Silicon based substrate with environmental/thermal barrier layer

Abstract: A barrier layer for a silicon containing substrate which inhibits the formation of gaseous species of silicon when exposed to a high temperature aqueous environment comprises a barium-strontium alumino silicate.

Description: The present invention relates to an article comprising a substrate containing silicon and a barrier layer which functions as a protective environmental/ thermal barrier coating and, more particularly, a barrier layer which inhibits the formation of gaseous species of Si, particularly Si(OH) x when the article is exposed to a high temperature, aqueous (water and/or steam) environment. Ceramic materials containing silicon and metal alloys containing silicon have been proposed for structures used in high temperature applications as, for example, gas turbine engines, heat exchangers, internal combustion engines, and the like. A particular useful application for these materials is for use in gas turbine engines which operate at high temperatures in aqueous environments. It has been found that these silicon containing substrates can recede and lose mass as a result of a formation volatile Si species, particularly Si(OH) x and SiO when exposed to high temperature, aqueous environments. For example, silicon carbide when exposed to a lean fuel environment of approximately 1 ATM pressure of water vapor at 1200°C will exhibit weight loss and recession at a rate of approximately 0.1524 mm (6 mils) per 1000 hrs. It is believed that the process involves oxidation of the silicon carbide to form silica on the surface of the silicon carbide followed by reaction of the silica with steam to form volatile species of silicon such as Si(OH) x . Naturally it would be highly desirable to provide a external barrier coating for silicon containing substrates which would inhibit the formation of volatile silicon species, Si(OH) x and SiO, and thereby reduce recession and mass loss. The US 5 164 266 A shows a slidable ceramic member including a base of a sintered ceramic material which is a compound including silicon (Si) as a constituent element, the base having a sliding surface, and a coated layer covering the sliding surface of the base, the coated layer comprising a compound of elements, such as barium (Ba) and calcium (Ca), belonging to group IIa of the periodic table, oxygen (O), and silicon like Si3N4 and Sic. This coating can be a barrier layer, which is able to inhibit the formation of gaseous species of Si when the article is exposed to high temperature. US 5 391 404 A discloses a silicon-base ceramic substrate which is provided with a mullite coating by flame-spraying heated crystalline mullite powders onto a substrate that is preheated to a temperature in excess of 800°C. The mullite immediately crystallizes as it solidifies. Accordingly, it is the principle object of the present invention to provide an article comprising a silicon containing substrate with a barrier layer which inhibits the formation of gaseous species of Si, particularly Si(OH) x , when the article is exposed to a high temperature, aqueous environment. A second objective of this invention is to provide an article comprising a substrate with a barrier layer providing thermal protection, such layer closely matching the thermal expansion of the substrate. It is further object of the present invention to provide method for producing an article as aforesaid. The problems are solved by the teaching according to the independent claims. Particular developments are given in the dependent claims. The present invention relates to an article comprising a silicon containing substrate having a barrier layer on the substrate, wherein the barrier layer functions to both inhibit the formation of undesirable gaseous species of silicon when the article is exposed to a high temperature, aqueous environment and to provide thermal protection. By high temperatures is meant the temperature at which the Si in the substrate forms Si(OH) x and/or SiO in an aqueous environment. By aqueous environment is meant a water and/or steam environment. The silicon containing composite is preferably a ceramic or metal alloy containing silicon. The external barrier layer is characterized by a coefficient of thermal expansion which should be within plus or minus 3.0 ppm per degree centigrade of the coefficient of expansion of the silicon containing substrate. The barrier layer in accordance with the present invention comprises a barium aluminosilicate and, preferably, a barium-alkaline earth aluminosilicate wherein the alkaline earth metal is strontium. In a preferred embodiment of the present invention the article can include one or more intermediate layers between the silicon based substrate and the barrier layer. The intermediate layer(s) and serve(s) to provide enhanced adherence between the barrier layer and the substrate and/or to prevent reactions between the barrier layer and the substrate. The said intermediate layer may be selected from the group consisting of SiO 2 , mullite, mullite-barium strontium aluminosilicate, mullite-yttrium silicate, mullite-calcium aluminosilicate, and silicon metal. Another embodiment shows an intermediate layer selected from the group consisting of mullite, barium strontium aluminosilicate, mullite-yttrium silicate, calcium aluminosilicate and mixture thereof. The said intermediate layer may have a thickness of ≥ 0.0127 mm (0.5 mils; 0.0005 inch), especially a thickness of 0.0762 mm to 0.762 mm (3 to 30 mils) or 0.0762 mm to 0.127 mm (3 to 5 mils) resp. and may comprise mullite. A bond layer may be situated between the substrate and the intermediate layer preferably silicon metal or SiO 2 . The thickness of the bond layer may be of between about 0.0762 mm to 0.1524 mm (3 to 6 mils). The invention further relates to a method for producing an article comprising a silicon containing substrate and a barrier layer which inhibits the formation of gaseous species of silicon and/or provides thermal protection when the article is exposed to a high temperature, aqueous environment as defined above. The method for preparing the article comprises that the coefficient of thermal expansion of the barrier layer should be within ± 3.0 ppm/°C the coefficient of thermal expansion of the substrate or within ± 0.5 ppm/°C the coefficient of thermal expansion of the substrate. The method may further include the step of grit blasting the substrate prior to applying the barrier layer and may include grit blast with alumina particles having a particle size of ≤ 30 microns, especially grit blasting at a velocity of 150 m/sec to 200 m/sec. Another optional step of the invention includes preoxidizing the substrate to form a layer of SiO 2 prior to applying the barrier layer, wherein preferably the preoxiding comprises heating the substrate at a temperature of between 800°C to 1200°C for 15 minutes to 100 hours. After applying the barrier layer begins the optional step of heat treating the article at a temperature of 1250°C for 24 hours. Within the frame of the invention is the step of thermal spraying while holding the substrate at a temperature of between 870°C and 1200°C. The coefficient of thermal expansion of the barrier layer is within ± 3.0 ppm/°C the coefficient of thermal expansion of the subtrate or ± 0.5 ppm/°C the coefficient of thermal expansion of the substrate. Further advantages, characteristics and details of the invention are apparent from the following detailed description of preferred embodiments of the invention with reference to the attached drawings. Figure 1 is a graph showing the stability of the barrier layer of the present invention with respect to recession and mass loss; Figure 2 is a photomicrograph through a sample of the barrier layer of the present invention on a silicon carbide substrate; Figure 3 is a photomicrograph of a sample of the barrier layer of the present invention applied to an intermediate layer on a silicon carbide substrate; and Figure 4 demonstrates the effect of three specimens of the barrier layer of the present invention on weight loss in high temperature, aqueous environments. The present invention relates to an article comprising a silicon containing substrate and a barrier layer, wherein the barrier layer inhibits the formation of gaseous species of silicon when the article is exposed to a high temperature, aqueous environment. The invention also relates to a method for producing the aforesaid article. In addition, it should be appreciated that while the barrier is particularly directed to an environmental barrier layer, the barrier layer also functions as a thermal barrier layer and thus the present invention broadly encompasses the use of environmental/ thermal barrier layers on silicon containing substrates and on substrates having comparable thermal expansion coefficients. According to the present invention, the silicon containing substrate may be a silicon containing ceramic substrate or a silicon containing metal alloy. In a preferred embodiment, the silicon containing substrate is a silicon containing ceramic material as, for example, silicon carbide, silicon nitride, silicon carbon nitride, silicon oxynitride and silicon aluminum oxynitride. In accordance with a particular embodiment of the present invention, the silicon containing ceramic substrate comprises a silicon containing matrix with reinforcing such as fibers, particles, and the like and, more particularly, a silicon based matrix which is fiber-reinforced. Particularly suitable ceramic substrates are a silicon carbide coated silicon carbide fiber-reinforced silicon carbide particle and silicon matrix, a carbon fiber-reinforced silicon carbide matrix and a silicon carbide fiber-reinforced silicon nitride matrix. Particularly useful silicon-metal alloys for use as substrates for the article of the present invention include molybdenum-silicon alloys, niobium-silicon alloys, and other Si containing alloys having a coefficient of thermal expansion compatable with the barrier layer of the present invention. The barrier layer in the article of the present invention include alkaline earth metal aluminosilicates, which are barium aluminosilicates, and, particularly, barium-strontium aluminosilicates. In a particular embodiment, the barrier layer comprises from about 0.00 to 1.00 mole BaO, from 0.00 to 1.00 mole of an oxide of a second alkaline earth metal, preferably SrO, 1.00 mole Al 2 O 3 and 2.00 mole SiO 2 . wherein the total of the BaO and the second alkaline earth metal or SrO is 1.00 mole. The preferred barrier layer of the present invention comprises from 0.10 mole to 0.9 mole, preferably 0.25 to 0.75 mole BaO, 0.1 mole to 0.9 mole, preferably 0.25 to 0.75 SrO, 1.00 mole Al 2 O 3 and 2.00 mole SiO 2 wherein the BaO and SrO total is 1.00 mole. A particularly suitable barrier layer for use on silicon containing ceramic compositions in the article of the present invention comprises 0.75 mole BaO, 0.25 mole SrO, 1.00 mole Al 2 O 3 , and 2.00 mole SiO 2 . It is an important feature of the present invention to maintain compatibility between the coefficient of thermal expansion of the silicon containing substrate and the barrier layer. In accordance with the present invention it has been found that the coefficient of thermal expansion of the barrier layer should be within ± 3.0 ppm per degrees centigrade, preferably ± 0.5 ppm per degrees centigrade, of the coefficient of thermal expansion of the silicon containing substrate. When using a silicon containing ceramic substrate such as a silicon carbide or a silicon nitride matrix with or without reinforcing fibers as described above in combination with the preferred barium-strontium aluminosilicate barrier layer of the present invention, it is necessary to develop a stable crystallographic structure in the barrier layer of at least 50% by volume celsian in order to insure both structural integrity of the barrier layer and the desired thermal compatibility with respect to expansion coefficient between the silicon containing substrate and the barrier layer. The crystallographic structure of the barium-strontium aluminosilicate barrier layer is obtained as a result of preferred processing application and heat treating processing steps as will be described hereinbelow. The barrier layer should be present in the article at a thickness of greater than or equal to 0.0127 mm (<0.5 mils 0.0005 inch), preferably between 0.0762 mm to 0.762 mm (3 to 30 mils) and ideally between 0.0762 mm to 0.127 mm (3 to 5 mils). The barrier layer may be applied to the silicon based substrate by any suitable manner known in the art, however, it is preferable that the barrier layer be applied by thermal spraying as will be described hereinbelow. In a further embodiment of the article of the present invention, an intermediate layer can be provided between the silicon containing substrate and the barrier layer. The intermediate layer(s) serve(s) to provide enhanced adhesion between the barrier layer and the substrate and/or to prevent reactions between the barrier layer and the substrate. The intermediate layer consists of, for example, SiO 2 , mullite, mullite-barium strontium aluminosilicate, mullite-yttrium silicate, mullite-calcium aluminosilicate, and silicon metal. Mullite has been found to be a particularly useful intermediate layer; however, mullite by itself tends to be cracked as the result of thermal spray fabrication processing. Accordingly, it is preferred that the barrier layer comprises mullite-barium strontium aluminosilicate, mullite-yttrium silicate, or mullite-calcium aluminosilicate in an amount of between 40 to 80 wt.% mullite and between 20 to 60 wt.% barium strontium aluminosilicate or yttrium silicate or calcium aluminosilicate. The thickness of the intermediate layer is typical to those described above with regard to the barrier layer and the intermediate layer may likewise be disposed in any manner known in the prior art, however, preferably by thermal spraying as described hereinbelow. In addition to the intermediate layer, a bond layer may be provided between the silicon containing substrate and the intermediate layer. A suitable bond layer includes silicon metal in a thickness of 0.0762 mm to 0.1524 mm, (3 to 6 mils). Alternatively, the silicon containing substrate may be pre-oxidized to provide a SiO 2 bond layer prior to application of the intermediate layer. The method of the present invention comprises providing a silicon containing substrate and applying a barrier layer wherein the barrier layer inhibits the formation of gaseous species of silicon when the article is exposed to a high temperature, aqueous environment. In accordance with the present invention it is preferred that the barrier layer be applied by thermal spraying. It has been found that the barrier layer should be thermal sprayed at a temperature of between 870°C and 1200°C in order to help equilibrate the as-sprayed, splat quenched, microstructure and to provide a means to manage stresses which control delamination. The article being prepared in accordance with the method of the present invention is a silicon containing ceramic with a barium (strontium) aluminosilicate containing barrier layer and the barium (strontium) aluminosilicate barrier layer has celsian crystallographic structure in an amount of at least 50% by volume in the barrier layer. The formation of the celsian crystallographic structure insures compatibility between the coefficient of thermal expansion of the silicon containing ceramic and the barium (strontium) aluminosilicate barrier layer as described above. The silicon containing substrate should be cleaned prior to application of the barrier layer to remove substrate fabrication contamination. It is preferred that the silicon based substrate be subjected to a grit blasting step prior to application of the barrier layer. The grit blasting step must be carried out carefully in order to avoid damage to the surface of the silicon-containing substrate such as silicon carbide fiber reinforced composite. It has been found that the particles used for the grit blasting should be hard enough to remove the undesired contamination but not as hard as the substrate material to prevent erosive removal of the substrate. Further, the particles must be small to prevent impact damage to the substrate. When processing an article comprising a silicon carbide ceramic composite substrate, it has been found that the grit blasting should be carried out with Al 2 O 3 particles, preferably of a particle size of ≤ 30 microns and, preferably, at a velocity of 150 to 200 m/sec. In addition to the foregoing, it may be particularly useful to preoxidize the silicon based substrate prior to application of the intermediate and/or barrier layer in order to improve adherence. It has been found that bond layers of between 100 nanometers to 2000 nanometers are preferred. SiO 2 bond layers of the desired thickness can be achieved by preoxidizing the silicon-carbide substrate at a temperature of between 800°C to 1200°C for 15 minutes to 100 hours. The silicon bond layer may be applied directly to the grit blasted surface by thermal spraying at a temperature of between 870°C to 1200°C to a thickness of 0.0762 mm to 0.1524 mm (3 to 6 mils). Intermediate layers may be applied between the substrate and/or bond layer and the barrier layer or between the bond layer and barrier layer by thermal spraying in the same manner described above with respect to the barrier layer. As noted above, the preferred intermediate layers include mullite, mullite-barium strontium aluminosilicate, mullite-yttrium silicate, and mullite-calcium aluminosilicate. After application of the desired layers to the silicon-based substrate material, the article is subjected to a heat treatment step in order to provide stress relief to the thermal sprayed structure, to promote bonding between the sprayed powder particles and between the layers and the substrate, and to develop the celsian phase in the BSAS barrier layer which is essentially amorphous in the as sprayed condition. The heat treatment step is carried out at a temperature of 1250°C for 24 hours. The advantages of the article of the present invention will become clear from consideration of the following examples. Example 1 Figure 1 shows a comparison of a hot pressed bulk specimen of BSAS, of composition 0.75 BaO·0.25 SrO·Al 2 O 3 ·2 SiO 2 in comparison to silicon carbide thermal cycle tested 250 cycles between room temperature and 1200°C in a simulated combustion environment of high steam, lean fuel conditions. The results show 8 mg/cm 2 weight loss for the silicon carbide while the BSAS gains a very small amount of weight ~0.4 mg/cm 2 . The results show that silicon carbide is not stable to this environment and that the BSAS system is much more stable. Example 2 Figure 2 is a cross section of a 4 mil thick BSAS of composition 0.75 BaO·0.25 SrO·Al 2 O 3 ·2 SiO 2 coating on SiC composite. The BSAS was thermal sprayed onto the silicon carbide composite using the following parameters: Parameter Setting Plasma torch Metco 3M Nozzle GH Anode std. Powder port Metco #2 Primary gas Ar@80 Metco gage Secondary gas H2@8 Metco gage Substrate temp. 850°C Carrier gas Ar@37 Metco gage Powder feed 15 to 25 gpm Intermed. Surface Power 30kw 25kw Stand-off 2.5-3" 5" Prior to coating the substrate was cleaned by grit blasting with 27 micron alumina particles at an impact velocity of 150 to 200 mps. As can be seen from Figure 2, the invention results in an excellent barrier layer structure. Example 3 Figure 3 is a cross sectional view of a BSAS of composition 0.75 BaO·0.25 SrO·Al 2 O 3 ·2 SiO 2 barrier layer on a mullite/BSAS intermediate layer of 4±1 mils thickness on a silicon layer on silicon carbide composite. The coating was fabricated using the following parameters. Plasma torch Metco 3M Nozzle GH Anode std. Powder port Metco #2 Primary gas Ar@80 Metco gage Secondary gas H2@8 Metco gage Substrate temp. 850°C Carrier gas Ar@37 Metco gage Powder feed 15 to 25 gpm Interface Intermed. Surface Power 25 kw 30kw 25kw Stand-off 4" 2.5-3" 5" Prior to coating the substrate was cleaned by grit blasting with 27 micron alumina particles at an impact velocity of 150 to 200 mps. As can be seen from Figure 3, the invention results in an excellent barrier layer structure. Example 4 Coatings of the BSAS (barium strontium aluminosilicate) based barrier layer coating system were fabricated onto silicon carbide composite substrates having an intermediate layer as indicated below and were exposed along with an uncoated silicon carbide composite substrate (98-17A) to high pressure, combustion environment, burner rig testing similar to conditions that occur in gas turbines engines. The BSAS coatings on all samples had the following composition: 0.75 BaO·0.25 SrO·Al 2 O 3 ·2 SiO 2 . The BSAS coatings were 4±1 mils in thickness and the intermediate layers were also 4±1 mils in thickness and were applied by thermal spraying as indicated below. These coatings consisted of variations of BSAS on mullite (98-17C) and BSAS on mullite plus BSAS (98-17B and 98-17D). Testing occurred using conditions of 1200°C test temperature, 200 hours exposure time, a fuel to air ratio of 0.053, and 6 atm pressure. After 200 hours exposure the uncoated substrate exhibited approximately 65 mg weight loss compared with weight gain of the coated coupons demonstrating that the coatings protected the substrate based on weight change data. No bond coat was used for these specimens. Thermal spray parameters were: Parameter Setting Plasma torch Electro-plasma 03CA Nozzle 03CA-27 Anode 03CA-167 Powder port ext. 90° Primary gas Ar@14.4 SLM Secondary gas He@9.8 SLM Substrate temp. 1050-1250°C Carrier gas Ar@3-6 SLM Powder feed 20 gpm Intermed. Surface Power 45kw 45kw Stand-off 4" 4" The results are shown in Figure 4 below which shows the effectiveness of the barrier layer of the present invention. Example 5 The coefficient of thermal expansion (CTE) was measured for BSAS systems of 0.75 BaO·0.25 SrO·Al 2 O 3 ·2 SiO 2 having different celsian contents. Celsian content was determined by x-ray analysis of hot pressed coupons of BSAS. The celsian content affected the CTE as seen below. % Celsian Content CTE 5 8.1 25 7.4 95 5.2

Claims: An article comprising: a substrate comprising silicon; and a barrier layer, wherein the barrier layer comprises a barium aluminosilicate, especially a barium strontium aluminosilicate, wherein the crystallographic structure of the barrier layer is at least 50 % by volume celsian and wherein the barrier layer inhibits the formation of gaseous species of Si when the article is exposed to a high temperature, aqueous environment. An article according to claim 1, wherein the barrier layer comprises from 0.00 to 1.00 moles BaO, from 0.00 to 1.00 mole SrO, 1.0 mole Al 2 O 3 and 2.00 mole SiO2 wherein the total of BaO and SrO is 1.00 mole. An article according to claim 1 wherein the barrier layer consists essentially of from 0.00 to 1.00 mole BaO, from 0.00 to 1.00 mole of an oxide of second alkaline earth metal 1.00 mole Al 2 O 3 and 2.00 mole SiO 2 wherein BaO plus the other alkaline earth metal total 1 mole. An article according to one of the claims 1 to 3 wherein the substrate is selected from the group consisting of silicon containing ceramic and metal alloys containing silicon. An article according to claim 4 wherein the substrate is a silicon containing ceramic selected from the group consisting of silicon carbide, silicon nitride, silicon aluminum oxynitride. An article according to claim 4 wherein the substrate is a composite comprising a silicon based matrix and a reinforcing particle. An article according to claim 6 wherein said substrate is selected from the group consisting of silicon carbide fiber-reinforced silicon carbide matrix, carbon fiber-reinforced silicon carbide matrix and silicon carbide fiber-reinforced silicon nitride. An article according to claim 4 wherein said substrate is a silicon containing metal alloy selected from the group consisting of molybdenum-silicon alloys, niobium silicon alloys, iron-silicon alloys, and iron-nickel-silicon based alloys. An article according to one of the claims 2 to 8 wherein the barrier layer comprises from 0.10 mole to 0.90 mole BaO and from 0.10 mole to 0.90 mole SrO. An article according to claim 9 wherein the barrier layer comprises from 0.25 mole to 0.75 mole BaO and from 0.25 mole to 0.75 mole SrO. An article according to one of the claims 2 to 10 wherein the barrier layer comprises 0.75 mole BaO and 0.25 mole SrO. An article according to one of the claims 3 to 10 wherein the barrier layer comprises from 0.10 mole to 0.90 mole BaO and from 0.10 mole to 0.90 mole second alkaline earth oxide. An article according to claim 12 wherein the barrier layer comprises from 0.25 mole to about 0.75 mole BaO and from 0.25 mole to 0.75 mole second alkaline earth oxide. An article according to one of the claims 3 to 8, 12 or 13 wherein the barrier layer comprises 0.75 mole BaO and 0.25 mole second alkaline earth oxide. An article according to one of the claims 1 or 4 to 8 wherein the coefficent of thermal expansion of the barrier layer is within ± 3.0 ppm/°C the coefficient of thermal expansion of the substrate. An article according to claim 15 wherein the coefficent of thermal expansion of the barrier layer is within ± 0.5 ppm/°C the coefficient of thermal expansion of the substrate. An article according to one of the claims 1 or 4 to 8 wherein the barrier layer has a thickness of ≥ 0.0127 mm (0.5 mils; 0.0005 inch), preferably 0.0762 mm to 0.127 mm (3-5 mils). An article according to one of the claims 1 to 17 including an intermediate layer between the substrate and the barrier layer. An article according to claim 18 wherein said intermediate layer is selected from the group consisting of SiO 2 , mullite, mullite-barium strontium aluminosilicate, mullite-yttrium silicate, mullite-calcium aluminosilicate, and silicon metal. An article according to claim 18 wherein said intermediate layer is selected from the group consisting of mullite, barium strontium aluminosilicate, mullite-yttrium silicate, calcium aluminosilicate and mixtures thereof. An article according to claim 20 wherein said intermediate layer comprises mullite. An article according to claim 20 or 21 wherein said intermediate layer comprises from 40 to 80 wt.% mullite and from 60 to 20 wt.% barium strontium aluminosilicate. An article according to claim 20 or 21 wherein said intermediate layer comprises from 40 to 80 wt.% mullite and from 60 to 20 wt.% yttrium silicate or wherein said intermediate layer comprises from 40 to 80 wt.% mullite and from about 60 to 20 wt.% calcium aluminosilicate. An article according to claim 18 including a bond layer between the substrate and the intermediate layer. An article according to claim 24 wherein the bond layer is silicon metal or SiO 2 . An article according to one of the claims 18 to 24 wherein the intermediate layer has a thickness of ≥ 0.0127 mm (0.5 mils; 0.0005 inch). An article according to one of the claims 1 to 11 wherein the barrier layer has a thickness of between 0.0762 mm to 0.762 mm (3 to 30 mils), preferably a thickness of between 0.0762 mm to 0.127 mm (3 to 5 mils). An article according to one of the claims 18 to 23 wherein the intermediate layer has a thickness of 0.0762 mm to 0.762 mm (3 to 30 mils), preferably a thickness of 0.0762 mm to 0.127 mm (3 to 5 mils). An article according to claim 24 or 25 wherein the bond layer has a thickness of between 0.0762 mm to 0.1524 mm (3 to 6 mils). A method for preparing an article comprising the steps of: providing a substrate comprising silicon; and applying a barrier layer to the substrate wherein the barrier layer comprises a barium aluminosilicate, especially a barium strontium aluminosilicate, wherein the crystallographic structure of the barrier layer is at least 50 % by volume celsian and wherein the barrier layer inhibits the formation of a gaseous species of Si when the article is exposed to a high temperature, aqueous environment. A method according to claim 30 wherein the coefficient of thermal expansion of the barrier layer is within ± 3.0 ppm/°C the coefficient of thermal expansion of the substrate or wherein the coefficient of thermal expansion of the barrier layer is within ± 0.5 ppm/°C the coefficient of thermal expansion of the substrate. A method according to claim 30 or 31 further including the step of grit blasting the substrate prior to applying the barrier layer. A method according to claim 32 including grit blast with alumina particles having a particle size of ≤ 30 microns, especially including grit blasting at a velocity of 150 m/sec to 200 m/sec. A method according to one of the claims 30 to 33 including applying the barrier layer by thermal spraying. A method according to claim 34 including thermal spraying while holding the substrate at a temperature of between 870°C to 1200°C. A method according to one of the claims 30 to 33 including the step of preoxidizing the substrate to form a layer of SiO 2 prior to applying the barrier layer, wherein preferably the preoxidizing comprises heating the substrate at a temperature of between 800°C and 1200°C for 15 minutes to 100 hours. A method according to one of the claims 30 to 35 including heat treating at a temperature of 1250°C for about 24 hours, especially including the step of, after applying the barrier layer, heat treating the article at a temperature of 1250°C for about 24 hours. A method according to claim 36 wherein the coefficient of thermal expansion of the barrier layer is within ± 3.0 ppm/°C the coefficient of thermal expansion of the substrate or wherein the coefficient of thermal expansion of the barrier layer is within ± 0.5 ppm/°C the coefficient of thermal expansion of the substrate. A method according to one of the claims 30 to 38 wherein the barrier layer comprises from 0.00 to 1.00 mole BaO, from 0.00 to 1.00 mole SrO, 1.00 mole Al 2 O 3 and 2.00 mole SiO 2 wherein the total of BaO and SrO is 1.00 mole. A method according to one of the claims 30 to 38 wherein the barrier layer consists essentially of from 0.00 to 1.00 mole BaO, from 0.00 to 1.00 mole of an oxide of second alkaline earth metal 1.00 mole Al 2 O 3 and 2.00 mole SiO 2 wherein BaO plus the other alkaline earth metal total 1 mole. A method according to one of the claims 30 to 39 wherein the barrier layer comprises from 0.10 mole to 0.90 mole BaO and from 0.10 mole to 0.90 mole SrO, especially wherein the barrier layer comprises from 0.25 mole to 0.75 mole BaO and from 0.25 mole to 0.75 mole SrO. A method according to one of the claims 30 to 41 wherein the barrier layer comprises 0.75 mole BaO and 0.25 mole SrO.

Inventors: ALLEN WILLIAM P, BANSAL NARROTTAM P, EATON HARRY E, JACOBSON NATHAN S, LEE KANG N, LUTHRA KRISHAN L, MESCHTER PETER J, OPILA ELIZABETH J, SMIALEK JAMES L, SPITSBERG IRENE T, WANG HONGYU, ALLEN, WILLIAM P., BANSAL, NARROTTAM P., EATON, HARRY E., JACOBSON, NATHAN S., LEE, KANG N., LUTHRA, KRISHAN L., MESCHTER, PETER J., OPILA, ELIZABETH J., SMIALEK, JAMES L., SPITSBERG, IRENE T., WANG, HONGYU
Applicants: GEN ELECTRIC, NASA, UNITED TECHNOLOGIES CORP, GENERAL ELECTRIC COMPANY, THE UNITED STATES OF AMERICA, REPRESENTED BY THE ADMINISTRATOR OF THE NATIONAL AERONAUTICS AND SPACE ADMINISTRATION (NASA), UNITED TECHNOLOGIES CORPORATION
Application year: 2000
Main classification: C04B41
IPC codes: C04B41, B05D5, C23C28, C23C4, B32B18, B32B15, B05D7