Alkali metal-containing niobate-based piezoelectric material composition and a method for producing the same

Abstract: An alkali metal-containing niobate-based piezoelectric material composition comprises a solid solution represented by a composition formula (ANbO 3 ) (A: alkali metal), and at least one additive selected from Cu, Li and Ta. Preferably the solid solution comprises KNaNbO 3 or LiKNaNbTaO 3 and the additive is Cu to improve sintering.

Description: BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a niobate-based piezoelectric material composition and a method for producing the same; more specifically, the invention relates to an alkali metal-containing niobate-based piezoelectric material composition for use in the knocking sensor of automobile engine and the like. 2. Description of Related Art Piezoelectric materials have been used conventionally for the knocking sensor of an automobile engine. Piezoelectric materials are broadly divided as piezoelectric materials containing lead-based substances and piezoelectric materials not containing lead-based substance. These are selected and used, depending on the use. As known, lead is a hazardous substance. Hence, piezoelectric materials containing lead-based substances essentially contain the hazardous substances. Therefore, caution should be paid during the handling and use thereof. Thus, piezoelectric materials of excellent characteristic properties but with no content of hazardous substances such as lead-based substances are demanded. The piezoelectric materials with no content of lead-based substances are known, which are produced for example by adding various auxiliary components to niobate-based materials (ANbO 3 ); e.g., A: alkali metal, thereby elevating the sinterability of the materials to highly densify the materials and thereby raise the stability thereof over time. When the sinterability is enhanced in such a manner, the components and phases of the materials can be densified to final high densities. Hence, the resulting piezoelectric constants electromechanical coupling factors and mechanical quality factors thereof are relatively high. Additionally, piezoelectric materials are of great safety performance because of no content of hazardous substance, and with great piezoelectric properties and high stability. As auxiliary components to be added to such niobate-based materials, use is made of various materials. For example, Japanese Patent Laid-open No. Sho 50(1975)-47193 discloses a composition composed of a composition formula KNbO 3 -NaNbO 1 -LiNbo 2 with addition of manganese oxide; additionally, Japanese Patent Publication No. Sho 60 (1985) -52098 discloses a composition composed of a general formula Na 1-x Li x NbO 3 (0.02 ≤ x ≤ 0.30) with addition of aluminum oxide within a range of 0.02 to 2.0 % by weight and iron oxide within a range of 0.001 to 0.019 % by weight. These are both intended to promote the sinterability of a material and thereby highly raise the relative density, thereby improving the electromechanical coupling factor to recover a material with large mechanical strength. However, the niobate-based piezoelectric materials are so poor in terms of material sinterability and temperature properties including temperature stability at high temperature and stability over time, that the material properties are deteriorated, depending on the time elapsed in day, although the niobate-based piezoelectric materials have excellent properties at first. Thus, the niobate-based piezoelectric materials are prepared by molding above the re-crystallization temperature and pressing (by the hot press method). Compared with a so-called sintering method comprising molding a material at atmospheric pressure and then sintering the material, a sintered material at a high density can thereby be prepared at low temperature. However, the method is disadvantageous in that the production cost by the method is high and the method can never produce a larger sintered material. Thus, the material prepared by the hot press method has improved sinterability and is thus highly densified owing to the action of the auxiliary component therein. But the temperature stability and stability over time thereof are not satisfactory; and additionally, the production cost is disadvantageously high. Patent Abstracts of Japan, vol. 1995, no. 6, 31 July 1995 & JP 07 082024 discloses a piezoelectric ceramic composition of the general formula (Na x K 1-x )(Nb 1-y Ta y )O 3 , wherein 0.2 ≤ x ≤ 0.8 and 0.0 ≤ y ≤ 0.5. Li or Cu are not mentioned as possible components of the piezoelectric ceramic composition. Patent Abstracts of Japan, vol. 004, no. 087, 21 June 1980 & JP 55 055589 discloses a piezoelectric K x Na 1-x NbO 3 composition, wherein x is preferably 0.02 to 0.5. Furthermore, this document discloses that a Li compound may be added to the above composition to facilitate the sintering thereof, but does not disclose Cu as a possible component of the piezoelectric ceramic composition. Journal of the American Chemical Society, vol. 60, no. 1-2, January 1977, pages 15 to 17 discloses a pressure-sintered piezoelectric Li x Na 1-x NbO 3 composition, wherein 0.015 ≤ x ≤ 0.150. This document does not disclose K as a component of the piezoelectric composition. US 5,476,720 A discloses a K 1-y M y Ta 1-x Nb x O 3 solid solution composition, wherein M = Na + , Li + or Ag + and y = 0.02 to 0.20 and x = 0.05 to 0.95. Furthermore, this document discloses that said solid solution composition may be used as a piezoelectric sensor. However, this document is silent as regards the presence of three alkali metals or of Cu in the composition. The present invention has been made in view of the above circumstances and has an object to overcome the above problems and to provide an alkali metal-containing niobate-based piezoelectric material composition by which a substitutional solid solubilization agent so as to improve the temperature property and stability over time of niobate-piezoelectric materials not containing lead-based materials can be found. Another object of the present invention is to provide a niobate-based piezoelectric material composition which can be prepared by the existing sintering method at atmospheric pressure, as a preparation method thereof; and to provide a method for producing a niobate-based piezoelectric material composition which utilize the existing sintering method at atmospheric pressure. Additional objects and advantages of the invention will set forth in part in the description which follows and in part will be obvious from the description, or may be learned by practice of the invention. The objects and advantages of the invention may be realized and attained by means of the instrumentalities and combinations particularly pointed out in the appended claims. The above-mentioned objects are achieved by the alkali metal-containing niobate-based piezoelectric material compositions according to claims 1 and 3, and the methods for producing the same according to claims 6 and 10, respectively. Further developments of the present invention are set forth in the dependent claims. In one aspect of the present invention, a material with good properties can be obtained because Cu which is added as an additive acts as a sintering auxiliary agent for the solid solution so that the relative density can be improved. Furthermore, because Cu acts on the domain in the solid solution with an effect on the stabilization of the domain, the stability over time can be improved. Thus, a piezoelectric material with such a good property as described above can be provided. When the amount of Cu to be added then is below 0.001 mol %, Cu cannot function as a sintering auxiliary agent; while Cu is added above 5.0 mol %, the resulting properties are poor, disadvantageously. Thus, the optimum amount occupies 0.001 to 5.0 mol %. Furthermore, the reason why Li and Ta are optionally added is as following. Li acts as a sintering auxiliary agent because Li is sintered in the liquid phase during sintering; Ta acts on the ferroelectric domain in the solid solution to fix the ferroelectric domain and stabilize the dielectric loss. Through these actions, a piezoelectric material with great properties can be provided. As to the amount of Li then, an amount below 0.1 mol % or above 20 mol % is disadvantageous in that the resulting piezoelectric properties are deteriorated. Accordingly, the optimum amount occupies 0.1 to 20 mol %. According to the present invention, the action of the additive (e.g., an additive powder containing Cu) as a sintering auxiliary agent can highly densify the material. Still furthermore, the action of the additive (e.g., an additive powder containing Cu) for substitutional solid solubilization can prevent the reduction of dielectric loss, so that excellent piezoelectric properties with good stability over time can be recovered. Because the material cannot contain any lead-based material, a material with great safety and high piezoelectric performance can be produced. According to the present invention, the Li functions as a sintering auxiliary agent for promoting the high densification of the material and the Ta acts on the ferroelectric domain of a solid solution to reduce the dielectric loss and improve the dielectric constant, with the resultant recovery of a material with great stability over time and temperature stability. Because the resulting material does not contain any lead-based material either, the material can be used for a wide variety of use. Fig. 1 shows a graph depicting the relation between sintering temperature and density in Example 1; Fig. 2 shows a graph depicting the relation between dielectric constant and time elapsed in day in Example 1; Fig. 3 shows a graph depicting the relation between dielectric loss and time elapsed in day in Example 1; Fig. 4 shows a graph depicting the relation between dielectric constant and temperature in Example 1; Fig. 5 shows a graph depicting the relation between density and sintering temperature in Example 2; Fig. 6 shows a graph depicting the relation between dielectric constant and time elapsed in day in Example 2; Fig. 7 shows a graph depicting the relation between dielectric loss and time elapsed in day in Example 2; Fig. 8 shows a graph depicting the relation between dielectric constant and temperature in Example 2; Figs. 9(a), 9(b) and 9(c) show graphs depicting the changes of piezoelectric properties at various amounts of Ta and Li in the compositions of Li 4 (K 0.5 Na 0.5 ) 1-x (Nb 1-y Ta y )O 3 (wherein x = 0 to 0.20, y = 0 to 0.40); and Figs. 10(a), 10(b) and 10(c) show graphs depicting curie temperature, dielectric constant and dielectric loss at various amounts of Ta and Li as shown in Fig. 9. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS Examples of the present invention are described in detail with reference to drawings. The process of producing sample is first described in accordance with the present invention. As the sintering method for use in the production, any of sintering at . atmospheric pressure and sintering under pressure is satisfactory. As to the method for heating, all of the following heating methods are applicable: electric furnace heating; microwave heating; high frequency induction heating; infrared heating and the like. As to the state during sintering, sintering can satisfactorily be effected in oxygen flow and in air. In the present examples, therefore, the existing sintering method at atmospheric pressure for use in the production of ceramic material is adopted in oxygen flow (oxygen at 5 % to 100 %). Hereinbelow, the examples and the properties of the resulting produced samples are described on the basis of the measurement results of the samples. (Example 1) A sample of the invention (Sample No. 1: KNN-CuO) was prepared by adding CuO to a base sample composed of the composition formula K 1-x Na x NbO 3 (0 ≤ x ≤ 0.8). The starting raw materials, namely K 2 CO 3 , NaHCO 3 and Nb 2 O 3 , individually at a purity of 99 % or more and in powder, were blended together to a final composition formula of K 0.5 Na 0.5 NbO 3 , to prepare a substance weighed in total of 50 g. By using acetone, then, the blend was mixed together with a ball mill for 20 hours; the mixture powder was dried and subsequently calcined at 900 °C for five hours; the resulting product was cracked and graded through a sieve of #60 mesh, to prepare a powder in a crystal phase of K 0.5 Na 0.5 NbO 3 , To one mole of the crystal powder of R 0.5 Na 0.5 NbO 3 was added 0.01 mole of CuO, which was again mixed together with a ball mill, by using acetone for 20 hours; the resulting mixture was ground into a powder of an average particle size of 0.3 to 0.4 micron, by using a sieve of #60 mesh. To the resulting ground powder was added 2 wt % of polyvinyl butyral; and the resulting mixture was dried and graded with a #60-mesh sieve, to prepare a pressed substance of a 18-mm diameter and a thickness of about 2 mm by using a single screw press of 2 ton/cm 2 . Then, the temperature of the pressed substance was elevated at a temperature elevation rate of 5 °C/min in an oxygen flow of 0.3 l/min to 600 °C and was retained at the temperature for one hour; subsequently, the temperature of the pressed substance was heated at the same temperature elevation rate to 1050 °C and was then retained at the temperature for additional one hour. The temperature of the pressed substance was then cooled at 5 °C/min to ambient temperature (about 25 °C), to prepare a sintered substance. Subsequently, the sintered substance was ground, polished and processed to a final thickness of 1 mm and a diameter of 15 mm; and an Au electrode was coated and deposited on the upper and lower faces of the disk-like sample by the sputtering method, followed by application of an electric field of 3 kV/mm in silicone oil at 100 °C for 10 minutes for poling treatment, to give piezoelectricity to the substance. After the sample thus prepared was left to stand for one hour, various properties thereof were measured. At a stage when one hour passed after the poling of the sample No. 1 (KNN-CuO) thus prepared, the results of the measurement of the sample No. 1 are shown in Table 1. The results of the measurement at a stage when 28 days passed after the poling of the sample are shown in Table 2. For comparative examination of these results of the measurement of the sample, the results of the measurement of a base sample (KNN) with no addition of CuO are simultaneously shown below. The results of the measurement of KNN-CuO (one hour passed after the poling) A Sample of the invention A Comparative Sample Sample No. 1 Base sample Sample name KNN-CuO KNN A composition formula K 0.5 Na 0.5 NbO 3 + 0.01 mole of CuO K 0.5 Na 0.5 NbO 3 Measurement Item Relative density (%) 98.8 96.2 Piezoelectric properties Electromechanical coupling factors (kp) 0.389 0.334 Piezoelectric constant (d31 pm/V) 29.2 37.6 Piezoelectric constant (d33 pm/V) 96.2 115 Piezoelectric constant (g31 10 -3 Vm/N) 13.92 9.90 Piezoelectric constant (g33 10 -3 Vm/N) 46.1 30.3 Elastic properties Mechanical quality factor (Qm) 1408.2 100.6 Dielectric property Dielectric constant (E33t) 237 429 Dielectric loss ( tanδ ) 0.0045 0.0356 Phase transition temperature Curie point (°C) 415 415 Temperature coefficient Dielectric constant (%/-50 to 100 °C) 27 93 Resistivity (Ω·cm) 1.32E + 13 7.67E + 10 The results of the measurement of KNN-CuO (28 days passed after the poling) A Sample of the invention A Comparative Sample Sample No. 1 Base sample Sample name KNN-CuO KNN A composition formula K 0.5 Na 0.5 NbO 3 + 0.01 mole of CuO K 0.5 Na 0.5 NbO 3 Measurement Item Relative density (%) 98.8 96.2 Piezoelectric properties Electromechanical coupling factors (kp) 0.377 0.329 Piezoelectric constant (d31 pm/V) 27.8 38.6 Piezoelectric constant (d33 pm/V) 96.7 115 Piezoelectric constant (g31 10 -3 Vm/N) 13.59 9.30 Piezoelectric constant (g33 10 -3 Vm/N) 46.1 30.3 Elastic properties Mechanical quality factor (Qm) 1661.9 85.6 Dielectric property Dielectric constant (E33t) 231 470 Dielectric loss ( tanδ ) 0.0045 0.0890 Phase transition temperature Curie point (°C) 415 415 Temperature coefficient Dielectric constant (%/-50 to 100 °C) 27 93 Resistivity (Ω·cm) 1.32E + 13 7.67E + 10 In addition to relative density (%), the measurement items are electromechanical coupling factor (kp) during vibration along diameter direction, mechanical quality factor (Qm), electric voltage output piezoelectric factor (g31, g33), electric charge output piezoelectric factor (d31, d33), dielectric constant [ε33T/ε0 (in value at 1 kHZ)], and dielectric loss [tanδ (in value at 1 kHZ). For the measurement and examination of the samples, use was made of the resonance/anti-resonance method according to EMAS-6007 was used. Herein, the curie temperature (curie point) representing the phase transition temperature from ferroelectric phase to paraelectric phase was determined on the basis of the temperature where the dielectric constant was the highest. Additionally, the stability over time when left to stand at ambient temperature was measured by using dielectric constant and dielectric loss at 1 kHz; the resistivity was determined on the basis of the values of electric current and electric voltage as measured 30 minutes after the application of electric voltage by the bi-terminal I-V method. As shown in Table 1, the comparison of the results of the sample No. 1 (KNN-CuO) and the base sample (KNN) measured one hour after poling indicates that in the sample No. 1 as one inventive product, the relative density is increased and additionally, the electromechanical coupling factor (kp) and piezoelectric constant (g31, g33) as piezoelectric properties, and mechanical quality factor (Qm) as an elastic property are at far higher values. Furthermore, it is indicated that in the sample No. 1, the dielectric loss (tanδ) as a dielectric property is small, involving low values of the dielectric constant (%/-50 to 100 °C), and resistivity (Ω·cm) is large. As shown in Table 2, the measured results of the sample No. 1 (KNN-CuO) and the base sample (KNN) 28 days after poling are greatly improved in the same manner as shown in Table 1. Additionally, because the improved measurement results do not show any significant variation even 28 days after poling, it is confirmed that CuO exerts its action on various properties and also an action on the stability over time. Fig. 1 shows graphs depicting the relations between sintering temperature and density in the sample No. 1 (KNN-CuO) and the base sample (KNN). Fig. 1 shows that the sample No. 1 was highly densified over all the sintering temperatures and was at the highest density around a sintering temperature of about 1050 °C to about 1125 °C. This is because a liquid phase emerges around 1050 °C to 1125 °C owing to the melting point of CuO at 1025 °C; the flow of the liquid then embeds (or replaces) the space among the solid-phase crystal particles, thereby highly densifying the crystal and involving the increase of the density. This indicates that CuO acts as a sintering auxiliary agent to highly densify the sample. Fig. 2 shows graphs depicting the change of dielectric constant at a given temperature (ambient temperature of 25 °C) per a day interval over time. The graphs show that the dielectric constant of the sample No. 1 (KNN-CuO) was almost stable while the dielectric constant of the base sample (KNN) was gradually increased. As shown in Fig. 3, additionally, the dielectric loss of the sample No. 1 was likely to be stabilized, while the dielectric constant of the base sample was gradually increased over time. Furthermore, the sample No. 1 was at lower values of dielectric constant over the temperatures, as shown in Fig. 4. This is because CuO was substitutionally solid solubilized in the crystal in the sample and exerted an action in such a way that CuO pinned and fixed the ferroelectric domain in the crystal. Generally, it is known that the movement of such domain causes the increase of the dielectric loss. Thus, the fixing of the domain stabilizes the dielectric loss and simultaneously improves the mechanical quality factor (Qm). Additionally because the dielectric constant is reduced with no change of piezoelectric constant d, the piezoelectric constant g can be improved greatly. It is verified from this that a material with great sinterability and good stability over time can be prepared by the existing sintering method at atmospheric pressure. Although not shown in these figures, the amount of CuO added within a range of 0.00 1 mol % to 5.0 mol % improves the piezoelectric constant g and simultaneously improves the stability over time. within a range of 0.1 mol % to 2.0 mol %, in particular, CuO acts as a sintering auxiliary agent. Less than the amount thereof to be added, CuO does not work as a sintering auxiliary agent; more than the amount thereof to be added, the resulting piezoelectric properties are poor. Thus, the amount of copper oxide to be added is considered as appropriate at about 1 mol %. A sample (sample No. 2) prepared by adding Li and Ta to a base sample composed of a composition formula K 1-x Na x NbO 3 (0 ≤ x ≤ 0.8) is described below. (Example 2) For a sample (sample No. 2; KNN-LT) to be used in Example 2, use was made of LiCO 3 , K 2 CO 5 , NaHCO 3 , Nb 2 O 5 , and Ta 2 O 5 , individually at a purity of 99 % or more. These individual powders were blended together to a final composition formula of (Li 0.1 K 0.45 Na 0.45 ) (Nb, Ta)O 3 , to weight a composition of a total weight of 50 g. At the same production process as shown in Example 1, the sample No. 2 was prepared. The production process is already described in Example 1. Accordingly, the description of the production process is omitted herein. Subsequently, the sample No. 2 (KNN-LT) was measured at a stage when one hour passed after poling. The results are shown in Table 3. Table 4 shows the results of the measurement at a stage when 28 days passed after poling. Simultaneously, the measurement results of a base sample (KNN) with no addition of Li and Ta are individually shown additionally. For the measurement and examination of the samples, the resonance/anti-resonance method was used in the same manner as in Example 1. The curie temperature was determined as the temperature at the highest dielectric constant. The results of the measurement of KNN-LT (one hour passed after the poling) A Sample of the invention A Comparative Sample Sample No. 2 Base sample Sample name KNN-LT KNN A composition formula {(K 0.5 Na 0.5 ) 0.9 Li 0.1 } (Na 0.8 Ta 0.2 )O 3 K 0.5 Na 0.5 NbO 3 Measurement Item Relative density (%) 99.0 96.2 Piezoelectric properties Electromechanical coupling factors (kp) 0.307 0.334 Piezoelectric constant (d31 pm/V) 36.3 37.6 Piezoelectric constant (d33 pm/V) 104 115 Piezoelectric constant (g31 10 -3 Vm/N) 6.57 9.90 Piezoelectric constant (g33 10 -3 Vm/N) 11.9 30.3 Elastic properties Mechanical quality factor (Qm) 273.4 100.6 Dielectric property Dielectric constant (E33t) 624 429 Dielectric loss ( tanδ ) 0.0071 0.0356 Phase transition temperature Curie point (°C) 380 415 Phase transition temperature (Ortho → Tetra) NONE 210 Temperature coefficient Dielectric constant (%/-50 to 100 °C) 10 93 Resistivity (Ω·cm) 3.15E + 10 7.67E + 10 The results of the measurement of KNN-LT (28 days passed after the poling) A Sample of the invention A Comparative Sample Sample No. 2 Base sample Sample name KNN-LT KNN A composition formula {(K 0.5 Na 0.5 ) 0.9 Li 0.1 } (Na 0.8 Ta 0.2) O 3 K 0.5 Na 0.5 NbO 3 Measurement Item Relative density (%) 99.0 96.2 Piezoelectric properties Electromechanical coupling factors (kp) 0.290 0.329 Piezoelectric constant (d31 pm/V) 33.4 38.6 Piezoelectric constant (d33 pm/V) 104 115 Piezoelectric constant (g31 10 -3 Vm/N) 6.23 9.30 Piezoelectric constant (g33 10 -3 Vm/N) 11.6 30.3 Elastic properties Mechanical quality factor (Qm) 360.1 85.6 Dielectric property Dielectric constant (E33t) 606 470 Dielectric loss ( tanδ ) 0.0070 0.0890 Phase transition temperature Curie point (°C) 330 415 Phase transition temperature (Ortho → Tetra) NONE 210 Temperature coefficient Dielectric constant (%/-50 to 100 °C) 10 93 Resistivity (Ω·cm) 3.15E + 10 7.67E + 10 As shown in Table 3, the comparison of the measured results of the sample No. 2 (KNN-LT) and the base sample (KNN) one hour after poling indicates an improvement in the stability of dielectric constant(%/-50 to 100 °C) over temperature as well as large mechanical quality factor (Qm) including small dielectric loss (tanδ). As shown in Table 4, furthermore, the measured results 28 days after poling are not markedly different from the measured results shown in Table 3. Thus, it is verified that Li and Ta act on the temperature properties and also act on the stability over time. Fig. 5 shows graphs depicting the relation between density and sintering temperature in the sample No. 2 (KNN-LT) and the base sample (KNN). The figure indicates that the sample No. 2 is highly densified. This is due to the fact that while materials are generally sintered by solid-phase sintering, the component and phase of added Li oxide are liquefied as the sintering temperature is raised, so that a state emerges where the liquefied component is concurrently present with solidified components and phases of other materials with no occurrence of liquefaction, which is then subjected to sintering (liquid-phase sintering). In such a manner, the high densification of material can be accomplished. Fig. 6 shows graphs depicting the relation between dielectric constant and time elapsed in day at a given temperature (ambient temperature of 25 °C). As shown in the figure, the dielectric constant of the sample No. 2 is rather higher at an almost stable value even after days pass. It is confirmed that the stability of the sample No. 2 over time is good. Fig. 7 additionally shows graphs depicting the relation between dielectric loss and time elapsed in day at a given temperature (ambient temperature of 25 °C). The graphs show that the sample No. 2 (KNN-LT) retains a stable value despite the time elapsed in day. This is ascribed to the role of Ta such that Ta pins and fixes the ferroelectric domain in the crystal. As described above, the movement of the domain is caused by the increase of the dielectric loss. Thus, the dielectric loss can be reduced at a stable value due to the fixing of the ferroelectric domain. Fig. 8 shows graphs depicting the relations between dielectric constant and temperature in the sample No. 2 (KNN-LT) and the base sample (KNN). As shown in the figure, it is confirmed that no intermediate transfer phase transition (around 210 °C) is present in the sample No. 2 and that an almost stable dielectric constant can be recovered. This is ascribed to the fact that the crystal phase changes from orthorhombic crystal to tetragonal crystal at room temperature due to the addition of Li at 10 mol %. It is considered that the intermediate phase transition is thus lost, whereby the temperature properties are stabilized. As not shown in the figure, the Li to be added at an amount within a range of 0.1 mol % to 20 mol % acts as a sintering auxiliary agent to highly densify the material; above 20 mol %, LiNbo 3 is generated so that a mixture phase emerges, which deteriorates the piezoelectric properties. Figs. 9 and 10 show graphs depicting the piezoelectric properties at the compositions of Li x (K 0.5 Na 0.5 ) 1-x (Nb 1-y Ta y )O 3 , wherein x = 0.002, 0.06, 0.08, 0.10, 0.15, 0.20; y = 0, 0.10, 0.20, 0.30, 0.40 [Fig. 9(a), electromechanical coupling factor; Fig. 9(b), piezoelectric constant (d31); Fig. 9c, piezoelectric constant (g31)] and dielectric properties [Fig. 10(a), curie temperature; Fig. 10(b), dielectric constant; Fig. 10(c), dielectric loss]. It is confirmed that the electric coupling factors are at larger values above 10 mol % of Ta (wherein 0 to 6 mol % of Li) added in amount than the base sample (KNN), as shown in Fig. 10(a) ; the piezoelectric constant (d31) shown in Fig. 9(b) is at the highest value at about 20 mol % of Ta (at 4 mol % of Li) added in amount; additionally, the piezoelectric constant (g31) shown in Fig. 9(c) are larger values at 10 mol % and 20 mol % of Ta (at 0 mol % of Li) than the base sample (KNN). . As shown in Fig. 10(a), furthermore, it is confirmed that the curie temperature is the highest at 0 mol % of Ta (at 20 mol % of Li) added in amount; and then, the increase of the amount of Ta added involves a tendency of the decrease; as shown in Fig. 10(b), further, the dielectric constant gradually decreases as the amount of Ta added increases at 10 mol % of Li; the dielectric loss shown in Fig. 10(c) is at the highest value, at 0 mol % of Ta (at 20 mol % of Li) added in amount, while the dielectric loss is at almost stable and low values, at 10 mol % to 40 mol % of Ta added in amount. In such a fashion, the results of the measurement at 0 mol % to 40 mol % of Ta added in amount are shown; it is herein confirmed that above 40 mol % of Ta added in amount, the curie temperature is below 300 °C, which indicates that the temperature properties are deteriorated. These results suggest that as to the amount of Ta added, about 20 mol % (at 10 mol % of Li) acts most highly on the temperature stability. The present invention is never limited to the aforementioned examples. Various modifications are possible within the scope of the present invention as claimed. For example, a material composed of a composition formula (K x Na x )NbO 3 is used as an alkali metal-based material in the above examples, but other materials can be used and additives therefor can be modified. In such a manner, a material with good sinterability and stability over time, and high temperature stability, can be produced. The foregoing description of the preferred embodiments of the invention has been presented for purposes of illustration and description. It is not intended to be exhaustive or to limit the invention to the precise form disclosed, and modifications and variations are possible in the light of the above teachings or may be acquired from practice of the invention. The embodiments chosen and described in order to explain the principles of the invention and its practical application to enable one skilled in the art to utilize the invention in various embodiments and with various modifications as are suited to the particular use contemplated. It is intended that the scope of the invention be defined by the claims appended hereto, and their equivalents.

Claims: An alkali metal-containing niobate-based piezoelectric material composition comprising: a solid solution represented by a composition formula K 1-x Na x NbO 3 wherein 0 < x ≤ 0.8; Cu as an additive, and optionally at least one further additive selected from Li and Ta. The composition according to claim 1, wherein Cu is present in an amount of 0.001 to 5 mol%. An alkali metal-containing niobate-based piezoelectric material composition represented by a composition formula Li x (K 1-y Na y ) 1-x (Nb 1-z Ta z )O 3 wherein 0.001 ≤ x ≤ 0.2, 0 < y ≤ 0.8, 0 < z ≤ 0.4. The composition according to claim 3, wherein Cu is further contained as an additive. The composition according to claim 4, wherein Cu is present in an amount of 0.001 to 5 mol%. A method for producing an alkali metal-containing niobate-based piezoelectric material composition, comprising: adding an additive powder containing Cu and optionally at least one element selected from Li and Ta to a mixture powder represented by a composition formula K 1-x Na x NbO 3 wherein 0 < x ≤ 0.8, then blending these powders together; molding the resulting blended powder and sintering the same; and giving piezoelectricity to the resulting sintered substance in a polarization treatment process. The method according to claim 6, wherein said sintering process is an atmospheric pressure sintering method or a mechanically press sintering method. The method according to claim 7, wherein said sintering process is carried out with a heating method selected from the group consisting of electric furnace heating, microwave heating, high frequency induction heating, and infrared heating. The method according to any one of claims 6 to 8, wherein said additive powder is 0.001 to 5 mol% of Cu. A method for producing an alkali metal-containing niobate-based piezoelectric material composition, comprising: blending a mixture powder represented by a composition formula Li x (K 1-y Na y ) 1-x (Nb 1-z Ta z )O 3 wherein 0.001 ≤ x ≤ 0.2, 0 < y ≤ 0.8, 0 < z ≤ 0.4; molding the resulting blended powder and sintering the same; and giving piezoelectricity to the resulting sintered substance in a polarization treatment process. The method according to claim 10, wherein an additive powder containing Cu in an amount of 0.001 to 5 mol% is further added to said mixture powder.

Inventors: SAITO YASUYOSHI, SAITO, YASUYOSHI, Saito, Yasuyoshi, c/o 41-1, Aza Yokomichi
Applicants: TOYOTA CHUO KENKYUSHO KK, KABUSHIKI KAISHA TOYOTA CHUO KENKYUSHO
Application year: 2000
Main classification: H01L41
IPC codes: H01L41, C04B35