FLAME-RETARDED POLYPHENYLENE ETHER COMPOSITION AND METHOD OF MAKING SAME

Abstract: Polyphenylene ether (PPE) compositions with good fire and flame-retardant characteristics utilize lower levels of organophosphate fire-retardant, and therefore do not suffer from the drawbacks of previously known fire- and flame-retardant PPE compositions. The compositions include (a) a polymer component containing at least 50 % of a polyphenylene ether; (b) glass reinforcing fibers in an amount sufficient to increase the modulus and strength of the polymer component; (c) a fire retardant component which is preferably an organophosphate fire retardant; (d) an organoclay component in an amount effective to enhance the flame-retardant characteristics of the composition; and (e) a mineral component. Other conventional additives utilized in formulation of PPE may be included. The composition is made by mixing the ingredients and compounding into a composition which is suitable for injection molding. This composition can be used in the manufacture of injection molded articles such as electronic components, including television internals such as deflection yokes; printer chassis and plastic pallets.

Description: FLAME-RETARDED POLYPHENYLENE ETHER COMPOSITION AND METHOD OF MAKING SAME BACKGROUND OF THE INVENTION This application relates to a flame-retarded polyphenylene ether (PPE) compositions and to a method of making same. PPE is a thermoplastic material with high glass transition temperature, high dimensional stability, low specific gravity, hydrolytic stability and good mechanical performance. This combination of propeπies allows PPE based formulations to be injected molded into products which are used for high heat applications, for example in the automotive, electrical, and construction industries For some applications, where increased modulus and strength are required, PPE may be reinforced with glass fibers. However, these reinforced PPE formulations have undesirable flammability characteristics. At high temperature or when exposed to flame, glass-filled PPE tends to burn continuously without extinguishing. Because of this, fire-retarded grades of glass-filled PPE (especially those rated UL94 V0) tend to be formulated using a large amount (for example >15% by weight for a rating of UL94 V0 at l/16th inch thickness) of fire-retardant additives such as phosphorus-containing organic compounds. This increases the cost of the product, and also makes it more difficult to formulate glass fiber-reinforced PPE to meet UL94 V0 fire-retardant standards, because the addition of large amounts of phosphorus-containing organic compounds like resorcinol diphosphate plasticizes the composition and significantly reduces the heat deflection temperature of the formulation. SUMMARY OF THE INVENTION The present invention provides PPE compositions with good fire and flame- retardant characteristics, which utilize lower levels of organophosphate fire-retardant and which therefore do not suffer from the drawbacks of previously known fire- and flame-retardant PPE compositions. The compositions comprise (a) a polymer component comprising at least 50% of a polyphenylene ether; (b) glass reinforcing fibers in an amount sufficient to increase the modulus and strength of the polymer component, (c) a fire retardant component, preferably comprising an organophosphate fire retardant; (d) an organoclay component in an amount effective to enhance the flame- retardant characteristics of the composition; and (e) a mineral component. Other conventional additives utilized in formulation of PPE may be included. This composition can be used in the manufacture of injection molded articles such as electronic components, including television internals such as deflection yokes; printer chassis and plastic pallets. The present invention further provides a method for preparation of a glass- reinforced PPE composition. In accordance with this method, the composition is prepared by compounding a mixture of (a) a polymer component comprising at least 50% of a polyphenylene ether; (b) glass reinforcing fibers in an amount sufficient to increase the modulus and strength of the polyphenylene ether matrix; (c) a fire retardant component, preferably comprising an organophosphate fire retardant; (d) an organoclay component in an amount effective to enhance the flame- retardant characteristics of the composition; and (e) a mineral component., as well as optional other components at elevated temperature to provide a homogenous blend of the materials. This compounding is suitably carried out in a screw type extruder at a temperature of 520 to 620 °F, preferably from 540 to 560 °F. DETAILED DESCRIPTION OF THE INVENTION The PPE compositions of the present invention comprise a polymer component comprising at least 50% of a polyphenylene ether; glass reinforcing fibers in an amount sufficient to increase the modulus and strength of the polyphenylene ether matrix; an organophosphate fire retardant component; an organoclay component in an amount effective to enhance the flame-retardant characteristics of the composition; and a mineral component. These components act synergistically to provide glass-fiber reinforced PPE with good fire and flame-retardant characteristics, which utilize lower levels of organophosphate fire-retardant and which therefore do not suffer from the drawbacks of previously known fire- and flame-retardant PPE compositions. This synergism is demonstrated in the results of the tests described below in the Examples which are summarized in Tables 1, 3 and 4. In these tests, samples of glass- fiber reinforced PPE without organoclay and with various loadings of organoclay were prepared by compounding in a twin screw extruder. Some of the compositions were prepared with a mineral component (mica) and others without a mineral component. The samples were then injection molded and tested for flame-out time in accordance with the UL protocol for V0 rating. The experiments indicated that addition of small amounts of organoclay along with a mineral component to fire-retardant glass-fiber reinforced PPE allowed achievement of enhanced fire-retardant performance and compliance with the UL94 VO standard Addition of larger amounts of organoclay or the addition of small amounts of organoclay in the absence of the mineral component resulted in a deterioration of the fire-retardant performance Thus, it is clear that there is a critical and synergistic combination of ingredients which leads to the improved characteristics of the compositions of the present invention The composition of the invention is made from a polymer component in which various fillers and additives are incorporated As used herein, the term "polymer component" refers to the combined mass of all organic polymers present in the composition While the polymer component may be 100% of a polyphenylene ether, it may also include other polymers selected to achieve desired properties in the final composition Thus, the polymer component of the composition comprises at least 50% and preferably at least of one or more species of polyphenylene ether As used herein, the term "polyphenylene ether" refers to individual polymeric PPE species or to mixtures of polymeric PPE species unless the context indicates otherwise PPE useful in the present invention is a polymer having repeat units of the general formula wherein in the formula, R 2 , R 3 , and R4 which may be the same or different each represent a member selected from the group consisting of hydrogen atoms halogen atoms, substituted and unsubstituted alkyl groups and substituted and unsubstituted alkoxy groups The PPE may be a homopolymer, 1 e the repeat units have the same structural formula, or a copolymer consisting of a combination of two or more types of repeat units where at least one of the Ri, R 2 , R 3 , and R4 are different for each different repeat unit comprising the copolymer The polymer is tei minated at each end by a monovalent chemical group or atom such as hydrogen a halogen, a monovalent hydrocarbon radical (saturated, unsaturated or aromatic) or the like There are no particular restrictions on the method of manufacturing PPE For example, this may be produced by reacting phenols according to the procedures presented in the specifications of U S Pat Nos 3,306 874, 3,257,357, or 3,257,358 Examples of these phenols include 2,6-dιmethylphenol, 2,6-dιeth>lphenol, 2,6-dιbutylphenol, 2,6-dιlaurylphenol, 2,6-dιpropylphenol, 2,6-dιphenylphenol, 2-methyl-6-ethylphenol, 2-methyl-6-cyclohexylphenol, 2-methyl-6-tolyl)phenol, 2-methyl-6-methoxyphenol, 2-methyl-6-butylphenol, 2,6-dιmethoxyphenol, 2,3,6-tπmethylphenol, 2,3,5,6-tetramethylphenol, 2,6-dιethoxyphenol, etc , but the invention is not limited to these One may either use a corresponding homopolymer obtained by reacting one of the above substances or a corresponding copolymer obtained by reacting two or more of the above substances and having the different units contained in the above formula Specific examples of PPE polymers useful in the invention include but are not limited to poly(2,6-dιmethyl-l,4-phenylene) ether, poly(2,6-dιethyl-l,4-phenylene) ether, poly(2-methyl-6-ethyl-l,4-phenylene) ether, poly(2-methyl-6-propyl- 1,4-phenylene) ether, poly(2,6-dιpropyl- 1,4-phenylene) ether, and poly(2-ethyl-6-propyl- 1,4-phenylene) ether Moreover, an example of the PPE copolymer is a copolymer partially containing an alkyl tπsubstituted phenol such as 2,3,6-trimethylphenol in the aforementioned polyphenvlene ether repeated unit The PPE resins may also be copolymers having a styrene compound grafted on An example of such a styrene-compound-grafted polyphenylene ether is a copolymer obtained by graft polymerization of a styrene compound such as styrene, alpha -methylstyrene, vinylstyrene, or chlorostyrene onto the aforementioned PPE Additional polymeric materials which may be included, individually or in combination, in the polymer component of the invention include crystalline polystyrene which can be added in amounts of 0 to 50 % by weight of the polymer component to improve processability, high impact polystyrene (HIPS) , which can be added in amounts of 0 to 50 % by weight of the polymer component to improve processability and increase impact strength, EPDM and styrene-butadiene block copolymers which can be added in amounts of 0 to 20 % by weight of the polymer component to improve the impact properties of the polymer component, and polyamides such as nylon-6,6 and nylon-6 which can be added in amounts of 0 to 50% by weight of the polymer component to improve melt flow and impart increased resistance to organic solvents The polymeric component may also include a terpene phenol resin (i e, a copolymer of monoterpenes and phenol such as N1REZ 2150/7042™) in amounts of 0 to 25 % by weight of the polymeric component to provide better flow to the composition Other polymers that can be blended in the compositions of the invention include polyphenylene sulfides in amounts from 0 to 50 % by weight to improve heat deflection temperature and the flow Glass fibers suitable for use in the compositions of the invention may be of various lengths appropriate and thicknesses appropriate to the application Coatings of * coupling agents, such as aminosilanes may be employed if desired The glass fibers are added in an amount sufficient to increase the modulus and the strength of the product by a desired amount, and persons skilled in the art will be able to judge the appropriate levels and type of glass fiber needed to achieve a given result In general, glass fibers are added in amounts of 5 to 50% by weight The fire retardant component of the compositions may be a halogenated fire retardant such as brominated polystyrene Ecologically-preferred compositions, however, are halogen-free and utilize an organophosphate fire retardant The organophosphate fire retardant component of the compositions may be any of numerous organophosphorus fire retardants which are known in the art Specific examples include resorcinol diphosphate, bisphenol A diphosphate, tetraxylyl piperazine diphosphamide and the like, e g such as disclosed in US patents 4,933,386, 4,343,732, 5,455,292 and RE 36, 188 herein and herewith specifically incorporated by reference. The amount of organophosphate fire retardant is selected to achieve the desired final level of fire-retardance Because of the synergistic effects of utilizing the organoclay additives in the compositions of the invention, the amount of organophosphate fire-retardant can be reduced, and will generally be in the range of 5 to 30%) by weight The organoclay component comprises one or more organoclay materials. As used herein, organoclay is a layered silicate clay, derived from layered minerals, in which organic structures have been chemically incorporated Illustrative examples of organic structures are trimethyldodecylammonium ion and N,N'-didodecylimidazolium ion. Since the surfaces of clay layers, which have a lattice-like arrangement, are electrically charged, they are capable of binding organic ions. There is no limitation with respect to the layered minerals employed in this invention other than that they are capable of undergoing an ion exchange with the organic ions The preferred organoclays are layered minerals that have undergone cation exchange with organo- cations and/or onium compounds Illustrative of such layered minerals are the kaolinite group and the montmorillonite group It is also within the scope of this invention to employ minerals of the illite group which can include hydromicas, phengite, brammallite, glaucomite, celadonite and the like. Often, however, the preferred layered minerals include those often referred to as 2: 1 layered silicate minerals like muscovite, vermiculite, saponite, hectorite and montmorillonite, wherein montmorillonite is often preferred. The layered minerals described above may be synthetically produced However, most often they are naturally occurring and commercially available Organoclays of the type suitable for use in this invention are described in US Patents Nos 5,773,502 and 5,530,052 which are incorporated herein by reference. The mineral component may be a silicate, such as mica, or regular clay or talc. Other additives can be included in the compositions of the invention in accordance with conventional practice in the art. For example, stabilizers such as sterically hindered phenols, organic phosphites, diazide oxalates, sterically hindered amines or amine N- oxides may be incorporated. Other exemplary additives include ZnS which functions to deactivate residual copper-based catalyst present in PPE, MgO or ZnO which function as an acid quencher to quench acid generated by the deactivation of residual catalyst, and carbon black or other colorant which functions as a pigment to color the composition The invention will now be further described with reference to the following, non-limiting examples Example 1 Samples of glass fiber-reinforced PPE were prepared without organoclay and with various loadings of organoclay The materials used in each sample are summarized in Table 1, where 0 33 IV PPE refers to a PPE homopolymer prepared by an oxidative coupling process and having an intrinsic viscosity of 0 33 , Nirez 2150/7240 is a terpene phenol resin available from Arizona Chemical Co , OCF R22Y K-filament glass fibers are 4 mm long, 14 micron diameter glass fibers sized with an amino silane coupling agent and a urethane film former obtained from Owens-Corning Fiberglas, Mica Suzoπte 200HK is a preparation of special delaminated pure phlogopite mica having a median particle size of 45 microns obtained from Zemex Industrial Minerals, Inc , organoclay CLOISITE 15A is a sodium montmorillonite that has been exchanged with dimethyl hydrogenated ditallow ammonium chloride obtained from Southern Clay Products, Gonzalez, TX, and phosphite 168 stabilizer is tns-(2,4- dι-/-butylphenyl) phosphite which acts as a thermal stabilizer and antioxidant and which is available from various sources including Argus Chemical, Witco, Great Lakes Chemical and Ciba Geigy Corp All amounts in the Table are set forth in units of weight The samples were compounded in a Werner & Pfleiderer co-rotating lntermeshing twin-screw extruder The extruder has a primary (upstream) melting and mixing section for melting resins and mixing with each other, and mixing mica with the polymer melt, and a secondary (downstream) mixing section for distributive mixing of glass fibers Thus, glass fibers are added downstream For the experiments described in this example, the extruder was operated at a temperature of 550 °F, and a speed of 350 rpm, to result in polymer production at a rate of 40 lb/hr After compounding the samples were injection molded using a Van Dorn Demag 120 ton injection molding machine (melt temperature 560 °F, mold temperature 1 0 ϋ F) to produce specimens for testing Table The compositions made in Example 1 were tested for flammability using a flame retardance testing tool which provides a prediction of the likelihood that a particular UL standard, such as UL-94 will be passed The UL-94 protocol calls for bar-shaped specimens of dimensions 5"( 12 7 cm) x '/ ' ( 1 3 cm) width x the desired normal thickness, UL-94 ratings being specified for a particular thickness A flame having an inner cone of height V*" (1 9 cm) is applied to each specimen so that a distance of 3/8" (1.0 cm) separates the lower end of the specimen from base of the flame The flame is held in that position for 10 seconds and then removed A burn time is defined as the time required for the flame issuing from the specimen to disappear. If burning of the specimen ceases within 30 seconds, the flame is reapplied for an additional 10 seconds The criteria for V-0, V- 1 , and V-2 ratings are listed in Table 2 Table 2 Vertical Flame Class Requirements For a V-0 rating, no individual burn times, from the first or second application may exceed 10 seconds. The total of the burn times for any five specimens may not exceed 50 seconds. Drip particles that ignite a piece of cotton gauze situated below the specimen are not allowed For a V-l rating, no individual burn times, from the first or second application may exceed 30 seconds. The total of the burn times for any five specimens may not exceed 250 seconds Drip particles that ignite a piece of cotton gauze situated below the specimen are not allowed For a V-2 rating, no individual burn times, from the first or second application may exceed 30 seconds The total of the burn times for any five specimens may not exceed 250 seconds. Drip particles that ignite a piece of cotton gauze situated below the specimen are allowed. A statistical analysis of the data obtained from a flame test can be applied to determine the probability of at least one possible outcome of the test. Possible outcomes include a first submittal pass, including first time pass and retest, and a second submittal pass, including first time pass and retest, and failure The probability of at least one outcome, preferably a first time pass on a first submission, provides a measure of the flame retardance of the polymer composition, while minimizing the variability inherent in flame testing, particularly the UL-94 test The raw data may be transformed prior to use in the statistical calculations by conversion to equivalent logarithmic values ("Logarithm" and "logarithmic" refer to base 10 logarithms.) Times less than one second may be rounded up to one second in order to avoid negative logarithmic values The logarithm of the burn time may then be calculated and used in subsequent steps Use of transformed data is preferred as a more normal distribution of values associated with burn time is thereby provided Raw data do not show a normal (bell-shaped) distribution curve because there can be no values less than zero, and data points are typically clustered in the space below the maximum individual burn time The transformed data, however, more closely fit a normal distribution curve. The probability of a first time pass may be determined according to the formula. "first time pass = (Ptl>mbt, n=ϋ X Pl2>mbt, n=0 "total mtbt X Pdπp, n=θ) where Pu » m bt, n =o is the probability that no first burn time exceeds a maximum burn time value, Pt 2 >mbt, n=o is the probability that no second burn time exceeds a maximum burn time value, P ot K -mtbt is the probability that the sum of the burn times is less than or equal to a maximum total burn time value, and Pd np n -ι > is the probability that no specimen exhibits dripping during the flame test First and second burn time refer to burn times after a first and second application of the flame, respectively The probability that no first burn time exceeds a maximum burn time value, Pu>mbt, n=o, may be determined from the formula where P t ι> m bt is the area under the log normal distribution curve for t l >mbt and where the exponent "5" relates to the number of bars tested The probability that a single second burn time exceeds a maximum burn time value may be determined from the formula where Po >m bt is the area under the normal distribution curve for t2>mbt. As above, the mean and standard deviation of the burn time data set are used to calculate the normal distribution curve For the UL-94 V-0 rating, the maximum burn time is 10 seconds For a V-l or V-2 rating, the maximum burn time is 30 seconds The probability Pd np, n =o that no specimen exhibits dripping during the flame test is an attribute function, estimated by where the number of bars that drip / the number of bars tested The probability that the sum of the burn times is less than or equal to a maximum total burn time value may be determined from a normal distribution curve of simulated 5-bar total burn times The distribution may be generated from a Monte Carlo simulation of 1000 sets of five bars using the distribution for the burn time data determined above. Techniques for Monte Carlo simulation are well known in the art. A normal distribution curve for 5-bar total burn times may be generated using the mean and standard deviation of the simulated 1000 sets Therefore, may be determined from the area under a log normal distribution curve of a set of 1000 Monte Carlo simulated 5-bar total burn time for total <= maximum total burn time For the UL-94 V-0 rating, the maximum total burn time is 50 seconds For a V-l or V-2 rating, the maximum total burn time is 250 seconds The probability of a retest is determined according to the following formula: Pretest = ("tl>mbt, n=l X Pβ mbl, n=0 X Ptutal mtbt Pdnp, n=θ) "" * " (Ptl>mbt, + (Ptl>mbt, n=0 x Pl2>mbt, n=0 * mtbt<total<=mrtbt X Pdnp, n=θ) ~*~ X " drip, n=l) where P t ι>mbt, n = ι is the probability that a single first burn time exceeds a maximum burn time value, is the probability that a single second burn time exceeds a maximum burn time value, is the probability that the sum of individual burn times is greater than the maximum total burn time value and is less than or equal to the maximum retest total burn time value, is the probability that a single specimen exhibits dripping during the flame test and P t ι . m bι. and Pdnp, n=o, are as defined above The probability that a single first burn time exceeds a maximum burn time value may be determined from the formula. "tl>mbt, n=l = 5 X Ptl mbt X 1 "Pt l ^ mbt) where P t ι- m bt is defined as above The probability that a single second burn time exceeds a maximum burn time value may be determined from the formula Pt2>mbt, n=l = 5 X Pt2>mbt X ( 1 "Pt2 mbt) where P t 2>mbt is defined above. The probability that the sum of individual burn times is greater than the maximum total burn time value and is less than or equal to the maximum retest total burn time value may be determined from the normal distribution curve of simulated 5- bar total times, as described above for is equal to the area under a log normal distribution curve of a set of 1000 Monte Carlo simulated 5-bar total burn time for maximum total burn time < total <= the maximum retest total burn time value. For the UL-94 V-0 rating, the maximum total burn time is 50 seconds, and the maximum retest total burn time value is 55 seconds For a V-l or V-2 rating, the maximum total burn time is 250 seconds, and the maximum retest total burn time value is 255. The probability that a single specimen exhibits dripping during the flame test may be estimated from the following attribute function: Pdnp, n= l = 5 X Pd p X ( 1 " Pdnp) where P dπp is defined as for a first time pass, above By definition, the sum of the probabilities of possible outcomes of a first submittal is one: Σ(Prθbabilities) = P fi time pas s + P retest + P failure, no retest = 1 ■ Therefore, the probability of a failure is given by: * failure, no retest — 1 " i first time pass " r retest The probability of a first submittal pass is given by. " 1 st submittal P ass — "first time P ass " * " " ictesi "first time pass where P flrst tιm _ pass and P re tesi are as defined above. The probability of a second submittal pass is determined according to: "2nd submittal pass " failure, no retest ^ "first time P ass ± retest X * first time pass where Pf lrs t time pa s , Pretest and P failure, no retest as defined above Finally, the probability of a pass after a first and second submittal, or the overall probability of a pass is- ^ ov erall pass * 1st submittal pass "■ " 2 nd submittal pass Using this procedure, each of the compositions of Table 1 were evaluated, and the results are summarized in Table 3 As shown, compositions containing mineral filler and organoclay in an amount of from 0.5 to 0 75 % by weight had very good flame retardance properties and high likelihood of passing the UL-94 tests. Compositions with lower levels of organoclay worked less well, while compositions with 5 % by weight exhibited a deterioration in performance. Example 2 The experiments of Examples 1 were repeated using samples with and without mineral filler in accordance with the compositions set forth in Table 4 and tested for flame retardance characteristics In these compositions, the importance of mineral filler with various levels of the organoclay component was tested As shown, the presence of both the organoclay and the mineral filler result in the best flame- retardance properties. Table 3 Notes 1 Sample 5 burned completely when the flame was applied the first time Thus a second flame application was not possible. A consequence of this was that tl -total flame out time, first application (sec ) was 880 second, and t2 could not be calculated. Table 4 0 ) n - D Note to Table 4: The total loading of glass fiber and mica was kept constant at 20 weight percent which enabled studying the effect of replacing glass fibers by mica. n 00 0 > n

Claims: WHAT IS CLAIMED IS: 1 A composition comprising (a) a polymer component comprising at least 50% of polyphenylene ether; (b) glass reinforcing fibers in an amount sufficient to increase the modulus and strength of the composition, (c) a fire retardant component; (d) an organoclay component in an amount effective to enhance the flame-retardant characteristics of the composition, and (e) a mineral component 2. The composition of claim 1, wherein the fire retardant component is an organophosphate 3. The composition of claim 2, wherein the organoclay component is a silicate 4. The composition according to claim 3, wherein the organoclay component is present in an amount from 0 25 to 0 75 % by weight of the composition. 5 The composition of claim 2, wherein the mineral component is mica 6. The composition according to claim 5, wherein the organoclay component is present in an amount from 0 25 to 0 75 % by weight of the composition. 7. The composition of claim 2, wherein the composition comprises 5 to 50%) by weight of glass fibers and 5 to 30% by weight of the organophosphoais fire retardant 8. The composition of claim 2, wherein the organophosphorus fire retardant is resorcinol diphosphate. 9. The composition of claim 8, wherein the mineral component is mica. 10. The composition of claim 9, wherein the organoclay component is present in an amount from 0.25 to 0.75 % by weight of the composition. 1 1. The composition of claim 10, wherein the composition comprises 5 to 50%) by weight of glass fibers and 5 to 30% by weight of the organophosphorus fire retardant. 12. An injection-molded article formed from a glass fiber-reinforced polyphenylene ether composition, wherein the glass fiber-reinforced polyphenylene ether composition comprises: (a) a polymer component comprising at least 50% of a polyphenylene ether; (b) glass reinforcing fibers in an amount sufficient to increase the modulus and strength of the polyphenylene ether composition; (c) a fire retardant component; (d) an organoclay component in an amount effective to enhance the flame-retardant characteristics of the composition; and (e) a mineral component. 13. The article of claim 12, wherein the fire retardant component is an organophosphate. 14. The article of claim 13, wherein the organoclay component is a silicate. 15. The article of claim 13, wherein the organoclay component is present in an amount from 0.25 to 0.75 % by weight of the composition. 16. The article of claim 13, wherein the mineral component is mica 17 The article of claim 16, wherein the organoclay component is present in an amount from 0.25 to 0 75 % by weight of the composition 18. The article of claim 17, wherein the composition comprises 5 to 50% by weight of glass fibers and 5 to 30% by weight of the organophosphorus fire retardant 19. A method for making a glass fiber-reinforced polyphenylene ether composition, comprising the steps of preparing a mixture by combining the following ingredients (a) a polymer component comprising at least 50%) of a polyphenylene ether; (b) glass reinforcing fibers in an amount sufficient to increase the modulus and strength of the polyphenylene ether composition, (c) a fire retardant component; d) an organoclay component in an amount effective to enhance the flame-retardant characteristics of the composition; and e) a mineral component, and compounding the mixture to blend the ingredients into a uniform composition 20. The method of claim 19, wherein the fire retardant component comprises an organophosphate fire retardant. 21. The method of claim 20, wherein the mineral component is mica 22. The method of claim 22, wherein the organoclay component is present in an amount from 0.25 to 0 75 % by weight of the composition

Inventors: PATEL NIRAJKUMAR, PATEL, NIRAJKUMAR
Applicants: GEN ELECTRIC, GENERAL ELECTRIC COMPANY
Application year: 2000
Main classification: C08K5
IPC codes: C08J5, C08K3, C08K5, C08K7, C08K9, C08L71