ELASTOMERIC COMPOSITIONS FOR DAMPING

Abstract: A vulcanizate that has improved damping properties where the vulcanizate is prepared by the steps comprising blending a damping additive within a vulcanizable composition of matter, wherein the vulcanizable composition of matter includes a vulcanizable elastomer, and effecting vulcanization of the elastomer.

Description: ELASTOMERIC COMPOSITIONS FOR DAMPING TECHNICAL FIELD This invention is generally directed toward compositions of matter that are useful for damping. More particularly, the compositions of this invention are elastomeric and exhibit improved damping capability over a wide temperature and frequency range due to the addition of a novel damping additive. BACKGROUND OF THE INVENTION Damping is the absorption of energy, such as vibrational or sound energy, by a material in contact with the source of that energy. It is desirable to damp or mitigate the transmission of vibrational energy from a number of sources such as motors, engines, and other power sources. It is known to employ viscoelastic materials for damping applications. In general, energy, such as vibrational energy, is absorbed by the viscoelastic material and the energy is subsequently converted into heat rather than being transferred to the environment as vibrational energy. Ideally, the viscoelastic materials employed for dampening are useful and effective over a wide range of temperatures and frequencies. The viscoelastic nature of materials can be mathematically represented by the formula G*=G'+/G" where G* is the complex shear modulus, G' is the elastic or storage modulus, G" is the viscous or loss modulus and i = "AT. The effectiveness of an viscoelastic material for damping purposes can be quantified by measuring its viscoelastic response to a periodic stress or strain. Results of dynamic mechanical tests are generally given in terms of elastic or storage modulus, G', and viscous or loss modulus, G". The loss modulus G" is directly related to the amount of mechanical energy that is converted to heat, or in other words, damping. The ratio of the loss modulus G", to the elastic modulus, G', is denoted by tan (δ) = G'VG' which is a parameter that quantifies the ability of a material to dissipate mechanical energy into heat versus the purely elastic storage of mechanical motion during one cycle of oscillatory movement. The measurement of tan (δ) can be made by a dynamic analyzer, and may be made by a sweep of frequencies at a fixed temperature, then repeating that sweep of frequencies at several other temperatures, followed by the development of a master curve of tan (δ) versus frequency by curve alignment. An alternate method is to measure tan (δ) at constant frequency over a temperature range. In common practices, the tan (δ) of a material is usually adjusted or broadened by taking advantage of the glass transition temperature of several materials within a temperature range. SUMMARY OF INVENTION Although numerous compositions are known for damping, there is a need for improved damping compositions that exhibit a high degree of damping over a wide range of temperatures and frequencies without involving glass transition peaks. Enhancing hysteresis (tan (δ)) by using super position of glass transition peaks is not desirable because the modulus of the material drops dramatically at or about the glass transition temperature. One aspect of the present invention to provide a composition of matter that is useful as a damping material without involving glass transition peaks. Another aspect of the present invention provides a composition of matter that is useful as a damping material over a wide range of temperatures and frequencies without involving glass transition peaks. Another aspect of the present invention provides a vulcanizable composition that is useful as a damping material, and provides damping over a wide temperature and frequency range without involving glass transition peaks. Another aspect of the present invention provides tire rubbers that exhibit increased damping over a wide temperature and frequency range. Another aspect of the present invention provides tires having a high degree of damping. Another aspect of the present invention provides tires having improved traction and skid resistance. In general, therefore, the present invention provides a vulcanizate that has improved damping properties where the vulcanizate is prepared by the steps comprising blending an unsaturated damping additive within a vulcanizable composition of matter, wherein the vulcanizable composition of matter includes a vulcanizable elastomer, and effecting vulcanization of the elastomer The present invention also provides an elastomeric composition of matter that has improved damping properties comprising a cured elastomeric matrix, and from about 10 to about 1 ,000 parts by weight per one hundred parts by weight rubber of an unsaturated damping additive dispersed within the elastomeric matrix. BRIEF DESCRIPTION OF THE DRAWINGS The Figure is a theoretical plot of a crosslinking reaction and shows the percent gelation as a function of the ratio of crosslinking agent to prepolymer that is crosslinked. EMBODIMENTS OF THE INVENTION The addition of certain polymeric materials to an elastomeric composition of matter gives rise to rubber compounds having improved mechanical properties including improved damping. These polymeric materials, which may also be referred to as damping additives, are characterized by having a tan (δ) that is greater than or equal to about 0.35 in the temperature range from about -40°C to about 120°C. Preferably, the tan (δ) is substantially constant within this temperature range. In a preferred embodiment, the damping additives are viscoelastic and therefore have a glass transition temperature that is less than or equal to about -20°C. According to one embodiment of the present invention, at least one damping additive is added to an elastomeric binder or matrix. Preferably, the damping additive is miscible within the elastomeric matrix. A useful amount of damping additive includes from about 10 to about 1,000 parts by weight damping additive per one hundred parts by weight elastomeric binder (phr). Preferably, the damping additive is employed in an amount from about 30 to about 500 parts by weight phr, and even more preferably in an amount from about 50 to about 300 parts by weight phr. Many elastomeric materials can be used as a binder or matrix. Useful elastomeric materials include, without limitation, natural and synthetic elastomers. For example, these elastomers include, without limitation, natural rubber, synthetic polyisoprene rubber, styrene/butadiene rubber (SBR), polybutadiene, butyl rubber, neoprene, ethylene/propylene rubber, ethylene/propylene/diene rubber (EPDM), acrylonitrile/butadiene rubber (NBR), silicone rubber, the fluoroelastomers, ethylene acrylic rubber, ethylene vinyl acetate copolymers (EVA) epichlorohydrin rubbers, chlorinated polyethylene rubber, chlorosulfonated polyethylene rubbers, hydrogenated nitrile rubber, tetrafluoroethylene/propylene rubber, polyurethane, and mixtures thereof. As used herein, the term "elastomer" will refer to a blend of synthetic and natural rubber, a blend of various synthetic elastomers, or simply one type of elastomer. The elastomers that are useful in practicing this invention include any of the various functionalized elastomers conventionally employed in the art of manufacturing rubber materials and tire rubbers. The damping additive is typically blended with the elastomeric binder by dry mixing methods. For example, the dampening additive may be pre-blended with the binder and then the pre-blend or masterbatch can be compounded with optional fillers, vulcanizing agents, and other rubber additives. Alternatively, the dampening additive may be added directly to a vulcanizable composition of matter or binder that includes at least one elastomer as well as other optional rubber additives including fillers and vulcanizing agents. This mixing or blending preferably occurs in mixing apparatus that are conventionally employed in the art. For example, a mill or internal mixer can be employed. Alternatively, the damping additive can be blended in to the elastomeric binder while in solution. For example, the damping additive and polymeric matrix can be dissolved in a solvent and the solution can be subsequently blended. The solvent is then evaporated, which leaves behind the elastomer-damping additive mixture. Without excluding heterogeneous mixtures, it is preferred that the elastomeric matrix and the damping additive form a homogeneous blend; that is, discrete particles or domains of the elastomeric matrix or damping additive are not visible when using light scattering techniques. Once the damping additive is added, the elastomeric matrix is cured or vulcanized by using techniques that are conventional in the art. Conventional vulcanization typically includes using vulcanizing agents in an amount from about 0.5 to about 4 parts by weight per hundred parts elastomeric binder (phr). For example, sulfur or peroxide-based curing systems may be employed. For a general disclosure of suitable vulcanizing agents one can refer to Kirk-Othmer, Encyclopedia of Chemical Technology, 3rd Edition, Wiley Interscience, N.Y. 1982, Vol. 20, pp. 365-468, particularly "Vulcanization Agents and Auxiliary Materials" pp. 390-402, or "Vulcanization" by A.Y. Coran, Encyclopedia of Polymer Science and Engineering, 2 nd Edition, John Wiley & Sons, Inc., 1989; both of which are incorporated herein by reference. Vulcanizing agents may be used alone or in combination. This invention does not affect cure processes and thus the matrix polymers can be cured using conventional processes. The cured elastomeric binder, which according to this invention will include a damping additive and optional other additives, will be referred to as a rubber product, vulcanizate, or simply rubber. Once cured, the elastomeric matrix or rubber product containing the damping additive according to this invention is preferably soft and has a Shore A hardness that is less than or equal to about 80; more preferably, the Shore A hardness is less than or equal to about 50, and even more preferably less than or equal to about 40. Where the damping additive does not contain a functionality that will react with a vulcanizing agent, vulcanization or curing of the elastomeric matrix will entrap the damping additive within the elastomeric network. On the other hand, where the damping additive contains unsaturation or a functionality that will react with a vulcanizing agent, vulcanization of the elastomeric matrix will cause the damping additive to likewise undergo crosslinking and become incorporated into the crosslinked elastomeric network. Other components that may be added to the elastomeric binder or matrix include reinforcing fillers, plasticizers, antioxidants, processing aids, and dyes. In general, reinforcing fillers can preferably include carbon black and silica. The present invention should not be limited to the use of these fillers inasmuch as those practicing the invention can likewise employ mineral fillers such as clays, including hard clays, soft clays, and chemically modified clays, mica, talc (magnesium silicate), calcium carbonate, titanium dioxide, ground coal, ground and/or reclaimed rubber, magnesium hydroxide, alumina trihydrate, and mixtures thereof. For further explanation of rubber compounding and additives conventionally employed, one can refer to The Compounding and Vulcanization of Rubber by Stephens in RUBBER TECHNOLOGY, SECOND EDITION, Van Nostrand Reinhold Company (1973). The damping additives employed in this invention are polymeric materials that are characterized by having a tan (δ) that is greater than or equal to about 0.35 in the temperature range from about -20°C to about 120°C. Preferably, the tan (δ) within this temperature range is greater than or equal to about 0.50, and even more preferably greater than or equal to about 0.8. In an especially preferred embodiment, the damping additives are characterized by a substantially constant tan (δ) within the temperature range from about -20°C to about 120°C. By substantially constant, it is meant that the tan (δ) within this range should not vary by more than 50 percent. Even more preferably, the tan (<5) should not vary by more than 30 percent, more preferably by not more than 20 percent, and even more preferably by not more than 10 percent. In a preferred embodiment, the damping additive is elastomeric and has a glass transition temperature that is less than or equal to about -20°C. More preferably its T g is less than or equal to about -35°C, and even more preferably it is less than or equal to about -50°C. Several polymeric materials can be employed as the damping additive of this invention. Therefore, the selection of any one specific polymeric material exhibiting the desired properties should not limit the scope of the invention. Indeed, once provided with the knowledge of this invention, those skilled in the art will be able to select and synthesize other polymeric compositions for use as a damping additive. Useful damping additives of this invention typically are made of branched and non-linear macro molecules. The branching may follow a regular structure, as in the case of centipede polymers, or an irregular or random structure, as in the case of hyper-branched polymers. For example, the so-called centipede polymers typically include a high molecular weight spine or backbone having connected thereto many relatively short side chains. It is, however, useful to note that not all regularly branched macromolecules exhibit the damping properties of this invention. For example, the so-called star architecture does not have the superior damping properties needed to materialize this invention. In the case of the centipede structure, when practicing this invention the main polymeric chain, i.e., the spine, is much larger than the entanglement length. As known in the art, the entanglement length of a polymer chain is that number of polymer chain repeating units that correspond to a molecular weight sufficiently large for entanglements to occur between molecules of undiluted polymer. This has been measured as the molecular weight where the slope of a plot of log viscosity vs. log molecular weight changes from 1.0 to 3.4; the change being associated with intermolecular entanglements. In general, the entanglement length has been defined as that length of polymer resulting from about 100 polymer chain repeating units. For purposes of this specification, entanglement length will refer to a polymer chain length that includes a number of polymer chain repeating units that is on the order of magnitude of 100. For example, the entanglement length for polystyrene has been experimentally determined to be about 340 repeating units, a number that is on the order of magnitude of 100. Additional experimental techniques for determining the entanglement length of a polymer are summarized by W.W. Graessley in ADV. POLYM. Sci., Vol. 16, 1974. By much larger than the entanglement length, it is preferred that the main polymeric chain is greater than 10 times larger than the entanglement length, and even more preferably greater than 50 times the entanglement length. The relatively short side chains, on the other hand, should be smaller than or equal to three times the entanglement length. Examples of centipede polymers that can be used in this invention include poly(isobutylene- α/t-n-alkylmaleimide), poly(n-alkylmaleimide-α/t-alkenyl benzene). These centipede polymers are disclosed in co-pending applications including U.S. Serial No. 097,034 and U.S. Serial No. 995,791. Both of these applications and their resulting patents are incorporated herein by reference. Other branched polymeric materials that are useful as damping additives include dendrimers. Dendrimers, in general, are described in great detail in DENDRITIC MOLECULES, CONCEPTS, SYNTHESES, PERSPECTIVES, by G. R. Neukome et al., (VCH Verlagsgesellschaft GmbH, 1996), which is incorporated herein by reference. When practicing this invention, it is useful to use dendrimers where the length of any given dendritic branch is smaller than or on the order of the entanglement length. By smaller than the entanglement length, it is preferred that any given dendritic branch is smaller than five times the entanglement length, and even more preferably smaller than 10 times the entanglement length. Still other branched polymeric materials that are useful as damping additives include hyper-branched polymers where the branching is random or irregular. A hyper-branched polymer refers to a polymeric composition, which includes more than one discrete polymer molecule, that has undergone some degree of crosslinking but is not fully cured. Full or complete cure occurs when a stoiciometrically equivalent amount of curative reacts with a stoiciometrically equivalent amount of polymer. Preferably, a hyper-branched polymer is formed when the degree of inter-chain reaction nears or approaches the gel point of the polymeric composition. For the purposes of this invention, the hyper-branched polymers may be referred to as near-gel polymers. The gel point is where one first observes the visible formation of a gel or insoluble polymer fraction within a polymeric composition. The gel in general is insoluble in all solvents at elevated temperatures under conditions where polymer degradation does not occur, and it theoretically corresponds to the formation of an "infinite" network in which polymer molecules have been crosslinked to one another to form a macroscopic molecule. The gel may then be considered one molecule and the non-gel portion of the polymer remains soluble in solvents and is often referred to as sol. There are several techniques known in the art for estimating the gel point of polymeric compositions. Experimentally, the gel point can be determined by solvent extraction. This procedure is set forth in Principles of Polymer Chemistry, by Paul J. Flory. Other experimental procedures are also set forth therein. The skilled artisan will also appreciate that the gel point can be approximated by using theoretical calculations. In this regard, Principles of Polymerization, Third Edition, by George Odian, John Wiley & Sons, Inc., 1991, pp. 108-123, and Principles of Polymer Chemistry, by Paul J. Flory, pp. 46-47, are incorporated herein by reference. In practicing the present embodiment, the skilled artisan should determine the gel point of the polymeric composition that is employed to create the hyper-branched polymer. For purposes of this specification, the polymeric composition that is employed to create the hyper-branched polymer may be referred to as the prepolymer system. Although the gel point can be discussed in terms of a number of parameters, it is convenient to determine the ratio of the weight of curative to the weight of prepolymer necessary to reach the gel point. Thus, the gel point can be represented by the weight of curative necessary to reach gelation, ^curative-gel, Over the weight Of the prepolymer, JFprepolymer- Likewise, the point of complete cure can be represented by the weight of curative necessary to reach complete cure, over the weight of the prepolymer ^ pre p o ly mer - In general, therefore, the extent of any curing reaction can be represented by the weight of curative added, Curative, over the weight of the prepolymer, ^prep ol ymer- For purposes of this specification, the extent of reaction, r, can be represented by the weight of curative, rF CU rat.ve, over the weight of the prepolymer, f P re P oiymer, i.e.,f curatlve /f prepo ι ymer =r Therefore, the extent of gelation r ge! , is r ge\ = W curaUve . complete/'' prepolymer- Thus, once the gel point of the prepolymer is determined, an appropriate amount of curative is added and reacted with the prepolymer to achieve a hyper-branched polymer. When selecting an appropriate amount of curative, those practicing the present invention should preferably attempt to approach the gel point without exceeding the gel point; although it should be understood that the definition of hyper-branched polymer broadly includes those reaction products of curative and prepolymer that exceed the gel point without actually reaching complete cure. Thus, in the preferred embodiment, the weight ratio that is employed to create a hyper-branched polymer is based on the following formula: E = (|r-rgel|)/(rgel) where E is the relative distance to the gel point, r is the extent of the reaction, and r ge i is the extent of the reaction at the gel point. Generally, E should be less than or equal to 1, preferably less than about 0.5, more preferably less than about 0.2, still more preferably less than about 0.1, and even more preferably equal to or less than 0.05. It should be understood that the foregoing formula includes absolute value brackets and therefore the extent of the reaction, r, is a relative distance, E, beyond the gel point, as well as a relative distance, E, before the gel point. This is best understood with reference to Fig. 1. Here, the relative distance around the gel point, i.e., +1- E, is shown. According to this invention, a hyper-branched polymer is formed when the extent of reaction, r, is within this range. For example, where one determines the gel point of a particular polymeric composition to be about 0.5 parts of curative per part of prepolymer, a hyper-branched polymer can be obtained by reacting the polymeric composition with about 0.3 parts of curative per part of the prepolymer. In this case, the relative distance E = (|0.3 - 0.5|)/(0.5) = 0.4. In another example, where one again determines the gel point of a particular polymeric composition to be about 0.5 parts of curative per part of prepolymer, a hyper-branched polymer can be obtained by reacting the polymeric composition with about 0.7 parts of curative per part of the prepolymer. In this case, the relative distance, E = (|0.7 - 0.5|)/(0.5) = 0.4. With specific regard to the embodiment wherein hyper-branched polymers are employed, the prepolymer that is selected for preparing the hyper- branched polymer should include at least one functional group. Preferably the prepolymer will include at least two functional groups, more preferably between two and about ten functional groups, and even more preferably between two and about five functional groups. For purposes of this specification, the prepolymer may be referred to as the functionalized prepolymer. The functional groups can be located at the terminal end of the prepolymer, including the initiated end of the polymer, or along the backbone of the prepolymer. Therefore, crosslinking of the prepolymer can occur by way of end-linking or random-linking. The functionalized prepolymers that are usefully employed in preparing the hyper-branched polymers can include any of the sundry functional groups that are commonly incorporated in, or grafted to, polymers. Accordingly, the present invention is not limited by any particular functional group. For example and without limitation, functional groups can include primary amino groups (NH 2 ), secondary amino groups (NH), hydroxyl groups (OH), carboxyl groups (COOH), vinyl groups (RCHCH 2 ), epoxy groups, anhydride groups , acyl halide groups (RCOC1), carboxylic acid anhydride groups (RCOOCOR), carboxamide groups (RCONH 2 ), and isocyanate groups (RNCO). As noted above, these functional groups can be located anywhere along the prepolymer backbone including the ends of the prepolymer. Additional examples and a further discussion of functionalized prepolymers is contained in Reactive Extrusion: A Survey of Chemical Reactions of Monomers and Polymers During Extrusion Processing, by Brown, REACTIVE EXTRUSION PRINCIPLES AND PRACTICE, edited by Xanthos, Hanser Publishing, (1992), which is incorporated herein by reference. Any polymeric macromolecule can be selected and functionalized to form the functionalized prepolymers. Accordingly, the scope of the present invention should not be limited by the selection of any one polymer. Preferably, however, the prepolymers are elastomeric. As noted above, these elastomers can be unsaturated and are therefore capable of being vulcanized after formation of the hyper-branched polymers. In another embodiment, the prepolymer containing a functional group or groups is an elastomer that contains little or no unsaturation, and therefore the resulting hyper-branched polymer is not crosslinked with the elastomeric matrix upon vulcanization of that matrix. Instead, the hyper-branched polymer is entrapped within a crosslinked elastomeric network. For purposes of this specification, a saturated elastomer will refer to those elastomers where less than about five weight percent of the polymer includes curable double bonds. Preferably, saturated elastomers are those where less than about three weight percent of the polymer includes curable double bonds, more preferably where less than about one weight percent of the polymer includes curable double bonds, and even more preferably less than about 0.5 weight percent of the polymer includes curable double bonds. For example, the functionalized prepolymer can include, without limitation, unsaturated elastomers such as polybutadiene, polyisoprene, styrene- butadiene copolymer, ethylene-propylene-diene terpolymer, nitrile rubber, fluoroelastomers, polyurethane, natural rubber and silicone rubber. Examples of saturated polymers that may be functionalized in obtaining the functionalized prepolymers of this embodiment include ethylene-propylene copolymer, polyisobutylene, butyl rubber, hydrogenated copolymers such as styrene- butadiene copolymer, hydrogenated polyisoprene, and hydrogenated high-vinyl polybutadiene. Each of these elastomers are well known in the art and are commercially available from a number of sources. Also, because these polymers are well known in the art, there are a number of synthetic techniques known and published that can be employed in preparing these polymers. These techniques include, but are not limited to, anionic polymerization, cationic polymerization, Ziegler-Natta polymerization, and radical chain polymerization including free radical polymerization. One can refer to Principles of Polymerization, Third Edition, by George Odian for additional information on the various techniques that can be employed in making polymers. The molecular weight of the functionalized prepolymer can vary. In a preferred embodiment, the molecular weight - number average molecular weight (Mn) - of the polymeric backbone or prepolymer should be between about 1,000 and about 100,000, more preferably between 1,000 and about 80,000, and even more preferably between about 2,000 and about 50,000. As for the degree of functionalization of the prepolymer, there should be at least one functional group per one hundred repeating units within the polymer. Stated another way, there should be at least one functional group per entanglement molecular weight. The crosslinking agents that can be employed to react with the functionalized prepolymer and thereby form the hyper-branched polymers include any of the sundry crosslinking agents that are known in the art. The one proviso, of course, is that the crosslinking agent must be capable of reacting with and forming a covalent bond with the functional group on or within the functionalized prepolymer. In order to be effective, the crosslinking agent should at least be difunctional. In other words, the crosslinking agent should contain at least two functional groups that will react with functional groups on the prepolymer molecules. Preferably, the crosslinking agent should contain between two and about 10 functional groups, and more preferably between 2 and about 5 functional groups. For purposes of this specification, these agents may be referred to as multi-functional crosslinking agents. These functional groups can include, without limitation, primary amino groups (NH ), secondary amino groups (NH), hydroxyl groups (OH), carboxyl groups (COOH), vinyl groups (RCHCH 2 ), epoxy groups, anhydride groups , acyl halide groups (RCOCL), carboxylic acid anhydride groups (RCOOCOR), carboxamide groups (RCONH 2 ), and isocyanate groups (RNCO). Accordingly, practice of the present invention should not be limited by the crosslinking agent selected. Some specific crosslinking agents that are useful in practicing this embodiment and that are conventional in the art include, without limitation, diisocyanates, phenolic resins including resole phenolics and novolac phenolics, diamines, dihydroxyl ethane, and dicarboxyl ethane. Those skilled in the art will be able to readily select an appropriate functionalized prepolymer and complementary crosslinking agent to carry out the hyper-branching or crosslinking reaction. Preferably, the crosslinking reaction will be a single step reaction. For example, 2,4-diisocyanate will react with and crosslink a hydroxy functionalized prepolymer. Other single-step reactions include, but are not limited to, ester reactions that take place between carboxyl and hydroxyl groups, amide reactions that take place between amino groups and carboxyl groups, urethane reactions that take place between isocyanate groups and hydroxyl groups, epoxy reactions that take place between epoxy groups and amino groups, and imide reactions that take place between anhydride groups and amino groups. Preferred reactions include those that do not generate small molecules, such as urethane and epoxy reactions. For a further understanding of these reactions, one can refer to Reactive Extrusion, by Brown, discussed hereinabove. Those skilled in the art will be able to readily select the appropriate reaction conditions necessary to achieve hyper-branched polymers. In other words, the reaction between a functional group and a crosslinking agent is conventional in the art and can be carried out without undue calculation or experimentation. Under certain circumstances, it should be appreciated that a catalyst may be needed in order to effect the crosslinking reaction. When used, those catalysts that do not deleteriously impact the final composition should be selected. In one preferred embodiment of this invention, the damping additive is added to a vulcanizable composition of matter that is useful for making tire rubber. Here, the damping additive is added in an amount from about 10 to about 1,000 parts by weight per hundred parts rubber (phr). Even more preferably, the damping additive should be added in an amount from about 10 to about 300 parts by weight phr. It has been found that the addition of the damping additives according to the present invention improves the overall traction of tire rubber including wet traction, snow traction, and dry traction. Advantageously, the wet traction of tire rubber, as predicted by hysteresis loss at 5°C, can be improved by at least 10 percent, even more advantageously by at least 20 percent, and even more advantageously by about 30 percent. Likewise, the snow traction of tire rubber, as predicted by hysteresis loss at -5°C, can be improved by at least 10 percent, more advantageously by at least 20 percent, and even more advantageously by about 30 percent. Although damping additives are added to vulcanizable compositions of matter that are useful for fabricating tire rubber, practice of this invention does not alter the type or amount of other ingredients typically included within these vulcanizable compositions of matter. Accordingly, practice of this invention is not limited to any one particular vulcanizable composition of matter or tire compounding stock. Typically, these vulcanizable compositions of matter include an elastomer component that is blended with reinforcing fillers and at least one vulcanizing agent. These compositions typically also include other compounding additives such as accelerators, oils, waxes, scorch inhibiting agents, and processing aids. As known in the art, vulcanizable compositions of matter containing synthetic rubbers typically include antidegradants, processing oils, zinc oxide, optional tackifying resins, optional reinforcing resins, optional fatty acids, optional peptizers, and optional scorch inhibiting agents. These vulcanizable compositions are compounded or blended by using mixing equipment and procedures conventionally employed in the art. Preferably, an initial masterbatch is prepared that includes the elastomer component and the reinforcing fillers, as well as other optional additives such as processing oil and antioxidants. According to this invention, it is preferred to add the damping additive during preparation of the initial masterbatch. Once this initial masterbatch is prepared, the vulcanizing agents are blended into the composition. This vulcanizable composition of matter can then be processed according to ordinary tire manufacturing techniques including standard rubber curing techniques. For further explanation of rubber compounding and the additives conventionally employed, one can refer to The Compounding and Vulcanization of Rubber, by Stevens in RUBBER TECHNOLOGY SECOND EDITION (1973 Van Nostrand Reihold Company), which is incorporated herein by reference. Tires can be produced from this tire rubber by using techniques conventionally employed in the art. The elastomers that are typically employed within vulcanizable compositions of matter that are useful for making tires include both natural and synthetic elastomers rubbers. For example, these elastomers include, without limitation, natural rubber, synthetic polyisoprene rubber, styrene/butadiene rubber (SBR), polybutadiene, butyl rubber, neoprene, ethylene/propylene rubber, ethylene/propylene/diene rubber (EPDM), acrylonitrile/butadiene rubber (NBR), silicone rubber, the fluoroelastomer, ethylene acrylic rubber, ethylene vinyl acetate copolymers (EVA) epichlorohydrin rubbers, chlorinated polyethylene rubber, chlorosulfonated polyethylene rubbers, hydrogenated nitrile rubber, tetrafluoroethylene/propylene rubber and the like. As used herein, the term elastomer or rubber will refer to a blend of synthetic and natural rubber, a blend of various synthetic rubbers, or simply one type of elastomer or rubber. Also, the elastomers that are useful in practicing this invention include any of the various functionalized elastomers that are conventionally employed in the art of making tires. The reinforcing agents, such as carbon black or silica, typically are employed in amounts ranging from about 1 to about 100 parts by weight per 100 parts by weight rubber (phr), with about 20 to about 80 parts by weight (phr) being preferred, and with about 40 to about 80 parts by weight (phr) being most preferred. The carbon blacks may include any of the commonly available, commercially-produced carbon blacks, but those having a surface area (EMSA) 2 2 2 of at least 20 m /g and more preferably at least 35 m /g up to 200 m /g or higher are preferred. Surface area values used in this application are those determined by ASTM test D-1765 using the cetyltrimethyl-ammonium bromide (CTAB) technique. Among the useful carbon blacks are furnace black, channel blacks and lamp blacks. More specifically, examples of the carbon blacks include super abrasion furnace (SAF) blacks, high abrasion furnace (HAF) blacks, fast extrusion furnace (FEF) blacks, fine furnace (FF) blacks, intermediate super abrasion furnace (ISAF) blacks, semi-reinforcing furnace (SRF) blacks, medium processing channel blacks, hard processing channel blacks and conducting channel blacks. Other carbon blacks that may be utilized include acetylene blacks. Mixtures of two or more of the above blacks can be used in preparing the carbon black products of the invention. Typical values for surface areas of usable carbon blacks are summarized in the following table. CARBON BLACKS ASTM Surface Area Designation ( 2 /g) (D-1765-82a) (D-3765) N-110 126 N-220 111 N-339 95 N-330 83 N-550 42 N-660 35 The carbon blacks utilized in the preparation of the rubber compounds used may be in pelletized form or in unpelletized flocculent mass. Preferably, for more uniform mixing, unpelletized carbon black is preferred. With respect to the silica fillers, the vulcanizable compositions of the present invention may preferably be reinforced with amorphous silica (silicon dioxide). Silicas are generally referred to as wet-process, hydrated silicas because they are produced by a chemical reaction in water, from which they are precipitated as ultrafine, spherical particles. These particles strongly associate into aggregates that in turn combine less strongly into agglomerates. The surface area, as measured by the BET method, gives the best measure of the reinforcing character of different silicas. Useful silicas preferably have a 2 surface area of about 32 to about 400 m7g, with the range of about 100 to about 2 2 250 m /g being preferred, and the range of about 150 to about 220 m /g being most preferred. The pH of the silica filler is generally about 5.5 to about 7 or slightly over, preferably about 5.5 to about 6.8. When employed, silica can be used in the amount of about 1 part to about 100 parts by weight per 100 parts of polymer (phr), preferably in an amount from about 5 to about 80 phr. The useful upper range is limited by the high viscosity imparted by fillers of this type. Usually, both carbon black and silica are employed in combination as the reinforcing filler. When both are used, they can be used in a carbon black:silica ratio of from about 10:1 to about 1 :2. Some of the commercially available silicas that may be used include: Hi- Sil 215, Hi-Sil ® 233, and Hi-Sil ® 190, produced by PPG Industries. Also, a number of useful commercial grades of different silicas are available from a number of sources including Rhone Poulenc. Typically, a coupling agent is added when silica is used as a reinforcing filler. One coupling agent that is conventionally used is bis-[3(triethoxysilyl) propylj-tetrasulfide, which is commercially available from Degussa, Inc. of New York, New York under the tradename SI69. The reinforced rubber compounds can be cured in a conventional manner with known vulcanizing agents at about 0.5 to about 4 phr. For example, sulfur or peroxide-based curing systems may be employed. For a general disclosure of suitable vulcanizing agents one can refer to Kirk-Othmer, ENCYCLOPEDIA OF CHEMICAL TECHNOLOGY, 3 rd Edition, Wiley Interscience, N.Y. 1982, Vol. 20, pp. 365-468, particularly VULCANIZATION AGENTS AND AUXILIARY MATERIALS pp. 390-402, or VULCANIZATION by A.Y. Coran , ENCYCLOPEDIA OF POLYMER SCIENCE AND ENGINEERING, 2 nd Edition, John Wiley & Sons, Inc., 1989; both of which are incorporated herein by reference. Vulcanizing agents may be used alone or in combination. This invention does not appreciably affect cure times, and thus the polymers can be cured for a conventional amount of time. Typically, vulcanization is effected by heating the vulcanizable composition of matter; e.g., it is heated to about 170°C. Cured or crosslinked polymers will be referred to as vulcanizates for purposes of this disclosure. In other embodiments of this invention, damping additives are added to elastomeric compositions of matter that are useful for fabricating damping and vibration restraining materials. These uses involve connecting materials such as sealing materials, packing, gaskets and grommets, supporting materials such as mounts, holders and insulators, and cushion materials such as stoppers, cushions, and bumpers. These materials are also used in equipment producing vibration or noise and household electrical appliances. For example, these materials could be used in air-conditioners, laundry machines, refrigerators, electric fans, vacuums, driers, printers and ventilator fans. Further, these materials are also suitable for impact absorbing or damping materials in audio equipment and electronic or electrical equipment. For example, these materials could be used in compact disc players including portable units and those within vehicles, video cassette recorders, radio cassette recorders, microphones, insulators for disc drives within computers, various holders for optical disc readers, microphones, or speakers including those within portable and cellular telephones. Still further, these materials are useful in sporting goods and shoes. In order to demonstrate the practice of the present invention, the following examples have been prepared and tested as described in the Experimental Section disclosed hereinbelow. The examples should not, however, be viewed as limiting the scope of the invention. GENERAL EXPERIMENTATION EXPERIMENT I Four tire stocks were prepared according to the general recipe set forth in Table I. TABLE I Parts by Weight Elastomeric Binder 100 Carbon black 80 Damping Additive 50 Stearic Acid 1.5 Wax 1 Antioxidant 1 Zinc Oxide 2.5 186 Sulfur -1.7 Diphenylguanidine 0.6 N-tert-butyl-benzothiazolesulfenamine 0.35 Benzothiazyl disulfide 0.7 3.35 189.35 The elastomeric binder was a butadiene rubber obtained from the Firestone Synthetic Rubber Company under the tradename D-40NF. The carbon black was an intermediate super abrasion furnace black that is commercially available from a number of sources. The antioxidant was N-(l ,3 dimethylbutyl)-N'-phenyl-p-phenylene-diamine is likewise available from a number of sources. Also, the diphenylguanidine, N-tert-butyl- benzothiazolesulfenamine, and benzolthiazyl disulfide accelerators that were used are conventionally used in the art and are commercially available from many sources. Similarly, the antioxidant, stearic acid, wax, zinc oxide, sulfur an other ingredients that were employed are conventionally employed in the art and are commercially available from many sources. Each of the four stocks that were prepared included a different damping additive. The first stock included a linear liquid butadiene; the second stock included a light aromatic processing oil; the third stock included a heavy aromatic processing oil; and the fourth stock included a hyper-branched polymer in accordance with this invention. The linear liquid butadiene rubber was obtained from Aldrich Chemical Company and was characterized by having 47.9 weight percent trans- 1,4 microstructure, 44.0 percent cis-1,4 microstructure, and 12.1 weight percent vinyl- 1,2 microstructure. The light aromatic processing oil was obtained from The Shell Chemical Company under the tradename Durex 727, and the heavy aromatic processing oil was obtained from Witco Chemical Company under the tradename Califlux 55. The hyper-branched polymer was prepared by crosslinking a liquid hydroxy-terminated polybutadiene prepolymer with toluene 2,4- diisocyanate. The hydroxy-terminated butadiene prepolymer was obtained from Aldrich Chemical Company and was characterized by having 52.1 percent by weight trans- 1 ,4 microstructure, 22.4 percent by weight cis- 1 ,4 microstructure, and 25.5 percent by weight percent vinyl-1,2 microstructure. The prepolymer was also characterized by a viscosity of 44.1 poise. The hydroxyl value of the prepolymer was measured by using a method in which the hydroxyl groups were esterified by acetic anhydride in pyridiene, and the resulting acid was titrated with a standard base. According to this procedure, the hydroxyl value was estimated to be 0.903 mmol/g. The molecular weight was determined by GPC using polystyrene as the standard. This analysis gave an number average molecular weight (M n ) of 2,900, and an average molecular weight (M w ) of 6,100. From these analytical results, the functionality of the polymer was calculated to be about 2.62. The 2,4 diisocyanate was obtained from Aldrich, had a purity of 99 percent, and was used without further purification. With specific regard to the preparation of the hyper-branched polymer, various reaction mixtures were prepared as follows. The mixture of prepolymer and crosslink agent was vigorously stirred at about 22°C for 30 minutes in order to dissolve the 2.4 diisocyanate into the prepolymer. Each sample was then allowed to react at about 70°C for about three days. Specifically, the hyper-branched polymer that was chosen was prepared from a mixture of 300.46 g of butadiene prepolymer and 12.475 g of 2,4 diisocyanate. Notably, this hyper-branched polymer showed the high tan (δ) properties. The damping properties were tested on a temperature range of from about 20 to about 100°C, and also on a frequency range of from about 0.01 to about 10 Hz. Over this range of conditions, the hyper-branched polymer demonstrated a tan (δ) of 1.1 ± 0.2. The T g of the hyper-branched polymer is about -60°C, as determined by DSC. In preparing the elastomeric composition that contains the damping additive, the elastomeric binder and the damping additive were initially charged and masticated for about 30 seconds within a 60 gram Brabender internal mixer. The carbon black, stearic acid, wax, antioxidant, and zinc oxide were then mixed with the rubber/additive blend for about five minutes at about 110°C and at about 60 rpm. The composition was dropped and allowed to cool. Subsequent to this step, the sulfur and accelerators were charged, and the entire composition was mixed for about 80 seconds at about 75°C. The four stocks were individually sheeted and molded at about 165°C for about 15 minutes. Each recipe was then tested for 50 percent modulus according to ASTM-D 412 at about 22°C. The test specimens were in the form of rings having a width of about 0.05 inch and a thickness of about 0.075 inch. The specimens were tested at a specific gauge length of about 1.0 inch. Hysteresis of the material at 50°C was measured by using a dynamic mechanical analyzer. The test specimens employed with the dynamic mechanical analyzer were strips having a length of about 1.0 inches, a width of about 0.25 inches, and a thickness of about 0.075 inches. The testing conditions included a 5 Hz temperature ramp and about 1% strain. The results of this testing is set forth in Table II. TABLE II Stock Damping Additives 50% Young's tan (δ) at modulus at 23°C (psi) 50°C 1 Linear liquid polybutadiene 1 10.0 0.17 2 light aromatic processing oil 107.3 0.18 3 heavy aromatic processing oil 108.7 0.19 4 hyper-branched polymer 122.6 0.25 As can be seen from the foregoing data, the tire recipe that included the hyper-branched polymer, i.e., Stock No. 4, exhibited the highest damping as indicated by the large tan (δ) value. Additionally, the stock containing the hyper-branched polymer was examined for hysteresis over a wide temperature range. The data obtained from this testing is set forth in Table III. TABLE HI tan (δ) at Stock Additive 35°C 45°C 55°C 65°C 75°C 85°C 95°C 4 hyper-branched 0.246 0.250 0.253 0.251 0.247 0.246 0.244 polymer Notably, the material exhibited a constant tan (δ) plateau over a temperature range from about 35 to about 95°C. EXPERIMENT II Three rubber compositions were prepared according to the general recipe set forth in Table IV. TABLE IV Parts by Weight Elastomeric Binder 100 Damping Additive 100 Stearic Acid 1.5 Zinc Oxide 2.5 204.00 Sulfur -2.5 Accelerator 1.5 4.00 208.00 The elastomeric binder that was employed was EPDM (ethylene- propylene diene terpolymer) obtained from Exxon Chemicals under the tradename Vistalon ® 6505. The accelerator that was used was benzolthiazyl disulfide. The accelerator, stearic acid, zinc oxide, and sulfur are conventionally used in the art and are commercially available from many sources. As noted in Table IV, each of the three rubber compositions included a damping additive that was different for each stock. The first stock included a paraffin oil that was obtained from Idemitsu Corporation of Japan under the tradename PW380. The second stock included a hyper-branched polymer in accordance with the present invention. And, the third stock having a low sulfur content included a paraffin oil that was obtained from Idemitsu Corporation of Japan under the tradename PW380. The hyper-branched polymer was prepared by crosslinking a liquid hydroxy-terminated hydrogenated polyisoprene prepolymer, which was obtained from Kurary Inc. of Japan under the tradename TH-21, with toluene 2,4-diisocyanate. Specifically, various reaction mixtures were prepared. These mixtures were mixed at about 22°C for about one hour in order to dissolve a crosslink agent into the prepolymer. The resulting polymeric mixtures were then allowed to react at 70°C for about three days. The hyper-branched polymer selected for the experiment was prepared from the reaction of 19.74 grams of hydroxy-terminated EPR and 0.66 grams of toluene 2,4-diisocyanate. The polymer showed a relatively constant tan (δ) plateau with tan (e>)=1.2 ± 0.3 over a temperature range from about 40 to about 100°C. The T g of the hyper- branched polymer is about -40°C, as determined by DSC. The EPDM polymer rubber was initially charged at 110°C and mixed for about one minute within a 300 gram Brabender internal mixer at an agitation speed of 60 rpm. The damping additive, stearic acid, and zinc oxide were subsequently charged over the course of about 15 minutes while mixing continued. The mixture was then masticated for another 15 minutes, dropped, and cooled. Once cooled to about 75°C, mixing was continued for about 30 seconds and the curing agent and accelerator was added. Mixing was continued for another 90 seconds and the composition was removed from the internal mixer. The three stocks were individually sheeted and molded at about 160°C for about 30 minutes. Each stock was then tested for 50% modulus according to ASTM-D 412 at about 22°C. Tensile strength at break and elongation at break were likewise determined according to ASTM-D 412 at 22°C. For purposes of this testing, the test specimens were in the form of rings having a width of about 0.05 inches and a thickness of 0.075 inches. The specimens were tested at a specific gauge length of about 1.0 inch. Hysteresis was measured by using a dynamic mechanical analyzer as set forth above. The test specimens were strips having a length of about 1.0 inches, a width of about 0.25 inches, and a thickness of about 0.075 inches. The testing condition was 1 Hz and about 1% strain. The glass transition temperature (T g ) of each stock was determined by the tan (δ) peak. The results of this testing is set forth in Table V. TABLE V Stock Damping Additive 50% Young's Tensile Elongation tan (δ) tan tan (δ) tan (δ) Tg modulus at 23°C at Break at Break at (δ) at at at (measured (psi) (psi) (psi) -20°C 5°C 20°C 50°C by tan peak) Paraffin oil 9.83 130 1429 0.15 0.12 0.11 0.09 -41 (PW380) Hyper-Branched 10.15 180 1474 0.39 0.29 0.25 0.20 -38 polymer (Sample 1) Paraffin oil 5.83 0.13 0.13 0.15 0.15 -42 (PW380), low sulfur content As can be seen by the foregoing data, the EPDM rubber composition including the hyper-branched polymer (Stock 6) exhibits the highest damping properties among the other EPDM rubber compounds. Likewise, the EPDM rubber composition including the hyper-branched polymer exhibited superior mechanical properties. EXPERIMENT III Three rubber compositions were prepared according to the general recipe set forth in Table VI hereinbelow: TABLE VI Parts by Weight Elastomeric Binder 100 Carbon Black 100 Damping Additive 100 Stearic Acid 1.5 Zinc Oxide 2.5 304.00 Sulfur -2.5 Accelerator 1.5 4.00 308.00 The elastomeric that was employed was EPDM (ethylene- propylene diene terpolymer) obtained from Exxon Chemicals under the tradename Vistalon ® 6505. The accelerator that was used was benzolthiazyl disulfide. The accelerator, stearic acid, zinc oxide, and sulfur are conventionally used in the art and are commercially available from many sources. The carbon black that was employed was an intermediate abrasion furnace-black (Nl 10) that is commercially available from a number of sources. The accelerator, carbon black, stearic acid, zinc oxide, and sulfur are conventionally used in the art and commercially available from a number of sources. As noted in Table VI, each of the three rubber compositions included a damping additive that was different for each stock. The first stock included a paraffin oil that was obtained from Idemitsu Corporation under the tradename PW380. The second stock included a hyper-branched polymer in accordance with the present invention. And, the third stock included a paraffin oil having a low sulfur content that was obtained from Idemitsu Corporation under the tradename PW380. The hyper-branched polymer was prepared by crosslinking a liquid hydroxy-terminated hydrogenated polyisoprene, which was obtained from Kurary Inc. under the tradename TH-21, with toluene 2,4- diisocyanate. Specifically, various reaction mixtures were prepared, and the reaction mixture that showed a relatively constant tan (δ) plateau was selected as the hyper-branched polymer additive of choice. These mixtures were mixed at about 22°C for about one hour in order to dissolve the crosslinking agent into the polymer. The experimental polymers were then cured at 70°C for about three days. The hyper-branched polymer selected for the experiment was prepared from the reaction of 19.739 grams of hydroxy-terminated polyisoprene and 0.66 grams of toluene 2,4- diisocyanate. The T g of the hyper-branched polymer is about 40°C, as measured by DSC. The EPDM polymer rubber was initially charged at 110°C and mixed for about one minute within a 300 gram Brabender internal mixer at an agitation speed of 60 rpm. The damping additive, carbon black, stearic acid, and zinc oxide were subsequently charged over the course of about 5 minutes while mixing continued. The mixture was then dropped and cooled. Once cooled to about 75°C, mixing was continued for about 30 seconds and the curing agent and accelerator were added. Mixing was continued for another 45 seconds and the composition was removed from the internal mixer. The three stocks were individually sheeted and molded at about 160°C for about 30 minutes. Each stock was then tested for 50% modulus according to ASTM-D 412 at about 22°C. Tensile strength at break and elongation at break were likewise determined according to ASTM-D 412 at 22°C. For purposes of this testing, the test specimens were in the form of rings having a width of about 0.05 inches and a thickness of 0.075 inches. The specimens were tested at a specific gauge length of about 1.0 inch. Each sample was also tested for wet traction by using the British Portable Skid Tester according to the procedure set forth in the Road Research Laboratory Technical Paper No. 66 by Giles et al., London (1966). The sample geometry for the test was a rectangular bar having the dimensions of 1 x 3 x 0.25 inches. Hysteresis was measured using a dynamic mechanical analyzer at about 0°C. The test specimens were strips having a length of about 1.0 inches, a width of about 0.25 inches, and a thickness of about 0.075 inches. The measurements were performed at 1 Hz and about 1 percent strain. The results of this testing is set forth in Table VII. TABLE VII Stock Damping Additive 50% Youngs 's Shore A Tensile at Elongation at G' (at 0°C tan (δ) (at Stanley Modulus at Hardness Break (psi) Break (psi) dyn/cm 2 ) 0°C) London 23°C (psi) Index Paraffin oil 123 52.7 1427 482 1.3x10* 0.182 33 (PW380) Hyper-Branched 145 55.1 978 773 1.4x10 s 0.230 38 polymer (Sample 1) 10 Paraffin oil 118 51.7 1532 536 l.lxlO 8 0.174 32 (PW380), low sulfur content Based upon the foregoing data, it should be evident that the vulcanizate stock (Stock 9) according to the present invention demonstrated superior damping as evidenced by tan (δ) at 0°C of about 0.230, which corresponds to about 26 percent improvement over the controls, as well as a superior wet traction of 38, as measured by the Stanley London Test which corresponds to about 15 percent improvement over the controls. Based on the relatively constant tan (δ) obtained over the broad temperature range as demonstrated from the above data, it should be understood that the technology including a hyper-branched polymers in rubber recipes improves the damping properties of many important rubber applications including tires. Based upon the foregoing disclosure, it should now be apparent that the addition of hyper-branched polymers to rubber binders as described herein will carry out the objects set forth hereinabove. It is, therefore, to be understood that any variations evident fall within the scope of the claimed invention and thus, the selection of specific component elements can be determined without departing from the spirit of the invention herein disclosed and described. In particular, tire recipes or vulcanizable compositions of matter according to the present invention are not necessarily limited to those described herein inasmuch as it is believed that the addition of the hyper-branched polymers to any useful rubber or tire recipe will improve the damping thereof. Thus, the scope of the invention shall include all modifications and variations that may fall within the scope of the attached claims.

Claims: What is claimed is: 1. An elastomeric composition of matter that has improved damping properties, comprising: a cured elastomeric matrix, and from about 10 to about 1,000 parts by weight per one hundred parts by weight rubber of a damping additive dispersed within said elastomeric matrix. 2. The elastomeric composition of claim 1, where said damping additive is characterized by having a tan (δ) that is greater than or equal to about 0.35 in the temperature range from about -20°C to about 120°C. 3. The elastomeric composition of either claim 1 or claim 2, where said damping additive is characterized by having a substantially constant tan (δ) within the temperature range from about -20°C to about 120°C. 4. The elastomeric composition of any of claims 1-3, where said damping additive is characterized by having a glass transition temperature that is less than or equal to about -20°C. 5. The elastomeric composition of any of claims 1-4, where said cured elastomeric matrix is characterized by having a Shore A hardness that is less than or equal to about 80. 6. The elastomeric composition of any of claims 1-5, where said damping additive is selected from the group including dendrimers, centipede polymers, and hyper-branched polymers. 7. The elastomeric composition of claim 6, where said hyper-branched polymer is the reaction product of a functionalized elastomer and a multifunctional crosslinking agent. 8. The elastomeric composition of claim 7, where the extent of reaction between the functionalized elastomer and multi-functional crosslinking agent is defined by the following formula: where E is the relative distance to the gel point and is a value of less than 1 , r is the extent of the reaction, and r ge ι is the extent of the reaction at the gel point. 9. The elastomeric composition of either claim 7 or claim 8, where said hyper-branched polymer is selected from the group of reaction products consisting of the reaction product of a hydroxy-terminated polybutadiene prepolymer and a diisocyanate; the reaction product of a hydroxy-terminated ethylene-propylene prepolymer and a diisocyanate, the reaction product of a hydroxy-terminated polyisoprene prepolymer and a diisocyanate, the reaction product of a carboxyl and hydroxyl groups, an amino group and carboxyl group, the reaction product of an isocyanate and hydroxyl group, an epoxy group and amino group, and the reaction product of an anhydride group and amino group. 10. The elastomeric composition of any of claims 1-9, where said elastomeric composition also comprises at least one reinforcing filler. 11. A tire component comprising the elastomeric composition of any of claims 1-10. 12. The tire component of claim 11, where said component is a tire tread. 13. A tire comprising the tire component of either claim 11 or claim 12. 14. A method of making an elastomeric composition of any of claims 1- 10, a tire component of either of claims 11 or 12, or a tire of claim 13, comprising the steps: (a) adding a damping additive to a vulcanizable composition of matter; and (b) processing the vulcanizable composition of matter containing the damping additive into the elastomeric composition. 15. The method of claim 14, where the processing step includes adding a vulcanizing agent to the composition and effecting vulcanization. 16. The method of either claim 14 or claim 15, where the processing step includes adding at least one reinforcing filler to the vulcanizable composition.

Inventors: FOLTZ VICTOR J, HAMADA TATSURO, HAYES MICHAEL W, KELLEY EDWARD D, PAKDEL PEYMAN, WANG XIAORONG, FOLTZ, VICTOR, J., HAMADA, TATSURO, HAYES, MICHAEL, W., KELLEY, EDWARD, D., PAKDEL, PEYMAN, WANG, XIAORONG
Applicants: BRIDGESTONE CORP, FOLTZ VICTOR J, HAMADA TATSURO, HAYES MICHAEL W, KELLEY EDWARD D, PAKDEL PEYMAN, WANG XIAORONG, BRIDGESTONE CORPORATION, FOLTZ, VICTOR, J., HAMADA, TATSURO, HAYES, MICHAEL, W., KELLEY, EDWARD, D., PAKDEL, PEYMAN, WANG, XIAORONG
Application year: 2000
Main classification: C08L21
IPC codes: B29D30, B29K21, B29K105, B60C1, C08K3, C08K5, C08L21, C08L51, C08L75, C08L101, F16F15