Radiation-sensitive compositions for printing plates for improving their chemical and developer resistance and printing plates comprising said compositions

Abstract: The invention describes radiation-sensitive compositions comprising at least one novolak, at least one naphthoquinone diazide derivative and a copolymer; the copolymer consisting of the units A, B and C wherein unit A is present in an amount of 5 to a maximum of 50 mol% and R 1 and R 4 are selected such that the homopolymer of A is alkali-soluble, B is present in an amount of 20 to 70 mol% and R 2 , R 6 and R 7 are selected such that the homopolymer of B has a high glass transition temperature, and C is present in an amount of 10 to 50 mol% and R 3 and R 5 are selected such that the homopolymer of C is water-soluble and that unit A is different from unit C. Furthermore, the invention describes printing plates produced therefrom.

Description: The present invention relates to radiation-sensitive compositions as well as to positive working printing plates produced therefrom; in particular, the invention relates to radiation-sensitive compositions which lead to an increased chemical and developer resistance of positive working printing plates and the like. Recently, the resistance of offset printing plates to solvents and common printing room chemicals such as plate cleaning agents or rubber blanket washing agents as well as to alcohol substitutes in the fountain water has had to meet ever increasing demands. Particularly in printing processes using UV-curing inks, where rinsing agents with a high content of esters, ethers or ketones are used, the chemical resistance of conventional positive working printing plates is no longer sufficient without special stabilizing processes. In order to improve the chemical resistance of positive working offset printing plates, three approaches have essentially been discussed. 1) In the most basic case, positive working offset printing plates comprise two components, namely a naphthoquinone diazide derivative (NQD derivative) and a novolak. One possibility is to chemically alter the NQD such that it is imparted an increased chemical and solvent resistance (cf. US-A-5,609,983). The disadvantage of this method is that the resistance of a printing plate produced therefrom cannot be increased indefinitely by increasing the NQD content since the NQD content has to lie in a certain range to make sense from a practical point of view. 2) Another approach is to thermally stabilize a conventional positive working printing plate (based on novolak and NQD). This can be carried out either by "baking" or by means of the Pulsar™ process. During baking, a completely developed printing form is heated to about 230°C for a few minutes causing the mostly phenolic binders to cross-link. This results in an extremely high chemical and mechanical resistance. In the other thermal process (Pulsar™ process), the developed printing plate is subjected to a short-time "shock heating" to about 175°C. This results in a slight cross-linking (and thus an increase in the chemical resistance) of the image areas. For the user, the two thermal stabilizing processes entail the important disadvantage that they require somewhat complicated apparatuses and are therefore quite costly. 3) A third option is the change of the binder content of a radiation-sensitive composition. For example, additives can be added to the formulation. However, in the case of commercially available additives, the amount to be added is often limited since these substances are not adapted to the composition and therefore most of the time affect the properties of the printing plate when added at too high a concentration. Another frequently used method is the use of higher molecular novolaks; however, this leads to a deterioration of the photosensitivity of the composition which leads to a considerable loss of time for the user, particularly in the case of high numbers of prints or when Step & Repeat exposure machines are used. Furthermore, the properties of the binders in the photosensitive composition can be improved by way of chemical modification. Since such special binders with a high degree of chemical resistance are either not commercially available or very pricey (e.g. EP-A-0 737 896), it is often necessary that the manufacturers develop their own binders. In order to avoid high costs in the developing process, efforts have to be made to keep the synthetic requirements for preparing such tailor-made high-performance binders as simple as possible. Therefore, despite intensive research in the field of chemically resistant binders for offset printing plates, the available approaches to solve the problem still leave some improvements to be desired, in particular with respect to binders that can be used more flexibly and are less expensive. It is therefore the object of the present invention to provide radiation-sensitive compostions which significantly increase the chemical resistance of printed circuit boards for integrated circuits, photomasks and in particular printing forms without suffering the disadvantages described above. Furthermore, development with conventional developers should be possible and a high degree of radiation sensitivity, good resolution and quick ink acceptance should be guaranteed; furthermore, the binder to be used should also be inexpensive. It is another object of the present invention to provide processes for the preparation of such radiation-sensitive compositions as well as printing plates produced therefrom. This object is achieved by a radiation-sensitive composition comprising (a) at least one novolak (b) at least one naphthoquinone diazide derivative and (c) a copolymer consisting of the units A, B and C wherein unit A is present in an amount of at least 5 to a maximum of 50 mol% and has the following formula wherein R 1 and R 4 are selected such that the homopolymer of A is alkali-soluble, unit B is present in an amount of 20 to 70 mol% and has the following formula wherein R 2 , R 6 and R 7 are selected such that the homopolymer of B has a high glass transition temperature and unit C is present in an amount of 10 to 50 mol% and has the following formula wherein R 3 and R 5 are selected such that the homopolymer of C is water-soluble, with the proviso that unit C is different from unit A. The printing plate according to the present invention comprises a substrate and a radiation-sensitive layer consisting of a composition as defined above. Figure 1 shows the developer resistance behavior and the photosensitivity of a series of novolak/copolymer mixtures. The NQD content is kept at a constant 21% by weight throughout the series. The dotted line shows the expected curve of the developer resistance, the solid line shows the values found in the experiments. The dashed line shows the photosensitivity (i.e. the free grey scale steps). Figure 2 shows the influence of the unit A content in the copolymer on the developer resistance, photosensitivity and chemical resistance at a constant NQD content of the composition (21% by weight). Figure 3 shows the photosensitivity of the compositions of converted plates with (dotted line) and without (solid line) copolymer P3 as a function of the conversion temperature. The copolymer is a terpolymer, the backbone thereof consists of units A to C, each of which having a certain function in the copolymer. Structural unit A is responsible for the alkali-solubility of the copolymer according to the present invention. As a prerequisite, the homopolymer of monomer A has to be alkali-soluble, it may, however, does not have to be water-soluble. Structural unit B is mainly responsible for a high glass temperature of the copolymer and thus also prevents a rapid penetration of organic solvents. As a prerequisite, the homopolymer of B has to have a high glass transition temperature, preferably above 100°C. Structural unit C ensures a sufficient hydrophilicity of the copolymer so that the copolymer can be developed quickly and completely and that there is no undesired skin formation during the developing process. As a prerequisite, the homopolymer of structural unit C has to be water-soluble which often also entails alkali-solubility. The following applies throughout the application: Unless otherwise defined, the term "alkyl" in this application is intended to signify straight-chain or branched alkyl groups with 1 to 12 carbon atoms, preferably 1 to 4 carbon atoms, the term "cycloalkyl" signifies cycloalkyl groups with 3 to 8 ring-carbon atoms, preferably 5 or 6 ring-carbon atoms, the term "aryl" signifies phenyl, naphthyl, anthryl or an N-substituted carbazole group, and the term "halogen" signifies fluorine, chlorine, bromine or iodine. Unless stated otherwise, the terms "alkyl" and "cycloalkyl" comprise unsubstituted alkyl groups/cycloalkyl groups, as well as alkyl groups/cycloalkyl groups having at least one substituent selected from halogen atoms and -NO 2 . Furthermore, unless stated otherwise, the term "aryl" in the present application is intended to signify unsubstituted aryl groups as well as aryl groups having at least one substituent selected from halogen atoms, alkyl groups and - NO 2 . The term "alkoxy group" comprises alkoxy groups with 1 to 12 carbon atoms; the alkyl unit of the alkoxy groups can be branched, straight-chain or cyclic and may optionally contain one or several substituents selected from -OH, a halogen atom, an alkyl group and an aryl group. Preferably, R 1 is hydrogen, aryl having at least one hydroxy group, and optionally at least one substituent selected from halogen, (C 1 -C 12 ) alkyl and -NO 2 , an arylsulfonamide group (like phenylsulfonamide) or (C 1 -C 12 ) alkyl having at least one carboxy group. Especially preferred, R 1 is hydrogen, hydroxyphenyl or carboxy-(C 1 -C 4 ) alkyl. Preferably, R 4 and R 5 are independently hydrogen, halogen or (C 1 -C 12 ) alkyl. Especially preferred, R 4 is H or -CH 3 ; the same applies for R 5 . R 2 is preferably hydrogen, aryl, optionally having one or several substituents selected from halogen, alkyl, -NO 2 and -OH, alkyl, cycloalkyl, an arylsulfonamide group (like phenylsulfonamide) or a sulfonamide group. Especially preferred, R 2 is hydrogen, phenyl, cyclohexyl or hydroxyphenyl. Preferably, R 6 and R 7 are independently hydrogen, halogen, (C 1 -C 4 ) alkyl or phenyl. Especially preferred, R 6 and R 7 are both hydrogen. Preferably, R 3 is hydrogen, (C 1 -C 12 ) alkyl having at least one hydroxy group and optionally also one or several substituents selected from halogen and -NO 2 , (C 3 -C 8 ) cycloalkyl having at least one hydroxy group and optionally also one or several substituents selected from halogen and -NO 2 , aryl having at least one hydroxy group and optionally one or several substituents selected from halogen, (C 1 -C 12 ) alkyl and -NO 2 , a (C 1 -C 12 ) alkylsulfonamide group, an arylsulfonamide group, -NH(CH 2 ) n O-alkyl (wherein n is an integer from 1 to 20), -NHR 8 (wherein R 8 is hydrogen, (C 1 -C 12 ) alkyl or aryl) or (C 1 -C 12 ) alkoxy. Especially preferred, R 3 is -NH 2 or -CH 2 -CH 2 -OH. The content of monomer unit A in the copolymer of the present invention is at least 5 and at most 50 mol%, based on the copolymer, preferably, the content of A is 7 to 40 mol%, especially preferred 10 to 30 mol%. The content of unit B is 20 to 70 mol%, based on the copolymer, preferably 35 to 60 mol%. The content of unit C is 10 to 50 mol%, based on the copolymer, preferably 20 to 45 mol%. The weight-average molecular weight of the copolymer is preferably 500 to 1,000,000, especially preferred 2,000 to 250,000. The copolymer can be prepared from the monomers A', B' and C' wherein R 1 to R 7 are as defined for A, B and C, by means of known polymerization processes (e.g. solution polymerization, bulk polymerization, emulsion and suspension polymerization). Preferably, a solution containing monomers A', B' and C' is heated and a common initiator is added. It is also possible to add the initiator to the monomer mixture, then add an organic solvent and subsequently heat the resulting solution. An especially preferred monomer A' is methacrylic acid. Especially preferred monomers B' are N-phenylmaleimide and N-cyclohexylmaleimide. Especially preferred monomers C' are methacrylamide and N-methoxymethyl methacrylate. The copolymer can be used both as a "stand-alone" binder and as an additive, i.e. in addition to one or several further binder in the radiation-sensitive compositions of the present invention. The preparation of the copolymer is inexpensive and it can synthetically easily be adapted to the individual compositions, i.e. independently of whether it is used as a "stand-alone" binder or as an additive, it can be adapted accordingly. The printing forms of the present invention which are produced with such radiation-sensitive compositions are characterized by their high degree of chemical resistance, i.e. resistance to printing room chemicals and developers. In order to take full advantage of the favorable properties of the radiation-sensitive compositions it is reasonable to adapt the copolymers to their intended use, i.e. whether they are used as an additive or as a stand-alone binder. This adaptation can easily be effected for example by modifying the monomer A content, which above all influences the alkali-solubility. If the intended use is as a resistance-increasing additive in a common positive working formulation, a higher content of unit A in the copolymer is recommended, preferably 20 to 40 mol%, than for a use as stand-alone binder for UV ink printing plates (preferably 5 to 20 mol%). In this connection, an important effect shown only by this group of copolymers plays a decisive role. The effect will be described in more detail below. The basic working principle of a positive working system such as for example a printing plate are the different rates at which exposed and unexposed image areas dissolve in the developer. Ideally, the exposed areas should dissolve as quickly as possible and the unexposed areas should not dissolve at all. The dissolution rate of the exposed elements determines the photosensitivity (or "speed") of a printing plate; the dissolution rate of the unexposed plate is the developer resistance. In practical applications, most of the time 1 to 4 minutes elapse between the point when the exposed areas are completely developed and the point when the unexposed areas are dissolved by the developer. This time period is also referred to as developer margin. In the case of especially aggressive developers, this margin can be considerably reduced so that it is often only slightly longer than the actual developing time (15-30 s). In the radiation-sensitive compositions of the present invention, the copolymers in combination with novolaks and naphthoquinone diazide derivatives are able to markedly increase the developer margin without reducing the photosensitivity at the same time. As is shown in Fig. 1, the maximum developer resistance (solid line) occurs in the middle of a series of novolak/copolymer mixtures. This nonlinear behavior clearly differs from the expected curve (dotted line). In contrast, the photosensitivity (dashed line) of the mixture series does not show a minimum, which would be expected, since formulations having a high developer resistance are generally less photosensitive. This phenomenon of a resistance maximum does not occur in a mixture of novolak/copolymer lacking the NQD; in that case, a linear curve is obtained. Since all three components, i.e. novolak, copolymer and NQD, show an insolubilisation synergy in this effect, the effect is also referred to as "cross-insolubilisation" in the following. If one starts from a composition comprising only the copolymer and NQD and keeps adding increasing amounts of novolak, the developer resistance increases. This is of particular interest for printing plates which are employed in UV ink printing; compositions suitable therefor require the highest possible chemical resistance and a favorable developer margin. In the case where it is merely intended to improve the chemical resistance of radiation-sensitive compositions based on novolak and NQD by means of the copolymer additive, it is recommended to increase the amount of unit A in the copolymer (see Fig. 2). If a polymer with a low unit A content is used (e.g. 15 mol%), the plate's photosensitivity is affected (as in Fig. 2a). Although the binder as a stand-alone binder together with an NQD (see Fig. 2b) shows hardly any developer resistance in a composition, the "cross-insolubilisation" effect makes it possible that at a content of up to 50% copolymer (based on the total amount of copolymer and novolak), good developer resistance is obtained without a decisive decrease in photosensitivity if the unit A content is increased (e.g. to 20% or more). In the case of common commercial additives (e.g. cellulose acetate hydrogenphthalate) containing a high amount of alkali-soluble groups for increasing the chemical resistance a rapidly falling curve of developer resistance would result, as shown in Fig. 2b by the dotted line. However, due to the "cross-insolubilisation" effect, the copolymers are able to keep both photosensitivity and developer resistance constant over a wide range; it is not until very high copolymer contents are reached that the system "overturns". The special copolymers provide a significantly increased formulation margin compared to common resistance-increasing additives. The resistance to aggressive chemicals is significantly increased, as can be inferred from Fig. 2b (in some cases 100-fold). In the photosensitive compositions it is irrelevant for the resistance to printing room chemicals whether the polymeric binder comprises a high or low content of e.g. unit A. Furthermore, it was found that such positive working radiation-sensitive compositions, if they are convertible (also: reversible), show a markedly broadened conversion margin. In the tested cases, the conversion temperature could also be lowered which constitutes a practical advantage because oxidation and cross-linking processes at higher temperatures no longer occur. The copolymers make it possible to drastically increase the chemical resistance to, e.g., printing room chemicals, of a positive working system such as e.g. a printing plate without affecting photosensitivity and developer resistance. On the other hand, these copolymers can also be employed as main binder component in a positive working printing plate of the highest chemical resistance for UV-curing inks. The ability of the copolymers to induce an insolubilisation synergism ("cross-insolubilisation effect) together with novolak and NQD is the key to this extremely flexible applicability. As novolaks, all the polycondensation products from formaldehyde and phenols, obtained from acid catalysis or neutral catalysts, which are known to the person skilled in the art can be used. All naphthoquinone diazide derivatives known to the person skilled in the art can be used. Examples include the ester from naphthoquinone-1,2-diazido-5-sulfonic acid chloride or -4-sulfonic acid chloride and 2,4-dihydroxybenzophenone or 2,3,4-trihydroxybenzophenone. In the present invention, it is not necessary to use novolak(s) and naphthoquinone diazide derivative(s) as separate components; naphthoquinone diazide derivative(s) reacted with novolak(s) can also be employed (which is referred to as "two-in-one" systems). The weight ratio of novolak to copolymer in the inventive composition is preferably in the range of 90:10 to 10:90. As a principle, the copolymer can be admixed in any ratio with a common positive working composition on the basis of NQD and novolak. At a ratio of novolak/copolymer of almost 100/0 to about 60/40 (% by weight), the copolymer can still be called an additive. A positive working printing plate according to the present invention produced therefrom shows a significantly improved chemical resistance compared to a printing plate whose photosensitive composition does not comprise the copolymer. If compositions with a novolak/copolymer ratio of about 40/60 to almost 0/100 (% by weight) are used for the production of positive working printing plates according to the present invention, printing plates of the highest chemical resistance are obtained which are perfectly suitable for printing processes using UV-curing inks. In addition to the essential components (copolymer, novolak and NQD), the radiation-sensitive compositions of the present invention can furthermore comprise one or more additional components selected from radiation-sensitive acid donors, dyes or pigments for increasing the contrast of the image, exposure indicators, plasticizers and mixtures thereof. The exposure indicators suitable for use in the radiation-sensitive compositions are known to the person skilled in the art. Exposure indicators selected from triarylmethane dyes (such as Victoria Pure Blue BO, Victoria Blue R, crystal violet) or azo dyes (such as 4-phenylazodiphenylamine, azobenzene or 4-N,N-dimethylaminoazobenzene) are preferred. The exposure indicators may be present in the composition in an amount from 0.02 to 10% by weight, especially preferred in an amount from 0.5 to 6% by weight. Suitable dyes for increasing the contrast of the image include those which dissolve well in the solvent or solvent mixture used for the coating or which can be introduced as a pigment in particulate form. Suitable contrast dyes include, i.a., rhodamine dyes, methyl violet, anthraquinone pigments and phthalocyanin dyes or pigments. Suitable plasticizers include dibutylphthalate, triarylphosphate and dioctylphthalate. Dioctylphthalate is especially preferred. The plasticizer is preferably used in an amount of 0.25 to 2% by weight. Based on the total weight, the radiation-sensitive composition preferably comprises 2 to 90% by weight of the copolymer, more preferably 7 to 80% by weight and most preferred 10 to 70% by weight. The photosensitive compositions can be used in the production of printing forms (in particular offset printing plates), printed circuit boards for integrated circuits and photomasks. The carrier to be used for the printing plate of the present invention is preferably a material in the form of a sheet or a film, having a good dimensional stability. As such a dimensionally stable sheet or film material, use is preferably made of a material that has already been used as a carrier for printed matter. Examples of such carriers include paper, paper coated with plastic materials (such as polyethylene, polypropylene, polystyrene), metal sheets or foils, such as e.g. aluminum (including aluminum alloys), zinc and copper sheets, plastic films made from e.g. cellulose diacetate, cellulose triacetate, cellulose propionate, cellulose acetate, cellulose acetate butyrate, cellulose nitrate, polyethyleneterephthalate, polyethylene, polystyrene, polypropylene, polycarbonate and polyvinylacetate, and a laminate comprising paper or a plastic film and one of the above-mentioned metals, or a paper/plastic film which has been metallized by chemical vapor deposition. Among these carriers, an aluminum sheet or foil is especially preferred since it has a remarkable dimensional stability, is inexpensive and furthermore shows an excellent adhesion of the radiation-sensitive layer. Furthermore, a composite film can be used wherein an aluminum foil has been laminated onto a polyethyleneterephthalate film. A metal carrier, in particular an aluminum carrier, is preferably subjected to a surface treatment, for example graining by brushing in a dry state, brushing with abrasive suspensions or electrochemically, e.g. in a hydrochloric acid electrolyte, and optionally to anodic oxidation. Furthermore, in order to improve the hydrophilic properties of the surface of the grained metal carrier which has optionally been anodically oxidized in sulfuric or phosphoric acid, it is subjected to an aftertreatment in an aqueous solution of sodium silicate, calcium zirconium fluoride, polyvinyl phosphonic acid or phosphonic acid. The details of the above-mentioned pretreatment of the substrate are well known to the person skilled in the art. The subsequently dried plates are coated with the radiation-sensitive layers of organic solvents or solvent mixtures such that dry layer weights preferably in the range of 0.5 to 4 g/m 2 , especially preferred 0.8 to 3 g/m 2 are obtained. In some cases it may be advantageous to additionally apply an oxygen- and/or moisture-blocking overcoat on the radiation-sensitive layer. The printing plates of the present invention thus produced are exposed and developed by means of common processes known to the person skilled in the art. The developed plates are usually treated with a preservative ("rubber coating"). The preservatives are aqueous solutions of hydrophilic copolymers, wetting agents and other known additives. The invention will be described in more detail with reference to the examples below which, however, should not be understood as limiting the present invention in any way. Examples Synthesis Example: The monomers listed in Table 1 were used to prepare copolymers. For polymerization, the monomers were provided in a flask with a stirrer and nitrogen inlet at 60°C in methylglycol (total monomer concentration: 2.5 mol/l) and 0.1 mol% azobisisobutyronitrile was added as initiator. Reprecipitation was carried out in three times the amount of methanol. The obtained copolymers were dried for 48 h at 50°C. Copolymers CP1, CP2, CP3 and CP4 are comparative copolymers. Copolymers P1 - P6 can be prepared very inexpensively; the costs for the monomer raw material lie in the range of 5 - 25 DM/kg. Also, there is not much solvent waste since high concentrations and little precipitator are used. In the case of the comparative copolymers CP2 and CP3, the costs for the raw materials are considerably higher, in particular the APK monomer in CP2 has to be prepared in a complicated manner via the expensive intermediate methacryloyloxyethylisocyanate. Preparation Example 1: The copolymers obtained in the Synthesis Example were added to positive working radiation-sensitive standard compositions for printing plates. In addition to a naphthoquinone diazide and a novolak, these standard compositions also comprise a photosensitive acid donor and a pigment for increasing the contrast of the image between exposed and unexposed areas (see Table 2). Standard compositions with the copolymers from Table 1 (in % by weight) Ratio copolymer:novolak No. A0 Reference (0% copolymer) No. A1 20/80 copolymer/novolak No. A2 40/60 copolymer/novolak No. A3 60/40 copolymer/novolak No. A4 80/20 copolymer/novolak No. A5 100/0 copolymer/novolak Ester from naphthoquinone-1,2-diazido-5-sulfonic acid-chloride and 2,4-dihydroxy-benzophenone (85% reacted) 21.0 21.0 21.0 21.0 21.0 21.0 Cresol/formaldehyde novolak resin (meta:para=75/25), Mw=7,000 76.6 61.3 46.0 30.6 15.3 - - - Copolymer from Table 1 - - - 15.3 30.6 46.0 61.3 76.6 2,4-Trichloromethyl-6[1(4-methoxy)-naphthyl)]1,3,5-triazine 1.0 1.0 1.0 1.0 1.0 1.0 Ethyl violet (triphenylmethane dye) 1.4 1.4 1.4 1.4 1.4 1.4 From charges A0 to A5, the solids components are dissolved with methylglycol to give a 10% solution. After filtration of the solution, it is applied by means of a common process to an electrochemically grained and anodized aluminum foil which has been subjected to an aftertreatment with polyvinyl phosphonic acid and is dried, at first without air supply and heating. Final drying took place for 5 minutes at 100°C. The dry layer weight was 2 g/m 2 in all cases. The copying layer is exposed by means of a metal halide lamp (MH-Burner 5,000W, company Sack) with 800 mJ/cm 2 under a silver film half-step scale (UGRA grey scales) with a density range of 0.15 to 1.95, wherein the density increments are 0.15, as a positive copy. The exposed layer is treated for 15 s with a developer solution consisting of 87.79 % by weight demineralized water 9.20 % by weight soda waterglass 2.10 % by weight sodium hydroxide 0.90 % by weight ethylene glycol 0.01 % by weight tetramethylammoniumchloride (50% aqueous solution) Subsequently, the developer solution is again rubbed onto the surface with a wet cloth for 5 s and then the entire plate is rinsed with water. After this treatment the unexposed areas remain on the plate. In order to evaluate photosensitivity and ink acceptance of the plate, the wet plate is blackened with printing ink. The products PC 904™ (company Polychrome) and RC 43™ (company Hoechst) were used as printing ink. The results are shown in Table 3. Regarding the entries in the table marked "soak loss", an evaluation was not possible because these samples had already been attacked by the developer. Photosensitivity of the plate formulations from Table 2 (UGRA step free) Copolymer No.A0 Reference (0% copolymer) No. A1 20/80 copolymer/novolak No. A2 40/60 copolymer/novolak No. A3 60/40 copolymer/novolak No. A4 80/20 copolymer/novolak No.A5 100/0 copolymer/novolak P1 5 4 2 2.5 2.5 2.5 P3 5 5 5 6 soak loss soak loss P4 5 6 soak loss soak loss soak loss soak loss CP1 5 6 soak loss soak loss soak loss soak loss CP2 5 4 4 3.5 3.5 3.5 CP3 5 5.5 soak loss soak loss soak loss soak loss CP4 5 3.5 1.5 < 1 <1 <1 As can be inferred from Table 3, copolymer P3 shows a constant photosensitivity beyond a novolak/P3 ratio of higher than 40/60 [% by weight]. Thus, this copolymer is particularly suitable as an additive for increasing the chemical and solvent resistance without having a negative effect on the developer resistance and photosensitivity (which will be explained further in Table 4). The comparative copolymers CP1 and CP3 show a weak developer resistance which limits their application range in the plate; a formulation may not contain more than 20%. CP4 requires high exposure times in a formulation. In order to examine developability of the exposed layer and to be able to compare it with other formulations, the following steps are carried out: at intervals of 5 s, the above developer solution is applied streak-wise to the exposed plate by means of a pipet. After a dwell time of 20 s, the entire plate is quickly rinsed with water, blackened with printing ink and then dried. The time period of developer action after blackening is determined after which the layer no longer accepts ink (in the following, this test is referred to as drop test). In all samples A0-A5, the plate was completely developed after only 5 seconds. In order to examine the developer resistance of the unexposed layer (the image areas), the above developer solution is applied streak-wise to an unexposed plate at intervals of 30 s by means of a pipet. After a dwell time of 4 min, the entire plate is quickly rinsed with water. If necessary, this time period can also be extended. The point of time of developer action is determined at which the layer shows clear light areas (in the following, this test is referred to as soak test). Table 4 shows the developer resistance of positive working formulations from Table 2 with different copolymers of Table 1 at different novolak/copolymer ratios. Developer resistance in [min] using the different copolymers from Table 1 No. A0 Reference (0% copolymer) No. A1 20/80 copolymer/novolak No. A2 40/60 copolymer/novolak No. A3 60/40 copolymer/novolak No. A4 80/20 copolymer/novolak No. A5 100/0 copolymer/novolak P1 3 4 8 8 4 2 P3 3 4 3 1 <1 <1 P4 3 3 2 <1 <1 <1 CP1 3 2 2 <1 <1 <1 CP2 3 4 3 3 2 2 CP3 3 2 <1 <1 <1 <1 CP4 3 3 3 2 2 2 In order to evaluate the resistance of the photosensitive layer to aggressive, mostly alcohol-containing washing agents (e.g. film and glass cleansers and, in the printing room, cleansers for printing forms, rubber blankets and rolls), a laboratory test washing agent (WA) is used. This test allows reliable statements regarding the chemical resistance to other organic solvents. The composition of the test washing agent is as follows: 20% by weight isopropanol (water content below 0.1%), 85% by weight gasoline 135/180 (also referred to as type K21) and 1% by weight water. The final water content is determined by means of the Karl Fischer technique and may vary by ±0.1%. The test is carried out as follows: The upper third of a printing plate sample with a size of about 10 x 10 cm is exposed and immersed in a dry Petri dish which is filled with the washing agent and held at a temperature of ∼25°C. At intervals of 1, 2, 3 and 4 min (if necessary, this time period can also be extended), a cloth is rubbed over the sample from top to bottom, exerting pressure. The unexposed half is evaluated. The time period (in minutes) is determined after which a clear loss of contrast can be observed (a loss of contrast of about 30%). Only in cases where the exposed part shows resistance for more than 0.5 min, this value is noted down as well. In order to evaluate the resistance of the photosensitive layer to extremely aggressive rinsing agents which most of the time contain high amounts of solvents (ethers, ester, ketones and the like) as used in printing with UV-curing inks, a laboratory test washing agent is used. The composition of the test washing agent is as follows: 80% by weight diacetone alcohol (DAA) and 20% by weight water. The test is carried out as follows: The upper third of a printing plate sample with a size of about 18 x 6 cm is exposed and the above UV washing agent is applied streak-wise by means of a pipet at intervals of 30 seconds. After a dwell time of 2 min, the entire plate is quickly rinsed with water and rubbed with a moist cloth. If necessary, this time period can be extended. The point of time of action is determined at which the layer shows clear light areas. In cases where two samples show the same resistance on the unexposed part, the value of the exposed third is also taken into consideration. Table 5 shows the chemical resistance of the individual compositions to common plate washing agents. The individual mixture series were divided for the washing agent tests: Mixtures with a copolymer/novolak ratio of 0/100 up to and including 40/60 % by weight were treated with the "normal" gasoline-containing rinsing agent. Samples with still higher copolymer contents showed too high a resistance to be evaluated with the test washing agent within a reasonable period of time. The resistance of samples with a copolymer/novolak ratio of 60/40 to 100/0 % by weight was tested with the UV washing agent. Here, it made little sense to also examine samples having a copolymer content of < 60% by weight since they were attacked too early to be evaluated in a reasonable manner. Resistance to plate washing agents in [min] No.B0 Reference (0% copolymer) No. B1 20/80 copolymer/novolak No. B2 40/60 copolymer/novolak No. B3 60/40 copolymer/novolak No. B4 80/20 copolymer/novolak No.B5 100/0 copolymer/novolak gasoline-containing washing agent DAA/Water P1 < 1 16 >> 16 2 2 >2 P3 < 1 16 >> 16 2 - - P4 < 1 14 >> 16 - - - CP1 < 1 6 11 - - - CP2 < 1 4 8 2 2 >2 CP3 < 1 2 - - - - CP4 < 1 5 6 < 0.5 < 0.5 < 0.5 As shown in the table, the chemical resistance of the inventive copolymers is very high whereby the different contents of methacrylic acid in the copolymers has little influence on the resistance properties. The chemical resistance of the comparative copolymers is significantly lower. The panels that have been left blank were not evaluated since these plates do not have sufficient developer resistance (see Table 4). Printing tests: As described in Preparation Example 1, for preparing a printing plate a copying layer is applied to the aluminum substrate, exposed, developed and after rinsing with water the plate is squeezed and rubbed with an aqueous solution of 0.5% phosphoric acid and 6% gum arabic. The thus produced plate is mounted in a sheet-fed offset press (type Favorit, MAN Roland) and printing is carried out under the usual conditions. During printing, the machine is stopped after every 10,000 turns and the plate is washed with a plate washing agent consisting of 85% by volume gasoline and 15% by volume isopropanol. The obtained numbers of copies of some plates of Preparation Example 1, Table 1, are shown in Table 6. Obtained numbers of copies of Preparation Example 1, Table 2 Sample Copies A0 without copolymer 70,000 A1 with copolymer P3 90,000 A1 with copolymer CP2 80,000 In order to examine the resistance to aggressive alcohol substitutes in the fountain water, a high-concentrated substitute (5% Substifix™ + 5% isopropanol) was used in the fountain water. The numbers of copies of some plates from Preparation Example 1, Table 1, obtained with this type of fountain water are shown in Table 7. Obtained numbers of copies when using especially aggressive fountain water Sample Copies A0 without copolymer 70,000 A1 with copolymer P3 120,000 A1 with copolymer CP2 100,000 In order to examine the resistance of the printing forms to UV-curing inks, the plate was washed every 10,000 turns with an aggressive washing agent instead of a normal plate washing agent. The obtained numbers of copies of some plates of Preparation Example 1, Table 1, are shown in Table 8. Obtained numbers of copies when using an aggressive UV-curing ink washing agent from Preparation Example 1, Table 2 Sample Copies A0 without copolymer 10,000 A4 with copolymer P1 120,000 A5 with copolymer CP2 110,000 In all three cases it became apparent that the numbers of copies of plates with the inventive copolymers is considerably higher than that of printing plates not comprising a copolymer or the comparative copolymers. Compared to CP2, copolymer P1 is superior, which is all the more important since the production costs of P1 are about ten times lower than those of CP2. Baking tests: For thermal stabilization (baking) of the samples, they were heated in an oven to 250°C for 8 minutes. For determining the mechanical abrasion resistance, the printing plates were subjected to an abrasion test. During that test, a cloth soaked with an aqueous abrasive suspension rubs over the plate in an oscillating movement for a defined period of time (15 min). The lower the weight loss in this process, the higher the mechanical resistance of a sample. By selecting the abrasive emulsion accordingly, this test was adjusted such that it allowed a qualitative prediction of the number of copies yielded by the printing plate in a printing press. The mechanical stability is determined indirectly by means of a chemical test. For this purpose, a correction fluid for positive working plates (type 243, Kodak Polychrome) is left to react with the layer for 15 min. If no attack can be observed, the cross-linking of the binder components and thus the chemical (and mechanical) resistance is sufficient. The results of the tests described above are shown in Table 9. Mechanical and chemical resistance of the plates (formulations from Table 2) Sample Weight loss [g/m 2 ] non-baked samples Weight loss [g/m 2 ] baked samples correction fluid test [min] A0 without copolymer 0.85 0.73 > 15 A4 with P1 0.82 0.80 2 - 3 A1 with P3 0.78 0.65 > 15 Sample A4 with P1, as it were, represents a UV-curing ink printing plate, Sample A1 with P3 represents a highly washing agent resistant conventional positive working plate. It is interesting that while the UV-curing ink plate (Sample P1) has reached the same mechanical strength as a normal positive working printing plate, it still corresponds to correction fluids. This represents an almost ideal behavior: the printing plate shows the highest possible mechanical strength, but can still be corrected. This property is very user-friendly since it also allows the correction of a plate which has already been baked and which otherwise would have had to be discarded. Preparation Example 2: In order to demonstrate that the inventive copolymers are not only geared to a certain type of novolak or NQD, the corresponding components from Table 2 were replaced by differently structured derivatives as shown in Tables 10 to 12. The copolymer in this series was not modified; P1 was used in all formulations. Naphthoquinone diazides polymer-analogously esterified with a novolak (grafted) constitute a special case, i.e. this class of substances already carries the NQD in the main chain of the novolak so that it is not necessary to incorporate NQDs. Thus, those two substances not only replace the novolak part but additionally also the NQD part of the formulations in Table 2. In this connection, it has to be kept in mind that an addition of copolymer to the composition automatically decreases the NQD content, which is not the case in other compositions. Therefore, it does not make sense to examine formulations comprising more than 60% copolymer. As can be inferred from Table 10, a markedly increased developer resistance can be observed in the medium range of novolak/copolymer ratios (similarly as shown in Fig. 2a). This shows that the inventive copolymers exhibit a "cross-insolubilisation" effect with differently structured novolaks as well. In short-chain novolaks, the a "cross-insolubilisation" effect is somewhat less pronounced than in the long-chain varieties. As can be inferred from Table 11, at an increasing copolymer/novolak ratio, all novolaks show a similar behavior in the course of the exposure times. As can be inferred from Table 12, at least starting at a copolymer content of about 40% all samples are sufficiently resistant to the test washing agent. Preparation Example 3: In positive working compositions as used in convertible printing plates, the inventive copolymers exhibit an expansion of the conversion margin and a decrease of the lower conversion temperature. Two different systems are shown in Tables 13 and 15 and the results are shown in Tables 14 and 16. Influence of the copolymers on the conversion properties (weight of sample in [g]) Reference without copolymer with P3 with CP2 Ester of a low-molecular novolak with 1,2-naphthoquinone diazide-4-sulfonic acid 21.00 21.00 21.00 Cresol/formaldehyde novolak resin (meta : para=75/25), Mw=7,000 77.00 57.40 57.40 P3 - - - 20.60 - - - CP2 - - - - - - 20.60 2,4-Trichloromethyl-6[1(4-methoxy)-naphthyl)]1,3,5-triazine 0.50 0.50 0.50 Ethyl violet (triphenylmethane dye) 1.50 1.50 1.50 The compositions of Table 13 were used to coat plates, the plates were exposed and then tempered for 5 min at different temperatures as shown in Table 14. Subsequently, the printing plate was subjected to overall exposure. Then the plate was developed. Conversion properties of the compositions from Table 13 115°C 125°C 135°C 145°C 155°C Reference - +/- + + n.d. + P3 - + + + n.d. + CP2 - - + n.d. n.d. -: developer resistance of the converted layer too weak +: optimum conversion n.d. : plate cannot be completely developed Compared to the reference sample, the sample with copolymer P3 shows an expanded conversion margin shifted towards lower temperatures. If only for the narrow margin in which conversion is possible, the sample with the reference polymer is only conditionally recommended for this purpose. The photosensitivity of the formulation with the inventive copolymer as well has been improved compared to the reference sample: The solid steps in the UGRA grey step show about one more grey scale (on the converted side). The sample with the comparative polymer was not taken into account. Influence of the copolymers on the conversion properties (given in % by weight) Reference without copolymer with P1 with CP2 2,1,4-NQD, polymeranalog esterified with a cresol/phenol/formaldehyde novolak (Mw=4,000) (reacted ∼6%) 97.60 82.00 82.00 P1 - - - 15.60 - - - CP2 - - - - - - 15.60 2,4-Trichloromethyl-6[1(4-methoxy)-naphthyl)]1,3,5-triazine 1.00 1.00 1.00 Ethyl violet (triphenylmethane dye) 1.40 1.40 1.40 The compositions of Table 15 were used to coat plates, the plates were exposed and then tempered for 5 min at different temperatures as shown in Table 16. Subsequently, the printing plate was subjected to overall exposure. Then the plate was developed. Conversion properties of the compositions from Table 15 115°C 125°C 135°C 145°C 155°C Reference - - + + n.d. + P1 - +/- + + n.d. + CP2 - - + n.d. n.d. -: developer resistance of the converted layer too weak +: optimum conversion n.d.: plate cannot be completely developed Compared to the reference sample, the sample with copolymer P1 shows an expanded conversion margin shifted towards lower temperatures. This is consistent with the findings in Table 14. If only for the narrow margin in which conversion is possible, the sample with the reference polymer is only conditionally recommended for this purpose. The photosensitivity of the formulation with the inventive copolymer as well has been improved compared to the reference sample: The solid steps in the UGRA grey step show about one more grey scale (on the converted side). The sample with the comparative polymer was not taken into account. In Fig. 3, the solid UGRA grey scale steps are shown as an indication of the photosensitivity of the compositions (from Tables 14 and 16) with the inventive copolymer (dotted line) and without the inventive copolymer (solid line). It can be inferred from Fig. 3 that the formulations comprising the inventive copolymer exhibit a broader and more gradual working range. Thus, the temperature margin for conversion is larger. The samples without copolymer show a relatively regular increase in photosensitivity at increasing temperatures, which is less desirable from a practical point of view.

Claims: Radiation-sensitive composition comprising (a) at least one naphthoquinone diazide derivative, (b) at least one novolak and (c) a copolymer consisting of the units A, B and C wherein unit A is present in an amount of 5 to a maximum of 50 mol% and has the following formula wherein R 1 and R 4 are selected such that the homopolymer of A is alkali-soluble, unit B is present in an amount of 20-70 mol% and has the following formula wherein R 2 , R 6 and R 7 are selected such that the homopolymer of B has a high glass transition temperature and unit C is present in an amount of 10-50 mol% and has the following formula wherein R 3 and R 5 are selected such that the homopolymer of C is water-soluble, with the proviso that unit C is different from unit A. Radiation-sensitive composition according to claim 1 wherein the weight ratio novolak/copolymer is in the range of 90:10 to 10:90. Radiation-sensitive composition according to claim 2 wherein the copolymer is present in an amount of at least 60 % by weight based on the total amount of copolymer and novolak. Radiation-sensitive composition according to any of claims 1 to 3 wherein the composition does not comprise an additional binder. Radiation-sensitive composition according to any of claims 1 to 4 wherein the composition additionally comprises at least one further component selected from radiation-sensitive acid donors, dyes or pigments for increasing the contrast of the image, exposure indicators and plasticizers. Radiation-sensitive composition according to any of claims 1 to 5 wherein R 1 in unit A of the copolymer is hydrogen, aryl having at least one hydroxy group and moreover optionally having at least one substituent selected from the group consisting of halogen, (C 1 -C 12 ) alkyl and -NO 2 , arylsulfonamide or (C 1 -C 12 ) alkyl having at least one carboxy group. Radiation-sensitive composition according to any of claims 1 to 6 wherein R 4 in unit A and R 5 in unit C independently are hydrogen, halogen or (C 1 -C 12 ) alkyl. Radiation-sensitive composition according to any of claims 1 to 7 wherein R 2 in unit B of the copolymer is hydrogen, aryl optionally having at least one substituent selected from the group consisting of halogen, (C 1 -C 12 ) alkyl, -NO 2 and -OH, (C 1 -C 12 ) alkyl, (C 3 -C 8 ) cycloalkyl, arylsulfonamide or sulfonamide. Radiation-sensitive composition according to any of claims 1 to 8 wherein R 3 in unit C of the copolymer is hydrogen, (C 1 -C 12 ) alkyl having at least one hydroxy group and optionally one or several substituents selected from the group consisting of halogen and -NO 2 , (C 3 -C 8 ) cycloalkyl having at least one hydroxy group and optionally one or several substituents selected from the group consisting of halogen and -NO 2 , aryl having at least one hydroxy group and optionally one or several substituents selected from the group consisting of halogen, (C 1 -C 12 ) alkyl and -NO 2 , (C 1 -C 12 ) alkylsulfonamide, arylsulfonamide, -NH(CH 2 ) n O alkyl (wherein n is an integer of 1-20), -NHR 8 (wherein R 8 is hydrogen, (C 1 -C 12 ) alkyl or aryl) or a (C 1 -C 12 ) alkoxy group. Radiation-sensitive composition according to any of claims 1 to 9 wherein R 6 and R 7 in unit B of the copolymer independently are hydrogen, halogen, (C 1 -C 4 ) alkyl or phenyl. Radiation-sensitive composition according to any of claims 1 to 10 wherein the copolymer has a weight-average molecular weight in the range of 500 to 1,000,000. Radiation-sensitive composition according to any of claims 1 to 11 wherein novolak(s) and naphthoquinone diazide derivative(s) are not used as separate components but in the form of naphthoquinone diazide derivative(s) reacted with novolak(s). Use of a radiation-sensitive composition according to any of claims 1 to 12 for producing printing plates, printed circuit boards for integrated circuits and photomasks. Method for the preparation of a radiation-sensitive composition according to any of claims 1 to 12 comprising mixing at least one novolak, at least one naphthoquinone diazide derivative and a copolymer as defined in any of claims 1 and 6 to 12 in the desired ratio and subsequently dissolving the solids components in an organic solvent. Method for the preparation of a radiation-sensitive composition according to any of claims 1 to 12 comprising dissolving the individual components separately in an organic solvent and subsequently mixing the solutions. Printing plate comprising a substrate and a radiation-sensitive composition wherein the radiation-sensitive composition is defined as in any of claims 1 to 12. Printing plate according to claim 16 wherein the substrate is an aluminum substrate which has optionally been subjected to a pre-treatment or a polyethyleneterephthalate substrate having a hydrophilic surface. Method for producing a printing plate according to claim 16 or 17 comprising (a) providing a substrate and optionally subjecting the substrate to a pre-treatment, (b) preparing a solution of the radiation-sensitive composition in an organic solvent, (c) applying the solution prepared in step (b) to the substrate and (d) drying.

Inventors: HAUCK GERHARD, JAREK MATHIAS, HAUCK, GERHARD, JAREK, MATHIAS
Applicants: KODAK POLYCHROME GRAPHICS GMBH
Application year: 2000
Main classification: G03F7
IPC codes: C08L33, C08F222, C08L35, B41N1, G03F7, C08K5, C08F220, C08L61