Modified conjugated diene polymer and rubber composition comprising it

Abstract: A conjugated diene polymer is produced by continuously polymerizing a conjugated diene monomer with a catalyst consisting essentially of specified components (a) to (c) and reacting with at least one of specified components (d) and (e) and has a content of cis-1,4-bond of not less than 85%, a content of 1,2-vinyl bond of not more than 2.0% and a ratio of weight average molecular weight (Mw) to number average molecular weight (Mn) of not more than 5, and contains at least one functional group selected from epoxy group and hydroxyl group in its molecule. And also, a rubber composition comprises 10-200 parts by weight of silica based on 100 parts by weight of rubber ingredient consisting of 10-100% by weight of the above conjugated diene polymer and 90-0% by weight of the other diene polymer or natural rubber.

Description: This invention relates to a rubber composition obtained by compounding a conjugated diene polymer with silica, and more particularly to a rubber composition having excellent properties such as wear resistance, mechanical properties, and low heat build-up by polymerizing a conjugated diene compound with a rare earth element containing compound as a catalyst and then reacting the resulting polymer just after the polymerization with a compound having a particular functional group (a modifying agent) so as to interact with silica to improve the dispersibility of silica. As a polymerization catalyst for conjugated diene compounds, there have hitherto been proposed many catalysts, which play an important role in industry. Particularly, many polymerization catalysts giving a high content of cis-1,4-bond have been studied and developed for the purpose of providing conjugated diene polymers having excellent mechanical and thermal properties. For example, there is well-known a composite catalyst system containing a compound of a transition metal such as nickel, cobalt or titanium as an essential component. Among them, some catalysts have industrially and widely been used as a polymerization catalyst of butadiene, isoprene or the like (see End. Ing. Chem., 48, 784(1956) and JP-B-37-8198). On the other hand, in order to give a higher content of cis-1,4-bond and an excellent polymerization activity, there has been studied and developed a high stereospecific polymerization using a composite catalyst system comprising a rare earth metal compound and an organometal compound of an element of Group I-III. In JP-B-47-14729 is disclosed a catalyst system comprising a rare earth metal compound such as cerium octanoate and an alkyl aluminium hydride such as diisobutyl aluminium hydride or an aluminium hydride such as trialkyl aluminium or ethyl aluminium dichloride. Especially, this publication discloses that catalytic activity is increased by aging the catalyst system in the presence of butadiene. Also, JP-B-62-1404, JP-B-63-64444 and JP-B-1-16244 propose a method wherein the catalytic activity is increased by enhancing the solubility of a compound of a rare earth element in a polymerization solvent. Further, JP-B-4-2601 discloses that a catalyst system comprising a rare earth metal compound, trialkyl aluminium or aluminium hydride and an organic halogen derivative indicates an activity higher than that of the conventional one in the polymerization of 1,3-butadiene. However, the polymers obtained through the conventional catalyst system containing the rare earth metal compound become wider in the molecular weight distribution and do not sufficiently improve the wear resistance and rebound resilience. Furthermore, JP-A-6-211916, JP-A-6-306113 and JP-A-8-73515 report that a catalyst system using a neodymium compound and methyl aluminoxane indicates a high polymerization activity and provides a conjugated diene polymer having a narrow molecular weight distribution. However, in order to provide polymers having a narrow molecular weight distribution while maintaining sufficient catalytic activity in the above polymerization method, it is required to use a greater amount of aluminoxane as compared with the conventional catalyst using an organo-aluminum compound. Such an aluminoxane is expensive in cost as compared with the usual organoaluminium compound and exhibits large cold flow and has problems in respect of storage stability and the like, so that there is a problem in practical use. In order to solve these problems, JP-A-10-306113 and JP-A-10-35633 report that the conjugated diene polymer polymerized through a catalyst system using methyl aluminoxane is modified with a hetero three-membered ring compound, a halogenated metal compound or a metal carbonate to suppress the cold flow. Recently, resource-saving, environmental measures are regarded as important and hence the demand for reducing fuel consumption of automobiles becomes more severe and also it is demanded to reduce the rolling resistance even in automobile tires in order to obtain low fuel consumption. For the purpose of reducing the rolling resistance of the tire, a rubber material capable of providing a cured rubber having a low heat build-up is generally used as a rubber material for the tire. However, when the aforementioned conjugated diene polymer is used to prepare a rubber composition with silica, the interaction between such a polymer (rubber) and silica is not sufficient and hence the dispersibility of silica into the resulting rubber composition is poor and also the properties of the resulting cured rubber such as wear resistance, mechanical properties and, low heat build-up do not achieve a satisfactory level. The present inventors have made various studies and found that conjugated diene polymers having a high content of 1,4-cis bond, a low content of 1,2-vinyl bond and a narrow molecular weight distribution, and containing a specified functional group in their molecule have excellent interaction with silica and a vulcanizate of the resulting rubber composition has excellent properties such as wear resistance, mechanical properties, and low heat build-up, and as a result the invention has been accomplished. Attention is also drawn to the disclosure of Hattori et al "Chemical Modification of Neodymium High Cis-1,4-Polybutadiene with Styreneoxide", Polymers for Advanced Technologies, 1993, 4, No. 7, p. 450-456, which describes carbon black-filled rubber compositions. The present invention provides a rubber composition comprising 10-200 parts by weight of silica based on 100 parts by weight of rubber ingredient consisting of 10-100% by weight of a conjugated diene polymer having a content of cis-1,4-bond of not less than 85%, a content of 1,2-vinyl bond of not more than 2.0% and a ratio of weight average molecular weight (Mw) to number average molecular weight (Mn) of not more than 5, and containing at least one functional group selected from epoxy group and hydroxyl group in its molecule, and 90-0% by weight of another diene polymer or natural rubber; wherein said conjugated diene polymer is obtained by polymerizing a conjugated diene compound with a catalyst consisting essentially of the following components (a) to (c) and subsequently reacting with at least one compound selected from the group consisting of the following components (d) and (e): Component (a): a compound containing a rare earth element belonging to atomic numbers 57-71 in the Periodic Table, or a reaction product between such a compound and a Lewis base wherein said compound containing the rase earth element as the component (a) is a carboxylate, an alkoxide, a β-diketone complex, a phosphate or a phosphite; Component (b): an aluminoxane and/or an organoaluminium compound having a general formula of A1R 1 R 2 R 3 , wherein R 1 and R 2 are the same or different and are a hydrogen atom and a hydrocarbon group having a carbon number of 1-10, and R 3 is a hydrocarbon group having a carbon number of 1-10, provided that R 3 is the same or different from R 1 and R 2 ; Component (c): a halogen-containing compound which is a reaction product between a metal halide and a Lewis base, diethylaluminium chloride, silicon tetrachloride, trimethyl chlorosilane, methyl dichlorosilane, dimethyl dichlorosilane, methyl trichlorosilane, ethylaluminium dichloride, ethylaluminium sesquichloride, tin tetrachloride, tin trichloride, phosphorus trichloride, benzoyl chloride and t-butylchloride; Component (d): a hydroxyl group-containing vinyl compound; Component (e): an epoxy compound. The above halogen-containing compound (c) is preferably a reaction product between a metal halide and a Lewis base. It is preferable that the Lewis base is a phosphoric ester, a diketone compound, a carboxylic acid and/or an alcohol. The rubber composition preferably further contains 1-20 parts by weight of a silane coupling agent based on 100 parts by weight of the rubber ingredient. The conjugated diene polymer used in the rubber composition according to the invention has a content of cis-1,4-bond of not less than 85%, preferably not less than 90%, a content of 1,2-vinyl bond of not more than 2.0%, preferably not more than 1.5% and a ratio of weight average molecular weight (Mw) to number average molecular weight (Mn) of not more than 5, preferably not more than 4, and contains at least one functional group selected from epoxy group and hydroxyl group in its molecule. When the content of cis-1,4-bond is less than 85%, the wear resistance is poor. When the content of 1,2-vinyl bond exceeds 2.0%, the durability is poor. When Mw/Mn exceeds 5, the wear resistance is poor. Also, when the functional group selected from epoxy group and hydroxyl group is not contained in the molecule of the conjugated diene polymer, the interaction with silica is insufficient and the dispersibility of silica lowers. Furthermore, the conjugated diene polymer preferably has a Moony viscosity at 100°C (ML 1+4 , 100°C) of 10-150. When the Moony viscosity is less than 10, the wear resistance after the vulcanization is poor, while when it exceeds 150, the processability in the kneading is poor. Moreover, the conjugated diene polymer according to the invention preferably has a weight average molecular weight as converted by polystyrene of 100,000-1,500,000, more preferably 150,000-1,000,000. When it is outside the above range, the processability and the properties of the cured rubber are unfavorably poor. The conjugated diene polymer is obtained by polymerizing a conjugated diene compound with a catalyst consisting of the components (a) to (c) and subsequently reacting with at least one compound selected from the components (d) to (e). The component (a) used in the catalyst is a compound containing a rare earth element belonging to atomic numbers 57-71 in the Periodic Table (rare earth element containing compound), or a reaction product between such a compound and a Lewis base. As the rare earth element, neodymium, praseodymium, cerium, lanthanum or gadolinium, or a mixture thereof is preferable, and neodymium is particularly preferred. The rare earth element containing compound, is selected from carboxylates, alkoxides, β-diketone complexes, phosphates and phosphites. Among them, the carboxylates and phosphates are preferable, and the carboxylate is particularly preferred. The carboxylate of the rare earth element is represented by a general formula of (R 4 -CO 2 ) 3 M, wherein M is a rare earth element belonging to atomic numbers 57-71 in the Periodic Table and R 4 is a hydrocarbon group having a carbon number of 1-20, preferably a saturated or unsaturated and straight-chain, branched-chain or cyclic hydrocarbon group, to a primary, secondary or tertiary carbon atom of which is bonded a carboxyl group. Concretely, salts of octanoic acid, 2-ethylhexanoic acid, oleic acid, stearic acid, benzoic acid, naphthenic acid, and versatic acid (carboxylic acid wherein carboxyl group is bonded to a tertiary carbon atom, trade name made by Shell Chemical Corporation) are mentioned. Among them, salts of 2-ethyjhexanoic acid, naphthenic acid and versatic acid are preferable. The alkoxide of the rare earth element is represented by a general formula of (R 5 O) 3 M, wherein R 5 is a hydrocarbon group having a carbon number of 1-20 and M is a rare earth element belonging to atomic numbers 57-71 in the Periodic Table. As an example of a group represented by R 5 O, there are mentioned 2-ethyl-hexyl alkoxy group, oleyl alkoxy group, stearyl alkoxy group, phenoxy group, and benzyl alkoxy group. Among them, 2-ethyl-hexyl alkoxy group and benzyl alkoxy group are preferred. As the β-diketone complex of the rare earth element, there are mentioned acetylacetone complex, benzoylacetone complex, propionitorileacetone complex, valerylacetone complex, and ethylacetylacetone complex of the rare earth element. Among them, acetylacetone complex and ethylacetylacetone complex are preferred. As the phosphate or phosphite of the rare earth element, there are mentioned bis(2-ethylhexyl) phosphate, bis(1-methylheptyl)phosphate, bis(p-nonylphenyl) phosphate, bis(polyethylene glycol-p-nonylphenyl) phosphate, (1-methylheptyl)(2-ethylhexyl) phosphate, (2-ethylhexyl)(p-nonylphenyl) phosphate, 2-ethylhexyl, mono-2-ethylhexyl phosphonate, 2-ethylhexyl, mono-p-nonylphenyl phosphonate, bis(2-ethylhexyl) phosphite, bis(1-methylheptyl) phosphite, bis(p-nonylphenyl) phosphite, (1-methylheptyl)(2-ethylhexyl) phosphite and (2-ethylhexyl)(p-nonylphenyl) phosphite of the rare earth element. Among them, bis(2-ethylhexyl) phosphate, bis(1-methylheptyl) phosphate, 2-ethylhexyl, mono-2-ethylhexyl phosphite and bis(2-ethylhexyl) phosphite are preferred. Among the above rare earth element containing compounds, phosphates of neodymium and carboxylates of neodymium are preferable, and carboxylates of neodymium such as neodymium 2-ethyl-hexanoate and neodymium versatate are most preferable. In order to easily dissolve the rare earth element containing compound in a solvent or stably store over a long time of period, a Lewis base is used in an amount of 0-30 mole, preferably 1-10 mole per 1 mole of the rare earth element as a mixture of both compounds or a reaction product obtained by previously reacting both compounds. As the Lewis base, mention may be made of acetylacetone, tetrahydrofuran, pyridine, N,N-dimethylformamide, thiophene, diphenyl ether, triethylamine, an organophosphorus compound, and a monovalent or bivalent alcohol. The rare earth element containing compounds or reaction products thereof with Lewis base as the component (a) may be used alone or in admixture of two or more compounds and products. The aluminoxane (b) used in the catalyst according to the invention is a compound represented by the following general formula (I) or (II): wherein R 6 s are the same or different and are a hydrocarbon group having a carbon number of 1-20, and n is an integer of not less than 2. Also, it may be an association body of aluminoxanes described in Fine Chemical, 23, (9), 5 (1994), J. Am. Chem. Soc., 115, 4971 (1993) and J. Am. Chem. Soc., 117, 6465 (1995). In the aluminoxane of the formula (I) or (II), the hydrocarbon group represented by R 6 includes methyl group, ethyl group, propyl group, butyl group, isobutyl group, t-butyl group, hexyl group, isohexyl group, octyl group, and isooctyl group. Among them, methyl, ethyl, isobutyl and t-butyl groups are preferred, and methyl group is particularly preferred Also, n is 2 or more, preferably an integer of 4-100. As a concrete example of the aluminoxane (b), mention may be made of methylaluminoxane, ethylaluminoxane, n-propylaluminoxane, n-butylaluminoxane, isobutylaluminoxane, t-butylaluminoxane, hexylaluminoxane and isoheyxlaluminoxane. The aluminoxane (b) may be produced by any one of the conventionally known methods. For example, it can be produced by adding trialkylaluminium or dialkylaluminium monochloride to an organic solvent such as benzene, toluene, xylene or the like and then adding and reacting with water, steam, steam-containing nitrogen gas or a salt having water of crystallization such as copper sulfate pentahydrate or aluminium sulfate hexadecahydrate. The aluminoxanes (b) may be used alone or in an admixture of two or more compounds. Another component (b) used in the catalyst according to the invention is an organoaluminium compound represented by a general formula of AlR 1 R 2 R 3 , wherein R 1 and R 2 are the same or different and are a hydrogen atom and a hydrocarbon group having a carbon number of 1-10, and R 3 is a hydrocarbon group having a carbon number of 1-10, provided that R 3 is the same or different from R 1 and R 2 . As the organoaluminium compound, mention may be made of trimethylaluminium, triethylaluminium, tri-n-propylaluminium, triisopropylaluminium, tri-n-butylaluminium, triisobutyl-aluminium, tri-t-butylaluminium, tripentylaluminium, trihexylaluminium, tricyclohexylaluminium, trioctylaluminium, hydrogenated diethylaluminium, hydrogenated di-n-propylaluminium, hydrogenated di-n-butylaluminium, hydrogenated diisobutylaluminium, hydrogenated dihexylaluminium, hydrogenated diisohexylaluminium, hydrogenated dioctylaluminium, hydrogenated diisooctylaluminium, ethylaluminium dihydride, n-propylaluminium dibydride and isobutylaluminium dihydride.Among them, triethylaluminium, triisobutylaluminium, hydrogenated diethylaluminium and hydrogenated diisobutylaluminium are preferred. The organoaluminium compounds as the component (b) may be used alone or in admixture of two or more compounds. The component (c) used in the catalyst according to the invention is a halogen-containing metal compound, which is a reaction product between a metal halide and a Lewis base, diethylaluminium chloride, silicon tetrachloride, trimethyl chlorosilane, methyl dichlorosilane, dimethyl dichlorosilane, methyl trichlorosilane, ethylaluminium dichloride, ethylaluminium sesquichloride, tin tetrachloride, tin trichloride, phosphorus trichloride, benzoyl chloride and t-butylchloride. Among them, the reaction product between the metal halide and the Lewis base is preferable. The metal halide is selected from beryllium chloride, beryllium bromide, beryllium iodide, magnesium chloride, magnesium bromide, magnesium iodide, calcium chloride, calcium bromide, calcium iodide, barium chloride, barium bromide, barium iodide, zinc chloride, zinc bromide, zinc iodide, cadmium chloride, cadmium bromide, cadmium iodide, mercury chloride, mercury bromide, mercury iodide, manganese chloride, manganese bromide, manganese iodide, rhenium chloride, rhenium bromide, rhenium iodide, copper chloride, copper bromide, copper iodide, silver chloride, silver bromide, silver iodide, gold chloride, gold bromide, and gold iodide. Among them, magnesium chloride, calcium chloride, barium chloride, manganese chloride, zinc chloride and copper chloride are preferred and particularly magnesium chloride, manganese chloride, zinc chloride and copper chloride are particularly preferred. As the Lewis base used for producing the reaction product with the above metal halide, phosphorus compounds, carbonyl compounds, nitrogen compounds, ether compounds and alcohols are preferred. Concretely, they include tributyl phosphate, tri-2-ethylhexyl phosphate, triphenyl phosphate, tricresyl phosphate, triethyl phosphine, tributyl phosphine, triphenyl phosphine, diethyl phosphinoethane, diphenyl phosphinoethane, acetylacetone, benzoylacetone, propiontrileacetone, valerylacetone, ethylacetylacetone, methyl acetoacetate, ethylacetoacetate, phenyl acetoacetate, dimethyl malonate, diethyl malonate, diphenyl malonate, acetic acid, octanoic acid, 2-ethyl-hexanoic acid, oleic acid, stearic acid, benzoic acid, napthenic acid, versatic acid (carboxylic acid wherein carboxyl group is bonded to a tertiary carbon atom, trade name made by Shell Chemical Corporation), triethylamine, N,N-dimethyl acetoamide, tetrahydrofuran, diphenyl ether, 2-ethyl-hexylalcohol, oleyl alcohol, stearyl alcohol, phenol, benzyl alcohol, 1-decanol and lauryl alcohol. Among them, tri-2-ethylhexyl phosphate, tricresyl phosphate, acetylacetone, 2-ethyl-hexanoic acid, versatic acid, 2-ethylhexyl alcohol, 1-decanol and lauryl alcohol are preferred. The above Lewis base is reacted i n an amount of 0.01-30 moles, preferably 0.5-10 moles per 1 mole of the metal halide. When using the reaction product between the metal halide and the Lewis base, metal remaining in the polymer can be decreased. The amount and composition ratio of the components used in the invention are set to various different values in accordance with the use purpose and necessity. The amount of the component (a) is preferably 0.00001-1.0 mmol per 100 g of the conjugated diene compound. When the amount is less than 0.00001 mmol, the polymerization activity undesirably lowers, while when it exceeds 1.0 mmol, the catalyst concentration becomes undesirably high and the step of removing ash is required. More preferably, the component (a) is used in an amount of 0.0001-0.5 mmol. Also, the amount of the component (b) used can be represented by a molar ratio of Al to the component (a). The molar ratio of component (a) to component (b) is preferably 1:1-1:500, more preferably 1:3-1:250, more particularly 1:5-1:200. Moreover, a ratio of component (a) to component (c) is preferably 1:0.1-1:30, more preferably 1:0.2-1:15 as a molar ratio. When the amount or composition ratio is outside the above range, the resulting catalyst does not act as a high activity catalyst and a step of removing a catalyst residue is undesirably required. On the other hand, hydrogen gas for adjusting the molecular weight of the polymer can be used together with the catalyst consisting of the components (a), (b) and (c) to conduct the polymerization reaction. In addition to the above components (a), (b) and (c), a conjugated diene monomer and/or a non-conjugated diene compound may be used in an amount of 0-1,000 mol per 1 mol of the component (a), if necessary. As the conjugated diene compound used in the production of the catalyst, use may be made of the same monomer as used in the polymerization such as 1,3-butadiene and isoprene. As the non-conjugated diene compound, mention may be made of divinylbenzene, diisopropenyl benzene, triisopropenyl benzene, 1,4-vinylhexadiene, ethylidene norbornene and the like. The conjugated diene compound as a catalyst component is not essential, but has the merit of more improving the catalyst activity when it is used together with the components (a)-(c). The catalyst may be prepared by reacting the components (a)-(c) dissolved in a solvent or further with the conjugated diene compound and/or non-conjugated diene compound, if necessary. In this case, the addition order of these components is optional. It is preferred that these components are previously mixed and reacted and then maturated from the viewpoint of improvement of polymerization activity and shortening of polymerization induction period. The maturating temperature is 0-100°C, preferably 20-80°C. When the temperature is lower than 0°C, sufficient maturation is not conducted, while when it exceeds 100°C, the catalyst activity lowers and broadening of molecular weight distribution is undesirably caused. The maturating time is not particularly restricted, but is usually not less than 0.5 minute. The maturation may be conducted by contacting the components with each other in a line before the addition to a polymerization reaction vessel and is stable over several days. In the invention, the conjugated diene compound is polymerized by using the catalyst consisting essentially of the above components (a)-(c) . As the conjugated diene compound polymerizable with the catalyst according to the invention, mention may be made of 1,3-butadiene, 2-methyl-1,3-butadiene (isoprene), 2,3-dimethyl-1,3-butadiene, 1,3-pentadiene, 1,3-hexadiene, myrcene and cyclo-1,3-pentadiene. Particularly, 1,3-butadiene, isoprene and 1,3-pentadiene are preferred. These conjugated compounds may be used alone or in admixture of two or more compounds. When two or more compounds are used, a copolymer is obtained. The polymerization of the conjugated diene compound according to the invention can be carried out by using a solvent or in the absence of solvent. The polymerization solvent is an inert organic solvent, which includes, for example, a saturated aliphatic hydrocarbon having a carbon number of 4-10 such as butane, pentane, hexane or heptane; a saturated alicyclic hydrocarbon having a carbon number of 5-20 such as cyclopentane or cyclohexane; a mono-olefin such as 1-butene or 2-butene; an aromatic hydrocarbon such as benzene, toluene or xylene; and a halogenated hydrocarbon such as methylene chloride, chloroform, carbon tetrachloride, trichloroethylene, perchloroethylene, 1,2-dichloroethane, chlorobenzene, bromobenzene and chlorotoluene. These polymerization solvents may be used alone or in admixture of two or more solvents. The polymerization temperature is usually -30°C-200°C, preferably 0-150°C. The polymerization reaction may be batch or continuous. Moreover, it is necessary to sufficiently take care that a substance having a deactivation action such as oxygen, water, or carbon dioxide is not incorporated into the polymerization system in order to deactivate the catalyst of the rare earth element containing compound and the polymer. Since the specified catalyst is used in the invention, there can be obtained conjugated diene polymers having a high content of cis-1,4-bond and a sharp molecular weight distribution. Thus, the conjugated diene polymer obtained by using the catalyst consisting essentially of the components (a)-(c) before the modification has a content of cis-1,4-bond of not less than 85%, preferably not less than 90%, a content of 1,2-vinyl bond of not more than 2.0%, preferably not more than 1.5%, and a ratio Mw/Mn of not more than 5.0, preferably not more than 4.0. When the content of cis-1,4-bond in the conjugated diene polymer obtained before the modification is less than 85%, the mechanical properties and wear resistance are poor. Also, when the content of 1,2-vinyl bond exceeds 2.0%, the mechanical properties and wear resistance are poor. The adjustment of such a microstructure (content of cis-1,4-bond, content of 1,2-vinyl bond) can easily be conducted by controlling the polymerization temperature. On the other hand, when the ratio Mw/Mn of the conjugated diene polymer before the modification according to the invention exceeds 5.0, the mechanical properties and wear resistance are poor. The adjustment of such a ratio Mw/Mn can easily be conducted by controlling the molar ratio of the components (a)-(c). Moreover, the conjugated diene polymer before the modification preferably has a Moony viscosity (ML1+4, 100°C) of 10-100. When the Moony viscosity is less than 10, the mechanical properties and wear resistance after the vulcanization are poor, while when it exceeds 100, the processability in the kneading is poor and the mechanical properties are degraded. According to the invention, after the conjugated diene compound is polymerized by using the catalyst of the rare earth element containing compound, a compound having a specified functional group is subsequently added to an active terminal of the resulting living polymer to react (modify) the active terminal of the polymer with the compound having the specified functional group and increase the molecular weight of the polymer or branch the polymer chain, if necessary, whereby a polymer having a good interaction with silica is formed. By such a modification there is improved the interaction with silica to further improve the properties such as wear resistance, mechanical properties, low heat build-up and the like. In the invention, the component (d) to be reacted with the active terminal of the polymer is a vinyl compound containing a hydroxyl group in its molecule. As the component (d), mention may be made of hydroxymethyl (metha)acrylate, 2-hydroxyethyl (metha)acrylate, 2-hydroxypropyl (metha)acrylate, 3-hydroxypropyl (metha)acrylate, 3-chloro-2-hydroxypropyl (metha)acrylate, 3-phenoxy-2-hydroxypropyl (metha)acrylate, glycerol mono(metha)acrylate, hydroxybutyl (metha)acrylate, hydroxyhexyl (metha)acrylate, hydroxyoctyl (metha)acrylate, hydroxymethyl (metha)acrylamide, 2-hydroxyethyl (metha)acrylamide, 2-hydroxypropyl (metha)acrylamide, 3-hydroxypropyl (metha)acrylamide, di-(ethylene glycol) itaconate, di-(propylene glycol) itaconate, bis(2-hydroxypropyl) itaconate, bis(2-hydroxyethyl) itaconate, bis(2-hydroxyethyl) fumarate and bis(2-hydroxyethyl) maleate. The components (d) may be used alone or in admixture of two or more compounds. The component (e) to be reacted with the active terminal of the polymer is an epoxy compound, which includes, for example, styrene oxide, epoxidized soybean oil, glycidyl (metha)acrylate, allylglycidyl ether, vinylglycidyl ether, ethylene oxide, propylene oxide, 1,2-epoxybutane, 1,2-epoxy-i-butane, 2,3-epoxybutane, 1,2-epoxyhexane, 1,2-epoxyoctane, 1,2-epoxydecane, 1,2-epoxytetradecane, 1,2-epoxyhexadecane, 1,2-epoxyoctadecane, 1,2-epoxyeicosane, 1,2-epoxy-2-pentylpropane, 3,4-epoxy-1-butene, 1,2-epoxy-5-hexene, 1,2-epoxy-9-decene, 1,2-epoxy cyclopentane, 1,2-epoxy cyclohexane, 1,2-epoxy cyclododecane, 1,2-epoxy ethylbenzene, 1,2-epoxy-1-methoxy-2-methylpropane, glycidyl methyl ether, glycidyl ethyl ether, glycidyl isopropyl ether, glycidyl phenyl ether, glycidyl butyl ether, ethylene glycol diglycidyl ether, neopentyl glycol diglycidyl ether, trimethylol propane polyglycidyl ether, glycerol polyglycidyl ether, polypropylene glycol diglycidyl ether, polyethylene glycol diglycidyl ether, sorbitol polyglycidyl ether, N,N-diglycidyl aniline, N,N-diglycidyl toluidine, N,N-diglycidyl-3-glycidyloxyaniline, N,N-diglycidyl-2-glycidyloxyaniline, N,N,N',N'-tetraglycidyl aminodiphenyl methane, trisepoxypropyl isocyanurate, N,N-diglycidyl butylamine, N-glycidyl pyrolidine, N-glycidyl piperidine, N-glycidyl morpholine, N,N'-diglycidyl piperadine, N,N'-diglycidyl homopiperadine, N-glycidyl-N'-methyl piperadine, N-glycidyl-N'-benzyl piperadine and 2-diglycidylaminoethyl-N-methyl pyrrolidone. The components (e) may be used alone or in admixture of two or more compounds. Moreover, the compounds of the above components (d)-(e) (hereinafter referred to as a modifying agent) may be used alone or in admixture of two or more compounds. The amount of the modifying agent (d) and/or (e) used with respect to the component (a) is 0.01-200, preferably 0.1-150 as a molar ratio. When the amount is less than 0.01, the reaction insufficiently proceeds and also the interaction with silica is not sufficiently developed and the effect of improving the wear resistance and low heat build-up is not developed, while when it exceeds 200, the effect of improving the dispersibility of silica and the properties is saturated and insoluble matter in toluene (gel) is undesirably formed according to circumstances. It is desirable that the modification reaction is carried out at a temperature of not higher than 160°C, preferably -30°C to +130°C for 0.1-10 hours, more preferably 0.2-5 hours. After the completion of the modification, an objective polymer can be recovered by adding a short-stop, a polymerization stabilizer or the like to the reaction system, if necessary, and conducting well-known solvent-removing and drying operations in the production of the conjugated diene polymer. Moreover, the resulting polymer can be recovered by adding a process oil such as aromatic oil, or naphthenic oil prior to the solvent removal, if necessary, and then by the solvent-removing and drying operations. The conjugated diene polymer obtained according to the invention is used in rubber applications requiring mechanical properties and wear resistance such as tread, sidewall and various members in tires for passenger cars trucks and buses and tires for winter season such as studless tires, hoses, belts, vibration damping rubber and other industrial articles alone or by blending with other synthetic rubber or natural rubber and compounding with a process oil, if necessary, and further with a filler which is silica, a vulcanizing agent, a vulcanization accelerator and other additives and thereafter vulcanizing them. Also, it may be blended with emulsion-polymerized SBR, solution-polymerized SBR, polyisoprene, EP(D)M, butyl rubber, hydrogenated BR or hydrogenated SBR other than natural rubber. The conjugated diene polymer obtained is modified with the modifying agent having the specified functional group, so that the dispersibility of silica in the rubber composition is improved by bonding such a functional group to various functional groups existing on the surface of silica to conduct the interaction between silica and rubber. The rubber composition according to the invention is formed by using the above conjugated diene polymer alone as a starting rubber or blending it with other synthetic rubber or natural rubber and compounding with a process oil, if necessary, and adding silica as a filler and usual additives such as a vulcanizing agent, a vulcanization accelerator and the like thereto. In order to well develop the excellent properties of the conjugated diene polymer, such a polymer is included in the starting rubber at an amount of not less than 10% by weight, preferably not less than 20% by weight, more particularly not less than 30% by weight. Also, paraffinic, naphthenic, aromatic oils are mentioned as the process oil used for oil-extending or compounding. The amount used is not more than 80 parts by weight, preferably 20-60 parts by weight per 100 parts by weight of the starting rubber. As silica used, mention may be made of dry-process white carbon, wet-process white carbon, colloidal silica and precipitated silica. The wet-process white carbon consisting essentially of hydrous silicate is preferred. Silica preferably exists in an acidic zone for further improving the dispersibility. Also, silica treated with a coupling agent may be used. The specific surface area of silica is not particularly restricted, but is usually 50-400 m 2 /g, preferably 100-250 m 2 /g. When the specific surface area is too small, the reinforcing property is poor, while when it is too large, the processability is poor and the improvement of the wear resistance and rebound resilience is insufficient. The amount of silica used is 10-200 parts by weight, preferably 20-150 parts by weight per 100 parts by weight of the starting rubber. When it is less than 10 parts by weight, the reinforcing property is poor and the effect of improving the wear resistance and low heat build-up is not obtained, while when it exceeds 200 parts by weight, the viscosity of the uncured rubber composition rises and hence the processability, wear resistance and low heat build-up are poor. Moreover, a silane coupling agent may further be compounded in the rubber composition according to the invention. As the silane coupling agent, mention may be made of γ-mercaptopropyl trimethoxysilane, γ-aminopropyl triethoxysilane, bis[3-(triethoxysilyl)propyl] tetrasulfide, bis[3-(triethoxysilyl)propyl] disulfide, bis[3-(triethoxysilyl)propyl] trisulfide, tetrasulfides such as bis[3-(triethoxysilyl)propyl] tetrasulfide, γ-trimethoxysilylpropyl dimethylthiocarbamyl tetrasulfide and γ-trimethoxysilylpropyl benzothiazyl tetrasulfide. The amount of the silane coupling agent used is 1-20 parts by weight, preferably 1-15 parts by weight per 100 parts by weight of the starting rubber. When the amount is less than 1 part by weight, the reinforcing property with silica is not obtained and the breaking strength, wear resistance and low heat build-up are poor, while when the amount exceeds 20 parts by weight, it is uneconomical and the effect of improving the properties is saturated. As the vulcanizing agent there is usually used sulfur, an amount of which is 0.1-3 parts by weight, preferably 0.5-2 parts by weight per 100 parts by weight of the starting rubber. As the vulcanization aid and processing aid there is generally used stearic acid, an amount of which is 0.5-5 parts by weight per 100 parts by weight of the starting rubber. The vulcanization accelerator is not particularly restricted, but is preferably a thiazole based vulcanization accelerator such as M (2-mercaptobenzothiazole), DM (dibenzothiazyl disulfide), or CZ (N-cyclohexyl-2-benzothiazyl sulfenamide), in an amount of 0.1-5 parts by weight, preferably 0.2-3 parts by weight per 100 parts by weight of the starting rubber. If necessary, the rubber composition according to the invention may be compounded with an additive such as zinc oxide, antioxidant or antiozonant. The rubber composition according to the invention is obtained by kneading in a kneader such as rolls, or internal mixer, and shaped and vulcanized, and can be used not only for tire applications such as a tread, under-tread, carcass, sidewall or bead portion but also for industrial applications such as a hose, belt, shoe bottom, window frame, sealing member, or vibration damping rubber. Particularly, it is preferred to be used as a rubber for the tire tread. The following examples are given in illustration of the invention and are not intended as limitations thereof. In these examples, part and % are by weight unless otherwise specified. Also, various measurements in the examples are carried out by the following methods. Mooney viscosity (ML 1+4 ,100°C) It is measured at a temperature of 100°C for a measuring time of 4 minutes after preliminary heating for 1 minute. Number average molecular weight (Mn), weight average molecular weight (Mw): They are measured by using an apparatus of Model "HLC-8120GPC", made by Toso Co., Ltd., and a differential refractometer as a detector under the following conditions. Column: "Column GMHHXL", made by Toso Co., Ltd. Mobile phase: tetrahydrofuran Microstructure (content of cis-1,4-bond, content of 1,2-vinyl bond): It is measured by an infrared ray method (Morero's method). Tensile strength It is measured according to a method of JIS K6301. tan δ A value at 50°C is measured by using a mechanical spectrometer (made by Rheometric Corporation). Wear resistance It is evaluated at room temperature by using a Lambourn type abrasion testing machine (made by Shimada Giken Co., Ltd.) at a slip ratio of 60%. Example 1 Into an autoclave of 5 liters purged with nitrogen are charged 2.4 kg of cyclohexane and 300 g of 1,3-butadiene under a nitrogen atmosphere. A catalyst, which is obtained by previously reacting and maturing a cyclohexane solution of neodymium versatate (hereinafter abbreviated as Nd(ver) 3 ) (0.09 mmol), a toluene solution of methyl aluminoxane (hereinafter abbreviated as MAO)(7.2 mmol), hydrogenated diisobutylaluminium (hereinafter abbreviated as Al i Bu 2 H)(3.6 mmol) and a toluene solution of diethylaluminium chloride (hereinafter abbreviated as DEAC)(0.18 mmol) as a catalyst component with an amount of 1,3-butadiene corresponding to 5 times an amount of neodymium at 50°C for 30 minutes, is added to conduct polymerization at 80°C for 60 minutes. The conversion of 1,3-butadiene is approximately 100%. Then, the resulting polymer solution is kept at a temperature of 50°C and added with an epoxidized soybean oil (4.5 mmol) and reacted therewith for 30 minutes. Thereafter, a methanol solution containing 1.5 g of 2,4-di-tert-butyl-p-cresol is added to stop polymerization and the solvent is removed by steam stripping and the resulting reaction product is dried on rolls of 110°C to obtain a polymer. The polymerization conditions and analytical results are shown in Table 1. Example 2 The same procedure as in Example 1 is repeated except that silicon tetrachloride is used instead of diethylaluminium chloride. The polymerization conditions and analytical results are shown in Table 1. Example 3 The same procedure as in Example 1 is repeated except that a complex of zinc chloride and 1-decanol is used instead of diethylaluminum chloride. The polymerization conditions and analytical results are shown in Table 1. Example 4 The same procedure as in Example 3 is repeated except that styrene oxide is used instead of the epoxidized soybean oil. The polymerization conditions and analytical results are shown in Table 1. Example 5 The same procedure as in Example 3 is repeated except that 2-hydroxyethyl methacrylate (hereinafter abbreviated as HEMA) is used instead of the epoxidized soybean oil. The polymerization conditions and analytical results are shown in Table 1. Example 6 Into an autoclave of 5 liters purged with nitrogen are charged 2.4 kg of cyclohexane and 300 g of 1,3-butadiene under a nitrogen atmosphere. A catalyst, which is obtained by previously reacting and maturing a cyclohexane solution of neodymium versatate (0.37 mmol), a toluene solution of triisobutyl aluminium (hereinafter abbreviated as Al i Bu 3 )(11.1 mmol), hydrogenated diisobutylaluminium (3.7 mmol) and a toluene solution of diethylaluminium chloride (0.74 mmol) as a catalyst component with an amount of 1,3-butadiene corresponding to 5 times an amount of neodymium at 50°C for 30 minutes, is added to conduct polymerization at 80°C for 60 minutes. The conversion of 1,3-butadiene is approximately 100%. Then, the resulting polymer solution is kept at a temperature of 50°C and added with an epoxidized soybean oil (4.5 mmol) and reacted therewith for 30 minutes. Thereafter, a methanol solution containing 1.5 g of 2,4-di-tert-butyl-p-cresol is added to stop polymerization and the solvent is removed by steam stripping and the resulting reaction product is dried on rolls at 110°C to obtain a polymer. The polymerization conditions and analytical results are shown in Table 1. Example 7 The same procedure as in Example 6 is repeated except that styrene oxide is used instead of the epoxidized soybean oil. The polymerization conditions and analytical results are shown in Table 1. Example 8 The same procedure as in Example 6 is repeated except that HEMA is used instead of the epoxidized soybean oil. The polymerization conditions and analytical results are shown in Table 1. Comparative Example 1 Into an autoclave of 5 liters purged with nitrogen are charged 2.4 kg of cyclohexane and 300 g of 1,3-butadiene under a nitrogen atmosphere. A catalyst, which is obtained by previously reacting and maturing a cyclohexane solution of neodymium versatate (0.09 mmol), a toluene solution of methyl aluminoxane (7.2 mmol), hydrogenated diisobutylaluminium (3.6 mmol) and a toluene solution of diethylaluminium chloride (0.18 mmol) as a catalyst component with an amount of 1,3-butadiene corresponding to 5 times an amount of neodymium at 50°C for 30 minutes, is added to conduct polymerization at 80°C for 60 minutes. The conversion of 1,3-butadiene is approximately 100%. Then, a methanol solution containing 1.5 g of 2,4-di-tert-butyl-p-cresol is added to stop polymerization and the solvent is removed by steam stripping and the resulting reaction product is dried on rolls of 110°C to obtain a polymer. The polymerization conditions and analytical results are shown in Table 2. Comparative Example 2 The same procedure as in Comparative Example 1 is repeated except that silicon tetrachloride is used instead of diethylaluminum chloride. The polymerization conditions and analytical results are shown in Table 2. Comparative Example 3 The same procedure as in Comparative Example 1 is repeated except that a complex of zinc chloride and 1-decanol is used instead of diethylaluminium chloride. The polymerization conditions and analytical results are shown in Table 2. Comparative Example 4 Into an autoclave of 5 liters purged with nitrogen are charged 2.4 kg of cyclohexane and 300 g of 1,3-butadiene under a nitrogen atmosphere. A catalyst, which is obtained by previously reacting and maturing a cyclohexane solution of neodymium versatate (0.37 mmol), a toluene solution of triisobutyl aluminium (11.1 mmol), hydrogenated diisobutylaluminium (3.6 mmol) and a toluene solution of diethylaluminium chloride (0.74 mmol) as a catalyst component with an amount of 1,3-butadiene corresponding to 5 times an amount of neodymium at 50°C for 30 minutes, is added to conduct polymerization at 80°C for 60 minutes. The conversion of 1,3-butadiene is approximately 100%. Then, a methanol solution containing 1.5 g of 2,4-di-tert-butyl-p-cresol is added to stop polymerization and the solvent is removed by steam stripping and the resulting reaction product is dried on rolls of 110°C to obtain a polymer. The polymerization conditions and analytical results are shown in Table 2. Comparative Example 5 The same procedure as in Example 1 is repeated except that diethylaluminium chloride is not used. The polymerization conditions and analytical results are shown in Table 2. Comparative Example 6 The same procedure as in Example 6 is repeated except that diethylaluminium chloride is not used. However, the measurement of Mooney viscosity and evaluation on the properties of vulcanizate can not be carried out because the yield of the polymer is only 12 g. The polymerization conditions and analytical results are shown in Table 2. Comparative Example 7 The properties of a commercially available polybutadiene rubber (BR01, trade name, made by JSR Corporation) are shown in Table 2. Then, the evaluation of the properties is carried out by using the polymers of Examples 1-8 and Comparative Examples 1-7. A rubber composition containing silica is prepared by the following method. At first, the kneading is carried out according to the following compounding recipe A in a plastomill at a kneading start temperature of 110°C for 3.5 minutes. The resulting kneaded mass is again kneaded in a plastomill. In the rekneading, the kneading start temperature is 110°C and the kneading time is 2 minutes. Compounding Recipe A (part) polymer 100 silica ( ) 50 aromatic oil 10 stearic acid 2 antioxidant ( ) 1 Then, the kneaded mass is added with chemicals according to the following compounding recipe B and kneaded in a plastomill at a kneading start temperature of 80°C for 1 minute. The resulting rubber composition is vulcanized under pressure at 160°C for an optimum time to obtain a specimen of a vulcanizate. The properties of the thus vulcanized rubber are shown in Tables 1 and 2. Compounding recipe B (part) zinc white 2.5 vulcanization accelerator( ) 0.8 vulcanization accelerator( ) 1 vulcanization accelerator( ) 1 sulfur 1.3 As seen from Tables 1 and 2, Examples 1-5 improve the breaking strength, low heat build-up and wear resistance after the vulcanization as compared with Comparative Examples 1-3. That is, when hydroxyl group and/or epoxy group are introduced into the polymer, the reinforcing property with silica is improved and the properties of the vulcanizate are largely improved. Similarly, Examples 6-8 improve the breaking strength, low heat build-up and wear resistance after the vulcanization as compared with Comparative Example 4. That is, when the above functional groups are introduced into the polymer irrespectively of the catalyst composition, the properties of the vulcanizate are largely improved. It is understood from Comparative Example 5 that when the content of cis-1,4 bond is low and the content of 1,2-vinyl bond is high, the breaking strength, low heat build-up and wear resistance are considerably poor as compared with Examples 1-3. Examples 9-17. Comparative Examples 8-16 The polymer of each of Examples 5-7 and Comparative Examples 3 and 7 is blended with natural rubber or solution-polymerized SBR, which is vulcanized by the following compounding method to obtain a vulcanizate. At first, the kneading is carried out according to the following compounding recipe A in a plastomill at a kneading start temperature of 110°C for 3.5 minutes. The thus kneaded mass is again kneaded in a plastomill. In the rekneading, the kneading start temperature is 110°C and the kneading time is 2 minutes. Compounding recipe A (part) polymer ( 1) 100 silica ( 2) 50 aromatic oil 10 stearic acid 2 antioxidant ( ) 1 Then, the thus obtained mass is added with chemicals of the following compounding recipe B and kneaded in a plastomill at a kneading start temperature of 80°C for 1 minute. The thus obtained rubber composition is vulcanized under pressure at 160°C for an optimum time to obtain a specimen of a vulcanizate. The properties of the thus vulcanized rubber are shown in Table 3. Compounding recipe B (part) zinc white 2.5 vulcanization accelerator( 1) 0.8 vulcanization accelerator( 2) 1 vulcanization accelerator( 3) 1 sulfur 1.3 As seen from Table 3, Examples 9-14 improve the breaking strength, low heat build-up and wear resistance after the vulcanization as compared with Comparative Examples 11, 12 and 14. This shows that the properties are improved even when the polymer according to the invention is blended with natural rubber. However, when the amount of the polymer according to the invention is too small per 100 parts in total of the rubber ingredient, the effect of improving the properties is not sufficiently obtained as seen from Comparative Examples 8-10 and 13. Similarly, Examples 15-17 improve the breaking strength, low heat build-up and wear resistance after the vulcanization as compared with Comparative Examples 15-16. This shows that the properties are improved even when the polymer according to the invention is blended with the synthetic rubber instead of natural rubber. Examples 18-25. Comparative Examples 17-18 The polymer of each of Examples 5-7 and Comparative Example 3 is blended with natural rubber, which is vulcanized by the following compounding method to obtain a vulcanizate. At first, the kneading is carried out according to the following compounding recipe A in a plastomill at a kneading start temperature of 110°C for 3.5 minutes. The thus kneaded mass is again kneaded in a plastomill. In the rekneading, the kneading start temperature is 110°C and the kneading time is 2 minutes. Compounding recipe A (part) polymer 50 natural rubber 50 silica 10-130 aromatic oil 10 stearic acid 2 antioxidant 1 silane coupling agent 0 or 5 Then, the thus obtained mass is added with chemicals of the following compounding recipe B and kneaded in a plastomill at a kneading start temperature of 80°C for 1 minute. The thus obtained rubber composition is vulcanized under pressure at 160°C for an optimum time to obtain a specimen of a vulcanizate. The properties of the thus vulcanized rubber are shown in Table 4. Compounding recipe B (part) zinc white 2.5 vulcanization accelerator( ) 0.8 vulcanization accelerator( 1 vulcanization accelerator( ) 1 sulfur 1.3 As seen from Table 4, Examples 18-25 improve the breaking strength, low heat build-up and wear resistance after the vulcanization as compared with Comparative Examples 17-18. As seen from Examples 19, 21 and 22 and Comparative Examples 17-18, the rubber compositions containing the polymer according to the invention have properties after the vulcanization equal to or more than those of the rubber composition containing the unmodified polymer and the silane coupling agent and provide satisfactory properties even when the silane coupling agent is not added. Moreover, as seen from Examples 23-25, the properties after the vulcanization are further improved by adding the silane coupling agent to the rubber composition containing the polymer according to the invention during the compounding. The conjugated diene polymers according to the invention have a high content of cis-1,4-bond and a low content of 1,2-vinyl bond and have a narrow molecular weight distribution and have the specified functional group interacting with silica in their molecules. Therefore, the conjugated diene polymer according to the invention has excellent dispersibility of silica and provides a rubber composition having excellent wear resistance and mechanical strength and low heat build-up.

Claims: A rubber composition comprising 10-200 parts by weight of silica based on 100 parts by weight of rubber ingredient consisting of 10-100% by weight of a conjugated diene polymer having a content of cis-1,4-bond of not less than 85%, a content of 1,2-vinyl bond of not more than 2.0% and a ratio of weight average molecular weight (Mw) to number average molecular weight (Mn) of not more than 5, and containing at least one functional group selected from epoxy group and hydroxyl group in its molecule, and 90-0% by weight of another diene polymer or natural rubber; wherein said conjugated diene polymer is obtained by polymerizing a conjugated diene compound with a catalyst consisting essentially of the following components (a) to (c) and subsequently reacting with at least one compound selected from the group consisting of the following components (d) and (e): Component (a): a compound containing a rare earth element belonging to atomic numbers 57-71 in the Periodic Table, or a reaction product between such a compound and a Lewis base, wherein said compound containing the rare earth element as the component (a) is a carboxylate, an alkoxide, a β-diketone complex, a phosphate or a phosphite; Component (b): an aluminoxane and/or an organoaluminium compound having a general formula of A1R 1 R 2 R 3 , wherein R 1 and R 2 are the same or different and are a hydrogen atom and a hydrocarbon group having a carbon number of 1-10, and R 3 is a hydrocarbon group having a carbon number of 1-10, provided that R 3 is the same or different from R 1 and R 2 ; Component (c): a halogen-containing compound which is a reaction product between metal halide and Lewis base, diethylaluminium chloride, silicon tetrachloride, trimethyl chlorosilane, methyl dichlorosilane, dimethyl dichlorosilane, methyl trichlorosilane, ethylaluminium dichloride, ethylaluminium sesquichloride, tin tetrachloride, tin trichloride, phosphorus trichloride, benzoyl chloride and t-butylchloride; Component (d): a hydroxyl group-containing vinyl compound; Component (e): an epoxy compound. A rubber composition as claimed in claim 1, characterized in that said rare earth element constituting the component (a) is neodymium, praseodymium, cerium, lanthanum or gadolinium. A rubber composition as claimed in claim 1 or 2, characterized in that said aluminoxane as the component (b) is selected from the group consisting of methylaluminoxane, ethylaluminoxane, n-propylaluminoxane, n-butylaluminoxane, isobutylaluminoxane, t-butylaluminoxane, hexylaluminoxane and isohexylaluminoxane. A rubber composition as claimed in any of claims 1 to 3, characterized in that said halogen-containing compound (c) is a reaction product between a metal halide and a Lewis base. A rubber composition as claimed in claim 4, characterized in that said Lewis base is a phosphoric ester, a diketone compound, a carboxylic acid and/or an alcohol, and in that said metal halide constituting the component (c) is selected from the group consisting of beryllium chloride, beryllium bromide, beryllium iodide, magnesium chloride, magnesium bromide, magnesium iodide, calcium chloride, calcium bromide, calcium iodide, barium chloride, barium bromide, barium iodide, zinc chloride, zinc bromide, zinc iodide, cadmium chloride, cadmium bromide, cadmium iodide, mercury chloride, mercury bromide, mercury iodide, manganese chloride, manganese bromide, manganese iodide, rhenium chloride, rhenium bromide, rhenium iodide, copper chloride, copper bromide, copper iodide, silver chloride, silver bromide, silver iodide, gold chloride, gold bromide, and gold iodide. A rubber composition as claimed in any of claims 1 to 5, characterized in that said component (a) is used in an amount of 0.00001-1.0 mmol per 100 g of the conjugated diene compound. A rubber composition as claimed in any of claims 1 to 6, characterized in that a molar ratio of said component (a) to said component (b) is 1:1-1:500. A rubber composition as claimed in any of claims 1 to 7, characterized in that a molar ratio of said component (a) to said component (c) is 1:0.1-1:30. A rubber composition as claimed in any of claims 1 to 8, characterized in that said conjugated diene compound is selected from the group consisting of 1,3-butadiene, 2-methyl-1,3-butadiene (isoprene), 2,3-dimethyl-1,3-butadiene, 1,3-pentadiene, 1,3-hexadiene, myrcene and cyclo-1,3-pentadiene. A rubber composition as claimed in any of claims 1 to 9, characterized in that said compound as the component (d) or (e) is used in a molar ratio to said component (a) of 0.01-200. A rubber composition as claimed in any of claims 1 to 10, characterized by further comprising 1-20 parts by weight of a silane coupling agent based on 100 parts by weight of the rubber ingredient.

Inventors: HATTORI IWAKAZU, NONAKA KATSUTOSHI, SONE TAKUO, YAMAZAKI DAISUKE, HATTORI, IWAKAZU, NONAKA, KATSUTOSHI, SONE, TAKUO, YAMAZAKI, DAISUKE
Applicants: JSR CORP, JSR CORPORATION
Application year: 2000
Main classification: C08C19
IPC codes: C08L9, C08C19, C08L19, C08K3