A CATALYST FOR ETHYLENE HOMO- AND COPOLYMERIZATION

Abstract: The present invention relates to a catalyst for homo- or co-polymerization of ethylene, or more particularly to a solid titanium catalyst supported on a magnesium-containing carrier, having high catalytic activity and excellent polymerization properties, which can provide polymers of high bulk density and reduce the amount of polymers dissolvable in a medium during polymerization.

Description: A CATALYST FOR ETHYLENE HOMO- OR COPOLYMERIZATION Field of the Invention The present invention relates to a catalyst for homo- or co-polymerization of ethylene, or more particularly to a solid titanium catalyst supported on a magnesium-containing carrier, having high catalytic activity and excellent polymerization properties, which can provide polymers of high bulk density and reduce the amount of polymers soluble in a medium during polymerization. Background of the Invention Magnesium-containing catalysts for preparation of an ethylene polymer or copolymer are known to have a high catalytic activity and to be instrumental in production of polymers having a high bulk density. They are also known to be suitable for both liquid and gaseous phase polymerization alike. By the liquid phase ethylene polymerization is meant the polymerization reaction performed of bulk ethylene or in such media as isopentane and hexane, while the features important for the catalyst used in such polymerizations are high catalytic activity, the resultant polymer's high bulk density, etc. Apart from these, a salient variable to decide the quahty of a catalyst, especially its commercial usefulness, is how much polymer remains soluble in the medium. Many catalysts based on magnesium titanium along with the processes of their production have been reported. Uses of a magnesium solution intended to obtain a catalyst for polymerization of olefin having a high bulk density have also been learned. There are ways of obtaining magnesium solutions by means of reacting magnesium compounds with such electron donors as alcohol, amine, cyclic ether, organic carboxylic acid, etc, in the presence of hydrocarbon solvents. Of which, instances of using alcohol are disclosed in U. S. Patents 4,330,649 and 5,106,807. A way of preparation of a magnesium-c-urying catalyst by reacting a magnesium solution with such a halogen-containing compound as titanium tetrachloride is also well known. Attempts have been made by addition thereto of ester compounds to adjust the catalytic activity and the resultant polymer's molecular weight distribution. Such catalysts provide high bulk density of polymer, but have much yet to be improved in the aspects of the catalytic activity and the produced polymer's molecular weight distribution. Tetrahydrofuran, a cyclic ether, is in use as solvent for magnesium compounds in U.S. Patents 4,777,639 and 4,518,706. U. S. Patents 4,847,227, 4,816,433, 4,829,037, 4,970,186, and 5,130,284 have disclosed processes for producing catalysts of excellent activity for polymerization of olefin having a high bulk density by reacting titanium chlorides with such electron donors as magnesium alkoxide, dialkyl phthalate, phthaloil chloride, etc. U.S. Patent 5,459,H6 has reported a process for preparation of a titanium-c-trrying solid catalyst by contact-reacting a magnesium solution containing, as electron donor, an ester having at least one hydroxy group with a titanium compound. Such processes make it possible to obtain a catalyst with a high catalytic activity, ensuring the produced polymer a high bulk density, but co-polymerization aspects have not been paid due heed. Summary of the Invention As can be seen from the above, it is desirable that catalysts be developed for homo- and co-polymerization of ethylene that are simple in their production processes, yet have a high catalytic activity, and provide the produced polymers with a high bulk density, and give reduced soluble polymer left behind in the medium in slurry polymerization. Hence the present invention, wherein it has been made possible to produce a catalyst of high activity from low-priced materials by means of a simple industrial process, the said catalyst being instrumental in preparation of polymers having a high bulk density and with less polymeric constituents soluble in the medium after the reaction. The actual steps and processes for production of the catalyst revealed in the present embodiment have never before been known in any existing patents or literature. The present embodiment provides a sohd catalyst of high catalytic activity for homo- and co-polymerization of ethylene, ensuring the polymer produced by the use of the catalyst with a high bulk density and excellent polymerization activity as well as highly decreased polymeric material to remain un-recovered in the medium. The present embodiment also provides a method, simple yet practical, for producing the catalyst solid component for homo- and coOpolymerization of ethylene. The other objectives and utility of the present invention will become clearer with references to the descriptions as below and the claims therein. The sohd titanium catalyst, described herein, for homo- and co-polymerization of ethylene, excellent in catalytic activity and instrumental in production of polymers with a high bulk density and less polymer soluble the medium, is produced by a simple yet effective process comprising Step (i) of producing a magnesium solution by contact-reacting a halogenated magnesium compound and alcohol, Step (ii) of reacting the solution with a phosphorus compound and an ester compound having at least one hydroxy group, and Step (iii) of adding thereto a mixture of a titanium compound and a silicon compound. The kinds of halogenated magnesium compounds usable include such dihalogenated magnesiums as magnesium chloride, magnesium iodide, magnesium fluoride, and magnesium bromide; such alkylmagnesium halides as methylmagnesium halide, ethylmagnesium halide, propylmagnesium hahde, butylmagnesium halide, isobutylmagnesium hahde, hexyhnagnesium halide, and amyhnagnesium hahde; such alkoxymagnesium halides as methoxymagnesium halide, ethoxymagnesium halide, iso-propoxymagnesium halide, butoxymagnseium hahde, and octoxymagnesium halide; and such an aryloxymagnesium hahde as phenoxymagnesium halide or methylphenoxymagnesium halide. A mixture of two or more of these compounds can also be used. These magnesium compounds may be effective when they are used in the form of a complex with other metals. The above-hsted halogenated magnesium compounds may be represented by simple chemical formulae, but exceptions may arise from differences in the methods of their production. In such exceptional cases they generally can be regarded as mixtures of these listed magnesium compounds. For instance, the compounds obtained by reacting a magnesium compound with a polysiloxane compound, a halogen-containing silane compound, ester, or alcohol; the compounds obtained by reacting a magnesium metal with alcohol, phenol, or ether in the presence of halosilane, phosphorus pentachloride, or thionyl chloride may also be used. The preferable magnesium compounds are magnesium halides, especially magnesium chloride and alkylmagnesium chloride, preferably those that have Cr-C 10 alkyl groups; alkoxymagnesium chlorides, preferably those that have Cι~Cιo alkoxy groups; and aryloxy magnesium chlorides and preferably those that have C 6 ~C o aryloxy groups. The magnesium solution may be produced with the aforesaid magnesium compounds by the use of an alcohol solvent in the presence or absence of a hy drocarbon solvent. The kinds of hydrocarbon solvents which may be used for this purpose include, for instance, such aliphatic hydrocarbons as pentane, hexane, heptane, octane, decane, and kerosene; such alicyclic hydrocarbons as cyclobenzene, methylcyclobenzene, cyclohexane, and methylcyclohexane; such aromatic hydrocarbons as benzene, toluene, xylene, ethylbenzene, cumene, and cymene; and such halogenated hydrocarbons as dichloropropane, dichloroethylene, trichloroethylene, carbon tetrachloride. and chlorobenzene. When a magnesium compound is turned into a solution, alcohol is used in the presence of any of the above-hsted hydrocarbons. The kinds of alcohols used for this puipose include, for instance, such an alcohol, which contains from 1~20 carbons as methanol, ethanol, propanol, butanol, pentanol, hexanol, octanol, decanol, dodecanol, octadecylalcohol, benzylalcohol, phenylethylalcohol, isopropylbenzylalcohol, and cumyl alcohol. Of these, the preferable is such an alcohol which contains 1~12 carbons. The desired average size and distribution of particles of the catalyst may vary according to the kinds and total quantity of alcohol, the kinds of magnesium compounds, the ratio of magnesium to alcohol, etc., but the total quantity of alcohol to obtain the magnesium solution is at least 0.5mol to one mol of the magnesium compound, preferably about 1.0mol~20mols, and more preferably about 2.0mols~10mols. The reaction of a magnesium compound with alcohol, in preparation of the solution, is preferably performed in a hydrocarbon medium, at the reaction temperature, though dependent upon the kinds and quantity of the alcohol, of about -25° C, preferably -10° C~200° C, and still more preferably about 0° C~150° C. The reaction preferably continues for about 30 minutes to four hours. The phosphorus compound used as an electron donor in preparation of the catalyst is represented by the following general formula: PX a R^OR^ or POX d R 3 e (OR 4 ) f . Here "X" is halogen atom or atoms; R 1 , R 2 , R 3 , and R 4 are independently hydrocarbons having 1~20 carbons, for example alkyl, alkenyl, aryl groups, etc., and , with a+b+c=3, O≤ a < 3, 0< b< 3, 0< c< 3; d+e+f+3, 0< d< 3, 0< e< 3, 0< f 3. Actual examples of these include phosphorus tribromide, diethylchlorophosphite, diphenylchlorophosphite, diethylbromophosphite, diphenylbromophosphite, dimethylchlorophospliite, phenylchlorophospl ite, trimethylphosphite, triethylphosphite, tri-n- bu-tylphosphite, trioctylphosphite, tridecylphosphite, tiiphenylphosphite, triethylphosphite, tri- n-butylphosphate, triphenylphosphate, etc., and, besides these, other phosphorus compounds, if they satisfy the above formula, can also be used. The quantity of these for use is adequately something below 0.25mol to a mol of the magnesium compound, and more preferably 0.2mol. The ester compound containing at least one hydroxy group for use as another electron donor in the production of the catalyst may include, for example: such unsaturated ahphatic acid esters containing at least one hydroxy group as 2-hydroxy ethylaciylate, 2-hydroxy ethylmethacrylate, 2-hydroxy propylacrylate, 2-hydroxy propylmethacrylate, 4-hydroxy butylacrylate, and pentaerythiitol triacrylate; such aliphatic monoesters or polyesters containing at least one hydroxy group as 2-hydroxy ethylacetate, methyl 3 -hydroxy butylate, ethyl 3-hydroxy butylate, methyl 2-hydroxy isobutylate, ethyl 2-hydoxy isobutylate, methyl-3- hydroxy-2-methyl propionate, 2,2-di-methyl-3-hydroxy propionate, eti.ιyl-6-hydiOxy hexanoate, t-butyl-2-hydroxy isobutylate, diethyl-3-hydroxy glutarate, ethyl lactate, isopropyl lactate, butylisobutyl lactate, isobutyl lactate, ethylmandelate, dimethyl ethyl tartrate, ethyl tartrate, dibutyl tartrate, diethyl citrate, triethyl citrate, ethyl 2-hydroxy caproate, and diethyl bis-( ydroxy methyl) malonate; such aromatic esters containing at least one hydroxy group as 2-hydroxy ethyl benzoate, 2-hydroxy ethyl salicylate, methyl 4-(hydroxy methyl) benzoate, methyl 4-hydroxy benzoate, ethyl 3-hydroxy benzoate, 4-methyl salicylate, ethyl salicylate, phenyl salicylate, propyl 4-hydroxy benzoate, phenyl 3-hydroxy naphthanoate, monoethylene glycol monobenzoate, diethylene glycol monobenzoate, and triethylene glycol monobenzoate; and such ahcychc esters containing at least one hydroxy group as hydroxy butyl lactone. The quantity of such an ester compound containing at least one hydroxy group should be 0.001mol~5mols to a mol of the magnesium, and preferably O.Olmol ~ 2mols. The quantity of these should preferably be 0.05mol ~ 3mols to one mol of the magnesium, and more preferably OJmol ~ 2mols. The temperature for the contact-reaction of the magnesium compound solution with a phosphorus compound and an ester compound containing at least one hydroxy group is adequately 0° C ~100° C, and more preferably 10° C~70° C. The magnesium compound solution which has been reacted with an ester compound containing at least one hydroxy group and a phosphorus compound is reacted with a mixture of a liquid titanium compound represented by the general formula Ti(OR) a X -^ ("R" is a hydrocarbon group, "X" a halogen atom, and "a" a natural number from 0 to 4) and a silicon compound represented by the general formula R n SiClψ- n ("R" is hydrogen; an alkyl, alkoxy, haloalkyl, or aryl group having 1—10 carbons; or a halosillyl or halosillylalkyl group having 1-8 carbons, and "n" is a natural number from 0 to 3), for crystallization of the particles of the catalyst. The kinds of titanium compounds which satisfy the above general formula Ti(OR) a X ^ include, for example, such tetrahalogenated titaniums as TiC , TiBr 4 , and TU 4 ; such trihalogenated alkoxytitaniums as Ti(OCH 3 )Cl 3 , Ti(OC 2 H 5 )Cl 3 , Ti(OC 2 H 5 )Br 3 , and Ti(O(i-C 4 H 3 ))Br 3 ; such dihalogenated alkoxy titaniums as Ti(OCH 3 ) 2 Cl 2 , Ti(OC 2 H 5 ) 2 Cl 2 . Ti(O(i- QH 9 )) 2 C_ 2 , or Ti(OC 2 H 5 ) 2 Br 2 ; and such tetraalkoxy titaniums as Ti(OCH 3 ) 4 , Ti(OC 2 H 5 ) 4 , and Ti(OGιH 9 ) 4 . Mixtures of the above titanium compounds may also be used. The preferable titanium compounds are halogen-containing compounds, and more preferably tetrachlorides of titanium. The silicon compounds which satisfy the above general foπnula R n SiCLi- n include, for example, silicon tetrachloride; such trichlorosilanes as methyltrichlorosilane, ethyltrichlorosilane, and phenyltrichlorosilane; such dichlorosilanes as dimethyldichlorosilane, diethyldichlorosilane, diphenyldichlorosilane, and methylphenyldichlorosilane; and such monochloorsilanes as tiimethylchlorosilane. The mixtures of these sihcon compounds can also be used. The preferable sihcon compound is silicon tetrachloride. The quantity of the mixture of titanium and sihcon compounds used in crystallization of the magnesium compound solution is adequately 0Jmol~200mols to a mol of the magnesium compound, preferably OJmol-lOOmols, and still more preferably 0.2mol~80mols. The molar ratio of titanium compound to sihcon compound is adequately 1 : 0.05-0.95, preferably 1 : 0J-0.8. The shape and size of the sohd matter crystallized by reaction of the magnesium compound solution with the mixture of titanium and sihcon compounds greatly vary, dependant upon the reaction conditions. Therefore it is advisable to carry out the reaction at a sufficiently low temperature for formation of the sohd constituents. Preferably, it is better to carry out a contact reaction at -70° C -70° C, and more profitably at -50° C - 50° C. After the contact reaction the temperature is slowly raised and it is left at 50° C~150° C for 0.5 hour to five hours for sufficient reaction. The solid particles obtained by the above-said reaction can be further reacted with a titanium compound. The titanium compound, which can be used for this purpose, is a titanium hahde or a halogenated alkoxy titanium having 1 to 20 carbons in the alkoxy group. In some cases mixtures of these may also be used. Of these, the preferable is a titanium hahde or a halogenated alkoxy titanium having one to eight carbons in the alkoxy group, and still more preferable is a titanium tetrahahde. The solid titanium catalyst produced by the method provided herein is profitably used in homo- and co-polymerization of ethylene. This catalyst is especially preferably used in polymerization of ethylene and also in co-polymerization of ethylene with such α-olefins containing three or more carbons as propylene, 1-butene, 1-pentene, 4-methyl-l-pentene, and 1-hexene. The polymerization reaction in the presence of the catalyst is performed with the use of (a) the sohd titanium catalyst consisting of magnesium, titanium, halogen and an electron donor, and (b) a catalyst system consisting of compounds of the organometals of Groups II and III on the periodic table of elements. The sohd complex titanium catalyst (a) can also be pre-polymerized in ethylene or α- olefin, prior to use as constituent in a polymerization reaction. The pre-polymerization can be performed in the presence of a hydrocarbon solvent like hexane at a sufficiently low temperature and under the low pressure conditions of ethylene or α-olefin in the presence of the aforesaid catalyst constituents and such an organic aluminum compound as triethylaluminum. Pre-polymerization makes catalyst particles wrapped in polymers to maintain the shape of the catalyst and thus helps to better the shape of the polymer after polymerization. The ratio in weight of polymer to catalyst after the pre-polymerization is usually 0.1 : 1 -20 : 1. The organometal compound (b) can be represented by the general formula: MR„. Here "M" is a metals of Groups 2, 12, or 13 on the periodic table of elements, such as magnesium, calcium, zinc, boron, aluminum or gallium; "R" is an alkyl groups having 1 to 20 carbons such as methyl, ethyl, butyl, hexyl, octyl, or decyl; and "n" is the valences of the metal atoms. For the more preferable organic metal compounds such trialkylaluminums containing an alkyl group of one to six carbons as triethyl-duminum and triisobutylaluminum. Their ir ixtures are also commendable. In some cases such organic aluminum compounds containing one or more halogen or hydride groups as etiiylalu inum dichloride, chemyl-duminum chloride, ethylaluminum sesquichloride, or diisobutylεduminum hydride may be used. The polymerization reaction may be performed in gaseous phase in bulk in the absence of an organic solvent, or in a liquid slurry in the presence of an organic solvent. The reactions, however, are performed in the absence of oxygen, water, or any compounds that may act as catalytic poison. In the case of liquid slurry polymerization, the preferable concentration of the solid complex*catalyst, is about 0.001Mmol~5 Mmols, more preferably about 0.001molA).5Mmols in terms of the number of titanium atoms in the catalyst to a hter of the solvent. For the solvent, such alkanes or cycloalkanes as pentane, hexene, heptane, n-octane, isooctane, cyclohexene, and methylcyclohexene, such alkylaromatics as toluene, xylene, ethylbenzene, isopropylbenzene, ethyltoluene, n-propylbenzene, and diethylbenzene, such halogenated aromatics as chlorobenzene, chloronaphthalene, and orthodichlorobenzene; and nrixtures of these, are useful. In the case of gaseous polymerization the quantity of the solid complex titanium catalyst (a) is about 0.001Mmol~5Mmols, preferably about O.OOlMmo .OMmols, still more preferably about 0.01MmoM).5Mmols in terms of the number of titanium atoms to a hter of polymerization reaction volume. The preferable concentration of the organometal compound (b) is about lmol- 2,000mols, more preferably about 5mols~500mols, in terms of the number of the atoms of the organometal to a mol of the titanium atoms in the catalyst (a). To secure a high speed in polymerization the reaction is performed at a sufficiently high temperature regardless of the polymerization process. Generally, about 20° C -200° C are adequate, and more preferably 20° C~95° C. The pressure of a monomer at the time of polymerization is adequately 1 ~100 atm, and more preferably 2~50 arm. In the present invention, the molecular weight is expressed as a melt index (ASTM D1238), which is generally known in the art. The value of MI generally becomes greater as the molecular weight decreases. The density of ethylene co-polymers was measured according to the method of ASTM D-1505 by way of use of indirect gauge of co- polymerization by catalysts, which is also commonly known in the art. In other words, the lower the density of co-polymers obtained at the same ratio of concentrations of co-monomers and monomers, the better was the co-polymerization by the catalyst. After cooling the entire polymerization reactor to room temperature after polymerization, the polymers were filtered out, followed by separation of the medium and its volatilization. Then, the weight of polymers remaining therein was measured. As a result, the amount (wt%) of polymers melted in the polymerization medium was expressed as a weight ratio as against that of the polymers not melted therein. Of course, this type of measurement is generally well known in the art as well. The products obtained with the use of the catalyst are ethylene polymer or copolymers of ethylene with α-olefin, having an excellent bulk density and fluidity. The yield of polymers is sufficiently high, requiring therefore no further process for removal of the residue of the catalyst. The present invention is described in further detail below, through embodiment examples and comparative examples. The present invention is not limited to these examples. Detailed Description of the Preferred Embodiment Example 1 Production of catalyst A sohd complex titanium catalyst was prepared through the following three steps: Step (i) Production of a magnesium solution Into a 1.0-liter reactor equipped with a mechanical stirrer, converted into nitrogenous atmosphere, 9.5g of MgCl 2 and 500ml of decane were introduces. The reactor was stirred at 300rpm, 72ml of 2-ethylhexanol was added. The temperature was raised to 110° C, and the reaction was allowed to continue for three hours. The homogeneous solution obtained in this way was cooled to room temperature (25° C). Step (ii) Contact-reaction of the magnesium solution with a phosphorus compound and ester compound containing a hydroxy group To the above magnesium solution cooled to room temperature was added 5Jml of trietylphosphate and 2.4ml of 2-hydroxyethylmethacrylate, and the solution was left to react for one hour. Step (iii) Treatment with a mixture of titanium compound and a sihcon compound The above solution was adjusted to room temperature (25° C), and to it a solution of a mixture of 70ml of titanium tetrachloride and 70ml of silicon tetrachloride was dripped for two hours. After the dripping the temperature of the reactor was raised to 80° C, for one hour, and the reactor was then kept at that temperature for another hour. After stirring was stopped, the solution at the top was separated, and to the sohd layer left behind 300ml of decane and 100ml of titanium tetrachloride were added. The temperature was raised to 100° C and kept at that temperature for two hours. After the reaction the reactor was cooled to room temperature, and washed with 400ml of hexane until unreacted titanium tetrachloride was completely removed. The titanium content of the thus prepared sohd catalyst was 5.1%. Polymerization of ethylene A 2-liter high pressure reactor was dried in an oven, and assembled while it was hot. The inside of the reactor was converted into nitrogen atmosphere by the alternating treatment with nitrogen and evacuation for three times. 1,000ml of n-hexane was put into the reactor, and trietliyl-Juminum by 2mmols and the sohd catalyst by 0.03mmol in terms of the number of titanium atoms were added, followed by the addition of 1000ml of hydrogen. While agitating at 700rpm, the temperature of the reactor was raised to 80° C, and after adjusting the pressure of ethylene to 80psi, polymerization was performed for an hour. After the polymerization, the reactor was cooled to room temperature, and a small amount of ethanol was added to the polymerized. The thus prepared polymer was then collected by separation, and dried in a vacuum oven at 50° C for at least six hours to finally obtain polyethylene in the form of white powder. Copolymerization of ethylene with 1 -hexene A 2-liter high-pressure reactor was dried in an oven, and assembled while hot. The inside of the reactor was converted into a nitrogen atmosphere by the alternating treatment with nitrogen and evacuation three times. After pouring 1,000ml of n-hexane into the reactor, 2mmols of triethyl-iluminum and 14.0ml of 1-hexane were added thereto, and thereafter 200ml of hydrogen was added. As the stirrer was turned at 700rpm, the temperature of the reactor was raised to 80° C, 0.03mmols of the catalyst in a bo be, fixed in advance to the reactor, was added to the reactor by the pressure of ethylene, adjusted to 80psi. The remnants of the catalyst in the bombe were washed down to the reactor with a small quantity of hexane connected with the bombe. The reaction was allowed to continue for 20 minutes. After completion of the reaction, the reactor was lowered to room temperature, and the content of the reactor was separated into the produced polymer and hexane, the polymerization medium. The polymer was dried in a vacuum oven at 50° C for six hours, to obtain polyethylene in the form of white powder. The polymerization activity (kg polyethylene/g catalyst) was calculated in terms of the amount of the used catalyst (g) per the weight (kg) of the thus produced polymer. The results of the polymerization are given together with the polymer's bulk density, flow index (g 10 minutes), concentration, the quantity (wt%) of the polymer soluble in the medium, in Table 1. Example 2 The catalyst was produced using 7.2ml of triethylphosphate and 2.4ml of 2-hydroxy ethylmethacrylate in Step (ii) of the process for production of the catalyst in Example 1. The prepared catalyst's titanium content was 4.9%. Ethylene polymerization and ethylene/1- hexene copolymerization were carried out as in Example 1, the results being given in Table 1 below. Example 3 The catalyst was produced using 8Jml of tributylphosphate and 2.4ml of 2-hydroxy ethylmethacrylate in Step (ii) of the process for production of the catalyst in Example 1. The prepared catalyst's titanium content was 4.7%. Ethylene polymerization and ethylene/1- hexene copolymerization were carried out as in Example 1 , the results being given in Table 1 below. Example 4 The catalyst was produced using 8Jml of tributylphosphite and 2.4ml of 2-hydroxy ethylmethacrylate in Step (ii) of the process for production of the catalyst in Example 1. The prepared catalyst's titanium content was 5.2%. Ethylene polymerization and ethylene/1- hexene copolymerization were carried out as in Example 1, the results being given in Table 1 below. Example 5 The catalyst was produced using 4.3ml of diethylchlorophosphite and 2.4ml of 2-hydroxy ethyhnethacrylate in Step (ii) of the process for production of the catalyst in Example 1. The prepared catalyst's titanium content was 5.0%. Ethylene polymerization and ethylene/1- hexene copolymerization were carried out as in Example 1, the results being given in Table 1 below. Example 6 The catalyst was produced using 2.6ml of phosphorus tetrachloride and 2.6ml of 2- hydroxy ethylmethacrylate in Step (ii) of the process for production of the catalyst in Example 1. The prepared catalyst's titanium content was 4.6%. Ethylene polymerization and ethylene/1 -hexene copolymerization were carried out as in Example 1, the results being given in Table 1 below. Example 7 The catalyst was produced using 7.2ml of triethylphosphate and the same mols of 2- hydroxy ethylacrylate instead of 2-hydroxy ethylmethacrylate in Step (ii) of the process for production of the catalyst in Example 1. The prepared catalyst's titanium content was 4.5%. Ethylene polymerization and ethylene/1 -hexene copolymerization were carried out as in Example 1, the results being given in Table 1 below. Example 8 The catalyst was produced using 7.2ml of triethylphosphate and the same mols of diethyl- 3-hydroxyglutarate instead of 2-hydroxy ethylmethacrylate in Step (ii) of the process for production of the catalyst in Example 1. The prepared catalyst's titanium content was 4.6%. Ethylene polymerization and ethylene/1 -hexene copolymerization were carried out as in Example 1, the results being given in Table 1 below. Example 9 The catalyst was produced using 5Jml of triethylphosphate and 1.2ml of 2-hydroxyethyl methaacrylate in Step (ii) of the process for production of the catalyst in Example 1. The prepared catalyst's titanium content was 5.3%. Ethylene polymerization and ethylene/1- hexene copolymerization were carried out as in Example 1, the results being given in Table 1 below. Comparative Example 1 The catalyst was prepared as in Example 1 above, using only 5Jml of triethylphosphate without 2-hydroxy ethyl methacrylate in Step (ii) of the process for preparation of catalyst. The thus prepared catalyst's titanium content was 5.7%. ethylene polymerization and ethylene/1 -hexene copolymerization were carried out as in Example 1, the results being given in Table 1 below. Comparative Example 2 The catalyst was prepared as in Example 1 above, but using only 2.4ml of 2-hydroxyethyl methacrylate without triethylphosphate in Step (ii) of the process for preparation of catalyst. The thus prepared catalyst's titanium content was 5.1%. Ethylene polymerization and ethylene/1 -hexene copolymerization were carried out as in Example 1, the results being given in Table 1 below. Comparative Example 3 The catalyst was prepared as in Example 1 above, not using either triethylphosphate or 2- hydroxy ethylmethaacrylate in Step (ii) of the process for preparation of catalyst. The thus prepared catalyst's titanium content was 5.5%. Ethylene polymerization and ethylene/1- hexene copolymerization were carried out as in Example 1, the results being given in Table 1 below. ISA KR i5.io.200i Table 1 Bulk Melting Amount of Dissolved Examples Density Index Density Polymers Activity* (g/ml) (g/lO min) (g ml) (wt%) Polymer 3.9 0.37 3.8 0.967 Copolymer 12.5 0.26 0J2 0.941 0J2 Polymer 3.7 0.36 4J 0.966 Copolymer 11.7 0.27 0.65 0.939 0.69 Polymer 4.1 0.37 3.9 0.965 Copolymer 13.8 0.26 0.82 0.938 0.61 Polymer 0.36 3.5 0.966 Copolymer 11.6 0.25 0.94 0.941 0.81 Polymer 5.6 0.36 3.3 0.965 Copolymer 11.9 0.25 0.86 0.94 0.80 Polymer 3.9 0.37 3.5 0.966 Copolymer 12.1 0.27 0.88 0.941 0.74 Polymer 3.6 0.36 3.9 0.967 Copolymer 11.4 0.27 0.74 0.940 0.89 Polymer 3.6 0.36 3.3 0.966 Copolymer 11.2 0.26 0.69 0.938 0.89 Polymer 3.9 0.37 3.9 0.967 Copolymer 12.3 0.27 0.71 0.938 0.83 Comp. 1 Polymer 3.2 0.30 2.2 0.967 Copolymer 9.3 0.12 0.31 0.951 1.81 Comp.2 Polymer 3.1 0.31 2.5 0.966 Copolymer 9.6 0.17 0.62 0.950 1.56 Comp. 3 Polymer 3.0 0.29 1.8 0.966 Copolymer 8.7 0.11 0.21 0.954 2.94 1 (Kg PE./g catalyst, HR) The catalyst prepared herein for preparation of an ethylene polymer and copolymer, though simple in its production method is excellent in its catalytic activity and polymerization activity alike, while the polymer processed with the catalyst has a high bulk density but less polymers soluble in the polymerization medium. Further modification and alternative embodiments of various aspects of the invention will be apparent to those skilled in the art in view of this description. Accordingly, this description is to be constructed as illustrative only and is for the purpose of teaching those skilled in the art the general manner of carrying out the invention. It is to be understood that the forms of the invention shown and described herein are to be taken as the presently preferred embodiments. Elements and materials may be substituted for those illustrated and described herein, parts and processes may be reversed, and certain features of the invention may be utihzed independently, all as would be apparent to one skilled in the art after having the benefit of this description of the invention. Changes may be made in the elements described herein without departing from the spirit and scope of the invention as described in the following claims.

Claims: CLAIMS What is claimed is: 1. A sohd titanium catalyst for homo- or co-polymerization of ethylene, wherein said catalyst is produced by the method comprising: (1) producing a magnesium solution by contact-reacting a halogenated magnesium compound with alcohol; (2) reacting said magnesium solution with a phosphorus compound and an ester compound having at least one hydroxy group; and (3) adding a mixture of a titanium compound and a sihcon compound thereto. 2. The catalyst of Claim 1, wherein said phosphorus compound comprises a compound represented by a general formula of PXaR^OR 2 ). or POXdR 3 e (OR )f , in which X is a halogen atom; R 1 , R 2 , R 3 , and R 4 are hydrocarbons respectively having 1~20 carbons, an alkyl, alkenyl, or aryl group, either identical with or different from each other, with a+b+c=3, 0< a< 3, 0< b< 3, 0< c< 3, and d+e+f^3, 0< d< 3, 0< e< 3, 0< f< 3. 3. The catalyst of Claim 2, wherein said phosphorus compound is phosphorus trichloride, phosphorus tribromide, diethylchlorophosphite, diphenylchlorophosphite, diethylbromophosphite, diphenylbromophosphite, dimethylchlorophosphite, phenylchlorophosphite, trimehtylphosphite, triethylphosphite, tri-n-butylphosphite, trioctylphosphite, tridecylphosphite, triphenylphosphite, triethylphosphate, tri-n- butylphosphate, or triphenylphosphate. 4. The catalyst of Claim 1, wherein said ester compound containing at least one hydroxy group is an unsaturated ahphatic acid ester having at least one hydroxy group, which is selected from the group consisting of 2-hydroxy ethylacrylate, 2-hydroxy ethylmethacrylate, 2-hydroxy propyl acrylate, 2-hydroxy propylmethacrylate, 4- hydroxy butylacrylate, pentaerithritol tri-acrylate; an ahphatic monoester or polyester containing at least one hydroxy group, which is selected from the group consisting of 2- hydroxy ethyl acetate, methyl 3-hydroxy butylate, ethyl 3-hydroxy butylate, methyl 2- hydroxy isobutylate, ethyl 2-hydroxy isobutylate, methyl 3-hydroxy-2-methyl propionate, 2,2-dimethyl-3-hydroxy propionate, ethyl-6-hydroxy hexanoate, t-butyl-2- hydroxy isobutylate, diethyl-3-hydroxy glutarate, ethyl-lactate, isopropyl lactate, butyl- isobutyl lactate, isobutyl lactate, ethyl mandelate, dimethyl ethyl tartrate, ethyl tartrate, dibutyl tartrate, diethyl citrate, triethyl citrate, ethyl-2-hydroxy-caproate, diethyl bis- (hydroxymethyl) malonate; an aromatic ester having at least one hydroxy group, which is selected from the group consisting of 2-hydroxy ethyl benzoate, 2-hydroxy ethyl salicylate, methyl-4-(hydroxy methyl) benzoate, methyl-4-hydroxy benzoate, ethyl-3-hydroxy benzoate, 4-methyl salicylate, ethyl salicylate, phenyl salicylate, propyl-4-hydroxy benzoate, phenyl-3-hydroxy naphthanoate, monoethylene glycol monobenzoate, diethylene glycol benzoate, triethylene glycol monobenzoate; and an ahcychc ester having at least one hydroxy group as in hydroxy butyl-lactone; 5. The catalyst of Claim 1, wherein said titanium compound is represented by a general formula of Ti(OR) a Xι- a , in which R is a hydrocarbon group, X is a halogen atom, and a is a natural number of 0 -4; and wherein said sihcon compound is represented by a general formula of R n SiCl n4 , in which R is hydrogen, an aryl, alkoxy, haloalkyl or alkyl group having 1-10 carbon atoms, or a halosilylalkyl or halosilyl group having 1-8 carbon atoms, and n is a natural number of 0 ~ 3. 6. The catalyst of Claim 5, wherein said titanium compound is a 4-halogenated titanium, which is selected from the group consisting of TiCL t , TiBr 4 , and Til-.; a 3-halogenated alkoxy titanium, which is selected from the group consisting of Ti(OCH 3 )Cl 3 , Ti(OC 2 H 5 )Cl 3 , Ti(OC 2 H 5 )Br 3 , and Ti(O(i-QH 9 ))Br 3 ; a 2-halogenated alkoxy titanium, which is selected from the group consisting of Ti(OCH 3 ) 2 Cl 2 , Ti(OC 2 H 5 ) 2 Cl 2 , Ti(O(i- QHg hCk, and Ti(OC 2 H 5 ) 2 Br 2 ; and a tetralkoxy titanium, which is selected from the group consisting of Ti(OCH 3 ) 4 , Ti(OC 2 H 5 ) , and Ti(OGιH 9 ) ; and wherein said silicon compound is silicone tetrachloride; a trichlorosilane, which is selected from the group consisting of trichlorosilane, methyltrichlorosilane, ethyltrichlorosilane, and phenyltrichlorosilane; a dichlorosilane, wliich is selected from the group consisting of dimethylchlorosilane, diethyldichlorosilane, diphenyldichlorosilane, and methylphenyldichlorosilane; and amonochlorosilane as intrimethylchlorosilane. 7. The catalyst of Claim 5, wherein said titanium compound is titanium tetrachloride, and said sihcon compound is silicon tetrachloride.

Inventors: KIM SANG-YULL, LEE WEON, YANG CHUN-BYUNG, KIM, SANG-YULL, LEE, WEON, YANG, CHUN-BYUNG
Applicants: SAMSUNG GENERAL CHEMICALS CO, SAMSUNG GENERAL CHEMICALS CO. LTD.
Application year: 2000
Main classification: C08F4
IPC codes: C08F4, C08F10, C08F110, C08F210