Plastic container and method for manufacturing same

Abstract: A plastic container (10) comprises a main body (11), a large-diameter member (12) and a small-diameter-formed member (13). The main body is formed of a plastic laminate film into a tubular shape. The large-diameter-formed member is joined to the outer surface of the end of the main body by an insert-injection process. The small-diameter-formed member is jointed to the inner surface of the other end of the main body by the insert-injection process. Further, there is disclosed a fluid discharging apparatus, comprising a receiving tube (131) having a pressing body (132), a piston (124) and a fluid dispensing cartridge adapted to be squeezed by said piston through said pressing body, said pressing body comprising a tubular member and a plate member, a central portion of which elastically deforms into a curved shape when pushed by said piston.

Description: The present invention relates to a method of manufacturing a plastic container, and to a plastic container which is suitable for receiving contents in the form of powder, particle or liquid. Containers for receiving solids such as ground coffee beans, the moisture of which should be decreased, are required to be formed of material through which moisture cannot pass. For this kind of container, glass containers, metallic cans or plastic containers obtained by a blow molding method, are generally used. Glass containers and metallic cans have excellent moisture-proof, gas isolating, and good storage properties. They do however have problems relating to the weight and volume of the container itself, which may hinder disposal of the used container. Plastic containers obtained by a blow molding method can solve the problems of weight and volume of a glass container or a metallic can. It is, however, impossible to decrease the thickness of a plastic container under 0.7 mm by conventional blow molding methods. Accordingly, for plastic containers obtained by a blow molding method, only a co-extruded article of a barrier base material such as ethylene vinyl alcohol (EVOH) copolymer resins (i.e., "EVAL® ") and a synthetic resin material such as polyethylene, polypropylene or the like can provide appropriate moisture-proof and gas isolating properties. Containers may otherwise be manufactured by putting an intermediate tubular body formed of a plastic laminate film on a mandrel serving as a core for a mold; putting upper and lower local molds on the mandrel in which the intermediate tubular body has already been put; and injecting synthetic resin material in a molten state into the upper and lower local molds by an insert-injection process so as to form upper and lower formed members integrally with the outer surface of the intermediate tubular body. Plastic containers 1 obtained by the above-described method, may comprise an intermediate tubular body 2, an upper formed member 3 integrally connected to the outer surface of the upper end portion of the intermediate tubular body 2, a lower formed member 4 integrally connected to an outer surface of the lower end portion of the intermediate tubular body 2 and a cover member 5 for closing the opening end of the upper formed member 3, as shown in FIG. 6. The intermediate tubular body of the plastic container is formed of plastic laminate film to enable multicolor printing on the outer surface of the intermediate tubular body. A disadvantage of this style of container, is that the upper and lower formed members formed on the outer surface of the intermediate tubular body decrease the effective area on which the printing may be applied. US patent No. 5, 873,970 discloses a method of manufacturing a plastic container, comprising the steps of: preparing a mold having a first cavity arranged to form a first formed member, and a second cavity arranged to form a second formed member; forming a tubular body of a plastic laminate film; putting the tubular body on an outer surface of a mandrel serving as a core for the mold; placing said mandrel in the mold; and injecting synthetic resin material in a molten state into the first and second cavities by an insert-injection process, wherein the first formed member is formed integrally with an outer surface of an end of the tubular body. A disadvantage of the above-described methods for manufacturing a plastic container can be seen when the lower formed member is provided with a bottom and the lower edge of the intermediate tubular body comes into contact with this lower formed member. Wrinkles may occur at the end of the intermediate tubular body or the end thereof may be turned up due to the injection pressure of the synthetic resin material in the molten state during the insert injection forming, thus leading to substandard articles. The present invention seeks to reduce some of the disadvantages outlined above. According to a first aspect of the present invention, a method of manufacturing a plastic container as defined above, is characterised in that: the first and second cavities are arranged such that an inner diameter of the first formed member is greater than an outer diameter of the second formed member; the mandrel is placed so that an end of the tubular body locates at an inner side of said first cavity and another end thereof locates at an outer side of the second cavity; wherein the synthetic resin material is injected such that the second formed member is formed integrally with an inner surface of the other end of the tubular body. Preferably, a method of the present invention further comprises the step of: pulling the mandrel out of the mold after the insert-injection process, wherein the first formed member and the second formed member are arranged so that the mandrel may be pulled out without being hindered. A method of manufacturing as disclosed in the present invention has the advantage that a mandrel can smoothly be inserted into a mold, the mold having a first cavity formed with a larger inner diameter than an outer diameter of a second cavity formed in the mold. A further advantage is that this method also enables the mandrel to be pulled out easily without hindering the first formed member. A further advantage of the present invention is that it is possible to prevent wrinkles from occurring at the end of the tubular body and to prevent the end thereof from being turned up during the insert-injection process. According to a second aspect of the present invention a plastic container comprises: a main body formed of a plastic laminate film into a tubular shape; a first formed member joined to an outer surface of an end of the main body by an insert-injection process; and a second formed member joined to another end of the main body by the insert-injection process; the plastic container being characterised in that: said first formed member is a large diameter member of tubular shape; and said second formed member is a small diameter member joined to an inner surface of the main body, wherein: an outer diameter of the second formed member is smaller than an inner diameter of the first formed member. Embodiments of this invention provide a plastic container with a larger effective area on which printing is enabled, in comparison with conventional plastic containers. This printing area is provided on the tubular body. Locating the second formed member inside the main body provides a larger effective area of the main body, on which to print. Preferably, the first formed member and the second formed member are arranged so that a mandrel used in the insert-injection process may be pulled out of the main body without being hindered. More preferably, a container of the present invention has a grip portion formed on an outer surface at a lower end of the first formed member. Embodiments of the present invention will hereinafter be described, by way of example, with reference to the accompanying drawings, in which: FIG. 1 shows a front view having a half cross-sectional portion, illustrating a plastic container obtained in accordance with a manufacturing method of an embodiment of the present invention; FIG. 2 shows a schematic view illustrating the method for manufacturing an embodiment of the plastic container of the present invention; FIG. 3 illustrates the second cavity for forming the second formed member in the method for manufacturing the plastic container, FIG. 4 shows a schematic view illustrating a method of manufacturing another embodiment of the plastic container of the present invention; FIG. 5 shows another schematic view illustrating the method of manufacturing the plastic container; FIG. 6 shows a perspective view illustrating a plastic container obtained by the conventional manufacturing method; FIG. 7 shows an enlarged cross-sectional view of a portion of a laminate used in the container of the present invention; FIG. 8 illustrates a side view of a container for storing fluid that is not an embodiment of the present invention; FIG. 9 illustrates a method for preparing a main body for the container of the present invention with the use of the laminate; FIG. 10 is a view illustrating another method for preparing the main body for the container of the present invention with the use of the laminate; and FIG. 11 is a plan view illustrating the entirety of the laminate as shown in FIG. 7. FIG. 1 illustrates an embodiment of the present invention, in which a plastic container is used as a container for ground coffee beans or powdery coffee (hereinafter referred to as the "coffee-container"). The coffee-container 10 is composed of a main body 11 that is formed of a plastic laminate film in a tubular shape, an upper-formed member 12 that is integrally formed with the outer surface of one end of the main body 11 and a lower-formed member 13 that is integrally formed with the inner surface of the other end of the main body 11. The upper formed member 12 is formed into a tubular shape, and is provided with an upper opening end having an inside diameter R1. The upper-formed member 12 is provided on the outer surface of its upper portion with a threaded portion 14 and on the outer surface of its lower portion with a grip portion 15. The upper opening end of the upper-formed member 12 is sealed with a cover member. A cap (not shown) is screwed on the thread portion 14 of the upper-formed member 12. The lower-formed member 13 is formed into a tubular shape with a bottom having an outside diameter R2. The outside diameter R2 of the lower-formed member 13 is designed to be smaller than the inside diameter R1 of the upper-formed member 12. More specifically, the upper-formed member 12 serves as the large-diameter-formed member and the lower-formed member 13 serves as the small-diameter-formed member. The main body 11 is of tubular shape with opposite opening ends. As illustrated in FIGS. 8 to 11, it can be obtained by cutting a plastic laminate film into a rectangular shape to form a sheet material and then joining the outer surface of one side edge of the thus formed sheet material with the inner surface of the other side edge thereof. For the preparation of the main body 11, a different process may be adopted involving joining the inner surface of the one side edge of the sheet material with the inner surface of the other side edge thereof (hereinafter referred to as the "first optional joining process"). A different process that may be adopted involves placing the outer surface of the one side edge of the sheet material with the inner surface of the other side edge thereof and joining them with the use of an adhesive tape applied from the inside of the main body (hereinafter referred to as the "second optional joining process"). In view of the requirement for excellent moisture-proof and excellent gas isolating properties, suitable use may be made of the above-mentioned plastic laminate film (i) a laminate of polyethylene film having a thickness of 70 µm, a polyester film having a thickness of 12 µm, an aluminium foil having a thickness of 12 µm and a polyethylene film having a thickness of 70 µm, (ii) a laminate of a cast polypropylene having a thickness of 70 µm, a polyester film having a thickness of 12 µm, an aluminium foil having a thickness of 12 µm and a cast polypropylene having a thickness of 70 µ m or (iii) a laminate of a cast polypropylene having a thickness of 70 µ m, a polyester film having a thickness of 12 µ m and a cast polypropylene having a thickness of 70 µm. When the aluminum film is substituted by a film of ethylene-vinylalcohol copolymer or a silica-deposited film, it is possible to make the main body transparent, while maintaining the excellent moisture-proof property and gas isolating property. The contents received in the container can visually be observed from the outside thereof. When the main body 11 for the coffee-container 10 is formed of the plastic laminate film including the aluminum foil, it is preferable to adopt the first or second optional joining process described above. When the contents to be received in the container is liquid such as fruit juice drink, which has a pH value of up to 4, it is preferable to adopt the second optional joining process for the formation of the main body 11 in order to prevent the aluminum foil from being oxidized to cause elution of aluminum in the liquid. When the main body 11 for the coffee-container 10 is formed of the plastic laminate film including no aluminum foil, it is preferable to adopt the first or second optional joining process for the formation of the main body 11 in order to prevent the adhesive used in the lamination process from being eluted into the contents received in the container. Now, description will be given below of the method for manufacturing the coffee-container 10. The moisture of ground coffee beans or powdery coffee should be decreased as small as possible and the good aroma thereof should be maintained. Accordingly, the coffee-container 10 is required to have the excellent moisture-proof property and the excellent gas isolating property. For these reasons, the plastic laminate film having these excellent properties is selected to be used for the formation of the main body 11 for the coffee-container 10. A mold 20 for the formation of the coffee-container 10 has the first cavity 21 for forming the large-diameter-formed member and the second cavity 22 for forming the small-diameter-formed member as shown in FIG. 2. The first cavity 21 and the second cavity 22 are spaced from each other at a distance corresponding to the dimensions of the main body 11. The first cavity 21 has an inside diameter, which is larger than the outside diameter of the second cavity 22. The first cavity 21 of the mold has a shape corresponding to the upper-formed member 12 of the above-described coffee-container 10. The second cavity 22 of the mold has a shape corresponding to the lower-formed member 13 thereof. The lower-formed member 13, which is formed by the second cavity 22, has a bottom that provides the excellent moisture-proof property and the excellent gas isolating property. The main body 11 is formed into a tubular shape of the plastic laminate film having the excellent moisture-proof property and the excellent gas isolating property. The thus formed main tubular body 11 is put on the outer surface of a mandrel 23, which serves as a core for the mold. When the main tubular body 11 has a circular cross section, the mandrel 23 also has the corresponding circular cross section. When the main tubular body 11 has a rectangular cross section, the mandrel 23 also has, on the other hand, the corresponding rectangular cross section. Then, the mandrel 23 on which the main tubular body 11 has been put, is placed in the mold 20 so that the end of the main tubular body 11 locates inside the first cavity 21 and the other end thereof locates outside the second cavity 22. The mandrel 23, on which the main tubular body 11 has been put, can smoothly be inserted into the mold 20 due to the fact that the inside diameter of the first cavity 21 of the mold 20 is larger than the outside diameter of the second cavity 22 thereof. After the completion of the placement of the mandrel 23 on which the main tubular body 11 is put, in the mold 20, synthetic resin material such as polyethylene resin is injected in a molten state into the first cavity 21 and the second cavity 22 of the mold 20 from a gate 25 formed therein through a runner 24 by means of an insert-injection process. In this case, even when the lower end of the main tubular body 11 reaches the bottom of the second cavity 22 as shown in FIG. 3, an injection pressure of the molten synthetic resin material is applied in directions that are indicated by arrows in FIG. 3 during the insert-injection process. Consequently, wrinkles does not occur at the end of the main tubular body 11 or the end of the main tubular body 11 is not turned up, irrespective of the injection pressure of the molten synthetic resin material. After the completion of a cooling process which is applied to the molten synthetic resin material injected into the first cavity 21 and the second cavity 22, the formation of the coffee-container 10 in which the upper-formed member 12 is integrally formed with the outer surface of the end of the main tubular body 11 and the lower-formed member 13 is integrally formed with the inner surface of the other end of the main tubular body 11. The mandrel 23 placed in the mold 20 is pulled out after the formation of the coffee-container 10. It is possible to pull out easily the mandrel 23 from the mold without being hindered by the upper-formed member 13 due to the fact that the inside diameter of the first cavity 21 of the mold 20 is larger than the outside diameter of the second cavity 22 thereof. In the above-described coffee-container 10, the lower-formed member (i.e., the smaller-diameter-formed member) 13, which is joined to the lower end of the main tubular body 11, locates on the inner surface of the main tubular body 11. As a result, it is possible to increase the effective area, on which the printing is to be applied, by an area occupied by the smaller-diameter-formed member 13. In the coffee-container 10 of the above-mentioned embodiment, the upper-formed member 12 is integrally formed with the outer surface of the end of the main body 11, which is formed into the tubular shape of the plastic laminate film, and the lower-formed member 13 is integrally formed with the inner surface of the other end of the main body 11. It is possible to form the coffee-container 10 in which the upper-formed member 12 is integrally formed with the inner surface of the end of the main body 11, by changing the positional relationship between the mold 20 and the mandrel 23 on the outer surface of which the main body 11 is put. According to such a coffee-container 10, it is possible to increase the effective area, on which the printing is to be applied, by the total area occupied by the small-diameter-formed member 13 and the large-diameter-formed member 12. FIGS. 4 and 5 show another embodiment of the present invention. In the embodiment as shown in FIG. 4, a suction line 31 is formed in the mandrel 30 on the outer surface of which the main tubular body 11 is put. A laminate film 32 can be placed on the lower surface of the mandrel 30 by a suction effect. It is therefore possible to join the laminate film 32 integrally with the smaller-diameter-formed member 13 by injecting the synthetic resin material such as polyethylene resin in a molten state into the smalter-diameter-formed member 13 by means of the insert-injection process. There may suitably be used as the above-mentioned plastic laminate film 32 (i) a laminate of a polyethylene film having a thickness of 70 µm, a polyester film having a thickness of 12 µm, an aluminum foil having a thickness of 12 µm and a polyethylene film having a thickness of 70 µm, (ii) a laminate of a polyethylene film having a thickness of 70 µm, a polyester film having a thickness of 12 µm, a film of ethylene vinyl alcohol (EVOH) copolymer resins (i.e., "EVAL" (trademark)) having a thickness of 15 µm and a polyethylene film having a thickness of 70 µm or (iii) a laminate of a polyethylene film having a thickness of 70 µm, a polyester film having a thickness of 12 µm, an aluminum foil having a thickness of 40 µm and a polyethylene film having a thickness of 70 µ m. In the embodiment as shown in FIG. 5, a suction line 41 is formed in the mandrel 40 on the outer surface of which the main tubular body 11 is put. A synthetic resin-formed body 42, which has previously been formed, can be placed on the lower surface of the mandrel 40 by a suction effect. It is therefore possible to join the synthetic resin-formed body 42 integrally with the smaller-diameter-formed member 13 by injecting the synthetic resin material such as polyethylene resin in a molten state into the smaller-diameter-formed member 13 by means of the insert-injection process. The synthetic resin-formed body 42 can be obtained by subjecting a polyethylene film having a thickness of 70 µm, a polyester film having a thickness of 12 µm, an aluminium foil having a thickness of 40 µm and a polyethylene film having a thickness of 7 µm to a press-forming process. When the plastic container is used as a container in which invasion of oxygen should be avoided, it is preferable to form the synthetic resin-formed body 42 integrally with the small-diameter-formed member 13 of the plastic container in this manner. FIG. 8 shows a container for fluid that is not an embodiment of the present invention. However, FIG. 8 illustrates various aspects of the present invention, in particular how the container of the present invention is formed from the laminate. The container 51 for fluid, of this embodiment, is composed of a main body 60 having opposite opening ends, i.e., front and rear opening ends, and of a pair of closing devices, i.e., a front-bottom member 70 for closing the front opening end of the main body 60 and a rear bottom member 80 for closing the rear opening end of the main body 60. The main body 60 is formed of a laminate 61 in a tubular shape. The laminate 61 comprises a plurality of flexible films (in general, at least three flexible films). The main body 60 tapers off from one end (i.e., the left-hand end in FIG. 8, hereinafter referred to as the "front end") to the other end (i.e., the right-hand end in FIG. 8, hereinafter referred to as the "rear end"). The main body 60 can receive in its inside various fluid such as adhesive, sealant, jam or the like. With reference to the present invention, the width of the laminate 61 becomes gradually smaller from the front end to the rear end as shown in FIG. 11 in correspondence to the tapered main body 11. The main body 11 can be formed by joining one longitudinal edge of the laminate 61 with the other longitudinal edge thereof as described later. The laminate 61 is composed of four films, i.e., the first to fourth films 62 to 65 as shown in FIG. 7, which locate from the outer peripheral side of the main body 11 toward the inner peripheral side thereof in this order. It is preferable to use a film having excellent scratch resistance and a small coefficient of friction, as the first film 62. Resin film is generally used as the first film 62. In this case, it is preferable to use a transparent polyethylene film having a thickness of from 30 µm to 60 µm. A cast polypropylene (CPP) film may be used. The second film 63 is also a resin film. Characters, devices, symbols and the like can easily be printed on the surface (appearing on the outer peripheral side of the main body 11) of the above-mentioned resin film. In this embodiment, a polyester film having a thickness of from 12 µm to 16 µm is used. A film of nylon or oriented polypropylene (OPP) may be used alternatively. The transparent first film 62 permits the characters or the like printed on the surface of the second film 63 to be observed visually from the outside of the main body 11. The third film 64 has a function of imparting non-permeability to the laminate 61. A metallic foil is usually used as the third film 64. With respect to the metallic film, it is preferable to use an aluminium foil having a light weight. The aluminium foil preferably has a thickness of from 9 µm to 12 µm. The fourth film 65 has a function of protecting the third film 64, which is formed of the aluminium foil to prevent it from breaking during the manufacturing process of the container 51. A resin film is usually used as the fourth film 65. There is no specific limitation of material for forming the fourth film 65. However, the same polyethylene film as the first film 62 is used in this embodiment in view of the fact that the main body 11 is formed of the laminate 61. These aspects will be described later. The second film 63 and the third film 64 are joined with each other over their entire opposing surfaces by adhesive 90. The third film 64 and the fourth film 65 are joined with each other in the same manner. The respective opposing portions of the first film 62 and the second film 63 are merely joined with each other by adhesive 90 (the portions of the first and second films 62, 63 which are joined with each other by the adhesive, are hereinafter referred to as the "joined portions" 91). The remaining portions of the first and second films 62, 63 other than the joined portions 91 are not joined with each other. As a result, the remaining portions of the first and second films 62, 63 other than the joined portions 91 can independently behave as the flexible film. Gaps having a height corresponding to the thickness of the adhesive 90 are formed between the above-mentioned remaining portions of the first and second films 62, 63. The supply of air into these gaps forms air layers 66 between the first and second films 62, 63. These air layers 66 have the advantage of improving an impact resistance of the main body 11. The above-mentioned adhesion process for joining the first and second films 62 and 63 with each other may be substituted by a fusion bonding process. The first to fourth films 62 to 65 are subjected to a lamination process to form the laminate 61. In this case, application of adhesive onto at least one of the opposing surfaces of each set of the second and third films 63, 64 and the third and fourth films 64, 65 over its entirety may suffice prior to the lamination process. Application of adhesive onto a portion of at least one of the opposing surfaces of the first and second films 62 and 63, in which portion the joined portion 91 is to be formed, may suffice on the other hand. The laminate 61 having the above-mentioned structure is wound up into a roll as shown in FIG. 9 and one edge 61a of the laminate 61 is placed on the other edge 61b thereof. The inner surface of the one edge 61a of the laminate (i.e., the inner surface of the first film 62) and the outer surface of the other edge 61b thereof (i.e. the outer surface of the fourth film 65) are joined with each other by means of adhesive. The formation of the main body 11 is completed in this manner. The same kind of material is used for forming the first and fourth films 62 and 65 in order to improve the adhesive strength of the opposite edge portions 61a, 61b. The main body 11 may be formed by bending the opposite edge portions 61a, 61b of the laminate 61 so as to cause them to project outward in the diametrical direction of the main body 11 and joining the opposite edge portions 61a, 61b (on the inner surface of the fourth film 65) with each other by means of adhesive. In such a case, the joined portions 61a, 61b, which project outward, are pushed down in any one of directions, which are indicated by arrows in FIG. 10, and joined onto the outer surface of the main body 60 by means of adhesive. As a result, the joined portions of the main body 60 have a larger thickness than the remaining portion. In view of this fact, it is preferable to form the main body 11 in the manner as shown in FIG. 9. In the main body 11 as shown in FIG. 10 the opposite edge portions of the same film, i.e., the fourth film 65 are joined with each other. Consequently, the formation of the first film 62 of the different material from that of the fourth film 65 will cause no problem. The other joining process may be adopted to form the main body 11 of the laminate 61. Provided that a sufficient adhesive strength can be ensured, the opposite edges of the laminate 61 may be butted together and joined with each other by means of adhesive. In any one of the above-described joining processes, the adhesive joining may be substituted by a fusion bonding joining. FIG. 11 shows the laminate 61 in an expanded state. Portions where the joined portions 91 are formed are shown by cross-hatching in FIG. 11. As is clear from the figure, the joined portions 91 are composed of (i) portions that are formed so as to extend on the entire periphery of the front and rear ends of the main body 11, which is formed of the laminate 61, (ii) a portion that is formed so as to extend from the front end of the laminate 61 to the rear end thereof along the horizontal line, which passes through the center of the laminate 61, and (iii) portions (in this embodiment, three portions) that are formed so as to extend from the longitudinal upper edge of the laminate 61 to the longitudinal lower edge thereof at regular intervals. When the main body 11 is formed by winding up the laminate 61 into a roll so as to place its longitudinal edge (i.e., the one edge 61a as shown in FIG. 9) on the other longitudinal edge (i.e., the other edge 61 b as shown in FIG. 9) joined portions 91 are formed that have circular-shaped glued (joined) portions 92 circumferentially extending on the main body 11 and longitudinal glued (joined) portions 93 extending from the front end of the main body 11 to the rear end thereof in its longitudinal direction. The circular-shaped glued portions 92 are formed on the front and rear end of the main body and the middle portion thereof so as to provide the total number of five. The longitudinal edge of the laminate 61 is glued onto the other longitudinal edge thereof, with the result that the two longitudinal glued portions 93 are formed on the periphery of the main body 11 so as to separate from each other by the central angle of 180 degrees of the main body 11. Portions of the laminate 61 other than the circular-shaped glued portions 92 and the longitudinal glued portions 93 (i.e., the portions surrounded by the circular-shaped glued portions 92) are remained as non-glued portions (i.e., non-joined portions) 94 in which the first film 62 and the second film 63 are not glued to each other. In these non-glued portions 94, the first and second films 62 and 63 can independently behave as the flexible film.

Claims: A method of manufacturing a plastic container, comprising the steps of: preparing a mold (20) having a first cavity (21) arranged to form a first formed member (12), and a second cavity (22) arranged to form a second formed member (13); forming a tubular body (11) of a plastic laminate film; putting the tubular body (11) on an outer surface of a mandrel (23) serving as a core for the mold (20); placing said mandrel (23) in the mold (20); and injecting synthetic resin material in a molten state into the first and second cavities (21, 22) by an insert-injection process, wherein the first formed member (12) is formed integrally with an outer surface of an end of the tubular body (11); the method being characterised in that : the second cavity (22) has an outer diameter which is smaller than an inner diameter of the first cavity, the cavities (21, 22) are arranged such that an inner diameter (R1) of the first formed member (12) is greater than an outer diameter (R2) of the second formed member; the mandrel (23) is placed so that an end of the tubular body (11) locates at an inner side of said first cavity (21) and another end thereof locates at an outer side of the second cavity (22); wherein the synthetic resin material is injected such that the second formed member (13) is formed integrally with an inner surface of the other end of the tubular body (11). A method of manufacturing a plastic container as claimed in Claim 1, further comprising the step of: pulling the mandrel (23) out of the mold (20), after the insert-injection process wherein the first formed member and the second formed member are arranged so that the mandrel (23) may be pulled out without being hindered. A plastic container, comprising: a main body (11) formed of a plastic laminate film into a tubular shape; a first formed member (12) joined to an outer surface of an end of the main body (11) by an insert-injection process; and a second formed member (13) joined to another end of the main body (11) by the insert-injection process; the plastic container being characterised in that : said first formed member (12) is a large diameter member of tubular shape; and said second formed member is a small diameter member joined to an inner surface of the main body (11), wherein: an inner diameter of the first formed member (13) is greater than an outer diameter of the second formed member. A container as claimed in Claim 3, wherein: the first formed member and the second formed member are arranged so that a mandrel (23) used in the insert-injection process may be pulled out of the main body (11) without being hindered. A container as claimed in Claims 3 and 4, wherein: a grip portion (15) is formed on an outer surface at a lower end of the first formed member.

Inventors: ICHIKAWA TOORU, MOTEKI YOSHIJI, TANAKA YOJI, ICHIKAWA, TOORU, MOTEKI, YOSHIJI, TANAKA, YOJI, Tanaka, Yoji, Kabushiki Kaisha Polymer Systems
Applicants: HOSOKAWA YOKO KK, HOSOKAWA YOKO CO., LTD
Application year: 2000
Main classification: B65D33
IPC codes: B29C45, B05C17, B65D33, B65D83