TOUGHENED NYLON COMPOSITIONS WITH IMPROVED FLOW AND PROCESSES FOR THEIR PREPARATION

Abstract: Rubber-toughened and ionomer-toughened polyamide compositions are provided which exhibit decreased molecular weight in comparison with conventional systems but without compromising the toughness of the system. Processes for their preparation are also provided, in which excess organic acid is incorporated into the polyamide-functionalized rubber system.

Description: TITLE TOUGHENED NYLON COMPOSITIONS WITH IMPROVED FLOW AND PROCESSES FOR THEIR PREPARATION FIELD OF THE INVENTION This invention relates to toughened polyamide compositions and processes for their preparation. More specifically, this invention relates to such compositions toughened with rubber or ionomer, which incorporate organic acids to desirably decrease viscosity but without significantly reducing the toughness thereof, together with methods for their preparation. BACKGROUND OF THE INVENTION High flow (or low melt viscosity, as these terms are used interchangeably) is a very desirable characteristic of an injection molding resin. A resin with higher flow or lower melt viscosity can be injection molded with greater ease compared to another resin which does not possess this characteristic. Such a resin has the capability of filling a mold to a much greater length at lower injection pressures and temperatures and greater capability to fill intricate mold designs with thin cross-sections. It is well known that the melt viscosity of a polymer is directly proportional to its molecular weight. It is also well known that the melt viscosity of a polymer, especially at low shear rates are much higher for a branched polymer compared to a linear polymer at the same molecular weight. It is also well known that polyamide polymers react with organic acids and amines when added in the melt causing a reduction in its molecular weight. This method is sometimes used to increase the flow or lower the melt viscosity of a polyamide polymer. The presence of a dispersed phase such as mineral and glass reinforcements in a polymer results in increased melt viscosity. The presence of a dispersed phase of an incompatible polymer also results in an increase in the melt viscosity. To be able to form a stable dispersion, the toughener is generally functionahzed with for example, anhydride or epoxide. Thus, generally, rubber- toughened polyamides containing dispersed rubber have melt viscosities much higher than the original polyamide polvmer It is also well know n that to obtain good toughness and to optimi/e dispersion ot incompatible polymers such as olefin rubbers and/or lonomers w ith polyamides, the melt v iscosities of the two polymers must be fairly close to each other The adv antages of reduced viscosity resins are well known to those skilled in the practice of injection molding However, the most highly desirable combination of properties was previously not available For example, tougheners such as are disclosed in US 4,174,358, incorporated herein by reference, can be utilized in improving the toughness of polyamide resins by melt blending polyamide res s with low tensile modulus copolymers that have adherent sites to obtain a highly toughened polyamide mateπal However, addition of tougheners also increases the viscosity of the resin This fact has inevitably led to compromises in property selection Preparation of tough, high melt flow polyamides has also been addressed somewhat in the literature For example, US 5,274,033 discloses blending of low molecular weight polyamide into the toughened polyamide blend as a route to production of a high flow toughened polyamide While quite suitable, this has the disadvantage of adding expensive process steps such as preparation of the low molecular weight polyamide Meeting the objective of producing high melt flow toughened polyamides in an easily commercial step had previously eluded the trade. It is an object of the present invention to provide toughened nylon compositions exhibiting improved flow as compared to conventional resins duπng injection molding operations It is a further object of the invention to provide rubber or lonomer-toughened nylon compositions that exhibit such desirable flow characteπstics while not detracting from their toughness A feature of the present invention is its applicability across a wide range of process conditions An advantage of the invention is the incorporation of organic acids into the polyamide-functiona zed rubber or ionomer system to enhance flow but without sacrificing toughness properties These and other objects, features and advantages will become better appreciated upon having reference to the following description of the invention herein SUMMARY OF THE INVENTION Toughened polyamide compositions are provided, compπsing (a) 40-94 percent by weight polyamide, (b) 6-60 percent by weight toughener selected from the group consisting of rubber and ionic copolymer, and (c) up to 10 percent by weight organic acid Useful polyamides in conjunction with the compositions of the invention include those listed throughout the descπption, together with blends and copolymers thereof The toughener is preferably used in amounts of from about 8 to about 40 percent by weight, and most preferably from about 10 to about 30 percent by weight In a preferred embodiment of the invention, the polyamide compositions compπse 50-94 weight percent polyamide, 6-50 weight percent of the toughener, and up to 10 weight percent of organic acid Any number of organic acids may be selected Organic acids are organic compounds of C, H, and O containing one or more carboxyhc acid functionalities Examples of suitable organic acids include adipic acid, pime c acid, subeπc acid, azelaic acid, sebacic acid, undecanedioic acid, and dodecanedioic acid (all dicarboxy c acids), and, valeπc acid, tπmethylacetic acid, caproic acid, and capry c acid (all monocarboxyhc acids) Dodecanedioic acid ("DDDA") is of particular interest There is also disclosed and claimed herein processes for the preparation of toughened polyamide compositions exhibiting high flow and toughness. comprising melt-mixing in a conventional extruder 40-94 percent by weight polyamide, 6-60 percent by weight toughener selected from the group consisting of rubber and ionic copolymer, and up to 10 percent by weight organic acid. There are many process variations contemplated herein. For example, the polyamide, toughener and organic acid may be melt-mixed as one step; a blend of polyamide and toughener may be melt-mixed with the acid; or polyamide and toughener may be blended and subsequently melt-mixed with the acid. Further, melt-mixing may be effected by extrusion or molding alone or in combination. DETAILED DESCRIPTION OF THE INVENTION A process is herein provided for the manufacture of rubber-toughened nylon compositions with improved flow during injection molding. It has been discovered that a rubber-toughened nylon composition can be produced by the addition of organic acids added during the melt compounding step. Rubber-toughened polyamide compositions have been commercially available for more than twenty years. The technology involves incorporating an olefinic rubber in the polyamide. This is often done in the melt phase. The rubber dispersion must be fairly stable, i. e., the rubber phase must not coalesce substantially during subsequent melt processing such as injection molding. Since olefinic rubbers are incompatible with polyamides, it is necessary to modify the rubber with functional groups that are capable of reacting with the acid or amine ends in the polyamide polymer. The reaction of an anhydride with amine is very fast, therefore, an anhydride is often the functionality of choice. When an incompatible olefinic rubber with an anhydride functionality is mixed with a polyamide, the anhydride functionality of the rubber reacts with the amine ends of the polyamide resulting in the rubber becoming grafted on the polyamide molecule. This molecular bonding minimizes coalescence of the rubber phase. The use of ionic copolymers to produce toughened nylon blends is well known in the art. See for example US 3,845, 163 which discloses blends of nylon and ionic copolymers. Further, US 5,688,868 discloses the preparation of such toughened blends wherein the ionic copolymer is prepared in-situ with very high levels of neutralization. USP 5,091 ,478 discloses flexible thermoplastic blends wherein the nylon component may be between 25-50 volume % with the polyamide comprising at least one continuous phase of the composition. Finally, US 5,866,658 covers ionomer / polyamide blends in the range 40-60 weight percent ionomer and 60-40 weight percent polyamide. The present invention may be applied to the types and ranges of ionic copolymers as disclosed therein. The reaction between the functionality of the toughener and the end groups of the polyamide is necessary for the grafting to occur. For example, with the anhydride-amine end, reaction is necessary in order for the rubber toughening to occur. Any significant interference with this reaction will impact negatively on the toughening. It is also important that the melt viscosities of the rubber and the polyamides are close to each other to accomplish good dispersion. The discovery herein involves a process for the preparation of a rubber-toughened polyamide wherein excess organic acid is incorporated in the polyamide-functionalized rubber system without negative impact on the toughness of the system. Without intending to be limited to any particular theory, it is thought that the added organic acids react with the polyamide decreasing the polyamide molecular weight and its melt viscosity without apparent interference with the toughening chemistry. This is very surprising because the expected interference of the organic acids on the anhydride-amine end reaction and the negative effect of lowered melt viscosity did not have an impact on toughness. Those skilled in the art will appreciate that the above described benefits are suitable for a wide range of polyamide compositions. Without intending to limit the generality of the foregoing, the following are of particular interest: • Polyamides selected from the group consisting of nylon-4,6, nylon-6,6, nylon-6,10, nylon-6,9, nylon-6,12, nylon-6, nylon- 1 1 , nylon-12, 6T through 12T, 61 through 121, polyamides formed from 2- methylpentamethylene diamine with one or more acids selected from the group consisting of isophthalic acid and terephtha c acid, and blends and copolymers of all of the above • Notched Izod toughnesses of at least 3 0 ft-lb (however, compositions featuπng lower Notched Izod values are observed as the rubber or ionomer content is decreased) The polyamides disclosed herein are also used in blends with other polymers to produce engineeπng resins The blends of this invention may also contain certain additional polymers that could partially replace the polyamide component. Examples of such additional polymers are melamine formaldehyde, phenol formaldehyde (novolac), polyphenylene oxide (see for example EP 0 936 237 A2), polyphenylene sulfide, polysulfone and the like These polymers can be added dunng the mixing step. It will be obvious to those skilled in the art that the present invention relates to modification of the polyamide component and that additional polymers could be added appropπately without departing form the spiπt of this present invention Representative tougheners useful in the practice of this invention include many branched and straight chain polymers and block copolymers and mixtures thereof. These are represented by the formula A f nj-B^-Q^-D fl-Etej-F^-G -Hrt, deπved in any order, e.g , random, from monomers A to H where A is ethylene; C is an unsaturated monomer taken from the class consisting of a β- ethylemcally unsaturated carboxyhc acids having form 3 to 8 carbon atoms, and deπvatives thereof taken from the class consisting of monoesters of alcohols of 1 to 29 carbon atoms and the dicarboxylic acids and anhydπdes of the dicarboxylic acids and the metal salts of the monocarboxylic, dicarboxylic acids and the monoester of the dicarboxylic acid having from 0 to 100 percent of the carboxyhc acid groups ionized by neutralization with metal ions and dicarboxylic acids and monoesters of the dicarboxylic acid neutralized by amine-ended caprolactain oligomers having a DP to 6 to 24; D is an unsaturated epoxide of 4 to 1 1 carbon atoms; E is the residue derived by the loss of nitrogen from an aromatic sulfonyl azide substituted by carboxyhc acids taken from the class consisting of monocarboxylic and dicarboxylic acids having from 7 to 12 carbon atoms and derivatives thereof taken from the class consisting of monoesters of alcohols of 1 to 29 carbon atoms and the dicarboxylic acids and anhydrides of the dicarboxylic acids and the metal salts of the monocarboxylic, dicarboxylic acids and the monoester of the dicarboxylic acid having form 0 to 100 percent of the carboxyhc acid groups ionized by neutralization with metal ions; F is an unsaturated monomer taken form the class consisting of acrylates esters having form 4 to 22 carbons atoms, vinyl esters of acids having form 1 to 20 carbon atoms (substantially no residual acid), vinyl ethers of 3 to 20 carbon atoms, and the vinyl and vinylidene halides, and nitriles having from 3 to 6 carbon atoms; G is an unsaturated monomer having pendant hydrocarbon chains of 1 to 12 carbon atoms capable of being grafted with monomers having at least one reactive group of the type defined in C, D and E, and pendant aromatic groups which my have 1 to 6 substituent groups having a total of 14 carbon atoms; and H is an unsaturated monomer taken from the class consisting of branched, straight chain and cyclic compounds having from 4 to 14 carbon atoms and at least one additional nonconjugated unsaturated carbon-carbon bond capable of being grafted with a monomer having at least one reactive group of the type defined in C, D and E. The aforementioned monomers may be present in the polymer in the following mole fraction: (a) 0 to 0.95; (b) 0 to 0.3; (c) 0 to 0.5; (d) 0 to 0.5; (e) 0 to 0.5; ( 0 0 to 0 99, (g) 0 to 0 99, and (h) 0 to 0 99 so that the total of all components is a mole fraction of 1 0 Preferably (a) to (h) are present in the following mole fraction (a) 0 to 0 9, (b) 0 to 0 2, most preferably 0 1 to 0 2 (c) 0 0002 to 0 2 most preferably 0 002 to 0 05, (d) 0 005 to 0 2, most preferably 0 01 to 0 1 , (e) 0 0002 to 0 1 , most preferably 0 002 to 0 01 , (f) 0 to 0 98, (g) 0 to 0 98, and (h) 0 to 0 98 The blends of this invention may also contain one or more conventional additives such as stabilizers and inhibitors of oxidative, thermal, and ultraviolet light degradation, lubπcants and mold release agents, colorants including dyes and pigments, flame-retardants, plasticizers, and the like These additives are commonly added duπng the mixing step They may be added in effective amounts as is readily appreciated by those having skill in the art Representative oxidative and thermal stabilizers which may be present m blends of the present invention include hahde salts, e g , sodium, potassium, lithium with copper salts, e g , chioπde, bromide, iodide, hindered phenols, hydroquinones, and vaπeties of substituted members of those groups and combinations thereof Representative ultraviolet light stabilizers, include vaπous substituted resorcinols, sa cylates, benzotπazoles, benzophenones, and the like Representative lubπcants and mold release agents include steaπc acid, stearyl alcohol, and stearamides Representative organic dyes include nigrosine, while representative pigments, include titanium dioxide, cadmium sulfide, cadmium selenide, phthalocyanines, ultramarine blue, carbon black, and the like Representative flame-retardants include organic halogenated compounds such as decabromodiphenyl ether and the like. The toughener can be used in neat or diluted form. In the latter case, either EPDM, EPR, or polyethylene can be used as the diluent. EXAMPLES The invention is illustrated by the following Examples and Comparative Examples herein. Melt Viscosity data were obtained at 280 C using a commecial rheometer such at the Kayeness Rheometer, Model 8052. Notched Izod toughness were determined in accordance with ASTM D256 at room temperature on a 5" x '/_" x l/8"specimens, or with ISO 527-2C at room temperature an a 4mm thick x 80mm in length specimen. Comparative Example 1 A pellet blend of 141.8 lb of nylon 66 under the tradename ZYTEL® 101 (available from E.I. duPont de Nemours and Co., Wilmington, DE) and 33.2 lb of anhydride functionahzed rubber under the tradename FUSABOND® N MF521D (available from E.I. duPont de Nemours and Co.) was introduced into the first barrel of a ten-barrel 53 mm Werner & Pfleiderer twin-screw extruder at a rate of 300 lb/hr, extruder RPM of 250 with a high shear screw, and vacuum of 14" - 15" applied on barrel 9. The melt temperature during the extrusion process was 329 C. The polymer strands coming from the extπider were quenched in water and fed to a cutter. The hot pellets were collected in a vessel that was continuously swept with nitrogen gas to avoid moisture absorption from the air. Example 1 Example 1 was prepared in the manner described for Comparative Example 1 above from a pellet blend of 140.9 lb of ZYTEL ® 101, 33.2 lb of FUSABOND® N MF521 D, and 397.2 g of dodecanedioic acid. Using the same extruder conditions as in the Comparative Example and a rate of 300 Ib/hr, the melt temperature duπng extmsion was 314 C The polymer strands coming from the extruder were quenched in water and fed into a cutter The hot pellets were collected in a vessel that was continuously swept with nitrogen gas Example 2 A pellet blend of 135 1 lb of ZYTEL ® 101 and 39 9 lb of FUSABOND® N MF521 D was introduced into the first barrel of a ten-barrel 53 mm Werner & Pfleiderer twin-screw extruder at 250 lb/hr using same conditions as Comparative Example 1 At the same time a blend of 169 8 lb ZYTEL® 101 and 5.2 lb of dodecanedioic acid was introduced into barrel #7 at a rate of 50 lb/hr This composition is equivalent to Example 1 The melt temperature duπng extrusion was 312 C The polymer strands coming from the extruder were quenched in water and fed into a cutter The hot pellets were collected in a vessel that was continuously swept with nitrogen gas A compaπson of the results of this work is provided in Table 1 below Table 1 The results above show that in the presence of the dodecanedioic acid there was a dramatic decrease in melt viscosity The change in melt viscosity also is essentially unaffected by the location of the where the dodecanedioic acid is introduced The results also show that there is essentially no change in the Notched Izod toughness in the presence of the diacid Comparative Examples 2-3 and Example 3 In the following series of experiments the ingredients were melt blended with each other under high shear. The various ingredients may first be dry blended with each other by tumbling in a drum or they may be combined with one another via simultaneous or separate meteπng of one or more of the components. Preferably the melt blending will be done in a twin screw extruder manufactured by Werner & Pfleiderer or Berstorff, although numerous other high shear melt blending devices, apparent and well known to those skilled in the art, may be used. Table 2 shows re-extrusion of a polyamide blend together with the dodecanedioic acid. The polyamide blend and dodecanedioic acid feeds were controlled by dry blending and feeding with a single metering device. The ingredients were blended by tumbling 74.5 pounds. ZYTEL® ST801HS NC010 (a rubber-toughened 6,6-nylon available commercially from E. I. DuPont de Nemours & Co.) and 221.3 grams dodecanedioic acid (available commercially from E. I. DuPont de Nemours & Co.) in a drum. The blended ingredients were fed into the extruder by a K-Tron loss-in-weight screw feeder running at 180 lb/hr. In this case the melt blending occurred in a 40 mm Werner & Pfleiderer twin screw extruder operating 300 rpm screw speed with a high shear screw. The ingredients were fed into barrel 1 with a screw feeder. A vacuum was applied at barrel 8. After exiting through a 4-hole die, the strands were quenched in an ambient water trough with circulating water. The strands were subsequently pelletized and allowed to cool under nitrogen sparge. Table 2 Ingredient (weight %) Example 3 Comp Ex 2 Comp Ex 3 ZYTST801HS NC010 99.35% 100.00% 100.00% Dodecanedioic Acid 0.65% Notched Izod, DAM, 63.37 69.7 59.28 23°C, kj/m 2 Melt viscosity, Pa-S 96 198 182 This series of examples demonstrates that the benefits and attributes of the invention herein are recognized even with the addition of the acid as a separate step. The commercial grade of nylon selected as above is already rubber- toughened, and the subsequent introduction of the acid still imparted the desirable enhancement in melt viscosity without compromising the toughness. This is illustrative of the range of applicability of the process and compositions of the invention, and for example is well suited for injection-molding applications. Comparative Example 4 and Examples 4-6 This series of examples shows the applicability of dodecanedioic acid in reducing the viscosity of nylon/ionic polymer blends without degrading physical properties. Table 3 shows compositions containing nylon 66 as the thermoplastic polyamide and an ionic polymer as the toughening material together with the dodecanedioic acid sufficient to produce an appropriate degree of viscosity reduction. In these examples, the nylon and toughener feeds were controlled by separate metering. The ionic polymer feed stream was SURLY ® 9520W acid (available commercially from E. I. DuPont deNemours & Co.). It was fed by a K-Tron loss-in-weight screw feeder running at 31.6 lb/hr. The nylon feed stream was comprised of a 66-nylon polymer having an RV of approximately 50 and about 40 amine ends), copper-based heat stabilizer, Ampacet Black Concentrate 19238 ("Amp Bk 19238") (available commercially from Ampacet Corp., Tarrytown, NY), and optionally, dodecanedioic acid (available commercially from E. I. DuPont deNemours & Co.). The nylon feed stream ingredients were blended by tumbling in a drum. This feed stream was fed into the extruder by a K-Tron loss-in-weight screw feeder running at 148.4 lb/hr. In this case the melt blending occurred in a 40 mm Werner & Pfleiderer twin screw extruder operating 300 rpm screw speed with a high shear screw. The ingredients were fed into barrel 1 with a screw feeder. A vacuum was applied at barrel 8. After exiting through a 4-hole die, the strands were quenched in an ambient water trough with circulating water. The strands were subsequently pelletized and allowed to cool under nitrogen sparge. Table 3 Ingredient Comp Example Example Example (weight %) Ex 4 4 5 6 HS711 0.003 0.003 0.003 0.003 66-nylon 0.777 0.7745 0.772 0.7705 polymer SURLYN® 0.1755 0.1755 0.1755 0.1755 9520W Amp Bk 19238 0.0445 0.0445 0.0445 0.0445 DDDA 0 0.0025 0.005 0.0065 Notched Izod, 18.5 17.02 16.76 17.04 DAM, 23°C, ft-lb/in Melt Viscosity, 146 110 91 87 Pa-S NOTE: HS71 1 is a physical blend of cuprous iodide / potassium iodide / aluminum distearate in the ratio of 7/1/1. Comparative Examples 5-6 and Examples 7-12 A series of experiments was conducted to illustrate the effect of high amounts of DDDA (up to 1.0 weight percent) on properties of nylon 66 compositions including 7.0 weight % and 19.0 weight % FUSABOND® N MF52 I D toughener. These compositions were prepared in the manner detailed in Comparative Example 1 and Example 1. The results are shown in Table 4. Surprisingly, even at 1.0 % DDDA there was only about a 14% decrease in the Notched Izod toughness at both low and high levels of toughener. There are enough acid equivalents at 1.0 % DDDA to react completely with the amine ends of the nylon These results indicate that the composition of the invention is fairly robust across various levels of DDDA, and with this information one of ordinary skill in the art will readily appreciate that existing manufacturing equipment and procedures are capable of producing these types of products. TABLE 4 Example or NYLON 66 FUSABOND®N %DDDA Notched Izod Melt Viscosity(Pa-S)@Various Shear Rates CompEx MF521D,% (ft-lb/in) 1001/sec 10001/sec 29991/sec Comp Ex 5 9300%Z101 700 0.00 1.84 239 87 29 Example 7 9250%Z101 700 0.50 1.98 119 64 21 Example 8 9235%Z101 700 0.65 1.90 104 46 21 Example 9 9200%Z101 700 1.00 1.58 62 14 14 Comp Ex 6 8100%Z101 1900 0.00 13.42 967 203 68 Ul Example 10 8050%Z101 1900 050 12.40 498 117 39 Example 11 8035%Z101 1900 065 12.53 397 89 41 Example 12 8000%Z101 1900 1.00 11.69 267 80 27 It is to be further appreciated that these compositions are adaptable to suit any number of processing techniques. For example, molders of toughened polyamide parts may find very different means of using these products to improve their existing injection molding processes. A molder using a multi-cavity mold to produce small parts may have difficulty completely filling the mold due to the limits of temperature, maximum machine pressure, and resin viscosity. A higher melt flow resin would allow use of even higher numbers of mold cavities without exceeding the machine's maximum injection pressures. In other cases, a manufacturer may have difficulties arising from high melt temperatures, such as part surface blemish defects commonly referred to as "ghosting." While reductions of melt temperatures frequently alleviate such defects, certain manufacturers may be unable to operate successfully at lower melt temperatures due to the viscosity of the resin in use. A higher melt flow resin would allow molders to use lower melt temperatures and thereby eliminate part appearance defects.

Claims: IN THE CLAIMS: 1 A toughened polyamide composition comprising (a) 40-94 percent by weight polyamide, (b) 6-60 percent by weight toughener selected from the group consisting of rubber and ionic copolymer, and (c) up to 10 percent by weight organic acid 2 The composition of Claim 1 wherein said polyamide is selected from the group consisting of nylon-4,6, nylon-6, 6, nylon-6, 10, nylon-6, 9, nylon-6, 12, nylon-6, nylon-1 1, nylon- 12, 6T through 12T, 61 through 121, polyamides formed from 2-methylpentamefhylene diamme with one or more acids selected from the group consisting of lsophtha c acid and terephtha c acid, and blends and copolymers of said nylons and polyamides thereof 3 The composition of Claim 1 wherein the amount of said polyamide is 50-94 percent by weight, the amount of said toughener is 6-50 percent by weight, and the amount of said organic acid is up to 10 percent by weight 4 The composition of Claim 1 wherein the amount of said toughener is about 8 to about 40 percent by weight 5 The composition of Claim 3 wherein the amount of said toughener is about 10 to about 30 percent by weight 6 The composition of Claim 1 wherein said organic acid is selected from the group consisting of adipic acid, pime c acid, subeπc acid, azelaic acid, sebacic acid, undecanedioic acid, dodecanedioic acid, valeπc acid, tπmethylacetic acid, caproic acid, and capryhc acid 7 The composition of Claim 6 wherein said organic acid is dodecanedioic acid 8 An article made from the composition of Claim 1 9 A process for the preparation of toughened polyamide compositions exhibiting high flow and toughness, compπsing melt-mixing 40-94 percent by weight polyamide, 6-60 percent by weight toughener selected from the group consisting of rubber and ionic copolymer, and up to 10 percent by weight organic acid 10. The process of Claim 9 wherein said polyamide, said toughener, and said organic acid are melt-mixed in one step. 11. The process of Claim 9 wherein a blend of said polyamide and said toughener is melt-mixed with said organic acid. 12 The process of Claim 9 wherein said polyamide and said toughener are blended and said organic acid is subsequently melt-mixed therewith. 13. The process of Claim 12 wherein said melt-mixing is accomplished by one or both of extrusion and molding. 14. The process of Claim 9 wherein said organic acid is dodecanedioic acid. S \Patent DocumentsvEng Polymers\Ad-66xx\AD66 5 0NA doc

Inventors: FISH ROBERT B JR, PAGILAGAN ROLANDO UMALI, FISH, ROBERT, B., JR., PAGILAGAN, ROLANDO, UMALI
Applicants: DU PONT, E.I. DU PONT DE NEMOURS AND COMPANY
Application year: 2000
Main classification: C08L77
IPC codes: C08G69, C08J5, C08K5, C08L21, C08L77, C08L101