Croslinkable modified fluorinated polymers

Abstract: Melt-processable thermally crosslinkable compositions comprising: I) termoprocessable copolymers of ethylene (E) with tetrafluoroethylene (TFE) and/or chlorotrifluoroethylene (CTFE) modified with acrylic monomers of formula: CH 2 =CH-CO-O-R 2 R 2 is an hydrogenated radical from 1 to 20 carbon atoms, C 1 -C 20 , alkyl, linear and/or branched radical, or cycloalkyl, or R 2 is H. The radical R 2 can optionally contain: heteroatoms preferably Cl, O, N; one or more functional groups preferably selected from OH, COOH, epoxide, ester and ether; and double bonds; the above n is an integer in the range 0-10. II) one or more cross-linking agents.

Description: The present invention relates to processes for the preparation of crosslinked fluorinated copolymers with acrylic monomers. In particular the invention relates to processes for the preparation of melt-processable curable compositions, comprising thermoprocessable copolymers of ethylene (E) with tetrafluoroethylene (TFE) and/or chlorotrifluoroethylene (CTFE) and acrylic monomers, which subjected to thermal treatment improve their mechanical properties at high temperatures and chemical resistance, increasing their rating. Said crosslinkable compositions adhere to hydrogenated polymers. The improvement of the mechanical properties at high temperatures is shown by the increase of the stress at break without jeopardizing the elongation at break. The use of hydrogenated polymers in the car industry for preparing fuel hoses and fuel lines is known in the prior art. Examples of hydrogenated polymers are polyamides, polyvinylchloride (PVC), nitrile rubbers (NBR). The drawbacks of the manufactured articles obtained therefrom are the low chemical resistance and high permeability to gasolines and oils, in particular SF® oils which show high aggressivity towards the vinylidenfluoride (VDF)-based elastomers, presently used in the car industry. A high permeability to these fluids, in particular gasolines, implies a high emission of dangerous substances to the environment. The laws of most countries are more and more restrictive on these emissions due to their environmental impact. Therefore, materials having a lower permeability, improved chemical resistance and at the same time having improved mechanical properties at high temperatures, in particular stress at break, are required. Fluorinated polymers having an improved chemical resistance to gasolines and to particularly aggressive oils used in the car industry in comparison with hydrogenated polymers, are known. Besides, said fluorinated polymers have a combination of mechanical properties which make them suitable for the above mentioned uses. The drawback of these fluorinated polymers is the high cost which limits their use. In order to make economically possible the use of fluorinated polymers it has been suggested the use of composites of hydrogenated polymers with fluorinated polymers. However the adhesion between fluorinated polymers and hydrogenated polymers is very poor. The research is directed to find solutions such as to make possible these composites. In particular for the thermoprocessable fluorinated of ethylene (E) copolymers with tetrafluoroethylene (TFE) and/or chlorotrifluoroethylene (CTFE), for example Halar® commercialized by Ausimont USA Inc., the solutions suggested for their coupling with hydrogenated polymers, use adhesives of various types. In this case the technologies for obtaining multilaminates from the industrial point of view are more complex for the introduction of an additional adhesive layer (tie-layer technology). The need was felt to make multi-layer manufactured articles, made of hydrogenated and fluorinated polymers having improved mechanical properties, impermeability and chemical resistance to liquid fuels without using the tie-layer technology. Among the most known applications of multi-layer manufactured articles, fuel hoses (hydrogenated rubbers/fluorinated polymers) and fuel lines (polyamides/fluorinated polymers) can be mentioned. JP-A-5008353 discloses resin tube vehicle fuel dispense comprising an inner layer of F-containing resin and an outer layer of polyamide resin, wherein the intermediate layer is crosslinked by irradiating radiation beams. JP-A-2121206 concerns coating material comprising a mixture of (A): ethylene-fluoroolefin (e.g.TFE) copolymer and (B): a polymer made by grafting a tetrafluoroethylene-propylene copolymer with acrylic ester. US 4039631 concerns compositions of copolymers of Ethylene with halogenated comonomer (e.g. TFE, CTFE and mixture thereof) radiation-curable. FR 2494702 concerns copolymers of polytetrafluoroethylene grafted with a monomer (e.g. acrylate). EP-A-866079 deals with thermoprocessable fluorinated copolymers comprising acrylic units in the chain, suitable for flexible cables which are free of whitening effects when they are bended. The Applicant has surprisingly and unexpectedly found a process for the preparation of melt-processable curable compositions by thermally treating said compositions consisting of thermoprocessable copolymers of ethylene (E) with tetrafluoroethylene (TFE) or chlorotrifluoroethylene (CTFE) and acrylic monomers or thermoprocessable copolymers of ethylene (E) with chlorotrifluoroethylene (CTFE), tetraflouroethylene and acrylic monomers and a cross-linking agent, which subjected to thermal treatment are capable to crosslink, improving their mechanical and chemical resistance properties, showing adhesive properties with hydrogenated polymers. An object of the present invention are therefore crosslinking processes for producing melt-processable compositions by thermally treating said compositions consisting of: I) thermoprocessable copolymers of ethylene (E) with chlorotrifluoroethylene (CTFE) or tetrafluoroethylene (TFE) and acrylic monomers of formula: CH 2 =CH-CO-O-R 2 or thermoprocessable copolymers of ethylene (E) with chlorotrifluoroethylene (CTFE), tetrafluoroethylene (TFE), and acrylic monomers of formula : CH 2 = CH - CO-O-R 2 wherein R 2 is an hydrogenated radical from 1 to 20 carbon atoms, C 1 -C 20 , alklyl, linear and/or branched radical, or cycloalkyl, or R 2 is H. The radical R 2 can optionally contain: heteroatoms preferably Cl, O, N; one or more functional groups preferably selected from OH, COOH, epoxide, ester and ether. II) one or more cross-linking agents selected from triallylisocyanurate (TAIC), triallylcyanurate (TAC), diallylisophthalate, diallylterephthalate, phenyl indene esters, triallylester of the aryl polycarboxylic acid, bis-olefins such as 1,6 divinylperfluorohexane, hexamethylendiaminecarbamate (DIAK 1), N,N'-dicinnamylidene-1,6-hexanediamine (DIAK 3), maleimide derivatives such as m-phenylenbismaleimide, C 4 -C 20 aliphatic diamines, polyhydroxyl aromatic compounds such as bisphenols A, AF and S. The thermoprocessable copolymers of the present invention composition comprise from at least 10 %, preferably from at least 35, by moles of ethylene, from 30 to 90%, preferably from 45 to 65%, by moles of a fluorinated monomer selected from tetrafluoroethylene, chlorotrifluoroethylene, or mixtures thereof, from 0.1 to 30%, preferably from 1 to 15% by moles of the comonomer (a). As component I), thermoprocessable copolymers wherein the fluorinated monomer is chlorotrifluoroethylene are preferred. n-Butylacrylate (n-BuA) is the preferred acrylic monomer. The cross-linking agents can be active by radical way, such as for example triallylisocyanurate (TAIC), triallylcyanurate (TAC), diallylisophthalate (USP 4,039,631), diallylterephthalate (USP 4,039,631), esters of phenyl indan (USP 3,763,222), triallylester of the aryl polycarboxylic acid (USP 3,840,619), bis-olefins such as for example 1,6 divinylperfluorohexane (see USP 5,612,419) and others (see USP 4,121,001); or active by ionic way such as for example hexamethylendiaminecarbamate (DIAK 1), N,N'-dicinnamylidene-1,6-hexanediamine (DIAK 3), maleimide derivatives such as for example m-phenylenbismaleimide, C 4 -C 20 aliphatic diamines, polyhydroxyl aromatic compounds for example bisphenols A, AF and S. As crosslinking agents active by radical way triallylisocyanurate is preferred. As crosslinking agents active by ionic route, the protected both aliphatic and aromatic diamines are preferred. The cross-linking agent amounts ranges from 0.1 to 20.0% by weight, preferably from 0.5 to 10.0%, more preferably from 1.0 to 5.0%. The composition for the processes of the present invention is obtainable by closely mixing the ethylene thermoprocessable copolymers with tetrafluoroethylene (TFE) and/or chlorotrifluoroethylene (CTFE) modified with acrylic monomers, with one or more crosslinking agents. Alternatively, the composition of the present invention can be obtained uniformly distributing one or more crosslinking agents on a manufactured article of thermoprocessable copolymers of ethylene with tetrafluoroethylene (TFE) and/or chlorotrifluoroethylene (CTFE) modified with acrylic monomers, or by contacting the surfaces of said manufactured article with a hydrogenated polymer containing one or more crosslinking agents. A further object of the present invention is a crosslinking process subjecting the melt-processable crosslinkable compositions of the present invention, to a thermal treatment. Such a process is carried out at a temperature generally higher than 150°C. When the crosslinking agents are activated by ionic way, the process is carried out at temperature preferably lower than 200°C. When the crosslinking agents are activated by radical way, the process is carried out at a temperature preferably higher than 250°C. For a given composition of the invention, the time of the thermal treatment decreases as the chosen temperature for the crosslinking increases. A further object of the present invention are the manufactured articles obtained by crosslinking the melt-processable compositions of the present invention. A further object of the invention are multi-layer manufactured articles of hydrogenated polymers and melt-processable crosslinkable compositions of the invention, thermally treated and untreated. The preferred manufactured articles are: fuel lines, obtainable for example by coextrusion of polyamide and the compositions of the invention; fuel hoses, obtainable for example by extrusion of hydrogenated rubber on a tube made of the compositions of the invention. As hydrogenated polymers we can mention thermoplastics and elastomers. As thermoplastic polymers: for example cellulose polymers, polyamides such as NYLON 6, NYLON 66, NYLON 11, NYLON 12, polyamide copolymers, polycarbonates, polyesters, such as polyethylenterephthalate, polyester copolymers, polyolefins such as high and low density polyethylene, olefine copolymers, polyimides, polystyrene, polyurethanes, polyvinylchloride (PVC), polysulphones, ethylene/vinylacetate copolymers, polyacrylbutadienestyrene (ABS). The preferred thermoplastic hydrogenated polymers are polyesters, polyolefins, polyamides. As hydrogenated elastomers we can mention acrylic rubbers, nitrile rubbers (NBR), ethylene-propylene rubbers (EPM), ethylene-propylene-diene rubbers (EPDM), NVC rubbers (nitrile NBR rubbers mixed with PVC), epichlorohydrin rubbers (CO and ECO). As hydrogenated elastomers, epichlorohydrin and nitrile rubbers (NBR) are preferred. Some examples of the present invention are hereinafter reported, the purpose of which is merely illustrative but not limitative of the scope of the invention itself. EXAMPLE 1 1.1 - Preparation of the "Polymer A" (E/CTFE/n-BuA 40/55/5 moles %) In an enamelled autoclave equipped with baffles and stirrer working at 450 rpm in Hastelloy C, 5.3 l of demineralized water, 1.7 l of methyl alcohol, 20 ml of methylcyclopentane, 10 g of n-butylacrylate and 2 kg of chlorotrifluoroethylene were introduced. The autoclave was then heated to the reaction temperature of 15°C and ethylene was fed up to a pressure of 8.2 absolute bar. In the autoclave the radical initiator was then continuously fed during the polymerization under the form of a trichloroacetylperoxide (TCAP) solution in isooctane, maintained at -17°C, having a titre equal to 0.1 g TCAP/ml. Furthermore, 10 g of n-butylacrylate were fed at consumption of 20, 40, 60, 80, 100, 120, 140, 160 and 180 g of ethylene. The pressure was maintained constant during the polymerization by continuously feeding ethylene to the reactor up to a consumption of 200 g; in total 399 ml of initiator solution were introduced. The polymerization lasted 555 minutes. The product discharged from the autoclave was dried at 120°C for about 16 hours. The amount of the obtained dry product was 1200 g. The obtained product is defined "Polymer A". The mechanical properties at 120°C, obtained according to the ASTM D1708 method by using compression molded specimens of the polymer A, are reported in Table 1. 1.2 - Preparation of the "Polymer A' ": Polymer A + TAIC 5% by weight The polymer A was additivated with TAIC at 5% by weight and optional components such as MARK-260® in an amount of 0.45% by weight and Aclyn-316® in an amount of 0.15% by weight, both mainly used as thermal stabilizers. The obtained polymer, defined "Polymer A'", is pelletized at a maximum temperature of 240°C, in a single screw Brabender extruder of Hastelloy C-276 having a 18 mm diameter and a length equivalent to 25 times the diameter. 1.3 - "Thermal crosslinking" The Polymer A' was compression molded at 240°C for 8 minutes at 40 bar obtaining specimens having a 0.3 mm thickness. One specimen is thermally treated at 275°C for 18 minutes and another one under the same conditions for 25 minutes. The mechanical properties at 120°C, obtained according to the ASTM D1708 method, of the above mentioned specimens, are reported in Table 1. 1.4 - Permeability to "Fuel C" (isooctane-toluene 50/50) at 50°C The permeability at 50°C is measured in grams of solvent (Fuel C) per surface area of the specimen in function of time. The permeability ratios between the specimens of polymer A and of the polymer A' thermally treated at 275°C for 25 minutes in function of time are: at 3 hours 1.85; at 6 hours 1.45; at 24 hours 1.47; at 48 hours 1.48. These ratios show how the polymer A' according to the present invention permeates at least 50% less than polymer A. EXAMPLE 2 (comparative) 2.1 - Preparation of the "Polymer B" (E/CTFE 49/51 moles %) In an enamelled autoclave equipped with baffle and stirrer working at 450 rpm in Hastelloy C, 5.3 l of demineralized water, 1.7 l of methyl alcohol, 52 ml of methylcyclopentane and 2 kg of chlorotrifluoroethylene were introduced. The autoclave was then heated to the reaction temperature of 15°C and ethylene was introduced up to a pressure of 12.6 absolute bar. In the autoclave the radical initiator was then continuously fed during the polymerization under the form of a trichloroacetylperoxide (TCAP) solution in isooctane, maintained at -17°C, having a titre equal to 0.12 g TCAP/ml. The pressure was maintained constant during the polymerization by continuously feeding ethylene into the reactor up to a consumption of 200 g; in total 200 ml of initiator solution were introduced. The product discharged from the autoclave was dried at 120°C for about 16 hours. The amount of the obtained dry product was 1507 g. The obtained product is defined "Polymer B". The mechanical properties at 120°C obtained according to the ASTM D1708 method by using compression molded specimens of the polymer B are reported in Table 2. 2.2 - Preparation of the "Polymer B' ": "Polymer B" + TAIC 5% by weight The polymer B was additivated with TAIC at 5% by weight and optional components such as MARK-260® in an amount of 0.45% by weight and Aclyn-316® in an amount of 0.15% by weight both mainly used as thermal stabilizers. The obtained polymer, defined "Polymer B'", is pelletized at a maximum temperature of 270°C in a single screw Brabender extruder of Hastelloy C-276 having a 18 mm diameter and a length equivalent to 25 times the diameter. 2.3 - "Thermal crosslinking" The Polymer B' was compression molded at 260°C for 8 minutes at 40 bar obtaining specimens having a 0.3 mm thickness. One specimen is thermally treated at 275°C for 18 minutes and another one under the same conditions for 25 minutes. The mechanical properties at 120°C, obtained according to the ASTM D1708 method of the above mentioned specimen, are reported in Table 1. From Table 1 it is observed a substantial improvement of the stress at break at high temperature of the thermally treated composition object of the present invention, based on the polymer A, even maintaining an elongation at break higher than 100%, in comparison with the untreated polymer A. From Table 2 no improvement is observed in the stress at break at high temperture of the thermally treated composition based on polymer B, in comparison to the untreated polymer B. It is therefore evident from the comparison between the two Tables that the presence of the formula (a) comonomer in the thermoplastic fluorinated copolymer of the composition object of the present invention is essential. EXAMPLE 3 3.1 - Formulation of the epichlorohydrin rubber, "Polymer C" 400 g of epichlorohydrin are loaded in a two-rolls open mixer (=150 mm, L=300 mm) and formulated as follows: Rubber: Hydrin ® C 50 phr. Hydrin ® T 50 phr. Span ® 60 3 phr. Carbon Black: SRF 20 phr. FEF 550N 30 phr. Ultrasil VN 3 (precipitated silica) 10 phr. NBC (nickel dibutyldithiocarbamate) 1 phr. Thiokol TP 95 (di(butoxy-ethoxy-ethyl)adipate) 8 phr. Maglite Y (MgO having low activity) 15 phr. MB/MB1 (mercaptobenzoimidazol) 1 phr. CBS (N-cyclohexylbenzothiazolsulphenamide) 1 phr. DIAK 1 2 phr. DC 40 (dicumylperoxide) 3 phr. Diphenylguanidine 5 phr. Bisphenol in powder 2.1 phr. Accelerant (diphenyl-benzyl-N,N-diethyl-aminophosphonium chloride) 0.7 phr. Subsequently they are processed in the mixer according to the ASTM D-3182 method. The obtained product is defined "Polymer C". 3.2 - Polymer A/polymer C bi-layer preparation Polymer C is distributed on the exposed surface of a sheet of polymer A placed in a mold having a rectangular cavity, and kept under pressure for 10 minutes at 170°C. The peeling force between the two layers of polymer A and polymer C was measured with a dynamometer. Such force is of 0.9 N/mm. This is an example wherein the composition according to the present invention is formed in the contact zone between the surfaces of polymer A (component I of the invention composition) and of polymer C (containing the components II of the invention composition). EXAMPLE 4 Polymer A'/polymer C bi-layer preparation Example 3 was repeated by replacing the polymer A with polymer A'. The peeling force is 1.2 N/mm. EXAMPLE 5 (comparative) Polymer B/polymer C bi-layer preparation Example 3 was repeated by replacing the polymer A with polymer B. There is no adhesion. In the contact zone between the two polymer surfaces the invention composition is not formed. EXAMPLE 6 Polyamide 12 hereinafter defined "Polymer D" was used. 6.1 - Preparation of the "Polymer D'": Polymer D + TAIC 5% by weight The polymer D was additivated with TAIC at 5% by weight and pelletized in a single screw Brabender extruder of Hastelloy C-276 having a diameter of 18 mm and a length equivalent to 25 times the diameter. The obtained polymer is defined "Polymer D'". 6.2 - Polymer A/polymer D' bi-layer preparation In a mold having a rectangular cavity a sheet of polymer A and a sheet of polymer D' are placed and then the whole is maintained under pressure for 9 minutes at 260°C. In this case the peeling force between the two layers of polymer A and polymer D' is about 1 N/mm. EXAMPLE 7 Example 6 was repeated by replacing the polymer A with polymer A' and polymer D' with polymer D. The peeling force is analogous to the previous Example. EXAMPLE 8 (comparative) Example 6 was repeated by replacing the polymer D' with polymer D. There is no adhesion. Mechanical properties at 120°C Polymer A Polymer A' (treated for 18') Polymer A' (treated for 25') Elastic modulus (MPa) 7 9.8 6.7 Yield Stress (MPa) 1.1 1.2 1.2 Elongation at break (%) 724 309 199 Stress at break (MPa) 1.7 3.8 3.0 % variation of stress at break - 123.5 76.5 % variation of elongation at break - - 57.3 - 72.5 Mechanical properties at 120 °C Polymer B Polymer B' (treated for 18') Polymer B' (treated for 25') Elastic modulus (MPa) 140 175 145 Yield Stress (MPa) 5.9 5.6 5.3 Elongation at break (%) 799 550 600 Stress at break (MPa) 9.8 6.8 10.2 % variation of stress at break - - 30.6 4.1 % variation of elongation at break - - 31.2 - 24,9

Claims: A crosslinking process for producing melt-processable compositions by thermally treating said compositions which consist of: (I) thermoprocessable copolymers of ethylene (E) with chlorotrifluoroethylene (CTFE) or tetrafluoroethylene (TFE), and acrylic monomers of formula: CH 2 =CH-CO-O-R 2 or thermoprocessable copolymers of ethylene (E) with chlorotrifluoroethylene (CTFE), tetrafluoroethylene (TFE), and acrylic monomers of formula: CH 2 =CH-CO-O-R 2 wherein R 2 is an hydrogenated radical from 1 to 20 carbon atoms C 1 -C 20 , alklyl, linear and/or branched radical, or cycloalkyl, or R 2 is H; the radical R 2 can optionally contain heteroatoms, preferably Cl, O or N, and one or more functional groups preferably selected from OH, COOH, epoxide, ester and ether, and (II) one or more cross-linking agents selected from: triallylisocyanurate (TAIC), triallylcyanurate (TAC), diallylisophthalate, diallylterephthalate, phenyl indene esters, triallylester of the aryl polycarboxylic acid, bis-olefins such as 1,6 divinylperfluorohexane, hexamethylendiaminecarbamate (DIAK 1), N,N'-dicinnamylidene-1,6-hexanediamine (DIAK 3), maleimide derivatives such as m-phenylenbismaleimide, C 4 -C 20 aliphatic diamines, polyhydroxyl aromatic compounds such as bisphenols A, AF and S. A process according to claim 1 wherein the thermoprocessable copolymers are constituted from at least 10, preferably from at least 35, by moles of ethylene, from at least 30, preferably from at least 45, by moles of a fluorinated monomer selected from tetrafluoroethylene, chlorotrifluoroethylene, or mixtures thereof, from 0.1 to 30%, preferably from 1 to 15% by moles of the comonomer (a), provided that the total percent of the monomers is 100% by moles. A process according to claim 2 characterized in that the components I) are thermoprocessable copolymers wherein the fluorinated monomer is chlorotrifluoroethylene. A process according to claims 1-3 characterized in that the acrylic monomers of formula (a) are n-butyl-acrylate. A process according to claim 1 wherein among the crosslinking agents triallylisocyanurate, aliphatic and aromatic diamines are preferred. A process according to claims 1-5 characterized in that the crosslinking agent amounts are in the range 0.1-20.0% by weight, preferably 0.5-10.0% by weight, more preferably 1.0-5.0% by weight of the compositions. A process according to claims 1-8 wherein said compositions are obtained by closely mixing said thermoprocessable copolymers (I) with one or more crosslinking agents or uniformly distributing one or more crosslinking agents on a manufactured article of the thermoprocessable copolymers (I) or by contacting the surfaces of said manufactured article with an hydrogenated polymer containing one or more crosslinking agents. A process according to claim 10 wherein the temperature is higher than 150°C; when the crosslinking agents are activated by ionic way the process is carried out at a temperature preferably lower than 200°C, when the croslinking agents are activated by radical way, the process is carried out at a temperature preferably higher than 250°C.

Inventors: ABUSLEME JULIO A, BESANA GIAMBATTISTA, VITA GIANDOMENICO, ABUSLEME, JULIO A., BESANA, GIAMBATTISTA, VITA, GIANDOMENICO
Applicants: SOLVAY SOLEXIS SPA, SOLVAY SOLEXIS S.P.A.
Application year: 2000
Main classification: C08K13
IPC codes: C08K5, C08J3, C08L27, C08L23