PREVENTION OF POST SURGICAL ADHESIONS USING A FIBRIN MONOMER SEALANT

Abstract: A method and a composition for preventing or reducing the incidence of post surgical adhesion formation is disclosed. The method involves application of fibrin monomer composition under polymerizing conditions to the surgical wound site. The fibrin monomer composition free of exogenous thrombin, free from proteins, enzymes or polymers foreign to the patient polymerize at the surgical wound site to form the fibrin polymer that provides hemostasis and promotes wound healing while functioning as a barrier/sealant. Autologous plasma proteins derived from the patient's blood may be added to the sealant composition before or during application to the surgical wound site.

Description: PREVENTION OF POST SURGICAL ADHESIONS USING A FIBRIN MONOMER SEALANT Field of the Invention This invention relates to the prevention of post surgical adhesions and, more particularly, concerns enhanced methods and compositions using a fibrin sealant to prevent such adhesions . Background of the Invention Formation of tissue adhesions between adjacent tissues is an adverse side effect of many surgical procedures. It is believed that following abdominal surgery the incidence of peritoneal adhesion formation may be as high as 90%. These post surgical adhesions often lead to pain, discomfort, immobility and, in the case of gynecological surgery, female infertility. Also, post surgical adhesions may even result in life-threatening bowel strangulation is some instances. Thus, there exists a large unmet need for a way to prevent post surgical adhesions, given the potential discomfort and medical risks they pose following routine surgery and the accompanying financial burden of remedying this adverse effect. A number of pathways have been investigated to reduce or prevent post surgical adhesions. One proposed mechanism involves the reduction of the inflammatory reaction at the wounded site following surgery. In this regard, the use of corticosteroids, NSAIDS, histamme antagonists and calcium channel blockers has been suggested. Another prevention method recommends the inhibition of coagulation at the wounded site using, e.g., heparin or oral anticoagulants. Still further methods entail the promotion of fibπnolysis through appropriate administration of, for example, flbrinolysm, Streptokmase, Urokmase and t-PA. More recently, barrier materials have been suggested for the prevention of post surgical adhesions. These include, but are not limited to, amniotic membrane, rubber, silver foil, Teflon, dextran, hyaluronic acid, Surgigel ® (regenerated cellulose) , Interceed® (TC7 oxidized, regenerated cellulose) , Polaxamer 407 (temperature dependent polymer) , Gore-Tex® (expanded polytetrafluorethylene) and SepraFilm® (hyaluronic acid derivative film) . The above materials and methods fall into two basic categories; those which do not work effectively, and those which may provide some efficacy but are limited m either their use or applicability. Accordingly, new efforts have continued in this area. The role of fibrin sealants in surgical procedures generally has been reviewed for many years. The role of fibrin sealants preventing or reducing of post surgical adhesions has been investigated over the past few years and is not totally understood at this time. Indeed, the literature m this area seems somewhat divided. Several researchers have reported an improvement in post surgical adhesion prevention using fibrin sealants. For example, the incidence of parovaπan adhesions was significantly reduced in women subjected to laser vaporization of endometriomas and fibrin sealant (Donner, J. et al . ; J Gynecol Surg 7:163, 1991), mcisioned and colonic adhesions formation was reduced in abraded rabbit uterine horns (Chmielewski, G. et al.; The Ameri can Surgeon Vol 58 No. 9; 590, 1992), mtrabdommal adhesion formation was reduced in rats (deVirgilio, et al.; Aarcn Surg Vol 125; 1378, 1990), epidural scar formation in rats was reduced after laminectomy (Vaquero, J. et al.; Acta Neurochir (Wien) 120; 159-163, 1993) and flexor tendon adhesion formation in rabbits was reduced following a partial laceration of the flexor tendon (Fryknra, E. et al.; Journal of Hand Surgery Vol. 18A, No. 1 ; 68, 1993). Others reporting on the use of fibrin sealants to prevent post surgical adhesions have not been so positive. For example, fibrin sealant was found to have no statistically significant effect in preventing peπvascular adhesions following artenotemics of the femoral and carotid arteries of dogs (Dickinson, C. et al., Vascular Surgery; 15, 1993); fibrin sealant did not prevent adhesion formation in colonic anastomoses in the rat (van der Ham, A., et al.; J Surgical Research, 55; 256-260, 1993) and fibrin sealant did not reduce post surgical adhesions following ovarian reconstruction in the rabbit (Bilgm, T., et al.; Gynecol Obstet Invest 39; 186- 187, 1995) . WO 92/22312 to Wadstrom discloses combinations of fibrin sealants and biocompatible polymers reportedly useful for the prevention of post surgical adhesions. WO 92/22312 reports that fibrin sealants alone provide a wound healing effect which results in strong scar formation and does not prevent adhesions. The viscosity enhancing polymers are useful to allow application of the otherwise watery sealant components to vertical surfaces and also prevents adhesions. These polymers are high molecular polyglycans or polysaccharides . WO 96/22115 discloses a self supporting sheet material of cross-linked fibrin having a particular range of pore sizes to prevent or reduce post surgical adhesions. The use of spray application to prepare these and similar sheets is reported in WO 98/02098. These sheets are described as generally non- adherent and non-hemostatic and are preferably used in conjunction with a known fibrin sealant which does possess adherence and hemostatic capabilities. These sheets are prepared using high concentrations of fibrinogen and high dose thrombin to obtain the desired structure regarding pore size and distribution (preferably <20 μm, more preferably < 5 μm, most preferably < 1 μm) . Also, the sheet is pre-formed outside of the body and needs to be applied as a solid material, i.e., not applied as a spray or liquid. Since fibrin sealants are used increasingly for hemostasis and fluid and air leakage m surgical procedures, it is important that a sealant is used which does not promote adhesion formation. Also, since fibrin is a part of the natural healing process it seems desirable to attempt to use fibrin in resolving the post surgical adhesions problem, as well. It would be preferable to be able to accomplish this without polymer additives, without high concentrations of fibrinogen, without subjecting the patient to high dose thrombin and, preferably, without the need for preformed sheets which must, in turn, be used with standard sealants. A more natural, single-step sealant/hemostat/adherent/ adhesion barrier, preferably applicable by spraying and preferably free of added thrombin would be a significant advance in the art. Brief Description of the Figures Fig. 1 Illustrates a rabbit paw flexor tendon per the experiments of Example 2. Fig. 2 Is a graph showing variation of dG' /dt with time per Example 2. Fig. 3 Is a graph illustrating the adhesion experiment of Example 3. Fig. 4 Is a graph comparison of Vivostat™, Tissucol© and BeriplastO kinetic rate constants based on a second orαer reaction over the initial 200 seconds of polymerisation. Fig. 5 Is a graph illustrating adhesion strength at first breaking point at various polymerisation times for of Vivostat™, Tissucol® and Beπplast®. Fig. 6 Is a graph illustrating elongation at first breaking point at various polymerisation times for Vivostat™, Tissucol® and Beπplast®. Summary of the Invention In accordance with the present invention it has been found that a fibrin polymer film formed by applying materials most closely resembling the natural clotting materials are useful in a method to prevent or reduce the incidence of surgical adhesion formation. Preferred embodiments involve application of a fibrin monomer under polymerizing conditions to the surgical wound site which fibrin is preferably patient- derived, i.e., a sealant wherein the blood/clotting components are autologous to the patient. Unexpectedly, in addition to this improved prevention of adhesions, the more chemically- natural clots, especially the flbnn-monomer based fibrin polymer, also functions as a fibrin sealant, i.e., has adherence, provides hemostasis and promotes wound healing while also functioning as a barrier. In preferred embodiments the novel methods of this invention conveniently use one or more plasma proteins in addition to fibrinogen/fibrin derived from the patient's own blood so as to be autologous. Further, the sealant material is preferably substantially free of any added or exogenous enzymes, e.g., thrombin, etc., which catalyze the cleavage of flbπnopeptides A and/or B from fibrinogen. Preferably a fibrin monomer solution is sprayed over the wounded surgical site. Detailed Description of the Invention The present invention is founded upon the idea that providing a fibrin polymer which can act as a barrier, while most closely resembling the natural clotting materials, provide enhanced reduction in the incidence of post surgical adhesion formation. The enhancement can be realized as increased convenience and/or diminished immunogenic or inflammatory response and/or superior post surgical adhesion prevention. The methods of the present invention rely, therefore, on several factors which individually provide improvements over the prior art and which cumulatively provide an optimum result. The factors, in no particular order, include applying fibrin monomer instead of fibrinogen, using fibrin substantially free of thrombin or other flbrmopeptide- cleavmg enzyme, using autologous fibrin, using freshly prepared fibrin which has not been denatured in processing, using fibrin with co-harvested plasma proteins, using fibrin with lower concentrations and eliminating the need for polymer additives . Accordingly, methods employing one, some or all of these aspects are considered to be a part of the present invention. As mentioned above, it has been found that the fibrin polymer resulting from the present methods is able to reduce or prevent post surgical adhesions over a variety of fibrin concentrations and need not be a high concentration material when compared to the prior art. Further, there is no need to pre-form sheet-like materials ex vivo for application to a surgical wound site and no need for additional sealant layers to be used. The present fibrin sealants, when applied using the methods described herein, possess not only good barrier qualities to resist post surgical adhesion formation but also provide hemostasis, fluid sealing, adherence to the tissue and enhanced cell migration at the wound site. This enhanced cell migration is believed to provide improved angiogenesis and tissue repair. In one embodiment of the present invention an improved method of preventing or reducing the incidence of post surgical adhesions involves using a fibrin polymer formed from a fibrin monomer composition. This, in turn, can be conveniently accomplished by applying, e.g., spraying, a fibrin monomer composition onto the surgical wound site under polymerizing conditions to form the fibrin polymer. The fibrin monomer composition has the advantage that it can polymerize mucn more rapidly than prior art fibrmogen/thrombm systems and does not therefore require added polymer, as in WO 92/22312 to Wadstrom, or "pre-form" time as in WO 98/02098 in order to set up and stay in place even on vertical surfaces. This more rapid polymerization is because the fibrin monomer has had at least one of the fibnnopeptides of fibrinogen already cleaved and polymerization can begin virtually immediately. U.S. 5,750,657 to Edwardson et al. Describes a preferred fibrm monomer composition which is "nondynamic", i.e., prepared such that it is inhibited from polymerizing until the nondynamic conditions are reversed. A preferred way to render fibrm monomer nondynamic is to prepare it as a low pH composition. For example, aqueous fibrm monomer solutions having pH 2-5 are suitable. These can be co-applied with sufficient higher pH buffer, e.g., a pH 10 buffer, to raise the pH and trigger the fibrm monomer polymerization. The advantages of the fibrm monomer method include the multifunctional aspects of the resulting single polymer, i.e., hemostat/fluid seal/adhesive/bamer, and the advantage that no added or exogenous thrombin is required. Also, lower fibrm concentrations, on the order of 10-30 mg/ml and preferably 15- 25 mg/ml, are not only adequate, but preferred. Although any fibrm monomer concentration greater than 10 mg/ml, e.g., 10- 200 mg/ml, could be used. If it is desired to make an ex vivo preformed sheet, the fibrm monomer method is still advantageous for the reasons mentioned aoove . In either case, the fibrm monomer can be fibrin I, fibrm II, des ββ fibrin or mixtures of any of these depending upon the enzyme used (thrombin or other enzyme which catalyzes the cleavage of flbπnopeptide A and/or B from fibrinogen) . Preferably, especially in the case of thrombin, the enzyme is removed from the fibrin monomer composition. Additional parameters for preparing and applying fibrin monomer solutions are known from U.S. 5, 750,657 to Edwardson et al., an exemplary combination being the co-application of a pH 4 aqueous solution of 15-25 mg/ml of fibrin I monomer with pri 10 acetate buffer in a ratio of " XI fibrin to buffer. As discussed above, the fibrm monomer method provides the option that a fibrm polymer can be applied and used in the present methods while avoiding application of thrombin or thrombin-like enzyme to tne patient. This turns out to be an enhanced method in and of itself. That is, prevention or reduction of the incidence of post surgical adhesions using fibrm polymer/fibrin sealant materials is enhanced where no added or exogenous thromom or thrombm-like enzyme are used. It has been found that high dose thrombin as is used in prior art sealant methods and the prior art post surgical adhesion reduction methods as described in WO 96/22115 and WO 98/02098 may cause an inflammatory response in tissues, organs and, particularly, wound sites. In a surgical wound site it is believed that added thrombin can cause an inflammatory response which may itself be negative and which may indirectly "kick-start" the wound healing process before the prior art sealant has polymerized sufficiently to form a barrier. The result could actually be some local acceleration of adhesion formation. Thus, although the prior art may require thrombin to produce the desired barrier layer, the presence of the thrombin in the barrier layer and in the co-applied sealant (in the case of the two part adhesion prevention process of WO 98/02098) may have an opposite and unwanted effect. Further, from an immunological perspective there is a possible risk, after an initial thrombin sensitization, to a more pronounced immune response upon a future challenge, e.g., in future surgery using fibrm sealant incorporating thrombin. Finally, recent evidence suggests that thrombin retained with fibrin sealant on blood vessels, even intact vessels, permeates the vessel wall and is measurable in the bloodstream. This could increase the risk of adverse thrombogenic events, especially at tne higher doses of thrombin suggested in prior art sea ant/barπer methods. Thus, preferred methods of preventing or reducing the incidence of post surgical adhesions involve the formation of a fibrin polymer either from a fibrin monomer composition where no added exogenous thrombin is required, or from a flbrmogen/thrombm system where the thrombin is separated, removed or otherwise not applied to the patient following the appropriate catalysis of the flbnnogen-to-fibrin polymer conversion. Although this method is described with regard to being substantially free of exogenous or added thrombin, it should be appreciated that it may apply to other enzymes capable of catalyzing the cleavage of flbnnopeptide A and/or B from fibrinogen, as well. Although the other enzymes known in the art, e.g., batroxobm, Ancrod and the like, do not precipitate the issues described above for thrombin but can nonetheless be removed from fibrm polymer-forming compositions where a sealant/barrier substantially free from any foreign proteins is desired. Since materials most natural to the patient are now believed to provide a more natural biologic response, methods of preventing or reducing the incidence of post surgical adhesions using a fibrm sealant/fibrin polymer which is substantially free from proteins, enzymes or polymers foreign to the patient are part of the present invention. Although the exact mechanism is not understood, it is possible that minimizing foreign agents minimizes the inflammatory response of the wounded tissues where post surgical adhesions are expected. Althougn some workers in the prior art have attempted to use antnnflamatory agents to prevent or reduce the incidence of post surgical adhesions, others working with fibrm sealants in post surgical adhesion methods have ignored the antnnflamatory theory and essentially viewed the sealants as physical barriers. In accordance with the present invention fibrm sealants/polymers substantially free from proteins, enzymes or polymers exogenous to the patient provide the physical barrier aspects while reducing the possibility of accelerating adhesion formation which may otherwise result from an inflammatory response. In accordance with this autologous aspect of the present invention, it shouiα be understood that the term "substantially free" refers to the fact that the sealant materials applied to prevent or reduce the incidence of post surgical adnesions contain less than 10% by weight and preferably less than 5% and more preferably less than 1% and most preferably between 0.5 and 0% of proteins, enzymes or polymers which are foreign or exogenous to the patients. Pursuant to this autologous method the fibrin sealant/fibrin polymer can be applied as autologous fibrinogen and autologous thrombin. This flbrmogen/thrombm sealant may also include autologous stabilizers or antiflbrmolytics such as is described in U.S. Serial No. 60/069,652 filed December 9, 1997. If a proteolytic enzyme other than autologous thrombin is used to treat the fibrinogen, then the fibrinogen applied needs to be at least 90% free of this enzyme as described above. Similarly, if a fibrm monomer composition is applied it should be at least 90% free of the enzyme used to prepare the autologous fibrm monomer from autologous fibrinogen. Further to these autologous methods, it has been found in accordance with the present invention that one or more additional autologous plasma proteins help provide a more cnemically natural clot material and, thereby, enhanced results in preventing or reducing the incidence of post surgical adhesions. Autologous plasma proteins, preferably selected from those which would otherwise be present in a natural clotting process can be added to the sealant components before or during application to the surgical wound site in accordance with the present methods. Alternatively, they can be coharvested in the process of producing the one or more autologous blood components which will form the fibrm sealant. For example, a process to prepare autologous fibrinogen may result in a natural cocktail including the and may be co-applied with the monomer. GB 97/11927.5 describes such compositions useful as fibrm sealants for hemostasis and sealing. These have now been found to additionally function as natural barriers to adhesion formation without the need for preforming sheets ex vivo, using multiple sheets or layers, or adding polymers. Thus, autologous blood components, such as fibrm monomer, may include one or more autologous proteins which are added or co- harvested and are selected from the group consisting of prothrombm, factor XIII (activatable) , plasmmogen, fibronectin, antithrombin III and factor X. Preferably, compositions useful herein include about 10-30 mg/ml of autologous fibrm monomer, about 10-40 μg/ml of autologous prothrombm and about 100-200 μg/ml of plasmmogen. They may further include 5-100 μg/ml of activable factor XIII and/or 45-150 μg/ml of fibronection and/or 2.0-7.0μg/ml of factor X and/or 50-200 μg/ml of antithrombin III, all such components being autologous to the patient receiving the anti-adhesion treatment . Also, it is now understood that certain processing steps may have an effect on the efficacy of the prevention of post surgical adhesions using fibrm polymers. For example, some fibrm sealants are subject to processes design to reduce the risk of viral infection. "Solvent/detergent" processes are reportedly helpful m reducing viral risk for certain viruses. Also, some fibrm sealant precursors are lyophilized so as to be commercially available in a reconstitutable, powder form. Many sealants processed under these relatively harsh conditions tend to "denature" the important plasma proteins, e.g., fibrinogen and thrombin. This, m turn, may explain the relatively high concentrations of such proteins in prior art sealant methods to facilitate polymerization. Even at these higher concentrations, polymerization is slow compared to components not subject to the solvent/detergent processes. To prevent or reduce the incidence of post surgical adhesions it is clear that fibr polymers formeα of blood proteins which have not oeen subjected to solvent/detergent processing anα/or lyophilization provide better results. Process steps believed to chemically and/or biologically denature clot-formmg blood proteins include the use of harsh chemicals and extreme temperatures . The present invention teaches fibrm sealants/fibrm polymers which are chemically more ak to natural clots m that they have fewer exogenous materials and/or have been subjected to less extreme processing. The physical structure may also closely resemble the natural clot or may take on a different structural make-up as described in a co-pending application U.S. Ser. No. 60/136,902 filed concurrently herewith. EXAMPLE 1 A fibrm sealant in accordance with the present methods was prepared as αescribed by Edwardson et al. in U.S. 5,750,657 and using a process and apparatus as disclosed by Holm, inter alia , in U.S. 5,741,428, U.S. 5,603,845, U.S. 5,824,230 and U.S. 5,958,253. Freshly drawn anti coagulated whole blood (120ml plus 17ml 4% trisodiurn citrate USP) was centrifugally separated and the resulting plasma (60ml) reacted with biot -batroxobm for 10 minute at 37°C. The acid soluble fibr I polymer produced was isolated by centrifugation and dissolved in 3.5 - 5.2ml 0.2M sodium acetate buffer (pH4) containing calcium ions. Approximately 6ml of concentrated fibrin I (20 + 2mg/ml) which is stable for several days at -20°C resulted. Trace amounts of biotm-batroxobm were removed by addition of freeze-dπed avidm covalently coupled to agarose, which hydrates the fibrm I. Within 5 minutes the biotm-batroxobin: avidm- agarose was removed by filtration and the concentrated fibrm I monomer was transferred to the desired applicator devices for use in the following experiments. The resulting FI monomer solution was co-applied with a carbonate/bicarbonate buffer (pHIO) in a ratio of 7 : 1 (Fl:pH10) . EXAMPLE 2 This study was constructed to assess the effect of the fibrm monomer sealant of Example 1 (hereinafter " FI monomer sealant" ) on post-surgical flexor tenαon adhesion formation in a rabbit experimental model. Further subdivision mto mobilized and immobilized postoperative groups allowed assessment of any synergy between the FI monomer sealant and a method well documented to reduce adhesion formation, namely early active mobilization. Materials and Methods Animal Model and Surgical Procedure 20 Murex Lop rabbits were used for this study. They were of equal sex distribution and the body weight ranged from 2500 to 4500 grams. There was one αeath prior to end point assessment making the total number of rabbits 19 (9 male, 10 female). The animals were obtained at least seven days prior to surgery from Murex BioTech Ltd (Dartfort, Kent) to allow for acclimatization. Throughout the study period they were housed in single cages and fed and watered ad libi tum . Regular assessment of the animals' general condition and surgical wound were carried out in accordance with the U.K. Home Office "Guide for the Care and the Use of Laboratory Animals" 1996. The surgical procedure was carried out in a fully equipped operating theatre, which was "Good Laboratory Practice" compliant. Induction of anaesthesia was by Hypnorm® (Janseen Copenhagen, Denmark, 0.2ml/kg, lm) followed by Diazeparm (Phoenix, 0.5ml/kg, iv) . Maintenance was via an anaesthetic mask, which delivered 2% halothane (Zeneca) and oxygen flowing at 21/mιn. The condition of the anaesthetised animals was continuously monitored using a pulse and oxygen saturation probe. Recovery from anaesthesia was encourageα with pure oxygen delivery via the facemask. Prior to the start of the procedure the left front paw' s flexor aspect was shaved with hair clippers. After anaesthetic induction the operative site was prepared with chlorhexidme in alcohol and iodine m alcohol scrubs. The field was isolated with sterile drapes. With the aid of an operating microscope, the second and fourth digits of the left front paw were longitudinally incised over the base of the proximal phalanx. Blunt dissection in the midlme revealed the digital sheath and its tendinous contents. The sheath was then opened between pulleys A2 and A3 (a point corresponding to the middle of the proximal phalanx) . Flexor digitorum profundus was exposed (Figure 1) . This long flexor tendon of digits two and four then received a standard surgical injury on its volar aspect with a 15 blade. The injury measured 5 mm in length and exposed the core substance of the tendon. Prior to wound closure the flexor digitorum profundus wounds of digit two and four were either treated with FI monomer sealant (Figure 3) or received no treatment. Application of FI monomer sealant (between 0.1 - 0.4 mis) was through a variable fine jet applicator as disclosed in WO 97/20585 and WO 98/20931. The resultant coating was allowed to polymerise in air for 3 minutes and the injured tendon was then returned to the base of the wound. The operated untreated digits also received 3 minutes of air exposure. All second digits were immobilised with the additional surgical procedure of proximal tendon transaction. This was performed through a transverse skin incision just distal to the carpal tunnel. Both flexor digitorum profundus and flexor digitorurn superflcialis to digit two were sharply transacted m the palm thus immobilising the digit. All skin incisions were closed with subcuticular interrupted horizontal mattress sutures (4/0 V cryl (Ethicon) ) . The wound was then dressed with Cicatπn© (Wellcome) antimicrobial powder and sprayed with Opsite® (Smith and nephew). No external dressings were applied. All animals received buprenorphme (0,01-0,05 mg/kg) for postoperative analgesia. After recovery animals were allowed to move about as normal in their cages. At 14 days post surgery, the animals were euthanased using a lethal barbiturate mtravascular injection. Biomechanical Assessment of Adhesion Development Adhesion development was assessed by the use of a tensiometer m all operated groups. In addition the animals unoperated right front paw (digits two and four) were assessed in the same way so as to provide an unoperated control group for comparative analysis. Double blind biomechanical assessment was therefore conducted on 5 groups. Group 1 Unoperated controls. Group 2 Immobilised (digit 2) operated and FI monomer sealant tested. Group 3 Mobilised (digit 4) operated and FI monomer sealant tested. Group 4 Immobilised (digit 2) operated and no further treatment . Group 5 Mobilised (digit 4) operated and no further treatment . The tensiometer (NE Holm A/S, Denmark) measured the force m grams required to pull the flexor digitorurn profundus tendon from its sheath. The freshly culled animals' front left and right second and fourth digit were each dissected and the flexor digitorum superflcialis and flexor digitoru profunαus were transacted proximal and distal to the operative injury site. The proximal dissection culminated in transacting the two tendons approximately 15 mm proximal to the mouth of the digital sheath. The αistal dissection culminated in the flexor digitorum profunαus tendon being transacted between the A3 and A4 pulley making sure that this was proximal to the insertion of the vmcular vessels. The proximal stump of the flexor digitorurn profunαus tendon was then transfixed witn a silk 2/0-stay suture. With the nail of the relevant digit held rigid in a clamp, the silk tie was then connected to the tensiometer. The force required to pull the tendon free from the sheath was recorded in grams and was indicative of adhesion build-up. Statistical assessment of tne observed data was carried out using a robust regression technique m a Stata Release 6 statistical software package. This analysis accounted for the structure of the data, which consisted of several measurements per animal. This technique specifies that there is inter but not necessarily mtra animal observation independence. Robust estimates of the standard errors of regression coefficients were calculated using the Huber/White/sandwich estimator. This takes mto account the potential lack of independence from the same sample. The residual variances were not constant between groups on the original scale of measurement. They were therefore not normally distributed. The statistical analysis was therefore performed after applying a log . , transformation. Regression analysis obtained estimates of geometric mean tension and 95% confidence intervals per group. To obtain these values the coefficients and confidence intervals on the logarithmic scale were transformed back mto the original scale of measurement (Table 1 and 2) . The raw data has been graphed on a box and whisker plot (Sigma Plot version 4.0). The boxes correspond to the interquartile range (the central 50% of the data) with an internal line to marK the median. The mean is represented with a dotted line. The length of the whiskers are 1.5 times the interquartile range. Values outside the whiskers have been plotted individually. Results This study used 20 rabbits. One died prior to biomecnanical assessment. They were randomly assigned to one of four treatment groups or an unoperated control group. The potential maximum number of observations of the 19 rabbits was 76, four per rabbit. However out of these only 67 were suitable for statistical analysis (88%) due for example to tne tendon snapping in the mooile group, or incomplete distal transaction prior to tensiometer pull. Statistical assessment was therefore performed on the following number of tendons per group. Group 1 (n = 36) Group 2 (n = 7) Group 3 (n = 6) Group 4 (n = 10) and finally Group 5 (n = 8) . The raw tensiometer pulls mean value for each group is graphically represented in graph 1. Interpretation of the raw data revealed an overall reduction in pull required to remove the tendon from its sheath by 75.6% when comparing the total treated FI monomer sealant groups. When separated mto mobile and immobile the reduction from untreated to treated groups was 79.7% and 76.8% respectively. As previously stated the group data was not normally distributed. Meaningful interpretation of the raw data required application of a logarithmic scale. Table 1 shows the geometric mean tension values and 95% confidence intervals for the mean per group. Comparison was made between operateα groups and unoperated controls using robust regression analysis. This analysis demonstrated no statistical difference when comparing the FI monomer sealant treated groups (immobilised p=0.42, and mobilised p=0.47) with the normal unoperated control pulls. This implies there was no significant difference adhesion formation between FI monomer sealant treated injuries and unoperated controls. There was however a highly significant difference with comparisons made between the operated untreated groups and the unoperated controls (immobilised p<0.001, and mobilised p<0.001). This indicated that without treatment with FI monomer sealant, surgical injury produced significant increases m adhesion formation, as evaluated by tensiometer pull in comparison to the unoperated controls. Further analysis of the data snows that between the operated groups witn the same type of post operative mobilisation, the addition of FI monomer sealant makes a significant difference (difference between FI monomer sealant immobilised and untreated immobilised p=0.03, difference between FI monomer sealant mobilised and untreated immobilised p=0.03). After performing regression analysis on the logi, of the raw data, percentage change in mean tension from unoperated control side was as follows: Group 2 Immobilised operated and FI monomer sealant treated (increased by 72%) Group 3 Mobilised operated FI monomer sealant treated (increased by 39%) Group 4 Immobiliseα operated and no further treatment (increased by 980%) Group 5 Mobilised operated and no further treatment (increased by 490%) From these data it can be concluded that both the mobile and immobile FI monomer sealant treated groups were not significantly different to unoperated control group (P=0.47 and P=0.42 respectively Table 2) . The raw data graph (Graph 1) shows that FI monomer sealant works in combination with active mobilisation to reduce the force required to pull the tendon from the sheath, indicating a considerable reduction in adhesion generation in treated cases. This is contrasted with the comparison made between the unoperated control group and the operated untreated group. Both the mobile and immobile untreated groups form significantly more adhesion than the unoperated control (P<0.001 respectively (Table 2)). Again the raw data graph does show the benefits of mobilisation in the reduction of adhesion formation (Graph 1). Control Treat Imm Treat Mob Untreat Imm Untreat Mob Group Gra p I Box and Whisker plot of raw data. The boxes correspond to the interquartile range (the central 50% of the data). The solid internal line represents the median value. The dotted horizontal line is the mean value. The length of the whiskers are plotted individually. Points outside these are individually graphed. Table 1 The geometric mean tension and 95% confidence intervals for the mean per group Table 2 P Values from the robust regression analysis comparing every pair of group means. EXAMPLE 3 The clinical performance of fibrm sealants is influenced by physical properties such as elasticity, tensile strength, and ability to adhere to human tissue. These properties are related to the internal structure of the fibrm sealant that builds as it polymerises. Analysis of the minimum polymerisation time to achieve a functional fibrm clot is clinically important. Instant tissue-fibrin sealant adhesion is desirable to ensure that the fibr sealant functions on contact and remains at the site of application without being washed away by blood or displaced by movement of the target tissue (e.g., the heart or lungs). The physical characteristics of fibrm sealants are related to the extent of fibrm crosslmkmg. Determination of the polymerisation rate allows calculation of the minimum time required to produce a functional clot. The adhesion characteristics to vital human tissue and kinetics of polymerisation between 20 and 300 seconds post-application of Vivostat™ Fibrm 1 monomer based sealant have been analysed and compared to those obtained for two conventional fibrm sealants, Tissucol® and Beriplast®. Mathematical analysis of the experimental data revealed that polymerisation of Vivostat™ sealant followed first order kinetics whereas that of Beriplast® and Tissucol® followed second order kinetics. This study demonstrates that Vivostat™ sealant polymerises faster than conventional fibrm sealants . 1. Materials and Methods Solutions were prepared from fresh blood donations as described m Example 1 and used within I hour. Sealant was delivered using the Spraypen™ applicator in combination with the automated Vivostat™ application unit as disclosed by Holm et al. in WO 97/20585 and WO 98/20931. Conventional fibrm sealants Tissucol® (Baxter) (1 ml and 2 ml kits) and Beriplast® (Aventis) (1 ml and 3 ml kits) were prepared and applied according to the manufacturers' instructions. Tissucol® and Beriplast® were applied using the Duploject® and Pantaject® applicators, respectively, fitted with a needle or a spray head. Torsion rheometry experiments were performed using a controlled stress rheometer, Cam-Med CSL 100 auto gap. Approximately 0.5 ml of fibrm sealant was applied on to the bottom of the rheometer. The top was a 2 cm diameter fine- hatched plate and the sample platform consisted of a 2 cm diameter fine-hatched plate over a Peltier baseplate. The temperature of the rheometer was set at 37°C. Oscillation experiments were pertormed using a constant oscillation torque of 15 μNm at a frequency of 0.1 Hz for 11 minutes. Adhesion experiments were performed using a recently described model involving use of vital human tissue (Kjaergaardetal, Eur. Surg. Res. 1999). The human tissue samples were greater saphenous vein grafts left over from coronary artery bypass grafting. To ensure tissue vitality, all samples were kept in physiological saline solution and used within 24 hours of harvesting. The vein graft was split longitudinally and the split graft was cut mto 1 cm 2 samples that were fixed to the sample holder using Gore-Tex V5 retaining sutures. The two samples were brought into close proximity at an angle of 45°, and 0.1 ml of fibrm sealant was sprayed on the tissue surfaces, where the adventitia was exposed. The two tissue samples were brought mto contact without external pressure and were left polymerised until the adhesion experiment began. Tests were performed using a Nene universal testing machine model M5 at a speed of 10 mm per minute. Adhesion strength defined as force divided by the cross-sectional area of the sample, adhesion energy (i.e., area under the experimental curve as seen in Figure 3), and elongation (i.e., extension reached by the specimen) were calculated for each experiment. Mean values were calculated at each polymerisation time. Confidence intervals (i.e., 95% CI) were also calculated for each parameter as 95% CI=1.95 CV/ n, where n is the number of samples analysed and CV=6.60, 8.35, and 9.81% for the adhesion strength, extension and adhesion energy, respectively. 2 . Results Sixteen solutions, each prepared from fresh blood donations from different donors, were sprayed on to the rheometer stage, and the rheology of the fibrm clot formed was studied over a period of 11 minutes. The average fibrm I concentration was 22.20 mg/ml + 12.7%(CV). Four samples of Tissucol® and Beriplast® were also analysed the rheometer. Curve fitting analysis of dG' /dt against time revealed that the polymerisation of sealant followed first order kinetics as shown m equation (1) where t is the time, (dGXdt) 0 is the value of the derivative at t=0 and k is the kinetic rate constant : dG' (dG') (1) dt (dt) 0 A single curve showing dG' /dt versus time was prepared averaging the values for the sixteen samples at each time point. The values obtained for k and (dG'/dt) _ were 1.17-10 " 2 +0.05 10 ~2 s "1 and 3.17+0.15 pa s "1 , respectively (r=0.9926; χ=0.0683) . Analogous mathematical analysis was applied to samples of Tissucol® and Beriplast® fibrm sealants. An attempt to fit the experimental data to equation (1) gave a very poor correlation ( r=0.8300-0.9400) . In this case, dG'/dt followed second order kinetics as shown in equation (2) where t is the time, (dG Xdt) o is the value of the derivative at t=0 and k is the kinetic rate constant in pascals "1 . (dG') = 1 (2) !dt kt [dG' (dt Kinetic parameters for Tissucol® and Beriplast® were calculated by fitting the average dG' /dt curve to equation (2) . Table 3 shows the results obtained following this procedure. For conventional fibrm sealants, the mixing efficiency of the two components of the fibrm sealant had a great influence on the speed of formation of the clot. Spray delivery systems increased the kinetic rate constant by almost 43% for Tissucol® and by 18% for Tissucol®. The kinetics of polymerisation of Tissucol® and Beriplast® were compared over the first 200 seconds of polymerisation. Over this period of time and for tne sake of comparison, the experimental curve can be fitted using the second order kinetics model represented by equation (2) with a good correlation (r=0.9974). In this case, the kinetic rate constant exhibited a similar absolute value (i.e., k=l.06.10 " 2 +0.06 10 "2 pa "x) to that obtained using equation (1). Results are summarised in Figure 4. As shown, the second order kinetic rate constant was between 6 and 20 times greater than the other fibrm sealants. Adhesion experiments were performed on samples of sprayed fibrm sealant in order to compare similar application systems. Most of the samples showed a first breaking point (i.e., intersection of points A and B, see Figure 3) before the maximum force was reached. This point was detected by a sudden reduction in adhesion force (Figure 3) and was visually observed as a partial breaking of the sample. This represents the limit of the elastic character of the sealant and the first failure of the system, which has clear implications from a clinical point of view. Elongation at first breaking point (i.e., elongation at B) and adhesion strength at first breaking point (i.e., force at point A divided by the cross- sectional area) were measured for each sample. Maximum adhesion strength and elongation as well as adhesion energy (i.e., area under the experimental curve) were also calculated. Two identical adhesion experiments were prepared at each time point and the mean value recorded for each sealant sample. Results are summarised in Tables 4-6. Reached a high degree of elasticity much faster than either Tissucol® or Beriplast®. This is consistent with the kinetic analysis showing that the polymerisation rate was much faster than that of competitor products. As a result, superior instant adhesion to tissue (Figure 5) as well as better elastic characteristics (Figure 6). Table 3 Kinetic parameters and regression analysis correlation for Tissucol® or Beriplast® fibrm sealants Applicator (dG' /dt) 0 /pa s "1 k 10 3 /pa " Tissucc ιl® Needle 14.15+0.43 0. .48+0.02 0.9893 3.20 Spray 54.19+4.71 0. .84+0.04 0.9934 5.53 Beriplast® Needle 19.75+1.65 1.11+0.07 0.9739 8.80 Spray 29.22+4.35 0.84+0.04 0.9615 6.56 Table 4 Adhesion properties + 95% CI for Vivostat™ fibrm sealant Time (seconds) 20 40 120 300 Adhesion strength 36.35+3.31 34.83+3.17 37.80+3.44 53.13+4.84 (gem " -) Elongation (mm) 18.36+2.11 15.73+1.81 14.20+1.63 11.56+1.33 Elongation at ..54+0.18 1.62+0.19 1.90+0.22 1.88+0.22 first break (mm) Adhesion Strength 33.65^3.06 34.83 + 3.17 34.67 + 3 16 34.67 + 3.16 at first break (gem " ) Adhesion energy 3.12+0.42 2.81+0.38 2.47+0.33 2.99+0.40 (mJ) Table 5 Adhesion properties + 95% CI for Tissucol© fibrin sealant Time (seconds) 20 40* 120 300 Adhesion Strength 24.94+2.68 40.92 + 5.26 65.39 + 5.95 81.11 + 7.38 (gcπX) Elongation (mm) 4.45+0.51 6.38 + 1.04 8.14 + 0.94 11.65+1.34 Elongation at 0.80+0.09 0.29+0.05 0.21+0.02 0.39+0.04 first break (mm) Adhesion Strength 21.41+1.95 i " \ 34+3.32 19.37+1.76 27.53+2.51 at first break (gem--) Adhesion energy 0.68+0.09 1.65+0.32 2.41+0.33 6.29+0.85 (mJ) * Single experiment Table 6 Adhesion properties + 95% CI for Beriplast© fibrm sealant Time (seconds) 20 40 120 300 Adhesion strength 49.95+4.55 93.61+8.52 131.64+11.98 168.35+15.32 (gcm ": ) Elongation (mm) 6.60 " X. "7 6 4.23+0.49 11.84+1.36 18.48+2.13 Elongation at first 0.46+0.05 0.19+0.02 1.17+0.13 1.25+0.14 break (mm) Adhesion Strength 22.43 + 2.04 34.67 + 3.16 30.59+2. ^ 9 " 75.46+6.e " at first break (cm--) Adhesion energy (mJ) l .41+0.19 1.58+0.21 7.53+1.02 7.59^1.03 EXAMPLE 4 The purpose of this Example 4 is to evaluate the ability of three fibrm sealants in the prevention of post surgical adhesion (PSA) in the peritoneal cavity of rabbits following surgical injury to the uterine horn and the opposing ipsilateral peritoneal wall. This example evaluate syringe- applied sealants as follows: a) the Vivostat™ fibr I monomer-based fibrm sealant as used in the earlier examples; b) Tissucol®, a fibrm sealant which was commercially available m Europe through Immuno AG in Austria, and which is a two component sealant system involving the coapplication of pooled human fibrinogen (in an aprotinim-contammg solution) and a bovine thrombin component in a calcium chloride solution; and c) Cyroprecipitate (CYRO) , a cryoprecipitate concentrated blood component containing fibrinogen from a single donor and co-applied with bovine thrombin. The Tissucol® and CRYO were all evaluated with 4 units and 500 units of bovine thrombin. Model In summary a standard abrasion injury was inflicted on each uterine horn and ipsilateral peritoneal] wall, which would naturally lie in juxtaposition. The injured areas were then held apposed using positional sutures, placed outside the experimental site, with treated sites separated by a layer of fibrm sealant. Experimental sites were then left m vivo for the length of recovery time dictated by the study protocol. Due to the level of injury induced and injured surfaces being apposed this rabbit uterine horn abrasion model is a severe experimental PSA model, with a "worse case" scenario created. To ensure that injuries of consistent standard area could be induced, templates, 25 mm x 3 mm, designed to fit the uterine horn or peritoneal wall, were specially constructed. Abrasions were induced using a scraper with a standard depth (1.5mm) which fitted the exact area of the template. With the additional parameter of using a set number of scrapes for each injury site, injuries were maximally standardised within the limits of biological variation. Uterine horns were chosen as the experimental site, together with the peritoneal wall, due to their size, structure and location within the peritoneal cavity. Heavy nandlmg of tissues has been shown to induce PSA formation (Boys, 1942; Connolly & Smith, 1960) and hence excessive tissue handling needed to be avoided. In addition, ex-breedmg rabbits were also chosen for these investigations due to their large size facilitating appropriate procedures. Procedure Premedication was administrated with hypnorm (Fentanyl citrate 0.315mg/ml and fluanisone lOmg/ml. Supplied by Janssen Saunderton, High Wycombe, Buckinghamshire.) (0.2ml/kg body weight intramuscular) to the right gluteous maximus muscle. Surgical anaesthesia was induced with hypnorm (0.3ml/kg body weight intramuscular) and diazepam (5mg/ml diazepam. Supplied by Phoenix Pharmaceuticals Limited, Gloucester.) (2.5mg/kg body weight intravenous). Full sterile operating procedures were observed. Particular attention was paid to the washing of surgical gloves in sterile water to remove all traces of particulate matter (starch, powder) which might, if transferred to the operative site, induce granuloma or adhesion formation. Fur was shaved from the surgical area and the area scrubbed with alcoholic chlorhexidme followed by iodine. Laparotomy was performed using cutting diathermy, by a single incision in the midlme, from lower liver margin to the level of the iliac fossa, through skin and muscle to peritoneum, which was diviαed with scissors. Retraction was applied to laparotomy wound edges to allow access to uterine horns. Experimental areas were selected on the serosal surface of each uterine horn and corresponding internal ipsilateral surfaces of the peritoneum, which would naturally lie in juxtaposition with each other. A standard template, constructed specifically either for the uterine horn or peritoneal wall, was placed on the selected areas and each area abraded with the sharp edge of a scraping tool. A standard number of 10 scrapes was used to cause homogeneous punctate bleeding but not so far as to cause frank contiguous hemorrhage. Hence a standard, and reproducible injury was produced m each case. Single throws of Stannius positional suture (Ethibond 6/0 or similar) were placed 5mm outside each end of abraded areas (peritoneal wall and uterine horn) . These sutures passed only through the serosa of the peritoneum and corresponding uterine horn. For control groups, sutures were tightened to bring the two j uxtapositional aoraαeα areas toqether ana maintain contact between tne two areas. Timing was commenced from this point. For treated groups positional sutures were tightened to bring the two aoradeα areas close together but not m contact and fibr sealant was then applied to abraded areas. Sutures were then αrawn together to bring the two areas into contact, using as much tension as was needed to create reasonable contact but avoiding tight sutures. Timing commenced from this point. In groups which sampled up to 30 minutes post injury, rabbits were kept anaesthetised, in the supine position with the laparotomy incision held closed with tissue clamps. In groups which sampled from 1 hour post injury onwards, the laparotomy was closed and reopened after the relevant time period. Laparotomy wound closure was in two layers: first with 2/0 plain catgut on atraumatic half round needle for the peritoneum and muscle layers, using transplant longflow, overunder, non-interrupteα crossed sutures; ana secondly with 2/0 Prolene or similar on half round cutting needle using interrupted mattress sutures for the skin. Immediately after closure of the wound, wound dressing was applied on and around the wound. At 14 days post surgery animals were anesthetized (as for the surgical procedure) . Laparotomy was reopened along the original incision with experimental areas identified and macroscopic observations recorded and photographed. The abraded area of the peritonem together with a border of unabraded tissue in excess of 5 mm and the associated uterine horn were resected. A summary of the experimental groups is Table 7 below. Macroscopic Results All cf the control groups (13/13) showed PSAs joining the abraded areas <">f the peritoneal wall and uterine horn. The macroscc ic incidence of experimentally induced PSAs for treatment group" was 8.3% for Vivostat™ sealant, 16.7% CRYO 4 units thrombin, G6.7% CPYO 500 units thrombin, 100% Tissucol® ^ units >r mhιn and in Grapn 1 e 1 ow . G : a i 11 oscoiJic E'GA incidence. Microscopic Quantitative Results Mean volumes of PSAs were 73.93mm 3 for the control group, 1130mm' for the Vivostat™ sealant treated group, 21.06 and l^.gθmrX for the CRYO treated groups with 4 and 500 units thrombin respectively and 106.12 and 69.42mm 3 for the Tissucol® treated groups with 4 and 500 units thrombin respectively (Graph 3) . Significant reduction in mean PSA volume compared to controls was seen with Vivostat™ sealant (P<0.001) and CRYO (P=0.0152) 4 units thrombin treated groups only. Assuming that the control group demonstrated 100% PSA formation, the percentage volume of PSAs for each treatment was 15.28% Vivostat™ sealant, 28.49% CRYO (4 units thrombin), 2 3. 6% CRYO (500 units thrombin), 143.55% Tissucol® (4 units thrombin) and 93.90% Tissucol® (500 units thrombin) (Graph 4). Graph ! :an TGA volumes together with SEMs and statistical iffer' :S . Graph 4. Mean PSA percentage volume. Thus, the Vivostat fibrin I monomer based sealant demonstrated a superior prevention of PSAs in this model by providing a nearly 85% reduction in PSAs over the control and a significant improvement over the other sealants tested. Table 8 Post Surgical Incidence/Reduction EXAMPLE 5 The aim of this example was to assess the ability of Vivostat™ Fibrm Monomer-Based Fibrm Sealant made from human blood (prepared as in Example 1) to reduce or prevent post surgical adhesions m a rat caecal abrasion model. Experimental Procedure Sixteen, female, Sprague Dawley rats were randomised mto two groups. Each group received a standardized caecal and opposing peritoneal abrasion wounding which was either left untreated or sprayed with Vivostat™ Fibrm Sealant. The abrasions were then apposed with sutures. The animals were then allowed to recover and maintained in the animal unit for 14 days. On day 14, the control and Vivostat™ Fibrm Sealant treated animals were euthanased and the experimental sites removed. The wounds were examined grossly, histopathologically and stereologically. Results The abrasion procedures resulted n an inadvertent perforation of the caecum in two animals (which was repaired using a purse string suture of 4/0 vicryl (Ethicon UK) . The sites were still used for evaluation. All other surgical procedures were completed uneventfully. There were no abnormal clinical signs observed and no mortalities . The fibrm I solution concentrations used on the treated wounds ranged from 13.46 to 16.02 mg/ml. A mean volume of 0.79ml Vivostat™ Fibrm Sealant was applied via the spray application to experimental sites. Macroscopic examination of the wounds on day 14 showed adhesions in 8/8 control wounds and 0/8 Vivostat™ Fibrm Sealant treated wounds. All adhesions were dense, tenacious and fibrous. Mean volume of post surgical adhesions measured stereologically was 89.91mm J for control cases and 17.82mm 3 for Vivostat™ Fibrm Sealant treated cases. There were fibrmous like connections, which were not considered to be adhesions, in the Vivostat™ Fibrm Sealant treated cases, but they were recorded as adhesion volumes for the purpose of analysis. Conclusion The mean volume of adhesions was significantly less (P< 0.1) in the Vivostat™ Fibr Sealant treated group compared to the control group. Vivostat™ Fibrm Sealant is an effective agent for the reduction of post-surgical adnesions when compared to controls in this rat caecal abrasion model. EXAMPLE 6 This example is designed to evaluate the formation/prevention of PSAs in the stomach, colon and caecum of the pig by introducing a surgical injury to those sites similar to the raboit uterine from model above. Pig models previously used to investigate PSAs demonstrate that pigs from PSAs m response to injury or trauma by identical pathogenesis to humans. In this example control (untreated/injured) animals were compared to those treated with of Vivostat™ Fibrm Monomer-Based Fibrm Sealant as prepared in Example 1, but wherem the sources were (a) human and (b) from the pig being treated, i.e., autologous sealant. Pre-medication was administered using Ketamme (Ketalar- 50mg/ml ketamme hydrochloride. Supplied by Parke-Davis, Pontypool, Gwent . ) (5mgs/Kg) plus Xylazme (Rompun 2%-Xylazme hyαrochloride 23.32mg/ml (equivalent to 20mg/ml xylazme) and lMg/ml methyl 4-hydroxy-benzoate (preservative) . Supplied oy Bayer Pic, Animal Health Business Group, Bury St. Edmunds, Suffolk.) (lmg/kg)) intramuscularly in the gluteous maximus muscle. At the operating suite, pigs were induced to and maintained at full anaesthesia with Halothane at 4% in oxygen and nitrous oxide delivered at 1.5 litres per minute and 0.5 litres respectively per minute via mask to the snout. Once anaesthetised pigs were transferred to lay in the supine position on the operating table, where they were secured by soft tapes to each limb. A plastic ear tag bearing the unique pig identification number for the study was secured to one of the animals' ears. For each pig, the surgical site was shaved and scrubbed with chlorhexidine in alcohol followed by swaobmg twice with iodine in alcohol. Sterile operative proceαures were adhered to from this point on. The animals were draped. Cutting diathermy and scissors were used to expose the spiral colon and the stomach through a midline laparotomy starting at the level of the distal xyphoid process of the sternum and extending distally 10 - 12cms. One area was selected on the lateral surface of the spiral colon or on the blunt end of the caecum and the medio-lateral serosal aspect of the stomach such that these areas each laid naturally against the ipsilateral peritoneal wall. Areas were then selected on the ipsilateral peritoneal wall. As with the rabbit uterine horn abrasion model, each selected area was aoraded, using a template and scraper, a standardised number of 12 scrapes which caused homogeneous punctate bleeding but not so far as to cause frank contiguous haemorrhage was performed. A single throw suture (Ethibond 0.6 or similar) was placed at each end of the experimental site but outside of the abraded areas. These sutures passed only through the internal serosa of the peritoneum and then passed through the serosa at the respective ends of the apposed abraded areas on the stomach or colon. Sutures were tightened to bring the two apposed abraded areas close together but not in contact. For treated cases, human or porcine fibrm sealant was applied to the abraded areas (mean volume of 1.3ml per experimental site), whereas no treatment was applied in control cases. Positional sutures were then tightened to bring the two abraded areas mto close contact. The laparotomy was closed in two layers, first with 2/0 Dexon Plus on an atraumatic half round needle for peritoneum and muscle layers, second with 2/0 Prolene or similar on half round cutting needle for skin. The first suture layer was of "transplant" longflow, over-under, non-interrupted crossed sutures, the second layer was of interrupted cruciate mattress sutures . At 7 days post-surgery the animals were scarified and evaluated as follows. Animals were anaesthetised as for the surgical procedure. Laparotomy was reopened along the original incision, with experimental areas identified and macroscopic observations recorded and photographed. The colon, caecum and stomach experimental sites, joined to the peritoneum by positional sutures at each end of the site, were resected. Euthanasia was achieved by high dose intravenous pentabarbitone (Expiral-Pentobarbitone sodium BP 200mg/ml. Supplied by Sanofi Animal Health Ltd., Watford, Hertforαshire . ) (150mg/kg body weight)). Resected tissues were trimmed of excess adipose tissue, pinned flat on stiff card, to retain a standard, lifelike tissue positional relationship, and immersion fixed m 10% neutral buffered formal saline for at least 24 hours at room temperature. The table below summarizes the experiment. Results All animals demonstrated general PSAs between the peritoneal suture line and underlying tissues: most frequently the omentum, ileum, caecum, spleen and liver respectively. All these PSAs were separated by blunt dissection and did not interfere with experimental sites. All control experimental sites were adhered, many being quite severe. 5 out of the 8 sites treated with human fibrin sealant were clear of adhesions, with the remaining sites joined by either PSAs or fibrin sealant. 2 out of the 4 porcine fibrin sealant treated sites were identified as non-adhered with the other sites joined by either PSAs or fibrin sealant. Mean volume of PSAs for the control group was 207.25mm 3 for the colon, 31.33mm 3 for the caecum and 248.11 mm 3 for the stomach with an overall mean of 181.78mm 3 . Human fibrin sealant treated group demonstrated mean volumes of 42.83mm 3 , 8.96mm 3 and 204.47mm 3 for the colon, caecum and stomach, respectively, with an overall volume of 74.77mm 3 . Whereas no PSAs were present in colon and caecum (Figure 8.5) experimental sites treated with porcine fibrin sealant, with 6.25mm 3 for the stomach and a group mean of 1.27mm 3 (Graph 5). Assuming that the control group demonstrated 100% volume of PSA, reduction with human fibrin sealant was 79, 71 and 18% for the colon, caecum and stomach, respectively, with an overall reduction of 59%. Porcine fibrin sealant demonstrated 100% reduction for both colon and caecum, 97% for the stomach and overall 99% reduction of PSAs compared to controls (Graph 6) . Experimental Site Graph 5 " : Mean PSA volumes together with SEMs. Experimental Site Graph Mean PSA percentages.

Claims: l aims A method for the prevention of post surgical adhesion formation at, e.g., a surgical wound site comprising the steps of a) preparing a composition comprising fibrm monomer; and b) applying said composition to said surgical wound site under polymerizing conditions such that a fibrm polymer is formed which prevents post surgical adhesions of said site. The method of claim 1 wherem said fibrm polymer which prevents surgical adhesions in adhesive to said surgical wound site. The method of claim 1 where said fibrm polymer which prevents surgical adhesions provides hemostasis at said surgical wound site. The method of claim 1 wherem said fibrm polymer which prevents surgical adhesions provides sealing of fluid or air leakage at said surgical wound site. The method of claim 1 wherem said fibrm polymer which prevents surgical adhesions provides enhanced angiogenesis and would healing to said surgical wound site . The method of claim 1 wherein said composition comprises fibrm monomer inhibited from polymerizing and wherem the polymer inhibition qualities are reversed upon application. The method of claim 6 wherem said composition comprises fibrm monomer in a low pH solution. The method of claim 7 wherein said pH is between 2 and 5. The method of claim 7 wherem said low pH fibrm monomer solution is coapplied with a buffer solution which raises the pH and initiates polymerization. 10. The method of claims 6 and 9 wherem said fibrm monomer solution is coapplied with a pH 10 buffer. 11. The method of claim 10 wherem said fibrm monomer and buffer are coapplicable in a ratio of about 7:1. 12. The method of claim 1 where said composition comprising fibrm monomer is a fibrm monomer solution having a fibrm concentration between 10 and 20 mg/ml. 13. The method of claim 12 wherem said concentration is between 10 and 50 mg/ml. 14. The method of claim 12 wherem said concentration is between 10 and 30 mg/ml. 15. The method of claim 12 wherem said concentration is between 15 and 25 mg/ml. 16. The method of claim 1 wherem said composition comprising fibrm monomer is substantially free of exogenous or added enzyme which catalyzes the cleavage of fibrinopeptides A and/or B. 17. The method of claim 1 wherem said formed fibrm polymer is substantially free of any exogenous or added enzyme which catalyzes the cleavage of fibrinopeptides A and/or B. 18. The method of claim 1 wherem said fibrm monomer is selected from fibr I, fibr II, des ββ fibrm or mixtures thereof. 19. The method of claim 1 wherem said fibrm monomer is prepared by subjecting fibrinogen to an enzyme which catalyzes the cleavage of flbrmopeptide A from fibrinogen such that said fibrm monomer is fibrm I. 20. The method of claim 19 wherem said enzyme is batroxobm. 21. A method for the prevention of post surgical adhesion formation at a surgical wound site comprising the steps of a) preparing a composition which is capaole of forming a fibrm polymer; and b) applying said composition to said site under conditions where the resulting fibrin polymer is substantially free of an enzyme which catalyzes the cleavage of fibrinopeptides A and/or B from fibrinogen. 22. The method of claim 21 wherem said fibrm polymer is substantailly free of thrombin. 23. The method of claim 21 wherem said composition capable of forming a fibrm polymer is fibrm monomer. 24. The method of claim 23 wherem said composition capable of forming a fibrm polymer is recombinant fibrm monomer. 25. The method of claim 23 wherem said composition capable of forming a fibrm polymer is fibr monomer autologous to said recipient. 26. The method of claim 23 wherem said fibrm monomer composition is prepared by subjecting fibrinogen to an enzyme which catalyzes the cleavage of fibrinopeptides A and/or B from said fibrinogen and thereafter separating said enzyme from the so-treated fibrinogen. 27. The method of claim 21 wherem said composition capable of forming a fibrm polymer is fibrinogen. 28. The method of claim 27 wherem said fibrinogen is applied following treatment with an enzyme capable of catalyzing the cleavage of fibrinopeptides A and/or B and further wherem said enzyme is not applied to said site. 29. The method of claim 21 wherem said fibrm polymer is selected from fibrm I, fibrm II, des ββ fibrm or mixtures thereof. 30. The method of claim 29 wherem said polymer is fibrm I. 31. A method for the prevention of post surgical adhesion formation at a surgical wound site of a patient comprising the steps of a) preparing a composition capable of forming a fibrm polymer wherem said fibrm polymer is autologous to said patient; and b) applying said comoosition to said wound site to form said polymer such that all materials applied to said wound site are substantailly free of proteins and/or polymers exogenous to said patient. 32. The method of claim 31 wherem said composition is fibrinogen and further wherem it is applied to the wound site in the presence of thrombin wherem said fibrinogen and said thrombin are autologous to said patient. 33. The method of claim 31 wherem exogenous proteins or enzymes are used to prepare said composition capaole of forming fibr polymer but wnere said proteins or enzymes are removed from said composition prior to application. 34. The method of claim 33 wherem autologous fibrinogen and one or more enzymes which catalyze the cleavage of fibrinopeptides A and/or B are used to prepare a fibrm monomer composition in step (a) . 35. The method of claim 34 wherem batroxobm is used to catalyze said cleavage. 36. The method of claim 31 wherem said composition is autologous fibrinogen and wherein said composition is applied in the presence of, or after being subjected to, one or more enzymes which catalyze the cleavage of fibrinopeptides A and/or B from said fibrinogen but where said one or more enzymes are not applied to said surgical wound site. 37. The method of claim 31 where said fibr polymer is selected from fibrm I, fibrm II, des ββ fibrm or mixtures thereof. 38. The method of claim 37 wherein said polymer is crosslmked. 39. The method of claim 34 wherem additional plasma proteins coharvested with said fibrm monomer and autologous to said patient are applied to said surgical wound site. 40. The method of claim 39 wherem said plasma proteins are selected from one or more of prothrombm, factor XIII, plasmmogen, fibronectin, antithrombin III and factor X. 41. A method for the prevention of post surgical adhesion formation at a surgical wound site in a patient comprising the steps of a) preparing a composition capable of forming a fibrm polymer which composition comprises fibrm monomer and one or more additional plasma proteins selected from prothrombm, factor XIII, plasmmogen, fibronectin, antithrombin III and factor X; and b) applying said composition to said surgical wound site under conditions to polymerize said fibrm monomer. 42. The method of claim 41 wherein said composition contains from about 10 to 30 mg/ml of fibrm monomer. 43. The method of claim 42 wherem said composition further contains from about 10 to 40 μg/ml of prothrombm. 44. The method of claim 42 wherem said composition further contains at least about 9 μg/ml of factor XIII. 45. The method of claim 42 wherem said composition further contains from about 100 to 200 μg/ml of plasmmogen. 46. The method of claim 42 wherem said composition further contains from about 60 to 210 μg/ml of fibronectin. 47. The method of claim 42 where said composition further contains at least about 50 μg/ml of antithrombin III. 48. The method of claim 42 wherem said composition further contains from about 2 to 7 μg/ml of factor X. 49. The method of claim 41 wherem said composition is a fibrm I monomer. 50. The method of claim 41 where said polymer is a fibrm II polymer which is crosslmked. 51. A method for the prevention of post surgical adhesion formation at a surgical wound site of a patient comprising the steps of a) preparing a composition capable of forming a fibrm polymer from materials which have not been subjected to a denaturing process and by a process which, itself, is not denaturing; and b) applying said composition to said surgical wound site from said fibrm polymer. 52. The method of claim 51 wherem said composition is prepared from materials which have not been treated in a solvent/ detergent viral interaction process. 53. The method of claim 51 wherem said composition or precursors of said composition have not been frozen. 54. The method of claim 51 where said composition or precursors of said composition have not been lyophilized. 55. The method of claim 51 wherem said composition or precursors of said composition are applied within 72 hours of preparation.

Inventors: AMERY MICHAEL J, BURNETT STUART, CEDERHOLM-WILLIAMS STEWART A, EDWARDSON PETER A D, GRIFFIN H EUGENE, HOLLINGSBEE DEREK A, HUGHES JONATHAN, RICKETTS SALLY-ANNE, SIBBONS PAUL, TRUMBULL HORACE R, AMERY, MICHAEL, J., BURNETT, STUART, CEDERHOLM-WILLIAMS, STEWART, A., EDWARDSON, PETER, A., D., GRIFFIN, H., EUGENE, HOLLINGSBEE, DEREK, A., HUGHES, JONATHAN, RICKETTS, SALLY-ANNE, SIBBONS, PAUL, TRUMBULL, HORACE, R.
Applicants: SQUIBB BRISTOL MYERS CO, BRISTOL-MYERS SQUIBB COMPANY
Application year: 2000
Main classification: A61K31
IPC codes: A61K38, A61L24, A61L26, A61L31