Non-aqueous ball point pen ink and ball point pen using the ink

Abstract: A non-aqueous ball point pen ink and a ball point pen using this ink contains a colorant, an organic solvent, a non-Newtonian viscosity imparting agent, and 0.4 to 0.8 mass% in total of 0.2 to 0.6 mass% of polyvinyl pyrrolidone with a weight-average molecular weight of about 1,000,000 to 1,500,000 and 0.1 to 0.4 mass% of polyvinyl pyrrolidone with the weight-average molecular weight of about 2,500,000 to 3,000,000. Feathering and blobbing of the ink are eliminated, ink leakage is prevented, and satisfactory writing smoothness of the ball-point pen is obtained.

Description: The present invention relates to a non-aqueous ball point pen ink and a ball point pen using the ink. Specifically, the present invention relates to a non-aqueous ink provided with pseudoplasticity. The ink is so provided by blending a non-Newtonian viscosity imparting agent and is provided with viscoelasticity by blending with two types of polyvinyl pyrrolidone having different weight-average molecular weights to eliminate ink blobbing and scratching; and to a non-aqueous ball point pen using this ink. A conventional non-aqueous ball point pen has been designed by setting the ink viscosity in the range of 10,000 to 30,000 mPa s (20°C) to prevent leakage. However, when the viscosity during writing is high to this degree, the ball rotation resistance during writing automatically increases and writing smoothness is very low and fails to be satisfactory. Moreover, a high writing pressure is necessary during writing. In some cases, a load of 500 gf or more is applied to the pen point. The heavy load causes the pen point to be soon damaged. Furthermore, ball breakage and writing defects frequently occur in consequence. On the other hand, as disclosed in Japanese Laid-Open Patent Applications Nos. 6-313143 (1994), 6-313144 (1994), 7-196972 (1995) and 9-48941 (1997), attempts have been made to improve the above-described defects by creating inks having pseudoplasticity viscosity, where the ink viscosity is low when writing and where the ink viscosity is relatively high when writing is not being performed. However, these attempts were not sufficient to enhance writing smoothness nor to completely prevent leakage. The present invention provides an ink which achieves remarkably satisfactory writing smoothness, eliminates blobbing and feathering and which can completely prevent leakage, and further provides a non-aqueous ball point pen in which during ink flow when writing, no ink adheres to the ink reservoir tube inner wall and the residual amount of ink is clear. "Blobbing" is a phenomenon in which surplus ink during writing accumulates at the pen point. "Feathering" is blurring of the ink due to absorption by the paper or other substrate which is being written on. The present invention relates to a non-aqueous ball point pen ink which contains, as main components, a colorant, an organic solvent, a non-Newtonian viscosity imparting agent, and a total of 0.4 to 0.8 mass% of polyvinyl pyrrolidone, where 0.2 to 0.6 mass% of the polyvinyl pyrrolidone has a weight-average molecular weight of 1,000,000 to 1,500,000 and 0.1 to 0.4 mass% of the polyvinyl pyrrolidone has a weight-average molecular weight of 2,500,000 to 3,000,000. The non-Newtonian viscosity index of the ink may be in the range of 0.4 to 0.7, the viscosity at a shearing speed of 500 sec -1 is in the range of 3,000 to 6,000 mPa.s (20°C), and the viscosity at a shearing speed of 0.19 sec -1 may be in the range of 20,000 to 60,000 mPa·s (20°C). The non-Newtonian viscosity imparting agent may be a fatty acid amide wax which may have a melting temperature of 140°C or more. The blend amount of the fatty acid amide wax may be in the range of 1.0 to 2.0 mass%. The non-aqueous ink described above can be directly filled into an ink reservoir tube of a ball point pen. The ink reservoir tube can be a polypropylene tube. An inner wall of the ink reservoir tube can be treated with silicone. According to the present invention, there is provided an ink in which the ink viscosity at a shearing speed of 500 sec -1 can preferably be in the range of 3,000 to 6,000 mPa·s. When the ink viscosity is less than 3,000 mPa·s, writing smoothness is satisfactory but drawn line blobbing can be significant, also feathering can be unsatisfactory, even though it is still acceptable. Moreover, when the viscosity exceeds 6,000 mPa·s, low writing pressure and smooth stroke as objects of the present invention can scarcely be achieved, even though these properties are still acceptable. As a result of intensive studies on the writing stroke of a ball point pen, the present inventors found that the stroke largely depends on the ball rotation resistance during writing. As a result of experiments, when the ink viscosity at a shearing speed of 500 sec -1 is less than 1,000 mPa·s, the ball rotation resistance is found to be significantly reduced, but a boundary lubrication area is formed without forming an ink oil film between the ball and the ball seat and the intrinsic smoothness of the non-aqueous ball point pen is thereby reduced. Moreover, when the viscosity exceeds 10,000 mPa·s, the ball rotation resistance tends to increase and the stroke obviously tends to become heavy. Specifically, when the ink viscosity is in the range of 1,000 to 10,000 mPa-s, the stroke becomes satisfactory. However, to prevent feathering and blobbing, and to embody the intrinsic deep drawn line of the non-aqueous ball point pen, the ink viscosity should preferably be 3,000 mPa·s or more at least. Furthermore, not only to pursue smoothness of touch, but also to enable low pressure writing of about 100 gf like an aqueous ball point pen, the ink viscosity should preferably be 6,000 mPa·s or less. The ink viscosity referred to herein was measured in a measurement environment of 20°C using a CSL rheometer manufactured by British Carrymay, Ltd. Moreover, in the present invention, a non-Newtonian viscosity imparting agent is blended into the ink composition, and the ink non-Newtonian viscosity index is set to 0.4 to 0.7. As described above, to obtain a satisfactory stroke, the ink viscosity during writing, that is, during high shearing, is set to be low. The likelihood of occurrence of leakage necessarily increases, and this cannot be prevented by conventional ink design. To prevent this defect, pseudoplasticity is set as an ink viscosity property by including the non-Newtonian viscosity imparting agent in the ink composition, and the ink viscosity when the ball point pen is not being used is set to be as high as possible. Moreover, adequate consideration has been given also to drawn line blobbing in the study of ink viscosity, but it is also a fact that drawn line blobbing increases when the viscosity is set low. It should be mentioned that when the pseudoplasticity is set as an ink viscosity property, the cohesive force of the ink itself increases, the generation of surplus ink at the pen point is reduced and the effect of eliminating blobbing is brought about. When the non-Newtonian viscosity index is less than 0.4, the cohesive force of the ink itself increases excessively, an ink follow-up defect is caused, and also the phenomena of discontinuity, line cut and non-uniformity in line darkness ("scratching"). On the other hand, when the index exceeds 0.7, the cohesive force decreases and the effect of preventing blobbing is weakened. The non-Newtonian viscosity imparting agent for use in the non-aqueous ink includes a fatty acid amide wax and derivatives thereof, straight chain fatty acid ester polymers, polyethylene oxide, hardened castor oil, organic bentonite, silica and, sulfate-based anion activators, but a fatty acid amide wax is preferable from the point of view of stability. Further, considering stability during high-temperature storage of the ball point pen, it is most preferable to select a fatty acid amide wax with a melting temperature of 140°C or more as the non-Newtonian viscosity imparting agent. The amount of the fatty acid amide wax is in a range of 1.0 to 2.0 mass% in order to realize the non-Newtonian viscosity index of 0.4 to 0.7. The non-Newtonian viscosity index described herein was measured using a CSL rheometer manufactured by British Carrymay, Ltd. in a measurement environment of 20°C with appropriate values of angle and diameter of cone plate in the shearing speed range of 1 to 600 sec -1 . Furthermore, in the present invention, the viscosity at a shearing speed of 0.19 sec -1 was set to a range of 20,000 to 60,000 mPa·s. By providing the ink viscosity with pseudoplasticity, leakage could be minimized, but the ink viscosity during writing needs to be set to be low to obtain a satisfactory stroke, and it was therefore difficult to prevent completely the leakage of various ball point pen inks only by imparting pseudoplasticity. The inventors found that the viscosity at a shearing speed of 0.19 sec -1 needed to be 20,000 mPa·s or more to completely prevent leakage, even though a viscosity lower than that amount was still acceptable. Moreover, when the viscosity at a shearing speed of 0.19 sec -1 exceeds 60,000 mPa·s, the ink fluidity tends to be reduced, the ink follow-up during writing tends to be degraded, and the ink becomes inappropriate as a writing utensil ink. Examples of an ink viscosity adjuster include phenol resin, amide resin, xylene resin, hydro-rosin resin and ketone resin, and the adjuster is also effective as a fixer of a line drawn on a paper surface. The ink viscosity as described herein was also measured using a CSL rheometer manufactured by British Carrymay, Ltd. in a measurement environment of 20°C. The present invention realizes a remarkably smooth touch, embodies a non-aqueous ball point pen ink with which low pressure writing is possible similar to an aqueous ball point pen, and provides an ink capable of simultaneously preventing blobbing and leakage. Specifically, the ink viscosity at a shearing speed of 500 sec -1 is set to the range of 3,000 to 6,000 mPa·s (20°C) in order to obtain a satisfactory touch, and the ink viscosity is provided with pseudoplasticity in order to completely prevent feathering and blobbing which would normally tend to increase because of the low ink viscosity setting. Furthermore, in order to satisfy ink leakage preventing performance and ink follow-up which become insufficient when the ink is applied to various ball point pens, the viscosity at a shearing speed of 0.19 sec -1 is set to the range of 20,000 to 60,000 mPa·s (20°C). Furthermore, the inventors thoroughly analyzed the relation between scratching and blobbing to achieve a remarkably superior ball point pen performance. In the conventional non-aqueous ball point pen, a deep drawn line is obtained by interposing a pen point ball and transferring an ink film to the paper surface. In this case, as described above, the generation of surplus ink, that is, blobbing, is prevented by the favorable viscoelasticity of the ink itself. On the other hand, when the viscoelasticity is too strong, a defect in ink follow-up is caused as described above, and a smooth ink film cannot be formed on the pen point ball surface. This phenomenon is the scratching phenomenon. Specifically, blobbing performance is a phenomenon opposite to scratching, and it is very difficult to simultaneously avoid both phenomena. The inventors empirically found that this difficult problem could be solved by simultaneously using resins having different properties in the ink components. It is necessary to provide ink performance with viscoelasticity and select a resin which does not degrade ink stability, and polyvinyl pyrrolidone is an optimum in this respect. Although the resins need to be different in properties as described above, there is a danger that completely different types of resins may react together in the ink. In this respect, for polyvinyl pyrrolidone, various grades which are different in molecular weights are well known and polyvinyl pyrrolidone can safely be employed in the ink. When polyvinyl pyrrolidone with a weight-average molecular weight of 1,000,000 to 1,500,000 is added, the viscoelastic action is slightly deficient, but a smooth ink film can easily be formed on the pen point ball surface, and a stable drawn line can be achieved. Moreover, polyvinyl pyrrolidone with a weight-average molecular weight of 2,500,000 to 3,000,000 provides a remarkably high viscoelasticity, and is effective for preventing blobbing. By simultaneously using polyvinyl pyrrolidone compounds having different properties, both blobbing and the scratching phenomena, which are opposite to each other, are reduced. The effect of polyvinyl pyrrolidone as an additive for providing ink with viscoelasticity has been reported, but the action of effectively facilitating the forming of the ink film with respect to the pen point ball has not previously been known. The total addition amount of polyvinyl pyrrolidone needs to be in the range of 0.4 to 0.8 mass% with respect to the total ink composition. When the amount is less than 0.4 mass%, the ink can be deficient in its viscoelasticity and the reduction of blobbing can hardly be sufficient. Moreover, when the amount exceeds 0.8 mass%, the viscoelasticity can be too strong, and scratching can result. For the blend ratio of polyvinyl pyrrolidone, an empirically obtained combination of 0.2 to 0.6 mass% of polyvinyl pyrrolidone with a weight-average molecular weight of 1,000,000 to 1,500,000 and 0.1 to 0.4 mass% of polyvinyl pyrrolidone with a weight-average molecular weight of 2,500,000 to 3,000,000 is most effective. When the blend amount of polyvinyl pyrrolidone with a weight-average molecular weight of 1,000,000 to 1,500,000 is less than 0.2 mass%, or when the blend amount of polyvinyl pyrrolidone with a weight-average molecular weight of 2,500,000 to 3,000,000 is less than 0.1 mass%, the ink is deficient in its viscoelasticity and anti-blobbing performance cannot be enhanced. Moreover, when the blend amount of polyvinyl pyrrolidone with a weight-average molecular weight of 1,000,000 to 1,500,000 exceeds 0.6 mass%, or when the blend amount of polyvinyl pyrrolidone with a weight-average molecular weight of 2,500,000 to 3,000,000 exceeds 0.4 mass%, the viscoelasticity is too strong, and scratching results. The total blend amount of polyvinyl pyrrolidone needs to be in the range of 0.4 to 0.8 mass% with respect to the total ink composition. With an amount of less than 0.4 mass%, even when polyvinyl pyrrolidone with a weight-average molecular weight of 2,500,000 to 3,000,000 is used, the ink can be deficient in its viscoelasticity and the anti-blobbing performance cannot be enhanced. As a polyvinyl pyrrolidone with a weight-average molecular weight of 1,000,000 to 1,500,000, PVP K-90 (manufactured by GAF, Ltd., weight-average molecular weight of 1,280,000) is exemplified, and as a polyvinyl pyrrolidone with a weight-average molecular weight of 2,500,000 to 3,000,000, PVP K-120 (manufactured by GAF, Ltd., weight-average molecular weight of 2,800,000) is exemplified. A colorant as an essential component of the present invention can be used without being particularly limited to the dyes or pigments heretofore employed in non-aqueous ball point pens. Examples of pigments include organic, inorganic and processed pigments, such as carbon black, phthalocyanine, azo, quinacridone, anthraquinone, and indigo pigments. Moreover, as a dye, an alcohol-soluble dye, oil-soluble dye, direct dye, acid dye, basic dye, metallized dye, and various salt-forming type dyes can be employed. Moreover, these can be used alone or as a mixture. The blend proportion is preferably in the range of 5 to 50 mass% with respect to the total ink composition. The organic solvent for use in the present invention is used as an ink composition solvent, or dispersing medium. Specifically, alcohol and glycol solvents such as benzyl alcohol, propylene glycol and butylene glycol, Cellosolve solvents such as phenyl Cellosolve, Carbitol solvents such as phenyl Carbitol, and nitrogen-containing solvents such as N-methyl pyrrolidone can be used alone or as a mixture. The blend proportion is preferably in the range of 30 to 70 mass% with respect to the total ink composition. Now, a ball point pen structure will be described. For an ink reservoir tube for a non-aqueous ball point pen, usable materials are limited from the standpoints of e.g. chemical resistance, moisture permeability, and air permeability. In these respects, it has heretofore been most usual to use polypropylene as the material. However, in the present invention, particularly when a fatty acid amide wax is selected as the non-Newtonian viscosity imparting agent, the fatty acid amide wax has a very strong affinity for polypropylene. Therefore, when the ink is transferred from the ink reservoir tube, a defect occurs in that the ink adheres to the inner wall and the residual amount of the ink fails to be clear. As a countermeasure against this defect, the present inventors have found that when the ink reservoir tube is formed of polypropylene, the ink reservoir tube inner wall should be treated with silicone. When silicone is applied to the ink reservoir tube inner wall, polypropylene as the reservoir tube material does not directly contact the ink and maintains the relation that silicone is interposed, so that during flow of the ink, the prevention of adherence to the reservoir tube inner wall is embodied. As a silicone material, TSF-4420 (Toshiba Silicone Co., Ltd.) is exemplified. It is a most effective application method to simultaneously and uniformly apply silicone to the inner wall during extrusion molding. When a tube of polyethylene terephthalate or nylon is used as the ink reservoir tube, the application of silicone is not necessarily required. Examples Specific examples will next be described. Example 1 NIGROSINE EX 15.0 mass% VALIFAST VIOLET 1701 15.0 mass% phenyl glycol 52.1 mass% benzyl alcohol 13.0 mass% fatty acid amide wax 2.5 mass% polyvinyl pyrrolidone K-90 0.2 mass% polyvinyl pyrrolidone K-120 0.2 mass% viscosity adjustment resin 2.0 mass% By mixing, then heating at 60°C and stirring the above-described components, dissolving dyes and resin, and uniformly dispersing the fatty acid amide wax in the ink, a black non-aqueous ball point pen ink was obtained. NIGROSINE EX, and VALIFAST VIOLET 1701 (both are dyes manufactured by Orient Kagaku Kogyo K.K.) were used as the dyes to adjust the color to black. For the fatty acid amide wax, as the non-Newtonian viscosity imparting agent, TAREN 7200 (manufactured by Kyoeisha Kagaku K.K.) was employed. As a viscosity adjuster and a drawn line adjuster, polyvinyl pyrrolidone K-90 (manufactured by GAF Co., Ltd., weight-average molecular weight of 1,280,000), and polyvinyl pyrrolidone K-120 (manufactured by GAF Co., Ltd., weight-average molecular weight of 2,800,000) were employed. As the viscosity adjustment resin, HIRACK 110H (manufactured by Hitachi Chemical Co., Ltd., ketone resin) was employed. Then, by directly inserting the black non-aqueous ball point pen ink obtained into a polypropylene reservoir tube with the inner wall treated by silicone (TSF-4420 manufactured by Toshiba Silicone Co., Ltd.), and mounting the ink reservoir tube in a shaft cylinder, a non-aqueous ball point pen was formed. Examples 2 to 11 The non-aqueous ball point pen was formed as in Example 1 except that the ink composition shown in Table 1 was used. Comparative Examples 1 to 19 The non-aqueous ball point pen was formed as in Example 1 except that the ink compositions shown in Tables 2 and 3 were used. N.B. Polyvinyl pyrrolidone K-30 manufactured by GAF Co. Ltd. with a weight-average molecular weight of 55,000 was used. Test and Evaluation With respect to the respective non-aqueous ball point pens of the Examples 1 to 11 and Comparative Examples 1 to 19, the following tests and evaluations were performed. 1. Writing smoothness: Evaluation by manual writing Low pressure writing is possible to such an extent that writing is possible with a ball point pen weight, smooth and particularly satisfactory o ○ Satisfactory ○ Slightly inferior Δ Low pressure writing is impossible, and no smooth touch × 2. Drawn line scratching: Evaluation by manual writing Not generated and remarkably satisfactory o ○ Unnoticeable degree in practical use ○ Slightly noticeable Δ Very noticeable × 3. Drawn line blobbing: By setting the writing load to 200 gf and a writing angle to 65°, and using the writing tester for spiral writing at a writing speed of 4 m/min., the state after the writing of 100 m was confirmed. No blobbing in drawn line, no drop (ink rising) in pen point o ○ Less than one blob in drawn line, drop very slightly generated ○ One to five blobs in drawn line, drop slightly generated Δ Five or more blobs in drawn line, drop remarkably generated × 4. Feathering: After writing characters on a writing sheet A in an environment of 30°C and 60%RH and leaving the written sheet surface to stand in the similar environment for 24 hours, the feathering was checked. No feathering in drawn line o ○ Almost no feathering ○ Slight feathering Δ Significant feathering × 5. Leakage: After leaving the ball point pen to stand vertically in an environment of 40°C and 95%RH with a chip facing downward for 24 hours, the leakage from the pen point was checked. No leakage from pen point confirmed o ○ Almost no leakage from pen point confirmed ○ No ink rising confirmed up to 1/4 of chip taper part Δ Ink rising by 1/4 of chip taper part or more × The evaluation results of the respective Examples and Comparative Examples are shown in Tables 1, 2 and 3. Comparative example 14 15 16 17 18 19 Ink blend nigrosine EX 15.0 15.0 15.0 15.0 15.0 15.0 Valifast violet 1701 15.0 15.0 15.0 15.0 15.0 15.0 phenyl glycol 51.9 49.3 49.2 49.7 49.2 50.3 benzyl alcohol 13.0 12.3 12.3 12.4 12.3 15.1 fatty acid amide wax 2.0 2.5 2.5 2.5 2.5 1.8 polyvinyl pyrrolidone K-30 0.5 0.5 - - 1.0 - polyvinyl pyrrolidone K-90 0.6 - 1.0 - - 0.6 polyvinyl pyrrolidone K-120 - 0.4 - 0.4 - 0.2 viscosity adjustment resin 2.0 5.0 5.0 5.0 5.0 2.0 Ink physical properties Non-Newtonian viscosity index 0.64 0.48 0.48 0.46 0.47 0.52 Ink viscosity (at. 20°C, 500 sec -1 ) 5000 4400 4400 3800 3000 5000 Ink viscosity (at. 20°C, 0.19 sec -1 ) 40000 52500 52500 51000 48000 65000 Ball point pen performance Smoothness o ○ × o ○ × × × Scratching × × × × × × Blobbing × o ○ × o ○ × × Leakage o ○ × o ○ o ○ o ○ o ○ As not described in Tables 1, 2 and 3, for the ball point pens of the respective Examples and Comparative Examples, the ink flows from the ink reservoir tube with ink consumption by the respective tests. In this case, since no ink adhered to the ink reservoir tube inner wall, it was possible to clearly confirm the residual amount of ink. Comparative Example 1 is an example in which the addition amount of polyvinyl pyrrolidone K-90 is small. In an attempt to eliminate drawn line blobbing, a slight excess of polyvinyl pyrrolidone K-120 was added, writing smoothness became heavy, and additionally scratchiness was generated in the drawn line. When the combination of polyvinyl pyrrolidone is used as in Comparative Example 1, a satisfactory ink film is not generated at the pen point ball during writing, the ball rotates, writing smoothness is degraded, and scratching results in the drawn line. Comparative Example 2 is an example opposite to Comparative Example 1, in which the addition amount of polyvinyl pyrrolidone K-90 is large. In this case, it was obvious from Comparative Example 1 that writing smoothness was degraded and scratching resulted unless the amount of polyvinyl pyrrolidone K-120 was reduced, and therefore the addition amount of polyvinyl pyrrolidone K-120 was minimized. However, writing smoothness failed to be satisfactory and scratching could not be improved. Additionally, even blobbing, which was satisfactory in Comparative Example 1, was generated. Comparative Example 3 is an example in which the addition amount of polyvinyl pyrrolidone K-90 is slightly smaller than that of Comparative Example 2, and the addition amount of polyvinyl pyrrolidone K-120 is set to be even lower. Scratching was successfully eliminated, but writing smoothness and reduction of blobbing could not be enhanced. Comparative Examples 4 and 5 are examples in which the addition amount of polyvinyl pyrrolidone K-120 is too large. In this case, even when the ink component is adjusted, writing smoothness cannot be enhanced, and scratching cannot be improved. This is because the ink viscoelasticity is excessively strong. When the ink viscoelasticity is too strong, the anti-blobbing performance is enhanced, but a smooth and stable ink film cannot be obtained with respect to ball rotation during writing, an unnecessary ball rotation resistance is thus generated and the touch is not enhanced. Moreover, since a smooth ink transfer cannot be performed onto the paper surface during ball rotation, scratching results in the drawn line. Comparative Example 6 is an example in which the total addition amount of polyvinyl pyrrolidone is basically too small. Ink viscoelasticity is naturally weakened and fierce blobbing occurs during writing. Moreover, since a smooth and stable ink film cannot be obtained with respect to the ball during writing, the stroke is not enhanced, and a stable drawn line cannot be obtained. In Comparative Example 7, an attempt was made to adjust the combination by adding a large amount of polyvinyl pyrrolidone K-90 and a slightly smaller amount of polyvinyl pyrrolidone K-120, but writing smoothness was not enhanced, scratching was not prevented, and reduction of blobbing could not be improved. A result similar to that of Comparative Examples 2 or 3 was obtained. Comparative Example 8 is an example opposite to Comparative Example 6, in which the total addition amount of polyvinyl pyrrolidone is too large. Of course, since the ink viscoelasticity is increased, no drawn line blobbing is generated. However, excessively strong ink viscoelasticity is a natural result, the stroke is degraded, and significant scratching is generated. Comparative Example 9 is an example in which the non-Newtonian viscosity index is too small. The ink transfer to the paper surface via the ball rotation needs to be embodied in order to obtain a deep drawn line typical of a non-aqueous ball point pen, and the ink viscosity at a shearing speed of 500 sec -1 (at 20°C) needs to be 3,000 mPa·s at minimum as described hereinbefore. In the present invention, on the assumption that a deep drawn line is to be obtained, the ink viscosity at a shearing speed of 500 sec -1 (at 20°C) is set to 3,000 mPa·s. Even with this ink viscosity, however, when the non-Newtonian viscosity index is 0.3, a smooth ink film cannot be obtained in the vicinity of the pen point ball during writing and satisfactory writing performance cannot be realized. Comparative Example 10 is an example in which the non-Newtonian viscosity index is too large. The ink viscosity at a shearing speed of 0.19 sec -1 (at 20°C) was first set in order to prevent leakage as a major defect for the ball point pen. When the non-Newtonian viscosity index is set to be as large as 0.8 as in Comparative Example 10, the ink viscosity at a shearing speed of 0.19 sec -1 (at 20°C) needs to be 20,000 mPa·s at minimum in order to prevent leakage. The ink viscosity at an ink shearing speed of 500 sec -1 (at 20°C) was measured at 8,000 mPa·s. As described hereinbefore, the stroke was not enhanced, and scratching resulted. Moreover, the excessive non-Newtonian viscosity index means a deficiency of the ink in its viscoelasticity and results in the generation of drawn line blobbing. Comparative Example 11 is an example in which the ink viscosity at a shearing speed of 500 sec -1 (at 20°C) is too low. The deep drawn line and stroke typical of a non-aqueous ball point pen cannot be obtained. Moreover, since the ink viscosity is reduced more than necessary by pen point ball rotation during writing, drawn line blobbing and scratching occur as a result. Comparative Example 12 is an example in which the ink viscosity at a shearing speed of 500 sec -1 (at 20°C) is too high. The viscosity is not high as compared with conventional non-aqueous ball point pens and can be regarded as rather low, but the ink of the present invention is a pseudoplastic ink and the viscoelasticity of the ink itself is strong. Additionally, in the present invention, polyvinyl pyrrolidone is adjusted, that is, the ink viscoelasticity is controlled to simultaneously solve both the scratching and the blobbing problems. Therefore, the ink viscosity at a shearing speed of 500 sec -1 (at 20°C) is a factor which directly exerts an influence on writing performance. When the viscosity exceeds 6,000 mPa·s, ink smoothness is distroyed and writing performance is not enhanced. Comparative Example 13 is an example in which the ink viscosity at a shearing speed of 0.19 sec -1 (at 20°C) is low. An experiment was performed by setting the ink viscosity at a shearing speed of 500 sec -1 (at 20°C) to 3,000 mPa·s in order to obtain the deep drawn line of a non-aqueous ball point pen and confirming the occurrence of leakage, and it has been found that when the viscosity is below 2,000 mPa·s, leakage cannot be prevented. Moreover, the ink of Comparative Example 13 is weak in its own viscoelasticity and a satisfactory drawn line cannot be obtained. Comparative Examples 14 to 18 are examples in which the combination of polyvinyl pyrrolidone is changed. Comparative Example 14 is an example in which K-30 with a weight-average molecular weight of 55,000 was employed instead of polyvinyl pyrrolidone K-120. Comparative Example 15 is an example in which K-30 was employed instead of polyvinyl pyrrolidone K-90. Comparative Example 16 is an example in which adjustment was attempted only with K-90 without employing polyvinyl pyrrolidone K-120. Comparative Example 17 is an example in which the adjustment was attempted only with K-120 without employing polyvinyl pyrrolidone K-90. Comparative Example 18 is an example in which the adjustment was attempted only with K-30 without employing polyvinyl pyrrolidone K-120 or K-90. The viscoelasticity of these inks could not be adjusted and scratching and blobbing could not simultaneously be prevented. Comparative Example 19 is an example in which the ink viscosity at a shearing speed of 0.19 sec -1 (at 20°C) is too high. In this case, leakage can be prevented, but smooth ink fluidity is not obtained at the pen point, and satisfactory writing performance could not be realized. The non-aqueous ball point pen ink and the ink-containing non-aqueous ball point pen of the present invention are characterized in that writing smoothness is remarkably satisfactory, neither blobbing nor feathering is found, and leakage can be completely prevented. Moreover, a fatty acid amide wax is particularly selected as the non-Newtonian viscosity imparting agent, and for the ink reservoir tube of polypropylene, the ink reservoir tube inner wall surface can be treated with silicone, so that no ink adheres to the inner wall surface and therefore the remaining amount of ink can advantageously be confirmed clearly.

Claims: A non-aqueous ball point pen ink comprising: a colorant; an organic solvent; a non-Newtonian viscosity imparting agent; and a total of 0.4 to 0.8 mass% of polyvinyl pyrrolidone, including a total of 0.2 to 0.6 mass% of a first polyvinyl pyrrolidone with a weight-average molecular weight of 1,000,000 to 1,500,000 and 0.1 to 0.4 mass% of a second polyvinyl pyrrolidone with a weight-average molecular weight of 2,500,000 to 3,000,000. The non-aqueous ball point pen ink according to claim 1 wherein the non-Newtonian viscosity index of said ink is in the range of 0.4 to 0.7, the viscosity of said ink at a shearing speed of 500 sec -1 is in the range of 3,000 to 6,000 mPa·s at 20°C, and the viscosity of said ink at a shearing speed of 0.19 sec -1 is in the range of 20,000 to 60,000 mPa·s at 20°C. The non-aqueous ball point pen ink according to claim 1 or claim 2 wherein the non-Newtonian viscosity imparting agent is a fatty acid amide wax with a melting temperature of 140°C or more. The non-aqueous ball point pen ink according to any one of the preceding claims wherein the blend amount of the fatty acid amide wax as the non-Newtonian viscosity imparting agent is in the range of 1.0 to 2.0 mass%. A ball point pen formed by directly inserting the non-aqueous ball point pen ink according to any one of the preceding claims into an ink reservoir tube whose inner wall is treated with silicone. The ball point pen according to claim 5 wherein the ink reservoir tube is a polypropylene tube with silicone applied to an inner face.

Inventors: FUJII TAKESHI, FUKASAWA TERUAKI, FUNABASHI KAHORI, FUJII, TAKESHI, FUKASAWA, TERUAKI, FUNABASHI, KAHORI, Fujii, Takeshi, c/o Kabushiki Kaisha Pilot, Fukasawa, Teruaki, c/o Kabushiki Kaisha Pilot, Funabashi, Kahori, c/o Kabushiki Kaisha Pilot
Applicants: PILOT KK, KABUSHIKI KAISHA PILOT
Application year: 2000
Main classification: C09D11
IPC codes: C09D11