Dimerization of isobutene

Abstract: A process for the dimerization of at least one olefin with a carbon number between 2 and 10 by contacting the feed with a catalyst system comprising at least: (a) tectometallosilicate zeolite with having TON-type structure, (b) tectometallosilicate zeolite with having MTT-type structure, (c) tectometallosilicate zeolite with the same structure as that of the ZSM-48 zeolite, or (d) silicoaluminophosphate (SAPO) zeo-type with AEL-type structure; under dimerization condition to produce highly branched olefins.

Description: BACKGROUND OF INVENTION 1. Field of the invention This invention relates to the conversion of isobutene by dimerization to highly branched octenes especially trimethylpentenes and dimethylhexenes, in the presence of a catalyst. This invention also pertains to the use of specific zeolite and/or zeo-type containing catalyst. Trimethylpentenes are highly valuable intermediates for the production of isooctane by hydrogenation. In addition, both the trimethylpentenes and dimethylhexenes may be used as intermediate for the production of xylenes especially p-xylene. Isooctane and p-xylene are valuable chemicals for gasoline blending and the manufacture of polyester fiber respectively. 2. Description of the prior art Dimerization ofbutenes especially isobutene is a commercially important reaction. Many catalysts have been claimed for this reaction. For example supported and promoted sulfuric acid and phosphoric acid, and a variety of other catalysts have been claimed in USP 3,760,026 . USP 5,118,900 describes the dimerization of isobutene over zeolite Y or a modified zeolite Y. However, these catalysts also produce oligomers of isobutenes. European Patent 0 247 802 describes the isomerization of olefins especially butenes to produce isobutenes over uni-directional medium pore zeolites whereas European Patent 0 124 998 describes the production of transport fuel from small olefins by oligomerization, cracking, and isomerization over medium pore zeolites. WO 91/18851 discloses a process for a conversion of an n-olefin of 3 to 9 carbon atoms to another unsaturated compound comprising contacting the olefin in the liquid or vapor phase with a catalyst which comprises a molecular sieve which has been ion-exchanged with a cation to provide a Lewis acid site. The molecular sieve may be a zeolite or a silica/alumina phosphate, such as zeolite Y, zeolite beta, ZK-5; ZSM-5, ZSM-12, ZSM-22, ZSM-23 or a SAPO 11. The cation may be a divalent cation, such as Mg, Ca, Sr or Ba. SUMMARY OF THE INVENTION The present invention relates to the dimerization of isobutene over a zeolite or a zeo-type containing catalyst. DESCRIPTION OF PREFERRED EMBODIMENTS The object is achieved by a process according to claim 1. The inventive process is moreover characterized in that the catalyst is subjected to an activation treatment thermochemically, which is heating in steam, in an inert atmosphere, oxidative or reductive environment prior to contact with the olefinic feed. In one embodiment the dimerization reaction is carried out at temperature ranging from 0° to 300°C. In one preferred embodiment the dimerization reaction is carried out at temperature ranging from 10°C to 150°C. According to another embodiment the dimerization reaction is carried out at pressure ranging from 203 kPa (15 psig) to 6997 kPa (1000 psig). It is preferred that the dimerization reaction is carried out at pressure ranging from 307 kPa (30 psig) to 1479 kPa (200 psig). Additionally, the inventive process is characterized in that the dimerization reaction is carried out at WHSV of 0.5h -1 to 100h -1 . It is preferred that the dimerization reaction is carried out at WHSV of 1.0h -1 to 30h -1 . Finally, it is preferred that the dimerization reaction is carried out in conjunction with an aromatization process of the highly branched products especially those products having 8 carbons. The present invention relates to the dimerization of isobutene over a zeolite or a zeo-type containing catalyst. The zeolite or zeo-type material is chosen from any of the following or a combination thereof (a) tectometallosilicate with having TON-type structure, (b) tectometallosilicate with having MTT-type structure, (c) tectometallosilicate with the same structure as that of the ZSM-48 zeolite, or (d) silicoaluminophosphate (SAPO) with AEL-type structure. These structure types are described in (a) the Atlas of Zeolite Structure Types by W.M. Meier, D. H. Olson and Ch. Baerlocher, fourth revised edition (I 996), published on behalf of the Structure Commission of the International Zeolite Association, and/or (b) (Handbook of Molecular Sieves, by Rosemarie Szostak (I 992), published by van Nostrand Reinhold. Zeolites and zeotype materials (such as silicoaluminophosphates) are structurally ordered porous materials having a rigid regular three dimensional network of SiO 4 and AlO 4 tetrahedra in case of the zeolite materials and SiO 4 , AlO 4 , and PO 4 tetrahedra in the case of silicoaluminophosphates. The tetrahedra are cross-linked by sharing the oxygen atoms forming a structure that is sufficiently open to accommodate voids and /or channels that are capable of sorbing water and hydrocarbons depending on the diameter of the window controlling the entrance to the channel system relative to the size of sorbate species. This has led to zeolites and other zeo-type materials being called "molecular sieves". The relative population of the different tetrahedral atoms in the framework determines the composition of the framework. The extra-framework material together with the framework composition adds up to the bulk composition of the molecular sieve. Zeolites and zeo-type materials are best classified by their framework topological structure irrespective of their composition, exact cell parameters, or symmetry. A code consisting of three capital letters has been adopted for each known structure type following the recommendations by IUPAC on zeolite nomenclature (Chemical Nomenclature, and Formulation of Composition, of Synthetic and Natural Zeolites). These nomenclatures refer only to those zeolite and zeo-type materials that have known zeolite. Materials with unknown structure (topology) are referred to by their individual reference but still identified by their x-ray powder diffraction pattern. In addition to their diffraction pattern the structural properties of these zeolite may also be characterized by e.g. their sorption and ion-exchange properties. The zeolites and. zeo-type materials of interest to the invention are those that have a medium pore and unidirectional channel system. Medium pore means that the window controlling the entrance to the channel system consists of 10-T ring, i.e. the window is formed by joining 10 tetrahedra through their oxygen atoms. Unidirectional medium pore channel system means that the channel that is controlled by 10-T-ring window is not intersected by a another channel with another 10-T-ring channel or larger. Examples of the zeolites of interest to this invention include TON-type structure (Theta-1, ZSM-22, NU- 10, KZ-2, ISI-1, and their compositional variants), MTT-type structure (ZSM-23, EU-13, KZ-1, IST-4, and their compositional variants), FER-type structure (FU-9, NU-23, ZSM-35, and their compositional variants), ZSM-48 and its compositional variants, AEL-type structure (SAPO-1 I and its compositional variants), All these materials have unidirectional I O-T-ring channel system as defined above. These catalysts have been found to be effective for the dimerization of isobutene. Although, the known sorption properties of these catalysts indicate that they would not promote the formation of highly branched products such as 2,4,4-trimethylpentene-1 and 2,4,4-trimethylpentene-2, upon the application of these catalysts high conversion and selectivity to the formation of the highly branched products were obtained. Without wishing to affect the novelty of the invention, it seems that the catalytic sites near the pore mouth and on the outside surface of the catalyst crystallites take part in the conversion of the present invention. When an organic base is used in the synthesis of the zeolite or zeo-type material it is customary that this is removed by calcination in air at a temperature of at 200-600°C, preferably at 300-550°C. When the zeolite or the zeo-type material is synthesized in the absence of organic base the calcination step may not be necessary. The H 2 O content "y" of the zeolite or the zeo-type material is the water of hydration and will depend, within the ratios set above, upon the conditions under which it is dried or calcined and the relative humidity. The H 2 O content "y" does not include water which may be notionally presents when the cation is hydrogen. The proton or H-form may be prepared by ammonium exchange followed by calcination as mentioned above or by ion exchange with a mineral acid or a combination thereof. The metal X in the metal oxide XO 2 of the zeolite is preferably Al, Ga, Zn, B, or a mixture thereof. The molar ratio of silica to metal X is preferably 10:1 to 200: 1. The molar ratio of the aluminium to phosphorous ratio (b:c) is preferably 0.8:1 to 1.3:1; whereas the molar silicon to aluminium ratio (a:b) is preferably 0.005:1 to 0.4:1. In addition, the aluminium in the composition may be replaced partly or wholly by Ga, B, Fe, or a mixture thereof. It is well known to those skilled in the art that the x-ray powder diffraction pattern, in terms of the relative intensities (I/I 0 x 100) or the interplanar spacing (d), may vary. The variation usually depends on many factors. Examples of these factors include the degree of hydration, the skeletal composition, the type of the cations present in the material, the presence of occluded organic or inorganic materials, the presence of preferred orientation, the aspect ratio of the crystallites or their average size and distribution, the experimental errors involved in the measurement, or the techniques used with regard to the arrangement of slit (i.e fixed slits vs. auto-divergent slits) in the measurement. Taking these variables into consideration and from studying the x-powder diffraction pattern as a whole, the structure-types of a given material can be identified. The zeolite material is suitably synthesized by mixing a source of silica, a source of metal X, a source of alkali metal(s), water and an organic or inorganic nitrogen containing base to form a homogeneously mixed gel and crystallizing the gel at a temperature above 70°C under the self generated pressure. In case of the zeo-type material, it is suitably synthesized by mixing a source of aluminium or its substituent, a source of phosphorous, a source of silica, water, and an organic nitrogen containing base to form a homogenously mixed gel and crystallizing the gel at a temperature above 70°C under the self generated pressure. The zeolite or the zeo-type materials of the present invention may be bound in a suitable binding material using methods and binding materials well known in the art. Examples of binders that may be suitably used include silica, alumina, aluminophosphates, clays such as kaolin and meta-kaolin, or a combination thereof. The bound catalyst may be subjected to further activation treatment which may be hydrothermally which includes steaming at elevated temperature, thermochemically which include heating the catalyst in a reducing or oxidative environment such as passing a flow of oxygen, air or hydrogen. The catalyst may be activated by carrying out any or more of the above treatments either consecutively or con-currently. These treatments may be carried out before the introduction of the hydrocarbon feed or/and periodically after catalytic cycles of times on stream with the hydrocarbon feed. The reactor may be a batch reactor or a flow reactor with a fixed bed catalyst. However other systems for example fluidized bed system may also be used. The dimerization reaction can be carried out by contacting the isobutene with the catalysts. Whereas the catalyst will be present in the solid phase the feedstock and the products may be present in the liquid or the gas phase depending on the structure and molecular weight of the individual compounds and the reaction conditions used. The applied temperature of the dimerization reaction and the temperature of the catalyst can vary depending on the catalyst used, the content of the feedstock, whether the feed contains a diluent, and the type of the reactor used. Typically a temperature range of 0°C and 300°C is suitable. A temperature range of 10°C to 150°C is most preferred. The applied pressure will depend on many factors such as the catalyst performance and the engineering aspect of the process e.g. liquid phase vs. gas phase and optimization of cost. The reactor pressure can be equal or higher than atmospheric pressure in order to optimize the yield and the selectivity of the desired products such as isooctenes (2,4,4 trimethylpentene-1 and 2,4,4 trimethylpentene-2). A pressure range of 203 kPa (15 psig) to 6997 kPa (1000 psig) is preferred and 307 kPa (30 psig) to 1479 kPa (200 psig) is most preferred. The weight hourly space velocity (WHSV) defines the rate of the introduction of the feed for a given catalyst charge and it has an influence on the performance of the catalyst and the productivity rate of the desired products. WHSV is defined as the weight of the reactants per hour fed per weight of the catalyst. Thus it has a unit of h -1 . In the present invention a WHSV of higher than 0.1h -1 may be employed. A WHSV range of 0.5h -1 to 100h -1 is preferred with 1.0h -1 to 30h -1 is most preferred. The desired products are highly branched olefins specifically octenes. These product may be hydrogenated to produce high octane alkylate for gasoline blending or aromatized into xylenes for the production of polyester. The present invention will be further demonstrated by specific examples. Example 0.80 grains of sodium hydroxide and 1.10 of sodium aluminate (ex. BDH and containing 40% by weight Al 2 O 3 and 28% by weight Na 2 O) were dissolved in 20 grams of distilled water. 50 grams of ammonia solution containing 25% by weight of NH 3 were added while stirring followed by 50 grams of ludox AS40 (colloidal silica containing 40% by weight silica). The ludox was added slowly over ten minutes period while stirring ensuring that the hydrogel formed is always homogeneous. The hydrogel was stirred for a further 10 minutes and then loaded into a 150 ml PTFE lined pressure vessel. The pressure vessels were rotated in an oven at 150°C for 36 hours. It is known to those are skilled in the art that zeolites are metastable and the optimum period of crystallization depend on factors affecting the effective rate of formation of the desired zeolite and may vary depending on for example the equipment used and the degree and type of stirring. After the crystallization period the solid was filtered, washed several times with distilled water, and dried at 90°C. The dried solid was examined by X-ray powder diffraction and found to be consistent with the TON-type structure with some cristoblite material present. The X-ray powder diffraction pattern is shown in Table 1. Chemical analysis showed that the powder had a Si/Al molar ratio of 34.7. Table 1 2-θ (degrees) d-spacing (Angstroms) Relatively Intensity 100 x I/I o 8.128 10.896 59.6 10.123 8.731 22.1 12.751 6.937 27.5 16.322 5.426 14.6 18.334 4.835 4.2 19.387 4.575 13.5 20.318 4.367 100.0 21.667 4.098 28.9 24.179 3.678 78.9 24.592 3.617 52.9 25.696 3.464 36.8 26.653 3.342 11.0 26.993 3.300 9.2 27.714 3.216 5.6 30.002 2.976 4.7 30.403 2.938 6.4 30.742 2.906 6.2 32.131 2.783 4.4 32.745 2.733 5.2 32.975 2.714 5.1 35.591 2.520 21.7 35.935 2.497 7.9 36.862 2.436 11.1 37.991 2.366 7.7 43.715 2.069 5.1 44.433 2.037 5.5 45.282 2.001 4.9 47.734 1.904 4.9 48.565 1.873 9.6 The zeolite powder was stirred in excess ammonium nitrate solution (concentration ∼ 1 mole/liter and using ∼ 50 ml of solution per gram of zeolite) for a few hours. The powder was filtered and a fresh ammonium nitrate solution was added and the treatment was repeated once more. The filtered zeolite was finally washed copiously with distilled water and dried at 90°C. The zeolite powder was packed into a 2.5 cm diameter die and pressed at a pressure of about 8 metric tons for 2 minute. The formed tablet was broken down into granules and sieved between 1 and 2 mm sieves. 30 cm 3 were packed into the middle of a tubular stainless steel reactor (1.0mm inner diamerer and 45 cm length) and sandwiched between two of at least 20 cm 3 of inert beads. The reactor had a coaxial tube (0.2 cm outer diameter) to enable the measuring of the catalyst bed temperature via an inserted thermocouple. The reactor was re-connected into the micro-reactor and a 50cm 3 /minute-air flow was passed over the catalyst and the temperature was raised to 550°C at the rate of 60°C/hour. The temperature was maintained for at least 8 hours and then reduced to the required reaction temperature. The catalyst was then flushed with a nitrogen flow to remove traces of air. Isobutene feed was introduced via a liquid pump from a reservoir maintained at room temperature and pressure of 1272 kPa (170 psig) to keep the isobutene in the liquid state. The results of the dimerization reaction are shown in Table 2. The products C 8 = were isomers of octenes with highly branched skeletons. The main portion of the isomers were 2,4,4-trimethyl-pentene-2, 2,4,4-trimethyl-pentene-1, 3,4,4-trimethyl-pentene-2, 2-methyl- heptene-3, 1-ethyl-1-methylcyclopentane, and 2,3,4-trimethyl-pentene-2. The products C 12 = also consisted of highly branched isomers. Table 2 Feed: Catalyst: WHSV: Isobutene SAB-9CNC - TON-type structure 5h -1 Hours on Stream Temperature °C Furnace/Catalyst Reactor Pressure psig Conversion Wt% Selectivities Wt% C1-C3 C8= C12= 1.0 150/195 Ambient 38.1 0.54 82.8 3.9 2.0 45/155 50-100* 98.4 nd 72.3 26.2 6.0 45/155 50-100* 83.7 nd 53.5 46.5 * pressure could not be maintained high enough in the absence of the initial nitrogen pressure due to fast condensation of the products.

Claims: A process for dimerization of isobutene by contacting a feed wherein the feed is isobutene with a catalyst system comprising at least: (a) tectometallosilicate zeolite with having TON-type structure, (b) tectometallosilicate zeolite with having MTT-type structure, (c) tectometallosilicate zeolite with the same structure as that of the ZSM-48 zeolite, or (d) silicoaluminophosphate (SAPO) zeo-type with AEL-type structure; under dimerization condition to produce highly branched olefins wherein the zeolite or the zeo-type material is wholly in the H-form, wherein the zeolite in its H-form has the following composition in terms of the mole ratios of the oxides: (0.9 ± 0.1)H (4.m) : XO 2 : xSIO 2 : yH 2 O wherein H is a proton, X is one or more of the metals selected from Al, Ga, Zn, Fe, Cr, and B, m is the valency of the metal X in the metal oxide XO 2 , x is at least 10, y/x is from 0 to 5, or in case of using zeo-type materials of AEL-type structure, the composition of the H-form is (O - a)H : (Si 2 Al b P c )O 2 : yH 2 O wherein H is a proton and a, b, and c represent the mole fraction of silicon, aluminium and phosphorus respectively present in tetrahedral oxides. A process according to claim 1 wherein the catalyst is subjected to an activation treatment thermochemically, which is heating in steam, in an inert atmosphere, oxidative or reductive environment prior to contact with the isobutene feed. A process according to any of the preceding claims wherein the dimerization reaction is carried out at temperature ranging from 0° to 300°C. A process according to claim 3 wherein the dimerization reaction is carried out at temperature ranging from 10°C to 150°C. A process according to any of the preceding claims wherein the dimerization reaction is carried out at pressure ranging from 203 kPa (15 psig) to 6997 kPa (1000 psig). A process according to claim 5 wherein the dimerization reaction is carried out at pressure ranging from 307 kPa (30 psig) to 1479 kPa (200 psig). A process according to any of the preceding claims wherein the dimerization reaction is carried out at WHSV of 0.5h -1 to 100h -1 . A process according to claim 7 wherein the dimerization reaction is carried out at WHSV of 1.0h -1 to 30h -1 . A process according to any of the preceding claims wherein the dimerization reaction is carried out in conjunction with an aromatization process of the highly branched products especially those products having 8 carbons.

Inventors: AL-SOUFI FAROUK, BARRI SAMI A I, BHAT YAJNAVALKYA S, HUSAIN ALTAF, AL-SOUFI, FAROUK, BARRI, SAMI A.I., BHAT, YAJNAVALKYA S., HUSAIN, ALTAF, Al-Soufi, Farouk Saudi Basic Industries Corp., Barri, Sami A.I., King Fahad University of P.& M., Bhat, Yajnavalkya S., Saudi Basic Industries Corp., Husain, Altaf, Saudi Basic Industries Corp.
Applicants: SAUDI BASIC IND CORP, SAUDI BASIC INDUSTRIES CORPORATION
Application year: 2000
Main classification: C07C2
IPC codes: C07C2, C07B61, B01J29, C10G50, B01J37, C07C11