LIQUID CRYSTAL COMPOUNDS

Abstract: A compound of formula (I), wherein G<1> and G<2> independently represent a polymerisable mesogenic residue X represents a group selected from the group consisting -CH2-, -O-, -CO-, -COO-, -OOC-, -CONR'-, -OCOO- and -OCONR'; Sp represents a group of the formula -(CH2)p- in which p is an integer of 1 to 18 and in which one or two non adjacent -CH2- groups are optionally replaced by -CH=CH-; or in which one or two -CH2- groups may be replaced by one or two groups selected from the group consisting -CH2-, -O-, -CO-, -COO-, -OOC-, -CONR'-, -OCOO- and -OCONR'- with the proviso that firstly the spacer group does not contain two adjacent heteroatoms and secondly when X is -CH2-, p can also have a value of 0; Q represents a a polar group selected from -CN, -COR, -COOR, -OCOR, -CONR'R, -NR'COR, -OCOOR, -OCONR'R, -NR'COOR, F, Cl, -CF3, -OCF3 or -OR or a cyclic group which is unsubstituted or optionally substituted by a group selected from a lower alkyl, lower alkenyl, lower alkoxy, lower alkenyloxy, halogen, -CN, -COR'', -COOR'', -OCOR'', -CONR'R'', -NR'COR'', -OCOOR'', -OCONR'R'', -NR'COOR'', -CF3, and -OCF3; where R represents hydrogen, a lower alkyl, a lower alkenyl or a cyclic group as defined above; and R' is hydrogen, a lower alkyl or a lower alkenyl group; R'' represents a lower alkyl or a lower alkenyl group and liquid crystal mixtures containing the compounds.

Description: Liquid Crystal Compounds The present invention relates to laterally substituted curable Liquid Crystals (LCPs) having mesogenic properties or properties which cause these LCPs to be compatible with a mesogenic molecular architecture. In particular the present invention relates to laterally substituted curable Liquid Crystals (LCPs) having a low melting point and good alignment properties and the use of such LCPs in the preparation of substantially uniform or patterned films in which the orientation of the LCP molecules in the plane and relative to the plane ofthe substrate can be controlled. Films prepared from curable Liquid Crystals (LCP films) are well known to a skilled person and are used in the preparation of optical and electro-optical devices. These films are generally manufactured by using coating techniques such as spin coating. This involves casting an organic solution of a cross-linkable LCP or LCP mixture onto a substrate provided with an orientation layer. The organic solvent is subsequently removed to give a well orientated, solvent free mesogenic LCP layer. This mesogenic LCP layer may be cross-linked to give a LCP film. The thickness ofthe LCP film depends upon the viscosity and therefore the concentration of the organic solution of the polymerisable LCP mixture used in the coating process. The uniformity of the film formed depends upon the ability of the LCPs to form homogeneous layers free of tilt domains as well as the stability of the LCP mixture during the coating and cross- linking processes. By the term "tilt domains" it should be understood to mean regions within the LCP film in which the long axis of the LCP molecules form tilt angles with the substrate plane which are ofthe same size, but have opposite directions. A problem with known LCPs, especially those having high clearing and melting points, is that they are not able to form mixtures that remain stable during both the coating and cross-linking processes. These prior art LCP mixtures tend to be characterised by a poor solubility in organic solvents; a tendency for the components of the mixture to separate from one another; and a tendency to crystallise. Although attempts have been made to solve these problems by, for example, preparing LCPs with lower melting points, the ability of these prior art LCPs to align with the tilt direction imposed on the film tends to be poor. Such poorly aligned films tend to be characterised by a low contrast ratio. A further problem associated with existing LCP materials is the formation of tilt domains and disclinations during the preparation of LCP films. By the term disclination it should be understood to mean borderlines of neighbouring tilt domains where LCP molecules of opposite tilt angles are adjacent. These tilt domains and disclinations result in both a disturbance in the uniform appearance of the film and an inhomogeneous optical performance. The aforementioned problems are of particular relevance if photooriented and photopatterned orientation layers are used for the orientation of LCPs. This so called linear photopolymerisation (LPP) technology (Nature, 381 , p. 212 (1996) allows the production of not only uniform but also structured (photopatterned) orientation layers. If such structured orientation layers are used for the orientation of LCPs, the LCP molecules should adapt the information given by the orientation layer with respect to the direction of alignment and the tilt angle in each single pixel individually. There is, therefore, a need for a new LCP material that may be used in the preparation of LCP mixtures and layers, which significantly reduces the aforementioned disadvantages and which is especially suitable when applied to LPP orientation layers. The present invention addresses that need. A first aspect ofthe invention provides a compound of formula (I) wherein G ! and G 2 independently represent a polymerisable mesogenic residue; X represents a group selected from -CH 2 -, -0-, -CO-, -COO-, -OOC-, -CONR'-, -OCOO-, -OCONR'; Sp represents a group of the formula -(CH 2 ) p - in which p is an integer of 1 to 18 and in which one or two non adjacent -CH 2 - groups are optionally replaced by -CH=CH-; or in which one or two -CH 2 - groups are optionally replaced by one or two groups selected from the group consisting -O-, -CO-, -COO-, -OOC-, -CONR'-. -OCOO-, -OCONR'- with the proviso that firstly the spacer group does not contain two adjacent heteroatoms and secondly when X is -CH 2 -, p can also have a value of 0; Q represents a a polar group selected from -CN, -COR, -COOR, -OCOR. -CONR'R, -NR'COR, -OCOOR, -OCONR'R, -NR'COOR. F, Cl, -CF 3 , - OCF 3 or -OR or a cyclic group which is unsubstituted or optionally substituted by a group selected from a lower alkyl. lower alkenyl. lower alkoxy, lower alkenyloxy, halogen, -CN, -COR", -COOR", -OCOR". -CONR'R", -NR'COR", -OCOOR", -OCONR'R". -NR'COOR", -CF 3 , and where R represents hydrogen, a lower alkyl, a lower alkenyl or a cyclic group as defined above; and R' is hydrogen, a lower alkyl or a lower alkenyl group R" represents a lower alkyl or a lower alkenyl group. The compounds of the invention have been found to have lower melting points compared to the compounds of the prior art. They have also been found to be more miscible with other components ofthe liquid crystal mixtures of which they form a part. have a reduced tendency to crystallise from and little effect on the clearing points of such mixtures. In addition they exhibit improved alignment abilities compared to the compounds of the prior art. Laterally substituted mesogenic compounds are known from WO 95/24454, WO 95/24455, US 5,650,534, US 5,593,617, US 5,567,347 and US 5,707.544. However, many of these compounds are not suitable for preparing LCP films and networks that are substantially free of tilt domains. Others exhibit high melting points, higher viscosities (US 5,567,347), lower clearing points (US 5,593,617), poor solubility and/or poor orientation properties. It has been found that by using the compounds of the present invention it is possible to control the orientation or alignment of LCPs or LCP mixtures in the plane of the substrate, to form a tilt angle relative to the plane and to suppress the formation of tilt domains in the mesogenic layers and films formed. The compounds of the invention may therefore be used in the preparation of high contrast optical or electro-optical devices. The compounds of the invention have also been found to be highly miscible with other LCP compounds over a broad range of concentrations. These compounds and mixtures containing them are extremely soluble in organic solvents. These properties mean that it is possible to prepare coating solutions having a concentration and viscosity that can be controlled over a wide range. Consequently, the thickness of the LCP layers formed using these coating solutions can be readily controlled. The compounds of the invention are further characterised by relatively low melting points and clearing points that are generally above room temperature. Therefore, during the formation of LCP films or networks using the compounds of the invention or mixtures thereof, spontaneous crystallisation does not tend to occur. This property (otherwise known as supercooling) greatly facilitates the formation of LCP films and networks free of defects. This further means that it is also possible to reduce the number of liquid crystal components used in the manufacture of LCP mixture. The polymerisable mesogenic residues G ! and G 2 may be the same or different, but are preferably the same. The group X is preferably selected from -CH 2 -, -0-, -COO- and -OOC-. The spacer group Sp may be optionally substituted by one or more fluorine atoms. Groups in which there are no substituent groups present are preferred. It is especially preferred that the integer p has a value of from 1 to 1 1 and that no more than one -CH 2 - group is replaced by -CH=CH-, -0-, CO-, -COO-, -OOC-, -CONR'-, -OCOO-, -OCONR'. The group Q is preferably selected from -CN, -COOR, -OCOR. Cl, -CF 3 , -OCF 3 and -OR in which R is defined as above. The cyclic group may be a saturated or unsaturated, isocyclic or heterocyclic five or six membered cyclic group. The cyclic group may be unsubstituted or may contain one or two substituents independently selected from the group consisting a lower alkyl, lower alkenyl. lower alkoxy, lower alkenyloxy, halogen, -CN, -COR", -COOR", -OCOR", -CONR'R", -NR'COR", -OCOOR", -OCONR'R", -NR'COOR", -CF 3 , -OCF 3 and -OR" in which R' is as defined above and R" represents a lower alkyl or a lower alkenyl group. Preferred halogen substituents for the cyclic group include F and Cl. Preferred five membered cyclic groups included in the group Q are selected from the group consisting of optionally substituted furanyl, tetrahydrofuranyl, dioxolanyl. oxazolyl, 3,4-dihydrooxazolyl and cyclopentyl. Especially preferred five membered cyclic groups include 2-furanyl, 2-tetrahydrofuranyl, 2-dioxolanyl and 3 ,4-dihydo-2-oxazoly 1. Preferred six membered cyclic groups included in the group Q are selected from the group consisting of an optionally substituted phenyl, pyridinyl, pyrimidinyl, cyclohexyl, cyclohexenyl, tetrahydropyranyl, 1,3-dioxanyl. Especially preferred six membered groups include phenyl, cyclohexyl, l,3-dioxan-2-yl and 2-tetrahydropyranyl. It is preferred that the five or six membered cyclic groups are unsubstituted or contain no more than one substituent group. If a substituent group is present, it is preferably selected from the group consisting of a lower alkyl, lower alkoxy, F, Cl, -CN, -COOR", -OCOR", -OCF 3 , OR", in which R" is lower alkyl. By the term "lower alkyl" it should be understood to include a Cι -0 achiral, branched or straight-chained alkyl group. Examples of lower alkyl groups that may be present in the compounds of the invention include methyl, ethyl, propyl, butyl, pentyl hexyl and the like. By the term "lower alkenyl" it should be understood to include C 3 _ achiral, branched or straight-chained alkenyl group in which the double bond is at position 2- or higher. Examples of lower alkenyl groups that may be present in the compounds of the invention include 2-propylene, 3-butylene, 3-isopentylene, 4-pentylene and the like. By the term "lower alkoxy" it should be understood to include Cι -6 achiral, branched or straight-chained alkoxy group. Examples of lower alkoxy groups that may be present in the compounds of the invention include methoxy. ethoxy. propoxy. butoxy, pentoxy, hexoxy and the like. 1 7 Preferably the polymerisable mesogenic residues G and G are each independently represented by the group of formula II II wherein A and B are independently selected from the group consisting of 1 ,4-phenylene, pyridine-2,5-diyl, pyrimidine-2,5-diyl, trans- 1,4-cyclohexylene and trans-l,3-dioxane-l,4-diyl; optionally substituted with a halogen, -CN, a lower alkyl, lower alkenyl, lower alkoxy or lower alkenyloxy group; nis 1 or 0, Z 1 and Z 2 are independently selected from the group consisting a single bond, -COO-, -OOC-, -CH 2 -CH , -CH 2 0-, -OCH 2 -, -CH=CH-, -C≡C-, -(CH 2 ) 4 -, or -(CH 2 ) 3 0- ; Z represents a group of formula -(CH 2 ) p X- in which p is an integer having a value of 1 to 18 and X is defined above, and in which one or two non adjacent -CH 2 - groups may be optionally replaced by -CH=CH- or in which one or two -CH 2 - groups may be replaced by one or two additional linking groups X with the proviso that firstly the group Z does not contain two adjacent heteroatoms and secondly when X is -CH 2 , p can also have a value of 0 R 1 represents a polymerisable group selected from the group consisting of CH 2 =C(Ph)-, CH 2 =CW-COO-, CH 2 =CH-COO-Ph-, CH 2 =CW-CO-NH-, CH 2 =CH-0-, CH 2 =CH-OOC-, Ph-CH=CH-, CH 2 =CH-Ph-, CH 2 =CH-Ph-0-, R 3 -Ph-CH=CH-COO-, R 3 -OOC-CH=CH-Ph-0- and 2-W-epoxyethyl in which W represents H, Cl, Ph or a lower alkyl, R 3 represents a lower alkyl with the proviso that when R 3 is attached to a phenylene group (-Ph-) it may also represent hydrogen or a lower alkoxy. The terms "Ph" and "Ph- "' will be understood to indicate a phenyl group, and "-Ph-" any isomer of phenylene, namely 1 ,2- phenylene. 1.3- phenylene or 1 ,4-phenylene, except where the context requires otherwise. The groups A and B may be optionally substituted with a halogen, -CN. a lower alkyl, lower alkenyl, lower alkoxy or lower alkenyloxy group. If a halogen substituent is present this is preferably F or Cl. It is preferred that the groups A and B are selected from optionally substituted 1 ,4-phenylene and 1,4-cyclohexylene rings. It is especially preferred that the groups A and B are unsubstituted. By the term "alkenyloxy" it should be understood to include C 3- 6 achiral, branched or straight-chained alkenyloxy group in which the double bond is at position 2- or higher. Examples of lower alkenyloxy groups that may be present in the compounds of the invention include 2-propenyloxy, 3-butenyloxy, 4-pentenyloxy, 5- hexenyloxy and the like. It is preferred that the groups Z 1 and Z 7 are selected from the group consisting a single bond, -COO-, -OOC-, -CH 2 -CH 2 -, -CH 2 0-, -OCH 2 -, -CH=CH- and -C≡C-. It is especially preferred that Z 1 and Z 2 represent a single bond, -C≡C-, -COO- or -OOC-. Z 3 may be optionally substituted by one or more halogen atoms, preferably one or more fluorine atoms. It is preferred that p has a value of 1 to 11. It is also preferred that Z J contains no substitution. It is further preferred that, for the group Z , X is selected from -CH 2 -, -0-, -COO- and -OOC-, especially -CH 2 - or -0-. It is preferred that the group R is selected from the group consisting CH 2 =CW-. CH 2 =CW-COO- and CH 2 =CH-0-. It is preferred that the sum of the two integers n for each of the groups G 1 and G 2 is 0 or 1. It is especially preferred that for both G 1 and G 2 n has a value of 0. The compounds of the invention may be readily prepared using procedures well known to a skilled person accordance with any one of the procedures set out in Schemes 1 to 6 below. Scheme 1 DBU / Acetonitril / Rfl. in which : DBU is L8-diazabicyclo[5.4.0]undec-7-ene EDC is N-(3-dimethylaminopropyl)-N'-ethylcarbodiimide hydrochloride DMAP is 4-dimethylaminopyridine Scheme 2 Pyridine in which : DBU is l ,8-diazabicyclo[5.4.0]undec-7-ene KI is potassium iodide EDC is N-(3-dimethylaminopropyl)-N'-ethylcarbodiimide hydrochloride DMAP is 4-dimethylaminopyridine Scheme 3 in which : DEAD is diethyl azodicarboxylate KI is potassium iodide DBU is 1.8-diazabicyclo[5.4.0]undec-7-ene EDC is N-(3-dimethylaminopropyl)-N'-ethylcarbodiimide hydrochloride DMAP is 4-dimethylaminopyridine Scheme 4 in which: TBPB is tetrabutylphosphonium bromide HBr is 48-% hydrobromic acid AcOH is acetic acid DBU is l,8-diazabicyclo[5.4.0]undec-7-ene EDC is N-(3-dimethylaminopropyl)-N'-ethylcarbodiimide hydrochloride DMAP is 4-dimethylaminopyridine Scheme 5 in which : NMP is l,3-dimethyl-2-imidazolidinone EDC is N-(3-dimethylaminopropyl)-N'-ethylcarbodiimide hydrochloride DMAP is 4-dimethylaminopyridine Scheme 6 Suitable starting materials used in the preparation of the compounds of the present invention include, amongst others, phenyl and biphenyl carboxylic acid compounds as well as 1 ,4-cyclohexanedione. The compounds of the invention are preferably prepared by forming a ring that includes a lateral group prior to linking the mesogenic residues. Alternatively, the compounds may be prepared by forming a ring that includes a polymerisable mesogenic residue prior to linking the lateral group. A second aspect of the invention therefore provides a method of preparation of a compound of formula (I), the method comprising forming a ring that includes a lateral group and subsequently linking the mesogenic residue thereto. The mesogenic residues G 1 and G 2 are preferably attached simultaneously. As indicated above, it is especially preferred that the mesogenic residues G 1 and G 9 are identical. It will be appreciated that the compounds of the invention may be used in the preparation of liquid crystalline mixtures. Such mixtures may be prepared by admixing a compound of formula (II) with one or more additional components. An organic solvent may also be used in the preparation of these mixtures. A third aspect of the invention therefore provides a liquid crystalline mixture comprising a compound of formula (I) and one or more additional components. The one or more additional components present in the liquid crystalline mixture may be further compounds of formula (I), other mesogenic compounds, compounds that are compatible with a mesogenic molecular architecture or chiral dopants for the introduction of helical pitch. The LCP mixture may also include a suitable organic solvent. Examples of solvents that may be used in the preparation of such liquid crystalline mixtures include anisole, caprolactone, cyclohexanone, methyl ethyl ketone, methyl propyl ketone and the like. Examples of additional components that may be used in the preparation of liquid crystalline LCP mixtures according to the third aspect of the invention include those compounds represented by formulae III to X. 4 — (CH in which R 4 is selected from the group consisting CH 2 =CH-0-, CH 2 =CH-COO- CH 2 =C(CH 3 )-COO-, CH 2 =C(Cl)-COO- and H 2 C-CH- \ / O S -.3 ' , c S4 independently represent -(CH 2 )„- or -0(CH 2 )„-; E', E 2 are independently selected from the group consisting 1 ,4-phenylene trans- 1 ,4-cyclohexylene, pyridine-2,5-diyl, pyrimidine-2,5-diyl and trans 1 ,4-cyclohexy lene- 1 ,4-phenylene; F , F are independently selected from the group consisting 1 ,4-phenylene, and 2- or 3-fluoro-l,4-phenylene; L , L^, L are independently selected from the group consisting OH, C|-C 2 o-alkyl, Cι-C 20 -alkenyl, C]-C 2 o-alkoxy, Cι-C 2 o-alkoxy-carbonyl, formyl, C|-C 2 o-alkylcarbonyl, Cι-C 2 o-alkylcarbonyloxy, halogen, cyano and nitro; Z 6 is selected from the group consisting -COO-, -OOC-, -OCH 2 -, -CH 2 0-, - 0(CH 2 ) 3 -, -OOC(CH 2 ) 2 - and -COO(CH 2 ) 3 -; Z 7 is selected from the group consisting a single bond, -CH 2 CH 2 -, -CH 2 O-, - OCH 2 -, -COO-, -OOC-, -(CH 2 ) 4 -, -0(CH 2 ) 3 -, (CH 2 ) 3 0- and -C≡C-; Z 8 is selected from the group consisting a single bond, -CH 2 CH 2 -, -CH 2 0-, - OCH 2 -, -COO-, -OOC-, and -C≡C-; Y is independently selected from the group consisting hydroxy, C C 20 -alkyl, Cι-C 20 -alkenyl, Cι-C 2 o-alkoxy, C C 2 o-alkoxy carbonyl, formyl-, Cι-C 2 o-alkylcarbonyl, Cι-C 20 -alkylcarbonyloxy, fluoro, chloro, bromo, cyano and nitro; m is an integer having a value of from 2 to 20; and v is an integer having a value of from 2 to 12 The compounds of the invention may also be used in the formation of a LCP layer by casting a LCP compound according to the first aspect of the invention or a mixture according to the third aspect of the invention onto a substrate. A fourth aspect of the invention therefore provides a method forming a LCP network comprising forming a LCP layer including a compound of formula (I) and cross-linking the layer. Liquid crystalline mixtures according to the third aspect of the invention may also be used in the manufacture of LCP networks in a similar way. The invention also includes, in a fifth aspect of the invention, a cross-linked LCP network comprising a compound of formula (I) in a cross-linked form. Cross-linked LCP networks comprising a mixture according to the third aspect of the invention in cross-linked form may also be included in this aspect of the invention. A sixth aspect of the invention provides the use of a compound of formula (I) in the preparation of an optical or an electro-optical device. The use, in the preparation of an optical or electro-optical device, of liquid crystalline mixtures according to the third aspect ofthe invention is also included in this aspect ofthe invention. An seventh aspect of the invention provides an optical or an electro-optical device comprising a compound of formula (I) in a cross-linked state. An optical or electro-optical device comprising a LCP liquid crystalline mixture in a cross-linked state according to the third aspect of the invention is also included in this aspect of the invention. The invention will now be described with reference to the following non- limiting examples. These examples are provided by way of illustration only. Variations on these examples falling within the scope of the invention will be apparent to a skilled person. Examples Example 1 Synthesis of 3-cyanopropyl 2,5-dihvdroxybenzoate A mixture of 2,5-dihydroxybenzoic acid (4.6g; 30mmol), l,8-diazabicyclo[5.4.0] undec-7-ene (5.0g; 33mmol), 4-bromobutyronitrile (4.9g; 33mmol) and acetonitrile (70ml) was heated under reflux overnight. The reaction mixture was added to water (500ml) and extracted with ethyl acetate (3 x 100ml). The combined organic layers were washed with lN-hydrochloric acid (150ml) and water (2 x 150ml), dried over magnesium sulphate and filtered. The organic solvent was then removed in vacua. The residue (6.2g) was recrystallised from ethyl acetate/hexane to yield 5.2g (78%) of the desired 3-cyanopropyl 2,5-dihydroxybenzoate. Synthesis of 2.5-bis-[4-(6-acryloyloxy-hexyloxy)benzoyloxylbenzoic acid 3-cvanopropyl ester A solution of N-(3-dimethylaminopropyl)-N'-ethylcarbodiimide hydrochloride (6.5g; 39.9mmol) in dichloromethane (100ml) was added slowly to a solution of 3-cyanopropyl 2,5-dihydroxybenzoate (9.9g; 33.9mmol), 4-(6-acryloy4hexyloxy)- benzoic acid (5.7; 19.5mmol) and 4-dimethylaminopyridine (0.8g; 6.7mmol) in dichloromethane (60ml) at 0°C. The mixture was stirred at room temperature overnight. It was then added to water (300ml) and extracted with dichloromethane (3 x 100ml). The combined organic layers were washed with water (2 x 130ml), dried over magnesium sulphate and filtered. The organic solvent was then removed in vacuo. The residue (14.0g) was purified by column flash chromatography on silica gel using toluene/ethyl acetate (85:15) as eluent, to yield 6.3g (60.6%) of 2,5-bis-[4-(6-acryloyl- oxy)hexyloxybenzoyloxy]benzoic acid 3-cyanopropyl ester. Mp = 42°C; Clp (N-I) = 63.7°C. This compound may be supercooled. The following compounds were prepared in a similar way. 2.5-bis-|4-(6-acryloyloxyhexyloxy)benzoyloxylbenzoic acid 2-cyanoethyl ester Mp = 46.5°C; Clp (N-I) = 61 °C The compound may be supercooled. 2,5-bis-f4-(6-(2-methacryloyloxy)hexyloxy)benzoyloxyj benzoic acid 3-cyanopropyl ester Mp = 10°C; Clp (N-I) = 41.4°C 2,5-bis-|4-(6-acryloyloxyhexyloxy)benzoyloxyjbenzoic acid 4-cyanobutyl ester Mp = 79°C; Clp (N-I) = 56°C 2,5-bis-[4-(6-acryloyloxyhexyloxy)benzoyloxy| benzoic acid 5-cyanopentyl ester Mp = 85°C; Clp (N-I) = 63.1°C 2,5-bis-[4-(6-acryIoyloxyhexyloxy)benzoyloxyl benzoic acid 6-cyanohexyl ester Mp = 57°C; Clp (N-I) = 58.2°C The compound may be supercooled. 2.5-bis-[4-(5-acryloyloxypentyloxy)benzoy.oxy] benzoic acid 3-cyanopropyl ester Mp = 97°C; Clp (N-I) = 72.2°C The compound may be supercooled. 2.5-bis-[4-(8-acryIoyloxyoctyloxy)benzoyloxy] benzoic acid 3-cyanopropyl ester Mp = 63.5°C; Clp; (N-I) = 66°C The compound may be supercooled. 2,5-bis-[4-(6-acryloyloxyhexy.oxy)benzoyIoxy]benzoic acid 4-methoxybutyl ester Clp (N-I) = 59°C The compound may be supercooled. [[3-(ethoxycarbonyl)propoxy|carbonyl]-p-phenylene bis[p-[6-(acryloyloxy)hexyl oxy]benzoate [f(6-chlorohexyl)oxy]carbonyl]-p-phenylene bis[p-[6-(acryloyloxy)hexyloxyj benzoate] Mp = 44°C; Clp (N-I) = 62.6°C [(4-phenoxybutoxy)carbonyl|-p-phenylene bis[p-[6-(acryloyloxy)hexyloxy|- benzoate] f(4,4.4-trifluorobutoxy)carbonyll-p-phenylene bis[p-(6-(acryloyloxy)hexyloxyl- benzoatel Mp = 69.7°C; Clp (N-I) = 55.1°C The compound may be supercooled. [trans-4-butylcvclohexyl)methoxycarbonyl|-p-phenvIene bis[p-([6-(acryloyloxy) hexylloxyl-benzoate Mp = 66°C; Clp (N-I) = 59.8°C. The compound may be supercooled Example 2 Synthesis of 8-chlorooctyl 2-furancarboxylate A solution of 2-furoyl chloride (6.5g; 50mmol) was added dropwise at 0°C to a solution of 8-chloro-l-octanol (6.6g; 40mmol) and pyridine (20g; 253mmol) and stirred at room temperature for 2h. The resulting mixture was added to a mixture of lN-hydrochloric acid and ice (200ml) and extracted with ethyl acetate (3 x 80ml). The combined organic layers were washed with saturated sodium chloride solution (2 x 80ml), dried over magnesium sulphate and filtered. The organic solvent was removed in vacuo to give 8-chlorooctyl-2-furancarboxylate (9.7g) (94%) as an oil. Synthesis of octamethylene 2,5-dihydroxybenzoate 2-furoate A mixture of 2,5-dihydroxybenzoic acid (5.8 g; 37mmol), l,8-diazabicyclo[5.4.0] undec-7-ene (5.7g; 37mmol), 8-chlorooctyl-2-furancarboxylate (9.7g; 37mmol). potassium iodide (7.8g; 47mmol) and acetonitrile (150ml) was heated, under reflux for 44h. The cooled reaction mixture was added to water (600ml) and extracted with ethyl acetate (3 x 150ml). The combined organic layers were washed with lN-hydrochloric acid (150ml) and water (2 x 150ml), dried over magnesium sulphate and filtered. The solvent was then removed in vacuo. Recrystallisation of the residue (12.3g) from ethyl acetate/hexane gave 9.5g (68%) of octamethylene-2,5-dihydroxybenzoate-2-furoate. Synthesis of furan-2-carboxylic acid 8-{2,5-bis-f4-(6-acryloyloxyhexyloxy) benzoyloxy]benzoyloxy}octyl ester A solution of N-(3-Dimethylaminopropyl)-N'-ethylcarbodiimide hydrochloride (8.9 g: 46.5mmol) in dichloromethane (140ml) was slowly added to a solution of octamethylene-2.5-dihydroxybenzoate-2-furoate (7.0g; 18.6mmol), 4-(6-acryloyl hexyloxy)benzoic acid (13.6g; 46.5mmol) and 4-dimethylaminopyridine (1.1 g: 9.3mmol) in dichloromethane (130ml) at 0°C. The mixture was stirred overnight at room temperature. The resulting solution was then added to water (600ml) and extracted with dichloromethane (3 x 250ml). The combined organic layers were washed with water (2 x 200ml), dried over magnesium sulphate and filtered. The solvent was removed in vacuo. The residue (21. Og) was purified by column flash chromatography on silica gel using toluene/ethyl acetate (93:7) as eluent, to give 8.3g (48,2%) of furan-2-carboxylic acid 8-{2,5-bis-[4-(6-acryloyloxyhexyloxy)benzoyloxy]- benzoyloxy}octyl ester Mp = 36°C; Clp (N-I) = 41.2°C. The compound may be supercooled. The following compounds were prepared in a similar manner. (RS)-tetrahydrofuran-2-carboxylic acid 8-{2,5-bis-[4-(6-acryloyloxyhexyloxy) benzoyloxy|benzoyloxy}octyI ester Clp (N-I) = 27°C Furan-2-carboxylic acid ll-{2,5-bis-[4-(6-acryloyloxyhexyloxy)benzoyloxy| benzoyloxyjundecyl ester Mp = 43.9°C; Clp (N-I) = 45.8°C The compound may be supercooled. Furan-2-carboxylic acid 4-{2,5-bis-[4-(6-acryloy.oxyhexyloxy)benzoyloxy] benzoyloxy} butyl ester Clp (N-I) = 40.7°C The compound may be supercooled. Example 3 Synthesis of p-[(8-chIorooctyl)oxy]benzonitrile A solution of diethyl azodicarboxylate (7.3 g; 42mmol) and tetrahydrofuran (15ml) was added dropwise at 0°C to a solution of 4-hydroxybenzonitrile (4.2g; 35mmol), 8-chloro-l-octanol (6.9g; 42mmol), triphenylphosphine (11. Og; 42mmol) and tetrahydrofuran (70ml) and stirred at room temperature overnight. The reaction mixture was added to water (200ml) and extracted with ethyl acetate (3 x 100ml), dried over magnesium sulphate and filtered. The solvent was then removed in vacuo. The residue was purified by column flash chromatography on silica gel using toluene/ethyl acetate (97:3) as eluent, to give 8.8g (94%) of p-[(8-chlorooctyl)oxy] benzonitrile. Synthesis of 8-(p-cyanophenoxy)octyl 2,5-dihydroxybenzoate A mixture of 2,5-dihydroxybenzoic acid (4.2g; 27.5mmol), 1.8-diazabicyclo[5.4.0] undec-7-ene (4.2g; 27.5mmol), potassium iodide (41. Og; 247mmol), p-[(8-chlorooctyl)oxy]benzonitrile (6.6g; 25mmol) and acetonitrile (100ml) was heated under reflux for 72h. The reaction mixture was cooled, poured into water (500ml) and extracted with ethyl acetate (3 x 150ml). The combined organic layers were washed with lN-hydrochloric acid (150ml) and water (2 x 150ml), dried over magnesium sulphate and filtered. The solvent was removed in vacuo. The residue was purified by column flash chromatography on silica gel using a toluene/ethyl acetate 80:20 as eluent to give 8.0g (84%>) of 8-(p-cyanophenoxy)octyl 2,5-dihydroxybenzoate. Synthesis of 2,5-bis-[4-(6-acryloyloxyhexyloxy)benzoyloxy] benzoic acid 8-(4-cyano- phenoxy)octyl ester A solution of N-(3-dimethylaminopropyl)-N'-ethylcarbodiimide hydrochloride (3.7g; 19.5mmol) in dichloromethane (60ml) was added slowly to a solution of 8-(p-cyanophenoxy)octyl-2,5-dihydroxybenzoate (3g; 7.8mmol), 4-(acryloylhexyloxy)- benzoic acid (5.7g; 19.5mmol) and 4-dimethylaminopyridine (0.5g; 3.9mmol) in dichloromethane (80ml) at 0°C. The mixture was stirred overnight at room temperature. The resulting mixture was added to water (350ml) and extracted with dichloromethane (3 x 100ml). The combined organic layers were washed with water (2 x 100ml), dried over magnesium sulphate and filtered. The organic solvent was removed in vacuo. The residue (9.0g) was purified by flash chromatography using a silica gel column and toluene/ethyl acetate (98:2) as eluent, to give 4.6g (63%) of 2,5-bis-[4-(6-acryloyloxyhexyloxy)benzoyloxy]benzoic acid 8-(4-cyanophenoxy)octyl ester. Mp = 54.5°C; Clp (N-I) = 78.4°C; (S A -N) = 43.5°C. The compound may be supercooled. Example 4 Synthesis of 4-hydroxy-4'-methoxy-3-biphenylcarboxylic acid Palladium(II)acetate (55mg; 0.23mmol) was added under argon to a mixture of 5-bromosalicylic acid (5.4g; 22.4mmol), sodium carbonate (7.2g; 68.1 mmol) and 4-methoxyboronic acid (3.8g; 25mmol) in water (125ml). The reaction mixture was stirred at room temperature for lh. The resulting slurry was dissolved in hot water (1300ml) and filtered to give a filtrate and a precipitate. The filtrate was acidified with hydrochloric acid. The precipitate was washed with water and dried in vacuo to give 5.3g (95%) of 4-hydroxy-4'-methoxy-3-biphenylcarboxylic acid. Synthesis of 4,4'-dihydroxy-3-biphenylcarboxyIic acid A solution of 4-hydroxy-4'-methoxy-3-biphenylcarboxylic acid (5.3g; 21.6mmol), tetrabutylphosphonium bromide (0.8g; 2.3mmol), acetic acid (35ml) and hydrobromic acid (35ml of a 48% solution) was heated at reflux for 6h. The reaction mixture was cooled and poured into water (400ml). The resulting precipitate was isolated and recrystallised from ethyl acetate to give 2.4g (47%) of 4,4'-dihydroxy-3-biphenyl- carboxylic acid. Synthesis of 3-cyanopropyl-4,4'-dihydroxy-3-biphenylcarboxylate A mixture of 4,4'-dihydroxy-3-biphenylcarboxylic acid (2.3g: lOmmol). 1 ,8-diaza- bicyclo[5.4.0]undec-7-ene (1.7g; 1 1.2mmol), 4-bromobutyronitrile (1.7g: 1 1.2mmol) and N,N-dimethylformamide (40ml) was heated at 75°C for 4h. The reaction mixture was cooled, poured into water (300ml) and extracted with ethyl acetate (3 x 100ml). The combined organic layers were washed with lN-hydrochloric acid (150ml) and with water (2 x 100ml), dried over magnesium sulphate and filtered. The organic solvent was removed in vacuo. The residue (3.0g) was purified by flash chromatography using a silica gel column and toluene/ethyl acetate (97:3) as eluent to give 2.1g (70%) of 3-cyanopropyl-4,4'-dihydroxy-3-biphenylcarboxylate. Synthesis of 3-|(3-cyanopropoxy)carbonyl]-4,4'-biphenylene bis[p-[6- (acryloyloxy)hexyloxy]benzoate] A solution of N-(3-dimethylaminopropyl)-N'-ethylcarbodiimide hydrochloride (2.9g; 15.4mmol) in dichloromethane (50ml) was slowly added to a solution of 3-cyanopropyl- 4,4'-dihydroxy-3-biphenylcarboxylate (2.1g; 7.1 mmol), 4-(6-acryloylhexyloxy)benzoic acid (4.5g; 15.4mmol) and 4-dimethylaminopyridine (0.5g; 3.9mmol) in dichloromethane (80ml) at 0°C. The mixture was stirred at room temperature overnight. The resulting mixture was added to water (300ml) and extracted with dichloromethane (3 x 100ml). The combined organic layers were washed with water (2 x 100ml), dried over magnesium sulphate and filtered. The organic solvent was removed in vacuo. The residue (6.3g) was purified by flash chromatography using a silica gel column and toluene/ethyl acetate (90:10) as eluent, to yield 1.3g (20%) of 3-[(3- cyanopropoxy)carbonyl]-4,4'-biphenylene bis[p-[6-(acryloyloxy)hexyloxy]benzoate]. Mp = 85.5°C; Clp (N-I) = 154.5°C. The compound may be supercooled. The following compound was prepared in a similar way: 3-[(3-cyanopropoxy)carbonyl]-4-(trans-4-cyclohexyl)-phenyl bis[p-([6- (acryloyloxy)hexyl]oxy)-benzoate] Mp = 98°C; Clp (N-I) = 140°C. Example 5 Synthesis of 2-furfurylhydroquinone A mixture of 1 ,4-cyclohexanedione (5.6g; 50mmol), furan-2-carbaldehyde (4.8g; 50mmol) and anhydrous lithium chloride (2.1g; 50mmol) in l ,3-dimethyl-2-imidazolidinone (20ml) was heated with stirring over an a oil bath at atmospheric pressure. The temperature of the bath was maintained at 165°C for lh. The cooled reaction mixture was poured into water (300ml) and extracted with ethyl acetate (2 x 150ml). The combined organic layers were washed with water (2 x 100ml), dried over magnesium sulphate and filtered. The organic solvent was removed in vacuo. The residue (9.4g) was purified by flash chromatography using a silica gel column and toluene/ethyl acetate (90:10) as eluent, to give 6.7g (70%) of 3-furfurylhydroquinone. Synthesis of 4-(6-acryloyloxyhexyloxy)benzoic acid 4-|4-(6-acryloyloxyhexyloxy)benzoyloxy|3-furan-2-yImethylphenyl ester A solution of N-(3-dimethylaminopropyl)-N'-ethylcarbodiimide hydrochloride (8.8g; 46mmol) in dichloromethane (160ml) was added slowly to a solution of 2-furfurylhydroquinone (3.5g; 18.4mmol), 4-(6-acryloylhexyloxy)benzoic acid (13.4g; 46mmol) and 4-dimethylaminopyridine (0.5g; 3.9mmol) in dichloromethane (50ml) at 0°C. The reaction mixture was stirred at room temperature overnight, added to water (350ml) and extracted with dichloromethane (3 x 100ml). The combined organic layers were washed with water (2 x 100ml) dried over magnesium sulphate and filtered. The organic solvent was removed in vacuo. The residue (18.6g) was purified by flash chromatography using a silica gel column and toluene/ethyl acetate (95:5) as eluent and recrystallised from ethyl acetate/hexane to give 6.4g (47%) of 4-(6-acryloyloxyhexyloxy)benzoic acid 4-[4-(6-acryloyloxyhexyloxy,Lbenzoyloxy]- 3-furan-2-yl methylphenyl ester. Mp = 65°C Clp (N-I) = 51°C. The compound may be supercooled. Example 6 Synthesis of [[(3-cyanopropoxy)carbonyl|-p-phenylene]bisfoxymethylene-p- phenyleneoxyhexamethylene] diacrylate A solution of diethyl azodicarboxylate (4.2g; 24mmol) and tetrahydrofuran (20ml) was added dropwise at 0°C, to a solution of triphenylphosphine (6.4g; 24mmol) into tetrahydrofuran (40ml), the salt mixture was stirred for 2h at 0°C. After the salt mixture was added slowly at 0°C to a solution of 6-[(α-hydroxy-p-tolyl)oxy]hexyl acrylate (3.1g; lOmmol), 3-cyanopropyl-2,5-dihydroxybenzoate (2.2; lOmmol) and tetrahydrofuran (60ml), stirred at room temperature overnight. The reaction mixture was added to water (400ml) and extracted with ethyl acetate (3 x 200ml). The combined organic layers were washed with water (2 x 200ml), dried over magnesium sulphate, filtered and then evaporated down under reduced pressure. The residue (lό.Og) was purified by column flash chromatography on silica gel using a 95:5 toluene / ethyl acetate mixture as eluent. to yield 2. 3g (31%) of the desired ether. The following compound may be synthesised using a similar method: [[(3-cyanopropoxy)carbonyl]-p-phenylene]bis[oxymethyIene(trans-l,4-cyclo- hexylene)oxyhexamethylene] diacrylate Example 7 Preparation of nematic LCP Films (i) A mixture ofthe following components in anisole was prepared: 70wt% of lOOOppm of a Tinuvin 123 stabiliser and 500ppm of a 2,6-di-(t-butyl)-4-hydroxytoluene (BHT) inhibitor were added to this mixture. 500ppm of an Irgacure 369 polymerisation initiator (commercially available from Ciba Geigy, Basle, Switzerland) was added. The mixture was stirred at room temperature and then spincoated on a glass plate having an orientation layer to form an LCP film of approximately 800nm in thickness. This film was dried at 50°C for 1 or 2 minutes and photopolymerised by irradiation with UV light for approximately 5 minutes at room temperature in a N 2 atmosphere using a mercury lamp. The film exhibits a nematic mesophase at room temperature. In addition this film exhibits a tilt angle of about 10° relative to the plane of the substrate, as shown by ellipsometric measurements. The non-polymerised film exhibits an excellent super cooling behaviour. (ii) A mixture of the following components in anisole was prepared according to procedure (i) above. 60wt% of 20wt% of and 10 wt% of 1 ,4-butanediol diacrylate (Aldrich) The nematic film formed exhibits a well oriented nematic mesophase at room temperature with a clearing point of 80°C. In addition this film exhibits a tilt angle of about 1 ° relative to the plane ofthe substrate, as shown by ellipsometric measurements.

Claims: Claims 1. A compound of formula (I) wherein G 1 and G 2 independently represent a polymerisable mesogenic residue X represents a group selected from the group consisting -CH 2 -, -O-, -CO-, -COO-, -OOC-, -CONR'-, -OCOO- and -OCONR'; Sp represents a group of the formula -(CH 2 ) p - in which p is an integer of 1 to 18 and in which one or two non adjacent -CH 2 - groups are optionally replaced by -CH=CH-; or in which one or two -CH 2 - groups may be replaced by one or two groups selected from the group consisting -CH 2 -, -0-, -CO-, -COO-, -OOC-, -CONR'-, -OCOO- and -OCONR'- with the proviso that firstly the spacer group does not contain two adjacent heteroatoms and secondly when X is -CH 2 -, p can also have a value of 0; Q represents a a polar group selected from -CN, -COR, -COOR, -OCOR, -CONR'R, -NR'COR, -OCOOR, -OCONR'R, -NR'COOR, F, Cl, -CF 3 , - OCF 3 or -OR or a cyclic group which is unsubstituted or optionally substituted by a group selected from a lower alkyl, lower alkenyl, lower alkoxy, lower alkenyloxy, halogen, -CN, -COR", -COOR", -OCOR", -CONR'R", -NR'COR", -OCOOR", -OCONR'R", -NR'COOR", -CF 3 , and -OCF 3 ; where R represents hydrogen, a lower alkyl, a lower alkenyl or a cyclic group as defined above; and R' is hydrogen, a lower alkyl or a lower alkenyl group K" represents a lower alkyl or a lower alkenyl group. 2. A compound according to Claim 1 , in which G 1 and G 2 are the same. 3. A compound according to Claim 1 or Claim 2, in which X is selected from -CH 2 -. - 0-, -COO- and -OOC-. 4. A compound according to any one of claims 1 to 3. in which the integer p of the Sp group has a value of from 1 to 1 1. 5. A compound according to any one of the preceding claims, in which no more than one -CH 2 - moiety of the Sp group is replaced by -CH=CH-, -0-, CO-, -COO-. -OOC-. -CONR'-, -OCOO-, -OCONR'. 6. A compound according to any one of the preceding claims, in which Q is selected from -CN. -COOR. -OCOR, Cl, -CF 3 . -OCF 3 . -OR or a cyclic group. 7. A compound according to any one of the preceding claims, in which the c\ chc group is selected from a five or six membered saturated or unsaturated. isocyclic oi heterocyclic moiety. 8. A compound according to any one of the preceding claims in which the cyclic group is optionally substituted by a group selected from a lower alkyl, lower alkoxy, F, Cl. -CN, -COOR", -OCOR", -OCF 3 , OR", in which R" is lower alkyl 9. A compound according to any one of the preceding claims in which the mesogenic residues G 1 and G 2 are of formula II wherein A and B independently represent 1 ,4-phenylene, pyridine-2.5-diyl, pyrimidine- 2,5-diyl, trans- 1 ,4-cyclohexylene or trans-1.3-dioxane-l ,4-diyl: optionally substituted with a halogen, -CN, a lower alkyl, lower alke 1. lower alkoxy or lower alk lylo* ^ group; n is 1 or 0, . Z 1 and Z 2 independently represent a single bond, -COO-, -OOC-, -CH 2 -CH 2 -, -CH 2 0-, -OCH 2 -, -CH=CH-, -C≡C-, -(CH 2 ) 4 -, or -(CH 2 ) 3 O-; Z represents a group of formula -(CH 2 ) p X- in which one or two non adjacent -CH - groups may be optionally replaced by -CH=CH- or in which one or two -CH 2 - groups may be replaced by one or two groups selected from the group consisting -CH 2 -, -0-, CO-, -COO-, -OOC-, -CONR'-, -OCOO- and -OCONR' with the proviso that firstly the spacer group does not contain two adjacent heteroatoms and secondly when X is -CH 2 -, p can also have a value of 0; wherein p is an integer having a value of 1 to 12; and X is selected from the group consisting -CH 2 -, -0-, CO-, -COO-, -OOC-, -CONR'-, -OCOO- and -OCONR'; R 1 represents a polymerisable group selected from CH 2 =C(Ph)-, CH 2 =CW-COO-, CH 2 =CH-COO-Ph-, CH 2 =CW-CO-NH-, CH 2 =CH-O-, CH 2 =CH-OOC-, Ph-CH=CH-, CH 2 =CH-Ph-, CH 2 =CH-Ph-O-, R 3 -Ph-CH=CH-COO-, R 3 -OOC-CH=CH-Ph-O- or 2-W-epoxyethyl in which W represents H, Cl, Ph or a lower alkyl, R 3 represents a lower alkyl or with the proviso that when R 3 is attached to a 1 ,4-phenylene group (-Ph-) it may also represent hydrogen or a lower alkoxy. 10. A compound according to Claim 9, in which Z 1 and Z 2 are selected from a single bond, -COO-, -OOC-, -CH 2 -CH 2 -, -CH 2 0-, -OCH 2 -, -CH=CH- and -C≡C-. 11. A compound according to Claim 9 or Claim 10, in which Rl is selected from CH 2 =CW-, CH 2 =CW-COO- and CH 2 =CH-O-. 12. A LCP mixture comprising a compound of formula (I) wherein G 1 and G independently represent a polymerisable mesogenic residue X is selected from the group consisting of -CH 2 -, -0-, -CO-, -COO-, -OOC-, -CONR'-, -OCOO- and -OCONR'; Sp represents a group of the formula -(CH 2 ) p - in which p is an integer of 1 to 18 and in which one or two non adjacent -CH 2 - groups are optionally replaced by -CH=CH-; or in which one or two -CH 2 - groups may be replaced by one or two groups selected from -CH 2 -, -0-, CO-, -COO-, -OOC-, -CONR'-, -OCOO-, -OCONR' with the proviso that firstly the spacer group does not contain two adjacent heteroatoms and secondly when X is -CH 2 -, p can also have a value of 0; Q represents a a polar group selected from -CN, -COR, -COOR, -OCOR, -CONR'R, -NR'COR, -OCOOR, -OCONR'R, -NR'COOR, F, Cl, -CF 3 , - OCF 3 or -OR or a cyclic group which is unsubstituted or optionally substituted by a group selected from a lower alkyl, lower alkenyl, lower alkoxy, lower alkenyloxy, halogen, -CN, -COR", -COOR", -OCOR", -CONR'R", -NR'COR", -OCOOR", -OCONR'R", -NR'COOR", -CF 3 , and -OCF 3 ; where R represents hydrogen, a lower alkyl, a lower alkenyl or a cyclic group as defined above; and R is hydrogen, a lower alkyl or a lower alkenyl group R" represents a lower alkyl or a lower alkenyl group, and one or more additional suitable components. 13. A LCP network comprising a compound according to any one of claims 1 to 11 or a mixture according to Claim 12 in cross-linked or polymerised form. 14. Use of a compound according to any one of claims 1 to 1 1. or a mixture according to Claim 12. in the manufacture of an optical or an electro-optical device. 15. An optical or electro-optical device including a compound according to any one of claims 1 to 1 1 or a mixture according to Claim 12 in cross-linked or polymerised form.

Inventors: BENECKE CARSTEN, BUCHECKER RICHARD, LUKAC TEODOR, BENECKE, CARSTEN, BUCHECKER, RICHARD, LUKAC, TEODOR
Applicants: BENECKE CARSTEN, BUCHECKER RICHARD, LUKAC TEODOR, ROLIC AG, BENECKE, CARSTEN, BUCHECKER, RICHARD, LUKAC, TEODOR
Application year: 2000
Main classification: C07C69
IPC codes: C07C69, C07C255, C07D307, C08F20, C09K19, G02F1