Non-aqueous secondary Lithium cell containing carbon fibers in the negative electrode

Abstract: The present invention improves cell characteristics at a low temperature. The negative electrode contains fiber carbon, which enables smooth doping and dedoping of lithium ions at a low temperature. Accordingly, the internal resistance value at a low temperature is reduced and the cell capacity value is increased.

Description: Background of the Invention Field of the Invention The present invention relates to a non-aqueous electrolytic cell including a positive electrode, a negative electrode, and a non-aqueous electrolyte. Description of the Relates Arts Conventionally, a nickel-cadmium cell, a lead cell, and-the like have been used as secondary cells for electronic apparatuses. However, with the recent progress in the electronic technology, many of the electronic apparatuses have become smaller and portable, which requires increase of high energy density of the secondary cell for the electronic apparatuses. However, the nickel-cadmium cell or the lead cell has a low discharge voltage and cannot increase the energy density sufficiently. To cope with this, a so-called lithium-ion cell is studied and developed. The lithium-ion cell has advantages that the discharge voltage is high and the cycle service life is long because of little self discharge. The lithium-ion cell is a non-aqueous electrolytic secondary cell in which the negative electrode is made from a carbon material capable of doping and dedoping lithium ions and the positive electrode is made from a lithium transition metal composite oxide. In such a lithium-ion cell, firstly, during a charge process, lithium ions are discharged from the positive electrode, after which the lithium ions are inserted between carbons of the negative electrode to form a compound with the carbons. This phenomenon is called doping. During a discharge, lithium atoms contained in the compound of the negative electrode become lithium ions, which are discharged from the negative electrode and again becomes the aforementioned LiM x O y in the positive electrode. This phenomenon is called dedoping. That is, in a lithium-ion cell, electric energy is generated by movement of lithium ions. In order to improve cell characteristics such as the cell initial capacity, internal resistance, and the like in the aforementioned non-aqueous electrolytic cell, the characteristic of the negative electrode is very important in addition to the characteristics of the positive electrode and the non-aqueous electrolyte. The negative electrode is made from a substance capable of doping and dedoping lithium ions. There can be exemplified a carbon material, a crystalline metal oxide, non-crystalline metal oxide, and the like. The carbon material may be, pyrocarbon, coke, graphite, vitreous carbons, active carbon, or the like. Document US 5,856,043 describes a non-aqueous electrolyte secondary battery which comprises an anode comprising a pressed compact of graphitized vapor-grown carbon fibers having a specific surface area of at most 5 m 2 /g and an average aspect ratio of 2-30, said compact having a packing density of 1.2-2.0 g/cm 3 . The use of carbon fibers as anode material improves the safety of the secondary battery because a graphitized vapor-grown carbon fiber which has been cut so as to have an aspect ratio of 2-30 has exposed parts of fracture of the graphite crystal, or the carbon lattices, only on both ends, which lowers the fibers function as a catalyst for the electrolysis of the solvent. Therefore, less decomposition of the solvent occurs and as a consequence the formation of gases which may lead to a breakage of the charged batteries is suppressed. The anode material mainly consists of carbon fibers which are linked to each other and to the electricity collector by a binder. The graphitized vapor-gown carbon fiber is used in a specific packing density and therefore conductivity of the anode increases. Addition of materials for improving conductivity, such as acetylene black, which is a high conductive carbon black having a remarkably great specific surface area, is not necessary. Document EP 0 893 026 A2 discloses a secondary battery or cell with a non-aqueous electrolyte. The anode comprises graphite spherical particles such as spherical cokes and mesocarbon microbeads. Optionally, a composite carbon material can be used for assembling the anode. The composite carbon material is comprising a graphite material mixed with carbon fibers to intensify the stiffness of the anode depolarizing mix and thus prevents the anode body from swelling and decomposing. As a carbon fiber material there may be used a vapor phase growth carbon fiber or pitch carbon fibers, made from petroleum or coal pitch as a raw material through a spinning and carbonating treatment. Document EP 0 644 603 A1 describes a negative electrode for use in a secondary battery. The negative electrode comprises milled carbon fibers derived from meso-phase pitch wherein the milled carbon fibers each has a fiber cut surface and a fiber axis intersecting with each other at cross angles, the smaller one thereof being at least 65° on the average. This negative electrode does not suffer from property deterioration, irrespective of multiple repetitions of charge and discharge. from which a non-aqueous-electrolyte-loaded lithic secondary battery having excellent cycle characteristics can be fabricated. The negative electrode consists of carbon fibers as the main component which are connected to each other by a binder material. Document US 5,443,928 discloses a carbon electrode for a non-aqueous secondary electrochemical cell. The carbon electrode comprises a "hairy carbon" as the main component. The hairy carbon electrode material is developed by growing submicron carbon filaments on a carbon substrate. A catalyst is used to Initiate hair growth with carbonaceous gases serving as the carbon source. The electrode is formed by mixing the hairy carbon material with a suitable binder pressing the admixture into a desired shape. Document EP 0 817 293 A1 describes a secondary battery which is produced by using an electrode containing carbon fiber of average length less than 100 µm and an electroconductive agent. The electroconductive agent is added from 0.01 to 50 wt-% in terms of the carbon fiber. The negative electrode is produced from carbon fiber plus carbon black (acetylene black) and polyvinyliden fluoride powder which were mixed together at a weight ratio of 80:15:5, and then a solvent is added to produce a flurry. However, the non-aqueous electrolytic cells produced using the aforementioned materials have the problem that when used at a low temperature, lithium ion doping and dedoping cannot be performed smoothly in the negative electrode and it is impossible to obtain sufficient cell characteristics. Summary of the Invention It is therefore an object of the present invention to provide a non-aqueous electrolytic cell having a preferable cell characteristic at a low temperature. In order to achieve the aforementioned object, the non-aqueous electrolytic cell according to the present invention includes a negative electrode capable doping and dedoping lithium ions, a positive electrode capable of doping and dedoping lithium ions, and a non-aqueous electrolyte, wherein the negative electrode comprises a negative electrode material capable of doping and dedoping lithium ions and the negative electrode material is containing fiber carbon in a range not less than 0.02 weight% and not greater than 4.8 weight%. The non-aqueous electrolytic cell according to the present invention having the aforementioned configuration exhibits preferable cell characteristics at a low temperature. Brief Description of the Drawing Fig. 1 is a longitudinal cross sectional view of an example of a non-aqueous electrolytic cell according to the present invention. Description of Preferred Embodiments Fig. 1 is a longitudinal cross sectional view of an example of a non-aqueous electrolytic cell according to the present invention. This non-aqueous electrolytic cell 1 includes a film-shaped positive electrode 2 and a film-shaped negative electrode 3 which are wound via a separator 4 so as to be wound layers which are contained in a cell can 5. The aforementioned positive electrode 2 is produced by applying a positive electrode composite agent containing a positive electrode active material and an adhesive onto a current collector, which is dried. The current collector may be, for example, a metal foil such as an aluminium foil. The aforementioned positive electrode active material may be a metal oxide, a metal sulfide, or a particular high-molecular material according to the type of cell to be obtained. For example, when producing a lithium-ion secondary cell, the positive electrode active material may be a metal sulfide or oxide such as TiS 2 , MoS 2 , NbSe 2 , V 2 O 5 , or the like. Moreover, it is possible to use a lithium composite oxide containing as a main content LiM x O 2 , (where M represents one or more than one transition metal, and x differs depending on the cell charge/discharge state and is normally between 0.05 and 1.10). The transition metal M constituting this lithium composite oxide is preferably Co, Ni, Mn, Fe, Al, V, Ti, or the like. More specifically, the lithium composite oxide may be LiCoO 2 , LiNiO 2 , LiNi y Co 1-y O 2 (where 0 < y < 1), LiMn 2 O 4 , or the like. Moreover, as the positive electrode active material, an inter-layer compound containing Li may also be used preferably. These lithium composite oxides can generate a high voltage and serves as a positive electrode active material having an excellent energy density. The positive electrode 2 maybe formed using more than one of these positive electrode active materials may be used in combination. Moreover, the adhesive used in the aforementioned positive electrode composite agent may be known adhesives which are usually used for the cell positive electrode composite agent. Moreover, it is possible to add known binders such as a conductive agent to the positive electrode composite agent. The negative electrode 3 is produced by applying a negative electrode composite agent containing a negative electrode active material and an adhesive onto a current collector and drying it. The current collector may be a metal foil such as a copper foil. When producing a lithium-ion secondary cell, it is preferable to use a material capable of doping and dedoping lithium, lithium alloy, or lithium ions. As the material capable of doping and dedoping lithium ions, there can be exemplified non-graphitizable carbon material, graphite material, and other carbon material. More specifically, it is possible to use carbon materials such as pyrocarbon, coke, graphite, organic high-molecular sintered compound, active carbon, or the like. The coke may be a pitch coke, needle coke, petroleum coke, or the like. Moreover, the organic high-molecular sintered compound may be a phenol resin, furan resin, or the like which have been sintered at an appropriate temperature and carbonized. In addition to the aforementioned carbon materials, as the material capable of doping and dedoping lithium, it is also possible to use a high molecule such as polyacetylene and polypyrol and an oxide such as SnO 2 . Moreover, the lithium alloy may be a lithium-aluminium alloy and the like. Moreover, as the adhesive of the negative electrode composite agent, it is possible to use known adhesives which are usually used for the negative electrode composite agent of the lithium-ion cell. It is also possible to add known binders to the aforementioned negative electrode composite agent. In the non-aqueous electrolytic cell according to the present invention, the negative electrode 3 is produced by using the aforementioned negative electrode materials in combination with a fiber carbon produced by a method detailed later. When the negative electrode 3 contains a fiber carbon, the internal resistance at a low temperature is decreased and the cell capacity is increased. The fiber carbon used for the negative electrode 3 may be, for example, a high molecule spun into a fiber shape, pitch, and other precursors which have been thermally treated, or so-called epitaxial carbon. The epitaxial carbon can be obtained by applying vapor of an organic substance such as benzene directly onto a substrate at a temperature of about 1000°C so as to grow a carbon crystal. Firstly, explanation will be given on the method to obtain a fiber carbon using a thermal treatment. Among the precursors used here, a high molecule spun into a fiber shape may be, for example, polyacrylonitrile (PAN), rayon, polyamide, lignin, polyvinylalcohol, and the like. Moreover, among the precursors, the pitch may be a pitch obtained from tar, asphalt, or the like by way of distillation such as vacuum distillation, normal pressure distillation, steam distillation, and treatments such as thermal condensation polymerization, extraction, chemical polymerization condensation, and the like. The tar may be obtained by a high temperature pyrolysis of coal tar, ethylene bottom oil, crude petroleum, and the like. Moreover, the pitch and the like produced during a dry distillation of lumber also serves as a precursor. Moreover, the aforementioned pitch may be made from polyvinyl chloride resin, polyvinyl acetate, polyvinyl butyrate, 3, 5-dimethylphenol resin, and the like as raw materials. In the aforementioned pitch, when maintained at about 400°C, aromatic rings contained in the pitch are condensed with one another into a multi-ring layered-orientated state. After this, when the temperature is increased above 500°C, the pitch becomes a solid carbon precursor, i.e., semi coke. This process is called a liquid-phase carbonization, which is typical in the process for producing a graphitizable carbon. In order to make the precursor unmeltable and stable, acid, oxygen, ozone, or the like is used for oxidizing the surface of the precursor. The oxidization method may be selected depending on the type of the precursor. However, the temperature in the oxidization should be below the melting point of the precursor. After the precursor has become unmeltable and stable, the precursor will not cause melting or pyrolysis during a carbonization which will be detailed later. It should be noted that the process for making the precursor unmeltable and stable may be repeated several times if necessary. The precursor becomes sufficiently unmeltable and stable by repeating the aforementioned process several times. The precursor which has become unmeltable and stable is then subjected to a thermal treatment in an inert gas such as nitrogen of 300°C to 700°C for carbonization. It should be noted that this carbonization process may be omitted depending on a particular case. The precursor which has been carbonized is calcinated in an inert gas so as to obtain a fiber carbon. The calcination conditions are as follows: the temperature increase speed is 1°C to 100°C/minute, the final temperature is 900°C to 1500°C, and the holding time at the final temperature is about 0 to 30 hours. Next, explanation will be given on a method to obtain a fiber carbon by vapor-phase epitaxis. In this case, the raw material may be any if it can be vaporized such as ethylene and propane which exist as a vapor at a room temperature or a material which can be vaporized when heated by a temperature below the pyrolysis temperature. The aforementioned raw material is applied directly onto the substrate. By performing the aforementioned process, the raw material grows a crystal into a fiber carbon. The temperature of the substrate is preferably 400°C to 1500°C, but can be selected according to the type of the raw material. Moreover, the substrate is preferably made from quartz, nickel, or the like but can be selected according to the type of the raw material. It should be noted that it is possible to use a catalyst for promoting the aforementioned epitaxis. The catalysis may be iron, nickel, mixture of iron and nickel, or the like which have been made into fine particles. It is also use as the catalyst metals which are generally called a graphitizing catalyst or an oxide of the graphitizing catalyst. The catalyst may be selected depending on the raw material. The fiber carbon may have an outer diameter and length selected according to the production conditions. When producing a fiber carbon by a thermal treatment of a high molecule spun material, the outer diameter and length of the fiber carbon can be adjusted by the inner diameter of the blow nozzle and the blow speed for forming a fiber shape. When producing a fiber carbon by the vapor-phase expitaxy, the outer diameter and the length can be adjusted by selecting a size of a substrate and a catalyst serving as a kernel of the crystal epitaxy. Moreover, the outer diameter and the length can be adjusted by defining the raw material supply quantity. It should be noted that the fiber carbon thus obtained may further be subjected to a graphitizing process in an inert gas stream. The graphitization conditions are as follows: the temperature increase speed is 1°C to 100°C/minute, the target temperature is above 2000°C and preferably, above 2500°C, and the target temperature is maintained for about 0 to 30 hours. Moreover, the fiber carbon obtained may be crushed according to the electrode thickness and the active material particle size. When the fiber carbon is crushed for use, it is possible to use a single fiber carbon as well. It should be noted that the crushing may be performed before or after the carbonization and calcination or during a temperature increase before the carbonization. The content of the aforementioned fiber carbon is preferably not less than 0.02 weight % and not greater than 5 weight % and more preferably, not less than 0.05 weight % and not greater than 4 weight %. When the content is not less than 5 weight %, the internal resistance value at a low temperature is increased and the cell capacity value is decreased. Moreover, when the content is below 0.02 weight %, it becomes impossible to obtain a sufficient effect of the fiber carbon contained. The outer diameter of the fiber carbon is preferably not greater than 20 µm. When the outer diameter is greater than 20 µm, it becomes impossible to obtain a sufficient effect of the fiber carbon contained. The specific area of the aforementioned fiber carbon is preferably not greater than 50 m 2 /g and more preferably, not less than 0.5 m 2 /g and not greater than 50 m 2 /g. When the specific area is greater than 50 m 2 /g, the cell initial capacity is decreased. Moreover, when the specific area is smaller than 0.5 m 2 /g, it is impossible to obtain a sufficient effect of the fiber carbon contained. The bulk density of the aforementioned fiber carbon is in a range not less than 0.01 g/cm 3 and not greater than 1.8 g/cm 3 . When the bulk density is below 0.01 g/cm 3 , the cell initial capacity is lowered. Moreover, when the bulk density is greater than 1.8 g/cm 3 , it is impossible to obtain a sufficient effect of the fiber carbon contained. The non-aqueous electrolytic liquid is prepared by solving an electrolytic material in a non-aqueous solvent. The electrolytic material may be any of the known electrolytic material conventionally used for a cell electrolytic liquid. More specifically, there can be exemplified LiPF 6 , LiBF 4 , LiAsF 6 , LiClO 4 , LiCH 3 SO 3 , LiCF 3 SO 3 , LiN(SO 2 CF 3 ) 2 , LiC(SO 2 CF 3 ) 3 , LiAlCl 4 , LiSiF 6 , LiB(C 6 H 5 ) 4 , LiCl, LiBr, and the like. Moreover, the aforementioned non-aqueous solvent may be any of the known non-aqueous solvents conventionally used for the non-aqueous electrolytic liquid such as propylene carbonate, ethylene carbonate, vinylene carbonate, 1,2-dimethoxyethane, 1, 2-ethoxyethane, diethyl carbonate, dimethyl carbonate, γ-butyrolactone, tetrahydrofuran, 2-methyltetrahydrofuran, 1, 3-dioxolane, 4-methyl-1, 3-dioxolane, diethyl ether, sulfolane, methylsulfolane, acetonitrile, propiononitrile, methyl propionate, methyl butyrate, and the like. Each of these non-aqueous solvents may be used solely or in combination with the others. The non-aqueous electrolytic cell1 is prepared as follows. The positive electrode is prepared by uniformly applying the positive electrode composite agent containing a positive electrode active material and an adhesive as has been explained above, onto a metal foil such as an aluminium foil to serve as a positive electrode current collector and drying the positive electrode composite agent so as to form a positive electrode active material layer. The negative electrode 3 is prepared by uniformly applying the negative electrode composite agent containing a negative electrode active material and an adhesive as has been described above, onto a metal foil such as a copper foil to serve as the negative electrode current collector, and drying the negative electrode composite agent so as to form a negative electrode active material layer. The positive electrode 2 and the negative electrode 3 thus obtained are attached to each other via the separator 4 made from, for example, a porous polypropylene film and wound into an eddy shape so as to obtain a wound layered body. Next, an insulation plate 6 is inserted onto the bottom of the cell can and the wound layered body is placed. The cell can 5 may be made from iron, nickel, stainless steel, aluminium, titanium, or the like. In case the cell operation causes electro-chemical corrosion of the cell can in the non-aqueous electrolytic liquid, the can may be plated. Next, for current collection of the negative electrode, one end of a negative electrode lead wire 7 made from, for example, nickel is fixed to the negative electrode 3 and the other end is welded to the cell can 5. Thus, the cell can 5 becomes conductive to the negative electrode 3 and serves as an external negative electrode of the non-aqueous electrolytic cell1. Moreover, for current collection of the positive electrode 2, one end of a positive electrode lead wire 8 made from, for example, aluminium is attached to the positive electrode 2 and the other end is electrically connected to a cell cover 10 via a current cut-off thin plate 9. The current cut-off thin plate 9 cuts off current according to the cell inner pressure. Thus, the cell cover 10 becomes conductive to the positive electrode and serves as an external positive electrode of the non-aqueous electrolytic cell 1. Next, a non-aqueous electrolytic liquid is poured into the cell can 5. This non-aqueous electrolytic liquid, as has been described above, is prepared by solving an electrolytic material in a non-aqueous solvent. Next, the cell can 5 is caulked via an insulation seal gasket 11 coated with asphalt, so as to fix the cell cover 10 and obtain the non-aqueous electrolytic cell 1 of a cylindrical shape. It should be noted that as shown in Fig. 1, this non-aqueous electrolytic cell 1 includes: a center pin 12 for connecting the negative lead wire 7 and the positive lead wire 8; a safety valve apparatus 13 for removing the inner gas when the pressure inside the cell has become above a predetermined value; and a PTC element 14 for preventing the temperature increase in the cell. The non-aqueous electrolytic cell 1 according to the aforementioned embodiment is not to be limited to a particular shape and may have any shape such as a cylindrical, rectangular, coin or button shape and may have any size such as thin type or large size type. In the aforementioned embodiment, the non-aqueous electrolytic cell has been explained as a non-aqueous electrolytic liquid cell using a non-aqueous electrolytic liquid. However, the present invention is not to be limited to this. The present invention can be applied to a case when the non-aqueous electrolytic material is a so-called polymer gel electrolytic material, i.e., a high-molecular compound such as polyvinylidene fluoride and polyacrylonitrile containing a non-aqueous solvent. Moreover, the present invention can be applied to a primary cell and to a secondary cell. Examples Next, explanation will be given on specific examples of the present invention. Example 1 Firstly, a graphite powder was prepared to be used for the negative electrode. For 100 weight parts of coal coke, 30 weight parts of coal tar pitch is added and mixed at about 100°C, after which the mixture is compression-molded by a press to obtain a carbon molded precursor. The carbon molded precursor is subjected to a thermal treatment at a temperature not greater than 1000°C to obtain a carbon molded body. This carbon molded body was impregnated with a binder pitch solved at a temperature not greater than 200°C, after which a thermal treatment was performed at a temperature not greater than 1000°C. This process of pitch impregnation and the sintering was repeated several times. After this, the carbon molded body was subjected to a thermal treatment in an inert gas stream at 2700°C to obtain a graphitized molded body, which was crushed into several classes to prepare a graphite powder. The graphite powder was subjected to an X-ray structure analysis and it was found that the plane interval of the (002) plane was 0.337 nm and the C axis of the (002) plane had a thickness of 50.0 nm. The pycnometer method was applied to find that the graphite powder had a true density of 2.23 g/cm 3 and a bulk density of 0.83 g/cm 3 . The Brunauer-Emmett-Teller method (BET method) was used to find that the graphite powder had a specific area of 4.4 m 2 /g. The graphite powder was subjected to a laser analysis method to find that the average grain diameter of the grain size distribution was 3.12 µm; the accumulative 10% grain diameter was 12.3 µm; the accumulative 50% grain diameter was 29.5 µm; and the accumulative 90% grain diameter was 53.7 µm. Moreover, by the aforementioned laser analysis method, it was found that the graphite powder had a graphite grain breaking strength of 7.1 kgf/mm 2 as an average. The graphite powder thus prepared was mixed with 1 weight % of fiber carbon having an outer diameter of 0.2 µm, a specific area of 15 m 2 /g, and bulk density of 0.1 g/cm 3 to obtain a negative electrode material. The negative electrode material was used to prepare a negative electrode. 90 weight parts of the negative electrode material was mixed with 10 weight parts of polyvinylidene fluoride (PVDF) as a binder, and the mixture was dispersed in N-methylpyrolidone into a slurry state to obtain a negative electrode composite agent slurry. The negative electrode composite agent slurry was uniformly applied onto the both surfaces of a belt-shaped copper foil having a thickness of 10 µm serving as a negative electrode current collector and after dried, pressure-molded with a constant pressure to obtain a belt-shaped negative electrode. Next, a positive electrode was prepared as follows. Lithium carbonate 0.5 mol was mixed with cobalt carbonate 1 mol and this mixture was burnt in the atmosphere at temperature of 900°C for 5 hours. The burnt material was subjected to an X-ray structure analysis and it was found that the peak almost matched with LiCoO 2 registered in the JCPDS file. That is, the burnt material was identified as LiCoO 2 . The LiCoO 2 was crushed to a degree that the 50% grain diameter obtained by the laser analysis method was 15 µm, so as to obtain LiCoO 2 powder. Then, 95 weight parts of the LiCoO 2 powder was mixed with 5 weight parts of lithium carbonate powder. 91 weight parts of the mixture, 6 weight parts of scaly graphite as a conductive agent, and 3 weight parts of PVDF as a binder were mixed and dispersed in N-methylpyrolidone as a solvent to obtain a slurry state, i.e., a positive electrode composite agent slurry. The positive electrode composite agent slurry was uniformly applied onto the both sides of a belt shaped aluminium foil having a thickness of 20 µm serving as a positive electrode current collector and after dried, pressure-molded with a constant pressure to obtain a belt-shaped positive electrode. Next, the electrodes and the separator were layered in the order of the negative electrode, the separator, the positive electrode, and the separator. The layered body was wound plenty of times to obtain a wound electrode body. The separator used was a porous polypropylene film having a thickness of 25 µm. The outer diameter of the wound electrode body was 18 mm. The wound electrode body thus prepared was placed in a cell can plated with nickel. An insulator was arranged on the upper and lower surfaces of the wound electrode body, and the aluminium positive electrode lead wire was brought out from the positive electrode current collector and welded to the cell cover. Moreover, the nickel negative electrode lead wire was brought out from the negative electrode current body and welded to the cell can. Next, a non-aqueous electrolytic liquid was poured into the cell can. The non-aqueous electrolytic liquid was prepared by mixing identical volumes of ethylene carbonate (EC) and dimethyl carbonate (DMC), to which 1.0 mol/l of LiPF 6 was added. Next, the cell can was caulked via an insulation seal gasket having a surface coated with asphalt, so as to fix the safety apparatus having the current cut-off mechanism, the PTC element, and the cell cover and to maintain air-tightness in the cell. Thus, a cylindrical non-aqueous electrolytic secondary cell having a diameter of 18 mm and height of 65 mm was prepared. Example 2 A cylindrical non-aqueous electrolytic secondary cell was prepared in the same way as Example 1 except for that the quantity of fiber carbon to be mixed in the negative electrode material was 2 weight %. Example 3 A cylindrical non-aqueous electrolytic secondary cell was prepared in the same way as Example 1 except for that the quantity of fiber carbon to be mixed in the negative electrode material was 3 weight %. Example 4 A cylindrical non-aqueous electrolytic secondary cell was prepared in the same way as Example 1 except for that the quantity of fiber carbon to be mixed in the negative electrode material was 4 weight %. Example 5 A cylindrical non-aqueous electrolytic secondary cell was prepared in the same way as Example 1 except for that the quantity of fiber carbon to be mixed in the negative electrode material was 4.8 weight %. Example 6 A cylindrical non-aqueous electrolytic secondary cell was prepared in the same way as Example 1 except for that the quantity of fiber carbon to be mixed in the negative electrode material was 0.05 weight %. Example 7 A cylindrical non-aqueous electrolytic secondary cell was prepared in the same way as Example 1 except for that the quantity of fiber carbon to be mixed in the negative electrode material was 0.02 weight %. Example 8 A cylindrical non-aqueous electrolytic secondary cell was prepared in the same way as Example 1 except for that the quantity of fiber carbon to be mixed in the negative electrode material was 0.01 weight %. Example 9 A cylindrical non-aqueous electrolytic secondary cell was prepared in the same way as Example 1 except for that the quantity of fiber carbon to be mixed in the negative electrode material was 5 weight %. Example 10 A cylindrical non-aqueous electrolytic secondary cell was prepared in the same way as Example 1 except for that the quantity of fiber carbon to be mixed in the negative electrode material was 6 weight %. Example 11 A cylindrical non-aqueous electrolytic secondary cell was prepared in the same way as Example 1 except for that the fiber carbon to be mixed in the negative electrode material had an outer diameter of 0.1 µm and a specific area of 18 m 2 /g. Example 12 A cylindrical non-aqueous electrolytic secondary cell was prepared in the same way as Example 1 except for that the fiber carbon to be mixed in the negative electrode material had an outer diameter of 0.01 µm and a specific area of 25 m 2 /g. Example 13 A cylindrical non-aqueous electrolytic secondary cell was prepared in the same way as Example 1 except for that the fiber carbon to be mixed in the negative electrode material had an outer diameter of 0.008 µm and a specific area of 50 m 2 /g. Example 14 A cylindrical non-aqueous electrolytic secondary cell was prepared in the same way as Example 1 except for that the fiber carbon to be mixed in the negative electrode material had an outer diameter of 1 µm and a specific area of 9 m 2 /g. Example 15 A cylindrical non-aqueous electrolytic secondary cell was prepared in the same way as Example 1 except for that the fiber carbon to be mixed in the negative electrode material had an outer diameter of 0.007 µm and a specific area of 70 m 2 /g. Example 16 A cylindrical non-aqueous electrolytic secondary cell was prepared in the same way as Example 1 except for that the fiber carbon to be mixed in the negative electrode material had an outer diameter of 0.3 µm and a specific area of 5 m 2 /g. Example 17 A cylindrical non-aqueous electrolytic secondary cell was prepared in the same way as Example 1 except for that the fiber carbon to be mixed in the negative electrode material had an outer diameter of 20 µm, a specific area of 0.5 m 2 /g, and a bulk density of 1.6 g/cm 3 . Example 18 A cylindrical non-aqueous electrolytic secondary cell was prepared in the same way as Example 1 except for that the fiber carbon to be mixed in the negative electrode material had a specific area of 20 m 2 /g and a bulk density of 0.005 g/cm 3 . Example 19 A cylindrical non-aqueous electrolytic secondary cell was prepared in the same way as Example 1 except for that the fiber carbon to be mixed in the negative electrode material had an outer diameter of 30 µm, a specific area of 0.2 m 2 /g, and a bulk density of 1.8 g/cm 3 . Example 20 A cylindrical non-aqueous electrolytic secondary cell was prepared in the same way as Example 1 except for that the fiber carbon to be mixed in the negative electrode material had a specific area of 20 m 2 /g and a bulk density of 0.5 g/cm 3 . Example 21 A cylindrical non-aqueous electrolytic secondary cell was prepared in the same way as Example 1 except for that the fiber carbon to be mixed in the negative electrode material had an outer diameter of 0.09 µm, a specific area of 20 m 2 /g, and a bulk density of 0.01 g/cm 3 . Comparative Example 1 A cylindrical non-aqueous electrolytic secondary cell was prepared in the same way as Example 1 except for that the negative material did not contain any fiber carbon. The cells thus prepared were charged. The charge conditions were as follows: the temperature was 23°C, the constant current was 0.5A, the maximum voltage was 4.2V, the charge was performed with a constant current and a constant voltage, and the charge time was 4 hours. Next, discharge was performed at 23°C with a constant current of 0.5A until the final voltage became 2.75V to check the initial capacity of the aforementioned cells. Next, the cells were again charged under the conditions as follows. The temperature was 23°C, the constant current was 1.0A, the maximum voltage was 4.2V, the charge was performed with a constant current and a constant voltage, and the charge time was 2.5 hours. Next, cell characteristics were checked at a low temperature. Firstly, the cells were placed under the temperature of -35°C for 3 hours. After this, under the temperature of -35°C, with a frequency of 1 KHz, and voltage of 10mV applied, the AC impedance was measured to check the cell internal resistance. After this, at the temperature of -35°C with a constant current 0.7A, discharge was performed until the final voltage became 2.75V, so as to check the cell capacity. Table 1 below shows results of the aforementioned measurements on the initial capacity, the cell internal resistance at -35°C, and the cell capacity at -35°C of the cells prepared in Examples 1 to 21 and Comparative Example 1. Fiber carbon content (weight %) Fiber carbon outer diameter (µm) Fiber carbon specific area (m 2 /g) Example 1 1.00 0.200 15.0 Example 2 2.00 0.200 15.0 Example 3 3.00 0.200 15.0 Example 4 4.00 0.200 15.0 Example 5 4.80 0.200 15.0 Example 6 0.05 0.200 15.0 Example 7 0.02 0.200 15.0 Example 8 0.01 0.200 15.0 Example 9 5.00 0.200 15.0 Example 10 6.00 0.200 15.0 Example 11 1.00 0.100 18.0 Example 12 1.00 0.010 25.0 Example 13 1.00 0.008 50.0 Example 14 1.00 1.000 9.0 Example 15 1.00 0.007 70.0 Example 16 1.00 0.300 5.0 Example 17 1.00 20.000 0.5 Example 18 1.00 0.200 20.0 Example 19 1.00 30.000 0.2 Example 20 1.00 0.200 20.0 Example 21 1.00 0.090 20.0 Comparative Example 1 0.00 ― ― Fiber carbon bulk density (g/cm 3 ) Initial capacity (mAh) Example 1 0.100 1625 Example 2 0.100 1622 Example 3 0.100 1615 Example 4 0.100 1605 Example 5 0.100 1606 Example 6 0.100 1625 Example 7 0.100 1608 Example 8 0.100 1624 Example 9 0.100 1602 Example 10 0.100 1595 Example 11 0.100 1620 Example 12 0.100 1615 Example 13 0.100 1614 Example 14 0.100 1620 Example 15 0.100 1532 Example 16 0.100 1616 Example 17 1.600 1603 Example 18 0.005 1554 Example 19 1.800 1601 Example 20 0.500 1630 Example 21 0.010 1600 Comparative Example 1 ― 1600 Cell capacity at -35°C (mAh) Cell internal resistance at -35°C (mΩ) Example 1 400 88 Example 2 481 70 Example 3 502 68 Example 4 405 72 Example 5 350 90 Example 6 332 105 Example 7 270 128 Example 8 62 140 Example 9 70 138 Example 10 64 141 Example 11 385 90 Example 12 472 72 Example 13 479 70 Example 14 288 121 Example 15 323 86 Example 16 370 92 Example 17 266 129 Example 18 367 95 Example 19 68 139 Example 20 500 67 Example 21 479 70 Comparative Example 1 59 152 Table 1 shows that Examples 1 to 21 using fiber carbon in the negative electrode material have smaller internal resistance values at -35°C and greater cell capacity values than Comparative Example 1 not using the fiber carbon in the negative electrode material. The reason is considered to be that when fiber carbon is inserted between negative electrode grains, the electrolytic liquid has a greater strength to maintain the liquid state and lithium ions are doped and dedoped smoothly even at a low temperature. However, as can be seen from Example 8, when the content of the fiber carbon in the negative electrode material is 0.01 weight %, the internal resistance at -35°C is increased and it is impossible to obtain a sufficient effect to reduce the cell capacity value. Moreover, as can be seen from Example 9 and Example 10, when the content of the fiber carbon in the negative electrode material is not less than 5 weight %, the internal resistance at -35°C is increased and the cell capacity value becomes smaller. Consequently, the content of the fiber carbon in the negative electrode material is preferably in a range not less than 0.02 weight % and below 5 weight %. Moreover, as can be seen from Examples 1 to 7, the range is more preferably not less than 0.05 weight % and not greater than 4 weight %. Moreover, as can be seen from Example 19, when the outer diameter of the fiber carbon contained in the negative electrode material is 30 µm, the internal resistance at -35°C is increased and it is impossible to obtain a sufficient effect to reduce the cell capacity value. As can be seen from the comparison between Example 1, Examples 11 to 14, Examples 16 and 17, and Example 21, the outer diameter of the fiber carbon in the negative electrode material is preferably in a range not greater than 20 µm. Furthermore, as can be seen from Example 15, when the specific area of the fiber carbon contained in the negative electrode material is 70 m 2 /g, the initial capacity value is lowered than Comparative Example 1 although the internal resistance at -35 °C and the cell capacity value remain unchanged. The comparison between Example 1, Examples 11 to 14, Examples 16 and 17, and Examples 20 and 21 shows that the specific area of the fiber carbon in the negative electrode material is preferably in a range not greater than 50 m 2 /g. Moreover, as can be seen from Example 19, when the specific area is 0.2 m 2 /g, although the cell initial capacity value remains unchanged, the internal resistance at -35°C is increased and it is impossible to obtain a sufficient effect to reduce the cell capacity value. Accordingly, the specific area of the fiber carbon in the negative electrode material is more preferably in a range not less than 0.5 m 2 /g and not greater than 50 m 2 /g. Moreover, as can be seen from Example 18, when the bulk density of the fiber carbon in the negative electrode material is 0.005 g/cm 3 , although the internal resistance at -35°C and the cell capacity value are improved, the cell initial capacity is lowered than Comparative Example 1. The comparison between Example 1, Example 17, and Examples 20 and 21 shows that the bulk density of the fiber carbon in the negative electrode material is preferably in a range not less than 0.01 g/cm 3 . Moreover, as can be seen from Example 19, when the bulk density of the fiber carbon contained in the negative electrode material is 1.8 g/cm 3 , although the cell initial capacity remains unchanged, the internal resistance at -35°C is increased and it is impossible to obtain a sufficient effect to reduce the cell capacity value. Accordingly, the bulk density of the fiber carbon in the negative electrode material is more preferably in a range not less than 0.01 g/cm 3 and not greater than 1.8 g/cm 3 . As is clear from the above given explanation, since the non-aqueous electrolytic cell according to the present invention contains fiber carbon in the negative electrode, the internal resistance value at a low temperature is lowered and the cell resistance value is increased. Accordingly, the cell can also be used at a low temperature.

Claims: A non-aqueous electrolytic cell comprising a negative electrode capable of doping and dedoping lithium ions, a positive electrode capable of doping and dedoping lithium ions, and a non-aqueous electrolyte, wherein the negative electrode comprises a negative electrode material capable of doping and dedoping lithium ions and the negative electrode material Is containing fiber carbon in a range not less than 0.02 weight% and not greater than 4.8 weight%. A non-aqueous electrolytic cell according to claim 1, wherein the fiber carbon is contained in the negative electrode material in an amount of not less than 0.05 weight% and not greater than 4 weight%. A non-aqueous electrolytic cell as claimed in claim 1, wherein the fiber carbon has an outer diameter in a range not greater than 20 µm. A non-aqueous electrolytic cell as claimed in claim 1, wherein the fiber carbon has a specific area in a range not greater than 50 m 2 /g. A non-aqueous electrolytic cell as claimed in claim 1, wherein the fiber carbon has a bulk density in a range not less than 0.01 g/cm 3 and not greater than 1.8 g/cm 3 . A non-aqueous electrolytic cell as claimed in claim 1, wherein the negative electrode capable of doping and dedoping lithium ions contains a negative electrode material selected from a group consisting of carbon material, polyacetylene, polypyrole, and oxide. A non-aqueous electrolytic cell as claimed in claim 6, wherein the carbon material is a non-graphitizable carbon or graphite. A non-aqueous electrolytic cell as claimed in claim 1, the positive electrode capable of doping and dedoping lithium ions contains a positive electrode material selected from a group consisting of TiS 2 , MoS 2 , NbSe 2 , V 2 O 5 , and LiM x O 2 (where M represents one or more than one transition metal and x differs depending on the cell charge/discharge state and is normally not less than 0.05 and not greater than 1.10). A non-aqueous electrolytic cell as claimed in claim 1, wherein the electrolyte is at least one selected from a group consisting of LiPF 6 , LiBF 4 , LiAsF 6 , LiClO 4 , LiCH 3 SO 3 , LiCF 3 SO 3 , LiN(SO 2 CF 3 ) 2 , LiC(SO 2 CF 3 ) 3 , LiAlCl 4 , LiSiF 6 . LiB(C 6 H 5 ) 4 , LiCl, and LiBr.

Inventors: NAGAMINE MASAYUKI, OMARU ATSUO, YAMAGUCHI AKIRA, NAGAMINE, MASAYUKI, OMARU, ATSUO, YAMAGUCHI, AKIRA, NAGAMINE, MASAYUKI, SONY ENERGYTEC INC., OMARU, ATSUO, SONY ENERGYTEC INC., Yamaguchi, Akira, SONY ENERGYTEC INC.
Applicants: SONY CORP, SONY CORPORATION
Application year: 2000
Main classification: H01M10
IPC codes: H01M10, H01M4, H01M6