Preparation of organoxy-terminated organopolysiloxane

Abstract: An organoxy-terminated organopolysiloxane of the general formula (A): wherein R is a monovalent hydrocarbon group, R 1 is a monovalent hydrocarbon group of 1-18 carbon atoms, and R 2 is an organic group of 1-18 carbon atoms, and "a" is an integer of 0, 1 or 2, is prepared by reacting an organopolysiloxane of the formula: HO(R 2 SiO) n H having a viscosity of 10-100,000 centistokes at 25°C with an organoxysilane of the formula: (R 2 O) 4-a -Si-(R 1 ) a or a partial hydrolyzate thereof in the presence of a tetraalkoxytitanium.

Description: This invention relates to methods for preparing organoxy-terminated organopolysiloxanes, for example such as are useful as base polymers in one-part organopolysiloxane elastomer compositions of the type which is generally stable during storage in the absence of moisture but crosslinkable by airborne moisture at substantially ambient temperature. BACKGROUND It is well known in the art to prepare organoxy-terminated organopolysiloxanes by reacting di-, tri- or tetraalkoxysilanes with hydrosilyl groups attached to silicon atoms at molecular ends in the presence of catalysts. The use of amine catalysts is disclosed in USP 3,542,901, USP 4,489,191, French Patent No. 2,597,876, and French Patent No. 2,597,877. USP 3,504,051 discloses the use of potassium acetate, French Patent No. 1,495,011 discloses the use of inorganic oxides, USP 3,647,846 discloses the combination of titanates and amines, French Patent No. 2,604,713 discloses the combination of carboxylic acids and amines, EP 0210402 discloses the use of carbamates, French Patent No. 2,597,875 discloses the use of oxime functional group-containing organic compounds, and JP-B 6-45698 discloses the use of lithium hydroxide. However, the use of amine catalysts has many problems including a reaction time as long as about 15 to 30 minutes at a heating temperature of 60°C, a low percent end blockage, an increased amount of residual SiOH, yellowing and storage instability due to the residual amine which is difficult to remove. The foregoing methods use acids or bases and need a neutralizing step. Although the products are now required to be neutral, the use of amine catalysts suffers from a high probability of leaving amines in the products. Additionally, USP 4,111,890 describes the use of organic titanium derivatives, and British Patent No. 2,144,758 describes the use of alkoxyaluminum chelates. The aluminum and titanium chelates used therein are adequate as the condensation curing catalyst, but not for end blockage because they promote crosslinking during reaction, resulting in gelation and substantial thickening. Therefore, an object of the invention is to provide new and useful methods for preparing organoxy-terminated organopolysiloxanes. Preferred aims include efficiency, the avoidance of gelation and other troubles and the avoidance of the need for neutralisation. The invention provides a method for preparing an organoxy-terminated organopolysiloxane, comprising the step of reacting (1) an organopolysiloxane of the following general formula (I): wherein R is a monovalent hydrocarbon group and n is such an integer that the organopolysiloxane has a viscosity of 10 to 100,000 centistokes at 25°C, with (2) an organoxysilane of the following general formula (II): wherein "a" is an integer of 0, 1 or 2, R 1 is a substituted or unsubstituted monovalent hydrocarbon group of 1 to 18 carbon atoms, and R 2 is an organic group of 1 to 18 carbon atoms, or a partial hydrolyzate thereof, to form an organoxy-terminated organopolysiloxane of the general formula (A): wherein R, R 1 , R 2 , "a" and n are as defined above, wherein the reaction of components (1) and (2) is effected in the presence of (3) a tetraalkoxytitanium of the following general formula (III): Ti(OR 3 ) 4 wherein R 3 is an alkyl group, characterised in that methanol is added during and formed after the reaction. We have found that the organopolysiloxane of formula (A) can be prepared within one hour even at room temperature and usually, at an end blockage of at least 85%. By adding methanol to a mixture of components (1), (2) and (3) during reaction or at the end of reaction, the end blocking time is significantly reduced. The method is advantageous in that since neither basic nor acidic catalysts need be used, the resulting organoxy-terminated organopolysiloxane is suited to electric and electronic applications. In the presence of moisture, this organopolysiloxane will readily cure into a rubbery elastomer. A room temperature curable composition comprising such organopolysiloxane as a base polymer is useful in a wide variety of applications such as adhesives, coating agents, electrically insulating sealants, and building sealants. OPTIONS, PREFERENCES, FURTHER EXPLANATIONS The method for preparing an organoxy-terminated organopolysiloxane according to the invention starts with (1) an organopolysiloxane and (2) an organoxysilane. Component (1) is an organopolysiloxane of the following general formula (I). Herein R is a monovalent hydrocarbon group and n is such an integer that the organopolysiloxane has a viscosity of 10 to 100,000 centistokes at 25°C. R is selected from substituted or unsubstituted monovalent hydrocarbon groups preferably of 1 to 10 carbon atoms, and more preferably 1 to 8 carbon atoms, for example, alkyl groups such as methyl, ethyl, propyl, butyl and hexyl, aryl groups such as phenyl and tolyl, alkenyl groups such as vinyl, allyl and butenyl, aralkyl groups such as benzyl and 2-phenylethyl, Substituted ones of the foregoing groups, e.g. in which some or all of the hydrogen atoms attached to carbon atoms are replaced by halogen atoms or cyano groups, such as chloromethyl, trifluoropropyl and cyanoethyl, are useful in line with established knowledge. Of these, methyl, phenyl, vinyl and trifluoropropyl are preferred, with methyl being most preferred. The letter n representative of the degree of polymerization is such an integer that the organopolysiloxane has a viscosity of 10 to 100,000 centistokes at 25°C and preferably 500 to 100,000 centistokes at 25°C for ease of working. Illustrative, non-limiting examples of the organopolysiloxane of formula (I) are given below. In the formulas, Me is methyl, Ph is phenyl, p and q are positive integers, p+q is an integer corresponding to n. Of these, the compounds of formula (I-a) are preferred. In addition to the above-described structure, the polymer may include a structure which is blocked at one end with 0 to 10 mol% of trimethylsilyl groups. Also the polymer may contain 0 to 3 mol% based on its molecular weight of a branched structure as shown by the following structural formula. The other starting reactant, component (2) serves as an end blocking agent for component (1) and is an organoxysilane of the following general formula (II) or a partial hydrolyzate thereof. Herein "a" is an integer of 0, 1 or 2, and preferably 0 or 1, R 1 is a substituted or unsubstituted monovalent hydrocarbon group of 1 to 18 carbon atoms, and R 2 is an organic group of 1 to 18 carbon atoms. Examples of R 1 are alkyl, alkenyl, aryl and aralkyl groups and halo- and cyano-substituted groups thereof as exemplified above for R, with alkyl, alkenyl and aryl groups being preferred. R 2 is preferably selected from aliphatic organic groups of 1 to 18 carbon atoms, for example, alkyl, alkenyl, aryl, alkyl ether, alkyl ester, alkyl ketone and alkylcyano groups. R2 is preferably an alkyl group, more preferably alkyl group of 1 to 4 carbon atoms, and most preferably methyl. The preferred organoxysilane is an alkoxysilane of the following general formula (II-a): R 1 b Si(OCH 3 ) 4-b wherein R 1 is as defined above and b is equal to 0 or 1, or a partial hydrolyzate thereof. Illustrative, non-limiting examples of the organoxysilane include n-propyltrimethoxysilane, methyltrimethoxysilane, vinyltrimethoxysilane, tetramethoxysilane, ethyltrimethoxysilane, and phenyltrimethoxysilane. For ease of handling, vinyltrimethoxysilane and n-propyltrimethoxysilane are especially preferred. In the batchwise preparation where reaction heat accumulates, n-propyltrimethoxysilane is especially preferred because of its low volatility. Preferably components (1) and (2) are used in such amounts that the moles of component (2) is at least equal to the moles of component (1) or silanol. More preferably the ratio of the moles of component (1) to the moles of component (2) is from 1:1 to 1:100 and especially from 1:1 to 1:20. Using component (2) in excess is usually effective for reducing the time for ends to be blocked and yielding a high percent end blockage. A molar ratio within the above range permits a continuous process to be employed with better results. By reacting components (1) and (2), there is prepared an organoxy-terminated organopolysiloxane of the general formula (A): wherein R, R 1 , R 2 , "a" and n are as defined above. According to the invention, the reaction of components (1) and (2) is effected in the presence of (3) a tetraalkoxytitanium or titanium tetraalkoxide catalyst of the following general formula (III): Ti(OR 3 ) 4 wherein R 3 is alkyl group. Preferably the alkyl groups have 2 or more carbon atoms. Preferably they have not more than 19 carbon atoms, more preferably not more than 4 carbon atoms. Any titanium tetraalkoxide may be used only for end blocking purposes. The end blocking rate is faster in the order of titanium tetraethoxide > titanium tetra-n-propoxide > titanium tetraisopropoxide > titanium tetrabutoxide. Of these, titanium tetraethoxide is most preferred although titanium tetraisopropoxide is most readily available in the industry. For best effect component (3) is preferably used in such amounts that the ratio of the moles of component (3) to the moles of silanol (1) is at least 0.001, more preferably at least 0.01, especially at least 0.05. Preferably the ratio is up to 20, more preferably up to 10, especially up to 5. Components (1) to (3) are admitted into a suitable reactor whereupon reaction may proceed at room temperature or elevated temperature. Preferably the reaction is effected under pressure. In this regard, a reactor capable of tight closure so that pressure is naturally applied is preferred because the reaction is promoted thereby. Although a higher pressure is preferable, an upper limit of up to 1013.3 kPa [10 atm]. and especially up to 506.7 kPa [5 atm]. is recommended for safety. The lower limit is not critical for a pressure higher than atmospheric; typically it is at least 106.4 kPa [1.05 atm]. and especially at least 111.5 kPa [1.1 atm]. Reaction is effected by mixing components (1) to (3) under atmospheric pressure or under applied pressure. More specifically, component (1) first reacts with component (3) and thus thickens. Then component (2) substitutes for component (3) whereupon the desired organoxy-terminated organopolysiloxane is obtained. Although the viscosity is once increased, the product generally resumes the original or desired viscosity at this point. The invention is characterised in that methanol is added to the reaction system after it has thickened by reaction of component (1) with component (3). By adding methanol, the time for end blockage with organoxy groups can be significantly reduced. If methanol is added at the initial, there is a potential for methanol to stop the end blocking reaction. It is therefore preferred to add methanol after component (1) has reacted with component (3) to incur a viscosity increase and before the end blocking reaction with component (3) proceeds to completion. Even when methanol is added at the substantial end of reaction, the percent end blockage can be further increased. An appropriate amount of methanol added is 0.1 to 20 parts, and especially 0.2 to 10 parts by weight per 100 parts by weight of component (1). Less amounts of methanol have little effect whereas excessive amounts may rather restrain the end blocking reaction. Since there is a situation where the viscosity changes a little even after the completion of reaction, mixing for deaeration under vacuum or atmospheric pressure is recommended. Organopolysiloxanes of formula (A) are usually useful as a base polymer in a room temperature curable organopolysiloxane composition of the one part type. To the organopolysiloxane, there may be added a filler, for example, surface treated or untreated silica, heavy calcium carbonate, surface treated or untreated colloidal calcium carbonate; a curing agent, for example, a compound having at least two hydrolyzable groups; an adhesive aid as typified by aminosilane; a condensation catalyst, and other additives. By adding these additives during the mixing step for deaeration, there is obtained a room temperature curable organopolysiloxane composition of the one part type. The room temperature curable organopolysiloxane composition comprising the organoxy-terminated organopolysiloxane according to the invention remains stable during storage, is strongly adhesive to adherends, especially surface treated aluminum members, and cures into a product maintaining a firm bond against water immersion and heating. The room temperature curable composition is thus useful in a wide variety of applications such as adhesives, coating agents, electrically insulating sealants, and building sealants. EXAMPLE Examples of the invention are given below by way of illustration and not by way of limitation. All parts are by weight. The base oils obtained in Examples were analyzed by 29 Si-NMR, from which a percent end blockage was determined. The results are shown in Tables 1 and 2. Reference Example 1 In a Shinagawa mixer, 100 parts of α,ω-dihydroxydimethylpolysiloxane having a viscosity of 50,000 cSt at 25°C, 7 parts of n-propyltrimethoxysilane, and 0.1 part of titanium tetraethoxide were mixed for 30 minutes at room temperature. The mixture was further mixed in vacuum for 30 minutes for deaeration purposes, yielding a base oil which was measured for end blockage by 29 Si-NMR. Reference Example 2 A base oil was prepared as in Example 1 except that 0.1 part of titanium tetra-n-propoxide was used instead of 0.1 part of titanium tetraethoxide. Reference Example 3 A base oil was prepared as in Example 1 except that 0.1 part of titanium tetraisopropoxide was used instead of 0.1 part of titanium tetraethoxide. Reference Example 4 A base oil was prepared as in Example 1 except that 0.1 part of titanium tetra-n-butoxide was used instead of 0.1 part of titanium tetraethoxide. Reference Example 5 A base oil was prepared as in Example 1 except that 0.1 part of titanium tetra-2-ethylhexyloxide was used instead of 0.1 part of titanium tetraethoxide. Example 1 A base oil was prepared as in Example 1 except that the amount of titanium tetraethoxide was changed to 0.25 part, and 2 parts of methanol was added after the mixture thickened. Example 2 A base oil was prepared as in Example 6 except that the amount of methanol was changed to 5 parts. Reference Example 6 A base oil was prepared as in Example 1 except that 6.5 parts of vinyltrimethoxysilane was used instead of 7 parts of n-propyltrimethoxysilane. Reference Example 7 A base oil was prepared as in Example 1 except that 6 parts of methyltrimethoxysilane was used instead of 7 parts of n-propyltrimethoxysilane. Reference Example 8 A base oil was prepared as in Example 1 except that the amount of n-propyltrimethoxysilane was changed to 3.5 parts. Reference Example 9 A base oil was prepared as in Example 1 except that the amount of n-propyltrimethoxysilane was changed to 10.5 parts. Reference Example 10 A base oil was prepared as in Example 1 except that the amount of titanium tetraethoxide was changed to 1 part. Reference Example 11 A base oil was prepared as in Example 1 except that 10 parts of γ-(methacryloxypropyl)trimethoxysilane was used instead of 7 parts of n-propyltrimethoxysilane. Reference Example 12 A base oil was prepared as in Example 1 except that 7 parts of vinyltri(3-methoxypropyleneglycoxy)silane was used instead of 7 parts of n-propyltrimethoxysilane. Reference Example 13 A base oil was prepared as in Example 1 except that 10 parts of γ-(methacryloxypropyl)methyldimethoxysilane was used instead of 7 parts of n-propyltrimethoxysilane. Example 3 In a Shinagawa mixer, 100 parts of α,ω-dihydroxydimethylpolysiloxane having a viscosity of 50,000 cSt at 25°C, 7 parts of n-propyltrimethoxysilane, and 5 parts of methanol were mixed for 5 minutes at room temperature, and 0.2 part of titanium tetraethoxide was added. The mixture was mixed for 30 minutes at room temperature, then mixed in vacuum for 30 minutes for deaeration purposes, yielding a base oil. Reference Example 14 In a Shinagawa mixer, 100 parts of α,ω-dihydroxydimethylpolysiloxane having a viscosity of 50,000 cSt at 25°C, 7 parts of n-propyltrimethoxysilane, and 0.1 part of titanium tetraethoxide were mixed for 10 minutes at room temperature and a pressure of 2 atm. The mixture was then mixed for 30 minutes for deaeration purposes, yielding a base oil. Reference Example 15 In a Shinagawa mixer, 100 parts of α,ω-dihydroxydimethylpolysiloxane having a viscosity of 20,000 cSt at 25°C, 5 parts of methyltrimethoxysilane, and 0.1 part of titanium tetraethoxide were mixed for 3 minutes at room temperature and a pressure of 5 atm. The mixture was then mixed under atmospheric pressure for 20 minutes for deaeration purposes, yielding a base oil. Example 4 In a Shinagawa mixer, 100 parts of α,ω-dihydroxydimethylpolysiloxane having a viscosity of 5,000 cSt at 25°C, 6 parts of vinyltrimethoxysilane, and 0.2 part of titanium tetraethoxide were mixed for 5 minutes at 40°C and a pressure of 2 atm., and 2 parts of methanol was added. The mixture was then mixed under atmospheric pressure for 20 minutes for deaeration purposes, and mixed at 60°C for 30 minutes for deaeration purposes, yielding a base oil. Comparative Example 1 In a Shinagawa mixer, 100 parts of α,ω-dihydroxydimethylpolysiloxane having a viscosity of 50,000 cSt at 25°C, 6.5 parts of vinyltrimethoxysilane, and 0.2 part of lithium hydroxide were mixed for one hour at room temperature, and 3 parts of ethylene chlorohydrin was added for neutralization. The mixture was then mixed under vacuum at 100°C for deaeration purposes, yielding a base oil which was measured for end blockage by 29 Si-NMR. Comparative Example 2 A base oil was prepared as in Comparative Example 1 except that 0.5 part of a 10% methanol solution of lithium hydroxide was added. Comparative Example 3 A base oil was prepared as in Comparative Example 1 except that 0.2 part of aluminum isopropoxide di(ethylacetoacetonato) was added instead of the 10% methanol solution of lithium hydroxide. Gelation occurred. Comparative Example 4 A base oil was prepared as in Comparative Example 1 except that 0.2 part of titanium diisopropoxide di(ethylacetoacetonato) was added instead of the 10% methanol solution of lithium hydroxide. Gelation occurred. Comparative Example 5 A base oil was prepared as in Comparative Example 1 except that 0.2 part of dibutyltin dilaurate was added instead of the 10% methanol solution of lithium hydroxide. Gelation occurred. Comparative Example 6 A base oil was prepared as in Comparative Example 1 except that 0.2 part of tin dilaurate was added instead of the 10% methanol solution of lithium hydroxide. Gelation occurred. Comparative Example 7 A base oil was prepared as in Comparative Example 1 except that the 10% methanol solution of lithium hydroxide was omitted and no catalyst was added. End blockage (%) Reaction time (min) Terminal monomethoxide content (%) Reference Example 1 94.5 30 0.52 Reference Example 2 93.8 30 0.58 Reference Example 3 93.3 30 0.60 Reference Example 4 92.4 30 0.80 Reference Example 5 90.8 30 0.88 Example 1 95.7 30 0.12 Example 2 92.8 30 0.12 Reference Example 6 93.0 30 0.59 Reference Example 7 92.7 30 0.52 Reference Example 8 91.1 30 0.57 Reference Example 9 98.2 30 0.57 Reference Example 10 89.9 30 1.02 Reference Example 11 93.4 30 0.62 Reference Example 12 97.8 30 0.34 Reference Example 13 88.8 30 0.45 Example 3 97.1 30 0.21 Reference Example 14 98.4 10 0.38 Reference Example 15 99.0 3 0.15 Example 4 97.5 5 0.20 End blockage (%) Reaction time (min) Terminal monomethoxide content (%) CE 1 56.7 60 7.45 CE 2 60.3 60 9.25 CE 3 unmeasurable because of gelation upon admission CE 4 unmeasurable because of gelation upon admission CE 5 unmeasurable because of gelation upon admission CE 6 unmeasurable because of gelation upon admission CE 7 0 60 0 In the embodiments, therefore, organoxy-terminated organopolysiloxanes were prepared within about one hour while maintaining a good end blocking rate of about 85 to 99%. Reasonable modifications and variations are possible from the foregoing disclosure of embodiments in the light of the general teaching herein.

Claims: A method of preparing organoxy-terminated organopolysiloxane, comprising reacting (1) organopolysiloxane of the following general formula(I): wherein R is monovalent hydrocarbon group and n is an integer such that the organopolysiloxane has a viscosity of from 10 to 100,000 centistokes at 25°C, with (2) organoxysilane of the following general formula (II), or partial hydrolysate thereof: wherein a is 0, 1 or 2, R 1 is substituted or unsubstituted monovalent hydrocarbon group of from 1 to 18 carbon atoms and R 2 is an organic group of from 1 to 18 carbon atoms; to form organoxy-terminated organopolysiloxane of the general formula (A): wherein R, R 1 , R 2 , a and n are as defined above, wherein the reaction of components (1) and (2) is effected in the presence of (3) tetraalkoxytitanium compound of the following general formula (III): Ti(OR 3 ) 4 (III) wherein R 3 is alkyl group, characterised in that methanol is added during and/or after the reaction. A method of claim 1 wherein the methanol is added at from 0.1 to 20 parts by weight per 100 parts by weight of component (1). A method of claim 1 wherein the methanol is added at from 0.2 to 10 parts by weight per 100 parts by weight of component (1). A method of any one of the above claims wherein said reaction is effected under raised pressure. A method of claim 4 wherein the raised pressure is at least 106.4 kPa [1.05 atm]. A method of claim 4 wherein the raised pressure is at least 111.5 kPa [1.1 atm]. A method of any one of the above claims wherein R is selected from substituted or unsubstituted monovalent hydrocarbon groups of 1 to 10 carbon atoms. A method of claim 7 wherein R is selected from alkyl, aryl, alkenyl and aralkyl. A method of claim 7 wherein the organopolysiloxane of formula (I) is selected from: wherein Me is methyl, Ph is phenyl, and p and q are positive integers and p + q corresponds to n in formula (I). A method of any one of the above claims wherein component (2) is alkoxysilane of the following general formula (II-a), or partial hydrolysate thereof: R 1 b Si(OCH 3 ) 4-b (II-a) wherein R 1 is as defined above and b is 0 or 1. A method of claim 10 wherein component (2) is selected from n-propyltrimethoxysilane, methyltrimethoxysilane, vinyltrimethoxysilane, tetramethoxysilane, ethyltrimethoxysilane and phenyltrimethoxysilane. A method of any one of the above claims wherein the molar ratio of component (1) to component (2) is between 1:1 and 1:100. A method according to any one of the above claims wherein component (3) is selected from the group comprising: titanium tetrabutoxide, titanium tetraisopropoxide, titanium tetra-n-propoxide and tetraethoxytitanium. A method of claim 13 wherein component (3) is tetraethoxytitanium. A method of any one of the above claims wherein the molar ratio of component (3) to component (1) is from 1:001 to 1:20. A method of making a room-temperature curable organopolysiloxane composition, comprising making an organoxy-terminated organopolysiloxane by a method according to any one of the preceding claims, followed by blending the organoxy-terminated organopolysiloxane as base polymer in the manufacture of said room temperature curable organopolysiloxane composition.

Inventors: FUJIKI HIRONAO, KIMURA KENICHI, MATSUI CHINAMI, MIYAKE MASATOSHI, FUJIKI, HIRONAO, KIMURA, KENICHI, MATSUI, CHINAMI, MIYAKE, MASATOSHI, Fujiki, Hironao, Silicone-Electronics Materials, Kimura, Kenichi, c/o Gunma Complex, Matsui, Chinami, c/o Gunma Complex, Miyake, Masatoshi, Silicone-Electronics Materials
Applicants: SHINETSU CHEMICAL CO, SHIN-ETSU CHEMICAL CO., LTD.
Application year: 2000
Main classification: C08G77
IPC codes: C08G77, C08L83