NEW MOLECULARLY IMPRINTED POLYMERS GRAFTED ON SOLID SUPPORTS

Abstract: The invention refers to a molecularly imprinted polymer, a method of preparing a molecularly imprinted polymer material, and the use thereof. According to the invention a support and a composition comprising at least one monomer, and a template, in a polymerisation medium is polymerised with a free radical initiator, whereafter the template is removed from the molecularly imprinted polymer obtained. The polymerisation is confined to the surface of the support, preferably by confining the free radical initiator to the support by bonding or adsorption. The molecularly imprinted polymer may be used in chromatography, for separations, in chemical sensors, in molecular recognition as stationary phase in capillaries, in selective sample enrichment or in catalysis.

Description: NEW MOLECULARLY IMPRINTED POLYMERS GRAFTED ON SOLID SUPPORTS Technical Field of the Invention The present invention relates to a molecularly imprinted polymer, to a method for preparing said molecularly imprinted polymer, and to the use of said molecu- larly imprinted polymer. Background Art In the fields of medical, dietary, environmental and chemical sciences there is an increasing need for the selective separation of specific substances m complex mixtures of related substances. The end goal can be the preparative isolation of a certain compound or compounds or measurements of their concentration. Molecularly imprinted polymers (MIPs) often exhibit a high selectivity towards their substrate m analogy with the antibody- antigen complementarity . (1 , 2) The technique shows promise m chiral separations of for example ammo acid derivatives, peptides, phosphonates, ammoalcohols and beta-blocking compounds, affinity chromatography of nucleotides and the DNA-bases as well as substitute for antibodies m immunoassays for commercial drugs. Molecular imprinting (MI) consists of the following key steps: (1) Functional monomers are allowed to interact reversibly with a template molecule m solution. (2) The hereby formed template assemblies are copolymensed with a cross-linking monomer resulting m a cross-linked network polymer. (3) The template is displaced and the resulting MIP material can be used for selective molecular recognition of the corresponding compound. If the MIP material is crushed and sieved it can be packed m a chromatographic column and used for chromatographic separation of the template from structurally related analogs. Analytical as well as preparative applications are here possible. Preparative applications can be separation of a compound from a complex mixture of structurally related compounds and isolation of the compound. This can be through an affinity chromatographic procedure where pH, ion strength or solvent gradients can be used in order to control the strength of interaction with the stationary phase. The separation can target enantiomers or diastereomers m a mixture of enantiomers or diastereomers of one or many compounds. Analytical applications can m addition to the above mentioned separa- tions be: competetitive binding assays, chemical sensors or selective sample enrichments. Currently the most widely applied technique to generate molecularly imprinted binding sites is represented by the non-covalent route developed by the group of Mosbach(3) . This makes use of non-covalent self-assembly of the template with functional monomers prior to polymerisation, free radical polymerisation with a cross-linking monomer and then template extraction followed by re- binding by non-covalent interactions. Although the prepa- ration of a MIP by this method is technically simple it relies on the success of stabilisation of the relatively weak interactions between the template and the functional monomers. Stable monomer-template assemblies will m turn lead to a larger concentration of high affinity binding sites m the resulting polymer. The materials can be synthesized m any standard equipped laboratory m a relatively short time and some of the MIPs exhibit binding affinities and selectivities m the order of those exhibited by antibodies towards their antigens. Most MIPs are synthesized by free radical polymerisation of functional monounsaturated (vinyhc, acrylic, methacrylic) monomers and an excess of cross-linking di- or triunsatu- rated (vmylic, acrylic, methacrylic) monomers resulting m porous organic network materials. These polymeπsa- tions have the advantage of being relatively robust allowing polymers to be prepared m high yield using different solvents (aqueous or organic) and at different temperatures (4) . This is necessary in view of the varying solubilities of the template molecules. The most successful non-covalent imprinting systems are based on commodity acrylic or methacrylic monomers, such as methacrylic acid (MAA) , cross-linked with ethyle- neglycol dimethacrylate (EDMA) . Initially, derivatives of amino acid enantiomers were used as templates for the preparation of imprinted stationary phases for chiral separations (MICSPs) but this system has proven generally applicable to the imprinting of templates allowing hydrogen bonding or electrostatic interactions to develop with MAA. (5, 6) The procedure applied to the imprinting with L-phenylalanine anilide (L-PA) is outlined in Fig. 1. In the first step, the template (L-PA) , the functional mono- mer (MAA) and the cross-linking monomer (EDMA) are dissolved in a poorly hydrogen bonding solvent (diluent) of low to medium polarity. The free radical polymerisation is then initiated with an azo initiator, commonly azo- N, N' -bis-isobutyronitrile (AIBN) either by photochemical homolysis below room temperature (6 , 7) or thermochemi- cally at 60°C or higher (5) . Lower thermochemical initiation temperatures down to 40°C or 30°C may be obtained using azo-N, N' -bis-divaleronitrile (ABDV) and V70 resp. instead of AIBN as initiator (see) . (7, 8) In the final step, the resultant polymer is crushed by mortar and pestle or in a ball mill, extracted by a Soxhlet apparatus, and sieved to a particle size suitable for chromatographic (25-38 μm) or batch (150-250 μm) applications. (6) The polymers are then evaluated as stationary phases in chromatography by comparing the retention time or capacity factor (k' ) (9) of the template with that of structurally related analogs. As appears from above MIPs have sofar been prepared in the form of continuous blocks that need to be crushed and sieved before use. This results in a low yield of irregular particles, a high consumption of template and a material exhibiting low chromatographic efficiency. There is therefore a need for MI -materials that can be prepared m high yield m the form of regularly shaped particles with low size dispersity and a controlled porosity. These are expected to be superior in terms of mass transfer characteristics and sample load capacity compared to the materials obtained from the monolithic approach. Such MIPs have been previously prepared through sus- pensιon(10, 11)- polymerisation techniques, dispersion polymerisation (12) or precipitation polymerisation (13) . This resulted in spherical particles of a narrow size distribution. These procedures have the limitation of being very sensitive to small changes m the manufacturing conditions and the type of solvents and polymerisation conditions that can be applied. Thus the procedures need careful optimization for each new template target which significantly reduces the usefulness of this route. Moreover conditions leading to low dispersity spherical particles may not be compatible with conditions leading to high selectivity and affinity for the template target. An alternative to this procedure is the coating of preformed support materials. (14-16) MIPs have been prepared as grafted coatings on oxide supports (14, 16) on organic polymer supports (15) and on the walls of fused silica capillaries (17-19) . The former technique allows the use of the wide variety of oxide support materials available with different sizes and porosities. Grafting techniques to prepare organic polymer coatings are expected to be generally applicable to molecular imprinting since the structure of the underlying support is already fixed. Thus compared to the large number of factors influencing the end result m suspension or precipitation type polymerisations a smaller number of factors is likely to influence the end result m the preparation of the imprinted coatings. This will make the grafted coatings techniques less sensitive to changes m conditions offering a more robust method. These types of coating tech- niqes are furthermore applicable to modify surfaces of monolithic type supports or microchips prepared by lithographic techniques. The oxide based materials are rigid porous supports with a limited inner pore volume. An alternative support that could potentially carry more grafted imprinted polymer per unit weight and thus allow a higher density of imprinted sites would be to make use of swellable organic resins. In this context Merrifield resins containing grafted initiator or monomer could be used. Sofar most imprinted coatings have been prepared by grafting polymers to the various surfaces. Thus the surface contains prior to polymerisation polymerizable double bonds that can add to the growing polymer chains m solution linking them to the surface. The problem with this technique is the presence of initiator m solution requiring the monomer mixture to be applied as a liquid thin film on the surface prior to polymerisation. Thus the exact amount of monomers that will coat the available surface with an up to ca 100 A thick liquid film is dis- solved together with initiator m an excess of solvent. Thereafter the modified support is added and the solvent evaporated to leave the monomer film and initiator on the surface. Polymerisation is then carried out usually at elevated temperatures. With this procedure the thickness of the polymer layer is difficult to control and capillary forces upon evaporation of solvent may cause incomplete wetting of the surface. Moreover a continuous method of synthesismg the particles is difficult to envisage with this method. A considerable improvement m this regard would be to confine the initiator radicals to the support surface (Fig. 2) . (20, 21) In absence of chain transfer this would lead to chain growth occurmg only from the surface of the support with no polymerisation occurmg m solution. For molecular imprinting this would have important consequences. For instance the polymerisation can be carried out on the surface of initiator modified support particl- es suspended m a mixture of the monomers and solvent . This would allow polymerisation in a simple tank reactor by either thermal or photochemical initiation. The latter technique would allow the particles to be modified during the sedimentation possibly leading to a continuous method for preparing the imprinted composite particles (Fig. 3) . Polymerisation would here only occur on the particle surface leaving the solution containing the monomers unre- acted. The monomer solution can thus be reused for the coating of several batches of particles. The problem of confining polymer chain growth to the support surface and supress it in solution can be solved by attaching the radical initiator so that the radical formed upon bond homolysis remains bound to the surface. Alternatively the radical formed that is not attached to the surface should undergo rapid reaction to give an unreactive species. It should be possible to prepare the grafted coatings using monomers such as those based on styren/divmylbenzene, methacrylates, acrylates, acrylamides and m the presence of one or more template molecules. Summary of the Invention Thus, the present invention relates to a molecularly imprinted polymer obtainable by polymerising a composition comprising at least one monomer, and a template, on a support m a polymerisation medium with a free radical initiator, whereafter the template is removed from the molecularly imprinted polymer obtained, said polymerisation being confined to the surface of the support. The invention further relates to a method for preparing a molecularly imprinted polymer which comprises polymerising a composition comprising at least one monomer, and a template, on a support in a polymerisation me- dium with a free radical initiator, whereafter the template is removed from the molecularly imprinted polymer obtained, said polymerisation being confined to the surface of the support . Still further the invention relates to the use of a molecularly imprinted polymer as defined above in chromatography, for separations, in chemical sensors, m molecular recognition as stationary phase m capillaries, m selective sample enrichment or m catalysis. These and other advantages and characterising fea- tures of the present invention will appear from the following specification and the appended claims. Brief Description of the Drawings Fig. 1 illustrates molecular imprinting with L- phenylalamne anilide (L-PA) . Fig. 2 illustrates the procedure of confining initiator radicals to the surface of a support Fig. 3 illustrates a method for preparing imprinted composite particles. Fig. 4A illustrates the use of a presynthesized azo- silane initiator where both ends may be attached to the surface of a support . Fig. 4B illustrates an initiator that may be pread- sorbed on a support surface and that is insoluble m the monomer containing solution. Fig. 4C illustrates the use of microwaves to selectively heat the particle surface. Fig. 4D illustrates the use of miferters such as dithiocarbamate coupled onto the surface. Detailed Description of the Invention The invention will now be described m more detail with reference to a number of non-limitmg examples: The invention refers to a material that consists m a support (porous or nonporous material or planar surface) coated with a polymer layer, a method for its fabrication and use of said material m for instance chroma- tography, for separations, m chemical sensors, m selective sample enrichment, m molecular recognition as stationary phase in capillaries or m catalysis. The material is prepared by grafting a polymer layer on the surface of a preformed organic or inorganic support material or surface. The grafting can be combined with the technique of molecular imprinting. In one embodiment of the present invention the polymerisation is confined to the surface of the support by confining the free radical initiator to the support. Ac- cording to one aspect the free radical initiator is bound (covalently or non-covalently such as e.g. by hydrogen bonds) to the surface of the support. According to another aspect the free radical initiator is adsorbed to the surface of the support, preferably by dissolving it m a solvent for the free radical initiator, applying the solution to the support, and removing the solvent, said free radical initiator being insoluble m the polymerisation medium or remaining attached to the support surface by adsorptive forces. In another embodiment of the present invention the polymerisation is confined to the surface of the support by subjecting the composition, the support and the free radical initiator to microwave irradiation which selectively heats the support and thereby initiates a polymeπ- sation reaction at the surface of the support. In a further embodiment of the present invention the polymerisation is repeated at least once with a different composition to obtain at least one further layer of molecularly imprinted polymer. This allows the manufacturing of layered surfaces containing one or more imprinted layers using possibly different templates and layers of different polarity or other functional properties. The support used in the present invention is preferably selected from the group consisting of porous and non-porous, planar and non-planar inorganic and organic supports. As examples of such support materials may be mentioned oxides such as alumina and silica, and organic resins in the form of particles such as spheres, or sheets . The template used in the present invention may be any molecule or ion and is preferably selected from the group consisting of organic or inorganic molecule entities, ions, antibodies, antigens, amino acids, peptides, proteins, nucleotides, DNA-bases, carbohydrates, drugs, pesticides, and derivatives thereof, etc. The expression "polymerisation medium" as used her- ein means a liquid medium in which the polymerisation is carried out. The polymerisation medium may e.g. be a solvent in which the monomers are soluble. It may also be a monomer acting as a solvent for the other components of the polymerisable composition. The support surface is prepared as follows. A free radical initiator is bound to the surface either covalently or noncovalently so that the free radicals generated upon initiation remain confined to the surface or vicinity of the surface. The absence of polymer propaga- tion in solution will lead to a higher accessibility of the monomers at the surface. Furthermore this method will allow the tuning of the thickness of the polymer layer. Surface attachment of a free radical initiator has been disclosed generally by Guyot et.al. (21) and Tsubokawa et.al. (22, 23) It relies on presilanization of the surface using 3 -aminopropyltriethoxysilane or a gly- cidoxypropylsilane (GPS) followed by reaction of the amino groups or the epoxy groups with an azoinitiator such as azo-bis (cyanopentanoic acid, ACPA) leading to the formation of an amide (using DCC as condensing reagent) or ester link between the surface and the azoinitiator. Also peroxy initiators may be used although better re- suits are obtained using the grafted azoinitiator followed by photochemical initiation. High yields of grafted polymer are obtained using silica reacted with toluene- 2 , 4 -diisocyanate (TDI) followed by reaction with ACPA. Example 1 Coupling of initiator to ammo, epoxy or chloromethyl modified supports or resins Epoxy and chloromethyl modified supports: A typical example is as follows. Into a flask, 3 g of epoxy modi- fied particles 50 mL of DMSO, 0.5 g of ACPA and picolme were charged. The reaction mixture was stirred for 5 h at 50°C. After the reaction the particles were washed with methanol and dried. Ammo modified supports: A typical example is as follows. Into a flask, 3 g of epoxy modified particles 50 mL of DMF, 0.5 g of ACPA and dicyclohexyldicarbodi- lmide (DCCI) and base were charged. The reaction mixture was stirred for 5 h. After the reaction the particles were washed with methanol and dried. The above procedure does not confine all initiator radicals to the surface since the initiator is bound at only one position. This invention describes three alternative procedures to confine the polymerisation to the surface . 1 The use of a presynthesized azosilane (Fig. 4A) . This will more likely lead to a two point attachment of the initiator to the surface. Example 2 Synthesis of azosilane for two point coupling of an azo- initiator to a surface or support The azosilane was synthesized by mixing 0.5 mole glycidoxypropyltπmethoxysilane (GPS) and 0.25 mole ACPA m 200 mL isopropanol and catalytic amounts of picolme. The reaction was allowed to continue at room temperature and the product isolated by evaporation to dryness followed by purification by column chromatography giving the product m 60 % yield. Example 3 Coupling of silane to a surface The silane was coupled by reaction m water at low temperature (20°C) for 24 hours. 2. Preadsorbtion of an initiator that is insoluble in the monomer containing solution. Thus, a polar water soluble initiator as for instance an azo-bis-amidine, (24) can be adsorbed to the surface from aqueous solvent, the surface dried and then the polymerisation initiated as described above (Fig. 4B) . The free radicals generated from the initiator will stay associated to the surface due to their insolubility m the monomer mixture. Example 4 Adsorption of amidmeazomitiator to a support surface An amidmeazomitiator such as 2 , 2 ' -azobis (N,N' - dimethyleneisobutyramidme) or 2 , 2 ' -azobis (2-amidmo- propane) is dissolved m methanol/water and support par- tides such as silica are added. After several hours of equilibration the solvent is removed by filtration and the particles dried under vacuum. 3. Use of microwaves to selectively heat the particle surface (Fig. 4C) . Example 5 Microwave initiated polymerisation Particles are added to a solution of monomers and initiator m a suitable solvent. The polymerisation is initiated by microwave irradiation at a wavelength caus- mg local heating of the particles only. . Use of miferters such as dithiocarbamate coupled onto the surface (Fig. 4D).(25) (The term "miferter" is an abbreviation for "initiator + transfer agent + terminator" ) . Example 6 Synthesis of support or polymeresm bound initiator To a surface or polymer containing bound chloromethyl groups is given N,N-dιethyldιthιocarbamate m solution and the reaction allowed to proceed at elevated temperatures . Example 7 Synthesis of block-graft imprinted copolymer Particles or a surface containing bound dithiocarba- mate groups are/is added to a mixture of monomers (concentration about 5 moles/litre) , template and solvent under nitrogen. The polymerisation was initiated by irradiation with an ultrahigh pressure mercury UV lamp and allowed to proceed for a certain time. Then the unreacted monomers and template were washed away. The obtained particles or surface can then be immersed in another solution containing another monomer and the procedure repeated. This allows the manufacturing of layered surfaces containing one or more imprinted layers using possibly different templates and layers of different polarity or other functional properties. Example 8 Endcappmg of unreacted silanol groups Prior to polymerisation endcappmg of unreacted si- lanol groups can be done. Hexamethylsilazane is here effective. Good wetting is critical for the formation of a homogenous layer fully covering the support. Another possibility to enhance the wetting is to use organosilan- es containing functionalities resembling solvents known to be good solvents for the methacrylate polymerisations. Among these chlorinated hydrocarbons are particularly useful . Grafting of polymer layer The polymerisation can be carried out m a stirred suspension of the particles the monomer mixture since growth only takes place on the surface (see Fig. 3) . Thus the initiator modified particles are added to a monomer containing solution and solvent and possibly a template and the suspension stirred. The polymerisation is then carried out photochemically or thermally. The particles can be based on any inorganic or organic sup- port material and the template on any molecule or ion dissolved in the monomer mixture solution. The grafting can also occur on other surfaces such as those generated by lithographic processes or on the walls of capillaries or fibres. The thickness of the polymer layer is tunable by varying the time of reaction. Example To a stirred solution of 38 ml (0.2 mole) EDMA, 3.4 ml (40 mmole) MAA and 10 mmole terbutylazine (or no template) in 56 ml dichloromethane is added 5 g of any of the initiator modified particles described in Examples 1- 6. The suspension is sparged with nitrogen and the polymerisation initiated by UV irradiation using a standard high pressure mercury lamp at 15°C or by heating to a temperature providing a suitable rate of polymerisation. The suspension is stirred under nitrogen and UV irradiation or heating for 24 h and the particles then filtered, washed and dried under vacuum. The monomer mixture is then used to modify a second batch of particles. The resulting particles exhibit high selectivity and affinity for the template, terbutylazine. LITTERATURE I. Wulff, G. 1995. Angew. Chem., Int. Ed. Engl. 34: 1812-32 2. Bartsch, R. A., Maeda, M. 1998. In ACS Symposium Series 703. Washington: Oxford University Press 3. Mosbach, K. 1994. Trends Biochem. Sci. 19: 9-14 4. Cowie, J. M. G. 1991. Polymers: Chemistry & Physics of modern materials. Glasgow: Blackie and Son Ltd. 5. Sellergren, B., Lepistoe, M., Mosbach, K. 1988. J. Am. Chem. Soc. 110: 5853-60 6. Sellergren, B., Shea, K. J. 1993. J. Chroma togr . 635: 31 7. O'Shannessy, D. J., Ekberg, B., Mosbach, K. 1989. Anal. Biochem. Ill: 144-9 8. Sellergren, B. 1989. Makromol . Chem. 190: 2703- 11 9. Snyder, L. R., Kirkland, J. J. 1979. Jntroduction to Modern Liquid Chromatography. US: Wiley 10. Mayes, A. G., Mosbach, K. 1996. Anal. Chem. 68: 3769-3774 II. Matsui, J., Okada, M., Tsuruoka, M., Takeuchi , T. 1997. Anal. Commun. 34: 85-87 12. Sellergren, B. 1994. J " . Chro atogr. A. 673: 133-141 13. Lei, Y., Cormack, P. A. G., Mosbach, K. 1999. Anal . Commun. 36: 35-38 14. Wulff, G., Oberkobusch, D., Minarik, M. 1985. React. Polym. , Ion Exch. , Sorbents . 3: 261-75 15. Glad, M., Reinholdsson, P., Mosbach, K. 1995. .React. Polym. 25: 47-54 16. Arnold, F. H., Plunkett, S., Dhal , P. K. , Vidyasankar, S. 1995. Polym. Prepr . 36(1) : 97-8 17. Schweitz, L., Andersson, L. I., Nilsson, S. 1997. Anal. Chem. 69: 1179-1183 18. Brϋggemann, 0., Freitag, R. , Whitcombe, M. J., Vulfson, E. N. 1997. J " . Chromatogr. 781: 43-53 19. Lin, J.-M., Nakagama, T., Uchiyama, K. , Hobo, T. 1997. J. Liq. Chromatogr. Relat. Technol. 20: 1489- 1506 20. Carlier, E., Guyot , A., Revillon, A. 1991. React. Polym. 16: 115 21. Carlier, E., Guyot, A., Revillon, A. 1992. .React. Polym. 18: 167 22. Tsubokawa, N. , Kogure , A., Maruyama, K. , Sone, Y., Shimomura, M. 1990. Polym. J. 22: 827-833 23. Tsubokawa, N. , Shirai, Y., Tsuchida, H., Handa, S. 1994. J " . Polym. Sci. A: Polym. Chem. 32: 2327-2332 24. Dekking, H. G. G., 1965, J " . Appl. Polym. Sci. 9, 1641-1651 25. Nakayama, Y . ; Matsuda, T. 1999, Langmuir, 15, 5560-5566.

Claims: CLAIMS 1. A molecularly imprinted polymer, c h a r a c - t e r i s e d m that it is obtainable by polymerising a composition comprising at least one monomer, and a template, on a support in a polymerisation medium with a free radical initiator, whereafter the template is removed from the molecularly imprinted polymer obtained, and that said polymerisation is confined to the surface of the support. 2. A molecularly imprinted polymer according to claim 1, wherem the polymerisation is confined to the surface of the support by confining the free radical initiator to the support. 3. A molecularly imprinted polymer according to claim 2, wherem the free radical initiator is bound or adsorbed to the surface of the support . 4. A molecularly imprinted polymer according to claim 1, wherein the polymerisation is confined to the surface of the support by subjecting the composition, the support and the free radical initiator to microwave irradiation which selectively heats the support and thereby initiates a polymerisation reaction at the surface of the support . 5. A molecularly imprinted polymer according to any one of claims 1-4, wherem the polymerisation is repeated at least once with a different composition to obtain at least one further layer of molecularly imprinted polymer 6. A molecularly imprinted polymer according to any one of claims 1-5, wherem the support is selected from the group consisting of porous and non-porous, planar and non-planar inorganic and organic supports. 7. A molecularly imprinted polymer according to any one of claims 1-6, wherein the template is selected from the group consisting of organic or inorganic molecule entities, ions, antibodies, antigens, ammo acids, pep- tides, protems, nucleotides, DNA-bases, carbohydrates, drugs, pesticides, and derivatives thereof. 8. A method for preparing a molecularly imprinted polymer c h a r a c t e r i s e d by polymerising a com- position comprising at least one monomer, and a template, on a support m a polymerisation medium with a free radical initiator, whereafter the template is removed from the molecularly imprinted polymer obtained, said polymerisation being confined to the surface of the support. 9. A method accordmg to claim 8, wherem the polymerisation is confined to the surface of the support by confining the free radical initiator to the support. 10. A method according to claim 9, wherem the free radical initiator is bound or adsorbed to the surface of the support. 11. A method according to claim 8, wherem the polymerisation is confined to the surface of the support by subjecting the composition, the support and the free radical initiator to microwave irradiation which selec- tively heats the support and thereby initiates a polymerisation reaction at the surface of the support. 12. A method according to any one of claims 8-11, where the polymerisation is repeated at least once with a different composition to obtain at least one further layer of molecularly imprinted polymer. 13 Use of a molecularly imprinted polymer accordmg to any one of claims 1-7, or prepared according to any one of claims 8-13, m chromatography, for separations, chemical sensors, molecular recognition as station- ary phase capillaries, m selective sample enrichment or m catalysis

Inventors: RUECKERT BAERBEL, SELLERGREN BOERJE, SULITZKY CLAUDIA, RUECKERT, BAERBEL, SELLERGREN, BOERJE, SULITZKY, CLAUDIA
Applicants: MIP TECHNOLOGIES AB, RUECKERT BAERBEL, SELLERGREN BOERJE, SULITZKY CLAUDIA, RUECKERT, BAERBEL, SELLERGREN, BOERJE, SULITZKY, CLAUDIA
Application year: 2000
Main classification: C08F291
IPC codes: B01D15, B01J20, C08F2, C08F285, C08F291, C08F292