Coating of membranes for medical devices

Abstract: The invention provides a coating for microporous hollow fibre membrane blood oxygenators which is capable of increasing the resistance of the fibres to passage of blood plasma through the micropores. The coating comprises an alkoxysilane/alkylsilane copolymer, preferably an aminoalkylsiloxane.

Description: This invention relates to medical devices, such as polyvinylchloride (PVC) tubing and oxygenators that use hollow fibre membranes to replace carbon dioxide in the blood with oxygen. In particular, the invention relates to an alkoxysiloxane/alkylsiloxane copolymer coating capable of reducing the migration of plasma across micropores in such membranes. Microporous hollow fibre membrane oxygenators are commonly used to support patients during heart bypass procedures such as cardiac artery bypass grafting (CABG), heart valve repair and replacement, and the like. Such oxygenators are designed to direct blood flow over (or through) the microporous hollow fibres while oxygen-rich gas flows through (or over) the fibre lumens. This results in simultaneous mass transfer of molecular oxygen and carbon dioxide in opposite directions across the membrane. The efficiency of the device can be described by the gas transfer per unit area of membrane at a given blood flow rate, gas flow rate, and composition (i.e. the specific gas transfer rate, typically cm 3 of gas per litres of blood flow per minute per square metre of gas transfer area). The micropores in the microporous hollow fibres are small enough to prevent whole-blood components such as platelets and red cells from passing through to the gas side of the membrane. However, the materials used to manufacture the fibre (polypropylenes, polyethylenes) are not primarily designed for blood compatibility. Both platelets and leukocytes adhere in great numbers to the materials, leading to significant activation of deleterious responses in the blood. Several coating methods have been used to improve blood compatibility by providing an additional layer or "second skin" for the underlying structural material comprising the fibre membrane. The added layer of material provides a blood-surface interaction superior to that seen for the bulk fibre materials. For example, heparin is known to have good blood compatibility properties and has been used as a coating on several commercialized products. Unfortunately, heparin-based coatings are inherently expensive and complex due to the use of sodium heparin, a complex, costly and fragile biologically derived substance. The Carmeda Bioactive Surface (Medtronic, Inc.) uses a polymer primer coat followed by covalent attachment of heparin to primary amino groups present in the primer coat. The Duraflo Bonded Heparin Surface (Baxter, Inc.) uses a heparin-polymer blend-based coating that is intended to achieve similar results. Other heparin-based coatings intended to improve blood compatibility are available from other medical device manufacturers (Terumo, Jostra, 3M Sarns, etc.). Silicone (polydimethyl siloxane-based resins) is known to be compatible with blood. A process commercialized by Cobe Laboratories, Inc. uses a block copolymer polymer additive/coating that is intended to decrease platelet and leukocyte adhesion/activation. Another problem is that, over time, the fluid component of blood (plasma) can migrate through the pores, a problem known as plasma migration or plasma breakthrough. In the case of a design in which the blood flows over the fibres and the oxygen-rich gas flows within the fibre lumens, this migration will eventually render the device inoperable by filling the lumens with liquid that impedes gas flow. Reducing the average pore size can increase the time to failure somewhat. This is the approach taken in a fibre commercially available from Hoescht-Celanese and known under the tradename of Plasma Resistant Fibre or PRF. Further improvement is desirable. One approach to the problem has been to use nonporous silicone membrane oxygenation systems. While no plasma can migrate through the membrane, gas transfer is very poor compared to that of microporous hollow fibre membrane oxygenators due to gas diffusion limitations through the solid polymer material. Another approach to improving plasma breakthrough performance is to modify the microporous hollow fibre membrane. Previous coating methods have attempted to close off the pores with a thin film of silicon resin, mechanically preventing fluid migration. Specific gas transfer rates are improved compared to silicon membrane oxygenators, but are still well below the rates found in uncoated microporous hollow fibre membrane devices. Another approach is the use of chemical vapour deposition (CVD) to deposit various coatings such as silicone resins on devices (e.g. Thoratec, InnerDyne). This approach suffers from poor specific gas transfer and also uses costly, toxic reagents. In addition, the CVD method is difficult to apply to the internal surfaces of finished products. Biocompatibles, Inc. has a process for applying a phosphatidyl choline-methacrylate/butyl methacrylate copolymer that is intended to improve blood compatibility. BioInteractions, Inc. has a hydrogel/heparin mixture that is also intended to improve blood compatibility of blood oxygenators. WO91/15952 describes thrombo-resistant coatings for use with gas permeable biomedical devices and implants. The coatings comprise an amine-containing siloxane surface which is reacted with poly(ethylene oxide) chains which themselves are in turn coupled to bioactive molecules capable of counteracting a blood-material incompatibility reaction. US-A-4923679 describes hollow fibre membrane type oxygenators having micropores which are filled with a silicone compound, for example a polymer of vinylmethylsiloxane units and methylhydrogensiloxane units. A need exists for alternative methods of preventing plasma breakthrough in medical devices, such as PVC tubing and oxygenators, which use hollow fibre membranes to replace carbon dioxide in the blood with oxygen. Surprisingly, the applicants have found that this need can be met by the use of a coating comprising an alkoxysiloxane/alkylsiloxane copolymer. Viewed from one aspect the invention thus provides a medical device comprising a microporous hollow fibre membrane having a plurality of micropores, in which the membrane is provided with a coating comprising an alkoxysiloxane/alkylsiloxane copolymer. Preferably, the membrane is coated with an alkoxysiloxane/alkylsiloxane copolymer to an extent sufficient to reduce migration of plasma across micropores in the membrane. Viewed from a further aspect the invention provides a method of coating a device comprising a microporous hollow fibre membrane, said method comprising the steps of: (a) formulating a coating solution comprising an alkoxysiloxane/alkylsiloxane copolymer; (b) contacting said device with the coating solution whereby to form a film of silicone on said membrane; and (c) curing the copolymer on the device. The device may be polyvinylchloride (PVC) tubing, any device comprising microporous hollow fibre membranes (such as blood oxygenators), or any other medical device which is prone to the plasma migration or plasma breakthrough problem. The coating compound of the invention comprises alkoxysiloxane/alkylsiloxane copolymers, preferably aminoalkylsiloxane, and most preferably the aminoalkylsiloxane commercially available from Dow Corning under the designation MDX4-4159 (see, for example, http://www.factor2.com/a-4159.htm). One of the key aspects of the invention is that it uses a siloxane material that cures in-place under very mild conditions. This is due to the use of an alkoxysiloxane/alkylsiloxane copolymer as mentioned above. The material cures via cross-linking of the alkoxysiloxane groups with each other, which occurs at room temperature in the presence of a trace amount of water as catalyst. The method of coating the medical device creates a thin film of silicone on the device (including the microporous fibres of the device), but does not cover or fill the micropores with the thin film. The improved resistance to plasma breakthrough (i.e. increased time to device failure) is achieved instead by changing the surface of the fibre polymer near the pore opening to better resist the intrusion of plasma. The prepolymer is applied as a thin film via solvent; after the solvent carrier evaporates away, the prepolymer cures to a soft resin layer completely covering the treated surface. All blood contact occurs with the silicon resin rather than with the underlying material. The result is a device with significantly greater time to failure for plasma breakthrough with specific gas transfer rates almost unchanged compared to identical uncoated devices. The process is also economically attractive, easier to implement, avoids toxic reagents, and can be used with a wider variety of finished products. Preferred embodiments of the invention will now be described with reference to the accompanying Figures in which: Figure 1 is a perspective view of a blood oxygenator constructed in accordance with this invention. Figure 2 is an exploded isometric view of a blood oxygenator constructed in accordance with this invention. Figure 3 is a side elevation view of the assembled blood oxygenator of Figure 2. Figure 4 is a top plan view of the blood oxygenator of Figure 3. Figure 5 is a diagrammatic view illustrating the blood, heat transfer fluid and gas mixture flow paths of the blood oxygenator of Figures 2-4. Figure 6 is a diagrammatic view illustrating the fabrication of the oxygenator fibre bundle of the blood oxygenator of Figures 2-5. Figure 7 is a diagrammatic view of the heat exchanger fibre bundle of the blood oxygenator of Figures 2-5. Figure 8 is an enlarged side elevation view of the spindle of the heat exchanger of the blood oxygenator around which is wound the micro-conduit wrapping material. Figure 9 is a cross-section view of the spindle of Figure 8 taken along line 9-9 of Figure 8. Figure 10 is an end elevation view of the spindle of Figure 8 taken from the right end of Figure 8. Figure 11 is a side detail view of polymeric micro-conduit material suitable for construction of the bundle of Figure 7. Figure 12 is a magnified side detail view of a portion of the polymeric micro-conduit material of Figure 11. Figure 13 is a top plan view of the lower venous gas header of the blood oxygenator. Also visible in this figure are the inner heat exchanger housing, the water inlet nozzle, the water outlet nozzle and the gas mixture outlet nozzle. Figure 14 is a sectional view of the lower venous gas header and inner heat exchanger housing taken along line 14-14 of Figure 13. Figure 15 is a sectional view of the lower venous gas header and inner heat exchanger housing taken along line 15-15 of Figure 13. Figure 16 is a front elevation view of the lower venous gas header and inner heat exchanger housing of the blood oxygenator. Figure 17 is a side elevation view of the lower venous gas header and inner heat exchanger housing of the blood oxygenator. Figure 18 is an enlarged vertical sectional view of the lower venous gas header and the inner heat exchanger housing with the blood inlet manifold connected. Also illustrated in this view is the micro-conduit fibre bundle of the heat exchanger. Figure 19 is a flowchart showing the process steps of a protocol for practising an embodiment of the invention. Commercially available examples of oxygenators employing microporous hollow fibre membranes for blood/gas exchange include the AFFINITY brand and MAXIMA FORTÉ brand oxygenators available from Medtronic Perfusion Systems, Medtronic, Inc. of Minneapolis, Minnesota, USA (see US Patents Re. 36,125, 5,462,619, and 5,346,621 for the AFFINITY brand oxygenator; and US Patents 5,858,233, 5,823,987, 5,762,875, and 5,718,871 for the MAXIMA FORTÉ brand oxygenator). Dow Corning MDX4-4159 Fluid 50% Medical Grade Dispersion is a liquid RTV solution containing 50 percent active silicone ingredients in mixed aliphatic and isopropanol solvents. The active silicone used is an aminofunctional dimethylsiloxane copolymer. The polar nature of the aminofunctional groups and the ability of the fluid to cure cause films to deposit and adhere to metal cutting edges, such as razor blades. The primary known use of MDX4-4159 is dipping, coating and spraying devices to create a thin layer of silicone for lubrication. The most general expression of the alkoxysiloxane/alkylsiloxane copolymer coating for use in the invention is a random or block copolymer of the form: (in which R 1 represents an alkyl group, preferably a C 1-6 alkyl group, e.g. a methyl group; R 2 represents an alkoxy group, preferably a C 1-6 alkoxy group such as -O-CH 3 or -O-CH 2 CH 3 ; R 3 represents an alkyl or alkoxy group, e.g. as defined for R 1 or R 2 ; R 4 represents a functional group, preferably an aminofunctional group such as -CH 2 CH 2 CHNHCH 2 CH 2 NH 2 ; R 5 represents a functional group, e.g. as defined for R 4 , or an alkoxy or alkyl group, e.g. as defined for R 2 or R 1 ; and a, b and c are integers in which a >> b and a >> c) . A preferred embodiment of the invention may be illustrated by considering the design of the MAXIMA FORTE oxygenator available from Medtronic Perfusion Systems, Medtronic, Inc., Minneapolis, Minnesota, USA. Of course, details described below that are specific to this device, but not necessary to practice of the invention, may be different in other embodiments of the invention. Referring to Figures 1-4, a blood oxygenator 10 comprises an outer generally cylindrical vessel 12, which is sealed at its upper end by a generally saucer-shaped upper hollow venous gas header 14. A generally saucer-shaped lower hollow venous gas header 16 seals the lower end of the vessel 12. A blood inlet manifold 18 is connected to the centre of the underside of the lower venous gas header 16. Concentric, generally cylindrical inner and outer heat exchanger housings 20 and 22 are connected at their lower ends to the centre of the lower venous header 16. The upper end of the outer heat exchanger housing 22 includes a transition manifold 24. The interior of the inner heat exchanger housing 20 surrounds and encloses a generally cylindrical first fibre bundle 26 made up of a plurality of vertically oriented hollow micro-conduits. These micro-conduits convey blood vertically upward. A second generally cylindrical fibre bundle 28 concentrically surrounds the outer heat exchanger housing 22 and is positioned inside the inner wall of the cylindrical vessel 12. The upper and lower ends of the generally ring-shaped second fibre bundle 28 interact with the upper and lower venous gas headers 14 and 16, respectively. The blood inlet manifold 18 (Figure 3) includes a barbed blood inlet nozzle 30 which bends downwardly at an angle relative to the central vertical axis of the vessel 12. A barbed blood outlet nozzle 32 (Figures 3 and 4) extends horizontally from the exterior of an enlarged or flared portion 12a of the vessel 12. A standard Leur fitting 34 (Figure 3) extends vertically from the base of the blood outlet nozzle 32. A thermometer probe fitting 36 (Figure 4) extends horizontally from the base of the blood outlet nozzle 32. Inlet and outlet nozzles 38 and 40 (Figures 2 and 4) for a heat transfer fluid such as water extend horizontally from one side of the low venous gas header 16 and communicate with water flow passages inside the inner heat exchanger housing 20. A barbed de-bubbler nozzle 42 (Figure 3) extends upwardly at an angle from the flared portion 12a of the vessel 12. A gas mixture inlet nozzle 44 (Figures 2, 3 and 4) extends horizontally from the periphery of the upper venous gas header 14. A gas mixture outlet nozzle 46 (Figures 2 and 4) extends from the periphery of the lower venous gas header 16 parallel to the water inlet and outlet nozzles 38 and 40. The blood, heat transfer fluid and gas mixture flow paths of the blood oxygenator 10 can best be understood by way of reference to the diagrammatic vertical sectional view of Figure 5. In that figure, the flow of blood is illustrated diagrammatically by the bold solid arrows. The dashed lines illustrate the flow of heat transfer fluid (water). The flow of gas mixture is illustrated by the sequence of dots. Blood from the patient flows through tubing (not illustrated) connected to the blood inlet nozzle 30. This incoming blood spreads out through the blood inlet manifold 18 and travels vertically through the micro-conduits of the first fibre bundle 26 of the central heat exchanger that forms the core of the blood oxygenator 10. Water flows in through the inlet nozzle 38 vertically to the top of the heat exchanger fibre bundle 26 through a separate channel isolated from the fibre bundle 26. The water is then directed down and across the outside of the micro-conduits of the fibre bundle 26. The water flows around the outside of the micro-conduits opposite the flow of the blood within the micro-conduits. The water exiting from the lower end of the first fibre bundle 26 exits through the outlet nozzle 40. The water is heated or cooled outside the blood oxygenator, as necessary to regulate the temperature of the blood flowing through the micro-conduits of the heat exchanger. The use of a counter-flow heat exchanger provides optimum heat exchange efficiency. However, as noted above, the counter-flow design is not essential to the invention. The temperature of the blood can be monitored by a circuit (not illustrated) that includes a thermistor or other temperature sensing device (not illustrated) mounted inside the thermometer probe fitting 36 (Figures 3 and 4). The thermometer probe fitting 36 is a preferred location for connection of an electrical bridge to the blood side of the heat exchanger, since the temperature sensing device is likely to be coincidentally an electrically conductive material (typically metal) already in physical contact with the blood. Thus, the invention may be implemented by connecting a conductive bridge between the temperature sensing device and any convenient location on the other side of the heat exchanger. Blood exiting from the upper end of the first fibre bundle 26 (Figure 5) of the heat exchanger is directed radially outwardly by the transition manifold 24. This blood then travels around the outside of the fibres of the second fibre bundle 28 that forms the oxygenator. The blood travels downwardly past the outside surfaces of the fibres of the second fibre bundle 28. When the blood reaches the lower portion of the second fibre bundle 28, it is collected in an outlet manifold defined by the flared portion 12a of the vessel and exits through the blood outlet nozzle 32. The blood outlet nozzle 32 is connected to tubing (not illustrated) for returning the blood to the patient. A gas mixture rich in oxygen from a pressurized source (not illustrated) is conveyed through a hose (not illustrated), through the gas mixture inlet nozzle 44, and into the upper venous gas header 14. The upper gas header 14 communicates with the upper ends of the fibres in the second fibre bundle 28 forming the membrane oxygenator. The oxygen-rich gas mixture travels down through the interior of the fibres in the fibre bundle 28. These fibres are micro-porous. Carbon dioxide from the blood surrounding the fibres in the bundle 28 diffuses through the walls of the fibres into the gas mixture. Similarly, oxygen from the gas mixture inside the fibres of the bundle 28 diffuses through the micropores into the blood. The gas mixture now having an elevated carbon dioxide content exits the lower ends of the fibres of the second fibre bundle 28 into the lower venous gas header 16 and then exits therefrom via the gas mixture outlet nozzle 46. This gas mixture now has a lower oxygen content. The nozzle 46 is connected to another gas hose (not illustrated). Figure 7 is a diagrammatic illustration of the first fibre bundle 26 which serves as the core of the heat exchanger portion of the blood oxygenator 10. The fibre bundle 26 has a generally cylindrical configuration and comprises approximately 5,400 vertically (axially) extending hollow fibres 50. Preferably the fibres are provided as a continuous long web of micro-conduit wrapping material in which the fibres are held together by a thin, flexible, horizontally extending woven interconnect. Such wrapping material is commercially available from Mitsubishi Rayon, Co., Ltd. under the designation HFE430-1 Hollow Fibre. This material uses polyethylene fibres. Similar wrapping material is also commercially available from Hoechst Celanese Corporation under the designation Heat Exchanger Fibre Mat. This material uses polypropylene fibres. The micro-conduit wrapping material of the heat exchanger core is wound about a central, vertically orientated elongated spindle 52 (Figure 8). The spindle 52 has an intermediate segment 54 naving a cross-shaped cross-section, as best seen in Figure 9. The spindle 52 has enlarged driving ends 56 connected to the opposite ends of the intermediate segment 54. Each of the driving ends 56 has a pair of parallel extending ribs 58 (Figure 10) which are used to lock the spindle into a winding machine (not illustrated). This machine is utilized to wind the micro-conduit wrapping material about the spindle 52. Preferably the micro-conduit wrapping material is compactly wound about the central spindle 52, but without any substantial tension on the web. As mentioned above, the micro-conduit may be provided in a heat exchanger micro-conduit wrapping material. The wrapping material comprises micro-conduit fibres attached to a thin flexible interconnect, such as woven netting, to maintain the fibres at predetermined spacings in substantially parallel alignment with each other. The wrapping material is wrapped about an elongated spindle having first and second ends, such that the ends of each fibre reside proximate the spindle's first and second ends. After the ends of the fibres are trimmed as needed, a shell is placed around the wrapping material and spindle. Opposing first and second seals are created by applying potting compound between fibres proximate the spindle's first end and proximate the spindle's second end. A shown in detail in Figures 11 and 12, the heat exchanger micro-conduit, "micro-conduit" for short, preferably comprises a plurality of small fibres 100, as shown in Figure 11. In Figure 11, the fibres 100 are arranged in a "mat" of micro-conduit wrapping material 102, which is described in greater detail below. Each fibre 100 comprises an elongated two-ended fibre. Each fibre 100 is hollow, with a cross-sectional shape preferably being rounded, or alternatively triangular, rectangular, or another appropriate shape. Since the fibres 100 are hollow, each fibre 100 defines an inner channel 150 having an inner surface 152, as shown in Figure 12. In the illustrated embodiment, the outer diameter of the fibre is about 475 µm while the diameter of the inner channel 150 is about 428 µm. However, a wide variety of inner and outer diameters may be used, depending upon the requirements of the particular application. The difference between the inner and outer diameters is preferably small, to encourage heat exchange through the fibres' walls. The fibres 100 may be about 10 cm long, for example. However, a wide range of fibre lengths may be used, depending upon the requirements of the particular application. The fibres 100 may be made from a plastic material such as polypropylene, polyethylene, a different polymeric substance, or another material that is inexpensive, pharmacologically safe, lightweight, easily cut, and flexible. The material of the fibres 100 must also be easily formed into fibres with sufficiently small inner and outer dimensions. Preferably the fibres 100 would be made of a hydrophilic material, however, micro-conduit made of such material is not presently commercially available. As mentioned above, Figure 11 illustrates a section of micro-conduit wrapping material 102. The material 102 includes a thin flexible interconnect 104 that maintains the fibres 100 at predetermined spacings in substantially parallel alignment with each other. In the illustrated embodiment, the interconnect comprises substantially parallel lengths of flexible thread that are woven or khotted to hold the fibres about 0.5 mm apart, generally parallel to each other. The wrapping material 102 aids in positioning the fibres 100 during construction of a blood heat exchanger, as discussed below. The mat or wrapping material 102 may be made of commercially available product from Mitsubishi Rayon Co., Ltd. sold under the designation HFE 430-1 Hollow Fibre, which uses polyethylene fibres. Similar wrapping material is also commercially available from Hoechst Celanese Corp. under the designation Heat Exchanger Fibre Mat, which uses polypropylene fibres. To manufacture the blood heat exchanger, the micro-conduit wrapping material 102 is wrapped about the spindle, the fibres are installed into the shell, and the upper and lower seals are formed by injecting potting compound between the fibres 100 near the upper and lower surfaces of the core. Sufficient potting compound is applied to substantially seal the spaces between the fibres. Then, the fibres 100 are trimmed near each end of the spindle. Preferably, the trimmed fibres 100 form uniform flat upper and lower surfaces of the core. With the seals in place, liquids such as aqueous priming solution and blood may be directed into the fibres 100 through their ends, without leaking any liquid into the spaces between the fibres. Finally, the manifolds are attached to the shell. Also, hoses and other plumbing lines are attached to the heat exchanger 300 as needed, for transportation of heat exchange medium, blood, priming solution, oxygen, and other media as appropriate. Generally, the heat exchanger regulates the temperature of a patient's blood during a medical procedure such as open heart surgery. Due to the large number of fibres 100 and the small size of the fibres, there is a substantial area of surface contact between the heat exchange medium and the contents of the fibres 100. The temperature of blood flowing through the core is efficiently regulated, due to the high degree of contact between the blood and the heat exchange medium. The configuration of the lower venous gas header 16, the inner heat exchanger housing 20, the water inlet and outlet nozzles 38 and 40 and the gas mixture outlet nozzle 46, are illustrated in Figures 13-17. These parts, along with the raised annular wall member 68 that receives the blood inlet manifold 18, are all injection molded as a single unitary piece of plastic. The inner heat exchanger housing 20 is formed with an interior vertical wall member 76 (Figure 15) that defines a water flow channel or path 78 (Figures 13 and 15) which extends vertically along one side of the heat exchanger housing 20. The lower end of the water flow path 78 communicates with the interior of the water inlet nozzle 38. The upper end of the water flow path 78 communicates through a port 80 (Figure 15) into the upper interior of the housing 20. This permits the incoming heat exchange water to be disbursed around the upper ends of the thousands of micro-conduits or fibres 50 of the heat exchanger fibre bundle 26. As previously explained, this water flows down around the outside of the fibres 50, through another port 82, and then out through water outlet nozzle 40. The opening of the nozzle 40 is shown at 84 in Figure 15. The upper end of the cylindrical heat exchanger housing 20 is molded with a fitting ring 86 (Figures 15 and 17) having an upwardly opening circular recess 88 (Figure 18) for receiving, and interfitting with, a downwardly extending circular flange of the outer heat exchanger housing 22. The fitting ring 86 is connected to the main part of the housing 20 by small plastic extensions 91 (Figure 17). Except for the fibre bundles 26 and 28, and the potting compound comprising the seals 92, 94, 106 and 108, the remainder of the structures illustrated and described herein are preferably injection molded of clear polycarbonate plastic. Suitable plastics are commercially available from Bayer under the designation MAKROLON and from General Electric under the designation LEXAN HP2R-1112. The separately molded plastic components may be assembled and permanently affixed to each other with a suitable non-toxic ultraviolet (UV) curable adhesive. The practice of the invention may be illustrated by the following protocol, which should be read in conjunction with the flowchart of Figure 19. This protocol covers siloxane coating of PVC tubing, oxygenators (using the Medtronic Maxima Forté as a nonlimiting example), and other medical devices. The required process equipment includes: adequately vented fume hood; roller or centrifugal pump capable of pumping a minimum of 2 litres/minute; Lindberg/Blue M constant temperature water bath or equivalent; stir-plate (Bibby B212 or equivalent); stir bars; 4000 ml to 6000 ml glass flasks; Viton brand tubing; balance (Mettler 4000 or equivalent); pH metre; 2000 ml to 6000 ml glass volumetric flasks; 500 ml to 2000 ml graduated cylinders; polypropylene and glass funnels; polypropylene and glass containers; aluminum foil; lint-free paper towels; and PVC tubing or equivalent. The required process materials are: hexanes (ACS Reagent Grade); deionized water ("DI"); Dow Corning MDX4-4159 fluid; 0.1-N Glacial acetic acid; isopropyl alcohol ("IPA"); and 1.0 N hydrochloric acid. Safety glasses and protective gloves should be worn at all times. All operations should be performed in a well vented fume hood. All waste chemicals/solvents should be disposed in appropriate waste containers. Stock solutions (defined as solutions that have a defined shelf-life which allows preparation before initiating the actual process) should be prepared as follows. Preparation of IPA premix: combine 75.0 g (74.6 wt %) of IPA, 25.0 g (24.9 wt %) of DI, and 0.5 g (00.5 wt %) of 1.0 N HCl. The solution should be covered immediately and allowed to stir for a minimum of 5 minutes. The IPA premix should be stored at ambient temperature in a tightly closed container free from moisture. Preparation of aminoalkylsiloxane ("ZX") solids solution may be performed according to either of two options. In the first option, a 3 wt % mixture of ZX solids solution in hexane is formed by combining 1880.0 g (94 wt %) of hexane and 120.0 g (6 wt %) of MDX4-4159. In the second option, a 1.5 wt % ZX solids solution in a IPA/hexane mixture is formed by combining 1580.0 g (79 wt %) of IPA, 360.0 g (18 wt %) of hexane, and 60.0 g (3 wt %) of MDX4-4159. Mixing of the IPA premix and ZX solids solution may also be performed according to either of two options. In the first option, mixing of the IPA premix and 3 wt % ZX solids in hexane is performed by combining 2000.0 g (99 wt %) of 3 wt % ZX solids solution and 20.0 g (1 wt %) of IPA premix. In the second option, mixing of the IPA premix and 1.5 wt % ZX solids in IPA/hexane is performed by combining 2000.0 g (99.5 wt %) of 1.5 wt % ZX solids solution and 10.0 g (0.5 wt %) of IPA premix. The solution should be covered immediately and allowed to stir for a minimum of 5 minutes. The ZX solution should be stored at ambient temperature in a tightly closed container free from moisture. The ZX coating procedure for PVC tubing involves dipping the tubing in the container of ZX solution for 2 minutes and then removing the tubing from the solution. Removal of excess coating from PVC tubing is performed by allowing excess ZX solution to gravity drain for 1 minute. Then, supply 3 PSI (21 kPa, 5-6 SCFM) for 2 minutes, followed by 10 PSI (69 kPa, 7-8 SCFM) for 10 minutes. Curing of the ZX coating on the PVC tubing is performed with humid air (50 ± 5 % relative humidity) at less than 3 PSI (21 kPa) for 30 minutes, followed by 60 minutes of 5-8 PSI (34-55 kPa) of dry air (0 % relative humidity). The coating procedure for microporous hollow fibre membrane oxygenators may be illustrated with the following procedure, which uses, as an example only, the Medtronic MAXIMA FORTÉ brand oxygenator. The procedure is easily adapted to other oxygenators using microporous hollow fibre membranes, such as the Medtronic AFFINITY brand oxygenator, according to principles known in the art. To prepare the device for coating, plug two exhaust air ports using any appropriate technique, along with the outlet air port. Position the device in its upright position. The oxygenator must be properly grounded to insure that any static buildup is properly discharged. This can be accomplished by connecting a lead from the thermocouple connector to the micropump. Using a micropump and Viton brand tubing, connect the inlet of the pump to a container of ZX solution and the outlet of the pump to the blood inlet connection of the device. Using Viton brand tubing and the appropriate connections, connect both the recirculation port and blood outlet to the container of ZX solution, thus allowing recirculation of the ZX solution. Connect an air line capable of supplying 1 PSI (7 kPa, 8 LPM) to the inlet gas port. Have an air line capable of supplying 3 to 10 PSI (21 to 69 kPa, 5 to 8 SCFM) to the blood inlet port, which will be used for excess ZX removal. To coat the device, supply air to the inlet gas port at less than 1 PSI (7 kPa, 6 LPM). Turn the micropump on full power for two minutes. After the micropump is turned off, continue to supply air to the inlet gas port at 6 LPM. To remove excess coating from the device, allow the device to gravity drain for 1 minute. For the next two minutes, continue to supply air to the inlet gas port at less than 1 PSI (7 kPa, 6 LPM) and supply 3 PSI (21 kPa, 5-6 SCFM) to the blood outlet and recirculation port. After the two minute period, supply 1 PSI (7 kPa, 8 LPM) to the inlet gas port and 10 PSI (69 kPa, 7-8 SCFM) to the blood outlet and recirculation port for 10 minutes. To cure the device, use humid air (50 ± 5 % relative humidity) at less than 3 PSI (21 kPa) for 30 minutes, and then use 5-8 PSI (34-55 kPa) of dry air (0 % relative humidity) for 60 minutes. As for other medical devices, appropriate coating process steps and parameters should take into consideration geometry differences. The curing procedure involves using humid air (50 ± 5 % relative humidity) at less than 3 PSI (21 kPa) for 30 minutes and then 5-8 PSI (34-55 kPa) of dry air (0 % relative humidity) for 60 minutes. The success of the invention may be demonstrated by considering the following data. Twelve identical Medtronic MAXIMA FORTÉ brand oxygenators were tested for plasma breakthrough under identical conditions. The oxygenators were considered and tested in six pairs. One member of each pair of oxygenators was coated with aminoalkylsiloxane compound according to the protocol described above. The other member was uncoated. The test measured the time in hours for confirmed plasma breakthrough. Results appear below. Test Devices Control Devices Identifier Time (hours) Identifier Time (hours) T1 97324804 72 C1 29 T1 97324483 34 C2 26 T1 97324458 74 C3 25 T1 97324474 54 C4 14 T1 97324467 36 C5 22 T1 97324753 54 C6 23 Mean 54 Mean 23 Standard 16 Standard 5 Deviation Deviation The tests of units T2 and T5 were terminated after 34 and 36 hours, respectively, because of excessive inlet pressure (>1000 mm Hg, >1.3 x 10 5 Pa) buildup. This type of pressure increase is common due to the aging of the test fluid (bovine blood) during the study and is not reflective of the performance of the coating. The test of unit C4 was terminated after 14 hours after the microporous fibre developed a leak, which interfered with effluent specific gravity measurements. Using standard t-Test calculations for two samples (assuming unequal variances), the following results were obtained. Variable 1 Variable 2 Mean 54 23.16666667 Variance 289.6 26.16666667 Observations 6 6 Hypothesized Mean Difference 0 df 6 t Stat 4.250235182 P(T<=t)one-tail 0.002689373 t Critical one-tail 1.943180905 P(T<=t) two tail 0.005378746 t Critical two-tail 2.446913641 Based on a criterion of p<0.01, the conclusion was that coating the microporous hollow fibre membranes with an aminoalkylsiloxane compound to reduce migration of plasma across the micropores produced large and statistically significant improvement in plasma breakthrough time.

Claims: A medical device comprising a microporous hollow fibre membrane having a plurality of micropores, in which the membrane is provided with a coating comprising an alkoxysiloxane/alkylsiloxane copolymer. A device as claimed in claim 1 wherein said coating is effective to reduce migration of plasma across said micropores. A device as claimed in claim 1 or claim 2 wherein said coating neither covers nor fills said micropores. A device as claimed in any one of claims 1 to 3 wherein said coating increases resistance to plasma breakthrough in the device by changing the surface of the microporous fibre membrane near micropore openings. A device as claimed in any preceding claim wherein said copolymer comprises a random or block copolymer of formula: (in which R 1 represents an alkyl group, preferably methyl; R 2 represents an alkoxy group, preferably -O-CH 3 or -O-CH 2 CH 3 ; R 3 represents an alkyl or alkoxy group; R 4 represents a functional group, preferably - CH 2 CH 2 CH 2 NHCH 2 CH 2 NH 2 ; R 5 represents a functional group, an alkoxy group or an alkyl group; and a, b and c are integers in which a > b and a > c). A device as claimed in any preceding claim wherein said copolymer comprises an aminoalkylsiloxane. A device as claimed in any preceding claim wherein said membrane comprises a polymeric material. A device as claimed in any preceding claim which comprises PVC tubing or a blood oxygenator. A method of coating a device comprising a microporous hollow fibre membrane, said method comprising the steps of: (a) formulating a coating solution comprising an alkoxysiloxane/alkylsiloxane copolymer; (b) contacting said device with the coating solution whereby to form a film of silicone on said membrane; and (c) curing the copolymer on the device. A method as claimed in claim 9 wherein said coating solution comprises an active aminofunctional dimethylsiloxane copolymer together with at least one aliphatic solvent and at least one isopropanol solvent.

Inventors: PLUNKETT SEAN D, PLUNKETT, SEAN D.
Applicants: MEDTRONIC INC, MEDTRONIC, INC.
Application year: 2000
Main classification: A61L33
IPC codes: B01D71, B01D63, B01D67, B01D69, A61L33