PROCESSES FOR THE RAPID PREPARATION OF FOAM MATERIALS FROM HIGH INTERNAL PHASE EMULSIONS AT HIGH TEMPERATURES AND PRESSURES

Abstract: This application relates to flexible, microporous, open-celled polymeric foam materials with physical characteristics that make them suitable for a variety of uses. This application particularly relates to high temperature processes having short curing times for preparing such foam materials from high internal phase emulsions.

Description: PROCESSES FOR THE RAPID PREPARATION OF FOAM MATERIALS FROM HIGH INTERNAL PHASE EMULSIONS AT HIGH TEMPERATURES AND PRESSURES FIELD OF THE INVENTION This application relates to rapid curing of high internal phase emulsions to produce microporous, open-celled polymeric foam materials with physical characteristics that make them suitable for a variety of uses BACKGROUND OF THE INVENTION The development of microporous foams is the subject of substantial commercial interest Such foams have found utility in various applications, such as thermal, acoustic, electrical, and mechanical (e.g., for cushioning or packaging) insulators, absorbent materials, filters, membranes, floor mats, toys, carriers for inks, dyes, lubricants, and lotions, and the like References describing such uses and properties of foams include Oertel, G., Polvurethane Handbook, Hanser Publishers, Munich, 1985, and Gibson, L. J.; Ashby, M. F., Cellular Solids Structure and Properties, Pergamon Press, Oxford, 1988. The term "insulator" refers to any material which reduces the transfer of energy from one location to another. The term "absorbent" refers to materials which imbibe and hold or distribute fluids, usually liquids, an example being a sponge. The term "filter" refers to materials which pass a fluid, either gas or liquid, while retaining impurities withm the material by size exclusion Other uses for foams are generally obvious to one skilled in the art. Open-celled foams prepared from High Internal Phase Emulsions (hereinafter referred to as "HIPEs") are particularly useful in a variety of applications including absorbent disposable articles (US Patents 5,331,015 (DesMarais et al.) issued July 19, 1994, 5,260,345 (DesMarais et al.) issued November 9, 1993, 5,268,224 (DesMarais et al.) issued December 7, 1993, 5,632,737 (Stone et al.) issued May 27, 1997, 5,387,207 (Dyer et al.) issued February 7, 1995, 5,786,395 (Stone et al ) July 28, 1998, 5,795,921 (Dyer et al.) issued August 18, 1998), insulation (thermal, acoustic, mechanical) (US Patents 5,770,634 (Dyer et al ) issued June 23, 1998, 5,753,359 (Dyer et al.) issued May 19, 1998, and 5,633,291 (Dyer et al.) issued May 27, 1997), filtration (Bhumgara, Z. Filtration & Separation 1995, March, 245-251; Walsh et al. J. Aerosol Sci 1996, 27, 5629-5630, published PCT application W/O 97/37745, published on October 16, 1997, m the name of Shell Oil Co ), and various other uses. The cited patents and references above are incorporated herein by reference. The HIPE process provides facile control over the density, cell and pore size and distribution, proportion of cell struts to windows, and porosity m these foams. An important issue in making HIPE foams commercially attractive is economics. The economics of HIPE foams depend on the amount and cost of the monomers used per unit volume of the foam, as well as the cost of converting the monomers to a usable polymeric foam (process costs). Making HIPE foams economically attractive can require using: (1) less total monomer per unit volume of foam, (2) less expensive monomers, (3) a less expensive process for converting these monomers to a usable HEPE foam, or (4) combinations of these factors. The monomer formulation and process conditions must be such that the properties of the HIPE foam meet the requirements for the particular application. The physical properties of the foam are governed by: (1) the properties of the polymer from which the foam is comprised, (2) the density of the foam, (3) the structure of the foam (i.e. the thickness, shape and aspect ratio of the polymer struts, cell size, pore size, pore size distribution, etc.), and (4) the surface properties of the foam (e.g., whether the surface of the foam is hydrophihc or hydrophobic). Once these parameters have been defined and achieved for a particular application, an economically attractive process for preparing the material is desired. A key aspect of this process is the rate of polymerization and crosslmkmg, together referred to as curing, of the oil phase of a HIPE to form a crosslmked polymer network. Previously, this curing step required that the emulsion be held at an elevated temperature (40°C-82°C) for a relatively long period of time (typically from 2 hours to 18 hours or longer). Such long cure times necessitate relatively low throughput rates, as well as high capital and production costs. Previous efforts to devise commercially successful schemes for producing HIPE foams have involved, for example, pouring the HEPE into a large holding vessel which is then placed in a heated area for curing (see for example US Patent 5,250,576 (Desmarais et al.) issued October 5, 1993). US Patents 5,189,070 (Brownscombe et al), issued February 23, 1993; 5,290,820 (Brownscombe et al.) issued March 1, 1994; and 5,252,619 (Brownscombe, et al.) issued October 12, 1993 disclose curing the HIPE in multiple stages. The first stage is conducted at a temperature of less than about 65°C until the foam reaches a partial state of cure. Then the temperature is increased to between 70°C and 175°C to effect final curing rapidly. The whole process takes about 3 hours. Another scheme to produce HIPE foams envisaged placing the emulsion on a layer of impermeable film which would then be coiled and placed m a curing chamber (US Patent 5,670,101 (Nathoo, et al.) issued September 23, 1997). The coiled film/emulsion sandwich could then be cured using the sequential temperature sequence disclosed in the Brownscombe, et al patents discussed above. US Patent 5,849,805 issued in the name of Dyer on December 15, 1998 discloses forming the H-PE at a temperature of 82°C (pour temperature in Example 2) and curing the HIPE at 82°C for 2 hours. However, none of these approaches offer the combination of very fast conversion (e.g., m minutes or seconds) from H-PE to polymeric foam that would provide for a relatively simple, low capital process for producing H-PE foams both economically and with the desired set of properties. The art also discloses using pressure to control the volatility of monomers that, otherwise, would boil off at a suitable polymeπzation/cuπng temperature. For example, commonly assigned US Patent 5,767,168, issued to Dyer, et al. on June 16, 1998, discloses the suitability of pressuπzation to control the volatility of relatively volatile conjugated diene monomers However, the cure time for the foams disclosed therein is still greater than two hours so there is still substantial opportunity for substantial improvement m curing rate that would improve the economic attractiveness of HIPE foams. Accordingly, it would be desirable to develop a rapid and efficient process for preparing open-celled polymeric HIPE foam materials with the desired properties. SUMMARY OF THE INVENTION The present invention relates to a process for obtaining open-celled foams by polymerizing a High Internal Phase Emulsion, or HIPE, which has a relatively small amount of a continuous oil phase and a relatively greater amount of a discontinuous aqueous phase. The present invention particularly relates to relatively high temperature processes for curing the oil phase This enables the foam to be prepared m a much shorter interval than has heretofore been possible. This enables practical continuous production processes of HIPE foams which have to this point been made via batch processes. The process of the present invention generally comprises the steps of. 1) forming a water in oil emulsion (HIPE) wherein the oil phase comprises polymeπzable monomers; and 2) polymerizing and crosslmkmg the monomers at temperatures greater than 90°C to form a HIPE foam. Specifically, the oil phase comprises: 1) from about 85 to 99% by weight of a monomer component capable of forming a copolymer having a Tg of about 90°C or lower, wherein the monomer component comprises a blend of monofunctional monomers, crosslmkng agents, and comonomers capable of modifying foam properties, and 2) from about 1 to about 20% of an emulsifier component capable of forming a stable HIPE. The aqueous phase comprises from about 0.2 to about 40% by weight of a water soluble electrolyte and an effective amount of a polymerization initiator. The volume to weight ratio of aqueous phase to oil phase is between about 8: 1 and about 140:1. After polymerization, the aqueous fraction of the H-PE foam may be removed by a variety of techniques to yield the open-celled, microporous, low density product. The curing of HIPEs m a relatively short time period at elevated temperatures allows increased production and improved economics relative to previously described methods. Either batch or continuous processes can be used. In either case, because the vapor pressure of both phases m the emulsion increases as the temperature is increased, some containment and/or pressurized system is generally required to prevent volatilization of the HIPE components during the high temperature curing and or emulsification steps. Volatilization to form gas or vapor bubbles may damage the fine structure, particularly the cell size distribution, of the HIPE and resulting HIPE foam, and is generally to be avoided This may be accomplished by applying pressure from an external source such as a pump or pressurized gas cylinder, by heating the emulsion in a closed container with relatively small headspace volume, by heating a portion of the composition under the surface of the emulsion in an open container such that the "hydrostatic" pressure prevents volatilization of the liquid comprising the emulsion, or by any other method or device generally known to those skilled in the art. Elements of these approaches may be combined to develop a suitable process for rapid curing of HEPE foams. BRIEF DESCRIPTION OF THE DRAWINGS Figure 1 is an. electron photomicrograph at 500 X magnification of a control HIPE foam in its expanded state wherein the emulsion was formed at 47°C and cured at 65°C under ambient pressure according to the prior art. Figure 2 is an electron photomicrographs at 500 X magnification of a representative polymeric foam in its expanded state according to the present invention prepared as described in Example 1. Figure 3 is an. electron photomicrograph at 1000 X magnification of a control HIPE foam in its expanded state wherein the emulsion was formed at 47°C and cured at 65 °C under ambient pressure according to the prior art. Figure 4 is an electron photomicrographs at 1000 X magnification of a representative polymeric foam in its expanded state according to the present invention prepared as described m Example 1. Figure 5 is an. electron photomicrograph at 2500 X magnification of a control HIPE foam in its expanded state wherein the emulsion was formed at 47°C and cured at 65°C under ambient pressure according to the prior art. Figure 6 is an electron photomicrographs at 2500 X magnification of a representative polymeric foam in its expanded state according to the present invention prepared as described in Example 1 Figure 7 is a schematic diagram of the curing chamber used to prepare foams depicted in Figures 1 and 2 Figure 8 is a schematic diagram of a continuous process for preparing HIPE foams DETAILED DESCRIPTION OF THE INVENTION I. Definitions The following definitions are offered relative to the current invention. "Curing" is the process of converting a HEPE to a HEPE foam. Cuπng involves the polymerization of monomers into polymers. A further step included m the curing process is crosslmkmg. A cured HIPE foam is one which has the physical properties, e.g., mechanical integrity, to be handled in subsequent processing steps (which may include a post-curing treatment to confer the final properties desired). Generally, curing is effected via the application of heat. An indication of the extent of cure is the mechanical strength of the foam, as measured by the yield stress described in the Test Methods section below "Polymerization" is the part of the curing process whereby the monomers of the oil phase are converted to a relatively high molecular weight polymer. "Crosslmkmg" is the part of the curing process whereby the monomers having more than one functional group with respect to free radical polymerization are copolymeπzed into more than one chain of the growing polymer "Hydrostatic" relates to pressure conferred by a column of liquid m a gravitational field, sometimes referred to as "hydrostatic head". The liquid is not necessarily water, but may be an aqueous solution, emulsion, suspension or other liquid. I. Polymeric Foam Derived From a High Internal Phase Emulsion A. General Foam Characteristics 1. Oil Phase Components The continuous oil phase of the HIPE comprises monomers that are polymerized to form the solid foam structure and the emulsifier necessary to stabilize the emulsion. In general, the monomers will include from about 20 to about 95% by weight of at least one substantially water- msoluble monofunctional monomer capable of forming an atactic amorphous polymer having a glass transition temperature (Tg) of about 35°C or lower. This comonomer is added to lower the overall Tg of the resulting HIPE foam. Exemplary monomers of this type include C4-C14 alkyl acrylates and Cg-Ci g methacrylates such as 2-ethylhexyl acrylate, n-butyl acrylate, hexyl acrylate, n-octyl acrylate, nonyl acrylate, decyl acrylate, isodecyl acrylate, tetradecyl acrylate, benzyl acrylate, nonyl phenyl acrylate, hexyl methacrylate, octyl methacrylate, nonyl methacrylate, decyl methacrylate, isodecyl methacrylate, dodecyl methacrylate, and tetradecyl methacrylate; substituted acrylamides, such as N-octadecyl acrylamide, dienes such as isoprene, butadiene, chloroprene, piperylene, 1,3,7-octatriene, β-myrcene and amyl butadiene; substituted C4-C12 styremcs such as p-n-octyl styrene; and combinations of such monomers. The Tg lowering monofunctional monomers will generally comprise 20% to about 95%, more preferably 45% to about 65%, by weight of the monomer component. The oil phase will also comprise from about 5 to about 80% by weight of a first substantially water-msoluble, polyfunctional crosslmkmg agent. This comonomer is added to confer strength to the resulting HIPE foam. Exemplary crosslmkmg monomers of this type encompass a wide variety of monomers containing two or more activated vmyl groups, such as the divmyl benzenes and analogs thereof. These analogs include m,p-dwmy\ benzene mixtures with ethyl styrene, divmyl naphthalene, tnvmyl benzene, divmyl alkyl benzenes, divinyl biphenyls, divmyl phenyl ethers, divmyl ferrocenes, divmyl furans, and the like. Other useful crosslmkmg agents may be selected from a group derived from the reaction of acrylic acid or mefhacryhc acid with polyfunctional alcohols and ammes. Nonhmitmg examples of this group include 1,6-hexanedιoldιacrylate, 1,4-butanedιoldιmethacrylate, trimethylolpropane triacrylate, hexamethylene bisacrylamide, and the like. Other examples of crosslmkmg monomers include divmyl sulfide, divmyl sulfone, and tnvmyl phosphme. Other crosslmkers useful in this regard are well known to those skilled m the art It should be noted that the weight fraction of the crosslmkmg component is calculated on the basis of the pure crosslmker m cases wherein the crosslmkmg monomer is commonly used as a mixture (e.g., divmyl benzene often is a 55% pure mixture with the balance being ethyl styrene). Any third substantially water-insoluble comonomer may be added to the oil phase in weight percentages of from about 0% to about 70%, preferably from about 15% to about 40%, to modify properties m other ways. In certain cases, "toughening" monomers may be desired which impart toughness to the resulting HIPE foam equivalent to that provided by styrene. These include styremcs such as styrene and ethyl styrene and methyl methacrylate. Also include are styrenics and other compounds which may also help reduce the Tg or enhance the strength of the resulting HIPE foam such as p-n-octyl styrene. Monomers may be added to confer flame retardancy as disclosed in commonly assigned copendmg application 09/118,613 (Dyer) filed July 17, 1998. Monomers may be added to confer color, fluorescent properties, radiation resistance, opacity to radiation (e.g., lead tetraacrylate), to disperse charge, to reflect incident infrared light, to absorb radio waves, to form a wettable surface on the HEPE foam struts, or for any other purpose. 2. Aqueous Phase Components The discontinuous aqueous internal phase of the HEPE is generally an aqueous solution containing one or more dissolved components. One essential dissolved component of the water phase is a water-soluble electrolyte. The dissolved electrolyte minimizes the tendency of monomers, comonomers, and crosslmkers that are primarily oil soluble to also dissolve in the water phase. Another component of the aqueous phase is a water-soluble free-radical initiator as may be known to the art. The initiator can be present at up to about 20 mole percent based on the total moles of polymeπzable monomers present m the oil phase. More preferably, the initiator is present in an amount of from about 0.001 to about 10 mole percent based on the total moles of polymeπzable monomers m the oil phase. Suitable initiators include ammonium persulfate and potassium persulfate. 3. Emulsifier The emulsifier is necessary for forming and stabilizing the HIPE. The emulsifier is generally included in the oil phase and tends to be relatively hydrophobic in character. (See for example Williams, J. M., Langmmr 1991, 7, 1370-1377, incorporated herein by reference.) An example emulsifier which functions very well is diglycerol monooleate. Other emulsifiers of this general sort also include diglycerol monomyπstate, diglycerol monoisostearate, diglycerol monoesters of coconut fatty acids, sorbitan monooleate, sorbitan monomyristate, sorbitan monoesters of coconut fatty acids, sorbitan isostearate, and like compounds and mixtures thereof. US Patent 5,786,395 (Stone et al.) issued July 28, 1998 offer further examples of these emulsifiers and is incorporated herein by reference. Such emulsifiers are advantageously added to the oil phase so that it comprises between about 1% and about 15% thereof. Obviously, emulsifiers that are particularly able to stabilize HEPEs at high temperatures are preferred. Diglycerol monooleate is exemplary in this respect. Coemulsifiers may also be used to provide additional control of cell size, cell size distribution, and emulsion stability. Exemplary coemulsifiers include phosphatidyl chohnes and phosphatidyl choline-contammg compositions, aliphatic betames, long chain C12-C22 diahphatic, short chain C1 -C4 diahphatic quaternary ammonium salts, long chain C12-C22 dιalkoyl(alkenoyl)-2-hydroxyethyl, short chain C1 -C4 diahphatic quaternary ammonium salts, long chain C12-C22 diahphatic lmidazolmium quaternary ammonium salts, short chain C1-C4 diahphatic, long chain C12-C22 monoahphatic benzyl quaternary ammonium salts, the long chain C12-C22 dιalkoyl(alkenoyl)-2-ammoethyl, short chain C1 -C4 monoahphatic, short chain C1 -C4 monohydroxyahphatic quaternary ammonium salts Particularly preferred is ditallow, dimethyl ammonium methyl sulfate. Such coemulsifiers and additional examples are described in greater detail in US Patent 5,650,222, issued in the name of DesMarais, et al. on July 22, 1997, the disclosure of which is incorporated herein by reference. 4 Optional Ingredients Various optional ingredients may also be included in either the water or oil phase for various reasons. Examples include antioxidants (e.g., hindered phenohcs, hindered amine light stabilizers, UV absorbers), plasticizers (e.g., dioctyl phthalate, dmonyl sebacate), flame retardants (e.g., halogenated hydrocarbons, phosphates, borates, inorganic salts such as antimony trioxide or ammonium phosphate or magnesium hydroxide), dyes and pigments, fluorescers, filler particles (e.g., starch, titanium dioxide, carbon black, or calcium carbonate) fibers, chain transfer agents, odor absorbers such as activated carbon particulates, dissolved polymers and ohogomers, and such other agents as are commonly added to polymers for a variety of reasons. Such additives may be added to confer color, fluorescent properties, radiation resistance, opacity to radiation (e.g., lead compounds), to disperse charge, to reflect incident infrared light, to absorb radio waves, to form a wettable surface on the HEPE foam struts, or for any other purpose. B. Processing Conditions for Obtaining HEPE Foams Foam preparation typically involves the steps of: 1) forming a stable high internal phase emulsion (HIPE); 2) curing this stable emulsion under conditions suitable for forming a cellular polymeric structure; 3) optionally squeezing and washing the cellular polymeric structure to remove the original residual water phase from the polymeric foam structure and, if necessary, treating the polymeric foam structure with a hydrophihzing surfactant and/or hydratable salt to deposit any needed hydrophihzing surfactant/hydratable salt, and 4) thereafter dewatermg this polymeric foam structure. 1. Formation of HIPE The HIPE is formed by combining the water and oil phase components m a ratio between about 8: 1 and 140: 1. Preferably, the ratio is between about 10: 1 and about 75:1, more preferably between about 13: 1 and about 65: 1 As discussed above, the oil phase will typically contain the requisite monomers, comonomers, crosslmkers, and emulsifiers, as well as optional components The water phase will typically contain electrolyte or electrolytes and polymerization initiator or initiators The HEPE can be formed from the combined oil and water phases by subjecting these combined phases to shear agitation. Shear agitation is generally applied to the extent and for a time period necessary to form a stable emulsion Such a process can be conducted in either batchwise or continuous fashion and is generally carried out under conditions suitable for forming an emulsion where the water phase droplets are dispersed to such an extent that the resulting polymeric foam will have the requisite structural characteristics. Emulsification of the oil and water phase combination will frequently involve the use of a mixing or agitation device such as an impeller. One preferred method of forming HEPE involves a continuous process that combines and emulsifies the requisite oil and water phases. In such a process, a liquid stream comprising the oil phase is formed. Concurrently, a separate liquid stream comprising the water phase is also formed. The two separate streams are provided to a suitable mixing chamber or zone at a suitable emulsification pressure and combined therein such that the requisite water to oil phase weight ratios previously specified are achieved In the mixing chamber or zone, the combined streams are generally subjected to shear agitation provided, for example, by an impeller of suitable configuration and dimensions, or by any other means of imparting shear or turbulent mixing generally known to those skilled m the art. Shear will typically be applied to the combined oil/water phase stream at an appropriate rate and extent. Once formed, the stable liquid HIPE can then be withdrawn or pumped from the mixing chamber or zone. This preferred method for forming HEPEs via a continuous process is described in greater detail in US Patent 5,149,720 (DesMarais et al), issued September 22, 1992, which is incorporated by reference. See also commonly assigned US Patent 5,827,909 (DesMarais) issued on October, 27, 1998 (incorporated herein by reference), which describes an improved continuous process having a recirculation loop for the H-PE. The process also allows for the formation of two or more different kinds of HIPEs in the same vessel as disclosed m US Patent 5,817,704 (Shiveley et al.) issued October 6, 1998, incorporated herein by reference. In this example, two or more pairs of oil and water streams may be independently mixed and then blended as required. 2 Polvmeπzation/Curmg of the oil phase of the HEPE The present invention relates to polymerization/curing of the oil phase of the emulsion at high curing temperatures for short periods. The HEPE formed as described above may be polymerized/cured in a batch process, or in a continuous process. A measure of the extent of cure of the polymer is the strength of the foam, as measured by the yield stress described in the Test Methods section below. Another measure of the extent of cure of the polymer is the extent to which it swells in a good solvent such as toluene (being crosslmked, the HEPE foam does not dissolve without being chemically altered). Without being bound by theory, it is believed that curing comprises two overlapping but distinct processes. The first involves polymerization of the monomers. The second the formation of crosslinks between active sites on adjacent polymer backbones. Crosslmkmg is essential to the formation of HIPE foams with strength and integrity essential to their further handling and use. The rate controlling step of this crosslmkmg reaction is believed to be related to the rate of diffusion of the active sites attached to the polymer chains. It has been discovered surprisingly that an increase in the rate of production of free-radicals in the HIPE does not accelerate curing usefully. However, increasing the diffusion rate of the active sites by increasing the temperature of the system in a conventional curing process is limited by the volatility of the components of the emulsion The current invention provides for curing the emulsion under an elevated pressure in order to allow high temperatures and rapid cure times to be attained without excessive volatilization of the emulsion components. It should be noted that the oil phase and the aqueous phase of the emulsion may contain dissolved gases At elevated temperatures, the solubility of these gases in the liquid phases is reduced, and the gas may be released to form bubbles in the emulsion. These bubbles may disrupt the structure of the HIPE and cause undesirable voids in the finished foam structure. The formation of these voids may be reduced or eliminated by 1) degassing the aqueous and/or oil phases of the emulsion prior to heating, 2) employing sufficient pressure to reduce or eliminate bubble formation at the curing temperature, or combinations of these approaches. Because the amount of aqueous phase is typically much larger than the amount of oil phase in the H-PE, most of the dissolved gas in the system may be removed by degassing only the aqueous phase. Degassing may be achieved by heating the liquid, or applying a vacuum, with or without a nucleating agent (e.g., boiling media, available from Aldrich Chemical Co., Milwaukee, WI), or by any other technique known to those skilled m the art. The liquid may be degassed in a batchwise process, or preferably in a continuous process immediately prior to formation of the HEPE. It has been found that HEPE structural disruption is minimized if one or both of the phases used to form the HIPE is degassed such that the level of a tracer gas (e. g., oxygen) is reduced to at least half its initial value after the degassing step and prior to formation of the HEPE. Preferably, the level of tracer gas is reduced to 25% of its initial value by the degassing step. More preferably, the tracer gas level is reduced to less than about 15% of its initial value (The amount of the tracer gas m a phase is measured when the phase is at room temperature (~25°C) and at a pressure of 1 atmosphere). Exposure of the liquid to be degassed to a vacuum of about 24 inches of mercury with a residence time of about 20 seconds has been found to reduce dissolved gas to a suitable level in a reasonable time. One of skill m the art will recognize that variables such as the amount of liquid to be degassed, the level of vacuum, the temperature of the liquid, the surface area of the exposed liquid?, and other similar variables all interact to determine the amount of time under vacuum that is required to reduce the initial dissolved gas level to an acceptable level. Such determination is readily done by those having skill in the chemical engineering arts It should be noted that as the temperature of the system is increased, both the rates of polymerization and depolymeπzation typically increase. At some elevated temperature, the rates of polymerization of the monomers and depolymeπzation of the polymer may become equal under the specific curing conditions. This is analogous to the ceiling temperature observed for many polymerization systems under a pressure of 1 atmosphere (see "Textbook of Polymer Science, 2 nd Ed " 1971, pp 306, F. W. Billmeyer, John Wiley & Sons, New York). This limits the practical upper limit of the curing temperature for a particular system The following describes exemplary nonhmitmg embodiments of this invention. In the first embodiment, the HIPE is formed in a batchwise process, as described m Example 1 below. The formed H-PE is transferred to a suitable reaction vessel 200, such as that shown m Figure 7, capable of withstanding pressures (typically from about 2 to about 40 atmospheres) necessary to enable curing at the desired temperature (typically from about 90° to about 250°C). As will be recognized, such pressure is necessary to prevent volatilization or evaporation of one or more of the HIPE components. The temperature at which the HIPE is provided to the vessel may be significantly lower than the polymerization/curing temperature. Figure 7 is an exemplary reaction vessel 200 that is suitable for batch curing of HEPEs according to the present invention. The vessel 200 comprises a vessel body 210 having sufficient volume to cure the desired amount of HIPE. The vessel body can have any desired shape including cylindrical, cubic, rectangular solid, or other irregular shape as may be desired. The container should be constructed such that the polymerized/cured solid foam material can be easily removed for further processing after polymenzation/curmg has been carried out to the extent desired. For certain purposes where the cured HIPE is further processed into a web of material by cutting it as is described m US Patent application Serial No. 08/939,172, filed in the name of Sabatelh, et al. on September 29, 1997, a cylindrical shape has been found to be useful. The vessel closure 220 has a shape that is complementary to the shape of the vessel body 210 so as to provide a closure therefor. The seal 230 is interposed between the closure 220 and the body 210 to provide resistance to leakage of materials enclosed in the reaction vessel 200 during the curing process. The vessel 200 should be constructed of materials that are capable of withstanding the pressures necessary to cure the HIPE at the desired temperature as is discussed above. Closure means (not shown) capable of resisting such pressure are also necessary in order to maintain the vessel 200 in a sealed condition during the curing process. The vessel 200 may further be lined with a material compatible with the H-PE so that it does not cause the HIPE to degrade at the interior surfaces of the vessel which contact the HEPE. Exemplary surfaces in this regard include: stainless steel, titanium, glass, polyethylene, polypropylene, and polytetrafluoroethylene. One of skill in the art will recognize that the choice of materials will depend on the environmental factors that the material will experience. For example, curing temperatures greater than the softening point of a polymer surface would render a polymeric lining unsuitable. For curing conditions requiring the surface to be exposed to high concentration of chloride ion (from the aqueous phase of the HEPE) and the combination of high pressure and temperature which provides the accelerated curing described herein, a titanium surface is suitable. The vessel 200 is filled with HIPE so as to minimize headspace volume before being sealed. Minimizing the headspace volume limits the extent to which volatilization of the emulsion components can occur. The vessel 200 may be pressurized simply by heating the container and its contents, for example in an oven. In such a case, the pressure inside the container is determined by the partial vapor pressures of the components of the emulsion. Alternatively, pressure can be introduced through an appropriate valve from an external pressure source such as a pump which can provide an incompatible liquid to raise the pressure or pressurized gas cylinder. Suitable curing conditions will vary depending upon the composition of the oil and aqueous phases of the emulsion (especially the emulsifier systems used), and the type and amounts of polymerization initiators used. Frequently, however, suitable curing conditions will involve maintaining the HIPE at elevated temperatures above about 90°C, more preferably above about 100°C, most preferably between about 125°C and 165°C (2.5 to 7 atmospheres), for a time period ranging from about 20 seconds to about 1 hour, more preferably from about 40 seconds to about 20 minutes, most preferably from about 1 mmute to about 10 minutes. Figures 1-6 are photomicrographs that compare exemplary foams produced according to the prior art and according to the present invention as described m Example 1 at various magnifications Specifically, the foam of Figures 1, 3, and 5 was produced according to Condition 2 of Example 1 and the foam of Figures 2, 4, and 6 was produced according to Condition 7 of Example 1. As can be seen by comparing the process conditions given in table 1 , the only substantial difference in curing is the curing temperature, with the resulting reduction m curing time. As is clearly evident from the property data in Table 1 below and by comparing the various pairs of figures, the rapid curing process of the present invention provides foams having essentially the same properties as foams produced according to the prior art using curing processes that required substantially longer curing times. In alternative embodiments of the batchwise process, a plurality of reaction vessels 200 may be attached, for example, to a continuous belt which moves the vessels from a HEPE filling station through a heating zone to a section which ejects the cured HIPE foam to a processing line and carriers the containers back to the filling zone (after any washing process that may be needed to restore the containers to usable condition) In a second embodiment, the HIPE is formed m a continuous process, as is shown schematically in Figure 8 and described in Example 2 below. Figure 8 describes one method and an apparatus 300 suitable for continuously forming H-PE foams according to the present invention. A HIPE is made using the methods generally described in the aforementioned US Patents 5,149,720 and 5,827,909. That is, the oil phase (desired blend of monomers and emulsifier) is prepared and stored in an oil phase supply vessel 305. Similarly, the desired aqueous phase (blend of water, electrolyte and initiator) is prepared and stored in an aqueous phase supply vessel 310. The oil phase and the aqueous phase are supplied in the desired proportions to mixhead 330 by an oil phase supply pump 315 and an aqueous phase supply pump 325. The mixhead 330 supplies the mechanical energy (shear) necessary to form the HIPE. If desired, a HEPE recirculation pump 335 can be used. The formed HEPE is pumped into an elongated curing chamber 340 with specific cross- sectional shape and dimensions as desired for the foam product. The oil phase supply pump 315 and the aqueous phase supply pump may be used to pump the HEPE from the mixhead 330 to the curing chamber 340. En this case, emulsification will occur at substantially the curing pressure. One of skill in the art will recognize that the emulsification pressure must be somewhat greater than curing pressure to enable flow to occur. Alternatively, an optional booster pump 345 may be used to pump the HIPE from the mixhead 330 to the curing chamber 340. In this case, emulsification will occur at a lower pressure and temperature than the curing step. In an alternative embodiment of the present invention (not shown), multiple systems, similar to those described above, can be used to make multiple HIPEs having different combinations of properties (e.g. pore dimensions, mechanical properties, etc.). Such multiple HIPEs can be introduced into the curing chamber 340 so as to provided a cured foam having regions of varying properties as may be desired for a particular end use. The chamber 340 may further be lined with a material compatible with the HEPE so that it does not cause degradation of the HEPE structure at the interior surfaces which contact the HIPE, and is not degraded by the oil or water phase components at the elevated temperatures intended. Optionally, a slip layer may be provided between the curing HIPE and the chamber walls to minimize uneven flow patterns as the HIPE progresses through the chamber 340. As with the lining discussed above, the slip layer must be compatible with the oil and water phase components of the HIPE and have sufficient mechanical stability at the curing temperature so as to be effective. Such a slip layer has particular utility when used with curing chamber designs incorporating the "hydrostatic head" as are discussed below. At least a portion of the chamber 340 is heated m order to bring the HEPE to the intended curing temperature as it passes through this section or zone. Any manner of heating this section or zone may be employed in order to reach and maintain the desired temperature in a controlled fashion. Examples include heating by resistive electrical elements, steam, hot oil or other fluids, hot air or other gases, open flame, or any other method of heating known to those skilled in the art. Optionally, a static mixer/heat exchanger or other forced convection heat exchanger can be utilized in the heated section to improve heat transfer into the HIPE Once the HIPE begins to gel, the composition can no longer be mixed because of the risk of damaging or even destroying the structure of the foam. The chamber 340 should be designed such that the pressure required to pump the emulsion and/or cured foam through the chamber under steady state conditions is sufficient to prevent volatilization of the emulsion components at the cure temperature The chamber 340 may be in a horizontal, inclined, or vertical position. The inclined and vertical orientations may be employed to provide additional "hydrostatic" back-pressure to help prevent the volatilization of HEPE components, thereby allowing a shorter curing chamber to be employed. The length of the optional heated section, the temperature of the optional heated section and the rate at which the emulsion is pumped through the tube are selected to allow for sufficient residence time withm the chamber 340 for adequate heat transfer to the center of the chamber 340 in order to attain complete cure. If the optional heating is done in chambers 340, then Chambers 340 with relatively thm cross-sectional dimensions are preferred in order to facilitate rapid heat transfer. The HEPE is substantially cured into a HIPE foam by the time it exits the curing chamber 340. Optionally, an elevated extension 350 may be located above and downstream of the curing chamber 340 so as to provide a hydrostatic head. The curing chamber 340 can have any desired cross section that is consistent with the flow requirements of pumping the curing HIPE. For example, the cross section can be rectangular, circular, triangular, annular, oval, hourglass, dog bone, asymmetric, etc., as may be desired for a particular use of the cured HEPE. Preferably, the cross sectional dimensions of the chamber 340 are such that the polymerized HEPE foam is produced in sheet-like form with the desired cross-sectional dimensions. Alternatively, the cross-sectional shape can be designed to facilitate manufacture of the desired product in subsequent processes. For example, an hourglass-shaped cross-section (or conjoined hourglass sections) of the appropriate size may facilitate making disposable absorbent products such as diapers by cutting relatively thm slices or sheets of the shaped HEPE foam. Other sizes and shapes may be prepared for making feminine hygiene pads, surgical drapes, face masks, and the like. Regardless of the cross-sectional dimensions of the curing chamber 340, the resultant HEPE foam may be cut or sliced into a sheet-like form with thickness suitable for the intended application. The cross-section of the curing chamber 340 may be varied along the length of the chamber m order to increase or decrease the pressure required to pump the HIPE through the chamber. For example, the cross-sectional area of a vertical curing chamber may be increased above the point at which the HIPE foam is cured, in order to reduce the resistance to flow caused by friction between the walls of the chamber and the cured foam. Alternatively, the cross- sectional area of a curing chamber may be decreased past the point at which the HIPE foam is cured, in order to increase the pressure required to pump the HEPE through the chamber thereby allowing a shorter curing chamber to be employed. A solution of initiator can optionally be injected into the HEPE at a point between the mixhead 330 and the curing chamber 340 (not shown). If the optional injection of initiator is chosen, the aqueous phase, as provided from the aqueous phase supply vessel, is substantially initiator free. Additional mixing means, such as a continuous mixer (not shown) may also be desirable downstream of the injection point and upstream of the curing chamber 340 to ensure the initiator solution is distributed throughout the HIPE. Such an arrangement has the advantage of substantially reducing the risk of undesirable curing in the mixhead 330 the event of an unanticipated equipment shutdown. A porous, water-filled, open-celled HEPE foam is the product obtained after curing in the reaction chamber. As noted above, the cross sectional dimensions of the chamber 340 are preferably such that the polymerized HIPE foam is produced in sheet-like form with the desired cross-sectional dimensions. Alternative cross-sectional dimensions may be employed, but regardless of the shape of the curing chamber 340, the resultant HIPE foam may be cut or sliced into a sheet-like form with thickness suitable for the intended application. Sheets of cured HIPE foam are easier to process during subsequent treating/washing and dewateπng steps, as well as to prepare the HEPE foam for use in the intended application. Alternatively, the product HEPE foam may be cut, ground or otherwise comminuted into particles, cubes, rods, spheres, plates, strands, fibers, or other desired shapes. The aqueous phase remaining with the HEPE is typically removed by compressing the foam. Residual moisture can be removed as desired by conventional evaporative drying techniques As noted above, m the continuous curing process, the emulsification step may be carried out at a relatively low pressure and the pre-formed emulsion pumped into the curing chamber under relatively high pressure using booster pump 345 An alternative process entails pumping the oil phase and the aqueous phase into the mixing chamber under relatively high pressure using oil phase supply pump 315 and aqueous phase supply pump 325. In this case, the emulsification step occurs under relatively high pressure, and the emulsion exits from the mixing chamber directly into the curing chamber under the requisite pressure. This eliminates the need to actively pump the pre-formed emulsion into the curing chamber. The HEPE may comprise at least one monomer with a boiling point less than about 60°C Exemplary monomers include chloroprene, isoprene, and butadiene These volatile monomers are not easily managed with the HIPE curing processes disclosed to date When these are employed in the current invention, the pressure of the process must be sufficient to prevent undue volatilization of these monomers even with the heating necessary to effect rapid cure. Foams using these monomers appropriately may be biodegradable as disclosed m aforementioned US Patent 5,767,168, in which HIPE foams made with isoprene are prepared at a pressure of about 30 psi (2 atmospheres) and a temperature of 50°C for 48 hours or more. The process according to the current invention enables the curing time to be shortened significantly by applying higher temperatures and pressures. Foams based on chloroprene may be flame retardant, as disclosed in aforementioned copendmg application Serial No. 09/118,613. As taught m each of these references, the inclusion of antioxidants may be especially preferred for HIPE foams made with 1,3-dienes. m. Test Methods The test methodologies for measuring Tg, yield stress, expansion factors, and stability in the compressed state are disclosed in US Patent 5,753,359. The methodologies for measuring Resistance to Compression Deflection (RTCD), and Free Absorbent Capacity (FAC) are disclosed in US Patent 5,849,805. Swelling Ratio: Swelling ratio may be used as a relative measure of the degree of crosslmkmg of the polymer comprising the HEPE foam. The degree of crosslmkmg is the critical part of curing as defined herein above. Swelling ratio is determined by cutting a cylindrical sample of the foam 2-6 mm thick, 2.5 cm m diameter. The foam sample is thoroughly washed with water and 2-propanol to remove any residual salts and/or emulsifier. This is be accomplished by placing the sample on a piece of filter paper m a Bϋchner funnel attached to a filter flask. A vacuum is applied to the filter flask by means of a laboratory aspirator and the sample is thoroughly washed with distilled water and then with 2-propanol such that the water and 2-propanol are drawn through the porous foam by the vacuum. The washed foam sample is then dried m an oven at 65°C for three hours, removed from the oven, and allowed to cool to room temperature prior to measurement of the swelling ratio. The sample is weighed to withm ± 1 mg, to obtain the dry weight of the sample, Wd. The sample is then placed in a vacuum flask containing sufficient methanol to completely submerge the foam sample. Remaining air bubbles in the foam structure are removed by gentle reduction of the pressure in the flask by means of a laboratory aspirator. Gentle vacuum is applied and released several times until no more bubbles are observed leaving the foam sample when the vacuum is applied, and the foam sample sinks upon release of the vacuum. The completely saturated foam sample is gently removed from the flask and weighed to withm ± 1 mg, taking care not to squeeze any of the methanol out of the sample during the weighing process. After the weight of the methanol saturated sample is recorded, (Wm), the sample is again dried by gently expressing most of the methanol followed by oven drying at 65°C for 1 hour. The dry sample is then placed into a vacuum flask containing sufficient toluene to completely submerge the foam sample. Residual air trapped withm the pores of the foam is removed by gentle application and release of vacuum, as described above. The toluene saturated weight of the sample, Wt, is also obtained as described above. The swelling ratio may be calculated from the densities of methanol and toluene, and the weights recorded in the above procedure as follows: Swelling Ratio = [(Wt - Wd)/ (Wm-Wd)] x 0.912 where 0.912 is the ratio of the densities of methanol and toluene. Yield Stress: Yield stress is the most practical measure of the degree of curing and relates to the compression strength of the HIPE foam. Yield stress is the stress at which a marked change in the slope of the stress-strain curve occurs. This is practically determined by the intersection of extrapolated regions of the stress-strain curve above and below the yield point, as described in more detail below. The general test method for measuring yield stress is disclosed in US Patent 5,753,359. Specifically, for the purposes of this application, the following method is used: Apparatus: Rheometrics RSA-2 DMA, as is available from Rheometrics Inc., of Piscatawy, NJ. Setup: 0.1% strain rate per second for 600 seconds (to 60% strain) using 2.5 cm diameter parallel plates in compression mode; 31°C oven temperature held for 10 minutes prior to the start of the test, and throughout the test. Sample: HIPE foam samples cut into cylinders 2-6 mm thick and 2.5 cm in diameter The resulting stress-stram curve can be analyzed by line fitting the initial linear elastic and plateau portions of the plot using a linear regression method. The intersection of the two lines thus obtained provides the yield stress (and yield strain). Density: Foam density can be measured on dry, expanded foams using any reasonable method. The method used herein is disclosed in the aforementioned US Patent 5,387,207. Curing Rate Determinations: HEPEs are prepared at specified temperatures and placed in suitable containers for specified times at the cure temperatures. The HEPE foams so produced are plunged into an ice bath to quench the curing process. The cooled foams are removed and processed for analysis, usually comprising removal of water by use of pressure, washing m water and/or organic solvent, and drying followed by slicing and/or cutting to the desired dimensions. V. Specific Examples These nonhmitmg examples illustrate the specific preparation of HIPE foams according the present invention. Example 1 : Batch Preparation of Foam from a HIPE A) HIPE Preparation Anhydrous calcium chloride (12.0 g) and potassium persulfate (0.150 g) are dissolved in 300 mL of water. This provides the aqueous phase to be used in forming the HEPE. To a monomer combination comprising 2-ethylhexylacrylate (EHA) (5.50 g), divmylbenzene (of 42% purity with balance being ethyl styrene) (DVB42) (3.30 g), and 1,6- hexanediol diacrylate (HDD A) (1.20 g) is added a high purity diglycerol monooleate (DGMO) (0.6 g), and ditallowdimethylammonium methyl sulfate (DTDMAMS) (O.lg). (DVB42 may be obtained from Dow Chemical, Midland, MI; other monomers may be obtained from Aldrich Chemical Co., Milwaukee, WI; DGMO may be obtained from Danisco Ingredients, Brabrand, Denmark; and DTDMAMS may be obtained Witco Corp., Greenwich CT.) The diglycerol monooleate emulsifier comprises approximately 81% diglycerol monooleate, 1% other diglycerol monoesters, 3% polyglycerols, and 15% other polyglycerol esters, imparts a minimum oil phase/water phase interfacial tension value of approximately 2.5 dyne/cm and has a critical aggregation concentration of approximately 2.9 wt% This provides the oil phase to be used in forming the HIPE. The monomer percentages by weight are 55% EHA, 33% DVB42, and 12% HDDA. A portion of the oil phase (5.00 g) is weighed into a high-density polyethylene cup with vertical sides and a flat bottom. The internal diameter of the cup is 70 mm and the height of the cup is 120 mm. The oil phase is stirred using an overhead stirrer equipped with a stainless steel impeller attached to the bottom of a stainless steel shaft 3/8 inch (9.5mm) in diameter. The impeller has 6 arms extending radially from a central hub, each arm with a square cross section 3.5 mm x 3.5 mm, and a length of 27 mm measured from the shaft to the tip of the arm. The oil phase is stirred with the impeller rotating at 250 to 300 rpm while 240 mL of pre-heated aqueous phase (47°C) is added drop-wise over a period of ca. 4 minutes to form a thick high internal phase emulsion. The impeller is raised and lowered withm the emulsion during the addition of the aqueous phase so as to achieve uniform mixing of the components. After all of the aqueous phase has been added, the emulsion is stirred for an additional minute with an impeller speed of ca 400 rpm to achieve a thick but pourable, uniform HIPE. B) Polymeπzation/Cuπng of HIPE A portion of the emulsion is poured into a cylindrical stainless steel vessel (see Figure 7) with a wall thickness of ca. 3 mm, a depth of ca. 16 mm and an internal diameter of ca. 3.8 cm so as to completely fill the vessel. A 6 mm thick stainless steel lid equipped with an O-πng is used to seal the vessel, the lid being secured by means of a C-clamp. The entire vessel is submerged in a bath of sihcone oil pre-heated to the desired curing temperature for the required length of time. Upon removal from the oil bath, the vessel is immediately submerged in bath containing a mixture of ice and water in order to cool the vessel and its contents rapidly. After several minutes, the vessel is removed from the ice/water bath and the cured foam within is removed carefully for washing, dewatermg, and characterization, as described m the Test Methods section above. C) Foam Washing and Dewatermg The cured HIPE foam is removed from the container. The foam at this point has residual water phase (containing dissolved or suspended emulsifiers, electrolyte, initiator residues, and initiator) about 48 times the weight of polymerized monomers. The foam is dewatered by placing the sample on a piece of filter paper in a Bϋchner funnel attached to a filter flask. A vacuum is applied to the filter flask by means of a laboratory aspirator and the sample is thoroughly washed with distilled water and then with 2-propanol such that the water and 2- propanol are drawn through the porous foam by the vacuum. The washed foam sample is then dried in an oven at 65 °C for three hours, removed from the oven, and allowed to cool to room temperature prior to characterization as described in the Test Methods section above. Exemplary data are presented in Table 1 below Table 1 *Comparatιve Conditions 1 and 2 demonstrate curing at ambient pressure according to the prior art. Long cure times (typically > 8 hours) are required to achieve full cure at 65°C, as evidenced by the yield stress data. At 65°C, no foam is recoverable at cure times less than about 2.5 hours, i.e. a minimum of about 2.5 hours is required for the HEPE to cure sufficiently so as to have enough mechanical integrity to be recovered. Example 2: Continuous Preparation of Foam from a HIPE A) HEPE Preparation Anhydrous calcium chloride (36.32 kg) and potassium persulfate (189 g) are dissolved in 378 L of water. This provides the water phase stream to be used in a continuous process for forming the HEPE. To a monomer combination comprising DVB42 (2100 g), 2-EHA (3300 g), and HDDA (600 g) is added a very high purity DGMO (360 g), and Tmuvm 765 (30 g). After mixing, this emulsifier mixture is allowed to settle overnight No visible residue is formed and all of the mix is withdrawn and used in the oil phase as the emulsifier in forming the HEPE. Separate streams of the oil phase (25°C) and water phase (65°C) are fed to a dynamic mixing apparatus as in Example 1 of US Patent 5,827,909. A portion of the material exiting the dynamic mixing apparatus is withdrawn and recirculated by a recirculation loop as shown and described in the Figure of the aforementioned US Patent 5,827,909 to the entry point of the oil and water phase flow streams to the dynamic mixing zone. The combined mixing and recirculation apparatus is filled with oil phase and water phase at a ratio of 4 parts water to 1 part oil. The dynamic mixing apparatus is vented to allow air to escape while filling the apparatus completely. The flow rates during filling are 3.78 g/sec oil phase and 15.12 cc/sec water phase with about 15 cc/sec in the recirculation loop. During the start-up phase, the HEPE produced is diverted into a holding tank until production conditions are achieved. Once the apparatus set-up is filled, the water phase flow rate is cut m half to reduce the pressure build up while the vent is closed Agitation is then begun in the dynamic mixer, with the impeller turning at 1800 RPM. The flow rate of the water phase is then steadily increased to a rate of 45.4 cc/sec over a time period of about 1 mm., and the oil phase flow rate is reduced to 0.757 g/sec over a time period of about 2 mm. The recirculation rate is steadily increased to about 45 cc/sec during the latter time period. The back pressure created by the dynamic and static mixers at this point is about 10 PSI (69 kPa). The Waukesha pump speed is then steadily decreased to yield a recirculation rate of about 11 cc/sec. B) Polvmerization/Cunng of HEPE Once steady-state production of HIPE is achieved, a portion of the emulsion flowing from the static mixer is pumped into the bottom of a vertical stainless steel chamber with a rectangular cross-section having internal dimensions of 5 mm x 300 mm, and a length (height) of 15 meters. A section near the bottom of the tube is jacketed and oil at 140°C is continuously pumped through the jacket. The emulsion is pumped through the chamber at a rate such that the residence time in the heated section is 10 minutes. During this 10 minute period, the oil phase is polymerized/cured to form an open celled foam. C) Foam Washing and Dewatermg The cured H-PE foam exits from the top of the chamber in the form of a continuous sheet with the same cross-section as that of the curing chamber (300 mm wide, 5 mm thick). The foam at this point has residual aqueous phase (containing dissolved or suspended emulsifiers, electrolyte, initiator residues, and initiator) about 50-60 times (50-60X) the weight of polymerized monomers. The foam sheet is then subjected to compression in a series of 2 porous nip rolls equipped with vacuum which gradually reduce the residual water phase content of the foam to about 6 times (6X) the weight of the polymerized material. At this point, the sheet is then resaturated with a 1.5% CaCl2 solution at 60°C, and squeezed in a series of 3 porous nip rolls equipped with vacuum to a water phase content of about 4X The CaCl2 content of the foam is between 8 and 10 %. The foam remains compressed after the final nip at a thickness of about 0.021 in. (0.053 cm). The foam is then dried in air for about 16 hours. Such drying reduces the moisture content to about 9-17 % by weight of polymerized material. At this point, the foam sheets are very drapeable. The foam also contains about 5% by weight of residual diglycerol monooleate emulsifier. In the collapsed state, the density of the foam is about 0.14 g/cc. When expanded m water, its free absorbent capacity is about 60 mL/g and has a glass transition temperature of about 23°C. Example 3. Alternate Formulations. The process of Example 2 is replicated with different monomer types and ratios and other conditions as shown in Table 2 below. Table 2 *EHA = 2-ethylhexyl acrylate; DVB42 = divmyl benzene of 42% purity; STY = styrene; HDDA = 1,6-hexanedιol diacrylate; ISO = isoprene; CPR = chloroprene, used in ED # 6 only, wherein the emulsification is carried out under a pressure of 7 atmospheres. The foams produced in these examples are open-celled and sufficiently cured in the time noted to have useful properties. Each can be post-treated to be either hydrophilic or hydrophobic, depending on the intended use. Foam number 1, for example, may be used as a packaging or insulating foam, among other uses. Foam 2 is biodegradable. Foam 3 may be used as a material for acquiring urine rapidly, for example. Foams 4 and 5 may be used in applications like floor mats where a high degree of toughness and abrasion resistance is required. Foam 6 is an example of a foam which does not burn on exposure to open flame. (An optional adjuvant in Foam 6 is, for example, antimony trioxide microparticles added to the oil phase prior to emulsification ) Each of these uses is exemplary but non-hmitmg. The formulations may be altered in each parameter to modify the properties such as Tg (add more Tg lowering monomer), cell size (decrease by increasing shear or RPM), density (decrease by increasing W:0 ratio), toughness (increase by adding styrene), and the like. The disclosures of all patents, patent applications (and any patents which issue thereon, as well as any corresponding published foreign patent applications), and publications mentioned throughout this description are hereby incorporated by reference herein. It is expressly not admitted, however, that any of the documents incorporated by reference herein teach or disclose the present invention. While particular embodiments of the present invention have been illustrated and described, it would be obvious to those skilled in the art that various other changes and modifications can be made without departing from the spirit and scope of the invention. It is therefore intended to cover m the appended claims all such changes and modifications that are withm the scope of this invention.

Claims: What is claimed is: 1. A process for the preparation of a polymeric foam material which compπses the steps of. A) forming a water-m-oil emulsion from: 1) an oil phase comprising: a) from about 85 to about 99% by weight of a monomer component capable of forming a copolymer having a Tg value of below about 90°C or lower, the monomer component comprising- l) from about 5 to about 80% by weight of a substantially water-msoluble, monofunctional monomer capable of forming a polymer having a Tg of about 35°C or less; n) from about 0 to about 70% by weight of a substantially water-msoluble, monofunctional comonomer capable of imparting other desired properties to the foam; in) about 5 to about 80% by weight of a first substantially water-msoluble, polyfunctional crosslmkmg agent; and b) from about 1 to about 20% by weight of an emulsifier component which is soluble m the oil phase and which is suitable for forming a stable water-m-oil emulsion, the emulsifier preferably comprising emulsifying components selected from the group consisting of diglycerol monooleate, diglycerol monomyπstate, diglycerol monoisostearate, diglycerol monoesters of coconut fatty acids, sorbitan monooleate, sorbitan monomyπstate, sorbitan monoesters of coconut fatty acids, sorbitan isostearate, ditallow, dimethyl ammonium methyl sulfate, and mixtures thereof and at least about 70% by weight of the emulsifying components; and 2) a water phase comprising an aqueous solution containing: (a) from about 0.2 to about 40% by weight of a water-soluble electrolyte; and (b) an effective amount of a polymerization initiator, preferably the polymerization initiator is selected from the group consisting of ammonium persulfate and potassium persulfate, wherein the emulsion has a volume to weight ratio of water phase to oil phase in the range of from about 8: 1 to about 140: 1, preferably from about 10:1 to about 75.1, more preferably from about 13 T to about 65: 1; B) characterized by providing means to minimize volatilization of the components of the emulsion; and C) curing the monomer component in the oil phase of the water-m-oil emulsion using a polymerization reaction that is conducted at a curing temperature, the curing temperature being between about 90°C and about 250°C to form a polymeric foam material. 2. The process of Claiml wherein: 1) the oil phase comprises: a) from about 90 to about 97% by weight of a monomer component capable of forming a copolymer having a Tg value from about 15° to about 50°C, the monomer component comprising. I) from about 40 to about 70% by weight monomer selected from the group consisting of C4-C14 alkyl acrylates, aryl acrylates, Cg-Ci g alkyl methacrylates, dienes, C4-C12 alkyl styrenes and mixtures thereof, the monomer preferably being selected from the group consisting of butyl acrylate, hexyl acrylate, octyl acrylate, 2-ethylhexyl acrylate, nonyl acrylate, decyl acrylate, dodecyl acrylate, isodecyl acrylate, tetradecyl acrylate, benzyl acrylate, nonylphenyl acrylate, hexyl methacrylate, octyl methacrylate, nonyl methacrylate, decyl methacrylate, isodecyl methacrylate, dodecyl methacrylate, tetradecyl methacrylate, N-octadecyl acrylamide, . -n-octylstyrene, isoprene, butadiene, piperylene, chloroprene, β-myrcene, and mixtures thereof; II) from about 15 to about 23% by weight comonomer selected from the group consisting of styrene, ethyl styrene and mixtures thereof; III) from about 5 to about 18% by weight divmyl benzene; and b) from about 3 to about 10% by weight of the emulsifier component; and 2) the water phase comprises from about 1 to about 40% calcium chloride 3. The process of any of the above claims wherein the monomer component in the oil phase is cured at a temperature between about 125°C and about 165°C. 4. The process of any of the above claims wherein the volume to weight ratio of water phase to oil phase is in the range of from about 10:1 to about 75: 1 5. The process of any of the above claims wherein the means to minimize volatilization of the components comprises conducting the polymerization and crosslmkmg at a curing pressure greater than atmospheπc pressure, preferably the cuπng pressure is provided by a hydrostatic head 6. The process of Claim 5 wherein the emulsion is formed at an emulsification pressure and the emulsification pressure is substantially equal to the curing pressure. 7. The process of Claim 5 wherein the emulsion is formed at an emulsification pressure and the emulsification pressure is lower than the curing pressure. 8. The process of any of the above claims wherein the process comprises the further step of dewatermg the polymeric foam material. 9. A polymeric foam prepared according to the process of any of the above claims.

Inventors: DESMARAIS THOMAS ALLEN, DYER JOHN COLLINS, HIRD BRYN, SHIVELEY THOMAS MICHAEL, DESMARAIS, THOMAS, ALLEN, DYER, JOHN, COLLINS, HIRD, BRYN, SHIVELEY, THOMAS, MICHAEL
Applicants: PROCTER & GAMBLE, THE PROCTER & GAMBLE COMPANY
Application year: 2000
Main classification: C08J9
IPC codes: C08F2, C08J9