Method for the preparation of granular ammonium sulphate

Abstract: A new method for the preparation of granular ammonium sulphate that is free-flowing and does not clump, with a minimum title of 20.5% and a granular composition and hardness similar to common granular fertilisers. The method is characterised by the combined use of the classic reaction tank and the tubular reactor (without excluding the use of either element alone). It uses sulphuric acid, liquid or gaseous ammonia and the water from the washing of the tail gases from the reaction. The liquor produced in the reaction tank and in the tubular reactor is of temperature, pressure, humidity, concentration and pH such that upon entering the granulator it is transformed into granules of the desired size and hardness. The proper feeding distribution of raw materials and water at both stages of production is an important factor in the success of the method. The method is used for the rapid production, with minimal impact on the environment, of a fertiliser with good quality characteristics.

Description: The invention relates to a method for the production of ammonium sulphate and to the resulting product, which is granular, free-flowing and non-agglomerating. Briefly the method is using as equipment a classic reaction tank followed by a tubular reactor, while the raw materials are being fed in both apparatus. The product produced by this method has a minimum title of 20.5% by weight, and a granular composition and hardness similar to that of ordinary fertilisers. Ammonium sulphate has many applications, the most important being in the manufacture of fertiliser, for which it is a source of nitrogen (ammonium) and sulphur. Crystalline ammonium sulphate can be prepared in many ways, both as a by-product and as the primary product of the reaction between sulphuric acid and ammonia. It is very frequently used in blends with other types of fertilisers. Crystalline ammonium sulphate, however, has a number of major drawbacks, including the fact that its grains are small in size and irregular in shape, do not flow easily, have a tendency to agglomerate and are lacking in hardness. This makes it difficult to use as a fertiliser, given that fertilisers require uniformity of dispersion and specific grain properties (shape - dimensions). A comprehensive review of the methods of ammonium sulphate production and allusions for its granulation and uses are presented in the "Ullmann's encyclopedia of industrial chemistry,(4 th Edition, volume 7, pages 521-5), published by VCH-Verlag, Germany (1974)". In this publication, the main way for producing ammonium sulphate is to receive it necessarily as a by-product, or by neutralising either ammonia gas or sulphuric acid. The crystals of the salt are obtained through a crystallizer. However the (through granulation) obtained particles appear to have a size between 0.5 and 2mm, which isn't the today desired granulometry. Also the described method needs a pH-value of about 3 in order to obtain the above mentioned granulometry, which forces the producer either to select special equipment material or to accept high rates of corrosion. Numerous attempts have been made to reduce these defects by improving the crystallisation process. One such way is the use of a reverse-flow crystallisation process, in which the small crystals that are formed at low temperatures are mixed with a hot solution of ammonium sulphate or acidic ammonium sulphate. While there is an improvement in the crystalline ammonium sulphate thus produced, the production cost is high and, in addition, the grains are irregular in shape and dimensions, making them difficult to use as fertiliser. Further improvements in the product were achieved with the use of granulation techniques, yielding a granular product, enhanced in certain cases with the use of additives, such as a variety of metallic ions, phosphoric acid, phosphorites, urea, ammonium nitrate and other compounds. While these techniques have brought about further improvements, existing methods nonetheless still produce a granular product of little hardness and with a substantial percentage of grains outside the desired size range (2-4.5 mm). A different point of view is shown in the patent GB 2116159A (TOYO ENGINEERING CORP.- MITSUI TOATSU CHEMICALS) from 28.9.1983, which describes the manufacture of NPK fertilisers through the use of a tubular reactor followed by a reaction tank (just the opposite combination as our method) and a fluidised bed granulator. The outcoming slurry has a temperature of 80-130°C and a liquid content of 40-90% by volume.However this method -as described- has been tested only for low production rates. From the technical standpoint, all granular ammonium sulphate production methods present problems of corrosion of the material of the installations used, because of the low pH of the liquor produced during the reaction. Furthermore, none of the occasional improvements that have been achieved have brought about any substantial increase in production rates. This invention eliminates the above drawbacks and creates a series of advantages, which are analysed below. The main feature of this invention is the combination in series of a agitated cylindrical reaction tank followed by a tubular reactor, and the primary gain is the increase in production rate in comparison with the use of just one of the above machines. In addition, the extensive use of recycled water, either from the stripping of tail gases or from other factory units, allows the liquor produced in the reactor to be kept at a fairly low density, moderating the quantities of ammonia channelled into the tail gas stripping system, while finally, given the relatively high (compared to other methods) pH of the liquor, there is no corrosion of the reaction tank. As we have said, the production of granular ammonium sulphate is carried out in two successive stages, which are shown in diagrams N°1 and N°2, attached. In the first stage, ammonia (liquid or gas), sulphuric acid of at least 70% concentration by weight and recycled water from the stripping of tail gases are fed into a reaction tank fitted with co-axial agitators. Alternatively, two agitation tanks in series may be used. The reaction temperature is 100-120°C, with a usual value of 108-115°C, and the pressure is normal atmospheric pressure. The water added is acidic because of the presence of acidic ammonium sulphate. The reaction tank is made of steel with an acid-resistant lining. The liquor produced has a moisture level of 34-42%, a density of 1260-1430 g/l with a usual value of 1290-1370 g/l, and a pH of 2.5 - 6 with a usual value of 3- 5. From the overflow of the tank, the liquor produced flows into an agitated intermediate vessel, to which may be added liquid effluents from other parts of the plant. From the intermediate vessel, the liquor produced in the first stage is first mixed with the rest of the sulphuric acid of the reaction and then pumped into the tubular reactor. To the tubular reactor are also added water and ammonia, in either liquid or gaseous form. The pressure is 3-6 bar, usually 3.5-5 bar, and the temperature is over 130°C. The liquor that is projected from the tubular reactor into the rotating granulator has a moisture level of 5-12% after expansion. To the granulator is also added a small quantity of ammonia (liquid or gas) to complete the reaction. The pH of the product in the granulator, measured in a 1% solution by weight, is 3-5, with a usual value of 3.2-4.5, and the moisture level is 2-4.5%. The tail gases from the reaction tank and the granulator are conducted into 2 stripping columns, where the ammonia is neutralised and absorbed by recycled water and sulphuric acid. The acidic ammonium sulphate solution produced is fed into the reaction tank and the tubular reactor instead of plain recycled water. In both stages of preparation the proper feeding of raw materials and water is very important. This must be done as follows: Sulphuric acid : Discounting the acid from the stripping process, the remainder is fed into the reaction tank and the tubular reactor at a desired proportion of 45-55% respectively. In total 31-45% may be fed into the tank, 42-52% into the tubular reactor and 10-20% into the vessels where, mixed with recycled water, it is fed into the stripping columns to capture the ammonia. Ammonia : The ammonia is fed in equal quantities into the reaction tank and the tubular reactor. Specifically, 37-55% of the total ammonia is consumed in the reaction tank, 42-52% in the tubular reactor and 3-11% in the granulator. Acidic solution from stripping columns : As we have already mentioned, recycled water is fed into the vessels, where it is mixed with part of the sulphuric acid and then used to strip the tail gases. Of the resulting solution 5-11% is fed into the tubular reactor and the rest into the reaction tank. After granulation the product undergoes a series of processes to give it its final form; these are as follows : Drying in a rotary oven with a concurrent flow of exhaust gases from the combustion of natural gas (or diesel oil). The temperature of the exhaust gas at the entrance to the drying oven is 440-480°C, and may rise to 500°C, while the fertiliser exits at 95-110°C, with a usual value of 98-105°C. Sieving, in two stages, when the fine grains are returned to the granulator and the coarse ones sent for crushing, while the marketable grains (2-4.5 mm) move on to the cooling stage. Crushing of coarse grains, which are then returned to the granulator Cooling, with (cold) atmospheric air in a solid-fluid bed to a final temperature of 10-45°C (depending on climate conditions), and simultaneous dust removal. Coating with some suitable material, to keep the grains from agglomerating; this is done in a rotating drum called a coater. The final product produced by the above method has the following chemical properties: Nitrogen content : minimum 20.5% by weight, entirely in ammoniac form, using the method of analysis described in directive 77/535/EEC, Method 2.1. Sulphur content : minimum 23% by weight, using the method of analysis described in directive 89/519/EEC, Method 8.4, 8.9. Free moisture : maximum 0.3% by weight, measured by the ISO 8189 method. pH : between 3.2 and 4.5 , measured in an aqueous solution 1% by weight. Similarly, the physical properties of the final product produced by the above method are as follows : Form : granular, free-flowing, non-agglomerating Granulometry : 90% by weight minimum between 2 and 4.5 mm, and : specifically > 4.5 mm 0.3% by weight maximum 4.5 mm - 4 mm 1-3% by weight 4 mm - 2 mm 87-95% by weight < 2 mm 5-9% by weight according to the Pr EN 1236 method (ISO 8397 modified) Hardness : Average value : 3 kg minimum, and usually more than 4 kg Maximum value : 5 kg at least, and usually more than 5.5 kg Minimum value : 2 kg at least, and usually more than 3 kg determined on a sample of at least 10 grains with a diameter of between 3.15 and 4 mm by measurement of the necessary applied weight to crush each grain. SGN (size guide number): 200-300 as determined by the formula: SGN = d 50 x 100, where d 50 is the diameter of 50% of the grains according to the cumulative distribution of the granulometric analysis. UI (uniformity index): 50-55 as determined by the formula: UI = (d 5 / d 90 ) x 100, where d 5 , d 90 are the diameters of 5% and 90% of the grains respectively, according to the cumulative distribution of the granulometric analysis. Tendency to agglomerate : 0.3 kg at most (usually 0 kg) determined by an original method which measures the applied weight necessary to crush a sample of 30 grams of product that has been centrifuged at 4500 rpm for 4 hours and then left to rest for another 4 hours. The method is repeated once, and the final value is the average of the two results. The advantages of this invention are many and varied. The direct and obvious advantage lies in the properties of the product itself, which has grains of uniform size (as demonstrated by the granulometric analysis, the SGN and the UI) and appropriate hardness (as demonstrated by the hardness index) that do not agglomerate. There are in addition, however, a number of secondary advantages, relating to the production process. These are : 1. Full use of recycled water. Since the method requires large quantities of water to produce a reaction liquor of the desired low density, this permits the recycling of various liquid effluents not only from the production unit itself but from other parts of the plant and even from other factories. This has a twofold significance, since on the one hand it reduces the quantity of liquid effluents released into the final liquid receptor and on the other it reduces ammonia losses into the atmosphere. 2. Minimalisation of the corrosion of the reaction tank. The consequence of the low density of the liquor in the reaction tank and the capturing of gaseous ammonia in the stripping process, which is then returned to the reaction tank, is a higher pH than in other methods. This not only results in less chemical corrosion but at the same time prevents mechanical erosion, on the one hand because the higher pH prevents crystallisation and on the other because of the fact that the liquor is thinner than in traditional methods. 3. Use of smaller granulator. Since most of the gases created are captured by the reaction tank, the volume of gas in the granulator is less than in traditional methods. Thus in a new unit applying this process the granulator could be significantly smaller than in a traditional unit of the same capacity. 4. Increased production in existing units, as a consequence of advantage number 3. In the unit of our company the production rate using this method rose from 35 t/h to 65 t/h, for a period of 72 hours of continuous operation. This rate of production may be expected for a single production line and for a total consumption of electricity of 30-40 kWh/t of product or 1800-2200 kWh/hour of operation. The two figures below show in sequence the simplified flow chart of a compound fertiliser production unit that applies the method described above for the production of granular ammonium sulphate. Figure N°1 shows the standard reaction tank (1), the intermediate vessel (2), the granulator (3), the tubular reactor (4), the gas stripping system (5) and the water reservoirs (6). Figure N°2 shows the drying oven (7), the sieves (8), the crushers (9), the final sieve (10), the gas-stripping, drying and cooling system (11), the cooler (12) and the coater (13). The diagrams do not show various machines for the propulsion of solids, liquids and gases, which are not characteristic of the production installation for this product, while the arrangement of the machines as given on the diagrams is not binding and may differ in a real installation. Finally, these diagrams may in no sense be considered working drawings for the forms of the machines in question. Presented below are three examples of the application of this invention, which however must be taken as merely indicative and not be considered as defining the precise limits of the present invention. 1 st EXAMPLE a) Production rate : 40-60 t/h b)Operational conditions : Sulfuric acid concentration : 96,4% b.w. N° of sample Reaction temperature (°C) Liquor density (g/l) Liquor pH Tubular reactor pressure Tub. reactor temperature (°C) Granulator pH (1%b.w) Fuel gases temper. (dryer inlet)(°C) Fuel gases temper. (dryer outlet)(°C) Product tem. (cooler outlet) (°C) 1 105,9 1313 2,7 4,1 153 4,0 460 108 2 112,4 1322 2,8 3,7 150 3,8 480 102 3 112,2 1333 3,7 4,4 154 4,0 444 102 18 4 113,3 1317 2,7 4,7 157 4,1 452 108 5 113,3 1314 2,6 4,8 158 4,0 452 109 6 112,9 1306 3,5 4,9 159 3,9 450 109 7 110,8 1313 5,6 4,4 155 4,0 455 109 22 8 110,5 1315 4,6 4,3 154 3,8 443 109 9 111,1 1314 2,6 4,4 154 3,9 499 107 20 10 112,6 1303 3,8 4,6 156 4,2 472 105 11 111,6 1310 4,9 4,5 156 4,5 482 102 c) Feeding proportions (%) Sulfuric acid Ammonia Water N° of sample Reaction tank Tubular reactor stripping columns Reaction tank Tubular reactor Granulator Reaction tank Tubular reactor 1 35 47 18 40 50 10 92 8 2 36 47 17 39 49 12 94 6 3 36 46 18 42 50 8 91 9 4 37 48 15 44 51 5 91 9 5 36 49 15 43 50 7 92 8 6 37 49 14 44 50 6 91 9 7 36 49 15 42 50 8 94 6 8 37 48 15 41 52 7 91 9 9 35 48 17 41 50 9 91 9 10 36 50 14 43 51 6 90 10 11 37 49 14 43 51 6 91 9 d) Chemical - physical properties of product N° of sample Nitrogen cont.(%b.w.) Sulfur cont(%b.w.) Free molst. (%b.w.) pH 1%b.w . Granulom. (%b.w.)*1 Hardness (%b.w.)*2 SGN UI Tendency to agglomerate (kg) 1 20,55 0,12 2 20,55 0,12 4,1 0,3-1,4-90,7-7,6 4-5,7-3 282 50 0 3 20,56 23,27 0,16 4 20,53 0,12 3,8 0,5-2,9-89,6-7,0 4,2-5,2-2,7 288 50 0 5 20,53 0,07 6 20,48 23,18 0,09 3,9 0,1-1,2-88,8-9,9 4,3-5,6-2,9 282 49 7 20,58 0,10 8 20,47 0,18 4,0 0-2,2-89,7-8,1 6,4-9,3-4,0 284 50 0 9 20,52 23,23 0,10 10 20,49 0,09 4,4 0-1,7-87,8-10,5 7,3-10,1-5,2 281 50 0 11 20,57 0,11 2 nd EXAMPLE a) Production rate : 50 t/h b) Operational conditions : Sulfuric acid concentration : 96,6% b.w. N° of sample Reaction temperature (°C) Liquor density (g/l) Liquor pH Tubular reactor pressure Tub. reactor temperature (°C) Granulator pH (1%b.w) Fuel gases temper. (dryer inlet)(°C) Fuel gases temper. (dryer outlet)(°C) Product term. (cooler outlet) (°C) 1 111,0 1365 3,5 4,0 152 4,1 461 99 2 110,7 1353 4,1 4,1 153 4,1 459 100 3 110,7 1332 4,2 4,1 153 4,5 482 99 15 4 112,1 1333 3,7 4,1 153 4,4 481 99 5 112,3 1330 2,6 3,9 151 4,4 497 95 6 111,9 1320 2,7 3,9 151 4,1 498 101 7 110,8 1314 3,9 4,0 152 4,3 476 98 8 112,2 1321 3,4 3,9 151 4,3 485 98 15 9 111,8 1329 3,6 3,8 151 4,2 472 98 10 112.3 1313 3,9 3,8 151 4,0 437 99 18 11 111.5 1317 3,9 4,3 154 4,4 443 101 12 112,1 1330 3,3 4,2 153 4,2 482 99 13 112.2 1335 2,9 4,0 152 3,9 497 100 14 112,0 1307 2,7 4,0 152 4,0 496 101 15 112,1 1324 2,9 4,1 153 3,9 484 101 c) Feeding proportions (%) Sulfuric acid Ammonia Water N° of sample Reaction tank Tubular reactor Stripping columns Reaction tank Tubular reactor Granulator Reaction tank Tubular reactor 1 35 46 19 43 48 9 92 8 2 36 46 18 46 49 5 89 11 3 36 46 18 44 48 8 91 9 4 36 46 18 43 50 7 91 9 5 36 46 18 45 49 6 90 10 6 36 46 18 45 48 7 92 8 7 36 46 18 44 50 6 92 8 8 36 46 18 45 49 6 92 8 9 36 46 18 45 49 6 92 8 10 36 46 18 46 50 4 88 12 11 36 46 18 44 49 7 90 10 12 36 46 18 45 48 7 91 9 13 36 46 18 44 48 8 92 8 14 35 47 18 45 48 7 92 8 15 35 47 18 44 48 8 92 8 d) Chemical - physical properties of product N° of sample Nitrogen cont.(%b.w.) Sulfur cont.(%b.w.) Free moist. (%b.w.) pH 1%b.w. Granulom. (%b.w.)*1 Hardness (%b.w.)*2 SGN UI Tendency to agglomerate (kg) 1 20,55 0,06 2 20,55 0,08 3,6 0,3-2,9-88,1-8,7 5,0-5,9-3,7 261 54 0 3 20,46 23,36 0,09 4 20,59 0,09 5 20,60 0,11 4,7 0-2,5-89,8-7,7 5,5-9,1-3,8 268 52 0 6 20,55 23,43 0,08 7 20,52 0,07 8 20,53 0,09 4,7 0-2,2-87,9-9,9 4,9-5,7-4,3 286 50 0 9 20,57 23,46 0,10 10 20,59 0,07 11 20,52 0,09 3,6 0-1,3-88,0-10,7 5,0-5,8-4,0 282 50 0 12 20,55 23,50 0,09 13 20,55 0,09 14 20,52 23,60 0,09 4,3 0,1-2,3-91,1-6,5 - 281 53 15 20,58 0,09 3 rd EXAMPLE a) Production rate : 55-65 t/h b)Operational conditions : Sulfuric acid concentration : 96,9% b.w. N° of sample Reaction temperature (°C) Liquor density (g/l) Liquor pH Tubular reactor pressure Tub. reactor temperature (°C) Granulator pH (1%b.w) Fuel gases temper. (dryer inlet)(°C) Fuel gases temper. (dryer outlet)(°C) Product tem. (cooler outlet) (°C) 1 113,5 1326 2,4 4,5 156 3,8 465 104 2 112.6 1328 2,7 4,2 153 4,1 428 103 27 3 112,0 1303 3,7 4,2 153 4,0 430 101 4 111,5 1305 4,3 4,3 154 3,9 460 102 5 111,7 1323 4,0 4,4 155 4,0 460 108 31 6 112,1 1330 3,6 4,4 155 3,7 465 109 7 111,3 1371 4,0 4,3 154 4,0 500 106 8 111,0 1350 4,5 4,2 153 3,9 469 105 32 c) Feeding proportions (%) Sulfuric acid Ammonia Water N° of sample Reaction tank Tubular reactor Stripping columns Reaction tank Tubular reactor Granulator Reaction tank Tubular reactor 1 39 48 13 45 45 10 94 6 2 39 48 13 44 44 12 94 6 3 39 48 13 43 46 11 94 6 4 40 48 12 44 45 11 94 6 5 42 47 11 43 47 10 93 7 6 40 46 14 49 43 8 97 3 7 41 44 15 43 45 12 98 2 8 41 43 16 43 46 11 99 1 d) Chemical - physical properties of product N° of sample Nitrogen cont.(%b.w.) Sulfur cont.(%b.w.) Free moist (%b.w.) pH 1%b.w . Granulom. (%b.w.)* Hardness (%b.w.)* SGN UI Tendency to agglomerate (kg) 1 20,44 0,17 2 20,54 0,10 3,5 0,2-2,8-91,5-5,5 7,6-8,8-6,3 286 52 0 3 20,55 23,26 0,10 4 20,53 0,08 0 5 20.47 0,09 3,6 0-2,6-91,6-5,8 5,8-9,0-4,1 286 51 6 20,58 23,30 0,09 7 20,45 0,10 8 20,63 0,08 3,7 0-1,3-86,7-12,0 5,1-6,7-3,7 281 49 0

Claims: Production method for granular ammonium sulphate, using a combination of by : a. The reaction of sulphuric acid of more than 70 % concentration by weight with liquid or gaseous ammonia, with the simultaneous addition of recycled water acidified by sulphuric acid in a cylindrical reaction tank fitted with co-axial agitators and in a serially positioned tubular reactor. b. The fact that the addition of raw materials and acidified recycled water takes place in both the reaction tank and in the tubular reactor. Production method as described in claim 1, characterised by the fact that the reaction in the cylindrical tank takes place at a temperature of 100-120°C and at normal atmospheric pressure. Production method as described in claim 1, characterised by the fact that the reaction in the cylindrical tank takes place at a temperature of 108-115 °C and at normal atmospheric pressure. Production method as described in claims 1 and 2, characterised by the fact that the liquor produced in the reaction tank has a moisture level of 34-42 % by weight and a density of 1260-1430 g/l, measured at the reaction temperature. Production method as described in claims 1 and 3, characterised by the fact that the liquor produced in the reaction tank has a moisture level of 34-42 % by weight and a density of 1290-1370 g/l, measured at the reaction temperature. Production method as described in claim 1, characterised by the fact that the liquor produced in the reaction tank has a pH of 2.5 - 6. Production method as described in claim 1, characterised by the fact that the liquor produced in the reaction tank has a pH of 3 - 5 . Production method as described in claim 1, characterised by the fact that the liquor produced in the reaction tank ends up in an intermediate vessel, to which may be added liquid effluents from other production units or other plants and from which it is pumped into a tubular reactor. Production method as described in claims 1 and 8, characterised by the fact that the reaction in the tubular reactor takes place at a pressure of 3 - 6 bar and a temperature above 130°C. Production method as described in claims 1 and 8, characterised by the fact that the reaction in the tubular reactor takes place at a pressure of 3.5 - 5 bar and a temperature above 130°C. Production method as described in claim 1, characterised by the fact that the liquor from the tubular reactor - with a moisture level of 5 - 12 % by weight, is projected into a rotating granulator to which ammonia is added in either liquid or gaseous form. Production method as described in claim 11, characterised by the fact that the solid product leaving the granulator has a pH, measured in a 1% by weight solution, from 3 to 5 and a moisture level of 2 to 4.5 % by weight. Production method as described in claim 1, characterised by the fact that the solid product leaving the granulator has a pH, measured in a 1% by weight solution, from 3.2 to 4.5 and a moisture level of 2 to 4.5 % by weight. Production method as described in claim 1, characterised by the fact that the liquid or gaseous ammonia added to the cylindrical reaction tank amounts to 37-55 % by weight of the total quantity of ammonia added. Production method as described in claim 1, characterised by the fact that the liquid or gaseous ammonia added to the tubular reactor amounts to 42 - 52 % by weight of the total quantity of ammonia added. Production method as described in claim 1, characterised by the fact that the liquid or gaseous ammonia added to the granulator amounts to 3-11 % by weight of the total quantity of ammonia added. Production method as described in claims 1,14,15 and 16, characterised by the fact that the acidified recycled water added to the reactor tank and the tubular reactor is first sprayed through the tail gas stripping columns, where it absorbs and neutralises the gaseous ammonia that may have remained in the reaction tank, the tubular reactor and the granulator, turning it into a solution of acidic ammonium sulphate. Production method as described in claim 1, characterised by the fact that the sulphuric acid added to the reaction tank amounts to 31-45 % by weight of the total quantity of acid added. Production method as described in claim 1, characterised by the fact that the sulphuric acid added to the tubular reactor amounts to 42-52 % by weight of the total quantity of acid added. Production method as described in claims 1 and 17, characterised by the fact that the sulphuric acid added to the stripping columns to capture the tail gases amounts to 10-20% by weight of the total quantity of acid added. Production method as described in claims 1,17 and 20, characterised by the fact that the acidified (by sulphuric acid) recycled water that exits the stripping columns and is fed into the reaction tank amounts to 89-95 % by weight of the total quantity of recycled water added. Production method as described in claims 1,17 and 20, characterised by the fact that the acidified (by sulphuric acid) recycled water that exits the stripping columns and is fed into the tubular reactor amounts to 5-11 % by weight of the total quantity of recycled water added. Production method as described in claim 12, characterised by the fact that the product produced in the granulate is dried in a rotary oven with a concurrent flow of exhaust gases, with a temperature of 440-480 °C at the entrance of the oven. Production method as described in claims 12 and 23, characterised by the fact that the product produced in the granulator is dried in a rotary oven with a concurrent flow of exhaust gases, with a temperature at the entrance of the oven that may reach 500 °C. Production method as described in claims 12, 23 and 24, characterised by the fact that the product produced in the granulator is dried in a rotary oven with an exit temperature of 95 - 110 °C. Production method as described in claims 12, 23 and 24, characterised by the fact that the product produced in the granulator is dried in a rotary oven with an exit temperature of 98 - 110 °C. Production method as described in claims 25 and 26, characterised by the fact that the product produced in the granulator is fed into a system of sieves such that at the end of the system at least 90 % by weight of the grains have a diameter between 2 and 4.5 mm. Production method as described in claim 27, characterised by the fact that the commercial product leaving the sieves is air-cooled on a fluidized bed, exiting at a temperature of 10 - 45 °C whereafter it is coated with a suitable substance to prevent grains from agglomerating. Production method as described in claims 1 to and including 28, characterised by the fact that the total amount of energy absorbed for a single production line amounts to 30 - 40 kwh per ton of product. Production method as described in claims 1 to and including 29, characterised by the fact that the total amount of energy absorbed for a single production line amounts to 1800 - 2200 kwh per hour of operation. Production method as described in claims 1 to and including 30, characterised by the fact that the level of production for a single production line may reach 65 t/hr. Product in the form of granular ammonium sulphate produced according to claims 1 to and including 31, characterised by : a. The fact that it is free-flowing and non agglomerating b. Its nitrogen content of more than 20.5 % by weight, entirely in the form of ammonium c. Its free moisture content, which does not exceed 0.3 % by weight d. The pH of a 1 % solution by weight, which lies between 3.2 and 4.5 Product produced according to claims 1 to and including 22 and claims 27 and 31, characterised by the fact that at least 90% by weight of grains have a diameter of between 2 and 4.5 mm. Product produced according to claims 1 to and including 22 and claims 27 and 31, characterised by the fact that 87-95% by weight of grains have a diameter of between 2 and 4 mm. Product according to claim 32 characterised by the hardness of the grains, which has an average value of 3 kg at least, a maximum value of 5 kg at least, and a minimum value of 2 kg at least. Product according to claim 32, characterised by the hardness of the grains, which have an average value usually superior to 4 kg, a maximum value usually superior to 5.5 kg and a minimum value usually superior to 3 kg. Product according to claim 32, characterised by the flexibility of having a SGN ranging from 200 to 300 and a UI of 50 to 55, according to requirements. Product according to claim 32, characterised by its low agglomeration tendency, which does not exceed 0.3kg, determined by an original method, which measures the applied weight necessary to crush a sample of 30gr of product that has been centrifuged at 4500rpm for 4 hours and then left for another 4 hours. The method is repeated once and the final value is defined as the average of the two results. Product according to claim 32, characterised by the fact that it usually has an agglomeration tendency of 0 kg, determined by the original method described in claim 38.

Inventors: BELLIS D, BELLIS, D., Bellis, D., Biomihania Fosforikon Lipasmaton AE
Applicants: BIOMIHANIA FOSFORIKON LIPASMAT, BIOMIHANIA FOSFORIKON LIPASMATON A.E.
Application year: 2000
Main classification: C01C1
IPC codes: C01C1, C05C3