POWDER-FREE NITRILE-COATED GLOVES WITH AN INTERMEDIATE RUBBER-NITRILE LAYER BETWEEN THE GLOVE AND THE COATING

Abstract: Powder-free natural rubber and synthetic elastomeric articles, in particular, gloves, having an inner coating of a nitrile rubber with an intermediate layer of a rubber blend comprised of natural or synthetic rubber and nitrile rubber interposed between the nitrile coating and the base glove and their method of manufacture are described. The intermediate layer of the rubber blend interposed between the coating and the glove imparts a unique surface texture to the glove which aids donning and eliminates self-sticking of the inner glove surfaces, especially after the glove has been sterilized by radiation. Additionally the gloves of the invention exhibit good grippability, good donnability, superior tensile strength, elongation to break and stress at 500 % elongation.

Description: 2 "POWDER-FREE NITRILE-COATED GLOVES WITH 3 AN INTERMEDIATE RUBBER-NITRILE LAYER BETWEEN THE GLOVE AND THE COATING" 4 5 6 BACKGROUND OF THE INVENTION 7 The majority of commercially available powder-free latex gloves are 8 manufactured by first preparing a powdered glove on-line and then removing the 9 powder from the glove by chlorination and rinsing off-line. The chlorination 10 process oxidizes the natural rubber surface of the giove thereby providing ii improved dry donning characteristics. Chlorination also removes any powder i2 deposited on the gloves during the rinsing operation. i3 Other powder free gloves have been produced by using powder free i4 coating technology in combination with chlorination or other post treatment is processes. Some of these coated gloves use a manufacturing process which i6 requires that the rubber substrate be treated with acid or other harsh chemicals i7 to improve adhesion of the coating to the base rubber glove. This additional is chemical processing step is not preferable in glove manufacturing because the i9 chemicals used are generally corrosive and/or difficult to handle in large scale 20 production processes. Additionally, most of the coated and non-coated gloves 2i do not have acceptable donning characteristics with respect to damp and wet 22 skin, which is one of the critical product requirements for surgical glove 23 applications. Finally, some of these gloves also exhibit self-sticking between the 24 inner glove surfaces which create difficulties for health care workers trying to don 25 the gloves in a sterile environment. i SUMMARY OF THE INVENTION ?. The present invention provides a powder-free, inner-nitrile rubber coated, 3 natural rubber or synthetic elastomer glove for medical and industrial applications which has good donning characteristics and good grippability (as 5 measured by the coefficient of friction of the donning and gripping surfaces). 6 The glove of the invention also exhibits good tensile strength, stress at 500% 7 elongation and elongation to break. The inner coating on the gloves of the invention is a cross-linked nitrile 9 rubber blended with a lubricant. Interposed between the nitrile rubber coating lo and the base elastomeric glove is an intermediate layer of a rubber blend li comprised of natural or synthetic rubber and nitrile rubber. Comparative testing i2 demonstrates that the inventive gloves have improved adhesion between the i3 coating and the base glove as compared to those coated gloves which do not i4 contain the intermediate layer of rubber blend. The gloves of the invention do is not show any appearance of surface sticking between the inner surfaces and/or i6 the outer surfaces and also exhibit good donning with respect to both dry and i7 wet skin. The inventive gloves also have a unique surface texture which is improves donnability. is BRIEF DESCRIPTION OF THE FIGURES 20 Figure 1A is a scanning electron microscope (SEM) photograph (x2000 2i magnification) of the interior surface of a prior art natural rubber latex glove SUBSTΓΓUTE SHEET RULE 26 1 which contains neither an intermediate layer nor an inner nitrile coating. The 2 glove has been chlorinated and lubricated. 3 Figure 1 B is a scanning electron microscope (SEM) photograph (x2000 4 magnification) of the interior surface of a natural rubber latex glove in 5 accordance with the invention which has an intermediate layer containing 2.5% 6 total solids and an inner nitrile coating containing 5.0% total solids. The glove 7 has been chlorinated and lubricated. 8 Figure 2A is a scanning electron microscope (SEM) photograph (x2000 9 magnification) of the interior surface of a natural rubber latex glove which does 10 not contain an intermediate layer but which has a nitrile coating. The glove has ii not been chlorinated or lubricated. i2 Figure 2B is a scanning electron microscope (SEM) photograph (x2000 i3 magnification) of the interior surface of a natural rubber latex glove which has an i4 intermediate layer but which has no nitrile coating. The glove has not been is chlorinated or lubricated. 16 PREFERRED EMBODIMENTS OF THE INVENTION i7 The gloves of the invention are comprised of a natural rubber, nitrile, is polychloroprene, polybutadiene, polyvinylchloride, polyurethane, synthetic i9 polyisoprene, styrene diblock and triblock copolymers, or other synthetic 20 elastomers, including blends thereof, which have on their inner surface a coating 2i comprised of a cross-linked nitrile rubber blended with lubricant with an 22 intermediate layer of a rubber blend of natural or synthetic rubber and nitrile 1 rubber interposed between the elastomeric glove and the coating of nitrile 2 rubber. 3 The natural rubber latex used to form the base glove may be compounded 4 with stabilizers, a crosslinker, a vulcanization activator, a vulcanization 5 accelerator, an antioxidant, an antiozonant and optionally, white or other colored 6 pigments. 7 Suitable stabilizers include oleates, stearates, alginates, polyacrylates, 8 xanthan gums, caseinates or other nonionic and ionic surfactants. Typical 9 crosslinkers which may be used in the compounding formulation include sulfur or lo other organic peroxides. Suitable vulcanization activators include metal oxides, ii such as magnesium oxide, lead oxide, and preferably, zinc oxide. The 12 vulcanization accelerator may be chosen from mercaptobenzothiazoles and their i3 derivatives, dithiocarbamates and their derivatives, sulfur donors, guanidines and i4 aldehyde-amine reaction products. Suitable antioxidants include hindered is arylamines or polymeric hindered phenols. Typical antiozonants which may be i6 used in the compounding formulation include paraffinic waxes, microcrystalline i7 waxes and intermediate types of waxes (which are blends of both paraffinic and is microcrystalline waxes). Typical white pigments that may be used include i9 titanium dioxide and zinc oxide. 2o Synthetic diene based elastomers used to form the base glove such as 2i polybutadiene, synthetic polyisoprene, nitrile, polychloroprene and its blends can 22 be compounded with similar compounding ingredients as set forth above. Other 1 synthetic thermoplastic elastomeric materials used for the base glove such as 2 polyvinylchloride, polyurethanes, styrene diblock and triblock copolymers and its 3 blends do not require crosslinking to prepare a glove with the desired physical 4 properties. Accordingly, these synthetic elastomers may be compounded with 5 stabilizers, antioxidants, antiozonants and color pigments as described above. 6 Those skilled in the art will readily be able to vary the total solid content of 7 the dipping formulation to form the base glove with the desired thickness and the 8 compounding ingredients in the dipping formulation to suit the particular 9 elastomers used to form the base glove as well as the final article desired. lo An intermediate layer of a rubber blend comprised of a natural or synthetic ii rubber and nitrile rubber is interposed between the elastomeric glove and the i2 nitrile coating by dipping the glove a second time after coagulation has formed i3 the base glove or first elastomeric layer. The nitrile rubber latex used to form the i intermediate rubber blend is a carboxylated acrylonitrile butadiene terpolymer is dispersion. The carboxylated acrylonitrile butadiene terpolymer preferably has 16 an acrylonitrile content of about 25 to about 40 parts, a butadiene content of i7 about 55 to about 68 parts and a carboxylic acid content of about 3 to about 6 is parts. The carboxylated acrylonitrile butadiene terpolymer most preferably has i9 an acrylonitrile/butadiene/carboxylic acid ratio of 39/58/3. 20 Alternatively, the nitrile rubber latex used to form the intermediate rubber 2i blend is an acrylonitrile butadiene based copolymer dispersion or a dispersion of 22 a hydrogenated acrylonitrile butadiene copolymer. If the latter polymer is used, 1 the degree of hydrogenation is preferably greater than about 85%. Preferably, 2 the acrylonitrile content of these copolymers varies from about 25 to about 50 3 parts and the butadiene content varies from about 50 to about 75 parts. Most 4 preferably, the acrylonitrile content of these copolymers varies from about 25 to 5 about 45 parts and the butadiene content varies from about 50 to about 75 parts. 6 For a base glove or first elastomeric layer comprised of natural rubber, the 7 intermediate layer is preferably comprised of a blend of natural rubber and nitrile 8 rubber. Preferably, the blend ratio is about 5 parts natural rubber/95 parts nitrile 9 rubber (a blend ratio of 5/95) to about 95 parts natural rubber/5 parts nitrile lo rubber (a blend ratio of 95/5). Most preferably, the blend ratio is about 40/60 to ii about 90/10. For a base glove comprised of a synthetic rubber, the intermediate i2 layer is preferably comprised of a blend of the same synthetic rubber used to i3 form the base glove and nitrile rubber. Preferably, the blend ratio is about 5 parts i4 synthetic rubber/95 parts nitrile rubber (a blend ratio of 5/95) to about 95 parts is synthetic rubber/5 parts nitrile rubber (a blend ratio of 95/5). Most preferably, the i6 blend ratio is about 40/60 to about 90/10. The rubber blend latex which forms i7 the intermediate layer is compounded with stabilizers, a crosslinker, a is vulcanization activator, a vulcanization accelerator and the following optional i9 ingredients: an antioxidant, an antiozonant and white or colored pigments. 20 Suitable stabilizers include oleates, stearates, alginates, polyacrylates, 2i xanthan gums, caseinates and other nonionic and ionic surfactants. Preferably 1 the stabilizers are caseinates and surfactants. Most preferably, the stabilizer is a 2 non-ionic and/or ionic surfactant. 3 Typical crosslinkers used in the compounding formulation include sulfur, 4 and organic peroxides. Preferably, the crosslinker is sulfur. 5 Suitable vulcanization activators include metal oxides, such as 6 magnesium oxide, lead oxide and preferably, zinc oxide. The vulcanization 7 accelerator may be chosen from mercaptobenzothiazoles and their derivatives, 8 dithiocarbamates and their derivatives, sulfur donors, guanidines and aldehyde- 9 amine reaction products. lo Suitable antioxidants include hindered arylamines and polymeric hindered ii phenols. Typical antiozonants which may be used in the compounding i2 formulation include paraffinic waxes, microcrystalline waxes and intermediate 13 types of waxes (which are blends of both paraffinic and microcrystalline waxes). 14 Typical white pigments that may be used include titanium dioxide and zinc oxide. is The compounding ingredients used to prepare the intermediate rubber i6 blend layer dispersion and their relative proportions are set forth below in Table - i7 1. The total percent solid of this dispersion is adjusted to be less than about is 45%. During the dipping of the intermediate rubber blend latex, chemical i9 contaminants such as ionic species, especially bivalent ions from the coagulated 2o natural rubber layer or synthetic rubber layer may inadvertently be introduced 2i into the rubber blend latex. Because of the increasing concentration of these 22 contaminants, the rubber blend latex should be adequately stabilized to prevent latex flocculation. It is important that the rubber blend latex be stabilized adequately toward ionic species and yet not be too stable to prevent the coagulation of the rubber blend latex onto the rubber layer that forms the base glove or first elastomeric layer. If the percent solid content of the rubber blend latex is low, the rubber blend latex is not as stable as a high percent solid content rubber blend latex and thus additional stabilizers are typically added during the compounding of the rubber blend latex. The total amount of natural rubber or synthetic rubber and nitrile rubber will be about 100 parts. Table 1 The nitrile rubber latex used to coat the interior surface of the formed glove, i.e., disposed on the intermediate layer, is a carboxylated acrylonitrile 1 butadiene rubber dispersion, preferably, a dispersion of a carboxylated 2 acrylonitrile butadiene terpolymer containing an acrylonitrile content of about 25 3 to about 40 parts, a butadiene content of about 55 to about 68 parts and a 4 carboxylic acid content of about 3 to about 6 parts. More preferably, the nitrile 5 rubber latex is a blend of two carboxylated acrylonitrile butadiene rubber 6 dispersions of different acrylonitrile/butadiene/carboxylic acid ratios [A and B in 7 Table 2]. Most preferably, the nitrile rubber latex is a dispersion blend of a 8 carboxylated acrylonitrile butadiene rubber with an 9 acrylonitrile/butadiene/carboxylic acid ratio of about 39/58/3 and a carboxylated lo acrylonitrile butadiene rubber with an acrylonitrile/butadiene/carboxylic acid ratio ii of about 39/55/6. The blend ratio of the two carboxylated acrylonitrile butadiene i2 terpolymers is about 1/99 to about 99/1. Preferably, the blend ratio is about i3 75/25 to about 25/75. Most preferably, the blend ratio is about 50/50. A single i4 nitrile rubber dispersion may be used instead of a nitrile blend dispersion for is ease of material handling and manufacturing, preferably a carboxylated i6 acrylonitrile butadiene rubber with an acrylonitrile/butadiene/carboxylic acid ratio i7 of about 39/55/6. For use as part of the coating on the interior of the gloves of is the invention, the nitrile rubber dispersion is additionally compounded with a i9 crosslinker, vulcanization accelerator, vulcanization activator, lubricant, and 20 optionally, a biocide. 2i Alternatively, the nitrile rubber latex used to coat the interior surface of the 22 formed glove, i.e. disposed on the intermediate layer, is an acrylonitrile 23 butadiene based copolymer dispersion or a hydrogenated acrylonitrile butadiene 1 copolymer. If the latter polymer is used, the degree of hydrogenation is 2 preferably greater than about 85%. Preferably, the acrylonitrile content of these 3 copolymers varies from about 25 to about 50 parts and the butadiene content 4 varies from about 50 to about 75 parts. Most preferably, the acrylonitrile content 5 of these copolymers varies from about 25 to about 45 parts and the butadiene 6 content varies from about 50 to about 75 parts. The nitrile rubber latex is 7 preferably a blend of two acrylonitrile butadiene rubber dispersions of different 8 acrylonitrile/butadiene ratios. [A and B in Table 2] 9 The crosslinker may be chosen from sulfur, organic peroxides and metal lo oxides. Preferably, the crosslinker is selected from the group consisting of sulfur ii and metal oxides. Most preferably, the crosslinker is sulfur. i2 The vulcanization activator may be metal oxides. The preferred metal i3 oxides are magnesium and zinc oxide. The most preferred metal oxide is zinc i4 oxide. is The vulcanization accelerator is chosen from mercaptobenzothiazoles and i6 their derivatives, dithiocarbamates and their derivatives, sulfur donors, i7 guanidines and aldehyde-amine reaction products. Preferably, the accelerator is chosen from the dithiocarbamates and their derivatives. Most preferably, the i9 accelerator is a dispersion of zinc dibutuyldithiocarbamate. 20 The lubricant may be chosen from organic powders, inorganic powders, 2i silicones, stearates, fluorochemicals, petroleum oils, organic esters, polyglycols, 22 synthetic hydrocarbons and phosphates. Preferably, the lubricant is a siioxane 1 based silicone emulsion. Most preferably, the silicone is a poly(alkylsubstituted 2 siioxane) emulsion. 3 Optionally, a small amount of biocide may be added into the nitrile rubber 4 latex to inhibit the growth of microorganisms. The biocide may be chosen from 5 the following classes of individual biocides but is not limited to them: phenolics, 6 halogen compounds, quaternary ammonium compounds, metal-containing 7 compounds, anilides, amines, alkanolamines, nitro compounds, organosuifur and 8 sulfur-nitrogen compounds. Preferably, the biocide is chosen from the industrial 9 biocides generally used in paints, latexes, polymer emulsions and water based ιo coating systems. Most preferably, the biocide is chosen from the biocide list ii approved by the FDA for food and food-packaging applications and is compatible i2 with the nitrile rubber latex. Materials approved by the FDA are listed in the i3 Federal Register under appropriate sections based on specific applications. i4 They can be seen in the reference: "Biocides", Encyclopedia of Polymer Science is and Engineering, Second Edition, Volume 2, John Wiley & Sons, 1985, pages 16 202 - 219 which is hereby incorporated by reference. Examples of suitable i7 biocides are formaldehyde based and triazine based biocides. is The compounding ingredients used to prepare the nitrile rubber powder i9 free dispersion and their relative proportions are set forth below in Table 2. The 20 total amount of [A] and [B] will be about 100 parts. 21 22 TABLE 2 Alternatively, the powder free dispersion used to coat the interior surface of the formed glove, i.e. disposed on the intermediate layer, is a dispersion blend of nitrile rubber and other synthetic rubber. Preferably, the blend ratio of the nitrile rubber and synthetic rubber is about 50/50 to about 99/1. Most preferably, the blend ratio of the nitrile rubber and synthetic rubber is about 75/25 to about 95/5. Synthetic rubber dispersions may be chosen from the following classes of synthetic materials but is not limited to them: polyurethanes, acrylics, synthetic polyisoprene, polybutadiene and other synthetic diene based elastomers. The compounding ingredients used to prepare the synthetic blend powder free dispersion and their relative proportions are set forth below in Table 3. The total amount of [A] and [B] will be about 100 parts. TABLE 3 Those skilled in the art will readily be able to vary the compounding ingredients in the dipping formulation to suit the final synthetic or natural rubber article desired. For example, if a carboxylated acrylonitrile butadiene terpolymer dispersion is used, the crosslinker and the vulcanization accelerator may not be needed in the dipping formulation since the metal oxide vulcanization activator may also function as a crosslinker to crosslink the nitrile rubber via ionic bonding. Alternatively, the lubricant may be added separately to the dispersion during the manufacturing of the nitrile dispersion or the nitrile may be chemically modified to incorporate lubrication characteristics during polymerization. An example of the chemical modification approach is to incorporate a silicone based compound into the nitrile by chemical grafting or by polymerization. In these 1 cases, the addition of the lubricant in the dipping formulation as listed in Table 2 2 and Table 3 may not be necessary. The nitrile-based powder-free dispersion can be used to coat the interior 4 of a variety of natural rubber and synthetic elastomer articles, including surgical 5 and examination gloves, industrial gloves, finger cots, tubing, ultrasound probe 6 covers, protective sheaths and catheter balloons for medical and industrial 7 applications. 8 The gloves fabricated in accordance with the present invention may be 9 prepared as follows. A mold in a contoured shape of a glove is first oven dried lo and then dipped into an alcohol or water-based coagulant dispersion comprising ii calcium nitrate, powder (calcium carbonate or comstarch), wetting agent and i2 water or alcohol (for alcohol based coagulant dispersion). The coagulant layer i3 deposited on the glove former is then dried. The glove former is then dipped into i the compounded natural rubber latex or synthetic elastomer dispersion and a film is of the natural rubber or synthetic elastomer is coagulated on the glove former. i6 While still on the former, the layer of coagulated natural rubber or synthetic .7 elastomer is then dipped into a blend of natural rubber and nitrile rubber is dispersion or a blend of synthetic rubber and nitrile rubber dispersion to form an i9 intermediate layer on the glove. The glove is optionally leached with water and 20 then dipped into a powder-free dispersion comprising a nitrile rubber (or a 2i dispersion blend of nitrile rubber and other synthetic rubbers), a lubricant, a 22 cross-linker, a vulcanization accelerator and a vulcanization activator as set forth 1 in Table 2. The former carrying the nitrile rubber coated natural rubber or 2 synthetic elastomer glove with an intermediate layer of natural rubber and nitrile 3 rubber or synthetic rubber and nitrile rubber interposed between the nitrile rubber 4 coating and the base glove is then cured in an oven. The former is removed 5 from the oven and the glove is then stripped from the former. 6 To prepare the powder free coated gloves, the gloves are post-processed 7 by chlorination as follows. The coated gloves are initially turned inside out with 8 the coated surfaces on the outside of the gloves. The gloves are optionally pre- 9 rinsed with water two times (for about 2.5 minutes per time) and immersed in an lo aqueous chlorinated solution in a chlorinator for about at least 6 minutes. The ii chlorine concentration may vary from about 50 ppm to about 1500 ppm. i2 Preferably the chlorine concentration is about 150 to about 700 ppm. Most i3 preferably, the chlorine concentration is about 250 ppm to about 350 ppm. After i4 chlorination, the chlorinated solution is neutralized by adding a base (e.g., is sodium hydroxide or ammonium hydroxide) to the solution and the gloves are i6 then tumbled for about 4 minutes or until the pH of the solution is about 7 or i7 above. The neutralized solution is then drained and the gloves are rinsed with is water for about 2.5 minutes. The gloves may be rinsed three more times (for i9 about 2.5 minutes per time) to remove traces of the chlorinated solution. 20 For medical examination and industrial glove applications, after rinsing, 2i the gloves are dried at about 55°C for about 20 minutes. The gloves are then 1 turned again so that the coated surface is on the inside of the glove. The gloves 2 are then dried again at about 50°C for about 5 minutes. 3 Alternatively, for medical examination and industrial applications, the powder-free coated gloves of the invention are prepared as set forth above 5 except the chlorination processing steps are modified as follows. After stripping e from the former, the coated gloves are optionally pre-rinsed with water and 7 immersed in an aqueous chlorinated solution in a chlorinator for at least about 6 8 minutes. The chlorine concentration may vary from about 50 ppm to about 1500 9 ppm. Preferably, the chlorine concentration is about 150 to about 700 ppm. lo Most preferably, the chlorine concentration is about 250 ppm to about 350 ppm. ii After chlorination, the chlorinated solution is neutralized by adding a base to the i2 solution and the gloves are then tumbled for about 4 minutes or until the pH of i3 the solution is about 7 or above. The neutralized solution is then drained and the i4 gloves are rinsed with water for about 2.5 minutes. The gloves are then rinsed is three more times to remove traces of the chlorinated solution. After rinsing, the i6 gloves are dried at about 55°C for at least 20 minutes or until the gloves are i7 dried. The powder-free coated gloves are now ready for packing. Preferably, is the above described post-processing steps are suitable for processing a coated i9 glove with a bead on the cuff. The beading step can be applied before or after 20 dipping of the former with the intermediate rubber blend layer into the powder- 2i free nitrile rubber dispersion as described above. 1 For surgical glove applications, the gloves are preferably lubricated after 2 chlorination with a lubricant solution to provide good donning characteristics with 3 respect to damp and wet skin. For these applications the rinsed gloves are 4 removed from the chlorinator and placed in an extractor/lubricator/dryer. The 5 gloves are extracted to remove excess water and a lubricant solution is then 6 applied to the coating surface, e.g., by spraying or by tumbling. The lubrication 7 solution is preferably comprised of about 0.1 wt % to about 2 wt. % 8 cetylpyridinium chloride and about 0.01 wt % to about 2 wt. % silicone emulsion. 9 After the lubricant application, the gloves are dried at about 55° C for about 20 ιo minutes. After the first dry, the gloves are turned inside out so that the coated ii surfaces are on the inside of the glove. The gloves are then dried again at about i2 50 ° C for about 5 minutes. i3 Other suitable lubricants that may be used to provide wet and damp 14 donning characteristics are nonionic and ionic surfactants. Among these is surfactants, the cationic and amphoteric surfactants are most preferred for these i6 applications. These surfactants may also be combined with other lubricants i7 such as silicones, stearates, or other water soluble polymers such as chitosan, is polyethylene oxide or polyvinyl alcohol, to provide acceptable donning features i9 for surgical glove applications 20 The finished gloves are packaged and sent for sterilization by gamma or 2i electron beam radiation. 1 The gloves of the invention have a thickness of at least about 0.003 2 inches. Preferably, the thickness of the gloves ranges between about 0.004 3 inches and about 0.020 inches. Most preferably, the glove thickness is between 4 about 0.005 and about 0.0018 inches. 5 The gloves of the invention exhibit a tensile strength of greater than about 6 1300 psi, preferably greater than about 2600 psi and most preferably, greater 7 than about 3500 psi. The stress at 500% of the gloves of the invention is less 8 than about 3000 psi, preferably less than about 2000 psi and most preferably, 9 less than about 1000 psi. The gloves of the invention have an elongation at lo break greater than about 200 %, preferably greater than about 500 % and most ii preferably greater than about 800%. i2 The gloves of the invention exhibit a dry kinetic COF of less than about i3 0.6 for the donning (coated) inner surface and greater than about 0.6 for the i4 gripping (uncoated) outer surface. Preferably, the dry kinetic COF is less than is about 0.5 for the donning surface and greater than about 0.7 for the gripping i6 surface. Most preferably, the dry kinetic COF is less than about 0.4 for the i7 donning surface and greater than about 0.8 for the gripping surface. is The glove thickness is measured by a digital thickness gauge and is the i9 average of three measurements in the palm area. Tensile strength, stress at 20 500% elongation and elongation to break are measured according to ASTM 2i D412-92. Dry kinetic COF is measured according to ASTM D1894. 1 The gloves of the invention after gamma and electron beam sterilization at 2 a dose range of about 25 kGy to about 80 kGy show no appearance of surface 3 sticking between the inner surfaces and/or outer surfaces. The gloves of the 4 invention were further characterized by scanning electron microscopy (SEM) at 5 x2000 magnification which illustrated the difference in surface morphology 6 between gloves with and without an intermediate layer and the nitrile inner 7 coating. 8 Figure 1 A is a SEM photograph of the inner glove surface of a prior art 9 powder free natural rubber latex glove without the intermediate rubber blend lo layer and the inner nitrile coating layer and Figure 1 B is a SEM photograph of ii the inner glove surface of the inventive powder free coated natural rubber latex i2 glove. Comparison of the two figures clearly shows that the coated glove i3 surface exhibits rough domains on the order of about 10 micrometers with 14 unique surface texturing, whereas the non-coated natural rubber surface shows is a typical natural rubber surface with microdomains of less than 1 micrometer. i6 The unique surface texture of the gloves of the invention provides a reduced i7 surface contact area which contributes to the reduction or elimination of self- is sticking of the inner glove surfaces. The unique surface texture also facilitates i9 glove donning. 20 Figures 2A and 2B illustrate that the unique surface texturing on the 2i coated glove is mainly due to the presence of the intermediate rubber blend 22 layer. Figure 2A is a SEM photograph of the inner glove surface of a nitrile 1 coated natural rubber latex glove without the intermediate rubber blend layer and 2 Figure 2B is a SEM photograph of the inner glove surface of a natural rubber 3 latex glove coated with just the intermediate rubber blend layer. It is apparent 4 that the intermediate rubber blend coated surface shown in Figure 2B exhibits 5 numerous cavities with pore diameters of about 5 - 10 micrometers which are 6 absent in the nitrile coated surface without the intermediate rubber blend layer. 7 The improved adhesion exhibited by the gloves with an intermediate layer 8 or rubber blend as compared to similarly coated gloves which do not contain the 9 intermediate layer of rubber blend is illustrated by the following comparative o example. ii COMPARATIVE EXAMPLE 1. i2 A nitrile-coated natural rubber latex glove with an intermediate natural i3 rubber-nitrile layer between the glove and the nitrile coating was prepared as i4 follows. A glove former was pre-heated in an oven at about 50°C for about 2 is minutes. The preheated former then was dipped into a stirred, water based i6 coagulant suspension maintained at a temperature between about 50°C to about i7 55°C. The coagulant-dipped former was then returned to the heated oven for is about 2 to about 3 minutes to dry the coagulant layer. i9 The coagulant-coated former was dipped into compounded natural rubber 2o latex for a time sufficient to produce the desired glove thickness. The natural 2i rubber latex was compounded with stabilizers, crosslinker, vulcanization 22 activator, vulcanization accelerators, antioxidant, antiozonant and white pigment. 1 The solid content of the compounded latex was about 40 wt %. The former 2 bearing the coagulated latex was then removed from the compounded natural 3 rubber latex and immediately dipped into a second rubber blend latex for about 4 13 to 15 seconds. The rubber blend latex comprised about 0.75% compounded 5 natural rubber latex and about 0.75% of carboxylated acrylonitrile butadiene 6 latex and about 98.5% water. The formulation of the compounded natural rubber 7 latex used in this rubber blend latex was the same as the one used in the first 8 latex dipping. The acrylonitrile/butadiene/carboxylic acid ratio of the nitrile rubber 9 was 39/58/3. lo The former was removed from the second rubber blend latex and leached ii in water maintained at about 50°C for about 5 minutes. The former was then i2 dipped into a compounded nitrile blend latex with a total solid content of about i3 5% to form a coating on the intermediate natural rubber-nitrile blend layer. The i4 nitrile blend was comprised of a 50/50 blend of two carboxylated acrylonitrile is butadiene rubber iatices with two different acrylonitrile/butadiene/carboxylic acid i6 ratios, 39/58/3 and 39/55/6. The nitrile blend latex was further compounded with i7 1 part of sulfur dispersion (crosslinker), 1 part of ZDBC dispersion (vulcanization is accelerator), 3 parts of ZnO dispersion (vulcanization activator) and 15 parts of i9 silicone emulsion. The former was removed from the compounded nitrile blend 20 latex and placed in an oven at about 125°C for about 20 minutes to cure the 2i glove. The former bearing the glove was then removed from the oven and 22 allowed to cool. The glove was then stripped from the former. SUBSTΓΠJTE SHEET (RULE 26) 1 The adhesion of the nitrile coating was evaluated qualitatively using two 2 samples of each glove. In this test, the coated glove surface in the palm and 3 finger areas was stretched to about 500% and the coating was rubbed 4 repeatedly using the thumb. The coated surface was then visually examined for 5 coating flakes and powdery substance The adhesion of the coating was rated 6 qualitatively on a scale of 1 to 5, 1 being the worst with the entire coating flaking 7 off the rubber substrate and 5 being the best with no visual appearance of 8 powdery substance on the surface of the glove. Using this test, the adhesion of 9 the inventive coating was excellent with a rating of 5 on a scale of 1 to 5, i.e., no lo flaking or shedding of the powder was observed after stretching the glove to ii about 500% and rubbing it repeatedly with the thumb. 12 COMPARATIVE EXAMPLE 2. 13 A nitrile-coated natural rubber latex glove without an intermediate natural i4 rubber-nitrile layer between the glove and the nitrile coating was prepared as is follows. A glove former was pre-heated in an oven at about 50°C for about 2 i6 minutes. The preheated former was dipped into a stirred, water based coagulant i7 suspension maintained at a temperature between about 50°C to about 55°C. is The coagulant-dipped former was then returned to the heated oven for about 2 i9 to about 3 minutes to dry the coagulant layer. 20 The coagulant-coated former was dipped into a compounded natural 2i rubber latex for a time sufficient to produce the desired glove thickness. The 22 natural rubber latex was compounded with stabilizers, crosslinker, vulcanization 1 activator, vulcanization accelerators, antioxidant, antiozonant and white pigment. 2 The solid content of the compounded latex was about 40 wt %. The former 3 bearing the coagulated latex was then removed from the compounded natural 4 rubber latex and leached in water maintained at about 50°C for about 5 minutes. 5 The former was then dipped into a compounded nitrile blend latex with a total 6 solid content of about 5% to form a coating on the intermediate natural rubber- 7 nitrile blend layer. The nitrile blend coating formulation was the same as 8 described in comparative example 1. 9 The adhesion of the nitrile coating was fair with a rating of 3 on a scale of lo 1 to 5, i.e., powdery material was shed from the glove after it was stretched to ii about 500% and rubbed repeatedly with a thumb. 12 The invention is further illustrated by the following examples. It is i3 understood that one of ordinary skill in the art will understand how to vary the i4 times and temperatures of the process in accordance with the article is manufactured, the specific elastomer or blend employed, the particular i6 formulation ingredients selected and the percent solid content of the rubber and 17 rubber blend latex. Similarly, one of ordinary skill in the art will know how to is select a post-processing method compatible with his individual glove i9 manufacturing line and equipment. 20 Example 1 2i A powder-free nitrile-coated natural rubber latex glove with an 22 intermediate natural rubber-nitrile layer between the glove and the nitrile coating 1 was prepared as follows. Glove formers were pre-heated to about 60-70°C in an 2 oven for about 5 minutes. The preheated former then was dipped into a stirred, 3 water based coagulant dispersion maintained at a temperature between about 4 55°C to about 60°C. The coagulant-dipped former was then returned to the 5 heated oven for about 5 minutes to dry the coagulant layer. 6 The coagulant-coated former was dipped into a compounded natural 7 rubber latex for a time sufficient to produce the desired glove thickness. The 8 natural rubber latex was compounded with stabilizers, crosslinker, vulcanization 9 activator, vulcanization accelerators, antioxidant, antiozonant and white pigment. lo The solid content of the compounded latex was about 38 wt. %. The former ii bearing the coagulated latex was then removed from the compounded natural 12 rubber latex and immediately dipped into a second rubber blend latex for about i3 13 to about 15 seconds. The rubber blend latex comprised about 2.3% i4 compounded natural rubber latex and about 2.3% of carboxylated acrylonitrile is butadiene latex and about 95.4% water. The formulation of the compounded i6 natural rubber latex used in this rubber blend latex was the same as the one i7 used in the first latex dipping. The ratio of acrylonitrile/butadiene/carboxylic acid is for the nitrile rubber was 39/58/3. i9 The former was removed from the second rubber blend latex and dried in 20 a heated oven at about 58°C. The coagulated latex layer was leached in water 2i maintained at about 55°C to about 80°C for about 5 minutes. The former was 22 then dipped into a compounded nitrile blend latex with a total solid content of 1 about 5% to form a coating on the intermediate natural rubber-nitrile blend layer. 2 The nitrile blend was comprised of a 50/50 blend of two carboxylated acrylonitrile 3 butadiene rubber latices with two different acrylonitrile/butadiene/carboxylic acid 4 ratios 39/58/3 and 39/55/6. The nitrile blend latex was further compounded with 5 1 part of sulfur dispersion (crosslinker), 1 part of ZDBC dispersion (vulcanization e accelerator), 3 parts of ZnO dispersion (vulcanization activator) and 15 parts of 7 silicone emulsion (SM 2140 obtained from General Electric). The dwell time for 8 the coating dipping was about 13 to about 15 seconds. 9 The cuff of the coated glove was beaded by a beader and the former was lo placed in an oven maintained at about 110 - 136°C for about 20 minutes in order ii to cure the glove. The former bearing the glove was then removed from the i2 oven and allowed to cool. The glove was then stripped from the former. i3 The glove was then post-processed by chlorination. First, the coated i4 glove was turned inside out manually and loaded into a chlorinator. The glove is was pre-rinsed 2 times for a total time of about 5 minutes. An aqueous chlorine i6 solution of about 300 ppm chlorine was added to the chlorinator and the gloves i7 tumbled for about 8.3 minutes. The chlorinated solution was then neutralized is with 50% sodium hydroxide solution for about 4 minutes. The glove was post- 19 rinsed 4 times for a total time of about 10 minutes. The glove was then 20 transferred to a tumbling washer for the lubrication process. Excess water was 21 removed from the glove by spinning the glove for about 2 minutes. The washer 22 was then filled with an aqueous lubrication solution comprised of about 0.5 wt % 1 of cetylpyridinium chloride and 0.15 wt % of silicone emulsion. The glove was 2 tumbled in the lubrication solution for about 5 minutes. The lubrication solution 3 was drained and the glove was tumbled for an additional 5 minutes. The glove 4 was then removed from the tumbler washer and dried in a dryer with a heating 5 cycle of about 20 minutes at about 55°C and a cool down cycle for about 10 6 minutes. The glove was removed from the dryer and turned inside out manually. 7 The glove was dried again in the dryer at about 50°C for about 5 minutes and 8 allowed to cool down to room temperature for about 5 minutes. 9 The physical properties of the powder-free coated glove prepared as set lo forth in Example 1 were measured according to ASTM D412-92. The gloves had ii a tensile strength of 4323 psi, a tensile stress at 500% of 313 psi, and an i2 ultimate elongation of 1022%. The coefficient of friction (COF) of both the 13 outside and inside surfaces in the palm area of the glove were measured 14 according to ASTM D1894-95. The static and kinetic COF for the inside surface is were 0.72 and 0.46, respectively. The static and kinetic COF for the outside i6 surface were 1.22 and 1.61 , respectively. i7 The donning characteristics of the glove were evaluated qualitatively with is respect to damp skin on a scale of 1 to 5, 1 being the worst with extreme i9 difficulties in donning the glove and 5 being the best with extreme ease in 20 donning the glove. This determination was made by having the glove donned by 2i a person with damp skin. The glove dons extremely well with respect to damp 22 and wet skin with a rating of 5. 1 The adhesion of the coating was also evaluated qualitatively. In this test, 2 the coated glove surface was stretched to more than 500% and the coating was 3 rubbed repeatedly using the thumb. The coated surface was then visually 4 examined for coating flakes and powdery substance. The adhesion of the 5 coating was rated qualitatively on a scale of 1 to 5, 1 being the worst with the 6 entire coating flaking off the rubber substrate and 5 being the best with no visual 7 appearance of powdery substance on the surface of the glove. Using this test, 8 the adhesion of the inventive coating is quite good with a rating of 5 on a scale of 9 1 to 5, i.e. , no flaking or shedding of the powder was observed after stretching lo the glove to about 500% and rubbing it repeatedly with the thumb. ii The finished glove was packaged as follows: a pair of gloves with a right i2 and a left hand was manually cuffed down to about 4 inches so that the inside i3 surface of the cuff was exposed to the outside. The left hand glove was laid flat i4 in the left side of the inner wrap paper with the thumb exposed outward and the i5 paper wrapped around the glove. The right hand glove was laid flat in the right i6 side of the inner wrap paper with the thumb exposed outward and the paper i7 wrapped around the glove. One wrapped glove was then flipped over the other is to produce a rectangular wallet-shaped packet. The inner wrap with a pair of i9 gloves was then placed in between a top web paper and a bottom web paper, 2o and thermally sealed on all sides 50 pairs of gloves were packed into a 2i dispenser box and 4 boxes were then packed into a carton. The packed gloves 22 were sterilized by gamma sterilization at a dose range of 28.1 KGy and 31.1 23 KGy. 1 The sterile glove had a tensile strength of 4309 psi, a tensile stress at 2 500% of 313 psi, and an ultimate elongation of 993%. The static and kinetic 3 COF for the inside surface were 0.37 and 0.15, respectively. The static and 4 kinetic COF for the outside surface were 0.6 and 0.8, respectively. The donning 5 characteristics of the sterile glove were excellent with a rating of 5 with respect to 6 damp skin on a scale of 1 to 5, i.e., no flaking or shedding of the powder was 7 observed after stretching the glove to about 500% and rubbing it repeatedly with 8 the thumb. The adhesion of the inventive coating was excellent with a rating of 5 9 on a scale of 1 to 5 (where about 4 to about 4.5 is the adhesion value exhibited lo by commercially available glove coatings). ii Example 2 i2 A powder-free nitrile-coated natural rubber latex glove with an i3 intermediate natural rubber-nitrile layer between the glove and the nitrile coating i4 was prepared as set forth in Example 1 except that the chlorine concentration in is the aqueous chlorinated solution was adjusted to about 238 ppm and that the i6 lubricant solution was applied using a spraying process as follows. i7 After the chlorination process, the glove was transferred to an extractor is and excess water was removed from the glove by spinning the glove for about 5 i9 minutes. The glove was then placed in a lubricator equipped with a spray gun. 20 The glove was tumbled in the dryer maintained at about 55°C for about 1 minute. 2i An aqueous lubrication solution comprised of about 0.5 wt % of cetylpyridinium 22 chloride and about 0.15 wt % of silicone emulsion was then sprayed on the glove 1 while tumbling in the lubricator for about 156 seconds at 55°C. The spraying 2 was stopped for about 1 minute. The spraying process was repeated again two 3 more times. At the end of the third spraying, the glove was tumbled for about 25 4 minutes and allowed to cool for about 10 minutes. The glove was removed from 5 the lubricator and turned inside out manually. The glove was dried again in the e dryer at about 50°C for about 5 minutes and allowed to cool down to room 7 temperature for about 5 minutes. 8 The packed glove after gamma sterilization had a tensile strength of 4352 9 psi, a tensile stress at 500% of 341 psi, and an ultimate elongation of 984%. lo The static and kinetic COF for the inside surface were 0.41 and 0.17, ii respectively. The static and kinetic COF for the outside surface were 1.38 and i2 1.62, respectively. The donning characteristics of the sterile glove were i3 excellent with a rating of 5 with respect to damp skin on a scale of 1 to 5. The i4 adhesion of the coating was excellent with a rating of 5 on a scale of 1 to 5, i.e., is no flaking or shedding of the powder was observed after stretching the glove to i6 about 500% and rubbing it repeatedly with the thumb (where about 4 to about i7 4.5 is the adhesion value exhibited by commercially available glove coatings). is Example 3 i9 A powder-free coated natural rubber latex glove with an intermediate 20 natural rubber-nitrile layer between the glove and the nitrile coating was 2i prepared as set forth in Example 1 except that the chlorine concentration in the 22 aqueous chlorinated solution was adjusted to about 546 ppm. 1 Before sterilization, the glove had a tensile strength of 4324 psi, a tensile 2 stress at 500% of 270 psi, and an ultimate elongation of 1032%. The static and 3 kinetic COF for the inside surface were 0.39 and 0.28, respectively. The static 4 and kinetic COF for the outside surface were 1.34 and 1.57, respectively. The 5 donning characteristics of the sterile glove were excellent with a rating of 5 with 6 respect to damp skin on a scale of 1 to 5. The adhesion of the coating was 7 excellent with a rating of 5 on a scale of 1 to 5, i.e., no flaking or shedding of the 8 powder was observed after stretching the giove to about 500% and rubbing it 9 repeatedly with the thumb. ιo Example 4 ii A powder-free coated natural rubber latex glove with an intermediate i2 natural rubber-nitrile layer between the glove and the nitrile coating was i3 prepared as set forth in Example 1 except that the chlorine concentration in the i4 aqueous chlorinated solution was adjusted to about 146 ppm. is Before sterilization, the glove had a tensile strength of 4310 psi, a tensile i6 stress at 500% of 299 psi, and an ultimate elongation of 1042%. The static and 17 kinetic COF for the inside surface were 1.06 and 0.64, respectively. The static is and kinetic COF for the outside surface were 1.1 and 1.33, respectively. The i9 donning characteristics of the sterile glove were good with a rating of 4 with 20 respect to damp skin on a scale of 1 to 5. The adhesion of the coating was 2i excellent with a rating of 5 on a scale of 1 to 5, i.e., no flaking or shedding of the 1 powder was observed after stretching the glove to about 500% and rubbing it 2 repeatedly with the thumb. 3 Examples 5-8 4 Powder-free coated natural rubber latex gloves with an intermediate 5 natural rubber-nitrile layer between the glove and the nitrile coating are prepared 6 as set forth in Examples 1 , 2, 3 or 4 except that the total percent solid content for 7 the intermediate natural rubber-nitrile blend latex is adjusted to 1 .5%, 2.0%, 8 2.5%. and 10% [corresponding to Examples 5, 6, 7 and 8 respectively]. 9 The gloves prepared as set forth in Examples 5-8 will have physical lo properties similar to those described in Examples 1 through 4. The donning ii characteristics of the gloves are excellent with a rating of 4 to 5 with respect to 12 damp skin on a scale of 1 to 5. The adhesion of the coatings are excellent with a 13 rating of 5 on a scale of 1 to 5. 14 Example 9 is A powder-free nitrile-coated Neoprene glove with an intermediate natural 16 rubber-nitrile layer between the glove and the nitrile coating is prepared as 17 follows. A glove former is pre-heated to about 40°C to about 60°C in an oven. is The preheated former is dipped into a stirred, alcohol based coagulant i9 suspension maintained at less than about 55°C. The coagulant-dipped former is 20 then returned to the heated oven to dry the coagulant layer. 2i The coagulant-coated former is dipped into a compounded neoprene 22 copolymer latex which is maintained at about 20°C to about 28°C for a time 1 sufficient to produce the desired glove thickness. The neoprene copolymer latex 2 is compounded with stabilizers, crosslinker, vulcanization activator, vulcanization 3 accelerators, antioxidant, antiozonant and optionally, white or colored pigments. 4 The solid content of the compounded latex is about 48 wt. %. The former 5 bearing the coagulated latex is then removed from the compounded neoprene 6 copolymer latex and immediately dipped into a second rubber blend latex for a 7 time sufficient to produce the desired thickness. The rubber blend latex is 8 comprised of about 2.5% compounded natural rubber latex and about 2.5% of 9 carboxylated acrylonitrile butadiene latex and about 95% water. The formulation lo of the compounded natural rubber latex used in this rubber latex is the same as ii the one used in Example 1. The ratio of acrylonitrile/butadiene/carboxylic acid i2 for the nitrile rubber is 39/58/3. 13 The former is removed from the second rubber blend latex and leached in i4 water maintained at about 60°C. The former is then dipped into a compounded is nitrile blend latex with a total solid content of about 5% to form a coating on the i6 intermediate natural rubber-nitrile blend layer. The nitrile blend latex is i7 comprised of a 50/50 blend of two carboxylated acrylonitrile butadiene rubber is latices with two different acrylonitrile/butadiene/carboxylic acid ratios, 39/58/3 i9 and 38/55/6. The formulation of the nitrile blend latex is the same as the one 0 used in Example 1. 2i The cuff of the coated glove is beaded and the former placed in an oven 22 maintained at about 150°C for about 20 minutes in order to cure the glove. The 1 former bearing the glove is then removed from the oven and allowed to cool. 2 The glove is stripped from the former. The glove is then post-processed by 3 chlorination/lubrication according to the process set forth in Example 1 except 4 that the chlorine concentration of the chlorinated solution is adjusted to about 5 344 ppm. 6 Before sterilization, the powder-free nitrile coated neoprene copolymer 7 glove prepared as set forth in Example 9 will have a thickness of about 7 to 8 about 9 mils in the palm area and a tensile strength of about 2700 to about 3200 9 psi, a tensile stress at 500% of about 220 to about 280 psi, and an elongation at lo break of about 900 to about 1100%. The coated glove has excellent donning ii characteristics with a rating of 5 with respect to damp skin on a scale of 1 to 5. i2 The adhesion of the coating is excellent with a rating of 5 on a scale of 1 to 5. 13 Example 10 i4 A powder-free nitrile-coated neoprene copolymer glove with an is intermediate neoprene rubber-nitrile layer between the glove and the nitrile i6 coating is prepared as set forth in Example 9 with the exception that the second i7 rubber blend latex is comprised of about 2.5% compounded neoprene copolymer is latex and about 2.5% of carboxylated acrylonitrile butadiene latex and about i9 95% water;. The formulation of the neoprene copolymer latex is the same used 20 in the first neoprene copolymer latex. The ratio of 2i acrylonitrile/butadiene/carboxylic acid for the nitrile rubber is 39/58/3. 1 Before sterilization, the powder-free nitrile coated neoprene copolymer 2 glove before sterilization will have a thickness of about 0.007 to about 0.009 3 inches in the palm area and a tensile strength of about 2700 to about 3200 psi, a 4 tensile stress at 500% of about 220 to about 280 psi, and an elongation at break 5 of about 900 to about 1100%. The coated glove has excellent donning 6 characteristics with a rating of 4 to 4.5 with respect to a damp skin on a scale of 7 1 to 5. The adhesion of the coating is excellent with a rating of 5 on a scale of 1 8 to 5. 9 Example 11 lo A powder-free nitrile-coated nitrile rubber glove with an intermediate ii natural rubber-nitrile layer between the glove and the nitrile coating is prepared i2 as follows. A glove former is pre-heated to about 40°C to about 60°C in an oven. i3 The preheated former then is dipped into a stirred, alcohol based coagulant i4 suspension maintained at less than about 55°C. The coagulant layer which had is been deposited on the glove former is then allowed to dry. 16 The coagulant-coated former is dipped into a compounded nitrile latex i7 which is maintained at about 20°C to about 30°C for a time sufficient to produce is the desired glove thickness. The nitrile latex is compounded with crosslinker, i9 vulcanization activator, vulcanization accelerator, and optionally, antioxidant and 2o white or colored pigment. The solid content of the compounded latex is about 30 2i wt. %. The former bearing the coagulated latex is then removed from the 22 compounded nitrile latex and immediately dipped into a second rubber blend „ 1 latex for a time sufficient to produce the desired thickness. The rubber blend 2 latex is comprised of about 2.5% compounded natural rubber latex and about 3 2.5% of carboxylated acrylonitrile butadiene latex and about 95% water. The 4 formulation of the compounded natural rubber latex used in this rubber blend 5 latex is the same as the one used in Example 1. 6 The former is removed from the second rubber blend latex and leached in 7 water maintained at about 25°C to about 45°C. The former is then dipped into a β compounded nitrile blend latex with a total solid content of about 5% to form a 9 coating on the intermediate natural rubber-nitrile blend layer. The nitrile blend lo latex is comprised of a 50/50 blend of two carboxylated acrylonitrile butadiene ii rubber lattices with two different acrylonitrile/butadiene/carboxylic acid ratios, i2 39/58/3 and 39/55/6. The formulation of the nitrile blend latex is the same as the i3 one used in Example 1. i4 The cuff of the coated glove is beaded and the former placed in an oven is maintained at about 125°C for about 20 minutes in order to cure the glove. The i6 former bearing the glove is then removed from the oven and allowed to cool. i7 The glove is stripped from the former. The glove is then post-processed by is chlorination/lubrication according to the process set forth in Example 1. i9 Before sterilization, the powder-free nitrile coated nitrile glove prepared as 2o set forth in Example 10 will have a thickness of about 0.004 to about 0.007 2i inches in the palm area and a tensile strength of about 2000 to about 5000 psi, a 22 tensile stress at 500% of about 600 to about 2000 psi, and an elongation at ^ 36 1 break of about 400% to about 900%. The coated glove has excellent donning 2 characteristics with a rating of 5 with respect to dry and damp skin on a scale of 3 1 to 5. The adhesion of the coating is excellent with a rating of 5 on a scale of 1 4 to 5. The adhesion of the coating is excellent with a rating of 5 on a scale of 1 to 5 5. 6 Example 12 7 A powder-free nitrile-coated nitrile glove with an intermediate rubber-nitrile 8 layer between the glove and the nitrile coating is prepared as set forth in 9 Example 11 with the exception that the second rubber blend latex is comprised ιo of about 2.5% compounded nitrile latex and about 2.5% of carboxylated ii acrylonitrile butadiene latex and about 95% water. The formulation of the i2 compounded nitrile latex is the same used in the first compounded nitrile latex i3 that makes up the nitrile base glove. The ratio of i4 acrylonitrile/butadiene/carboxylic acid for the carboxylated nitrile rubber used in is the blend is 39/58/3. i6 Before sterilization, the powder-free nitrile coated nitrile glove will have a i7 thickness of about 0.004 to about 0.007 inches in the palm area, a tensile is strength of about 2000 to about 5000 psi, a tensile stress at 500% of about 600 i9 to about 2000 psi, and an elongation at break of about 400% to about 900%. 20 The coated glove has excellent donning characteristics with a rating of 5 with 2i respect to dry and damp skin on a scale of 1 to 5. The adhesion of the coating is 22 excellent with a rating of 5 on a scale of 1 to 5. i Example 13 2 A powder-free nitrile-coated natural rubber latex glove with an 3 intermediate natural rubber-nitrile layer between the glove and the nitrile coating 4 was prepared as follows. Glove formers were pre-heated to about 60°-70°C in 5 an oven for about 5 minutes. The preheated former then was dipped into a 6 stirred, water based coagulant dispersion maintained at a temperature between 7 about 55°C to about 60°C. The coagulant-dipped former was then returned to 8 the heated oven for about 5 minutes to dry the coagulant layer. 9 The coagulant-coated former was dipped into a compounded natural lo rubber latex for a time sufficient to produce the desired glove thickness. The ii natural rubber latex was compounded with stabilizers, crosslinker, vulcanization 12 activator, vulcanization accelerators, antioxidant, antiozonant and white pigment. i3 The solid content of the compounded latex was about 36 -37 wt. %. The former i4 bearing the coagulated latex was then removed from the compounded natural is rubber latex and immediately dipped into a second rubber blend latex for about i6 13 to 15 seconds. The rubber blend latex comprised about 8.0% compounded i7 natural rubber latex and about 2.5% of carboxylated acrylonitrile butadiene latex is and about 89.5% water. The formulation of the compounded natural rubber latex i9 used in this rubber blend latex was the same as the one used in the first latex 20 dipping. The ratio of acrylonitrile/butadiene/carboxylic acid for the nitrile rubber 2i was 39/58/3. 1 The former was removed from the second rubber blend latex and dried in 2 a heated oven at about 140° - 145°C. The coagulated latex layer was leached 3 in water maintained at about 55°C to about 80°C for about 5 minutes. The 4 former was then dipped into a compounded nitrile blend latex with a total solid 5 content of about 4 - 5.5% to form a coating on the intermediate natural rubber- 6 nitrile blend layer. The nitrile blend was comprised of a 50/50 blend of two 7 carboxylated acrylonitirile butadiene latices with two different 8 acrylonitrile/butadiene/carboxylic acid ratios 39/58/3 and 39/55/6. The nitrile 9 blend latex was further compounded with 1 part of sulfur dispersion (crosslinker), ιo 1 part of ZDBC dispersion (vulcanization accelerator), 3 parts of ZnO dispersion ii (vulcanization activator) and 15 parts of silicone emulsion (SM 2140 obtained 12 from General Electric). The dwell time for the coating dipping was about 13 to i3 about 15 seconds. i4 The cuff of the coated glove was beaded by a header and the former was is placed in an oven maintained at about 100 - 136 C for about 20 minutes in order i6 to cure the glove. The former bearing the glove was then removed from the i7 oven and allowed to cool. The glove was then stripped from the former. is The glove was then post-processed by cholorination. First, the coated i9 glove was turned inside out manually and loaded into a chlorinator. The glove 2o was pre-rinsed 2 times for a total time of about 5 minutes. An aqueous chlorine 2i solution of about 250 -350 ppm chlorine was added to the chlorinator and the 22 gloves tumbled for about 8.3 minutes. The chlorinated solution was then 1 neutralized with 50% sodium hydroxide solution for about 4 minutes. The glove 2 was post-rinsed 4 times for a total time of about 10 minutes. The glove was then 3 transferred to a tumbling washer for the lubrication process. Excess water was 4 removed from the glove by spinning the glove for about 2 minutes. The washer 5 was then filled with an aqueous lubrication solution comprised of about 0.8 wt % 6 of cetylpyridinium chloride and 0.1 wt % of silicone emulsion. The glove was 7 tumbled in the lubrication solution for about 5 minutes. The lubrication solution 8 was drained and the glove was tumbled for an additional 5 minutes. The glove 9 was then removed from the tumbler washer and dried in a dryer with a heating ιo cycle of about 20 minutes at about 55 C and a cool down cycle for about 10 ii minutes. The glove was removed from the dryer and turned inside out manually. i2 The glove was dried again in the dryer at about 50 C for about 5 minutes and i3 allowed to cool down to room temperature for about 5 minutes. i4 The powder-free coated gloves had a tensile strength of 3769 psi, a is tensile stress at 500% of 156 psi, and an ultimate elongation of 943%. The static i6 and kinetic COF for the inside surface were 0.44 and 0.32, respectively. The i7 static and kinetic COF for the outside surface were 1.90 and 2.98, respectively. is The glove dons extremely well with respect to damp and wet skin with a rating of i9 5. The adhesion of the inventive coating is excellent with a rating of 5 on a scale 20 of 1 to 5, i.e., no flaking or shedding of the powder was observed after stretching 2i the glove to about 500% and rubbing it repeatedly with the thumb. 22 The packed gloves were sterilized by electron beam sterilization at a dose 1 range of 29.4 KGy and 30.3 KGy. The sterile glove had a tensile strength of 2 4064 psi, a tensile stress at 500% of 288 psi, and an ultimate elongation of 3 908%. The donning characteristics of the sterile glove were excellent with a 4 rating of 5 with respect to damp skin on a scale of 1 to 5, i.e., no flaking or 5 shedding of the powder was observed after stretching the glove to about 500% e and rubbing it repeatedly with the thumb. The adhesion of the inventive coating 7 was excellent with a rating of 5 on a scale of 1 to 5. 8 Example 14 9 A powder-free nitrile-coated rubber latex glove with an intermediate lo natural rubber-nitrile layer between the glove and the nitrile coating was ii prepared as set forth in Example 13 except that the nitrile blend latex was 12 compounded with 1 part of sulfur dispersion (crosslinker), 1 part of ZDBC i3 dispersion (vulcanization accelertor), 3 parts of ZnO dispersion (vulcanization i4 activator), 15 parts of silicone emulsion (SM 2140 obtained from General is Electric), and 1 part of an industrial biocide. i6 Before sterilization, the glove had a tensile strength of 3954 psi, a tensile i7 stress at 500% of 156 psi, and an ultimate elongation of 943%. The static and is kinetic COF for the inside surface were 0.43 and 0.29, respectively. The static i9 and kinetic COF for the outside surface were 1.72 and 2.75, respectively. The 20 donning characteristics of the sterile glove were excellent with a rating of 5 with 2i respect to damp skin on a scale of 1 to 5. The adhesion of the coating was 22 excellent with a rating of 5 on a scale of 1 to 5, i.e., no flaking or shedding of the 1 powder was observed after stretching the glove to about 500% and rubbing it 2 repeatedly with the thumb. 3 Example 15 4 A powder-free nitrile-coated natural rubber latex glove with an 5 intermediate natural rubber-nitrile layer between the glove and the nitrile coating e was prepared as set forth in Example 13 with the exception that the second 7 rubber blend latex is comprised of about 8.0% compounded natural rubber latex 8 and about 2.5% of acrylonitrile butadiene copolymer latex and about 89.5% 9 water. lo Before sterilization, the powder-free nitrile coated natural rubber latex ii glove will have a thickness of about 0.004 to about 0.0010 inches in the palm i2 area, a tensile strength of about 3500 to about 4800 psi, a tensile stress at 500% i3 of 150 to about 800 psi and an elongation at break of about 700 to about 1000%. i4 The coated glove has excellent donning characteristics with a rating of 5 with is respect to dry and damp kin on a scale of 1 to 5. The adhesion of the coating is i6 excellent with a rating of 5 on a scale of 1 to 5. i7 The foregoing description and examples relate only to preferred is embodiments of the present invention and numerous changes and modifications i9 may be made therein without departing from the spirit and scope of the invention 20 as defined in the following claims.

Claims: 2 What is claimed is: 3 1. A powder-free elastomeric glove having an internal surface comprising a 4 first elastomeric layer, a second intermediate layer of a rubber blend 5 comprised of a natural rubber and a nitrile rubber disposed on said first 6 layer and a nitrile rubber coating disposed on said intermediate layer. 7 2. The glove of claim 1 wherein the first elastomeric layer is comprised of 8 natural rubber. 9 3. The glove of claim 1 wherein the first elastomeric layer is comprised of lo neoprene rubber. ii 4. The glove of claim 1 wherein the first elastomeric layer is comprised of i2 nitrile rubber. i3 5. The glove of claim 1 wherein the first elastomeric layer is comprised of i4 synthetic polyisoprene rubber. is 6. The glove of claim 1 wherein the nitrile rubber coating is comprised of a i6 carboxylated acrylonitrile butadiene rubber. i7 7. The glove of claim 1 wherein the nitrile rubber in the second intermediate is layer is comprised of a carboxylated acrylonitrile butadiene rubber having 19 an acrylonitrile content of about 25 to about 40 parts, a butadiene content 20 of about 55 to about 68 parts and a carboxylic acid content of about 3 to 2i about 6 parts. 1 8. The glove of claim 6 wherein the nitrile rubber coating is comprised of a 2 blend of two carboxylated acrylonitrile butadiene rubbers with different 3 acrylonitrile/butadiene/carboxylic acid ratios. 4 9. The glove of claim 8 wherein each of the two carboxylated acrylonitrile 5 butadiene rubbers with different acrylonitrile/butadiene/carboxylic acid 6 ratios has an acrylonitrile content of about 25 to about 40 parts, a 7 butadiene content of about 55 to about 68 parts and a carboxylic acid 8 content of about 3 to about 6 parts. 9 10. A powder-free elastomeric glove having an internal surface comprising a lo first elastomeric layer, a second intermediate layer of a rubber blend ii comprised of a synthetic rubber and a nitrile rubber disposed on said first i2 layer and a nitrile rubber coating disposed on said intermediate layer. i3 11. The glove of claim 10 wherein the first elastomeric layer is comprised of i4 natural rubber. is 12. The glove of claim 10 wherein the first elastomeric layer is comprised of i6 neoprene rubber. i7 13. The glove of claim 10 wherein the first elastomeric layer is comprised of is nitrile rubber. i9 14. The glove of claim 10 wherein the first elastomeric layer comprised of a 20 synthetic polyisoprene rubber. 1 15. The glove of claim 10 wherein the first elastomeric layer is comprised of 2 the same synthetic rubber used in the intermediate layer. 3 16. The glove of claim 15 wherein the synthetic rubber is neoprene rubber. 4 17. The glove of claim 15 wherein the synthetic rubber is nitrile rubber. 5 18. The glove of claim 15 wherein the synthetic rubber is a synthetic 6 polyisoprene. 7 19. The glove of claim 10 wherein the nitrile rubber coating is comprised of a 8 carboxylated acrylonitrile butadiene rubber. 9 20. The glove of claim 19 wherein the nitrile rubber in the second intermediate lo layer is comprised of a carboxylated acrylonitrile butadiene rubber having ii an acrylonitrile content of about 25 to about 40 parts, a butadiene content i2 of about 55 to about 68 parts and a carboxylic acid content of about 3 to i3 about 6 parts. i4 21. The glove of claim 19 wherein the nitrile rubber coating is comprised of a is blend of two carboxylated acrylonitrile butadiene rubbers with different i6 acrylonitrile/butadiene/carboxylic acid ratios. i7 22. The glove of claim 21 wherein each of the two carboxylated acrylonitrile is butadiene rubbers with different acrylonitrile/butadiene/carboxylic acid 19 ratios has an acrylonitrile content of about 25 to about 40 parts, a 20 butadiene content of about 55 to about 68 parts and a carboxylic acid 2i content of about 3 to about 6 parts. 1 23. A process for making a powder-free elastomeric glove having an internal 2 surface comprising a first elastomeric layer, a second intermediate layer of 3 a rubber blend comprised of a natural rubber and a nitrile rubber disposed 4 on said first layer and a nitrile rubber coating disposed on said 5 intermediate layer, comprising the steps of: 6 (a) dipping a former into a coagulant dispersion to deposit a 7 coagulant layer on the former; 8 (b) dipping the former with the deposited coagulant layer into an 9 elastomer to produce a second layer comprising coagulated ιo elastomer layer thereon; ii (c) dipping the second layer of coagulated elastomer into a i2 blend of a natural rubber and a nitrile rubber dispersion to form an i3 intermediate layer on the glove; i4 (d) dipping the intermediate layer of a natural rubber and a is nitrile rubber into a powder-free dispersion comprised of a nitrile 16 rubber dispersion and a lubricant; i7 (e) curing the layers and the coating on the former; is (f) stripping the article from the former; 19 (g) turning the article so that the coated side of the article is on 20 the exterior of the article; 2i ( ) treating the article to remove powder; 22 (i) drying the article; 1 (j) turning the article so that the coated side of the article is on 2 the interior of the article; and 3 (k) drying the article. 4 24. The process of claim 23 wherein the step of treating the article to remove 5 powder comprises the step of immersing the article into an aqueous 6 chlorinated solution followed by the step of rinsing the article. 7 25. The process of claim 24 comprising the additional step of applying a β lubricant solution to the coated surface of the article after the chlorination 9 and rinsing steps. lo 26. The process of claim 23 comprising the additional step of leaching the ii article in water after the former is dipped into the natural rubber and nitrile i2 rubber dispersion to produce the intermediate layer. i3 27. The process of claim 26 wherein the step of treating the article to remove i4 powder comprises the step of immersing the article into an aqueous is chlorinated solution followed by the step of rinsing the article. i6 28. The process of claim 27 comprising the additional step of applying a i7 lubricant solution to the coated surface of the article after the chlorination is and rinsing steps. i9 29. A process for making a powder-free elastomeric glove having an internal 20 surface comprising a first elastomeric layer, a second intermediate layer of 2i a rubber blend comprised of a synthetic rubber and a nitrile rubber 1 disposed on said first layer and a nitrile rubber coating disposed on said 2 intermediate layer, comprising the steps of: 3 (a) dipping a former into a coagulant dispersion to deposit a 4 coagulant layer on the former; 5 (b) dipping the former with the deposited coagulant layer into an 6 elastomer to produce a second layer comprising coagulated elastomer 7 layer thereon; 8 (c) dipping the second layer of coagulated elastomer into a blend of 9 a synthetic rubber and a nitrile rubber dispersion to form an lo intermediate layer on the glove; ii (d) dipping the intermediate layer of a synthetic rubber and a nitrile i2 rubber into a powder-free dispersion comprised of a nitrile rubber 13 dispersion and a lubricant; i4 (e) curing the layers and the coating en the former; is (f) stripping the article from the former; i6 (g) turning the article so that the coated side of the article is on the 17 exterior of the article; is (h) treating the article to remove powder; 19 (i) drying the article; 20 (j) turning the article so that the coated side of the article is on the 2i interior of the article; and 1 (k) drying the article. 2 30. The process of claim 29 wherein the step of treating the article to remove 3 powder comprises the step of immersing the article into an aqueous 4 chlorinated solution followed by the step of rinsing the article. 5 31. The process of claim 30 comprising the additional step of applying a 6 lubricant solution to the coated surface of the article after the chlorination 7 and rinsing steps. 8 32. The process of claim 29 comprising the additional step of leaching the 9 article in water after the former is dipped into the synthetic rubber and lo nitrile rubber dispersion to produce the intermediate layer. ii 33. The process of claim 32 wherein the step of treating the article to remove i2 powder comprises the step of immersing the article into an aqueous i3 chlorinated solution followed by the step of rinsing the article. 14 34. The process of claim 33 comprising the additional step of applying a is lubricant solution to the coated surface of the article after the chlorination 16 and rinsing steps. i7 35. A powder-free elastomeric glove having an internal surface comprising a is first elastomeric layer and a second intermediate layer of a rubber blend i9 comprised of a natural rubber and a nitrile rubber disposed on said first 20 layer. 1 36. A powder-free elastomeric glove having an internal surface comprising a 2 first elastomeric layer and a second intermediate layer of a rubber blend 3 comprised of a synthetic rubber and a nitrile rubber disposed on said first 4 layer. 5 37. A process for making a powder-free elastomeric glove having an internal 6 surface comprising a first elastomeric layer, a second intermediate layer of 7 a rubber blend comprised of a natural rubber and a nitrile rubber disposed 8 on said first layer and a nitrile rubber coating disposed on said 9 intermediate layer comprising the steps of; lo (a) dipping a former into a coagulant dispersion to deposit a ii coagulant layer on the former; i2 (b) dipping the former with the deposited coagulant layer into an 13 elastomer to produce a second layer comprising coagulated i4 elastomer layer thereon; is (c) dipping the second layer of coagulated elastomer into a i6 blend of natural rubber and a nitrile rubber dispersion to form an 17 intermediate layer on the glove; is (d) leaching the former with the coagulated elastomer layer and i9 the intermediate rubber blend layer in water; 20 (e) dipping the intermediate layer of a natural rubber and a 2i nitrile rubber into a powder-free dispersion comprised of a nitrile 22 rubber dispersion and a lubricant; 1 (f) curing the layers and the coating on the former; 2 (g) stripping the article from the former; 3 (h) treating the article to remove powder by immersing the 4 article into an aqueous chlorinated solution; 5 (i) rinsing the article; and 6 (j) drying the article. 7 38. A process for making a powder-free elastomeric glove having an internal 8 surface comprising a first elastomeric layer, a second intermediate layer of 9 a rubber blend comprised of a synthetic rubber and a nitrile rubber lo disposed on said first layer and a nitrile rubber coating disposed on said ii intermediate layer comprising the steps of: 12 (a) dipping a former into a coagulant dispersion to deposit a i3 coagulant layer on the former. i4 (b) dipping the former with the deposited coagulant layer into an is elastomer to produce a second layer comprising coagulated i6 elastromer layer thereon; i7 (c) dipping the second layer of coagulated elastomer into a is blend of synthetic rubber and a nitrile rubber dispersion to 19 form an intermediate layer on the glove; 20 (d) leaching the former with the coagulated elastomer layer and 2i the intermediate rubber blend layer in water; 1 (e) dipping the intermediate layer of a synthetic rubber and a 2 nitrile rubber into a powder-free dispersion comprised of a 3 nitrile rubber dispersion and a lubricant; 4 (f) curing the layers and the coating on the former; 5 (g) stripping the article from the former; 6 (h) treating the article to remove powder by immersing the 7 article into an aqueous chlorinated solution; 8 (i) rinsing the article; and 9 (j) drying the article. lo 39. The glove of claim 1 wherein the nitrile rubber coating is comprised of an ii acrylonitrile butadiene rubber. i2 40. The glove of claim 1 wherein the nitrile rubber in the second intermediate i3 layer is comprised of an acrylonitrile butadiene rubber having an i4 acrylonitrile content of about 25 to about 40 parts and a butadiene content is of about 50 to about 75 parts. i6 41. The glove of claim 1 wherein the total solid content of the dispersion from i7 which the intermediate rubber blend layer is formed is less than about i9 42. The glove of claim 1 wherein the nitrile rubber coating is comprised of a 20 blend of nitrile rubber and synthetic rubber. 1 43. A powder-free elastomeric article having an internal surface comprising a 2 first elastomeric layer, a second intermediate layer of a rubber blend 3 comprised of a natural rubber and a nitrile rubber disposed on said first 4 layer and a nitrile rubber coating disposed on said intermediate layer. 5 44. The article of claim 43 wherein the first elastomeric layer is comprised of 6 natural rubber. 7 45. The article of claim 43 wherein the first elastomeric layer is comprised of 8 neoprene rubber. 9 46. The article of claim 43 wherein the first elastomeric layer is comprised of lo nitrile rubber. ii 47. The article of claim 43 wherein the first elastomeric layer is comprised of i2 synthetic polyisoprene rubber. i3 48. The article of claim 43 wherein the nitrile rubber coating is comprised of a i4 carboxylated acrylonitrile bu t adiene rubber.

Inventors: TAN SHARON MI LYN, WONG WEI CHEONG, YEH YUN-SIUNG TONY, ZHU DUANNA, TAN, SHARON, MI, LYN, WONG, WEI, CHEONG, YEH, YUN-SIUNG, TONY, ZHU, DUANNA
Applicants: ALLEGIANCE CORP, ALLEGIANCE CORPORATION
Application year: 2000
Main classification: A41D19
IPC codes: A41D19, B29C41, C08J7