MULTI-PHASE MELT CAST TOILET BAR AND A METHOD FOR ITS MANUFACTURE

Abstract: A multi-phase melt cast toilet bar which has at least one interface along a plane perpendicular to the plane formed by the x and y-axis of said bar, and a process of making the bar is described. Each phase, containing a cleansing agent, is reproducibly positioned in the bar to be used simultaneously thereby allowing the user to simultaneously derive benefits from the use of the cleansing agents contained in the bar's layers. The process for making the bar is a continuous one, whereby the molten cleansing agents are simultaneously or separately poured into the mould, simultaneously or separately allowed to harden, and where the mould divider is not removed or removed either after hardening of the adjacent molten cleansing agent but before the pouring of the next molten cleansing agent, or removed while at least one phase remains flowable. The hardened multi-phase toilet bar is finally ejected from the mould.

Description: MU TI-PHASE MELT CAST TOILET BAR AND A METHOD FOR ITS MANUFACTURE BACKGROUND OF THE INVENTION This invention relates generally to cleansing bars, and more particularly to cleansing bars having a plurality of layers of different materials oriented along a plane perpendicular to the plane formed by the x and y axis of said bar. DESCRIPTION OF THE RELATED ART Solid cleansing materials in the form of bars or cakes have been commercially available for many years. These bars may consist of soaps or detergents and may contain various other substances such as colouring materials, perfumes, benefiting agents, moisturisers and fillers. Different cleansing bar formulations are used to accomplish different cleansing needs. For example, skin on some parts of the body may be more sensitive than other areas. Some body areas are also more prone to perspire than other areas. In addition, the hands are more often exposed to more hard to remove dirt and grease than the rest of the body. These divergent cleansing problems have lead to the production of different cleansing bars designed for such different needs. Moreover, various individuals in the household may have different preferences or needs so that the household may keep on hand, at the lavatory or the shower, several different cleansing bars. European Patent Application No. 366209 and U.S. Patent No. 4,996,000 both disclose a cast moulded cleansing bar having a plurality of layers of different cleansing materials oriented along a plane parallel to the plane formed by the x and y axis. As used herein, the x axis is positioned along the longest dimension of the bar, typically the length, the y axis is positioned along the 2 nd longest dimension, typically the width, and the z axis is positioned along the shortest dimension of the bar, typically the height. Bars having layers oriented along a plane parallel to the plane formed by the x and y axis of the bar are characterised in that the user must rotate the bar in order to contact a substantial area of a different cleansing material. These bars are usually made using a layer by layer cast moulding or an extrusion process. On the other hand, the user would not have to rotate the toilet bar in order to simultaneously contact substantial areas of different cleansing materials using the toilet bar of the present invention. U.S. Patent No. 5,198,140 discloses an extrusion formed dual composition bar, the two layers of which are oriented along a plane parallel to the plane formed by the x and y-axis of the bar. Japanese Patent Application No. 59-157200 discloses a two phase toilet bar where the boundary layer is oriented along the bar' s plane perpendicular to the plane formed by the x and y axis of the bar. This two phase bar is made by melt casting a first cleansing composition, removing the first casting from the mould, spraying with colouring pigment, cutting the casting to shape a decorative curve, repositioning the cut first casting in a mould, and casting a second cleansing composition, which adheres to the first cleansing composition layer, to form a two phase bar with a curvilinear boundary layer. Although the finished bar of JP 59-157200 may be produced in a reproducible fashion, this process is disadvantageous because of the many separate manufacturing steps required. U.S. Patent No. 5,217,639 discloses a dual phase toilet bar where the interface layer between the two phases of the bar is located generally along the plane parallel to the plane formed by the x and y axis. The bar is cast by a sequential moulding technique wherein a first molten toilet composition is poured into a plastic mould filling the mould to the 50% mark, allowed to harden, and then a second molten toilet composition is poured into the mould and subsequently allowed to harden. One disadvantage of this moulding technique is the variability of the boundary line that is obtained between the two cleansing materials. None of the foregoing patents however, disclose a toilet bar with multi-layers cast along a straight or curvilinear plane perpendicular to the plane formed by the x and y axis of said bar, nor a moulding process where a formed divider is used to control the shape of each layer reproducibly in a multi-layer toilet bar such that the shape of the boundary layer can be custom made and is consistent from bar to bar. A distinct drawback of bars that are cast without formed dividers is that they may display random variation with the position of the boundary between the different cleansing compositions . SUMMARY OF THE INVENTION In one aspect, the present invention relates to a multilayer toilet bar containing a plurality of layers of cleansing material which are oriented to give maximum simultaneous benefit to the user of the toilet bar. In another aspect of the present invention, multi-layer toilet bars are provided with highly reproducible boundary lines between each layer. In another aspect of the present invention, a multi-layer toilet bar is provided that functions similarly to conventional toilet bar and its cleansing activity yet can provide skin benefits associated with different cleansing material compositions. A further aspect of the present invention is to provide a multi-layer toilet bar wherein certain active ingredients are incorporated into one layer but, not in the other. A still further aspect of the present invention is to provide a process for manufacturing a multi-layer toilet bar wherein a highly reproducible plurality of boundary layers oriented along the plane perpendicular to the plane formed by the x and y axis of the bar is obtainable. These and other aspects of the present invention will become more apparent from the summary, detailed description, and examples which follow. A multi-layer toilet bar is provided comprising a plurality of layers of cleansing materials, the layers having a common interface along said bar's flat or curvilinear plane perpendicular to the plane formed by the x and y axis of said bar and said layers having been melt cast in a unitary mould having a cavity and at least one removable formed divider contained within said cavity. The multi-layer bar is cast using a melt casting process that is continuous whereby the casting is not removed from the mould prior to completion of casting the finished toilet bar. Preferably, the multi-layer toilet bar has two layers of cleansing material and the mould has one removable formed divider. The formed divider can be slidably positioned in the mould cavity and in another aspect can be pivotally positioned in the mould cavity in a first position and the like. Preferably, the formed divider has a curvilinear shape. Preferably one of the layers of the multi-layer toilet bar is composed of a cleansing material which lathers and another layer is composed of a cleansing material which moisturises the skin. A first melt casting process for making the multi-layer toilet bar is also provided which comprises the steps of: positioning at least one removable formed divider along a flat or curvilinear plane perpendicular to the plane formed by the x and y axis of said bar in a unitary mould cavity to form at least two cavities; pouring a molten cleansing material into a first cavity defined by said mould and the removable divider; cooling the molten cleansing material until it is hardened sufficiently so that the formed divider can be removed from the mould; removing the divider from the mould either by sliding, pivoting or the like; pouring a second molten cleansing material into the mould cavity defined by the first hardened material and the mould; cooling the second molten cleansing material until it is hardened, and finally ejecting a hardened multi-layer toilet bar casting from the mould. Preferably, the process is continuous wherein the melt casting is not removed from the mould prior to completion of the casting of the finished bar. In another embodiment, a plurality of molten cleansing materials at a first temperature can be poured simultaneously or consecutively into their respective cavities, the molten material allowed to cool to a semi-solid state at a second temperature, and the removable dividers are then removed from the mould while at least one of the molten cleansing materials at said second temperature is hot enough to both flow away from the removable divider and fill the space in the mould formerly occupied by the divider. Preferably two molten materials are poured into two separate cavities divided by a single removable divider. In the case of the simultaneous pouring of a plurality of molten materials, the removable divider is preferably removed before the molten material cools to a second temperature of 85°C. Preferably, only one removable divider is positioned in the mould cavity and made to be slidably removed from the mould or pivotally removed from the mould. Preferably the multi-cleansing material is cooled by a method selected from the group consisting of refrigeration, cryogenics, ambient air cooling, and the like. In another embodiment of the bar and process of the present invention, at least one of the removable formed dividers may be a water soluble or water dispersible solid material, preferably a solid cleansing material, which is not removed after casting the adjacent layers whereby the divider becomes part of the finished bar. BRIEF DESCRIPTION OF THE DRAWINGS The invention will now be described by way of example only with reference to the accompanying drawings. Figure 1 is a perspective diagrammatic view of a formed divider being received in one embodiment of a unitary mould of the present invention. Figure 2 is a top planar view of a second embodiment of a unitary mould of the present invention. Figure 3 is a cross section taken along line 2-2 of figure 2. Figure 4 is a perspective view of the formed divider illustrated in figure 2. Figure 5 is a top planar view of one embodiment of a toilet bar of the present invention. Figure 6 is a cross section taken along line 4-4 of figure 5. Figure 7 is a top planar view of another embodiment of a toilet bar of the present invention. Figure 8 is a cross section taken along line 4-4 of figure 7. Figure 9 is a top planar view of a prior art toilet bar. Figure 10 is a cross section taken along line 4-4 of figure 9. DETAILED DESCRIPTION OF THE INVENTION: Referring to figure 1, casting assembly 10 includes unitary bottom mould 12, having a mould cavity 14 and locating apertures 16. Also depicted in Figure 1, is divider assembly 24 being received into unitary bottom mould 12. Divider assembly 24 includes formed divider 20, which is attached to divider assembly 24 via clip 22. Divider assembly 24 also includes handle 25 and locating pins 18. Locating pins 18 are received into their respective locating apertures 16 when the formed divider 20 is properly positioned in unitary bottom mould 12 and mould cavity 14. Figure 2 illustrates a top planar view of a second embodiment of casting assembly 30. Casting assembly 30 includes unitary bottom mould 12, formed divider 20, and mould cavity 14. In position 1, formed divider 20, is slidably positioned in casting assembly 30 when divider handles 28 are positioned in locating aperture 26. In position 2, formed divider 20 is slidably removed from casting assembly 30. Divider handles 28 are rigidly affixed to formed divider 20. Figure 3 shows a cross section taken along line 2-2 of figure 2. Figure 4 shows a perspective view of the formed divider 20 of figure 2 that has been slidably removed from casting assembly 30 in position 2. Figure 5 is a top planar view of one embodiment of a toilet bar 40 of the present invention. Toilet bar 40 has x axis 4, y axis 5 and z axis 6 and contains a first layer of cleansing material 46 and a second layer of cleansing material 44 juxtaposed along layer boundary 42. Figure 6 is a cross section taken along the line 4-4 of Figure 5. Figure 6 also depicts x axis 4, y axis 5 and z axis 6 of toilet bar 40 and second layer of cleansing material 44. Figure 7 is a top planar view of another embodiment of a toilet bar 60 of the present invention. Toilet bar 60 has x axis 4, y axis 5 and z axis 6 and contains first layer of cleansing material 66 and second layer of cleansing material 64 juxtaposed along layer 62. Figure 8 shows a cross section taken along line 4-4 of figure 7. Figure 8 also depicts x axis 4, y axis 5, and z axis 6 of toilet bar 60 and first cleansing layer 64 and second cleansing layer 66. Figure 9 is a top planar view of a prior art toilet bar 50 having x axis 4, y axis 5 and z axis 6 and a first cleansing layer 54. Figure 10 shows a cross section taken along line 4-4 of Figure 7. In figure 10, toilet bar 50 has x axis 6, a first cleansing material layer 54 and the second cleansing material layer 56, juxtaposed along boundary 52 which is oriented along x axis 6. The toilet bar of the present invention may contain one or more transparent, coloured, or opaque layers in any combination. Furthermore, the toilet bar of the present invention may contain layers with the same or different compositions. For good cohesion between adjacent layers, the composition of the layers should be compatible with each other. Usually this is achieved by minimising the disparity in the adjacent layers formulations or by minimising the difference in the surface free energy of the adjacent layer formulations. When a subsequent layer is poured, it may dissolve part of the previously solidified formulations at the layer' s interface and therefore provide good cohesion upon solidification. The multi-layer toilet bar of the present invention may contain one or more anionic detergents. The anionic detergent active which may be used may be an aliphatic sulfonate, such as a primary alkane (e.g., C 8 -C 2 2) sulfonate, primary alkane (e.g., C8-C22) disulfonate, C 8 -C2 2 alkene sulfonate, C 8 -C 2 2 hydroxyalkane sulfonate or alkyl glyceryl ether sulfonate (AGS) ; or an aromatic sulfonate such as alkyl benzene sulfonate. The anionic detergent active may also be an alkyl sulfate (e.g. C 12 -C 1 8 alkyl sulfate) or alkyl ether sulfate (including alkyl glyceryl ether sulfates) . Among the alkyl ether sulfates are those having the formula: RO(CH 2 CH 2 0) n Sθ3M wherein R is an alkyl or alkenyl having 8 to 18 carbons, preferably 12 to 18 carbons, n has an average value of greater than 1.0, preferably greater than 3; and M is a solubilising cation such as sodium, potassium, ammonium or substituted ammonium. Ammonium and sodium lauryl ether sulfates are preferred. The anionic may also be alkyl sulfosuccinates (including mono- and dialkyl, e.g. C6-C2 2 sulfosuccinates) ; alkyl and acyl taurates, alkyl and acyl sarcosinates, sulfoacetates, Cs- C2 2 alkyl phosphates and phosphates, alkyl phosphate esters and alkoxyl alkyl phosphate esters, acyl lactates, C 8 -C22 monoalkyl succinates and maleates, sulphoacetates, alkyl glucosides and acyl isethionates, and the like. Sulfosuccinates may be monoalkyl sulfosuccinates having the formula: R 0 2 CCH 2 CH(S0 3 M)C0 2 M; and amide-MEA sulfosuccinates of the formula; R 4 CONHCH 2 CH 2 θ 2 CCH 2 CH (SO3M) C0 2 M 4 wherein R ranges from C8-C2 2 alkyl and M is a solubilizing cation. Sarcosinates are generally indicated by the formula: R 1 CON(CH 3 )CH 2 C0 2 M, wherein R ranges from C8-C 2 0 alkyl and M is a solubilizing cation. Taurates are generally identified by the formula: R 2 CONR 3 CH2CH 2 S03M 2 3 wherein R ranges from Cs-C 20 alkyl, R ranges from C 1 -C 4 alkyl and M is a solubilizing cation. Particularly preferred are the Cs-Cis acyl isethionates . These esters are prepared by reaction between alkali metal isethionate with mixed aliphatic fatty acids having from 6 to 18 carbon atoms and an iodine value of less than 20. At least 75% of the mixed fatty acids have from 12 to 18 carbon atoms and up to 25% have from 6 to 10 carbon atoms. Acyl isethionates, when present, will generally range from about 10% to about 70% by weight of at least one layer of the toilet bar. Preferably, this component is present from about 30% to about 60% in the layer. The acyl isethionate may be an alkoxylated isethionate such as is described in U.S. Patent No. 5,393,466; which is hereby incorporated by reference. This compound has the general formula: 0 X Y R C-0-CH-CH 2 -(OCH-CH 2 ) m -S03M wherein R is an alkyl group having 8 to 18 carbons, m is an integer from 1 to 4, X and Y are hydrogen or an alkyl group having 1 to 4 carbons and M is a monovalent cation such as, for example, sodium, potassium or ammonium. It should be understood that at least one layer of the bar may comprise a certain amount of soap as anionic surfactant. When used, the term "soap" is used in its popular sense, i.e. alkali metal or alkanol ammonium salt of aliphatic alkane or alkene monocarboxylic acids. Sodium, potassium, mono-, di- and triethanol ammonium cations, or combinations thereof, are suitable for the purposes of the invention. Generally, sodium soaps are used. Soaps useful herein are the well known alkali metal salts of natural or synthetic aliphatic (alkanoic or alkenoic) acids having 13 to 22 cations, preferably 12 to 18. They may be described as alkali metal carboxylates of acrylic hydrocarbons having about 12 to 22 carbons . One or more amphoteric surfactants may be used in this invention. Such surfactants include at least one acid group. This may be a carboxylic or a sulphonic acid group. They include quaternary nitrogen and therefore are quaternary amido acids. They should generally include an alkyl or alkenyl group of 7 to 18 carbon atoms. They will usually comply with an overall structural formula: 0 R R -[-C-NH (CH 2 ) n -]m-N -X-Y R 3 where R is alkyl or alkenyl of 7 to 18 carbon atoms; 2 3 R and R are each independently alkyl, hydroxyalkyl or carboxyalkyl of 1 to 3 carbon atoms; n is 2 to 4; m is 0 to 1 ; X is alkylene of 1 to 3 carbon atoms optionally substituted with hydroxyl, and Y is -C0 2 - or -SO3-. Suitable amphoteric surfactants within the above general formula include simple betaines of formula: R R 1 -N + -CH2Cθ2 " R " and amido betaines of formula: R R 1 - CONH(CH 2 ) n -N + -CH 2 Cθ2 " R ~ where n is 2 or 3. 1 2 3 1 In both formulae R , R and R are as defined previously. R may in particular be a mixture of Cχ 2 and C 14 alkyl groups derived from coconut oil so that at least half, preferably at 1 least three quarters of the groups R have 10 to 14 carbon 2 3 atoms. R and R are preferably methyl. A further possibility is that the amphoteric detergent is a sulphobetaine of formula: R R 1 -N + -(CH 2 )3S0 3 " R J or R R 1 - CONH(CH 2 )m-N + -(CH 2 )3S03 " R where m is 2 or 3, or variants of these in which -(CH2. 3 SO 3 is replaced by: OH -CH 2 CHCH 2 S0 3 1 2 3 In these formulae R , R and R are as discussed previously. One or more nonionic surfactants may also be used in at least one layer of the toilet bar of the present invention. The nonionics which may be used include in particular the reaction products of compounds having a hydrophobic group and a reactive hydrogen atom, for example aliphatic alcohols, acids, amides or alkylphenols with alkylene oxides, especially ethylene oxide either alone or with propylene oxide. Specific nonionic detergent compounds are alkyl (Cg- 22) phenols ethylene oxide condensates, the condensation products of aliphatic (Cs-Ciβ) primary or secondary linear or branched alcohols with ethylene oxide, and products made by condensation of ethylene oxide with the reaction products of propylene oxide and ethylenediamine . Other so-called nonionic detergent compounds include long chain tertiary amine oxides, long chain tertiary phosphine oxides and dialkyl sulphoxide, and the like. The nonionic may also be a sugar amide, such as a polysaccharide amide. Specifically, the surfactant may be one of the lactobionamides described in U.S. Patent No. 5,389,279; which is hereby incorporated by reference or it may be one of the sugar amides described in Patent No. 5,009,814; which is hereby incorporated by reference. One or more cationic surfactants may also be used in at least one layer of the multi-layer toilet bar of the present invention . Examples of cationic detergents are the quaternary ammonium compounds such as alkyldimethylammonium halogenides. Other suitable surfactants which may be used are described in U.S. Patent No. 3,723,325 and "Surface Active Agents and Detergents" (Vol. I & II) by Schwartz, Perry & Berch, both of - I S which are incorporated into the subject application by reference. The multi-layer toilet bar of the present invention may also contain at least one layer having from 10 to 90% by wt . , preferably from 20 to 80% by wt . of a structurant and/or filler. Such structurant can be used to enhance the bar integrity, improve the processing properties, and enhance desired user sensory profiles. The structurant is generally a long chain, preferably straight and saturated, (C8-C24) fatty acid or ester derivative thereof; and/or branched long chain, preferably straight and saturated, (C8-C2 4 ) alcohol or ether derivative thereof. A preferred bar structurant is polyalkylene glycol with molecular weight between 2000 and 20,000, preferably between 3000 and 10,000. Those PEGs are commercially available, such as those marketed under the tradename of CARBOWAX SENTRY PEG8000 (R) or PEG4000 (R) by Union Carbide. Other ingredients that can be used as structurant or fillers include starches, preferably water soluble starches such as maltodextrin and polyethylene wax or paraffin wax. Structuring aids can also be selected from water soluble polymers chemically modified with a hydrophobic moiety or moieties, for example, EO-PO block copolymer, hydrophobically modified PEGs such as POE (200) -glyceryl-stearate, glucam DOE 120 (PEG 120 Methyl Glucose Dioleate) , and Hodag CSA-102 (R) (PEG-150 stearate) , and Rewoderm (PEG modified glyceryl cocoate, palmate or tallowate) from Rewo Chemicals. Other structuring aids which may be used include Amerchol Polymer HM 1500 (Nonoxynyl Hydroethyl Cellulose) . In addition, at least one layer of the multi-layer bar compositions of the invention may include from 0 to 15% by wt . optional ingredients as follows: perfumes; sequestering agents, such as tetrasodium ethylenediaminetetraacetate (EDTA) , EHDP or mixtures in an amount of from 0.01 to 1%, preferably from 0.01 to 0.05%; and colouring agents, opacifiers and pearlizers such as zinc stearate, magnesium stearate, Tiθ2, EGMS (ethylene glycol monostearate) or Lytron 621 (Styrene/Acrylate copolymer) and the like; all of which are useful in enhancing the appearance or cosmetic properties of the product. The compositions may further comprise antimicrobials such as 2-hydroxy-4,2' , 4 ' -trichlorodiphenylether (DP300) ; preservatives such as dimethyloldimethylhydantoin (Glydant XL1000) , parabens, sorbic acid, and the like. The compositions may also comprise coconut acyl mono- or diethanol amides as suds boosters, and strongly ionizing salts such as sodium chloride and sodium sulfate may also be used to advantage. Antioxidants such as, for example, butylated hydroxytoluene (BHT) and the like may be used advantageously in amounts of about 0.01% or higher if appropriate. Cationic polymers as conditioners which may be used include Quatrisoft LM-200 Polyquaternium-24 , Merquat Plus 3330 - (R) Polyquaternium 39; and Jaguar type conditioners. Polyethylene glycols as conditioners which may be used include: Polyox WSR-205 PEG 14M, Polyox WSR-N-60K PEG 45M, or Polyox WSR-N-750 PEG 7M. Another ingredient which may be included are exfoliants such as polyoxyethylene beads, walnut shells, apricot seeds, and the like. Compositions of the multi-layer inventive toilet bar also comprise from 1% to 10% by wt . , preferably from 4% to 7% by wt. water. In one embodiment of the invention, each layer' s composition comprises no more than about 60% surfactant. Said composition also contains from 10% to 70% by wt . structurant /filler . Because of lower surfactant levels, such compositions would be more "drying" on the skin and such compositions would comprise from 0.01 to 10% benefit agent/emollient. The benefit agent "composition" may be a single benefit agent component or it may be a benefit agent compound added via a carrier. Further the benefit agent composition may be a mixture of two or more compounds one or all of which may have a beneficial aspect. In addition, the benefit agent itself may act as a carrier for other components one may wish to add to the bar composition. The benefit agent can be an "emollient oil" by which is meant a substance which softens the skin (stratum corneum) by increasing its water content and keeping it soft by retarding decrease of water content. Preferred emollients include: (a) silicone oils, gums and modifications thereof such as linear and cyclic polydimethylsiloxanes; amino, alkyl, alkylaryl, and aryl silicone oils; (b) fats and oils including natural fats and oils such as jojoba, soybean, rice bran, avocado, almond, olive, sesame, persic, castor, coconut, mink oils; cacao fat; beef tallow, lard; hardened oils obtained by hydrogenating the aforementioned oils; and synthetic mono-, di- and triglycerides such as myristic acid glyceride and 2-ethylhexanoic acid glyceride; (c) waxes such as carnauba, spermaceti, beeswax, lanolin and derivatives thereof; (d) hydrophobic plant extracts; (e) hydrocarbons such as liquid paraffins, vaseline, macrocrystalline wax, ceresin, squalene, pristan and mineral oil; (f) higher fatty acids such as lauric, myristic, palmitic, stearic, behenic, oleic, linoleic, linolenic, lanolic, isostearic and poly unsaturated fatty acids (PUFA); (g) higher alcohols such as lauryl, cetyl, stearyl, oleyl, behenyl, cholesterol and 2-hexydecanol alcohol; (h) esters such as cetyl octanoate, myristyl lactate, cetyl lactate, isopropyl myristate, myristyl myristate, isopropyl palmitate, isopropyl adipate, butyl stearate, decyl oleate, cholesterol isostearate, glycerol monostearate, glycerol distearate, glycerol tristearate, alkyl lactate, alkyl citrate and alkyl tartrate; (i) essential oils such as mentha, jasmine, camphor, white cedar, bitter orange peel, ryu, turpentine, cinnamon, bergamot, citrus unshiu, calamus, pine, lavender, bay, clove, hiba, eucalyptus, lemon, starflower, thyme, peppermint, rose, sage, menthol, cineole, eugenol, citral, citronelle, borneol, linalool, geraniol, evening primrose, camphor, thymol, spirantol, penene, limonene and terpenoid oils; (j) lipids such as cholesterol, ceramides, sucrose esters and pseudo-ceramides as described in European Patent Specification No. 556,957; (k) vitamins such as vitamin A and E, and vitamin alkyl esters, including those vitamin C alkyl esters; (1) sunscreens such as octyl methoxyl cinnamate (Parsol MCX) and butyl methoxy benzoylmethane (Parsol 1789) ; (m) phospholipids; and (n) mixtures of any of the foregoing components, and the like. A particularly preferred benefit agent is silicone, preferably silicones having a viscosity greater than about 10,000 centipoise. The silicone may be a gum and/or it may be a mixture of silicones. One example is polydimethylsiloxane having viscosity of about 60,000 centistokes . The composition may also comprise decorative particulates including speckles, coloured or reflective particles, or shaped particles and the like. Conventional art recognised cast melt processing techniques may be used to fabricate the multi-layer toilet bar of the present invention. For example, the melted components of the bar of the present invention are usually blended together at elevated temperatures. Optionally the water level may be adjusted and the blending will continue. Next an optional drying step may follow whereby the water is reduced. Finally, the molten cleaning composition is poured into moulds and cooled to its hardening point. The moulds may be made of any rigid material that is not subject to attack by the ingredients of the toilet bar. Mould materials may include plastic, metal, glass, ceramic, or composite materials and the like. Cooling the molten cleansing materials can be accomplished by art recognised cooling techniques including refrigeration, cryogenics, ambient air and the like. Controlled cooling using thermostatic control cooling devices may also be employed. Conventional art recognised packaging materials may be used to package the inventive multi-layered toilet bar. The package may hold one or more separately packaged bars. The package may also have an optional transparent area to view part or all of the bar contained therein. Paper, plastic, or coated paper, or other flexible or rigid packaging materials that are compatible with the toilet bar may be used. Single layer or laminated packaging material structures may also be used. Preferably, the packaging material is moisture proof, and mould resistant. The packaging material should have good barrier properties to prevent the loss of volatile cleansing composition ingredients such as perfume. Examples of useful barrier materials are polymer coated paper board or other appropriate materials. Hot melt adhesive or contact adhesive such as glue may be used to adhere a portion of the carton and the wrapper. An appropriate coating would be a low density polyethylene coating and the like. Examples Two examples of the present invention are given below by way of illustration and not by way of limitation. In both examples, a two-layer cleansing bar according to the present invention, having a clear and a coloured cleansing layer oriented along a plane perpendicular to the plane formed by the x and y-axis of the bar was prepared having the formula listed below. The ingredients were blended together at a temperature of approximately 90°C in separate mixing vessels, with occasional stirring. All concentrations are expressed as a weight/weight percentage. A unitary elastomeric polymer mould having a substantially ovoid shape cavity size of 92 mm along its x axis, 64 mm along its y axis, and 35 mm along its z axis was used. A 3.2 mm (1/8 inch) thick, single sinusoidal shaped plastic divider, having an amplitude of 8 mm, was slidably positioned in the cavity along the bar's x- axis and perpendicular to the plane formed by the x and y- axis of the bar. In the first example, the transparent molten mixture at a temperature of 90°C was poured into one side of the mould and allowed to air cool for one hour until it was hardened. The divider was then removed and the coloured molten mixture at a temperature of 90°C was then poured into the mould cavity and also allowed to air cool for one hour until it was hardened. The bar was then easily ejected from the mould. In the second example, the transparent and coloured molten mixture at 90 °C was poured simultaneously into the divided cavities and the removable divider was removed before the melt had cooled below 85°C. The bars were tested under shower conditions at 100% RH with approximately 115 F water. Nine washes and two drops from a height of 1.07 m (42 inches) were used. The toilet bar did not fracture or break during the testing. Toilet bars produced by the sequential pouring and cooling technique have a sharp boundary between the two phases. Production time may however be reduced (e.g. cooling time may be reduced by 1/3) when the toilet bars are produced by the simultaneous or near simultaneous pouring of the molten components into the mould. The divider is then removed before any of the components cool to the point that neither component flows, preferably at a temperature equal to or greater than 85°C. The divider may be removed at temperatures below 85°C if lower melting components are used which still flow at such lower temperatures. Toilet bars produced by the simultaneous pour method are seen to have a distinct separation which follows the divider shape along the face of the bar that touches the inside or bottom face of the mould, i.e. the end opposite the open end. On the other hand, the side of the bar adjacent to the open end of the mould usually takes on a more linear and less distinct separation of the phases, notwithstanding the shape of the removable divider.

Claims: CLAIMS : 1. A multi-layered toilet bar comprising a plurality of layers of cleansing material, the layers having at least one common interface along a plane perpendicular to the plane formed by the x and y-axis of the bar; and at least two of the layers having been melt cast in a unitary mould having a cavity. 2. The multi-layered toilet bar of claim 1, wherein the melt casting is a continuous process whereby the casting is not removed from the mould prior to completion of casting the toilet bar. 3. The multi-layered toilet bar of claim 1, wherein the unitary mould has at least one removable, formed divider, and the toilet bar has at least two layers of cleansing material. 4. The multi-layered toilet bar of claim 3, wherein the at least one removable, formed divider in a first position divides the cavity into at least two cavities, the at least one divider being individually and slidably removed from the cavity in a second position. 5. The multi-layered toilet bar of claim 3, wherein the at least one removable, formed divider in a first position divides the cavity into at least two cavities, the at least one divider being individually and pivotally removed from the cavity in a second position. 6. The multi-layered toilet bar of any one of claims 3 to 5, wherein at least one of said formed dividers has a curvilinear shape. 7. The multi-layered toilet bar of any one of claims 3 to 6, wherein the at least one removable formed divider is composed of a material selected from a solid water soluble or dispersible material, metal, plastic, glass, ceramic, or a composite material. 8. The multi-layered toilet bar of claim 7, wherein at least one removable formed divider is a solid water soluble or dispersible material which becomes a part of the toilet bar. 9. The multi-layered toilet bar of claim 1 wherein at least one layer is composed of a cleansing material which lathers and at least one layer is composed of a cleansing material which moisturises. 10. A melt casting process for making a multi-layered toilet bar, comprising the steps of: positioning at least one removable, formed divider along a plane perpendicular to the plane formed by the x and y-axis of the bar in a unitary mould having a cavity, to form at least two cavities; pouring a first molten cleansing material into a first cavity defined by the mould and the at least one removable divider; cooling the first molten cleansing material until it is hardened; removing the at least one divider from the mould; pouring a second molten cleansing material into a second mould cavity defined by the hardened first cleansing material and the mould; cooling the second molten cleansing material until it is hardened; and ejecting a hardened multi-layered toilet bar casting from the mould. 11. The process of claim 10, wherein the melt casting is a continuous process whereby the casting is not removed from the mould prior to the completion of the casting. 12. The process of claim 10 wherein one removable divider in a first position divides the divisible cavity into a first cavity and a second cavity, said divider being slidably removed from the cavity in a second position. 13. The process of claim 10, wherein one removable divider in a first position divides said cavity into a first cavity and a second cavity, the divider being pivotally removed from said cavity in a second position. 14. The process of claim 12 or claim 13, wherein each of the formed dividers is composed of a material selected from a water soluble or dispersible material, metal, plastic, glass, ceramic, or a composite material. 15. The process of any one of claims 12 to 14, wherein each of the formed dividers has a curvilinear shape. 16. The process of claim 10, wherein at least one cleansing material lathers and the at least one second cleansing material moisturises. 17. The process of claim 10, wherein each of the molten cleansing materials are cooled by a method selected from refrigeration, cryogenics, or exposure to ambient air. 18. A melt casting process for making a multi-layered toilet bar, comprising the steps of: positioning at least one formed divider along a plane perpendicular to the plane formed by the x and y-axis of the bar in a unitary mould having a cavity to form at least two cavities; pouring a first molten cleansing material into a first cavity defined by the mould and the at least one formed divider; pouring a second molten cleansing material into a second cavity defined by the mould and the at least one formed divider; cooling the first and second cleansing material until they are hardened; ejecting a hardened, multi-layered toilet bar casting incorporating the at least one formed divider from the mould; and the at least one formed divider contains a water soluble or dispersible composition. 19. The process of claim 18 wherein the at least one formed divider contains a cleansing composition with a higher melting point then its adjacent cleansing composition phases . 20. A melt casting process for making a multi-layered toilet bar, comprising the steps of: positioning at least one removable, formed divider along a plane perpendicular to the plane formed by the x and y-axis of the bar in a unitary mould having a cavity, to form at least two cavities; pouring at least two molten cleansing materials into the at least two cavities at a first temperature; cooling the molten cleansing materials to a second temperature wherein at least one of the materials remain flowable; removing the at least one divider from the mould at the second temperature; cooling the molten materials until they are hardened; and ejecting a hardened multi-layered toilet bar casting from the mould. 21. The process of claim 20 wherein the second temperature is equal to or greater than 85°C.

Inventors: ABBAS SYED HUSAIN, ARKINS THOMAS DANIEL, BENNETT ROBERT ALFREAD, ROSS MICHAEL EDWARD, ABBAS, SYED, HUSAIN, ARKINS, THOMAS, DANIEL, BENNETT, ROBERT, ALFREAD, ROSS, MICHAEL, EDWARD
Applicants: LEVER HINDUSTAN LTD, UNILEVER NV, UNILEVER PLC, HINDUSTAN LEVER LIMITED
Application year: 2000
Main classification: C11D13
IPC codes: C11D13, C11D17