Silicon containing compounds from Michael-type adduct reactions useful as monomers and macromers

Abstract: A zwitterion containing an adduct having the formula (I) wherein X is an electron withdrawing group selected from the group consisting of carbonyl and sulphone groups, sulphonium and phosphonium salts; R is selected from the group consisting of hydrogen, linear and branched alkyl, alkenyl, alkynyl, cycloalkyl, cycloalkenyl, cycloalkynyl, aryl, alkaryl, aralkyl, alkoxyaryl, alkoxyalkyl, oligoalkoxyalkyl, di- alkylaminoalkyl, N-aryl-N-alkylaminoalkyl, hydroxyalkoxy, alkoxy, alkenyloxy, alkynyloxy, cycloalkoxy, cycloalkenyloxy, cycloalkynyloxy, aralkoxy, alkoxyaryloxy, alkoxyalkoxy, oligoalkoxyalkoxy, aminoalkoxy, di-alkylaminoalkoxy, N-aryl-N-alkylamino-alkoxy, acyloxy, acyloxyalkyl, N-diacyl-iminoalkyl groups, organosilane, organosiloxane, and hydroxy groups and any of the above groups substituted with one or more zwitterionic group Z or one or more isocyanate groups, or R-X- is a nitrile group; R 3 and R 4 are individually selected from the group consisting hydrogen, linear and branched alkyl, alkenyl, and alkynyl groups, alkoxycarbonyl, alkylaminocarbonyl, cycloalkyl, cycloalkenyl, cycloalkynyl, haloaryl, haloalkyl, aryl, alkaryl, aralkyl, alkoxyaryl, alkoxyalkyl, oligoalkoxyalkyl, aminoalkyl, mono-and di-alkylaminoalkyl, arylaminoalkyl, N-aryl-N-alkylaminoalkyl and -aminoaryl, acyloxy, acyloxyalkyl, acylaminoalkyl, N-diacyl-iminoalkyl groups, alkylaminocarbonyl, organosilane and organosiloxane groups and any of the above groups substituted with a zwitterionic group Z or an isocyanate group; R 1 and R 2 are individually selected from hydrogen and C 1 -C 12 alkyl groups; and at least one of groups R, R 3 , and R 4 contain a zwitterionic group Z. The invention additionally provides processes for the production of such an adduct, polymers formed therefrom, coating processes and compositions comprising an adduct or polymers produced therefrom.

Description: Phospholipids are phosphate diester compounds, naturally found in the cell membrane, in which one of the alcohol residues is generally a glycerol derivative, and the other is a derivative of a different alcohol which may include a non-ionic, cationic or even an anionic functionality. Phospholipid and phospholipid analogues are of increasing interest, for example to impart the useful properties of biocompatibility, haemocompatibility and to influence the interaction of surfaces with biomolecules such as proteins or enzymes. Our previous disclosures such as EP-A 0032622, EP-A-0157469, EP-A-0555295, EP-A-0601041, EP-A-0593561 (EP-A-0 818 479), EP-A-00639989, WO-A-9416748 and WO-A-9416749 describe various synthetic zwitterionic compounds including phospholipid analogues and their application in devices having biocompatible and haemocompatible surfaces. The present invention extends this methodology to new polymer systems comprising monomers and macromers produced by a Michael-type addition. It is well known in the literature that amines undertake nucleophilic attack on the α,β-unsaturated carbonyl of an acrylate functionality, resulting in a Michael-type 1,4-adduct ( Recent stereoselective synthetic approaches to -amino acids . Cole, Derek C., Tetrahedron (1994), 50(32), 9517-82 ). This technology has been applied in the preparation of a range of curable coatings ( Addition products, radiation-curable surface coating compositions based on the addition products, and their use for wood coating and paper coating, Hintze-Bruning, Horst; Cibura, Klaus; Baltus, Wolfgang, US 5792827; High-solids coatings - formulation aspects. Nowak, Michael T. USA. High Solids Coat. (1982), 7(3), 23-8 ) or resins ( Curing agents for liquid epoxy resins, and curable polymer compositions containing them. Shiono, Kenji; Suzuki, Takehiro. JP 09291135; A process for preparation of room-temperature-curable resins. Furukawa, Hisao; Kawamura, Jo., EP 274112 ). It has also been used extensively in polymer science, for example, to produce a variety of polymer hybrids ( Conductive wire coating based on a curable acrylate-modified amine-terminated polyamide. Frihart, Charles R.; Kliwinski, Joseph. WO 9724191; A polylactone having amino groups, its preparation, and coating and printing ink compositions containing it. Matsui, Hideki., EP 713894; Grafting of amine-functional polymers onto functionalized oxymethylene polymers and the resulting graft polymers thereof. Auerbach, Andrew B.; Broussard, Jerry A.; Yang, Nan L.; Paul, James L. EP 400827 ) or to build dendrimer structures ( Dense star polymers. Tomalia, Donald A.; Dewald, James R. WO 8402705 ). It can also be used to functionalise biologically active amine-bearing compounds ( A synthesis of N-substituted -alanines: Michael addition of amines to trimethylsilyl acrylate. Kwiatkowski, Stefan; Jeganathan, Azhwarsamy; Tobin, Thomas; Watt, David S. Maxwell H. Synthesis (1989), Issue 12, 946-9) . The reaction may be carried out with either acrylate or methacrylate, although the former is generally preferred in the literature on reactivity grounds. The reaction proceeds usually without catalysis, although there are reports of catalysts to promote soley 1,4 addition in good yields ( Catalysis of the specific Michael addition: the example of acrylate acceptors. Cabral, Jose; Laszlo, Pierre; Mahe, Loic; Montaufier, Marie Therese; Randriamahefa, S. Lalatiana., Tetrahedron Lett. (1989), 30(30), 3969-72 ). In EP-A-0933399 an amine functional organopolysiloxane is crosslinked by the Michael addition of a diacrylate. Optional components include substituted acrylates. One example of such a component is the zwitterion containing compound N,N-dimethyl-N-methacryloyloxyethyl-N-(3sulphopropyl)ammonium betaine. In particular, the present invention relates to new polymers, processes for producing them, processes for coating surfaces with them and polymer compositions. The invention also provides new prepolymers and processes for their production. Such polymers are particularly useful in the manufacture or coating of devices with medical applications such as blood contacting devices, contact and intraocular lenses, and other devices which are used in contact with protein-containing or biological fluids. The design of materials for biological or medical applications necessitates that a number of strict material requirements be met. For example, the design of contact lenses necessitates that the material must be optically transparent even after autoclaving, possess chemical stability, have suitable mechanical properties (low modulus of elasticity for patient comfort, adequate tear strength for handling), be biocompatible and have a sufficient water content so that the lens is wettable by tears and moves freely over the eye. In addition, because of lack of blood vesicles in cornea, the lens must be permeable to oxygen directly from the atmosphere. It is also important that the material can be polymerised using present contact lens manufacturing techniques. This normally involves the free radical initiated casting of methacrylate functional monomers, particularly hydrophilic monomers, to form water-swellable hydrogels. These many and often contradictory requirements have most conveniently been met using materials containing, for example, polydimethylsiloxane (PDMS) and polyether compounds. Polydimethylsiloxane based materials are well known to have low modulus of elasticity, excellent transparency and high oxygen permeability. However, PDMS is completely non wettable by tears and exhibits a high affinity for lipids with poor wetting and lens adhesion. Simple blending of PDMS or methacrylate functionalised PDMS with hydrophilic monomers tends to give rise to incompatibility and phase-separated opaque materials exhibiting poor mechanical properties. The present invention provides a zwitterion containing Michael-type adduct having the formula (I) wherein X is an electron withdrawing group selected from the group consisting of carbonyl and sulphone groups, sulphonium and phosphonium salts; wherein X is an etectron withdrawing group selected from the group consisting of carbonyl and sulphone groups, sulphonium and phosphonium salts; R is a group OR' wherein R' consists of an alkanediyl group joined to a zwitterionic group Z having the general formula (II) in which the moieties A 1 and A 2 , which are the same or different, are -O-, -S-, - NH- or a valence bond, and W + is a group comprising an ammonium, phosphonium or sulphonium cationic group and a group linking the anionic and cationic moieties. R 3 and R 4 are individually selected from the group consisting hydrogen, linear and branched alkyl, alkenyl, and alkynyl groups, alkoxycarbonyl, alkylaminocarbonyl, cycloalkyl, cycloalkenyl, cycloalkynyl, haloaryl, haloalkyl, aryl, alkaryl, aralkyl, alkoxyaryl, alkoxyalkyl, oligoalkoxyalkyl, aminoalkyl, mono-and di-alkylaminoalkyl, arylaminoalkyl, N-aryl-N-alkylaminoalkyl and -aminoaryl, acyloxy, acyloxyalkyl, acylaminoalkyl, N-diacyl-iminoalkyl groups, alkylaminocarbonyl, organosilane and organosiloxane groups and any of the above groups substituted with a zwitterionic group Z or an isocyanate group; and R 1 and R 2 are individually selected from hydrogen and C 1 -C 12 alkyl groups. In the definition of R, R 3 and R 4 , any alkyl group or moiety is preferably C 1-18 alkyl, any alkenyl group or moiety is preferably C 2-18 alkenyl, any alkynyl group or moiety is preferably C 2-12 alkynyl, any aryl group or moiety is preferably C 6-24 aryl, any alkaryl group or moiety is preferably C 7-24 alkaryl and any aralkyl group or moiety is preferably C 7-24 aralkyl, any cycloalkyl group or moiety is preferably C 4-24 cycloalkyl, any cycloalkenyl group or moiety is preferably C 5-24 cycloalkenyl, any cycloalkynyl group or moiety is preferably C 5-24 cycloalkynyl. In the zwitterionic group Z the moieties A 1 and A 2 are preferably -O-, and W + is preferably a group of formula - W 1 -N + R 5 3 , -W 1 -P + R 6 3 , -W 1 -S + R 6 2 or -W 1 -Het + in which: W 1 is alkanediyl of 1 or more, preferably 2-6 carbon atoms optionally containing one or more ethylenically unsaturated double or triple bonds, disubstituted-aryl (arylene), alkylene arylene, arylene alkylene, or alkylene aryl alkylene, cycloalkanediyl, alkylene cycloalkyl, cycloalkyl alkylene or alkylene cycloalkyl alkylene, which group W 1 optionally contains one or more fluorine substituents and/or one or more functional groups; and either the groups R 5 are the same or different and each is hydrogen or alkyl of 1 to 4 carbon atoms, preferably methyl, or aryl, such as phenyl, or two of the groups R 5 together with the nitrogen atom to which they are attached form an aliphatic heterocyclic ring containing from 5 to 7 atoms, or the three groups R 5 together with the nitrogen atom to which they are attached form a fused ring structure containing from 5 to 7 atoms in each ring, and optionally one or more of the groups R 5 is substituted by a hydrophilic functional group, and the groups R 6 are the same or different and each is R 5 or a group OR 5 , where R 5 is as defined above; or Het is an aromatic nitrogen-, phosphorus- or sulphur-, preferably nitrogen-, containing ring, for example pyridine. Most preferably the zwitterionic group of the formula (II), has the general formula (III): where the groups R 7 are the same or different and each is hydrogen or C 1-4 alkyl, and m is from 1 to 4, in which preferably the groups R 7 are the same preferably methyl. R 1 and R 2 are preferably selected from hydrogen or C 1 -C 4 alkyl groups, most preferably both hydrogen. X is preferably a carbonyl group and adduct (I) has the formula Most preferably the zwitterionic group is an ethylene-2-(trimethylammonium)ethylphosphate inner salt. An organosiloxane group utilised in the present invention, for example as R 4 , preferably has the formula (VII) in which R 8 -R 13 are each selected from a valence bond, hydrogen, branched and straight C 1-12 alkyl, C 6-18 aryl, C 6-18 alkaryl, C 6-18 aralkyl, C 2-12 alkenyl, C 2-12 alkynyl and O-Si-(R 14 ) 3 , where R 14 is C 1-12 alkyl or C 6-18 aryl, any of which may be substituted by a primary, secondary or tertiary amine group, and n is 0-300, provided that at least one of the groups R 8 -R 13 is selected from the group consisting of a valence bond, C 1-12 alkanediyl, C 2-12 alkenediyl and C 2-12 alkynediyl and is covalently bonded to the nitrogen atom of adduct (I). (VII) has a molecular weight of 300-20000. Preferably (VII) has a molecular weight in the range 500-10000, more preferably 1000-7000, most preferably 3000-6000. Preferably, R 9 -R 12 are individually selected from the group consisting of C 1-6 alkyl groups, preferably C 1-4 alkyl groups, most preferably methyl, and are preferably the same. R 3 or R 4 may comprise a polyoxyalkylene group having the formula (VIII) wherein R 29 - R 36 are individually selected from the group consisting of hydrogen, C 1-6 alkyl, C 6-18 aryl, C 6-18 aralkyl, C 6-18 alkaryl and C 2-6 alkenyl; R 37 and R 38 are individually selected from the group consisting of a valence bond, hydrogen, C 1-6 alkyl, C 6-18 aryl, C 6-18 aralkyl, C 2-6 alkenyl aminoalkyl, mono-, di- and tri- alkylaminoalkyl, arylaminoalkyl, N-aryl-N-alkylaminoalkyl and -aminoaryl; a is an integer of 0-10, b is an integer of 0-500, a is an integer of 0-10; and (VIII) has a molecular weight of 100-10000. (VIII) is bound to the nitrogen atom by one of R 37 or R 38 . Where this is the case, the group connected to the nitrogen atom is usually a valence bond and the groups (R 37 or R 38 ) not connected to the nitrogen atom is preferably connected to another adduct (I) and comprises a -NH(R 3' ), or -N(R 3' ) 2 group, wherein R 3' is selected from the same group as R 3 , or consists of a hydrogen atom or C 1-4 alkyl group. R 31 - R 34 are preferably selected from hydrogen or C 1-4 alkyl, most preferably hydrogen or methyl. For instance one of R 31 - R 34 may be a methyl and the rest hydrogen, but most preferably all hydrogen. Preferably group (VIII) has a molecular weight in the range of 300-10,000. Most preferably R 4 comprises the organosiloxane (VII). Where R 4 comprises (VII), (VII) is preferably connected to the nitrogen atom of adduct (I) through group R 8 or R 13 . Where this is the case, the group connected to the nitrogen atom is usually valence bond, C 1-12 . alkanediyl, C 2-12 alkenediyl and C 2-12 alkynediyl. Preferably R 8 and R 13 are bonded to the nitrogen atoms of 2 separate adducts (I). Preferably R 8 and R 13 are selected from methanediyl, ethanediyl, propanediyl and butanediyl and are both covalently bound to the nitrogen atom of individual adducts (I). Alternatively R 3 and/or R 4 comprise a polyoxyalkylene group as defined by structure (VIII). Alternatively, one or more of R 3 and R 4 can be an organosilane group. A preferred organosilane group for use in the present invention has the general formula (IX) wherein R 16 , R 17 and R 18 are selected from the group consisting of hydrogen, branched and straight C 1-12 alkyl, C 6-18 aryl, C 6-18 alkaryl, C 6-18 aralkyl, C 2-12 alkenyl and C 2-12 alkynyl; R 15 is selected from the group consisting of a valence bond, branched and straight chain C 1-12 alkanediyl, straight and branched C 2-12 alkenediyl and straight and branched C 2-12 alkynediyl; and (IX) is connected to the N atom of (I) through R 15 . In a preferred embodiment R 3 is a hydrogen atom or comprises a reactive group. Reactive groups include, for example, groups containing an ionic group or a site of unsaturation that is capable of forming a covalent bond with another group or to a substrate. Alternatively the reactive group may increase the ability of the adduct to physisorb or chemisorb to another group or to a substrate relative to the ability of the adducts to physisorb or chemisorb exclusive of the reactive group. Preferred substrates include, for example, silicones, polyurethanes, polyalkacrylates, polystyrenes, polycarbonates, polyesters and metals (particularly stainless steel). Other groups with which the reactive group may bond, physisorb or chemisorb to include, for example, another adduct (I) or polymer formed by polymerisation of adduct (I), polymers having desirable physical or mechanical properties, drugs, ligands or biological molecules such as enzymes or heparin. Where R 3 comprises a reactive group, it preferably comprises at least one group selected from the group consisting of isocyanate, organosilane and (meth)acryloyloxy. Most preferably R 3 is an cycloalkylaminocarbonyl, arylaminocarbonyl, or alkylaminocarbonyl group containing an isocyanate substituent. In one preferred embodiment adduct (I) has the formula (X), (XI), (XII), (XIII) or (XIV) wherein each R 19 , R 20 , R 21 , R 23 , R 24 , R 25 and R 26 are individually selected from the group consisting of hydrogen, C 1-6 alkyl, C 6-18 aryl, C 6-18 aralkyl, C 6-18 alkaryl, and C 2-6 alkenyl, preferably C 1-6 alkyl, most preferably methyl or ethyl; each R 22 is individually selected from the group consisting of C 1-6 alkanediyl, C 2-6 alkendiyl and C 2-6 alkynediyl, preferably C 1-6 alkanediyl; R 27 is selected from the group consisting of hydrogen, C 1-6 alkyl, C 6-18 aryl, C 6-18 aralkyl, C 2-6 alkenyl, C 6-18 alkaryl, preferably hydrogen or C 1-4 alkyl; each R 28 is individually selected from the group consisting hydrogen, linear and branched alkyl, alkenyl, and alkynyl groups, alkoxycarbonyl, alkylaminocarbonyl, cycloalkyl, cycloalkenyl, cycloalkynyl, haloaryl, haloalkyl, aryl, alkaryl, aralkyl, alkoxyaryl, alkoxyalkyl, oligoalkoxyalkyl, aminoalkyl, mono-, di- and tri- alkylaminoalkyl, arylaminoalkyl, N-aryl-N-alkylaminoalkyl and -aminoaryl, acyloxy (including alkenoyloxy), acyloxyalkyl (including alkenoyloxyalkyl), acylaminoalkyl, N-diacyl-iminoalkyl groups, alkylaminocarbonyl, organosilane and organosiloxane groups and any of the above groups substituted with a zwitterionic group Z or an isocyanate group; n is an integer of 1 to 500; p is an integer of 1 to 50; q is an integer of 1 to 500; r is an integer of 1 to 50; and s is an integer of 0 or 1. The formula (XIII) and (XIII) are not intended to represent the specific order within the organosiloxane backbone of the groups -O-SiR 21 R 22 , -O-SiR 23 R 24 and -O-SiR 25 (R 22 ), and in fact these groups can be randomly or specifically ordered within the backbone. Most preferably R 19 , R 20 , R 21 , R 23 , R 24 , R 25 and R 26 are all methyl and R 22 is selected from ethanediyl, propanediyl and butanediyl. In a further preferred embodiment, adduct (I) has the formula (XV), (XVI) or (XVII) wherein R 39 - R 46 are individually selected from the group consisting of hydrogen, C 1-4 alkyl, C 6-18 aryl, C 6-18 aralkyl, C 6-18 alkaryl; and R 47 is selected from the group consisting of hydrogen, C 1-4 alkyl, C 6-18 aryl, C 6-18 aralkyl, C 6-18 alkaryl, and C 2-6 alkenyl; and a is an integer of 0-10, b is an integer of 0-500, a is an integer of 0-10. Preferably R 39 - R 46 are selected from propyl, ethyl, methyl and hydrogen and are preferably all the same. R 47 is preferably hydrogen. The present invention additionally provides a method for the production of an adduct by the Michael-type addition of a compound having the formula (XVIII) with a compound having the formula (XIX) H 2 NR 51 to form a zwitterion containing compound having the formula (XX) wherein X is an electron withdrawing group selected from the group consisting of carbonyl and sulphone groups, sulphonium and phosphonium salts; R 48 is a OR 48' , where R 48' consists of an alkanediyl group joined to a zwitterionic group Z having the general formula (II) in which the moieties A 1 and A 2 , which are the same or different, are -O-, -S-, - NH- or a valence bond, and W + is a group comprising an ammonium, phosphonium or sulphonium cationic group and a group linking the anionic and cationic moieties; R 51 is selected from the group consisting hydrogen, linear and branched alkyl, alkenyl, and alkynyl groups, alkoxycarbonyl, alkylaminocarbonyl, cycloalkyl, cycloalkenyl, cycloalkynyl, haloaryl, haloalkyl, aryl, alkaryl, aralkyl, alkoxyaryl, alkoxyalkyl, oligoalkoxyalkyl, aminoalkyl, mono- and di-alkylaminoalkyl, arylaminoalkyl, N-aryl-N-alkylaminoalkyl and -aminoaryl, acyloxy, acyloxyalkyl, acylaminoalkyl, N-diacyl-iminoalkyl groups, alkylaminocarbonyl, organosilane and organosiloxane groups; and R 49 and R 50 are individually selected from hydrogen and C 1 -C 12 alkyl groups. R 49 and R 50 are preferably selected from hydrogen or C 1 -C 4 alkyl groups most preferably both hydrogen. In the definition of R 47 and R 50 , any alkyl group or moiety is preferably C 1-18 alkyl, any alkenyl group or moiety is preferably C 2-18 alkenyl, any alkynyl group or moiety is preferably C 2-12 alkynyl, any aryl group or moiety is preferably C 6-24 aryl, any alkaryl group or moiety is preferably C 7-24 alkaryl and any aralkyl group or moiety is preferably C 7-24 aralkyl, any cycloalkyl group or moiety is preferably C 4-24 cycloalkyl, any cycloalkenyl group or moiety is preferably C 5-24 cycloalkenyl, any cycloalkynyl group or moiety is preferably C 5-24 cycloalkynyl. The structure is not intended to represent that when R 49 and R 50 are not both hydrogen atoms that are in a cis-configuration about the double bond and in fact they may be trans. Preferably (XIII) has the formula (XXI) Preferably, R 48 , R 49 , R 50 , R 51 and X have the same definitions as R, R 1 , R 2 , R 4 and X respectively as hereinbefore defined. In any particularly preferred embodiment, R 51 comprises a primary or secondary amine group. This allows for a reaction whereby one equivalent of compound (XIX) reacts with two equivalents of compound (XVIII) to form, a compound of, for example (XI) or (XVI). Preferably the reaction of two equivalents of (XVIII) occurs at 2 separate amine groups on (XIX), not at the same amine group. This reaction is usually carried out with a diamine compound, preferably an amine disubstituted organosiloxane or an amine disubstituted polyoxyalkylene. Alternatively the primary or secondary amine in group R 51 may be used to crosslink to a different group or substrate, either by a Michael type addition or an alternative reaction mechanism, for example, nucleophilic addition or substitution. Compound (XX) may undergo a second reaction with a compound (XXII) R 52 -N=C=O wherein R 52 is selected from the group consisting of linear and branched alkyl, alkenyl, and alkynyl groups, alkoxycarbonyl, cycloalkyl, cycloalkenyl, cycloalkynyl, haloaryl, haloalkyl, aryl, alkaryl, aralkyl, alkoxyaryl, alkoxyalkyl, oligoalkoxyalkyl, di-alkylaminoalkyl, N-aryl-N-alkylaminoalkyl and acyloxy (including alkenoyloxy), acyloxyalkyl (including alkenoyloxyalkyl), N-diacyl-iminoalkyl groups, organosilane and organosiloxane groups and any of the above groups substituted with a zwitterionic group Z or an isocyanate group, to form a compound having the formula (XXIII) In a preferred embodiment, R 52 comprises a site of unsaturation, most preferably an isocyanate group capable of crosslinking to another compound of general structure (XX), another polymer or group, or alternatively a substrate as defined hereinbefore. Said site of unsaturation may alternatively provide a site at which homo or co-polymerisation of a compound (XXIII) may occur, for example an ethylenically unsaturated group such as alkenoyloxy. Most preferably the compound (XXII) is an isocyanate or diisocyanate and is preferably selected from the group consisting of C 2-30 aliphatic, C 6-30 aromatic and C 6-20 alicyclic isocyanates or diisocyanates C 4-30 allyl isocyanates, C 3-30 isocyanatoalkylacrylates, C 5-30 isocyanato alkylmethacrylates, more preferably preferably allyl isocyanate, dimethyl meta-isopropenylbenzylisocyanate, isophorone diisocyanate, hexamethylene diisocyanate, meta-tetramethylxylylene diisocyanate. The reaction may be carried out in a single or two steps. A two step reaction is favoured as this allows work up of a characterisable, pure product after the first step. The first step (reaction of the α,β-unsaturated group with amine-bearing component) may be performed in a solventless system when one component is able to solubilise the other. Alternatively, an aqueous or organic solvent may be utilised. Preferred organic solvents include alcohols (including hydroxyalkyl(meth)acrylates), chlorinated hydrocarbons, organosulphoxides, alkylamides and ethers. Where (I) contains an ester linkage, one prerequisite for the Michael addition step is that the solvent in which the reaction occurs is chosen carefully in order to avoid the possibility of transesterification of the ester linkage in the resulting adduct. Transesterifications are acid or base catalysed reactions and it is likely that the basic structure of the secondary amine in the adduct is sufficient to catalyse the convertion. In particular it is found that the use of methanol as a reaction solvent results in a Michael adduct that has been almost exclusively transesterified, producing the methyl ester of the amine. When isopropylalcohol is used instead of methanol, the transesterification is virtually eliminated with only traces of the transesterified product being detected. Acidity, nucleophilicity and steric hinderance of the alcohol group are all considerations in determining whether the solvent system used will be suitable for the Michael addition. The second step of the reaction with the isocyanate may be carried out in a solventless system or in aqueous or organic solvents. Preferably, where isocyanate or diisocyanates are utilised, the reaction is carried out in the absence of water. As the reaction proceeds an organic solvent is usually required. Preferred organic solvents include alcohols (including hydroxyalkyl(meth)acrylate), chlorinated hydrocarbons, organosulphoxides, alkylamides and ethers. A particularly preferred solvent for the first reaction is isopropanol or hydroxyethylmethacrylate. For the second reaction, the preferred solvents include dimethylsulphoxide, isopropanol, hydroxyethylmethacrylate, tetrahydrofuran, or N-methylpyrrolidone or mixtures thereof. Scheme 1 shows two reaction routes resulting in particularly preferred products. wherein m and are integers of 10-400. In both examples (reaction with organosiloxane (B) or polyoxyalkylene) (C)) the first two steps may be carried out separately or concurrently depending on the stoichiometry of the reaction. Preferably the production of (E) or (H) by the zwitterion containing group (A) occurs in one step. The reaction product is preferably recovered and the further step of reaction with a reactive group (in the examples shown, an isocyanate), is carried out. For example, if a diisocyanate compound is used to functionalise compound (E) or compound (H), this will produce an isocyanate-functionalised oligomer that could form a block in a segmented polyurethane urea. Scheme 2 illustrates another particularly preferred embodiment of the present invention. Compound (E) (or more generally a compound (XX) is reacted with a diisocyanate compound to produce a compound of type (K) having pendant isocyanate groups. This compound can be reacted further with a capping reagent, for example, hydroxyethylmethacrylate or t-butylaminoethyl methacrylate to produce a methacrylate-terminated oligomer (compounds (L) and (M) in scheme 2, ideal for free-radical polymerisation with other ethylenically unsaturated monomers. This could also be achieved in one step if a zwitterion containing Michael adduct is reacted with an isocyanate bearing unsaturation in some form. Particularly useful are isocyanates such as dimethylmeta-isopropenylbenzylisocyanate, allylisocyanate or methacryloloxyethylisocyanate. Alternatively, or prior to introduction of a cap, compound K, for example, could be reacted with a similar or dissimilar group E, for example. Another amine (either having undergone or not undergone a Michael addition reaction) may be introduced to react with (K) as another way of adding additional entities with desired physical and/or chemical properties into the molecule. The "other amine" is typically any diamine for which the ratio of diisocyanate is adjusted such that some chain extension of compound (K) occurs, prior to capping the molecule. The addition of the "other" amine is prior to cap addition and may be accompanied by further diisocyanate addition to maintain stoichiometry. Materials comprising the adducts described hereinbefore are of particular utility in medical device manufacture. In particular, organosiloxane containing adducts, or polymers or copolymers produced by their polymerisation have particular utility in the manufacture of contact and intra ocular lenses. They provide high oxygen permeability and biocompatibility within the ocular environment. Where (XIX) comprises functional groups in addition to the amine functionality, an adduct formed therefrom can provide products that possess utility as graftable coatings. For example, where (XIX) is functionalised with pendant reactive groups such as alkyl groups substituted with aldehyde or carboxylic acid groups, adducts (or polymers) formed therefrom may be used to graft onto biological tissue bearing lysine moieties. Alternatively, where an amine is functionalised with an organosilane group such as (IX), this may be used to graft an adduct of the present invention to an organic or inorganic substrate. Compounds and polymers bearing such an organosilane group show particular utility in bonding to metal surfaces. The presence of the zwitterionic component in a polymer provided by polymerisation of an adduct of the present invention improves the biocompatibibility of the material compared with non-zwitterionic containing analogues. If, for example, it is desirable to make biodegradable materials, this could be achieved by the incorporation of a suitably labile chain extender, the degradation product being less toxic to the body than a similar compound not bearing a zwitterionic group. Similarly, wear-debris from a non-degradable implant or contact lens of the materials should also be of less risk than a similar material not bearing a zwitterionic group to the body or ocular environment. The production of a polymer comprising an adduct of the present invention may be achieved by any known polymerisation method. As described above, this may be achieved by funtionalising the adduct to incorporate a site of unsaturation, thus providing an adduct capable of, for example, free radical polymerisation. The present invention additionally incorporates compositions comprising adduct(s) of the present invention, and compositions of polymers produced by polymerisation of such an adduct. The following examples illustrate the working of the present invention. Starting Materials: Material Code Supplier Pendant amino-functional PDMS (AEW 1170) AMS 162 Apollo Terminal amino-functional PDMS (AEW 810) DMS A12 Apollo Terminal amino-functional PDMS (AEW 1265) DMS A15 Apollo Terminal amino-functional PEG (AEW 315) (Jeffamine ED 600) JED 600 Huntsman Ethylene diamine ED Aldrich Allyl isocyanate Al Aldrich Dimethyl meta-isopropenyl benzyl isocyanate TMI Cytec Isophorone diisocyanate IPDI Aldrich Hexamethylene diisocyanate HMDI Aldrich Meta-tetramethylxylylene diisocyanate TMXDI Cytec Dimethylacrylamide DMA Aldrich t-Butylaminoethyl methacrylate 3AM Aldrich 2-Acryoyloxyethyl phosphorylcholine APC Synthesised Isopropanol IPA Romil N,N'-Dimethylacrylamide NNDMA Aldrich 3-[Tris(trimethylsilyloxy)silyl]propyl methacrylate TRIS Aldrich Ethylene glycol dimethacrylate EGDM Aldrich Terminal aminofunctional poly(propylene glycol) D400 PEG refers to polyethyleneglycol and AEW refers to amine equivalent weight. The molecular weight (Mw) of AMS 162 is 4000-5000. All materials were obtained and purified as described in the examples. (2-acryloyloxyethyl)-2'-(trimethyl-ammoniumethyl) phosphate, inner salt (Acryloyl-phosphorylcholine, APC) was made by a modification of the route described previously by Ishihara et al . ( Polym. J., 22 (3), 355, 1990): All glassware was dried thoroughly before use. 2-Chloro-2-oxo 1,3,2 dioxaphospholane (CCP, Avocado Chemical Co.) (68.3g, 0.48mol, 1.05 equiv.) was weighed into a 250ml self-equilibrating dropping funnel and dissolved in ∼50ml of acetonitrile. Hydroxyethyl acrylate (HEA, Aldrich Chemical Co.) (53g, 0.46mole) was measured into a 3-neck 2L r.b. flask, fitted with a thermometer (range -100°C-50°C), the dropping funnel, a N 2 bubbler and a magnetic stirrer. The HEA was dissolved in 700ml acetonitrile and cooled to 0°C using a solvent/CO 2 bath. Whilst stirring, N,N,N',N'-tetramethylene diamine (TMEDA, Aldrich Chemical Co.) (36g, 0.24mol, 1.05equiv.) were added, followed by the dropwise addition of the CCP solution over a 20 minute period. The reaction mixture went cloudy upon addition of the CCP as the TMEDA.2HCl salt formed. The reaction was left to stir for 2 hours. The TMEDA.2HCl was filtered off under vacuum and an N 2 atmosphere and washed with acetonitrile (∼60ml). The clear pale yellow solution was collected in a 2L Florentine flask. A solvent/CO 2 bath was used to cool the solution to ∼0°C before bubbling Trimethylamine (TMA, Aldrich Chemical Co.) (81.53, 1.38mol, 3 equiv.) into the solution, while stirring. The flask was fitted with an air condenser with a balloon attached to the top and stirred at 50°C for 16 hours. Excess TMA was then removed under vacuum via a solvent/CO 2 cold trap, using a HCI trap, whilst stirring at 40°C. ∼300ml of acetonitrile was removed and white solid product of APC was filtered off under vacuum and N 2 . Weight of product collected = 93.7g 73%. 1 H NMR (in D 2 O) confirmed the product had been made (characteristic singlet for -N + (CH 3 ) 3 @ 3.15-3.22ppm, double bond of the acrylate @ 5.98-6.02ppm (doublet), 6.19-6.26ppm (quartet), 6.44-6.48ppm (doublet)). 31 P NMR (in CDCl 3 ) showed a peak @ -0.53ppm as expected. Example 1: Preparation of the APC:Polyoxyalkyleneamine Adduct. 18.73g (0.067mol) of APC was weighed into a 1 00ml r.b. flask fitted with a condenser and a magnetic stirrer and placed in an oil bath. To this was added 50ml of IPA and the solution stirred in order to dissolve the solid. A 600 Mw Polyoxyalkyleneamine macromonomer(Jeffamine ED600, Huntsman Corp.) (20g, 0.033mol) was dissolved in 20ml of IPA and this was added to the APC solution and the mixture allowed to reflux for 16 hours with stirring. After this time the IPA was removed by vacuum distillation to yield the clear, yellow viscous liquid product. The conversion was almost quantitative (37g, 97%). 1 H NMR confirmed the loss of the acrylate double bond, whereas the quaternary ammonium group of the head group could still be clearly seen. Example 2: Preparation of the Polyurethane Urea based on [1,4 butanediol:Polyoxyalkyleneamine:hexamethylene diisocyanate 2 ]. All glassware was thoroughly dried before use. The Polyoxyalkyleneamine (8.79g, 22mmol) was weighed into an appropriately sized flask equipped with condenser and stirrer, with 40ml DMSO (Aldrich Chemical Co.) to produce a ∼40% w/v. This was stirred at 50°C until the adduct had dissolved, followed by the addition of two equivalents of hexamethylene diisocyanate (7.39g, 44mmol), an appropriate amount of a suitable catalyst (normally 3 drops of stannous octoate) and stirring for 5 minutes to form a prepolymer. The chain extender butanediol (2.00g, 22mmol) was then added to the mix and the temperature stirred for 1.5 hours, before raising the temperature to 100°C for 16 hours. The resulting polymer solution was precipitated into water, and the solid filtered off under vacuum. Residual solvent was removed by Solvent extraction of the solid. The polymer was then dried for at least 24 hours before subjecting to analysis. Polymer yield = ∼79%. 1 H NMR (d 6 DMSO) confirmed the polymer structure, peaks for hexamethylene diisocyanate @ 1.22, 1.32 + 2.94ppm, 3.91 ppm (doublet), 3.65ppm (multiplet), NH of urea @ 5.60, 5.74 + 5.84ppm (singlets), NH of urethane @ 7.06ppm (doublet). FTIR also confirms the structure with absorption peaks for N-H @ 3339cm -1 , C-H @ 2932cm -1 , Urethane -CONH- @ 1685cm -1 , Urea - NHCONH- @ 1626cm -1 , N-H deformation @ 1561cm -1 , C-H @ 1258cm- 1 , CH 2 -O-CH 2 @ 1101cm -1 . Example 3: Preparation of the Polyurethane Urea based on [1,4 butanediol: (APC:Polyoxyalkyleneamine):hexamethylene diisocyanate 2 ]. All glassware was thoroughly dried before use. The APC:Polyoxyalkyleneamine (7.5g, 7.8mmol) and butanediol (0.7g, 7.8mmol) was weighed into an appropriately sized flask equipped with mechanical stirrer. This was stirred at 70°C until the mix became homgenous before cooling to 50°C, followed by the addition of two equivalents of hexamethylene diisocyanate (2.6g, 15.4mmol). As the mix thickened to form a stiff white gum 30ml DMSO (Aldrich Chemical Co.) was added to produce a ∼40% w/v solution, which was stirred for a 16 hour period at 50°C. The resulting polymer solution was precipitated into 1L acetone, and the solid filtered off under vacuum. Residual solvent was removed by Soxhlet extraction of the solid. The polymer was then dried for at least 24 hours before subjecting to analysis. Polymer yield = ∼59%. 1 H NMR (d 6 DMSO) confirmed the polymer structure, peaks for hexamethylene diisocyanate @ 1.22, 1.37 + 2.94ppm, -N + (CH 3 ) 3 of PC @ 3.13ppm (singlet), 3.92ppm (doublet), 3.68ppm (multiplet), NH of urethane @ 7.06ppm (doublet). FTIR also confirms the structure with absorption peaks for N-H @ 3371cm -1 , C-H @ 2934cm -1 , Ur ethane -CONH- @ 1718cm -1 , Urea - NHCON H- @ 1631 cm -1 , N-H deformation @ 1538cm -1 , C-H @ 1240cm -1 , CH 2-O-CH 2 @ 1089cm -1 . Example 4: Preparation of the Polyurethane Urea based [1,4 butanediol: (APC:Polyoxyalkyleneamine):dicyclohexylmethane diisocyanate 2 ]. All glassware was thoroughly dried before use. The APC:Polyoxyalkyleneamine (7.712g, 8.0mmol) and butanediol (0.72g, 8.0mmol) was weighed into an appropriately sized flask equipped with mechanical stirrer. This was stirred at 70°C until the mix became homgenous before cooling to 50°C, followed by the addition of two equivalents of dicyclohexylmethane diisocyanate (4.0g, 15.5mmol). As the mix thickened to form a stiff white gum 30ml NMP (Aldrich Chemical Co.) was added to produce a ∼40% w/v solution, which was stirred for 16 hours at 50°C. The resulting polymer solution was precipitated into 1 L acetone, and the solid filtered off under vacuum. Residual solvent was removed by Soxhlet extraction of the solid. The polymer was then dried for at least 24 hours before subjecting to analysis. Polymer yield = ∼59%. 1 H NMR (d 6 DMSO) confirmed the polymer structure, peaks for dicyclohexylmethane diisocyanate @ 1.20, 1.44 + 1.75ppm (multiplet), -N + (CH 3 ) 3 of PC @ 3.14ppm (singlet), 3.68ppm (multiplet), 3.92ppm (doublet), NH of urea @ 5.78, 5.90 + 6.02ppm (singlets), NH of urethane @ 7.00ppm (doublet). FTIR also confirms the structure with absorption peaks for N-H @ 3370cm -1 , C-H @ 2971 cm -1 , Urethane -CONH- @ 1723cm -1 , Urea -NHCONH-@ 1631cm -1 , N-H deformation @ 1532cm -1 , C-H @ 1234cm -1 , CH 2 -O-CH 2 @ 1089cm -1 . Example 5: Preparation of the Polyurethane Urea based on [1,4 butanediol: (APC:Polyoxyalkyleneamine):diphenylmethane diisocyanate 2 ]. All glassware was thoroughly dried before use. The APC:Polyoxyalkyleneamine (5.5g, 5.7mmol) and butanediol (0.51g, 5.7mmol) was weighed into an appropriately sized flask equipped with mechanical stirrer. This was stirred at 70°C until the mix became homgenous before cooling to 50°C, followed by the addition of two equivalents of dicyclohexylmethane diisocyanate (2.85g, 11.4mmol). As the mix thickened to form a stiff white gum 30ml NMP (Aldrich Chemical Co.) was added to produce a ∼40% w/v solution, which was stirred for 16 hours at 50°C. The resulting polymer solution was precipitated into 1 L acetone, and the solid filtered off under vacuum. Residual solvent was removed by solvent extraction of the solid. The polymer was then dried for at least 24 hours before subjecting to analysis. Polymer yield = ∼59%, 1 H NMR (d 6 DMSO) confirmed the polymer structure, peaks for -N + (CH 3 ) 3 of PC @ 3.12ppm (singlet), 3.76ppm (multiplet), 4.05ppm (doublet), NH of urea @ 5.55(singlet), NH of urethane @ 7.03ppm (doublet), diphenylmethane diisocyanate @ 7.07 + 7.35ppm (doublets). FTIR also confirms the structure with absorption peaks for N-H @ 3338cm -1 , C-H @ 2973cm -1 , Urethane -CONH- @ 1729cm -1 , Urea -NHCONH-@ 1651cm -1 , N-H deformation @ 1538cm -1 , C-H @ 1224cm -1 , CH 2 -O-CH 2 @ 1089cm -1 . Example 6: Properties of some selected Polyurethane Ureas based on [chain extender x :(APC:Polyoxyalkyleneamine): Diisocyanate x+1 ]. The polymers were found to be soluble in 2,2,2-trifluoroethanol. Solutions containing 10mgml -1 were made and used to coat PET strips (9mm x 30mm) by dipping the strip in and out of the solution at a speed of 3mmsec -1 . After air-drying for 16 hours the coated PET strips were subjected to a double antibody fibrinogen assay for the detection of protein adsorption to the strip. Table 1 summarises the results obtained on polymers of the invention as described in examples 2-5. The bioevaluation results are expressed as a percentage reduction of the adsorbed protein compared to that adsorbed to an uncoated PET control strip. Clearly, the inclusion of the PC moiety on the Jeffamine soft segment leads to a further significant reduction in the amount of fibrinogen that adsorbs to the surface of the coating, compared to the non-PC containing control polyurethane urea. The information from this assay therefore provides further evidence to add to that already in existence, suggesting that the PC group does indeed improve the 'biocompatibility' of the material. Preparative and bioevaluation results for some polyurethane ureas. Ex. # Chain Extender Soft Segment Diisocyanate Appearance Yield (%) Reduction in Fg (%) 2 1,4-Butanediol (1) Jeffamine D400 (1) 1,6 Hexamethylene Diisocyanate (2) White Solid 79 39 3 1,4-Butanediol (1) APC:D400 Adduct (1) 1,6 Hexamethylene Diisocyanate (2) White Gum 59 72 4 1,4-Butanediol (1) APC:D400 Adduct (1) Dicyclohexylmethan e 4,4'-Diisocyanate (2) White Crystalline Solid 79 66 5 1,4-Butanediol (1) APC:D400 Adduct (1) Diphenylmethane Diisocyanate (2) White Crystalline Solid 82 83 * Numbers in parentheses indicate molar ratio of the monomer in the polymer. Example 7: Preparation of APC:Aminopropylmethylsiloxane-Dimethylsiloxane Adduct. 20g (0.02 mole NH 2 ) of aminopropylmethylsiloxane-dimethylsiloxane copolymer (APDMS) having an amine equivalent weight of 1000 (AMS-162, Apollo Scientific) was dissolved in 10g of isopropanol in a suitable flask fitted with a mechanical stirrer, thermometer and N 2 feed. A solution of APC (5.6g, 0.02 mole) dissolved in 16g isopropanol was added to the APDMS solution and the temperature increased to a set point. The kinetics of this reaction were followed at different temperatures and shown to be complete within 20, 40 & 80 minutes at 80, 60 & 40°C respectively. 60°C was chosen as the preferred reaction temperature to reduce the possibility of acrylate homopolymerisation. After 60 minutes at 60°C the product was evaporated to dryness using a rotary evaporator to give 26g of a viscous gum. 1 H NMR confirmed the loss of the HEA acrylate double bond (5.8(d)/6.1(q)/6.4(d)). Peak assignments (Jeol GSX 400, 399.9MHz, CDCl 3 , ppm): ∼0.1 (Si-C H 3 ); 0.45 (Si-C H 2 -); 1.50 (Si-CH 2 -C H 2 -); 2.55 (combined multiplet, -C H 2 -NH-C H 2 -); 2.87 (-C H 2 -CO-); 3.71 (-C H 2 -OH); 4.22 (-COO-C H 2 -) Example 8a: Preparation of Allyl Isocyanate Adduct of Example 7. The adduct from Example 7 (23g) was dissolved in THF (90g) in a suitable flask fitted with a mechanical stirrer, thermometer and N 2 feed. The flask and contents were heated to 45°C to aid dissolution. A solution of allyl isocyanate (1.5g) in THF (3.0g) was quickly added. A small exotherm was observed and the temperature was then raised to 60°C and held for 1 hour. FT-IR spectroscopy of the liquor after this time showed no characteristic peak for the isocyanate stretch at ∼2259cm -1 . The solvent was evaporated to give a very viscous gum. 1 H NMR (in CD 3 OD) confirmed that the product was the desired allyl derivative: (Jeol GSX 400, 399.9MHz, CDCl 3 , ppm): ∼0.1 (Si-C H 3 ); 0.46 (Si-C H 2 -); 1.57 (Si-CH 2 -C H 2 -); 2.59 (-C H 2 -COO-); 3.08 (b, C H 2 -N-C H 2 & CONH-C H 2 -); 3.30 (N + (CH 3 ) 3 ); 3.49/3.8/4.1/4.25 (-COOC H 2 C H 2 OP(OO-)OC H 2 C H 2 -N-); 4.22 (-COO-C H 2 -); 5.05/5.15/ 5.87 (allyl-C H =C H 2 ) Example 8b: Preparation of a Silicone/APC/Al Macromer 7.4g of APC was weighed into a 250ml r.b. flask fitted with stirrer, thermometer and nitrogen blanket. 18.0g of iPA solvent was added and the mixture was heated to 60°C. The APC completely dissolved at about 50°C. 30g of AMS 162 was added with a wash of a further 7.0g of iPA. The temperature was held at 60°C for 15 min and then raised to reflux (ca. 80°C). After 1h the reaction was cooled to 40°C and 2.1g of allyl isocyanate (Al) (Aldrich) added with a wash of 1.4g of iPA. An exotherm was noted and the mixture was heated to reflux for 1 h. After cooling, FT-IR spectroscopy confirmed the reaction of all isocyanate by loss of the N=C=O stretch. Removal of the solvent under vacuum to yield a thick gum and subsequent 1 H NMR analysis of this product confirmed the expected structure for the adduct. Example 9: Preparation of APC-Polydimethylsiloxane using an amine-functional PDMS, APC and an unsaturated isocyanate. 11.2g of APC (0.04 mole) and hydroxyethyl methacrylate (30.5g) were charged into a flask fitted with a thermometer, mechanical stirrer and N 2 blanket. The contents were stirred at room temperature until a clear solution was obtained. Hydroquinone (ca. 0.001 g) was added (to inhibit the premature polymerisation of the hydroxyethyl methacrylate) followed by 40g (0.04 mole) of aminopropylmethylsiloxane-dimethylsiloxane copolymer. The temperature was raised to 60°C and after about 20 minutes the solution cleared. The reaction was maintained at 60°C for 1 hour. The reaction was then cooled to 30°C and 8.0g (0.04 mole) of dimethyl meta-isopropenyl benzyl isocyanate (m-TMI, Cytec Industries) added with good stirring. This reacts selectively with the secondary amine and not the alcohol group of the hydroxyethyl methacrylate. A small exotherm was observed and the temperature was then raised to 55°C and held for 1 hour. The product was obtained as a 67% solution in hydroxyethyl methacrylate. Examples 10-18: The preparation of an APC-Polydimethylsiloxane adducts suitable for use in contact lens formulations. Using a synthetic procedure based on that described for Example 9, macromers suitable for use in contact lens manufacture were made using the components described in Table 2: APC-Silicone macromers for contact lens formulation Example # Silicone Other Amine Isocyanate Cap Adductor Solvent 10 AMS-162 - TMI - APC IPA 11 AMS-162 - TMI - APC DMA 12 AMS-162 - TMI - APC IPA/Hex 13 DMS-A12 - TMXDI BAM APC IPA 14 DMS-A12 - HMDI HEMA APC Hexanol 15 DMS-A15 - TMI - APC HEMA 16 DMS-A15 JED600 TMXDI BAM APC IPA 17 DMS-A15 ED TMXDI BAM APC IPA/Hex 18 DMS-A15 JED600 TMXDI TMI APC IPA The term "Cap" is used to denote the group which "end-caps" to product. The usual order of reaction is the Michael addition followed by addition of a cap and then a diisocyanate to extend the chain. The term "other amine" is used to denote any diamine for which the ratio of diisocyanate is adjusted such that some chain extension is achieved using the "other amine" before capping is carried out. Example 19: Generic Method for Contact Lens Preparation and Evaluation The contact lens formulation (macromer/comonomers/initiator/crosslinker) was placed into a glass vial and the mixture degasssed for 10 mins with N 2 before dispensing known amounts into polypropylene contact lens moulds (to give -3.0 D power lenses). The moulds were then sealed and UV cured for 1 hour using a Blak-Ray longwave UV lamp model B100AP. The lenses were removed from the mould by soaking in high purity water for 1 hour. They were then soaked in a 70:30 water IPA solution for 2 hours and in borate buffered saline for a further hour. The lenses were then bottled in buffer. A visual assessment of the lenses was made and this was recorded. Lenses were placed in vials that were filled with buffer solution. They were then sterilised by autoclaving at 120°C for 30 mins. A visual assessment of the lenses was made and this was recorded. The equilibrium water content (EWC) of the lens was determined by firstly removing excess (free) water from the lens surface by use of filter paper. The lenses were then placed on a Pyrex dish containing drierite and microwaved for 5 minutes on full power (800 watts) and reweighed. The EWC was then calculated as follows: EWC (%) = hydrated weight of lens - dry weight of lens hydrated weight of lens x 100% The oxygen permeability (Dk) of the lenses was determined by use of Mocon's OptiPerm™ technology according to their SOP#70-006, designed for measuring the Dk value of hydrophilic contact lens materials (Mocon/Modern Controls Inc., 7500 Boone Avenue North, Minneapolis, Minnesota, 55428 USA). In the cases where the Michael-type adduct is prepared using hydroxyethyl methacrylate as a solvent, this is usually to avoid using a solvent in the formation of contact lenses. This allows direct formulation into hydroxyethyl methacrylate-based lenses and the hydroxyethyl methacrylate is not recovered from the Michael reaction. Examples 20-23: The preparation of a moulded contact lenses using selected adducts from Examples 9-18 Lens formulations using macromers of the invention. Example # Macromer Example # Macromer (g) NNDMA (g) TRIS (g) EGDMA (g) Darocur (g) 20 9 1.2438 0.7069 0.6575 - 0.0230 21 12 1.2523 0.6604 0.6336 0.025 0.025 22 13 1.8291 0.7503 0.5773 0.0532 0.0311 23 16 1.5841 0.2610 0.7794 0.0557 0.025 Typical examples of the properties of the lenses formed are shown in Table 4 below. Lenses were clear upon hydration and could be made with a wide range of EWCs. Oxygen permeability could be altered by formulating with more silicone content. Properties of lenses made using macromers of the invention. Example # Appearance (post UV cure) EWC (%) Dk x 10 10 (ccO 2 /cm 2 sec mmHg) 20 Clear, colourless 24.7 21 Clear, colourless 18.4 22 Clear, colourless 31.0 81.9 23 Clear, colourless 11.3 Biological properties of lenses made from the invention were also favourable compared to commercially available hydrogel and silicone hydrogel lenses. Lenses were assessed using a UV detection method at 280nm (Table 5): Total protein adsorption to various lens types. Example # Lens Type Total Protein Adsorption (mg protein/lens) Ewc (%) (ccO 2 /cm 2 sec mmHg) D k + 10 10 Omafilcon A Hydrogel 9.37 ± 1.94 62 27 Balafilcon A Silicone Hydrogel 11.35 ± 2.59 36 99 22 Invention 5.28 ± 2.00 31 81.9 Example 24: Preparation of an APC-trimethoxysilane based adduct as a coating formulation. 11 g (0.039 mol) of APC were dissolved in 50ml IPA with gentle warming and stirring under an atmosphere of N 2 . Once clear, 6.80g (0.039 mol) of 3-aminopropyl trimethoxysilane (3-APTMS) were added and the reaction mixture bought to reflux for 1 hour. 1 H & 13 C NMR showed conversion to the Michael adduct and proton COSY was used to assign the peaks. 1 H NMR (CDCl 3 , 400MHz, ppm): 0.61 (2H, m, Si-C H 2 -), 1.20 (d, exchanged iPA -CH 3 ), 1.60 (2H, m, Si-CH 2 - CH 2 -), 2.55 (2H, t, C H 2 -COO-), 2.60 & 2.88 (2H each, t, C H 2 -NH-C H 2 ), 3.42 (9H, s, N + (C H 3 ) 3 ), 3.52 (integral shows some exchange with iPA has occurred, C H 3 -O-Si), 3.80 (2H, b, C H 2 -N + (CH 3 ) 3 ), 4.10 (2H, b, COO-CH 2 -C H 2 -O-P), 4.21, (m, exchanged iPA (m, -C H OH), 4.24 (2H, b, COO-C H 2 -), 4.29 (2H, b, P-O-C H 2 -CH 2 - N + (CH 3 ) 3 ). 13 C NMR (CDCl 3 ) further su pports assignment of structure with characteristic peaks, e.g. 172 ( C =O), 54.9 (N + ( C H 3 ) 3 ). FT-IR indicates carbonyl/ester, Si-O-CH 3 and Si-O-CH(CH 3 ) 2 present. To the cooled IPA solution was added 3.29g of hexamethylene diisocyanate (0.0196mol) and the reaction mixture taken to reflux for a further hour. FT-IR confirmed reaction of the isocyanate by disappearance of the N=C=O stretch at ∼2230cm -1 . 1 H NMR & 13 C confirmed formation of the APC-TMS dimer. 1 H NMR (CDCl 3 , 400MHz, ppm): 0.55 (2H, m, Si-C H 2 -), 1.20 (d, exchanged iPA -CH 3 ), 1.30 (2H, b, C H 2 -CH 2 -CH 2 -NHCO), 1.48 (2H, b, C H 2 -CH 2 -NHCO), 1.62 (2H, m, Si-CH 2 - CH 2 -), 2.57 (2H, t, C H 2 -COO-), 3.12 (4H, b, C H 2 -NH-C H 2 ), 3.42 (9H, s, N+(C H 3 ) 3 ), 3.48 (2H, b, C H 2 -NHCO), 3.52 (integral shows some exchange with iPA has occurred, C H 3 -O-Si), 3.80 (2H, b, C H 2 -N + (CH 3 ) 3 ), 4.05 (2H, b, COO-CH 2 -C H 2 -O-P), 4.21, (m, exchanged iPA (m, -C H OH), 4.24 (2H, b, COO-C H 2 -), 4.29 (2H, b, P-O-C H 2 -CH 2 - N + (CH 3 ) 3 ). 13 C NMR (CDCl 3 ) further supports assignment of structure with characteristic peaks, e.g. 172 ( C =O), 154 (-NR C ONH-), 54.9 (N + ( C H 3 ) 3 ), 26, 30 & 41 (dimer bridging methylene groups) Example 25: Biological evaluation of a coating based on example 24. A solution of 20mgml -1 of the APC-trimethoxysilane compound described in example 24 in iPA was coated onto PET at a speed of 3mmsec -1 . The PET strip was allowed to air dry for 30 minutes before the coating was cured in an oven at 70°C overnight. The coated PET samples were assessed for their ability to resist adsorption of protein using an enzyme immunoassay based on fibrinogen. The data shown in Table 6 shows that the coating substantially reduced the amount of fibrinogen that adsorbed to the surface compared to the uncoated control. Reduction of fibrinogen adsorption for coatings of Example 24. Sample Type Absorbance @ 450nm (n=7) Standard Deviation % Reduction of Fg Adsorption Uncoated PET 1.795 0.350 N/A PET coated as per example 15 0.551 0.090 69.3 A similar enzyme immunoassay that shows the extent of bacterial adhesion ( E.coli ) to substrates was used to challenge PET samples coated with the invention of Example 24. The data shows substantial reduction of bacterial adhesion to the surface of the coated sample relative to the control. Reduction of E.coli adhesion for coatings of Example 24. Sample Type Absorbance @ 450nm (n= 5 ) Standard Deviation % Reduction of E.Coli Adhesion Uncoated PET 0.639 0.071 N/A PET coated as per example 15 0.149 0.021 76.8

Claims: A zwitterion containing an adduct having the formula (I) wherein X is an electron withdrawing group selected from the group consisting of carbonyl and sulphone groups, sulphonium and phosphonium salts; R is a group OR' wherein R' consists of an alkanediyl group joined to a zwitterionic group Z having the general formula (II) in which the moieties A 1 and A 2 , which are the same or different, are -O-, -S-, -NH- or a valence bond, and W + is a group comprising an ammonium, phosphonium or sulphonium cationic group and a group linking the anionic and cationic moieties. R 3 and R 4 are individually selected from the group consisting hydrogen, linear and branched alkyl, alkenyl, and alkynyl groups, alkoxycarbonyl, alkylaminocarbonyl, cycloalkyl, cycloalkenyl, cycloalkynyl, haloaryl, haloalkyl, aryl, alkaryl, aralkyl, alkoxyaryl, alkoxyalkyl, oligoalkoxyalkyl, aminoalkyl, mono-and di-alkylaminoalkyl, arylaminoalkyl, N-aryl-N-alkylaminoalkyl and -aminoaryl, acyloxy, acyloxyalkyl, acylaminoalkyl, N-diacyl-iminoalkyl groups, alkylaminocarbonyl, organosilane and organosiloxane groups and any of the above groups substituted with a zwitterionic group Z or an isocyanate group; and R 1 and R 2 are individually selected from hydrogen and C 1 -C 12 alkyl groups. An adduct according to claim 1, wherein W + is a group of formula -W 1 -N + R 5 3 , -W 1 -P + R 6 3 , -W 1 -S + R 6 2 or -W 1 -Het + in which: W 1 is alkanediyl of 1 or more, preferably 2-6 carbon atoms optionally containing one or more ethylenically unsaturated double or triple bonds, disubstituted-aryl (arylene), alkylene arylene, arylene alkylene, or alkylene aryl alkylene, cycloalkanediyl, alkylene cycloalkyl, cycloalkyl alkylene or alkylene cycloalkyl alkylene, which group W 1 optionally contains one or more fluorine substituents and/or one or more functional groups; and either the groups R 5 are the same or different and each is hydrogen or alkyl of 1 to 4 carbon atoms, preferably methyl, or aryl, such as phenyl, or two of the groups R 5 together with the nitrogen atom to which they are attached form an aliphatic heterocyclic ring containing from 5 to 7 atoms, or the three groups R 5 together with the nitrogen atom to which they are attached form a fused ring structure containing from 5 to 7 atoms in each ring, and optionally one or more of the groups R 5 is substituted by a hydrophilic functional group, and the groups R 6 are the same or different and each is R 5 or a group OR 5 , where R 5 is as defined above; or Het is an aromatic nitrogen-, phosphorus- or sulphur- containing ring. An adduct according to claim 2 wherein the zwitterionic group of the formula (II), has the general formula (III): where the groups R 7 are the same or different and each is hydrogen or C 1-4 alkyl, and m is from 1 to 4, preferably in which the groups R 7 are the same more preferably and are methyl. An adduct according to any preceding claim, wherein group R' has the structure An adduct according to any preceding claim, wherein X is a carbonyl group. An adduct according to any preceding claim, wherein R 1 and R 2 are individually selected from hydrogen or C 1 -C 4 alkyl, preferably hydrogen. An adduct according to any preceding claim, wherein R 4 is an organosiloxane having the formula (VII) in which R 8 -R 13 are each selected from a valence bond, hydrogen, branched and straight C 1-12 alkyl, C 6-18 aryl, C 6-18 alkaryl, C 6-18 aralkyl, C 2-12 alkenyl, C 2-12 alkynyl and O-Si-(R 14 ) 3 , where R 14 is C 1-12 alkyl or C 6-18 aryl, any of which may be substituted by a primary, secondary or tertiary amine group, and n is 0-300, provided that at least one of the groups R 8 -R 13 is selected from the group consisting of a valence bond, C 1-12 alkanediyl, C 2-12 alkenediyl and C 2-12 alkynediyl and is covalently bonded to the nitrogen atom of adduct (I) and (VII) has a molecular weight of 300-20000. An adduct according to claim 7, wherein R 8 and R 13 are selected from methanediyl, ethanediyl, propanediyl and butanediyl, and are both covalently bound to the nitrogen atom of individual adducts (I). An adduct according to claim 7 or claim 8, wherein the groups R 9 -R 12 are individually selected from the group consisting of C 1-6 alkyl groups, preferably C 1-4 alkyl groups, most preferably methyl, and are preferably the same. An adduct according to any of claims 1 to 6, wherein R 3 comprises a reactive group capable of forming a covalent bond a polymer or monomer bearing a site of unsaturation, or to a substrate. An adduct according to claim 10, wherein the reactive group is isocyanate or (meth)acryloyloxy. An adduct according to any preceding claim having the the formula (X), (XI), (XII), (XIII) or (XIV) wherein each R 19 , R 20 , R 21 , R 23 , R 24 , R 25 and R 26 are individually selected from the group consisting of hydrogen, C 1-6 alkyl, C 6-18 aryl, C 6-18 aralkyl, C 6-18 alkaryl, and C 2-6 alkenyl, preferably C 1-6 alkyl, most preferably methyl or ethyl; each R 22 is individually selected from the group consisting of C 1-6 alkanediyl, C 2-6 alkendiyl and C 2-6 alkynediyl, preferably C 1-6 alkanediyl; R 27 is selected from the group consisting of hydrogen, C 1-6 alkyl, C 6-18 aryl, C 6-18 aralkyl, C 2-6 alkenyl, C 6-18 alkaryl, preferably hydrogen or C 1-4 alkyl; each R 28 is individually selected from the group consisting hydrogen, linear and branched alkyl, alkenyl, and alkynyl groups, alkoxycarbonyl, alkylaminocarbonyl, cycloalkyl, cycloalkenyl, cycloalkynyl, haloaryl, haloalkyl, aryl, alkaryl, aralkyl, alkoxyaryl, alkoxyalkyl, oligoalkoxyalkyl, aminoalkyl, mono-, di- and tri- alkylaminoalkyl, arylaminoalkyl, N-aryl-N-alkylaminoalkyl and - aminoaryl, acyloxy (including alkenoyloxy), acyloxyalkyl (including alkenoyloxyalkyl), acylaminoalkyl, N-diacyl-iminoalkyl groups, alkylaminocarbonyl, organosilane and organosiloxane groups and any of the above groups substituted with a zwitterionic group Z or an isocyanate group; n is an integer of 1 to 500; p is an integer of 1 to 50; q is an integer of 1 to 500; r is an integer of 1 to 50; and s is an integer of 0 or 1. An adduct according to claim 12, wherein R 19 , R 20 , R 21 , R 23 , R 24 , R 25 and R 26 are all methyl and R 22 is selected from ethanediyl, propanediyl and butanediyl. An adduct according to any of claims 1 to 6 wherein R 3 or R 4 are selected from the group consisting of the formula (VIII) wherein R 29 - R 36 are individually selected from the group consisting of hydrogen, C 1-6 alkyl, C 6-18 aryl, C 6-18 aralkyl, C 6-18 alkaryl and C 2-6 alkenyl; R 37 and R 38 are individually selected from the group consisting of a valence bond, hydrogen, C 1-6 alkyl, C 6-18 aryl, C 6-16 aralkyl, C 2-6 alkenyl aminoalkyl, mono-, di-and tri-alkylaminoalkyl, arylaminoalkyl, N-aryl-N-alkylaminoalkyl and - aminoaryl; a is an integer of 0-10, b is an integer of 0-500, a is an integer of 0-10; and (VIII) has a molecular weight of 100-10000. An adduct according to claim 14, wherein the adduct has the formula (XV), (XVI) or (XVII) wherein R 39 - R 46 are individually selected from the group consisting of hydrogen, C 1-4 alkyl, C 6-18 aryl, C 6-18 aralkyl, C 6-18 alkaryl; R 47 is selected from the group consisting of hydrogen, C 1-4 alkyl, C 6-18 aryl, C 6-18 aralkyl, C 6-18 alkaryl, and C 2-6 alkenyl; and each R 28 is individually selected from the group consisting hydrogen, linear and branched alkyl, alkenyl, and alkynyl groups, alkoxycarbonyl, alkylaminocarbonyl, cycloalkyl, cycloalkenyl, cycloalkynyl, haloaryl, haloalkyl, aryl, alkaryl, aralkyl, alkoxyaryl, alkoxyalkyl, oligoalkoxyalkyl, aminoalkyl, mono-, di- and tri- alkylaminoalkyl, arylaminoalkyl, N-aryl-N-alkylaminoalkyl and - aminoaryl, acyloxy (including alkenoyloxy), acyloxyalkyl (including alkenoyloxyalkyl), acylaminoalkyl, N-diacyl-iminoalkyl groups, alkylaminocarbonyl, organosilane and organosiloxane groups and any of the above groups substituted with a zwitterionic group Z or an isocyanate group. An adduct according to any of claims 1 to 6 wherein R 3 is an organosilane group having the general formula (IX) wherein R 16 , R 17 and R 18 are selected from the group consisting of hydrogen, branched and straight C 1-12 alkyl, C 6-18 aryl, C 6-18 alkaryl, C 6-18 aralkyl, C 2-12 alkenyl and C 2-12 alkynyl; R 15 is selected from the group consisting of a valence bond, branched and straight chain C 1-12 alkanediyl, straight and branched C 2-12 alkenediyl and straight and branched C 2-12 alkynediyl; and (IX) Is connected to the N atom of (I) through R 15 . A method for the production of an adduct by the Michael-type addition of a compound having the formula (XVIII) with a compound having the formula (XIX) H 2 NR 51 to form a zwitterion containing compound having the formula (XX) wherein X is an electron-withdrawing rang group selected from carbonyl and sulphone groups sulphonium and phosphonium-salts R 48 is a OR 48' , where R 48' consists of an alkanediyl group joined to a zwitterionic group Z having the general formula (II) in which the moieties A 1 and A 2 , which are the same or different, are -O-, -S-, -NH- or a valence bond, and W + is a group comprising an ammonium, phosphonium or sulphonium cationic group and a group linking the anionic and cationic moieties; R 51 is selected from the group consisting hydrogen, linear and branched alkyl, alkenyl, and alkynyl groups, alkoxycarbonyl, alkylaminocarbonyl, cycloalkyl, cycloalkenyl, cycloalkynyl, haloaryl, haloalkyl, aryl, alkaryl, aralkyl, alkoxyaryl, alkoxyalkyl, oligoalkoxyalkyl, aminoalkyl, mono- and di-alkylaminoalkyl, arylaminoalkyl, N-aryl-N-alkylaminoalkyl and -aminoaryl, acyloxy, acyloxyalkyl, acylaminoalkyl, N-diacyl-iminoalkyl groups, alkylaminocarbonyl, organosilane and organosiloxane groups; and R 49 and R 50 are individually selected from hydrogen and C 1 -C 12 alkyl groups. The method according to claim 17, wherein R 49 and R 50 are selected from hydrogen or C 1 -C 4 alkyl groups, most preferably both hydrogen. The method according to claim 17 or 18, wherein (XIII) has the formula (XXI) The method according to claim 17 to 19; wherein compound (XX) undergoes a second reaction with a compound (XXII) which is an isocyanate or diisocyanate and is preferably selected from the group consisting of C 2-30 aliphatic, C 6-30 aromatic and C 6-20 alicyclic isocyanates or diisocyanates C 4-30 allyl isocyanates, C 4-30 isocyanatoalkylacrylates, and C 5-30 isocyanato alkylmethacrylates. The method according to claim 20, wherein compound (XXII) is selected from allyl isocyanate, dimethyl meta-isopropenylbenzylisocyanate, isophorone diisocyanate, hexamethylene diisocyanate and meta-tetramethylxylylene diisocyanate. The method according to any of claims 17 to 21, wherein R 48 , R 49 , R 50 , R 51 , R 52 and X have the same definitions as R, R 1 , R 2 , R 4 , R 3 and X respectively as defined in any of claims 2 to 11. The method according to any of claims 17 to 22, wherein the reaction is carried out in a solventless system. The method according to any of claims 17 to 22 wherein the reaction is carried out in the presence of a solvent, preferably an organic solvent selected from C 1-8 alcohols, C 1-8 chlorinated hydrocarbons and ethers C 1-8 , preferably secondary C 1-8 or tertiary alcohols. The method according to claim 24, wherein the alcohol is selected from isopropanol, isobutanol, tertbutanol and hydroxyethylmethacrylate, preferably isopropanol. A liquid composition comprising an adduct according to any of claim 1 to 16 and a liquid composition comprising a solvent in which the polymer or adduct is dissolved or suspended. An article produced from or coated by a composition comprising an adduct according to any of claims 1 to 16. An article according to claim 27, wherein the article is a contact lens. An article according to claim 28, wherein R 3 comprises an organosiloxane, preferably an aminopropylmethylsiloxane-dimethylsiloxane copolymer. A polymer produced by the homo-polymerisation or co-polymerisation of an adduct according to any of claims 1 - 16, wherein the adduct is polymerised through a reactive group on R 3 , preferably an ethylenically unsaturated group or an isocyanate group. A polymer according to claim 30, produced by a polymerisation process selected from free radical, cationic, anionic and metal catalysed polymerisations, preferably free radical polymerisation. A process for coating a surface comprising applying a composition according to claim 26 to the surface of a polymer or metal and substantially removing the solvent. A process according to claim 32, wherein the surface is a reactive surface capable of forming at least one covalent bond with the coating polymer. A process according to claim 33, wherein the surface is metal and the coating polymer is formed by polymerisation of an adduct according to claim 16. A polymerisation process comprising the homo-polymerisation or co-polymerisation of an adduct according to any of claims 1 to 16 through polymerisable groups on R 3 , preferably ethylenically unsaturated or iso-cyanate groups. A process according to claim 35, wherein R 4 comprises an organosiloxane as defined in any of claims 7 to 9, and R 3 comprises a reactive group as defined in claim 10 or 11. A process according to claim 35, wherein R 4 comprises an organosiloxane as defined in any of claims 7 to 9, and R 3 comprises an organosilane as defined in claim 16 A process according to claim 35, wherein R 4 comprises an polyoxyalkylene as defined in claim 14 and R 3 comprises an organosilane as defined in claim 16. A process according to claim 35, wherein R 4 comprises an polyoxyalkylene as defined in claim 14 and R 3 comprises a reactive group as defined in claim 10 or 11.

Inventors: LEWIS ANDREW LENNARD, REDMAN RICHARD, LEWIS, ANDREW LENNARD, REDMAN, RICHARD
Applicants: BIOCOMPATIBLES UK LTD, BIOCOMPATIBLES UK LIMITED
Application year: 2000
Main classification: C07F7
IPC codes: C08L83, C08J5, G02B1, C08G77, C08G85, C07F9, C08G18, C08G65, G02C7