Method for recovery of terephthalic acid from a material containing poly(ethylene terephthalates)

Abstract: The present invention relates to a method of recovering terephthalic acid from a material containing poly(ethylene terephthalate) (P.E.T.) in the form of bottles, by making said material react, in the absence of water, with a reagent consisting of one or more metal salts of a weaker acid than the terephthalic acid, until a water-soluble compound is obtained, and subsequently carrying out dissolution in water and acidification.

Description: The present invention relates to a method of recovering terephthalic acid from a material containing poly(ethylene terephthalate). In particular, the present invention relates to a method of obtaining terephthalic acid starting from poly(ethylene terephthalate (P.E.T.) materials, for instance in the form of bottles or other manufactured articles coming from a differentiated salvage dump. Known in the art is the existence of some chemical methods involving recovery of terephthalic acid starting from materials containing poly(ethylene terephthalate). Poly(ethylene terephthalate) (P.E.T.) is a saturated polyester resin made from terephthalic acid and ethylene glycol. P.E.T. is widely used in the food-industry packaging sector and in particular in the manufacture of bottles for soft drinks. Due to its large use, an increasingly growing interest in P.E.T. recycling has been developed in the most recent years. Substantially chemical methods for terephthalic acid recovery are distinguishable from each other due to the mechanism used which can belong to one of the following main categories: alcoholysis, glycolysis, acid hydrolysis, neutral hydrolysis and alkaline hydrolysis. Obviously, each individual mechanism can find application through various techniques differing from each other due, for example, to a different number of phases, different temperatures, pressures, involved reagents, reaction solvents. The chemical method utilizing alcoholysis brings to formation of di(alkyl)-terephthalates, whereas glycolysis produces di(hydroxy-alkyl)-terephtalates. Due to difficulties connected with purging of the obtained reaction products, these methods can only apply to materials containing poly(ethylene terephthalate) (P.E.T.) of high purity. Consequently these methods cannot apply if P.E.T. comes from a material obtained through a differentiated salvage dump as in the case of P.E.T. bottles from said differentiated dump. The chemical method utilizing acid hydrolysis is carried out by making the P.E.T. react with a large excess of strong acid in solution, concentrated sulfuric acid for example. The sulfuric acid acts in a very short period of time, say some minutes, at a temperature included between room temperature and 95°C, by dissolving the starting P.E.T. with formation of terephthalic acid (TPA). The chemical method utilizing acid hydrolysis is scarcely applied in the industrial field, mainly due to the high corrosiveness of the reaction system and also dire to the huge amount of salt solution produced for neutralizing the employed acid. The chemical method utilizing neutral hydrolysis is conducted by treating the P.E.T. with water or steam, under pressure at a temperature included between 200 and 300°C, in the presence of appropriate catalysts. This method too has some drawbacks. The main disadvantages of this technology are represented by high energy consumptions and the impossibility of eliminating all mechanical impurities from the terephthalic acid (TPA) obtained by precipitation, such as undissolved particulate matter and insoluble polymers originally present in the starting material. Finally, the chemical method utilizing alkaline hydrolysis is almost always carried out by use of alkaline hydroxides or ammonium hydroxides. Use of these bases leads to formation of aqueous solutions of the corresponding salt of the terephthalic acid (TPA). These solutions can be easily cleared from mechanical impurities by filtering, flocculating or settling processes. In addition, terephthalic acid (TPA) is recovered from said aqueous solutions by precipitation in an acid medium. Of all the above mentioned methods, the method utilizing alkaline hydrolysis has recently found many applications. Some of them are reproduced hereinafter: a first application contemplates treatment of the P.E.T. with a concentrated solution of an alkaline hydroxide, under pressure and at temperatures close to or higher than 250°C. The P.E.T./alkaline solution ratio is greater than 20. a second application contemplates treatment of the P.E.T. with a stoichiometric amount of an alkaline hydroxide in ethylene glycol (EG) at a temperature included between 100 and 200°C. If an ammonium hydroxide is used as the base, the method is carried out under pressure. In both cases, at all events, the obtained reaction mixture is dissolved in water. Finally, a third application provides for the P.E.T. to be extruded in the presence of hydroxide at temperatures higher than 250°C. Subsequently, the obtained salt is dissolved in an aqueous solution. Generally problems resulting from use of alkaline or alkaline-earth hydroxides or from use of concentrated solutions of such hydroxides are well known. For alkaline hydroxides it is meant a sodium hydroxide for example, for alkaline-earth hydroxide it is for example meant a calcium hydroxide. The main disadvantages are connected with difficulties in manipulating these types of very aggressive reagents by operators. In addition, modifications in the plants are required to be adopted together with a series of technical expedients in plant construction due to the big problems connected with corrosion of these reagents, above all if used in solution. In the above first application, disadvantages consist in being obliged to heat, filter and recover great amounts of solution. In addition, in this application use of great amounts of hydroxides and adoption of high pressures is provided. In the above second and third applications, the main disadvantage resides in the fact that it is impossible to obtain terephthalic acid (TPA) free from undesirable yellow-pink colourations. In fact, in the absence of water the hydroxides employed at temperatures higher than 100°C react with the ethylene glycol (EG) resulting from the hydrolysis reaction. The reaction between hydroxides and ethylene glycol brings to formation of strongly red-coloured and water-soluble products. Formation of these coloured compounds prevents precipitation of uncontaminated white TPA. Therefore, the terephthalic acid (TPA) containing coloured impurities must be bleached. Methods described in literature for TPA bleaching are long and expensive. Some methods of bleaching for example involve extraction of impurities by use of water-insoluble higher alcohols. In addition, the above third application requires use of starting material containing P.E.T. in the form of ground, washed and dried scraps, which will involve an increase in the costs of the starting raw material. Document US 5,545,746 relates to method for recovery alkaline metal or alkaline-earth metal terephthalate which comprises the following steps: the initial compound P.E.T. is mixed with an alkali metal or alkaline-earth hydroxide anhydrous, in the absence of solvent; the mixture obtained is heated, in order to stimulate the saponification of P.E.T.; the ethylene glycol formed during the saponification reaction is removed; and the alkali metal or alkaline-earth terephthalate is recovered in the form of a powdery material. A process for removing contaminants from PET components by depolymerizing PET is described in WO 95/27753. It includes a main depolymerization step obtained by transesterification with alkanediols to form a solution containing soluble short-chain PET polymers, recovering the said short-chain polymers and hydrolyzing them at elevated pressure and temperature to form ethanediol solution and crystals of terephthalic acid. Here, again, the disadvantages of using high temperature and pressure are apparent. Document DE 195 34 276, relates to a process for recovery terephthalic acid wherein the starting material containing poly(ethylene terephthalate), for istance waste material in the form of small fragments, is set in a mixer device with molten acetate. After molten potassium acetate KOAc is added at temperature about 150-300 °C and ethylene glycol diacetate and potassium terephthalate are abtained from the reaction. The ethylene glycol diacetate is removed away from the reaction and the potassium terephthalate is acidified with acetic acid in order to separate terephthalic acid. Document DE 196 29 042 relates to a method of obtaining of terephthalic acid and ethylene glycol from waste materials comprising a hydrolytic decomposition of polyester with an aqueous solution of alkaline metal at the increased temperature and under the increased pressure, oxidation and neutralisation of a reaction mixture, separation of the product phases and purification of ethylene glycol by distillation. Another process for recovery of terephthalic acid and ethylene glycol is described in WO 99/28285. This process heats PET in an aqueous solution of bicarbonates of ammonia and alkali metals or ammonium carbamate and urea to obtain a digestion of PET leading to an aqueous solution of terephthalic acid salts which are further processed to give crystallized terephthalic acid and distilled or extracted polyethylene glycol. Document EP 597 751 relates to a method of recovery alkaline metal or alkaline-earth metal terephthalate and ethylene glycol from poly(alkylene terephthalate. Therefore there is a need for a method of recovering terephthalic acid from a material containing poly(ethylene terephthalate), coming for example from a differentiated salvage dump, which is devoid of the drawbacks of the known art. In particular, a method is required which enables recovery of a terephthalic acid free from coloured contaminations and impurities. Still more particularly, there is a need for a method of recovering terephthalic acid which does not involve use of alkaline hydroxides, alkaline-earth hydroxides and ammonium hydroxide or concentrated solutions of these hydroxides. In addition, there is a requirement for a method of recovering terephthalic acid which is particularly cheap. This is very important when a raw material of low value is to be treated, such as the material from a differentiated salvage dump for example. For the above reasons, the volumes of the materials to be heated must be reduced, if possible. In addition, secondary reactions producing by-products must be reduced or eliminated, such as the above mentioned coloured contaminations. Finally, also useful is a reduction in the amount of solvent or water used for the purpose of reducing the amounts of strong acids to employ for acidification of the solution of the metal salt or salts of the TPA so as to obtain precipitation thereof. In addition, a limited use of solvent and water amounts enables the cost of the individual processes to be controlled. It is an aim of the present invention to provide a method of recovering terephthalic acid devoid of coloured contaminations starting from a material containing poly(ethylene terephthalate). Another aim of the invention is to provide a method of recovering terephthalic acid that does not use alkaline hydroxides, alkaline-earth hydroxides and ammonium hydroxide or concentrated solutions of these hydroxides. It is a further aim of the invention to provide a method of recovering terephthalic acid in which a starting reagent-heating step is not required. The foregoing and still further objects that will also become more apparent during the following detailed description have been achieved by the Applicant that has surprisingly found out that recovery of terephthalic acid from materials containing poly(ethylene terephthalate) is possible and advantageous, for example in the case of waste materials in the form of bottles or other manufactured articles coming from a differentiated salvage dump, by making said materials react in the absence of water, with ethylene glycol and a reagent consisting of one or more metal salts of weaker acids than the terephthalic acid, until a water-soluble reaction compound is obtained which comprises soluble chemical species containing chemically-bound TPA and possible parts of unreacted P.E.T. or parts of material of different nature from P.E.T. which are present in the waste material. Therefore it is an object of the present invention to provide a method of recovering terephthalic acid the essential features of which are defined in the independent claim 1. It is a further object of the present invention to provide a method of recovering terephthalic acid the essential features of which are defined in the independent claim 2. Further technical features and the advantages of the present invention will be best understood from the following detailed description. Some preferred embodiments of the present invention are described in appended dependent claims. In accordance with the present invention, the starting material containing poly(ethylene terephthalate) (P.E.T.), for instance waste material in the form of unbroken bottles or small fragments, fibres, ground scraps or films, is set in a mixer device. The mixer device can be of mechanical or electrical operation. Preferably, in a preferred embodiment it can be a reactor equipped with a stirrer or, alternatively, it can be a propeller reactor, the propeller being anchored to the device bottom. The propeller preferably rotates at a speed adapted to enable grinding of the starting material and cause heating by friction of same. The mixing speed is preferably included between 300 and 1600 revolutions per minute (r.p.m.). Advantageous results have been reached at a speed included between 900 and 1450 r.p.m. Added to the starting material are ethylene glycol and a reagent in a solid form, so that the whole forms a reaction mixture in the absence of water. Alternatively, the reagent can be added after a mechanical pre-treating step of the starting material. The reagent used is made up of an anhydrous composition comprising one or more metal salts of weaker acids than the terephthalic acid. These metal salts must have a metallic cation forming water-soluble salts with the TPA. Practically, if the types of salts used are wished to be represented by a chemical formula, we can say that these salts are selected from a group consisting of salts having M n X m (n = valence of anion X and m = valence of cation M) as the general chemical formula; wherein M = metal of valence m supplying water-soluble terephthalates such as for example sodium, potassium, zinc, antimony and tin; and X = cation of a weaker acid than the terephthalic acid. The terephthalic acid has a pKa of 3.51. The dissociation constants pK1 and pK2 for the terephthalic acid at a temperature of 25°C are 3.54 and 4.46, respectively. As a reference parameter to establish the force of an acid, the value herein assumed is that of the dissociation constant of an acid in water, i.e. the value of Ka or Kb, knowing that Kw=Ka.Kb=10 -14 . For instance, the acids that can be used in salts M n X m are selected from inorganic weak acids such as H 2 CO 3 , H 2 S, HNO 2 , H 3 BO 4 , HClO, H 3 BO 3 or from aliphatic organic acids (with the exclusion of formic acid and the acids alpha-substituted with electron-attractor groups like halogens, -OH, -SH, -CHO, -CRO, -CN, -COOH) such as acetic acid, propionic acid, acrylic acid, or aromatic acids such as benzoic acid, meta or para-toluic acid and acids having groups like -OH, -OR and -NH 2 as substituent in the aromatic ring. Further possible examples of salts M n X m finding application in the method of the present invention are represented by: carbonates, bicarbonates, borates (orthoborates, metaborates, perborates and tetraborates), acetates, benzoates and salicylates. Preferably used are sodium carbonate, potassium carbonate, sodium bicarbonate, potassium bicarbonate, sodium sulfide, sodium acetate, potassium acetate, antimony triacetate, zinc acetate and sodium tetraborate. Preferably, mixtures of the above salts are used; for instance, the following mixtures have been found very advantageous: 50% Na 2 CO 3 /50% K 2 CO 3 , 50% (CH 3 COO) 3 Sb/50% CH 3 COONa, 50% (CH 3 COO) 3 Sb/50% (CH 3 COO) 2 Zn. Preferably, the reaction mixture of the mixing step a) comprises an amount by weight of reagent capable of ensuring, at the end of the process of the invention, complete salification of all molecules of terephthalic acid. The terephthalic acid has two carboxyl groups to be salified. Theoretically, the reagent amount used is at least sufficient to salify one of the two carboxyl groups of the terephthalic acid present in the starting P.E.T. Consequently, the reagent used is capable of ensuring at least one metal equivalent per mole of terephthalic acid to be salified. In practice, an excess of reagent is always used independently of the type of salt and the type of salt mixture employed. By way of example, the Applicant in texts carried out has taken into account the amounts of salts commonly used. Preferably, the reaction mixture of the mixing step a) comprises an amount by weight of reagent capable of ensuring at least one monovalent metal equivalent per mole of terephthalic acid to be salified. More preferably, an amount by weight included between at least one equivalent and ten equivalents of monovalent metal per mole of terephthalic acid to be salified. Most preferably, an amount by weight included between one and four equivalents of monovalent metal per mole of terephthalic acid to be salified. The reaction mixture is mixed under ambient pressure and in the absence of water until, by effect of a mechanical working, the reaction mixture is changed to a water-soluble reaction compound. The reaction mixture is mixed over a a period of time preferably included between 5 and 200 minutes; more preferably over a period of time included between 10 and 140 minutes; most preferably over a period of time included between 15 and 100 minutes. Following the mechanical working, the temperature within the device reaches the desired value, at ambient pressure. Alternatively, heating means such as electric resistors, circulation of heating fluids, induction heaters and microwave ovens can be used. Preferably, the heating means is used to bring the reaction mixture to the desired temperature or, alternatively, to keep temperature constant to a given value. Preferably, the temperature is included between 90 and 260°C; more preferably values included between 95 and 220°C and most preferably values included between 100 and 190°C are involved. Heating of the reaction mixture at the above temperatures takes place by mechanical action due to mixing of the reaction mixture in the mixing device. Alternatively, heating is obtained by external heating means. Surprisingly, the applicant has found that at the above temperatures the P.E.T. present in the reaction mixture changes to an intermediate product having the unexpected property of being highly water soluble. Said product comprises soluble chemical species containing unfree TPA in their structure. The soluble chemical species are obtained following an interaction between the P.E.T. and said metal salts of weaker acids than the terephthalic acid. Possibly, the water-soluble reaction compound, in addition to the chemical species, comprises portions of unreacted P.E.T. or part of material of different nature than P.E.T., present in the starting material. Practically, the poly(ethylene terephthalate) is submitted to a "digestion" step, under ambient pressure and in the absence of water, with ethylene glycol and the M n X m salts used. The reaction compound containing the intermediate product physically has a consistency of a paste in a melted or semi-solid state. From a chemical point of view, it can be assumed that the poly(ethylene terephthalate) polymer, by interacting with the reagent, reduces its average molecular weight and the chains of smaller size that are formed have, at their terminations, carboxyl groups salified with the reagent metals and consequently are water-soluble. Therefore, in accordance with the present invention, the water-insoluble starting material, following treatment with ethylene glycol and a solid reagent in the absence of water, is changed to a water-soluble intermediate product or compound because it contains smaller chains having salified carboxyl groups. The soluble compound may also comprise the ethylene glycol possibly created following interaction with one or more metal salts of weaker acids than the terephthalic acid during the mechanical working. Alternatively, the soluble compound can also contain the ethylene glycol added in the mixing step. Alternatively, the intermediate product may comprise a portion of starting material that did not react with the reagent. The Applicant has surprisingly found that the ethylene glycol under these specific work conditions, does not react with the salts of formula M n X m present in the reaction medium and consequently there is no formation of coloured contaminations and impurities that would pollute the final terephthalic acid. In addition, the Applicant has found that the ethylene glycol formed must not be moved away from the reaction medium since its presence does not hinder recovery of the produced terephthalic acid. In the present invention the Applicant has carried out adding of an amount of ethylene glycol to the reaction mixture. The reaction mixture will be comprised of: the material containing poly(ethylene terephthalate) (P.E.T.) and ethylene glycol added in a ratio by weight included between 10:1 and 1:10; preferably the ratio by weight will be included between 7:1 and 1:7 more preferably the ratio by weight will be included between 4:1 and 1:4. The ethylene glycol possibly added can be at room temperature or alternatively can be heated to a temperature included between 100 and 190°C. The ethylene glycol that is added aims at improving heat distribution within the mixer device as well as at improving (speeding up) interaction between the P.E.T. chains and the metal salts of weaker acids than the terephthalic acid. Subsequently, the compound obtained from the intermediate mixing is brought into contact with a fraction of said aqueous medium until a reaction of complete hydrolysis of said soluble chemical species and salification of the TPA contained therein is achieved. Preferably, the water portion is in a ratio by weight included between 4 and 30 parts of reaction mixture; more preferably it is included between 8 and 25 parts; most preferably it is included between 10 and 20 parts of the reaction mixture. The intermediate product is held under stirring over a period of time included between 10 and 100 minutes; more preferably over a period of time included between 20 and 70 minutes. Following addition of water to the soluble compound, a solution is obtained that comprises one or more metal salts of the TPA, ethylene glycol, unreacted parts of said metal salts, parts of water-soluble acids, weaker than the TPA liberated from said metal salts by reaction with the TPA and that did not move away from the reaction medium by evaporation, and possible parts of unreacted P.E.T. or parts of material of different nature than the P.E.T., present in the starting materials (the last mentioned parts being present in the solution as bottom body). Possibly, the obtained solution can be heated to a temperature included between 20 and 100°C; more preferably to a temperature included between 40 and 90°C. Under these conditions, the soluble chemical species are divided into TPA molecules salified with the cations of the M n X m salts and ethylene glycol. Practically, said solution comprises ethylene glycol, terephthalic acid salified with a metal, water, M n X m salt and impurities present in the starting material (P.E.T.), such as colouring substances, unsolubilized polymers, unreacted P.E.T., paper and others. Subsequently, an amount of stronger acid than TPA is added to said first solution for the purpose of creating the appropriate conditions for causing precipitation of the terephthalic acid from said solution. Preferably, said solution can be submitted to filtering and/or washing steps for the purpose of removing impurities present therein, before addition of the strong acid. Practically, the salt of the terephthalic acid salified with a metal, contained in said solution, in the presence of the strong acid is changed to a water-insoluble terephthalic acid and the corresponding salt. For example TPA(Na) 2 + H 2 SO 4 --> TPA(H) 2 + 2Na + + SO 4 2- . Depending on the temperature conditions, ionic force and acidity of the obtained solution after treatment with a strong acid, said salt can precipitate or remain in solution. As strong acids, the following can be preferably employed: H 2 SO 4 , HCl, HNO 3 , H 3 PO 4 and HCOOH. The terephthalic acid precipitated in said solution is separated from the remaining liquid portion. The liquid portion will be comprised of: water, salt formed following acidification of said first solution, ethylene glycol formed from the full hydrolysis reaction and ethylene glycol added, weaker acids that are formed and do not move away from the reaction medium by evaporation. Preferably, the ethylene glycol present in the liquid portion can be recovered. For example, the ethylene glycol can be drawn out by distillation at ambient pressure or under vacuum. It is a further object of the present invention a method of recovering terephthalic acid from a material containing P.E.T. in which, after obtaining the soluble compound, a first portion of water is added which is sufficient to carry out a full hydrolysis of said soluble chemical species and salification of the TPA contained therein, but not to carry out a full dissolution of the reaction compound, thereby obtaining a moist powder and/or a solid or semi-solid paste. Preferably, an amount of water included between 0.1 and 3 parts of the obtained paste is used; more preferably 0.3 to 2 parts; most preferably 0.5 to 1 part. Subsequently, in the same reaction medium where the semi-solid paste is present, the volatile components present in said semi-solid paste are moved away. The volatile components may for example comprise water, ethylene glycol formed during the mixing step, ethylene glycol added to the reaction mixture, or others. To eliminate the volatile components, common means known to those skilled in the art can be used. After the volatile components are eliminated, a solid residue is obtained which contains portions of salified TPA and partly unreacted P.E.T. and others. Subsequently, a second portion of water is added to the solid residue. Preferably an amount of water included between 4 and 30 parts of the obtained paste is employed; more preferably 8 to 25 parts; most preferably 10 to 20 parts, until complete solubilization is reached and an aqueous solution is obtained which comprises one or more metal salts of the TPA, ethylene glycol, unreacted material, water. This solution can then be submitted to filtering and/or washing steps and acidification with a stronger acid than the above TPA. The method of the invention does not contemplate use of alkaline hydroxides such as caustic soda NaOH and ammonium hydroxide NH 4 OH. In addition, the steps provided by the method of the invention can be carried out both following a continuous modality and a batch modality, without any limitations as far as plants are concerned. The yield of the method of the present invention can vary based on the operating conditions and will depend on some process variables. The method of the present invention has all the advantages of the methods based on alkaline hydrolysis presently known in the art, without having any of the drawbacks connected therewith, such as for example: necessity to operate with great volumes of solution and hydrolysis; necessity to operate under pressure; production of coloured by-products that will cause pollution of the TPA produced; necessity to eliminate the ethylene glycol being formed from the reaction medium; and necessity to operate with washed and dried P.E.T. The method of the present invention also represents a method of separation of P.E.T. from other plastic materials. In fact in this method it is also possible to use scraps of P.E.T. containing even important amounts of plastic materials of different nature that, as they do not react and do come out of the reaction medium unaltered, can be easily separated by filtering from the solution containing the salt of a metal of the terephthalic acid. One of the preferred embodiments of the present invention is now given hereinafter, by way of example. EXAMPLE The examples below, 1-60, have been carried out in two different reactors. Reactor No. 1 consists of a cylinder with a diameter of 1 m and a height of 1.5 m, to the bottom of which a propeller rotating at a fixed speed of 1420 r.p.m. is fastened. This reactor is equipped with heating resistors. Reactor No. 2 consists of a cylinder with a diameter of 1 m and a height of 2.8 m, equipped with a propeller-stirrer having a speed varying between 300 and 600 r.p.m. and with heating resistors. Examples 1 to 45 have been carried out in reactor No. 1 with the following modalities: the reactor is loaded with 50 kg of P.E.T. bottles, from a differentiated salvage dump, which still hold PP caps and PE or paper labels, so that P.E.T. content in the charge is about 90% of the total amount = 45 kg. Loading is carried out while the propeller is rotating, at ambient pressure, in the absence of water and with the heating resistors turned off. The loaded material is left under very strong stirring for about 10 minutes, so that bottles are ground and heated by friction to about 100°C. At this point a reagent is added which comprises one or more salts of weaker acids than TPA or mixtures of same in the presence of ethylene glycol, already heated to the desired reaction temperature (100-190°C), and the heating resistors are switched on to maintain said temperature, and the reaction is allowed to go on until it comes to an end. A convenient manner to follow the reaction course is based on measurement of the amounts of liberated weak acid; this is particularly simple where carbonates or acetates are concerned; in fact when evolution of CO 2 or of acetic acid ceases the reaction has come to an end. When this step a) of the mixing process has been completed, water is added which, by evaporating, cools the reaction mixture to a temperature below 100°C. At this point further water is added and the mixture is maintained under stirring at a temperature included between 40 and 99°C until complete dissolution of the soluble species present in the reaction mixture is reached. The solution is filtered and sent to the stage of acidification and precipitation of the TPA with a stronger acid than the terephthalic acid, such as H 2 SO 4 , HCl, HNO 3 , H 3 PO 4 , HCOOH. Thus step b) has been carried out, the process yields are measured by putting the solid residue resulting from filtration into water, separating the supernatant portion (PP, PE, cellulose) from the bottom body (ground and unreacted PET), drying and weighing said bottom body. Practically the unreacted P.E.T. gives the yield value. Examples 46 to 60 have been carried out in reactor No. 2. In this reactor higher amounts of ethylene glycol are required to be used so that the reaction mixture may be conveniently stirred. In this case the reagents are simultaneously loaded and the reaction times are measured at the moment that the system reaches the desired reaction temperature by effect of heating exclusively due to the heating resistors (since in this case friction due to stirring produces negligible heat). Modalities are the same as in examples 1 to 45. The results are reproduced in the Table below. Ex. No. Salt or mixture of metal salts kg of salt or mixture of metal salts kg of ethylene glycol Reaction temp.°C Reaction time Minutes Reacted PET % 1 Na 2 CO 3 12,425 5 100 33 60 2 Na 2 CO 3 12,425 5 150 19 72 3 Na 2 CO 3 12,425 5 190 14 80 4 Na 2 CO 3 24,850 5 100 30 63 5 Na 2 CO 3 24,850 5 150 15 74 6 Na 2 CO 3 24,850 5 190 11 82 7 Na 2 CO 3 36,000 5 100 27 65 8 Na 2 CO 3 36,000 5 150 12 77 9 Na 2 CO 3 36,000 5 190 9 85 10 Na 2 CO 3 12,425 30 100 30 65 11 Na 2 CO 3 12,425 30 150 15 79 12 Na 2 CO 3 12,425 30 190 9 88 13 Na 2 CO 3 24,850 30 100 25 67 14 Na 2 CO 3 24,850 30 150 12 80 15 Na 2 CO 3 24,850 30 190 7 90 16 Na 2 CO 3 36,000 30 100 20 70 17 Na 2 CO 3 36,000 30 150 9 83 18 Na 2 CO 3 36,000 30 190 5 92 19 Na 2 CO 3 12,425 70 100 25 67 20 Na 2 CO 3 12,425 70 150 13 82 21 Na 2 CO 3 12,425 70 190 6 90 22 Na 2 CO 3 24,850 70 100 23 69 23 Na 2 CO 3 24,850 70 150 11 84 24 Na 2 CO 3 24,850 70 190 6 92 25 Na 2 CO 3 36,000 70 100 16 72 26 Na 2 CO 3 36,000 70 150 8 85 27 Na 2 CO 3 36,000 70 190 5 94 28 K 2 CO 3 32,400 5 190 12 78 29 K 2 CO 3 32,400 30 190 8 88 30 K 2 CO 3 32,400 70 190 7 90 31 K 2 CO 3 48,500 70 190 69 92 32 Na 2 CO 3 39,400 5 190 110 78 33 Na 2 CO 3 39,400 30 190 7 88 34 Na 2 CO 3 39,400 70 190 6 90 35 50% Na 2 CO 3 50% K 2 CO 3 28,650 5 190 10 80 36 50% Na 2 CO 3 50% K 2 CO 3 28,650 30 190 8 90 37 50% Na 2 CO 3 50% K 2 CO 3 28,650 70 190 7 91 38 Na 2 S 18,300 30 190 10 85 39 CH 3 COONa 19,300 30 190 15 80 40 CH 3 COONa 39,500 30 190 12 85 41 (CH 3 COO) 3 Sb 46,500 5 190 14 89 42 (CH 3 COO) 3 Sb 46,500 30 190 9 91 43 50% (CH 3 COO) 3 Sb 50% CH 3 COONa 37,000 5 190 12 88 44 50% (CH 3 COO) 3 Sb 50% (CH 3 COO) 2 Zn 66,000 30 190 8 94 45 (CH 3 COO) 2 Zn 43,000 30 190 9 95 46 Na 2 CO 3 12,425 150 100 35 85 47 Na 2 CO 3 24,850 150 150 15 90 48 Na 2 CO 3 36,000 150 190 10 92 49 K 2 CO 3 16,200 150 100 35 83 50 K 2 CO 3 32,400 150 150 15 88 51 K 2 CO 3 48,500 150 190 10 90 52 NaHCO 3 19,700 150 100 35 83 53 NaHCO 3 39,400 150 150 15 90 54 NaHCO 3 59,500 150 190 10 92 55 50%Na 2 CO 3 50% K 2 CO 3 14,400 150 100 35 84 56 50%Na 2 CO 3 50% K 2 CO 3 28,650 150 150 15 89 57 50%Na 2 CO 3 50% K 2 CO 3 43,000 150 190 10 90 58 CH 3 COONa 39,500 150 150 15 90 59 (CH 3 COO) 3 Sb 46,500 150 150 15 90 60 (CH 3 COO) 2 Zn 43,000 150 190 10 95

Claims: A method of recovering terephthalic acid (TPA) from materials containing poly(ethylene terephthalate) (P.E.T.) through precipitation by acidification with a stronger acid than TPA of an aqueous solution comprising one or more water-soluble metal salts of the TPA and subsequent separation, washing and drying of the precipitated TPA, wherein said solution comprising one or more metal salts of the TPA is obtained by a process comprising the following steps: a) mixing, in the absence of water, a reaction mixture comprising said material containing P.E.T. ethylene glycol in an amount by weight included between 10:1 and 1:10 and one or more water-soluble salts of weaker acids than the TPA until a water-soluble reaction compound is obtained; said soluble compound being comprised of soluble chemical species obtained following interaction between P.E.T. and said metal salts of weaker acids than the TPA in the presence of ethylene glycol and possible parts of the unreacted P.E.T. or parts of material of different nature than P.E.T., present in the starting material; b) adding a fraction of water to the soluble compound obtained from step a), until a reaction of salifying the TPA contained in said soluble chemical species is carried out, so that an aqueous solution is obtained which comprises one or more metal salts of the TPA, ethylene glycol and possible parts of the unreacted starting material. A method of recovering terephthalic acid (TPA) from a material containing poly(ethylene terephthalate) (P.E.T.) through precipitation by acidification with a stronger acid than the TPA of an aqueous solution comprising one or more water-soluble metal salts of the TPA and subsequent separation, washing and drying of the precipitated TPA, wherein said solution comprising one or more metal salts of the TPA is obtained by a process comprising the following steps: a) mixing, in the absence of water, a reaction mixture comprising said material containing P.E.T. ethylene glycol in an amount by weight included between 10:1 and 1:10 and one or more metal salts of weaker acids than the TPA until a water-soluble reaction compound is obtained; said soluble compound being comprised of soluble chemical species obtained following interaction between the P.E.T. and said metal salts of weaker acids than the TPA in the presence of ethylene glycol and possible parts of unreacted P.E.T. or parts of material of different nature than the P.E.T., present in the starting material; b) adding a first portion of water to the obtained soluble compound, until a reaction of salifying the TPA contained in said soluble chemical species is achieved but not the complete dissolution of said species, a semi-solid paste being obtained; c) eliminating the volatile components present -in the semi-solid paste of step b) to obtain a solid residue; d) adding a second portion of water to the solid residue obtained from step c), until the TPA is completely solubilized and an aqueous solution comprising one or more metal salts of the TPA is obtained. The method as claimed in claim 1 or 2, wherein the metal salts of weaker acids than the TPA are selected from the group consisting of: sodium carbonate, potassium carbonate, sodium bicarbonate, potassium bicarbonate, sodium sulfide, sodium acetate, potassium acetate, sodium propionate, potassium propionate, sodium benzoate, potassium benzoate, zinc acetate, antimony triacetate, and sodium tetraborate. The method as claimed in claim 3, wherein the metal salt is sodium carbonate. The method as claimed in claim 3, wherein the metal salt is potassium carbonate. the method as claimed in claim 3, wherein the metal salt is sodium sulfide. The method as claimed in claim 3, wherein the metal salt is sodium acetate. The method as claimed in claim 3, wherein the metal salt is sodium bicarbonate. The method as claimed in claim 3, wherein the salt is zinc acetate. The method as claimed in claim 3, wherein the salt is antimony triacetate. The method as claimed in claim 3, wherein the metal salt is present in the form of mixtures. The method as claimed in one or more of the preceding claims, wherein the reaction mixture of step a) comprises the material containing P.E.T. and a reagent amount sufficient to ensure one to four metal equivalents per mole of terephthalic acid to be salified. The method as claimed in claim 1 or 2, wherein the ethylene glycol is added to the reaction mixture at room temperature or pre-heated to a temperature included between 100 and 190°C. The method as claimed in claim 1 or 2, wherein the reaction mixture during step a) is mixed, in the presence of ethylene glycol, in a propeller reactor at a reaction speed included between 600 and 1600 revolutions per minute (r.p.m.), at a temperature included between 90 and 260°C and over a period of time included between 5 and 200 minutes. The method as claimed in claim 14, wherein the reaction mixture during step a) is mixed, in the presence of ethylene glycol, in a propeller reactor at a reaction speed included between 800 and 1500 r.p.m., at a temperature included between 95 and 220°C and over a period of time included between 10 and 140 minutes. The method as claimed in claim 1 or 2, wherein in the mixer device the temperature to which formation of the soluble reaction compound takes place, in the presence of ethylene glycol, is reached by virtue of a mechanical mixing action alone. The method as claimed in claim 1 or 2, wherein in the mixer device the temperature to which formation of the soluble reaction compound takes place, in the presence of ethylene glycol, is reached by virtue of the mechanical mixing action alone and/or by use of heating means.

Inventors: BROCCATELLI MASSIMO, BROCCATELLI, MASSIMO
Applicants: BROCCATELLI MASSIMO, BROCCATELLI, MASSIMO
Application year: 2000
Main classification: C07C51
IPC codes: C07C51