DIELECTRIC FILMS FROM ORGANOHYDRIDOSILOXANE RESINS

Abstract: A method of making a dielectric film on a substrate from a composition containing an organohydridosiloxane resin is presented. The organohydridosiloxane resins have a cage conformation. The process of making a dielectric film includes forming a solution of a solvent and the organohydridosiloxane resin, dispensing the solution on a substrate, spinning the substrate, baking the substrate to remove the solvent, and curing the substrate to form the dielectric film. Dielectric films of the present invention exhibit dielectric constants of approximately 3.0 or lower.

Description: DIELECTRIC FILMS FROM ORGANOHYDRIDOSILOXANE RESINS BACKGROUND Field of the Invention The present invention relates generally to dielectric films formed from siloxane based resins and methods of manufacturing those films, and more specifically to low dielectric constant films formed from high organic content organohydridosiloxane compositions and methods of manufacture thereof. Related Art Semiconductor devices often have one or more arrays of patterned interconnect levels that serve to electrically couple the individual circuit elements thus forming an integrated circuit (IC) . These interconnect levels are typically separated by an insulating or dielectric film. Previously, a silicon oxide film formed using chemical vapor deposition (CVD) or plasma enhanced CVD (PECVD) techniques was the most commonly used material for such dielectric films. However, as the size of circuit elements and the spaces between such elements decreases, the relatively high dielectric constant of such silicon oxide films is problematic. In order to provide a lower dielectric constant than that of silicon oxide, dielectric films formed from siloxane based resins are becoming widely used. One such family of films formed from siloxane based resins are the films derived from hydrogen silsesquioxane (HSQ) resins (See, U.S. Pat. No. 3,615,272, Oct. 19, 1971, Collins et al.; and U.S. Pat. No. 4,756,977, Jul . 12, 1988, Haluska et al . ) However, while such films do provide lower dielectric constants than CVD or PECVD silicon oxide films and also provide other benefits such as enhanced gap filling and surface planarization, it has been found that typically the dielectric constants of such films are limited to approximately 3.0 or greater (See, U.S. Pat. No. 5,523,163, Jun. 4, 1996, Ballance et al.). Since, as known, the dielectric constant of such insulating films is an important factor where IC's with low power consumption, cross-talk, and signal delay are required, forming an insulating film with a dielectric constant below 3.0 is desirable. As siloxane based resin materials have beneficial gap filling and planarization properties, forming such films from siloxane based resin materials is very desirable. In addition, it would be desirable to have low dielectric constant films formed from siloxane based resin materials which have a high resistance to cracking. Additionally, it would be desirable to manufacture low dielectric constant films from siloxane based resins via standard processing techniques. In this manner curing processes that require an ammonia or ammonia derivative type of atmosphere (See, U.S. Patent No. 5,145,723, Sep. 8, 1992, Ballance et al.), an ozone atmosphere (See, U.S. Patent No. 5,336,532, Haluska et al.), or other non-standard type of semiconductor process, are avoided. SUMMARY In accordance with the present invention, methods of using solutions of organohydridosiloxane resins of high organic content to manufacture low dielectric constant insulating films are provided. The solutions from which the dielectric films in accordance with the present invention are formed, contain organohydridosiloxane resins having one of the four general formulae: [HSiOι. 5 ] n [RSiOι. 5 ] m ; or Formula 1 [Ho.4-i.oSiOi.5-i.8ln [Ro.4-1.oSiOi .5-ι.8J rrJ or Formula 2 [Ho-i.oSiOi.5-2.oln [RSiOι. 5 ] m ; or Formula 3 [HSi0 1 . ] x [RSiOι. 5 ] y [Si0 2 ] z Formula 4 wherein: the sum of n and m is from about 8 to about 5000; the sum of x, y and z is from about 8 to about 5000; and R is selected from substituted and unsubstituted groups including normal and branched alkyl groups, cycloalkyl groups, aryl groups, and mixtures thereof. A specific Mol % of organic or carbon containing substituents in the resins of Formulae 1-4 is a function of the ratio of the amounts of starting materials . Embodiments of the present invention employ solutions containing organohydridosiloxane resins having a caged structure. These organohydridosiloxane resins have a polymer backbone encompassing alternate silicon and oxygen atoms. In particular, each backbone silicon atom is bonded to at least three backbone oxygen atoms. Some embodiments in accordance with the present invention employ spin coating techniques for application of solutions of the organohydridosiloxane resins. Typically, such resin solutions are approximately 5% to 35% (by weight) resin in an appropriate solvent. In certain embodiments of the present invention, dielectric films formed from organohydridosiloxane resin solutions by spin coating methods are provided. Such dielectric films advantageously have low dielectric constants, typically less than 3.0. Films with greater than 40 Mol% organic substituents typically have dielectric constants less than 2.8. DETAILED DESCRIPTION As the present invention is described with reference to various embodiments thereof, it will be understood that these embodiments are presented as examples and not limitations of this invention. Thus, various modifications or adaptations of the specific materials and methods may become apparent to those skilled in the art. All such modifications, adaptations or variations that rely upon the teachings of the present invention as illustrated by the embodiments herein, are considered to be within the spirit and scope of the present invention. Methods of forming dielectric films from solutions containing organohydridosiloxane resins are provided according to embodiments of the present invention. The solutions contain organohydridosiloxane resins having one of the four general formulae: [HSiOι. 5 ] n [RSiOi. 5 ] m ; or Formula 1 [Ho.4-i.oSiOi.5-i.8jn [Ro.4-i.oSiOi.5-1.8] m r or Formula 2 [Ho-i.oSiOi.5-2.oln [RSiOι. 5 l m ; or Formula 3 [HSiOι. ] x [RSiOι. 5 ] y [Si0 2 ] z Formula 4 wherein: the sum of n and m is from about 8 to about 5000; the sum of x, y and z is from about 8 to about 5000; and R is selected from substituted and unsubstituted groups including normal and branched alkyl groups, cycloalkyl groups, aryl groups, and mixtures thereof; and The specific Mol % of organic or carbon containing substituents in the resins of Formulae 1-4 is a function of the ratio of the amounts of starting materials. In some embodiments, particularly favorable results are obtained with the mole percent of organic substituents being in the range of between about 40 Mol % to about 80 Mol %. In other embodiments, favorable results are obtained with the mole percent of organic substituents being in the range of between about 5 Mol % to about 25 Mol %. For substituent R a methyl group, these ranges correspond to a carbon content of the organohydridosiloxane resin of between about 8% and about 14%, or between about 1% and about 6% by weight, respectively. The organohydridosiloxane resins used in making dielectric films, according to embodiments of the present invention, can have molecular weights between about 400 and 200,000 atomic mass units. Preferably the resins have molecular weights between about 1000 and 100,000 atomic mass units, more preferably between about 10,000 and 60,000 atomic mass units, and most preferably between about 20,000 and 40,000 atomic mass units . The organohydridosiloxane resins used in making the dielectric films are further described in PCT International Applications WO 98/47944 and WO 98/47945, published 29 October 1998, which are commonly assigned with the present application and incorporated herein by reference Methods of the present invention typically employ spin coating techniques for application of films containing organohydridosiloxane resins. As one of ordinary skill in the art knows, semiconductor substrates are currently available in a variety of sizes ranging from as small as three or four inches in diameter to as large as twelve inches in diameter. Therefore, it will be understood that the process parameters presented hereinafter are for a four inch or six inch wafer and are for illustrative purposes only. Thus, modifications to the volume of material, solution concentration, rotational speeds or the various times described below are appropriate for any specific application. It will be further understood, therefore, that all such modification are within the scope and spirit of the present invention. A solution of organohydridosiloxane resin is prepared by combining the resin with an appropriate solvent. Typically, such resin solutions are approximately 5% to 35% (by weight) resin. Advantageously, methyl isobutyl ketone (MIBK) , heptane, dodecane, butyl ether, butyl acetate, isobutyl acetate, propyl acetate or a blend of hexamethyldisiloxane, octamethyltrisiloxane, and octamethylcyclotetrasiloxane, or combinations thereof are useful as solvents, although other appropriate solvents may also be employed. Prior to use, the solvents are preferably dried over 3A or 4A molecular sieves. The resulting solution is then filtered under ambient conditions via any of the filtration devices well known in the art. It is generally preferable to use a filtration device having a pore size less than about 1 μm. A typical filtration process uses a pore size of about 0.1 μm. In the spin coating process, the organohydridosiloxane resin solution prepared in the manner described above is dispensed onto a wafer at or near its center. In some embodiments, the wafer will remain stationary during the dispense cycle, while in some embodiments, the wafer will turn or spin at a relatively low speed, typically less than about 500 revolutions per minute (rpm) . The dispense cycle is followed by a short rest period and then additional spins, hereinafter referred to as thickness spins, generally between approximately 2000 and 3000 rpm, although other spin speeds may be used, as appropriate. Once the coating process, as described above, is completed, the coated substrate, that is the substrate coated with the resin solution, is heated to effect a bake process and a subsequent cure process. The bake process removes the solvent from the resin solution on the substrate, causes the polymer to flow, and begins the conversion of the coating to the dielectric film. The cure process completes the conversion of the coating to the dielectric film. Any conventional apparatus known in the art can be employed for these processes. Preferably, the apparatus for the bake process is an integral part of a spin coating apparatus used for coating the substrate or wafer, although a separate apparatus for curing coatings applied in accordance with embodiments of the present invention is also suitable. The bake process can be carried out in an inert atmosphere such as an atmosphere of an inert gas, nitrogen, or nitrogen/air mixture. One commonly employed heating apparatus employs one or more "hot plates" to heat the coated wafer from below. The coated wafer is typically heated for up to about 120 sec at each of several hot plates at successively higher temperatures. Typically, the hot plates are at temperatures between about 70°C and 350°C. One typical process employs a heating apparatus having three hot plates. First, the wafer is baked for about 60 sec at 150°C. Then the wafer is transferred to a second hot plate for an approximately 60 sec bake period at 200°C. Finally, the wafer is transferred to a third hot plate for a third bake period of approximately 60 sec at 350°C. A final cure process is preferably employed to complete the curing of the film. The cure is preferably performed in an inert atmosphere, as described above for the bake process. This final cure process can employ a conventional thermal curing apparatus, for example a horizontal furnace with a temperature range of about 300 °C to about 450 °C and preferably from about 375°C to about 425°C. In a typical furnace cure process, the baked wafer is cured for 30 minutes to one hour at 400 °C at a nitrogen flow rate of 4 liters/min to 20 liters/min. Alternatively, the cure process can employ a high- temperature hot plate curing module which has an oxygen-density-controlled environment. In this process, the baked wafer is cured on a hot plate at a temperature between about 400°C and 450°C for a period of from about 1 to about 15 minutes in a nitrogen or inert atmosphere with an oxygen density of less than about 100 parts per million. For example, a suitable cure atmosphere is achieved with a nitrogen flow rate of between about 10 and about 30 liters/min. It will be understood that the above bake and cure processes were described for illustrative purposes only and that other temperatures, durations, and number of bake cycles can be employed, where appropriate. The thickness of the resulting dielectric film on a substrate depends on a number of variables. The variables include, organic content of the organohydridosiloxane resin, type of substituent in the resin, solvent properties, resin molecular weight, percentage of the resin solids in the resin solution, the amount of resin solution dispensed onto the substrate, and the speed of the thickness spin. The higher the percentage of resin solids in the solution, the thicker the resulting dielectric film. Conversely, the higher the speed of the thickness spin, the thinner the resulting dielectric film. In addition, the thickness of the dielectric film can depend on the nature and amount of the organic constituents in the organohydridosiloxane resin. According to embodiments of the present invention, dispensing 2 ml of resin solution that is between about 5 % and about 35 % resin by weight on a 4 inch wafer, using a spin speed between about 2000 and about 3000 rpm, results in dielectric films ranging from about 1000 A to about 9000 A in thickness. Variation in thickness, determined by independent measurements on a single wafer, ranges from about 0.4 % to 6 % and preferably the variation in thickness is less than 1 %. In certain embodiments of the present invention, dielectric films formed from organohydridosiloxane resin solutions by spin coating methods are provided. The dielectric films are formed from solutions of organohydridosiloxane resins having a mole percent of organic substituents preferably in the range between about 40 Mol % and about 80 Mol % . and in the range between about 5 Mol % and about 35 Mol %. As demonstrated in the examples below, such dielectric films advantageously exhibit low dielectric constants, typically approximately 3.0 or lower. In addition, the films exhibit adhesion to semiconductor substrates of greater than about 8 kpsi. The following characteristics encompass non- limiting measurements that illustrate the properties of films of organohydridosiloxane polymer resins of the present invention. The methods of measurement used are as follows: 1) Film Thickness (A) : Film thickness is measured using a calibrated Nanospec® AFT-Y CTS-102 model 010-180 Film Thickness Measurement System available from Nanometrics, Co. An average of measurements at five locations on a wafer are reported as the film thickness for each sample. Thickness measurements are corrected for the refractive index as measured on a Rudolph ellipsometer. 2) Refractive Index: Refractive index is measured on a Rudolph Research AutoEL ellipsometer using a wavelength of 633.3 nm. 3) Dielectric Constant: Dielectric constant is determined using the capacitance-voltage ("CV") measurement technique and employs a Hewlett-Packard Model 4061A semiconductor measurement system at a frequency of 1 MHz. This test procedure employs a metal-insulator-metal (MIM) structure with the thickness of each layer ranging from about 0.5 to 1 micron (μm) . 4) Solution Viscosity (cP) : A Brookfield Synchro-lectric Viscometer, Model LVT 62238 is employed to measure the viscosity of organohydridosiloxane resin solutions at ambient temperature. 5) Isothermal TGA: Cured films are carefully removed from the wafers, heated to 100°C and held for one hour to equilibrate before recording initial weight. The instrument is then ramped from 100°C to 425°C at 25°C per minute (under nitrogen atmosphere) and held at 425°C for four hours to determine percent weight loss . 6) Planarization: Polymer films are spun on silicon wafers patterned with line and space patterns of varying widths (0.35 - 3.0 μm) . The wafers are baked and cured using the appropriate recipe. The cured wafers are then cleaved horizontally across the pattern of lines and this cross-section is examined using a scanning electron microscope (SEM) . The degree of planarization for a particular line and space width is calculated by measuring the ratio of the highest point of the film versus the lowest point. 7) Stress : Film stress is measured using a Flexus™ model 2410 Film Stress Measurement System available from Tencor Instruments using standard methods . 8) Crack Threshold: A single coat film is spun, baked, and cured on a bare silicon wafer using the appropriate recipe in 1000A thickness increments. The wafers are examined 24-48 hrs following cure to check for cracking. Example 1 Methyl isobutyl ketone (MIBK) (127.4 g) was dried over 4A molecular sieves and combined with 28 g of 80 Mol % methylhydridosiloxane resin, which contains approximately 14% carbon, as measured by Rutherford back scattering, to form an 18 weight % resin solution. The solution was filtered to 0.2 μm. The solution was coated on a bare 4 inch silicon wafer using a conventional spin coater. Approximately 3 ml of the polymer solution was placed on the wafer. After a 3 second delay, the wafer was spun at 2000 rpm for 20 seconds. The coated wafer was baked on three successive hot plates for one minute each at 150°C, 200°C, and 350°C, respectively. The baked wafer was then cured in a nitrogen atmosphere in a horizontal furnace set initially at 300°C, followed by a ramp to 380°C at a rate of 4°C/minute, where it was held for 10 minutes, then increased to 400°C at a rate of 1°C/minute. The furnace temperature was held at 400°C for one hour and then lowered back to 300°C over a period of about 2 hours. Film thickness for Examples 1-6, determined after the bake step and determined again after the cure step, corrected for refractive index, is given below in Table 1. Example 2 A siloxane solvent blend (hexamethyldisiloxane, octamethyltrisiloxane, and octamethylcyclotrisiloxane) (57.4 g) was dried over 4A molecular sieves and combined with 12.6 g of 80 Mol % methylhydridosiloxane resin to form an 18 weight % resin solution. The solution was filtered to 0.2 μm. Approximately 3 ml of the polymer solution was placed on a bare 4 inch silicon wafer. After a 3 second delay, the wafer was spun at 3000 rpm for 20 seconds. The coated wafer was baked on three successive hot plates for one minute each at 150°C, 200°C, and 350°C, respectively. The baked wafer was then cured in a nitrogen atmosphere in a horizontal furnace set initially at 300°C, followed by a ramp to 360°C at a rate of 4°C/minute, where it was held for 5 minutes, then increased to 380°C at a rate of l°C/minute. The furnace temperature was held at 380°C for 30 minutes and then lowered back to 300°C over a period of about 2 hours . Example 3 The siloxane solvent blend as in Example 2 (661.5 g) was dried over 4A molecular sieves and combined with 238.5 g of 80 Mol % methylhydridosiloxane resin to form a 26.5 weight % resin solution. The solution was filtered to 0.1 μm. The solution was dispensed on a silicon wafer, which was spun, baked, and cured as in Example 2. Example 4 40 Mol % methylhydridosiloxane resin (14 g) , which contains approximately 9% carbon, as measured by Rutherford back scattering, was combined with MIBK solvent (63.7 g) to form an 18 weight % resin solution. The solution was dispensed on a silicon wafer, which was spun and baked as in Example 1. The baked wafer was then cured in a nitrogen atmosphere in a furnace set initially at 300°C followed by a ramp to 400°C at a rate of 4°C/minute, held at 400°C for one hour and then lowered back to 300°C over a period of about 2 hours. Example 5 60 Mol % methyl/20 Mol % benzyl hydridosiloxane resin was combined with MIBK solvent to form an 18 weight % resin solution. The solution was dispensed on a silicon wafer, which was spun and baked as in Example 1. The baked wafer was then cured in a nitrogen atmosphere in a furnace set initially at 300°C followed by a ramp to 380 °C at a rate of 4°C/minute, held at 400°C for one hour and then lowered back to 300°C over a period of about 2 hours. Example 6 60 Mol % methyl/20 Mol % chloromethyl hydridosiloxane resin was combined with MIBK solvent to form an 18 weight % resin solution. The solution was dispensed on a silicon wafer, which was spun, baked, and cured as in Example 5. TABLE 1. THICKNESS OF FILMS FROM EXAMPLES 1-6 Example 7 An 18 weight % resin solution of an 80 Mol % methylhydridosiloxane resin in a variety of solvents was spun and baked as described in Example 4. The film thickness after bake, corrected for the refractive index is given below in Table 2. TABLE 2. THICKNESS OF FILMS OF 80 MOL % METHYLHYDRIDOSILOXANE RESIN IN DIFFERENT SOLVENTS Example 8 Resin solutions of 80 Mol % methylhydridosiloxane resin in the siloxane solvent were prepared by the methods of Example 2 (18 weight % resin) and Example 3 (26.5 weight % resin). The solutions were dispensed on a wafer, spun for 20 seconds at speeds between 1000 and 5000 rpm, and baked as given in Examples 2 and 3. Thickness after bake as a function of spin speed is given below in Tables 3 and 4. TABLE 3. THICKNESS OF FILMS OF 80 MOL % METHYLHYDRIDOSILOXANE RESIN IN SILOXANE SOLVENT (18% RESIN) AS FUNCTION OF SPIN SPEED TABLE 4. THICKNESS OF FILMS OF 80 MOL % METHYLHYDRIDOSILOXANE RESIN IN SILOXANE SOLVENT (26.5% RESIN) AS FUNCTION OF SPIN SPEED Example 9 Viscosity of solutions of 80 Mol % methylhydridosiloxane resin in different solvents are given below in Table 5. TABLE 5. VISCOSITY OF SOLUTIONS OF 80 mol % METHYLHYDRIDOSILOXANE RESIN Example 10 Properties of the dielectric films of Examples 1 and 4 are given below in Table 6. TABLE 6. PROPERTIES OF DIELECTRIC FILMS Example 11 Methyl isobutyl ketone (MIBK) (2000. Ig) was dried over 4A molecular sieves and combined with 501. Ig of 20 mol% methylhydridosiloxane resin, which contains approximately 4% to 5% carbon, as measured by Rutherford back scattering, to form a solution. The solution was filtered to 0.1 μm. The solution was coated on six bare silicon wafers using a conventional spin coater. After a 3 second delay, the wafers were spun at speeds ranging from 1000 to 6000 rpm for 20 seconds. Acceleration before the thickness spin and deceleration afterwards were both at a rate of 50,000 rpm/sec. The wafers were baked on three successive hot plates for one minute each at 150°C, 200°C, and 350°C, respectively. The wafers were cured at 400°C for 45 minutes in a horizontal furnace under a nitrogen atmosphere at a flow rate of 14 liters/min. Film thickness as a function of spin speed, determined after the bake step and determined again after the cure step, corrected for refractive index, is given below in Table 7. TABLE 7. THICKNESS OF FILMS FROM SOLUTIONS OF METHYLHYDRIDOSILOXANE RESIN CONTAINING 4-5% CARBON Example 12 Methyl isobutyl ketone (MIBK) (30.5g) was dried over 4A molecular sieves and combined with 10.5g of 20 mol% methylhydridosiloxane resin, which contains approximately 4% to 5% carbon to form a solution. The solution was filtered to 0.2 μm. The solution was coated on a bare silicon wafer using a spin coater. After a 3 second delay, the wafers were spun at 3000 rpm for 20 seconds. Acceleration before the thickness spin and deceleration afterwards were both at a rate of 50,000 rpm/sec. The wafer was baked on three successive hot plates for one minute each at 150°C, 200°C, and 350°C, respectively. Film thickness on the wafer averaged 5907A, corrected for the refractive index of 1.4. Thickness varied by 0.5% over 5 measurements. The wafer was cured at 400°C for 30 minutes in a horizontal furnace under a nitrogen atmosphere at a flow rate of 14 liters/min. Thickness after curing averaged 6178A, corrected for the refractive index of 1.366. Thickness varied by 0.4% over 5 measurements. Example 13 Viscosity of the solutions of Examples 11 and 12, is given below in Table 8. TABLE 8. VISCOSITY OF SOLUTIONS OF METHYLHYDRIDOSILOXANE RESIN CONTAINING 4-5% CARBON Example 14 Polymer solutions were prepared according to the methods of Example 11, using the percentages of methyl subtituent in the methylhydridosiloxane resin listed in Table 9, below. Films were prepared by spinning the polymer solutions onto 6 inch silicon wafers with a 6000 A film of silane oxide deposited on the surface. The spin, bake and cure conditions used were identical to those described in Example 12. Each wafer was cleaved into 15 samples and the adhesion to each sample was measured by the stud pull test in the manner previously described. The values reported are the average of 15 samples tested for each film. In most cases, the adhesion failure occurs at the stud/epoxy interface, which suggests the adhesion at the film/substrate interface is greater than the values reported below. TABLE 9. STUD PULL VALUES FOR FILMS WITH DIFFERENT PER CENT METHYL SUBSTITUENTS Example 15 Methyl isobutyl ketone (MIBK) (63.8g) was dried over 4A molecular sieves and combined with 14.0 g of 20 mol% methylhydridosiloxane resin, which contains approximately 4% to 5% carbon to form a solution. The solution was filtered to 0.2 μm. The solution was coated on two bare silicon wafers using a spin coater. After a 3 second delay, the wafers were spun at 2000 rpm for 20 seconds. Acceleration before the thickness spin and deceleration afterwards were both at a rate of 50,000 rpm/sec. The wafer were baked on three successive hot plates for one minute each at 150°C, 180°C, and 300°C, respectively. Film thickness on the two wafers averaged 4550A, corrected for the refractive index of 1.403. Thickness varied by < 0.7% over 5 measurements on each of two wafers. The wafers were cured at 400°C for one hour in an horizontal furnace under a nitrogen atmosphere at a flow rate of 4 liters/min. Thickness after curing averaged 4688A, corrected for the refractive index of 1.366. Thickness varied by < 1.4% over 5 measurements on each of the two wafers. The dielectric constant of the film after curing was 3.04. Examples 16 through 20 Examples 16 through 20 describe the process of making dielectric films from organohydridosiloxane resins of different organic substituents. The same process of forming a solution, filtering, dispensing, spinning, baking, and curing, as described in Example 15 above was used. One bare silicon wafer was coated in each of Examples 16 through 20. Reported thickness values are the average of five measurements on a single wafer. Results are summarized in Tables 10 and 11, below. TABLE 10. SOLUTIONS OF ORGANOHYDRIDOSILOXANE RESINS Blend of hexamethyldisiloxane, octamethyltrisiloxane, and octamethylcyclotetrasiloxane TABLE 11. PROPERTIES OF DIELECTRIC FILMS As it can be seen, dielectric constants for films according to the present invention were approximately 3.0 or lower. Films with greater than 40 Mol% organic substituents typically have dielectric constants less than 2.8. These values may be compared with the dielectric constant of a film of a previously known hydridosiloxane resin with no organic substituents, cured at 400°C which exhibits a dielectric constant of 3.27. In view of the foregoing, it will be understood that the present invention provides methods of preparing dielectric films of organohydridosiloxane resins. It will be understood these methods of preparing dielectric films employ standard processing techniques of semiconductor fabrication, avoiding use of ammonia, ozone, or other non-standard atmospheres. Further, it will be understood that the present invention additionally includes the dielectric films so produced. These films are advantageously used in semiconductor devices as insulating materials with low dielectric constants.

Claims: WE CLAIM : 1. A method of making a dielectric film on a substrate comprising: forming a solution of a solvent and an organohydridosiloxane resin comprising a polymer having a general formula: [HSiOi.s.n [RSiOi.sJm, or [ Ho. -l.θSiOι.5-1.8] n [ θ .4-1. oSiOl .5-1.8 ] me Or [Ho-i.oSiOi.5_2.oJn [RSiOι. 5 ] m , or [HSiOi.slx [RSiOi.sJy [Si0 2 ] 2 , wherein the sum of n and m is from about 8 to about 5000, the sum of x, y and z is from about 8 to about 5000, and R, in any general formula, is selected from substituted and unsubstituted normal and branched alkyl groups, cycloalkyl groups, substituted and unsubstituted aryl groups, and mixtures thereof; dispensing the solution on the substrate; spinning the substrate to form an organohydridosiloxane resin coated substrate; baking the organohydridosiloxane resin coated substrate to remove any residual solvent, cause said polymer to flow, and partially convert said resin to said dielectric film; and curing the organohydridosiloxane resin coated substrate, wherein said conversion to said dielectric film is completed. 2. The method of Claim 1 wherein baking the coated substrate comprises heating the organohydridosiloxane resin coated substrate at a first bake temperature for a first bake time period. 3. The method of Claim 2 wherein baking the coated substrate further comprises heating the organohydridosiloxane resin coated substrate to a second bake temperature for a second bake time period, said second bake temperature being equal to or higher than said first bake temperature. 4. The method of Claim 3 wherein baking the coated substrate further comprises heating the organohydridosiloxane resin coated substrate to a third bake temperature for a third bake time period, said third bake temperature being equal to or higher than said second bake temperature. 5. The method of Claim 1 wherein curing the coated substrate comprises heating the organohydridosiloxane resin coated substrate on a hot plate to a cure temperature for a cure time period in an oxygen-density-controlled atmosphere. 6. The method of Claim 5 wherein the cure temperature is at least about 400°C; the cure time period is less than or equal to about 15 minutes and the atmosphere is controlled such that the oxygen density is less than about 100 parts per million. 7. The method of Claim 1 wherein the solvent is selected from the group consisting of methyl isobutyl ketone, heptane, dodecane, butyl ether, butyl acetate, isobutyl acetate, propyl acetate, hexamethyldisiloxane, octamethyltrisiloxane, octamethylcyclotetrasiloxane, and combinations thereof. 8. The method of Claim 5 wherein the solvent is dried over molecular sieves with characteristic dimension between about 3 and about 4 A. 9. The method of Claim 1 wherein forming a solution of a solvent and an organohydridosiloxane resin is forming a solution of a solvent and an organohydridosiloxane resin having a cage conformation. 10. The method of Claim 1 wherein forming a solution of a solvent and an organohydridosiloxane resin is forming a solution of a solvent and an organohydridosiloxane resin having a molecular weight of between about 400 and about 200,000 atomic mass units . 11. The method of Claim 10 wherein forming a solution of a solvent and an organohydridosiloxane resin is forming a solution of a solvent and an organohydridosiloxane resin having a molecular weight of between about 1,000 and about 100,000 atomic mass units . 12. The method of Claim 11 wherein forming a solution of a solvent and an organohydridosiloxane resin is forming a solution of a solvent and an organohydridosiloxane resin having a molecular weight of between about 10,000 and about 60,000 atomic mass units. 13. The method of Claim 1 wherein forming a solution of a solvent and an organohydridosiloxane resin is forming a solution of a solvent and an organohydridosiloxane resin comprising R selected from the group consisting of methyl, ethyl, propyl, butyl, t-butyl, pentyl, hexyl, cyclohexyl, phenyl, benzyl, chloromethyl, and mixtures thereof. 14. The dielectric film formed by the method of Claim 1. 15. A dielectric film on a substrate formed by a method comprising: forming a solution of a solvent and an organohydridosiloxane resin comprising a polymer having a general formula: [HSiOi.sJn [RSiOi.slm, or [Ho. -l.θSiOι.5-1.8] n [ Rθ .4-1.oSiOl .5-1.8 ] mr Or [H0-1.0SiO1.5-2.0-n [RSiOι. 5 ] m , or [HSiOi.s.x [RSiOi. 5 ] y [Si0 2 ] z , wherein the sum of n and m is from about 8 to about 5000, the sum of x, y and z is from about 8 to about 5000, and R, in any general formula, is selected from substituted and unsubstituted normal and branched alkyl groups, cycloalkyl groups, substituted and unsubstituted aryl groups, and mixtures thereof; dispensing the solution on the substrate; spinning the substrate to form an organohydridosiloxane resin coated substrate; baking the organohydridosiloxane resin coated substrate to remove any residual solvent, cause said polymer to flow, and partially convert said resin to said dielectric film; and curing the organohydridosiloxane resin coated substrate, wherein said conversion to said dielectric film is completed. 16. The dielectric film of Claim 15, wherein said dielectric film has a dielectric constant of approximately 2.8 or less. 17. The dielectric film of Claim 15, wherein the dielectric film has a carbon content of between approximately 8 % and 14 %. 18. The dielectric film of Claim 15, wherein the dielectric film has a carbon content of between approximately 1 % and 6 % 19. The dielectric film of Claim 15 wherein the organohydridosiloxane resin has a cage conformation. 20. The dielectric film of Claim 15, wherein the dielectric film has a thickness variation over a single substrate of less than approximately 1 %.

Inventors: FIGGE LISA K, HACKER NIGEL P, LEFFERTS SCOTT, SLESSOR MICHAEL D, FIGGE, LISA, K., HACKER, NIGEL, P., LEFFERTS, SCOTT, SLESSOR, MICHAEL, D.
Applicants: ALLIED SIGNAL INC, ALLIEDSIGNAL, INC.
Application year: 2000
Main classification: H01L21
IPC codes: C08G77, H01L21