Biodegradable complex fiber and method for producing the same

Abstract: The invention has an object of providing a biodegradable complex fiber which retains excellent biodegradability and hydrolyzability and has high strength and high melting temperature which are fit for practical use and also providing a method for producing the biodegradable complex fiber. The biodegradable complex fiber comprises at least one polymer material selected from the group consisting of a polyglycolic acid, a poly(glycolic acid-co-lactic acid) and polylactic acid as a core component or as a shell component and a polymer material of poly(3-hydroxybutyric acid) groups or a polymer material of an aliphatic polyester consisting of a dibasic acid and a diol as a shell component or as a core component. The method comprises producing the biodegradable complex fiber by melt spinning.

Description: BACKGROUND OF THE INVENTION Field of the Invention The present invention relates to a biodegradable complex fiber and a method for producing the fiber, and more particularly, to a biodegradable complex fiber which can be widely used as fishing materials, e.g., fishing lines and fish nets, agricultural materials, e.g., insect or bird nets and vegetation nets, cloth fibers and non-woven fibers for living articles, e.g., disposable women's sanitary items, masks, wet tissues, underwear, towels, handkerchiefs, kitchen towels and diapers and medical supplies, e.g., operating sutures which may not be removed, operating nets and suture-reinforcing materials and does not pollute the environment. The present invention also relates to a method for producing the biodegradable fiber. Description of the Related Art As polymer materials used for fishing lines, fish nets, agricultural nets, living articles or the like, those comprising, for example, a polyamide, polyester, vinylon or polyolefin have been used. These polymer materials are resistant to degradation and hence have the problem that the environment is polluted when the above products are left under the natural environment after they are used. In order to solve this problem, these products must be subjected to treatments such as incineration, recovery and reproduction after being used. However, these treatments need considerable costs. Moreover, many used products cannot be recovered and are left under the natural environment, causing environmental disruption. Among methods used to solve such a problem, there is a method utilizing a polymer material which is easily degraded by microorganisms present in the natural world. For example, surgical sutures comprising poly-ε -caprolactone and monofilaments comprising poly-β-propiolactone are disclosed in Japanese Patent Application Laid-Open (JP-A) Nos. H1-175855 and H5-78912 respectively. Poly-ε-caprolactone and poly-β-propiolactone, however, have melting temperatures as low as about 60°C and about 97°C respectively, giving rise to the problem that there is a limitation to a method of using these compounds. Also, JP-A No. H5-93316 discloses a microorganisms-degradable complex fiber using poly-ε -caprolactone and/or poly-β-propiolactone as the core component and poly(β-hydroxyalkanoate) or its copolymer as the shell component. However, the melting temperatures of poly-ε-caprolactone and poly-β-propiolactone are about 60°C and about 97°C. Therefore, in the case of using these compounds as fibers, the deterioration of the strength of the fibers cannot be avoided when the operating temperature exceeds 100 or the temperature partly exceeds 100°C by frictional heat. As for an instance of microorganisms-degradable fibers having high melting temperature, surgical sutural materials comprising polylactic acid and its copolymer are disclosed in JP-A No. S45-31696. However, such a fiber has insufficient strength and even though it can be made into a monofilament, the resulting monofilament is very hard so that it can be tied up with difficulty. Also its degradation is slow and cannot be controlled. As for polyglycolic acid type and polylactide type fibers, these fibers are already commercially available as sutures. These fibers are, however, sensitive to moisture and tend to deteriorate. Also, these fibers are hard and this tends to limit their application. Moreover, they have a biological compatibility problem. For instance, when they are used as a suture for blood vessels, they can be unnecessarily said to be suitable because thrombus tends to be produced and adhesions of tissue are caused. While, biodegradable polyester fibers using random copolymer polyester containing a 3-hydroxybutyric acid unit produced by microorganisms are disclosed in Biomaterials, 1987, Vol 8, 129. These poly(3-hydroxybutyric acid) groups are known to be degraded very well by bacteria which exist under the ground and in water in a large number. Also, they are used in applications, such as non-woven fabrics for preventing adhesions of tissue after operations because of their excellent biological compatibility. However, when they are made into fibers, the spinning and drawing of these fibers are found to be difficult, giving rise to the problem that high strength fibers cannot be obtained. For example, it is reported that after poly(3-hydroxybutyric acid) groups produced by microorganisms are melted and extruded in a melt spinning step, they are deformed rubber-wise in a stage of drawing them into strings when they are not crystallized whereas when they are highly crystallized, they are brittle-fractured even at any temperature or even if any stress is applied, with the result that the spun strings are brittle and hence have very low strength (Elsevier Applied Science, London, pp33-43, 1988). SUMMARY OF THE INVENTION As outlined above, a biodegradable fiber has not be obtained yet which has high strength and melting temperature which are fit for practical use and exhibits excellent biodegradability and hydrolyzability so that it can be widely utilized as, for example, agricultural materials, living articles and medical supplies. Therefore, it is an object of the present invention to provide a biodegradable complex fiber which keeps excellent biodegradability and hydrolyzability and has high strength and melting temperature which are fit for practical use and to provide a method for producing the biodegradable complex fiber. The inventors of the present invention have made earnest studies concerning each component material of a core-shell type fiber to solve the above problem and as a result, found that if a core component and a shell component are respectively formed of specific polymer materials, a complex fiber which has high strength, exhibits a melting temperature that can be freely controlled in a temperature range between 100 and 180, possesses expansion ability that can be controlled and has good biodegradability and hydrolyzability can be obtained by melt spinning. Thus, the present invention has been completed. According to a first aspect of the present invention, there is provided a biodegradable complex fiber comprising at least one polymer material selected from the group consisting of a polyglycolic acid, a poly(glycolic acid-co-lactic acid) and polylactic acid as a core component and a polymer material of poly(3-hydroxybutyric acid) groups as a shell component. According to a second aspect of the present invention, there is provided a biodegradable complex fiber comprising a polymer material of poly(3-hydroxybutyric acid) groups as a core component and at least one polymer material selected from the group consisting of a polyglycolic acid, a poly(glycolic acid-co-lactic acid) and polylactic acid as a shell component. According to a third aspect of the present invention in the first aspect, there is provided a method for producing a biodegradable complex fiber comprising melt-spinning and drawing at least one polymer material selected from the group consisting of a polyglycolic acid, a poly(glycolic acid-co-lactic acid) and polylactic acid as a core component and a polymer material constituting of poly(3-hydroxybutyric acid) groups as a shell component by using a spinneret for complex fiber. According to a fourth aspect of the present invention in the second aspect, there is provided a method for producing a biodegradable complex fiber comprising melt-spinning and drawing a polymer material of poly(3-hydroxybutyric acid) groups as a core component and at least one polymer material selected from the group consisting of a polyglycolic acid, a poly(glycolic acid-co-lactic acid) and polylactic acid as a shell component at the same time by using a spinneret for complex fiber. In one form of the method according to the third or fourth aspect of the present invention, the drawing is performed at a temperature lower than the melting temperature of the polymer material at a drawing magnification of 5 X to 10 X. In the present invention, a core-shell type biodegradable complex fiber is constituted using at least one polymer material (hereinafter called a «material A») selected from the group consisting of a polyglycolic acid, a poly(glycolic acid-co-lactic acid) and polylactic acid and a polymer material (hereinafter called a «material B») of poly(3-hydroxybutyric acid) groups, wherein either when the material A is the core component, the material B is the shell component or when the material A is the shell component, the material B is the core component. By properly selecting materials constituting the core component and the shell component from the materials A and B and by appropriately selecting the ratio by volume of the core component to the shell component, a biodegradable complex fiber having higher strength than biodegradable complex fibers which are conventionally used and a melting temperature ranging from 100°C to 180°C can be obtained by melt spinning. Such a biodegradable complex fiber can also be controlled with respect to its expansion ability and produces excellent biodegradable and hydrolyzable effects. Such effects cannot be obtained only by blending and spinning the materials A and B. BRIEF DESCRIPTION OF THE DRAWINGS FIG. 1 is a typical view showing a melt spinning machine used in an example; FIG. 2 is a graph showing the relation between days elapsed and retention of weight in a test example 1 of a degradability test; FIG. 3 is a graph showing days elapsed and retention of tensile strength in the test example 1 of the degradability test; FIG. 4 is a graph showing the relation between days elapsed and retention of elastic modulus in the test example 1 of the degradability test; FIG. 5 is a graph showing the relation between days elapsed and retention of elongation at break in the test example 1 of the degradability test; FIG. 6 is a graph showing the relation between days elapsed and retention of tensile strength in a comparative test example 1 of the degradability test; FIG. 7 is a graph showing the relation between days elapsed and retention of tensile strength or retention of elastic modulus or retention of elongation at break in a comparative test example 2 of the degradability test; and DETAILED DESCRIPTION OF THE INVENTION The present invention will be explained in detail. Firstly, a polymer material (a biodegradable polyester) used in the present invention will be explained. Preferable examples of a group of polymers containing 3-hydroxybutyric acid, referred to as poly(3-hydroxybutyric acid) groups used in the biodegradable complex fiber of the present invention may include a poly(3-hydroxybutyric acid) (hereinafter, (R)-isomers and (S)-isomers are abbreviated as P[(R)-3HB] and P[(S)-3HB] respectively) and copolymerized polyesters of 3-hydroxybutyric acid such as a poly(3-hydroxybutyric acid-co-3-hydroxypropanoic acid), poly(3-hydroxybutyric acid-co-3-hydroxypentanoic acid), poly(3-hydroxybutyric acid-co-4-hydroxybutyric acid), poly(3-hydroxybutyric acid-co-3-hydroxyhexanoic acid), poly(3-hydroxybutyric acid-co-3-hydroxyheptanoic acid), poly(3-hydroxybutyric acid-co-3-hydroxyoctanoic acid), poly(3-hydroxybutyric acid-co-5-hydroxypentanoic acid), poly(3-hydroxybutyric acid-co-3-methyl-5-hydroxypentanoic acid), poly(3-hydroxybutyric acid-co-6-hydroxyhexanoic acid), poly(3-hydroxybutyric acid-co-15-hydroxypentadecanoic acid), poly(3-hydroxybutyric acid-co-L-lactide), poly(3-hydroxybutyric acid-co-7-methyl-1,4-dioxepan-5-one) and poly(3-hydroxybutyric acid-co-12-oxa-16-hexadecanoride). Among these compounds, P[(R)-3HB] and P[(S)-3HB] are preferable. As these poly(3-hydroxybutyric acid) groups, any one of chemical synthetic products and products synthesized by microorganisms may be used. In the case of a chemical product; poly(3-hydroxybutyric acid, the optical purity of β-butyrolactone as a monomer is preferably 90%ee or more though it is optional as far as it does not cause a reduction in the strength of a fiber. In the biodegradable complex fiber of the present invention, preferably the core portion is constituted of a polyglycolic acid (hereinafter abbreviated as «PGA») which is sensitive to moisture though it has a high melting temperature or of polylactic acid (hereinafter abbreviated as «PLA») and the shell portion is constituted of a compound having excellent biological compatibility such as poly(3-hydroxybutyric acid) groups. Although the biodegradable polymer material (biodegradable polyester ) used in the present invention can be obtained by a well-known production method, a commercially available product may be used as the biodegradable polymer material. As required, two or more types may be combined. In the present invention, biodegradable complex fiber to be used, preferably the ratio by volume of a polymer material of the core portion to a polymer material of the shell portion is 10:90 to 90:10. Such a ratio by volume may be arbitrarily changed by changing the rotating speed of a motor, the diameter of a nozzle and the diameter of a cylinder in a melt spinning machine corresponding to the qualities of the polymer material to be used. When the biodegradable complex fiber of the present invention is produced by melt spinning, a spinneret for complex fiber which has a diameter of about 1.0 mm, and, as required, larger than 1.0 mm is used. It is proper that the temperature of the spinneret portion, though it differs depending upon the degree of polymerization and composition of the polymer material, is 100 to 240°C and preferably 200 to 240°C. The temperature of the melting portion is generally above the melting temperature of the polymer material to be used. When the temperature exceeds 240°C, the polymer is degraded significantly, making it difficult to obtain high strength fibers. Usual compounding ingredients such as stabilizers and colorants may be appropriately added to the biodegradable polymer material of the present invention. In order to increase recrystallization rate and to improve processability, core agents such as talc, boron nitride, titanium oxide, micromica and chalk may be added as required in an amount of 0.01 to 1% by weight. The fiber which has been melt-spun is continuously drawn either after it is once rolled or without being rolled. The drawing is carried out at room temperature, or using hot air or a heated plate or a hot pin, or in a heating medium such as water, glycerol, ethylene glycol or silicon oil at 30 to 150°C and preferably 50 to 120°C. It is generally desirable to carry out such drawing at a temperature lower than the melting temperature of the aforementioned biodegradable polymer material at a drawing magnification of 5 X to 10 X corresponding to the desired requirements. A magnification less than 5 X brings about a small increase in the strength whereas a magnification exceeding 10 X results in frequent occurrences of breaking accidents. The fiber drawn in this manner is heat-treated as required at 50 to 150°C. The fineness of the finally obtained fiber of the present invention is usually 50 d or more although it differs depending upon its application. EXAMPLE The present invention will be hereinafter explained in more detail by way of examples, test examples and the like, which are not intended to be limiting of the present invention. Instruments for analysis used in the examples and test examples are as follows. 1) Melt spinning machine: 15  miniature spinning machine (manufactured by Ooba Machine Corporation). 2) Drawing machine: Miniature thermal drawing machine (equipped with a bath) (manufactured by Ooba Machine Corporation). 3) Strength measuring instrument: Shimadzu AGS500B (manufactured by Shimadzu Corporation). The data of the drawing magnification, drawing temperature, tensile strength, elastic modulus, elongation at break, outside diameter and core diameter are collectively shown in the following Table 1. Example 1 Production of P[(R)-3HB] (shell)-PGA (core) complex fiber Using a melt spinning machine shown in FIG. 1, PGA (weight average molecular weight: 100,000, melting temperature: 237°C, glass transition temperature: 37°C) was supplied from a core polymer material inlet 8 in the condition that the temperature of a cylinder 2 was 200°C, the temperature of a cylinder 3 was 225°C and the temperature of a nozzle 7 was 232°C and P[(R)-3HB] (chemical synthetic product, weight average molecular weight: 315,000, optical purity of a monomer: 94%ee, melting temperature: 168°C, glass transition temperature: 0°C) was supplied from a shell polymer material inlet 9 in the condition that the temperature of a cylinder 5 was 140°C, the temperature of a cylinder 6 was 155°C and the temperature of a nozzle 7 was 232°C. Both PGA and P[(R)-3HB] were melt-extruded at the same time and the resulting fiber was drawn at 63°C at a magnification of 6 X. The ratio by volume of the polymer materials in the resulting fiber was as follows: P[(R)-3HB]:PGA=40:60. This fiber had two melting temperatures; 157.7°C (P[(R)-3HB]) and 216.4°C (PGA). In a melt spinning machine shown in (A) of FIG. 1, 1 and 4 respectively show a motor and (B) in FIG. 1 shows the state of the inside of the nozzle 7. Example 2 Production of P[(R)-3HB] (shell)-PGA (core) complex fiber A complex fiber was produced in the same manner as in Example 1 except that the fiber obtained by melt extrusion was drawn at 67°C at a magnification of 7 X. The ratio by volume of the polymer materials in the resulting fiber was as follows: P[(R)-3HB]:PGA=42:58. Example 3 Production of P[(R)-3HB] (shell)-PGA (core) complex fiber Using a melt spinning machine shown in FIG. 1 and the same PGA and P[(R)-3HB] that were used in Example 1, PGA was supplied from the core polymer material inlet 8 in the condition that the temperature of the cylinder 2 was 200°C, the temperature of the cylinder 3 was 240°C and the temperature of the nozzle 7 was 240°C and P[(R)-3HB] was supplied from the shell polymer material inlet 9 in the condition that the temperature of the cylinder 5 was 140°C, the temperature of the cylinder 6 was 230°C and the temperature of the nozzle 7 was 240°C. Both PGA and P[(R)-3HB] were melt-extruded at the same time and the resulting fiber was drawn at 80°C at a magnification of 9 X. The ratio by volume of the polymer materials in the resulting fiber was as follows: P[(R)-3HB]:PGA=36:64. Example 4 Production of P[(R)-3HB] (shell)-PGA (core) complex fiber A complex fiber was produced in the same manner as in Example 3 except that the fiber obtained by melt extrusion was drawn at 50°C at a magnification of 6 X. The ratio by volume of the polymer materials in the resulting fiber was as follows: P[(R)-3HB]:PGA=40:60. Example 5 Production of P[(R)-3HB] (shell)-PGA (core) complex fiber A complex fiber was produced in the same manner as in Example 3 except that the fiber obtained by melt extrusion was drawn at 50°C at a magnification of 9 X. The ratio by volume of the polymer materials in the resulting fiber was as follows: P[(R)-3HB]:PGA=57:43. Example 6 Production of P[(R)-3HB] (shell)-poly-L-lactic acid (core) complex fiber Using a melt spinning machine shown in FIG. 1 and a poly-L-lactic acid (hereinafter abbreviated as PLLA) (weight average molecular weight: 200,000, melting temperature: 178°C, glass transition temperature: 61°C) and the same P[(R)-3HB] that was used in Example 1, PLLA was supplied from the core polymer material inlet 8 in the condition that the temperature of the cylinder 2 was 200°C, the temperature of the cylinder 3 was 200°C and the temperature of the nozzle 7 was 210°C and P[(R)-3HB] was supplied from the shell polymer material inlet 9 in condition that the temperature of the cylinder 5 was 160°C, the temperature-of the cylinder 6 was 168°C and the temperature of the nozzle 7 was 210°C. Both PLLA and P[(R)-3HB] were melt-extruded at the same time and the resulting fiber was drawn at 80° at. a magnification of 5 X. The ratio by volume of the polymer materials in the resulting fiber was as follows: P[(R)-3HB]:PLLA=93:7. Example 7 Production of P[(R)-3HB] (shell)-PGA (core) complex fiber A complex fiber was produced in the same manner as in Example 3 except that the discharge amount from the shell polymer material inlet 9 was altered to one-half that of Example 3 and the fiber obtained by melt extrusion was drawn at a magnification of 7 X. The ratio by volume of the polymer materials in the resulting fiber was as follows: P[(R)-3HB]:PGA=18:82. Shell compone nt Core component Ratio by volume (shell: core) Drawing magnification (magnifications) Drawing temperature (°C) Tensile strength (MPa) Elastic modulus (GPa) Elongation at break (%) Outside diameter (µm) Core diameter (µm) Example 1 P[(R)-3HB] PGA 40:60 6.0 50 536 4.23 182 59 46 Example 2 P[(R)-3HB] PGA 42:58 6.0 50 403 3.73 176 79 52 Example 3 P[(R)-3HB] PGA 36:64 6.0 63 700 9.2 88 40 31 Example 4 P[(R)-3HB] PGA 40:60 7.0 67 900 9.8 79 29 22 Example 5 P[(R)-3HB] PGA 57:43 9.0 80 1000 11 68 25 20 Example 6 P[(R)-3HB] PLLA 93:7 5.0 80 380 3.9 250 200 54 Example 7 P[(R)-3HB] PGA 18:82 7.0 63 880 14.7 125 44 40 Degradability test The degradability test of the complex fibers was made as follows. 15 strings (about 80 mm per string) of the complex fiber were tied up in a bundle to weigh and were sterilized by UV-rays for 30 minutes to make a sample. While, ample vials for phosphoric acid buffer solutions of pHs of 6.0, 7.0 and 8.0 were respectively sterilized under pressure at 121°C for 20 minutes. The above sample was filled in these ample vials and dipped in the phosphoric acid buffer solution of each pH to carry out a degradability test in 37°C thermostat. Test example 1 Degradability test for P[(R)-3HB] (shell)-PGA (core) complex fiber The complex fiber with the following ratio by volume: P[(R)-3HB]:PGA=18:82, which was obtained in Example 9 was measured for the retention of weight 2 weeks or 3 weeks after the test was started, the retention of tensile strength 7 days and 10 days after the test was started, the retention of elastic modulus 7 days and 10 days after the test was started and the retention of elongation at break 7 days and 10 days after the test was started in each of phosphoric acid buffer solutions of pHs of 6.0, 7.0 and 8.0. The obtained results are shown in FIG. 2, FIG. 3, FIG. 4 and FIG. 5, respectively. From these results, each retention of weight is 48%, 35% and 12% three weeks after, showing that the sample is considerably degraded. The retention of tensile strength of every one of the samples is around 23% 10 days after, showing that the strength is extremely reduced. The retention of elastic modulus of every one of the samples is around 63% 10 days after, showing that the elastic modulus is remarkably reduced. Moreover, each retention of elongation at break is 16%, 36% and 38% 10 days after, showing that it is considerably decreased in every case and the sample was made brittle. It is found from these results that the degradability of the complex fiber is good. Comparative test example 1 Degradability test for PLLA single fiber A PLLA single fiber was measured for the retention of tensile strength 1 week, 2 weeks, 3 weeks and 4 weeks after the test was started in a phosphoric acid buffer solution of a pH of 7.2. The obtained results are shown in FIG. 6. Comparing the results shown in FIG. 10 with the results shown in FIG. 3 (P[(R)-3HB] (shell)-PGA (core) complex fiber), it is found that a reduction in the strength of the PLEA single fiber is slow, showing that the PLLA single fiber is degraded slowly. Comparative test example 2 Degradability test for PGA single fiber A PGA single fiber was measured for the retention of tensile strength 1 week, 2 weeks and 3 weeks after the test was started, the retention of elastic modulus 1 week, 2 weeks and 17 days after the test was started and the retention of elongation at break 1 week and 2 weeks after the test was started, in a phosphoric acid buffer solution of a pH of 7.0. The obtained results are shown in FIG. 7. It is understood from the results shown in FIG. 7 that a reduction in the tensile strength is the same as or slightly slower than that of results shown in FIG. 3 (P[(R)-3HB] (shell)-PGA (core) complex fiber). The retention of elastic modulus is kept higher than that of results shown in FIG. 4 (P[(R)-3HB] (shell)-PGA (core) complex fiber). Moreover, the retention of elongation at break is lost quickly and specifically, it is decreased more quickly than that of the results shown in FIG. 5 (P[(R)-3HB] (shell)-PGA (core) complex fiber). Namely, the PGA single fiber quickly becomes easily cut. As is clear from the results of Comparative test examples 1 and 2, the PLLA single fiber is degraded slowly and it is difficult to control the degradation rate because it is a single fiber. The PGA single fiber, though its degradation is fast, the control of degradation rate is difficult because it is a single fiber. On the contrary, the degradation rate of the complex fiber of the present invention can be controlled with ease by properly selecting the ratio of the shell component to the core component and the qualities of these shell and core components. As explained above, in the core-shell type biodegradable complex fiber of the present invention, even if the polymer material (biodegradable polyester) to be used has the drawbacks of low extension, high brittleness, impaired hydrolyzability, excessively high hydrolyzability, reduced biodegradability and impaired biological compatibility, these drawbacks can be overcome by using, as either one of the core component and the shell component, a polymer material (biodegradable polyester) having high extension, low brittleness, appropriate hydrolyzability, high biodegradability and good biological compatibility. Also, by this measures, the expansion ability can be controlled and hence a biodegradable complex fiber with high strength can be produced. As a consequence, the biodegradable complex fiber of the present invention is a polyester complex fiber which has heat resistance sufficient for use in usual material applications, has melting temperature and degradation rate that can be optionally changed for use in medical applications and has high strength and biodegradability. Accordingly, the biodegradable complex fiber is preferable as fishing materials, e.g., fishing lines and fish nets, agricultural materials, e.g., insect or bird nets and vegetation nets, cloth fibers and non-woven fibers for living articles, e.g., disposable women's sanitary items, masks, wet tissues, underwear, towels, handkerchiefs, kitchen towels and diapers and other general industrial materials. They are degraded and reduced in the strength by leaving them in an environment, under which microorganisms can exist, after they are used and can be completely degraded after a fixed period of time. Therefore, if the fiber of the present invention is used, it is possible to prevent environmental pollution and environmental disruption without the provision of a special waste treating equipment. Furthermore, the fiber of the present invention has biological compatibility and excellent stability in human tissue so that it is hydrolyzed and absorbed in the body. Therefore the fiber of the present invention can be utilized as medical supplies, e.g., operating sutures which need not be removed, operating nets and suture-reinforcing materials.

Claims: A biodegradable complex fiber comprising at least one polymer material selected from the group consisting of a polyglycolic acid, a poly(glycolic acid-co-lactic acid) and polylactic acid as a core component and a polymer material of poly(3-hydroxybutyric acid) groups as a shell component. A biodegradable complex fiber comprising a polymer material of poly(3-hydroxybutyric acid) groups as a core component and at least one polymer material selected from the group consisting of a polyglycolic acid, a poly(glycolic acid-co-lactic acid) and polylactic acid as a shell component. A method for producing a biodegradable complex fiber according to Claim 1 or 2, comprising melt-spinning and drawing at least one polymer material selected from the group consisting of a polyglycolic acid, a poly(glycolic acid-co-lactic acid) and polylactic acid as a core component and a compound selected from the group consisting of a polymer material of poly(3-hydroxybutyric acid) groups and a polymer material of an aliphatic polyester consisting of a dibasic acid and a diol as a shell component by using a spinneret for complex fiber. A method for producing a biodegradable complex fiber according to Claim 1 or 2, comprising melt-spinning and drawing a compound selected from the group consisting of a polymer material of poly(3-hydroxybutyric acid) groups and a polymer material of an aliphatic polyester consisting of a dibasic acid and a diol as a core component and at least one polymer material selected from the group consisting of a polyglycolic acid, a poly(glycolic acid-co-lactic acid) and polylactic acid as a shell component by using a spinneret for complex fiber. A method for producing a biodegradable complex fiber according to Claim 3 or 4, wherein said drawing is performed at a temperature lower than the melting temperature of the polymer material at a drawing magnification of 5 X to 10 X.

Inventors: HORI YOJI, KIMURA YOSHIHARU, HORI, YOJI, KIMURA, YOSHIHARU
Applicants: TAKASAGO PERFUMERY CO LTD, TAKASAGO INTERNATIONAL CORPORATION
Application year: 2000
Main classification: D01F8
IPC codes: C08G63, C08L67, C08L101, D01F8