IONICALLY CONDUCTIVE POLYMER, POLYMER ELECTROLYTE, AND ELECTRICAL DEVICE

Abstract: A polymeric electrolyte which is improved in a transport rate of charge carrier ions by containing a boron atom-containing polymeric compound and an electric device using the same are provided. As the boron-containing polymeric compound, any of the following (A) to (D) can be used. (A) Compound represented by the following general formula (1) wherein X represents a hetero-atom, R represents a divalent to hexavalent group having a molecular weight of at least 150, m represents an integer of 1 to 5, and n represents a recurring number of 1 or more. (B) Compound obtained by crosslinking a compound represented by the following general formula (7) wherein X represents a hetero-atom, R represents a divalent group having a molecular weight of at least 150 , and Y represents a polymerizable functional group. (C) Compound in which a boron atom is present in, for example, a polymeric side chain, preferably in an end of a polymeric main chain and/or a polymeric side chain as a part of a boron compound, more preferably in an end of a polymeric side chain as a part of an organoboron compound. (D) Tetravalent boron-containing polymeric compound.

Description: Technical Field The present invention relates to a novel ion-conductive polymeric compound, a polymeric electrolyte and an electric device using the same. Background of the Invention According to the development of cells having a high voltage and a high capacity, a large number of various polymeric electrolytes have been proposed. However, polymeric electrolytes have an ionic conductivity which is lower than that of aqueous electrolytes by more than one figure. Further, for example, a polymeric electrolyte using polyethylene glycol has defects that it is low in transfer and transport rates of charge carrier ions. Thus, attempts of improvement have been made by using various methods. In view of the foregoing, the invention has been made, and it aims to provide a polymeric electrolyte which is improved in a transport rate of charge carrier ions. Moreover, the invention provides a novel ion-conductive polymeric compound used in the polymeric electrolyte, and further an electric device such as a cell or the like, which is improved in performance by using the polymeric electrolyte. Mehta et al., Chemistry Letters 1997, p. 915-916, and EP 898 319 A1 disclose compounds comprising boroxine rings used as ion conductors. GB 1 076 379 A discloses boron containing compounds containing boron clusters, i.e. multiple directly connected boron atoms. US 4,620,944 and US 4,091,022 disclose boron compounds with boron atoms at crosslinked points of the polymer. Disclosure of the Invention The present inventors have assiduously conducted investigations to solve the problems, and have consequently found that dissociation of an electrolytic salt can be expedited by using a polymeric compound having a trivalent boron atom in the structure (hereinafter referred to as a trivalent boron-containing polymeric compound or an ion-conductive polymeric compound) which is a Lewis acid and a transport rate of charge carrier ions can be controlled by trapping counter ions of charge carrier ions in the polymeric chain. The invention is based on these findings. That is, in the ion-conductive polymeric compound of the invention, one or more trivalent boron atoms are present in the polymeric structure. Specific examples thereof include the following two. The first compound is that obtained by crosslinking a compound represented by the following general formula (7). In formula (7), X represents a hetero-atom, R represents a divalent group having a molecular weight of at least 150, and Y represents a polymerizable functional group. The compound is further defined below. The second compound is a compound in which a boron atom is present in a polymeric side chain, said compound being obtained as defined further below. The polymeric electrolyte of the invention contains one or more of the foregoing ion-conductive polymeric compounds and an electrolytic salt and further, as required, a nonaqueous solvent. As the electrolytic salt, for example, a lithium salt is used, and as the nonaqueous solvent, for example, an aprotic solvent is used. Moreover, the electric device of the invention uses any of the polymeric electrolytes. For example, when the electric device is a cell, a positive electrode and a negative electrode are linked through any of the polymeric electrolytes. Best Mode For Carrying Out the Invention Preferable embodiments of the invention are described below. However, the invention is not limited thereto. 1. Boron-containing polymeric compound (1) First ion-conductive polymeric compound The first ion-conductive polymeric compound is obtained by crosslinking a compound represented by the following general formula (7). In formula (7), X represents a hetero-atom, R represents a divalent group having a molecular weight of at least 150, and Y represents a polymerizable functional group. R in general formula (7) is a polymer or a copolymer of compound (A) represented by formula (2) and/or compound (B) represented by formula (3), wherein R 1 represents a methyl group, an ethyl group, a propyl group, a butyl group or a group represented by the following formula (4). -CH 2 O-[-CH 2 CH 2 O-] r -Ra wherein r represents 0 or an integer of 1 or more, and Ra represents a methyl group, an ethyl group, a propyl group or a butyl group; and wherein Y is selected from the group consisting of acryloyl, methacryloyl, allyl and vinyl. The molecular weight of R in formula (7) is at least 150, preferably at least 150 and at most 1,700,000. The compound represented by general formula (7) is especially preferably a compound represented by the following general formula (8). In formula (8), R represents the divalent group having a molecular weight of at least 150, represented by formula (6), and Y represents a polymerizable functional group. The molecular weight of R is at least 150 and at most 1,700,000. wherein R 1 represents a methyl group, an ethyl group, a propyl group or a butyl group or a group represented by the following formula (4), p represents an integer of 0 to 38,000, and q represents an integer of 0 to 28,000, .provided p and q are not 0 at the same time -CH 2 O- [-CH 2 CH 2 O-] r -Ra wherein r represents 0 or an integer of 1 or more, and Ra represents a methyl group, an ethyl group, a propyl group or a butyl group. The polymerizable functional group Y in formulas (7) and (8) are selected from an acrylic residue, a methacrylic residue, an allyl group and a vinyl group. (2) Second ion-conductive polymeric compound The second ion-conductive polymeric compound is, as mentioned above, for example, a compound in which one or more boron atoms are present in a polymeric side chain. The second ion-conductive polymeric compound is obtained by polymerizing a mixture of compounds represented by the following general formulas (9) and (10). In formula (9), R 1 represents a divalent group having a molecular weight of at least 100, and R 2 in formula (10) represents a divalent group having a molecular weight of at least 150. With respect to the molecular weights of the two, preferably, that of R 1 is at least 100 and at most 1,700,000, and that of R 2 is at least 150 and at most 1,700,000. The mixing ratio of the compounds represented by formulas (9) and (10) is 1/99 to 99/1, preferably 10/90 to 90/10 in terms of a weight ratio. R 1 in formula (9) and/or R 2 in formula (10) are a polymer or a copolymer of compound (A) represented by formula (2) and/or compound (B) represented by formula (3) as defined above, most preferably a compound represented by formula (6) as defined above. In formulas (9) and (10), Y represents a polymerizable functional group selected from the group consisting of a (meth)acrylic residue, an allyl group and a vinyl group. In formula (9), R 11 and R 12 , which may be the same or different, each represent a hydrogen atom, a halogen atom or a monovalent group. Examples of the monovalent group include an alkyl group, an alkoxy group, an aryl group, an alkenyl group, an alkinyl group, an aralkyl group, a cycloalkyl group, a cyano group, a hydroxyl group, a formyl group, an aryloxy group, an alkylthio group, an arylthio group, an acyloxy group, a sulfonyloxy group, an amino group, an alkylamino group, an arylamino group, a carboxyamino group, an oxysulfonylamino group, a sulfonamido group, an oxycarbonylamino group, a ureido group, an acyl group, an oxycarbonyl group, a carbamoyl group, a sulfonyl group, a sulfinyl group, an oxysulfonyl group, a sulfamoyl group, a carboxylic group, a sulfonic group, a phosphonic group, a heterocyclic group, -B(R a )(R b ), -OB(R a )(R b ) and -OSi(R a )(R b )(R c ). R a , R b and R c herein each represent a hydrogen atom, a halogen atom or a monovalent group. Examples of the monovalent group include an alkyl group, an alkoxy group, an aryl group, an alkenyl group, an alkinyl group, an aralkyl group, a cycloalkyl group, a cyano group, a hydroxyl group, a formyl group, an aryloxy group, an alkylthio group, an arylthio group, an acyloxy group, a sulfonyloxy group, an amino group, an alkylamino group, an arylamino group, a carboxyamino group, an oxysulfonylamino group, a sulfonamide group, an oxycarbonylamino group, a ureido group, an acyl group, an oxycarbonyl group, a carbamoyl group, a sulfonyl group, a sulfinyl group, an oxysulfonyl group, a sulfamoyl group, a carboxylic group, a sulfonic group, a phosphonic group, a heterocyclic group and derivatives thereof. Further in formula (9), R 11 and R 12 may be bound to each other to form a ring, and this ring may have a substituent. Still further, each group may be substituted with a group which can be substituted. R 11 and R 12 are preferably those selected from the group consisting of an alkyl group, an aryl group, derivatives thereof and fluorine-substituted derivatives thereof. Specific examples of -BR 11 R 12 are as follows. Moreover, in general formula (10), Z represents a residue of an active hydrogen compound. Examples of the active hydrogen compound include ethylene glycol, glycerin, trimethylolethane, diglycerin and pentaerythritol. k represents an integer of 2 to 6, preferably 2 to 4. 2. Polymeric electrolyte The polymeric electrolyte of the invention comprises one or more of the foregoing ion-conductive polymeric compounds, and an electrolytic salt, and further, as required, a nonaqueous solvent. The electrolytic salt used in the invention is not particularly limited. A lithium salt is preferably used. Examples thereof include LiBF 4 , LiPF 6 , LiClO 4 , LiAsF 6 , LiCF 3 SO 3 , LiN(CF 3 SO 2 ) 2 , LiN(C 2 F 5 SO 2 ) 2 , LiC(CF 3 SO 2 ) 3 , LiCl, LiF, LiBr, LiI, derivatives thereof and the like. These lithium salts may be used either singly or in combination. The concentration of the electrolytic salt is 0.01 mol/kg to 10 mols/kg, preferably 0.2 mol/kg to 6.0 mols/kg. The nonaqueous solvent is preferably an aprotic solvent, and examples thereof include carbonates, lactones, ethers, sulfolanes and dioxolanes. These nonaqueous solvents may be used either singly or in combination. The mixing ratio of the first ion-conductive polymeric compound to nonaqueous solvent is 1/99 to 99/1, preferably 1/99 to 50/50, more preferably 1/99 to 30/70 in terms of a weight ratio. The mixing ratio of the second ion-conductive polymeric compound to nonaqueous solvent is 1/99 to 99/1, preferably 5/95 to 95/5, more preferably 10/90 to 90/10 in terms of a weight ratio. 3. Electric devices The polymeric electrolyte of the invention can be applied to various electric devices, and examples thereof include cells, capacitors and the like. Typical of these are cells which are obtained by linking a positive electrode and a negative electrode through any of the foregoing polymeric electrolytes. In the positive electrode herein, a double metal oxide capable of occluding and releasing lithium ions is used. Examples thereof include cobalt lithium oxide, nickel lithium oxide, manganese lithium oxide, vanadium pentoxide and the like. Further, in the negative electrode, a lithium metal, a lithium alloy or a substance capable of reversibly occluding and releasing lithium ions is used. Examples of such a substance include carbon and the like. 4. Examples The invention is illustrated more specifically below by referring to Examples. However, the invention is not limited to these Examples. (1) Production of monomers A to E (compounds (B) represented by formula (3)) · Monomer A Potassium hydroxide (0.01 mol) was added to 1 mol of ethylene glycol monobutyl ether as a starting material, and a vessel was purged with nitrogen while stirring the mixture. Subsequently, the pressure inside the vessel was reduced using a vacuum pump. The temperature was then raised to 120°C, and the reaction was conducted using 1 mol of ethylene oxide as a monomer. After the completion of the reaction, the reaction mixture was cooled until the temperature inside the vessel reached room temperature. A methanol solution of 1.1 mols of sodium methylate was added, and the temperature was slowly raised to 50°C while reducing the pressure. After methanol was completely removed, 1.2 mols of epichlorohydrin was added, and the mixture was reacted for 4 hours. After the completion of the reaction, adsorption treatment was conducted. Dehydration was conducted under reduced pressure, and the residue was then filtered to obtain a desired product. · Monomer B A desired product was obtained in the same manner as monomer A except that ethylene glycol monomethyl ether was used as a starting material and 9 mols of ethylene oxide was used as a monomer. · Monomer C A desired product was obtained in the same manner as monomer A except that ethylene glycol monopropyl ether was used as a starting material and 2 mols of ethylene oxide was used as a monomer. · Monomer D A desired product was obtained in the same manner as monomer A except that ethylene glycol monoethyl ether was used as a starting material and 49 mols of ethylene oxide was used as a monomer. · Monomer E A desired product was obtained in the same manner as monomer A except that ethylene glycol monomethyl ether was used as a starting material and 9 mols of ethylene oxide was used as a monomer. (2) Examples and Comparative Examples on the first ion-conductive polymeric compound [Production of a compound represented by general formula (8)] · Compound A-1 One mol of potassium hydroxide was added to 500 g of toluene, and a vessel was purged with nitrogen while stirring the mixture. The pressure inside the vessel was reduced using a vacuum pump. The temperature was raised to 120°C, and the reaction was conducted using 38,000 mols of ethylene oxide as a monomer. After the completion of the reaction, the reaction mixture was cooled until the temperature inside the vessel reached room temperature. A methanol solution of 1.1 mols of sodium methylate was added, and the temperature was slowly raised while reducing the pressure. After methanol was completely removed and the reaction mixture was allowed to cool, 1 kg of toluene was added, 1 mol of acrylic acid chloride was added, and the reaction was conducted for 4 hours. After acid and alkali adsorption treatment was conducted, the product was filtered, and toluene was removed under reduced pressure to obtain a mono-ol having a polymerizable functional group. Three mols of the resulting mono-ol and 1 mol of borane were reacted in dichloromethane at room temperature to obtain a desired compound. · Compound A-2 A desired compound was obtained in the same manner as compound A-1 except that 28,000 mols of propylene oxide was used as a monomer and methacrylic acid chloride was used instead of acrylic acid chloride. · Compound A-3 A desired compound was obtained in the same manner as compound A-1 except that 1,500 mols of ethylene oxide and 600 mols of 1,2-epoxyhexane were used as monomers and allyl chloride was used instead of acrylic acid chloride. · Compound A-4 A desired compound was obtained in the same manner as compound A-1 except that 2 mols of ethylene oxide and 1 mol of butylene oxide were used as monomers and vinyl chloride was used instead of acrylic acid chloride. · Compound A-5 A desired compound was obtained in the same manner as compound A-1 except that 300 mols of ethylene oxide and 20 mols of 1,2-epoxypentane were used as monomers. · Compound B-1 A desired compound was obtained in the same manner as compound A-1 except that 600 mols of monomer A was used as a monomer. · Compound B-2 A desired compound was obtained in the same manner as compound A-2 except that 50 mols of ethylene oxide and 15 mols of monomer B were used as monomers. · Compound B-3 A desired compound was obtained in the same manner as compound A-3 except that 1 mol of ethylene oxide and 1 mol of monomer C were used as monomers. · Compound B-4 A desired compound was obtained in the same manner as compound A-4 except that 1,600 mols of ethylene oxide and 400 mols of monomer D were used as monomers. · Compound B-5 A desired compound was obtained in the same manner as compound A-5 except that 10 mols of ethylene oxide and 10 mols of monomer E were used as monomers. The structures of compounds A-1 to A-5 and B-1 to B-5 represented by formula (8), which were obtained as mentioned above, are as shown in the following chemical formulas and tables. Compound p1 q1 t Y A-1 38000 0 0 acryloyl group A-2 0 28000 0 methacryloyl group A-3 1500 600 3 allyl group A-4 2 1 1 vinyl group A-5 300 20 2 acryloyl group Compound p2 q2 r s Y B-1 0 600 2 3 acryloyl group B-2 50 15 10 0 methacryloyl group B-3 1 1 3 2 allyl group B-4 1600 400 50 1 vinyl group B-5 10 10 10 0 acryloyl group [Production of a polymeric electrolyte] · Example 1 One gram of compound A-1, mol/kg of LiBF 4 and 0.01 g of azoisobutyronitrile (AIBN) were dissolved in 2.3 g of γ-butyrolactone at 40°C. The mixture was poured between glass plates, and allowed to stand at 80°C for 2 hours to obtain a polymeric electrolyte having a thickness of 500 µm. · Example 2 One gram of compound A-2, 0.01 mol/kg of LiPF 6 and 0.01 g of AIBN were dissolved in 0.2 g of acetonitrile at 40°C. The mixture was poured between glass plates, and allowed to stand at 80°C for 2 hours. Acetonitrile was then distilled off under reduced pressure to obtain a polymeric electrolyte having a thickness of 500 µm. · Examples 3 to 9 Polymeric electrolytes were obtained in the same manner as in Example 2 except that types and amounts of compounds represented by general formula (8) and electrolytic salts, shown in Table 1 below were used. Examples 10 to 12 Polymeric electrolytes were obtained in the same manner as in Example 1 except that types and amounts of compounds represented by general formula (8), electrolytic salts and aprotic solvents, shown in Table 1 below were used. · Comparative Examples 1 and 2 Polymeric electrolytes were obtained in the same manner as in Example 2 except that types and amounts of compounds represented by general formula (8) and electrolytic salts, shown in Table 1 below were used. Comparative Example 3 One gram of polyethylene oxide (PEO) having a molecular weight of 1,000,000 and 1 mol/kg of LiBF 4 were dissolved in 0.2 g of acetonitrile at 40°C, and the mixture was poured between glass plates. Acetonitrile was then distilled off under reduced pressure to obtain a polymeric electrolyte having a thickness of 500 µm. [Measurement of a lithium ion transport rate] Each of the polymeric electrolytes obtained in the foregoing Examples and Comparative Examples was cut in a circle having a diameter of 13 mm, and this was held between lithium metal electrodes having the same diameter. A lithium ion transport rate was measured by a DC polarization method. The results are also shown in Table 1. (3) Examples and Comparative Examples on the second ion-conductive polymeric compound [Production of a compound represented by general formula (9)] · Compound A-1 One mol of potassium hydroxide was added to 500 g of toluene, and a vessel was purged with nitrogen while stirring the mixture. The pressure inside the vessel was reduced using a vacuum pump. The temperature was raised to 120°C, and the reaction was conducted using 220 mols of ethylene oxide as a monomer. After the completion of the reaction, the reaction mixture was cooled until the temperature inside the vessel reached room temperature. A methanol solution of 1.1 mols of sodium methylate was added, and the temperature was slowly raised to 50°C while reducing the pressure. After methanol was completely removed, the reaction mixture was allowed to cool. One kilogram of toluene was added, 1 mol of acrylic acid chloride was added, and the reaction was conducted for 4 hours. After acid and alkali adsorption treatment was conducted, the product was filtered, and toluene was removed under reduced pressure to obtain a mono-ol having a polymerizable functional group. One mol of the resulting mono-ol, 2 mols of methanol and 1 mol of borane were reacted in dichloromethane at room temperature to obtain a desired compound. · Compound A-2 A mono-ol having a polymerizable functional group was prepared in the same manner as in compound A-1 except that 240 mols of propylene oxide was used as a monomer and methacrylic acid chloride was used instead of acrylic acid chloride. One mol of the resulting mono-ol, 2 mols of octanol and 1 mol of borane were reacted in dichloromethane at room temperature to obtain a desired compound. · Compound A-3 A mono-ol having a polymerizable functional group was prepared in the same manner as in compound A-1 except that 30 mols of ethylene oxide and 8 mols of 1,2-epoxyhexane were used as monomers and allyl chloride was used instead of acrylic acid chloride. One mol of the resulting mono-ol, 1 mol of biphenyl-2,2'-diol and 1 mol of borane were reacted in dichloromethane at room temperature to obtain a desired compound. · Compound A-4 A mono-ol having a polymerizable functional group was prepared in the same manner as in compound A-1 except that 3 mols of ethylene oxide was used as a monomer and vinyl chloride was used instead of acrylic acid chloride. One mol of the resulting mono-ol, 1 mol of catechol and 1 mol of borane were reacted in dichloromethane at room temperature to obtain a desired compound. · Compound A-5 A mono-ol having a polymerizable functional group was prepared in the same manner as in compound A-1 except that 15 mols of ethylene oxide and 4 mols of 1,2-epoxypentane were used as monomers. One mol of the resulting mono-ol, 2 mols of 3,4-difluorobromobenzene and 1 mol of borane were reacted in dichloromethane at room temperature to obtain a desired compound. · Compound A-6 A mono-ol having a polymerizable functional group was prepared in the same manner as in compound A-1 except that 240 mols of monomer A was used as a monomer. One mol of the resulting mono-ol, 2 mols of ethylene glycol monomethyl ether and 1 mol of borane were reacted in dichloromethane at room temperature to obtain a desired compound. · Compound A-7 A mono-ol having a polymerizable functional group was prepared in the same manner as in compound A-2 except that 15 mols of ethylene oxide and 5 mols of monomer B were used as monomers. One mol of the resulting mono-ol, 2 mols of phenol and 1 mol of borane were reacted in dichloromethane at room temperature to obtain a desired compound. · Compound A-8 A mono-ol having a polymerizable functional group was prepared in the same manner as in compound A-3 except that 1 mol of ethylene oxide and 1 mol of monomer C were used as monomers. One mol of the resulting mono-ol, 2 mols of p-nitrophenol and 1 mol of borane were reacted in dichloromethane at room temperature to obtain a desired compound. · Compound A-9 A mono-ol having a polymerizable functional group was prepared in the same manner as in compound A-4 except that 10 mols of ethylene oxide and 3 mols of monomer D were used as monomers. One mol of the resulting moho-ol, 1 mol of 1,8-dinaphthol and 1 mol of borane were reacted in dichloromethane at room temperature to obtain a desired compound. Compound A-10 A mono-ol having a polymerizable functional group was prepared in the same manner as in compound A-5 except that 10 mols of ethylene oxide and 2 mols of monomer E were used as monomers. One mol of the resulting mono-ol, 2 mols of bromobenzene and 1 mol of borane were reacted in dichloromethane at room temperature to obtain a desired compound. [Production of a compound represented by general formula (10)] · Compound B-1 Potassium hydroxide (0.01 mol) was added to 0.5 mol of ethylene glycol as a starting material, and a vessel was purged with nitrogen while stirring the mixture. The pressure inside the vessel was reduced using a vacuum pump. The temperature was then raised to 120°C, and the reaction was conducted using 38,000 mols of ethylene oxide as a monomer. After the completion of the reaction, the reaction mixture was cooled until the temperature inside the vessel reached room temperature. A methanol solution of 1.1 mols of sodium methylate was added, and the temperature was slowly raised to 50°C while reducing the pressure. After methanol was completely removed, the reaction mixture was allowed to cool. One kilogram of toluene was added, 1 mol of acrylic acid chloride was added, and the reaction was conducted for 4 hours. After acid and alkali adsorption treatment was conducted, the product was filtered, and toluene was removed under reduced pressure to obtain a desired compound. · Compound B-2 A desired compound was obtained in the same manner as compound B-1 except that 0.33 mol of glycerin was used as a starting material, 28,000 mols of propylene oxide was used as a monomer and methacrylic acid chloride was used instead of acrylic acid chloride. · Compound B-3 A desired compound was obtained in the same manner as compound B-1 except that 0.25 mol of diglycerin was used as a starting material, 150 mols of ethylene oxide and 600 mols of 1,2-epoxyhexane were used as monomers and allyl chloride was used instead of acrylic acid chloride. · Compound B-4 A desired compound was obtained in the same manner as compound B-1 except that 0.5 mol of ethylene glycol was used as a starting material, 2 molls of ethylene oxide and 1 mol of butylene oxide were used as monomers and vinyl chloride was used instead of acrylic acid chloride. · Compound B-5 A desired compound was obtained in the same manner as compound B-1 except that 0.33 mol of glycerin was used as a starting material and 300 mols of ethylene oxide and 20 mols of 1,2-epoxypentane were used as monomers. · Compound B-6 A desired compound was obtained in the same manner as compound B-1 except that 600 mols of monomer A was used as a monomer. · Compound B-7 A desired compound was obtained in the same manner as compound B-2 except that 50 mols of ethylene oxide and 15 mols of monomer B were used as monomers. · Compound B-8 A desired compound was obtained in the same manner as compound B-3 except that 1 mol of ethylene oxide and 1 mol of monomer C were used as monomers. · Compound B-9 A desired compound was obtained in the same manner as compound B-4 except that 1,600 mols of ethylene oxide and 400 mols of monomer D were used as monomers. · Compound B-10 A desired compound was obtained in the same manner as compound B-5 except that 10 mols of ethylene oxide and 10 mols of monomer E were used as monomers. The structures of compounds A-1 to A-10 represented by general formula (9) and compounds B-1 to B-10 represented by formula (10), which were obtained as mentioned above, are as shown in the following chemical formulas and tables. Compound p1 q1 s Y B(R 11 )(R 12 ) A-1 220 0 0 acryloyl group 1-1 A-2 0 240 1 methacryloyl group 1-4 A-3 30 8 3 allyl group 1-17 A-4 3 0 0 vinyl group 2-4 A-5 15 4 2 acryloyl group 2-13 Compound p2 q2 r t Y B(R 11 )(R 12 ) A-6 0 240 2 3 acryloyl group 1-5 A-7 15 5 10 0 methacryloyl group 1-10 A-8 1 1 3 2 allyl group 1-13 A-9 10 3 50 1 vinyl group 1-24 A-10 10 2 10 0 acryloyl group 2-9 Z represents a residue of an active hydrogen compound. Compound p3 q3 s1 Y k B-1 38000 0 0 acryloyl group 2 B-2 0 28000 1 methacryloyl group 3 B-3 150 600 3 allyl group 4 B-4 2 1 1 vinyl group 2 B-5 300 20 2 acryloyl group 3 Z represents a residue of an active hydrogen Compound p4 q4 r1 t1 Y k1 B-6 0 600 2 3 acryloyl group 2 B-7 50 15 10 0 methacryloyl group 3 B-8 1 1 3 2 allyl group 4 B-9 1600 400 50 1 vinyl group 2 B-10 10 10 10 0 acryloyl group 3 More specific structures of compounds B-1 to B-10 represented by general formula (10) are as follows. [Production of a polymeric electrolyte] · Example 1 One gram of compound A-1, 9 g of B-10, 1 mol/kg of LiBF 4 and 0.01 g of azoisobutyronitrile (AIBN) were dissolved in 1.2 g of γ-butyrolactone at 40°C. The mixture was poured between glass plates, and allowed to stand at 80°C for 2 hours to obtain a polymeric electrolyte having a thickness of 500 µm. · Example 2 Two grams of compound A-2, 8 g of B-8, 0.01 mol/kg of LiPF 6 and 0.01 g of AIBN were dissolved in 0.2 g of acetonitrile at 40°C. The mixture was poured between glass plates, and allowed to stand at 80°C for 2 hours. Acetonitrile was then distilled off under reduced pressure to obtain a polymeric electrolyte having a thickness of 500 µm. · Examples 3 to 9 Polymeric electrolytes were obtained in the same manner as in Example 2 except that types and amounts of compounds represented by general formula (9) or (10) and electrolytic salts, shown in Table 2 below were used. · Examples 10 to 12 Polymeric electrolytes were obtained in the same manner as in Example 1 except that types and amounts of compounds represented by general formula (9) or (10), electrolytic salts and aprotic solvents, shown in Table 2 below were used. · Comparative Examples 1 and 2 Polymeric electrolytes were obtained in the same manner as in Example 2 except that types and amounts of compounds represented by general formula (9) or (10) and electrolytic salts, shown in Table 2 below were used. · Comparative Example 3 One gram of polyethylene oxide (PEO) having a molecular weight of 1,000,000 and 1 mol/kg of LiBF 4 were dissolved in 0.2 g of acetonitrile at 40°C, and the mixture was poured between glass plates. Acetonitrile was then distilled off under reduced pressure to obtain a polymeric electrolyte having a thickness of 500 µm. [Measurement of a lithium ion transport rate] Each of the polymeric electrolytes obtained in the foregoing Examples and Comparative Examples was cut in a circle having a diameter of 13 mm, and this was held between lithium metal electrodes having the same diameter. A lithium ion transport rate was measured by a DC polarization method. The results are also shown in Table 2. Industrial Applicability The polymeric electrolyte of the invention is greatly improved in a transport rate of charge carrier ions as compared with the ordinary ones. A transport rate refers to a rate of transporting anions and cations. Accordingly, when anions are fixed in a polymer chain and less moved, a rate of transporting cations is relatively increased consequently, which is considered to contribute toward improvement of a transport rate. The polymeric electrolyte of the invention can be applied to various electric devices. Owing to the above-described characteristics, for example, cells having a higher voltage and a higher capacity than usual ones can be obtained. Although the usage of cells is not particularly limited, they are preferably used in portable electric appliances such as a video, a camera, a personal computer, a cellular phone and the like.

Claims: An ion-conductive polymeric compound, characterized in that at least one boron atom is present in a polymeric structure, said ion-conductive polymeric compound being obtained by crosslinking a compound represented by the following general formula (7) wherein X represents a hetero-atom, R represents a divalent group having a molecular weight of at least 150, and Y represents a polymerizable functional group, wherein R in general formula (7) is a polymer or a copolymer of compound (A) represented by the following formula (2) and/or compound (B) represented by the following formula (3) wherein R 1 represents a methyl group, an ethyl group, a propyl group, a butyl group or a group represented by the following formula (4) -CH 2 O-[-CH 2 CH 2 O-] r -Ra wherein r represents 0 or an integer of 1 or more, and Ra represents a methyl group, an ethyl group, a propyl group or a butyl group; and wherein Y is selected from the group consisting of acryloyl, methacryloyl, allyl and vinyl. The ion-conductive polymeric compound according to claim 1, characterized in that the compound represented by general formula (7) is represented by the following general formula (8) wherein R represents the divalent group having a molecular weight of at least 150, represented by the following formula (6), and Y represents the polymerizable functional group wherein R 1 represents a methyl group, an ethyl group, a propyl group or a butyl group or a group represented by the following formula (4), p represents an integer of 0 to 38,000, and q represents an integer of 0 to 28,000, provided p and q are not 0 at the same time -CH 2 O-[-CH 2 CH 2 O-] r -Ra wherein r represents 0 or an integer of 1 or more; and Ra represents a methyl group, an ethyl group, a propyl group or a butyl group. An ion-conductive polymeric compound characterized in that at least one boron atom is present in a polymeric structure, wherein the boron atom is present in a polymeric side chain, and wherein said ion-conductive polymeric compound is obtained by polymerizing a mixture of compounds represented by the following formulas (9) and (10) respectively wherein R1 represents a divalent group having a molecular weight of at least 100, Y represents a polymerizable functional group selected from the group consisting of acryloyl, methacryloyl, ally and vinyl, and R 11 and R 12 , which may be the same or different, each represent a hydrogen atom, a halogen atom or a monovalent group, or R 11 and R 12 are bound to each other to form a ring wherein R 2 represents a divalent group having a molecular weight of at least 150, Y represents a polymerizable functional group as defined above, Z represents an active hydrogen residue, and k represents an integer of 2 to 6; and wherein R 1 in general formula (9) and/or R 2 in general formula (10) is a polymer of compound (A) represented by the following formula (2) and/or compound (B) represented by the following formula (3) wherein R 1 represents a methyl group, an ethyl group, a propyl group, a butyl group or a group represented by the following formula (4) -CH 2 O-[-CH 2 CH 2 O-] r -Ra wherein r represents 0 or an integer cf 1 or more, and Ra represents a methyl group, an ethyl group, a propyl group or a butyl group. An ion-conductive polymeric compound according to claim 3, wherein Z in formula (10) is selected from the group consisting of ethylene glycol, glycerin, trimethylolethane, diglycerin and pentaerythritol. The ion-conductive polymeric compound according to claim 3 or 4, characterized in that R 1 in general formula (9) and/or R 2 in general formula (10) is a divalent group represented by the following formula wherein R 1 represents a methyl group, an ethyl group, a propyl group or a butyl group or a group represented by the following formula (4), p represents an integer of 0 to 38,000, and q represents an integer of 0 to 28,000, provided p and q are not 0 at the same time -CH 2 O-[-CH 2 CH 2 O-] r -Ra wherein r represents 0 or an integer of 1 or more, and Ra represents a methyl group, an ethyl group, a propyl group or a butyl group. The ion-conductive polymeric compound according to any one of claims 3, 4 or 5, characterized in that R 11 and R 12 in general formula (9) are one or more selected from the group consisting of an alkyl group, an aryl group, derivatives thereof and fluorine-substituted derivatives thereof. A polymeric electrolyte comprising one or more types of the ion-conductive polymeric compound according to anyone of claims 1 to 6. The polymeric electrolyte according to claim 7, characterized by further comprising a nonaqueous solvent. The polymeric electrolyte according to claim 7, characterized in that the nonaqueous solvent is an aprotic solvent. The polymeric electrolyte according to any on of claims 7 to 9 which further comprises an.electrolytic salt. The polymeric electrolyte according to claim 10, characterized in that the electrolytic salt is a lithium salt. The polymeric electrolyte according to claim 11, characterized in that the lithium salt is one or more selected from the group consisting of LiBF 4 , LiPF 6 , LiClO 4 , LiAsF 6 , LiCF 3 SO 3 , LiN(CF 3 SO 2 ) 2 , LiN(C 2 F 5 SO 2 ) 2 , LiC(CF 3 SO 2 ), LiCl, LiF, LiBr, LiI, derivatives thereof. The polymeric electrolyte according to claim 9, characterized in that the aprotic solvent is one or more selected from the group consisting of carbonates, lactones, ethers, sulfolanes and dioxolanes. An electric device using the polymeric electrolyte according to any one of claims 7 to 13. A cell in which a positive electrode and a negative electrode are linked through the polymeric electrolyte according to any one of claims 7 to 13. The cell according to claim 15, characterized in that the positive electrode is made of a double metal oxide capable of occluding and releasing lithium ions, and the negative electrode is made of a lithium metal, a lithium alloy or a compound capable of occluding and releasing lithium ions reversibly.

Inventors: KONO MICHIYUKI, NISHIURA MASAHITO, WATANABE MASAYOSHI, KONO, MICHIYUKI, NISHIURA, MASAHITO, WATANABE, MASAYOSHI
Applicants: DAI ICHI KOGYO SEIYAKU CO LTD, DAI-ICHI KOGYO SEIYAKU CO., LTD.
Application year: 2000
Main classification: C08G79
IPC codes: C08G65, H01M10, H01M6, H01B1, C08G79