BLOW MOLDING METHOD AND MACHINE FOR PRODUCING PASTEURIZABLE CONTAINERS

Abstract: A method for producing a biaxially oriented, heat set plastic container, including the steps of providing a plastic perform whithin a mold cavity; expanding and stretching the plastic preform into conformity with the surfaces defining the mold cavity to form abiaxially oriented plastic container; inducing crystallinity in the plastic container by using convection heat transfer to heat a surface of the plastic container to a temperature of at least 120 DEG C; and removing the plastic container from the mold cavity. The PET containers produced by the method have an average sidewall crystallinity greater than about 30 %, which allows the PET container to maintain its material integrity during any subsequent pasteurization or retort process of the contents in the PET container, and during shipment of the PET container.

Description: BLOW MOLDING METHOD AND MACHINE FOR PRODUCING PASTEURIZABLE CONTAINERS TECHNICAL FIELD OF THE INVENTION This invention generally relates to blow molding methods and machines for producing heat set plastic containers. More specifically, this invention relates to blow molding methods and machines for producing biaxially oriented plastic containers with high crystallinity sidewalls. BACKGROUND Recently, manufacturers of polyethylene terephthalate (PET) containers have begun to supply plastic containers for commodities that were previously packaged in glass containers. The manufacturers, as well as consumers, have recognized that PET containers are lightweight, inexpensive, recyclable, and manufacturable in large quantities. Manufacturers currently supply PET containers for various liquid commodities, such as juices. They also desire to supply PET containers for solid commodities, such as pickles. Many solid commodities, however, require pasteurization or retort, which presents an enormous challenge for manufactures of PET containers. Pasteurization and retort are both methods for sterilizing the contents of a container after it has been filled. Both processes include the heating of the contents of the container to a specified temperature, usually above 70°C, for duration of a specified length. Retort differs from pasteurization in that it also applies overpressure to the container. This overpressure is necessary because a hot water bath is often used and the overpressure keeps the water in liquid form above its boiling point temperature. These processes present technical challenges for manufactures of PET containers, since new pasteurizable and retortable PET containers for these food products will have to perform above and beyond the current capabilities of conventional heat set containers. Quite simply, the PET containers of the current techniques in the art cannot be produced in an economical manner such that they maintain their material integrity during the thermal processing of pasteurization and retort and during subsequent shipping. PET is a crystallizable polymer, meaning that it is available in an amorphous form or a semi-crystalline form. The ability of a PET container to maintain its material integrity is related to the percentage of the PET container in crystalline form, also known as the "crystallinity" of the PET container. Crystallinity is characterized as a volume fraction by the equation: Crystallinity = P ~ Pa where p is the density of the PET material; p a is the density of pure amorphous PET material (1.333 g/cc); and p c is the density of pure crystalline material (1.455 g/cc). The crystallinity of a PET container can be increased by mechanical processing and by thermal processing. Mechanical processing involves orienting the amorphous material to achieve strain hardening. This processing commonly involves stretching a PET container along a longitudinal axis and expanding the PET container along a transverse axis. The combination promotes biaxial orientation. Manufacturers of PET bottles currently use mechanical processing to produce PET bottles having roughly 20% crystallinity (average sidewall crystallinity). Thermal processing involves heating the material (either amorphous or semi- crystalline) to promote crystal growth. Used by itself on amorphous material, thermal processing of PET material results in a spherulitic morphology that interferes with the transmission of light. In other words, the resulting crystalline material is opaque (and generally undesirable as the sidewall of the container). Used after mechanical processing, however, thermal processing results in higher crystallinity and excellent clarity. The thermal processing of an oriented PET container, which is known as heat setting, typically includes blow molding a PET preform against a heated blow mold, at a temperature of 120 - 130°C, and holding the blown container for about 3 seconds. Manufacturers of PET juice bottles, which must be hot filled at about 85°C, currently use heat setting to produce PET juice bottles having a range of up to 25-30% crystallinity. Although these hot fill PET containers exhibit a significant improvement over the non-hot fill PET containers, they cannot maintain material integrity during the thermal processing of pasteurization and retort. A logical extension of this heat setting process involves blow molding a PET preform against a blow mold that is held at a considerably higher temperature, up to 250°C, as discussed in the Jabarin references (US 4,476,170 and US 4,512,948). In theory, a manufacturer using this process could produce a PET container having over 50% crystallinity which allows the PET container to maintain its material integrity properties during a subsequent pasteurization or retort process of the contents in the PET container as well as during any subsequent shipment of the PET container. However, once this heat setting process has been completed, the PET container must be removed from the mold. At a temperature around 250°C, upon removal of the PET container will instantly shrink and possibly collapse. Recognizing this disadvantage, the Jabarin references offer two options for removing the PET containers: (1) lowering the mold temperature to the point where the PET container may be removed without any deformation, and (2) removing the PET container while applying internal pressure sufficient to resist any subsequent shrinkage thereafter and reducing the pressure when the bottle has reached a self-sustaining temperature. Neither of these options are commercially feasible. The first option involves extremely long cycle times (unless expensive liquid nitrogen machinery is employed) while the second option involves extremely complex processing to control the inherent variability of the system. Thus, the manufacturers of PET containers desire an efficient and inexpensive method and apparatus that produces PET containers having average sidewall crystallinities greater than 30%, which allow the PET containers to maintain their material integrity during any subsequent pasteurization or retort of the contents in the PET container, and during shipment of the PET containers. It is therefore an object of this invention to provide such a container that overcomes the problems and disadvantages of the conventional techniques in the art. SUMMARY OF THE INVENTION Accordingly, this invention provides for a blow molding method and machine that produces PET containers having average sidewall crystallinities of at least 30%, which allow the PET containers to maintain their material integrity during any subsequent high performance pasteurization or retort of the contents in the PET containers, and during shipment of the PET containers. As used herein, "high performance" pasteurization and retort are pasteurization and retort processes where the container is exposed to temperatures greater than about 80°C. At its broadest, the invention is a method for producing a heat set plastic container including the steps of providing a plastic preform within a mold cavity; expanding and stretching the plastic preform into conformity with surfaces defining the mold cavity; and inducing crystallinity in the plastic container by heating an interior surface of the plastic container. The invention also includes a blow molding machine for producing blow molded heat set containers from plastic preforms according to the method mentioned above. Briefly, the machine includes a blow mold having portions defining a mold cavity which is capable of receiving a plastic preform. A high-pressure fluid source and a high-temperature fluid source communicate with a blow core assembly that is movable to engage the plastic preform when the plastic preform is received within the mold cavity. The blow core assembly also includes at least one inlet port communicating the high-pressure fluid source and the high-temperature source with an interior of the plastic preform. The blow core assembly further includes an exhaust port coupled to an exhaust valve which has an open position to permit the exhausting of fluid through the exhaust valve. The exhaust valve also has a closed position to prevent the exhausting of fluid through the exhaust port. A controller coupled to the high-pressure fluid source selectively controls the supplying of high- pressure fluid to the blow core assembly. The controller is also coupled to the high- temperature fluid source to selectively control the supplying of high-temperature fluid to the blow core assembly. The controller is further coupled to the exhaust valve to control the position of the exhaust valve. During heating, the interior surface of the container may be heated to at least 120°C to achieve the objects set out above. Further features and advantages of the invention will become apparent from the following discussion and accompanying drawings. BRIEF DESCRIPTION OF THE DRAWINGS FIGS. 1-4 are schematic cross-sectional views of a portion of a blow molding machine of the present invention during various stages and processes taken along a line generally bisecting the blow molding machine; FIG. 5 is a timing chart for the control valves of the blow molding machine according to the blow molding method of the present invention; FIG. 6 is a schematic cross-sectional view of a portion of another embodiment of the present invention; and FIG. 7 is a timing chart for the embodiment shown in FIG. 6. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENT As shown in FIG. 1 , the blow molding machine of the present invention has a blow molding station 10 that generally includes a blow mold 12, a neck ring 13, a blow core assembly 14, a stretch rod 16, and a heating element 18. While the machine itself will have other stations and components, those are conventional in nature and need only be briefly discussed below. Two styles of blow molding machines exist, one-step machines and two-step machines. The difference between them is that in a one-step machine, a plastic preform is both injection molded and blow molded while in a two-step machine, an already formed plastic preform is fed into the machine and then blow molded. Each machine includes various stations. The number and type of these stations will differ from machine to machine. Generally, the stations may include either a preform injection molding station or a preform infeed station, a preform conditioning station, a blow mold station and a bottle outtake station. The present invention particularly involves the blow molding station 10 of either a one or two-step machine. As such, only the blow molding station 10 is described in detail. The blow mold 12 itself includes two separable halves (hydraulically or pneumatically controlled, the actuators not being shown) that cooperate to define a mold cavity 20, which functions to receive a plastic preform 22 conditioned for blow molding. The blow mold 12 is made from appropriate materials, such as steel, to withstand and to hold temperatures of about 120-250°C, typically 130-170°C. The mold cavity 20 is designed with an appropriate shape to ultimately define the contours of the exterior surface of the desired plastic container. The neck ring 13 (also hydraulically or pneumatically actuated, the actuators not being shown) is located above the blow mold 12 and adapted to receive, hold and position the plastic preform 22 in an appropriate location relative to the mold cavity 20 during the blow molding and heat setting processes. To accomplish this function, the neck ring 13 defines an annular receiving cavity 28 of a shape and size to receive the neck of the plastic preform 22. The blow core assembly 14 engages the top of the plastic preform 22 to allow for the injection of a fluid medium into the plastic preform 22. To accomplish this function, the assembly 14 includes a blow core manifold 15 to which is mounted, in a conventional manner, a blow seal 31. The blow seal 31 defines an annular channel 32 that communicates with a first inlet port 24 and a second inlet port 26, as further discussed below. The neck ring 13, as well as the blow core manifold 15 and the blow seal 31 , are all made from a strong material, such as steel. The stretch rod 16, also a part of the blow core assembly 14, extends generally through the center of the blow core manifold 15 and is movable from a retracted position, as shown in FIG. 1 , to an extended position, as shown in FIG. 2. The stretch rod 16 functions to stretch the plastic preform 22 along a longitudinal axis and to induce axial orientation into the plastic material of the plastic preform 22. In the preferred embodiment of the present invention, the stretch rod 16 includes several exhaust ports 34. The exhaust ports 34 function to exhaust fluids from the plastic preform 22, as further explained below. The exhaust ports 34 communicate with a channel 35 inside the stretch rod 16 to convey the fluids to an exhaust area (not shown). The stretch rod 16 is made from a strong material, such as steel. As shown in FIGS. 1 and 3, the first inlet port 24 is connected to a high-pressure conduit 36, which supplies a high-pressure fluid 38 from a high-pressure fluid source 39. The high-pressure fluid 38 functions to expand the plastic preform 22 against the mold cavity 20 and to thereby form a biaxially oriented plastic container 40 in a process commonly referred to as blow molding. A control valve 42 controls the flow of the high-pressure fluid 38. The control valve 42 may be either manually or electronically controlled, but in the preferred embodiment the control valve 42 is automatically and systematically controlled by a system controller 43, as further explained below. The high-pressure conduit 36 is made from a flexible material, which permits movement and retraction of the blow core assembly 14 as it engages and disengages during the blow molding process. As shown in FIGS. 1 and 4, the second inlet port 26 is connected to a high- temperature conduit 44, which supplies a high-temperature fluid 46 from a high-temperature fluid source 47. The high-temperature fluid 46 functions to heat set the plastic container 40, through a convection heat transfer, and to thereby form a biaxially oriented, heat set plastic container 40. The term "convection heat transfer" is defined as the transfer of heat from a fluid to a solid, by way of the fluid flowing over or near the surface of the solid. "Convection heat transfer" actually includes both a conductive heat transfer and a convection heat transfer, but the combination of these two heat transfers is commonly referred to as simply "convection heat transfer." The high-temperature fluid 46 may include air, steam, water, or any other fluid capable of transferring heat energy to the plastic container 40. To supply the high-temperature fluid 46, a fluid from a fluid source 49 is passed through a filter 50 and the heating element 18. The heating element 18 may be one of a well-known variety, such as an electrical resistance heater, which may contain a ferrous alloy wound around a ceramic rod (not shown). A person of ordinary skill in the art will readily appreciate the various types of filters and heating elements capable of being used with the invention to produce the desired effects. In the preferred embodiment, the heating element 18 is small in size and high in intensity to heat the fluid from ambient air temperature to roughly the 370°C temperature of the high-temperature fluid 46. Located between the heating element 18 and the second inlet port 26 is a control valve 52 and a check valve 54. Like the control valve 42, the control valve 52 controls the flow of the high-temperature fluid 46 and may be either manually or electronically controlled. In the preferred embodiment, the control valve 52 is automatically and systematically controlled by the system controller 43, as further explained below. The check valve 54 functions to prevent the high-pressure fluid 38 from traveling through the second inlet port 26 and into the high-temperature conduit 44. A person of ordinary skill in the art will readily appreciate the appropriate control valves and check valves. The method of the present invention for producing a biaxially oriented, heat set plastic container having a sidewall with a high crystallinity generally includes blow molding process and a heat setting process. The blow molding process includes providing a properly conditioned plastic preform 22 in the mold cavity 20 of the blow mold 12 and closing the blow mold 12. The plastic preform 22 is preferably made from PET, but may be made from other crystallizable materials. The blow core assembly 14 is next lowered into the plastic preform 22 such that a collar 33 of the blow seal is positioned interiorly of the finish or neck of the plastic preform 22 and a flange 37 engages the top of the plastic preform 22, as shown in FIG. 1. The stretch rod 16 is then moved by the pneumatic or hydraulic actuator from its retracted position to its extended position, as shown in FIG. 2. This extension of the stretch rod 16 into the plastic preform 22 axially stretches the sidewall 56 of the plastic preform 22, and triggers the start of the fluid cycle. The fluid cycle includes the opening and closing of the control valves 42 and 52 and a control valve 58, to blow mold the plastic preform 22 and to circulate the high-temperature fluid 46 over an interior surface 59 of the plastic preform 22, as shown in FIGS. 2-4. The extension of the stretch rod 16 starts the fluid cycle at time=to, as shown in FIG. 5. After the time delay 62 from time=t 0 to time=t 1 , the control valve 52 is opened and the high- temperature fluid 46 is injected through the second inlet port 26, through the annular channel 32, and into the plastic preform 22. The pre-blow stage 64 occurs during stretching of the plastic preform 22 and operates to keep the stretching plastic preform 22 from contacting the stretch rod 16. The pre-blow stage 64 is in preparation for the blow molding process 66 and is of relatively short duration. At time=t 2 , the control valve 42 is opened and the high- pressure fluid 38 is injected through the first inlet port 24, through the annular channel 32, and into the plastic preform 22. This blow molding process 66 occurs when the plastic preform 22 is pinned against the bottom of the blow mold 12 by the stretch rod 16. As the high-pressure fluid 38 is injected into the plastic preform 22, while the high-temperature fluid 46 is not turned off via the control valve 52, the high-pressure fluid 38 causes the check valve 54 to close, effectively shutting off the high-temperature fluid 46, as shown by the dashed lines in FIG. 5. The high-pressure fluid 38, which is preferably at a pressure of 500- 600psi, inflates and expands the plastic preform 22 against the mold cavity 20 of the blow mold 12. As the plastic preform 22 is stretched and expanded, it forms the biaxially oriented plastic container 40. Throughout the blow molding process 66, the blow mold 12 is held at a temperature of around 120-250°C, preferably 130-170°C. Once the plastic container 40 has been fully stretched and expanded, at time=t 3 , the control valve 58 is opened and the control valve 42 is closed, while the control valve 52 remains open. During the circulation process 68, the high-pressure fluid is exhausted through the exhaust ports 34 of the stretch rod 16. More importantly, the control valve 52 and the control valve 58 cooperate to circulate the high-temperature fluid 46 over an interior surface 60 of the sidewall 56 of the plastic container 40. The high-temperature fluid 46 exhausts through the exhaust ports 34, through the channel 35 in the stretch rod 16, past the control valve 58, and into the exhaust area (not shown). The high-temperature fluid 46 may be recycled through the filter 50 and the heating element 18 to conserve energy. The high-temperature fluid 46 is circulated over the interior surface 60 of the plastic container 40 for a sufficient duration to allow the interior surface 60 of the plastic container 40 to reach a temperature of at least 120°C. The duration will depend on the composition of the high-temperature fluid 46, the temperature and pressure of the high-temperature fluid 46, and the flow rate of the high-temperature fluid 46 over the interior surface 60. In the preferred method, the high-temperature fluid 46 is air, at a temperature between 200 to 400°C, preferably 285 to 370°C, and at a pressure typically between 100 to 300 psi, preferably 250 to 300 psi, but pressures up to 600 psi may be used. Other fluids, such as steam, may be used, as well as higher temperatures and pressures. At the preferred values, the high-temperature fluid 46 is circulated over the interior surface 60 of the plastic container 40 for 1 to 15 seconds, preferably 3 to 7 seconds, in order to transfer the necessary heat energy and in order to induce the appropriate amount of crystallinity into the plastic container 40. After the conclusion of the circulation process 68, at time^, the control valve 52 is closed and the control valve 42 is opened. During the cooling process 70, the cooler high- pressure fluid 38 is circulated over the interior surface 60 to reduce the temperature of the plastic container 40. The temperature of the plastic container 40 must be reduced to a temperature that allows the plastic container 40 to be removed from the mold cavity 20 without any shrinkage or other deformation. After the cooling process 70, the control valve 42 is closed and shortly thereafter, as the final stage 72, the high-pressure fluid 38 is exhausted, the control valve 58 is closed, the mold cavity 20 is opened, and the plastic container 40 is removed. This entire process is then repeated for the subsequent production of further plastic containers. Since the entire process can be completed in about 6 seconds, the process provides an efficient and inexpensive method for producing plastic containers having a high crystallinity, which allows the plastic containers to maintain their material integrity during any subsequent pasteurization or retort of its contents, and during shipment. Using the method of the invention, the plastic container 40 can be produced having a sidewall 56 with an average density greater than 1.367 g/cc. This average density roughly corresponds to a 30% crystallinity and will allow the plastic containers 40 to maintain its material integrity during subsequent high performance pasteurization or retort of the contents in the plastic containers 40, and during shipment of the plastic containers 40. As used herein, crystallinities greater than 30% are considered "high crystallinities". Other average densities greater than 1.367 g/cc, including 1.375 g/cc (roughly corresponding to 34.4% crystallinity), 1.38 g/cc (roughly corresponding to 38.5% crystallinity), 1.385 g/cc (roughly corresponding to 42.6% crystallinity), and even 1.39 g/cc (roughly corresponding to 46.7% crystallinity) are possible with the method of the present invention and without significantly impacting the visually perceptible transparency or clarity of the plastic containers 40. As shown in FIG. 6, an alternative embodiment of the invention is particularly adaptable to multi-cavity machines, which have more than one mold cavity where stretching and blowing occurs simultaneously. In this embodiment, the high-temperature fluid 46 and the high-pressure fluid 38 are provided as in the first embodiment (and therefore attention is directed to the discussion above regarding the same) except that they communicate through the stretch/blow rod 16 ' . Located along the length of a stretch/blow rod 16 ' are a large number of small diameter blow ports 74, preferably all of the same diameter. The ports 74 direct the high-temperature fluid 46 to the interior surface of the plastic preform and direct the high-pressure fluid 38 to the interior surface 60 of the plastic container 40, generally in a perpendicular direction. The consistent and small diameter of the ports 74 enhances the velocity at which the fluids are introduced and further allows for a more even discharge of the fluids along the length of the stretch/blow rod 16 ' . Exhausting of the high-temperature fluid 46 and the high-pressure fluid 38 is accomplished through a channel 76 formed within the blow seal 31. An exhaust valve 78, controlled by the system controller 43, is opened when necessary during the blow molding process. A muffler or silencer 80 may be mounted at the end of the exhaust line 82 to reduce noise during exhausting. Another variance from the first embodiment is that the pre-blow fluid is no longer provided through the high-temperature fluid 46. Instead, a low pressure, low temperature fluid 84 is provided from a source 86 through a line 88 and into the plastic preform 22 through a channel 90, also formed in the blow seal 31. As shown in FIG. 6, the pre-blow fluid 84, preferably air at ambient temperature and at about 200 psi, is provided by the opening of a control valve 92 by the system controller 43 during advancement of the stretch/blow rod 16 ' and stretching of the plastic preform 22. For maximum control of the pre-blow fluid 84, one control valve 92 is used for each mold cavity of the machine 10. As shown in FIG. 7, at time^, the control valve 92 is opened and pre-blow fluid 84 is injected through the channel 90 into the plastic preform 22. This pre-blow stage 64 ' occurs during stretching of the plastic preform 22 and operates to keep the plastic preform 22 from contacting the stretch/blow rod 16 ' . At time=t 2 , the control valve 92 is closed and the control valve 42 is opened to inject the high-pressure fluid 38 through the stretch/blow rod 16 ' and to inflate and expand the plastic preform 22 against the mold cavity 20 thereby forming the plastic container 40. At time=t 3 , the control valve 42 is closed. Preferably, at sometime between time=t 1 and time=t 3 , the control valve 52 is opened by the system controller 43. In this manner, when the control valve 42 is closed at time=t 3 , the high-temperature fluid 46 immediately flows through the ports 74 and is directed at the interior surface 60 of the plastic container 40. The remainder of the process sequence is as described above and reference should be made to that portion of this description. The foregoing discussion discloses and describes a preferred embodiment of the present invention. One skilled in the art will readily recognize from such discussion, and from the accompanying drawings and claims, that changes and modifications can be made to the invention, including varying the timing sequence, without departing from the true spirit and fair scope of the invention as defined in the following claims.

Claims: CLAIMS We claim: 1. A method of producing a heat set plastic container comprising the steps of: providing a plastic preform within a mold cavity; expanding and stretching the preform into conformity with surfaces defining the mold cavity; and inducing crystallinity in the plastic container by applying heat from an interior portion of the plastic container to an interior surface of the plastic container to raise the temperature of the interior surface to at least 120° C. 2. The method of Claim 1 wherein said inducing step includes using convection heat transfer to heat the interior surface of the plastic container. 3. The method of Claim 1 wherein said inducing step includes circulating a high- temperature fluid through the interior portion of the plastic container. 4. The method of Claim 3 wherein the high-temperature fluid includes air. 5. The method of Claim 3 wherein the high-temperature fluid has a temperature in the range of 200°C to 400°C. 6. The method of Claim 3, wherein the high-temperature fluid is at a pressure in the range of 100psi to 600psi. 7. The method of Claim 3 wherein the high-temperature fluid is introduced for a duration in the range of 1 second to 15 seconds. 8. The method of Claim 3 wherein said inducing step includes circulating the high-temperature fluid into and out of the interior of the plastic container. 9. The method of Claim 8 wherein said circulating of the high-temperature fluid is done continuously during said inducing step. 10. The method of Claim 3, wherein said circulating of the high-temperature fluid includes introducing the high-temperature fluid into the plastic container while also exhausting the high-temperature fluid from the plastic container. 11. The method of Claim 10 wherein said introducing of the high-temperature fluid occurs simultaneously with said exhausting of the high-temperature fluid. 12. The method of Claim 3 wherein said circulating of the high-temperature fluid includes directing the high-temperature fluid toward the interior surface of the plastic container. 13. The method of Claim 12 wherein said directing of the high-temperature fluid includes directing the high-temperature fluid substantially perpendicular to the interior surface of the plastic container. 14. The method of Claim 1 wherein said inducing step produces a plastic container having a sidewall with an average density in the range of 1.367 g/cc to 1.40g/cc. 15. The method of Claim 1 wherein said inducing step is performed while the plastic container remains within the mold cavity. 16. The method of Claim 1 wherein said surfaces defining said mold cavity have a temperature in the range of 120°C to 250°C. 17. A blow molding machine for producing a heat set container, said machine comprising: a blow mold defining a mold cavity capable of receiving a preform; a high-pressure fluid source; a high-temperature fluid source; a blow core assembly engagable with the preform and coupled to said high- pressure source and to said high-temperature source to supply high-pressure fluid and high- temperature fluid to an interior portion of the preform, said blow core assembly having an exhaust to exhaust fluid from the interior portion of the preform; and a controller coupled to said high-pressure fluid source and to said high- temperature fluid source to selectively control the supply of high-pressure fluid and high- temperature fluid, said controller further coupled to said exhaust to selectively control the fluid exhaust. 18. The blow molding machine of Claim 17 wherein said blow core assembly further includes a stretch rod which is movable from a retracted position to an extended position to axially stretch the preform. 19. The blow molding machine of Claim 18 wherein said stretch rod includes an interior channel coupled to said exhaust. 20. The blow molding machine of Claim 18 wherein said stretch rod includes an interior channel coupled to at least one of said high-temperature fluid source and said high- pressure fluid source, said stretch rod further including at least one port to supply fluid to the interior portion of the preform. 21. The blow molding machine of Claim 20 wherein said port is oriented to supply fluid in a direction substantially perpendicular to an interior surface of the preform. 22. The blow molding machine of Claim 17 wherein said high-pressure fluid source supplies high-pressure fluid at a pressure in the range of 100psi to 600psi. 23. The blow molding machine of Claim 17 wherein said high-temperature fluid source supplies high-temperature fluid at a temperature in the range of 200°C to 400°C. 24. The blow molding machine of Claim 17 further comprising a pre-blow fluid source to supply a pre-blow fluid, said blow core assembly being coupled to said pre-blow fluid source to supply the pre-blow fluid to the interior portion of the preform.

Inventors: BOYD TIMOTHY J, VAILLIENCOURT DWAYNE G, BOYD, TIMOTHY, J., VAILLIENCOURT, DWAYNE, G.
Applicants: BOYD TIMOTHY J, SCHMALBACH LUBECA, VAILLIENCOURT DWAYNE G, BOYD, TIMOTHY, J., SCHMALBACH-LUBECA AG, VAILLIENCOURT, DWAYNE, G.
Application year: 2000
Main classification: B29C49
IPC codes: B29C35, B29C49