COATING COMPOSITION

Abstract: The present invention relates to a coating composition containing 0.1 to 50 parts by weight of (A) an organosilicate and/or its condensates per 100 parts by weight of a resin solid content in the coating composition, and 0.1 to 50 parts by weight of (B) an acid surface active agent or a boric acid compound per 100 parts by weight of a solid content of the component (A).

Description: The present invention relates to a coating composition for use at room temperature and which is capable of forming a coating film showing a low contamination from early time after coating. An outdoor coating composition showing good weather resistance has conventionally been applied onto outdoor substrates such as building structures, displays, guard fences, machines, vehicles and the like for the purpose of decoration or protection. However, the conventionally used outdoor coating composition has the disadvantage that the surface of a coated product may easily be contaminated and show poor appearance by influence of exhaust gas, sand, dust, iron powder, rain, sunlight, etc. during outdoor exposure. In connection therewith, the present applicant proposed a coating composition with the addition of an organosilicate and/or its condensates which makes it possible to form a coating film having self-cleaning properties and hard to be contaminated (see International Publication No. WO94/06870 specification). However, the above coating composition had such drawbacks that hydrolysis of the organosilicate in the coating film does not easily take place depending on the weather on coating or immediately after coating, so the film may be easily contaminated before developing self-cleaning properties. An initial contamination may disappear with time, but may cause claims from clients, and self-cleaning properties from early time after coating are demanded. Disclosure of the Invention The present inventors made intensive studies for the purpose of solving the above problems to find out that a coating composition containing specified amounts of an organosilicate and/or its condensate and a boric acid compound can form a coating film showing a low contamination from early time after coating and good interlayer adhesion properties between the coating film and a substrate. That is, the present invention provides a coating composition which is for use at room temperature to form a coating film showing hydrophilic properties, said composition containing (A) 0.1 to 50 parts by weight of an organosilicate represented by the general formula: where the R groups are the same or different and each represents a hydrogen atom or a monovalent hydrocarbon group having 1 to 7 carbon atoms, and/or a condensate thereof per 100 parts by weight of a resin solid content in the coating composition, and (B) 0.1 to 50 parts by weight of a boric acid compound per 100 parts by weight of a solid content of the component (A), said coating composition being selected from (1) a curable resin composition comprising (a) a base resin consisting of a hydroxyl group-containing resin dissolved or dispersed into an organic solvent, and (b) a crosslinking agent; and (2) an organic solvent based non-crosslinking coating composition capable of forming a coating film by volatilizing the organic solvent at room temperature and selected from a cellulose derivative based coating composition, acrylic resin based coating composition, urethane resin based coating composition, vinyl chloride resin based coating composition, fluorocarbon resin based coating composition, alkyd resin based coating composition, vinyl acetate resin based coating composition and styrene-butadiene resin based coating composition. Brief Description of the Drawing Fig. 1 is a schematic view of a test panel. Preferable Embodiment in the Practice of the Invention The organosilicate and/or its condensates (A) used in the present invention include ones represented by the above and following formulas. The R groups in the above formula may be selected from alkyl and aryl groups, for example. An alkyl group may be straight-chain or branched, for example, methyl, ethyl, n-propyl, iso-propyl, n-butyl, iso-butyl, tert-butyl, n-pentyl, iso-pentyl, neopentyl, n-hexyl, iso-hexyl, and the like. Of these, lower alkyl groups having 1 to 4 carbon atoms are preferred. An aryl group may be monocyclic or polycyclic, for example, phenyl group, toluyl group or xylyl group, phenyl group being preferred. Preferable examples of the organosilicate used in the present invention may include tetrahydroxysilane, tetramethoxysilane, tetraethoxysilane, tetrapropoxysilane, tetrabutoxysilane, tetraphenoxysilane and dimethoxydiethoxysilane. These may be used alone or in combination. The condensate of organosilicate may include branched or straight-chain condensates between organosilicates represented by the above general formula and preferably includes condensates having a degree of condensation of 2 to 100 and represented by the general formula: where R is defined as above, n is an integer of 2 to 100. In the above general formula, when n is more than 100, effect of stain resistance is undesirably reduced. The condensate of the organosilicate may particularly include such ones that R in the general formula is a lower alkyl group having 1 to 4 carbon atoms and that the degree of condensation is in the range of 2 to 15. Use of an organosilicate and/or its condensate (A) containing both ethyl group and methyl group as R in the above general formula is preferable from the standpoints of ease of floating of the component (A) up to the surface of the coating film and hydrolysis, and an ethyl group/methyl group mixing ratio is in the range of 1/99 to 99/1, preferably 30/70 to 70/30, more preferably 40/60 to 60/40. Ethyl group in an amount less than in the above mixing ratio range makes undesirably difficult the floating of the component (A) up to the surface of the coating film, and methyl group in a less amount may undesirably retard hydrolysis. In the present invention, a modified organosilicate prepared by reacting the organosilicate and/or its condensate (A) with a mercapto compound or a boric acid compound may also be used from the standpoint of promoting the hydrolysis reaction. On the other hand, modification of the organosilicate and/or its condensate (A) by introducing an alkyl chain having 8 or more carbon atoms may be effective for reducing the following solubility parameter, but orientation of the long chain alkyl moiety on the surface of the coating film may retard hydrolysis, resulting in making it impossible to form a coating film capable of showing low contamination from the early time after coating. The organosilicate and/or its condensate (A) is desirably selected so as to have a solubility parameter (hereinafter may simply be referred to as SP) lower than that of the resin contained in the coating composition, to which the component (A) is added. A higher SP value of the organosilicate and/or its condensate (A) compared with that of the resin in the coating composition may make difficult the orientation of the organosilicate and/or its condensate (A) onto the surface of the coating An film, resulting in reducing stain resistance. An SP difference between the organosilicate and/or its condensate (A) and the resin in the coating composition is preferably 0.01 or more, more preferably 0.1 or more. In the present invention, a mixing amount of the organosilicate and/or its condensate (A) is in the range of 0.1 to 50 parts by weight, preferably 1 to 20 parts by weight per 100 parts by weight of the resin solid content in the coating composition. A mixing amount less than 0.1 part by weight may result poor stain resistance of the coating film, and the mixing amount more than 50 parts by weight may result drawbacks of the resulting coating film, for example, hardening, cracks, reduction in gloss and the like. The boric acid compound (B) in the present invention has a function to promote hydrolysis of the organosilicate and/or its condensate (A), and may include ones known in the art without particular limitations, for example, boric acid or trialkyl borate. Examples of the trialkyl borate as the boric acid compound may include trimethyl borate, triethyl borate and tributyl borate. In the present invention, a condensation product of the organosilicate and/or its condensate (A) with the boric acid compound (B) may also be used. The boric acid-modified organosilicate and/or its condensate may be prepared by heating and reacting the organosilicate and/or its condensate, for example, tetramethoxysilane, tetraethoxysilane, methyltrimethoxysilane, ethyltrimethoxysilane and their condensates with orthoboric acid or methaboric acid in the presence of an alcohol solvent as disclosed in Japanese Patent Application Laid-Open No. 69634/89. In the present invention, the boric acid compound (B) may be mixed in an amount in the range of 0.1 to 50 parts by weight, preferably 1 to 30 parts by weight per 100 parts by weight of the solid content of the organosilicate and./or its condensate (A). A mixing amount less than 0.1 part by weight makes it difficult to develop hydrophilic properties from early time after coating, and a mixing amount more than 50 parts by weight may undesirably shorten a service period of time or result reduction in gloss. The coating composition may be a reactively curing one or a non-crosslinking one. The reactively curing coating composition may include a coating composition prepared by dissolving or dispersing a curable resin composition capable of forming a crosslinked coating film structure by being reacted and cured per se into an organic solvent, for example, a coating composition containing a curable resin composition comprising a base resin consisting of a hydroxyl group-containing resin such as fluorocarbon resin, acrylic resin, polyester resin, alkyd resin, silicone resin and the like, and a crosslinking agent such as polyisocyanate, amino resin and the like, and may also include a coating composition containing a curable resin composition comprising a base resin consisting of a resin containing silanol group and/or hydrolyzable silyl group, hydroxyl group and epoxy group as essential functional group components, or mixtures thereof, and a curing catalyst. The coating composition of the present invention may optionally contain additives for use in the coating composition, for. example, colorant, filler, flow control agent, anti-foaming agent, plastisizer, curing catalyst, ultraviolet light absorber, and the like. The coating composition of the present invention is applicable various kinds of substrates and coating substrates thereof, and coating thereof may be carried out by the general coating methods such as brushing, spray coating, roller coating, various coater coatings, and the like. A coating amount is preferably in the range of 2 to 100 µm, preferably 10 to 40 µm as a dry film thickness. Example The present invention is explained more in detail by the following Examples, in which "part" and "%" mean "part by weight" and "% by weight" respectively. Examples 1-4 and Comparative Examples 1-11. Respective commercially available coating compositions shown in Table 1 were mixed and stirred with the organosilicate and/or its condensate, and a boric acid compound in accordance with the formulations (amount based on the resin solid content of the coating composition) as shown in Table 1 to prepare respective coating compositions of Examples 1-4 and Comparative Examples 1-11. In Table 1, (Note 1) to (Note 11) are explained as follows. (Note 1) Ales Retan: Trade name, marketed by Kansai Paint Co., Ltd., solvent based acrylic urethane resin coating composition, SP value of the resin: 9.24. (Note 2) ES48: Trade name, marketed by Colcoat Co., Ltd., low condensation product of ethyl silicate, SP value: 8.84. (Note 3) Boric acid-modified ethyl silicate: A reactor was charged with 744 g of Ethyl Silicate 40 (trade name, marketed by Tama Chemicals Co., Ltd.), 62 g of orthoboric acid and 178 g of ethyl alcohol, followed by heating and reacting under reflux for 2 hours, and carrying out condensation reaction for one hour while solvating by 316 g to obtain a boric acid-modified ethyl silicate having a nonvolatile content of 80%. (Note 4) Triethyl borate: Reagent marketed by Tokyo Kasei Kogyo Co., Ltd. (Note 5) EMS-485: Trade name, marketed by Colcoat Co., Ltd., low condensation product of ethyl/methyl silicate, ethyl/methyl = 50/50 (molar ratio), SP 8.75. (Note 6) X40-2638: Trade name, marketed by Shinetsu Chemical Co., Ltd., low condensation product of long chain (C 10 ) alkyl-modified ethyl/methyl silicate, SP7.79. (Note 7) X41-1805: Trade name, marketed by Shinetsu Chemical Co., Ltd., low condensation product of mercapto-modified ethyl/methyl silicate, SP8.26. (Note 8) Modified organosilicate: A reactor equipped with a stirrer, thermometer, reflux condenser, nitrugen inlet and water separator was charged with 500 g of ES-48 (trade name, marketed by Colcoat Co., Ltd., ethyl silicate), 345 g of n-octanol (C 8 ) and 0.082 g of Scat 24 (trade name, marketed by Sankyo Organic Chemicals Co., Ltd.), followed by heating up to 120°C with agitation under nitrogen atmosphere, heating up to 160°C over 4 hours, keeping at that temperature for one hour to obtain a long chain alcohol-modified organosilicate having a SP of 8.26. Coating Film Performance Test Coating films of Examples 1-4 and Comparative Examples 1-11 as shown in Table 1 were subjected to coating film performance tests as follows. Results are shown in Table 2. Preparation of Test Panel: Esco (trade name, marketed by Kansai Paint Co., Ltd., Epoxy resin based anticorrosive coating composition) was coated onto a zinc phosphate-treated 0.8 mm thick steel sleet so as to be a dry film thickness of 50 µm respectively, followed by drying for one day, coating an Epomarine intercoating (trade name, marketed by Kansai Paint Co., Ltd., Epoxy resin based intercoat coating composition) so as to be a dry film thickness of 30 µm, and drying for one day to prepare a test panel respectively. A stripe-like contaminating rain mark resistant properties test was carried out by use of a test panel shown in Fig. 1. In Table 2, (*1) to (*4) are represented as follows. (*1) Hydrophilic Properties: Respective coating compositions of Examples and Comparative Examples were coated onto a test panel so as to be a dry film thickness of about 20 µm, followed by drying for 7 days under the conditions of 20°C and 65% RH to obtain a coating test panel respectively, applying the coating test panel to a Sunshine Carbon Arc Weathermeter for 4 hours respectively, and measuring a contact angle (°) to water on the surface of a resulting coating film respectively. (*2) Stripe-like contaminating rain mark resistant properties: Respective coating compositions of Examples and Comparative Examples were coated in the same manner as in the above (*1) onto the test panel shown in Fig. 1 to prepare a coating test panel respectively, exposing outdoors for 3 months in such a condition as shown in Fig. 1 on the north side at Ota-ku, Tokyo, Japan, respectively, and visually evaluating stripe-like contaminating rain marks as follows. 4: No stripe-like contaminating rain marks developed, 3: some stripe-like contaminating rain marks developed, 2: No stripe-like contaminating rain marks developed, but contamination developed all over the surface, 1: stripe-like contaminating rain marks developed, and contamination developed all over the surface. (*3) Self-recoat properties: Respective coating compositions of Examples and Comparative Examples were coated onto a test panel so as to be a dry film thickness of about 20 µm respectively, followed by drying for 7 days under the conditions of 20°C and 65% RH, recoating thereonto the above coating compositions so as to be a dry film thickness of about 20 µm, and drying for 7 days under the conditions of 20°C and 65% RH to obtain a coating test panel, completely dipping into water for 48 hours, taking out the coating test panel, two hours thereafter, making cross cuts, adhering an adhesive cellophane tape, and peeling off immediately thereafter to examine the surface of the coating film respectively. Evaluation was made as follows. 3: No peeling observed, 2: partial peeling observed, 1: complete peeling observed. (*4) Gloss: Respective coating compositions of Examples and Comparative Examples were coated onto a test panel so as to be a dry film thickness of about 20 µm, followed by drying for 7 days under the conditions of 20°C and 65% RH to obtain a coating test panel respectively. Gloss on the surface of the coating film was visually evaluated as follows. 2: good, 1: hazy. Effect of the Invention The present invention provides a coating composition containing the organosilicate and/or its condensate and the boric acid compound in a specified amount respectively, and capable of forming a coating film developing low contamination properties from early time after coating, and showing good interlayer adhesion properties to the substrate. Particularly, the use of the coating composition containing an organic solvent based coating composition, an organosilicate and/or its condensate having a SP lower than that of the resin contained in the coating composition, and a boric acid compound in a specified amount makes it possible to orientate the organosilicate and/or its condensate toward the surface of the coating film and to promote hydrolysis thereof. Consequently, the coating composition of the present invention can form a coating film showing low contamination properties from early time after coating, and good interlayer adhesion properties to the substrate. Industrial Applicability The coating composition of the present invention is useful as an outdoor coating composition to be coated onto outdoor substrates such as building structures and the like.

Claims: A coating composition which is for use at room temperature to form a coating film showing hydrophilic properties, said composition containing (A) 0.1 to 50 parts by weight of an organosilicate represented by the general formula: where the R groups are the same or different and each represents a hydrogen atom or a monovalent hydrocarbon group having 1 to 7 carbon atoms, and/or a condensate thereof per 100 parts by weight of a resin solid content in the coating composition, and (B) 0.1 to 50 parts by weight of a boric acid compound per 100 parts by weight of a solid content of the component (A), said coating composition being selected from (1) a curable resin composition comprising (a) a base resin consisting of a hydroxyl group-containing resin dissolved or dispersed into an organic solvent, and (b) a crosslinking agent; and (2) an organic solvent based non-crosslinking coating composition capable of forming a coating film by volatilizing the organic solvent at room temperature and selected from a cellulose derivative based coating composition, acrylic resin based coating composition, urethane resin based coating composition, vinyl chloride resin based coating composition, fluorocarbon resin based coating composition, alkyd resin based coating composition, vinyl acetate resin based coating composition and styrene-butadiene resin based coating composition. A coating composition according to claim 1 which is of type (1), and wherein the resin is selected from fluorocarbon resin, acrylic resin, polyester resin and alkyd resin. A coating composition according to claim 1 or claim 2 wherein the organosilicate and/or its condensate (A) has a solubility parameter lower than that of the resin contained in the coating composition. A coating composition as claimed in claim 3 wherein the organosilicate and/or its condensate (A) is such that R of the general formula defined in claim 1 represents both ethyl group and methyl group. A coating composition as claimed in claim 4, wherein the organosilicate and/or its condensate (A) is modified by the reaction with a mercapto compound or a boric acid compound. A coating composition as claimed in claim 1 or 2 wherein the coating composition contains a condensation product between the organosilicate and/or its condensate (A) and the boric acid compound (B). A coating composition as claimed in any preceding claim wherein the boric acid compound (B) is trialkyl borate.

Inventors: HAMAMURA TOSHIHIRO, KASEI KAZUHIKO, KUTSUMA HIDEKAZU, NAKAI KAZUHISA, NOMURA MINEYUKI, HAMAMURA, TOSHIHIRO, KASEI, KAZUHIKO, KUTSUMA, HIDEKAZU, NAKAI, KAZUHISA, NOMURA, MINEYUKI, HAMAMURA, Toshihiro, Kansai Paint Co., Ltd, KASEI, Kazuhiko, Kansai Paint Co., Ltd, KUTSUMA, Hidekazu, Kansai Paint Co., Ltd, NAKAI, Kazuhisa, Kansai Paint Co., Ltd, NOMURA, Mineyuki, Kansai Paint Co., Ltd
Applicants: KANSAI PAINT CO LTD, KANSAI PAINT CO., LTD.
Application year: 2000
Main classification: C09D201
IPC codes: C09D183, C08K5, C08L83