A NEW FAMILY OF CONDUCTING LIQUID CRYSTALS

Abstract: A mixture comprising a molecule of formula (I); in which A1, A2, A3, A4, A5 and A6, which may be the same or different, are each N or -CH; Y1, Y2, Y3, Y4, Y5 and Y6, which may be the same or different, are each hydrogen or C1 to C12 alkoxy; X1, X2, X3, X4, X5 and X6, which may be the same or different, are each hydrogen, C1 to C12 alkoxy or alkyl C1 to C12; and R7, R8, R9, R10, R11 and R12 are each hydrogen, or each of R7 and R8, R9 and R10 and R11 and R12 may form a bond; and a molecule of formula (II); in which R1, R2, R3, R4, R5 and R6, which may be the same or different, are each alkyl or substituted (and/or chiral) alkyl C1 to C16, acyl C1 to C16, polyethyleneoxy, a flexible connection to a polymer backbone or part of a polymer backbone in homopolymers, copolymers or block copolymers; and B1, B2, B3, B4, B5 and B6a, which may be the same or different, are each, hydrogen, alkyl C1 to C16, alkoxy C1 to C16, nitro, halogeno, cyano, amido, diazo or ester, e.g. alkyl C1 to C16 ester.

Description: A New Family of Conducting Liquid Crystals This invention relates to novel mixtures of compounds and, in particular, novel mixtures that exist as discotic liquid crystals and which have significantly improved liquid crystal and conductive properties. The invention also relates to certain novel compounds per se. Several potential applications of discotic liquid crystals which are based on a combination of their processability and their ability to act as semiconductors have already been described. These include their use as (1) conducting interconnects in stacked silicon chip systems (2) as conducting layers in photoreproductive and electrophotographic systems (3) as active elements in electronic 'nose' arrays (4) as conductive elements in spatial light modulators and many others and as (5) electron/hole transporting materials in light emitting diodes. Thus according to the main feature of the invention we provide a mixture comprising a molecule of formula I; Formula in which A\, A 2 , A 3 , A , A 5 and A 6 , which may be the same or different, are each N or -CH; Yi, Y 2 , Y 3 , Y 4 , Y 5 and Y 6 , which may be the same or different, are each hydrogen or Ci to Cι 2 alkoxy; Xi, X 2 , X , X 4 , X5 and X 6 , which may be the same or different, are each hydrogen, C| to C 12 alkoxy or alkyl Ci to C 12 ; and R 7 , R 8 , R9, Rio, Rn and Rι 2 are each hydrogen, or each of R 7 and R 8 , R 9 and Rio and Rn and Rj may form a bond; and a molecule of formula II; Formula II in which Ri, R 2 , R 3 , R , R 5 and R 6 , which may be the same or different, are each alkyl or substituted (and/or chiral) alkyl Ci to 6 , acyl C \ to Cι 6 , polyethyleneoxy, a flexible connection to a polymer backbone or part of a polymer backbone in homopolymers, copolymers or block copolymers; and Bi, B , B 3 , B 4 , B 5 and B 6 a, which may be the same or different, are each, hydrogen, alkyl to Cι 6 , alkoxy Ci to C i6 , nitro, halogeno, cyano, amido, diazo or ester, e.g. alkyl Ci to Cι 6 ester. By the term "mixture" we mean a combination of compounds of formula I and formula II. In such combinations, quadrupolar attractions and van der Waals forces, between compounds of formula I and compounds of formula II suggests that the mixtures exist as compounds per se. Thus, any reference to mixtures of compounds of formula I and II should be construed accordingly. In a preferred mixture of the invention, in the compound of formula I each of Ai, A , A 3 , A 4 , A 5 and A 6 are the same. When each of Ai, A 2 , A 3 , A 4 , A 5 and A 6 is N, then each of Y Y 2 , Y 3 , Y 4 , Y 5 and Y 6 preferentially represents hydrogen or alkoxy C 3 to C 8 . Further, when each of Ai, A , A 3 , A 4 , A 5 and A 6 is N, then each of Xj, X 2 , X 3 , X , X 5 and X is preferably C 2 to C) alkyl or C 4 to Cι alkoxy, more preferably C 6 to C 9 alkyl or C to C 9 alkoxy. Most preferably, when each of A], A 2 , A 3 , A 4 , A 5 and A 6 is N, then each of Xi, X , X , X 4 , X 5 and X 6 is either C 9 alkyl or C 6 alkoxy. We especially prefer each of Xi, X , X 3 , X 4 , X 5 and X 6 to be the same C 9 alkyl or each of Xj, X , X , X , X 5 and X 6 to be the same C 6 alkoxy. When each of A l s A , A , A , A 5 and A 6 is N, especially preferred mixtures are those in which each of Yi, Y , Y , Y 4 , Y 5 and Y 6 is hydrogen and each of Xi, X 2 , X 3 , X 4 , X 5 and X 6 is C 9 alkyl, or, alternatively, each of Yi, Y 2 , Y 3 , Y 4 , Y 5 and Y 6 is C 6 alkoxy and each of Xj, X 2 , X 3 , X 4 , X 5 and X 6 is C 6 alkoxy. When each of A l s A 2 , A 3 , A , A 5 and A 6 is C-H, then each of Y ls Y 2 , Y 3 , Y , Y 5 and Y 6 preferentially represents hydrogen or alkoxy C 3 to C 8 , preferably hydrogen or alkoxy C 5 to C 7 and most preferably hydrogen or alkoxy C . When each of Ai, A 2 , A 3 , A 4 , A 5 and A 6 is C-H, then each of Xi, X 2 , X 3 , X4, X 5 and X 6 is C 2 to C ]2 alkyl or C 2 to Cι 2 alkoxy. When each of X b X 2 , X 3 , X4, X5 and X 6 is alkoxy, they are preferably C 6 to 2 alkoxy. Preferred mixtures are those in which compounds of formula I are compounds of formula III; Formula III in which Xi, X 2 , X , X 4 , X 5 and X are each the same and are selected from - Cι 2 H 25 , -OC 6 Hi 3 and -OC π H 23 ; and each of Y], Y , Y 3 , Y , Y 5 and Y 6 are each the same and are selected from hydrogen and -OC 6 Hι 3 . Further preferred mixtures are those in which the compounds of formula I are compounds of formula IV; Formula IV in which Xi, X 2 , X 3 , X , X 5 and X 6 are each the same and are selected from -CgHig , and -OC 6 Hι 3 ; and each of Yi, Y 2 , Y 3 , Y 4 , Y5 and Y 6 are each the same and are selected from hydrogen and -OC 6 Hι 3 . In a preferred mixture of the invention, in the molecule of formula II each of Ri, R 2 , R 3 , *, R 5 and R 6 are the same and B \ , B 2 , B 3 , B 4 , B 5 and B 6 are hydrogen. Preferably, each of R \ , R , R 3 , *, R 5 and Re are alkyl C 3 to Cι 6 , more preferably alkyl C 4 to Cu and most preferably C 6 or Cn alkyl. The most preferred compounds of formula II are 2,3,6,7,10,11 -hexahexyloxytriphenylene and 2,3,6,7,10,11- hexaundecy loxytripheny lene . A further preferred mixture of the invention, contains the compound of formula II in which each of Ri, R , R 3 , R4, R5 and R 6 are the same and are alkyl C 3 -C 1 6, more preferably C -Cπ alkyl and most preferably C 6 alkyl. Bi, B 2 , B 3 , and B are hydrogen and B 5 and B 6 are the same or different and are each or both hydrogen or fluorine. Most preferable is the compound formed by the mixture of formula I with formula II in which formula II is l,4-difluoro-2,3,6,7,10,l l-hexahexyloxytriphenylene. These mixtures are advantages in that the mesophase persists well below room temperature. Liquid crystal phases can be induced in non-mesogenic materials such as those of formula II in which each of Ri, R , R 3 , R , R 5 and R 6 are the same or different and are alkyl C 2 -Cπ or ethyleneoxy C 3 -C 9 . More preferably when Ri, R , R 3 , R^ R 5 and R 6 are the same and ethyleneoxy C 5 , and when R \ , R 2 , R 3 , R 4 , R 5 and R 6 are a combination of ethyleneoxy C 5 and alkyl C 6 . Most preferably when formula II is 2- ( 1 ,4,7-Trioxaoctyl)-3 ,6,7,10,11 -pentahexyloxytriphenylene, 2,7-Di( 1 ,4,7- trioxaoctyl)-3,6,10,l 1 -tetrahexyloxytriphenylene, 2,7,10-Tri(l ,4,7-trioxaoctyl)- 3,6,11-trihexyloxytriphenylene or 2,3,6,7,10,1 l-Hexa(l,4,7-trioxaoctyl)triphenylene. A preferred mixture contains a polythene main chain polymer with formula II as a side chain substituent in the form shown in formula V. X is alkyl C 1 -C 10 or an ether oxygen linkage (-0-), and R is hydrogen or methyl. Addition of molecules of formula I to polymers such as those in Formula V produces a liquid crystal polymer which shows much better alignment properties than the polymer of formula V alone. A further preferred mixture contains formula II as a functionality in polystyrene block copolymers of the form shown in formula VI. The ratio of n:m is from 6-18: 1. The compound formed with formula I is again easier to align than the polymer of formula V alone with the added advantage that the blocks comprising the copolymer undergo micro-phase separation. Another preferred mixture contains the formula I as a constituent part of the polymer backbone, the length of the flexible spacer n is between 6 and 18, most preferably 6, 12, and 18 and the number of molecules of formula II per polymer formula VII, m, is between 2 and 1000. Formula VII Block copolymers containing blocks of polyethylene oxide and blocks of formula VII can also be made to undergo micro-phase separation and further preferred mixtures contain the polymer of formula VIII. Where the number of molecules of formula I (m) is 10-100 and the number of ethyleneoxide groups in the side chains (n) is 200- 500 In the mixture of the invention, specific compounds of formula I which may be mentioned include the following; 2,3,6,7,10,1 l-hexakis(4-n-nonylphenyl)dipyrazine[2,3-f:2',3'-h]quinoxaline; 2,3,6,7,10,1 l-hexakis-(3,4-dehexyloxyphenyl)dipyrazino[2,3-f:2'3'-h]quinoxaline; 2,3,6,7, 10, 11 -hexakis-4(-n-nonylphenyl)-triphenylene; 2,3,6,7,10,11 -hexakis-(4-n-dodecylphenyl)triphenylene; 2,3,6,7,10,1 1 -hexakis-(4-n-hexyloxy-phenyl)-triphenylene; 2,3,6,7, 10,l l-hexakis-(4-n-undecyloxy-phenyl)-triphenylene; 2,3 ,6,7, 10,11 -hexakis-(3,4-n-dihexyloxy-phenyl)-triphenylene; and 2,3,8,9,12,13,18,19,22,23,28,29-dodecakis(hexyloxy)hexabenz[a,c,k,m,v,w] trinaphthylene. In the mixture of the invention, specific compounds of formula II which may be mentioned include the following; 2,3,6,7,10,11 -hexahexyloxytriphenylene, 2,3,6,7,10,11-hexaundecyloxytriphenylene, 1 ,4-difluoro-2,3,6,7, 10, 1 1 -hexahexyloxytriphenylene, 2-( 1 ,4,7-trioxaoctyl)-3 ,6,7, 10,1 1 -pentahexyloxytriphenylene, 2,7-di(l,4,7-trioxaoctyl)-3,6,10,l 1 -tetrahexyloxytriphenylene, 2,7,10-tri(l,4,7-trioxaoctyl)-3,6 11 -trihexyloxytriphenylene, 2,3,6,7,10,1 l-hexa(l, 4, 7-trioxaoctyl)triphenylene, acetic acid 2-hydroxy-3 ,6,7, 10,1 1 -pentahexyloxytriphenylene ester, hexanoic acid 2-hydroxy-3, 6,7, 10, 11 -pentahexyloxytriphenylene ester, 4-biphenylcarboic acid 2-hydroxy-3,6,7,l 0, 11 -pentahexyloxytriphenylene ester, 4-nitrobenzoic acid 2-hydroxy-3, 6,7, 10, 11 -pentahexyloxytriphenylene ester, 3,5-dinitrobenzoic acid 2-hydroxy-3, 6,7,10,11 -pentahexyloxytriphenylene ester, 4-cyanobenzoic acid 2-hydroxy-3, 6,7, 10,11 -pentahexyloxytriphenylene ester, 4-fluorobenzoic acid 2-hydroxy-3,6,7,10,l 1 -pentahexyloxytriphenylene ester, 1 -naphthoic acid 2-hydroxy-3 ,6,7,10,11 -pentahexyloxytriphenylene ester, 2-naphthoic acid 2-hydroxy-3,6,7,10,l 1 -pentahexyloxytriphenylene ester, polythenes bearing formula II as a side chain substituent (formula V), polyacrylates bearing formula II as a side chain substituent (formula VI polymers containing formula II as part of the polymer backbone (formula VII), block copolymers containing a central core of polymer with formula II as part of the polymer backbone surrounded by blocks of poly(ethyleneoxide) with molecular weights in the range 750-2000 (formula VIII). Thus the most preferred mixtures of the invention are mixtures comprising a compound of formula I selected from the group; 2,3,6,7,10,1 l-hexakis(4-nonylphenyl)dipyrazine[2,3-f:2',3'-h]quinoxaline; 2,3,6,7, 10,l l-hexakis-(4-nonylphenyl)-triphenylene; 2,3,6,7, 10, 11 -hexakis-(4-dodecylphenyl)triphenylene; 2,3,6,7,10,1 l-hexakis-(4-hexyloxy-phenyl)-triphenylene; 2,3,6,7,10,11 -hexakis-(4-n-undecyloxy-phenyl)-triphenylene; and a compound of formula II selected from the group; 2,3,6,7,10,11 -hexahexyloxytriphenylene, 2,3,6,7, 10,11 -hexaundecyloxytriphenylene, 1 ,4-difluoro-2,3 ,6,7,10, 11 -hexahexyloxytriphenylene, 2-(l ,4,7-trioxaoctyl)-3,6,7,l 0,11 -pentahexyloxytriphenylene, 2,7-di(l ,4,7-trioxaoctyl)-3 ,6, 10, 11 -tetrahexyloxytriphenylene, 2,7,10-tri(l ,4,7-trioxaoctyl)-3,6,l 1 -trihexyloxytriphenylene, 2,3 ,6,7, 10,11 -hexa( 1 ,4,7-trioxaoctyl)triphenylene, acetic acid 2-hydroxy-3, 6, 7, 10,1 l-pentahexyloxytriphenylene ester, hexanoic acid 2-hydroxy-3,6,7,10,l l-pentahexyloxytriphenylene ester, 4-biphenylcarboic acid 2-hydroxy-3 ,6,7, 10,1 l-pentahexyloxytriphenylene ester, 4-nitrobenzoic acid 2-hydroxy-3,6,7, 10,1 l-pentahexyloxytriphenylene ester, 3,5-dinitrobenzoic acid 2-hydroxy-3, 6,7, 10,1 l-pentahexyloxytriphenylene ester, 4-cyanobenzoic acid 2-hydroxy-3,6,7,l 0,1 l-pentahexyloxytriphenylene ester, 4-fluorobenzoic acid 2-hydroxy-3, 6, 7, 10,1 l-pentahexyloxytriphenylene ester, 1 -naphthoic acid 2-hydroxy-3,6,7,10,l l-pentahexyloxytriphenylene ester, 2-naphthoic acid 2-hydroxy-3,6,7, 10,1 l-pentahexyloxytriphenylene ester, l,4-difluoro-2,3,6,7,10,l l-hexakis(hexyloxy)triphenylene, and polythenes bearing formula II as a side chain substituent (formula V), polyacrylates bearing formula II as a side chain substituent (formula VI polymers containing formula II as part of the polymer backbone (formula VII), block copolymers containing a central core of polymer with formula II as part of the polymer backbone surrounded by blocks of poly(ethyleneoxide) with molecular weights in the range 750-2000 (formula VIII). The compounds of formula I are novel per se. Thus, according to a further feature of the invention we provide a compound of formula I Formula in which A )-6 , Xι -6 , Yι -6 and R 7- ι 2 are as defined above; provided that the compound of formula I is not 2, 3, 6, 7, 10, 1 1 - hexakis (4- n- nonylphenyl)dipyrazine [2, 3, -f: 2 ,3 -h] quinoxaline. The compounds of formula I are especially advantageous in that they may be mixed with compounds of formula II to form novel compounds which possess properties as, inter alia, highly ordered and highly conducting liquid crystals. Certain compounds of formula II are also novel per se. Thus according to the invention we also provide a novel compound of formula II selected from the group; 1 ,4-difluoro-2,3 ,6,7, 10,11 -hexahexyloxytriphenylene, 2-( 1 ,4,7-trioxaoctyl)-3 ,6,7, 10,11 -pentahexyloxytriphenylene, 2,7-di( 1 ,4,7-trioxaoctyl)-3 ,6,10,11 -tetrahexyloxytriphenylene, 2,7,10-tri( 1 ,4,7-trioxaoctyl)-3 ,6,11 -trihexyloxytriphenylene, acetic acid 2-hydroxy-3,6,7, 10,1 l-pentahexyloxytriphenylene ester, hexanoic acid 2-hydroxy-3,6,7, 10,1 l-pentahexyloxytriphenylene ester, 4-biphenylcarboic acid 2-hydroxy-3 ,6,7,10,11 -pentahexyloxytriphenylene ester, 4-nitrobenzoic acid 2-hydroxy-3,6,7,10,l 1 -pentahexyloxytriphenylene ester, 3,5-dinitrobenzoic acid 2-hydroxy-3, 6,7, 10,1 l-pentahexyloxytriphenylene ester, 4-cyanobenzoic acid 2-hydroxy-3,6,7,l 0,1 l-pentahexyloxytriphenylene ester, 4-fluorobenzoic acid 2-hydroxy-3,6,7,10,l l-pentahexyloxytriphenylene ester, 1 -naphthoic acid 2-hydroxy-3 ,6,7,10,1 1 -pentahexyloxytriphenylene ester, l,4-difluoro-2,3,6,7,10,l l-hexakis(hexyloxy)triphenylene, and block copolymers containing a central core of polymer with formula II as part of the polymer backbone surrounded by blocks of poly(ethyleneoxide) with molecular weights in the range 750-2000 (formula VIII). According to the invention we also provide a process for the manufacture of a compound of formula I which comprises reacting a hexahalotriphenylene or a hexahaloquinoxaline with a boronic ester of formula V; Synthesis of the quinoxalines involves a straightforward condensation of hexaaminobenzene with the appropriate benzil but to make the hexakis (4- alkoxyphenyl) triphenylenes a variation on the normal Suzuki reaction conditions had to be employed. The conditions required for this type of polyarylation are more demanding than those for simple aryl-aryl coupling. Under standard Suzuki coupling conditions (0.3 mol% Pd(0) as Pd(PPh 3 ) 4 , toluene, water Na 2 C0 3 , reflux under argon for 24 hours) the reaction of the appropriate aryl boronic acid with hexabromotriphenylene gave the product formula III contaminated with a reduction product. Competitive reduction under these reaction conditions is a well-known problem. Ordinarily it is not significant since it often only amounts to only 1-2% and the by-product is usually easily removed. However, in this case the by-product is very difficult to remove and the "error is cumulative" giving 5-12% of the reduction product. To overcome this problem we have modified the Suzuki protocol to minimise reduction. A stronger base was used to improve the rate of metathesis of the boronic acid species and DME was used to give a homogenous reaction medium. In order to prevent excessive de-borylation of the boronic acid starting material, the less labile pinacol ester (above) was used. This ester is also easier to purify (by distillation or column chromatography) than the acid and is more stable with respect to temperature, pH and oxygen. These modifications improved the yield and purity of formula III giving a product in which the by-product could no longer be detected by 1H NMR. The pioneering work of the group of Mullen suggested that oxidative cyclisation of compounds of formula I should yield systems with exceptionally large aromatic cores. This was achieved using dichloromethane/FeCl 3 followed by a reductive methanol work up and excellent yields were obtained (70%, 2 hrs at 25°C). This is a new type of polynuclear aromatic core. We also provide a method of manufacturing a mixture and or a liquid crystal as hereinbefore described which comprises mixing a compound of formula I with a compound of formula II. 2,3,6,7,10,11 -hexahexyloxytriphenylene is known to display a hexagonal columnar mesophase between about 70 and 100°C. However the novel mixtures of the invention comprising a compound of formula II, e.g. 2,3,6,7,10,1 1- hexahexyloxytriphenylene, and a compound of formula I form a novel liquid crystal with a hexagonal columnar phase at a higher temperature than 2,3,6,7,10,11- hexahexyloxytriphenylene alone. Thus, for example, a mixture of 2,3,6,7,10,11- hexahexyloxytriphenylene and 2,3,6,7,10,1 l-hexakis(4-nonylphenyl)dipyrazine[2,3- f:2',3'-h]quinoxaline form a novel liquid crystal with a hexagonal columnar phase at a temperature of between 130 and 240°C. The mesophase properties are altered by changing the properties of either formula I or formula II possible combinations of which were discussed earlier. The properties of a selection of the most preferable combinations of formula I and formula II are shown in Table 1. Thus according to a further feature of the present invention we provide a liquid crystal with a hexagonal columnar phase between temperatures of less than room temperature and 280°C. The low temperature phase of many of the mixtures is glassy, allowing the columnar order of the mesophase to persist at low temperature without the introduction of crystalline defects. The liquid crystal of the invention especially comprises a mixture of compounds of formula I and formula II as hereinbefore described. In the mixtures and liquid crystals of the invention the ratio of the compound of formula I and formula II may vary. However, it is preferred that the ratio is substantially 50:50. Table 1 Phase Behaviour + Phase Behaviour Formula II Formula IV + Formula III Name (Xl-6 = C9H19, Yι_6 = (Xl-6 = C9H19, Yj H) 6 = H) 2,3,6,7, 10,11 -hexahexyloxytriphenylene K <0 Col h 240 (33) I <0 Col h 155 (19) 1 l,4- ifluoro-2,3,6,7,10,l l- K <0 Col h 225.6 (36) 1 K <0 Col h 129.3 ( 16) hexakis(hexy loxy)tripheny lene . 2-( 1 ,4,7-Trioxaoctyl)-3,6,7, 10,1 1- Col 240.4 (28.7 J/g) I Col 137 (15.2J/g) I pentahexyloxytriphenylene 2,7-Di( 1 ,4,7-trioxaocty l)-3 ,6, 10, 1 1- Col 23 1.8 (29.7J/g) I Col 1 17.7 (9.1J/g) I tetrahexyloxytriphenylene 2,7, 10-Tri( 1 ,4,7-trioxaocty l)-3, 6, 11 - Col 226.3 (29.6 J/g) I Col 88.0 (3.8 J/g) I trihexyloxytriphenylene 2,3,6,7,10,11-Hexa(l,4,7- Col 200.2 (19.9 J/g) I Col51.7(17.4J/g)I trioxaoctyl)triphenylene 2-hydroxy-3,6,7,10,ll- pentahexyloxytriphenylene esters of: Acetic acid K<0Col h 214(29.5)I K<0 Col h 155 (15.4) I Hexanoic acid K<0Col h 218(31.1)I K<0Col h 166(18.7) I 4-Biphenylcarboic acid K <0 Col h 228 (29.4) I K<0 Col h 169 (17.0) I 4-Nitrobenzoic acid K <0 Col h 237 (29.9) I K<0 Col h 180 (17.9) I 3,5-Dinitrobenzoic acid K<0Col r 229(28.2)I K<0Col rl 114.5(0.5) Col, 2 169(13.0)1 4-Cyanobenzoic acid K <0 Col h 227 (27.2) I K<OCol h 175(17.6) I 4-Fluorobenzoic acid K<0 Col h 231 (30.0)1 K<0Col h 174(19.6) I 1 -Naphthoic acid K<0 Col h 205 (18.3) I K<0 Col h 151 (10.9) I 2-Naphthoic acid K <0 Col h 230 (32.8) I K<0 Col h 176(19.2) and Polymers I Formula V (X=0, R=H) Col 235 (26.1) I Col 147(12.5)1 Formula VI (m:n = 6:1) Glass 104 Col 228.8 Glass 104 Col 127.1 (12.2)1 (3.66) I Formula VI (m:n = 18:1) Cr 101 (0.1) Col Col 243.1 (12.2)1 136.9 (-4.4) I Formula VII (n = 8) Cr 48.7 (3.1), Colh Col h 190.9(2.4)1 100.0(2.4)1 Formula VII (n = 12) Cr 67.0 (1.0) Col h 194.Ϊ Glass 57.2 Colh 128.4 (14.8)1 (9.2) 1 Formula VII (n = 16) Glass 90 Col h 245.3 Col h 155.7(2.5)1 (26.6) I Formula VIII (n = 20) Col h 213.9 (15.1) I Col 137.5(8.85)1 Formula VIII (n = 40) Cr 52 (15.2) Col h 223 Cr461 (11.29) Col (15.7)1 141.0(6.6)1 The unit cell parameters for the some of these mixtures are given in Table II. The fact that there is a single column/column repeat distance and a hexagonal lattice shows that there cannot be segregated stacks of compounds of formula I and formula II. Thus there is an alternating stack structure in which a compound of formula I is stacked on a compound of formula II and so on. Thus according to a further feature of the invention we provide a liquid crystal as hereinbefore described which has an alternating stack structure. We especially provide a liquid crystal which comprises an alternating stack of compounds of formula I and formula II. In relation to the entries displayed in Table I it is important to note that: 1) There is 1: 1 compound formation in the mixture of compounds of formula I and formula II. That the temperature of the clearing temperature of the 1 : 1 compound is generally above that of the individual components and that this 1 : 1 compound undergoes isothermal phase transitions. A specific example is given in Figure 1 (the phase/composition diagram of HAT6 (2,3,6,7,10,11- hexahexyloxytriphenylene) + PDQ9 (2,3,6,7,10,1 1 -hexakis(4-n- nonylphenyl)dipyrazine[2,3-f:2',3'-h]quinoxaline) 2) There may be induction of liquid crystalline behaviour . The 1 : 1 compounds give columnar liquid crystal phases whereas the individual components of formula I and formula II may either be mesogenic or non-mesogenic. Preferable examples are 2,3,6,7,10,1 l-Hexa(l,4,7-trioxaoctyl)triphenylene and 2-Naphthoic acid 2-hydroxy- 3,6,7,10,1 l-pentahexyloxytriphenylene ester. 3) In the use of polymer derivatives of formula II 1 : 1 compounds with formula I are often easier to align by surface or shear interactions than the polymers on their own. Hence Figure 2 shows the alignment of the mixture of Formula VII (n = 12) with (2,3,6,7,10,1 l-hexakis(4-n-nonylphenyl)dipyrazine[2,3-f:2',3'-h]quinoxaline) compared to that of the polymer alone. 4) In the case of block copolymers of compound formula VIII, addition of the compound of formula I can induce microphase separation, for example when Formula VIII (n = 40) is mixed with 2,3,6,7,10,1 l-hexakis(4-n- nonylphenyl)dipyrazine[2,3-f:2',3'-h]quinoxaline. 5) These new mixtures show enhanced conductive behaviour. Studies on the photoconductivity of 2,3,6,7, 10, 11 -hexahexyloxytriphenylene have found that there exist clear hole transits in the mesophase while the transient photocurrent displayed a featureless decay in the crystalline phase. Holes in the mesophase of that material were found to have a mobility of μ π = 3.0xlO ~4 cm 2 V " V, which is generally a 200 fold enhancement over known liquid crystals. Detailed analysis of the featureless photocurrent transient decays demonstrated that the columnar stacks behave like one dimensional semiconductors and that the holes had a range of S = 4μm before deep trapping in the crystalline phase. Thus discotics have already been demonstrated as hole transporting layers. The liquid crystals of the invention demonstrate improved hole mobility and hole range by using a mixture designed to give favourable π- stacking. Thus the liquid crystals of the invention have an enhanced conductivity over known liquid crystals, with an enhancement factor of from 10 to 10 5 For sandwich samples of thickness 25 μm, of 2,3,6,7,10,11- hexaundecyloxytriphenylene (HATH) the photocurrent is not detectable in either the discotic or crystalline phase. This places an upper limit on the peak photocurrent, I p of I p «4xlO "7 A even at the highest applied electric fields of E = 6.0MVm " \ This is in stark contrast to the photoconductivity of 2,3,6,7,10,11 -hexahexyloxytriphenylene where the magnitude of the peak photocurrent in the discotic phase at similar electric field and sample thickness was I p = 10 "5 A. With 1 : 1 mixture of 2,3,6,7,10,1 1 -hexaundecyloxytriphenylene and 2,3,6,7,10,11 - hexakis-(4-nonylphenyl)-triphenylene however, there is a transient photocurrent generated by a thin sheet of positive carriers of thickness, δ- 0.1 μm travelling from a top electrode, where they are generated by a laser pulse, to a bottom counter electrode under the influence of an electric field (Figure 3). 9 1 1 Taking a mobility of 0.017cm V " s " , as representative of the discotic phase, it is noteworthy that in the system of the invention the mobility has increased, by a factor « 57, in comparison to that previously found for HATH . Also of interest is the observation in the mixture of a clear transit even in the low temperature regime. From the pre transit time photocurrent decay it is possible to estimate a trapping time and a consequent carrier schubweg and the increased mobility are indicative of a great improvement in the ordering of the columnar stacks in the mixed system. This ordering is a direct consequence of the mixture as 2,3,6,7,10,H-hexakis-(4- nonylphenyl)-triphenylene alone does not photoconduct. Ordering has been found elsewhere to lead to higher mobility in compounds forming a helical columnar phase and to dominate the mobility parallel to the column in hexagonal phases. Therefore, according to a yet further feature of the invention we provide a liquid crystal which has enhance hole electron mobility and charge carrier schubweg. Conductivity in these systems has also been investigated by sandwiching a homeotropic film of the mixtures between conducting ITO coated glass electrodes. Figure 4 shows the IV characteristics of 2,3,6,7,10,1 l-hexakis-(4-nonylphenyl)- triphenylene, 2,3,6,7,10,1 1 -hexahexyloxytriphenylene and their 1 :1 mixture Figure 5 shows the frequency dependent AC conduction properties of the mixture before and after the sample cell is annealed by the action of heat and applied field. Typically the annealing process is carried out in the liquid crystalline phase of the mixture, a field is then applied, the intensity of which is steadily increased until the resistance of the sample begins to suddenly fall (typically 20V across a 6μm cell). We also provide the use of a mixture of a compound of formula I and a compound of formula II in the manufacture of a liquid crystal as hereinbefore described. We further provide the use of a compound of formula I in the manufacture of a mixture or a liquid crystal as hereinbefore described. We yet further provide the use of a compound of formula II in the manufacture of a mixture or a liquid crystal as hereinbefore described. The invention will now be described by way of example only. Example 1 Photoconduction Studies Electrode cells were fabricated by evaporating aluminium on two quartz slides making one of them semitransparent. The two slides are placed on top of one another being separated by 25 μm Teflon spacers. The slides were held in an assembly allowing temperature control. By melting the compound at the entrance to the cell it fills the cell by capillary flow. The thickness of the cell and its uniformity was monitored using interference fringes and measurement of the interference transmission spectrum using a Hitachi U3000 spectrophotometer. The potential was supplied by a Fluke high voltage power supply. A lambda Physik EMG101 nitrogen laser at 337nm with a 6ns pulse width was used to excite the photocurrent transients. The light intensity was controlled using neutral density filters and kept low to avoid distortion of the resulting signal by space charge. The photocurrents were detected as a voltage across a 50Ω input resistor to a high speed 592 differential video pre amplifier with xlOO gain. The two outputs of the 592 act as input to EL2002 50Ω line drivers in turn delivering the signal to a 50Ω terminated Tektronix digitising oscilloscope, TDS 320. The laser emits radio frequency interference, RFI, picked up by the detection apparatus so it is necessary to collect a second baseline signal with no light on the sample. In this way, in post acquisition processing the RFI was subtracted and the signal greatly cleaned up. White noise was also reduced by signal averaging. Example 2 - Synthesis Compound Preparation. The mixtures/compounds were prepared by dissolving the components, in a 1 :1 molar ratio, in dichloromethane. The components were weighed to within a tolerance of ±0.001 g. To aid dissolution of the components the solution was warmed gently in an ultra-sonic bath. Rotary evaporation under reduced pressure was used to remove the solvent, leaving a thin film of the compound on the walls of the flask. This thin film was dried at 40°C under vacuum (O.OlmmHg) for 5 days. The compound was then scraped from the flask and powdered. Thermal characterisation. The thermal behaviour of all the materials was investigated by polarising optical microscopy (Olympus BH-2 microscope and with a Linkam hot stage) and differential scanning calorimetry (Perkin-Elmer DSC 7, 2-3mg in closed AI pans) with heating and cooling scans performed at 10°Cmin "1 . Onset values (°C) are reported together with the associated transition enthalpies (ΔH) in kcal mol " . Exothermic transitions are conventionally reported with a negative enthalpy change. The phase-composition diagrams were constructed using OPM and DSC data collected for mixtures with varying amounts of each component. For mixtures containing >10% of both components the sample was prepared by weighing the components accurately as described in Section 0. For mixtures where one component was present as less than 10% of the total, accurately prepared, standard solutions of the components prepared and these were mixed in the correct proportions using a pipette. X-ray diffraction experiments. X-ray diffraction experiments were performed at room temperature (in the crystalline phase) and, for those compounds with mesomorphic properties, at a range of temperatures increasing towards the upper limit of the columnar phase(s). The diffraction pattern was collected on film using a pinhole camera consisting of a Philips generator and tubes, nickel filtered Cu K α radiation of wavelength λ=0.154nm, and a Lindemann sample tube (1.5mm inner diameter) to plate distance of 135.5mm. Powder samples were packed into the capillary, which was degassed with argon before the end was cleaned (dichloromethane), dried and sealed using a flame. Sticky or fine powders were initially loaded by forming a plug of material in the mouth of the capillary tube. The end of the tube was cleaned with dichloromethane (to avoid contamination with charred organic material) and dried before being sealed. Once the tube was sealed it was placed into a pre-heated aluminium holder and centrifuged for five minutes or until the plug of material was packed into the bottom of the tube and no air bubbles could be seen. Exposure times in excess of three hours were required to get good resolution of both wide and small angle regions. The film was developed for five minutes, fixed for five minutes and then washed for one hour before being hung to dry at room temperature overnight. The diameters of the diffraction rings were measured using a ruler with the aid of a light box. A spreadsheet was used to collate the data for each sample and temperature and calculate the lattice distances (to within ±0.3 A). A small in-house package was used to assist in the assignment of the unit cell parameters. NMR experiments. 1H and 13 C NMR (1H {BB} and INEPT) spectra were acquired on a 400MHz Bruker AM400 NMR spectrometer; chemical shifts are reported in δ units (ppm, relative to Me Si (TMS)). COSY and HMQC NMR experiments were run as necessary, to assign any ambiguous peaks in the ! H or 13 C spectra. Η {BB} refers to broadband decoupling of protons. π B spectra were also proton decoupled. In the spectra of boronic acids and esters it is worth noting that the resonance due to the carbon atom attached directly to boron is so broad that its detection is impossible (quantum effect). Mass spectra Mass spectra were recorded on a VG Autospec instrument and all peaks >20% were routinely recorded unless stated; FAB+ refers to the caesium atom bombardment method of ionisation. Unless stated the electron ionisation method was used. Spectroscopic Measurements UV/VIS (250-600nm, 1cm path length quartz cell) were recorded on a Perkin- Elmer Lambda series 2 spectrometer, the extinction co-efficients (ε) are given in units of dm mol " cm " . FTIR spectra were recorded on a Perkin-Elmer 1760X FTIR spectrometer in the range 4000-600cm '1 ) as a liquid film or Nujol mull between polished NaCl disks. Example 3 General synthesis of boronic esters Chemicals and solvents (AR) grade were obtained from Sigma-Aldrich and, unless mentioned, were used without further purification. Column chromatographic separations were performed on silica gel (Merck, Kieselgel 9385 Type 60). Thin layer chromatography (TLC) was performed on aluminium sheets pre-coated with silica gel (Whatman AL SIL G UV plates). Petroleum ether refers to the petroleum fraction boiling 40-60°C, which was double distilled before use. The boronic acid, synthesised by literature methods known per se, (1 mmol) was weighed into a clean, dry round bottom flask fitted with a reflux condenser and a gas bubbler. Pinacol (distilled, 1.1 mol) was added in 5ml of dry, distilled tetrahydrofuran. The reaction mixture was refluxed under nitrogen for at least one hour. Removal of the solvent yields the crude product, which was purified by flash column chromatography (1 : 1 dichloromethane/petroleum ether as eluent). Example 4 General synthesis of hexakis(4-alkoxy phenyl)triphenylenes 2,3,6,7,10,11 -hexahexyloxytriphenylene (lmmol) was added to a mixture of dimethyl ether (DME) (50ml) and water (2ml). Argon was bubbled through the suspension for fifteen minutes before adding tetrakis-triphenylphosphine palladium (0) (0.3-3mol% Pd per reaction site). The boronic ester (7mmol) was added carefully under a stream of argon and stirring was continued for 10 minutes. Finally barium hydroxide monohydrate (7mmol) was added. The mixture was heated to 80°C and stirred under argon until the reaction was complete (1-3 days), cool water was added to the reaction mixture and the organic phase extracted with ether. The combined extracts were washed with water and dried over magnesium sulphate. The dry organic phase was passed through a short silica column and the solvent removed to give the crude product as a straw coloured oil. Flash column chromatography was used to purify the product and (where possible) it was precipitated from ether (-30°C for 14 days) or ethanol. The following compounds were synthesised using the general methods set out above; Example 5 2, 3, 6, 7, 10, 11 - Hexakis - (4-n-nonylphenyl) - triphenylene (PTP9) Yield 88%. White solid M.p.53°C and 65°C. Found: C,89.9; H, 10.2. C I08 H 144 requires C, 89.9; H, 10.1%); IR(Nujol) v~= 1909cm -1 (C=C); Η NMR (300 MHz, CDC1 3 , 25°C, TMS): δ = 0.81 (t, 3 J(H,H) = 7Hz, 18H; 6 x -CH 3 ), 1.20 (m, 72Η; 6 x - CH 2 ) 6 -), 1.55 (m, 12Η; 6 x - CH 2 CH 2 -Ar), 2.53 (t, 3 J(H,H)=7Hz, 12H; 6 x CH 2 CH 2 - Ar), 7.02 (d, 3 J(Η,Η)=8.0Ηz, 12H; 6 x 2 -CH, Phenyl C 3>6 ), 7.15 (d, 3 J(H,H)-8.0Hz, 12H; 6 x 22 - CH, Phenyl C 3, 6 ), 7.15 (d, 3 J(H,H)=8.0Hz, 12H; 6 x 2 -CH-, Phenyl C 2,5 ), 8.61 (s, 6Η; 6-CH-, triphenylene): ,3 C NMR (75 MHz, Η{BB} and DEPT, CDC1 3 , 25°C, TMS): δ = 14.53 (CH 3 ), 23.10 (CH 2 ), 29.73 (CH 2 ), 29.73 (CH 2 ), 29.76 (CH 2 ), 29.76 (CH 2 ), 29.96 (CH 2 ), 30.02 (CH 2 ), 31.82 (CH 2 ), 32.33 (CH 2 ), 36.04 (CH 2 ), 125.85 (C, triphenylene Cι, 4 , 5 ,8,9.i2), 128.40 (CH, Phenyl C 2>6 ), 129.22 (C, triphenylene C 4a , 4b 8a,8b,i2a,i2b), 130.34 9CH, Phenyl C 3 , 5 ), 139.27 (C, Phenyl C 4 ), 140.24 (C, Phenyl Ci), 141.76 (C, triphenylene C 2 ,3,6,7,ιo,ιι); MS (FAB+): m/z(%): 1442 (100) [M + ], 1370(10), 1329(15), 1239(35). Example 6 2, 3, 6, 7, 10, 11 -Hexakis- (4-n-dodecylphenyl) - triphenylene (PTP12) Yield 78%. White solid M.p. 36°C. Found: C, 89.1 ; H, 10.5. Cι 26 Hι 80 requires C, 89.3; H, 10.5%); IR(Nujol): v~=1909cm 1 (C=C); 1H NMR (300 MHz, CDC1 3 , 25°C, TMS): δ= 0.91 (t, 3 J(H,H)=7HZ, 18H; 6 x - CH 3 ), 1.30 (m, 84Η; 6 x -(CH 2 )ι- 1.33 (m. 12H; 6 x -CH 2 CH 2 CH 2 CH 2 -Ar), 1.34 (m, 12H; 6 x CH 2 CH 2 CH 2 -Ar), 1.65 (m, 12H; 6 x -CH 2 CH 2 -Ar), 2.63 (t, 3 J(H,H)-7Hz, 12H; 6 x CH 2 CH 2 -Ar), 7.12 (d 3 J(H,H)=8.2Hz, 12H; 6 x 2 - CH-, phenyl C 3>5 ), 7.27 (d, 3 J(Η,Η)=8.2Ηz, 12H; 6 x 2 - CH-, phenyl C 2,6 ), 8.71 (s, 6Η; 6 x - CH-, triphenylene; 13 C NMR (75 MHz, 1H{BB} and DEPT, CDC1 3 , 25°, TMS): δ= 14.53 (CH 3 ), 23.11 (CH 2 ), 29.75 (CH 2 ), 29.79 (CH 2 ), 29.97 (CH 2 ), 30.08 (CH 2 ), 30.12 (2 x CH 2 ), 30.81 (2 x CH 2 ), 32.34(CH 2 ), 36.04 (CH 2 ), 125.87 (CH, triphenylene C 1 Λ5, 8, 9 ,i 2 ), 128.38 (CH, phenyl C 2>6 ), 129.22 (C, triphenylene C 4aj4b , 8a ,8b,i2a,i2b), 130.35 (CH, phenyl C 3>5 ), 139.28 (C, phenyl C 4 ), 140.25 (C, phenyl C,), 1421.74 (C, triphenylene C 2>3 ,6,7,ιo,n); MS (FAB+): m/z(%): 1694(75) [M + ], 1552(10), 57(100)/ Example 7 2, 3, 6, 7, 10, 11 -Hexakis- (4-n-hexyIoxy-phenyl) - triphenylene (PTPO6) Yield 66%. White Solid M.p. 59°C and 139°C. Found: C, 83.8; H, 8.65, C 9 oH 108 θ6 requires C, 84.0; H, 8.5; O, 7.5%); IR (Nujol): v ~= 1908cm "1 (C=C); 1H NMR (300 MHz, CDC1 3 , 25°C, TMS): δ = 0.85 (t, 3 J(H,H)=7Hz, 18H; 6 x CH 3 ), 1.28 (m, 24H; 6 x -(CH 2 ) 2 -), 1.40 (m, 12Η; 6 x CH 2 CH 2 CH 2 -OAr), 1.72 (quint, 3 J(H,H)=7Hz, 12H, 6 x CH 2 CH 2 CH 2 -OAr), 3.89 (t, 3 J(H,H)=7Hz, 12H; 6 x CH 2 CH 2 -OAr), 6.76 (d, 3 J(Η,Η)=8.8Ηz, 12H; 6 x 2 - CH-, phenyl C 3,5 ), 7.16 (d, 3 J(H<H)=8.8Hz, 12H; 6 x 2 - CH-, phenyl C 2>6 ), 8.56 (s, 6H; 6 x CH-, triphenylene); 13 C NMR (75 MHz, 1H{BB} and DEPT, CDC1 3, 25°C, TMS): δ = 14.46 (CH 3 ), 23.02 (CH 2 ), 26.16 (CH 2 ), 29.68 (CH 2 ), 30.98 (CH 2 ), 32.02 (CH 2 ), 68.39 (CH 2 ), 114.48 (CH, phenyl C 3>5 ), 125.73 (CH, triphenylene Cι, 4ι5; 8,9,i2), 129.08 (C, triphenylene C a> 4b J 8a,8b,i2a,i2b), 131.51 (CH, phenyl C 2;6 ), 134,29 (C, phenyl Ci), 139.81 (C, triphenylene C 2 ,3,6,7,ιo.ι 1), 159.46 (C, phenyl C 4 ); MS (FAB+): m/z(5); 1285(28) [M + ], 1 108(10), 109(25), 69(100). Example 8 2, 3, 6, 7, 10, 11 -Hexakis- (4-n-undecyloxy-phenyl) - triphenylene (PTPO11) Yield 77%. Pale Yellow solid M.p. 66°C. Found C, 84.8; H, 10.2. Cι 20 Hι 68 θ 6 requires C, 84.5; H, 9.9; 0, 5.6%; IRfNujol): v —2300cm "1 (C=C), 1H NMR (300 MHz, DCD1 3 , 25°C, TMS: δ = 0.92 (t, 3 J(H,H)=7Hz, 18H; 6 x CH 3 ), 1.31 )m,84Η: 6 x -(CH 2 ) τ ), 1.60 (m, 12H; 6 x CH 2 CH 2 CH 2 -OAr), 1.82 (quint, 3 J(H,H)=7Hz, 12H; 6 x - CH 2 CH 2 CH 2 -OAr), 3.99 (t, 3 J(H,H)=7Hz, 12H; 6 x CH 2 CH -OAr), 6.90 (d, 3 J(H,H)=8.5Hz, 12H: 6 x 2 -CH-, phenyl C 3 , 5 ), 7.28 (d, 3 J(H,H)=8.5Hz, 12H; 6 x 2 - CH-, phenyl C 2>6 ), 8.66 (s, 6Η, 6 x -CH-, triphenylene); 13 C NMR (75 MHz, 1H{BB} and DEPT, CDC1 3 , 25°C, TMS): δ = 14.54 (CH 3 ), 23.11 (CH 2 ), 26.50 (CH 2 ), 29.76 (CH 2 ), 29.77 (CH 2 ), 29.86 (CH 2 ), 29.86 (CH 2 ), 29.87 (CH 2 ), 30.03 (CH 2 ), 30.04 (CH 2 ), 32.33 (CH 2 ), 68.39 (CH 2 ), 114.48 (CH, phenyl C 3>5 ), 125.74 (CH, triphenylene Cι A5 ,8,9.i2), 129.09 (C, triphenylene C 4a>4b , 8 a j8b ,ι 2a ,ι 2b ), 131.52 (CH, phenyl C 2 , 6 ), 134.29 (C, phenyl C,), 139.82 (C, triphenylene C 2 6 ,7 , ιo,n) 158.47 (C, phenyl C 4 ); MS (FAB+): m/z(%): 1705(70) [M + ], 1459(100), 1305(35), 79(30), 502(35), 423(40). Example 9 2, 3, 6, 7, 10, 11 - Hexakis (3, 4-n-dihexyloxy-phenyl) - triphenylene (PTPO6 2 ) Yield 40%. K: 65°C, Col,: 135,1 :. Found: C,80.2; H, 9,5. C 126 H 180 Oι 2 requires C, 80.2; H, 9.6; O, 10.8%); IRfNujol): c~=2350cm "1 (C=C); 1H NMR (300 MHz, CDCI 3 , 25°C, TMS): δ = 0.84, (t, 3 J(H,H)-7Hz, 18H; 6 x -CH 3 ), 0.84 (T, 3 j(h,h)=7Ηz, 18H; 6 x - CH 3 ), 1.27 (M, 24h; 6 x -(CH 2 ) 2 -), 1.42 (m, 24Η; 6 x 2 - CH 2 CH 2 CH 2 -OAr), 1.74 (m, 12H; 6 x -CH 2 CH 2 CH 2 -OAr), 1.78 (m, 12H; 6 x 2 CH 2 CH 2 CH 2 -OAr), 3.95 (t, J J(H<H)=7Hz, 12H; 6 x CH 2 ,CH 2 -OAr), 3.98 (t, 3 J(H,H)=7Hz, 12H; 6 x CH 2 CH2-OAr), 6.86 (d, 3 J(Η,Η)=9.0Ηz, 6H; 6 x -CH-, phenyl C 5 ), 6.98 (dd, 3 J(H,H)=9.0Hz, 4 J(H,H)=2Hz, 6H; 6 x - CH-, phenyl C 6 ), 7.00 (d, 4 J(H,H)=2Hz, 6H; 6 x - CH-, phenyl C 2 ), 8.60 (s, 6H; 6 x -CH-, triphenylene); 13 C NMR (75 MHz, Η{BB} and DEPT, CDC1 3 , 25°C, TMS): δ = 14.43 (CH 3 ), 23.03 (CH 2 ), 26.13 (CH 2 ), 29.72 (CH 2 ), 32.02 (CH 2 ), 69.93 (CH 2 ), 1 13.58 (CH, phenyl C 2 ), 1 14.59 (CH, phenyl C 5 ), 1 19.70 (CH, phenyl C 6> ), 125.10 (CH, triphenylene Cι,4, 5 ,8,9,i2), 129.13 (C, triphenylene C 4a , 4b , 8a)8b ,, 2a ,ι 2b ), 134.76 (C, phenyl d), 148.87 (CH, phenyl C 4 ), 149.67 (C, phenyl C 3 ), 162 (C, triphenylene C 2 , 3j6> 7,ιo,ιι); MS 9FAB+): m/z(%): 1894(10) [M + }, 554(100), 470(10), 310(50), 218(25). Example 10 2,3,8,9, 12, 13, 18,19,22,23,28,29-dodecakis(hexyloxy)hexabenz[a,c,k,m,v,w] trinaphthylene 2, 3, 6, 7, 10, 1 1 - Hexakis (3, 4-n-dihexyloxy-phenyl) - triphenylene (O.lg, 5.3x10 " 5 mol) was stirred in dry, distilled dichloromethane (10ml). Iron (III) chloride (anhydrous, 0.22g, 8.3x10 "4 mol) was then added carefully. A stream of nitrogen through the reaction mixture helps to remove the hydrogen chloride produced (which can act as a de-alkylating agent). After four hours methanol (HPLC, 5m) was added, followed by dichloromethane (10ml) and water (5ml). The aqueous layer was extracted with dichloromethane (2x5ml) and the combined organic extracts were washed with water (4x5ml). Drying and removal of the solvent left 4 as a dark brown solid. This was purified by flash column chromatography using dichloromethane/petroleum spirit (1 :3) as the eluting solvent. The compound was obtained pure as a pale yellow solid. Yield 86%. K: 100°C, Col h :>300°C,I: Found: C, 80.2; H, 9.6. Cι 26 H, 74 0 12 requires C, 80.4; H, 9.4; O, 10.2%); IRfNujol): 2360cm "1 (C=C);); ! H NMR (300 MHz, CDC1 3 , 25°C, TMS): δ = 0.93 (t, 3 J(H,H)=7Hz, 18H; 6 x -CH 3 ), 0.98 (t, 3 J(Η,Η)=7Ηz, 18H; 6 x -CH 3 ), 1.42 (m, 24Η; 6 x CH 2 ) 2 -), 1.43 (M, 24h; 6 X -(CH 2 ) 2 -), 1.97 (M, 24h; 6 X 2 -CΗ 2 ,CH 2 CΗ 2 -OAr), 2.02 (m, 24H; 6 x 2 x -CH 2 CH 2 CH 2 -OAr), 4.22 (t, 3 J(H,H)=7Hz, 12H; 6 x - CH 2 CH 2 -OAr), 4.34 (t, 3 J(Η,Η)=7Ηz, 12H; 6 x CH 2 CH 2 - OAr), 7.55 (s, 6Η: hexabenztrinaphthylene Ci^o.i 1,20,21,30), 8.21 (S, 6H; hexabenztrinaphthylene C 5)6, ι 5ι ι 6j25,26 ); 13 C NMR (75 MHz, 1H{BB} and DEPT, CDCI 3 , 25°C, TMS): δ = 14.54 (2 x CH 3 ), 23.18 (2 x CH 2 ), 26.47 (CH 2 ), 26.70 (CH 2 ), 30.02 (CH 2 ), 30.35 (CH 2 ), 32.29 (CH ), 32.45 (CH 2 ), 69.60 (CH 2 ),69.82 (CH 2 ), 107.14 (CH, phenyl C 2 ), 108.17 9CH, phenyl C 5 ), 1 17.12 (CH triphenylene Cι,4,5,8,9,i2), 124.05 (C, phenyl d), 124.96 (CH, phenyl C 6 ), 128.31 (C, triphenylene C 2 ,3,6,7,ιo,π), 128.45 (C, triphenylene C 4a , 4b , 8a ,8b,i2b), 149.30 (C, phenyl C 4 ), 150.22 (C, phenyl C 3 ); MS (FAB+): m/z(%): 1885(1) [M + ], 424(15), 305(10), 176(30), 55(100). Example 11 2,3,6,7,10,1 l-hexakis(4-n-nonylphenyl)dipyrazino[2,3-f:2'3'-hl-quinoxaline Yield 10%. M.p.71°C and 82°C. Found: C, 84.9; H, 9.4. Cι 02 H 136 N 6 requires C, 84.5; H, 9.5; N, 5.8%; IR (Nujol): v ~= 2360(C=C), 1913cm "1 (C=N); 1H NMR (300 MHz, CC1 3 , 25°C, TMS): δ = 0.90 (T, 3 J(H,H)=7Hz, 18H; 6 x -CH 3 ), 1.31 (m, 72H; 6 x - (CH 2 ) 6 ), 1.59 (m, 12H, 6 x -CH 2 CH 2 -Ar), 2.73 (t, 3 J(H,H)=7Hz, 12H; 6 x -CH 2 CH 2 - Ar), 7.20 (d, 3 J(Η-Η)=8.02Ηz, 12H; 6 x 2 CH), 7.145 (D, 3 J(H-H)=8.02Hz, 12H; 6 x 2 CH); 13 C NMR (75 MHz, Η{BB} and DEPT, CDC1 3 , 25°C, TMS): δ = 14.52 (CH 3 ), 23.08 (CH 2 , 29.60 (CH 2 ), 29.73 (CH 2 ), 29.92 (CH 2 ), 29.99 (CH 2 ), 31.63 (CH 2 ), 32.30 (CH 2 ), 36.21 (CH 2 ), 128.86 (phenyl CH), 136.55 (quinoxaline C 2 a,2b,6a,a6b,ioa,iob), 139.51 (phenyl C), 144.76 (phenyl C), 154.28 (quinoxaline C 2,3 ,6,7,ιo , n); MS (FAB+): m/z(%): 1448(100) [M + ], 1348(44), 1248(15), 204(30). Example 12 2,3,6,7,10,1 l-hexakis-(3,4-dihexyloxyphenyI)dipyrazino[2,3-f:2'3'-h] quinoxaline Yield 66%. K, : 98°C, K 2 : 147 C, Colι : 194°C, L.Found: C, 75.95; H, 9.4; N, 4.35%. Cι 20 Hι 74 N 6 O ]2 requires C, 76.2; H, 9.3; N 6 0 12 requires C 76.2; H, 9.3; N, 4.4; O, 10.1%); IR (Nujol): v ~= and (C-H aliph); Η NMR (300 MHz, CDC1 3 , 25°C, TMS): δ = 0.91 (t, 3 J(H,H) = 7Hz, 18H; 6 x -Me), 0.92 (t, 3 J(H,H)=7Hz, 18H; 6 x -Me), 1.34 (m, 24H; 6 x - (CH 2 ) 2 -), 1.35 (m, 24H; 6 x -(CH 2 ) 2 -), 1.46 (m, 24H; 12 x -CH 2 CH 2 - OAr), 1.75 (t. 3 J(H,H)-7H 2 , 12H; 6 x -CH 2 CH 2 -OAr), 1.85 (t, 3 J(Η,Η)=7Ηz, 12H; 6 x -CH 2 CH 2 -OAr), 6.88 (d, 3 J(Η,Η)=8.02Ηz, 6H; 6 x CH, phenyl C 5 ), 7.45 (d, 4 J(H,H)=2.01Hz, 6H; 6 x CH, phenyl C 6 ), 7.,51 (dd, 3 J(H,H)=2.01Hz, 6H x CH, phenyl C 2 ); 13 C NMR (75 MHz, Η{BB} and DEPT, CDC1 3 , 25°C, TMS); δ = 14.00 (12 x CH 3 ), 22.60 (12 x CH 2 ), 25.70 (12 x CH 2 ), 29.15 (6 x CH 2 ), 29.19 (6 x CH 2 ), 29.15 (6 x CH 2 ), 29.20 (6 x CH 2 ), 31.6 (12 x CH 2 ), 69.15 (6 x CH 2 ) 69.24 (6 x CH 2 ), 113,12 (phenyl CH), 115.72 (phenyl CH), 123.35 (phenyl CH), 131.47 (phenyl C), 138.68 (quinoxaline C 3a ,3b,7a,7b,iia,iib), 148.72 (phenyl C), 150.39 (phenyl C), 154.28 (quinoxaline C 1 ' 2 ' 5 ' 6 - 9 ' 10 ); MS 9FAB+):m/z(%):1892(10)[M + +2]. Example 13 2-(l,4,7-Trioxaoctyl)-3,6,7,10,l l-pentahexyloxytriphenylene A mixture of 2-hydroxy-3, 6,7, 10,1 l-pentahexyloxytriphenylene (0.37 g, 0.5 mmol), l-bromo-2-(2-methoxyethoxy)ethane (0.37 g) and potassium carbonate (0.4 g, 3 mmol) in ethanol (10 ml) was heated under reflux for 72 hours. After which time, it was filtered, extracted with dichloromethane (25 ml), concentrated in vacuo, and the product isolated by column chromatography (silica gel eluting with ethyl acetate) and recrystallised from ethanol to give the title compound as a white solid (0.06 g, 14%o, K → D 55.4°C, D → I 69.3°C). Elemental Analysis: C, 74.95; H, 9.55. C 53 H 82 O 8 requires: C, 75.14; H, 9.75. Mass Spectrum: m/z (FAB) 869 ([M + 23] + , 100%); 846 (M + , 94.5%). Η-NMR: δ H (CDCl 3 ) 0.93 (15H, t, J = 6.7 Hz, 0(CH 2 ) 5 CH 3 ), 1.10- 1.70 (30H, m, OCH 2 CH 2 (CH 2 ) 3 ), 1.94 (10H, m, OCH 2 CH 2 ), 3.41 (3H, s, OCH 2 CH 2 OCH 2 CH 2 CH 3 ), 3.61 (2H, t, J = 5.0 Hz, OCH 2 CH 2 OCH 2 CH 2 ), 3.82 (2H, t, J = 5.0 Hz, OCH 2 CH 2 OCH 2 ), 4.00 (2H, t, J = 5.0 Hz, OCH 2 CH 2 ), 4.23 (10H, t, J = 6.5 Hz, OCH 2 ), 4.42 (2H, t, J = 5.0 Hz, OCH 2 ), 7.83 (5H, s, ArH), 7.90 (1H, s, ArH). Example 14 2,7-Di(l,4,7-trioxaoctyI)-3,6,10,ll-tetrahexyloxytriphenylene was prepared as above from 2,7-dihydroxy-3,6,10,l 1 -tetrahexyloxytriphenylene as a white solid (0.79 g, 61%, mp 44.2°C). Elemental Analysis: C, 72.35; H, 9.25. C 52 H 80 Oιo requires: C, 72.19; H, 9.32. Mass Spectrum: m/z (El) 864 (M + ,100%). Η-NMR: δ H (CDCl 3 ) 0.93 (12 T, t, J = 6.7 Hz, 0(CH 2 ) 5 CH 3 ), 1.10-1.70 (24H, m, OCH 2 CH 2 (CH 2 ) 3 ), 1.94 (8H, m, OCH 2 CH 2 ), 3.41 (6H, s, OCH 2 CH 2 OCH 2 CH 2 CH 3 ), 3.61 (4H, t, J = 5.0 Hz, OCH 2 CH 2 OCH 2 CH 2 ), 3.82 (4H, t, J = 5.0 Hz, OCH 2 CH 2 OCH2), 4.00 (4H, t, J = 5.0 Hz, OCH 2 CH 2 ), 4.23 (8H, t, J = 6.5 Hz, OCH 2 ), 4.42 (4H, t, J = 5.0 Hz, OCIfc), 7.83 (4H, s, ArH), 7.90 (2H, s, ArH). Example 15 2,7,10-Tri(l,4,7-trioxaoctyl)-3,6,ll-trihexyloxytriphenylene was prepared as above from 2,7, 10-trihydroxy-3, 6, 1 1 -trihexyloxytriphenylene as a white solid (0.26 g, 60%, mp 36.5°C). Elemental Analysis: C, 69.2; H, 8.75. C 52 H 78 Oi 2 requires: C, 69.36; H, 8.90. Mass Spectrum: m/z (El) 882, (M + ,100%). 1H-NMR: δ H (CDCl 3 ) 0.93 (9H, t, J = 6.7 Hz, 0(CH 2 ) 5 CH 3 ), 1.10-1.70 (18H, m, OCH 2 CH 2 (CH2) 3 ), 1.94 (6H, m, OCH 2 CH 2 ), 3.41 (9H, s, OCH 2 CH 2 OCH 2 CH 2 CH 3 ), 3.61 (6H, t, J = 5.0 Hz, OCH 2 CH 2 OCH 2 CH 2 ), 3.82 (6H, t, J =- 5.0 Hz, OCH 2 CH 2 OCH 2 ), 4.00 (6H, t, J = 5.0 Hz, OCH 2 CH 2 ), 4.23 (6H, t, J = 6.5 Hz, OCH 2 ), 4.42 (6H, t, J = 5.0 Hz, OCH,), 7.83 (3H, s, ArH), 7.90 (3H, s, ArH). Example 16 2-Hydroxy-3,6,7,10,l l-pentahexyloxytriphenylene a) 2-Hexyloxyphenol Catechol (35.0 g, 0.32 mol), potassium carbonate (109.0 g, 0.79 mol) and 1- bromohexane (52.5 g, 0.32 mol) were added to ethanol (300 ml) and heated under reflux for 48 h. After cooling, dichloromethane (300 ml) was added and the solid residues removed by filtration. The solvents were then removed in vacuo and the crude product was purified by column chromatography on silica gel to give title compound (17.9 g, 29%) as a colourless liquid. Found: C, 73.90, H, 9.20, Cι 2 Hι 8 O 2 requires C, 74.19, H, 9.34;δ H (CHC1 3 ) 6.95-6.83 (m, 4H, ArH), 5.66 (s, 1Η, OΗ), 4.04 (t, J 7, 2Η, ArOCH 2 ), 1.89-1.79 (m, 2Η, ArOCH 2 CH 2 1.55-1.35 (m, 6Η, CH 2 ), 0.95 (t, J 7, 3H, CH 2 CH 5 J. MS (FAB), 194 (M + , 100%), 110 (45%), 95 (7%), 83 (12%), 69 (9%), 55 (18%). b) 2-Acetoxy-l-hexyloxybenzene Acetyl chloride (2.4 g, 30.1 mmol) was added dropwise to vigorously stirred mixture of 2-hexyloxyphenol (5.0 g, 25.8 mmol) and pyridine (5 ml) in dichloromethane (50 ml). The mixture was stirred for 1 hour and poured onto water. The organic layer was separated, dried (MgSO 4 ), concentrated to give crude product which was purified by column chromatography on silica gel using dichloromethane petroleum spirit (1 :3) as eluent to give title compound as a colourless oil (5.78 g, 95%). Found: C, 71.00, Η, 8.35, Cι 4 Η 20 O 3 requires C, 71.19, H, 8.47; δ H (CHCl 3 ) 7.21-7.15 (m, 1H, ArH), 7.05- 7.01 (m, 1Η, ArH), 6.97-6.89 (m, 2Η, ArH), 3.97 (t, J 6.5, 2Η, OCH 2 ), 2.30 (s, 3Η, COCH ), 1.78-1.71 (m, 2Η, ArOCH 2 CH 2 1.57-1.30 (m, 6Η, CH 2 ), 0.90 (t, J 6.9, 3H, CH 2 CH 3 ). MS (FAB), 236 (M + , 53%), 194 (100%), 153 (27%), 1 10 (34%), 85 (7%), 55 (7%). c) 2-Ηydroxy-3,6,7,10,l l-pentahexyloxytriphenylene Anhydrous iron chloride (4.7 g, 28.9 mmol) was added to a stirred mixture of 2- acetoxy-1-hexyloxybenzene (3.4 g, 14.4 mmol) and 3,3',4,4'-tetrahexyloxybiphenyl (4.0 g, 7.2 mmol) in dichloromethane. The mixture was stirred for 5 h and poured onto methanol (300 ml). The resultant precipitate was filtered off and saponified with potassium carbonate in ethanol (5% water) under reflux for over night. After cooling, water (50 ml) was added and the product was extracted with dichloromethane, dried (MgSO 4 ), concentrated and purified by column chromatography on silica gel using dichloromethane and petroleum spirit (1 : 1) as eluent and then recrystallised from ethanol to yield a white solid (3.59 g, 67%). Found: C, 77.30, H, 9.85, C 48 H 72 O 6 requires C, 77.38, H, 9.74; δ H (CHC1 3 ) 7.96 (s, 1H, ArH), 7.83-7.82 (m, 4Η, ArH), 7.77 (s, 1Η, ArH), 5.92 (1Η, s, OH), 4.31-4.18 (m, 10Η, OCH 2 ), 1.99-1.92 (m, 10Η, CH 2 ), 1.58-1.55 (m, 10Η, CH 2 ), 1.46-1.38 (m, 20Η, CH 2 ), 0.97-0.83 (15H, m, CHj). Example 17 Acetic acid 2-hydroxy-3,6,7,l 0,1 l-pentahexyloxytriphenylene ester Acetic acid 2-hydroxy-3,6,7, 10,1 l-pentahexyloxytriphenylene ester (7) can be separated before the saponification step in the preparation of (6) as a white solid. Found: C, 76.20, H, 9.60, C 50 H 74 O 7 requires C, 76.30, H, 9.48; δ H (CHCl 3 ) 8.08 (s, 1H, ArH), 7.86 (d, 2Η, J 4.0, ArH), 7.82 (d, 2Η, J 2.6, ArH), 7.77 (1Η, s, ArH), 4.26- 4.19 (m, 10Η, OCH 2 ), 2.41 (s, 3Η, OCOCHj), 1.98-1.86 (m, 10Η, CH 2 ), 1.58-1.57 (m, 10Η, CH 2 ), 1.42-1.32 (m, 20Η, CH 2 ), 0.96-0.88 (m, 15H, CH). MS (El), 786 (M + , 89%), 744 (82%), 660 (1 1%), 491 (5%), 407 (7%), 324 (5%), 295 (10%), 43 (100%). Example 18 Hexanoic acid 2-hydroxy-3,6,7,10,l l-pentahexyloxytriphenylene ester Hexanoyl chloride (0.10 g, 0.78 mmol) was added to 2-hydroxy-3,6,7,10,l l- pentahexyloxytriphenylene (0.29 g, 0.39 mmol) in pyridine (1 ml). The reaction mixture was stirred for 3 hours at room temperature. Water (5 ml) was then added and the product was extracted with dichloromethane, dried (MgS0 ), concentrated, and purified by column chromatography on silica gel using dichloromethane and petroleum spirit (1 : 1) as eluent and then recrystallised from ethanol as a white solid (0.26 g, 79%). Found: C, 76.75, H, 9.90, C 54 H 82 0 7 requires C, 76.92, H, 9.80; δ H (CHC1 3 ) 8.07 (s, 1H, ArH), 7.86 (s, 2Η, ArH) 7.81 (2Η, d J3.0, ArH) 7.77 (1Η, s, ArH) 4.26-4.19 (m, 10Η, OCH 2 ), 2.67 (2Η, t J 7.5, OCH 2 ) 2.02-1.83 (m, 12Η, CH>J, 1.65-1.35 (m, 34Η, CH 2 ), 0.99-0.89 (18H, m, CH 3 ). MS (El), 842 (MM, 100%), 744 (62%), 660 (9%), 491 (6%), 407 (6%), 323 (10%), 99 (12%), 71 (10%). Example 19 Biphenyl-4-carboxylic acid 2-hydroxy-3,6,7,10,l l-pentahexyloxytriphenylene ester 4-Biphenylcarbonyl chloride (0.17 g, 0.78 mmol) was added to 2 -hydro xy- 3,6,7,10,1 l-pentahexyloxytriphenylene (0.29 g, 0.39 mmol) in pyridine (1 ml). The reaction mixture was stirred for 3 h. at room temperature. Water (5 ml) was then added and the product was extracted with dichloromethane, dried (MgS0 4 ), concentrated, and purified by column chromatography on silica gel using dichloromethane and petroleum spirit (1 :2) as eluent and then recrystallised from ethanol as a grey solid (0.30 g, 83%). Found: C, 79.45, H, 8.75, C 6 ,H 8 o0 7 requires C, 79.18, H, 8.71 ; δ H (CHCl 3 ) 8.37 (d, 2H, J 8.4 ArH), 8.23 (s, 1 Η, ArH) 7.92-7.69 (8Η, m, ArH) 7.55-7.36 (4Η, m, ArH) 4.28-4.18 (m, 10Η, OCH 2 ), 1.98-1.87 (m, 8Η, CH 2 j, 1.83-1.70 (2Η, m, CH 2 ), 1.62-1.15 (m, 30H, CH 2 ), 0.98-0.78 (15Η, m, CHj). MS (El), 924 (M + -l , 100%), 744 (61%), 660 (5%), 295 (6%), 181 (89%), 153 (9%). Example 20 4-Nitrobenzoic acid 2-hydroxy-3,6,7,10,ll-pentahexyloxytriphenylene ester 4-Nitrobenzoyl chloride (0.15 g, 0.81 mmol) was added to 2-hydroxy-3,6,7, 10, l 1 - pentahexyloxytriphenylene (0.40 g, 0.54 mmol) in pyridine (1 ml). The reaction mixture was stirred for 3 h. at room temperature. Water (5 ml) was then added and the product was extracted with dichloromethane, dried (MgS0 4 ), concentrated, and purified by column chromatography on silica gel using dichloromethane and petroleum spirit (1 :2) as eluent and then recrystallised from ethanol as a yellow solid (0.40 g, 83%). Found: C, 74.0, Η, 8.45, N, 1.40, requires C, 73.88, Η, 8.45, N, 1.57; δ Η (CΗCl 3 ) 8.48 (d, 2H, J 8.6 ArH), 8.41 (d, 2Η, J 8.6, ArH) 8.22 (1Η, s, ArH) 7.92 (1Η, s, ArΗ), 7.88 (1Η, s, ArΗ), 7.82 (2Η, d, J 3, ArH), 7.79 (1H, m, ArH), 4.28-4.18 (m, 10Η, OCH 2 ), 1.98-1.92 (m, 8Η, CH ? 1.78-1.70 (2Η, m, CH 2 Λ 1.62-1.10 (m, 30Η, CH 2 ), 0.98-0.78 (15H, m, CH 3 ). ); MS (FAB), 895 (M + +l , 32%), 880 (11%), 811 (12%), 747 (14%), 660 (9%) 311 (94%), 150 (100%). Example 21 3,5-Dinitrobenzoic acid 2-hyciroxy -3,6,7,10,1 l-pentahexyloxytriphenylene ester 3,5-Dinitrobenzoyl chloride (0.17 g, 0.75 mmol) was added to 2-hydroxy- 3,6,7,10,1 l-pentahexyloxytriphenylene (0.28 g, 0.38 mmol) in pyridine (1 ml). The reaction mixture was stirred for 3 h. at room temperature. Water (5 ml) was then added and the product was extracted with dichloromethane, dried (MgS0 ), concentrated, and purified by column chromatography on silica gel using dichloromethane and petroleum spirit (1 :2) as eluent and then recrystallised from hexane as a yellow solid (0.30 g, 85%). Found: C, 70.45, H, 8.10, N, 2.70, C 55 H 74 N 2 0,ι requires C, 70.34, H, 7.94, N, 2.98; δ H (CHC1 3 ) 9.36 (s, 2H, ArH), 9.24 (s, 1Η, ArH), 8.26 (1Η, s, ArH) 7.92 (1Η, s, ArΗ), 7.88 (1Η, s, ArΗ), 7.83 (1Η, s, J 3, ArΗ), 7.82 (1Η, s, ArH), 7.78 (1Η, s, ArH), 4.28-4.18 (m, 10Η, OCH 2 ), 2.02-1.92 (m, 8Η, CH 2 ), 1.87-1.75 (2H, m, CH 1.69-1.18 (m, 30Η, CH 2 ), 0.99-0.81 (15Η, m, CH 3 ). MS (El), 938 (MM, 27%), 878 (41%), 744 (52%), 660 (9%), 415 (10%), 149 (100%). Example 22 4-Cyanobenzoic acid 2-hydroxy-3,6,7,10,l l-pentahexyloxytriphenylene ester 4-Cyanobenzoyl chloride (0.10 g, 0.59 mmol) was added to 2-hydroxy-3,6,7,10,l 1- pentahexyloxytriphenylene (0.22 g, 0.29 mmol) in pyridine (1 ml). The reaction mixture was stirred for 3 h. at room temperature. Water (5 ml) was then added and the product was extracted with dichloromethane, dried (MgS0 ), concentrated, and purified by column chromatography on silica gel using dichloromethane and petroleum spirit (2: 1) as eluent and then recrystallised from ethanol as a pale yellow solid (0.22 g, 87%). Found: C, 77.20, H, 8.70, N, 1.60, C 56 H 75 N0 7 requires C, 76.94, H, 8.65, N, 1.60; δ H (CHCl 3 ) 8.41 (d, IH, J 1.9, ArH), 8.39 (d, 1Η, J 1.9, ArH), 8.20 (s, 1Η, ArH), 7.91 (s, 1Η, ArH), 7.87 (s, 2Η, ArH), 7.86-7.83 (3Η, m, ArH), 7.78 (s, 1Η, ArΗ), 4.28-4.18 (m, 10Η, OCH 2 ), 1.99-1.89 (m, 8Η, CH 2 ), 1.78-1.73 (2H, m, CH 2 J, 1.57-1.52 (m, 10Η, CH 2 ), 1.44-1.35 (m, 16Η, CH 2 1.25-1.17 (m, 4Η, CH 2 ), 0.96-0.85 (m, 12H, CH 3 ). 0.81 (3H, t, J 7.2, CH 3 ). ); MS (FAB), 874 (M + , 100%), 789 (12%), 744 (21%), 660 (8%), 322 (7%). Example 23 4-FIuorobenzoic acid 2-hydroxy-3,6,7,10, 11 -pentahexyloxytriphenylene ester 4-Fluorobenzoyl chloride (0.09 g, 0.59 mmol) was added to 2-hydroxy-3, 6,7, 10,1 1- pentahexyloxytriphenylene (0.22 g, 0.29 mmol) in pyridine (1 ml). The reaction mixture was stirred for 3 h. at room temperature. Water (5 ml) was then added and the product was extracted with dichloromethane, dried (MgS0 4 ), concentrated, and purified by column chromatography on silica gel using dichloromethane and petroleum spirit (2: 1) as eluent and then recrystallised from ethanol as a white solid (0.21 g, 85%). Found: C, 76.05, H, 8.95, requires C, 76.18, H, 8.72; δ H (CHC1 3 ) 8.34-8.30 (m, 2H, ArH), 8.20 (s, 1Η, ArH), 8.91-8.79 (m, 5Η, ArH), 7.26- 7.20 (m, 2Η, ArH), 4.27-4.17 (m, 10Η, OCH 2 ), 1.98-1.90 (m, 8Η, CH 2 1.79-1.72 (2Η, m, CH 2 1.59-1.50 (m, 10Η, CH 2 ), 1.44-1.35 (m, 16Η, CH 2 ), 1.25-1.17 (m, 4H, CH>λ 0.96-0.85 (m, 12Η, CH 5 ). 0.81 (3Η, t, J 7.2, CH 3 ). ); MS (El), 866 (MM , 62%), 782 (5%), 744 (14%), 123 (100%), 95 (11%). Example 24 1-Naphthoic acid 2-hydroxy-3,6,7,10,l l-pentahexyloxytriphenylene ester 1-Naphthoyl chloride (0.09 g, 0.46 mmol) was added to 2-hydroxy-3,6,7,10,l 1- pentahexyloxytriphenylene (0.17 g, 0.23 mmol) in pyridine (1 ml). The reaction mixture was stirred for 3 h. at room temperature. Water (5 ml) was then added and the product was extracted with dichloromethane, dried (MgS0 ), concentrated, and purified by column chromatography on silica gel using dichloromethane and petroleum spirit (1 :2) as eluent and then recrystallised from ethanol as a grey solid (0.16 g, 80%). Found: C, 78.55, Η, 8.95, C 59 Η 78 0 7 requires C, 78.80, FI, 8.74; δ H (CHCI 3 ) 9.11 (d, J 8.1, IH, ArH), 8.59 (d, J 7.3, 1Η, ArH), 8.26 (1Η, s, ArH) 8.13 (1Η, d, J 8.1 ArΗ), 7.97-7.82 (5Η, m, ArH), 7.66-7.59 (4H, m, ArH), 4.28-4.18 (m, 10H, OCH 2 ), 2.17-1.92 (m, 8Η, CH 2 ), 1.90-1.77 (2H, m, CH 2 ), 1.58-1.10 (m, 30H, CH 2 ), 0.97-0.81 (12H, m, CHj). 0.75 (3Η, t, J 7.0 CH 5 ); MS (El), 898 (MM, 100%), 744 (27%), 658 (6%), 279 (8%), 155 (90%). Example 25 2-Naphthoic acid 2-hydroxy-3,6,7,10,l l-pentahexyloxytriphenylene ester 2-Naphthoyl chloride (0.13 g, 0.67 mmol) was added to 2-hydroxy-3,6,7,10,l 1- pentahexyloxytriphenylene (0.25 g, 0.34 mmol) in pyridine (1 ml). The reaction mixture was stirred for 3 h. at room temperature. Water (5 ml) was then added and the product was extracted with dichloromethane, dried (MgS0 4 ), concentrated, and purified by column chromatography on silica gel using dichloromethane and petroleum spirit (1 :2) as eluent and then recrystallised from ethanol as a pale yellow solid (0.24 g, 81%). mp 162 °C. Found: C, 78.70, Η, 8.75, C 59 Η 78 0 7 requires C, 78.80, H, 8.74; δ H (CHCl 3 ) 8.91 (s, IH, ArH), 8.31-8.28 (m, 2Η, ArH), 8.06-7.82 (m, 7Η, ArH), 7.67-7.60 (m, 3Η, ArH), 4.28-4.18 (m, 10Η, OCH 2 ), 1.98-1.92 (m, 8Η, CH 2 ), 1.89-1.73 (2Η, m, CH 2 ), 1.58-1.10 (m, 30H, CH 2 , 0.97-0.81 (12Η, m, CH 3 ). 0.71 (3Η, t, J 7.0 CH 3 ); MS (El), 898 (MM, 79%), 744 (36%), 323 (6%), 273 (9%), 155 (100%). Example 26 1 ,4-difluoro-2,3,6,7,l 0, 11 -hexakis(hexyloxy)triphenylene a) l,4-difluoro,2-hexyloxybenzene 2,5-Difluorophenol (23g, 0.172mol) was dissolved in dry, distilled ethanol (300ml) under a stream of nitrogen. 1 -Bromohexane (31.75g, 0.193mol, 1.2eq) and potassium carbonate (133g, 0.964mol, 5.5eq) were added and the reaction mixture was stirred vigorously under reflux for 4 days. Dichloromethane (300ml) was added to the straw coloured mixture, which was then filtered through a bed of celite to remove the potassium carbonate. The filtrate was washed with water (3x100ml), and dried with magnesium sulphate. Removal of the solvent in vacuo yields 34.07g of pale brown oil. This was distilled under reduced pressure to yield a colourless oil (29.22g, 77%), bp 70°C @ 0.7mmHg; (Found: C, 67.35; H, 7.55. Cι 2 H ! 6 OF 2 requires C, 67.3; H, 7.53; O, 7.47; F, 17.76%); v^filmVcm "1 3090 (C-H unsat.), 2932 (C-H aliph.), 1832 (C=C); δ H (300 MHz; CDC1 3 ) 0.90 (3 H, t, 3 J(H,H)=7Hz, -CH 3 ), 1.33 (4 Η, m, 2 x -CH 2 -), 1.35 (2 Η, septet, 3 J(Η,Η)=7Ηz, -CH 2 CH 2 CH 2 0-Ar), 1.81 (2 H, quintet, 3 J(H,H)=7Hz, -CH 2 CH 2 CH 2 0-Ar), 3.98 (2 H, t, 3 J(H,H)=7Hz, -CH 2 CH 2 0- Ar), 6.56 (Η, dddd, 3 J(Η,F)=10.8, 4 J(H,F)=5.3, 4 J(H,H)=2.4, 5 J(H,H)=0.7Hz, C 6 H), 6.67 (Η, dddd, 3 J(Η,F)=10.8, 3 J(H,H)=9.0, 4 J(H,F)=5.3, 4 J(H-H)=2.4Hz, C 4 H), 6.99 (Η, dddd, 3 J(Η,F)=10.8, 3 J(H,H)=9.0, 4 J(H,F)=5.3, 5 J(H,H)=0.7Hz, C 3 H); m z 214 (M + , 19%), 130 (M + -alkoxy chain, 100%), 43 (56%). b) l,4-difluoro,2-hexyloxybenzene-l-boronic acid 1 ,4-Difluoro-2-hexyloxybenzene (29.22g, 0.137mol) was stirred in tetrahydrofuran (150ml) under anhydrous conditions. The solution was cooled to -78°C under a stream of dry nitrogen and butyl-lithium (1.6M in hexanes, 81ml, 0.129mol) was added drop- wise via cannular over 60 minutes. Stirring was continued for 3 hours at -78°C. The reaction was then quenched (at -78°C over 30min) with a solution of tri- methylborate (13.23g, 0.129mol) in tetrahydrofuran (200ml). The cooling bath was then removed, and the reaction mixture was stirred overnight at room temperature overnight. Upon addition of hydrochloric acid (10%, 90ml) the white suspension dissolved to produce a straw coloured solution. Stirring was continued for lhour and then the tetrahydrofuran was removed in vacuo to yield a colourless oil which crystallised rapidly, forming white crystals (49g). These crystals were dissolved in ether (250ml), washed with water (3x100ml) and dried with magnesium sulphate. Removal of the solvent yielded white crystals of the title compound (48g), which were used without further purification. c) 3,6-difluoro-2-hexyloxyphenol White crystals of l,4-difluoro-2-hexyloxybenzene-l -boronic acid (48g) were dissolved in warm toluene (150ml) and hydrogen peroxide (43ml, 30%>) was added drop-wise. Heating was continued for 45min at 100°C. Once the solution had cooled to room temperature water was added (50ml) and the layers were separated. The toluene layer was washed with ferrous ammonium sulphate (10%), 2x50ml) and water (2x50ml). The combined organic extracts were dried with magnesium sulphate, filtered and the solvent was removed to yield crude 3,6-difluoro,2- hexyloxyphenol as a pale yellow oil (31.67g, 100%>). The crude product was dissolved in toluene (150ml), extracted with sodium hydroxide solution (10%w/v in methanol, 3x50ml). The purple, aqueous extract, containing the phenoxide anion of the product, was then re-acidified with concentrated HC1 until all of the colour had been displaced (pH~4). The phenol was then extracted with dichloromethane (3x100ml), washed with water (3x50ml), dried with magnesium sulphate and filtered. Removal of the solvent in vacuo yielded the required product as an orange/brown oil (27.2g, 87%). Kugelrohr distillation was performed under reduced pressure (2mbar), the colourless distillate collected when the oven temp was 100°C was found to contain only 4 (26.5g, 82%), (Found: C, 62.65; H, 6.9. C, 2 H 16 0 2 F 2 requires C, 62.6; H, 6.9; O, 13.91 ; F, 16.52%); v max (film)/cm-' 3524 and 2932 (C-H aliph), 2300 (C=C); δ H (300 MHz; CDC1 3 ) 0.90 (3 H, t, 3 J(H,H)=7Hz, -CH 3 ), 1.32 (4 Η, m, 2 x -CH 2 -), 1.34 (2 Η, septet, 3 J(Η,Η)=7Ηz, -CH 2 CH 2 CH 2 0-Ar), 1.76 (2 H, quintet, 3 J(H,H)=7Hz, -CH 2 CH 2 CH 2 0-Ar), 4.17 (2 H, t, 3 J(H,H)=7Hz, -CH 2 CH 2 0- Ar), 5.70 (1 Η, s, -OH, removed with D 2 0), 6.58 (1 Η, ddd, 3 J(Η,F)=13.3, 3 J(H,H)=7.4, 4 J(H,F)=4.5Hz, C 3 H), 6.74 (1 Η, ddd, 3 J(Η,F)=18.3, 3 J(H,H)=7.4, 4 J(H,F)=4.6Hz, C 4 H); δ c (75 MHz Η{BB}, INEPT; CDC1 3 ) 14.31 (CH 3 ), 22.91 (CH 2 ), 25.78 (CH 2 ), 30.34 (CH 2 ), 31.87 (CH 2 ), 74.90 (CH 2 ), 106.65 (CH, dd, 2 J(C,F)=15.1 , 3 J(C,F)=8.4Hz, C 4 ), 1 10.75 (CH, dd, 2 J(C,F)=15.1 , 3 J(C,F)=8.4Hz, C 5 ), 135.67 (C, dd, 2 J(C,F)=15.1, 3 J(C,F)=8.4Hz, C,), 138.42 (C, dd, 2 J(C,F)=15.1, 3 J(C,F)=8.4Hz, C 2 ), 147.65 (C, dd, *J(C,F)=239, 4 J(C,F)=2.6Hz, C 6 ), 151.7 (C, dd, 'J(C,F)=248, 4 J(C,F)=2.6Hz, C 3 ); m/z 230 (M + , 10%), 146 (M + -alkoxy chain, 100%), 43 (50%). d) l,4-difluoro-2,3-dihexyloxybenzene 3,6-Difluoro-2-hexyloxyphenol (25g, O.l lmol) was dissolved in dry, distilled ethanol (350ml) under a stream of nitrogen. 1 -Bromohexane (45.35g, 0.275mol, 2.2eq) and potassium carbonate (75. lg, 0.54mol, 5.5eq) were added and the reaction mixture was stirred vigorously under reflux for 2 days. Dichloromethane (300ml) was added to the orange reaction mixture, which was then filtered through a bed of celite to remove the potassium carbonate. The filtrate was washed with water (3x100ml), and dried with magnesium sulphate. Removal of the solvent in vacuo yields 24.07g of pale brown oil. This was distilled under reduced pressure to yield a colourless oil (18.82g, 80%), bp 102°C, 0.2mbar; (Found: C, 68.8; H, 9.05. C, 8 H 28 0 2 F 2 requires C, 68.76; H, 8.98; O, 10.18; F, 12.08%); v max (film)/cm-' 2956 and 2860 (C-H aliph), 2361 (C=C); δ H (300 MHz; CDC1 3 ) 0.90 (3 H, t, 3 J(H,H)=7Hz, -CH 3 ), 1.33 (4 Η, m, 2 x -CH 2 -), 1.46 (2 Η, septet, 3 J(Η,Η)=7Ηz, -CH 2 CFI 2 CH 2 0-Ar), 1.76 (2 H, quintet, 3 J(H,H)=7Hz, -CH 2 CH 2 CH 2 0-Ar), 4.08 (2 H, t, 3 J(H,H)=7Hz, -CH 2 CH,0-Ar), 6.73 (2 Η, dd, 3 J(Η,F)=14.5, 4 J(H,F)= 7.2Hz, C 5,6 H); δ c (75 MHz 1H{BB}, INEPT; CDC1 3 ) 14.41 (CH 3 ), 23.01 (CH 2 ), 25.87 (CH 2 ), 30.45 (CH 2 ), 31.98 (CH 2 ), 74.99 (CH 2 ), 110.15 (CH, dd, 2 J(C,F)=17.7, 3 J(C,F)=4.3Hz, C 5,6 ), 141.94 (C, dd, 2 J(C,F)=1 1.0, 3 J(C,F)=7.0Hz, C 2,3 ), 153.12 (C, dd, 'j(C,F)=244.2, 4 J(C,F)=3.6Hz, Cι ,4 ); m/z (FAB+); 314 (M + , 99%), 146 (M + -alkoxy chains, 100%), 85 (79), 55 (40%). e) 2,5-difluoro-3,4-dihexyloxybenzene-l-boronic acid l,4-Difluoro-2,3-dihexyloxybenzene (1 1.2g, 0.036mol) was stirred, under nitrogen, in anhydrous tetrahydrofuran (150ml). The reaction mixture was cooled to -78°C and then butyl lithium (1.6M in hexanes, 24.38ml, 0.039mol) was added via cannular over one hour. Stirring was continued at -78°C for 2 hours. This temperature was maintained whilst a solution of trimethylborate (4.05g, 0.039mol) in dry tetrahydrofuran (100ml) was added drop- wise. The cooling bath was then removed and the reaction was stirred overnight at room temperature. Addition of HCl (IM, 36ml) dissolved the white suspension and a yellow solution was formed. Extraction was performed with toluene (2x100ml), the combined organics extracts were then washed with water (2x50ml), dried with magnesium sulphate. Removal of the drying agent by filtration and the solvent in vacuo yielded a brown oil containing the crude product (11.95g, 93%>). The product was used in the next step without further purification. f) Pinacol ester of 2,5-difluoro-3,4-dihexyloxybenzene-l-boronic acid The crude 2, 5-difluoro-3,4-dihexyloxybenzene-l -boronic acid (1 1.95g as brown oil) was dissolved in tetrahydrofuran (100ml). Concentrated sulphuric acid (3 drops) and pinacol (3.92g, 0.033mol) were then added and the solution was heated to reflux overnight under a protective dry nitrogen atmosphere. The cool solution was filtered to remove any insoluble impurities and the solvent was removed in vacuo to yield a brown oil. TLC analysis was hampered due to the product spreading and sticking to the silica, purification was affected by Kugelrohr distillation. The title compound was obtained as a colourless, viscous oil (8.1g, 51%), oven temp 150°C, 0.2mbar (Found: C, 65.6; H, 8.7 C 24 H 39 B F 2 0 requires C, 65.46; H, 8.93; B, 2.45; F, 8.63; O, 14.53%); v^filmycm "1 2932 (C-H aliph), 2359 (C=C), 1371 (B-O); δ H (300 MHz; CDC1 3 ) 0.90 (6 H, t, 3 J(H,H)=7Hz, 2 x -CH 3 ), 1.35 (8 Η, m, 4 x -CH 2 -), 1.46 (4 Η, septet, 3 J(Η,Η)=7Ηz, 2 x -CH2CH 2 CH 2 0-Ar), 1.75 (4 H, quintet, 3 J(H,H)=7Hz, 2 x - CH 2 CH 2 CH 2 0-Ar), 4.06 (2 H, t, 3 J(H,H)=7Hz, -CH 2 CH 2 θ-Ar), 4.14 (2 Η, t, 3 J(Η,Η)=7Ηz, -CH 2 CH 2 0-Ar), 6.58 (Η, dd, 3 J(Η,F)=9.9, 4 J(H,F)=5Hz, C 6 H); δ c (75 MHz Η{BB}, INEPT; CDC1 3 ) 14.42 (CH 3 ), 22.99 (CH 2 ), 25.16 (CH 3 , pinacol), 25.83 (CH 2 ), 30.47 (CH 2 ), 31.98 (CH 2 ), 74.90 (CH 2 ), 84.42 (C, pinacol), 1 16.25 (CH, dd, 2 J(C,F)=20.14, 3 J(C,F)=9.6Hz, C 6 ), 141.44 (C, dd, 2 J(C,F)=15.6, 3 J(C,F)-4.0Hz, C 3 ), 144.71 (C, dd, 2 J(C,F)=13.2, 3 J(C,F)=5.0Hz, C 4 ), 152.3 (C, d, 1 J(C,F)=246.1Hz, C 2 ), 157.4 (C, d, 1 J(C,F)=248.17; m/z 440 (M + , 12%), 272 (M + - both alkyl chains, 57%), 212 (65%), 43 (100%). g) 3,4,-dibromo-l,2-dihexyloxybenzene 1 ,2-Dihexyloxybenzene (35g, 0.126mol) was stirred in anhydrous dichloromethane (250ml) at 0°C to which was added iron powder (lg, cat) and iodine (0.5g, cat). The reaction vessel was fitted with a trap containing sodium hydroxide and nitrogen was bubbled through the reaction mixture to remove the HBr produced. Elemental bromine (50g, 0.3 Mmol, 2.5eq) in dichloromethane (250ml) was added drop wise from an addition funnel over 2 hours, the temperature being maintained at 0°C. After addition was complete, stirring was continued at room temperature overnight. Saturated sodium metabisulphate solution (200ml) was added and the product was extracted with dichloromethane (2x250ml). The combined organic extracts were washed with water (2x100ml), dried with magnesium sulphate and filtered. Removal of the solvent in vacuo yields a brown oil. Filtration through a short silica column using 1 : 1 toluene: dichloromethane as eluant removed the coloured impurities. The solvent was removed in vacuo to yield 3,4-dibromo-l,2-dihexyloxybenzene as a colourless oil (45.9g, 95%); (Found: C, 50.1; H, 6.4;. C 18 H 28 0 Br 2 requires: C, 49.7; H, 6.47; O, 7.34; Br, 36.63%); v max (fιlm)/cm " ' 2931 and 2859 (C-H aliph), 2360 (C=C), 652 (C-Br); δ H (300 MHz; CDC1 3 ) 0.90 (6 H, t, 3 J(H,H)=7Hz, 2 x -CH 3 ), 1.33 (8 Η, m, 4 x -CH 2 -), 1.45 (4 Η, septet, 4 J(Η,Η)=7Ηz, 2 x -CH 2 CH 2 CH 2 0-Ar), 1.77 (4 H, quintet, 3 J(H,H)=7Hz, 2 x -CH 2 CH 2 CH 2 0-Ar), 3.91 (4 H, t, 3 J(H,H)=7Hz, 2 x - CH 2 CH 2 0-Ar), 7.06 (2 Η, s); δ c (75 MHz Η{BB}, INEPT; CDC1 3 ) 14.42 (CH 3 ), 22.99 (CH 2 ), 26.01 (CH 2 ), 29.50 (CH 2 ), 31.92 (CH 2 ), 69.82 (CH 2 ), 1 15.03 (C, C ,5 ), 1 18.29 (CH, C 3>6 ), 149.40(C, C,, 2 );m/z 436 (M + , 16%), 352 (M + - C 6 H 12 , 11%), 268 (MM x C 6 Hι 2j 85%), 43 (100%). h) 3',6'-difluoro-3,4,4',5',3",4"-hexakishexyloxy[l,l':2 , ,r , ]terphenyI l,2-Dibromo-3,6-difluoro-4,5-dihexyloxybenzene (0.5mmol.) and Pd(PPh 3 ) (3mol% Pd(0), per bromine atom) were stirred in degassed DME (50ml) under argon. The pinacol boronate ester (3,4-dihexyloxybenzene boronic acid, 1.5mmol) was dissolved in toluene, degassed, and after about 15 minutes was added to the reaction by cannular. A suspension of barium hydroxide (1.5mmol.) in water (2.5ml) was degassed and added directly to the reaction. The reaction was carried out under argon at 80°C, for 21 hours, and then allowed to cool, water was added. The mixture was extracted with ether, the extracts were washed with saturated sodium chloride solution (2 x 50ml), water (2x50ml), dried (Na 2 S0 4 ), and the solvent removed in vacuo to leave a red, viscous oil (-80 %). This was subjected to column chromatography on silica gel using petroleum ether/ ethyl acetate as the eluting solvent (using a gradient of 9: 1 initially to 4: 1 finally) (Found: C, 74.65; H, 9.8;. C 54 H 84 0 6 F 2 requires: C, 74.79; H, 9.76; O, 11.07; F, 4.38%); v max (film)/cm " ' 2931 and 2859 (C-H aliph), 2360 (C=C); δ H (300 MHz; CDC1 3 ) 0.9048 (18 H, t, J=7Hz, 9 x -Me), 1.3340 (36 H, m, 18 x -CH 2 -), 1.5664 (4 H, quint, J=7Hz, 2 x - CH 2 CH 2 CH 2 0-Ar), 1.6672 (4 H, quint, J=7Hz, 2 x -CH 2 CH 2 CH 2 0-Ar), 1.7906 (4 H, quint, J=7Hz, 2 x -CH 2 CH 2 CH>0-Ar), 3.6982 (4 H, t, J=7Hz, 2 x -CH 2 CH 2 0-Ar), 3.9253 (4 Η, t, J=7Ηz, 2 x -CH 2 CH 2 0-Ar), 4.1342 (4 Η, t, J=7Ηz, 2 x -CH 2 CH 2 0- Ar), 6.5294 (Η c , 2 H, d, J=1.81Hz, coupled: p to H a ), 6.6261 (H a , 2 H, dd, J=8.235, 1.81Hz, coupled: o to H b , m to H c ); δ c (75 MHz Η{BB}, INEPT; CDC1 3 ) 14.43 (6 x CH 3 ), 23.04 (6 x CH 2 ), 26.08 (2 x CH 2 ), 26.12 (4 x CH 2 ), 29.47 (2 x CH 2 ), 29.65 (4 x CH 2 ), 30.55 (2 x CH 2 ), 31.99 (2 x CH 2 ), 32.03 (2 x CH 2 ), 69.36 (2 x CH 2 OAr), 69.51 (2 x CH 2 OAr), 75.20 (2 x CH 2 OAr) 113.07 (CH, s, C 2>2 »), 1 17.1 1(CH, s, C 6,6 "), 123.83 (C, s, C 5 ,5")» 124.48 (C, dd , 2 J F-c =10.5Hz, 3 J F . c =9.5Hz, C r>2 -), 126.03 (C, s, Ci,]-), 140.83 (CF, dd, 4 J F-c =7.5Hz, C 3 -, 6 -), 148.63 (C, s, C 4 , 4 » ), 148.69 (C, s, C 3>3 "), 151.92 (C, s (low intensity), C 4 -, 5 '): m/z (FAB+) 867 (M + , 100%). i) 1, 4-difluoro-2,3, 6,7,10,1 l-hexakis(hexyloxy)triphenylene The terphenyl of example 26 h) (0.5mmol) was stirred in dry dichloromethane (50ml). Iron (III) chloride (lmmol) was weighed and added to the reaction flask under an inert atmosphere. The reaction mixture turned a deep green colour and was stirred at room temperature until no starting material remained (TLC (1 : 1 dichloromethane/ petroleum spirit) on small portions following methanol work up). The reaction mixture was worked up by pouring onto methanol (anhydrous, 50ml). To the resulting, brown solution, was added water (50ml) and dichloromethane (50ml). The layers were extracted with dichloromethane, washed with ferrous ammonium sulphate (5% solution, 50ml) and water (2x50ml). Drying over magnesium sulphate, filtration and removal of solvent in vacuo yielded a red to purple solid. The purple solid was dissolved in dichloromethane and filtered through a bed of silica, removal of solvent yielded a sticky off-white solid. The product was recrystallised from ethanol and dried in glass (Yield >85%). The melting point of the solid was below room temperature (Found: C, 74.7; H, 9.7;. C 54 H 84 0 6 F 2 requires: C, 74.96; H, 9.76; O, 11.07; F, 4.38%); δ H (300 MHz; CDC1 3 ) 0.9286 (18 H, t, J=7Hz, 6 x -Me), 1.380 (24 H, m, 12 x -CH 2 -), 1.57 (12 H, m, 6 x -CH 2 CH 2 CH 2 0-Ar), 1.860 (4 H, quint, J=7Hz, 2 x -CH 2 CH 2 CH 2 0-Ar), 1.918 (8 H, quint, J=7Hz, 4 x - CH 2 CH 2 CH 2 0-Ar), 4.19 (4 H, t, J=7Hz, 2 x -CH 2 CH 2 0-Ar), 4.224 (8 Η, t, J=7Ηz, 4 x -CH 2 CH 2 O-Ar), 7.81 (Η b , 2 H, s), 8.47 (H a , 2 H, t, J=3.01Hz, nOe coupling to ,9 F); 14.07 (6 x CH 3 ), 22.66 (6 x CH 2 ), 25.58 (2 x CH 2 ), 25.81 (4 x CH 2 ), 29.23 (2 x CH 2 ), 29.33 (4 x CH 2 ), 30.21 (2 x CH 2 ), 31.66 (2 x CH 2 ), 31.68 (2 x CH 2 ), 69.06 (2 x CH 2 OAr), 69.50 (2 x CH 2 OAr), 75.14 (2 x CH 2 OAr) 106. 70 (CH, s, C 8j9 ), 1 1 1.43 (CH, m, nOe coupling to 19 F, C 5)12 -), 1 15.49 (C, m, C 4a ,i2b), 120.68 (C, s, C 4b , 12a ), 124.84 (C, s, C 8a>8 b), 139.44 (C, m, C 2 , 3 ), 148.53 (C, s, C 7, ιo), 149.14 (C, s, C 6 ,„), 152.40 (C, m, (low intensity), C ); m/z (FAB+) 866 (M + , 100%). P36278W0.6

Claims: Claims 1. A mixture comprising a molecule of formula I; Formula in which Ai, A 2 , A , A 4 , A 5 and A 6 , which may be the same or different, are each N or -CH; Yi, Y 2 , Y.3, Y 4 , Y5 and Y 6 , which may be the same or different, are each hydrogen or Ci to C12 alkoxy; Xi, X , X 3 , X 4 , X5 and X 6 , which may be the same or different, are each hydrogen, d to C] 2 alkoxy or alkyl Cj to C 12 ; and R , R 8 , R9, Rio, RΠ and R [ are each hydrogen, or each of R 7 and R 8 , R9 and Rio and Rn and Rι 2 may form a bond; and a molecule of formula II; Formula II in which Ri, R 2 , R 3 , R , R5 and R 6 , which may be the same or different, are each alkyl or substituted (and/or chiral) alkyl Ci to C| 6 , acyl C| to Cι 6 , polyethyleneoxy, a flexible connection to a polymer backbone or part of a polymer backbone in homopolymers, copolymers or block copolymers; and B], B 2 , B 3 , B 4 , B 5 and B 6 , which may be the same or different, are each, hydrogen, alkyl Ci to C 16 , alkoxy Ci to C !6 , nitro, halogeno, cyano, amido, diazo or ester, e.g. alkyl Ci to C ie ester. 2. A mixture according to claim 1 characterised in that in the compound of formula I each of A l s A 2 , A 3 , A , A 5 and A 6 are the same. 3. A mixture according to claim 2 characterised in that each of Ai, A 2 , A 3 , Ai, A 5 and A 6 is N, and each of Y\, Y 2 , Y 3 , Y 4 , Y 5 and Y 6 represents hydrogen or alkoxy C 3 to C 8 . 4. A mixture according to claim 2 characterised in that each of Ai, A , A 3 , A , A 5 and A 6 is N, and each of X ls X 2 , X 3 , X 4 , X 5 and X 6 is C 2 to C) alkyl or C 4 to Cι alkoxy, 5. A mixture according 1o claim 4 characterised in that each of Xj, X 2 , X 3 , X^ X 5 and X 6 is C 6 to C9 alkyl or C 6 to C9 alkoxy. 6. A mixture according to claim 5 characterised in that each of X l s X 2 , X 3 , X , X 5 and X 6 is either C9 alkyl or C 6 alkoxy. 7. A mixture according to claim 6 characterised in that each of Xi, X 2 , X 3 , X 4 , X 5 and X 6 are the same C 9 alkyl or each of X], X 2 , X 3 , X 4 , X 5 and X 6 are the same C 6 alkoxy. 8. A mixture according to claim 4 characterised in that each of Yi, Y 2 , Y , Y 4 , Y 5 and Yβ is hydrogen and each of Xj, X 2 , X 3 , X , X 5 and X 6 is C 9 alkyl, 9. A mixture according to claim 4 characterised in that each of Yi, Y 2 , Y 3 , Y 4 , Y 5 and Y 6 is C 6 alkoxy and each of X|, X 2 , X 3 , X 4 , X 5 and X 6 is C 6 alkoxy. 10. A mixture according to claim 1 characterised in that each of Ai, A 2 , A 3 , A 4 , As and A 6 is C-H and each of Yi, Y 2 , Y 3 , Y 4 , Y 5 and Y 6 represents hydrogen or alkoxy C 3 to Cs, 11. A mixture according to claim 10 characterised in that each of YI, Y 2 , Y 3 , Y 4 , Y 5 and Y 6 represents hydrogen or alkoxy C 5 to C and 12. A mixture according to claim 1 1 characterised in that each of Y \ , Y 2 , Y 3 , Y 4 , Y 5 and Y 6 represents hydrogen or alkoxy C 6 . 13. A mixture according to claim 1 characterised in that each of Aj, A 2 , A 3 , A 4 , A 5 and A is C-H, and each of Xi, X 2 , X 3 , X 4 , X 5 and X 6 is C 2 to Cj 2 alkyl or C 2 to Cι 2 alkoxy. 14. A mixture according to claim 1 characterised in that each of X|, X 2 , X 3 , , X 5 and X 6 is C 6 to Ci 2 alkoxy. 15. A mixture according to claim 1 characterised in that the compounds of formula I are compounds of formula III; Formula in which Xi, X 2 , X 3 , X , X 5 and X 6 are each the same and are selected from -CgHig , - Cι 2 H 25 , -OC 6 Hi 3 and -OC n H 23 ; and each of Yi, Y 2 , Y 3 , Y 4 , Y 5 and Y 6 are each the same and are selected from hydrogen and -OC 6 Hι 3 . 16. A mixture according to claim 1 characterised in that compounds of formula I are compounds of formula IV; Formula IV in which Xj, X 2 , X 3 , X4, X 5 and X 6 are each the same and are selected from -CgH^ and -OC 6 Hι 3 ; and each of Yi, Y 2 , Y 3 , Y 4 , Y 5 and Y 6 are each the same and are selected from hydrogen and -OC 6 Hι 3 . 17. A mixture according to claim 1 characterised in that in the molecule of formula II each of Ri, R2, R3, R 4 , R 5 and R 6 are the same and B l s B 2 , B 3 , B 4 , B 5 and B 6 are hydrogen. 18. A mixture according to claim 17 characterised in that each of Rj, R 2 , R 3 , R4, R 5 and R are alkyl C3 to Cι 6 , 19. A mixture according to claim 1 characterised in that each of Ri, R 2 , R 3 , R 4 , R 5 and R 6 are alkyl C 4 to C 11. 20. A mixture according to claim 19 characterised in that each of Ri, R 2 , R 3 , R 4, R 5 and Re are C 6 or Ci 1 alkyl. 21. A mixture according to claim 1 characterised in that compounds of formula II are selected from 2,3,6,7,10,1 1 -hexahexyloxytriphenylene and 2,3,6,7,10,1 1- hexaundecyloxytriphenylene. 22. A mixture according to claim 1 characterised in that in the compound of formula II each of Ri, R 2 , R 3 , R 4 , R 5 and R 6 are the same and are alkyl C 3 -C 16 . 23. A mixture according to claim 22 characterised in that each of Ri, R 2 , R 3 , R4, R 5 and R 6 are C 4 -Cπ alkyl. 24. A mixture according to claim 1 characterised in that each of Bj, B 2 , B 3 , and B 4 are hydrogen and each of B 5 and B 6 which may be the same or different, are each hydrogen or fluorine. 25. A mixture according to claim 21 characterised in that the compound of the formula II is 1 , 4-difluoro-2, 3, 6, 7, 10, 1 1 -hexahexyloxytriphenylene. 26. A mixture according to claim 1 characterised in that in the compounds of formula II each of Rj, R2, R 3 , R , R 5 and R 6 are the same or different and are alkyl C 2 -C 1 1 or ethyleneoxy C 3 -C 9 . 27. A mixture according to claim 26 characterised in that each of Ri, R 2 , R 3 , R 4 , R 5 and R 6 are the same and ethyleneoxy C 5 , 28. A mixture according to claim 26 characterised in that each of Ri, R2, R 3 , i, R 5 and R 6 are a combination of ethyleneoxy C 5 and alkyl C 6 . 29. A mixture according to claim 1 characterised in that the compound of formula II is selected from the group 2-(l, 4,7-Trioxaoctyl)-3, 6,7,10,1 1- pentahexyloxytriphenylene, 2,7-Di(l,4,7-trioxaoctyl)-3,6,10,l 1- tetrahexyloxytriphenylene, 2,7,10-Tri(l,4,7-trioxaoctyl)-3,6,l 1- trihexyloxytriphenylene or 2,3,6,7,10,1 l-Hexa(l ,4,7-trioxaoctyl)triphenylene. 30. A mixture according to claim 1 characterised in that the compound of formula II is a side chain substituent in the form shown in formula V. Formula V X is alkyl C J -C J O or an ether oxygen linkage (-0-), and R is hydrogen or methyl. 31. A mixture according to claim 1 characterised in that the compound of formula II as a functionality in polystyrene block copolymers of the form shown in formula VI in which the ratio of n:m is from 6-18: 1. 32. A mixture according to claim 1 characterised in that the compound of formula I is a constituent part of a polymer backbone of formulae VII, the length of the flexible spacer n is between 6 and 18 and the number of molecules of formula II per polymer formula VII, m, is between 2 and 1000. Formula VII 33. A mixture according to claim 1 characterised in that the compound of formula II is part of a block copolymer containing blocks of polyethylene oxide and blocks of formula VII, where the number of molecules of formula I (m) is 10-100 and the number of ethyleneoxide groups in the side chains (n) is 200-500 Formula VIII 34. A mixture according to claim 1 characterised in that the compounds of formula I are selected from the group; 2,3,6,7,10,1 l-hexakis(4-n-nonylphenyl)dipyrazine[2,3-f:2',3'-h]quinoxaline; 2,3,6,7,10,1 l-hexakis-(3,4-dehexyloxyphenyl)dipyrazino[2,3-f:2'3'-h]quinoxaline; 2,3,6,7, 10, 1 1 -hexakis-4(-n-nonylphenyl)-triphenylene; 2,3,6,7,10,1 1 -hexakis-(4-n-dodecylphenyl)triphenylene; 2,3,6,7, 10,1 1 -hexakis-(4-n-hexyloxy-phenyl)-triphenylene; 2,3,6,7, 10,1 1 -hexakis-(4-n-undecyloxy-phenyl)-triphenylene; 2,3,6,7, 10,l l-hexakis-(3,4-n-dihexyloxy-phenyl)-triphenylene; and 2,3,8,9,12,13,18,19,22,23,28,29-dodecakis(hexyloxy)hexabenz[a,c,k,m,v,w] trinaphthylene. 35. A mixture according to claim 1 characterised in that the compounds of formula II are selected from the group; 2,3,6,7,10,1 1 -hexahexyloxytriphenylene, 2,3,6,7,10,1 1 -hexaundecyloxytriphenylene, 1 ,4-difluoro-2,3 ,6,7,10,1 1 -hexahexyloxytriphenylene, 2-(l ,4,7-trioxaoctyl)-3 ,6,7, 10, 1 1 -pentahexyloxytriphenylene, 2,7-di( 1 ,4,7-trioxaoctyl)-3 ,6,10,1 1 -tetrahexyloxytriphenylene, 2,7, 10-tri(l,4,7-trioxaoctyl)-3, 6, 11 -trihexyloxytriphenylene, 2,3 ,6,7, 10,11 -hexa( 1 ,4,7-trioxaoctyl)triphenylene, acetic acid 2-hydroxy-3,6,7,10,l l-pentahexyloxytriphenylene ester, hexanoic acid 2-hydroxy-3,6,7, 10, 11 -pentahexyloxytriphenylene ester, 4-biphenylcarboic acid 2-hydroxy-3,6,7, 10,1 l-pentahexyloxytriphenylene ester, 4-nitrobenzoic acid 2-hydroxy-3 ,6,7, 10,1 l-pentahexyloxytriphenylene ester, 3,5-dinitrobenzoic acid 2-hydroxy-3,6,7, 10, 11 -pentahexyloxytriphenylene ester, 4-cyanobenzoic acid 2-hydroxy-3,6,7, 10,1 l-pentahexyloxytriphenylene ester, 4-fluorobenzoic acid 2-hydroxy-3,6,7,10,l l-pentahexyloxytriphenylene ester, 1 -naphthoic acid 2-hydroxy-3 ,6,7,10,11 -pentahexyloxytriphenylene ester, 2-naphthoic acid 2-hydroxy-3,6,7,10,l 1 -pentahexyloxytriphenylene ester, l,4-difluoro-2,3,6,7,10,l l-hexakis(hexyloxy)triphenylene, and polythenes bearing formula II as a side chain substituent (formula V), polyacrylates bearing formula II as a side chain substituent (formula VI polymers containing formula II as part of the polymer backbone (formula VII), block copolymers containing a central core of polymer with formula II as part of the polymer backbone surrounded by blocks of poly(ethyleneoxide) with molecular weights in the range 750-2000 (formula VIII). 36. A mixture according to claim 1 characterised in that the mixture comprises a compound of formula I selected from the group; 2,3,6,7, 10, l l-hexakis(4-nonylphenyl)dipyrazine[2,3-f:2',3'-h]quinoxaline; 2,3,6,7,10,1 l-hexakis-(4-nonylphenyl)-triphenylene; 2,3,6,7,10,1 l-hexakis-(4-dodecylphenyl)triphenylene; 2,3,6,7,10,1 l-hexakis-(4-hexyloxy-pheny " l)-triphenylene; 2,3,6,7, 10,11 -hexakis-(4-n-undecyloxy-phenyl)-triphenylene; and a compound of formula II selected from the group; 2,3 ,6,7, 10,11 -hexahexyloxytriphenylene, 2,3,6,7,10, 11 -hexaundecyloxy triphenylene, l,4-difluoro-2,3,6,7,10,l l-he>ahexyloxytriphenylene, 2-(l ,4,7-trioxaoctyl)-3,6,7,l 0, 11 -pentahexyloxytriphenylene, 2,7-di( 1 ,4,7-trioxaoctyl)-3 ,6, 10,11 -tetrahexyloxytriphenylene, 2, 7, 10-tri(l, 4, 7-trioxaoctyl)-3, 6, 11 -trihexyloxytriphenylene, 2,3,6,7,10, 1 1 -hexa( 1 ,4,7-trioxaoctyl)triphenylene, acetic acid 2-hydroxy-3,6,7,10,l l-pentahexyloxytriphenylene ester, hexanoic acid 2-hydroxy-3,6,7,10,l l-pentahexyloxytriphenylene ester, 4-biphenylcarboic acid 2-hydroxy-3,6,7, 10,1 l-pentahexyloxytriphenylene ester, 4-nitrobenzoic acid 2-hydroxy-3 ,6,7,10,1 1 -pentahexyloxytriphenylene ester, 3,5-dinitrobenzoic acid 2-hydroxy-3 ,6,7, 10,1 l-pentahexyloxytriphenylene ester, 4-cyanobenzoic acid 2-hydroxy-3,6,7,10,l l-pentahexyloxytriphenylene ester, 4-fluorobenzoic acid 2-hydroxy-3,6,7, 10,1 l-pentahexyloxytriphenylene ester, 1 -naphthoic acid 2-hydroxy-3 ,6,7, 10,1 l-pentahexyloxytriphenylene ester, 2-naphthoic acid 2-hydroxy-3,6,7,10,l l-pentahexyloxytriphenylene ester, l,4-difluoro-2,3,6,7,10,l l-hexakis(hexyloxy)triphenylene, and polythenes bearing formula II as a side chain substituent (formula V), polyacrylates bearing formula II as a side chain substituent (formula VI polymers containing formula II as part of the polymer backbone (formula VII), block copolymers containing a central core of polymer with formula II as part of the polymer backbone surrounded by blocks of poly(ethyleneoxide) with molecular weights in the range 750-2000 (formula VIII). 37. A compound of formula I Formula in which Aι -6 , Xι -6 , Yι-6 and R 7- i2 are as defined in claim 1 provided that the compound of formula I is not 2, 3, 6, 7, 10, 11 - hexakis (4- n- nonylphenyl)dipyrazine [2, 3, -f: 2 ,3 -h] quinoxaline. 38. A compound of formula II selected from the group; 1 , 4-difluoro-2,3, 6,7, 10, 11 -hexahexyloxytriphenylene, 2-( 1 ,4,7-trioxaoctyl)-3 ,6,7,10,11 -pentahexyloxytriphenylene, 2,7-di( 1 ,4,7-trioxaoctyl)-3 ,6, 10,11 -tetrahexyloxytriphenylene, 2,7,10-Tri( 1 ,4,7-trioxaoctyl)-3 ,6, 11 -trihexyloxytriphenylene, acetic acid 2-hydroxy-3,6,7, 10, 11 -pentahexyloxytriphenylene ester, hexanoic acid 2-hydroxy-3 ,6,7,10,1 1 -pentahexyloxytriphenylene ester, 4-biphenylcarboic acid 2-hydroxy-3, 6, 7, 10,1 l-pentahexyloxytriphenylene ester, 4-nitrobenzoic acid 2-hydroxy-3, 6, 7, 10,1 l-pentahexyloxytriphenylene ester, 3,5-dinitrobenzoic acid 2-hydroxy-3, 6, 7, 10,1 l-pentahexyloxytriphenylene ester, 4-cyanobenzoic acid 2-hydroxy-3,6,7, 10,1 l-pentahexyloxytriphenylene ester, 4-fluorobenzoic acid 2-hydroxy-3,6,7, 10,1 l-pentahexyloxytriphenylene ester, 1-naphthoic acid 2-hydroxy-3,6,7,l 0,11 -pentahexyloxytriphenylene ester, l,4-difluoro-2,3,6,7,10,l l-hexakis(hexyloxy)triphenylene, and block copolymers containing a central core of polymer with formula II as part of the 5 polymer backbone surrounded by blocks of poly(ethyleneoxide) with molecular weights in the range 750-2000 (formula VIII). 39. process for the manufacture of a compound of formula I which comprises reacting a hexahalotriphenylene or a hexahaloquinoxaline with a boronic ester of [ 0 formula V; 5 40. We also provide a method of manufacturing a mixture and or a liquid crystal according hereinbefore described which comprises mixing a compound of formula I with a compound of formula II. 41. A mixture according to claim 1 characterised in that the ratio of the 0 compound of formula I to the compound of formula II is substantially 1 : 1. 42. A liquid crystal with a hexagonal columnar phase at a temperature of between less than room temperature and 280°C 5 43. A liquid crystal according to claim 42 characterised in that the liquid crystal comprises a mixture of compounds of formula I and formula II. 44. A liquid crystal according to claim 42 characterised in that the liquid crystal has an alternating stack structure. 45. A liquid crystal according to claim 44 characterised in that the liquid crystal comprises an alternating stack of compounds of formula I and formula II. 46. A liquid crystal which has enhanced low temperature conductivity. 47. The use of a mixture according to claim 1 in the manufacture of a liquid crystal. 48. The use of a compound of formula I in the manufacture of a mixture according to claim 1. 49. The use of a compound of formula II in the manufacture of a mixture according to claim 1. 50. The use of a liquid crystal according to claim 43 as a conducting interconnect in a stacked silicon chip system. 51. The use of a liquid crystal according to claim 43 as a conducting layer in a photoreproductive and/or an electrophotographic system. 52. The use of a liquid crystal according to claim 43 as an active element in an electronic 'nose' array. 53. The use of a liquid crystal according to claim 43 as a conductive element in a spatial light modulator. 54. A mixture or a compound substantially as described with reference to the accompanying examples.

Inventors: ARIKANIEN EKATERINA OLEGOVNA, BODEN NEVILLE, BUSHBY RICHARD JAMES, DONOVAN KEVIN JOHN, HEADDOCK GARETH, KREOUZIS THEODOROS, LIU QUAYLING, LOZMAN OWEN ROGER, LU ZHIBAO, MCNEILL ANDREW PAUL, WOOD ANDREW, ARIKANIEN, EKATERINA, OLEGOVNA, BODEN, NEVILLE, BUSHBY, RICHARD, JAMES, DONOVAN, KEVIN, JOHN, HEADDOCK, GARETH, KREOUZIS, THEODOROS, LIU, QUAYLING, LOZMAN, OWEN, ROGER, LU, ZHIBAO, MCNEILL, ANDREW, PAUL, WOOD, ANDREW
Applicants: ARIKANIEN EKATERINA OLEGOVNA, BODEN NEVILLE, BUSHBY RICHARD JAMES, DONOVAN KEVIN JOHN, HEADDOCK GARETH, KREOUZIS THEODOROS, LIU QUAYLING, LOZMAN OWEN ROGER, LU ZHIBAO, MCNEILL ANDREW PAUL, UNIV LEEDS, WOOD ANDREW, ARIKANIEN, EKATERINA, OLEGOVNA, BODEN, NEVILLE, BUSHBY, RICHARD, JAMES, DONOVAN, KEVIN, JOHN, HEADDOCK, GARETH, KREOUZIS, THEODOROS, LIU, QUAYLING, LOZMAN, OWEN, ROGER, LU, ZHIBAO, MCNEILL, ANDREW, PAUL, UNIVERSITY OF LEEDS, WOOD, ANDREW
Application year: 2000
Main classification: C09K19
IPC codes: C07C1, C07C15, C07C41, C07C43, C07C69, C07C205, C07C255, C07D487, C08F8, C08G65, C09K19, G02F1