wherein said fatty-acid ester is jojoba oil. 31. The formulation of Claim 28 further comprising at least one additive, said additive being at least one of a chain extender, a catalyst, a surfactant, and an internal-mold-release agent. 32. The formulation of Claim 28 further comprising a polyepoxide.

Inventors: ARNOLD KENNETH B, JAMES ALLAN, ARNOLD, KENNETH, B., JAMES, ALLAN
Applicants: DOW CHEMICAL CO, THE DOW CHEMICAL COMPANY
Application year: 2000
Main classification: C08K5
IPC codes: C08G18, C08K5, C08L63, C08L75