Method for producing microbial polyester

Abstract: A method for producing a microbial polyester by culturing a microorganism being capable of producing a poly hydroxyalkanoate polyester in a culture medium containing 1-hexene as a sole carbon source.

Description: BACKGROUND OF THE INVENTION Field of the Invention The present invention relates to a production method of a polyester by using a microorganism. Related Background Art Microbial polyesters represented by poly 3-hydroxybutyrate (PHB) have a remarkable feature that they are biologically degradable, differing from the synthetic polymers made from petroleum. Synthetic polymers have been used as plastics etc. for a long time. On disposal, however, this feature of hard-to-decompose makes them accumulated in waste-disposal facilities, or when they are burned, harmful substances such as dioxin and endocrine-disruptors are generated to cause environmental pollution On the other hand, polyesters produced by microorganisms (hereinafter referred to as "microbial polyesters") can be biologically degraded to be incorporated in a natural recycling system, usable as environment-maintaining plastics. They also have a potential as soft materials for medical use (Japanese Patent Application Laid-Open No. 5-159). Heretofore, various bacteria have been reported to produce and accumulate PHB or copolymers of other hydroxyalkanoic acids in the cells (Handbook of Biodegradable Plastics, ed. by Biodegradable Plastics Society, published by N.T.S., p. 178-197 (1995)). Recently, for industrial use of such poly hydroxyalkanoic acids (PHA), various attempts have been done to make the microorganisms produce modified PHA comprised of unusual monomer units for broader physicochemical properties. One of these attempts, Japanese Patent Application Laid-Open No. 5-30980, discloses that Pseudomonas fluorescence FA-031 (FERM P-3433) can produce copolymers of poly hydroxyfatty acid esters made of monomer units of C4 to C16, when the cells are cultured using oleic acid, triolein (olive oil) or triglyceride as a carbon source under nitrogen starvation. The presence of carbon-carbon double bonds were confirmed in C14 and C16 units. Further, it discloses that when linoleic acid is used as a substrate, the produced polyester is comprised of units of C4 to C16, the presence of double bond was confirmed in units of C10, C12, C14, and C16, and when α-linolenic acid is used as a substrate, the produced polyester is comprised of units of C4 to C16, the presence of double bonds were confirmed in units of C8, C10, C12, C14, and C16. A method to produce PHA containing units of 3-hydroxyoctenoic acid and 3-hydroxyhexenoic acid is disclosed in Int. J. Biol. Macromol. Vol,12 p. 85-91 (1989), where Pseudomonas oleovorans ATCC 29347 is grown using 3-hydroxy-6-octenoic acid or 3-hydroxy-7-octenoic acid as a substrate. A method to produce PHA containing units of 3-hydroxydecenoic acid and 3-hydroxytetradecenoic acid is disclosed in Appl. Environ. Microbiol. (1992) Vol. 58(2) p. 536-544, where Pseudomonas putida KT2442 is grown using glucose, fructose and glycerol as substrates. A method to produce PHA containing units of 3-hydroxyoctenoic acid and 3-hydroxyhexenoic acid is disclosed in Polymer, Vol 35(10) (1994) p. 2090-2097, where Pseudomonas oleovorans ATCC 29347 is grown using n-octane and 1-octene as substrates. A method to produce PHA containing units of 3-hydroxydecenoic acid and 3-hydroxytetradecenoic acid is disclosed in Int. J. Biol. Macromol. 23 (1994) p. 61-72 where Pseudomonas resinovorans NRRL B-2649 is grown using tallow as a substrate. Although various methods have been studied to produce PHA having carbon-carbon double bonds in their side chains using microorganisms as described above, the inventors have come to think that more variety of the culture conditions and substrates are required for practical use. At present, studies on the use of organic substrate materials derived from relatively inexpensive minerals such as petroleum are not at least sufficient. EP 0 274 151 A2 discloses a process for producing polyester biopolymers by culturing Pseudomonas oleovorans bacteria on substrates comprising certain nutrients. The nature of the polyesters can be varied by varying the nature of the carbon source used. In this way polyesters with unsaturated double bonds can be produced. SUMMARY OF THE INVENTION According to the present invention, there is provided a method for producing microbial polyester according to claim 1. Preferred embodiments are subject of the dependent claims. BRIEF DESCRIPTION OF THE DRAWINGS FIG.1 is an 1 H-NMR chart of PHA. FIG.2 is a 13 C-NMR chart of PHA. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS The present invention provides a method for producing a PHA containing a monomer unit having a carbon-carbon double bond in the side chain, by growing a microorganism in a medium containing 1-hexene as a sole carbon source. Preferably, the microorganism is a bacterium of genus Pseudomonas , more preferably, Pseudomonas cichorii YN2 (FERM BP-7375). Taxonomical characteristics of Pseudomonas cichorii YN2 are as follows: Growth temperature: 30°C Morphology: rod (0.8 × 1.5 to 2.0 µm) Gram staining: gram-negative Spore formation: negative Motility: positive Colony morphology: circular, entire, convex, smooth, glossy, translucent Catalase: positive Oxidase: positive O/F test: non-fermentive Nitric acid reduction: negative Indole production: positive Glucose acidification: negative Arginine dehydrolase: negative Urease: negative Esculin hydrolysis (β-glucosidase): negative Gelatin hydrolysis (protease): negative β-galactosidase: negative Assimilation of compounds: glucose: positive L-arabinose: positive D-mannose: negative D-mannitol: negative N-acetyl-D-glucosamine: negative maltose: negative potassium gluconate: positive n-capric acid: positive adipic acid: negative dl-malic acid: positive sodium citrate: positive phenyl acetate: positive Production of fluorescent pigment on King's B agar: positive Growth in 4% NaCl: positive (weak) Accumulation of poly-p-hydroxybutyrate: negative* Tween 80 degradation: positive (* by staining of colonies on the nutrient agar with Sudan Black) With the above characteristics, the bacterium was determined to be a strain of Pseudomonas cichorii according to Bergey's Manual of Determinative Bacteriology, 9th Edition. Further, the PHA production behavior of this strain indicates this being a novel strain, so that it has been deposited in National Institute of Bioscience and Human Technology, Agency of Industrial Science and Technology, as FERM BP-7375. The culture medium used in the present invention may be any mineral salts medium containing phosphate and a nitrogen source such as ammonium salt or nitrate. By controlling the nitrogen concentration can be enhanced the PHA productivity. 1-hexene to be added in the culture medium is volatile, and poorly soluble in water, so that the culture vessel must be tightly closed after securing the required oxygen. An example of the mineral salt medium composition is shown below. M9 medium Na 2 HPO 4 6.3 g/l KH 2 PO 4 3.0 g/l NaCl 0.5 g/l NH 4 Cl 1.0 g/l pH 7.0 1/10 M9 medium Na 2 HPO 4 6.3 g/l KH 2 PO 4 3.0 g/l NaCl 0.5 g/l NH 4 Cl 0.1 g/l pH 7.0 For better growth and PHA production, the following trace element solution must be added to the above inorganic salt medium to 0.3% (v/v). Trace element solution (g/L) nitrilotriacetic acid 1.5 MgSO 4 3.0 MnSO 4 0.5 NaCl 1.0 FeSO 4 0.1 CaCl 2 0.1 ZnSO 4 0.1 CuSO 4 0.1 AlK(SO 4 ) 2 0.1 H 3 BO 3 0.1 Na 2 MoO 4 0.1 NiCl 2 0.1 The culture temperature may be any temperature so long as the above strain can grow well, e.g., 15 to 40°C, preferably about 20 to 30°C. Any culture method can be used in the present invention so long as the above strain can grow and produce PHA, for example, such as liquid culture, solid culture, batch culture, fedbatch culture, semi-continuous culture, and continuous culture. As for PHA recovery from the cells in the present invention, ordinary chloroform extraction is most convenient. However, where the organic solvent is difficult to use, PHA can be recovered by removing the cell components other than PHA by treating with surfactants such as SDS, enzymes such as lysozyme, agents such as EDTA, sodium hypochlorite and ammonia. Now the present invention will be described with reference to the following Example, however it is our intention that the scope of the invention be not limited by any of the details of the description. EXAMPLE PHA Production by Culturing Strain YN2 with 1-Hexene Carbon Source Strain YN2 was grown on an M9 agar medium containing 0.1% yeast extract, and a colony was taken and suspended in a sterilized physiological saline to prepare a cell suspension of OD 600 1.0. The suspension was spread on 20 plates of 1/10N-M9 agar not containing a carbon source, and the plates were incubated at 30°C under 1-hexene atmosphere. After 4 days incubation, cells were collected, washed with methanol, and the collected cells by centrifugation was dried under a reduced pressure. The dry weight of the cells was 150 mg. To the dried cells, 50 ml of chloroform was added and stirred at 50°C for 24 hrs to extract PHA. The chloroform layer was filtrated, concentrated by an evaporator. Cold methanol was added to remove the precipitate, which was then dried under a reduced pressure. Thus, 68 mg of dried PHA was obtained. The PHA weighed to about 45% of the dried cell weight. The composition of the obtained polymer was determined as follows: 10 mg of the polymer was put into a 25 ml egg-plant type flask and dissolved by adding 2 ml chloroform, to which 2 ml of a methanol solution containing 3% sulfuric acid was added, and reacted at 100°C under reflux for 3.5 hrs. After the completion of the reaction, 2 ml water was added to the flask, and the flask was shaken vigorously for 10 min, and left stand for phase separation. The lower chloroform layer was removed and dried over magnesium sulfate. This was then subjected to gas-mass chromatography to identify each methyl hydroxyalkanoate peak by using a gas chromatograph-mass spectrograph (GC-MS; Shimadzu QP-5050, DB-WAX capillary column (J&W). The result is shown in Table 1. Unit C4 C6 C6: C8 C8: C10 C12 C12' C14 C14: Area % 0.5 27.2 8.0 11.9 0.5 25.7 10.3 10.9 2.5 0.6 In Table 1, each value represents the peak area (%) in the GC-MS TIC chromatogram. C4 :3-hydroxybutyric acid C6 :3-hydroxyhexanoic acid C6: :3-hydroxyhexenoic acid C8 :3-hydroxyoctanoic acid C8: :3-hydroxyoctenoic acid C10 :3-hydroxydecanoic acid C11 :3-hydroxyundecanoic acid C12':3-HA unit having a double bond or a branch, not identified C14 :3-hydroxytetradecanoic acid C14: :presumably 3-hydroxytetradecenoic acid, not identified The obtained polymer was further analyzed by NMR (FT-NMR:Bruker DPX400, subject nuclides: 1 H, 13 C, solvent:D-chloroform with TMS). FIGS. 1 and 2 show the 1 H-NMR and 13 C-NMR charts. Table 2 shows the peak assignment in 1 H-NMR. resonant frequency :400MHz δ (ppm) Assignment 0.88 m; 2H, f 1.27 m; 4H, e 1.58 m; 2H, d 2.03 m; 0.3H, g 2.37 m; 0.7H, j 2.60 m; 1.6H, a 5.09 s; α 5.13 d; β 5.18 m; b 5.28 m; i 5.52 m; 0.068H, h 5.73 m; 0.143H, y m:multiplet, d:doublet, s:singlet As shown above, PHA containing at least 3-hydroxyhexenoic acid units and 3-hydroxyoctenoic acid units is synthesized in Pseudomonas cichorii YN2 (FERM BP-7375) by culturing the strain in the presence of 1-hexene.

Claims: A method for producing a microbial polyester comprising a step of culturing a microorganism in a culture medium containing 1-hexene as a sole carbon source, wherein the microorganism is Pseudomonas cichorii YN2 (FERM BP7375) being capable of producing a polyhydroxyalkanoate. The method according claim 1, wherein the microbial polyester comprises at least one monomer unit of hydroxyfatty acid having a carbon-carbon double bond. The method according to claim 2, wherein the hydroxyfatty acid unit is selected from the group consisting of 3-hydroxyhexenoic acid and 3-hydroxyoctenoic acid.

Inventors: HONMA TSUTOMU, IMAMURA TAKESHI, KOBAYASHI SHIN, SUDA SAKAE, YANO TETSUYA, HONMA, TSUTOMU, IMAMURA, TAKESHI, KOBAYASHI, SHIN, SUDA, SAKAE, YANO, TETSUYA
Applicants: CANON KK, CANON KABUSHIKI KAISHA
Application year: 2000
Main classification: C12P7
IPC codes: C08G63, C12P7, C08L101, C12R1