Process for producing amorphous anisotropic melt-forming polymers having a high degree of stretchability and polymers produced by same

Abstract: Process for producing highly stretchable, amorphous anisotropic melt-forming polymers having recurring units derived from p-hydroxybenzoic acid, 6-hydroxy-2-naphthoic acid, at least one aromatic diacid and an aromatic diol and/or hydroxyamine component, at least a portion of which is 4,4'-biphenol, which comprises incorporating into such polymers recurring units derived from resorcinol and at least one additional monomer that provides the resulting polymer with selected meta linkages, wherein each of said recurring units is present in the polymer in specified amounts. The resulting polymer is especially suitable for use in multilayer laminates and bicomponent fibers.

Description: BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a process for producing highly stretchable amorphous anisotropic melt-forming polymers suitable for use in the production of a variety of shaped articles including films, fibers, and blow molded forms. This invention also relates to the polymers produced from the subject process, as well as to shaped articles made from such polymers. 2. Description of the Prior Art Anisotropic melt-forming polymers, also known as liquid crystalline polymers or "LCPs", are well known in the art. Anisotropic melt-forming polymers exhibit a parallel ordering of molecular chains in the melt phase and are also termed "thermotropic" liquid crystal polymers. Many of these materials are wholly aromatic in nature. Thermotropic polymers include aromatic copolyesters having recurring units derived from p-hydroxybenzoic acid, at least one aromatic diol and at least one aromatic dicarboxylic acid as well as wholly aromatic copolyesteramides having recurring units derived from p-hydroxybenzoic acid, at least one aromatic diol, at least one aromatic diacid, and aminophenol. Without the inclusion of recurring units that disrupt the crystalline structure, such polymers tend to have very high melting points, for example, 360°C and above, making them difficult to melt fabricate. Incorporation of recurring units that provide non-parallel or "kinky" linkages is a common means of lowering melting point. These kinky linkages include "meta"or 1,3- aromatic ring structures. Common materials from which meta linkages are derived include m-hydroxybenzoic acid, isophthalic acid, resorcinol, and m-aminophenol. U.S. Pat. Nos. 4,563,508; 5,037,939; and 5,066,767 disclose polymers containing recurring units derived from p-hydroxybenzoic acid, terephthalic acid, isophthalic acid, hydroquinone and 4,4'-biphenol; U.S. Pat. No. 4,912,193 discloses polymers having recurring units derived from p-hydroxybenzoic acid, 4,4'-biphenol, terephthalic acid and isophthalic acid; U.S. Pat. No. 4,966,956 discloses polymers having recurring units derived from p-hydroxybenzoic acid, terepthalic acid, isophthalic acid, 4,4'-biphenol and aminophenol; U.S. Pat. No. 5,663,276 discloses polymers having recurring units derived from p-hydroxybenzoic acid, terephthalic acid, 4,4'-biphenol, isophthalic acid, hydroquinone and 4,4'-biphenyldicarboxylic acid; U.S. Pat. No. 5,089,594 discloses polymers having recurring units derived from p-hydroxybenzoic acid, terephthalic acid, isophthalic acid, 4,4'-biphenol, and an aromatic diol, for example, hydroquinone; U.S. Pat. No. 4,722,993 discloses polymers having recurring units derived from m-aminophenol, p-hydroxybenzoic acid, terephthalic and/or isophthalic acid, one or more of hydroquinone, 4,4'-biphenol or resorcinol and, if desired, m-hydroxybenzoic acid; U.S. Pat. No. 5,399,656 discloses polymers having recurring units derived from p-hydroxybenzoic acid, terephthalic acid, resorcinol and an aromatic diol, for example, 4,4'-biphenol; U.S. Pat. No. 5,025,082, discloses polymers having recurring units derived from p-hydroxybenzoic acid, terephthalic acid, 4,4'-biphenol, 2,6-naphthalene dicarboxylic acid, and at least one aromatic diol selected from hydroquinone, methylhydroquinone, trimethylhydroquinone, resorcinol and tetramethylbiphenol; and U.S. Pat. No. 5,798,432 discloses polymers having requiring units derived from p-hydroxy benzoic acid, 2,6-naphthalene dicarboxylic acid, terephthalic acid, isophthalic acid, hydroquinone, p-aminophenol and 4,4'-biphenol. The presence of meta linkages notwithstanding, aromatic polymers derived from p-hydroxybenzoic acid, at least one aromatic dicarboxylic acid and at least one aromatic diol and/or aminophenol tend to have highly ordered crystalline structures and, although drawable in the melt, generally lack the ability to be stretched to a significant degree at temperatures below the molten state. Another class of thermotropic polymers have recurring units derived from p-hydroxybenzoic acid, 6-hydroxy-2-naphthoic acid, at least one aromatic diacid and at least one aromatic diol. The incorporation of meta linkages into such polymers is described, for example, in the following: U.S. Pat. No. 4,522,974 disclosing polymers having recurring units derived from p-hydroxybenzoic acid, 6-hydroxy-2-naphthoic acid, hydroquinone and isophthalic and/or terephthalic acid; U.S. Pat. No. 4,920,197 disclosing polymers having recurring units derived from p-hydroxybenzoic acid, 6-hydroxy-2-naphthoic acid, terephthalic acid, isophthalic acid and resorcinol; U.S. Pat. No. 4,937,310 disclosing polymers having recurring units derived from p-hydroxybenzoic acid, 6-hydroxy-2-naphthoic acid, terephthalic acid, isophthalic acid and resorcinol; U.S. Pat. No. 4,918,154 disclosing polymers having recurring units derived from p-hydroxybenzoic acid, 6-hydroxy-2-naphthoic acid, terephthalic and/or isophthalic acid, resorcinol and hydroquinone; and U.S. Pat. No. 4,983,713 disclosing polymers having recurring units derived from p-hydroxybenzoic acid, 6-hydroxy-2-naphthoic acid, terephthalic acid, 4,4'-biphenol, and isophthalic acid. The polymers set forth in the examples of these patents tend to have ordered crystalline structures and are not considered to be highly stretchable materials. More recent patents disclose liquid crystalline polymers that include amorphous materials. Example 5 of U.S. Pat. No. 5,525,700 is directed to what appears to be an amorphous polymer having recurring units derived from p-hydroxybenzoic acid, 6-hydroxy-2-naphthoic acid, hydroquinone, terephthalic acid, 4,4'-biphenol and 2,6-naphthalene dicarboxylic acid. Crystalline polymers derived from the same recurring units are also disclosed. In fact, of the numerous polymers exemplified by this patent, all but Example 5 are crystalline materials. Example 5 is not believed to be a highly stretchable polymer. U.S. Pat. No. 5,656,714 discloses amorphous and what are termed "semi-crystalline" polymers having recurring units derived from p-hydroxybenzoic acid, 6-hydroxy-2-naphthoic acid, terephthalic acid, 4,4'-biphenol, and resorcinol. Fibers made from the amorphous polymers of Examples I and IX were respectively reported to be drawn to 73 and 30 times their as-spun length. Apart from Examples I and IX, no additional data regarding the stretchability of the exemplified polymers is provided. The polymers exemplified by U.S. Pat. No. 5,656,714 vary in terms of their degree of crystallinity; some, but not all, of these polymers are highly stretchable. LCPs that are stretchable at lower temperatures have a diverse range of end-use applications. Amorphous LCPs having a Tg (i.e., onset of the glass transition temperature as measured by differential scanning calorimetry or "DSC") of 150°C or less that are highly stretchable at temperatures above Tg, but below the temperature at which the LCP is in the molten state, are of particular interest in the production of articles that are stretched, drawn or otherwise processed at lower temperatures. Liquid crystalline polymers that are stretchable at temperatures below the processing temperatures of conventional film-forming polymers such as, for example, polyolefins or polyalkylene terephthalates, for example, PBT or PET, may be particularly desirable for use in the production of multilayer articles such as films, laminates, blow-molded containers, and the like. In these multi-layer applications, the barrier, mechanical and/or optical properties of liquid crystalline polymers may provide advantages that are typically not obtained from conventional thermoplastics. EP 0 928 683 A2, published July 14, 1999, discloses a variety of multi-layer laminates, including laminates formed from wholly aromatic, liquid crystalline polymers of the type disclosed in U.S. Patent No. 5,656,714. A process for producing highly stretchable amorphous LCPs and the LCPs so produced are desired. SUMMARY OF THE INVENTION It now been found that in order to produce highly stretchable amorphous anisotropic polymers, it is necessary to provide the polymer with specific recurring units in narrowly defined amounts. In one embodiment, the present invention is directed to a process for forming highly stretchable, amorphous anisotropic melt-forming polymers which comprises incorporating recurring unit V consisting essentially of: in combination with at least one additional unit selected from the group consisting of: wherein R 1 is independently selected from the group consisting of hydrogen and C 1 to C 6 alkyl, into a polymer comprising recurring units I, II, III, and IV, wherein recurring unit I is recurring unit II is: recurring unit III is: wherein Ar 1 is selected from the group consisting of: and mixtures thereof; and recurring unit IV is: wherein Ar 2 is selected from the group consisting of: and mixtures thereof, and X is independently selected from the group consisting of O and NR 2 wherein R 2 is independently selected from the group consisting of hydrogen and C 1 to C 6 alkyl; to provide a polymer that consists essentially of from 15 to 60 mole percent of recurring unit I, from 15 to 60 mole percent of recurring unit II, from 5 to 20 mole percent of recurring unit III, from 5 to 20 mole percent of recurring unit IV, and from 7 to 15 mole percent of recurring unit V wherein: (a) recurring units I and II combined are present in the polymer an amount of from 50 to 75 mole percent, and (b) the polymer contains at least 5 mole percent of recurring units of the formula: with the proviso that recurring unit II is present in the polymer in an amount of at least 30 mole percent, if and when unit (Vc) is also present and units (Va), (Vb), (Vd) and (Ve) combined, constitute up to 5 mole percent of the polymer. In further embodiments this invention is directed to anisotropic melt-forming polymers produced in accordance with the process described in the immediately preceding paragraph as well as to stretched articles formed from such polymers. DETAILED DESCRIPTION OF THE INVENTION The process of this invention produces highly stretchable amorphous polymers. The polymers are considered to be amorphous in that they lack a well defined melting point or T m (i.e., a solid to nematic endothermic peak as measured by differential scanning calorimetry). Despite the absence of a classic melting point, the subject polymers possess a solid to nematic fluid transition temperature that defines their melt processability. Polymers produced in accordance with this invention are melt processable at temperatures below 270°C. Additionally, such polymers have T g values of 150°C or less. Preferably, the polymers have T g values of 130°C or less, most preferably 120°C or less. For co-extrusion applications with polyolefins, polymers that are melt processable at temperatures at or below 220°C are of particular interest. As noted above, the thermal properties of liquid crystalline polymers vary with composition. While almost all liquid crystalline polymers are stretchable in the melt, relatively few are stretchable at temperatures below which they are molten. The extent to which a polymer can be stretched or drawn depends upon the temperature at which stretching occurs as well as the form and size of the material that is being stretched. LCPs of the subject invention exhibit a percentage of break strain (herein also referred to as the polymer's degree of stretchability) of at least 100% at break point, when spun into tapes that are tested in accordance with the procedure set forth in the Examples below. Anisotropic melt-phase forming polymers formed by the present invention consist essentially of at least six different recurring units. Unit I of the subject polymers, termed a para-oxybenzoyl unit, possesses the structural formula: While not specifically illustrated in the structural formula, at least some of the hydrogen atoms present on the aromatic ring of unit I may be substituted. Included among the representative precursors from which recurring unit I may be derived are: 4-hydroxybenzoic acid; 3-chloro-4-hydroxybenzoic acid; 3-methyl-4-hydroxybenzoic acid; 3-methoxy-4-hydroxybenzoic acid 3-phenyl-4-hydroxybenzoic acid; 3,5-dichloro-4-hydroxybenzoic acid; 3,5-dimethyl-4-hydroxybenzoic acid; 3,5-dimethoxy-4-hydroxybenzoic acid; and the like. In a preferred embodiment, no ring substitution is present on recurring unit I. Recurring unit I is present in the polymers of the subject invention in an amount of from 15 to 60 mole percent, preferably from 20 to 40 mole percent. Recurring unit II of the subject polymers, termed a 6-oxy-2-naphthoyl unit, possesses the structural formula: As in the case of recurring unit I, at least some of the hydrogen atoms present on the aromatic ring structure of recurring unit II may be substituted. Exemplary of such substituents are alkyl groups of 1 to 4 carbon atoms, alkoxy groups of 1 to 4 carbon atoms, phenyl, halogen (e.g., Cl, Br, and I), and mixtures thereof. Representative of the precursors from which recurring unit II may be derived are aromatic hydroxy-naphthoic acids which include: 6-hydroxy-2-naphthoic acid; 6-hydroxy-5-chloro-2-naphthoic acid; 6-hydroxy-5-methyl-2-naphthoic acid; 6-hydroxy-5-methoxy-2-naphthoic acid; 6-hydroxy-5-phenyl-2-naphthoic acid; 6-hydroxy-7-chloro-2-naphthoic acid; 6-hydroxy-5,7-dichloro-2-naphthoic acid, and the like. In a preferred embodiment no ring substitution is present on recurring unit II. Recurring unit II is present in the subject polymers in an amount of from 15 to 60 mole percent, preferably from 20 to 40 mole percent, except when recurring unit V constitutes significant amounts of meta-oxybenzoyl units and little or no additional meta units, in which case unit II shall be present in an amount of from 30 to 60 mole percent. Additionally, recurring units I and II combined constitute from 50 to 75 mole percent, preferably 60 to 70 mole percent of the subject polymers. Recurring unit III of the subject polymers possesses the structural formula: wherein Ar 1 is a divalent radical selected from the group consisting of: and mixtures thereof. Although not specifically shown in the formula given, the aromatic ring structure of recurring unit III may be substituted in a manner similar to that described for recurring unit I. Preferably no ring substitution is present on recurring unit III. Representative of the precursors from which recurring unit III may be derived are aromatic diacids such as, for example, terephthalic acid, 2,6-naphthalene dicarboxylic acid, 4,4'-biphenyldicarboxylic acid, and the like. In a preferred embodiment no ring substitution is present on recurring unit III. Recurring unit III is present in the polymers of the subject invention in an amount of from 5 to 20 mole percent, preferably from 10 to 15 mole percent. In one embodiment of interest, recurring unit III consists of units of the formula: In another embodiment interest, recurring unit III consists of units of the formula: In yet another embodiment of interest, recurring unit III is selected from the group consisting of: and mixtures thereof. Recurring unit IV of the subject polymers, possesses the formula: wherein Ar 2 and X are as previously defined. Although not specifically illustrated in the structural formula given, the aromatic ring structure of recurring unit IV may be substituted in a manner similar to that described for recurring unit I. Representative of the precursors from which recurring unit IV may be derived are aromatic diols such as, for example, 4,4'-biphenol, hydroquinone, 2,6-naphthalene diol, p-aminophenol, and the like. Preferably, no ring substitution is present on recurring unit IV. Recurring unit IV is present in the polymers of the subject invention in an amount of from 5 to 20 mole percent, preferably from 10 to 15 mole percent. In the practice of this invention, the subject polymers contain at least 5 mole percent of recurring units of the formula: In one embodiment of particular interest recurring unit IV consists of units of the formula: In another embodiment of interest, recurring unit IV consists of a mixture of the following: Recurring unit V of the subject polymers comprises a dioxy unit of the formula: in combination with at least one additional dicarboxyl, oxyamino, oxycarboxyl, or aminocarboxyl unit selected from the group consisting of: wherein R 1 is independently selected from the group consisting of hydrogen and C 1 to C 6 alkyl. Although not specifically illustrated in the structural formulas given, the aromatic ring structure of recurring unit V may be substituted in a manner similar to that described for recurring unit I. Preferably no ring substitution is present on recurring unit V. In the practice of this invention, recurring unit V is present in the subject polymer in an amount of from 7 to 15 mole percent, preferably from 10 to 15 mole percent. The amount of recurring unit V made up of unit Va is variable. In one embodiment, recurring unit V contains up to 50 mole percent of unit Va; in other embodiments, recurring unit V contains up to 70 mole percent or more of unit Va. The choice of units comprising recurring unit V and the relative amounts of recurring unit V and the other constituent monomers are factors that affect the thermal properties, including melt processability and stretchability of the resulting polymers. When recurring unit V is a meta-dioxybenzene unit in combination with an isophthaloyl unit and/or a meta-oxybenzoyl unit: the resulting polymers tend to have T g values under 120°C. When recurring unit V is a meta-dioxybenzene unit: in combination with a meta-aminobenzyol unit: and/or an oxyaminobenzene unit: the resulting polymers may have higher T g values than similar polymers wherein recurring unit V consists of meta-dioxybenzene units in combination with isophthaloyl and/or meta-oxybenzoyl units. The solid to nematic transition temperature of polymers having esteramide linkages may also be increased, as well as the processing temperature thereof. When lower T g values are desired, recurring unit V preferably consists of meta-dioxybenzene units in combination with units selected from the group consisting of: and mixtures thereof. Meta-oxybenzoyl recurring units may not have as intense an effect on stretchability as meta-dioxybenzene or the other units that may comprise recurring unit V. When recurring unit V constitutes significant amounts of meta-oxybenzoyl units, and recurring units (Va), (Vb), (Vd), and (Ve) combined account for up to 5 mole percent of the polymer, a minimum of 30 mole percent of recurring unit II should also be present for the polymer to be highly stretchable. Minor amounts of other units that provide ester or ester-amide linkages may be present, provided, that such units do not obviate the properties desired by this invention. It will be apparent to those skilled in the art that the total amount of dioxy and oxy-amino units present in the subject polymers will be substantially equal to the total amount of dicarboxy units. In general, the various recurring units will be present in the resultant polymers in a random configuration. Preferably the polymers are wholly aromatic materials. The polymers formed by the process of this invention commonly exhibit a weight average molecular weight of from 10,000 to 80,000. The molecular weight of preference will depend, in part, on the intended end-use application. For example, in fiber and film applications, weight average molecular weights of from 20,000 to 40,000 are commonly of interest. The polymers typically exhibit an inherent viscosity (I.V.), measured at 25°C as a 0.1% by weight solution of polymer in a mixture of equal volumes of pentafluorophenol and hexafluoroisopropanol, of at least 1.0 dl/g, with polymers having inherent viscosities of from 3.0 dl/g to 7.0 dl/g being of particular interest. Characteristic of the subject polymers is the formation of an anisotropic melt phase. Thus, in the melt there is a tendency for the polymer chains to orient in the shear direction. Such thermotropic properties are manifest at a temperature which is amenable for melt processing to form shaped articles. Anisotropy in the melt may be confirmed by conventional polarized light microscopy techniques. The polymers of this invention are typically prepared by a polymerization reaction that proceeds through the acetate form of the hydroxycarboxylic acid, diol and, when present, hydroxyamine and aminocarboxylic acid reactants. Thus, it is possible to employ as starting materials reactants having pre-acetylated hydroxyl groups and amino groups, heat the reaction mix to polycondensation temperature and maintain reaction until a desired polymer viscosity is reached. Alternatively, it is possible to acetylate in situ, in which case the aromatic hydroxycarboxylic acid, aromatic diol and, when present, hydroxyamine and aminocarboxylic acid are reacted with acetic anhydride, acetic acid by-product is removed, the esterified reactants together with the aromatic diacid are heated to polycondensation temperature, and reaction is maintained until a desired polymer viscosity is reached. The aromatic diacid reactant may, but need not, be present during the acetylation reaction. If the acetylation and polycondensation reactions are conducted in a single reactor, it is common to charge the reactor with the reactant materials in a single step. Using separate acetylation and polymerization reactors, it may be desirable to introduce the diacid component to the polymerization reactor as opposed to the acetylation reactor. The acetylation and polycondensation reactions are typically conducted in the presence of suitable catalysts. Such catalysts are well known in the art and include, for example, alkali and alkaline earth metal salts of carboxylic acids, such as, for example, potassium acetate, sodium acetate, magnesium acetate, and the like. Such catalysts are typically used in amounts of from 50 to 500 parts per million based on the total weight of the recurring unit precursors. Acetylation is generally initiated at temperatures of about 90°C. In the initial stage of the acetylation reflux is desirably employed to maintain vapor phase temperature below the point at which acetic acid byproduct and anhydride begin to distill. Temperatures during the initial stage of acetylation typically range from between 90° to 150°C, preferably 100° to 130°C. In order to complete the acetylation, the reaction mixture is then heated to final melt temperature of about 150° to 220°C, preferably 150° to 200°C, with temperatures of 180° to 200°C being of particular interest. At this point, if reflux is used, the vapor phase temperature should exceed the boiling point of acetic acid but remain low enough to retain residual acetic anhydride. To ensure substantially complete reaction, it may be desirable to utilize an excess amount of acetic anhydride in conducting the acetylation. The amount of excess anhydride utilized will vary depending upon the particular acetylation conditions employed, including the presence or absence of reflux. The use of an excess of from 1 to 10 mole percent of acetic anhydride, based on the total moles of reactant hydroxyl groups present is not uncommon. To obtain both complete acetylation and maintenance of stoichiometric balance, anhydride loss should be minimized. Acetic acid vaporizes at temperatures of about 118°C. At higher temperatures, i.e., about 140°C acetic anhydride also begins to vaporize. Providing the reactor with a means of controlling vapor phase reflux is desirable. Maintaining vapor phase reflux temperature at 120° to 130°C is particularly desirable. Polycondensation of the acetylated starting materials generally begins to take place at a temperature within a range of from 210° to 260°C. As acetic acid is also a byproduct of the polymerization reaction, it is desirable to employ controlled vapor phase reflux when conducting the polycondensation reaction. In the absence of controlled vapor phase reflux, acetic anhydride, acetoxybenzoic acid and other volatile materials are vaporized as the polymerization temperature is increased. Depending on the particular polymer synthesized, it is preferable to maintain vapor phase reflux temperatures of 120° to 130°C during the polymerization reaction. As the final polymerization temperature is approached, volatile byproducts of the reaction having boiling points above that of acetic acid and acetic anhydride should be removed. Accordingly, at reactor temperatures of 250° to 300°C, vapor phase reflux, if used, is generally adjusted to allow higher vapor phase temperatures or is discontinued. The polymerization is generally allowed to proceed until a desired polymer viscosity is reached. To build molecular weight in the melt, the polymerization reaction is generally conducted under vacuum, the application of which facilitates the removal of volatiles formed during the final stage of the polycondensation. Following polymerization, the molten polymer is discharged from the reactor, typically through an extrusion orifice fitted with a die of desired configuration; cooled; and collected. Commonly, the melt is discharged through a perforated die to form strands which are taken up in a water bath, pelletized and dried. In an embodiment of particular interest this invention is directed to highly stretchable, amorphous anisotropic melt-forming polymers consisting essentially of recurring units I, II, III, IV and V, wherein recurring unit I is recurring unit II is: recurring unit III is: wherein Ar 1 is selected from the group consisting of: and mixtures thereof; recurring unit IV is: wherein Ar 2 is selected from the group consisting of: and mixtures thereof; and recurring unit V consists of: in combination with at least one of the following: wherein R 1 is independently selected from the group consisting of hydrogen and C 1 to C 6 alkyl; wherein said polymer contains from 20 to 40 mole percent of recurring unit I, from 20 to 40 mole percent of recurring unit II, from 10 to 15 mole percent of recurring unit III, from 10 to 15 mole percent of recurring unit IV, and from 10 to 15 mole percent of recurring unit V and wherein: (a) recurring units I and II combined are present in the polymer in an amount of from 60 to 70 mole percent, (b) the polymer contains at least 5 mole percent of recurring units of the formula: and (c) the polymer contains at least 5 mole percent of recurring units of the formula: In another embodiment of particular interest this invention is directed to highly stretchable, amorphous anisotropic melt-forming polymers consisting essentially of recurring units I, II, III, IV and V, wherein recurring unit I is recurring unit II is: recurring unit III is: recurring unit IV is: and recurring unit V consists of a mixture of : and wherein said polymer contains of from 30 to 35 mole percent of recurring unit I, from 30 to 35 mole percent of recurring unit II, from 10 to 15 mole percent of recurring unit III, from 10 to 15 mole percent of recurring unit IV, and from 10 to 15 mole percent of recurring unit V. Although the polymers produced by the process of this invention are particularly well suited for extrusion and co-extrusion applications such as the production of fiber, film, sheet, blow molded articles and the like, they may also be used in the production of injection molded parts. If desired, compositions containing the subject polymers may contain one or more additional optional components such as for example, colorants, lubricants, processing aids, stabilizers, fillers, reinforcing agents, and the like. Fillers and reinforcing agents are not typically present in compositions used in fiber and film applications. Due to their ability to be stretched at relatively low temperatures, the subject polymers are particularly well suited for use as barrier layers in the production of multilayer laminates, in particular blown films and containers, allowing fabricators to orient conventional thermoplastics used in the multilayer films for better strength and to obtain better oxygen and moisture barrier resistance with a thinner barrier layer made from the subject LCPs. Blown films and containers of interest include multilayer laminates having a polyolefin/barrier layer/polyolefin structure, wherein one or more intermediate layers, such as adhesive layers, are optionally interposed between the barrier and polyolefin layers. Polyolefins commonly used in such multilayer laminates are polyolefin homopolymers and copolymers, for example polyethylene, polypropylene, ethylene vinyl acetate, and the like. The polyolefin of choice varies depending upon the end-use application of interest. In addition, an adhesive layer may also be used to adhere the polyolefin to the LCP. Any suitable adhesive material may be used as the adhesive layer, including but not limited to, ethylene-maleic anhydride copolymer, ethylene-methyl acrylate copolymer, ethylene-methyl acrylate copolymer grafted with maleic anhydride, ethylene-methyl acrylate-maleic acid terpolymer, ethylene-glycidyl methacrylate copolymer, ethylene-methyl acrylate-glycidyl methacrylate terpolymer, ethylene-methyl methacrylate-acrylic acid terpolymer, ethylene-vinyl acetate copolymer, an alkoxysilane modified ethylene-ethylacrylate copolymer, ethylene-acrylic acid copolymer, and a blend of polypropylene grafted with maleic anhydride with a dimer based polyamide. Also of interest are multilayer laminates made with polyesters such as those having a polyalkylene terephthalate/barrier layer/polyalkylene terephthalate structure, where one or more intermediate layers are optionally interposed between the barrier and polyester layers. Polyalkyene terephthalates of particular interest in the production of such laminates include polyethylene terephthalate and polybutylene terephthalate. Also, an adhesive layer may be used to adhere the polyester to the LCP. Any suitable adhesive material may be used as the adhesive layer, including but not limited to polyester polyurethane, polyether polyurethane, polyester elastomer, and a polyether elastomer. Another thermoplastic that may also be used as a layer with the subject polymer are polyamides such as nylon. In multilayer laminates, the thickness of the barrier layer will typically range from 1 to 25 microns, depending upon the particular end use application. A major advantage of these laminates is that they can be stretched at temperatures typically used to stretch conventional thermoplastics (e.g., 120°C to 160°C). The stretching of the laminate orients the conventional thermoplastic polymer and improves the strength of the laminate. Conventional LCPs are typically not used in oriented multilayer laminates because of their inability to be stretched well below their molten state. One application for which stretchable liquid crystal polymers are especially suitable is the production of fibers such as monofilaments, multifilaments and bicomponent fibers using conventional fiber forming equipment. Particularly, stretchable liquid crystal polymers may be used as at least one component in a bicomponent fiber. Bicomponent fibers are well known and may be defined as a fiber having at least two distinct cross-sectional domains respectively formed from polymers having different relative viscosities. The distinct domains may be formed by at least two different polymers, or the same polymer class having different relative viscosities. Bicomponent fibers are intended to include, but are not limited to core and sheath fiber structures, side by side fiber structures, tipped fiber structures, micro-denier structures and mixed fiber structures. These types of bicomponent fiber structures are described in U.S. Patent No. 6,074,590, herein incorporated by reference. The stretchable liquid crystal polymers disclosed in the present application are well suited to be used as one of the components in bicomponent fibers because of their ability to be stretched at temperatures used in a post extrusion orientation process. Bicomponent fibers using conventional thermoplastics are stretched in a post extrusion orientation process to orient the polymer and improve the strength of the fiber. Conventional liquid crystal polymers can not be used as one of the components in bicomponent fibers in a post orientation process because they can not be stretched at temperatures used to stretch conventional thermoplastics. Any suitable type of fiber forming polymer may be used as one of the other components in the bicomponent fiber. Suitable classes of polymers that may be used, include but are not limited to polyamides, polyesters, acrylics, and polyolefins. Specifically, nylon, low and high density polyethylene, polypropylene and polyethylene terephthalate may be employed as one of the other components in a bicomponent fiber. The bicomponent fibers are spun using conventional fiber-forming processes and equipment such as those described in U.S. Patent Nos. 6, 074,590; 5,948,528; 5,618,479; 5,162,074; 5,125,818; 5,344,297 and 5,445,884, herein incorporated by reference. Basically, spinning of bicomponent fibers involves co-extrusion of the two or more components to form single filaments in which the different components are brought together in a desired predetermined configuration. As mentioned previously, the stretchable liquid crystal polymers may be used as any component in the bicomponent fiber. For example, in a core and sheath fiber, the stretchable liquid crystal polymer could be used as either the core or the sheath component. One such example would have the stretchable, liquid crystal polymer as the core and polyethylene terephthalate as the sheath. The stretchable liquid crystal polymer core component would contribute high modulus and tenacity at room temperatures. Another example would have the stretchable liquid crystal polymer as the sheath and polyethylene terephthalate as the core to improve harsh environment resistance capabilities because of the superior barrier properties of the stretchable liquid crystal polymer. EXAMPLES The following examples are presented to further illustrate this invention. The examples are not, however, intended to limit the invention in any way. Examples 1 to 2 and Comparative Examples C 1 and C 2 To a 3-necked cylindrically shaped flask equipped with a stainless steel "C"-shaped agitator, gas inlet tube, thermocouple, distilling trap and Vigreux column attached to a condenser and receiver were added: 248.4 grams p-hydroxybenzoic acid 338.4 grams 6-hydroxy-2-naphthoic acid 149.4 grams of terephthalic acid 167.4 grams of 4,4'-biphenol 49.8 grams of isophthalic acid 33.0 grams of resorcinol 632.9 grams of acetic anhydride 0.12 grams of potassium acetate (60 ppm) The flask was purged of oxygen by evacuation and flushing with dried nitrogen and immersed into an electrically heated fluidized sand bath. The contents of the flask were heated to ~150°C while stirring at 75 rpm to acetylate hydroxyl groups. Temperature was raised from 150° to 220°C over a period of 70 minutes to distill by-product acetic acid. Polymerization commenced at 220°C and batch temperature was raised to 340°C over a period of 130 minutes. During this time acetic acid that evolved was removed by distillation. After a 30 minute hold time at 340°C, vacuum was applied and the pressure gradually reduced to -5mm Hg over a period of 20 minutes. The vacuum was maintained until the torque required to maintain agitator speed reached the target value necessary to give the desired melt viscosity. At the target torque the vacuum was discontinued and the flask brought to atmospheric pressure with dry nitrogen. This process produced a polymer having an inherent viscosity (I.V.) of 3.8 dl/g, measured at 25°C as a 0.1% by weight solution of polymer in a mixture of equal volumes of pentafluorophenol and hexafluoroisopropanol. The melt viscosity (M.V.) was ∼1500 poise at a shear rate of 1000 sec -1 , measured at 270°C in a capillary rheometer using an orifice 1mm in diameter and 20mm long. DSC (20°C/min. heating rate) indicated that the polymer had a Tg of 109°C. Additional polymers were made and tested following a similar procedure. Table 1 lists the various Examples and Comparative Examples together with the mole percentges of the reactant monomers employed. Abbreviations are as follows: "p-HBA" means p-hydroxybenzoic acid; "HNA" means 6-hydroxy-2-naphthoic acid; "TA" means terephthalic acid; "BP" means 4,4'-biphenol; "IA" means isophthalic acid; "m-AP" means m-aminophenol (as m-actamidophenol); and "R" means resorcinol. All polymerizations were conducted in the presence of 60 ppm potassium acetate, using sufficient acetic anhydride to completely acetylate the hydroxyl groups present. Hot stage microscopy with polarized light confirmed that all of the polymers were optically anisotropic. The polymers contained molar quantities of recurring units that corresponded to the molar charge of the reactant monomers. I.V., M.V. and T g data for the polymers (measured as described above) are reported in Table 2. Excluding C 1 , the polymers were amorphous. Example REACTANT MONOMERS (Mole %) p-HBA HNA TA BP R IA m-AP 1 30 30 15 15 5 5 -- 2 30 30 20 10 5 -- 5 C 1 30 30 15 20 5 -- -- C 2 30 30 15 20 -- 5 -- The polymers were melt spun into tapes using a Micromelt ™ apparatus. The apparatus was equipped with a 0.127mm by 6.35mm die. Melt temperatures varied between about 270-300°C depending upon the melt characteristics of the sample. Throughput rates were 0.45cc/min; take-up roller speeds were 2 rpm; and pack pressures ranged from about 140 kg/cm 2 to about 290 kg.cm 2 , depending upon the T g (or T m ) of the polymer. The resulting tapes had an approximate thickness of 0.05mm and a width of about 6mm. Five test specimens, each 12.7cm in length were cut from each tape. The thickness of the specimens was measured to the nearest 0.0025mm and the width to the nearest 0.25mm. Each specimen was placed in a preheated Instron oven, allowed 6 minutes to come to temperature and then tested on an Instron type universal tester (equipped with a thermal chamber), set to a test temperature of 150°C. The gauge length was set at 25mm and the crosshead speed was set at 50.8mm/min. The % break strain was calculated at the break point. The % break strain is reported in Table 2 as the average of the data for the five specimens tested. Standard deviations are also provided. TESTING DATA EXAMPLE I.V. (dl/g) M.V. (poise) BREAK STRAIN, % Avg./Std. Dev. TEST TEMP. (°C) Tg (°C) 1 3.8 1507 240/60 150 109 2 3.1 2351 200/70 150 121 C 1 9.5 2592 2.3/0.2 150 Tm of 250°C C 2 6.7 1899 20/10 150 115

Claims: A liquid crystal polymer consisting essentially of recurring units I, II, III, IV and V wherein recurring unit I is recurring unit II is: recurring unit III is: wherein is Ar 1 is selected from the group consisting of: and mixtures thereof; recurring unit IV is: wherein Ar 2 is selected from the group consisting of: and mixtures thereof, and X is independently selected from the group consisting of O and NR 2 wherein R 2 is independently selected from the group consisting of hydrogen and a C 1 to C 6 alkyl; and recurring unit V is a dioxy unit of the formula: in combination with at least one additional unit selected from the group consisting of: wherein R 1 is independently selected from the group consisting of hydrogen and C 1 to C 6 alkyl, wherein recurring unit I is present in the polymer in an amount of from 15 to 60 mole percent, recurring unit II is present in the polymer in an amount of from 15 to 60 mole percent, recurring unit III is present in the polymer in an amount of from 5 to 20 mole percent, recurring unit IV is present in the polymer in an amount of from 5 to 20 mole percent, and recurring unit V is present in the polymer in an amount of from 7 to 15 mole percent and wherein: (a) recurring units I and II combined are present in the polymer in an amount of from 50 to 75 mole percent and (b) the polymer contains at least 5 mole percent of recurring units of the formula: with the proviso that recurring unit II is present in the polymer in an amount of at least 30 mole percent, if and when unit (Vc) is also present and the units (Va), (Vb), (Vd) and (Ve) combined, constitute up to 5 mole percent of the polymer. A polymer as defined in claim 1 which is a highly stretchable, amorphous anisotropic melt-forming polymer. A polymer as described in claim 1 or claim 2 wherein recurring unit V consists of: in combination with at least one of: A polymer as described in any one of the preceding claims wherein recurring unit V consists of: in combination with: A polymer as described in any one of the preceding claims wherein recurring unit V is present in the polymer in an amount of from 10 to 15 mole percent. A polymer as described in any one of the preceding claims wherein recurring unit IV is A polymer as described in any one of the preceding claims wherein recurring unit III is selected from the group consisting of: and mixtures thereof. A polymer as described in any one of the preceding claims wherein recurring unit III is A polymer as described in any one of the preceding claims wherein recurring unit IV is and recurring unit III is The polymer of any one of the preceding claims wherein recurring unit III is recurring unit IV is and recurring group V has the formula (Va) in combination with the formula selected from the group consisting of: (Vb), (Vc), and mixtures thereof. A polymer as described in any one of the preceding claims wherein recurring unit I is present in the polymer in an amount of from 30 to 35 mole percent, recurring unit II is present in the polymer in an amount of from 30 to 35 mole percent, recurring unit III is present in the polymer in an amount of from 10 to 15 mole percent, recurring unit IV is present in the polymer in an amount of from 10 to 15 mole percent, and recurring unit V is present in the polymer in an amount of from 10 to 15 mole percent. A polymer as described in any one of the preceding claims wherein V consists of: in combination with: A highly stretchable, amorphous anisotropic melt-forming polymer as defined in any one of the preceding claims consisting essentially of recurring units I, II, III, IV and V, wherein recurring unit I is recurring unit II is: recurring unit III is: wherein is Ar 1 is selected from the group consisting of: and mixtures thereof; recurring unit IV is: wherein Ar 2 is selected from the group consisting of: and mixtures thereof; and recurring unit V consists of: in combination with at least one additional unit selected from the group consisting of: wherein R 1 is independently selected from the group consisting of hydrogen and C 1 to C 6 alkyl, wherein said polymer contains from 20 to 40 mole percent of recurring unit I, from 20 to 40 mole percent of recurring unit II, from 10 to 15 mole percent of recurring unit III, from 10 to 15 mole percent of recurring unit IV, and from 10 to 15 mole percent of recurring unit V and wherein: (a) recurring units I and II combined are present in the polymer in an amount of from 60 to 70 mole percent, (b) the polymer contains at least 5 mole percent of recurring units of the formula: and (c) the polymer contains at least 5 mole percent of recurring units of the formula: A highly stretchable, amorphous anisotropic melt-forming polymer as defined in any one of the preceding claims consisting essentially of recurring units I, II, III, IV and V, wherein recurring unit I is recurring unit II is: recurring unit III is: recurring unit IV is: and recurring unit V consists of a mixture of : and wherein said polymer contains from 30 to 35 mole percent of recurring unit I, from 30 to 35 mole percent of recurring unit II, from 10 to 15 mole percent of recurring unit III, from 10 to 15 mole percent of recurring unit IV, and from 10 to 15 mole percent of recurring unit V. A shaped article produced from the polymer of any one of the preceding claims. A fiber formed from the polymer of any one of claims 1 to 14. A film formed from the polymer of any one of claims 1 to 14. A multilayer laminate comprising a layer of a thermoplastic and a layer of the polymer of any one of claims 1 to 14. The laminate of claim 18 wherein recurring unit I is present in the amount of from 30 to 35 mole percent, recurring unit II is present in the amount of from 30 to 35 mole percent, recurring unit III is present in the amount of from 10 to 15 mole percent, recurring unit IV is present in the amount of from 10 to 15 mole percent, and recurring unit V is present in the amount of from 10 to 15 mole percent. The laminate of claim 18 or claim 19 wherein recurring unit III is recurring unit IV is and recurring group V has the formula (Va) in combination with the formula selected from the group consisting of : (Vb), (Vc), and mixtures thereof. The laminate of any one of claims 18 to 20 further comprising an adhesive layer, wherein said adhesive layer is made from materials selected from the group consisting of: ethylene-maleic anhydride copolymer, ethylene-methyl acrylate copolymer, ethylene-methyl acrylate copolymer grafted with maleic anhydride, ethylene-methyl acrylate-maleic acid terpolymer, ethylene-glycidyl methacrylate copolymer, ethylene-methyl acrylate-glycidyl methacrylate terpolymer, ethylene-methyl methacrylate-acrylic acid terpolymer, ethylene-vinyl acetate copolymer, an alkoxysilane modified ethylene-ethylacrylate copolymer, ethylene-acrylic acid copolymer, a blend of polypropylene grafted with maleic anhydride with a dimer based polyamide polyester, a polyurethane, a polyether polyurethane, a polyester elastomer, and a polyether elastomer. The laminate of claim 21 wherein said thermoplastic is selected from the group consisting of: polyethylene, polypropylene, ethylene vinyl acetate, nylon and polyalkylene terephthalate. The laminate of any one of claims 18 to 22 wherein said laminate is stretched at a temperature of from about 120°C to about 160°C. A bicomponent fiber formed from the polymer of any one of claims 1 to 17. The bicomponent fiber of claim 24 wherein said fiber has a structure selected from the group consisting of: core and sheath fiber structure, side by side fiber structure, tipped fiber structure, micro-denier structure and mixed fiber structures. The bicomponent fiber of claim 24 or claim 25 wherein one of the components is selected from the group consisting of: nylon, low or high density polyethylene, polypropylene and polyethylene terephthalate. The bicomponent fiber of any one of claims 24 to 26 wherein said fiber is stretched. A process for forming highly stretchable, amorphous anisotropic melt-forming polymers which comprises incorporating recurring unit V consisting essentially of: in combination with at least one additional unit selected from the group consisting of: wherein R 1 is independently selected from the group consisting of hydrogen and C 1 to C 6 alkyl, into a polymer comprising recurring units I, II, III, and IV, wherein recurring unit I is recurring unit II is: recurring unit III is: wherein is Ar 1 is selected from the group consisting of: and mixtures thereof; and recurring unit IV is: wherein Ar 2 is selected from the group consisting of: and mixtures thereof, and X is independently selected from the group consisting of O and NR 2 wherein R 2 is independently selected from the group consisting of hydrogen and C 1 to C 6 alkyl; to provide a polymer that consists essentially of from 15 to 60 mole percent of recurring unit I, from 15 to 60 mole percent of recurring unit II, from 5 to 20 mole percent of recurring unit III, from 5 to 20 mole percent of recurring unit IV, and from 7 to 15 mole percent of recurring unit V and wherein: (a) recurring units I and II combined are present in the polymer in an amount of from 50 to 75 mole percent, and (b) the polymer contains at least 5 mole percent of recurring units of the formula: with the proviso that recurring unit II is present in the polymer in an amount of at least 30 mole percent, if and when unit (Vc) is also present and units (Va), (Vb), (Vd) and (Ve) combined, constitute up to 5 mole percent of the polymer.

Inventors: CANGIANO DOMINICK LOUIS, DEMARTINO RONALD NICHOLAS, KUDER JAMES EDGAR, LINSTID HENRY CLAY III, PROVINO VINCENT JAMES, CANGIANO, DOMINICK LOUIS, DEMARTINO, RONALD NICHOLAS, KUDER, JAMES EDGAR, LINSTID, HENRY CLAY, III, PROVINO, VINCENT JAMES
Applicants: TICONA LLC
Application year: 2000
Main classification: C08G63
IPC codes: D01F6, C08G63, D01F8, B32B27, C08J5, C08G69